Patent Number: 050248057
Section: description

DETAILED DESCRIPTION The present method for decontaminating metal surfaces having an oxide coating containing radioactive substances, such as the primary system surfaces of a pressurized water nuclear reactor, uses an aqueous solution of weak chelants and iron (II) or ferrous iron. The weak chelant maintains the dissolved metals in solution and prevents precipitation, while the ferrous iron improves the dissolution rate and minimizes base metal corrosion. The radioactive metals that are to be removed in a pressurized water reactor primary system include ferric iron (Fe.sup.III), nickel, chromiun, cobalt and manganese, which are metals forming the primary system components. The process uses an aqueous decontamination solution containing a weak chelant, capable of forming multiligand complexes with the metals of the oxide coating, in an amount of between 0.1 to 2.0 percent by weight based on the weight of the solution. The weak chelants are complexing agents generally having an equilibrium constant for metal ions, such as ferric ions, of between about 10.sup.12 to 10.sup.19. Examples of such chelants are nitrilotriacetic acid (NTA), hydroxyethylenediamine tetraacetic acid (HEDTA), citric acid, and iminodiacetic acid (IDA), with NTA being preferred because of its high iron capacity, multiligand ability, and relatively low complexation constant. Preferably, the concentration of the chelant is about 0.2 percent based on the weight of the aqueous solution. The use of less than about 0.1 percent chelant will not keep the ions in solution and chelate ions removed from the surface, while more than about 2.0 percent is inefficient and unnecessary. In addition to the weak chelant, the aqueous solution contains an organic ferrous salt in an amount to provide a ferrous iron (Fe.sup.II) concentration of between about 50 to 500 parts per million (ppm) based on the weight of solution. If less than about 50 ppm ferrous iron is present, the decontamination will not be effected, while more than about 500 ppm is inefficient and wasteful. Preferably about 100 ppm of ferrous iron of such an organic ferrous salt is used. These salts are ferrous salts of polyfunctional organic acids that are compatible with the materials of the primary system during operation of the pressurized water nuclear reactor. Organic acids are required to form the ferrous salts because inorganic acids can leave residual ions that can cause corrosion problems in the reactor during subsequent operations, whereas organic acids decompose to produce water and carbon dioxide. Such ferrous salts include ferrous acetate, ferrous oxalate, and ferrous gluconate. While the latter two ferrous salts are relatively insoluble in water, the same will dissolve in dilute chelant solutions. The ferrous iron (Fe.sup.II), with NTA, provides for reduction dissolution of the metal oxide with rapid kinetics (equations 1 and 2): ##EQU1## Multiple ligand complexes can then form. Corrosion of the base metal is inhibited by reactions such as equation 3, as compared to equation 4 for ferric ion corrosion: ##EQU2## The presence of a relatively large concentration of ferrous iron (Fe.sup.II) shifts the equilibrium and also inhibits ferric iron (Fe.sup.III) corrosion by equation 4. Additional ferrous iron is provided during decontamination. During the decontamination, the metal oxide film dissolves, and iron is present generally as ferric iron (Fe.sup.III). This can be reduced in a sidestream, electrolytic reactor using porous electrodes, as described in U.S. Pat. No. 4,537,666, assigned to the assignee of the present invention and incorporated by reference herein, i.e.: ##STR1## The electrolytic approach is effective for concentrated solutions (say 1 wt %), and will provide for a gradual buildup of ferrous iron (Fe.sup.II). However, entire loop decontamination will use dilute solutions, and will require a consistent ferrous iron (Fe.sup.II) presence throughout the application for corrosion and kinetic purposes. After passing the decontamination solution over the metal surface to remove radioactive substances therefor, the solution is regenerated and returned for further contact with those surfaces. Regeneration may be effected by treating a portion or sidestream thereof, either by use of cation exchange resins or electrolytically. The use of cation exchange resins to remove contaminants and recover reagents for reuse in decontamination methods is known. Solution regeneration by cation exchange is somewhat complicated, here, however, as ferrous iron (Fe.sup.II) complexes are more readily removed than ferric iron (Fe.sup.III) complexes. It is thus advisable to valve in an ion exchange column after the method has been running for a period of time, e.g. two hours. Electrolytic regeneration is the preferred regeneration method since it preferentially reduces the ferric iron (Fe.sup.III), albeit at a reduced efficiency in the dilute solution. Such electrolytic regeneration, as described in U.S. Pat. No. 4,537,666, passes the decontamination solution through a permeable electrode formed by a stainless steel wire or copper mesh in order to plate out the ions. When the electrode becomes spent, it is replaced. Or, as described in U.S. Pat. No. 4,792,385, assigned to the assignee of the present invention, the contents of which are incorporated herein, the permeable electrode may be comprised of a bed of carbon, or graphite particles, or an electrically conductive plastic material such as polyacetylene. Regardless of the method of regeneration used, however, slipsream regeneration of a large pressurized water reactor will have a long time constant, such as approximately 6 hours, and thus, will be incomplete. The time for decontamination of a pressurized water invention system using a present process would be expected to be in a range of about 6 to 24 hours. The temperature of the decontamination solution does not need adjustment and will typically be at a temperature of 70.degree. C. to 150.degree. C. during the decontamination method. The present process thus provides a chemical method for decontaminating pressurized water nuclear reactor systems utilizing a ferrous salt in the decontamination solution with the benefits described herein.