Patent Description:
Heads and handles for oral care implements, like manual toothbrushes, are well known in the art. Generally, tufts of bristles for cleaning teeth are attached to a bristle carrier or mounting surface of the brush head intended for insertion into a user's oral cavity. The handle is usually attached to the head, which handle is held by a user during brushing. Usually, manual toothbrushes are made of relatively light materials, e.g. polypropylene, optionally in combination with thermoplastic elastomers. Typically, these thermoplastic elastomers form gripping members on the handle of the toothbrush, e.g. a thumb rest improving gripping properties. However, due to the lightweight handle, the axis of rotation of said manual toothbrushes is below the center of gravity, in particular when the toothbrush is loaded with toothpaste. If the axis of rotation is below the center of gravity, the toothbrush is in an instable/unbalanced position when the brush is placed on a substantially flat surface. The brush can easily rotate aside/tip to the side, and toothpaste may soil the surface onto which the brush has been placed. To prevent the loaded toothbrush from tipping to the side, additional geometrical structures, like roll stops are necessary. Toothbrushes are known having such roll stops in the form of edges attached to the handle or to the head. However, such additional edges are uncomfortable in the hand/in the mouth during brushing.

Further, brushes comprising relatively light handles, in particular handles being made of common plastic materials, e.g. polypropylene, provide low product quality perception during use of the brushes.

Additionally, in order to clean teeth effectively, appropriate maneuverability and good handling properties of the overall toothbrush have to be provided, which properties, inter alia, depend on the bending stiffness of the handle and the brush head. Usually handles of toothbrushes have the shape of a linear rod to be handled and manipulated by a user as needed. It has been seen in the past that manual toothbrushes with lightweight handles, e.g. made of polypropylene, are neither comfortable to handle nor easy to maneuver in the oral care cavity. Further, bending stiffness of such handles is relatively low. They tend to flex away easily and the relatively low bending stiffness results in reduced plaque removal efficiency on teeth surfaces. Further, such handles provide poor maneuverability in the mouth during brushing. In order to compensate said low bending stiffness, the size of the cross-sectional area of the handle could be increased. However, relatively thick handles may also reduce ease of rotating the brush in the hand, thus, impeding the user reaching all areas in the oral cavity. Consequently, maneuverability of the overall brush is not sufficient. However, in order to achieve and preserve good oral health, and to prevent gingivitis, it is important to clean teeth and gums thoroughly, in particular in hard to reach areas, e. in the region of the back molars. Further, gaps between teeth and periodontium, the so called gingival groove has to be thoroughly cleaned which requires a good and well-coordinated brushing technique, which may not be achievable by using the above-mentioned manual toothbrushes. Further, it is known that users/consumers use different brushing techniques, and, therefore, it is critical to identify optimal ergonomics of a toothbrush in order to provide good sensory feeling during brushing when using all types of brushing techniques.

<CIT> discloses a toothbrush constructed to have a self-righting tendency to elevate a brush head portion to avoid contamination form a support surface.

<CIT> discloses a method for forming a molded article comprising (a) metering a polymer composition to a mold defining cavity, and (b) holding the mold under pressure to cool to form an article, wherein the polymer composition comprises a polymer material and a thermally conductive filler.

<CIT>discloses an oral care implement having an adjustable mass centroid.

<CIT> discloses polymer material formed as a layer, the material having an non-organic filler.

It is an object of the present disclosure to provide an oral care implement which overcomes at least one of the above-mentioned drawbacks, in particular an oral care implement which does not rotate aside when loaded with toothpaste and placed on a substantially planar surface. Further, the oral care implement shall provide more comfort and improved quality perception as well as better maneuverability in the oral care cavity during brushing. It is also an object of the present disclosure to provide a method for manufacturing such oral care implement.

In accordance with one aspect an oral care implement is provided, the oral care implement having a front side and a back side opposite the front side, an overall length extension extending between a proximal end and a distal end, the distal end being opposite the proximal end, the oral care implement comprising a head at the proximal end and a handle, the head having at least one cleaning element extending from the front side, the handle being at least partially made from a material having a density being higher than the density of the material of the head, the handle having a cross-sectional area extending substantially perpendicular to the overall length extension of the oral are implement, the cross-sectional area having a height extension extending between the front side and the back side, the oral care implement having a center of gravity and an axis of rotation when the oral care implement is placed with the back side on a surface, wherein the center of gravity is below the axis of rotation and the center of gravity is closer to the back side than to the front side of the oral care implement when measured along the height extension of the handle. The material of the head is a non-magnetic and/or non-ferromagnetic material, preferably polypropylene; and the material of the handle comprises a magnetic and/or ferromagnetic material, comprising amorphous thermoplastic resin; iron oxide; and aluminium oxide, boron nitride or aluminium silicate.

