Patent Description:
Dendritic molecules or highly branched molecules such as dendrimers are a class of well-defined nanostructured macromolecules with narrow polydispersity or even monodispersity, and a multivalent surface amenable for further modifications, Dendrimers are extensively and continually investigated for biomedical applications such as gene therapy, drug delivery and bioimaging purposes. Dendrimers are versatile which allows conjugation, complexation, and/or encapsulation of multifunctional moieties. Functional groups may be arranged on the periphery of dendrimer acting as highly accessible handles for drug or other functional group attachments. Since the functionalities of the drugs and ligands are diverse, there is a need to explore various functional group presentations at the dendrimer surface. By using different functional moieties (drugs or imaging agents) onto a single dendrimer in a control way is difficult because all the peripheral groups of the symmetric dendrimer have the same reactivity. A suitable linker or spacer is required to react with the surface functionality of dendrimer, providing the flexibility to link multiple moieties such as drugs, imaging or targeting agents.

In the prior art it is well known the use of dendritic molecules/dendrimers as carriers for drug delivery. It is also known that low molecular weight peptide could be attached to a dendrimer in order to be carried to a specific target. Different type of "raw materials" can be used to produce a dendritic structure and several "strategies" can be used to attach or encapsulate peptides and polypeptides.

The use of functional dendritic structures based on aliphatic polyester building blocks to increase the efficiency of Antimicrobial peptides AMPs (Feliu et al. <NUM>), have a huge potential since they are commercially available, biocompatible, highly homogenous and can efficiently be tailored in terms of composition, hydrophilicity, size and geometry to efficiently encapsulate peptides with various properties.

Most biomedical applications of dendrimers have so far been focused on delivery of small molecular drugs, mainly directed towards oncological applications, such as delivery of the antracyline antibiotic doxorubicin used in breast cancer treatment, using the positively charged poly(amidoamine) PAMAM class of dendrimer. The commercial availability of dendrimers is currently increasing as a consequence of their potential as therapeutic vehicles in the field of nanomedicine (Rolland et al. To date, hyperbranched polymers have solely been commercially exploited in industrial large scale applications. For instance, hyperbranched BoltornTM based on <NUM>,<NUM>-bis(methylol) propionic acid (bis-MPA) facilitate the production of polyurethane car seats worldwide (Perstorp AB).

From the array of dendritic materials found in literature, the non-toxic and biocompatible bis-MPA based dendrimer belongs to one of the most promising scaffolds for biological applications (Feliu et al. <NUM>, Carlmark et.

Resistance to traditional antibiotics is a rapidly increasing problem that in a few years could make infections impossible to treat and bring the state of medical care back to the pre-antibiotic era from the beginning of the last century. Antimicrobial peptides (AMPs) have a huge potential as new therapeutics against infectious diseases as they are less prone to induce resistance due to their fast and non-specific mechanism of action. Functional delivery systems that can be applied directly on the infected site will be developed for treatment of infections in skin and burn wounds, as well as lung infections caused by Methicillin-resistant Staphylococcus aureus (MRSA), Pseudomonas aeruginosa and Mycobacterium tuberculosis (MTB).

Although large efforts in research and development have been directed towards the area of AMPs, only a few candidates have reached later stages of clinical trials and to date no or only few product based on AMPs has reached the market (Pasupuleti et al. One of the main reasons is the challenges related to stability of peptides in the formulations and after administration, which leads to reduced efficiency (Eckert <NUM>). Proteolytic degradation and self-aggregation are typical problems observed with these compounds. In order to increase efficiency and stability, various approaches to modify the peptide structure have been employed. However, these challenges can be overcome by choosing novel formulation strategies. With this respect, nanotechnology offers a wide range of unexplored possibilities.

The unique properties of biodegradable, nanostructured materials, including large surface areas, smart size ranges that enables transport across physiological barriers, ease of engineering and functionalization, possibility for targeting to different organs as well as high loading capacity of actives and various approaches to control the release kinetics, have led to a significant increase in the interest of using nanoparticles in various drug delivery applications.

