Patent Description:
Lithium borate compounds are used, for example, in the field of electrochemistry.

For example, an electrolyte solution for a lithium ion battery including lithium bis(oxalato)borate as an electrolyte, is known (See, for example, Patent Document <NUM>). Furthermore, for example, an electrolyte solution for a lithium ion battery including lithium difluoro(oxalato)borate as an electrolyte, is also known (See, for example, Patent Document <NUM>).

Patent Document <NUM> provides a lithium battery which is said to be constructed by sealing into a metallic outer package material a power generation element comprising a positive electrode containing a lithium-contained metal oxide, a negative electrode containing lithium metal or lithium alloy as an active material, an electrolytic liquid and a separator.

Patent Document <NUM> provides a nonaqueous electrolyte solution for a power storage device comprising an electrolyte dissolved in a nonaqueous solvent, and one or more compounds selected from a group consisting of organic sulfone compounds, wherein the electrolyte is a lithium salt soluble in the nonaqueous solvent.

Patent Document <NUM> provides a lithium ion secondary battery comprising a positive electrode including a positive electrode active material, a negative electrode including a negative electrode active material, and a nonaqueous electrolytic solution with an electrolyte dissolved in a nonaqueous solvent.

Patent Document <NUM> provides lithium sulphur batteries comprising an electrolyte containing lithium alkoxyborates and lithium alkoxyaluminates.

Patent Document <NUM> provides a solute for a non-aqueous electrolyte battery, comprising at least one group selected from an alkoxy group, a phenoxy group and a derivative group thereof, bonded to lithium borate.

Patent Document <NUM> provides oligomeric lithium borate salts and their applications and a polymeric electrolyte with oligomeric lithium borate salts.

Patent Document <NUM> provides an electrolyte composition containing lithium alkoxyborates, use of lithium alkoxyborates in lithium ion batteries and lithium ion batteries comprising the electrolyte composition.

Patent Document <NUM> describes compounds containing perfluoroalkyl-cyano-alkoxy-borate anions or perfluoroalkyl-cyano-alkoxy-fluoro-borate anions. Such compounds are said to particularly be useful as part of electrolyte formulations for dye sensitized solar cells.

Non-patent Document <NUM> provides a fluorinated and alkylated lithium malonatoborate salt for lithium ion battery application.

An object of one aspect of the present disclosure is to provide an additive for a lithium secondary battery that includes a lithium borate compound.

An object of another aspect of the present disclosure is to provide a nonaqueous electrolyte solution for a lithium secondary battery that is capable of reducing battery resistances after storage and after charge-discharge cycles; a lithium secondary battery precursor including the nonaqueous electrolyte solution for a lithium secondary battery; and a method of manufacturing a lithium secondary battery using the lithium secondary battery precursor.

A solution to the problems described above includes the following aspects.

According to one aspect of the present disclosure, there is provided an additive for a lithium secondary battery, including a lithium borate compound.

In addition, according to another aspect of the present disclosure, there are provided: a nonaqueous electrolyte solution for a lithium secondary battery that is capable of reducing battery resistances after storage and after charge-discharge cycles; a lithium secondary battery precursor including the nonaqueous electrolyte solution for a lithium secondary battery; and a method of manufacturing a lithium secondary battery using the lithium secondary battery precursor.

In the present specification, a numerical range represented by using "to" means a range including a numerical value described before "to" and a numerical value described after "to" as a lower limit value and an upper limit value, respectively.

In the present specification, in a case in which there are plural substances corresponding to each of a component present in a composition, unless otherwise specified, the amount of each of the component in the composition means the total amount of the plural substances present in the composition.

In the present specification, a term "step" includes not only an independent step but also a step that cannot be clearly distinguished from other steps as long as an intended purpose of the step is achieved.

The lithium borate compound of the present disclosure is a novel lithium borate compound represented by the following Formula (I). Hereinafter, the lithium borate compound represented by Formula (I) is also simply referred to as a "lithium borate compound".

In Formula (I), each of R<NUM>, R<NUM> and R<NUM> independently represents a hydrocarbon group having from <NUM> to <NUM> carbon atoms, which does not have a substituent.

The hydrocarbon group having from <NUM> to <NUM> carbon atoms means that the number of carbon atoms in a skeleton that is composed only of a hydrocarbon group that does not include a substituent, is from <NUM> to <NUM>.

In Formula (I), each of R<NUM>, R<NUM>, and R<NUM> independently is a hydrocarbon group having from <NUM> to <NUM> carbon atoms, which does not have a substituent, two or more of R<NUM>, R<NUM>, and R<NUM> are preferably a hydrocarbon group having from <NUM> to <NUM> carbon atoms, and all three of R<NUM>, R<NUM>, and R<NUM> are more preferably a hydrocarbon group having from <NUM> to <NUM> carbon atoms.

Examples of the hydrocarbon group having from <NUM> to <NUM> carbon atoms, which does not have a substituent, represented by R<NUM> to R<NUM>, include: an aryl group having from <NUM> to <NUM> carbon atoms, which does not have a substituent; and an aliphatic group having from <NUM> to <NUM> carbon atoms, which does not have a substituent.

Examples of the aryl group having from <NUM> to <NUM> carbon atoms, which does not have a substituent, include: a phenyl group; a group in which one hydrogen atom is removed from an alkylbenzene (e.g. a benzyl group, a tolyl group, a xylyl group, a mesityl group, etc.); a naphthyl group; a group in which one hydrogen atom is removed from an alkyl group-substitution of naphthalene.

Among the above, the aryl group having from <NUM> to <NUM> carbon atoms, which does not have a substituent, is preferably a phenyl group or a <NUM>-methylphenyl group, and is more preferably a phenyl group.

The aliphatic group having from <NUM> to <NUM> carbon atoms, which does not have a substituent, may be a saturated aliphatic group (i.e. an alkyl group) or an unsaturated aliphatic group (i.e. an alkenyl group or an alkynyl group).

The aliphatic group having from <NUM> to <NUM> carbon atoms, which does not have a substituent, may be linear, branched, or cyclic.

The aliphatic group having from <NUM> to <NUM> carbon atoms, which does not have a substituent, is preferably an aliphatic group having from <NUM> to <NUM> carbon atoms, and more preferably an aliphatic group having from <NUM> to <NUM> carbon atoms.

Examples of the aliphatic group having from <NUM> to <NUM> carbon atoms include:.

Among the above, the aliphatic group having from <NUM> to <NUM> carbon atoms represented by R<NUM> to R<NUM> is preferably a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, an n-hexyl group, an n-octyl group, a vinyl group, an allyl group, or an ethynyl group, and more preferably a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a vinyl group, an allyl group, or an ethynyl group.

Each of R<NUM>, R<NUM>, and R<NUM> in Formula (I) independently is preferably a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a vinyl group, an allyl group, an ethynyl group, or a phenyl group.

In Formula (I), R<NUM> represents a trifluoromethyl group.

Preferable specific examples of the lithium borate compound represented by Formula (I) include: lithium borate compounds represented by the following Formula (II), the following Formula (III), the following Formula (IV), and the following Formula (V). However, a lithium borate compound represented by Formula (I) is not limited to this specific example.

Hereinafter, one example of the method of manufacturing the lithium borate compound of the present disclosure (manufacturing method X) will be described. However, the method of manufacturing the lithium borate compound of the present disclosure is not limited to the manufacturing method X.

The manufacturing method X includes: a first reaction step of reacting (trifluoromethyl)trimethylsilane, a potassium halide, and a borate ester compound in a solvent, thereby obtaining a potassium borate compound that is a reaction intermediate; and a second reaction step of reacting the potassium borate compound and a lithium halide in a solvent, thereby obtaining the lithium borate compound of the present disclosure.

Examples of the potassium halide in the first reaction step include potassium fluoride, potassium chloride, potassium bromide, and potassium iodide. Among them, potassium fluoride or potassium chloride are more preferable. The potassium halides may be used singly or in combination of two or more kinds thereof.

Examples of the borate ester compound in the first reaction step include: trimethyl borate, triethyl borate, tri-n-propyl borate, triisopropyl borate, tri-n-butyl borate, triisobutyl borate, tri-sec-butyl borate, tri-tert-butyl borate, trihexyl borate, tricyclohexyl borate, trioctyl borate, and triphenyl borate. Trimethyl borate, triethyl borate, tri-n-propyl borate, triisopropyl borate, tri-n-butyl borate, tricyclohexyl borate, triphenyl borate, or the like is preferable. Among them, trimethyl borate, triethyl borate, triisopropyl borate, or tri-n-butyl borate is more preferable. The borate ester compounds may be used singly, or in combination of two or more kinds thereof.

