Patent Document

FIELD OF THE INVENTION 
       [0001]    The present invention relates to semiconductor light sources and to a method of fabricating a semiconductor light source. 
       BACKGROUND 
       [0002]    Superluminescent diodes (SLDs) and semiconductor optical amplifiers (SOAs) are opto-electronic devices that provide amplified spontaneous emission of radiation. The devices may be formed by providing a laser cavity structure defining a waveguide that is bounded at opposed longitudinal ends by low reflectivity surfaces. The reflectivity of the surfaces must be sufficiently low to suppress lasing in the cavity. 
         [0003]    K. Tateoka et al, “A High Power GaAlAs Superluminescent Diode with an Antireflective Window Structure” (IEEE J. Quantum Electronics Vol 27 No 6 June 1991 pages 1568 to 1573) discloses providing a buried twin ridge substrate (BTRS) structure as part of an SLD structure. An antireflection (AR) coating is provided at a front end of the structure. At a rear end of the structure a window region is provided. The window region is provided by etching through a portion of an active layer of the BTRS structure, forming a current blocking layer, and subsequently regrowing a GaAlAs window region. The GaAlAs window region is arranged to have a mode index to match that of the waveguide. 
         [0004]      FIG. 1(   a ) is a schematic illustration of a known semiconductor laser structure  100  having a laser cavity defined by a self-aligned stripe (SAS) structure  102 . The SAS structure  102  is bounded at opposed longitudinal ends by reflective surfaces  103 ,  104  also referred to as ‘mirrors’. 
       STATEMENT OF THE INVENTION 
       [0005]    In a first aspect of the present invention there is provided a method of fabricating a semiconductor light source structure comprising:
       providing a GaAs substrate;   forming a lower cladding layer above the substrate, the lower cladding layer comprising an Al x Ga 1-x As alloy;   forming an active region above the lower cladding layer, the active region comprising a GaAs separate confinement heterostructure;   forming an upper cladding layer comprising an Al x Ga 1-x As alloy above the active region in the form of an elongate stripe bounded on either side by a current-blocking layer comprising InGaP, the elongate stripe defining an index-guided optical waveguide,   wherein the stripe is formed such that at least one free end of the stripe is spaced apart from an edge of the substrate in a direction parallel to a longitudinal axis of the stripe such that a portion of the lower cladding layer, active region, current blocking layer and upper cladding layer extend beyond the at least one free end of the stripe thereby to provide an unpumped and laterally unguided window region.       
 
         [0011]    Embodiments of the invention have the advantage that an interface between an end of the waveguide defined by the stripe and the window region may be formed to be of very low reflectivity. In some embodiments the reflectivity is of the order of 10 −7 . 
         [0012]    Embodiments of the invention have the further advantage that during a process of fabricating the structure an Al-containing layer need not be exposed to atmosphere or any other environment leading to oxidation of the Al-containing layer. Thus a reliability of a process of fabricating structures according to embodiments of the invention is enhanced relative to a process in which exposure of Al-containing layers to atmosphere takes place. 
         [0013]    Furthermore, a process of fabricating a structure according to an embodiment of the invention may be completed in a lower number of steps compared with a process according to some embodiments of the invention. This is because separate growth steps are not required for the window region and the active region. Rather, the portions of the structure defining the active region, lower cladding layer, current blocking layer and upper cladding layer extend laterally and continuously into the window region in an uninterrupted manner. This feature allows a further reduction in reflectivity at the interface between the active region (and the lower and upper cladding layers) and the window region. 
         [0014]    The at least one free end of the stripe may be formed to be substantially flat as viewed in plan view. The at least one free end may be substantially planar, optionally provided in a substantially vertical plane. 
         [0015]    Alternatively the at least one free end of the stripe may be formed to be tapered in plan view. 
         [0016]    Providing a tapered stripe allows a further reduction in reflectivity of the interface between the stripe and the window region by allowing an optical mode propagating along the stripe to leak out from the stripe. 
         [0017]    The at least one free end of the stripe may be formed to be substantially V-shaped in plan view. 
         [0018]    The method may comprise the step of cleaving the structure parallel to a crystallographic facet thereby to define a free end of the stripe. Alternatively the method may comprise etching a portion of the stripe thereby to define a free end of the stripe. Etching of the stripe may be performed whereby a surface exposed by the etching process is sufficiently rough to reduce a reflectivity of the surface compared with a perfectly flat surface. 
