US10046524B2 - Substrate for additive manufacturing - Google Patents
Substrate for additive manufacturing Download PDF
US10046524B2
US10046524B2 US14/386,742 US201314386742A US10046524B2 US 10046524 B2 US10046524 B2 US 10046524B2 US 201314386742 A US201314386742 A US 201314386742A US 10046524 B2 US10046524 B2 US 10046524B2
Active, expires 2035-05-16
US14/386,742
US20150054193A1 (en
2012-03-21 Priority to GB1204922.7A priority Critical patent/GB2500412A/en
2012-03-21 Priority to GB1204922.7 priority
2013-03-18 Application filed by Airbus Operations Ltd filed Critical Airbus Operations Ltd
2013-03-18 Priority to PCT/GB2013/050686 priority patent/WO2013140146A1/en
2015-01-21 Assigned to AIRBUSGROUP LIMITED reassignment AIRBUSGROUP LIMITED ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: MEYER, JONATHAN
2015-02-26 Publication of US20150054193A1 publication Critical patent/US20150054193A1/en
2018-08-14 Publication of US10046524B2 publication Critical patent/US10046524B2/en
2035-05-16 Adjusted expiration legal-status Critical
239000000758 substrates Substances 0 abstract claims description title 135
230000000996 additive Effects 0 abstract claims description title 44
239000000654 additives Substances 0 abstract claims description title 44
238000004519 manufacturing process Methods 0 abstract claims description 42
239000000843 powders Substances 0 claims description 38
238000005245 sintering Methods 0 claims description 11
238000009760 electrical discharge machining Methods 0 description 6
B29L2031/757—Moulds, cores, dies
A substrate for an additive manufacturing process, the substrate having a build surface for fusing to a part being formed on the substrate by the additive manufacturing process, wherein the substrate is configured to provide relatively high stiffness in a direction substantially perpendicular to the build surface, while having a low longitudinal stiffness in the plane of the build surface. Also, a method of forming the substrate, a system including the substrate, and use of the system for creating a part by an additive manufacturing process.
The present application is a National Phase of International Application Number PCT/GB2013/050686, filed Mar. 18, 2013, and claims priority from Great Britain Application Number 1204922.7, filed Mar. 21, 2012.
The present invention relates to a substrate for an additive manufacturing process, a method of forming the substrate, a system including the substrate, and use of the system for creating a part by an additive manufacturing process.
Additive manufacturing is a process by which an article is produced by joining materials together. Additive layer manufacturing (ALM) involves producing the article layer by layer using 3D model data. The process may be used for producing prototypes, samples, models, tooling or full scale components.
A known ALM technique uses a power beam, such as a laser or an electron beam for example, to selectively sinter powdered material. A layer of the powdered material is laid over a substrate (also known as a build plate, start plate, start platform or build platform) in a sintering chamber to provide a “powder bed”. The powder is applied using a re-coating blade. The power beam is used to selectively sinter the powder in a desired pattern by scanning across the surface of the powder bed. The power beam is controlled to produce the desired pattern according to cross-sections generated from 3D model data (e.g. a CAD file) of the article.
After each cross-section is scanned and the melted powder has solidified, the substrate is lowered by one layer thickness (typically of the order of 0.1 mm) to prepare for growth of the next layer. Another layer of the powder is applied on top of the preceding layer in preparation for sintering. The process is repeated until the article is completed. Thus as the process proceeds, a sintered article is constructed, supported by unconsolidated powder. After the article has been completed it is removed from the substrate and the unconsolidated powder is typically recycled to produce another article by the same ALM process.
Selective sintering may be used to produce shaped articles from powders of some metals, ceramics, glasses and thermoplastic polymers.
Due to the thermal energy involved in sintering the powder it is generally necessary to constrain the article during the build against thermal residual stresses which tend to make the article curl up, clashing with the re-coating blade and causing the build to fail. The article is generally constrained by fusing it to the substrate. In conventional processing a thick, solid substrate is used and the first layer of powder is fused to this, with subsequent layers being built on top. The fusion to the substrate provides the desired constraint in the z-axis (through layers) but also applies an additional constraint in the x-y plane, resulting in high residual stresses in the article which cannot be relieved during the build process. This can lead to bending of the substrate, and distortion and cracking of the article.
