Patent US8128689 - Bioerodible endoprosthesis with biostable inorganic layers - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inAdvanced Patent SearchPatentsMedical devices such as endoprostheses (e.g., stents) containing one or more biostable layers (e.g., biostable inorganic layers) and a biodegradable underlying structure are disclosed....http://www.google.com/patents/US8128689?utm_source=gb-gplus-sharePatent US8128689 - Bioerodible endoprosthesis with biostable inorganic layersAdvanced Patent SearchPublication numberUS8128689 B2Publication typeGrantApplication numberUS 11/855,542Publication dateMar 6, 2012Filing dateSep 14, 2007Priority dateSep 15, 2006Also published asCA2663304A1, DE602007011114D1, EP2121068A2, EP2121068B1, EP2210625A1, EP2210625B1, EP2210625B8, EP2399616A1, US20080071352, US20120150286, WO2008034048A2, WO2008034048A3Publication number11855542, 855542, US 8128689 B2, US 8128689B2, US-B2-8128689, US8128689 B2, US8128689B2InventorsJan Weber, Liliana Atanasoska, Scott ScheweOriginal AssigneeBoston Scientific Scimed, Inc.Export CitationBiBTeX, EndNote, RefManPatent Citations (198), Non-Patent Citations (332), Referenced by (2), Classifications (9), Legal Events (1) External Links: USPTO, USPTO Assignment, EspacenetBioerodible endoprosthesis with biostable inorganic layers
US 8128689 B2Abstract
1. A stent comprising a biostable layer and a bioerodible underlying structure, wherein the biostable layer is about 5% or less of a wall thickness of a strut of the stent, wherein the bioerodible underlying structure comprises a bioerodible metal.
2. The stent of claim 1, wherein the biostable layer has a thickness on average of about 10 to 20 nm.
3. The stent of claim 1, wherein the biostable layer has an average volume in the range of about 5,000 to 20,000 cubic micrometer per square millimeter of stent surface area.
4. The stent of any of claims 1-3, wherein the biostable layer comprises ceramic material.
5. The stent of claim 1, wherein the biostable layer comprises one or more metal oxides.
6. The stent of any of claims 1-3, wherein the biostable layer comprises a crystalline form of titanium oxide.
7. The stent of claim 1, wherein the biostable layer is on a surface of the stent.
8. The stent of claim 7, wherein the biostable layer is on an interior surface, an exterior surface or a sidewall.
9. The stent of claim 1, wherein at least a portion of the biostable layer is covered by a bioerodible layer.
10. The stent of claim 1, wherein the biostable layer formed by a sol-gel process.
11. The stent of claim 1, wherein the biostable layer is formed by a process comprising:
modifying a selected portion of the surface of the underlying structure with hydroxyl groups;
allowing the hydroxyl groups to react with one or more metal alkoxides to form a covalently-bound biostable layer of the one or more metal alkoxides;
(optionally) removing excess adsorbed metal alkoxide; and
hydrolyzing the covalently-bound surface of the biostable layer.
12. The stent of claim 1, wherein the biostable layer is a monolayer.
13. The stent of claim 1, comprising one or more monolayers of a metal oxide, an organic material, a polymeric material or a biological material.
14. The stent of claim 1, further comprising at least one therapeutic agent.
15. The stent of claim 14, wherein the therapeutic agent is paclitaxel.
16. A method comprising implanting the stent of claim 1 in a body passageway to stimulate the attachment of endothelial cells to the stent or control the erosion rate of the underlying structure.
17. The method of claim 16, wherein at least a portion of the stent degrades over a period of time inside the organism and releases a therapeutic agent.
18. The method of claim 16, wherein the stent is implanted in a cardiovascular passageway.
19. A stent comprising a biostable layer and a bioerodible underlying structure, wherein the biostable layer is about 5% or less of a wall thickness of a strut of the stent, wherein the bioerodible underlying structure comprises a bioerodible metal, wherein the biostable layer comprises one or more of titanium oxide, ruthenium oxide, or iridium oxide.
20. A stent comprising a biostable layer and a bioerodible underlying structure, wherein the biostable layer is about 5% or less of a wall thickness of a strut of the stent, wherein the biostable layer comprises a plurality of nodules about 15-20 nm in size.
21. The stent of claim 1, wherein the bioerodible underlying structure comprises magnesium or an alloy thereof. Description
This application claims priority under 35 USC �119(e) to U.S. Provisional Patent Application Ser. No. 60/845,135, filed on Sep. 15, 2006, the entire contents of which are hereby incorporated by reference.
This invention relates to medical devices, such as endoprostheses, and methods of making and using the same.
In one aspect, the invention features an endoprosthesis, e.g., a stent, having a biostable layer and a bioerodible underlying structure, wherein the biostable layer is about 5% or less of the wall thickness.
In another aspect, the invention features a method of making an endoprosthesis, e.g., stent, having a biostable layer and an underlying structure.
In yet another aspect, the invention features a method that includes implanting an endoprosthesis, e.g., stent, having a biostable layer and an underlying structure in a body passageway to stimulate the attachment of endothelial cells to the stent or control the erosion rate of the underlying structure.
Embodiments may include one or more of the following features. The biostable layer of the endoprosthesis, e.g., stent, has one or more of the following characteristics: a thickness on average of about 10 to 20 nm; an average volume in the range of about 5,000 to 20,000 cubic micrometer per square millimeter of stent surface area; includes ceramic material; includes one or more metal oxides; includes one or more of titanium oxide, ruthenium oxide, or iridium oxide; includes a crystalline form of titanium oxide; includes a plurality of nodules about 15-20 nm in size; is on a surface of the stent, e.g., an interior surface, an exterior surface or a sidewall, of the stent; is covered, in full or in part, by a bioerodible layer; and/or is a monolayer. In embodiments, the bioerodible underlying structure includes one or more bioerodible materials chosen from one or more of a bioerodible metal, a bioerodible metal alloy or a bioerodible non-metal.
In embodiments, the endoprosthesis, e.g., stent, includes: one or more monolayers of a metal oxide, an organic material, a polymeric material or a biological material; and/or further includes at least one therapeutic agent, e.g., paclitaxel.
Further embodiments may include one or more of the following features. The biostable layer is formed by a sol-gel process. In embodiments, the process of making the biostable layer includes: modifying a selected portion of the surface of the underlying structure with hydroxyl groups; allowing the hydroxyl groups to react with one or more metal alkoxides to form a covalently-bound biostable layer of the one or more metal alkoxides; (optionally) removing excess adsorbed metal alkoxide; and hydrolyzing the covalently-bound surface of the biostable layer. In embodiments, the process of making endoprosthesis, e.g., stent, having a biostable layer and a bioerodible structure includes: applying the biostable layer on a surface of a substantially tubular polymer; exposing the biostable layer to temperature sufficiently elevated to remove the tubular polymer without substantially affecting the biostable layer; and applying a bioerodible polymer to the biostable layer. In embodiments, the process further includes applying a bioerodible polymer layer onto at least a portion of the biostable layer.
Further embodiments may include one or more of the following features: at least a portion of the stent degrades over a period of time inside the organism and releases the therapeutic agent; and/or the stent is implanted in a cardiovascular passageway.
Aspects and/or embodiments may have one or more of the following additional advantages. The presence of a biostable layer in a bioerodible medical device offers several advantages including one or more of: providing a firm substrate to an otherwise eroding structure, thus facilitating endothelial cell growth and/or attachment while retaining sufficient flexibility to facilitate stent delivery and deployment; providing a biostable layer that offers increased flexibility for tailoring a stent surface (e.g., tailoring one or more of: texture, thickness, functional group attachment and/or formation of molecule-sized cavities upon removal of organic templates or “molecular imprinting”); and/or controlling erosion (e.g., bioerosion) of the endoprosthesis by protecting the underlying structure from corrosion. By placing one or more biostable layers at predetermined locations, the rate of erosion of different portions of the endoprosthesis can be controlled. Release of a therapeutic agent from the endoprosthesis can be controlled as the rate of erosion is controlled. Moreover, the visibility of the endoprosthesis, e.g., biodegradable endoprosthesis, to imaging methods, e.g., X-ray and/or Magnetic Resonance Imaging (MRI), can be enhanced, even after the endoprosthesis is partly eroded, by e.g., incorporating a radiopaque material into the biostable layer.
FIGS. 1A-1B are a perspective view and a cross-sectional view through the stent wall, respectively, of a stent.
FIGS. 2A-2D are longitudinal cross-sectional views, illustrating delivery of a stent in a collapsed state (FIG. 2A), expansion of the stent (FIG. 2B), deployment of the stent (FIG. 2C), and degradation of the stent (FIG. 2D).
FIGS. 3A-3B are cross-sectional views of a stent wall before and after erosion of an erodible layer, respectively.
FIGS. 4A-4B are a perspective view and a cross-sectional view, respectively, of a textured stent.
FIG. 5 is a scanning electron microscopy (SEM) micrograph of an exemplary textured stent.
FIG. 6 is a general scheme of the surface sol-gel process.
FIGS. 7A-7F are perspective and cross-sectional views of a process for making the stent having a biostable and a bioerodible underlying structure.
Referring to FIGS. 1A-1B, the stent 10 is generally a tubular device defined by a stent wall 21 including fenestrations 22 separated by struts 23. Referring as well to FIG. 1B, a cross-section through the stent wall, a thin continuous biostable layer 11 is provided on the outside of an erodible layer 25. In this embodiment, the bioerodible layer is eroded by exposure to bodily fluid from the interior of the stent, while the biostable layer provides a firm structure to enhance endothelization and reduce dislodgement of fragments of the bioerodible layer. Referring to FIGS. 2A-2D, in use, stent 10 is placed over a balloon 15 carried near the distal end of a catheter 14, and is directed through a lumen 16 (FIG. 2A) until the portion carrying the balloon and stent reaches the region of an occlusion 18. The stent 10 is then radially expanded by inflating the balloon 15 and pressed against the vessel wall with the result that occlusion 18 is compressed (FIG. 2B). The vessel wall surrounding the stent 10 undergoes a radial expansion (FIG. 2B). The pressure is then released from the balloon 15, and the catheter 14 is withdrawn from the vessel (FIG. 2C). Over time, the underlying structure 25 of the stent 10 erodes in the body, sometimes creating fragments 19. The biostable layer 11 remains leaving a firm structure for endothelization from the lumen wall which envelopes the stent and, to some extent, reducing erosion and/or dislodgement of the fragments (FIG. 2D).
Referring to FIGS. 3A and 3B, in another embodiment, stent 30 having a non-continuous biostable layer 31 on top of a bioerodible underlying structure 35 is illustrated before and after exposure to external fluids, respectively. The non-continuous layer 31 defines a window 32 through which the bioerodible structure is exposed to the body from the exterior of the stent. Prior to exposure to the bodily fluids, the bioerodible underlying structure 35 is substantially intact (FIG. 3A). Over time, portion(s) of the underlying structure 35 exposed to external fluids erode at a faster rate than the corresponding areas covered by the biostable layer 31, thus creating a differentially fragmented stent structure (FIG. 3B).
The underlying stent structure can include one or more bioerodible materials chosen from, e.g., a bioerodible metal, a bioerodible metal alloy, or a bioerodible non-metal. In particular embodiments, the stent structure has an overall thickness, stiffness and other mechanical properties sufficient to maintain the patency of the occluded region of a lumen after an angioplasty procedure. As the erodible structure degrades over time, the wall thickness is reduced and the flexibility of the stent is increased. Endothelization of the erodible structure may be typically inhibited by the continuous erosion. The biostable layer provides a non-eroding surface on which cell growth can occur. The biostable layer is sufficiently flexible, e.g., because of its thinness, so that it does not substantially inhibit the mechanical properties of the stent needed for delivery and deployment or inhibit the natural motion of the blood vessel. The biostable layer can also be textured to enhance endothelization. The biostable layer can be provided, and textured morphologies can be formed, by low temperature processes, such as sol-gel processes.
In particular embodiments, the biostable material is a ceramic and the bioerodible material is a polymer. The biostable layer typically makes up about 50%, 20%, 10% or less of the wall thickness of the stent at implantation, e.g., about 5%, 1%, 0.5%, or 0.05% or less of the wall thickness of the stent at implantation. Typically, the relative thinness of the biostable layer is adjusted such that the stent retains the flexibility needed for stent delivery and deployment. The stent typically retains at least about 50%, 75%, 90% or more of the flexibility of a stent otherwise identical but without the biostable layer. The flexibility of the stent can be measured by techniques known in the art. For example, the stent can be expanded into a silicon rubber test tube with similar mechanical properties as a blood vessel. After expansion, the change in flexibility of the stented vessel area can be measured by bending the vessel in a three-point bend test. The three-point bend test is known in the art as a way of evaluating stent stiffness (or its reciprocal, flexibility). It typically involves determining the slope of a force-displacement curve by measuring the stent deflection when the sent is secured by two end-points at a predetermined distance apart, e.g., 20 mm apart, and applying a vertical force or traction midway between the two secured end-points (e.g., applying a force to a hook suspended by an Instron), which provides the third point of the three-point bend test. The three-point bend test is described further in Ormiston, J. et al. (2000) Catherization and Cardiovascular Interventions 50:120-124. Alternatively, the bending of the stent on the balloon catheter can be measured, e.g., by performing a track test. Track testing is known in the art, and is described, for example, in paragraphs 47-53 of U.S. 2004-0210211.
Examples of ceramics include metal oxides, e.g., oxides that include one or more of titanium oxide, ruthenium oxide or iridium oxide. For example, one or more layers of titanium oxide can be used because of its good biocompatibility and induction of endothelization. Titanium oxide can be used in crystalline or amorphous form. Crystalline forms can enhance attachment and/or growth of endothelial cells. Titanium oxides are discussed further in Chen, J. Y., Wan, G. J. (2004) Surface & Coating Technology 186:270-276. The thickness of the biostable layer can vary as needed, but is typically substantially thin to provide a flexible stent structure to facilitate, e.g., stent deployment, while providing a substantially firm substrate to facilitate endothelization. Typically, the biostable layer 11 has a thickness in the range of less than 1000 nm, typically less than 100 nm microns, and about 1 to 50 nm, more typically, about 10 to 20 nm. The biostable layer can have a volume an average volume in the range of about 2,000 to 30,000, more typically 5,000 to 20,000 cubic micrometer per square millimeter of stent surface area. The volume can be measured, e.g., indirectly by statistically making a line measurement along the stent surface using, for example, atomic force microscopy (AFM), or focused ion beam to produce cross-sections along lines. Alternatively, field emission scanning electron microscopy (FSEM) can be used to examine the surface topology and/or the percentage of the stent surface that is covered with the biostable layer. The biostable layer 11 can extend over an entire surface of the stent 10 (e.g., an inner or outer surface, or a side wall, or any combination thereof), or can cover a portion of the stent (e.g., 25%, 50%, 75% of the length of the stent surface).
