Patent Description:
The present disclosure relates to, among other things, magnetoresistive stacks and methods for fabricating and using the disclosed magnetoresistive stacks. US application <CIT> relates to a magnetic tunnel junction (MTJ) device in a magnetoresistive random access memory (MRAM) and method of making the same which are provided to achieve a high tunneling magnetoresistance (TMR), a high perpendicular magnetic anisotropy (PMA), good data retention, and a high level of thermal stability. The MTJ device includes a first free ferromagnetic layer, a synthetic antiferromagnetic (SAF) coupling layer, and a second free ferromagnetic layer, where the first and second free ferromagnetic layers have opposite magnetic moments.

US patent <CIT> relates to a magnetic junction usable in a magnetic device which includes a pinned layer, a nonmagnetic spacer layer, an asymmetric free layer and a perpendicular magnetic anisotropy (PMA) inducing layer. The nonmagnetic spacer layer is between the pinned layer and the free layer. The free layer is between the nonmagnetic spacer layer and the PMA inducing layer. The asymmetric free layer includes a first ferromagnetic layer having a first boron content and a second ferromagnetic layer having a second boron content. The second boron content is less than the first boron content. The first boron content and the second boron content are each greater than zero atomic percent. The magnetic junction is configured such that the asymmetric free layer is switchable between stable magnetic states when a write current is passed through the magnetic junction.

Finally, US application <CIT> relates to a MgO-based magnetic tunnel junction (MTJ) device which includes a ferromagnetic reference layer, a MgO tunnel barrier and a ferromagnetic free layer. The microstructure of the MgO tunnel barrier, which is prepared by a metallic Mg deposition followed by the oxidation process or reactive sputtering, is amorphous or microcrystalline with poor (<NUM>) out-of-plane texture. At least only the ferromagnetic reference layer or both of the ferromagnetic reference and free layer are proposed to have a bi-layer structure having a crystalline preferred grain growth promotion (PGGP) seed layer adjacent to the tunnel barrier. This crystalline PGGP seed layer induces the crystallization and the preferred grain growth of the MgO tunnel barrier upon post-deposition annealing.

The claimed invention is defined by the appended claims <NUM> and <NUM>. Preferred embodiments of the claimed invention are defined by claims <NUM> to <NUM> and <NUM> to <NUM>. In one aspect, the present disclosure relates to a magnetoresistive stack or structure (for example, part of a magnetoresistive memory device, magnetoresistive sensor/transducer device, etc.) and methods of manufacturing the described magnetoresistive stacks. In one embodiment, an exemplary magnetoresistive stack (for example, used in a magnetic tunnel junction (MTJ) magnetoresistive device) of the present disclosure includes one or more layers of magnetic or ferromagnetic material configured to improve the reliability, thermal stability, and/or thermal endurance of the magnetoresistive device.

Briefly, a magnetoresistive stack used in a memory device (e.g., a magnetoresistive random access memory (MRAM)) includes at least one non-magnetic layer (for example, at least one dielectric layer or a non-magnetic yet electrically conductive layer) disposed between a "fixed" magnetic region and a "free" magnetic region, each including one or more layers of ferromagnetic materials. Information is stored in the magnetoresistive memory stack by switching, programming, and/or controlling the direction of magnetization vectors in the magnetic layer(s) of the "free" magnetic region. The direction of the magnetization vectors of the "free" magnetic region may be switched and/or programmed (for example, through spin transfer torque) by application of a write signal (e.g., one or more current pulses) through the magnetoresistive memory stack. In contrast, the magnetization vectors in the magnetic layers of a "fixed" magnetic region are magnetically fixed in a predetermined direction. When the magnetization vectors of the "free" magnetic region adjacent to the non-magnetic layer are in the same direction as the magnetization vectors of the "fixed" magnetic region adjacent to the non-magnetic layer, the magnetoresistive memory stack has a first magnetic state. Conversely, when the magnetization vectors of the "free" magnetic region adjacent to the non-magnetic layer are opposite the direction of the magnetization vectors of the "fixed" magnetic region adjacent to the non-magnetic layer, the magnetoresistive memory stack has a second magnetic state. The magnetic state of the magnetoresistive memory stack is determined or read based on the resistance of the stack in response to a read current (IR).

In some applications, a device incorporating a magnetoresistive stack (such as, for example, an MTJ device such as an MRAM) may be subject to high temperatures (during, e.g., fabrication, testing, operation, etc.). It is known that a strong perpendicular magnetic anisotropy (PMA) of the magnetoresistive stack is desirable for high temperature data retention capabilities of the device. For improved high temperature performance of the device, it is desirable to have a "free" magnetic region with high enough PMA and magnetic moment to enable the device to have a high energy barrier to thermal reversal at elevated temperatures (for example, at <NUM>, the typical temperature for soldering of packaged devices onto printed circuit boards (PCBs)), and also have reasonable switching voltage or current in the operating temperature range so that the device will have useful cycling endurance characteristics (for example, at least <NUM>,<NUM> cycles, or preferably more than <NUM> million, and more preferably over <NUM><NUM> cycles). The disclosed magnetoresistive stacks may have some or all of these desired characteristics. The scope of the current disclosure, however, is defined by the attached claims, and not by any characteristics of the resulting device or method.

Embodiments of the present disclosure may be implemented in connection with aspects illustrated in the attached drawings. These drawings show different aspects of the present inventions and, where appropriate, reference numerals illustrating like structures, components, materials and/or elements in different figures are labeled similarly. It is understood that various combinations of the structures, components, and/or elements, other than those specifically shown, are contemplated and are within the scope of the present disclosure.

For simplicity and clarity of illustration, the figures depict the general structure and/or manner of construction of the various embodiments described herein. For ease of illustration, the figures depict the different layers/regions of the illustrated magnetoresistive stacks as having a uniform thickness and well defined boundaries with straight edges. However, a person skilled in the art would recognize that, in reality, the different layers typically have a non-uniform thickness. And, at the interface between adjacent layers, the materials of these layers alloy together, or migrate into one or the other material, making their boundaries ill defined. Descriptions and details of well-known features (e.g., interconnects, etc.) and techniques may be omitted to avoid obscuring other features. Elements in the figures are not necessarily drawn to scale. The dimensions of some features may be exaggerated relative to other features to improve understanding of the exemplary embodiments. Cross-sectional views are simplifications provided to help illustrate the relative positioning of various regions/layers and describe various processing steps. One skilled in the art would appreciate that the cross-sectional views are not drawn to scale and should not be viewed as representing proportional relationships between different regions/layers. Moreover, while certain regions/layers and features are illustrated with straight <NUM>-degree edges, in actuality or practice such regions/layers may be more "rounded" and gradually sloping.

Further, one skilled in the art would understand that, although multiple layers with distinct interfaces are illustrated in the figures, in some cases, over time and/or exposure to high temperatures, materials of some of the layers may migrate into or interact with materials of other layers to present a more diffuse interface between these layers. It should be noted that, even if it is not specifically mentioned, aspects described with reference to one embodiment may also be applicable to, and may be used with, other embodiments.

Moreover, there are many embodiments described and illustrated herein. The present disclosure is neither limited to any single aspect nor embodiment thereof, nor to any combinations and/or permutations of such aspects and/or embodiments. Moreover, each aspect of the present disclosure, and/or embodiments thereof, may be employed alone or in combination with one or more of the other aspects of the present disclosure and/or embodiments thereof. For the sake of brevity, certain permutations and combinations are not discussed and/or illustrated separately herein. Notably, an embodiment or implementation described herein as "exemplary" is not to be construed as preferred or advantageous, for example, over other embodiments or implementations; rather, it is intended reflect or indicate the embodiment(s) is/are "example" embodiment(s). Further, even though the figures and this written disclosure appear to describe the disclosed magnetoresistive stacks in a particular order of construction (e.g., from bottom to top), it is understood that the depicted magnetoresistive stacks may have a different order (e.g., the opposite order (i.e., from top to bottom)). For example, a "fixed" magnetic region may be formed on or above a "free" magnetic region or layer, which in turn may be formed on or above an insertion layer of the present disclosure.

Again, there are many embodiments described and illustrated herein. The present disclosure is neither limited to any single aspect nor embodiment thereof, nor to any combinations and/or permutations of such aspects and/or embodiments. Each of the aspects of the present disclosure, and/or embodiments thereof, may be employed alone or in combination with one or more of the other aspects of the present disclosure and/or embodiments thereof. For the sake of brevity, many of those combinations and permutations are not discussed separately herein.

It should be noted that all numeric values disclosed herein (including all disclosed thickness values, limits, and ranges) may have a variation of ±<NUM>% (unless a different variation is specified) from the disclosed numeric value. For example, a layer disclosed as being "t" units thick can vary in thickness from (t-<NUM>. 1t) to (t+<NUM>. Further, all relative terms such as "about," "substantially," "approximately," etc. are used to indicate a possible variation of ±<NUM>% (unless noted otherwise or another variation is specified). Moreover, in the claims, values, limits, and/or ranges of the thickness and atomic composition of, for example, the described layers/regions, mean the value, limit, and/or range ±<NUM>%. It should be noted that, unless otherwise indicated, all the alloy compositions discussed in this disclosure are in atomic percent.

It should be noted that the description set forth herein is merely illustrative in nature and is not intended to limit the embodiments of the subject matter, or the application and uses of such embodiments. Any implementation described herein as exemplary is not to be construed as preferred or advantageous over other implementations. Rather, the term "exemplary" is used in the sense of example or "illustrative," rather than "ideal. " The terms "comprise," "include," "have," "with," and any variations thereof are used synonymously to denote or describe a non-exclusive inclusion. As such, a device or a method that uses such terms does not include only those elements or steps, but may include other elements and steps not expressly listed or inherent to such device and method. Further, the terms "first," "second," and the like, herein do not denote any order, quantity, or importance, but rather are used to distinguish one element from another. Similarly, terms of relative orientation, such as "top," "bottom," etc. are used with reference to the orientation of the structure illustrated in the figures being described. Moreover, the terms "a" and "an" herein do not denote a limitation of quantity, but rather denote the presence of at least one of the referenced item.

In this disclosure, the term "region" is used generally to refer to one or more layers. That is, a region (as used herein) may include a single layer (deposit, film, coating, etc.) of material or multiple layers of materials stacked one on top of another (i.e., a multi-layer structure). Further, although in the description below, the different regions and/or layers in the disclosed magnetoresistive stacks are referred to by specific names (capping region, reference region, transition region, etc.), this is only for ease of description and not intended as a functional description of the layer. Moreover, although the description below and the figures appear to depict a certain orientation of the layers relative to each other, those of ordinary skill in the art will understand that such descriptions and depictions are only exemplary. For example, though the "free" region is depicted as being "above" an intermediate region, in some aspects the entire magnetoresistive stack may be flipped such that the intermediate region is "above" the "free" region.

In one exemplary aspect, the magnetoresistive stack of the present disclosure may be implemented as a spin-torque magnetoresistive random access memory ("MRAM") element ("memory element"). In such aspects, the magnetoresistive stack may include an intermediate region positioned (or sandwiched) between two ferromagnetic regions to form a magnetic tunnel junction (MTJ) device or an MTJ-type device. The intermediate region may be a tunnel barrier and include an insulating material, such as, e.g., a dielectric material. In other embodiments, the intermediate region may be a conductive material, e.g., copper, gold, or alloys thereof. In these other embodiments, where the magnetoresistive stack includes a conductive material in between two ferromagnetic regions, the magnetoresistive stack may form a giant magnetoresistance (GMR) or GMR-type device.

Of the two ferromagnetic regions disposed on either side of the intermediate region, one ferromagnetic region may be a magnetically "fixed" (or pinned) region, and the other ferromagnetic region may be a magnetically "free" region. The term "free" is intended to refer to ferromagnetic regions having a magnetic moment that may shift or move significantly in response to applied magnetic fields or spin-polarized currents used to switch the magnetic moment vector. On the other hand, the words "fixed" and "pinned" are used to refer to ferromagnetic regions having a magnetic moment vector does not move substantially in response to such applied magnetic fields or spin-polarized currents. As is known in the art, an electrical resistance of the described magnetoresistive stack may change based on whether the magnetization direction (e.g., the direction of the magnetic moment) of the "free" region adjacent to the non-magnetic layer is in a parallel alignment or in an antiparallel alignment with the magnetization direction (e.g., the direction of the magnetic moment) of the "fixed" region adjacent to the non-magnetic layer. Typically, if the two regions have the same magnetization alignment, the resulting low resistance is considered as a digital "<NUM>," while if the alignment is antiparallel the resulting higher resistance is considered to be a digital "<NUM>. " A memory device (such as an MRAM) may include multiple such magnetoresistive stacks, which may be referred to as memory cells or elements, arranged in an array of columns and rows. By measuring the current through each cell, the resistance of each cell, and thus the data stored in the memory array can be read.

Switching the magnetization direction of the "free" region of a magnetoresistive stack may be accomplished by driving a tunneling current pulse through the magnetoresistive stack. The polarity of the current pulse determines the final magnetization state (i.e., parallel or antiparallel) of the "free" region. The mean current required to switch the magnetic state of the "free" region may be referred to as the critical current (Ic). The critical current is indicative of the current required to "write" data in (or the write current of) a magnetoresistive memory cell. Reducing the required write current(s) is desirable so that, among other things, a smaller access transistor can be used for each memory cell and a higher density, lower cost memory can be produced. Reduced write current requirements may also lead to greater longevity of a magnetoresistive memory cell.

For the sake of brevity, conventional techniques related to semiconductor processing may not be described in detail herein. The exemplary embodiments may be fabricated using known lithographic processes. The fabrication of integrated circuits, microelectronic devices, micro electro mechanical devices, microfluidic devices, and photonic devices involves the creation of several layers or regions (i.e., comprising one or more layers) of materials that interact in some fashion. One or more of these regions may be patterned so various regions of the layer have different electrical or other characteristics, which may be interconnected within the region or to other regions to create electrical components and circuits. These regions may be created by selectively introducing or removing various materials. The patterns that define such regions are often created by lithographic processes. For example, a layer of photoresist is applied onto a layer overlying a wafer substrate. A photo mask (containing clear and opaque areas) is used to selectively expose the photoresist by a form of radiation, such as ultraviolet light, electrons, or x-rays. Either the photoresist exposed to the radiation, or not exposed to the radiation, is removed by the application of a developer. An etch may then be employed/applied whereby the layer (or material) not protected by the remaining resist is patterned. Alternatively, an additive process can be used in which a structure is built up using the photoresist as a template.

As noted above, in one aspect, the described embodiments relate to, among other things, methods of manufacturing a magnetoresistive stack having one or more electrically conductive electrodes, vias, or conductors on either side of a magnetic material stack. As described in further detail below, the magnetic material stack may include many different regions of material, where some of these regions include magnetic materials, whereas others do not. In one embodiment, the methods of manufacturing include sequentially depositing, growing, sputtering, evaporating, and/or providing (as noted above, herein collectively "depositing" or other verb tense (e.g., "deposit" or "deposited")) regions which, after further processing (for example, etching) form a magnetoresistive stack.

The disclosed magnetoresistive stacks may be formed between a top electrode/via/line and a bottom electrode/via/line and, which permit access to the stack by allowing for connectivity (for example, electrical) to circuitry and other elements of the magnetoresistive device. Between the electrodes/vias/lines are multiple regions, including at least one "fixed" magnetic region (referred to hereinafter as a "fixed" region) and at least one "free" magnetic region (referred to hereinafter as a "free" region) with one or more intermediate region(s), such as, e.g., a dielectric layer (that form(s) a tunnel barrier) between the "fixed" and "free" magnetic regions. Each of the "fixed" and "free" magnetic regions may include, among other things, a plurality of ferromagnetic layers. In some embodiments, the top electrode (and/or the bottom electrode) may be eliminated, and the bit line may be formed on top of the stack.

<FIG> is a cross-sectional view of the regions of an exemplary magnetoresistive stack <NUM> of the current disclosure. Magnetoresistive stack <NUM> may include, for example, an in-plane or out-of-plane magnetic anisotropy magnetoresistive stack (e.g., a perpendicular magnetic anisotropy magnetoresistive stack). As illustrated in <FIG>, magnetoresistive stack <NUM> includes multiple regions (or layers) arranged one over the other to form a stack of regions between a first electrode <NUM> (e.g., a top electrode) and a second electrode <NUM> (e.g., a bottom electrode). When implemented as an MTJ or MTJ-like memory device, the magnetoresistive stack <NUM> of <FIG> may represent a dual spin filter structure (or a double MTJ structure) where a "free" region <NUM> is formed between two "fixed" regions <NUM> and <NUM>. It should be noted that depiction of the magnetoresistive stack <NUM> as having a dual spin filter structure (in <FIG>) is merely exemplary and not a requirement of the current disclosure. That is, the current disclosure also is applicable to magnetoresistive stacks having a different structure (e.g., a single MTJ structure where a "free" region <NUM> is formed over a single "fixed" region <NUM>). It will be recognized that several other commonly-used regions or layers of stack <NUM> (e.g., various protective cap layers, seed layers, underlying substrate, etc.) have not been illustrated in <FIG> (and in subsequent figures) for clarity. The different regions of the multi-layer magnetoresistive stack <NUM> of <FIG> will be described below.

