Patent Document

CROSS-REFERENCE TO RELATED APPLICATIONS  
       [0001]    The present document claims the benefit of U.S. Provisional Application No. 60/376,995, filed Apr. 30, 2002, the contents of which are incorporated by reference herein. 
     
    
     
       FIELD  
         [0002]    The present invention relates to a method for making a resonator. More specifically, the present invention relates to a method for fabricating nanoresonators using a quartz substrate integrated with a base substrate, and a method for thinning the quartz substrate.  
         BACKGROUND  
         [0003]    The use of quartz substrates in a MEMS process provides for the fabrication of high Q, thermally compensated resonators. For thickness shear mode resonators, the thickness of the substrate determines its resonant frequency. The thinner the quartz substrate, the higher the resonant frequency. Therefore, by varying the dimensions of the substrate over a broad range, the resonant frequency can be adjusted over a broad range. The Q of a resonator is a measure of the frequency selectivity of a resonator and is related to how well the energy of the oscillations are trapped. One factor that influences how well the energy of the oscillations is trapped is the smoothness of the surface. When thinning a quartz substrate it is desirable to maintain a smooth undamaged surface to ensure a high Q. However, present quartz fabrication techniques for oscillators or filters do not allow the resonators to be integrated on a chip with other electronics. This is a significant contributing factor to the size and cost of a device. Using separate on chip components also contributes significantly to the size and cost of a device.  
           [0004]    Furthermore, present quartz thinning processes have not be able to thin substrates to a thickness on the order of 10 micrometers or less, because of the inability to monitor the thickness of the quartz substrate in real time with sub micron resolution. Another difficulty is the handling of the quartz substrate after it has been thinned. One reference which discusses thinning quartz substrates is Takahsi Abe, Masayoshi, “One-Chip Multichannel Quartz crystal microbalance (QCM) Fabricated By Deep RIE,” Sensors and Actuators, 2000, pp. 139-143. Having a quartz substrate with a thickness on the order of 10 microns or less can result in resonant frequencies greater than 100 MHz, which is desirable for high frequency applications. By combining several quartz based resonators having different resonant frequency, with a RF MEMS switch on the same chip, frequency hopping and filter reconfiguration can occur on the microsecond time scale. In frequency hopping and filter reconfiguration the desired frequency in a band of frequencies is selected by using the RF MEMS switch to activate the quartz resonator having a resonant frequency equal to the desired frequency. The spectral band for most radio frequency hopping and filter reconfiguration applications is 20 MHz to 3 GHz. The low frequency part of the band is extremely difficult to cover with conventional capacitive-based filters since capacitive-based filters are larger in size. Frequency hopping and filter reconfiguration applications would also benefit from temperature compensated, stable, high-Q (in the amount of about 10,000), small arrays of resonators which cover that spectral band.  
           [0005]    MEMS devices which consist of silicon-based nanoresonators have been fabricated in an attempt to integrate nanoresonators or microresonators with other electronics. Nanoresonators and microresonators are resonators which have linear dimensions on the order of nanometers and micrometers, respectively. These silicon-based nanoresonators have shown resonant frequencies as high as 600 MHz, and Q&#39;s in the range of 1000-2000. However, the problem with silicon-based nanoresonators is that they have high electrical impedances and lower Q&#39;s. Two documents which discuss silicon-based nanoresonators are S. Evoy, A. Olkhovets, L. Sekaric, J. M. Parpia, H. G. Craighead, D. W. Carr, “Temperature-dependent Internal Friction in Silicon Nanoelectromechanical Systems,” Applied Physics Letters, Vol. 77, Number 15, and A. N. Cleland, M. L. Roukes, “Fabrication of High Frequency Nanometer Scale Mechanical Resonators From Bulk Si Crystals,” Applied Physics Letters, Oct. 28, 1996.  
           [0006]    An alternative solution, is known which makes use of non-MEMS quartz resonators. Such resonators consist of shear strip individual resonators operating in ranges of about 10 MHz to about 1 GHz. These resonators are packaged as discrete devices and mounted as hybrids to other RF circuits. The problem with non-MEMS quartz resonators is that they are non-integrable, they have higher costs, and they are physically larger in size.  
