Silicone Composition Used In The Production Of Antifriction Varnishes, Method For The Application Of Said Varnishes To A Support And Support Thus Treated - Patent 7311945
55795793
The general field of the invention is that of polymer coatings or varnishes capable of conferring anti-friction properties on substrates. More precisely, the invention relates to silicone compositions useful in particular for the production ofvarnishes which can be applied to supports whose coefficient of friction it is sought to reduce. The supports in question are varied and may consist in particular: of woven or nonwoven fibrous substrates coated with at least one layer for protection orfor mechanical reinforcement, based on a coating polymer of the silicone elastomer type for example; of polymer substrates, in particular plastic films such as for example: thermal transfer ribbons which can be used in particular as support for ink inthermal transfer printers, or protective wrapping films,The present invention also relates to the methods for applying the anti-friction varnish to which it relates, to various supports.Finally, the subject of the invention is the supports coated with such anti-friction varnishes and, in particular: textile fabrics coated with an elastomer layer onto which the anti-friction varnish is applied, such fabrics being capable of beingused for the manufacture of bags for the personal protection of the occupants of vehicles, also called air bag, thermal transfer ribbons consisting for example of plastic films (e.g. made of polyester) carrying ink and which can be used in thermaltransfer printers, protective wrapping films.PRIOR ARTThe general problem forming the basis of the invention is the development of an anti-friction silicone varnish. This problem of reducing coefficients of friction is posed with particular intensity for substrates coated with crosslinkedelastomeric silicone coatings. Indeed, it is well known to persons skilled in the art that coating layers made of elastomeric silicone have a sticky feel which is damaging for numerous applications.As regards more precisely the air bag application, it is known that these inflatable
United States Patent: 7311945
7,311,945
Silicone composition used in the production of antifriction varnishes,
method for the application of said varnishes to a support and support
A silicone composition which can be used in the production of varnishes
that can be applied to supports to reduce the friction coefficient. The
silicone composition includes at least one polyorganosilane A (POS) which
can be cationically and radically cross-linked by functional
cross-linking groups (GER) and a primer C chosen from onium borates. The
composition also includes molecules (POS D) which are substituted by
secondary functional groups (GFS) caned by silicon atoms and selected
from those that include at least one alkoxy and/or epoxy and/or carboxy
motif and optionally a charge (e.g. silica). The composition can be used
with antifriction varnishes for RTV silicone coatings for material used
in airbags, thermal transfer ribbons or packing films ##STR00001##
Bertry; Jean-Louis (Lyons, FR), Frances; Jean-Marc (Meyzieu, FR), Bohin; Fabrice (Paris, FR), Priou; Christian (Princeton, NJ)
10/945,081
099581796902816
PCT/FR00/00861Apr., 2000
99 04421
427/397.7  ; 427/515; 522/25; 522/66; 525/477; 528/12; 528/32; 528/901
525/477 528/12,32,901 522/25,66 427/397.7,515
97/35924
This application is a continuation of Ser. No. 09/958,179, now U.S. Pat.
No. 6,902,816, which is a U.S. National Stage of International
application PCT/FR00/00861, filed Apr. 5, 2000.
1.  A varnish support having antifriction properties, said support comprising a substrate coated on at least one of its surfaces with at least one layer of silicone
elastomer which is crosslinked or which is at least partially crosslinked, said layer of silicone elastomer coated with an antifriction varnish obtained from a silicone composition comprising at least one polyorganosiloxane (POS) which is crosslinked by
means of crosslinking functional groups (CFG) by the cationic and/or free-radical route and an effective quantity of a cationic initiator system comprising, as thermal initiator and/or photoinitiator, a product chosen from the onium salts of an element
of groups 15 to 17 of the Periodic Table or the salts of an organometallic complex of an element of groups 4 to 10 of the Periodic Table, whose cationic entity is selected from: 1) the onium salts of formula (I): [(R.sup.1).sub.n-A-(R.sup.2).sub.m].sup.+
(I) in which formula: A represents an element of groups 15 to 17 of the Periodic Table;  R.sup.1 represents a carbocyclic or heterocyclic C.sub.6-C.sub.20 aryl radical, it being possible for said heterocyclic radical to contain, as heteroelements,
nitrogen or sulfur;  R.sup.2 represents R.sup.1 or a linear or branched C.sub.1-C.sub.30 alkyl or alkenyl radical, said radicals R.sup.1 and R.sup.2 being optionally substituted with a C.sub.1-C.sub.25 alkoxy, C.sub.1-C.sub.25 alkyl, nitro, chloro,
brorao, cyano, carboxyl, ester or mercapto group;  n is an integer ranging from 1 to v+1, v being the valency of the element A;  m is an integer ranging from 0 to v 1 with n+m =v+1;  2) oxoisothiochromanium salts;  3) sulfonium salts in which the
cationic entity comprises: 3-1) at least one polysulfonium species of formula (III.1): ##STR00024## in which: the symbols Ar.sup.1, which may be mutually identical or different, each represent a monovalent phenyl or naphthyl radical optionally
substituted with one or more radicals chosen from: a linear or branched C.sub.1-C.sub.12 alkyl radical, a linear or branched C.sub.1-C.sub.2 alkoxy radical, a halogen atom, an --OH group, a --COOH group, an ester group --COO-alkyl where the alkyl portion
is a linear or branched C.sub.1-C.sub.12 residue, and a group of formula --Y.sup.4--Ar.sup.2 where the symbols Y.sup.4 and Ar.sup.2 have the meanings given just below;  the symbols Ar.sup.2, which may be mutually identical or different, or identical to
A.sup.1, each represent a monovalent phenyl or naphthyl radical optionally substituted with one or more radicals chosen from: a linear or branched C.sub.1-C.sub.12 alkyl radical, a linear or branched C.sub.1-C.sub.12 alkoxy radical, a halogen atom, an
--OH group, a --COOH group, an ester group --COO-alkyl where the alkyl portion is a linear or branched C.sub.1-C.sub.12 residue, the symbols Ar.sup.3, which may be mutually identical or different, each represent a divalent phenylene or naphthylene
radical optionally substituted with one or more radicals chosen from: a linear or branched C.sub.1-C.sub.12 alkyl radical, a linear or branched C.sub.1-C.sub.12 alkoxy radical, a halogen atom, an --OH group, a --COOH group, an ester group --COO-alkyl
where the alkyl portion is a linear or branched C.sub.1-C.sub.12 residue, t is an integer equal to 0 or 1, with the additional conditions according to which: a) when t=0, the symbol Y is then a monovalent radical Y.sup.1 representing the group of
formula: ##STR00025## where the symbols Ar.sup.1 and Ar.sup.2 have the meanings given above, b) when t=1: b1) on the one hand, the symbol Y is then a divalent radical having the following meanings Y.sup.2 to Y.sup.4: Y.sup.2: a group of formula:
##STR00026## where the symbol Ar.sup.2 has the meanings given above, Y.sup.3: a single valency bond, Y.sup.4: a divalent residue chosen from: ##STR00027## a linear or branched C.sub.1-C.sub.12 alkylene residue, and a residue of formula
--Si(CH.sub.3).sub.2O--, b2) on the other hand, only in the case where the symbol Y represents Y.sup.3 or Y.sup.4, the radicals Ar.sup.1 and Ar.sup.2 (terminal) possess, in addition to the meanings given above, the possibility of being linked to each
other by the residue Y&#39; consisting of Y&#39;.sup.1 a single valency bond or of Y&#39;.sup.2 a divalent residue chosen from the residues cited in the definition of Y.sup.4, which is seated between the carbon atoms, facing one another, situated on each aromatic
ring at the ortho position with respect to the carbon atom directly linked to the cation S.sup.+;  3-2) and/or at least one mono-sulfonium species possessing a single cationic center S.sup.+ per mol of cation and consisting of species of formula (III.2):
##STR00028## in which Ar.sup.1 and Ar.sup.2 have the meanings given above in formula (III.1), including the possibility of directly linking to one another only one of the radicals Ar.sup.1 to Ar.sup.2 in the manner indicated above in the definition of
the additional condition which applies when t=1 in formula (III.1), involving the residue Y&#39;;  4) the organometallic salts of formula (IV): (L.sup.1L.sup.2L.sup.3M).sup.+q (IV) in which formula: M represents a metal of group 4 to 10 of the Periodic
Table;  L.sup.1 represents a ligand linked to the metal M by .pi.  electrons, a ligand chosen from the ligands .eta..sup.3-alkyl, .eta..sup.5-cyclopentadienyl and .eta..sup.7-cycloheptatrienyl and the .eta..sup.6-aromatic compounds chosen from the
optionally substituted .eta.6-benzene ligands and the compounds having from 2 to 4 fused rings each ring being capable of contributing to the valency layer of the metal N by 3 to 8 .pi.  electrons;  L.sup.2 represents a ligand linked to the metal M by
.pi.  electrons, a ligand chosen from the ligands .eta..sup.7-cycloheptatrienyl and the .eta..sup.6-aromatic compounds chosen from the optionally substituted .eta..sup.6-benzene ligands and the compounds having from 2 to 4 fused rings, each ring being
capable of contributing to the valency layer of the metal M by 6 or 7 .pi.  electrons;  L.sup.3 represents from 0 to 3 identical or different ligands linked to the metal M by .sigma.  electrons, ligand(s) chosen from CO and NO.sub.2.sup.+;  the total
electron charge q of the complex to which L.sup.1, L.sup.2 and L.sup.3 contribute and the ionic charge of the metal M being positive and equal to 1 or 2;  the anionic entity having the formula: [X.sup.1X.sup.2.sub.aR.sub.b].sup.- in which formula: a and
b are integers ranging, for a, from 0 to 6 and, for b, from 0 to 6 with a+b.gtoreq.2;  the symbols X.sup.1 represent elements chosen from groups 3A, 4A, 5A of the Periodic Table;  the symbols X.sup.2 represent: a halogen atom with a=0 to 3, an OH
functional group with a=0 to 2;  the symbols R are identical or different and represent: a phenyl radical substituted with at least one electron-attracting group, and/or with at least 2 halogen atoms, and this being when the cationic entity is an onium
of an element of groups 15 to 17 of the Periodic Table, a phenyl radical substituted with at least one electron-attracting atom or one electron-attracting group, and this being when the cationic entity is an organo-metallic complex of an element of
groups 4 to 10 of the Periodic Table, an aryl radical containing at least two aromatic nuclei, optionally substituted with at least one element or one electron-attracting group, regardless of the cationic entity;  wherein said POS carrying CFG are
epoxysilicones and/or vinyl ether silicones which are: 1) either linear and consist of units of formula (II-1), ending with units of formula (II-2), 2) or cyclic and consisting of units of formula (II-1): ##STR00029## in which formulae: the symbols
R.sup.16 are similar or different and represent either a linear or branched C.sub.1-C.sub.6 alkyl radical optionally substituted with one or more halogens, or an optionally substituted C.sub.5-C.sub.8 cycloalkyl radical, or an aryl or aralkyl radical
optionally substituted with halogens and/or alkoxyls, the symbols Z are similar or different and represent either the radical R.sup.16, or a CFG group corresponding to an epoxide or vinyl ether residue linked to the silicon by means of a divalent radical
containing from 2 to 20 carbon atoms optionally comprising a heteroatom, at least one of the symbols Z corresponding to a CFG group, said composition comprising, in addition, a silane substituted with CFG and hydrolyzable secondary functional groups
(SFG) and having the formula ##STR00030##
2.  The varnish support of claim 1, wherein said POS carrying CFG are epoxysilicones of the following formulae (A-I) or (A-II): ##STR00031## with X+CH.sub.3;  phenyl;  cycloalkyl;  C.sub.1-C.sub.18 alkyl;  alkenyl;  --OH;  H;
CH.sub.2--CH.sub.2--CH.sub.2--OH;  CH.sub.2--CH.sub.2--CF.sub.3;  or --(CH.sub.2).sub.n--CF.sub.3, n=1 to 20;  ##STR00032## a.sub.1, a.sub.2 and b.sub.1, b.sub.2 being defined as below in these formulae (A-I) and (A-II) 1.ltoreq.a.sub.1,
a.sub.21.ltoreq.b.sub.1, b.sub.2;  a.sub.2, b.sub.2 being=0 in formula (A-II) to gave the epoxydized disiloxane (A-III).
