Patent Number: 051679124
Section: description

DETAILED DESCRIPTION OF THE INVENTION The instant invention is an improved neutron reflecting supermirror which comprises a plurality of stacked sets of bilayers of high and low neutron scattering powered materials. The high and low neutron scattering power materials are deposited on a substrate, which substrate is typically selected from the group consisting of pyrex glass, boron containing glasses, float glass and silicon. One layer of each of said sets of bilayers consists of titanium and second layer of each set of said bilayers consists of an alloy including nickel and a microstructure enhancing element. In a first preferred embodiment the microstructure enhancing element has a high neutron scattering potential and is present interstitially in the nickel layer so as to reduce the nickel grain size. In a further preferred embodiment the microstructure enhancing element is carbon and is present in the nickel layer in concentrations between five and fifty percent and particularly in concentrations between twelve and thirty percent. The nickel alloy layer of each of said sets of bilayers typically has the nominal composition of Ni.sub.86 C.sub.14 or Ni.sub.72 C.sub.28. As referred to hereinabove, the improved neutron reflecting supermirror comprises a number of stacked sets of bilayers, which sets of bilayers is typically numbered between two and one thousand and most preferably between twenty and five hundred. The thickness of each of said sets of bilayers is typically between five and two hundred nm. The improved neutron reflecting supermirror may further include a buffer layer disposed either between said substrate and the first of said sets of bilayers, or atop the upper most layer of the top set of bilayers. The buffer layer is typically between 10 and 1500 nm thick and most preferably approximately one hundred nm. The buffer layer is typically a layer of nickel or nickel carbon alloy disposed to a thickness of approximately one hundred nm. The improved neutron reflecting supermirror may further include an intermediate layer disposed between between each of said alternating layers of titanium and nickel carbon alloy. In a preferred embodiment the intermediate layer is a layer of carbon deposited to a thickness of between two and five hundred nms. Referring now to FIG. 1, there is illustrated therein the improved neutron reflecting supermirror structure of the present invention. The supermirror structure 18 is constructed as a plurality of stacked sets of bilayers 20, only two of which are illustrated, but which typically would be between two and one thousand sets. Each of the layer set 20 is formed from at least two units U.sub.1 and U.sub.2. Each of the layer sets have respective d spacings of d.sub.1 and d.sub.2, which may or may not be equal to one another. One of the units U.sub.1 and U.sub.2 includes at least one layer of material which has a relatively high neutron scattering power or potential and the other of said units of U.sub.1 and U.sub.2 includes at least a layer of material with relatively low neutron scattering potential material. In a preferred embodiment, U.sub.1 is a relatively low neutron reflecting material such as titanium disposed atop a layer of relatively high neutron scattering potential material such as a layer nickel. It is the essence of the invention that the relatively high neutron scattering power layer include a microstructure enhancing element also having a high neutron scattering potential. In the preferred embodiment the microstructure enhancing element is carbon and is present interstitially in the nickel crystal grain in concentrations between five and fifty percent. In one embodiment, the nominal composition of the high neutron scattering potential layer, U.sub.2 is Ni.sub.72 C.sub.28. In a second embodiment of the instant invention the nominal composition of the layer U.sub.2 is Ni.sub.86 C.sub.14. It is however to be understood that the instant invention contemplates high neutron scattering potential layers having carbon present in concentrations from 5% to 50%. I.e., Ni.sub.95 C.sub.5 through Ni.sub.50 C.sub.50. While not wishing to be bound by theory, the instant inventors have hypothesized that layers of pure Ni alone a insufficiently dense: i.e., too many voids exist in the Ni crystalline lattice. The result is the buckling, cusping, and layer distortion reported by earlier researchers. Conversely, it is believed that the microstructure enhancing material, carbon, may be serving as a catalyst to prevent the buckling and cusping by occupying otherwise vacant parts of the Ni lattice. The result is a smoother, flatter Nickel alloy layer free from the cusping and layer distortions found in previous Ni-Ti supermirrors, and hence better able to reflect neutrons incident thereupon. The neutron reflecting supermirror structure of the instant invention is disposed atop the substrate 19 and may further include a buffer layer 21a. The buffer layer 21a may be disposed either upon said substrate 19 and below the first set of bilayers 20, or as is illustrated in FIG. 1, the buffer layer 21 may be disposed upon the to top or uppermost of said sets of bilayers 20. Alternatively the neutron reflecting supermirror may include said buffer layer disposed as both the uppermost and lowermost layers. The buffer layer 21 and 21a is typically between one and one thousand nm thick and preferably approximately one hundred nm thick. The buffer layer 21 and 21a is typically formed as a layer of nickel, a nickel carbon alloy or carbon deposited upon said substrate and providing a base upon which to subsequently deposit said plurality of sets of bilayers, or upon the uppermost set of bilayers. The neutron reflecting supermirror of FIG. 1 further possess a neutron dispersion pattern which can be altered to reflect incident neutrons from desired angles. Specifically, an incident beam of cold neutrons is made up of neutrons of a single wavelength (lambda) of 4 angstroms. The reflected beam is hence made up of a single wavelength of 4 angstroms reflected at an angle theta approximately according to Bragg's law: EQU n lambda=2d sine theta wherein n=1 (for consideration of 1st order reflections); lambda=4 angstroms, the wavelength of cold neutrons; and 2d= the period or thickness of a given set of bilayers. Since the value of n lambda remains constant it is thus possible to alter the reflected angle theta by varying the value for 2d. Algorithms for fabricating basic layered supermirror structures are disclosed in, for example, Majkrzck, et al, MRS Proc., "Fe-W Supermirrors for Polarizing Neutrons", 103, 115-120 (1988); and Hayter and Mook, J. Appl. Cryst., "Discrete Thin-Film