Matched Legal Cases: ['art.\n18', 'art.\n20', 'art.\n29', 'art.\n41', 'art 1', 'art 2', 'art 1', 'art 2', 'art 2', 'art 2', 'art 1', 'art 2', 'arts 1', 'art 2', 'art 1', 'arts 1', 'art 2', 'art 2', 'art 1', 'art 2', 'art 1', 'art 1', 'art 1', 'art 1', 'art 1', 'art 2', 'art 1', 'art 2', 'art 1', 'art 2', 'art 1', 'art 1', 'art 1', 'art 1', 'art 1', 'art 1', 'art 1', 'art 2', 'art 1', 'art 1', 'art 2', 'art 2', 'art 2', 'art 2', 'arts 13', 'art 1', 'art 1', 'art 1', 'art 1', 'art 1', 'art 1', 'art 1', 'art 1', 'art 1', 'art 2', 'art 1', 'art 2', 'art 1']

Patent US6921264 - Implant to be implanted in bone tissue or in bone tissue supplemented with ... - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsAn implant (1) to be implanted in bone tissue, e.g. a dental implant or an implant for an orthopedic application, comprises surface regions (4) of a first type which have e.g. osseo-integrative, inflammation-inhibiting, infection-combating and/or growth-promoting properties, and surface regions (8) of...http://www.google.com/patents/US6921264?utm_source=gb-gplus-sharePatent US6921264 - Implant to be implanted in bone tissue or in bone tissue supplemented with bone substitute materialAdvanced Patent SearchPublication numberUS6921264 B2Publication typeGrantApplication numberUS 10/661,692Publication dateJul 26, 2005Filing dateSep 12, 2003Priority dateAug 23, 2002Fee statusPaidAlso published asCA2496119A1, CA2496119C, CN1688263A, CN100506186C, DE50311713D1, EP1530446A1, EP1530446B1, EP2108331A1, EP2108332A1, EP2108333A1, EP2108334A1, EP2108334B1, US7008226, US20040038180, US20040053196, WO2004017857A1Publication number10661692, 661692, US 6921264 B2, US 6921264B2, US-B2-6921264, US6921264 B2, US6921264B2InventorsJorg Mayer, Marcel Aeschlimann, Laurent TorrianiOriginal AssigneeWoodwelding AgExport CitationBiBTeX, EndNote, RefManPatent Citations (99), Non-Patent Citations (4), Referenced by (101), Classifications (48), Legal Events (3) External Links: USPTO, USPTO Assignment, EspacenetImplant to be implanted in bone tissue or in bone tissue supplemented with bone substitute material
US 6921264 B2Abstract
An implant (1) to be implanted in bone tissue, e.g. a dental implant or an implant for an orthopedic application, comprises surface regions (4) of a first type which have e.g. osseo-integrative, inflammation-inhibiting, infection-combating and/or growth-promoting properties, and surface regions (8) of a second type which consist of a material being liquefiable by mechanical oscillation. The implant is positioned in an opening of e.g. a jawbone and then mechanical oscillations, e.g. ultrasound is applied to it while it is pressed against the bone. The liquefiable material is such liquefied at least partly and is pressed into unevennesses and pores of the surrounding bone tissue where after resolidification it forms a positive-fit connection between the implant and the bone tissue. The surface regions of the two types are arranged and dimensioned such that, during implantation, the liquefied material does not flow or flows only to a clinically irrelevant degree over the surface regions of the first type such enabling the biologically integrative properties of these surface regions to start acting directly after implantation. The implant achieves with the help of the named positive fit a very good (primary) stability, i.e. it can be loaded immediately after implantation. By this, negative effects of non-loading are prevented and relative movements between implant and bone tissue are reduced to physiological measures and therefore have an osseo-integration promoting effect.
1. An implant for implantation in human or animal bone tissue or in bone tissue supplemented with bone substitute material, wherein at least a part of the implant surface is adapted to comes into contact with the bone tissue, wherein said part of the implant surface comprises surface regions (4) of a first type and surface regions (8) of a second type being different from the surface regions (4) of the first type, wherein the surface regions (8) of the second type comprise a material which is liquefiable by mechanical oscillation and with the aid of which on implantation by mechanical oscillation the implant is stabilized at least primarily in the bone tissue, wherein the surface regions (8) of the first type are equipped for a further clinical function being different from the function of primary stabilization and wherein the surface regions (4, 8) of the first type and of the second type are dimensioned and arranged in a manner such that the surface regions of the first type remain at least partly free from liquefied material on implantation by mechanical oscillation.
2. The implant according to claim 1, wherein the clinical function of the surface regions (4) of the first type, which function is different from primary stabilization, comprises osseointegration, permeation of particles or molecules out of the implant into bone tissue surrounding the implant or out of bone tissue surrounding the implant into the implant or electric or chemical stimulation.
3. The implant according to claim 1, wherein the liquefiable material is a material with thermoplastic properties or with thixotropic properties.
4. The implant according to claim 3, wherein the liquefiable material is a polymer based on lactic acid and/or glycolic acid, a polyhydroxy alkanoate, a polycaprolactone, a polysacharide, a polypeptide, a polydioxanone, a polyanhydride, a polyolefin, a polyacrylate, a polymetacrylate, a polycarbonate, a polyamide, a polyester, a polyurethane, a polysulphone, a polyarylketone, a polyimide, a polyphenyl sulphide, a liquid crystal polymer, a polyacetal, a halogenated polmer, in particular a halogenated polyolefin, a polyphenylene sulphide, a polysulphone, or a polyether or a copolymer or blended polymer of the said polymers or a composite material containing one of said polymers, or a polymeric, ceramic or hydraulic cement.
5. The implant according to claim 1, wherein the surface regions (4) of the first type comprise structures suitable for being ingrown or grown through by vital bone tissue.
6. The implant according to claim 5, wherein the surface regions (4) of the first type further have inflammation-inhibiting, infection-combating and/or growth-promoting properties.
7. The implant according to claim 1, wherein the surface regions (4, 8) of the first and of the second type are arranged beside each other and in parallel to an implantation direction (A).
8. The implant according to claim 1, comprising a central implant part (1) constituting the surface regions (4) of the first type and a peripheral implant part (2) being arranged on the outside of the central implant part, consisting at least partly of the liquefiable material and constituting the surface regions (8) of the second type.
9. The implant according to claim 8, wherein the surface regions (8) of the second type protrude at least locally over the surface regions (4) of the first type.
10. The implant according claim 1, comprising a central implant part (1) constituting the surface regions (4) of the first type and comprising an inner space (2′) in which the liquefiable material is arranged or arrangeable, wherein the inner space (2′) is connected to the outside of the central implant part (1) by openings (20) which are dimensioned for pressing the liquefiable material when liquid through and which are arranged in an area in which the surface regions (8) of the second type are to be produced.
11. The implant according to claim 7, wherein the implant has a load bearing function and the central implant part (1) constitutes the load bearing element of the implant.
12. The implant according to claim 11, wherein the central implant part (1) consists at least partly of a metal, a metal alloy, a ceramic material, a polymer or a composite material.
13. The implant according to claim 11, wherein the central implant part (1) comprises selfcutting or grooving elements.
14. The implant according to claim 11, wherein the central implant part (1) comprises a load bearing part (1.1) and a body part (1.2) having a variable shape.
15. The implant according to claim 11, wherein the central implant part (1) comprises a load bearing support (1.3) and a body (1.4).
16. The implant according to claim 15, wherein body (1.4) comprises a bone substitute material, bone chips or a gel.
17. The implant according to claim 8, wherein the peripheral implant part (2) is equipped for being a load bearing implant part.
18. The implant according to claim 17, wherein the central implant part (1) is a container having permeable walls or consists of a bone substitute material, of bone chips or of a gel.
19. The implant according to claim 1, being a dental implant and comprising at least one fixing location (3) or at least one crown part.
20. The implant according to claim 1, being equipped for an orthopedic application.
21. The implant according to claim 19, being pin-shaped, plate-shaped, disk-shaped or blade-shaped or having a shape being adapted or adaptable to the shape of a predetermined cavity in a bone.
22. The implant according to claim 20, being equipped for connecting two bone parts or for fixing a support plate or for serving as a shaft of a prosthesis for a hip joint, finger joint, knee joint, or shoulder joint.
23. The implant according to claim 1, having the shape of a spinal disk and comprising on its lower and upper side at least one ridge (40), wherein the surface regions (8) of the second type are arranged in the area of the ridges (40).
24. The implant according to claim 20, being pin-shaped, plate-shaped, disk-shaped or blade-shaped or having a shape being adapted or adaptable to the shape of a predetermined cavity in a bone.
25. A method for implanting an implant in bone tissue or in bone tissue supplemented with bone substitute material, the method comprising the steps of:
providing an implant having an implant surface of which at least a contact part is adapted to come into contact with the bone tissue, wherein said contact part of the implant surface comprises surface regions of a first type and surface regions of a second type that are different from the surface regions of the first type, wherein the surface regions of the second type comprise a material that is liquefiable by mechanical oscillation, and wherein the surface regions of the first type are equipped for a further clinical function that is different from the function of primary stabilization; positioning the implant on or in the bone tissue; applying mechanical oscillation to the implant and at the same time pressing the implant against the bone tissue, thereby liquefying at least part of the liquefiable material and pressing the liquefied material into unevenesses and pores of the bone tissue; re-solidifying the liquefied material to form a connection with the bone tissue for primarily stabilizing the implant in the bone tissue; wherein the surface regions of the first and second type are dimensioned and arranged in a manner such that the surface regions of the first type remain at least partly free from liquefied material when mechanical oscillation is applied to the implant and the implant is pressed against the bone tissue; and wherein the surface regions of the second type are equipped and arranged for the further clinical function taking effect on the bone tissue immediately after the step of re-solidifying. 26. The method according to claim 25, wherein the implant is loaded immediately after the step of re-solidifying.
