Patent Document

BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to a prefilled syringe and to a production method for a barrel thereof and, more specifically, to a prefilled syringe excelling in gas barrier property and water vapor barrier property and to a production method for a barrel thereof. 
     2. Description of the Related Art 
     A prefilled syringe containing, in advance, a medication inside a barrel is prevailing recently for reasons such as savings of time of transferring the medication from a container to the syringe and a low risk of contamination by bacteria. A prefilled syringe with a non-breakable plastic barrel is generally used. 
     However, a prefilled syringe with a plastic barrel has problems such as deterioration of the medication caused by oxygen and evaporation of water from the medication. If the barrel is molded by a resin with barrier properties to avoid these problems, a problem such as elution occurs, involving another problem concerning safety. Therefore, a prefilled syringe with a plastic barrel is generally packaged along with a deoxidant or the like using an external packaging material made of a film which excels in gas barrier property or water vapor barrier property. The packaging step complicates production, and the packaging material makes storage cumbersome, taking significant space as a whole. Further, the packaging material and the deoxidant must be disposed of as waste after use, and it is hardly ecologically friendly. Further, in the case where only a heat-labile resin such as polyethylene can be used in order to prevent an interaction with the medication, the barrel itself may be deformed by high pressure steam sterilization. 
     Although a glass barrel does not have such faults as described above, it is brittle and variations occur in dimensional accuracy; hence it is not yet widely used. 
     There is also an invention of coating the whole outer wall surface of a barrel with a film having a gas barrier property. The film is made of materials, such as polyvinylidene chloride (PVDC), having a water vapor permeability of 20 g/m 2 ·24 h (at 40° C., 90% RH) and may be deposited with aluminum. This prevents penetration of water vapor, oxygen, or the like through a wall surface into the barrel. Thus, the need for packaging the whole prefilled syringe along with a deoxidant or the like can be eliminated, thereby achieving a reduction in production steps as well as in storage space (see Japanese laid-open publication No. JP 11-332984 A). 
     Further, as an invention imparting a gas barrier property to a barrel itself, other than the invention of the above JP 11-332984 A, there is an invention in which 90% or more of an amorphous silicon oxide (SiO m ) layer, which is obtained by baking a polysilazane film in an oxidizing atmosphere, is formed on a wall surface of the barrel at a thickness of 0.05 to 20 μm (see Japanese laid-open publication No. JP 10-57446 A). 
     In addition, there is an invention of obtaining a multilayer parison by sequentially and alternately injecting two or more kinds of molten thermoplastic resins into one mold with shifting injection timing from a molding machine having plural injection cylinders with one mold closing operation. Herewith, the multilayer parison, which is a preform for a hollow container, is sanitary and excels in gas permeability resistance and water permeability resistance. The multilayer parison can be obtained using a polyethylene terephthalate (PET) resin or a polyamide resin containing a meta-xylylene group as an intermediate layer and using the PET resin for inner and outer surface layers. A hollow container also usable for medical applications may be obtained by blow molding the multilayer parison (see U.S. Pat. No. 4,535,901). 
     However, although JP 11-332984 A does not mention a method of coating an outer wall of a syringe barrel with a film having a gas barrier property, an adhesive or a bonding layer is required for bonding the film on the barrel. In addition, it is difficult to coat the whole cylindrical barrel. When shrink packaging, the gas barrier property may not be ensured because the film and the syringe do not completely bond. Further, ethylene vinyl alcohol copolymer (EVOH), which is a typical gas barrier material, significantly degrades in barrier property by high pressure steam sterilization, so even if the outer wall of the barrel could be supposedly coated, it is pondered whether a desirable effect will be obtained. 
     On the other hand, when producing a barrel for a prefilled syringe using the method described in JP 10-57446 A, the method must go through 5 stages of the steps of (a) molding the barrel with a predetermined resin, (b) applying a polysilazane solution to the barrel, (c) removing an organic solvent in the polysilazane solution by drying in an oxygen atmosphere at 60° C. or less, (d) forming an amorphous silicon oxide layer by baking the barrel at a temperature of 60° C. to 200° C., and (e) forming a protective film with an epoxy resin or the like on the outermost layer. The production method is thus complicated, and it cannot be said that production efficiency is satisfactory. Further, polysilazane hydrolyzes when coming in contact with water and an alcohol solvent; therefore, an aromatic hydrocarbon such as xylene or petroleum ether must be inevitably used for a solvent. It takes time to completely remove those organic solvents, and in a case of incomplete removal thereof, a problem arises in terms of safety of the medication. Further, polysilazane produces pyrophoric silane gas, so control and handling thereof are difficult. 
