Glass With Terminal (Nippon Sheet Glass) FreshPatents Stats n/a views for this patent on FreshPatents.comUpdated: November 20 2015 TOP 200 Companiesfiling patents this week
Glass with terminal Title: Glass with terminal.Abstract: A glass-with-terminal, in which a terminal is bonded to a glass without using solder, is disclosed. The glass-with-terminal has a configuration wherein a terminal (14) is bonded to a glass (11) provided on the surface thereof with a silver print (12). The terminal (14) includes a bent portion (21) formed, in at least one end of the terminal, to be bent toward the silver print (12). The terminal (14) is bonded to the glass (11) through an adhesive (23), so that the bent portion (21) makes contact with the upper surface of the silver print (12). ...
Browse recent Nippon Sheet Glass Company patentsUSPTO Applicaton #: #20120067641 - Class: 174 84 R (USPTO) - Inventors: Junichi Tokiwa, Miki Yoneyama
The Patent Description & Claims data below is from USPTO Patent Application 20120067641, Glass with terminal.
The present invention relates to a glass having a terminal (i.e., a “glass-with-terminal”), in which a terminal is bonded to a glass provided on the surface thereof with a silver print.
For example, a vehicle window glass is provided on the surface thereof with a silver print, and a terminal for supplying electricity to the silver print is bonded to the glass. The silver print is used as an antenna, and is connected via the terminal to a radio or TV unit provided in the vehicle. The silver print is also used as a conductor for a heating wire used for defogging the glass (see, e.g., Patent Literature 1 and Patent Literature 2).
FIG. 11 shows a glass-with-terminal disclosed in Patent Literature 1. Referring to FIG. 11, a terminal 100 is configured by legs 105, 106 bonded via solders 103, 104 to an upper side of a glass plate 102 with an electrically conductive film 101 coated on the upper surface thereof, and a support part 107 disposed at the end of the leg 106. A lead wire 109 extends from the end of a joint part 108 joined to the support part 107 to, e.g., an apparatus disposed in the vehicle, such as an electric power source.
In the configuration of the terminal 100, higher contact strength is ensured by increasing a bonding area of the solder 103, 104. However, in recent years, in view of reducing environmental concerns, it is desired to reduce the use of solder containing lead as much as possible.
FIG. 12 shows a terminal structure disclosed in Patent Literature 2. Referring to FIG. 12, a T-shaped terminal 110 includes a female-type terminal part 111 disposed at the distal end of a stem, and is bonded to a glass through an adhesive 112 and solder 113.
According to the T-shaped terminal 110, the usage of the solder can be reduced by using the adhesive 112 together with the solder 113. However, in this case, it is necessary to use the solder in order to reinforce the bonding strength of the adhesive.
If lead-free solder is used, the melting temperature thereof is higher and thus a stress generating at the time of solidification thereof is also higher compared to solder containing lead, and therefore, a glass is subjected to a greater load. Also, lead-free solder is higher in hardness than solder containing lead, and is therefore more readily broken by shock.
Further, in many recent designs, a terminal used for a window glass of a vehicle is mounted in the interior of the vehicle and is covered by an interior finishing material. A space inside the interior finishing material is limited, and the terminal has to be arranged inside the limited space. Thus, it is necessary to use a lead-free terminal without changing layout and a connecting condition for a vehicle-side connector.
Further, if an adhesive is provided directly on a surface of a silver print, long-term reliability of bonding strength is low. Therefore, it is desired to provide a glass-with-terminal, in which a terminal is bonded without using solder.
Patent Literature 1: Japanese Patent No. 3957302
Patent Literature 2: Japanese Unexamined Patent Publication No. 2003-521093
It is an object of the present invention to provide a glass-with-terminal, in which a terminal is bonded without using solder.
According to an aspect of the present invention, there is provided a glass-with-terminal, comprising a glass; a silver print provided on a surface of said glass; a terminal bonded to said glass provided with said silver print; wherein said terminal includes a terminal part adapted to be connected to an electrical component and a base part supporting said terminal part, said base part including a bent portion formed to be bent toward said silver print, said base part being made by using a material thinner than a material of said terminal part; and wherein said base part is bonded to said glass through an adhesive, so that said bent portion makes contact with an upper surface of said silver print.
Preferably, said adhesive is disposed on a non-printed area formed by cutting away a part of an extended pattern; and wherein said terminal is bonded to said glass at said non-printed area with said bent portion contacting the upper surface of said silver print.
