Patent US5196173 - Apparatus for process for growing crystals of semiconductor materials - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign in<nobr>Advanced Patent Search</nobr>PatentsIn apparatuses for melting semiconductor material and growing single crystals of semiconductor material, the apparatus comprising: (a) a furnace, (b) a cylindrical double crucible assembly comprising an inner crucible in which single crystals of semiconductor material are grown at a vertical-concentric...http://www.google.com/patents/US5196173?utm_source=gb-gplus-sharePatent US5196173 - Apparatus for process for growing crystals of semiconductor materialsAdvanced Patent SearchPublication numberUS5196173 APublication typeGrantApplication numberUS 07/420,518Publication dateMar 23, 1993Filing dateOct 12, 1989Priority dateOct 13, 1988Fee statusLapsedAlso published asDE68916157D1, DE68916157T2, EP0364899A1, EP0364899B1Publication number07420518, 420518, US 5196173 A, US 5196173A, US-A-5196173, US5196173 A, US5196173AInventorsYoshiaki Arai, Michio Kida, Naoki Ono, Kensho SahiraOriginal AssigneeMitsubishi Materials CorporationExport CitationBiBTeX, EndNote, RefManPatent Citations (17), Non-Patent Citations (4), Referenced by (24), Classifications (7), Legal Events (6) External Links: USPTO, USPTO Assignment, EspacenetApparatus for process for growing crystals of semiconductor materialsUS 5196173 AAbstract In apparatuses for melting semiconductor material and growing single crystals of semiconductor material, the apparatus comprising:
(b) a cylindrical double crucible assembly comprising an inner crucible in which single crystals of semiconductor material are grown at a vertical-concentric line thereof, the inner crucible having an upper part and a lower part, and an outer crucible in which melted semiconductor material is received, the outer crucible having the inner crucible disposed therein,
(c) a susceptor for supporting the outer crucible,
(d) rotating means for rotating the susceptor,
(e) a feed pipe for supplying starting material in the space formed between the inner and the outer crucibles,
(f) fluid-passage means for permitting the melted semiconductor material to flow between the inner and outer crucibles, the fluid-passage means being disposed at the lower part of the inner crucible, and
wherein the inner crucible being set inside the outer crucible in a separable manner, the apparatus improved comprising:
(g) joining means for setting the inner crucible inside the outer crucible concentrically, the joining means being disposed inside the furnace, and
(h) engaging means for engaging the inner crucible and joining means detachably, the engaging means being disposed at the upper part of the inner crucible so as to engage a respective joining means.
What is claimed is: 1. An apparatus for melting semiconductor material and growing single crystals of semiconductor material, the apparatus comprising:(a) a furnace, (b) a cylindrical double crucible assembly comprising a) an inner crucible open at a bottom thereof, in which single crystals of semiconductor material are grown, the inner crucible having side walls and being bottomless, and b) an outer crucible having a bottom in which melted semiconductor material is received, the outer crucible having the inner crucible disposed in contact with said outer crucible bottom in a separable manner, (c) a susceptor for supporting the outer crucible, (d) rotating means for rotating the susceptor, (e) a feed pipe for supplying starting material in the space formed between the inner and outer crucibles, (f) fluid-passage means for permitting the melted semiconductor material to flow between the inner and outer crucibles, the fluid-passage means being disposed at the lower part of the inner crucible, (g) heating means disposed to surround the susceptor for heating the semiconductor material in the double crucible, (h) at least two joining means for concentrically setting the inner crucible inside the outer crucible inside the furnace, said joining means being disposed at least at two circumferential locations relative to the inner crucible, separated by circumferential intervals, (i) engaging means coupled to said inner crucible at an upper end of said side walls, for detachably engaging with each said joining means at the upper end of the inner crucible, said inner crucible being adapted to operate with said joining means detached, and (j) drive means for providing vertical movement of either said inner or outer crucible. 2. A semiconductor crystal growing apparatus according to claim 1, wherein said drive means moves the joining means vertically inside the furnace between a coupled position in which the inner crucible is inside the outer crucible and a removed position in which the inner crucible is separated from the outer crucible.
3. A semiconductor crystal growing apparatus according to claim 1 or claim 2, wherein the inner crucible is composed of quartz and joining means are composed of heat-resistant materials.
