Patent Description:
Embodiments of this invention relate to composite elongate elements, which are used to produce a fabric incorporating similar or dissimilar materials in the warp and weft, such fabric being suitable for consolidating into single layer or multilayer shells or structures, e.g. under the action of heat and pressure without the need for additional resin or adhesive.

Self-reinforcing Polypropylene (srPP) fabric is known. Such is marketed by the present Applicant under the brand name ARMORDON ®. Similar materials are available from other companies, e.g. CURV ® from Propex and PURE ® from DIT.

<CIT>) discloses a thermoplastic composite material comprising a molecularly-oriented thermoplastic polymer base having at least one thermoplastic surface polymeric layer compatibly bonded to said polymer base by molecular interspersion between the contiguous surfaces of the adjoining base and surface layers, and said surface polymeric layer having a softening temperature lower than that of the polymer base.

<CIT>) discloses a knotted net structure, e.g. a fishing net, formed of a plurality of interwoven elongate elements, each of said elements comprising a thermoplastic polymer base having at least one thermoplastic surface polymeric layer bonded to said polymer base, said surface polymeric layer having a softening temperature lower than that of the polymer base.

<CIT>) discloses a fabric or material comprising: at least first elongate elements and second elongate elements that are mutually interspersed; wherein the first elongate elements comprise a polymer base and at least one polymeric surface layer, wherein the at least one polymeric surface layer has a softening temperature lower than that of the polymer base; and wherein at least a surface of the second elongate elements comprises an ultra high molecular weight polyalkylene (UHMWPA), wherein the ultra high molecular weight polyalkylene is a material dissimilar to the polymeric surface layer, and the first elongate elements are fusible together with the second elongate elements at least at intersections.

By "molecular interspersion" is meant the intimate molecular compatibility of molecules of the surface layer and the adjacent polymer and vice versa, so that there is intermingling or fusion at their contiguous boundaries. It is believed that such molecular interspersion effectively forms an amorphous sheath which protects the polymer base against fracture during drawing, thus providing mutual mechanical reinforcement.

Mutual mechanical reinforcement involves the surface material being capable of high elongation when drawn in the solid state (or even being drawn at a temperature above its softening point, i.e. in the molten state). With a polymer layer of high modulus, and crystalline or oriented material sandwiched between amorphous high elongation surface layers, propagation of transverse fractures is inhibited allowing the total composite to be highly drawn.

A problem exists in the prior art. Single ribbon tapes of co-extruded polymer are used as warp and weft to weave fabrics. These fabrics are then layered up and hot pressed to make shaped articles. When those articles are subjected to shock loads then an article may fail due to delamination between consolidated fabric layers.

It is an object of at least one embodiment of at least one aspect of the present invention to obviate or at least mitigate one or more problems or disadvantages in the prior art.

It is an object of at least one embodiment of at least one aspect of the present invention to provide a fabric that may be formed without the use of, for example, a resin matric material, a film, or an adhesive. The fabric may, therefore, be self-adhering or self-supporting.

It is an object of at least one embodiment of at least one aspect of the present invention to provide a single layer fabric which has sufficient impact resistance for use in a formed article, e.g. a suitcase shell.

It is an object of at least one embodiment of at least one aspect of the present invention to provide a laminated fabric or material which has sufficient impact resistance for use in a formed article, e.g. a suitcase shell, and which has a reduced number of layers compared to the prior art.

According to a first aspect of the present invention there is provided a woven fabric, comprising at least one composite elongate element adapted for use as a tape, the composite elongate element comprising a plurality of elongate elements twisted together, wherein at least one of the elongate elements comprises a polymeric base and at least one polymeric surface layer, the at least one polymeric surface layer having a softening temperature lower than that of the polymeric base (e.g. at least <NUM> lower), and wherein the at least one elongate element is substantially planar prior to twisting.

The polymeric base and the/each at least one polymeric surface layer may be sandwiched and/or bonded together.

Herein, composite elongate element is meant to comprise or include a plurality of elongate elements that are twisted together.

