Patent Description:
Integrated circuit (IC) devices typically include circuit elements such as transistors, capacitors and resistors formed within or on a semiconductor substrate. Interconnect structures are used to electrically couple or connect the discrete circuit elements into functional circuits. Typical metal interconnects may include a line portion and a via portion.

Interconnect structures may be fabricated from copper, and may include a barrier layer such as titanium or tantalum or nitride materials such as tantalum nitride or titanium nitride, or a combination thereof (e.g., tantalum nitride/tantalum (TNT)). A problem with utilizing copper interconnect structures is that they are highly susceptible to electromigration which can lead to void formation and failure.

Tungsten metallization has been successfully used to fabricate front end contacts and, thus, has been suggested for back end metallization for interconnect fabrication. A desirable advantage with utilizing tungsten metallization is that it is highly resistant to detrimental electromigration effects. However, a disadvantage with utilizing tungsten metallization is that its electrical resistivity is higher than copper. More specifically, tungsten line resistances are <NUM> to <NUM> times higher than copper interconnects, and via resistances can be as much as <NUM>% higher. These high resistances severely degrade IC performance and are therefore undesirable. <CIT> describes a semiconductor device, including a plurality of insulation layers; and a plurality of wiring line layers, each of the plurality of wiring line layers including a wiring line having a line width and a line height, at least one of which is <NUM> or less, and containing Ni or Co as a main component thereof. The invention is set forth in independent claim <NUM>. Embodiments of the invention are described in the dependent claims.

Reference will now be made to the drawings wherein like structures may be provided with like suffix reference designations. In order to show the structures of various embodiments more clearly, the drawings included herein are diagrammatic representations of semiconductor/circuit structures. Thus, the actual appearance of the fabricated integrated circuit structures, for example in a photomicrograph, may appear different while still incorporating the claimed structures of the illustrated embodiments. Moreover, the drawings may only show the structures useful to understand the illustrated embodiments. Additional structures known in the art may not have been included to maintain the clarity of the drawings. For example, not every layer of a semiconductor device is necessarily shown. "An embodiment", "various embodiments" and the like indicate embodiment(s) so described may include particular features, structures, or characteristics, but not every embodiment necessarily includes the particular features, structures, or characteristics. "First", "second", "third" and the like describe a common object and indicate different instances of like objects are being referred to. Such adjectives do not imply objects so described must be in a given sequence, either temporally, spatially, in ranking, or in any other manner. "Connected" may indicate elements are in direct physical or electrical contact with each other and "coupled" may indicate elements co-operate or interact with each other, but they may or may not be in direct physical or electrical contact.

The invention is a cobalt interconnect which includes a manganese (Mn) based adhesion layer and a cobalt fill material. The adhesion layer (sometimes also referred to herein as a barrier layer or wetting layer) may include various Mn based compositions such as, for example, Mn, manganese nitride (MnN), or manganese silicon nitride (MnSixNy). The Mn based adhesion layer may comprise a film deposited in patterned backend interconnect structures. These interconnect structures are metalized with cobalt. The Mn based layer adheres well to the interlayer dielectric (ILD) that helps form the interconnect in some embodiments. The Mn based layer also provides wetting to the cobalt metal. Thus, the Mn based adhesion layer helps achieve robust gap filling of interconnect structures at small scales such as <NUM>, <NUM>, <NUM> and beyond.

An embodiment includes a cobalt interconnect that includes a cobalt plug layer and a cobalt fill material. The plug layer is formed from a different composition and/or by a different process than that used to for the cobalt fill material. Such cobalt interconnects are advantageous since they have a low resistance (e.g., lower than tungsten) and are highly resistive to electromigration (e.g., more resistive to electromigration than copper), enabling fabrication of high performance interconnect structures. As dimensions scale in conventional interconnect processing, the high resistance of traditional barrier layers (e.g., TNT barrier layers) can impact the performance of conventional copper interconnects to greater extents. However, lower resistance Mn layers may mitigate these resistance issues.

In a first aspect, a conformal Mn based adhesion layer is formed in an opening in a dielectric layer. A cobalt-based fill material is then deposited or grown on the Mn based adhesion layer to form a cobalt interconnect.

<FIG> illustrate a method of forming a cobalt interconnect with a Mn based adhesion layer and a cobalt-containing fill layer according to embodiments of the present invention. <FIG> illustrates a substrate <NUM> with top surface <NUM> that may be used as a substrate on which a cobalt interconnect can be formed. Substrate <NUM> can include any portion of a partially fabricated IC on which a cobalt interconnect is ultimately fabricated. For example, substrate <NUM> will typically include, or have formed thereon, active and passive devices. As depicted in <FIG>, a conductive region <NUM> is included in substrate <NUM>, on to which a cobalt interconnect is ultimately formed. In one such embodiment, the substrate <NUM> has been processed through front end of line (FEOL), and the conductive region <NUM> is a metal silicide region.

Although embodiments may be ideally suited for fabricating semiconductor ICs such as, but not limited to, microprocessors, memories, charge-coupled devices (CCDs), system on chip (SoC) ICs, or baseband processors, other applications can also include microelectronic machines, MEMS, lasers, optical devices, packaging layers, and the like. Embodiments may also be used to fabricate individual semiconductor devices.

