Patent Description:
A thermoplastic resin composition including a polycarbonate resin, a rubber modified aromatic vinyl copolymer resin and a flame retardant has good impact resistance, flame retardancy and processability, and is advantageously used for interior/exterior materials for office machines and housings of electric/electronic devices that radiate heat.

However, articles formed of the thermoplastic resin composition including a polycarbonate resin and a rubber modified aromatic vinyl copolymer resin may become yellow over time and various bacteria may proliferate on the surface. In order to improve weather resistance and antibacterial properties of the thermoplastic resin composition, antibacterial agents and weathering stabilizers may be applied, but there is a problem that compatibility and impact resistance are deteriorated, and gas can be generated during injection molding due to resin decomposition.

Therefore, there is a need for a thermoplastic resin composition that is excellent in antibacterial properties, weather resistance, impact resistance, thermal resistance, and the like.

The background technique of the present invention is disclosed in <CIT>.

It is also disclosed in <CIT> which describes a thermoplastic resin composition and a molded article produced therefrom, said composition comprising <NUM>-<NUM> wt% of a polycarbonate resin; <NUM>-<NUM> wt% of an aromatic vinyl resin; an inorganic filler; a maleic anhydride-grafter rubber; and a phosphorus flame retardant; said composition exhibiting a low shrinkage, an good impact resistance and a good flexural modulus.

It is one object of the present invention to provide a thermoplastic resin composition having good properties in terms of antibacterial properties, weather resistance, impact resistance, thermal resistance, and the like.

It is another object of the present invention to provide a molded article formed of the thermoplastic resin composition.

The above and other objects of the present invention can be achieved by the present invention described below.

The present invention provides a thermoplastic resin composition having good properties in terms of antibacterial properties, weather resistance, impact resistance, thermal resistance, and the like, and a molded article formed therefrom.

A thermoplastic resin composition according to the present invention comprises (A) a polycarbonate resin; (B) a rubber modified aromatic vinyl copolymer resin; (C) a zinc oxide; (D) an alkyl phosphate; (E) a maleic anhydride-grafted rubber polymer; and (F) phosphite antioxidant.

The polycarbonate resin may be a polycarbonate resin used in a typical thermoplastic resin composition. For example, the polycarbonate resin may be an aromatic polycarbonate resin prepared by reacting a diphenol(s) (aromatic diol compounds) with a precursor, such as phosgene, halogen formate, carbonate diester, and the like.

In some embodiments, the diphenols may include, for example, <NUM>,<NUM>'-biphenol, <NUM>,<NUM>-bis(<NUM>-hydroxyphenyl)-propane, <NUM>,<NUM>-bis(<NUM>-hydroxyphenyl)-<NUM>-methylbutane, <NUM>,<NUM>-bis(<NUM>-hydroxyphenyl)cyclohexane, <NUM>,<NUM>-bis(<NUM>-chloro-<NUM>-hydroxyphenyl)propane, and <NUM>,<NUM>-bis-(<NUM>,<NUM>-dichloro-<NUM>-hydroxyphenyl)propane, without being limited thereto. For example, the diphenols may be <NUM>,<NUM>-bis(<NUM>-hydroxyphenyl)propane, <NUM>,<NUM>-bis(<NUM>,<NUM>-dichloro-<NUM>-hydroxyphenyl)propane or <NUM>,<NUM>-bis(<NUM>-hydroxyphenyl)cyclohexane, specifically <NUM>,<NUM>-bis(<NUM>-hydroxyphenyl)propane, which is also referred to as bisphenol-A.

In some embodiments, the polycarbonate resin may be a branched polycarbonate resin. For example, the polycarbonate resin may be a polycarbonate resin prepared by adding a tri- or higher polyfunctional compound, specifically, a tri- or higher valent phenol group-containing compound, in an amount of about <NUM> mol% to about <NUM> mol% based on the total number of moles of the diphenols used in polymerization.

In some embodiments, the polycarbonate resin may be a homopolycarbonate resin, a copolycarbonate resin, or a blend thereof. In addition, the polycarbonate resin may be partly or completely replaced by an aromatic polyester-carbonate resin obtained by polymerization in the presence of an ester precursor, for example, a bifunctional carboxylic acid.

