Patent US5983976 - Method and apparatus for manufacturing metallic parts by fine die casting - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsAn injection molding system includes a feeder in which a metal is melted and a first chamber into which a desired amount of melted metal is introduced. A piston in a second chamber first retracts to create suction, assisting in drawing in the melted metal into the second chamber from the first chamber...http://www.google.com/patents/US5983976?utm_source=gb-gplus-sharePatent US5983976 - Method and apparatus for manufacturing metallic parts by fine die castingAdvanced Patent SearchTry the new Google Patents, with machine-classified Google Scholar results, and Japanese and South Korean patents.Publication numberUS5983976 APublication typeGrantApplication numberUS 09/160,792Publication dateNov 16, 1999Filing dateSep 25, 1998Priority dateMar 31, 1998Fee statusPaidAlso published asDE69927900D1, DE69927900T2, EP0986444A1, EP0986444B1, US6283197, US20030066620, WO1999050006A1Publication number09160792, 160792, US 5983976 A, US 5983976A, US-A-5983976, US5983976 A, US5983976AInventorsKaname KonoOriginal AssigneeTakata CorporationExport CitationBiBTeX, EndNote, RefManPatent Citations (98), Non-Patent Citations (25), Referenced by (44), Classifications (14), Legal Events (5) External Links: USPTO, USPTO Assignment, EspacenetMethod and apparatus for manufacturing metallic parts by fine die casting
US 5983976 AAbstract
An injection molding system includes a feeder in which a metal is melted and a first chamber into which a desired amount of melted metal is introduced. A piston in a second chamber first retracts to create suction, assisting in drawing in the melted metal into the second chamber from the first chamber and evacuating gas. A ram then pushes some melted metal remaining in the first chamber into the second chamber, forcing out gas present in the second chamber. The piston then injects the melted metal out of the second chamber into a mold. The melted metal is preferably maintained in a liquid state throughout the system.
1. A method of injecting melted material into a mold, comprising:introducing the melted material into a first chamber; allowing at least a portion of the melted material to pass through said first chamber into a second chamber, wherein said allowing step comprises creating a suction in the second chamber to draw the portion of the melted material from the first chamber into the second chamber; pushing at least a portion of the melted material remaining in the first chamber into said second chamber; and injecting the melted material from the second chamber into the mold. 2. The method as claimed in claim 1, wherein the suction in the second chamber is created before the pushing of the melted material portion from the first chamber into the second chamber.
3. The method as claimed in claim 1, wherein a piston in the second chamber retracts to create suction that draws the melted material into the second chamber.
4. The method as claimed in claim 1, wherein a ram in the first chamber advances to push the melted material portion from the first chamber into the second chamber while covering an outlet port of the first chamber during injection to prevent the melted material from flowing between the first and the second chambers.
5. The method of claim 4, wherein the first chamber includes a valve that permits melted material to pass only in a direction toward the second chamber.
6. The method of claim 5, wherein the ram is advanced so that an end of the ram seals off an outlet port of the first chamber during injection to prevent melted material from passing between the first and the second chambers.
7. The method as claimed in claim 4, comprising rotating the ram to enhance the uniform temperature distribution of the melted material in the first chamber, and wherein the ram contains supporting fins.
8. The method as claimed in claim 1, wherein the melted material is a metal in a liquid state.
9. The method as claimed in claim 8, wherein the melted material is a melted magnesium alloy.
10. The method as claimed in claim 8, wherein the injected metal solidifies into a metal part in the mold.
11. The method as claimed in claim 1, wherein the first chamber is located above the second chamber to allow gravity to assist passage of the melted material from the first chamber into the second chamber.
12. The method as claimed in claim 11, wherein the melted material passing into the second chamber forces out at least a portion of at least one gas present in the second chamber out of the second chamber.
13. The method as claimed in claim 1, wherein at least a portion of at least one gas present in the second chamber escapes the second chamber through a second material in the wall of the second chamber which resists passage the melted material.
14. The method as claimed in claim 1, comprisingintroducing solid material into a feeder; melting the material in the feeder; and introducing the material into the first chamber from the feeder. 15. The method as claimed in claim 14, wherein the solid material is at least one metal ingot.
16. The method as claimed in claim 15, comprisingintroducing the at least one metal ingot into a third chamber; and transferring the at least one metal ingot from the third chamber into the feeder. 17. The method as claimed in claim 16, wherein at least one of the third chamber and the feeder contain an inert gas ambient.
18. The method as claimed in claim 17, wherein the inert gas comprises a at least one of argon, nitrogen, SF6 and CO2.
19. The method as claimed in claim 16, comprisingopening a first door to the third chamber; advancing at least one metal ingot into the third chamber; closing the first door; opening a second door; and advancing the at least one metal ingot from the third chamber into the feeder. 20. The method as claimed in claim 16, comprisingintroducing the metal ingots into the third chamber; and passing the metal ingots down a sloping surface into the feeder. 21. The method as claimed in claim 16, comprising controlling access to the feeder from the third chamber by movable cover plate.
22. The method as claimed in claim 21, wherein the movable cover plate contains an access aperture.
23. The method as claimed in claim 14, comprising controlling access to the feeder by movable transfer chamber.
24. The method as claimed in claim 23, wherein the movable transfer chamber comprises a cylinder containing an access aperture.
25. The method as claimed in claim 1, comprisinguncovering an injection nozzle in the second chamber; injecting the melted material into the mold through the injection nozzle by advancing a piston; and covering the injection nozzle. 26. The method as claimed in claim 25, wherein the injection nozzle is covered by a nozzle shut-off plate.
27. The method as claimed in claim 25, comprising partially advancing the piston, which is surrounded by a seal, to squeeze at least a portion of at least one gas present in the second chamber out of the second chamber through at least one of a material in the wall of the second chamber which resists passage of melted material, prior to injecting the melted material into the mold.
28. The method as claimed in claim 4, comprisingadvancing a ram in the first chamber so that the ram seals off an outlet port of the first chamber during injection to prevent the melted material from passing between the first and the second chambers; uncovering an injection nozzle in the second chamber; injecting the melted material into the mold through the injection nozzle by advancing a piston; retracting the ram; and retracting an outer portion of the piston to create a suction in the second chamber to draw the melted material from the first chamber into the second chamber, while leaving an inner portion of the piston fully advanced to cover the injection nozzle. Description
This application is related to application Ser. No. 09/160,330, filed on the same day as the current application, titled "Method And Apparatus For Manufacturing Metallic Parts by Injection Molding From the Semi-Solid State."
The invention relates to a method and apparatus for manufacturing metallic parts, more particularly to a method and apparatus for manufacturing metallic parts by a process involving injection of a melted metal into a mold, including die casting methods.
One conventional method used to produce molded metallic parts from melted metal is by die casting. Die casting methods use liquid metal during casting and, as a consequence, molded metallic parts produced from this method can have low densities. Molded metallic parts having low densities are not generally desirable because of their reduced mechanical strength, higher porosity, and larger micro shrinkage. It is thus difficult to accurately dimension conventional molded metallic parts and, once dimensioned, to maintain their shapes. Moreover, molded metallic parts produced from conventional die casting have difficulty in reducing the resilient stresses developed therein.
Thixotropic methods for producing molded metallic parts generally improve upon the die casting method by injection molding a metal from its thixotropic (semi-solid) state rather than from its liquid state. The result is a molded metallic part which has a higher density than one produced from the die casting method. Thixotropic methods are disclosed in U.S. Pat. Nos. 3,902,544 and 3,936,298, both of which are incorporated by reference herein.
Methods and apparatuses for manufacturing molded metallic parts from melted metal in its thixotropic state are also disclosed in U.S. Pat. No. 5,501,226 and Japanese patent publications 5-285626 and 5-285627, which are incorporated by reference herein. Methods of converting a metal into a thixotropic state by controlled heating and shearing in an extruder are disclosed in U.S. Pat. Nos. 5,501,226, 4,694,881 and 4,694,882. The systems disclosed in these patent documents are essentially in-line systems, in which the conversion of the metal alloy into a thixotropic state is assisted by an extruder and the pressurizing of the same for the purposes of injection molding; all these steps are carried out within a single cylindrical housing. It is difficult to accurately control all of the process parameters within a single cylindrical housing, especially temperature, shot volume, pressure, time, etc., and as a result, molded metallic parts of inconsistent characteristics are produced.
Moreover, some of these systems require that the metal supplied to the feeder be in pellet form. As a consequence, if a molded metallic part of undesired characteristics is produced by its system, recycling of the defective part is not possible unless the defective part is first recast in pellet form. Furthermore, metal parts made from metal in the thixotropic state which is injected into a mold may have an uneven surface. Such metal parts require further processing before they can be painted.
The present inventor's co-pending application, Ser. No. 08/873,922, filed on Jun. 12, 1997, which is incorporated by reference herein, describes a different and improved method for producing molded metallic parts from melted metal in a thixotropic state wherein the conversion of melted metal into the thixotropic state takes place in a physically separate location from the location where the metal is injected into the mold and under different conditions.
An improved system for manufacturing molded metallic parts, which is capable of accurately producing molded metallic parts of specified dimensions within a narrow density tolerance that operates with melted metal in a liquid state, is desired. Further, a production process for molded metallic parts that can consistently produce molded metallic parts of desired characteristics and that can easily accommodate recycling of defective parts is desired. Further, an improved production process for molded metallic parts made of lighter metals, like magnesium, is desired.
An object of the invention is to provide a method and apparatus for producing molded metallic parts through injection of melted metal into a mold.
Another object of the invention is to provide an improved injection molding system for producing molded metallic parts that is capable of producing molded metallic parts of accurate dimensions within a narrow density tolerance and operates using melted metal in a liquid state.