The biostable layer can coat one or more of the interior or exterior stent surfaces and/or sidewalls, leaving the abluminal surface exposed. In embodiments, the interior surface is coated. Selected portions of the biostable layer can be removed as desired using, for example, a laser to control the rate and/or location of erosion. The stent can have one, two or more layers of biostable materials as desired. In other embodiments, one or more layers of biostable materials can be embedded with one or more bioerodible materials (e.g., organic, polymeric, biological or metallic materials), thus forming a multi-layered hybrid structure.
The biostable layer offers additional advantages, such as allowing tailoring of the stent surface (e.g., tailoring of one or more of: texture, thickness, functional group attachment and/or molecular imprinting by forming molecule-sized cavities upon removal of organic templates). Referring to FIGS. 4A-4B, a perspective view of a stent 40 having a textured surface 41, and a cross-sectional view of the region A in FIG. 4A, respectively, the biostable layer 45 can have a texture (also referred to herein as “nanotexture”) characterized by a plurality of nodules 44 that facilitates endothelial cell migration and/or attachment. Referring to FIG. 5, a scanning electron microscopy (SEM) micrograph of an exemplary high magnification top view of a textured surface titania layer shows a spherical grain morphology of a plurality of nodules about 15-20 nm in size (scale bar in FIG. 5 corresponds to about 70 nm). Surface morphologies of ceramic layers are described further in Daoud, W. et al. (2005) Journal of Non-Crystalline Solids 351:1486-1490. The nodule diameter is typically less than 100 nm, e.g., less than 50 nm, typically about 5 to 30 nm, more typically about 10 to 20 nm. The texture defines spaces between the nodules of about 50 to 500 nm, e.g., around 200 nm, or about the size of a typical endothelial cell. Textured coatings enhance growth and migration of both smooth muscle and endothelial cells. In order to reduce smooth muscle coverage, the textured biostable layer can include a drug that preferentially inhibits smooth muscle cell growth, e.g., paclitaxel, thereby maximizing endothelial cell coverage of the stent.
The biostable layer can be formed by sol-gel processes. Sol-gel processes, in particular, low temperature sol-gel process, are useful for creating a crystalline metal oxide coating on a polymeric substrate (Daoud, W. et al. (2005) supra; Yun, Y-J et al. (2004) Materials Letters 58:3703-3706; Nishio, K. et al. (1999) Thin Solid Films 350:96-100; Wu, L. et al. (2005) Journal of Solid State Chemistry 178:321-328). In embodiments, the metal oxide is applied to the polymer. In other embodiments, the polymer is applied to the metal oxide. Sol gel processes can form thin coatings, without excessive heating which could destroy the polymer or other substrates. For example, crystalline titanium dioxide (TiO2) thin films can be deposited onto an erodible stent at low temperatures using a sol-gel dip-coating method. The titania sol can be prepared, for example, at room temperature by mixing titanium tetraisopropoxide (TTIP) in acidic aqueous solutions and subsequently refluxed at 80� C. for 8 hours to facilitate the formation of anatase crystallites. The deposited titanium oxide films can be heated at 115� C. Homogeneous surfaces of spheroids typically about 20-60 nm in size can be formed. One or more biostable layers of iridium oxide can be prepared by, e.g., a sol-gel dip-coating process where iridium chloride is used as the starting material. The coating solution can also be prepared by reacting iridium chloride, ethanol and acetic acid as described in Nishio, K. et al. (1999) supra. Sol-solvothermal processes can be used to form mesoporous nanocrystalline titanium dioxide with photocatlytic activity as described in Wu et al. (2005) supra. In embodiments, the deposition of the biostable layers is carried out at room temperature.
A surface sol-gel process involving a layer-by-layer approach can be used to add one or more monolayers of metal oxides, organic, polymeric, and/or biological materials (e.g., peptides such as RGD peptides to promote endothelial cell binding) (see e.g., Kunitake, T., Lee, S-W. (2004) Analytica Chimica Acta 504:1-6).
Referring to FIG. 6, a general scheme of surface sol-gel process shows a solid substrate with hydroxyl groups on its surface, which is allowed to react with metal alkoxides in solution to form a covalently-bound surface monolayer of the metal alkoxide. The excessively adsorbed alkoxide can be removed by rinsing. The chemisorbed alkoxide monolayer is then hydrolyzed to give a new hydroxylated surface. The thickness of the metal oxide layer can be as thin as about 1 nm. In embodiments, the polyhydroxyl compounds adsorbed on the surface provide free hydroxyl groups, and metal alkoxides are subsequently adsorbed. The process can be repeated as desired to form one or more multilayers of the same or different materials, e.g., other metal oxides, organic materials (e.g., functional groups), polymeric materials, and/or biological materials (e.g., peptides). The biostable layer can be derivatized as desired by altering the compositions of the layers, thus creating functionalized groups and/or selective molecular imprinting sites. For example, organic polyhydroxyl compounds (e.g., carboxylic acids) can be readily incorporated onto a surface of a metal oxide layer. Upon removal of the organic template, molecule-sized cavities are formed imprinting a cavity that reflects the structural and enantioselective features of the template. The biostable layer can be derivatized further, e.g., to include biodegradable polymers to create surface features that enhance endothelial cell function. For example, biodegradable polymers, such as polylactic acid and/or polyglycolic acid (e.g., poly(lactic-co-glycolic acid) (PLGA)) can be used as scaffolds to support endothelial cell attachment. Suitable techniques are described in Miller, D. C. et al. (2004) Biomaterials 25:53-61. Since the attachment of both smooth muscle and endothelial cells is typically increased using PLGA, the polymer may optionally include an inhibitor of smooth muscle cells, such as paclitaxel.
The biostable layer can be applied to the stent before or after adding the bioerodible structure. For example, the biostable layer can be applied to the stent prior to forming the bioerodible structure. In those embodiments, the biostable layer(s) (e.g., ceramic layer) can be exposed to high temperatures before it is connected to the bioerodible structure.
Referring to FIGS. 7A-7F, perspective and cross-sectional views of the stent undergoing coating steps 7A-7E (upper and lower panels, respectively), starting from step 7A, a solid polymer of tubular shape 50 (e.g., a tube made of nylon, poly(ethylene oxide), polyimine (PI)) having a substantially smooth surface is shown. Referring to FIG. 7B, a stent pattern 54 can be formed on the polymer tube 50, e.g., by writing the stent shape on the polymer tube 50 using an ink pen containing a thick sol-gel solution. In other embodiments, a metallic solution can be used to write a metallic layer on the polymer tube. Ink pens are commercially available from Ohm Craft, Honeoye Falls, N.Y. under the registered mark MicroPen�. Referring back to FIG. 7B and FIG. 7C, by applying heating conditions according to ceramic specifications, a titanium oxide coating is converted into an anatase state (e.g., by heating the polymer to about 500� C. for about 6 hours) and the polymer tube is eliminated, thereby resulting in a very thin biostable (e.g., ceramic) film 56 in the shape of the stent. The biostable film 56 can then be fitted inside a cylindrical tube (not shown) with an inner diameter the size of the desired inner diameter of the final stent and an outer diameter slightly larger than the biostable (e.g., ceramic) film 56. Referring to FIG. 7D, a bioerodible polymer is deposited within the cylindrical tube, resulting in a bioerodible tube 58 with a biostable (e.g., ceramic) layer 56 having a stent shape embedded within. Portions of the bioerodible tube 58 can be selectively removed, e.g., using an excimer laser to ablate the polymer, thereby forming a coated ceramic film 60 (i.e., a ceramic film 56 coated with a biodegradable layer 58). Referring back to FIG. 7D, the removal can be done, for example, by aiming the laser radially to the bioerodible tube 58 and focusing the laser in a number steps to the whole cylinder at a fluence level which is high enough to ablate the polymer, but lower than the ablation threshold of the biostable, e.g., ceramic, film 56. The biodegradable polymer 58 adjacent to the biostable, e.g., ceramic, film 56 will remain substantially intact as it is in the shadow of the biostable, e.g., ceramic, film. Referring to FIG. 7E, the polymer in between can be ablated, thus resulting in a stent 60 made of a biodegradable polymer 58 with a biostable, e.g., ceramic, outer film 56. Referring to FIG. 7F, further embodiments (optionally) include applying (e.g., spraying) to the stent 60 of FIG. 7E, one or more layers of a bioerodible polymer (e.g., the same or different bioerodible polymer as the one used to form the bioerodible tube 58), such that the biostable (e.g., ceramic) film 56 is embedded (fully or a portion thereof) within a thin bioerodible polymeric film 58. In the embodiment shown in FIG. 7F, the same bioerodible polymer is applied to the stent 60 as the one used in FIGS. 7D-7E. The bioerodible polymer is expected to degrade in the body at a fast rate, however it is expected to reduce the propensity of the biostable ceramic layer to break off after expansion.
Referring back to FIG. 7A-7F, the biostable, e.g., ceramic, layer can be further altered to enhance the bond between the bioerodible and the biostable layers. In embodiments, a plurality of indentations or markings can be formed on stent pattern 54, using, for example, an excimer laser. Such indentations or markings will create pitts on the inside of the ceramic shape once the firing has taken place, thus enhancing the bond between the biodegradable polymer and the biostable, e.g., ceramic, layer.
In embodiments, the biostable layer can be used for corrosion protection when the bioerodible underlying structure of the stent is a bioerodible metal, such as magnesium, iron, and nickel (Cheng, F. T. et al. (2004) Scripta Materilia 51:1041-1045; Atik, M. et al. (1995) Ceramics International 21:403-406). Other coatings that can be used to form thin layers by sol-gel for corrosion protection include zirconium dioxide (ZrO2), binary compositions of titanium dioxide and silicon dioxide (TiO2—SiO2), and aluminium oxide and silicon dioxide (Al2O3—SiO2) (Atik, M. et al. (1995) supra).
The stent may additionally include one or more biostable materials in addition to one or more biostable layer described above. Examples of biostable materials include stainless steel, tantalum, niobium, platinum, nickel-chrome, cobalt-chromium alloys such as Elgiloy� and Phynox�, Nitinol (e.g., 55% nickel, 45% titanium), and other alloys based on titanium, including nickel titanium alloys, thermo-memory alloy materials. Stents including biostable and bioerodible regions are described, for example, in US 2006-0122694, entitled “Medical Devices and Methods of Making the Same.” The material can be suitable for use in, for example, a balloon-expandable stent, a self-expandable stent, or a combination of both (see e.g., U.S. Pat. No. 5,366,504). The components of the medical device can be manufactured, or can be obtained commercially. Methods of making medical devices such as stents are described in, for example, U.S. Pat. No. 5,780,807, and U.S. Patent Application Publication No. 2004-0000046-A1, both of which are incorporated herein by reference. Stents are also available, for example, from Boston Scientific Corporation, Natick, Mass., USA, and Maple Grove, Minn., USA.
Bioerodible materials are described, for example, in U.S. Pat. No. 6,287,332 to Bolz; U.S. Patent Application Publication No. US 2002/0004060 A1 to Heublein; U.S. Pat. Nos. 5,587,507 and 6,475,477 to Kohn et al., the entire contents of each of which is hereby incorporated by reference. Examples of bioerodible metals include alkali metals, alkaline earth metals (e.g., magnesium), iron, zinc, and aluminum. Examples of bioerodible metal alloys include alkali metal alloys, alkaline earth metal alloys (e.g., magnesium alloys), iron alloys (e.g., alloys including iron and up to seven percent carbon), zinc alloys, and aluminum alloys. Examples of bioerodible non-metals include bioerodible polymers, such as, e.g., polyanhydrides, polyorthoesters, polylactides, polyglycolides, polysiloxanes, cellulose derivatives and blends or copolymers of any of these. Bioerodible polymers are disclosed in U.S. Published Patent Application No. 2005/0010275, filed Oct. 10, 2003; U.S. Published Patent Application No. 2005/0216074, filed Oct. 5, 2004; and U.S. Pat. No. 6,720,402, the entire contents of each of which is incorporated by reference herein.
The endoprosthesis, e.g., the stent, can, further include at least one therapeutic agent present in the biostable and/or bioerodible portion of the stent. If the therapeutic agent is found in the bioerodible portion of the stent (e.g., interspersed throughout or localized to a predetermined site), release of the therapeutic agent can be controlled as the bioerodible portion of the stent erodes. The terms “therapeutic agent”, “pharmaceutically active agent”, “pharmaceutically active material”, “pharmaceutically active ingredient”, “drug” and other related terms may be used interchangeably herein and include, but are not limited to, small organic molecules, peptides, oligopeptides, proteins, nucleic acids, oligonucleotides, genetic therapeutic agents, non-genetic therapeutic agents, vectors for delivery of genetic therapeutic agents, cells, and therapeutic agents identified as candidates for vascular treatment regimens, for example, as agents that reduce or inhibit restenosis. By small organic molecule is meant an organic molecule having 50 or fewer carbon atoms, and fewer than 100 non-hydrogen atoms in total.
