Patent US5003026 - UV curable no-wax coating - Google PatentS�k Bilder Kartor Play YouTube Nyheter Gmail Drive Mer » Avancerad patents�kning | Webbhistorik | Logga in Avancerad patents�kning PatentGloss retention and stain resistance are improved in a no-wax UV cured flooring wear surface by reacting a phthalate polyester polyol and a long chain hydroxy acrylate with an aromatic or cycloalkyl diisocyanate to form an oligomer which is employed as a major ingredient of the UV curable coating composition...http://www.google.se/patents/US5003026?utm_source=gb-gplus-sharePatent US5003026 - UV curable no-wax coating PublikationsnummerUS5003026 ATyp av kung�relseBeviljande Ans�kningsnummer07/369,866 Publiceringsdatum26 mar 1991 Registreringsdatum22 jun 1989 Prioritetsdatum22 jun 1989 UppfinnareWendell A. EhrhartDavid A. Smith Ursprunglig innehavareArmstrong World Industries, Inc.Bank Of America, N.A., As Collateral AgentAwi Licensing Company, Inc. USA-klassificering528/49 Internationell klassificeringC08G18/42D06N3/14C08G18/67 Kooperativ klassningD06N3/144C08G18/4219C08G18/672 Europeisk klassificeringC08G18/67B4C08G18/42B2D9D06N3/14D4H�nvisningarCitat fr�n patent (7) H�nvisningar finns i f�ljande patent (20)Externa l�nkarUSPTO �verl�telse av �gander�tt till patent som har registrerats av USPTO EspacenetUV curable no-wax coatingUS 5003026 A Sammanfattning Gloss retention and stain resistance are improved in a no-wax UV cured flooring wear surface by reacting a phthalate polyester polyol and a long chain hydroxy acrylate with an aromatic or cycloalkyl diisocyanate to form an oligomer which is employed as a major ingredient of the UV curable coating composition used to produce the wear surface.
What is claimed is: 1. A floor covering product comprising a wear layer including a polymerized urethane-acrylate oligomer, said oligomer comprising the reaction product of an aromatic or cycloalkyl diisocyanate, a monohydroxymonoacrylate having an hydroxyl equivalent weight of about 250 to about 600 and a phthalate polyester polyol having an hydroxyl equivalent weight of about 175 to about 500.
2. The floor covering product of claim 1 wherein the number of equivalents of isocyanate functionalities to equivalents of hydroxyl functionalities is about 0.7 to about 1.5, and the number of equivalents of hydroxyacrylate functionalities to equivalents of polyester polyol functionalities is greater than about 1
3. The floor covering product of claim 1 wherein the aliphatic diisocyanate is selected from the group consisting of 1,1'-methylenebis(4-isocyanatocyclohexane), isophorone diisocyanate and tetramethyl xylene diisocyanate.
4. The floor covering product of claim 2 wherein the monohydroxymonoacrylate has the following structure: ##STR2## where n has a value of at least 1 and no greater than about 4.
5. The floor covering product of claim 4 wherein the phthalate polyester polyol is a predominately 1,6-hexylene o-phthalate polyester polyol.
6. The floor covering product of claim 1 wherein the wear layer comprises the reaction product of the urethane-acrylate oligomer, an acrylate reactive diluent and a photoinitiator.
7. The floor covering product of claim 6 wherein the wear layer comprises the reaction product of about 40 to about 70 percent by weight of the urethane-acrylate oligomer, about 30 to about 60 percent by weight of the acrylate reactive diluent and about 0.01 to about 25 parts per 100 parts of oligomer and diluent of the photoinitiator.
8. The floor covering product of claim 7 wherein the acrylate reactive diluent comprises at least 55% by weight of a diacrylate having a molecular weight of about 250 to about 1500.
9. The floor covering product of claim 2 wherein the wear layer comprises the reaction produt of the urethane-acrylate oligomer, an acrylate reactive diluent and a photoinitiator.
10. The floor covering product of claim 9 wherein the wear layer comprises the reaction product of about 40 to about 70 percent by weight of the urethane-acrylate oligomer, about 30 to about 60 percent by weight of the acrylate reactive diluent and about 0.01 to about 25 parts per 100 parts of oligomer and diluent of the photoinitiator.