Still another object of the invention is to provide an injection molding system for molded metallic parts that is capable of producing metallic parts of desired characteristics in a consistent manner.
Still another object of the invention is to provide an injection molding system that minimizes the amount of gas trapped in liquid metal prior to its injection into the mold.
Still another object of the invention is to provide molded metallic parts having exceptionally smooth surfaces.
Still another object of the invention is to provide molded metallic parts having reduced porosity compared to parts produced by known die casting and thixotropic methods.
Still another object of the invention is to provide molded metallic parts that do not need to be further processed before they are painted.
Still another object of the invention is to provide an injection molding system for producing molded metallic parts that accommodates recycling of defective molded metallic parts easily.
These and other objects are accomplished by an improved injection molding method for producing molded metallic parts comprising the steps of introducing melted metal into a first chamber through a feeder port, allowing at least a portion of the melted metal to flow through said first chamber toward an outlet port, drawing into a second chamber at least a portion of the melted metal through the outlet port under a suction created in said second chamber, pushing at least a portion of the melted metal remaining in the first chamber into said second chamber, and injecting the melted metal from the second chamber into a mold.
The improved system comprises a feeder in which the metal is melted. Melted metal is allowed to flow from the feeder through a feeder port into a first chamber. At least a portion of the melted metal is drawn into a second chamber, assisted by suction through an outlet port leading from the first chamber into the second chamber. A ram in the first chamber pushes some of the remaining melted metal from the first chamber through the outlet port leading into the second chamber, thereby forcing out gas that has accumulated in the second chamber between the melted metal and a piston (commonly referred to as the "plunger") that is positioned inside the second chamber. The pressure from the melted metal being driven into the second chamber by the ram forces the gas between the melted metal and the piston to flow past the piston through the small space between the piston and the wall of the second chamber. The piston in the second chamber then injects the melted metal, which is substantially gas-free, into a mold. Before the injection, the piston in the second chamber is retracted to draw in the melted metal from the first chamber by creating suction and also to regulate the volume of melted metal that is held in the second chamber prior to injection so that it precisely corresponds to the size of the molded part.
The above-described process and system provide a very precise control of the injection volume, to within �0.5% by weight or less, because the injection volume is determined in accordance with the position of the piston and any gas that is present in the melted metal, which can be about 20% by volume, is forced out by operation the ram advancing, before the melted metal is injected.
Further, a fine die-cast method according to the invention is more advantageous than current thixotropic processes because conversion of metal into the thixotropic state takes more time. With the fine die-cast method according to the invention, the injection cycle time is reduced to about 30 seconds, a 50% reduction when compared to current thixotropic processes.
Also, the method of the present invention can be used to mold parts of a liquid material that are more preferred than parts molded from current thixotropic processes. They generally require less post-molding processing, given their more accurate molding volume and smooth surfaces. This permits a production process that is stable over many runs.
In addition, the method of the present invention can provide molded parts of extremely fine dimensions, having thicknesses less than 1 mm for a rectangular-shaped part measuring about 21.0 cm by 29.7 cm (which is roughly the size of a DIN size A4 sheet of paper) and also having more complex structures.
FIG. 1 is a schematic illustration of a side view of the injection molding system according to one embodiment of the invention;
FIG. 2A is a side view showing one embodiment of a valve on the ram when it is in the position that prevents melted metal from flowing to positions to the right of the valve;
FIG. 2B is a side view showing one embodiment of a valve on the ram when it is in the position that permits melted metal to flow from the right of the valve to positions to the left of the valve;
FIG. 2C is a front view showing one embodiment of a valve when it is not fitted onto the ram;
FIG. 2D is a side view showing one embodiment of a valve when it is not fitted onto the ram;
FIG. 3 is a side view of an alternative embodiment of the feeder tank;
FIG. 4A is a side view of an embodiment of the nozzle shut-off plate which includes a die plate that rests flush against the nozzle;
FIG. 4B is a side view of an alternative embodiment of the nozzle shut-off plate which includes a recess in the die assembly to receive the nozzle; and
FIG. 4C is a front view of an alternative embodiment of a die assembly which has a receiving slot to guide the nozzle shut-off plate;
FIG. 4D is a side view of the shut-off plate guide and the drive assembly for the nozzle shut-off plate.
FIG. 5A is a top view of an embodiment of a loading system used to load metal ingots into the apparatus of the present invention;
FIG. 5B is a side view of another embodiment of a loading system which includes sealing doors;
FIG. 5C is a side view of an embodiment of a loading system which includes a vacuum pump;
FIG. 5D is a side view of an embodiment of a loading system which includes inert gas screens;
FIGS. 5E-H are top views of an alternative embodiment of a loading system used to load metal ingots into the apparatus of the present invention;
FIG. 5I is a three dimensional view of an alternative embodiment of a loading system used to load metal ingots into the apparatus of the present invention;
FIG. 5J is a side view of an elevator used to deliver the metal ingots to the conveyor of the loading system;
FIG. 5K is a side view of an embodiment of a feeder which utilizes substantially vertical outlet containment rods;
FIG. 6A is a photomicrograph of a metal sample made by a prior art method;
FIG. 6B is a photomicrograph of a metal sample made by a method of the present invention;
FIG. 7A is a schematic illustration of a side view of the injection molding system according to an embodiment of the invention which contains supporting fins around the ram;
FIGS. 7B-G are cross sectional and three dimensional views of specific arrangements of the support fins.
FIGS. 8A-D are side views of an embodiment of an injection chamber which includes a two part piston.
FIG. 9 shows the side view of plug formation in prior art injection nozzles.
FIG. 10 is a side view of an embodiment of an injection chamber with includes an outlet port.
FIGS. 11A-B are side views of an alternative method of operating the piston.
FIGS. 12A-B are side views of an embodiment of a barrel which includes a two part ram.
In the discussion of the preferred embodiment which follows, a metal alloy is produced by injection molding from a magnesium (Mg) alloy ingot or pellets which are melted and processed in a liquid state. The invention is not limited to processing of Mg and is equally applicable to other types of materials, metals and metal alloys.
The terms "melted metal" and "melted material" as used herein encompasses metals, metal alloys and other materials which can be converted to a liquid state and processed in an injection molding system. A wide range of such metals is potentially useful in this invention, including aluminum (Al), Al alloys, zinc (Zn), Zn alloys, and the like.
Unless otherwise indicated, the terms "a" or "an" refer to one or more. Unless otherwise indicated, the term "gas" refers to any gas (including air) that can be present in the injection chamber at start-up or that is trapped in the injection chamber and forced out during operation of the invention's system.
Specific temperature and temperature ranges cited in the following description of the preferred embodiment are applicable to the preferred embodiment for processing Mg alloy in a liquid state, but could readily be modified in accordance with the principles of the invention by those skilled in the art in order to accommodate other metals and metal alloys. For example, some Zn alloys become liquid at temperatures above 450� C., and the temperatures in the injection molding system of the present invention can be adjusted for processing of Zn alloys.
FIG. 1 illustrates an injection molding system 10 according to a first embodiment of the invention. The system 10 includes pre-heat tank 19 where Mg alloy pieces or ingots 18 are pre-heated to approximately 250� C. A conveyor belt 20 transfers the pre-heated Mg alloy pieces or ingots 18 into a holding tank 12. Other transporting means can be used. A metering device shown as a threaded screw 21 feeds the Mg alloy pieces or ingots 18 into a feeder 23. The feeder 23 is provided with at least one heating element 25 disposed around its outer periphery. The heating element 25 may be of any conventional type and operates to maintain the feeder 23 at a temperature high enough to keep the metal alloy supplied through the feeder 23 in a liquid state. For a Mg alloy ingot, this temperature would be about 600� C. or greater. Two level detectors 22 detect minimum and maximum levels of melted metal in the feeder 23. When the upper level detector 22 detects that the level of melted metal has risen to a maximum point, it relays a signal to a microprocessor control unit (not shown) which instructs the screw 21 to stop dispensing. When the lower level detector 22 detects that the level of melted metal has been depleted to a minimum point, it relays a signal to the control unit which activates the screw 21 so that more Mg alloy is dispensed into the feeder 23.
Preferably, sufficient metal should be kept in the feeder 23 to supply about 20 times the volume needed for one injection cycle (or shot). This is because the amount of time required to melt the metal necessary for one injection cycle is longer than the injection cycle time, which in the preferred embodiment is about 30 seconds.
The feeder 23 further includes a filter 24, which may be in the form of a grate whose openings are small enough to prevent Mg alloy pieces 18 from falling through while they are being melted. This is primarily a concern when the feeder 23 is initially started. After that, alloy pieces will fall into the molten bath and be melted, although larger pieces could also be introduced later on without concern. A mixer (not shown) in feeder 23 may be included for the purposes of evenly distributing the heat from the heating element 25 to the metal supplied to the feeder 23.
The feeder 23, pre-heat tank 19, and all elements therebetween contain an atmosphere of an inert gas to minimize oxidizing of the pre-heated and melted metal. A mixture of carbon dioxide (CO2) and sulfur fluoride (SF6) gas is preferred. However, other gasses, such as CO2, SF6, nitrogen or argon may be used alone or in any combination with each other. The inert gas may be introduced (e.g. from a pressurized tank) into the feeder 23 through port 11 to create an inert gas atmosphere above the bath. The inert gas also travels around the screw and into the pre-heat tank 19 to also minimize oxidizing there, as well. It is therefore preferred for the entire feeding system as described to be maintained under an inert gas environment.
