Patent US5327285 - Methods for manufacturing micropolarizers - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsA method of mass producing a micropolarizer including the steps exposing films of predetermined polarization states to electromagnetic radiation through masks of predetermined patterns, etching away exposed parts of each film and aligning and laminating the films to one another to provide a microplolarizer...http://www.google.com/patents/US5327285?utm_source=gb-gplus-sharePatent US5327285 - Methods for manufacturing micropolarizersAdvanced Patent SearchPublication numberUS5327285 APublication typeGrantApplication numberUS 07/536,419Publication dateJul 5, 1994Filing dateJun 11, 1990Priority dateJun 11, 1990Fee statusPaidAlso published asUS5844717, US6384971Publication number07536419, 536419, US 5327285 A, US 5327285A, US-A-5327285, US5327285 A, US5327285AInventorsSadeg M. FarisOriginal AssigneeFaris Sadeg MExport CitationBiBTeX, EndNote, RefManPatent Citations (15), Non-Patent Citations (22), Referenced by (131), Classifications (25), Legal Events (8) External Links: USPTO, USPTO Assignment, EspacenetMethods for manufacturing micropolarizers
US 5327285 AAbstract
A method of mass producing a micropolarizer including the steps exposing films of predetermined polarization states to electromagnetic radiation through masks of predetermined patterns, etching away exposed parts of each film and aligning and laminating the films to one another to provide a microplolarizer comprising alternating sets of microscopic polarizers with different polarization states.
1. A method for fabricating a micropolarizer, comprising the steps of:providing a first polarized film having a first polarization state, P1 and coated with photoresist; exposing the film to a source of electromagnetic radiation through a mask having a first predetermined pattern; removing parts of the first film exposed to the electromagnetic radiation through the mask; repeating the providing, exposing and removing steps with a second polarized film having a second polarization state, P2 and coated with photoresist and using a mask having a second predetermined pattern that is an inverse of the first predetermined pattern; aligning the first polarized film and the second polarized film so that the removed parts of the first film are aligned with those parts of the second film that were not removed; laminating the aligned first and second films to one another. 2. A method of fabricating a micropolarizer, comprising the steps of:providing a first film having a first pattern of optically active and non-optically active parts; providing a second film having a second pattern of optically active and non-optically active parts; wherein the optically active parts of the second film affect light differently than the optically active parts of the first film and the first pattern is an inverse of the second pattern; thereafter, aligning the first and second films so that the optically active parts of the first film are aligned with and overlap the non-optically active parts of the second film and vice versa; and laminating the aligned first and second films to one another. 3. The method of claim 2, wherein the providing step includes providing the first film as a first set of optically active parts mounted on a first substrate according to the first pattern and providing the second film as a second set of optically active parts mounted on a second substrate according to the second pattern.
4. The method of claim 3, wherein the laminating step is carried out by contacting and laminating the optically active parts of one of the first and second films to the substrate layer of the other of the first and second films.
5. The method of claim 3, wherein the laminating step is carried out by contacting and laminating the optically active parts of each of the first and second films to the substrate layer of the other of the first and second films to provide a layer of interposed optically active parts of the first and second films, the interposed optically active parts being sandwiched between the respective substrate layers.
6. The method of claim 3, wherein the laminating step is carried out by contacting and laminating the substrate layers of the first and second films to one another.
7. The method of claim 2, wherein the providing step includes providing the first film as a first set of optically active parts mounted on a first side of a common substrate according to the first pattern and providing the second film as a second set of optically active parts mounted on a second side of the common substrate according to the second pattern.
8. The method of claim 2, wherein the optically active parts of each of the first and second films are quarter wave retarders having respective optical axes oriented 90� from each other; and wherein the laminating step includes laminating a sheet of polarizer to the laminated first and second films.
9. The method of claim 8, wherein the sheet of polarizer is a linear polarizer.
10. A method for fabricating a micropolarizer, comprising the steps of:providing a first film coated with a protective mask having a predetermined pattern that exposes preselected parts of the first film; thereafter, treating the first film to affect the preselected parts of the first film to provide a pattern of polarized and unpolarized parts of the first film, the polarized parts of the first film having a first polarization state, P1; repeating the providing and treating steps with a second film coated with a protective mask to provide a pattern of polarized and unpolarized parts of the second film, the polarized parts of the second film having a second polarization state, P2, and, using a mask having a second predetermined pattern that is an inverse of the first predetermined pattern; thereafter, aligning the treated first and second films so that the polarized parts of the first film are aligned with and overlap the unpolarized parts of the second film and vice versa; and laminating the aligned first and second films to one another. 11. The method of claim 10, wherein the first film comprises a polarized film having the first polarization state, P1, and the second film comprises a polarized film having the second polarized state, P2; and wherein the treating step is carried out by treating the first and second films to remove the polarization state of the respective preselected exposed parts of each of the first and second films
12. The method claim of 11, wherein the first and second films each comprise a polarized PVA film.
13. The method of claim 11, wherein the first and second films are cholesteric liquid crystal polarizers of P1 and P2 polarization states respectively.
14. The method of claim 10, wherein the step of treating each of the first and second films to remove the polarization state of the respective preselected exposed parts is carried out by applying a solvent or an etchant solution to the respective preselected exposed parts.
15. The method of claim 10 wherein each of the first and second films comprise a stretched PVA film without a dichroic effect and wherein the treating step is carried out by applying an iodine solution to the respective exposed parts of the first and second films to cause a dichroic effect at each respective exposed part, the stretched PVA of the first film polarizing light according to the first polarization state, P1, after treatment and the stretched PVA of the second film polarizing light according to the second polarization state, P2, after treatment.
16. The method of claim 15, wherein the iodine solution comprises a solution of iodine and potassium iodide and comprising the further step of applying a stabilizing solution to the respective preselected parts after application of the iodine solution.
17. The method of claim 10, wherein the providing step includes mounting each of the first and second films on a respective substrate layer.
18. The method of claim 17, wherein the laminating step is carried out by contacting and laminating one of the first and second films to the substrate layer of the other of the first and second films.
19. The method of claim 17, wherein the laminating step is carried out by contacting and laminating the substrate layers of the first and second films to one another.
20. The method of claim 10, wherein the aligning and laminating steps are carried out by mounting each of the first and second films to a common substrate layer interposed between the first and second films.
21. The method of claim 10, wherein the first and second polarization states are linear polarization states oriented 90� from one another.
22. The method of claim 10, wherein the first film comprises a polarized film having the first polarization state, P1, and the second film comprises a polarized film having the second polarization state, P2;wherein the providing step includes mounting each of the first and second films on a respective substrate layer; and wherein the treating step is carried out by etching away the respective preselected parts of each of the first and second films to provide a pattern of polarized parts mounted on each respective substrate layer. 23. The method claim of 22, wherein the etching step is carried out by chemically etching away the respective preselected parts of each of the first and second films.