Currently, there are some ALM processes that make use of either a heated sintering chamber, or a heated substrate in order to reduce the level of differential shrinkage between the article and the substrate. This can reduce the level of residual stress, but has other drawbacks. The heated nature of the process results in a significant increase in system complexity, requiring heat shielding of sensitive electronics. It also changes the environment of the process, changing cooling characteristics which can be advantageous for some alloys, but can have a severe detrimental effect on other, e.g. Scalmalloy™, which requires fast solidification and high cooling rates.
A first aspect of the invention provides a substrate for an additive manufacturing process, the substrate having a build surface for fusing to a part being formed on the substrate by the additive manufacturing process, wherein the substrate is configured to provide relatively high stiffness in a direction substantially perpendicular to the build surface, whilst having a low longitudinal stiffness in the plane of the build surface.
A further aspect of the invention provides a substrate for an additive manufacturing process, the substrate having a build surface for fusing to a part being formed on the substrate by the additive manufacturing process, wherein the substrate has an upper portion nearest the build surface and a lower portion, and wherein the upper portion includes an array of protrusions with their longitudinal axis aligned substantially perpendicular to the build surface.
A further aspect of the invention provides a substrate for an additive manufacturing process, the substrate having a build surface for fusing to a part being formed on the substrate by the additive manufacturing process, and one or more slits extending from the build surface through part of the thickness of the substrate.
A further aspect of the invention provides a substrate for an additive manufacturing process, the substrate having a build surface for fusing to a part being formed on the substrate by the additive manufacturing process, wherein the substrate has an upper portion nearest the build surface and a lower portion, and wherein the upper portion includes a different material to that of the lower portion.
A further aspect of the invention provides a system for creating a part by an additive manufacturing process, the system including a substrate in accordance with one or more aspects of the invention.
A further aspect of the invention provides a method of forming a substrate for an additive manufacturing process, comprising providing a plate, and cutting one or more slits extending from the upper surface of the plate through part of the thickness of the plate.
A further aspect of the invention provides a method of forming a substrate for an additive manufacturing process, comprising using an additive manufacturing process to form a substrate having an upper portion and a lower portion, wherein the upper portion includes an array of upstanding protrusions.
A further aspect of the invention provides use of a system according to the invention for creating a part by an additive manufacturing process.
The invention is advantageous in that the substrate allows high strain deformation in the plane of the build surface, but retains high stiffness in the direction of the build, i.e. perpendicular to the build surface. This effectively creates a sliding constraint at the interface between the substrate and the part being formed by the additive manufacturing process, allowing the part to shrink in the plane of the build surface and thereby avoiding the build up of large residual stresses. Preferred embodiments of the invention provide various ways in which this can be achieved.
The substrate may have an upper portion nearest the build surface and a lower portion, wherein the upper portion includes a different construction and/or material to that of the lower portion.
Where the upper portion includes an array of protrusions, the protrusions may be arranged to deform like beams in the plane of the build surface, whilst being substantially rigid in the direction perpendicular to the build surface.
The tops of the protrusions may provide at least a portion of the build surface. The entire upper portion of the substrate may comprise the protrusions, in which case the tops of the protrusions may provide the entire build surface. Alternatively, the protrusions may be provided on only a portion of the build surface. The remainder of the build surface may be solid. It may be advantageous to provide the protrusions only at those regions of the build surface upon which the part is to be built.
The bases of the protrusions may be integrally formed with the lower portion of the substrate. For example, the substrate may be a monolith. Alternatively, each protrusion, or an array of protrusions, may be attached to the lower portion of the substrate, e.g. by fastening. This may allow for use of a common lower portion with one of a plurality of different upper portions than can be exchanged.
The protrusions may be slender, preferably having an aspect ratio of at least 3. The aspect ratio is the ratio of the height of the protrusion vs. its width/depth. The larger the aspect ratio of the protrusions, for a given material, the greater their ability to deform as beams in the plane of the build surface. The aspect ratio may be in the range 3 to 10, preferably 4 to 8, and most preferably 5 to 6.
The protrusions may each have straight sides substantially perpendicular to the build surface. Alternatively, the protrusions may each have a taper of increasing cross section along their longitudinal axis. In particular, the protrusions may have a taper of increasing cross section towards the build surface, i.e. an inverse taper. In this way the base of the protrusions provide great flexibility, whilst the top of the protrusions have only a small gap to their neighbouring protrusions in the array.