The melted metal is subsequently supplied into a temperature-controlled barrel 30 by way of gravity through a feeder port 27 which may optionally be supplied with a valve serving as a stopper (not shown). Preferably, no valve is present. A ram 32 is arranged coaxially with the barrel 30 and extends along the center axis of the barrel 30. The outer diameter of the ram 32 is smaller than the inner diameter of the barrel 30 such that melted metal flows in the space between the ram 32 and the barrel 30. The ram 32 is also controlled by motor 33 for axial movement in both retracting and advancing directions along the barrel 30 and for rotation around its own axis if stirring of the melted metal is desired inside barrel 30.
A valve 17 is mounted around the outer circumference of the ram 32 to separate the barrel 30 into upper and lower chambers. The valve 17 opens and closes to selectively permit and block the flow of metal between the upper and lower chambers of the barrel 30. Suitable valves having such a function are known per se to those skilled in the art, and any of them may be used for purposes of the present invention. Preferably, the valve 17 is frictionally mounted on an inner circumference of the barrel 30 and slidably mounted on the outer circumference of the ram 32 such that, when, for example, the ram 32 retracts upwardly in the barrel 30, the valve 17 moves relative to the ram 32 to permit flow of melted metal therethrough, and when, for example, the ram 32 advances downwardly in the barrel 30, the valve 17 moves relative to the ram 32 to block flow therethrough.
FIG. 2A is a side view showing one embodiment of a valve on the ram when it is in the position that prevents melted metal from flowing to positions upstream of (to the right of) the valve. FIG. 2B is a side view showing one embodiment of a valve on the ram when it is in the position that permits melted metal to flow downstream of the valve (to the left of the valve). FIG. 2C is a front view showing one embodiment of a valve when it is not fitted onto the ram. FIG. 2D is a side view showing one embodiment of a valve when it is not fitted onto the ram.
In the closed position of FIG. 2A, the rear section 17b of the valve 17 abuts the body 32b of the ram 32. The blockage of the flow in this position permits the ram 32 to push the metal in the lower chamber into an injection chamber 50 through an outlet port 37 (see FIG. 1) without the metal flowing back (as shown in FIG. 2A) into the upper chamber. In the open position of FIG. 2B, the front section 17a of the valve 17 abuts the head 32a of the ram 32. The metal is permitted to flow through the valve in this position because the front section 17a of the valve 17 has gaps formed between toothed portions and the flow through the valve 17 takes place through these gaps. As a result, when the valve 17 is in the open position, the metal in the upper chamber flows into and collects in the lower chamber.
The ram 32 as shown in the Figures has a pointed tip, but any shape may be used, including a blunt end or a rounded end. Preferably, the end of ram 32 has a shape capable of blocking outlet port 37 to prevent the flow of melted metal between barrel 30 and injection chamber 50 if ram 32 is fully advanced inside barrel 30. While injection takes place, ram 32 is preferably fully advanced inside barrel 30 so that outlet port 37 is closed. However, the ram 32 need not be fully advanced since valve 17 and the melted metal that occupies the lower chamber of barrel 30 would also prevent melted metal from leaving the second chamber during injection. After injection, the ram 32 is retracted (but may continue rotating if rotation is being used to stir the melted metal inside barrel 30), and a piston 45 which is housed in the injection chamber 50 begins retracting (moved to the right as shown in FIG. 1) to expand the volume of the injection chamber 50 to a desired volume according to the dimensions of the molded part being produced. The piston 45 is stopped when the volume of the injection chamber 50 becomes equal to the desired injection volume. The piston 45 may be retracted at the same time that ram 32 is being retracted or after ram 32 has been retracted to a desired position.
After piston 45 is stopped, the ram 32 is advanced downward, and, as a result, a portion of the metal collected in the lower chamber of barrel 30 is pushed into the injection chamber 50 through the outlet port 37. The pressure of the metal entering into injection chamber 50 assists in driving out gas present in the injection chamber 50 that accumulates between the melted metal and piston 45. The ram 32 preferably advances through barrel 30 until its end closes off outlet port 37, and the ram 32 preferably remains in this position to keep outlet port 37 sealed off until injection is complete and the next shot is started.
During each shot, a certain amount of gas accumulates between the melted metal and the piston 45 as the melted metal enters injection chamber 50. The volume of this gas can make up as much as 20% of the volume of the injection chamber 50. Injecting such a melted metal/gas mix into a mold can result in molded parts that have uneven surfaces, porosity (caused by gas bubbles trapped in the metal's surface), or other imperfections including those that result from an inconsistent volume of melted metal being injected. Removing as much gas as possible before injection is desired. In the method of the present invention, that gas evacuation is primarily accomplished in two ways. First, the piston 45 and injection chamber 50 can evacuate gas like a pharmaceutical syringe that draws in liquid from a container of liquid. Specifically, as piston 45 retracts, it creates a suction to draw in melted metal from the barrel 30 into the injection chamber 50 and it pushes gas out behind it. Secondly, the additional portion of melted metal driven into the second chamber by ram 32 forces the gas that accumulates between the melted metal and the piston 45 to escape around the small space between the piston 45 and the wall of the second chamber (i.e., the gas is forced out to the right of piston 45 due to the pressure of the melted metal). Optionally, an O-ring seal or other implement may be fitted around at least a portion of piston 45 that allows the gas to pass behind piston 45 and out of the system but not back in. An injection nozzle 57 is provided with a nozzle shut-off plate 15 which is lowered to prevent the melted metal from escaping out of the injection chamber 50 when the ram 32 pushes the metal into the injection chamber 50. When the injection chamber 50 has been filled with the metal and substantially all gas has been forced out, the nozzle shut-off plate 15 is pulled up and the nozzle 57 is moved forward (to the left in FIG. 1) to contact the opening in a die 14. In the preferred embodiment, the movement of the nozzle 57 is achieved by mounting the entire apparatus on a slide and moving the entire apparatus towards the die 14 (to the left in FIG. 1).
Simultaneously, the piston 45 is pushed to the left, relative to the injection chamber 50, to force the melted metal in the injection chamber 50 through the die 14 into a mold 13. After a pre-set dwell time, the two halves of the die are opened and the molded metallic part is removed, so that a new cycle can begin.
The melted metal, while housed in injection chamber 50, is substantially sealed off from gas that would otherwise enter injection chamber 50 from outside the machine by virtue of nozzle shut-off plate 15, seal 41 on piston 45, and the melted metal which continuously occupies barrel 30 during operation. Although gas is present in injection chamber 50 prior to start-up, the first run of shots drives out substantially all gas in injection chamber 50. Thus, the melted metal that is injected from injection chamber 50 into mold 13 is substantially free of gas. Preferably, the amount of gas present in injection chamber 50 during injection is less than 20%, more preferably less than or equal to 1% by volume of the second chamber.
As shown in FIG. 1, heating elements 70f-70j are also provided along the lengths of the injection chamber 50. The temperature in the feeder differs depending on the material present in the feeder. For the AZ91 Mg alloy, heating elements 25 are preferably controlled so that the temperature in the feeder 23 is about 640� C. near the upper surface of the melted Mg alloy and about 660� C. near the lower region of feeder 23. Heating elements referenced and prefixed by the numeral 70 are preferably resistance heating elements.
In the barrel 30, the temperature near heating element 70a is preferably maintained at around 640� C. for the AZ91 Mg alloy. The temperature near heating element 70b is preferably maintained at around 650� C. for the AZ91 Mg alloy. The temperature near heating element 70e is preferably maintained at around 630� C. for the AZ91 Mg alloy. These temperatures facilitate the downward flow of metal toward outlet port 37 and inhibit flow in the opposite direction.
In the injection chamber 50, the temperature near heating elements 70h, 70i, and 70j is preferably maintained at around 620� C. for the AZ91 Mg alloy. These temperatures are sufficiently high to maintain the melted metal entirely in the liquid state from the time it exits the feeder 23 into the barrel 30 to the time the melted metal is injected into the mold 14 from the injection chamber 50. The temperature near heating elements 70g and 70f is preferably maintained at around 570� C. for the AZ91 Mg alloy. The lower temperature behind the seal 41 helps prevent the metal from flowing past the seal 41.
Using the preceding temperatures at these locations permits molding of the AZ91 Mg alloy in the liquid state. Under these conditions, one cycle lasts approximately 30 seconds. Molded metallic parts having extremely smooth surfaces and minimal porosity can be produced, which allows them to be painted directly without any further processing. The castings also have extremely accurate dimensions and consistency, and can be produced with thicknesses of less than 1 mm when the part roughly has the dimensions of a DIN size A4 sheet of paper (21.0 cm by 29.7 cm). Preferably, the range of thickness of molded parts produced according to the invention is between 0.5 and 1 mm for parts that have roughly the dimensions of a DIN size A4 sheet of paper. With known die casting and thixotropic methods, thicknesses no less than about 1.3 mm can be obtained for parts that have roughly the dimensions of a DIN size A4 sheet of paper.
FIG. 6A shows a photomicrograph of a Mg alloy sample made by a conventional thixotropic method at a magnification of 350 times. As noted previously, the prior art requires injection molding of the metal from its thixotropic state in order to obtain sufficiently high metal density to improve the mechanical strength of the cast metal part.
FIG. 6B shows a photomicrograph of a Mg alloy sample made by the method of the current invention at a magnification of 350 times. The sample area and thickness are similar to those of the sample shown in FIG. 6A. The sample in FIG. 6B was made by fine die casting the metal from its liquid state according to this invention. The surface of the sample is extremely smooth and has no visible voids. Such a sample can be painted directly without any further processing, thus reducing process cost. Furthermore, the sample made according to the present invention has minimal porosity and high strength. Thus, it is believed that the method of the current invention is the first method that allows the achievement of a low porosity cast metal together with a smooth surface that requires no further processing, because it is the first process that uses a uniform liquid metal volume that is substantially free of trapped gas. The prior art cast metal parts made by liquid state injection methods suffer from high porosity and low mechanical strength due to the trapped gas in the liquid metal.
