Patent Description:
An OED refers to a device including an organic material layer generating an exchange of charges using holes and electrons. Examples of the OEDs may include a photovoltaic device, a rectifier, a transmitter, and an organic light emitting diode (OLED).

In one exemplary embodiment, an OLED has less power consumption and a higher response speed, and is advantageous in forming a thinner display device or light than a conventional light source. Since the OLED also has excellent space utilization, the OLED is expected to be applied in various fields including all types of portable devices, monitors, notebook computers and TVs.

To expand commercialization and use of the OLED, the most important problem is durability. Organic materials and metal electrodes included in the OLED are very easily oxidized by external factors such as moisture. In addition, when a display is realized by applying the OLED, a part in which an electrical connection is deposited on an outer peripheral part of the display, and a part in which an electrical connection is not deposited on the outer peripheral part of the display are included. In the non-deposited part, internal or external light may be reflected or scattered, and some parts seen bright from an outside cause an external defect.

<CIT> relates to an opaque coverlay comprising an epoxy adhesive and carbon black powder.

<CIT> relates to an adhesive film comprising a curable hot-melt adhesive layer including an epoxy curable resin comprising a moisture absorbent, and to a method of encapsulating an organic light emitting device.

The present invention is directed to providing an encapsulation film which has an excellent moisture barrier property and is capable of preventing a external defect of an OED by absorbing and blocking internal or external light to prevent reflection or scattering of the light, an OED having the same, and a method of manufacturing the OED.

Hereinafter, exemplary embodiments of the present invention will be described in further detail with respect to the accompanying drawings. In addition, to explain the present invention, related known detail description for a common function or configuration is omitted. In addition, the accompanying drawings are provided to help in understanding the present invention, and to more clearly explain the present invention, parts not relating to the description are omitted. To clearly express several layers and regions in the drawing, thicknesses or sizes are exaggerated. The scope of the present invention is not limited to thicknesses, sizes and ratios represented in the drawings.

In one aspect, the present invention provides a film for encapsulating an organic electronic element. The encapsulation film of the present invention may be applied to encapsulate or capsulate an entire area of the organic electronic element such as an OLED.

The exemplary encapsulation film includes a light absorbing region. In the present invention, the light absorbing region means a region having a light transmittance of <NUM> % or less with respect to a visible light region in the encapsulation film. The light absorbing region includes an encapsulation resin and a light absorbing material. The encapsulation film includes a light absorbing layer which includes a light absorbing region comprising an encapsulation resin and a light absorbing material and having a light transmittance of <NUM> % or less with respect to the visible light region; and a moisture barrier layer. In another aspect, the present invention provides an OED, which includes a substrate, an organic electronic element present on the substrate and an encapsulation film having the light absorbing region attached to an entire surface of the organic electronic element. Meanwhile, the light absorbing region means a region including a light absorbing material in a thickness direction when the encapsulation film is formed in two or more layers. That is, in this case, a part of the moisture barrier layer may be defined as the light absorbing region, in addition to a part of the light absorbing layer.

The term "OED" used herein means a product or device having an element including an organic material layer generating an exchange of charges using holes and electrons between a pair of electrodes facing each other, and as an example, a photovoltaic device, a rectifier, a transmitter and an OLED may be included, but the present invention is not limited thereto. In one example of the present invention, the OED may be an OLED.

The term "light absorbing layer" or "moisture barrier layer" used herein may be an adhesive layer, a pressure-sensitive adhesive layer or a curable pressure-sensitive adhesive, which forms the encapsulation film. Accordingly, when needed, the encapsulation film and the light absorbing layer and/or the moisture barrier layer may be mutually used with the same meaning. Here, the term "curable pressure-sensitive adhesive layer" used herein means a type of adhesive layer which is maintained in a solid or semi-solid state at room temperature to attach an adherend without bubbles due to flowability generated when heated and tightly fix the adherend using an adhesive after solidifying. In one exemplary embodiment, the "light absorbing layer" means a layer including the light absorbing region. In addition, in one exemplary embodiment, the "moisture barrier layer" means a layer having a water vapor transmission rate (WVTR) of <NUM>/m<NUM>·day or less, preferably <NUM>/m<NUM>·day or less, more preferably <NUM>/m<NUM>·day or less, and further more preferably, <NUM>/m<NUM>·day or less. In the present invention, the WVTR is a rate measured with respect to a thickness direction of a crosslinked product or cured product at <NUM> and a relative humidity of <NUM> % after an encapsulation resin which will be described below is crosslinked or cured, and a crosslinked product or a cured product is formed in a film shape having a thickness of <NUM>. In addition, the WVTR is measured according to ASTM F1249. As the WVTR is controlled in the above range, permeation of moisture, vapor or oxygen into an encapsulation product of the OED may be effectively inhibited. In the present invention, as a level of the WVTR of the encapsulation film is lower, an encapsulation structure exhibits an excellent performance. The lower limit of the WVTR may be, but is not particularly limited to, for example, <NUM>, <NUM> or <NUM>/m<NUM>·day. The moisture barrier layer may include an encapsulation resin, and further include a moisture absorbent. Components constituting the moisture barrier layer, for example, the encapsulation resin or the moisture absorbent, may be equal to or different from the components constituting the light absorbing layer.

The term "encapsulation composition" used herein is a component constituting the light absorbing layer or moisture barrier layer of the encapsulation film. The encapsulation composition may include an encapsulation resin, a light absorbing material, a moisture absorbent, or other additives. In the light absorbing layer and the moisture barrier layer of the encapsulation film, types and contents of the components of the encapsulation composition, excluding the light absorbing material, for example, the encapsulation resin, the moisture absorbent, other additives or a filler may be the same as or different from each other. Unless particularly cited otherwise, description of the encapsulation composition which will be described below corresponds to all of the light absorbing layer and the moisture barrier layer of the encapsulation film.

The encapsulation film has a multilayer structure including at least two layers. According to the invention, the encapsulation film has a multilayer structure having at least two layers, the above-described light absorbing layer and the moisture barrier layer are included.

