Patent Description:
It is estimated that about <NUM>% of the world wide population uses spectacles for some sort of vision correction. This number is much higher if contact lenses and spectacles which do not primarily have a correction function are also considered, for example, safety spectacles, sunglasses, and swimming goggles. Most spectacles have some sort of frame to hold a pair of lenses in place, so that when the frame is rested on facial features (e.g. nose and ears), the lenses are placed in front to the eyes. Most types of known spectacles adjust the light and/or image to be received by an observer wearing the spectacles, and may further have aesthetical and ergonomic features.

Today, digital devices have become part of everyone's daily life, bringing a lot of convenience and benefits for the users. However, there are also certain risks associated with the use of digital devices, e.g. eye fatigue, deterioration of vision, etc. Actually, many parents believe that inappropriate usage of digital devices would cause myopia progression, or early onset of myopia, for their kids. Many people may require lenses for correcting myopia or to control progression of myopia.

Thus, there is a need to provide for means for reducing myopia onset and/or controlling progression.

Today, most digital multi-function devices (e.g., smartphones, tablets) already have their built-in proximity sensors. Such proximity sensors emit infrared light and by measuring the reflected infrared light from an object, the distance between the proximity sensor and the object can be determined. The most common use of this function is to determine whether a phone is placed near the user's ear during a phone call. In this situation, the proximity sensor may activate a background application which will turn off the digital screen in order to avoid undesirable operations from accidental touch on the screen.

The present invention intends to provide a user wearable optical articles with a interferential coating to enhance the reflection of a NIR signal reflected by the user wearable optical article, thus the user wearable optical article may be used in connection with a digital screen to indicate the distance between the screen and the user wearable optical article, and therefore the distance between the digital screen and user's eye(s). Such distance may be used to alert the user that his reading distance is not within an optimal or healthy range.

In order to achieve high reflection of NIR radiation, various solutions have been proposed in the prior art. One known prior-art solution, as presented in documents <CIT>, <CIT> and <CIT>, is the multilayer (usually more than <NUM> layers) quarter-wave reflection stacks, consisting of alternative high index and low index layers. As implied by the name, optical thickness of each layer in such stacks is λ/<NUM> except the outmost low index layer being λ/<NUM>, where λ is the targeted center-wavelength of the reflection band. Sometimes such quarter-wave stacks also start with a λ/<NUM> inner-most low index layer. <FIG> of the present invention also depict some examples of such quarter-wave reflection stacks. The peak position of the reflection band can be easily adjusted by changing the value of center-wavelength λ. The maximum reflectance of such coatings increases with increasing the number of quarter-wave layers in the stacks, and can even approach <NUM>% if there are sufficient number of layers. However, in order to have a sufficient reflectance (e.g. ><NUM>% at <NUM> or <NUM>), the overall thickness of the quarter-wave reflection stacks is very thick, typically ≥ <NUM>, which is not applicable for common organic substrates used for the user wearable optical article. Moreover, the reflectance value (Rv) of these quarter-wave reflection stacks is typically around <NUM>% or higher.

Another prior-art solution for achieving high NIR reflection is by the general interferential multilayer stacks, in which optical thickness of all layers can be very different from each other, no longer limited to λ/<NUM>. Documents <CIT> and <CIT> for example disclose some multilayer interferential AR stacks with high NIR reflection. The AR stacks designing strategy in these documents is to maximize mean reflection in NIR region (RmNIR) from <NUM> to <NUM> while keeping anti-reflective effect in visible light region. Under such designing strategy, it is hard to achieve high reflectance (~<NUM>%) at a specific interesting wavelength, e.g. <NUM> or <NUM>, with a restriction of total thickness of the AR stacks (e.g. <<NUM>). The reflection at the interesting wavelength, <NUM> or <NUM>, of all the example AR stacks in those documents is less than <NUM>%.

It's an objective of the invention to address the above problems.

The claimed invention is as defined in independent claim <NUM> and claim <NUM>. Optional features are defined in the dependent claims.

