Brevet US6348110 - Methods of manufacturing rotary drill bits - Google Brevets
A rotary drill bit is manufactured by a method including the step of forming at least a portion of the bit body from a precipitation hardening alloy, and brazing cutters to the bit body by a heating and cooling cycle during which the bit body is first heated to a temperature sufficient to melt the brazing...http://www.google.fr/patents/US6348110?utm_source=gb-gplus-shareBrevet US6348110 - Methods of manufacturing rotary drill bits
Numéro de publication US6348110 B1
Numéro de demande US 09/543,306
Date de dépôt 5 avr. 2000
Autre référence de publication US6116360
Numéro de publication 09543306, 543306, US 6348110 B1, US 6348110B1, US-B1-6348110, US6348110 B1, US6348110B1
Inventeurs Stephen Martin Evans
Cessionnaire d'origine Camco International (Uk) Limited
Citations de brevets (8), Référencé par (72), Classifications (9), Événements juridiques (6)
Methods of manufacturing rotary drill bits
US 6348110 B1
A rotary drill bit is manufactured by a method including the step of forming at least a portion of the bit body from a precipitation hardening alloy, and brazing cutters to the bit body by a heating and cooling cycle during which the bit body is first heated to a temperature sufficient to melt the brazing material and is then cooled to room temperature, the heating and cooling brazing cycle being controlled in a manner so as also to effect precipitation hardening of the alloy from which the bit body is formed. In the case where the bit body is formed from solid infiltrated matrix material around a solid preformed mandrel, the heating and cooling cycle of the matrix forming process may also be controlled in a manner to effect precipitation hardening of the alloy from which the mandrel is formed.
1. A method of manufacturing a rotary drill bit comprising a bit body having a threaded shank for connection to a drill string and a leading face to which cutters are brazed, the method including the step of forming at least a portion of the bit body from a precipitation hardening alloy, brazing at least some of said cutters to the bit body by a heating and cooling cycle during which the bit body is first heated to a temperature sufficient to melt the brazing material and is then cooled to room temperature, the heating and cooling brazing cycle being controlled in a manner so as also to effect precipitation hardening of the alloy from which the bit body is formed.
2. A method according to claim 1, including the initial step of locating in a mold a metal mandrel at least a portion of which is formed from a precipitation hardening alloy, packing the mold around part of the mandrel with particulate matrix-forming material, infiltrating said material at elevated temperature with a molten binding alloy, and cooling the material, binding alloy and mandrel to room temperature to form a solid infiltrated matrix bonded to the mandrel, the heating of the mandrel to the infiltration temperature, and subsequent cooling, being controlled in a manner to effect solution treatment of the alloy in the mandrel.
3. A method according to claim 2, wherein substantially all of the mandrel is formed from the precipitation hardening alloy.
4. A method according to claim 3, wherein the mandrel is formed in one piece.
5. A method according to claim 1, wherein substantially all of the bit body is formed from the precipitation hardening alloy.
6. A method according to claim 5, wherein substantially all of the bit body is formed in one piece.
7. A method according to claim 1, wherein the precipitation hardening alloy is a precipitation hardening steel.
8. A method according to claim 7, wherein the precipitation hardening alloy is a martensitic or semi-austenitic steel.
9. A method according to claim 1, wherein the precipitation hardening alloy is a stainless steel.
10. A method according to claim 1, wherein the precipitation hardening alloy is a nickel based alloy.
11. A method according to claim 1, wherein the bit body is further shaped following said precipitation hardening.
12. A method of manufacturing a rotary drill bit comprising a bit body having a threaded shank for connection to a drill string and a leading face to which cutters are brazed, the method including the step of forming the bit body by locating in a mold a metal mandrel, packing the mold around part of the mandrel with particulate matrix-forming material, infiltrating the particulate material at elevated temperature with a binding alloy, and cooling the material and mandrel to room temperature to form a solid infiltrated matrix bonded to the mandrel, wherein the infiltration alloy is a precipitation hardening alloy and wherein the heating of the matrix-forming material to the infiltration temperature, and subsequent cooling, are controlled in a manner to effect precipitation hardening of the infiltration alloy.
This is a Divisional of U.S. patent application Ser. No. 09/108,748, now U.S. Pat. No. 6,116,360, filed Jul. 1, 1998, by Stephen Martin Evans, entitled “METHODS OF MANUFACTURING ROTARY DRILL BITS”.
The invention relates to methods of manufacturing rotary drill bits, and particularly rotary drag-type drill bits of the kind comprising a bit body having a threaded shank for connection to a drill string and a leading face on which are mounted a plurality of cutters secured to the bit body by brazing.
The cutters may, for example, be preform cutting elements comprising a layer of superhard material, such as polycrystalline diamond, bonded to a substrate of less hard material, such as cemented tungsten carbide. The substrate of the cutting element may be bonded, for example by brazing, to a carrier which may also be of cemented tungsten carbide, the carrier then being brazed within a socket on the leading face of the bit body. Alternatively, the substrate of the cutter may itself be of sufficient size to be brazed directly within a socket in the bit body.
Drag-type drill bits of this kind are commonly of two basic types. The bit body may be machined from metal, usually steel, and in this case the sockets to receive the cutters are formed in the bit body by conventional machining processes. Alternatively, the bit body may be formed using a powder metallurgy process in which a metal mandrel is located within a graphite mold, the internal shape of which corresponds to the desired external shape of the bit body. The space between the mandrel and the interior of the mold is packed with a particulate matrix-forming material, such as tungsten carbide particles, and this material is then infiltrated with a binder alloy, usually a copper alloy, in a furnace which is raised to a sufficiently high temperature to melt the body of the infiltration alloy and cause it to infiltrate downwardly through the matrix-forming particles under gravity. The mandrel and matrix material are then cooled to room temperature so that the infiltrate solidifies so as to form, with the particles, a solid infiltrated matrix surrounding and bonded to the metal mandrel.