As shown in <FIG>, the first electrode <NUM> may be a "bottom" electrode, and the second electrode <NUM> may be a "top" electrode. However, those of ordinary skill in the art will recognize that the relative order of the various regions (or layers) of magnetoresistive stack <NUM> may be reversed. Further, in some embodiments, the top electrode (and/or the bottom electrode) may be eliminated, and the bit line may be formed on top of the stack. The bottom and top electrodes <NUM>, <NUM> may comprise an electrically conductive material, and may be part of (or be in physical contact with) electrically conductive interconnects (e.g., vias, traces, lines, etc.) of a device (e.g., MRAM) formed using the magnetoresistive stack <NUM>. Although any electrically conductive material may be used for bottom and top electrodes <NUM>, <NUM>, in some embodiments, a metal such as tantalum (Ta), titanium (Ti), tungsten (W), or a composite or alloy of these elements (e.g., tantalum-nitride alloy) may be used.

Bottom electrode <NUM> may be formed on a planar surface of a semiconductor substrate <NUM> (e.g., surface of a semiconductor substrate having electrical circuits (e.g., CMOS circuits) formed thereon, etc.). Although not illustrated in <FIG>, in some embodiments, electrode <NUM> may include a seed layer at its interface with the overlying region (e.g., region <NUM>). During fabrication, the seed layer may assist in the formation of the overlying region on electrode <NUM>. The seed layer may include one or more of nickel (Ni), chromium (Cr), cobalt (Co), iron (Fe), and alloys thereof (for example, an alloy including nickel and/or chromium). In some embodiments, the seed layer may be eliminated, and the top surface of electrode <NUM> itself may act as the seed layer.

With continuing reference to <FIG>, a "fixed" region <NUM> may be formed on (or above) the bottom electrode <NUM>. As explained previously, "fixed" region <NUM> may serve as a "fixed" magnetic region of magnetoresistive stack <NUM>. That is, a magnetic moment vector in the "fixed" region <NUM> does not move significantly in response to applied magnetic fields (e.g., an external field) or applied currents used to switch the magnetic moment vector of a "free" region <NUM> of the magnetoresistive stack <NUM>. It should be noted that the structure of the "fixed" region <NUM> illustrated in <FIG> is only exemplary. As known to those of ordinary skill in the art, many other configurations of the "fixed" region <NUM> also are possible. In general, the "fixed" region <NUM> may include a single layer or multiple layers stacked one on top of another. The layers of "fixed" region <NUM> may include alloys that include cobalt and iron and other materials (preferably cobalt, iron, and boron). Typically, the composition of materials (e.g., cobalt, iron, and boron) in the "fixed" region <NUM> may be selected to achieve good temperature compensation. For the sake of clarity, only certain layers of "fixed" region <NUM> (and regions on either side of "fixed" region <NUM>) are illustrated in <FIG>. Those of ordinary skill in the art will readily recognize that the "fixed" region <NUM> may include one or more additional layers.

In one embodiment, "fixed" region <NUM> may be a fixed, unpinned synthetic antiferromagnetic (SAF) region disposed on or above electrode <NUM>. The fixed, unpinned synthetic antiferromagnetic (SAF) region may include at least two magnetic regions (i.e., made of one or more layers) <NUM>, <NUM> (e.g., ferromagnetic layer <NUM> and ferromagnetic layer <NUM>) separated by a coupling region <NUM>. The one or more of magnetic regions <NUM>, <NUM> may include one or more of the ferromagnetic elements nickel, iron, and cobalt, including alloys or engineered materials with one or more of the elements palladium (Pd), platinum (Pt), chromium, and alloys thereof. The coupling region <NUM> may be an antiferromagnetic (AF) coupling region that includes non-ferromagnetic materials such as, for example, iridium (Ir), ruthenium (Ru), rhenium (Re), or rhodium (Rh). In some embodiments, one or both regions <NUM>, <NUM> may comprise a magnetic multi-layer structure that includes a plurality of layers of (i) a first ferromagnetic material (e.g., cobalt) and (ii) a second ferromagnetic material (e.g., nickel) or a paramagnetic material (e.g., platinum). In some embodiments, regions <NUM>, <NUM> may also include, for example, alloys or engineered materials with one or more of palladium, platinum, magnesium (Mg), manganese (Mn), and chromium. Additionally, or alternatively, in some embodiments, the "fixed" region <NUM> may include one or more synthetic ferromagnetic structures (SyF). Since SyFs are known to those skilled in the art, they are not described in greater detail herein. In some embodiments, the "fixed" region <NUM> may have a thickness in the range of between approximately <NUM>Å and approximately <NUM>Å, between approximately <NUM>Å and approximately <NUM>Å, greater than or equal to <NUM>Å, greater than or equal to <NUM>Å, less than or equal to <NUM>Å, or less than or equal to <NUM>Å.

In some embodiments, the "fixed" region <NUM> may also include one or more additional layers, such as, for example, a transition region <NUM> and a reference region <NUM>, disposed at the interface between the magnetic region <NUM> and an overlying region (e.g., region <NUM>, which as will be explained later may include a dielectric material in an MTJ structure). The reference and/or transition regions may include one or more layers of material that, among other things, facilitate/improve growth of the overlying region <NUM> during fabrication of stack <NUM>. In one embodiment, the reference region <NUM> may comprise one or more (e.g., all) of cobalt, iron, and boron (for example, in an alloy - such as an amorphous alloy (e.g., CoFeB or CoFeBTa or CoFeTa)), and the transition region <NUM> may include a non-ferromagnetic transition metal such as tantalum (Ta), titanium (Ti), tungsten (W), ruthenium, niobium (Nb), zirconium (Zr), and/or molybdenum (Mo).

In general, the transition region <NUM> and the reference region <NUM> may have any thickness. In some embodiments, a thickness (t) of the reference region <NUM> may be between approximately <NUM> - <NUM>Å, preferably approximately <NUM> - 12Å, and more preferably approximately <NUM> - <NUM>. 5Å, and the thickness of the transition region <NUM> may be between approximately <NUM> - <NUM>Å, preferably approximately <NUM> - <NUM>Å, and more preferably approximately <NUM> - <NUM>Å. It should be noted that, in some embodiments of magnetoresistive stacks <NUM>, both transition region <NUM> and reference region <NUM> may be provided in the "fixed" region <NUM>. In some embodiments, the transition region <NUM> or both of the transition region <NUM> and the reference region <NUM> may be eliminated altogether from magnetoresistive stack <NUM>. And, in some embodiments, only the reference region <NUM> may be provided in the "fixed" region <NUM>.

"Fixed" region <NUM> may be deposited or formed using any technique now known or later developed, all of which are intended to fall within the scope of the present disclosure. In some embodiments, one or more of the magnetic regions of the "fixed" region <NUM> (e.g., regions <NUM>, <NUM>) may be deposited using a "heavy" inert gas (for example, xenon (Xe)), for example, at room temperature (for example, <NUM>-<NUM>, and more preferably <NUM>-<NUM>, and most preferably <NUM> (+/- <NUM>%)) or a conventional/typical elevated temperature. In some embodiments, the AF coupling region <NUM> may also be deposited using a "heavy" inert gas (for example, xenon (Xe), argon (Ar), and/or krypton (Kr)) at such temperatures. In embodiments where the transition region <NUM> and/or the reference region <NUM> are provided, they may also be deposited using a "heavy" inert gas (for example, xenon (Xe), argon (Ar), and/or krypton (Kr)) at about room temperature (for example, approximately <NUM>-<NUM>, and more preferably <NUM>-<NUM>, and most preferably <NUM> (+/- <NUM>%)) or an elevated temperature (e.g., approximately <NUM>-<NUM>).

The various regions or layers of "fixed" region <NUM> depicted in <FIG> may be deposited individually during a fabrication process. However, as would be recognized by those of ordinary skill in the art, in some embodiments, the materials that make up the various depicted regions may alloy with (intermix with, diffuse into, etc.) the materials of adjacent regions during a subsequent processing (e.g., high temperature processing operations, such as, annealing, etc.). Therefore, a person skilled in the art would recognize that, although the different regions (of "fixed" region <NUM> of <FIG>) may appear as separate regions with distinct interfaces immediately after formation of these regions, after subsequent processing operations, the materials of the different regions may alloy together to form a single alloyed "fixed" region <NUM> having a higher concentration of different materials at interfaces between different regions. Thus, in some cases, it may be difficult to distinguish the different regions of the "fixed" region <NUM> (and other regions) in a finished magnetoresistive stack <NUM>.

With renewed reference to <FIG>, a "free" region <NUM>, or storage region, may be provided "above" the "fixed" region <NUM> with an intermediate region <NUM> formed between the "fixed" region <NUM> and the "free" region <NUM>. The relative orientation depicted in <FIG> is only exemplary. Those of ordinary skill will readily recognize that "free" region <NUM> may be provided "below" the "fixed" region <NUM> in the illustration of <FIG>. As explained previously, the type of intermediate region <NUM> formed depends upon the type of magnetoresistive stack <NUM> being fabricated. For a magnetoresistive stack <NUM> having an MTJ structure, the intermediate region <NUM> may include a dielectric material and may function as a tunnel barrier. In a spin valve structure, the intermediate region <NUM> may include a conductive material (e.g., copper) to form a GMR-type magnetoresistive stack <NUM>. Intermediate region <NUM> may be formed on (or above) a surface of the "fixed" region <NUM>, and the "free" region <NUM> may be formed on (or above) a surface of the intermediate region <NUM>. In general, intermediate region <NUM> may be formed on or above the "fixed" region <NUM> using any technique now known (e.g., deposition, sputtering, evaporation, etc.) or later developed. In some embodiments, intermediate region <NUM> may include an oxide material, such as, for example, Magnesium Oxide (MgOx) or Aluminum Oxide (AlOx (e.g., Al<NUM>O<NUM>)), and may be formed by multiple steps of material deposition and oxidation. In general, intermediate region <NUM> may have any thickness. In some embodiments, the intermediate region <NUM> may have a thickness between approximately <NUM> - <NUM>Å, preferably between approximately <NUM> - <NUM>Å, and more preferably between approximately <NUM> - <NUM>Å.

