Patent Number: 052001172
Section: description

DETAILED DESCRIPTION According to the present invention, alkaline earth metal sulfate scales, especially barium sulfate scale, are removed by the use of a combination of chemical scale-removing agents. The method is particularly useful for the removal of such scale from oilfield equipment used to bring oil and/or water from subterranean formations to the surface. The method may, however, also be used to remove scale from the formations themselves, especially in the regions surrounding production and injection wells, as mentioned above. The method may also be used to remove scale from above- ground equipment both in the oilfield and elsewhere, for example, from boilers and heat exchangers and other equipment exposed to scale-forming conditions. The scale itself is usually in the form of an adherent deposit of the scale-forming mineral on metal surfaces which have been exposed to the water containing the scale-forming components. These components comprise alkaline earth metals including calcium, strontium and barium, together with variable amounts of radium, depending upon the origin of the waters. As noted above barium sulfate scale is particularly difficult to remove by existing chemical methods in view of its very low solubility. The present scale removal is effected with an aqueous solvent which comprises a polyaminopolycarboxylic acid such as EDTA or DTPA as a chelant or chelating agent which is intended to form a stable complex with the cation of the alkaline earth scale-forming material. Of these chelants, DTPA is the preferred species since it forms the most soluble complexes at greatest reaction rate. EDTA may be used but is somewhat less favorable and, as noted below, may be less responsive to the addition of the catalyst or synergist. The chelant may be added to the solvent in the acid form or, alternatively, as a salt of the acid, preferably the potassium salt. In any event the alkaline conditions used in the scale removal process will convert the free acid to the salt. The concentration of the chelant in the solvent should normally be at least 0.1M in order to achieve acceptable degree of scale removal. Chelant concentrations in excess of 1.0M are usually not necessary and concentrations from about 0.3M up to about 0.6M will normally give good results; although higher concentrations of chelant may be used, there is generally no advantage to doing so because the efficiency of the chelant utilisation will be lower at excess chelant concentrations. This economic penalty is particularly notable in oilfield operations where large volumes of solvent may be used, especially in formation scale removal treatment. In addition to the chelant, the present scale removal compositions contain a catalyst or synergist for the dissolution of the scale. This catalyst is an anion or anions of at least one monocarboxylic acid. The acid may be substituted with various functional groups, especially electronegative groups such as hydroxyl, amino, halo or mercapto or may be unsubstituted. The lower substituted fatty acids such as the C.sub.1 -C.sub.3 substituted fatty acids where the substituent is an electronegative group such as hydroxy, mercapto, or amino are suitable since they have good solubility in oilfield waters, are readily available and are relatively inexpensive. Suitable acids of this type include mercaptoacetic acid, aminoacetic acid and hydoxyacetic acid. The unsubstituted fatty acids such as acetic acid and formic acid have not be found to provide any major improvement in scale removal with DTPA as a chelant and are therefore not preferred. The aromatic carboxylic acids may also be used when they have an adequately high solubility in water. The acid may have substituents other than the carboxyl group on the aromatic nucleus, for example, hydroxyl as in salicylic acid which is a preferred acid of this type. Other aromatic carboxylic acids with carboxyl groups attached directly to the aromatic nucleus may also be used. The preferred acids have been found to enhance the rate of barium sulfate scale dissolution using polyaminopolycarboxylic chelants, especially DTPA, to a significant and useful degree, so that dissolution of oilfield scales is usefully accelerated by the use of these compositions. It has been found that the action of the synergist may be selective for the chelant. For example, salicylate produces a significant increase in scale removal with the chelant DTPA but only a slight improvement with EDTA. The use of DTPA is therefore favored not only because it generally shows an improved propensity in itself to remove the alkaline earth metal sulfate scales but also because it exhibits better response to a number of these synergists. The concentration of the catalyst or synergist in the aqueous solvent will be of a similar order: thus, the amount of the carboxylate anion in the solvent should normally be at least 0.1M in order to achieve a perceptible increase in the efficiency of the scale removal, and concentrations from about 0.3M up to about 0.6M will give good results. Although higher concentrations of the synergist e.g. above 1.0M may be used, there is generally no advantage to doing so because the efficiency of the process will be lower at excess catalyst concentrations. Again, this economic penalty is particularly notable in oilfield operations. As with the chelant, the carboxylate synergist may be added as the free acid or the salt, preferably the potassium salt. If the free acid is used addition of the potassium base to provide the requisite solution pH will convert the acid to the salt form under the conditions of use. The scale removal is effected under alkaline conditions preferably at pH values of from about 8.0 to about 14.0, with optimum values being from about 11 to 13, preferably about 12. The prefered solvents comprise about 0.1 to about 1.0M ethylenediaminetetraacetic acid (EDTA) or diethylenetriaminepentaacetic acid (DTPA), or salts of these acids, as a chelant. In addition, the carboxylate catalyst is added to the aqueous solution in about 0.01 to about 1.0 preferably about up to 0.5M. The pH of the solvent is then adjusted by the addition of a base to the desired value, preferably to about pH 12. We have found that it is important to avoid the use of sodium cations when operating at high pH values, above pH 8, and instead, to use potassium or alternatively, cesium as the cation of the scale-removing agent. Potassium is preferred for economy as well as availability. Thus, the normal course of making up the solvent will be to dissolve the chelant and the acid synergist (or its potassium salt) in the water to the desired concentration, after which a potassium base , usually potassium hydroxide is added to bring the pH to the desired value of about 