           [0007]    As a result, a new process for manufacturing a quartz-based nanoresonator is desired in order to solve all the aforementioned problems.  
         SUMMARY  
         [0008]    The present invention describes a method for fabricating and integrating quartz-based resonators on a high speed substrate for integrated signal processing by utilizing a combination of novel bonding and etching steps to form ultra thin quartz based resonators. Thinning the quartz substrate in the quartz resonator can be used to provide the desired resonant frequency and may be in excess of 100 MHz.  
           [0009]    According to one aspect of the present invention, a novel method for fabricating a quartz based resonator is disclosed. The method makes use of the bond between the quartz substrate and the silicon substrate, as well as a novel process to thin the quartz substrate to a desired thickness. A quartz substrate is provided having a first electrode deposited thereon. The quartz substrate is bonded to a first substrate having a cavity etched therein to accommodate the first electrode. The quartz substrate is then thinned to a desired thickness and a second electrode is deposited on the quartz substrate. The first electrode is connected to the second electrode with vias which are filled with a metal. In addition to the first and second electrodes, a tuning pad is preferably deposited on the quartz substrate. Further, the present invention provides a base substrate which contains probe pads. After depositing the first and second electrodes and the tuning pads on the quartz substrate, the probe pads of the base substrate are bonded to the second electrodes of the quartz substrate. The tuning pad can be used to adjust the resonant frequency of the quartz substrate. Further, it is also possible to use the first and second electrodes as tuning pads. More specifically, the first and second electrodes may be ablated to adjust the resonant frequency of the nanoresonator. Additionally, the base wafer could contain high-speed RF electronics, which would suppress the need for lengthy bond wires. The first substrate is then removed from the quartz substrate thereby releasing the resonator.  
           [0010]    It is also an object of the present invention to provide a method for fabricating a quartz based resonator without the use of a silicon wafer. In this embodiment first electrodes and a tuning pad are deposited on the quartz resonator. A base substrate is also provided. The base substrate contains probe pads for providing an electrical connection to the quartz substrate. The quartz substrate is bonded to the base substrate and then undergoes a thinning process. After the quartz substrate is thinned, second electrodes and a tuning pad are deposited on the quartz substrate.  
           [0011]    It is also an object of the present invention to provide a novel method for thinning a quartz substrate. In this method, a lap and polish system is used to remove a substantial portion of the quartz substrate. Then reactive ion etching is used thin the quartz substrate to a thickness less than 10 micrometers, which is needed for resonant frequencies greater than 100 MHz. The reactive ion etching is used simultaneously with an optical monitoring technique to obtain the current thickness of the quartz substrate as it is being thinned. After obtaining the desired thickness of the quartz substrate using reactive ion etching, the quartz substrate can be further polished using a chemical mechanical polish (CMP) or a wet etch. 
       
    
    
     BRIEF DESCRIPTION OF DRAWINGS  
       [0012]    The present invention will be understood and appreciated more fully from the following detailed description taken in conjunction with the drawings in which:  
         [0013]    [0013]FIG. 1 shows a quartz substrate, silicon substrate and base substrate, to be used in accordance with a first embodiment of the present invention;  
         [0014]    [0014]FIG. 2 shows the silicon substrate with a cavity;  
         [0015]    [0015]FIG. 3 shows photoresist on the quartz substrate;  
         [0016]    [0016]FIG. 4 shows the quartz substrate with first electrodes and a tuning pad;  
         [0017]    [0017]FIG. 5 a  shows the quartz substrate bonded to the silicon substrate;  
         [0018]    [0018]FIGS. 5 b - 5   e  show the thinning of the quartz substrate while bonded to the silicon substrate;  
         [0019]    [0019]FIGS. 6 a  and  6   b  show two methods used to monitor the thickness of the quartz substrate while being thinned;  
         [0020]    [0020]FIG. 7 shows vias in the quartz substrate;  
         [0021]    [0021]FIG. 8 shows the same as FIG. 7 except second electrodes and a tuning pad have been deposited on the quartz substrate;  
         [0022]    [0022]FIG. 9 shows the same as FIG. 8 except a portion of the quartz substrate has been removed;  
         [0023]    [0023]FIG. 10 shows a portion of the base substrate having been removed;  
         [0024]    [0024]FIG. 11 shows the same as FIG. 10 except probe pads have been added to the base substrate;  
         [0025]    [0025]FIG. 12 shows the bond between the probe pads of the base substrate and the second electrodes on the quartz substrate; and  
         [0026]    [0026]FIG. 13 shows the same as FIG. 12 except the silicon substrate has been removed.  
