Patent Description:
As conventional automobile interior product materials, there are an acrylonitrile-butadiene-styrene (ABS) resin, a composite resin prepared by mixing a polycarbonate (PC) resin with an acrylonitrile-butadiene-styrene (ABS) resin, a composite resin prepared by mixing a polycarbonate (PC) resin with acrylate-styrene-acrylonitrile (ASA) resin, a composite resin prepared by mixing a polycarbonate (PC) resin with a polybutylene terephthalate (PBT) resin, and the like. These materials have excellent physical properties, thus being used in various automobile interior components.

However, the materials may cause hydrolysis in a high-temperature and high-humidity environment to deteriorate physical properties. In particular, when a polycarbonate (PC) resin is mixed with a polybutylene terephthalate (PBT) resin, physical properties are decreased due to transesterification reaction. Accordingly, it is necessary to appropriately control a reaction.

Therefore, it is necessary to develop an automobile interior product material that can satisfy physical properties, such as mechanical properties and heat resistance, without causing hydrolysis in a dry environment, especially in a high-temperature and high-humidity environment.

<CIT> discloses a composition comprising (A) <NUM> to <NUM>% by weight of a polycarbonate resin, (B) <NUM> to <NUM>% by weight of a polybutylene terephthalate resin, (C) <NUM> to <NUM>% by weight of a polyethylene terephthalate resin, and for <NUM> parts by weight of the basic resin containing (D) <NUM> to <NUM> parts by weight of a methyl methacrylate-butadiene-styrene graft copolymer and (E) <NUM> to <NUM> parts by weight of a polyolefin-based polymer containing a glycidyl group, which can be, among other compounds, glycidyl (meth)acrylate or methacryl-glycidyl ether. <CIT> discloses a composition comprising a polycarbonate resin, a organopolysiloxane-polycarbonate block copolymer and poly(ethylene terephthalate), poly(butylene terephthalate), or a combination thereof. <CIT> discloses a polymer composition comprising at least one plasticizer, which can be a phthalate ester or a dialkyl phthalate and that reactive impact modifiers may be used in the composition, such as glycidyl (meth)acrylate copolymers.

Therefore, the present invention has been made in view of the above problems, and it is one object of the present invention to provide a composite resin composition for automobile interior products, wherein the composite resin composition includes optimal materials so that production cost can be reduced and the composite resin composition can be used for an unpainted product, thereby providing superior economic feasibility. In addition, heat resistance and hydrolysis resistance stability can be improved, the balance between physical properties such as mechanical properties and fluidity is satisfied, and excellent product reliability and appearance quality are provided.

It is another object of the present invention to provide an automobile interior product manufactured using the composite resin composition for automobile interior products.

The above and other objects can be accomplished by the present disclosure described below.

In accordance with an aspect of the present invention, the above and other objects can be accomplished by the provision of a composite resin composition for automobile interior products, including:.

The polyethylene terephthalate resin may include <NUM> to <NUM> % by weight of a crystallization rate reducing agent based on a total weight of the polyethylene terephthalate resin comprising the crystallization rate reducing agent.

The crystallization rate reducing agent may be one or more selected from the group consisting of isophthalic acid, cyclohexylene dimethanol, diethylene glycol and neopentyl glycol.

The polybutylene terephthalate resin may have an intrinsic viscosity of <NUM> dl/g or more, and the polyethylene terephthalate resin may have an intrinsic viscosity of <NUM> to <NUM> dl/g.

The polycarbonate resin may have a flow index (<NUM>, load: <NUM>) of <NUM> to <NUM>/<NUM>.

The polyorganosiloxane-polycarbonate resin may include a diorganosiloxane-derived block in an amount of <NUM> to <NUM> % by weight (calculated by a weight of diorganosiloxane compound) of the polyorganosiloxane-polycarbonate resin.

The (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer may include <NUM> to <NUM> % by weight of a conjugated diene compound based on the weight of (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer, <NUM> to <NUM> % by weight of an aromatic vinyl compound based on the weight of (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer, and <NUM> to <NUM> % by weight of a (meth) acrylate compound based on the weight of (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer.

A particle size of the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer may be <NUM> to <NUM>.

The dialkyl phthalate compound may have an alkyl group having <NUM> to <NUM> carbon atoms.

The carboxy-reactive epoxy resin may be one or more selected from among an ethylene-n-butyl acrylate-glycidyl methacrylate copolymer, an ethylene-glycidyl methacrylate copolymer, an ethylene-acrylic ester-glycidyl methacrylate copolymer, an ethylene-methyl acrylate-glycidyl methacrylate copolymer, an ethylene-dimethacrylate-glycidyl methacrylate copolymer, an ethylene-acrylate-glycidyl methacrylate copolymer and an ethylene-vinyl acetate-glycidyl methacrylate copolymer.

The carboxy-reactive epoxy resin may include <NUM> to <NUM> % by weight of a glycidyl methacrylate-derived unit.

An intrinsic viscosity of the polybutylene terephthalate resin may be higher than an intrinsic viscosity of the polyethylene terephthalate resin.

The polyethylene terephthalate resin may have a melting point of <NUM> or less.

A high-load heat resistance, measured under <NUM> MPa according to ISO <NUM>, of the composite resin composition may be <NUM> or more.

A hydrolysis-resistance retention rate, which is represented by Equation <NUM> below, of the composite resin composition may be <NUM>% or more:
<MAT>
where aging is performed for <NUM> hr in a chamber under conditions of <NUM> and <NUM>%, and Izod impact strength is a notch impact strength measured at <NUM> according to ISO <NUM>/1A.

In accordance with another aspect of the present invention, there is provided a composite resin composition, including:.

In accordance with still another aspect of the present invention, there is provided a method of preparing a composite resin composition, the method comprising:
a step of feeding <NUM> parts by weight of the composite resin comprising <NUM> to <NUM> % by weight of a polycarbonate resin based on <NUM> % by weight of a total of the composite resin, <NUM> to <NUM> % by weight of a polybutylene terephthalate resin based on <NUM> % by weight of a total of the composite resin and <NUM> to <NUM> % by weight of a polyethylene terephthalate resin based on <NUM> % by weight of a total of the composite resin; and <NUM> to <NUM> parts by weight of a hydrolysis stabilizer prepared by mixing <NUM> to <NUM> % by weight of a polyorganosiloxane-polycarbonate resin based on <NUM> % by weight of a total of the hydrolysis stabilizer, <NUM> to <NUM> % by weight of a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer based on <NUM> % by weight of a total of the hydrolysis stabilizer, <NUM> to <NUM> % by weight of a dialkyl phthalate compound based on <NUM> % by weight of a total of the hydrolysis stabilizer and <NUM> to <NUM> % by weight of a carboxy-reactive epoxy resin into an extruder based on <NUM> % by weight of a total of the hydrolysis stabilizer, followed by melt-kneading and extruding.

