Patent Description:
Acrylonitrile-butadiene-styrene resins (hereinafter referred to as "ABS resins") based on conjugated diene rubber have excellent processability, mechanical properties, and appearance properties, and thus have been widely used in electric and electronic products, automobiles, small toys, furniture, construction materials, and the like. However, since ABS resins are based on butadiene rubber containing an unsaturated bond that is chemically unstable, ABS resins have very poor weather resistance due to aging of the rubber polymer by ultraviolet light. Thus, ABS resins are not suitable as outdoor materials. To address such problems, a method of using ABS resins after painting has been proposed, but there is a problem of environmental pollution during the painting process. In addition, the painted product is difficult to recycle and has poor durability.

To overcome these problems of ABS resins, acrylic copolymers typified by acrylate-styrene-acrylonitrile graft copolymers (hereinafter referred to as "ASA resins") without an ethylenically unsaturated bond have been used. ASA resins have excellent physical properties, such as processability, impact resistance, chemical resistance, and weather resistance, and thus have been used in various fields, such as materials for buildings, interior and exterior materials for automobiles and motorcycles, electric and electronic products, ships, leisure goods, and gardening goods. In addition, there is increasing demand for ASA resins. However, appearance characteristics, such as colorability, of ASA resins are poor, compared to painted ABS resins, and ASA resins are insufficient to satisfy increasing weather resistance levels required in the market.

In addition, as the importance of aesthetics increases in the market, research is being conducted to realize a luxurious appearance and excellent colorability and weather resistance by finishing the outer surfaces of substrates, such as ABS, PVC, and steel sheets, with thermoplastic resins. Such a finishing material is mainly manufactured in the form of a film and then processed into a final product through a process such as bending or folding according to the shape of a substrate to which the finishing material is applied. However, due to the characteristics of a thermoplastic ASA resin, when the above-described finishing treatment is performed at room temperature, whitening occurs, thereby losing the original color of the resin and deteriorating aesthetics.

Such a whitening phenomenon is analyzed to be caused by voids due to cracks occurring inside a thermoplastic resin when bent. To address this, a method for improving whitening properties by adjusting the content of rubber in a thermoplastic resin or by mixing a thermoplastic resin with an elastomer to soften a thermoplastic resin has been proposed. However, the methods can address whitening, but there is a problem that other mechanical properties, colorability, surface gloss, etc. are deteriorated. Accordingly, a thermoplastic resin composition exhibiting excellent physical properties has not yet been developed, and non-whitening properties have also not been satisfactorily implemented. <CIT> discloses a thermoplastic resin composition, its preparation method and a moulded article prepared therefrom, comprising a BA/MMA graft copolymer and a matrix resin comprising an MMA/MA copolymer.

Therefore, the present invention has been made in view of the above problems, and it is one object of the present invention to provide a transparent thermoplastic resin having excellent transparency, impact strength, gloss, weather resistance, and fluidity and excellent non-whitening properties, characterized in that occurrence of whitening is suppressed even when bent or hit and a method of preparing the thermoplastic resin. It is another object of the present invention to provide a molded article manufactured using the thermoplastic resin of the present invention.

In accordance with an aspect of the present invention, the above and other objects can be accomplished by the provision of a thermoplastic resin, including: an alkyl acrylate-alkyl methacrylate graft copolymer (A), or an alkyl acrylate-alkyl methacrylate graft copolymer (A); and a matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer, wherein a transparency (haze value), measured according to ASTM D-<NUM> under a condition of <NUM> thickness, is <NUM> or less, and a transparency measured under a condition of <NUM> thickness is <NUM> or less, a total content of the alkyl acrylate is <NUM> to <NUM> % by weight, and a butyl acrylate coverage value (X) as calculated by Equation <NUM> below is <NUM> or more:.

<MAT>
wherein G represents a total gel content (%) of the thermoplastic resin, and Y represents a content (% by weight) of butyl acrylate in the gel of the thermoplastic resin, wherein the copolymer (A) comprises <NUM> to <NUM> % by weight of an alkyl acrylate rubber (a-<NUM>) having a DLS average particle diameter of <NUM> to <NUM> or a TEM average particle diameter of <NUM> to <NUM>; and <NUM> to <NUM> % by weight of an alkyl acrylate-alkyl methacrylate copolymer (a-<NUM>) based on <NUM> % by weight in total of the copolymer (A) and wherein the copolymer (A) has a grafting degree of <NUM> to <NUM> %, and the copolymer (a-<NUM>) has a weight-average molecular weight of <NUM>,<NUM> to <NUM>,<NUM>/mol.

In accordance with another aspect of the present disclosure, there is provided a thermoplastic resin, including: an alkyl acrylate-alkyl methacrylate graft copolymer (A), or an alkyl acrylate-alkyl methacrylate graft copolymer (A); and a matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer, wherein a transparency (haze value), measured according to ASTM D-<NUM> under a condition of <NUM> thickness, is <NUM> or less, and a transparency measured under a condition of <NUM> thickness is <NUM> or less, a total content of the alkyl acrylate is <NUM> to <NUM> % by weight, and a refractive index difference (according to ASTM D542) between a sol and a gel of the thermoplastic resin under a condition of using acetone is <NUM> or less.

In accordance with another aspect of the present disclosure, there is provided a thermoplastic resin, including: an alkyl acrylate-alkyl methacrylate graft copolymer (A), or an alkyl acrylate-alkyl methacrylate graft copolymer (A); and a matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer, wherein a transparency (haze value), measured according to ASTM D-<NUM> under a condition of <NUM> thickness, is <NUM> or less, and a transparency measured under a condition of <NUM> thickness is <NUM> or less, a total content of the alkyl acrylate is <NUM> to <NUM> % by weight, and an elution amount of butyl acrylate in acetone is <NUM> % by weight or more.

Preferably, a refractive index difference (according to ASTM D542) between a sol and a gel of the thermoplastic resin under a condition of using acetone may be <NUM> or less.

Preferably, the thermoplastic resin may include <NUM> to <NUM> % by weight of the alkyl acrylate-alkyl methacrylate graft copolymer (A), and <NUM> to <NUM> % by weight of the matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer.

Preferably, when elution of the thermoplastic resin is performed using acetone, an elution amount of butyl acrylate may be <NUM> % by weight or more.

The copolymer (A) includes. <NUM> to <NUM> % by weight of an alkyl acrylate rubber (a-<NUM>) having a DLS average particle diameter of <NUM> to <NUM> or a TEM average particle diameter of <NUM> to <NUM>; and <NUM> to <NUM> % by weight of an alkyl acrylate-alkyl methacrylate copolymer (a-<NUM>) based on <NUM> % by weight in total of the copolymer (A).

The copolymer (A) has a grafting degree of <NUM> to <NUM> %, and the copolymer (a-<NUM>) may have a weight-average molecular weight of <NUM>,<NUM> to <NUM>,<NUM>/mol.

Preferably, the thermoplastic resin, the rubber (a-<NUM>), or both the thermoplastic resin and the rubber (a-<NUM>) may have a glass transition temperature of -<NUM> to -<NUM>.

Preferably, the rubber (a-<NUM>) may further include alkyl methacrylate. In this case, the alkyl methacrylate may be included in an amount of <NUM> to <NUM> % by weight based on <NUM> % by weight in total of the rubber (a-<NUM>).

Preferably, the copolymer (a-<NUM>) may include <NUM> to <NUM> % by weight of alkyl methacrylate and <NUM> to <NUM> % by weight of alkyl acrylate based on <NUM> % by weight in total of the copolymer (a-<NUM>).

Preferably, a refractive index difference (according to ASTM D542) between the rubber (a-<NUM>) and the matrix resin (B) may be <NUM> or more.

Preferably, when the thermoplastic resin is extruded to obtain a film having a thickness of <NUM>, and a weight having a weight of <NUM> is vertically dropped onto the film from a height of <NUM> at a temperature of <NUM> using a Gardner impact tester, a difference in haze values measured before and after impact according to ASTM D1003-<NUM> for an area impacted (hit) by the weight may be <NUM> or less.

In accordance with another aspect of the present invention, there is provided a method of preparing a thermoplastic resin, the method including: a step of kneading and extruding an alkyl acrylate-alkyl methacrylate graft copolymer (A), or an alkyl acrylate-alkyl methacrylate graft copolymer (A); and a matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer, wherein a transparency (haze value), measured according to ASTM D-<NUM> under a condition of <NUM> thickness, of the thermoplastic resin is <NUM> or less, and a transparency under a condition of <NUM> thickness is <NUM> or less, a total content of the alkyl acrylate in the thermoplastic resin is <NUM> to <NUM> % by weight, and a butyl acrylate coverage value (X), as calculated by Equation <NUM> below, of the thermoplastic resin is <NUM> or more:.