The patent application <CIT>) provides a biocompatible nanosized hydrogel particles suitable for injectable delivery of therapeutic agents for treatment of diseases or disease states and also for bioimaging purposes. These nanoparticles, including crosslinked hydrogels of the modified asymmetric PAMAM dendrimers and other polymers, are biodegradable and release the therapeutic agent over an extended period of time. It is also disclosed an injectable hydrogel comprising: a crosslinked poly(amidoamine) dendrimer having at least two asymmetrical orthogonal chemoselective peripheral ends, at least one of said asymmetrical orthogonal ends being crosslinked to form a gel and at least one other of said asymmetrical orthogonal ends being conjugated to a chemical agent. Said patent application describes that the drug contained within the hydrogel can be a peptide and, in addition, it is described that hydrogels can be used for many different applications such as molecularly engineered scaffolds for controlled drug release, cellular delivery, tissue engineering and as wound dressings. However, PAMAM is not biocompatible and the degradation products are potentially toxic.

The patent application <CIT>) discloses a dendrimer molecule comprising surface carboxylic acid groups. Said application discloses a therapeutic-loaded polymer that is covalently attached to a low molecular weight peptide. The polymer can be usefully derivatized. It is claimed a method of preparing a modified dendrimer comprising the step of obtaining a dendrimer molecule comprising surface carboxylic acid groups. This patent application also discloses that the recognition moiety is selected from the group consisting of (i) a peptide comprising one or more hapten moieties; (ii) folic acid; (iii) a targeting peptide; (iv) biotin; (v) an oligonucleotide; (vi) an anchoring domain peptide; (vii) an antibody; and (viii) an antibody fragment.

The patent application <CIT>) discloses the use of polypeptides to be used for the prevention and treatment of infections. However, it does not disclose an efficient way of delivering said polypeptides.

The patent application <CIT>) discloses a delivery system emulsion-based wherein the emulsion comprises carbohydrate nanoparticles and bacteriocin are adsorbed on the nanoparticles surfaces. Said system is made of a nanoparticle comprising a carbohydrate carrier and a bacteriocin, wherein the bacteriocin comprises a peptide. In some embodiments this patent application describes an amphiphilic carbohydrate nanoparticle, phytoglycogen octenyl succinate (PG- OS), and used PG-OS-stabilized emulsion to deliver functional peptides with prolonged efficacy. The terms "phytoglycogen or glycogen-type material" refer to dendritic (i.e., highly branched) a-D-glucan and carbohydrate nanoparticles. In other embodiments, the nanocarriers used are negatively charged, phytoglycogen-based dendritic polysaccharides that adsorb positively charged nisin molecules via electrostatic interactions.

Patent application <CIT> discloses a nanocarrier having a hydrophobic core and a hydrophilic exterior, which is a micelle resulting from aggregation of the dendrimer conjugates, like a boronate-catechol cross-linked nanoparticles comprising a compound of formula I: (PEG)mA(Y1)p-L-D(Y2)q-(R)n (I) wherein A is linked to at least one PEG group; D is a dendritic polymer having a single focal point group, a plurality of branched monomer units X and a plurality of end groups; L is a bond or a linker linked to the focal point group of the dendritic polymer; each PEG is a polyethyleneglycol (PEG) polymer, wherein each PEG polymer has a molecular weight of <NUM> -<NUM> kDa; each R is independently selected from the group consisting of the end group of the dendritic polymer, a hydrophobic group, a hydrophilic group, an amphiphilic compound and a drug, such that when R is not an end group then each R is linked to one of the end groups; each Y1 and Y2 is a crosslinkable group independently selected from the group consisting of boronic acid, dihydroxybenzene and a thiol; subscript m is an integer from <NUM> to <NUM>; and wherein each branched monomer unit X is <NUM>,<NUM>-Bis(hydroxymethyl)propionic acid.

The article in <NPL>, discloses self assembly of linear dendritic block copolymers PEGm-AZOn with cyano azobenzene as fluorescent tag, but no cross linking. Example is PEG45-A7O8/<NUM> hydrophilic/ hydrophobic weight ratio is <NUM>/<NUM> and resp. <NUM>/<NUM>.