According to various embodiments, the interferential coating may include at least two low refractive index layers and at least two high refractive index layers, wherein the low refractive index layers and the high refractive index layers are in an alternating sequence, for example as a stack of layers. The low refractive index layers may be layers of low refractive index material. The high refractive index layers may be layers of high refractive index material. The low refractive index layers may have a refractive index lower than the high refractive index layers. Each of the low refractive index layers may have a refractive index lower than <NUM> and each of the high refractive index layers may have a refractive index higher than <NUM>.

According to various embodiments, the stack of layers may be, for example, a quarter wavelength stack also named herein as quarter wave interferential coating, or an anti-reflection (AR) stack also named herein as anti-reflection interferential coating. Anti-reflection may mean reducing reflection in at least a portion of the visible spectrum, for example in the whole visible spectrum. The stacks are optimized for enhanced reflection in the near infra-red.

According to various embodiments, the ratio of a highest refractive index amongst the high refractive index layers to a lowest refractive index amongst the low refractive index layers may be greater than <NUM>, for example greater than <NUM>.

According to various embodiments, the low refractive index layers may have a low refractive index material composition of a first refractive index and a first thickness, and the high refractive index layers may have a high refractive index material composition of a second refractive index different from the first refractive index and a second thickness different from the first thickness.

According to various embodiments, the interferential coating may include low refractive index layers and high refractive index layers in an alternating sequence. The optical thickness of each layer of the low refractive index layers may equal to a quarter of a targeted center reflection wavelength. The optical thickness of each layer of the high refractive index layers may equal to a quarter of a targeted center reflection wavelength. The interferential coating may include an outer high refractive index layer, which is furthest from the optical substrate amongst the high refractive index layers. The interferential coating may further include an outer low refractive index layer which is disposed on the outer high refractive index layer on a side which is distal from the optical substrate. The outer low refractive index layer may have an optical thickness equal to one-eighth of the targeted wavelength.

According to various embodiments, the multilayered interferential coating may include at least <NUM> layers.

According to various embodiments, a reflectance of the interferential coating at <NUM> and/or a reflectance of the interferential coating at <NUM> is at least <NUM>%, for example at least <NUM>%.

According to various embodiments, the peak reflectance of the optical filter is at <NUM> +/- <NUM> or at <NUM> +/- <NUM>.

According to various embodiments, the optical article may be an article selected from the group of: spectacle lens, sunglasses lens, contact lens, optical lens of a head mounted device, optical lens of an augmented reality device, optical lens of a virtual reality device.

According to various embodiments, the optical filter may have a reflectance value (Rv) equal or lower than <NUM>%, for example equal or lower than <NUM>%, for example equal or lower than <NUM>%.

According to various embodiments the optical article may be for use in the prevention or treatment of asthenopia and/or myopia.

A second aspect of the claimed invention concerns an eyewear including an optical article according to various embodiments.

A third aspect of the claimed invention concerns a method for producing an optical article. The method may include providing the optical substrate. The method may further include providing the interferential coating disposed on at least one of the front main face and rear main face of the optical substrate. The interferential coating may be configured to selectively reflect light of at least one range of wavelengths of an incident light in the near infrared light spectrum. A peak reflectance measured at <NUM> or <NUM> at a substantially normal to the optical substrate may be at least <NUM>%. The total thickness of the interferential coating is equal to or less than <NUM>, optionally equal to or less than <NUM>, and optionally equal to or less than <NUM>.

According to various embodiments the method may further include obtaining a product model designation of a multi-purpose mobile computing device (for example a smartphone) including an infrared proximity sensor. The method may further include obtaining from a pre-populated database an operating wavelength of the infrared proximity sensor, or a value derived thereof. In the method, the providing the interferential coating may include providing the at least one range of wavelengths of incident light in the near infrared light spectrum to overlap with the operating wavelength of the infrared proximity sensor.

Embodiments of the invention will now be described, by way of example, and with reference to the following drawings in which:.

The figures are of schematic nature and elements therein may be of different scale or positioned differently to improve readability.

