Patent US6479368 - Method of manufacturing a semiconductor device having a shallow trench ... - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsA method of manufacturing a semiconductor device, in which the depth of a divot in a shallow trench isolation can be decreased. The method comprises forming a trench in a semiconductor substrate, for isolating elements, forming a nitride film on a surface of the trench, depositing mask material on an...http://www.google.com/patents/US6479368?utm_source=gb-gplus-sharePatent US6479368 - Method of manufacturing a semiconductor device having a shallow trench isolating regionAdvanced Patent SearchPublication numberUS6479368 B1Publication typeGrantApplication numberUS 09/033,067Publication dateNov 12, 2002Filing dateMar 2, 1998Priority dateMar 2, 1998Fee statusPaidPublication number033067, 09033067, US 6479368 B1, US 6479368B1, US-B1-6479368, US6479368 B1, US6479368B1InventorsJack A. Mandelman, Mutsuo Morikado, Herbert Ho, Jeffrey P. GambinoOriginal AssigneeKabushiki Kaisha Toshiba, International Business Machines Corp.Export CitationBiBTeX, EndNote, RefManPatent Citations (19), Non-Patent Citations (1), Referenced by (14), Classifications (10), Legal Events (4) External Links: USPTO, USPTO Assignment, EspacenetMethod of manufacturing a semiconductor device having a shallow trench isolating region
US 6479368 B1Abstract
A method of manufacturing a semiconductor device, in which the depth of a divot in a shallow trench isolation can be decreased. The method comprises forming a trench in a semiconductor substrate, for isolating elements, forming a nitride film on a surface of the trench, depositing mask material on an entire surface of the semiconductor substrate, filling the trench with the mask material, etching the mask material until a surface level of the mask material in the trench falls below the surface of the semiconductor substrate, removing an exposed upper portion of the nitride film on the surface of the trench, removing the mask material from the trench, filling the trench with element-isolating material, thereby forming an element-isolating region, and forming a transistor in an element region isolated from another element region by the element-isolating region.
What is claimed is: 1. A method of manufacturing a semiconductor device having a shallow trench isolating region comprising the steps of:
forming a pad nitride layer on a semiconductor substrate; selectively etching the pad nitride layer and the semiconductor substrate to form a trench in the semiconductor substrate; forming a nitride film on a surface of the trench; depositing mask material on an entire surface of the semiconductor substrate so as to fill the trench with the mask material; etching the mask material until an upper surface level of the mask material in the trench falls below the surface of the semiconductor substrate while removing the nitride film on the inner surface of the trench above the upper surface level of the mask material at the same time, a portion of the trench below the upper surface level of the mask material in the trench being entirely filled with said mask material, and a portion of the nitride film formed on the inner surface of the trench below the upper surface level of the mask material in the trench being entirely covered with said mask material and remaining on the surface of the trench; etching off the entire mask material from the trench while the portion of the nitride film formed on the inner surface of the trench below the upper surface level of the mask material in the trench remains on the surface of the trench; filling the trench with an insulating material, thereby forming an element isolating region; etching off the pad nitride layer on the semiconductor substrate; and forming a transistor in an element region isolated from another element region by the element isolating region. 2. A method according to claim 1, wherein the mask material is a resist.
3. A method according to claim 1, wherein the step of etching the mask material until an upper surface level of the mask material in the trench falls below the surface of the semiconductor substrate comprises etching the mask material until the surface level of the mask material in the trench falls 415 to 1585 angstroms below the surface of the semiconductor substrate.
4. A method according to claim 1, wherein the mask material and the nitride film on the upper part of the surface of the trench are etched in an atmosphere of a CF4—O2 mixture using a chemical dry etching process.
5. A method according to claim 1, wherein the insulating material is TEOS oxide.
6. A method according to claim 1, wherein the nitride film has a thickness of 5nm or less.
7. A method according to claim 1, wherein the step of removing the pad nitride layer is performed after the step of filling the trench with the insulating material.