     Further, the method described in U.S. Pat. No. 4,535,901 relates to a production method for a parison, which is a preform for a hollow container to be obtained by blow molding, and is not related to a barrel of a medical syringe with both ends opened and a production method thereof. 
     BRIEF SUMMARY OF THE INVENTION 
     The inventors of the present invention, devoting themselves to research for solving the problems described above, have completed the present invention. 
     That is, the present invention relates to: 
     (1) a prefilled syringe including: a shoulder portion provided with a luer tip for connecting an injection needle at the tip; a barrel with an opened proximal end; and a gasket inserted from the proximal end of the barrel in a fluid-tight manner while being freely slidable, a medication being contained inside the barrel, in which the barrel has a multilayer structure in which an innermost layer and an outermost layer are both made of a polyolefin resin, and an intermediate layer is composed of at least one layer made of a resin excelling in barrier property.
 
(2) a prefilled syringe according to the above-mentioned (1), in which the intermediate layer is formed up to the vicinity of a luer tip surface.
 
(3) a prefilled syringe according to the above-mentioned (1), in which a tip of the intermediate layer in a cylindrical wall portion of the barrel is formed up to a rim of the shoulder portion, the shoulder portion is formed with the polyolefin resin to a thickness which exerts a barrier property, and the luer tip is sealed by a cap having a barrier property.
 
(4) a prefilled syringe according to any one of the above-mentioned (1) to (3), in which the intermediate layer is formed toward a direction of the proximal end of the barrel from a proximal end of a presumed insertion position of the gasket inserted in the barrel.
 
(5) a production method for a barrel according to any one of the above-mentioned (1) to (4) including the steps of: (a) injecting a specific amount of a polyolefin resin from a gate of a cavity provided at a position corresponding to a luer tip surface of the barrel; (b) sequentially injecting a specific amount of a resin excelling in a barrier property; (c) injecting a specific amount of the polyolefin resin again; and (d) separating the luer tip surface and an injection unit by pushing off at least one of a valve pin provided inside a valve gate and an inner nozzle of the injection unit, which injects the resin excelling in a barrier property toward the luer tip surface.
 
(6) a production method for a barrel according to any of one of the above-mentioned (1) to (4) including the steps of: (a) injecting a specific amount of a polyolefin resin inside a cavity from a gate provided at an arbitrary position of the shoulder portion of the barrel; and (b) sequentially injecting a specific amount of a resin excelling in a barrier property.
 
     It should be note that “barrier property” refers to a “gas barrier property”, “water vapor barrier property”, or “gas barrier property and water vapor barrier property”. “Excelling in gas barrier property” means that an oxygen permeability at 25° C., 50% RH, is 2 ml/m 2 ·24 hr·atm/25 μm or less. “Excelling in water vapor barrier property” means that a water vapor permeability at 40° C., 90% RH, is 10 g/m 2 ·24 hr·atm/25 μm or less. Further, “having barrier property” refers to having a feature excelling in a barrier property described above. 
     Further, “excelling in thermal resistance” refers to enduring high pressure steam sterilization under harsh conditions such as at 105° C. for 30 minutes or more. “Elution” refers to an elution of a resin component into a medication or an elution of a plasticizer contained in the resin component. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1(   a )-( c ) is a diagram showing an embodiment of the present invention. Part (a) is a longitudinal sectional view, and part (b) is a cross sectional view taken along line A-A (the gasket is not shown). 
         FIG. 2  is a partial view showing another embodiment of the present invention, in which a syringe is a so-called eccentric luer tip type syringe and has a luer tip provided in a position eccentric from the center. 
         FIG. 3  is a partial longitudinal sectional view showing a state during use of a syringe of an embodiment of the present invention and shows a state of an injection needle connected to a luer tip. 