Sockets to receive the cutters are formed in the matrix by mounting graphite formers in the mold before it is packed with the particulate material so as to define sockets in the material, the formers being removed from the sockets after formation of the matrix. Alternatively or additionally, the sockets may be machined in the matrix. The cutters are again secured in the sockets by brazing.
In order to braze the cutters in place the cutters are located in their respective sockets with a supply of brazing alloy. The bit body, with the cutters in place, is then heated in a furnace to a temperature at which the brazing alloy melts and spreads by capillary action between the inner surfaces of the sockets and the outer surfaces of the cutters, an appropriate flux being used to facilitate this action.
In use, such drill bits are subject to considerable wear and erosion, for example due to the high pressure flow of drilling fluid over the surface of the bit body for the purpose of cooling and cleaning the cutters and transporting the cuttings to the surface. Matrix-bodied bits are very resistant to such wear and erosion but it is desirable for a steel bodied bit to be hardened and/or formed with a harder erosion-resistant coating.
During the process of brazing the cutters to the bit body, the bit body must be heated to a temperature which is usually in the range of 500°-750° and with the steels hitherto used in the manufacture of the bit bodies of rotary drag-type bits, the heating/cooling cycle employed during brazing of the cutters in position has the effect of reducing the hardness and strength of the steel. In view of this, it is common practice to manufacture the steel body of the bit, or the steel mandrel of a matrix bit, in two parts. In the case of a steel bodied bit, one part of the bit provides the leading surface to which the cutters are brazed while the other part provides the threaded shank for connection to the drill string. The two parts are welded together after the cutters have been brazed to the leading part so that the shank part is not reduced in hardness or strength as a result of the brazing process.
Similarly, in a matrix bodied bit the steel mandrel is formed in two parts. A first part is mounted within the mold so that the solid infiltrated matrix may be bonded to it and the second part of the mandrel, providing the threaded shank, is welded to the first part after the matrix has been formed and after the cutters have been brazed into the sockets in the matrix. The part of the mandrel providing the shank does not therefore have its hardness or strength reduced by the brazing process nor by the heating/cooling cycle of the infiltration process.
It would be desirable to avoid the necessity of forming the bit body or mandrel in two parts. Forming the bit or mandrel in two parts not only adds to the cost of the manufacturing process but the necessity of welding the parts together may compromise the design of the bit body. For example, the bit body must be of sufficient length, and so shaped, as to provide a region where the two parts can be welded together. Accordingly, a one-piece bit body could be shorter in length than a two-piece body and this may have advantage, particularly where the drill bit is for use in steerable drilling systems. Furthermore, the reduction in hardness and strength of the first part of the bit body or mandrel during brazing, or infiltration and brazing, is in itself undesirable and in the case of a steel bodied bit makes it even more necessary to hard face the surface of the bit body to avoid unacceptable wear or erosion. Also, the reduction in strength can lead to premature failure of the bit, particularly due to fracture of the blades on which the cutters are mounted.
The present invention is based on the realisation that by using a different type of steel, or other metal alloy, from those hitherto used for rotary drag-type drill bit bodies, the heating/cooling cycles to which the bit body is subjected during manufacture may be used actually to harden and strengthen the alloy of the bit body rather than reduce its hardness and strength, with the result that the bit body, or mandrel in the case of a matrix-bodied bit, may be formed in one piece, thus avoiding the above-mentioned disadvantages.
This is achieved by using for the bit body or mandrel a precipitation hardening alloy, which may, for example, be steel or stainless steel. As is well known, a precipitation hardening alloy is an alloy in which very fine particles of constituents of the alloy may be caused to precipitate, i.e. initiate and grow from the parent alloy, so as to harden and strengthen the alloy. Such precipitation may be effected by subjecting the alloy to a controlled heating and cooling cycle.
The initiation and growth of precipitates (“precipitation”) is a diffusion process, i.e. it is controlled by time and temperature. A certain threshold amount of energy is required to trigger initiation. In certain alloys, there is sufficient energy at room temperature to trigger initiation; albeit at a very slow pace. In the majority of alloys, however, an elevated temperature, and a minimum time at that temperature, is required to trigger initiation.
The size of the precipitates is critical to the degree of hardness, strength, and ductility obtained. The precipitation hardening effect arises from the precipitates causing local distortion of the crystal lattice. The greatest hardness (and the lowest ductility) is achieved when the precipitates are numerous and exceptionally fine. As the temperature is increased above a threshold temperature, larger and fewer particles are precipitated and, as a result, hardness decreases and ductility increases. As the temperature is raised further, there comes a point where the particles are too few and too large to contribute appreciably to the hardness/strength of the alloy.
A “solution” heat treatment in which the alloy is raised to an even higher temperature, acts to “dissolve” the majority of existing precipitates, by taking them back into the solid solution. Subsequent cooling to room temperature tends to lock the precipitation hardening elements into solid solution. The faster the cooling rate, the greater is this tendency. The slower the cooling rate, the more chance there is to initiate and grow precipitates during the cooling cycle. The precipitates created during the cooling cycle, from the higher temperature, tend to be less beneficial to increasing hardness/strength than those created by a subsequent, separate, precipitation hardening heat treatment.