The step of melt-kneading and extruding the composite resin composition may be performed under conditions of <NUM> to <NUM>, an F/R (flow ratio) of <NUM> to <NUM>/hr, and a screw rotation number of <NUM> to <NUM> rpm.

After extruding the composite resin composition, a step of injecting the composite resin composition at an injection temperature of <NUM> to <NUM> and a mold temperature of <NUM> to <NUM> may be further performed.

In accordance with still another aspect of the present invention, there is provided a method of preparing a composite resin composition, the method comprising:.

In accordance with yet another aspect of the present invention, there is provided an automobile interior product manufactured using the composite resin composition.

The automobile interior product may include a floor console front tray, a cup holder, an inner garnish, a switch bezel, a cup holder housing, or an indicator panel.

A composite resin composition for automobile interior products according to the present invention includes a composite resin comprising a polycarbonate resin, a polybutylene terephthalate resin and a polyethylene terephthalate resin in specific % by weight; and a hydrolysis stabilizer prepared by mixing a polyorganosiloxane-polycarbonate resin, a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer, a dialkyl phthalate compound and a carboxy-reactive epoxy resin in specific % by weight and can be used to mold an automobile interior product.

In addition, an automobile interior product manufactured using the composition has improved heat resistance and hydrolysis resistance stability, thus satisfying the balance between physical properties such as mechanical properties and fluidity and providing improved appearance quality due to excellent moldability.

Therefore, the composite resin composition for automobile interior products according to the present invention and a molded article manufactured using the same can be applied to automobile interior products such as a floor console front tray, a cup holder, an inner garnish, a switch bezel, a cup holder housing, and an indicator panel.

Hereinafter, the present invention will be described in more detail to help the understanding of the present invention.

The terms or words used in the present specification and claims should not be construed as being limited to conventional or dictionary meanings, and considering that inventors can appropriately define the concept of a term to describe the invention in the best way, it should be interpreted as a meaning and concept consistent with the technical idea of the present invention.

In the present disclosure, "comprising" may be defined as "polymerized comprising" or "comprising as a unit derived. ," unless otherwise defined.

Unless otherwise specified, all numbers, values, and/or expressions expressing the quantities of ingredients, reaction conditions, polymer compositions and formulations used in the present disclosure are approximations reflecting various uncertainties due to measurements conducted to obtain the values from essentially different values. Accordingly, it should be understood as being modified by the term "about" in all cases. Also, when numerical ranges are disclosed in the present disclosure, such ranges are continuous and include all values from the minimum values to the maximum values of the ranges, unless otherwise indicated. Furthermore, when such ranges refer to integers, all integers including from the minimum value to the maximum value are included, unless otherwise specified.

In the present disclosure, when a variable is expressed as a range, it will be understood that the variable includes all values within the range including the endpoints of the range. For example, it will be understood that a range from "<NUM> to <NUM>" includes the values of <NUM>,<NUM>,<NUM>,<NUM>,<NUM> and <NUM>, as well as any subranges from <NUM> to <NUM>, <NUM> to <NUM>, <NUM> to <NUM>, <NUM> to <NUM>, etc. and any values between integers that fall within the scope of the recited range such as <NUM> to <NUM>, and <NUM> to <NUM>, and the like. Also, it will be understood that a range from <NUM> to <NUM>% include values of <NUM>%, <NUM>%, <NUM>%, <NUM>%, etc. and all integers including up to <NUM>%, as well as any values between valid integers within the range of stated ranges such as <NUM>%, <NUM>%, <NUM>%, etc..

The term "hydrolysis stabilizer" used in the present disclosure refers to a substance that is added to improve hydrolysis resistance stability unless otherwise specified.

The present inventors have confirmed that an interior material for automobiles prepared using a composite resin composition comprising a composite resin including a polycarbonate resin, a polybutylene terephthalate resin and a polyethylene terephthalate resin in specific % by weight; and a hydrolysis stabilizer prepared by mixing a polyorganosiloxane-polycarbonate resin, a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer, a dialkyl phthalate compound and a carboxy-reactive epoxy resin in specific % by weight exhibits improved heat resistance and hydrolysis resistance stability so that the balance between physical properties such as mechanical properties and fluidity is satisfied and excellent product reliability and appearance quality are provided. In addition, the present inventors have completed an interior product material for automobiles that has excellent moldability and appearance quality while satisfying the balance between physical properties such as mechanical properties and fluidity and does not need to be painted.

A composite resin composition according to an embodiment of the present invention includes <NUM> parts by weight of a composite resin comprising <NUM> to <NUM> % by weight of a polycarbonate resin based on <NUM> % by weight of a total of the composite resin, <NUM> to <NUM> % by weight of a polybutylene terephthalate resin based on <NUM> % by weight of a total of the composite resin and <NUM> to <NUM> % by weight of a polyethylene terephthalate resin based on <NUM> % by weight of a total of the composite resin; and <NUM> to <NUM> parts by weight of a hydrolysis stabilizer prepared by mixing <NUM> to <NUM> % by weight of a polyorganosiloxane-polycarbonate resin based on <NUM> % by weight of a total of the hydrolysis stabilizer, <NUM> to <NUM> % by weight of a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer based on <NUM> % by weight of a total of the hydrolysis stabilizer, <NUM> to <NUM> % by weight of a dialkyl phthalate compoundbased on <NUM> % by weight of a total of the hydrolysis stabilizer, and <NUM> to <NUM> % by weight of a carboxy-reactive epoxy resin based on <NUM> % by weight of a total of the hydrolysis stabilizer.

When a polycarbonate resin according to an embodiment of the present invention is included in a composite resin composition, the composite resin composition may be imparted with hydrolysis resistance stability and heat resistance. An automobile interior product prepared using the composite resin composition provides improved mechanical properties and fluidity and improves the appearance of an injected product.

The polycarbonate resin may have a flow index (<NUM>, load: <NUM>) of <NUM> to <NUM>/<NUM> or more, <NUM> to <NUM>/<NUM>, or <NUM> to <NUM>/<NUM>. When the flow index too low outside the range, it is difficult to perform injection molding. When the flow index is too high, moldability, mechanical properties and chemical resistance are decreased, which may cause problems in the appearance of components.

In the present disclosure, the flow index may be a melt flow index measured under a load of <NUM> at <NUM> according to ISO <NUM>, unless otherwise specified.

The polycarbonate resin is not specifically limited and may be prepared and used by a method known in the art. Alternatively, a commercially available material may be used.