8. A method of manufacturing a semiconductor device having a shallow trench isolating region comprising the steps of:
forming a pad nitride layer on a semiconductor substrate; selectively etching the pad nitride layer and the semiconductor substrate to form an element isolation trench in the semiconductor substrate; forming a nitride film on a surface of the trench; depositing mask material on an entire surface of the semiconductor substrate so as to fill the trench with the mask material; etching the mask material to a depth below the surface of the semiconductor substrate while removing the nitride film on the inner surface of the trench above the upper surface level of the mask material at the same time, a portion of the trench below the upper surface level of the mask material in the trench being entirely filled with said mask material, and a portion of the nitride film formed on the inner surface of the trench below the upper surface level of the mask material in the trench being entirely covered with said mask material and remaining on the surface of the trench; etching off the entire mask material from the trench while a second portion of the nitride film remains on the surface of the trench; filling the trench with an insulating material, thereby forming an element isolating region; etching off the pad nitride layer on the semiconductor substrate; and forming a transistor in an element region isolated from another element region by the element isolating region. 9. The method of claim 8, wherein the step of etching the mask material to a depth below the surface of the semiconductor substrate comprises etching the mask material until the surface level of the mask material in the trench falls 415 to 1585 angstroms below the surface of the semiconductor substrate.
10. The method of claim 8, wherein the step of removing the pad nitride layer is performed after the step of filling the trench with an insulating material.
11. The method of claim 10, wherein the step of etching the mask material to a depth below the surface of the semiconductor substrate comprises etching the mask material until the surface level of the mask material in the trench falls 415 to 1585 angstroms below the surface of the semiconductor substrate.
The present invention relates to a method of manufacturing a semiconductor device, and more particularly to a method of manufacturing a semiconductor device, in which the depth of a divot in the shallow trench isolation can be controlled.
In a typical process of forming a shallow trench isolation (hereinafter referred to as “STI”), a nitride liner is formed on the thermally oxidized film on the surface of a shallow trench. The nitride liner is so formed to prevent oxidization of the silicon sidewall of the collar region of a deep storage trench. TEOS oxide is then deposited in the shallow trench by means of LPCVD. As a result, a STI is formed which isolates adjacent elements from one another.
As may be seen from FIG. 1, a nitride liner 1 is formed in a shallow trench in order to prevent oxidation of the silicon sidewall of the collar oxide region 4 of a deep storage trench 2. As shown in FIG. 1, the deep storage trench 2 is covered with an STI 3. Where the silicon sidewall of the collar oxide region 4 oxidized, a bird's beak of SiO2 would grow to generate a stress and cause dislocation of silicon. The nitride liner laid on the bottom of the STI 3 acts as a barrier, which prevents oxygen from diffusing into the trench collar 4. Thus, the nitride liner greatly reduces the defects in silicon.
However, the STI nitride liner makes it easy for etchant to attack the near-top part of the trench and the near-corner part of the active layer in the wet etching which is performed later to remove the pad nitride film on the element regions. The nitride liner on the upper part of the STI is inevitably etched while the pad nitride film is being etched with hot phosphoric acid. A removing of the pad nitride film is typically accompanied by over-etching for 5 to 10 minutes.
The nitride liner on the upper part of the STI is etched by this over-etching, whereby a small recess known as “divot” is formed in the top edge of the STI. The divot exposes the oxide thermally grown on the sidewall of the shallow trench and the surface of the LPTEOS layer. The etchant invades the recess, etching the oxide during the etching of the pad oxide and gate-sacrificing oxide. Inevitably, the etchant deepens the divot toward the corners of the active region and expands the divot in the horizontal direction.
It is difficult to control this isotropic etching of the near-corner part of the active region. The off current therefore changes greatly, making it impossible to lengthen the charge-holding time. FIG. 2 is a schematic representation of the divot formed in the top of the STI. Numeral 10 in FIG. 2 indicates the divot expanded.
The off current depends upon the conductivity of the corner parts of the active region, due to the reduced width of the semiconductor device and also to the electric field concentrated at the corner parts of the active region. The off current is much influenced by the geometrical shapes of the corner parts and the area over which the corner parts overlap the gate conductor (i.e., word line). The overlapping area is determined by the depth of the divot formed on the STI upon completion of the etching of the pad oxide and gate-sacrificing oxide.
Experiments and model simulation have indicated that the threshold voltage (Vt) of a field-effect transistor decreases about 1 mV each time the depth of the divot increases one angstrom. FIG. 3 shows the results of the model simulation, and FIG. 4 shows the values actually measured.
Generally, the divot is observed to be 300 angstroms deep. The threshold voltage Vt which corresponds to the depth of 300 angstroms causes, as seen from FIG. 5, a change of more than three orders in the off current and increased incidence of retention time fails.