<MAT>
wherein G represents a total gel content (%) of the thermoplastic resin, and Y represents a content (% by weight) of the butyl acrylate in the gel of the thermoplastic resin, wherein the copolymer (A) comprises <NUM> to <NUM> % by weight of an alkyl acrylate rubber (a-<NUM>) having a DLS average particle diameter of <NUM> to <NUM> or a TEM average particle diameter of <NUM> to <NUM>; and <NUM> to <NUM> % by weight of an alkyl acrylate-alkyl methacrylate copolymer (a-<NUM>) based on <NUM> % by weight in total of the copolymer (A) and wherein the copolymer (A) has a grafting degree of <NUM> to <NUM> %, and the copolymer (a-<NUM>) has a weight-average molecular weight of <NUM>,<NUM> to <NUM>,<NUM>/mol.

Preferably, the graft copolymer (A) may be prepared by a method including a step of emulsion polymerization of <NUM> parts by weight in total of a monomer mixture including <NUM> to <NUM> % by weight of alkyl acrylate rubber having a DLS average particle diameter of <NUM> to <NUM> or a TEM average particle diameter of <NUM> to <NUM>; and <NUM> to <NUM> % by weight of an alkyl acrylate compound and an alkyl methacrylate compound.

In accordance with yet another aspect of the present invention, there is provided a molded article including the thermoplastic resin.

Preferably, the molded article may be a finishing material.

As apparent from the foregoing, the present invention advantageously provides a thermoplastic resin having excellent transparency, impact strength, weather resistance, gloss, and fluidity and excellent non-whitening properties, characterized in that whitening does not occur even when bent or hit and a method of preparing the thermoplastic resin. According to the present invention, the properties of the thermoplastic resin can be implemented by adjusting the particle diameter and content of a rubber included in the resin, a grafting degree and molecular weight, a gel content of the resin, a refractive index difference between a sol and gel of the resin, and the like.

Hereinafter, a thermoplastic resin of the present invention will be described in detail.

The present inventors conducted studies to develop a transparent thermoplastic resin capable of providing a finishing material having a luxurious appearance. As a result of such study, the present inventors confirmed that transparency is improved by adjusting a refractive index difference between a sol and a gel, and non-whitening properties are significantly improved when formation of voids due to cracks is minimized by reducing the distance between rubber particles and increasing a grafting degree up to a predetermined range. Based on these results, the present inventors conducted further studies to complete the present invention.

In this description, a resin does not mean only a single (co)polymer, and may include two or more (co)polymers as main components.

In this description, the composition ratio of a (co)polymer may mean the content of units constituting the (co)polymer, or may mean the content of units fed during polymerization of the (co)polymer.

The thermoplastic resin of the present invention includes an alkyl acrylate-alkyl methacrylate graft copolymer (A), or an alkyl acrylate-alkyl methacrylate graft copolymer (A); and a matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer, wherein a transparency measured according to ASTM D-<NUM> under a condition of <NUM> thickness is <NUM> or less, a transparency measured under a condition of <NUM> thickness is <NUM> or less, a total content of the alkyl acrylate is <NUM> to <NUM> % by weight, and a butyl acrylate coverage value (X) as calculated by Equation <NUM> below is <NUM> or more, wherein the copolymer (A) comprises <NUM> to <NUM> % by weight of an alkyl acrylate rubber (a-<NUM>) having a DLS average particle diameter of <NUM> to <NUM> or a TEM average particle diameter of <NUM> to <NUM>; and <NUM> to <NUM> % by weight of an alkyl acrylate-alkyl methacrylate copolymer (a-<NUM>) based on <NUM> % by weight in total of the copolymer (A) and wherein the copolymer (A) has a grafting degree of <NUM> to <NUM> %, and the copolymer (a-<NUM>) has a weight-average molecular weight of <NUM>,<NUM> to <NUM>,<NUM>/mol. In this case, transparency, impact resistance, weather resistance, and molding processability are excellent. In addition, whitening does not occur when bent or hit. That is, non-whitening properties are excellent.

In Equation <NUM>, G represents the total gel content (%) of the thermoplastic resin, and Y represents the content (% by weight) of butyl acrylate in the gel of the thermoplastic resin.

As another example, the thermoplastic resin of the present disclosure may include <NUM> to <NUM> % by weight of an alkyl acrylate-alkyl methacrylate graft copolymer (A); and <NUM> to <NUM> % by weight of a matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer, wherein a transparency (haze value) measured according to ASTM D-<NUM> under a condition of <NUM> thickness is <NUM> or less, a transparency measured under a condition of <NUM> thickness is <NUM> or less, and value X as calculated by Equation <NUM> below is <NUM> % or more. In this case, transparency, impact resistance, weather resistance, and molding processability are excellent. In addition, whitening does not occur when bent. That is, non-whitening properties are excellent.

In addition, as still another example, the thermoplastic resin of the present disclosure may include <NUM> to <NUM> % by weight of an alkyl acrylate-alkyl methacrylate graft copolymer (A); and <NUM> to <NUM> % by weight of a matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer, wherein the total content of alkyl acrylate is <NUM> to <NUM> % by weight, a transparency (haze value) measured according to ASTM D-<NUM> under a condition of <NUM> thickness is <NUM> or less, a transparency measured under a condition of <NUM> thickness is <NUM> or less, and a refractive index difference (according to ASTM D542) between a sol and a gel under a condition of using acetone is <NUM> or less. In this case, transparency, impact resistance, weather resistance, and molding processability are excellent. In addition, whitening does not occur when bent. That is, non-whitening properties are excellent.

In addition, as still another example, the thermoplastic resin of the present disclosure may include <NUM> to <NUM> % by weight of an alkyl acrylate-alkyl methacrylate graft copolymer (A); and <NUM> to <NUM> % by weight of a matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer, wherein the total content of alkyl acrylate is <NUM> to <NUM> % by weight, a transparency (haze value) measured according to ASTM D-<NUM> under a condition of <NUM> thickness is <NUM> or less, a transparency measured under a condition of <NUM> thickness is <NUM> or less, and an elution amount of butyl acrylate under a condition of using acetone is <NUM> or more. In this case, transparency, impact resistance, weather resistance, and molding processability are excellent. In addition, whitening does not occur when bent. That is, non-whitening properties are excellent.

In this description, when measuring gel content, <NUM> of acetone is added to <NUM> of dry powder of a thermoplastic resin, agitation is performed at <NUM> rpm at room temperature for <NUM> hours using a shaker (SKC-<NUM>, Lab Companion Co. ), centrifugation is performed at <NUM>,<NUM> rpm at <NUM> for <NUM> hours using a centrifuge (Supra R30, Hanil Science Co. ) to separate only insoluble matter that is not dissolved in acetone, and the separated insoluble matter is dried in a forced circulation manner at <NUM> for <NUM> hours using a forced convection oven (OF-12GW, Lab Companion Co. Then, the weight of the dried insoluble matter is measured, and gel content is calculated by Equation <NUM> below.

In this description, when measuring grafting degree, <NUM> of acetone is added to <NUM> of dry powder of a graft polymer, agitation is performed at <NUM> rpm at room temperature for <NUM> hours using a shaker (SKC-<NUM>, Lab Companion Co. ), centrifugation is performed at <NUM>,<NUM> rpm at <NUM> for <NUM> hours using a centrifuge (Supra R30, Hanil Science Co. ) to separate only insoluble matter that is not dissolved in acetone, and the separated insoluble matter is dried in a forced circulation manner at <NUM> for <NUM> hours using a forced convection oven (OF-12GW, Lab Companion Co. Then, the weight of the dried insoluble matter is measured, and grafting degree is calculated by Equation <NUM> below.

In Equation <NUM>, the weight (g) of grafted monomers is a value obtained by subtracting the weight (g) of rubber from the weight of insoluble matter (gel) obtained by dissolving a graft copolymer in acetone and performing centrifugation, and the weight (g) of rubber is the amount of rubber components theoretically included in the graft copolymer powder.

In this description, DLS average particle diameter may be measured by dynamic light scattering, and specifically, may be measured as an intensity value using a sample in the form of latex and using a particle size analyzer (Nicomp CW380, PPS Co. ) in a Gaussian mode. As a particular example, <NUM> of latex having a solids content of <NUM> to <NUM> % by weight is diluted with <NUM> of deionized water to prepare a sample, and the DLS average particle diameter of the sample may be measured at <NUM> using a particle size analyzer (Nicomp CW380, PPS Co. ) in a measurement method of using an auto-dilution manner and flow cells and in a measurement mode of dynamic light scattering/intensity <NUM>/intensity-weight Gaussian analysis.

In this description, TEM average particle diameter may be measured by transmission electron microscope (TEM) analysis. Specifically, the TEM average particle diameter refers to a value obtained by numerically measuring particle size on a high magnification image of a TEM and averaging the measurement results. In this case, a specific measurement example is as follows:.

