Patent Number: 045129398
Section: abstract

Method for the manufacture of oxidic sintered nuclear fuel bodies by compacting UO.sub.2 -starting powder or a mixture of UO.sub.2 -and PuO.sub.2 starting powder which contains up to 10% by weight rare-earth oxide, especially Gd.sub.2 O.sub.3, as an additive into blanks and subsequent densification of these blanks by a heat treatment in a sintering atomsphere with reducing action. The UO.sub.2 -starting powder used for compacting has a specific surface in the range of 2 to 4.5 m.sup.2 /g and/or a mean crystallite diameter in the range of 80 nm to 250 nm, and the heat treatment in the sintering atmosphere with reducing action is carried out at a temperature in the range of 1,500.degree. C. to 1,750.degree. C.