4. An apparatus for melting semiconductor material and growing single crystals of semiconductor material according to claim 1, wherein the fluid passage means is an orifice formed in a lower part of the side walls of the inner crucible.
5. An apparatus for melting semiconductor material and growing single crystals of semiconductor material according to claim 1, wherein the fluid passage means is a hole formed in a lower part of the side walls of the inner crucible.
6. An apparatus for melting semiconductor material and growing single crystals of semiconductor material according to claim 1, wherein the fluid passage means is a notch formed in a lower edge of the side walls of the inner crucible.
The field of the invention relates to an apparatus and to a process for growing crystals of semiconductor materials by using a double crucible which has an inner crucible and an outer crucible and in which the semiconductor material is continually supplied in a space formed between the inner and outer crucible.
In a batch-type apparatus for growing silicon single-crystal ingots, the quantity of melted silicon contained in a quartz crucible decreases as the silicon single crystal grows. As a result, qualities such as oxygen concentration, crystallization front, and dopant concentration are not uniform longitudinally within the crystalline ingot obtained by the batch-type apparatus. More specifically, the oxygen concentration in the crystal depends on the quantity of oxygen dissolved in the silicon melt, thereby varying as the silicon melt in the quartz crucible varies. In addition, since the quantity of the melt varies, the thermal distribution in the furnace fluctuates and the convection in the melt varies, so that the crystallization front varies. Furthermore, the dopant, such as phosphorus, boron, antimony, and the like, is generally added to the melt in order to control the electric conductivity of the single crystal. Since the segregation constant of such impurities is not identical to 1, the dopant concentration in the crystal differs as the crystal grows.
Thus, the quality of the single crystal ingot varies in the longitudinal direction, and therefore only a portion of the ingot has the desired qualities. Additionally, productivity has been low in such batch processes.
The approach to resolve the above disadvantages is to use a continually-supplied-type apparatus hitherto proposed wherein the single crystal ingot is grown while the quartz crucible is being charged with material. U.S. Pat. No. 2,892,739 and Japanese Patent Application First Publication "Kokai" No. 61-36197 describe one such apparatus which is the simplest crucible characterized by the combination of a continually-supplied-type crucible charging of the material and a two-wall-type crucible.
The above continually-supplied-type apparatus has, however, the following problems. First, although the melting point of the silicon is above 1420� C., the quartz of which the crucible is composed begins to soften at about 1100� C. As a result, the outer crucible supported by a graphite susceptor is not greatly deformed from its original shape greatly and the inner crucible may be deformed since the inner one is not supported sufficiently, so that the growing of the single crystal is adversely affected. Specifically, a great quantity of heat must be applied to the crucible in the initial stage of the pulling cycle in order to melt the material in the crucible, and the temperature in the furnace reaches the maximum at that time. Therefore, the deformation of the inner crucible is greatest at that time. FIGS. 1 to 4 illustrate conventional apparatuses each of which comprises a double quartz crucible. The double quartz crucible assembly is housed in a graphite susceptor 103 and comprises an inner crucible 101 and an outer crucible 102, and a resistance heater 104. The double crucible assembly is filled with a charge of unmelted starting silicon material 105 which, upon heating, forms silicon material melt 106. As shown in FIG. 1, the charge is heated by the heater 104 until it is melted thoroughly. Each inner crucible 101, however, is subjected to deformation as shown in FIGS. 2 and 4, respectively, as the silicon material is melted.
In addition, since quartz has a high heat-insulating effect, the temperature is lower on the inner side of the inner crucible than on the outer side thereof. This may be advantageous during the growth of crystals since the silicon material introduced between the inner and outer crucibles can be melted efficiently, but it is disadvantageous when melting the silicon material initially fed in the crucible since the inner crucible itself prevents the heat generated by the heater from being transferred to its interior, so that the efficiency of the melting is lowered. If the quantity of heat applied to the material should be increased to reduce the time required for the melting, the inner crucible would be subjected to excessive deformation.
In Japanese Patent Application First Publication "Kokai" No. 55-47300, there has been proposed an apparatus as shown in FIG. 5. The apparatus comprises the inner crucible 101 fixedly secured to a fixed portion 108 through a support 107. Such an apparatus, however, has the disadvantages that the inner crucible 101 cannot be rotated together with the outer crucible 102. For growing a single crystal ingot, the crucible must be generally rotated at a speed of 5 rpm to 10 rpm. Without such rotation, the formation of single crystals may be difficult.