         [0019]    The method may comprise the step of forming the stripe whereby an angle between a longitudinal axis of the stripe and a plane defining the free end of the stripe is greater than 90° thereby to reduce an amount of light propagating along the stripe that is reflected at the free end back along the stripe. 
         [0020]    The stripe may be formed such that each of two free ends of the stripe are spaced apart from an edge of the substrate whereby an unpumped and laterally unguided window region is provided at each end of the stripe. 
         [0021]    The method may comprise the step of forming a plurality of electrical contacts along at least a portion of a length of the stripe thereby to allow different respective potentials to be applied to the stripe at different respective longitudinal positions. 
         [0022]    Preferably the step of forming the upper cladding layer is preceded by the step of forming an etch stop layer above the active region. 
         [0023]    Preferably the step of forming the upper cladding layer is preceded by the step of forming the InGaP current blocking layer and etching the current blocking layer to form a trench, subsequently filling the trench with AlGaAs alloy thereby to form the elongate stripe. 
         [0024]    Preferably a refractive index of the AlGaAs filling the trench is arranged to be greater than a refractive index of the current blocking layer. 
         [0025]    Thus, in the case that the current blocking layer comprises InGaP, the refractive index of the Al x Ga 1-x As may be arranged to be greater than that of InGaP. The refractive index of InGaP is around 3.25. The refractive index of Al x Ga 1-x As may be arranged to be up to around 3.5 or more depending on the value of x. 
         [0026]    Alternatively a refractive index of the AlGaAs filling the trench may be arranged to be less than a refractive index of the current blocking layer. 
         [0027]    In this case an optical mode propagating parallel to the stripe experiences anti-guiding. 
         [0028]    x may be from around 0.1 to around 0.9, optionally from around 0.15 to around 0.8, further optionally from around 0.35 to around 0.5, still further optionally from around 0.4 to 0.44, optionally around 0.42. 
         [0029]    In a second aspect of the invention there is provided a semiconductor light source structure comprising:
       a GaAs substrate;   a lower cladding layer above the substrate, the lower cladding layer comprising an Al x Ga 1-x As alloy;   an active region above the lower cladding layer, the active region comprising a GaAs separate confinement heterostructure;   an upper cladding layer comprising an Al x Ga 1-x As alloy above the active region in the form of an elongate stripe bounded on either side by an InGaP current-blocking layer, the elongate stripe defining an index-guided optical waveguide,   wherein the stripe is arranged wherein at least one free end of the stripe is spaced apart from an edge of the substrate along a direction parallel to a longitudinal axis of the stripe such that a portion of the lower cladding layer, active region, current blocking layer and upper cladding layer extend beyond a free end of the stripe thereby to provide an unpumped and unguided window region.       
 
         [0035]    The at least one free end of the stripe may be formed to be substantially flat as viewed in plan view. 
         [0036]    Alternatively the at least one free end of the stripe is formed to be tapered in plan view. 
         [0037]    The at least one free end of the stripe may be formed to be substantially V-shaped in plan view. 
         [0038]    A free end of the stripe may be defined by a crystallographic facet. 
         [0039]    The stripe may be formed such that an angle between a longitudinal axis of the stripe and a plane of the facet defining the free end of the stripe is greater than 90° thereby to reduce an amount of light propagating along the stripe that is reflected by the facet back along the stripe. 
         [0040]    The stripe may be formed such that each of two free ends of the stripe are spaced apart from an edge of the substrate whereby an unpumped and unguided window region is provided at each end of the stripe. 
         [0041]    The structure may comprise a plurality of electrical contacts along at least a portion of a length of the stripe, the contacts being arranged to allow different respective potentials to be applied to the stripe at different respective longitudinal positions. 