11. The floor covering product of claim 10 wherein the acrylate reactive diluent comprises at least 55% by weight of a diacrylate having a molecular weight of about 250 to about 1500.
12. The floor covering product of claim 4 wherein the wear layer comprises the reaction product of the urethane-acrylate oligomer, an acrylate reactive diluent and a photoinitiator.
13. The floor covering product of claim 12 wherein the wear layer comprises the reaction product of about 40 to about 70 percent by weight of the urethane-acrylate oligomer, about 30 to about 60 percent by weight of the acrylate reactive diluent and about 0.01 to about 25 parts per 100 parts of oligomer and diluent of the photoinitiator.
14. The floor covering product of claim 13 wherein the acrylate reactive diluent comprises at least 55% by weight of a diacrylate having a molecular weight of about 250 to about 1500.
15. The floor covering product of claim 5 wherein the wear layer comprises the reaction product of the urethane-acrylate oligomer, an acrylate reactive diluent and a photoinitiator.
16. The floor covering product of claim 15 wherein the polyester polyol comprises the reaction product of phthalic anhydride and 1,6-hexanediol.
17. The floor covering product of claim 15 wherein the wear layer comprises the reaction product of about 40 to about 70 percent by weight of the urethane-acrylate oligomer, about 30 to about 60 percent by weight of the acrylate reactive diluent and about 0.01 to about 25 parts per 100 parts of oligomer and diluent of the photoinitiator.
18. The floor covering product of claim 17 wherein the polyester polyol comprises the reaction product of phthalic anhydride and 1,6-hexanediol.
19. The floor covering product of claim 17 wherein the acrylate reactive diluent comprises at least 55% by weight of a diacrylate having a molecular weight of about 250 to about 1500.
20. The floor covering product of claim 19 wherein the diacrylate is selected from the group consisting of a diacrylate ester of ethoxylated bisphenol A, a diacrylated linear aliphatic diol of average chain length of about 14 carbon atoms and mixtures thereof.
FIELD OF THE INVENTION The invention relates to UV curable coatings useful as wear surfaces for resilient floor coverings. More particularly, the invention relates to a UV cured wear surface which provides improved gloss and stain protection for floor coverings.
BACKGROUND OF THE INVENTION Urethane acrylates are known as radiation cured wear layers for flexible surface coverings, e.g. floor tile and sheet flooring. Products and processes using UV curing are described in U.S. Pat. Nos. 3,924,023; 3,935,364; 3,959,521; 4,016,306; 4,075,366; 4,421,782; and 4,138,299.
A wear surface composition, comprising a UV curable, polyester based, urethane acrylate/reactive diluent composition, overcoated (wet-on-wet) with an acrylic acid/water solution containing surfactant during UV curing, is described in U.S. Pat. No. 4,421,782. The present invention provides an improvement over the base compositions of U.S. Pat. No. 4,421,782 in terms of gloss retention and stain resistance, without requiring the cumbersome wet-on-wet process.
SUMMARY OF THE INVENTION An improved UV curable coating for a floor covering comprises:
(1) an oligomer comprising the reaction product of a phthalate polyester polyol, an aromatic or cycloalkyl diisocyanate and a monohydroxymonoacrylate with a molecular weight of between about 250 to about 600;
(2) an acrylate reactive diluent; and
Preferred reactive diluents are diacrylates of about 250 to about 1500 molecular weight. The preferred oligomer is the reaction product of about 20 to about 38 weight percent isocyanate, about 28 to about 60 weight percent acrylate and about 14 to about 38 weight percent polyol.
Preferably, the isocyanate moiety of the aromatic diisocyanate is not attached directly to the aromatic ring. The preferred diisocyanate is 1,1'-methylenebis(4-isocyanatocyclohexane).
DETAILED DESCRIPTION OF THE INVENTION Ultraviolet (UV) cured no-wax coatings are commercially available based on the processes of U.S. Pat. Nos. 4,138,299 and 4,421,782. Oligomers based on 2-hydroxyethylacrylate, predominately aliphatic polyester polyol and 1,1'-methylenebis(4-isocyanatocyclohexane) are mixed with acrylate reactive diluents and photoinitiators and employed as no-wax wear surfaces for floor coverings. While these prior art compositions (particularly those containing substantial amounts of acrylic acid as reactive diluent) provided good no-wax performance, there were still some properties such as gloss retention, hydrolytic stability and stain resistance which could be improved. In addition, it was desirable to reduce or eliminate acrylic acid in the reactive diluent due to its volatility and corrosive properties. According to the practice of the present invention, it is possible to advance the state of the art to improve properties from good to excellent while lowering or eliminating acrylic acid.
