Patent US6507006 - Ceramic substrate and process for producing the same - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsAn object of the present invention is to provide a ceramic substrate that is superior in heat uniformity and thermal shock resistance, and has a large chuck power in the case that the ceramic substrate is made to be an electrostatic chuck. The ceramic substrate of the present invention is a ceramic substrate...http://www.google.com/patents/US6507006?utm_source=gb-gplus-sharePatent US6507006 - Ceramic substrate and process for producing the sameAdvanced Patent SearchTry the new Google Patents, with machine-classified Google Scholar results, and Japanese and South Korean patents.Publication numberUS6507006 B1Publication typeGrantApplication numberUS 09/869,594PCT numberPCT/JP2000/003080Publication dateJan 14, 2003Filing dateMay 15, 2000Priority dateFeb 25, 2000Fee statusPaidAlso published asCN1175711C, CN1437837A, CN1592502A, EP1303167A1, US6878907, US20030042245, US20040140040, US20050023270, WO2001063972A1Publication number09869594, 869594, PCT/2000/3080, PCT/JP/0/003080, PCT/JP/0/03080, PCT/JP/2000/003080, PCT/JP/2000/03080, PCT/JP0/003080, PCT/JP0/03080, PCT/JP0003080, PCT/JP003080, PCT/JP2000/003080, PCT/JP2000/03080, PCT/JP2000003080, PCT/JP200003080, US 6507006 B1, US 6507006B1, US-B1-6507006, US6507006 B1, US6507006B1InventorsYasuji Hiramatsu, Yasutaka ItoOriginal AssigneeIbiden Co., Ltd.Export CitationBiBTeX, EndNote, RefManPatent Citations (12), Referenced by (109), Classifications (23), Legal Events (4) External Links: USPTO, USPTO Assignment, EspacenetCeramic substrate and process for producing the same
In the process for producing this semiconductor chip, a silicon wafer put on an electrostatic chuck is subjected to various treatments such as etching and CVD to form a conductor circuit, an element and the like. At this time, corrosive gas such as gas for deposition or gas for etching is used; therefore, it is necessary to protect an electrostatic electrode layer from corrosion by these gas. Since it is also necessary to induce adsorption power, the electrostatic electrode layer is usually coated with a ceramic dielectric film and the like.
As this ceramic substrate, Japanese Patent gazette No. 279850 and Japanese Patent gazette No. 2513995, JP Kokai Hei 11-74064 and so on describe electrostatic chucks with a heater which is produced through the process of stacking the green sheets, on which paste of a metal such as tungsten (W) is printed.
However, in ceramic substrates produced by such a process, problems as follows arise: cracks start to be generated at edges of their conductor layer such as a resistance heating element when thermal shock is given to the substrates; or a high temperature area is generated along the resistance heating element.
Furthermore, a scatter is generated in chuck power so that sufficient adsorption power cannot be obtained.
About an internal electrode or a resistance heating element, a leakage current between the electrodes or between the resistance heating elements at high temperature comes into a problem.
The inventors made eager investigations to solve the above-mentioned problems. As a result, the inventors have newly found out that these problems can be solved by making the edge of a cross section of conductor layer constituting an electrostatic electrode, an RF electrode and a resistance heating element into a peaked shape. Thus, the present invention has been made.
Namely, the present invention is a ceramic substrate comprising a conductor layer formed therein, characterized in that a section of the edge of the conductor layer is in a peaked shape.
In the case that the above-mentioned conductor layer in the ceramic substrate of the present invention is a resistance heating element, the present invention functions as a hot plate. In the case that the above-mentioned conductor layer is an electrostatic electrode, the present invention functions as an electrostatic chuck.
In the ceramic substrate, the conductor layer desirably has a portion in the peaked-shape having a width of 0.1 to 200 μm.
The process for producing a ceramic substrate of the present invention is characterized by printing a conductor layer on a ceramic green sheet, integrating the green sheet with another green sheet under heating and pressure, and then sintering the ceramic powder.
FIG. 1 is a plain view that schematically illustrates one example of a ceramic heater using a ceramic substrate of the present invention.
FIG. 4 is a sectional view taken along A—A line of the ceramic heater illustrated in FIG. 3.
FIGS. 8(a) through (d) are sectional views that schematically illustrate a part of the process for, producing the electrostatic chuck illustrated in FIG. 5.
FIG. 9 is a horizontal sectional view that schematically illustrates a shape of an electrostatic electrode constituting an electrostatic chuck according to the present invention.
FIG. 10 is a horizontal sectional view that schematically illustrates a shape of an electrostatic electrode constituting an electrostatic chuck according to the present invention.
FIG. 13 is a sectional view that schematically illustrates a guard electrode of the wafer prober illustrated in FIG. 12.
FIG. 14 is an SEM photograph showing a destruction section of a ceramic substrate constituting the electrostatic chuck according to Example 1.
2, 22, 32 a, 32 b chuck positive electrode electrostatic layer
3, 23, 33 a, 33 b chuck negative electrode electrostatic layer
2 a, 3 a semicircular part
2 b, 3 b comb-teeth-shaped part
7 metal line
16, 17, 18 plated through hole
25 a metal covering layer
66 a non-electrode forming area
The present invention is a ceramic substrate comprising a conductor layer formed therein, characterized in that a section of the edge of the conductor layer is in a peaked shape.
In the case that the conductor layer in the above-mentioned ceramic substrate is a resistance heating element, the present invention functions as a hot plate. In the case that the conductor layer is an electrostatic electrode, the present invention functions as an electrostatic chuck.
The ceramic substrate of the present invention is desirably used at 150� C. or higher, and is most desirably used at 200� C. or higher.
In the ceramic substrate, the conductor layer desirably has a portion in the peaked shape having a width of 0.1 to 200 μm, and more desirably has the peaked portion having a width of 5 to 100 μm.
In the process for producing the above-mentioned ceramic substrate, the following process is desirably adopted: a process of printing a conductor layer on a ceramic green sheet, integrating the green sheet with another green sheet under heating and pressure, and then sintering the ceramic powder.
In the case that the conductor layer embedded in the ceramic substrate used in the present invention is an electrode for inducing chuck power of an electrostatic chuck, that is, an electrostatic electrode, the edges of the electrode is in a peaked shape so that an electric field concentrates along the edge. Thus, large chuck power is considered to be induced.
The reason why cracks are generated by thermal shock is analyzed. A conductor layer produced by a conventional printing process and the like has a substantially rectangular section and, therefore, has a face perpendicular to a wafer processing surface (a surface for heating, supporting or adsorbing a semiconductor wafer). Moreover, the thermal expansion coefficient of the conductor layer is different from that of the ceramic constituting the ceramic substrate. Therefore, if the ceramic substrate is heated or cooled, power for separating the face perpendicular to the wafer processing surface of the conductor layer from the ceramic around the face is produced. This power would cause generation of cracks easily.
However, in the ceramic substrate of the present invention, its conductor layer has no face perpendicular to the wafer processing surface. As a result, cracks are not easily generated.
The reason why a high-temperature area is generated along the resistance heating element would be that heat is easily accumulated in the following portion inside the resistance heating element: the line intersection portion between the face perpendicular to the wafer processing surface and the face horizontal to the wafer processing surface. The reason why such a heat-accumulating phenomenon is caused is unclear. It is however presumed that heats are emitted and transmitted from both of the face perpendicular to the wafer processing surface and the face horizontal to the wafer processing surface so that these heats cross each other in the line intersection portion.
However, the ceramic substrate of the present invention has no face perpendicular to the wafer processing surface. Therefore, such a heat accumulating phenomenon is not caused so that heat uniformity of the wafer processing surface is superior.
Furthermore, in the case that the ceramic substrate has therein a conductor layer such as an electrode (a guard electrode and a ground electrode of a wafer prober, an electrode of an electrostatic chuck, an RF electrode and the like) or a resistance heating element, the faces perpendicular to the wafer processing surface of the conductor layer, if exist, confront each other. Thus, a leakage current is easily generated at high temperature. In the present invention, a section of the edge of the conductor is in a peaked shape. No faces confront each other. Thus, a leakage current is not easily generated at high temperature.
The ceramic substrate of the present invention is used in the range of 150� C. or higher, and preferably in the range of 200� C. or higher.
The conductor layer of the present invention may be an electrostatic electrode, a resistance heating element, an RF electrode and also may be a guard electrode or a ground electrode used in a wafer prober.
The conductor layer desirably has the peaked shape portion having a width of 0.1 to 200 μm. If the width of the peaked shape portion is over 200 μm, its ohmic resistance value is scattered. On the other hand, if the width is below 0.1 μm, the effect of preventing cracks is not caused. The width of the peaked shape portion is optimally from 5 to 100 μm. The curvature radius of the peaked shape portion is optimally from 0.5 to 500 μm.
In the ceramic substrate of the present invention, the pore diameter of the maximum pore is desirably 50 μm or less. The porosity thereof is desirably 5% or less. It is also desirable that no pores are present or, if present, the pore diameter of the maximum pore is 50 μm or less.
The reason why the pore diameter of the maximum pore is desirably 50 μm or less in the present invention is that if the pore diameter is over 50 μm, it is difficult to keep breakdown voltage property at high temperature and particularly at 200� C. or higher.
The pore diameter of the maximum pore is desirably 10 μm or less. This is because the amount of warp becomes small at 200� C. or higher.
The porosity and the pore diameter of the maximum pore are adjusted by press time, pressure and temperature at the time of sintering, or additives such as SiC and BN. Since SiC or BN hinders sintering, pores can be produced.
