Patent Number: 045227691
Section: claims

1. A method of producing coherent compacts of particulate ceramic nuclear fuel material whereby the ceramic material is rendered more plastic and amenable to processing, consisting essentially of the sequence of steps of: (a) adding a fugitive binder consisting essentially of at least one amine selected from the group consisting of ethylene diamine, 3.3 diaminodipropylamine, 1.3 diaminopropane, 1.6 diaminohexane, 1.7 diaminoheptane, diethylenetriamine, and 3-dimethylaminopropylamine to particulate nuclear fuel material of uranium dioxide and blending the binder therethrough;  (b) thereafter introducing carbon dioxide gas into the blend of particulate fuel material and amine binder; and  (c) pressing the resultant blend comprising particulate fuel material and amine binder having had the carbon dioxide gas introduced therein into a coherent compact.  (a) adding a fugitive binder consisting essentially of at least one multifunctional primary amine selected from the group consisting of ethylene diamine, 3.3 diaminodipropylamine, 1.3 diaminopropane, 1.6 diaminohexane, 1.7 diaminoheptane, diethylenetriamine, and 3-dimethylaminopropylamine to particulate nuclear fuel material consisting of uranium dioxide and blending the binder therethrough;  (b) thereafter introducing carbon dioxide gas into the blend of particulate fuel material and amine binder; and  (c) pressing the resultant blend comprising particulate fuel material and amine binder having had the carbon dioxide gas introduced therein into a coherent compact.  (a) adding a fugitive binder consisting essentially of ethylene diamine to particulate nuclear fuel material consisting of uranium dioxide and blending the binder therethrough;  (b) thereafter introducing carbon dioxide gas into the blend comprising particulate fuel material and amine binder;  (c) pressing the resultant blend comprising particulate nuclear fuel material and ethylene diamine having had the carbon dioxide gas introduced therein into a coherent compact; and  (d) sintering the compact of the blend to expel binder material and integrate the particulate nuclear fuel material into a uniform body.  (a) adding a fugitive binder consisting essentially of at least one amine selected from the group consisting of ethylene diamine, 3.3 diaminodipropylamine, 1.3 diaminopropane, 1.6 diaminohexane, diethylene triamine and 3-dimethylaminoproplyamine to particulate nuclear fuel material consisting of uranium dioxide in amount of about 0.5 to about 4% by weight of the amine based upon the weight of the fuel material and blending the binder thereof;  (b) thereafter introducing carbon dioxide gas into the blend comprising particulate fuel material and amine binder in amount of at least one mole of carbon dioxide gas for each gram mole of NH.sub.2 in the amine;  (c) pressing the resultant blend comprising particulate nuclear fuel material and ethylene diamine having had the carbon dioxide gas introduced therein into a coherent compact; and  (d) sintering the compact of the blend to expel binder material and integrate the particulate nuclear fuel material into a uniform body. 2. The method of claim 1, wherein the fugitive binder is a water solution of the amine. 3. The method of claim 1, wherein the fugitive binder comprises a multifunctional primary amine. 4. The method of claim 1, wherein the fugitive binder comprises ethylene diamine. 5. A method of producing coherent compacts of particulate ceramic nuclear fuel material whereby the ceramic material is rendered more plastic and amenable to processing, consisting essentially of the sequence of steps of: 6. The method of claim 5, wherein the fugitive binder is a water solution of the multifunctional primary amine. 7. The method of claim 5, wherein the fugitive binder comprises ethylene diamine. 8. The method of claim 5 wherein multifunctional primary amine is added to the particulate nuclear fuel material in amount of about 0.3 to about 4% by weight of the amine based upon the weight of the fuel material. 9. A method of producing coherent compacts of particulate ceramic nuclear fuel material whereby the ceramic material is rendered more plastic and amenable to processing, consisting essentially of the sequence of steps of: 10. The method of claim 9 wherein the fugitive binder is a water solution of the multifunctional primary amine. 11. The method of claim 9, wherein the carbon dioxide gas is introduced in amount of at least one mole of carbon dioxide gas for each gram mole of NH.sub.2 in the amine. 12. The method of claim 9, wherein multifunctional primary amine is added to the particulate nuclear fuel material in amount of about 0.3 to about 4% by weight of the amine based upon the weight of the fuel material. 13. A method of producing coherent compacts of particulate cdramic nuclear fuel material whereby the ceramic material is rendered more plastic and amenable to processing, consisting essentially of the sequence of steps of: