Patent Number: 051184680
Section: claims

1. A method for forming a metal, neutron absorbing element for control of a nuclear reactor, comprising the steps of: a) preparing a compactable metal product consisting essentially of, by weight:  b) introducing said compactable metal product into a substantially neutron non-absorbing metal container through an open end;  c) before said introducing step, compacting said metal product outside of said container, and/or  during and/or after said introducing step, compacting said metal product in said container through said open end,  said metal product being compacted to a density of at least 80% of its mean, solid state density with said container being at least 95% full; and  d) placing said compacted metal product under a vacuum better than 1.3 Pa, and sealing said open end by welding a metal lid or plug thereto. 2. The method of claim 1, wherein the hafnium used comprises electrolytic crystals representing at least 25% of the total weight of products, the crystals having a hydrogen and a chlorine content respectively less than 40 ppm and 50 ppm. 3. The method of claim 2, wherein the products used comprise electrolytic crystals of Zr and/or Ti, with a hydrogen and a chlorine content respectively less than 40 ppm and 50 ppm. 4. The method of claim 1 wherein the products used comprise electrolytic crystals of Zr and/or Ti, with a hydrogen and a chlorine content respectively less than 40 ppm and 50 ppm. 5. The method of claim 4, wherein the electrolytic crystals used have a mean hydrogen and chlorine content respectively less than 25 and 30 ppm. 6. The method of claim 2, wherein the electrolytic crystals used have a mean hydrogen and chlorine content respectively less than 25 and 30 ppm. 7. The method of claim 6, wherein the electrolytic crystals used have been treated previously at from 150.degree. to 300.degree. C., under vacuum or in an inert gas. 8. The method of claim 4, wherein the electrolytic crystals used have been treated previously, for 8 to 48 hours at from 1000.degree. to 1250.degree. C. 9. The method of claim 8, wherein the electrolytic crystals have been treated previously, for 16 to 32 hours at from 1050.degree. to 1150.degree. C. 10. The method of any of claims 1, 2, 4 or 6-8, wherein the compactable products are mixed before being compressed and/or placed in the metal container, so that the variations in the weight of Hf per unit length or per unit useful surface area obtained along the sealed container or element are less than 2 relative percent. 11. The method of claim 10, wherein the metal container and its lid are made of stainless steel. 12. The method of claim 10, wherein the element or filled container is expanded or shaped by cold forming or forming at below 260.degree. C. 13. The method of any of claims 1, 2, 4 or 6-8, wherein discrete variations in the Hf content along the sealed container or element are produced, by preparing pellets from batches of compactable products with a different Hf content before placing them in the container. 14. The method of claim 13, wherein the metal container and its lid are made of stainless steel. 15. The method of claim 13, wherein the element or filled container is expanded or shaped by cold forming or forming at below 260.degree. C. 16. The method of any of claims 1, 2, 4 or 6-8, wherein continuous variation of the Hf density along a container is produced, by inserting Hf and/or alloy containing Hf in the container in one or more stages, in quantities increasing continuously from one end of the container to the other, while simultaneously inserting a decreasing quantity of metal or alloy containing no Hf or less Hf, and by compressing them after each inserting sequence or at the end of the operation before sealing the end of the container. 17. The method of claim 16, wherein the metal container and its lid are made of stainless steel. 18. The method of claim 16, wherein the element or filled container is expanded or shaped by cold forming or forming at below 260.degree. C. 19. The method of any of claims 1, 2, 4 or 6-8 wherein the metal container and its lid are made of stainless steel. 20. The method of claim 19, wherein said stainless steel is AISI 316L. 21. The method of any of claims 1, 2, 4 or 6-8 wherein the element or filled container is expanded or shaped by cold forming or forming at below 260.degree. C.