Source: http://www.google.com/patents/US20030138699?ie=ISO-8859-1
Timestamp: 2014-09-30 16:35:07
Document Index: 785861357

Matched Legal Cases: ['application No. 2002', 'Application No. 98', 'Application No. 98', 'Application No. 98', 'Application No. 98', 'Application No. 98', 'Application No. 98', 'Application No. 98', 'Application No. 98']

Patent US20030138699 - Positive active material for rechargeable lithium battery - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign in<nobr>Advanced Patent Search</nobr>PatentsDisclosed is a positive active material for a rechargeable lithium battery, including a lithiated intercalation compound and an additive compound. The additive compound comprises one or more intercalation element-included oxides which have a charging voltage of 4.0 to 4.6V when 5-50% of total intercalation...http://www.google.com/patents/US20030138699?utm_source=gb-gplus-sharePatent US20030138699 - Positive active material for rechargeable lithium batteryAdvanced Patent SearchPublication numberUS20030138699 A1Publication typeApplicationApplication numberUS 10/264,043Publication dateJul 24, 2003Filing dateOct 3, 2002Priority dateJan 24, 2002Also published asCN1434527A, CN100426570C, US7309546Publication number10264043, 264043, US 2003/0138699 A1, US 2003/138699 A1, US 20030138699 A1, US 20030138699A1, US 2003138699 A1, US 2003138699A1, US-A1-20030138699, US-A1-2003138699, US2003/0138699A1, US2003/138699A1, US20030138699 A1, US20030138699A1, US2003138699 A1, US2003138699A1InventorsHo-jin Kweon, Jun-Won Suh, Kyung-Ho Kim, Hee-young SunOriginal AssigneeKweon Ho-Jin, Jun-Won Suh, Kyung-Ho Kim, Sun Hee-YoungExport CitationBiBTeX, EndNote, RefManReferenced by (9), Classifications (23), Legal Events (3) External Links: USPTO, USPTO Assignment, EspacenetPositive active material for rechargeable lithium batteryUS 20030138699 A1Abstract Disclosed is a positive active material for a rechargeable lithium battery, including a lithiated intercalation compound and an additive compound. The additive compound comprises one or more intercalation element-included oxides which have a charging voltage of 4.0 to 4.6V when 5-50% of total intercalation elements of the one or more intercalation element-included oxides are released during charging. Images(4) Claims(33)
What is claimed is: 1. A positive active material for a rechargeable lithium battery comprising: a lithiated intercalation compound and an additive compound, wherein the additive compound comprises one or more intercalation elementincluded oxides having a charging voltage of 4.0 to 4.6V when 5-50% of total intercalation elements of the one or more intercalation element-included oxides are released during charging. 2. The positive active material of claim 1 wherein the additive compound is MMn2-xNixO4, where M is Li or Na, and x ranges from 0.1 to 0.9. 3. The positive active material of claim 1 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.99 to 70:0.01 to 30. 4. The positive active material of claim 3 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound oxides ranges from 99.99 to 80:0.01 to 20. 5. The positive active material of claim 4 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.9 to 90:0.01 to 10. 6. The positive active material of claim 1 wherein the lithiated intercalation compound is at least one bare compound represented by the following formulas (1) to (12), or a surface-treated compound comprising a bare compound coated with metal oxide: LixMn1-yMyA2 (1) LixMn1-yMyO2-zXz (2) LixMn2O4-zXz (3) LixCo1-yMyA2 (4) LixCo1-yMyO2-zXz (5) LixNi1-yMyA2 (6) LixNi1-yMyO2-zXz (7) LixNi1-yCoyO2-zXz (8) LixNi1-y-zCoyMzAα (9) LixNi1-y-zCOyMzO2-αXα (10) LixNi1-y-zMnyMzAα (11) LixNi1-y-zMnyMzO2-αXα (12) wherein 0.90≦x≦1.1;0≦y≦0.5;0≦z≦0.5;0≦α≦2; M is selected from Al, Ni, Co, Mn, Cr, Fe, Mg, Sr, V, and rare earth elements; A is selected from O, F, S and P; and X is selected from F, S, and P. 7. The positive active material of claim 6 wherein the surface-treated compound is a compound with a metal oxide shell. 8. The positive active material of claim 7 wherein the metal oxide shell includes a metal selected from the group consisting of Mg, Al, Co, K, Na, Ca, Si, Ti, V, Sn, Ge, Ga, B, As, Zr, and mixtures thereof. 9. A positive active material for a rechargeable lithium battery comprising: a lithiated intercalation compound and an additive compound, wherein the additive compound comprises one or more intercalation element-included oxides having a discharging voltage of 4.0 to 5.0V when 5-50% of total intercalation elements of the one or more intercalation element-included oxides are released during discharging. 10. The positive active material of claim 9 wherein the additive compound is MMn2-xNixO4, where M is Li or Na, and x ranges from 0.1 to 0.9. 11. The positive active material of claim 9 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.99 to 70:0.01 to 30. 12. The positive active material of claim 11 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.99 to 80:0.01 to 20. 