Patent Document

[0001]    The present application relates to semiconductor processing technologies, and particularly to a method of annealing semiconductor wafers with rapid thermal processing.  
         BACKGROUND OF THE INVENTION  
         [0002]    In today&#39;s high speed semiconductor devices, ultra-shallow junctions, low sheet resistance and abrupt lateral junctions are vital to reduce short channel effects and to increase transistor saturation current in source drain extensions. Several techniques have been developed to deal with the issues associated with the formation of shallow, low sheet resistance junctions. Examples of these issues are transient enhanced diffusion (TED), solid solubility, and channeling, which can be resolved by using low energy implants and sharp spike anneals. During low energy implant processes, the implant energies are limited to about 1 keV or less. Thus, TED is minimized because defects caused by the implant processes are confined close to the surface. Sharp spike anneals following the implant processes provide high dopant activation and effective implant damage removal while minimizing dopant diffusion.  
           [0003]    Spike anneal is typically performed by subjecting a semiconductor wafer or substrate having implanted dopants to temperature treatment in a rapid thermal processing (RTP) system. A typical annealing profile using RTP involves ramping up to a target temperature, e.g. 1050° C., soaking the wafer at the target temperature for a period of time (soak time), and ramping down to a base temperature, e.g. 200° C. For spike anneal, high ramp rates, e.g., 75° C./sec or higher, and short (˜1 sec) or no soak time are desired to prevent excessive dopant diffusion. Besides the tight temperature control requirement, gas composition in the annealing ambient may also need to be controlled. For example, the presence of oxygen has been found to be necessary in order to decrease the evaporation or out-diffusion of implanted dopants such as boron and arsenic, but too much oxygen in the annealing ambient results in oxygen enhanced diffusion (OED). OED has been found to be a limiting factor for the creation of shallow junctions, particularly when dopants such as boron are used.  
           [0004]    Conventional spike anneal processes are typically performed at an ambient gas pressure that is comparable to atmospheric pressure. The oxygen concentration in these processes can not be accurately and dynamically controlled, due partly to the long response time for the oxygen concentration to adjust to a desired concentration level in these processes. At around atmospheric pressure, this response time may be comparable with the time a spike anneal process typically takes. For example, in a spike anneal process disclosed in U.S. Pat. No. 6,087,247, oxygen concentration has to be adjusted and stabilized before thermal processing of each wafer by first purging the RTP chamber with a process gas until the oxygen concentration in the chamber is below a threshold, and then introducing oxygen into the chamber at a controlled level. At atmospheric pressure, this process of obtaining desired oxygen concentration in an RTP chamber before thermal processing of each wafer is time consuming and can become a wafer fabrication bottleneck.  
         SUMMARY OF THE INVENTION  
         [0005]    The present invention includes a process of annealing semiconductor substrates with rapid thermal processing, in which gas pressure and gas composition in an annealing ambient is actively and dynamically controlled during thermal processing of the semiconductor substrates. In one embodiment of the present invention, a method for activating implanted dopants in a semiconductor substrate to form shallow junctions comprises placing the substrate in a thermal processing chamber and subjecting the substrate to a temperature treatment process (or thermal process) which includes a plurality of temperature ramp phases. The chamber pressure is maintained at a level lower than about 300 Torr by a closed-loop pressure control system, and a pump system is used to accelerate gas exchanges in the chamber. A transfer chamber is provided so that substrates can be transferred in and out of the processing chamber without increasing the chamber pressure and substantially changing the gas composition in the chamber. Oxygen is introduced during all or part of the thermal process, such as a fast-ramp phase of the thermal process in which substrate temperature is ramped up rapidly to a peak temperature. A volumetric flow rate at which oxygen is introduced into the processing chamber is selected such that the oxygen concentration in the processing chamber reaches a level within a range of 1500-75000 ppm before the substrate reaches the peak temperature. The volumetric flow rate of oxygen may be controlled by a closed-loop fluid control system that adjusts the volumetric flow rate of oxygen according to an oxygen concentration set point.  
           [0006]    The low gas pressure in the annealing ambient provides much faster response time in adjusting gas compositions in the annealing ambient and allows dynamic control of the gas compositions in the annealing ambient during thermal processing of the semiconductor substrates. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0007]    Additional objects and features of the invention will be more readily apparent from the following detailed description and appended claims when taken in conjunction with the drawings, in which:  
         [0008]    [0008]FIG. 1 is a diagrammatic view in vertical cross-section of a portion of an RTP system according to one embodiment of the present invention;  
         [0009]    [0009]FIG. 2 is a block diagram of a fluid control system that dynamically monitors and controls gas composition and gas pressure in a processing chamber of the RTP system;  
         [0010]    [0010]FIG. 3 is a flow diagram of a method for annealing a silicon substrate in the processing chamber of the RTP system; and  
         [0011]    [0011]FIG. 4 is a chart of a heating schedule according to one embodiment of the present invention. 