<FIG> (not claimed) is a cross-sectional view of an encapsulation film. An exemplary encapsulation film <NUM> includes a light absorbing layer <NUM>. In addition, as shown in <FIG>, the encapsulation film <NUM> has a multilayer structure having at least two layers, and in this case, the encapsulation film <NUM> includes at least one light absorbing layer <NUM>. In addition, as shown in <FIG>, when the encapsulation film <NUM> has a bilayer structure as claimed, a light absorbing layer <NUM> and a moisture barrier layer <NUM> are included. When the encapsulation film has a multilayer structure, a sequence of stacking a light absorbing layer and a moisture barrier layer is not particularly limited. In addition, when the encapsulation film has a multilayer structure including at least three layers, the moisture barrier layer may have a multilayer structure. When the moisture barrier layer has a multilayer structure, the light absorbing layer may be disposed between the at least two moisture barrier layers, or may be formed on one or both surfaces of a structure in which at least two moisture barrier layers are stacked. <FIG> shows that the light absorbing layer <NUM> is disposed between two moisture barrier layers <NUM> and <NUM>, and one (the moisture barrier layer <NUM>) of the two moisture barrier layers does not include a moisture absorbent <NUM> or includes a small amount of moisture absorbent <NUM> since it is encapsulated in contact with the organic electronic element. <FIG> shows that the light absorbing layer <NUM> is formed on one surface of a structure in which the two moisture barrier layers <NUM> and <NUM> are stacked, and one (the moisture barrier layer <NUM>) of the two moisture barrier layers <NUM> and <NUM> does not include a moisture absorbent <NUM> or includes a small amount of moisture absorbent <NUM> since it is encapsulated in contact with an organic electronic element. In addition, the encapsulation film may include at least two light absorbing layers. In this case, two light absorbing layers may be continuously stacked, and the moisture barrier layer may be included between the two light absorbing layers.

The encapsulation film includes a light absorbing region comprising an encapsulation resin and a light absorbing material as described above, and having a light transmittance of <NUM> % or less with respect to a visible light region. In the encapsulation film, a non-light absorbing region, not the light absorbing region, may consist of the same components as those constituting the light absorbing region, except that a small amount of light absorbing material is included or a light absorbing material is not included. The non-light absorbing region has a light transmittance of more than <NUM> % with respect to the visible light region. A part of the encapsulation film in which the light absorbing region is formed is not particularly limited, but for example, the light absorbing region may be formed in at least one outer peripheral part of the encapsulation film. The term "outer peripheral part" used herein means an edge. That is, the outer peripheral part of the film may mean an edge of a circumference of the film. In another exemplary embodiment, the light absorbing region may be formed in an entire area of the encapsulation film. That is, when the encapsulation film is observed in a plan view, the entire area of the encapsulation film has a light transmittance in a visible light region of <NUM> % or less, or only at least one outer peripheral part of the encapsulation film has a light transmittance of <NUM> % or less. In addition, when a film has a multilayer structure, the light transmittance may be a light transmittance, which is measured in a multilayer stacked structure including at least one light absorbing layer and at least one moisture barrier layer. For example, when the encapsulation film according to the present invention is observed in the plan view, the above-described light absorbing region is a region having a light transmittance of <NUM> % or less in a thickness direction of the film having a stacked structure. In one example, the lower limit of the light transmittance in the visible light region of the encapsulation film according to the present invention may be, but is not particularly limited to, <NUM> %. The light transmittance may be, for example, <NUM> to <NUM> %, <NUM> % to <NUM> %, <NUM> % to <NUM> %. <NUM> % to <NUM> %, <NUM> % to <NUM> %, <NUM> % to <NUM> %, <NUM> % to <NUM> %, or <NUM>% to <NUM> %. Particularly, when a display is realized by applying an OLED, a part of the display in which an electrical connection is deposited on a side surface thereof and a non-deposited part are included. Accordingly, in the non-deposited part, external light may be reflected or scattered, and the encapsulation film may serve to absorb and prevent reflected or scattered light. In one example, the light transmittance may be measured at <NUM> using an UV-Vis Spectrometer.

<FIG> are plan views of the encapsulation film of the present invention.

As described above, as shown in <FIG>, a light absorbing region may be formed in an entire area of the encapsulation film, but the present invention is not limited. That is, the encapsulation film, when observed in a plan view, as shown in <FIG>, the light absorbing region may be formed in at least one outer peripheral part. That is, when a region of the encapsulation film <NUM> having a light transmittance in a visible light region of <NUM> % or less is referred to as a light absorbing region or a first region <NUM>, and a region having a light transmittance in a visible light region of more than <NUM> % may be referred to as a non-light absorbing region or a second region <NUM>, the entire area of the encapsulation film may be a first region <NUM>. Alternatively, only one outer peripheral part of the encapsulation film <NUM> may be the first region <NUM>. That is, as shown in <FIG>, one of four outer peripheral parts is the first region <NUM>, and the others may be the second regions <NUM>. Alternatively, as shown in <FIG>, all four outer peripheral parts may be first regions <NUM>. Here, a thickness of each outer peripheral part may be suitably adjusted according to a field and application to which the encapsulation film is applied by those of ordinary skill in the art. In addition, the term "first region <NUM>" used herein may be used with the same meaning as the above-described light absorbing region.

In the present invention, an encapsulation composition constituting the light absorbing layer or moisture barrier layer may be formed of a known material. For example, the encapsulation composition constituting the light absorbing region of the light absorbing layer includes the encapsulation resin and the light absorbing material as described above. In addition, a type or content of the light absorbing material may be adjusted for the light absorbing region of the encapsulation film to have the above range of light transmittance by those of ordinary skill in the art.

The encapsulation resin described herein may be included in all of the light absorbing layer and the moisture barrier layer.

In one example, the encapsulation resin may be solid or semi-solid, preferably solid, at room temperature. Here, when the resin is solid or semi-solid at room temperature, the resin may not have flowability at room temperature. For example, the "solid or semi-solid at room temperature" used herein may mean that a viscosity of a target at room temperature is approximately <NUM><NUM> poise or more or approximately <NUM><NUM> poise or more. Here, the viscosity is measured at a strain of <NUM> % and a frequency of <NUM> using an Advanced Rheometric Expansion System (ARES).

When the encapsulation resin is solid or semi-solid at room temperature, it can be maintained in a film or sheet shape in an uncured state. Accordingly, in encapsulation or capsulation of the organic electronic element using the encapsulation film, physical or chemical damage applied to the element may be prevented, and the process may be smoothly performed. In addition, the addition of bubbles during the encapsulation or capsulation of the organic electronic element or the decrease in a life span of the element may be prevented. The upper limit of the viscosity of the encapsulation resin is not particularly limited, and may be controlled in a range of approximately <NUM><NUM> poise or less, for example, in consideration of processibility.

The encapsulation resin is a silane-modified epoxy resin.

As a component for the encapsulation resin, a base resin having a weight average molecular weight (Mw) capable of being molded in a film shape may be used. In one example, a range of the weight average molecular weight capable of being molded in a film shape may be approximately <NUM>,<NUM> to <NUM>,<NUM>,<NUM>, <NUM>,<NUM> to <NUM>,<NUM>,<NUM>, or <NUM>,<NUM> to <NUM>,<NUM>,<NUM>. The term "weight average molecular weight" used herein means a conversion value with respect to standard polystyrene measured by gel permeation chromatography (GPC).