In some embodiments, the polycarbonate resin may have a weight average molecular weight (Mw) of about <NUM>,<NUM>/mol to about <NUM>,<NUM>/mol, for example, about <NUM>,<NUM>/mol to about <NUM>,<NUM>/mol, as measured by gel permeation chromatography (GPC). Within this range, the thermoplastic resin composition may have good mechanical properties, flowability (processability), and the like. In addition, the polycarbonate resin may be a mixture of two or more polycarbonate resins having different weight average molecular weights.

According to one embodiment of the invention, the rubber modified aromatic vinyl copolymer resin may include (B1) a rubber modified vinyl graft copolymer and (B2) an aromatic vinyl copolymer resin.

According to one embodiment of the invention, the rubber modified vinyl graft copolymer may be obtained by graft polymerization of a monomer mixture comprising an aromatic vinyl monomer and a vinyl cyanide monomer to a rubber polymer. For example, the rubber modified vinyl graft copolymer may be obtained by graft polymerization of the monomer mixture comprising the aromatic vinyl monomer and the vinyl cyanide monomer to the rubber polymer, in which the monomer mixture may further include a monomer for imparting processability and thermal resistance, as needed. Here, polymerization may be performed by any typical polymerization method, such as emulsion polymerization, suspension polymerization, and the like. In addition, the rubber modified vinyl graft copolymer may form a core (rubber polymer)-shell (copolymer of the monomer mixture) structure, without being limited thereto.

In some embodiments, the rubber polymer may include diene rubbers, such as polybutadiene, poly(styrene-butadiene), and poly(acrylonitrile-butadiene); saturated rubbers obtained by adding hydrogen to the diene rubbers; isoprene rubbers; C<NUM> to C<NUM> alkyl (meth)acrylate rubbers; a copolymer of a C<NUM> to C<NUM> alkyl (meth)acrylate and styrene; and ethylene-propylene-diene monomer terpolymer (EPDM), and the like. These may be used alone or as a mixture thereof. For example, the rubber polymer may include diene rubbers and C2 to C10 alkyl (meth)acrylate rubbers. Specifically, the rubber polymer may include butadiene rubber, butyl acrylate rubber and the like.

The rubber polymer (rubber particle) may have an average particle diameter (Z-average) of about <NUM> to about <NUM>, for example, about <NUM> to about <NUM>, specifically about <NUM> to about <NUM>. Within this range, the thermoplastic resin composition can have good properties in terms of impact resistance, external appearance, and the like. Here, the average particle diameter (Z-average) of the rubber polymer (rubber particles) may be measured by a light scattering method in a latex state. Specifically, a rubber polymer latex is filtered through a mesh to remove coagulum generated during polymerization of the rubber polymer. Then, a mixed solution of <NUM> of the latex and <NUM> of distilled water is poured in a <NUM>,<NUM> flask, and filled with distilled water to prepare a specimen. Then, <NUM> of the specimen is transferred to a quartz cell, followed by measurement of the average particle diameter of the rubber polymer using a light scattering particle analyzer (Malvern Co. , nano-zs).

In some embodiments, based on <NUM> wt% of the rubber modified vinyl graft copolymer, the rubber polymer may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%, and the monomer mixture (including the aromatic vinyl monomer and the vinyl cyanide monomer) may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%. Within this range, the thermoplastic resin composition can have good properties in terms of impact resistance, external appearance, and the like.

In some embodiments, the aromatic vinyl monomer may be graft copolymerizable with the rubber polymer and may include, for example, styrene, α-methylstyrene, β-methylstyrene, p-methylstyrene, p-t-butylstyrene, ethylstyrene, vinylxylene, monochlorostyrene, dichlorostyrene, dibromostyrene, and vinyl naphthalene, without being limited thereto. These may be used alone or as a mixture thereof. The aromatic vinyl monomer may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%, based on <NUM> wt% of the monomer mixture. Within this range, the thermoplastic resin composition can have good properties in terms of processability, impact resistance, and the like.

