This application claims priority based on provisional application 61/383,425, titled “Improvement of Corrosion Resistance of Magnesium Alloys by Burnishing,” filed Sep. 16, 2010 and which is incorporated herein by reference. 
    
    
     TECHNICAL FIELD 
     This invention pertains to improving the resistance of surfaces of magnesium-based alloy workpieces to aggressive media induced corrosion. More specifically, this invention pertains to the burnishing, or like mechanical working, of surfaces of magnesium alloys, such as AZ31 magnesium alloy, to refine the metallurgical grain structure in surface layers of magnesium workpieces for the purpose of increasing their resistance to corrosive environments. 
     BACKGROUND OF THE INVENTION 
     Magnesium-based alloys are potential lightweight materials for automotive applications and the use of the alloys may significantly improve the vehicle fuel economy. However, the poor corrosion resistance of Mg alloys significantly limits their wider application. The corrosion performance of Mg AZ31 alloy is among the poorest compared with other common cast Mg alloys, such as AZ91 or AM60. There is a need for a method of improving the corrosion resistance of workpieces of susceptible magnesium based alloys. 
     SUMMARY OF THE INVENTION 
     Methods are provided for the relatively simple and inexpensive mechanical working of surfaces of magnesium-based alloys (typically containing at least about ninety percent by weight magnesium) for the purpose of refining the grains of a surface layer of the workpiece in a manner that reduces the susceptibility of the treated workpiece layers to corrosion in water-containing, salt and water containing, and other aggressive media containing environments. Such mechanical working processes of surfaces of magnesium alloy workpieces improves opportunities for their use, for example, in components of automotive vehicles that are exposed to water and salt. The surface working may also increase the fatigue resistance of the workpiece. 
     In accordance with embodiments of the invention, magnesium alloy workpieces, such as cast workpieces or wrought bar, tube, sheet, or strip materials are burnished with a mechanical tool that plastically deforms surface regions of the workpiece to selectively reduce the size of the metallurgical grains in the surface layer. The orientation of the refined grains may also be altered. Both changes in the grains in the surface layer are found to reduce the tendency for the deformed surface layer to corrode. The tool is suitably formed of a material that is harder than the magnesium workpiece, such as a tool steel alloy material, or the like, and the surface of the tool has a roughness determined for the squeezing, sliding (such as rolling and sliding), frictional engagement with the workpiece surface in a manner that refines the grain structure in the surface region. Knurling tools or other non-cutting surface working tools may also be used. Such mechanical working of the workpiece is performed so as to refine the grain size of the microstructure in a surface layer to a depth of about three millimeters or so as determined to be suitable for improving resistance to corrosion on the workpiece shape and magnesium-base alloy composition of interest. In general, the sizes of the metallurgical grains in the surface layer of the workpiece are reduced to a few microns or even to a nanometer level by the mechanical deformation. 
     Practices of the invention are demonstrated below in the text of this specification on AZ31 magnesium-based alloys because of their particular susceptibility to salt water corrosion. AZ31 alloys are nominally composed, by weight, of about three percent aluminum, one percent zinc, and the balance magnesium except for very small amounts of other elements present in materials used in formulating the workpiece material. Workpieces of AZ31 alloy are often made by casting into desired workpiece shapes, or by casting, and hot rolling into slabs, strips, or sheets of desired thickness. But the practice of the invention may be adapted to other magnesium-based alloys and to many workpiece configurations. 
     The practice of the invention has been demonstrated by burnishing (or like mechanical working) of surfaces of workpieces with the workpiece initially at ambient temperature. The methods of this invention may also be practiced by burnishing while the workpiece is being cooled such as by spraying the surface of the workpiece with a cooling fluid, such as with liquid nitrogen, as the surface layer is being worked. In other embodiments, the workpiece may be partially immersed in a cooling liquid. 
     One or more surfaces of a magnesium-based alloy workpiece may be selected to be worked in accordance with this invention to reduce the susceptibility of the workpiece to water-based corrosive attack (or other corrosive media) from the environment in which the article is expected to serve. Such surface working for grain refinement may be practiced on a generally finished workpiece shape or on a precursor shape. Since each worked surface experiences some level of deformation, a workpiece may be initially slightly over-sized for the corrosion resisting treatment if a surface dimension may be affected by the method of this invention. 