An object of the present invention is to provide a method of manufacturing a semiconductor device, in which the depth of a divot in a shallow trench isolation can be decreased.
Another object of the invention is to provide a semiconductor device which is manufactured by such a method.
According to the present invention, there is provided a method of manufacturing a semiconductor device comprising the steps of: forming a trench in a semiconductor substrate, for isolating elements; forming a nitride film on a surface of the trench; depositing mask material on an entire surface of the semiconductor substrate to fill the trench with the mask material; etching the mask material until a surface level of the mask material in the trench falls below the surface of the semiconductor substrate; removing an exposed upper portion of the nitride film formed on the surface of the trench; removing the mask material from the trench; filling the trench with element-isolating material, thereby forming an element-isolating region; and forming a transistor in an element region isolated from another element region by the element-isolating region.
According to the present invention, there is provided a semiconductor conductor device which comprises: a semiconductor substrate; an element-isolating region formed by filling element-isolating material in a trench formed in the semiconductor substrate; and a transistor formed in an element region isolated from another element region by the element-isolating region, wherein a nitride film is provided on an entire surface of the trench except an upper part of the surface.
FIG. 1 is a sectional view of a semiconductor device in which the nitride liner on the bottom of the shallow trench isolation serves as a barrier which prevents diffusion of oxygen into the silicon layer provided on the side wall of the deep trench collar;
FIG. 2 is a schematic representation of the divot formed in the top of the shallow trench isolation of the device shown in FIG. 1;
FIG. 3 is a graph representing the relationship between the depth of the divot and the threshold voltage, which has been obtained by model simulation;
FIG. 4 is a graph illustrating the relationship between the depth of the divot and the threshold voltage, which has been obtained by actual measuring;
FIG. 5 is a graph depicting the relationship between the depth of the divot and the relative off current;
FIGS. 6A to 6F are sectional views for explaining a method of manufacturing a semiconductor device according to an embodiment of the invention;
FIG. 7 is a plan view of the semiconductor device which has been manufactured by the method explained with reference to FIGS. 6A to 6F;
FIG. 9 is a sectional view taken along line 9—9 in FIG. 7; and
FIG. 10 is a schematic representation of a divot which is shallow in the top of the shallow trench isolation of the semiconductor device.
FIGS. 6A to 6F are sectional views for explaining the method of manufacturing a semiconductor device according to one embodiment of the present invention.
As shown in FIG. 6A, a pad oxide film 12 having a thickness of 80 angstroms is formed on a single-crystal silicon substrate 11. Further, a pad nitride film 13 having a thickness of 1,500 angstroms is formed on the pad oxide film 12. Next, the pad nitride film 13, pad oxide film 12 and single-crystal silicon substrate 11 are selectively etched by known anisotropic etching. A shallow trench 14 is thereby formed, which is 2,500 angstroms deep from the surface of the substrate 11 as illustrated in FIG. 6B.
As shown in FIG. 6C, an oxide film 15 having a thickness of 100 angstroms is formed on the surface of the shallow trench 14 by performing thermal oxidation in an atmosphere containing H2O and O2. Further, CVD is carried out by using a feed gas which is a mixture of SiH4 and NH3. As a result, a silicon nitride liner 16 having a thickness of 80 angstroms is formed on the entire surface of the structure, including the surface of the shallow trench 14.
Thereafter, a resist 17 is coated to a thickness of 10,000 angstroms, filling the shallow trench 14 as shown in FIG. 6D. The resist 17 is, for example, AZ7500 (trade name).
As shown in FIG. 6E, CDE (Chemical Dry Etching) is conducted on the structure in an atmosphere of CF4—O2 mixture (flow ratio: 50SCCM/300SCCM). The resist 17 is thereby etched to a depth of 1,000 angstroms from the surface of the silicon substrate 11. The tolerance of the thickness of the pad nitride film 13 may be controlled to �10%, and that of the resist 17 a remaining on the surface of the shallow trench 14 may be controlled to �10% or less. If so, the resist 17 a on the surface of the trench 14 will have such a thickness that its surface is at a distance of 415 to 1,585 angstroms from the surface of the silicon substrate 11. In other words, a part of the resist 17, which has such a thickness, is removed, whereby a part 16 a of the silicon nitride liner 16 is exposed.
