Patent Description:
Hot melt adhesives have been widely used in disposable articles like baby diapers and feminine napkins, which comprise multiple layers such as a PE film, a hydrophobic non-woven layer, a hydrophilic non-woven layer, stretchable TPU film, tissue, cotton and the like. The layers are bonded together with the hot melt adhesive. Disposable articles usually comprise a core part for absorbing body fluids, and the core part often is composed of hydrophilic substrates as a wrapping material, and inside which is fluff and super absorbent polymer (SAP). The core part is usually soaked in body fluids and thus the adhesive used in the core part requires a high bonding strength under both dry and wet conditions. Otherwise, delamination of the layers will lead to leakage of body fluids, causing product quality issues. Therefore, a high wet peel strength for the hot melt adhesive used here is very important.

Typically, hot melt adhesives can be based on polymers such like functionalized or non-functionalized polyolefins, or styrenic block copolymers such as styrene-isoprene-styrene (SIS) or styrene-butadienestyrene (SBS) polymers.

In the past, many different olefinic polymers have been used in the hot melt adhesives for disposable articles. One important kind of the olefinic polymers is amorphous polyolefins (APO), such as amorphous polypropylene (APP). Later, polymers having much improved properties over the original APO polymers became available, such as amorphous poly alpha olefins (APAO).

<CIT> discloses a low application temperature hot melt adhesive comprising a polyolefin copolymer component and a maleated polyethylene wax component. The polyolefin copolymer component comprises two different polyolefin copolymers wherein at least one polyolefin copolymer is a metallocene-catalyzed ethylene/α-olefin copolymer prepared from ethylene and <NUM>-octene monomers, which copolymer that has a Melt Index of greater than about <NUM>/<NUM> at <NUM>. The adhesive has a viscosity at <NUM> of below about <NUM> centipoises.

<CIT> discloses a hot melt adhesive comprising: (A) a metallocene based propylene homopolymer; (B) a metallocene based ethylene/α-olefin copolymer; (C) a tackifier resin, and (D) a plasticizer, wherein the plasticizer (D) comprises (D1) an oil and (D2) at least one polymer selected from polybutene, polybutadiene, polyisobutylene, and polyisoprene.

Traditional APOs are homopolymers or copolymers of ethylene, propene, butene, monoene with longer aliphatic chains. In this case, physical performances like green strength, elasticity, resistance to elevated temperature of APO are not that good, because the molecular structure of APOs is quite random.

Spray uniformity is another concern for the hot melt adhesive used in the disposable articles. For application, the adhesive is firstly heated to become liquid, and then spray coated or slot coated onto substrates. The spray nozzle can be designed into specific shapes to create different spray patterns including summit, signature, spiral, curtain, omega etc. The spray process requires the hot melt adhesive to be featured with excellent spray uniformity. Traditional polyolefin has poor spray uniformity, which means the spray pattern is not even or regular as what it should be like. Uniform spray pattern is very important for creating suitable bonding effects, sometimes bad spray patterns will lead to bonding failure and cause serious issues.

The hot melt adhesives used in the disposable articles are desired to have a wide application window. The term 'application window' means various application conditions in which hot melt adhesives are used well in manufacturing lines. For disposable articles, the application window refers to the conditions including spray temperature, air pressure, spray pattern, open time, setting time, green strength etc. It is very important for hot melt adhesives to have a broad application window to meet all the above requirements, in order to reduce machine downtime and scrap as well as to make adhesive suitable for various working conditions. For example, on a manufacturing line of baby diapers, the hot melt adhesive is spray coated from the nozzle onto the first substrate, then the substrate moves forward for <NUM> meters on the conveyor, requiring <NUM> seconds as the open time for bonding of this position. The hot melt adhesive should remain tacky within the open time and therefore after <NUM> seconds it is still able to bond to the second substrate. Meanwhile, the hot melt adhesive should have excellent green strength so that in some working positions the adhesive can have instant bonding effect after lamination and therefore no misposition would take place. Modern high-speed manufacturing lines of disposable articles run at a speed up to <NUM>-<NUM> meters per minute, once the hot melt adhesive does not fall in the application window, it is very likely that the bonding performance of hot melt adhesive cannot meet the requirement of continuous production. For disposable hygiene applications, traditional APO-based hot melt adhesives cannot meet one or more of these requirements.

