Patent Number: 053612825
Section: claims

1. A method for manufacturing a dimensionally stable and corrosion-resistant fuel channel, comprising the steps of: forming first and second strips of material comprising metal alloy in a hexagonal close-packed crystallographic phase having a uniform texture;  subjecting said first and second strips to heat treatment by heating to a first temperature which initiates transformation from said hexagonal close-packed crystallographic phase to a body-centered cubic crystallographic phase and then quenching to a second temperature at a rate which initiates transformation to a hexagonal close-packed crystallographic phase having a texture factor f.sub.L =0.28-0.38;  forming each of said heat-treated first and second strips into first and second fuel channel components respectively;  seam welding said first and second fuel channel components to assemble a fuel channel; and  subjecting said fuel channel to thermal sizing by heating to a third temperature less than said second temperature and sufficient to anneal said material and then cooling.  forming first and second strips of material comprising metal alloy in a hexagonal close-packed crystallographic phase having a uniform texture;  subjecting said first and second strips to heat treatment by heating to a first temperature in the temperature range of 1800.degree. F. to 2050.degree. F., holding at a temperature no less than said first temperature for no less than 0.25 sec and then quenching to a second temperature not greater than 1500.degree. F.;  warm forming each of said heat-treated first and second strips into first and second fuel channel components respectively by heating said first and second strips to a third temperature sufficient to increase the ductility of said strip material prior to forming;  seam welding said first and second fuel channel components to assemble a fuel channel; and  subjecting said fuel channel to thermal sizing by heating to a fourth temperature in a temperature range of 1000.degree. F. to 1250.degree. F., holding at a temperature no less than said fourth temperature for no less than 15 minutes and then cooling, wherein said third temperature is less than said fourth temperature.  forming first and second strips of material comprising metal alloy in a hexagonal close-packed crystallographic phase having a uniform texture;  subjecting said first and second strips to heat treatment by heating to a first temperature which initiates transformation from said hexagonal close-packed crystallographic phase to a body-centered cubic crystallographic phase and then quenching to a second temperature at a rate which initiates transformation to a hexagonal close-packed crystallographic phase having a texture factor f.sub.L =0.28-0.38;  forming each of said heat-treated first and second strips into first and second fuel channel components respectively;  seam welding said first and second fuel channel components to assemble a fuel channel; and  subjecting said fuel channel to thermal sizing by heating to a third temperature less than said second temperature and sufficient to anneal said material and then cooling. 2. The method as defined in claim 1, wherein said first temperature lies in the temperature range of 1800.degree. F. to 2050.degree. F., said first and second strips are held at a temperature in said temperature range for at least 0.25 sec and said second temperature is no more than 1500.degree. F. 3. The method as defined in claim 1, wherein at least one of said heat treatment and thermal sizing steps is carried out in an inert atmosphere or in a vacuum. 4. The method as defined in claim 1, wherein said quenching is performed using an inert gas as the quenching medium. 5. The method as defined in claim 4, wherein said inert gas is helium. 6. The method as defined in claim 1, wherein said quenching is carried out at a rate of 10.degree. F./sec to 400.degree. F./sec. 7. The method as defined in claim 1, wherein said third temperature is in a temperature range of 1000.degree. F. to 1250.degree. F. and said fuel channel is held at a temperature in said temperature range for at least 15 minutes. 8. The method as defined in claim 1, wherein after said heat treatment and before said first and second fuel channel components are formed, said first and second strips are heated to a fourth temperature sufficient to increase the ductility of said strip material, wherein said fourth temperature is less than said third temperature. 9. The method as defined in claim 8, wherein said fourth temperature lies in a temperature range of 50.degree. F. to 800.degree. F. 10. A method for manufacturing a dimensionally stable and corrosion-resistant fuel channel, comprising the steps of: 11. The method as defined in claim 10, wherein said quenching is performed using an inert gas as the quenching medium. 12. The method as defined in claim 10, wherein said quenching is carried out at a rate of 10.degree. F./sec to 400.degree. F./sec. 13. The method as defined in claim 10, wherein said third temperature lies in a temperature range of 50.degree. F. to 800.degree. F. 14. A dimensionally stable and corrosion-resistant fuel channel made of metal alloy having a hexagonal close-packed crystallographic phase which is stable in a first temperature range and a body-centered cubic crystallographic phase which is stable in a second temperature range different than said first temperature range, formed by the steps of: 15. The fuel channel as defined in claim 14, wherein said metal alloy is zirconium-based alloy. 16. The fuel channel as defined in claim 14, wherein said first temperature lies in the temperature range of 1800.degree. F. to 2050.degree. F., said first and second strips are held at a temperature in said temperature range for at least 0.25 sec and said second temperature is no more than 1500.degree. F. 17. The fuel channel as defined in claim 14, wherein said quenching is carried out at a rate of 10.degree. F./sec to 400.degree. F./sec. 18. The fuel channel as defined in claim 14, wherein said third temperature is in a temperature range of 1000.degree. F. to 1250.degree. F. and said fuel channel is held at a temperature in said temperature range for at least 15 minutes. 19. The fuel channel as defined in claim 14, wherein after said heat treatment and before said first and second fuel channel components are formed, said first and second strips are heated to a fourth temperature sufficient to increase the ductility of said strip material, wherein said fourth temperature is less than said third temperature. 20. The fuel channel as defined in claim 19, wherein said fourth temperature lies in a temperature range of 50.degree. F. to 800.degree. F.