         [0042]    x may be from around 0.1 to around 0.9, optionally from around 0.15 to around 0.8, further optionally from around 0.35 to around 0.5, still further optionally from around 0.4 to 0.44, optionally around 0.42. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0043]    Embodiments of the invention will now be described with reference to the accompanying figures in which: 
           [0044]      FIG. 1  shows (a) a prior art self-aligned stripe semiconductor laser structure and (b) to (e) structures according to embodiments of the present invention; 
           [0045]      FIG. 2  is a cross-sectional view of a structure according to an embodiment of the invention; 
           [0046]      FIG. 3  shows (a) a portion of the structure of  FIGS. 1(   c ) and (b) a cross-section through (a) along line X-X; 
           [0047]      FIG. 4  shows an end portion of the structure of  FIG. 1(   b ) showing a wavefront propagating from a waveguide defined by a stripe portion propagating from the stripe portion into a window region; and 
           [0048]      FIG. 5  shows a schematic plan view of a structure according to an embodiment of the invention having a plurality of electrical contacts formed over a stripe portion of the structure. 
       
    
    
     DETAILED DESCRIPTION 
       [0049]    In one embodiment of the invention a structure  200  is provided as shown in  FIG. 1(   b ). The structure is similar to that of the known self-aligned stripe (SAS) semiconductor laser structure  100  of  FIG. 1(   a ) in that it has a self-aligned stripe portion  202  terminated at one end by a cleaved surface  203 . However, in the structure of  FIG. 1(   b ) one free end  202 F of the stripe portion  202  terminates within the lateral boundaries of the structure  200  whereby a window region  250  is provided between that free end  202 F and a further cleaved facet  204  at an edge of the structure  200 . 
         [0050]      FIG. 2  shows a cross-sectional view of the structure  200  of  FIG. 1(   b ) along line X-X. 
         [0051]    An example of a method of fabrication of the structure  200  will now be described with reference to  FIG. 2 . 
         [0052]    In the present example a substrate  210  formed from n-doped GaAs (n-GaAs) was provided. Above the substrate a lower cladding layer  212  was formed from Al x Ga 1-x As 1500 nm in thickness. In the present embodiment the layer was of composition Al 0.42 Ga 0.58 As. Other compositions of Al x Ga 1-x As are also useful. 
         [0053]    A double quantum well (DOW) separate confinement heterostructure (active region)  215  was then provided above the lower cladding layer  212 . The active region  215  comprised two In 0.17 Ga 0.83 As quantum wells  217  separated by a 20 nm thick layer of GaAs, the wells  217  being sandwiched between first and second layers of GaAs to provide an active region having a total thickness of 100 nm. Other compositions of In x Ga 1-x As are also useful for forming the quantum wells  217 . 
         [0054]    Above the active region  215  a p-doped layer of Al 0.42 Ga 0.58 As  220  was formed. The layer  220  was formed to be 300 nm in thickness and doped with Zn to a concentration of 5×10 17 cm −3  thereby to complete a p-i-n structure  221  in which the intrinsic region was provided by the active region  215 . 
         [0055]    Above the p-doped layer  220  an etch-stop layer  222  formed from GaAs was provided. The etch-stop layer  222  was formed to have a thickness of around 10-20 nm. Other thicknesses of GaAs providing a suitable etch stop layer are also useful. 
         [0056]    A layer of InGaP  224  600 nm in thickness was formed over the etch-stop layer  222 . A mask layer  226  was then formed over the InGaP layer  224 , the mask layer  226  being formed from a layer of GaAs 10 nm in thickness. 
         [0057]    To form the self aligned stripe, the mask layer  226  was patterned and wet chemically etched ex-situ to form a narrow stripe (in the form of a trench) parallel to major flat ( 110 ). Etching was performed first with C 6 H 8 O 7 /H 2 O 2  to selectively etch the mask layer  226 , then H 3 PO 4 /HCl to selectively etch the InGaP layer  224  to expose the GaAs etch-stop layer  222  at the bottom of the trench. 
         [0058]    It is to be understood that no AlGaAs is exposed during the course of the etch process. 
         [0059]    Other methods of etching are also useful including dry etching. 
         [0060]    A layer of GaAs  228  was then formed (or ‘regrown’) over the mask layer  226 . Prior to growth of the GaAs layer  228  the wafer was cleaned in 1% buffered HF. 
         [0061]    The low pressure regrowth process was performed by rapidly ramping a temperature of the structure to 690° as measured by an EpiTT pyrometer in an arsine mole fraction of 7.5×10 −3  before growth of the GaAs layer  228  (C-doped from 5×1017 cm −3 ). 