The therapeutic agent can be chosen from one or more of, e.g., an anti-thrombogenic agent, an anti-proliferative/anti-mitotic agents, an inhibitor of smooth muscle cell proliferation, an antioxidant, an anti-inflammatory agent, an anesthetic agents, an anti-coagulant, an antibiotic, or an agent that stimulates endothelial cell growth and/or attachment. Exemplary therapeutic agents include, e.g., anti-thrombogenic agents (e.g., heparin); anti-proliferative/anti-mitotic agents (e.g., paclitaxel, 5-fluorouracil, cisplatin, vinblastine, vincristine, inhibitors of smooth muscle cell proliferation (e.g., monoclonal antibodies), and thymidine kinase inhibitors); antioxidants; anti-inflammatory agents (e.g., dexamethasone, prednisolone, corticosterone); anesthetic agents (e.g., lidocaine, bupivacaine and ropivacaine); anti-coagulants; antibiotics (e.g., erythromycin, triclosan, cephalosporins, and aminoglycosides); agents that stimulate endothelial cell growth and/or attachment. Therapeutic agents can be nonionic, or they can be anionic and/or cationic in nature. Therapeutic agents can be used singularly, or in combination. Preferred therapeutic agents include inhibitors of restenosis (e.g., paclitaxel), anti-proliferative agents (e.g., cisplatin), and antibiotics (e.g., erythromycin). Additional examples of therapeutic agents are described in U.S. Published Patent Application No. 2005/0216074, the entire disclosure of which is hereby incorporated by reference herein.
To enhance the radiopacity of stent, a radiopaque material, such as gold nanoparticles, can be incorporated into endoprosthesis, e.g., the biostable layer or the stent body. For example, gold nanoparticles can be made positively charged by applying a outer layer of lysine to the nanoparticles, e.g., as described in “DNA Mediated Electrostatic Assembly of Gold Nanoparticles into Linear Arrays by a Simple Dropcoating Procedure” Murali Sastrya and Ashavani Kumar, Applied Physics Letters, Vol. 78, No. 19, 7 May 2001. Other radiopaque materials include, for example, tantalum, platinum, palladium, tungsten, iridium, and their alloys.
Medical devices, in particular endoprostheses, as described above include implantable or insertable medical devices, including catheters (for example, urinary catheters or vascular catheters such as balloon catheters), guide wires, balloons, filters (e.g., vena cava filters), stents of any desired shape and size (including coronary vascular stents, aortic stents, cerebral stents, urology stents such as urethral stents and ureteral stents, biliary stents, tracheal stents, gastrointestinal stents, peripheral vascular stents, neurology stents and esophageal stents), grafts such as stent grafts and vascular grafts, cerebral aneurysm filler coils (including GDC—Guglilmi detachable coils—and metal coils), filters, myocardial plugs, patches, pacemakers and pacemaker leads, heart valves, and biopsy devices. In one embodiment, the medical device includes a catheter having an expandable member, e.g., an inflatable balloon, at its distal end, and a stent or other endoprosthesis (e.g., an endoprosthesis or stent as described herein). The stent is typically an apertured tubular member (e.g., a substantially cylindrical uniform structure or a mesh) that can be assembled about the balloon. The stent typically has an initial diameter for delivery into the body that can be expanded to a larger diameter by inflating the balloon. The medical devices may further include drug delivery medical devices for systemic treatment, or for treatment of any mammalian tissue or organ.
The medical device, e.g., endoprosthesis, can be generally tubular in shape and can be a part of a stent. Simple tubular structures having a single tube, or with complex structures, such as branched tubular structures, can be used. Depending on specific application, stents can have a diameter of between, for example, 1 mm and 46 mm. In certain embodiments, a coronary stent can have an expanded diameter of from about 2 mm to about 6 mm. In some embodiments, a peripheral stent can have an expanded diameter of from about 4 mm to about 24 mm. In certain embodiments, a gastrointestinal and/or urology stent can have an expanded diameter of from about 6 mm to about 30 mm. In some embodiments, a neurology stent can have an expanded diameter of from about 1 mm to about 12 mm. An abdominal aortic aneurysm (AAA) stent and a thoracic aortic aneurysm (TAA) stent can have a diameter from about 20 mm to about 46 mm. Stents can also be preferably bioerodible, such; as a bioerodible abdominal aortic aneurysm (AAA) stent, or a bioerodible vessel graft.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS2950187Sep 5, 1958Aug 23, 1960Other Metals Of The Tohoku UniIron-calcium base alloyUS3560362Aug 1, 1967Feb 2, 1971Japan Atomic Energy Res InstMethod and apparatus for promoting chemical reactions by means of radioactive inert gasesUS3569660Jul 29, 1968Mar 9, 1971Nat Res DevLaser cutting apparatusUS3687135Sep 15, 1969Aug 29, 1972Evgeny Mikhailovich SavitskyMagnesium-base alloy for use in bone surgeryUS3758396Aug 31, 1971Sep 11, 1973Research CorpItion preparation of immobilized enzymemembrane complexes by electrocodeposUS3868578Oct 2, 1972Feb 25, 1975Canadian Patents DevMethod and apparatus for electroanalysisUS3910819Feb 19, 1974Oct 7, 1975California Inst Of TechnTreatment of surfaces to stimulate biological cell adhesion and growthUS3948254Aug 28, 1974Apr 6, 1976Alza CorporationNovel drug delivery deviceUS3952334Nov 29, 1974Apr 27, 1976General Atomic CompanyBiocompatible carbon prosthetic devicesUS3993072Oct 17, 1975Nov 23, 1976Alza CorporationMicroporous drug delivery deviceUS4002877Dec 13, 1974Jan 11, 1977United Technologies CorporationMethod of cutting with laser radiation and liquid coolantUS4101984May 5, 1976Jul 25, 1978Macgregor David CCardiovascular prosthetic devices and implants with porous systemsUS4143661Dec 12, 1977Mar 13, 1979Andros IncorporatedPower supply for body implant and method for operationUS4202055May 12, 1977May 13, 1980Battelle-Institut E.V.Anchorage for highly stressed endoprosthesesUS4237559May 11, 1979Dec 9, 1980General Electric CompanyBone implant embodying a composite high and low density fired ceramic constructionUS4308868May 27, 1980Jan 5, 1982The United States Of America As Represented By The Administrator Of The National Aeronautics And Space AdministrationImplantable electrical deviceUS4334327Dec 21, 1979Jun 15, 1982University Of UtahUreteral prosthesisUS4401546Mar 25, 1982Aug 30, 1983Nihon Shinku Gijutsu Kabushiki KaishaFerromagnetic high speed sputtering apparatusUS4532929Jul 23, 1984Aug 6, 1985Ethicon, Inc.Dry coating of surgical filamentsUS4539061Sep 7, 1983Sep 3, 1985Yeda Research And Development Co., Ltd.Process for the production of built-up films by the stepwise adsorption of individual monolayersUS4542539Jan 31, 1984Sep 24, 1985Artech Corp.Surgical implant having a graded porous coatingUS4585652Nov 19, 1984Apr 29, 1986Regents Of The University Of MinnesotaElectrochemical controlled release drug delivery systemUS4634502Aug 26, 1985Jan 6, 1987The Standard Oil CompanyProcess for the reductive deposition of polyoxometallatesUS4655771Apr 11, 1983Apr 7, 1987Shepherd Patents S.A.Prosthesis comprising an expansible or contractile tubular bodyUS4657544 *Apr 18, 1984Apr 14, 1987Cordis CorporationCardiovascular graft and method of forming sameUS4665896Jul 22, 1985May 19, 1987Novacor Medical CorporationPower supply for body implant and method of useUS4705502Dec 31, 1986Nov 10, 1987The Kendall CompanySuprapubic catheter with dual balloonsUS4713070 *Jan 24, 1986Dec 15, 1987Sumitom Electric Industries, Ltd.Porous structure of polytetrafluoroethylene and process for production thereofUS4725273 *Aug 20, 1986Feb 16, 1988Kanegafuchi Kagaku Kogyo Kabushiki KaishaArtificial vessel having excellent patencyUS4733665Nov 7, 1985Mar 29, 1988Expandable Grafts PartnershipExpandable intraluminal graft, and method and apparatus for implanting an expandable intraluminal graftUS4767418 *Feb 13, 1986Aug 30, 1988California Institute Of TechnologyLuminal surface fabrication for cardiovascular prosthesesUS4784659Mar 3, 1987Nov 15, 1988Intermedicat GmbhVessel and prosthesis impregnated with diisocyanate crosslinked gelatinUS4800882Mar 13, 1987Jan 31, 1989Cook IncorporatedEndovascular stent and delivery systemUS4804382 *May 19, 1987Feb 14, 1989Sulzer Brothers LimitedArtificial vesselUS4886062Oct 19, 1987Dec 12, 1989Medtronic, Inc.Intravascular radially expandable stent and method of implantUS4954126Mar 28, 1989Sep 4, 1990Shepherd Patents S.A.Prosthesis comprising an expansible or contractile tubular bodyUS4976692Sep 25, 1989Dec 11, 1990Travenol Laboratories (Israel) Ltd.Catheter particularly useful for inducing labor and/or for the application of a pharmaceutical substance to the cervix of the uterusUS4994071May 22, 1989Feb 19, 1991Cordis CorporationBifurcating stent apparatus and methodUS5024671Sep 19, 1988Jun 18, 1991Baxter International Inc.Microporous vascular graftUS5059211Jun 25, 1987Oct 22, 1991Duke UniversityAbsorbable vascular stentUS5061275Dec 29, 1989Oct 29, 1991Medinvent S.A.Self-expanding prosthesisUS5061914Jun 27, 1989Oct 29, 1991Tini Alloy CompanyShape-memory alloy micro-actuatorUS5073365Jun 1, 1989Dec 17, 1991Advanced Polymer SystemsClinical and personal care articles enhanced by lubricants and adjuvantsUS5079203May 25, 1990Jan 7, 1992Board Of Trustees Operating Michigan State UniversityPolyoxometalate intercalated layered double hydroxidesUS5091024Jun 27, 1990Feb 25, 1992Carpenter Technology CorporationCorrosion resistant, magnetic alloy articleUS5091205Dec 22, 1989Feb 25, 1992Union Carbide Chemicals & Plastics Technology CorporationHydrophilic lubricious coatingsUS5102403Jun 18, 1990Apr 7, 1992Eckhard AltTherapeutic medical instrument for insertion into bodyUS5120322Jun 13, 1990Jun 9, 1992Lathrotec, Inc.Method and apparatus for treatment of fibrotic lesionsUS5125971Jun 29, 1990Jun 30, 1992Tdk CorporationLiving hard tissue replacement, its preparationUS5147370Jun 12, 1991Sep 15, 1992Mcnamara Thomas ONitinol stent for hollow body conduitsUS5163958Aug 13, 1991Nov 17, 1992Cordis CorporationCarbon coated tubular endoprosthesisUS5195969Apr 26, 1991Mar 23, 1993Boston Scientific CorporationCo-extruded medical balloons and catheter using such balloonsUS5205921Feb 4, 1991Apr 27, 1993Queen's University At KingstonMethod for depositing bioactive coatings on conductive substratesUS5234457Oct 9, 1991Aug 10, 1993Boston Scientific CorporationImpregnated stentUS5236413May 7, 1990Aug 17, 1993Feiring Andrew JMethod and apparatus for inducing the permeation of medication into internal tissueUS5236447 *Jun 28, 1991Aug 17, 1993Nissho CorporationArtificial tubular organUS5270086Jul 9, 1991Dec 14, 1993Schneider (Usa) Inc.Multilayer extrusion of angioplasty balloonsUS5279292Feb 13, 1992Jan 18, 1994Implex GmbhCharging system for implantable hearing aids and tinnitus maskersUS5290585Jun 10, 1992Mar 1, 1994C. R. Bard, Inc.Lubricious hydrogel coatingsUS5292558Aug 8, 1991Mar 8, 1994University Of Texas At Austin, TexasProcess for metal deposition for microelectronic interconnectionsUS5302414May 19, 1990Apr 12, 1994Anatoly Nikiforovich PapyrinGas-dynamic spraying method for applying a coatingUS5304121Nov 22, 1991Apr 19, 1994Boston Scientific CorporationDrug delivery system making use of a hydrogel polymer coatingUS5304195Jan 21, 1993Apr 19, 1994Target Therapeutics, Inc.Detachable pusher-vasoocclusive coil assembly with interlocking couplingUS5306286Feb 1, 1991Apr 26, 1994Duke UniversityAbsorbable stentUS5314453Dec 6, 1991May 24, 1994Spinal Cord SocietyPosition sensitive power transfer antennaUS5322520Nov 12, 1992Jun 21, 1994Implemed, Inc.Iontophoretic structure for medical devicesUS5342348Dec 4, 1992Aug 30, 1994Kaplan Aaron VMethod and device for treating and enlarging body lumensUS5348553Dec 18, 1991Sep 20, 1994Whitney Douglass GMethod for promoting blood vessel healingUS5356433Nov 3, 1993Oct 18, 1994Cordis CorporationBiocompatible metal surfacesUS5360440Mar 9, 1992Nov 1, 1994Boston Scientific CorporationIn situ apparatus for generating an electrical current in a biological environmentUS5366504Jul 13, 1992Nov 22, 1994Boston Scientific CorporationTubular medical prosthesisUS5380298Apr 7, 1993Jan 10, 1995The United States Of America As Represented By The Secretary Of The NavyMedical device with infection preventing featureUS5383935Sep 28, 1993Jan 24, 1995Shirkhanzadeh; MortezaProsthetic implant with self-generated current for early fixation in skeletal boneUS5385776Nov 