The protrusions may take the form of pillars having a generally planar top. The pillars may have any cross section, but are preferably regularly shaped such that the gap between neighbouring pillars is substantially constant. For ease of manufacture, the pillars may have a rectangular section, constant along the length of the protrusion. Alternatively, a hexagonal, octagonal, circular, elliptical or other section may be provided.
A gap between adjacent protrusions may be filled by a material dissimilar to that of the protrusions. For example, the gap may be filled with a material of low stiffness as compared with that of the protrusions. Alternatively the gap may be an air gap, i.e. a material of negligible stiffness.
The protrusions may be formed by cutting slits in the substrate. The slits may be provided in an upper portion of the substrate, and a lower portion of the substrate may be substantially solid. The slits may take the form of a grid.
The build surface may be substantially rectangular and the grid may be aligned substantially with an edge or a diagonal of the build surface. Aligning with the diagonal may be preferable, such that the part being built by the additive manufacturing process may be arranged diagonally on the build surface. In this way larger parts can be built for a given size of substrate or ALM system.
The slits may be provided on only a portion of the build surface. The slits may have a substantially uniform width. The slits may have a particularly small width, e.g. approximately 0.1 mm, and a high aspect ratio. The aspect ratio is the length of the slit in the direction extending from the build surface vs. the slit width. The aspect ratio may therefore be at least 100, preferably at least 150, and may be up to approximately 500. Cutting the slits with such a high aspect ratio can be achieved using electrical discharge machining (EDM), e.g. wire EDM. Alternatively laser cutting may be used, for example.
The base of each slit may have a radius corner so as to protect against stress concentrations and crack propagation into the substrate from the end of the slit. The radius may be generally U-shaped or generally tear drop shaped. The radius may be at least 0.5 times the width of the slit, preferably at least 2 times.
In the case where the upper portion of the substrate has a different material to the lower portion, the lower portion may have a higher stiffness than the upper portion. The upper portion may be substantially solid, and free from slits, cuts, grooves, indentations or the like.
The upper portion may include a material of high ductility and low yield strength as compared with the material of the part intended to be fused to it during the additive manufacturing process.
The upper portion may include a includes a material of low elastic modulus and high strain to failure as compared with the material of the part intended to be fused to it during the additive manufacturing process.
The upper portion may include a material that is weldable with the material of the part intended to be fused to it during the additive manufacturing process.
Regardless of the material and/or construction of the substrate, the substrate may be re-useable for building successive part(s) by the additive manufacturing process. In particular, a top layer of the substrate may be adapted to be removed after each build to redefine the build surface. The thickness and/or construction of the upper portion of the substrate may be arranged to permit at least 5, and preferably at least 10, builds. A thickness of approximately 1 mm may be milled, or otherwise removed, from the top of the substrate to redefine the build surface after each build. Removing this material from the substrate is intended to remove any material that may have plastically deformed during the previous build, leaving only material that has elastically deformed remaining in the substrate. The material properties, and/or the construction (e.g. slit gap width) in the build surface may therefore be restored.
The additive manufacturing process typically progresses by creating the part layer by layer. For example, the part may be created by selectively sintering successive powder layers. However, the substrate may alternatively be used with other additive manufacturing processes.
FIG. 1 illustrates schematically a powder bed ALM processing system;
FIG. 2 illustrates a side view of the substrate of the system;
FIG. 3 illustrates a detail view of region A of FIG. 2;
FIG. 4 illustrates a three-dimensional view of the substrate;
FIG. 5 illustrates a plan view of another embodiment of the substrate, showing a part built upon the substrate;
FIG. 6 illustrates a schematic partial view of the slits in the substrate;
FIG. 7 illustrates a partial schematic view of the substrate with a part built on the build surface;
FIG. 8 illustrates a schematic partial view of protrusions of another embodiment of the substrate; and
FIG. 9 illustrates a cross section view of another embodiment of the substrate having upper and lower portions including different materials.
FIG. 1 illustrates a cold powder bed processing additive layer manufacturing (ALM) system. The system is “cold” in that the processing environment is at ambient temperature, and is not maintained at an elevated temperature. The system comprises a pair of feed containers 10, 11 containing powdered metallic material such as powdered Titanium. A roller 12 picks up powder from one of the feed containers (in the example of FIG. 1, the roller 12 is picking up powder from the right hand feed container) and rolls a continuous bed of powder over a substrate 13. A laser head 14 then scans over the powder bed, and a laser beam from the head is turned on and off to melt the powder in a desired pattern.