FIG. 3 shows an alternative embodiment of the invention having a feeder 23'. Like the feeder 23 of FIG. 1, the feeder 23' of FIG. 3 includes metering screw 21', level indicators 22', and heating elements 25'. However, the feeder 23' of FIG. 3 has a lower region with a bottom surface that is at a lower position than feeder port 27'. This lower region catches sludge and other material that is heavier than the melted metal and prevents them from passing through the feeder port 27', ensuring that pure melted metal enters barrel 30. Another opening (not shown) may be provided from this lower region for periodically extracting the heavier material.
FIG. 4A shows an alternative embodiment of the invention having a nozzle shut-off plate 15' that is positioned a predetermined distance away from a die 14'. In this alternative embodiment, when the nozzle shut-off plate 15' is pulled up, the nozzle 57 is pushed to the left to enter a relatively deep recess that extends partially into support walls 59 and 60. Die 14' is then positioned to abut support walls 59 and 60. The recess ensures proper alignment of the nozzle 57' with the opening that leads into mold 13'. The nozzle shut-off plate may be maintained at a temperature that minimizes solidification of the liquid metal in the nozzle. This may be achieved by providing a heating element on or inside the shut-off plate. However, the plate may also be left unheated.
FIG. 4B shows a side view of an alternative embodiment of the invention having a nozzle shut-off plate 15" that retracts and advances through a slot just inside the right edge of die 14". In this alternative embodiment, when the nozzle shut-off plate 15" is pulled up, the nozzle 57" is pushed to the left to enter a relatively shallow recess that extends partially into the die 14". The shallow recess ensures proper alignment of the nozzle 57" with the opening that leads into mold 13". Support walls 59' and 60' assist in aligning the nozzle.
FIG. 4C shows a front view of an alternative embodiment of the invention having a nozzle shut-off plate 15"' that retracts and advances through a slot in the face of die 14"'. In this alternative embodiment, when the nozzle shut-off plate 15"' is pulled up, a shallow recess, shown as the larger circle around the smaller circle that is the opening into the die 14"', is exposed. The shallow recess ensures proper alignment of the nozzle (not shown) with the opening into die 14"'. In an alternative embodiment (not shown), the shallow recess may be placed on support walls 59' and 60' enclosing the nozzle 57, with the shut-off plate moving within that recess.
A further embodiment of the present invention shown in FIG. 4D is directed to operation of nozzle shut-off plates 15, 15', 15" and 15"' shown in FIGS. 1 and 4A-C. In this embodiment, the shut-off plate 15 moves up and down between the face of the die 14 and support walls 59 and 60 inside the shut-off plate guide 16. Shut-off plate guide 16 could be a vertical void, which can be formed between the die face and the support walls as shown in FIG. 1 or inside the die as shown in FIGS. 4A-C. The guide 16 can also comprise a void in another direction, such as horizontal. The shut-off plate 15 is moved through the guide 16 by a cylindrical motor, an oil cylinder and/or an air cylinder 46. The cylindrical motor 46 is held upright by a cylinder guide 47.
In one embodiment, metal ingots can be loaded into the apparatus of the present invention instead of metal pellets or chips. There are several advantages of using ingots instead of metal pellets and chips. First, the ingots are cheaper than pellets or chips. Second, the pellets tend to agglomerate into clusters on the surface of the liquid metal in the feeder. This increases the time it takes to melt the pellets, because only the pellets on the bottom of the cluster are in contact with the liquid metal. The pellets on top of the cluster are only in contact with the solid pellets below them. On the other hand, the heavier ingots sink to the bottom of the feeder. Therefore, since the entire ingot is surrounded by the liquid metal, it melts faster than the pellets. A loading system configured for loading ingots may also be used to load recycled molded metallic parts of undesired characteristics into the feeder without recasting the defective part in pellet form. Thus, recycled parts may be used instead of ingots according to another aspect of this embodiment.
FIG. 5A shows a top view of an alternative loading system to that shown in FIG. 1 for loading metal ingots 63 into the feeder 23. Ingots may comprise Mg, Zn, Al or alloys thereof or other metals and alloys. The ingots 63 are transported from a first conveyor belt 61 onto a second conveyor belt 62. A push arm 64 controlled by a conventional motor 65 pushes the ingots 63 into the holding chamber 66. The push arm has a size sufficient to completely cover the opening to the holding chamber. The push arm can form an air tight seal with the opening into the holding chamber, if desired. The ingots 63 inside the holding chamber 66 end up on a downward sloping part (e.g. inclined surface) 67, where a motor controlled piston 68 pushes the ingots 63 into the feeder 23. The holding chamber is preferably maintained under an inert gas ambient, supplied from a gas port. The gas may be argon, nitrogen or a sulfur hexafluoride and carbon dioxide mix. The gas pressure in the holding chamber 66 should preferably be maintained at a pressure above one atmosphere to prevent outside air, which contains oxygen, from reaching the feeder 23. The gas pressure and/or the position of the ingots may be monitored by one or more sensors. The controlled atmosphere in the holding chamber 66 allows a decreased amount of air in the feeder and thus decreases a chance of explosion.
FIG. 5B shows a side view of another alternative loading system to that shown in FIGS. 1 and 5A for loading metal ingots 63 into the feeder 23. The ingots 63 are transported on a conveyor 81 to a holding chamber 86, which may have a downward sloping shape. Access to the holding chamber is controlled by a first door 82. Egress from the holding chamber is controlled by a second door 84. The chamber may be heated by heaters 85 to 100-200 � C. to evaporate moisture on the surface of the ingots. The holding chamber 86 operates as follows. First, door 82 is opened as ingot 63 approaches it. Door 82 can preferably be opened by moving up, down or sideways through the walls of chamber 86. The ingot 63 enters the chamber 86 and the first door 82 is closed. After the first door 82 is closed, the second door 84 is opened and the ingot 63 moves out of chamber 86. The conveyor 81 can move continuously through chamber 86 with doors 82 and 84 opened and closed while the conveyor is moving. Alternatively, the conveyor 81 moves intermittently. It stops when an ingot approaches door 82 and when the ingot is inside the chamber 86. This allows doors to be sealed hermetically. The conveyor 81 may also end at the sloping part of chamber 86, such that the ingots slide down under the force of gravity.
In another alternative embodiment (not shown), the loading system shown in FIG. 5A can be used with door 82 of FIG. 5B positioned between conveyor 62 and chamber 66 and with door 84 of FIG. 5B positioned between chamber area 67 and the melt tank (e.g. melt feeder) 23. Door 82 opens synchronously with the movement of the push arm 64, while door 84 opens synchronously with the movement of piston 68.
The holding chamber 86 in FIG. 5B is connected to the melt tank 23". Melt tank 23" contains a single metal level detector 22". Alternatively, two level detectors 22, shown in FIG. 1 can be used. Tank 23" also contains gas port 11". An inert gas, such as at least one gas selected from a group comprising nitrogen, argon, SF6 and CO2, is introduced (e.g. under pressure from a pressurized tank) into melt chamber 23". The gas pressure of the pumped gas is preferably above one atmosphere to keep air from entering the melt tank 23" through holding chamber 86 (the pumped gas flows out through chamber 86, thus preventing air from flowing into chamber 86).
The melt chamber shown in FIG. 5B also contains heaters 25", a filter or screen 24" and a feeder port 27" located above the bottom of the tank, similar to feeder tank 23' shown in FIG. 3. The filter may be formed inside port 27" or above port 27", as shown in FIG. 1.
Alternatively, a vacuum pump, 87 shown in FIG. 5C can be attached in chamber 86, between doors 82 and 84. As the ingot 63 enters chamber 86, both doors 82, 84 are closed and the vacuum pump creates a near vacuum in chamber 86. Door 84 is then opened to release ingot 63 into melt tank 23" without allowing any air to enter melt tank 23" because chamber 86 was at vacuum when door 84 is opened.
As shown in FIG. 5D an inert gas screen 90 can be made to flow from inert gas source(s) 88 across the back of door 82 and/or 84 and out through optional suction pipes or vents 89. The inert gas screen 90 keeps air from entering chamber 86 and tank 23". The inert gas can comprise at least on gas selected from a group comprising argon, nitrogen, CO2 and SF6. The gas screen of FIG. 5D can be used in combination with vacuum pump of FIG. 5C to obtain the least air penetration into melt tank 23". The air control measures, such as melt tank gas port 11", doors 82, 84, vacuum pump 87 and inert gas screen(s) 90 are all used to prevent the introduction of air into the melt tank and/or the holding chamber to reduce the possibility of explosion.
FIGS. 5E and 5F show an alternative loading system to that shown in FIGS. 5A. The holding chamber 66' utilizes a movable aperture plate 72. FIG. 5E shows a top view of the loading system where the access to the feeder 23 is closed. The movable aperture plate 72 contains an aperture 73 which is larger than an ingot. When no more ingots should be added to the feeder 23, the plate 72 is moved to one side by a movable arm 74 such that the plate covers the entrance to the feeder. As shown in FIG. 5F, when additional ingots should be added into the feeder 23, the plate 72 is moved to the other side, such that the aperture 73 corresponds to the opening to the feeder 23. This way, the ingots coming off the conveyor 61' pass through aperture 73 into the feeder 23. In the embodiment shown in FIGS. 5E and 5F the aperture plate 72 is utilized instead of a push arm 64 and piston 68 shown in FIG. 5B. However, the aperture cover plate 72 can be utilized in addition to the push arm 64 and piston 68. In this case, the plate 72 is blocks access to ingots sliding down sloped surface 67.