For example, the polycarbonate resin may be prepared by reacting a diphenol compound with a phosgene compound, a halogen acid ester compound, a carbonic acid ester compound or a combination thereof in the presence of a molecular weight regulator and a catalyst.

The diphenol compound may be, without being specifically limited to, <NUM>,<NUM>'-dihydroxydiphenyl, <NUM>,<NUM>-bis-(<NUM>-hydroxyphenyl)-propane, <NUM>,<NUM>-bis- (<NUM>-hydroxyphenyl)-<NUM>-methylbutane, <NUM>,<NUM>-bis- (<NUM>-hydroxyphenyl)-cyclohexane, <NUM>,<NUM>-bis- (<NUM>-chloro-<NUM>-hydroxyphenyl)-propane, <NUM>,<NUM>-bis- (<NUM>,<NUM>-dichloro-<NUM>-hydroxyphenyl)-propane, or the like. Preferably, the diphenol compound may be bisphenol A, <NUM>,<NUM>-bis- (<NUM>-hydroxyphenyl)-propane.

The polycarbonate resin may be a homopolymer, a copolymer including two or more types of diphenol compounds, or a mixture thereof and may be a linear polycarbonate resin, a branched polycarbonate resin or a polyestercarbonate copolymer, preferably a linear polycarbonate resin. The linear polycarbonate resin refers to a resin excluding a crosslinking agent, unless otherwise specified. As a particular example, the linear polycarbonate resin may be a bisphenol A-based polycarbonate resin.

The content of the polycarbonate resin may be <NUM> to <NUM> % by weight based on <NUM> % by weight of a total of the composite resin (polycarbonate resin + polybutylene terephthalate resin + polyethylene terephthalate resin). As a particular example, the content of the polycarbonate resin may be <NUM> to <NUM> % by weight, preferably <NUM> to <NUM> % by weight. When the content of the polycarbonate resin is less than range, an automobile interior product prepared using a composite resin composition including the polycarbonate resin may be cracked. When the content of the polycarbonate resin exceeds the range, the stiffness and heat resistance of an automobile interior product prepared using a composite resin composition including the polycarbonate resin are decreased.

That is, when the polycarbonate resin according to an embodiment of the present invention includes a polycarbonate resin in a content of <NUM> to <NUM> % by weight based on <NUM> % by weight of a total of the composite resin, a composite resin composition is provided with moldability and thus an automobile interior product prepared using the composite resin composition may realize fluidity, mechanical strength, heat resistance, appearance quality.

The polybutylene terephthalate resin and polyethylene terephthalate resin according to an embodiment of the present invention are crystalline materials. A composite resin composition including the polybutylene terephthalate resin and the polyethylene terephthalate resin is imparted with moldability, and an automobile interior product prepared using the composite resin composition is imparted with chemical resistance.

The polybutylene terephthalate resin is a crystalline resin and thus prevents the penetration of chemicals introduced from the outside. When the polybutylene terephthalate resin is included in a composite resin composition, the flowability of the composite resin composition is improved during injection molding so that excellent appearance quality is provided.

The intrinsic viscosity of the polybutylene terephthalate resin may be <NUM> dl/g or more, or <NUM> to <NUM> dl/g. When the intrinsic viscosity is too low outside the range, the effect of reinforcing physical properties is decreased so that the effect of improving chemical resistance is insignificant. When the intrinsic viscosity is too high, moldability is decreased so that problems in the appearance of components may occur.

In the present disclosure, when intrinsic viscosity is measured, unless noted otherwise, a sample to be measured is completely dissolved in a methylene chloride solvent at a concentration of <NUM>/ml, and then is filtered using a filter to obtain a filtrate. Then, using the obtained filtrate, intrinsic viscosity is measured at <NUM> using a Ubbelohde viscometer.

The content of the polybutylene terephthalate resin may be <NUM> to <NUM> % by weight, <NUM> to <NUM> % by weight as a particular example, preferably <NUM> to <NUM> % by weight, based on <NUM> % by weight of a total of the composite resin (polycarbonate resin + polybutylene terephthalate resin + polyethylene terephthalate resin). When the polybutylene terephthalate resin is included in a content less than the range, an automobile interior product prepared using a composite resin composition including the polybutylene terephthalate resin may be cracked. When the polybutylene terephthalate resin is included in a content greater than the range, the stiffness and heat resistance of an automobile interior product prepared using a composite resin composition including the polybutylene terephthalate resin are decreased.

The intrinsic viscosity of the polybutylene terephthalate resin may be greater than the intrinsic viscosity of the polyethylene terephthalate resin.

In the present disclosure, the intrinsic viscosity of the polyethylene terephthalate resin may be <NUM> to <NUM> dl/g, or <NUM> to <NUM> dl/g. When the intrinsic viscosity is too low outside the range, the effect of reinforcing physical properties is decreased so that the effect of improving chemical resistance is insignificant. When the intrinsic viscosity is too high, moldability is decreased so that problems in the appearance of components may occur.

The polyethylene terephthalate resin may include a crystallization rate reducing agent.

The crystallization rate reducing agent may be one or more selected from the group consisting of isophthalic acid, cyclohexylene dimethanol, diethylene glycol and neopentyl glycol. Considering the reaction efficiency, isophthalic acid or cyclohexylene dimethanol is preferred.

In a step of preparing a polyethylene terephthalate resin, the crystallization rate reducing agent may be added together with raw materials including terephthalic acid and ethylene or after primarily reacting terephthalic acid with ethylene glycol.

Here, the amount of the crystallization rate reducing agent may be less than <NUM> % by weight, particularly <NUM> to <NUM> % by weight based on a total weight of the polyethylene terephthalate resin including the crystallization rate reducing agent.

The polyethylene terephthalate resin is not specifically limited and may be prepared and used by a method known in the art. Alternatively, a commercially available material may be used.

For example, the polyethylene terephthalate resin may be prepared by reacting a terephthalic acid compound with a glycol-based compound (except for diethylene glycol and neopentyl glycol) such as ethylene glycol in the presence of one or more crystallization rate reducing agents selected from the group consisting of isophthalic acid, cyclohexylene dimethanol, diethylene glycol and neopentyl glycol.

The polyethylene terephthalate resin may have a melting point of <NUM> or less, particularly <NUM> to <NUM>. In this case, the melt flow index of the composite resin composition may be improved, thus improving moldability.

In the present disclosure, the melting point may be measured using a method known in the art. For example, a heat absorption peak may be measured using a differential scanning calorimeter (DSC).