Examples of the lithium halide in the second reaction step include lithium fluoride, lithium chloride, lithium bromide, and lithium iodide. Among them, lithium fluoride or lithium chloride is more preferable. The lithium halides may be used singly, or in combination of two or more kinds thereof.

Examples of the solvent in the first reaction step and the second reaction step include a nonaqueous solvent such as acetone, ethyl acetate, acetonitrile, tetrahydrofuran, dimethyl carbonate, ethyl methyl carbonate, diethyl carbonate, methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, sec-butanol, tert-butanol, pentane, hexane, heptane, octane, nonane, decane, toluene, xylene (i.e. orthoxylene, metaxylene, or paraxylene), ethylbenzene, butylbenzene, pentylbenzene, hexylbenzene, heptylbenzene, propylbenzene, isopropylbenzene (also called cumene), cyclohexylbenzene, tetralin, mesitylene, methylcyclopentane, cyclohexane, methylcyclohexane, cycloheptane, cyclooctane, or cyclononane. The solvent may be used singly or in combination of two or more kinds thereof.

The first reaction step and the second reaction step may be conducted either under a normal pressure or under a reduced pressure.

The first reaction step and the second reaction step may be conducted either under an air atmosphere or under an inert atmosphere.

The first reaction step and the second reaction step are preferably conducted under an inert atmosphere (e.g. under an atmosphere of an inert gas such as nitrogen or argon), for example, from a viewpoint of preventing a contamination of a component (such as a moisture) that inhibits a production of the potassium borate compound and the lithium borate compound.

A reaction temperature in the first reaction step is preferably from <NUM> to <NUM>, more preferably from <NUM> to <NUM>, and still more preferably from <NUM> to <NUM>.

A reaction time in the first reaction step is preferably from <NUM> minutes to <NUM> hours, and more preferably from <NUM> hour to <NUM> hours, from a viewpoint of efficiently producing the potassium borate compound.

A reaction temperature in the second reaction step is preferably from <NUM> to <NUM>, more preferably from <NUM> to <NUM>, and still more preferably from <NUM> to <NUM>.

In a case in which a reaction temperature in the second reaction step is <NUM> or higher, a production of the lithium borate compound is likely to be promoted. In a case in which a reaction temperature in the second reaction step is <NUM> or lower, a decomposition of the generated lithium borate compound is suppressed, and thus a formation rate of the lithium borate compound is likely to be improved.

A reaction time in the second reaction step is preferably from <NUM> minutes to <NUM> hours, and more preferably from <NUM> minutes to <NUM> hours, from a viewpoint of efficiently producing the lithium borate compound.

The second reaction step may be an aspect in which the reaction solution obtained after the first reaction step is mixed as it is with the lithium halide, or may be an aspect in which a solid obtained after distilling off a product such as a halogenated trimethylsilane and a solvent from the reaction solution obtained after the first reaction step is mixed with the lithium halide.

There is no particular limitation for a method of extracting the lithium borate compound after the second reaction step.

For example, in a case in which only an intended component (i.e. the lithium borate compound per se) is obtained as a solid, the solid can be extracted as the lithium borate compound without any special treatment.

In a case in which a slurry in which the lithium borate compound is dispersed in the solvent is obtained by the second reaction step, the solvent is separated from the slurry by a solid-liquid separation such as a filtration, and the obtained filtrate is dried, whereby the lithium borate compound can be extracted.

In a case in which a solution in which the lithium borate compound is dissolved in the solvent is obtained by the second reaction step, the lithium borate compound can be extracted by distilling off the solvent from the solution by a heat concentration or the like.

Also in a case in which a solution in which the lithium borate compound is dissolved in the solvent is obtained by the second reaction step, a solvent not dissolving the lithium borate compound is added to the solution, whereby the lithium borate compound is allowed to precipitate, then the lithium borate compound precipitated from the solution is separated from the solvent by a solid-liquid separation, and the resultant solid is dried, whereby the lithium borate compound can be extracted.

As a method of drying the extracted lithium borate compound, a ventilation drying method using a shelf type drying machine; a fluidized drying method using a conical drying machine; a method of drying using an apparatus such as a hot plate or an oven; a method of supplying warm air or hot air with a drying machine such as a dryer, or the like can be applied.

A pressure at which the extracted lithium borate compound is dried may be either a normal pressure or a reduced pressure.

A temperature at which the extracted lithium borate compound is dried is preferably from <NUM> to <NUM>, more preferably from <NUM> to <NUM>, and still more preferably from <NUM> to <NUM>.

In a case in which the temperature is <NUM> or higher, a drying efficiency is excellent. In a case in which the temperature is <NUM> or lower, a decomposition of the generated lithium borate compound is suppressed, and the lithium borate compound is stably and easily extracted.

The extracted lithium borate compound may be used as it is, or, for example, may be used as being dispersed or dissolved in a solvent, or may be used after being mixed with another solid material.

The lithium borate compound of the present disclosure can be usefully used for applications such as an additive for a lithium battery (preferably, an additive for a lithium secondary battery, more preferably, an additive for a nonaqueous electrolyte solution of a lithium secondary battery), a reaction agent, a synthetic reaction catalyst, an electrolyte for various electrochemical devices, a doping agent, or an additive for a lubricating oil.

An additive for a secondary battery of the present disclosure includes the above-described lithium borate compound of the present disclosure. The additive for a secondary battery of the present disclosure is suitable in particular as an additive for a nonaqueous electrolyte solution of a lithium secondary battery.

A nonaqueous electrolyte solution for a lithium secondary battery according to an embodiment of the present disclosure (hereinafter, also simply referred to as a "nonaqueous electrolyte solution of the present embodiment") includes: an electrolyte that is a lithium salt including fluorine; a nonaqueous solvent; and the lithium borate compound represented by the following Formula (I):
<CHM>
wherein, in Formula (I), each of R<NUM>, R<NUM>, and R<NUM> independently represents a hydrocarbon group having from <NUM> to <NUM> carbon atoms, which does not have a substituent, and R<NUM> represents a fluorine atom or a fluorinated hydrocarbon group having from <NUM> to <NUM> carbon atoms.

According to the nonaqueous electrolyte solution of the present embodiment, a battery resistance after storage and after charge-discharge cycles can be reduced.

A nonaqueous electrolyte solution of the present embodiment (hereinafter, also simply referred to as a "nonaqueous electrolyte solution") includes a lithium borate compound.

The nonaqueous electrolyte solution of the present disclosure includes a lithium borate compound, whereby a battery resistance after storage and after charge-discharge cycles can be reduced.

The reason why the above-described effect is achieved is assumed as follows. However, the nonaqueous electrolyte solution of the present embodiment is not limited by the following reason.

In a case in which a lithium secondary battery is manufactured using the nonaqueous electrolyte solution of the present embodiment, in a process of manufacturing a lithium secondary battery (e.g. in an aging step described later), a reaction product of a lithium borate compound and LiF generated from the electrolyte is considered to be produced in a vicinity of a surface of a negative electrode of the lithium secondary battery, and furthermore a component that is a decomposition product of the reaction product, is considered to be produced. This component is considered, in the manufacturing process, to move to a vicinity of a surface of a positive electrode and the vicinity of the surface of the negative electrode, and to adhere to the surface of the positive electrode and the surface of the negative electrode to form a positive electrode coating film and a negative electrode coating film. Owing to this, a stability of the battery after storage and after charge-discharge cycles is improved (e.g. an elution of a metal element in a positive electrode active material is suppressed), and as a result of this, battery resistances after storage and after charge-discharge cycles are considered to be reduced.

Because of the above reasons, by using the nonaqueous electrolyte solution of the present embodiment, it is considered that battery resistances after storage and after charge-discharge cycles can be reduced.

It is considered that the adhesion of the component to the surfaces of the positive electrode and the negative electrode (i.e. a formation of the positive electrode coating film and the negative electrode coating film) described above still proceeds during a storage period in a case in which the lithium secondary battery is stored after the lithium secondary battery has been manufactured.

Hence, in a case in which the lithium secondary battery is stored, the battery resistance of the lithium secondary battery with respect to the storage period of the lithium secondary battery is considered to be reduced.

The nonaqueous electrolyte solution of the present disclosure may include only one kind of the lithium borate compounds, or may include two or more kinds thereof.