The substrate 13 then moves down by a small distance (typically of the order of 0.1 mm) to prepare for growth of the next layer. After a pause for the melted powder to solidify, the roller 12 proceeds to roll another layer of powder over substrate 13 in preparation for sintering. Thus as the process proceeds, a sintered part 15 is constructed, supported by unconsolidated powder parts 16. After the part has been completed, it is removed from substrate 13 and the unconsolidated powder 16 is recycled before being returned to the feed containers 10, 11.
Movement of the laser head 14 and modulation of the laser beam is determined by a Computer Aided Design (CAD) model of the desired profile and layout of the part.
Various embodiments of the substrate 13 for use in the powder bed system shown in FIG. 1 will now be described in detail.
FIGS. 2 to 4 illustrate a first embodiment of the substrate 13′. The substrate 13′ has a build surface 20. The first layer of powder laid on the build surface 20 is fused to the build surface across substantially the entire base area of the part to be formed by the ALM process. This fixes the part to the substrate and substantially prevents curling of the part during the build. The substrate 13′ is configured to provide relatively high stiffness in a direction (z) substantially perpendicular to the build surface, whilst having a low longitudinal stiffness in the plane (x-y) of the build surface.
The substrate 13′ has an upper portion 21 nearest the build surface 20 and a lower portion 22. The material for the upper and lower portions 21, 22 is the same, and in this example is Titanium to provide a suitable match with the Ti 6-4 powder used to create the part 15. This material match is important for fusing the part to the substrate.
The upper portion 21 of the substrate includes an array of slits 23 extending from the build surface 20 through part of the thickness of the substrate. The slits 23 form a rectangular grid pattern across the build surface 20 to define an array of protrusions 24 with their longitudinal axis aligned with the build direction (z) and substantially perpendicular to the build surface 20.
The slits 23 have a width s of approximately 0.1 mm and a depth d of approximately 15 mm. The slits are regularly spaced approximately 3 mm apart such that the protrusions 24 are square section pillars, having a height of approximately 15 mm and a 3×3 mm cross section with parallel sides aligned with the z direction. The tops 25 of the pillars make up the build surface 20.
The slits 23 are cut by spark erosion, such as wire EDM, or may alternatively be laser cut. The substrate 13′ may initially be similar to a conventional Titanium plate substrate for powder bed ALM. Cutting the slits 23 into the monolithic plate has the effect of maintaining high stiffness in the z direction whilst introducing relatively low longitudinal stiffness in the x-y plane of the build plate. Due to the slits 23 the resultant base of the pillars remain integrally formed with the lower portion 22 of the substrate, and the pillars act as beams for deflection in the x-y plane at the build surface 20.
In this way, the material shrinkage which occurs as the sintered powder solidifies during creation of each successive layer of the ALM part 15 is accommodated by bending of the pillars about their respective bases. This has the effect of closing up at least some of the slits 23, with this effect being most pronounced at the edges of the part 15. Naturally, this slightly disturbs the planar build surface such that small steps are created between adjacent pillars but this step is small due to the size (3×3 mm) of the top of the pillars and the very high aspect ratio of the slits, which in this example is 150. Generally, the higher the aspect ratio of the slits, the flatter the build surface will be at maximum deflection of the pillars.
The base of the slits 23 has a radius r of approximately 0.05 mm so as to function as crack inhibitors and prevent crack propagation through the substrate.
As shown in FIG. 4 the substrate 13′ includes mounting holes 26, one at each corner of the substrate for fixing, e.g. by bolting, the substrate to the ALM system transport for raising/lowering the substrate.
It may generally be observed that the lower portion 22 of the substrate 13′ is substantially isotropic, whilst the upper portion 21 having the slits 23 is anisotropic. The lower portion 22 is sufficiently stiff to prevent bending or curling of the substrate 13′ during the build. The upper portion 21 maintains sufficient stiffness in the z-direction, whilst having a low longitudinal stiffness in the x-y plane of the build surface 20. The deformation in the upper portion 21 due to bending of the pillars is mostly elastic but the design accommodates a limited degree of plastic deformation, if particularly high residual stresses are created, e.g. due to the shape of the part being built.
