Patent Number: 049851837
Section: claims

1. A process for fabricating uranium dioxide (UO.sub.2) pellets from highly active uranium dioxide powders, comprising: (1) uniformly adding at least one pore-former agent in the range of 0.3 to 1.4% by weight to uranium dioxide powders as a starting material, the pore-former agent decomposing and sublimating below 600.degree. C. and having an average particle size in the range of 5 to 500 microns,  (2) compacting the uranium dioxide powders including the pore-former agent to form green pellets, and  (3) sintering the green pellets to form sintered UO.sub.2 pellets having an average crystalline grain size larger than 20 microns. 2. A process for fabricating UO.sub.2 pellets as claimed in claim 1, wherein the compacting step is performed after at least one lubricant is added to the uranium dioxide powders including the pore-former agent. 3. A process for fabricating UO.sub.2 pellets as claimed in claim 1, wherein the compacting step is performed after inner surfaces of a mold are coated with at least one lubricant. 4. A process for fabricating UO.sub.2 pellets as claimed in claim 1, wherein the uranium dioxide powders including the pore-former agent are subjected to rough compacting and pulverization to form granules having particle sizes less than 2000 .mu.m, and the granules are subjected to compacting. 5. A process for fabricating UO.sub.2 pellets as claimed in claim 4, wherein the compacting is performed after at least one lubricant is uniformly added to the granules. 6. A process for fabricating UO.sub.2 pellets as claimed in claim 4, wherein the compacting is performed after the granules are filled into a mold whose inner surfaces is coated with at least one lubricant. 7. A process for fabricating UO.sub.2 pellets as claimed in claim 1, wherein at least one pore-former agent is selected from the group consisting of ammonium acetate, ammonium carbonate, ammonium bicarbonate, ammonium oxalate, ammonium alginate and stearic acid. 8. A process for fabricating UO.sub.2 pellets as claimed in claim 1, wherein at least one of the lubricants is selected from the group consisting of stearic acid, zinc stearate, lithium stearate, stearic amide, ethylene-bis-stearic amide and polyethylene glycol. 9. A process for fabricating UO.sub.2 pellets as claimed in claim 1, wherein said sintered pellets have a sintered density in the range between 94 to 97 percent of the theoretical density. 10. A process for fabricating UO.sub.2 pellets as claimed in claim 1, wherein said pore-former agent has a particle size between 10 and 100 microns. 11. A process for fabricating UO.sub.2 pellets as claimed in claim 4, wherein said granules have particle sizes less than 1000 microns.