In some embodiments, the vinyl cyanide monomer is copolymerizable with the aromatic vinyl monomer, and may include, for example, acrylonitrile, methacrylonitrile, ethacrylonitrile, phenyl acrylonitrile, α-chloroacrylonitrile, fumaronitrile, and the like. These may be used alone or as a mixture thereof. For example, the vinyl cyanide monomer may be acrylonitrile or methacrylonitrile. The vinyl cyanide monomer may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%, based on <NUM> wt% of the monomer mixture. Within this range, the thermoplastic resin composition can have good properties in terms of chemical resistance, mechanical properties, and the like.

Examples of the monomer for imparting processability and thermal resistance may include (meth)acrylic acid, maleic anhydride, and N-substituted maleimide, without being limited thereto. The monomer for imparting processability and thermal resistance may be present in an amount of about <NUM> wt% or less, for example, about <NUM> wt% to about <NUM> wt%, based on <NUM> wt% of the monomer mixture. Within this range, the monomer for imparting processability and thermal resistance can impart processability and thermal resistance to the thermoplastic resin composition without deterioration in other properties.

Examples of the rubber modified vinyl graft copolymer may include a g-ABS copolymer obtained by grafting a styrene monomer (as the aromatic vinyl monomer) and an acrylonitrile monomer (as the vinyl cyanide monomer) to a butadiene-based rubber polymer, a g-MBS copolymer obtained by grafting a styrene monomer (as the aromatic vinyl monomer) and methyl methacrylate (as the monomer copolymerizable therewith) to a butadiene-based rubber polymer, an acrylate-styrene-acrylate (g-ASA) copolymer obtained by grafting a styrene monomer (as the aromatic vinyl monomer) and an acrylonitrile monomer (as the vinyl cyanide monomer) to a butyl acrylate-based rubber polymer, and the like. For example, g-MBS , and the like can be used.

According to the embodiment of the invention, the aromatic vinyl copolymer resin may be an aromatic vinyl copolymer resin used for a typical rubber modified aromatic vinyl graft copolymer resin. For example, the aromatic vinyl copolymer resin may be a polymer of a monomer mixture comprising an aromatic vinyl monomer and a monomer copolymerizable with the aromatic vinyl monomer.

In some embodiments, the aromatic vinyl copolymer resin may be obtained by mixing the aromatic vinyl monomer and the monomer copolymerizable with the aromatic vinyl monomer, followed by polymerization. Here, polymerization may be carried out by any well-known polymerization method, such as emulsion polymerization, suspension polymerization, bulk polymerization, and the like.

Examples of the aromatic vinyl monomer may include styrene, α-methylstyrene, β-methylstyrene, p-methylstyrene, p-t-butylstyrene, ethylstyrene, vinylxylene, monochlorostyrene, dichlorostyrene, dibromostyrene, vinyl naphthalene, and the like. These may be used alone or as a mixture thereof. The aromatic vinyl monomer may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%, based on <NUM> wt% of the aromatic vinyl copolymer resin. Within this range, the thermoplastic resin composition can exhibit good properties in terms of impact resistance, fluidity, and the like.

In some embodiments, the monomer copolymerizable with the aromatic vinyl monomer may include at least one of a vinyl cyanide monomer and an alkyl (meth)acrylic monomer. For example, the monomer copolymerizable with the aromatic vinyl monomer may include a vinyl cyanide monomer, or a combination of a vinyl cyanide monomer and an alkyl (meth)acrylic monomer, specifically a vinyl cyanide monomer and an alkyl (meth)acrylic monomer.

Examples of the vinyl cyanide monomer may include acrylonitrile, methacrylonitrile, ethacrylonitrile, phenylacrylonitrile, α-chloroacrylonitrile, and fumaronitrile, without being limited thereto. These may be used alone or as a mixture thereof. For example, acrylonitrile, methacrylonitrile, and the like may be used.

In some embodiments, the alkyl (meth)acrylic monomer may include (meth)acrylic acid and/or C<NUM> to C<NUM> alkyl (meth)acrylates. These may be used alone or as a mixture thereof. For example, methyl methacrylate, methyl acrylate, and the like may be used.

