Tamper Evident Adhesive And Identification Document Including Same - Patent 7744002 by Patents-403
58068538
The present invention is generally related to identification documents. In one implementation an identification document has an adhesion controlling layer (formed from an inventive material) applied to couple an overlaminate to the rest of anidentification document using an inventive adhesive. The adhesive provides strong adhesion to many different kinds of identification document materials, including plastic card materials such as polyvinyl chloride (PVC), polycarbonate (PC), and amorphouspolyester such as amorphous polyethylene terephthalate (APET). More particularly, this inventive adhesive helps to provide unique evidence to protect the security document from heat intrusion and to enable detection of such intrusion.BACKGROUND AND SUMMARYIdentification DocumentsIdentification documents (hereafter "ID documents") play a critical role in today's society. One example of an ID document is an identification card ("ID card"). ID documents are used on a daily basis--to prove identity, to verify age, toaccess a secure area, to evidence driving privileges, to cash a check, and so on. Airplane passengers are required to show an ID document during check in, security screening and prior to boarding their flight. In addition, because we live in anever-evolving cashless society, ID documents are used to make payments, access an automated teller machine (ATM), debit an account, or make a payment, etc.(For the purposes of this disclosure, ID documents are broadly defined herein, and include, e.g., credit cards, bank cards, phone cards, passports, driver's licenses, network access cards, employee badges, debit cards, security cards, visas,immigration documentation, national ID cards, citizenship cards, social security cards, security badges, certificates, identification cards or documents, voter registration cards, police ID cards, border crossing cards, legal instruments, securityclearance badges and cards, gun permits, gift certificates or cards, membership cards or badg
United States Patent: 7744002
A composition is provided for adhering a first article to a second
article, the composition comprising a thermally active low Tg polymeric
resin; and a multifunctional crystalline polymer. The thermally active
low Tg polymeric resin can, for example, comprise 50-99% of the
composition. The multifunctional crystalline polymer can, for example,
comprise 1-50% of the composition. In one embodiment, the multifunctional
crystalline polymer comprises 5-20% by weight of the composition. In one
embodiment, the multifunctional crystalline polymer has a low molecular
Jones; Robert L. (Andover, MA), Bi; Daoshen (Boxborough, MA), Yeh; Tung-Feng (Waltham, MA)
(Billierca,
11/078,655
60552172Mar., 2004
235/487  ; 235/380; 235/488
235/487,380,375,488 428/347
Simjiam
2002/0068792
2002/0145652
2003/0062421
2003/0113533
2003/0226897
2005/0000642
2005/0230481
2005/0247794
2005/0274455
2006/0009021
2006/0138243
2006/0222830
2006/0228530
2007/0158939
63-146909
1982/04149
1989/08915
1994/27228
1995/10835
1995/14289
1995/20291
1996/27259
1996/36163
1997/43736
1998/14887
1998-20642
1998/24050
1998/40823
1998/49813
1999/34277
2000/43216
2001/43080
2003/05291
&quot;Access Control and Copyright Protection for Images WorkPackage 8: Watermarking &quot; Jun. 30 1995, 46 pages. cited by other
&quot;Copyright Protection for Digital Images, Digital Fingerprinting from FBI, &quot;Highwater FBI brochure 1995, 4 pages. cited by other
Bender et al., &quot;Techniques for Data Hiding, &quot;Massachusetts Institute of Technology, Media Laboratory, Jan. 1995, 10 pages. cited by other
Boland et al, &quot;Watermarking Digital Images for Copyright Protection, &quot;Fifth International Conference on Image Processing and its Applications, Conference Date 4-6 Jul. 1995, Conf. Publ. No. 410, pp. 326-330. cited by other
Caronni, &quot;Assuring Ownership Rights for Digital Images,&quot; Published in the Proceedings of &#39;Reliable It Systems,&#39; vis &#39;95 Hh. Bruggemann and W. Gerhardt-Hackl (Ed.), Vieweg Publishing Company, Germany, 1995, Jun. 14, 1994, 10 pages. cited by other
Clarke, &quot;Invisible Code Tags Electronic Images,&quot; Electronic Engineering Times, Jun. 12, 1995, No. 852, p. 42. cited by other
Collins, et al., &quot;Using Bar Code--Why It&#39;s Taking Over&quot;, Second Edition, Data Capture Institute, 1990 (Contents &amp; Index). cited by other
Friedman, &quot;The Trustworthy Digital Camera: Restoring Credibility to the Photographic Image,&quot; IEEE Transaction on Consumer Electronics, vol. 39, No. 4, Nov., 1993, pp. 905-910. cited by other
Grieco, Jr. et al.,&quot; Behind Bars--Bar Coding Principles and Applications&quot;, PT Publication, Inc., 1989 (Table of Contents &amp; Index). cited by other
Kawagucki, et al., &quot;Principle and Applications of BCPS-Streganography,&quot; Proc. SPIE vol. 3258: Multimedia Systems and Applications, 2-4 Nov. 1998, pp. 464-473. cited by other
Komatsu, et al., &quot;A Proposal on Digital Watermarking in Document Image Communication and Its Application to Realizing a Signature,&quot; Electronics and Communications in Japan, Part I, vol., 73, No. 5, 1990, pp. 22-23. cited by other
Matsui et al., &quot;Video-Steganography: How to Secretly Embed a Signature in a Picture,&quot; IMA Intellectual Property Project Proceedings, Jan. 1995, vol, 1, Issue 1, pp. 187-205. cited by other
Moller, et al., &quot;Rechnergestutzte Steganographie: Wie sie Funktioniert und warum folglich jede Reglementierung von Verschlusselung unsinnig ist,&quot; DuD, Datenschutz und Datensicherung, Jun. 18 (1994) 318-326. cited by other
PCT- Notification of the Transmittal of TheInternational Search Report or the Decleration, for the International Application No. PCT/US02/40843, mailed on May 15, 2003. cited by other
PCT-International Search Report for International Application No. PCT/US02/40843, mailed on May 15, 2003. cited by other
PCT- Notification of the Transmittal of the International Search Report or the Decleration, for the International Application No. PCT/US02/31786, mailed on May 2, 2003. cited by other
PCT-International Search Report for International Application No. PCT/US02/31786, mailed on May 2, 2003. cited by other
Palmer, &quot; The Bar Code Book&quot;, Third Edition, Helmers Publishing, Inc., 1995 (Contents &amp; Index). cited by other
Pitas et al., &quot;Applying Signatures on Digital Images,&quot; IEEE Workshop on Nonlinear and Signal Processing, Neos Marmaras, Greece, pp. 460-463, Jun., 1995. cited by other
Schneier, &quot;Digital Signatures, Cryptographic Algorithms Can Create Nonforeable Signatures for Electronic Documents, Making Them Valid Legal Instruments&quot; Byte, No. 1993, pp. 309-312. cited by other
Szepanski, &quot;Additive Binary Data Transmission for Video Signals,&quot; Papers Presented at Conf. Of Comm. Engineering Soc. Sept. 30-Oct. 3, 1980, Technical Reports vol. 74, 342-352. cited by other
&quot;Lenticular Prints,&quot; 6 pinted pages, printed on Dec. 16, 2002 and accessed from http://www.shortcourses.com/how/lenticular/lenticular.htm. cited by other