When the pore diameter of the maximum pore is measured, 5 samples are prepared. The surfaces thereof are polished into mirror planes. With an electron microscope, ten points on the surface are photographed with 2000 to 5000 magnifications. The maximum pore diameter is selected from the photos obtained by the photographing, and the average of the 50 shoots is defined as the pore diameter of the maximum pore.
The porosity is measured by Archimedes' method. This is a method of crushing a sintered product to pieces, putting the pieces into an organic solvent or mercury to measure the volume thereof, obtain the true specific gravity of the pieces from the weight and the volume thereof, and calculating the porosity from the true specific gravity and apparent specific gravity.
The diameter of the ceramic substrate of the present invention is desirably 200 mm or more. It is especially desirable that the diameter is 12 inches (300 mm) or more. This is because semiconductor wafers having such a diameter become main currents of the next-generation semiconductor: wafers.
The thickness of the ceramic substrate of the present invention is desirably 50 mm or less, and especially desirably 25 mm or less.
If the thickness of the ceramic substrate is over 25 mm, the thermal capacity of the ceramic substrate is too large. Particularly when a temperature control means is set up to heat or cool the substrate, temperature-following property may become poor because of the large thermal capacity.
The thickness of the ceramic substrate is optimally 5 mm or less. Incidentally the thickness of the ceramic substrate is desirably 1 mm or more.
The ceramic material constituting the ceramic substrate of the present invention is not especially limited. Examples thereof include nitride ceramics, carbide ceramics, and oxide ceramics.
Examples of the nitride ceramics include metal nitride ceramics such as aluminum nitride, silicon nitride and boron nitride.
Examples of the carbide ceramics include metal carbide ceramics such as silicon carbide, zirconium carbide, tantalum carbide, and tungsten carbide.
Examples of the oxide ceramics include metal oxide ceramics such as alumina, zirconia, cordierite and mullite.
The ceramic substrate preferably contains 0.1 to 5% by weight of oxygen. In this case, for example, the sintering of the nitride ceramic advances easily. Thus, even if the nitride ceramic contains pores, the pores are independently of each other so that the breakdown voltage is improved.
If the content is below 0.1% by weight, the breakdown voltage cannot be kept. Contrarily, if the content is over 5% by weight, the breakdown voltage property at high temperature of oxides becomes poor so that the breakdown voltage drops as well. If the oxygen content is over 5% by weight, the thermal conductivity drops so that temperature-rising and temperature-fall property becomes poor.
In order to incorporate oxygen into, for example, the nitride ceramic, it is general that the nitride ceramic powder is fired in an oxidizing atmosphere or that a metal oxide is mixed with ingredient powder of the nitride ceramic and then the mixture is sintered. In the case of the oxide ceramic, another oxide is mixed with it to make a complex oxide.
Examples of the metal oxide include yttria (Y2O3),alumina (Al2O3), rubidium oxide (Rb2O), lithium oxide (Li2O) and calcium oxide (CaCO3)
The content by percentage of these metal oxides is preferably from 0.1 to 20% by weight.
When carbon is incorporated into the ceramic carbon, carbon is preferably incorporated in the manner that its brightness will be below N4 as a value based on the rule of JIS Z 8721. The ceramic having such a brightness is superior in radiant heat capacity and covering property.
The brightness N is defined as follows: the brightness of ideal black is made to 0; that of ideal white is made to 10; respective colors are divided into 10 parts in the manner that the brightness of the respective colors is recognized stepwise between the brightness of black and that of white; and the resultant parts are indicated by symbols N0 through N10, respectively.
Actual brightness is measured by comparison with color signals corresponding to N0 through N10. One place of decimals in this case is made to 0 or 5.
The ceramic substrate of the present invention is a ceramic substrate used in a device for producing a semiconductor or examining a semiconductor. Examples of specific devices include an electrostatic chuck, a hot plate (ceramic heater) and a wafer prober.
In the case that the conductor formed inside the ceramic substrate is a resistance heating element, the ceramic substrate can be used as a ceramic heater (hot plate).
FIG. 1 is a plain view that schematically shows an example of a ceramic heater that is one embodiment of the ceramic substrate of the present invention. FIG. 2 is a partially enlarged section showing a part of the ceramic heater shown in FIG. 1.
A ceramic substrate 11 is made in a disk form. Inside the ceramic substrate 11, resistance heating elements 12 as temperature control means are formed in the pattern of concentric circles. About these resistor heating elements 12, two concentric circles near to each other are connected to produce one line as a circuit, and external terminals 13 that become inputting/outputting terminal pins are connected to both ends of the circuit via plated through holes 19. As shown in FIG. 2, sections of both edges of the resistance heating element 12 are in a peaked shape. Therefore, cracks based on thermal shock and the like are not easily generated in the ceramic substrate 11, and a heat-accumulating phenomenon is not generated in the edge of the resistance heating elements 12, either. Moreover, distribution of temperature in the wafer processing surface is not caused so that the temperature of the face becomes uniform.
As shown in FIG. 2, through holes 15 are made in the ceramic substrate 11, and support pins 26 are inserted into the through holes 15 to support a silicon wafer 9. By moving the support pins 26 up and down, it is possible to receive the silicon wafer 9 from a carrier machine, put the silicon wafer 9 on a wafer processing surface 11 a of the ceramic substrate 11 and heat the wafer 9, or support the silicon wafer 9 in the state that the wafer 9 is apart from the wafer processing surface 11 a at an distance of about 50 to 2000 μm and then heat the wafer 9. Bottomed holes 14 into which temperature-measuring elements such as thermocouples are fitted are made in a bottom surface 11 a of the ceramic substrate 11. When an electric current is passed through the resistance heating elements 12, the ceramic substrate 11 is heated so that a product to be heated, such as a silicon wafer, can be uniformly heated.
In the case of a ceramic heater, the resistance heating elements whose edge has a peaked-shape section are set inside the ceramic substrate. In this manner, the resistance heating elements have the advantages of the present invention. In the case of an electrostatic chuck or wafer prober that will be described later, the resistance heating elements may be set on the bottom surface of the ceramic substrate In this case, a section of the edge of an electrostatic electrode, a guard electrode, a ground electrode and so on is made into a peaked shape. In this manner, these electrodes have the above-mentioned advantageous effects of the present invention.
In the case that the resistance heating elements are set inside the ceramic substrate, an coolant outlet for a coolant such as air as a cooling means may be made in a supporting case into which the ceramic substrate is fitted. In the case that the resistance heating elements are set inside the ceramic substrate, each of the resistance heating elements may be made of a plurality of layers. In this case, the patterns of the respective layers may be formed to complement them mutually. A pattern is desirably formed on any one of the layers when being viewed from the heating surface. For example, a structure having a staggered arrangement is desirable.
The resistance heating element is desirably made of a metal such as a noble metal (gold, silver, platinum and palladium), lead, tungsten, molybdenum, nickel; and a conductive ceramics such as tungsten carbide and molybdenum carbide. These can make the ohmic resistance value high and make the thickness itself large to prevent the element-disconnection and the like, and are not easily oxidized. Their thermal conductivity is not easily lowered, either. These may be used alone or in combination of two or more.
Since it is necessary that the temperature of the whole of the ceramic substrate is made uniform, the resistance heating element preferably has a pattern of concentric circles shown in FIG. 1, or a combination of a pattern of concentric circles and that of bent lines. The thickness of the resistance heating element is desirably from 1 to 50 μm, and the width thereof is preferably from 5 to 20 mm. The resistance heating element desirably has the peaked shape portion having a width of 0.1 to 200 μm.
By changing the thickness or the width of the resistance heating element, its ohmic resistance value can be changed; however, the above-mentioned ranges are most practical. As the resistance heating element becomes thinner or narrower, the ohmic resistance value of the resistance heating element becomes larger.
If the resistance heating element is set inside, the distance between a heating surface and the resistance heating element becomes close so that uniformity of the temperature of the surface becomes poor. Thus, it is necessary to widen the width of the resistance heating element itself. Since the resistance heating element is set inside the ceramic substrate, it is unnecessary to consider adhesiveness of this element to the ceramic substrate.
A section of the resistance heating element may be rectangular, elliptic, spindle-shaped, or semicylindrical. The section is desirably flat. A section of the edge of the resistance heating element is desirably in a peaked shape. This is because; if the section is flat, heat is easier to be radiated toward the heating surface, so that the amount of heat transmitted to the heating surface can be made large. Thus, temperature distribution in the heating surface is not easily formed. The shape of the resistance heating element may be spiral.
When the resistance heating elements are formed inside the ceramic substrate, the resistance heating elements are desirably formed within the domain extending from the bottom of the substrate up to 60% of the thickness thereof. This is because the temperature distribution in the heating surface is removed so that a semiconductor wafer can be uniformly heated.
A thing to be heated, such as a semiconductor wafer, can be directly put on the heating surface and then heated. The product may be kept about 50 to 200 μm apart from the heating surface and then heated.
In order to form the resistance heating elements on the bottom surface of the ceramic substrate for semiconductor devices of the present invention, or inside the ceramic substrate, it is preferred to use a conductor containing paste comprising a metal or a conductive ceramic.
Namely, in the case that the resistance heating elements are formed on the bottom surface of the ceramic substrate, sintering is usually performed to produce the ceramic substrate and then a layer of the conductor containing paste is formed on the surface of the ceramic substrate and sintered to produce the resistance heating elements.
On the other hand, in the case that the resistance heating elements 12 are formed inside the ceramic substrate 12 as shown in FIGS. 1 and 2, a layer of the conductor containing paste is formed on a green sheet and then the green sheet is integrated with another green sheet under heating and pressure to produce a lamination of the green sheets. At this time, the conductor containing paste layer having the edge in a peaked shape can be formed by heating the lamination up to a temperature at which the conductor containing paste after drying is liable to deform to some extent. Thereafter, the lamination is sintered to make the resistance heating elements whose edge has a section in a peaked shape inside the ceramic substrate.