3.  The varnish support of claim 1, wherein said composition further comprises: at least one organic reactive diluent chosen from organic resins of the epoxide and/or vinyl ether and/or oxethane type;  optionally at least one organic or
inorganic pigment;  optionally a filler;  optionally at least one photosensitizer.
4.  The varnish support of claim 1, wherein said at least one layer of silicone elastomer which is crosslinked or at least partially crosslinked, is chosen from the polyaddition or polycondensation RTV silicones, and/or the peroxide HVE
silicones, and/or the polyaddition LSR silicones.
5.  A method of coating a silicone composition as an antifriction varnish upon a support, comprising coating at least one surface of a support with at least one layer of a silicone composition comprising at least one polyorganosiloxane (POS)
which is crosslinked by means of crosslinking functional groups (CFG) by the cationic and/or free-radical route and an effective quantity of a cationic initiator system comprising, as thermal initiator and/or photoinitiator, a product chosen from the
onium salts of an element of groups 15 to 17 of the Periodic Table or the salts of an organometallic complex of an element of groups 4 to 10 of the Periodic Table, whose cationic entity is selected from: 1) the onium salts of formula (I):
[(R.sup.1).sub.n-A-(R.sup.2).sub.m].sup.+ (I) in which formula: A represents an element of groups 15 to 17 of the Periodic Table;  R.sup.1 represents a carbocyclic or heterocyclic C.sub.6-C.sub.20 aryl radical, it being possible for said heterocyclic
radical to contain, as heteroelements, nitrogen or sulfur;  R2 represents R.sup.1 or a linear or branched C.sub.1-C.sub.30 alkyl or alkenyl radical, said radicals R.sup.1 and R.sup.2 being optionally substituted with a C.sub.1-C.sub.25 alkoxy,
C.sub.1-C.sub.25 alkyl, nitro, chloro, bromo, cyano, carboxyl, ester or mercapto group;  n is an integer ranging from 1 to v+1, v being the valency of the element A;  m is an integer ranging from 0 to v-1 with n+m=v+1;  2) oxoisothiochromanium salts;  3)
sulfonium salts in which the cationic entity comprises: 3-1) at least one polysulfonium species of formula (III.1): ##STR00033## in which: the symbols Ar.sup.1, which may be mutually identical or different, each represent a monovalent phenyl or naphthyl
where the alkyl portion is a linear or branched C.sub.1-C.sub.12 residue, and a group of formula --Y.sup.4--Ar.sup.2 where the symbols Y.sup.4 and Ar.sup.2 have the meanings given just below;  the symbols Ar.sup.2, which may be mutually identical or
different, or identical to Ar.sup.1, each represent a monovalent phenyl or naphthyl radical optionally substituted with one or more radicals chosen from: a linear or branched C.sub.1-C.sub.12 alkyl radical, a linear or branched C.sub.1-C.sub.12 alkoxy
radical, a halogen atom, an --OH group, a --COOH group, an ester group --COO-alkyl where the alkyl portion is a linear or branched C.sub.1-C.sub.12 residue, the symbols Ar.sup.3, which may be mutually identical or different, each represent a divalent
phenylene or naphthylene radical optionally substituted with one or more radicals chosen from: a linear or branched C.sub.1-C.sub.12, alkyl radical, a linear or branched C.sub.1-C.sub.12, alkoxy radical, a halogen atom, an OH group, a --COOH group, an
ester group --COO-alkyl where the alkyl portion is a linear or branched C.sub.1-C.sub.12 residue, t is an integer equal to 0 or 1, with the additional conditions according to which: a) when t=0, the symbol Y is then a monovalent radical Y.sup.1
representing the group of formula: ##STR00034## where the symbols Ar.sup.1 and Ar.sup.2 have the meanings given above, b) when t=1: b1) on the one hand, the symbol Y is then a divalent radical having the following meanings Y.sup.2 to Y.sup.4: Y.sup.2: a
group of formula: ##STR00035## where the symbol Ar.sup.2 has the meanings given above, Y.sup.3: a single valency bond, Y.sup.4: a divalent residue chosen from: ##STR00036## a linear or branched C.sub.1-C.sub.12 alkylene residue, and a residue of formula
##STR00037## in which Ar.sup.1 and Ar.sup.2 have the meanings given above in formula (III.1), including the possibility of directly linking to one another only one of the radicals Ar.sup.1 to Ar.sup.2 in the manner indicated above in the definition of
Table;  L.sup.1 represents a ligand linked to the metal M by .pi.  electrons, a ligand chosen from the ligands .eta..sup.3-alkyl, .eta..sup.5-cycloheptatrienyl and .eta..sup.7-cycloheptatrienyl and the .eta..sup.6-aromatic compounds chosen from the
optionally substituted .eta..sup.6-benzene ligands and the compounds having from 2 to 4 fused rings, each ring being capable of contributing to the valency layer of the metal M by 3 to 8 .pi.  electrons;  L.sup.2 represents a ligand linked to the metal M
by .pi.  electrons, a ligand chosen from the ligands .eta..sup.7-cycloheptatrienyl and the .eta..sup.6-aromatic compounds chosen from the optionally substituted .eta..sup.6-benzene ligands and the compounds having from 2 to 4 fused rings, each ring being
epoxysilicones and/or vinyl ether silicones which are;  2.) either linear and consist of units of formula (II-1), ending with units of formula (II-2), 2) or cyclic and consisting of units of formula (II-1): ##STR00038## in which formulae: the symbols
optionally substituted with halogens and/or alkoxyls, the symbols Z are similar or different and represent either the radical R.sub.16, or a CFG croup corresponding to an epoxide or vinyl ether residue linked to the silicon by means of a divalent radical
(SFG) having the formula ##STR00039## exposing the surface thus coated to actinic radiation and/or to a beam of electrons and/or to heat, so as to cause the crosslinking of the silicone composition and obtain an antifriction layer.
6.  The method of claim 5, wherein said POS carrying CFG are epoxysilicones of the following formulae (A-I) or (A-II): ##STR00040## with X.dbd.CR.sub.3;  phenyl;  cycloalkyl;  C.sub.1-C.sub.18 alkyl;  alkenyl;  --OR;  H;
CH.sub.2--CH.sub.2--CH.sub.2--OH;  CH.sub.2--CH.sub.2--CF.sub.3;  or --(CH.sub.2).sub.n--CF.sub.3, n=1 to 20;  ##STR00041## a.sub.1, a.sub.2 and b.sub.1, b.sub.2 being defined as below in these formulae (A-I) and (A.sup.II) 1.ltoreq.a.sub.1, a.sub.2
1.ltoreq.b.sub.1, b.sub.2;  a.sub.2, b.sub.2 being=0 in formula (A-II) to give the epoxydized disiloxane (A-III).
7.  The method of claim 5, wherein said composition further comprises: at least one organic reactive diluent chosen from organic resins containing at least one functional group selected from the group consisting of expoxide, vinyl ether and
oxethane;  optionally at least one organic or inorganic pigment;  optionally a filler;  optionally at least one photosensitizer.
8.  The method of claim 5, wherein said support comprises a substrate coated on at least one of its surfaces with at least one layer of silicone elastomer which is crosslinked or which is at least partially crosslinked.