In accordance with one aspect a kit is provided, the kit comprising such oral care implement and a holder for attaching and holding the oral care implement.

In accordance with one aspect, a method for manufacturing such oral care implement is provided, the method comprising the following steps:.

Further embodiments of the invention are defined in the dependent claims.

The oral care implement according to the present disclosure comprises a handle and a head on which at least one tooth cleaning element, e.g. a tuft of bristles and/or an elastomeric element, is fixed. The head may be repeatedly attachable to and detachable from the handle. Alternatively, the head may be permanently attached to the handle. The oral care implement may be a manual toothbrush. The oral care implement may also be an inter-proximal pick, a plaque scraper or tissue/tongue cleanser.

The oral care implement has a front side and a back side, the back side being opposite the front side. The front side is defined as the side from which the at least one tooth cleaning element extends. The oral care implement has an overall length extension extending between a proximal end, i.e. the end where the head with the at least one tooth cleaning element is located, and a distal end.

The handle has a cross sectional area which extends substantially perpendicular to the overall length extension of the oral care implement. The height extension of the cross-sectional area is defined as the maximum extension between the front side and the back side of the oral care implement.

The center of gravity of the oral care implement is located at a position which is closer to the back side than to the front side of the oral care implement, the position being measured along the height extension of the cross-sectional area of the handle. If the oral care implement is loaded with toothpaste and placed on a substantially planar/flat surface, the center of gravity is below the axis of rotation which renders the overall oral care implement stable and balanced. The oral care implement returns automatically to an upright position (i.e. into a position which keeps the toothpaste away from/opposite to the surface) once the oral care implement is moved out of the balanced position.

The center of gravity is located at a distance measured from the distal end of the oral care implement. The ratio of said distance measured from the distal end to the overall length extension of the oral care implement may be from about <NUM> to about <NUM>, or from about <NUM> to about <NUM>, or from about <NUM> to about <NUM>. Such ratio provides an oral care implement having the center of gravity closer to the center of the length extension of the handle, as compared to toothbrushes according to the state of the art. Consequently, when the user holds the oral care implement in his hand during brushing, the center of gravity is closer to the pivot point of the wrist joint enabling better control of the oral care implement in the mouth, thereby allowing more precise and accurate brushing movements. In other words, the center of gravity lies within the handle (even if the brush head is loaded with toothpaste), thereby enabling users to perform a well-coordinated brushing technique with improved sensory feeling during brushing. The center of gravity positioned substantially in the center of the handle renders the oral care implement balanced. The oral care implement does not easily tip over / cannot get head loaded once toothpaste is applied onto the brush head. When applying the different brushing techniques as shown in <FIG>, a balanced toothbrush has the advantage that the center of gravity is in or very close to the pivot point of the wrist joint, thereby enabling better cleaning.

The overall length extension of the oral care implement may be from about <NUM> to about <NUM>, or about <NUM>. The length extension of the handle may be <NUM>/<NUM> of the overall length extension of the oral care implement.

The handle of the oral care implement is at least partially made from a material having a higher density than the density of the material from which the head - optionally including the shaft/neck - is made. At least a portion of the head, e g. the neck/shaft and the bristle carrier may be made from a material having a density from about <NUM>/cm<NUM> to about <NUM>/cm<NUM>, or from about <NUM>/cm<NUM> to about <NUM>/cm<NUM>, or about <NUM>/cm<NUM>. For example, the head and the neck may be injection molded from a thermoplastic polymer, e.g. polypropylene having a density of about <NUM>/cm<NUM>. In contrast to the head, the handle is at least partially made from a material having a significant higher density, e.g. a density from about <NUM>/cm<NUM> to about <NUM>/cm<NUM>, or from about <NUM>/cm<NUM> to about <NUM>/cm<NUM>, or from about <NUM>/cm<NUM> to about <NUM>/cm<NUM>.

Usually, users are accustomed that products, in particular in the personal health care sector, have a specific weight that guarantees high product quality and provides comfortable feeling during use of the product. As the weight of the handle material is relatively high, the oral care implement according to the present disclosure provides such high-quality perception and comfortable feeling during use. The oral care implement according to the present disclosure provides superior product quality perception.