27. The method according to claim 25, wherein before the step of positioning, an opening suitable for positioning the implant is produced in the bone tissue.
28. The method according to claim 27, wherein the bone comprises a cortical part and a cancellous part underneath the cortical part, wherein the opening is produced in the cortical part and wherein the step of applying and pressing comprises advancing the implant into the cancellous part.
29. The method according to claim 25, wherein the implant is positioned on the bone tissue and the step of pressing comprises pressing the implant in a self cutting manner into the bone tissue.
30. The method according to claim 25, wherein before the step of positioning, unevenesses of a suitable geometry are produced in the bone tissue, into which unevenesses the liquefied material is to be pressed.
31. The method according to claim 25, wherein the step of applying and pressing comprises positioning a sonotrode of an ultrasound device on a proximal face of the implant.
32. The method according to claim 25, wherein the implant has the form of a cavity in the bone tissue and is implanted in this cavity.
33. The method according to claim 32, wherein the cavity is created by extracting a natural tooth root from a jaw bone.
34. The method according to claim 25, wherein the step of providing comprises combining two implant parts of two different materials to form the implant.
35. The method according to claim 25, wherein after the step of re-solidifying a further implant part is fixed on a proximal end of the implant.
36. The method according to claim 25, wherein the implant is designed for connecting two vertebrae and the step of applying and pressing comprises pushing the implant between the two vertebrae.
37. A method for implanting an implant in bone tissue or in bone tissue supplemented with bone substitute material, the method comprising the steps of:
providing an implant having an implant surface of which at least a contact part is adapted to come into contact with the bone tissue, wherein said contact part of the implant surface comprises surface regions of a first type and surface regions of a second type that are different from the surface regions of the first type, wherein the surface regions of the second type comprise openings to an inside cavity of the implant, the inside cavity containing a material which is liquefiable by mechanical oscillation, and wherein the surface regions of the first type are equipped for a further clinical function that is different from the function of primary stabilization; positioning the implant on or in the bone tissue; applying mechanical oscillation to the implant and at the same time applying a force to the liquefiable material in the cavity, thereby liquefying at least part of the liquefiable material and pressing the liquefied material through the openings in the surface regions of the second type and into unevenesses and pores of the bone tissue; re-solidifying the liquefied material to form a connection with the bone tissue for primarily stabilizing the implant in the bone tissue, wherein the surface regions of the first and second type are dimensioned and arranged in a manner such that the surface regions of the first type remain at least partly free from liquefied material when the mechanical oscillation is applied to the implant and the liquefied material is pressed through the openings; and wherein the surface regions of the second type are equipped and arranged for the further clinical function taking effect on the bone tissue immediately after the step of re-solidifying. 38. The method according to claim 37 wherein the implant is loaded immediately after the step of re-solidifying.
39. The method according to claim 37, wherein before the step of positioning, an opening suitable for positioning the implant is produced in the bone tissue.
40. The method according to claim 39, wherein the bone comprises a cortical part and a cancellous part underneath the cortical part, wherein the opening is produced in the cortical part and wherein the step of applying and pressing comprises advancing the implant into the cancellous part.
41. The method according to claim 37, wherein the implant is positioned on the bone tissue and the step of pressing comprises pressing the implant in a self cutting manner into the bone tissue.
42. The method according to claim 37, wherein before the step of positioning, unevenesses of a suitable geometry are produced in the bone tissue, into which unevenesses the liquefied material is to be pressed.
43. The method according to claim 37, wherein the step of applying and pressing comprises positioning a sonotrode of an ultrasound device on a proximal face of the implant.
44. The method according to claim 37, wherein the implant has the form of a cavity in the bone tissue and is implanted in this cavity.
45. The method according to claim 44, wherein the cavity is created by extracting a natural tooth root from a jawbone.
46. The method according to claim 37, wherein the step of providing comprises combining two implant parts of two different materials to form the implant.
47. The method according to claim 37, wherein after the step of re-solidifying a further implant part is fixed on a proximal end of the implant.
48. The method according to claim 37, wherein the implant is designed for connecting two vertebrae and the step of applying and pressing comprises pushing the implant between the two vertebrae.
The Invention lies in the field of medical technology and relates to an implant that is implanted in human or animal bone tissue or in bone tissue supplemented with bone substitute material.
The implant according to the invention is, for example, a dental implant that, assuming the function of a natural tooth root, is implanted into a jawbone. In order to permit fastening of an artificial tooth crown, a bridge, or a dental prosthesis, the dental implant comprises, at its proximal end, a fixation location that, after implantation, is located in the region of the bone surface. The dental implant may represent a complete tooth replacement, that is to say may also have a crown region in addition to a root region to be implanted. The implant may also have a different function and may be suitable for implantation in another human or animal bone. Generally speaking, the implant serves for connecting a bone part with another tissue part, in particular with another bone part, or with an artificial part, which artificial part may support or replace a bone part (e.g., artificial joint) or a tooth or it may be a therapeutic auxiliary device (e.g., drug release device, drainage device, or stimulating device for electric or chemical stimulation). The implant may further be such therapeutic auxiliary device itself or it may serve for replacing missing bone tissue or possibly bone tissue to be regenerated (e.g. after removal of a tumor) or it may be an augmentation element for augmenting natural bone in a desired way.
Fixation of tooth replacement structures (individual teeth, groups of teeth, part-prostheses, or complete prostheses) based on the above mentioned dental implants with fixation locations is, according to the state of the art, realized in the following steps: after removal of the natural tooth root one waits until naturally regenerated bone tissue fills the opening in the jawbone. In the region of the regenerated bone tissue an opening adapted to the implant is created. The implant is positioned in the opening, wherein the opening is deep enough for housing the complete implant, which therefore does not protrude beyond the opening. An inner thread defining the fixation location at the proximal face of the implant is closed with a cover screw. The gum is closed over the cover screw and one waits until the bone tissue has ingrown with the implant and by way of this has a stability (secondary stability) sufficient for the loading to be expected. Then; in a further step, the gum is opened over the implant and the cover screw is replaced by a spacer, wherein the spacer projects beyond the gum. Only when the gum around the spacer is healed is the tooth replacement structure fastened on the implant. The briefly described procedure entails a treatment duration of twelve to eighteen months for the patient, of which two to three months fall in the time between the implantation and a point in time at which the bone tissue has grown around the implant or the implant is ingrown in the bone tissue such that the implant has sufficient stability for loading.
The first waiting period (regeneration of bone tissue in an opening in the jawbone) may be avoided or shortened if implants are used which in their shape are adapted as exactly as possible to the original opening, as for example described in the publication U.S. Pat. No. 6,132,214 (Suhonen et al.).
The dental implants according to the state of the art usually consist of pure titanium or of a titanium alloy. These materials exhibit a very good biological compatibility and there are various known surface designs that further improve osseointegration. Very often the implants also comprise macroscopic structures that permit the bone tissue to grow into or through the implant. However, the stability of these known dental implants is only adequate for full loading after complete osseointegration, i.e. only when they are intimately grown around by bone tissue or ingrown or intergrown with bone tissue (secondary stability). In osteoporotic or soft bone, as well as in poorly regenerating bone tissue, for example of older patients it may happen that no sufficient implant stability can be achieved.
The primary stability of the above-described dental implants, i.e. their stability directly after implantation, is greatly limited. For this reason the above mentioned waiting time is added between implantation and further build up. The primary stability of the mentioned implants varies according to implant form, but in most cases it is not sufficient for full loading. Pin-like implants with a thread are restrictedly loadable by tension and compression and possibly transverse forces, in particular when implanted such that at least one thread convolution lies in the region of the cortical part of the bone. They can hardly be loaded by torsion. Implants that do not have a round cross section, i.e. which are adapted to a natural tooth root, are more stable when loaded by torsion, but less stable when loaded by tension. The same applies to plate-like dental implants that may also comprise a plurality of fixation locations.
The un-sufficient loadability of known dental implants would, on loading immediately after implantation lead to movements between implant and bone tissue great enough for impeding or even preventing osseo-integration. However, immediate loading of implants is not only desirable in order to shorten the treatment duration, but also to avoid atrophy of the jawbone due to non-loading, i.e. to promote osseo-integration by way of micro-movements (not exceeding a physiological measure) between implant and bone tissue, which can only be achieved by loading a stable implant.
The primary stability, in particular the ability to be loaded in tension and compression is increased for pin-like implants according to the state of the art by way of a suitably formed threads (U.S. Pat. No. 3,499,222), by spread-out elements (e.g. U.S. Pat. No. 5,766,009, EP-1184006) or by collar-like elements. Anchor-like implants in particular used for fastening wires or sutures are equipped with barb-like surface structures (U.S. Pat. No. 4,360,343) for increasing the primary and secondary stability regarding tension loading. However, these improvements neither permit loading of the implants directly after implantation.
It is therefore the object of the invention to provide an implant suitable for implantation in bone tissue or in bone tissue being supplemented by bone substitute material, which implant has a very good primary stability, such that it is, for instance, able to be loaded immediately after implantation, which implant however is equipped for further clinical functions, e.g. for osseo-integration, for passage of particles or molecules into or out of the implant (delivery or drainage), for electric or chemical stimulation, etc., and this also immediately after implantation. The further clinical functions of the implant are not to suffer clinically relevant restriction by the wanted primary stability. If the implant has a load bearing function, i.e. if it is e.g. a dental implant, it is to be able to be loaded as unlimited as possible immediately after implantation or at least significantly earlier after implantation than known such implants. However, osseo-integration (further clinical function) remains substantially unhindered, i.e. begins immediately after implantation such that the above mentioned positive effects on osseo-integration effected by early loading can be fully exploited. Furthermore, neither the implant according to the invention nor its implantation is to be significantly more complicated than is the case for implants according to the state of the art.
The surfaces of the implant according to the invention, which are to come into contact with bone tissue or which are, for instance, to be grown around by bone tissue or are to be intergrown by bone tissue comprise regions of a first type and regions of a second type different from the surface regions of the first type.