         [0027]    [0027]FIG. 14 shows the quartz substrate and base substrate to be used in accordance with a second embodiment of the present invention;  
         [0028]    [0028]FIG. 15 shows the quartz substrate with first electrodes and a tuning pad;  
         [0029]    [0029]FIG. 16 shows a portion of the base substrate having been removed;  
         [0030]    [0030]FIG. 17 shows the same as FIG. 16 except probe pads have been added to the base substrate;  
         [0031]    [0031]FIG. 18 shows the quartz substrate bonded to the base substrate;  
         [0032]    [0032]FIG. 19 shows the thinning of the quartz substrate while bonded to the base substrate;  
         [0033]    [0033]FIG. 20 shows the vias created in the quartz substrate;  
         [0034]    [0034]FIG. 21 shows the second electrodes and tuning pad on the quartz substrate; and  
         [0035]    [0035]FIG. 22 shows the same as FIG. 21 except a portion of the quartz substrate removed. 
     
    
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS  
       [0036]    The present invention provides a method for fabricating a resonator with reference to FIGS. 1-22.  
         [0037]    First Embodiment  
         [0038]    A method of fabricating a quartz resonator according to a first embodiment of the present invention will now be described with reference to FIGS. 1-13. Referring to FIG. 1, a quartz substrate  2  having a first surface  3  and a second surface  5 , a first substrate  4 , and a base substrate  14  are provided. The first substrate  4  may comprise a material such as silicon or GaAs. In this embodiment, both the first substrate  4  and quartz substrate  2  may be provided in the form of 3 inch or larger wafers. A portion of the first substrate  4  is etched away creating a cavity  6 , as shown in FIG. 2. The etched cavity  6  can be fabricated with a wet etch of potassium hydroxide, or a dry reactive ion etch using a gas having a fluorine chemistry.  
         [0039]    The first surface  3  of the quartz substrate  2  is then patterned and metallized using a lift-off technique. In the lift-off technique, a thin layer of photoresist  7  is patterned on the first surface  3  of the quartz substrate  2 , as shown in FIG. 3. Using lithography, photoresist is removed in the regions where metallization is desired. The metal is then deposited on the photoresist  7  and in the regions where the photoresist  7  was removed. The photoresist is then removed leaving metal only in the desired regions on the first surface  3  of the quartz substrate  2  as shown in FIG. 4. During patterning and metallizing at least one first electrode  8  is deposited on the first surface  3  of the quartz substrate  2 . The first electrode  8  may be comprised of a combination of Ti, Pt, Au, or Cr, Pt, Au, deposited in that order on the first surface  3  of the quartz substrate  2  in that order. Shown in FIG. 4 are two first electrodes  8  on the first surface  3  of the quartz substrate  2 . Additionally, a first tuning pad  10  may be deposited on the first surface  3  of the quartz substrate  2 . The first tuning pad  10  is comprised of the same material as the first electrodes  8 . The purpose of the two first electrodes  8  and the first tuning pad  10  will be discussed later.  