An oral care implement comprising a head being repeatedly attachable to and detachable from the handle provides several benefits: While the high quality and relatively expensive handle of the oral care implement is adapted for use over a longer period of time as compared to common manual toothbrushes which are discarded after about three months of use, the relatively cheap brush refill can be exchanged on a regular basis, e.g. after about three months. This provides a cost-efficient and environmentally sustainable high quality oral care implement with improved handling properties. The head of the oral care implement may be attachable to the handle via a snap-fit locking mechanism. For example, the handle may comprise a connector which may be insertable into a hollow portion in the head, or the head may comprise a connector inserable into a hollow portion in the handle. Alternatively, a connector may be provided as a further, i.e. separate part of the oral care implement. Such connector may be insertable into a hollow portion in the handle and into a hollow portion the head, respectively, thereby providing a sufficiently strong connection and sufficient stability between the head and the handle to enable a user to perform a brushing action.

In the past, it has been seen that after use of the brush/after brushing the teeth the user usually stores the wet brush in a toothbrush beaker for drying. However, in a classical toothbrush beaker, drained fluids get collected and accumulated at the bottom of the beaker, and the fluids stay in contact with the toothbrush for a longer period of time. Since the beaker is open on one side only, the toothbrush dries relatively slowly. Bacteria living in wet conditions/in a wet environment can grow quickly, contaminate the toothbrush and finally render the brush unhygienic. Consequently, there exists a need for a solution for hygienically storing and drying a manual toothbrush, thereby enabling remaining water, toothpaste slurry and saliva to drain off from the brush. The brush shall dry quickly thereby inhibiting bacterial growth.

The material of the head is made from a non-magnetic or non-ferromagnetic material, while the material of the handle is made from a magnetic and/or ferromagnetic material. Magnetic/ferromagnetic material possesses not only a relatively high density, and, thus, a relatively heavy weight, which provides the oral care implement with the above-mentioned benefits, but the magnetic/ferromagnetic material also makes the oral care implement magnetically attachable to a magnetic holder. The magnetic/ferromagnetic material of the handle may allow for hygienic storage of the oral care implement. If the oral care implement is magnetically attached to a magnetic holder, remaining water, toothpaste slurry and saliva can drain off from the brush. The oral care implement can dry relatively quickly. Consequently, bacteria growth can significantly be reduced, thereby rendering the oral care implement more hygienic. In contrast to a common toothbrush being stored in a toothbrush beaker where drained fluids get collected and accumulated at the bottom of the beaker, the brush according to the present disclosure is exposed to wet conditions over a significantly shorter period of time.

For example, the magnetic holder may have the form of a flat disk attachable to a wall. Such flat disk may represent an easy to clean surface. Further, a user just needs to bring the oral care implement in close proximity to the magnetic holder, and then the oral care implement gets attached automatically. No precise positioning or threading as with common toothbrush holders is required. Since the magnetic properties are merely provided in the handle, and not in the head, the head portion cannot accidentally be attached to the magnetic holder, thereby reducing the risk that the magnetic holder gets soiled.

The magnetic and/or ferromagnetic material forming at least a part of the handle may comprise an amorphous thermoplastic resin. The magnetic and/or ferromagnetic material may further comprise aluminium oxide, boron nitride or aluminium silicate. Furthermore, the magnetic and/or ferromagnetic material may comprise in addition or alternatively iron oxide. The magnetic and/or ferromagnetic material may further comprise glass fibers which may be pre-mixed with at least a portion of the amorphous thermoplastic resin. Such handle material allows for control of the weight of the handle in whatever location, e.g. by filler variation. Control of the overall toothbrush is required due to the relatively high weight of the handle. It is now possible to use the mass/weight distribution of the material for adaption of the inertial moment of the finished toothbrush.

The magnetic and/or ferromagnetic material may comprise from about <NUM> weight percent to about <NUM> weight percent of an amorphous thermoplastic resin; from about <NUM> weight percent to about <NUM> weight percent of aluminium oxide, boron nitride or aluminium silicate; and from about <NUM> weight percent to about <NUM> weight percent of iron oxide. Such composition provides a material density that is about three times the density of a standard plastic material used for toothbrushes, e.g. polypropylene. With the higher weight and higher thermal conductivity, the material drives value perception, in particular in combination with a galvanic coating. Such coating may be made from real metal. The galvanic coating can be applied in a selective electroplating process. During this coating process for a multicomponent plastic part, a metallic layer is only deposited on a hard material while a further over molded soft component may remain unaffected.