Preferably, said bent portion includes a plurality of contact points contacting the upper surface of said silver print.
Preferably, said bent portion includes a distal end portion formed in an arcuate cross-sectional shape.
Preferably, said terminal has a height of 25 mm or less.
Preferably, said terminal has a width of 15 mm or less.
Preferably, said terminal has a length of 50 mm or less.
Preferably, said adhesive become hardened at room temperature.
Preferably, said base part is provided with at least one through-hole, and wherein said base part is sandwiched by said adhesive through said through-hole.
Preferably, said base part has a thickness in a range of 0.1 mm to 0.6 mm.
In another aspect of the present invention, there is provided a glass-with-terminal, comprising a glass; a silver print provided on a surface of said glass; a terminal bonded to said glass provided with said silver print; wherein said terminal includes a terminal part adapted to be connected to an electrical component and a base part supporting said terminal part, said base part including a bent portion formed to be bent toward said silver print, said base part being made by using a material thinner than a material of said terminal part; wherein said base part is bonded to said glass through an adhesive, so that said bent portion makes contact with an upper surface of said silver paint; and wherein said terminal is bonded to the upper surface of said silver print, the bonding surface of said silver print being previously treated with a primer.
In still another aspect of the present invention, there is provided a vehicle comprising an above-described glass-with-terminal mounted thereon.
The terminal includes the bent portion bent toward the silver print. A spring structure is obtained by bending the terminal, which urges the terminal in the direction of contact relative to the silver print. According to this structure, contact strength can be increased, which otherwise may be inadequate when only adhesive is used, and thus sufficient contact strength can be obtained.
The base part is thinner than the terminal part. By forming the base part thinner than the terminal part, the separation of the terminal due to repulsive force of the base part can be prevented, and the size of the terminal can be reduced.
The terminal is bonded to the glass at the non-printed area where the silver print is not applied. In other words, an adhesive layer for bonding the terminal to the glass is directly disposed on the upper surface of the glass. When the adhesive layer is disposed directly on the upper surface of the glass, as compared to an adhesive layer disposed on the upper surface of the silver print, initial adhesion strength is equivalent to that of the latter, but a remarkable effect (78.4 N or more) is verified through a humidity resistance test (50° C., RH 90% or higher, for 720 hrs). The non-printed area also includes, besides the glass surface, a black ceramic print area printed on the glass surface. In other words, the term “non-printed” of the non-printed area means that no silver print is provided.
The plurality of contact points contacting the upper surface of the silver print are provided. In other words, the terminal makes contact with the silver print at the plurality of contact points. As a result, the contact area of the terminal in contact with the silver print can be increased, and thereby the function of the terminal 14 can be stably exerted, even if the terminal is subjected to a flow of a large current or used in a location subjected to vibration. The configuration of the plurality of contact points is an effective means for preventing the occurrence of a spark due to the separation of the contact point when a large current is passed.
The distal end of the bent portion is formed in an arcuate cross-sectional shape. Due to the arcuate shape, a sharp contact point is eliminated, and thus the wear of the silver print can be prevented. The lifetime of the glass-with-terminal 10 is thereby increased.
The terminal is formed smaller than a specified size. In a spring contact structure, it is difficult to ensure installation volume, which may be accomplished by a conventional terminal using solder containing lead, and therefore, a separate structure of the present invention is required.
The adhesive becomes hardened at room temperature. If the hardening occurs at room temperature, residual stress caused in the glass due to a temperature difference at the time of rapid cooling can be suppressed as compared to a case wherein the hardening occurs at higher temperature.
The base part is provided with a single through-hole, and the base part is sandwiched in the adhesive via the through-hole. By sandwiching the base part in the adhesive, adhesion strength can be increased.
The base part has the thickness in the range of 0.1 mm to 0.6 mm. If the thickness is less than 0.1 mm, rigidity is inadequate, and if the thickness exceeds 0.6 mm, the remarkable effect of the reduction in thickness is deteriorated. Thus, according to the thickness of the base part in the range of 0.1 mm to 0.6 mm, a predetermined rigidity is ensured and the remarkable effect of the present invention is obvious.
The terminal is bonded to the glass at the upper surface of the silver print, and the silver print is previously treated with the primer. According to the pre-treatment with the primer, initial adhesion strength is equivalent, but high adhesion strength (78.4 N or higher) can be obtained through a humidity resistance test (50° C., RH 90% or higher, for 720 hrs).
The glass-with-terminal according to the present invention is suitable for an automobile that may be subjected to an external load, such as vibrations.