In the description, which follows, the drawing figures are not necessarily to scale and certain features may be shown in generalized or schematic form in the interest of clarity and conciseness or for informational purposes. In addition, although making and using various embodiments are discussed in detail below, it should be appreciated that as described herein are provided many inventive concepts that may be embodied in a wide variety of contexts within the scope of the appended claims. Embodiments discussed herein are merely representative and not limiting.

The term "user wearable optical article" or simply "optical article", as used herein, and in accordance with various embodiments, may refer to an optical article configured to be worn by a user, for example, in front of a user's eye. For example, the user wearable optical article may be selected from the group of: spectacle lens, sunglasses lens, contact lens, optical lens of a head mounted device, optical lens of an augmented reality device, optical lens of a virtual reality device. A "lens", according to various embodiments, may have corrective power or may not have corrective power (e.g. a plano lens).

The term "eyewear", as used herein and according to various embodiments, may refer to an object to be worn on/in relation to the eye, for example spectacles. An eyewear according to various embodiments, may include a user wearable optical article, for example one or more user wearable optical articles. The eyewear may be selected from the group of: spectacles, sunglasses, head mounted device, augmented reality device, virtual reality device.

The expression "visible spectrum", as used herein and according to various embodiments, may be defined as light having wavelength in vacuum from <NUM> to <NUM>.

The expression "near infrared spectrum" (or abbreviated NIR spectrum), as used herein and according to various embodiments, may be defined as light having a wavelength in vacuum longer than <NUM> and shorter or equal to <NUM>, for example shorter than <NUM>, optionally from <NUM> to <NUM>.

According to various embodiments, Rv is described and may be may be determined with the equation below, where R(λ) is the reflectance at wavelength of λ, V(λ) is the eye sensitivity function in CIE <NUM>, and D65(λ) is the daylight illuminant defined in standard CIE S005/E-<NUM>.

<FIG> shows a schematic illustration of a user wearable optical article <NUM> including an optical substrate <NUM> and an interferential coating <NUM>, in accordance with various embodiments. The user wearable optical article <NUM>, may include an optical substrate <NUM> and an interferential coating <NUM>. The optical substrate <NUM> may have a front main face <NUM> and a rear main face <NUM> on opposite sides, wherein the front main face <NUM> is for facing the user when wearing the optical article <NUM>. The interferential coating <NUM> may be disposed on at least one of the front main face <NUM> and rear main face <NUM> and may be configured to selectively reflect light of at least one range of wavelengths of an incident light I1 in the near infrared light spectrum. A peak reflectance measured at a substantially normal to the optical article may be at least <NUM>%. The expression "substantially normal", as used herein and according to various embodiments, may mean within an angle of <NUM> degrees from the geometric normal to a surface on which light may be incident, e.g., surface <NUM> of the user wearable optical article at the point where light I1 is incident.

According to various embodiments, the optical substrate may include, for example, be composed of: transparent materials, transparent mineral glass, transparent organic materials. An organic substrate may include, for example, be composed of: thermoset or thermoplastic materials, for example, commercially available material: Orma, <NUM>, MR8, MR7, polycarbonate. Alternatively or in addition to transparent materials, the optical substrate may include, for example, be composed of, tinted materials, for example substrate for sunglasses. The term "transparent" may mean a peak transmittance of at least <NUM>%, preferably at least <NUM>%, in any or all concerned wavelengths, for example in the visible spectrum. In examples, the substrate thickness may be selected from the range of <NUM> to <NUM>.

According to various embodiments, the interferential coating may include at least two low refractive index layers and at least two high refractive index layers, wherein the low refractive index layers and the high refractive index layers are in an alternating sequence. The low refractive index layers may be layers of low refractive index material. The high refractive index layers may be layers of high refractive index material. The low refractive index layers may have a refractive index lower than the high refractive index layers.

An exemplary interferential coating <NUM> on an optical substrate <NUM> is schematically illustrated in <FIG>. According to various embodiments, the interferential coating may include low refractive index layers m1 and high refractive index layers m2 in an alternating sequence forming a stack. The interferential coating <NUM> of <FIG> includes low refractive index layers m1 and high refractive index layers m2, which form a stack <NUM>. Except for the first and last layers of the stack, each of the low refractive index layers m1 may be in contact with two high refractive index layers m2 and vice-versa. The optical thickness of each layer of the low refractive index layers m1 may equal to a quarter of a targeted center reflection wavelength. The optical thickness of each layer of the high refractive index layers m2 may equal to a quarter of a targeted center reflection wavelength. The interferential coating <NUM> may include an outer low refractive index layer <NUM> which is disposed on the outer high refractive index layer on a side which is distal from the optical substrate <NUM>. The outer low refractive index layer <NUM> may have an optical thickness equal to one-eighth of the targeted wavelength. The outer low refractive index layer <NUM>, may be configured to, for example, optically interface the stack <NUM> with air.

In some embodiments, the low refractive index layers may have a low refractive index material composition of a first refractive index and a first thickness, and the high refractive index layers may have a high refractive index material composition of a second refractive index different from the first refractive index and a second thickness different from the first thickness. For example, each of the low refractive index layers may have the low refractive index material composition of the first refractive index and may have the first thickness; each of the high refractive index layers may have the high refractive index material composition of the second refractive index and may have the second thickness.

Each of the low refractive index layers may have a refractive index lower than <NUM> and each of the high refractive index layers may have a refractive index higher than <NUM>. Low refractive index layers may include or be formed of: SiO<NUM>, SiO2-Al2O3 composite with less than <NUM> mol% of Al<NUM>O<NUM>, MgF<NUM>, and their mixtured. High refractive index layers may include or be formed of: SiN, TiO<NUM>, Nb<NUM>O<NUM>, ZrO<NUM>, Ta<NUM>O<NUM>, Nd<NUM>O<NUM>, Pr<NUM>O<NUM>, PrTiO<NUM>, La<NUM>O<NUM>, and their mixtures. According to various embodiments, the refractive index of a material, if not otherwise defined, refers to the refractive index of the material in vacuum at the wavelength of <NUM>.

<FIG> show examples of interferential coatings according to some embodiments including quarter wavelength stacks.

<FIG> shows a table with a layer configuration of an interferential coating optimized for <NUM>, the columns from left to right represent: material composition, optical thickness in wavelengths of <NUM>, and physical thickness in nanometers (nm). In <FIG>, the interferential coating includes a stack of alternated SiO<NUM> as low refractive index layers and SiN layers as high refractive index layers. The optical thickness of each of the low refractive index layers and the high refractive index layers is <NUM>. The physical thickness of each of the low refractive index layers is <NUM>, and the physical thickness of each of the high refractive index layers is <NUM>. The interferential coating further includes an outer low refractive index layer (first line of the table) of SiO<NUM> with optical thickness of <NUM> and physical thickness of <NUM>. <FIG> also shows reflectance plots as function of the wavelength for the interference coatings with a stack varying from <NUM> layers (<NUM>), <NUM> layers, <NUM> layers, <NUM> layers, and <NUM> layers (<NUM>). The number of layers increases from bottom up. As can be seen, with the exemplary configuration of <FIG>, a stack of <NUM> or more layers provides a peak reflectance measured at a substantially normal to the optical article is at least <NUM>%.

<FIG> shows another table with a layer configuration of an interferential coating optimized for <NUM>, the columns from left to right represent: material composition, optical thickness in wavelengths of <NUM>, and physical thickness in nanometers (nm). In <FIG>, the interferential coating includes a stack of alternated SiO<NUM> as low refractive index layers and SiN layers as high refractive index layers. The optical thickness of each of the low refractive index layers and the high refractive index layers is <NUM>. The physical thickness of each of the low refractive index layers is <NUM>, and the physical thickness of each of the high refractive index layers is <NUM>. The interferential coating further includes an outer low refractive index layer (first line of the table) of SiO<NUM> with optical thickness of <NUM> and physical thickness of <NUM>. <FIG> also shows reflectance plots as function of the wavelength for the interference coatings with a stack varying from <NUM> layers (<NUM>), <NUM> layers, <NUM> layers, <NUM> layers, and <NUM> layers (<NUM>). The number of layers increases from bottom up. As can be seen, with the exemplary configuration of <FIG>, a stack of <NUM> or more layers provides a peak reflectance measured at a substantially normal to the optical article is at least <NUM>%.

