US20110114170A1 - Conductive paste and solar cell - Google Patents
Conductive paste and solar cell Download PDF
US20110114170A1
US20110114170A1 US12943732 US94373210A US2011114170A1 US 20110114170 A1 US20110114170 A1 US 20110114170A1 US 12943732 US12943732 US 12943732 US 94373210 A US94373210 A US 94373210A US 2011114170 A1 US2011114170 A1 US 2011114170A1
US12943732
US9984787B2 (en )
Disclosed is a conductive paste including; a conductive powder including a plurality of conductive particles, a metallic glass disposed between adjacent conductive particles of the conductive powder, and an organic vehicle in which the conductive powder and metallic glass are disposed, and a solar cell using the conductive paste.
This application claims priority to Korean Patent Application No. 10-2009-0108674, filed on Nov. 11, 2009, and Korean Patent Application No. 10-2010-0096382, filed on Oct. 4, 2010, and all the benefits accruing therefrom under 35 U.S.C. §119, the contents of which in their entirety are herein incorporated by reference.
This disclosure relates to a conductive paste and a solar cell utilizing the same.
A solar cell is a photoelectric conversion device that transforms photonic energy, e.g., solar energy, into electrical energy, and it has attracted much attention as a renewable and pollution-free next generation energy source.
A solar cell typically includes p-type and n-type semiconductors and produces electrical energy by transferring electrons and holes to the n-type and p-type semiconductors, respectively, and then collecting the electrons and holes in each of a pair of oppositely disposed electrodes, when an electron-hole pair (“EHP”) including electron and hole charge carries is produced by the absorption of solar light energy in a photoactive layer inside the semiconductors.
Furthermore, it is typically beneficial for a solar cell to be as efficient as possible for producing electrical energy from solar energy. In order to improve solar energy conversion efficiency, the solar cell may be able to effectively absorb light with little loss so that it may produce as many electron-hole pairs as possible, and then collect the produced charges without losses of the electrons or holes.
Furthermore, an electrode of a solar cell may be fabricated by screen printing using a conductive paste.
One aspect of the present invention provides a conductive paste that may reduce loss of electrical charges and improve efficiency of a solar cell.
Another aspect of the present invention provides a solar cell using the conductive paste.
According to one aspect, a conductive paste including; a conductive powder including a plurality of conductive particles, a metallic glass disposed between adjacent conductive particles of the conductive powder, and an organic vehicle in which the conductive powder and metallic glass are disposed is provided.
In one exemplary embodiment, the metallic glass may include at least one of copper (Cu), titanium (Ti), nickel (Ni), zirconium (Zr), iron (Fe), magnesium (Mg), calcium (Ca), cobalt (Co), palladium (Pd), platinum (Pt), gold (Au), cerium (Ce), lanthanum (La), yttrium (Y), gadolinium (Gd), beryllium (Be), tantalum (Ta), gallium (Ga), aluminum (Al), hafnium (Hf), niobium (Nb), lead (Pb), silver (Ag), phosphorus (P), boron (B), silicon (Si), carbon (C), tin (Sn), zinc (Zn), molybdenum (Mo), tungsten (W), manganese (Mn), erbium (Er), chromium (Cr), praseodymium (Pr), thulium (Tm), or a combination thereof.
In one exemplary embodiment, the metallic glass may include an alloy of copper (Cu), zirconium (Zr), nickel (Ni), iron (Fe), titanium (Ti), magnesium (Mg), or a combination thereof.
In one exemplary embodiment, a glass transition temperature (Tg) of the metallic glass may be lower than an eutectic temperature of silicon and the conductive powder.
In one exemplary embodiment, an eutectic temperature of the conductive powder and the metallic glass may be lower than that of the silicon and the conductive powder.
In one exemplary embodiment, an eutectic temperature of the silicon and the metallic glass may be lower than that of the silicon and the conductive powder.
In one exemplary embodiment, the metallic glass may exist as one of a solid, a supercooled liquid, and a liquid at a sintering temperature of the conductive powder.
In one exemplary embodiment, the conductive powder may include at least one of silver (Ag), aluminum (Al), copper (Cu), nickel (Ni), and a combination thereof.
In one exemplary embodiment, the conductive paste may include about 50 wt % to about 90 wt % of the conductive powder, about 1 wt % to about 20 wt % of the metallic glass, and a remaining amount of the organic vehicle based on a total amount of the conductive paste.
In one exemplary embodiment, the conductive paste may further include glass frit.
In one exemplary embodiment, the conductive paste may include about 50 wt % to about 90 wt % of the conductive powder, about 1 wt % to about 20 wt % of the metallic glass, about 1 wt % to 10 wt % of the glass frit, and a remaining amount of the organic vehicle based on a total amount of the conductive paste.
According to another exemplary embodiment, the solar cell may include a semiconductor layer including a semiconductor material, an electrode including a conductive material electrically connected to the semiconductor layer, and a buffer layer including a metallic glass contacted with the semiconductor layer and the electrode.
In one exemplary embodiment, the buffer layer may be disposed between the semiconductor layer and the electrode.
In one exemplary embodiment, a glass transition temperature of the metallic glass may be lower than the eutectic temperature of the semiconductor material and the conductive material.
In one exemplary embodiment, an eutectic temperature of the conductive material and the metallic glass may be lower than the eutectic temperature of the semiconductor material and the conductive material.
In one exemplary embodiment, an eutectic temperature of the semiconductor material and the metallic glass may be lower than an eutectic temperature of the semiconductor material and the conductive material.
In one exemplary embodiment, the buffer layer may further include glass frit.
In one exemplary embodiment, the semiconductor material may include silicon.
In one exemplary embodiment, the solar cell may further include a first eutectic layer where the conductive material and the metallic glass are subjected to eutectic melting.
In one exemplary embodiment, the solar cell may further include a second eutectic layer that is disposed between the semiconductor layer and the buffer layer and where the semiconductor material and the metallic glass are subjected to eutectic melting.
In one exemplary embodiment, the second eutectic layer may be where the semiconductor material, the metallic glass, and glass frit are subjected to eutectic melting.
In one exemplary embodiment, the metallic glass may be an alloy including at least one of copper (Cu), titanium (Ti), nickel (Ni), zirconium (Zr), iron (Fe), magnesium (Mg), calcium (Ca), cobalt (Co), palladium (Pd), platinum (Pt), gold (Au), cerium (Ce), lanthanum (La), yttrium (Y), gadolinium (Gd), beryllium (Be), tantalum (Ta), gallium (Ga), aluminum (Al), hafnium (Hf), niobium (Nb), lead (Pb), silver (Ag), phosphorus (P), boron (B), silicon (Si), carbon (C), tin (Sn), zinc (Zn), molybdenum (Mo), tungsten (W), manganese (Mn), erbium (Er), chromium (Cr), praseodymium (Pr), thulium (Tm), or a combination thereof.