The magnetic and/or ferromagnetic material may comprise about <NUM> weight percent of an amorphous thermoplastic resin, about <NUM> weight percent of aluminium oxide, about <NUM> weight percent of iron oxide, and about <NUM>% glass fiber.

The amorphous thermoplastic resin may comprise a styrene resin, e.g. styrene acrylonitrile "SAN". The amorphous thermoplastic resin may be selected from the list consisting of acrylonitrile butadiene styrene, polystyrene, and styrene acrylonitrile.

The amorphous thermoplastic resin may comprise about <NUM>% weight percent styrene acrylonitrile, and <NUM> weight percent of a mixture comprising polybutylene terephthalate and polyethylene terephthalate.

Surprisingly, it has been found out that said composition provides a high gravity molding material appropriate for injection molding or extrusion molding. A high specific gravity molding material high in surface hardness, excellent in coating characteristics as well as excellent in thermal conductivity is provided.

The use of molding materials having a relatively high specific gravity is known. Such molding materials usually contain a polymeric resin and a high-density filler such as iron oxide. However, in such molding materials the amount of iron oxide which can be included is limited as the thermal conductivity properties of the molding material are relatively poor. Thus, on the one side, lower thermal conductivity leads to relatively longer cycle times during manufacturing to allow the molding material to cool after molding. On the other side, if heavy polymeric materials are filled with high heat conductive additives such as metal powder or fibers, the addition of these materials leads to tight process windows in molding because of the immediate freezing when the molten material contacts the cold wall of the tool. This fast freezing leads to high injection speed and low flow length to wall thickness ratio at the produced part.

Now, it has been surprisingly found out that the molding material according to the present disclosure has a high specific gravity and optimally controlled thermal conductivity properties to reduce or expand the time needed for the molding material to cool during or after injection molding. Surprisingly, it has been found out that a relatively high percentage of iron oxide can be maintained in the molding material while improving on the thermal conductivity properties of the molding material. The addition of aluminium oxide, boron nitride or aluminium silicate provides the molding material with improved thermal conductivity as compared to materials containing a styrene resin and iron oxide only. This improved thermal conductivity may lead to lower cycle times as the molding material needs less time to cool after molding.

Another benefit of adding aluminium oxide, boron nitride or aluminium silicate to the material is the ability to increase the overall amount of iron oxide in the molding material as compared with materials comprising iron oxide and resins of the past. The improvements in the molding material properties come from the addition of relatively small amounts of aluminium oxide, boron nitride or aluminium silicate. A material composition comprising a relatively high percentage of iron oxide (magnetite), i.e. from about <NUM> weight percent to about <NUM> weight percent, preferably about <NUM> weight percent, provides good magnetic properties and a relatively heavy weight of the overall material.

Styrene acrylonitrile "SAN" provides high thermal resistance properties. The acrylonitrile units in the chain enable SAN to have a glass transition temperature greater than <NUM>. The properties of SAN may allow for reduced cycle time due to relatively earlier and quicker transition temperature. Amorphous polymers are suitable for heavy resin compounds of the present disclosure due to the glass transition temperature Tg at which an amorphous polymer is transformed, in a reversible way, from a viscous or rubbery condition to a hard one. By injection molding of the heavy resin material of the present disclosure the temperature of the material melt is above the Tg region (viscous or rubbery condition). During cooling the compound attains the high Tg temperature early and reaches dimensional stability (glassy condition). Over-molding of the heavy resin material is possible as the material stays dimensional stable due to the high Tg of the material.

Polybutylene terephthalate (PBT) and/or polyethylene terephthalate (PET) provide the handle with high quality surface properties, including improved optical characteristics, and high impact strength. Once heated, a mixture of PBT and PET represent a high temperature-resistant melt having low viscosity and a high Melt Flow Index (MFI). Therefore, processability of the magnetic/ferromagnetic material during molding is improved.

It is known, that heavy resin materials tend to show high shrinkage effects for products having thick walls/dimensions. However, it has been surprisingly found out that glass fibers added to the magentic/ferromagentic material provide the material composition with improved stability and low shrinkage effects.

A method for manufacturing an oral care implement according to the present disclosure comprises the following steps:.

molding the non-magnetic and/or non-ferromagnetic material into a head or part of a head.

The amorphous thermoplastic resin may comprise styrene acrylonitrile, polybutylene terephthalate and polyethylene terephthalate, wherein polybutylene terephthalate and polyethylene terephthalate may be premixed with glass fibers. The amorphous thermoplastic resin may be provided in a range from about <NUM> weight percent to about <NUM> weight percent; the aluminium oxide, boron nitride or aluminium silicate may be provided in a range from about <NUM> weight percent to about <NUM> weight percent; and the iron oxide may be provided in a range from about <NUM> weight percent to about <NUM> weight percent.