Here, the average value of the largest diameters of each of particles in the top <NUM> % of a particle diameter distribution may mean an arithmetic mean value of the top <NUM> % of the largest diameters of each of <NUM> or more particles randomly selected from a TEM image.

Hereinafter, each component constituting the thermoplastic resin of the present invention will be described in detail.

The copolymer (A) includes an alkyl acrylate and an alkyl methacrylate, and is included in an amount of <NUM> to <NUM> % by weight based on <NUM> % by weight in total of the thermoplastic resin.

For example, based on <NUM> % by weight in total of the copolymer (A), the copolymer (A) includes <NUM> to <NUM> % by weight, preferably <NUM> to <NUM> % by weight, more preferably <NUM> to <NUM> % by weight of an alkyl acrylate rubber (a-<NUM>) having a DLS average particle diameter of <NUM> to <NUM> or a TEM average particle diameter of <NUM> to <NUM> and <NUM> to <NUM> % by weight, preferably <NUM> to <NUM> % by weight, more preferably <NUM> to <NUM> % by weight of an alkyl acrylate-alkyl methacrylate copolymer (a-<NUM>). Within this range, transparency, gloss, non-whitening properties, and impact resistance are excellent. The rubber (a-<NUM>) may have a DLS average particle diameter of preferably <NUM> to <NUM>, more preferably <NUM> to <NUM>, and a TEM average particle diameter of, preferably, <NUM> to <NUM>, more preferably <NUM> to <NUM>. Within this range, excellent transparency and weather resistance are provided without lowering the mechanical strength.

In this description, the graft copolymer (A) including the alkyl acrylate rubber (a-<NUM>) and the alkyl acrylate-alkyl methacrylate copolymer (a-<NUM>) refers to a graft copolymer (A) including the alkyl acrylate rubber (a-<NUM>) and the alkyl acrylate-alkyl methacrylate copolymer (a-<NUM>) surrounding the alkyl acrylate rubber (a-<NUM>). In addition, the graft copolymer (A) may be represented as a graft copolymer (A) formed by graft-polymerizing an alkyl acrylate and an alkyl methacrylate onto the alkyl acrylate rubber (a-<NUM>).

The copolymer (A) has a grafting degree of <NUM> to <NUM> % and a weight average molecular weight of <NUM>,<NUM> to <NUM>,<NUM>/mol. Within these ranges, molding processability and non-whitening properties may be excellent. The copolymer (A) preferably has a grafting degree of <NUM> to <NUM> %, more preferably <NUM> to <NUM> %. Within this range, non-whitening properties may be excellent without deterioration in impact resistance and molding processability. The copolymer (a-<NUM>) preferably has a weight average molecular weight of <NUM>,<NUM> to <NUM>,<NUM>/mol, more preferably <NUM>,<NUM> to <NUM>,<NUM>/mol. Within this range, molding processability and non-whitening properties may be excellent without deterioration in impact resistance.

In this description, unless otherwise defined, weight average molecular weight may be measured using gel permeation chromatography (GPC, Waters Breeze). As a specific example, the weight average molecular weight may be measured using tetrahydrofuran (THF) as an eluate through gel permeation chromatography (GPC, Waters Breeze). In this case, weight average molecular weight is obtained as a relative value to a polystyrene (PS) standard sample. As a specific measurement example, the weight average molecular weight may be measured under conditions of solvent: THF, column temperature: <NUM>, flow rate: <NUM>/min, sample concentration: <NUM>/ml, injection amount: <NUM>µl, column model: <NUM>× PLgel <NUM> MiniMix-B (<NUM> × <NUM>) + <NUM>× PLgel <NUM> MiniMix-B (<NUM> × <NUM>) + <NUM>× PLgel <NUM> MiniMix-B Guard (<NUM> × <NUM>), equipment name: Agilent <NUM> series system, refractive index detector: Agilent G1362 RID, RI temperature: <NUM>, data processing: Agilent ChemStation S/W, and test method (Mn, Mw and PDI): OECD TG <NUM>.

For example, the rubber (a-<NUM>) may have a glass transition temperature of -<NUM> to -<NUM>, preferably -<NUM> to - <NUM>. Within this range, impact strength is further improved without deterioration of other physical properties.

In this description, glass transition temperature may be measured at a heating rate of <NUM>/min using a differential scanning calorimeter (TA Instruments Q100 DSC) according to ASTM D <NUM>.

For example, the rubber (a-<NUM>) may further include an alkyl methacrylate. In this case, chemical resistance and impact resistance may be further improved. For example, the content of the alkyl methacrylate included in the rubber (a-<NUM>) may be <NUM> to <NUM> % by weight, preferably <NUM> to <NUM> % by weight, more preferably <NUM> to <NUM> % by weight based on <NUM> % by weight in total of the rubber (a-<NUM>). Within this range, desired effects may be sufficiently obtained without deterioration in other physical properties.

For example, the alkyl acrylate rubber may be prepared by emulsion polymerization of an alkyl acrylate-based compound. As a specific example, the acrylate rubber may be prepared by mixing an acrylate-based compound, an emulsifier, an initiator, a grafting agent, a crosslinking agent, an electrolyte, and a solvent and performing emulsion polymerization of the mixture. In this case, grafting efficiency may increase, thereby improving physical properties such as impact resistance.

For example, based on <NUM> % by weight of the copolymer (a-<NUM>), the copolymer (a-<NUM>) may include <NUM> to <NUM> % by weight of alkyl methacrylate and <NUM> to <NUM> % by weight of alkyl acrylate, preferably <NUM> to <NUM> % by weight of alkyl methacrylate and <NUM> to <NUM> % by weight of alkyl acrylate, more preferably <NUM> to <NUM> % by weight of alkyl methacrylate and <NUM> to <NUM> % by weight of alkyl acrylate. Within this range, impact strength and weather resistance may be further improved.

For example, the rubber (a-<NUM>) may include a rubber seed.

For example, the rubber seed may be prepared by polymerizing alkyl acrylate and, optionally alkyl methacrylate. When alkyl methacrylate is included, the alkyl methacrylate may be included in an amount of <NUM> to <NUM> % by weight, preferably <NUM> to <NUM> % by weight, more preferably <NUM> to <NUM> % by weight based on <NUM> % by weight of the rubber seed. Within this range, impact strength, weather resistance, and physical property balance are excellent.

As a specific example, the rubber seed may be prepared by polymerizing an alkyl acrylate with <NUM> to <NUM> parts by weight of a crosslinking agent, <NUM> to <NUM> parts by weight of an initiator, and <NUM> to <NUM> parts by weight of an emulsifier based on <NUM> parts by weight of units constituting the copolymer (A). Within this range, a polymer having an even size may be prepared within a short time, and physical properties such as weather resistance and impact strength may be further improved.

As another specific example, based on <NUM> parts by weight of units constituting the copolymer (A), the rubber seed may be prepared by adding <NUM> to <NUM> part by weight of a crosslinking agent, <NUM> to <NUM> part by weight of an initiator, and <NUM> to <NUM> parts by weight of an emulsifier to monomers including an alkyl acrylate and an alkyl methacrylate and performing polymerization. Within this range, a polymer having an even size may be prepared within a short time, and physical properties such as weather resistance and impact strength may be further improved.

For example, based on <NUM> parts by weight of units constituting the copolymer (A), the copolymer (A) may be prepared by a method including a step (A-<NUM>) of preparing a rubber seed by polymerizing a mixture containing <NUM> to <NUM> part by weight of an electrolyte, <NUM> to <NUM> parts by weight of a crosslinking agent, <NUM> to <NUM> parts by weight of an initiator, and <NUM> to <NUM> parts by weight of an emulsifier with <NUM> to <NUM> parts by weight of an alkyl acrylate and optionally an alkyl methacrylate; a step (A-<NUM>) of preparing a rubber core by polymerizing, in the presence of the rubber seed, a mixture containing <NUM> to <NUM> parts by weight of an alkyl acrylate and optionally an alkyl methacrylate, <NUM> to <NUM> part by weight of a crosslinking agent, <NUM> to <NUM> parts by weight of an initiator, and <NUM> to <NUM> parts by weight of an emulsifier; and a step (A-<NUM>) of preparing a graft shell by adding <NUM> to <NUM> parts by weight of a crosslinking agent, <NUM> to <NUM> parts by weight of an initiator, <NUM> to <NUM> parts by weight of an emulsifier, and <NUM> to <NUM> part by weight of an activator to <NUM> to <NUM> parts by weight of the sum of an alkyl acrylate and an alkyl methacrylate in the presence of the rubber core and mixing the components. In this case, the physical property balance of impact resistance, weather resistance, molding processability, and non-whitening properties are excellent.