In conjunction with the use of the double crucible, Japanese Patent Application First Publication "Kokai" No. 58-204895 discloses an apparatus which comprises a mechanism for causing the inner crucible to rotate and move upwardly and downwardly. The apparatus, however, has the drawbacks that it is large and complex in construction, thereby being high in cost.
SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to solve the above problems and to provide an apparatus and process for growing crystals of semiconductor materials by using a two-wall-type crucible which has an inner crucible and an outer crucible and in which the semiconductor material is supplied between the inner and outer crucible successively. In apparatuses for melting semiconductor material and growing single crystals of semiconductor material, the apparatus comprising:
(g) heating means disposed so as to surround the susceptor for heating the semiconductor material contained in the double crucible;
(h) joining means for setting the inner crucible inside the outer crucible concentrically, the joining means being disposed inside the furnace, and
(i) engaging means for engaging the inner crucible and joining means detachably, the engaging means being disposed at the upper part of the inner crucible so as to engage a respective joining means.
According to a second aspect of the present invention, there is provided a process for melting semiconductor material and growing single crystals of the semiconductor material, the process comprising the steps of:
(a) providing a crystal-growing apparatus having a cylindrical double crucible comprising an inner crucible in which single crystals of the semiconductor material are grown at a concentric line therein, the inner crucible being contained in a separable manner in an outer crucible in which melted semiconductor material is received, a susceptor for supporting the outer crucible, a rotating means for rotating the susceptor, joining means for setting the inner crucible and the outer crucible concentrically, the joining means disposed inside a furnace, and engaging means for engaging the inner crucible with joining means detachably, the engaging means disposed at the upper part of the inner crucible so as to engage the engaging means with a respective joining means;
(b) raising the inner crucible by engaging the joining means with the respective engaging means of the inner crucible, so as to remove the inner crucible from the outer crucible;
(c) charging the outer crucible with semiconductor material;
(d) subsequently heating the outer crucible to thereby melt the semiconductor material in the outer crucible;
(e) subsequently moving downwardly joining means holding the inner crucible so as to couple the inner and outer crucibles concentrically;
(d) subsequently immersing a seed crystal in the melt in the inner crucible on the concentric line and withdrawing the seed crystal from the melt to thereby grow the semiconductor crystal.
BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic cross-sectional view showing a conventional crystal-growing apparatus;
FIG. 2 is a view similar to FIG. 1, but showing how an inner crucible thereof is deformed after heating;
FIG. 3 is a schematic cross-sectional view showing another conventional crystal-growing apparatus;
FIG. 4 is a view similar to FIG. 3, but showing how an inner crucible thereof is deformed after heating;
FIG. 5 is a cross-sectional view of a part of a third conventional crystal-growing apparatus;
FIG. 6 is a vertical cross-sectional view of a crystal-growing apparatus provided in accordance with a first embodiment of the present invention in a condition that an inner crucible is removed from an outer crucible;
FIG. 7 is a view similar to FIG. 6, but showing a set position where an inner crucible is set in an outer crucible;
FIG. 8 is a vertical cross-sectional view of a mechanism to move the inner crucible upwardly and downwardly;
FIG. 9 is a side view of a part of the mechanism shown in FIG. 8;
FIG. 10 is a plan view showing how engaging members engage with holders connected to holder joining members;
FIG. 11 is a view similar to FIG. 10, but showing the inner crucible removed from the outer crucible;
FIG. 12 is a schematic cross-sectional view of a part of a modified apparatus in accordance with the present invention;
FIG. 13 is a plan view of the same apparatus as shown in FIG. 12;
FIG. 14 is a plan view of a part of another modified apparatus in accordance with the present invention;
FIG. 15 is a plan view of a part of a third modified apparatus in accordance with the present invention;
FIG. 16 is a side view of a part of a fourth modified apparatus in accordance with the present invention;
FIG. 17 is a side view of a part of a fifth modified apparatus in accordance with the present invention;
FIG. 18 is a vertical cross-sectional view of a sixth modified apparatus in accordance with the present invention;
FIG. 19 is a vertical cross-sectional view of a seventh modified apparatus in accordance with the present invention;
FIG. 20 is a vertical cross-sectional view of an eighth modified apparatus in accordance with the present invention;
FIG. 21 is a plan view of a joining ring for joining an inner crucible of the apparatus shown in FIG. 20; and
FIG. 22 is a vertical cross-sectional view of the ring cut along the arrows XVII--XVII.
DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION Referring to FIGS. 6 to 11, there is illustrated an apparatus for growing single crystals of semiconductor materials according to the present invention.
The apparatus comprises a furnace 10 consisting of an upper part 10A and a lower part 10B, an outer crucible 13 made of quartz, an inner crucible 16 made of quartz, to be disposed detachably inside the outer crucible 13, a susceptor 12 made of graphite for supporting the outer crucible 13 fixedly, a shaft 11 fixed to the susceptor 12 thereupon for rotating the outer crucible 13 and moving it upwardly and downwardly, a heater 14 surrounding the susceptor 12, and a heat reserving shell 15 surrounding the heater 14. The inner crucible 16 is of a cylindrical shape smaller in diameter than the outer crucible 13, and includes a plurality of apertures of fluid passages 16A formed therethrough and disposed adjacent to its lower end. Such apparatuses 16A permit the flow of molten material toward and away from the inner crucible 16, from and to an annular volume defined between the peripheral walls of the outer and inner crucibles 13 and 16. The inner crucible is also preferably open at a bottom thereof. A pair of engaging members 17 made of quartz are disposed outwardly on the opposite side of the upper peripheral part of the inner crucible 16. A feed pipe 18 for supplying starting silicon materials between the inner crucible 16 and the outer crucible 13 is inserted into the furnace 10 from the outside thereof. A drive mechanism (not shown) for pulling and rotating a wire for retaining a seed crystal is provided above the furnace 10. The wire must be concentric with both the inner and outer crucibles.
The upper part 10A of the furnace 10 is fixed to the lower part 10B at one end thereof and fixed to a cylindrical insert part 20 for pulling the wire at the other end thereof. A pair of hollow rods 21 made of stainless steel are set vertically through a shoulder part 10C of the upper part 10A. Each hollow rod 21 is supported by an airtight and air-cooled seal 22 so that the hollow rod 21 can be moved upwardly and downwardly. As shown in FIG. 8, a stainless steel pipe 21A is inserted into the hollow rod 21. Cooled water is supplied from an inlet nozzle 21B disposed between the hollow rod 21 and the pipe 21A, passes through the pipe 21A upwardly, and is then drawn off outside from an outlet nozzle 21C connected to the pipe 21A.
In addition, a screw shaft 23 for moving the inner crucible 16 upwardly and downwardly is set parallel to each hollow rod 21 by a shaft receiver 24 and supported by a supporting plate 23A attached to the shoulder part 10C of the furnace 10. The screw shaft 23 has an exterior threaded portion and the shaft receiver 24 has an interior threaded portion engaged with the exterior threaded portion of the screw shaft 23. On an upper end of the screw shaft 23, a handle 25 for rotating the screw shaft 23 is fixed so that each hollow rod 21 can be moved upwardly and downwardly by rotating the handle 25.
A lower end portion of each hollow rod 21 is fixed to a horizontal part 26A of a holder joining member 26 for setting the inner crucible 16 in the outer crucible 13 concentrically and a vertical part 26B fixed to the horizontal part 26A at one end thereof is fixed to a holder 27 for holding the engaging member 17 of the inner crucible 16. The feed pipe 18 is disposed so that the pipe 18 does not disturb the holder joining member 26. As the material of the holder joining member 26, a heat resistant simplex such as Mo, Ta, W, C, SiC, or the like, or a composite material, is applied. Furthermore, a coating layer made of SiC or the like is disposed on the surface of the holder joining member 26, if necessary.
As shown in FIGS. 10 and 11, the pair of holders 27 fixed to the pair of holder joining members 26 respectively are disposed at a distance shorter than the distance between outer ends of the pair of engaging members 17 and longer than the outside diameter of the inner crucible 16. In order to move the inner crucible 16 upwardly, each engaging member 17 is set so as to meet each holder 27 respectively as shown in FIG. 10 and the handle 25 is rotated so as to move the screw shaft 23 upwardly. In order to remove each holder 27 from each engaging member 17, the shaft 11 indirectly connected to the outer crucible 13 is rotated in the condition of the inner crucible 16 being held in the outer crucible 13 as shown in FIG. 11. There must be friction between the surfaces of engaging member 17 and the holder 27 so as not to separate them when the inner crucible 16 is moved upwardly and downwardly. A concave-convex mechanism may be applied between each engaging member 17 and each holder 27.