Referring again to <FIG>, a dielectric layer <NUM> is formed above substrate <NUM>. The dielectric layer <NUM> may be composed of any suitable dielectric or insulating material such as, but not limited to, silicon dioxide, SiOF, carbon-doped oxide, a glass or polymer material, and the like. An opening is formed in the dielectric layer. The opening exposes the conductive region <NUM> to which contact (indirect or direct) by a cobalt interconnect is ultimately made. In one embodiment, as depicted in <FIG>, the opening includes a lower opening <NUM> (e.g., a via hole or slot) with sidewalls <NUM> and an upper opening <NUM> (e.g., a metal line trench) with sidewalls <NUM>, as is common in a dual damascene process. Although two openings are depicted (or a single opening with varying widths), it is to be appreciated that a single opening may instead be formed in the dielectric layer <NUM> (e.g., as is used in a single damascene approach where only a line or a via, but not both, is fabricated in a single operation). The opening or openings may be fabricated in dielectric layer <NUM> by well known lithography and etch processing techniques typically used in damascene and dual damascene type fabrication. Although only a single dielectric layer <NUM> is depicted, multiple layers of the same or differing dielectric materials may instead be used (e.g., a first dielectric layer having opening <NUM> therein, and a second dielectric layer having opening <NUM> therein). Additionally, as depicted in <FIG>, the dielectric layer <NUM> is formed on an etch stop layer <NUM> disposed on substrate <NUM>. The etch stop layer <NUM> may be composed of a material such as silicon nitride or silicon oxynitride.

Referring to <FIG>, a Mn based adhesion layer <NUM> (e.g., an adhesion layer including Mn, MnN, MnSixNy and the like) is deposited. In other systems a seed layer may be formed on a TNT based adhesion layer. Seed layers, such as the seed layer disclosed in U. Patent App. Publication <CIT> may facilitate formation of fill material. However, no such seed layer is needed in the embodiment of <FIG>. Nor is deposition of an alloy between an adhesion layer and a seed layer needed in the embodiment of <FIG>. Thus, as will be seen below, a Mn based adhesion layer may directly contact ILD <NUM> and directly contact cobalt fill (described below) without the need for a TNT based adhesion layer, any seed layer, or any alloy layer between a TNT based adhesion layer and a seed layer.

In <FIG> the Mn based adhesion layer <NUM> may be formed on a top surface <NUM> of the dielectric layer <NUM> as well as on the exposed top surface <NUM> of the substrate <NUM> (e.g., on conductive region <NUM>). While <NUM> is referred to as "substrate" in another embodiment <NUM> could be a metal interconnect line, and the like. The Mn based adhesion layer <NUM> is also formed on the sidewalls <NUM> of the upper opening <NUM>, and the sidewalls <NUM> of the lower opening <NUM>.

Mn based adhesion layer <NUM> may be a conformal layer composed of a material including Mn, MnN, MnSixNy, MnSixOy (e.g., Mn<NUM>[SiO<NUM>], MnSiO<NUM>), other Mn based silicates, and the like. In an embodiment with the adhesion layer including Mn, the Mn content may include <NUM>-<NUM>% Mn, where contamination (i.e., the remaining <NUM>%) may include C, H, O and combinations thereof. In an embodiment with the adhesion layer including MnNx, the Mn may compose <NUM>-<NUM>% Mn and the N may compose <NUM>-<NUM>%. In an embodiment with the adhesion layer including MnNx, the adhesion layer may include Mn<NUM>N or Mn<NUM>N<NUM>. In an embodiment with the adhesion layer including MnNxSiy the Mn and N may include up to <NUM>% with the Si constituting the remainder of the material. In an embodiment Mn, N, and Si may be included with one another in various adhesion multilayer combinations such as bilayers or trilayers (e.g., an adhesion layer includes one sublayer including MnN and another sublayer including Mn), (e.g., one adhesion layer including a sublayer having Mn and N and another sublayer including primarily Mn), (e.g., one adhesion layer including a sublayer including MnNxSiy and another sublayer including primarily Mn), and the like. As used herein, % of composition refers to atomic %.

In one embodiment, the Mn based adhesion layer <NUM> is formed to a thickness less than <NUM>, and typically <NUM> to <NUM>. In an embodiment thickness ranges for layer <NUM> (whether layer <NUM> includes a single layer or multiple sublayers such as one sublayer including MnN and another immediately adjacent sublayer including Mn) may range from <NUM>. In an embodiment layer <NUM> is between 10A-20A including, for example, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, or 20A.

In an embodiment, conductive region <NUM> includes at least some germanium (e.g., an exposed doped silicon germanium or doped germanium region, or a metal germanide region). In an embodiment, conductive region <NUM> includes at least some silicon (e.g., an exposed doped silicon region, or a metal silicide region).

The layer <NUM> may be deposited or grown by chemical vapor deposition (CVD), atomic layer deposition (ALD), physical vapor deposition (PVD), electroplating, electroless plating or other suitable process that deposits conformal thin films. In an embodiment, the layer <NUM> is deposited to form a high quality conformal layer that sufficiently and evenly covers all exposed surfaces within the openings and top surfaces. The adhesion layer may be formed, in one embodiment, by depositing the Mn based material at a slow deposition rate to evenly and consistently deposit the conformal adhesion layer. By forming the layer <NUM> in a conformal manner, compatibility of a subsequently formed fill material (such as cobalt) with the underlying structure may be improved. Specifically, the layer <NUM> can assist a deposition process by providing appropriate surface energetics for deposition thereon.

Deposition recipes of thin films using processes such as CVD, ALD, and PVD may vary depending on the desired process time, thickness, and quality of conformity. For example, utilizing CVD to deposit the adhesion layer <NUM> may create a conformal thin film layer more quickly than it would take an ALD process to deposit the same layer; however, the quality of the thin film deposited by the CVD process may be lower than the quality of the thin film deposited by the ALD process. In another embodiment, the layer <NUM> is deposited by a PVD process. The PVD process may be performed with an increased distance between the receiving substrate and the corresponding sputter target to form a highly conformal thin film.