The surface regions of the first type are equipped in a per se known manner for one or more than one predetermined clinical function. Examples of such clinical functions include the promotion or at least enablement of osseointegration for a good secondary stability, delivery of therapeutically effective compounds into tissue surrounding the implant, removal of unwanted compounds from tissue surrounding the implant (drainage), and electric or chemical stimulation of tissue surrounding the implant.
For an implant with a load bearing function, the surface regions of the first type comprise, for example, structures suitable for a stable ingrowth or through growth with vital bone tissue and they are, at least regarding osseo-integration, biologically active. Further or additional compounds having desirable effects, such as osseointegrative, inflammation-suppressing, infection-combating, and growth-promoting effects, may be delivered through the surface regions of the first type or these surfaces may be equipped for passage of therapeutically effective stimulating impulses.
The surface regions of the first type are, for example, biologically compatible surfaces (e.g. made of titanium) and they can be formed to have structures that are suitable for bone. tissue ingrowth. Such surfaces may further be coated with a material comprising calcium phosphate, they may be modified by phosphonates or peptide sequences, for example, and/or they may comprise gels or polymers containing growth factors.
The surface regions of the second type are designed for producing the primary stability. For this purpose these regions comprise a material that can be liquefied by mechanical oscillation, i.e. a material having thermoplastic properties (thermoplast or composite material comprising a thermoplastic component) or a thixotropic cement, wherein the liquefiable material is liquefied and pressed into unevennesses, pores or suitably produced geometries of the bone tissue surrounding the implant by application of mechanical oscillation (e.g. ultrasonic oscillation) during implantation.
The material constituting the surface regions of the second type forms part of the outer surface of the implant already before implantation or it is located on the inside of the implant and during implantation it is pressed in a liquefied state through corresponding openings to the outer surface of the implant, where it creates, in situ, the surface regions of the second type.
For the liquefied material of the surface regions of the second type to be able to be pressed into the bone tissue during implantation, the surface regions of the second type are arranged such that they come into contact with the bone tissue on positioning the implant in the bone. This means that the surface regions of the second type project, for example, at least locally beyond the surface regions of the first type or they are located at implant edges, projections, etc. For implants containing the material forming the surface regions of the second type inside, openings for pressing out the liquefiable material are arranged accordingly.
The surface regions of the two types are arranged and the liquefiable material and/or liquefaction are dimensioned such that the surface regions of the second type remain as free as possible of the liquefied material. This guarantees that the further clinical functions of the first type regions are not hindered or are hindered only to a clinically acceptable degree, even immediately after implantation. Therewith it is achieved that osseo-integration of surface regions of the first type is not only not hindered but is also not delayed and, therefore, starts immediately after implantation.
For implants which during implantation are moved relative to the bone tissue in an implantation direction, separation of the two types of surface regions is achieved by arranging the two types of surface regions next to one another and parallel to the implantation direction.
In the same way as known implants, the implant according to the invention is implanted in an opening specifically created for the implant possibly in beforehand regenerated bone tissue (e.g. of the jawbone) wherein this opening may accommodate the whole implant (root region) or wherein the implant in a self-cutting manner may be forced deeper than the opening into the bone tissue. The opening may, for example, only concern the cortical bone layer or, with a suitable design of the implant, it may be completely omitted. The implant according to the invention may also in the sense of a replica have a shape adapted to an irregular form of a bone cavity, e.g. the shape of a removed, natural tooth root and may be implanted directly into this cavity.
The implant according to the invention is, for example, a dental implant having the shape of a pin or of a natural tooth root and having at its proximal end a fixation location (e.g. pocket hole with an inner thread or location at which the dental surgeon may create such a pocket hole) or an artificial crown region. At its distal end it may be formed chisel-shaped and/or be provided with lateral self-cutting or grooving structures. It may furthermore be plate-shaped, disk-shaped, or blade-shaped and comprise one or more fixation locations, or it may have the shape of an anchor on which for example a wire or a suture can be fastened.
The implant according to the invention is of one piece and comprises the above-defined, different surface regions that, for example, consist of different materials, or it contains the liquefiable material inside and comprises openings through which the material when liquefied is pressed to the outer side of the implant. The implant may also be two-piece or multi-piece, wherein the surgeon combines two or more parts of various materials to form the implant.
For implantation, the implant according to the invention is positioned in the opening in the bone (or bone tissue supplemented with bone substitute material), e.g. in a jawbone, and then mechanical oscillation is applied to it, for example ultrasound, and simultaneously it is pressed against the bone. This causes at least part of the liquefiable material to be liquefied and pressed into pores, surface unevennesses and/or created geometries of the surrounding bone tissue, where after solidification it forms a positive-fit connection between the implant and the surrounding bone tissue or possibly bone substitute material. Depending on the implant design, the implant may also be advanced in the bone tissue (implantation direction) simultaneously to liquefaction.
For applying mechanical oscillation to the positioned implant, the sonotrode of an ultrasound apparatus is placed onto the proximal end of the implant. Experiments show that good results are achieved with a power of 0.2 to 20 W per square millimeters active surface. The frequency of the oscillations is between 2 and 200 kHz.
Implants according to the invention and having a load bearing function (e.g. dental implants) comprise a central implant part carrying the surface regions of the first type and being made of metal (e.g. steel, titanium, cobalt/chromium alloy), of a ceramic or glass-like material (e.g. aluminum oxide, zirconium oxide, ceramic or glass of calcium phosphate), of a thermoset or high-temperature thermoplastic polymers (Polyether arylketones, Polyfluoro- or polychloroethylenes, polyether imides, polyether sulphones, polyvinylchloride, polyurthanes, polysulphones, polyesters) or of a composite material (e.g. high-temperature thermoplast reinforced with carbon fibers). Such implants also comprise a peripheral implant part of the liquefiable material, for example of a material with thermoplastic properties. The liquefiable material may also be placed on the inside of a hollow, central implant part, wherein the walling of the central implant part has through openings through which the liquefied material is pressed under the influence of the mechanical oscillation, in order to form surface regions of the second type on the outside of the walling. The implant parts may be connected to one another on the part of the manufacturer or only be brought into connection with one another by the surgeon directly before or during implantation.
Implants according to the invention which have no relevant load bearing function (e.g. implants having a delivery function, a drainage function, or a stimulating function) may also comprise a central implant part and a peripheral implant part, the peripheral implant part consisting at least partly of the liquefiable material, wherein the mechanical stability (load bearing function), which is necessary for implantation may be taken over by the peripheral implant part, the central implant part having but very little mechanical-stability. Such a central implant part is e.g. a permeable container e.g. of porous calcium phosphate or of an other bone substitute material having little mechanical stability or of a thin membrane, wherein delivery or drainage or simulation takes place through the container wall. The central implant part may also be a body of porous calcium phosphate or of another bone substitute material and have the function of initiating or assisting formation of missing or additionally desired bone tissue. It is possible to provide the liquefiable material on the inside of the central implant part and press it when liquefied through corresponding openings to the outer surface of the central implant part, even if the latter implant part has little mechanical stability.
The implant according to the invention may also consist of only one material that is able at the same time to fulfill the demands with regard to the mechanical strength of the implant and possibly of a fixation location, the demands set by the further clinical functions of the surface regions of the first type (e.g. biological integration or secondary stabilization respectively) and the demand of the liquifiability by mechanical oscillation. As the case may be, in various regions of the implant the one material may be filled to varying degrees (e.g. with fibers, whiskers, or particles) or it may be filled with different materials in different regions. In this case too, a suitable design of the surface regions to be integrated in the bone tissue must ensure that, upon implantation, the surface regions of the second type or the liquefied material respectively comes into contact in particular with the bone tissue and that the liquefied material is not or only to a clinically irrelevant degree carried onto the surface regions of the first type.
For implants with surface regions equipped for osseo-integration, the liquefiable material is advantageously at least partly biologically degradable (resorbable) so that the stability function (primary stability) of the positive fit between the implant and the bone tissue is gradually taken over by the stability function (secondary stability) of the osseo-integration, which advantageously increases to the same degree as the liquefiable material is resorbed, i.e. the primary stability decreases. In particular in the case of osteoporotic bone tissue or poorly regenerating bone tissue it may be advantageous to permanently retain the primary stabilization as a supplement to the secondary stabilization, i.e. to use a non-resorbable, liquefiable material, which may also be equipped for good biological integration (secondary osseointegration).
For implants with other than load bearing functions, the liquefiable material is advantageously at least partly resorbable, if the implant is to be removed from the bone tissue or to be completely replaced by bone tissue. If the primary stability is to be retained, the liquefiable material is not resorbable or only partly resorbable.
Resorbable polymers such as those based on lactic acid and/or glycolic acid (PLA, PLLA, PGA, PLGA etc.) or polyhydroxyalkanoates (PHA), polycaprolactones (PCL), polysaccharides, polydioxanones (PD), polyanhydrides, polypeptides or corresponding copolymers or blended polymers or composite materials containing the mentioned polymers as components are suitable as resorbable liquefiable materials. Thermoplasts such as, for example, polyolefins, polyacrylates, polymetacrylates, polycarbonates, polyamides, polyesters, polyurethanes, polysulphones, polyaryl ketones, polyimides, polyphenyl sulphides or liquid crystal polymers (LCPS), polyacetals, halogenated polymers, in particular halogenated polyoelefins, polyphenylene sulphides, polysulphones, polyethers or corresponding copolymers or blended polymers or composite materials containing the mentioned polymers as components are suitable as non-resorbable polymers. Applicable thixotropic systems are resorbable, partly resorbable, or non-resorbable polymeric, ceramic or hydraulic cements (e.g. Norian� of Synthes or Sulfix� of Centerpulse).
