Patent Number: 
Section: description

The present invention provides an ion beam generator capable of high average power and repetitive operation over an extended number of operating cycles for thermally treating large surface areas of materials at commercially attractive costs. In particular, the ion beam generator of the present invention can produce high average power (1-1000 kW) pulsed ion beams at 0.25-2.5 MeV energies and pulse durations or lengths of 30-500 nanoseconds (ns). The ion beam generator can directly deposit energy in the top 1-50 micrometers (xcexcm) of the surface of any material. The depth of thermal treatment can be controlled by varying the ion energy and species as well as the pulse length. Irradiating a material with ion beams in accordance with the present invention is a thermal process that does not significantly change the atomic composition of the material. Instead it thermally heats the near surface using typically 3xc3x971013 ions/cm2 per pulse, only approximately 10xe2x88x925-10xe2x88x923 atomic percent of the sample density. Deposition of ion beam energy in a thin near surface layer allows melting of the layer with relatively small energies (typically 1-10 J/cm2) and allows rapid cooling of the melted layer by thermal diffusion into the underlying substrate as depicted in FIG. 1. The relatively small energy densities needed for treatment together with the high instantaneous powers available using the present invention allows large surfaces areas (up to 1000 cm2) to be treated with a single ion beam pulse greatly reducing or eliminating edge effects at the transition between treated and untreated areas. The relatively short ion beam pulse lengths, preferably xe2x89xa6200 ns, developed by the ion beam generator limit the depth of thermal diffusion, thus allowing the treated/melted region to be localized to a selected depth. Typical cooling rates of the present invention (108-1010 K/sec) are sufficient to cause amorphous layer formation in some materials, fine grain structures in some materials, the production of non-equilibrium microstructures (nano-crystalline and metastable phases), and the formation of new alloys by rapid quenching and/or liquid phase mixing of layers of different materials. Such rapid thermal quenching ( greater than 108 K/sec) can significantly improve corrosion, wear and hardness properties of the treated near surface layer. Other applications of the present invention can include etching and cross linking of polymers, surface glazing and sealing of ceramic surfaces for reduced porosity, and a cost-effective, solvent-free process for surface deburring, polishing, cleaning, and oxide layer removal. The unique energy deposition as a function of depth, as depicted in FIG. 2, also allows ion beams produced according to the present invention to be used for bonding films to substrates and mixing interface materials by liquid phase mixing. Surface modification by rapid, localized melting, with or without vaporization of the surface can be used for annealing of surfaces and modifying surface microstructure, including metals, semiconductors, and polymers. The microstructures produced will be determined by the choice of material, the beam intensity, energy, composition, and the number of pulses used to treat an area. The ion beam generator can also produce pulsed ion beams with intensities sufficient to vaporize surface layers. Applications of this capability include the production of high energy vapor for depositing films. The ion beam generator can also be used for ion implantation at relatively high voltages (0.25-2.5 MV), with greatly reduced cost, greater depths, and larger treatment area due to the higher energy per pulse, higher voltage, and low cost, repetitive capability of this new technology. At higher intensities, the ion beam generator can also be used to produce surface ablation that creates shock waves that propagate into materials, causing dislocations and increasing the hardness of the material. The ion beam generator of the present invention is composed of two major components: a high energy, pulsed power system and an ion beam source both capable of high repetition rates and both having extended operating lives. The first of these components is a compact, electrically efficient, repetitively pulsed, magnetically switched, pulsed power system capable of 109 pulse operating cycles as generally described by H. C. Harjes, et al, Pro 8th IEEE Int. Pulsed Power Conference (1991) all of which is incorporated by reference herein. The power system can operate continuously at a pulse repetition rate of 120 Hz delivering up to 2.5 kJ of energy per pulse in 60 ns pulses. The power system can deliver pulsed power signals of 30-500 ns duration with ion beam energies of 0.25-2.5 MeV. The power system can operate at 50% electrical efficiency from the wall plug to energy delivered to a matched load. The power system uses low pulse compression stages incorporating, for example, low loss magnetic material and solid state components, to convert