Disclosed are an optical member, a display device including the same, and a method of fabricating the same. The optical member includes a host layer; a plurality of first wavelength conversion particles in the host layer; and a plurality of second wavelength conversion particles in the host layer, wherein the first wavelength conversion particles include compound semiconductors, and the second wavelength conversion particles include phosphors.
1. An optical member comprising: a host layer; a plurality of first wavelength conversion particles in the host layer; and a plurality of second wavelength conversion particles in the host layer, wherein the first wavelength conversion particles include compound semiconductors, and the second wavelength conversion particles include phosphors.
2. The optical member of claim 1, further comprising a plurality of dispersion enhancing particles in the host layer.
3. The optical member of claim 2, wherein the dispersion enhancing particles include silicon oxide.
4. The optical member of claim 2, wherein the dispersion enhancing particles have a diameter in a range of about 10 nm to about 10 μm.
5. The optical member of claim 2, wherein the dispersion enhancing particles are contained in the host layer at a ratio of about 0.5 wt % to about 5 wt %.
6. The optical member of claim 1, wherein the second wavelength conversion particles have a diameter larger than a diameter of the first wavelength conversion particles.
7. The optical member of claim 6, wherein the diameter of the first wavelength conversion particles is in a range of 1 nm to 50 nm and the diameter of the second wavelength conversion particles is in a range of 1 μm to 50 μm.
8. The optical member of claim 1, wherein the first wavelength conversion particles are contained in the host layer at a ratio of about 0.5 wt % to about 5 wt %.
9. The optical member of claim 1, wherein the first wavelength conversion particles include quantum dots.
10. The optical member of claim 1, wherein the second wavelength conversion particles include green phosphors.
11. The optical member of claim 1, further comprising a plurality of third wavelength conversion particles in the host layer, wherein the second wavelength conversion particles include green phosphors and the third wavelength conversion particles include yellow phosphors.
12. A display device comprising: a light source; a wavelength conversion member to which light emitted from the light source is incident; and a display panel to which light output from the wavelength conversion member is incident, wherein the wavelength conversion member comprises: host layer; a plurality of first wavelength conversion particles in the host layer; and a plurality of second wavelength conversion particles in the host layer, and wherein the first wavelength conversion particles include compound semiconductors, and the second wavelength conversion particles include phosphors.
13. The display device of claim 12, further comprising a plurality of dispersion enhancing particles in the host layer.
14. The display device of claim 12, wherein the second wavelength conversion particles have a diameter larger than a diameter of the first wavelength conversion particles.
15. The display device of claim 14, wherein the diameter of the first wavelength conversion particles is in a range of 1 nm to 50 nm and the diameter of the second wavelength conversion particles is in a range of 1 μm to 50 μm.
16. The display device of claim 12, wherein the first wavelength conversion particles include quantum dots and the second wavelength conversion particles include green phosphors.
17. The display device of claim 12, further comprising a plurality of third wavelength conversion particles in the host layer, wherein the second wavelength conversion particles include green phosphors and the third wavelength conversion particles include yellow phosphors.
[0003] Alight emitting diode (LED) can be used as a light source for the display device. In addition, a light guide plate and optical sheets may be laminated in the display device to effectively transfer the light generated from the light source to the display panel.
[0008] The embodiment provides an optical member representing the superior brightness and color reproduction rate, a display device and a method of fabricating the same.
[0009] An optical member according to the embodiment includes a host layer; a plurality of first wavelength conversion particles in the host layer; and a plurality of second wavelength conversion particles in the host layer, wherein the first wavelength conversion particles include compound semiconductors, and the second wavelength conversion particles include phosphors.
[0010] A display device according to the embodiment includes a light source; a wavelength conversion member to which light emitted from the light source is incident; and a display panel to which light output from the wavelength conversion member is incident, wherein the wavelength conversion member includes a host layer; a plurality of first wavelength conversion particles in the host layer; and a plurality of second wavelength conversion particles in the host layer, and wherein the first wavelength conversion particles include compound semiconductors, and the second wavelength conversion particles include phosphors.
[0011] A method of fabricating an optical member according to the embodiment includes the steps of adding a plurality of second wavelength conversion particles including phosphors to a resin composition including resin and dispersing the second wavelength conversion particles; adding a plurality of dispersion enhancing particles to the resin composition; adding a plurality of first wavelength conversion particles including compound semiconductors to the resin composition; and curing the resin composition.