The liquefiable material may contain foreign phases or compounds serving further functions. In particular, the liquefiable material may be strengthened by admixing fibers or whiskers (e.g. of calcium phosphate ceramics or glasses) and such represent a composite material. The liquefiable material may further contain components that expand or dissolve (create pores) in situ (e.g. polyesters, polysaccharides, hydrogels, sodium phosphates) or compounds to be released in situ and having a therapeutic effect for promotion of healing and regeneration (e.g. growth factors, antibiotics, inflammation inhibitors or buffers such as sodium phosphate against adverse effects of acidic decomposition). If the liquefiable material is resorbable, release of such compounds is delayed.
The implant part not comprising the liquefiable material is not resorbable, if the implant is to remain in the patient's body or if it is to be removed surgically. However, this implant part may also be made at least partly of a resorbable material, which after implantation is gradually replaced by vital tissue.
The design of the implant and the selection of the liquefiable material are to be matched to one another such that the strength of the positive fit is sufficient for the expected loading, and such that liquefaction entails a reasonable, that is to say, a low as possible heat release. If liquefiable materials with a relatively high softening temperature are used, it is advantageous to ensure that the implant as a whole (including liquefiable material) conducts the mechanical oscillations as a resonator so that the liquefiable material is liquefied in the surface regions of the second type only very locally, e.g. only in regions of suitably provided energy directors. In this manner the released quantity of heat can be kept to within an acceptable scope. In particular, when using a material with a relatively low softening temperature or a material being liquefiable without release of heat (e.g. thixotropic cements), liquefaction may also be effected in the inside of the liquefiable material (by large damping of the exciting oscillation) or at contact locations between the central and peripheral implant part.
The heat burden on the tissue during implantation may be reduced even further by designing the central implant part to comprise materials with a large heatconducting capability and/or a large thermal capacity (e.g. silicon carbide) and, as the case may be, to comprise cooling channels through which a cooling medium flows.
Exemplary embodiments of the implant according to the invention are described in detail by way of the following Figures, wherein:
FIGS. 1, 2A, 2B, 2C show three first exemplary embodiments of a substantially pin-shaped implant according to the invention (e.g. dental implant), the implants comprising a central and a peripheral implant part, (FIG. 1: side view, FIGS. 2A to 2C: cross sections);
FIG. 3 shows a second exemplary embodiment of the implant according to the invention (e.g. dental implant), the implant comprising a central and a peripheral implant part, wherein the shape of the implant is adapted to an existing cavity in a bone (e.g. cavity caused by removal of a natural tooth root from a jawbone);
FIGS. 4 and 5 show two further embodiments of the implant according to the invention (e.g. dental implant), the implant comprising a central and a peripheral implant part, wherein the central implant part is adapted to an existing cavity in a bone (e.g. is an imitation of a natural tooth root) and is designed to be self-cutting or grooving (cross section);
FIG. 6 shows a further essentially pin-shaped embodiment of an implant according to the invention (e.g. dental implant), the implant comprising a central and a peripheral implant part (side view);
FIGS. 7 and 8 show an exemplary embodiment of an implant according to the invention, the implant being shaped as an anchor (FIG. 7: side view; FIG. 8: cross section);
FIGS. 9 and 10 show an exemplary embodiment of a plate-shaped, diskshaped or blade-shaped implant according to the invention (e.g. dental implant with two fixation locations) as a side view (FIG. 9) and a plan view (FIG. 10);
FIGS. 11 and 12 show an exemplary embodiment of a substantially pinshaped implant according to the invention (e.g. dental implant), the implant comprising a hollow central implant part (FIG. 11: longitudinal section; FIG. 12: plan view);
FIG. 13 shows an exemplary embodiment of the implant according to the invention, the implant comprising a central implant part with no relevant mechanical stability;
FIG. 14 shows an augmentation element as a further example of the implant according to the invention;
FIGS. 15 and 16 (A, B and C of each) show two embodiments of implants serving for connecting two spinal vertebrae, in three dimensional illustrations (FIGS. 15A and 16A), during implantation between the two vertebrae in a side view (FIGS. 15B and 16B), and when implanted as a front view (FIGS. 15C and 16C).
FIGS. 1 and 2A to 2C show an exemplary, pin-shaped embodiment of the implant according to the invention, which implant has a load bearing function and therefore is, for example, a dental implant or an orthopedic implant serving for stabilizing a bone fracture or for fixing a support plate or as a shaft of an artificial joint part (e.g. hip, knee, shoulder or finger joint). The implant comprises a central implant part 1 and a peripheral implant part 2, wherein the central implant part comprises at its proximal end a fixation location 3 (e.g. pocket hole with inner thread or location at which a surgeon may create such a pocket hole). The distal implant end is chisel-shaped for a self-cutting effect. The implant may also, as illustrated in the cross section according to FIG. 2C, comprise axially extending, self-cutting or grooving elements 9.
The central implant part 1 comprises surface regions 4 of the first type (e.g. with osseo-integrative, inflammation-inhibiting, infection-combating and/or growthpromoting properties) extending parallel to the implantation direction A. Between the surface regions 4 of the first type, the implant comprises surfaces that are suitable for connection to the peripheral implant part 2. The connection between the peripheral implant part 2 and the central implant part may be an adhesive connection 5 (FIG. 2A) or a positive fit connection, e.g. individual grooves 5′ (FIGS. 2A and 2C) with a narrowed opening slot or surfaces 5″ with a multitude of openings or grooves (FIG. 2B). The peripheral implant part 2 comprises fingers 6 that, for example, fit into the grooves 5′ or onto the surface regions 5″ and that form at least part of the surface regions 8 of the second type.
As seen in FIGS. 2A to 2C, the invention does not set any conditions on the cross section of the pin-shaped implants so that this may be selected depending on the function. Therefore, cross sections other than those shown in the three FIGS. 2A to 2C are conceivable, for example a central implant part with a round cross section and fingers 6 seated thereon, as shown in FIG. 2A.
The implant illustrated in FIG. 2C may in particular be driven into the bone tissue for example in a largely self-cutting manner. For preventing the liquefied material from being driven onto the surface regions 4 of the first type, the surface regions of the first and of the second type (4 and 8) extend next to one another and parallel to the implantation direction A. In the proximal region where the implantation path is only short, the fingers 6 may open out into a ring 6′ extending around the central implant part 1 and advantageously held in a groove of the central implant part. The ring 6′ not only groups the fingers 6 together into a coherent, peripheral implant part 2, which is advantageous for easy connection of the two parts possibly by the surgeon, but also constitutes a means for intimate primary stabilization between the implant and the cortical bone tissue in particular against tension and torsion. Where appropriate, a thread or a similar structure is created in the cortical bone so that the ring 6′ can be connected to this relatively compact bone layer by a positive fit.
For an implant to be positioned in a deeper opening and not to be displaced or only slightly during oscillation, the surface regions of the first and second type may be arranged differently. The surface regions 8 of the second type may form, instead of fingers 6, a pattern of points or intersecting lines. The arrangement of the surface regions 8 of the second type is thus to be adapted to the manner of implantation. Furthermore, the arrangement of the second type surface regions is to be adapted to the primary stability to be achieved by the liquefied material, i.e. the primary stability that cannot be achieved by the implant shape.
The two implant parts 1 and 2 of the implants shown in FIGS. 1 and 2A to 2C may be connected to one another by the manufacturer. The peripheral implant part 2 may, for example, be manufactured by injection molding directly on the central implant part 1. The two implant parts 1 and 2 may also be manufactured separately and joined together by the surgeon directly before the implantation. In this case it is advantageous to realize the positive-fit or adhesive connection between the two materials during the implantation in that the material of the peripheral implant part 2 is liquefied and, for example, is pressed into openings or grooves according to FIG. 2B of the central implant part. For this it may be necessary to provide the inner side of the peripheral implant part 2 or the corresponding surface of the central implant part 1 with energy directors.
The advantage of the joining-together by the surgeon lies in the fact that the two parts can be sterilized separately, i.e. possibly using different methods being adapted to the various functionalities of the parts. Sterilization of the whole implant is then not necessary. The joining-together just before implantation allows the manufacturer to make available a set of central implant parts differing from one another. For example, the central implant parts may vary with respect to length and diameter and peripheral implant parts differing for example with respect to material or finger thickness, so that the surgeon may himself put together a suitable implant exactly for the case in question (greater variability at lower number of components).
For implanting the pin-shaped implants according to FIGS. 1 and 2A to 2C an implantation device (e.g. sonotrode of an ultrasonic device) is used, which device has a distal end substantially adapted to the proximal face of the implant. If necessary, a coupling piece is introduced between sonotrode and implant. The oscillation energy is advantageously applied to the central implant part.
FIG. 3 shows a dental implant according to the invention which in principle is designed in a similar way as the implant according to FIG. 1 but takes its shape not from the known pin-like or screw-like implants, but rather from a natural cavity in a bone, in the illustrated case from an natural tooth root. Between the surface regions 8 of the second type, which are formed by the peripheral implant part 2, i.e. in the surface regions 4 of the first type, the central implant 1 is provided with structures permitting like a thread an improved anchoring in the regenerated bone tissue (secondary stability).
FIGS. 4 and 5 show in cross section two further embodiments of the implant according to the invention, which are suitable for being implanted in existing bone cavities, e.g. in a cavity created by removal of a natural tooth root. The implant is adapted to a specific cavity and comprises axially extending, self-cutting or grooving elements 9. The central implant part 1 of the two implants consists of a pin part 1.1 (load bearing part) that carries a fixation location 3 or an artificial tooth crown and a body part 1.2. The body part 1.2 is shaped ex situ in the sense of a replica, for example using the removed tooth root, such as described in the publication U.S. Pat. No. 6,132,214 (Suhonen et al.), or in situ, i.e. in the corresponding cavity.