     Other objects and advantages of the invention will be apparent from a detailed description of illustrative embodiments of the invention. Reference will be made to drawing figures which are summarized in the following section of this specification. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1A  is a schematic drawing illustration of an end of a round cylindrical steel burnishing tool being rotated and pressed into a surface region of a magnesium alloy workpiece in the form of a strip. The rotating tool may be translated over a surface region of the workpiece. The strip workpiece is supported on an anvil as its surface is being deformed. 
         FIG. 1B  is a schematic drawing illustration of a circumferential surface of a round cylindrical steel burnishing tool being rotated as a roller and pressed into a surface region of a magnesium alloy workpiece in the form of a strip. The strip workpiece is supported on an anvil during surface working of the strip. 
         FIG. 1C  is a schematic illustration of a rotating steel roller pressed into a surface region of fragmentary view of a formed magnesium alloy workpiece. The roller is translated over a surface region of a fragmented portion of a shaped magnesium alloy workpiece. 
         FIG. 1D  is a schematic side view illustration of rotating steel roller pressed into and translated along the edge surface of a magnesium alloy strip work piece. 
         FIG. 1E  is a schematic side view illustration of a rotating AZ31 magnesium alloy disk in which the circumferential edge surface of the disc is engaged under pressure by a fixed tool steel roller. In a specific example, described below in this specification, the disc is rotated by a lathe. A spray of liquid nitrogen is applied to the interface of the edge of the rotating disc and the steel roller. 
         FIG. 2A  shows a pie-shaped portion taken from the outer circumferential edge of an AZ31 disc which was burnished using the process shown in  FIG. 1E . The sample was etched with acetic picric acid to reveal its grain structure. 
         FIG. 2B  is a photomicrograph (at 30× magnification) of the section, outlined in  FIG. 2A , of the cryogenically burnished AZ31 disc showing the microstructure from the outer edge surface of the disc after working to a depth of about three millimeters. The dotted line generally parallel to the edge of the disc indicates the approximate distance from the edge in which the grain structure was affected by the burnishing. The numbers  1 - 7  on the  FIG. 2B  photograph show locations of the seven enlarged numbered photomicrographs of  FIG. 4 . 
         FIG. 3  is a photomicrograph (at 1000×) of a section, outlined in  FIG. 2B , of the sample portion shown in  FIG. 2B , and labeled “3”, which shows the boundary between the burnished and un-burnished material of the disc of  FIG. 2A . The upper edge of the micrograph corresponds generally to the location of point  6  of  FIG. 2B  and the lower edge of the micrograph corresponds generally to the location of point  7  in  FIG. 2B . 
         FIG. 4  consists of seven photomicrographs (at 5000×) respectively, at locations  1 - 7  of  FIG. 2B . 
         FIG. 5  consists of two bar graphs, with different grain size scales, showing the percentage of grains lying within specified grain size ranges for an unmodified AZ 31B Mg sample (Graph (a)) and an AZ 31B Mg sample after cryogenic burnishing (Graph (b)) at the sample surface (Location  1  in  FIG. 2B ). 
         FIG. 6  is a graph showing the variation in hardness, measured in gigapascals (GPa), from the surface to the interior of a cryogenically-burnished AZ 31 B Mg sample (triangular data points) and of dry-burnished AZ 31B sample (square data points) burnished in an ambient environment (about 25° C.) without cooling. 
         FIG. 7  shows two bar graphs comparing the arithmetic mean or average surface roughness (Ra), measured in micrometers (μm), of two AZ 31 Mg samples, one after cryogenic burnishing (triangular data points), the other after grinding (square data points). 
         FIG. 8  shows polarization curves for AZ 31B Mg samples after cryogenic burnishing and grinding respectively. 
         FIG. 9  shows AC impedance Nyquist spectra of AZ31B Mg samples immersed in 5 wt. % NaCl solution after grinding (square data points) and cryogenic burnishing (triangular data points) respectively. 