The conductor containing paste is not limited. Preferably, the conductor containing paste contains a resin, a solvent, a thickener and so on, as well as metal particles or conductive ceramic particles to ensure conductivity.
The material of the metal particles or the conductive ceramic particles may be the above-mentioned ones. The particle diameter of the metal particles or the conductive ceramic particles is preferably from 0.1 to 100 μm. If the diameter is too fine, that is, below 0.1 μm, these particles are easily oxidized. On the other hand, if the diameter is over 100 μm, these particles are not easily sintered so that the ohmic resistance value becomes large.
The shape of the metal particles may be spherical or scaly. In the case that these metal particles are used, a mixture of spherical particles and scaly particles can be used.
The case that the above-mentioned metal particles are scaly, or are a mixture of spherical and scaly particles is profitable since metal oxides are easily kept between the metal particles so that the adhesion between the resistance heating elements and ceramic substrate is made sure and the ohmic resistance value can be made large.
Examples of the resin used in the conductor containing paste include acrylic resins, epoxy resins, and phenol resins. An example of the solvent is isopropyl alcohol and the like. An example of the thickener is cellulose and the like.
When the conductor containing paste for the resistance heating elements is formed on the surface of the ceramic substrate, it is preferred to add not only these metal particles but also a metal oxide to the conductor containing paste and sinter the metal particles and the metal oxide. By sintering the metal oxide together with the metal particles as described above, the ceramic substrate still more adhered to the metal particles can be obtained.
The reason why the adhesiveness of the metal particles to the ceramic substrate is improved by the mixing of the metal oxide is unclear, but would be as follows: the surface of the metal particles or the surface of the ceramic substrate comprising non-oxides is slightly oxidized to form oxidized films; and the oxidized films are sintered and integrated with each other through the metal oxide, so that the metal particles are closely adhered to the ceramic. In the case that the ceramic constituting the ceramic substrate is an oxide, the surface thereof is naturally made of the oxide. Therefore, the conductor layer superior in adhesiveness is formed.
Preferred examples of the above-mentioned oxide may be at least one selected from the group consisting of lead oxide, zinc oxide, silica, boron oxide (B2O3), alumina, yttria and titania.
These oxides can improve the adhesiveness between the metal particles and the ceramic substrate without increasing the ohmic resistance value of the resistance heating element.
When the total amount of the metal oxides is, made to 100 parts by weight, the weight ratio of lead oxide, zinc oxide, silica, boron oxide (B2O3) , alumina, yttria and titania is as follows: lead oxide: 1 to 10, silica: 1 to 30, boron oxide: 5 to 50, zinc oxide: 20 to 70, alumina: 1 to 10, yttria: 1 to 50 and titania: 1 to 50, and the ratio preferably being adjusted within the scope that the total thereof is not over 100 parts by weight.
By adjusting the amounts of these oxides within these ranges, the adhesiveness to the ceramic substrate can be particularly improved.
The addition amount of the metal oxides to the metal particles is preferably from 0.1% by weight (including 0.1%) to 10% by weight (not including 10%) . The area resistivity when the conductor containing paste having such a structure is used to form the resistance heating element is preferably from 1 to 45 mΩ/□.
If the area resistivity is over 45 mΩ/□, the calorific value to an applied voltage becomes too large so that, in the ceramic substrate for semiconductor devices wherein resistance heating elements are set on its surface, its calorific value is not easily controlled. If the addition amount of the metal oxides is 10% or more by weight, the area resistivity exceeds 50 mΩ/□ so that the calorific value becomes too large. Thus, temperature-control is not easily performed so that the uniformity in temperature distribution becomes poor.
In the case that the resistance heating elements are formed on the surface of the ceramic substrate, a metal covering layer is preferably formed on the surfaces of the resistance heating elements. The metal covering layer prevents a change in the ohmic resistance value resulting from the oxidization of the inner metal sintered product. The thickness of the formed metal covering layer is preferably from 0.1 to 10 μm.
The metal used for forming the metal covering layer is not particularly limited provided that the metal is a metal which is hardly oxidized. Specific examples thereof include gold, silver, palladium, platinum, and nickel. These may be used alone or in combination of two or more. Among these metals, nickel is preferred.
In the case that the resistance heating elements are formed inside the ceramic substrate, no covering is necessary since the surfaces of the resistance heating elements are not oxidized.
In the case that the conductor formed inside the ceramic substrate is an electrostatic electrode layer, the ceramic substrate can be used as an electrostatic chuck. In this case, an RF electrode and resistance heating elements may be formed as conductors below the electrostatic electrode and inside the ceramic substrate.
FIG. 3 is a vertical sectional view that schematically shows one embodiment of an electrostatic chuck according to the present invention. FIG. 4 is a sectional view taken on A—A line of the electrostatic chuck shown in FIG. 3.
In this electrostatic chuck 101, an electrostatic electrode layer composed of a chuck positive electrostatic layer 2 and a chuck negative electrostatic layer 3 is buried in a disk-shaped ceramic substrate 1. A thin ceramic layer 4 (hereinafter referred to as a ceramic dielectric film) is made on the electrostatic electrode layer. A silicon wafer 9 is put on the electrostatic chuck 101 and is earthed.
As shown in FIG. 4, the chuck positive electrostatic layer 2 is composed of a semicircular part 2 a and a comb-teeth-shaped part 2 b. The chuck negative electrostatic layer 3 is also composed of a semicircular part 3 a and a comb-teeth-shaped part 3 b. These chuck positive electrostatic layer 2 and chuck negative electrostatic layer 3 are arranged by facing each other so that the comb-teeth-shaped parts 2 b and 3 b cross each other. The positive side and the negative side of a direct power source are connected to the chuck positive electrostatic layer 2 and chuck negative electrostatic layer 3, respectively. Thus, a direct current V2 is applied thereto.
As shown in FIG. 3, a section of the edges of the resistance heating elements 5, and a section of the edge of the semicircular parts 2 a and 3 a and the comb-teeth-shaped parts 2 b and 3 b, which constitute the chuck positive electrostatic layer 2 and the chuck negative electrostatic layer 3, respectively, are in a peaked shape.
In order to control the temperature of the silicon wafer 9, resistance heating elements 5 in the form of concentric circles as viewed from the above, as shown in FIG. 1, are set up inside the ceramic substrate 1. External terminals are connected and fixed to both ends of the resistance heating elements 5, and a voltage V1 is applied thereto. A bottomed hole into which a temperature-measuring element is inserted and a through hole through which a support pin (not illustrated) that supports the silicon wafer 9 and moves it up and down penetrates are made in the ceramic substrate 1, as shown in FIGS. 1 and 2 but not shown in FIGS. 3 and 4. The resistance heating elements may be formed on the bottom surface of the ceramic substrate.
In the electrostatic chuck 101 according to the present invention, the section of the edge of the chuck positive and negative electrostatic layers 2 and 3 is in a peaked shape; therefore, an electric field concentrates along the edge so that a large chuck power is induced. Since the section of the edge of the chuck positive and negative electrostatic layers 2 and 3 and the resistance heating elements 5 is in a peaked shape, cracks are not easily generated and no heat-accumulating phenomenon is generated in the edge of the resistance heating elements 5.
In the electrostatic chuck 101, the ceramic dielectric film 4 is made of a nitride ceramic containing oxygen, and desirably has a porosity of 5% or less and a maximum pore diameter of 50μm or less. The pores in this ceramic dielectric film 4 are desirably composed of pores independent of each other.
In the ceramic dielectric film 4 having such a structure, it does not happen that gas and so on which will lower the breakdown voltage penetrate through the ceramic dielectric film to corrode the electrostatic electrodes. Moreover, the breakdown voltage of the ceramic dielectric film does not drop even at high temperature.
In the case that the Peltier device is used as the temperature control element, both heating and cooling can be attained by changing the direction along which an electric current passes. Thus, this case is advantageous.
Examples of the Peltier device include silicon/germanium, bismuth/antimony, and lead/tellurium materials and the like.
The material of the ceramic dielectric film constituting the electrostatic chuck of the present invention is not particularly limited. Examples thereof include oxide ceramics, nitride ceramics and oxide ceramics and the like. Among these, nitride ceramics are preferred.
As this nitride ceramic, the same as materials of the above-mentioned ceramic substrate can be listed up. The nitride ceramic desirably contains oxygen. In this case, the sintering of the nitride ceramic advances easily. In the case that the nitride ceramic substrate includes pores, the pores are formed to be independent of each other so that the breakdown voltage is improved.
The metal oxide may be alumina (Al2O3) , silicon oxide (SiO2), and the like.
By setting the thickness of the ceramic dielectric film to 50 to 5000 μm, sufficient breakdown voltage can be kept without lowering chucking power.
If the thickness of the ceramic dielectric film is less than 50μm, the thickness is too thin to obtain sufficient breakdown voltage. Thus, when a silicon wafer is put and adsorbed thereon, the ceramic dielectric film may undergo dielectric breakdown. On the other hand, if the thickness of the ceramic dielectric film is over 5000 μm, the distance between the silicon wafer and the electrostatic electrodes is large so that the capability of adsorbing the silicon wafer is lowered. The thickness of the ceramic dielectric film is preferably from 100 to 1500 μm.
Preferably, the porosity of the ceramic dielectric film is 5% or less and the pore diameter of maximum pores is 50 μm or less.