9.  A method of coating a silicone composition as an antifriction varnish upon a support, comprising coating at least one surface of a support with at least one layer of a silicone composition comprising at least one polyorganosiloxane (POS)
radical to contain, as heteroelements, nitrogen or sulfur;  R.sup.2 represents R.sup.1 or a linear or branched C.sub.1-C.sub.30 alkyl or alkenyl radical, said radicals R.sup.1 and R.sup.2 being optionally substituted with a C.sub.1-C.sub.25 alkoxy,
sulfonium salts in which the cationic entity comprises: 3-1) at least one polysulfonium species of formula (III.1) ##STR00042## in which: the symbols Ar.sup.1, which may be mutually identical or different, each represent a monovalent phenyl or naphthyl
radical optionally substituted with one or more radicals chosen from: a linear or branched C.sub.1-C12 alkyl radical, a linear or branched C.sub.1-C.sub.12 alkoxy radical, a halogen atom, an --OH group, a --COOH group, an ester group --COO-alkyl where
the alkyl portion is a linear or branched C.sub.1-C.sub.12 residue, and a group of formula --Y.sup.4--Ar.sup.2 where the symbols Y.sup.4 and Ar.sup.2 have the meanings given just below;  the symbols Ar.sup.2, which may be mutually identical or different,
or identical to Ar.sub.1, each represent a monovalent phenyl or naphthyl radical optionally substituted with one or more radicals chosen from: a linear or branched C.sub.1-C.sub.12 alkyl radical, a linear or branched C.sub.1-C.sub.12 alkoxy radical, a
halogen atom, an --OH group, a --COOH group, an ester group --COO-alkyl where the alkyl portion is a linear or branched C.sub.1-C.sub.12 residue, the symbols Ar.sup.3, which may be mutually identical or different, each represent a divalent phenylene or
naphthylene radical optionally substituted with one or more radicals chosen from: a linear or branched C.sub.1-C.sub.12, alkyl radical, a linear or branched C.sub.1--C.sub.12, alkoxy radical, a halogen atom, an --OH group, a --COOH group, an ester group
--COO-alkyl where the alkyl portion is a linear or branched C.sub.1-C.sub.12 residue, t is an integer equal to 0 or 1, with the additional conditions according to which: a) when t=0, the symbol Y is then a monovalent radical Y.sup.1 representing the
group of formula: ##STR00043## where the symbols Ar.sup.1 and Ar.sup.2 have the meanings given above, b) when t=1: b1) on the one hand, the symbol Y is then a divalent radical having the following meanings Y.sup.2 to Y.sup.4: Y.sup.2: a group of formula:
##STR00044## where the symbol Ar.sup.2 has the meanings given above, Y.sup.3: a single valency bond, Y.sup.4: a divalent residue chosen from: ##STR00045## a linear or branched C.sub.1-C.sub.12 alkylene residue, and a residue of formula
--Si(CH.sub.3).sub.2O--, b.sub.2) on the other hand, only in the case where the symbol Y represents Y.sup.3 or Y.sup.4, the radicals Ar.sup.1 and Ar.sup.1 (terminal) possess, in addition to the meanings given above, the possibility of being linked to
each other by the residue Y&#39; consisting of Y&#39;.sup.1 a single valency bond or of Y&#39;.sup.2 a divalent residue chosen from the residues cited in the definition of Y.sup.4, which is seated between the carbon atoms, facing one another, situated on each
aromatic ring at the ortho position with respect to the carbon atom directly linked to the cation S.sup.+;  3-2) and/or at least one mono-sulfonium species possessing a single cationic center S.sup.+, per mol of cation and consisting of species of
formula (III.2): ##STR00046## in which Ar.sup.1 and Ar.sup.2 have the meanings given above in formula (III.1), including the possibility of directly linking to one another only one of the radicals Ar.sup.1 to Ar.sup.2 in the manner indicated above in the
definition of the additional condition which applies when t=1 in formula (III.1), involving the residue Y&#39;;  4) the organometallic salts of formula (IV): (L.sup.1L.sup.2L.sup.3M).sup.+q (IV) in which formula: M represents a metal of group 4 to 10 of the
Periodic Table;  L.sup.1 represents a ligand linked to the metal M by .pi.  electrons, a ligand chosen from the ligands .eta..sup.3-alkyl, .eta..sup.5-cycloheptatrienyl and .eta..sup.7-cycloheptatrienyl and the .eta..sup.6-aromatic compounds chosen from
the optionally substituted .eta..sup.6-benzene ligands and the compounds having from 2 to 4 fused rings, each ring being capable of contributing to the valency layer of the metal M by 3 to 8 .pi.  electrons;  L.sup.2 represents a ligand linked to the
metal M by .pi.  electrons, a ligand chosen from the ligands .eta..sup.7-cycloheptatrienyl and the .eta..sup.6-aromatic compounds chosen from the optionally substituted .eta..sup.6-benzene ligands and the compounds having from 2 to 4 fused rings, each
ring being capable of contributing to the valency layer of the metal M by 6 or 7 .pi.  electrons;  L.sup.3 represents from 0 to 3 identical or different ligands linked to the metal M by .sigma.  electrons, ligand(s) chosen from CO and NO.sub.2.sup.+;
the total electron charge q of the complex to which L.sup.1, L.sup.2 and L.sup.3 contribute and the ionic charge of the metal M being positive and equal to 1 or 2;  the anionic entity having the formula: [X.sup.1X.sup.2.sub.aR.sub.b].sup.- in which
formula: a and b are integers ranging, for a, from 0 to 6 and, for b, from 0 to 6 with a+b.gtoreq.2;  the symbols X.sup.1 represent elements chosen from groups 3A, 4A, 5A of the Periodic Table;  the symbols X.sup.2 represent: a halogen atom with a=0 to
3, an OR functional group with a=0 to 2;  the symbols R are identical or different and represent: a phenyl radical substituted with at least one electron-attracting group, and/or with at least 2 halogen atoms, and this being when the cationic entity is
an onium of an element of groups 15 to 17 of the Periodic Table, a phenyl radical substituted with at least one electron-attracting atom or one electron-attracting group, and this being when the cationic entity is an organo-metallic complex of an element
of groups 4 to 10 of the Periodic Table, an aryl radical containing at least two aromatic nuclei, optionally substituted with at least one element or one electron-attracting group, regardless of the cationic entity;  said composition comprising, in
addition, a silane substituted with CFG and hydrolyzable secondary functional groups (SFG), exposing the surface thus coated to actinic radiation and/or to a beam of electrons and/or to heat, so as to cause the crosslinking of the silicone composition
and obtain an antifriction layer, wherein said support comprises a substrate coated on at least one of its surfaces with at least one layer of silicone elastomer which is crosslinked or which is at least partially crosslinked.
The general field of the invention is that of polymer coatings or varnishes capable of conferring anti-friction properties on substrates.  More precisely, the invention relates to silicone compositions useful in particular for the production of
varnishes which can be applied to supports whose coefficient of friction it is sought to reduce.  The supports in question are varied and may consist in particular: of woven or nonwoven fibrous substrates coated with at least one layer for protection or
for mechanical reinforcement, based on a coating polymer of the silicone elastomer type for example; of polymer substrates, in particular plastic films such as for example: thermal transfer ribbons which can be used in particular as support for ink in
thermal transfer printers, or protective wrapping films,
The present invention also relates to the methods for applying the anti-friction varnish to which it relates, to various supports.
Finally, the subject of the invention is the supports coated with such anti-friction varnishes and, in particular: textile fabrics coated with an elastomer layer onto which the anti-friction varnish is applied, such fabrics being capable of being
used for the manufacture of bags for the personal protection of the occupants of vehicles, also called air bag, thermal transfer ribbons consisting for example of plastic films (e.g. made of polyester) carrying ink and which can be used in thermal
transfer printers, protective wrapping films.
The general problem forming the basis of the invention is the development of an anti-friction silicone varnish.  This problem of reducing coefficients of friction is posed with particular intensity for substrates coated with crosslinked
elastomeric silicone coatings.  Indeed, it is well known to persons skilled in the art that coating layers made of elastomeric silicone have a sticky feel which is damaging for numerous applications.
As regards more precisely the air bag application, it is known that these inflatable bags for the personal protection of the occupants of vehicles are made from a synthetic fiber fabric, for example made of polyamide (nylon.RTM.), coated on at
least one of its sides with a layer of an elastomer which may be a silicone elastomer which is cold crosslinkable or vulcanizable by polyaddition (CVEII), polycondensation (CVEI), a silicone elastomer which is hot crosslinkable or vulcanizable by
polycondensation with peroxide or by polyaddition (HVE) or a viscous silicone elastomer which is crosslinkable or vulcanizable by polyaddition of the LSR type.
This protective coating for example made of silicone is at least internal and makes it possible to guard against the effects of the explosion from the inflating of the bag.  The fact that the elastomeric silicone coating has a sticky feel
constitutes an impediment on the opening of the bag.  Improving the efficiency of the air bags therefore involves making them from a coated material with a low coefficient of friction.
For further details on air bags for personal protection, reference may be made in particular to French patent No. 2 668 106 and more especially to French patent No. 2 719 598 for air bags coated with an RTV silicone elastomer which is
crosslinkable by polyaddition.
This search for a low coefficient of friction for coatings on substrates coated or otherwise with silicone elastomer is also a concern in other applications such as, for example, coatings for thermal transfer ribbons (e.g. made of polyester) or
protective wrapping films (e.g. made of polyethylene or made of polypropylene.
The thermal transfer ribbons can be used in thermal transfer printers.  These thermal transfer ribbons are very thin (a few microns) and are coated, on one of their surfaces, with a layer of ink (waxes or resins) and on the other surfaces, with a
protective coating.  A very thin protective coating having a thickness of between 0.1 and 1 micrometer is generally used to protect the surface of the film and to improve the impact of the printing head without deforming the transfer of the ink onto the
applied support.
In printers whose printing speed is between 150 and 300 mm/s, it is very important for the printing head (flat or wedge-shaped), when it strikes the protective coating of the ribbon, to slide on the surface of the coating, at a high temperature
of between 100 and 200.degree.  C.
Faced with this problem, one of the essential objectives of the present invention is to propose to reduce the coefficient of friction of the substrate which may be coated with a coating layer, for example made of silicone, using an anti-friction
Another essential objective of the present invention is to provide a silicone composition which is useful in particular for the production of an anti-friction varnish, it being necessary for this composition to have a reasonable cost price and to
be simple to prepare.
Another essential objective of the invention is to provide an anti-friction varnish consisting of a crosslinkable silicone composition, capable of significantly reducing the coefficient of friction of various types of coated or uncoated
Another objective of the invention is to provide a simple and economical method of applying an anti-friction varnish based on a silicone composition to various supports consisting, for example, of woven or nonwoven fibrous substrates and
optionally coated, for example, with a layer of crosslinked silicone elastomer.
Another essential objective of the invention is to provide a fibrous support, for example a fabric, coated with a crosslinked elastomeric coating and endowed with a static coefficient of friction (Ks) corresponding to the force necessary to
initiate the movement of a rectangular mass covered with the fabric in question on a flat glass support at a value of Ks.ltoreq.1, for a coating deposit all layers sticking together D&amp;lt;20 g/m.sup.2.
These objectives, among others, are achieved by the present invention which relates, in the first place, to a silicone composition useful in particular for the production of varnish having in particular anti-friction properties, this composition
being of the type comprising at least one polyorganosiloxane (POS) which can be crosslinked by means of crosslinking functional groups (CFG) by the cationic and/or free-radical route and an effective quantity of a cationic initiator system comprising, as
thermal initiator and/or photoinitiator, a product chosen from the onium salts of an element of groups 15 to 17 of the Periodic Table [Chem &amp; Eng.  News, vol. 63, No. 5, of 4 Feb.  1985] or the salts of an organometallic complex of an element of groups 4
to 10 of the Periodic Table [same reference], whose cationic entity is selected from: 1) the onium salts of formula (I): [(R.sup.1).sub.n-A-(R.sup.2).sub.m].sup.+ (I) in which formula: A represents an element of groups 15 to 17 such as for example: I, S,
Se, P or N, R.sup.1 represents a carbocyclic or heterocyclic C.sub.6-C.sub.20 aryl radical, it being possible for said heterocyclic radical to contain, as heteroelements, nitrogen or sulfur; R.sup.2 represents R.sup.1 or a linear or branched
C.sub.1-C.sub.30 alkyl or alkenyl radical, said radicals R.sup.1 and R.sup.2 being optionally substituted with a C.sub.1-C.sub.25 alkoxy, C.sub.1-C.sub.25 alkyl, nitro, chloro, bromo, cyano, carboxyl, ester or mercapto group; n is an integer ranging from
1 to v+1, v being the valency of the element A, m is an integer ranging from 0 to v-1 with n+m=v+1, 2) the oxoisothiochromanium salts described in patent application WO 90/11303, in particular the sulfonium salt of 2-ethyl-4-oxoisothiochromanium or of
2-dodecyl-4-oxoisothiochromanium, 3) the sulfonium salts in which the cationic entity comprises: 3.1.  at least one polysulfonium species of formula III.1.