Referring to <FIG>, a fill material <NUM> may be formed on the exposed surfaces of the adhesion layer <NUM>, such that the fill material <NUM> completely fills the openings <NUM> and <NUM> and is formed on the top surface of the adhesion layer <NUM> and on the top surface <NUM> of dielectric <NUM>. A seam <NUM> may be formed within the openings <NUM>, <NUM> during deposition of the fill material <NUM>. In an embodiment, the fill material <NUM> is composed of a dilute alloy composed of approximately <NUM>-<NUM>% of a non-cobalt element (e.g., Al, Ni, Cu, Ag, Au, Mn, Ti, V, Cr, Fe, Ta, W, Ru, P, B, C, N, Si, Ge, Mg, Zn, Rh, Pt, Cd, Hf, In, Sn, C, O, Be, Ca, Zr, Nb, Mo, Ir, Re, or Pd) with the remainder approximately <NUM>+% cobalt. Such a dilute alloy can involve, either during deposition or processing subsequent to deposition, migration of the non-cobalt species to surfaces of fill <NUM>. The migration can provide a diffusion barrier for the cobalt (in addition to adhesion/barrier layer <NUM>) and/or be used to enhance adhesion of the cobalt to layer <NUM>. Grain boundaries within the cobalt may also be filled by the non-cobalt species. In one embodiment, the fill material <NUM> consists essentially only of cobalt. In another embodiment, the fill material <NUM> is at least <NUM>% cobalt. The fill material <NUM> is composed of at least <NUM>% cobalt.

In an embodiment of the invention, the cobalt fill material <NUM> may be formed by a process such as, but not limited to, CVD, ALD, PVD, electroplating, or electroless plating. In one embodiment, the process method used to form the fill material <NUM> may be different than the process used to form the layer <NUM>. Furthermore, the layer <NUM> may be formed conformally, while the fill material <NUM> is formed in a non-conformal or bottom up approach. For example, the layer <NUM> may be formed by an ALD deposition process that forms a conformal layer on exposed surfaces of the receiving substrate, while the fill material <NUM> may be formed by PVD process that directionally sputters the fill material onto the surfaces of the layer <NUM>, with greater deposition rates on flat horizontal surfaces as opposed to on more vertically oriented sidewall surfaces. In another example, the layer <NUM> may be formed by an ALD deposition process that forms a conformal layer on exposed surfaces of the receiving substrate, while the fill material <NUM> may be formed by an electroplating process that grows the fill material from the surfaces of the layer <NUM>. In yet another example, the layer <NUM> may be formed by a CVD deposition process and the fill material may be formed by a PVD process.

In another embodiment, the layer <NUM> and the fill material <NUM> may be deposited by the same process (e.g. ALD, CVD, or PVD) but with different sets of deposition parameters, such as pressure, deposition rate, temperature, and the like. For example, the layer <NUM> and the fill material <NUM> may be deposited by a CVD process; however, the set of parameters used in the CVD processing for the adhesion layer <NUM>, such as deposition pressure and temperature, may be different than the set of parameters used in the CVD processing for the fill material <NUM>. In another example, the layer <NUM> and the fill material <NUM> are formed by a PVD process, but the layer <NUM> may be formed by a PVD process with a larger distance between the target and the receiving substrate than the PVD process used to form the fill material <NUM>. In another embodiment, the metal fill material <NUM> is formed by a colummated PVD process, while the layer <NUM> is formed by a non-colummated PVD process. Or alternatively, the layer <NUM> is formed by an ALD process with a lower deposition rate than the deposition rate of the ALD process used to form the fill material <NUM> such that the layer <NUM> is formed more conformally than the fill material <NUM>.

Referring to <FIG>, an anneal process may optionally be performed to reflow the deposited interconnect layer. The seam <NUM> from <FIG> may be removed subsequent to the anneal process, forming a solid structure within openings <NUM> and <NUM> within dielectric layer <NUM>. The anneal process may help grow larger grain structures within the fill material <NUM>, decreasing resistivity and expelling impurities from poor grain structures. In one embodiment, the anneal process uses gasses such as nitrogen, hydrogen, and argon. Furthermore, the anneal process may be performed at a temperature less than the thermal budget of the backend structures. For example, in one embodiment, the anneal process is performed at a temperature of room temperature to <NUM>, <NUM>, <NUM> or more. In another embodiment, the anneal process is performed at a temperature that is higher than the melting point of fill material <NUM> but lower than the thermal budget of the backend structures. In various embodiments the anneal process can vary widely (e.g., room temperature to <NUM>, <NUM>, <NUM> or more for interconnects ranging up to <NUM> for Front end applications). In such embodiments the anneal temperature is not higher than the melting point of the material being annealed as reflow of materials to be annealed can happen at much lower temperatures than the melting point for the material to be annealed. In such embodiments anneal temperatures for the material to be annealed may be less than the thermal budget of backend structures.

In yet another embodiment, a cycling technique may optionally be utilized to deposit the interconnect layer <NUM> (also referred to as fill layer <NUM>) within the openings <NUM> and <NUM> without the seam <NUM>. One cycle may involve one deposition of the fill material <NUM> and one anneal process. The anneal operation of one cycle may be set at a temperature and time duration to briefly reflow the fill material to improve step coverage. The deposition operation of one cycle may be a short deposition to deposit less fill material, such that several operations are required to completely fill the via and line openings <NUM> and <NUM>. In one embodiment, less than <NUM> cycles are needed to deposit the fill material <NUM> without a seam <NUM>.

Referring to <FIG>, a chemical mechanical planarization (CMP) process may be performed to remove the fill material <NUM> and the adhesion layer <NUM> disposed above the top surface <NUM> of the dielectric layer <NUM>. In one embodiment, the CMP process may be a timed CMP process that is timed to stop at the top surface <NUM> of the line dielectric layer. In another embodiment, the CMP process may utilize the top surface <NUM> of the line dielectric layer as a stopping layer. Because the thickness of the fill material deposited above the top surface of the line dielectric layer may vary, utilizing the top surface <NUM> as a stopping layer may be a more reliable method. In an alternative embodiment, an etch process is used to remove the fill material <NUM> and the layer <NUM> disposed above the top surface <NUM> of the dielectric layer <NUM>.