13. The positive active material of claim 12 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.9 to 90:0.1 to 10. 14. The positive active material of claim 13 wherein the lithiated intercalation compound is at least one bare compound represented by the following formulas (1) to (12), or a surface-treated compound comprising a bare compound coated with metal oxide: LixMn1-yMyA2 (1) LixMn1-yMyO2-zXz (2) LixMn2O4-zXz (3) LixCo1-yMyA2 (4) LixCo1-yMyO2-zXz (5) LixNi1-yMyA2 (6) LixNi1-yMyO2-zXz (7) LixNi1-yCoyO2-zXz (8) LixNi1-y-zCoyMzAα (9) LixNi1-y-zCOyMzO2-αXα (10) LixNi1-y-zMnyMzAα (11) LixNi1-y-zMnyMzO2-αXα (12) wherein 0.90≦x≦1.1;0≦y≦0.5;0≦z≦0.5;0≦α≦2; M is selected from Al, Ni, Co, Mn, Cr, Fe, Mg, Sr, V, and rare earth elements; A is selected from O, F, S and P; and X is selected from F, S, and P. 15. The positive active material of claim 14 wherein the surface-treated compound is a compound with a metal oxide shell. 16. The positive active material of claim 15 wherein the metal oxide shell includes a metal selected from the group consisting of Mg, Al, Co, K, Na, Ca, Si, Ti, V, Sn, Ge, Ga, B, As, Zr, and mixtures thereof. 17. A positive active material for a rechargeable lithium battery comprising: a lithiated intercalation compound and an additive compound, wherein the additive compound comprises one or more intercalation element-included oxides having two discharging plateaus during discharge. 18. The positive active material of claim 17 wherein the additive compound is MMn2-xNixO4, where M is Li or Na, and x ranges from 0.1 to 0.9. 19. The positive active material of claim 17 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.99 to 70:0.01 to 30. 20. The positive active material of claim 19 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound oxides ranges from 99.99 to 80:0.01 to 20. 21. The positive active material of claim 20 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.9 to 90:0.1 to 10. 22. The positive active material of claim 17 wherein the lithium-based compound is at least one bare compound represented by formulas (1) to (12), or a surface-treated compound comprising a bare compound coated with metal oxide: LixMn1-yMyA2 (1) LixMn1-yMyO2-zXz (2) LixMn2O4-zXz (3) LixCo1-yMyA2 (4) LixCo1-yMyO2-zXz (5) LixNi1-yMyA2 (6) LixNi1-yMyO2-zXz (7) LixNi1-yCoyO2-zXz (8) LixNi1-y-zCoyMzAα (9) LixNi1-y-zCOyMzO2-αXα (10) LixNi1-y-zMnyMzAα (11) LixNi1-y-zMnyMzO2-αXα (12) wherein 0.90≦x≦1.1;0≦y≦0.5;0≦z≦0.5;0≦α≦2; M is selected from Al, Ni, Co, Mn, Cr, Fe, Mg, Sr, V, and rare earth elements; A is selected from O, F, S and P; and X is selected from F, S, and P. 23. The positive active material of claim 22 wherein the surface-treated compound is a compound with a metal oxide shell. 24. The positive active material of claim 23 wherein the metal oxide shell includes a metal selected from the group consisting of Mg, Al, Co, K, Na, Ca, Si, Ti, V, Sn, Ge, Ga, B, As, Zr, and mixtures thereof. 25. A positive active material for a rechargeable lithium battery comprising: a lithiated intercalation compound: and an additive compound, wherein the additive compound comprises one or more intercalation element-included oxides prepared by mixing intercalation element sources, manganese sources and nickel sources to prepare a mixture; and heat-treating the mixture. 26. The positive active material of claim 25 wherein the additive compound is MMn2-xNixO4, where M is Li or Na, and x ranges from 0.1 to 0.9. 27. The positive active material of claim 25 wherein the heat-treating is performed at 600 to 1000� C. 28. The positive active material of claim 25 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.99 to 70:0.01 to 30. 29. The positive active material of claim 28 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.99 to 80:0.01 to 20. 30. The positive active material of claim 29 wherein the mixing weight ratio of the lithiated intercalation compound and the additive compound ranges from 99.9 to 90:0.1 to 10. 31. The positive active material of claim 25 wherein the lithiated intercalation compound is at least one bare compound represented by formulas (1) to (12), or a surface-treated compound comprises a bare compound coated with metal oxide: LixMn1-yMyA2 (1) LixMn1-yMyO2-zXz (2) LixMn2O4-zXz (3) LixCo1-yMyA2 (4) LixCo1-yMyO2-zXz (5) LixNi1-yMyA2 (6) LixNi1-yMyO2-zXz (7) LixNi1-yCoyO2-zXz (8) LixNi1-y-zCoyMzAα (9) LixNi1-y-zCOyMzO2-αXα (10) LixNi1-y-zMnyMzAα (11) LixNi1-y-zMnyMzO2-αXα (12) wherein 0.90≦x≦1.1;0≦y≦0.5;0≦z≦0.5;0≦α≦2; M is selected from Al, Ni, Co, Mn, Cr, Fe, Mg, Sr, V, and rare earth elements; A is selected from O, F, S and P; and X is selected from F, S, and P. 32. The positive active material of claim 31 wherein the surface-treated compound is a compound with a metal oxide shell. 33. The positive active material of claim 32 wherein the metal oxide shell includes a metal selected from the group consisting of Mg, Al, Co, K, Na, Ca, Si, Ti, V, Sn, Ge, Ga, B, As, Zr, and mixtures thereof.
