Patent US5874885 - Electrical devices containing conductive polymers - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsAn electrical device (1) in which an element (7) composed of a conductive polymer is positioned in contact with the surface layer of one or more metal electrodes (3,5). The metal electrode contains a base layer (9) which comprises a first metal, an intermediate metal layer (15) which comprises a metal...http://www.google.com/patents/US5874885?utm_source=gb-gplus-sharePatent US5874885 - Electrical devices containing conductive polymersAdvanced Patent SearchPublication numberUS5874885 APublication typeGrantApplication numberUS 08/750,294PCT numberPCT/US1995/007888Publication dateFeb 23, 1999Filing dateJun 7, 1995Priority dateJun 8, 1994Fee statusPaidAlso published asCA2192363A1, CA2192363C, CN1078381C, CN1149928A, DE69513656D1, DE69513656T2, DE69533562D1, DE69533562T2, EP0764333A1, EP0764333B1, EP0952590A2, EP0952590A3, EP0952590B1, US6570483, WO1995034081A1Publication number08750294, 750294, PCT/1995/7888, PCT/US/1995/007888, PCT/US/1995/07888, PCT/US/95/007888, PCT/US/95/07888, PCT/US1995/007888, PCT/US1995/07888, PCT/US1995007888, PCT/US199507888, PCT/US95/007888, PCT/US95/07888, PCT/US95007888, PCT/US9507888, US 5874885 A, US 5874885A, US-A-5874885, US5874885 A, US5874885AInventorsDaniel A. Chandler, Martin Matthiesen, Derek Leong, Matthew P. GallaOriginal AssigneeRaychem CorporationExport CitationBiBTeX, EndNote, RefManPatent Citations (40), Non-Patent Citations (16), Referenced by (55), Classifications (13), Legal Events (7) External Links: USPTO, USPTO Assignment, EspacenetElectrical devices containing conductive polymers
US 5874885 AAbstract
An electrical device (1) in which an element (7) composed of a conductive polymer is positioned in contact with the surface layer of one or more metal electrodes (3,5). The metal electrode contains a base layer (9) which comprises a first metal, an intermediate metal layer (15) which comprises a metal that is different from the first metal, and a surface layer (17) which (i) comprises a second metal, (ii) has a center line average roughness Ra of at least 1.3, and (iii) has a reflection density Rd of at least 0.60. The conductive polymer composition preferably exhibits PTC behavior. The electrical devices, which may be, for example, circuit protection devices or heaters, have improved thermal and electrical performance over devices prepared with electrodes which do not meet the center line average roughness and reflection density requirements.
1. An electrical device (1) which comprises(A) an element (7) composed of a conductive polymer; and (B) at least one metal foil electrode (3) which(1) comprises(a) a base layer (9) which (i) comprises a first metal, and (ii) has been prepared by rolling, (b) an intermediate metal layer (15) which (i) is positioned between the base layer (9) and a surface layer (17), and (ii) comprises a metal which is different from the first metal, and (c) a surface layer (17) which (i) consists essentially of a second metal, (ii) has a center line average roughness Ra of at least 1.6, and (iii) has a reflection density Rd of at least 0.81, and (2) is positioned so that the surface layer (17) is in direct physical contact with the conductive polymer element (7). 2. A device according to claim 1 wherein the first metal is copper.
3. A device according to claim 2 wherein the second metal is nickel.
4. A device according to claim 1 wherein the second metal is nickel.
5. A device according to claim 1 wherein the metal in the intermediate layer (15) is the same as the metal in the surface layer (17).
6. A device according to claim 1 wherein Ra is at most 2.5.
7. A device according to claim 1 wherein the base layer (9) has a surface which (a) has a center line average roughness Ra of less than 1.0, and (b) contacts the intermediate layer.
8. A device according to claim 1 wherein the conductive polymer (a) exhibits PTC behavior, and (b) comprises a polyolefin or a fluoropolymer, and dispersed therein, a particulate conductive filler.
9. A device according to claim 1, further comprising a second metal foil electrode, wherein said conductive polymer element is sandwiched between said at least one metal foil electrode and said second metal foil electrode.
10. A device according to claim 9 wherein the device is a circuit protection device which has a resistance of less than 50 ohms.
11. A device according to claim 9 wherein the device is a heater which has a resistance of at least 100 ohms.
12. A device according to claim 1 wherein the surface layer (17) is composed of nodules (11), each of which is composed of a number of smaller nodules.
13. An electrical circuit which comprises(A) a source of electrical power; (B) a load; and (C) a circuit protection device according to claim 1 connecting said source and load. 14. A circuit according to claim 13 wherein the device has a resistance of less than 50 ohms.
15. A circuit according to claim 14 wherein the device has a resistance of less than 10 ohms.
16. A circuit according to claim 15 wherein the device has a resistance of less than 1 ohm.
17. A device according to claim 1 wherein the first metal is nickel.
This application draws priority from commonly assigned International Application No. PCT/US95/07888, filed Jun. 7, 1995, published as WO95/34081 Dec. 14, 1995, which is a continuation-in-part of commonly assigned application Ser. No. 08/255,584, filed Jun. 8, 1994, now abandoned. This application is also related to copending, commonly assigned U.S. application Ser. No. 08/672,496, filed Jun. 28, 1996 now abandoned, which is a continuation of application Ser. No. 08/255,584, filed Jun. 8, 1994, now abandoned. The disclosure of each of these applications is incorporated herein by reference.
This invention relates to electrical devices comprising conductive polymer compositions and to circuits comprising such devices.
Electrical devices comprising conductive polymer compositions are well-known. Such devices comprise an element composed of a conductive polymer. The element is physically and electrically connected to at least one electrode suitable for attachment to a source of electrical power. Those factors determining the type of electrode used include the specific application, the configuration of the device, the surface to which the device is to be attached, and the nature of the conductive polymer. Among those types of electrodes which have been used are solid and stranded wires, metal foils, perforated and expanded metal sheets, and conductive inks and paints. When the conductive polymer element is in the form of a sheet or laminar element, metal foil electrodes which are directly attached to the surface of the conductive polymer, sandwiching the element, are particularly preferred. Examples of such devices are found in U.S. Pat. Nos. 4,426,633 (Taylor), 4,689,475 (Matthiesen), 4,800,253 (Kleiner et al), 4,857,880 (Au et al), 4,907,340 (Fang et al), and 4,924,074 (Fang et al), the disclosures of which are incorporated herein by reference.