In one exemplary embodiment, the conductive material may include silver (Ag), aluminum (Al), copper (Cu), nickel (Ni), or a combination thereof.
In one exemplary embodiment, the semiconductor layer may include a p-type layer doped with a p-type impurity and an n-type layer doped with an n-type impurity, the electrode may include a first electrode electrically connected with the p-type layer and a second electrode electrically connected with the n-type layer, and the buffer layer may be disposed at least one of between the p-type layer and the first electrode and the n-type layer and the second electrode.
FIGS. 1 and 2 are schematic views of exemplary embodiments showing a conductive powder applied on a semiconductor substrate in an exemplary embodiment of a solar cell according to the present invention;
FIGS. 3A to 3F are schematic views showing exemplary embodiments of processes of providing a buffer layer on a semiconductor substrate applied with a conductive paste while increasing the temperature thereof;
FIG. 4 is a cross-sectional view of an exemplary embodiment of a solar cell according to the present invention;
FIG. 5 is a cross-sectional view of another exemplary embodiment of a solar cell according to the present invention; and
FIG. 6 is a cross-sectional view of another exemplary embodiment of a solar cell according to the present invention.
First, an exemplary embodiment of a conductive paste according to the present invention will be explained in detail.
According to the present exemplary embodiment, the conductive paste includes a conductive powder, a metallic glass, and an organic vehicle.
The conductive powder includes aluminum (Al), or an aluminum (Al)-containing metal such as an aluminum alloy, silver (Ag), or a silver (Ag)-containing metal such as a silver alloy, copper (Cu), or a copper (Cu)-containing metal such as a copper alloy, nickel (Ni), or a nickel (Ni)-containing metal such as a nickel alloy, a combination thereof or other materials with similar characteristics. Exemplary embodiments include configurations wherein the conductive powder may include other metals, and may include different additives besides the above mentioned metals. In one exemplary embodiment, the conductive powder may have a size of about 0.1 μm to about 50 μm.
The metallic glass includes an alloy having a disordered atomic structure including two or more metals, and is also referred to as an amorphous metal. Since the metallic glass has low resistance that is different from a regular glass such as a silicate, it may be considered an electrical conductor at voltages and currents typically applied to a solar cell.
The metallic glass may be an alloy of transition elements, a noble metal, a rare earth element metal, an alkaline-earth metal, a semimetal, and a combination thereof, and the alloy may include at least one of copper (Cu), titanium (Ti), nickel (Ni), zirconium (Zr), iron (Fe), magnesium (Mg), calcium (Ca), cobalt (Co), palladium (Pd), platinum (Pt), gold (Au), cerium (Ce), lanthanum (La), yttrium (Y), gadolinium (Gd), beryllium (Be), tantalum (Ta), gallium (Ga), aluminum (Al), hafnium (Hf), niobium (Nb), lead (Pb), silver (Ag), phosphorus (P), boron (B), silicon (Si), carbon (C), tin (Sn), zinc (Zn), molybdenum (Mo), tungsten (W), manganese (Mn), erbium (Er), chromium (Cr), praseodymium (Pr), thulium (Tm), a combination thereof or other materials with similar characteristics.
In one exemplary embodiment, the metallic glass may include at least one selected from copper (Cu), zirconium (Zr), nickel (Ni), iron (Fe), titanium (Ti), magnesium (Mg), and a combination thereof.
Exemplary embodiments of the metallic glass may include Cu50Zr50, Cu30Ag30Zr30Ti10, Cu43Zr43Al7Ag7, Cu46Zr46Al8, Cu58.1Zr35.9Al6, Ti50Ni15Cu32Sn3, Ti45Ni15Cu25Sn3Be7Zr5, Ni60Nb30Ta10, Ni61Zr20Nb7Al4Ta8, Ni57.5Zr35Al7.5, Zr41.2Ti13.8Ni10Cu12.5Be22.5, Mg65Y10Cu15Ag5Pd5, Mn55Al25Ni20, La55Al25Ni10Cu10, Mg65Cu7.5Ni7.5Ag5Zn5Gd10, Mg65Cu15Ag10Y6Gd4, Fe77Nb6B17, Fe67Mo13B17Y3, Ca65Mg15Zn20, Ca66.4Al33.6, a combination thereof or other materials with similar characteristics, but is not limited thereto.
The metallic glass may be softened once heated to a glass transition temperature (Tg) or greater, similar to a regular, e.g., non-metallic, glass.
Herein, the glass transition temperature Tg of the metallic glass may be lower than the eutectic temperature of a semiconductor material such as silicon and the conductive powder. Accordingly, the metallic glass may be softened at a temperature lower than the eutectic melting of the semiconductor material and the conductive powder, and therefore the softening may occur prior to eutectic melting of the semiconductor material and the conductive powder during a heating process.
The eutectic temperature of the conductive powder and the metallic glass may be lower than the eutectic temperature of the semiconductor material and the conductive powder. Accordingly, the conductive powder and the metallic glass may be eutectically melted before the eutectic melting of the semiconductor material and the conductive powder during a heating process as described above.
Also, the eutectic temperature of the semiconductor material and the metallic glass may be lower than the eutectic temperature of the semiconductor material and the conductive powder. Accordingly, the semiconductor material and the metallic glass may be eutectically melted before the eutectic melting of the conductive powder and the semiconductor material.
The metallic glass may exist as a solid, a supercooled liquid, or a liquid when heated to a sintering temperature of the conductive powder.
In short, when the conductive paste is applied on the semiconductor layer made of semiconductor material and the temperature is increased, e.g., from a room temperature, the metallic glass is first softened and the softened metallic glass widens an electric charge transfer passage between a semiconductor material and a conductive material by extending a contact area between the semiconductor substrate and a conductive powder. Afterward, the eutectic melting of the metallic glass and the conductive powder, the eutectic melting of the metallic glass and the semiconductor material, and the eutectic melting of the semiconductor material and the conductive powder may be carried out.
The organic vehicle may include an organic compound mixed with a conductive powder and a metallic glass that imparts viscosity to the organic vehicle, and a solvent dissolving the above components.
Exemplary embodiments of the organic compound may include at least one of a (meth)acrylate resin; a cellulose resin such as ethyl cellulose; a phenol resin; an alcohol resin; tetrafluoroethylene (TEFLON); and a combination thereof, and furthermore, it may include an additive such as a surfactant, a thickening agent, a stabilizer and other similar elements.
The solvent may include any kind of solvent as long as it may be soluble with the components.
In one exemplary embodiment, the conductive paste may include about 50 wt % to about 90 wt % of the conductive powder, about 1 wt % to about 20 wt % of the metallic glass, and the balance amount of the conductive paste may be the organic vehicle based on the total amount of the conductive paste.
In the embodiment where it is included, the glass frit has an etching property that etches an insulating layer such as anti-reflective layer in a solar cell to penetrate the insulating layer. Accordingly, the conductive paste including the glass frit may be used in a solar cell provided with an anti-reflective layer.