<FIG> illustrates a cross-section <NUM> of a portion of an IC structure with cobalt metal interconnects not forming part of the present invention. A stack of dielectric layers <NUM> includes metal interconnects having adhesion layers <NUM> and metal (e.g., cobalt) fill layers <NUM>. The portion of the IC structure shown in <FIG> can be a portion of a back end of line (BEOL) metallization structure as found, for example, in a microprocessor die or memory die.

<FIG> is a flow chart <NUM> illustrating a method of forming a cobalt metal interconnect according to an embodiment of the present invention. At <NUM>, an opening is formed in a dielectric layer to expose a conductive region in a substrate (or on an additional metal interconnect). At <NUM>, a Mn based adhesion/barrier layer is formed over the substrate, in contact with the conductive region, as well as over the dielectric layer and on sidewalls of the opening. At <NUM>, a fill material is formed on the adhesion layer and fills the opening. The fill material is composed of a cobalt-based material. At <NUM>, in an optional embodiment, heat is applied to reflow the fill material. At <NUM>, the fill material and adhesion layer material disposed above an upper surface of the dielectric layer are removed.

In an embodiment a cobalt-based plug is formed in a lower portion (e.g., a via hole or slot) of an opening in a dielectric layer. A cobalt-based conductive line is then formed on the cobalt-based plug, in an upper portion (e.g., a metal line trench) of the opening, to form a cobalt interconnect.

For example, <FIG> illustrate a method of forming a cobalt metal interconnect according to an embodiment of the invention. The method begins with the same structure as illustrated and described in association with <FIG>, which includes adhesion layer <NUM> and will not be described again for the sake of brevity.

Referring to <FIG>, a plug <NUM> is formed on adhesion layer <NUM>. In an embodiment, as depicted, the plug <NUM> is formed only within the lower opening <NUM> of the dielectric layer <NUM> such that the lower opening <NUM> is completely filled with plug material <NUM>. In another embodiment, however, the top surface of the plug <NUM> may not be planar with the top surface of the lower opening <NUM>. For example, the top surface of the plug <NUM> may be higher or lower than the top surface of the lower opening. The top surface of the plug <NUM> may be at, above, or below the horizontal top surface of layer <NUM> where layer <NUM> is horizontally disposed at the top of <NUM> and bottom of <NUM>. As depicted in <FIG> the plug <NUM> has a top surface just below the horizontal top surface of layer <NUM> where layer <NUM> is horizontally disposed at the top of <NUM> and bottom of <NUM>. In another embodiment, the top surface of the plug <NUM> may form a mushroom-like dome as a result of the growth profile during formation of plug <NUM>.

In an embodiment, plug <NUM> is formed in a bottom-up approach. That is, the plug <NUM> is not formed by conformal deposition. For example, in one embodiment, the formation of plug <NUM> is performed by selectively depositing on, and then growing from, the surface of layer <NUM> directly above the conductive region <NUM>. In a specific embodiment, the plug <NUM> is formed by electrolessly plating the plug material onto an exposed and compatible surface of layer <NUM>. As an example, a cobalt-based plug <NUM> is formed by electroless deposition involving bottom-up growth from the layer <NUM> above the metalized or metal-containing surface of conductive region <NUM>. In other embodiments, other suitable bottom-up fill and growth deposition approaches may be used such as, but not limited to, electroplating. A bottom-up fill approach is one in which a deposition rate is faster on planar or flat surfaces than on vertical sidewall surfaces.

The plug <NUM> is a cobalt-based plug composed of at least <NUM>% cobalt. In a particular embodiment, the plug <NUM> is composed of at least <NUM>% cobalt. In any such cases, the non-cobalt remainder of the plug <NUM> composition, if any, can include one or more of Al, Ni, Cu, Ag, Au, Mn, Ti, V, Cr, Fe, Ta, W, Ru, P, B, C, N, Si, Ge, Mg, Zn, Rh, Pt, Cd, Hf, In, Sn, C, O, Be, Ca, Zr, Nb, Mo, Ir, Re, or Pd. In another embodiment, the plug <NUM> is composed of a cobalt-based compound or alloy material. For example, in one embodiment, the plug <NUM> is composed of a dilute alloy composed of approximately <NUM>-<NUM>% of a non-cobalt element, such as those listed above, with the remainder approximately <NUM>+% cobalt, is used. Such a dilute alloy can involve, either during deposition or processing subsequent to deposition, migration of the non-cobalt species to surfaces or interfaces of the cobalt plug. The migration can provide a diffusion barrier for the cobalt and/or be used to enhance adhesion of the cobalt to layer <NUM>. Grain boundaries within the cobalt may also be filled by the non-cobalt species. In other embodiments, however, the plug <NUM> may include less than <NUM>% cobalt, but still be referred to as a cobalt-based material. Exemplary embodiments of cobalt-based compound plug <NUM> materials include cobalt silicide or cobalt germanide plug materials. In a specific such embodiment, conductive region <NUM> includes at least some germanium (e.g., an exposed doped silicon germanium or doped germanium region, or a metal germanide region), and the plug <NUM> material is a cobalt germanide layer. In another specific such embodiment, conductive region <NUM> includes at least some silicon (e.g., an exposed doped silicon region, or a metal silicide region), and the plug <NUM> material is a cobalt silicide layer. Exemplary embodiments of cobalt-based alloy plug <NUM> materials include cobalt alloyed with one or more of the following: Al, Ni, Cu, Ag, Au, Mn, Ti, V, Cr, Fe, Ta, W, Ru, P, B, C, N, Si, Ge, Mg, Zn, Rh, Pt, Cd, Hf, In, Sn, C, O, Be, Ca, Zr, Nb, Mo, Ir, Re, or Pd. In the above described embodiments, the cobalt plug <NUM> may have a small grain structure. In an embodiment the above mentioned dopant (i.e., the <NUM>-<NUM>% of a non-cobalt element) could be used without layer <NUM> so that cobalt would adhere directly to sidewall <NUM> as well as portion <NUM>. In an embodiment the dopant essentially creates a layer <NUM> (an adhesion layer) by diffusion to interfaces such as interfaces at <NUM> and <NUM>. In one embodiment the dopant forms a layer with portion <NUM>. In another embodiment the dopant makes no layer formation with <NUM> so that the barrier is bottomless and plug <NUM> directly contacts area <NUM>.

Referring to <FIG>, pretreatment <NUM> may optionally be performed on the exposed top surface of the plug <NUM> and layer <NUM>. Pretreatment may be performed by a plasma process or ion bombardment to enhance adhesion of a later formed compound to the treated surface. In one embodiment, pretreatment may be performed in a plasma chamber at a temperature ranging from room temperature up to approximately <NUM>, <NUM>, <NUM> or more for approximately <NUM> to <NUM> seconds utilizing, for example, H<NUM>/He plasma, Ar plasma, NH<NUM> plasma, N<NUM> plasma, and/or combinations thereof. In another embodiment, the pretreatment may include Ar ion bombardment. It is to be understood that such pretreatment may be performed at other stages of the process flow (e.g., prior to forming plug materials). In an embodiment the pretreatment is performed before layer <NUM> is formed. However, in other embodiments a treatment of layer <NUM> can be quite beneficial to density without affecting dielectrics such as layer <NUM>.

Referring to <FIG>, a fill material <NUM> is formed on the plug <NUM> and layer <NUM> within upper opening <NUM>. A seam <NUM> may be formed within the upper opening <NUM> subsequent to deposition of the fill material <NUM>. In one embodiment, fill material <NUM> is composed of a material comprising cobalt. For example, fill material may be composed of, and deposited by, materials and processes described above for fill material <NUM>. Furthermore, the fill material <NUM> may differ from the plug <NUM> material by composition and/or deposition technique.

An anneal process may optionally be performed to reflow the deposited fill material <NUM>. The seam <NUM> from <FIG> may be removed subsequent to the anneal process, forming a solid structure within openings <NUM> and <NUM> within dielectric layer <NUM>. The anneal process may enable growth of larger grain structures within the fill material <NUM>, decreasing resistivity and expelling impurities from otherwise poor grain structures. In one embodiment, the anneal process involves use of a forming gas such as, but not limited to, nitrogen, hydrogen, or argon. Furthermore, the anneal process may be performed at a temperature less than the thermal budget of the backend structures. For example, in one embodiment, the anneal process is performed at a temperature of room temperature to <NUM>, <NUM>, <NUM> or more. In another embodiment, the anneal process is performed at a temperature that is higher than the melting point of fill material <NUM> but lower than the thermal budget of the backend structures. In embodiments the anneal temperature is not higher than the melting point of the material being annealed as reflow of materials to be annealed can happen at much lower temperatures than the melting point for the material to be annealed. In such embodiments anneal temperatures for the material to be annealed may be less than the thermal budget of backend structures.

In yet another embodiment, a cycling technique is optionally utilized to deposit the fill material <NUM> within the opening <NUM> without the seam <NUM>. One cycle may involve a single deposition of the fill material <NUM> and a single anneal process. The anneal operation of one cycle may be set at a temperature and time duration to briefly reflow the fill material <NUM> to improve step coverage. The deposition operation of one cycle may be a short deposition to deposit less fill material <NUM>, such that several operations are required to completely fill the upper opening <NUM>. In one embodiment, less than <NUM> cycles are needed to deposit the fill material <NUM> without a seam <NUM>.

Referring to <FIG>, a CMP process may be performed to remove the fill material <NUM> above the top surface of layer <NUM> to provide the cobalt-based structure <NUM>. In one embodiment, the CMP process may be a timed CMP process that is timed to stop at the top surface <NUM> of the line dielectric layer. In another embodiment, the CMP process may utilize the top surface <NUM> of the dielectric layer <NUM> as a stopping layer. Because the thickness of the fill material deposited above the top surface <NUM> of the dielectric layer <NUM> may vary, utilizing the top surface <NUM> as a stopping layer may be a more reliable method. In an alternative embodiment, an etch process is used to remove the fill material <NUM> above the top surface <NUM> of the dielectric layer <NUM>.

In an embodiment a cobalt-based plug is formed in a lower portion (e.g., a via hole or slot) of an opening in a dielectric layer. An adhesive layer is then formed in an upper portion (e.g., a metal line trench) of the opening, over the cobalt-based plug. A cobalt-based conductive line is then formed on the portion of the adhesive layer that is directly over the plug to fill the upper portion of the opening to form a cobalt interconnect.

For example, <FIG> illustrate a method of forming a cobalt interconnect with a Mn based adhesion layer and a cobalt containing fill layer according to an embodiment of the invention. The method begins with the same structure as illustrated and described in association with <FIG>. Next, referring to <FIG>, the cobalt-based plug <NUM> is formed in the lower opening <NUM> of the dielectric layer <NUM>, on the conductive region <NUM> of substrate <NUM>. However, in another embodiment the adhesion layer be first formed along the side walls of dielectric <NUM> and/or on top of portion <NUM> before plug <NUM> is formed.

Referring to <FIG>, a Mn based adhesion layer <NUM> (e.g., Mn, MnN, MnSixNy MnSixOy (e.g., Mn<NUM>[SiO<NUM>], MnSiO<NUM>), other Mn based silicates, and the like) is deposited conformally with the structure of <FIG>. For example, in one embodiment, the Mn based adhesion layer <NUM> is formed in the upper opening <NUM> of the dielectric layer <NUM> and on the exposed plug <NUM>. The composition and method of forming the adhesion layer <NUM> may be as described for adhesion layer <NUM> of <FIG>.