In a conventional manner, the top 1 mm or so of the substrate 13′ can be milled away after each build so as to redefine the build surface. This beneficially removes any material that may have plastically deformed during the last build. The substrate 13′ is thus re-useable a plurality of times. With sufficient depth of the slits 23 the substrate 13′ may be re-used up to approximately 5 to 10 times.
FIG. 5 illustrates an alternative embodiment of the substrate 13″, which differs in that the slit grid occupies only a portion of the build surface 20 and in that the slit grid is oriented approximately along the diagonal of the rectangular build surface. These features may be provided independently or jointly as here. Providing the slits across only a portion of the build surface where the part is to be built may save production costs, as cutting the slits by spark erosion for example can be expensive. Orienting the slit grid to the diagonal of the build surface provides greater movement in the primary shrinkage directions of the part 15, which is typically oriented along the diagonal to maximise the size of part that can be built for a given rectangular build surface area.
FIG. 6 illustrates a schematic detailed view of the base of the slits 23′ in accordance with another embodiment, in which the radiused base has a tear drop shape so as to maximise the radius r, thus further improving resistance to crack propagation through the substrate.
A gap between adjacent pillars defined by the slits 23 is typically air filled, but in an alternative embodiment this gap may be filled with a material different than that of the pillars, e.g. a ductile plastics material. Filling the slits may prevent the powder from falling into the slits. However, even with an air gap this is generally not problematic. The very narrow slit width s of approximately 0.01 mm is approximately twice the diameter of the powder particles used in the ALM process. This is beneficial as the powder particles will tend to easily bridge the slits in the build surface during application of the first or second powder layers. FIG. 7 illustrates this bridging effect, and also shows a cut line 30 for cutting the completed part 15 from the substrate 13 by wire EDM, or similar. As can be seen, this cut line 30 is disposed just above the bridging between adjacent pillars. This leaves a small thickness of the sintered powder material fused to the substrate, which is removed when the top layer of the substrate is milled after the build to redefine the build surface in readiness for a subsequent build.
FIG. 8 illustrates schematically a yet further design of the protrusions and slits in the upper portion of the substrate. The protrusions 24″ have a tapered shape, as compared with this straight sided protrusions described previously. The protrusions 24″ retain a substantially rectangular cross section but have a taper of increasing cross section towards the build surface 20. The slits 23″ have a corresponding taper of increasing cross section away from the build surface 20. The tapered protrusions are advantageous in that the base has a reduced cross section, which promotes greater bending of the beam like protrusions in the x-y plane at the build surface 20. The slits 23″ however may be more difficult to manufacture. Accordingly, it may be preferable to manufacture the substrate having the protrusions in the upper portion by an ALM process, such as that described above. Forming re-entrant or undercut projections is generally straightforward in ALM.
Finally, FIG. 9 illustrates a yet further embodiment of the substrate 13′″ having an upper portion 41 of a first material and a lower portion 42 of a second material. By contrast with the embodiments described above both the upper and lower portions are solid, and the upper portion in particular is free from slits. The lower portion has a higher stiffness than the upper portion. For example, the upper portion 41 includes a material of high ductility and low yield strength such as grade 1 or grade 2 pure Titanium. This provides a good match for the Titanium 6-4 material used to form the part as the part will readily fuse to the substrate.
Alternatively, the upper portion 41 may include a material of low elastic modulus and high strain to failure as compared with the material of the part intended to be fused to it during the additive manufacturing process. For example, a super-elastic material such as the shape memory alloy Nitinol may be used, which includes approximately 50% Ni and 50% Ti. The upper portion 41 includes a material that is weldable with the material of the part intended to be fused to it during the additive manufacturing process. The large proportion of Titanium in Nitinol would satisfy this requirement when building parts from Titanium powder by ALM.
Where different materials are provided for the upper and lower portions of the substrate, the overall depth of the substrate may increase slightly as compared with the embodiments described with reference to FIGS. 2 to 4.
Once the build has completed and the part has been removed from the substrate, the part is typically heat treated to reduce any remaining residual stresses. So long as the modified substrate in accordance with this invention can prevent crack initiation during the build, due to the increased strain deformation across the build surface, then the finished part should be free from stress induced defects.