In some embodiments, when the monomer copolymerizable with the aromatic vinyl monomer is a mixture of the vinyl cyanide monomer and the alkyl (meth)acrylic monomer, the vinyl cyanide monomer may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%, and the alkyl (meth)acrylic monomer may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%, based on <NUM> wt% of the monomer copolymerizable with the aromatic vinyl monomer. Within this range, the thermoplastic resin composition can exhibit good properties in terms of transparency, thermal resistance, processability, and the like.

In some embodiments, the monomer copolymerizable with the aromatic vinyl monomer may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%, based on <NUM> wt% of the aromatic vinyl copolymer resin. Within this range, the thermoplastic resin composition can exhibit good properties in terms of impact resistance, fluidity, and the like.

In some embodiments, the aromatic vinyl copolymer resin may have a weight average molecular weight (Mw) of about <NUM>,<NUM>/mol to about <NUM>,<NUM>/mol, for example, about <NUM>,<NUM>/mol to about <NUM>,<NUM>/mol, as measured by gel permeation chromatography (GPC). Within this range, the thermoplastic resin exhibits good properties in terms of mechanical strength, processability, and the like.

In some embodiments, when the rubber modified aromatic vinyl copolymer resin(B) includes (B1) a rubber modified vinyl graft copolymer and (B2) an aromatic vinyl copolymer resin, the rubber modified vinyl graft copolymer may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%, based on <NUM> wt% of the rubber modified aromatic vinyl copolymer resin, and the aromatic vinyl copolymer resin may be present in an amount of about <NUM> wt% to about <NUM> wt%, for example, about <NUM> wt% to about <NUM> wt%, based on <NUM> wt% of the rubber modified aromatic vinyl copolymer resin. Within this range, the thermoplastic resin composition can exhibit good properties in terms of impact resistance, fluidity (molding processability), and the like.

In some embodiments, the rubber modified aromatic vinyl copolymer resin may be present in an amount of about <NUM> parts by weight to about <NUM> parts by weight, for example, about <NUM> parts by weight to about <NUM> parts by weight, relative to <NUM> parts by weight of the polycarbonate resin. If the amount of the rubber modified aromatic vinyl copolymer resin is less than <NUM> part by weight, the thermoplastic resin composition can suffer from deterioration in impact resistance, and the like, and if the amount of the rubber modified aromatic vinyl copolymer resin exceeds <NUM> parts by weight, the thermoplastic resin composition can suffer from deterioration in stiffness (flexural modulus, etc.), thermal resistance (retention heat stability during injection).

According to the present invention, the zinc oxide serves to improve antibacterial properties, weather resistance, impact resistance, thermal resistance and balance therebetween of the thermoplastic resin composition together with the alkyl phosphate and the phosphite antioxidant. The zinc oxide may have an average particle diameter (D50) of primary particles (not forming a secondary particle through agglomeration of particles) of about <NUM> to about <NUM>, for example, about <NUM> to about <NUM>, as measured using a particle size analyzer (Laser Diffraction Particle Size Analyzer LS I3 <NUM>, Beckman Coulter Co. Further, the zinc oxide may have a BET specific surface area of about <NUM><NUM>/g to about <NUM><NUM>/g, for example, about <NUM><NUM>/g to about <NUM><NUM>/g, as measured by a nitrogen gas adsorption method using a BET analyzer (Surface Area and Porosity Analyzer ASAP <NUM>, Micromeritics Co. ) and may have a purity of about <NUM>% or higher. If these parameters of the zinc oxide are outside these ranges, the thermoplastic resin composition may have poor properties in terms of weather resistance (light resistance, discoloration resistance) and antibacterial properties.

In one embodiment, the zinc oxide may have a peak position degree (2θ) in the range of <NUM>° to <NUM>° and a crystallite size of about <NUM>,<NUM>Å to about <NUM>,<NUM>Å, for example, about <NUM>,<NUM>Å to about <NUM>,<NUM>Å in analysis of X-ray diffraction (XRD), as calculated by Scherrer's Equation (Equation <NUM>) with reference to a measured FWHM value (full width at half maximum of a diffraction peak). If these parameters of the zinc oxide are outside these ranges, the thermoplastic resin composition may have poor properties in terms of weather resistance (light resistance, discoloration resistance), antibacterial properties, and the like. <MAT>
where K is a shape factor, λ is an X-ray wavelength, β is an FWHM value (degree), and θ is a peak position degree.