Bonny Lhotka, et al. &quot;Lenticular Inkjet Printmaking&quot;, 2 printed pages, printed on Dec. 16, 2002, and accessed from http://www.dypratt.com/evesmind/lentOverhtm. cited by other
Boucqueau, J.-M, Equitable Conditional Access and copyright Protection for Image Based on Trusted Third Parties, Teleservices and Multimedia Communications, vol. 1052, pp. 229-243 (1996). cited by other
Castro, et al., &quot;Registration of Translated and Rotated Images Using Finite Fourier Transforms,&quot; IEEE Transactions on Pattern Analysis and Machine Intelligence, vol. Pami-9, No. 5, Sep. 1987, pp. 700-703. cited by other
Computergram Internations, &quot;The Copyright Can of Worms Opened Up By The New Electronic Media,&quot; http://www.cbronline.com/news/the.sub.--copyright.sub.--can.sub.--of.sub.- --worms.sub.--opened.sub.--up?pint=1 , Jul. 17, 1995 2 pages. cited by other
Computergram Internations, The Copyright Can of Worms Opened Up By the New Electronic Media--2, pCGN07210008, Jul. 21, 1995, 2 pages. cited by other
Eastman, Product Data Sheet, Easter Copolyester 5011, Dec. 7, 2004, 2 pages. cited by other
Eastman, Product Data Sheet, Easter Copolyester 6763, Apr. 26, 2005 4 pages. cited by other
Eastman, Product Data Sheet, Easter Copolyester A150, Jun. 27, 2001, 3 pages. cited by other
Moran, &quot;3-D Imagery&quot;, 3 printed pages, printed on Dec. 16, 2002 and accessed from http://mvw.flexgraphy.org/flexo/article.cfm?ID=45. cited by other
Printed copy of Orasee company web page entitled &quot;Welcome to Orasee Corporation&quot;, 2 printed pages, printed on Dec. 13, 2002 and accessed from: http://www.orasee.com/one/main.php3. cited by other
Quisquater, et al. &quot;Conditional Access and Copyright Protection based on the use of Trusted Third Parties&quot; 43 pages (1995). cited by other
Roberts, &quot;Picture Coding Using Pseudorandom Noise,&quot; IRE Trans. on Information Theory, vol. 8, No. 2, Feb., 1962, pp. 145-154. cited by other.
60/552,172, filed Mar. 11, 2004, which is hereby incorporated by
This application is related to the following United States Provisional
Application: Tamper Evident Security Feature and Identification Document
Including Same (Application Number 60/514,178, filed Oct. 23, 2003,
Inventors Daoshen Bi, Robert Jones, and Tom Regan and Application No.
10/973,924, filed Oct. 25, 2004);
The present application also is related to the following U.S. Patents and
patent applications, each of which is hereby incorporated by reference:
Document Laminate Formed From Different Polyester Materials(Application
No. 10/692,463, filed Oct. 22, 2003, Inventor Brian Labrec, (U.S. Patent
Publication No. 2005-0084693));
(Application No 10/673,048, filed Sep. 26, 2003, Inventors Robert Jones
and Daoshen Bi (U.S. Patent Publication No. 2005-0067497));
Identification Document (Application No. 60/471,429, filed May 16, 2003,
inventors Robert Jones, Brian Labrec, Daoshen Bi, and Thomas Regan).
Use of Pearlescent and Other Pigments to Create Security Documents
(Application No. 09/969,200, Inventors Bentley Bloomberg and Robert L.
Jones, filed Oct. 2, 2001 (now U.S. Pat. No. 6,827,277)).
Identification Card Printed With Jet Inks and Systems and Methods of
Making Same (Application No. 10/289,962, Inventors Robert Jones, Dennis
Mailloux, and Daoshen Bi, filed Nov. 6, 2002 U.S. Patent Publication No.
2003-0211296)).
Contact Smart Cards Having a Document Core, Contactless Smart Cards
Including Multi-Layered Structure, PET-Based Identification Document, and
Methods of Making Same (Application No. 10/329,318, filed Dec. 23,
2002--Inventors Robert Jones, Joseph Anderson, Daoshen Bi, Thomas Regan,
and Dennis Mailloux (now U.S. Pat. No. 6,843,422)).
of Making Same (Application No. 10/325,434, filed Dec. 18, 2002
--Inventors Brian Labrec, Joseph Anderson, Robert Jones, and Danielle
Batey (now U.S. Pat. No. 6,817,530)).
Each of the above U.S. Patent documents is herein incorporated by
patent application Ser. No. 09/747,735, filed Dec. 22, 2000 (now
Publication No. 2003-0038174), Ser. No. 09/602,313, filed Jun. 23, 2000
(now U.S. Pat. No. 6,752,432), and Ser. No. 10/094,593, filed Mar. 6,
2002 (now Publication No. 2002-0170966), U.S. Provisional Patent
Application No. 60/358,321, filed Feb. 19, 2002, as well as U.S. Pat. No.
6,066,594. Each of the above U.S. Patent documents is herein incorporated
by reference in its entirety
1.  A composition for adhering a first polymer laminate layer to a second polymer laminate layer, the composition comprising: a thermally active polymeric resin;  and a
multifunctional crystalline polymer, wherein the composition maintains adhesion between the first and second polymer layers above a temperature at which a plurality of crystals form within the multifunctional crystalline polymer;  wherein the composition
forms a plurality of crystals that provide visible evidence of tampering with the adhesion formed between the first and second polymer layers when heated at a temperature above a predetermined temperature.
2.  The composition of claim 1, wherein the thermally active polymeric resin comprises a low Tg polymeric resin that comprises 50-99% of the composition.
3.  The composition of claim 2, wherein the multifunctional crystalline polymer comprises 1-50% of the composition.
4.  The composition of claim 1, wherein the multifunctional crystalline polymer comprises 1-50% of the composition.
5.  The composition of claim 1, wherein the multifunctional crystalline polymer comprises 5-20% by weight of the composition.
6.  The composition of claim 1, wherein the multifunctional crystalline polymer has a low molecular weight.
7.  The composition of claim 1, wherein the thermally active polymeric resin comprises a low Tg polymeric resin that comprises at least one of a high molecular weight low Tg linear amorphous polyester, a polymeric plasticizer, VITEL 3650,
polyacrylate, polyethylene vinylacrylate, polyester, and polyurethane.
8.  The composition of claim 1, wherein the multifunctional crystalline polymer comprises at least one of a di-functional polyester, a tri-functional polyester, a multi-functional polyester, polypropylene, polyamide, acetal, high density
polyethylene, and VITEL 5833.
9.  The composition of claim 1, wherein the predetermined temperature is a temperature lower than a standard lamination temperature.
10.  The composition of claim 1, wherein the predetermined temperature is about 220 degrees Fahrenheit.
11.  The composition of claim 1, wherein the crystals have a &quot;snow flake&quot; like appearance after being subjected to heat above the predetermined temperature, and the &quot;snow flake&quot; like appearance provides evidence of tampering with the adhesion
between the first and second polymer layers.
12.  An identification document, comprising: an information-bearing layer;  an adhesive layer overlaying at least a portion of the information-bearing layer, the adhesive layer comprising a thermally active low Tg polymeric resin and a
multifunctional crystalline polymer;  and a protective layer coupled to the information-bearing layer via the adhesive layer, wherein the adhesive layer is constructed and arranged such that subjecting the identification document to a temperature above a
predetermined temperature causes a plurality of crystals to form in the adhesive layer.