24. The method of claim 22, wherein the etching step is carried out by photochemically etching away the respective preselected parts of each of the first and second films.
25. The method of claim 22, wherein the etching step is carried out by laser etching away the respective preselected parts of each of the first and second films.
26. The method of claim 22, wherein the etching step is carried out by reactive ion etching away the respective preselected parts of each of the first and second films.
27. The method of claim 22, wherein the laminating step is carried out by contacting and laminating the polarized parts of one of the first and second films to the substrate layer of the other of the first and second films.
28. The method of claim 22, wherein the laminating step is carried out by contacting and laminating the polarized parts of each of the first and second films to the substrate layer of the other of the first and second films to provide a layer of interposed polarized parts of the first and second films, the interposed polarized parts being sandwiched between the respective substrate layers.
29. The method of claim 22, wherein the laminating step is carried out by contacting and laminating the substrate layers of the first and second films to one another.
30. The method of claim 22, wherein the first and second films are mounted on a common substrate layer.
31. A method for fabricating a patterned polarizer film, comprising the steps of:providing a first film coated with a protective mask having a predetermined pattern that exposes preselected parts of the first film; and thereafter, treating the first film to affect the preselected parts of the first film to provide a pattern of polarized and unpolarized parts of the first film, the polarized parts of the first film having a first polarization state, P1. 32. The method of claim 31, wherein the first film comprises a polarized film having the first polarization state, P1; and wherein the treating step is carried out by treating the first film to remove the polarization state of the preselected exposed parts of the first film.
33. The method of claim 32, wherein the first film comprises a polarized PVA film.
34. The method of claim 32, wherein the first film comprises a cholesteric liquid crystal polarizer.
35. The method of claim 32, wherein the first film comprises a half-wave retarder.
36. The method of claim 32, wherein the first film comprises a quarter-wave retarder.
37. The method of claim 31, wherein the step of treating the first film to remove the polarization state of the preselected exposed parts is carried out by applying an etchant or a solvent solution to the preselected exposed parts.
38. The method of claim 31, comprising the further step of laminating the first film to a sheet of polarizer.
39. The method of claim 38, wherein the first film is a retarder and wherein the sheet of polarizer comprises a sheet of linear polarizer.
40. The method of claim 31, wherein the first film comprises a polarized film having the first polarization state, P1;wherein the providing step includes mounting the first film on a substrate layer; and wherein the treating step is carried out by etching away the preselected parts of the first film to provide a pattern of polarized parts mounted on the substrate layer. 41. The method of claim 40, wherein the etching step is carried out by chemically etching away the preselected parts of the first film.
42. The method of claim 40, wherein the etching step is carried out by photochemically etching away the preselected parts of the first film.
43. The method of claim 40, wherein the etching step is carried out by laser etching away the preselected parts of the first film.
44. The method of claim 40, wherein the etching step is carried out by reactive ion etching away the preselected parts of the first film.
45. A method of fabricating a micropolarizer, comprising the steps of:providing a first film having a first pattern of polarized and unpolarized parts, the polarized parts of the first film having a first polarization state, P1; providing a second film having a second pattern of polarized and unpolarized parts, the polarized parts of the second film having a second polarization state, P2, and wherein the first pattern is an inverse of the second pattern; thereafter, aligning the first and second films so that the polarized parts of the first film are aligned with and overlap the unpolarized parts of the second film and vice versa; and laminating the aligned first and second films to one another. 46. The method of claim 45, wherein the providing step includes mounting each of the first and second films on a respective substrate layer.
47. The method of claim 46, wherein the laminating step is carried out by contacting and laminating the first and second films to one another.
48. The method of claim 46, wherein the laminating step is carried out by contacting and laminating the first and second films to the substrate layer of the other of the first and second films.
49. The method of claim 46, wherein the laminating step is carried out by contacting and laminating the substrate layers of the first and second films to one another.
50. The method of claim 45, wherein the aligning and laminating steps are carried out by mounting each of the first and second films to a common substrate layer interposed between the first and second films.
51. The method of claim 45, wherein the first and second polarization states are linear polarization states oriented 90� from one another.
52. The method of claim 45, wherein the first and second polarization states are left and right circular polarization.
53. The method of claim 45, wherein the providing step includes providing the first film as a first set of polarized parts each having the first polarization state, P1, and the first set being mounted on a first substrate according to the first pattern and providing the second film as a second set of polarized parts each having the second polarization state, P2, and the second set being mounted on a second substrate according to the second pattern.
54. The method of claim 52, wherein the laminating step is carried out by contacting and laminating the polarized parts of one of the first and second films to the substrate layer of the other of the first and second films.
55. The method of claim 52, wherein the laminating step is carried out by contacting and laminating the polarized parts of each of the first and second films to the substrate layer of the other of the first and second films to provide a layer of interposed polarized parts of the first and second films, the interposed polarized parts being sandwiched between the respective substrate layers.
56. The method of claim 52, wherein the laminating step is carried out by contacting and laminating the substrate layers of the first and second films to one another.
This invention relates to the field of polarizers and the high throughput mass manufacturing of a new class of polarizars called micropolarizers. Micropolarizers have been developed for use in spatial multiplexing and demultiplexing image elements in a 3-D stereo imaging and display system.
This invention is related to my co-pending application Serial No. 07/536,190 entitled "A System For Producing 3-D Stereo Images" filed on even date herewith which introduces a fundamentally new optical element called a micropolarizer. The function of the micropolarizer is to spatially multiplex and spatially demultiplex image elements in the 3-D stereo imaging and displaying system of the aforementioned co-pending application. As shown in FIG. 1, the micropolarizer (μPol) 1, 2 is a regular array of cells 3 each of which comprises a set of microscopic polarizers with polarization states P1 and P2. The array has a period p which is the cell size and is also the pixel size of the imaging or displaying devices.
It is possible to turn unpolarized light into linearly polarized light by one Of three well known means: 1) Nicol prisms; 2) Brewster Angle (condition of total internal reflection in dielectric materials); and 3) Polaroid film. These are called linear polarizers. The Polaroids are special plastic films which are inexpensive and come in very large sheets. They are made of polyvinyl alcohol (PVA) sheets stretched between 3 to 5 times their original length and treated with iodine/potassium iodide mixture to produce the dichroic effect. This effect is responsible for heavily attenuating (absorbing) the electric field components along the stretching direction while transmitting the perpendicular electric field components. Therefore, if P1 is along the stretching direction of the PVA sheets, it is not transmitted, where as only P2 is transmitted, producing polarized light. By simply rotating the PVA sheet 90 degrees, P1 state will now be transmitted and P2 will be absorbed.