         FIG. 4  is a diagram showing another embodiment of the present invention in which an intermediate layer is formed up to a thickly formed shoulder portion rim. 
         FIG. 5(   a )-( c ) is a diagram showing steps of a production method of a barrel according to the present invention. The production method includes injecting resins from a gate provided at a luer tip surface. 
         FIG. 6(   a )-( b ) is a diagram showing steps of a production method of a barrel according to the present invention. The production method separating a product and an injection unit by pushing off of an inner nozzle. 
         FIG. 7(   a )-( b ) is a diagram showing steps of another production method of a barrel according to the present invention. The production method includes separating a product and an injection unit by pushing off of a valve pin inside a valve gate. 
         FIG. 8  is a diagram showing another production method of a barrel according to the present invention. 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     First, a barrel for a prefilled syringe of the present invention is described. As shown in  FIG. 1(   a ), a preferably adopted shape of the barrel  10  of a prefilled syringe of the present invention is a cylindrical shape having a male “Luer-taper” luer tip  11  at the tip, where an injection needle can be connected in a fluid-tight manner, a shoulder portion  13  formed from a proximal end  11   a  of the luer tip  11  to a cylindrical wall  12 , and a finger-hooking flange  14  at an opened proximal end  10   a . The luer tip  11  is sealed in a fluid-tight manner by a cap  20 . Further, a gasket  30  is inserted in the barrel  10  in a fluid-tight manner while being freely slidable. The gasket  30  can be connected with a plunger  40  at a proximal end  30   a . The space from the gasket  30 , inserted inside the barrel  10 , to the luer tip  11  can contain a medication  50 . A position for providing the luer tip  11  does not have to be at the center of the shoulder portion  13 . As shown in  FIG. 2 , a luer tip  61  may be provided in a position eccentric from the center of a shoulder portion  63 . 
     As shown in  FIGS. 1(   a ) and ( b ), the barrel  10  has at least a three-layer structure of an innermost layer  15 , an outermost layer  16 , and an intermediate layer  17  between the innermost layer  15  and the outermost layer  16 . The innermost layer  15  and the outermost layer  16  are preferably formed from the same material, and examples of preferable materials include polyethylene, polypropylene, a mixture of polyethylene and polypropylene, and a polyolefin resin such as cyclic polyolefin. However, any resin known for use as a medical material such as polycarbonate, a methacrylate resin, and poly (4-methyl-1-pentene), which does not interact with the medication  50  contained inside the barrel  10 , and having no risk of elution or the like can be preferably adopted. Further, the material for the intermediate layer  17  is selected from a resin excelling in a gas barrier property, a resin excelling in a water vapor barrier property, and a resin excelling in thermal resistance. Examples of resins excelling in a gas barrier property and a water vapor barrier property include an ethylene vinyl alcohol copolymer, polyacrylonitrile, vinylidene chloride, polyvinyl alcohol, nylon, polyester, or the like. Examples of a resin excelling in thermal resistance include polypropylene, poly-4-methylpentene-1, polyester, polycarbonate, polyether imide, polyacrylate, or the like. The intermediate layer  17  is not required to be a single layer and may be a multilayer structure with two or more layers. 
     As described, by sandwiching a resin excelling in barrier property or thermal resistance with a resin having a low risk of interacting with a medication or eluting thereinto, a barrel for a prefilled syringe, which has a low risk of interacting with a medication or eluting thereinto, excels in barrier property, and is highly safe, can be provided. 
     When only resins having low thermal resistance are adopted for the innermost layer and the outermost layer because of limitations concerning interaction with a medication, deformation of the barrel can be avoided even when conducting a high pressure steam sterilization such as at 105° C. for 30 minutes, at 121° C. for 20 minutes, or the like by forming an intermediate layer using a thermal resistant resin. 
     As shown in  FIG. 1(   a ), securing of the barrier property of the barrel  10  is further ensured by forming the intermediate layer  17  up to the vicinity of the luer tip surface  11   b . However, the intermediate layer  17  must not be exposed at the luer tip surface  11   b . The reason is that if a gap exists between the luer tip surface  11   b  and a cap  20 , the medication  50  and the luer tip surface  11   b  are at a high risk of coming into contact with each other. Also as shown in  FIG. 3 , in a case of connecting an injection needle  70  to the luer tip  11  during use, the medication  50  and the luer tip surface  11   b  have a high chance of coming into contact with each other, so there is a risk of elution from the intermediate layer  17  into the medication  50 . 