[0012] According to the embodiment, the first wavelength conversion particles and the second wavelength conversion particles are contained in one host layer. In particular, the first wavelength conversion particles may include quantum dots and the second wavelength conversion particles may include phosphors. In addition, the first wavelength conversion particles convert incident light into light having a first wavelength band, and the second wavelength conversion particles convert the incident light into light having a second wavelength band.
[0013] In addition, in order to form the optical member according to the embodiment, the phosphors are primarily added and the dispersion enhancing particles are used later. Therefore, the phosphors, which are strong against the mechanical impact, are primarily dispersed and then the dispersion enhancing particles prevent the conglomeration of the phosphors. Thus, according to the method of fabricating the optical member of the embodiment, the phosphors and the quantum dots may be readily dispersed.
[0014] Therefore, the optical member according to the embodiment may represent the superior brightness and the color reproduction.
[0015] FIG. 1 is an exploded perspective view showing a liquid crystal display according to the first embodiment;
[0016] FIG. 2 is a perspective view showing a wavelength conversion member according to the first embodiment;
[0017] FIG. 3 is a sectional view taken along line A-A' of FIG. 2;
[0018] FIGS. 4 and 5 are views showing the method of fabricating a wavelength conversion member according to the first embodiment;
[0019] FIG. 6 is a sectional view showing a wavelength conversion member according to the second embodiment;
[0020] FIG. 7 is a view showing a graph showing the intensity of white light as a function of the wavelength of the white light generated by a wavelength conversion member according to the second embodiment;
[0021] FIG. 8 is an exploded perspective view showing a liquid crystal display according to the third embodiment;
[0022] FIG. 9 is a perspective view showing a wavelength conversion member according to the third embodiment;
[0023] FIG. 10 is a sectional view taken along line B-B' of FIG. 5;
[0024] FIG. 11 is a sectional view showing a light guide plate, a light emitting diode and a wavelength conversion member according to the third embodiment;
[0025] FIGS. 12 to 14 are views showing a method of fabricating a wavelength conversion member according to the third embodiment;
[0026] FIG. 15 is an exploded perspective view showing a liquid crystal display according to the fourth embodiment;
[0027] FIG. 16 is a perspective view showing a wavelength conversion member according to the fourth embodiment;
[0028] FIG. 17 is a sectional view taken along line C-C' of FIG. 15; and
[0029] FIG. 18 is a sectional view showing a light guide plate, a light emitting diode and a wavelength conversion member according to the fourth embodiment.
[0030] In the description of the embodiments, it will be understood that when a substrate, a frame, a sheet a layer or a pattern is referred to as being "on" or "under" another substrate, another frame, another sheet, another layer, or another pattern, it can be "directly" or "indirectly" on the other substrate, frame, sheet, layer, or pattern, or one or more intervening layers may also be present. Such a position of the layer has been described with reference to the drawings. The thickness and size of each layer shown in the drawings may be exaggerated, omitted or schematically drawn for the purpose of convenience or clarity. In addition, the size of elements does not utterly reflect an actual size.
[0031] FIG. 1 is an exploded perspective view showing a liquid crystal display according to the first embodiment, FIG. 2 is a perspective view showing a wavelength conversion member according to the first embodiment, FIG. 3 is a sectional view taken along line A-A' of FIG. 2, and FIGS. 4 and 5 are views showing the method of fabricating the wavelength conversion member according to the first embodiment.
[0032] Referring to FIGS. 1 to 3, the liquid crystal display device (LCD) according to the embodiment includes a backlight unit 10 and a liquid crystal panel 20.
[0039] The light emitting diodes 400 may include a blue light emitting diode generating the blue light or a UV light emitting diode generating the UV light. In detail, the light emitting diodes 400 may emit the blue light having the wavelength band of about 430 nm to about 470 nm or the UV light having the wavelength band of about 300 nm to abut 400 nm.
[0043] The optical sheets 500 may include a wavelength conversion member 501, a diffusion sheet 502, a first prism sheet 503, and a second prism sheet 503.
[0044] The wavelength conversion member 501 is provided on a light path between the light source 400 and the liquid crystal panel 20. For instance, the wavelength conversion member 501 is provided on the light guide plate 200. In detail, the wavelength conversion member 501 is interposed between the light guide plate 200 and the diffusion sheet 502. The wavelength conversion member 501 converts the wavelength of the incident light so that the incident light can be output upward.