1. A system for creating a part by an additive manufacturing process, the system including a substrate having a build surface for fusing to a part being formed on the substrate by the additive manufacturing process, wherein the substrate is re-useable for building successive parts by the additive manufacturing process, wherein the substrate has an upper portion nearest the build surface and a lower portion, wherein the upper portion includes an array of protrusions with their longitudinal axis aligned substantially perpendicular to the build surface, and wherein the protrusions include a different material to that of the lower portion, and the protrusions are not incorporated in the part created on the substrate.
2. A system according to claim 1, wherein tops of the protrusions provide at least a portion of the build surface.
3. A system according to claim 1, wherein bases of the protrusions are integrally formed with the lower portion of the substrate.
4. A system according to claim 1, wherein the protrusions are slender and take the form of pillars having a generally planar top.
5. A system according to claim 1, wherein the protrusions each have straight sides substantially perpendicular to the build surface.
6. A system according to claim 1, wherein the substrate is a monolith.
7. A system according to claim 1, wherein a gap between adjacent protrusions is filled by a material dissimilar to that of the protrusions.
8. A system according to claim 1, wherein the array of projections are defined by an array of slits.
9. A system according to claim 8, wherein the slits have a width of 0.1 mm or below.
10. A system according to claim 8, wherein the slits form a grid.
11. A system according to claim 8, wherein the slits have a substantially uniform width.
12. A system according to claim 8, wherein the base of each slit has a radius corner.
13. A system according to claim 1 configured to create the part layer by layer.
14. A system according to claim 13, configured to create the part by selectively sintering successive powder layers.
15. A system for creating a part by an additive manufacturing process, the system including a substrate having a build surface for fusing to a part being formed on the substrate by the additive manufacturing process, wherein the substrate is re-useable for building successive parts by the additive manufacturing process, wherein the substrate has an upper portion nearest the build surface and a lower portion, wherein the upper portion includes an array of protrusions with their longitudinal axis aligned substantially perpendicular to the build surface, and wherein the protrusions are slender, having an aspect ratio of at least 3, and take the form of pillars having a generally planar top.
16. A system according to claim 15, wherein tops of the protrusions provide at least a portion of the build surface.
17. A system according to claim 15, wherein bases of the protrusions are integrally formed with the lower portion of the substrate.
18. A system according to claim 15, wherein the protrusions each have straight sides substantially perpendicular to the build surface.
19. A system according to claim 15, wherein the substrate is a monolith.
20. A system according to claim 15, wherein a gap between adjacent protrusions is filled by a material dissimilar to that of the protrusions.
21. A system according to claim 15, wherein the array of projections are defined by an array of slits.
22. A system according to claim 21, wherein the slits have a width of 0.1 mm or below.
23. A system according to claim 21, wherein the slits form a grid.
24. A system according to claim 21, wherein the slits have a substantially uniform width.
25. A system according to claim 21, wherein the base of each slit has a radius corner.
26. A system according to claim 15, configured to create the part layer by layer.
27. A system according to claim 26, configured to create the part by selectively sintering successive powder layers.
28. A system for creating a part by an additive manufacturing process, the system including a substrate having a build surface for fusing to a part being formed on the substrate by the additive manufacturing process, wherein the substrate is re-useable for building successive parts by the additive manufacturing process, wherein the substrate has an upper portion nearest the build surface and a lower portion, wherein the upper portion includes an array of protrusions with their longitudinal axis aligned substantially perpendicular to the build surface, wherein the protrusions each have a taper of increasing cross section towards the build surface and wherein the array of projections are defined by an array of slits, wherein the slits have a width of 0.1 mm or below.
29. A system according to claim 28, wherein tops of the protrusions provide at least a portion of the build surface.
30. A system according to claim 28, wherein bases of the protrusions are integrally formed with the lower portion of the substrate.
31. A system according to claim 28, wherein the protrusions are slender and take the form of pillars having a generally planar top.
32. A system according to claim 28, wherein the substrate is a monolith.
33. A system according to claim 28, wherein a gap between adjacent protrusions is filled by a material dissimilar to that of the protrusions.
34. A system according to claim 28, wherein the slits are provided in an upper portion of the substrate, and a lower portion of the substrate is substantially solid.