Also, the glass frit may have an excellent adhesion with a lower layer to improve an adhesion between an electrode made of the conductive paste and a lower layer.
Exemplary embodiments of the glass frit may include PbO—SiO2, PbO—SiO2—B2O3, PbO—SiO2—B2O3—ZnO, PbO—SiO2—B2O3—BaO, PbO—SiO2—ZnO—BaO, ZnO—SiO2, ZnO—B2O3—SiO2, ZnO—K2O—B2O3—SiO2—BaO, Bi2O3—SiO2, Bi2O3—B2O3—SiO2, Bi2O3—B2O3—SiO2—BaO, ZnO—BaO—B2O3—P2O5—Na2O, Bi2O3—B2O3—SiO2—BaO—ZnO, a combination thereof or other materials with similar characteristics.
In an exemplary embodiment wherein the glass frit is included, the conductive paste may include about 50 wt % to about 90 wt % of the conductive powder, about 1 wt % to about 20 wt % of the metallic glass, about 1 wt % to about 10 wt % of the glass frit, and the balance amount of the conductive paste may be the organic vehicle based on the total amount of the conductive paste.
Exemplary embodiments include configurations wherein the conductive paste including the conductive powder, the metallic glass and the organic vehicle may be applied by, for example, screen-printing, when an electrode is formed in various electronic devices. The electronic devices may include a solar cell.
When the electrode is formed in a solar cell, above-mentioned conductive paste may be applied on a semiconductor substrate such as silicon wafer and fired, e.g., heated and dried, to form an electrode.
Hereinafter, an exemplary embodiment of a solar cell will be described with reference to FIGS. 1 and 2.
FIGS. 1 and 2 are schematic views of exemplary embodiments showing the conductive paste applied on the semiconductor substrate in one exemplary embodiment of a solar cell according to the present invention. The present invention is not limited to using the conductive paste within a solar cell and may be applied to other applications such as a PDP electrode or an OLED grid electrode.
Referring to FIG. 1, when an exemplary embodiment of a conductive paste according to the present invention is applied on the semiconductor substrate 110, a conductive powder 120 a and a metallic glass 115 a included in the conductive paste may be present as particles, respectively.
As mentioned above, since a glass transition temperature Tg of the metallic glass 115 a is lower than an eutectic temperature of a semiconductor material, such as silicon, and the conductive powder 120 a, when the conductive paste is applied on the semiconductor substrate 110 and heat-treated (A) at greater than a glass transition temperature Tg of the metallic glass 115 a, the metallic glass 115 a may be softened to fill the gap between a plurality of conductive powder 120 a particles and the semiconductor substrate 110, to form a softened metallic glass 115 b, as shown in FIG. 1.
Referring to FIG. 2, the softened metallic glass 115 b may provide contact portions C1 and C2 with the conductive powder 120 a, a contact portion C3 with a semiconductor substrate 110, and a contact portion C4 between neighboring particles of the conductive powder 120 a to increase close contacting properties therebetween. The softened metallic glass closely contacts the conductive powder 120 a and the semiconductor substrate 110, and thereby may provide a path for transferring electric charges generated by the semiconductor substrate 110 to the conductive powder 120 a. That is, the distance between the conductive powders 120 a particles or between the conductive powder 120 a particles and the semiconductor substrate 110 is minimal.
The softened metallic glass 115 b may be formed as a buffer layer on the semiconductor substrate 110.
Hereinafter, the formation of the softened metallic glass 115 b as a buffer layer on the semiconductor substrate 110 will be described in detail referring to FIGS. 3A to 3E.
FIGS. 3A to 3E are schematic views showing processes of providing a buffer layer on a semiconductor substrate applied with a conductive paste while increasing the temperature thereof.
Referring to FIG. 3A, a conductive paste including the conductive powder 120 a and the metallic glass 115 a (here, the illustration of the organic vehicle is omitted) is applied on a semiconductor substrate 110.
Referring to FIG. 3B, the temperature is increased to a temperature higher than the glass transition temperature Tg of the metallic glass 115 a. In the exemplary embodiment wherein the metallic glass 115 a includes Cu50Zr40Al10, the glass transition temperature Tg may range from about 450° C. to about 500° C. The metallic glass 115 b that is softened at a higher temperature than the glass transition temperature Tg may have wettability to contact the semiconductor substrate 110, and therefore closely contacts the semiconductor substrate 110. When the softened metallic glass 115 b has low viscosity, it may have high wettability, and therefore may increase the close contacting property thereof.
Referring to FIG. 3C, the temperature is increased to a temperature higher than a sintering temperature Ts of the conductive powder 120 a. In the exemplary embodiment wherein the conductive powder 120 a is silver (Ag), the sintering temperature Ts may range from about 580° C. to about 700° C. The adjacent conductive powder 120 a may provide a firmly fastened and sintered conductive powder 120 b at a temperature higher than the sintering temperature Ts. The metallic glass may exist as a solid, a supercooled liquid, or a liquid at the sintering temperature of the conductive powder 120 a.
Referring to FIG. 3D, temperature is increased to be greater than the eutectic temperature T1 of a sintered conductive powder 120 b and the softened metallic glass 115 b. In the exemplary embodiment wherein the conductive powder 120 b is silver (Ag) and the metallic glass 115 b is Cu50Zr40Al10, the eutectic temperature may be about 780° C. The conductive powder 120 b and the metallic glass 115 b may be an eutectic mixture having an increased close contacting property, and the first eutectic layer 117 may be disposed between them.
Referring to FIGS. 3E and 3F, wherein FIG. 3F is an enlarged view of Section ‘A’ (as indicated by dashed lines) shown in FIG. 3E. the temperature is increased to higher than the eutectic temperature T2 of the softened metallic glass 115 b and the semiconductor substrate 110. In the exemplary embodiment wherein the metallic glass 115 b includes Cu50Zr40Al10 and the semiconductor substrate 110 includes silicon, the eutectic temperature may be about 802° C. The metallic glass 115 b and the semiconductor substrate 110 may be an eutectic mixture having an increased close contacting property, and the second eutectic layer 118 may be disposed between them.
The softened metallic glass 115 b may provide a buffer layer 115 by being crystallized at a certain temperature, and the buffer layer 115 may prevent the conductive powder 120 b from diffusing into the semiconductor substrate 110.
In the present exemplary embodiment, a semiconductor substrate and an electrode are electrically connected to each other using a conductive metallic glass. Thereby, loss of electric charges is decreased by enlarging the path for transferring the electric charges to the electrode from the semiconductor substrate, and a buffer layer including the metallic glass may prevent a conductive material of the electrode from deleteriously diffusing into the semiconductor substrate.
Meanwhile, as mentioned above, exemplary embodiments of the conductive paste may further include glass frit. The glass frit may show a similar behavior as a metallic glass to form a part of a buffer layer and an eutectic layer.
Referring to FIG. 4, another exemplary embodiment of a solar cell according to the present invention is described in detail.