As disclosed in U.S. Pat. Nos. 4,689,475 (Matthiesen) and 4,800,253 (Kleiner et al), microrough metal foils having certain characteristics give excellent results when used as electrodes in contact with conductive polymers. Thus U.S. Pat. No. 4,689,475 discloses the use of metal foilswhich have surface irregularities, e.g. nodules, which protrude from the surface by 0.1 to 100 microns and have at least one dimension parallel to the surface which is at most 100 microns, and U.S. Pat. No. 4,800,253 discloses the use of metal foils with a microrough surface which comprises macronodules which themselves comprise micronodules. Other documents which disclose the use of metal foils having rough surfaces, but which do not disclose the characteristics of the foils disclosed in U.S. Pat. Nos. 4,689,475 and 4,800,253, are Japanese Patent Kokai No. 62-113402 (Murata, 1987), Japanese Patent Kokoku H4-18681 (Idemitsu Kosan, 1992), and German Patent Application No. 3707494A (Nippon Mektron Ltd). The disclosure of each of these U.S., Japanese, and German documents is incorporated herein by reference.
We have found that still better results for electrodes which are in contact with a conductive polymer can be obtained by using rough-surfaces metal foils having one or both of two characteristics which are not found in the metal foils which have been used, or proposed for use, in the past. These characteristics are
(1) The protrusions from the surface of the foil should have a certain minimum average height (and preferably a certain maximum average height), as expressed by a value known as the "center line average roughness", whose measurement is described below. In addition, the protrusions from the surface of the foil have a certain minimum irregularity (or "structure"), as expressed by a value known as the "reflection density", whose measurement is also described below.
(2) The base of the foil comprises a first metal and the protrusions from the surface of the foil comprise a second metal. The first metal is selected to have high thermal and electrical conductivity, and is preferably easily manufactured at a relatively low cost. In addition, the first metal is often more likely to cause degradation of the conductive polymer than the second metal. Fracture of the protrusions, caused by thermal cycling of the device, and/or thermal diffusion of the metals at elevated temperature, exposes the second metal rather than the first metal.
Characteristic (1) is believed to be important because it ensures that the conductive polymer penetrates into the surface of the foil sufficiently to provide a good mechanical bond. However, if the height of the protrusions is too great, the polymer will not completely fill the crevices between the protrusions, leaving an air gap which will result in accelerated aging of the conductive polymer and/or more rapid corrosion of the polymer/metal interface surrounding the air gap. Characteristic (2) is based upon our discovery that thermal cycling of the device will cause fracture of some of the protrusions as a result of the different thermal expansion characteristics of the conductive polymer and the foil, so that it is important that such fracture does not expose the conductive polymer to a metal which will promote polymer degradation. In addition, it is important that a sufficient thickness of the second metal be in contact with the conductive polymer so that even if the first metal diffuses into the second metal at elevated temperature, there is little chance that the first metal will contact the conductive polymer.
In a first aspect, this invention discloses an electrical device which comprises
(A) an element composed of a conductive polymer; and
(B) at least one metal foil electrode which
(a) a base layer which comprises a first metal,
(b) an intermediate metal layer which (i) is positioned between the base layer and a surface layer, and (ii) comprises a metal which is different from the first metal, and
(c) a surface layer which (i) comprises a second metal, (ii) has a center line average roughness Ra of at least 1.3, and (iii) has a reflection density Rd of at least 0.60, and
(2) is positioned so that the surface layer is in direct physical contact with the conductive polymer element.
In a second aspect, this invention provides a circuit protection device which comprises
(A) an element composed of a conductive polymer which exhibits PTC behavior; and
(B) two metal foil electrodes positioned on opposite sides of the conductive polymer element, each of which electrodes comprises
(1) a base layer which comprises copper,
(2) an intermediate layer which (a) is adjacent to the base layer and (b) comprises nickel, and
(3) a surface layer which (a) comprises nickel, (b) has a center line average roughness Ra of at least 1.3 and at most 2.5, (c) has a reflection density Rd of at least 0.60, and (d) is in direct physical contact with the conductive polymer element.
In a third aspect, this invention provides an electrical circuit which comprises
(B) a load; and
(C) an electrical device, e.g. a circuit protection device, of the first aspect of the invention.
FIG. 1 shows a plan view of a device of the invention;
FIG. 2 shows a cross-sectional schematic view of a conventional metal foil; and
FIG. 3 shows a cross-sectional schematic view of a metal foil used in devices of the invention.
Electrical devices of the invention are prepared from an element composed of a conductive polymer composition. The conductive polymer composition is one in which a particulate conductive filler is dispersed or distributed in a polymeric component. The composition generally exhibits positive temperature coefficient (PTC) behavior, i.e. it shows a sharp increase in resistivity with temperature over a relatively small temperature range, although for some applications, the composition may exhibit zero temperature coefficient (ZTC) behavior. In this specification, the term "PTC" is used to mean a composition or device which has an R14 value of at least 2.5 and/or an R100 value of at least 10, and it is preferred that the composition or device should have an R30 value of at least 6, where R14 is the ratio of the resistivities at the end and the beginning of a 14� C. range, R100 is the ratio of the resistivities at the end and the beginning of a 100� C. range, and R30 is the ratio of the resistivities, at the end and the beginning of a 30� C. range. Generally the compositions used in devices of the invention which exhibit PTC behavior show increases in resistivity which are much greater than those minimum values.
The polymeric component of the composition is preferably a crystalline organic polymers Suitable crystalline polymers include polymers of one or more olefins, particularly poly ethylene; copolymers of at least one olefin and at least one monomer copolymerisable therewith such as ethylene/acrylic acid, ethylene/ethyl acrylate, ethylene/vinyl acetate, and ethylene/butyl acrylate copolymers; melt-shapeable fluoropolymers such as polyvinylidene fluoride and ethylene/tetrafluoroethylene copolymers (including terpolymers); and blends of two or more such polymers. For some applications it may be desirable to blend one crystalline polymer with another polymer, e.g. an elastomer, an amorphous thermoplastic polymer, or another crystalline polymer, in order to achieve specific physical or thermal properties, e.g. flexibility or maximum exposure temperature. Electrical devices of the invention are particularly useful when the conductive polymer composition comprises a polyolefin because of the difficulty of bonding conventional metal foil electrodes to nonpolar polyolefins. For applications in which the composition is used in a circuit protection device, it is preferred that the crystalline polymer comprise polyethylene, particularly high density polyethylene, and/or an ethylene copolymer. The polymeric component generally comprises 40 to 90% by volume, preferably 45 to 80% by volume, especially 50 to 75% by volume of the total volume of the composition.