The content of the polyethylene terephthalate resin may be <NUM> to <NUM> % by weight, particularly <NUM> to <NUM> % by weight, based on <NUM> % by weight of a total of the composite resin (polycarbonate resin + polybutylene terephthalate resin + polyethylene terephthalate resin). When the content of the polyethylene terephthalate resin is less than the range, an automobile interior product prepared using a composite resin composition including the polyethylene terephthalate resin may be cracked. When the content of the polyethylene terephthalate resin exceeds the range, the stiffness and heat resistance of an automobile interior product prepared using a composite resin composition including the composite resin composition are deceased.

In the present disclosure, the hydrolysis stabilizer may be composed of a quaternary system prepared by mixing a polyorganosiloxane-polycarbonate resin, a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer, a dialkyl phthalate compound and a carboxy-reactive epoxy resin, unless otherwise specified.

The polyorganosiloxane-polycarbonate resin according to an embodiment of the present invention is a block copolymer. When a composite resin composition includes the polyorganosiloxane-polycarbonate resin together with a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer described below, the hydrolysis resistance stability of the composite resin composition is greatly affected and an automobile interior product prepared using the composite resin composition exhibits a hydrolysis-resistant stabilization effect.

The polyorganosiloxane-polycarbonate resin is not specifically limited so long as the properties thereof can be secured and may include preferably a polysiloxane-polycarbonate copolymer, a polycarbonate-polysiloxane polymer or a polysiloxane-polycarbonate polymer. Preferably, the polyorganosiloxane-polycarbonate resin includes a diorganosiloxane block including a structural unit represented by Formula <NUM> below:
<CHM>
<CHM>.

In Formula <NUM>, the length (E) of a polydiorganosiloxane block is <NUM> to <NUM>, respective R groups are the same or different and are independently selected from C1-C13 alkyl, C1-C13 alkoxy, C2-C13 alkenyl, C2-C13 alkenyloxy, C3-C13 cycloalkyl, C3-C13 cycloalkoxy, C6-C13 aryl, C6-C13 aryloxy, C7-C13 aralkyl, C7-C13 aralkyloxy, C7-C13 alkylaryl and C7-C13 alkylaryloxy; respective M are the same or different and are selected from among halogen, cyano, nitro, C1-C8 alkylthio, C1-C8 alkyl, C1-C8 alkoxy, C2-C8 alkenyl, C2-C8 alkenyloxy, C3-C8 cycloalkyl, C1-C8 cycloalkoxy, C6-C10 aryl, C6-C10 aryloxy, C7-C12 aralkyl, C7-C12 aralkyloxy, C7-C12 alkylaryl and C7-C12 alkylaryloxy; and respective n are independently an integer of <NUM> to <NUM>.

In the present disclosure, the polycarbonate-diorganosiloxane block copolymer may include a diorganosiloxane block represented by Formula <NUM> below:
<CHM>.

In Formula <NUM>, x represents an integer of <NUM> to <NUM>, and a terminal group of a short chain directly connected to Si represents CH3.

In the present disclosure, the polycarbonate block may be derived from a bisphenol-A monomer, and the diorganosiloxane block of Formula <NUM> may be derived from a dihydroxypolysiloxane compound obtained by reacting dihydroxyarylene with, for example, α,ω-bisacetoxypolydiorganosiloxane in a phase transition condition.

The dihydroxypolysiloxane compound may be prepared by platinum catalyzed addition reaction between siloxane hydrides.

The polyorganosiloxane-polycarbonate resin may include a diorganosiloxane-derived block in an amount of <NUM> to <NUM> % by weight, particularly <NUM> to <NUM> % by weight (calculated based on the weight of the diorganosiloxane compound). When the diorganosiloxane-derived block is present in a small amount outside the range, the effect of reinforcing physical properties is decreased so that hydrolysis resistance stability is insignificant. When the diorganosiloxane-derived block is present in an excessive amount, moldability is decreased which may cause problems in the appearance of components.

In the present disclosure, % by weight of a unit in a polymer, % by weight of a unit, or % by weight of a block may mean % by weight of a derived monomer.

In addition, in the present disclosure, % by weight of a unit in a polymer, % by weight of a unit, or % by weight of a block may be measured by a method generally used in the technical field to which the present invention pertains. As another method, on the premise that all monomers are polymerized, the contents of added monomers may be defined as a content such as a unit in a prepared polymer.

The polyorganosiloxane-polycarbonate resin may have a flow index of <NUM> to <NUM>/<NUM>, <NUM> to <NUM>/<NUM>, or <NUM> to <NUM>/<NUM>. When the flow index of the polyorganosiloxane-polycarbonate resin is too low outside the range, it is difficult to perform injection molding. When the flow index of the polyorganosiloxane-polycarbonate resin is too high, moldability, mechanical properties and chemical resistance are decreased so that problems in the appearance of components may occur.

The content of the polyorganosiloxane-polycarbonate resin may be <NUM> to <NUM> % by weight, <NUM> to <NUM> % by weight as a particular example, preferably <NUM> to <NUM> % by weight, based on <NUM> % by weight of a total of the hydrolysis stabilizer (polyorganosiloxane-polycarbonate resin + (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer + dialkyl phthalate compound + carboxy-reactive epoxy resin). When the content of the polyorganosiloxane-polycarbonate resin is less than the range, an automobile interior product prepared using a composite resin composition including the polyorganosiloxane-polycarbonate resin may be cracked. When the content of the polyorganosiloxane-polycarbonate resin exceeds the range, the stiffness and heat resistance of an automobile interior product prepared using a composite resin composition including the polyorganosiloxane-polycarbonate resin are decreased.

A (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer according to an embodiment of the present invention may compensate for reduced physical properties due to the polycarbonate resin and the polyester resin. An automobile interior product prepared using a composite resin composition including the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer may have improved impact resistance, mechanical properties, and hydrolysis resistance stability.

The (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer may be a graft copolymer including <NUM> to <NUM> % by weight of a conjugated diene compound, <NUM> to <NUM> % by weight of an aromatic vinyl compound and <NUM> to <NUM> % by weight of a vinyl cyanide compound, preferably a graft copolymer including <NUM> to <NUM> % by weight of a conjugated diene compound, <NUM> to <NUM> % by weight of an aromatic vinyl compound and <NUM> to <NUM> % by weight of a vinyl cyanide compound, more preferably a graft copolymer including <NUM> to <NUM> % by weight of a conjugated diene compound, <NUM> to <NUM> % by weight of an aromatic vinyl compound and <NUM> to <NUM> % by weight of a vinyl cyanide compound. When the content of the conjugated diene compound is too low outside the range, impact resistance is decreased. When the content of the conjugated diene compound is too high, stiffness (modulus of elasticity) is decreased. In addition, when the content of the vinyl cyanide compound is too small, the effect of reinforcing rigidity is insufficient. When the content of the vinyl cyanide compound is too high, impact resistance is decreased.