FIG. 4 is a cross-sectional view of an exemplary embodiment of a solar cell according to the present invention.
Hereinafter, positions of components will be described with respect to a vertical relation to a semiconductor substrate 110 for better understanding and ease of description, but the present invention is not limited thereto. In addition, as used herein a solar energy incident side of a semiconductor substrate 110 is called a front side, and the opposite side is called a rear side; although alternative configurations are possible.
Referring to FIG. 4, the exemplary embodiment of a solar cell according to the present invention may include a semiconductor substrate 110 including a lower semiconductor layer 110 a and an upper semiconductor layer 110 b.
Exemplary embodiments of the semiconductor substrate 110 may be formed of a crystalline silicon or a compound semiconductor. Exemplary embodiments of the crystalline silicon may be, for example, a silicon wafer. One of the lower semiconductor layer 110 a and the upper semiconductor layer 110 b may be a semiconductor layer doped with a p-type impurity, and the other may be a semiconductor layer doped with an n-type impurity. For example, in one exemplary embodiment the lower semiconductor layer 110 a may be a semiconductor layer doped with a p-type impurity, and the upper semiconductor layer 110 b may be a semiconductor layer doped with an n-type impurity. Herein, in one exemplary embodiment the p-type impurity may be a Group III element such as boron (B), and the n-type impurity may be a Group V element such as phosphorus (P).
In one exemplary embodiment, the surface of the upper semiconductor layer 110 b may be subjected to surface texturing. The surface-textured upper semiconductor layer 110 b may have protrusions and depressions such as in a pyramid shape, or a porous structure such as a honeycomb or various other similar shapes. The surface-textured upper semiconductor layer 110 b may have an enlarged surface area to enhance the light-absorption rate and decrease reflectivity, resultantly improving efficiency of a solar cell.
A plurality of front electrodes 120 are disposed on the semiconductor layer 110 b. The front electrodes 120 are arranged substantially in parallel to the plane of the substrate, and may be designed in a grid pattern with respect to shadowing loss and sheet resistance of the resulting solar cell.
In one exemplary embodiment, the front electrode 120 may be formed of a conductive material, for example a low resistance conductive material such as silver (Ag). The front electrode 120 may be disposed by a screen printing process using the conductive paste as described above. As mentioned above, the conductive paste includes a conductive powder, a metallic glass, and an organic vehicle.
A buffer layer 115 is disposed between the upper semiconductor layer 110 b and the front electrode 120. The buffer layer 115 is a layer formed by softening the metallic glass in the conductive paste at a temperature greater than a glass transition temperature Tg of the metallic glass. Since the buffer layer 115 has conductivity due to the metallic glass and has parts that contact the electrode 120 and the upper semiconductor layer 110 b, it may decrease loss of electric charges by enlarging the path for transferring electric charges between the upper semiconductor layer 110 b and the front electrode 120. In addition, the buffer layer 115 may prevent a material of the front electrode 120 from deleteriously diffusing into the semiconductor substrate 110.
A first eutectic layer 117 is disposed between the front electrode 120 and the buffer layer 115, and a second eutectic layer 118 is disposed between the buffer layer 115 and the upper semiconductor layer 110 b. The first eutectic layer 117 includes an eutectic mixture of the conductive material included in the front electrode 120 and the metallic glass included in the buffer layer 115, and the second eutectic layer 118 includes an eutectic mixture of the metallic glass included in the buffer layer 115 and the semiconductor material included in the upper semiconductor layer 110 b.
In an exemplary embodiment wherein the solar cell is part of a larger solar array, a bus bar electrode (not shown) may be disposed on the front electrode 120. The bus bar electrode connects adjacent solar cells during assembly of a plurality of solar cells.
A dielectric layer 130 is disposed under the semiconductor substrate 110. The dielectric layer 130 may increase efficiency of a solar cell by preventing recombination of electric charges and leaking of a current. The dielectric layer 130 may include a plurality of penetration parts 135, and the semiconductor substrate 110 and a rear electrode 140 that will be described in more detail below may contact one another through the penetration parts 135.
In one exemplary embodiment, the dielectric layer 130 may be formed with silicon oxide (SiO2), silicon nitride (SiNx), aluminum oxide (Al2O3), a combination thereof or other materials with similar characteristics, and may have a thickness of about 100 Å to about 2000 Å.
A rear electrode 140 is disposed under the dielectric layer 130. The rear electrode 140 may be formed of a conductive material, and in one exemplary embodiment it may be an opaque metal such as aluminum (Al). The rear electrode 140 may be disposed by a screen printing process using the above-mentioned conductive paste in the same manner as the front electrode 120.
In one exemplary embodiment, a buffer layer (not shown) is disposed between the rear electrode 140 and the lower semiconductor layer 110 a in the same manner as the front electrode 120. Further, a first eutectic layer (not shown) is disposed between the rear electrode 140 and the buffer layer, and a second eutectic layer (not shown) is disposed between the lower semiconductor layer 110 b and the buffer layer in the same manner as the front electrode 120.
Hereinafter, an exemplary embodiment of the conductive paste used for manufacturing the exemplary embodiment of a solar cell will be described in more detail.
Hereinafter, an exemplary embodiment of a method of manufacturing an exemplary embodiment of a solar cell using the conductive paste will be described with reference to FIG. 4.
First, a semiconductor substrate 110 such as a silicon wafer is prepared. In one exemplary embodiment, the semiconductor substrate 110 may be doped with a p-type impurity.
Then the semiconductor substrate 110 is subjected to a surface texturing treatment. Exemplary embodiments of the surface-texturing treatment may be performed by a wet method using a strong acid such as nitric acid and hydrofluoric acid or a strong base such as sodium hydroxide, or by a dry method using plasma.
Then, in one exemplary embodiment the semiconductor substrate 110 may be doped with an n-type impurity. The n-type impurity may be doped by diffusing POCl3 or H3PO4 or the like into the semiconductor substrate 110 at a high temperature. Thus, the semiconductor substrate 110 includes a lower semiconductor layer 110 a and an upper semiconductor layer 110 b doped with different impurities from each other.
Then a conductive paste for a front electrode is applied on the upper semiconductor layer 110 b. The conductive paste for a front electrode may be provided by a screen printing method. The screen printing method includes applying a front electrode conductive paste including a conductive powder such as silver (Ag), a metallic glass, and an organic vehicle on the position where a front electrode is positioned, and drying the same.
As described above, a conductive paste may include a metallic glass, and the metallic glass may be prepared using any kind of method such as melt spinning, infiltration casting, gas atomization, ion irradiation, mechanical alloying or other similar methods.
Then the conductive paste for forming a front electrode is dried.
A dielectric layer 130 may be provided by stacking aluminum oxide (Al2O3) or silicon oxide (SiO2) on the rear side of the semiconductor substrate 110, as an example, by a plasma enhanced chemical vapor deposition (“PECVD”) method or other similar methods.