Multilayer Design for X-Ray and Neutron Supermirrors", 22, 35-41 (1989) the disclosure of which is incorporated herein by reference. The result of employing a known algorithm is a distribution of bilayer (2d) thicknesses that cause overlapping Bragg diffraction peaks to occur from the region just above the Nickel cutoff angle to some increased angle of acceptance. It is of course critical that reflectivity remain near 100% as the reflection angle is extended, since otherwise the cumulative reduction from each reflection along the guidetube would result in an unacceptable loss of neutron flux. It is this point which the inventive neutron reflecting supermirror addresses. More specifically and referring now to FIG. 2, there is illustrated therein a plot of reflectivity versus angle for a standard Nickel coating and the improved neutron reflecting supermirror. A perusal of FIG. 2 illustrates that the reflectivity of the best standard nickel coating, illustrated by Curve 30, is extremely good, i.e., approximately 100% up to the critical angle of nickel, approximately 0.4 degrees theta. However, as the critical angle increases, the reflectivity of the nickel coating falls off drastically; down to 0% reflectivity before 2x the critical angle of nickel, (approx. 0.8 degrees theta) and certainly to less than 10% by 0.5 degrees theta. Conversely, Ti:Ni-C alloy supermirros as illustrated in FIG. 1 demonstrate excellent neutron reflectivity, i.e. greater than 95% at critical angles of up to 3.times. the critical angle of nickel alone. More specifically, Curves 32 and 34 illustrate a Ti:Ni.sub.72 -C.sub.28 alloy in two different layering algorithm structures. The structure illustrated in Curve 32 demonstrates reflection of approximately 95% out to two times the critical angle of the best standard Ni coating. The structure of Curve 34 demonstrates even better performance, having reflection of approximately 97% out to three times the critical angle of the best standard Ni coating. In order to better understand the structure of the neutron reflecting supermirror structures of the instant invention, the following examples are presented as illustrative of the method of fabricating the same. EXAMPLE The inventive neutron reflecting supermirror structure of the instant invention was fabricated with a Ti/Ni.sub.72 C.sub.28 coating deposited on 5 cm .times.10 cm float glass. The glass substrate was cut to size from a 4 in .times.4 in piece of float glass. Prior to deposition of the neutron reflecting supermirror structure upon the float glass, said substrate was cleaned by first hand washing said substrate in a CDC degreaser, which is thereafter thoroughly rinsed off in de-ionized water. Thereafter the substrate was immersed in a de-ionized water ultrasonic bath for one half hour and was then rinsed with methanol and blown dry with nitrogen. The substrate is then loaded into an ion beam chamber and mounted on the substrate spinning rotation stage. The chamber was a horizontal cylinder with two 5" round by a 1/4" thick target materials screwed onto opposite sides of a water cooled stainless steel block. The target block centered in the chamber and fixed to a horizontal shaft pointing inwards radially to the cylinder. The targets were positioned at a 45% angle to the horizontal and rotate 180.degree. at specified intervals. The ion beam source was a 5 cm Hollow Cathode Source fixed to the end of the cylinder. An ion beam of Ar+ ions from the source was propelled towards the target block along the axis of the cylindrical chamber. Between the source and the target block was a Hollow Cathode Neutralizer which is aimed at a perpendicular to the beam of ions, intersecting with the beam roughly 3" from the source. The Hollow Cathode Neutralizer neutralizes the argon ions, which keeps the beam from spreading out from charge repulsion. Atoms strike the target materials, causing atoms of the target materials to be ejected. The sputtered atoms leave the target in all directions, with the highest percentage leaving at a perpendicular to the target. The substrates to be coated were approximately seven inches from the target. Also at a 45.degree. angle, the substrate was parallel to the target and rotated slowly in order to insure the uniformity of the coating. The substrate assembly attached to the end of the chamber, just above the 5 cm source. The 5 cm source parameters are: 1500 V beam, 180 V Accelerator, and 50 mA beam current. The system was pumped down to 1.0E-6 torr with a cryogenic pump. Argon gas was introduced into the chamber through a hollow cathode at a rate of 4.0 sccms/sec, bringing the chamber pressure to 2.0E-4 torr. A Ni-alloy target was constructed by covering 30% of a carbon target with four inward pointing triangles of nickel foil. The foil was tied to the target with nickel wire. The other target sputtered was simply solid titanium. After the beam sputters a target for a set length of time, the beam shuts off, the target block rotates 180.degree. and exposes the other target, then the beam starts back up again. The timers were connected to magnetic proximity switches, which stopped the target every 180.degree. and told the stepper motor when to turn the target block. The process is repeated over and over, resulting in a stack of layers of alternating materials on the substrate. One layer of material 1 (e.g. NiC), together with one layer of material 2 (Ti), constitutes a d-spacing. Calibration runs were performed in order to relate the time a target si sputtered to resultant thicknesses of that material on the substrate. The sputtering times for the various d-spacings required for a supermirror were interpolated from a graph of sputter time vs layer thickness for the two materials with a straight line connecting the two data points. Following all depositions, the substrates and system are allowed to cool in a vacuum with a background pressure of argon gas. As the layer structure of the supermirror is multiple graded, i.e., the d-spacing of each of said sets of bilayers is different, the deposition time of the titanium and nickel carbon alloy for each bilayer set will vary. The grading herein and the pattern for setting down the graded layers is established by a layer algorithm of the type disclosed hereinabove in, for example, the Hayter and Mook reference. While the invention has been described in connection with preferred embodiments and procedures be understood that it is not intended to limit the invention to the described embodiments and procedures. On the contrary it is intended to cover all alternatives, modifications and equivalents which may be included within the sphere and scope of the invention as defined by the claims appended herein after.