FIG. 1 is a front view showing a glass-with-terminal according to embodiment 1 of the present invention.
FIG. 3 is a view as seen in the direction of an arrow 3 of FIG. 2.
FIG. 4 is a view showing a manufacturing process of a glass-with-terminal according to embodiment 1.
FIG. 5 is a view showing a manufacturing process of a glass-with-terminal according to embodiment 2.
FIG. 6 is a view showing a manufacturing process of a glass-with-terminal according to embodiment 3.
FIG. 7 is a cross-sectional view showing a glass-with-terminal according to embodiment 4.
FIG. 8 is a cross-sectional view showing a glass-with-terminal according to embodiment 5.
FIG. 9 is a cross-sectional view showing a glass-with-terminal according to embodiment 6.
FIG. 10 is a view showing an exemplary process of joining a terminal part to a base part.
FIG. 11 is a cross-sectional view showing a conventional glass-with-terminal according to Patent Literature 1.
FIG. 12 is a view showing a conventional terminal according to Patent Literature 2.
Some preferred embodiments of the present invention will be described below with reference to appended drawings.
FIGS. 1 to 4 depict embodiment 1 of the present invention. Referring to FIG. 1, a glass-with-terminal 10 includes a glass 11 such as a window pane of a vehicle, a silver print 12 provided on the surface of the glass 11 and capable of functioning as an antenna, a non-printed area 13 free of the silver print 2, and a terminal 14 bonded to the glass 11 at the non-printed area 13 and electrically connecting vehicle-mounted units to the silver print 12.
Non-printed area 13 can be formed by masking a part of the surface of the glass 11 during a printing process of the silver print 12. Alternatively, it may be formed by cutting away a part of the silver print 12 after the silver print has been provided. Thus, a process of forming the non-printed area 13 can be optionally selected, as long as a resultant non-printed portion is obtained. It is advantageous to adopt the process of masking a part of the surface of the glass 11, since the non-printed area 13 can be formed in a short time.
On the other hand, if a conventionally-produced glass on which a silver print 12 is provided is used, the non-printed area 13 may be formed by cutting away a part of the silver print 12. Thus, the glass-with-terminal 10 can be manufactured by using a conventional glass-with-terminal. In this case, the terminal 14 can be arranged in a layout similar to a conventional terminal layout, and thus the glass-with-terminal 10 can be easily manufactured.
The non-printed area 13 also includes, besides the glass surface, a black ceramics print area printed on the glass surface. In other words, the term “non-printed” of the non-printed area means that no silver print is provided.
As depicted in FIG. 2, it is desirable that, before an adhesive 23 is applied, an oxide film is removed from the silver print 12. In this case, the adhesion strength of the adhesive 23 in relation to the silver print 12 can be increased.
It is desirable that the adhesive 23 become hardened at room temperature. If the hardening occurs at room temperature, residual stress caused in the glass 11 due to a temperature difference at the time of rapid cooling can be suppressed as compared to a case wherein the hardening occurs at higher temperature (e.g., at 150° C.).
As depicted in FIG. 2, the terminal 14 is formed by two plates having different thicknesses, and includes a base part 17 (e.g., 0.4 mm in thickness) with a lower surface thereof being bonded to an adhesive layer 16, and a terminal part 19 (e.g., 0.8 mm in thickness) extending upright from the base part 17 and connected at a female-type terminal portion 18 to TV unit or the like provided in the interior of a vehicle. The thickness of the base part 17 is smaller than the thickness of the terminal part 19, and may be in the range of 0.1 mm to 0.6 mm including the above-mentioned 0.4 mm.
It is desirable that the terminal 14 has a height of 25 mm or less, a width of 15 mm or less, and a length of 50 mm or less. Thus, the terminal 14 is formed with a size smaller than a predetermined size. In a spring contact structure, it is difficult to ensure permissible volume and adequate strength, which may be accomplished by using a conventional lead-containing-soldered terminal, if the base part 17 has a thickness equal to a thickness of the terminal part 19, and therefore, the separated structure of the present invention is required.
The base part 17 includes arcuate bent portions 21, 21 at opposite ends thereof, which are bent toward the silver print 12. The adhesive layer 16 is constructed by arranging a first double-sided tape 22, an adhesive 23, and a second double-sided tape 24, in the order from left to right in the drawing, along the longitudinal direction of the terminal 14. Reference numerals 26, 26 denote contact points at which the bent portions 21, 21 of the terminal 14 come into contact with the upper surface of the silver print 12. Thus, the terminal 14 contacts the upper surface of the silver print 12 at a plurality of contact points 26, 26.