In some embodiments, the zinc oxide may have various shape, for example, a spherical shape, a plate shape, a rod shape, a combination thereof, and the like.

In some embodiments, the zinc oxide may have a peak intensity ratio (B/A) of about <NUM> to about <NUM>, for example, about <NUM> to about <NUM>, specifically about <NUM> to about <NUM>, where A indicates a peak in the wavelength range of <NUM> to <NUM> and B indicates a peak in the wavelength range of <NUM> to <NUM> in photoluminescence measurement. Within this range, the thermoplastic resin composition may have good properties in terms of weather resistance, antibacterial properties, impact resistance and the like.

In some embodiments, the zinc oxide may be prepared by melting metallic zinc in a reactor, heating the molten zinc to about <NUM> to about <NUM>,<NUM>, for example, about <NUM> to about <NUM>, to vaporize the molten zinc, injecting oxygen gas into the reactor, cooling the reactor to about <NUM> to about <NUM>, followed by heating the reactor to about <NUM> to about <NUM>, for example about <NUM> to about <NUM> for about <NUM> minutes to about <NUM> minutes, for example, about <NUM> minutes to about <NUM> minutes.

In some embodiments, the zinc oxide may be present in an amount of about <NUM> part by weight to about <NUM> parts by weight, for example, about <NUM> part by weight to about <NUM> parts by weight, specifically, about <NUM> parts by weight to about <NUM> parts by weight, relative to about <NUM> parts by weight of the polycarbonate resin. If the amount of the zinc oxide is less than <NUM> part by weight, the thermoplastic resin composition can suffer from deterioration in weather resistance (light resistance, discoloration resistance), antibacterial properties. If the amount of the zinc oxide is more than <NUM> parts by weight, impact resistance and thermal resistance (retention heat stability during injection) of the thermoplastic resin composition could be deteriorated.

The alkyl phosphate may serve to improve impact resistance, weather resistance, antibacterial properties, thermal resistance, and the like of the thermoplastic resin composition together with the zinc oxide and the phosphite antioxidant, and C<NUM> to C<NUM> alkyl phosphate can be used.

In some embodiments, examples of the alkyl phosphate may include dodecyl phosphate, tetradecyl phosphate, hexadecyl phosphate, octadecyl phosphate, and the like. These can be used alone or in combination of two or more. For example, the alkyl phosphate may be octadecyl phosphate.

In some embodiments, the alkyl phosphate may be present in an amount of about <NUM> parts by weight to about <NUM> parts by weight, for example about <NUM> parts by weight to about <NUM> part by weight, specifically, about <NUM> parts by weight to about <NUM> parts by weight, relative to about <NUM> parts by weight of the polycarbonate resin. If the amount of the alkyl phosphate is less than <NUM> part by weight, the thermoplastic resin composition can suffer from deterioration in thermal resistance (retention heat stability during injection). If the amount of the alkyl phosphate is more than <NUM> parts by weight, impact resistance and thermal resistance of the thermoplastic resin composition could be deteriorated.

In some embodiments, the zinc oxide and the alkyl phosphate may be present in a weight ratio (zinc oxide : alkyl phosphate) of about about <NUM> : <NUM> to about <NUM> : <NUM>, for example about <NUM> : <NUM> to about <NUM> : <NUM>. Within this range, the thermoplastic resin composition may have further improved properties in terms of antibacterial properties, weather resistance, impact resistance and balance therebetween.

The maleic anhydride-grafted rubber polymer according to one embodiment of the invention serves to improve flowability, impact resistance, thermal stability of the thermoplastic resin composition, and may be prepared by graft polymerization of maleic anhydride (MAH) to a rubber polymer (a copolymer of olefin and/or an aromatic vinyl monomer).