In this description, for example, the alkyl acrylate compound may be an alkyl acrylate containing an alkyl group having <NUM> to <NUM> carbon atoms, and as a specific example, may include one or more selected from the group consisting of methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, <NUM>-ethylbutyl acrylate, octyl acrylate, <NUM>-ethylhexyl acrylate, hexyl acrylate, heptyl acrylate, n-pentyl acrylate, and lauryl acrylate. As another example, the alkyl acrylate compound preferably is an alkyl acrylate containing a chain alkyl group having <NUM> to <NUM> carbon atoms, more preferably butyl acrylate.

In this description, for example, the alkyl methacrylate may be an alkyl methacrylate containing an alkyl group having <NUM> to <NUM> carbon atoms, and as a specific example, may include one or more selected from the group consisting of methyl methacrylate, ethyl methacrylate, butyl methacrylate, <NUM>-ethylbutyl methacrylate, <NUM>-ethylhexyl methacrylate, and lauryl methacrylate. The alkyl methacrylate preferably is an alkyl methacrylate containing a chain alkyl group having <NUM> to <NUM> carbon atoms, more preferably methyl methacrylate.

In this description, unless otherwise defined, crosslinking agents commonly used in the art to which the present invention pertains may be used in the present invention without particular limitation. For example, one or more compounds including an unsaturated vinyl group and capable of serving as a crosslinking agent, or one or more compounds including two or more unsaturated vinyl groups having different reactivities may be used as the crosslinking agent of the present invention. As a specific example, the crosslinking agent of the present invention may include one or more selected from the group consisting of polyethyleneglycol diacrylate, polyethyleneglycol dimethacrylate, polypropyleneglycol diacrylate, polypropyleneglycol dimethacrylate, ethyleneglycol diacrylate, ethyleneglycol dimethacrylate, divinylbenzene, diethyleneglycol dimethacrylate, triethyleneglycol dimethacrylate, <NUM>,<NUM>-butadiol dimethacrylate, hexanediol propoxylate diacrylate, neopentylglycol dimethacrylate, neopentylglycol ethoxylate diacrylate, neopentylglycol propoxylate diacrylate, trimethylolpropane trimethacrylate, trimethylolmethane triacrylate, trimethylpropane ethoxylate triacrylate, trimethylpropane propoxylate triacrylate, pentaerythritol ethoxylate triacrylate, pentaerythritol propoxylate triacrylate, vinyltrimethoxysilane, allyl methacrylate, triallyl isocyanurate, triallyl amine, and diallyl amine, without being limited thereto.

In this description, for example, a mixture containing one or more selected from the group consisting of KCl, NaCl, KHCO<NUM>, NaHCO<NUM>, K<NUM>CO<NUM>, Na<NUM>CO<NUM>, KHSO<NUM>, NaHSO<NUM>, K<NUM>P<NUM>O<NUM>, Na<NUM>P<NUM>O<NUM>, K<NUM>PO<NUM>, Na<NUM>PO<NUM>, K<NUM>HPO<NUM>, Na<NUM>HPO<NUM>, KOH, NaOH, and Na<NUM>S<NUM>O<NUM> may be used as the electrolyte, without being limited thereto.

In this description, initiators commonly used in the art to which the present invention pertains may be used in the present invention without particular limitation. For example, radical initiators such as water-soluble initiators and fat-soluble initiators may be used, and a mixture containing one or more of the radical initiators may be used.

The water-soluble initiator may include one or more selected from the group consisting of inorganic peroxides including sodium persulfate, potassium persulfate, ammonium persulfate, potassium superphosphate, and hydrogen peroxide, without being limited thereto.

The fat-soluble initiator may include one or more selected from the group consisting of dialkyl peroxides, diacyl peroxides, diperoxyketals, hydroperoxides, peroxyesters, peroxydicarbonates, and azo compounds.

As a more specific example, the fat-soluble initiator may include one or more selected from the group consisting of organic peroxides such as cumene hydroperoxide, p-menthane hydroperoxide, di-t-butyl peroxide, dicumyl peroxide, t-butylcumyl peroxide, di-t-amyl peroxide, <NUM>,<NUM>-dimethyl-<NUM>,<NUM>-di(t-butylperoxy)-hexane, <NUM>,<NUM>,-di(t-butylperoxy)-<NUM>,<NUM>,<NUM>-trimethylcyclohexane, <NUM>,<NUM>-di(t-butylperoxy)-cyclohexane, <NUM>,<NUM>-di(t-amylperoxy)-cyclohexane, ethyl <NUM>,<NUM>-di(t-amylperoxy)-butyrate, diisopropylbenzene mono-hydroperoxide, t-amyl hydroperoxide, t-butyl hydroperoxide, t-butyl peroxyneodecanoate, t-butyl peroxypivalate, di-(<NUM>,<NUM>,<NUM>-trimethylhexanoyl)-peroxide, t-butyl peroxy-<NUM>-ethylhexanoate, t-butyl peroxy-<NUM>,<NUM>,<NUM>-trimethylhexanoate, t-amyl peroxy neodecanoate, t-amyl peroxypivalate, t-amyl peroxy-<NUM>-ethylhexanoate, t-butyl peroxyacetate, t-butyl peroxybenzoate, t-amyl peroxy <NUM>-ethylhexyl carbonate, t-butyl peroxy <NUM>-ethylhexyl carbonate, t-butyl peroxy isopropyl monocarbonate, t-butyl peroxy maleic acid, cumyl peroxyneodecanoate, <NUM>,<NUM>,<NUM>,<NUM>,-tetramethylbutyl peroxy neodecanoate, <NUM>,<NUM>,<NUM>,<NUM>,-tetramethylbutyl peroxy <NUM>-ethylhexanoate, di-<NUM>-ethylhexyl peroxydicarbonate, <NUM>-hydroxy-<NUM>,<NUM>-dimethylbutylperoxy neodecanoate, acetyl peroxide, isobutyl peroxide, octanoyl peroxide, dibenzoyl peroxide, dilauroyl peroxide, <NUM>,<NUM>,<NUM>-trimethylhexanoyl peroxide, and t-butyl peroxy isobutyrate; azobisisobutyronitrile; azobismethylbutyronitrile; azobis-<NUM>-methoxy-<NUM>,<NUM>-dimethylvaleronitrile; azobis-<NUM>,<NUM>-dimethylvaleronitrile; azobis cyclohexanecarbonitrile; and azobis isobutyric acid methyl, without being limited thereto.

In the step of preparing a rubber seed, the step of preparing a rubber core, and the step of preparing a copolymer shell (graft shell), in addition to the initiator, an oxidation-reduction catalyst may be optionally used to further accelerate initiation reaction. For example, the oxidation-reduction catalyst may include one or more selected from the group consisting of sodium pyrophosphate, dextrose, ferrous sulfide, sodium sulfite, sodium formaldehyde sulfoxylate, sodium ethylenediaminetetraacetate, sulfonato acetic acid metal salt, and sulfinato acetic acid metal salt without being limited thereto.

In at least one step of the step of preparing a rubber seed, the step of preparing a rubber core, and the step of preparing a copolymer shell (graft shell), in addition to the polymerization initiator, an activator is preferably used to promote initiation reaction of peroxides. The activator preferably includes one or more selected from the group consisting of sodium formaldehyde, sulfoxylate, sodium ethylenediamine, tetraacetate, ferrous sulfate, dextrose, sodium pyrrolate, sodium sulfite, sulfonato acetic acid metal salt, and sulfinato acetic acid metal salt.

Based on <NUM> parts by weight in total of monomers added to prepare the copolymer (A), the activator may be added in an amount of <NUM> to <NUM> parts by weight or <NUM> to <NUM> part by weight. Within this range, polymerization rate may increase.

In the step of preparing a seed and the step of preparing a core, as a method of feeding monomers, batch feed or continuous feed may be used alone, or two methods may be used in combination.

In this description, "continuous feed" means that components are not fed batchwise. For example, according to continuous feed, components may be fed for <NUM> minutes or more, <NUM> minutes or more, <NUM> hour or more, preferably <NUM> hours or more within a polymerization time range in drop by drop, little by little, step by step, or continuous flow.

In this description, emulsifiers commonly used in the art to which the present invention pertains may be used in the present invention without particular limitation. For example, the emulsifier of the present invention may include one or more selected from the group consisting of low-molecular weight carboxylates having <NUM> or fewer carbon atoms or <NUM> to <NUM> carbon atoms, such as rosin acid salt, lauric acid salt, oleic acid salt, and stearic acid salt; alkyl sulfosuccinates having <NUM> or fewer carbon atoms or <NUM> to <NUM> carbon atoms or derivatives thereof; alkyl sulfates or sulfonates having <NUM> or fewer carbon atoms or <NUM> to <NUM> carbon atoms; polyfunctional carboxylic acids having <NUM> to <NUM>, <NUM> to <NUM>, or <NUM> to <NUM> carbon atoms and having two or more carboxy groups, preferably <NUM> to <NUM> carboxy groups, or salts thereof; and one or more phosphoric acid salts selected from the group consisting of mono alkyl ether phosphates and dialkyl ether phosphates.