         [0040]    After the first electrodes  8  and the first tuning pad  10  are deposited, the quartz substrate  2  is bonded to the etched first substrate  4 , as shown in FIG. 5 a  using for example, an EV 501 Wafer Bonder which is commercially available. To bond the quartz substrate  2  to the first substrate  4 , the quartz substrate  2  and first substrate  4  are thoroughly cleaned in a megasonic cleaning system, which makes use of ultrasonic waves to remove particle contaminants. After the wafers are cleaned, they are brought in contact with each other. The contact between the quartz substrate  2  and the first substrate  4  creates a bond due to the well known van der Waals force. The first electrodes  8  and the first tuning pad  10  are now located in the cavity  6  of the first substrate  4 .  
         [0041]    The second surface  5  of the quartz substrate  2  remains exposed, and undergoes a thinning process, shown in FIGS. 5 b - 5   e.  In order to thin the quartz substrate  2 , the following method is used. For exemplary purposes only, the quartz substrate  2  has an initial thickness of 500 micrometers. A first portion of the quartz substrate  2  is removed by thinning the quartz substrate from about 500 micrometers to 50 micrometers as shown in FIG. 5 b  using a mechanical lapping and polishing system. Lapping and polishing systems are well known and commercially available from manufacturers such as Logitech. In a mechanical lapping and polishing system, a polishing head is spun at a high rate of speed. The lapping and polishing system also comprises a nozzle for dispensing slurry on the quartz substrate  2 . While spinning, the polishing head contacts the quartz substrate in the presence of the slurry, thereby evenly grinding away portions of the quartz substrate  2 . The slurry may be comprised of chemicals such as aluminum oxide to remove quartz from the quartz substrate  2 .  
         [0042]    Next, a second portion of about 1 micrometer of quartz is removed from the quartz substrate  2 , as shown in FIG. 5 c  to ensure a smooth surface. This is done with the above described mechanical lapping and polishing system, except a softer chemical such as colloidal silica or cerium oxide is used in the slurry to remove quartz from the quartz substrate  2 .  
         [0043]    Next, a third portion of the quartz substrate  2  is removed to reduce the thickness of the quartz substrate  2  to less than 10 micrometers as shown in FIG. 5 d  using reactive ion etching (RIE) with CF 4  or SF 6 gas  9 , as shown in FIGS. 6 a - 6   b.  While being thinned in the RIE machine, the thickness of quartz substrate  2  is simultaneously monitored using spectropic ellipsometry or reflectometry techniques, as shown in FIGS. 6 a - 6   b.  In spectroscopic ellipsometry, shown in FIG. 6 a,  a beam of white light  18  from a source  19  is shone onto the quartz substrate  2  at an angle of about 15° off horizontal. The white light has a known polarization. The reflected white light  20  off the quartz substrate  2  will have a different polarization which is directly related to the thickness of the quartz substrate  2 . A receiver  21  receives the reflected white light  20  and calculates the change in polarization. The change in polarization is directly proportional to the thickness of the quartz substrate  2 . In reflectometry, shown in FIG. 6 b,  a laser source  22  shines light  23 , with a known wavelength, onto the second surface  5  of the quartz substrate  2  at an angle of 90° off horizontal as shown in FIG. 6 b.  A first reflected beam  24  is reflected off the second surface  5  of the quartz substrate  2 . A portion of the incident light also penetrates through the quartz substrate  2 . This creates a second reflected beam  25  which is reflected off the first surface  3  back through the quartz substrate  2  and out the second surface  5 . The first reflected beam  24  and second reflected beam  25  are parallel to each other and are received by a receiver  26  which determines whether the first reflected beam  24  and the second reflected beam  25  add constructively or destructively. If the first and second reflected beams  24 ,  25  add constructively, the thickness of the quartz substrate is equal to 25% of the ratio of the incident light wavelength divided by the refractive index of quartz, or an odd integer multiple thereof, such as 75%, 125%, etc. The refractive index of quartz is typically about 1.46. If the first and second reflected beams  24 ,  25  add destructively, the thickness of the quartz substrate  2  is equal to 50% of the ratio of the incident light wavelength divided by the refractive index of quartz, or an integer multiple thereof, such as 100%, 150%, etc.  