16, 1992Jan 31, 1995Alliedsignal Inc.Nanocomposites of gamma phase polymers containing inorganic particulate materialUS5397307Dec 7, 1993Mar 14, 1995Schneider (Usa) Inc.Drug delivery PTCA catheter and method for drug deliveryUS5405367Mar 3, 1993Apr 11, 1995Alfred E. Mann Foundation For Scientific ResearchStructure and method of manufacture of an implantable microstimulatorUS5421955Mar 17, 1994Jun 6, 1995Advanced Cardiovascular Systems, Inc.Expandable stents and method for making sameUS5439446Jun 30, 1994Aug 8, 1995Boston Scientific CorporationStent and therapeutic delivery systemUS5443458Dec 3, 1993Aug 22, 1995Advanced Cardiovascular Systems, Inc.Multilayered biodegradable stent and method of manufactureUS5443496Oct 15, 1993Aug 22, 1995Medtronic, Inc.Intravascular radially expandable stentUS5443500 *Apr 8, 1994Aug 22, 1995Advanced Cardiovascular Systems, Inc.Intravascular stentUS5449373Mar 17, 1994Sep 12, 1995Medinol Ltd.Articulated stentUS5449382 *Mar 2, 1994Sep 12, 1995Dayton; Michael P.Minimally invasive bioactivated endoprosthesis for vessel repairUS5458627Jul 15, 1993Oct 17, 1995Electro-Biology, Inc.Electrochemically controlled faradic stimulation of osteogenesisUS5462575Dec 23, 1993Oct 31, 1995Crs Holding, Inc.Co-Cr-Mo powder metallurgy articles and process for their manufactureUS5464450 *Mar 21, 1994Nov 7, 1995Scimed Lifesystems Inc.Biodegradable drug delivery vascular stentUS5464650Apr 26, 1993Nov 7, 1995Medtronic, Inc.Intravascular stent and methodUS5468574May 23, 1994Nov 21, 1995Dais CorporationFuel cell incorporating novel ion-conducting membraneUS5474797Feb 10, 1994Dec 12, 1995Spire CorporationBactericidal coatings for implantsUS5500013Jan 13, 1995Mar 19, 1996Scimed Life Systems, Inc.Biodegradable drug delivery vascular stentUS5514154Jul 28, 1994May 7, 1996Advanced Cardiovascular Systems, Inc.Expandable stentsUS5527337Feb 22, 1994Jun 18, 1996Duke UniversityBioabsorbable stent and method of making the sameUS5536573Jul 6, 1994Jul 16, 1996Massachusetts Institute Of TechnologyMolecular self-assembly of electrically conductive polymersUS5545208 *Dec 21, 1993Aug 13, 1996Medtronic, Inc.Intralumenal drug eluting prosthesisUS5549664 *May 2, 1994Aug 27, 1996Ube Industries, Ltd.Artificial blood vesselUS5551954Oct 12, 1994Sep 3, 1996Scimed Life Systems, Inc.Biodegradable drug delivery vascular stentUS5578075 *Jun 1, 1995Nov 26, 1996Michael Peck DaytonMinimally invasive bioactivated endoprosthesis for vessel repairUS5587200Nov 7, 1995Dec 24, 1996Pacesetter AbMethod for manufacturing a medical electrodeUS5587507Mar 31, 1995Dec 24, 1996Rutgers, The State UniversitySynthesis of tyrosine derived diphenol monomersUS5591222Mar 28, 1994Jan 7, 1997Susawa; TakashiMethod of manufacturing a device to dilate ducts in vivoUS5591224Sep 15, 1994Jan 7, 1997Medtronic, Inc.Bioelastomeric stentUS5599352Sep 15, 1994Feb 4, 1997Medtronic, Inc.Method of making a drug eluting stentUS5603556Nov 20, 1995Feb 18, 1997Technical Services And Marketing, Inc.Rail car load sensorUS5605696Mar 30, 1995Feb 25, 1997Advanced Cardiovascular Systems, Inc.Drug loaded polymeric material and method of manufactureUS5607463 *Mar 30, 1993Mar 4, 1997Medtronic, Inc.Intravascular medical deviceUS5609629Jun 7, 1995Mar 11, 1997Med Institute, Inc.Coated implantable medical deviceUS5614549Jan 30, 1995Mar 25, 1997Enzon, Inc.High molecular weight polymer-based prodrugsUS5624411Jun 7, 1995Apr 29, 1997Medtronic, Inc.Intravascular stent and methodUS5628787Jun 7, 1995May 13, 1997Schneider (Usa) Inc.Clad composite stentUS5629077Jun 27, 1994May 13, 1997Advanced Cardiovascular Systems, Inc.Biodegradable mesh and film stentUS5632771Jan 25, 1995May 27, 1997Cook IncorporatedFlexible stent having a pattern formed from a sheet of materialUS5632840Jun 6, 1995May 27, 1997Advanced Cardiovascular System, Inc.Method of making metal reinforced polymer stentUS5649951 *Jun 6, 1995Jul 22, 1997Smith & Nephew Richards, Inc.Zirconium oxide and zirconium nitride coated stentsUS5690670 *Jun 6, 1995Nov 25, 1997Davidson; James A.Stents of enhanced biocompatibility and hemocompatibilityUS5788626 *Nov 18, 1996Aug 4, 1998Schneider (Usa) IncMethod of making a stent-graft covered with expanded polytetrafluoroethyleneUS5837275 *Jun 2, 1995Nov 17, 1998Westaim Technologies, Inc.Anti-microbial materialsUS5854382 *Aug 18, 1997Dec 29, 1998Meadox Medicals, Inc.Bioresorbable compositions for implantable prosthesesUS5873904 *Feb 24, 1997Feb 23, 1999Cook IncorporatedSilver implantable medical deviceUS5891108 *Sep 12, 1994Apr 6, 1999Cordis CorporationDrug delivery stentUS5958440 *Nov 18, 1993Sep 28, 1999Westaim Technologies, Inc.Anti-microbial materialsUS5980566 *Apr 11, 1998Nov 9, 1999Alt; EckhardVascular and endoluminal stents with iridium oxide coatingUS6013591 *Jan 16, 1998Jan 11, 2000Massachusetts Institute Of TechnologyNanocrystalline apatites and composites, prostheses incorporating them, and method for their productionUS6017553 *Jun 2, 1995Jan 25, 2000Westaim Technologies, Inc.Anti-microbial materialsUS6027742 *Oct 16, 1996Feb 22, 2000Etex CorporationBioresorbable ceramic compositesUS6086773 *May 22, 1998Jul 11, 2000Bmc Industries, Inc.Method and apparatus for etching-manufacture of cylindrical elementsUS6099561 *Oct 20, 1998Aug 8, 2000Inflow Dynamics, Inc.Vascular and endoluminal stents with improved coatingsUS6120535 *Nov 21, 1997Sep 19, 2000Radiance Medical Systems, Inc.Microporous tubular prosthesisUS6132463 *Oct 16, 1996Oct 17, 2000Etex CorporationCell seeding of ceramic compositionsUS6139574 *Aug 20, 1997Oct 31, 2000Children's Medical Center CorporationVascularized tissue regeneration matrices formed by solid free form fabrication techniquesUS6165211 *Dec 11, 1997Dec 26, 2000Schneider (Usa) Inc.Expandable stent-graft covered with expanded polytetrafluoroethyleneUS6217607 *Aug 2, 1999Apr 17, 2001Inflow Dynamics Inc.Premounted stent delivery system for small vesselsUS6240616 *Apr 15, 1997Jun 5, 2001Advanced Cardiovascular Systems, Inc.Method of manufacturing a medicated porous metal prosthesisUS6245104 *Feb 28, 1999Jun 12, 2001Inflow Dynamics Inc.Method of fabricating a biocompatible stentUS6253252 *Jul 11, 1996Jun 26, 2001Andrew SchofieldMethod and apparatus for asynchronously calling and implementing objectsUS6270831 *Apr 30, 1998Aug 7, 2001Medquest Products, Inc.Method and apparatus for providing a conductive, amorphous non-stick coatingUS6331312 *Mar 2, 1998Dec 18, 2001Etex CorporationBioresorbable ceramic compositesUS6335029 *Dec 3, 1998Jan 1, 2002Scimed Life Systems, Inc.Polymeric coatings for controlled delivery of active agentsUS6379382 *Mar 13, 2000Apr 30, 2002Jun YangStent having cover with drug delivery capabilityUS6419692 *Feb 3, 1999Jul 16, 2002Scimed Life Systems, Inc.Surface protection method for stents and balloon catheters for drug deliveryUS6440166 *Feb 16, 2000Aug 27, 2002Omprakash S. KolluriMultilayer and multifunction vascular graftUS6524334 *Apr 21, 2000Feb 25, 2003Schneider (Usa)Expandable stent-graft covered with expanded polytetrafluoroethyleneUS6641607 *Dec 29, 2000Nov 4, 2003Advanced Cardiovascular Systems, Inc.Double tube stentUS6652582 *Oct 8, 1999Nov 25, 2003Boston Scientific Scimed, Inc.Bioabsorbable endoprosthesis having porosity for by-product collectionUS6689160 *May 30, 2000Feb 10, 2004Sumitomo Electric Industries, Ltd.Prosthesis for blood vesselUS6716444 *Sep 28, 2000Apr 6, 2004Advanced Cardiovascular Systems, Inc.Barriers for polymer-coated implantable medical devices and methods for making the sameUS6719987 *Apr 16, 2001Apr 13, 2004Nucryst Pharmaceuticals Corp.Antimicrobial bioabsorbable materialsUS6723350 *Apr 23, 2002Apr 20, 2004Nucryst Pharmaceuticals Corp.Lubricious coatings for substratesUS6805898 *Sep 28, 2000Oct 19, 2004Advanced Cardiovascular Systems, Inc.Surface features of an implantable medical deviceUS6833004 *Jul 5, 2002Dec 21, 2004Terumo Kabushiki KaishaStentUS6849089 *Oct 2, 2002Feb 1, 2005Biotronik Mess-Und Therapiegeraete Gmbh & Co Ingenieurbuero BerlinImplant with proliferation-inhibiting substanceUS6869701 *Aug 16, 1999Mar 22, 2005Carolyn AitaSelf-repairing ceramic coatingsUS6908624 *Dec 16, 2002Jun 21, 2005Advanced Cardiovascular Systems, Inc.Coating for implantable devices and a method of forming the sameUS6918927 *Oct 31, 2001Jul 19, 2005Cook IncorporatedCoated implantable medical deviceUS6921390 *Jul 23, 2001Jul 26, 2005Boston Scientific Scimed, Inc.Long-term indwelling medical devices containing slow-releasing antimicrobial agents and having a surfactant surfaceUS6926735 *Dec 23, 2002Aug 9, 2005Scimed Life Systems, Inc.Multi-lumen vascular grafts having improved self-sealing propertiesUS6972130 *Oct 16, 1997Dec 6, 2005Etex CorporationBioceramic compositionsUS6989156 *Apr 23, 2002Jan 24, 2006Nucryst Pharmaceuticals Corp.Therapeutic treatments using the direct application of antimicrobial metal compositionsUS7022334 *Mar 20, 2002Apr 4, 2006Advanced Cardiovascular Systems, Inc.Therapeutic composition and a method of coating implantable medical devicesUS7048767 *Jun 11, 2002May 23, 2006Spire CorporationNano-crystalline, homo-metallic, protective coatingsUS7060240 *Nov 14, 2003Jun 13, 2006Degussa Novara Technology S.P.A.Sol-gel process for the manufacture of nanocomposite photoluminescent materials and materials thus producedUS7078108 *Jul 14, 2004Jul 18, 2006The Regents Of The University Of CaliforniaPreparation of high-strength nanometer scale twinned coating and foilUS7099091 *Nov 26, 2003Aug 29, 2006Hitachi Displays, Ltd.Display deviceUS7101394 *May 2, 2003Sep 5, 2006Boston Scientific Scimed, Inc.Energetically-controlled delivery of biologically active material from an implanted medical deviceUS7157096 *Oct 14, 2002Jan 2, 2007Inframat CorporationCoatings, coated articles and methods of manufacture thereofUS7160592 *Feb 14, 2003Jan 9, 2007Cv Therapeutics, Inc.Polymer coating for medical devicesUS7244272 *Feb 14, 2005Jul 17, 2007Nicast Ltd.Vascular prosthesis and method for production thereofUS7261735 *Jun 22, 2001Aug 28, 2007Cordis CorporationLocal drug delivery devices and methods for maintaining the drug coatings thereonUS7279175 *Sep 17, 2002Oct 9, 2007Psivida Inc.Stent coated with a sustained-release drug delivery and method for use thereofUS7323189 *Dec 21, 2001Jan 29, 2008Ev3 Peripheral, Inc.Liquid and low melting coatings for stentsUS7344560 *Oct 8, 2004Mar 18, 2008Boston Scientific Scimed, Inc.Medical devices and methods of making the sameUS7432327 *Dec 30, 2004Oct 7, 2008Sabic Innovative Plastics Ip B.V.Transparent polymeric compositions comprising polysiloxane-polycarbonate copolymer, articles made therefrom and methods of making sameUS7498385 *Feb 26, 2007Mar 3, 2009Gore Enterprise HoldingsPolyester compositions, methods of manufacturing said compositions, and articles made therefromUS7507433 *Sep 3, 2004Mar 24, 2009Boston Scientific Scimed, Inc.Method of coating a medical device using an electrowetting processUS7537610 *Jul 7, 2004May 26, 2009Advanced Cardiovascular Systems, Inc.Method and system for creating a textured surface on an implantable medical deviceUS7691401 *May 17, 2005Apr 6, 2010Advanced Cardiovascular Systems, Inc.Poly(butylmethacrylate) and rapamycin coated stentUS7713297 *Aug 29, 2003May 11, 2010Boston Scientific Scimed, Inc.Drug-releasing stent with ceramic-containing layerUS7713573 *Feb 10, 2006May 11, 2010Medtronic Vascular, Inc.Method for loading nanoporous layers with therapeutic agentUS7722805 *Nov 25, 2004May 25, 2010Institute Of Metal Research Chinese Academy Of SciencesTitanium alloy with extra-low modulus and superelasticity and its producing method and processing thereofUS7749264 *Jan 23, 2008Jul 6, 2010Boston Scientific Scimed, Inc.Medical devices and methods of making the sameUS7758635 *Feb 13, 2007Jul 20, 2010Boston Scientific Scimed, Inc.Medical device including cylindrical micellesUS7771773 *May 22, 2006Aug 10, 2010Spire CorporationNano-crystalline, homo-metallic, protective coatingsUS7776926 *Dec 11, 2002Aug 17, 2010Advanced Cardiovascular Systems, Inc.Biocompatible coating for implantable medical devicesUS20020004060 *Jul 17, 1998Jan 10, 2002Bernd HeubleinMetallic implant which is degradable in vivoUS20020138154 *Mar 21, 2001Sep 26, 2002Jianmin LiControlling resorption of bioresorbable medical implant materialUS20030003127 *Jun 27, 2001Jan 2, 2003Ethicon, Inc.Porous ceramic/porous polymer layered scaffolds for the repair and regeneration of tissueUS20030004564 *Mar 11, 2002Jan 2, 2003Elkins Christopher J.Drug delivery platformUS20030118692 *Oct 21, 2002Jun 26, 2003Yadong WangBiodegradable polymerUS20030190406 *Apr 10, 2003Oct 9, 2003Hossainy Syed F. A.Implantable device having substances impregnated therein and a method of impregnating the sameUS20040039438 *Aug 29, 2003Feb 26, 2004Inflow Dynamics, Inc., A Delaware CorporationVascular and endoluminal stents with multi-layer coating including porous radiopaque layerUS20040106975 *Nov 14, 2003Jun 3, 2004Gmp/Cardiac Care, Inc.Rail stentUS20040117008 *Aug 15, 2003Jun 17, 2004Abbott Laboratories Vascular Enterprises Ltd.Medical implants containing FK506 (tacrolimus), methods of making and methods of use thereofUS20040157073 *Feb 5, 2004Aug 12, 2004Nucryst Pharmaceuticals Corp., A Alberta, Canada CorporationLubricious coatings for substratesUS20040182511 *Dec 19, 2003Sep 23, 2004Scimed Life Systems, Inc.Pressure lamination method for forming composite ePTFE/textile and ePTFE/stent/textile prosthesesUS20050033407 *Aug 7, 2003Feb 10, 2005Scimed Life Systems, Inc.Stent designs which enable the visibility of the inside of the stent during MRIUS20050060021 *Sep 16, 2003Mar 17, 2005O'brien BarryMedical devicesUS20050107870 *Aug 20, 2004May 19, 2005Xingwu WangMedical device with multiple coating layersUS20050159805 *Jan 20, 2004Jul 21, 2005Jan WeberFunctional coatings and designs for medical implantsUS20050228483 *Mar 9, 2005Oct 13, 2005Kaplan Aaron VVascular bifurcation prosthesis with multiple thin fronds* Cited by examinerNon-Patent CitationsReference1"Corrosion Theory and Corrosion Protection," EM 1110-2-3400, 1995, 8 pages.2"Galvanic cell" printout from wikipedia, 2 pgs, printed Oct. 28, 2005.3"Galvanic corrosion", http://www.corrosion-doctors.org/Aircraft/galvdefi.htm, 3 pgs., printed Oct. 28, 2005.4"Galvanic series" printout from Wikipedia, p. 1 of 2, printed Oct. 28, 2005.5"Best of the ACC Scientific Session 2002," Rev. Cardiovasc. Med., 2002, 3(2):85-104.6"Galvanic cell" printout from wikipedia, 5 pages, printed on Aug. 16. 