As another example, the emulsifier may include one or more selected from the group consisting of reactive emulsifiers selected from the group consisting of sulfoethyl methacrylate, <NUM>-acrylamido-<NUM>-methylpropane sulfonic acid, sodium styrene sulfonate, sodium dodecyl allyl sulfosuccinate, a copolymer of styrene and sodium dodecyl allyl sulfosuccinate, polyoxyethylene alkylphenyl ether ammonium sulfates, C16-<NUM> alkenyl succinic acid di-potassium salt, and sodium methallyl sulfonate; and non-reactive emulsifiers selected from the group consisting of alkyl aryl sulfonate, alkali methyl alkyl sulfate, sulfonated alkyl esters, fatty acid soap, and alkali salts of rosin acid.

As another example, the derivatives of C12 to C18 alkyl sulfosuccinate metal salts, C12 to C20 alkyl sulfate esters, or the derivatives of sulfonic acid metal salts may be used as the emulsifier. For example, the derivatives of C12 to C18 alkyl sulfosuccinate metal salts may includesodium or potassium salts of dicyclohexyl sulfonate, dihexyl sulfosuccinate, and dioctyl sulfosuccinate, and the C12 to C20 alkyl sulfate esters or the sulfonic acid metal salts may include alkyl sulfate metal salts such as sodium lauric sulfate, sodium dodecyl sulfate, sodium dodecyl benzene sulfate, sodium octadecyl sulfate, sodium oleic sulfate, potassium dodecyl sulfate, and potassium octadecyl sulfate. The emulsifiers may be used alone or in combination thereof.

In this description, a derivative of a compound refers to a substance obtained by substituting at least one of hydrogen and a functional group of the compound with another type of group such as an alkyl group or a halogen group.

In this description, when preparing the copolymer (A), a molecular weight modifier may be optionally included, and then emulsion polymerization may be performed. Based on <NUM> parts by weight of units constituting the copolymer (A), the molecular weight modifier may be included in an amount of <NUM> to <NUM> parts by weight, <NUM> to <NUM> parts by weight, or <NUM> to <NUM> part by weight. Within this range, a polymer having a desired molecular weight may be easily prepared.

For example, the molecular weight modifier may include one or more selected from the group consisting of mercaptans such as α-methyl styrene dimer, t-dodecyl mercaptan, n-dodecyl mercaptan, and octyl mercaptan; halogenated hydrocarbons such as carbon tetrachloride, methylene chloride, and methylene bromide; and sulfur-containing compounds such as tetra ethyl thiuram disulfide, dipentamethylene thiuram disulfide, and diisopropylxanthogen disulfide, and preferably includes mercaptan compounds such as tert-dodecylmercaptan, without being limited thereto.

When emulsion polymerization is performed, polymerization temperature is not particularly limited. In general, emulsion polymerization may be performed at <NUM> to <NUM>, preferably <NUM> to <NUM>.

For example, the copolymer latex (A) prepared in the above step may have a coagulum content of <NUM> % or less, preferably <NUM> % or less, still more preferably <NUM> % or less. Within this range, the productivity of a resin may be increased, and mechanical strength and appearance properties may be improved.

In this description, the weight of coagulum produced in a reactor, the total weight of rubber, and the weight of monomers are measured, and coagulum content (%) is calculated by Equation <NUM> below.

For example, the latex of the copolymer (A) may be prepared in the form of powder through a conventional process including coagulation, washing, and drying. As a specific example, a metal salt or an acid is added, coagulation is performed at <NUM> to <NUM>, and aging, dehydration, washing, and drying are performed to prepare the latex of the copolymer (A) in the form of powder, but the present invention is not limited thereto.

Other conditions not specified in the method for preparing the above-described copolymer (A), i.e., polymerization conversion rate, reaction pressure, reaction time, gel content, etc., are not particularly limited when the conditions are within the ranges commonly used in the technical field to which the present invention pertains. The above conditions may be appropriately selected and used when necessary.

In this description, "%" means "% by weight" unless defined otherwise.

Based on <NUM> % by weight in total of the thermoplastic resin of the present invention, the thermoplastic resin includes <NUM> to <NUM> % by weight of a matrix resin including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer. When the matrix resin (B) is included in the thermoplastic resin, mechanical properties and molding processability may be further improved.

The matrix resin (B) is a hard matrix capable of being melt-kneaded with the dry powder (DP) of the copolymer (A), and includes a hard polymer-forming monomer having a glass transition temperature of <NUM> or higher. The matrix resin (B) preferably has a glass transition temperature of <NUM> to <NUM>, more preferably <NUM> to <NUM>. Within this range, molding processability may be further improved.

The matrix resin (B) includes one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer. Preferably, the matrix resin (B) may be an alkyl methacrylate polymer. In this case, transparency is further improved without deterioration in other properties.

The alkyl methacrylate-alkyl acrylate copolymer that may be included in the matrix resin (B) differs from the graft copolymer (A).

Each of the alkyl methacrylate and the alkyl acrylate included in the matrix resin may be appropriately selected within the same range as those referred regarding the graft copolymer (A).

Preferably, the alkyl methacrylate included in the matrix resin may be methyl methacrylate.

Preferably, the alkyl acrylate included in the matrix resin may be one or more selected from the group consisting of methyl acrylate and ethyl acrylate.

The matrix resin (B) may be prepared by a commonly known method. When preparing the matrix resin (B), one or more of an initiator, a crosslinking agent, and a molecular weight modifier may be included when necessary. The matrix resin (B) may be prepared by suspension polymerization, emulsion polymerization, bulk polymerization, or solution polymerization.

Materials required for reaction such as solvents and emulsifiers or conditions such as polymerization temperature and polymerization time, which are to be added or changed according to polymerization methods, may be appropriately selected without particular limitation when the materials and the conditions are generally applicable depending on a polymerization method selected for the preparation of a matrix resin.

As another example, a commercially available matrix resin may be used as the matrix resin (B).

Based on <NUM> % by weight in total of the thermoplastic resin of the present invention, the thermoplastic resin may include <NUM> to <NUM> % by weight of the copolymer (A) and <NUM> to <NUM> % by weight of the matrix resin (B), preferably <NUM> to <NUM> % by weight of the copolymer (A) and <NUM> to <NUM> % by weight of the matrix resin (B), more preferably <NUM> to <NUM> % by weight of the copolymer (A) and <NUM> to <NUM> % by weight of the matrix resin (B). Within this range, impact resistance, fluidity, and non-whitening properties may be excellent.

The total content of the alkyl acrylate included in <NUM> % by weight in total of the thermoplastic resin is <NUM> to <NUM> % by weight, preferably <NUM> to <NUM> % by weight, more preferably <NUM> to <NUM> % by weight. Within this range, impact strength and non-whitening properties may be excellent without deterioration in weather resistance.

In this description, the total content of the alkyl acrylate included in <NUM> % by weight in total of the thermoplastic resin refers to the sum of the total weight of the alkyl acrylate compounds respectively included in the copolymer (A) and the matrix resin (B), and may be calculated, for example, by summing the weights (parts by weight) of alkyl acrylate compounds fed to prepare the thermoplastic resin. As another example, the total content of the alkyl acrylate may be quantitatively determined by subjecting the thermoplastic resin to nuclear magnetic resonance (NMR) analysis or Fourier transform infrared spectroscopy (FT-IR) analysis.

In this description, NMR analysis means analysis by <NUM>H NMR unless otherwise specified.

In this description, NMR analysis may be performed according to a method commonly practiced in the art, and a specific measurement example is as follows.

In this description, FT-IR analysis may be performed according to a method commonly practiced in the art, and a specific measurement example is as follows.

The thermoplastic resin has a butyl acrylate coverage value (X)of <NUM> % or more, preferably <NUM> to <NUM> %, more preferably <NUM> to <NUM> % as calculated by Equation <NUM> below through the limited composition as described above. Within this range, non-whitening is further improved. <MAT>
wherein G represents the total gel content (%) of the thermoplastic resin, and Y represents the content (% by weight) of butyl acrylate in the gel contained in the thermoplastic resin.

In Equation <NUM>, the content of butyl acrylate in the gel of the thermoplastic resin refers to the content (based on based on <NUM> % by weight in total of the fed thermoplastic resin) of butyl acrylate in insoluble matter (gel) obtained in the aforementioned process of determining gel content. Here, the gel content refers to the content (% by weight) of the insoluble matter based on <NUM> % by weight in total of the thermoplastic resin.