13.  An identification document, comprising: an information-bearing layer;  an adhesive layer overlaying at least a portion of the information-bearing layer, the adhesive layer comprising a thermally active polymeric resin and a multifunctional
crystalline polymer;  and a protective layer coupled to the information-bearing layer via the adhesive layer, wherein the adhesive layer is constructed and arranged such that subjecting the identification document to a temperature above a predetermined
temperature causes a plurality of crystals to form in the adhesive layer.
14.  The identification document of claim 13, wherein the crystal formation is substantially irreversible.
15.  The identification document of claim 13, wherein the crystals are visible to an unaided human eye.
16.  The identification document of claim 13, wherein the thermally active lot Tg polymeric resin comprises 50-99% of the adhesive layer.
17.  The identification document of claim 13, wherein the multifunctional crystalline polymer comprises 1-50% of the adhesive layer.
18.  The identification document of claim 13, wherein the multifunctional crystalline polymer comprises 5-20% by weight of the adhesive layer.
19.  The identification document of claim 13, wherein the thermally active low Tg polymeric resin comprises at least one of a high molecular weight low Tg linear amorphous polyester, a polymeric plasticizer, VITEL 3650, polyacrylate,
polyethylene vinylacrylate, polyester, and polyurethane.
20.  The identification document of claim 13, wherein the multifunctional crystalline polymer comprises at least one of a di-functional polyester, a tri-functional polyester, a multi-functional polyester, polypropylene, polyamide, acetal, high
density polyethylene, and VITEL 5833.
21.  A laminate for a document comprising: an outer-laminate layer;  and an adhesive layer including a thermally active polymeric resin, and a multifunctional crystalline polymer;  wherein the adhesive layer maintains adhesion between the
outer-laminate layer and an information bearing document layer above a temperature at which a plurality of crystals form within the multifunctional crystalline polymer: and wherein subjecting the laminate to a temperature above a predetermined
temperature causes a plurality of crystals to form in the adhesive layer.  Description
The present invention is generally related to identification documents.  In one implementation an identification document has an adhesion controlling layer (formed from an inventive material) applied to couple an overlaminate to the rest of an
identification document using an inventive adhesive.  The adhesive provides strong adhesion to many different kinds of identification document materials, including plastic card materials such as polyvinyl chloride (PVC), polycarbonate (PC), and amorphous
polyester such as amorphous polyethylene terephthalate (APET).  More particularly, this inventive adhesive helps to provide unique evidence to protect the security document from heat intrusion and to enable detection of such intrusion.
(For the purposes of this disclosure, ID documents are broadly defined herein, and include, e.g., credit cards, bank cards, phone cards, passports, driver&#39;s licenses, network access cards, employee badges, debit cards, security cards, visas,
immigration documentation, national ID cards, citizenship cards, social security cards, security badges, certificates, identification cards or documents, voter registration cards, police ID cards, border crossing cards, legal instruments, security
clearance badges and cards, gun permits, gift certificates or cards, membership cards or badges, etc., etc. Also, the terms &quot;document,&quot; &quot;card,&quot; &quot;badge&quot; and &quot;documentation&quot; are used interchangeably throughout this patent application.).
the identity of the bearer.  Examples of such information include name, address, birth date, signature and photographic image; the cards or documents may in addition carry other so-called personalized or variable data (e.g., data specific to a particular
card or document, for example an employee number) and so-called fixed or invariant data (e.g., data common to a large number of cards, for example the name of an employer).  All of the cards described above will hereinafter be generically referred to as
&quot;ID documents&quot; .
As those skilled in the art know, ID documents such as drivers licenses can contain additional information such as a photographic image, a bar code (which may contain information specific to the person whose image appears in the photographic
image, and/or information that is the same from ID document to ID document), variable personal information, such as an address, signature, and/or birthdate, biometric information associated with the person whose image appears in the photographic image
(e.g., a fingerprint), a magnetic stripe (which, for example, can be on the a side of the ID document that is opposite the side with the photographic image), and various security features, such as a security pattern (for example, a printed pattern
comprising a tightly printed pattern of finely divided printed and unprinted areas in close proximity to each other, such as a fine-line printed security pattern as is used in the printing of banknote paper, stock certificates, and the like).
An exemplary ID document can comprise a substrate or core layer (which can be pre-printed), such as a light-colored, opaque material (e.g., polycarbonate, TESLIN (available from PPG Industries) polyvinyl chloride (PVC) material, etc).  In certain
instances and with certain printing or information forming technologies, variable or personalized data can be formed directly on the substrate or core layer.  In other instances, the core layer may be coated and/or laminated with another material to
enable printing or other methods of forming information.  For example, the substrate or core layer can be laminated with a transparent material, such as clear polycarbonate or PVC to form a so-called &quot;card blank&quot; .
Certain technologies for forming or printing information may require further protection of the information, so an additional layer of transparent overlaminate can be coupled to the core layer or card blank and the information printed thereon, as
is known by those skilled in the art.  Illustrative examples of usable materials for overlaminates include polycarbonate, biaxially oriented polyester, or other optically clear durable plastic film.
Information, such as variable personal information (e.g., photographic information), can be formed on the card blank using one or more methods, such as laser xerography, Indigo, intaglio, laser engraving or marking, inket printing, thermal or
mass transfer printing, dye diffusion thermal transfer (&quot;D2T2&quot;) printing, (described in commonly assigned U. S. Pat.  No. 6066594, which is incorporated herein by reference in its entirety.), etc. The information can, for example, comprise an indicium or
indicia, such as the invariant or nonvarying information common to a large number of identification documents, for example the name and logo of the organization issuing the documents.  The information may be formed by any known process capable of forming
the indicium on the specific core material used.
Identification documents of the types mentioned above can take a number of forms, depending on cost and desired features.  For example, some ID documents comprise highly plasticized poly(vinyl chloride) or have a composite structure with
polyester laminated to 0.5-2.0 mil (13-51 .mu.m) poly(vinyl chloride) film, which provides a suitable receiving layer for heat transferable dyes which form a photographic image, together with any variant or invariant data required for the identification
of the bearer.  These data are subsequently protected to varying degrees by clear, thin (0.125-0.250 mil, 3-6 .mu.m) overlay patches applied at the printhead, holographic hot stamp foils (0.125-0.250 mil 3-6 .mu.m), or a clear polyester laminate (0.5-10
mil, 13-254 .mu.m) supporting common security features.  These last two types of protective foil or laminate sometimes are applied at a laminating station separate from the printhead.  The choice of laminate dictates the degree of durability and security
imparted to the system in protecting the image and other data.
One response to the problem of counterfeiting ID documents has involved the integration of verification features that are difficult to copy by hand or by machine, or which are manufactured using secure and/or difficult to obtain materials.  One
such verification feature is the use in the card of a signature of the card&#39;s issuer or bearer.  Other verification features have involved, for example, the use of watermarks, biometric information, microprinting, covert materials or media (e.g.,
ultraviolet (UV) inks, infrared (IR) inks, fluorescent materials, phosphorescent materials), optically varying images, fine line details, validation patterns or marking, and polarizing stripes.  These verification features are integrated into an
identification card in various ways, as appreciated by those skilled in the art, and they may be visible or invisible (covert) in the finished card.  If invisible, they can be detected by viewing the feature under conditions which render it visible.  At
least some of the verification features discussed above have been employed to help prevent and/or discourage counterfeiting.