<FIG> show the structure and reflection spectra of SiN/SiO<NUM> quarter-wavelength reflection filters. It is noted that reflectance at <NUM> or <NUM> of these reflection filter increases gradually with increasing the number of layers of the stacks, while the mean reflectance in visible region changes little, with Rv remaining at around <NUM>%. With about <NUM> layers (<NUM> layers of SiN and <NUM> layers SiO<NUM>), about <NUM>% reflectance at <NUM> or <NUM> can be achieved.

<FIG> shows another table with a layer configuration of an interferential coating optimized for <NUM>, the columns from left to right represent: material composition, optical thickness in wavelengths of <NUM>, and physical thickness in nanometers (nm). In <FIG>, the interferential coating includes a stack of alternated SiO<NUM> as low refractive index layers and ZrO<NUM> layers as high refractive index layers. The optical thickness of each of the low refractive index layers and the high refractive index layers is <NUM>. The physical thickness of each of the low refractive index layers is <NUM>, and the physical thickness of each of the high refractive index layers is <NUM>. The interferential coating further includes an outer low refractive index layer (first line of the table) of SiO<NUM> with optical thickness of <NUM> and physical thickness of <NUM>. <FIG> also shows reflectance plots as function of the wavelength for the interference coatings with a stack varying from <NUM> layers (<NUM>), <NUM> layers, <NUM> layers, <NUM> layers, and <NUM> layers (<NUM>). The number of layers increases from bottom up. As can be seen, with the exemplary configuration of <FIG>, a stack of <NUM> or more layers provides a peak reflectance measured at a substantially normal to the optical article is at least <NUM>%.

<FIG> shows another table with a layer configuration of an interferential coating optimized for <NUM>, the columns from left to right represent: material composition, optical thickness in wavelengths of <NUM>, and physical thickness in nanometers (nm). In <FIG>, the interferential coating includes a stack of alternated SiO<NUM> as low refractive index layers and Ta<NUM>O<NUM> layers as high refractive index layers. The optical thickness of each of the low refractive index layers and the high refractive index layers is <NUM>. The physical thickness of each of the low refractive index layers is <NUM>, and the physical thickness of each of the high refractive index layers is <NUM>. The interferential coating further includes an outer low refractive index layer (first line of the table) of SiO<NUM> with optical thickness of <NUM> and physical thickness of <NUM>. <FIG> also shows reflectance plots as function of the wavelength for the interference coatings with a stack varying from <NUM> layers (<NUM>), <NUM> layers, <NUM> layers, <NUM> layers, and <NUM> layers (<NUM>). The number of layers increases from bottom up. As can be seen, with the exemplary configuration of <FIG>, a stack of <NUM> or more layers provides a peak reflectance measured at a substantially normal to the optical article is at least <NUM>%.

In summary, <FIG> show a method to achieve high reflectance at <NUM> or at <NUM> with quarter-wavelength (λ/<NUM>) interferential coatings, which include multilayer optical materials, including at least one kind of low index material and one kind of high index material. The optical thickness of each layer is λ/<NUM>, where λ is the center wavelength of the reflection band. In some embodiments a <NUM>% variation may be acceptable. In the present disclosure, an outer low refractive index layer may be added to the interferential coating which may have an optical thickness of λ/<NUM> instead of λ/<NUM>, in order to minimize the reflection in visible region. In order to have a reflectance of <NUM>% or higher, is some embodiments, at least <NUM> layers of the stack are required, and as a consequence, the overall coating thickness is ≥ <NUM> (for the filters centered at <NUM>) or ≥ <NUM> (for the filters centered at <NUM>). The substrate may be a mineral lens substrate, for example, if enhanced adhesion is desired.