         FIG. 10  shows cumulative hydrogen evolution, expressed as volume of hydrogen per unit area, with time of AZ 31B Mg samples immersed in 5 wt. % NaCl solution after grinding and cryogenic burnishing respectively. 
     
    
    
     DESCRIPTION OF PREFERRED EMBODIMENTS 
     Practices of this invention are used to work surfaces of a magnesium-based alloy article to intentionally deform and reduce the grain size of the magnesium-containing material in the outer few millimeters of the surface layer. Metal material is not removed from the surface, but the surface layer is reshaped by burnishing, knurling, or the like, to form a thin layer of fine-grained microstructure that is more resistant to galvanic corrosion caused by exposure of the surface to salty water and air. In some embodiments of the invention such working may be performed at ambient temperatures (for example, about 25° C.) without cooling of the workpiece. The worked surface regions will, of course, experience some heating. In other embodiments of the invention, the worked surface portions of the workpiece may be cooled with a fluid. Usually such cooling leads to smaller grain sizes in the worked areas. For example, cooling with liquid nitrogen has been used for this purpose. The working is practiced to reduce the grain size of the surface material to a depth of, for example, about one to three millimeters. Often it is desired to obtain grains sizes in the range of about one to five micrometers in largest dimension, or smaller. 
     Thus, practices of the invention may be particularly useful in preparing magnesium alloy components which, for example, are located on automotive vehicles and exposed to aggressive water-containing materials that react chemically and corrosively with magnesium and its alloys. 
     In  FIG. 1A  a workpiece strip  10  of magnesium alloy material (such as AZ 31 magnesium alloy) is supported on an anvil  12 , or a like supporting device, for burnishing with rotating friction tool  14 . Workpiece strip  10  may, for example be a portion of a vehicle body panel that is likely to be exposed to salt water or the like when used in an automotive vehicle. Anvil  12  may be formed of any suitable load bearing material that is compatible with a magnesium alloy workpiece. Rotating friction tool  14  maybe formed of a hard, high melting tool steel alloy or the like. In other embodiments of the invention, a knurling tool or other non-cutting working tool may be used. 
     Friction tool  14  is pressed against a side surface region  16  of workpiece strip  10  and rotated. The rotating tool  14  may be traversed over a surface  16  of the workpiece  10  for the purpose of working a predetermined area of the surface  16  of the article  10 . The pressing force, rate of tool rotation, and working time are determined by experiment or other experience to deform and reduce the grain size of the surface material  16  to improve its metallurgical resistance to corrosion, such as, for example, galvanic corrosion in the presence of water. Often the goal is to thus affect the microstructure of a surface  16  of the workpiece  10  to a depth of about one to three millimeters. The size and shape of the article prior to such deformation may be determined to accommodate such deformation will retaining a desired dimension or shape of the workpiece. 
       FIG. 1B  illustrates a similar magnesium alloy workpiece strip  20  and anvil support  22 . In this example, a rotating steel roller  24  is pressed against a side surface  26  of workpiece strip  20  while traversed across the surface  26 . In  FIG. 1B , the arrow indicates that the direction of traversing is opposed to the direction of rotation, but the direction of traversing may be varied to each practice of the invention. This pressing and shearing force is applied so as to deform a thin surface  26  layer of magnesium alloy material of workpiece  20  and to improve its resistance to galvanic corrosion when wetted with water. 
       FIG. 1C  illustrates the working of a surface portion  32  of a magnesium-based alloy workpiece  30 . Workpiece  30  may be a casting or other formed shape of a magnesium-based alloy article. In this example, a selected surface portion  32  is being worked and deformed by steel roller  34  which is being rotated in one direction, pressed against surface  32  and traversed across surface  32 . In  FIG. 1C , the arrow indicates that the direction of traversing is opposed to the direction of rotation, but, again, the direction of traversing may be varied to each practice of the invention. Again the parameters of the surface working process is to refine the grain size and structure of a thin layer of surface  32  (one to three millimeters or so in depth) to improve the resistance of the magnesium material to galvanic corrosion when exposed to water. 