The nonaqueous electrolyte solution of the present disclosure may include the lithium borate compound as an additive for a battery, or may include the lithium borate compound as a supply source of an electrolyte.

A content of the lithium borate compound in the nonaqueous electrolyte solution of the present disclosure is not particularly limited, but is preferably from <NUM>% by mass to <NUM>% by mass with respect to the total amount of the nonaqueous electrolyte solution.

In a case in which the content of the lithium borate compound with respect to the total amount of the nonaqueous electrolyte solution is <NUM>% by mass or more, the effect by the nonaqueous electrolyte solution of the present disclosure is more effectively achieved. The content of the lithium borate compound with respect to the total amount of the nonaqueous electrolyte solution is more preferably <NUM>% by mass or more, still more preferably <NUM>% by mass or more, and still more preferably <NUM>% by mass or more.

In a case in which the content of the lithium borate compound with respect to the total amount of the nonaqueous electrolyte solution is <NUM>% by mass or less, a chemical stability of the nonaqueous electrolyte solution is further improved.

The content of the lithium borate compound with respect to the total amount of the nonaqueous electrolyte solution is more preferably <NUM>% by mass or less, still more preferably <NUM>% by mass or less, and still more preferably <NUM>% by mass or less.

In a case in which the nonaqueous electrolyte solution of the present disclosure includes the lithium borate compound as a supply source of an electrolyte, a concentration of the electrolyte is preferably from <NUM> mol/L to <NUM> mol/L, and more preferably from <NUM> mol/L to <NUM> mol/L.

In an actual analysis of a nonaqueous electrolyte solution collected by disassembling a battery, there may be a case in which the amount of the lithium borate compound is reduced as compared with the amount of the lithium borate compound added to the nonaqueous electrolyte solution. Therefore, in a case in which even a small amount of the lithium borate compound can be detected in a nonaqueous electrolyte solution extracted from a battery, the nonaqueous electrolyte solution is included in the scope of the nonaqueous electrolyte solution of the present disclosure.

Even in a case in which the lithium borate compound cannot be detected from a nonaqueous electrolyte solution, but a compound derived from a decomposition product of the lithium borate compound is detected in the nonaqueous electrolyte solution or in a coating film of an electrode, the nonaqueous electrolyte solution is also considered to be included in the scope of the nonaqueous electrolyte solution of the present disclosure.

The same applies to a compound, other than the lithium borate compound, that can be included in the nonaqueous electrolyte solution.

The nonaqueous electrolyte solution of the present embodiment includes at least one electrolyte that is a lithium salt including fluorine (hereinafter, also referred to as a "fluorine-containing lithium salt").

Examples of the fluorine-containing lithium salt include;.

As the fluorine-containing lithium salt, LiPF<NUM> is particularly preferable.

The nonaqueous electrolyte solution of the present embodiment may include an electrolyte which is a lithium salt that does not include fluorine.

Examples of the lithium salt that does not include fluorine include: lithium perchlorate (LiClO<NUM>), lithium aluminum tetrachloride (LiAlCl<NUM>), and lithium decachlorodecaborate (Li<NUM>B<NUM>Cl<NUM>).

A percentage of the fluorine-containing lithium salt in the entire electrolytes included in the nonaqueous electrolyte solution of the present embodiment is preferably from <NUM>% by mass to <NUM>% by mass, more preferably from <NUM>% by mass to <NUM>% by mass, and still more preferably from <NUM>% by mass to <NUM>% by mass.

A percentage of LiPF<NUM> in the entire electrolytes included in the nonaqueous electrolyte solution of the present embodiment is preferably from <NUM>% by mass to <NUM>% by mass, more preferably from <NUM>% by mass to <NUM>% by mass, and still more preferably from <NUM>% by mass to <NUM>% by mass.

A concentration of electrolytes in the nonaqueous electrolyte solution of the present embodiment is preferably from <NUM> mol/L to <NUM> mol/L, and more preferably from <NUM> mol/L to <NUM> mol/L.

A concentration of LiPF<NUM> in the nonaqueous electrolyte solution of the present embodiment is preferably from <NUM> mol/L to <NUM> mol/L, and more preferably from <NUM> mol/L to <NUM> mol/L.

The nonaqueous electrolyte solution of the present embodiment includes at least one nonaqueous solvent.

Examples of the nonaqueous solvent include: a cyclic carbonate, a fluorine-containing cyclic carbonate, a chain carbonate, a fluorine-containing chain carbonate, an aliphatic carboxylate ester, a fluorine-containing aliphatic carboxylate ester, a γ-lactone, a fluorine-containing γ-lactone, a cyclic ether, a fluorine-containing cyclic ether, a chain ether, a fluorine-containing chain ether, a nitrile, an amide, a lactam, nitromethane, nitroethane, sulfolane, trimethyl phosphate, dimethyl sulfoxide, and dimethyl sulfoxide phosphoric acid.

Examples of the cyclic carbonate include: ethylene carbonate (EC), propylene carbonate (PC), and butylene carbonate (BC).

Examples of the fluorine-containing cyclic carbonate include fluoroethylene carbonate (FEC).

Examples of the chain carbonate include: dimethyl carbonate (DMC), diethyl carbonate (DEC), ethyl methyl carbonate (EMC), methyl propyl carbonate (MPC), ethyl propyl carbonate (EPC), and dipropyl carbonate (DPC).

Examples of the aliphatic carboxylate ester include: methyl formate, methyl acetate, methyl propionate, methyl butyrate, methyl isobutyrate, methyl trimethylbutyrate, ethyl formate, ethyl acetate, ethyl propionate, ethyl butyrate, ethyl isobutyrate, and ethyl trimethylbutyrate.

Examples of the γ-lactone include: γ-butyrolactone, and γ-valerolactone.

Examples of the cyclic ether include: tetrahydrofuran, <NUM>-methyltetrahydrofuran, tetrahydropyran, <NUM>,<NUM>-dioxolane, <NUM>-methyl-<NUM>,<NUM>-dioxolane, <NUM>,<NUM>-dioxane, and <NUM>,<NUM>-dioxane.

Examples of the chain ether include: <NUM>,<NUM>-ethoxyethane (DEE), ethoxymethoxyethane (EME), diethyl ether, <NUM>,<NUM>-dimethoxyethane, and <NUM>,<NUM>-dibutoxyethane.

Examples of the nitrile include: acetonitrile, glutaronitrile, adiponitrile, methoxyacetonitrile, and <NUM>-methoxypropionitrile.

Examples of the amide include N,N-dimethylformamide.

Examples of the lactam include: N-methylpyrrolidinone, N-methyloxazolidinone, and N,N'-dimethylimidazolidinone.

The nonaqueous solvent preferably includes at least one selected from the group consisting of a cyclic carbonate, a fluorine-containing cyclic carbonate, a chain carbonate, and a fluorine-containing chain carbonate.

In this case, a total percentage of the cyclic carbonate, the fluorine-containing cyclic carbonate, the chain carbonate, and the fluorine-containing chain carbonate in the nonaqueous solvent is preferably from <NUM>% by mass to <NUM>% by mass, more preferably from <NUM>% by mass to <NUM>% by mass, and still more preferably from <NUM>% by mass to <NUM>% by mass.

The nonaqueous solvent preferably includes at least one selected from the group consisting of a cyclic carbonate, and a chain carbonate.

In this case, a total percentage of the cyclic carbonate and the chain carbonate in the nonaqueous solvent is preferably from <NUM>% by mass to <NUM>% by mass, more preferably from <NUM>% by mass to <NUM>% by mass, and still more preferably from <NUM>% by mass to <NUM>% by mass.

A percentage of the nonaqueous solvent in the nonaqueous electrolyte solution of the present embodiment is preferably <NUM>% by mass or more, and more preferably <NUM>% by mass or more.

An upper limit of the percentage of the nonaqueous solvent in the nonaqueous electrolyte solution of the present embodiment depends on contents of other components (a lithium borate compound, an electrolyte, etc.), but the upper limit is, for example, <NUM>% by mass, preferably <NUM>% by mass, and still more preferably <NUM>% by mass.

An intrinsic viscosity of the nonaqueous solvent is preferably <NUM> mPa·s or less at <NUM> from a viewpoint of further improving dissociability of the electrolyte and ionic mobility.

From a viewpoint of further improving a chemical stability of the nonaqueous electrolyte solution, the nonaqueous electrolyte solution of the present embodiment preferably includes at least one cyclic carbonate ester having an unsaturated bond.