FIGS. 5G and 5H show an alternative loading system to that shown in FIGS. 5E and 5F. In this embodiment, the holding chamber 66" utilizes a movable cover plate 75 instead of a movable aperture plate 72. The cover plate 75 has a roughly circular shape which is sufficient to cover the opening to the feeder 23. FIG. 5G shows a top view of the loading system where the access to the feeder 23 is closed. A movable arm 74' moves the cover plate 75 over the opening to the feeder 23 to block access of ingots coming off conveyor 61". As shown in FIG. 5H, when additional ingots should be added into the feeder 23, the cover plate 75 is moved to the other side or raised up (out of the plane of the drawing), to expose the opening to the feeder 23. The ingots coming off the conveyor 61" can drop directly into the feeder 23. In the embodiment shown in FIGS. 5G and 5H the cover plate 75 is utilized instead of a push arm 64 and piston 68 shown in FIG. 5A. However, the cover plate 75 can be utilized in addition to the push arm 64 and piston 68.
FIG. 5I shows an alternative loading system to that shown in FIG. 5A. The opening 78 to the feeder 23 is covered by a movable transfer chamber 76, such as a cylinder. Cylinder 76 has an aperture 77. Aperture 77 is at the same level as the conveyor 81', as shown in FIG. 5J. When ever it is desired to add more ingots 63 to the feeder 23, a movable arm 74" moves the cylinder into a position where the aperture 77 lines up with the end of the conveyor 81' to allow the ingots to fall from conveyor 81' through aperture 77 into cylinder 76 and down into the feeder 23 through opening 78. To close access to the feeder 23, movable arm 74" moves the cylinder 76 in any direction (e.g. up, to the left or to the right) such that the end of the conveyor is no longer aligned with the aperture 77. While transfer chamber 76 has been described as a cylinder, it may have any other shapes, such as a cube, etc. The transfer chamber may also be used with a push arm 64 and piston 68 shown in FIG. 5A. In this case, the ingots 63 would slide down the sloping surface 67 into the transfer chamber instead of dropping directly into the feeder 23. The transfer chamber 76 may also be used with the holding chamber 86 FIG. 5B. This is shown in FIG. 5J.
FIG. 5J shows elevator 100 which delivers the ingots to the conveyor 81' in the holding chamber 86'. As shown in FIG. 5B, the holding chamber 86 may have one or two doors (82,84). In FIG. 5J, only one door 82' is shown for clarity. The ingots are moved up toward the holding chamber 86' on elevator platforms 101. Each platform comprises a platform base 102 and a movable platform top 103 connected by at least one connector 104. As each platform reaches the top of the conveyor 81', a lifting member 105 moves up pole 106 and pushes up on the back end of the platform top 103. The back end of the platform top 103 is lifted above platform base 102 by the lifting member 105, which causes the ingot(s) 63 to slide off the platform top onto the conveyor 81'. The ingots 63 pass from the conveyor 81' into the feeder. The ingots 63 may optionally pass through the transfer chamber 76 shown in FIGS. 5I and 5J. After the ingot(s) are removed from the platform top, the lifting member moves down the pole 106, placing the platform top 103 onto the platform base 102. The lifting member 105 then disengages the first platform 101, the next platform 101 is moved up and the process is repeated.
Connector 104 may be a bolt which rotably connects platform top 103 and base 102. Preferably, the platform top is rotated up about 20 degrees by the lifting member 105. Alternatively, the entire platform 101, and not just the platform top may be lifted by the lifting member. The elevator 100 may also be used with the holding chamber 66 shown in FIG. 5A and ingots may slide into the feeder 23 down sloped surface 67.
Preferably, the movement of the lifting member 105 is synchronized with the opening of the doors. For example, as the lifting member 105 moves up on the pole 106, the door 82' is simultaneously opened to allow the ingot 63 to pass into the holding chamber 86'. Furthermore, the cover plates 72 or 75 shown in FIGS. 5E-H or the transfer chamber 76 shown in FIG. 5I may also be synchronized with the door 82'. Thus, after the door 82' is closed, the cover plates or the transfer chamber may be moved to open access to the feeder 23. If back door 84 (shown in FIG. 5B) is also present, it should be opened after the front door 82' is closed. Elevator 100 may also be used with conveyor 61 and holding chamber 66 shown in FIG. 5A.
FIG. 5K shows another embodiment of a feeder 23 utilizing substantially vertical outlet containment rods. In FIG. 1 (as well as FIG. 5B) feeder port 27 was protected by a filter 24 is a shape of a grate. A grate is required to prevent unmelted metal pieces from exiting feeder 23 into the barrel 30 through feeder port 27. However, metal ingots 63 sink to the bottom of the feeder port and lie flat on the grate. This positioning is not desirable because the ingots may substantially block liquid metal flow through feeder port 27"' into the barrel 30. To prevent ingots from blocking the grate, outlet containment rods 76 should be utilized above the feeder port 27"' as shown in FIG. 5K. The rods may be of any shape as long as they prevent the sinking ingots 63 from laying flat across the feeder port 27"' and blocking it. For example, as shown in FIG. 5K, the rods in the middle of the feeder port may rise above the rods near the circumference of the feeder port to force the ingots 63 to rest on their side toward the edge of the feeder 23"' while melting. Feed tank 23"' may also have a lower region with a bottom surface that is at a lower position than the feeder port 27"', as shown in FIG. 3. The sinking ingots which come in contact with rods 76 will be deflected sideways into the lower region. The ingots will melt in the lower region without blocking the feeder port 27"'.
FIG. 7A shows a side view of an alternative embodiment of the invention having supporting ribs or fins 34 arranged on ram 32. FIG. 7A is not to scale and the barrel 30 thickness has been exaggerated for clarity. The heaters 70 are present but have been omitted from FIG. 7 for clarity. The fins 34 are preferably attached to the ram 32 and can slide on the inner circumference of the barrel 30, both coaxially with the length of the barrel and/or in a circular motion about the barrel axis 38. The movement produces a rotation of the fins 34 around the inner circumference of the barrel 30. Alternatively, the fins 34 may be attached to the inner circumference of the barrel 30 in such a manner as to allow the bare ram 32 to slide by. The fins 34 can be made of the same material as the ram 32 or form a different material that can withstand the required process temperatures. The purpose of the fins is two fold. The first purpose is to prevent the ram 32 from tilting and wobbling away from the barrel axis 38. Since the ram 32 is fairly long, without the fins 34 it has a tendency to tilt. The unsupported front part of the ram comes closer to the bottom part of the interior barrel surface than to the top interior barrel surface under the weight of gravity. Fins 34 prevent ram from tilting and wobbling by making contact with the inner surface of the barrel 30, thus keeping the ram 32 centered and aligned with the axis of the barrel. The second purpose is to enhance the uniform temperature distribution of the melted metal.
As shown in FIG. 7A, there are no fins in area 32c of the ram that moves inside valve 17 so as not to strike the valve. The cross sectional view across section A-A' in FIG. 7A is shown in FIG. 7B. As can be seen, the fins 34 do not extend around the entire circumference of the ram 32 to allow the metal to flow through the barrel. The fins 34 can be arranged in a number of different formations around ram 32. For example, as shown in FIG. 7C, two fins can be arranged on opposite sides of the rod at periodic intervals 36. Each interval can be of the same or different length. For example, the fins can be spaced closed to each other on one end of the ram than on another end of the ram, or the fins can be spaced closer together in one or more sections nearer to the middle of the ram than one or both ends of the ram. Alternatively, as shown in FIG. 7D, more than two fins (e.g. three) can be arranged around the ram at spaced intervals 39. Again, the intervals along the ram 36, and intervals around the circumference of the ram 39 can be of the same or different length. Furthermore, the fins 34 can be tilted at one or more angles other than 90 degrees with respect to the axis of the barrel, as shown in FIG. 7E. Otherwise, some fins 34 may be tilted at 90 degrees while other fins at an angle other than 90 degrees. As noted above, there can be more than two tilted fins spaced along the rod at equal or unequal intervals. Still further, the width and/or thickness of the fins along the ram and/or around the ram circumference the may differ, as shown in FIG. 7F. The fins may also be staggered about the length of the ram, as shown in FIG. 7G. In general any combination of one of more of the above alternative arrangements are possible, even if the fins 34 are mounted on the inside of the barrel 30 rather than on the ram 32. The ram 32 with fins 34 may be also be used with the embodiments shown in FIGS. 3-5.
FIGS. 8A-D show side views of another embodiment of the injection chamber 50'. In this embodiment, the piston 45' is composed of two parts: an inner part 46 and an outer part 47. The outer part is substantially a hollow cylinder and the inner part is substantially a cylinder which slidably fits inside the outer part. The two parts have separate drive mechanisms. FIG. 8A shows the situation when the ram 32 is retracted back in the barrel 30 to allow metal to flow into injection chamber 50'. The inner part 46 of the piston is fully extended to block the exit 58 from the injection nozzle 57"' to prevent metal flow into the die 14"". The outer part 47 of the piston is retracted to expand the volume of the injection chamber 50' to a desired volume. Likewise, the ram 32 is retracted in the barrel 30. In this configuration, metal flows into injection chamber 50' from barrel 30' but does not prematurely flow into the die through injection nozzle aperture 58 because it is blocked by inner piston part 46. The heating elements 70 are present but are omitted from the Figure for clarity.
FIG. 8B shows the next step in the operation of the injection chamber 50'. Here, ram 32 is fully advanced inside the barrel 30 to advance the remaining metal from barrel 30 to injection chamber 50'. The inner piston part 46 is still fully advanced to block the injection nozzle aperture 58. The outer piston part 47 is still retracted to allow metal to flow from barrel 30 into injection chamber 50'. This configuration also prevents premature flow of the metal into the die.