The magnetic and/or ferromagnetic material may comprise about <NUM> weight percent of styrene acrylonitrile; about <NUM> weight percent of a composition comprising polybutylene terephthalate and polyethylene terephthalate; about <NUM> weight percent of glass fibers; about <NUM> weight percent of aluminium oxide; and about <NUM> weight percent of iron oxide.

The material composition may be made by blending the amorphous thermoplastic resin with powder of aluminium oxide, boron nitride or aluminium silicate, and with iron oxide powder. Increasing the amount of iron oxide within the material composition has further the advantage of providing a lower cost molding material because iron oxide powder is less expensive than the other filling agents. Amorphous thermoplastic resin, glass fibers, aluminium oxide/ boron nitride or aluminium silicate powder, and iron oxide powder may be blended by using a uniaxial extruder, a biaxial extruder, a kneader, a Banbury mixer, a roll or other such extruders. After blending the material is heated to become flowable. The flowable material may then be molded into a handle or part of a handle by either injection molding or extrusion molding.

In an additional step, the handle or part of the handle may be electroplated to add improved appearance and a pleasant feel. Thermoplastic elastomers are well suited for electroplating as they allow for the creation of both hard and soft composite components to be electroplated selectively in one operation.

For example, the handle may comprise a thumb rest being made from a thermoplastic elastomer material and/or from a polypropylene material. These materials can be easily injection molded over the heavy resin material as discussed above. Such thumb rest may provide the handle of the oral care implement with improved handling properties, e.g. with anti-slip properties to improve the maneuverability of the oral care implement under wet conditions, e.g. when the user brushes his teeth. The thumb rest may be made from thermoplastic elastomer having a Shore A hardness from about <NUM> to about <NUM>, or about <NUM> to prevent the oral care implement from being too slippery when used in wet conditions. At least a portion of the thumb rest may have a concave shape with an angle α with respect to the area of the remaining portion of the thumb rest from about <NUM>° to about <NUM>°, or about <NUM>°. The thumb rest or a gripping region may be attached onto the front surface of the handle in the region close to the proximal end, i.e. closest to the head. The thumb rest may comprise a plurality of ribs extending substantially perpendicular to the longitudinal axis of the oral care implement. Such ribs may allow users/consumers to use the oral care implement with even more control. The user/consumer can better grasp and manipulate the handle of the oral care implement during brushing. Such handle may provide further improved control and greater comfort during brushing, in particular under wet conditions.

Furthermore, the handle may be made from at least two, or at least three different materials, each forming different parts of the handle. For example, a first material according to the present disclosure, e.g. a magnetic and/or ferromagnetic material may be injection molded into a first component of the handle thereby forming an underlying base structure of the oral care implement. A second component, e.g. of polypropylene material may be injection molded over the first component, and/or a third component, e.g. of thermoplastic elastomer material may be injection molded over the first component and/or the second component.

The third component of thermoplastic elastomer material may form the thumb rest on the front surface of the oral care implement and/or a palm grip on the back surface being opposite the front surface to be gripped by the user's/consumer's fingers and thumb. Such handle configuration may even further resist slippage during use. The thermoplastic elastomer material may extend through an aperture provided in the underlying base structure and/or second component of the handle.

The tooth cleaning elements of the oral care implement, e.g. bundle of filaments forming one or a plurality of tufts, may be attached to the head by means of a hot tufting process. One method of manufacturing the head with tufts of filaments embedded in the head may comprise the following steps: In a first step, tufts are formed by providing a desired amount of filaments. In a second step, the tufts are placed into a mold cavity so that ends of the filaments which are supposed to be attached to the head extend into said cavity. The opposite ends of the filaments not extending into said cavity may be either end-rounded or non-end-rounded. For example, the filaments may be not end-rounded in case the filaments are tapered filaments having a pointed tip. In a third step the head is formed around the ends of the filaments extending into the mold cavity by an injection molding process, thereby anchoring the tufts in the head. Alternatively, the tufts may be anchored by forming a first part of the head - a so called "sealplate" - around the ends of the filaments extending into the mold cavity by an injection molding process before the remaining part of the oral care implement is formed. Before starting the injection molding process the ends of the tufts extending into the mold cavity may be optionally melted or fusion-bonded to join the filaments together in a fused mass or ball so that the fused masses or balls are located within the cavity. The tufts may be held in the mold cavity by a mold bar having blind holes that correspond to the desired position of the tufts on the finished head of the oral care implement. In other words, the tufts attached to the head by means of a hot tufting process are not doubled over a middle portion along their length and are not mounted in the head by using an anchor/staple. The tufts are mounted on the head by means of an anchor-free tufting process.