It has been found that twisting together of the plurality of elongate elements (e.g. along their length) provides advantage over the prior art, e.g. weaving together of single yarns. An advantage is beneficial increased distribution of the at least one polymeric base/polymeric surface layer throughout a matrix of the woven fabric.

Each of the plurality of elongate elements and/or the composite elongate element may have tensile strength, but may be too flexible to provide compressive strength. The/each of the plurality of elongate elements and/or composite elongate elements may be coilable or reelable.

In one embodiment of the present invention the plurality of elongate elements may comprise two elongate elements. In another embodiment of the present invention the plurality of elongate elements may comprise three elongate elements. Alternatively, the plurality of elongate elements may comprise more than three elongate elements.

Beneficially there may be provided <NUM> to <NUM> or <NUM> to <NUM> twists per metre length of the composite elongate element.

The plurality of elongate elements may be twisted together in a left-handed or S-twist or in a right-handed or Z-twist (according to ISO <NUM>).

In one implementation the at least one of the elongate elements may comprise one or more of the plurality of elongate elements. In another implementation the at least one of the elongate elements may comprise each of the plurality of elongate elements. In said one implementation, other of the plurality of elongate elements may comprise a polymeric material(s). At least a surface of the other of the plurality of elongate elements may comprise a material or materials similar or dissimilar to, and/or thermally compatible (e.g. having a softening temperature the same as or higher, e.g. at least to <NUM> higher) than the at least one polymeric surface of the at least one elongate element.

In one implementation each of the plurality of elongate elements may be substantially planar, e.g. comprise tapes, prior to twisting.

Beneficially, surfaces, e.g. said at least one polymeric surface layer, of adjacent elongate elements may contact or touch one another.

The/each at least one elongate element may be a coextruded tape, for example, made by a co-extrusion process.

The/each at least one elongate element may comprise a tape of the form A-B, where B comprises the polymeric base and A comprises the at least one polymeric surface layer.

The/each at least one elongate element may comprise a tape of the form A-B-A, where B comprises the polymeric base and A comprises opposing polymeric surface layers.

Advantageously the at least one elongate element may comprise a self-reinforcing polymeric material such as self-reinforcing polypropylene (srPP).

The/each at least one elongate element may comprise a molecularly-oriented thermoplastic polymeric base which may have at least one thermoplastic surface polymeric layer compatibly bonded to said polymeric base by molecular interspersion between contiguous surfaces of the adjoining base and surface layer(s).

The/each at least one elongate element may be selected from polypropylene, polyesters, polyethyleneterephthalate, polyamides, Nylon (e.g. Nylon <NUM> or <NUM>), or a polyethylene, e.g. having a density in the range <NUM> to <NUM>, or linear low density polyethylene.

The polymer base may comprise a molecularly-oriented polyolefin polymer, such as a polypropylene polymer.

The polymeric surface layer(s) may be compatibly bonded to the polymer base by molecular interspersion between the contiguous surfaces of the adjoining base and surface layers.

The polymeric surface layer may comprise ethylene-propylene co-polymer, polybutylene, polybutene-<NUM> or a co-polymer comprising two or more of butylene, ethylene and propylene, co-polyesters and co-polyamides.

The polymer base may be polypropylene and/or the surface layer(s) may comprise an ethylene-propylene co-polymer, a polybutylene such as polybutene-<NUM> or a co-polymer comprising two or more of butylene, ethylene and propylene.

The polymer base may be polyester and/or the polymeric surface layer(s) may comprise a co-polyester, or the polymer base may be a polyamide and the polymeric surface layer(s) may comprise a co-polyamide.

Elongate elements other than the at least one elongate element may comprise (or solely comprise) a polymeric material, e.g. polypropylene, polyester, polyethylene.

The polymeric material and/or at least a surface layer polymer material of the other elongate elements may be thermally compatible, and/or autogenously bonded with the polymeric material of the at least one surface layer of the/each at least one elongate element. The polymeric material and/or at least a surface layer polymer material of the other elongate elements may have a softening point of <NUM> or more higher than the softening point of the polymer material of the at least one surface layer of the/each at least one elongate element.