If the porosity is over 5%, the number of the pores increases and the diameter of the pores becomes too large so that the pores are easily connected to each other. In ceramic dielectric films having such a structure, their breakdown voltage drops.
When the pore diameter of the maximum pores is over 50 μm, breakdown voltage cannot be kept at high temperature even if oxides are present at boundaries between the grains. The porosity is preferably from 0.01 to 3%. The diameter of the maximum pores is preferably from 0.1 to 10 μm.
The ceramic dielectric film desirably contains 50 to 5000 ppm of carbon. This is because carbon can hide the electrode pattern arranged in the electrostatic chuck and give high radiant heat. As the volume resistivity is lower, the adsorption power of the silicon wafer becomes higher at low temperatures.
The electrostatic electrode may be, for example, a sintered product made of a metal or a conductive ceramic, or a metal foil. As the metal sintered product, a product made of at least one selected from tungsten and molybdenum is preferable. The metal foil is preferably made of the same as the raw material of the metal sintered product as well. This is because these metals are not relatively liable to be oxidized and have sufficient conductivity for electrodes. In this case, the edge of the metal foil is heated and pressed, or is made into a peaked shape by chemical or physical etching. Examples of the chemical etching include etching with an acidic or alkaline solution. Examples of the physical etching include ion beam etching, and plasma etching. As the conductive ceramic, there may be used at least one selected from carbides of tungsten and molybdenum.
FIGS. 9 and 10 are horizontal sectional views, each of which schematically shows an electrostatic electrode in other electrostatic chuck. In an electrostatic chuck 20 shown in FIG. 9, a chuck positive electrostatic layer 22 and a chuck negative electrostatic layer 23 in a semicircular form are formed inside a ceramic substrate 1. In an electrostatic chuck shown in FIG. 10, chuck positive electrostatic layers 32a and 32 b and chuck negative electrostatic layers 33 a and 33 b, each of which has shape obtained by dividing a circle into 4 parts, are formed inside a ceramic substrate 1. The two chuck positive electrostatic layers 22 a and 22 b and the two chuck negative electrostatic layers 33 a and 33 b are formed to cross.
A section of the edge of these electrostatic electrodes is also in a peaked shape. An electric field, therefore, concentrates along the edge of the electrostatic electrodes so that a large chuck power is induced. Cracks are not easily generated in the ceramic substrate.
In the case that an electrode having a form that an electrode in the shape of a circle and the like is divided is formed, the number of divided pieces is not particularly limited and may be 5 or more. Its shape is not limited to a fan-shape.
Examples of the electrostatic chuck in the present invention include the electrostatic chuck 101 having a structure wherein the chuck positive electrostatic layer 2 and the chuck negative electrostatic layer 3 are arranged between the ceramic substrate 1 and the ceramic dielectric film 4 and the resistance heating elements 5 are set up inside the ceramic substrate 1, as shown in FIG. 3; the electrostatic chuck 201 having a structure wherein the chuck positive electrostatic layer 2 and the chuck negative electrostatic layer 3 are arranged between the ceramic substrate 1 and the ceramic dielectric film 4 and the resistance heating elements 25 are disposed on the bottom surface of the ceramic substrate 1, as shown in FIG. 5; the electrostatic chuck 301 having a structure wherein the chuck positive electrostatic layer 2 and the chuck negative electrostatic layer 3 are arranged between the ceramic substrate 1 and the ceramic dielectric film 4 and the metal line 7, which is a resistance heating element, is buried in the ceramic substrate 1, as shown in FIG. 6, and the electrostatic chuck 401 having a structure wherein the chuck positive electrostatic layer 2 and the chuck negative electrostatic layer 3 are arranged between the ceramic substrate 1 and the ceramic dielectric film 4 and the Peltier device 8 composed of the thermoelectric element 81 and the ceramic plate 82 is formed on the bottom surface of the ceramic substrate 1, as shown in FIG. 7.
A section of the edge of the electrostatic electrodes in these electrostatic chucks is in a peaked shape. Therefore, a large chuck power is induced. Cracks are not easily generated in the ceramic substrate.
As shown in FIGS. 3 through 7, in the present invention the chuck positive electrostatic layer 2 and the chuck negative electrostatic layer 3 are arranged between the ceramic substrate 1 and the ceramic dielectric film 4 and the resistance heating elements 5 or the metal line 7 is formed inside the ceramic substrate 1. Therefore, connecting units (plated through holes) 16, 17 are necessary for connecting these units to external terminals. The plated through holes 16, 17 are made by filling with a high melting point metal such as tungsten paste or molybdenum paste, or a conductive ceramic such as tungsten carbide or molybdenum carbide.
The diameter of the connecting units (plated through holes) 16, 17 is desirably from 0.1 to 10 mm. This is because disconnection can be prevented and further cracks or strains can be prevented.
The connecting thereof is performed with solder or brazing-filler. As the brazing-filler, brazing silver, brazing palladium, brazing aluminum, or brazing gold is used. Brazing gold is desirably Au—Ni alloy. Au—Ni alloy is superior in adhesiveness to tungsten.
The thickness of the Au—Ni layer is desirably from 0.1 to 50 μm. This is because this range is a range sufficient for keeping connection. If Au—Cu alloy is used at a high temperature of 500 to 1000� C. and at a high vacuum of 10−6 to 10−5 Pa, the Au—Cu alloy deteriorates. However, Au—Ni alloy does not cause such deterioration and is profitable. When the total amount of the Au—Ni alloy is regarded as 100 parts by weight, the amount of impurities therein is desirably below 1 part by weight.
If necessary, in the present invention a thermocouple may be buried in the bottomed hole in the ceramic substrate. This is because the thermocouple makes it possible to measure the temperature of the resistance heating element and, on the basis of the resultant data, voltage or electric current is changed so that the temperature can be controlled.
The size of the connecting portions of metal lines of the thermocouples is the same as the strand diameter of the respective metal lines or more, and is preferably 0.5 mm or less. Such a structure makes the thermal capacity of the connecting portion small, and causes a temperature to be correctly and speedy converted to a current value. For this reason, temperature control ability is improved so that the temperature distribution of the heated surface of the wafer becomes small.
The electrostatic chuck 101 is fitted into the supporting case 41 through a heat insulator 45. Coolant outlets 42 are made in the supporting case 11, and a coolant is blown from a coolant inlet 44 and passes outside an inhalation duct 43 through the coolant outlet 42. By the action of this coolant, the electrostatic chuck 101 can be cooled.
The following will describe one example of the process for producing an electrostatic chuck as one example of the ceramic substrate of the present invention on the basis of sections shown in FIGS. 8(a through (d).
As the ceramic powder, there may be used, for example, oxygen-containing aluminum nitride powder. If necessary, a sintering aid such as alumina or sulfur may be added.
One or several green sheets 50′ laminated on the green sheet on which an electrostatic electrode layer printed unit 51 that will be described later is formed are layers which will be a ceramic dielectric film 4; therefore, the sheets 50′ may have a composition different from that of the ceramic substrate if necessary.
Usually, the raw material of the ceramic dielectric film 4 and that of the ceramic substrate 1 are desirably the same. This is because these are sintered under the same condition since these are sintered together in many cases. In the case that the raw materials are different, it is allowable that a ceramic substrate is firstly produced, an electrostatic electrode layer is formed thereon and then a ceramic dielectric film is formed thereon.
As the binder, desirable is at least one selected from an acrylic binder, ethylcellulose, butylcllusolve, and polyvinyl alcohol.
If necessary, a through hole into which a support pin of a silicon wafer is inserted, a concave portion in which the thermocouple is buried may be made in the green sheet 50, and further a through hole may be made in a portion where a plated through hole and the like is to be formed. The through hole can be made by punching and the like.
Next, a conductor containing paste is filled up into the through holes in the green sheet 50, to obtain plated through hole printed units 53, 54. Next, a conductor containing paste that will be electrostatic electrode layers and resistance heating elements is printed on the green sheet 50.
As such a paste, the following conductor containing paste is optimal: a conductor containing paste prepared by mixing 85 to 97 parts by weight of the metal particles or the conductive ceramic particles; 1.5 to 10 parts by weight of at least one binder selected from acrylic, ethylcellusolve, butylcellusolve and polyvinyl alcohol; 1.5 to 10 parts by weight of at least one solvent selected from α-terpineol, glycol, ethyl alcohol, and butanol.
Next, as shown in FIG. 8(a), the green sheet 50 having the printed units 51, 52, 53 and 54 and the green sheet 50′ having no printed units are made into a lamination. The reason why the green sheet 50′ having no printed units at the side where the resistance heating elements are formed is deposited is that the following phenomenon is prevented: the end faces of the plated through holes are exposed and the end faces are oxidized at the time of the sintering for the formation of the resistance heating elements. If the sintering for the formation of the resistance heating elements is performed in the state that the end faces of the plated through holes are exposed, it is necessary to sputter a metal which is not easily oxidized, such as nickel. More preferably, the end faces may be covered with brazing gold of Au—Ni.
(2) Next, as shown in FIG. 8(b), the lamination is heated and pressed to form a lamination of the green sheets. The conductor containing paste layer is pressed at this time. Thus, in the case that the formed conductor containing paste layer contains an appropriate binder, a section of the edge thereof turns into a peaked shape. The heating temperature of the lamination is preferably from 50 to 300� C., and the pressure upon the pressing is preferably from 20 to 200 kg/cm2.
Thereafter, the green sheets and the conductor containing paste are sintered.