[0045] For instance, if the light emitting diodes 400 are blue light emitting diodes, the wavelength conversion member 501 converts the blue light output upward from the light guide plate 200 into the green light and the red light. In detail, the wavelength conversion member 501 converts a part of the blue light into the green light having the wavelength in the range of about 520 nm to about 560 nm, and a part of the blue light into the red light having the wavelength in the range of about 630 nm to about 660 nm.
[0046] Therefore, the white light may be generated by the light passing through the wavelength conversion member 501 without being converted and the lights converted by the wavelength conversion member 501. In detail, the white light can be incident into the liquid crystal panel 20 through the combination of the blue light, the green light and the red right.
[0047] In other words, the wavelength conversion member 501 is an optical member to change or improve the characteristic of the incident light. The wavelength conversion member 501 may have a sheet shape. That is, the wavelength conversion member 501 is an optical sheet.
[0048] As shown in FIGS. 2 and 3, the wavelength conversion member 501 includes a lower substrate 510, an upper substrate 520, a wavelength conversion layer 530, and a sealing part 540.
[0049] The lower substrate 510 is provided under the wavelength conversion layer 530. The lower substrate 510 may be transparent and flexible. The lower substrate 510 may adhere to a bottom surface of the wavelength conversion layer 530.
[0050] The lower substrate 510 may include a transparent polymer such as polyethyleneterephthalate (PET).
[0051] The upper substrate 520 is disposed on the wavelength conversion layer 530. The upper substrate 520 may be transparent and flexible. The upper substrate 520 may adhere to the top surface of the wavelength conversion layer 530.
[0052] The upper substrate 520 may include a transparent polymer such as PET.
[0053] The wavelength conversion layer 530 is sandwiched between the upper and lower substrates 520 and 510. The upper and lower substrates 520 and 510 support the wavelength conversion layer 530. The upper and lower substrates 520 and 510 protect the wavelength conversion layer 530 from external physical impact. The upper and lower substrates 520 and 510 directly make contact with the wavelength conversion layer 530.
[0054] In addition, the upper and lower substrates 520 and 510 have low oxygen permeability and low moisture permeability. Thus, the upper and lower substrates 520 and 510 can protect the wavelength conversion layer 530 from external chemical penetration by oxygen and/or moisture.
[0055] The wavelength conversion layer 530 is interposed between the lower and upper substrates 510 and 520. The wavelength conversion layer 530 may adhere to the top surface of the lower substrate 510, and adhere to the bottom surface of the upper substrate 520.
[0056] The wavelength conversion layer 530 includes a host layer 531, a plurality of first wavelength conversion particles 532, a plurality of second wavelength conversion particles 533 and a plurality of dispersion enhancing particles.
[0057] The host layer 531 surrounds the first wavelength conversion particles 532, the second wavelength conversion particles 533 and the dispersion enhancing particles. That is, the first wavelength conversion particles 532, the second wavelength conversion particles 533 and the dispersion enhancing particles are uniformly distributed in the host layer 531. The host layer 531 may include a polymer, such as a silicon resin. The host layer 531 is transparent. That is, the host layer 531 may be formed by using a transparent polymer.
[0058] The host layer 531 is interposed between the lower and upper substrates 510 and 520. In more detail, the host layer 531 adheres to the top surface of the lower substrate 510 and the bottom surface of the upper substrate 520.
[0059] The first wavelength conversion particles 532 are interposed between the lower and upper substrates 510 and 520. In more detail, the first wavelength conversion particles 532 are uniformly distributed in the host layer 531, and the host layer 531 is interposed between the lower substrate 510 and the upper substrate 520. The first wavelength conversion particles 532 may be distributed in the host layer 531 in the concentration of about 0.5 wt % to about 5 wt %.
[0060] The first wavelength conversion particles 532 convert the wavelength of the light emitted from the light emitting diodes 400. In detail, the first wavelength conversion particles 532 receive light emitted from the light emitting diodes 400 to convert the wavelength of the incident light. For instance, the first wavelength conversion particles 532 may convert the blue light emitted from the light emitting diodes 400 into the green light and the red light. That is, the first wavelength conversion particles 532 may convert the blue light into the red light having the wavelength in the range of about 630 nm to about 660 nm.