Next, a process for using the apparatus of the present invention will be shown.
In the condition that the inner crucible 16 is released from the outer crucible 13 as shown in FIG. 6, the starting silicon material of silicon is charged in the outer crucible 13 from the feed pipe 18 under an argon atmosphere by injecting argon gas from the insert part 20 into the furnace 10 and the heater 14 is turned on after the position of the outer crucible 13 is set by adjusting the shaft 11 connected to the susceptor 12.
After the starting silicon material contained in the outer crucible 13 is dissolved, the inner crucible 16 is moved downwardly by rotating the handle 25 so that the inner crucible 16 and the outer crucible 13 are fitted in an appropriate position so that both crucibles are positioned concentrically. Each engaging member 17 of the inner crucible 16 is released from each holder 27 by rotating the shaft 11 connected to the susceptor 12 fixed to the outer crucible 13 including the inner crucible 16 at a 90� angle. The holder 27 is lifted by rotating the handle 25 so as to move the screw shaft 23 connected indirectly to the holder 27 upwardly. The growing of a single crystal ingot is begun in a usual manner when starting the melt of the silicon material.
As described above, in the apparatus in accordance with the present invention, the inner crucible 16 is released from the outer crucible 13 when the silicon starting material is melted at a high temperature, so that the inner crucible 16 is prevented from excessive deformation by heat and the effectiveness of melting the starting material is greater than in the inner crucible 16. Therefore, the time required for the melting can be reduced substantially, thereby enhancing the productivity markedly.
Furthermore, as the inner crucible 16 is moved to the prescribed position in the outer crucible 13, the crucibles are worked and rotated as a double crucible. Therefore, a silicon single-crystal having a uniform quality can be grown smoothly and the apparatus according to the present invention is simple in construction and is easily serviced.
When growing a silicon single crystal, the holder joining member 26 and the holder 27 are released upwardly from the double crucible by using the screw shaft 23 which is connected to them indirectly. Therefore, there are the advantages such that the holder joining member 26 does not meet the feed pipe 18 and that the pieces of the starting silicon materials striking the holder joining member 26 cause the growing single-crystal to break. Furthermore, the inner crucible 16 can be removed the upper inside of the furnace 10, so that the deformation of the inner crucible 16 by heat is smaller than in the case where the holder joining member 26 and the holder 27 are fixed to the furnace 10. The outer crucible 13 is set in an appropriate position by adjusting the shaft 11 when the starting silicon material filled in the outer crucible 13 is heated and melted. Accordingly, a good position of the outer crucible 13 can be selected so that the effectiveness of melting the starting material is optimal.
While the present invention has been specifically shown and described herein, many modifications and variations are possible in the light of the above teachings. For example, although in the above embodiment, each holder 27 holds each engaging member 17 of the inner crucible 16 radially-inwardly outside of the inner crucible 16, the holder 27 may hold the engaging member 17 radially-outwardly inside of the inner crucible 16 as shown in FIGS. 12 and 13. In addition, as schematically shown in FIG. 14, two pairs of engaging members 17 of the inner crucible 16 may be utilized instead of a pair of engaging members 17 shown in FIG. 11. Two pairs of holders 27, each holder 27 connected to the holder joining member 26, are needed so that each holder meets each engaging member 17. In this case, the apparatus has an advantage in that the inner crucible 16 can be moved upwardly and downwardly while horizontally stable. When each engaging member 17 is lengthened circumferentially and the rim of the inner crucible 16 is expanded into a flange as shown in FIG. 15, the rim of the inner crucible 16 is strengthened so as to be less deformable.
In addition, an engaging member 17 is made by cutting the upper part of the inner crucible 16 to form an L-shaped or T-shaped gutter or concavity as shown in FIG. 16. Furthermore, an inner crucible 16 comprises a cylindrical member 30 made of quartz and a pair of reverse-L-shaped engaging members 31 made of heat-resistant material fixed to the upper part of the cylindrical member 30 detachably by bolts. In this case, although the cylindrical member 30 is disposable after use, the engaging members 31 can be reused. Therefore, the cost of the apparatus is reduced.