The overall aim, according to the invention, therefore, is to subject the alloy from which a bit body is formed to a combination of time and temperature which causes precipitation hardening and gives rise to the optimum hardness/ductility combination. In theory, this may be achieved by first taking all the precipitates into solution at a high “solution treatment” temperature; followed by fast cooling to room temperature; followed by heating quickly to a lower precipitation hardening temperature and holding at that temperature for a prescribed time; followed by a fast cool back to room temperature. Precipitation hardening may also be effected by performing the latter precipitation hardening step alone.
The present invention lies in controlling the heating/cooling cycle to which the bit body or mandrel is subjected during the process of brazing the cutters to the bit body, so as to effect precipitation hardening, or, in a matrix-bodied bit, controlling the heating/cooling cycle to which the bit body is subjected during the infiltration process, so as to effect a preliminary “solution” heat treatment, as described above, prior to the precipitation hardening effected by subsequently brazing the cutters to the bit body.
According to the broadest aspect of the present invention, therefore, there is provided a method of manufacturing a rotary drill bit of the kind comprising a bit body having a threaded shank for connection to a drill string and a leading face to which cutters are brazed, the method including the step of forming at least a portion of the bit body from a precipitation hardening alloy, brazing at least some of said cutters to the bit body by a heating and cooling cycle during which the bit body is first heated to a temperature sufficient to melt the brazing material and is then cooled to room temperature, the heating and cooling brazing cycle being controlled in a manner so as also to effect precipitation hardening of the alloy from which the bit body is formed.
In the case of the manufacture of a matrix-bodied bit, the method also includes the initial step of locating in a mold a metal mandrel at least a portion of which is formed from a precipitation hardening alloy, packing the mold around part of the mandrel with particulate matrix-forming material, infiltrating said material at elevated temperature with a molten binding alloy, and cooling the material, binding alloy and mandrel to room temperature to form a solid infiltrated matrix bonded to the mandrel, the heating of the mandrel to the infiltration temperature, and subsequent cooling, being controlled in a manner to effect solution treatment of the alloy in the mandrel.
As previously described, solution treatment may be the first stage in a two-stage precipitation hardening process. Raising the temperature of the precipitation hardening alloy to the typical infiltration temperature, say 1160° C., dissolves the majority of any existing precipitates in the alloy, taking them into solid solution, so that cooling from that temperature, and the subsequent brazing process, forms precipitates which increase the hardness and strength of the alloy, as previously described.
In the case of a matrix-bodied bit preferably substantially all of the mandrel is formed from the precipitation hardening alloy, and the mandrel is preferably formed in one piece.
Similarly in the case of a steel or other metal-bodied bit all of the bit body is preferably formed from the precipitation hardening alloy and, again, is preferably formed in one piece.
The precipitation hardening alloy may be a precipitation hardening steel. For example it may be a martensitic or semi-austenitic type steel. The steel may be a stainless steel.
However, the invention is not limited to the use of steel or stainless steel for the bit body or mandrel and the use of other precipitation hardening alloys is contemplated, for example nickel based alloys.
In any of the methods according to the invention the bit body may be further shaped, for example by machining, following said precipitation hardening.
The invention includes within its scope a rotary drill bit comprising a bit body having a threaded shank for connection to a drill string and a leading face to which cutters are brazed, wherein at least a major portion of the bit body is formed from an alloy which has been precipitation hardened.
The bit body may comprise a metal mandrel around part of the outer surface of which is formed a layer of solid infiltrated matrix material, at least part of the mandrel being formed from said alloy which has been precipitation hardened.
Preferably, substantially all of the mandrel is formed from said alloy which has been precipitation hardened, and the mandrel may be formed in one piece.
Alternatively, all of the bit body may be formed, for example in one piece, from said alloy which has been precipitation hardened.
There may also be advantage in using a precipitation hardening alloy as the infiltration alloy in a matrix-bodied drill bit regardless of whether or not the mandrel is formed from a precipitation hardening alloy also. The use of a precipitation hardening infiltration alloy may be advantageous in increasing the hardness and strength of the resultant solid infiltrated matrix, making such matrix material more resistant to wear and erosion.
Accordingly, the invention also provides a method of manufacturing a rotary drill bit of the kind comprising a bit body having a threaded shank for connection to a drill string and a leading face to which cutters are brazed, the method including the step of forming the bit body by locating in a mold a metal mandrel, packing the mold around part of the mandrel with particulate matrix-forming material, infiltrating the particulate material at elevated temperature with a binding alloy, and cooling the material and mandrel to room temperature to form a solid infiltrated matrix bonded to the mandrel, wherein the infiltration alloy is a precipitation hardening alloy and wherein the heating of the matrix-forming material to the infiltration temperature, and subsequent cooling, are controlled in a manner to effect precipitation hardening of the infiltration alloy.
FIG. 1 is a diagrammatic section through a prior art rotary drag-type drill bit.
FIG. 2 shows diagrammatically the manufacture of part of a prior art matrix-bodied drill bit.
FIG. 3 is a similar view to FIG. 1 showing diagrammatically a drill bit manufactured by the method according to the present invention.
FIG. 4 shows diagrammatically the manufacture of a matrix-bodied drill bit by a method according to the present invention.
FIG. 1 shows a prior art steel bodied drill bit. The main body 10 of the drill bit comprises a leading part 11 which provides the leading face 12 of the drill bit. The leading part 11 is welded, as indicated at 13, to a shank part 14 which provides a tapered threaded pin 15 for connecting the drill bit to a drill string, and at least two parallel breaker slots 16 on opposite sides of the shank which, in use, are engaged by a suitable tool when making or breaking the connection between the bit and the drill string.