In addition, as the component for the encapsulation resin, one or at least two components may be used. When at least two components are used, at least two different types of resins, at least two resins having different weight average molecular weights, or at least two different types of resins having different weight average molecular weights may be used.

The encapsulation resin according to the present invention is a heat-curable resin or a photocurable resin. The term "heat-curable resin" means a resin which can be cured through a process of suitably applying heat or an aging process, and the term "photocurable resin" means a resin which can be cured by irradiation of electromagnetic waves. In addition, the curable resin may be a dual curable resin including all heat curing and photocuring characteristics. In one example, the curable resin of the present invention may be a heat-curable resin, not a photocurable resin, in consideration that the encapsulation composition is composed of the curable resin with a light absorbing material which will be described below, but the present invention is not limited thereto.

For example, the curable resin may have an adhesive characteristic by curing, and may be a resin including at least one heat-curable functional group such as a glycidyl group, an isocyanate group, a hydroxyl group, a carboxyl group or an amide group, or a resin including at least one functional group which can be cured by irradiation of electromagnetic waves such as an epoxide group, a cyclic ether group, a sulfide group, an acetal group or a lactone group. In addition, a specific type of the above-described resin may be an acryl resin, a polyester resin, an isocyanate resin or an epoxy resin, but the present invention is not limited thereto.

In the present invention, as the curable resin, a silane-modified epoxy resin comprising at least two functional groups and having an epoxy equivalent of <NUM> to <NUM>,<NUM>/eq may be used. As the epoxy resin having the above range of epoxy equivalent is used, properties of the cured product such as adhesive performance and a glass transition temperature may be effectively maintained. Such an epoxy resin may be one or a mixture of at least two of a cresol novolac epoxy resin, a bisphenol A-type epoxy resin, a bisphenol A-type novolac epoxy resin, a phenol novolac epoxy resin, a tetrafunctional epoxy resin, a biphenyl-type epoxy resin, a triphenol methane-type epoxy resin, an alkyl-modified triphenol methane epoxy resin, a naphthalene-type epoxy resin, a dicyclopentadiene-type epoxy resin, and a dicyclopentadiene modified phenol-type epoxy resin.

In the present invention, as the curable resin, a silane-modified epoxy resin including a cyclic structure in a molecular structure may be used, or a silane-modified epoxy resin including an aromatic group (for example, a phenyl group) may be used. When the epoxy resin includes an aromatic group, a cured product may have excellent thermal and chemical stabilities, and exhibit a low moisture absorption amount, and thus reliability of the encapsulation structure of the OED may be enhanced. As a specific example of the epoxy resin comprising an aromatic group which can be used in the present invention, one or a mixture of at least two of a biphenyl-type epoxy resin, a dicyclopentadiene-type epoxy resin, a naphthalene-type epoxy resin, a dicyclopentadiene-modified phenol-type epoxy resin, a cresol-based epoxy resin, a bisphenol-based epoxy resin, a xylol-based epoxy resin, a multifunctional epoxy resin, a phenol novolac epoxy resin, a triphenolmethane-type epoxy resin and an alkyl-modified triphenolmethane epoxy resin may be used, but the present invention is not limited thereto.

In the present invention, as the epoxy resin, a silane-modified epoxy resin, or a silane-modified epoxy resin having an aromatic group is used. Likewise, when an epoxy resin which has a silane group structurally modified by a silane is used, an adhesive property to a glass substrate or an inorganic material of the substrate of the OED may be maximized, and a moisture barrier property or durability and reliability may be enhanced. A specific type of the epoxy resin which can be used in the present invention is not particularly limited, and such a resin may be easily obtained from a manufacturer such as Kukdo Chemical, Co.

In an exemplary embodiment of the present invention, a light absorbing region of the encapsulation film includes a light absorbing material, and the type or content of the light absorbing material may be appropriately controlled by those of ordinary skill in the art to satisfy the above-described range of the light transmittance of the film.

The term "light absorbing material" used herein is a material which can absorb visible rays, for example, a pigment or a dye.

In one example, the light absorbing material may be a non-conductive material. When the encapsulation composition including the light absorbing material is manufactured in a film form to be applied in encapsulation of the OED, if the film has electric conductivity, the OED has a problem in driving. Accordingly, in an exemplary embodiment of the present invention, the light absorbing material is preferably a non-conductive material.

The light absorbing material is not particularly limited to those described above, but may be, for example, a pigment or a dye. In one example, the light absorbing material may be any material capable of absorbing light in an entire range of wavelength or a specific wavelength range, and may be, but is not particularly limited to, for example, carbon black, carbon nanotube, fluorene (C6), a phthalocyanine derivative, a porphyrin derivative, a triphenylamine derivative or a mixture thereof. The light absorbing material is included at <NUM> to <NUM> parts by weight, in particular <NUM> to <NUM> parts by weight, <NUM> to <NUM> parts by weight, <NUM> to <NUM> parts by weight, <NUM> to <NUM> parts by weight, or <NUM> to <NUM> parts by weight with respect to <NUM> parts by weight of the encapsulation resin. As the light absorbing material is adjusted within the above range, when the encapsulation composition is applied to an OED, internal or external light may be effectively absorbed and blocked to prevent reflection or scattering of the light.

In yet another exemplary embodiment, the light absorbing material may be adjusted to absorb a light source in a specific wavelength range as needed.

The moisture barrier layer of the encapsulation film of the present invention includes a moisture absorbent. The term "moisture absorbent" includes all components which can adsorb or remove moisture or vapor permeated from an external environment through a physical or chemical reaction. That is, the moisture absorbent is a moisture reactive adsorbent.

The moisture reactive adsorbent adsorbs moisture or vapor by a chemical reaction with vapor, moisture or oxygen permeated into the encapsulation film.

A specific type of the moisture absorbent which can be used in the present invention is not particularly limited, and for example, the moisture reactive adsorbent may be one or a mixture of at least two of metal powders such as alumina, a metal oxide, a metal salt, and phosphorus pentoxide (P<NUM>O<NUM>), and the physical adsorbent may be silica, zeolite, titania, zirconia or montmorillonite.