2010.7"Galvanicc corrosion," http://www.corrosion-doctors.org/aircraft/galvdefi.htm, 3 pgs., printed Oct. 28, 2005.8Aaltonen, "Atomic Layer Deposition of Noble Metal Thin Films," University of Helsinki, Apr. 8, 2005, pp. 1-71.9Aghion et al., "Newly Developed Magnesium Alloys for Powertrain Applications," JOM, 2003, p. 30.10Aghion et al., "Newly Developed Magnesium Alloys for Powertrain Applications," p. 30 JOM, 2003, p. 30.11Albion Research Notes, Newsletter, Oct. 1994, 3(4): 1-4.12Anand et al., "Ion-exchange resins: carrying drug delivery forward," DDT, 2001, 6: 905-914.13Anderson et al., "A new conductive polymer as a replacement for chrome coatings," 2003 Aerospace Coatings Removel and Coatings Conference,May 20-22, 2003, Colorado Springs, CO, 7 pages.14Andi�n et al., "Corrosion behaviour at the interface of steel bars embedded in cement slurries. Effect of phenol polymer coatings," Corrosion Science, 2002, 44:2805-2816.15Antipov et al., "Polyelectrolyte Multilayer Capsule Permeability Control," Colloids and Surfaces A: Physiochem. Eng. Aspects, 2002, 198-200, 535-541.16Antipov et al., "Polyelectrolyte Multilayer Capsules as Vehicles with Tunable Permeability," Advances in Colloid and Interface Science, 2004, 111:49-61.17Arts et al., "Polyphenols and disease risk in epidemiologic studies," Am. J. Clin. Nutr., 2005, 81:317S-325S.18Artyukhin et al., "Layer-by-Layer Electrostatic Self-Assembly of Polyelectrolyte Nanoshells on Individual Carbon Nanotube Templates," Langmuir, 2004, 20:1442-1448.19Ashtari et al. "An efficient method for recovery of target ssDNA based on amino-modified silica-coated magnetic nanoparticles" Talanta 67. (2005). 548-554.20Atta, "Electrochemical synthesis, characterization and some properties of a polymer derived from thioflavin S.," European Polymer Journal, 2005, 41: 3018-3025.21Australian Government, Department of Health and Aging, "Horizon Scanning Prioritising Summary-Biodegradable stents for coronary artery disease," Horizon Scanning Network (ANZHSN), Aug. 2007, pp. 1-13.22Authorized Officer Antoine Laurent, International Preliminary Report on Patentability in PCT/US09/046750 mailed Dec. 23, 2010, 8 pages.23Authorized Officer Antonio Espuch, International Preliminary Report on Patentability in PCT/US09/49422 mailed Jan. 13, 2011, 7 pages.24Authorized Officer Athina Nickitas-Etienne, International Preliminary Report on Patentability in PCT/US07/78449 mailed Mar. 26, 2009, 9 pages.25Authorized Officer Athina Nickitas-Etienne, International Preliminary Report on Patentability in PCT/US07/79841 mailed Apr. 30, 2009, 7 pages.26Authorized officer Athina Nickitas-Etienne, International Preliminary Report on Patentability in PCT/US08/86639 mailed Jun. 24, 2010, 2 pages.27Authorized Officer Athina Nickitas-Etienne, International Search Report/Written Opinion in PCT/US07/78449, mailed Jan. 13, 2009, 24 pages.28Authorized Officer Aurore Schneider, International Preliminary Report on Patentability from PCT/US2010/042772 mailed Feb. 4, 2011, 9 pages.29Authorized Officer Cecilia Giel-Barragan Ramos, International Search Report/Written in PCT/US07/79841 mailed Feb. 4, 2009, 11 pages.30Authorized Officer Cecilia Giel-Barrag�n Ramos, International Search Report/Written Opinion in PCT/US07/79841 mailed Feb. 4, 2009, 21 pages.31Authorized Officer Elisabeth Reinecke, International Search Report/Written Opinion in PCT/US07/60137 mailed Jul. 27, 2007, 20 pages.32Authorized Officer Henrique Amaro, International Preliminary Report on Patentability from PCT/US09/043326 mailed Nov. 18, 2010, 7 pages.33Authorized Officer Henrique Amaro, International Preliminary Report on Patentability in PCT/US2009/43326 mailed Nov. 18, 2010, 7 pages.34Authorized Officer Jasmine Messemanne, International Preliminary Report on Patentability from PCT/US09/051965 mailed Feb. 10, 2011, 8 pages.35Authorized Officer Jasmine Messemanne, International Search Report from PCT/US09/051965 mailed Aug. 20, 2010, 13 pages.36Authorized Officer Jo�lle Gerber, International Search Report/Written Opinion in PCT/US07/78450 mailed Nov. 19, 2008, 17 pages.37Authorized Officer Jo�lle Gerber, International Search Report/Written Opinion in PCT/US07/88888 mailed Jul. 13, 2009, 24 pages.38Authorized Officer Mary Celine, International Search Report from PCT/US2010/060412 mailed Feb. 21, 2011, 10 pages.39Authorized Officer Nora Lindner, International Preliminary Report on Patentability in PCT/US07/88888 mailed Jul. 30, 2009, 11 pages.40Authorized Officer Razik Menidjel, International Preliminary Report on Patentability from PCT/US09/059424, mailed May 5, 2011, 8 pages.41Authorized Officer Simin Baharlou, International Preliminary Report on Patentability in PCT/US07/66568 mailed Oct. 23, 2008, 10 pages.42Authorized Officer Simin Baharlou, International Preliminary Report on Patentability in PCT/US07/75072 mailed Feb. 12, 2009, 9 pages.43Authorized Officer Simin Baharlou, International Preliminary Report on Patentability in PCT/US07/75072 mailed Feb.12, 2009, 9 pages.44Authorized Officer Simin Baharlou, International Search Report/Written Opinion in PCT/US07/66568 mailed Oct. 8, 2007, 11 pages.45Authorized Officer Simin Baharlou, International Search Report/Written Opinion in PCT/US07/75072 mailed Jan. 25, 2008, 21 pages.46Authorized Officer Trudy Hinterwimmer, International Search Report/Written Opinion in PCT/US07/78412 mailed Mar. 3, 2008, 10 pages.47Authorized Officer Trudy Hinterwimmer, International Search Report/Written Opinion in PCT/US09/49422 mailed Aug. 24, 2009, 10 pages.48Authorized Officer V�ronique van Loon-Megard, International Search Report/Written Opinion in PCT/US08/75976 mailed Nov. 25, 2008, 20 pages.49Authorized Officer V�ronique van Loon-M�gard, International Search Report/Written Opinion in PCT/US08/75976 mailed Nov. 25, 2008, 20 pages.50Babapulle and Eisenberg, "Coatred stents for their prevention of restenosis: 2002, 106: 2849-2866 Part II," Circulation, 2002, 106: 2849-2866.51Bach et al., "Corrosion, Protection and Repassivation After the Deformation of Magnesium Alloys Coated With a Protective Magnesium Fluoride Layer," JOM, 2004, p. 343.52Bakkar et al., "Improving corrosion resistance of magnesium-based alloys by surface modification with hydrogen by electrochemical ion reduction (EIR) and by plasma immersion ion implantation (PIII)," Corrosion Science, 2005, 47:1211-1225.53Balasubramanian et al. "Dispersion and Stability Studies of Resorcinarene-Encapsulated Gold Nanoparticles." Langmuir, 2002, 1676-3681.54Bao, Y. et al. "Preparation of functionalized and gold-coated cobalt nanocrystals for biomedical applications." Journal of Magnetism and Magnetic Materials, 2005, 293:15-19.55Baurschmidt et al., "The Electrochemical Aspects of the Thrombogenicity of a Material," J. Bioengineering, 1977, 1:261-278.56Bekesi et al., "Efficient Submircon Processing of Metals with Femto," Appl. Phys. A., Published Oct. 25, 2002, pp. 355-357.57Ben-Hamu et al., "Influence of Si, Ca and Ag addition on corrosion behaviour of new wrought Mg-Zn alloys," Materials Science and Technology, 2006, vol. 22, No. 10, pp. 1213-1218.58Bereket et al., "Electrochemical synthesis and anti-corrosive properties of polyaniline, poly(2-anisidine), and poly (aniline-co-2-anisidine) films on stainless steel," Progress in Organic Coatings, 2005, 54: 63-72.59Berkland et al., "Controlling Surface Nano-structure Using Flow-Limited Field-Injection Electrostatic Spraying (FFESS) of poly(D,L-lactide-co-glycolide)," Biomaterials, 2004, 25:5649-5658.60Bernkop-Schnurch, "Chitosan and its derivatives: potential excipients for peroral peptide delivery systems," International J. Of Pharmaceutics, 2000, 194: 1-13.61Berry et al., "Functionalisation of magnetic nanoparticles for applications in biomedicine," J. Phys. D: Appl. Phys. , 2003, 36:R198-R206.62Berry et al., "Functionalisation of magnetic nanoparticles for applications in biomedicine," J. Phys. D: Appl. Phys., 2003, 36:R198-R206.63Biercuk et al., "Low-temperature atomic-layer-deposition lift-off method for microelectronic and nanoelectronic applications," Applied Physics Letters, vol. 83, No. 12, Sep. 22, 2003, pages.2405-2407.64Blanusa et al., "Chelators as Antidotes of Metal Toxicity Therapeutic and Experimental Aspects," Current Medicinal Chemistry, 2005, vol. 12, pp. 2771-2794.65Bolz et al., "Effect of smooth, porous and fractal surface structure on the properties of an interface," J. Materials Science: Materials in Medicine, 1995, 6:844-848.66Bolz et al., "Effect of smooth, porous and fractal surface structure on the properties of an interface," J. Materials Science: Materials in Medicine, 1995, 844-848.67Bosiers et al., "Absorbable Metal stent for CLI in Infrapopliteal lesions: 1 year results," CX 2005 Global Endovascular Forum, Apr. 2005, pp. 1-23.68Brandau et al., "Nanoporous Ceramic Coatings for Synthesis of Radioactive Implants," Journal of Nuclear Medicine Abstract Book, Jun. 7, 2000, p. 244P, Abstract No. 1076.69Br�ckner et al., "Metal plasma immersion ion implantation and deposition (MPIIID): chromium on magnesium," Surface and Coatings Technology, 1998, 103-104, pp. 227-230.70Br�ckner et al., "Metal plasma immersion ion implantation and deposition (MPIID): chromium on magnesium," Surface and Coatings Technology, 1998, 103-104, pp. 227-230.71Brunatto and Muzart, "Influence of the gas mixture flow on the processing parameters of hollow cathode discharge ion sintering," J. Phys. D.: Appl. Phys., 2007, 40: 3937-3944.72Brunner et al., "Porosity Tailored Growth of Black Anodic Layers on Magnesium in an Organic Electrolyte," Journal of the Electrochemical Society, vol. 156 (2), Dec. 12, 2008, pp. C62-C66.73Buescher et al., "Characterization of Wet-Chemically Nanostructured Stainless Steel Surfaces," Mat. Res. Soc. Symp. Proc., 2001, 676:1-6.74Caruso et al., "Ultrathin Molybdenum Polyoxometalate-Polyelectrolyte Multilayer Films," Langmuir, 1998,14:3462-3465.75Caruso et al., "Ultrathin Molybdenum Polyoxometalate-Polyelectrolyte Multilayer Films," Langmuir, 1998, 14:3462-3465.76Casan-Pastor et al., "Polyoxometalates: From Inorganic Chemistry to Materials Science," Frontiers in Bioscience, 2004, 9:1759-1770.77Chaieb et al , "Inhibition of the corrosion of steel in 1 M HC1 by eugenol derivatives," Applied Surface Science, 2005, 246:199-206.78Chaieb et al , "Inhibition of the corrosion of steel in 1 M HC1 by eugenol derivaives," Applied Surface Science, 2005, 246:199-206.79Chang et al., "Effect of Heat Treatment on Corrosion and Electrochemical behavior of Mg-3Nd-0.2Zn-0.4Zr (wt. %) alloy," Science Direct, Electrochimica Acta 52, 2007, 3160-3167.80Chang et al., "Templated sythesis of Gold-iron Alloy nanoparticles using pulsed laser