Referring to <FIG>, a fill material <NUM> is formed on the adhesion layer <NUM>, within upper opening <NUM>, and on the top surface <NUM> of the dielectric layer <NUM>. A seam <NUM> may be formed within the opening <NUM> subsequent to deposition of the fill material <NUM>. The composition and method of forming the fill material layer <NUM> may be as described for fill material <NUM> of <FIG>. Furthermore, although in an embodiment the plug <NUM> and the fill material <NUM> are all cobalt-based, they may all differ from one another by composition and/or deposition technique.

An anneal process may optionally be performed to reflow the deposited fill material <NUM>; The seam <NUM> from <FIG> may be removed subsequent to the anneal process, forming a solid structure within opening <NUM> of dielectric layer <NUM>. The anneal process may enable growth of larger grain structures within the fill material <NUM>, decreasing resistivity and expelling impurities from poor grain structures. In one embodiment, the anneal process involves a use of gas such as, but not limited to, nitrogen, hydrogen, or argon. Furthermore, the anneal process may be performed at a temperature less than the thermal budget of the backend structures. For example, in one embodiment, the anneal process is performed at a temperature of room temperature to <NUM>, <NUM>, <NUM> or more. In another embodiment, the anneal process is performed at a temperature that is higher than the melting point of fill material <NUM> but lower than the thermal budget of the backend structures. In embodiments the anneal temperature is not higher than the melting point of the material being annealed as reflow of materials to be annealed can happen at much lower temperatures than the melting point for the material to be annealed. In such embodiments anneal temperatures for the material to be annealed may be less than the thermal budget of backend structures.

In yet another embodiment, a cycling technique may be utilized to deposit the fill material <NUM> within the opening <NUM> without the seam <NUM>. One cycle may involve one deposition of the fill material <NUM> and one anneal process. The anneal operation of one cycle may be set at a temperature and time duration to briefly reflow the fill material to improve step coverage. The deposition operation of one cycle may be a short deposition to deposit less fill material, such that several operations are required to completely fill the opening <NUM>. In one embodiment, less than <NUM> cycles are needed to deposit the fill material <NUM> without a seam <NUM>.

Referring to <FIG>, a CMP process may be performed to remove the fill material <NUM> and the adhesion layer <NUM> disposed above the top surface <NUM> of the dielectric layer <NUM> to provide the cobalt-based structure <NUM>. In one embodiment, the CMP process may be a timed CMP process that is timed to stop at the top surface <NUM> of the dielectric layer <NUM>. In another embodiment, the CMP process may utilize the top surface <NUM> of the dielectric layer <NUM> as a stopping layer. Because the thickness of the fill material deposited above the top surface <NUM> of the dielectric layer <NUM> may vary, utilizing the top surface <NUM> as a stopping layer may be a more reliable method. In an alternative embodiment, an etch process is used to remove the fill material <NUM> and the layer <NUM> disposed above the top surface <NUM> of the dielectric layer <NUM>.

<FIG> is a flow chart <NUM> illustrating a method of forming a cobalt metal interconnect not forming part of the present invention. At <NUM>, an opening is formed in a dielectric layer to expose a conductive region in a substrate. At <NUM>, a cobalt plug is formed in a lower portion of the opening, in contact with the conductive region. At <NUM> a Mn based adhesion layer (e.g., Mn, MnN, MnSixNy and the like) is formed in the upper portion of the opening. At <NUM>, a fill material is formed on the plug and adhesion layer to fill the opening. The fill material is composed of a cobalt-based material. At <NUM>, in an optional embodiment, heat is applied to reflow the fill material. At <NUM>, the fill material disposed above an upper surface of the dielectric layer is removed. In one such embodiment, the fill material and the plug both include cobalt, but have different material compositions. In another such embodiment, the fill material and the plug both include cobalt, but are formed by different deposition or growth techniques. In yet another such embodiment, the fill material and the plug both include cobalt, but have different material compositions and are formed by different deposition or growth techniques.

In an embodiment a metal gate electrode of a semiconductor device is composed, as least partially, of cobalt. That is, embodiments of the present invention need not be limited to forming cobalt-based interconnects.

In an example, <FIG> depicts a metal oxide semiconductor field effect transistor (MOS-FET) <NUM> fabricated on a substrate <NUM>, not forming part of the present invention. A gate dielectric layer <NUM> is disposed above a channel region <NUM>, and a gate electrode <NUM> is disposed above gate dielectric layer <NUM>. Gate dielectric layer <NUM> and gate electrode <NUM> may be isolated by gate isolation spacers <NUM>. Tip extensions <NUM> may be formed by implanting dopant atoms into substrate <NUM>. Source and drain regions (e.g., strain-inducing source/drain regions <NUM>) may be formed by selectively growing an epitaxial film in etched-out portions of substrate <NUM> and are doped either in situ or after epitaxial film growth, or both. In an embodiment tip extensions <NUM> may be formed simultaneously with the source and drain regions to create "epi" tip extensions. In typical MOS-FETs, the channel region <NUM> is composed of a semiconductor material, such as single crystalline silicon. In an embodiment, the gate electrode <NUM> is a metal gate electrode (e.g., the workfunction of the gate electrode <NUM> is based on a metal or metal-containing layer). In one such embodiment, the metal gate electrode is composed, at least somewhat, of cobalt. For example, in a specific embodiment, the metal gate electrode <NUM> includes a Mn based adhesion layer (e.g., Mn, MnN, MnSixNy and the like as described above) 708A and a cobalt fill metal thereon 708B. For example, the cobalt-based material or film 708B is composed of at least <NUM>% cobalt. In a specific such embodiment, the cobalt-based material or film 708B is composed of a dilute alloy having approximately <NUM>-<NUM>% of a non-cobalt element, with the remainder approximately <NUM>+% cobalt.

