Patent Document

BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The oxidative coupling reaction of 2,6-di-orthosubstituted phenols results in solutions of polyphenylene ethers (PPEs) in organic solvents. The concentration of the solution obtained varies to a certain degree, depending on the composition of the reaction mixture and on the reaction conditions. 
     2. Discussion of the Background 
     According to the current state of the art, PPE polymers are no longer precipitated out by adding a so-called anti-solvent, but are recovered by concentrating the solution. Other polymers, e.g., polystyrenes, and additives, may be optionally added in this step. It is difficult to carry out the concentration process because of the difficulty of removing residual amounts of solvents from the highly viscous solutions. If high temperatures are applied over fairly long periods, undesirable product damage occurs. 
     Indeed, the reasons for producing PPE solutions of constant concentration is to avoid having to subject the polymer to excessive thermal stressing in subsequent processing steps. 
     Various methods are known for concentrating solutions of organic plastics. For example, a flash evaporation stage may be provided and can be operated as a direct flow-through operation or in recycle. The direct or single-pass operation has the disadvantage that it accentuates variations in the concentration of the initial solution which are reflected in the concentrated solutions produced. The recycle operation requires temperatures which exceed the boiling point of the solvent at normal pressure by more than 40° C., due to the high viscosity of the PPE solutions. The long residence time of the product in the evaporator is also disadvantageous. 
     In German OS No. 31 31 440, a method is described in which other polymers, e.g., styrene polymers, are added to solutions of PPE, and the resulting mixtures are evaporated in a multistage process. A disadvantage of this process is that substantial amounts of solvent must be removed from the polymer mixture, thereby requiring apparatus of large dimensions. 
     The methods of German OS No. 33 15 802 and OS No. 33 15 803, which are improvements over the method of German OS No. 31 31 440, comprise concentrating dilute PPE solutions to at least 60% in an evaporation process, and then processing the concentrate further with addition of plastic additives and/or melts of other polymers. It is emphasized (see OS No. 33 15 802, page 8, line 25) that it is advantageous to carry out the first evaporation process in a single stage, regardless of whether the PPE solutions: 
     (i) are heated under pressure in a heat exchanger and then are depressurized; 
     (ii) are fed to a zonewise heatable dynamic thin layer evaporator; 
     (iii) are concentrated in a heatable tube assembly evaporator; or 
     (iv) are concentrated in a zonewise heatable falling film evaporator. 
     All the methods described above have the disadvantage that they either expose the PPE solution to excess thermal stressing or they produce substantial variations in the concentrations of the concentrated PPE solutions when presented with variations in concentration of the dilute starting solutions. 
     SUMMARY OF THE INVENTION 
     Accordingly, the object of the present invention is to provide a method for concentrating PPE solutions without exposing them to excessive thermal stress. 
     A further object of the invention is to provide a method for concentrating PPE solutions which produces a uniformly concentrated PPE solution from dilute starting solutions having various concentrations. 
     These objects and other objects which will become apparent from the following specification have been achieved by the surprisingly gentle method of the present invention in which one can concentrate dilute PPE solutions (5-15%) having concentrations which vary over time, to produce concentrated solutions (50-60%), by a two-stage process. 
     In a first flash evaporation stage with recycle, the concentration increases to 20-35%, and in a second direct flow trough flash evaporation stage without recycle, the desired final concentration in the range of 50-60% is reached. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings. 
     FIG. 1 illustrates a test apparatus for one- and two-stage concentrating of toluene solutions of PPE such as used in Examples 1 and A. 
     FIG. 2 is a process schematic for concentrating solutions of PPE in toluene. 
    