The following is a non-limiting discussion of example embodiments of oral care implements and parts thereof in accordance with the present disclosure, where reference to the Figures is made.

<FIG> shows an oral care implement <NUM>, in this specific embodiment a manual toothbrush <NUM>, the manual toothbrush <NUM> comprising a handle <NUM> and head <NUM> being repeatedly attachable to and detachable from the handle <NUM>. The oral care implement <NUM> has a front side <NUM> and a back side <NUM>. An overall length extension <NUM> extends between a proximal end <NUM> and a distal end <NUM> of the implement <NUM> (cf. Tooth cleaning elements <NUM> are attached to the head <NUM> and extend from the front side <NUM>. The handle <NUM> may be formed by using the process as shown in the flow chart of <FIG> and as further explained below. The handle <NUM> may be molded from a magnetic and/or ferromagnetic material. In addition, the handle <NUM> may have been undergone electroplating with any additional material, for example a polyethylene material or a thermoplastic elastomer to create a soft region, e.g. a thumb rest <NUM>. The soft region/thumb rest <NUM> may improve comfort and feel of the handle <NUM>. Alternatively, or in addition, by a further electroplating step the handle <NUM> may be provided with a metal layer <NUM> directly on the magnetic and/or ferromagnetic material of the present disclosure to further improve the appearance of the handle <NUM>. For example, the metal layer <NUM> may have the form of a ring surrounding the outer circumference <NUM> of the handle <NUM>.

The material of which the handle <NUM> is at least partially made possesses magnetic and/or ferromagnetic properties. <FIG> shows a kit <NUM> comprising a manual toothbrush <NUM> with handle <NUM> to which head <NUM> is attached, and a magnetic holder <NUM> onto which toothbrush <NUM> is magnetically attached.

<FIG> shows a diagram of a flow chart illustrating the steps of making a handle <NUM> or a portion of a handle of the oral care implement <NUM> according to the present disclosure. An amorphous thermoplastic resin, optionally comprising glass fibers, is provided at <NUM>. Aluminium oxide, boron nitride or aluminium silicate is provided at <NUM>. Iron oxide is provided at <NUM>. At <NUM>, the amorphous thermoplastic resin (optionally comprising glass fibers), the aluminium oxide, boron nitride or aluminium silicate, and the iron oxide are mixed into a molding material. The molding material is then heated into a flowable condition at <NUM>. The heated and flowable molding material is molded into a handle <NUM> or part of a handle at <NUM>. The molding step may be either an injection molding or extrusion molding step. The optional step of electroplating the oral care implement/handle is shown at <NUM>.

The material according to the present disclosure is an alternative to metal/zinc-die-cast material. The material of the disclosure enables to offer an attractive solution with respect to the manufacturing process according to the present disclosure, price and environment. This alternative allows the handle to have the look and feel in the final state like a metal product. At the same time the material of the present disclosure should be easily processable by injection molding and should save on the assembly effort. For example, for the process of the present disclosure there are three basic steps required: (<NUM>) injection molding of the handle <NUM>; (<NUM>) two-component injection molding of hard material and/or soft material, e.g. to form a thumb rest <NUM>; and (<NUM>) electroplating of the handle, e.g. to form a metal layer in the form of a ring <NUM>. In contrast, when using a zinc-die-cast material five steps are needed: (<NUM>) manufacturing of the zinc-die-casted main part; (<NUM>) deflashing of the main part; (<NUM>) electroplating the main part; (<NUM>) separately producing a soft material part; (<NUM>) and assembling the main part with the separately produced soft material part. A lubricant may be added to the material to improve the molding processing fluidity.

Table <NUM> shows the flowability and heat transfer results of several different formulas/material compositions:.

Graph <NUM> plots the average results of heat transfer and flow distance of the formulas/material compositions from Table <NUM>.

As can be seen, different fillers and different concentrations of fillers control the thermal conductivity or heat transmission and flowability of the material.

Test results revealed that the use of boron nitride or aluminium silicate showed very similar results to that of aluminium oxide depicted in Table <NUM> and Graph <NUM> above.

