Patent Document

CROSS REFERENCE TO RELATED APPLICATIONS 
     This application is a divisional of U.S. patent application bearing Ser. No. 13/317,564 with filing date of Oct. 20, 2011 now U.S. Pat. No. 8,709,956, which is hereby incorporated by reference and which is a Continuation-In-Part of U.S. patent application bearing Ser. No. 13/136,454 with filing date of Aug. 1, 2011 now U.S. Pat. No. 8,796,795, which is also hereby incorporated by reference. 
    
    
     FIELD OF THE INVENTION 
     The present invention relates generally to semiconductor Back-End-Of-Line (BEOL) memories and particularly to Magnetic Random Access Memory (MRAM) and particularly to protecting the memory elements from being shorted during the interconnect process. 
     DESCRIPTION OF THE PRIOR ART 
     The BEOL memories such as RRAM (Resistive Random Access Memory), PRAM (Phase Change Random Access Memory), MRAM have a resistive device as a memory element. Because high speed access and non-volatility at power off are promised by these devices, they may replace existing memories and create new markets. 
     The memory device consists of a top electrode, a bottom electrode and the resistive memory element in between. The bottom electrode is connected to a control device such as a transistor or a diode. After the layers of the memory device have been patterned, the top electrode is connected to a bit line in a series of process steps collectively referred to as BEOL process which creates metal interconnect wires that are insulated by dielectric material. Herein arises a problem with the prior art that can result in an electrical short being formed between the top and bottom electrodes during fabrication. The design trend for the resistive device is to scale down minimum feature size to minimize the cell area. The BEOL feature size is generally larger than the minimum feature size defined in FEOL (Front End Of Line) process. Therefore, when using a via hole to interconnect the resistive device to the bit line, there is no margin for the bit line to land on the top electrode. The sidewall of the memory element would be exposed by the via etch process. If the etching of the via reaches to the sidewall of the bottom electrode, then the subsequent metal deposition in the bit line interconnect process causes a short between the top electrode to the bottom electrode, thereby destroying the functionality of the device. This failure condition that can arise during prior art processing is illustrated  FIG. 1 . 
     The resistive device of MRAM is a MTJ (Magnetic Tunnel Junction) including a free layer, a fixed layer and a barrier layer in between. A magnetic moment of the free layer is manipulated to parallel or antiparallel to the fixed layer by applying an electric current. Whether the magnetic vector of the free layer is parallel or antiparallel to the fixed layer determines the low or high resistance state of the MTJ. The two resistance states are defined as memory state “ 0 ” or “ 1 ”. Therefore, an electrical short that could happen when the via etch reaches down to the level of the barrier layer is a severe issue in this device. 
     In published US patent application 20100181654 by Fujiwara, et al. (Jul. 22, 2010) an insulating film, which will be called a borazinic film herein, for a semiconductor device is described. The film is described as having low permittivity, a low leak current, high mechanical strength, stability over time, and excellent water resistance. The process for forming the film uses a carrier gas and a raw material gas, which has borazine skeletal molecules. The insulating film includes cross-linked borazine skeletal molecules and is said to have both inorganic or organic properties. 
     SUMMARY OF THE INVENTION 
     Embodiments of the invention include one or more protection layers deposited on the sidewall of the memory device (including, for example, an MTJ element) prior to interconnect via etching to protect the sidewall during the via etching and prevent the formation of electrical shorts between the top and bottom electrodes. The invention is applicable to MRAM and other BEOL memories. Embodiments of the invention disclose a MTJ MRAM memory cell having one or more sidewall protection layers on a memory device sidewall and the fabrication method thereof. Two embodiments are described. 
     The first embodiment uses a single layer sidewall protection sleeve that is deposited after the memory device has been patterned. The bulk material for the protection sleeve layer is deposited and then vertically etched down to expose the upper surface of the top electrode while leaving a residual layer of protective material surrounding the rest of the memory device. The material for the protection sleeve layer is selected to resist the etchant used to remove the dielectric material from the via in the subsequent interconnect process. The interconnect process can be performed in the conventional manner. 