Ultraviolet (UV) curable no-wax floor coatings, similar to Product B of U.S. Pat. No. 4,421,782, are used commercially. These contain oligomers which are the reaction products of 2-hydroxyethylacrylate, polyester polyols (based mainly on aliphatic acids) and 1,1'-methylenebis(4-isocyanatocyclohexane); and relatively low molecular weight acrylate reactive diluents. Substantial amounts of monoacrylates and/or acrylic acid have been used as reactive diluents, in part to reduce viscosities to workable levels. These wear layers are generally adhered to polyvinyl chloride composition substrates. While these prior art compositions provided good no-wax performance, there were still some properties such as gloss retention, hydrolytic stability and stain resistance which could be improved.
Although the wet-on-wet coating process of U.S. Pat. No. 4,421,782 is one way of upgrading these properties, it is somewhat cumbersome to perform in production and results in increased exposure to the volatile and corrosive acrylic acid. According to the practice of the present invention, it is possible to advance the state of the art to improve properties from good to excellent, while lowering the amount or even eliminating acrylic acid and still obtain desirably low coating viscosities, often lower than prior art formulations.
It was discovered that reacting 1,1'-methylenebis(4-isocyanatocyclohexane) [Mobay Chemical's Desmodur W] with a long chain monohydroxymonoacrylate and a phthalate polyester polyol could produce oligomers which would provide UV curable coatings of improved gloss retention, stain resistance and alkali resistance. Surprisingly, the viscosity of many of these coatings was lower than prior art formulas, even when little or no acrylic acid was used in the reactive diluent and wear appearance properties were superior.
A phthalate polyester polyol is defined as a polyester polyol of acid number less than about 15, preferably less than about 5, comprising the reaction product of an equivalent excess of one or more polyols of equivalent weight less than 150 with at least one polycarboxylic acid, wherein at least 50 equivalent percent of the polycarboxylic acid is terephthalic acid, isophthalic acid and/or phthalic acid or equivalent (e.g. phthalic anhydride or dimethyl terephthalate).
It was further discovered that oligomers, which are the reaction products of 0.7 to 1.5 equivalents of 1,1'-methylenebis(4-isocyanatocyclohexane) with 1.0 equivalent of a mixture of relatively high molecular weight (250 to 600) hydroxyacrylates and phthalate polyester polyols (equivalent ratio of hydroxyacrylate to polyester polyol greater than about 1.0) provide improved gloss retention, stain resistance and alkali resistance within a solventless UV curable coating of desirably low application viscosity. The coatings of the present invention comprise the above oligomers, acrylate reactive diluents and photoinitiators. Especially valuable properties are obtained when substantial quantites of high molecular weight (250 to 1500) diacrylates are the principle reactive diluents. Surprisingly, the viscosities of many of these preferred formulations are still lower than prior art formulations even when the excellent viscosity reducer acrylic acid is absent.
Diacrylate as used herein is an ester of acrylic acid and an alcohol, or a mixture of such esters, with an average of 1.5 to 2.5 acrylate groups per molecule. All molecular weights are number average molecular weights.
It is preferred to employ a polycaprolactone based hydroxyacrylate (e.g. Union Carbide's Tone M-100) and a predominately 1,6-hexylene phthalate polyester polyol in preparing the oligomer. A predominately 1,6-hexylene phthalate polyester polyol is defined as a phthalate polyester polyol wherein at least 50 equivalent percent of the &lt;150 eq. wt. polyol is 1,6-hexanediol and wherein at least 50 eq. percent of the polycarboxylic acid is phthalic acid or equivalent (e.g. phthalic anhydride).
Tone M-100 (molecular weight 344) has an average skeletal structure of ##STR1## where n averages about 2.