     
    
     DETAILED DESCRIPTION OF THE INVENTION  
       [0012]    The method of the present invention can be performed in an RTP system capable of maintaining gas pressure in the annealing ambient at a level significantly lower than the atmospheric pressure. An example of such an RTP system is the RADIANCE CENTURA® SYSTEM commercially available from Applied Materials, Inc., in Santa Clara, Calif. FIG. 1 illustrates a rapid thermal processing (RTP) system  10  including a processing chamber  14  for annealing a disk-shaped semiconductor substrate  12 , according to one embodiment of the present invention. Chamber  14  is radiatively heated through a water-cooled quartz window  18  by a heating lamp assembly  16 . The peripheral edge of substrate  12  is supported by a rotatable support structure  20 , which can rotate at a rate of up to about 120 rpm (revolutions per minute). Beneath substrate  12  is a nickel-plated aluminum reflector plate assembly  22  that has an optically reflective surface facing the backside of substrate  12  to enhance the effective emissivity of substrate  12 . Reflector plate assembly  22  is mounted on a water-cooled base  23 , which is typically maintained at about room temperature, e.g., 23° C. Between the top surface of reflector plate assembly  22  and the backside of substrate  12  is a reflective cavity  15 .  
         [0013]    In a system designed for processing eight inch (200 mm) silicon wafers, reflector  22  has a diameter of about 8.9 inches, the separation between substrate  12  and the top surface of reflector  22  is about 5-10 mm, and the separation between substrate  12  and the bottom surface of quartz window assembly  18  is about 25 mm. In a system designed for processing twelve-inch (300 mm) silicon wafers, reflector  22  has a diameter of about 13 inches, the separation between substrate  12  and the top surface of reflector  22  is about 18 mm, and the separation between substrate  12  and the bottom surface of quartz window assembly  18  is about 30 mm.  
         [0014]    The temperatures at localized regions of substrate  12  are measured by a plurality of temperature probes  24  that are positioned to measure substrate temperature at different radial locations across the substrate. Temperature probes  24  receive light from inside the processing chamber through optical ports  25 , 26 , and  27 , which extend through the top surface of reflector plate assembly  22 . While processing system  10  typically may have a total of ten such temperature probes, only some of the probes are shown in FIG. 1. At the reflector plate surface, each optical port may have a diameter of about 0.08 inch. Sapphire light pipes deliver the light received by the optical ports to respective optical detectors (for example, pyrometers), which are used to determine the temperature at the localized regions of substrate  12 . Temperature measurements from the optical detectors are received by a first controller  28  that controls the radiative output of heating lamp assembly  16 . The resulting feedback loop improves the ability of the processing system to uniformly heat substrate  12 .  
         [0015]    During processing, gases for the annealing ambient are introduced into processing chamber  14  through an ambient gas input  30 . The ambient gases flow across the top surface of substrate  12  and may react with a heated substrate. Excess ambient gases, as well as any reaction by-products, are withdrawn from processing chamber  14  through an ambient gas output  32  by a pump system  34 .  
         [0016]    Most of the excess ambient gases and reaction products can be pumped out of processing chamber  14 , but some volatile contaminants, especially those with relatively high vapor pressures such as BO x  and PO x , may leak into reflective cavity  15  and deposit onto the optical components situated around the reflective cavity. The rate at which volatile contaminants are deposited onto these optical components can be substantially reduced by a flow of a purge gas across the top surface of reflective plate assembly  22 . As described in commonly assigned U.S. Pat. No. 6,281,790 B1, which is incorporated herein by reference, a purge fluid injector  40  can be used to produce a substantially laminar flow of a purge gas across the top surface of reflector plate assembly  22 .  
         [0017]    The composition of the ambient gases, the flow rate of the purge gas, and the gas pressure in processing chamber  14  are controlled by a fluid control system shown in FIG. 2. In one embodiment of the present invention, the ambient gases comprise oxygen ( 02 ) and a carrier gas, such as nitrogen (N 2 ). Mass flow controllers (MFC)  81  and  80  are used to regulate the flow of the carrier gas and oxygen, respectively, into processing chamber  14 . A second feedback loop associated with processing chamber  14  controls the oxygen concentration in processing chamber. The second feedback loop includes the MFC  80 , an oxygen sensor  95  coupled to the processing chamber  14  and configured to monitor the oxygen concentration in processing chamber, and a second controller  99  coupled between the oxygen sensor  95  and MFC  80 , and configured to adjust the MFC based on an oxygen concentration set point (O 2  set point) and the oxygen concentration value detected by the oxygen sensor  95 . The second feedback loop insures that a desired O 2  concentration is maintained in processing chamber  14 , and may be used as part of a shut down mechanism associated with chamber  14  to prevent substrates from being processed in chamber  14  when the oxygen concentration cannot be regulated properly.  