Therefore, it still needs to improve the application performance of the hot melt adhesives used for disposable articles.

To solve the above-mention problems, an object of the present invention is to provide a hot melt adhesive composition having one or more properties of good green strength, good odor, good wet bonding strength, and good spray uniformity, preferably having all the above properties.

After intensive studies, the inventors have found that the above problems may be solved with a hot melt adhesive composition as defined in claim <NUM> appended hereto and which comprises: (A) an olefin block copolymer of ethylene and octene having a melt index of <NUM> to <NUM>/<NUM> @ <NUM>, <NUM>, preferably <NUM> to <NUM>/<NUM> @ <NUM>, <NUM>; and, (B) a wax modified with carboxylic acid and/or carboxylic acid anhydride.

In the present invention, the wax (B) preferably is a polyolefin wax modified with maleic acid and/or maleic acid anhydride.

In the present invention, the wax (B) preferably is a polypropylene wax modified with maleic acid and/or maleic acid anhydride, or a polyethylene wax modified with maleic acid and/or maleic acid anhydride.

In the present invention, the wax (B) preferably has an acid number of no less than <NUM> KOH/g, preferably no less than <NUM> KOH/g.

The advantages of the hot melt adhesive composition include that:.

It is to be understood by one of ordinary skill in the art that the present invention is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention. Each aspect so described may be combined with any other aspect or aspects unless clearly indicated to the contrary. In particular, any feature indicated as being preferred or advantageous may be combined with any other feature or features indicated as being preferred or advantageous.

Unless specified otherwise, in the context of the present invention, the terms used are to be construed in accordance with the following definitions.

Unless specified otherwise, all wt% or % by weight values quoted herein are percentages by weight based on total weight of the cyanoacrylate adhesive composition.

Unless specified otherwise, as used herein, the terms "a", "an" and "the" include both singular and plural referents.

The terms "comprising" and "comprises" as used herein are synonymous with "including", "includes" or "containing", "contains", and are inclusive or open-ended and do not exclude additional, non-recited members, elements or process steps.

Unless specified otherwise, the recitation of numerical end points includes all numbers and fractions subsumed within the respective ranges, as well as the recited end points.

Unless otherwise defined, all terms used in the present invention, including technical and scientific terms, have the meaning as commonly understood by one of the ordinary skilled in the art to which this invention belongs.

According to the present invention, the hot melt adhesive composition comprises: (A) an olefin block copolymer of ethylene and octene, having a melt index of <NUM> to <NUM>/<NUM> @ <NUM>, <NUM>, preferably <NUM> to <NUM>/<NUM> @ <NUM>, <NUM>, and (B) a wax modified with carboxylic acid and/or carboxylic acid anhydride.

An important component used in a hot melt adhesive formula according to the present invention is an olefin block copolymer (OBC).

OBCs are relatively new but known in the art. OBCs belong to a new class of polyolefin polymers produced using a chain shuttling catalysis technology that produces a linear block structure of the monomers rather than a random polymer produced by Ziegler-Natta or traditional metallocene technology. At present, they are mainly manufactured by Dow Chemical under the trade name of Infuse®. The OBCs consist of crystallizable ethylene-octene blocks (hard) with very low comonomer content and high melting point alternating with amorphous ethylene-octene blocks (soft) with high comonomer content and low glass transition temperature. This gives the polymer much better elevated temperature resistance and elasticity compared to a typical metallocene random polymer of similar density. Details of these polymers and their synthesis and physical properties can be found in, for example, <CIT>, <CIT>, <CIT>, <CIT> and <CIT>, the disclosures of which are specifically incorporated herein by reference.