The leading part 11 of the bit body is formed with a number of blades 17 which extend outwardly away from the axis of rotation of the bit. Cutters 18 are mounted side-by-side along each blade.
As is well known, each cutter may comprise a front facing table of polycrystalline diamond or other superhard material which is bonded in a high pressure high temperature press to a substrate of less hard material, usually cemented tungsten carbide. Each cutter is generally cylindrical and the substrate may be of sufficient axial length that it may be brazed directly into a socket machined in the blade 17. Alternatively, the cutter may be bonded to a generally cylindrical stud or post which is in turn brazed into a socket in the blade. The invention is not limited to the use of cutters of this type, and other forms of cutter may be employed.
The two parts of the bit body 10 are formed with a central passage 19 through which drilling fluid is delivered under pressure, in known manner, to nozzles (not shown), in the leading face 12 of the bit. The flow of drilling fluid from the nozzles is arranged to cool and clean the cutters 18 and to transport the cuttings of the formation being drilled upwardly through the annulus between the drill string and the walls of the borehole.
As previously discussed, in order to braze the cutters 18 into their respective sockets on the blades 17 the part on which the cutters are mounted must be subjected to a heating/cooling cycle in a furnace. This process tends to reduce the hardness and strength of the steel part which is subjected to it, and it is for this reason that the bit body 10 is formed in two parts. It is then only the leading part 11 on which the cutters 18 are to be mounted which subjected to the heating/cooling brazing cycle, this part being subsequently welded to the shank part 14. This ensures that the shank part 14 is not subjected to the reduction in hardness or strength would occur if it were subjected to the brazing cycle.
The two parts of the bit body may be entirely machined to the required shape before being welded together, but it is also possible to effect some machining after the two parts have been welded together. For example, arrangements are known in which the breaker slots 16 extend partly across the weld 13 and in this case the breaker slots are machined after the two parts have been welded together.
This known type of drill bit suffers from certain disadvantages. Thus, the reduction in hardness of the leading part 11 of the bit body during the brazing cycle makes it necessary subsequently to treat the bit part in order to prevent damaging erosion and wear in use. This may be achieved by hardening the part 11 by a process which will not damage the cutters 18 or their brazed connection to the blade 17, or by applying a hard facing to the outer surface of the leading part of the bit body. However, such additional processes add to the complexity of the overall process of manufacturing the bit and inevitably increase the cost.
Also, the necessity of welding the two parts of the bit body together means that each part must be so designed that it can be securely fitted and welded to the other. In practice, this tends to have the effect of increasing the axial length of the drill bit. There is often now a requirement for drill bits to be as axially short as possible, particularly where the bit is to be used in a steerable drilling system, so as more easily to permit deflection of the direction in which the bit drills in the borehole.
As previously mentioned, in another form of drag-type drill bit the leading part 11 of the bit body, instead of being wholly machined from steel or other metal, consists of a metal mandrel around which is formed a solid infiltrated matrix. FIG. 2 illustrates a known method of manufacturing a bit body of this type.
Referring to FIG. 2, there is machined a graphite mold 20, the inner surface 21 of which corresponds substantially in shape to the desired outer configuration of the leading part of a two-part bit body, including the blades.
A metal mandrel 22, usually of steel, is supported within the mold 20. Formers 23, 24 are also located within the mold so as to form the central passage in the bit body and the subsidiary passages leading to the nozzles. Graphite formers (not shown) are also located on the interior surface of the mold to form the sockets into which the cutters will eventually be brazed.
The spaces between the mandrel 22 and the interior of the mold 20 are packed with a particulate matrix-forming material, such as particles of tungsten carbide, this material also being packed around the graphite formers. A body of a suitable binder alloy, usually a copper based alloy, is then located around and above the mandrel 22 and packed matrix-forming material. The body of alloy is usually in the form of an annulus which surrounds the central former 23 above the mandrel 22. The mold is then closed and placed in a furnace and heated to a temperature at which the alloy fuses and infiltrates downwardly into the mass of particulate material. The mold is then cooled so that the binder alloy solidifies, binding the tungsten carbide particles together and to the mandrel 22 so as to form a solid infiltrated matrix surrounding the mandrel 22 and in the desired shape of the outer surface of the bit body.
When the matrix-covered mandrel is removed from the mold, the formers are removed so as to define the passages in the bit body and the sockets for the cutters, and the component is then machined to the appropriate final shape, as indicated by the lines 25 in FIG. 2.
The blades of the bit may be entirely formed of matrix or metal cores may be located in the mold at each blade location so as to be surrounded by matrix and thus form a blade comprising a matrix layer on a central metal core.
After machining, the matrix/steel bit part is welded to the machined steel shank part in similar fashion to the arrangement of FIG. 1.
In this method of manufacture of a drill bit, the infiltration temperature to which the components must be heated is significantly higher than the subsequent brazing temperature at which the cutters are brazed within the sockets in the matrix, and the infiltration heating/cooling cycle also has the effect of reducing the hardness and strength of the steel mandrel 22. It is for this reason that, again, the shank part of the drill bit is separately formed from steel and is subsequently welded to the matrix/steel leading part.
By contrast, the present invention allows the whole bit body in a steel or other metal machined bit, or the mandrel in a matrix-bodied bit, to be formed in one piece with the advantages that this gives.
FIG. 3 shows diagrammatically a steel-bodied bit manufactured in accordance with the present invention.