The fabric may advantageously comprise a single layer of fabric. The single layer of fabric may be consolidated or consolidatable, e.g. by application of heat and/or pressure. The fabric of the present invention has been found to possibly provide advantages over the prior art, e.g. it has been found that since a single layer of the fabric is heavier than a single layer of single yarn weave of the prior art, whereas in the prior art single layers have been laminated together to provide a suitable material for forming of a product, a single layer of fabric of the present invention suffices. This avoids the need for lamination, so simplifying the manufacturing process and/or obviates and/or mitigates the problem of delamination.

The fabric may also comprise a plurality of further elongate elements, e.g. twisted elongate elements, which may be polymeric. The plurality of further elongate elements may beneficially be the same as the plurality of composite elongate elements.

The plurality of composite elongate elements and plurality of further elongate elements may be mutually interspersed.

At least a surface of the further elongate elements may comprise a material or materials similar or dissimilar to the polymer surface layer(s).

Adjacent, e.g. side-by-side, overlaid, cross-laid or intersecting, elongate elements may be fusible together at least at intersections.

Fusing may comprise heating the fabric above the melting temperature of the polymeric surface layer(s). Fusing may comprise cooling the fabric to allow the surface layer to solidify. Fusing the elements may comprise subjecting the fabric to pressure. Fusing may be achieved by single closure press with flat or contoured plates, continuous belt press, induction heated press or via vacuum bagging and autoclaving.

Preferably the fabric may be formed without the use of, for example, a resin matrix material, a film or an adhesive.

The further elongate elements may be selected from tapes, threads, fibres, filaments, strands, or the like.

The further elongate elements may comprise a single layer or homogenous layer.

The further elongate elements may comprise a plurality of layers.

The further elongate elements may comprise a material or material similar or dissimilar to the polymeric surface layer.

The elongate elements or members and the further elongate members may be formed as tapes.

The elongate elements may comprise one or two surface layers or two opposing surface layers.

The elongate elements may comprise a layered structure, e.g. may comprise a base polymer sandwiched by two polymeric surface layers.

The elongate elements and/or further elongate elements may be woven, knitted, stitched, or may be laid out to form a random fibrous web or may be randomly interspersed to form the material.

Beneficially, the elongate elements and/or further elongate elements may be woven together to form a fabric.

The composite elongate elements and further elongate elements may be woven together to form the fabric or material. The warp may be formed of composite or further elongate elements and the weft may be formed of the other. The warp may be formed of composite elongate elements and the weft may be formed of further elongate elements. Alternatively, the warp may be formed of further elongate elements and the weft may be formed of composite elongate elements.

Alternatively, the composite and further elongate elements are woven together to form the fabric or material, and the warp and/or the weft may comprise a mixture of composite and further elongate elements. The mixture of composite and further elongate elements may be a random arrangement of composite and further elongate elements. Alternatively, the mixture of composite and further elongate elements may be a regular alternation of composite and elongate elements.

The further elongate elements may comprise one or more of: polyesters, polyamides, aramids, thermoplastic polymers, molecularly-oriented thermoplastic polymers, ultra high molecular weight polyalkylenes (UHMWPA), such as ultra high molecular weight polyethylene (UHMWPE) or ultra high molecular weight polypropylene (UHMWPP), multifilament nucleated polypropylenes, and/or carbon fibres.

The further elongate elements may be formed of hybrid yarns.

The hybrid yarns may be formed of at least two different materials or fibres comprising polyesters, polyamides, aramids, thermoplastic polymers, molecularly-oriented thermoplastic polymers, ultra high molecular weight polyalkylenes (UHMWPA), such as ultra high molecular weight polyethylene (UHMWPE) or ultra high molecular weight polypropylene (UHMWPP), multifilament nucleated polypropylenes, and/or carbon fibres.

The further elongate elements may be formed of hybrid yarns selected from hybrid yarns comprising aramids and UHMWPE or hybrid yarns comprising polypropylene.

The further elongate elements may comprise or consist of ultra high molecular weight polyalkylenes selected from UHMWPE or UHMWPP.