Despite the advances in the manufacture of ID documents, the ID document counterfeiter remains surprisingly resourceful.  Improvements are needed to stay ahead of the counterfeiter.  One counterfeiting technique involves a de-lamination attack.
Consider an ID document that includes a printed substrate covered by a laminate layer.  A de-lamination attack removes the laminate layer, sometimes with the aid of heat, to access information printed on the substrate.  Once revealed, the counterfeiter
can alter the printed information and reuse the substrate or laminate.
Some ID documents are susceptible to this type of attack.  Consider the ID document including a substrate, ink applied to the substrate (or laminate layer) to convey information and a laminate layer covering the ink and substrate.  Conventional
inks generally include a strong adhesion to either a document substrate or to a laminate.  A counterfeiter can use this design characteristic (adhesion) to his advantage.  Upon de-lamination, the ink may adhere to the substrate layer or to a laminate
layer.  Regardless, the printed information is typically preserved on at least one layer and may be used again.  (For example, if the ink adheres to a laminate, the counterfeiter can reuse the laminate.  Or if the ink adheres to the substrate, the
counterfeiter can perhaps alter the information by applying additional ink, or simply reuse the remaining information on the substrate.).
U.S.  Pat.  No. 5,380,695, herein incorporated by reference, discloses an identification document designed to help deter intrusion attempts.  With reference to FIG. 1, an image-receiving element 10 includes a support 12, a polymeric security
layer 14 including printing, and an image-receiving layer 16.  The polymeric security layer 14 is designed such that its cohesivity is less than its adhesivity for each layer that is contiguous thereto (layers 16 and 12b).  A printed security pattern 18
is hopefully destroyed (into pieces 18a and 18b) through partitioning of the security layer 14 during an attempted de-lamination of the image-receiving layer 16 from the image-receiving element 12b (see FIG. 2).
Another type of delamination attack involves removal of the overlaminate.  Over-laminate has been commonly applied as a protective layer for many types of security documents, such as identification cards, driver licenses, passports, and security
badges.  Over-laminates can be used to protect printed plastic cards (and the information formed on them) from abrasion, chemical attack such as plasticizer from the wallet, coffee, and bleach, from ultraviolet radiation, and from counterfeiting and
tampering.  Currently, most overlaminates consist of two layers: polyester base film and a thin layer of thermal active adhesive.  With appropriate levels of heat and pressure, the overlaminate will bond to plastic card surface.
(a) Some overlaminate products are compatible only with certain types of other laminates and/or card blanks.  For example, TBSN (available from Transilwrap Company, Inc., of Franklin Park, Illinois) generally is compatible only with PVC and
cannot be used with polyester or polycarbonate.
In one embodiment, we provide a composition for adhering a first article to a second article, the composition comprising a thermally active low Tg polymeric resin; and a multifunctional crystalline polymer.  The thermally active low Tg polymeric
resin can, for example, comprise 50-99% of the composition.  The multifunctional crystalline polymer can, for example, comprise 1-50% of the composition.  In one embodiment, the multifunctional crystalline polymer comprises 5-20% by weight of the
composition.  In one embodiment, the multifunctional crystalline polymer has a low molecular weight.
The thermally active low Tg polymeric resin can, for example, comprise at least one of a high molecular weight low Tg linear amorphous polyester, a polymeric plasticizer, VITEL 3650, polyacrylate, polyethylene vinylacrylate, polyester, and
In one embodiment, the composition forms a plurality of crystals when heated at a temperature above a predetermined temperature and then cooled, wherein the predetermined temperature is a temperature lower than a standard lamination temperature,
for example about 220 degrees Fahrenheit.  The crystals can have a &quot;snow flake&quot; like appearance.
In another embodiment, we provide an identification document, comprising an information bearing layer, an adhesive layer, and a protective layer.  The adhesive layer overlays at least a portion of the information-bearing layer and comprises a
thermally active low Tg polymeric resin and a multifunctional crystalline polymer.  The protective layer is coupled to the information-bearing layer via the adhesive layer.  The adhesive layer, in one embodiment, is constructed and arranged such that
subjecting the identification document to a temperature above a predetermined temperature causes a plurality of crystals to form in the adhesive layer.  This crystal formation can be substantially irreversible.
driver&#39;s licenses, network access cards, employee badges, debit cards, security cards, visas, immigration documentation, national ID cards, citizenship cards, social security cards, security badges, certificates, identification cards or documents, voter
registration and/or identification cards, police ID cards, border crossing cards, security clearance badges and cards, legal instruments, gun permits, badges, gift certificates or cards, membership cards or badges, and tags.  Also, the terms &quot;document,&quot;
&quot;card,&quot; &quot;badge&quot; and &quot;documentation&quot; are used interchangeably throughout this patent application.).  In at least some aspects of the invention, ID document can include any item of value (e.g., currency, bank notes, and checks) where authenticity of the
item is important and/or where counterfeiting or fraud is an issue.
Of course, it is appreciated that certain images may be considered to be &quot;identification quality&quot; if the images are machine readable or recognizable, even if such images do not appear to be &quot;identification quality&quot; to a human eye, whether or not
the human eye is assisted by a particular piece of equipment, such as a special light source.  For example, in at least one embodiment of the invention, an image or data on an ID document can be considered to be &quot;identification quality&quot; if it has
embedded in it machine-readable information (such as digital watermarks or steganographic information) that also facilitate identification and/or authentication.
&quot;Personalization&quot;, &quot;Personalized data&quot; and &quot;variable&quot; data are used interchangeably herein, and refer at least to data, images, and information that are &quot;personal to&quot; or &quot;specific to&quot; a specific cardholder or group of cardholders.  Personalized
birthdate).  In at least some embodiments of the invention, personal/variable data can include some fixed data, as well.  For example, in at least some embodiments, personalized data refers to any data that is not pre-printed onto an ID document in
advance, so such personalized data can include both data that is cardholder-specific and data that is common to many cardholders.  Variable data can, for example, be printed on an information-bearing layer of the ID card using thermal printing ribbons
and thermal printheads.
The terms &quot;indicium&quot; and indicia as used herein cover not only markings suitable for human reading, but also markings intended for machine reading.  Especially when intended for machine reading, such an indicium need not be visible to the human
eye, but may be in the form of a marking visible only under infra-red, ultra-violet or other non-visible radiation.  Thus, in at least some embodiments of the invention, an indicium formed on any layer in an identification document (e.g., the core layer)
may be partially or wholly in the form of a marking visible only under non-visible radiation.  Markings comprising, for example, a visible &quot;dummy&quot; image superposed over a non-visible &quot;real&quot; image intended to be machine read may also be used.
transparent adhesives, or which have substantially transparent polymers and/or substantially transparent adhesives as a part of their structure, e.g., as an extruded feature.  However, transparency is not required.  Examples of usable laminates include
at least polyester, polycarbonate, polystyrene, cellulose ester, polyolefin, polysulfone, or polyamide.  Laminates can be made using either an amorphous or biaxially oriented polymer as well.  The laminate can comprise a plurality of separate laminate
layers, for example a boundary layer and/or a film layer.  Of course, the types and structures of the laminates described herein are provided only by way of example, those skilled in the art will appreciated that many different types of laminates are
usable in accordance with the invention.