It should be noted that the construction of the "free" region <NUM> illustrated in <FIG> is only exemplary, and many other constructions are possible. Notwithstanding the specific construction of the "free" region <NUM>, as explained previously, a magnetic vector (or moment) in "free" region <NUM> may be moved or switched by applied magnetic fields or spin torque currents. In some embodiments, the "free" region <NUM> may include one or more regions <NUM>, <NUM>, <NUM>, <NUM> formed of a magnetic or ferromagnetic material separated by one or more non-magnetic insertion region(s) <NUM>. The insertion region <NUM> may provide either ferromagnetic coupling or antiferromagnetic coupling between the ferromagnetic regions <NUM>, <NUM> and <NUM>, <NUM> of the "free" region <NUM>. The materials of ferromagnetic regions <NUM>, <NUM>, <NUM>, <NUM> may include alloys of one or more of ferromagnetic elements, such as, nickel, iron, and/or cobalt, and in some embodiments, boron. In some embodiments, the ferromagnetic regions <NUM>, <NUM>, <NUM>, <NUM> comprise cobalt, iron, and boron (referred to as CoFeB).

As will be explained in more detail below, in some embodiments, some of the ferromagnetic regions (e.g., regions <NUM>, <NUM>) of "free" region <NUM> may be formed by directly depositing a boron-containing ferromagnetic alloy (such as, for example, CoFeB), and some of the regions (e.g., regions <NUM>, <NUM>) may be formed by separately depositing a boron-free ferromagnetic alloy (such as, for example, CoFe) and a boron-containing ferromagnetic alloy (e.g., region <NUM>) adjacently. In some such embodiments, the ferromagnetic regions <NUM>, <NUM> on one side of the insertion region <NUM> may comprise cobalt and iron (i.e., CoFe) (i.e., a boron-free ferromagnetic alloy), and the ferromagnetic regions <NUM>, <NUM> on the other side of the insertion region <NUM> may comprise cobalt, iron, and boron (CoFeB) (i.e., a boron-containing ferromagnetic alloy). As will be explained in more detail later, in some embodiments, the ferromagnetic regions of "free" region <NUM> on either side of insertion region <NUM> (e.g., regions <NUM>, <NUM>, <NUM>, and/or <NUM>) may be formed by separately depositing a boron-free ferromagnetic alloy (such as, for example, an alloy of cobalt (Co) and iron (Fe), e.g., cobalt-iron alloy (CoFe) and a boron-containing ferromagnetic alloy (e.g., region <NUM>) adjacent to the boron-free ferromagnetic alloy.

The exact composition of the CoFe in regions <NUM> and <NUM>, and CoFeB alloys in regions <NUM> and <NUM> may depend upon the application. In some embodiments, one or more of the ferromagnetic regions <NUM>, <NUM> may comprise a CoFeB alloy having a composition of between approximately <NUM>-<NUM> atomic percent (at. %) of Co, approximately <NUM>-<NUM> at. % of B, and the remainder being iron, or preferably between approximately <NUM>-<NUM> at. % Co, approximately <NUM>-<NUM> at. % B, and the remainder being iron, or more preferably approximately <NUM>% at. % Fe, approximately <NUM> at. % B, and the remaining cobalt. In some embodiments, one or more of the ferromagnetic regions <NUM>, <NUM> may comprise a CoFe alloy having a composition of between approximately <NUM>-<NUM> at. % Co and the remainder being iron, or preferably between approximately <NUM>-<NUM> at. % Co and the remainder being iron, or more preferably approximately <NUM>-<NUM> at. % Co and the remainder being iron. In some embodiments, the CoFe alloy of ferromagnetic regions <NUM>, <NUM> may have a crystalline or a non-amorphous crystal structure. In some embodiments, additional elements may be added to the alloys of ferromagnetic regions <NUM>, <NUM>, <NUM>, <NUM> to provide improved magnetic, electrical, or microstructural properties.

Insertion region <NUM> may include any nonmagnetic material (now known or developed in the future) that can provide coupling (e.g., ferromagnetic or antiferromagnetic) between the ferromagnetic regions on either side of the intermediate region <NUM>. That is, insertion region <NUM> may provide coupling between the ferromagnetic regions <NUM>, <NUM> on the one side, and the ferromagnetic regions <NUM>, <NUM> on the other side. In some embodiments, the insertion region <NUM> may include materials such as tantalum (Ta), tungsten (W), molybdenum (Mo), ruthenium (Ru), rhodium (Rh), rhenium (Re), iridium (Ir), hafnium (Hf), chromium (Cr), osmium (Os), and their combinations. Although ferromagnetic regions <NUM>, <NUM> separated by a single insertion region <NUM> is illustrated in <FIG>, this is only exemplary. In general, "free" region <NUM> may have any number of ferromagnetic regions (<NUM>, <NUM>, <NUM>, <NUM>, etc.) with insertion regions <NUM> provided between adjacent ferromagnetic regions.

In general, the ferromagnetic regions <NUM>, <NUM>, <NUM>, <NUM> may have any thickness. In some embodiments, the thickness of the ferromagnetic regions <NUM>, <NUM>, <NUM>, <NUM> may each be between approximately <NUM> - <NUM>Å (preferably approximately <NUM> - <NUM>Å, or more preferably between approximately <NUM> - <NUM>Å). The thickness of insertion region <NUM> is typically chosen to provide strong ferromagnetic or antiferromagnetic coupling between the ferromagnetic regions (sometimes referred to as ferromagnetic region <NUM> (FM1) and ferromagnetic region <NUM> (FM2)) on either side of the insertion region <NUM>. In general, the insertion region <NUM> may comprise a thin layer positioned between ferromagnetic regions <NUM>/<NUM> (e.g., ferromagnetic region <NUM> (FM1)) and ferromagnetic regions <NUM>/<NUM> (e.g., ferromagnetic region <NUM> (FM2)). The thickness of insertion region <NUM> may be chosen such that it does not form a continuous layer, which would break or otherwise inhibit the exchange coupling between adjacent ferromagnetic regions. Instead, the material of insertion region <NUM> may mix with the materials of the adjacent ferromagnetic regions <NUM>, <NUM> and <NUM>, <NUM> to form a uniform layer, or may form a layer that is not continuous, so that the adjacent ferromagnetic regions <NUM>, <NUM> and <NUM>, <NUM> are directly exchange coupled to each other and the entire structure acts as a single ferromagnetic "free" region of stack <NUM>. In general, the thickness of the insertion region <NUM> may be between approximately <NUM> - <NUM>Å (preferably approximately <NUM> - <NUM>Å, or more preferably between approximately <NUM> - <NUM>Å). In some embodiments, the as-deposited thickness of the insertion region <NUM> may be less than approximately <NUM>Å, or between approximately <NUM>Å and <NUM>Å, or approximately <NUM>Å.

With continuing reference to <FIG>, in some embodiments, region <NUM>, which may include a boron-containing ferromagnetic alloy, may be provided as part of the "free" region <NUM>. Although not a requirement, in some embodiments, as illustrated in <FIG>, region <NUM> may be provided between the ferromagnetic region <NUM> and intermediate region <NUM> (which, as explained above, may include a dielectric material and may function as a tunnel barrier in an MTJ stack <NUM>). Region <NUM> may comprise a boron alloy having between about <NUM> at. % or greater and less than about <NUM> at. % of boron, and preferably between approximately <NUM> to <NUM> at. % of boron, and more preferably between approximately <NUM> to <NUM> at. % of boron. In some embodiments, region <NUM> may consist essentially of approximately <NUM> at. % of boron and the remainder may be iron (i.e., FeB50 in atomic percent). In some embodiments, the boron alloy of region <NUM> may have an amorphous crystal structure. In some embodiments, the material of region <NUM> may also include additional elements to improve the magnetic and other properties of the region <NUM>. In some embodiments, region <NUM> may include any suitable composition of boron that is less than <NUM> at. Stated differently, region <NUM> may not include only pure boron. In general, region <NUM> may have any thickness. In some embodiments, the thickness of region <NUM> may be between approximately <NUM> - <NUM>Å (preferably approximately <NUM> - <NUM>Å, or more preferably between approximately <NUM> - <NUM>Å).