FIG. 8C shows the next step in the operation of the injection chamber 50'. The inner piston part 46 has been retracted into the outer piston part 47. The injection nozzle is now open. However, no extra metal flows from barrel 30 into injection chamber 50' because barrel opening is blocked by the advanced ram 32.
FIG. 8D shows the last step in the operation of the injection chamber 50'. Both the inner and outer parts 46,47 of the piston 45' are pushed to the left to force the melted metal in the injection chamber 50' into the die 14"" through the injection nozzle 57"'. As described above, the injection nozzle 57"' may be moved forward to contact the opening in the die prior to moving the piston 45' to the left.
After the step shown in FIG. 8D, the ram 32 and the outer piston part 47 are retracted, while the inner piston part 46 is positioned to block the injection nozzle aperture 58, as shown in FIG. 8A, and the process is repeated as necessary.
Alternatively, the inner piston part 46 may be retracted partially into the outer piston part 47, (shown as dashed lines in FIG. 8C) to allow metal into the die opening, instead of being retracted all the way in as shown in FIG. 8C. Furthermore, the inner piston part 46 may move into the injection nozzle 57"' and further to the left (shown as dashed lines in FIG. 8D) than the outer piston part 47 instead of moving as far left as the outer piston part 47, as shown by the solid line in FIG. 8D. Thus, the nozzle shut-off plate may be replaced by the inner piston part 46, since both perform the same function. Thus, the apparatus of FIGS. 8A-D is an improvement on the apparatus of FIG. 1 because it requires only one motor to move the two part piston instead of two motors required in FIG. 1 (one to operate the piston and the other to operate the shut-off plate).
Furthermore, the apparatus shown in FIGS. 8A-D prevents metal accumulation in the nozzle aperture and allows the inner piston part 46 to force the melted metal in the injection nozzle 57"' into the die opening. Without the two part piston, the melted metal may accumulate in the prior art injection nozzle even after the injection motion by the piston, and solidify as a plug 91, as shown in FIG. 9. The plug 91 forms in the exit aperture 92 of the injection nozzle 90 because the tip 93 of the nozzle comes in contact with the cooler walls of the die (or die support walls) 94. Therefore, the nozzle tip is at a lower temperature than the rest of the injection chamber. Such plugs are undesirable because they block egress from the injection nozzle, thus decreasing the amount of metal injected into the mold or rendering the apparatus inoperative.
However, the inner portion of the piston 46 in FIGS. 8A-D blocks the injection nozzle aperture from the inside of the nozzle prior to piston injection movement, thus preventing any metal from accumulating in the aperture. In addition, the inner piston portion may be designed to push out any residual metal that may accumulate in the aperture by including a tapered tip 49 of the inner piston portion 46 that extends into the aperture, as shown in FIG. 8A.
FIG. 10 shows another embodiment of the present invention. In this embodiment, an extra gas outlet port 110 is added. The extra gas outlet port allows the gas 111 that is trapped between the melted metal 115 and the piston 45 to escape the injection chamber. The use of outlet port 110 in addition to the opening around the piston allows more gas to escape the injection chamber. Alternatively, the outlet port 110 can comprise the only means for the trapped gasses to escape. The outlet port 110 is preferably positioned between the inlet to the injection chamber and the position of the retracted piston. The outlet port can comprise any structure which would allow the gasses trapped in the injection chamber to escape, without letting in the air from outside of the apparatus into the injection chamber and without letting the melted metal escape through it during injection into the mold. For example, the outlet port 110 can contain a semi-permeable material, such as porous ceramic 112. The porous material allows gas, but not melted material to pass through it. The outlet port can be connected to an outlet pipe 113, which contains a one way valve 114 which allows gasses to escape, but which prevents outside air from entering the injection chamber.
FIGS. 11A and 11B show an alternative method of operating the piston. Prior to injecting the melted metal 115 into the mold 14, the piston is partially advanced forward, while the nozzle shut-off plate 15 blocks metal flow into the mold. The forward movement of the piston forces the trapped gasses out of the injection chamber. The gasses exit through the space between the piston and the injection chamber wall and through the outlet port 110, if present. However, the forward movement of the piston does not result in the injection of the melted metal into the mold because the nozzle shut-off plate blocks the nozzle. Once the trapped gasses are squeezed out of the injection chamber, the shut-off plate is lifted and the piston is advanced forward to inject the metal into the mold, as shown in FIG. 11B.
If the two part piston shown in FIGS. 8A-D is used, then a similar gas squeeze out method can be used. With the inner portion of the two part piston blocking the injection nozzle, the outer portion is partially advanced forward to squeeze the trapped gasses out of the injection chamber. Then, as the inner portion of the piston is retracted, the injection nozzle is opened and the piston is advanced forward to inject the metal into the mold.
FIG. 12A shows another embodiment of the barrel according to the present invention. In this embodiment, the ram is composed of two parts, an inner portion 32d and an outer portion 32e. The outer portion 32e is slidably mounted on the first portion 32d and can be advanced and retracted along the axis of the barrel 30. The inner portion 32d is roughly circular in cross section, whole the outer portion 32e has a doughnut shape cross section, with an inner diameter slightly larger than the diameter of the inner portion 32d. The two part ram operates on a principle similar to the two part piston shown in FIGS. 8A-D. After each injection cycle, the inner ram portion 32d is partially retracted, while the outer ram portion 32e is fully retracted. As the melted metal flows from the feeder 23 through the barrel 30 and into the injection chamber 50, the inner portion of the ram 32d is extended down the length of the barrel and rotates about its axis to keep the temperature of the melted metal uniform. The outer portion 32e is then advanced forward to push the melted metal in the barrel into the injection chamber. Prior to the injection of the metal from the injection chamber to the mold, access to the barrel through the outlet port 37 must be closed. This can be accomplished by blocking the outlet port 37 with the end of the inner portion of the ram 32b or by blocking the outlet port 37 with both portions of the ram. The shape of the outlet port 37 can correspond to the tip of the composite two part ram such that when both portions of the ram are fully advanced, they are capable of blocking the outlet port 37, as shown in FIG. 12B. When the outer portion 32e is fully advanced, it substantially blocks the inlet to the barrel 30 from the melt feeder 23, such that substantially no melted metal enter the barrel 30 when the outer ram portion is fully advanced.
It is important to note that all embodiments shown in FIGS. 1-12 may be used together or separately or in any combination or permutation without departing from the scope of the current invention. In other words, any one or more improvements shown in FIGS. 2-8 may be added to the basic apparatus shown in FIG. 1 without departing from the scope of the current invention.