         [0044]    After using RIE to remove quartz from the quartz substrate  2 , the surface of the quartz substrate  2  may have imperfections that need to be corrected. This can done by using the mechanical lapping and polishing system described above with a chemical such as silica or cerium oxide, to remove about 0.01-0.02 micrometers of quartz, followed up with a wet etch in ammonium bifluoride to remove about 0.005 micrometers of quartz from the quartz substrate  2 , as shown in FIG. 5 e.  This additional step will help ensure a polished, defect free quartz substrate  2 .  
         [0045]    After the quartz substrate  2  is thinned, vias  11  are fabricated in the quartz substrate  2 , as shown in FIG. 7. The vias  11  are created using lithography techniques well known in the art. The vias  11  are contacts which are etched through the quartz substrate  2  to the first electrodes  8 . FIG. 7 shows two vias  11 . Once the vias  11  are fabricated, the vias are metallized and the second surface  5  of the quartz substrate  2  is patterned and metallized, as shown in FIG. 8, using the lift-off technique described for depositing the at least one first electrode  8 . During the metallization step, at least one second electrode  12  is deposited on the second surface  5  over the vias  11 . The second electrode  12  may be comprised of a combination of Ti, Pt, Au, or Cr, Pt, Au, deposited in that order on the second surface  5  of the quartz substrate  2  in that order. Shown in FIG. 8 are two second electrodes  12 .  
         [0046]    The first and second electrodes  8 ,  12  are now connected through the vias  11 . Additionally, a second tuning pad  13  can be deposited during the step of depositing the second electrodes  12 , as shown in FIG. 8. The second tuning pad  13  is comprised of the same material as the second electrodes  12 . Once the first and second electrodes  8 ,  12  and first and second tuning pads  10 ,  13  have been deposited, a portion of the quartz substrate  2  is removed, thereby creating a modified quartz substrate  2   a,  as shown in FIG. 9. Such portion is removed using lithography and REI techniques well known in the art to divide the quartz substrate into individual devices and determine the desired dimensions of the quartz substrate  2 .  
         [0047]    The first and second tuning pads  10 ,  13  on the modified quartz substrate  2   a  allow the resonant frequency of the quartz substrate  2   a  to be adjusted. By ablating a portion of the first and second tuning pads  10 ,  13 , the resonant frequency of the quartz substrate  2   a  can be adjusted. However, it is also possible to adjust the resonant frequency by ablating a portion of the first and second electrodes  8 ,  12 . The first and second tuning pads  10 ,  13  can be ablated using known techniques such as focused ion beam milling or laser ablation.  
         [0048]    As already mentioned above with reference to the detailed description of FIG. 1, a base substrate  14  is provided. The base substrate  14  is comprised of a group III-V material or SiGe. FIG. 10 shows a modified base substrate  14   a,  where a portion of the base substrate  14  shown in FIG. 1 has been removed. The removal of a portion of the base substrate  14  is done using lithography techniques well known in the art. At least one probe pad  16  is deposited on the modified base substrate  14   a.  FIG. 11 shows, for example, two probe pads  16 . The probe pads are deposited using the same lift off technique used to deposit the at least one first electrode  8  discussed previously. The probe pads  16  may be comprised of a gold/germanium alloy, nickel, and gold deposited in that order.  
         [0049]    After the probe pads  16  have been deposited on the modified base substrate  14   a,  the bottom electrodes  12  of the modified quartz substrate  2   a  are bonded to the probe pads  16  along bonding line  17 , as shown in FIG. 12 using an Au—Au compression bonding scheme. In the Au—Au compression bonding scheme, the quartz substrate  2 , the second electrodes  12 , the probe pads  16 , and the modified base substrate  14   a  are heated to a temperature greater than 300° C. in a vacuum having a pressure no greater than 10 −4  Torr. Then the second electrodes  12  and probe pads  16  are pressed together, while depressurized, with a pressure of approximately 1 MPa. This will fuse the probe pads  16  and the second electrodes  12  together, as shown in FIG. 12.  
         [0050]    The above described bonded structure provides electrical access from the probe pads  16  to the first electrodes  8 . After the second electrodes  12  have been bonded to the probe pads  16 , the quartz substrate  2   a  is removed from the remaining structure, using a combination of wet and dry etches so that a structure like the one shown in FIG. 13 is obtained.  