     The second embodiment uses dual-layer sidewall protection sleeve (or equivalently dual sleeves) in which the first layer covers the sidewalls of the memory element and the bottom electrode and the second layer protects the first layer during the via etch process. The first layer of the sidewall protection sleeve is formed in the same manner as described for the single layer in the first embodiment. However, the material for the first layer in this second embodiment is preferably an oxygen-free dielectric and does not need to be resistant to the etchants used during the interconnect process. After the first sidewall protection layer is vertically etched to expose the upper surface of the top electrode, the bulk material for the second layer of the sidewall protection sleeve is deposited over the device(s) on the wafer, then it is vertically etched to again expose the upper surface of the top electrode while leaving residual material on the sidewall. The material for the second protection layer is selected to resist the etchant used to remove the etch-stop dielectric material from the via in the subsequent interconnect process. The interconnect process can be performed in the conventional manner. 
     In either the first or second embodiments a single layer or a dual layer etch stop layer structure can be deposited over the wafer after the sidewall protection sleeve has been formed and before the inter-layer dielectric (ILD) is deposited. An advantage of the alternative embodiment with the dual layer etch stop layer structure is that it helps address the problem of thickness variations of ILD after CMP planarization across a wafer and between wafers. The material for the top etch stop layer is selected to have high selectivity during etching of the ILD so that the etching depth reliably stops in the top etch stop layer even when the ILD is thinner than average. 
    
    
     
       BRIEF DESCRIPTION OF THE FIGURES 
         FIG. 1  illustrates a failure condition that can arise during prior art processing of a memory device where the etching of the interconnect via hole has exposed the bottom electrode resulting in a short between the top and bottom electrodes when the metal for the bit line interconnect is deposited. 
         FIG. 2  illustrates a cross sectional view, perpendicular to the substrate surface, of a completed memory cell according to a first embodiment of the invention with a single layer sidewall protection sleeve. 
         FIGS. 3 ,  4 A,  4 B,  5 A and  5 B illustrate cross sectional views of selected stages of the fabrication process for a memory cell according to the first embodiment of the invention. 
         FIG. 6  illustrates a cross sectional view of a completed memory cell according to a second embodiment of the invention with a dual-layer sidewall protection sleeve. 
         FIGS. 7 and 8  illustrate cross sectional views of selected stages of the fabrication process for a memory cell according to the second embodiment of the invention with a dual-layer sidewall protection sleeve. 
         FIG. 9  illustrates a cross sectional view of a selected stage of the fabrication process for a memory cell according to an alternative embodiment of the second embodiment of the invention with a dual-layer sidewall protection sleeve and dual layer etch stop layer structure. 
         FIG. 10  illustrates a cross sectional view of a selected stage of the fabrication process for a memory cell according to an alternative embodiment of the first embodiment of the invention with a single layer sidewall protection sleeve and dual layer etch stop layer structure. 
         FIG. 11  illustrates a cross sectional view of a completed memory cell according to the alternative embodiment of the first embodiment of the invention with a single layer sidewall protection sleeve and a dual layer etch stop layer structure. 
         FIG. 12  illustrates a cross sectional view of a completed memory cell according to the alternative embodiment of the second embodiment of the invention with a dual-layer sidewall protection sleeve and a dual layer etch stop layer structure. 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     In the following description of the embodiments, reference is made to the accompanying drawings that form a part hereof, and in which is shown by way of illustration of specific embodiments in which the invention may be practiced. It is to be understood that other embodiments may be utilized without departing from the scope of the present invention. It should be noted that the figures discussed herein are not drawn to scale and thicknesses of lines are not indicative of actual sizes. The cross section view in the figures is generally taken through the approximate center the memory cell in a plane perpendicular to the substrate except where otherwise noted. Although only one cell is shown in the figures, the method may used for the simultaneous fabrication of a many cells on a wafer according to standard techniques. 