CROSS REFERENCE TO RELATED APPLICATION [0001] This application claims priority to application No. 2002-4292, filed in the Korean Intellectual Property Office on Jan. 24, 2002, the disclosure of which is incorporated hereinto by reference. BACKGROUND OF THE INVENTION [0002] (a) Field of the Invention [0003] The present invention is directed to to a positive active material for a rechargeable lithium battery and, more particularly, to a positive active material for a rechargeable lithium battery exhibiting high capacity. [0004] (b) Description of the Related Art [0005] As the recent trend is toward more compact and lighter portable electronic equipment, the need has increased for a high performance and high capacity battery for electric power for portable electronic equipment. Especially with the forthcoming commercialization of IMT 2000 service, the demand for high capacity battery is greater than ever, and many battery manufacturers are already intensely researching high specific capacity batteries. [0006] In order to increase the specific capacity of a battery, either development of a high capacity positive active material or a more compact positive active material content is needed. [0007] For a high-capacity positive active material, LiCoO2 is widely used, and there is considerable desire to find a higher energy-density active material. One scheme to satisfy such a demand is to develop LiNixCoyO2 (where, x=0.1 to 0.99, and y=0.01 to 0.9) or LiNixMnyO2 (where, x=0.1 to 0.99, and y=0.01 to 0.9) compounds for the positive active material, which exhibit a higher discharge capacity than LiCoO2 by 20-30%. Another scheme is to increase the energy density per weight of the positive active material by using a nano composite compound of V or Fe. [0008] In order to increase the loading level of the positive active material in the given volume of the battery cell, a thin separator or a thin can may be used. Alternatively, the density of the active composite of the electrode can be increased to improve the volumetric energy density (Wh/Liter) of the battery cell. [0009] Although many advances have been made in the technology of positive active materials for batteries, the desire to further improve the charging and discharging capacity of the active materials led to continuous development of such materials. SUMMARY OF THE INVENTION [0010] The present invention is directed to a positive active material for a rechargeable lithium battery. According to an embodiment of the present invention, the positive active material includes a lithiated intercalation compound and an additive compound, wherein the additive compound comprises one or more intercalation element-included oxides having a charge voltage of 4.0 to 4.6V when 5-50% of total intercalation elements of the one or more intercalation element-included oxide are released during charging. [0011] According to another embodiment of the present invention, the positive active material includes a lithiated intercalation compound and an additive compound, wherein the additive compound comprises one or more intercalation element-included oxides having a discharge voltage of 4.0 to 5.0V when 5-50% of total intercalation elements of the one or more intercalation element-included oxides are released during discharging. [0012] According to still another embodiment of the present invention, the positive active material includes a lithiated intercalation compound and an additive compound, wherein the additive compound comprises one or more intercalation element-included oxides having two discharging plateaus within the voltage range of 4 to 5V during discharge. [0013] According to still another embodiment of the present invention, the mixed positive active material includes a lithiated intercalation compound and an additive compound, wherein the additive compound comprises one or more intercalation element-included oxides prepared by mixing intercalation element sources, manganese sources, and nickel sources to prepare a mixture and heat-treating the mixture.
BRIEF DESCRIPTION OF THE DRAWINGS [0014] A more complete appreciation of the invention, and many of the attendant advantages thereof, will be readily apparent as the same becomes better understood by reference to the following detailed description when considered in conjunction with the accompanying drawings, wherein: [0015]FIG. 1 is a graph showing charge and discharge characteristics of LiMn1 5Ni0 5O4 (B) prepared by a solid phase reaction according to the present invention, and LiMn1 5Ni0 5O4 (A) prepared by the conventional co-precipitation process; [0016]FIG. 2 is a graph showing charge and discharge characteristics of LiMn1 7Ni0 3O4 (a), LiMn1 2Ni0 8O4 (b), and LiMn1 5Ni0 5O4 (c) prepared by a solid phase reaction according to the present invention and LiCoO2 (d); [0017]FIG. 3 is a graph showing discharge voltage curves for standard capacities of prismatic cells according to Example 1 of the present invention and Comparative Example 2; and [0018]FIG. 4 is a graph showing discharge voltage curves for standard capacities of prismatic cells according to Example 4 of the present invention and Comparative Example 5.