Hybrids between dendritic structures and linear segments, as those shown in <FIG>, are well-known in the prior art (so-called linear-dendritic hybrids). The dendritic part can be varied in size by growing different generations i.e. G1, G2, G3 etc of which each generation is based on a number of monomers. The linear part can also be varied by varying the chain lenght, so that the molecular weight varies (<NUM> kDa, <NUM> kDa, <NUM> kDa, <NUM> kDa etc.). Due to their amphiphilic nature, the structures can self-assemble in different ways, depening on solvent, temperature, drying method etc..

It is an object of the present invention to present a biocompatible carrier that may be adapted in order to encapsulate anionic, cationic, hydrophilic or hydrophobic cargo. The present carrier protects encapsulated peptides against chemical and enzymatic degradation. It is another object of the invention to avoid peptide self-assembly, as well as to target and control the release of actives peptides. The present invention provides nanogels that are monomodal or esssentially monomodal with a low polydisperisty index (PDI).

Accordingly the present invention provides nanostructured materials, more specifically a nanogel suitable for release of AMPs, characterized in that they provide:.

Furthermore, the present invention provides a simple and cheap way of preparing a nanogel that may function as a carrier for drugs.

In view of the above the present invention is directed to a nanogel and a method to produce said nanogel. The nanogel according to the invention comprises a polymer having hydrophobic and hydrophilic segments: wherein the hydrophilic segments are or comprise polyethylene glycol (PEG) molecules and the hydrophobic segmentes are modified dendritic <NUM>,<NUM>-Bis(hydroxymethyl)propionic acid (bis-MPA) molecules where hydrophobic segments are modified with allyl groups.

In a first aspect the present invention relates to a nanogel according to claim <NUM>.

In a second aspect the present invention relates to a pharmaceutical composition containing the nanogel according to present invention for use in topical drug delivery.

In a third aspect the present invention relates to a pharmaceutical composition containing the nanogel according to the present invention for use in treating infections selected from the group consisting of skin infections, burn wounds and lung infections.

In a fourth aspect the present invention relates to a method method for preparing the nanogel according to the present invention wherein the method comprises the following steps:.

In a fifth aspect the present invention relates to an aqueous composition comprising the nanogel according to the present invention wherein the aqeous composition comprises <NUM> to <NUM> wt% of the nanogel.

In a sixth aspect the present invention relates to a nanogel comprising nanoparticles, individual and/or inter connected, having a core and a shell;.

In the present invention the core of the dendritic nanogel carrier is either anionic, cationic, hydrophilic or hydrophobic. According to the core charge, anionic drug or cationic drug or hydrophobic drug is loaded thereof.

In a preferred embodiment of the present invention the delivered active substances are AMPs.

The present invention provides also a formulation comprising a dendritic nanogel carrier delivered in the form of topical spray, gel, pulmonary aerosol.

All embodiments disclosed herein relates to all aspects of the invention unless otherwise stated.

Other advantages of the present invention will be readily appreciated as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings wherein:.

With reference to the cited drawings it is provided, in the following, a description of a nanogel or a dendritic nanogel carrier and the method for producing it, according to the present invention.

The structure of said nanogel comprises a dendritic containing polymer comprising dendritic segments that are hydrophobic and segments that are hydrophilic which are also preferably linear. Said dendritic segments and linear segments undergo a self-assembling mechanism followed by covalent cross-linking (inter connections) to produce nanogels. The nanogel may comprise water.