The particulate conductive filler which is dispersed in the polymeric component may be any suitable material, including carbon black, graphite, metal, metal oxide, conductive coated glass or ceramic beads, particulate conductive polymer, or a combination of these. The filler may be in the form of powder, beads, flakes, fibers, or any other suitable shape. The quantity of conductive filler needed is based on the required resistivity of the composition and the resistivity of the conductive filler itself. For many compositions the conductive filler comprises 10 to 60% by volume, preferably 20 to 55% by volume, especially 25 to 50% by volume of the total volume of the composition. When used for circuit protection devices, the conductive polymer composition has a resistivity at 20� C., ρ20, of less than 10 ohm-cm, preferably less than 7 ohm-cm, particularly less than 5 ohm-cm, especially less than 3 ohm-cm, e.g. 0.005 to 2 ohm-cm. When the electrical device is a heater, the resistivity of the conductive polymer composition is preferably higher, e.g. 102 to 105 ohm-cm, preferably 102 to 104 ohm-cm.
The conductive polymer composition may comprise additional components, such as antioxidants, inert fillers, nonconductive fillers, radiation crosslinking agents (often referred to as prorads or crosslinking enhancers), stabilizers, dispersing agents, coupling agents, acid scavengers (e.g. CaCO3), or other components. These components generally comprise at most 20% by volume of the total composition.
Dispersion of the conductive filler and other components may be achieved by meltprocessing, solvent-mixing, or any other suitable means of mixing. Following mixing the composition can be melt-shaped by any suitable method to produce the element. Suitable methods include may be melt-extruding, injection-molding, compression-molding, and sintering. For many applications, it is desirable that the compound be extruded into sheet from which the element may be cut, diced, or otherwise removed. The element may be of any shape, e.g. rectangular, square, or circular. Depending on the intended end-use, the composition may undergo various processing techniques, e.g. crosslinking or heat-treatment, following shaping. Crosslinking can be accomplished by chemical means or by irradiation, e.g. using an electron beam or a Co60 γ irradiation source, and may be done either before or after the attachment of the electrode.
The conductive polymer element may comprise one or more layers of a conductive polymer composition. For some applications, e.g. where it is necessary to control the location at which a hotline or hotzone corresponding to a region of high current density forms, it is desirable to prepare the element from layers of conductive polymers which have different resistivity values. Alternatively, it may be beneficial to apply a conductive tie layer to the surface of the element to enhance bonding to the electrode.
Suitable conductive polymer compositions are disclosed in U.S. Pat. Nos. 4,237,441 (van Konynenburg et al), 4,388,607 (Toy et al), 4,534,889 (van Konynenburg et al), 4,545,926 (Fouts et al), 4,560,498 (Horsma et al), 4,591,700 (Sopory), 4,724,417 (Au et al), 4,774,024 (Deep et al), 4,935,156 (van Konynenburg et al), 5,049,850 (Evans et al), and 5,250,228 (Baigrie et al), and in pending U.S. application Ser. Nos. 07/894,119 (Chandler et al, filed Jun. 5, 1992), now U.S. Pat. No. 5,378,407 (issued Jan. 3, 1995), 08/085,859 (Chu et al, filed Jun. 29, 1993), now U.S. Pat. No. 5,451,919 (issued Sep. 19, 1995), 08/173,444 (Chandler et al, filed Dec. 23, 1993), now abandoned and 08/255,497 (Chu et al, filed Jun. 8, 1995) now U.S. Pat. No. 5,582,770 (issued Dec. 10, 1996). The disclosure of each of these patents and applications is incorporated herein by reference.
The devices of the invention comprise at least one electrode which is in direct physical contact with, generally bonded directly to, the conductive polymer element. For many devices of the invention, two electrodes are present, sandwiching the conductive polymer element. The electrode is generally in the form of a solid metal sheet, e.g. a foil, although for some applications, the electrode may be perforated, e.g. contain holes or slits. The electrode comprises at least two layers, i.e. a base layer which comprises a first metal, and a surface layer which comprises a second metal. In addition, as discussed below, one or more intermediate metal layers may be present, each of which is positioned between the base layer and the surface layer.
The first metal, used in the base layer, may be any suitable material, e.g. nickel, copper, aluminum, brass, or zinc, but is most often copper. Copper is preferred because of its excellent thermal and electrical conductivity which allows uniform distribution of electrical current across a device, the reproducibility of its production process, the ease of its manufacture which allows production of defect-free continuous lengths, and its relatively low cost. The base layer may be prepared by any suitable method. Copper, for example, may be prepared by rolling or electrodeposition. For some applications, it is preferred to use rolled nickel, produced by a powder metallurgical process, as the base layer. Such nickel is more conductive than nickel prepared by a conventional electrodeposited process due to increased purity.
The surface of the base layer may be relatively smooth or may be microrough. Microrough surfaces generally are those which have irregularities or nodules which protrude from the surface by a distance of at least 0.03 microns, preferably at least 0.1 microns, particularly 0.1 to 100 micronss, and which have at least one dimension parallel to the surface which is at most 500 micronss, preferably at most 100 micronss, particularly at most 10 microns, and which is preferably at least 0.03 microns, particularly at least 0.1 micron. Each irregularity or nodule may be composed of smaller nodules, e.g. in the form of a bunch of grapes. Such microroughness is often produced by electrodeposition in which a metal foil is exposed to an electrolyte, but a microrough surface may also be achieved by removing material from a smooth surface, e.g. by etching; by chemical reaction with a smooth surface, e.g. by galvanic deposition; or by contacting a smooth surface with a patterned surface, e.g. by rolling, pressing, or embossing. In general, a foil is said to have a smooth surface if its center line average roughness Ra is less than 1.0, and a microrough surface if Ra is greater than 1.0. It is often preferred that the surface of the base layer in contact with the intermediate layer have an Ra value of less than 1.0, preferably less than 0.9, particularly less than 0.8, especially less than 0.7. Metal foils with such a smooth surface generally are difficult to bond to conductive polymer compositions, especially if the conductive polymer composition has a high level of filler and/or comprises a non-polar polymer. Ra is defined as the arithmetic average deviation of the absolute values of the roughness profile from the mean line or center line of a surface when measured using a profilometer having a stylus with a 5 micron radius. The value of the center line is such that the sum of all areas of the profile above the center line is equal to the sum of all areas below the center line, when viewed at right angles to the foil. Appropriate measurements can be made by using a Tencor P-2 profilometer, available from Tencor. Thus Ra is a gauge of the height of protrusions from the surface of the foil.