AC power to short, high voltage pulses. High electrical efficiency is important in reducing the cooling requirements and the capital and operating costs of the power system. The ability to produce voltages from 250 kV to several MV by stacking voltage using inductive adders incorporating low loss magnetic material is also an important feature when high voltages are needed although it is also possible to use a single stage, eliminating the need for the adder. The power system can operate at relatively low impedances ( less than  less than 100 xcexa9) which also sets it apart from many other repetitive, power supply technologies such as transformer-based systems. This feature is necessary to allow high treatment rates and the treatment of large areas (up to 1000 cm2) with a single pulse so as to reduce edge effects occurring at the transition between treated and untreated areas. A block diagram of the power system P is shown in FIG. 3. From the prime power input, several stages of magnetic pulse compression and voltage addition are used to deliver a pulsed power signal of up to 2.5 MV, 60 ns FWHM, 2.9 kJ pulses at a rate of 120 Hz to an ion beam source. The power system P converts AC power from the local power grid into a form that can be used by the ion beam source. In one embodiment of the invention, the power system P comprises a motor driven 600 kW, 120 Hz alternator 10. In the unipolar mode it provides 210 A rms at a voltage of 3200 V rms with a power factor of 0.88 to a pulse compressor system 15. In an alternative embodiment, the alternator 10 can be replaced by a variable frequency modulator (not shown). Such modulator can deliver a 5 kJ, (1xe2x88x92cos xcfx89t) voltage pulse to the pulse compressor system 15 with a time to peak that permits the elimination of the first 2 or 3 stages in the pulse compressor system 15. The modulator can have a variable pulse repetition frequency (prf) and consequently will be a more flexible power source for the ion beam source (i.e. the input power can be adjusted by simply changing the prf). The pulse compression system 15 can provide unipolar, 250 kV, 15 ns rise, 60 ns FWHM, 4 kJ pulses, at a rate of 120 Hz, to a linear inductive voltage adder (LIVA) 20. In one embodiment, the pulse compression system 15 is a common magnetic pulse compressor composed of a plurality of magnetic switches (i.e. saturable reactors) the operation of which is well known to those skilled in the art. In order to satisfy the systems performance requirements, the pulse compression system 15 should have an efficiency 80% and be composed of high reliability components with very long lifetimes (xcx9c109-1010 pulses). Magnetic switches are preferably used in all of the pulse compression stages because they can handle very high peak powers (i.e. high voltages and currents), and because they are basically solid state devices with the potential to satisfy the lifetime requirement. The LIVA 20 is a liquid dielectric insulated voltage adder and can deliver nominal 2.5 MV, 2.9 kJ, pulses at a rate of 120 Hz to the ion beam source 25. The nominal output pulse of the LIVA 20 is trapezoidal with 15 ns rise and fall times and 60 ns FWHM. The second component of the present invention is an ion beam source or accelerator capable of operating repetitively and efficiently to transform the pulsed power signal from the power system efficiently into an ion beam as described generally by J. B. Greenly et al, xe2x80x9cPlasma Anode Ion Diode Research at Cornell: Repetitive Pulse and 0.1 TW Single Pulse Experimentsxe2x80x9d, Proceedings of 8th Intl. Conf. on High Power Particle Beams (1990) all of which is incorporated by reference herein. The ion beam source is capable of operating at repetitive pulse rates of 100 Hz continuously with long component lifetimes  greater than 106. Preferably, the ion beam source comprises a magnetically-confined anode plasma (MAP) source, which draws ions from a plasma anode rather than a solid dielectric surface flashover anode used in present single pulse ion beam sources. The MAP source can provide pure beams of different ion species without employing components or techniques that have intrinsically short lifetimes. The ion beam generates is pulsed rather than continuous, allowing more compact, less expensive equipment to achieve high ion energies. Any ion can be used to deposit the energy. Protons have the greatest penetration depth of any ion and thus provide the greatest treatment depth while higher mass ions can deposit their energy at lesser depths. The MAP source M is shown in FIG. 4. In particular, FIG. 4 is a partially cross-sectional view of one symmetric side of the MAP source M. The MAP source M produces an annular ion beam K which can be brought to a broad focus symmetric about the axis Xxe2x80x94X shown. In the cathode electrode assembly 30 slow (1 xcexcs rise time) magnetic field coils 32 produce magnetic flux S which provides the magnetic insulation of the accelerating gap between the cathode 32 and the anode electrode assembly 34 and which