##STR00002## in which: the symbols Ar.sup.1, which may be mutually identical or different, each represent a monovalent phenyl or naphthyl radical optionally substituted with one or more radicals chosen from: a linear or branched
C.sub.1-C.sub.12, preferably C.sub.1-C.sub.6, alkyl radical, a linear or branched C.sub.1-C.sub.12, preferably C.sub.1-C.sub.6, alkoxy radical, a halogen atom, an --OH group, a --COOH group, an ester group --COO-alkyl where the alkyl portion is a linear
or branched C.sub.1-C.sub.12, preferably C.sub.1-C.sub.6, residue, and a group of formula --Y.sup.4--Ar.sup.2 where the symbols Y.sup.4 and Ar.sup.2 have the meanings given just below, the symbols Ar.sup.2, which may be mutually identical or different or
with Ar.sup.1, each represents a monovalent phenyl or naphthyl radical optionally substituted with one or more radicals chosen from: a linear or branched C.sub.1-C.sub.12, preferably C.sub.1-C.sub.6, alkyl radical, a linear or branched C.sub.1-C.sub.12,
preferably C.sub.1-C.sub.6, alkoxy radical, a halogen atom, an --OH group, a --COOH group, an ester group --COO-alkyl where the alkyl portion is a linear or branched C.sub.1-C.sub.12, preferably C.sub.1-C.sub.6, residue, the symbols Ar.sup.3, which may
be mutually identical or different, each represent a divalent phenylene or naphthylene radical optionally substituted with one or more radicals chosen from: a linear or branched C.sub.1-C.sub.12, preferably C.sub.1-C.sub.6, alkyl radical, a linear or
branched C.sub.1-C.sub.12, preferably C.sub.1-C.sub.6, alkoxy radical, a halogen atom, an --OH group, a --COOH group, an ester group --COO-alkyl where the alkyl portion is a linear or branched C.sub.1-C.sub.12, preferably C.sub.1-C.sub.6, residue, t is
an integer equal to 0 or 1, with the additional conditions according to which: when t=0, the symbol Y is then a monovalent radical Y.sup.1 representing the group of formula:
##STR00003## where the symbols Ar.sup.1 and Ar.sup.2 have the meanings given above, when t=1: on the one hand, the symbol Y is then a divalent radical having the following meanings Y.sup.2 to Y.sup.4: Y.sup.2: a group of formula:
##STR00004## where the symbol Ar.sup.2 has the meanings given above, Y.sup.3: a single valency bond, Y.sup.4: a divalent residue chosen from:
##STR00005## a linear or branched C.sub.1-C.sub.12, preferably C.sub.1-C.sub.6, alkylene residue, and a residue of formula --Si(CH.sub.3).sub.2O--, on the other hand, in the case solely where the symbol Y represents Y.sup.3 or Y.sup.4, the
radicals Ar.sup.1 and Ar.sup.2 (terminal) possess, in addition to the meanings given above, the possibility of being linked to each other by the residue Y&#39; consisting in Y&#39;.sup.1 a single valency bond or in Y&#39;.sup.2 a divalent residue chosen from the
residues cited in relation to the definition of Y.sup.4, which is seated between the carbon atoms, facing one another, situated on each aromatic ring at the ortho position with respect to the carbon atom directly linked to the cation S.sup.+; 3.2.
and/or at least one mono-sulfonium species possessing a single cationic center S+per mol of cation and consisting in most cases in species of formula:
##STR00006## in which Ar.sup.1 and Ar.sup.2 have the meanings given above in relation to formula (III.1), including the possibility of directly linking to one another only one of the radicals Ar.sup.1 to Ar.sup.2 in the manner indicated above in
relation to the definition of the additional condition which applies when t=1 in formula (III.I), involving the residue Y&#39;; 4) the organometallic salts of formula (IV): (L.sup.1L.sup.2 L.sup.3M).sup.+q (IV) in which formula: M represents a metal of group
4 to 10, in particular iron, manganese, chromium, cobalt and the like L.sup.1 represents 1 ligand linked to the metal M by .pi.  electrons, a ligand chosen from the ligands .eta..sup.3-alkyl, .eta..sup.5-cyclopendadienyl and
.eta..sup.7-cycloheptratrienyl and the .eta..sup.6-aromatic compounds chosen from the optionally substituted .eta..sup.6-benzene ligands and the compounds having from 2 to 4 fused rings, each ring being capable of contributing to the valency layer of the
metal M by 3 to 8 .pi.  electrons; L.sup.2 represents a ligand linked to the metal M by .pi.  electrons, a ligand chosen from the ligands .eta..sup.7-cycloheptatrienyl and the .eta..sup.6-aromatic compounds chosen from the optionally substi-tuted
.eta..sup.6-benzene ligands and the compounds having from 2 to 4 fused rings, each ring being capable of contributing to the valency layer of the metal M by 6 or 7 .pi.  electrons; L.sup.3 represents from 0 to 3 identical or different ligands linked to
the metal M by .sigma.  electrons, ligand(s) chosen from CO and NO.sub.2.sup.+; the total electron charge q of the complex to which L.sup.1, L.sup.2 and L.sup.3 contribute and the ionic charge of the metal M being positive and equal to 1 or 2; the
anionic entity having the formula: [X.sup.1X.sup.2.sub.aR.sub.b]-- in which formula: a and b are integers ranging, for a, from 0 to 6 and, for b, from 0 to 6 with a+b.gtoreq.2; the symbols X.sup.1 represent elements chosen from groups IIIA, IVA, VA of
the Periodic Table, preferably from the group comprising: B, P and Sb; the symbols X.sup.2 represent: a halogen atom (chlorine, fluorine) with a=0 to 3, an OH functional group with a=0 to 2, the symbols R are identical or different and represent: a
phenyl radical substituted with at least one electron-attracting group such as for example OCF.sub.3, CF.sub.3, NO.sub.2, CN, and/or with at least 2 halogen atoms (fluorine most particu-larly), and this being when the cationic entity is an onium of an
element of groups 15 to 17, a phenyl radical substituted with at least one element or one electron-attracting group, in particular a halogen atom (fluorine most particularly), CF.sub.3, OCF.sub.3, NO.sub.2, CN, and this being when the cationic entity is
an organo-metallic complex of an element of groups 4 to 10 an aryl radical contain-ing at least two aromatic nuclei such as for example biphenyl, naphthyl, optionally substituted with at least one element or one electron-attracting group, in particular a
halogen atom (fluorine most particularly), OCF.sub.3, CF.sub.3, NO.sub.2, CN, regardless of the cationic entity; this composition being characterized in that it comprises, in addition, molecules substituted with secondary functional groups (SFG) carried
by at least one silicon atom per molecule and preferably selected from those comprising at least one alkoxy and/or enoxy and/or carboxyl unit.
The silicone varnish composition according to the invention is advantageous in that it can be easily and industrially crosslinked by the cationic and/or free-radical route, by exposing to a beam of electrons and/or to actinic radiation of the UV
type and/or by thermal activation.  Once applied and crosslinked on a support, this varnish confers significant antifriction characteristics thereon.
These advantageous results stem from the judicious selection of a silicone varnish composition comprising compounds in which the silicon atoms (POS-silanes) carry crosslinking functional groups CFG as well as functional groups SFG, advantageously
of alkoxy and/or enoxy and/or carboxyl type.  The SFGs have a significant role in providing the antifriction properties to the coating composition.  The fact that this silicone varnish composition can be easily applied and crosslinked on a support, for
example a fabric or a plastic film, also stems from the use of a specific photoinitiator family of the type described in French patent application No. 96 16237 whose entire content is included by reference in the present application.  Such
photoinitiators allow rapid and complete photocrosslinking of the varnish.
According to a first embodiment of the invention, the silicone varnish composition comprises: A--at least one POS carrying CFGs, the latter being preferably chosen from the groups comprising at least one ethylenically unsaturated functional
group--advantageously acrylate and/or alkenyl ether--and/or epoxide and/or oxethane; B--at least one silane and/or one POS carrying SFGs, the latter preferably representing at least 0.5% and more preferably still at least 1% by weight of B; C--at least
one photoinitiator system as defined above.
In this first embodiment, the CFGs, on the one hand, and the SFGs, on the other hand, are carried by different molecules or macromolecules based on silicon.
The alternative which corresponds to the second embodiment of the invention is that these silicon-based molecules are substituted both with CFG groups and with SFG groups.  In this case, the silicone varnish composition according to the invention
comprises: C--at least one photoinitiator system as defined above, D--at least one POS carrying CFGs and SFGs, the CFGs being preferably chosen from groups comprising at least one ethylenically unsaturated functional group-- advantageously acrylate
and/or alkenyl ether--and/or epoxide and/or oxethane;
These hardening (for example under UV and/or under a beam of electrons) varnish compositions providing surface antifriction properties may comprise in addition: F--optionally at least one organic reactive diluent chosen from organic resins of the
epoxide and/or vinyl ether and/or oxethane type; G--optionally at least one organic or inorganic pigment; H--optionally a filler, preferably a silicic filler; I--optionally at least one photosensitizer, preferably selected from (poly)aromatics
(optionally metallic) and/or heterocyclics.
Entering into detail on the nature of the various constituents of the silicone varnish composition according to the invention, it will be specified, as regards the POSs A, that they are preferably epoxysilicones and/or vinyl ether silicones which
are: either linear or substantially linear and consist of units of formula II.1, ending with units of formulae (II.2) or cyclic and consisting of units of formula (11.1):
##STR00007## in which formulae: the symbols R.sup.1 are similar or different and represent: either a linear or branched C.sub.1-C.sub.6 alkyl radical optionally advantageously substituted with one or more halogens, the preferred optionally
substituted alkyl radicals being: methyl, ethyl, propyl, octyl and 3,3,3-trifluoropropyl, or an optionally substituted C.sub.1-C.sub.8 cycloalkyl radical, or an aryl or aralkyl radical optionally substituted: in particular with halogens and/or alkoxyls,
the phenyl, xylyl, tolyl and dichlorophenyl radicals being most particularly selected, and, more preferably still, at least 60 mol % of the R.sup.3 radicals being methyls, the symbols Z are similar or different and represent: either the radical R.sup.1,
or a CFG group corresponding to an epoxide or vinyl ether residue linked to the silicon by means of a divalent radical advantageously containing from 2 to 20 carbon atoms optionally comprising a heteroatom, at least one of the symbols Z corresponding to
a CFG group.
As examples of organofunctional CFG groups of the epoxy type, there may be mentioned those of the following formula:
As regards the organofunctional CFG groups of the vinyl ether type, there may be mentioned, e.g., those contained in the following formulae:
##STR00009## with R.sup.40.dbd.  optionally substituted linear or branched C.sub.1-C.sub.12 alkylene, or arylene, preferably phenylene, optionally substituted preferably with one to three C.sub.1-C.sub.6 alkyl groups; with R.sup.50=linear or
branched C.sub.1-C.sub.6 alkyl.