The present dendritic nanogels (DNGs) are formed by means of a self-assemble process of dendritic containing polymers into self-assembled core shell nanoparticles (NP), which subsequently are cross-linked to fixate the structure. The nanogels can be post-functionalized to introduce desired functionality, such as anionic, cationic, hydrophilic or hydrophobic moieties, <FIG>. According to the present invention such dendritic containing polymer is a hybrid material comprising a hydrophilic region of polyethylene glycol (PEG) and a modified hydrophobic region of dendritic <NUM>,<NUM>-Bis(hydroxymethyl)propionic acid (bis-MPA). The modification of the hydrophobic region is done by introduction of one or more allyl groups on the bis-MPA. The PEG may have a molecular weight of <NUM>,<NUM>/mol to <NUM>,<NUM>/mol such as <NUM>,<NUM>/mol or higher, or <NUM>,<NUM>/mol or higher, but <NUM>,<NUM>/mol or less, or <NUM>,<NUM>/mol or less. The PEG is preferably linear. The bis-MPA is bonded preferably directly to the PEG via an ester.

The present inventors found that the size of the nanoparticle or nanogel can be adapted or controlled by the length of hydrophilic segments. For example using PEG with a molecular weight of <NUM>,<NUM>/mol gave an average size (Z-average, ISO <NUM>) of <NUM>, while a PEG of <NUM>,<NUM>/mol and <NUM>,<NUM>/mol resulted in a Z-average of <NUM> and <NUM> respectively (<FIG>). This is of interest since the body will take up smaller particles much faster than larger particles that instead remain circulating in the body. Thereby the uptake and release rate of the drug may be adapted.

The above hybrid material or dendritic containing polymer can be produced using three different scaffold architectures, as showed in <FIG>: a linear dendritic (LD), a dendritic linear dendritic (DLD), a dendritic linear dendritic hyperbranched (DLDhb) hybrids; wherein the linear poly ethylene glycol (PEG) block can have two different lengths. The DLDhb is characterized in that the hyper branched scaffold is not structurally perfect in comparison with LD and DLD. How close to the dendritic structure a hyperbranched strcture is usually quantified by the degree of branching (DB). DB is defined as the ratio between perfect branches and the sum of all branches. The degree of branching was calculated using the Fréchet equation.

Quantification of terminal (T), linear (L) and dendritic (D) branchesd was conducted using quantitative carbon NMR. Using the integrals of the signals characteristic to the specific monomer units, the degree of branching (DB) was calculated from Formula <NUM>.

Preferably the DB is <<NUM> i.e. the dendritic part is hyperbranched since it results in better nanogels, in comparison with perfect dendritic strucutures, where the nanogels are monomodal or essentially monomodal (singel or narrow size distribution) with a low PDI.

Said hybrid materials are characterized in that having different relative percentages of hydrophilic and hydrophobic regions, as showed in the following <FIG>.

The self-assembly step of the dendritic hybrid materials into a scaffold can be realized using four different methods known from literature, as showed in <FIG> and <FIG>.

In a preferred realisation of the invention a thin film absorption method is used for the self-assembly step of the dendritic hybrid materials, as showed in <FIG>. In comparison with other methods of the prior art (<FIG> and <FIG>), the thin film absorption method is characterized by a superior self-assembly outcome, ease of use and convenient scalability. Said method consists of dissolving in a suitable container the dendritic containing polymer along with UV initiator and cross linker in a suitable solvent, for example dichloromethane (DCM), followed by slowly evaporating the solvent while twisting the container to coat a thin layer of polymer film onto the sides of the container. A suitable amount of water is then added to disperse the dendritic containing polymer forcing it to encircle the hydrophobic cross linker and initiator with the hydrophilic part of the molecule towards the water causing the formation of self-assembled core shell nanoparticles. The solution containing self-assembled NP constructs are then exposed to UV light causing radical crosslinking in the core, fixating the structure and thus preventing disassembly.

Functionalization of the interior of said NP constructs may be conducted by adding an excess of intended functionality along with UV-Initiator dissolved in water and again exposing the mixture to UV irradiation. Purification may then be performed using dialysis against THF for one hour and then milli-Q water for <NUM> hours with water.

The self-assembly of the dendritic containing polymer shows best performance with a relative molecular weight percentage (wt%) of hydrophilic segment between <NUM> - <NUM> wt% and with a hydrophobic segment between <NUM> - <NUM> wt%. This means for example that <NUM>-<NUM>% of the total molecular weight of the linear-dendritic polymer may be the hydrophilic segmentssuch as PEG and <NUM>-<NUM>% may be the hydrophobic segments such as bis-MPA and pheripheral groups.