The thermoplastic resin may include one or more types of alkyl acrylate compounds. Specifically, a thermoplastic resin exhibiting excellent non-whitening properties together with excellent mechanical properties such as excellent impact resistance, excellent molding processability, excellent gloss can be provided by limiting the difference between the total gel content and the content of butyl acrylate in the gel with respect to the content of butyl acrylate in the gel included in the thermoplastic resin into a specific range.

In addition, the transparency (haze value) of the thermoplastic resin measured according to ASTM D-<NUM> under a condition of <NUM> thickness according to the aforementioned limited composition may be <NUM> or less, preferably <NUM> or less, more preferably <NUM> or less, and the transparency measured under a condition of <NUM> thickness may be <NUM> or less, preferably <NUM> or less, more preferably <NUM> or less. Within this range, the thermoplastic resin exhibits excellent transparency, thereby proving a finishing material having excellent appearance quality.

The haze of the thermoplastic resin can be measured using a method known in the related art for measuring transparency. Particularly, the haze may be measured according to ASTM D1003. As a particular example, the haze value may be measured at <NUM> according to ASTM D1003 using a haze meter (model name: HM-<NUM>) manufactured by MURAKAMI. Here, a film specimen extruded to a thickness of <NUM> at an extrusion temperature of <NUM> may be used as the specimen having a thickness of <NUM>, and a specimen injected to a thickness of <NUM> at a barrel temperature of <NUM> may be used as the specimen having a thickness of <NUM>.

When elution of the thermoplastic resin is performed using acetone, the elution amount of butyl acrylate is preferably <NUM> % by weight or more, more preferably <NUM> % by weight or more, as a preferred example, <NUM> to <NUM> % by weight, as a more preferred example, <NUM> to <NUM> % by weight. Within this range, non-whitening properties may be excellent.

In this description, when measuring the elution amount of alkyl acrylate using acetone, <NUM> of acetone is added to <NUM> of dry powder of a thermoplastic resin, agitation is performed at <NUM> rpm at room temperature for <NUM> hours using a shaker (SKC-<NUM>, Lab Companion Co. ), centrifugation is performed at <NUM>,<NUM> rpm at <NUM> for <NUM> hours using a centrifuge (Supra R30, Hanil Science Co. ) to obtain an acetone solution from which insoluble matter is separated, and the obtained acetone solution is dried in a forced circulation manner at <NUM> for <NUM> hours using a forced convection oven (OF-12GW, Lab Companion Co. ) to obtain a resin sol. Then, NMR analysis or FT-IR analysis is performed on the resin sol to quantitatively determine the elution amount of an alkyl acrylate.

A difference of refractive index (according to ASTM D542) between a sol and a gel of the thermoplastic resin under a condition of using acetone may be, for example, <NUM> or less, preferably <NUM> to <NUM>, more preferably <NUM> to <NUM>. Within this range, transparency is further improved without deterioration of other physical properties.

In the description, the refractive index difference between a sol and a gel can be obtained as follows: <NUM> of acetone is added to <NUM> of dry powder of the thermoplastic resin, agitation is performed at <NUM> rpm at room temperature for <NUM> hours using a shaker (SKC-<NUM>, Lab Companion Co. ), centrifugation is performed at <NUM>,<NUM> rpm at <NUM> for <NUM> hours using a centrifuge (Supra R30, Hanil Science Co. ) to obtain an acetone solution from which insoluble matter is separated, and then, the dissolved portion is dried in a forced circulation manner at <NUM> for <NUM> hours using a forced convection oven (OF-12GW, Lab Companion Co. ) to obtain a sol, and the separated insoluble matter is dried in a forced circulation manner at <NUM> for <NUM> hours using a forced convection oven (OF-12GW, Lab Companion Co. ) to obtain a gel. Then, a refractive index of each of the sol and the gel is measured according to ASTM D542. The present invention can provide a thermoplastic resin having more improved transparency by controlling a refractive index difference between a sol and a gel within the above range.

In this description, the refractive index may be measured using an Abbe refractometer at <NUM> according to ASTM D542.

When the thermoplastic resin includes the matrix resin (B), a refractive index difference between the rubber (a-<NUM>) of the copolymer (A) and the matrix resin (B) included therein may be for example <NUM> or more, preferably <NUM> to <NUM>, more preferably <NUM> to <NUM>. Within this range, desired effects can be sufficiently realized without deterioration in other properties.

Even when a refractive index difference between the rubber particles and the matrix is <NUM> or more, a refractive index difference between the sol and gel of the thermoplastic resin may be adjusted to <NUM> or less as described above, whereby the transparency of the thermoplastic resin is further improved.

The thermoplastic resin, the rubber (a-<NUM>), or both of them may have a glass transition temperature of, for example, -<NUM> to -<NUM>, preferably -<NUM> to -<NUM>. Within this range, impact strength is further improved without deterioration in other properties.

The thermoplastic resin of the present invention has excellent whitening resistance when bending or folding. For example, when the thermoplastic resin is extruded into a film having a width and length of <NUM> x <NUM> and a thickness of <NUM> and the film is bent at <NUM>° at a temperature of <NUM>, whitening does not occur, indicating that non-whitening properties are excellent.

In addition, the thermoplastic resin of the present invention has excellent whitening resistance against external impact (hit). For example, when the thermoplastic resin is extruded into a film having a thickness of <NUM> and a weight having a weight of <NUM> is vertically dropped onto the film from a height of <NUM> at a temperature of <NUM> using a Gardner impact tester, a difference in haze values measured before and after impact according to ASTM D1003-<NUM> for an area hit by the weight may be <NUM> or less, preferably <NUM> or less, more preferably <NUM> or less. In this case, when bending or external impact is applied, whitening is significantly reduced, and thus problems such as inhibition of expression of intrinsic color due to whitening, deterioration of appearance quality, and reduction of luxuriousness may be prevented, thereby providing a molded article having excellent appearance quality.

In this description, specifically, when a difference in haze values before and after impact is measured, impact is applied to the middle portion of a film having a thickness of <NUM> and a width and length of <NUM> × <NUM> using a weight (Falling Weight <NUM>, Cat. No. <NUM>) and using a Gardner impact tester (Impact Tester <NUM>, BYK Gardner Co. ), haze values before and after impact are measured for the middle portion of the film, and a difference in haze values before and after impact is calculated based the measured values.

The haze value before and after impact may be measured using a method known for measuring transparency in the related field, and in detail, may be measured according to ASTM D1003. As a specific example, the haze value of a film extruded at an extrusion temperature of <NUM> may be measured at <NUM> using a haze meter (model name: HM-<NUM>, MURAKAMI Co. ) according to ASTM D1003.

For example, the thermoplastic resin may have a gloss of <NUM> or more, preferably <NUM> to <NUM>, more preferably <NUM> or <NUM>, still more preferably <NUM> to <NUM> as measured at an incidence angle of <NUM>° according to ASTM D528. Within this range, gloss may be excellent without deterioration in other physical properties, thereby providing a molded article having excellent appearance quality.

For example, the thermoplastic resin may have a melt index (MI) of <NUM>/<NUM> or more, preferably <NUM> to <NUM>/<NUM>, more preferably <NUM> to <NUM>/<NUM>, still more preferably <NUM> to <NUM>/<NUM> as measured according to ASTM D1238. Within this range, molding processability may be excellent without deterioration in other physical properties.

In this description, a melt index may be measured at a temperature of <NUM> for a reference time of <NUM> minutes under a load of <NUM> according to ASTM D1238. As a more particular example, a specimen is heated to <NUM> using a melt indexer (GOETTFERT Co. ), the specimen is placed in the cylinder of the melt indexer, and a load of <NUM> is applied with a piston. At this time, the weight (g) of a resin melted and flowing out for <NUM> minutes is measured, and a melt index is calculated based on the measured value.

A method of preparing the thermoplastic resin of the present invention as defined previously includes a step of kneading and extruding <NUM> to <NUM> parts by weight of the alkyl acrylate-alkyl methacrylate graft copolymer (A) and <NUM> to <NUM> parts by weight of the matrix resin (B) including one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer, wherein an X value as measured by Equation <NUM> below is <NUM> % or more. In this case, molding processability, transparency, gloss, and non-whitening properties may be excellent while maintaining mechanical properties to be equal to those of conventional ASA based resins, thereby providing excellent appearance quality.

The copolymer (A) used in the preparation of the thermoplastic resin may be prepared by the method of preparing the copolymer (A). In this case, grafting degree and molecular weight may be properly adjusted, and thus molding processability and non-whitening properties may be excellent.