The (meth)acrylate compound included in the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer of the present invention may include a general (meth)acrylate compound, for example, methacrylate or acrylate, without being limited to a specific (meth)acrylate compound. For example, the (meth) acrylate compound may be one or more selected from methacrylate and acrylate, preferably methacrylate. In addition, the conjugated diene compound included in the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer may include, for example, butadiene, without being limited to a specific conjugated diene compound. In addition, the aromatic vinyl compound included in the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer may be, for example, one or more selected from among styrene, α-methyl styrene, α-ethyl styrene and p-methyl styrene, preferably styrene.

Accordingly, the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer may include a resin prepared by polymerizing the components in the above specific content ranges. Preferably, the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer includes a resin including a (meth)acrylate component in an appropriate content and, accordingly, being capable of improving heat resistance. As needed, an alkyl acrylate component may be further included in addition to the (meth)acrylate component.

The (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer may be used in a powder form having a particle size of <NUM> to <NUM>, particularly a particle size of <NUM> to <NUM>. In this case, impact strength and injection molding properties are improved.

In the present disclosure, a particle size may be measured according to a known method of measuring the size of particles. Specifically, the average particle diameter of the metal pigment may be measured using BET analysis equipment (Surface Area and Porosity Analyzer ASAP <NUM>, Micromeritics Co. ) according to a nitrogen gas adsorption method. More particularly, a particle size may be measured using ASAP <NUM> analysis equipment at room temperature after adding <NUM> to <NUM> of a sample to a tube and pre-treating the sample at <NUM> for <NUM> hours. An average value may be obtained by measuring the same sample three times.

The content of the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer may be <NUM> to <NUM> % by weight, particularly <NUM> to <NUM> % by weight, based on <NUM> % by weight of a total of the hydrolysis stabilizer (polyorganosiloxane-polycarbonate resin + (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer + dialkyl phthalate compound + carboxy-reactive epoxy resin). When the content of the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer is less than the range, an automobile interior product prepared using a composite resin composition including the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer has low impact resistance. When the content of the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer exceeds the range, an automobile interior product prepared using a composite resin composition including the (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer exhibits deteriorated stiffness.

A dialkyl phthalate compound according to an embodiment of the present invention serves to inhibit various routes of transesterification reactions between the polycarbonate resin and polybutylene terephthalate resin described above.

For reference, when a polycarbonate (PC) resin is mixed with a polybutylene terephthalate (PBT) resin, physical properties are reduced by three types of transesterification reactions as shown below, so that appropriate reaction inhibition is required.

The dialkyl phthalate compound may be a compound being capable of securing transesterification inhibitory properties, preferably a phthalate compound having an alkyl group having <NUM> to <NUM> carbon atoms. As a particular example, di-n-pentyl phthalate, di-n-octyl phthalate or a combination thereof may be used.

The content of the dialkyl phthalate compound may be <NUM> to <NUM> % by weight, <NUM> to <NUM> % by weight as a particular example, preferably <NUM> to <NUM> % by weight, based on <NUM> % by weight of a total of the hydrolysis stabilizer (polyorganosiloxane-polycarbonate resin + (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer + dialkyl phthalate compound + carboxy-reactive epoxy resin). When the content of the dialkyl phthalate compound is too high outside the range, the dialkyl phthalate compound is generated as a gas in a molded article during injection molding, which may affect the appearance quality.

The carboxy-reactive epoxy resin according to an embodiment of the present invention may be used to improve chemical resistance while providing hydrolysis resistance stability to an automobile interior product prepared using the composite resin composition according to the present disclosure.

As used herein, the term "carboxy-reactive epoxy resin" refers to an epoxy-functional alkylene (meth)acrylic copolymer generated from an epoxy-functional (meth)acrylic monomer and an alkylene, unless otherwise specified.

As used herein, the term " (meth)acrylic" includes both acrylic and methacrylic monomers, unless otherwise specified, and the term " (meth)acrylate" includes both acrylate and methacrylate monomers, unless otherwise specified.

Specific examples of the epoxy-functional (meth) acrylic monomer may include monomers containing a <NUM>,<NUM>-epoxy group such as glycidyl acrylate and glycidyl methacrylate.

The carboxy-reactive epoxy resin used in the present disclosure may be one or more selected from, as a particular example, an ethylene-n-butyl acrylate-glycidyl methacrylate copolymer, an ethylene-glycidyl methacrylate copolymer, an ethylene-acrylic ester-glycidyl methacrylate copolymer, an ethylene-methyl acrylate-glycidyl methacrylate copolymer, an ethylene-dimethacrylate-glycidyl methacrylate copolymer, an ethylene-acrylate-glycidyl methacrylate copolymer and an ethylene-vinyl acetate-glycidyl methacrylate copolymer.

The carboxy-reactive epoxy resin of the present disclosure may be, for example, a copolymer prepared by polymerizing <NUM> to <NUM> % by weight or <NUM> to <NUM> % by weight of a glycidyl methacrylate unit, <NUM> to <NUM> % by weight or <NUM> to <NUM> % by weight of an ethylene unit, and <NUM> to <NUM> % by weight or <NUM> to <NUM> % by weight of an n-butyl acrylate. Here, when the content of the glycidyl methacrylate unit is too high, the appearance quality of an injection-molded article manufactured using a composite resin composition including the glycidyl methacrylate unit is decreased due to a decrease in the flow of the composition.

The content of the carboxy-reactive epoxy resin may be <NUM> to <NUM> % by weight, <NUM> to <NUM> % by weight as a particular example, preferably <NUM> to <NUM> % by weight, based on <NUM> % by weight of a total of the hydrolysis stabilizer (polyorganosiloxane-polycarbonate resin + (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer + dialkyl phthalate compound + carboxy-reactive epoxy resin). When the content of the carboxy-reactive epoxy resin is too high outside the range, gas may be generated from the surface of an automobile interior product prepared using a composite resin composition including the carboxy-reactive epoxy resin, resulting in decrease in appearance quality.

In particular, the hydrolysis stabilizer (polyorganosiloxane-polycarbonate resin + (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer + dialkyl phthalate compound + carboxy-reactive epoxy resin) may be included in an amount of <NUM> to <NUM> parts by weight, <NUM> to <NUM> parts by weight as a particular example, <NUM> to <NUM> parts by weight as a preferred example, based on <NUM> parts by weight of the composite resin including a polycarbonate resin, a polybutylene terephthalate resin and a polyethylene terephthalate resin. When the content of the hydrolysis stabilizer is too high outside the range, the appearance quality of the surface of an injection-molded article prepared an automobile interior product prepared using a composite resin composition including the hydrolysis stabilizer may be decreased. When the content of the hydrolysis stabilizer is too low, sufficient hydrolysis resistance stability and further transesterification inhibitory effect may not be provided. Within the above range, impact strength, specifically low-temperature impact strength, heat resistance and processability may be improved.