35. A system according to claim 28, wherein the slits form a grid.
36. A system according to claim 35, wherein the slits have a substantially uniform width.
37. A system according to claim 35, wherein the base of each slit has a radius corner.
38. A system according to claim 28, configured to create the part layer by layer.
39. A system according to claim 38, configured to create the part by selectively sintering successive powder layers.
40. A system for creating a part by an additive manufacturing process, the system including a substrate having a build surface for fusing to a part being formed on the substrate by the additive manufacturing process, and a plurality of slits extending from the build surface through part of the thickness of the substrate, wherein the substrate is re-useable for building successive parts by the additive manufacturing process, wherein the build surface is substantially rectangular, wherein the slits form a grid and are provided on only a portion of the build surface, and wherein the grid is aligned substantially with a diagonal of the build surface.
41. A system according to claim 40, wherein the slits are provided in an upper portion of the substrate, and a lower portion of the substrate is substantially solid.
42. A system according to claim 40, wherein the slits have a substantially uniform width.
43. A system according to claim 40, wherein the substrate is a monolith.
44. A system according to claim 40, wherein the base of each slit has a radius corner.
45. A system according to claim 40, wherein the slits have a width of 0.1 mm or below.
46. A system according to claim 40, configured to create the part layer by layer.
47. A system according to claim 46, configured to create the part by selectively sintering successive powder layers.
US14/386,742 2012-03-21 2013-03-18 Substrate for additive manufacturing Active 2035-05-16 US10046524B2 (en)
GB1204922.7A GB2500412A (en) 2012-03-21 2012-03-21 Build Plate for an additive manufacturing process
GB1204922.7 2012-03-21
PCT/GB2013/050686 WO2013140146A1 (en) 2012-03-21 2013-03-18 Substrate for additive manufacturing
US20150054193A1 US20150054193A1 (en) 2015-02-26
US10046524B2 true US10046524B2 (en) 2018-08-14
ID=46052268
US14/386,742 Active 2035-05-16 US10046524B2 (en) 2012-03-21 2013-03-18 Substrate for additive manufacturing
US (1) US10046524B2 (en)
EP (1) EP2828068A1 (en)
JP (1) JP2015516316A (en)
GB (1) GB2500412A (en)
WO (1) WO2013140146A1 (en)
DE102014207510A1 (en) 2014-04-17 2015-10-22 Kennametal Inc. Cutting tool and method for producing a cutting tool
DE102014207507A1 (en) 2014-04-17 2015-10-22 Kennametal Inc. Cutting tool and method for producing a cutting tool
JP2016053198A (en) * 2014-09-04 2016-04-14 株式会社コイワイ Metal molded product and metal powder for metal molded product
US9908287B2 (en) 2014-11-20 2018-03-06 Ut-Battelle, Llc Build platform that provides mechanical engagement with additive manufacturing prints
JP2017160485A (en) * 2016-03-09 2017-09-14 パナソニックＩｐマネジメント株式会社 Manufacturing method of three-dimensional shape molded object
DE102016105215A1 (en) 2016-03-21 2017-09-21 GEFERTEC GmbH Construction platform system and method for the additive production of a molding
WO2017163405A1 (en) * 2016-03-25 2017-09-28 技術研究組合次世代３Ｄ積層造形技術総合開発機構 Three-dimensional additive fabrication device, method for controlling three-dimensional additive fabrication device, and program for controlling three-dimensional additive fabrication device
DE102016222555A1 (en) * 2016-11-16 2018-05-17 Siemens Aktiengesellschaft Method for additive production of a component and computer-readable medium
JP2001018298A (en) * 1992-11-24 2001-01-23 Matsushita Electric Works Ltd Molding method for three-dimensional molded article
EP1279480A1 (en) 2001-07-27 2003-01-29 Next Factory S.R.L. Apparatus for creating three-dimensional objects
JP2003305778A (en) 2003-03-31 2003-10-28 Matsushita Electric Works Ltd Method for manufacturing three-dimensionally shaped article
WO2005025781A1 (en) 2003-09-15 2005-03-24 Trumpf Werkzeugmaschinen Gmbh + Co. Kg Substrate sheet for a 3d-shaping method
GB2458745A (en) 2008-02-13 2009-10-07 Materials Solutions Grooved support for selective sintering or melting process
WO2010044008A1 (en) 2008-10-13 2010-04-22 Philips Intellectual Property & Standards Gmbh Grid and method of manufacturing a grid for selective transmission of electromagnetic radiation, particularly x-ray radiation for mammography applications