If the nitride liner 16 is relatively thin (5 nm or less), the CDE for removing the resist may remove the exposed part 16 a of the nitride liner 16, too. If the nitride liner 16 is thicker (exceeding 5 nm), the part 16 a of the nitride liner would not be removed simultaneously with the resist 17. In this case, the exposed part 16 a of the nitride liner 16 is removed as shown in FIG. 6F, by performing additional CDE on the exposed part 16 a of the nitride liner 16, which dose etch the resist 17.
That part 16 a of the nitride liner 16 which is removed should be large enough to provide a barrier to prevent diffusion of oxygen when a deep trench collar is formed and to decrease the depth of the divot. In view of this it is desired that the lower edge of the part 16 a be at a distance of 415 to 1585 angstroms from the surface of the silicon substrate 11.
After the silicon nitride liner 16 a has been removed from the upper part of the surface of the shallow trench 14, the resist 17 a is removed from the shallow trench 14 in its entirety. Thereafter, an ordinary process of manufacturing a semiconductor device is performed.
That is, as shown in FIGS. 7 to 8, the shallow trench 14 is filled with TEOS oxide or the like, forming a STI 31. The STI 31 electrically isolates the element regions from each other. Parts of the pad nitride film 13 and the pad oxide film 12 are removed from the element regions thus isolated. A gate oxide film 32 is then formed, and a gate electrode 33 is formed on the gate oxide film 32. Further, ion implantation is carried out, forming a source region 34 a and a drain region 34 b. A MOSFET is thereby manufactured. No silicon nitride liner is exposed when the pad nitride film 13 is removed, and no divot would be formed at the time the silicon nitride liner is removed.
FIG. 7 is a plan view of the MOSFET thus manufactured. FIG. 8 is a sectional view taken along line 8—8 in FIG. 7, and FIG. 9 is a sectional view taken along line 9—9 in FIG. 7.
FIG. 10 is a schematic representation of the divot 20 which is small in the top of the STI of the MOSFET. The divot 20 is much smaller than the divot formed in the conventional device shown in FIG. 2.
As has been described, in the method according to the invention, the nitride liner on the upper part of the sidewall of the STI is removed prior to the ordinary process of manufacturing a semiconductor device. Therefore, no nitride liner is exposed when the pad nitride film is removed, and no divot would be formed when the pad nitride film is removed. The threshold voltage of the MOSFET does not greatly change. Nor does the off current change greatly. Nor will there occur increased incidence of retention time fails.
As described above, the nitride liner on the upper part of the STI is removed before oxidation is effected to form a gate-sacrificing oxide film and a gate oxide film. These oxide films therefore grow so thick that the parasitic current in their corner can be decreased.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS4348905 *Jul 8, 1980Sep 14, 1982Nissan Motor Company, LimitedVibration sensor for an automotive vehicleUS4533430Jan 4, 1984Aug 6, 1985Advanced Micro Devices, Inc.Process for forming slots having near vertical sidewalls at their upper extremitiesUS4534826 *Dec 29, 1983Aug 13, 1985Ibm CorporationTrench etch process for dielectric isolationUS4549927 *Jun 29, 1984Oct 29, 1985International Business Machines CorporationMethod of selectively exposing the sidewalls of a trench and its use to the forming of a metal silicide substrate contact for dielectric filled deep trench isolated devicesUS4671970Feb 5, 1986Jun 9, 1987Ncr CorporationTrench filling and planarization processUS4839306 *Mar 23, 1988Jun 13, 1989Oki Electric Industry Co., Ltd.Method of manufacturing a trench filled with an insulating material in a semiconductor substrateUS4849369Aug 20, 1987Jul 18, 1989Commissariat A L'energie AtomiqueMethod of making an EPROM memory cellUS4892614 *Mar 10, 1989Jan 9, 1990Texas Instruments IncorporatedIntegrated circuit isolation processUS4945069Dec 16, 1988Jul 31, 1990Texas Instruments, IncorporatedOrganic space holder for trench processingUS4994409Jul 18, 1989Feb 19, 1991Hyundai Electronics Industries Co. Ltd.Method for manufacturing a trench capacitor using a