deposition," Nanotechnology, vol. 17, 2006, pp. 5131-5135.81Changwen et al., "Polyoxometalate-based organic-inorganic hybrid materials"; http://www.solgel.com/articles/oct01/changwen.asp, Retrieved from the Internet on Nov. 1, 2004 (17 pages).82Changwen et al., "Polyoxometalate-based organic-inorganic hybrid materials," 2004, Sol-Gel, pg 1.83Chen et al., "Laser Cladding of Mg20A18o Powder on ZM5 Magnesium Alloy," Corrosion Engineering, Science and Technology, 2007, vol. 42, No. 2, pp. 130-136.84Cheng et al., "Electrogeneration and electrochemical properties of hybrid materials: polypyrrole doped with polyoxometalates PW12-xMoxM40 3-(x=0,3,6,12)," Synthetic Metals, 2002, 129: 53-59.85Cho et al., "Gold-coated iron nanoparticles: a novel magnetic resonance agent for T1 and T2 weighted imaging," Nanotechnology, vol. 17, 2006, pp. 640-644.86Chou et al., "Electrochemical treatment of mouse and rat fibrosarcomas with direct current," Bioelectromagnetics, 1997, 18:14-24.87Clemente-Leon et al., "Hybrid Langmuir-Blodgett Films Formed by Alternating Layers of Magnetic Polyoxometalate Clusters and Organic Donor Molecules-Towards the Preparation of Multifunctional Molecular Materials," Adv. Mater., 2001, 13:574-577.88Clemente-Leon et al., "Hybrid Langmuir-Blodgett Films Formed by Alternating Layers of Magnetic Polyoxometalate Clusters and Organic Donor Molecules—Towards the Preparation of Multifunctional Molecular Materials," Adv. Mater., 2001, 13:574-577.89Cogger et al. "An Introduction to Electrochemical Impedance Measurement," Solartron Analytical, 1999, 2-14.90Conolly et al., "X-Ray microtomography studies of localized corrosion and transitions to stress corrosion cracking," Materials Science and Technology, 2006, vol. 22, No. 9, pp. 1076-1085.91Costa et al., "The effect of the magnetic field on the corrosion behavior of Nd-Fe-B permanent magnets." Journal of Magnetism and Magnetic Material, 278, 2004, pp. 348-358.92Damen et al., "Paclitaxel esters of malic acid as prodrugs with improved water solubility," Bioorganic & Medicinal Chemistry, 2000, 8: 427-432.93Damiani et al., "Vasorelaxant effects on eugenol on rat thoracic aorta," Vascular Pharmacol., 2003, 40:59-66.94Davies, "Changing the salt, changing the drug," The Pharmaceutical Journal, 2001, 266: 322-323.95De Geest et al., "Self-rupturing Microcapsules," Adv. Mater., 2005, vol. 17, pp. 2357-2361.96de Witte, "Analysis of the principal component of external casing corrosion in deep wells," J. Appl. Electrochem., 1985, 15: 325-334.97Dexter, "Galvanic Corrosion," MAS Note, University of Delaware Sea Grant Marine Advisory Service, 2003.98Di Mario et al. "MOONLIGHT: a controlled registry of an iridium-oxide coated stent with angiographic follow up" International Journal of Cardiology. 2004 (95) 329-331.99Di Mario et al., "Drug-eluting bioabsorbable magnesium stent," J. Interventional Cardiol., 2004, 17(6): 391-395.100Dowling et al., "Anti-bacterial silver coatings exhibiting enhanced activity through the addition of Platinum," Surf. & Coatings Tech., 2003, 163-164:637-640.101Dumas et al., "Characterization of magnesium fluoride thin films produced by argon ion beam-assisted deposition," Thin Solid Films, 2001, pp. 61-68.102Duncan et al., "Polymer-drug conjugates, PDEPY and PELT: basic principles for design and transfer from the laboratory to clinic," Journal of Controlled Release, 2001, 74: 135-146.103Duncan, "The dawning era of polymer 360 therapeutics," Nature Reviews/Drug Discovery, 2003, 2: 347-360.104Duygu, "Controlled Release Systems," http://www.biomed.metu.edu.tr/courses/term-papers/contr-rel-sys-duygu.htp (Dec. 30, 2005).105Duygu, "Controlled Release Systems," http://www.biomed.metu.edu.tr/courses/term—papers/contr-rel-sys—duygu.htm (Dec. 30, 2005).106Duygu, "Controlled Release Systems," http://www.biomed.metu.edu.tr/courses/term—papers/contr-rel-sys—duygu.htp (Dec. 30, 2005).107Eggebrecht et al., "Novel Magnetic Resonance-Compatible Coronary Stent: The Absorbable Magnesium-Alloy Stent," Circulation, 2005, 112: 303-304.108Eniola and Hammer, "Characterization of biodegradable drug delivery vehicles with the adhesive properties of leukocytes II: effect of degradation on targeting activity," Biomaterials, 2005, 26:661-670.109Eniola et al., "Characterization of Biodegradable Drug Delivery Vehicles with the Adhesive Properties of Leukocytes II: Effect of Degradation on Targeting Activity," Biomaterials, 2005, 26:661-670.110Erbel et al., "Absorbierbare Stents-Eine Vielversprechende Neuerung?" Urban & Vogel, No. 4, 2007, pp. 308-319.111Erbel et al., "Temporary scaffolding of coronary arteries with bioabsorbable magnesium stents: a prospective, non-randomised multicentre trial," Lancet, 2007, vol. 369, pp. 1869-1875.112Erne et al., "The Road to Bioabsorbable Stents: Reaching Clinical Reality?" Cardio Vascular and Interventional Radiology, Sep. 26, 2005, pp. 11-16.113European Search Report from EP 10159664.1, mailed Jun. 4, 2010, 3 pages.114Falotico, "Cordis Fully Bioabsorbable Stent Program," Euro PCR09, May 22, 2009, pp. 1-21.115Fan et al., "Influence of Lanthanum on the microstructure, mechanical property and corrosion resistance of magnesium alloy," J. Mater Sci, 2006, vol. 41, pp. 5409-5416.116Farhat et al., "Corrosion Control Using Polyelectrolyte Multilayers," Electrochemical and Solid State Letters, 2002, 5(4):B13-B15.117Feng et al., "Sonochemical preparation of photochromic nanocomposite thin film based on polyoxometalates well dispersed in polyacrylamide," Journal of Solid State Chemistry, 2002, 169: 1-5.118Feng et al., "Superplasticity and texture of SiC whiskers in a magnesium-based composite," Scripta Materialia, 2005, 53: 361-365.119Ferguson et al., "Corrosion—Fatigue Performance of Magnesium Alloys," International Journal of Modern Physics B, vol. 17, Nos. 8 & 9, 2003, pp. 1601-1607.120Fernando, "Review of Corrosion and Corrosion Control of Magnesium Alloys and Composites," J. Mater. Eng., 1989, 11:299-313.121Ferrando, "Review of Corrosion and Corrosion Control of Magnesium Alloys and Composites," J. Mater. Eng., 1989, 11:299-313.122Fischer et al., "Hydrogen in magnesium alloys and magnesium interfaces: preparation, electronic properties and interdiffusion," J. Less Common Metals, 1991, 172:808-815.123Fischer et al., "Hydrogen in magnesium alloys and magnesium interfaces: preparation, electronic properties and interdiffusion," J. Less-Common Metals, 1991, 172:808-815.124Fontenier et al., "Study of a 'Platinum-Magnesium' Cell to Supply Current to a Pacemaker," Bioelectrochemistry and Bioenergetics, 1975, 2(2):106-123.125Fontenier et al., "Study of a ‘Platinum-Magnesium’ Cell to Supply Current to a Pacemaker," Bioelectrochemistry and Bioenergetics, 1975, 2(2):106-123.126Fraunhofer EZRT, "Quantitative material analysis by dual energy computed tomography for industrial NDT applications," 2009, 1 pg.127Fraunhofer IIS—Poster (German), "Prinzip der hochauflosenden Comptuertomographie," 2009, 1 page.128Frei, "On the Role of Vitamin C and Other Antioxidants in Atherogenesis and Vascular Dysfunction," Proceedings-Society for Experimental Biology and Medicine, 1999, 222:196-204.129Frei, "On the Role of Vitamin C and Other Antioxidants in Atherogenesis and Vascular Dysfunction," Proceedings—Society for Experimental Biology and Medicine, 1999, 222:196-204.130Gabrielli, Claude. "Use and Applications of Electrochemical Impedance Analytical, 1997, 1-102. Techniques," Solartron Analytical, 1997, 1-102.131Garner et al., "Polypyrrole-heparin composites as stimulus-responsive substrates for endothelial cell growth," J. Biomed. Mater. Res., 1999, 44: 121-129.132Gettleman et al., "Materials Science: Measurement of in vivo Corrosion Rates in Baboons, and Correlation with in vitro Tests," Journal of Dental Research, 1980, vol. 59, pp. 689-707.133Gettleman et al., "Measurement of in vivo corrosion rates in baboons, and correlation with in vitro tests," Journal of Dental Research, 1980, 59: 689-707.134Gomes et al., "Alternative tissue engineering scaffolds based on starch: processing methodologies, morphology, degradation and mechanical properties," Materials Science and Engineering C, 2002, 20:19-26.135Gomes et al., "Alternative tissue engineering morphology, degradation and mechanical 20:19-26 scaffolds based on starch: processing methodologies, properties," Materials Science and Engineering C, 2002, 20:19-26.136Grassi et al., "Short-term administration of dark chocolate is followed by a significant increase in insulin sensitivity and a decrease in blood pressure in healthy persons," Am. J. Clin. Nutr., 2005, 81(3):611-614.137Gray and Luan, "Protective coatings on magnesium and its alloys-a critical review," J. Alloys Compounds, 2002, 336:88-113.138Gray and Luan, "Protective coatings on magnesium and its alloys — A critical review" J. Alloys Compounds, 2002, 336:88-113.139Gray and Luan, "Protective coatings on magnesium and its alloys—a critical review," J. Alloys Compounds, 2002, 336:88-113.140Griffiths et al., "Future devices: bioabsorbable stents" Br. J. Cardiol. (Acute & Cardiology), 2004, 11: AIC80-AIC84.141Grube, "Bioabsorbable Stents-The Boston Scientific & REVA Technology," EuroPCR 2009, 2009, pp. 1-27.142Guo et al., "Manipulation of single-wall carbon nanotubes into aligned molecular layers," Chem. Phys. Lett., 2002, 362:314-318.143Guo et al., "Multi-layer LB films of single-wall carbon nanotubes," Physica B. 2002, 323:235-236.144Gurib-Fakim, "Medicinal plants: Traditions of yesterday and drugs of tomorrow," Molecular Aspects of Medicine, 2006, 27:1-93.145Haferkamp et al., "Magnesium-Base-Alloys as Impant-Material Steps to the Production of Thin Components," Magnesium, 2000, 159-164.146Hau et al., "Surface-Chemistry Technology for Microfluidics," J. Micromech. Microeng., 2003, 13:272-278.147Hau et al., "Surface-Chemistry Technology for Microfluidies," J. Micromech. Microeng., 2003,13;272-278.148Heublein et al., "Biocorrosion of magnesium alloys: a new principle in cardiovascular implant technology?" Heart, 2003, 89:651-656.149Heublein et al., "Bio-corrosion-a new principle for temporary cardiovascular implants?" European Heart Journal, Journal of the European Society of Cardiology, 2000, vol. 21, p. 286, Abstract No. P1605.150Heublein et al., "Degradation of Metallic Alloys-A New Principle in Stent Technology?" The American Journal of Cardiology, Eleventh Annual Symposium Transcatheter Cardiovascular Therapeutics Abstracts, Sep. 22, 1999.151Heublein et al., "Local Tissue Engineering by Biocorrosion Vision or Reality?" The American Journal of Cardiology, TCT Abstracts/Poster, Oct. 16, 2000.152Heublein et al., "Bio-corrosion—a new principle for temporary cardiovascular implants?" European Heart Journal, Journal of the European Society of Cardiology, 2000, vol. 21, p. 286, Abstract No. P1605.153Heublein et al., "Degradation of Metallic Alloys—A New Principle in Stent Technology?" he American Journal of Cardiology, Elevent Annual Symposium Transcatheter Cardiovascular Therapeutics Abstracts, Sep. 22, 1999.154Heublein et al., "Degradation of Metallic Alloys—A New Principle in Stent Technology?" The American Journal of Cardiology, Eleventh Annual Symposium Transcatheter Cardiovascular Therapeutics Abstracts, Sep. 22, 1999.155Huang et al., "A Review on Polymer Nanofibers by Electro-spinning and their Applications in Nanocomposites," Composites Science & Technology, 2003, 63:2223-2253.156Huang et al., "A review on Polymer Nanofibers by Electro-spinning and their Applications in Nanocomposites," 2003, 63:2223-2253.157International Preliminary Report on Patentability in Application No. PCT/US2007/078476, mailed Mar. 26, 2009, 7 pages.158International Preliminary Report on Patentability in PCT/US05/16600 mailed Nov. 30, 2006, 7 pages.159International Preliminary Report on Patentability in PCT/US07/73839 mailed Apr. 2, 2009, 10 pages.160International Preliminary Report on Patentability in PCT/US07/73839 mailed Apr. 2, 2009.161International Preliminary Report on Patentability in PCT/US07/78411 mailed Feb. 4, 2009, 8 pages.162International Preliminary Report on Patentability in PCT/US07/78412 mailed Apr. 2, 2009, 7 pages.163International Preliminary Report on Patentability in PCT/US07/78429 mailed Apr. 2, 2009, 8 pages.164International Preliminary Report on Patentability in PCT/US07/78429 mailed Apr. 2, 2009.165International Preliminary Report on Patentability in PCT/US07/78450 mailed Mar. 26, 2009, 7 pages.166International Preliminary Report on Patentability in PCT/US07/78476 mailed Mar. 26, 2009, 7 pages.167International Preliminary Report on Patentability