DETAILED DESCRIPTION OF THE INVENTION [0019] The present invention relates to a positive active material for a rechargeable lithium battery exhibiting high capacity. The conventional research to accomplish a high-capacity positive active material has been focused on the synthesis of new active materials other than LiCoO2, which is widely used for positive active materials. The present invention improves the utilization of the conventional active material rather than synthesizing new active material. [0020] The amount of Li+ participating in electrochemical reactions at positive and negative electrodes is a critical factor for determining the capacity of a battery. That is, the capacity depends on the utilization of LiCoO2. Generally, it is known that only half (i.e. 0.5M) of the total Li+ in LiCoO2 participates in electrochemical reactions (4.2V to 2.75V). Thus, it is expected that if the utilization of LiCoO2 increases over 0.5 Li per LiCoO2, the capacity will improve over the state of the art. [0021] The present invention can increase the utilization of positive active materials simply by adding an additive compound to a lithiated compound used as the conventional active material. The additive compounds show a two-plateau charge-discharge voltage characteristic whereas the conventional active material, for example LiCoO2, shows a single-plateau charge-discharge voltage curve. Both charge and discharge voltages of the two-plateau curves of the additive compounds are higher than the corresponding plateau voltages of LiCoO2. The full-charge voltage for the lower voltage plateau of the additive compounds, for example, intercalation element-included oxides prepared by a solid phase synthesis method according to the present invention, is approximately 4.4V. An average discharge voltage for this plateau of the additive compounds is approximately 0.2V higher than that of the LiCoO2. The capacity of the lower voltage plateau of the additive compounds, intercalation element-included oxides, ranges from 10 to 40% of the theoretical capacity of the compounds for full lithium extraction. The compounds of similar compositions but prepared by a co-precipitation synthesis method showed only a minimal capacity, less than 10% of the theoretical capacity, for the lower voltage plateau. This latter compound does not improve the electrode capacity when it is used as an additive compound to the conventional active material of LiCoO2, whereas the additive compounds prepared by the solid phase method improved the electrode capacity significantly when they were used as additive compounds. [0022] The intercalation element-included oxides have a charge-discharge voltage of 4.0 to 4.6V when 5-50% of total intercalation elements of the intercalation element-included oxides are released during charging. [0023] Preferred intercalation element-included oxides are lithium-included oxides or sodium-included oxides. More preferred is an intercalation element-included manganese-based compound such as MMn2-xNixO4, where M is Li or Na, and x is 0.1 to 0.9. [0024] One example of the solid-phase reaction for this intercalation element-included manganese-based compound comprising manganese and nickel will be illustrated below in detail. [0025] An intercalation element source, a manganese source, and a nickel source are mixed together, and the resulting mixture is heat-treated. As a result, intercalation element-included oxides are prepared. [0026] The mixing ratio of the intercalation element source, the manganese source, and the nickel source may be controlled according to the desired composition. The heat-treating step is preferably performed at 600 to 1000� C. If the heat-treating temperature is less than 600� C., a crystalline material is not likely be formed. If the heat-treating temperature is more than 1000� C., Li is easily lost by evaporation due to to obtain unwanted material. [0027] Any compound that includes intercalation elements may be used as the intercalation element source, and exemplary thereof are lithium sources and sodium sources. The preferred intercalation element source is a lithium source. Exemplary sodium sources include sodium nitrate and sodium sulfate. Exemplary lithium sources include lithium hydroxide, lithium nitrate, and lithium acetate. [0028] Exemplary manganese source include manganese acetate and manganese dioxide, and exemplary nickel sources include nickel hydroxide, nickel nitrate, and nickel acetate. [0029] The positive active material of the present invention includes 99.99 to 70 wt %, preferably 99.99 to 80 wt %, and more preferably 99.9 to 90 wt %, of a lithiated intercalation compound, and 0.01 to 30 wt %, preferably 0.01 to 20 wt %, and more preferably 0.1 to 10 wt %, of the intercalation element-included oxides. If the amount of the intercalation element-included oxides is less than 0.01 wt %, the effect of the addition is not sufficiently high enough to show any changes in the capacity. On the other hand, if the amount of the intercalation element-included oxides is more than 30 wt %, the discharge capacity is reduced due to the added weight of the intercalation element-included oxide. [0030] The