When the thermoplastic resin of the present invention is prepared, in the step of kneading and extruding, when necessary, one or more selected from the group consisting of a lubricant, a heat stabilizer, a light stabilizer, an antioxidant, a ultraviolet light stabilizer, a dye, a pigment, a colorant, a release agent, an antistatic agent, an antibacterial agent, a processing aid, a compatibilizer, a metal deactivator, a flame retardant, a smoke suppressant, an anti-drip agent, a foaming agent, a plasticizer, a reinforcing agent, a filler, a matting agent, an antifriction agent, and an anti-wear agent may be further included in an amount of <NUM> to <NUM> parts by weight, <NUM> to <NUM> parts by weight, <NUM> to <NUM> parts by weight, or <NUM> to <NUM> part by weight based on <NUM> parts by weight in total of the copolymer (A) and the matrix resin (B). Within this range, required physical properties may be implemented without deterioration in the intrinsic physical properties of an ASA resin.

For example, the lubricant may include one or more selected from ethylene bis stearamide, polyethylene oxide wax, magnesium stearate, calcium stearamide, and stearic acid, without being limited thereto.

For example, the antioxidant may include phenolic antioxidants, phosphorus antioxidants and the like, without being limited thereto.

For example, the light stabilizer may include HALS-based light stabilizers, benzophenone-based light stabilizers, benzotriazol-based light stabilizers and the like, without being limited thereto.

For example, the antistatic agent may include one or more of anionic surfactants, nonionic surfactants and the like, without being limited thereto.

For example, the release agent may include one or more selected from glycerinstearate, polyethylene tetra stearate and the like, without being limited thereto.

A molded article of the present invention includes the thermoplastic resin of the present invention having excellent non-whitening properties. In this case, weather resistance, impact resistance, molding processability, gloss, and whitening resistance may be excellent, thereby providing excellent appearance quality. Thus, the molded article may be applied to film or sheet products.

For example, the molded article may be a finishing material. In this case, non-whitening properties may be excellent, and thus appearance quality may be excellent.

However, these examples are provided for illustrative purposes only.

<NUM> parts by weight of butyl acrylate, <NUM> part by weight of sodium dodecyl sulfate, <NUM> parts by weight of ethylene glycol dimethacrylate, <NUM> parts by weight of allyl methacrylate, <NUM> parts by weight of sodium hydrogen carbonate, and <NUM> parts by weight of distilled water were fed into a nitrogen-substituted reactor batchwise, temperature was raised to <NUM>, and then <NUM> parts by weight of potassium persulfate was added thereto to initiate reaction. Then, polymerization was performed for <NUM> hour.

<NUM> parts by weight of butyl acrylate, <NUM> part by weight of sodium dodecyl sulfate, <NUM> parts by weight of ethylene glycol dimethacrylate, <NUM> parts by weight of allyl methacrylate, <NUM> parts by weight of distilled water, and <NUM> parts by weight of potassium persulfate were mixed with the rubber seed, and the mixture was continuously fed into a reactor at <NUM> for <NUM> hours. After feeding, polymerization was further performed for <NUM> hour. After completion of the reaction, the average particle size of the obtained rubber polymer was <NUM>.

A mixture prepared by homogeneously mixing <NUM> parts by weight of distilled water, <NUM> parts by weight of methyl methacrylate, <NUM> parts by weight of butyl acrylate, <NUM> part by weight of sodium dodecylbenzene sulfonate, <NUM> parts by weight of tert-dodecyl mercaptan, and <NUM> parts by weight of t-butyl hydroperoxide as an initiator and a mixed solution containing <NUM> parts by weight of sodium ethylenediaminetetraacetate as an activator, <NUM> parts by weight of sodium formaldehyde sulfoxylate, and <NUM> parts by weight of ferrous sulfide were each continuously fed into the reactor containing the rubber core at <NUM> for <NUM> hours to perform polymerization. After completion of the continuous feed, polymerization was further performed at <NUM> for <NUM> hour, and temperature was cooled to <NUM> to terminate and prepare graft copolymer latex.

After completion of the reaction, the grafting degree of the obtained graft copolymer was <NUM> %, and the weight average molecular weight of the shell was <NUM>,<NUM> (g/mol).

<NUM> part by weight of an aqueous calcium chloride solution was added to the prepared graft copolymer latex, coagulation was performed at <NUM> to <NUM> under atmospheric pressure, aging was performed at <NUM> to <NUM>, dehydration and washing were performed, and then drying was performed with hot blast at <NUM> for <NUM> hours to obtain graft copolymer powder.

<NUM> parts by weight of the graft copolymer powder, <NUM> parts by weight of a methyl methacrylate (BA611 manufactured by LGMMA) as a matrix resin, <NUM> parts by weight of a lubricant, <NUM> part by weight of an antioxidant, and <NUM> parts by weight of an ultraviolet light stabilizer were added and mixed. Upon preparation of a specimen for weather resistance evaluation, <NUM> part by weight of black colorant was additionally added to and mixed with <NUM> parts by weight of the total of the graft copolymer and the matrix resin. The mixture was introduced into a <NUM> pie extrusion kneader at a cylinder temperature of <NUM> to prepare pellets. The prepared pellets were injected using an injection machine at a barrel temperature of <NUM> to prepare a specimen for measuring physical properties such as impact strength.

The butyl acrylate (BA) content of the prepared thermoplastic resin was <NUM> % (wt %), the glass transition temperature of the rubber was -<NUM>, a BA coverage value was <NUM> %, and the elution amount of BA in a resin sol was <NUM> %.

A refractive index difference between the sol and the gel of the thermoplastic resin was <NUM>, and a refractive index difference between the rubber (the rubber seed and the rubber core containing the rubber seed) and the matrix resin was <NUM>.

The thermoplastic resin pellets were introduced into a <NUM> pi single extrusion kneader equipped with a T-die at a cylinder temperature of <NUM> to prepare a film having a thickness of <NUM>.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of butyl acrylate was used when preparing a rubber core, and <NUM> parts by weight of methyl methacrylate and <NUM> parts by weight of butyl acrylate were used when preparing a copolymer shell.

The grafting degree of the obtained graft copolymer was <NUM> %, and the weight-average molecular weight of the shell was <NUM>,<NUM>.

The BA content in the prepared thermoplastic resin was <NUM> %, a BA coverage value was <NUM> %, and the elution amount of BA in a resin sol was <NUM> %.

A refractive index difference between the sol and the gel of the thermoplastic resin was <NUM>, and a refractive index difference between the rubber and the matrix resin was <NUM>.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of butyl acrylate were used when preparing a rubber core, and <NUM> parts by weight of methyl methacrylate and <NUM> parts by weight of butyl acrylate were used when preparing a copolymer shell.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of sodium dodecyl sulfate were used when preparing a rubber seed.

An average particle size of the obtained rubber polymer (rubber core) was <NUM>, a grafting degree of the graft copolymer was <NUM> %, and the weight-average molecular weight of the shell was <NUM>,<NUM>.

An average particle size of the obtained rubber polymer was <NUM>, a grafting degree of the graft copolymer was <NUM> %, and the weight-average molecular weight of the shell was <NUM>,<NUM>.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of butyl acrylate and <NUM> parts by weight of methyl methacrylate were used when preparing a rubber core, and <NUM> parts by weight of sodium dodecyl sulfate, <NUM> parts by weight of butyl acrylate, and <NUM> parts by weight of methyl methacrylate were used when preparing a rubber seed.

The BA content in the prepared thermoplastic resin was <NUM> %, the glass transition temperature of the rubber was - <NUM>, a BA coverage value was <NUM> %, and the elution amount of BA in a resin sol was <NUM> %.

The BA content in the prepared thermoplastic resin was <NUM> %, a rubber glass transition temperature was -<NUM>, a BA coverage value was <NUM> %, and the elution amount of BA in a resin sol was <NUM> %.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of butyl acrylate and <NUM> parts by weight of methyl methacrylate were used when preparing a rubber core, <NUM> parts by weight of sodium dodecyl sulfate, <NUM> parts by weight of butyl acrylate, and <NUM> parts by weight of methyl methacrylate were used when preparing a rubber seed, and <NUM> parts by weight of methyl methacrylate and <NUM> parts by weight of butyl acrylate were used when preparing a shell.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of methyl methacrylate and <NUM> parts by weight of butyl acrylate were used when preparing a copolymer shell.

A grafting degree of the obtained graft copolymer was <NUM> %, and the weight-average molecular weight of the shell was <NUM>,<NUM>.

The BA content in the resin was <NUM> %, a BA coverage value was <NUM> %, and the elution amount of BA in a resin sol was <NUM> %.

The BA content in the resin was <NUM> %, the glass transition temperature of the rubber was -<NUM>, a BA coverage value was <NUM> %, and the elution amount of BA in a resin sol was <NUM> %.

Preparation processes were performed in the same manner as in Example <NUM>, except that, when preparing thermoplastic resin, a matrix resin was not used and the graft copolymer was used in an amount of <NUM> parts by weight.