According to a second aspect of the present invention there is provided a laminated material comprising a plurality of layers, wherein at least one of said layers comprises a fabric according to the first aspect of the present invention.

In one implementation the laminated material comprises two layers, e.g. only two layers, or three layers, e.g. only three layers.

Preferably each layer comprises a fabric according to the first aspect of the present invention.

According to a third aspect of the present invention there is provided an article, such as a three-dimensional article, formed from a (single layer of) fabric of the first aspect of the present invention, or alternatively formed from a laminated material of the second aspect of the present invention.

The article may be formed by a moulding technique, e.g. press-moulding.

The article may be capable of withstanding relatively high impact, i.e. the article may have high impact resistance properties.

The article may comprise a luggage shell, e.g. a shell for a suitcase.

The article may comprise or be selected from: an armour product, e.g. body armour, automotive (vehicle) component, or sportswear product.

The article may be adapted for antiballistic purposes and/or comprises bulletproof vests, body armour, panels suitable for the protection of military and commercial vehicles, bin liners, blast basket or blast blankets to contain fragmentation debris from the detonation of explosive devices.

The article may find use as carpet backing which may be used in automotive or aerospace application or which comprises panels suitable for use on automotive vehicles.

The article may comprise toe-caps for protective footwear, connecting straps of handles of intermediate bulk containers or the containers themselves, tarpaulins, packaging, luggage, protective cases, or pipes.

According to a fourth aspect of the present invention there is provided a method of forming a woven fabric, the method comprising:
providing a plurality of composite elongate elements, wherein each composite elongate element comprises a plurality of elongate elements twisted together, wherein at least one of the elongate elements comprises a polymeric base and at least one polymeric surface layer, the at least one polymeric surface layer having a softening temperature lower than that of the polymeric base, and wherein the at least one elongate element is substantially planar prior to twisting; weaving said plurality of composite elongate elements into said woven fabric; and consolidating the fabric by application of heat and/or pressure.

Said step of providing may also comprise providing a plurality of further elongate elements, which may be polymeric.

The plurality of composite elongate elements may comprise warp yarns. Alternatively or additionally, the plurality of composite elongate elements may comprise weft yarns.

According to a fifth aspect of the present invention there is provided a method of forming an article, such as a three-dimensional article, comprising the steps of:.

Embodiments of the present invention will now be described by way of example only, with reference to the accompanying drawings, which are:.

Referring to <FIG>, there are shown first to fourth embodiments of a composite elongate element according to the present invention, the composite elongate element 5a to 5d comprising a plurality of elongate elements <NUM> twisted together, wherein at least one of the elongate elements <NUM> comprises a polymeric base <NUM> and at least one polymeric surface layer <NUM>, the at least one polymeric surface layer <NUM> having a softening temperature lower than that of the polymeric base <NUM>.

Herein, the term 'composite elongate element' is meant to comprise or include a plurality of elongate elements, yarns, tapes, strands, plies, or fibres that are twisted together.

It has been found that twisting together of the plurality of elongate elements <NUM> provides advantage over the prior art, e.g. weaving together of single yarns. An advantage is believed to be beneficial increased distribution of the at least one polymeric base/polymeric surface layer <NUM> throughout a matrix of the woven fabric.

Each of the plurality of elongate elements <NUM> and the composite elongate elements 5a to 5d per se has/have tensile strength, but is/are too flexible to provide compressive strength. The composite elongate element 5a to 5d is capable of being woven.

The elongate elements <NUM>, <NUM> are twisted together. In one embodiment (see <FIG>), the plurality of elongate elements may comprise two elongate elements. In another embodiment (see <FIG>), the plurality of elongate elements <NUM> comprises three elongate elements <NUM>. It will, however, be appreciated that in other embodiments more than three elongate elements <NUM>, <NUM> may be provided.

There are typically provided <NUM> to <NUM>, e.g. advantageously <NUM> to <NUM> twists per metre length of the composite elongate element. The plurality of elongate elements <NUM> can be twisted together in a left-handed or S-twist or in a right-handed or Z-twist (according to ISO <NUM>).