[0061] The first wavelength conversion particles 532 may include compound semiconductors. In detail, the first wavelength conversion particles 532 may include nano particles including the compound semiconductors. In more detail, the first wavelength conversion particles 532 may include quantum dots (QD). The quantum dots may include core nano-crystals and shell nano-crystals surrounding the core nano-crystals. In addition, the quantum dots may include organic ligands bonded to the shell nano-crystals. Further, the quantum dots may include an organic coating layer surrounding the shell nano-crystals.
[0062] The shell nano-crystals may be prepared as at least two layers. The shell nano-crystals are formed on the surface of the core nano-crystals. The quantum dots lengthen the wavelength of the light incident into the core nano-crystals by using the shell nano-crystals forming a shell layer, thereby improving the light efficiency.
[0063] The quantum dots may include at least one of a group-II compound semiconductor, a group-III compound semiconductor, a group-V compound semiconductor, and a group-VI compound semiconductor. In more detail, the core nano-crystals may include CdSe, InGaP, CdTe, CdS, ZnSe, ZnTe, ZnS, HgTe or HgS. In addition, the shell nano-crystals may include CuZnS, CdSe, CdTe, CdS, ZnSe, ZnTe, ZnS, HgTe or HgS. The quantum dot may have a diameter of about 1 nm to about 15 nm. In detail, the quantum dot may have a diameter of about 8 nm to about 11 nm.
[0064] The wavelength of the light emitted from the quantum dots can be adjusted according to the size of the quantum dots. The organic ligand may include pyridine, mercapto alcohol, thiol, phosphine and phosphine oxide. The organic ligand may stabilize the unstable quantum dots after the synthesis process. Dangling bonds may be formed at the valence band and the quantum dots may be unstable due to the dangling bonds. However, since one end of the organic ligand is the non-bonding state, the one end of the organic ligand is bonded with the dangling bonds, thereby stabilizing the quantum dots.
[0065] In particular, if the size of the quantum dot is smaller than the Bohr radius of an exciton, which consists of an electron and a hole excited by light and electricity, the quantum confinement effect may occur, so that the quantum dot may have the discrete energy level. Thus, the size of the energy gap is changed. In addition, the charges are confined within the quantum dot, so that the light emitting efficiency can be improved.
[0066] Different from general fluorescent pigments, the fluorescent wavelength of the quantum dot may vary depending on the size of the particles. In detail, the light has the shorter wavelength as the size of the particle is reduced, so that the fluorescent light having the wavelength band of visible ray can be generated by adjusting the size of the particles. In addition, the quantum dot represents the extinction coefficient which is 100 to 1000 times higher than that of the general pigment and has the superior quantum yield as compared with the general pigment, so that strong fluorescent light can be generated.
[0067] The quantum dots can be synthesized through the chemical wet scheme. The chemical wet scheme is to grow the particles by immersing the precursor material in the organic solvent. According to the chemical wet scheme, the quantum dots can be synthesized.
[0068] In detail, the first wavelength conversion particles may include quantum dots capable of converting the blue light into the red light.
[0069] The second wavelength conversion particles 533 are disposed in the host layer 531. In detail, the second wavelength conversion particles 533 are uniformly distributed in the host layer 531.
[0070] The second wavelength conversion particles 533 may have a diameter larger than that of the first wavelength conversion particles 532. In detail, the second wavelength conversion particles 533 may have a diameter in the range of about 0.5 μm to about 10 μm.
[0071] The second wavelength conversion particles 533 convert the wavelength of the light emitted from the light emitting diodes 400. In detail, the second wavelength conversion particles 533 receive light emitted from the light emitting diodes 400 to convert the wavelength of the incident light. For instance, the second wavelength conversion particles 533 may convert the blue light emitted from the light emitting diodes 400 into the green light and the red light. That is, the second wavelength conversion particles 533 may convert the blue light into the red light having the wavelength in the range of about 500 nm to about 600 nm.
[0072] The second wavelength conversion particles 533 may include phosphors. In detail, the second wavelength conversion particles 533 may include green phosphors. In more detail, the green phosphors may include zinc oxide phosphors doped with Mn (i.e., Zn2SiO4:Mn), strontium gallium sulfide phosphors doped with europium (i.e., SrGa2S4:Eu), or barium silicon oxide chloride phosphors doped with europium (i.e., Ba5Si2O7C14:Eu).