The aforementioned three known means for producing polarized light have always been used in situations where the polarizer elements have large areas, in excess of 1 cm2. However, for 3-D imaging with μPols using 35 mm film, to preserve the high resolution, the μPol array period p may be as small as 10 micron. Therefore, there is no prior art anticipating the use of or teaching how to mass produce μPols having such small dimensions.
The present invention provides a means for high through put mass manufacturing of micropolarizer arrays. To use the μPols in consumer 3-D photography, and printing applications, the economics dictate that the cost of μPols be in the range of 1 to 5 cents per square inch. For this reason, the low cost PVA is the basis for the manufacturing process.
The present invention also provides a flexible μPols manufacturing process which can be adapted to low and high resolution situations as well as alternative manufacturing methods, each of which may be advantageous in certain applications and adaptable to processing different polarizer materials. The present invention further provides an electronically controllable μPol.
FIG. 1 is an illustration of a micropolarizer array according to the present invention.
FIGS. 2 and 3 illustrate fabrication processes of linear micropolarizers using, respectively, bleaching and selective application of iodine.
FIG. 4 shows final alignment and lamination processes for making linear micropolarizers.
FIG. 5 illustrates a process for fabricating linear micropolarizers by means of etching.
FIG. 6 illustrates a method for patterning micropolarizer by mechanical means.
FIG. 7 shows final alignment and lamination processes for making linear micropolarizers by the etching method.
FIG. 8 shows final alignment and lamination processes for making circular micropolarizers by the etching method.
FIGS. 9 and 10 illustrate processes for making linear and circular polarizers eliminating an alignment step.
FIGS. 11 and 12 illustrate photo-lithographic patterning steps.
FIG. 13 illustrates an automated high through-put process for continuous production of micropolarizer sheets by photo-lithographic means.
FIG. 14 illustrates an automated high throughput process for continuous production of micropolarizer sheets by direct application of bleaching ink or iodine-based ink.
FIG. 15 illustrates an active electronically controllable micropolarizer based on electro-optical effect of liquid crystals.
Since its invention by E. Land in the 1930's, polyvinyl alcohol (PVA) has been the polarizer material of choice. It is available from several manufacturers including the Polaroid Corporation. It comes as rolls 19 inches wide and thousands of feet long. The PVA, which is 10 to 20 micron thick, is stretched 3 to 5 times original length and treated with iodine to give it its dichroic (polarizing) property. The PVA treated in this manner crystallizes and becomes brittle. The processes below employ certain chemical properties of the PVA. These are: i) resistance to organic solvents and oils; ii) water solubility, 30% water and 70% ethyl alcohol; iii) bleaching of the dichroic effect in hot humid atmosphere and by means of caustic solutions; iv) manifestation of dichroic effect by painting the PVA in iodine/potassium iodide solution; and v) the stabilization of the dichroic effect in boric acid solution. The starting PVA material comes laminated to a clear plastic substrate which protects the brittle PVA and facilitates handling and processing. The substrate is made either of cellulose aceto bytyrate (CAB) or cellulose triacetate (CTA), and is typically 50 to 125 micron thick. CAB and CTA are ultra-clear plastics and at the same time they are good barriers against humidity. For some applications, large glass plates are also used as substrates. Although other polymers, when stretched and treated by dichroic dyes, exhibit similar optical activity to that of PVA and may be fabricated into micropolarizers following the methods taught here, only PVA is considered in the manufacturing processes described in the present invention.
The physical principles on which the polarization of light and other electromagnetic waves, and the optical activity which produces phase retardation (quarter wave and half wave retarders) are described in books on optics, such as: M. Born and E. Wolf, Principles of Optics Pergamon Press, London, fourth edition, 1970; F. S. Crawford, Jr., Waves McGraw-Hill, New York, 1968; and M. V. Klein, Optics, Wiley, New York, 1970. There are several important facts used in this invention:
1. Two linear polarizers with their optical axis 90 degrees from each other extinguish light.
2. A linear polarization which is 45 degrees from the optical axis of a quarter wave retarder is converted into a circular polarization.
3. A linear polarization which is 45 degrees from the optical axis of a half wave retarder is converted into a linear polarization rotated 90 degrees.
4. Two linear polarization states, P1 and P2, 90 degrees from each other, are converted into clockwise and counter-clockwise circular polarization states by means of a quarter waver retarder.
5. A circular polarization is converted into a linear polarization by means of a linear polarizer.
6. A clockwise circular polarization is converted into a counter-clockwise polarization by means of a half-wave retarder.
The process for producing the micropolarizers, μPols, 1, 2 in FIG. 1 is described in FIG. 2 which starts with a sheet of linear polarizer 5 laminated onto a clear substrate 4. The laminate is coated with photosensitive material 6 called photoresist. This can be one of several well known liquid photoresists marketed by Eastman Kodak and Shipley, or in the form of a dry photoresist sheet called Riston from the Du Pont Company. The latter is preferred because complete laminated rolls of the three materials 3, 5, 6 can be produced and used to start the μPols process. The photoresist is subsequently exposed and developed using a mask having the desired pattern of the μPols cell 3 producing a pattern with polarization parts protected with the photoresist 6 and unprotected parts 7 exposed for further treatment. These exposed parts 7 are treated for several seconds with a caustic solution, e.g., a solution of potassium hydroxide. This bleaching solution removes the dichroic effect from the PVA so that the exposed parts 8 are no longer able to polarize light. The photoresist is removed by known strippers, which have no bleaching effect, thus the first part 9 of the μPols fabrication is produced.
Alternatively, FIG. 3 shows a method for making linear μPols by starting with a laminate of PVA 10 which is stretched but does not yet have the dichroic effect, i.e., it has not yet been treated with iodine, and the substrate 4. Following identical steps as above, windows 7 are opened in the photoresist revealing part of the PVA. The next step is to treat the exposed parts with a solution of iodine/potassium iodide and subsequently with a boric acid stabilizing solution. The exposed parts 11 of the PVA become polarizers while those protected with the photoresist remain unpolarizers. Stripping the photoresist completes the first part of the process.
As illustrated in FIG. 4, a complete μPol is made using two parts 13, 14 produced by either the process of FIG. 2 or FIG. 3 except that part 13 has polarization axis oriented 90 degrees from that of part 14. The two parts are aligned 15 so that the patterned polarizer areas do not over lap, and then laminated together to from the final product 16. The μPol 16 is laminated with the PVA surfaces facing and in contact with each other. The μPol 17 is laminated with the PVA of part 13 is in contact with the substrate of part 14. The μPol 18 is laminated with the substrates of both parts are in contact with each other. Finally, it is possible to produce the μPol 19 with only one substrate onto which two PVA films are laminated and patterned according to the process described above.