Then, in one exemplary embodiment, a plurality of penetration parts 135 may be provided on one part of the dielectric layer 130 using a laser.
The conductive paste for forming a rear electrode is subsequently applied on one side of the dielectric layer 130, e.g., by a screen printing.
The conductive paste for forming a rear electrode is then dried.
Next, in the present exemplary embodiment the conductive paste for forming a front electrode and the conductive paste for forming a rear electrode are co-fired. However, alternative exemplary embodiments include configurations wherein the conductive paste for a front electrode and the conductive paste for a rear electrode may be respectively fired.
The firing may be performed at a higher temperature than the melting temperature of the conductive metal in a furnace, for example at a temperature ranging from about 400° C. to about 1000° C.
Hereinafter, another exemplary embodiment of a solar cell according to the present invention is described referring to FIG. 5.
FIG. 5 is a cross-sectional view showing another exemplary embodiment of a solar cell according to the present invention.
Referring to FIG. 5, an exemplary embodiment of a solar cell according to the present invention includes, as described with respect to the above-mentioned embodiment, a semiconductor substrate 110 including lower semiconductor layer 110 a and upper semiconductor layer 110 b; a plurality of front electrodes 120; a buffer layer 115 positioned between an upper semiconductor layer 110 b and the front electrodes 120; a first eutectic layer 117 positioned between the front electrode 120 and the buffer layer 115; a second eutectic layer 118 positioned between the upper semiconductor layer 110 b and the buffer layer 115; a dielectric layer 130 positioned under the semiconductor substrate 110; and a rear electrode 140 positioned under the dielectric layer 130.
However, the solar cell according to the present embodiment, unlike the above-mentioned embodiment, includes an insulating layer 112 covering the entire surface of the semiconductor substrate 110 except the regions corresponding to the buffer layer 115 as described in more detail below.
Exemplary embodiments of the insulating layer 112 may be made of insulating material that absorbs relatively little light, for example, silicon nitride (SiNx), silicon oxide (SiO2), titanium oxide (TiO2), aluminum oxide (Al2O3), magnesium oxide (MgO), cerium oxide (CeO2), a combination thereof, or other materials with similar characteristics. Exemplary embodiments of the insulating layer 112 include a single layer configuration and a multiple layer configuration.
In one exemplary embodiment, the insulating layer 112 may have a thickness ranging from about 200 Å to about 1500 Å.
The insulating layer 112 may decrease the reflection rate of light and increase selectivity of a particular wavelength or a particular range of wavelengths on the front side of the solar cell to serve as an anti-reflective coating (“ARC”). The insulating layer 112 may be manufactured from a material that is effective to improve its contact properties with the silicon in the surface of the semiconductor substrate 110, thereby increasing the efficiency of the solar cell.
The front electrodes 120 may penetrate the insulating layer 112 to contact the upper semiconductor layer 110 b. The contacting part of the front electrode 120 and the upper semiconductor layer 110 b may be removed by etching, and the etching may be carried out by using the conductive paste further including glass frit with the conductive powder, the metallic glass and the organic vehicle. The glass frit may have an etching property with respect to the insulating layer 112.
The glass frit may act as the metallic glass, and by further including the glass frit with metallic glass, it may improve adhesion to a lower layer.
Hereinafter, another exemplary embodiment of a solar cell according to the present invention is described referring to FIG. 6.
FIG. 6 is a cross-sectional view showing another exemplary embodiment of a solar cell according to the present invention.
The present exemplary embodiment of a solar cell may include a semiconductor substrate 110 doped with a p-type or an n-type impurity. The semiconductor substrate 110 may include a plurality of first doping regions 111 a and second doping regions 111 b that are provided on the rear side and are doped with different impurities from each other. For example, in one exemplary embodiment the first doping regions 111 a may be doped with an n-type impurity, and the second doping regions 111 b may be doped with a p-type impurity. The first doping regions 111 a and the second doping regions 111 b may be alternately disposed in the rear side of the semiconductor substrate 110.
The front side of the semiconductor substrate 110 may be surface-textured, and therefore may enhance the light-absorption rate and decrease the reflectivity thereof, resultantly improving efficiency of a resulting solar cell. In the present exemplary embodiment, an insulation layer 112 is provided on the semiconductor substrate 110.
A dielectric layer 150 including a plurality of penetration parts may be disposed on the rear side of the semiconductor substrate 110.
The first electrode 121 connected with the first doping region 111 a and the second electrode 141 connected with the second doping region 111 b are disposed on the rear side of the semiconductor substrate 110, respectively. The first electrode 121 and the first doping region 111 a may be contacted with one another through a penetration part, and the second electrode 141 and the second doping region 111 b may be contacted with one another through a penetration part. The first electrode 121 and the second electrode 141 may be alternately disposed with one another.
As described in the above exemplary embodiment, the first electrode 121 and the second electrode 141 may be disposed on the semiconductor 110 using a conductive paste including a conductive powder, a metallic glass, an organic vehicle, and optionally glass frit, which is substantially the same as described above.
A buffer layer 115 is disposed between the first doping region 111 a and the first electrode 121, and/or between the second doping region 111 b and the second electrode 141. The buffer layer 115 may have conductivity due to a metallic glass used in the formation thereof. Since the buffer layer 115 includes parts contacting the first electrode 121 and/or the second electrode 141 and parts contacting the first doping region 111 a and/or the second doping region 111 b, loss of electric charges may decrease by enlarging the path for charge transfer between the first doping region 111 a and the first electrode 121, and/or between the second doping region 111 b and the second electrode 141. In addition, the buffer layer 115 may prevent a material of the first electrode 121 or the second electrode 141 from deleteriously diffusing into the first or second doping region 111 a or 111 b.
A first eutectic layer 117 including an eutectic mixture of a conductive material of the first electrode 121 or the second electrode 141, and a metallic glass of the buffer layer 115, is disposed between the first electrode 121 or the second electrode 141 and the buffer layer 115. A second eutectic layer 118 including an eutectic mixture of a semiconductor material and a metallic glass is disposed between the first or second doping region 111 a or 111 b and the buffer layer 115.
An exemplary embodiment of a solar cell including both of the first electrode 121 and the second electrode 141 on the rear surface of the solar cell may decrease an area where a metal is positioned on the front, i.e., light incident, surface of the solar cell. This may decrease shadowing loss and increase solar cell efficiency.
Hereinafter, an exemplary embodiment of a method of manufacturing an exemplary embodiment of a solar cell will be described.
First, a semiconductor substrate 110 doped with, for example, an n-type impurity is prepared. Then, the semiconductor substrate 110 is surface-textured, and insulation layer 112 and dielectric layer 150 are disposed on front side and rear side of the semiconductor substrate 110, respectively. The insulation layer 112 and the dielectric layer 150, as an example, may be provided by chemical vapor deposition (“CVD”).
Then, a part of the dielectric layer 150 is removed by, for example, using a laser to form a plurality of openings.
