Patent Number: 059466391
Section: claims

1. A method for treating cutting swarf, said method comprising: collecting swarf in a vessel; said vessel having a top and a bottom;  compressing said swarf in said vessel;  injecting a binder mixture comprising vinyl ester styrene into the bottom of said vessel to fill void volume while maintaining said vessel and said swarf submerged under water; wherein said injecting, and said compressing of said swarf, provides an even flow of said binder mixture upward through said swarf to fill said void volume;  forming a mixture comprising said swarf and said vinyl ester styrene and maintaining said mixture under water; and  curing said mixture into a solid matrix. 2. The method for treating swarf of claim 1, comprising preparing said solid matrix for storage. 3. The method for treating swarf of claim 1, wherein said swarf comprises a metal selected from a group consisting of zirconium, magnesium, and thorium. 4. The method for treating swarf of claim 3, wherein said swarf comprises zirconium. 5. The method for treating swarf of claim 1, wherein said swarf is radioactive. 6. The method for treating swarf of claim 4, wherein said swarf comprises radioactive zirconium generated during operations to prepare spent nuclear fuel for storage. 7. The method for treating swarf of claim 1, wherein said binder mixture comprising said vinyl ester styrene, further comprises a catalyst, and a promotor. 8. The method for treating swarf of claim 7, wherein said binder mixture further comprises a temperature suppressant. 9. The method for treating swarf of claim 1, comprising solidifying said swarf in layers in said vessel. 10. The method for treating swarf of claim 9, wherein said vessel for solidifying said swarf comprises a mold comprising a liner. 11. The method for treating swarf of claim 10, wherein said mold comprises pre-installed distribution laterals for distributing said vinyl ester styrene. 12. The method for treating swarf of claim 11, wherein said mold is made of vinyl ester fiberglass. 13. The method for treating swarf of claim 1, comprising loading said swarf underwater into said vessel, wherein said vessel comprises a bottom orifice plate and a top orifice plate. 14. The method for treating swarf of claim 13, comprising formulating said binder mixture in a pouring bucket. 15. The method for treating swarf of claim 14, comprising placing a lid on said pouring bucket and rotating said pouring bucket to a substantially horizontal position to start flow of the binding mixture into said vessel. 16. The method of claim 13, wherein said swarf is compressed by moving said top orifice plate. 17. The method for treating swarf of claim 1, wherein said curing comprises an exothermic reaction at an exotherm temperature within a range of about 140.degree. F. to about 210.degree. F. 18. The method for treating swarf of claim 17, wherein said water is at a temperature within a range of about 55.degree. F. and to about 85.degree. F. 19. The method for treating swarf of claim 1, wherein said binder mixture is cooled to a temperature below room temperature before injecting it into said vessel containing said swarf. 20. The method for treating swarf of claim 19 wherein said binder is at a temperature of about 55.degree. F. 21. The method for treating swarf of claim 1 wherein said swarf exhibits an ignitable hazard, and wherein said method stabilizes the ignitable hazard to produce a waste form of said swarf acceptable for land disposal.