As may be seen from FIG. 3, the steel body 26 of the bit, including the leading part 27, the shank part 28 and blades 29, is machined in one piece from a single solid body of steel or other metal. According to the present invention, however, the steel or other alloy from which the bit body 26 is formed is a precipitation hardening alloy. As previously described, when a precipitation hardening alloy is subjected to an appropriately controlled heating/cooling cycle, particles of constituents of the alloy precipitate and locally distort the lattice of the alloy at the microscopic level to create local stress zones and thereby increase the hardness and strength of the material. It has been found that the heating and cooling cycle to which a bit body must be subjected in order to braze the cutters to the blades 29 can be so controlled that, where the metal of the bit body is a precipitation hardening alloy, the brazing process itself may have the effect of precipitation hardening of the bit body, instead of reducing its hardness and strength as has been the case with the metals used hitherto.
For example, one suitable form of alloy for use in manufacture of the bit body is a 17-4 PH grade of martensitic precipitation hardening stainless steel having the following chemical composition:
Phosphorus 0.04
Chromium 15.00 17.50
Molybdenum 0.50
Nickel 3.00 5.00
Niobium 5 × C min 0.45
Copper 3.00 5.00
The metal may be that which conforms to the following standard specifications:
AMS 5622 (remelt)
AMS 5643 QQ-S-763 B
MIL-S-862 B
MIL-C-24111 (Nuclear)
ASTM A564-72 Type 630
W.1.4548
NACE MR.01.75
During the brazing process the temperature of the bit body is raised to the region of 500°-750° C., preferably about 715°-720° C., and is held at this temperature for about 20 minutes before cooling naturally to room temperature. It is found that this cycle is effective for brazing the cutters into their sockets while at the same time effecting precipitation hardening of the whole bit body.
As may be seen from FIG. 3, the fact that the bit body can now be formed in one piece allows the bit to be designed without needing to accommodate welding between two parts. The breaker slots 30 may therefore be closer to the upper ends of the blades 29, thus reducing the overall axial length of the drill bit.
FIG. 4 shows the use of a precipitation hardening alloy in the manufacture of a matrix bodied bit.
As in the arrangement of FIG. 2, a metal mandrel 31 is located within a suitably shaped graphite mold 32 and matrix-forming particulate material is packed around the lower part of the mandrel before being infiltrated in a furnace with an appropriate binder alloy.
According to the present invention, however, the mandrel 31 is formed from a precipitation hardening alloy, such as the 17-4 PH grade stainless steel referred to above. In this case, the mandrel 31 includes an upper portion 33 from which the threaded shank 34 of the bit body may be subsequently machined as indicated in chain lines in FIG. 4.
During the infiltration process the mandrel is heated to a temperature of about 1160° C. before being allowed to cool naturally to room temperature. During the heating part of this “solution” treatment, the majority of any existing precipitates in the alloy are dissolved into solid solution. During the subsequent cooling from the infiltration temperature, precipitates of constituents of the alloy are formed in solution as the first stage of a precipitation hardening process. The bit body is then subjected to a further heating/cooling cycle in order to effect brazing of the cutters to the sockets in the matrix part of the bit and during this heating/cooling cycle the precipitation hardening is completed.
Other suitable forms of precipitation hardening alloys are 15-5 PH grade and 520 B grade stainless steels having the following typical compositions.
15-5 PH Grade:
Phosphorus 0.03
Sulphur 0.015
Chromium 14.00 15.50
Nickel 3.50 5.50
Copper 2.50 4.50
AMS 5659 (remelt)
ASTM A630 Type XM12
520 B Grade:
Chromium 14.00
Molybdenum 1.70
Nickel 5.60
Niobium 0.30
Copper 1.80
BS.5143
BS.5144
Other proprietary grades of stainless steel may be used allowing up to 3% Molybdenum, 0.15% carbon 8% nickel and down to 13% chromium.
Semi-austenitic precipitation hardening stainless steels may also be employed, including 17-7 PH grade stainless steel having the following composition:
Chromium 17.0
Nickel 7.0
Titanium 0.4 to 1.2
Other proprietary grades of semi-austenitic precipitation hardening stainless steels may be used, in grades allowing up to 0.2% carbon, 2% copper, 3% molybdenum, 2% cobalt, 1.2% aluminium, 2% cobalt, 0.3% phosphorus and down to 12% chromium and 3.5% nickel. All percentages are by weight.
Although the specific alloys described above are steel, and this is preferred, the present invention does not exclude the use of other precipitation hardening alloys in the manufacture of the bit body, or the mandrel in a matrix-bodied bit, provided of course that the alloy has other characteristics which are suitable for use as the body of a drag-type drill bit. Such required characteristics are well known to those skilled in the art and will not be discussed in detail.
As previously mentioned, in the manufacture of a matrix-bodied bit, as described above, there may also be advantage in using a precipitation hardening alloy as the infiltration alloy, whether or not the mandrel is formed from a precipitation hardening alloy also. The use of a precipitation hardening infiltration alloy may increase the hardness and strength of the resultant solid infiltrated matrix, since the alloy will be precipitation hardened during the infiltration and subsequent brazing heating/cooling cycles.
Typical precipitation hardening copper-base alloys which may be used as infiltrant alloys in the formation of matrix-bodied bits are defined in the following Tables 1 and 2.
Table 3 shows, for 17-4 PH steel, the theoretical time and temperature conditions of solution treatment and precipitation hardening which will achieve the optimum hardness and strength for the alloy. It also shows the actual conditions which have been employed to achieve precipitation hardening in the two heating/cooling stages involved in the manufacture of a matrix bodied bit, together with the actual hardness and strength achieved.
It will be seen that the hardness and strength achieved in the process according to the invention is comparable to the hardness and strength of the pin steel used in prior art two-part bits, i.e. that portion of the two-part bit which is not subjected to heat treatment and provides the threaded pin of the bit, for attachment to the drill string.