Furthermore, a holder joining member 26 may be fixed to the furnace 10, as shown in FIG. 18, or it may be fixed to each upper end of the heat-reserving shell 15 as shown in FIG. 19. The outer crucible 13 is moved upwardly until fitting to the inner crucible 16 to comprise a double crucible, and the double crucible is rotated to release the inner crucible 16 from the holder joining member 26. These apparatuses are simpler than the apparatus having a mechanism of moving the holder joining member 26.
An applied apparatus is shown in FIG. 20. This apparatus has a joining ring 37 fixed horizontally to the heat-reserving shell 15. As best shown in FIGS. 21 and 22, the joining ring 37 has four plate-shaped engaging portions 37A extended radially-inwardly at every 90� angle of the circumference of the joining ring 37. The material of the joining ring 37 is the same as the holder joining member 26 described above. Four long plate-shaped joining members 38 are fixed to the upper end of the inner crucible 16 at every 90� angle of the circumference of the upper end of the inner crucible 16 by using bolts 39 and nuts 40 made of Mo. The material of the joining member 38 is the same as the holder joining member 26 described above. At the upper end of each joining member 38, a hanging member 38A is disposed horizontally radially outward of the inner crucible 16. At the upper and inner circumference of each engaging portion 37A of the joining ring 37, a tapered part 37B is disposed. Each tapered part 37B is engaged with the respective hanging member 38A when the outer crucible is moved upwardly. In this apparatus, the operations are the same as those in the apparatus shown in FIGS. 18 and 19.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS2892739 *Oct 1, 1954Jun 30, 1959Honeywell Regulator CoCrystal growing procedureUS3637439 *Jul 2, 1969Jan 25, 1972Metallurgie HobokenProcess and apparatus for pulling single crystals of germaniumUS4609425 *May 2, 1984Sep 2, 1986U.S. Philips CorporationCold crucible system and method for the meeting and crystallization of non-metallic inorganic compoundsUS4936949 *Jun 1, 1988Jun 26, 1990Mitsubishi Kinzoku Kabushiki KaishaCzochraski process for growing crystals using double wall crucibleUS4938837 *Jul 6, 1988Jul 3, 1990Sumitomo Electric Industries, Ltd.Semiconductor single crystal drawingUS4944834 *Jul 7, 1988Jul 31, 1990Sumitomo Electric Industries, Ltd.Process of pulling a crystalEP0219776A1 *Oct 10, 1986Apr 29, 1987Sumitomo Electric Industries LimitedCrucible recovering method and apparatus thereforEP0293865A1 *Jun 1, 1988Dec 7, 1988Mitsubishi Materials CorporationApparatus and process for growing crystals of semiconductor materialsGB939102A * Title not availableJPS5547300A * Title not availableJPS6018634A * Title not availableJPS6472987A * Title not availableJPS6483593A * Title not availableJPS58204895A * Title not availableJPS62275088A * Title not availableJPS63248792A * Title not availableJPS63303894A * Title not available* Cited by examinerNon-Patent CitationsReference1"Properties of Gap Single Crystals" Journal of Electrochemical Society, vol. 118, No. 2, Feb. 1971, pp. 307-312.2 *English Translation of JP 62 275088, Tada et al., Nov. 30, 1992.3English Translation of JP-62-275088, Tada et al., Nov. 30, 1992.4 *Properties of Gap Single Crystals Journal of Electrochemical Society, vol. 118, No. 2, Feb. 1971, pp. 307 312.* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS5361721 *Feb 2, 1993Nov 8, 1994Shin-Etsu Handotai Co., Ltd.Continuous process; from molten polycrystals such as siliconUS5373805 *Oct 15, 1992Dec 20, 1994Shin-Etsu Handotai Co., Ltd.Single crystal pulling apparatusUS5575847 *Nov 8, 1994Nov 19, 1996Sumitomo Sitix CorporationApparatus for producing single crystalsUS5588993 *Jul 25, 1995Dec 31, 1996Memc Electronic Materials, Inc.Method for preparing molten silicon melt from polycrystalline silicon chargeUS5683505 *Feb 27, 1996Nov 4, 1997Sumitomo Sitix CorporationProcess for producing single crystalsUS5720809 *Aug 2, 1995Feb 24, 1998Shin-Etsu Handotai Co., Ltd.Crucible for pulling silicon single crystalUS5720810 *Aug 22, 1995Feb 24, 1998Mitsubishi Materials CorporationDouble-walled crucible, inverted conical flow guide cover, short passage, flow guide cylinderUS5858085 *May 28, 1997Jan 12, 1999Mitsubishi Materials CorporationMethod for growing a semiconductor single-crystalUS5900059 *Apr 14, 1998May 4, 1999Komatsu Electronic Metals Co., Ltd.Method and apparatus for fabricating semiconductor single crystalUS5942032 *Aug 1, 1997Aug 24, 1999Memc Electronic Materials, Inc.Heat shield assembly and method of growing vacancy rich single crystal siliconUS5976247 *Jun 14, 1995Nov 2, 1999Memc Electronic Materials, Inc.Surface-treated crucibles for improved zero dislocation performanceUS5980629 *Jun 14, 1995Nov 9, 1999Memc Electronic Materials, Inc.Methods for improving zero dislocation yield of single crystalsUS6251184 *May 26, 1999Jun 26, 2001Samsung Electronics Co., Ltd.Insulating-containing ring-shaped heat shields for czochralski pullersUS6261364Sep 1, 1998Jul 17, 2001Mitsubishi Materials CorporationSemiconductor single-crystal growth systemUS6409833Mar 9, 2001Jun 25, 2002Samsung Electronics Co., Ltd.Insulating-containing ring-shaped heat shields and support members for Czochralski pullersUS6472040Dec 3, 1999Oct 29, 2002Samsung Electronics Co., Ltd.Semi-pure and pure monocrystalline silicon ingots and wafersUS6485807Oct 31, 2000Nov 26, 2002Samsung Electronics Co., Ltd.Silicon wafers having controlled distribution of defects, and methods of preparing the sameUS6503594Jun 28, 2001Jan 7, 2003Samsung Electronics Co., Ltd.Silicon wafers having controlled distribution of defects and slipUS6572700 *Feb 7, 2001Jun 3, 2003Sumitomo Electric Industries, Ltd.Semiconductor crystal, and method and apparatus of production thereofUS6676753Sep 4, 2002Jan 13, 2004Samsung Electronics Co., Ltd.Czochralski pullers for manufacturing monocrystalline silicon ingots, including heat shield having sloped portionsUS6780238Sep 4, 2002Aug 24, 2004Samsung Electronics Co., Ltd.Argon/ammonia rapid thermal annealing for silicon wafersUS6780244Feb 26, 2003Aug 24, 2004Sumitomo Electric Industries, Ltd.Method for producing a semiconductor crystalUS6866714May 5, 2003Mar 15, 2005Sumitomo Electric Industries, Ltd.Large size semiconductor crystal with low dislocation densityWO2013070642A1 *Nov 7, 2012May 16, 2013Graftech International Holdings Inc.Graphite crucible for silicon crystal production and method of ingot removal* Cited by examinerClassifications U.S. Classification117/213, 117/900International ClassificationC30B15/12, H01L21/208Cooperative ClassificationY10S117/90, C30B15/12European ClassificationC30B15/12Legal EventsDateCodeEventDescriptionMay 29, 2001FPExpired due to failure to pay maintenance feeEffective date: 20010323Mar 25, 2001LAPSLapse for failure to pay maintenance feesOct 17, 2000REMIMaintenance fee reminder mailedJul 25, 1996FPAYFee paymentYear of fee payment: 4Jun 6, 1991ASAssignmentOwner name: MITSUBISHI MATERIALS CORPORATIONFree format text: CHANGE OF NAME;ASSIGNOR:MITSUBISHI METAL CORPORATION;REEL/FRAME:006285/0368Effective date: 19910524Oct 12, 1989ASAssignmentOwner name: MITSUBISHI METAL CORPORATION, 5-2, OTEMACHI 1-CHOMFree format text: ASSIGNMENT OF ASSIGNORS INTEREST.;ASSIGNORS:ARAI, YOSHIAKI;KIDA, MICHIO;ONO, NAOKI;AND OTHERS;REEL/FRAME:005162/0931Effective date: 19891004RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services©2012 Google