lithiated intercalation compound used in the present invention may be a bare compound represented in the following formulas (1) to (12), or a surface-treated compound, which is a bare compound coated with metal oxide. LixMn1-yMyA2 (1) LixMn1-yMyO2-zXz (2) LixMn2O4-zXz (3) LixCo1-yMyA2 (4) LixCo1-yMyO2-zXz (5) LixNi1-yMyA2 (6) LixNi1-yMyO2-zXz (7) LixNi1-yCoyO2-zXz (8) LixNi1-y-zCoyMzAα (9) LixNi1-y-zCOyMzO2-αXα (10) LixNi1-y-zMnyMzAα (11) LixNi1-y-zMnyMzO2-αXα (12) [0031] wherein [0032] 0.90≦x≦1.1;0≦y≦0.5;0≦z≦0.5;0≦α≦2; [0033] M is selected from Al, Ni, Co, Mn, Cr, Fe, Mg, Sr, V, and rare earth elements; [0034] A is selected from O, F, S and P; and [0035] X is selected from F, S, and P. [0036] The surface-treated compound is a compound coated with metal oxide. The surface-treated compound can be prepared by the procedures described in Korean Patent Application No. 98-42956, the disclosure of which is incorporated herein by reference. These procedures include coating the bare compound with an organic liquid or an aqueous liquid of a coating material source, and heat-treating it. The liquid may be in the form of a suspension or solution. The coating material source can be a coating element or a coating element-included alkoxide, salt, or oxide. Suitable coating material sources may be chosen from coating elements, and coating element-included alkoxides, salts, and oxides according to the type of the solvent, which is well known to one skilled in the related arts. For example, if an organic solvent is used for the solvent, then the coating element or the coating element-included alkoxide, salt, or oxide may be used for the coating material source, and if water is used for the solvent, then the coating element-included salt or oxide may be used for the coating material source. [0037] The coating element in the coating material source may be any element that is capable of being dissolved in an organic solvent or water. Examples are Mg, Al, Co, K, Na, Ca, Si, Ti, V, Sn, Ge, Ga, B, As, Zr, and mixtures thereof. Useful organic solvents include hexane, chloroform, tetrahydrofuran, ether, methylene chloride, acetone, and alcohol, such as methanol, ethanol or isopropanol. [0038] An exemplary organic liquid is a coating element-included alkoxide liquid. The alkoxide liquid may be prepared by adding the coating element to an alcohol such as methanol, ethanol or isopropanol, and refluxing them, or by adding a coating element-included alkoxide such as methoxide, ethoxide, or isopropoxide to alcohol. The organic liquid or aqueous liquid may also be available through commercial purchase. [0039] The following examples illustrate the present invention in further detail. However, it is understood that the present invention is not limited by these examples. COMPARATIVE EXAMPLE 1 [0040] A prismatic cell with a capacity of 950 mAh was fabricated using a surface-treated LiCoO2 positive active material. The surface-treated LiCoO2 was prepared by coating LiCoO2 with an Al-isopropoxide suspension and heat-treating it at 600� C. according to the procedure described in Korean Patent Application No. 98-42956. The negative active material used was an artificial graphite material, PHS, available from Japan Carbon Ltd., and the electrolyte used was a 1M LiPF6 solution in a mixture of ethylene carbonate, dimethyl carbonate, diethyl carbonate and fluorobenzene (3:5:1:1 volume ratio). [0041] A formation cycle of the prismatic cell was then performed at a 0.2C rate for both charge and discharge. The cell was then charged 4.2V at 0.2C rate and discharged to 2.75V at 0.5C rate for a standard capacity measurement. In addition, the cycle life characteristics tests and safety test (1C overcharging) were performed. COMPARATIVE EXAMPLE 2 [0042] A prismatic cell was fabricated by the same procedure as in Comparative Example 1 except that the positive active material was a mixture of 99 wt % of the surface-treated LiCoO2 and 1 wt % of LiMn1 5Ni0 5O4 which was obtained from a co-precipitation process. [0043] The co-precipitation process for preparing LiMn1 5Ni0 5O4 was performed as follows: MnSO4 and NiSO4 were dissolved in water to prepare an aqueous solution containing Mn and Ni ions in the ratio of 3:1. NH4(OH)2 was added to the solution to co-precipitate Mn and Ni ions to obtain Mn0 75Ni0 25(OH)2. The subsequently dried Mn0 75Ni0 25(OH)2 was mixed with LiOH followed by heat-treating at 450� C. to prepare LiMn1 5Ni0.5O4. The resultant material, LiMn1 5Ni0 5O4, will be referred to as �co-precipitated LiMn1 5Ni0 5O4�. COMPARATIVE EXAMPLE 3 [0044] A prismatic cell was fabricated by the same procedure as in Comparative Example 1, except that the positive active material was a mixture of 97 wt % of the surface-treated LiCoO2 and 3 wt % of co-precipitated LiMn1 5Ni0 5O4. COMPARATIVE EXAMPLE 4 [0045] A prismatic cell was fabricated by the same procedure as in Comparative Example 1, except that the positive active material was a mixture of 95 wt % of the surface-treated LiCoO2 and 5 wt % of co-precipitated LiMn1 5Ni0 5O4. COMPARATIVE EXAMPLE 5 [0046] A prismatic cell was fabricated by the same procedure as in Comparative Example 1, except that the positive active material was a mixture of 90 wt % of the surface-treated LiCoO2 and 10 wt % of co-precipitated LiMn1 5Ni0 5O4. COMPARATIVE EXAMPLE 6 [0047] A prismatic cell was fabricated by the same procedure as in Comparative Example 1, except that the positive active material was a mixture of 85 wt % of the surface-treated LiCoO2 and 15 wt % of co-precipitated LiMn1 5Ni0 5O4. COMPARATIVE EXAMPLE 7 [0048] A prismatic cell was fabricated by the same procedure as in Comparative Example 1, except that the positive active material was a mixture of 80 wt % of the surface-treated LiCoO2 and 20 wt % of co-precipitated LiMn1 5Ni0 5O4. COMPARATIVE EXAMPLE 8 [0049] A prismatic cell was fabricated by the same procedure as in Comparative Example 1, except that the positive active material was a mixture of 99 wt % of a surface-treated LiMn2O4 and 1 wt % of co-precipitated LiMn1 5Ni0 5O4. The surface-treated LiMn2O4 was prepared by coating LiMn2O4 with an Al-isopropoxide suspension and heat-treating them at 300� C. according to the procedure as shown in Korean Patent Application No. 98-42956. COMPARATIVE EXAMPLE 9 [0050] A prismatic cell was fabricated by the same procedure as in Comparative Example 8, except that the positive active material was a mixture of 90 wt % of the 10 surface-treated LiMn2O4 and 10 wt % of co-precipitated LiMn1 5Ni0 5O4. COMPARATIVE EXAMPLE 10 [0051] A prismatic cell was fabricated by the same procedure as in Comparative Example 1, except that the positive active material was a mixture of 99 wt % of a surface-treated LiNi0 9Co0 1Sr0 002O2 and 1 wt % of co-precipitated LiMn1 5Ni0.5O4. The surface-treated LiNi0 9Co0 1Sr0.002O2 was prepared by coating LiNi0 9Co0 1Sr0 002O2 with an Al-isopropoxide suspension and heat-treating them at 500� C. according to the procedure described in Korean Patent Application No. 98-42956. COMPARATIVE EXAMPLE 11 [0052] A prismatic cell was fabricated by the same procedure as in Comparative Example 10, except that the positive active material was a mixture of 90 wt % of the surface-treated LiNi0 9Co0 1Sr0 002O2 and 10 wt % of co-precipitated LiMn1 5Ni0 5O4. COMPARATIVE EXAMPLE 12 [0053] A prismatic cell was fabricated by the same procedure as in Comparative Example 10, except that the positive active material was a mixture of 99 wt % of LiNi0 68Mn0 2Co0 1Mg0.01Al0 01O2 and 1 wt % of co-precipitated LiMn1 5Ni0 5O4. COMPARATIVE EXAMPLE 13 [0054] A prismatic cell was fabricated by the same procedure as in Comparative Example 10, except that the positive active material was a mixture of 90 wt % of LiNi0 68Mn0 2Co0 1Mg0 01Al0 01O2 and 10 wt % of co-precipitated LiMn1 5Ni0 5O4. EXAMPLE 1 [0055] 99 weight percent (wt %) of �surface-treated LiCoO2�, which was coated with an Al-isopropoxide suspension and heat-treated at 600� C. as described in Korean Patent Application No. 98-42956, was mixed with 1 weight portion of a LiMn1 5Ni0 5O4 compound, which was synthesized via a solid phase reaction to prepare a positive active material. The solid phase reaction was performed by the following method. LiOH, MnO2, and NiO2 were mixed well in the mole ratio of 1:1.5:0.5. The resulting mixture was heat-treated at 800� C. to prepare the LiMn1 5Ni0 5O4 compound, which will be referred to as �solid phase-LiMn1 5Ni0 5O4�. [0056] The positive active material, a polyvinylidene fluoride binder, and a carbon conductive agent were mixed in an N-methylpyrrolidone solvent to prepare a positive active material slurry. The mixing ratio of the positive active material, the binder, and the conductive agent was 94:3:3 by weight. Using the slurry, a positive electrode was produced by the conventional coating process. A negative electrode was produced by using an artificial graphite material, PHS, available from Japan Carbon Ltd., as a negative active material. With the positive electrode, the negative electrode, and an electrolyte, a 653450-prismatic cell with a nominal capacity of 950 mAh was fabricated. The electrolyte used was 1 M LiPF6 in a mixture of ethylene carbonate, dimethyl carbonate, diethyl carbonate, and fluorobenzene. The formation of the prismatic cell was performed by charging and discharging at a 0.2C rate using cut-off voltages of 4.2 and 2.75V. The resulting cell was charged at 0.2C and discharged at 0.5C rate for a standard capacity measurement. The cycle life characteristics and a safety test (1C overcharge) were also performed. EXAMPLE 2 [0057] A prismatic cell was fabricated by the same procedure as in Example 1, except that the positive active material was a mixture of 97 wt % of the surface-treated LiCoO2 and 3 wt % of solid-phase LiMn1 5Ni0 5O4. EXAMPLE 3 [0058] A prismatic cell was fabricated by the same procedure as in Example 1, except that the positive active material was a mixture of 95 wt % of the surface-treated LiCoO2 and 5 wt % of solid-phase LiMn1 5NiO0 5O4. EXAMPLE 4 [0059] A prismatic cell was fabricated by the same procedure as in Example 1, except that the positive active material was a mixture of 90 wt % of the surface-treated LiCoO2 and 10 wt % of solid-phase LiMn1 5Ni0 5O4. EXAMPLE 5 [0060] A prismatic cell was fabricated by the same procedure as in Example 1, except that 80 wt % of the surface-treated LiCoO2 was mixed with 20 wt % of solid-phase LiMn1 5Ni0 5O4 to prepare a positive active material. EXAMPLE 6 [0061] LiOH, MnO2, and NiO2 were mixed in the mole ratio of 1:1.7:0.3, and the mixture was heat-treated at 800� C. to prepare solid-phase LiMn1 7Ni0 3O4. 10 wt % of the solid-phase LiMn1 7Ni0 3O4 as an additive compound was mixed with 90 wt % of the surface-treated LiCoO2 to prepare a positive active material. Using the positive active material, a prismatic cell was fabricated by the same procedure as in Example 1. EXAMPLE 7 [0062] LiOH, MnO2 and NiO2 were mixed in the mole ratio of 1:1.2:0.8, and the mixture was heat-treated at 800� C. to prepare solid-phase LiMn1 2Ni0 8O4. 10 wt % of the solid-phase LiMn1 2Ni0 8O4 as an additive compound was mixed with 90 wt % of the surface-treated LiCoO2 to prepare a positive active material. Using the positive active material, a prismatic cell was fabricated by the same procedure as in Example 1. EXAMPLE 8 [0063] A prismatic cell was fabricated by the same procedure as in Example 1, except that the positive active material was a mixture of 99 wt % of the surface-treated LiCoO2 and 1 wt % of the solid-phase LiMn1.5Ni0 5O4. The solid-phase LiMn1 5Ni0 5O4 was prepared by the same procedure as in Example 1, except that the heat-treatment was performed at 900� C. EXAMPLE 9 [0064] A prismatic cell was fabricated by the same procedure as in Example 8, except that the positive active material was a mixture of 90 wt % of the surface-treated LiCoO2 and 10 wt % of the solid-phase LiMn1 5Ni0 5O4. EXAMPLE 10 [0065] A prismatic cell was fabricated by the same procedure as in Example 1, except that the positive active material was a mixture of 99 wt % of the surface-treated LiCoO2 and 1 wt % of the solid-phase LiMn1 5Ni0 5O4. The solid-phase LiMn1.5Ni0 5O4 was prepared by the same procedure as in Example 1, except that the heat-treatment was performed at 700� C. EXAMPLE 11 [0066] A prismatic cell was fabricated by the same procedure as in Example 10, except that the positive active material was a mixture of 90 wt % of the surface-treated LiCoO2 and 10 wt % of the solid-phase LiMn1 5Ni0.5O4. EXAMPLE 12 [0067] A prismatic cell was fabricated by the same procedure as in Example 1, except that the positive active material was a mixture of 99 wt % of a surface-treated LiMn2O4 and 1 wt % of the solid-phase LiMn1.5Ni0 5O4. The surface-treated LiMn2O4 was prepared by coating with an Al-isopropoxide suspension and heat-treating it at 800� C., according to the procedure described in Korean Patent Application No. 98-42956. [0068] Using the positive active material, a prismatic cell was fabricated by the same procedure as in Example 1. EXAMPLE 13 [0069] A prismatic cell was fabricated by the same procedure as in Example 12, except that the positive active material was a mixture of 90 wt % of the surface-treated LiMn2O4 and 10 wt % of the solid-phase LiMn1 5Ni0 5O4. EXAMPLE 14 [0070] A prismatic cell was fabricated by the same procedure as in Example 1, except that the positive active material was a mixture of 99 wt % of a surface-treated LiNi0 9Co0 1Sr0 002O2 and 1 wt % of solid-phase LiMn1 5Ni0.5O4. The surface-treated LiNi0 9Co0 1Sr0 002O2was prepared by coating with an Al-isopropoxide suspension and heat-treating it at 800� C., according to the procedure described in Korean Patent Application No. 98-42956. The solid-phase LiMn1 5Ni0 5O4 was prepared by the same procedure as in Example 1. [0071] Using the positive active material, a prismatic cell was fabricated by the same procedure as in Example 1. EXAMPLE 15 [0072] A prismatic cell was fabricated by the same procedure as in Example 14, except that 90 wt % of the surface-treated LiNi0.9Co0 1Sr0.002O2 was mixed with 10 wt % of the solid-phase LiMn1 5Ni0 5O4 to prepare a positive active material. EXAMPLE 16 [0073] A prismatic cell was fabricated by the same procedure as in Example 1, except that 99 wt % of a surface-treated LiNi0 68Mn0 2Co0.1Mg0 01Al0 01O2was mixed with 1 wt % of the solid-phase LiMn1 5Ni0 5O4 to prepare a positive active material. The surface-treated LiNi0 68Mn0 2Co0 1Mg0 01Al0 01O2was prepared by coating with an Al-isopropoxide suspension and heat-treating it at 800� C., according to the procedure described in Korean Patent Application No. 98-42956. [0074] Using the positive active material, a prismatic cell was fabricated by the same procedure as in Example 1. EXAMPLE 17 [0075] A prismatic cell was fabricated by the same procedure as in Example 1, except that 90 wt % of the surface treated LiNi0 68Mn0 2Co0 1Mg0 01Al0 01O2was mixed with 10 wt % of the solid-phase LiMn1.5Ni0 5O4 to prepare a positive active material. [0076] The standard capacities of the prismatic cells according to Examples 1 and 4 having theoretical capacities of 950 mAh and 930 mAh, respectively, were measured. The measurement capacities were 999 mAh and 996 mAh, respectively. Thus, the cells according to Examples 1 and 4 exhibited higher than the theoretical capacities by about 50 and 70 mAh, respectively. [0077] Furthermore, in order to identify the effect on the battery performance by type of the additive compound preparation, the charge and discharge characteristics at 0.1C of solid phase-LiMn1 5Ni0 5O4 (B) (additive compound used in Example 1) and co-precipitated LiMn1 5Ni0 5O4 (A) (additive compound used in Comparative Example 2) were measured. The results are presented in FIG. 1. It is evident from FIG. 1 that the charge and discharge curve of the solid phase-LiMn1 5Ni0 5O4 has a sharp slope and two charge and discharge plateaus. In addition, the solid phase-LiMn1.5Ni0 5O4 exhibited a substantial portion of total capacity at potentials between about 3.9 and 4.3V, whereas the co-precipitated LiMn1.5Ni0 5O4 exhibited only a slight portion of the capacity in this potential. The co-precipitated LiMn1.5Ni0 5O4 was prepared by forming a Mn0 75Ni0 25(OH)2 co-precipitation product and mixing the product with LiOH followed by a heat-treatment. [0078] In addition, to evaluate the effect of the additive composition, the charge and discharge characteristic of LiMn2-xNixO4 while varying the value of x, was measured, and the results are presented in FIG. 2. For a control reference, the charge and discharge characteristics of LiCoO2 is also presented in FIG. 2. In FIG. 2, �a� refers to LiMn1.7Ni0 3O4 (additive compound used in Example 6), �b� refers to LiMn1 2Ni0 8O4 (additive compound used in Example 7), �c� refers to LiMn1.5Ni0 5O4 (additive compound used in Example 1) and �d� refers to LiCoO2. As shown in FIG. 2, the charge and discharge characteristic of LiMn2-xNixO4 is significantly different from that of LiCoO2. The charge and discharge characteristics vary according to the value of x (i.e. the ratio between Mn and Ni). [0079]FIG. 3 shows the discharge voltage curves for the standard capacity measurement of the prismatic cells according to Example 1 and Comparative Example 2. FIG. 4 shows those of the prismatic cells according to Example 4 and Comparative Example 5. It can be seen from FIGS. 3 and 4 that the cell according to Example 1 had a capacity of about 999 mAh, and the cell according to Example 4 had about 996 mAh. However, the cell according to Comparative Example 2 had a capacity of about 900 mAh, and the cell according to Comparative Example 5 had a capacity of about 910 mAh. That is, the cells according to Examples 1 and 4 had surprisingly higher capacities than those of Comparative Examples 1 and 5. From these results, it is believed that the positive active material of the present invention provides a high-capacity rechargeable lithium battery. [0080] While the present invention has been described in detail with reference to the preferred embodiments, those skilled in the art will appreciate that various modifications and substitutions can be made thereto without departing from the spirit and scope of the present invention as set forth in the appended claims. Referenced byCiting PatentFiling datePublication dateApplicantTitleUS7238450Dec 23, 2003Jul 3, 2007Tronox LlcIntercalation cathode materials especially suited for use in high-voltage, high-energy lithium rechargeable batteries, having the formulae Li[Li(1-2x)/3MyMn(2-x)/3Ni(x-y)O2, where 0<x<0.5, 0<y and = or less than 0.25, and M is a divalent Ca, Cu, Mg, and/or Zn cationUS7656125Jul 14, 2006Feb 2, 2010Boston-Power, Inc.Method and device for controlling a storage voltage of a battery packUS7807298Nov 10, 2004Oct 5, 2010Panasonic CorporationNon-aqueous electrolyte secondary battery with laminated separatorUS7811707Jul 12, 2006Oct 12, 2010Boston-Power, Inc.Cathode active material includes a mixture of lithium cobaltate and a manganate spinel containing oxides of lithium , manganese and one or more oxide(s)selected from magnesium, aluminum, cobalt, nickel and chromium; large batteriesUS7811708Dec 22, 2008Oct 12, 2010Boston-Power, Inc.Cathode active material includes a mixture of lithium cobaltate and a manganate spinel containing oxides of lithium , manganese and one or more oxide(s)selected from magnesium, aluminum, cobalt, nickel and chromium; large batteriesUS8067119May 18, 2007Nov 29, 2011Panasonic CorporationNon-aqueous electrolyte secondary batteryUS8084998Dec 31, 2009Dec 27, 2011Boston-Power, Inc.Method and device for controlling a storage voltage of a battery packUS8138726Oct 18, 2010Mar 20, 2012Boston-Power, Inc.Electronics with multiple charge rateUS8483886Aug 31, 2010Jul 9, 2013Boston-Power, Inc.Large scale battery systems and method of assemblyClassifications U.S. Classification429/231.95, 429/231.9, 429/224, 429/223, 429/231.1, 429/231.3, 252/182.1International ClassificationH01M10/05, H01M4/36, H01M4/505, H01M4/58, H01M4/525, H01M4/02, C01G53/00, H01M4/62Cooperative ClassificationH01M4/525, Y02E60/122, H01M10/052, H01M4/364, H01M4/505European ClassificationH01M4/505, H01M4/525, H01M4/36K1Legal EventsDateCodeEventDescriptionMar 29, 2011FPAYFee paymentYear of fee payment: 4Oct 28, 2008CCCertificate of correctionOct 3, 2002ASAssignmentOwner name: SAMSUNG SDI CO., LTD., KOREA, REPUBLIC OFFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KWEON, HO-JIN;SUH, JUN-WON;KIM, KYUNG-HO;AND OTHERS;REEL/FRAME:013365/0909Effective date: 20020925RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services©2012 Google