Patent Document

FIELD OF THE INVENTION  
         [0001]    The field of the invention is integrated circuit packaging and mounting.  
         BACKGROUND OF THE INVENTION  
         [0002]    The use of underfill compositions for mounting integrated circuit (IC) devices supporting surfaces such as printed wiring boards “PWBs” to obtain improved thermal and dimensional performance properties are known. An example of such can be found in U.S. Pat. No. 5,654,081, titled Integrated Circuit Assembly with Polymeric Underfill Body, which discusses the use of particular underfill compositions in mounting flip-chip IC devices to circuit boards.  
           [0003]    Underfill compositions can be positioned between the IC and the surface (hereinafter PWB for simplicity) to which it is to be mounted either before or after electrical/metallurgical connections between the IC and PWB are made. If it is to be done after electrical connections are formed, an underfill material can be injected from the sides of gap between the IC and PWB, or through a hole in the PWB located beneath the IC. However, such injection methods tend to be problematic in regard to the time required to inject the underfill, and the difficulty in assuring a complete, uniform distribution of underfill material.  
           [0004]    If it is to be accomplished prior to formation of the electrical connections, the underfill can either be “built-up” on (i.e. printed onto) either the IC or PWB, or provided as a pre-form which is sandwiched between the IC and PWB. Patents referencing the build up process include both U.S. Pat. No. 5,654,081 previously discussed and U.S. Pat. No. 5,936,847 titled Low Profile Electronic Circuit Modules. Printing material onto the IC or the PWB is not always desirable as it tends to overly complicate the handling process and cannot be done in parallel with formation of the ICs and PWBs.  
           [0005]    A patent which utilizes a conductorless pre-form is U.S. Pat. No. 6,040,630 titled Integrated Circuit Package for Flip Chip with Alignment Preform Feature and Method of Forming Same. Unfortunately, conductorless preforms require the use of pads or other conductors on the IC and/or PWB which can extend through the preform.  
           [0006]    A pre-from comprising a filled perforated dielectric structure wherein the dielectric comprises a coated polyimide film and the fill material comprises a transient liquid phase sintered material is utilized in U.S. Pat. No. 5,948,533 titled Vertically Interconnected Electronic Assemblies and Compositions Useful Therefor. However, the use of coated polyimide films is not desirable in all circumstances.  
           [0007]    Thus, there is a need for improved methods and devices for underfilling an IC mounted to a supporting surface such as a PWB.  
         SUMMARY OF THE INVENTION  
         [0008]    The present invention is directed to methods and apparatus in which an assembly comprising a thermosetting layer pierced by a plurality of conductors is formed on a release sheet and subsequently sandwiched between an IC and a PWB or other supporting surface and subsequently cured. The release sheet is removed either before or during curing of the thermosetting material. Removal prior to curing may be accomplished via peeling. Removal during curing may be by destruction of the layer by the curing process.  
           [0009]    Various objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of preferred embodiments of the invention, along with the accompanying drawings in which like numerals represent like components. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0010]    [0010]FIG. 1 is a perspective top view of a compliant pre-form interconnect embodying the invention.  
         [0011]    [0011]FIG. 2 is a cutaway view of a compliant pre-form interconnect embodying the invention.  
         [0012]    [0012]FIG. 3 is a cutaway view of the interconnect of a compliant pre-form interconnect embodying the invention coupling an integrated circuit to a printed wiring board.  
     