Specifically, the OBCs useful in the present invention comprise polymerized units of ethylene and octene, wherein the OBCs are characterized by an average block index greater than zero and up to about <NUM> and a molecular weight distribution, Mw/Mn, greater than about <NUM>. Preferably, the OBCs useful in the present invention comprise polymerized units of ethylene and octene, wherein the average block index is greater than <NUM> but less than about <NUM> and a molecular weight distribution, Mw/Mn, greater than about <NUM>. More preferably, the OBCs useful in the present invention are linear, multi-block copolymers with at least three blocks. More preferably, the ethylene content in the OBCs useful in the present invention is at least <NUM> mole percent.

In some embodiments, the average block index of the OBCs useful in the present invention is in the range from about <NUM> to about <NUM>, from about <NUM> to about <NUM>, from about <NUM> to about <NUM>, from about <NUM> to about <NUM>, or from about <NUM> to about <NUM>. In other embodiments, the OBCs have a density of less than about <NUM>/cc, such as from about <NUM>/cc to about <NUM>/cc. In other embodiments, the molecular weight distribution, Mw/Mn, is greater than about <NUM> or greater than about <NUM>. It can also range from about <NUM> to about <NUM> or from about <NUM> to about <NUM>.

Preferably, the OBCs useful in the present invention comprise at least one fraction obtained by Temperature Rising Elution Fractionation ("TREF"), wherein the fraction has a block index greater than about <NUM> and up to about <NUM>, and the OBCs useful in the present invention have a molecular weight distribution, Mw/Mn, greater than about <NUM>. Preferably, the OBCs useful in the present invention comprise polymerized units of ethylene and octene, the OBCs are characterized by having at least one fraction obtained by TREF, wherein the fraction has a block index greater than about <NUM> and up to about <NUM> and the OBCs have a molecular weight distribution, Mw/Mn, greater than about <NUM>. In some embodiments, the block index of the fraction is greater than about <NUM>, greater than about <NUM>, greater than about <NUM>, greater than about <NUM>, greater than about <NUM>, or greater than about <NUM>.

The term "block index" used herein has the same meaning as defined in <CIT>.

Preferably, the OBCs useful in the present invention comprise one or more hard segments and one or more soft segments. Preferably, the hard segments comprise at least <NUM>% of ethylene by weight. , and the soft segments comprise less than <NUM>%, preferably less than <NUM>%, of ethylene by weight. In some embodiments, the hard segments are present in an amount from about <NUM>% to about <NUM>% by weight of the OBC. In other embodiments, the OBC comprises at least <NUM> or at least <NUM> hard and soft segments connected in a linear fashion to form a linear chain. Preferably, the hard segments and soft segments are randomly distributed along the chain. In some embodiments, neither the soft segments nor the hard segments include a tip segment (which is different by chemical composition than the rest of the segments).

Olefin block copolymers should not be considered as amorphous poly-alpha-olefins because the polymer architecture is completely different (i.e. block vs. random) and is specifically produced to have crystalline regions. In addition, OBCs are significantly narrower in polydispersity than other traditionally used olefins, for example APAOs, which impacts their melt profiles as measured by DSC (Differential Scanning Calorimetry).

Olefin block copolymers (OBCs) are polyolefins with alternating blocks of hard (highly rigid) and soft (highly elastomeric) segments. The block structure of OBCs offers an advantaged performance balance of flexibility and sprayability compared to random polyolefin copolymers. OBCs useful in the present invention can be commercially available from Dow Chemical Company under the tradenames Infuse® <NUM>, Infuse® <NUM> and Infuse® <NUM>.

Olefin block copolymers of ethylene and octene useful in the present hot melt adhesive composition preferably are olefin block copolymers of ethylene and <NUM>-octene, more preferably have a melt index in the range of <NUM> to <NUM>/<NUM> @ <NUM>, <NUM>, preferably <NUM> to <NUM>/<NUM> @ <NUM>, <NUM>, as measured according to ASTM D1238, such as <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>/<NUM> @ <NUM>, <NUM>, as determined according to ASTM D1238. A melt index outside the above range may lead to unsatisfactory effect.