Here, specifically, the metal oxide may be lithium oxide (Li<NUM>O), sodium oxide (Na<NUM>O), barium oxide (BaO), calcium oxide (CaO) or magnesium oxide (MgO), and the metal salt may be, but is not limited to, a sulfate such as lithium sulfate (Li<NUM>SO<NUM>), sodium sulfate (Na<NUM>SO<NUM>), calcium sulfate (CaSO<NUM>), magnesium sulfate (MgSO<NUM>), cobalt sulfate (CoSO<NUM>), gallium sulfate (Ga<NUM>(SO<NUM>)<NUM>), titanium sulfate (Ti(SO<NUM>)<NUM>) or nickel sulfate (NiSO<NUM>); a metal halide such as calcium chloride (CaCl<NUM>), magnesium chloride (MgCl<NUM>), strontium chloride (SrCl<NUM>), yttrium chloride (YCl<NUM>), copper chloride (CuCl<NUM>), cesium fluoride (CsF), tantalum fluoride (TaF<NUM>), niobium fluoride (NbF<NUM>), lithium bromide (LiBr), calcium bromide (CaBr<NUM>), cesium bromide (CeBr<NUM>), selenium bromide (SeBr<NUM>), vanadium bromide (VBr<NUM>), magnesium bromide (MgBr<NUM>), barium iodide (BaI<NUM>) or magnesium iodide (MgI<NUM>); or a metal chlorate such as barium perchlorate (Ba(ClO<NUM>)<NUM>) or magnesium perchlorate (Mg(ClO<NUM>)<NUM>), but the present invention is not limited thereto.

In the present invention, the moisture absorbent such as the metal oxide may be suitably processed, and mixed in the composition. For example, depending on the type of the OED to which the encapsulation film is applied, the encapsulating composition may be formed in the form of a thin film having a thickness of <NUM> or less, and in this case, a grinding process of the moisture absorbent may be needed. To grind the moisture absorbent, three-roll milling, bead milling or ball milling may be used.

The moisture barrier layer of the encapsulation film of the present invention may include the moisture absorbent at <NUM> to <NUM>, <NUM> to <NUM>, <NUM> to <NUM>, or <NUM> to <NUM> parts by weight with respect to <NUM> parts by weight of the encapsulation resin. However, as the content of the moisture absorbent is controlled to <NUM> parts by weight or more, a cured product may exhibit an excellent moisture and vapor barrier property. In addition, as the content of the moisture absorbent is controlled to <NUM> parts by weight or less, a thin film-type encapsulation structure may be formed, and an excellent moisture barrier property may be exhibited.

In the specification, unless particularly defined otherwise, the unit "parts by weight" means a weight ratio between components.

In an exemplary embodiment of the present invention, the moisture absorbent may be suitably controlled according to a structure for encapsulating an organic electronic element. For example, in a layer in contact with the organic electronic element, the moisture absorbent may be included at <NUM> to <NUM> % based on the total weight of the moisture absorbent in the encapsulation film. For example, as shown in <FIG> and <FIG>, when the element is in contact with one (the moisture barrier layer <NUM>) of the two moisture barrier layers <NUM> and <NUM>, which are sequentially stacked, during the encapsulation of the organic electronic element, the underlying moisture barrier layer <NUM> may include <NUM> to <NUM> % of the moisture absorbent based on the total weight of the moisture absorbent, and the upper moisture barrier layer <NUM> which is not in contact with the organic electronic element may include <NUM> to <NUM> % of the moisture absorbent based on the total weight of the moisture absorbent.

The light absorbing layer or moisture barrier layer of the encapsulation film of the present invention may include a filler, and preferably, an inorganic filler when needed. The filler may extend a movement path of moisture or vapor permeated into the encapsulation structure to inhibit the permeation, and maximize a barrier property to moisture and vapor through interaction with the matrix structure of the encapsulation resin and the moisture absorbent. A specific type of the filler which can be used in the present invention may be, but is not particularly limited to, for example, one or a mixture of at least two of clay, talc, and silica.

In addition, in the present invention, to increase binding efficiency to the filler and an organic binder, as the filler, a product whose surface is treated with an organic material may be used, or a coupling agent may be additionally added.

The light absorbing layer or moisture barrier layer of the encapsulation film of the present invention may include the filler at <NUM> to <NUM>, <NUM> to <NUM>, or <NUM> to <NUM> parts by weight with respect to <NUM> parts by weight of the encapsulation resin. In the present invention, the filler is an optional component, and may not be included in the encapsulation film. However, a content of the filler is controlled to <NUM> part by weight or more, and thus an encapsulation structure having an excellent moisture or vapor barrier property and physical properties may be provided. In addition, in the present invention, as the content of the filler is controlled to <NUM> parts by weight or less, the encapsulation film may be manufactured in a film shape, and even when the encapsulation film is manufactured in a thin film, a cured product may exhibit an excellent moisture barrier property.

The term "encapsulation structure" used herein may be the above-described encapsulation film having a multilayer structure, and may be a product for encapsulating an OED including an encapsulation film encapsulating an entire surface of the OED and an organic electronic element.

In addition, in one example, the encapsulation film may further include a dispersant such that the light absorbing material or the moisture absorbent may be uniformly dispersed. As the dispersant which can be used herein, for example, a nonionic surfactant having affinity to a surface of the light absorbing material, and compatibility with the encapsulation resin may be used.

In one exemplary embodiment of the present invention, the light absorbing layer of the encapsulation film may further include a curing agent according to a type of the encapsulation resin. For example, a curing agent which can form a crosslinking structure by a reaction with the above-described encapsulation resin, or an initiator which can initiate a curing reaction of the resin may be further included.

A suitable type of the curing agent may be selected and used according to a type of the encapsulation resin or a type of a functional group included in the resin.

As a curing agent of the epoxy resin known in the art, for example, one or at least two of an amine curing agent, an imidazole curing agent, a phenol curing agent, a phosphorus curing agent, and an acid anhydride curing agent may be used, but the present invention is not limited thereto.

In one example, as the curing agent, an imidazole compound which is a solid at room temperature, and having a melting point or degradation temperature of <NUM> or more may be used. Such a compound may be, but is not limited to, for example, <NUM>-methyl imidazole, <NUM>-heptadecyl imidazole, <NUM>-phenyl imidazole, <NUM>-phenyl-<NUM>-methyl imidazole, or <NUM>-cyanoethyl-<NUM>-phenyl imidazole.

A content of the curing agent may be selected according to, for example, the type or ratio of the encapsulation resin. For example, the curing agent may be included at <NUM> to <NUM>, <NUM> to <NUM>, or <NUM> to <NUM> parts by weight with respect to <NUM> parts by weight of the encapsulation resin. However, the weight ratio may be changed according to the type and ratio of the encapsulation resin or a functional group of the resin, or a crosslinking density to be realized.

When the encapsulation resin is a resin that may be cured by irradiation of active energy rays, as an initiator, for example, a cationic photopolymerization initiator may be used.

As the cationic photopolymerization initiator, an onium salt- or organometallic salt-series ionized cationic initiator, or an organic silane- or latent sulfonic acid-series ionized cationic photopolymerization initiator, or a non-ionized cationic photopolymerization initiator may be used. The onium salt-series initiator may be a diaryliodonium salt, a triarylsulfonium salt, or an aryldiazonium salt, the organometallic salt-series initiator may be iron arene, the organic silane-series initiator may be o-nitrobenzyl triaryl silyl ether, triaryl silyl peroxide, or acyl silane, and the latent sulfonic acid-series initiator may be α-sulfonyloxy ketone or α-hydroxymethylbenzoin sulfonate, but the present invention is not limited thereto.