The body part 1.2 according to FIG. 4 forms the surface region 4 of the first type (e.g. with osseo-integrative, inflammation-inhibiting, infection-combating and/or growth promoting properties) and consists of an advantageously resorbable or partly resorbable bone substitute material (e.g. calcium phosphate, polylactide, nonresorbable polymer filled with calcium phosphate, combination system with reinforcing elements). The peripheral implant part 2 is limited to the self-cutting or grooving elements 9 into which, for example, pin-like parts of the liquefiable material are introduced.
The implant according to FIG. 4 may be implanted in two successive steps. Firstly the existing cavity is filled with a piece of a bone substitute material (body part 1.2). Then the pin part is implanted wherein the anchorage through the liquefiable material (peripheral implant part 2) may effect at least partly the bone substitute material. Such cases are illustrated in FIG. 4 by dash dot lines.
The body part 1.2 according to FIG. 5 is formed by a relatively thin and as flexible as possible layer of the liquefiable material, i.e. is surrounded by the peripheral implant part 2 that forms the surface of the second type. Instead of the thin layer, a membrane, which is at least partly coated with the liquefiable material, may also be provided. The axially extending, self-cutting or grooving elements 9 comprise the surfaces 4 of the first type. The body part 1.2 consists of a plastic, curable material, for example a bone cement that may be cured by light, ultrasound, or heat or of a hydraulic cement, which cement preferably has thixotropic properties. On introduction into the cavity, the body part 1.2 takes the shape of the cavity. On applying mechanical oscillations not only is the liquefiable material of the surface regions of the second type pressed into pores and unevennesses of the surrounding bone tissue but also the body part is adapted to the shape of the cavity and is possibly also cured. The liquefiable material is advantageously resorbable so that the primary stability created by the surface regions 8 of the second type is taken over by a secondary stability which is firstly caused by osseo-integration of the body part 1.2 and on resorption of the body part by osseo-integration of the pin part 1.1.
Implants according to FIGS. 4 and 5, which are designed as dental implants, may be implanted in the jawbone essentially directly after removal of a natural tooth root because their shape is adaptable to the cavity created by the removal. Thanks to the primary stability achieved by the surface regions 8 of the second type they may also be loaded immediately, thereby causing micro-movements with physiological measures accelerating osseo-integration in the surface regions of the first type of the body part 1.2 and later of the pin part 1.1. Such dental implants thus shorten the treatment time even more than the implants according to FIGS. 1 to 3. The same is applicable for implants designed for implantation in bones other than jawbones.
FIG. 6 shows a further, pin-like embodiment of the implant according to the invention (e.g. dental implant, implant for fixation of bone fractures, implants for fixing support plates, shaft of artificial joint), the implant comprising a central implant part 1 and a peripheral implant part 2. The central implant part 1 comprises through-openings and/or non-through openings 11 for intergrowth with bone tissue in which openings, for example, pins 12 of the liquefiable material are inserted projecting beyond the surface of the central implant part 1 and held firmly by a friction fit. The pins 12 together form the peripheral implant part 2, the ends of the pins projecting out of the openings 11 over the surfaces 8 of the second type.
FIGS. 7 and 8 show in a side view and in cross section an anchor-shaped embodiment of the implant according to the invention. The fixation location 3 of this embodiment is for example formed as an eyelet. The anchor has a per se known shape and comprises a slot running over its length, in which slot a pin of the liquefiable material (peripheral implant part 2) is arranged with a positive fit. The pin 13 projects on both sides beyond the surface of the anchor. The anchor-shaped implant, as known such anchor implants, may comprise additional barbs 14 which on loading in tension are pressed into the bone tissue such supplementing the positive-fit anchoring by the peripheral implant part 2. However, such barbs or similar retention means are by no means necessary.
The design of the anchor edges as cutter blades simplifies implantation without the use of a suitable opening in the bone tissue or in an opening that only concerns the cortical bone.
FIGS. 9 and 10 show as a further exemplary embodiment of the implant according to the invention a plate-shaped, disk-shaped, or blade-shaped dental implant that, for example, comprises two fixation locations 3 or two artificial tooth crowns and whose peripheral implant part 2 consists of a plurality of pin-like. parts 13 that are positioned in through openings in the plate, disk, or blade and in the region of the fixation locations in grooves of the central implant part.
The plate-, disk- or blade-shaped dental implants of which one example is shown in FIGS. 9 and 10 are positioned in the jaw from the jaw ridge the same as pinshaped dental implants during application of mechanical oscillation (implantation direction A, FIG. 9). However, they may also be implanted into the jawbone from the side (implantation direction A′, FIG. 10), for which implantation a part of the jawbone is removed and repositioned after implantation.
Plate-, disk- or blade-shaped implants are not applicable only in the dental field but also in the orthopedic field, for which they comprise suitably equipped proximal regions.
FIGS. 11 and 12 show a further pin-shaped embodiment of the implant according to the invention (e.g. dental implant or implant for orthopedic application) in a longitudinal section and as a plan view. The central implant part 1 is designed as a sleeve having an inner space 2′, in which the liquefiable material is contained. The sleeve wall comprises through openings or slots 20 that, for example, are arranged in axial rows or extend axially. The implant is positioned in a bone cavity and an oscillating element 21 (sonotrode of an ultrasound apparatus) is placed onto the liquefiable material in the inner space 2′ of the central implant part applying the oscillation to this material and simultaneously pressing it towards the distal implant end. By way of the oscillations the material is liquefied and by way of the pressure it is pressed through the openings or slots 20 into surface unevennesses and pores of the surrounding bone tissue, thereby creating the positive fit for primarily stabilizing the implant.
If the central implant part 1 is provided with a chisel-like, distal end, as shown, the implant according to FIGS. 11 and 12 can also be driven into the bone tissue (at least cancellous bone) without the need of an opening. An annular sonotrode 22 is suitable for this. Sonotrode 21 is applied as soon as the implant has reached the predefined position in the bone.
In an implant according to FIGS. 11 and 12 the peripheral implant part is actually created only when the implant is positioned in the bone tissue, i.e. it is created in situ.
The liquefiable material which is provided in the inner space 2′ of the central implant part may be a thermoplastic material like liquefiable material arranged on the outside of a central implant part. Advantageously, however, the liquefiable material is a polymer or hydraulic cement having thixotropic properties, which cement is curable after implantation by, for example, ultraviolet light, heat, mechanical oscillations or simply with time.
When using a thermoplast as a liquefiable material being provided in an inner space 2′ of the central implant part, energy directors may have to be arranged on the inner surfaces of the central implant part 1 or on the surfaces of the thermoplast.
The liquefiable material of the implant according to FIGS. 10 and 11 may be introduced in the central implant part 1 by the manufacturer or by the surgeon. It is introduced as any number of individual portions or it may be pressed through the sonotrode essentially continuously into the central implant part 1.
FIG. 13 shows a further exemplary embodiment of the implant according to the invention. In contrast to the implants according to the preceding Figs., this implant is not designed for a load bearing function, but rather for releasing a therapeutically effective compound, for drainage, for electric or chemical stimulation of tissue or organs, or for a similar function.
The peripheral implant part consists at least partly of the liquefiable material (surface regions 8 of the second type) and is designed as a cage having sufficient stability for implantation. The central implant part, which does not have any load bearing function, is arranged inside the cage. The implant is positioned in a bone cavity and the oscillation energy is applied to the implant it by a device (sonotrode of an ultrasound device) that is adapted to the proximal face of the implant. The sonotrode to be used for the implant according to FIG. 13 has the form of a hollow cylinder.
The central implant part constituting the surface regions 4 of the first type of the implant according to FIG. 13 has e.g. an osseo-integrative function and consists e.g. of highly porous calcium phosphate, of bone chips (patient's own cancellous bone), or of a gel. This central part may also be a device by which particles or molecules are released to the surrounding tissue (delivery device) or are removed from surrounding tissue (drainage device) or a stimulator, wherein the device is, for example, designed as a correspondingly permeable container comprising walls that constitute the surface regions 4 of the first type.
The cage according to FIG. 13 may be furnished with a central implant part by the manufacturer, or it may be filled with bone chips or the like in the operating theatre. It is also possible to implant the cage in an empty configuration and furnish it in situ with a central implant part, wherein a covering element holding the central implant part in place may be positioned and fixed by ultrasonic welding in situ also.
FIG. 14 shows as a further example of the implant according to the invention an augmentation element 31, which is applicable for producing bone tissue desirable in addition to the natural bone tissue, e.g. for enlarging the ridge 32 of a jawbone. This ridge 32 and the augmentation element 31 are shown in section and in a condition after implantation. The augmentation element 31 comprises a central implant part 1 consisting of a bone growth promoting material, e.g. of a highly porous calcium phosphate. Pins of the liquefiable material are arranged in through holes (inner spaces 2′) of the central implant part 1. For implantation the augmentation element 31 is positioned on the suitably prepared jawbone ridge 32, such that the pins are directed against the ridge 32. Then using a sonotrode 21 adapted to the cross section of the pins, oscillation energy is applied to the pins while the pins are pressed towards the ridge 32. Therewith the liquefiable material is at least partly liquefied and pressed into the bone tissue jawbone ridge and into the material of the augmentation element in order to fasten the augmentation element 31 pointwise to the jawbone ridge 32 and bringing the central implant part 1 (surface regions of the first type) into intensive contact with the bone tissue of the jawbone ridge, such enabling immediately after implantation infiltration of the central implant part with cells originating from the natural bone tissue for promoting bone formation. In this case, the liquefiable material is advantageously resorbable.
FIGS. 15A to 15C and 16A to 16C show two embodiments of the implant according to the invention, applicable for connecting two vertebrae. Again the implants comprise a central implant part 1 constituting a load bearing support 1.3 and a body 1.4 arranged inside the support and equipped for being penetrated by regenerating bone tissue. The body 1.4 consists of highly porous calcium phosphate, bone chips, or a gel. The central implant part is adapted in form to a natural spinal disk and comprises on its upper and lower side ridges 40 extending in implantation direction A and fitting into grooves which have to be formed in the bone tissue of the vertebrae.