     Further as shown in  FIG. 4 , a tip  97   a  of an intermediate layer  97  of a cylindrical wall portion  82  of a barrel  80  can be formed up to a rim portion  83   a  of a shoulder portion  83 . However, in this case, the shoulder portion  83  must be provided with a barrier property by molding a thick portion of the polyolefin resin. The cylindrical wall portion  82  of the barrel  80 , for visually observing a time course of medication contained therein and insoluble contaminants, must be provided with high transparency and, thus, cannot be thickly molded. Therefore, providing a barrier property by the intermediate layer  97  is indispensable. 
     Further as shown in  FIG. 1(   a ), the intermediate layer  17  does not have to be formed in the direction of the proximal end  10   a  from the proximal end  30   a  of an expected (initial) insertion position of the gasket  30  to be inserted inside the barrel  10 . In the space from the proximal end  30   a  of the gasket  30  to the proximal end  10   a  of the barrel  10 , a medication does not exist. Therefore, there is no need to provide a barrier property. 
     The gasket  30  is formed of a butyl rubber, a thermoplastic elastomer, or the like. The proximal end thereof is provided with a securing means such as a female screw  31  with which the plunger  40  provided with a male screw  41  at the tip thereof can be secured. 
     The cap  20  is formed of a butyl rubber, a thermoplastic elastomer, or the like. As shown in  FIG. 4 , when the intermediate layer is not formed up to the vicinity of a luer tip surface  81   b , the cap must have a thickness which ensures a sufficient gas barrier property and water vapor barrier property. 
     The medication  50  may be any of a solid preparation and a liquid solution. However, a solution that causes problems of an increase in concentration and a decrease in volume by water vapor evaporation is preferable. Among them, a solution, the quality of which degrades from the effect of oxygen, is most preferable. 
     Next, a production method for a barrel used for a prefilled syringe according to the present invention is described. As shown in  FIG. 5(   a ), first, a polyolefin resin  120  is injected from a gate  100 , provided at a position corresponding to the luer tip surface of the barrel portion of a cavity  90 , into the cavity  90  using a first injection unit  110 . 
     Then, as shown in  FIG. 5(   b ), after injecting a specific amount of the polyolefin resin  120 , a resin excelling in a barrier property  140  is injected into the cavity  90  using a second injection unit  130 . The polyolefin resin  120  which is injected first is cooled on wall surfaces of cavity mold  150  and core mold  160  to form a skin layer. The resin excelling in barrier property  140  becomes a core layer having fluidity, moving through a gap of the skin layer toward an end portion  90   a  of the cavity  90 . The amount of the polyolefin resin  120  injected first is preferably adjusted so that the proximal end  10   a  of the barrel  10  to the proximal end  30   a  of the gasket  30  is eventually filled, as shown in  FIG. 1(   a ). The reason is that the intermediate layer  17  does not necessarily have to be formed in the direction of the proximal end  10   a  of the barrel  10  from the proximal end  30   a  of the gasket  30 . 
     After injecting a specific amount of the resin excelling in barrier property  120 , the polyolefin resin  120  is injected again as shown in  FIG. 5(   c ). By pushing off an inner nozzle  131  of the second injection unit  130  toward the direction of the gate  100  as shown in  FIG. 6(   a ), the injection unit  170  and the luer tip surface  11   b  are separated as shown in  FIG. 6(   b ), thereby producing a barrel for a prefilled syringe used in the present invention. The polyolefin resin injection of a specific amount in advance may be stopped after injecting the specific amount, or the injection of the resin excelling in barrier property may be started without stopping the injection as described, for example, in U.S. Pat. No. 4,535,901 which is incorporated herein by reference. 
