Patent Document

RELATED APPLICATIONS 
   Japanese application No. 2004-239090 is hereby incorporated by reference in its entirety. 
   BACKGROUND OF THE INVENTION 
   1. Field of the Invention 
   The present invention relates to a support member for semiconductor device elements and to a method for reducing instabilities in the operation of the semiconductor device elements due to mobile ions in the support member. 
   2. Description of the Related Art 
   When mobile ions, such as sodium ions, are present in a support member that supports a semiconductor device element, operation of the semiconductor device element may become unstable if the mobile ions migrate while the semiconductor device element is being operated. The following background patent documents describe methods for alleviating the operation instability of semiconductor device elements caused by movements of mobile ions in support members. These background technologies are described with reference to the following two patent documents. 
   Japanese Laid-open Patent Application HEI 7-159809 proposes a technology for stably operating a semiconductor element, or device, on a support member in which, when silicate glass containing mobile ions is used as a support member base, a high density silicon nitride layer is formed on the silicate glass to prevent infiltration of mobile ions from the support member base to the semiconductor device element. Additionally, a phosphorous silica glass film is formed on the silicon nitride layer to thereby block, trap, or fix the mobile ions with the phosphorous silica glass and reduce operation instability due to mobile ions. 
   Further, Japanese Laid-open Patent Application HEI 5-85777 proposes a technology for stably operating a thin film transistor on a support member. A phosphorsilicate glass film is grown to block mobile ions and thereby reduce operation instability due to movement of mobile ions. Additionally, a silicon oxide film that does not contain phosphorous or boron is formed on the phosphorsilicate glass film. 
   However, according to the method described in Japanese Laid-open Patent Application HEI 7-159809, a silicon nitride film and a phosphorous silica glass, both of which are electrically insulating materials, are used as support members for supporting semiconductor device elements. In other words, electrically insulating films are used as supporting members in order to block the mobile ions and thereby reduce operation instability due to mobile ions traveling from the support member to the semiconductor device elements. Therefore, there is a problem in that constituent device elements of an electronic circuit that require conductive films cannot be realized using the support members of the HEI 7-159809 patent application. For example, an electric shield film cannot be formed with insulating materials, such as a silicon nitride film or a phosphorous silica glass. Therefore, additional wiring, i.e. conductive, layers are needed to provide electric shielding. The insulating, ion barrier films of the HEI 7-159809 application also make it difficult to form capacitors using capacitive coupling between semiconductor device elements. 
   Furthermore, because silicon nitride film and phosphorous silica glass are both transparent, i.e. translucent to light, there is a problem in that, when this technology is used for optical devices, MOS transistor regions that would likely malfunction if exposed to light cannot be blocked, or shielded, from light by these films. For this reason, a separate light blocking region, or film/layer, needs to be formed, which results in an increase in the number of manufacturing steps. 
   Similarly in Japanese Laid-open Patent Application HEI 5-85777, a phosphosilicate glass film and a silicon oxide film, both of which are electrically insulating materials and translucent to light, are used as the supporting member materials. This presents problems similar to those of Japanese Laid-open Patent Application HEI 7-159809. 
   OBJECTS OF THE INVENTION 
   It is an object of the present invention to provide a support member for semiconductor device elements that suppresses operation instabilities due to mobile ions in the support member. 
   It is another object of the present invention that the support member have conductive properties and light blocking properties. 
   SUMMARY OF THE INVENTION 
   To achieve the object described above, a support member for a semiconductor device element in accord with the present invention is characterized in comprising: a second dielectric film provided below the semiconductor device element for electrically isolating the semiconductor device element; a conductive film provided below the second dielectric film that suppresses re-distribution of positively charged mobile ions present in the second dielectric film and has at least a portion capacitively coupled to the semiconductor device element; a base provided below the conductive film and formed from a conductor or a semiconductor; and a first dielectric film formed between the base and the conductive film, that electrically insulates the base from the conductive film. 
   According to this structure, a conductive film is formed to be interposed between dielectric films in the support member, such that the potential on the conductive film does not need to be set to a ground potential, and re-distribution of mobile ions can be suppressed by applying a negative potential to the conductive film to thereby attract positively charged mobile ions to the conductive film. 
   Also, a support member for a semiconductor element in accord with the present invention is characterized in comprising: a dielectric film provided below a semiconductor device element for electrically isolating the semiconductor device element; and a conductive film provided below the dielectric film and which suppresses re-distribution of positively charged mobile ions present in the dielectric film, and has at least a portion capacitively coupled to the semiconductor device element. 