In general, in a case in which the nonaqueous electrolyte solution includes a cyclic carbonate ester having an unsaturated bond, an internal resistance of a battery tends to easily increase.

However, since the nonaqueous electrolyte solution of the present embodiment includes a lithium borate compound, the internal resistance of the battery can be reduced even in a case in which the nonaqueous electrolyte solution further includes the cyclic carbonate ester having an unsaturated bond.

Rather, in a case in which the nonaqueous electrolyte solution of the present embodiment includes the cyclic carbonate ester having an unsaturated bond, there is an advantage that an improvement range of a reduction in the internal resistance by an addition of the lithium borate compound is wide.

Examples of the cyclic carbonate ester having an unsaturated bond include: a vinylene carbonate-based compound, a vinyl ethylene carbonate-based compound, and a methylene ethylene carbonate-based compound.

Examples of the vinylene carbonate-based compound include: vinylene carbonate (also called: <NUM>,<NUM>-dioxol-<NUM>-one), methyl vinylene carbonate (also called: <NUM>-methyl-<NUM>,<NUM>-dioxol-<NUM>-one), ethyl vinylene carbonate (also called: <NUM>-ethyl-<NUM>,<NUM>-dioxol-<NUM>-one), <NUM>,<NUM>-dimethyl-<NUM>,<NUM>-dioxol-<NUM>-one, <NUM>,<NUM>-diethyl-<NUM>,<NUM>-dioxol-<NUM>-one, <NUM>-fluoro-<NUM>,<NUM>-dioxol-<NUM>-one, and <NUM>-trifluoromethyl-<NUM>,<NUM>-dioxol-<NUM>-one.

Examples of the vinyl ethylene carbonate-based compound include: vinyl ethylene carbonate (also called: <NUM>-vinyl-<NUM>,<NUM>-dioxolane-<NUM>-one), <NUM>-methyl-<NUM>-vinyl-<NUM>,<NUM>-dioxolane-<NUM>-one, <NUM>-ethyl-<NUM>-vinyl-<NUM>,<NUM>-dioxolane-<NUM>-one, <NUM>-n-propyl-<NUM>-vinyl-<NUM>,<NUM>-dioxolane-<NUM>-one, <NUM>-methyl-<NUM>-vinyl-<NUM>,<NUM>-dioxolane-<NUM>-one, <NUM>,<NUM>-divinyl-<NUM>,<NUM>-dioxolane-<NUM>-one, and <NUM>,<NUM>-divinyl-<NUM>,<NUM>-dioxolane-<NUM>-one.

Examples of the methylene ethylene carbonate-based compound include: <NUM>-methylene-<NUM>,<NUM>-dioxolane-<NUM>-one, <NUM>,<NUM>-dimethyl-<NUM>-methylene-<NUM>,<NUM>-dioxolane-<NUM>-one, and <NUM>,<NUM>-diethyl-<NUM>-methylene-<NUM>,<NUM>-dioxolane-<NUM>-one.

As the cyclic carbonate ester having an unsaturated bond, vinylene carbonate is particularly preferable.

In a case in which the nonaqueous electrolyte solution of the present embodiment includes the cyclic carbonate ester having an unsaturated bond, a content of the cyclic carbonate ester having an unsaturated bond is preferably from <NUM>% by mass to <NUM>% by mass, more preferably from <NUM>% by mass to <NUM>% by mass, still more preferably from <NUM>% by mass to <NUM>% by mass, and still more preferably from <NUM>% by mass to <NUM>% by mass with respect to the total amount of the nonaqueous electrolyte solution.

In a case in which the nonaqueous electrolyte solution of the present embodiment includes vinylene carbonate, a content of vinylene carbonate is preferably from <NUM>% by mass to <NUM>% by mass, more preferably from <NUM>% by mass to <NUM>% by mass, still more preferably from <NUM>% by mass to <NUM>% by mass, and still more preferably from <NUM>% by mass to <NUM>% by mass with respect to the total amount of the nonaqueous electrolyte solution.

In a case in which the nonaqueous electrolyte solution of the present embodiment includes vinylene carbonate, a ratio of a content by mass of vinylene carbonate to a content by mass of the lithium borate compound (hereinafter, also referred to as a "content ratio by mass [vinylene carbonate/lithium borate compound]") is preferably <NUM> or more, more preferably <NUM> or more, and still more preferably <NUM> or more.

In a case in which the content ratio by mass [vinylene carbonate/lithium borate compound] is <NUM> or more, an increase in an internal resistance of a lithium secondary battery after storage can be further suppressed.

An upper limit of the content ratio by mass [vinylene carbonate/lithium borate compound] is not particularly limited, but is preferably <NUM> or less, more preferably <NUM> or less, and still more preferably <NUM> or less from a viewpoint of more effectively obtaining an effect by vinylene carbonate.

The nonaqueous electrolyte solution of the present embodiment may include at least one component other than the above-described components.

Examples of the other component include a known additive that can be included in the nonaqueous electrolyte solution (hereinafter also referred to as a "known additive"), such as sultone (i.e. a cyclic sulfonate ester), an acid anhydride, an oxalato compound, or a cyclic sulfate ester compound.

In a case in which the nonaqueous electrolyte solution of the present embodiment includes the known additive, a content of the known additive with respect to the total amount of the nonaqueous electrolyte solution is preferably from <NUM>% by mass to <NUM>% by mass, and more preferably from <NUM>% by mass to <NUM>% by mass.

Examples of the sultone include: propane sultone, and propene sultone, and specific examples thereof include: <NUM>,<NUM>-propane sultone, <NUM>,<NUM>-butane sultone, <NUM>,<NUM>-propene sultone, <NUM>-methyl-<NUM>,<NUM>-propene sultone, <NUM>-methyl-<NUM>,<NUM>-propene sultone, and <NUM>-methyl-<NUM>,<NUM>-propene sultone. These may be used singly, or in mixture of plural kinds thereof.

As the sultone, propene sultone is preferable.

These may be used singly, or in mixture of plural kinds thereof.

As the acid anhydride, sulfobenzoic anhydride is preferable.

Examples of the oxalato compound include:
lithium difluorobis(oxalato)phosphate, lithium tetrafluoro(oxalato)phosphate, lithium tris(oxalato)phosphate, lithium difluoro(oxalato)borate, and lithium bis(oxalato)borate.

Examples of the cyclic sulfate ester compound include:
catechol sulfate, <NUM>,<NUM>-cyclohexyl sulfate, <NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane, <NUM>-methyl-<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane, <NUM>-ethyl-<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane, <NUM>-propyl-<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane, <NUM>-butyl-<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane, <NUM>-pentyl-<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane, <NUM>-hexyl-<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane, <NUM>-methylsulfonyloxymethyl-<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane, <NUM>-ethylsulfonyloxymethyl-<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane, bis((<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane-<NUM>-yl)methyl)sulfate, and <NUM>,<NUM>'-bis(<NUM>,<NUM>-dioxo-<NUM>,<NUM>,<NUM>-dioxathiolane).

Examples of the other additive also include:.

An intrinsic viscosity of the nonaqueous electrolyte solution of the present embodiment is preferably <NUM> mPa·s or less at <NUM> from a viewpoint of further improving dissociability of the electrolyte and ionic mobility.

There is no particular limitation for the method of manufacturing the nonaqueous electrolyte solution of the present embodiment. The nonaqueous electrolyte solution of the present embodiment may be manufactured by mixing respective components.

Examples of the method of manufacturing the nonaqueous electrolyte solution of the present embodiment include a manufacturing method including:.

In a manufacturing method according to this one example, an electrical conductivity of the resultant nonaqueous electrolyte solution is preferably reduced with respect to an electrical conductivity of the solution (before the addition of the lithium borate compound). By using the nonaqueous electrolyte solution obtained by the manufacturing method of this aspect, the above-described effect (i.e. an effect of reducing an internal resistance of the battery) of the nonaqueous electrolyte solution is more effectively achieved.

A lithium secondary battery precursor according to an embodiment of the present disclosure (hereinafter, also simply referred to as a "battery precursor of the present embodiment") is a lithium secondary battery precursor that includes:.

Here, the lithium secondary battery precursor means a lithium secondary battery before being charged and discharged.

The lithium secondary battery of the present embodiment described later is manufactured by housing a positive electrode, a negative electrode, a separator, and a nonaqueous electrolyte solution in a case, whereby a lithium secondary battery precursor is manufactured, and by subjecting the resultant lithium secondary battery precursor to charging and discharging (preferably, aging treatment including charging and discharging).

