Patent Document

FIELD OF THE INVENTION 
     The present invention generally relates to magnetic recording heads and, in particular, relates to reducing the thermal protrusion of a near field transducer (NFT) in an energy-assisted magnetic recording (EAMR) head. 
     BACKGROUND OF THE INVENTION 
     To increase the areal storage density of a magnetic recording device, the recording layer thereof may be provided with smaller and smaller individual magnetic grains. This reduction in grain size soon reaches a “superparamagnetic limit,” at which point the magnetic grains become thermally unstable and incapable of maintaining their magnetization. The thermal stability of the magnetic grains can be increased by increasing the magnetic anisotropy thereof (e.g., by utilizing materials with higher anisotropic constants). Increasing the magnetic anisotropy of the magnetic grains, however, increases their coercivity and therefore requires a stronger magnetic field to change the magnetic orientation of the grains (e.g., in a write operation). 
     Energy-assisted magnetic recording (EAMR) is used to address this challenge. In an EAMR system, a small spot where data is to be written is locally heated to reduce the coercivity of the magnetic grains therein for the duration of the write operation, thereby allowing materials with increased magnetic anisotropy to be used, and greater areal storage density to be exploited. 
     To reduce the size of the spot which is heated, a near field transducer (NFT) is used to concentrate optical energy in the near field to dimensions much smaller than the diffraction limit would otherwise allow. With a NFT, a nano-sized spot can be heated to assist the magnetic writing on the magnetic media. Due to the less-than-ideal NFT conversion efficiency, some of the optical energy provided on the NFT is absorbed by the materials near an air-bearing surface (ABS) surrounding the NFT, and heat-related protrusion and of the NFT and the surrounding materials may occur. 
     SUMMARY OF THE INVENTION 
     Various embodiments of the present invention solve the foregoing problem by modifying the ABS of the EAMR head to compensate for the NFT protrusion, thereby preventing protrusion-related damage to the NFT which may occur. These approaches provide a reliable method of forming EAMR heads without the aforementioned problems, and can greatly enhance reliability of the EAMR heads. 
     According to one embodiment of the subject disclosure, a method of fabricating an energy assisted magnetic recording (EAMR) head to compensate for a heat-induced protrusion of a near field transducer formed therein can comprise applying optical power to the near field transducer to generate heat therein, whereby the near field transducer protrudes beyond an air bearing surface of the EAMR head. The method can further include removing a protruded portion of the near field transducer. 
     According to another embodiment of the subject disclosure, an energy assisted magnetic recording (EAMR) head is provided. The EAMR head can comprise a slider having a leading edge, a trailing edge, and an air bearing surface (ABS). The EAMR head can further comprise a near field transducer disposed in the slider and having a distal end proximate the ABS. The distal end of the near field transducer is recessed from the ABS when no optical power is applied to the near field transducer, and is co-planar with the ABS when a predetermined amount of optical power is applied to the near field transducer. A portion of the slider surrounding the distal end forms a concave surface having a continuously varying slope when no optical power is applied to the near field transducer, and a flat surface coplanar with the ABS and the distal end of the near field transducer when the predetermined amount of optical power is applied to the near field transducer. 
     It is to be understood that both the foregoing summary of the invention and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The accompanying drawings, which are included to provide further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and together with the description serve to explain the principles of the invention. In the drawings: 
         FIG. 1  is a schematic diagram illustrating an exemplary EAMR head comprising a slider and a near field transducer according to one aspect of the subject technology; 
         FIG. 2  is a graph showing a simulated trace of a heat-induced protrusion according to one aspect of the subject technology; 
         FIG. 3  is a flowchart illustrating an exemplary iterative heat-and-remove process for producing an EAMR head according to one aspect of the subject technology; 
         FIG. 4A  is a cross-sectional views of a slider having a NFT modified by an iterative heat-and-remove process according to one aspect of the subject technology when no optical power is applied to the NFT; and 
         FIG. 4B  is a cross-sectional views of a slider having a NFT modified by an iterative heat-and-remove process according to one aspect of the subject technology when an operational optical power is applied to the NFT. 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     In the following detailed description, numerous specific details are set forth to provide a full understanding of the present invention. It will be apparent, however, to one ordinarily skilled in the art that the present invention may be practiced without some of these specific details. In other instances, well-known structures and techniques have not been shown in detail to avoid unnecessarily obscuring the present invention. The word “exemplary” is used herein to mean “serving as an example, instance, or illustration.” Any embodiment or design described herein as “exemplary” is not necessarily to be construed as preferred or advantageous over other embodiments or designs. 