<FIG> shows an interferential coating <NUM> as described above, for example in connection with <FIG>, with the exception that the low refractive index layers m1 may have different thicknesses from each other and the high refractive index layers m2 may have different thicknesses from each other. Furthermore, the low refractive index layers are not necessarily of a same material, and the high refractive index layers are not necessarily of a same material. The thicknesses of the layers may be determined, for example using a transfer matrix method. An example of the interferential coating <NUM> of <FIG> is an anti-reflection (AR) stack also named herein as anti-reflection interferential coating. In the example of <FIG>, the interferential coating <NUM> is shown as including a stack <NUM> of <NUM> layers, however the disclosure is not limited thereto. With the optimized layer thicknesses, such a stack <NUM> is able to achieve the peak reflectance of at least <NUM>% with less layers than the previous examples explained in connection with <FIG>. Meanwhile such a stack is able to achieve a mean light reflection factor in the visible region Rv is lower than or equal to <NUM>% and optionally lower than or equal to <NUM>%, which is unachievable for quarter-wavelength (λ/<NUM>) interferential coatings. The total thickness of such a stack <NUM> is less than <NUM>. The thickness of the outermost (furthest from the substrate) high index and low index bilayer m1+m2 is lower than <NUM>, while the thickness of the innermost (adjacent to the substrate) high index and low index bilayer m1+m2 is higher than <NUM>.

For stacks consisting of two kind of materials the index ratio may be determined as the ratio of the refractive index of m2 over the refractive index of m1. Two kind or materials may mean all low refractive index material layers having a same material and all high refractive index material layers having a same material. For stacks consisting of three or more materials, the index ratio may be determined as of the highest index over the lowest index. For example, in an <NUM> layer AR stacks consisting of SiO<NUM>, ZrO2, and TiO<NUM> layers, the index ratio is determined as the ratio of the refractive index of TiO<NUM> over the refractive index of SiO<NUM>.

<FIG> shows a table with the material composition and layer thickness (in nm) of an interference coating in accordance with various embodiments. The interference coating comprises low refractive index layers of SiO<NUM> and high refractive index layers of TiO<NUM> alternately stacked on the substrate. The structure of the stack is optimized to exhibit a maximum reflection at <NUM>, and an anti-reflective behavior in visible light region. The total thickness of this example stack is <NUM>. The thickness of the outermost (furthest from the substrate) high index and low index bilayer is <NUM>, while the thickness of the innermost (adjacent to the substrate) high index and low index bilayer is <NUM>. The reflectance spectrum of the interference coating is shown in <FIG>, it can be seen that a peak reflectance measured at a substantially normal to the optical article is greater than <NUM> %. The table in <FIG> shows extracted parameters from the reflectance spectrum, in this case, the reflectance at <NUM> is <NUM> % and at <NUM> is <NUM> %. The mean light reflection factor in the visible region Rv equals to <NUM>%.

<FIG> shows a table with the material composition and layer thickness (in nm) of an interference coating in accordance with various embodiments. The interference coating comprises low refractive index layers of SiO<NUM> and high refractive index layers of Nb<NUM>O<NUM> alternately stacked on the substrate. The structure of the stack is optimized to exhibit a maximum reflection at <NUM>, and an anti-reflective behavior in visible light region. The total thickness of this example stack is <NUM>. The thickness of the outermost (furthest from the substrate) high index and low index bilayer is <NUM>, while the thickness of the innermost (adjacent to the substrate) high index and low index bilayer is <NUM>. The reflectance spectrum of the interference coating is shown in <FIG>, it can be seen that a peak reflectance measured at a substantially normal to the optical article is greater than <NUM> %. The table in <FIG> shows extracted parameters from the reflectance spectrum, in this case, the reflectance at <NUM> is <NUM> % and at <NUM> is <NUM> %. The mean light reflection factor in the visible region Rv equals to <NUM>%.