In a preferred embodiment <NUM> wt% hydrophilic and <NUM> wt% hydrophobic ratio offered superior properties in terms of self-assembly using the thin film absorption method without the crosslinking and functionalization. Accordingly, different types of scaffolds can be prepared using said preferred hydrophobic to hydrophilic ratio, for example: LD87/<NUM>, DLD87/<NUM>, DLDhb87/<NUM>.

Surprisingly the DLDhb87/<NUM> scaffold shows superior control over the self-assembled adducts as showed in <FIG> where the size of the constructs and the amount of aggregates are plotted against the respective scaffolds and concentration. It is showed that the hyperbranced DLDhb87/<NUM> material provides a more controlled and defined NP in comparison with other scaffolds with the same hydrophobic to hydrophilic ratio. In <FIG>it is showed that LD87/<NUM> scaffold provides more aggregates while DLDhb87/<NUM> scaffold provides more control over self-assembled constructs. Size wise, relating to the nanogel or the self assembly, the LD87/<NUM> is smaller than the DLDhb87/<NUM> system offering sizes down to <NUM> in diameter while the larger DLDhb87/<NUM> system offers sizes between <NUM> and <NUM> <FIG> a.

Different PEG lengths and dendritic generation can be used for the formation of DNGs. In a preferred embodiment the dendritic segment is of second generation (G2) or of third generation (G3). In a more preferred embodiment the PEG has a molecular weight of <NUM>-<NUM>/mol and the dendritic segment is G2. In another more preferred embodiment the PEG has a molecular weight of <NUM>-<NUM>/mol and the dendritic segment is G3. These embodiments results in nanogels that are monomodal or essentially monomodal (singel or narrow size distribution) and with a low PDI such as <NUM> or lower preferably <NUM> or lower, <FIG>.

In one embodiment the size distribution of the nanogel is essentially monomodal or monomodal, Figure 7b. In another embodiment the nanogel has a polydispersity index (PDI) of <NUM> or lower preferably <NUM> or lower, or more preferably <NUM> or lower, or more preferably <NUM> or lower.

The crosslinking ratio in the nanogel may be <NUM>-<NUM> mol% i.e. <NUM>-65mol% of the allyl groups are used in the crosslinking. In a preferred embodiment the crosslinking ratio is <NUM>-<NUM> mol% more preferably <NUM>-60mol%.

In <FIG> it is shown the optimal concentration for formation of NP, where concentration is plotted against the dispersity index. It is apparent that the lowest PDI, that is the narrowest size distribution and the most uniform NP, is attained at a concentration of <NUM>/ml as confirmed by the DLS traces in <FIG> b. At a concentration of <NUM>/ml a small amount of aggregation of nanogels is seen in the intensity trace otherwise no aggregates can be seen for any concentration. In a preferred embodiment the concentration is <NUM>-<NUM>/ml more preferably <NUM>/ml. In a preferred embodiment the pharmaceutical composition according to the present invention comprises <NUM>-<NUM>/ml or more preferably <NUM>/ml of nanogel.

The formation of the dendritic nanogel, by means of a cross-linking step of the nanoscale assembled scaffold, provides a contraction from <NUM> to <NUM> (measured by DLS and TEM), probably caused by the constriction of covalent bonds forming in the core of the DNG. Cross-linking increases the stability with the current date passing <NUM> days. Addition of THF and acetone to the cross-linked system did not cause disassembly in the cross-linked system while in the non-cross-linked system it caused complete disassembly also indicating crosslinks were formed.

Crosslinking step can be performed on a different percentage of available allyls, for example between <NUM> mol% and <NUM> mol%. In preferred realisations of the present invention crosslinking is produced on the following percentage of available allyls: <NUM> mol%; <NUM> mol%; <NUM> mol%; <NUM> mol%; <NUM> mol%. A graphical representation of degree of crosslinking as well as molar amount of anionic moieties produced can be seen in <FIG>. The gels are abbreviated dendritic nano gel (DNG) and with a number from <NUM> to <NUM>. In Table <NUM> the ratios of crosslinking for the different DNGs can be seen.