photoresist etch back processUS5017506Jul 25, 1989May 21, 1991Texas Instruments IncorporatedMethod for fabricating a trench DRAMUS5387539Jun 18, 1993Feb 7, 1995Hyundai Electronics Industries Co., Ltd.Method of manufacturing trench isolationUS5472904 *Aug 8, 1994Dec 5, 1995Micron Technology, Inc.Thermal trench isolationUS5498564Mar 24, 1995Mar 12, 1996International Business Machines CorporationStructure and method for reducing parasitic leakage in a memory array with merged isolation and node trench constructionUS5529952Sep 20, 1994Jun 25, 1996Texas Instruments IncorporatedMethod of fabricating lateral resonant tunneling structureUS5593912Oct 6, 1994Jan 14, 1997International Business Machines CorporationSOI trench DRAM cell for 256 MB DRAM and beyondUS5643823 *Sep 21, 1995Jul 1, 1997Siemens AktiengesellschaftApplication of thin crystalline Si3 N4 liners in shallow trench isolation (STI) structuresUS5786276 *Mar 31, 1997Jul 28, 1998Applied Materials, Inc.Selective plasma etching of silicon nitride in presence of silicon or silicon oxides using mixture of CH3F or CH2F2 and CF4 and O2US5940717 *Oct 30, 1998Aug 17, 1999Siemens AktiengesellschaftRecessed shallow trench isolation structure nitride liner and method for making same* Cited by examinerNon-Patent CitationsReference1 *S. Wolf et al. "Silicon Processing for the VLSI Era", vol. 1-Process Technology, p. 428.* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS6596607 *Sep 14, 2001Jul 22, 2003Samsung Electronics Co., Ltd.Method of forming a trench type isolation layerUS6709952 *Jun 2, 2003Mar 23, 2004Mosel Vitelic, Inc.Method of forming a bottom oxide layer in a trenchUS6737706 *Apr 2, 2002May 18, 2004Samsung Electronics Co. Ltd.Silicon on insulator device having trench isolation layer and method for manufacturing the sameUS6995447Mar 26, 2004Feb 7, 2006Samsung Electronics, Co., Ltd.Silicon on insulator device having trench isolation layer and method for manufacturing the sameUS7274073Oct 8, 2004Sep 25, 2007International Business Machines CorporationIntegrated circuit with bulk and SOI devices connected with an epitaxial regionUS7682941Mar 23, 2010International Business Machines CorporationIntegrated circuit with bulk and SOI devices connected with an epitaxial regionUS8603895Sep 11, 2012Dec 10, 2013Globalfoundries Inc.Methods of forming isolation structures for semiconductor devices by performing a deposition-etch-deposition sequenceUS20030020117 *Apr 2, 2002Jan 30, 2003Samsung Electronics Co., Ltd.Silicon on insulator device having trench isolation layer and method for manufacturing the sameUS20040005766 *Jun 2, 2003Jan 8, 2004Mosel Vitelic, Inc.Method of forming a bottom oxide layer in a trenchUS20040178450 *Mar 26, 2004Sep 16, 2004Samsung Electronics Co., Ltd.Silicon on insulator device having trench isolation layer and method for manufacturing the sameUS20050266641 *Oct 8, 2004Dec 1, 2005Mosel Vitelic, Inc.Method of forming films in a trenchUS20060076628 *Oct 8, 2004Apr 13, 2006International Business Machines CorporationIntegrated circuit with bulk and soi devices connected with an epitaxial regionUS20070020879 *Jul 12, 2006Jan 25, 2007Samsung Electronics Co., LtdMethod of forming an isolation layer and method of manufacturing a field effect transistor using the sameUS20070212857 *May 16, 2007Sep 13, 2007Anderson Brent AIntegrated Circuit With Bulk and SOI Devices Connected with an Epitaxial Region* Cited by examinerClassifications U.S. Classification438/435, 438/443, 438/424, 257/E21.546, 438/444, 438/445International ClassificationH01L21/76, H01L21/762Cooperative ClassificationH01L21/76224European ClassificationH01L21/762CLegal EventsDateCodeEventDescriptionAug 28, 1998ASAssignmentOwner name: INTERNATIONAL BUSINESS MACHINES CORPORATION, NEW YFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MANDELMAN, JACK A.;HO, HERBERT;GAMBINO, JEFFREY P.;REEL/FRAME:009419/0956;SIGNING DATES FROM 19980728 TO 19980730Owner name: KABUSHIKI KAISHA TOSHIBA, JAPANFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:MORIKADO, MUTSUO;REEL/FRAME:009422/0570Effective date: 19980803Apr 14, 2006FPAYFee paymentYear of fee payment: 4May 12, 2010FPAYFee paymentYear of fee payment: 8Apr 16, 2014FPAYFee paymentYear of fee payment: 12RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services