In one example, as the cationic initiator, an ionized cationic photopolymerization initiator may be used.

In addition, when the encapsulation resin is a resin which can be cured by the irradiation of active energy rays, as an initiator, for example, a radical initiator may be used.

The radical initiator may be a photoinitiator or a thermal initiator. A specific type of the photoinitiator may be suitably selected in consideration of a curing speed and yellowing probability. For example, the photoinitiator may be a benzoin-, hydroxy ketone-, amino ketone-, or phosphine oxide-based photoinitiator, and specifically, benzoin, benzoin methylether, benzoin ethylether, benzoin isopropylether, benzoin n-butylether, benzoin isobutylether, acetophenone, dimethylamino acetophenone, <NUM>,<NUM>-dimethoxy-<NUM>-phenylacetophenone, <NUM>,<NUM>-diethoxy-<NUM>-phenylacetophenone, <NUM>-hydroxy-<NUM>-methyl-<NUM>-phenylpropane-<NUM>-one, <NUM>-hydroxy cyclohexylphenylketone, <NUM>-methyl-<NUM>-[<NUM>-(methylthio)phenyl]-<NUM>-morpholino-propane-<NUM>-one, <NUM>-(<NUM>-hydroxyethoxy)phenyl-<NUM>-(hydroxy-<NUM>-propyl)ketone, benzophenone, p-phenylbenzophenone, <NUM>,<NUM>'-diethylamino benzophenone, dichlorobenzophenone, <NUM>-methylanthraquinone, <NUM>-ethylanthraquinone, <NUM>-t-butylanthraquinone, <NUM>-aminoanthraquinone, <NUM>-methylthioxanthone, <NUM>-ethylthioxanthone, <NUM>-chlorothioxanthone, <NUM>,<NUM>-dimethylthioxanthone, <NUM>,<NUM>-diethylthioxanthone, benzyldimethylketal, acetophenone dimethylketal, p-dimethylamino benzoic acid ester, oligo[<NUM>-hydroxy-<NUM>-methyl-<NUM>-[<NUM>-(<NUM>-methylvinyl)phenyl]propanone], or <NUM>,<NUM>,<NUM>-trimethylbenzoyl-diphenyl-phosphineoxide.

A content of the initiator, like the curing agent, may be changed according to the type and ratio of the encapsulation resin or a functional group of the resin, or a crosslinking density to be realized. For example, the initiator may be included at <NUM> to <NUM> parts by weight or <NUM> to <NUM> parts by weight with respect to <NUM> parts by weight of the encapsulation resin.

The light absorbing layer or moisture barrier layer of the encapsulation film of the present invention may further include a high molecular weight resin. When the encapsulation composition of the present invention is molded in a film or sheet shape, the high molecular weight resin may serve to improve moldability. In addition, when a hot melting process is performed, the high molecular weight resin may serve as a high temperature viscosity controlling agent for controlling flowability.

A type of the high molecular weight resin which can be used herein is not particularly limited as long as the resin has compatibility with another component of the encapsulation resin. A specific example of the high molecular weight resin which can be used herein is a resin having a weight average molecular weight of <NUM>,<NUM> or more, for example, one or a mixture of at least two of a phenoxy resin, an acrylate resin, a high molecular weight epoxy resin, an ultra high molecular weight epoxy resin, a high polarity functional group-containing rubber, and a high polarity functional group-containing reactive rubber, but the present invention is not limited thereto.

When the high molecular weight resin is included in the encapsulation composition of the present invention, the content of the resin is adjusted according to a desired physical property, and is not particularly limited. For example, in the present invention, the high molecular weight resin may be included at approximately <NUM> parts by weight or less, preferably <NUM> parts by weight or less, and more preferably approximately <NUM> parts by weight or less, with respect to <NUM> parts by weight of the encapsulation resin. As the content of the high molecular weight resin of the present invention is controlled to <NUM> parts by weight or less, compatibility with each component of the resin composition may be effectively maintained, and thus the resin may serve as an adhesive.

In the encapsulation composition constituting the light absorbing layer or moisture barrier layer according to the present invention, various additives may be included according to a use, a type of the encapsulation resin and a process of manufacturing an encapsulation film which will be described below without affecting the effect of the present invention, in addition to the above-described components. For example, the encapsulation composition may include a coupling agent, a crosslinking agent, a curable material, a tackifier, a UV stabilizer or an antioxidant in a suitable range of contents according to desired physical properties. Here, the curable material may mean a material having a heat-curable functional group and/or an active energy ray-curable functional group separately included, other than the above-described components constituting the encapsulation composition. For example, the curable material may mean a compound including at least two of functional groups which can participate in polymerization by the irradiation of active energy rays, for example, a functional group including an ethylenically unsaturated double bond such as an acryloyl group or a methacryloyl group, and a functional group such as an epoxy group or an oxetane group.

In an exemplary embodiment of the present invention, the encapsulation film may further include a metal layer, in addition to the light absorbing layer or the moisture barrier layer. The metal layer according to an exemplary embodiment of the present invention may be transparent or opaque. The metal layer may be a thin film-type metal foil, or a layer formed by depositing a metal on a polymer base film. The metal layer may be formed of any material that can have thermal conductivity and a moisture barrier property without limitation. The metal layer may include any one of a metal, a metal oxide, a metal nitride, a metal carbide, a metal oxynitride, a metal oxyboride, and a mixture thereof. For example, the metal layer may include an alloy prepared by adding at least one metallic element or non-metallic element to one metal, for example, an iron-nickel alloy or stainless steel (SUS). In addition, in one example, the metal layer may include copper, aluminum, nickel, silicon oxide, aluminum oxide, titanium oxide, indium oxide, tin oxide, tin-indium oxide, tantalum oxide, zirconium oxide, niobium oxide, and a mixture thereof. The metal layer may be deposited by means of electrolysis, rolling, evaporation, electron beam evaporation, sputtering, reactive sputtering, chemical vapor deposition, plasma chemical vapor deposition, or electron cyclotron resonance source plasma chemical vapor deposition. In one exemplary embodiment of the present invention, the metal layer may be deposited by reactive sputtering. In one exemplary embodiment of the present invention, the encapsulation film including the metal layer may prevent reflection or scattering of external light in a non-deposited part of an electrical connection of the OED by the metal layer through a light absorbing region.

