Patent Number: 046701982
Section: claims

1. A method of producing durable coherent compacts of particulate ceramic nuclear fuel which imparts lasting plasticity to the particulate ceramic material, consisting essentially of the steps of: a. providing an aqueous solution of a diamine and adding a source of oxalate ions to said diamine aqueous solution whereby the high pH of the solution due to hydrolysis of the diamine dissolves the source of oxalate ions, then adding said aqueous solution of diamine and dissolved oxalate ions to particulate nuclear fuel material comprising uranium dioxide, and blending the solution containing diamine and oxalate ions therethrough to produce a fugitive binder for said fuel material; and  b. pressing the resultant blend comprising particulate fuel material and diamine with oxalate ions into a coherent compact.  a. providing an aqueous solution of a diamine and adding a source of oxalate ions derived from at least one source selected from the group consisting of oxalic acid and ammonium oxalate to said diamine aqueous solution whereby the high pH of the solution due to hydrolysis of the diamine dissolves the source of oxalate ions, then adding said aqueous solution of diamine and dissolved oxalate ion source to particulate nuclear fuel material comprising uranium dioxide and blending the solution containing diamine and oxalate ions therethrough to produce a fugitive binder for said fuel material; and  b. pressing the resultant blend comprising particulate fuel material and diamine and oxalate ions into a coherent compact.  a. providing an aqueous solution of ethylenediamine and adding a source of oxalate ions to said ethylenediamine aqueous solution whereby the high pH of the solution due to hydrolysis of the ethylenediamine dissolves the source of oxalate ions, then adding said aqueous solution of ethylenediamine and dissolved oxalate ions to particulate nuclear fuel material comprising uranium dioxide and blending the solution containing ethylenediamine and oxalate ions therethrough; and  b. pressing the resultant blend comprising particulate fuel material and ethylenediamine and oxalate ions into a coherent compact.  a. preparing a fugitive binder comprising a combination of a diamine and oxalate ions for particulate nuclear fuel material by providing an admixture of oxalate ions in an aqueous solution of ethylenediamine, in approximate ratios of about one part by weight of the oxalate ions to about two parts by weight of the ethylenediamine dissolved in approximately and equal part by weight of water, and adding said combined ingredients to particulate ceramic nuclear fuel containing uranium dioxide; and  b. blending said added admixture of ingredients with the particulate nuclear fuel containing uranium dioxide at a temperature of greater than 55.degree. C. to interact the ingredient and produce a binder for said particulate nuclear fuel.  a. preparing a fugitive binder for particulate nuclear fuel material by adding ammonium oxalate to an aqueous solution of ethylenediamine and dissolving the ammonium oxalate therein providing oxalate ions, in approximate ratios of about one part by weight of the oxalate ion to about two parts by weight of the ethylenediamine, and adding said combined ingredients of solution of ethylenediamine with oxalate ions to particulate ceramic nuclear fuel containing uranium dioxide;  b. blending said combined ingredients comprising ethylenediamine solution with oxalate ions with the particulate nuclear fuel at a temperature of at least about 55.degree. C. to interact the ethylenediamine and oxalate ions with uranium dioxide and produce a binder for said particulate nuclear fuel; and  c. drying the combined and interacted ingredients and removing water from the combined mass by applying a heated gas the temperature of which is not greater than about 150.degree. C.  a. providing a fugitive binder comprising a uranyl oxalate reaction product of a combination of diamine and oxalate ions admixed with uranium dioxide and having the composition of EQU [.sup.+ NH.sub.3 CH.sub.2 CH.sub.2 NH.sub.3.sup.+ ][.sup.- UO.sub.2 (C.sub.2 O.sub.4).sub.2.(H.sub.2 O).sub.2.sup.- ][.sup.+ NH.sub.3 CH.sub.2 CH.sub.2 NH.sub.3.sup.+ ]  for particulate nuclear fuel material containing uranium dioxide, and blending same; and  b. pressing the resultant blend comprising particulate fuel material and binder into a coherent compact.  a. providing a fugitive binder comprising uranyl oxalate reaction product of a combination of at least one diamine selected from the group consisting of ethylenediamine, propylenediamine and hexamethylenediamine and oxalate ions added to uranium dioxide for particulate nuclear fuel material containing uranium dioxide, and blending same through the particulate nuclear fuel material; and  b. pressing the resultant blend comprising particulate fuel material and the binder reaction product into a coherent compact. 2. The method of claim 1, wherein the aqueous solution of diamine and source of oxalate ions is heated before adding to the particulate nuclear fuel. 3. The method of claim 1, wherein the diamine comprises ethylenediamine. 4. The method of claim 1, wherein the oxalate ions are provided by ammonium oxalate or oxalic acid. 5. A method of producing durable coherent compacts of particulate ceramic nuclear fuel which imparts lasting plasticity to the particulate ceramic material, consisting essentially of the steps of: 6. The method of claim 5, wherein the diamine is selected from the group consisting of ethylenediamine, propylenediamine and hexamethylenediamine. 