The preferred epoxy or vinyloxyfunctional polyorganosiloxanes are described in particular in patents DE-A-4 009 889; EP-A-0 396 130; EP-A-0 355 381; EP-A-0 105 341; FR-A-2 110 115; FR-A-2 526 800.
The functional epoxy polyorganosiloxanes may be prepared by hydrosilylation reaction between oils with Si--H units and epoxyfunctional compounds, such as 4-vinylcyclohexene oxide, allyl glycidyl ether and the like.
The vinyloxyfunctional polyorganosiloxanes may be prepared by hydrosilylation reaction between oils with Si--H units and vinyloxyfunctional compounds, such as allyl vinyl ether, allyl-vinyloxyethoxybenzene and the like.
More preferably still, the POSs A are epoxysilicones of the following formulae (A.I) (A.II):
##STR00010## with X.dbd.CH.sub.3; Phenyl; Cycloalkyl; C.sub.1-C.sub.8 alkyl; alkenyl; --OH; H; CH.sub.2--CH.sub.2--CH.sub.2--OH; CH.sub.2--CH.sub.2--CF.sub.3; --(CH.sub.2).sub.n--CF.sub.3, n=1 to 20;
##STR00011## a.sub.1, a.sub.2 and b.sub.1, b.sub.2 being defined as below in these formulae (A.I) and (A.II) 1.ltoreq.a.sub.1, a.sub.2 1.ltoreq.b.sub.1, b.sub.2 preferably 1.ltoreq.a.sub.1, a.sub.2.ltoreq.5 000 1.ltoreq.b.sub.1,
b.sub.2.ltoreq.500 and more preferably still 1.ltoreq.a.sub.1, a.sub.2.ltoreq.1 000 1.ltoreq.b.sub.1, b.sub.2.ltoreq.100; a.sub.2, b.sub.2 being=0 in formula (A.II) to give the epoxydized disiloxane (A.III).
According to another advantageous characteristic of the invention, the POS(s) (A) has (have) a viscosity .eta.  (expressed in mPas at 25.degree.  C.) of between: 200 and 3 000, preferably 300 and 2 000, and more preferably still between 400 and
These viscosity values relate both to the linear POSs and the cyclic POSs which are capable of being used in accordance with the use according to the invention.
The dynamic viscosity at 25.degree.  C. of all the silicone polymers considered in the present disclosure may be measured using a BROOKFIELD viscometer, according to the AFNOR standard NFT 76 102 of February 1972.
The viscosity in question in the present disclosure is the dynamic viscosity at 25.degree.  C., called &quot;Newtonian&quot; viscosity, that is to say the dynamic viscosity which is measured, in a manner known per se, at a sufficiently low shearing speed
gradient for the measured viscosity to be independent of the speed gradient.
As regards the compound(s) B, it is advantageous in accordance with the invention that it/they is/are chosen from that (or those) of the following formula B: R.sup.2.sub.x[SFG].sub.ySiO.sub.4-(x+y)/2 (B) in which: x=0, 1, 2 or 3 y=1, 2, 3 or 4
the radicals R.sup.2 are mutually identical or different and correspond to a linear or branched alkyl, a cycloalkyl, a hydroxyl, a hydrogen, a vinyl, a --CF.sub.3, a --(CH.sub.2).sub.m--CF.sub.3 with m=1 to 50, the SFGs are mutually identical or
different and correspond to an alkoxy, preferably: --OR.sup.3 with R.sup.3 representing a linear or branched C.sub.1-C.sub.30 alkyl or a cycloalkyl; --(OR.sup.4).sub.n--OR.sup.5; --(R.sup.6).sub.q--Si(OR.sup.7).sub.r(R.sup.8).sub.t with R.sup.4, R.sup.7,
R.sup.8 mutually identical or different and having the same definition as that given above for R.sup.3 and with R.sup.6 mutually identical or different and preferably corresponding to an alkylene (advantageously a methylene); p, q=1 to 50, preferably 1
to 10; r=1, 2 or 3 and t=0, 1 or 2; an enoxy, preferably: --O--CH.dbd.CH--R.sup.8; --(R.sup.9).sub.u--Si(OCH.dbd.CHR10).sub.v(R.sup.11).sub.w; with R.sup.8, R.sup.10, R.sup.11 mutually identical or different and having the same definition as that given
above for R.sup.3, and with R.sup.9 having the same definition as that given above for R.sup.6; u=1 to 50, preferably 1 to 10, v=1, 2 or 3 and w=0, 1 or 2; a carboxyl, preferably: --OCOR.sup.2; --(R.sup.13).sub.z--Si(OCOR.sup.14).sub.z1(R.sup.15).sub.z2;
with R.sup.12, R.sup.14 as defined above for R.sup.8, R.sup.10, R.sup.11; R.sup.13 as defined above for R.sup.9; and z=1 to 50, preferably 1 to 10, z.sub.1=1, 2 or 3 and z.sub.2=0, 1 or 2;
By way of example of POS B, there may be mentioned:
##STR00012## with Et=ethyl.
By way of example of silane B, there may be mentioned: MeSi(OEt).sub.3; Si(OEt).sub.4; PrSi(OEt).sub.3; OctSi(OMe).sub.3; PrSi(OMe).sub.3; and the like
with Me=methyl; Et=ethyl; Pr=propyl, Oct=octyl.
In accordance with the second embodiment, mixed POSs D comprising both CFGs and SFGs are used.  Without that being limiting, it is found that this second embodiment is more especially preferred.  Thus, the POSs D used advantageously comprise SFGs
as defined above and CFGs of the epoxide type.
More preferably still, said POS D corresponds to the POSs of the following formulae (D&#39;, D&#39;&#39;, D&#39;&#39;&#39;):
##STR00013## with 0.ltoreq.d.sub.1 1.ltoreq.d.sub.2 1.ltoreq.d.sub.3 preferably 0.ltoreq.d.sub.1.ltoreq.5 000 1.ltoreq.d.sub.2.ltoreq.500 1.ltoreq.d.sub.3.ltoreq.500 and more preferably still 0.ltoreq.d.sub.1.ltoreq.1 000
1.ltoreq.d.sub.2.ltoreq.100 1.ltoreq.d.sub.3.ltoreq.100
##STR00014## with Me=methyl; Et=ethyl 0.ltoreq.e preferably 0.ltoreq.e.ltoreq.5 000 and more preferably still 0.ltoreq.e.ltoreq.1 000
In the case where the compound D is a silane comprising both CFGs of the (Meth)acrylate and/or vinyl ether and/or epoxide and/or oxethane--preferably epoxide--type--as well as SFGs--preferably of the alkoxy type--, it may include for example the
According to a preferred characteristic of the invention, the initiators C are e.g.: the onium borates described in European patent application No. 0 562 922 whose entire content is included by reference in the present application.  More
precisely still, there may be used in practice the initiator of the following formula:
In practice, the initiators for the use according to the invention are prepared in a very simple manner by dissolving the onium borate or organometallic complex, preferably of onium, provided in solid (powder) form in a solvent.
Preferably, it is envisaged in accordance with the use according to the invention that the initiator is used in solution in an organic solvent, preferably chosen from solvents which are proton donors and more preferably still from the following
group: isopropyl alcohol, isobenzyl alcohol, diacetone alcohol, butyl lactate, esters, and mixtures thereof.  As is claimed in French patent No. 2 724 660, organic solvents which are proton donors and which have an aromatic character (benzyl alcohol)
behave as crosslinking accelerators.  It is therefore advantageous to use them to dissolve the photoinitiator.
Since in practice--as indicated above--the photoinitiator is advantageously dissolved in a polar solvent, in a quantity such that its titer in the solution obtained is between 1 and 50% by weight, preferably between 10 and 30% by weight, and more
preferably still between 15 and 25% by weight.
According to an advantageous feature of the use according to the invention, the incorporation of the photoinitiator in solution into the composition comprising the POS at a given molar content of CFG is carried out at the rate of 0.1 to 10% by
weight of solution relative to the final mixture and preferably 0.5 to 5% by weight and more preferably of the order of 1% by weight.
According to one variant of the use in accordance with the invention, crosslinking inhibitors may be used which are preferably chosen from alkaline products, and more preferably still from alkaline products of the amine-containing type, for
example of the type consisting of a silicone onto which at least one amine group, preferably a tertiary amine group, is grafted.
As regards the optional additives, there may be mentioned in relation to the optional reactive diluent E that the compounds of formula E&#39; (epoxide) and E&#39;&#39; (vinyl ether) are examples among others:
The optional inorganic or organic pigments F are added to give color to the silicone varnish according to the invention.  In particular, this color makes it possible to recognize a nonvarnished fabric from a varnished fabric merely at a glance.
The fillers G and in particular the silicic fillers may be for example pyrogenic silicas treated with hexamethyldisilasanes or with octamethylcyclotetrasiloxanes (specific surface area 300 m.sup.2/g), fumed silica.
As regards the optional photosensitizers H, they may be selected from (poly)aromatic products--optionally metallic--and heterocyclic products, and preferably from the list of the following products: phenothiazine, tetracene, perylene, anthracene,
9,10-diphenylanthracene, thioxanthone, benzophenone, acetophenone, xanthone, fluorenone, anthraquinone, 9,10-dimethylanthracene, 2-ethyl-9,10-dimethyloxyanthracene, 2,6-dimethylnaphthalene, 2,5-diphenyl-1-3-4-oxadiazole, xanthopinacol,
1,2-benzanthracene, 9-nitroanthracene, and mixtures thereof.
More especially, they may be a product H based on thioxanthone:
Taking into account its ease of production its low cost and its antifriction properties, the silicone varnish according to the invention may have uses in numerous fields of application and in particular in the field of the coating of woven or
nonwoven fibrous supports.
It follows therefrom that the invention relates, according to another of its aspects, to the application of the composition as described above as antifriction varnish to a support, this support preferably comprising a substrate--advantageously
fibrous (and more especially textile)--optionally coated with at least one silicone elastomer layer which is at least partially crosslinked.
Advantageously, this method of application essentially consists: in coating a support with the varnish composition as defined above, and in exposing the surface thus coated to actinic radiation and/or to a beam of electrons and/or to heat, so as
to cause the crosslinking of the varnish layer.
The means of applying the layer of noncrosslinked varnish to the support are of the type known and appropriate for this purpose (bar or roll for coating).  The same applies as regards the means of exposing, for example, to UV radiation and/or to
the electron beams.
Other details will be given in this regard in the examples which follow.
According to a preferred embodiment of this varnish support, the latter comprises a substrate--preferably textile--coated on at least one of its surfaces with at least one layer of silicone elastomer which can be crosslinked or which is at least
partially crosslinked, preferably chosen from: the polyaddition or polycondensation RTV silicones, and/or the peroxide HVE silicones, and/or the polyaddition LSR silicones, the antifriction varnish obtained from the composition as defined above being
applied to the (top) layer(s) of silicone elastomer.  The expressions RTV, LSR and HVE are well known to persons skilled in the art: RTV is the abbreviation for &quot;room temperature vulcanizing&quot;; LSR is the abbreviation for &quot;liquid silicone rubber&quot;; HVE is
the abbreviation for hot vulcanizable elastomer.