The battery precursor of the present embodiment includes the nonaqueous electrolyte solution of the present embodiment.

Therefore, by using the battery precursor of the present embodiment, an effect similar to the effect by the nonaqueous electrolyte solution of the present embodiment is achieved.

The case for the battery precursor of the present embodiment is not particularly limited, and examples thereof include a known case for a lithium secondary battery.

Examples of the case include: a case including a laminate film, and a case including a battery can and a battery can lid.

The positive electrode in the battery precursor of the present embodiment is a positive electrode that is configured to intercalate and de-intercalate lithium ions.

The positive electrode in the battery precursor of the present embodiment preferably includes at least one positive electrode active material that is configured to intercalate and de-intercalate lithium ions.

The positive electrode in the battery precursor of the present embodiment more preferably includes: a positive electrode current collector; and a positive electrode mixture layer including the positive electrode active material and a binder.

The positive electrode mixture layer is provided on at least a part of a surface of the positive electrode current collector.

The positive electrode active material is not particularly limited as long as it is a material that is configured to intercalate and de-intercalate lithium ions, and may be a positive electrode active material usually used for a lithium secondary battery.

Examples of the positive electrode active material include:.

In the oxide, the metal element other than Li and Ni is preferably included at a percentage equivalent to or less than Ni in terms of the number of atoms.

The metal element other than Li and Ni may be, for example, at least one selected from the group consisting of Co, Mn, Al, Cr, Fe, V, Mg, Ca, Na, Ti, Zr, Nb, Mo, W, Cu, Zn, Ga, In, Sn, La, and Ce. These positive electrode active materials may be used singly, or in mixture of two or more thereof.

The positive electrode active material preferably includes a lithium-containing composite oxide (hereinafter, also referred to as an "NCM") represented by the following Formula (C1).

The lithium-containing composite oxide (C1) has advantages of a high energy density per unit volume and an excellent thermal stability.

wherein, in Formula (C1), each of a, b, and c independently is more than <NUM> but less than <NUM>, and the sum of a, b, and c is from <NUM> to <NUM>.

Specific examples of NCM include LiNi<NUM>Co<NUM>Mn<NUM>O<NUM>, LiNi<NUM>Co<NUM>Mn<NUM>O<NUM>, LiNi<NUM>Co<NUM>Mn<NUM>O<NUM>, and LiNi<NUM>Co<NUM>Mn<NUM>O<NUM>.

The positive electrode active material may include a lithium-containing composite oxide (hereinafter, also referred to as an "NCA") represented by the following Formula (C2).

LitNi<NUM>-x-yCoxAlyO<NUM> :     Formula (C2).

wherein, in Formula (C2), t is from <NUM> to <NUM>, x is from <NUM> to <NUM>, y is from <NUM> to <NUM>, and the sum of x and y is less than <NUM>.

Specific examples of NCA include LiNi<NUM>Co<NUM>Al<NUM>O<NUM>.

In a case in which the positive electrode in the battery precursor of the present embodiment includes: a positive electrode current collector; and a positive electrode mixture layer including a positive electrode active material and a binder, a content of the positive electrode active material in the positive electrode mixture layer is, for example, <NUM>% by mass or more, preferably <NUM>% by mass or more, still more preferably <NUM>% by mass or more, and particularly preferably <NUM>% by mass or more with respect to the total amount of the positive electrode mixture layer.

A content of the positive electrode active material in the positive electrode mixture layer is, for example, <NUM>% by mass or less, preferably <NUM>% by mass or less.

Examples of the binder that can be included in the positive electrode mixture layer include polyvinyl acetate, polymethyl methacrylate, nitrocellulose, a fluororesin, and rubber particle.

Examples of the fluororesin include polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), a tetrafluoroethylene-hexafluoropropylene copolymer (FEP), and a vinylidene fluoride-hexafluoropropylene copolymer.

Examples of the rubber particles include styrene-butadiene rubber particles and acrylonitrile rubber particles.

Among them, the fluororesin is preferable from a viewpoint of improving an oxidation resistance of the positive electrode mixture layer.

The binder can be used singly, or, in combination of two or more kinds thereof, if necessary.

A content of the binder in the positive electrode mixture layer is preferably from <NUM>% by mass to <NUM>% by mass with respect to the positive electrode mixture layer from a viewpoint of a good balance between physical properties (e.g. an electrolyte solution permeability, a peel strength, etc.) of the positive electrode mixture layer and a battery performance.

In a case in which a content of the binder is <NUM>% by mass or more, an adhesiveness of the positive electrode mixture layer to the positive electrode current collector and a binding property between the positive electrode active materials are further improved.

In a case in which the content of the binder is <NUM>% by mass or less, the amount of the positive electrode active material in the positive electrode mixture layer can be further increased, and thus a battery capacity is further improved.

In a case in which the positive electrode in the battery precursor of the present embodiment includes a positive electrode current collector and a positive electrode mixture layer, the positive electrode mixture layer preferably includes a conductive auxiliary material.

As the conductive auxiliary material, a known conductive auxiliary material can be used.

The known conductive auxiliary material is not particularly limited as long as it is a carbon material having conductivity, but graphite, carbon black, conductive carbon fiber (carbon nanotube, carbon nanofiber, carbon fiber), fullerene, and the like can be used singly, or in combination of two or more kinds thereof.

Examples of commercially available carbon blacks include: TOKABLACK #<NUM>, #<NUM>, #<NUM>, #<NUM> etc. (Furnace black manufactured by TOKAI CARBON CO. ); PRINTEX L etc. (Furnace black manufactured by Degussa AG); RAVEN <NUM>, <NUM>, <NUM>, <NUM> ULTRA III, <NUM> ULTRA etc., CONDUCTEX SC ULTRA, CONDUCTEX <NUM> ULTRA etc., PUER BLACK <NUM>, <NUM>, <NUM> etc. (Furnace black manufactured by Columbian Chemicals Company); #<NUM>, #2400B, #2600B, #30050B, #3030B, #3230B, #3350B, #3400B, #5400B etc. (Furnace black manufactured by Mitsubishi Chemical Corporation); MONARCH <NUM>, <NUM>, <NUM>, VULCAN XC-72R, BLACK PEARLS <NUM>, LITX-<NUM>, LITX-<NUM> etc. (Furnace black manufactured by Cabot Corporation); ENSACO <NUM>, ENSACO <NUM>, ENSACO <NUM>, SUPER-P (manufactured by TIMCAL GRAPHITE & CARBON); KETJENBLACK EC-300J, and EC-600JD (manufactured by AKZO N. ); DENKA BLACK, DENKA BLACK HS-<NUM>, and FX-<NUM> (Acetylene black manufactured by Denki Kagaku Kogyo K.

Examples of the graphite include: artificial graphite; and natural graphite (e.g. flake graphite, vein graphite, amorphous graphite, etc.), but are not limited thereto.

In a case in which the positive electrode in the battery precursor of the present embodiment includes a positive electrode current collector and a positive electrode mixture layer, the positive electrode mixture layer may include another component in addition to each of the above-described components.

Examples of another component include a thickening agent, a surfactant, a dispersant, a wetting agent, and an antifoaming agent.

As the positive electrode current collector, various materials can be used, for example, a metal or an alloy is used.

More specific examples of the positive electrode current collector include: aluminum, nickel, and a stainless steel (referred to as SUS in Japanese Industrial Standards). Among them, aluminum is preferable from a viewpoint of balancing a high electrical conductivity and a cost. Here, a term of "aluminum" means pure aluminum or an aluminum alloy.

A particular preferable positive electrode current collector is an aluminum foil.

The aluminum foil is not particularly limited, and examples thereof include: a material of A1085, and a material of A3003 as defined in Japanese Industrial standards.

The positive electrode mixture layer can be formed, for example, by applying a positive electrode mixture slurry including a positive electrode active material and a binder to a surface of a positive electrode current collector and then drying the slurry.

As a solvent included in the positive electrode mixture slurry, an organic solvent such as N-methyl-<NUM>-pyrrolidone (NMP) is preferable.

There are no particular limitation for the application method and the drying method in applicating the positive electrode mixture slurry on the positive electrode current collector and drying the slurry.

Examples of the application method include: slot-die coating, slide coating, curtain coating, and gravure coating.

Examples of the drying method include: drying with warm air, hot air, or low-humidity air; vacuum drying; and drying by infrared (e.g. far-infrared) irradiation.