In one implementation the at least one of the elongate element(s) <NUM> comprises one or more of the plurality of elongate elements <NUM>. In another implementation the at least one of the elongate element <NUM> comprises each of the plurality of elongate elements <NUM>. In said one implementation, other of the plurality of elongate elements comprise a polymeric material(s). At least a surface of the other of the plurality of elongate elements comprises a material or materials similar or dissimilar to, and/or thermally compatible with the at least one polymeric surface of the at least one elongate element.

Referring now to <FIG>, in one implementation, the at least one elongate element <NUM> is substantially planar or flat, e.g. comprises a tape, prior to twisting. In one implementation each of the plurality of elongate elements are substantially planar, e.g. comprise tapes, prior to twisting. Beneficially surfaces, e.g. said at least one polymeric surface layer, of adjacent elongate elements contact or touch one another. The/each at least one elongate element can be coextruded tape, and can be made by a coextrusion process. The/each at least one elongate element <NUM> can comprise a tape of the form A-B, where B comprises the polymeric base <NUM> and A comprises the at least one polymeric (planar) surface layer <NUM>.

Alternatively, referring to <FIG>, the/each at least one elongate element can comprise a tape of the form A-B-A, where B comprises the polymeric base <NUM> and A comprises opposing polymeric (planar) surface layers <NUM>.

Advantageously the/each at least one elongate element <NUM> comprises a self-reinforcing polymeric material such as self-reinforcing polypropylene (srPP). The/each at least one elongate element <NUM> comprises a molecularly-oriented thermoplastic polymeric base <NUM> having at least one thermoplastic surface polymeric layer <NUM> compatibly bonded to said polymeric base <NUM> by molecular interspersion between contiguous surfaces of the adjoining base and surface layer(s) <NUM>. Said surface polymeric layer(s) <NUM> have a softening temperature lower than that of the polymeric base <NUM>.

The/each at least one elongate element can be selected from polypropylene, polyesters, polyethyleneterephthalate, polyamides, Nylon (e.g. <NUM> or <NUM>), or a polyethylene, e.g. having a density in the range <NUM> to <NUM>, or linear low density polyethylene.

The polymer base <NUM> comprises a molecularly-oriented polyolefin polymer, such as a polypropylene polymer. The polymeric surface layer(s) <NUM> are compatibly bonded to the polymer base by molecular interspersion between the contiguous surfaces of the adjoining base and surface layers <NUM>, <NUM>.

The polymeric surface layer(s) <NUM> comprises a thermoplastic polymer or copolymer. The polymeric surface layer(s) <NUM> can comprise ethylene-propylene co-polymer, polybutylene, polybutene-<NUM>, or a co-polymer comprising two or more of butylene, ethylene and propylene, co-polyesters and co-polyamides.

The polymer base <NUM> can be polypropylene and/or the surface layer(s) <NUM> can comprise an ethylene-propylene co-polymer, a polybutylene such as polybutene-<NUM>, or a co-polymer comprising two or more of butylene, ethylene and propylene. Alternatively, the polymer base <NUM> can be polyester and/or the polymeric surface layer(s) <NUM> can comprise a co-polyester, or the polymer base <NUM> can be a polyamide and the surface layer(s) <NUM> can comprise a co-polyamide.

Elongate elements <NUM> other than the at least one elongate element <NUM> comprise (or solely comprise) a polymeric material, e.g. a thermoplastic, e.g. polypropylene, polyester, or polyethylene.

The polymeric material or at least a surface layer polymer material of the other elongate elements <NUM> is typically thermally compatible, and/or autogenously bondable with the polymeric material of the at least one surface layer <NUM> of the at least one elongate element <NUM>. For example, the polymeric material and/or surface layer polymer material of the other elongate elements may have a softening point of <NUM> or more higher than the softening point of the polymer material of the at least one surface layer of the/each at least one elongate element.

Referring now to <FIG>, there is shown a fabric <NUM> according to an embodiment of the present invention comprising at least one composite elongate element <NUM> of <FIG>. The fabric <NUM> comprises a plurality of composite elongate elements <NUM>.