In one example, the metal layer may have a reflectance of <NUM> to <NUM>, <NUM> to <NUM>, or <NUM> to <NUM>% in a specular component included (SCI) measurement. In addition, the metal layer may have a reflectance of <NUM> to <NUM>, <NUM> to <NUM>, <NUM> to <NUM>, or <NUM> to <NUM>% in a specular component excluded (SCE) measurement. Here, the SCI denotes total reflectance, and the SCE denotes an irregular reflectance caused by scattering. The reflectance may be measured by a known method in the art using, for example, the CM2006d produced by Konika Minolta (measurement condition: any one of the predetermined values from M/I+E, M/SCI, M/SCE, S/I+E, S/SCI and S/SCE, any one of the predetermined values from UV <NUM> to <NUM> % , any one of the light sources from D65, D50, C, A, F2, F6, F7, F8, F10, F11 and F12, and an observation view of <NUM> ° or <NUM> °). Due to the difference in reflectance between the electrical metal connection of the OED and the metal layer, when the OED is observed by an observer from an external environment, the electrical connection is observed. Particularly, when the light absorbing layer includes a moisture absorbent or a filler, or the moisture barrier layer includes a moisture absorbent or a filler, the light absorbing layer or the moisture barrier layer serves as an intermediate layer in which light is scattered. Accordingly, an effect of reducing a reflectance of a polarizer formed on one surface of the OED is degraded, and thus a part without the electrical metal connection is seen blurred. Therefore, as described above, the encapsulation film including the metal layer may prevent reflection or scattering of external light from a non-deposited part of an electrical connection of the OED due to the metal layer through a light absorbing region.

The metal layer may have a thermal conductivity of <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, <NUM> W/mK or more, or <NUM> W/mK or more. As the metal layer has the above-described high thermal conductivity, heat generated at a contact interface in a process of contacting the metal layer may be more rapidly emitted. In addition, due to the high thermal conductivity, heat accumulated in the operation of the OED is rapidly emitted to an external environment, and thus a temperature of the OED may be maintained lower, and the generation of a crack and a defect is reduced.

The term "thermal conductivity" used herein is a degree of an ability of a material to deliver heat through conduction, and a unit may be W/mK. The unit shows the degree in which a material delivers heat at the same temperature and distance, and is a unit of heat (watt) with respect to the unit of a distance (meter) and the unit of a temperature (Kelvin).

A structure of the encapsulation film of the present invention may be, but is not particularly limited to, for example, a structure including a base film or a releasing film (hereinafter, also referred to as a "first film"); and the light absorbing layer or the moisture barrier layer formed on the base film or the releasing film.

The encapsulation film of the present invention may further include a base film or a releasing film (hereinafter, also referred to as a "second film") formed on the light absorbing layer or moisture barrier layer.

A specific type of the first film which can be used in the present invention is not particularly limited. In the present invention, as the first film, for example, a polymer film generally used in the art may be used. In the present invention, for example, as the base or releasing film, a polyethyleneterephthalate film, a polytetrafluoroethylene film, a polyethylene film, a polypropylene film, a polybutene film, a polybutadiene film, a vinylchloride copolymer film, a polyurethane film, an ethylene-vinyl acetate film, an ethylene-propylene copolymer film, an ethylene-ethyl acrylate copolymer film, an ethylene-methyl acrylate copolymer film or a polyimide film may be used. In addition, one or both surfaces of the base film or releasing film of the present invention may be treated with suitable releasing treatment. As an example of a releasing agent used in the releasing treatment for the base film, an alkyd-, silicone-, fluorine-, unsaturated ester-, polyolefin- or wax-based releasing agent may be used, and in terms of thermal resistance, an alkyd-, silicone- or fluorine-based releasing agent is preferably used, but the present invention is not limited thereto.

In addition, a type of the second film which can be used in the present invention (hereinafter, referred to as a "cover film") is not particularly limited, either. For example, in the present invention, as the second film, in the above-listed category of the first film, the same or different type of film, compared to the first film, may be used. In addition, in the present invention, the second film may also be treated with a suitable releasing treatment.

In the present invention, a thickness of the above-described base film or releasing film (first film) may be, but is not particularly limited to, suitably selected according to a use. For example, the thickness of the first film in the present invention may be approximately <NUM> to <NUM>, and preferably <NUM> to <NUM>. When the thickness is less than <NUM>, the base film may be easily deformed in a manufacturing process, and when the thickness is more than <NUM>, economic feasibility is degraded.

In the present invention, a thickness of the second film is not particularly limited, either. In the present invention, for example, the thickness of the second film may be set the same as the first film. In the present invention, in consideration of processibility, the thickness of the second film may be set relatively smaller than that of the first film.

A thickness of the light absorbing layer or the moisture barrier layer included in the encapsulation film of the present invention is not particularly limited, and may be suitably selected according to the following condition in consideration of a use to which the film is applied. The thickness of the light absorbing layer or moisture barrier layer included in the encapsulation film of the present invention may be approximately <NUM> to <NUM>, and preferably <NUM> to <NUM>.

In the present invention, a method of manufacturing the encapsulation film is not particularly limited. For example, the encapsulation film may be manufactured by a method including a first operation of coating a base film or a releasing film with a coating solution including the above-described encapsulation composition; and a second operation of drying the coating solution coated in the first operation.

A method of stacking a light absorbing layer or a moisture barrier layer is not particularly limited. For example, the light absorbing layer or the moisture barrier layer formed on a separate releasing film may be laminated, thereby forming an encapsulation film having a multilayer structure, and a moisture barrier layer may be directly formed on the light absorbing layer, or vice versa.

In the method of manufacturing an encapsulation film of the present invention, a third operation of additionally pressing a base film or a releasing film on the coating solution dried in the second operation may be further included.

The first operation of the present invention is to prepare a coating solution by dissolving or dispersing the above-described encapsulation composition in a suitable solvent. In this operation, a content of the encapsulation resin included in the coating solution may be suitably controlled according to a desired moisture barrier property and film moldability.

A type of the solvent used in the preparation of the coating solution in the present invention is not particularly limited. However, when a drying time of the solvent is excessively long, or drying at a high temperature is needed, problems in workability or durability of the encapsulation film may occur, and thus a solvent having a volatilization temperature of <NUM> or less is preferably used. In the present invention, in consideration of film moldability, a small amount of a solvent having a volatilization temperature in the above range or more may be mixed. An example of the solvent which can be used in the present invention, one or a mixture of at least two of methylethylketone (MEK), acetone, toluene, dimethylformamide (DMF), methylcellosolve (MCS), tetrahydrofuran (THF) or N-methylpyrrolidone (NMP) may be used, but the present invention is not limited thereto.

In the first operation of the present invention, a method of coating a base film or a releasing film with the coating solution may be, but is not particularly limited to, for example, a known method such as knife coating, roll coating, spray coating, gravure coating, curtain coating, comma coating or lip coating.