This application claims priority of U.S. provisional application Ser. No. 60/080,078 (filed Mar. 31, 1998), the entire contents of which is incorporated.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS2386966 *Mar 10, 1943Oct 16, 1945Hydraulic Dev Corp IncHigh-frequency electrostatic heating of plasticsUS2505540 *Feb 4, 1946Apr 25, 1950Goldhard Franz KarlInjection molding apparatusUS2529146 *Mar 15, 1948Nov 7, 1950Waldes Kohinoor IncInjection molding apparatusUS2785448 *Jun 14, 1955Mar 19, 1957Hodler FritzApparatus for the automatic expulsion of air from the die-cavity of hot and cold chamber die-casting machinesUS3048892 *Jun 12, 1959Aug 14, 1962Copperweld Steel CoPowder applicatorUS3106002 *Aug 8, 1960Oct 8, 1963Nat Lead CoDie-casting methodUS3189945 *Mar 1, 1962Jun 22, 1965Pennsalt Chemicals CorpInjection molding apparatusUS3201836 *Sep 21, 1964Aug 24, 1965Mount Vernon Die Casting CorpMethod of, and apparatus for, die casting metalsUS3254377 *Apr 22, 1963Jun 7, 1966Morton Glenn RFluid cooled, lubricated and sealed piston means for casting devicesUS3268960 *Sep 8, 1964Aug 30, 1966Morton Glenn RMethod of and means for producing dense articles from molten materialsUS3270383 *Jun 24, 1963Sep 6, 1966Gen Motors CorpMethod of die castingUS3319702 *Nov 1, 1963May 16, 1967Union Carbide CorpDie casting machineUS3344848 *Apr 25, 1966Oct 3, 1967Gen Motors CorpDie casting apparatus with non-turbulent fill and dual shot plunger arrangementUS3447593 *May 25, 1967Jun 3, 1969Mt Vernon Die Casting CorpApparatus for die castingUS3550207 *Oct 15, 1968Dec 29, 1970Pennwalt CorpSprue bushing purge port for injection molding machineUS3693702 *May 26, 1970Sep 26, 1972Reinhardt AlbertPressure casting machine with pressure increase systemUS3810505 *Oct 17, 1972May 14, 1974Cross RDie casting methodUS3814170 *Feb 11, 1972Jun 4, 1974Kahn FApparatus for melting and casting material under pressureUS3874207 *Feb 1, 1967Apr 1, 1975Jerome H LemelsonExtrusion apparatusUS3893792 *Apr 6, 1973Jul 8, 1975Bbf Group IncController for injection molding machineUS3902544 *Jul 10, 1974Sep 2, 1975Massachusetts Inst TechnologyContinuous process for forming an alloy containing non-dendritic primary solidsUS3936298 *May 1, 1974Feb 3, 1976Massachusetts Institute Of TechnologyMetal composition and methods for preparing liquid-solid alloy metal composition and for casting the metal compositionsUS3976118 *Mar 25, 1974Aug 24, 1976Friedhelm KahnMethod for casting material under pressureUS4049040 *Aug 7, 1975Sep 20, 1977N L Industries, Inc.Squeeze casting apparatus and methodUS4088178 *Feb 3, 1977May 9, 1978Ube Industries, Ltd.Vertical die casting machinesUS4168789 *Oct 11, 1977Sep 25, 1979Novatome IndustriesMetering apparatus for molten metalUS4212625 *Mar 14, 1978Jul 15, 1980Shutt George VHigh speed injector for molding machinesUS4287935 *Jun 25, 1980Sep 8, 1981Ube Industries, Ltd.Vertical die casting machineUS4330026 *Jun 6, 1980May 18, 1982Oskar Frach Werkzeugbau Gmbh & Co. KgMethod and device for controlling injection process in cold-chamber die-casting machinesUS4347889 *Jan 3, 1980Sep 7, 1982Nissan Motor Co., Ltd.Diecasting apparatusUS4434839 *Aug 12, 1982Mar 6, 1984Secretary Of State In Her Brtannic Majesty's Government Of The United KingdomProcess for producing metallic slurriesUS4436140 *Jul 12, 1982Mar 13, 1984Honda Giken Kogyo Kabushiki KaishaMethod of charging molten metal into a vertical die casting machineUS4473103 *Jan 29, 1982Sep 25, 1984International Telephone And Telegraph CorporationContinuous production of metal alloy compositesUS4476912 *Jun 8, 1982Oct 16, 1984Harvill John IHot chamber die casting machineUS4510987 *Feb 7, 1983Apr 16, 1985Association Pour La Recherche Et Le Developpemente Des Methods Et Processus Industrieles (Armines)Method and apparatus for casting metal alloys in the thixotropic stateUS4534403 *Apr 18, 1983Aug 13, 1985Harvill John IHot chamber die casting machineUS4537242 *May 31, 1984Aug 27, 1985Olin CorporationMethod and apparatus for forming a thixoforged copper base alloy cartridge casingUS4559991 *Jun 2, 1983Dec 24, 1985Toshiba Kikai Kabushiki KaishaMethod and system of controlling injection molding machinesUS4586560 *May 22, 1985May 6, 1986Nippondenso Co., Ltd.Die-casting method and apparatusUS4687042 *Jul 23, 1986Aug 18, 1987Alumax, Inc.Method of producing shaped metal partsUS4694881 *Dec 1, 1981Sep 22, 1987The Dow Chemical CompanyMethod for making thixotropic materialsUS4694882 *Dec 1, 1981Sep 22, 1987The Dow Chemical CompanyMethod for making thixotropic materialsUS4730658 *Nov 25, 1986Mar 15, 1988Akio NakanoInjection method in a hot chamber type die casting machine and injection apparatus for carrying the methodUS4771818 *Aug 5, 1981Sep 20, 1988Alumax Inc.Process of shaping a metal alloy productUS4828460 *Aug 6, 1987May 9, 1989Toshiba Kikai Kabushiki KaishaElectromagnetic pump type automatic molten-metal supply apparatusUS4884621 *Jun 10, 1988Dec 5, 1989Honda Giken Kogyo Kabushiki KaishaHydraulic control method for implementsUS4997027 *May 11, 1989Mar 5, 1991Ube Industries, Ltd.Pressing mechanism for casting apparatusUS5040589 *Feb 10, 1989Aug 20, 1991The Dow Chemical CompanyMethod and apparatus for the injection molding of metal alloysUS5143141 *Aug 8, 1990Sep 1, 1992Tva Holding S.P.A.Process and apparatus for the controlled-pressure casting of molten metalsUS5144998 *Aug 20, 1991Sep 8, 1992Rheo-Technology Ltd.Process for the production of semi-solidified metal compositionUS5161598 *Sep 3, 1991Nov 10, 1992Toshiba Kikai Kabushiki KaishaMethod of controlling mold pressure pin for press casting machineUS5181551 *Sep 25, 1991Jan 26, 1993Electrovert Ltd.Double acting cylinder for filling dies with molten metalUS5186236 *Dec 12, 1991Feb 16, 1993Alusuisse-Lonza Services Ltd.Process for producing a liquid-solid metal alloy phase for further processing as material in the thixotropic stateUS5205338 *Dec 11, 1991Apr 27, 1993Nelson Metal Products CorporationClosed shot die castingUS5244033 *Mar 17, 1992Sep 14, 1993Ube Industries, Inc.Diecasting apparatusUS5375645 *Jan 19, 1993Dec 27, 1994Micromatic Operations, Inc.Apparatus and process for producing shaped articles from semisolid metal preformsUS5394931 *Jan 12, 1993Mar 7, 1995Honda Giken Kogyo Kabushiki KaishaAluminum-based alloy cast product and process for producing the sameUS5501266 *Jun 14, 1994Mar 26, 1996Cornell Research Foundation, Inc.Method and apparatus for injection molding of semi-solid metalsUS5531261 *Dec 30, 1994Jul 2, 1996Rheo-Technology, Ltd.Process for diecasting graphite cast iron at solid-liquid coexisting stateUS5533562 *Sep 29, 1994Jul 9, 1996Weber S.R.L.Method and system for semiliquid die casting high performance mechanical components from rheocast ingotsUS5571346 *Apr 14, 1995Nov 5, 1996Northwest Aluminum CompanyCasting, thermal transforming and semi-solid forming aluminum alloysUS5575325 *Feb 3, 1994Nov 19, 1996Asahi Tec CorporationSemi-molten metal molding method and apparatusUS5577546 *Sep 6, 1993Nov 26, 1996Comalco Aluminium LimitedParticulate feedstock for metal injection moldingUS5601136 *Jun 6, 1995Feb 11, 1997Nelson Metal Products CorporationInclined die cast shot sleeve systemUS5622216 *Nov 22, 1994Apr 22, 1997Brown; Stuart B.Method and apparatus for metal solid freeform fabrication utilizing partially solidified metal slurryUS5623984 *Jun 23, 1995Apr 29, 1997Toyota Jidosha Kabushiki KaishaMethod of controlling pressurizing pin and casting apparatus with pressurizing pin controllerUS5630463 *Dec 8, 1994May 20, 1997Nelson Metal Products CorporationVariable volume die casting shot sleeveUS5630466 *Jan 13, 1995May 20, 1997Aluminium PechineyProcess for shaping metal materials in a semi-solid stateUS5638889 *Apr 24, 1996Jun 17, 1997Asahi Tec CorportionSemi-molten metal molding apparatusUS5657812 *Nov 13, 1995Aug 19, 1997Bachmann Giesserei Und Formenbau Gmbh & Co. KgMetal-casting apparatus and methodUS5662159 *Mar 26, 1996Sep 2, 1997Toshiba Kikai Kabushiki KaishaMethod and apparatus of controlling injection of die casting machineUS5664618 *Mar 21, 1996Sep 9, 1997Honda Giken Kogyo Kabushiki KaishaInjection molding apparatusUS5665302 *Sep 20, 1995Sep 9, 1997Reynolds Wheels International Ltd.Method and equipment for bringing metal alloy ingots, billets and the like to the semisolid or semiliquid state in readiness for thixotropic formingUS5680894 *Oct 23, 1996Oct 28, 1997Lindberg CorporationApparatus for the injection molding of a metal alloy: sub-ring conceptUS5685357 *Apr 24, 1995Nov 11, 1997The Japan Steel Works, Ltd.Process for producing shaped parts of metalsUS5697422 *May 5, 1994Dec 16, 1997Aluminum Company Of AmericaApparatus and method for cold chamber die-casting of metal parts with reduced porosityUS5697425 *Aug 9, 1994Dec 16, 1997Rheo-Technology, Ltd.Method of producing thin cast sheet through continuous castingUS5701942 *Jul 15, 1996Dec 30, 1997Ube Industries, Ltd.Semi-solid metal processing method and a process for casting alloy billets suitable for that processing methodUS5716467 *Oct 25, 1994Feb 10, 1998Brush Wellman Inc.Beryllium-containing alloys of aluminum and semi-solid processing of such alloysUS5730198 *Jun 6, 1995Mar 24, 1998Reynolds Metals CompanyMethod of forming product having globular microstructureUS5730202 *Mar 18, 1996Mar 24, 1998Nelson Metal Products CorporationConstant volume shot sleeveUS5735333 *May 29, 1996Apr 7, 1998The Japan Steel Works, Ltd.Low-melting-point metal material injection molding method, and machine for practicing the methodEP0476843A1 *Aug 21, 1991Mar 25, 1992Rheo-Technology, LtdProcess for the production of semi-solidified metal compositionJPH058017A * Title not availableJPH0751827A * Title not availableJPH0872110A * Title not availableJPH01166874A * Title not availableJPH01178345A * Title not availableJPH02274360A * Title not availableJPH05285626A * Title not availableJPH05285627A * Title not availableJPH06306507A * Title not availableJPH08252661A * Title not availableJPH09155524A * Title not availableJPH09155527A * Title not availableJPH09295122A * Title not availableWO1997021509A1 *Dec 12, 1996Jun 19, 1997Thixomat, Inc.Apparatus for processing semisolid thixotropic metallic slurriesWO1997045218A1 *May 29, 1997Dec 4, 1997Thixomat, Inc.Apparatus for processing corrosive molten metals* Cited by examinerNon-Patent CitationsReference1"Advertisement for Sodick Tupal Injection Machine", May 1997 and "Sodick Advertising Material" (not