       FIG. 2  illustrates a cross sectional view of a completed memory cell according to a first embodiment of the invention wherein the sidewalls of the memory element and bottom electrode are covered by sidewall protection sleeve  200 . The material for sidewall protection sleeve  200  is selected to have a relative low etch rate in the etching gas ambient for dielectric material of etch stop layer  210  and is selected to be, for example, aluminum oxide, a borazinic film, silicon nitride, nitrogen-doped silicon carbide. A low dielectric constant borazinic film suitable for general MRAM applications can be deposited by a chemical vapor deposition (CVD) system such as the MAPLE (Multi Application PLasma Equipment) CVD system of Mitsubishi Heavy Industries. 
     The sidewall protection layer  200  conforms to the shape of the patterned memory device and in this embodiment is an open-topped elliptical cone shape. After describing the completed device, the process of fabricating the device will be described and illustrated. 
     The memory device includes a top electrode  120 , a bottom electrode  100  and an MTJ element formed by fixed ferromagnetic layer  112 , free ferromagnetic layer  116  and barrier layer  114 . Multi-layer structures can be substituted for single free and fixed layers in the MTJ as is known in the art. The bottom electrode can be connected to a control device like a transistor or diode (not shown) in the standard manner. The top electrode is electrically connected by metal bit line interconnect  300 , which is typically copper. The via area of the bit line interconnect  300  around the centrally located memory device is formed by etching away the dielectric etch stop layer  210  down below the plane of the upper surface of the top electrode, then refilling with metal as part of the interconnect process. Because the sidewall protection sleeve  200  extends the entire distance from the lower edge of the bottom electrode up onto the sides of the top electrode, the etching depth for the interconnect via in the dielectric etch stop layer  210  is less critical than in prior art designs. As long as the via exposes the upper surface of the top electrode, the depth of the via below the plane of the upper surface is not critical. The via could be etched all the way down the bottom electrode without causing a short failure. The invention, therefore, allows for higher yields even with inevitable variations in the etching depth during fabrication. The etch depth for the via in  FIG. 2  is shown at approximately the midpoint of the vertical height of the layer stack for the memory device as an example and variations in the depth are to be expected. 
     The dielectric layer  220  is an inter-layer dielectric (ILD). ILD layer  220  is preferably silicon oxide, which works well for CMP planarization. An etch-stop layer  210  under ILD  220  works as an etch-stop layer during etching of the ILD  220 . The dielectric material for etch stop layer  210  is selected to have a relatively slow etching rate in the etching ambient gas used for layer  220  etching. A dielectric material is selected for the protection sleeve  200  to be resistant during etching of layer  210 . Therefore, the protection sleeve  200  should be a different material than layer  210 . In embodiments a material such as aluminum oxide or a borazinic film is selected for the sidewall protection sleeve  200 , because it has slow etching rate in the typical ambient gas for layer  210  etching. The sidewalls of the memory element and the bottom electrode are covered by sidewall protection sleeve  200 , but the upper surface of the top electrode is left exposed to the bit line interconnect  300 . The sidewall protection sleeve  200  as shown extends almost to the plane of the upper surface of the top electrode and, therefore, covers most of the sidewall of the top electrode. 
     The cross section view in  FIG. 2  and the other figures is taken through the approximate center the memory cell in a plane perpendicular to the substrate. In a plan view (not shown) parallel to the substrate surface the top electrode  120  and the other layers in the MTJ are generally elliptically shaped and, therefore, the sidewall protection sleeve  200 , which conforms to the shape of the MTJ will typically be an elliptically shaped concentric band. However, the shape of the MTJ is not critical for any of the embodiments of the invention, because the sidewall protection sleeve will conform to whatever shape the MTJ has. Thus, the sidewall protection sleeve  200  is a generally a sleeve or ring of material that encircles the sidewalls of the layers of the memory element and the bottom electrode, separates these layers from contact with the surrounding metal material of bit line interconnect  300 , and thereby electrically insulates the sidewalls of these layers. 