       FIG. 1  is a schematic diagram illustrating an exemplary EAMR head  100  comprising a slider  101  and a near field transducer  158  according to one aspect of the subject technology. The slider  101  comprises a substrate  110 , a recorder/reader layer  120  disposed over the substrate  110 , and an overcoat layer  130  disposed over the recorder/reader layer  120 . In the illustrated example, the substrate  110  comprises AlTiC and the overcoat layer  130  comprises alumina. The slider  101  has a leading edge  107  and a trailing edge  109 , and an air-bearing surface (ABS)  105  facing a magnetic recording medium  103 . The recorder/reader layer  120  of the slider  101  includes a writer  122  for recording or erasing information on the medium  103  by focusing a magnetic field on a spot on the medium  103 , a coil  124  for generating the magnetic field, a reader  126  for reading a magnetic bit recorded on the medium  103 , and a waveguide structure  150 . The waveguide structure  150  is configured to couple incident laser beam  171  from a laser diode  102  into a waveguide core layer  154  disposed in the coupler  150 . The waveguide structure  150  includes a first clad layer  152  and a second clad layer  156  surrounding the waveguide core layer  154 . Disposed at an interface between the second clad layer  156  and the waveguide core layer  154  is a grating  128  having a period and a depth selected to couple incident laser beam  171  into waveguide core layer  154 . The waveguide structure  150  further includes a near field transducer (NFT)  158  formed at a distal end of the waveguide structure  150  proximate the ABS  109 . The NFT  158  is configured to concentrate energy from the laser beam to a nano-sized spot on the recording medium  103  well below the so-called “diffraction limit” imposed on standard focusing lenses. The NFT  158  is typically formed of a metal such as gold (Au), silver (Ag), aluminum (Al), copper (Cu), or a combination (alloy) thereof. 
     The EAMR head  100  can also includes a laser diode  102  configured to generate a laser beam in response to an electrical power applied thereto. In certain embodiments, the laser diode is affixed to the slider  101 . In some embodiments, the laser diode can be a vertical-cavity-surface-emitting laser (VCSEL). In other embodiments, the laser diode  102  can be a separate structure disposed at a certain distance from the slider  101  and transmitting light to the waveguide structure  150  via an airgap. 
     During the operation of a hard disk drive comprising the EAMR head  100 , the magnetic recording medium  103  rotates at high speed, and air flowing at high speed between the ABS  105  and the magnetic recording medium  103  provides an upward force to the slider  101  such that the slider  101  is maintained at a certain height from the magnetic recording medium  103 . A portion of the incident laser beam  171  emitted by the laser diode  102  and arrived at the waveguide structure  150  is coupled into the waveguide core layer  154  by means of the grating  128  to form a coupled laser beam  172  traveling down the waveguide core layer  154  toward the ABS  105 . The coupled laser beam  172  is concentrated onto a nano-sized spot on recording medium  103  by means of the NFT  158 . The nano-sized heated spot on the magnetic medium  103  is subsequently subjected to a pulse of write magnetic field from the writer  122 . 
     Viewed from the perspective of a power flow, a portion of an electrical energy provided to the laser diode  102  is converted into an incident optical power by the laser diode  102  in the form of the incident laser beam  171 . A portion of the incident optical power is coupled into the waveguide core layer  154  as a coupled optical power in the form of the coupled laser beam  172 . A portion of the coupled optical power is transmitted to the magnetic recording medium  103  as near field radiation  173 , which is absorbed by a nano-sized spot on the magnetic recording medium  103  to generate heat therein. 
     Typically, an optical conversion efficiency of the NFT  158 —the percentage of the coupled optical power converted into the focused optical power using the above-defined terminologies—is in the range of 1-10%. A portion of the coupled optical power not converted into the focused optical power generates heat at the NFT and a surrounding region. The heat at NFT  158  and the surrounding portion of the slider may cause the region to protrude above the ABS  105 .  FIG. 2  is a graph showing a simulated trace  201  of such a heat-induced protrusion as a function of a distance measured from the left edge of the substrate  110  ( FIG. 1 ), with the + direction being towards the trailing edge  109  of the slider  101 . The trace  201  shows a sharp protrusion at a region comprising the NFT and a portion of the slider surrounding the NFT, with its peak occurring at the center of the NFT. This simulation is performed with the assumption that 20 mW of optical power is applied to a volume of 273 nm×180 nm×100 nm at the write gap (WG). It can be seen that the protrusion is very localized due to the small size of the heat source. In the simulation embodiment, the maximum protrusion beyond the ABS is seen to be 50 nm at 20 mW. Even if the optical power is reduced by half, e.g., to 10 mW, the NFT protrusion above the ABS is still in the range of 20-30 nm. Considering that the slider can float at a height in the range of few nanometers above the magnetic recording medium, such a heat-induced NFT protrusion may result in the chipping or cracking of the NFT and damage to the recording media. 