Experimental studies have indicated that a "free" region <NUM> formed by depositing a boron-containing region (such as, e.g., region <NUM> of <FIG>) adjacent to ferromagnetic regions formed of a boron-free ferromagnetic alloy (such as, e.g., regions <NUM>, <NUM>) may improve the performance of the resulting magnetoresistive stack <NUM> (especially at relatively high temperatures (e.g., approximately <NUM>) in embedded MRAM applications) as compared to an exemplary "free" region <NUM> where the ferromagnetic regions are formed using a boron containing ferromagnetic alloy (e.g., CoFeB) (i.e., without a separate boron-containing alloy adjacent to a boron-free alloy - similar to regions <NUM> and <NUM> of <FIG>). It was found that increasing the concentration of boron in region <NUM> may increase defects (e.g., shorts, etc.) and may reduce performance and yield of the magnetoresistive stack <NUM>. Moreover, at increased concentrations (such as, e.g., pure boron), boron sputtering targets are known to be porous (e.g., having a density of approximately <NUM>% of theoretical bulk density even if the targets are fabricated at high temperatures and pressures). Sputter depositing a boron-containing region (such as region <NUM>) using a porous sputtering target may generate a large number of particles and may result in an increase in electrical shorts and other defects in the resulting magnetoresistive stack <NUM>.

To study the effect of boron concentration on defects, boron alloy films (such as region <NUM>) formed by sputter targets having different boron concentrations were evaluated. During these studies, it was found that as the boron concentration in the targets increased, the number of particles (an indicator of defects in the resulting magnetoresistive stack <NUM>) also increased. It was found that the density of the boron sputtering target decreased dramatically as boron content increased above about <NUM> at. %, and even more dramatically as the boron content increased above about <NUM> at. For example, these studies indicated that a <NUM>Å thick film comprising about <NUM> at. % boron and the remainder being iron (i.e., FeB60 in atomic percent) had a particle count of about <NUM>, while a <NUM>Å FeB50 (in atomic percent) film had a particle count of only about <NUM>, and an FeB50 (in atomic percent) film having a thickness between about <NUM>-<NUM>Å had a particle count of between about <NUM>-<NUM>. It should be noted that, in some embodiments of stack <NUM>, region <NUM> comprising an iron-boron (FeB) alloy may be less than about <NUM>Å thick, and therefore should have lower particle count and defect density. The magnetic properties (such as, for example, MR ratio, resistance-area product or RA, perpendicular magnetic anisotropy (PMA), etc.) of the "free" region <NUM> with region <NUM> comprising an FeB alloy (e.g., FeB50 (in atomic percent)) at room temperature was also found to be similar to or better than a "free" region <NUM> without region <NUM> (i.e., where the ferromagnetic regions are formed of CoFeB). Based on these studies, it was determined that a boron concentration of greater than, or equal to, approximately <NUM> at. % and less than <NUM> at. % in the boron-containing region <NUM> (preferably between approximately <NUM> to <NUM> at. %, and more preferably between approximately <NUM> to <NUM> at. %) will improve the performance of the magnetoresistive stack <NUM>.

With continuing reference to <FIG>, after forming "free" region <NUM> as described above, a second intermediate region <NUM> may be formed on or above the "free" region <NUM>. In embodiments of magnetoresistive stack <NUM> used in an MTJ device, both regions <NUM> and <NUM> may include a dielectric material and may function as a tunnel barrier. In some embodiments, intermediate region <NUM> may include the same material as intermediate region <NUM>. However, this is not a limitation, and in some embodiments, regions <NUM> and <NUM> may include different dielectric materials. For example, region <NUM> may include MgOx and region <NUM> may include AlOx (e.g., Al<NUM>O<NUM>). In some embodiments, region <NUM> also may be similar in thickness to region <NUM>. In other embodiments, region <NUM> may have a thickness that is larger or smaller than the thickness of region <NUM>. In some embodiments, region <NUM> may have a thickness between approximately <NUM> - <NUM>Å, preferably between approximately <NUM> - <NUM>Å, and more preferably between approximately <NUM> - <NUM>Å. Although not illustrated in <FIG>, in some embodiments, a dusting of an interfacial material (e.g., iridium, chromium, etc.) may also be provided at the interface between the "free" region <NUM> and the second intermediate region <NUM>. This interfacial material, deposited as, e.g., a discontinuous patchwork of material (as opposed to a continuous layer that would break exchange between the mating layers), may result in a high perpendicular magnetic anisotropy (PMA) of the resulting magnetoresistive stack <NUM>. Moreover, those of ordinary skill in the art also will recognize that region <NUM> also may include a non-magnetic conductive material, such as, e.g., Copper.

A second "fixed" region <NUM> may be formed on or above intermediate region <NUM>. Although "fixed" region <NUM> is illustrated as a single layer in <FIG>, "fixed" region <NUM> may also include a multi-layered structure similar to that described with reference to "fixed" region <NUM>. In some embodiments, a spacer region <NUM> and a capping region <NUM> may be formed above the second "fixed" region <NUM>, and electrode <NUM> may be formed above the capping region <NUM>. The capping region <NUM> may be formed from any suitable conductive material ( for example, a suitable metallic material, including, but not limited to, tantalum, titanium, tungsten, etc.) and may have any suitable thickness between approximately <NUM> - <NUM>Å. In some embodiments, the thickness of the spacer region <NUM> may be between approximately <NUM> - <NUM>Å, or preferably between approximately <NUM> - <NUM>Å, or more preferably between approximately <NUM> - <NUM>Å. The spacer region <NUM> may be formed of a non-ferromagnetic material, such as, e.g., ruthenium or an alloy of ruthenium. In some embodiments, spacer region <NUM> may include cobalt, iron, boron, or an alloy thereof (e.g., CoFeB). In some embodiments, the spacer region <NUM> may be formed of a bilayer structure comprising Ru and/or a CoFeB layer. In some embodiments, the thickness of the spacer region <NUM> may be approximately <NUM> - <NUM>Å, or preferably approximately <NUM> - <NUM>Å, or more preferably approximately <NUM> - <NUM>Å.

As explained previously, the magnetoresistive stack <NUM> of <FIG> represents a dual spin filter structure where a "free" region <NUM> is formed between a first "fixed" region <NUM> and a second "fixed" region <NUM>. However, this structure is only exemplary. In some embodiments, the second "fixed" region <NUM> may be eliminated to form a magnetoresistive stack having a single MTJ (magnetic tunnel junction) structure. Further, the structures of "free" region <NUM> and the "fixed" regions <NUM> and <NUM> described with reference to <FIG> are only exemplary. For example, <CIT>; <CIT>; and <CIT>, each assigned to the Assignee of the current application and incorporated by reference in its entirety herein, disclose several exemplary magnetoresistive stacks, and methods of making such stacks. Specifically, "fixed" regions <NUM>, <NUM> and "free" region <NUM> may have any of the structures and configurations disclosed in these references. Additionally, a few exemplary alternate configurations of the "free" region <NUM> of <FIG> are described below.

As described above, the "free" region <NUM> of <FIG> may include a boron-containing region <NUM> deposited proximate boron-free ferromagnetic regions <NUM> and <NUM> to improve the performance of the resulting magnetoresistive stack <NUM> at relatively high temperatures, e.g., <NUM>, (as compared to an exemplary "free" region <NUM> where a boron containing ferromagnetic alloy (e.g., CoFeB) is directly deposited to form the ferromagnetic regions of the "free" region (similar to regions <NUM> and <NUM> of <FIG>)). The exact composition of the materials in "free" region <NUM> may depend upon the application. With reference to the structure of the "free" region <NUM> of <FIG>, in some embodiments, the "free" region <NUM> may include: an approximately <NUM> - <NUM>Å thick boron-containing region <NUM> comprising essentially of FeB50 (in atomic percent); ferromagnetic regions <NUM> and <NUM> both comprising a boron-free materials, such as, e.g., cobalt, iron, or an alloy of cobalt and iron of any relative composition (i.e., CoFex, where x is any value, e.g., approximately <NUM> at. %); an approximately <NUM>Å thick insertion region <NUM> including one or more of molybdenum, tantalum, tungsten, or zirconium; a ferromagnetic region <NUM> comprising a boron-containing ferromagnetic alloy such as, for example, CoFe55B25 in atomic percent; and an approximately <NUM>-<NUM>Å thick ferromagnetic region <NUM> comprising essentially of iron. In some embodiments, the boron-free materials of ferromagnetic regions <NUM> and <NUM> may include an alloy of cobalt and iron with cobalt in the range of approximately <NUM>-<NUM>% in atomic percent. It is also contemplated that substantially pure cobalt may be used as the boron-free material.