     The process of fabricating a memory cell according to the first embodiment invention will be described starting with  FIG. 3 . A vertical cross sectional illustration after patterning the memory element stack is shown in  FIG. 3 . The bottom electrode layer  100 , MTJ layer stack  112 ,  114 ,  116  and the top electrode layer  120  are deposited in sequence. The film stack is then patterned using conventional photolithography and vertical etching. 
     Next a layer  200 ′ is deposited over the film stack as shown in  FIG. 4A . This layer provides the bulk material for the sidewall protection structures  200  after controlled etching. The layer  200 ′ is vertically etched until the top electrode  120  is exposed, which leaves residual material on the sidewalls as shown in  FIG. 4B  forming the sidewall protection sleeve  200 . The exposed upper surface of top electrode  120  will be connected to the bit line in later process steps. 
     As shown in  FIG. 5A , etch stop layer  210  is then deposited over the patterned film stack. Next the ILD oxide layer  220  is deposited. The ILD layer  220  is then planarized by chemical-mechanical polishing (CMP) as shown in  FIG. 5A . From the state shown in  FIG. 5A , conventional interconnect processing such as a Dual Damascene process is used. During the interconnect process, the sidewalls of the memory element and the bottom electrode are protected with the sidewall protection sleeve  200 . An exemplary Dual Damascene process can include multiple etch steps. For example, in one etch, using a photoresist mask defining the via, the exposed portion of the ILD layer  220  overlying the etch stop layer  210  is removed. A subsequent etch removes the etch stop layer  210  from the via area around the memory element stack. During the etching, the memory element stack is protected by sidewall protection sleeve  200  which is resistant to etching ambient used to remove layer  210 . The result of the sequence of etching steps is shown in  FIG. 5B . As noted above the via etching depth can be shallower or deeper than shown, with the requirement being that the upper surface of the top electrode is exposed. The remainder of the interconnect process is performed including depositing a metal, e.g., copper, over the wafer to form the bit line connection to the top electrode. The result is the memory cell having a sidewall protection sleeve embodiment of the invention as shown in  FIG. 2 . 
     In an alternative embodiment illustrated in  FIG. 10 , function of etch stop layer  210  is performed by sequentially deposited bottom and top etch stop layers  211 ,  212 . The stage of the process illustrated in  FIG. 10  is comparable to the one illustrated in  FIG. 5A  but with two layers  212 ,  211  replacing single layer  210 .  FIG. 11  illustrates a cross sectional view of a completed memory cell according to the alternative embodiment of the first embodiment of the invention with a single layer sidewall protection sleeve and a dual layer etch stop layer structure. The combined thickness of the two etch stop layers  212 ,  211  is comparable to that of the single etch stop layer  210 . An advantage of this alternative embodiment is that it helps address the problem of thickness variations of ILD  220  after CMP planarization across a wafer and between wafers. The material for the top etch stop layer  212  is selected to have high selectivity during etching of ILD  220  so that the etching depth reliably stops in the top etch stop layer  212  even when the ILD  220  is thinner than average. Thus the added etch resistance provided by top etch stop layer  212  reduces variation resulting from the ILD etching step caused by the thickness variation of ILD  220 . The result is that variation of residual thickness of the layers over the memory element is considerably smaller compared that of ILD  220 . 
     The dielectric material for top etch stop layer  212  is selected to have a relatively slow etching rate in the etching ambient gas used for layer  220  etching so that etching stops in the layer  212  controllably. For example, the material for top etch stop layer  212  can be silicon nitride, nitrogen-doped silicon carbide, aluminum oxide or a borazinic film. The material for bottom etch stop layer  211 , for example, can be silicon nitride, silicon oxide, Silicon carbide and so on is combined with a material of bottom top etch stop layer  212 . Subsequent etching of the dual etch stop layer embodiment is well controlled by selecting an etching ambient that etches the material in top etch stop layer  212  at a rate that is equal to or faster than the material in bottom etch layer  211 . 