   According to this structure, a conductive film is formed in the supporting member, such that the conductive film can be used as an electrical shield or the like. Also, because this film has light blocking property, malfunction of the semiconductor element which may be caused by irradiated light can be prevented. 
   Further, a support member for a semiconductor device element in accord with the present invention is characterized in that the first dielectric film consists of glass or plastic material. 
   According to this structure, transparent materials can be used as the dielectric material, such that light transmissive type devices can be readily manufactured. 
   Also, a support member for a semiconductor device element in accord with the present invention is characterized in that the second dielectric film consists of glass or plastic material. 
   According to this structure, a transparent material is formed on a conductive film, such that reflective type devices which reflect light by using the conductive film can be readily manufactured. 
   Also, the conductive film is characterized in consisting of titanium, tungsten, molybdenum, titanium nitride, tungsten nitride or molybdenum nitride. 
   According to this structure, because a high-melting point metal is used, a high-temperature treatment at 800° C. or higher that may be used in a semiconductor element manufacturing process can be applied. 
   Also, a method for driving a support member for a semiconductor device element is characterized in that, during at least a portion of a period in which a potential is applied to at least the semiconductor device element, a potential that is lower than a lowest potential applied to the semiconductor element is applied to the conductive film. 
   By this driving method, mobile ions with positive charge, such as, sodium ions or the like, can be attracted to the conductive film having a lower (i.e. relatively negative) potential, such that the mobile ions can be trapped by, i.e. fixed onto, the conductive film. For this reason, operation instability due to movement of mobile ions while semiconductor elements are operating can be reduced. 
   Other objects and attainments together with a fuller understanding of the invention will become apparent and appreciated by referring to the following description and claims taken in conjunction with the accompanying drawings. 
   BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1  is a cross-sectional view showing a supporting member for semiconductor elements. 
     FIG. 2  is a cross-sectional view showing a step in which a polycrystal silicon film is formed on the supporting member for semiconductor elements. 
     FIG. 3  is a cross-sectional view showing a step in which the polycrystal silicon film of  FIG. 2  is etched. 
     FIG. 4  is a cross-sectional view showing a state in which ion injection is conducted with the use of a resist as a mask. 
     FIG. 5  is a cross-sectional view showing a state in which an MOS transistor and a capacitor region are formed. 
     FIG. 6  is a cross-sectional view showing a step at the time when ashing is finished. 
     FIG. 7  is a cross-sectional view showing a step when metal wiring layers are formed. 

   DESCRIPTION OF THE PREFERRED EMBODIMENTS 
   A method for manufacturing a support member for supporting semiconductor device elements in accordance with an embodiment of the present invention is described below with reference to the accompanying drawings.  FIG. 1  is a cross-sectional view showing a step in a manufacturing process for a support member  100  for semiconductor devices in accordance with the present embodiment. The support member  100  for semiconductor device elements in accordance with the present embodiment preferably supports reflective type liquid crystal semiconductor device elements, and uses a conductive film  103  (i.e. a tungsten metal film) as a light reflective plate. A method for manufacturing support member  100  along with reflective type liquid crystal device elements is described below. 
     FIG. 1  is a cross-sectional view in which a conductive film  103  for trapping mobile ions, such as sodium ions, is formed over a silica glass base  101 . A support member  100  in accord with the present invention is formed in the following manner. 
   A first silicon oxide film  102 , which is a first dielectric layer, is deposited on silica glass base  101  by using a CVD process (Chemical Vapor Deposition, or chemical vapor phase growth). A tungsten film  103 , which is a conductive film, is then formed on oxide film  102  preferably by using a sputter method. A second silicon oxide film  104 , which constitutes a second dielectric film, is then formed on tungsten film  103  preferably by a CVD process. It is noted here that first silicon oxide film  102  has a preferred film thickness of 0.4 μm, tungsten film  103  has a preferred film thickness of 200 nm, and second silicon oxide film  104  has a preferred thickness of 200 nm. 
     FIG. 2  is a cross-sectional view showing a step in which a polycrystal silicon film  201  is formed on support member  100 . The polycrystal silicon film  201  is preferably formed by forming an amorphous silicon film, and then annealing the same. 
     FIG. 3  is a cross-sectional view showing a step in which the polycrystal silicon film  201  is selectively etched. To accomplish this, a resist layer  301  is first formed on polycrystal silicon film  201 . The resist  301  is then patterned using photolithography to configure resist  301  into a process mask. Then, using resist  301  as a mask, the polycrystal silicon film  201  is etched to define areas where a transistor  302  (see  FIG. 7 ) and a retention capacitor  303  (see  FIG. 7 ) are to be constructed. 