The temperature at the time of the sintering is preferably from 1000 to 2000� C. and pressure at the time of the sintering is preferably from 100 to 200 kgf/cm2. The heating and the pressing are performed in the atmosphere of inert gas. As the inert gas, argon, nitrogen and the like can be used. In this sintering step, plated through holes 16 and 17, and also the chuck positive electrostatic layer 2, the chuck negative electrostatic layer 3, the resistance heating elements 5, the edge of which is in a peaked shape, and so on can be formed.
(3) Next, as shown in FIG. 8(c), blind holes 35 and 36 for connecting external terminals are made.
It is desirable that at least a part of inside walls of the blind holes 35, 36 is made conductive and the conductive part of the inside walls is connected to the chuck positive electrostatic layer 2, the chuck negative electrostatic layer 3, the resistance heating elements 5 and so on.
(4) At last, as shown in FIG. 8(d), external terminals 6 and 18 are fitted into the bottomed holes 35, 36 through brazing gold. If necessary, a bottomed hole may be made so that a thermocouple may be buried therein.
As solder, an alloy such as silver-lead, lead-tin or bismuth-tin can be used. The thickness of the solder layer is desirably from 0.1 to 50 μm. This is because this range is a range sufficient for maintaining the connection based on the solder.
In the above description, the electrostatic chuck 101 (see FIG. 3) is given as an example. In the case that the electrostatic chuck 201 (see FIG. 5) is produced, it is advisable to produce a ceramic plate having an electrostatic electrode layer first, print a conductor containing paste on the bottom surface of this ceramic plate, sinter the resultant, form the resistance heating elements 25 and then form the metal covering layer 25 a by electroless plating or the like. In the case that the electrostatic chuck 301 (see FIG. 6) is produced, it is advisable that a metal foil or a metal line is buried, as electrostatic electrodes or resistance heating elements, in ceramic powder and then the resultant is sintered.
In the case that the electrostatic chuck 401 (see FIG. 7) is produced, it is advisable that a ceramic plate having an electrostatic electrode layer is produced and then a Peltier device is jointed to the ceramic plate through a metallized metal layer.
The above-mentioned ceramic substrate functions as a wafer prober in the following case: conductors are arranged on the surface of the ceramic substrate of the present invention and inside the ceramic substrate; the conductor layer on the surface is a chuck top conductor layer; and the inside conductor is either of a guard electrode or a ground electrode.
In this wafer prober 501, grooves 67, in the form of concentric circles as viewed from the above, are made in the surface of a disc-form ceramic substrate 63. Moreover, suction holes 68 for sucking a silicon wafer are made in a part of the grooves 67. A chuck top conductor layer 62 for connecting electrodes of the silicon wafer is formed, in a circular form, in the greater part of the ceramic plate 63 including the grooves 67.
On the other hand, resistance heating elements 61 as shown in FIG. 1, in the form of concentric circles as viewed from the above, are disposed on the bottom surface of the ceramic substrate 63 to control the temperature of the silicon wafer. External terminals (not illustrated) are connected and fixed to both ends of the resistance heating element 61. Inside the ceramic substrate 63, a guard electrode 65 and a ground electrode 66 (see FIG. 13), in the form of a lattice as viewed from the above, are disposed. Since a section of the edge of the guard electrode 65 and the ground electrode 66 is in a peaked shape, cracks are not easily generated.
In the electrostatic chuck, the resistance heating elements 61 may be set inside the ceramic substrate 63. In this case, if a section of the edge of the resistance heating elements 61 is made into a peaked shape, cracks are not easily generated and a heat-accumulating phenomenon is not easily generated.
The raw material of the guard electrode 65 and the ground electrode 66 may be the same as that of the electrostatic electrode.
The thickness of the chuck top conductor layer 62 is desirably from 1 to 20 μm. If the thickness is below 1 μm, its resistance is too high so as not to function as an electrode. On the other hand, if the thickness is over 20 μm, the layer exfoliates easily by stress that the conductor has.
According to the wafer prober having such a structure, a continuity test can be performed by putting a silicon wafer on which integrated circuits are formed, pushing a probe card having tester pins against the silicon wafer and applying a voltage thereto while heating and cooling the wafer. In the case that a wafer prober is produced, for example, a ceramic substrate wherein resistance heating elements are embedded is firstly produced in the same manner as in the case of the electrostatic chuck. Thereafter, grooves are made on the surface of the ceramic substrate and subsequently the surface in which the grooves are made is subjected to sputtering, plating and so on, to form a metal layer.
Production of an Electrostatic Chuck (see FIG. 3)
(1) The following paste was used to conduct formation by doctor blade method to obtain a green sheet 0.47 μm in thickness: a paste obtained by mixing 100 parts by weight of aluminum nitride powder (made by Tokuyama Corp., average particle diameter: 1. 1 μm), 4 parts by weight of yttria (average particle diameter: 0.4 μm), 11.5 parts by weight of an acrylic binder, 0.5 part by weight of a dispersant and 53 parts by weight of mixed alcohols of 1-butanol and ethanol.
(2) Next, this green sheet was dried at 80� C. for 5 hours, and subsequently the following holes were made by punching: holes which would be through holes through which semiconductor wafer supporting pins 1.8 mm, 3.0 mm and 5.0 mm in diameter were inserted; and holes which would be plated through holes for connecting external terminals.
This conductor containing paste A was printed on the green sheet by screen printing to form a conductor containing paste layer. The pattern of the printing was made into a concentric pattern. Furthermore, conductor containing paste layers having an electrostatic electrode pattern shown in FIG. 4 were formed on other green sheets.
Moreover, the conductor containing paste B was filled into the through holes for the plated through holes for connecting external terminals.
Thirty four green sheets 50′ on which no tungsten paste was printed were stacked on the upper side (heating surface) of the green sheet 50 that had been subjected to the above-mentioned processing, and the same thirteen green sheets 50′ were stacked on the lower side of the green sheet 50. The green sheet 50 on which the conductor containing paste layer having the electrostatic electrode pattern was printed was stacked thereon. Furthermore, two green sheets 50′ on which no tungsten paste was printed were stacked thereon. The resultant was pressed at 130� C. and a pressure of 80 kg/cm2 to form a lamination (FIG. 8(a)).
(4) Next, the resultant lamination was degreased at 600� C. in the atmosphere of nitrogen gas for 5 hours and hot-pressed at 1890� C. and a pressure of 150 kg/cm2 for 3 hours to obtain an aluminum nitride plate 3 mm in thickness. This was cut off into a disk of 230 mm in diameter to prepare a plate made of aluminum nitride and having therein resistance heating elements 5 having a thickness of 6 μm and a width of 10 mm, a chuck positive electrostatic layer 2 having a thickness of 10 μm, and a chuck negative electrostatic layer 3 having a thickness of 10 μm (FIG. 8(b)).
(5) Next, the plate obtained in the (4) was polished with a diamond grindstone. Subsequently a mask was put thereon, and bottomed holes (diameter: 1.2 mm, and depth: 2.0 mm) for thermocouples were made in the surface by blast treatment with SiC and the like.
(6) Furthermore, portions corresponding to where the plated through holes were made were hollowed out to make blind holes 35, 36 (FIG. 8(c)). Brazing gold made of Ni—Au was heated and allowed to reflow at 700� C. to connect external terminals 6, 18 made of Koval to the blind holes 35, 36 (FIG. 8(d)).
About the connection of the external terminals, a structure, wherein a support of tungsten supports at three points, is desirable. This is because the reliability of the connection can be kept.
The resultant ceramic substrate constituting the electrostatic chuck was cut in the manner that the cut section would contain the electrostatic electrode layer. The section was observed with a scanning electron microscope (SEM). The results are shown in FIG. 14. As is evident from FIG. 14, the section of the edge of the electrostatic electrode layer was in a peaked shape.
Green sheets were formed to be a lamination in the same manner as in Example 1 except that it was carried out without heating and at the temperature of 25� C. The observation thereof with the scanning electron microscope (500 magnifications) demonstrated that edges of sections of both the electrostatic electrodes and the resistance heating elements had a face perpendicular to the wafer-processing surface.
Production of a Wafer Prober 201 (see FIG. 12)
(1) The following paste was used to conduct formation by doctor blade method to obtain a green sheet 0.47 μm in thickness: a paste obtained by mixing 1000 parts by weight of aluminum nitride powder (made by Tokuyama Corp., average particle diameter: 1.1 μm), 40 parts by weight of yttria (average particle diameter: 0.4 μm) , and 530 parts by weight of mixed alcohol's of 1-butanol and ethanol.
(2) Next, this green sheet was dried at 80� C. for 5 hours, and subsequently through holes for plated through holes for connecting external terminals to resistance heating elements were made by punching.
Next, a printed unit for a guard electrode and a printed unit for a ground electrode in a lattice form were printed on the green sheet by screen sprinting using this conductor containing paste A.
Fifty green sheets on which the paste was printed and no paste was printed were stacked. The resultant was pressed at 130� C. and a pressure of 80 kg/cm2 to form a lamination.
(4) Next, this lamination was degreased at 600� C. in the atmosphere of nitrogen gas for 5 hours and hot-pressed at 1890� C. and a pressure of 150 kg/cm2 for 3 hours to obtain a aluminum nitride plate 3 mm in thickness. The resultant plate was cut off into a disk of 300 mm in diameter to prepare a ceramic plate. Regarding the size of plated through holes 17, their diameter was 0.2 mm and their depth was 0.2 mm.
The thickness of a guard electrode 65 and a ground electrode 66 was 10 μm. The position where the guard electrode 65 was formed were 1 mm apart from the wafer-putting surface. The position where the ground electrode 66 was formed was 1.2 mm apart from the wafer-putting surface. A section of the edge of the guard electrode 65 and the ground electrode 66 was in a peaked shape. The length of one side of each non-conductor forming area 66 a in the guard electrode 65 and the ground electrode 66 was 0.5 mm.