The crosslink may be obtained using thiolene chemistry forming a sulphur bond or sulphur bridge. The crosslinking may be performed using mercapto propionic acid or cysteamine and a di- or trifunctional thiol. The crosslinking may result in a thioether linkage.

The allyl group may be any suitable C3 or longer alkyl group comprising an unsaturation. In one embodiment the allyl group is a C3 to C6 group (-CH2-CH=CH2 to -(CH2)<NUM>-CH=CH2). In another embodiment the allyl group is a C5 group (-(CH2)<NUM>-CH=CH2). The C5 group may be obtained by modifying using <NUM>-pentenoic acid. Longer chain length in the allyl group increases the hydrophobicity in the hydrophobic segment.

DNGs offer several advantages as carrier, a large batch can be produced with a predetermined cross-linking degree. Then smaller batches can be functionalized to display anionic, cationic and hydrophobic core characteristics. The covalent attachement in the core of a flourescent dye in combination with previously mentioned core characteristics is also possible. The core characteristics can be altered to optimally suit the intended cargo using various degrees of anionic, cationic, hydrophobic or a combination of moieties. Each batch would be otherwise identical since the "naked" cross-linked scaffold is from the same batch. Any thiol functional moiety can potentially be used to provide function or characteristics to the core and any thiol molecule with a number of thiols equal to or greater then three can be used as crosslinker. Flourecent tags with a thiol functionality could be incorporated in the core to provide traceability to the scaffold. The modular nature of the DNGs with their vast possibilities for modification of the core characteristics offer the possibility to tailor the system to carry or encapsulate a wide variety of cargoes, for example: cationic or anionic molecules such as cationic drug loading, anionic drug loading; or hydrophobic or hydrophilic drug loading.

Wherein the nanogel encapsulates a cargo that are cationic drugs, DNGs are accordingly modified to show anionic characteristics in the core by means of thiol-ene chemistry of appropriatly cross-linked DNG with mercapto propionic acid.

Cargoes include cationic peptides, cationic proteins, cationic antigens and cationic synthetic molecules such as doxorubicin among many others.

Peptide loading is done by considering the charge of the peptide and the charge of the DNG. Peptide amount with equal or lower total charge than the charge of the DNG can be loaded into the system.

In a preferred embodiment the antimicrobial peptide loaded to the carrier is DPK-<NUM> for the treatment of skin and soft tissue infections (SSTI).

Higher peptide concentrations display more pronounced aggregation than at lower peptide concentrations. Interestingly, no significant change in z-potential was observed upon DPK-<NUM> loading suggesting that the gel structure contains a charged core screened from the surroundings by the linear PEG structure.

In another preferred embodiment the antimicrobial peptide loaded to the carrier is LL-<NUM>, a widely used AMP for a broad range of bacteria and also towards others pathogens (fungi, viruses).

The effect of nanoformulated AMPs (which are cationic) were evaluated with state-of-the art in vitro models and in vivo models.

Encapsulation of anionic substances Wherein the cargoes are anionic drugs, DNGs are accordingly modified to show cationic characteristics in the core by means of a functionalization performed using cysteamine or similar molecules thereof.

Cargoes include SI-RNA, anionic peptides, anionic proteins, anionic antigens and anionic synthetic molecules such as diclofenac, salicylic and ibuprofen acid among many others.

Loading is done by considering the charge of the drug and the charge of the DNG. Drug amount with equal or lower total charge than the charge of the DNG can be loaded into the system.

Encapsulation of hydrophobic substances Wherein the cargoes are hydrophobic drugs, DNGs can be used without modification since the residual allyls unused when cross-linking is performed, as well as the dendritic block, are hydrophobic. If a more hydrophobic nature is desired hexanethiol can for example be used to functionalize the core.

Cargoes include doxorubicin, cisplatin, gemcitabine, erlotinib, fluorouracil, mitoxantrone, irinotecan, Idarubicin, triptolite, paclitaxel among many other drugs that are hydrophobic in natutre.