For purposes of illustration, the following description will proceed with reference to ID document structures.  It should be appreciated, however, that the present invention is not so limited.  Indeed, as those skilled in the art will appreciate
the invention.  For example, in at least some embodiments, the invention is usable with virtually any product/process which is to be laminated or coupled to a laminate in any way.
We have developed an inventive material with unique adhesion and thermal response properties that enable it to provide useful manufacturing, anti-tampering, and anti-counterfeiting functionality to ID documents.  The inventive material can be
used in many different ways, including as an adhesive, as a seal, as a security pattern, as part of a coating, and as part of a laminate
In a first embodiment, the inventive material is an adhesive formulation containing 50-99% of a thermally active low glass transition temperature (T.sub.g) polymeric resin and 1-50% of a multifunctional crystalline polymer.
The thermally active low T.sub.g polymeric resin can, for example, be made of materials such as polyacrylate, polyethylene vinylacrylate, polyester, and polyurethane.  One example of a thermally active low T.sub.g (glass transition temperature)
polymeric resin that we have found useful is VITEL 3650, which is a high molecular weight, low T.sub.g linear amorphous polyester.  VITEL 3650 acts as a polymeric plasticizer to improve the melt flowability during heat lamination.
The multifunctional crystalline polymers can be di-, tri-, or multi- functional polyesters.  In an advantageous embodiment, the inventive material includes 5 to 20% by weight of di, tri, or multifunctional polymer material.  Illustrative examples
of usable multifunctional polymer materials, in accordance with at least some embodiments of the invention, include materials such as VITEL 5833 (available from Bostick-Findley, Inc., of Middleton, Massachusetts), which is a low molecular weight, highly
functional branched polyester with high crystallinity.  We have found that the high level of active sites in VITEL 5833 help to provide more interaction to some types of materials, such as polycarbonate, to improve adhesion.  In addition, we have found
that the low molecular weight of VITEL 5833 provides surface wetting during heat lamination.  We have produced a particularly effective embodiment of the inventive material using a concentration of 10% (by weight) of VITEL 5833.  Additional usable
multifunctional polyesters include polypropylene, polyamide, acetal, high density polyethylene (HDPE), low density polyethylene, etc.
In at least some embodiments, the multifunctional polymer is a multifunctional crystalline polymer.  Use of a multifunctional crystalline polymer provides at least two advantages.  First, the multifunctional crystalline polymer has a very good
anti-blocking property, which helps to improve processes for applying the multifunctional crystalline polymer to an ID document.  Another advantage of using the multifunctional crystalline polymer is that some types of this polymer form a pattern of
visible, irreversible &quot;snow flake like&quot; crystals when heated above 220 degrees Fahrenheit, which can help provide evidence of tampering.  This can be understood further by viewing the FIGs, as discussed below.
At least some embodiments of our inventive material also have advantages that enable certain manufacturing processes (e.g., lamination), to occur at lower temperatures.  Laminating at lower temperatures helps to achieve proper bond strength and
helps to ensure the flatness of the material (e.g., part of an ID document) being laminated.
We have also found that the adhesion properties of our inventive material can provide advantages when used with ID documents.  We have found that the inventive material has strong adhesion to many types of materials used to make ID documents,
including but not limited to polyvinyl chloride (PVC), polycarbonate (PC), amorphous polyester, polyethylene terephthalate (PET), amorphous PET (A-PET), polyolefin, TESLIN, etc. .  We have also found that our inventive material has excellent adhesion to
the certain of our proprietary materials, such as materials described in a commonly assigned patent application entitled &quot;Document Laminate Formed From Different Polyester Materials&quot; (Ser.  No. 10/692463, Attorney docket Number P0901D, filed Oct.  22,
2003, Inventor Brian Labrec).
The inventive material also has strong adhesion properties to many different types of inks that are printed on identification cards, including but not limited to inks used with printers such as the XEROX Doc-12, XEROX 3535, Hewlett Packard
Indigo, Intaglio, inkjet inks, etc. In at least one embodiment, we have found that, by applying the inventive material substantially adjacent to printed indicia (e.g., under it or over it), and by selecting appropriate core materials, laminate materials,
and inks, we are able to apply the inventive material in a manner that causes cohesive failures in the printed indicia when an intrusion to the ID document is attempted.  During such an attempted intrusion, the strong adhesion properties of the inventive
material cause it to adhere firmly to the printing and to any other materials to which it is applied.  This helps to make detection of tampering more apparent.
In one embodiment, by including a material such as a tri-functional polymer material, the inventive material described herein can be used with (and have good adhesion to) a variety of materials used for ID documents, especially materials used to
make ID cards (e.g., PVC, PC, PET, etc.), especially as compared with some types of polyester resins (e.g., VITEL 2700B LMW) or with certain materials (e.g., TBSN, available from Transilwrap Company, Inc., of Franklin Park, Illinois).
We have found use of di, tri, and/or multifunctional polymers particularly advantageous with ID document materials (e.g., substrate (or core layer) and laminate (or cover layer) made using polycarbonate, because of the good adhesion that results
from the high level of active sites in many of such polymers (e.g., the VITEL 5833) that provide more interaction to polycarbonate.  In addition, we have found that the low molecular weight of at least some of these polymers (e.g., VITEL 5833) provides
useful surface wetting during heat lamination processes.  Still another advantage is that use of the di, tri, and/or multifunctional polymers can enable lamination of ID documents to occur at lower temperatures while still achieving proper bond strength
and a substantially flat ID document (e.g., card).  For example, in the production of some known types of ID cards, a lamination temperature of 230 to 240 degrees Fahrenheit is required.  Using at least some of the di, tri-, and/or multifunctional
polymers described herein can enable lamination processes to occur at lower temperatures (e.g., 210 to 220 degrees Fahrenheit).
As those skilled in the art will appreciate, the inventive material used of the adhesion controlling layer can contain other materials, including additives such as ultraviolet (UV) colorants, infrared (IR) colorants, visible colorants (e.g., to
make the adhesion controlling layer appear blue, red, etc.), thermachromic colorants, optically varying colorants, pearlescent colorants, etc. For example, we specifically anticipate that the colorants described in commonly assigned U.S.  patent
application Ser.  no. 09/969,200, entitled &quot;Use of Pearlescent and Other Pigments to Create Security Documents&quot; (now U.S.  Pat.  No. 6,827,277), the contents of which are hereby incorporated by reference, are usable with the inventive materials described
herein.  Such additives enable the adhesion controlling layer to be visible, for example, only under selected conditions.  Such an additive also can enable the security seal to be substantially invisible when applied over certain types of indicia.  For
example, an adhesion controlling layer containing an infrared colorant could be applied over indicia formed using an ultraviolet ink.  The adhesion controlling layer would not, of course, be visible when the indicia is viewed using UV light.
A first approach involved tests of embodiments of the invention to see whether the inventive materials can improve the adhesion of a polyethylene terephthalate (PET) overlaminate film to the back of an ID document having a polycarbonate (PC)
surface.  We modified a Vitel 2700B LMW adhesive coating solution by the addition of Vitel 5833 and Vitel 3650.  Vitel 5833 is a low molecular weight, highly functional branched polyester with high crystallinity.  Its high level of active sites provides
more interaction to polycarbonate to improve adhesion.  The low molecular weight provides surface wetting during heat lamination.  Vitel 3650 is a high molecular weight, low Tg, linear amorphous polyester.  It acts as a polymeric plasticizer to improve
the melt flowability during heat lamination.