In some embodiments, the maleic anhydride-grafted rubber polymer may include at least one of maleic anhydride-grafted ethylene-octene rubber (MAH-g-EOR), maleic anhydride-grafted ethylene-butene rubber (MAH-g-EBR), maleic anhydride-grafted ethylene-propylene-diene monomer terpolymer (MAH-g-EPDM), maleic anhydride-grafted styrene-ethylene-butadiene-styrene copolymer (MAH-g-SEBS), maleic anhydride-grafted polypropylene (MAH-g-PP), and maleic anhydride-grafted polyethylene (MAH-g-PE).

In some embodiments, the maleic anhydride may be present in an amount of about <NUM> wt% to about <NUM> wt% and the rubber polymer may be present in an amount of about <NUM> wt% to about <NUM> wt% based on <NUM> wt% of the maleic anhydride-grafted rubber polymer, without being limited thereto.

In some embodiments, the maleic anhydride-grafted rubber polymer may be present in an amount of about <NUM> parts by weight to about <NUM> parts by weight, for example, about <NUM> parts by weight to about <NUM> part by weight, relative to about <NUM> parts by weight of the polycarbonate resin. If the amount of the maleic anhydride-grafted rubber polymer is less than <NUM> part by weight, the thermoplastic resin composition can suffer from deterioration in impact resistance, thermal resistance (retention heat stability during injection). If the amount of the maleic anhydride-grafted rubber polymer is more than <NUM> parts by weight, stiffness (flexural modulus, tensile strength, etc.) of the thermoplastic resin composition could be deteriorated.

According to the present invention, the phosphite antioxidant is applied together with the zinc oxide and the alkyl phosphate in preparation of the thermoplastic resin composition to improve impact resistance, weather resistance, antibacterial properties, thermal resistance, and the like of the thermoplastic resin composition, and the phosphite antioxidant may be a phosphite antioxidant used in a typical thermoplastic resin composition.

In one embodiment, the phosphite antioxidant may include at least one of bis(<NUM>,<NUM>-di-tert-butyl-<NUM>-methylphenyl)pentaerythritol diphosphite, bis(<NUM>,<NUM>-di-tert-butyl-<NUM>-ethylphenyl)pentaerythritol diphosphite, bis(<NUM>,<NUM>-dicumylphenyl) pentaerythritol diphosphate. For example, bis(<NUM>,<NUM>-di-tert-butyl-<NUM>-methylphenyl)pentaerythritol diphosphite can be used.

In some embodiments, the phosphite antioxidant may be present in an amount of about <NUM> part by weight to about <NUM> parts by weight, for example, about <NUM> parts by weight to about <NUM> part by weight, specifically, about <NUM> part by weight to about <NUM> parts by weight, relative to about <NUM> parts by weight of the polycarbonate resin. If the amount of the phosphite antioxidant is less than <NUM> part by weight, the thermoplastic resin composition can suffer from deterioration in weather resistance (discoloration resistance). If the amount of the phosphite antioxidant is more than <NUM> parts by weight, impact resistance and thermal resistance (retention heat stability during injection) of the thermoplastic resin composition could be deteriorated.

In some embodiments, the zinc oxide and the phosphite antioxidant may be present in a weight ratio (zinc oxide : phosphite antioxidant) of about <NUM> : <NUM> to about <NUM> : <NUM>, for example about <NUM> : <NUM> to about <NUM> : <NUM>. Within this range, the thermoplastic resin composition may have further improved properties in terms of antibacterial properties, weather resistance, impact resistance, thermal resistance and balance therebetween.

In one embodiment, the thermoplastic resin composition may further include any typical additive included in thermoplastic resin compositions. Examples of the additive may include a flame retardant, an anti-dripping agent, a lubricant, a nucleating agent, a stabilizer, a release agent, pigments, dyes, and the like, and mixtures thereof, without being limited thereto. The additives may be present in an amount of about <NUM> parts by weight to about <NUM> parts by weight, for example, about <NUM> parts by weight to about <NUM> parts by weight, relative to about <NUM> parts by weight of the thermoplastic resin.