The peripheral implant part 2 is in the embodiment according to FIG. 15 arranged on the ridges 40 and in the embodiment according to FIG. 16 the material for the peripheral implant part is provided in inner spaces 2′ of the central implant part 1, which in the region of the ridges 40 comprises openings 20.
The implant according to FIG. 15A is pushed with a sonotrode 30 between two suitably prepared vertebrae as shown in FIG. 15B, wherein the liquefiable material of the peripheral implant part 2 is liquefied and pressed into the bone tissue of the vertebrae so as to anchor the implant, as shown in FIG. 15C. The sonotrode used for implantation is substantially adapted to the proximal face of the implant.
The implant according to FIG. 16A is positioned between two vertebrae as shown in FIG. 16B, e.g. using a sonotrode 30 being adapted substantially to the proximal face of the load bearing support 1.3 of the central implant part 1. When the implant is positioned, oscillation energy is applied to the liquefiable material using a sonotrode adapted to the proximal face of the inner space 2′. Therewith the material is pressed through the openings 20 and into the bone tissue of the vertebrae 41 so as to anchor the implant to the vertebrae, as shown in FIG. 16C.
The implants according to FIGS. 15 and 16 are fixed to the vertebrae immediately after implantation (primary stabilization). Therefore, it is not necessary to stabilize the two vertebrae as known in similar prior art procedures. This makes the implants particularly suitable for minimally invasive operations.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS772029Nov 21, 1903Oct 11, 1904Dwight G ClarkRivet.US2366274Jun 3, 1942Jan 2, 1945Brunswick Balke Collender CoPlastic fastening means and method of applying the sameUS2458152Apr 3, 1945Jan 4, 1949Us Rubber CoPlastic rivet and method of making sameUS2510693Mar 29, 1944Jun 6, 1950Lee B GreenFastening memberUS2942748Oct 18, 1954Jun 28, 1960Anderson John WileyMethod of fastening two part plastic fastener by fusion from frictional heat of rotationUS3184353Nov 13, 1961May 18, 1965Cavitron Ultrasonics IncFastening together of members by high frequency vibrationsUS3481803Oct 19, 1966Dec 2, 1969Uniroyal IncFriction weldingUS3499222Aug 17, 1965Mar 10, 1970Leonard I LinkowIntra-osseous pins and posts and their use and techniques thereofUS3612803Feb 29, 1968Oct 12, 1971Ruth Elizabeth Barry KlaasFastening deviceUS3723215Mar 18, 1970Mar 27, 1973J KesslerMethod for fixing a fastener in two pieces of woodUS3919775Jun 11, 1973Nov 18, 1975Malmin OscarEndodontic sealing system and apparatusUS4032803Apr 12, 1976Jun 28, 1977Durr-Dental Kg.Hand tool for creating and applying ultrasonic vibrationUS4100954Oct 27, 1976Jul 18, 1978Dieter MullerDowel or anchoring meansUS4130751Nov 1, 1976Dec 19, 1978Gordon Stanley HMetal ornamentation and method of weldingUS4248232Sep 12, 1978Feb 3, 1981Eckart EngelbrechtMethod of dissolving the bond between interconnected componentsUS4328108Sep 20, 1979May 4, 1982The Goodyear Tire & Rubber CompanyComposition for the elimination of circumferential stress cracks in spun polyestersUS4360343Nov 4, 1980Nov 23, 1982Mamed HusseinMethod for the oral implantation of a dental prosthesisUS4482795Nov 14, 1983Nov 13, 1984Milton HindenLongitudinal finned resistance weld pinUS4525147May 31, 1983Jun 25, 1985Pitz Richard JRoot canal implant, proximity indicative, and method of implantationUS4566138Apr 24, 1985Jan 28, 1986Zimmer, Inc.Prosthetic device with spacersUS4675972Mar 19, 1986Jun 30, 1987Faster Gmbh & Co KgMethod of fixing an insulating material plate to be plastered to a structural surfaceUS4717302Jun 18, 1984Jan 5, 1988Tiodize Company, Inc.Composite fastenerUS4761871Nov 21, 1986Aug 9, 1988Phillips Petroleum CompanyMethod of joining two thermoplastic articlesUS5004422Nov 9, 1989Apr 2, 1991Propper Robert HOral endosteal implants and a process for preparing and implanting themUS5019083Jan 31, 1989May 28, 1991Advanced Osseous Technologies, Inc.Implanting and removal of orthopedic prosthesesUS5037442Aug 11, 1989Aug 6, 1991Sulzer Brothers LimitedFixing stem for a prosthesisUS5125442Jan 17, 1991Jun 30, 1992Marvin Lumber And Cedar Co.Wood component attachment methodUS5163960Jun 28, 1990Nov 17, 1992Bonutti Peter MSurgical devices assembled using heat bondable materialsUS5167619May 25, 1990Dec 1, 1992Sonokineticss GroupApparatus and method for removal of cement from bone cavitiesUS5171148Jun 30, 1989Dec 15, 1992Ethicon, Inc.Dental inserts for treatment of periodontal diseaseUS5244933Oct 11, 1991Sep 14, 1993Thera Patent Gmbh & Co. Kg Gesellschaft Fur Industrielle SchutzrechteDental compositions which can be prepared and worked by the action of oscillations and method for the preparation thereofUS5271785Apr 13, 1992Dec 21, 1993Davidson Textron Inc.Method of inserting an insert in an opening of a plastic partUS5308205Mar 23, 1992May 3, 1994Mepla-Werke Lautenschlager Gmbh & Co. KgPlastic retaining peg, particularly for furniture fittingsUS5393559Jul 8, 1993Feb 28, 1995Bay Mills LimitedProcess for reinforcing pavingUS5413578Jun 14, 1993May 9, 1995Zahedi; AmirDevice for removing a bone cement tubeUS5426341Oct 21, 1993Jun 20, 1995Durr Dental Gmbh & Co. KgSonotrode for ultrasonic machining deviceUS5447592Aug 17, 1993Sep 5, 1995Battelle Memorial InstituteProcess for glueing two non-metallic substrates by means of an adhesiveUS5547325Feb 18, 1994Aug 20, 1996Utility Composites, Inc.Nail packs made of composites having high compressive strength and flexural modulesUS5562450Apr 13, 1995Oct 8, 1996Reimplant Dentale Systeme GmbhProcess for the production of a dental implantUS5589015Feb 13, 1996Dec 31, 1996Foster-Miller, Inc.Method and system for inserting reinforcing elements in a composite structureUS5593425May 30, 1995Jan 14, 1997Peter M. BonuttiSurgical devices assembled using heat bonable materialsUS5709823Sep 16, 1996Jan 20, 1998Thera Patent Gmbh & Co. Kg Gesellschaft Fur Industrielle SchutzrechteMethod for producing sonotrodesUS5735875Jan 13, 1997Apr 7, 1998Peter M. BonuttiSurgical devices assembled using heat bondable materialsUS5752831Jul 19, 1996May 19, 1998Padros-Fradera; AlejandroDental implant replicaUS5766009Jan 20, 1995Jun 16, 1998Jeffcoat; Robert L.Elastically stabilized endosseous dental implantUS5772359Aug 28, 1996Jun 30, 1998Minnesota Mining And Manufacturing CompanySelf-propelled pavement marking tape applicatorUS5780536Jul 24, 1996Jul 14, 1998Nec CorporationJoining member and method for disintegrating joined structureUS5785476Oct 30, 1996Jul 28, 1998Mcdonnell; Robert L.Fastener with soft tipUS5803736Apr 25, 1994Sep 8, 1998Merritt, Jr.; Kenneth L.Dental cast post for direct intraoral patternsUS5840154Mar 28, 1996Nov 24, 1998Schober Gmbh Werkzeug- Und MaschinenbauMethod and device for joining a sealing foil with a web of materialUS5871514Aug 1, 1997Feb 16, 1999Medtronic, Inc.Attachment apparatus for an implantable medical device employing ultrasonic energyUS5871515Aug 27, 1998Feb 16, 1999Medtronic, Inc.Attachment apparatus and method for an implantable medical device employing ultrasonic energyUS5897578Aug 27, 1998Apr 27, 1999Medtronic, Inc.Attachment apparatus and method for an implantable medical device employing ultrasonic energyUS5919215Aug 27, 1998Jul 6, 1999Medtronic, Inc.Attachment apparatus for an implantable medical device employing ultrasonic energyUS5941901Apr 16, 1998Aug 24, 1999Axya Medical, Inc.Bondable expansion plug for soft tissue fixationUS5964764Mar 24, 1998Oct 12, 1999Hugh S. West, Jr.Apparatus and methods for mounting a ligament graft to a boneUS5993458Jun 25, 1998Nov 30, 1999Ethicon, Inc.Method of ultrasonically embedding bone anchorsUS5993477Jun 25, 1998Nov 30, 1999Ethicon Endo-Surgery, Inc.Ultrasonic bone anchorUS6007539Jan 8, 1997Dec 28, 1999Axel KirschFastening nailUS6039568Jun 2, 1998Mar 21, 2000Hinds; Kenneth F.Tooth shaped dental implantsUS6056751Apr 16, 1998May 2, 2000Axya Medical, Inc.Sutureless soft tissue fixation assemblyUS6059817Mar 12, 1999May 9, 2000Peter M. BonuttiSurgical devices assembled using heat bondable materialsUS6068482Jan 19, 1999May 30, 2000Snow; Michael DesmondMethod for creation and utilization of individualized 3-dimensional teeth modelsUS6080161Mar 19, 1999Jun 27, 2000Eaves, Iii; Felmont F.Fastener and method for bone fixationUS6099313Jun 27, 1997Aug 8, 2000Doerken; WolfgangDental implant, a template for inserting a dental