The second operation of the present invention is to form a light absorbing layer or a moisture barrier layer by drying the coating solution coated in the first operation. That is, in the second operation of the present invention, the light absorbing layer or the moisture barrier layer may be formed by drying and removing the solvent by heating the coating solution coated on the film. Here, a drying condition is not particularly limited, and for example, the drying may be performed at <NUM> to <NUM> for <NUM> to <NUM> minutes.

In the method of manufacturing an encapsulation film of the present invention, after the second operation, a third operation of pressing an additional base film or releasing film on the light absorbing layer or moisture barrier layer formed on the film may be further performed.

The third operation of the present invention may be performed by pressing an additional releasing film or base film (cover film or second film) on the light absorbing layer or moisture barrier layer formed by coating the film with the coating solution and drying the coated layer though hot roll lamination or pressing.

In addition, as shown in <FIG>, the present invention relates to an OED including a substrate <NUM>; an organic electronic element <NUM> including a transparent electrode layer present on the substrate, an organic layer present on the transparent electrode layer and including at least an emitting layer and a reflective electrode layer present on the organic layer; and an encapsulation film <NUM> encapsulating an entire surface of the organic electronic element <NUM>, and having a light absorbing region having a light transmittance of <NUM> % or less with respect to a visible light region.

The organic layer may be formed in various structures further including various functional layers known in the art as long as including an emitting layer. A layer which can be included in the organic layer may be an electron injection layer, a hole blocking layer, an electron transport layer, a hole transport layer, and a hole injection layer.

Various materials and methods of forming the same known in the art may be used to form a hole or electron injection electrode layer and an organic layer, for example, an emitting layer, an electron injection or transport layer, or a hole injection or transport layer, but the present invention is not limited thereto.

The organic electronic element <NUM> of the present invention may be an OLED.

In one example, the OED according to the present invention may be a bottom-emitting OED.

The OED may further include a protective film protecting the organic electronic element between the encapsulation film and the organic electronic element.

In addition, the OED may include an encapsulation film further including a metal layer, and in this case, a cover substrate which will be described below may be omitted.

In yet another embodiment of the present invention, a method of manufacturing an OED includes forming an organic electronic element including a transparent electrode layer, an organic layer present on the transparent electrode layer and including at least an emitting layer and a reflective electrode layer present on the organic layer on a substrate; and applying the above-described encapsulation film to the substrate on which the organic electronic element is formed to encapsulate an entire surface of the organic electronic element.

The operation of applying the encapsulation film to the OED may be performed by hot roll lamination, hot pressing or vacuum pressing of the encapsulation film, but the present invention is not particularly limited thereto.

The operation of applying the encapsulation film to the OED may be performed at <NUM> to <NUM>, and then curing may be performed thereon by heating at a temperature range of <NUM> to <NUM> or irradiating UV rays.

<FIG> is a cross-sectional view of an OED according to an exemplary embodiment of the present invention.

According to the method of manufacturing an OED in the present invention, for example, a transparent electrode is formed on the substrate <NUM> such as a glass or a film by vacuum deposition or sputtering, and an organic material layer is formed on the transparent electrode. The organic material layer may include a hole injection layer, a hole transport layer, an emitting layer, an electron injection layer and/or an electron transport layer. Subsequently, a second electrode is further formed on the organic material layer. Afterward, the above-described encapsulation film <NUM> is applied to an upper portion of an OED <NUM> on the substrate <NUM> to entirely cover the OED <NUM>. Here, the method of applying the encapsulation film <NUM> is not particularly limited, and may be heating, pressing or autoclaving a cover substrate <NUM> (e.g., a glass or a polymer film) to which the encapsulation film <NUM> of the present invention is previously transferred, for example, on the OED <NUM> formed on the substrate <NUM>. In this operation, for example, when the encapsulation film <NUM> is transferred to the cover substrate <NUM>, after a base or releasing film formed on the film may be delaminated, the encapsulation film <NUM> may be transferred to the cover substrate <NUM> through a vacuum press or a vacuum laminator while heated. In this operation, when curing of the encapsulation film <NUM> is performed in a predetermined range or more, a cohesive strength or an adhesive strength of the encapsulation film <NUM> may be decreased, and thus a process temperature may be controlled at approximately <NUM> or less, and a process time may be controlled within <NUM> minutes. Similarly, even when the cover substrate <NUM> to which the encapsulation film <NUM> is transferred is applied to the OED <NUM> through thermal pressing, a vacuum press or a vacuum laminator may be used. A temperature condition in this operation may be set as described above, and a process time may be set within <NUM> minutes.

In addition, in the present invention, an additional curing process may be performed on the encapsulation film to which the OED is pressed, and such a curing process (main curing) may be performed, for example, in a heating chamber or a UV chamber, and preferably a heating chamber. A condition of the main curing may be suitably selected in consideration of stability of the OED.

However, the above-described manufacturing process is merely an example to encapsulate the OED of the present invention, and the process sequence or process condition may be changed without limitation. For example, in the present invention, a sequence of the transferring and pressing processes may be changed into transferring the encapsulation film <NUM> of the present invention to the OED <NUM> on the substrate <NUM>, and pressing the cover substrate <NUM>. In addition, a protective layer may be formed on the OED <NUM>, the encapsulation film may be applied to the protective layer, and then curing may be performed thereon without the cover substrate <NUM>.

When an OED is encapsulated using an encapsulation film according to exemplary embodiments of the present invention, an excellent moisture barrier property can be realized, and as reflection or scattering of light is prevented by absorbing and blocking internal or external light, external defects of the OED can be prevented.

Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to examples according to the present invention and a comparative Example not according to the present invention. However, the scope of the present invention is not limited to the embodiments which will be disclosed below.

A carbon black dispersed solution was prepared by adding carbon black (#<NUM> Mitsubishi Carbon black) having a primary particle size of approximately <NUM> or less as a light absorbing material and methylethylketone (MEK) as a solvent in a solid concentration of <NUM> wt%. Meanwhile, a moisture absorbent solution was prepared by adding <NUM> of calcined dolomite as a moisture absorbent and MEK as a solvent in a solid concentration of <NUM> wt%.

<NUM> of a silane-modified epoxy resin (KSR-<NUM>, Kukdo Chemical Co. ) and <NUM> of a phenoxy resin (YP-<NUM>, Tohto Kasei Co. ) were added to a reactor at room temperature, and diluted with MEK. A solution for a light absorbing layer was prepared by adding <NUM> of an imidazole (Shikoku Chemicals Corporation) as a curing agent to the homogenized solution, and stirring the resulting solution at a high speed for <NUM> hour. The solution for a light absorbing layer was prepared by adding the previously prepared moisture absorbent solution to the solution to have a content of calcined dolomite of <NUM> parts by weight with respect to <NUM> parts by weight of an encapsulation resin of a light absorbing layer, adding the carbon black dispersed solution to have a carbon black content of <NUM> parts by weight with respect to <NUM> parts by weight of the encapsulation resin of a light absorbing layer, and mixing the solutions.