     Top etch stop layer  212  should not be the same material as ILD layer  220 . The 3 materials for layers  220 ,  212 ,  211  should be selected with regard to each other. Materials are selected using the following criteria. The etch rate of top etch stop layer  212  in ILD layer  220  etching ambient is much smaller (slower) than ILD layer  220 . This criterion is the same as for the single etch stop layer  210  embodiments. The etch rate of top etch stop layer  212  in bottom etch stop layer  211  etching ambient is comparable or faster than for top etch stop layer  212 . Therefore, bottom etch stop layer  211  can be a same material as top etch stop layer  212 . 
     The following combinations of material are preferred:
         A. Top etch stop layer  212 =(nitrogen-doped silicon carbide, aluminum oxide or a borazinic film) with bottom etch stop layer  211 =(silicon nitride, or silicon oxide);   B. Top etch stop layer  212 =(silicon nitride) with bottom etch stop layer  211 =(silicon nitride, or silicon oxide).
 
An exemplary embodiment can use a low k oxide such as silicon oxide for ILD  220 , nitrogen-doped silicon carbide for top etch stop layer  212 , and silicon nitride (low temperature) for bottom etch stop layer  211 .
       

     A cross sectional view of the second embodiment of the invention with a dual-layer sidewall protection sleeve is illustrated in  FIG. 6 . The memory element is the same as in the first embodiment. A first layer  230  of sidewall protection is preferably an oxygen free dielectric to avoid oxidation of the MTJ stack and can be patterned as described above for the first embodiment. The inner sidewall protection layer  230  is in contact with and covers the sidewall of the memory element. As in the first embodiment, the sidewall protection layer  230  conforms to the shape of the patterned memory element which in this embodiment is an open-topped cone. 
     After the inner sidewall protection layer  230  has been etched down to expose the upper surface of the top electrode, the second sidewall protection layer  240  is deposited over and covers the inner sidewall protection layer  230 . For the outer sidewall protection layer  240  a material having a relatively slow etching rate in etching ambient gas used to etch layer  210 . The material can be selected to be aluminum oxide or a comparable material. The upper surface of top electrode  120  is not covered with either of the sidewall protection layers to allow connection to the bit line interconnect  300  for standard interconnection. 
     The initial steps in a process according to second embodiment of the invention are generally the same as for the first embodiment, and the first sidewall protection layer  230  can be patterned as described above for layer  200  in the first embodiment. However, the material for the inner sidewall protection layer  230 , is preferably an oxygen free dielectric such as silicon nitride or a silicon carbide. A bulk dielectric material  240 ′ is deposited over the wafer and inner protection layer  230  as shown in  FIG. 7  which will be patterned into the outer sidewall protection layer  240 . The material for the outer sidewall protection layer  240  is preferably aluminum oxide or borazinic film or a comparable material. The outer sidewall protection layer  240  protects the inner sidewall protection layer  230  during the interconnect process. The outer sidewall protection layer  240  is vertically etched until top of the memory element is exposed to allow interconnection with the bit line as shown in  FIG. 8 . The process continues in the conventional manner after the outer sidewall protection layer  240  is vertically etched. Etch stop layer  210  and ILD oxide layer  220  are deposited sequentially. ILD  220  is planarized by CMP as shown in  FIG. 8 . 
     The etch stop layer  210  in the second embodiment as shown in  FIG. 8  can be replaced by a dual layer as described above for the first embodiment. A dual etch stop layer consisting of a top layer  212  and a bottom layer  211  is illustrated in  FIG. 9 . The stage of the process illustrated in  FIG. 9  is comparable to that shown in  FIG. 8 .  FIG. 12  illustrates a cross sectional view of a completed memory cell according to the alternative embodiment of the second embodiment of the invention with a dual-layer sidewall protection sleeve and a dual layer etch stop layer structure. 
     It is followed by conventional interconnect processing such as a Dual Damascene process. After this processing, a memory cell having dual sidewall protection layers is completed as shown in  FIG. 6 . During the interconnect process, the outer sidewall protection layer  240  protects the inner sidewall protection layer  230  covering the sidewall of the memory element and thereby protects the memory element.

Technology Category: 5