<FIG> shows a table with the material composition and layer thicknesses (in nm) for <NUM> exemplary interference coatings ExA, ExB, ExC. The interference coatings comprise low refractive index layers of SiO<NUM> and high refractive index layers of ZrO<NUM> and TiO<NUM>, stacked on a respective substrate. The total thickness of these example stacks is <NUM>, <NUM>, and <NUM>, respectively. The outermost (furthest from the substrate) and innermost (adjacent to the substrate) high-index layers in these example stacks consist of two high index materials (ZrO<NUM> and TiO<NUM>). The thickness of the outermost doublet high index and low index bilayer is <NUM>, <NUM>, <NUM> respectively, while the thickness of the innermost doublet high index and low index bilayer is <NUM>, <NUM> and <NUM>, respectively. From the reflectance spectra shown in <FIG> it can be seen that the reflectance peak shifts to longer wavelengths from ExA to ExC, wherein ExA has a reflectance of <NUM> % at <NUM> and <NUM> % at <NUM>, ExB has a reflectance of <NUM> % at <NUM> and <NUM> % at <NUM>, and ExC has a reflectance of <NUM> % at <NUM> and <NUM> % at <NUM>. With the reflectance peak shifts to longer wavelengths from ExA to ExC, the mean light reflection factor in the visible region Rv is significantly reduced from <NUM>% (ExA) down to <NUM>% (ExB) and further to <NUM>% (ExC). It can be seen that a peak reflectance measured at a substantially normal to the optical article is greater than <NUM> % for all <NUM> examples.

<FIG> shows a table with the material composition and layer thicknesses (in nm) for <NUM> exemplary interference coatings ExD, ExE, ExF. The interference coatings comprise low refractive index layers of SiO<NUM> and high refractive index layers of ZrO<NUM> and TiO<NUM>, stacked on a respective substrate. The total thickness of these example stacks is <NUM>, <NUM>, and <NUM>, respectively. The outermost (furthest from the substrate) and innermost (adjacent to the substrate) high-index layers in these example stacks consist of two high index materials (ZrO<NUM> and TiO<NUM>). The thickness of the outermost doublet high index and low index bilayer is <NUM>, <NUM>, <NUM> respectively, while the thickness of the innermost doublet high index and low index bilayer is <NUM>, <NUM> and <NUM>, respectively. From the reflectance spectra shown in <FIG> it can be seen that all <NUM> reflectance spectra are similar, wherein ExD has a reflectance of <NUM> % at <NUM> and <NUM> % at <NUM>, ExE has a reflectance of <NUM> % at <NUM> and <NUM> % at <NUM>, and ExF has a reflectance of <NUM> % at <NUM> and <NUM> % at <NUM>. With the reflectance peak shifts to longer wavelengths from ExD to ExF, the mean light reflection factor in the visible region Rv is significantly reduced from <NUM>% (ExD) down to <NUM>% (ExE) and further to <NUM>% (ExF). It can be seen that a peak reflectance measured at a substantially normal to the optical article is greater than <NUM> % at <NUM> for all <NUM> examples.

In summary, <FIG> show some example AR stacks with maximum reflectance around <NUM>. Similarly, <FIG> show some example AR stacks with maximum reflectance at <NUM>. The layer structure and major optical properties, including reflectance at <NUM> and <NUM>, of these AR stacks are also shown in these figures. Besides the high reflectance at <NUM> and/or <NUM>, all these stacks have a low Rv (equal or smaller than <NUM>%). For the specific <NUM>-layer ZTiQTiQTiZQ stacks (e.g. examples of ExC in <FIG> and ExF in <FIG>), an extreme low Rv (-<NUM>%) can be achieved. For some of these stacks, the reflectance at <NUM> or <NUM> is higher than <NUM>%. Even if only one surface of the lenses is coated with such coatings, reflectance at the targeted wavelength (<NUM> or <NUM>) is higher than <NUM>%. If both surfaces are coated with such coatings more than <NUM>% reflectance can be achieved. The TaQTaQ stacks have a reflectance ><NUM>% at <NUM> or <NUM>, if both surfaces are coated with such coatings, a total reflectance higher than <NUM>% can be achieved.

According to some embodiments, the interferential coating may have a thickness of equal to or less than <NUM>, for example of equal to or less than <NUM>, and for example of equal to or less than <NUM>. Such thicknesses ensure mechanical reliability of the interferential coating. According to some embodiments, the thickness of the outermost (furthest from the substrate) high index and low index bilayer of the interferential coating may be lower than <NUM>, for example of equal to or less than <NUM>, and for example of equal to or less than <NUM>. According to some embodiments, the thickness of the innermost (adjacent to the substrate) high index and low index bilayer m1+m2 may be higher than <NUM>, for example of equal to or higher than <NUM>, and for example of equal to or higher than <NUM>.