Phthalate polyester polyols suitable for the present invention can be prepared by a procedure similar to Example 1 of U.S. Pat. No. 4,138,299 by reacting acids such as isophthalic, terephthalic, phthalic anhydride, adipic, azelaic and/or sebacic with polyols such as 1,6-hexanediol, trimethylol propane, triethylene glycol, neopentyl glycol, cyclohexane dimethanol and glycerine in the presence of a catalyst such as stannous oxalate.
The diisocyanate may be an aromatic or cycloalkyl diisocyanate such as 1,1'methylenebis(4-isocyanatocyclohexane), isophorone diisocyanate or tetramethyl xylene diisocyanate. The 1,1'-methylenebis(4-isocyanatocyclohexane) is commercially available as Desmodur
Suitable acrylate reactive diluents include isodecyl acrylate, isobornyl acrylate, tetraethylene glycol diacrylate, hexanediol diacrylate and ethoxylated trimethylol propane triacrylate.
Preferred acrylate reactive diluents are diacrylates with molecular weights of about 250 to 1500. Examples of such are polybutanediol diacrylate, molecular weight of about 775 (Alcocur PBDDA from Alcolac Inc., Baltimore, Md.); ethoxylated bisphenol A diacrylates, molecular weight of 500 to 700 (SR-349, and Photomer 4028 and Photomer 4025 from Sartomer and Henkle, respectively); a diacrylate of a mixture of straight chain diols with 14 and 15 carbon atoms molecular weight of about 350 (SR-C2000, Sartomer); and acrylated hydroxy terminated polyesters.
Photoinitiators suitable for the practice of the invention include 2-hydroxy-2-methyl-1-phenyl-1-propane-1-one, benzyl dimethyl ketal, diethoxy acetophenone, 1-hydroxycyclohexylphenylketone, benzoin ethers and benzophenone. These can often advantageously be employed in combinations and/or in combination with photoactivators and photosensitizers. A preferred photoinitiator is benzophenone, which may be used in conjunction with other photoinitiators, photoactivators and/or photosensitizers. A preferred combination is about two parts benzophenone/part of 1-hydroxycyclohexylphenylketone.
Other components which may be useful include catalysts such as dialkyl tin dicarboxylates which aid in the preparation of the oligomer and will catalyze the reaction of any excess NCO with water. This can be allowed to occur in the film by the absorption of atmospheric moisture at ambient conditions or accelerated via elevated temperatures. Alternately, water can be added to the reaction vessel and the reaction of any excess NCO completed prior to UV curing. As would be obvious to one skilled in the art, plasticizers, dyes, pigments, light stabilizers, flow aids, etc. may also be employed for particular purposes.
The present invention has industrial applicability in the field of no-wax resilient floor surface coverings.
In the following examples, the wear layer samples were tested for gloss retention (steel wool rub), stain resistance (hair dye, shoe poish, ink, iodine) and alkali resistance (5% sodium hydroxide).
Example 1 ______________________________________A polyester polyol was prepared from the following ingredients______________________________________Phthalic Anhydride  20     equivalents1,6-Hexanediol      23.8   equivalentsGlycerine           6.0    equivalentsDibutyltin bislauryl               0.1    weight %mercaptide catalyst______________________________________
The ingredients were reacted at 220 a acid number less than one, producing a polyol with an hydroxyl eq. wt. of 315.
A coating composition was prepared as follows where the ingredients below in parts by weight were charged in order with stirring into a flask equipped with stirrer, condenser, heating mantle and gas inlet.
______________________________________1. Isodecyl acrylate, reactive diluent                     25.0   parts2. Hexanediol diacrylate, reactive diluent                     5.5    parts3. Tone M-100, hydroxyacrlyate mol. wt.                     30.0   parts344 from Union Carbide Corp.4. Polyester polyol (above)                     17.5   parts5. Dibutyltin dilaurate, catalyst                     0.2    parts6. Ionol                      0.02   parts7. Desmodur                      19.0   parts______________________________________
The mixture was heated, with stirring and under a trickle of dry air, to 70 groups of ingredient 7 with the hydroxy groups of ingredients 3 and 4 to form the oligomer. Upon cooling to about 45 following ingredients were charged with stirring:
______________________________________ 8. Acrylic acid, reactive diluent                     3.0 parts 9. Benzophenone, photoinitiator                     1.8 parts10. Irgacure 651, photoinitiator (Ciba-Geigy)                     0.9 parts11. DC-193, leveling aid (Dow Chemical)                     0.1 parts______________________________________
This formula had 66.5% oligomer and 33.5% reactive diluents. The oligomer had an NCO/OH ratio of 1.01 and a hydroxy acrylate/polyol ratio of 1.56. The oligomer composition was 26.3% polyester, 45.1% Tone M-100 and 28.6% Desmodur W. The 3% acrylic acid in the total formulation made up 9% of the reactive diluents.