is connected to the output of the pulsed power system (not shown). The anode electrodes 34 also act as magnetic flux shapers. The MAP M source operates in the following fashion: a fast gas valve 36 on the axis of anode assembly 35 produces a rapid (200 xcexcs) gas puff which is delivered through a supersonic nozzle 38 to produce a highly localized volume of gas directly in front of the surface of a fast driving coil 40 located in an insulating structure 42. After pre ionizing the gas with a 1 xcexcs induced electric field, the fast driving coil 40 is energized, inducing a loop voltage of 20 kV on the gas volume, driving a breakdown to full ionization, and moving the resulting plasma toward the flux shaping electrodes 34 in about 1.5 xcexcs, to form a thin magnetically-confined plasma layer. The pulsed power signal from the power system is then applied to the anode assembly 35, accelerating ions from the plasma to form the ion beam K. The slow (S) and fast (F) magnetic flux surfaces, at time of ion beam extraction, are also shown. The plasma can be formed using a variety of gases. This ion source system can use any gas (including hydrogen, nitrogen and argon) or high vapor pressure liquid or metal to produce a pure source of ions without consuming or damaging any component other than the gas supplied to the source. The ion beam K propagates 20-30 cm in vacuum (xcx9c10xe2x88x923) to a broad focal area (up to 1000 cm2) at the target plane where material samples are placed for treatment and can thermally alter areas from 50 cm2 to 1000 cm2. Operation of the MAP source depends in part on the ability to provide ions at current densities exceeding by factors of several those available using standard space charge limited flow defined by the geometric gap and voltage. This is done by forming a virtual cathode consisting of electrons emitted from the cathode near the ion source on the anode. The present invention provides a system and a process for generating high voltage ion beams repetitively over an extended number of operating cycles in a manner that satisfies several criteria and constraints imposed by the use of this technology for the efficient treatment of surfaces in commercial applications. In particular, the present invention comprises a pulsed power system and an ion beam source that are designed and combined in such a way as to satisfy the following criteria. The operation of high current, pulsed ion beam source depends in part on the ability to provide ions at current densities exceeding by factors of several those available using standard space charge limited flow defined by the geometric gap and voltage. This is done by forming a virtual cathode consisting of electrons emitted from the cathode near the ion source on the anode. A carefully optimized magnetic field topology is required to confine these electrons to form a sheath extending from the cathode to the anode in the ion emitting region of the anode. In the simplest model these electrons fill the gap in a few nanoseconds, providing a space charge profile in the gap that allows ion current densities to be much larger than those available without the virtual cathode formed by the electron sheath filling the anode-cathode gap. Experiments show that the delay in obtaining enhanced ion current density is 10-20 ns. This places a lower limit on the pulse length required for reasonable efficiency of the system. Based on this information the pulse length above half voltage points should be at least 30 ns. The voltage, current and impedance of the pulsed power system required for effective, repetitive ion beam surface treatment is constrained by several factors. These include the need to generate large enough voltages to obtain the needed depth of penetration of ions into materials. This voltage is at least 250 kV for multi-micron penetration depth and extends to several MV. A typical operating voltage is 0.75 MV. The energy deposition depth of protons in steel is approximately 5 microns at this voltage. The current density needed to provide 5 J/cm2, a typical level needed to melt surfaces to this depth, is approximately 100 A/cm2 for a 60 ns pulse. In order to treat a 100 cm2 area (large enough to minimize edge effects) a total ion current of 10,000 Amperes is needed. A 67% ion efficiency gives total current and impedance requirements of 15,000 Amperes and 50 xcexa9 respectively. In generally these considerations lead to an ion source impedance significantly less than 100 xcexa9, at voltages of at least 250 kV. The ion beam source must satisfy several criteria that are unique to its combination in repetitively pulsed, long lifetime, high voltage systems for pulsed ion beam treatment of surfaces. The ion beam source must produce only low levels of gas during operation to prevent vacuum degradation beyond the 1xc3x9710xe2x88x923 Torr level between pulses. The ion beam generated must be extractable through any insulating magnetic field with little or no rotation to allow propagation of the ion beam in a field-free region and