    
     DETAILED DESCRIPTION  
       [0013]    In FIG. 1- 3 , a preferred pre-form assembly  10  comprises a base layer assembly  100 , a sacrificial layer assembly  200 , and through conductors  300 .  
         [0014]    Base layer assembly preferably  100  comprises a single B-staged thermosetting material. Although a thermoplastic material may be used, it is contemplated that a thermosetting material provides additional strength and stability. Preferred B-staged thermosetting materials include but are not necessarily limited to cyanate esters, cycloaliphatic epoxies, bismaleimides, cyanate ester/epoxy copolymers, cyanate ester/bismaleimide copolymers or blends and cycloaliphatic epoxy/bismaleimide copolymers or blends. Although preferably formed from a single layer, it is contemplated that base layer assembly  100  may be a multi-layer assembly.  
         [0015]    Sacrificial assembly  200  comprises sacrificial layer  210  and release coating  220 . Sacrificial layer  210  is preferably formed from a relatively cheap material such as a polyester or a celluloid film. Release coating  220  preferably is located between the sacrificial layer  210  and base layer assembly  100 , and comprises standard silicon, Teflon® or graphite release agents such as commercially available materials which are available from Chemlease™ and Buehler™. An example of such a commercially available material is POL-ESE 233™. In other embodiments, the sacrificial layer assembly  200  may not include release coating  220 , particularly if using materials with low natural surface energy and low adhesion to other materials, such as Teflon® and oriented polyimide. In a less-preferred embodiment, the sacrificial layer is not removed but becomes part of the final structure. It is contemplated that in many embodiments, traces of the release coating  220  will remain after removal of sacrificial layer  100 .  
         [0016]    The use of release coating  220  in conjunction with a cheap sacrificial layer  210  which comprises a polyester or celluloid film is anticipated to provide numerous advantages over any existing protective covering methods and devices such as lowering the cost of sacrificial assembly  200 , making it easier to utilize assembly  10 , and increasing the flexibility of assembly  10 .  
         [0017]    Through conductors  300  may be formed by, among other methods, stitching/piercing wire through base layer assembly  100  or forming conductive vias in base layer assembly  100 . Through conductors  300  may or may not punch through the sacrificial layer assembly  200  with the choice of whether to have the conductors  300  punch through being at least partially dependent on the method of manufacturing used and the type of object (i.e. a pad, a solder ball, a stud, or some other type) the through connector will ultimately be electrically coupled to. Thus, wire piercing may be the choice for use to connect to a pad or via on a package or board, but a via may be a better choice if connecting to a stud or ball. It is preferred that the choice of type of through conductor and whether it penetrates the sacrificial layer assembly  200  be made so as to accommodate a variety of configurations and manufacturing methods. FIG. 2 provides examples of both vias ( 301  and  302 ) and wires ( 303 ) and examples of a through conductor piercing the entire interconnect ( 301 ), piercing the base layer assembly  100  and release coating  220  ( 302 ), and piercing only the base layer  100  ( 303 ).  
         [0018]    If conductive vias are used, it is contemplated that such vias will comprise a solder paste rather than a transient liquid phase sintered material. Preferred solder pastes include PbSn, PbSnAg, Indium alloys, and Au eutectic/alloys, if wire piercing/thermosonic ball formation is used..  
         [0019]    It is contemplated that extending the through conductors  300  into the sacrificial layer assembly  200  may provide additional mechanical stability for a corresponding alignment stability.  
         [0020]    A preferred method of forming pre-form assembly  10  comprises: providing sacrificial layer  210 , coating sacrificial later  210  with release coating  220 , applying a thermosetting material  100  on top of release coating  220 ; curing the thermosetting material  100  to form a B-stage layer; inserting through conductors  300  into thermosetting material  100 . Insertion of through conductors  300  preferably comprises either piercing wires  300  into the thermosetting material, or lasing or drilling and subsequently filling holes in thermosetting material  100 . The lased vias may be processed by “off-set” lasing to provide a larger bottom diameter footprint, to lessen registration to contact point difficulty. A preferred method of using pre-form assembly  10  comprises: providing an IC; providing a supporting surface to which the IC is to be mechanically and electrically bonded; providing pre-form assembly  10 ; applying pre-form assembly  10  to either the IC or supporting surface; peeling away sacrificial layer  210 ; sandwiching pre-form assembly  10  between the IC and the supporting surface; and curing the base layer assembly of pre-form assembly  10 .  
         [0021]    A mechanical support structure may be included during the construction of the thermosetting layer  100 . In one embodiment thermosetting layer  100  includes a fiber mesh material which consists of but is not limited to glass, graphite, KEVLAR®, TEFLON®, or polyester into which the thermoset of layer  100  is impregnated. For additional mechanical support the thermoset may also be formulated with particulate fillers. Such fillers include but are not limited to: alumina, silica, graphite fibers, graphite particles, silicon nitride, silicon carbide, aluminum nitride, diamond, berylium, and conductive polymer filler.  
         [0022]    If a thermal enhancement is required, the preform may include construction using a thermally conductive material. The preferred embodiment would use a non-electrically conductive filler into the thermosetting material  100 . Such fillers include but are not limited to silicon nitride, silicon carbide, aluminum nitride, boron nitride, diamond, conductive polymer filler, graphite and alumina. In another embodiment a thermally conductive mesh material may be used in conjunction with the construction of the thermoset layer  100 . In this example, a thermally conductive graphite mesh would be impregnated with the thermoset material and become part of layer  100 . The thermoset material may or may not include formulation with the conductive filler. In a less preferred embodiment a physical thermal layer  102  would be added to the construction of the preform. For example a copper plane or a phase change film  102  could be added as a center layer between thermoset layers  101  and  103 . The thermoset material used may or may not include formulation with the conductive filler, dependent upon the thermal construction desired.  
         [0023]    Thus, specific embodiments and applications of compliant preform interconnects have been disclosed. It should be apparent, however, to those skilled in the art that many more modifications besides those already described are possible without departing from the inventive concepts herein. The inventive subject matter, therefore, is not to be restricted except in the spirit of the appended claims. Moreover, in interpreting both the specification and the claims, all terms should be interpreted in the broadest possible manner consistent with the context. In particular, the terms “comprises” and “comprising” should be interpreted as referring to elements, components, or steps in a non-exclusive manner, indicating that the referenced elements, components, or steps may be present, or utilized, or combined with other elements, components, or steps that are not expressly referenced.

Technology Category: 4