The composition was coated on plate glass using a 3 mil Bird blade and UV cured via 2 passes under a pair of 200-watt-per-inch medium pressure mercury lamps at a belt speed which resulted in the delivery of 2.5 joules/sq. cm. per pass.
A comparative composition, Composition 1, was prepared which was similar in composition to Product B of U.S. Pat. No. 4,421,782. This comparison formulation is also very similar in composition and properties (e.g. stain resistance and gloss retention), to a commerical no-wax coating. It was similarly applied to and cured on plate glass. Table I contains comparitive results, where +=satisfactory, ++=good, +++=very good, and ++++=excellent.
TABLE I______________________________________          Comparative 1                     Example 1______________________________________Room Temperature Viscosity            10,000       2,700(CPS)Stain Resistance +            ++Gloss Retention  +            +++______________________________________
Not only were properties significantly improved, but viscosity was reduced by a third. Example 1 was scaled up to pilot plant size and curtain coated onto polyvinyl chloride based floor tiles, UV cured and put through a number of tests for suitability as a flooring wear layer. These tests confirmed the very good gloss retention under actual foot traffic and the good household stain resistance. These tests also confirmed the general suitability of this formula for flooring wear layers (e.g. adequate heat and light stability, ease of cleaning, etc.)
Example 2 The series of formulations in Table II was prepared and tested as in Example 1. All of the formulations except B and C were prepared using the same catalysts, inhibitor and procedure as in Example 1. B and C were made similarly except they were reacted for one hour at 70 adding the water, then for six hours after the water was added.
Comparative results can be found at the bottom of Table II. The results show that a wide range of acrylate reactive diluents can be used within the practice of the invention, either with or without acrylic acid. It is also apparent that high molecular weight diacrylates are preferred.
TABLE II__________________________________________________________________________              Comparative 1                      A   B   C   D   E   F    G__________________________________________________________________________Polyester Polyol Reactants(In Equivalents)Phthalic anhydride         20.0                          20.0                              --  20.0                                      20.0                                          20.0 20.0Isophthalic Acid           --  --  20.0                                  --  --  --   --1,6-Hexanediol             27.5                          23.8                              --  29.7                                      29.7                                          29.2 33.0SR-100 Diol, Sartomer      --  --  15.5                                  --  --  --   --Cyclohexane dimethanol     --  --  9.70                                  --  --  --   --Glycerine                  2.30                          6.00                              12.5                                  2.30                                      2.30                                          0.30 --Polyol Hydroxyl Eq. Wt.    317 315 300 278 278 300  260Oligomer Reactants(Weight % in Oligomer)Polyester polyol   52.8    26.3                          30.6                              26.8                                  29.0                                      18.9                                          29.4 18.4Tone M-100                 45.1                          38.7                              42.3                                  41.6                                      52.8                                          43.1 50.6Desmodur W                 28.6                          30.6                              30.9                                  24.4                                      28.3                                          27.5 31.0Water.sup.1                --  1.04                              1.04                                  --  --  --   --Oligomer Equivalent RatiosNCO/OH                     1.01                          1.11                              1.11                                  1.00                                      0.976                                          0.994                                               1.09Hydroxyacrylate/Polyol              .67     1.50                          1.17                              1.16                                  1.16                                      2.33                                          1.42 2.08Reactive Diluents (Weight %of Total Reactive Diluent)Hexanediol diacrylate      20.9                          18.4                              