ALLOYS WITH ADDITIONS OF ALUMINIUM, TITANIUM, NIOBIUM (COLUMBIUM IN USA), TO PROMOTE PRECIPITATION
ALLOY Trade Manu- COMPOSITIONAL LIMITS (Wt %)
GROUP Name facturer Copper Nickel Manganese Aluminium Iron Silicon Others
#1 Hiduron ® Langley Remainder 15 up to 2 3 up to 2 Residual Residual
Cupro- 130 Alloys
Nickels Hiduron ® Langley Remainder 15 5 2 1 Residual Up to 1% Cr for grain
191 Alloys refinement. Others
Hiduron ® Langley Remainder 14 10  2 5 Residual Up to 1% Cr for grain
501 Alloys refinement. Others
Marinel ® Langley Remainder 17 5 2 1 Residual Up to 1% Cr for grain
Alloys refinement. Others
residual + “Small” additions
of Ti, and Nb. Exact
values not known. Best
guess 0.5% of each.
“Blanket” Langley Remainder 12-20 up to 12 1-5 up to 5 Residual Up to 2% of each of Cr,
Spec. for Alloys Ti and Nb
Hiduron ®
G- Johnson Remainder 2.5 Residual Residual Residual 0.6% Residual
Bronze ® Matthey
ALLOYS WITH ADDITIONS OF BERYLLIUM, TITANIUM, AND ZIRCONIUM TO PROMOTE PRECIPITATION HARDENING
ALLOY Common Manu- COMPOSITIONAL LIMITS (Wt %)
GROUP Title facturer Copper Nickel Beryllium Iron Cobalt Silicon Others
#1 21C Various. Remainder — 2.00-2.25 Residual 1.0-1.2 0.2-0.4 Residual
Beryllium Not
Copper Proprietary
Special 71C Various. Remainder 29.0-33.0 0.4-0.7 0.8-1.1 Residual Residual Residual
Alloys (CA966) Not
72C Various. Remainder 29.0-33.0 (1.1-1.2) 0.7-1.0 (2) (5) 0.1-0.2 Zirconium; 0.1-
Not 0.2 Titanium
17-4 PH stainless steel, the ideal and actual conditions and results.
“Solution” Hardening”
Treatment Treatment Mechanical Properties
Cooling Cooling Strength
Ideal Temp. Medium Temp. Medium Hard- Proof/ Ductility
or and and and and ness Tensile Charpy
Actual Time Rate Time Rate (HRC) (MPa) (Joules)
17-4 1040° C. Oil/Air 620° C. Air 33 850/ 60
PH. × (Slow to × (Slow) 1000
Ideal 0.5 hr Medium) 4 hrs
17-4 1160° C. Water 0.5 to 1.0 hours to 30 690/ 50
PH. × Quench 650° C. Followed by 1040
Actual (2 to 5) on mould 0.5 to 1 hour at
Infil. hrs base 650° C. Followed by
and (Slow) 0.5 to 1 hour to
Braze 720° C. Followed by
Cycle 0.5 to 1 hour at
comb- 720° C. Followed by
ined furnace cool (0.5 to
1.5 hours) to
670° C. Followed
17-4 — — 0.5 to 1.0 hours to Not yet tested but likely to be
Actual 650° C. Followed by similar to current pin steel
Braze 0.5 to 1 hour at (below)
Cycle 650° C. Followed by
alone 0.5 to 1 hour to
720° C. Followed by
0.5 to 1 hour at
furnace cool (0.5 to
Curr- — — — 35 760/ 55
US4699227 12 déc. 1985 13 oct. 1987 Nl Petroleum Products Limited Method of forming cutting structures for rotary drill bits
US4781256 30 juin 1987 1 nov. 1988 Nl Petroleum Products Limited Cutting structures for rotary drill bits
US5666864 * 31 mars 1995 16 sept. 1997 Tibbitts; Gordon A. Earth boring drill bit with shell supporting an external drilling surface
US6148936 * 4 févr. 1999 21 nov. 2000 Camco International (Uk) Limited Methods of manufacturing rotary drill bits
EP0198627A1 1 avr. 1986 22 oct. 1986 Reed Tool Company Limited Improvements in or relating to the manufacture of rotary drill bits
EP0474092A2 27 août 1991 11 mars 1992 General Electric Company Using thermally-stable diamond or CBN compacts as tips for rotary drills
GB2075396A Titre non disponible
GB2211874A Titre non disponible
US7334652 9 févr. 2005 26 févr. 2008 Halliburton Energy Services, Inc. Roller cone drill bits with enhanced cutting elements and cutting structures
US7434632 17 août 2004 14 oct. 2008 Halliburton Energy Services, Inc. Roller cone drill bits with enhanced drilling stability and extended life of associated bearings and seals
US7497281 6 févr. 2007 3 mars 2009 Halliburton Energy Services, Inc. Roller cone drill bits with enhanced cutting elements and cutting structures
US7703555 30 août 2006 27 avr. 2010 Baker Hughes Incorporated Drilling tools having hardfacing with nickel-based matrix materials and hard particles
US7729895 7 août 2006 1 juin 2010 Halliburton Energy Services, Inc. Methods and systems for designing and/or selecting drilling equipment with desired drill bit steerability
US7775287 12 déc. 2006 17 août 2010 Baker Hughes Incorporated Methods of attaching a shank to a body of an earth-boring drilling tool, and tools formed by such methods
US7776256 10 nov. 2005 17 août 2010 Baker Huges Incorporated Earth-boring rotary drill bits and methods of manufacturing earth-boring rotary drill bits having particle-matrix composite bit bodies
US7778777 7 août 2006 17 août 2010 Halliburton Energy Services, Inc. Methods and systems for designing and/or selecting drilling equipment using predictions of rotary drill bit walk
US7784567 6 nov. 2006 31 août 2010 Baker Hughes Incorporated Earth-boring rotary drill bits including bit bodies comprising reinforced titanium or titanium-based alloy matrix materials, and methods for forming such bits
US7802495 10 nov. 2005 28 sept. 2010 Baker Hughes Incorporated Methods of forming earth-boring rotary drill bits