date).2"Injection Molding of Magnesium Alloys", Chemical Engineering News, Jun. 6, 1988.3"Plastic Processing Technology Book", Published in Japan.4"Semi-Solid Metalcasting", Foundry Management and Technology, Japan, Nov. 1995.5 *Advertisement for Sodick Tupal Injection Machine , May 1997 and Sodick Advertising Material (not date).6Carnahan et al., "New Manufacturing Process for Metal Matrix Composite Synthesis," Fabrication of Particulates Reinforced Metal Composites, Proceedings of an International Conference, Sep. 1990, pp. 101-105.7 *Carnahan et al., New Manufacturing Process for Metal Matrix Composite Synthesis, Fabrication of Particulates Reinforced Metal Composites, Proceedings of an International Conference , Sep. 1990, pp. 101 105.8Flemings et al., "Rheocasting," Materials Science and Engineering, vol. 25 (1976), pp. 103-117.9 *Flemings et al., Rheocasting, Materials Science and Engineering , vol. 25 (1976), pp. 103 117.10 *Injection Molding of Magnesium Alloys , Chemical Engineering News, Jun. 6, 1988.11Pasternak et al., "Semi-Solid Production Processing of Magnesium Alloys by Thixomolding," Proceedings of the Second International Conference on the Semi-Solid Processing of Alloys and Composites, Jun. 1992, pp. 159-169.12 *Pasternak et al., Semi Solid Production Processing of Magnesium Alloys by Thixomolding, Proceedings of the Second International Conference on the Semi Solid Processing of Alloys and Composites , Jun. 1992, pp. 159 169.13 *Plastic Processing Technology Book , Published in Japan.14R.D. Carnahan, et al., "New Manufacturing Process for Metal Matrix Composite Synthesis", Fabrication of.15 *R.D. Carnahan, et al., New Manufacturing Process for Metal Matrix Composite Synthesis , Fabrication of.16R.D. Carnalman, et al. "Advances in Thixomolding", 52nd Annual World Magnesium Conference, May 17-19.17 *R.D. Carnalman, et al. Advances in Thixomolding , 52nd Annual World Magnesium Conference, May 17 19.18 *Semi Solid Metalcasting , Foundry Management and Technology, Japan, Nov. 1995.19 *Seminar Material, Japan, Jul. 1995.20Staff Report, "Semi-Solid Metalcasting Gains Acceptance, Applications," Foundry Management & Technology, Nov. 1995 pp. 23-26.21 *Staff Report, Semi Solid Metalcasting Gains Acceptance, Applications, Foundry Management & Technology, Nov. 1995 pp. 23 26.22Tissier et al., "Magnesium rheocasting: a study of processing-microstructure interactions," Journal of Materials Science, vol. 25 (1990), pp. 1184-1196.23 *Tissier et al., Magnesium rheocasting: a study of processing microstructure interactions, Journal of Materials Science , vol. 25 (1990), pp. 1184 1196.24Worthy, "Injection Molding of Magnesium Alloys," Chemical & Engineering News, Jun. 1988, pp. 29-30.25 *Worthy, Injection Molding of Magnesium Alloys, Chemical & Engineering News , Jun. 1988, pp. 29 30.* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS6540006Apr 26, 2001Apr 1, 2003Takata CorporationMethod and apparatus for manufacturing metallic parts by fine die castingUS6588486 *Sep 28, 2000Jul 8, 2003Nissei Plastic Industrial Co., Ltd.Metering method of metal material in injection moldingUS6640875 *Sep 28, 2000Nov 4, 2003Nissei Plastic Industrial Co., Ltd.Injection molding method of metal materialUS6655445Nov 4, 2002Dec 2, 2003Takata CorporationInjection molding method and apparatus with reduced piston leakageUS6666258 *Jun 30, 2000Dec 23, 2003Takata CorporationMethod and apparatus for supplying melted material for injection moldingUS6675867 *Dec 19, 2000Jan 13, 2004Nissei Plastic Industrial Co., Ltd.Injection apparatus for melted metalsUS6681834 *Mar 18, 2002Jan 27, 2004Nissei Plastic Industrial Co., Ltd.Injection method for melted metalsUS6719035 *Sep 28, 2000Apr 13, 2004Nissei Plastic Industrial Co., Ltd.Method and apparatus for injection molding metal materialUS6739379Apr 26, 2001May 25, 2004Takata CorporationMethod and apparatus for manufacturing light metal alloyUS6742570May 1, 2002Jun 1, 2004Takata CorporationInjection molding method and apparatus with base mounted feederUS6789603Feb 2, 2004Sep 14, 2004Takata CorporationInjection molding method and apparatus with base mounted feederUS6808679 *Nov 27, 2001Oct 26, 2004Noranda, Inc.Magnesium-based casting alloys having improved elevated temperature performance, oxidation-resistant magnesium alloy melts, magnesium-based alloy castings prepared therefrom and methods for preparing sameUS6866088 *Dec 19, 2000Mar 15, 2005Nissei Plastic Industrial Co., Ltd.Injection molding machine for low-melting point metallic materialUS6923244 *Jul 1, 2002Aug 2, 2005Tetsuichi MotegiPouring apparatus for castingsUS7004225Jan 28, 2004Feb 28, 2006Nissei Plastic Industrial Co., Ltd.Injection molding machine for low-melting point metallic materialUS7066236 *Sep 23, 2004Jun 27, 2006Sodick Plustech Co., Ltd.Injection device for light metal injection molding machineUS7137435Nov 17, 2003Nov 21, 2006Sodick Plustech Co., Ltd.Enhanced cold chamber die casting molding machineUS7165599 *Jan 30, 2004Jan 23, 2007Nissei Plastic Industrial Co., Ltd.Melting and feeding method and apparatus of metallic material in metal molding machineUS7694715Jan 23, 2007Apr 13, 2010Husky Injection Molding Systems Ltd.Metal molding systemUS8030082Jan 13, 2006Oct 4, 2011Honeywell International Inc.Liquid-particle analysis of metal materialsUS8287495Oct 10, 2011Oct 16, 2012Tandem Diabetes Care, Inc.Infusion pump system with disposable cartridge having pressure venting and pressure feedbackUS8298184Oct 30, 2012Tandem Diabetes Care, Inc.Infusion pump system with disposable cartridge having pressure venting and pressure feedbackUS8408421Apr 2, 2013Tandem Diabetes Care, Inc.Flow regulating stopcocks and related methodsUS8448824Feb 26, 2009May 28, 2013Tandem Diabetes Care, Inc.Slideable flow metering devices and related methodsUS8650937Sep 18, 2009Feb 18, 2014Tandem Diabetes Care, Inc.Solute concentration measurement device and related methodsUS8758323Jul 29, 2010Jun 24, 2014Tandem Diabetes Care, Inc.Infusion pump system with disposable cartridge having pressure venting and pressure feedbackUS8926561Jul 29, 2010Jan 6, 2015Tandem Diabetes Care, Inc.Infusion pump system with disposable cartridge having pressure venting and pressure feedbackUS8986253Aug 7, 2009Mar 24, 2015Tandem Diabetes Care, Inc.Two chamber pumps and related methodsUS9051642 *Jan 16, 2008Jun 9, 2015Arcelormittal FranceProcess for coating a substrate, plant for implementing the process and feeder for feeding such a plant with metalUS9211377Jul 29, 2010Dec 15, 2015Tandem Diabetes Care, Inc.Infusion pump system with disposable cartridge having pressure venting and pressure feedbackUS20030000676 *Jul 1, 2002Jan 2, 2003Tetsuichi MotegiPouring apparatus for castingsUS20040182536 *Jan 28, 2004Sep 23, 2004Kiyoto TakizawaInjection molding machine for low-melting point metallic materialUS20040182537 *Jan 30, 2004Sep 23, 2004Nissei Plastic Industrial Co., Ltd.Melting and feeding method and apparatus of metallic material in metal molding machineUS20050056978 *Sep 23, 2004Mar 17, 2005Sodick Plustech Co., Ltd.Injection device for light metal injection molding machineUS20060042772 *Nov 17, 2003Mar 2, 2006Misao FujikawaInjection apparatus in cold chamber die casting molding machine and measuring method used thereinUS20070166828 *Jan 13, 2006Jul 19, 2007Honeywell International Inc.Liquid-particle analysis of metal materialsUS20080176094 *Jan 23, 2007Jul 24, 2008Husky Injection Molding Systems Ltd.Metal Molding SystemUS20090065354 *Sep 12, 2007Mar 12, 2009Kardokus Janine KSputtering targets comprising a novel manufacturing design, methods of production and uses thereofUS20100068412 *Jan 16, 2008Mar 18, 2010Daniel ChaleixProcess for coating a substrate, plant for implementing the process and feeder for feeding such a plant with metalEP1525932A1 *Jul 22, 2003Apr 27, 2005Sodick Plustech Co., Ltd.Injection device of light metal injection molding machineWO2001081076A1 *Apr 25, 2001Nov 1, 2001Takata Physics International CorporationMethod and apparatus for supplying melted material for injection moldingWO2003092932A2 *Apr 25, 2003Nov 13, 2003Takata CorporationInjection molding method and apparatus with base mounted feederWO2003092932A3 *Apr 25, 2003Jul 1, 2004Takata CorpInjection molding method and apparatus with base mounted feederWO2004018130A1Jul 22, 2003Mar 4, 2004Sodick Plustech Co., Ltd.Injection device of light metal injection molding machine* Cited by examinerClassifications U.S. Classification164/113, 164/900International ClassificationB22D17/20, B29C45/54, B22D17/30, B29C45/53, B22D17/00Cooperative ClassificationY10S164/90, B29C45/53, B22D17/007, B22D17/30European ClassificationB29C45/53, B22D17/30, B22D17/00SLegal EventsDateCodeEventDescriptionJul 21, 1999ASAssignmentOwner name: TAKATA CORPORATION, JAPANFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:KONO, KANAME;REEL/FRAME:010108/0083Effective date: 19990714Sep 18, 2001CCCertificate of correctionMay 5, 2003FPAYFee paymentYear of fee payment: 4Apr 20, 2007FPAYFee paymentYear of fee payment: 8May 12, 2011FPAYFee paymentYear of fee payment: 12RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services