Preferably, olefin block copolymers of ethylene and octene useful in the present hot melt adhesive composition have a melting point in the range of <NUM> to <NUM>, preferably, of <NUM> to <NUM>, such as <NUM>, <NUM> and <NUM>, as determined by differential scanning calorimetry (DSC).

One or more olefin block copolymers of ethylene and octene are incorporated into the adhesive composition in an amount of from <NUM>% to <NUM>% by weight, preferably from <NUM>% to about <NUM>% by weight, such as <NUM>%, <NUM>%, <NUM>%, <NUM>%, <NUM>%, <NUM>%, <NUM>% by weight, each based on the total weight of the adhesive composition.

The wax (B) used in the present invention is not particularly limited, as long as it is modified with carboxylic acid and/or carboxylic acid anhydride and the objective hot melt adhesive of the present invention can be obtained.

The carboxylic acid and/or carboxylic acid anhydride functional groups can be introduced in the wax (B) via various reactions.

The "base wax" useful in the present invention is not particularly limited as long as it is a wax to be commonly used in a hot melt adhesive and the objective hot melt adhesive of the present invention can be obtained. Specific examples thereof include synthetic waxes such as a polyolefin wax (polyethylene wax, polypropylene wax); petroleum waxes such as a paraffin wax and a microcrystalline wax; and natural waxes such as a castor wax.

The carboxylic acid and/or carboxylic acid anhydride to be used to modify the base wax is/are not particularly limited as long as the objective hot melt adhesive of the present invention can be obtained. Specific examples thereof include maleic acid, maleic acid anhydride, fumaric acid, succinic acid, succinic acid anhydride, phthalic acid, phthalic acid anhydride, glutaric acid, glutaric acid anhydride, itaconic acid, acrylic acid, methacrylic acid and the like. These carboxylic acids and/or carboxylic acid anhydrides may be used alone, or in combination. In the present invention, maleic acid and/or maleic acid anhydride is/are particularly preferable.

In order to modify the base wax, it is possible to use various carboxylic acid derivatives which can introduce polar groups (i.e., carboxylic acid group and/or carboxylic acid anhydride group). Herein, "carboxylic acid derivatives" include:.

The wax modified with carboxylic acid and/or carboxylic acid anhydride of the present invention is preferably a polyolefin wax modified with maleic acid and/or maleic acid anhydride, and particularly preferably a polypropylene wax modified with maleic acid anhydride or a polyethylene wax modified with maleic acid anhydride.

As (B) the wax modified with carboxylic acid and/or carboxylic acid anhydride, it is possible to use commercially available products in the present invention. Examples thereof include Licocene® PPMA <NUM> and PPMA <NUM> available from Clariant; A-C 575P and A-C 597P available from Honeywell.

Preferably, the wax modified with carboxylic acid and/or carboxylic acid anhydride of the present invention (B) useful in the present invention has an acid number of no less than <NUM> KOH/g, preferably no less than <NUM> KOH/g, such as <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM> KOH/g, as determined according to DIN EN ISO <NUM>.

Preferably, the wax modified with carboxylic acid and/or carboxylic acid anhydride of the present invention (B) useful in the present invention has a softening point in the range of <NUM> to <NUM>, preferably in the range of <NUM> to <NUM>, such as <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, as determined according to ASTM D <NUM>.

The hot melt adhesives of the present invention may comprise one or more waxes modified with carboxylic acid and/or carboxylic acid anhydride.

In the present invention, the blending amount of the wax (B) is preferably from <NUM> to <NUM> % by weight, preferably <NUM> to <NUM> % by weight, such as <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM> % by weight, each based on the total weight of the adhesive. By blending the wax (B) in the above amount, the obtained hot melt adhesive has little odor while providing wet adhesion.

In addition to the above component (A) and component (B), the adhesive composition of the present invention may further comprise (C) a tackifier (also called as tackifying resin).

The tackifier (C) is preferably blended in the amount within a range from <NUM> to <NUM> % by weight, more preferably from <NUM> to <NUM> % by weight, such as <NUM>% by weight, <NUM>% by weight, <NUM>% by weight, each based on the total weight of the adhesive composition.