WO2010049696A2 (en) 2008-10-30 2010-05-06 Mtt Technologies Limited Additive manufacturing apparatus and method
US20130256953A1 (en) 2011-04-29 2013-10-03 Phenix Systems Method for manufacturing an object by solidifying powder using a laser beam with the insertion of a member for absorbing deformations
JP3095302B2 (en) * 1992-11-24 2000-10-03 松下電工株式会社 Method of forming three-dimensionally shaped object
JP3090114U (en) * 2002-05-20 2002-11-29 中部日本工業株式会社 Stereolithography apparatus according-cellular build material
2012-03-21 GB GB1204922.7A patent/GB2500412A/en not_active Withdrawn
2013-03-18 EP EP13711944.2A patent/EP2828068A1/en active Pending
2013-03-18 JP JP2015500982A patent/JP2015516316A/en active Pending
2013-03-18 WO PCT/GB2013/050686 patent/WO2013140146A1/en active Application Filing
2013-03-18 US US14/386,742 patent/US10046524B2/en active Active
US20070023977A1 (en) 2003-09-15 2007-02-01 Stefan Braun Substrate sheet for a 3d-shaping method
US20110192997A1 (en) 2008-10-13 2011-08-11 Koninklijke Philips Electronics N.V. Grid and method of manufacturing a grid for selective transmission of electromagnetic radiation, particularly x-ray radiation for mammography applications
Azuma et al., JP 2001018298 A, Machine Translation, Jan. 23, 2001. *
European Office Action dated Sep. 16, 2016 EP Application No. 13711944.2.
International Search Report dated Jun. 6, 2013 in International Application No. PCT/GB2013/050686, filed Mar. 18, 2013.
JP-PCT Office Action dated Nov. 8, 2016 JP Patent Application No. 2015-500982.
Search Report dated Jul. 18, 2012 in Great Britain Application No. GB1204922.7.
US20150054193A1 (en) 2015-02-26
GB201204922D0 (en) 2012-05-02
EP2828068A1 (en) 2015-01-28
JP2015516316A (en) 2015-06-11
GB2500412A (en) 2013-09-25
WO2013140146A1 (en) 2013-09-26
Yan et al. 2014 Advanced lightweight 316L stainless steel cellular lattice structures fabricated via selective laser melting
Baufeld et al. 2011 Wire based additive layer manufacturing: Comparison of microstructure and mechanical properties of Ti–6Al–4V components fabricated by laser-beam deposition and shaped metal deposition
Morgan et al. 2004 Density analysis of direct metal laser re-melted 316L stainless steel cubic primitives
DE102011105045B3 (en) 2012-06-21 Producing a component by a layered structure using selective laser melting, comprises for each layer fusing a powdery component material corresponding to a desired geometry of the component, using a laser beam and solidifying by cooling
Mumtaz et al. 2010 Selective laser melting of thin wall parts using pulse shaping
Calignano 2014 Design optimization of supports for overhanging structures in aluminum and titanium alloys by selective laser melting
US20050142024A1 (en) 2005-06-30 Method for producing three-dimensional sintered work pieces
Bauereiß et al. 2014 Defect generation and propagation mechanism during additive manufacturing by selective beam melting
KR20160100883A (en) 2016-08-24 Method for manufacturing a metallic component by additive laser manufacturing
Hanzl et al. 2015 The influence of processing parameters on the mechanical properties of SLM parts
EP1400339A1 (en) 2004-03-24 Method for manufacturing a three-dimensional object
EP2785481B1 (en) 2020-01-15 Process for producing a shaped body by layerwise buildup from material powder
Wang et al. 2013 Research on the fabricating quality optimization of the overhanging surface in SLM process
JP5230264B2 (en) 2013-07-10 Manufacturing method of three-dimensional shaped object
DE10344901B4 (en) 2006-09-07 Method for producing a three-dimensional sintered product
JP5330656B2 (en) 2013-10-30 Mass production of 3D products made of intermetallic compounds
JP2016505415A (en) 2016-02-25 Method for additive fabrication of parts by selective melting or selective sintering of tightly optimized powder beds using high energy beams
Strano et al. 2013 Surface roughness analysis, modelling and prediction in selective laser melting
Hussein et al. 2013 Advanced lattice support structures for metal additive manufacturing
EP2815873B1 (en) 2019-03-20 Additive layer manufacturing method
Owner name: AIRBUSGROUP LIMITED, UNITED KINGDOM
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:MEYER, JONATHAN;REEL/FRAME:034772/0880