To improve the flowability of the composite resin composition according to an embodiment of the present invention, an appropriate additive may be further included.

Specifically, one or more additives selected from a lubricant, a heat stabilizer, and a UV absorber may be further included.

The lubricant is not specifically limited so long as it can ensure ease of extraction and flowability of an injection screw used for manufacturing an automobile interior product using a composite resin composition including the lubricant.

The lubricant is not specifically limited so long as it can be used in the present invention and the above characteristics can be secured. Preferably, the lubricant may include ethylene bis stearamide, polyethylene wax or a combination thereof.

The content of the lubricant may be <NUM> to <NUM> parts by weight, particularly <NUM> to <NUM> parts by weight, <NUM> parts by weight of the composite resin. When the content of the lubricant is too high outside the range, appearance problems such as stains may be generated on the surface of an automobile interior product prepared using a composite resin composition including the lubricant so that appearance quality may be decreased.

The heat stabilizer is not specifically limited so long as an automobile interior product prepared using a composite resin composition including the heat stabilizer can be prevented from being deformed due to high temperature.

The heat stabilizer is not specifically limited so long as the above characteristics can be secured, and is preferably a phenolic antioxidant.

The phenolic antioxidant may further include a hindered phenol-based stabilizer having crystallization temperature (Tm) of <NUM> to <NUM>. As a particular example, the phenolic antioxidant may include tetrakis[ethylene-<NUM>-(<NUM>,<NUM>-di-t-butyl-hydroxyphenyl)propionate], octadecyl <NUM>-(<NUM>,<NUM>-di-t-butyl-<NUM>-hydroxyphenyl)propionate or a combination thereof.

The content of the heat stabilizer may be <NUM> to <NUM> parts by weight, particularly <NUM> to <NUM> parts by weight, based on <NUM> parts by weight of the composite resin. Then the content of the heat stabilizer is too high, appearance problems such as stains may occur on the surface of an automobile interior product prepared using a composite resin composition including so that appearance quality may be decreased.

The UV absorber is not specifically limited so long as an automobile interior product prepared using a composite resin composition including the UV absorber can be prevented from being deformed by light.

The UV absorber is not specifically limited so long as the above characteristics can be secured, and may be preferably a benzotriazole-based compound, a triazine-based compound, or the like.

The triazine-based compound may be one or more selected from the group consisting of, for example, <NUM>,<NUM>-diphenyl-<NUM>- (<NUM>-hydroxy-<NUM>-methoxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>-diphenyl-<NUM>- (<NUM>-hydroxy-<NUM>-ethoxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>-diphenyl-<NUM>- (<NUM>-hydroxy-<NUM>-butoxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>-diphenyl-<NUM>- (<NUM>-hydroxy-<NUM>-hexyloxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>-diphenyl-<NUM>- (<NUM>-hydroxy-<NUM>-octyloxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>-diphenyl-<NUM>- (<NUM>-hydroxy-<NUM>-benzyloxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>,<NUM>-tris (<NUM>-hydroxy-<NUM>-octyloxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>,<NUM>-tris (<NUM>-hydroxy-<NUM>-benzyloxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>,<NUM>-tris (<NUM>-hydroxy-<NUM>-ethoxyethoxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>,<NUM>-tris (<NUM>-hydroxy-<NUM>-butoxyethoxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>,<NUM>-tris (<NUM>-hydroxy-<NUM>-methoxycarbonylpropyloxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>,<NUM>-tris (<NUM>-hydroxy-<NUM>-methyl-<NUM>-ethoxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>,<NUM>-tris (<NUM>-hydroxy-<NUM>-methyl-<NUM>-hexyloxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>,<NUM>-tris (<NUM>-hydroxy-<NUM>-methyl-<NUM>-ethoxyethoxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>,<NUM>-tris (<NUM>-hydroxy-<NUM>-methyl-<NUM>-ethoxycarbonylethyloxyphenyl)-<NUM>,<NUM>,<NUM>-triazine, <NUM>,<NUM>-bis (<NUM>,<NUM>-dimethylphenyl)-<NUM>- (<NUM>-hydroxy-<NUM>-N-octyloxyphenyl)-<NUM>,<NUM>,<NUM>-triazine and <NUM>- (<NUM>,<NUM>-diphenyl-<NUM>,<NUM>,<NUM>-triazine-<NUM>-yl)-<NUM>- (<NUM>- (<NUM>-ethylhexanoyloxy)ethoxy)phenol.

The benzotriazole-based compound may be one or more selected from among, for example, <NUM>,<NUM>-di-t-butyl-<NUM>- (<NUM>-chlorobenzotriazole-<NUM>-yl) phenol, <NUM>- (<NUM>'-hydroxy-<NUM>'-oxyphenyl)-benzotriazole, <NUM>- (<NUM>'-hydroxymethylphenyl)benzotriazole, <NUM>- (<NUM>'-hydroxy-<NUM>',<NUM>'-bis (α,α-dimethylbenzylphenyl)benzotriazole, <NUM>- (<NUM>'-hydroxy-<NUM>',<NUM>'-dibutylphenyl)benzotriazole, <NUM>- (<NUM>'-hydroxy-<NUM>'-tert-butyl-<NUM>'-methylphenyl)-<NUM>-chlorobenzotriazole, <NUM>, (<NUM>'-hydroxy-<NUM>',<NUM>'-di-tert-amyl)benzotriazole, <NUM>,<NUM>'-methylene bis[<NUM>- (<NUM>,<NUM>,<NUM>,<NUM>-tetramethylbutyl)-<NUM>- (<NUM>-N-benzotriazole-<NUM>-yl)phenol', <NUM>- (<NUM>,<NUM>-diphenyl-<NUM>,<NUM>,<NUM>-triazine-<NUM>-yl)-<NUM>-hexyloxyl-phenol and <NUM>- (<NUM>-benzotriazole-<NUM>-yl)-<NUM>,<NUM>-bis (<NUM>-methyl-<NUM>-phenylethyl) phenol.

The content of the UV absorber may be <NUM> to <NUM> parts by weight, particularly <NUM> to <NUM> parts by weight, based on <NUM> parts by weight of the composite resin. Within these ranges, physical properties balance is excellent and light resistance is further improved.

A specimen may be manufactured using the composite resin composition. A heat deflection temperature under high load, measured under <NUM> MPa according to ISO <NUM>, of the specimen may be <NUM> or more. As a particular example, the heat deflection temperature under high load may be <NUM> to <NUM>. The specimen will be described in detail below.

In the present disclosure, the heat deflection temperature under high load may be measured under a high load of <NUM> MPa according to ISO <NUM>.