     A tip  131   a  of the inner nozzle  131  is preferably pushed off to come closely into contact with the luer tip surface  11   b . The reason is that by doing so, an unnecessary runner does not remain in the luer tip surface  11   b , so that adjustment of dimensional accuracy of the luer tip surface  11   b  is not required after injection molding. Further, as shown in  FIG. 7 , a valve pin  181  provided inside a valve gate  180  may be pushed off toward the direction of the luer tip surface  11   b  instead of pushing off the inner nozzle  131 . The pushing off step of the inner nozzle  131  or the valve pin  181  is preferably conducted after the luer tip surface  11   b  is coated with the polyolefin resin  120  as shown in  FIG. 5(   c ). The reason is that, as described before, the intermediate layer  17  composed of a resin excelling in barrier property  140  must not be exposed at the luer tip surface  11   b.    
     When pushing off of the inner nozzle  131  or the valve pin  181  is not conducted, a runner is formed at the luer tip surface  11   b . The runner may be cut off after taking the barrel out from the mold. 
     Next, another production method of a barrel for a prefilled syringe of the present invention is described. 
     As shown in  FIG. 8(   a ), the polyolefin resin  120  is first injected from a gate  190 , provided at a position corresponding to the center of the luer tip surface of the barrel, into a cavity  210  using a first injection unit  200 . 
     Then, as shown in  FIG. 8(   b ), after injecting a specific amount of the polyolefin resin  120 , the resin excelling in barrier property  140  is injected into the cavity  210  using a second injection unit  220 . The polyolefin resin  120  which is injected first is cooled at the wall surfaces of cavity mold  230  and core mold  240  to form a skin layer. The resin excelling in barrier property  140  becomes a core layer having fluidity and moves through the space toward the direction of an end  210   a  of the cavity  210  to eventually reach the state shown in  FIG. 8(   c ). The resin excelling in barrier property  140  does not have to fill the portion inside the luer tip  61 . The reason is that the luer tip  61  is sealed with the cap  20  or the like, so the cap  20  or the like provides a barrier property to the luer tip portion  61 . The amount of the polyolefin injected first is preferably adjusted so that the proximal end  10   a  of the barrel to the distal end  30   a  which is the expected insertion position of the gasket  30  is filled as described with reference to  FIG. 1 . 
     After injecting a specific amount of the resin excelling in barrier property  140 , the injection of the resin  140  is stopped. After taking out the molded product from the mold, an unnecessary runner is removed, thereby producing the prefilled syringe barrel of the present invention. The injection of the polyolefin resin in a specific amount in advance may be stopped after injecting the specific amount, or the injection of the resin excelling in barrier property may be started without stopping the injection. Further, if it is not desired to leave an unnecessary runner at the gate, a method using the inner nozzle or the valve gate and the valve pin, as shown in  FIG. 6  or  FIG. 7 , can be used. 
     The gate can be provided at an arbitrary position of the barrel tip surface. However, when providing the gate in a position eccentric from the center of the tip surface, a weld line appears on the cylindrical wall of the barrel located symmetric to the central axis of the gate and the barrel. This creates a risk that the intermediate layer is not formed because the second resin does not pervade through the weld line. Therefore, it is preferable to provide the gate at the center of the tip surface of the barrel by decentering the position of the luer tip when not providing a gate at the luer tip surface. 
     Further, to produce a multilayer structure having two or more layers of an intermediate layer of the barrel for a prefilled syringe of the present invention, the number of injection units may be increased to inject the successive resin after stopping the injection of the prior resin as the first resin, second resin, third resin, and so on. Alternatively, timing of the start of the injection inside the cavity may be sequentially adjusted. 
     As described above, according to the present invention, a gas barrier property and a water vapor barrier property can be imparted to a barrel for a prefilled syringe solely through a step of injecting a resin into a single mold. In other words, a gas barrier property, a water vapor barrier property, and a thermal resistance property can be easily imparted with about the same effort and time as a general production method for a syringe. In addition, an adhesive or a bonding layer does not have to be provided, and a portion in contact with a medication is totally coated with the polyolefin resin. Therefore, a risk of interaction of the medication with the barrel or elution of resin used for the barrel during sterilization or storage is low, and safety is extremely high. Further, a container itself has a barrier property, so external packaging material becomes unnecessary, contributing to a savings in resources as well as a savings in storage space, and thereby being convenient for carrying.

Technology Category: 7