         [0051]    The purpose of the first and second electrodes  8 ,  12  is to receive an electrical signal from the probe pads  16  which can bias or drive the modified quartz substrate  2   a  with an electric field. The electrical signal is preferably an AC signal. When the electrical signal is received by the first and second electrodes  8 ,  12  a strain is placed on the modified quartz substrate  2   a.  This strain stimulates the mechanical resonant frequency of the modified quartz substrate  2   a  by the well-known piezoelectric effect, thereby causing the modified quartz substrate  2   a  to oscillate at its resonant frequency. Additionally, it is also possible to use the first and second electrodes  8 ,  12  to sense the movement of the modified quartz substrate  2   a  relative to a specified plane (not shown). Once the modified quartz substrate  2   a  is oscillating at its resonant frequency, it can be used to drive other components at a frequency equal to its resonant frequency.  
         [0052]    Second Embodiment  
         [0053]    A second embodiment of a method for fabricating a quartz resonator will now be described with reference to FIGS. 14-22. This second embodiment is similar to the first embodiment, except the first substrate is removed from the process. In this embodiment, a quartz substrate  30  and a base substrate  40  are provided, as shown in FIG. 14. A first surface  31  of the quartz substrate  30  is patterned and metallized using the lift-off technique discussed in the first embodiment for depositing first electrodes  8 . During patterning and metallizing, at least one first electrode  36  is deposited on the first surface  31  of the quartz substrate  30 . FIG. 15 shows two first electrodes  36 . Additionally, a first tuning pad  38  is deposited on the first surface  31  of the quartz substrate  30 .  
         [0054]    As aforementioned, a base substrate  40  is provided. This base substrate  40  is comprised of a group III-V material or SiGe. In order to obtain a modified base structure  40   a,  shown in FIG. 16, a portion of the base structure  40  is removed using the techniques discussed in the first embodiment. At least one probe pad  42  is deposited on the modified base substrate  40   a  using the lift-off technique discussed in the first embodiment for depositing probe pads  16 . Shown in FIG. 17 are two probe pads  42 .  
         [0055]    After the probe pads  42  have been deposited on the modified base substrate  40   a , the first electrodes  36  of the quartz substrate  30  are bonded to the probe pads  42  along bonding line  43 , as shown in FIG. 18 using the Au—Au bonding scheme discussed in the first embodiment.  
         [0056]    Next, the quartz substrate  30  is thinned to a thickness of 10 micrometers or less, as shown in FIG. 19, using the technique discussed in the first embodiment. Vias  39  are fabricated in the quartz substrate  30  using the techniques discussed in the first embodiment. The vias  39 , shown in FIG. 20, are contacts which are etched through the quartz substrate  30  to the first electrodes  36 . Once the vias  39  are fabricated, the vias  39  are metallized and the second surface  33  of the quartz substrate  30  is patterned and metallized using the lift-off technique discussed in the first embodiment for depositing second electrodes  12 . During the metallization step, at least one second electrode  46  is deposited on the second surface  33  over the vias  39 . Shown in FIG. 21 are two second electrodes  46 . The first and second electrodes  36 ,  46  are connected through the vias  39 . Furthermore, a second tuning pad  48  can be deposited as shown in FIG. 21, during patterning and metallization of the second electrodes  46 . Finally a portion of the quartz substrate  30  is removed, thereby creating a modified quartz substrate  30   a,  as shown in FIG. 22, using lithography and RIE techniques known in the art. Once the modified quartz substrate  30   a  is oscillating at its resonant frequency, it can be used to drive other components at a frequency equal to its resonant frequency.  
         [0057]    Let it be understood that the foregoing description is only illustrative of the invention. Various alternatives and modifications can be devised by those skilled in the art without departing from the spirit of the invention. Accordingly, the present invention is intended to embrace all such alternatives, modifications, and variances which fall within the scope of the appended claims.

Technology Category: y