       FIG. 1D  illustrates the use of rotating steel roller  42  to work edge surface  44  of magnesium alloy strip workpiece  40 . Again, the selected edge portion  44  of strip workpiece  40  was worked to a depth to obtain a refined grains structure more resistant to water-based corrosion than untreated portions of the workpiece  40 . 
       FIG. 1E  illustrates the processing of an edge surface  52  of a disc  50  of a magnesium alloy. The work material studied was the commercial AZ31B-O temper magnesium alloy. The work material was received in the form of a 3 mm thick sheet. The sheet material had been produced from a cast slab of AZ31B composition by rolling. The final sheet material was in an O-temper condition. Disc specimens (each as illustrated at  50 ) with 130 mm diameter were cut from the sheet. The circumferences of the disc specimens were further machined to make them suitably round for mounting on the chuck of a lathe. This reduced the diameters of the disks to 128 mm. The disks were subsequently subjected to burnishing as described below. As illustrated in  FIG. 1E , a center hole  54  and four radial anchoring holes  56  were drilled in the disc specimens for mounting to a lathe, not shown. As described in more detail in a following paragraph, a non-rotating roller  58 , longer that the thickness of each disc was pressed into the edge  52  of the rotating disc  50 . The rotating edge  52  of each disc  50  was cooled with a spray of liquid nitrogen with spray nozzle  60 . 
     Mechanical Working of the AZ31 Disc by Burnishing 
     These burnishing experiments were conducted on a Mazak Quick Turn-10 Turning Center equipped with an Air Products liquid nitrogen delivery system, which is capable of spraying liquid nitrogen in a managed steady stream to the processing zone for cooling. As described with respect to  FIGS. 1A-1D , working of the magnesium alloy workpiece may be accomplished without such cooling. Or, alternatively, a workpiece may be cooled with other suitable cooling fluids and by other cooling practices. 
     The AZ31B Mg disc  50  was fixed in the lathe chuck and was rotating during processing. A roller  58  made of high speed steel alloy and having a diameter of six millimeters was pushed radially inwardly against the circumferential edge  52  of the rotating disc  50  at a feed rate. Different from the traditional burnishing method, the roller used here was not rotated in order to introduce more severe plastic deformation from the forceful sliding contact with the disc. Some lateral movement of the roller, transverse to the disc, was also employed in working of the edge of the rotating disc. During processing, liquid nitrogen was sprayed to the processing zone as shown in  FIG. 1E . The application of liquid nitrogen was intended to reduce the temperature of the worked disc material during processing and introduce significant grain refinement near the surface after processing. However, it has been determined that such cooling is not necessary for all workpiece shapes and magnesium compositions. 
     Burnishing speed refers to the linear speed at the contact point between the fixed roller  58  and the rotated disc  50 . It was set at 100 m/min. The feed rate of the non-rotating roller tool into the circumferential surface of the rotated disc was 0.01 mm/rev of the disc. The burnishing process was stopped when the final diameter of the AZ31 disc was reduced by the burnishing-induced deformation from 128 mm to 125 mm. 
     This burnishing process was practiced on a number of AZ31 discs prepared as described. 
     Grinding Treatment 
     To eliminate any possible influence of surface roughness on corrosion resistance, some un-burnished AZ31B Magnesium alloy samples were abraded successively with course grade of sand paper and finer grades down to 4000 grit sand paper. In the following sections these samples are characterized as ground samples or as samples prepared by grinding. These samples, after grinding, were employed as the reference for the corrosion resistance comparison, presented subsequently, between samples prepared by burnishing and grinding. 
     Characterization Methods 
     After burnishing, metallurgical samples were cut from the burnished discs. After cold mounting, grinding and polishing, acetic picric acid solution was used as an etchant to reveal the grain structure. A KEYENCE digital microscope VHX-600 was used to observe and record the microstructures of the burnished samples. 
     Surface roughness values of the burnished and ground samples were measured using a ZYGO New View 6000 measurement system which was based on white light interferometry. 
     The hardness of the samples from the surface to the bulk material was measured using a Hysitron Tribolndenter. The load used was 8 mN. 