US7827014 7 août 2006 2 nov. 2010 Halliburton Energy Services, Inc. Methods and systems for design and/or selection of drilling equipment based on wellbore drilling simulations
US7841259 27 déc. 2006 30 nov. 2010 Baker Hughes Incorporated Methods of forming bit bodies
US7860693 18 avr. 2007 28 déc. 2010 Halliburton Energy Services, Inc. Methods and systems for designing and/or selecting drilling equipment using predictions of rotary drill bit walk
US7860696 12 déc. 2008 28 déc. 2010 Halliburton Energy Services, Inc. Methods and systems to predict rotary drill bit walk and to design rotary drill bits and other downhole tools
US7913779 29 sept. 2006 29 mars 2011 Baker Hughes Incorporated Earth-boring rotary drill bits including bit bodies having boron carbide particles in aluminum or aluminum-based alloy matrix materials, and methods for forming such bits
US7997359 27 sept. 2007 16 août 2011 Baker Hughes Incorporated Abrasive wear-resistant hardfacing materials, drill bits and drilling tools including abrasive wear-resistant hardfacing materials
US8002052 27 juin 2007 23 août 2011 Baker Hughes Incorporated Particle-matrix composite drill bits with hardfacing
US8074750 3 sept. 2010 13 déc. 2011 Baker Hughes Incorporated Earth-boring tools comprising silicon carbide composite materials, and methods of forming same
US8091452 * 5 janv. 2009 10 janv. 2012 Unitac, Incorporated Method for manufacturing drill head
US8104550 28 sept. 2007 31 janv. 2012 Baker Hughes Incorporated Methods for applying wear-resistant material to exterior surfaces of earth-boring tools and resulting structures
US8145465 28 sept. 2010 27 mars 2012 Halliburton Energy Services, Inc. Methods and systems to predict rotary drill bit walk and to design rotary drill bits and other downhole tools
US8176812 27 août 2010 15 mai 2012 Baker Hughes Incorporated Methods of forming bodies of earth-boring tools
US8230762 7 févr. 2011 31 juil. 2012 Baker Hughes Incorporated Methods of forming earth-boring rotary drill bits including bit bodies having boron carbide particles in aluminum or aluminum-based alloy matrix materials
US8261632 9 juil. 2008 11 sept. 2012 Baker Hughes Incorporated Methods of forming earth-boring drill bits
US8272295 7 déc. 2006 25 sept. 2012 Baker Hughes Incorporated Displacement members and intermediate structures for use in forming at least a portion of bit bodies of earth-boring rotary drill bits
US8296115 16 août 2010 23 oct. 2012 Halliburton Energy Services, Inc. Methods and systems for designing and/or selecting drilling equipment using predictions of rotary drill bit walk
US8309018 30 juin 2010 13 nov. 2012 Baker Hughes Incorporated Earth-boring rotary drill bits and methods of manufacturing earth-boring rotary drill bits having particle-matrix composite bit bodies
US8352221 2 nov. 2010 8 janv. 2013 Halliburton Energy Services, Inc. Methods and systems for design and/or selection of drilling equipment based on wellbore drilling simulations
US8388723 8 févr. 2010 5 mars 2013 Baker Hughes Incorporated Abrasive wear-resistant materials, methods for applying such materials to earth-boring tools, and methods of securing a cutting element to an earth-boring tool using such materials
US8606552 19 oct. 2012 10 déc. 2013 Halliburton Energy Services, Inc. Methods and systems for designing and/or selecting drilling equipment using predictions of rotary drill bit walk
US8758462 8 janv. 2009 24 juin 2014 Baker Hughes Incorporated Methods for applying abrasive wear-resistant materials to earth-boring tools and methods for securing cutting elements to earth-boring tools
US8770324 10 juin 2008 8 juil. 2014 Baker Hughes Incorporated Earth-boring tools including sinterbonded components and partially formed tools configured to be sinterbonded
US9192989 7 juil. 2014 24 nov. 2015 Baker Hughes Incorporated Methods of forming earth-boring tools including sinterbonded components
US9200485 9 févr. 2011 1 déc. 2015 Baker Hughes Incorporated Methods for applying abrasive wear-resistant materials to a surface of a drill bit
US9493990 4 déc. 2007 15 nov. 2016 Halliburton Energy Services, Inc. Roller cone drill bits with optimized bearing structures
US9506297 4 juin 2014 29 nov. 2016 Baker Hughes Incorporated Abrasive wear-resistant materials and earth-boring tools comprising such materials
US9700991 5 oct. 2015 11 juil. 2017 Baker Hughes Incorporated Methods of forming earth-boring tools including sinterbonded components
US9752204 11 févr. 2014 5 sept. 2017 Halliburton Energy Services, Inc. Precipitation hardened matrix drill bit
US20010037902 * 10 avr. 2001 8 nov. 2001 Shilin Chen Force-balanced roller-cone bits, systems, drilling methods, and design methods
US20030051917 * 3 juin 2002 20 mars 2003 Halliburton Energy Services, Inc. Roller cone bits, methods, and systems with anti-tracking variation in tooth orientation
US20040104053 * 8 mars 2003 3 juin 2004 Halliburton Energy Services, Inc. Methods for optimizing and balancing roller-cone bits