The fabric <NUM> has been found to provide advantages over the prior art, e.g. it has been found that since a single layer of the fabric <NUM> is heavier than a single layer of single yarn weave of the prior art, whereas in the prior art single layers have required to be laminated together to provide a suitable material for forming of a product, a single layer of fabric <NUM> of the present invention suffices. This avoids the need for lamination, so simplifying the manufacturing process and/or avoiding the problem of delamination.

The fabric <NUM> comprises a plurality of further twisted elongate elements <NUM>, which can be polymeric. Indeed, the plurality of further twisted elongate elements <NUM> are beneficially the same as the plurality of composite elements <NUM>.

The plurality of composite elongate elements <NUM> and plurality of further composite elongate elements <NUM> are mutually interspersed. At least a surface of the further elongate elements <NUM> comprise a material or materials similar or dissimilar to the polymer surface layer(s) <NUM>. Adjacent elongate elements <NUM>, <NUM> are fusible together at least at intersections. Fusing can comprise heating the fabric above the melting temperature of the polymeric surface layer(s) <NUM>. Fusing can comprise cooling the fabric <NUM> to allow the surface layers <NUM> to solidify. Fusing the elements <NUM>, <NUM> comprise subjecting the fabric to pressure. Fusing can be achieved by single closure press with flat or contoured plates, continuous belt press, induction heated press or via vacuum bagging and autoclaving.

<FIG> shows the fabric <NUM> after consolidation via a combination of heat and/or pressure.

As seen from <FIG>, the fabric <NUM> comprises a woven fabric. The fabric <NUM> comprises at least one mat of mutually intersecting elongate elements <NUM>, <NUM> fusible together at least at their intersections.

The thermoplastic fabric <NUM> comprises a consolidated mat or sheet, wherein the plurality of composite elongate elements <NUM>, <NUM> have been consolidated together, e.g. by application of heat and/or pressure. The fabric <NUM> is advantageously formed without the use of, for example, a resin matrix material, a film or an adhesive.

The elongate elements <NUM> and/or further elongate elements <NUM> are selected from tapes, threads, fibres, filaments, strands, or the like.

The further elongate elements can comprise a single layer or homogenous layer. Alternatively, the further elongate elements can comprise a plurality of layers, e.g. A-B, or A-B-A, the same or similar to the elongate elements <NUM>. The further elongate elements <NUM> can comprise a material or materials similar or dissimilar to the polymeric surface layer <NUM>. The elongate elements <NUM> and the further elongate elements <NUM> are formed as tapes. The elongate elements <NUM> comprise one or two surface layers <NUM> or two opposing surface layers <NUM>. The elongate elements <NUM> comprise a layered structure, e.g. comprising a base polymer sandwiched by two polymeric surface layers <NUM>.

The elongate elements <NUM> and/or further elongate elements <NUM> are woven together to form the fabric <NUM>. The warp can be formed of composite or further elongate elements <NUM>, <NUM> and the weft can be formed of the other <NUM>, <NUM>. The warp can be formed of composite elongate elements <NUM> and the weft can be formed of further elongate elements <NUM>. Alternatively, the warp can be formed of further elongate elements <NUM> and the weft can be formed of composite elongate elements <NUM>. As mentioned above, the further elongate elements can be the same (i.e. can be identical) to the composite elongate elements <NUM>.

Alternatively, the composite and further elongate elements <NUM>, <NUM> can be woven together to form the fabric <NUM>, and the warp and/or the weft comprise a mixture of composite and further elongate elements <NUM>, <NUM>. The mixture of composite and further elongate elements <NUM>, <NUM> can be a random arrangement of composite and further elongate elements <NUM>, <NUM>. Alternatively, the mixture of composite and further elongate elements <NUM>, <NUM> can be a regular alternation of composite and further elongate elements <NUM>, <NUM>.