A drying time and a drying temperature are not particularly limited, and the drying time is from <NUM> minute to <NUM> minutes, for example, and the drying temperature is from <NUM> to <NUM>, for example.

A method of manufacturing the positive electrode mixture layer preferably has a step of reducing a porosity of the positive electrode active material layer by pressurization treatment using a die press, a roll press, or the like, after the positive electrode mixture slurry has been applied onto the positive electrode current collector and the slurry has been dried.

The negative electrode in the battery precursor of the present embodiment is a negative electrode that is configured to intercalate and de-intercalate lithium ions.

The negative electrode in the battery precursor of the present embodiment preferably includes at least one negative electrode active material that is configured to intercalate and de-intercalate lithium ions.

The negative electrode in the battery precursor of the present embodiment more preferably includes: a negative electrode current collector; and a negative electrode mixture layer including a negative electrode active material and a binder.

The negative electrode mixture layer is provided on at least a part of a surface of the negative electrode current collector.

The negative electrode active material is not particularly limited as long as it is a material that is configured to intercalate and de-intercalate lithium ions, and, for example, at least one selected from the group consisting of metal lithium, a lithium-containing alloy, a metal or an alloy capable of being alloyed with lithium, an oxide capable of being doped/dedoped with lithium ions, a transition metal nitride capable of being doped/dedoped with lithium ions, and a carbon material capable of being doped/dedoped with lithium ions can be used (singly, or a mixture including two or more kinds thereof can be used).

Among them, a carbon material capable of being doped/dedoped with lithium ions is preferable.

Examples of the carbon material include: carbon black, activated carbon, a graphite material (e.g. artificial graphite, natural graphite, etc.), and an amorphous carbon material.

A form of the carbon material may be any of a fibrous form, a spherical form, a potato form, or a flake form.

A particle size of the carbon material is not particularly limited, and is, for example, from <NUM> to <NUM>, preferably from <NUM> to <NUM>.

Specific examples of the amorphous carbon material include: hard carbon, coke, mesocarbon microbeads (MCMB) calcined at <NUM> or lower, and mesophase pitch carbon fiber (MCF).

Examples of the graphite material include: natural graphite, and artificial graphite.

As the artificial graphite, graphitized MCMB, graphitized MCF, or the like is used.

As the graphite material, a graphite material that includes boron, or the like can also be used.

As the graphite material, a graphite material that is coated with a metal such as gold, platinum, silver, copper, or tin, a graphite material that is coated with amorphous carbon, or a mixture of amorphous carbon and graphite can also be used.

These carbon materials may be used singly, or in combination of two or more kinds thereof.

In a case in which the negative electrode in the battery precursor of the present embodiment includes a negative electrode current collector and a negative electrode mixture layer, the negative electrode mixture layer preferably includes a conductive auxiliary material.

Specific examples of the conductive auxiliary material that can be included in the negative electrode mixture layer are similar to the specific examples of the conductive auxiliary material that can be included in the positive electrode mixture layer described above.

In a case in which the negative electrode in the battery precursor of the present embodiment includes the negative electrode current collector and the negative electrode mixture layer, the negative electrode mixture layer may include another component in addition to each of the above-described components.

The negative electrode mixture layer can be formed, for example, by applying a negative electrode mixture slurry including a negative electrode active material and a binder to a surface of the negative electrode current collector and drying the slurry.

As a solvent included in the negative electrode mixture slurry, water is preferably used, but, if necessary, a liquid medium miscible with water may be used, for example, in order to improve an applicability to the current collector.

Examples of the liquid medium miscible with water include: an alcohol, a glycol, a cellosolve, an amino alcohol, an amine, a ketone, a carboxylic acid amide, a phosphoric acid amide, a sulfoxide, a carboxylate ester, a phosphoric ester, an ether, and a nitrile. The liquid medium may be used in a range of miscibility with water.

A preferable aspect of the method of forming the negative electrode mixture layer is similar to the preferable aspect of the method of forming the positive electrode mixture layer described above.

Examples of the separator in the battery precursor of the present embodiment include: a porous flat plate including a resin such as polyethylene (PE), polypropylene (PP), polyester, cellulose, or polyamide. Examples of the separator also include a non-woven fabric including the above-described resin.

Preferred examples include a porous resin sheet having a single layer or multilayer structure mainly including one kind of or two or more kinds of polyolefin resins.

A thickness of the separator can be, for example, from <NUM> to <NUM>.

The separator is preferably disposed between the positive electrode and the negative electrode.

The electrolyte solution in the battery precursor of the present embodiment is the nonaqueous electrolyte solution of the present embodiment described above.

The preferred aspect of the nonaqueous electrolyte solution of the present embodiment is as described above.

There is no particular limitation for the method of manufacturing the battery precursor of the present embodiment.

One example of the method of manufacturing the battery precursor of the present embodiment includes a step of housing a positive electrode, a negative electrode, a separator, and electrolyte solution into a case.

The one example described above preferably includes:.

The lithium secondary battery according to the present disclosure can be in various known shapes, and can be formed into a cylindrical shape, a coin shape, a square shape, a laminated shape, a film shape, or any other shape. However, a basic structure of the battery is identical regardless of the shape, and a design change can be made according to an intended purpose.

Examples of the lithium secondary battery according to the present disclosure include a laminated-type battery.

<FIG> is a schematic perspective view showing one example of a laminated-type battery, which is one example of a lithium secondary battery according to the present disclosure. <FIG> is a schematic cross-sectional view in a thickness direction of a laminated-type electrode body to be housed in the laminated-type battery shown in <FIG>.

The laminated-type battery shown in <FIG> includes a laminated exterior body <NUM> in which a nonaqueous electrolyte solution (not shown in <FIG>) and a laminated-type electrode body (not shown in <FIG>) are housed, and whose inside is sealed by sealing peripheral edge portions thereof. As the laminated exterior body <NUM>, a laminated exterior body made of aluminum is used, for example.

As shown in <FIG>, the laminated-type electrode body to be housed in the laminated exterior body <NUM> includes: a laminated body in which a positive electrode plate <NUM> and a negative electrode plate <NUM> are disposed one on another in layers with a separator <NUM> interposed therebetween; and a separator <NUM> that surrounds a periphery of the laminated body. The positive electrode plate <NUM>, the negative electrode plate <NUM>, the separator <NUM>, and the separator <NUM> are impregnated with the nonaqueous electrolyte solution of the present disclosure.

Each of plural positive electrode plates <NUM> in the laminated-type electrode body is electrically connected to a positive electrode terminal <NUM> via a positive electrode tab (not shown), and a part of the positive electrode terminal <NUM> protrudes outward from a peripheral end portion of the laminated exterior body <NUM> (<FIG>). A portion where the positive electrode terminal <NUM> protrudes at the peripheral end portion of the laminated exterior body <NUM> is sealed by an insulating seal <NUM>.

Similarly, each of plural negative electrode plates <NUM> in the laminated-type electrode body is electrically connected to a negative electrode terminal <NUM> via a negative electrode tab (not shown), and a part of the negative electrode terminal <NUM> protrudes outward from the peripheral end portion of the laminated exterior body <NUM> (<FIG>). A portion where the negative electrode terminal <NUM> protrudes at the peripheral end portion of the laminated exterior body <NUM> is sealed by an insulating seal <NUM>.

In the laminated-type battery according to the one example described above, the number of the positive electrode plates <NUM> is five, the number of the negative electrode plates <NUM> is six, and the positive electrode plates <NUM> and the negative electrode plates <NUM> are disposed in layers with the separators <NUM> interposed therebetween in such an arrangement that each of the outermost layers on opposite sides is a negative electrode plate <NUM>. However, the number of positive electrode plates, the number of negative electrode plates, and an arrangement in the laminated-type battery are not limited to this one example, and it is needless to say that various changes can be made.

Another one example of the lithium secondary battery according to the present disclosure includes a coin-type battery.

<FIG> is a schematic perspective view showing one example of a coin-type battery, which is another one example of the lithium secondary battery according to the present disclosure.

In the coin-type battery shown in <FIG>, a disk-shaped negative electrode <NUM>, a separator <NUM> into which a nonaqueous electrolyte solution is injected, a disk-shaped positive electrode <NUM>, and if necessary, spacer plates <NUM> and <NUM> made of stainless steel, aluminum, or the like are housed between a positive electrode can <NUM> (hereinafter, also referred to as a "battery can") and a sealing plate <NUM> (hereinafter, also referred to as a "battery can lid") in a state of being layered in this order. The positive electrode can <NUM> and the sealing plate <NUM> are caulked and sealed with a gasket <NUM> interposed therebetween.