An encapsulation film was manufactured by forming the light absorbing layer having a thickness of <NUM> by coating a releasing surface of a releasing PET film with the solution of the light absorbing layer and drying the coated solution at <NUM> for <NUM> minutes.

A carbon black dispersed solution was prepared by adding carbon black (#<NUM> Mitsubishi Carbon black) having a primary particle size of approximately <NUM> or less as a light absorbing material and MEK as a solvent in a solid concentration of <NUM> wt%.

<NUM> of a silane-modified epoxy resin (KSR-<NUM>, Kukdo Chemical Co. ) and <NUM> of a phenoxy resin (YP-<NUM>, Tohto Kasei Co. ) were added to a reactor at room temperature, and diluted with MEK. A solution for a light absorbing layer was prepared by adding <NUM> of an imidazole (Shikoku Chemicals Corporation) as a curing agent to the homogenized solution, and stirring the resulting solution at a high speed for <NUM> hour. The solution for a light absorbing layer was prepared by adding and mixing the previously prepared carbon black dispersed solution to the resulting solution to have a carbon black content of <NUM> parts by weight with respect to <NUM> parts by weight of an encapsulation resin of a light absorbing layer.

Meanwhile, a moisture absorbent solution was prepared by adding <NUM> of calcined dolomite as a moisture absorbent and MEK as a solvent at a solid content of <NUM> wt%.

<NUM> of a silane-modified epoxy resin (KSR-<NUM>, Kukdo Chemical Co. ) and <NUM> of a phenoxy resin (YP-<NUM>, Tohto Kasei Co. ) were added to a reactor at room temperature, and diluted with MEK. A moisture barrier layer solution was prepared by adding <NUM> of an imidazole (Shikoku Chemicals Corporation) as a curing agent to the homogenized solution, and stirring the resulting solution at a high speed for <NUM> hour. The previously prepared moisture absorbent solution was added to the solution to have a content of calcine dolomite of <NUM> parts by weight with respect to <NUM> parts by weight of the encapsulation resin of the moisture barrier layer.

A moisture barrier layer having a thickness of <NUM> was formed by coating a releasing surface of a releasing PET film with the solution of the moisture barrier layer, and drying the resulting surface at <NUM> for <NUM> minutes. According to the same method as described above, a light absorbing layer having a thickness of <NUM> was formed by coating a releasing surface of a releasing PET film with the solution of the light absorbing layer, and drying the resulting surface at <NUM> for <NUM> minutes. The moisture barrier layer and the light absorbing layer were laminated, thereby manufacturing an encapsulation film having a bilayer structure including the moisture barrier layer and the light absorbing layer.

A moisture barrier layer having a thickness of <NUM> was formed by coating a releasing surface of a releasing PET film with the solution of the moisture barrier layer prepared in Example <NUM>, and drying the resulting surface at <NUM> for <NUM> minutes. According to the same method as described above, a light absorbing layer having a thickness of <NUM> was formed by coating a releasing surface of a releasing PET film with the solution of the light absorbing layer prepared in Example <NUM>, and drying the resulting surface at <NUM> for <NUM> minutes.

The moisture barrier layer and the light absorbing layer were laminated to have a triple layer structure including the light absorbing layer/moisture barrier layer/light absorbing layer, thereby manufacturing an encapsulation film.

An encapsulation film was manufactured by the same method as described in Example <NUM>, except that a carbon black dispersed solution was added to have a carbon black content of <NUM> part by weight with respect to <NUM> parts by weight of an encapsulation resin of a light absorbing layer.

An encapsulation film was manufactured by the same method as described in Example <NUM>, except that the moisture absorbent was added to have a content of <NUM> parts by weight with respect to <NUM> parts by weight of an encapsulation resin.

An encapsulation film was manufactured by the same method as described in Example <NUM>, except that a carbon black dispersed solution was added to have a carbon black content of <NUM> parts by weight with respect to <NUM> parts by weight of an encapsulation resin of a light absorbing layer.

A light transmittance of a light absorbing region of the film manufactured above was measured at <NUM> using an UV-Vis spectrometer. When the film was formed in a single layer structure, the light transmittance was measured on the light absorbing region of a light absorbing layer in a thickness direction, and when the film was formed in a multilayer structure, the light transmittance was measured on the light absorbing region in a thickness direction in a state in which a plurality of layers were stacked.

An OED was manufactured by applying the encapsulation film manufactured according to the Examples or Comparative Example to an entire surface of an organic electronic element formed on a glass, and an electrical metal connection was connected to the OED. Specifically, a transparent electrode was formed on the glass by vacuum deposition, and an organic material layer was formed on the transparent electrode. The organic material layer includes a hole injection layer, a hole transport layer, an emitting layer, an electron injection layer and an electron transport layer. Subsequently, a reflective electrode was further formed on the organic material layer. Afterward, the encapsulation film manufactured in the Examples or Comparative Example was applied to an upper portion of the organic electronic element on the glass to cover all of the organic electronic elements (the transparent electrode, the reflective electrode and the organic material layer) (removal of releasing PET). Meanwhile, the encapsulation film is an encapsulation film which was manufactured by laminating a copper film having a thickness of <NUM> on one surface of the light absorbing layer and/or the moisture barrier layer (the copper film has one surface (glossy surface) having a reflectance of <NUM>% and the other surface (rough surface) having a reflectance of <NUM>% in Specular Component Included SCI measurement. In addition, the copper film has one surface (glossy surface) having a reflectance of <NUM>%, and the other surface (rough surface) having a reflectance of <NUM>% in Specular Component Excluded SCE measurement).

When the OED was placed on a white background, and viewed from approximately <NUM> (illuminance of <NUM> lux or more), observation was performed whether the electrical connection was detected or not detected with the naked eye. When the electrical connection was detected with the naked eye, it was denoted as O, and when the electrical connection was not detected with the naked eye, it was denoted as X.

Claim 1:
An encapsulation film (<NUM>) for organic electronic element, comprising:
a light absorbing layer (<NUM>) comprising a light absorbing region (<NUM>) comprising an encapsulation resin which is a heat-curable resin or a photocurable resin and a light absorbing material (<NUM>), and having a light transmittance of <NUM> % or less with respect to a visible light region, and
a moisture barrier layer (<NUM>) comprising a moisture reactive adsorbent (<NUM>);
wherein the curable resin is a silane-modified epoxy resin;
wherein the light absorbing material (<NUM>) is comprised at <NUM> to <NUM> parts by weight with respect to <NUM> parts by weight of the encapsulation resin.