[0073] The dispersion enhancing particles are disposed in the host. The dispersion enhancing particles are uniformly distributed in the host. The dispersion enhancing particles may be uniformly distributed between the first wavelength conversion particles and the second wavelength conversion particles.
[0074] The dispersion enhancing particles may be transparent. The dispersion enhancing particles may include inorganic materials. In detail, the dispersion enhancing particles may include oxides, such as a silicon oxide. For instance, the dispersion enhancing particles may include silica particles.
[0075] The dispersion enhancing particles may have a diameter in the range of about 10 nm to about 10 μm. The dispersion enhancing particles may be included in the host in the ratio of about 0.5 wt % to about 5 wt %.
[0076] The dispersion enhancing particles may improve the dispersive property of the first and second wavelength conversion particles in the host. In addition, the dispersion enhancing particles may serve as scattering particles that covert the route of the incident light.
[0077] The wavelength conversion member 501 can be formed through the following process.
[0078] Referring to FIG. 4, a plurality of second wavelength conversion particles 533 are uniformly distributed in the silicon resin, epoxy resin or acryl resin. At this time, the second wavelength conversion particles 533 may be dispersed through the ultrasonic dispersion. That is, the ultrasonic wave is applied to the second wavelength conversion particles 533, so that the second wavelength conversion particles 533 may be pulverized to have smaller diameters.
[0079] At this time, since the second wavelength conversion particles include the phosphors, the performance of the second wavelength conversion particles may not be degraded even if the second wavelength conversion particles are intensively dispersed through the ultrasonic dispersion. That is, the second wavelength conversion particles may be primarily dispersed intensively in a state that the first wavelength conversion particles are not included.
[0080] Then, the dispersion enhancing particles are added to the resin composition where the second wavelength conversion particles have been dispersed. The dispersion enhancing particles may improve the viscosity of the resin composition. Thus, the dispersion enhancing particles can prevent the second wavelength conversion particles from being conglomerated again. That is, the second wavelength conversion particles may hold the dispersion property by the dispersion enhancing particles.
[0081] The dispersion enhancing particles may be added to the resin composition in the ratio of about 0.5 wt % to about 5 wt %.
[0082] After that, the first wavelength conversion particles are added to the resin composition. The first wavelength conversion particles may be dispersed in the resin composition less intensively than the second wavelength conversion particles.
[0083] Then, referring to FIG. 5, the resin composition is uniformly coated on the lower substrate 510. The resin composition may be coated on the top surface of the lower substrate 510 through the slit coating, spin coating or spray coating.
[0084] After that, the second wavelength conversion particles 533 are immersed and the coated resin composition is cured by light and/or heat, so that the wavelength conversion layer is formed.
[0085] Thereafter, the upper substrate 520 is laminated on the upper substrate 520 and then the sealing part is formed, so that the wavelength conversion member 501 is obtained.
[0086] The sealing part 540 is disposed at the lateral side of the wavelength conversion layer 530. In detail, the sealing part 540 covers the lateral side of the wavelength conversion layer 530. In more detail, the sealing part 540 can be disposed at the lateral sides of the lower substrate 510 and the upper substrate 520. In this case, the sealing part 540 covers the lateral sides of the lower substrate 510 and the upper substrate 520.
[0087] In addition, the sealing part 540 may be bonded to the lateral sides of the wavelength conversion layer 530, the lower substrate 510 and the upper substrate 520. In addition, the sealing part 540 may closely adhere to the lateral sides of the wavelength conversion layer 530, the lower substrate 510 and the upper substrate 520.
[0088] Therefore, the sealing part 540 can seal the lateral side of the wavelength conversion layer 530. That is, the sealing part 540 may serve as a protective part for protecting the wavelength conversion layer 530 from the external chemical impact.
[0089] In addition, the wavelength conversion member 501 may further include first and second inorganic protective layers. The first inorganic protective layer is coated on the bottom surface of the lower substrate 510 and the second inorganic protective layer is coated on the top surface of the upper substrate 520. The first and second inorganic protective layers may include silicon oxides.
[0090] The diffusion sheet 502 is disposed on the wavelength conversion member 501. The diffusion sheet 502 may improve the uniformity of light passing through the diffusion sheet 502. The diffusion sheet 502 may include a plurality of beads.