The heat energy and shear heating affect the fluidity of the heavy resin material, and thereby the process window for an effective injection molding process can be exactly controlled. Further, with the ability of the material of the present disclosure to fill any available cavities within the mold, it is possible to use the mass/weight distribution of the material for adaption of the inertial moment/center of gravity of the finished handle.

The material of the present disclosure provides several benefits: The handle manufactured with the material of the present disclosure looks and feels like a heavy metal handle and it is resistant to corrosion. The material also has manufacturing advantages and cost saving advantages with fast cycle times due to its heat transfer properties as compared to metal inserted or die-casted handles and products with assembled component parts. The material of the present disclosure requires less energy and other essential resources for manufacturing in comparison to zinc-die casted products.

In contrast to material compositions that are highly loaded with fillers, the magnetic/ferromagnetic material of the present disclosure shows optimized mechanical properties, in particular dimensional stability under heat and impact strength due to the improved melt viscosity and glass transition temperature.

The material of the present disclosure possesses the ability to adhere to other components/materials, e.g. substrates and resins, which is important for multicomponent injection molding, e.g. for molding handles comprising two or three different materials.

<FIG> shows five different grip styles / ways how users usually hold a toothbrush during tooth brushing: "Power Grip" <NUM>, <NUM>, "Oblique Grip" <NUM>, <NUM>, "Distal Oblique Grip" <NUM>, <NUM>, "Precision Grip" <NUM>, <NUM> and "Spoon Grip" <NUM>, <NUM>. In the left column, the different grip styles <NUM>, <NUM>, <NUM>, <NUM>, <NUM> are shown when a user holds a toothbrush <NUM>, <NUM> according to the state of the art (cf. <FIG>, <FIG>, <FIG>), while in the right column the respective grip styles <NUM>, <NUM>, <NUM>, <NUM>, <NUM> are shown when a user holds an oral care implement <NUM>, <NUM>, <NUM> (cf. <FIG>, <FIG> and <FIG>) according to the present disclosure. The center of gravity is indicated with "X". The grip styles can be defined by the following characteristics:.

As derivable from <FIG>, the center of gravity X of the toothbrush according to the present disclosure is shifted closer to the center of the length extension of the toothbrush handle as compared to the toothbrush according to the state of the art, even if the toothbrush head is loaded with toothpaste. Since the center of gravity is close to the center of the length extension of the handle, the toothbrush is better balanced and does not easily tip over / does not get head loaded once paste is applied onto the brush head. Further, as shown in <FIG>, in all different grip styles the center of gravity is in or very close to the pivot point of the wrist joint. A balanced toothbrush is easier to control in the mouth and allows precise and accurate brushing movements, thereby enabling better cleaning of the teeth.

<FIG> shows three toothbrushes <NUM>, <NUM>, <NUM> which are identical except from the handle material <NUM>, <NUM>, <NUM>. <FIG> shows the toothbrushes <NUM>, <NUM>, <NUM> of <FIG>, but loaded with toothpaste <NUM>. Material compositions and characteristics of toothbrushes <NUM>, <NUM>, <NUM> are listed in Table <NUM>:.

The center of gravity of toothbrushes <NUM>, <NUM>, <NUM> are indicated with <NUM>, <NUM>, <NUM>, respectively. As shown in <FIG>, center of gravity <NUM> of brush <NUM>, and center of gravity <NUM> of brush <NUM> (according to the present disclosure) are closer to the center of the length extension of the toothbrush handle as compared to center of gravity <NUM> of brush <NUM> (according to the state of the art). Toothbrushes <NUM> and <NUM> are easier to control in the mouth and allow more precise and accurate brushing movements.

In <FIG> toothbrush <NUM> (without and with toothpaste) is compared with toothbrush <NUM> (with and without toothpaste). As clearly derivable from <FIG>, the center of gravity <NUM> is closer to the center of the length extension of the handle than the center of gravity <NUM> of toothbrush <NUM>. The center of gravity <NUM> of toothbrush <NUM> is shifted by distance <NUM>.

Further, as shown in <FIG>, toothbrush <NUM> has an overall length extension <NUM>. The center of gravity <NUM> is located at distance <NUM> measured from the distal end <NUM> of the handle <NUM>. The ratio of the distance <NUM> of the center of gravity <NUM> measured from the distal end <NUM> to the overall length extension <NUM> of the oral care implement <NUM> may be from about <NUM> to about <NUM>, or from about <NUM> to about <NUM>, or from about <NUM> to about <NUM>. Such ratio provides a toothbrush having a center of gravity being close to the pivot point of the wrist joint during brushing. When using the grip styles shown in <FIG>, the toothbrush is easier to control in the mouth, thereby allowing more precise and accurate brushing movements.