     Electrochemical Measurements 
     A Solatron 1280 potentiostat system was used for polarization curve and AC impedance measurements. Only the processed disc surfaces were exposed to the testing solution and all the other surfaces are protected by a thick layer of MICCROSTOP lacquer. The exposed area was 1.5 cm 2 . The testing solution was 5 wt. % NaCl. A platinum gauze was used as a counter electrode and a KCl-saturated Ag/AgCl electrode was used as a reference in the cell. During AC impedance measurements, the frequency ranged from 17,777 Hz to 0.1 Hz with 7 points/decade, and the amplitude of the sinusoidal potential signal was 5 mV with respect to the Open Circuit Potential (OCP). Potentiodynamic polarization curve measurements were performed at a potential scanning rate of 0.1 mV/s from −0.3V vs. OCP to −1.0V vs. reference. 
     Hydrogen Evolution Measurements 
     In addition to electrochemical methods, a hydrogen evolution method was also used to compare the corrosion rates of samples after cryogenic burnishing and after grinding. The samples were mounted in epoxy resin and only the processed surface was exposed to 5 wt. % NaCl. The exposed area was 1.5 cm 2 . Pipettes with 0.1 mL interval were used to collect the evolved hydrogen from the samples. 
     Results and Discussion 
     Microstructure 
       FIG. 2A  illustrates the shape and location of a pie-shaped segment  50 ′ removed from a burnished, etched magnesium alloy disc ( 50  as illustrated in  FIG. 1A ). As described, the diameter of the disc had been reduced to about 125 mm, and the removed segment included a portion of the circumferential edge  52  and radially inward side surfaces. The drawn square on  FIG. 2A  indicates an area of the side surface of the disc segment which was cleaned and photographed to provide an enlarged image of the surface. Contrast variations, indicative of microstructural variations, between the surface and interior of the disc are observed and are more clearly seen in higher magnification (30×) view of  FIG. 2B . There is a clear interface between the processing-influenced zone and the bulk. The dimension line with upper and lower arrow heads at the right side of  FIG. 2B  extends from the surface (upper arrow head) of the disc segment to the interface (lower arrow head). This interface is also indicated by dotted line  62  in  FIG. 2A . The interface is also shown in  FIG. 3  under 1000× magnification.  FIG. 3  illustrates the 1000 micrometer square region indicated by the box in the lower-right portion of  FIG. 2B . The total thickness of the processing-influenced circumferential disc layer is 3.40±0.01 mm. 
     Also indicated on  FIG. 2A  is a linear strip extending radially inwardly form the burnished edge and indicating seven point locations, the grain structures of which are further illustrated by the photomicrographs of  FIG. 4  which illustrate, respectively, the microstructures of the side surface of the disc segment at points  1 - 7 , where Point  1  is the worked edge and Point  7  in the innermost point below the processing influenced zone of this workpiece. 
     While no twinning can be seen in the initial material, there is a high density of deformation twinning above the interface as shown in  FIG. 3 . The location of twinning is near the bottom of the processing-influenced layer. Twinning gradually disappears when it becomes closer to the top surface. The deformation twinning indicates that the temperature near this interface is lower compared with the top portion of the layer. 
     Clear evidence of dynamic recrystallization (DRX) of the grain microstructure is observed in six of the seven micrographs of  FIG. 4 . The microstructures of  FIG. 4  at the seven different points located in  FIG. 2B , were obtained using the VHX-600 digital microscope, and are shown at a ×5000 magnification. 
     The image at Point  7  in  FIG. 4  represents the initial microstructure and Point  1  is the microstructure near the surface after cryogenic burnishing. It is clear that significant grain refinement occurred near the surface. As shown in the  FIG. 5  bar graphs, the grain size after cryogenic burnishing, graph  5 ( b ), is reduced to 1.03±0.26 μm from the initial grain size of 11.88±4.54 μm, graph  5 ( a ). Not only is the grain size reduced, but also the distribution of grain size becomes more uniform (less scatter). 