[0091] The first prism sheet 503 is provided on the diffusion sheet 502. The second prism sheet 504 is provided on the first prism sheet 503. The first prism sheet 503 and the second prism sheet 504 may improve the linearity of light passing therethrough.
[0092] The liquid crystal panel 20 is disposed on the optical sheets 500. In addition, the liquid crystal panel 20 is disposed on the panel guide 23. The liquid crystal panel 20 is guided by the panel guide 23.
[0093] The liquid crystal panel 20 displays images by adjusting intensity of light passing through the liquid crystal panel 20. In detail, the liquid crystal panel 20 is a display panel for displaying the images by using the light emitted from the backlight unit 10. The liquid crystal panel 20 includes a TFT substrate 21, a color filter substrate 22 and a liquid crystal layer interposed between the two substrates. In addition, the liquid crystal panel 20 includes polarizing filters.
[0094] Hereinafter, the TFT substrate 21 and the color filter substrate 22 will be described in detail although it is not shown in the drawings in detail. The TFT substrate 21 includes a plurality of gate lines and a plurality of data lines crossing the gate lines to form pixels and a thin film transistor (TFT) is provided at each cross section such that the thin film transistor TFT can be connected to a pixel electrode of the pixel in one-to-one correspondence. The color filter substrate 22 includes color filters having R, G and B colors corresponding to the pixels, a black matrix covering the gate lines, data lines and thin film transistors within the limit of the color filters, and a common electrode covering the above elements.
[0095] A driving PCB 25 is provided at an outer peripheral portion of the liquid crystal panel 20 to supply driving signals to the gate lines and data lines.
[0096] The driving PCB 25 is electrically connected to the liquid crystal panel 20 by a COF (chip on film) 24. The COF 24 may be replaced with a TCP (tape carrier package).
[0097] As described above, the first wavelength conversion particles and the second wavelength conversion particles are included in one host layer. In particular, the first wavelength conversion particles may include quantum dots and the second wavelength conversion particles may include phosphors. In addition, the first wavelength conversion particles convert incident light into light having a first wavelength band, and the second wavelength conversion particles convert the incident light into light having a second wavelength band.
[0098] In addition, in order to form the optical member according to the embodiment, the phosphors are primarily added and the dispersion enhancing particles are used later. Therefore, the phosphors, which are strong against the mechanical impact, are primarily dispersed and then the dispersion enhancing particles prevent the conglomeration of the phosphors. Thus, according to the method of fabricating the optical member of the embodiment, the phosphors and the quantum dots may be readily dispersed.
[0099] Therefore, the optical member according to the embodiment may represent the superior brightness and the color reproduction.
[0100] FIG. 6 is a sectional view showing a wavelength conversion member according to the second embodiment. In the description about the second embodiment, the description about the liquid crystal display according to the previous embodiment will be incorporated by reference except for the modified parts.
[0101] Referring to FIG. 6, the wavelength conversion member according to the second embodiment may include third wavelength conversion particles 534. The third wavelength conversion particles 534 are disposed in the host layer 531. In more detail, the third wavelength conversion particles 534 are uniformly distributed in the host layer 531.
[0102] The third wavelength conversion particles 534 may be distributed in the host layer 531 in the concentration of about 0.1 wt % to about 0.5 wt %.
[0103] The third wavelength conversion particles 533 may have a diameter larger than that of the first wavelength conversion particles 532. In detail, the third wavelength conversion particles 534 may have a diameter in the range of about 0.5 μm to about 10 μm.
[0104] The third wavelength conversion particles 534 convert the wavelength of the light emitted from the light emitting diodes 400. In detail, the third wavelength conversion particles 534 receive light emitted from the light emitting diodes 400 to convert the wavelength of the incident light. For instance, the third wavelength conversion particles 534 may convert the blue light emitted from the light emitting diodes 400 into the yellow light. That is, the third wavelength conversion particles 534 may convert the blue light into the yellow light having the wavelength in the range of about 540 nm to about 570 nm.
[0105] If the light emitting diodes 400 are blue light emitting diodes that emit the blue light, the third wavelength conversion particles 534 can be used to convert the blue light into the yellow light.
[0106] The third wavelength conversion particles 534 may include phosphors. In detail, the third wavelength conversion particles 534 may include yellow phosphors. In more detail, the yellow phosphors may include yttrium aluminum garnet (YAG) phosphors.