         [0018]    In one embodiment of the present invention, experiments are performed to measure the O 2  concentration in process chamber  14  with different flow rates of the carrier gas and oxygen, and at different gas pressure in processing chamber  14 . Then, given the actual flow rate of the carrier gas, the gas pressure, and the desired oxygen concentration, a pre-calibrated oxygen flow rate can be determined from the experimental data by a method such as curve fitting. The pre-calibrated oxygen flow rate can be used to reduce the time taken by the second feedback loop to arrive at a desired O 2  concentration level.  
         [0019]    When a purge gas, such as nitrogen, is used to prevent deposition of volatile contaminants in the reflective cavity  15 , the purge gas is introduced into processing chamber  14  through input  46  which is connected to a filter  86 . An MFC  88  is used to regulate the flow of purge gas into processing chamber  14 . An adjustable flow restrictor  90  and a mass flow meter (MFM)  92  are used to regulate the rate at which purge gas is removed from processing chamber  14 . To reduce the migration of purge gas into the processing region of the processing chamber  14 , which is above substrate  12 , flow restrictor  90  is adjusted such that the rate at which purge gas is introduced into processing chamber  14  is substantially the same as the rate at which purge gas is removed from processing chamber  14 . Solenoid shut-off valves  94  and  96  provide additional control over the flow of purge gas through processing chamber  14 .  
         [0020]    A third feedback loop associated with chamber  14  is a closed-loop pressure control system used to regulate the gas pressure in processing chamber  14  by controlling the rate at which gases are removed from processing chamber  14 . Still referring to FIG. 2, in one embodiment of the present invention, the pressure control system comprises a pressure control valve  84  at ambient gas output  32 , a pressure gauge  98  coupled to processing chamber  14 , a programmable logic controller (PLC)  82  coupled to pressure gauge  98 , and a third controller  97  coupled between PLC  82  and pressure control valve  84 . During the operation of the processing chamber  14 , the pressure gauge  98  measures the gas pressure in processing chamber  14  periodically and sends the measured pressure value to PLC  82 . PLC  82  subtracts the measured pressure value from a pressure set point, which indicates the intended gas pressure in chamber  14 , and uses an algorithm, such as a proportional integral derivative (PID) control algorithm, to produce a control signal based on a set of tuning parameters. The control signal is then used by PLC  82  to adjust the amount of flow through pressure control valve  84 .  
         [0021]    In one embodiment of the present invention, processing chamber  14  is coupled to one or more transfer chambers (not shown), each through a load lock (not shown). The transfer chamber(s) and the associated load lock system facilitate transfers of substrates in and out of processing chamber  14  without substantially changing the gas pressure in processing chamber  14 .  
         [0022]    A semiconductor substrate  12 , after going through a dopant implant process, can be annealed in processing chamber  14  using a process  300 , as illustrated in FIG. 3, according to one embodiment of the present invention. Referring to FIG. 3, before the substrate is loaded into the chamber, processing chamber  14  is pumped down at step  301  to a pressure level substantially lower than the atmospheric pressure. Then, while the gas pressure in processing chamber  14  is maintained at step  320  at the pressure level, processing chamber  14  is purged at step  310  with a carrier gas, such as nitrogen, which is introduced into chamber  14  through MFC  81 . Other suitable carrier gases include argon, krypton, and xenon. In one embodiment of the present invention, the gas pressure in processing chamber  14  is maintained at step  320  at a level that is in the range of about 1-300 Torr, or more typically, in the range of about 5-100 Torr. The flow rate of the carrier gas during the purge step  310  is in the range of about 5-10 standard liter per minute (slm). The purging step reduces the oxygen concentration in processing chamber  14  to below a predetermined minimum value, such as 5 or 50 parts per million (ppm). The time the purging step  310  takes depends on the pressure in processing chamber  14 . In one embodiment of the present invention, when the gas pressure in processing chamber  14  is maintained at 10 Torr, it takes less than a few seconds of purging for the oxygen concentration in processing chamber  14  to drop below 5 ppm. At 100 Torr, the purging step may take about 15 seconds, which is still about 4 times quicker than purging at atmospheric pressure, as in the conventional spike anneal process. Also, purging step  310  may not need to be performed for every substrate, as explained below.  