User wearable optical articles according to various embodiments have an increased reflectance in the near infra-red spectrum, which is not visible to the human eye. The interferential coating may be used for example, to identify the presence of the user wearable optical article proximal to a sensor. For example, due to the interferential coating, the reflection of a NIR signal reflected by the user wearable optical article may be enhanced. In one exemplary application, the user wearable optical article may be used in connection with a digital screen (e.g. for reading), for example of a mobile phone, a distance sensor may indicate the distance between the screen and the user wearable optical article, and therefore the distance between the digital screen and user's eye(s). Such distance may be used to alert the user that his reading distance is not within an optimal or healthy range.

Today, most digital multi-function devices (e.g., smartphones, tablets) already have their built-in proximity sensors. Such proximity sensors emit infrared light (for example at <NUM> or <NUM>) and by measuring the reflected infrared light from an object, the distance between the proximity sensor and the object can be determined. The most common use of this function is to determine whether a phone is placed near the user's ear during a phone call. In this situation, the proximity sensor may activate a background application which will turn off the digital screen in order to avoid undesirable operations from accidental touch on the screen. Such a combination of built-in proximity sensors and background application in today's mainstream digital devices will turn off the screen at a distance range of two centimeters or less.

The interferential coating in accordance with various embodiments has a strong reflection level at the working wavelength of the proximity sensor. This strong reflection may trigger the proximity sensor at a longer distance than current defined distance of two centimeters (or less).

A set of tests was carried out with optical articles in accordance with the present disclosure, including the above examples, using commercially available smartphones. The operating wavelength was <NUM>. For a same smartphone the distance to the optical article under which the screen is turned off was <NUM>, which is a significant more than the distance of <NUM> for a comparative example without the interferential coating. For a second phone, the distance to the optical article under which the screen is turned off was <NUM>, which is a significant more than the distance of <NUM> for a comparative example without the interferential coating. For a third phone, the distance to the optical article under which the screen is turned off was <NUM>, which is a significant more than the distance of <NUM> for a comparative example without the interferential coating. Other comparative examples using a hand in front of the smartphone have further halved the distance.

This longer distance to activate the background application to cut off digital screen can be used to control reading distance: when the reading distance is far enough, the digital screen will remain on, while the reading distance becomes shorter and the reflected infrared light triggers the proximity sensor, the screen will be turned off automatically without any intervention. A user just need to move the digital device further away, and the screen will be turned on again automatically. In some embodiments, no specific additional hardware (using existing built-in proximity sensors) is required. In other embodiments, for example, traditional display devices without such built-in proximity sensors, e.g. traditional TV, an additional NIR distance sensor, for example an external distance sensor, could added. Further, according to various embodiments, only a simple background software application may be required to turn off screen.

<FIG> shows an eyewear <NUM>, illustrated as a spectacle, including an optical article <NUM>, in accordance with various embodiments. The eyewear may include an optical articles as described herein.

The disclosure also concerns a method for producing an optical article as described in accordance with various embodiments. The method may include providing the optical substrate. The method may further include providing the interferential coating disposed on at least one of the front main face and rear main face of the optical substrate. The interferential coating may be deposited, for example, via vacuum deposition or another suitable method for deposition of optical films, such as magnetron sputtering.

Claim 1:
A user wearable optical article (<NUM>) comprising:
an optical substrate (<NUM>) with a front main face and a rear main face for facing the user when wearing the optical article (<NUM>); and
an interferential coating (<NUM>) disposed on at least one of the front main face and rear main face and configured to selectively reflect light of at least one range of wavelengths of an incident light in the near infrared light spectrum, so that a peak reflectance at <NUM> or <NUM> measured at a substantially normal to the optical article is at least <NUM>%, and the interferential coating (<NUM>) has a mean reflectance of less than <NUM>% in a visible light range, the total thickness of the interferential coating being equal to or less than <NUM>, optionally equal to or less than <NUM>, and optionally equal to or less than <NUM>.