    
     The reference abbreviations used in the Figures are as follows: 
     B1--Reservoir 
     B2--Flash container I (operating content=10 kg). 
     B3--Condensate receiver II. 
     B4--Flash container II. 
     B5--Condensate receiver II. 
     B6--Final product container. 
     W1--Heat exchanger I (operating content=3.5 kg). 
     W2--Heat exchanger II (operating content=1.2 kg). 
     V1, V2, V3--Valves. 
     K1, K2--Containers. 
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     The starting materials are PPE solutions which are produced after the PPE polycondensation is interrupted. These solutions no longer contain catalyst. Typically, they are comprised of a PPE, i.e., a polymer of a phenol wherein the phenol is at least ortho substituted. Typically employed phenol monomers are described, for example, in German OS No. 32 24 692, OS No. 32 24 691, and OS No. 33 13 864. The subject of German OS No. 33 32 377 is a method of purifying PPEs. 
     Suitable solvents for the PPE reactions are also described in the German Patents referred to in the preceding paragraph. Toluene and toluene-methanol mixtures (with methanol content ≦30 vol. %) have proven particularly advantageous. 
     The first flash evaporation stage (FIG. 2) is comprised of an evaporator 2 to which a dilute PPE solution is continuously fed. The temperature in this first stage should be at most 20° C., preferably at most 10° C., greater than the boiling point of the solvent or the solvent mixture, in order not to subject the polymer to unnecessary thermal stress. When toluenemethanol mixtures are used, the set point temperature will be, e.g., about 115° C. 
     The contents of the evaporator are constantly recycled via a loop including the heat exchange W1 and the flash valve V1. The temperature is kept down to about 10° C. above the solvent boiling point by adjusting the recycle quantity. The concentration of PPE is continuously monitored, e.g., via the density, and is adjusted to the desired value which is between 20 and 35 wt. %. 
     The solution emerging from the first stage is fed to the single-pass evaporator 6 via the heat exchanger W2 and the flash valve V2. In the second stage the desired final concentration can be accurately adjusted by controlled heating the solution to temperatures less than 100° C. in excess of the boiling point of the solvent in exchanger W2. 
     Other features of the invention will become apparent in the course of the following description of an exemplary embodiment which is given for illustration of the invention and is not intended to be limiting thereof. 
     EXAMPLES 
     Example 1: Two-Stage Concentrating 
     In the installation illustrated in FIG. 1, the first flash container B2, is fed with 24.3 kg/hr. of a 11.2 wt. % solution of PPE in toluene, and is concentrated at 112° C. to 25.6 wt. % by continuous recycle pumping via heat exchanger W1. The resulting solution is passed through heat exchanger W2 and is then flashed in container B4 at the rate of 10.6 kg/hr. A 53.7 wt. % solution of PPE is drawn off into container B6. 
     Comparison Example A: Single-Stage Concentrating 
     The container B2 is fed with 24.0 kg of a 11.2 wt. % solution of PPE in toluene, and this solution is concentrated at 180° C. to 54.1 wt. % PPE and is then passed through heat exchanger W2 (here used as a cooler) and B4, and into container B6 at 120° C. 
     Comparison Example B: Concentrating with Two Direct FIow through Flash Stages in Series 
     The concentrating of a 11.4 wt. % toluene solution of PPE led to a final concentration of 53.9 wt. %, while a 10.1 wt. % starting solution resulted in a final concentration of 47.6 wt. %. 
     These data are evidence that concentrating in two successive single-pass flash evaporation stages leads to different final concentrations for different starting concentrations. 
     It can be seen from a comparison of Example 1 of the invention and Comparison Examples A and B that the product undergoes only minor thermal stressing in the inventive method. The method for the present invention also enables one to prescribe a specific PPE content in the concentrated solution. 
     The process comparison given in Table 1 shows that the time load on the polymer, i.e., the time at elevated temperature, with single-stage concentrating is twice that with two-stage concentrating. 
     
                                           TABLE 1__________________________________________________________________________Process Comparison                      One-stage concentrating           Inventive two-stage                      process according to           concentrating process                      German OS 33 15 802__________________________________________________________________________Feed rate to B2, Kg/hr:           24.3       24.0PPE concentration in           11.2       11.2the feed, wt. %Temperature in B2, °C.:           112        180Mean combined residence time           76         163of the PPE in B2 and W1, min:Combined residence time of           175        375longest-residing 10% ofthe PPE in B2 and W1, min:PPE concentration in B2, wt. %           25.6       54.1Feed rate to B4, kg/hr:           10.6       5.0Temperature downstream of W2,           203        120°C.:Residence time in W2, min:           7          15Temperature in B4 and B6,           120        120°C.Input rate to B6, kg/hr:           5.0        5.0PPE concentration in B6, wt. %:           53.7       54.1__________________________________________________________________________ 
    
     Obviously, numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.

Technology Category: c