In this one example, the nonaqueous electrolyte solution of the present disclosure is used as a nonaqueous electrolyte solution to be injected into the separator <NUM>.

The lithium secondary battery according to the present disclosure may be a lithium secondary battery obtained by charging and discharging a lithium secondary battery (lithium secondary battery before charging and discharging) including a negative electrode, a positive electrode, and the nonaqueous electrolyte solution of the present disclosure.

That is, the lithium secondary battery according to the present disclosure may be a lithium secondary battery (charged and discharged lithium secondary battery) prepared by first preparing a lithium secondary battery before charging and discharging that includes a negative electrode, a positive electrode, and the nonaqueous electrolyte solution of the present disclosure, and then charging and discharging one or more times the lithium secondary battery that is prior to charging and discharging.

A method of manufacturing a lithium secondary battery according to an embodiment of the present disclosure (hereinafter, also referred to as a "method of manufacturing a battery of the present embodiment") is
a method of manufacturing a lithium secondary battery including:.

The aging treatment in the aging step preferably includes:.

According to the preferred embodiment described above, a reduction of battery resistances of the lithium secondary battery after storage and after cycles is effectively achieved.

A preferred aspect of the nonaqueous electrolyte solution in the lithium secondary battery according to the present embodiment is similar to the preferred aspect of the nonaqueous electrolyte solution of the present embodiment except that the nonaqueous electrolyte solution is not limited to the nonaqueous electrolyte solution that includes the lithium borate compound of the present disclosure.

The nonaqueous electrolyte solution in the battery according to the present embodiment may include the lithium borate compound.

For example, in a case in which the battery according to the present embodiment is manufactured by the method of manufacturing a battery of the present embodiment, the lithium borate compound may be completely consumed, or some of the lithium borate compound may remain, by the aging treatment.

The additive for a lithium secondary battery of the present disclosure, the nonaqueous electrolyte solution for a lithium secondary battery of the present disclosure, the lithium secondary battery precursor of the present disclosure, the method of manufacturing a lithium secondary battery of the present disclosure, and the lithium secondary battery of the present disclosure, which are described above, are applicable to, for example, an electronic device such as a mobile phone or a notebook personal computer; an electric vehicle; a hybrid vehicle; a power source for power storage; and the like.

The additive for a lithium secondary battery of the present disclosure, the nonaqueous electrolyte solution for a lithium secondary battery of the present disclosure, the lithium secondary battery precursor of the present disclosure, the method of manufacturing a lithium secondary battery of the present disclosure, and the lithium secondary battery of the disclosure are particularly suitably used for a hybrid vehicle or an electric vehicle.

Hereinafter, examples of the present disclosure will be described, but the present disclosure is not limited to the following examples.

A <NUM> flask equipped with a stirrer, a thermometer, a gas introduction line, an exhaust line, and a dropping tube was prepared. After the <NUM> flask was purged with dry nitrogen gas, <NUM> (<NUM> mol) of potassium fluoride, <NUM> (<NUM> mol) of trimethyl borate, and <NUM> of tetrahydrofuran were added, and the mixture was stirred and mixed to give a slurry. While stirring the slurry, <NUM> (<NUM> mol) of (trifluoromethyl)trimethylsilane was added dropwise from the dropping tube, and the stirring was continued at room temperature (<NUM>) for <NUM> hours. The reaction solution after the reaction described above changed from the slurry prior to the start of the reaction to a homogeneous solution. This solution was filtered to remove dust, and the resultant filtrate was dried under a condition of <NUM> and <NUM> kPa or below to give <NUM> of a solid product.

A part of the resultant solid was dissolved in a deuterated water solvent, and subjected to <NUM>H-NMR analysis, <NUM>B-NMR analysis, and <NUM>F-NMR analysis at room temperature (<NUM>). The chemical shifts [ppm] of the spectra obtained by each of the NMR analyses were as follows.

The resultant product was confirmed from the above-described NMR spectrum patterns to be potassium trimethoxy(trifluoromethyl)borate, which is a reaction intermediate shown in the following reaction scheme.

Together with <NUM> of methanol, <NUM> (<NUM> mol) of the reaction intermediate was added into the original reaction flask, then <NUM> (<NUM> mol) of lithium chloride was added thereto, and the mixture was stirred and mixed to give a homogeneous solution. Thereafter, this solution was heated to <NUM> and stirred in a solvent reflux condition for <NUM> hour. The reaction solution obtained by this step changed from the homogeneous solution to a slurry in which a solid salt was precipitated. The slurry was filtered to remove the solid, and the filtrate was dried under a condition of <NUM> and <NUM> kPa or below to give <NUM> of a white crystalline solid product.

A part of the resultant solid was dissolved in a deuterated water solvent, and subjected to <NUM>H-NMR analysis, <NUM>Li-NMR analysis, <NUM>B-NMR analysis, and <NUM>F-NMR analysis at room temperature (<NUM>). The chemical shifts [ppm] of the spectra obtained by each of the NMR analyses were as follows.

As described above, the product obtained by the synthesis of Example <NUM> was confirmed to be a lithium borate compound of the present disclosure shown by the following reaction scheme, that is, a lithium borate compound represented by Formula (II) (hereinafter, also referred to as a "lithium borate compound (II)").

The synthesis was conducted in the same manner as in Example <NUM>, except that the second reaction step in Example <NUM> was changed to the method shown below.

Together with <NUM> of ethanol, <NUM> (<NUM> mol) of the reaction intermediate was added into the original reaction flask, and then <NUM> (<NUM> mol) of lithium chloride was added thereto and stirred and mixed to give a homogeneous solution. Thereafter, the solution was heated to <NUM> and stirred in a solvent reflux condition for <NUM> hour. The reaction solution obtained by this step changed from the homogeneous solution to a slurry in which a solid salt was precipitated. The slurry was filtered to remove the solid, and the filtrate was dried under a condition of <NUM> and <NUM> kPa or below to give <NUM> of a white crystalline solid product.

As described above, the product obtained by the synthesis of Example <NUM> was confirmed to be a lithium borate compound of the present disclosure shown by the following reaction scheme, that is, a lithium borate compound (hereinafter, also referred to as a "lithium borate compound (III)") represented by Formula (III).

Together with <NUM> of isopropanol, <NUM> (<NUM> mol) of the reaction intermediate was added into the original reaction flask, and then <NUM> (<NUM> mol) of lithium chloride was added thereto and stirred and mixed to obtain a homogeneous solution. Thereafter, the solution was heated to <NUM> and stirred for <NUM> hour in a solvent reflux condition. The reaction solution obtained by this step changed from the homogeneous solution to a slurry in which a solid salt was precipitated. The slurry was filtered to remove the solid, and the filtrate was dried under a condition of <NUM> and <NUM> kPa or below to give <NUM> of a white crystalline solid product.

As described above, the product obtained by the synthesis of Example <NUM> was confirmed to be a lithium borate compound of the present disclosure shown by the following reaction scheme, that is, a lithium borate compound represented by Formula (IV) (hereinafter, also referred to as a "lithium borate compound (IV)").

The synthesis was conducted in the same manner as in Example <NUM>, except that the second reaction step in Example <NUM> was changed to the synthesis method shown below.

Together with <NUM> of n-butanol, <NUM> (<NUM> mol) of the reaction intermediate was added into the original reaction flask, and then <NUM> (<NUM> mol) of lithium chloride was added thereto and stirred and mixed to give a homogeneous solution. Thereafter, the solution was heated to <NUM> and stirred at this temperature for <NUM> hour. The reaction solution obtained by this step changed from the homogeneous solution to a slurry in which a solid salt was precipitated. The slurry was filtered to remove the solid, and the filtrate was dried under a condition of <NUM> and <NUM> kPa or below to give <NUM> of a white crystalline solid product.

As described above, the product obtained by the synthesis of Example <NUM> was confirmed to be a lithium borate compound of the present disclosure shown by the following reaction scheme, that is, a lithium borate compound represented by Formula (V) (hereinafter, also referred to as a "lithium borate compound (V)").

A coin-type lithium secondary battery (hereinafter, also referred to as a "coin-type battery") having a configuration shown in <FIG> was fabricated by the following procedure.