The thermoplastic resin composition may be prepared in pellet form by mixing the aforementioned components, followed by melt extrusion using a typical twin-screw extruder at about <NUM> to about <NUM>, for example about <NUM> to about <NUM>.

In some embodiments, the thermoplastic resin composition may have an antibacterial activity of about <NUM> to about <NUM>, for example about <NUM> to about <NUM> against each of Staphylococcus aureus and Escherichia coli, as measured on <NUM>×<NUM> specimens in accordance with JIS Z <NUM> after inoculation with Staphylococcus aureus and Escherichia coli, respectively, followed by culturing under conditions of <NUM> and <NUM>% RH for <NUM> hours.

In some embodiments, the thermoplastic resin composition may have a color difference (ΔE) of about <NUM> or less, for example, about <NUM> to about <NUM>, as calculated according to Equation <NUM> based on initial color values (L<NUM>*, a<NUM>*, b<NUM>*) measured on an injection-molded specimen having a size of <NUM>× <NUM>× <NUM> using a colorimeter and color values (L<NUM>*, a<NUM>*, b<NUM>*) of the specimen measured using the colorimeter after exposure to Xenon-Arc light for <NUM> hours in accordance with ASTM D4459. <MAT>
where ΔL* is a difference (L<NUM>*-L<NUM>*) between L* values before/after exposure; Δa* is a difference (a<NUM>*-a<NUM>*) between a* values before/after exposure; and Δb* is a difference (b<NUM>*-b<NUM>*) between b* values before/after exposure.

In some embodiments, the thermoplastic resin composition may have a yellow index difference (ΔYI) of about <NUM> or less, for example about <NUM> to about <NUM>, as calculated according to Equation <NUM>:.

<MAT>
wherein YI<NUM> is an initial yellow index (YI) of a specimen, as measured in accordance with ASTM D1925, and YI<NUM> is a yellow index (YI) of the specimen, as measured in accordance with ASTM D1925 after the specimen is kept at <NUM> for <NUM> minutes.

In some embodiments, the thermoplastic resin composition may have a Notched Izod impact strength of about <NUM> kgf·cm/cm to about <NUM> kgf·cm/cm, for example about <NUM> kgf·cm/cm to about <NUM> kgf·cm/cm, as measured on a <NUM>/<NUM>" thick specimen in accordance with ASTM D256.

In some embodiments, the thermoplastic resin composition may have a vicat softening temperature of about <NUM> to about <NUM>, for example about <NUM> to about <NUM>, as measured at a heating rate of <NUM>/hr under a load of <NUM> N in accordance with ISO <NUM>/B50.

A molded article according to the present invention is formed of the thermoplastic resin composition set forth above. The thermoplastic resin composition may be prepared in pellet form and the prepared pellets may be produced into various molded articles (products) by various molding methods, such as injection molding, extrusion, vacuum molding, and casting. Such molding methods are well known to those skilled in the art. The molded articles may exhibit good properties in terms of antibacterial properties, weather resistance, impact resistance, thermal resistance, and balance therebetween, and thus may be used in various fields, such as interior/exterior materials for electric/electronic products, such as electrical switch parts and the like.

Next, the present invention will be described in more detail with reference to some examples. It should be understood that these examples are provided for illustration only and are not to be in any way construed as limiting the present invention.

Details of components used in Examples and Comparative Examples are as follows:.

A bisphenol-A polycarbonate resin (weight average molecular weight: <NUM>,<NUM>/mol) was used.

MBS(Manufacturer: LG Chem. Ltd, product name: EM520) was used.

Average particle diameter, BET surface area, purity, peak intensity ratio (B/A) of peak B in the wavelength range of <NUM> to <NUM> to peak A in the wavelength range of <NUM> to <NUM> in photoluminescence measurement, and crystallite size of the zinc oxides (C1), (C2) and (C3) are shown in Table <NUM>.

Maleic anhydride-grafted ethylene-butene rubber (MAH-g-EBR, Manufacturer: Mitsui chemical, product name: TAFMER M) was used.

<MAT>
where K is a shape factor, λ is an X-ray wavelength, β is an FWHM value (degree), and θ is a peak position degree.

