Patent Number: 046684441
Section: claims

1. In a process for the production of a substantially isotropic spherical fuel or absorber element of high strength for a high temperature reactor by molding a mixture of graphite molding powder containing a resin binder with coated nuclear fuel or absorber particles to a spherical nucleus, pressing on a shell of the same graphite molding powder, carbonizing the resin binder and vacuum calcining at a temperature up to about 2000.degree. C., the improvement comprising employing as the graphite molding powder a mixture of graphitized coke particles having substantially isotropic properties and a hardenable binder resin, first preliminarily pressing from this graphite molding powder at 80.degree. to 120.degree. C. two ellipsoidally shaped shell halves successively in a first cylindrical steel molding die having a smooth ellipsoidal hollowing of the lower die and a smooth ellipsoidally shaped front surface of the upper die adjusted to it, also preliminarily pressing from another portion of the graphite molding power and coated particles likewise at 80.degree. to 120.degree. C. in a second steel molding die which also has smooth surfaces and relative to the shell halves, appropriately ellipsoidally shaped spherical nucleus whereby the pressing is to such an extent that the density of the graphite matrix in the preliminarily pressed nucleus and in the preliminarily pressed shell halves is between 1.1 and 1.4 g/cm.sup.3, then putting together the nucleus and the two shell halves to form an ellipsoidally shaped body and finally completing the molding in the plastic temperature range of the resin binder to form a final sphere and removing it from the mold. 2. A process according to claim 1 wherein there is employed graphitized soft coal secondary pitch coke as the graphite powder and that the density of the preliminary pressed portions is between 1.1 and 1.3 g/cm.sup.3. 3. A process according to claim 2 wherein the resin binder is hardened in the molding die in the final molding process and the molded body is discharged from the die at molding temperature. 4. A process according to claim 1 wherein the resin binder is hardened in the molding die in the final molding process and the molded body is discharged from the die at molding temperature. 5. A process according to claim 4 including the step of preheating the preliminarily pressed portions to a temperature just below the final molding temperature and inserting it in the preheated mold. 6. A process according to claim 3 including the step of preheating the preliminarily pressed portions to a temperature just below the final molding temperature and inserting it in the preheated mold. 7. A process according to claim 2 including the step of preheating the preliminarily pressed portions to a temperature just below the final molding temperature and inserting it in the preheated mold. 8. A process according to claim 1 including the step of preheating the preliminarily pressed portions to a temperature just below the final molding temperature and inserting it in the preheated mold. 9. A process according to claim 8 comprising carrying out the final molding in a floating matrix. 10. A process according to claim 5 comprising carrying out the final molding in a floating matrix. 11. A process according to claim 1 comprising carrying out the final molding in a floating matrix.