ID documents, in the form of cards, were made by laminating 12-mil polycarbonate/KRTY 3&#39;&#39; (Roll 817725-001-1-90070) on both sides of TESLIN sheets.  Overlaminate PET films were made by coating 30% solid adhesive solutions with #4 bar on 1.2 mil
301H PET film, and drying at 60.degree.  C. for 5 min. Coating solutions were made by 1.5-3.0% Vitel 5833, 28.5-27.0% Vitel 2700B LMW, 56.0% MEK, 14% Toluene; and by 3.0-15.0% Vitel 3650, 27.0-15.0% Vitel 2700B LMW, 56.0% MEK, 14% Toluene.  30% Vitel
2700B LMW solution.
These cards were overlaminated on a Polaroid ColorCard Printer Model 85 SC (Atlantek 85 DSC serial # 000233).  The both top and bottom temperature settings on the printer were 58.  The temperature between card and overlaminate PET film was
measured to be about 235.degree.  F. The overlaminate PET film containing more than 20% of Vitel 3650 in adhesive layer was very difficult to laminate by the printer.
A peel test was done on the cards using an Instron 5543 material test system.  All test samples were cut to a width of 0.5 inch.  All test data recorded were the average load force between peel extensions 0.5 to 1.0 inch at 10 inches/min peel
rate.  Table 1 lists the peel test data.  The data in Table 1 tends to indicate that addition of Vitel 5833 or Vitel 3650 into Vitel 2700B LMW increases adhesion strength.  Too much Vitel 3650 presumably decreases the total number of functional groups
leading to a loss of strength.
TABLE-US-00001 TABLE 1 Instron Peel Test (LBS/INCH WIDTH) Smurfit Vitel 2700B Vitel 5833 Vitel 5833 Vitel 5833 Vitel 3650 Vitel 3650 Sample #8017 LMW 5%* 8%* 10%* 10%* 20%* 1 0.58 0.98 1.16 0.66** 1.00 1.70** 1.17 2 1.02 1.32 1.42** 0.64 1.40
1.84 0.64 3 0.58 0.48 1.42 1.64 1.28** 1.38** 1.82 4 0.54 0.54 1.60 1.30 1.56** 1.16** 0.86 5 0.54 0.90 1.00 1.50** 2.12** 2.02** 0.46 6 0.66 0.68 0.98 0.68** 1.98 2.36** 0.98 7 0.92 0.56 1.74 1.32 1.88 2.10** 0.84 8 0.72 0.64 1.38 1.50 2.28 2.06** 0.30
9 0.76 0.56 1.28 1.62 1.84 2.06** 0.38 Ave 0.70 0.74 1.33 1.21 1.70 1.85 0.82 *% in coating with Vitel 2700B LMW **broke the film
The test cards were kept at 70.degree.  C. and 100% (RH) for 3days.  The peel tests were done without equilibration after taking samples out of 70/100.  Table 2 shows adhesion of Vitel 2700B LMW became better because of high temperature
annealing.  Addition of Vitel 3650 resulted in lost adhesion strength because of its plasticizing effect at high temperature.  Samples Vitel 5833 showed better adhesion property after 70/100.
TABLE-US-00002 TABLE 2 Instron Peel Test after 3 Days at 70/100 (LBS/INCH WIDTH) Vitel Vitel Vitel 2700B 5833 5833 Vitel 5833 Vitel 3650 Vitel 3650 Sample LMW 5%* 8%* 10%* 10%* 20%* 1 0.64** 0.46** 1.04 1.56** 0.48 0.84 2 1.88** 1.80** 1.24
2.30** 0.36 0.46 3 1.20** 1.00** 1.62** 1.58** 1.50** 0.90 4 1.82** 1.30** 1.08** 1.60** 0.70 0.72 5 1.42** 1.26** 1.20** 1.34** 0.52** 0.48 6 0.66** 1.06** 1.86** 2.22** 1.08** 0.48 Ave 1.27 1.15 1.34 1.77 0.77 0.65 *% in coating with Vitel 2700B LMW
The tests were done by facing the adhesive side of overlaminate film to uncoated overlaminate film, and adding 0.076 lb/inch.sup.2 weight on the top.  The samples with a higher content of Vitel 5833 showed better results.
TABLE-US-00003 TABLE 3 Blocking Test Vitel 2700B Vitel 5833 Vitel 5833 Vitel 5833 Vitel 3650 LMW 5%* 8%* 10%* 10%* 40.degree.  C. Pass Pass Pass Pass Fail 3 days 50.degree.  C. Fail Fail Pass Pass Fail 3 hrs *% in coating with Vitel 2700B LMW
Based on the testing in this example, the results indicated that addition of Vitel 5833 not only improved the adhesion of overlaminate PET film on polycarbonate but also gave better results in the blocking test.  Vitel 5833 has potential as a
component in a hot melt adhesive coating.
A second approach involved investigating the effect of the thickness of hot melt adhesive layers on the adhesion of overlamination PET film to the back of ID cards (polycarbonate surface).  Identification documents in the form of cards were made
by laminating 12-mil polycarbonate/KRTY 3&#39;&#39; (Roll 817725-001-1-90070) on both sides of Teslin sheets.  Overlaminate PET films were made by coating 30% solid adhesive solutions with #4, #7 and #10 bar on 1.2 mil 301H PET film, and drying at 60.degree.  C.
for 5 min. Coating solutions were made by 3.0% Vitel 5833, 27.0% Vitel 2700B LMW, 56.0% MEK, 14% Toluene.
The cards were overlaminated on a Polaroid ColorCard Printer Model 85SC (Atlantek 85 DSC serial #000233).  Both the top and bottom temperature settings on the printer were 58.  The temperature between card and overlaminate PET film was measured
to be about 235.degree.  F.
The coating thickness of the film was measured by RMES at different positions on the film.  The data in Table 4 shows that the thickness of hand coated samples was not very uniform.  The data also indicate that the condition of the #10 bar was
TABLE-US-00004 TABLE 4 Coating Thickness Measurement #4 bar #4 bar #7 bar #10 bar 1 0.0002 0.0002 0.0003 0.0001 2 0.0002 0.0004 0.0002 0.0001 3 0.0003 0.0003 0.0002 0.0002 4 0.0002 0.0002 0.0003 0.0002 5 0.0002 0.0003 0.0002 0.0001 6 0.0001
0.0003 0.0004 0.0002 7 0.0002 0.0003 0.0003 0.0001 8 0.0001 0.0002 0.0004 0.0001 9 0.0003 0.0002 0.0004 0.0001 Ave (in) 0.00020 0.00026 0.00030 0.00013 Ave (.mu.) 5.08 6.60 7.62 3.32
PEEL TEST All test samples were cut to a width of 0.5 inch.  All test data recorded involved the average between peel extensions of 0.5 to 1.0 inch at 10 inches/min peel rate.  Table 5&#39;s data indicates that the adhesion increases with an increase
in the thickness of the adhesive layer.