Any tackifying resins that are compatible in the formulation may be blended. Examples of the tackifier (C) include a natural rosin, a modified rosin, a hydrogenated rosin, a glycerol ester of a natural rosin, a glycerol ester of a modified rosin, a pentaerythritol ester of a natural rosin, a pentaerythritol ester of a modified rosin, a pentaerythritol ester of a hydrogenated rosin, a copolymer of a natural terpene, a terpolymer of a natural terpene, hydrogenated derivatives of a copolymer of a hydrogenated terpene, a polyterpene resin, hydrogenated derivatives of a phenol-based modified terpene resin, an aliphatic petroleum hydrocarbon resin, hydrogenated derivatives of an aliphatic petroleum hydrocarbon resin, an aromatic petroleum hydrocarbon resin, hydrogenated derivatives of an aromatic petroleum hydrocarbon resin, a cyclic aliphatic petroleum hydrocarbon resin, and hydrogenated derivatives of a cyclic aliphatic petroleum hydrocarbon resin. Synthetic aliphatic tackifiers are more preferred. More particularly, fully hydrogenated aliphatic tackifiers are even more preferred. Hydrogenated aliphatic C5 or dicyclopentadiene (DCPD) resins are fully compatible with SEBS and Polyolefin. These tackifiers can be used alone, or in combination. It is also possible to use a liquid type tackifier as long as it has a colorless to pale yellow color tone and substantially no odor, and also has satisfactory thermal stability. Taking these properties into consideration comprehensively, the tackifier is preferably hydrogenated derivatives of resins, and particularly preferably a hydrogenated dicyclopentadiene-based resin. Preferably, the tackifiers possess a Ring & Ball softening point of from <NUM> to <NUM>.

It is possible to use commercially available products as the tackifier (C). Examples of these commercially available products include C100R / C100W / H130R / H130W from Eastman, H5-<NUM> / <NUM> from Henghe China, SU <NUM> / <NUM> / <NUM> /<NUM> from Kolon, I-Marv P90 / P100 / P120 from Arakawa, Regalite R1100 / R1120 / S1100 from Eastman, Escorez <NUM> / <NUM> from Exxon, HA <NUM> from Tonen, HD <NUM> / <NUM> from Luhua, PRS-<NUM> / <NUM> from Ruisen, JH-<NUM> / <NUM> from Jin-hai. These commercially available tackifier resins can be used alone, or in combination.

The hot melt adhesive of the present invention can further include oil (D). The oil (D) is blended as a plasticizer for the purpose of decrease in melt viscosity and Tg of the hot melt adhesive, imparting of flexibility and improvement in wettability to an adherend. Examples of the oil (D) include mineral oils like paraffin oil, naphthene oil and aromatic oil, and colorless and odorless oils such as naphthene oil and paraffin oil are particularly preferable.

It is possible to use commercially available products as the oil (D). Examples thereof include KN <NUM>, KN <NUM>, KN <NUM> from Lubricant Company of PetroChina; white mineral oil LP <NUM>, LP <NUM> from Kukdong Korea; Nyflex 222B from Nynas; PS white mineral oil from PetroChina. These oils (D) can be used alone, or in combination.

If present, the oil (D) is preferably blended in the amount within a range from <NUM> to <NUM> % by weight, more preferably from <NUM> to <NUM> % by weight, such as <NUM>% by weight, <NUM>% by weight, <NUM>% by weight, <NUM>% by weight, each based on the total weight of the adhesive composition.

The hot melt adhesive of the present invention can further include stabilizer (E). The "stabilizer" is blended so as to improve stability of the hot melt adhesive by preventing decrease in molecular weight, gelation, coloration, and generation of odor of the hot melt adhesive due to heat, and there is no particular limitation on the stabilizer as long as the objective hot melt adhesive of the present invention can be obtained. In the present invention, the term "stabilizer" cover antioxidants and ultraviolet absorbers. The "ultraviolet absorber" is used so as to improve light resistance of the hot melt adhesive. The "antioxidant" is used so as to prevent oxidation degradation of the hot melt adhesive. The antioxidant and ultraviolet absorber are commonly used in the hot melt adhesive for disposable products and can be used without particular limitation as long as the objective disposable products can be obtained.