implant, and a process for producing themUS6132214Dec 10, 1996Oct 17, 2000Jouko SuhonenMedical implantUS6139320Feb 27, 1995Oct 31, 2000Hahn; RainerApparatus, method and expedient materials for ultrasonic preparation of human and animal hard or soft tissues and of dental or bone replacement materials as well as object obtained therebyUS6141874May 8, 1998Nov 7, 2000Andersen CorporationWindow frame welding methodUS6193516Jun 18, 1999Feb 27, 2001Sulzer Calcitek Inc.Dental implant having a force distribution shell to reduce stress shieldingUS6224373Oct 11, 1999May 1, 2001Samsung Sds Co., Ltd.Simulation method for visualizing density of jawbone for dental implantationUS6273717Apr 11, 2000Aug 14, 2001Durr Dental Gmbh & Co. KgDental instrument for sonic or ultrasonic treatmentUS6332885Nov 2, 2000Dec 25, 2001Pasquale MartellaSynthesis device for orthopaedia and traumatologyUS6545390Apr 11, 2000Apr 8, 2003Durr Dental Gmbh & Co. KgDevice for generating high-frequency mechanical vibrations for a dental handpieceUS6592609May 3, 2000Jul 15, 2003Bonutti 2003 Trust-AMethod and apparatus for securing tissueUS6635073Feb 21, 2001Oct 21, 2003Peter M. BonuttiMethod of securing body tissueUS20020044753Aug 28, 2001Apr 18, 2002Sumitomo Electric Industries, Ltd.Optical fiber and method of making the sameUS20020077662Feb 15, 2002Jun 20, 2002Bonutti Peter M.Method of using ultrasonic vibration to secure body tissueUS20030118518Oct 29, 2002Jun 26, 2003Rainer HahnSuspension for the treatment of natural hard tissue and method of treatmentDD257797A1 Title not availableDE2418198A1Apr 13, 1974Oct 16, 1975Reich Maschf Gmbh KarlStabfoermiges befestigungsmittelDE3045706A1Dec 4, 1980Jul 8, 1982Reich Maschf Gmbh KarlCover strip glued to edge of workpiece - esp. of wood using resistant adhesive applied liq. and set by ultrasonic energyDE3177577A Title not availableDE3723643A1Jul 17, 1987Jan 26, 1989Gerd RienksImprovement of teethDE3828340A1Aug 20, 1988Jul 13, 1989Daimler Benz AgMethod of bonding an object of plastic to an object of woodDE3919274C1Jun 13, 1989Jul 12, 1990Rademacher, Bernd, 5800 Hagen, DeRoot anchor dental pin - has threaded head and shaft, head having axially-parallel sockets for retainer pinsDE4100636A1Jan 11, 1991Jul 16, 1992Servo Dental Inh Bernd RademacDental implant production method - involves forming blank in artificial tooth socket or extracted-tooth root areaDE4209191A1Mar 22, 1992May 13, 1993Rainer Dr HahnBone and dental surgery tissue removing tool - is of oscillating type for shaping,using both longitudinal and transverse oscillationsDE4328108A1Aug 20, 1993Feb 23, 1995Dieter KlemmAdhesive for floor coverings, and method of loosening a floor coveringDE9012044U1Aug 21, 1990Oct 25, 1990Klaus, Gerold, 7832 Kenzingen, DeTitle not availableDE9012548U1Sep 1, 1990Dec 6, 1990Klaus, Gerold, 7832 Kenzingen, DeTitle not availableDE19735103A1Aug 13, 1997Oct 29, 1998Gieloff Burkhardt R Dr Med DenZahnmedizinisches Implantat sowie Instrument zum Einsatz eines ImplantatsDE19741087A1Sep 18, 1997Apr 8, 1999Schumann KlausSurgical connection between two bones or prosthesisDE19916158A1Apr 11, 1999Oct 19, 2000Duerr Dental Gmbh Co KgDental hand piece for ultrasound treatment; has rest that has support surfaces to complement contour of both sides of asymmetrical hand piece surface, so that it can be put down in different positionsDE19916160A1Apr 11, 1999Oct 26, 2000Duerr Dental Gmbh Co KgDental ultrasound hand piece; has ultrasound generator connected to resonance coupling body of ultrasound work piece by sonotrode, where coupling body is at least partly surrounded by coverDE20113692U1Aug 18, 2001Nov 15, 2001Duerr Dental Gmbh Co KgUltraschallhandst�ckEP0268957A1Nov 13, 1987Jun 1, 1988Phillips Petroleum CompanyMethod for joining thermoplastic articles as well as structures of such articlesEP0415615A2Aug 17, 1990Mar 6, 1991AT&amp;T Corp.Method and apparatus for joining thermoplastic partsEP0451932A1Apr 10, 1991Oct 16, 1991Johnson &amp; Johnson Professional Products GmbHBone screwEP0534078A1Jul 20, 1992Mar 31, 1993IMPLA GmbHDentalimplantatNon-Patent CitationsReference1"Linear Vibration Welding of Non Metallic Components", Welding & Metal Fabrication, May 1989, pp. 152-154.2Reader's Digest Complete Do-it-Yourself Manual (p. 69).3The Simon and Schuster Complete Guide to Home Repair and Maintenance (p. 45).4U.S. Appl. No. 10/415,454, filed Aug. 27, 2003, Aeschlimann et al.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS7335205 *Mar 4, 2002Feb 26, 2008Woodwelding AgImplants, device and method for joining tissue partsUS7429266Jun 10, 2003Sep 30, 2008Marctec, LlcMethod of using ultrasonic vibration to secure body tissueUS7708557Mar 15, 2007May 4, 2010Natural Dental Implants AgCustomized dental prosthesis for periodontal- or osseointegration, and related systems and methodsUS7854750Aug 17, 2006Dec 21, 2010P Tech, Llc.Apparatus and method for securing a sutureUS7964207Jun 21, 2011Doctor's Research Group, Inc.Methods of performing medical procedures that promote bone growth, method of making compositions that promote bone growth, and apparatus for use in such methodsUS7967820May 3, 2006Jun 28, 2011P Tech, Llc.Methods and devices for trauma weldingUS8114137Jun 8, 2007Feb 14, 2012Woodwelding AgImplants for creating connections to tissue parts, in particular to skeletal parts, as well as device and method for implantation thereofUS8142886Jul 24, 2008Mar 27, 2012Howmedica Osteonics Corp.Porous laser sintered articlesUS8147861Aug 15, 2006Apr 3, 2012Howmedica Osteonics Corp.Antimicrobial implantUS8162977Apr 24, 2012P Tech, Llc.Method for joining implantsUS8211458May 24, 2011Jul 3, 2012Doctor's Research Group, Inc.Methods of performing medical procedures that promote bone growth, methods of making compositions that promote bone growth, and apparatus for use in such methodsUS8216286Jun 8, 2007Jul 10, 2012Woodwelding AgImplants for creating connections to tissue parts, in particular to skeletal parts, as well as device and method for implantation thereofUS8221475Jul 17, 2012Woodwelding AgImplants for creating connections to tissue parts, in particular to skeletal parts, as well as device and method for implantation thereofUS8221477Jul 17, 2012Woodwelding AgImplants for creating connections to tissue parts, in particular to skeletal parts, as well as device and method for implantation thereofUS8268099Apr 22, 2009Sep 18, 2012Howmedica Osteonics Corp.Laser-produced porous surfaceUS8268100Jul 26, 2010Sep 18, 2012Howmedica Osteonics Corp.Laser-produced porous surfaceUS8323323Oct 24, 2007Dec 4, 2012Woodwelding AgImplants for creating connections to tissue parts, in particular to skeletal parts, as well as device and method for implantation thereofUS8350186Jan 8, 2013Howmedica Osteonics Corp.Laser-produced implantsUS8454362Oct 16, 2006Jun 4, 2013Natural Dental Implants AgCustomized dental prosthesis for periodontal- or osseointegration, and related systems and methodsUS8496657Aug 29, 2008Jul 30, 2013P Tech, Llc.Methods for utilizing vibratory energy to weld, stake and/or remove implantsUS8497023Aug 5, 2009Jul 30, 2013Biomimedica, Inc.Polyurethane-grafted hydrogelsUS8556981Sep 18, 2009Oct 15, 2013Howmedica Osteonics Corp.Laser-produced porous surfaceUS8602780Apr 19, 2010Dec 10, 2013Natural Dental Implants, AgCustomized dental prosthesis for periodontal or osseointegration and related systems and methodsUS8617185Feb 13, 2008Dec 31, 2013P Tech, Llc.Fixation deviceUS8679190Mar 12, 2012Mar 25, 2014The Board Of Trustees Of The Leland Stanford Junior UniversityHydrogel arthroplasty deviceUS8728387Dec 6, 2005May 20, 2014Howmedica Osteonics Corp.Laser-produced porous surfaceUS8747439Jul 10, 2006Jun 10, 2014P Tech, LlcMethod of using ultrasonic vibration to secure body tissue with fastening elementUS8808329Apr 3, 2012Aug 19, 2014Bonutti Skeletal Innovations LlcApparatus and method for securing a portion of a bodyUS8814902Jul 31, 2006Aug 26, 2014Bonutti Skeletal Innovations LlcMethod of securing body tissueUS8845699Mar 6, 2012Sep 30, 2014Bonutti Skeletal Innovations LlcMethod of securing tissueUS8853294May 29, 2013Oct 7, 2014Biomimedica, Inc.Polyurethane-grafted hydrogelsUS8870572 *Jun 17, 2009Oct 28, 2014Woodwelding AgImplant, method of preparing an implant, implantation method, and kit of partsUS8870933Sep 20, 2007Oct 28, 2014Woodwelding AgImplant, implantation device, implantation methodUS8883915Aug 26, 2011Nov 11, 2014Biomimedica, Inc.Hydrophobic