[0107] As shown in FIG. 7, due to the third wavelength conversion particles 534, the intensity of the white light generated by the wavelength conversion member 501 according to the embodiment may be increased in the wavelength band (Y) of about 555 nm to about 560 nm.
[0108] Therefore, the wavelength conversion member 501 according to the embodiment can generate the white light having the superior brightness. Thus, the display device including the wavelength conversion member 501 according to the embodiment may represent the superior brightness and color reproduction.
[0109] In addition, the third wavelength conversion particles 534 can be distributed in the resin composition together with the second wavelength conversion particles 533. That is, in order to form the wavelength conversion member 501 according to the embodiment, the second and third wavelength conversion particles 533 and 534 are primarily dispersed and then the first wavelength conversion particles 532 are dispersed.
[0110] FIG. 8 is an exploded perspective view showing a liquid crystal display according to the third embodiment. FIG. 9 is a perspective view showing a wavelength conversion member according to the third embodiment. FIG. 10 is a sectional view taken along line B-B' of FIG. 5. FIG. 11 is a sectional view showing a light guide plate, a light emitting diode and a wavelength conversion member according to the third embodiment. FIGS. 12 to 14 are views showing a method of fabricating a wavelength conversion member according to the third embodiment. In the description about the third embodiment, the description about the liquid crystal display according to the previous embodiments will be incorporated by reference except for the modified parts.
[0111] Referring to FIGS. 8 to 11, the wavelength conversion member 600 is disposed between the light emitting diodes 400 and the light guide plate 200.
[0112] The wavelength conversion member 600 may extend in one direction. In detail, the wavelength conversion member 600 may extend along one lateral side of the light guide plate 200. In more detail, the wavelength conversion member 600 may extend along an incident surface of the light guide plate 200.
[0113] The wavelength conversion member 600 receives light emitted from the light emitting diodes 400 to convert the wavelength of the incident light. For instance, the wavelength conversion member 600 may convert the blue light emitted from the light emitting diodes 400 into the green light and the red light. That is, the wavelength conversion member 600 may convert a part of the blue light into the green light having the wavelength in the range of about 520 nm to about 560 nm and convert a part of the blue light into the red light having the wavelength in the range of about 630 nm to about 660 nm.
[0114] Therefore, the white light may be generated by the light passing through the wavelength conversion member 600 and the lights converted by the wavelength conversion member 600. In detail, the white light can be incident into the liquid guide plate 200 through the combination of the blue light, the green light and the red right.
[0115] As shown in FIGS. 9 to 11, the wavelength conversion member 600 includes a lower substrate 610, an upper substrate 620, a wavelength conversion layer 630, and a sealing part 640.
[0116] As shown in FIG. 10, the lower substrate 610 is provided under the wavelength conversion layer 630. The lower substrate 610 may be transparent and flexible. The lower substrate 610 may adhere to a bottom surface of the wavelength conversion layer 630.
[0117] In addition, the upper substrate 620 is disposed on the wavelength conversion layer 630. The upper substrate 620 may be transparent and flexible. The upper substrate 620 may adhere to the top surface of the wavelength conversion layer 630.
[0118] In addition, as shown in FIG. 11, the lower substrate 610 faces the light emitting diodes 400. That is, the lower substrate 610 is disposed between the light emitting diodes 400 and the wavelength conversion layer 630. In addition, the upper substrate 620 faces the light guide plate 200. That is, the upper substrate 620 is disposed between the wavelength conversion layer 630 and the light guide plate 200. The wavelength conversion layer 630 is sandwiched between the upper and lower substrates 620 and 610. In addition, the sealing part 640 covers the lateral side of the wavelength conversion layer 630. The upper and lower substrates 620 and 610 support the wavelength conversion layer 630. In addition, That is, the upper and lower substrates 620 and 610 and the sealing part 540 may protect the wavelength conversion layer 630 from the external physical and chemical impact.
[0119] The wavelength conversion member according to the present embodiment can be formed through the following process.
[0120] Referring to FIG. 12, a resin composition including a plurality of first wavelength conversion particles 632, a plurality of second wavelength conversion particles 633 and a plurality of dispersion enhancing particles is coated on a first transparent substrate 611. Then, the resin composition is cured by light and/or heat so that a preliminary wavelength conversion layer 635 is formed on the first transparent substrate 611.