In practice, the invention relates more precisely to the supports (for example textiles such as those used for the manufacture of air bags) coated on one and/or the other of their surfaces with a layer of crosslinked silicone elastomer RTV, HVE
or LSR, itself coated with a coating of antifriction silicone varnish as defined above.
The polyorganosiloxanes, principal constituents of the sticky layers of crosslinked elastomers onto which the varnish according to the invention may be applied, may be linear, branched or crosslinked, and may comprise hydrocarbon radicals and/or
reactive groups such as for example hydroxyl groups, hydrolysable groups, alkenyl groups and hydrogen atoms.  It should be noted that the polyorganosiloxane compositions are fully described in the literature and in particular in the book by Walter NOLL:
&quot;Chemistry and Technology of Silicones&quot;, Academic Press, 1968, 2nd edition, pages 386 to 409.
More precisely, these varnishable polyorganosiloxanes consist of siloxyl units of general formula:
.times..times..degree..times.&#39; ##EQU00001## and/or siloxyl units of formula:
.times..times..degree..times..times..times..degree..times.&#39; ##EQU00002## in which formulae the various symbols have the following meaning: the symbols R.sup.o, which are identical or different, each represent a group of a nonhydrolysable
hydrocarbon nature, it being possible for this radical to be: an alkyl radical, a haloalkyl radical having from 1 to 5 carbon atoms and comprising from 1 to 6 chlorine atoms and/or fluorine atoms, cycloalkyl and halocycloalkyl radicals having from 3 to 8
carbon atoms and containing from 1 to 4 chlorine and/or fluorine atoms, aryl, alkylaryl and haloaryl radicals having from 6 to 8 carbon atoms and containing from 1 to 4 chlorine and/or fluorine atoms, cyanoalkyl radicals having from 3 to 4 carbon atoms;
the symbols Z.sup.o, which are identical or different, each represent a hydrogen atom, a C.sub.2-C.sub.6 alkenyl group, a hydroxyl group, a hydrolysable atom, a hydrolysable group; n.sub.1=an integer equal to 0, 1, 2 or 3; x.sub.1=an integer equal to 0,
1, 2 or 3; Y.sub.1=an integer equal to 0, 1 or 2; the sum x+y is between 1 and 3.
By way of illustration, there may be mentioned among the organic radicals R.sup.o directly linked to the silicon atoms: the groups methyl; ethyl; propyl; isopropyl; butyl; isobutyl; n-pentyl; t-butyl; chloromethyl; dichloromethyl;
.alpha.-chloroethyl; .alpha.,.beta.-dichloroethyl; fluoromethyl; difluoromethyl; .alpha.,.beta.-difluoroethyl; 3,3,3-trifluoropropyl; trifluorocyclopropyl; 4,4,4-trifluorobutyl; 3,3,4,4,5,5-hexafluoropentyl; .beta.-cyanoethyl; .gamma.-cyanopropyl;
phenyl: p-chlorophenyl; m-chlorophenyl; 3,5-dichlorophenyl; trichlorophenyl; tetrachlorophenyl; o-, p- or m-tolyl; .alpha.,.alpha.,.alpha.-trifluorotolyl; xylyl like 2,3-dimethylphenyl, 3,4-dimethylphenyl.
Preferably, the organic radicals R.sup.o linked to the silicon atoms are methyl or phenyl radicals, it being possible for these radicals to be optionally halogenated or even cyanoalkyl radicals.
The symbols Z.sup.o may be hydrogen atoms, hydrolysable atoms such as halogen atoms, in particular chlorine atoms, vinyl or hydroxyl groups or hydrolysable groups such as for example: amino, amido, aminoxy, oxime, alkoxy, alkenyloxy, acyloxy.
The nature of the polyorganosiloxane and therefore the ratios between the siloxyl units (I&#39;) and (II&#39;&#39;) and the distribution thereof is, as is known, chosen according to the crosslinking treatment which will be carried out on the curable (or
vulcanizable) composition with a view to its conversion to an elastomer.
The bicomponent or monocomponent polyorganosiloxane compositions which crosslink at room temperature (RTV) or with heat (HVE) by polyaddition reactions, essentially by reaction of hydrogenosilylated groups with alkenylsilylated groups, in the
presence generally of a metal catalyst, preferably platinum, are described for example in patents U.S.  Pat.  Nos.  3,220,972, 3,284,406, 3,436,366, 3,697,473 and 4,340,709.  The polyorganosiloxanes entering into these compositions consist in general of
pairs based, on the one hand, on a linear, branched or crosslinked polysiloxane consisting of units (II) in which the residue Z.sup.o represents a C.sub.2-C.sub.6 alkenyl group and where x.sub.1 is at least equal to 1, optionally combined with units
(I&#39;), and on the other hand on a linear, branched or crosslinked hydrogenopolysiloxane consisting of units (II&#39;) in which the residue Z.sup.o then represents a hydrogen atom and where x.sub.1 is at least equal to 1, optionally combined with units (I&#39;).
The bicomponent or monocomponent polyorganosiloxane compositions crosslinking at room temperature (RTV) by polycondensation reactions under the action of moisture, generally in the presence of a metal catalyst, for example a tin compound are
described for example for the monocomponent compositions in patents U.S.  Pat.  Nos.  3,065,194, 3,542,901, 3,779,986, 4,417,042, and in patent FR-A-2 638 752, and for the bicomponent compositions in patents U.S.  Pat.  Nos.  3,678,002, 3,888,815,
3,933,729 and 4,064,096.  The polyorganosiloxanes entering into these compositions are in general linear, branched or crosslinked polysiloxanes consisting of units (II&#39;) in which the residue Z.sup.o is a hydroxyl group or a hydrolysable group or atom and
where x.sub.1 is at least equal to 1, with the possibility of having at least one residue Z.sup.o which is equal to a hydroxyl group or to an atom or to a hydrolysable group and at least one residue Z.sup.o which is equal to an alkenyl group when x.sub.1
is equal to 2 or 3, said units (II&#39;) being optionally combined with units (I&#39;).  Parallel compositions may contain in addition a crosslinking agent which is in particular a silane carrying at least three hydrolysable groups such as for example a
These RTV polyorganosiloxane compositions which crosslink by polyaddition or polycondensation reactions advantageously have a viscosity at 25.degree.  C. at most equal to 100 000 mPas and preferably of between 10 and 50 000 mPas.
It is possible to use RTV compositions which crosslink at room temperature by polyaddition or polycondensation reactions, having a viscosity at 25.degree.  C. greater than 100 000 mPas, such as that situated in the interval ranging from a value
greater than 100 000 mPas to 300 000 mPas; this feature is recommended when it is desired to prepare charged curable compositions in which the filler(s) used has (have) a tendency to separate by sedimentation.
It is also possible to use compositions which crosslink with heat by polyaddition reactions and more precisely so-called polyaddition HVE type compositions having a viscosity at 25.degree.  C. at least equal to 500 000 mPas and preferably of
between 1 million mPas and 10 million mPas and even more.
This may also include compositions curable at high temperature under the action of organic peroxides such as 2,4-dichlorobenzoyl peroxide, benzoyl peroxide, t-butyl perbenzoate, cumyl peroxide, di-t-butyl peroxide.  The polyorganosiloxane or gum
entering into such compositions (termed simply of the HVE type) then essentially consists of siloxyl units (I&#39;), optionally combined with units (II&#39;) in which the Z.sup.o residue represents a C.sub.2-C.sub.6 alkenyl group and where x is equal to 1.  Such
HVEs are for example described in patents U.S.  Pat.  Nos.  3,142,655, 3,821,140, 3,836,489 and 3,839,266).  These compositions advantageously have a viscosity at 25.degree.  C. at least equal to 1 million mPas and preferably of between 2 million and 10
million mPas and even more.
Other polyorganosiloxane compositions which can be varnished with the silicone varnish composition according to the invention are those, monocomponent or bicomponent, which crosslink with heat by polyaddition reactions, called LSR compositions.
These compositions correspond to the definitions given above in relation to the preferred compositions called RTV, except as regards their viscosity which is situated, this time, in the interval ranging from a value greater than 100 000 mPas to 500 000
Without this being limiting, the elastomeric silicone coatings onto which the varnish according to the invention may be applied in order to reduce their coefficient of friction, are more especially coatings obtained from compositions of silicone
elastomers which are cold vulcanizable RTV, in particular of the bicomponent type (RTV 2), by polyaddition.
It results therefrom that another subject of the invention consists of the varnish support as defined above, characterized in that it is intended to be used for the manufacture of inflatable bags for the personal protection of the occupants of
In the context of this air bag application, the RTV elastomeric silicone coatings more particularly in question may be those belonging to the four groups (i) (ii) (iii) and (iv) as defined below.  (i) silicone elastomer composition for coating of
the RTV 2 type comprising at least one POS I of the SiVi type, at least one POS II of the SiH type, a platinum-based hydrosilylation catalyst III, an adhesion promoter IV comprising at least one alkoxylated organosilane IV.1 containing per molecule at
least one vinyl (vinyltrimethoxysilane) group, at least one organosilicon-containing compound IV.2 comprising at least one epoxy radical (3-glycidoxypropyltrimethoxysilane (GLYMO) and at least one chelate IV.3 of a metal M and/or a metal alkoxide (butyl
titanate).  These polyaddition RTV silicone coatings for air bags are described in French patent No. 2 719 598 (No. 94 05 652).  (ii) Polyaddition RTV 2 silicone elastomer obtained from a composition comprising POSs type I SiVi and POSs type II SiH, as
well as a particulate filler obtained by treatment using a compatibility-promoting agent introduced into the preparation medium: on the one hand, before and/or substantially simultaneously with the bringing into contact with a portion of the silicone oil
used with a portion of the particulate filler, this introduction of compatibility-promoting agent being carried out once or several times for a fraction of compatibility-promoting agent represents at most 8% by dry weight of the total particulate filler;
and, on the other hand, after this POS/filler bringing into contact.  The compatibility-promoting agent is hexamethyldisilasane HMDZ.  The oil SiVi is an .alpha.,.omega.-divinyl-containing polydimethylsiloxane and the oil II SiH is an
.alpha.,.omega.-dihydrogeno polydimethylsiloxane and a polyhydrogeno oil PDMS.  This RTV elastomer composition (ii) which can be crosslinked by polyaddition and comprises a particulate charge made compatible in a particular manner with HMDZ, is described
in detail in French patent application No. 97 08 171.  (iii) RTV silicone elastomer coating crosslinked by polycondensation and comprising a silicic particulate filler treated using a compatibility-promoting agent introduced into the preparation medium,
on the one hand, before and/or substantially simultaneously with the bringing into contact of a portion of the silicone oil used with a portion of the particulate filler, this introduction of compatibility-promoting agent being carried out once or
several times for a fraction of compatibility-promoting agent represents at most 8% by dry weight of the total particulate filler; and, on the other hand, after this POS/filler bringing into contact.  The compatibility-promoting agent is
hexamethyldisilasane HMDZ.  These polycondensation RTV silicone coatings whose filler is treated in a specific manner with HMDZ, which are intended in particular for the coating of textile fabric for air bags, are described in French patent application
No. 98 16 467 describing compositions comprising: 1--at least one linear reactive POS carrying at each chain end at least two condensable groups (other than OH) or which is hydrolysable, or a single hydroxyl group, 2--optionally at least one linear
nonreactive POS carrying no condensable group, which is hydrolysable or a hydroxyl group, 3--optionally water, 4--a particulate reinforcing filler based on silica treated with a compatibility-promoting agent (hexamethyldisilazane), this
compatibility-promoting agent being introduced into the composition before and after the incorporation of the reinforcing filler into at least a portion of the silicone material, the fraction of compatibility-promoting agent introduced before the
incorporation of the filler representing from 8 to 30% by weight of the reinforcing filler used.  (POS 1=polydimethylsiloxane.alpha.,.omega.-(CH.sub.3).sub.3SiO.sub.1/2; POS 2=polydimethylsiloxane.alpha.,.omega.-(CH.sub.3).sub.2OHSiO.sub.1/2); (iv) RTV
silicone elastomer coating crosslinked by polyaddition and obtained from a coating composition comprising: (1) at least one polyorganosiloxane having, per molecule, at least two C.sub.2-C.sub.6 alkenyl groups linked to the silicon (e.g.