The further elongate elements <NUM> can comprise one or more of: polyesters, polyamides, aramids, thermoplastic polymers, molecularly-oriented thermoplastic polymers, ultra high molecular weight polyalkylenes (UHMWPA), such as ultra high molecular weight polyethylene (UHMWPE) or ultra high molecular weight polypropylene (UHMWPP), and/or multifilament nucleated polypropylenes, and/or carbon fibres.

The further elongate elements <NUM> can be formed of hybrid yarns. The hybrid yarns can be formed of at least two different materials or fibres comprising polyesters, polyamides, aramids, thermoplastic polymers, molecularly-oriented thermoplastic polymers, ultra high molecular weight polyalkylenes (UHMWPA), such as ultra high molecular weight polyethylene (UHMWPE) or ultra high molecular weight polypropylene (UHMWPP), and/or multifilament nucleated polypropylenes, and/or carbon fibres.

The further elongate elements <NUM> can be formed of hybrid yarns selected from hybrid yarns comprising aramids and UHMWPE or hybrid yarns comprising polypropylene. The further elongate elements <NUM> can comprise or consist of ultra high molecular weight polyalkylenes selected from UHMWPE or UHMWPP.

Referring now to <FIG>, there is shown two layers of fabric <NUM> prior to lamination and after thermal lamination, respectively. Lamination of the two layers of fabric <NUM> forms a laminated material <NUM>.

The laminated material <NUM> comprises a plurality of layers <NUM>, wherein at least one of said layers <NUM> comprise the fabric <NUM>. In one implementation the laminated material <NUM> comprises two layers <NUM>, e.g. only two layers, or alternatively three layers, e.g. only three layers (see <FIG>). Advantageously, each layer <NUM> comprises the fabric <NUM>.

Referring now to <FIG>, there are shown articles, i.e. three-dimensional articles formed from fabric <NUM>, or alternatively formed from the laminated material <NUM>.

The articles 400a to 400d are typically formed by a moulding technique, e.g. press-moulding. The articles 400a to 400d are capable of withstanding relatively high impact, i.e. the articles 400a to 400d have relatively high impact resistance properties.

Referring to <FIG>, the article 400a comprises a luggage shell, e.g. a shell for a suitcase. Alternatively, the article can comprise or be selected from: an armour product, e.g. body armour, automotive (vehicle) component, or sportswear product. The article can be adapted for antiballistic purposes and/or comprises bulletproof vests, body armour, panels suitable for the protection of military and commercial vehicles, bin liners, blast basket or blast blankets to contain fragmentation debris from the detonation of explosive devices. The article may find use as carpet backing which may be used in automotive or aerospace application or which comprises panels suitable for use on automotive vehicles.

Referring to <FIG> and <FIG>, the article 400b comprises a toe-cap(s) for protective footwear. Alternatively, the article can comprise connecting straps of handles of intermediate bulk containers or the containers themselves, tarpaulins, packaging, luggage, protective cases, or pipes. <FIG> shows an article 400d comprising an automotive component (e.g. door trim) prior to finishing/trimming.

The present invention provides a method of forming a composite elongate element <NUM>, the method comprising:.

The present invention provides a method of forming a woven fabric, the method comprising: providing a plurality of composite elongate elements <NUM>; and weaving said plurality of composite elongate elements <NUM> into said woven fabric <NUM>.

Said step of providing also comprises providing a plurality of further elongate elements <NUM>. The plurality of composite elongate elements <NUM> can comprise warp/weft yarns. Alternatively or additionally, the plurality of composite elongate elements can comprise weft/warp yarns. The method further comprises the (subsequent) step of consolidating the fabric <NUM> by application of heat and/or pressure.

The present invention provides a method of forming an article <NUM>, such as a three-dimensional article, comprising the steps of:.

Claim 1:
A woven fabric (<NUM>), comprising at least one composite elongate element (5a-5d) adapted for use as a tape, the composite elongate element comprising a plurality of elongate elements (<NUM>) twisted together, wherein at least one of the elongate elements (<NUM>) comprises a polymeric base (<NUM>) and at least one polymeric surface layer (<NUM>), the at least one polymeric surface layer having a softening temperature lower than that of the polymeric base, and wherein the at least one elongate element is substantially planar prior to twisting.