   As shown in  FIG. 4 , after removing resist mask  301  by ashing, a first plate of what will be retention capacitor  303  and source/drain regions  402  of what will be MOS transistor  302  are formed. Specifically, using as a mask a resist layer  401 , which has been patterned using a photolithography process, phosphorous ions are injected in exposed portions of polycrystal silicon film  201  to from source/drain regions  402  of MOS transistor  302  and to form a conductive plate of retention capacitor  303 . 
     FIG. 5  is a cross-sectional view showing another process step in the construction of the MOS transistor and the retention capacitor. The resist layer  401  of  FIG. 4  is removed by ashing, and then a silicon oxide film  501  is formed. Silicon oxide film  501  is later patterned to form a gate oxide for MOS transistor  302  and to form an inter-plate dielectric film for the capacitor  303 . A polycrystal silicon film  502  is then formed on silicon oxide film  501 . Polycrystal silicon  502  is later patterned to form a control gate electrode over the gate oxide of MOS transistor  302 , and to form a second conductive plate over the dielectric film of retention capacitor  303 . Then, a resist mask  503  is formed on polycrystal silicon film  502  by patterning using photolithography. It is noted that the polycrystal silicon film  502  is preferably formed by forming an amorphous silicon film containing phosphorous, and annealing the same. 
     FIG. 6  is a cross-sectional view showing a step following an ashing step to remove resist mask  503 . Using resist  503  as a mask, polycrystal silicon film  502  was etched, and after the etching was complete, the resist mask  503  was removed by ashing. At this point, a control gate  601  of MOS transistor  302  and a plate electrode  602  of retention capacitor  303  are formed. 
     FIG. 7  is a cross-sectional view showing the construction of metal wiring layers. An interlayer dielectric film  701  composed of a silicon oxide film is formed by a CVD process, contact holes are then opened in specified portions of interlayer dielectric film  701  by photolithography. Following this, an aluminum film preferably containing silicon and copper added therein is formed by a sputtering, a resist mask is then formed by photolithography, and selected regions of the aluminum film is removed as defined by the resist mask. This leaves specific areas of aluminum film, which form aluminum wiring  702 . The the resist mask is preferably removed by ashing. 
   Next, a method for driving the support member  100  with semiconductor device elements formed thereon is described with reference to  FIG. 7 . In  FIG. 7 , when the lowest potential that is applied to semiconductor device elements formed on support member  100  (such as MOS transistor  302  and retention capacitance  303 ) is 0V, a potential of −3V is applied to tungsten film  103 , which is a constituent element of support member  100 , for driving the same. 
   Because a voltage that is lower than the lowest potential of 0V applied to the semiconductor device elements is applied to tungsten film  103 , alkaline metal ions (such as sodium ions, that are mobile and positively charged and present in silica glass base  101  and silicon oxide films  102  and  104 ) migrate to tungsten film  103  (which is maintained at a lower potential of −3V ) and are trapped and fixed by the tungsten film  103 . 
   Because a method of drawing (i.e. attracting) and holding fixed (i.e. trapping) mobile ions by means of an electric field is used, mobile ions that are present not only adjacent to the tungsten film  103  that is used for trapping the mobile ions, but also mobile ions within a range in which electric lines of force of the tungsten film  103  reach can be attracted and trapped by the tungsten film  103 . Therefore, operation of the semiconductor device elements can be made more stabile as compared to the prior art case using an insulating barrier to block the penetration of mobile ions and keep them fixed to a phosphorsilicate glass. 
   Also, the tungsten film  103  is conductive. For this reason, a capacitance region can be formed with the electrode  403  laminated through the silicon oxide film  104  deposited on the tungsten film  103 . In addition to the retention capacitor formed with the electrode  403 , the silicon oxide film  501  and the electrode  602 , a capacitor is also formed with electrode  403 , silicon oxide film  104  and tungsten film  103 , such that a greater retention capacitance value can be formed within a smaller area. In the case of the presently preferred embodiment where the silicon oxide film  104  is 200 nm in thickness and the silicon oxide film  501  is 100 nm in thickness, an area necessary for obtaining an equivalent capacitance can be achieved with about 70% less area than is needed in the case where the tungsten film  103  is not present, such that the area necessary for construction a retention capacitor can be reduced. 
   Also, in accord with the present embodiment, MOS transistor  302  and other semiconductor device elements on the support member  100  are electrically shielded. For this reason, even when electric noise infiltrates due to certain factors, malfunctions of MOS transistor  302  can be effectively suppressed by the shielding effect of the tungsten film  103 . 