Also, it is to be understood that the MOS-FET <NUM> may be a planar device or include a three-dimensional body (e.g., as in a double-gate, fin-fet, tri-gate, or gate-all-around transistor). As such, the substrate <NUM> may be a planar substrate or depict a cross-sectional view of a three-dimensional body. Finally, it is to be understood that only several features of the MOS-FET <NUM> are depicted for clarity. It is to be understood that isolation layers, e.g., interlayer dielectric layer <NUM>, and metallization routing layers used for integrating MOS-FET <NUM> into, e.g., an integrated circuit may also be included, as is well known in the art.

Various cobalt based embodiments may be included in, for example, a mobile computing node such as a cellular phone, Smartphone, tablet, Ultrabook®, notebook, laptop, personal digital assistant, and mobile processor based platform.

The following examples do not form part of the invention as claimed but may contain further useful information for understanding the embodiments of the invention.

Example <NUM> includes a dielectric layer disposed on a substrate; an opening in the dielectric layer, wherein the opening has sidewalls and exposes a conductive region of at least one of the substrate and an additional interconnect structure; an adhesive layer, comprising manganese, disposed over the conductive region and on the sidewalls; and a fill material, comprising cobalt, within the opening and on a surface of the adhesion layer. In an embodiment the dielectric directly contacts the substrate but in other embodiments one or more layers are between the dielectric and the substrate. In an embodiment the additional interconnect structure may include a via, a trench filled with metal (interconnect line), and the like. While examples have included dual damascene approaches the opening addressed immediately above need not have varying widths such as those found in, for example, <FIG> or the line over via commonly associated with dual damascene processes. As explained below, saying "an adhesive layer, comprising manganese, disposed over the conductive region" does not necessarily mean manganese will be in the portion of the adhesive layer that is over the conductive region. For example, "an adhesive layer, comprising manganese, disposed over the conductive region" is still satisfied if manganese in not in the adhesion layer portion over the conductive region but is in the adhesion layer that is on the sidewalls.

In example <NUM> the subject matter of Example <NUM> can optionally include wherein the fill material is composed of at least <NUM> atomic % cobalt.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the adhesion layer includes at least one element selected from a group consisting of silicon, nitrogen, carbon, hydrogen, and oxygen.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the adhesion layer is no thicker than 50A.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the adhesion layer directly contacts the fill material.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the adhesion layer directly contacts the conductive region. In another version of example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the adhesion layer directly contacts the conductive region and the dielectric layer.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the fill material includes at least one element selected from a group consisting of silicon and manganese. This may be due to silicon or manganese migrating from the adhesion layer into the fill material and/or this may be due to the fill material being deposited with silicon and/or manganese already present in addition to cobalt.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the fill material includes manganese that directly contacts the manganese included in the adhesion layer. The cobalt fill layer may include manganese and/or silicon. This may not be visually evident with a scanning electron microscopic (SEM) image or transmission electron microscopic (TEM) image but other detection methods may indicate the presence of manganese and/or silicon in the cobalt fill layer. The manganese and/or silicon may be present along the outer edge of the cobalt fill layer because the manganese and/or silicon may have migrated from the adhesion layer to the cobalt fill layer. For example, there is solubility between manganese and cobalt and the manganese from the adhesion layer, in contact with the fill layer, may have mixed with the cobalt fill layer. This migration helps the cobalt fill adhere to the adhesion layer and also allows the adhesion layer to function as a wetting layer for the cobalt fill layer. A wetting layer includes an initial layer of atoms epitaxially grown on a surface upon which self-assembled quantum dots or thin films are created.

An example concerns TEM energy dispersive x-rays (EDX). The small TEM probe electrons interact with material being imaged and that material emits x-rays from the different elements present within one pixel of the image. This allows for elemental maps of the image. Higher sensitivity is achieved by taking line scans across structures with more dwell time (e.g., across a via rather than every pixel in image). In an embodiment (example 8a) if there is manganese in the cobalt fill layer, the manganese may migrate to the adhesion layer/fill material interface improving adhesion. EDX may then detect manganese in the cobalt fill layer and around the adhesion layer/fill layer edge/interface. In an embodiment (example 8b) if manganese is at the adhesion layer/fill layer interface it might diffuse into cobalt and other interfaces (e.g., like top layer after CMP has been performed). Such a case would be detected in both the fill layer and around edges/interfaces. In an embodiment, if no diffusion of manganese occurs the manganese may only be in the fill layer of example 8a and at the interface in example 8b. In embodiment, if manganese is present both in <NUM> and the fill layer, the manganese may be detected in both areas. Diffusion may change relative concentrations/compositions and ability to adhere or wet so the processes of examples 8a and/or 8b take place but manganese may still be detectable in both scenarios in an embodiment.

An embodiment is similar to the embodiment of <FIG> but includes a dielectric capping layer/etch stop (e.g., similar or directly equal to the materials and structure of element <NUM>) that extends from the top surface on the left dielectric portion <NUM>, across the tops of <NUM> and <NUM>, and then across the top of the right dielectric portion <NUM>. This caps the polished metal and is later broken through by etch to form a via for a next layer just like shown with a via going through space <NUM> and through layer <NUM> in <FIG>. The cap protects the lines (e.g., material <NUM>) hermetically and manganese (which in this embodiment is mixed and present in cobalt fill <NUM>) would diffuse to the capping layer to improve adhesion of dielectric capping layer/etch stop to the cobalt <NUM> (e.g., by silicate formation). The manganese may diffuse from layer <NUM> or diffuse from an alloy cobalt fill layer that was deposited already including some amount of manganese. The dielectric cap may be deposited at a high temperature and so that temperature drives the thermal diffusion of manganese from within the layers <NUM> and/or <NUM> and/or <NUM> up to the top of the trench <NUM>. The manganese could be detected at the new dielectric cap/layer <NUM> interface by TEM EDX methods and the like.