The first doping region 111 a and the second doping region 111 b may be disposed by sequentially doping a p-type impurity and an n-type impurity at a high concentration in the openings at rear side of the semiconductor substrate 110.
Then, a conductive paste for forming a first electrode 121 is applied on one side of the dielectric layer 150 corresponding to the first doping region 111 a, and a conductive paste for forming a second electrode is applied on the other side corresponding to the second doping region 111 b. The conductive paste for forming a first electrode and the conductive paste for forming a second electrode are provided by a screen printing process, and the conductive paste including a conductive powder, a metallic glass, an organic vehicle, and optionally glass frit may be respectively used.
Next, the conductive paste for forming a front electrode and the conductive paste for forming a rear electrode may be fired together or respectively. The firing may be performed at a higher temperature than the melting temperature of a conductive metal in a furnace.
a conductive powder including a plurality of conductive particles;
a metallic glass disposed between adjacent conductive particles of the conductive powder; and
an organic vehicle in which the conductive powder and metallic glass are disposed.
2. The conductive paste of claim 1, wherein the metallic glass comprises at least one of copper (Cu), titanium (Ti), nickel (Ni), zirconium (Zr), iron (Fe), magnesium (Mg), calcium (Ca), cobalt (Co), palladium (Pd), platinum (Pt), gold (Au), cerium (Ce), lanthanum (La), yttrium (Y), gadolinium (Gd), beryllium (Be), tantalum (Ta), gallium (Ga), aluminum (Al), hafnium (Hf), niobium (Nb), lead (Pb), silver (Ag), phosphorus (P), boron (B), silicon (Si), carbon (C), tin (Sn), zinc (Zn), molybdenum (Mo), tungsten (W), manganese (Mn), erbium (Er), chromium (Cr), praseodymium (Pr), thulium (Tm), and a combination thereof.
3. The conductive paste of claim 2, wherein the metallic glass comprises at least one of an alloy of copper (Cu), zirconium (Zr), nickel (Ni), iron (Fe), titanium (Ti), magnesium (Mg), and a combination thereof.
4. The conductive paste of claim 1, wherein a glass transition temperature of the metallic glass is lower than an eutectic temperature of silicon and the conductive powder.
5. The conductive paste of claim 4, wherein an eutectic temperature of the conductive powder and the metallic glass is lower than an eutectic temperature of the silicon and the conductive powder.
6. The conductive paste of claim 4, wherein an eutectic temperature of the silicon and the metallic glass is lower than an eutectic temperature of the silicon and the conductive powder.
7. The conductive paste of claim 1, wherein the metallic glass is one of a solid, a supercooled liquid, and a liquid at a sintering temperature of the conductive powder.
8. The conductive paste of claim 1, wherein the conductive powder comprises at least one of silver (Ag), aluminum (Al), copper (Cu), nickel (Ni), and a combination thereof.
9. The conductive paste of claim 1, wherein the conductive paste comprises about 50 wt % to about 90 wt % of the conductive powder, about 1 wt % to about 20 wt % of the metallic glass, and a remaining amount of the organic vehicle based on a total amount of the conductive paste.
10. The conductive paste of claim 1, further comprising glass frit.
11. The conductive paste of claim 10, wherein the conductive paste comprises about 50 wt % to about 90 wt % of the conductive powder, about 1 wt % to about 20 wt % of the metallic glass, about 1 wt % to 10 wt % of the glass frit, and a remaining amount of the organic vehicle based on a total amount of the conductive paste.
a semiconductor layer comprising a semiconductor material;
an electrode comprising a conductive material electrically connected to the semiconductor layer; and
a buffer layer comprising a metallic glass which contacts the semiconductor layer and the electrode.
13. The solar cell of claim 12, wherein the buffer layer is disposed between the semiconductor layer and the electrode.
14. The solar cell of claim 12, wherein a glass transition temperature of the metallic glass is lower than an eutectic temperature of the semiconductor material and the conductive material.
15. The solar cell of claim 12, wherein an eutectic temperature of the conductive material and the metallic glass is lower than an eutectic temperature of the semiconductor material and the conductive material.
16. The solar cell of claim 12, wherein an eutectic temperature of the semiconductor material and the metallic glass is lower than an eutectic temperature of the semiconductor material and the conductive material.
17. The solar cell of claim 12, wherein the buffer layer further comprises glass frit.
18. The solar cell of claim 12, wherein the semiconductor material comprises silicon.
19. The solar cell of claim 12, wherein the solar cell further comprises a first eutectic layer disposed between the electrode and the buffer layer and wherein the conductive material and the metallic glass are subjected to eutectic melting.
20. The solar cell of claim 19, wherein the solar cell further comprises a second eutectic layer disposed between the semiconductor layer and the buffer layer where the semiconductor material and the metallic glass are subjected to eutectic melting.
21. The solar cell of claim 20, wherein the second eutectic layer is located at a position wherein the semiconductor material, the metallic glass, and glass frit are all subjected to eutectic melting.
22. The solar cell of claim 12, wherein the metallic glass is an alloy including at least one of copper (Cu), titanium (Ti), nickel (Ni), zirconium (Zr), iron (Fe), magnesium (Mg), calcium (Ca), cobalt (Co), palladium (Pd), platinum (Pt), gold (Au), cerium (Ce), lanthanum (La), yttrium (Y), gadolinium (Gd), beryllium (Be), tantalum (Ta), gallium (Ga), aluminum (Al), hafnium (Hf), niobium (Nb), lead (Pb), silver (Ag), phosphorus (P), boron (B), silicon (Si), carbon (C), tin (Sn), zinc (Zn), molybdenum (Mo), tungsten (W), manganese (Mn), erbium (Er), chromium (Cr), praseodymium (Pr), thulium (Tm), and a combination thereof.
23. The solar cell of claim 12, wherein the conductive material comprises at least one of silver (Ag), aluminum (Al), copper (Cu), nickel (Ni), and a combination thereof.
24. The solar cell of claim 12, wherein the semiconductor layer comprises a p-type layer doped with a p-type impurity and an n-type layer doped with an n-type impurity,
wherein the electrode comprises a first electrode electrically connected with the p-type layer and a second electrode electrically connected with the n-type layer, and
the buffer layer is disposed at least one of between the p-type layer and the first electrode and between the n-type layer and the second electrode.