The overall length extension <NUM> of the oral care implement <NUM> may be from about <NUM> to about <NUM>, or about <NUM>, while the handle <NUM> of said oral care implement <NUM> may have a length extension <NUM> from about <NUM> to about <NUM>, or about from <NUM> to about <NUM>, or about <NUM>. The center of gravity <NUM> (when the oral care implement <NUM> is loaded with <NUM> toothpaste) is located at about <NUM>, measured from the distal end <NUM> of handle <NUM>.

In contrast to toothbrush <NUM>, toothbrush <NUM> (according to the state of the art) has a center of gravity <NUM> located at a distance of about <NUM> measured from the distal end <NUM> (when toothbrush <NUM> is loaded with about <NUM> toothpaste). The center of gravity <NUM> of toothbrush <NUM> is shifted towards the distal end <NUM> of handle <NUM> by <NUM> (in comparison to toothbrush <NUM>).

<FIG> show in a front view and side view, respectively, axis of rotation <NUM> and center of gravity <NUM> of toothbrush <NUM> according to the state of the art. Toothbrush <NUM> comprises a handle <NUM> made of polypropylene having a density of about <NUM>/cm<NUM>. Toothbrush <NUM> is loaded with about <NUM> of toothpaste and placed on a substantially planar/flat surface <NUM>. As derivable from <FIG>, the center of gravity <NUM> is above the axis of rotation <NUM>, and, thus, toothbrush <NUM> is in an instable/unbalanced position. To prevent the toothbrush <NUM> from tipping/rotating to the side if the brush <NUM> is moved out of the balanced position, additional geometrical structures in the form of roll stops <NUM> are provided.

In contrast to the toothbrushes of the state of the art having a lightweight handle, toothbrush <NUM> according to the present disclosure has a center of gravity <NUM> being located below the axis of rotation <NUM> when the brush is loaded with about <NUM> of toothpaste and placed on a substantially planer/flat surface <NUM> (cf. As the center of gravity <NUM> is closer to the back side <NUM> than to the front side <NUM> of toothbrush <NUM> when measured along the height extension <NUM> of handle <NUM>, toothbrush <NUM> returns automatically to an upright positon (as shown in <FIG>) and keeps toothpaste <NUM> away from the surface <NUM> once the brush <NUM> is moved out of the balanced position.

Claim 1:
An oral care implement (<NUM>, <NUM>, <NUM>) having a front side (<NUM>) and a back side (<NUM>) opposite the front side (<NUM>), an overall length extension (<NUM>, <NUM>) extending between a proximal end (<NUM>) and a distal end (<NUM>, <NUM>), the distal end (<NUM>, <NUM>) being opposite the proximal end (<NUM>), the oral care implement (<NUM>, <NUM>, <NUM>) comprising a head (<NUM>) at the proximal end (<NUM>) and a handle (<NUM>, <NUM>, <NUM>), the head (<NUM>) having at least one cleaning element (<NUM>) extending from the front side (<NUM>), the handle (<NUM>, <NUM>, <NUM>) being at least partially made from a material having a density being higher than the density of the material of the head (<NUM>),
the handle (<NUM>, <NUM>, <NUM>) having a cross-sectional area extending substantially perpendicular to the overall length extension (<NUM>, <NUM>) of the oral are implement (<NUM>, <NUM>, <NUM>), the cross-sectional area having a height extension (<NUM>) extending between the front side (<NUM>) and the back side (<NUM>),
the oral care implement (<NUM>, <NUM>, <NUM>) having a center of gravity (<NUM>, <NUM>) and an axis of rotation (<NUM>) when the oral care implement (<NUM>, <NUM>, <NUM>) is placed with the back side (<NUM>) on a surface (<NUM>), wherein the center of gravity (<NUM>, <NUM>) is below
the axis of rotation (<NUM>) and the center of gravity (<NUM>) is closer to the back side (<NUM>) than to the front side (<NUM>) of the oral care implement (<NUM>, <NUM>, <NUM>) when measured along the height extension (<NUM>) of the handle (<NUM>, <NUM>, <NUM>), wherein
the material of the head (<NUM>) is a non-magnetic and/or non-ferromagnetic material, preferably polypropylene; characterized in that
the material of the handle (<NUM>, <NUM>, <NUM>) comprises a magnetic and/or ferromagnetic material comprising amorphous thermoplastic resin; iron oxide; and aluminium oxide, boron nitride or aluminium silicate.