         [0023]    Before or after the purging step  310 , substrate  12  is loaded at step  330  into processing chamber  14  from the transfer chamber, which is maintained at near vacuum and is also purged of oxygen. If substrate  12  is loaded after the purging step, a stabilization step (not shown) may be needed to allow the chamber pressure to stabilize after the loading step  330 . Once the chamber pressure is stabilized, while the carrier gas flow is maintained at a predetermined flow rate, such as 5 or 10 slm, the substrate is subjected to a thermal process at step  350 . In one embodiment of the present invention, the thermal process step  350  comprises several phases including a slow-ramp phase, a stabilization phase, a fast-ramp phase, and a cool-down phase. FIG. 4 illustrates a heating schedule of the thermal process step  350  in one embodiment of the present invention, showing changes in substrate temperature during part of the stabilization phase  420 , the fast-ramp phase  430 , and the cool-down phase  440 . During the slow-ramp phase, the substrate is heated slowly and uniformly using open-loop heating to an initial temperature of about 500-600° C. The slow-ramp phase typically takes about 10 seconds. Then the substrate is stabilized at the initial temperature during the stabilization phase  420  for less than about 5 seconds. Subsequently, during the fast ramp-up phase  430 , the substrate is heated again using closed-loop heating so that the substrate temperature rises at a rate of about 50-400° C. per second to a peak temperature of about 1000-1100° C. The substrate may be soaked at the peak temperature for a short period of time (˜0-1 second), and is then cooled down during the cool-down phase  440  so that the substrate temperature drops at a rate of about 50-400° C. per second. At the end of thermal process  350 , substrate  12  is unloaded at step  380  from processing chamber  14  and another substrate is loaded at step  330  into processing chamber  14  (if more substrates are to be processed).  
         [0024]    During or shortly before the thermal process step  350 , with the flow of the carrier gas continuing, oxygen is introduced at step  360  into processing chamber  14  at a precalibrated flow rate through MFC  80 . The pre-calibrated oxygen flow rate may depend on the gas pressure in processing chamber  14 , the flow rate of the carrier gas, and a predetermined oxygen concentration for the anneal ambient, as discussed above. The desired oxygen concentration for the anneal ambient depends on the type of dopants used, and the performance requirements of the devices being fabricated. In one embodiment of the present invention, the desired oxygen concentration in processing chamber  14  is in the range of 1500 to about 75,000 ppm, and more typically in the range of 10,000 to about 25,000 ppm. After oxygen is introduced into processing chamber  14 , the flow rate of oxygen (or the MFC  80 ) is periodically adjusted by controller  99  based on readings from oxygen sensor  95  so that the predetermined oxygen concentration value is maintained in processing chamber when oxygen in processing chamber is desired. By maintaining the gas pressure in processing chamber  14  at or below 100 Torr, the time it takes for the second feedback loop to adjust the oxygen concentration to the desired value, after a sufficient drift from that value is detected, should be less than a second. This allows accurate and dynamic control of the ambient gas composition during thermal process step  350 . The oxygen flow may be turned off at step  370  before the substrate is unloaded at step  380  from processing chamber  14 , so as to prevent the oxygen from leaking into the transfer chamber(s).  
         [0025]    Also, with the fast response provided by the low chamber gas pressure, oxygen in chamber  14  can be introduced into processing chamber  14  during a processing phase when a certain level of oxygen concentration in the annealing ambient is desired and can be turned off or down during a processing phase when oxygen is not desired. In one embodiment of the present invention, oxygen is introduced into processing chamber  14  throughout thermal process step  350 . In an alternative embodiment of the present invention, oxygen is introduced into processing chamber  14  only during certain phases of the thermal process step  350 . For example, oxygen may be introduced at step  360  into processing chamber near the time when the fast-ramp phase  430  starts and during the soak time (if there is any) in thermal process step  350 . Near the time when the substrate starts to cool down, the oxygen flow may be terminated at step  370  either by turning off the MFC  80  or by changing the O 2  set point to zero, allowing the oxygen concentration in the chamber to drop. At sufficiently low pressure, such as 5-20 Torr, the oxygen concentration may drop below the predetermined minimum value before the end of the thermal process step  350 . Considering also that oxygen is not introduced during the slow-ramp phase  410  and the stabilization phase  420  so that chamber  14  is further purged of oxygen during these phases, purging step  310  may be shortened or eliminated for the next substrate.  
         [0026]    The exact order of some of the steps in the process  300  and/or the operation of the processing chamber  14  as described above can be altered. In addition, steps may be added or omitted and process parameters varied depending upon the requirements of a particular processing application and the particular RTP system in which the annealing process takes place. The above operations and the order in which they are presented are chosen for illustrative purposes and to provide a picture of a complete run sequence.

Technology Category: 5