         [0062]    An upper cladding layer  230  of Al 0.42 Ga 0.58 As (C-doped from 5×10 17  to 1×10 18  cm −3 ) 1000 nm in thickness was formed over the regrown GaAs layer  228 , followed by a contact layer  232  being a layer of GaAs (C-doped, 2×10 19 cm −3 ) 20 nm in thickness. 
         [0063]    A AuZnAu contact metallisation was then deposited over the structure and annealed at 360°. The substrate  210  was then thinned and InGeAu back contacts deposited and annealed at 340° C. 
         [0064]    It is to be understood that other methods of fabricating structures according to embodiments of the invention are also useful. 
         [0065]    It is to be understood that the structure provides a p-i-n diode in a direction vertically through the structure in the region of the stripe portion  202 . The upper cladding layer  230  provides a portion of the p-doped region, the active region  215  provides the intrinsic region and the lower cladding layer  212  provides the n-doped region of the p-i-n structure. 
         [0066]    It is to be understood that a p-n-p-n current blocking structure is provided either side of the stripe region  202 . Refractive index contrast between the p-i-n structure and p-n-p-n structure confines the optical mode to the active region below the stripe during propagation of the optical mode along the waveguide defined by the stripe region  202 . 
         [0067]    As stated above, in the structure  200  of  FIG. 1(   b ) the self-aligned stripe portion  202  is not terminated at each end by a cleaved facet  203  at a free edge  210 F of the substrate as in the case of the structure of  FIG. 1(   a ) (see corresponding free edge  110 F). Rather, one free end  202 F of the stripe portion  202  terminates within the lateral boundaries of the structure  200  whereby a window region  250  is provided between that free end  202 F and cleaved facet  204 . 
         [0068]      FIG. 3(   a ) reproduces a portion of  FIG. 1(   c ) and  FIG. 3(   b ) shows a cross-sectional view of the structure of  FIG. 3(   a ) along line Y-Y. A cross-sectional view of the structure of 
         [0069]      FIG. 3(   a ) along line X-X is as shown in  FIG. 2 . 
         [0070]    It can be seen from  FIG. 3(   b ) that the window region  250  is a region of the structure  200  which is electrically unpumped and laterally unguided. The window region  250  is unpumped because electrically the structure provides a p-n-p-n structure rather than a p-i-n structure. The window region  250  is laterally unguided because the region  250  is formed substantially entirely from the p-n-p-n structure not having a variation in composition in a lateral direction. 
         [0071]    Light propagating through the window region  250  is not amplified. Rather, the optical mode spreads out due to diffraction and is partially reflected at end facet  204 . Because the active region  215  (being an optical gain region) is not removed from the window (but is simply not electrically pumped due to the presence of the current blocking layer) the window  250  is light-absorbing. 
         [0072]    Calculations of an effective refractive index n eff  of structures according to the embodiments of  FIG. 1(   b ) to ( e ) give a value of 3.284 for a structure with a stripe portion 3 um in width and a value of 3.281 for a structure with no stripe (e.g. window region  250 ). Thus, a reflectivity R of an abrupt free end  202 F of a stripe portion  202  at an interface between the stripe portion  202  and window region  250  may be estimated to be ˜10 −7 . This represents an improvement of around two orders of magnitude over existing low reflectivity facet technologies. 
         [0073]      FIG. 4  shows the structure of  FIG. 1(   b ) in which an optical wavefront is propagating along the structure  200 . At position A the wavefront is propagating left to right along the waveguide defined by the stripe portion  202 . At position B the wavefront has exited the stripe portion  202  and is propagating through the window region  250 . As discussed above, in the window region  250  the wavefront is unguided and the device unpumped. The wavefront spreads out due to diffraction and is to a certain extent absorbed by the window region  250 . 
         [0074]    A portion of the light passing left to right along the window region  250  is reflected by end facet  204  and propagates back along the structure  200  from right to left where it continues to spread out. It can be seen that only a small proportion of the reflected wavefront propagating back along the structure at position C is within the pumped stripe portion  202 . Thus a contribution of this wavefront to stimulated emission within the pumped region is small. This reduces a risk that lasing is established in the stripe portion  202 . 