A hydrolysis-resistance retention rate, represented by Equation <NUM> below, of the composite resin composition may be, for example, <NUM>% or more. As a particular example, the hydrolysis-resistance retention rate may be <NUM> to <NUM>%. In this case, optimal balance between heat resistance and hydrolysis-resistance retention may be maintained. <MAT>
(in the equation, aging is performed for <NUM> hr in a chamber under conditions of <NUM> and <NUM>%, and the Izod impact strength is a notch impact strength measured at <NUM> according to ISO <NUM>/1A.

Hereinafter, a method of preparing the composite resin composition of the present invention is described. In describing the method of preparing the composite resin composition of the present invention, all of the above particulars regarding the composite resin composition are included.

The method of preparing the composite resin composition of the present disclosure includes, for example, a step of feeding <NUM> parts by weight of a composite resin including <NUM> to <NUM> % by weight of a polycarbonate resin based on the weight of (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer, a polybutylene terephthalate resin <NUM> to <NUM> % by weight based on the weight of (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer, and <NUM> to <NUM> % by weight of a polyethylene terephthalate resin based on the weight of (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer; and <NUM> to <NUM> parts by weight of a hydrolysis stabilizer prepared by mixing <NUM> to <NUM> % by weight of a polyorganosiloxane-polycarbonate resin based on <NUM> % by weight of a total of the hydrolysis stabilizer, <NUM> to <NUM> % by weight of a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer based on <NUM> % by weight of a total of the hydrolysis stabilizer, <NUM> to <NUM> % by weight of a dialkyl phthalate compound based on <NUM> % by weight of a total of the hydrolysis stabilizer and <NUM> to <NUM> % by weight of a carboxy-reactive epoxy resin based on <NUM> % by weight of a total of the hydrolysis stabilizer into an extruder, and melt-kneading and extruding the same.

In the melt-kneading step, for example, the aforementioned other additives may be included.

The melt-kneading and extruding step may be performed, for example, using one or more selected from a group consisting of a single-screw extruder, a twin-screw extruder, and a Banbury mixer, preferably using a twin-screw extruder. The melt-kneading and extruding step may be performed by uniformly mixing components using the extruder, and then conducting extrusion to obtain a composite resin composition in a pellet form. In this case, mechanical property deterioration and thermal property decrease are prevented and excellent plating adhesion and appearance quality are provided.

A step of preparing pellets using an extrusion kneader may be performed, for example, under conditions of an extrusion temperature of <NUM> to <NUM>, a flow ratio (F/R) of <NUM> to <NUM>/hr, and a screw rotation number of <NUM> to <NUM> rpm, preferably under conditions of an extrusion temperature of <NUM> to <NUM>, F/R of <NUM> to <NUM>/hr, and a screw rotation number of <NUM> to <NUM> rpm.

After extruding the composite resin composition, a step of injection-molding under conditions of an injection temperature of <NUM> to <NUM>, particularly <NUM> to <NUM>, a mold temperature of <NUM> to <NUM>, particularly <NUM> to <NUM>, and an injection rate of <NUM> to <NUM>/sec, particularly <NUM> to <NUM>/sec may be further performed.

Further, an automobile interior product including the composite resin composition of the present invention is described. In describing an automobile interior product including the composite resin composition of the present invention, all of the above particulars regarding the composite resin composition are included.

Since the composite resin composition of the present invention is sufficiently optimized due to use of the above components, the composite resin composition may be usefully used for an automobile interior product requiring moldability, mechanical properties, heat resistance under high load, and chemical resistance.

The automobile interior product may be manufactured by a method generally used in the art. For example, using a melted kneaded material or pellets of the composite resin composition according to the present invention or a sheet (a plate) molded using the melted kneaded material or pellets as a low material, an injection molding method, an injection compression molding method, an extrusion molding method, a sheet casting method, a press molding method, a pressure forming method, a heat bending method, a compression molding method, a calender molding method, a rotating molding method, or the like may be applied.

For example, the composite resin composition of the present disclosure may be prepared in the form of pellets by feeding a polycarbonate resin, a polybutylene terephthalate resin, a polyethylene terephthalate resin, a polyorganosiloxane-polycarbonate resin, a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer, a dialkyl phthalate compound, a carboxy-reactive epoxy resin and additives into a main inlet of a twin-screw extruder (φ40, L/D: <NUM>, SM Platek equipment), set to <NUM>, at <NUM> rpm and at a flow ratio of <NUM>/h and melt-kneading and extruding the same.

The pellets are fed into an injection molding machine to prepare an automobile interior product.

To indirectly confirm the physical properties of the automobile interior product, the pellets are injected at an injection temperature of <NUM>, a mold temperature of <NUM>, and an injection rate of <NUM>/sec using an injection molding machine (ENGEL, <NUM> tons), thereby manufacturing a specimen according to ISO standards.

The flow index (melt flow rate), measured at <NUM> under a load of <NUM> according to ISO <NUM>, of the manufactured specimen may be, for example, <NUM>/<NUM> or more, particularly, <NUM> to <NUM>/<NUM>.

In addition, the Izod notch impact strength, measured at <NUM> according to ISO <NUM>, of the specimen may be, for example, <NUM> kJ/m<NUM> or more, particularly <NUM> to <NUM> kJ/m<NUM>.

In addition, the tensile strength, measured at a speed of <NUM>/min according to ISO <NUM>, of the specimen may be, for example, <NUM> MPa or more, particularly <NUM> to <NUM> MPa.

In addition, the flexural strength, which is measured at a speed of <NUM>/min using SPAN <NUM> according to ISO <NUM>, of a <NUM> (<NUM>/<NUM> inch) specimen may be, for example, <NUM> MPa or more, particularly <NUM> to <NUM> MPa, and a flexural modulus of which may be <NUM> MPa or more, particularly <NUM> to <NUM> MPa.

In addition, the density, measured according to ISO <NUM>, of the specimen may be <NUM> to <NUM>/cm3, particularly <NUM> to <NUM>/cm3.

The automobile interior product may be particularly a floor console front tray, a cup holder, an inner garnish, a switch bezel, a cup holder housing, or an indicator panel, without being limited thereto.

That is, the composite resin composition according to an embodiment of the present invention includes a composite resin including a polycarbonate resin, a polybutylene terephthalate resin and a polyethylene terephthalate resin in specific % by weight; and a hydrolysis stabilizer prepared by mixing a polyorganosiloxane-polycarbonate resin, a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer, a dialkyl phthalate compound and a carboxy-reactive epoxy resin in specific % by weight, and an automobile interior product prepared using the composition exhibits improved heat resistance and hydrolysis resistance stability, thus satisfying the balance between physical properties such as mechanical properties and fluidity and improving product reliability and appearance quality.