   Also, the tungsten film  103  is a light blocking material. Accordingly, when the tungsten film  103  is present under MOS transistor  302 , light infiltrating from the back surface of support member  100  is blocked, such that malfunctions of MOS transistor  302  caused by light, in particular, an increase in the off current accompanied with generation of carriers in the semiconductor due to light irradiation, can be prevented. 
   Effects of the embodiments are described below. 
   (1) Because the tungsten film  103 , which is a metal film having light blocking properties is used, areas of semiconductor device elements (including transistors) are shielded from light. For this reason, a leakage current due to carriers caused by light, which poses a problem especially in an OFF state, can be suppressed. 
   (2) Because the silicon oxide film  102  having few mobile ions is formed by a CVD method as a buffer layer on the silica glass base  101  that contains many mobile ions such as sodium ions, operations of the semiconductor device elements can be further stabilized. 
   (3) Because the transparent dielectric layer  104  is formed on the tungsten film  103 , which is a metal of a high light-reflecting ability, a reflective type device can be readily formed. 
   (4) Because the tungsten film  103 , which is an electrical conductor, is used for attracting and trapping mobile ions, a function of a capacitive element (such as a capacitor) and a shielding function can be obtained in addition to a gettering function for mobile ions. 
   (5) Because mobile ions are attracted and fixed by applying a negative potential to the tungsten film  103 , the mobile ions can be trapped within a range defined by the reach of electric lines of force, such that mobile ions in a greater range can be attracted and trapped, as compared to the case where a phosphosilicate glass is used for blocking infiltration (i.e. migration) by mobile ions. 
   MODIFIED EXAMPLE 1 
   Instead of using the silicate glass base  101  as a base in the present embodiment, and forming the silicon oxide film  102  thereon by a CVD method, a metal or semiconductor material may be used as a base. In particular, by using a base having a SOI (Silicon On Insulator: silicon (normally in single crystal) on a dielectric) structure, electrically excellent device characteristics can be obtained. 
   MODIFIED EXAMPLE 2 
   Instead of forming the silicon oxide film  102  as a first dielectric on the silica glass base  101  in the present embodiment, a tungsten film  103  (which is a metal film) may be formed without forming the silicon oxide film  102 . When the base is dielectric, the first dielectric film can be omitted. 
   MODIFIED EXAMPLE 3 
   Instead of forming a reflective type liquid crystal device by leaving the tungsten film  103  as a light reflecting film, the present embodiment can be applied to, for example, a light transmissive type liquid crystal device. Specifically, this can be realized by forming a tungsten film  103 , and immediately thereafter, etching the tungsten film  103  in portions where liquid crystal elements are to be formed. In this instance, by etching the tungsten film  103  while leaving portions thereof where the MOS transistor  302  and the retention capacitor  303  are present, mobile ions can be fixed, the capacitance of the retention capacitor  303  can be increased, and effects of light blocking mask can be obtained. 
   MODIFIED EXAMPLE 4 
   Instead of using the tungsten film  103  as a light reflecting film for fixing mobile ions in the present embodiment, or without limiting the subject matter to the application of tungsten for use as a light reflecting film, other metals, such as, for example, an aluminum film laminated in an upper layer can be used as a light reflecting film. 
   MODIFIED EXAMPLE 5 
   Instead of using the silicate glass base  101  as a base in accordance with the present embodiment, for example, a plastic material base can also be used. In this case, although the tungsten film  103  can be used for fixing mobile ions without a problem, a much softer metal such as aluminum may preferably be used. Also, when a plastic material substrate is used, it may be difficult to perform a high temperature treatment at 800° C. or higher. Accordingly, instead of using the polycrystal silicon film  201  as a semiconductor film, amorphous silicon may be used as a semiconductor film. 
   To recap one operation of the present invention, when the lowest operating potential that is applied to semiconductor device elements (such as transistor  302  and capacitor  303 ) on the support member  100  is 0V, a protective potential of −3V may be applied to the tungsten film  103 , which is a constituent element of support member  100 . Because the protective voltage applied to the tungsten film  103  is lower than the lowest operating potential of 0V applied to the semiconductor device elements, mobile and positively charged alkaline metal ions, such as sodium ions, present in the silica glass base  101  and in silicon oxide films  102  and  104  migrate to the tungsten film  103  due to the attractive force of the maintained lower potential, and are thereby trapped by and fixed to the tungsten film  103 . 
   While the invention has been described in conjunction with several specific embodiments, it is evident to those skilled in the art that many further alternatives, modifications and variations will be apparent in light of the foregoing description. Thus, the invention described herein is intended to embrace all such alternatives, modifications, applications and variations as may fall within the spirit and scope of the appended claims.