The aforementioned components were mixed in amounts as listed in Tables <NUM> and <NUM>, followed by extrusion at <NUM>, thereby preparing a thermoplastic resin composition in pellet form. Here, extrusion was performed using a twin-screw extruder (L/D: <NUM>, Φ: <NUM>). The prepared pellets were dried at <NUM> for <NUM> hours or more and then subjected to injection molding using a 140ton injection machine (molding temperature: <NUM>, mold temperature: <NUM>), thereby preparing a specimen. The prepared specimen was evaluated as to the following properties. Results are shown in Tables <NUM> and <NUM>.

From the above results, it can be seen that the thermoplastic resin composition according to the present invention had good properties in terms of antibacterial property (antibacterial activity), weather resistance (Color difference(ΔE), yellow index difference(ΔYI)), impact resistance (Notched Izod impact strength), thermal resistance (VST) and balance therebetween.

In contrast, it could be seen that the composition of Comparative Example <NUM> prepared using a small amount of the zinc oxide suffered from deterioration in antibacterial properties, weather resistance; the composition of Comparative Example <NUM> prepared using an excess of the zinc oxide suffered from deterioration in weather resistance, impact resistance and thermal resistance of the composition was relatively deteriorated; the composition of Comparative Example <NUM> prepared using zinc oxide (C2) instead of zinc oxide (C1) of the present invention suffered from deterioration in antibacterial properties, weather resistance, impact resistance and the like; the composition of Comparative Example <NUM> prepared using zinc oxide (C3) instead of zinc oxide (C1) of the present invention suffered from deterioration in antibacterial properties, weather resistance, impact resistance and the like; the composition of Comparative Example <NUM> not containing alkyl phosphate suffered from deterioration in weather resistance, impact resistance, and the like; the composition of Comparative Example <NUM> prepared using an excess of alkyl phosphate suffered from deterioration in weather resistance, impact resistance, and the like; the composition of Comparative Example <NUM> prepared using triphenyl phosphate (D2) instead of alkyl phosphate (D1) of the present invention suffered from deterioration in impact resistance and the like; the composition of Comparative Example <NUM> not containing maleic anhydride-grafted rubber polymer suffered from deterioration in weather resistance, impact resistance, and the like; the composition of Comparative Example <NUM> prepared using an excess of maleic anhydride-grafted rubber polymer suffered from deterioration in weather resistance, impact resistance, thermal resistance, and the like; the composition of Comparative Example <NUM> not containing phosphite antioxidant suffered from deterioration in weather resistance, impact resistance, and the like; the composition of Comparative Example <NUM> prepared using an excess of phosphite antioxidant suffered from deterioration in weather resistance, impact resistance, thermal resistance, and the like; the composition of Comparative Example <NUM> prepared using hindered phenolic antioxidant (F2) instead of phosphite antioxidant (F1) of the present invention suffered from deterioration in weather resistance and the like, and the impact resistance of the composition was relatively deteriorated.

Claim 1:
A thermoplastic resin composition comprising:
about <NUM> parts by weight of a polycarbonate resin;
about <NUM> to about <NUM> parts by weight of a rubber modified aromatic vinyl copolymer resin;
about <NUM> to about <NUM> parts by weight of a zinc oxide;
about <NUM> to about <NUM> parts by weight of a C<NUM> to C<NUM> alkyl phosphate;
about <NUM> to about <NUM> parts by weight of a maleic anhydride-grafted rubber polymer; and
about <NUM> to about <NUM> parts by weight of a phosphite antioxidant,
wherein the zinc oxide has an average particle size of about <NUM> to about <NUM> as measured in accordance with the method described in the specification, and a BET specific surface area of about <NUM><NUM>/g to about <NUM><NUM>/g as measured by a nitrogen gas adsorption method, a peak position (2θ) in the range of <NUM>° to <NUM>° and a crystallite size of about <NUM>,<NUM>Å to about <NUM>,<NUM>Å, in X-ray diffraction (XRD) analysis, as calculated by Equation <NUM>: <MAT>
where K is a shape factor, λ is an X-ray wavelength, β is an FWHM value (degree) of an X-ray diffraction peak, and θ is a peak position degree.