Examples of the antioxidant include a phenol-based antioxidant, a sulfur-based antioxidant and a phosphorus-based antioxidant. Examples of the ultraviolet absorber include a benzotriazole-based ultraviolet absorber and a benzophenone-based ultraviolet absorber. It is also possible to add a lactone-based stabilizer. These stabilizers can be used alone, or in combination.

It is possible to use commercially available products as the stabilizer. Examples thereof include Evernox 10GF / <NUM> from Everspring, Irganox <NUM>/ <NUM> from BASF, Thanox <NUM> / <NUM> from Rianlon; Commercial grades of phosphite include Everfos <NUM> from Everspring, Irgafos <NUM> from BASF, Thanox <NUM> from Rianlon; Commercial grades of thiodipropionate include Thanox <NUM> / DSTP from Rianlon, ADK AO <NUM> from Adeka, Sumilizer TP-D from Sumimoto. These stabilizers can be used alone, or in combination.

The stabilizer (E) can be contained in the adhesive composition of the present invention in an amount of less than <NUM> wt%, preferably less than <NUM> wt%, more preferably less than <NUM> wt%, such as about <NUM> wt%.

The hot melt adhesive composition of the present invention can further include a filler, especially a fine particle filler. Commonly used fine particle filler may be used, and there is no particular limitation as long as the objective hot melt adhesive of the present invention can be obtained. Examples of the "fine particle filler" include mica, calcium carbonate, kaolin, talc, titanium oxide, diatomaceous earth, urea-based resin, styrene beads, calcined clay, starch and the like. These particles preferably have a spherical shape, and there is no particular limitation on the size (diameter in case of a spherical shape).

The hot melt adhesive composition of the present invention can further include other additives commonly used in the art, such as pigments, dyes, rheology modifiers, and so on.

The hot melt adhesive of the present invention can be produced by blending the components (A) and (B) and other optional components, melting the mixture under high temperature e.g. above <NUM>, followed by mixing or homogenizing to form an uniform mixture. Any feasible blending methods or equipments that are known in the art can be adopted to prepare a homogeneous adhesive mixture.

The hot melt adhesive according to the present invention preferably has a melt viscosity at <NUM> from <NUM>,<NUM> to <NUM>,<NUM> mPa. s , and particularly preferably from <NUM>,<NUM> to <NUM>,<NUM> mPa. The "melt viscosity" is viscosity of the hot melt adhesive which is molten, and is measured by a Brookfield RVT-type viscometer (spindle No. <NUM>).

As mentioned above, the hot melt adhesive according to the present invention can be employed in disposable products since it is excellent in adhesion in a wet state. The disposable products can be constituted by coating at least one kind of member selected from a group consisting of a woven fabric, a nonwoven fabric, a rubber, a resin, papers and a polyolefin film with the hot melt adhesive according to the present invention. The polyolefin film is preferably a polyethylene film for the reason of durability, costs and the like.

There is no particular limitation on the disposable products as long as they are so-called sanitary materials. Specific examples thereof include a disposable diaper, a sanitary napkin, a bed pad, a bandage, a surgical drape, a pet sheet, a hospital gown, a surgical white garment and the like.

In the production line of the disposable products, various members (for example, tissue, cotton, nonwoven fabric, polyolefin film, etc.) of the disposable products are commonly coated with the hot melt adhesive. In case of coating, the hot melt adhesive may be discharged (or ejected) from various dischargers (or ejectors).