In the "free" region <NUM> of <FIG>, the boron-containing region <NUM> may be positioned between the intermediate region <NUM> (which is formed of a dielectric material in an MTJ structure) and the boron-free ferromagnetic region <NUM>. However, this is not a requirement. <FIG> are schematic illustrations of exemplary "free" regions 50A-<NUM> formed by two ferromagnetic regions (indicated in <FIG> as ferromagnetic region <NUM> (FM1) and ferromagnetic region <NUM>(FM2)) separated by a non-magnetic insertion region <NUM>. As illustrated in <FIG>, in ferromagnetic region FM1 of an exemplary "free" region 50A, the boron-containing region <NUM> is positioned between two boron-free ferromagnetic regions <NUM> and <NUM>. In some such embodiments, the "free" region 50A may include: an approximately <NUM>Å thick ferromagnetic region <NUM> including iron, cobalt, or an iron-cobalt alloy; an approximately <NUM>-<NUM>Å thick boron-containing region <NUM> including, e.g., FeB50 in atomic percent; a ferromagnetic region <NUM> comprising a boron-free material such as, e.g., iron, cobalt, or an alloy of cobalt and iron of any relative composition (i.e., CoFex, x is from <NUM> to <NUM> atomic percent); an approximately <NUM>Å thick insertion region <NUM> including one or more of molybdenum, tantalum, tungsten, hafnium, zirconium, or an alloy of these materials; a ferromagnetic region <NUM> comprising a boron-containing ferromagnetic alloy such as, for example, CoFe55B25 in atomic percent; and an approximately <NUM>-<NUM>Å thick ferromagnetic region <NUM> including at least iron. In some embodiments, one or more elements of the boron-containing region may be selected from iron or cobalt and others.

<FIG> illustrates another exemplary "free" region 50B of a magnetoresistive stack <NUM>. As illustrated in <FIG>, a ferromagnetic region (e.g., FM1) of the "free" region 50B may include a boron-containing region <NUM> (such as, for example, comprising FeB50 or another alloy of iron and boron having a boron concentration above <NUM> at. %, or between <NUM> and <NUM> at. %) provided between the insertion region <NUM> and the boron-free ferromagnetic region <NUM>. In some such embodiments, the "free" region 50B may include: an approximately <NUM>Å thick ferromagnetic region <NUM> comprising iron, cobalt, or an iron-cobalt alloy; a ferromagnetic region <NUM> comprising a boron-free material such as, e.g., iron, cobalt, or an alloy of cobalt and iron of any relative composition (i.e., CoFex, x is from <NUM> to <NUM> atomic percent); an approximately <NUM> - <NUM>Å thick boron-containing region <NUM> comprising essentially of FeB50; an approximately <NUM>Å thick insertion region <NUM> including molybdenum, tantalum, tungsten, zirconium, etc.); a ferromagnetic region <NUM> comprising a boron-containing ferromagnetic alloy such as, for example, CoFe55B25; and an approximately <NUM>-<NUM>Å thick ferromagnetic region <NUM> including at least iron. In <FIG>, the boron-containing region <NUM> that was provided between the boron-free ferromagnetic regions <NUM> and <NUM> in <FIG> is depicted as being positioned between regions <NUM> and <NUM>. However, this is only exemplary. In some embodiments, a boron-containing region (e.g., such as region <NUM>) may be provided both between regions <NUM> and <NUM> and regions <NUM> and <NUM> (and in some embodiments, also between regions <NUM> and <NUM>).

Although in the description above, both sides of the insertion region <NUM> are described as including a pair of ferromagnetic regions (<NUM>/<NUM> and <NUM>/<NUM>), this is only exemplary. In general, any number (<NUM>, <NUM>, <NUM>, <NUM>, etc.) of ferromagnetic regions may be positioned on either side of the insertion region <NUM>. In some embodiments, as illustrated in <FIG>, "free" region 50C may include boron-free ferromagnetic regions <NUM> and <NUM> positioned proximate to a boron-containing region <NUM> located on one side of an insertion region <NUM>, and a single boron-containing ferromagnetic region <NUM> positioned on the opposite side of the insertion region <NUM>. Similarly, in some embodiments, a "free" region 50C may include a single boron-free ferromagnetic region <NUM> positioned proximate to a boron-containing region <NUM> on one side of the insertion region <NUM>, and a single boron-containing ferromagnetic region <NUM> positioned on the opposite side of the insertion region <NUM>. With reference to the "free" region 50C of <FIG>, in some embodiments, region <NUM> may be approximately <NUM>Å thick and include iron, cobalt, or an alloy thereof; region <NUM> may include boron-free material such as, e.g., iron, cobalt, or an alloy of cobalt and iron of any relative composition (i.e., CoFex, x is from <NUM> to <NUM> atomic percent); region <NUM> may include an approximately <NUM> - <NUM>Å thick alloy of iron and boron (such as, for example, FeB50), region <NUM> may include an approximately <NUM>Å thick layer of one or more of molybdenum, tantalum, tungsten, zirconium, etc.; and region <NUM> may include a boron-containing ferromagnetic alloy (such as, for example, CoFe55B25 in atomic percent) of any thickness.

In some embodiments, a boron-containing region (such as region <NUM>) may additionally, or alternatively, be positioned proximate to the ferromagnetic regions (e.g., FM2 or regions <NUM>, <NUM>) above (in the relative orientation of, e.g., <FIG>) the insertion region <NUM>. For example, as illustrated in <FIG>, in some embodiments, a "free" region 50D or 50E may include: boron-containing ferromagnetic regions <NUM> and <NUM> (such as, for example, regions <NUM> and <NUM> may both include a cobalt-iron-boron alloy, e.g., CoFe55B25 in atomic percent, or region <NUM> or region <NUM> may include exclusively or predominantly iron or cobalt, and the other of region <NUM> and region <NUM> may include a cobalt-iron-boron alloy, e.g., CoFe55B25 in atomic percent) located on one side (e.g., below in the orientation of <FIG>) of an insertion region <NUM>, and a boron-free ferromagnetic region <NUM> (e.g., cobalt, iron, or a cobalt-iron alloy e.g., CoFex , x is from <NUM> to <NUM> atomic percent) positioned proximate to a boron-containing region <NUM> (e.g., FeB50 in atomic percent) on the opposite side of insertion region <NUM>. The boron-containing region <NUM> may be positioned above the boron-free ferromagnetic region <NUM> as illustrated in <FIG> or below region <NUM> (i.e., between the insertion region <NUM> and region <NUM>) as illustrated in <FIG>. In some embodiments, the boron-free ferromagnetic region <NUM> may comprise a cobalt-iron alloy (CoFex, x is from <NUM> to <NUM> atomic percent), and in some embodiments, region <NUM> may include exclusively or predominantly cobalt or iron.

In some embodiments, as illustrated in <FIG>, a "free" region 50F or <NUM> may include boron-containing ferromagnetic regions <NUM> and <NUM> (such as, for example, regions <NUM> and <NUM> may both include a cobalt-iron-boron alloy, e.g., CoFe55B25 in atomic percent, or region <NUM> or region <NUM> may include exclusively or predominantly iron or cobalt, and the other of region <NUM> and region <NUM> may include a cobalt-iron-boron alloy, e.g., CoFe55B25 in atomic percent) located on one side (e.g., below in the orientation of <FIG>) of an insertion region <NUM>, and boron-free ferromagnetic regions <NUM> and <NUM> (e.g., CoFex or Fe) positioned proximate a boron-containing region <NUM> (e.g., FeB50) on the opposite side of the insertion region <NUM>. In some embodiments, as illustrated in <FIG>, the boron-containing region <NUM> may be positioned between the boron-free ferromagnetic regions <NUM> and <NUM>, and in some embodiments, the boron-containing region <NUM> may be positioned below the boron-free ferromagnetic regions <NUM> and <NUM> (i.e., between the insertion region <NUM> and region <NUM>). Alternatively, or additionally, in some embodiments, the boron-containing region <NUM> may be positioned above the boron-free ferromagnetic regions <NUM> and <NUM> of <FIG>. That is, the boron-containing region <NUM> may be disposed between boron-free ferromagnetic region <NUM> and second intermediate region <NUM>.

It should be noted that although the boron-containing region <NUM> is illustrated as being positioned only on one side of the insertion region <NUM> (i.e., FM1 or FM2) in the embodiments of the "free" regions discussed above, this is only exemplary. In some embodiments, as will be described in more detail below, both FM1 and FM2 (i.e., the ferromagnetic regions above and below the insertion region <NUM>) of "free" region may include a boron-containing region <NUM> positioned proximate to a ferromagnetic region. It should also be noted that the above-described compositions and thicknesses of the various regions are only exemplary. For example, although the boron-containing region <NUM> is described as comprising FeB50 in atomic percent, this is only exemplary. In general, region <NUM> may include any alloy of iron and boron having a boron concentration above <NUM> at. %, or between <NUM> and <NUM> at. In some embodiments, region <NUM> may include any alloy of iron and boron having a boron concentration less than <NUM> at. It is contemplated that, in some embodiments, a boron-containing region (e.g., a high-boron alloy) and a boron-free region may be used in other layers of the MTJ stack, such as, for example, the reference layer.