12. This aqueous composition can be used to remove scale from the equipment, or alternatively, pumped into the subterranean formation when it is the formation which is to be subjected to descaling. The mode of operation of the synergist or catalyst is not presently understood. While not desiring to be bound to a particular theory concerning the actual mechanism of its activity in converting or dissolving the scale, it is believed that adsorption of the synergist or catalyst on the barium sulfate surface may modify the surface crystal structure in such a way that the barium in the modified crystal is easily removed by the chelating agent. The aqueous solution containing the composition can be directed down a wellbore to remove barium sulfate scale which has fouled the tubular equipment e.g. piping, casing etc., and passage ways. Prior to being directed into the wellbore, the composition may be heated to a temperature between about 25.degree. C. to about 100.degree. C., although the temperatures prevailing downhole may make pre-heating unnecessary. Once within the tubular goods and the passageways requiring treatment, the composition is allowed to remain there for about ten minutes to about 7 hours. After remaining in contact with the equipment for the desired time, the composition containing the dissolved scale is produced to the surface and may be disposed of as required, possibly by re-injection into the subsurface formation. This procedure can be repeated as often as required to remove scale from the equipment. In one procedure for circulating the solvent through the tubular goods the well the solvent is pumped down through the production tube and returned to the surface through the annular space between the production tubes and the casing (or vice versa). Also the cleaning solution may be pumped down through the production tubing and into the formation, thereby cleaning the well, including the well casing, and the formation pore space by dissolving barium sulfate present as it flows over and along the surfaces that need cleaning. The spent composition containing the dissolved, complexed barium together with any other alkaline earth metal cations which may have been present in the scale, especially radium, can be subsequently returned to the surface, for example, by displacement or entrainment with the fluids that are produced through the well after the cleaning operation. In an alterative manner, the cleaning solution may be applied batchwise fashion, for example, by flowing the solution into the well and optionally into the pore spaces of the adjacent earth formation and there keeping the solution in contact in non-flowing condition with the surfaces that are covered with barium sulfate scale, for a period of time sufficient to dissolve the scale. The present scale removal technique is very effective for lowering residual radioactivity of pipe contaminated with radium-containing barium sulfate scale. As noted above, radium is frequently precipitated with barium in scale with the result that scaled pipe is often radioactive to the point that it cannot safely be used. Using the present scale removal compositions, activity can be reduced to an acceptable levels comparatively short times without further treatment. Some residual activity which arises from lead and other radio isotopes which are not dissolved in the solvent: these isotopes are decay products of radium and have originally been incorporated in the scale with the barium and the radium sulfates. Although they are not removed chemically by the present scale removal technique, the dissolution of the barium scale together with the other alkaline earth metal sulfates enables these other components of the scale to be removed by simple abrasion, for example, by scrubbing with or without a detergent/water scrub solution. In this way, the residual activity level may be reduced to a very low value, below the appropriate regulatory standards. Thus, by using the present chemical scale removal technique in combination with a simple mechanical removal of loose, non-adherent material, previously radioactive pipe may quickly and readily be restored to useful, safe condition. In order to demonstrate the barium sulfate scale-dissolving capacities of the composition, several aqueous solutions have been tested in laboratory tests the results of which are described in the discussions which follow. The experiments described below were, except as noted below, carried out in a cylindrical glass vessel having a height of 10 cm and an internal diameter of 7.5 cm. Barium sulfate or, when applicable, other sulfates or solid scale components, were agitated with the selected solvents and the rates of dissolution and final dissolved concentrations determined. The results are reported graphically in the FIGS. As shown in FIG. 1, DTPA alone and DTPA with various substituted acetic acids were compared at 100.degree. C. The results demonstrate that the DTPA/carboxylate combination complexes more barium sulfate than DTPA alone. FIG. 2 compares the relative rates of barium sulfate dissolution using DTPA alone and DTPA in combination with salicylic acid. As shown in the FIG., the addition of salicylic acid is effective to almost double the degree of barium sulfate dissolution. Distilled water was used in the majority of the above tests (except the continuous flow loop tests) for determination of the rate of barium sulfate dissolution and saturation. Minor decreases in efficiency may be observed with tap water and more significant decreases with seawater, e.g. about 20 percent decrease with seawater. This is reasonably to be expected since seawater has interfering ions, e.g. calcium and magnesium. These interfering ions complex with the chelating agent, either DTPA or EDTA, and reduce the overall dissolving power. Additionally, it has been determined that halide ions have a negative effect on dissolving power as a function of the size of the halide ion. Dissolution rate is increased as the halide ion size is reduced and the charge density is increased, i.e. in the order of iodide, bromide, chloride and fluoride. Fluoride ion enhances the effect of EDTA-based solvents, but not DTPA: fluoride inhibits most DTPA/catalyst solvents. As noted above, the effect of cations is also very important to the success of the scale solvent, especially when added with the sizable portion of caustic required to adjust the pH to 12. Dissolution is enhanced as the size of the cation is increased, i.e. lithium, sodium, potassium and cesium. Lithium and sodium hydroxides in the presence of EDTA, or DTPA, and catalysts are not soluble at a pH of 12, the optimum value. Cesium is too difficult to obtain, both in quantity and price. Therefore, potassium hydroxide, in the form of caustic potash, is the pH adjusting reagent of choice.