The above process leaves the patterned PVA film in place and achieves the desired result by either bleaching it or treating it with iodine solution. The processes described in FIGS. 5 and 6 achieve the desired result by the complete removal of parts of the PVA. In FIG. 5, the starting material is any PVA film 20 (linear polarizer, quarter wave retarder, or half wave retarder) or any non-PVA optically active material laminated to a substrate. As described above, windows 7 in the photoresist are opened. The exposed PVA 7 is removed 21 by means of chemical etching (30% water/70% ethyl alcohol solution), photochemical etching, eximer laser etching or reactive ion etching. Stripping the photoresist, the first part 22 of the μPols process is completed.
The removal of PVA can also be accomplished by mechanical cutting or milling means. FIG. 6 illustrates the process which uses a diamond cutter 66 mounted on a motor driven shaft 74. In one embodiment, the PVA 68 is sandwiched between two polymers, such as poly-methyl methacrylate, PMMA, film 67, and the sandwich is laminated onto a substrate 69. The diamond saw is used to cut channels. The channel width and the distance between the channels are identical. The PMMA serves to protect the top PVA surface from abrasion and protects the substrate from being cut by the saw. Next the PMMA on top of the PVA and in the channel is dissolved away, leaving the part 71 with clean substrate surface 70. This part can be used as is to complete the μPol fabrication or the original substrate 69 is removed by dissolving away the rest of the PMMA, after having attached a second substrate 72. This part which consists of the patterned PVA 68 laminated to the substrate 72 is used in a subsequent step to complete the μPol.
Even though this process is mechanical in nature, it has been shown in Electronic Business, May 14, 1990, page 125, that channels and spacings as small as 5 micron can be made using diamond discs manufactured by Disco HI-TEC America Inc., of Santa Clara, Calif. Realizing that using only one disc makes the process slow and costly, the arrangement in FIG. 6 is used where many discs 73 in parallel 75 is preferred. Each disc has its center punched out in the shape of a hexagonal so that it can be mounted on a shaft 74 with a hexagonal cross section. Hundreds of such discs are mounted on the same shaft and are spaced apart by means of spacers 76 whose diameters are smaller than those of the discs. The diameter difference is used to control the cutting depth. The spacers also have hexagonal centers. The cutting discs and the spacers have the same thickness in order to obtain identical channel width and channel spacing. The discs and spacers are mounted on the shaft tightly to prevent lateral motion, while the hexagonal shaft prevents slipping. The discs are made to rotate between 20,000 and 50,000 RPM and the laminate is cut in continuous fashion, thus achieving high through put.
To complete making a whole μPol the parts 22, 71, 72 prepared by the PVA removal methods are used as in FIG. 7. If the PVA is a linear polarizer, then, parts 23, 24 have patterned polarizers which are oriented 90 degrees from each other, and when aligned 25, and laminated together, complete linear μPols 26,27,28, 29 result. If the PVA is quarter wave retarder, then the parts 30, 31 of FIG. 8 have patterned retarders with optical axes oriented 90 degrees from each other, and when aligned 32 and laminated to a sheet of linear polarizer 33, complete circular μPols 34, 35, 36 result.
Up until now all μPols have been made using two patterned parts aligned to each other and then laminated as in FIGS. 4, 7, and 8. It possible make μPols with a single patterned part 38 or 40 in FIGS. 9 and 10, and without the alignment step. In FIG. 9, the single patterned part 38 consists of a patterned half-wave retarder on a substrate 4. It is mounted simply on a sheet of polarizer 39 with no alignment necessary and a complete μPols results. If a linear polarizer sheet 39 is used, the result is a linear μPols. If a circular polarizer sheet 39 is used, the result is a circular μPols. In FIG. 10 the single patterned part 40 has a linear polarizer which is simply mounted on a circular polarizer sheet 41 to produce a complete μPols.
FIG. 11 shows the apparatus 42 used for contact printing of the laminate 46 made of photoresist, PVA, and its substrate. The apparatus consists of a vacuum box 47, and a vacuum pump 48 attached thereto. The top of box is flat surface with vacuum holes which hold the laminate flat during exposure. The mask 45 with its emulsion facing down, makes direct contact with the photoresist surface with the aid of the top glass cover 44. The very high intensity UV lamp 43 is then turned on for 30 to 60 seconds to expose the photoresist. The laminate is subsequently removed for development and the rest of the μPols fabrications processes as described in FIGS. 2, 3, and 5. This printing process using apparatus 46 is automated for large area μPols production as shown in FIG. 12. The laminate 46 is furnished in a large roll, is fed to apparatus 42 when the vacuum pump 48 is off and the mask and cover 44 are open. By means of an electronic controller, the following automatic sequences are carried out: (1) the vacuum is turned on; (2) the cover and mask are lowered; (3) the lamp is turned on for certain period of time; (4) the lamp is turned off; (5) the mask and cover are lifted; (6) the vacuum is turned off; and (7) the laminate is advanced. These steps are repeated until the whole roll is finished. The exposed roll 49 is then processed further. This exposure apparatus is simple and has no critical alignment requirements.
The fully automated embodiment in FIG. 13 is used for continuous mass production. The raw roll of laminate 46 enters from the right and the finished roll 56 of μPols exists from the left. As one laminate segment is exposed, it is advanced to the left, developed and rinsed in station 50. Said segment is then further advanced to the left to be dried in station 51, and advanced further to section 52. This station carries out the most critical μPols process by one of three methods discussed above in connection with FIGS. 2, 3, and 5. These are:
1. Bleaching by means of potassium hydroxide then rinsing.
2. Polarizing by means of iodine/potassium iodide solution, boric acid stabilizing solution, then water/methyl alcohol rinse.
3. Dry or wet etching of the PVA.
After the rinsing step in station 52, the segment is advanced to station 53 for drying and heat treatment. The photoresist stripping and rinsing is done in 54 and the final drying step in 55. The finished roll 56 is laminated with a polarizer sheet according to FIGS. 9 and 10 complete the μPols.
The photolithographic printing used above involves several steps:
1. Application of the photoresist
3. Making contact with the mask
8. Post baking
9. Stripping
10. Rinsing
11. Drying
These steps have been eliminated by using the mechanical method described in FIG. 6. They are also completely eliminated by using the embodiment illustrated in FIG. 14. This apparatus 57 promises to be the least expensive high volume manufacturing process for μPols. It consists of a plate drum 58 to which a plate a fixed, a blanket drum 59 which has a rubber surface, and an impression drum 60. The inks from ink fountains 62, 65, are transferred to the plate by means of rollers 63, 64. The pattern is transferred from the plate to the blanket drum which in turn it transfers to the PVA laminate 61. The rotation of the blanket drum and the impression drums draws in the laminate, and blanket rubber surface pressing on the laminate causes proper printing. Although the hardware is similar to that used in offset printing press, the process is different from offset printing. The principal difference is in the ink formulation. In offset printing slightly acidic water is used in fountain 65, and an oil-based paint (linseed oil, pigments, binder, and other additives) is used in fountain 62. These are not intended to interact with the paper. The pigments in the oil based solution will remain bonded to the paper, and the water evaporates. In the μPols printing process, on the other hand, the oil based solution is clear and is not intended to remain, while the water based solution is intended to interact with the PVA and permanently modify it, by bleaching it or by endowing it with the dichroic property. Another difference is the use of the negative image on the plate to print a positive image of the pattern on the PVA laminate, whereas in the offset printing, the opposite occurs. The plates are made by means which are well known in the offset printing industry.