(5) Next, the plate obtained in the (4) was polished with a diamond grindstone. Subsequently a mask was out thereon, and concaves for thermocouples, and grooves 67 (width: 0.5 mm, and depth: 0. 5 mm) for adsorbing a wafer were made in the surface by blast treatment with SiC and the like.
(6) Furthermore, a layer for forming resistance heating elements 61 was printed on the surface opposite to the wafer-putting surface. A conductor containing paste was used for the printing. The used conductor containing paste was Solvest PS603D made of Tokuriki Kagaku Kenkyu-zyo, which is used to form plated through holes in printed circuit boards. This conductor containing paste was a silver/lead paste, and contained 7.5 parts by weight of metal oxides consisting of lead oxide, zinc oxide, silica, boron oxide and alumina (the weight ratio thereof was 5/55/10/25/5) per 100 parts by weight of silver.
(7) The ceramic substrate 63 on which the conductor containing paste was printed was heated and fired at 780� C. to sinter and bake silver and lead in the conductor containing paste on the ceramic substrate 63. The heater plate was immersed in a bath for electroless nickel plating consisting an aqueous solution containing 30 g/L of nickel sulfate, 30 g/L of boric acid, 30 g/L of ammonium chloride, and 60 g/L of a Rochelle salt, to precipitate a nickel layer (not illustrated) having a thickness of 1 μm and a boron content of 1% or less by weight on the surface of the resistance heating elements 61 made of the sintered silver. Thereafter, the heater plate was annealed at 120� C. for 3 hours.
(8) By sputtering, a titanium layer, a molybdenum layer and a nickel layer were successively formed on the surface in which the grooves 67 were made. The used equipment for the sputtering was SV-4540 made of ULVAC Japan, Ltd. About conditions for the sputtering, air pressure was 0.6 Pa, temperature was 100� C. and electric power was 200 W. Sputtering time was within the range of 30 seconds to 1 minute, and was adjusted dependently on the respective metals.
(9) The ceramic substrate 63 obtained in the above (8) was immersed in a bath for electroless nickel plating consisting an aqueous solution containing of 30 g/L of nickel sulfate, 30 g/L of boric acid, 30 g/L of ammonium chloride, and 60 g/L of a Rochelle salt to precipitate a nickel layer having a thickness of 7 μm and a boron content of 1% or less by weight on the surface of the metal layer made by the sputtering. Thereafter, the resultant ceramic substrate was annealed at 120� C. for 3 hours.
No electric current was not allowed to pass on the surface of the resistance heating elements, and the surface was not coated with any electroplating nickel.
The ceramic substrate was immersed in an electroless gold plating solution containing 2 g/L of potassium gold cyanide, 75 g/L of ammonium chloride, 50 g/L of sodium citrate, and 10 g/L of sodium hypophosphite at 93� C. for 1 minute to form a gold plating layer 1 μm in thickness on the nickel plating layer.
(10) Air suction holes 68 piercing the back surface from the grooves 67 were made by drilling, and then blind holes (not illustrated) for exposing plated through holes 16 were made. Brazing gold made of Ni—Au (Au: 81.5% by weight, Ni: 18.4% by weight, and impurities: 0.1% by weight) was heated and allowed to reflow at 970� C. to connect external terminals made of koval to the blind holes. External terminals made of koval were also attached through a solder (tin: 90% by weight, and lead: 10% by weight) on the resistance heating elements.
(11) Next, thermocouples for controlling temperature were buried in the concaves to obtain a wafer prober heater 201.
In the ceramic substrate, its pore diameter of the maximum pore was 2 μm, and its porosity was 1%. The temperature of the ceramic substrate was raised to 200� C. Even if 200 V was applied thereto, no dielectric breakdown was caused. Its warp amount was 1 μm or less, which was good.
Green sheets were formed to be a lamination in the same manner as in Example 2 except that it was carried out without heating and at the temperature of 25� C. The observation thereof with the scanning electron microscope (500 magnifications) demonstrated that edges of sections of both the guard electrode and the ground electrode had a face, perpendicular to the wafer-processing surface.
Alumina Hot Plate (see FIGS. 1 and 2)
(1) The following paste was used to conduct formation by doctor blade method to obtain green sheets 0.47 μm in thickness: a paste obtained by mixing alumina: 93 parts by weight, SiO2: 5 parts by weight, CaO: 0.5 part by weight, MgO: 0.5part by weight, TiO2: 0.5 part by weight, an acrylic binder: 11.5 parts by weight, 0.5 part by weight of a dispersant and 53 parts by weight of mixed alcohols of 1-butanol and ethanol.
(2) Next, these green sheets were dried at 80� C. for 5 hours, and subsequently the following holes were made in the green sheets for which they are necessary by punching: holes which would be through holes through which semiconductor wafer supporting pins having diameter of 1.8 mm, 3.0 mm and 5.0 mm were inserted; and holes which would be plated through holes for connecting external terminals.
(3) The following were mixed to prepare a conductor containing paste B: 100 parts by weight of tungsten particles having an average particle diameter of 3 μm, 1.9 parts by weight of an acrylic binder, 3.7 parts by weight of α-terpineol solvent, and 0.2 part by weight of a dispersant.
This conductor containing paste B was printed on the green sheet by screen printing to form a conductor containing paste layer. The pattern of the printing was made into a concentric pattern.
(4) Moreover, the conductor containing paste B was filled into the through holes for the plated through holes for connecting external terminals.
Furthermore, 34 to 60 sheets on which no tungsten paste was printed were stacked on the upper surface (heating surface) of the green sheet on which the pattern of the resistance heating elements was formed, and the same 13 to 30 green sheets were stacked on the lower side of the green sheet. This was pressed at 130� C. and a pressure of 80 kg/cm2 to form a lamination.
(5) Next, the resultant lamination was degreased at 600� C. in the atmosphere of air for 5 hours and hot-pressed at 1600� C. and a pressure of 150 kg/cm2 for 2 hours to obtain an aluminum nitride plate 3 mm in thickness. This was made to a substrate 280 mm in diameter and 19 mm in thickness by changing working conditions and polishing conditions.
A plate which was made of alumina and had therein resistance heating elements 5 having a thickness of 6 μm and a width of 10 mm was prepared. A section of the edge of the resistance heating elements 5 was in a peaked shape.
(6) Next, the plate obtained in the (3) was polished with a diamond grindstone. Subsequently a mask was put thereon, and bottomed holes (diameter: 1.2 mm, and depth: 2.0 mm) for thermocouples were made in the surface by blast treatment with SiC and the like.
(7) Furthermore, portions corresponding to where the plated through holes were made were hollowed out to make blind holes. Brazing gold made of Ni—Au was heated and allowed to reflow at 700� C. to connect external terminals made of koval to the blind holes.
(8) Next, thermocouples for controlling temperature were buried in the bottomed holes to finish the production of a hot plate having the resistance heating elements.
Green sheets were formed to be a lamination in the same manner as in Example 3 except that it was carried out without heating and at the temperature of 25� C. The observation thereof with the scanning electron microscope (500 magnifications) demonstrated that edges of sections of the resistance heating elements had a face perpendicular to the wafer-processing surface.
Hot Plate Made of Aluminum Nitride (see FIGS. 1 and 2)
(1) The following paste was used to conduct formation by doctor blade method to obtain a green sheet 0.47 μm in thickness: a paste obtained by mixing 100 parts by weight of aluminum nitride powder (made by Tokuyama Corp., average particle diameter: 1.1 μm), 4 parts by weight of yttria (average particle diameter: 0.4μm) , 11.5 parts by weight of an acrylic binder, 0.5 part by weight of a dispersant, 8 parts by weight of an acrylic resin binder (made by Kyoeisyha Chemical Co., Ltd., trade name: KC-600, and acid value: 17 KOHmg/g) and 53 parts by weight of mixed alcohols of 1-butanol and ethanol.
(2) Next, this green sheet was dried at 80� C. for 5 hours, and subsequently the following holes were made by punching: holes which would be through holes through which semiconductor wafer supporting pins with a diameter of 1.8 mm, 3.0 mm and 5.0 mm were inserted; and holes which would be plated through holes for connecting external terminals.
This conductor containing paste A was printed on the green sheet by screen printing to form a conductor containing paste layer. The pattern of the printing was made into a concentric pattern. Furthermore, conductor containing paste layers having an electrostatic electrode pattern shown in FIG. 10 were formed on other green sheets.
At 130� C. and a pressure of 80 kg/cm2, thirty seven green sheets on which no tungsten paste was printed were stacked on the upper side (heating surface) of the green sheet that had went through the above-mentioned processing, and simultaneously the same thirteen green sheets were stacked on the lower side of the green sheet.
(4) Next, the resultant lamination was degreased at 600� C. in the atmosphere of nitrogen gas for 1 hour and hot-pressed at 1890� C. and a pressure of 150 kg/cm2 for 3 hours to obtain an aluminum nitride plate 3 mm in thickness, which contained 810 ppm of carbon. This was cut into a disk of 230 mm in diameter to prepare a plate having therein resistance heating elements having a thickness of 6 μm and a width of 10 mm and electrostatic electrodes. A section of the edge of the electrostatic electrodes was in a peaked shape.
(6) Furthermore, portions corresponding to where the plated through holes were made were hollowed out to make concaves. Brazing gold made of Ni—Au was heated and allowed to reflow at 700� C. to connect external terminals made of koval to the concaves.
(7) Next, thermocouples for controlling temperature were buried in the bottomed holes to finish the production of a ceramic heater (hot plate).