It should be emphasized that the compositions and thicknesses of the regions described herein are as-deposited values. In some embodiments, these described values are those that are seen immediately after deposition. In some embodiments, the described thicknesses and compositions are the target thicknesses and the composition of the sputter targets used in the deposition of the various regions. As known to those of ordinary skill in the art, experimental variations in these thicknesses and compositions can be expected. Further, as known to those of ordinary skill in the art, over time and/or exposure to high temperatures (such as, for example, during annealing, etc.), the materials of the various regions of the "free" regions <NUM>, 50A, 50B, etc. may alloy with each other to form a more homogenous structure without distinct interfaces demarcating the different regions. In such a structure, boron from the boron-containing region <NUM> may alloy with, and diffuse, into adjacent boron-free ferromagnetic regions (e.g., regions <NUM> and <NUM> in the embodiments of <FIG> and regions <NUM> and/or <NUM> in the embodiments of <FIG>). As a result of such alloying, over time, regions that were formed by depositing a boron-free ferromagnetic alloy may include some amount of boron. However, an increased boron concentration at region <NUM> and/or a decreasing boron concentration from region <NUM> towards the originally boron-free magnetic alloy may still be noticeable in the structure upon analysis.

As explained above, in some embodiments, the ferromagnetic regions (i.e., FM1 and FM2) on either side of the insertion region <NUM> may include an amorphous boron-containing or boron-rich region (such as, e.g., region <NUM>) positioned proximate crystalline (or non-amorphous) boron-free (or boron-lean, in some cases) ferromagnetic regions (e.g., regions <NUM>, <NUM>) to improve the performance of the resulting magnetoresistive stack <NUM> at relatively high temperatures. In some embodiments, one or both the ferromagnetic regions (i.e., FM1 and FM2) on either side of insertion region <NUM> may include a multi-layer structure of a crystalline (or non-amorphous) magnetic material and an amorphous magnetic material. The crystalline magnetic material may include a boron-free (or boron-lean, in some embodiments) ferromagnetic material and the amorphous magnetic material may include a boron-rich ferromagnetic material. In some embodiments, the crystalline boron-free ferromagnetic material may include at least one of iron (Fe), cobalt (Co), or an alloy of cobalt and iron (CoFe), and the amorphous boron-rich ferromagnetic material may include an alloy of iron and boron (FeB), an alloy of cobalt and boron (CoB), or an alloy of cobalt, iron, and boron (CoFeB).

<FIG> illustrate exemplary "free" regions <NUM>-50J of a magnetoresistive stack <NUM> where the ferromagnetic regions (i.e., FM1 and FM2) on both sides of the insertion region <NUM> includes alternating amorphous boron-rich and crystalline boron-lean (or boron-free) regions. In some embodiments, as illustrated in "free" region <NUM> of <FIG>, ferromagnetic regions (FM1 and FM2) on both sides of insertion region <NUM> may include an amorphous boron-rich region <NUM> positioned between two crystalline boron-free regions <NUM>, <NUM>. In some embodiments, as illustrated in <FIG>, ferromagnetic region <NUM> (FM1) may include an amorphous boron-rich region <NUM> positioned next to a crystalline boron-free region <NUM> (which is positioned adjacent to the insertion region <NUM>), and ferromagnetic region <NUM> (FM2) may include an amorphous boron-rich region <NUM> positioned between two crystalline boron-free regions <NUM>, <NUM>. With reference to ferromagnetic region <NUM> (FM1), the boron-rich region <NUM> may be positioned below the boron-free region <NUM> (see "free" region 50I of <FIG>) or above the boron-free region <NUM> (see "free" region 50J of <FIG>). In some embodiments, the ferromagnetic region above the insertion region <NUM> (i.e., FM2) may have a configuration as illustrated in <FIG> and the ferromagnetic region below the insertion region <NUM> (i.e., FM1) may have the configuration of FM1 in <FIG>. It should be noted that, in some embodiments, regions <NUM>, <NUM> and/or <NUM> above and below insertion region <NUM> may have different thicknesses based on device performance requirements.

In some embodiments, the amorphous boron-rich region <NUM> of <FIG> may include any one or more of the following alloys: (a) an alloy of iron (Fe) and boron (B) having a composition FeX,B<NUM>-X; (b) an alloy of cobalt (Co) and boron (B) having a composition CoXB<NUM>-X; (c) an alloy of a cobalt-iron alloy (CoFe) and boron having a composition (CoFe)XB<NUM>-X; (d) or an alloy of cobalt, iron, and an element M (CoFeM, where element M is one of tantalum (Ta), hafnium (Hf), zirconium (Zr), or chromium (Cr)) alloyed with boron (B) having a composition (CoFeM)XB<NUM>-X. In the above described alloys, X may be between <NUM> and <NUM> (in atomic percent). In some embodiments, the non-amorphous (or crystalline) boron-free region <NUM>, <NUM> of ferromagnetic region <NUM> (FM1) and ferromagnetic region <NUM> (FM2) may be an alloy of iron and cobalt (CoFe) having a composition CoXFe<NUM>-X, where X is between <NUM> and <NUM> in atomic percent. The configurations of "free" regions discussed above may result in a low switching voltage and a relatively higher energy barrier. The switching voltage and energy barrier may be tuned by adjusting the non-amorphous alloy's composition and thickness, as well as amorphous B-rich regions' alloy composition and thickness, as desired.

As alluded to above, magnetoresistive stack <NUM> may be implemented in a sensor architecture or a memory architecture (among other architectures). For example, in a memory configuration, the magnetoresistive stack <NUM> may be electrically connected to an access transistor and configured to couple or connect to various conductors, which may carry one or more control signals, as shown in <FIG>. The magnetoresistive stack <NUM> of the current disclosure may be used in any suitable application, including, e.g., in a memory configuration. In such instances, the magnetoresistive stack <NUM> may be formed as an integrated circuit comprising a discrete memory device (e.g., as shown in <FIG>) or an embedded memory device having a logic therein (e.g., as shown in <FIG>), each including MRAM, which, in one embodiment is representative of one or more arrays of MRAM having a plurality of magnetoresistive stacks, according to certain aspects of certain embodiments disclosed herein.

Exemplary methods of fabricating selected embodiments of the disclosed magnetoresistive stack <NUM> (e.g., magnetoresistive stack <NUM> of <FIG>) will now be described. It should be appreciated that the described methods are merely exemplary. In some embodiments, the methods may include a number of additional or alternative steps, and in some embodiments, one or more of the described steps may be omitted. Any described step may be omitted or modified, or other steps added, as long as the intended functionality of the fabricated magnetoresistive stack/structure remains substantially unaltered. Further, although a certain order is described or implied in the described methods, in general, the steps of the described methods need not be performed in the illustrated and described order. Further, the described methods may be incorporated into a more comprehensive procedure or process having additional functionality not described herein.

<FIG> depicts a flow chart of an exemplary method <NUM> of fabricating magnetoresistive stack <NUM> according to the present disclosure. In the discussion below, reference will be made to both <FIG> and <FIG>. A first electrode (e.g., bottom electrode <NUM>) may be first formed on the backend (surface with circuitry) of a semiconductor substrate <NUM> by any suitable process (step <NUM>). A "fixed" region <NUM> then may be formed on or above an exposed surface of electrode <NUM> (step <NUM>). In some embodiments, "fixed" region <NUM> may be formed by providing (e.g., sequentially) the different regions (e.g., regions <NUM>, <NUM>, <NUM>, <NUM>, and <NUM>) that comprise the "fixed" region <NUM> on the surface of electrode <NUM>. An intermediate region <NUM> then may be formed on or above an exposed surface of the "fixed" region <NUM> (step <NUM>). A "free" region <NUM> may be formed on or above the exposed surface of the intermediate region <NUM> (step <NUM>). In some embodiments, the "free" region <NUM> may be formed by first providing a boron-containing alloy, such as, for example, FeB50 (in atomic percent), on the exposed surface of the intermediate region <NUM> to form region <NUM> (step <NUM>), and then providing one or more boron-free ferromagnetic alloys (such as, for example, CoFex, x is from <NUM> to <NUM> atomic percent) on the exposed surface of region <NUM> to form regions <NUM> and <NUM> (step <NUM>). Next, an insertion region <NUM> is formed by providing a layer of molybdenum (or tantalum, tungsten, or zirconium) on or above the exposed surface of the boron-free ferromagnetic region <NUM> (step <NUM>). One or more boron-containing ferromagnetic alloys (such as, for example, CoFe55B25 in atomic percent) are then provided on the exposed surface of region <NUM> to form regions <NUM> and <NUM> (step <NUM>). In some embodiments, as described in connection with <FIG> above, free region <NUM> may be formed by providing (e.g., depositing) alternating amorphous boron-rich and crystalline boron-lean (or boron-free) regions on one or both sides of the insertion region <NUM>. A dielectric material may then be provided on the exposed surface of the "free" region <NUM> to form second intermediate region <NUM> (step <NUM>), and a second "fixed" region <NUM> may be formed on the exposed surface of region <NUM> (step <NUM>). Similar to step <NUM> above, the "fixed" region <NUM> may be formed by sequentially providing the different regions that comprise the "fixed" region <NUM> on the surface of intermediate region <NUM>. A spacer region <NUM> and a capping region <NUM> may be formed on or above (i.e., on an exposed surface of) the "fixed" region <NUM> (step <NUM>), and the second electrode <NUM> formed on the exposed surface of region <NUM> (step <NUM>). It should be noted that, in some embodiments, some of the above described steps (or regions) may be eliminated to form other embodiments of magnetoresistive stacks. For example, to form an exemplary magnetoresistive stack having a single MTJ structure, step <NUM> may be eliminated.