In another example the subject matter of Examples <NUM>-<NUM> can optionally include a dielectric layer formed directly on top of the adhesive layer and the fill material, the dielectric layer comprising manganese; wherein the fill material also includes manganese. The manganese may have migrated from the adhesion layer and/or adhesion layer into the dielectric.

In another example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include a dielectric layer formed directly on top of the fill material, the dielectric layer comprising a first material; wherein the first material is also included in the fill material and the first material is selected from the group comprising Al, Ni, Cu, Ag, Au, Mn, Ti, V, Cr, Fe, Ta, W, Ru, P, B, C, N, Si, Ge, Mg, Zn, Rh, Pt, Cd, Hf, In, Sn, C, O, Be, Ca, Zr, Nb, Mo, Ir, Re, and Pd. The material may have migrated into the dielectric from the fill material.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein (a) the adhesion layer includes a first portion directly contacting the dielectric layer and second portion directly contacting the conductive region, and (b) the first portion includes a higher atomic % manganese than the second portion. Manganese bonds well with the dielectric as well as the cobalt fill layer. On the adhesion layer/dielectric interface manganese forms MnSixOy (e.g., Mn<NUM>[SiO<NUM>], MnSiO<NUM>), and other Mn based silicates. The silicate has the function of a diffusion barrier, preventing diffusion of cobalt into the surrounding dielectric and will also will have adhesive/wetting functions making sure cobalt adheres well to the dielectric. On the adhesion layer/cobalt fill layer interface metal-to-metal bonding occurs (e.g., between the manganese and cobalt) and results in some alloying at the interface. This bonding gives an additional benefit that manganese will dissolve at the via bottom (where in an embodiment the adhesion layer directly contacts the metal fill layer and possibly another interconnect or a conduction substrate portion). This lowers electrical resistance in the via at the adhesion layer interface to the other interconnect or conductive portion of the substrate. For example, the manganese from <NUM> that forms at the via bottom initially starts out as thick as similar <NUM> portions on ILD. After anneal the manganese may diffuse completely into the cobalt fill or may remain in layer <NUM>. The amount that remains may vary. Thus, in some embodiments the adhesion layer near the bottom of the via may have little to no manganese remaining after device processing is complete.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the fill material consists essentially of cobalt. In another example the subject matter of Examples <NUM>-<NUM> can optionally include wherein the adhesion layer does not completely separate the conductive region from the fill material and the fill material directly contacts a portion of the conductive region. Thus, by TEM EDX detection or otherwise (regardless of whether the adhesion layer completely or incompletely separates the fill material from the conductive region); there may be areas where no manganese in an adhesion layer separates the fill material from the conductive region. This may be deemed an area where there is no adhesion layer present that can be detected (regardless of whether the layer is there or not) and thus the "adhesion layer does not completely separate the conductive region from the fill material and the fill material directly contacts a portion of the conductive region.

Example <NUM> includes a method of forming a metal interconnect structure, comprising: forming an opening in a dielectric layer on a substrate, wherein the opening exposes a conductive region of at least one of the substrate and an additional interconnect structure; forming an adhesion layer, comprising manganese, in the opening and on the conductive region and also on the sidewalls; forming a fill material, comprising cobalt, within the opening and on a surface of the adhesion layer; and removing portions of the fill material and the adhesion layer above an upper surface of the dielectric layer.

In example <NUM> the subject matter of Example <NUM> can optionally include wherein the adhesion layer includes at least one element selected from a group consisting of silicon, nitrogen, carbon, hydrogen, and oxygen.

In example, <NUM> the subject matter of examples <NUM>-<NUM> can optionally include wherein the adhesion layer directly contacts the fill material.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the adhesion layer directly contacts the conductive region.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein (a) the adhesion layer includes a first portion directly contacting the dielectric layer and second portion directly contacting the conductive region, and (b) the first portion includes a higher atomic % manganese than the second portion.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include forming the adhesion layer with a conformal method and forming the fill layer with a method that is non-conformal.

In another example the subject matter of Examples <NUM>-<NUM> can optionally include forming a dielectric layer directly on top of the adhesive layer and the fill material, the dielectric layer comprising manganese; wherein the fill material also includes manganese. Again, the manganese may have migrated into the dielectric from the adhesive layer and/or fill material.

Example <NUM> includes a metal interconnect structure, comprising: a dielectric layer disposed on a substrate; an opening disposed in the dielectric layer and exposing a conductive region in at least one of the substrate and an additional interconnect structure, the opening having a lower portion and an upper portion; a plug comprising cobalt disposed in the lower portion of the opening; an adhesive layer, comprising manganese, disposed on the sidewalls; and a fill material comprising cobalt disposed on the plug and in the upper portion of the opening.

In example <NUM> the subject matter of Example <NUM> can optionally include wherein the adhesive layer directly contacts the plug and the dielectric.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the adhesive layer is between the plug and the fill material.

In example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include wherein the plug and fill material have different compositions.

In another example <NUM> the subject matter of Examples <NUM>-<NUM> can optionally include a dielectric layer formed directly on top of the adhesive layer and the fill material, the dielectric layer comprising manganese; wherein the fill material also includes manganese. The manganese may have migrated from the adhesion layer into the dielectric.

Claim 1:
An integrated circuit structure, comprising:
a dielectric layer (<NUM>) formed on an etch stop layer (<NUM>) disposed on a substrate (<NUM>);
a conductive region (<NUM>) comprising a metal silicide region formed in the substrate;
a trench in the dielectric layer (<NUM>) having a bottom and sidewalls (<NUM>), the trench bottom extending to a top surface (<NUM>) of the metal silicide region such that the trench passes through the etch stop layer (<NUM>);
an adhesion layer (<NUM>) along the bottom and sidewalls (<NUM>) of the trench, the adhesion layer comprising manganese; and
a fill material on the adhesion layer (<NUM>) within the trench comprising at least <NUM> atomic % cobalt.