TABLE-US-00005 TABLE 5 Instron Peel Test (LBS/INCH WIDTH) 3.3.mu.  Sample Adhesive 5.1.mu.  Adhesive 6.6.mu.  Adhesive 7.6.mu.  Adhesive 1 0.66 1.18 1.42 1.42 2 0.68 1.10* 1.42 cannot peel 3 0.90 1.64* 1.72* 1.96* 4 1.26 1.24 1.52 1.82 5 1.30*
1.02 1.72 2.12* 6 1.00 0.98 1.54* 1.60* 7 1.24* 0.88* 1.72* 1.84 8 1.20 1.56* 1.20 1.96 9 1.08 1.00 1.42 1.50* Ave 1.04 1.18 1.52 1.78 *broke the film
Based on this approach in this example, we believe that increasing the thickness of the hot melt adhesive layer will improve adhesion.  Mechanism coated samples can help confirm the proper thickness of the adhesive layer for this.
In this approach, we investigated an embodiment of the inventive material in the form of a hot melt adhesive formulation.  We investigated it using the following three types identification documents (in the form of cards):
(b) TESLIN-core cards having a polyester (e.g., PET) laminate layer with a D2T2 receiving layer on the front and surface and polyester (e.g., PET) on the back surface.  These cards are codenamed &quot;DSC&quot; and are similar to those some embodiments
disclosed in commonly owned U.S.  Pat.  No. 6,066,594, the contents of which are herein incorporated by reference,
(c) TESLIN core cards having a PC laminate layer with a D2T2 receiving layer on the front surface and a PC layer on the back surface.  These cards are codenamed DM-1 and also are similar to those described in U.S.  Pat.  No. 6,066,594 and also to
those described in commonly assigned U.S.  patent application 60/471,429, entitled &quot;Identification Card&quot;.  The contents of both of these documents are hereby incorporated by reference).
Note that 12% Vitel 5833 film was made by coating 30% solid adhesive solutions of 3.6% Vitel, 26.4%Vitel 2700B LMW, 56.0% MEK, 14% Toluene with #4 bar on 1.2 mil 301H PET film, and drying at 60 .degree.  C. for 5 min.
The above cards were overlaminated on a Polaroid ColorCard Printer Model 85 SC (Atlantek 85 DSC serial # 000233) printer.  Both the top and bottom temperature settings on the printer were 58.  The temperature between card and overlaminate PET
film was measured to be about 235.degree.  F.
The peel test was done using an Instron 5543 material test system.  All test samples were cut to a width of 0.5 inch.  All test data recorded were the average load force between peel extensions 0.5 to 1.0 inch at 10 inches/min peel rate.  Tables
6 through 8 shows the results of peel testing on the three types of cards, each having the indicated overlaminate:
TABLE-US-00006 TABLE 6 Instron Peel Test of PVC Card (LBS/INCH WIDTH) PVC PVC Sample TG 12% Vitel 5833 1 Cannot peel Cannot peel 2 Cannot peel Cannot peel 3 2.26* Cannot peel 4 Cannot peel Cannot peel 5 Cannot peel Cannot peel 6 Cannot peel
Cannot peel 7 Cannot peel Cannot peel 8 Cannot peel Cannot peel 9 2.42* Cannot peel *broke the film
TABLE-US-00007 TABLE 7 Instron Peel Test of DSC Card (LBS/INCH WIDTH) DSC DSC Front DSC Back Samples Front TG 12% Vitel 5833 DSC Back TV 12% Vitel 5833 1 Cannot peel Cannot peel 0.58 1.94* 2 Cannot peel Cannot peel 0.88 Cannot peel 3 Cannot peel
Cannot peel 0.46 1.84* 4 Cannot peel Cannot peel 0.50 Cannot peel 5 Cannot peel Cannot peel 0.46 Cannot peel 6 Cannot peel Cannot peel 0.56 2.28* 7 Cannot peel Cannot peel 0.60 Cannot peel 8 Cannot peel Cannot peel 0.52 Cannot peel 9 Cannot peel Cannot
peel 0.62 Cannot peel *broke the film
TABLE-US-00008 TABLE 8 Instron Peel Test of DM-1 Card (LBS/INCH WIDTH) DM-1 Front DM-1 Front DM-1 Back DM-1 Back Samples TG 12% Vitel 5833 Smurfit 12% Vitel 5833 1 Cannot peel Cannot peel 0.92 2.44* 2 Cannot peel Cannot peel 0.84 2.24* 3 2.56*
Cannot peel 0.76 Cannot peel 4 2.52* Cannot peel 0.78 Cannot peel 5 Cannot peel Cannot peel 0.70 2.22* 6 Cannot peel Cannot peel 0.82 1.84* 7 2.64* Cannot peel 0.78 1.74* 8 Cannot peel Cannot peel 0.74 1.98* 9 2.40* Cannot peel 0.80 1.84* *broke the film
Based on our testing in this example, we have found that an inventive material that includes, for example, 12% Vitel 5833 film is equal to or better than the current overlaminate films used on many identification documents.  We believe that our
inventive material, using a range of 5-20% Vitel 5833 (or equivalent materials) has the potential to replace all other adhesive layers for overlamination of ID documents such as ID cards.
FIG. 1A is an illustrative example of an identification document 10, before an attempted tampering by heat intrusion.  Details of the construction of such an identification document and of forming information on or in it are presumed to be within
the skill of those in the art and are not provided here.  The identification document 10 includes, by way of example only, a bearer image 12, biometric data 14, a bar code 15, demographic data 16, and a ghost image 18.  The ID document 10 includes an
overlaminate 62 (shown in greater detail in FIGS. 2 and 3A), and, in this example, the overlaminate includes a pre-printed security pattern 17.  The pre-printed security pattern 17 can, in practice, cover the entire surface of the ID document 10, but for
purposes of illustration the details of the pattern are shown in just a few corners of the ID document.
The ID document 10 can be formed using a core material such as PVC, TESLIN, polycarbonate (PC), etc. Image 12 is preferably a color image, but the present invention is not limited to such.  The document optionally includes ghost image 18, which
can be a screened-back or &quot;Ghost&quot; version of image 10.  Ghost image 18 is can be visible under normal viewing conditions or may be a &quot;cover&quot; image, visible only under appropriate conditions (e.g., light, temperature, etc.).  We note that an ID document
10 need not include all of the features shown in FIG. 1A, and that the illustrated features are provided by way of example.  Additional features may, for example, include magnetic stripes, digital watermarks, optically variable devices (OVD&#39;s), tactile
features (e.g., those made by laser engraving), etc. These features, along with the positioning or embedding of the features, are optional, and are not required to practice the present invention.
FIG. 3A is a cross sectional view of the identification document 10 of FIG. 1, taken along the A-A line.  As FIG. 3A illustrates, the identification document 10 is made up of a core layer 50 sandwiched between layers of laminate 56 and
overlaminate 60.  The core layer 50 can be preprinted with fixed information 52, such as the name of the issuer (for example, in FIG. 1A the fixed information includes the issuer &quot;STATE OF MASSACHUSETTS&quot;.  A layer of a first type of adhesive 54 joins the
laminate 56 to the core layer 50 (alternately, if the core layer 50 and laminate 56 are substantially miscible (e.g., the same material), the layer of first type of adhesive 54 can be eliminated).  Personalized information 58, such as demographic data
16, bearer image 12, bar code 15, etc., can be printed or formed onto (or into) laminate layer 56 by any of the methods previously described (e.g., printing, laser engraving, etc., as described herein).  In this example, the personalized information 58
is formed using D2T2 printing.