     To reduce or eliminate such a heat-induced NFT protrusion, a fabrication process of the EAMR head can be configured to modify a shape of a region of the ABS surrounding the NFT to compensate for the heat-induced NFT protrusion, according to one aspect of the subject technology. In particular, the process can involve iteratively applying increasingly larger levels of optical power to the NFT, thereby generating heat in the NFT and the surrounding region, and removing a corresponding heat-induced protrusion at the NFT and the surrounding slider portion.  FIG. 3  is a flowchart illustrating an exemplary iterative heat-and-remove process  300  for producing an EAMR head. The iterative heat-and-remove process  300  begins at state  310  and proceeds to a state  320 , in which a first level of optical power (P opt ) is applied to the NFT. As explained above, the optical power is delivered to the NFT in the form of a laser light (e.g., the coupled laser beam  172  of  FIG. 1 ), and the optical power generates heat in the NFT and a surrounding portion of the slider. The laser light and its associated optical power can be coupled from a laser source (either affixed to the slider or separate) into a waveguide (e.g., the waveguide structure  150  of  FIG. 1 ) formed in the EAMR head and directed to the NFT. Alternatively, the laser light can be applied directly to the NFT from an external laser source during the fabrication process. Regardless of the chosen channel, the first level of optical power carried by the laser light generates heat at the NFT, which heat, in turn, induces a first localized protrusion in a region comprising the NFT and the surrounding slider portion as described above. 
     The process  300  proceeds to a state  330 , in which the first localized protrusion is removed by, e.g., a bar lapping process. In one embodiment, the bar lapping process is a chemical-mechanical polishing (CMP) process. In certain embodiments, the removal process is performed while a constant optical power is applied to the NFT. In other embodiments, the optical power is increasing while the removal process is in progress. In yet other embodiments, the optical power is temporarily turned off during the removal process. The process  300  proceeds to a decision state  340 , in which a query is made as to whether P opt  has reached a preset final optical power. In certain embodiments, the preset final optical power corresponds to an operational level of optical power for use during a recording operation of the EAMR head. In other embodiments, the preset final optical power can be a level of optical power different from the operational level due to the need to compensate for a thermal variation caused by the removal process or due to the fact that the optical power is being delivered by an external laser source during the fabrication process in which case the optical power required to produce the same amount of heat at the NFT may be different from the operational optical power delivered via the waveguide structure. 
     If the answer to the query at the decision state  340  is YES, the process  300  ends at state  390 . On the other hand, if the answer is NO, the process  300  continues at a state  350 , in which the optical power is increased to a next level, and then proceeds to the state  320 , in which the next level of optical power is applied to the NFT. The next level of optical power generates a next level of heat at the NFT, which heat, in turn, induces a next localized protrusion in the region comprising the NFT and the surrounding slider portion. The next localized protrusion is removed at the state  330 . The heat-and-remove process of the states  320 ,  330 ,  340 , and  350  is repeated until the optical power has reached a preset final optical power. 
     It shall be appreciated that many variations to the iterative heat-and-remove process  300  described above are possible without departing from the scope of the present disclosure. For example, in those embodiments in which a constant or increasing optical power is applied during the removal process, the states  320  and  330  may be combined into a single state, in which the localized protrusion is removed while the constant or increasing optical power is applied to the NFT. In the latter case in which the optical power is increased during the removal process, the state  350  may not be performed as a separate step. The iterative heat-and-remove process  300  described above is terminated when the optical power reaches a preset final optical power. For example, according to one aspect of the subject technology, the process may complete after a preset number of steps (e.g., 10 of 2 mw increments for an exemplary final optical power of 20 mw). Alternatively, the process may be terminated after a certain other condition is satisfied. For example, the temperature of the ABS near the NFT can be measured by a contact or remote measurement method, and the process can be terminated when the measured temperature reaches a preset final temperature. 