US12943732 2009-11-11 2010-11-10 Conductive paste and solar cell Active 2033-04-21 US9984787B2 (en)
KR10-2009-0108674 2009-11-11
KR20090108674 2009-11-11
KR10-2010-0096382 2010-10-04
KR20100096382A KR20110052452A (en) 2009-11-11 2010-10-04 Conductive paste and solar cell
US13673359 US9947809B2 (en) 2009-11-11 2012-11-09 Conductive paste and electronic device and solar cell including an electrode formed using the conductive paste
US13673359 Continuation-In-Part US9947809B2 (en) 2009-11-11 2012-11-09 Conductive paste and electronic device and solar cell including an electrode formed using the conductive paste
US20110114170A1 true true US20110114170A1 (en) 2011-05-19
US9984787B2 US9984787B2 (en) 2018-05-29
ID=43629384
US12943732 Active 2033-04-21 US9984787B2 (en) 2009-11-11 2010-11-10 Conductive paste and solar cell
US (1) US9984787B2 (en)
EP (1) EP2325848B1 (en)
CN (1) CN102097153A (en)
US20120103409A1 (en) * 2010-10-27 2012-05-03 Industry-Academic Cooperation Foundation, Yonsei University Of Yonsei University Conductive Paste And Electronic Device And Solar Cell Including An Electrode Formed Using The Same
US20120180859A1 (en) * 2011-01-13 2012-07-19 Samsung Electronics Co., Ltd. Conductive Paste, And Electronic Device And Solar Cell Including An Electrode Formed Using The Same
US20120247550A1 (en) * 2011-03-28 2012-10-04 Industry-Academic Cooperation Foundation, Yonsei University Conductive paste and electronic device and solar cell including an electrode formed using the conductive paste
CN102956282A (en) * 2011-08-26 2013-03-06 横滨橡胶株式会社 Conductive composition, solar cell unit, and solar cell module
US20130118572A1 (en) * 2009-11-11 2013-05-16 Samsung Electronics Co., Ltd. Conductive paste and electronic device and solar cell including an electrode formed using the conductive paste
US20130160834A1 (en) * 2011-12-27 2013-06-27 E.I. Du Pont De Nemours And Company Back-side electrode of p-type solar cell, and method for forming the same
WO2013096715A1 (en) * 2011-12-22 2013-06-27 Ferro Corporation Solar cell pastes for low resistance contacts
EP2680275A1 (en) * 2012-06-27 2014-01-01 Samsung Electronics Co., Ltd Conductive paste and electronic device and solar cell
WO2014052924A1 (en) * 2012-09-27 2014-04-03 Sunpower Corporation Conductive contact for solar cell
US20140109948A1 (en) * 2012-10-19 2014-04-24 Samsung Electronics Co., Ltd. Thermoelectric module, thermoelectric device comprising the same, and process for preparing the thermoelectric element
WO2014089103A1 (en) * 2012-12-06 2014-06-12 Michael Cudzinovic Seed layer for solar cell conductive contact
US20150027524A1 (en) * 2011-09-09 2015-01-29 Heraeus Precious Metals North America Conshohocken Llc Silver solar cell contacts
US9039940B2 (en) 2011-03-25 2015-05-26 Samsung Electronics Co., Ltd. Conductive paste and electronic device, and solar cell including an electrode formed using the conductive paste
WO2015083917A1 (en) * 2013-12-06 2015-06-11 Samsung Electronics Co., Ltd. Method of pulverizing metallic glass, pulverized metallic glass, conductive paste, and electronic device
US9218898B2 (en) 2011-12-09 2015-12-22 Samsung Electronics Co., Ltd. Conductive paste and electronic device and solar cell including an electrode formed using the conductive paste
ES2583627T3 (en) 2010-02-04 2016-09-21 Toray Industries, Inc. pharmaceutical composition for the treatment and / or prevention of cancer
CN102891213B (en) * 2011-06-29 2016-01-13 屏东科技大学 The active solder and the electrode of a solar cell production method
CN104321883A (en) * 2011-12-13 2015-01-28 道康宁公司 Photovoltaic cell and method of forming the same
CN102426873B (en) * 2011-12-28 2014-12-10 彩虹集团公司 Silicon solar battery positive silver paste and preparation method thereof
KR101648242B1 (en) * 2013-03-27 2016-08-12 제일모직주식회사 Composition for forming solar cell electrode and electrode prepared using the same
US20180076343A1 (en) * 2015-03-27 2018-03-15 Heraeus Deutschland GmbH & Co. KG Electro-conductive pastes comprising an organic metal oxide
US4434084A (en) * 1981-09-23 1984-02-28 E. I. Du Pont De Nemours And Company Base metal conductor cathode coating for tantalum capacitors
US6420067B1 (en) * 1998-07-06 2002-07-16 Canon Kabushiki Kaisha MG-based negative electrode active material, method of manufacturing the same, hydrogen-storage alloy electrode, and alkali secondary battery
US7947134B2 (en) * 2007-04-04 2011-05-24 California Institute Of Technology Process for joining materials using bulk metallic glasses
JPS6262870A (en) 1985-09-12 1987-03-19 Masami Kobayashi Electromagnetic wave shielding coating material
US5709958A (en) 1992-08-27 1998-01-20 Kabushiki Kaisha Toshiba Electronic parts
JP3592006B2 (en) * 1996-11-12 2004-11-24 松下電器産業株式会社 For via hole filling conductive paste and printed wiring board using the same
KR100386521B1 (en) 1999-09-09 2003-06-02 캐논 가부시끼가이샤 Alkali rechargeable batteries and process for the production of said rechargeable batteries
CA2287648C (en) 1999-10-26 2007-06-19 Donald W. Kirk Electrodes de metal amorphe/verre metallique pour processus electrochimiques
JP3918450B2 (en) 2000-07-05 2007-05-23 株式会社村田製作所 The method of manufacturing a conductive powder, conductive powder, conductive paste and multilayer ceramic electronic component
JP3564089B2 (en) 2001-01-24 2004-09-08 株式会社ノリタケカンパニーリミテド Conductive paste and a method of manufacturing the same
KR100855169B1 (en) 2001-09-06 2008-08-29 가부시키가이샤 노리타케 캄파니 리미티드 Conductor composition and method for production thereof
JP3860445B2 (en) 2001-04-19 2006-12-20 独立行政法人科学技術振興機構 Cu-Be based amorphous alloy
JP2003013103A (en) 2001-06-26 2003-01-15 Murata Mfg Co Ltd Method for manufacturing electroconductive powder, electroconductive powder, electroconductive paste and laminated ceramic electronic component
CN1204570C (en) 2002-03-01 2005-06-01 北京科技大学 Rare earth iron base soft magnetic metallic glass having very large super cooling region
KR20040002317A (en) 2002-06-29 2004-01-07 풀무원건강생활 주식회사 The formulation and preparation process of Pseudomicroem ulsion utilizing phase inversion temperature
JP3963802B2 (en) 2002-08-30 2007-08-22 独立行政法人科学技術振興機構 Cu-based amorphous alloy
JP3913167B2 (en) 2002-12-25 2007-05-09 独立行政法人科学技術振興機構 Bulk Fe-based sintered alloy soft magnetic material and a manufacturing method thereof comprising a metallic glass
JP4439213B2 (en) 2003-07-31 2010-03-24 京セラ株式会社 Solar cell device and a manufacturing method thereof
