Patent Number: 056489951
Section: abstract

The method serves to manufacture tubes for constituting sheaths for nuclear fuel rods. A bar is made out of a zirconium-based alloy containing 50 ppm to 250 ppm iron, 0.8% to 1.3% by weight niobium, less than 1600 ppm oxygen, less than 200 ppm carbon, and less than 120 ppm silicon. The bar is heated to a temperature in the range 1000.degree. C. to 1200.degree. C. and is quenched in water. A blank is extruded after heating to a temperature in the range 600.degree. C. to 800.degree. C. and cold-rolled in at least four passes in order to obtain a tube, with intermediate heat treatment being performed between passes at temperatures in the range 560.degree. C. to 620.degree. C. A final heat treatment is performed at a temperature in the range 560.degree. C. to 620.degree. C., all of the heat treatments being performed under an inert atmosphere or a vacuum.