     From Point  2  to Point  4  of  FIG. 4 , there is a clear trend that the quantity of ultrafined grains is decreasing. The strain induced by cryogenic burnishing or ambient temperature burnishing should decrease from the surface to the bulk material where the material was not influenced by the process and the strain becomes smaller. 
     The microstructural features at Point  6  of  FIG. 4  further shows that deformation twins are dominant in the transition layer from the processing-influenced microstructure to the initial microstructure. 
     Hardness Measurements 
       FIG. 6  is a graph of hardness values (GPa) versus distance from the top (worked surface) for the cryogenic cooled disc sample of this experiment (triangle data points) and a like uncooled (dry burnished) disc sample (square data points). As shown in  FIG. 6 , the hardness values far away from the surface of the cryogenic cooled disc sample, which is not influenced by the processing, is about 0.9 GPa. After cryogenic burnshing, the hardness near the surface reaches 1.35 GPa. The relationship between hardness and grain size in AZ31 Mg alloys has been frequently reported in literature. The large increase in hardness agrees with the previous finding that significant grain refinement occurs near the surface after cryogenic burnishing. It is also seen on the curve for the dry burnished sample that the are generally lower. 
     Surface Roughness 
       FIG. 7  shows a comparison of the arithmetic mean or average surface roughness (Ra) between grinding and cryogenic burnishing. It shows that grinding generates a slightly smoother surface (lesser value of Ra), which, in general, ought to promote better corrosion resistance. 
     Electrochemical Measurements 
     The polarization curves of samples after grinding and after cryogenic burnishing are presented in  FIG. 8 . This data shows that the cathodic polarization current density after cryogenic burnishing is smaller than the one after grinding, which suggests that burnishing leads to improved corrosion resistance. However, there is a large shift in corrosion potential from −1.44 mV after grinding to −1.53 mV after cryogenic burnishing. While, in general, metals with lower potential are prone to more corrosion, both the literature and the current study show the opposite trend. Without wishing to be bound by any theory it is possible that the burnished surface of the present study promotes more rapid passivation of the surface layer to thereby retard the corrosion process. 
       FIG. 9  shows the Nyquist diagrams of AZ31B Mg samples after grinding and cryogenic burnishing in 5 wt. % NaCl. Both spectra have a clear capacitive arc at the high frequency region. The diameter of this capacitive loop at the high frequency region is associated with the charge-transfer resistance. The diameter for the sample after cryogenic burnishing is remarkably larger than the one after grinding, which suggests the sample after cryogenic burnishing has better corrosion resistance than the ground sample. This finding agrees with the trend of cathodic polarization current densities as shown in  FIG. 8 . 
     Hydrogen Evolution Measurement 
     The cumulative hydrogen evolution of the samples in 5 wt. % NaCl over time for samples after grinding and burnishing are presented in FIG.  10 . It shows that more hydrogen is generated from the ground samples. Also, the scatter after grinding is larger than cryogenic burnishing. Since the cryogenic burnishing was carried out automatically on a CNC machine, it is expected that the process is more repeatable than grinding by hand. The finding from hydrogen evolution measurement further proves that the corrosion resistance of the AZ31B Mg alloy after cryogenic burnishing is improved compared with the corrosion resistance observed after grinding. 
     The present study shows that significant grain refinement as well as a large increase in hardness can be achieved in the surface layer of AZ31B Mg alloy after cryogenic burnishing. The microstructure of AZ31 up to 3.4 mm away from the surface can be remarkably changed by cryogenic burnishing. The mechanism for grain refinement is dynamic recrystallization. 
     Both the electrochemical method and hydrogen evolution methods show that the corrosion resistance of AZ31B Mg alloy is improved after burnishing. Such burnishing may be performed at ambient workpiece temperatures and with cooling of the worked surfaces of the workpiece to below ambient temperatures. 
     Practices of the subject invention provide an opportunity to improve material performance through fabricating a grain refined surface layer by burnishing and like modes of surface working and deformation. Not only corrosion resistance, but other properties, such as fatigue and wear resistance may also be significantly enhanced if proper processing conditions are used. 
     The original dimensions of the workpiece may be determined so as to allow for the deformation of the workpiece by the surface working operation.