7. The method of claim 5, wherein the oxalate ions are derived from ammonium oxalate. 8. The method of claim 5, wherein the added fugitive binder forming ingredients comprise the combination of about 30% to about 50% by weight of diamine with about 25% to about 60% by weight of water and about 10% to about 25% by weight of oxalate ions. 9. The method of claim 5, wherein the diamine solution and oxalate ion ingredients for producing the binder are combined and added to the particulate nuclear fuel material in amount of about 2% to about 6% by weight thereof. 10. A method of producing durable coherent compacts of particulate ceramic nuclear fuel which imparts lasting plasticity to the particulate ceramic material for extended processing, consisting essentially of the steps of: 11. The method of claim 10, wherein the ethylenediamine is in aqueous solution and ammonium oxalate powder is added as a powdered solid, and ammonia is removed in situ to form the binder solution without ammonium oxalate precipitation. 12. The method of claim 10, wherein the ethylenediamine is in aqueous solution and ammonium oxalate powder is dispersed in said aqueous solution of ethylenediamine before adding to the particulate nuclear fuel material, and ammonia is removed in situ to form the binder solution and to prevent ammonium oxalate precipitation. 13. The method of claim 10, wherein the added fugitive binder forming ingredients comprises a combination of about 1% to about 3% by weight of ethylenediamine and about 0.5% to about 1.5% by weight of ammonium oxalate based upon the weight of the particulate nuclear fuel material. 14. The method of claim 10, wherein the fugitive binder comprises a combination of about 1.5% of weight of ethylenediamine and about 0.8% by weight of ammonium oxalate based upon the weight of the particulate nuclear fuel material. 15. A method of producing durable coherent compacts of particulate ceramic nuclear fuel which imparts lasting plasticity to the particulate ceramic material for extending processing, consisting essentially of the steps of: 16. The method of claim 15, wherein the blend of particulate nuclear fuel material comprising uranium dioxide and admixture of oxalate ions in an aqueous solution of ethylenediamine is compressed into a coherent compact. 17. A compression moldable particulate mixture containing particulate ceramic nuclear fuel material, consisting essentially of the combination of particulate ceramic nuclear fuel material including uranium dioxide and a fugitive binder forming admixture of oxalate ions dissolved in a diamine aqueous solution with the ceramic nuclear fuel material containing uranium dioxide. 18. The compression moldable particulate mixture of claim 17, which has been compressed into coherent compacts. 19. The compression moldable particulate mixture of claim 17, wherein the diamine is selected from at least one diamine from the group consisting of ethylenediamine, propylenediamine, and hexamethylenediamine. 20. A compression moldable particulate mixture containing particulate ceramic nuclear fuel material, consisting essentially of the combination of particulate ceramic nuclear fuel material including uranium dioxide and a fugitive binder forming admixture of oxalate ions dissolved in an ethylenediamine aqueous solution with the uranium dioxide. 21. The compression moldable particulate material of claim 20, wherein the fugitive binder forming ingredients of the admixture comprise about 0.2% to about 0.5% by weight of oxalate ions with about 0.8% to about 3% by weight of ethylenediamine, based upon the weight of the particulate ceramic nuclear fuel material. 22. A method of producing durable coherent compacts of particulate ceramic nuclear fuel which imparts lasting plasticity to the particulate ceramic material for extending processing, consisting essentially of the steps of: 23. A method of producing coherent compacts of particulate ceramic nuclear fuel which imparts lasting plasticity to the particulate ceramic material for extended processing, consisting essentially of the steps of: 24. The method of claim 23, wherein the uranyl oxalate reaction product of EQU [.sup.+ NH.sub.3 CH.sub.2 CH.sub.2 NH.sub.3.sup.+ ][.sup.- UO.sub.2 (C.sub.2 O.sub.4).sub.2.(H.sub.2 O).sub.2.sup.- ][.sup.+ NH.sub.3 CH.sub.2 CH.sub.2 NH.sub.3.sup.+ ] 25. The method of claim 23, wherein the uranyl oxalate reaction product of EQU [.sup.+ NH.sub.3 CH.sub.2 CH.sub.2 NH.sub.3.sup.+ ][.sup.- UO.sub.2 (C.sub.2 O.sub.4).sub.2.(H.sub.2 O).sub.2.sup.- ][.sup.+ NH.sub.3 CH.sub.2 CH.sub.2 NH.sub.3.sup.+ ] 26. A method of producing coherent compacts of particulate ceramic nuclear fuel which imparts lasting plasticity to the particulate ceramic material for extended processing, consisting essentially of the steps of: 27. The method of claim 26, wherein the uranyl oxalate reaction product is prepared by combining the diamine in a water solution and oxalate ions in proportions by weight of about 30% to about 50% diamine, in about 25% to about 50% water with about 10% to about 25% oxalate ions. 28. The method of claim 26, wherein the combined solution of the diamine and oxalate ions is added to the particulate nuclear fuel material containing uranium dioxide in amount of about 2% to about 4% by weight of the fuel material. 29. The method in claim 26, wherein the diamine is ethylenediamine in aqueous solution.