US20040140130 * 13 janv. 2004 22 juil. 2004 Halliburton Energy Services, Inc., A Delaware Corporation Roller-cone bits, systems, drilling methods, and design methods with optimization of tooth orientation
US20040158445 * 26 janv. 2004 12 août 2004 Shilin Chen Force-balanced roller-cone bits, systems, drilling methods, and design methods
US20040158446 * 26 janv. 2004 12 août 2004 Shilin Chen Force-balanced roller-cone bits, systems, drilling methods, and design methods
US20040167762 * 26 févr. 2004 26 août 2004 Shilin Chen Force-balanced roller-cone bits, systems, drilling methods, and design methods
US20040182609 * 27 janv. 2004 23 sept. 2004 Shilin Chen Force-balanced roller-cone bits, systems, drilling methods, and design methods
US20040186700 * 28 janv. 2004 23 sept. 2004 Shilin Chen Force-balanced roller-cone bits, systems, drilling methods, and design methods
US20040188148 * 28 janv. 2004 30 sept. 2004 Halliburton Energy Service, Inc. Roller-cone bits, systems, drilling methods, and design methods with optimization of tooth orientation
US20050194191 * 17 août 2004 8 sept. 2005 Halliburton Energy Services, Inc. Roller cone drill bits with enhanced drilling stability and extended life of associated bearings and seals
US20060032674 * 12 août 2005 16 févr. 2006 Shilin Chen Roller cone drill bits with optimized bearing structures
US20060118333 * 11 nov. 2005 8 juin 2006 Halliburton Energy Services, Inc. Roller cone bits, methods, and systems with anti-tracking variation in tooth orientation
US20060224368 * 26 mai 2006 5 oct. 2006 Shilin Chen Force-balanced roller-cone bits, systems, drilling methods, and design methods
US20070029113 * 7 août 2006 8 févr. 2007 Shilin Chen Methods and system for designing and/or selecting drilling equipment with desired drill bit steerability
US20070102200 * 29 sept. 2006 10 mai 2007 Heeman Choe Earth-boring rotary drill bits including bit bodies having boron carbide particles in aluminum or aluminum-based alloy matrix materials, and methods for forming such bits
US20070125579 * 6 févr. 2007 7 juin 2007 Shilin Chen Roller Cone Drill Bits With Enhanced Cutting Elements And Cutting Structures
US20080029310 * 27 juin 2007 7 févr. 2008 Stevens John H Particle-matrix composite drill bits with hardfacing and methods of manufacturing and repairing such drill bits using hardfacing materials
US20080135305 * 7 déc. 2006 12 juin 2008 Baker Hughes Incorporated Displacement members and methods of using such displacement members to form bit bodies of earth-boring rotary drill bits
US20090090556 * 12 déc. 2008 9 avr. 2009 Shilin Chen Methods and Systems to Predict Rotary Drill Bit Walk and to Design Rotary Drill Bits and Other Downhole Tools
US20090113811 * 8 janv. 2009 7 mai 2009 Baker Hughes Incorporated Abrasive wear-resistant materials, methods for applying such materials to earth-boring tools, and methods for securing cutting elements to earth-boring tools
US20090120240 * 5 janv. 2009 14 mai 2009 Takuji Nomura Method for manufacturing drill head
US20090301789 * 10 juin 2008 10 déc. 2009 Smith Redd H Methods of forming earth-boring tools including sinterbonded components and tools formed by such methods
US20100006345 * 9 juil. 2008 14 janv. 2010 Stevens John H Infiltrated, machined carbide drill bit body
US20100300758 * 16 août 2010 2 déc. 2010 Shilin Chen Methods and systems for designing and/or selecting drilling equipment using predictions of rotary drill bit walk
US20110015911 * 28 sept. 2010 20 janv. 2011 Shilin Chen Methods and systems to predict rotary drill bit walk and to design rotary drill bits and other downhole tools
US20110062627 * 11 nov. 2010 17 mars 2011 Baker Hughes Incorporated Cutting tools and methods of making the same
US20110077928 * 2 nov. 2010 31 mars 2011 Shilin Chen Methods and systems for design and/or selection of drilling equipment based on wellbore drilling simulations
EP2085176A1 * 23 oct. 2007 5 août 2009 UNITAC, Incorporated Manufacturing method for drill head
EP2085176A4 * 23 oct. 2007 22 déc. 2010 Unitac Inc Manufacturing method for drill head
WO2008042328A1 * 28 sept. 2007 10 avr. 2008 Baker Hughes Incorporated Earth-boring rotary drill bits including bit bodies having boron carbide particles in aluminum or aluminum-based alloy matrix materials, and methods for forming such bits
WO2011160109A1 * 20 juin 2011 22 déc. 2011 National Machine Company Axle sleeve manufacturing process
Classification aux États-Unis 148/528, 148/228
Classification internationale B23K35/14, B23K1/00, E21B10/54
Classification coopérative E21B10/54, B23K1/0008
Classification européenne E21B10/54, B23K1/00S
15 août 2000 AS Assignment
Owner name: SCHLUMBERGER HOLDING LIMITED, VIRGIN ISLANDS, BRIT
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:EVANS, STEPHEN MARTIN;REEL/FRAME:011132/0120
30 août 2001 AS Assignment
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:SCHLUMBERGER HOLDINGS LIMITED;REEL/FRAME:012141/0602
27 juil. 2005 FPAY Fee payment
22 juil. 2009 FPAY Fee payment