         [0075]    In some embodiments, the free end  202 F of the stripe portion  202  is tapered thereby further reducing a reflectivity of the free end  202 F.  FIG. 1(   c ) shows such an embodiment in which a stripe region  302  has a tapered free end  302 F. Tapering of the stripe region  302  allows the optical mode to leak out from the waveguide defined by the stripe portion  302  further reducing an amount of coupling back into the waveguide. The tapered structure also offers reduced far-field divergence, improving fibre coupling efficiency. 
         [0076]    In the embodiment of  FIG. 1(   d ) the stripe portion  402  is tilted through an angle θ (i.e. rotated about an axis normal to a plane of substrate  410 ) in order to reduce a reflectivity of end facet  403 . In the embodiment of  FIG. 1(   e ) the stripe portion  502  is tilted and provided with a taper at both free ends  502 F,  502 F′. Corresponding window regions  550 ,  550 ′ are provided at each end of the stripe portion  502 . 
         [0077]    It is to be understood that in some embodiments in which long window regions are provided a coupling efficiency of the structure to an optical fibre may be degraded. 
         [0078]    In some embodiments an anti-reflection (AR) coating is provided on an exposed facet  203 ,  204  of a structure in order to further reduce a reflectivity of the facet. The facet  203 ,  204  may be a facet at an edge of a window region  250  or a stripe portion  202 . 
         [0079]    In some embodiments the window is arranged to be a substantially ‘infinitely long absorber’. By infinitely long absorber is meant that a product of an absorption coefficient α of the window region and a length of the window region L is much greater than 1, αL&gt;&gt;1. 
         [0080]    In some embodiments of the invention a reflectivity of end facets of the structure (and of one or both free ends of the stripe region within the structure depending on whether one or both free ends of the stripe terminate within the structure) is sufficiently low to allow the stripe to be fabricated parallel to a crystallographic axis or major crystallographic axis of the substrate (i.e. the stripe is untilted, θ being substantially zero, see  FIG. 1(   d )). This has the advantage that a yield of devices may be increased compared with tilted waveguide devices. 
         [0081]    Embodiments of the present invention have the advantage that an SLD or SOA device may be formed having a window region having a reduced reflectivity. Furthermore embodiments of the invention allow a GaAs-based device to be fabricated in which exposure of Al-containing layers to atmosphere during a course of fabricating the device may be avoided. Thus, a reliability of a manufacturing process of an SLD or SOA structure is greatly enhanced. Some embodiments of the present invention allow the number of processing steps required to provide a SLD or SOA device to be reduced relative to prior art SLD or SOA devices. 
       EXAMPLE 
       [0082]    An SLD device according to the embodiment of  FIG. 1(   b ) was fabricated having an emission wavelength centred at around 1060 nm. The SLD device was 4 mm long. The stripe portion of the structure had a cleaved facet at one end and a window region 500 um long at the other end. No lasing was observed even at a current flow of 1 A indicating the effectiveness of the window structures of embodiments of the present invention. 
         [0083]      FIG. 5  shows a structure according to an embodiment of the invention in which contact layer  632  has been etched to allow multiple mutually isolated contacts to be formed along a length of the stripe portion  602 . This allows different potentials to be applied to different regions as appropriate in order to optimise a performance of the structure. 
         [0084]    In some embodiments one or more contacts may be reverse biased in order to increase an absorption of one or more sections of the structure. In some embodiments a contact  632  is provided above a portion of the window region  650 . 
         [0085]    In some embodiments the contacts are defined by implantation into a contact layer  232  rather than by etching of the contact layer  232 . 
         [0086]    Throughout the description and claims of this specification, the words “comprise” and “contain” and variations of the words, for example “comprising” and “comprises”, means “including but not limited to”, and is not intended to (and does not) exclude other moieties, additives, components, integers or steps. 
         [0087]    Throughout the description and claims of this specification, the singular encompasses the plural unless the context otherwise requires. In particular, where the indefinite article is used, the specification is to be understood as contemplating plurality as well as singularity, unless the context requires otherwise. 
         [0088]    Features, integers, characteristics, compounds, chemical moieties or groups described in conjunction with a particular aspect, embodiment or example of the invention are to be understood to be applicable to any other aspect, embodiment or example described herein unless incompatible therewith.