focusing of the beam at intensities up to several tens of Joules/square centimeter on a material surface at least 20 centimeters away from the ion beam source. Many ion beam systems, including previous Magnetically confined Anode Plasma systems were fundamentally incapable of this because of incompatible magnetic field configurations in the diode (ion beam generating section). In particular, previous MAP sources produced an ion beam which rotated. Such rotation can result in the rapid dispersal of the ion beam as it propagates in free space. In the present invention it is necessary for the ion beam to travel up to 20-30 cm to a material surface and as such rotation of the ion beam is unacceptable. Applications of present invention include production of low cost materials with treated surfaces for handling corrosive environments and treatment of large area metal sheets and critical components used in manufacturing and other areas where hardness, toughness and corrosion or wear resistance are important. It can also be used to produce smooth, crack-resistant ceramic surfaces by melting and re solidification using pulsed ion beams. By varying ion beam deposition levels and pulse durations it is also possible to use this technology for either surface cleaning or annealing. At high deposition levels (xcx9c30 J/cm2) it is possible to do shock hardening of materials. Polymer processing and ion implantation can be done at lower deposition levels. Examples of thermal surface treatment using this process are shown in FIGS. 5, 6, 7a, 7b and 8a, 8b. Surface cleaning or preparation without the use of organic solvents, can be accomplished by choosing higher mass ions (e.g. nitrogen, carbon) to deposit all of the beam energy in an approximately 1 xcexcm thin region at the surface of the material, producing high surface temperatures which vaporize this contaminant-containing layer without significantly disturbing the underlying material. In particular, FIG. 5 depicts a stainless steel 304 sample, which was initially coated with machining oil, producing a 100 nm thick coating of hydrocarbons, after treatment with 1-2 Joules per square centimeter of 0.75 MeV carbon ions the hydrocarbon contamination layer was removed leaving only normal atmospheric contamination FIG. 6 is a cross sectional view of an 0-1 tool steel sample showing the effects of rapid surface melting and cooling after exposure by a 60 ns, 10 J/cm2, 1 MeV mixed proton and carbon beam which resulted in increased hardness as well as a mixture of amorphous and retained metastable austenite with dissolved carbide precipitates that are retained in solution. FIGS. 7a depicts a sample of Ti-6A1-4V alloy after treatment with a 300 keV, 2-4 J/cm2 beam of mixed protons and carbon resulting in polishing of pre-existing machining marks with 10 xcexcm roughness to  less than 1 xcexcm depicted in FIG. 7b. By inducing surface melting, porous dielectric films can be sealed or metal surfaces xe2x80x9cpolishedxe2x80x9d by material reflow. FIG. 8 depicts a sample of polished alumina which was subjected to a 60 ns, 10 J/cm2, 1 MeV beam of mixed protons and carbon resulting in surface melting and re-solidification. Unlike lasers which deposit energy to metals in the near surface (≈30 nm) only, an ion beam deposits its energy throughout its penetration depth extending to several microns. Additionally ion beams have the unique capability to deposit energy preferentially near the end of their penetration depth, in the interior of the sample, due to the inverse dependence of ion stopping power and energy. In addition to improving adhesion between the coating and substrate over large areas, the thermal fatigue resistance can also be enhanced. In a ceramic/metal system thermal-expansion-generated stresses at the boundary can be distributed over a relatively thick boundary layer following pulsed melting rather than being concentrated at the original atomically sharp interface. The flexibility of choosing the ion beam species and energy density provide substantial control over the degree of mixing, especially for dissimilar materials. Another related application of this technology is in the use of its rapid quenching and surface smoothing capability to produce thin layers of amorphous material with much higher quench rates and at much lower cost than is possible using existing splat-quenching techniques. The use of this technology to form very fine grain materials is also valuable in advanced battery applications. The capability of the present invention for producing high purity, high average power ion beams results in the potential for a new, low cost, compact surface treatment technology capable of high volume commercial applications and new treatment techniques not possible with existing systems. Having thus described the present invention with the aid of specific examples, those skilled in the art will appreciate that other similar combinations of the capabilities of this technology are also possible without departing from the scope of the claims attached herewith.