PolyDimethylSiloxane (PDMS-.alpha.,.omega.  vinylated); (2) at least one polyorganosiloxane having, per molecule, at least two hydrogen atoms linked to the silicon (e.g. PDMS .alpha.,.omega.  dihydrogeno and PDMS polyhydrogeno), (3) a catalytically
effective quantity of at least one catalyst composed of at least one metal belonging to the platinum group (e.g.: KARSTEDT 10% Pt) (4) a ternary adhesion promoter consisting of: (4.1.) at least one alkoxylated organosilane containing, per molecule, at
least one C.sub.3-C.sub.6 alkenyl group (e.g.: .gamma.-methacryloxypropylated trimethoxysilane) (4.2.) at least one organosilicon-containing compound comprising at least one epoxy radical (e.g.: .gamma.-glycidoxypropyl trimethoxysilane) (4.3) at least
one metal M chelate and/or one metal alkoxide of general formula: M(OJ)n, with n=valency of M and J=linear or branched C.sub.1-C.sub.8 alkyl, M being chosen from the group formed by: Ti, Zr, Ge, Li, Mn, Fe, Al and Mg (e.g.: butyl titanate).  (5) a
reinforcing siliceous filler treated in situ with a compatibility-promoting agent (e.g.: HMDZ) in the presence of polyorganosiloxane (1), (6) a so-called extending polyorganosiloxane having terminal siloxyl units with hydrogeno functional groups (e.g.
PDMS .alpha.,.omega.-hydrogeno--RHODORSIL.RTM.  620 from RHODIA CHIMIE) (7) optionally a neutralizing agent, (8) optionally a crosslinking inhibitor and/or other additive(s) in use in this type of compositions (e.g.: ethynylcyclohexanol).  (9) and
optionally expanded or expandable inorganic hollow microspherical fillers, in which method a suspension of reinforcing siliceous filler is prepared by bringing this siliceous filler into contact with the compatibility-promoting agent and
polyorganosiloxane (1), which constitutes the in situ treatment of the filler.
All these crosslinkable and/or crosslinked RTV elastomeric silicone compositions are prepared in a conventional manner (bicomponent precursor system) and are described for example in French patent No. 2 719 598, as regards the RTVs (iv).
Once the bicomponent impasting has been carried out, it is applied to the support by any appropriate means of coating, for example a scraper or a roller.  The crosslinking of the layer coated onto the support may be caused, for example, by the
thermal route and/or by UV radiation.
The support thus coated may be a flexible material such as, for example, an advantageously woven fibrous support made of synthetic fibers, e.g. polyester or polyamide.  Such coated tissues may be used for the manufacture, by sewing, of an
inflatable bag for an automobile (air bag).
Once the support has been coated with the crosslinked RTV elastomer layer, the antifriction silicon varnish is applied in accordance with the invention and then the crosslinking of said varnish is carried out by exposure to actinic radiation or
to electron beams.
In addition to the textile supports coated with silicone, the antifriction varnish according to the invention may be applied: to plastic films (e.g. made of polyester) such as thermal transfer ribbons for printers of the same name, or to
protective wrapping plastic films (e.g. made of polyethylene or of polypropylene).
In these two applications, the antifriction varnish according to the invention will promote the sliding of at least one of the surfaces of the plastic film, it being possible for this surface to be coated with at least one silicone layer.
The examples which follow describe: the preparation of the antifriction varnish compositions according to the invention, the application of the latter: to fabric supports coated with a polyaddition RTV crosslinked silicone elastomer, to thermal
transfer ribbons comprising a polyester film of a few microns, and to polyethylene wrapping films.  and the evaluation of the samples thus obtained in terms of coefficient of friction,
A.sub.1/SILCOLEASE.RTM.  UV POLY201: x=CH.sub.3; a=70; b=7
A.sub.2/SILCOLEASE.RTM.  UV POLY201; x=CH.sub.3; a=444; b=35
C.sub.2/
Photoinitiator SILCOLEASE.RTM.  UV CATA 211
Photoinitiator RHODORSIL.RTM.  Photoinitiator 2074
G2/Aerosil silica having a specific surface area of 300 m.sup.2/g from DEGUSSA treated with octamethylcyclotetrasiloxane Red 22/red pigment marketed by SUN CHEMICAL.
These compositions are then applied with the aid of coating bars numbered differently from 0 to 6 in order to deposit from 1 to 20 g/m.sup.2 on a rectangle of polyamide fabric comprising a silicone elastomer at the surface of the crosslinked
polyaddition RTV type (140 g/m.sup.2).
40 kg of an .alpha.,.omega.-divinylated silicone oil having a viscosity of 1.5 Pas with a titer of 0.1 meq of vinyl (Vi) per gram of oil, 0.24 kg of potable water and 0.24 kg of hexamethyldisilazane are introduced into a 100 l arm mixer.  After
homogenization, 13.9 kg of a pyrogenic silica characterized by its specific surface area of 200 m.sup.2/g are added in portions over roughly 2 hours.  After about 1 hour of mixing, 2.27 kg of hexamethyldisilazane are added over roughly 1 hour.  2 hours
later, a heating phase is started during which the mixture is placed under a nitrogen stream (30 m.sup.3/h); the heating continues until about 140.degree.  C. is reached, a plateau temperature which is maintained for 2 hours in order to remove the
volatile materials from the composition.  The suspension is then allowed to cool.
Portion A contains: 320 g of the suspension, 111 g of an .alpha.,.omega.-divinylated oil having a viscosity of 100 Pa.s which has a titer of 0.03 meq Vi per gram of oil, 35 g of ground quartz having a mean particle size (d50) close to 2.5 .mu.m,
12 g of a polyhydrogeno oil having a viscosity of 0.3 Pa.s which has a titer of 1.6 meq SiH per gram of oil, 12 g of an .alpha.,.omega.-dihydrogeno oil which has a titer of 1.9 meq SiH per gram of oil, 5 g of .gamma.-methacryloxypropyl trimethoxysilane,
5 g of .gamma.-glycidoxypropyl trimethoxysilane, 0.7 g of ethynylcyclohexano.
Portion B contains: 480 g of the suspension 20 g of butyl orthotitanate 1.1 g of a Karstedt catalyst containing a dose of 10% platinum.
100 parts by weight of A and 10 parts by weight of B are then mixed.
Depending on the experimental conditions, one or two lamps are in operation.  The lamps are traditional lamps with a spectrum of emission of mercury or of mercury doped for example with iron or with gallium or with lead or the like.
The coefficients of friction are measured after exposure with the aid of a 200 g block linked to a dynamometer which can exact a force of 10N in order to move the block.  To carry out the measurement, the tip of the fabric is installed on the
block on the surface coated with silicone varnish on the glass side.  A blank is carried out with a fabric coated with varnish-free crosslinked RTV.  All the results obtained for examples 1 to 14 are assembled in the following table.
TABLE-US-00001 Photocrosslinkable compositions for the varnishing of air bags C 1 2 3 4 5 6 7 8 9 10 11 12 13 14 A.sub.1 parts 0 100 90 0 0 0 0 0 0 0 50 70 0 20 20 A.sub.2 parts 0 0 0 0 0 0 0 0 0 0 0 0 50 0 0 D.sub.1 parts 0 0 0 100 90 0 0 0 45
45 50 30 50 72 72 D.sub.2 parts 0 0 0 0 0 100 100 90 45 45 0 0 0 0 0 C.sub.2 parts 0 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 G.sub.2 parts 0 0 10 0 10 0 0 10 10 10 0 0 0 8 8 Red22 parts 0 0 0 0 0 0 0 0 0 0 0 0 0 0 0.4 Hg lamp 200 0 1 1 1
1 1 1 1 0 0 1 1 1 2 1 W/cm Hg/Ca lamp 0 1 1 1 1 0 0 0 0 0 1 1 1 0 0 200 W/cm Hg/Ca lamp 80 0 0 0 0 0 0 0 0 1 1 0 0 0 0 0 W/cm Speed m/min 0 15 15 15 15 5 5 5 5 5 5 15 15 10 5 Deposit g/m.sup.2 0 4 9 5 7.8 1 6.9 8 4.5 1.8 9 6.4 5.6 6.4 5 Coef.  fric.  Ks
3.2 4 4 2 0.6 2.6 1.5 0.3 0.3 0.5 1.1 4.5 0.5 0.8
The best performances are obtained with the B.sub.2/type polymers in the presence of a silica-based filler.  The results vary according to the irradiation conditions; in particular, the values obtained at low power, examples 8 and 9, are of great
interest.  The A/type polymer may be added without affecting the results of Ks too much.
The irradiation conditions are obtained with a lamp from the company Fusion with an &quot;H.sup.+&quot; type bulb having a power of 80 W/cm.
The following are obtained: 3.5 g/m.sup.2 of varnish corresponds to a Ks=1.4 6.0 g/m.sup.2 of varnish corresponds to a Ks=0.8 9.0 g/m.sup.2 of varnish corresponds to a Ks=0.5
Preparation of B.sub.2
The synthesis is carried out in two steps from an .alpha.-.omega.-trimethylsilyl polymethylhydrogenodimethylsiloxane oil.  The synthesis is carried out according to the reaction scheme described below.
