Patent Number: 048426652
Section: claims

1. A process for producing a graphite monochromator for X-rays or neutrons having a mosaic spread of 4.degree. or less, which comprises pyrolyzing a plurality of sheets of film of a polymer selected from the group consisting of aromatic polyimides having the repeating unit represented by the formula (I): ##STR4## wherein X denotes O, CH.sub.2 or SO.sub.2 ; polyphenylene-vinylenes having the repeating unit represented by the formula (II): EQU --R--CH.dbd.CH-- (II)  wherein R denotes an aromatic hydrocarbon group conjugating with the adjacent vinylene group:  polymeric sulfonium salts represented by the formula (III): ##STR5## wherein R denotes the same as defined in the formula (II) above, R.sup.1 and R.sup.2 each denote an alkyl group of 1 to 10 carbon atoms and Y denotes a counter ion; and  polyoxadiazoles having the repeating unit represented by the general formula (IV): ##STR6## in an inert atmosphere at a temperature of 2,000.degree. C. to 3,500.degree. C. to form a graphitized film and  laminating the sheets of the resulting graphitized film to one another or laminating a plurality of sheets of the polymer film to one another prior to the pyrolysis.  pre-heating a film of polymer selected from the group consisting of aromatic polyimides having the repeating unit represented by the formula (I): ##STR8## wherein X denotes O, CH.sub.2 or SO.sub.2, polyphenylene-vinylenes having the repeating unit represented by the formula (II): EQU --R--CH .dbd.CH-- (II)  wherein R denotes an aromatic hydrocarbon group conjugating with the adjacent vinylene group,  polymeric sulfonium salts represented by the formula (III): ##STR9## wherein R denotes the same as defined in the formula (II) above, R.sup.1 and R.sup.2 each denote an alkyl group of 1 to 10 carbon atoms and Y denotes a counter ion, and  polyoxadiazole having the repeating unit represented by the general formula (IV): ##STR10## in an inert atmosphere at a temperature of 500.degree. C. to 1,500.degree. C. while holding the film between two thermally stable plates, and  pyrolyzing the pre-heated film in an inert atmosphere at a temperature of 2,000.degree. C. to 3,500.degree. C. while holding the film between two thermally stable plates having a clearance of 3 to 100 times the thickness of the film to form a graphite film and  laminating a plurality of sheets of the resulting graphite film to one another.  pre-heating a film of polymer selected from the group consisting of aromatic polymides having the repeating unit represented by the formula (I): ##STR11## wherein X denotes O, CH.sup.2 or SO.sub.2, polyphenylene-vinylenes having the repeating unit represented by the formula (II): EQU --R--CH.dbd.CH-- (II)  wherein R denotes an aromatic hydrocarbon group conjugating with the adjacent vinylene group,  polymeric sulfonium salts represented by the formula (III): ##STR12## wherein R denotes the same as defined in the formula (II) above, R.sup.1 and R.sup.2 each denote an alkyl group of 1 to 10 carbon atoms and Y denotes a counter ion, and  polyoxadiazole having the repeating unit represented by the general formula (IV): ##STR13## in an inert atmosphere at a temperature of 500.degree. C. to 1,500.degree. C. while holding the film between two thermally stable plates, and  pyrolyzing a plurality of sheets of the pre-heated film put between two thermally stable plates in an inert atmosphere at a temperature of 2,000.degree. C. to 3,000.degree. C. thereby to obtain a laminated graphite produce. 2. The process according to claim 1, wherein the lamination of the graphite films is carried out by adhering a plurality of the graphite film with an adhesive containing a graphitizable material and then heating the laminate at 700.degree. to 3,500.degree. C. 3. The process according to claim 2, wherein the graphitizable material is selected from the group consisting of polyvinyl chloride, a pitch and a polymeric sulfonium salt represented by the formula (III); ##STR7## wherein R denotes an aromatic hydrocarbon group conjugating with the adjacent vinylene group formed by elimination of the sulfonium salt, R.sup.1 and R.sup.2 each denote an alkyl group of 1 to 10 carbon atoms and Y denotes a counter ion. 4. The process according to claim 1, wherein a pre-heating of the polymer film is carried out in an inert atmosphere at a temperature of 500.degree. C. to 1,500.degree. C., a plurality of sheets of the pre-heated film are laminated prior to the pyrolysis, and the heating rate above the temperature at which the polymer begins to decompose and up to the pre-heating temperature is 1.degree. C./minute or more. 5. A process for producing a graphite monochromator for X-rays or neutrons having a mosaic spread of 4.degree. or less, which comprises 6. A process for producing a graphite monochromator for X-rays or neutrons having a mosaic spread of 4.degree. or less, which comprises