In accordance with the glass-with-terminal 10, the terminal 14 includes the bent portions 21, 21 bent toward the silver print 12. A spring structure is obtained by bending the terminal 14, which enhances a force in the direction of contact made between the terminal 14 and the silver print 12. According to this structure, contact strength can be increased, which otherwise may be inadequate when only the adhesive 23 is used, and thus sufficient contact strength can be obtained.
The terminal 14 is bonded to the glass 11 at a non-printed area 13 where the silver print 12 is not applied. The adhesive layer for bonding the terminal 14 to the glass 11 is disposed directly on the upper surface of the glass 11. When the adhesive layer is directly disposed on the upper surface of the glass 11, as compared to an adhesive layer disposed on the upper surface of the silver print 12, initial adhesion strength is equivalent to that of the latter, but a remarkable effect (78.4 N or more) is verified through a humidity resistance test (50° C., RH of 90% or higher, for 720 hrs).
The terminal part 19 is formed so as to be thicker than the base part 17. In other words, the base part 17 is thinner than the terminal part 19. By forming the base part 17 thinner than the terminal part 19, a contact force generating toward the silver print is increased. High contact strength can be obtained while maintaining the function of the terminal part 19.
The plurality of contact points 26 contacting the upper surface of the silver print 12 are provided. The terminal 14 makes contact with the silver print 12 at the plurality of contact points 26. As a result, the contact area of the terminal 14 in contact with the silver print 12 can be increased, and thereby the function of the terminal 14 can be stably exerted, even if the terminal is subjected to a large current flow or used in a location subjected to vibration. The configuration of the plurality of contact points is an effective means for preventing the occurrence of a spark due to the separation of the contact point when a large current is passed.
The distal end of each of the bent portions 21, 21 is formed in an arcuate cross-sectional shape. Due to the arcuate shape, a sharp contact point is eliminated, and thus the wear of the silver print can be prevented. The lifetime of the glass-with-terminal 10 is thereby increased.
The above configuration can be summarized below.
In the glass-with-terminal 10, in which the terminal 14 is bonded to the glass 11 provided on the surface thereof with the silver print 12, the terminal 14 includes the base part 17 including the bent portions 21 formed to be bent toward the silver print 12 and the terminal part 19 thicker than the base part 17 and extending upright from the base part 17, and the terminal 14 is bonded to the glass 11 by the adhesive 23 so that the bent portions 21 make contact with the upper surface of the silver print 12.
The adhesive 23 is disposed at the non-printed area 13 of the glass 11, to which the silver print 12 is not applied. The terminal 14 is bonded to the glass 11 at the non-printed area 13, and thereby the bent portions 21 make contact with the upper surface of the silver print 12.
The plurality of contact points 23 contacting the upper surface of the silver print 12 are provided. The distal end of the bent portion 21 is formed in the arcuate cross-sectional shape.
In the above description, the adhesive layer 16 has an exemplary configuration in which the adhesive 23 is arranged between the first and second double-sided adhesive tapes 22, 24. However, the adhesive layer may be configured by arranging a double-sided adhesive tape between adhesives, or arranging side-by-side an adhesive and a double-sided adhesive tape. The arrangement of an adhesive and a double-sided tape is not limited to those described above. When a double-sided adhesive tape is arranged between adhesives, significantly high adhesion strength against a load in a tensile direction can be obtained.
As depicted in FIG. 3, the terminal 14 is bonded to the glass 11 at the non-printed area 13 where the silver print 12 is not applied, and the bent portions 21, 21 formed at the opposite ends make contact with the upper surface of the silver print 12. A process for manufacturing the glass-with-terminal 10 will be described below with reference to FIG. 4.
First, as depicted in FIG. 4(a), the glass 11 having the non-printed area 13, to which the silver print 12 is not applied, is provided.
Next, as depicted in FIG. 4(b), the first double-sided adhesive tape 22 and the second double-sided adhesive tape 24 are attached to the opposite ends of the non-printed area 13.
As depicted in FIG. 4(c), the adhesive 23 is disposed between the double-sided adhesive tapes 22 and 24, and, as depicted in FIG. 4(d), the terminal 14 is arranged so that the opposite ends of the terminal 14 come into contact with the upper surface of the silver print 12. The terminal 14 is thereby bonded to the double-sided adhesive tapes 22, 24 and the adhesive 23. Thus, the glass-with-terminal 10 as depicted in FIG. 3 has been completely manufactured.