50 g of toluene and 28.8 mg of a complex of platinum having the oxidation level zero complexed with divinyltetramethyldisiloxane at 11.5% platinum, that is 3.31 mg of platinum are loaded into a three-necked reactor provided with a central
stirring paddle and with a capacity of 1 liter.  200 g of the siloxane polymer hydrogenated at 0.374%, that is 0.748 mol H, mixed with 70.97 g of vinyltriethoxysilane (that is 0.372 mol) at 25.degree.  C. are then poured in over 120 minutes and then the
reaction mass is heated at 60.degree.  C. for two hours.  The rate of conversion of the SiH units is 50%, that is 0.372 mol.
The freshly distilled vinylcyclohexene oxide is then added at the rate of 57 g (0.459 mol) and the reaction temperature is brought to 80.degree.  C. for three hours and 40 mg of the platinum complex are added during the last hour.
The medium is allowed to return to room temperature.  The rate of conversion of the SiH units is 98.3%.  The medium is heated to 100.degree.  C. and 40 mg of additional platinum complex are added and then the medium is left at 100.degree.  C. for
three hours.  The rate of conversion of the SiH units is 99.8%.  The reaction mass is drawn off into a 500 ml round-bottomed flask (360.2 g) and 0.3 g of 2,2-thiodiethanol is added and then a vacuum is created and the toluene is carried away by flushing
with argon at 97.degree.  C. into the reaction mass and 30 to 40.degree.  C. at the top of the column.  After stopping the vacuum and cooling to 40.degree.  C., 1.47 g of polyvinylpyridine (Reillex) and 1.53 g of hydrogen peroxide (Prolabo) are added.
The medium is heated at 80.degree.  C. for two hours and 4.72 g of magnesium sulfate are added to the reaction mass.  Filtration is then carried out on a carton of the oil obtained decolorized and the total mass yield of the synthesis is 86%,
that is 272 g.
The viscosity of the oil is 55 mm.sup.2/s.
The .sup.29Si NMR makes it possible to identify and quantify the units.
The reference is tetramethylsilane.  Me.sub.3SiO.sub.1/2 .delta.32 7 ppm that is two units Me.sub.2SiO.sub.2/2 and MeRSiO .delta.=22 ppm that is 13 units R&#39;Si(OEt).sub.3 .delta.=-45/-46 ppm that is two units
The .sup.1H NMR completes the analysis of the product and confirms the expected structure of the polymer D.sub.2.
100 parts of A.sub.1 Silcolease UV.RTM.  POLY200 having a viscosity of 350 mPas are mixed, with vigorous mechanical stirring for a quarter of an hour at room temperature (IKA20 stirrer equipped with a triple-paddle rod) in a light-tight
high-density polyethylene bottle, with 2.5 parts of C.sub.2, that is a dilution in isopropanol at 18% of photoinitiator Rhodorsil.RTM.  Photoinitiator 2074.
90 parts of A.sub.1 Silcolease UV.RTM.  POLY200 A.sub.1 having a viscosity of 350 mPas are mixed, with vigorous mechanical stirring for half an hour at room temperature (IKA20 stirrer equipped with a triple paddle rod) in a light-tight
high-density polyethylene bottle, with 10 parts of silica G.sub.2.  When the mixture is well homogeneous and the silica is incorporated, 2.5 parts of C.sub.2 are then added, that is a dilution in isopropanol at 18% of photoinitiator Rhodorsil.RTM.
Photoinitiator 2074 and the medium is vigorously stirred for an additional fifteen minutes.
100 parts of triethoxysilyl silane with epoxycyclohexyl functionality B.sub.1 having a viscosity of 10 mPas are mixed, with vigorous mechanical stirring for a quarter of an hour at room temperature (IKA20 stirrer equipped with a triple-paddle
rod) in a light-tight high-density polyethylene bottle, with 2.5 parts of C.sub.2, that is a dilution in isopropanol at 18% of photoinitiator Rhodorsil.RTM.  Photoinitiator 2074.
90 parts of Silane B.sub.1 having a viscosity of 10 mPas are mixed, with vigorous mechanical stirring for a half an hour at room temperature (IKA20 stirrer equipped with a triple paddle rod) in a light-tight high-density polyethylene bottle, with
10 parts of silica G.sub.2.  When the mixture is very homogeneous and the silica is incorporated, 2.5 parts of C.sub.2 are then added, that is a dilution in isopropanol at 18% of photoinitiator Rhodorsil.RTM.  Photoinitiator 2074 and the medium is
vigorously stirred for an additional fifteen minutes.
100 parts of polymer B.sub.2 having a viscosity of 55 mPas whose synthesis has just been described exp 17 are mixed, with vigorous mechanical stirring for a quarter of an hour at room temperature (IKA20 stirrer equipped with a triple paddle rod)
in a light-tight high-density polyethylene bottle, with 2.5 parts of C.sub.2 that is a dilution in isopropanol at 18% of photoinitiator Rhodorsil.RTM.  Photoinitiator 2074.
90 parts of polymer B.sub.2 having a viscosity of 55 mPas whose synthesis has just been described exp.17 are mixed, with vigorous mechanical stirring for a half an hour at room temperature (IKA20 stirrer equipped with a triple paddle rod) in a
light-tight high-density polyethylene bottle, with 10 parts of silica G.sub.2.  When the mixture is very homogeneous and the silica is incorporated, 2.5 parts of C.sub.2 are then added, that is a dilution in isopropanol at 18% of photoinitiator
Rhodorsil.RTM.  Photoinitiator 2074 and the mixture is vigorously stirred for an additional fifteen minutes.
45 parts of silane B.sub.1 and 45 parts of polymer B.sub.2 having a viscosity of 55 mPas whose synthesis has just been described exp.17 are mixed, with vigorous mechanical stirring for a half an hour at room temperature (IKA20 stirrer equipped
with a triple paddle rod) in a light-tight high-density polyethylene bottle, with 10 parts of silica G.sub.2.  When the mixture is well homogeneous and the silica is incorporated, 2.5 parts of C.sub.2 are then added, that is a dilution in isopropanol at
18% of photoinitiator Rhodorsil.RTM.  Photoinitiator 2074 and the medium is vigorously stirred for an additional fifteen minutes.
50 parts of silane B.sub.1 and 50 parts of polymer A.sub.1 having a viscosity of 350 mPas are mixed, with vigorous mechanical stirring, for a quarter of an hour at room temperature (IKA20 stirrer provided with a triple paddle rod) in a
light-tight high-density polyethylene bottle.
2.5 parts of C.sub.2 that is a dilution in isopropanol at 18% of photoinitiator Rhodorsil.RTM.  Photoinitiator 2074 are added and the medium is vigorously stirred for an additional five minutes.
30 parts of silane B.sub.1 and 70 parts of polymer A.sub.1 having a viscosity of 350 mPas are mixed, with vigorous mechanical stirring, for a quarter of an hour at room temperature (IKA20 stirrer provided with a triple paddle rod) in a
50 parts of silane B.sub.1 and 50 parts of polymer A.sub.2 having a viscosity of 5000 mPas are mixed, with vigorous mechanical stirring, for half an hour at room temperature (IKA20 stirrer provided with a triple paddle rod) in a light-tight
high-density polyethylene bottle.
72 parts of silane B.sub.1 and 20 parts of SILCOLEASE.RTM.  UV POLY200 A.sub.1 having a viscosity of 350 mPas whose synthesis has just been described exp.17 are mixed, with vigorous mechanical stirring for a half an hour at room temperature
(IKA20 stirrer equipped with a triple paddle rod) in a light-tight high-density polyethylene bottle, with 10 parts of silica G.sub.2.  When the mixture is very homogeneous and the silica is incorporated, 2.5 parts of C.sub.2 are then added, that is a
dilution in isopropanol at 18% of photoinitiator Rhodorsil.RTM.  Photoinitiator 2074 and the medium is vigorously stirred for an additional fifteen minutes.
(IKA20 stirrer equipped with a triple paddle rod) in a light-tight high-density polyethylene bottle, with 10 parts of silica G.sub.2.  When the mixture is very homogeneous and the silica is incorporated, 0.4 parts of red pigment Red22 marketed by Sun
chemical are then added and the medium is vigorously stirred until perfect dilution of the pigment is obtained which results in the production of a transparent light red formulation.  2.5 parts of C.sub.2 are then added, that is a dilution in isopropanol
at 18% of photoinitiator Rhodorsil.RTM.  Photoinitiator 2074 and the medium is vigorously stirred for an additional fifteen minutes.
Thermal transfer ribbons are used for example in the printing of labels.  They are used in printers whose printing speed varies between 150 and 300 mm/s. It is very important for the printing head (flat or wedge-like) which strikes the other side
of the surface containing the ink (waxes or resins) to be able to slide over this surface at high temperature of between 100 and 200.degree.  C.
To make the measurement, the polyester film coated with a protective coating layer based on photocrosslinked silicone preferably of less than 1 micrometer is installed.  A blank is made with the polyester film containing no silicone.
The results obtained are assembled in the following table for compositions containing various portions of: A.sub.1/SILCOLEASE.RTM.  UV POLY200 A.sub.2/SILCOLEASE.RTM.  UV POLY201
##STR00023## in isopropanolic solution at 18%.
G.sub.2/Aerosil silica 300 m.sup.2/g
The polyester films are coated with silicone on a 5-roll head, at a speed of 50 m/min (0.5 g/m.sup.2) and then photocrosslinked with a 120 W/cm lamp.
TABLE-US-00002 Silicone formulations: Control 1&#39; 2&#39; 3&#39; 4&#39; 5&#39; A.sub.1 parts 0 100 100 75 22 60 D.sub.1 parts 0 0 0 25 75 35 C.sub.2 parts 0 2.5 3 2.5 2.5 2.5 G.sub.2 parts 0 0 0 0 3 5 Coef.  fric.  Kd 0.3 3 1 0.33 0.25 0.4
It is also possible to seek to obtain plastic films mainly based on polyethylene or polypropylene intended for wrapping in order to protect market values.  In this case, it is possible to seek to have a top-varnishing based on silicone in order
to retain the anti-adhesion properties.
Trials were carried out for the application of silicone layers at less than 1 micrometer to 50 m/min to coronna-treated polyethylene film (electrical discharge which makes it possible to increase the surface tension of the film and to ensure good
sticking of the photocrosslinkable silicone to this surface).  The silicone is photocrosslinked in the presence of a 120 W/cm mercury lamp.  Two supports were used.  One virgin support, and one support printed with a blue cationic flexo.RTM.  ink 3 .mu.m
In both cases, 0.5 g/m.sup.2 of silicone of the formulation 5&#39; is applied according to example 18 described above.
In both cases, a perfectly crosslinked silicone layer is obtained whose coefficient of friction is in the region of 0.4.
"Silicone Composition Used In The Production Of Antifriction Varnishes, Method For The Application Of Said Varnishes To A Support And Support Thus Treated - Patent 7311945"
Silicone - Weicon
Extrusion lines for the production of silicone rubber ... - Krauss Maffei
RTV615 High Strength Transparent Silicone Rubber Compound