Green sheets were formed to be a lamination in the same manner as in Example 4 except that it was carried out without heating and at the temperature of 25� C. The observation thereof with the scanning electron microscope (500 magnifications) demonstrated that edges of sections of the resistance heating elements had a face perpendicular to the wafer-processing surface.
(1) Heat Uniformity
A thermo viewer (IR-162012-0012, made by Japan Datum Company) was used to measure temperatures at respective points on the wafer-putting surface of the ceramic substrates to obtain a temperature difference between the highest temperature and the lowest temperature.
(2) Adsorption Power
The temperature of the ceramic substrates was raised to 450� C. to measure the adsorption power thereof with a load cell (Autograph AGS-50, made by Shimadzu Corp.).
The temperature of the ceramic substrates was raised to 200� C. and then the ceramic substrates were thrown into water, and it was examined whether cracks were generated or not. In Table 1, ◯ indicates that no crack was generated and the ceramic substrate had thermal shock resistance, and x indicates that cracks were generated and the ceramic substrate had no thermal shock resistance.
A voltage of 1 kV was applied between conductors that were supposed to be insulated in the ceramic substrates, and then a leakage current at 300� C. was measured using a breakdown voltage tester (TOS-5051, made by Kikusui Electronics Corp.) and an Ultrahigh Resistor (R8340, made by Advantest Corp.).
As is clear from Table 1, the ceramic substrates according to Examples 1 to 4 were superior in both heat uniformity and thermal shock resistance. As is also clear from Example 1 and Comparative example 1, the electrostatic chuck according to Example 1 had a large chuck power.
As described above, the ceramic substrate of the present invention is superior in heat uniformity and thermal shock resistance. In the case that the ceramic substrate is used as an electrostatic chuck, its chuck power is large.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3067310 *Dec 2, 1959Dec 4, 1962William D OliverMicrofilm electric heatersUS4034207 *Apr 30, 1976Jul 5, 1977Murata Manufacturing Co., Ltd.Positive temperature coefficient semiconductor heating elementUS4443691 *Sep 30, 1982Apr 17, 1984Saint-Gobain VitrageElectrically heated windowUS5068517 *Aug 22, 1989Nov 26, 1991Toshiba Lighting & Technology CorporationPrinted strip heaterUS5072236 *Apr 24, 1990Dec 10, 1991Rohm Co., Ltd.Thick film type thermal headUS6080970 *Dec 22, 1998Jun 27, 2000Kyocera CorporationWafer heating apparatusUS6133557 *Jan 30, 1996Oct 17, 2000Kyocera CorporationWafer holding memberJP20012194A Title not availableJPH0652974A Title not availableJPH08273814A Title not availableJPH09180867A Title not availableJPS62167396A Title not available* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS6643115 *Feb 27, 2002Nov 4, 2003Kyocera CorporationElectrostatic chuckUS6677557 *May 1, 2001Jan 13, 2004Ibiden Co., Ltd.Ceramic heaterUS6689984 *Oct 31, 2002Feb 10, 2004Sumitomo Osaka Cement Co., Ltd.Susceptor with built-in electrode and manufacturing method thereforUS6710307Apr 10, 2002Mar 23, 2004Ibiden Co., Ltd.Ceramic heaterUS6730892 *May 6, 2003May 4, 2004Mitsubishi Pencil Co., Ltd.Resistive heating element and production methodUS6731496May 9, 2001May 4, 2004Ibiden Co., Ltd.Electrostatic chuckUS6753601Apr 18, 2001Jun 22, 2004Ibiden Co., Ltd.Ceramic substrate for semiconductor fabricating deviceUS6809299Jul 4, 2001Oct 26, 2004Ibiden Co., Ltd.Hot plate for semiconductor manufacture and testingUS6815646Jul 25, 2001Nov 9, 2004Ibiden Co., Ltd.Ceramic substrate for semiconductor manufacture/inspection apparatus, ceramic heater, electrostatic clampless holder, and substrate for wafer proberUS6825555Jun 15, 2001Nov 30, 2004Ibiden Co., Ltd.Hot plateUS6835916Aug 23, 2002Dec 28, 2004Ibiden, Co., LtdCeramic heaterUS6849938Aug 24, 2001Feb 1, 2005Ibiden Co., Ltd.Ceramic substrate for semiconductor production and inspectionUS6861165Feb 26, 2001Mar 1, 2005Ibiden Co., Ltd.Aluminum nitride sintered compact, ceramic substrate, ceramic heater and electrostatic chuckUS6861620Sep 10, 2003Mar 1, 2005Ibiden Co., Ltd.Ceramic heaterUS6878906Aug 30, 2001Apr 12, 2005Ibiden Co., Ltd.Ceramic heater for semiconductor manufacturing and inspecting equipmentUS6878907 *Oct 23, 2002Apr 12, 2005Ibiden Co., Ltd.Ceramic substrate and process for producing the sameUS6884972Apr 23, 2001Apr 26, 2005Ibiden Co., Ltd.Ceramic plate for a semiconductor producing/inspecting apparatusUS6888106Apr 9, 2001May 3, 2005Ibiden Co., Ltd.Ceramic heaterUS6888236Mar 7, 2001May 3, 2005Ibiden Co., Ltd.Ceramic substrate for manufacture/inspection of semiconductorUS6891263Feb 7, 2001May 10, 2005Ibiden Co., Ltd.Ceramic substrate for a semiconductor production/inspection deviceUS6897414Jul 3, 2001May 24, 2005Ibiden Co., Ltd.Ceramic heater for semiconductor manufacturing/testing apparatusUS6921881 *Aug 12, 2002Jul 26, 2005Ibiden Co., Ltd.Ceramic joint bodyUS6924464Nov 26, 2001Aug 2, 2005Ibiden Co., Ltd.Ceramic heater and manufacturing method of ceramic heaterUS6929874May 22, 2003Aug 16, 2005Ibiden Co., Ltd.Aluminum nitride sintered body, ceramic substrate, ceramic heater and electrostatic chuckUS6936343May 15, 2000Aug 30, 2005Ibiden Co., Ltd.Ceramic substrateUS6956186Aug 1, 2000Oct 18, 2005Ibiden Co., Ltd.Ceramic heaterUS6960743Dec 5, 2001Nov 1, 2005Ibiden Co., Ltd.Ceramic substrate for semiconductor manufacturing, and method of manufacturing the ceramic substrateUS6964812Dec 11, 2003Nov 15, 2005Ibiden Co., Ltd.Carbon-containing aluminum nitride sintered compact and ceramic substrate for use in equipment for manufacturing or inspecting semiconductorUS6967312Jul 19, 2001Nov 22, 2005Ibiden Co., Ltd.Semiconductor manufacturing/testing ceramic heater, production method for the ceramic heater and production system for the ceramic heaterUS6967313Apr 27, 2000Nov 22, 2005Ibiden Company, Ltd.Hot plate and method of producing the sameUS7011874Feb 8, 2001Mar 14, 2006Ibiden Co., Ltd.Ceramic substrate for semiconductor production and inspection devicesUS7015166Jun 28, 2004Mar 21, 2006Ibiden Co., Ltd.Carbon-containing aluminum nitride sintered compact and ceramic substrate for use in equipment for manufacturing or inspecting semiconductorUS7071551May 28, 2001Jul 4, 2006Ibiden Co., Ltd.Device used to produce or examine semiconductorsUS7084376Jan 17, 2003Aug 1, 2006Ibiden Co., Ltd.Semiconductor production device ceramic plateUS7126093 *Feb 23, 2005Oct 24, 2006Ngk Insulators, Ltd.Heating systemsUS7173219 *Nov 29, 2004Feb 6, 2007Ngk Insulators, Ltd.Ceramic heatersUS7282669 *Jul 30, 2002Oct 16, 2007Ngk Spark Plug Cc., Ltd.Ceramic heater and method for manufacturing the sameUS7364624Jan 16, 2004Apr 29, 2008Momentive Performance Materials Inc.Wafer handling apparatus and method of manufacturing thereofUS7982166Dec 22, 2004Jul 19, 2011Kyocera CorporationCeramic heater and method for manufacturing the sameUS8106331Oct 3, 2007Jan 31, 2012International Business Machines CorporationApparatus for controlling alignment between precision ground plates and method of controlling a desired alignment between opposing precision ground platesUS8136820 *Aug 20, 2007Mar 20, 2012Ngk Insulators, Ltd.Electrostatic chuck with heater and manufacturing method thereofUS8663391 *Jul 23, 2012Mar 4, 2014Applied Materials, Inc.Electrostatic chuck having a plurality of heater coilsUS9100992Mar 15, 2013Aug 4, 2015Minco Products, Inc.Heater assemblyUS20020150789 *Mar 13, 2001Oct 17, 2002Yasuji HiramatsuCeramic sunstrateUS20020179592 *Jul 19, 2001Dec 5, 2002Yasuji HiramatsuSemiconductor manufacturing/testing ceramic heater, production method for the ceramic heater and production system for the ceramic heaterUS20020180466 *May 28, 2001Dec 5, 2002Yasuji HiramatsuSemiconductor manufacturing and inspecting deviceUS20020190054 *Jul 3, 2001Dec 19, 2002Yasutaka ItoCeramic heater for semiconductor