[0121] Then, a second transparent substrate 621 is laminated on the preliminary wavelength conversion layer 635.
[0122] Referring to FIG. 13, the first transparent substrate 611, the preliminary wavelength conversion layer 635 and the second transparent substrate 621 are simultaneously cut. Therefore, a plurality of preliminary wavelength conversion members 601 can be formed. Each of the preliminary wavelength conversion members 601 may include the lower substrate 610, the wavelength conversion layer 630 and the upper substrate 620. Since the lower substrate 610, the wavelength conversion layer 630 and the upper substrate 620 are simultaneously cut through the cutting process, the same cutting surface 605 is formed at the lower substrate 610, the wavelength conversion layer 630 and the upper substrate 620.
[0123] Referring to FIG. 14, the preliminary wavelength conversion members 601 are aligned such that the lower substrate 610 may face the upper substrate 620. Then, the sealing part 640 is formed at the lateral sides of the preliminary wavelength conversion members 601, that is, at the cutting surface 605.
[0124] After that, the wavelength conversion members 601 may be separated from each other.
[0125] In the liquid crystal display device according to the present embodiment, the wavelength conversion layer 630 has a relatively small size. Thus, a smaller amount of first and second wavelength conversion particles 632 and 633 can be used to fabricate the liquid crystal display device according to the present embodiment.
[0126] Therefore, the liquid crystal display device according to the present embodiment can reduce the amount of the first and second wavelength conversion particles 632 and 633 and can be readily fabricated at the low cost.
[0127] FIG. 15 is an exploded perspective view showing a liquid crystal display according to the fourth embodiment. FIG. 16 is a perspective view showing a wavelength conversion member according to the fourth embodiment. FIG. 17 is a sectional view taken along line C-C' of FIG. 15. FIG. 18 is a sectional view showing a light guide plate, a light emitting diode and a wavelength conversion member according to the fourth embodiment. In the description about the fourth embodiment, the description about the liquid crystal display according to the previous embodiments will be incorporated by reference except for the modified parts.
[0128] Referring to FIGS. 15 to 18, the liquid crystal display device according to the present embodiment includes a plurality of wavelength conversion members 700. The wavelength conversion members 700 correspond to the light emitting diodes 400, respectively.
[0129] In addition, the wavelength conversion members 700 are disposed between the light emitting diodes 400 and the light guide plate 200. That is, each of the wavelength conversion members 700 is disposed between the corresponding light emitting diode and the light guide plate 200.
[0130] The wavelength conversion members 700 may have surface areas larger than surface areas of the light emitting diodes 400. Thus, most of the light emitted from each light emitting diode may be incident into the corresponding wavelength conversion member 700.
[0131] In addition, as shown in FIGS. 15 to 18, each of the wavelength conversion members 700 may include a lower substrate 710, an upper substrate 720, a wavelength conversion layer 730 and a sealing part 740.
[0132] The features of the lower substrate 710, the upper substrate 720, the wavelength conversion layer 730 and the sealing part 740 are substantially identical to those of the previous embodiments.
[0133] In the liquid crystal display device according to the present embodiment, the wavelength conversion layer 730 has a relatively small size. Thus, a smaller amount of first and second wavelength conversion particles 732 and 733 can be used to fabricate the liquid crystal display device according to the present embodiment.
[0134] Therefore, the liquid crystal display device according to the present embodiment can reduce the amount of the first and second wavelength conversion particles 732 and 733 and can be readily fabricated at the low cost.
[0135] In addition, the feature of each wavelength conversion member 700 can be modified suitably for the corresponding light emitting diode 400. Thus, the liquid crystal display device according to the embodiment may have the superior reliability, brightness, and color reproduction.
[0136] Any reference in this specification to "one embodiment," "an embodiment," "example embodiment," etc., means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment of the invention. The appearances of such phrases in various places in the specification are not necessarily all referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with any embodiment, it is submitted that it is within the purview of one skilled in the art to effects such feature, structure, or characteristic in connection with other ones of the embodiments.
Patent applications by Mun-Suk Kang, Seoul KR
2014-08-21 Led lighting module, led lighting system and led lighting retrofit kit
2015-05-28 Touch window and touch device including the same
2015-03-12 Touch window and display including the same