JP4064340B2 (en) 2003-12-25 2008-03-19 昭和シェル石油株式会社 Manufacturing method of an integrated thin-film solar cell
KR100583230B1 (en) 2004-03-29 2006-05-25 한국과학기술연구원 Cu-based amorphous alloy composition
JP2007007648A (en) 2005-06-30 2007-01-18 Samsung Electronics Co Ltd Dispersant, paste composition including it and inorganic element manufactured using it, and display device including it
KR101178053B1 (en) 2005-09-27 2012-08-30 삼성전자주식회사 Carboxylic ester dispersant and sulfide phosphor paste composition comprising the same
KR101146667B1 (en) 2005-11-07 2012-05-24 삼성에스디아이 주식회사 Metal oxide paste composition and preparaton method of a semiconductor electrode using the same
KR101485304B1 (en) 2006-06-30 2015-01-23 미쓰비시 마테리알 가부시키가이샤 Composition for forming electrode in solar cell, method of forming the electrode, and solar cell employing electrode obtained by the formation method
KR100784914B1 (en) 2006-05-01 2007-12-11 학교법인연세대학교 Two Phase Metallic Glass Alloys with Multi-Pass Deformation Property
JPWO2008078374A1 (en) 2006-12-25 2010-04-15 ナミックス株式会社 Solar cell conductive paste
US9580810B2 (en) 2007-02-27 2017-02-28 Mitsubishi Materials Corporation Dispersion of metal nanoparticles, method for producing the same, and method for synthesizing metal nanoparticles
CN101186128A (en) * 2007-10-29 2008-05-28 福建师范大学 High temperature resistant high photics reflexive conductive film and preparation method thereof
JP5332624B2 (en) 2008-01-22 2013-11-06 三菱マテリアル株式会社 Metal nanoparticle dispersion and a method of manufacturing the same
KR101448448B1 (en) 2008-02-20 2014-10-14 주성엔지니어링(주) Thin film type Solar Cell and Method for manufacturing the same
EP2107136B1 (en) 2008-03-31 2014-12-31 Permelec Electrode Ltd. Manufacturing process of electrodes for electrolysis
US8158504B2 (en) 2008-05-30 2012-04-17 E. I. Du Pont De Nemours And Company Conductive compositions and processes for use in the manufacture of semiconductor devices—organic medium components
CN102292823B (en) 2008-06-09 2016-05-25 Sdsu 研究基金会 The organic light emitting diode and a photovoltaic cell with a three-dimensional electrode array assembly
JP5224514B2 (en) 2008-07-14 2013-07-03 国立大学法人東北大学 Nano-sized metallic glass structure
CN101359564B (en) * 2008-09-16 2011-08-17 彩虹集团公司 Anti-Ag diffusion photosensitive and conductive pulp and method for preparing same
JP5326647B2 (en) 2009-02-24 2013-10-30 三菱マテリアル株式会社 Method for manufacturing an electrode-forming composition of the solar cell
KR101741683B1 (en) 2010-08-05 2017-05-31 삼성전자주식회사 Conductive paste and electronic device and solar cell including an electrode formed using the conductive paste
CN102376379B (en) 2010-08-13 2016-04-20 三星电子株式会社 And conductive paste comprising an electrode formed of an electronic device and a solar cell
US7183018B2 (en) * 1998-09-18 2007-02-27 Canon Kabushiki Kaisha Electrode material for anode of rechargeable lithium battery, electrode structural body using said electrode material, rechargeable lithium battery using said electrode structural body, process for producing said electrode structural body, and process for producing said rechargeable lithium battery
US20100037990A1 (en) * 2005-08-12 2010-02-18 Daewoong Suh Bulk metallic glass solder material
Lin, T., et al, "Effect of Ni on glass-forming ability of Cu-Ti based amorphous alloys," Trans. Nonferrous Met. Soc. China 16 (2006) 604-606. *
NIST, Properties of Lead-Free Solders, Release 4.0, February, 2002. *
Reda, I. M., et al., "Amorphous Cu-Ag Films With High Stability," International Centre For Theoretical Physics, 1982. *
US9947809B2 (en) * 2009-11-11 2018-04-17 Samsung Electronics Co., Ltd. Conductive paste and electronic device and solar cell including an electrode formed using the conductive paste
US8974703B2 (en) * 2010-10-27 2015-03-10 Samsung Electronics Co., Ltd. Conductive paste and electronic device and solar cell including an electrode formed using the same
US8940195B2 (en) * 2011-01-13 2015-01-27 Samsung Electronics Co., Ltd. Conductive paste, and electronic device and solar cell including an electrode formed using the same
US9039943B2 (en) * 2011-03-28 2015-05-26 Samsung Electronics Co., Ltd. Conductive paste and electronic device and solar cell including an electrode formed using the conductive paste
US10038109B2 (en) * 2011-09-09 2018-07-31 Heraeus Precious Metals North America Conshohocken Llc Silver solar cell contacts
US20140000694A1 (en) * 2012-06-27 2014-01-02 Samsung Electronics Co., Ltd. Conductive Paste And Electronic Device And Solar Cell
US10074752B2 (en) * 2012-06-27 2018-09-11 Samsung Electronics Co., Ltd. Conductive paste and electronic device and solar cell
US9978889B2 (en) 2012-09-27 2018-05-22 Sunpower Corporation Conductive contact for solar cell
US9984787B2 (en) 2018-05-29 grant
EP2325848A2 (en) 2011-05-25 application
CN102097153A (en) 2011-06-15 application
JP2011103301A (en) 2011-05-26 application
EP2325848B1 (en) 2017-07-19 grant
EP2325848A3 (en) 2011-09-07 application
US7435361B2 (en) 2008-10-14 Conductive compositions and processes for use in the manufacture of semiconductor devices
US8008575B2 (en) 2011-08-30 Solar cell with reduced base diffusion area
US20090243111A1 (en) 2009-10-01 Semiconductor substrate, electrode forming method, and solar cell fabricating method
US20100258176A1 (en) 2010-10-14 Solar cell and method of manufacturing the same
US20100267194A1 (en) 2010-10-21 Method for applying electrical contacts on semiconducting substrates, semiconducting substrate and use of the method
US20110073173A1 (en) 2011-03-31 Solar cell and method for manufacturing the same
US20110180139A1 (en) 2011-07-28 Paste composition for electrode and photovoltaic cell
US20100319766A1 (en) 2010-12-23 Solar cell and method for manufacturing the same
JP2006302891A (en) 2006-11-02 Manufacturing method for semiconductor device and conductive composition used in it
WO2010011429A1 (en) 2010-01-28 Glass compositions used in conductors for photovoltaic cells
US20100068848A1 (en) 2010-03-18 One-step diffusion method for fabricating a differential doped solar cell
US20120031481A1 (en) 2012-02-09 Conductive paste and electronic device and solar cell including an electrode formed using the conductive paste
WO2011090214A1 (en) 2011-07-28 Paste composition for electrodes, and solar cell
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:LEE, EUN-SUNG;KIM, SE-YUN;JEE, SANG-SOO;REEL/FRAME:025682/0270