Any suitable method may be used to form the different regions of the magnetoresistive stack <NUM>. Since suitable integrated circuit fabrication techniques (e.g., deposition, sputtering, evaporation, plating, etc.) that may be used to form the different regions are known to those of ordinary skill in the art, they are not described here in great detail. In some embodiments, forming some of the regions may involve thin-film deposition processes, including, but not limited to, physical vapor deposition techniques such as ion beam sputtering and magnetron sputtering. And, forming thin insulating layers (e.g., intermediate regions <NUM> and <NUM>, which form tunnel barrier layers) may involve physical vapor deposition from an oxide target, such as by radio-frequency (RF) sputtering, or by deposition of a thin metallic film followed by an oxidation step, such as oxygen plasma oxidation, oxygen radical oxidation, or natural oxidation by exposure to a low-pressure oxygen environment.

In some embodiments, formation of some or all of the regions of magnetoresistive stack <NUM> may also involve known processing steps such as, for example, selective deposition, photolithography processing, etching, etc., in accordance with any of the various conventional techniques known in the semiconductor industry. In some embodiments, during deposition of the disclosed "fixed" and "free" regions, a magnetic field may be provided to set a preferred easy magnetic axis of the region (e.g., via induced anisotropy). Similarly, a strong magnetic field applied during the post-deposition high-temperature anneal step may be used to induce a preferred easy axis and a preferred pinning direction for any antiferromagnetically pinned materials.

In one aspect, a magnetoresistive device is disclosed. The magnetoresistive device may include an intermediate region, a magnetically fixed region on one side of the intermediate region, and a magnetically free region on an opposite side of the intermediate region. The magnetically free region may include at least a first ferromagnetic region and a second ferromagnetic region separated by a non-magnetic insertion region. At least one of the first ferromagnetic region and the second ferromagnetic region may include at least a boron-rich ferromagnetic layer positioned proximate to a boron-free ferromagnetic layer.

Various embodiments of the disclosed magnetoresistive device may alternatively or additionally include one or more of the following aspects: the boron-free ferromagnetic layer may include an alloy of cobalt and iron; the boron-free ferromagnetic layer may include an alloy of cobalt and iron having a composition between approximately <NUM>-<NUM>% atomic percent of cobalt; the boron-rich ferromagnetic layer may include an alloy of iron and boron; the boron-rich ferromagnetic layer may include an alloy of boron having a composition between approximately <NUM>-<NUM>% atomic percent of boron; the boron-free ferromagnetic layer may include an alloy of cobalt and iron having a composition between approximately <NUM>-<NUM>% atomic percent of cobalt, and the boron-rich ferromagnetic layer may include an alloy of iron and boron having a composition between approximately <NUM>-<NUM>% atomic percent of boron; the boron-free ferromagnetic layer may include an alloy of at least cobalt and iron and have a crystalline microstructure, and the boron-rich ferromagnetic layer may include an alloy of at least iron and boron and have an amorphous microstructure; at least one of the first ferromagnetic region and the second ferromagnetic region may include at least a boron-rich ferromagnetic layer positioned between two boron-free ferromagnetic layers; the boron-free ferromagnetic layer may include an alloy of iron and cobalt having a composition CoXFe<NUM>-X, where X is between <NUM> and <NUM> (in atomic percent); the boron-rich ferromagnetic layer may include one or more of (a) an alloy of iron and boron having a composition FeXB<NUM>-X, (b) an alloy of cobalt and boron having a composition CoXB<NUM>-X, (c) an alloy of a cobalt-iron alloy and boron having a composition (CoFe)XB<NUM>-X, and (d) an alloy of cobalt, iron, and an element M, where element M is one of tantalum, hafnium, zirconium, or chromium, and boron having a composition (CoFeM)XB<NUM>-X, and wherein X is between <NUM> and <NUM> (in atomic percent); both the first ferromagnetic region and the second ferromagnetic region includes at least a boron-rich ferromagnetic layer positioned proximate to a boron-free ferromagnetic layer; each of the first ferromagnetic region and the second ferromagnetic region may include at least a boron-rich ferromagnetic layer positioned between two boron-free ferromagnetic layers; each of the first ferromagnetic region and the second ferromagnetic region includes at least a boron-rich ferromagnetic layer positioned proximate a boron-free ferromagnetic layer, and wherein the boron-rich ferromagnetic layer includes one or more of (a) an alloy of iron and boron having a composition FeXB<NUM>-X, (b) an alloy of cobalt and boron having a composition CoXB<NUM>-X, (c) an alloy of a cobalt-iron alloy and boron having a composition (CoFe)XB<NUM>-X, and (d) an alloy of cobalt, iron, and an element M, where element M is one of tantalum, hafnium, zirconium, or chromium, and boron having a composition (CoFeM)XB<NUM>-X, and wherein X is between <NUM> and <NUM> (in atomic percent); and each of the first ferromagnetic region and the second ferromagnetic region includes at least a boron-rich ferromagnetic layer positioned proximate to a boron-free ferromagnetic layer, and the boron-free ferromagnetic layer may include an alloy of iron and cobalt having a composition CoXFe<NUM>-X, where X is between <NUM> and <NUM> (in atomic percent).

In some aspects, a magnetoresistive device is disclosed. The magnetoresistive device may include an intermediate region, a magnetically fixed region on one side of the intermediate region, and a magnetically free region on an opposite side of the intermediate region. The magnetically free region may include at least a first ferromagnetic region and a second ferromagnetic region separated by a non-magnetic insertion region. At least one of the first ferromagnetic region and the second ferromagnetic region may include at least a boron-rich ferromagnetic layer positioned proximate to a boron-free ferromagnetic layer. The boron-rich ferromagnetic layer may include one or more of (a) an alloy of iron and boron having a composition FeXB<NUM>-X, (b) an alloy of cobalt and boron having a composition CoXB<NUM>-X, (c) an alloy of a cobalt-iron alloy and boron having a composition (CoFe)XB<NUM>-X, and (d) an alloy of cobalt, iron, and an element M, where element M is one of tantalum, hafnium, zirconium, or chromium, and boron having a composition (CoFeM)XB<NUM>-X, and wherein X is between <NUM> and <NUM>. And, the boron-free ferromagnetic layer may include an alloy of iron and cobalt having a composition CoXFe<NUM>-X, where X is between <NUM> and <NUM> (in atomic percent).

Various embodiments of the disclosed magnetoresistive device may alternatively or additionally include one or more of the following aspects: the boron-free ferromagnetic layer may include between approximately <NUM>-<NUM>% atomic percent of cobalt; the boron-rich ferromagnetic layer may include between approximately <NUM>-<NUM>% atomic percent of boron; the boron-free ferromagnetic layer may include between approximately <NUM>-<NUM>% atomic percent of cobalt, and the boron-rich ferromagnetic layer may include between approximately <NUM>-<NUM>% atomic percent of boron; each of the first ferromagnetic region and the second ferromagnetic region may include at least a boron-rich ferromagnetic layer positioned proximate to a boron-free ferromagnetic layer; and at least one of the first ferromagnetic region and the second ferromagnetic region may include at least a boron-rich ferromagnetic layer positioned between two boron-free ferromagnetic layers.

Claim 1:
A magnetoresistive device (<NUM>), comprising:
an intermediate region (<NUM>), wherein the intermediate region (<NUM>) includes at least one dielectric layer that forms a tunnel barrier;
a magnetically fixed region (<NUM>; <NUM>) on one side of the intermediate region (<NUM>); and
a magnetically free region (<NUM>) on an opposite side of the intermediate region (<NUM>), wherein the magnetically free region (<NUM>) includes at least a first ferromagnetic region (<NUM>: <NUM>) and a second ferromagnetic region (<NUM>; <NUM>) separated by a non-magnetic insertion region (<NUM>), wherein one of the first ferromagnetic region (<NUM>; <NUM>) and the second ferromagnetic region (<NUM>; <NUM>) includes at least a boron-rich ferromagnetic layer and at least one boron-free ferromagnetic layer, and wherein another of the first ferromagnetic region (<NUM>; <NUM>) and the second ferromagnetic region (<NUM>; <NUM>) includes a boron-containing ferromagnetic layer and a ferromagnetic layer including iron or cobalt contacting each other, characterized in that the boron-rich ferromagnetic layer is in direct contact with the tunnel barrier of the intermediate region (<NUM>).