in PCT/US07/78505 mailed Mar. 26, 2009, 7 pages.168International Preliminary report on Patentability received in PCT/US2007/078417, mailed Mar. 26, 2009, 8 pages.169International Preliminary Report on Patentability, received in PCT/US2007/078407, mailed Mar. 26, 2009, 6 pages.170International Search Report and Written Opinion in PCT/US07/78449, mailed Jan. 13, 2009, 15 pages.171International Search Report and Written Opinion in PCT/US2007/078476, mailed Jan. 28, 2009, 29 pages.172International Search Report and Written Opinion mailed Jan. 25, 2008 in PCT/US07/75072, 14 pages.173International Search Report for PCT/US07/66568 daed Oct. 8, 2007, 15 pages.174International Search Report from PCT/US 03/20215, mailed Nov. 11, 2003, 4 pages.175International Search Report/Written Opinion in PCT/US05/16600 mailed May 4, 2006, 15 pages.176International Search Report/Written Opinion in PCT/US07/73839 mailed Apr. 16, 2008, 16 pages.177International Search Report/Written Opinion in PCT/US07/73839 mailed Apr. 16, 2008, 17 pages.178International Search Report/Written Opinion in PCT/US07/78411 mailed Mar. 6, 2008, 12 pages.179International Search Report/Written Opinion in PCT/US07/78429 mailed Mar. 28, 2008, 13 pages.180International Search Report/Written Opinion in PCT/US07/78429 mailed Mar. 28, 2008, 14 pages.181International Search Report/Written Opinion in PCT/US07/78505 mailed Mar. 4, 2008, 10 pages.182International Search Report/Written Opinion in PCT/US2009/43326 mailed Aug. 6, 2009, 9 pages.183Ito et al., "Antioxidant action of eugenol compounds; role of metal ion in the inhibition of lipid peroxidation," Food Chem. Toxicol., 2005, 43:461-466.184Ivanova and Ivanov, "Mechanisms of the extracellular antioxidant defend," Experimental Pathology and Parasitology, 2000, 4:49-59.185Jiang, "A review of wet impregnation-An alternative method for the fabrication of high performance and nano-structured electrodes of solid oxide fuel cells," Materials Science and Engineering A, 2006, 418:199-210.186Jiang, "A review of wet impregnation—An alternative method for the fabrication of high performance and nano-structured electrodes of solid oxide fuel cells," Materials Science and Engineering A, 2006, 418:199-210.187Kean and Davies, "Cathodic Protection," 7 pages, 1981; http://www.npl.co.uk/upload/pdf/cathodic-protection.pdf.188Kean and Davies, "Cathodic Protection," 7 pages, 1981; http://www.npl.co.uk/upload/pdf/cathodic—protection.189Kean and Davies, "Cathodic Protection," 7 pages, 1981; http://www.npl.co.uk/upload/pdf/cathodic—protection.pdf.190Kim et al., "Comprehensive study on vitamin C equivalent antioxidant capacity (VCEAC) of various polyphenols in scavenging a free radical and its structural relationship," Crit. Rev. Food Sci. Nutr., 2004, 44(4):253-273.191Kim et al., "Effect of Anti-Oxidant (Carvedilol and Probucol) Loaded Stents in a Porcine Coronary Restenosis Model," Circ. J., 2005, 69:101-106.192Kong et al., "Polyelectrolyte-functionalized multiwalled carbon nanotubes: preparation, characterization and layer-by-layer self assembly," Polymer, 2005, 46:2472-2485.193Kumar et al., "Polyanhydrides: an overview," Advanced Drug Delivery Reviews, 2002, 54:889-910.194Kurth et al., "Multilayer on Solid Planar Substrates: From Structure to Function", Multi-layer Thin Films Sequential Assembly of Nanocomposite Materials, 2003, Chapter 14, pp. 393-426.195Kurth et al., "Ultrathin Composite Films Incorporating the Nanoporous Isopolyoxomolybdate 'Keplerate' (NH4)42[Mo132O372(CH3COO)30(H2O)72]," Chem. Mater., 2000, 12:2829-2831.196Kurth et al., "Ultrathin Composite Films Incorporating the Nanoporous Isopolyoxomolybdate ‘Keplerate’ (NH4)42[Mo132O372(CH3COO)30(H20)72]," Chem. Mater., 2000, 12:2829-2831.197Kurth et al., "Ultrathin Composite Films Incorporating the Nanoporous Isopolyoxomolybdate ‘Keplerate’ (NH4)42[Mo132O372(CH3COO)30(H2O)72]," Chem. Mater., 2000, 12:2829-2831.198Kutsenko et al., "Structural Changes in Mg Alloy induced by plasma immersion ion implantation of Ag," Acta Materialia, 2004, 52:4329-4335.199Lambert et al., "Inhibition of carcinogenesis by polyphenols: evidence from laboratory investigations," Am. J.Clin. Nutr., 2005, 81:284S-291S.200Lambert et al., "Inhibition of carcinogenesis by polyphenols: evidence from laboratory investigations," Am. J. Clin. Nutr., 2005, 81(suppl):284S-291S.201Lee et al., "Retentive and compressive strengths of modified zinc oxide-eugenol cements," J. Dentistry, 2000, 28:69-75.202Li et al., "The corrosion inhibition of the self assembled Au, and Ag nonoparticles films on the surface of copper," Colloids and Surfaces A: Physiochem. Eng. Aspects, 2006, 273: 16-23.203Liao et al., "Fabrication of porous biodegradable polymer scaffolds using a solvent merging/particulate leaching method," J. Biomed. Mater. Res., 2002, 59(4):676-681.204Liao et al., "Fabrication of porous biodegradable polymer scaffolds using a solvent merging/particulate leaching method," J. Biomed. Mater. Res., 2002, 59:676-681.205Lin et al., "Micropatterning proteins and cells on polylactic acid and poly(lactide-co-glycolide)," Biomaterials, 2005, 26:3655-3662.206Liu et al. "Sol-gel deposited Ti02 film on NiTi surgical alloy for biocompatibility improvement" Thin Solid Films. Apr. 1, 2003, pp. 225-230.207Liu et al., "Characterizations of polypyrrole (PPy) nano-tubules made by templated ac electropolymerization," European Polymer Journal, 2005, 41: 2117-2121.208Liu et al., "Functional Polyoxometalate Thin Films via Electrostatic Layer-by-Layer Self-Assembly," Journal of Cluster Science, 2003, 14:405-419.209Liu et al., "Layer-By-Layer Ionic Self-Assembly of Au Colloids Into Multilayer Thin-Films with Bulk Metal Conductivity," Chemical Physics Letters, 1998, 298:315-319.210Liu et al., "Sol-gel deposited TiO2 film on NiTi surgical alloy for biocompatibility improvement," Thin Solid Films, 2003, 429:225-230.211Liu, Introduction to Corrosion and Protection, Corrosion and Protection Centre, School of Materials, The University of Manchester, 2006, 36 pages.212Lu et al., "Theoretical analysis of calcium phosphate precipitation in simulated body fluid," Biomaterials, 2005, 26:1097-1108.213Maier et al., "High concentrations of magnesium modulate vascular endothelial cell behaviour in vitro," Biochim. Biophys. Acta, 2004, 1689:6-12.214Mamedov et al., "Molecular Design of Strong Single-Wall Carbon Nanotube/Polyelectrolyte Multilayer Composites," Nature Materials, 2002, 1:190-194.215Mansfeld, Florian. "Analysis and Interpretation of EIS Data for Metals and Alloys," Solartron Analytical, 1999, 1-77.216Matsuoka et al., "Hyperthermia Using Magnetite Cationic Liposomes for Hamster Osteosarcoma," BioMagnetic Research and Technology, 2004, 2:3-8.217Matsuoka et al., "Hyperthermia Using Magnetite Cationic Liposomes for Hamster Osteosarcoma," Biomagnetic Research and Technology, Mar. 25, 2004, pp. 1-6.218Medical Device Daily, "Conor Cites Positive 12-month Results for Its CoStar Stent", May 2005 (1 page).219Meng Han, "Laser nitriding of metals: Influences of the ambient pressure and the pulse duration," 2001, Dissertation, Georg-Aug.-Universitat Gottingen, 134 pages.220Middleton and Tipton, "Synthetic Biodegradable Polymers as Medical Devices," http://www.devicelink.com/mpb/archive/98/03/002.html, Mar. 1998, 9 pages.221Middleton and Tipton, "Synthetic Biodegradable Polymers as Medical Devices,"http://www.devicelink.com/mpb/archive/98/03/002.html, Mar. 1998, 9 pages.222Mihailovic et al., "Unusual Magnetic State in Lithium-Doped MoS2 Nanotubes," Phys. Rev. Lett., 2003, 90 146401-1-4.223Mihailovic et al., "Unusual Magnetic State in Lithium-Doped MoS2 Nanotubes," Phys. Rev. Lett., 2003, 90 146401-1-4.224Mikos and Temenoff, "Formation of highly porous biodegradable scaffolds for tissue engineering," Electronic Journal of Biotechnology, 2000, 3(2):1-6.225Mikos and Temenoff, "Formation of highly porous biodegradable scaffolds for tissue engineering," Electronic Journal of Biotechnology, 2000, 3(2):114-119.226Mohanty et al. "Evaluation of soft tissue response to a poly[urethane urea]," Biomaterials, 1992, 13(10):651-656.227Mohanty et al. "Evaluation of soft tissue response to a poly[urethane urea]," Biomaterials, 1992,13(10):651-656.228Mohanty et al., "Effect of Curcuma longa and Ocimum sanctum on myocardial apoptosis in experimentally induced myocardial ischemic-reperfusion injury," BMC Complementary and Alternative Medicine, 2006, 6:3-14.229Molnar and Garai, "Plant-derived anti-inflammatory compounds affect MIF tautomerase activity," International Immunopharmacology, 2005, 5:849-856.230Moskaug et al., "Polyphenols and glutathione synthesis regulation," Am. J. Clin. Nutr., 2005, 81:277S-283S.231Moskaug et al., "Polyphenols and glutathione synthesis regulation," Am. J. Clin. Nutr., 2005, 81 (suppl):277S-283 S.232Naderi et al., "Effect of some volatile oils on the affinity of intact and oxidized low-density lipoproteins for adrenal cell surface receptors," Mol. Cell. Biochem., 2004, 267:59-66.233Niemeyer et al., "Magnesium alloys as biodegradable metallic implant materials for cardiovascularic and orthopaedic surgery," Euromat 2001, 7th European Conference on Advanced Materials and Processes, Jun. 10-14, 2001 (Abstract).234Niinisto, "Atomic Layer deposition: A key technology for the controlled growth of oxide thin films for advanced applications," Proc. Estonian Acad. Sci. Phys. Math., 2003, 52(3):266-276.235Nilsson et al., "Development of a dosage method for electrochemical treatment of tumours: a simplified mathematical model," Bioelectrochemistry and Bioenergetics, 1998, 47:11-18.236Ormiston et al., "Bioabsorbable Coronary Stents," Circulation Cardiovasc Intervent, vol. 2, 2009, pp. 255-260.237Ou et al., "Protective effects of eugenol against oxidized LDL-induced cytotoxicity and adhesion molecule expression in endothelial cells," Food Chem. Toxicol., 2006, 44:1485-1495.238Park et al., "Microstructural change and precipitation hardening in melt-spun Mg-X-Ca alloys," Science and Technology of Advanced Materials, 2001, 2:73-78.239Park et al., "Microstructural change and precipitation hardening in melt-spun Mg—X—Ca alloys," Science and Technology of Advanced Materials, 2001, 2:73-78.240Peuster et al. "Long-term biocompatibility of a corrodible peripheral iron stent in the porcine of descending aorta," Biomaterials, 2006, 4955-4962.241Peuster et al., "A novel approach to temporary stenting: degradable cardiovascular stents produced from corrodible metal-results 6-18 months after implantation into New Zealand white rabbits," Heart, 2001, 86(5): 563-569.242Peuster et al., "Long-term biocompatibility of a corrodible peripheral iron stent in the porcine of descending aorta," Biomaterials, 2006, 27:4955-4962.243Peuster et al., "A novel approach to temporary stenting: degradable cardiovascular stents produced from corrodible metal-results 6-18 months after implantation into New Zealand white rabbits," Heart, 2001, 86(5):563-569.244Peuster et al., "Are resorbable implants about to become a reality," Cardiol Young, 2006, 16:107-116.245Pinto Slattow et al., "Optical coherence tomography and intravascular ultrasound imaging of bioabsorbable magnesium stent degradation in porcine coronary arteries," Cardiovascular Revascularization Medicine 9, (2008) pp. 248-254.246Prasse et al., "Electric Anisotropy of Carbon Nanofibre/Epoxy Resin Composites Due to Electric Field Induced Alignment," Composites Science and Technology, 2003, 63:1835-1841.247Purushothaman et al. "Reducing Mass-Transport Limitations by Application of Special Pulsed Current Modes". Journal of the Electrochemical Society, 152 (4), 2005, J33-J39.248Qasem et al., "Kinetics of paclitaxel 2′-N-methylpyridinium mesylate decomposition," AAPS PharmSciTech, 2003, 4(2), Article 21, 8 pages.249Quinard et al., "Development of metal/polymer mixtures for micro powder injection moulding," 10th ESAFORM Conference on Material Forming, 2007, pp. 933-939.250Ratnam et al., "Role of antioxidants in prophylaxis and therapy: A pharmaceutical perspective," J. Controlled Release, 2006, 113:189-207.251Remskar et al., "Self-Assembly of Subnanometer-Diameter Single-Wall MoS2 Nanotubes," Science, 2001,292:479-481.252Remskar et al., "Self-Assembly of Subnanometer-Diameter Single-Wall MoS2 Nanotubes," Science, 2001, 292:479-481.253Rezwan et al., "Biodegradable and bio active porous polymer/inorganic composite scaffolds for bone tissue engineering," Biomaterials, 2006, 27:3413-3431.254Rhule et al., "Polyoxometalates in Medicine," Chem. Rev., 1998, 98:327-357.255Russell-Stevens et al., "The