The surface layer is either in direct physical contact with the base layer or, preferably, is separated from the base layer by one or more intermediate conductive, preferably metal, layers. The surface layer comprises a second metal which is different from the first metal. Appropriate second metals include nickel, copper, brass, or zinc, but for many devices of the invention the second metal is most often nickel or a nickel-containing material, e.g. zinc-nickel. Nickel is preferred because it provides a diffusion barrier for a copper base layer, thus minimizing the rate at which copper comes in contact with the polymer and serves to degrade the polymer. Furthermore, a nickel surface layer will naturally comprise a thin nickel oxide covering layer which is stable to moisture. The surface layer is in direct physical contact with the conductive polymer element. To enhance adhesion to the conductive polymer element, the surface layer has a microrough surface, i.e. has a center line average roughness Ra of at least 1.3, preferably at least 1.4, particularly at least 1.5. Although it is desirable that the protrusions from the surface are high enough to allow adequate penetration of the polymer into the gaps to produce a good mechanical bond, it is not desirable that the height of the protrusions be so great that polymer is unable to fill the gap completely. Such an air gap results in poor aging performance when a device is exposed to elevated temperature or to applied voltage. Therefore, it is preferred that Ra be at most 2.5, preferably at most 2.2, particularly at most 2.0.
We have found that in addition to the required Ra, the surface layer must also have a particular reflection density Rd. Reflection density is defined as log (1/% reflected light) when light over the visible range (i.e. 200 to 700 nm) is directed at the surface. An average of measurements each taken over an area of 4 mm2 is calculated. Appropriate measurements can be made using a Macbeth Model 1130 Color Checker in the automatic filter selection mode "L" with calibration of a black standard to 1.61 prior to the measurement For a surface with perfect reflection, the value of Rd is 0; the value increases as the amount of light absorbed increases. Higher values indicate greater structure in the protrusions from the surface. For devices of the invention, the value of Rd is at least 0.60, preferably at least 0.65, particularly at least 0.70, especially at least 0.75, most especially at least 0.80.
When, as is preferred, an intermediate layer is present, it may comprise the second metal or a third metal. The metal in the intermediate layer may not be the same as the first metal. It is preferred that the intermediate layer comprise the second metal. In a preferred embodiment, the intermediate layer comprises a generally smooth layer attached to the base layer. The intermediate layer then serves as a basis from which a microrough surface layer can be prepared. For example, if the base layer is copper, the intermediate layer may be a generally smooth layer of nickel from which nickel nodules can be produced on electrodeposition to provide a surface layer.
The metal electrodes may be attached to the conductive polymer element by any suitable means, e.g. compression molding or nip lamination. Depending on the viscosity of the conductive polymer and the lamination conditions, different types and thicknesses of metal foils may be suitable. To provide adequate flexibility and adhesion, it is preferred that the metal foil have a thickness of less than 50 microns (0.002 inch), particularly less than 44 microns (0.00175 inch), especially less than 38 microns (0.0015 inch), most especially less than 32 microns (0.00125 inch). In general, the thickness of the base layer is 10 to 45 microns (0.0004 to 0.0018 inch), preferably 10 to 40 microns (0.0004 to 0.0017 inch). The thickness of the surface layer is generally 0.5 to 20 microns (0.00002 to 0.0008 inch), preferably 0.5 to 15 micronss (0.00002 to 0.0006 inch), particularly 0.7 to 10 microns (0.00003 to 0.0004 inch). If an intermediate layer is present, it generally has a thickness of 0.5 to 20 microns (0.00002 to 0.0008 inch), preferably 0.8 to 15 micronss (0.00003 to 0.0006 inch). When the layer comprises a microrough surface, the term "thickness" is used to refer to the average height of the nodules.
One measurement of the adequacy of attachment of the metal electrode to the conductive polymer composition is by peel strength. Peel strength, as described below, is measured by clamping one end of a sample in the jaw of a testing apparatus and then peeling the foil, at a constant rate of 127 mm/minute (5 inches/minute) and at an angle of 90�, i.e. perpendicular to the surface of the sample. The amount of force in pounds/linear inch required to remove the foil from the conductive polymer is recorded. It is preferred that the electrode have a peel strength of at least 3.0 pli, preferably at least 3.5 pli, particularly at least 4.0 pli, when attached to the conductive polymer composition.
The electrical devices of the invention may comprise circuit protection devices, heaters, sensors, or resistors. Circuit protection devices generally have a resistance of less than 100 ohms, preferably less than 50 ohms, particularly less than 30 ohms, especially less than 20 ohms, most especially less than 10 ohms. For many applications, the resistance of the circuit protection device is less than 1 ohm, e.g. 0.010 to 0.500 ohms. Heaters generally have a resistance of at least 100 ohms, preferably at least 250 ohms, particularly at least 500 ohms.
Electrical devices of the invention are often used in an electrical circuit which comprises a source of electrical power, a load, e.g. one or more resistors, and the device. In order to connect an electrical device of the invention to the other components in the circuit, it may be necessary to attach one or more additional metal leads, e.g. in the form of wires or straps to the metal foil electrodes. In addition, elements to control the thermal output of the device, i.e. one or more conductive terminals, can be used. These terminals can be in the form of metal plates, e.g. steel, copper, or brass, or fins, which are attached either directly or by means of an intermediate layer such as solder or a conductive adhesive, to the electrodes. See, for example, U.S. Pat. No. 5,089,801 (Chan et al), and in pending U.S. application Ser. No. 07/837,527 (Chan et al), filed Feb. 18, 1992, now abandoned in favor of U.S. application Ser. No. 08/087,017, filed Jul. 6, 1993, now U.S. Pat. No. 5,436,609 (issued Jul. 25, 1995). For some applications, it is preferred to attach the devices directly a circuit board. Examples of such attachment techniques are shown in U.S. application Ser. Nos. 07/910,950 (Graves et al, filed Jul. 9, 1992) and 08/121,717 (Siden et al, filed Sep. 15, 1993), both of which have been abandoned and the subject matter of which is pending in U.S. application Ser. No. 08/900,787, filed Jul. 25, 1997, and 08/242,916 (Zhang et al, filed May 13, 1994), abandoned in favor of U.S. application Ser. No. 08/710,925, filed Sep. 24, 1996 and in International Application No. PCT/US93/06480 (Raychem Corporation, filed Jul. 8, 1993). The disclosure of each of these patents and applications is incorporated herein by reference.
The invention is illustrated by the drawing in which FIG. 1 shows a plan view of electrical device 1 of the invention in which metal foil electrodes 3,5 are attached directly to a PTC conductive polymer element 7. Element 7 may comprise a single layer, as shown, or two or more layers of the same or different compositions.
FIG. 2 shows a schematic cross-sectional view of a conventional metal foil to be used as an electrode 3,5. A base layer 9 comprising a first metal, e.g. copper, has a 25 microrough surface produced preferably by electrodeposition. The nodules 11 comprising the microrough surface are composed of the first metal. A surface layer 13 of a second metal, e.g. nickel, covers the nodules 11.
FIG. 3 shows a schematic cross-sectional view of a metal foil used as an electrode 3,5 in devices of the invention. A base layer 9 comprising a first metal, e.g. copper, is in contact with an intermediate layer 15 comprising a second metal, e.g. nickel. The surface of the intermediate layer forms the base for a surface layer 17 which has a microrough surface. As shown in FIG. 3, the nodules comprising surface layer 17 are formed of the second metal.
The invention is illustrated by the following Examples 1 to 9 in which Examples 1, 2, 4, 7 and 8 are comparative examples.
For each of compositions A and B, the ingredients listed in Table I were preblended in a Henschel blender and then mixed in a Buss-Condux kneader. The compound was pelletized and extruded through a sheet die to give a sheet with dimensions of approximately 0.30 m�0.25 mm (12�0.010 inch).
TABLE I______________________________________Compositions in Weight PercentIngredient    Tradename/Supplier                      A        B______________________________________High density polyethylene         Petrothene &#8482;                         22.1%    22.1%         LB832/QuantumEthylene/acrylic acid         Primacor &#8482; 1320/                      27.6copolymer     DowEthylene/butyl acrylate         Enathene &#8482; EA      27.6copolymer     705/QuantumCarbon black  Raven &#8482; 430/                      50.3     50.3         Columbian______________________________________
The characteristics of the metal foils used in the Examples are shown in Table II. Each metal foil was approximately 35 microns thick.
TABLE II______________________________________Metal Foil CharacteristicsFoil Type   1       2       3     4     5______________________________________Name                N2PO    Type 31                             Type 28                                   Type 31Lot number  --      --      3 � 291                             --    35191-2Supplier    Fukuda  Gould   Fukuda                             Fukuda                                   FukudaBase Layer  Ni      Cu      Cu    Cu    CuIntermediate Layer       --      Cu      Ni    Ni    NiSurface Layer       Ni      Ni      Ni    Ni    NiNodule Type Ni      Cu      Ni    Ni    NiRa     --      2.0     1.6   1.25  1.9Rd     --      0.65    0.90  0.76  0.81______________________________________
The extruded sheet was laminated to the metal foil either by compression-molding (C) in a press or by nip-lamination (N). In the compression-molding process, the extruded sheet was cut into pieces with dimensions of 0.30�0.41 m (12�16 inch) and was sandwiched between two pieces of foil. Pressure absorbing silicone sheets were positioned over the foil and the foil was attached by heating in the press at 175� C. for 5.5 minutes at 188 psi and cooling at 25� C. for 6 minutes at 188 psi to form a plaque. In the nip-lamination procedure, the extruded sheet was laminated between two foil layers at a set temperature of 177� to 198� C. (350� to 390� F.). The laminate was cut into plaques with dimensions of 0.30�0.41 m (12�16 inch). Plaques made by both processes were irradiated to 10 Mrad using a 3.5 MeV electron beam. Individual devices were cut from the irradiated plaques. For the trip endurance and cycle life tests, the devices were circular disks with an outer diameter of 13.6 mm (0.537 inch) and an inner diameter of 4.4 mm (0.172 inch). For the humidity test, the devices had dimensions of 12.7�12.7 mm (0.5�0.5 inch). Each device was temperature cycled from -40 to +80� C. six times, holding the device at each temperature for 30 minutes.
Trip Endurance Test
Devices were tested for trip endurance by using a circuit consisting of the device in series with a switch, a 15 volt DC power source, and a fixed resistor which limited the initial current to 40A. The initial resistance of the device at 25� C., Ri, was measured. The device was inserted in the circuit, was tripped, and then was maintained in its tripped state for the specified time period. Periodically, the devices were removed from the circuit and cooled to 25� C., and the final resistance at 25� C., Rf, was measured.
Devices were tested for cycle life by using a circuit consisting of the device in series with a switch, a 15 volt DC power source, and a fixed resistor which limited the initial current to 50A. Prior to testing, the resistance at 25� C., Ri, was measured. The test consisted of a series of test cycles. Each cycle consisted of closing the switch for 3 seconds, thus tripping the device, and then opening the switch and allowing the device to cool for 60 seconds. The final resistance Rf was recorded after each cycle.
After measuring the initial resistance Ri at 25� C., devices were inserted into an oven maintained at 85� C. and 85% humidity. Periodically, the devices were removed from the oven, cooled to 25� C., and the final resistance Rf was measured. The ratio of Rf /Ri was then determined.
The peel strength was measured by cutting samples with dimensions of 25.4�254 mm (1�10 inch) from extruded sheet attached to metal foil. One end of the sample was clamped into an Tinius Olsen tester. At the other end, the foil was peeled away from the conductive polymer at an angle of 90� and a rate of 127 mm/minute (5 inches/minute). The amount of force in pounds/linear inch required to remove the foil from the conductive polymer was recorded.
TABLE III______________________________________Example 1       2      3     4    5     6    7______________________________________Composition   A       A      A     A    B     B    BFoil Type   1       2      3     4    5     3    2Preparation   C       C      N     C    N     N    NPeel (pli)                        5          3Trip Endurance (Rf /Ri after hours at 15 VDC) 24     3.75                      2.41       1.90 48     4.45                      2.65       1.76112                    5.2              2.68500                    23.7             3.71Cycle Life (Rf /Ri after cycles at 15 VDC/50 A) 500    1.69           1.41       1.77  1.34 1.541000    1.92           1.62       2.25  1.65 1.7515002500Humidity (Rf /Ri after hours at 85� C./85%)* 500            1.05   1.02             1.14 0.94 700                         1.821000    0.91    1.30   1.03       1.54  1.19 0.951100                         3.742000            2.652500    1.04                      1.86       0.94______________________________________ *Example 2 was tested at 85� C./90% humidity.
Following the above procedures and using a nip/lamination process at 185� C., devices were prepared from a composition comprising 28.5% by weight Enathene EA 705 ethylene/butyl acrylate copolymer, 23.4% by weight Petrothene LB832 high density polyethylene, and 48.1% by weight Raven 430 carbon black. Devices were tested as described above for trip endurance, cycle life, and humidity. Additional testing was conducted following cycle testing to 3500 cycles and storage at room temperature (25� C.) for approximately three months. Ten devices of each type which had been cycled 3500 cycles at 15 VDC and 40A were aged in a circulating air oven at 100� C. for 600 hours or at 85� C./85% humidity for 600 hours. Periodically the devices were cooled to 25� C. and their resistances were measured. Devices of the invention (Example 9) in which the nodules were nickel showed better aging behavior than devices prepared with conventional metal foil electrodes in which the nodules were copper (Example 8). Results are shown in Table IV. One metal electrode from one device from each of Examples 8 and 9 which had been aged at 100� C. for 170 hours was peeled off the polymeric element and the surface which had been in contact with the conductive polymer composition was analyzed by ESCA to determine elemental composition of the surface (i.e. the top 10 nm). The average of the measurements for two different regions of the surface is shown in Table V. As a control, samples of the metal foil used to prepare the electrode were aged in air for 24 hours at 200� C. to simulate the thermal exposure of the foil during processing and testing. The results are shown in Table V. The limit of detection of the equipment was 0.1 atomic percent.
TABLE IV______________________________________Example         8       9______________________________________Foil Type       2       3Peel (pli)      1.8-3.0 4.0-5.0Trip Endurance (Rf /Ri after hours at 15 VDC) 28             1.86    1.74 195            2.65    2.561128            7.61    6.40Cycle Life (Rf /Ri after cycles at 15 VDC/50 A)1500            1.66    1.452500            2.38    1.823500            2.70    1.14Aging data after 3500 cycles/3 months at 25� C.(Rf /Ri after hours at 100� C.) 24             1.06    0.87 72             1.20    0.91120             1.19    0.90600             1.32    1.03Humidity (Rf /Ri after hours at 85� C./85%)500             0.92    0.92Humidity data after 3500 cycles/3 months at 25� C.(Rf /Ri after hours at 85� C./85%) 24             0.89    0.81 72             0.92    0.79120             0.91    0.75600             1.26    0.82______________________________________
TABLE V______________________________________Results of ESCA Testing      Atomic Percent of Elements    Foil                             OtherExample  Type    C       Q     Ni    Cu   Element______________________________________Foil from 8    2       85.5    11.0  0.3   0.4  2.8Foil from 9    3       92.0    5.5   0.4   *    2.1Bare Foil    2       34.5    40.0  16.5  2.5  6.5Bare Foil    3       28.0    46.0  22.0  *    4.0______________________________________ * less than 0.1 atomic %
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS2037951 *Sep 11, 1933Apr 21, 1936Allen Bradley CoFixed resistor unit and process of forming the sameUS2278072 *Jun 3, 1939Mar 31, 1942Bell Telephone Labor IncElectrical resistance device and method of manufacture thereofUS3237286 *Nov 28, 1962Mar 1, 1966Int Resistance CoMethod of making electrical resistorsUS3344316 *Aug 17, 1965Sep 26, 1967John P StelmakElectrical connection of components to printed circuitsUS4103274 *Sep 13, 1976Jul 25, 1978General Electric CompanyReconstituted metal oxide varistorUS4237441 *Dec 1, 1978Dec 2, 1980Raychem CorporationLow resistivity PTC compositionsUS4388607 *Oct 17, 1979Jun 14, 1983Raychem CorporationConductive polymer compositions, and to devices comprising such compositionsUS4414052 *Dec 23, 1981Nov 8, 1983Matsushita Electric Industrial Co., Ltd.Positive-temperature-coefficient thermistor heating deviceUS4426633 *Apr 15, 1981Jan 17, 1984Raychem CorporationDevices containing PTC conductive polymer compositionsUS4444708 *Jun 17, 1982Apr 24, 1984Sunbeam CorporationFlexible production of heating elementsUS4454379 *May 21, 1982Jun 12, 1984General Electric CompanySemi-conductive, moisture barrier shielding tape and cableUS4482801 *Dec 14, 1982Nov 13, 1984Matsushita Electric Industrial Co., Ltd.Positive-temperature-coefficient thermistor heating deviceUS4534889 *Feb 11, 1983Aug 13, 1985Raychem CorporationPTC Compositions and devices comprising themUS4545926 *Apr 21, 1980Oct 8, 1985Raychem CorporationConductive polymer compositions and devicesUS4560498 *Oct 12, 1979Dec 24, 1985Raychem CorporationPositive temperature coefficient of resistance compositionsUS4591700 *Mar 12, 1984May 27, 1986Raychem CorporationPTC compositionsUS4689475 *Oct 15, 1985Aug 25, 1987Raychem CorporationElectrical devices containing conductive polymersUS4724417 *Mar 14, 1985Feb 9, 1988Raychem CorporationElectrical devices comprising cross-linked conductive polymersUS4774024 *Mar 14, 1985Sep 27, 1988Raychem CorporationConductive polymer compositionsUS4800253 *Aug 25, 1987Jan 24, 1989Raychem CorporationElectrical devices containing conductive polymersUS4857880 *Feb 8, 1988Aug 15, 1989Raychem CorporationElectrical devices comprising cross-linked conductive polymersUS4907340 *Sep 30, 1987Mar 13, 1990Raychem CorporationElectrical device comprising conductive polymersUS4924074 *Jan 3, 1989May 8, 1990Raychem CorporationElectrical device comprising conductive polymersUS4935156 *Sep 27, 1982Jun 19, 1990Raychem CorporationConductive polymer compositionsUS5049850 *Nov 21, 1990Sep 17, 1991Raychem CorporationElectrically conductive device having improved properties under electrical stressUS5089801 *Sep 28, 1990Feb 18, 1992Raychem CorporationSelf-regulating ptc devices having shaped laminar conductive terminalsUS5250228 *Nov 6, 1991Oct 5, 1993Raychem CorporationConductive polymer compositionUS5289155 *Sep 10, 1991Feb 22, 1994Kabushiki Kaisha Komatsu SeisakushoPositive temperature characteristic thermistor and manufacturing method thereforUS5354969 *May 13, 1993Oct 11, 1994Nippondenso Co., Ltd.Positive-temperature-coefficient thermistor heating device and process for production of the sameUS5358793 *May 7, 1992Oct 25, 1994Daito Communication Apparatus Co., Ltd.PTC deviceUS5382938 *Oct 25, 1991Jan 17, 1995Asea Brown Boveri AbPTC elementDE3707494A1 *Mar 9, 1987Mar 31, 1988Nippon Mektron KkPTC componentEP0223404A1 *Oct 14, 1986May 27, 1987RAYCHEM CORPORATION (a Delaware corporation)Circuit protection deviceEP0517372A2 *May 6, 1992Dec 9, 1992Daito Communication Apparatus Co. Ltd.PTC deviceJP62418681A * Title not availableJPH059921A * Title not availableJPH05275205A * Title not availableJPH05343203A * Title not availableJPS62113402A * Title not availableWO1994001876A1 *Jul 8, 1993Jan 20, 1994Raychem CorporationElectrical devices* Cited by examinerNon-Patent CitationsReference1D.J. Arrowsmith, "Adhesion of Electroformed Copper and Nickel to Plastic Laminates", Transactions of the Institute of Metal Finishing, vol. 48, 1970, pp. 88-92.2D.J. Arrowsmith, "Aspects of Adhesion", Product Finishing, vol. 24, No. 1, Jan. 1971, pp. 40-47.3 *D.J. Arrowsmith, Adhesion of Electroformed Copper and Nickel to Plastic Laminates , Transactions of the Institute of Metal Finishing, vol. 48, 1970, pp. 88 92.4 *D.J. Arrowsmith, Aspects of Adhesion , Product Finishing, vol. 24, No. 1, Jan. 1971, pp. 40 47.5Donald M. Bigg and E. Joseph Bradbury, "Conductive Polymeric Composites from Short Conductive Fibers", Conductive Polymers, Raymond B. Seymour, editor, Plenum Press, 1981, pp. 23-38.6 *Donald M. Bigg and E. Joseph Bradbury, Conductive Polymeric Composites from Short Conductive Fibers , Conductive Polymers, Raymond B. Seymour, editor, Plenum Press, 1981, pp. 23 38.7 *International Search Report for International Application No. PCT/US95/07888, mailed Aug. 31, 1995.8 *Patent Abstracts of Japan, vol. 13, No. 168 (E 747), Apr. 21, 1989 (abstract of JP A 64 001201 (Murata Manufacturing Co. Ltd.)).9Patent Abstracts of Japan, vol. 13, No. 168 (E-747), Apr. 21, 1989 (abstract of JP-A-64-001201 (Murata Manufacturing Co. Ltd.)).10 *U.S. Application No. 07/837,527 (Chan et al., filed Feb. 18, 1992).11 *U.S. Application No. 07/894,119 (Chandler et al., filed Jun. 5, 1992).12 *U.S. Application No. 07/910,950 (Graves et al., filed Jul. 9, 1992).13 *U.S. Application No. 08/085,859 (Chu et al., filed Jun. 29, 1993).14 *U.S. Application No. 08/121,717 (Siden et al., filed Sep. 15, 1993).15 *U.S. Application No. 08/173,444 (Chandler et al., filed Dec. 23, 1993).16 *U.S. Application No. 08/242,916 (Zhang et al., filed May 13, 1994).* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS6023403Nov 26, 1997Feb 8, 2000Littlefuse, Inc.Surface mountable electrical device comprising a PTC and fusible elementUS6104587 *Jul 25, 1997Aug 15, 2000Banich; AnnElectrical device comprising a conductive polymerUS6157289 *Sep 22, 1997Dec 5, 2000Mitsushita Electric Industrial Co., Ltd.PTC thermistorUS6163245 *Dec 22, 1998Dec 19, 2000Kabushiki Kaisha ToshibaNonlinear resistor with electrodes formed by plasma sprayingUS6188308 *Dec 25, 1997Feb 13, 2001Matsushita Electric Industrial Co., Ltd.PTC thermistor and method for manufacturing the sameUS6282072Feb 23, 1999Aug 28, 2001Littelfuse, Inc.Electrical devices having a polymer PTC arrayUS6349022Apr 7, 2000Feb 19, 2002Tyco Electronics CorporationLatching protection circuitUS6362721Aug 31, 1999Mar 26, 2002Tyco Electronics CorporationElectrical device and assemblyUS6438821Jan 11, 2000Aug 27, 2002Matsushita Electric Industrial Co., Ltd.PTC thermistor and method for manufacturing the sameUS6452476 *Jan 28, 1999Sep 17, 2002Tdk CorporationOrganic positive temperature coefficient thermistorUS6522237 *Nov 2, 1999Feb 18, 2003Matsushita Electric Industrial Co., Ltd.Electrode for PTC thermistor and method for producing the same, and PTC thermistorUS6531950Jun 28, 2000Mar 11, 2003Tyco Electronics CorporationElectrical devices containing conductive polymersUS6558616Feb 5, 2001May 6, 2003Matsushita Electric Industrial Co., Ltd.Electrode for PTC thermistor and method for producing the same, and PTC thermistorUS6570483 *Mar 13, 1997May 27, 2003Tyco Electronics CorporationElectrically resistive PTC devices containing conductive polymersUS6582647Sep 30, 1999Jun 24, 2003Littelfuse, Inc.Method for heat treating PTC devicesUS6593843Jun 28, 2000Jul 15, 2003Tyco Electronics CorporationElectrical devices containing conductive polymersUS6597551Dec 12, 2001Jul 22, 2003Huladyne CorporationPolymer current limiting device and method of manufactureUS6628498Jul 31, 2001Sep 30, 2003Steven J. WhitneyIntegrated electrostatic discharge and overcurrent deviceUS6856235 *Sep 12, 2001Feb 15, 2005Tessera, Inc.Methods for manufacturing resistors using a sacrificial layerUS6922131 *Nov 17, 2003Jul 26, 2005Tyco Electronics CorporationElectrical deviceUS6965293Jun 24, 2004Nov 15, 2005Lg Cable, Ltd.Electrical device having PTC conductive polymerUS6987440Jul 11, 2003Jan 17, 2006Tyco Electronics CorporationElectrical devices containing conductive polymersUS7091820Jun 30, 2004Aug 15, 2006Tessera, Inc.Methods for manufacturing resistors using a sacrificial layerUS7165316Apr 20, 2004Jan 23, 2007Tessera, Inc.Methods for manufacturing resistors using a sacrificial layerUS7371459 *Sep 3, 2004May 13, 2008Tyco Electronics CorporationElectrical devices having an oxygen barrier coatingUS7528350 *Sep 3, 2003May 5, 2009Tyco Electronics Raychem KkProcess for producing PTC element/metal lead element connecting structure and PTC element for use in the processUS7632373Dec 15, 2009Tyco Electronics CorporationMethod of making electrical devices having an oxygen barrier coatingUS7843308Feb 26, 2007Nov 30, 2010Littlefuse, Inc.Direct application voltage variable materialUS7920045Apr 5, 2011Tyco Electronics CorporationSurface mountable PPTC device with integral weld plateUS8686826Apr 5, 2011Apr 1, 2014Tyco Electronics CorporationSurface mountable PPTC device with integral weld plateUS9347137Sep 11, 2006May 24, 2016Ihi CorporationMethod of manufacturing electrode for electrical-discharge surface treatment, and electrode for electrical-discharge surface treatmentUS20020017702 *Sep 12, 2001Feb 14, 2002Joseph FjelstadMethods for manufacturing resistors using a sacrificial layerUS20030218851 *Apr 8, 2003Nov 27, 2003Harris Edwin JamesVoltage variable material for direct application and devices employing sameUS20040006867 *Jan 3, 2003Jan 15, 2004Becker Paul N.Electrical devices containing conductive polymersUS20040104802 *Jul 11, 2003Jun 3, 2004Becker Paul N.Electrical devices containing conductive polymersUS20040136136 *Nov 17, 2003Jul 15, 2004Walsh Cecilia AElectrical deviceUS20040194294 *Apr 20, 2004Oct 7, 2004Tessera, Inc.Methods for manufacturing resistors using a sacrificial layerUS20040201941 *Dec 23, 2003Oct 14, 2004Harris Edwin JamesDirect application voltage variable material, components thereof and devices employing sameUS20040233033 *Jun 24, 2004Nov 25, 2004Lg Cable, Inc.Electrical device having PTC conductive polymerUS20040233035 *Jun 30, 2004Nov 25, 2004Tessera, Inc.Methods for manufacturing resistors using a sacrificial layerUS20050057867 *Oct 5, 2004Mar 17, 2005Harris Edwin JamesDirect application voltage variable material, devices employing same and methods of manufacturing such devicesUS20050200447 *Mar 15, 2004Sep 15, 2005Chandler Daniel A.Surface mountable PPTC device with integral weld plateUS20060261922 *Jul 26, 2006Nov 23, 2006Chu Fu HOver-current protection device and manufacturing method thereofUS20070071462 *Sep 26, 2006Mar 29, 2007Oki Data CorporationImage forming apparatusUS20070139848 *Feb 26, 2007Jun 21, 2007Littelfuse, Inc.Direct application voltage variable materialUS20070146941 *Feb 26, 2007Jun 28, 2007Littelfuse, Inc.Flexible circuit having overvoltage protectionUS20090027821 *Jul 26, 2007Jan 29, 2009Littelfuse, Inc.Integrated thermistor and metallic element device and methodUS20090127110 *Sep 11, 2006May 21, 2009Mitsubishi Electric CorporationMethod of manufacturing electrode for electrical-discharge surface treatment, and electrode for electrical-discharge surface treatmentUS20120056133 *Oct 26, 2011Mar 8, 2012Ihi CorporationMethod of manufacturing electrode for electrical-discharge surface treatment, and electrode for electrical-discharge surface treatmentEP1327995A2 *Jan 10, 2003Jul 16, 2003Shipley Co. L.L.C.Resistor structureEP1435193A2 *Sep 13, 2002Jul 7, 2004Oak-Mitsui, Inc.Nickel coated copper as electrodes for embedded passive devicesWO2001078453A1 *Mar 30, 2001Oct 18, 2001Lg Cable Ltd.Electrical device having ptc conductive polymerWO2002001581A1 *Jun 27, 2001Jan 3, 2002Tyco Electronics CorporationElectrical devices containing conductive polymersWO2002001582A2 *Jun 27, 2001Jan 3, 2002Tyco Electronics CorporationElectrical devices containing conductive polymersWO2002001582A3 *Jun 27, 2001Oct 17, 2002Tyco Electronics CorpElectrical devices containing conductive polymers* Cited by examinerClassifications U.S. Classification338/22.00R, 338/327, 427/103, 338/328, 338/22.0SDInternational ClassificationH01C7/02, H01C1/14Cooperative ClassificationH01C1/1406, H01C7/027, H01C1/14European ClassificationH01C7/02D, H01C1/14B, H01C1/14Legal EventsDateCodeEventDescriptionMar 17, 1997ASAssignmentOwner name: RAYCHEM CORPORATION, CALIFORNIAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:CHANDLER, DANIEL A.;MATTHIESEN, MARTIN;LEONG, DEREK;AND OTHERS;REEL/FRAME:008406/0046;SIGNING DATES FROM 19970307 TO 19970312Aug 31, 1999CCCertificate of correctionApr 5, 2000ASAssignmentOwner name: TYCO INTERNATIONAL (PA), INC., A CORPORATION OF NEFree format text: MERGER & REORGANIZATION;ASSIGNOR:RAYCHEM CORPORATION, A CORPORATION OF DELAWARE;REEL/FRAME:011682/0001Effective date: 19990812Owner name: TYCO INTERNATIONAL LTD., A CORPORATION OF BERMUDA,Free format text: MERGER & REORGANIZATION;ASSIGNOR:RAYCHEM CORPORATION, A CORPORATION OF DELAWARE;REEL/FRAME:011682/0001Effective date: 19990812Owner name: AMP INCORPORATED, A CORPORATION OF PENNSYLVANIA, PFree format text: MERGER & REORGANIZATION;ASSIGNOR:RAYCHEM CORPORATION, A CORPORATION OF DELAWARE;REEL/FRAME:011682/0001Effective date: 19990812Apr 5, 2001ASAssignmentOwner name: TYCO ELECTRONICS CORPORATION, A CORPORATION OF PENFree format text: CHANGE OF NAME;ASSIGNOR:AMP INCORPORATED, A CORPORATION OF PENNSYLVANIA;REEL/FRAME:011675/0436Effective date: 19990913Jul 26, 2002FPAYFee paymentYear of fee payment: 4Aug 23, 2006FPAYFee paymentYear of fee payment: 8Aug 23, 2010FPAYFee paymentYear of fee payment: 12RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services