Loading is preformed by dissolving hydrophobic drug in a suitable solvent together with the freezedried DNG. Followed by the addition of water or buffert. The organic solvent is then allowed to evaporate compleatly, the excess drug can be purified by casette dialysis.

In a preferred embodiment the hydrophobic drug loaded is doxorubicine. <FIG> shows the release of said drug other time in the case of four samples: free DOX, DNG1, DNG2 and DNG5. Slow release characteristics can be seen where a release of approximatly <NUM> wt% can be seen almost linearly after <NUM> for DNG <NUM>, <NUM> and <NUM>.

The dendritic nanogels are all capable of both encapsulating and delivering target peptides, as evidenced by release studies monitored by confocal microscopy.

PEG20K-G3-Allyl (<NUM>, <NUM>µmol), Trimethylolpropane tris(<NUM>-mercaptopropionate) (TMP-SH) (<NUM>, <NUM>, <NUM>, <NUM>, <NUM>, eq/allyl for DNG <NUM>, <NUM>, <NUM>, <NUM>, <NUM> respectively) and <NUM>,<NUM>-Dimethoxy-<NUM>-phenylacetophenone (DMPA) (<NUM> wt%) was dissolved in DCM (<NUM>) in a round bottom flask. The solvent was slowly evaporated under reduced pressure to form a thin transparent film. Milli-Q water (<NUM>) was added to the flask and the flask was vortexed for <NUM> minute and submerged in an ultrasound bath (<NUM>) for <NUM> minutes. A sample was taken for size and <NUM>-NMR analysis. Resulting colloidal dispersion was exposed to UV light under constant stirring for <NUM> minutes (dosage = <NUM> J/mm2) (UVP Blak- Ray UV Benchtop Lamps, P/N: <NUM>-<NUM>-<NUM>, <NUM>, 230V, <NUM>). A sample was taken for size and <NUM>-NMR analysis. Mercapto propionic acid (<NUM>, <NUM>, <NUM>, <NUM>, <NUM> eq/allyl for DNG <NUM>, <NUM>, <NUM>, <NUM>, <NUM> respectively) along with DMPA (<NUM> wt%) dissolved in two mL of THF was added. The sample was vortexed for <NUM> minute and submerged in an ultrasound bath (<NUM>) for <NUM> minutes and subsequently exposed to UV light under constant stirring for <NUM> minutes (dosage = <NUM> J/mm2) (UVP Blak- Ray UV Benchtop Lamps, P/N: <NUM>-<NUM>-<NUM>, <NUM>, 230V, <NUM>). A sample was taken for size and <NUM>-NMR analysis (size: <NUM>, conversion allyls: (<NUM> mol%)). The liquid was poured in to a dialysis membrane and dialyzed against THF: H2O (<NUM>:<NUM>), (<NUM>:<NUM>) and then water changing solvent with even intervals: <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM>, <NUM> hours. Resulting slightly cloudy liquid was freeze dried to attain product as a fluffy cloud like solid (<NUM>).

Refer to the following publication by Ihre et. al3, different mPEG (Mw =<NUM><NUM>, <NUM><NUM>/mol) and PEG (Mw = <NUM><NUM> and <NUM><NUM>/mol) were used for fabrication of MM-PEG5K-G3-OH, MM-PEG10K-G3-OH, PEG10K-G3-OH and PEG20K-G3-OH, respectively.

The synthesis was based on polycondensation between PEG and Bis-MPA. PEG was added in a two necked round bottom flask equipped with argon inlet, magnetic stirrer and distillation equipment and heated to <NUM>. Every sixty minutes bis-MPA equivalent to one increase in dendritic generation was added along with pTSA, (wt% pTSA based bis-MPA added; <NUM> wt% PEG2K, <NUM> wt% PEG6K and <NUM> wt% PEG20K). During addition of bis-MPA, argon was flushed through the reaction vessel. When the desired generation had been reached one additional hour of argon flushing was applied after which vacuum was induced in the reaction vessel for <NUM> hours. The resin was extracted from the reaction vessel by dissolution in DCM and consecutively precipitated in ether two times and subsequent dried on high vacuum. Generation <NUM> to <NUM> (G2-<NUM>) were synthesized according to the same reaction scheme for two different PEG (Mw =<NUM><NUM> and <NUM><NUM>/mol) for the fabrication of PEG10K-(hb)G3-OH and PEG20K-(hb)G3-OH, respectively (reference is made to Andrén et.