There is no particular limitation on the method of coating with the hot melt adhesive as long as the objective disposable products can be obtained. Such a coating method is roughly classified into a contact coating method and a non-contact coating method. The "contact coating" method refers to a coating method in which a discharger is brought into contact with a member or a film in case of coating with the hot melt adhesive, while the "non-contact coating" method refers to a coating method in which a discharger is not brought into contact with a member or a film in case of coating with the hot melt adhesive. Examples of the contact coating method include a slot coater coating method, a roll coater coating method and the like, and examples of the non-contact coating method include a spiral coating capable of coating in a spiral form, an omega coating or control seam coating method capable of coating in a wavy form, a slot spray coating or curtain spray coating method capable of coating in a plane form, and dot coating capable of coating in a dot form.

In another aspect of the present invention, provided is a laminate, comprising a first substrate, a second substrate, and an adhesive layer sandwiched therebetween, wherein the first and second substrates are independently of each other selected from a woven fabric, a nonwoven fabric, a rubber, a resin, papers and a polyolefin film, and the adhesive layer is formed by the hot melt adhesive composition according to the present invention.

In yet another aspect of the present invention, provided is a disposable article comprising the laminate of the present invention or produced using the hot melt adhesive of the present invention.

The following examples are intended to assist one skilled in the art to better understand and practice the present invention. The scope of the invention is not limited by the examples but is defined in the appended claims. All parts and percentages are based on weight unless otherwise stated.

The soften point of the hot melt adhesive composition was determined according to ASTM D <NUM>.

The odor score of the hot melt adhesive composition was determined by the steps of:.

An odor score of greater than <NUM> is considered as unacceptable during use.

<NUM>-micron thickness adhesive were coated on a 50micron PET film with a film coater (laminated with a release film). Let it dwell at room temperature for <NUM>, then cut it into a <NUM> inch width and <NUM> inch length, hot pressed the adhesive film onto another 50micron PET film at <NUM>, pressure was <NUM>. 5MPa, pressing time was <NUM>. Then took the sample to the tensile tester to test the peel strength immediately. The test was started within <NUM> after hot pressing. The tensile test was done in the environment of <NUM> with an environmental box.

The hot melt adhesive was molten at <NUM>, and summit sprayed onto a substrate, the spray pattern was observed visually, and an uniform summit pattern was assigned as good, a nonuniform summit pattern was assigned as bad.

A PE sheet (Air permeable cast film with a thickness of <NUM> gsm from Foshan Landi) and a tissue (cellulose tissue with a thickness of <NUM> gsm from Zhongzhi) were adhered together to form a laminate sample by applying the hot melt adhesive between the two sheets via Summit nozzle head. The PE sheet and the tissue were peeled from one another at an angle of <NUM>° and with a rate of <NUM>/min using Instron <NUM> tensile strength tester (for wet peel, additionally soak the sample in water for 3mins and then take it out to test). The T peel test was carried out at <NUM> and <NUM>% relative humidity. The T peel test was made to the laminate sample at least <NUM> hours after the hot melt adhesive was applied. The PE sheet and the tissue were pulled <NUM> apart and the force was recorded as the T peel strength of the hot melt adhesive for PE and tissue.

As for the Cotton NW, the same procedure was conducted to determine the dry and wet peel strengths.

Adhesives were prepared with conventional method in the art using components in amounts (parts by weight) listed in the Table <NUM>, and the properties were tested using the methods stated above, and the results of evaluations are shown in Table <NUM>.

As can be seen from Table <NUM>, the adhesives of the present invention (Ex. <NUM> to <NUM>) showed good green strength, good odor, good wet bonding strength and good spray uniformity.

Claim 1:
A hot melt adhesive composition, comprising:
(A) <NUM>% to <NUM>% by weight, based on the total weight of the adhesive composition, of an olefin block copolymer of ethylene and octene, having a melt index of <NUM> to <NUM>/<NUM> @ <NUM>, <NUM>, preferably <NUM> to <NUM>/<NUM> @ <NUM>, <NUM>, and
(B) a wax modified with carboxylic acid and/or carboxylic acid anhydride,
wherein the composition has a melt viscosity at <NUM> from <NUM>,<NUM> to <NUM> mPa.s, as determined using a Brookfield RVT-type viscometer (Spindle No. <NUM>).