The overlaminate 62 (which may include a security pattern 17) is joined to the laminate 56 by a second adhesive layer 60 that includes at least a portion of the inventive material described herein.  For example, in one embodiment, the entire
second adhesive layer 60 comprises inventive material.  In an advantageous embodiment, the inventive material comprising the entire second adhesive layer 60 is an adhesive formulation containing 50-99% of a thermally active low glass transition
temperature (T.sub.g) polymeric resin and 1-50% of a multifunctional crystalline polymer.  We have found that a particularly advantageous embodiment of the invention uses, for the second adhesive layer 60, a formulation containing about 5-20%
tri-functional polyester (e.g., Vitel 5833) and 1-50% of a multifunctional crystalline polymer.  The layer 60 also can be constructed such that only portions of it contain the inventive material, and the remainder is another material, such as a material
similar to the first adhesive 54.  For example, the inventive material can be a pattern formed within the layer 60.
During an attempt at intrusion, an intruder may attempt to remove or lift the overlaminate 60, as shown in FIG. 2, to get at the personalized information formed on the card.  Heating the ID document to relatively high temperatures can sometimes
permit the overlaminate 60 to be lifted, as can application of certain chemicals.  Often, because the overlaminate contains security patterns 17 that are very difficult to replicate or purchase, the intruder will not completely remove the overlaminate
60, but will instead lift it, alter part or all of the information (e.g., by replacing photos, changing data, etc.), then relaminate the overlaminate to the remaining card structure (shown in FIG. 2 as 50, 54, 56, 60.  If heat is used to attempt to lift
the overlaminate 60, temperatures above a predetermined temperature (in the example of Vitel 5833, about 220 degrees Fahrenheit), will cause visible crystals to form that will remain visible even if the overlaminate 60 is successfully reattached.  If a
chemical is used to lift the overlaminate 60, the heat of re-laminating the overlaminate 60 likely still will cause crystals to form.
As those skilled in the art will appreciate, the inventive material can be adapted to have different &quot;predetermined temperatures&quot; of crystallization, and these predetermined temperatures can be kept confidential.  A counterfeiter likely will not
know that using conventional heat and lamination processes will cause crystallization, and he or she may not have access to equipment that can enable lamination in the limited &quot;non crystallizing&quot; effective range.
FIG. 3B is an illustrative example showing the identification document of FIG. 1A after a portion of it (the portion overlaying the bearer image 12 and signature disposed below it) were heated to a predetermined temperature (in this example, 220
degrees Fahrenheit).  As FIG. 1 illustrated, a plurality of crystals 20 are visible on the card in the portion that was heated.  These crystals 20 form in the layer 60, as shown in FIG. 3B.  It should be understood that the appearance, size, and location
of the crystals 20 are provided by way of example only and are not intended as limiting.  The crystals 20 need not be the same size as each other and need not be evenly distributed or oriented.  The crystals 20 may be much smaller or much larger than
shown in FIGS. 1B and 3B, but they will be visible, whether alone or as a pattern, to the naked eye.  Even if the peeled layer of FIG. 2 is successfully relaminated, the crystals will be visible if the relamination occurs above a certain temperature.
Thus, use of the multifunctional crystalline polymer can help to provide further visible evidence of tampering, especially if the attempted tampering used temperatures above 220 degrees Fahrenheit.  One example of a multifunctional crystalline
polymer that is used in at least some embodiments of the invention is VITEL 5833, which is a low molecular weight, highly functional branched polyester with high crystallinity.
The above described &quot;snow flake like&quot; crystals can be visible to the naked human eye and, in at least one embodiment, are substantially irreversible (e.g., once formed into the material after heating, they remain visible there).  The appearance
of the crystals provides visual evidence of possible tampering of the ID document (such as an attempt by the counterfeiter to delaminate an overlaminate in an attempt to alter information on the ID document), because the crystals ordinarily would not be
visible in the material unless the material has been exposed to temperatures above a predetermined level (e.g., in one embodiment, about 220 degrees Fahrenheit or above).
Of course, as those skilled in the art will appreciate, further modifications to the ID document can work together with the second adhesive layer 60 disclosed herein to further provide evidence of tampering.  For example, if the variable or
personalized information or indicia is an image (e.g., the image of the ID document bearer), the image can be printed so that it includes a feature that is difficult to replicate and/or re-align after an attempted de-lamination and re-lamination, such as
a pattern of fine lines, guilloche, interlocking patterns of colors, moire patterns, etc. We also expressly contemplate that the second adhesive layer 60 can be used with indicia that are printed using a cohesively failing ink, such as that described in
commonly assigned U.S.  patent application Ser.  No. 10/329,315 (now Publication no. 2003-0226897), entitled &quot;Ink with Cohesive Failure and Identification Document Including Same&quot;, the contents of which are hereby incorporated by reference.
The thickness of the applied material in second adhesive layer 60 is not important, and those skilled the art will appreciate that the thickness can be varied to suit different configurations of ID documents.  For example, we have found that
thicknesses of between 0.1 and 15 microns to be advantageous when used on ID documents such as ISO-compliant ID cards.
It also should be noted that the second adhesive layer 60 can be provided adjacent to ANY type of indicia on an ID document, fixed or variable, and that the use of variable indicia herein is provided merely by way of illustration.  As those
skilled in the art appreciate, tampering and/or counterfeiting of ID documents is not limited to actions taken with respect to variable indicia, but also can include actions taken with fixed indicia, as well.
We expressly anticipate that the invention also may be adapted to work with non-printed and non-laser engraved indicia on ID documents, such (OVD&#39;s), or virtually any feature which can be tampered with.
The particular combinations of elements and features in the above-detailed embodiments are exemplary only; the interchanging and substitution of these teachings with other teachings in this and the incorporated-by-reference patent documents are
It should be appreciated that while FIGS. 1-3 illustrate a particular species of ID document --a driver&#39;s license --the present invention is not so limited.  The technology disclosed herein can be used in combination with other technologies.
Also, instead of ID documents, the inventive techniques can be employed with product tags, product packaging, labels, business cards, bags, charts, smart cards, maps, labels, etc., etc. For example, we believe the invention may have applicability in
providing tamper detectable features for some types of packages.
It should be understood that, in the FIGs of this application, in some instances, a plurality of elements may be shown as illustrative of a particular system element, and a single system element or method step may be shown as illustrative of a
plurality of elements.  It should be understood that showing a plurality of a particular element is not intended to imply that a composition or article or method implemented in accordance with the invention must comprise more than one of that element or
step, nor is it intended by illustrating a single element that the invention is limited to embodiments having only a single one of that respective element.  In addition, the total number of elements shown for a particular article (e.g., layers of
laminate and/or adhesive) is not intended to be limiting; those skilled in the art will recognize that the number of a particular system element or method steps can, in some instances, be selected to accommodate the particular user needs.
scope of the present invention.  Thus, the exemplary embodiments are only selected samples of the solutions available by combining the teachings referenced above.  The other solutions necessarily are not exhaustively described herein, but are fairly
within the understanding of an artisan given the foregoing disclosure and familiarity with the cited art.  The particular combinations of elements and features in the above-detailed embodiments are exemplary only; the interchanging and substitution of
these teachings with other teachings in this and the incorporated-by-reference patent documents are also expressly contemplated.
"Tamper Evident Adhesive And Identification Document Including Same - Patent 7744002"
http://img.docstoccdn.com/thumb/206/118587542.png