and hydrophilic interpenetrating polymer networks derived from hydrophobic polymers and methods of preparing the sameUS8932330Feb 17, 2004Jan 13, 2015P Tech, LlcMethod and device for securing body tissueUS8932337Nov 2, 2012Jan 13, 2015Woodwelding AgImplants for creating connections to tissue parts, in particular to skeletal parts, as well as device and method for implantation thereofUS8945192Nov 2, 2012Feb 3, 2015Woodwelding AgImplants for creating connections to tissue parts, in particular to skeletal parts, as well as device and method for implantation thereofUS8979934Jan 14, 2014Mar 17, 2015X-Spine Systems, Inc.Composite orthopedic implant having a low friction material substrate with primary frictional features and secondary frictional featuresUS8992703Sep 6, 2012Mar 31, 2015Howmedica Osteonics Corp.Laser-produced porous surfaceUS9017380Mar 30, 2007Apr 28, 2015Woodwelding AgSurgical method, kit of parts, and implantUS9017384May 13, 2009Apr 28, 2015Stryker SpineComposite spinal rodUS9050112Aug 22, 2012Jun 9, 2015Flexmedex, LLCTissue removal device and methodUS9060767Mar 2, 2009Jun 23, 2015P Tech, LlcTissue fastener and methods for using sameUS9067362Oct 31, 2007Jun 30, 2015P Tech, LlcMethod of using ultrasonic vibration to secure body tissue with fastening elementUS9089323Feb 21, 2006Jul 28, 2015P Tech, LlcDevice and method for securing body tissueUS9114024Nov 21, 2012Aug 25, 2015Biomimedica, Inc.Systems, devices, and methods for anchoring orthopaedic implants to boneUS9135374Apr 6, 2012Sep 15, 2015Howmedica Osteonics Corp.Surface modified unit cell lattice structures for optimized secure freeform fabricationUS9138222Feb 17, 2004Sep 22, 2015P Tech, LlcMethod and device for securing body tissueUS9149281Jun 7, 2013Oct 6, 2015P Tech, LlcRobotic system for engaging a fastener with body tissueUS9149286Nov 14, 2011Oct 6, 2015Flexmedex, LLCGuidance tool and method for useUS9155544Mar 20, 2002Oct 13, 2015P Tech, LlcRobotic systems and methodsUS9173647Feb 21, 2006Nov 3, 2015P Tech, LlcTissue fixation systemUS9173650May 31, 2011Nov 3, 2015P Tech, LlcMethods and devices for trauma weldingUS9180010Sep 14, 2012Nov 10, 2015Howmedica Osteonics Corp.Surface modified unit cell lattice structures for optimized secure freeform fabricationUS9192395May 7, 2013Nov 24, 2015P Tech, LlcRobotic fastening systemUS9216083Dec 19, 2014Dec 22, 2015Woodwelding AgImplants for creating connections to tissue parts, in particular to skeletal parts, as well as device and method for implantation thereofUS9220534 *Apr 27, 2009Dec 29, 2015Stryker Trauma GmbhImplantation pin kit and method for implanting an implantation pinUS9220609Feb 24, 2010Dec 29, 2015Spinewelding AgSpine stabilization device, and method and kit for its implantationUS9226828Sep 20, 2013Jan 5, 2016P Tech, LlcDevices and methods for stabilizing tissue and implantsUS9241740 *Sep 22, 2011Jan 26, 2016Spinewelding AgAnterior cervical plateUS9259329Nov 20, 2013Feb 16, 2016Stout Medical Group, L.P.Expandable support device and method of useUS9271741Aug 8, 2013Mar 1, 2016P Tech, LlcRobotic ultrasonic energy systemUS9271766Nov 11, 2013Mar 1, 2016P Tech, LlcDevices and methods for stabilizing tissue and implantsUS9271779Aug 13, 2013Mar 1, 2016P Tech, LlcMethods of using a robotic spine systemUS9301790Aug 28, 2013Apr 5, 2016Woodwelding AgDevice for fixation of bone fracturesUS9314349Mar 21, 2007Apr 19, 2016Stout Medical Group, L.P.Expandable support device and method of useUS9345524Apr 5, 2011May 24, 2016Stryker European Holdings I, LlcUltrasonic applicatorUS9357996 *Mar 26, 2015Jun 7, 2016DePuy Synthes Products, Inc.Fixation device with magnesium coreUS9364896Feb 7, 2013Jun 14, 2016Medical Modeling Inc.Fabrication of hybrid solid-porous medical implantable devices with electron beam melting technologyUS9387082Feb 24, 2014Jul 12, 2016The Board Of Trustees Of The Leland Stanford Junior UniversityHydrogel arthroplasty deviceUS9402668Dec 4, 2013Aug 2, 2016P Tech, LlcTissue fixation system and methodUS20030225438 *Jun 10, 2003Dec 4, 2003Bonutti Peter M.Method of using ultrasonic vibration to secure body tissueUS20040030341 *Mar 4, 2002Feb 12, 2004Marcel AeschlimannImplants, device and method for joining tissue partsUS20050220771 *Mar 24, 2005Oct 6, 2005Doctor's Research Group, Inc.Methods of performing medical procedures that promote bone growth, methods of making compositions that promote bone growth, and apparatus for use in such methodsUS20060105295 *Jan 28, 2005May 18, 2006Woodwelding AgImplant that can be implanted in osseous tissue and method for producing said implant corresponding implantUS20060147332 *Dec 30, 2004Jul 6, 2006Howmedica Osteonics Corp.Laser-produced porous structureUS20060167495 *Mar 8, 2006Jul 27, 2006Bonutti Peter MMethod of using ultrasonic vibration to secure body tissueUS20060241695 *Jul 10, 2006Oct 26, 2006Bonutti Peter MMethod of using ultrasonic vibration to secure body tissue with fastening elementUS20070260250 *May 5, 2006Nov 8, 2007Sdgi Holdings, Inc.Reinforcement of boney material surrounding a bone implantUS20070265704 *Mar 30, 2007Nov 15, 2007Woodwelding AgSurgical method, kit of parts, and implantUS20070299539 *Apr 12, 2007Dec 27, 2007Shadi OthmanUltrasound accelerated tissue engineering processUS20080050412 *Aug 15, 2006Feb 28, 2008Howmedica Osteonics Corp.Antimicrobial implantUS20080090207 *Mar 15, 2007Apr 17, 2008Ruedger RubbertCustomized dental prosthesis for periodontal- or osseointegration, and related systems and methodsUS20080109007 *Nov 17, 2006May 8, 2008Stryker Trauma GmbhImplantation device, applicator and sonotrodeUS20080109008 *Nov 21, 2006May 8, 2008Stryker Trauma GmbhImplantation device and method for applying the sameUS20080109080 *Sep 20, 2007May 8, 2008Woodwelding AgImplant, implantation device, implantation methodUS20080269649 *Apr 21, 2008Oct 30, 2008Stryker Trauma GmbhDevice and method for preparing a recess in a boneUS20090287251 *May 13, 2009Nov 19, 2009Stryker SpineComposite spinal rodUS20090317768 *Dec 24, 2009Woodwelding AgImplant, method of preparing an implant, implantation method, and kit of partsUS20100203478 *Apr 19, 2010Aug 12, 2010Natural Dental Implants, AgCustomized Dental Prosthesis for Periodontal or Osseointegration and Related Systems and MethodsUS20100274358 *Oct 28, 2010Spinewelding AgSpine stabilization device, and method and kit for its implantationUS20110224739 *Apr 27, 2009Sep 15, 2011Stryker Trauma GmbhImplantation pin kit and method for implanting an implantation pinUS20120251977 *Dec 6, 2010Oct 4, 2012Tomaso VercellottiEndosseous Dental ImplantUS20130304123 *Sep 22, 2011Nov 14, 2013Spinewelding AgAnterior cervical plateEP1917924A1Nov 2, 2006May 7, 2008Stryker Trauma GmbHImplantation deviceEP2898843A2Nov 9, 2010Jul 29, 2015Spinewelding AGMedical device, apparatus, and surgical methodEP2910207A1Nov 9, 2010Aug 26, 2015Spinewelding AGMedical device, apparatusEP2992860A1Feb 24, 2010Mar 9, 2016Spinewelding AGSpine stabilization device, and method and kit for its implantationEP3045129A1Sep 22, 2011Jul 20, 2016Spinewelding AGSurgical stabilizer plateWO2010096942A1Feb 24, 2010Sep 2, 2010Spinewelding AgSpine stabilization device, and method and kit for its implantationWO2012040863A1Sep 22, 2011Apr 5, 2012Spinewelding AgAnterior cervical plate* Cited by examinerClassifications U.S. Classification433/173, 433/174International ClassificationA61F2/02, A61B17/68, A61F2/00, A61B17/70, A61C8/00, A61L27/00, A61F2/44, A61F2/46, A61F2/30, A61F2/28Cooperative ClassificationA61C8/0019, A61C8/0018, A61F2002/30088, A61F2002/30892, A61C8/0012, A61F2002/4475, A61F2/4611, A61F2002/30064, A61F2002/30032, A61F2/0077, A61F2210/0004, A61F2250/003, A61F2/30767, A61F2210/008, A61F2002/4683, A61F2002/30784, A61F2002/30067, A61L2430/02, A61B17/70, A61B17/68, A61F2210/0071, A61F2002/30899, A61F2002/30884, A61F2002/30065, A61F2/447, A61C8/0016, A61F2002/4627, A61F2002/30878, A61B2017/00955, A61F2002/30062European ClassificationA61C8/00E3, A61B17/70, A61C8/00E, A61B17/68, A61F2/44F6, A61F2/46B7Legal EventsDateCodeEventDescriptionNov 11, 2003ASAssignmentOwner name: WOODWELDING AG, SWITZERLANDFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MAYER, JORG;AESCHLIMANN, MARCEL;TORRIANI, LAURENT;REEL/FRAME:014120/0233Effective date: 20031027Jan 22, 2009FPAYFee paymentYear of fee payment: 4Jan 17, 2013FPAYFee paymentYear of fee payment: 8RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services