Patent Number: 
Section: claims

1. A composition to immobilize nuclear containing waste containing at least one radioactive element or alloy of uranium, graphite, magnesium, and aluminum, said composition comprising:at least one mineral phase forming element or compound that reacts with said at least one radioactive element or alloy; andat least one glass-forming element or compound to form a glass phase that incorporates waste radioisotopes and impurities that do not react with said least one mineral phase forming element or compound,wherein the composition immobilizes said nuclear containing waste in a solid wasteform,wherein the nuclear containing waste comprises a magnesium metal, carbonate or hydroxide, and the mineral phase is sufficient to convert the magnesium metal, carbonate or hydroxide to MgO, and/or the nuclear containing waste comprises a uranium metal and/or hydrated and carbonated uranium, and the mineral phase is sufficient to convert the uranium oxide. 2. The composition of claim 1, wherein nuclear containing waste comprises magnox sludges, clinoptilolite wastes, and combinations thereof. 3. The composition of claim 1, wherein the final wasteform has a density of greater than 90% theoretical density. 4. The composition of claim 1, wherein the magnesium has a magnesium-derived component with a particle size <250 μm. 5. The composition of claim 1, further comprising at least one additive to assist in the thermal treatment and consolidation of the final wasteform. 6. The composition of claim 5, wherein the at least one additive comprises a source of Ti, Si, P or Al, that react with the magnesium component to form stable phases. 7. The composition of claim 6, wherein the sources of Ti, Si, P or Al include titania, titanate minerals, alumina, phosphate silica, silicate minerals, silica sol and glass frit. 8. The composition of claim 6, wherein the stable phases comprise MgTiO3, Mg2TiO4, MgTi2O5, MgSiO3, Mg2SiO4, MgAl2O4, and combinations thereof. 9. The composition of claim 6, further comprising ternary multicomponent phases from other elements in the waste. 10. The composition of claim 9, wherein the ternary multicomponent phases comprise diopside (CaMgSi2O6) and perovskite (CaTiO3). 11. The composition of claim 1, wherein the wasteform comprises a mixture of MgO and other ceramic phases encapsulated in a protective glass plus ceramic phase matrix. 12. The composition of claim 1, wherein the wasteform comprises a uranium oxide or a compound selected from a titanate mineral: brannerite, pyrochlore, zirconolite encapsulated in a matrix. 13. The composition of claim 1, wherein the nuclear containing waste contains both coarse fraction and fine fractions of particulates in a ratio ranging from 10:90 to 90:10. 14. The composition of claim 13, wherein a majority of the coarse fractions have particulate sizes ranging from 200 μm to 6 mm and a majority of the fine fractions have particulate sizes ranging from 0.1 to less than 200 μm. 15. A method of treating nuclear containing waste, said method comprising:forming a slurry comprising nuclear containing waste containing a magnesium metal, carbonate or hydroxide and a composition comprising at least one mineral phase forming element or compound and at least one glass-forming element or compound, wherein the mineral phase is sufficient to convert the magnesium metal, carbonate or hydroxide to MgO, and/or the nuclear containing waste comprises a uranium metal and/or hydrated and carbonated uranium, and the mineral phase is sufficient to convert the uranium oxide;drying said slurry to form a dried product;calcining the dried product to form a calcined product;loading the calcined product into a canister;evacuating and sealing the metal canister; andthermally treating the calcined product in the canister to produce a dense wasteform product, which comprises a glass-ceramic. 16. The method of claim 15, further comprising mixing said slurry using at least one paddle type mixing, recirculating mixing, in-line mixing, turbulent slurry mixing or a combination thereof. 17. The method of claim 15, wherein drying the slurry is performed concurrently with a step that granulates the resulting product, said drying comprises at least one process selected from wipe or thin-film evaporation, rotary drying or conical mixer drying, spray drying, fluidized bed drying or flash drying. 18. The method of claim 15, wherein hot-isostatic pressing occurs at temperatures ranging from 900° C. and 1300° C. and pressures ranging from 5 MPa to 150 MPa. 19. The method of claim 15, wherein calcining occurs using a rotary calcination, vibratory calcination, fluidized bed calcination or a batch calcination method. 20. The method of claim 15, wherein calcining removes hydrogen and/or reactive water from the wasteform. 21. The method of claim 15, further comprising thermal processing to densify the product to greater than 90% theoretical density. 22. The method of claim 15, further comprising reacting a magnesium-derived component having a particle size less than 250 μm with at least one additive to assist in the thermal treatment and consolidation of the dense waste form product. 23. The method of claim 21, wherein said reacting comprises the intermixing of fine components of the waste with fine additives that provide sources of Ti, Si, P or Al, to form at least one stable phase. 24. The method of claim 23, wherein the sources of Ti, Si, P or Al include titania, alumina, phosphate silica, and glass frit. 25. The method of claim 23, wherein the at least one stable phase comprises MgTiO3, Mg2TiO4, MgTi2O5, MgSiO3, Mg2SiO4, MgAl2O4, and combinations thereof. 26. The method of claim 23, further comprising ternary multicomponent phases from other elements in the waste. 27. The method of claim 26, wherein the ternary multicomponent phases comprise diopside (CaMgSi2O6), perovskite (CaTiO3) and mixtures thereof. 28. The method of claim 15, wherein the dense wasteform product comprises a mixture of MgO and at least one other ceramic phase encapsulated in a protective glass plus ceramic phase matrix. 29. The method of claim 15, wherein the dense wasteform product comprises a uranium oxide and at least compound selected from a titanate mineral brannerite, pyrochlore, zirconolite encapsulated in a matrix. 30. The method of claim 15, wherein the at least one glass-forming element or compound comprises a zeolite. 31. The method of claim 30, wherein the zeolite comprises clinoptilolite, which is found in an amount to adsorb the volatile elements and isotopes thereof, to form a glass during processing that contains radioactive ions present in the waste, or both, such that their loss rate during thermal processing is reduced. 32. The method of claim 30, wherein the volatile elements and isotopes thereof comprise Cs. 33. The method of claim 30, wherein the zeolite reacts to form a glass during processing that contains radioactive ions present in the waste. 34. The method of claim 15, further comprising vibratory packing the calcined material prior to thermally treating. 35. The method of claim 34, wherein the canister is made of a metal, and thermally treating the metal material canister comprises hot isostatic pressing. 36. The method of claim 15, further comprising granulating the dried product.