A refractive index difference between the sol and the gel of the thermoplastic resin was <NUM>.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of butyl acrylate were used when preparing a rubber core, and <NUM> parts by weight of methyl methacrylate were used when preparing a copolymer shell.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of sodium dodecyl sulfate were used when preparing a rubber seed, and <NUM> parts by weight of methyl methacrylate were used to prepare a shell.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of sodium dodecyl sulfate, <NUM> parts by weight of butyl acrylate, and <NUM> parts by weight of methyl methacrylate were used when preparing a rubber seed, <NUM> parts by weight of butyl acrylate and <NUM> parts by weight of methyl methacrylate were used when preparing a rubber core, and <NUM> parts by weight of methyl methacrylate were used when preparing a shell.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of methyl methacrylate and <NUM> parts by weight of butyl acrylate were used when preparing a shell.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of the graft copolymer powder and <NUM> parts by weight of the matrix resin were used when preparing a thermoplastic resin.

Preparation processes were performed in the same manner as in Comparative Example <NUM>, except that <NUM> parts by weight of the graft copolymer powder and <NUM> parts by weight of the matrix resin were used when preparing a thermoplastic resin.

Preparation processes were performed in the same manner as in Comparative Example <NUM>, except that <NUM> parts by weight of methyl methacrylate and <NUM> parts by weight of butyl acrylate were used when preparing a shell, and <NUM> parts by weight of the graft copolymer powder and <NUM> parts by weight of the matrix resin were used when preparing a thermoplastic resin.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of sodium dodecyl sulfate, <NUM> parts by weight of butyl acrylate, and <NUM> parts by weight of styrene were used when preparing a rubber seed, <NUM> parts by weight of butyl acrylate and <NUM> parts by weight of styrene were used to prepare a rubber core, and <NUM> parts by weight of styrene and <NUM> parts by weight of acrylonitrile were used when preparing a shell.

The average particle size of the obtained rubber polymer was <NUM>, a grafting degree of the graft copolymer was <NUM> %, and the weight-average molecular weight of the shell was <NUM>,<NUM>.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of a styrene-acrylonitrile resin (S85RF manufactured by LG Chem) as a matrix resin were used when preparing a thermoplastic resin.

A BA coverage value was <NUM> %, and the elution amount of BA in a resin sol was <NUM> %.

Preparation processes were performed in the same manner as in Example <NUM>, except that <NUM> parts by weight of a styrene-acrylonitrile-methyl methacrylate copolymer (XT500 manufactured by LG Chem) as a matrix resin were used when preparing a thermoplastic resin.

A graft copolymer was prepared in the same manner as in Example <NUM>, except that <NUM> parts by weight of butyl acrylate and <NUM> parts by weight of methyl methacrylate were used when preparing a rubber seed, <NUM> parts by weight of butyl acrylate and <NUM> parts by weight of methyl methacrylate were used when preparing a rubber core, and <NUM> parts by weight of methyl methacrylate and <NUM> parts by weight of butyl acrylate were used when preparing a copolymer shell.

A thermoplastic resin was prepared in the same manner as in Example <NUM>, except that the prepared graft copolymer was used in an amount of <NUM> parts by weight, and <NUM> parts by weight of an alphamethylstyrene-styrene-acrylonitrile copolymer (S99UH manufactured by LG Chem) were used as a matrix resin.

The physical properties of the specimens and films prepared in Examples <NUM> to <NUM> and Comparative Examples <NUM> to <NUM> were measured according to the following methods, and the results are shown in Tables <NUM> and <NUM> below.

In Equation <NUM>, the weight of grafted monomers is a value obtained by subtracting the weight (g) of rubber from the weight of insoluble matter (gel) obtained by dissolving a graft copolymer in acetone and performing centrifugation, and the weight (g) of rubber is the amount (parts by weight) of rubber components theoretically included in the graft copolymer powder. Here, the parts by weight of the rubber means the total sum of parts by weights of unit components fed when preparing a rubber seed and a core.

In Equation <NUM>, G represents the total gel content (%) of the thermoplastic resin, and Y represents the content (% by weight) of butyl acrylate in the gel. Here, the content (% by weight) of butyl acrylate in the gel was quantitatively measured using an <NUM>H NMR analyzer or FT-IR.

Weather resistance (ΔE): The weather resistance of a specimen manufactured by adding <NUM> part by weight of a black colorant to <NUM> parts by weight of the thermoplastic resin was measured for <NUM>,<NUM> hours under SAE J2527 condition using an accelerated weather resistance test apparatus (weather-o-meter, Ci4000 manufactured by ATLAS, xenon arc lamp, Quartz (inner)/S. Boro (outer) filter, irradiance <NUM> W/m<NUM> at <NUM>), and then evaluated as ΔE calculated according to Equation <NUM> below. ΔE below is an arithmetic mean value of Hunter Lab (L, a, b) values measured before and after the accelerated weather resistance test. As ΔE is close to <NUM>, weather resistance is superior. <MAT> (√ : radical symbol).

In addition, a film having a thickness of <NUM> and a width and length of <NUM> × <NUM> was prepared. Then, a weight having a weight of <NUM> (Cat No. <NUM>, Falling Weight <NUM>) was vertically dropped onto the film from a height of <NUM> at a temperature of <NUM> using a Gardner impact tester (Impact Tester <NUM>, BYK Gardner Co. ), haze values before and after impact were measured for the middle portion of the film impacted by the weight according to ASTM D1003-<NUM>, and a difference in haze values was calculated by Equation <NUM> below (dropping-caused whitening).

Referring to Tables <NUM> and <NUM>, in the case of bending-caused whitening, when whitening occurs, it is marked as "O". When whitening does not occur (non-whitening), it was marked as "X". In the case of dropping-caused whitening, the haze difference values calculated by Equation <NUM> are shown.

In this case, haze was measured at a temperature of <NUM> using a haze meter (model name: HM-<NUM>, MURAKAMI Co. ) according to ASTM D1003-<NUM>.

Referring to Tables <NUM> and <NUM>, it can be confirmed that the thermoplastic resins (Examples <NUM> to <NUM>) according to the present invention exhibit excellent transparency, gloss and weather resistance while appropriately maintaining the balance between a melt index and impact strength and, specifically, do not exhibit bending-caused whitening and exhibit a haze difference of <NUM> or less before and after dropping impact, which indicates excellent non-whitening properties. On the other hand, it can be confirmed that, in the case of the thermoplastic resins (Comparative Examples <NUM> to <NUM>) outside the scope of the present invention, the balance between a melt index and impact strength is decreased, and transparency, gloss, and weather resistance are generally decreased or whitening occurs when bent, and a haze difference before and after dropping impact exceeds <NUM>, which indicates that the property balance among transparency, gloss, weather resistance, and non-whitening properties is very poor.

<FIG> includes images taken after bending, in the Md and Td directions, films manufactured in an example (left image) and a comparative example (right image) to check whether whitening occurs. As shown in <FIG>, in the case of the example according to the present invention, whitening does not occur at the bent portion, indicating that the example according to the present invention has non-whitening properties. However, in the case of the comparative example outside the scope of the present invention, whitening occurs clearly at the bent portion.

Claim 1:
A thermoplastic resin, comprising:
an alkyl acrylate-alkyl methacrylate graft copolymer (A), or an alkyl acrylate-alkyl methacrylate graft copolymer (A); and a matrix resin (B) comprising one or more selected from the group consisting of an alkyl methacrylate polymer and an alkyl methacrylate-alkyl acrylate copolymer,
wherein a transparency (haze value), measured according to ASTM D-<NUM> under a condition of <NUM> thickness, is <NUM> or less, and a transparency measured under a condition of <NUM> thickness is <NUM> or less,
a total content of the alkyl acrylate is <NUM> to <NUM> % by weight, and
a butyl acrylate coverage value (X) as calculated by Equation <NUM> below is <NUM> or more: <MAT>
wherein G represents a total gel content (%) of the thermoplastic resin, and Y represents a content (% by weight) of butyl acrylate in the gel of the thermoplastic resin,
wherein the copolymer (A) comprises <NUM> to <NUM> % by weight of an alkyl acrylate rubber (a-<NUM>) having a DLS average particle diameter of <NUM> to <NUM> or a TEM average particle diameter of <NUM> to <NUM>; and <NUM> to <NUM> % by weight of an alkyl acrylate-alkyl methacrylate copolymer (a-<NUM>) based on <NUM> % by weight in total of the copolymer (A),
wherein the copolymer (A) has a grafting degree of <NUM> to <NUM> %, and the copolymer (a-<NUM>) has a weight-average molecular weight of <NUM>,<NUM> to <NUM>,<NUM>/mol, and
wherein the total content of the alkyl acrylate, the butyl acrylate coverage value, the total gel content of the thermoplastic resin, the content of butyl acrylate in the gel, the grafting degree and the weight-average molecular weight are measured as disclosed in the specification.