The μPols process using apparatus 57 has three embodiments which depend on the content of the water based solutions in fountain 65, while fountain 62 contains a fast drying clear oil solution:
1. Selective Bleaching: The water based solution contains a bleaching agent such as potassium hydroxide or sodium hydroxide which applied selectively as pattern on the polarized PVA. Where applied, the solution removes the iodine and its polarizing effect. Rinsing and drying steps follow this bleaching step.
2. Selective Dichroism: The water based solution contains a iodine/potassium iodide which is applied selectively as a pattern on the unpolarized PVA. Where applied, the solution turns the PVA into a polarizer. This step is followed by a stabilizing step using a boric acid solution and subsequently rinsing using a methyl alcohol solution and drying steps.
3. Selective Etching: The water based solution contains a clear polymer which is applied selectively as a pattern on the polarized or unpolarized PVA. Where applied, the solution leaves a protective polymer layer. This step is followed by an etching step to remove the unprotected PVA, by rinsing and drying steps.
Electrically Controllable Micropolarizers
There are applications in which a variable μPols are needed, and in particular, μPols which are electronically alterable. This can be accomplished by using electro-optical materials such as liquid crystals or organic nonlinear optical polymers, see C. C. Teng and H. T. Man, Applied Physics Letters, 30, 1734 (1990), or magneto-optical materials which have large Faraday rotation. All these materials rotate the polarization of incident radiations by applying voltages or magnetic fields. The preferred embodiment 77 in FIG. 15 uses a twisted nematic liquid crystal 78 which rotates the polarization 90 degrees by applying a voltage alternating at 10 to 20 KHz and having an RMS value of about 10 volts. This voltage is applied between the checker-board patterned transparent electrode made of indium-tin oxide ITO 82 on a glass substrate 80 and an unpatterned ground ITO layer 81 deposited on a second glass substrate 79. The patterned ITO 82 are connected to a common voltage bus 85. Each connection 86 is made of aluminum film whose area is a small percentage of the ITO area, in the order of 10%. Thus we created two types of cells: One type which has liquid crystal and ITO 81, 82 on both sides, will be affected by the applied electric field; and the other type which has liquid crystal but has ITO 81 on one side only and hence will not be affected by the applied electric field. The polarizer sheet 83 with polarization state P1 is laminated to the glass substrate 80 completes the electronic μPols.
The operating principles of electronically switchable μPols is as follows: When the voltage 84 is zero, the polarization P1 of the incident light will not change. When a voltage is applied, the cells with ITO on both sides will rotate the polarization to a state P2, while the cells with ITO on one side only leave the polarization P1 unchanged. The end result is a regular periodic array of cells with two polarization states P1 and P2. This is a μPol that can be turned off and on.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS1435520 *Mar 2, 1921Nov 14, 1922Teleview CorpStereoscopic motion pictureUS2099694 *Mar 6, 1934Nov 23, 1937Sheet Polarizer Company IncPolarizing optical systemUS2417446 *Aug 1, 1941Mar 18, 1947Bell Telephone Labor IncStereotelevision and television range findingUS2647440 *Aug 8, 1947Aug 4, 1953Miles P RehornMolecularly aligned sheet materialUS2810318 *Aug 17, 1953Oct 22, 1957Dockhorn Wayne AStereoscopic apparatusUS3371324 *Nov 25, 1964Feb 27, 1968Sinoto NoriLight-modulating information storage and retrieval system and methodUS3741626 *Aug 18, 1971Jun 26, 1973Westinghouse Electric CorpCommunicationUS3821466 *May 25, 1973Jun 28, 1974Roese JLiquid crystal stereoscopic television systemUS4281341 *Oct 24, 1979Jul 28, 1981The Marconi Company LimitedStereoscopic television systemUS4523226 *Jan 19, 1983Jun 11, 1985Stereographics CorporationStereoscopic television systemUS4562463 *May 15, 1981Dec 31, 1985Stereographics Corp.Stereoscopic television system with field storage for sequential display of right and left imagesUS4719507 *Apr 26, 1985Jan 12, 1988Tektronix, Inc.Stereoscopic imaging system with passive viewing apparatusUS4743965 *May 6, 1986May 10, 1988Nippon Hoso KyokaiStereoscopic television picture transmission systemUS4902112 *Apr 17, 1986Feb 20, 1990Lowe Gregory EVariable density light transmitting deviceUS4936656 *Mar 18, 1988Jun 26, 1990Matsushita Electric Industrial Co., Ltd.Video projector* Cited by examinerNon-Patent CitationsReference1 *E. H. Land, J. Opt. Soc. of America 28, 30, 230 (1940).2 *F. S. Crawford, Jr., Waves, McGraw Hill, New York 1968.3F. S. Crawford, Jr., Waves, McGraw-Hill, New York 1968.4 *G. B. Trapani, editor, SPIE Polarizers and Applications, vol. 307, 1981.5 *Hartmann and Hikspoors, Information Displays, 3, 15 (1987).6 *J. S. Lipscomb, Proc. SPIE, 1083, 28 (1989).7 *L. F. Hodges and D. F. McAllister, Information Displays, 5, 18 (1987).8 *L. F. Hodges et al, Information Displays, 3, 9 (1987).9 *L. Lipton Proc. SPIE, 1083, 85 (1989).10 *L. Lipton, Foundations of the Stereoscopic Cinema, Van Nostrand Reinhold, New York, 1982.11 *M. Born and E. Wolf, Principles of Optics, Pergamon Press, London, fourth edition, 1970.12 *M. C. King and D. H. Berry, Appl. Opt., 9, Sep. 1970.13 *M. C. King, A. M. Knoll and D. H. Berry, A New Approach To Computer Generated Holography, Appl. Optics, Feb. 9, 1970.14M. C. King, A. M. Knoll and D. H. Berry, A New Approach To Computer-Generated Holography, Appl. Optics, Feb. 9, 1970.15 *M. V. Klein, Optics, Wiley, New York, 1970.16 *P. Bos et al., SID Digest, 19, 450 (1988).17 *R. D. Williams and F. Garcia Jr., SID Digest, 19, 91 (1988).18 *T. Okoshi, Three Dimensional Imaging Techniques, Academic Press, New York, 1976.19T. Okoshi, Three-Dimensional Imaging Techniques, Academic Press, New York, 1976.20 *V. Walwarth et al, SPIE Optics in Entertainment, vol. 462, 1984.21 *W. Robbins and S. Fisher, editors, Three Dimensional Visualization and Display Technologies, Proc. SPIE, 1083, (1989).22W. Robbins and S. Fisher, editors, Three-Dimensional Visualization and Display Technologies, Proc. SPIE, 1083, (1989).* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS5548427 *Jan 20, 1995Aug 20, 1996Sharp Kabushiki KaishaSwitchable holographic apparatusUS5638082 *Oct 25, 1993Jun 10, 1997Carl-Zeiss StiftungVision testing system for stereoscopic viewing by a test personUS5717522 *Jul 24, 1995Feb 10, 1998Fuji Photo Optical Co., Ltd.Polarizing films used for optical systems and three-dimensional image displaying apparatuses using the polarizing filmsUS5751389 *Feb 13, 1995May 12, 1998Sumitomo Chemical CompanyFilm containing oriented dye, method of manufacturing the same, and polarizer and liquid crystal display unit utilizing the sameUS5841581 *Mar 5, 1996Nov 24, 1998Eastman Kodak CompanyMethod and apparatus for making a spatially selective high resolution light filterUS5844717 *Sep 12, 1995Dec 1, 1998Reveo, Inc.Method and system for producing micropolarization panels for use in micropolarizing spatially multiplexed images of 3-D objects during stereoscopic display processesUS5861931 *Oct 9, 1996Jan 19, 1999Sharp Kabushiki KaishaPatterned polarization-rotating optical element and method of making the same, and 3D displayUS5917562 *Dec 15, 1995Jun 29, 1999Sharp Kabushiki KaishaAutostereoscopic display and spatial light modulatorUS5991074 *Jan 29, 1998Nov 23, 1999Canon Kabushiki KaishaStereoscopic image display apparatusUS6046849 *Sep 12, 1997Apr 4, 2000Sharp Kabushiki KaishaParallax barrier, display, passive polarisation modulating optical element and method of making such an elementUS6055103 *Jun 26, 1998Apr 25, 2000Sharp Kabushiki KaishaPassive polarisation modulating optical element and method of making such an elementUS6061043 *Feb 18, 1997May 9, 2000Sharp Kabushiki KaishaLiquid crystal display having grey levels with reduced variations due to temperature and liquid crystal variationsUS6072566 *Jul 2, 1997Jun 6, 2000Sharp Kabushiki KaishaOptical rotary device and manufacturing method thereof and image display device using thereofUS6075235 *Jan 2, 1998Jun 13, 2000Chun; Cornell Seu LunHigh-resolution polarization-sensitive imaging sensorsUS6075506 *Feb 18, 1997Jun 13, 2000Sharp Kabushiki KaishaDisplay and method of operating a displayUS6188451Apr 12, 2000Feb 13, 2001Sharp Kabushiki KaishaOptical rotary device and manufacturing method thereof and image display device using thereofUS6188460 *Sep 16, 1996Feb 13, 2001Reveo, Inc.Image display panel having a backlighting structure and a single-layer pixelated aray of reflective-type spectral filtering elements where between light is recycled for producing color images with enhanced brightnessUS6333773 *Sep 16, 1997Dec 25, 2001Reveo, Inc.Image display panel employing a broad-band polarizing/reflective backlighting structure and a pixelated array of reflective-type of filtering elementsUS6359664 *Jul 11, 1996Mar 19, 2002Reveo, Inc.Electro-optical display system for visually displaying polarized spatially multiplexed images of 3-D objects for use in stereoscopically viewing the same with high image quality and resolutionUS6384971 *Nov 19, 1998May 7, 2002Reveo, Inc.Methods for manufacturing micropolarizersUS6417899 *Aug 31, 1999Jul 9, 2002Guardian Industries Corp.Liquid crystal display with internal polarizer and method of making sameUS6437915Feb 10, 2000Aug 20, 2002Sharp Kabushiki KaishaParallax barrier, display, passive polarization modulating optical element and method of making such an elementUS6496239Jul 17, 2001Dec 17, 2002Rolic AgOptical component for producing linearly polarized lightUS6498679Dec 21, 2000Dec 24, 2002Industrial Technology Research InstituteMicro-retarder plateUS6541185Sep 20, 2000Apr 1, 2003Japan Chemical Innovation InstituteMicropattern polarized elementUS6542296Dec 21, 2000Apr 1, 2003Industrial Technology Research InstituteBack-lighted autostereoscopic displayUS6559903Feb 27, 1998May 6, 2003Reveo, Inc.Non-absorptive electro-optical glazing structure employing composite infrared reflective polarizing filterUS6573961May 17, 1999Jun 3, 2003Reveo, Inc.High-brightness color liquid crystal display panel employing light recycling thereinUS6583827Jul 15, 1999Jun 24, 2003Reveo, Inc.Electro-optical glazing structures having bi-directional control of electromagnetic radiation during total-reflection, semi-transparent and totally-transparent modes of operationUS6587168 *Apr 3, 2002Jul 1, 2003Guardian Industries Corp.Liquid crystal display with internal polarizer and method of making sameUS6624863Jun 26, 1998Sep 23, 2003Sharp Kabushiki KaishaMethod of making a patterned retarder, patterned retarder and illumination sourceUS6633354Jun 7, 1999Oct 14, 2003Reveo, Inc.Spectrum-controllable reflective polarizers having electrically-switchable modes of operationUS6671008Apr 6, 2000Dec 30, 2003Reveo, Inc.Electro-optical glazing structures having scattering and transparent modes of operation and methods and apparatus for making the sameUS6710823Nov 6, 2001Mar 23, 2004Reveo, Inc.Electro-optical glazing structures having reflection and transparent modes of operationUS6738114Nov 4, 1997May 18, 2004Reveo, Inc.Liquid crystal film structures with phase-retardation surface regions formed thereinUS6816207Dec 27, 2001Nov 9, 2004Lg.Philips Lcd Co., Ltd.Autostereoscopic display apparatus and method of manufacturing the sameUS6897936Apr 6, 2000May 24, 2005Inventqjaya Sdn. BhdElectro-optical glazing structures having scattering and transparent modes of operationUS6977695Aug 26, 2003Dec 20, 2005Reveo, Inc.Variable optical attenuator based on electrically switchable cholesteric liquid crystal reflective polarizersUS7002642Jul 7, 2004Feb 21, 2006Lg.Philips Lcd Co., Ltd.Autostereoscopic display apparatus and method of manufacturing the