In this configuration, the adhesive 23 may be first disposed and thereafter the double-sided tapes 22, 24 may be disposed, or alternatively, the adhesive 23 may be disposed and simultaneously the double-sided tapes 22, 24 may be attached. In any case, the double-sided adhesive tapes 22, 24 function so as to temporarily fix the terminal 14 until the adhesive 23 become hardened. These steps may be carried out in any order, as long as they are carried out before the terminal 14 is arranged.
In the case where a non-printed area 29 is formed in the shape of a U-groove as depicted in FIG. 5(a), the terminal 14 also can be electrically connected to the silver print 12 as depicted in FIG. 5(b). Even in this case, the adhesive layer is directly disposed on the upper surface of the glass, which can bring about an advantageous effect of the present invention such that the adhesive layer is bonded to the glass with higher adhesion strength.
In the case where a non-printed area 31 is formed in the shape of a window as depicted in FIG. 6(a), the terminal 14 also can be electrically connected to the silver print 12 as depicted in FIG. 6(b). Even in this case, the adhesive layer is directly disposed on the upper surface of the glass, which can bring about an advantageous effect of the present invention such that the adhesive layer is bonded to the glass with higher strength.
As depicted in FIG. 7, the adhesive layer 16 is disposed on the upper surface of the silver print 12. The terminal 14 is bonded to the glass 11 by the double-sided adhesive tapes 22, 24 and the adhesive 23. Even in this case, a force in the direction of contact made between the terminal 14 and the silver print 12, which can brings about an advantageous effect of the present invention such that contact strength can be increased, which otherwise likely be inadequate when only the adhesive 23 is used.
Further, when the silver print 12 is previously treated with a primer (a silane coupling agent), the following effect can be obtained.
In the glass-with-terminal, the terminal 14 being bonded to the glass 11 provided on the surface thereof with the silver print 12, the terminal 14 including the base part 17 including the bent portions 21 formed to be bent downward and the terminal part 19 thicker than the base part 17 and extending upright from the base part 17, and the terminal 14 being bonded to the glass 11 by the adhesive 23 so that the bent portions 21 make contact with the upper surface of the silver print 12, the terminal 14 is bonded to the glass 11 at the upper surface of the silver print, and the silver print 12 is previously treated with the primer.
According to the configuration wherein the silver print 12 is previously treated with the primer, as compared to the case where no previous treatment is performed, initial adhesion strength is equivalent to that of the latter, but high adhesion strength (78.4 N or higher) can be obtained through a humidity resistance test (50° C., RH 90% or higher, for 720 hrs).
← Previous Next → Advertise on FreshPatents.com - Rates & InfoYou can also Monitor Keywords and Search for tracking patents relating to this Glass with terminal patent application.
Browse recent Nippon Sheet Glass Company patents
How KEYWORD MONITOR works... a FREE service from FreshPatents1. Sign up (takes 30 seconds). 2. Fill in the keywords to be monitored. 3. Each week you receive an email with patent applications related to your keywords. Start now! - Receive info on patent apps like Glass with terminal or other areas of interest.###
Previous Patent Application:Electrical appliance with leaktight connections, and a method of fabricationNext Patent Application:Cable with a split tube and method for making the sameIndustry Class:Electricity: conductors and insulatorsThank you for viewing the Glass with terminal patent info.- - - Results in 0.14378 seconds Other interesting Freshpatents.com categories:
Computers: Graphics , I/O , Processors , Dyn. Storage , Static Storage , Printers ###Data source: patent applications published in the public domain by the United States Patent and Trademark Office (USPTO). Information published here is for research/educational purposes only. FreshPatents is not affiliated with the USPTO, assignee companies, inventors, law firms or other assignees. Patent applications, documents and images may contain trademarks of the respective companies/authors. FreshPatents is not responsible for the accuracy, validity or otherwise contents of these public document patent application filings. When possible a complete PDF is provided, however, in some cases the presented document/images is an abstract or sampling of the full patent application for display purposes. FreshPatents.com Terms/Support -g2-0.055366.232.115.224
Patent InfoApplication # US 20120067641 A1Publish Date 03/22/2012 Document # 13254968 File Date 01/13/2010 USPTO Class 174 84 R Other USPTO Classes International Class 01R4/00 Drawings 9 Follow us on Twitter@FreshPatents
Nippon Sheet Glass CompanyBrowse recent Nippon Sheet Glass Company patentsBrowse patents:Next →← Previous