manufacturing /testing apparatusUS20030015515 *Jul 25, 2001Jan 23, 2003Yasutaka ItoCeramic substrate for semiconductor manufacture/inspection apparatus, ceramic heater, electrostatic clampless holder, and substrate for wafer proberUS20030029856 *Jul 30, 2002Feb 13, 2003Ngk Spark Plug Co., Ltd.Ceramic heater and method for manufacturing the sameUS20030038129 *Jul 4, 2001Feb 27, 2003Yasuji HiramatsuHot plate for semiconductor manufacture and testingUS20030039796 *Feb 8, 2001Feb 27, 2003Yasutaka ItoCeramic substrate for semiconductor production and inspection devicesUS20030044653 *Feb 26, 2001Mar 6, 2003Yasuji HiramatsuAluminum nitride sintered compact, ceramic substrate, ceramic heater and electrostatic chuckUS20030080110 *Jun 15, 2001May 1, 2003Yasuji HiramatsuHot plateUS20030089699 *May 1, 2001May 15, 2003Yasuji HiramatsuHot plate unitUS20030132217 *Jan 17, 2003Jul 17, 2003Ibiden Co., Ltd.Semiconductor production device ceramic plateUS20030132218 *Jan 28, 2003Jul 17, 2003Ibiden Co., Ltd.Ceramic heater and supporting pinUS20030160041 *Apr 9, 2001Aug 28, 2003Yasuji HiramatsuCeramic heaterUS20030203225 *May 22, 2003Oct 30, 2003Ibiden Co., Ltd.Aluminum nitride sintered body, ceramic substrate, ceramic heater and electrostatic chuckUS20040007773 *Jul 10, 2003Jan 15, 2004Ibiden Co., Ltd.Ceramic substrate for semiconductor fabricating deviceUS20040011781 *Jul 15, 2003Jan 22, 2004Ibiden Co., Ltd.Ceramic heaterUS20040016746 *Jul 15, 2003Jan 29, 2004Ibiden Co., Ltd.Ceramic heaterUS20040021475 *Jun 6, 2001Feb 5, 2004Atsushi ItoWafer proberUS20040035846 *Aug 30, 2001Feb 26, 2004Yasuji HiramatsuCeramic heater for semiconductor manufacturing and inspecting equipmentUS20040045951 *Sep 10, 2003Mar 11, 2004Ibiden Co., Ltd.Ceramic heaterUS20040060919 *Sep 17, 2003Apr 1, 2004Ibiden Co., Ltd.Semiconductor production device ceramic plateUS20040065881 *Aug 24, 2001Apr 8, 2004Yasutaka ItoCeramic substrate for semiconductor production and inspectionUS20040071945 *Aug 12, 2002Apr 15, 2004Yasutaka ItoCeramic joint bodyUS20040084762 *Jul 16, 2003May 6, 2004Ibiden Co., Ltd.Ceramic substrateUS20040097359 *Nov 22, 2001May 20, 2004Yasuji HiramatsuAluminum nitride sintered body, method for producing aluminum nitride sintered body, ceramic substrate and method for producing ceramic substrateUS20040099708 *Nov 24, 2003May 27, 2004Ibiden, Co., Ltd.Semiconductor-producing/examining deviceUS20040117977 *Dec 5, 2001Jun 24, 2004Yasuji HiramatsuCeramic substrate for semiconductor manufacturing and inspecting devices, and method of manufacturing the ceramic substrateUS20040134899 *Dec 29, 2003Jul 15, 2004Ibiden, Co., Ltd.Ceramic substrate for a semiconductor-production/inspection deviceUS20040140040 *Jan 13, 2004Jul 22, 2004Ibiden Co., Ltd.Ceramic substrate and process for producing the sameUS20040142153 *Sep 26, 2003Jul 22, 2004Ibiden Co., Ltd.Ceramic substrate and sintered aluminum nitrideUS20040149718 *Apr 3, 2001Aug 5, 2004Yasutaka ItoCeramic heaterUS20040149723 *Jul 23, 2003Aug 5, 2004Ibiden Co., Ltd.Hot plate and method of producing the sameUS20040152582 *Dec 11, 2003Aug 5, 2004Ibiden Co., Ltd.Carbon-containing aluminum nitride sintered compact and ceramic substrate for use in equipment for manufacturing or inspecting semiconductorUS20040155025 *Jan 29, 2004Aug 12, 2004Ibiden Co., Ltd.Ceramic heaterUS20040169033 *Feb 23, 2004Sep 2, 2004Sumitomo Electric Industries, Ltd.Holder for use in semiconductor or liquid-crystal manufacturing device and semiconductor or liquid-crystal manufacturing device in which the holder is installedUS20040173161 *Jan 16, 2004Sep 9, 2004General Electric CompanyWafer handling apparatus and method of manufacturing thereofUS20040206747 *Apr 11, 2002Oct 21, 2004Yasutaka ItoCeramic heater for semiconductor manufacturing/inspecting apparatusUS20040211767 *Dec 14, 2000Oct 28, 2004Yasuji HiramatsuCeramic heater and support pinUS20040217105 *May 28, 2004Nov 4, 2004Ibiden Co., Ltd.Semiconductor production device ceramic plateUS20040222211 *Jun 2, 2004Nov 11, 2004Ibiden Co., Ltd.Carbon-containing aluminum nitride sintered body, and ceramic substrate for a semiconductor producing/examining deviceUS20040242400 *Jun 28, 2004Dec 2, 2004Ibiden Co., Ltd.Carbon-containing aluminum nitride sintered compact and ceramic substrate for use in equipment for manufacturing or inspecting semiconductorUS20050011878 *Aug 16, 2004Jan 20, 2005Ibiden Co., Ltd.Ceramic substrate for semiconductor manufacture/inspection apparatus, ceramic heater, electrostatic clampless holder, and substrate for wafer proberUS20050014031 *Aug 20, 2004Jan 20, 2005Ibiden Co., Ltd.Aluminum nitride sintered body, ceramic substrate, ceramic heater and electrostatic chuckUS20050016465 *Jul 23, 2003Jan 27, 2005Applied Materials, Inc.Electrostatic chuck having electrode with rounded edgeUS20050016987 *Aug 19, 2004Jan 27, 2005Ibiden, Co., Ltd.Ceramic heaterUS20050023269 *Aug 12, 2004Feb 3, 2005Ibiden Co., Ltd.Hot plate for semiconductor producing/examining deviceUS20050023270 *Aug 30, 2004Feb 3, 2005Ibiden Co., Ltd.Ceramic substrate and process for producing the sameUS20050029244 *Sep 20, 2004Feb 10, 2005Ibiden Co., Ltd.Ceramic substrate, ceramic heater, electrostatic chuck and wafer prober for use in semiconductor producing and inspecting devicesUS20050045618 *Jul 8, 2002Mar 3, 2005Ibiden Co., Ltd.Ceramic heater and ceramic joined articleUS20050153826 *Jan 6, 2005Jul 14, 2005Ibiden Co., Ltd.Carbon-containing aluminum nitride sintered body, and ceramic substrate for a semiconductor producing/examining deviceUS20050173410 *Nov 29, 2004Aug 11, 2005Ngk Insulators, Ltd.Ceramic heatersUS20050241584 *Mar 20, 2003Nov 3, 2005Sumitomo Electric Industries, Ltd.Ceramics heater for semiconductor production systemUS20050258164 *Jul 29, 2004Nov 24, 2005Ibiden Co., Ltd.Hot plateUS20060088692 *Oct 22, 2004Apr 27, 2006Ibiden Co., Ltd.Ceramic plate for a semiconductor producing/examining deviceUS20060186109 *Feb 23, 2005Aug 24, 2006Ngk Insulators, Ltd.Heating systemsUS20080032115 *Sep 30, 2005Feb 7, 2008Nihon Ceratec Co., Ltd.Corrosion-Resistant Member and Method for Manufacture ThereofUS20080049374 *Aug 20, 2007Feb 28, 2008Ngk Insulators, Ltd.Electrostatic chuck with heater and manufacturing method thereofUS20080210684 *Dec 22, 2004Sep 4, 2008Hiroshi KukinoCeramic Heater and Method for Manufacturing the SameUS20090059461 *Jul 11, 2008Mar 5, 2009Shinko Electric Industries Co., Ltd.Electrostatic chuckUS20090088041 *Sep 22, 2008Apr 2, 2009Canon Anelva CorporationDisplay substrate manufacturing method and vacuum processing apparatusUS20090090229 *Oct 3, 2007Apr 9, 2009International Business Machines CorporationMethod and apparatus for controlling size and alignment of precision ground platesUS20110233190 *Sep 29, 2011Kyocera CorporationCeramic Heater and Method for Manufacturing the SameUS20120285619 *Nov 15, 2012Alexander MatyushkinElectrostatic chuck having a plurality of heater coilsUS20130037532 *Feb 14, 2013Applied Materials, Inc.Substrate support with heaterUS20140091077 *Sep 27, 2013Apr 3, 2014Semes Co., Ltd.Supporting unit, substrate treating device including the same, and method of manufacturing the supporting unit* Cited by examinerClassifications U.S. Classification219/444.1International ClassificationH01L21/00, H05B3/18, H05B3/74, H05B3/12, H01L21/66, B23Q3/15, H05B3/14, H05B3/20, H05B3/26, H01L21/683Cooperative ClassificationH01L21/67103, H01L21/6831, H05B3/74, H05B3/265, H01L21/6833, H05B3/143European ClassificationH01L21/67S2H2, H05B3/14C2, H05B3/74, H05B3/26C, H01L21/683C2, H01L21/683CLegal EventsDateCodeEventDescriptionNov 13, 2001ASAssignmentOwner name: IBIDEN CO., LTD., JAPANFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HIRAMATSU, YASUJI;ITO, YASUTAKA;REEL/FRAME:012303/0839Effective date: 20010730Jun 16, 2006FPAYFee paymentYear of fee payment: 4Jun 16, 2010FPAYFee paymentYear of fee payment: 8Jun 18, 2014FPAYFee paymentYear of fee payment: 12RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services