sameUS7230717May 4, 2004Jun 12, 20074D Technology CorporationPixelated phase-mask interferometerUS7327418May 16, 2006Feb 5, 2008Nitto Denko CorporationTechnological machinery for production of polarizersUS7385669 *Mar 21, 2005Jun 10, 2008Vrex, Inc.Twisted nematic micropolarizer and its method of manufacturingUS7411677 *Jan 23, 2004Aug 12, 2008Photonic Lattice Inc.Driverless ellipsometer and ellipsometryUS7582857Apr 18, 2006Sep 1, 2009The Trustees Of The University Of PennsylvaniaSensor and polarimetric filters for real-time extraction of polarimetric information at the focal planeUS7736708Mar 29, 2005Jun 15, 2010National Institute Of Advanced Industrial Science And TechnologyMicropattern retardation elementUS7791686Sep 7, 2010Waterstrike IncorporatedLCD-based confidential viewing apparatus utilizing auto-inversion maskingUS7796134May 31, 2005Sep 14, 2010Infinite Z, Inc.Multi-plane horizontal perspective displayUS7907167Mar 15, 2011Infinite Z, Inc.Three dimensional horizontal perspective workstationUS7969541Jun 28, 2011Sony CorporationRetardation film, method of manufacturing the same, and displayUS8045163Jun 22, 2006Oct 25, 2011Gunter GrauMethod for producing polarisation filters and use of polarisation-sensitive photo-sensors and polarisation-generating reproduction devicesUS8062836Feb 2, 2010Nov 22, 2011Lg Chem, Ltd.Method for manufacturing an optical filter for a stereoscopic image display deviceUS8323538 *Nov 27, 2007Dec 4, 2012Nitto Denko CorporationMethod for producing polarizerUS8502110Aug 8, 2008Aug 6, 2013Industrial Technology Research InstituteMultibeam laser device for fabricating a microretarder by heating processUS8520176Feb 1, 2012Aug 27, 2013Industrial Technology Research InstituteStereoscopic display module, method for manufacturing the same and manufacturing system thereofUS8525970May 20, 2010Sep 3, 2013The Hong Kong University Of Science And TechnologyPhoto-aligned liquid-crystal micropolarimeter array and its manufacturing methodUS8643050 *Oct 6, 2010Feb 4, 2014Nec CorporationLight emitting element and image display apparatus using the light emitting elementUS8648982 *Feb 18, 2011Feb 11, 2014Fujifilm CorporationOptical film, polarizing plate and liquid crystal display deviceUS8717360Jun 10, 2010May 6, 2014Zspace, Inc.Presenting a view within a three dimensional sceneUS8717423Feb 2, 2011May 6, 2014Zspace, Inc.Modifying perspective of stereoscopic images based on changes in user viewpointUS8754994Apr 26, 2012Jun 17, 2014Fujifilm CorporationPatterned polarization plate, image display apparatus and image display systemUS8786529May 18, 2011Jul 22, 2014Zspace, Inc.Liquid crystal variable drive voltageUS8866172 *Oct 6, 2010Oct 21, 2014Nec CorporationLight emitting element and image display apparatus using the light emitting elementUS9097858Jun 29, 2011Aug 4, 20153M Innovative Properties CompanyRetarder film combinations with spatially selective birefringence reductionUS9101956Jun 29, 2011Aug 11, 20153M Innovative Properties CompanyMask processing using films with spatially selective birefringence reductionUS9134556Jul 18, 2014Sep 15, 2015Zspace, Inc.Liquid crystal variable drive voltageUS9164322Jul 30, 2012Oct 20, 2015Sony CorporationDisplay unitUS9202306May 2, 2014Dec 1, 2015Zspace, Inc.Presenting a view within a three dimensional sceneUS9259906Feb 23, 2012Feb 16, 2016Sony CorporationOptical laminated body, method of manufacturing the same, and display unitUS9292962May 2, 2014Mar 22, 2016Zspace, Inc.Modifying perspective of stereoscopic images based on changes in user viewpointUS20030137626 *Dec 18, 2002Jul 24, 2003Marina KhazovaMethod of making a passive patterned retarder and retarder made by such a methodUS20040141120 *Aug 26, 2003Jul 22, 2004Faris Sadeg M.Variable optical attenuator based on electrically switchable cholesteric liquid crystal reflective polarizersUS20040239835 *Jul 7, 2004Dec 2, 2004Jin-Hee JungAutostereoscopic display apparatus and method of manufacturing the sameUS20040263974 *Jun 26, 2003Dec 30, 2004Optical Coating Laboratory Inc., A Jds Unipahse Company And A Corporation Of The State Of DelwareFlat polarization conversion system with patterned retarderUS20050046865 *May 4, 2004Mar 3, 2005Brock Neal J.Pixelated phase-mask interferometerUS20050153079 *Dec 22, 2004Jul 14, 2005Nitto Denko CorporationMethod of manufacturing laminated polarizing plate, laminated polarizing plate obtained by the method, and image display including the sameUS20050219695 *Apr 4, 2005Oct 6, 2005Vesely Michael AHorizontal perspective displayUS20050247958 *Mar 21, 2005Nov 10, 2005Zongkai WangTwisted nematic micropolarizer and its method of manufacturingUS20050264559 *May 31, 2005Dec 1, 2005Vesely Michael AMulti-plane horizontal perspective hands-on simulatorUS20050264857 *May 31, 2005Dec 1, 2005Vesely Michael ABinaural horizontal perspective displayUS20050264858 *May 31, 2005Dec 1, 2005Vesely Michael AMulti-plane horizontal perspective displayUS20050275915 *May 31, 2005Dec 15, 2005Vesely Michael AMulti-plane horizontal perspective displayUS20050281411 *May 31, 2005Dec 22, 2005Vesely Michael ABinaural horizontal perspective displayUS20060050389 *Jan 11, 2005Mar 9, 2006Hynix Semiconductor Inc.Polarizing reticleUS20060126927 *Nov 28, 2005Jun 15, 2006Vesely Michael AHorizontal perspective representationUS20060215080 *May 16, 2006Sep 28, 2006Nitto Denko CorporationTechnological machinery for production of polarizersUS20060216615 *Mar 28, 2005Sep 28, 2006Michael GoldsteinWavefront engineering with off-focus mask featuresUS20060250391 *May 8, 2006Nov 9, 2006Vesely Michael AThree dimensional horizontal perspective workstationUS20060252978 *May 8, 2006Nov 9, 2006Vesely Michael ABiofeedback eyewear systemUS20060252979 *May 8, 2006Nov 9, 2006Vesely Michael ABiofeedback eyewear systemUS20060269437 *May 31, 2005Nov 30, 2006Pandey Awadh BHigh temperature aluminum alloysUS20070040905 *Aug 7, 2006Feb 22, 2007Vesely Michael AStereoscopic display using polarized eyewearUS20070043466 *Aug 7, 2006Feb 22, 2007Vesely Michael