Amphiphile was dissolved in pyridine (3eq. /OH) and DCM (<NUM>) in a round bottom flask equipped with magnetic stirrer. DMAP (<NUM>,<NUM> eq. /OH) was added and the reaction was cooled to <NUM> using an ice bath. <NUM>-Pentanoic anhydride (<NUM>,<NUM> eq. /OH) dissolved in <NUM> of DCM was slowly added over a period of <NUM> minutes. Reaction was allowed to proceed overnight and progression was monitored by 13C-NMR by confirming the presence of the anhydride peak at <NUM> ppm. The crude reaction was precipitated in ether (<NUM>) and white powder collected, re dissolved in DCM and re precipitated in cold ether (<NUM>). Product was collected as a white powder.

To ensure full conversion of the remaining allyls freeze-drying of DNG2 was preformed and allyl presence was investigated by NMR spectroscopy. In <FIG> (to the right) the spectra can be seen with complete disappearance of signal associated with allyls after functionalization, indicating full conversion to carboxylic interior. Since a core-shell structure is formed some degree of shielding of the desired structure can be expected causing the amount of allyls to be slightly underestimated (see <FIG>). The crosslinking step may be done as previously described and resulting in different crosslinking ratios as seen in Table <NUM>.

The stability and appearance at different pH was investigated for DNG2. A small pH dependant contraction can be seen for DNG2 at PH <NUM>. Indications showing that the interior is indeed anionic can be seen as an affect to alterations in the exterior pH, <FIG>.

The stability of the DNGs has been assed using DLS, the size and polydispersity index (PDI) was recorded for systems stored in milli-Q water at room temperature after a dilution in milli-Q water, <FIG>. DNG <NUM> with the lowest crosslinking density displays some degree of instability where spectra can no longer be recorded with satisfactory results after <NUM> days. The rest of the DNGs appears to be quite stable even after almost <NUM> days of storage at room temperature.

The DNGs are inherently non-toxic, below a MTT assay was preformed to evaluate the toxicity of DNG <NUM>,<NUM>,<NUM> modified to display anionic interior can be seen, <FIG>.

The subject-matter of the invention is susceptible of numerous modifications and variations, without departing from the inventive concept as expressed in the accompanying claims.

All the above-described details may furthermore be replaced with other technically equivalent elements, and the materials may be different according to the single needs, without departing from the scope of protection of the present invention.

Although the present invention has been described with particular reference to the accompanying drawings, the reference numbers used in the description and in the claims are used to improve the intelligibility of the invention and do not represent any limitation to the scope of protection claimed. Example <NUM>.

Different nanogels were prepared according to the method disclosed in Example <NUM>.

<FIG> : Doxorubicin (DOX) loaded DNGs showed similar or improved anticancer efficacy as free DOX.

Claim 1:
A nanogel comprising nanoparticles, individual and/or inter connected, having a core and a shell;
wherein the nanoparticles comprise self-assembled dendritic containing polymers having a scaffold architecture of dendritic linear dendritic (DLD) wherein the degree of branching of the hydrophobic segment is <<NUM> and wherein the dendritic segments form the core and the linear hydrophilic segment forms the shell;
wherein the hydrophilic segment is or comprises polyethylene glycol (PEG) and the hydrophobic segments are dendritic <NUM>,<NUM>-Bis(hydroxymethyl)propionic acid (bis-MPA) molecules modified with allyl groups;
wherein the core of said nanoparticles is either anionic, cationic, hydrophilic and/or hydrophobic; and wherein the hydrophobic segments are crosslinked via said allyl groups.