In describing the composite resin composition of the present invention, the method of preparing the same, and an automobile interior product including the composite resin composition, other conditions or equipment not expressly described may be appropriately selected within a range commonly practiced in the art, and there is no particular limitation.

Hereinafter, embodiments of the present invention will be described in detail so that those of ordinary skill in the art can easily carry out the present invention. However, the present invention may be embodied in various different forms and is not limited to the embodiments described herein.

Raw materials used in examples are as follows.

Raw materials of summarized in Table <NUM> below were mixed to prepare a composite resin composition, and then the composite resin composition having uniform dispersion was manufactured in the form of pellets through extrusion. Next, the pellets were heated and injected into a mold, followed by cooling. The cooled pellets were manufactured into a specimen to be used as an automobile interior product in an injection process of producing components.

Specifically, ingredients summarized in Table <NUM> below were mixed using a mixer, and then were fed into at <NUM> rpm and at a flow ratio of <NUM>/ha into a main inlet of a twin-screw extruder (φ40, L/D: <NUM>, SM Platek equipment) set to <NUM>, followed by extrusion for <NUM> to <NUM> minutes. As a result, composite resin composition pellets were produced.

The produced pellets were dried in a <NUM> convection oven for <NUM> hours or more, and then were injected under conditions of an injection temperature of <NUM>, a mold temperature of <NUM>, and an injection rate of <NUM>/sec using an injection molding machine (ENGEL, <NUM> tons), thereby manufacturing an ISO specimen.

For reference, the total weight % of the raw materials A-<NUM> to I summarized in Table <NUM> is <NUM> % by weight.

The automobile interior product specimens manufactured according to Examples <NUM> to <NUM>, Comparative Examples <NUM> to <NUM>, and Reference Examples <NUM> and <NUM> were subjected to physical property evaluation. The evaluation criteria are as follows.

The results measured according to the evaluation criteria are summarized in Table <NUM> below.

Referring to Table <NUM>, it can be confirmed that the composite resin compositions of Examples <NUM> to <NUM> according to the present invention can realize a density within an appropriate range and have improved impact strength, flexural modulus, high-load heat deflection temperature, and hydrolysis-resistance retention rate, so that automobile interior products manufactured using the composite resin compositions basically satisfy physical properties such as impact strength, tensile strength, and flexural strength, exhibit excellent chemical resistance and high-load heat resistance, and provide product reliability and appearance quality due to decreased gas generation during injection molding.

In addition, it can be confirmed that in the case of Comparative Example <NUM> in which a polyethylene terephthalate resin having a melting point within an appropriate range is used in an excessive amount, a flexural modulus and a hydrolysis-resistance retention rate are deteriorated compared to Examples <NUM> to <NUM>.

In addition, it can be confirmed that in the case of Comparative Example <NUM> in which a (meth) acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer as a hydrolysis stabilizer is used in a content exceeding an appropriate range, similar hydrolysis-resistance retention rate is exhibited, but flexural modulus and high-load heat deflection temperature are poor, compared to Examples <NUM> to <NUM>.

In addition, it can be confirmed that in the case of Comparative Example <NUM> in which a polyorganosiloxane-polycarbonate resin that is one of hydrolysis stabilizers is not used, similar mechanical properties and heat resistance are exhibited, but the hydrolysis-resistance retention rate is significantly poor, compared to Examples <NUM> to <NUM>.

In addition, it can be confirmed that in the case of Comparative Example <NUM> to <NUM> in which the hydrolysis stabilizers are not appropriately mixed, the hydrolysis-resistance retention rate is significantly deteriorated, and the appearance quality of the injection-molded articles is decreased, compared to Examples <NUM> to <NUM>.

Further, it can be confirmed that in the case of Reference Example <NUM> in which the melting point of the polyethylene terephthalate resin is inappropriate, the flow index is significantly poor, compared to Examples <NUM> to <NUM>.

In addition, it can be confirmed that in the case of Reference Example <NUM> in which the intrinsic viscosity of the polybutylene terephthalate resin is inappropriate, the flow index and the heat deflection temperature under high load are poor, compared to Examples <NUM> to <NUM>.

ISO specimens were manufactured in the same manner as in Example <NUM> described above except that raw materials for the composite resin composition were mixed as summarized in Table <NUM> below.

The physical properties of the automobile interior product specimens manufactured according to Comparative Examples <NUM> to <NUM> were evaluated as described above. The measurement results for evaluation are summarized in Table <NUM> below.

Referring to Tables <NUM> and <NUM>, it can be confirmed that in the case of Comparative Examples <NUM> and <NUM> using a low-flow polycarbonate resin, fluidity and a heat deflection temperature under high load are significantly poor, compared to Examples <NUM> to <NUM>.

In addition, it can be confirmed that in the case of Comparative Example <NUM> in which a polycarbonate resin having a flow index outside an appropriate range is used, mechanical properties such as a flexural modulus are deteriorated, compared to Examples <NUM> to <NUM>.

In addition, it can be confirmed that in the case of Comparative Example <NUM> in which the content of the hydrolysis stabilizer is less than an appropriate range, impact strength is significantly decreased, compared to Examples <NUM> to <NUM>.

Further, it can be confirmed that in the case of Comparative Example <NUM> in which the content of the hydrolysis stabilizer exceeds an appropriate range, fluidity is significantly deteriorated, and overall physical properties such as a tensile strength, a flexural strength, flexural modulus, a heat deformation temperature, and a density are poor, compared to Examples <NUM> to <NUM>.

Claim 1:
A composite resin composition, comprising:
<NUM> parts by weight of the composite resin comprising <NUM> to <NUM> % by weight of a polycarbonate resin based on <NUM> % by weight of a total of the composite resin, <NUM> to <NUM> % by weight of a polybutylene terephthalate resin based on <NUM> % by weight of a total of the composite resin and <NUM> to <NUM> % by weight of a polyethylene terephthalate resin based on <NUM> % by weight of a total of the composite resin; and
<NUM> to <NUM> parts by weight of a hydrolysis stabilizer prepared by mixing <NUM> to <NUM> % by weight of a polyorganosiloxane-polycarbonate resin based on <NUM> % by weight of a total of the hydrolysis stabilizer, <NUM> to <NUM> % by weight of a (meth)acrylate compound-conjugated diene compound-aromatic vinyl compound copolymer based on <NUM> % by weight of a total of the hydrolysis stabilizer, <NUM> to <NUM> % by weight of a dialkyl phthalate compound based on <NUM> % by weight of a total of the hydrolysis stabilizer and <NUM> to <NUM> % by weight of a carboxy-reactive epoxy resin based on <NUM> % by weight of a total of the hydrolysis stabilizer.