AStereoscopic display using polarized eyewearUS20070134442 *Mar 29, 2005Jun 14, 2007Daisaku MatsunagaMicropattern retardation elementUS20070195271 *Mar 22, 2005Aug 23, 2007Koninklijke Philips Electronics, N.V.Projection system with scanning deviceUS20070241267 *Apr 18, 2006Oct 18, 2007The Trustees Of The University Of PennsylvaniaSensor and polarimetric filters for real-time extraction of polarimetric information at the focal plane, and method of making sameUS20070268490 *Jan 23, 2004Nov 22, 2007Photonic Lattice Inc.Ellipsometer and EllipsometryUS20070296889 *Jun 23, 2006Dec 27, 2007Waterstrike IncorporatedLCD-based confidential viewing apparatus utilizing auto-inversion maskingUS20080144967 *Mar 30, 2005Jun 19, 2008Waterstrike IncorporatedConfidential Viewing System Utilizing Spatial MultiplexingUS20090051058 *Nov 27, 2007Feb 26, 2009Nitto Denko CorporationMethod for producing polarized, polarizer, polarizing plate, optical film, and image display deviceUS20090159578 *Aug 8, 2008Jun 25, 2009Industrial Technology Research InstituteMultibeam laser device for fabricating a microretarder by heating processUS20090219465 *Feb 29, 2008Sep 3, 2009Infinite Z, Inc.Polarizing Display DeviceUS20100073604 *Sep 22, 2009Mar 25, 2010Sony CorporationRetardation film, method of manufacturing the same, and displayUS20100118398 *Jun 22, 2006May 13, 2010Gunter GrauMethod for producing polarisation filters and use of polarisation-sensitive photo-sensors and polarisation-generating reproduction devicesUS20100296039 *May 20, 2010Nov 25, 2010The Hong Kong University Of Science And TechnologyPhoto-aligned liquid-crystal micropolarimeter array and its manufacturing methodUS20110122130 *May 26, 2011Vesely Michael AModifying Perspective of Stereoscopic Images Based on Changes in User ViewpointUS20110187706 *Jun 10, 2010Aug 4, 2011Vesely Michael APresenting a View within a Three Dimensional SceneUS20110217638 *Feb 2, 2010Sep 8, 2011Kim Sin-YoungMethod for manufacturing an optical filter for a stereoscopic image display deviceUS20110236681 *Sep 29, 2011Lg Chem, Ltd.Pressure sensitive adhesive film for an orientating treatment in a photo-orientable layerUS20120081784 *Apr 5, 2012Crysoptix KkPatterned retarderUS20120199855 *Oct 6, 2010Aug 9, 2012Nec CorporationLight emitting element and image display apparatus using the light emitting elementUS20120217529 *Oct 6, 2010Aug 30, 2012Nec CorporationLight emitting element and image display apparatus using the light emitting elementUS20120320316 *Feb 18, 2011Dec 20, 2012Fujifilm CorporationOptical film, polarizing plate and liquid crystal display deviceUS20150208061 *Jan 21, 2014Jul 23, 2015Chih-Ming YangThree-dimensional display deviceUSRE37752Jan 22, 1998Jun 18, 2002Equinox CorporationPolarization viewerCN102576791A *Oct 6, 2010Jul 11, 2012日本电气株式会社Light emitting element and image display device using the light emitting elementCN102576791B *Oct 6, 2010Nov 19, 2014日本电气株式会社Light emitting element and image display device using the light emitting elementCN103760681A *Jan 21, 2014Apr 30, 2014国家纳米科学中心Method for manufacturing micro-polarizer array based on metal nanometer gratingCN103969840A *Jan 25, 2013Aug 6, 2014中国科学技术大学Micro polaroid array on basis of metal nanometer optical gratings and preparation method thereofDE102005031966A1 *Jul 8, 2005Jan 18, 2007Grau, G�nter, Dr.-Ing.Herstellung von Polarisationsfiltern sowie entsprechende AnwendungenDE102005031966B4 *Jul 8, 2005Oct 27, 2011G�nter GrauHerstellung eines polarisationsempfindlichen Filters mit gezielter Ausdehnung und Orientierung f�r CCD- oder CMOS-BildsensorenDE102005063524B4 *Jul 8, 2005Jan 27, 2011Grau, G�nter, Dr.Vorrichtung zur Messung und Erzeugung der Polarisation von LichtEP0887667A2 *Jun 29, 1998Dec 30, 1998Sharp CorporationMethod of making a patterned retarder, patterned retarder and illumination sourceEP1174738A2 *Jul 11, 2001Jan 23, 2002Optiva, Inc.Technological machinery for production of polarizersWO1996007941A1 *Sep 8, 1995Mar 14, 1996Sumitomo Chemical Company, LimitedFilm containing oriented dye, method of manufacturing the same, and polarizer and liquid crystal display unit utilizing the sameWO2010032540A1Jul 14, 2009Mar 25, 2010Sony CorporationPhase difference plate, method of manufacturing same, and display deviceWO2010090429A2Feb 2, 2010Aug 12, 2010Lg Chem, Ltd.Method for manufacturing an optical filter for a stereoscopic image display deviceWO2015199213A1 *Jun 26, 2015Dec 30, 2015日東電工株式会社Method for producing long adhesive filmWO2015199214A1 *Jun 26, 2015Dec 30, 2015日東電工株式会社Long adhesive filmWO2015199215A1 *Jun 26, 2015Dec 30, 2015日東電工株式会社Long polarizer, long polarizing plate, and image display deviceWO2015199216A1 *Jun 26, 2015Dec 30, 2015日東電工株式会社Long polarizer film laminateWO2015199217A1 *Jun 26, 2015Dec 30, 2015日東電工株式会社Method for manufacturing long polarizer* Cited by examinerClassifications U.S. Classification359/486.02, 348/E05.141, 348/E05.145, 359/489.07, 359/487.02International ClassificationG06F1/16, G02B27/00, G03B21/132, H04N5/74, G06F3/01, G02B27/26, G06F3/033, G06F3/00, G06F3/048Cooperative ClassificationH04N5/7491, G02B27/26, G02B27/0093, G03B21/132, G06F3/011, H04N5/7441European ClassificationG06F3/0488, G03B21/132, G02B27/00T, G06F3/01B, G02B27/26Legal EventsDateCodeEventDescriptionDec 31, 1997FPAYFee paymentYear of fee payment: 4May 6, 1998ASAssignmentOwner name: REVEO, INC., NEW YORKFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:FARIS, SADEG M.;REEL/FRAME:009158/0655Effective date: 19980427Jan 7, 2002FPAYFee paymentYear of fee payment: 8Jan 30, 2002REMIMaintenance fee reminder mailedMay 27, 2003ASAssignmentOwner name: ARISAWA MANUFACTURING CO., LTD., JAPANFree format text: LOAN AND SECURITY AGREEMENT;ASSIGNOR:VREX INCORPORATION;REEL/FRAME:014102/0766Effective date: 20030324Jan 18, 2006REMIMaintenance fee reminder mailedJun 9, 2006FPAYFee paymentYear of fee payment: 12Jun 9, 2006SULPSurcharge for late paymentYear of fee payment: 11RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services