effect of thermal cycling on the properties of a carbon fibre reinforced magnesium composite," Materials Science and Engineering A, 2005, 397: 249-256.256Rutledge et al., "Electrostatic Spinning and Properties of Ultrafine Fibers," National Textile Center Annual Report, Nov. 2001, M01-D22, pp. 1-10.257Ryan et al., "Fabrication methods of porous metals for use in orthopaedic applications," Biomaterials, 2006, 27:2651-2670.258Sastry et al., "DNA-Mediated Electrostatic Assembly of Gold Nanoparticles into Linear Arrays by a Simple Drop-Coating Procedure," Appl. Phys. Lett., 2001, 78:2943-2945.259Satoh et al., "Effect of Antioxidants on Radical Intensity and Cytotoxic Activity of Eugenol," Anticancer Res., 1998, 18:1549-1552.260Satoh et al., "Effect of Antioxidants on Radical Intensity and Cytotoxic Activity of Eugenol," Anticancer Res.,1998, 18:1549-1552.261Sawitowski et al., "Nanoporous Alumina Coatings for Medical Implants and Stents—Radiotherapy, Drug Delivery, Biological Compatibility," Materials Research Society Symposium Proceedings, 1999, 581:523-528.262Sawitowski, "New Drug Delivery Systems—Examples of Applied Nanotechnology," VDE World Microtechnologies Congress, Sep. 25-27, 2000, Expo 2000, Hannover, Germany, Proveeds vol. 1, p. 343-346.263Sawyer et al., "Electrochemical Criteria in the Choice of Materials used in Vascular Prostheses," Biophysical Mechanisms in Vascular Homeostasis and Intravascular Thrombosis, 1965, pp. 337-348.264Schetky, "Shape Memory Alloys," Encyclopedia of Chemical Technology (3rd ed.), 1962, John Wiley & Sons, 20:726.265Schetky, "Shape Memory Alloys," Encyclopedia of Chemical Technology (3rd ed.), 1982, John Wiley & Sons, 20:726.266Shaw, "Corrosion Resistance of Magnesium Alloys," ASM Handbook vol. 13A: Corrosion: Fundamentals, Testing, and Protection, 2003, 5 pages.267Shenoy et al., "Role of Chain Entanglements on Fiber Formation During Electrospinning of Polymer Solutions: Good Solvent, Non-Specific Polymer-polymer Interaction Limit, " Polymer, 2005,46:3372-3384.268Shenoy et al., "Role of Chain Entanglements on Fiber Formation During Electrospinning of Polymer Solutions: Good Solvent, Non-Specific Polymer-polymer Interaction Limit," Polymer, 2005, 46:3372-3384.269Shi et al., "A novel electrically conductive and biodegradable composite made of polypyrrole nanoparticles and polylactide," Biomaterials, 2004, 25:2477-2488.270Shin, "Experimental Characterization of Electro spinning: the Electrically Forced Jet and Instabilities," Polymer, 2001, 42:9955-9967.271Shin, "Experimental Characterization of Electrospinning: the Electrically Forced Jet and Instabilities," Polymer, 2001, 42:9955-9967.272Singh et al., "Electrocatalytic Activity of Electrodeposited Composite Films of Polypyrrole and CoFe2O4 Nanoparticles Towards Oxygen 4612 Reduction Reaction," Electrochimica Acta, 2004, 49:4605-4612.273Singh et al., "Electrocatalytic Activity of Electrodeposited Composite Films of Polypyrrole and CoFe2O4 Nanoparticles Towards Oxygen Reduction Reaction," Electrochimica Acta, 2004, 49:4605-4612.274Song et al., "Galvanic corrosion of magnesium alloy AZ91D in contact with an aluminium alloy, steel and zinc," Corrosion Science, 2004, 46:955-977.275Stoclet et al., "Vascular protection by dietary polyphenols," Eur. J. Pharmacol., 2004, 500:299-313.276Straumal et al., "Vacuum arc deposition of protective layers on glass and polymer," Thin Solid Films, 2001, 383:224-226.277Straumal et al., "Vacuum arc deposition of protective layers on glass and polymer," Thin Solid Films,2001, 383:224-226.278Suhaj, "Spice antioxidants isolation and their antiradical activity: a review," J. Food Composition and Analysis, 2006, 19:531-537.279Sukhorukov et al., "Comparative Analysis of Hollow and Filled Polyelectrolyte Microcapsules Templated on Melamine Formaldehyde and Carbonate Cores," Macromol. Chem. Phys., 2004, 205:530-535.280Suslick et al., "The Photochemistry of Chromium, Manganese, and Iron Porphyrin Complexes," J. Chem., 1992, 16:633-642.281Suslick et al., "The photochemistry of chromium, manganese, and iron porphytin complexes," J. Chem., 1992, 16:633-642.282Tada et al., "Distribution of pH during galvanic corrosion of a Zn/steel couple," Electrochimica Acta, 2004, 49:1019-1026.283Tan et al., "Systematic Parameter Study for Ultra-Fine Fiber Fabrication Via Electrospinning Process," Polymer, 2005, 46:6128-6134.284Tian et al., "Corrosion resistance improvement of magnesium alloy using nitrogen plasma ion implantation," Surface & Coatings Technology, 2005, 198:454-458.285U.S. Appl. No. 10/849,742, filed May 20, 2004, Chen et al.286U.S. Appl. No. 60/826,002, filed Sep. 18, 2006, Girton et al.287U.S. Appl. No. 60/845,136, filed Sep. 15, 2006, Weber et al.288U.S. Appl. No. 60/862,318, filed Oct. 20, 2006, Atanasoska et al.289US 6,533,715, 03/2003, Hossainy et al. (withdrawn)290Vermette et al., "Immobilized Liposome Layers for Drug Delivery Applications," J. Controlled Release, 2002, 80:179-195.291Virtanen, "Corrosion of Biomedical Implant Materials," Corrosion of Biomedical Implant Materials, vol. 26, Nos. 2-3, 2008, pp. 147-171.292Viswanathamurthi et al., "Preparation and morphology of niobuim oxide fibres by electrospinning," Chemical Physics Letters, 2003, 374: 79-84.293von Euler et al., "Cell proliferation and apoptosis in rat mammary cancer after electrochemical treatment (EChT)," Bioelectrochemistry, 2004, 62:57-65.294Vrbanic et al., "Air-Stable Monodispersed Mo6S3I6 Nanowires," Nanotechnology, 2004, 15:635-638.295Waksman et al., "Early-and Long-Term Intravascular Ultrasound and Angiographic Findings After Bioabsorbable Magnesium Stent Implantation in Human Coronary Arteries," JACC: Cardiovascular Interventions, vol. 2, No. 4, 2009, pp. 1-9.296Wallerath et al., "A blend of polyphenolic compounds explains the stimulatory effect of red wine on human endothelial NO synthase," Nitric Oxide, 2005, 12:97-104.297Wallerath et al., "A blend of polyphenols explains the stimulatory effect of red wine on human endothelial NO synthase," Nitric Oxide, 2005, 12(2):97-104.298Wan et al., "Influence of Plasma Immersion Ion Implantation on Corrosion Properties of Magnesium," South Jiaotong University, Chengdu, 2005.299Wan et al., "Influence of Plasma Immersion Ion Implantation on Corrosion Properties of Magnesium," Southwest Jiaotong University, 2005, Chengu, 11 pages.300Wan et al., "Preparation and characterization of porous conducting poly(DL-lactide) composite membrances," Journal of Membrane Science, 2005, 246: 193-201.301Wang et al., "Characterisation of Severely Deformed Austenitic Stainless Steel Wire," Materials Science and Technology, 2005, 21:1323-1328.302Wang et al., "Characterisation of Severely Deformed Austenitic Stainless Steel Wire." Materials Science and Technology, 2005, 21(11):1323-1328.303Wang et al., "Nonlinear optical properties of thin iron films grown on MgO (100) by pulsed laser deposition," Thin Solid Films, 2005, 471:86-90.304Wang et al., "Nonlinear optical properties of thin iron films grown on MgO (100) by uplsed laser deposition," Thin Solid Films, 2005, 471:86-90.305Wang, "Recent development of non-platinum catalysts for oxygen reduction reaction," J. Power Sources, 2005, 152:1-15.306Wang, "Recent development of non-platinum catalysts for oxygen reduction reaction," J. PowerSources, 2005, 152:1-15.307Weber et al., "Hardness and corrosion resistance of single-phase nitride and carbide on ion," Materials Science and Engineering, 1995, 99:205-210.308Weber et al., "Hardness and corrosion resistance of single-phase nitride and carbide on ion," Materials Scienceand Engineering, 1995, 99:205-210.309Weh et al., "Evolution of afractal-like surface structures in layers of polyacrylonitrile solutions by interfacial dynamic processes," J. Colloid and Interface Science, 2004, 271: 407-415.310Weh et al., "Evolution of afractal-like surface structures in layers of polyacrylonitrile solutions by interfacial dynamic processes," J. Colloid and Interface Science, 2004, 271:407-415.311Widmer et al., "Manufacture of porous biodegradable polymer conduits by an extrusion process for guided tissue regeneration," Biomaterials, 1998, 19:1945-1955.312Wieneke et al., "Stent Coating: A New Approach in Interventional Cardiology," Herz, 2002, 27(6):518-526.313Wikipedia, the Free Encyclopedia, "Galvanic Corrosion." <http://en.wikipedia.org/wiki/Galvanic—corrosion> on Mar. 11, 2011, 7 pages.314Williamson et al., "Bioavailability and bioefficacy of polyphenols in humans. II. Review of 93 intervention studies," Am. J. Clin. Nutr., 2005, 81:243S-255S.315Witte et al., "In vitro and in vivo corrosion measurements of magnesium alloys," Biomaterials, 2006, 27:1013-1018.316Witte, "The history of biodegradable magnesium implants: A review," Acta Biomaterialia, 2010, 6:1680-1692.317Xu et al., "In Vivo corrosion behaviouc of Mg-MnZn alloy for bone implant application," Journal of Biomedical Materials Research Part A, Jun. 4, 2007, pp. 703-711.318Yamaguchi et al., "Mg2Si Coating Technology on Magnesium Alloys to Improve Corrosion and Wear Resistance", JOM, 2004, p. 343.319Yi et al., "Characterization of a bioactive nanotextured surface created by controlled chemical oxidation of titanium," Surface Science, 2006, 600:4613-4621.320You et al., "The Effect of Calcium Additions on the Oxidation Behavior in Magnesium Alloys," Scripta Mat., 2000, 42:1089-1094.321Yu and Uan, "Sacrificial Mg film anode for cathodic protection of die cast Mg-9-wt.%-1 wt.%Zn alloy in NaCl aqueous solution," Scripta Mat., 2006, 54:1253-1257.322Yue et al., "Improvement in the Corrosion Resistance of Magnesium ZK60/SiC Composite by Excimer Laser Surface Treatment," Scripta Materialia, 1998, 38(2):191-198.323Yun et al., "Revolutionizing Biodegradable Materials," Materials Today, Oct. 2009, vol. 12, No. 10, pp. 1-11.324Zarras et al., "Progress in using conductive polymers as corrosion-inhibiting coatings, " Radiation Physics and Chemistry, 2003, 68: 387-394.325Zberg et al., "MgZnCa glasses without clinically observable hydrogen evolution for biodegradable implants," Nature materials, Sep. 27, 2009, vol. 8, pp. 887-891.326Zeta Potential—An Introduction in 30 Minutes, Technical Note; http://www.nbtc.cornell.edu/facilities/downloads/Zeta%20potential%20-%20An%20introduction%20in%2030%20minutes.pdf, Retrieved from the Internet on May 9, 2005 (6 pages).327Zhang et al., "Improving multilayer films endurance by photoinduced interaction between Dawson-type polyoxometalate and diazo resin," Materials Chemistry and Physics, 2005, 90:57-52.328Zhang et al., "Natural Polyelectrolyte Films Based on Layer-by-Layer Deposition of Collagen and Hyaluronic Acid," Biomaterials, 2005, 26:3353-3361.329Zhang et al., "Ways for fabricating stable layer-by layer self-assemblies: combined ionic self-assembly and post chemical reaction," Colloids and Surfaces A: physiochemical and Engineering Aspects, 2002, pp. 198-200, 439-442.330Zheng, "Symposium on Biodegradable/Biocorroded metallic materials," Nov. 24, 2009, pp. 1-74.331Zhou et al., "Drug-loaded, Magnetic, hollow silica nanocomposites for nanomedicine," Nanomedicine: Nanotechnology, Biology and Medicine, 2005, 1:233-237.332Zucchi et al., "Influence of a silane treatment on the corrosion resistance of a WE43 magnesium alloy," Surface Coatings Technol., 2006, 200:4136-4143.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS20070203564 *Feb 28, 2006Aug 30, 2007Boston Scientific Scimed, Inc.Biodegradable implants having accelerated biodegradation properties in vivoUS20120150286 *Feb 14, 2012Jun 14, 2012Boston Scientific Scimed, Inc.Bioerodible endoprosthesis with biostable inorganic layers* Cited by examinerClassifications U.S. Classification623/1.42International ClassificationA61F2/06Cooperative ClassificationA61L31/022, A61L31/082, A61L2300/416, A61L31/16European ClassificationA61L31/16, A61L31/02B, A61L31/08BLegal EventsDateCodeEventDescriptionDec 18, 2007ASAssignmentOwner name: BOSTON SCIENTIFIC SCIMED, INC., MINNESOTAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:WEBER, JAN;ATANASOSKA, LILIANA;SCHEWE, SCOTT;REEL/FRAME:020260/0366;SIGNING DATES FROM 20070913 TO 20071119Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:WEBER, JAN;ATANASOSKA, LILIANA;SCHEWE, SCOTT;SIGNING DATES FROM 20070913 TO 20071119;REEL/FRAME:020260/0366Owner name: BOSTON SCIENTIFIC SCIMED, INC., MINNESOTAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:WEBER, JAN;ATANASOSKA, LILIANA;SCHEWE, SCOTT;SIGNING DATES FROM 20070913 TO 20071119;REEL/FRAME:020260/0366RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services