Amorphous coated natural graphite (<NUM> parts by mass), carboxymethyl cellulose (<NUM> part by mass) and SBR latex (<NUM> parts by mass) were kneaded with an aqueous solvent to prepare a paste-like negative electrode mixture slurry.

Next, the negative electrode mixture slurry was applied to a negative electrode current collector made of a strip-shaped copper foil having a thickness of <NUM>, and the slurry was dried, then the applied negative electrode current collector was compressed by a roll press to give a sheet-shaped negative electrode that includes the negative electrode current collector and a negative electrode active material layer. A coating density and a packing density of the negative electrode active material layer at this time were <NUM>/cm<NUM> and <NUM>/ml, respectively.

LiNi<NUM>Mn<NUM>Co<NUM>O<NUM> (<NUM> parts by mass), acetylene black (<NUM> parts by mass) and polyvinylidene fluoride (<NUM> parts by mass) were kneaded with N-methylpyrrolidinone as a solvent to prepare a paste-like positive electrode mixture slurry.

Next, the positive electrode mixture slurry was applied to a positive electrode current collector of a strip-shaped aluminum foil having a thickness of <NUM>, and the slurry was dried, then the applied positive electrode current collector was compressed by a roll press to give a sheet-like positive electrode that includes the positive electrode current collector and a positive electrode active material layer. A coating density and a packing density of the positive electrode active material layer at this time were <NUM>/cm<NUM> and <NUM>/ml, respectively.

As a nonaqueous solvent, ethylene carbonate (EC), dimethyl carbonate (DMC), and methylethyl carbonate (EMC) were mixed at a ratio of <NUM>:<NUM>:<NUM> (volume ratio), respectively, to give a mixed solvent.

In the resultant mixed solvent, LiPF<NUM> as an electrolyte was dissolved so that an electrolyte concentration became <NUM> mol/liter in a finally prepared nonaqueous electrolyte solution.

To the resultant solution, the lithium borate compound (II) was added by an addition amount shown in Table <NUM> and dissolved, thereby obtaining a nonaqueous electrolyte solution.

The negative electrode described above was punched into a disk shape having a diameter of <NUM>, and the positive electrode described above was punched into a disk shape having a diameter of <NUM> to give a coin-shaped negative electrode and a coin-shaped positive electrode, respectively. A microporous polyethylene film having a thickness of <NUM> was punched into a disk shape having a diameter of <NUM> to give a separator.

The obtained coin-shaped negative electrode, separator, and coin-shaped positive electrode were layered in this order in a stainless steel battery can (a size of <NUM> type), and then <NUM>µL of the above-described nonaqueous electrolyte solution was injected into the battery can so as to be impregnated into the separator, the positive electrode, and the negative electrode.

Next, an aluminum plate (thickness: <NUM>, diameter: <NUM>) and a spring were placed on the positive electrode, and the battery was sealed by caulking a battery can lid with a polypropylene gasket interposed therebetween.

As described above, a coin-type battery (i.e. a coin-type lithium secondary battery) that had a configuration shown in <FIG> having a diameter of <NUM> and a height of <NUM> was obtained.

A lithium secondary battery was fabricated in the same manner as in Example <NUM> except that a type of an additive included in the nonaqueous electrolyte solution was changed as shown in Table <NUM>, and the following evaluation was made in the same manner as in Example <NUM>. The results are shown in Table <NUM>.

An evaluation of a direct current resistance was made for each of batteries of Examples <NUM> to <NUM> and Comparative Example <NUM> as an evaluation of an internal resistance of the battery.

A coin-type battery was three times repeatedly charged and discharged at a constant voltage of <NUM> V, and then charged up to a constant voltage of <NUM> V. Next, the charged coin-type battery was cooled to <NUM> in a thermostatic chamber, and discharged at a constant current of <NUM> mA at <NUM>, and then a decrease in potential was measured during <NUM> seconds from the start of discharge so that a direct current resistance [Ω] of the coin-type battery was determined. The obtained value was defined as an initial resistance [Ω] (<NUM>). An initial resistance [Ω] (<NUM>) of a coin-type battery of Comparative Example <NUM> described later was determined in the same manner.

From these results, based on the following Formula, an "initial resistance (<NUM>) (relative value; %)" is determined as an initial resistance (relative value; %) in Example <NUM> in a case in which an initial resistance [Ω] (<NUM>) in Comparative Example <NUM> was defined as <NUM>%. The results are shown in Table <NUM>.

The coin-type battery was three times repeatedly charged and discharged at a constant voltage of <NUM> V, then charged up to <NUM> V, and was stored at <NUM> for <NUM> days. The direct current resistance of the battery after storage for <NUM> days was determined by the same method as the method for the initial resistance described above, and the obtained value of the direct current resistance was defined as a direct current resistance for the battery after <NUM> days of storage.

Respective relative values for the values of the direct current resistance for the battery after <NUM> days of storage were determined in a case in which the initial value for the direct current resistance of the battery in Comparative Example <NUM> was defined as <NUM>.

In Table <NUM>, the initial direct current resistance in Comparative Example <NUM> was shown as <NUM>, and the relative values described above (i.e. the relative values in a case in which the initial direct current resistance in Comparative Example <NUM> was defined as <NUM>) of the direct current resistances after <NUM> days of storage were shown.

Table <NUM> shows that, the battery resistances after storage in Examples, in which the lithium borate compound of the present disclosure was included in the nonaqueous solvent, were reduced as compared with the battery resistance after storage in Comparative Example.

A lithium secondary battery was fabricated in the same manner as in Example <NUM> except that a type and a content of an additive included in the nonaqueous electrolyte solution were changed as shown in Table <NUM>.

The following evaluation was made for the resultant coin-type batteries shown in Table <NUM>.

For each battery obtained in each example, the direct current resistance was evaluated as an evaluation of an internal resistance of the battery after the cycle. Details are shown below.

The following operation was conducted at a temperature condition of <NUM>.

A battery was charged up to SOC <NUM>% at a charge rate of <NUM>. 2C, and then discharged to SOC <NUM>% at a discharge rate of 1C, and this cycle was conducted for <NUM> cycle, <NUM> cycles, and <NUM> cycles.

A direct current resistance (Ω) of a battery obtained after each cycle was measured by the following method. The relative value was determined in a case in which a value of direct current resistance after <NUM> cycle (i.e. at an initial stage) of the battery in Comparative Example <NUM> was defined as <NUM>. The results are shown in Table <NUM>.

The coin-type battery was three times repeatedly charged and discharged at a constant voltage of <NUM> V, and then charged up to a constant voltage of <NUM> V. Next, the charged coin-type battery was cooled to -<NUM> in a thermostatic chamber, and discharged at a constant current of <NUM> mA at -<NUM>, and then a decrease in potential during <NUM> seconds from the start of discharge was measured so that the direct current resistance [Ω] of the coin-type battery was determined, and the obtained value was defined as a resistance after <NUM> cycle (also referred to as an "initial resistance [Ω] (-<NUM>)"). The initial resistance [Ω] (-<NUM>) was measured in the same manner for a coin-type battery of Comparative Example <NUM> described later.

From these results, based on the following Formula, the "initial resistance (-<NUM>) (relative value; %) was determined as an initial resistance (relative value; %) in Example <NUM> in a case in which the initial resistance [Ω] (-<NUM>) of Comparative Example <NUM> was defined as <NUM>%. The results are shown in Table <NUM>.

Table <NUM> shows that the battery resistances after cycles in Examples, in which the lithium borate compound of the present disclosure was included in the nonaqueous solvent, were reduced as compared with those in Comparative Example.

A lithium secondary battery was fabricated in the same manner as in Example <NUM> except that a nonaqueous electrolyte solution was prepared with a type and a content of the lithium borate compound included in the nonaqueous electrolyte solution as shown in Table <NUM>, and also with a content of vinylene carbonate included in the nonaqueous electrolyte solution as shown in Table <NUM>.

An evaluation of battery resistances after cycles was made for the obtained coin-type batteries shown in Table <NUM> by the same method as the method of measuring the direct current resistance (Ω) of the battery obtained after each cycle described above. The results are shown in Table <NUM>.

Claim 1:
An additive for a lithium secondary battery, the additive comprising a lithium borate compound represented by the following Formula (I):
<CHM>
wherein, in Formula (I), each of R<NUM>, R<NUM>, and R<NUM> independently represents a hydrocarbon group having from <NUM> to <NUM> carbon atoms, which does not have a substituent, and R<NUM> represents a trifluoromethyl group.