     An iterative heat-and-remove process such as the one described above with respect to  FIG. 3  is superior to a single (non-iterative) heat-and-remove process in which a preset maximum optical power is applied to the NFT and the corresponding heat-induced protrusion is removed in a single step, because such a single heat-and-remove process can lead to an abrupt breakage in the NFT protrusion and cause an attendant damage to the NFT during the removal process. By iteratively applying increased levels of heat to the NFT and removing corresponding incremental protrusions, the iterative heat-and-remove method described herein can prevent breakage of the NFT and also produces a smooth surrounding concave surface in the slider at the end of the removal process.  FIGS. 4A and 4B  are cross-sectional views of a slider  401  having a near field transducer (NFT)  410  modified by an iterative heat-and-remove process such as the one described above.  FIG. 4A  corresponds to a case in which no optical power is applied to the NFT  410 , and  FIG. 4B  corresponds to a case in which an operational optical power (e.g., the optical power to be used during a recording operation) is applied to the NFT  410 . The shown section of the slider  401  has an ABS  405 . The NFT  410  has a distal end  412  proximate the ABS  405 . The distal end  412  of the NFT  410  is recessed from the ABS  405  when no optical power is applied to the NFT  410  as shown in  FIG. 4A , and is co-planar with the ABS  405  when a predetermined amount of optical power (e.g., an operational optical power) is applied to the NFT  410  as shown in  FIG. 4B . A portion of the slider  401  surrounding the distal end  412  of the NFT  410  forms a concave surface  430 A having a continuously varying slope when no optical power is applied to the NFT  410  as shown in  FIG. 4A , and a substantially flat surface  430 B coplanar with the ABS  405  and the distal end  412  of the NFT  410  when the predetermined optical power is applied to the NFT  410 . As shown in  FIG. 4A , for example, there is a smooth transition from the ABS  405  to the concave surface  430 A without a sharp edge such as a 90-degree bend. Similarly, there is a smooth transition from the concave side surface to the bottom of the recess without a sharp edge such as a 90-degree bend. Put another way, a region  407  comprising the concave surface  430 A and its surrounding ABS portion has a continuously-varying slope (e.g., continuously differentiable without a discontinuity). 
     A recess having such a smooth surface with a continuously-varying slope caused by the iterative heat-and-remove process described herein has several advantages over a recess having sharp 90-degree edges at the top and bottom of the recess. For example, the smooth surface reduces the risk of having debris particles stuck in the recess after the fabrication and causing aberrations (e.g., absorption, attenuation, diffraction, divergence) in the focused laser beam pattern. In addition, as  FIG. 4B  illustrates, the smoothed-surface recess turns into a flat surface co-planar with the ABS  405  and the distal end  412  of the NFT  410  when an operational optical power is applied to the NFT  410 . In contrast, a recess having 90-degree edges at the top and bottom when no optical power is applied turns into an irregular surface not coplanar with the ABS and the NFT when an operational optical power is applied to the NFT. Such a non-coplanar surface can produce a portion of the slider slightly protruding beyond the ABS or the distal end of the NFT slightly below the ABS with the attendant degradation in the focusing ability of the NFT. 
     The description of the invention is provided to enable any person skilled in the art to practice the various embodiments described herein. While the present invention has been particularly described with reference to the various figures and embodiments, it should be understood that these are for illustration purposes only and should not be taken as limiting the scope of the invention. 
     There may be many other ways to implement the invention. Various functions and elements described herein may be partitioned differently from those shown without departing from the spirit and scope of the invention. Various modifications to these embodiments will be readily apparent to those skilled in the art, and generic principles defined herein may be applied to other embodiments. Thus, many changes and modifications may be made to the invention, by one having ordinary skill in the art, without departing from the spirit and scope of the invention. 
     A reference to an element in the singular is not intended to mean “one and only one” unless specifically stated, but rather “one or more.” The term “some” refers to one or more. Underlined and/or italicized headings and subheadings are used for convenience only, do not limit the invention, and are not referred to in connection with the interpretation of the description of the invention. All structural and functional equivalents to the elements of the various embodiments of the invention described throughout this disclosure that are known or later come to be known to those of ordinary skill in the art are expressly incorporated herein by reference and intended to be encompassed by the invention. Moreover, nothing disclosed herein is intended to be dedicated to the public regardless of whether such disclosure is explicitly recited in the above description.

Technology Category: 4