16.4                                  --  --  --   --Isodecyl Acrylate          47.8                          69.7                              75.8                                  --  6.40                                          --   --Isobornyl Acrylate         31.3                          --  --  --  --  --   --Acrylic Acid       23.2    --  11.8                              7.80                                  --  --  --   --SR-349.sup.2               --  --  --  50.0                                      --  --   --Reactive Diluents (Weight %of Total Reactive Diluent)Alcocur PBDDA.sup.3        --  --  --  50.0                                      --  --   --Photomer 4028.sup.4        --  --  --  --  70.2                                          --   --Chemlink 2000.sup.5        --  --  --  --  23.4                                          26.5 --Photomer 4025.sup.6        --  --  --  --  --  73.5 --Polyester Diacrylate.sup.7 --  --  --  --  --  --   100Oligomer in Complete Formula              69.8    66.5                          62.0                              61.5                                  50.0                                      53.0                                          51.0 49.0(Except for Photoinitiators)(Wt. %)Reactive Diluents in Complete Formula              30.2    33.5                          38.0                              38.5                                  50.0                                      47.0                                          49.0 51.0(Except for Photoinitiators)(Wt. %)Photoinitiators (PHR)Benzophenone               1.80                          2.00                              2.00                                  1.80                                      1.80                                          1.80 1.80Irgacure 184               0.90                          --  --  0.90                                      0.90                                          0.90 0.90Irgacure 651               --  0.90                              0.90                                  --  --  --   --Properties versusComparative FormulaRT VISC (CPS)      10000   3,600                          3,200                              3,200                                  9,000                                      4,600                                          5,400                                               15,000Stain Resistance   +       ++  ++  ++  +++ +++ +++  +++Gloss Retention    +       +++ ++  ++  +++ +++ ++++ +++Alkali Resistance  +       +++ ++  ++  +++ +++ +++  +++__________________________________________________________________________ .sup.1 Parts added/100 parts of other oligomer ingrs. (not all of the water reacts) .sup.2 Sartomer's ethoxylated Bisphenol A diacrylate (MW approximately 510) .sup.3 Alcolac' s polybutanediol diacrylate (mol. wt. approximately 775) .sup.4 Henkle's ethoxylated Bisphenol A diacrylate (MW approximately 540) .sup.5 Sartomer's long straight chain aliphatic diacrylate (MW approximately 350) .sup.6 Henkle's ethoxylated Bisphenol A diacrylate (MW approximately 690) .sup.7 Acrylated 1,6hexylene phthalate (MW approximately 625)
Citat fr�n patent citerade patent Registreringsdatum Publiceringsdatum S�kande TitelUS39240233 apr 19732 dec 1975Gaf CorporationFloor tile production and productsUS393536411 jan 197427 jan 1976Eternit-Werke Ludwig Hatschek & Ucb,S.A.Porous, heat-sensitive substrates coated with synthetic resinsUS39595216 dec 197425 maj 1976Mitsubishi Rayon Co., Ltd.Process for the formation of cured coatingsUS40163063 jul 19755 apr 1977Mitsubishi Rayon Co., Ltd.Process for forming a coated film in waterUS407536621 okt 197621 feb 1978Desoto, Inc.Low gloss radiation cureUS413829923 dec 19776 feb 1979Armstrong Cork CompanyProcess utilizing a photopolymerizable and moisture curable coating containing partially capped isocyanate prepolymers and acrylate monomersUS442178217 jun 198220 dec 1983Armstrong World Industries, Inc.Process for providing improved radiation-curable surface coverings and products produced thereby H�nvisningar finns i f�ljande patent citeras i Registreringsdatum Publiceringsdatum S�kande TitelUS50667132 apr 199019 nov 1991Huels AktiengesellschaftProcess for the preparation of aqueous, radiation-curable urethaneacrylate dispersionsUS55432326 apr 19956 aug 1996Armstrong World Industries, Inc.(Meth) acrylated aromatic polyester floor covering wear layerUS561663017 feb 19951 apr 1997Lord CorporationEster/urethane acrylate hybrid oligomersUS566300310 maj 19962 sep 1997Armstrong World Industries, Inc.(Meth)acrylated, aromatic polyester/highly ethoxylated (meth)acrylate blend floor covering wear layerUS57192279 maj 199717 feb 1998Armstrong World Industries, Inc.Coating compositionUS580090429 okt 19931 sep 1998Awi Licensing Company, Inc.Embossable surface covering with inorganic wear layerUS583093725 maj 19933 nov 1998Congoleum CorporationCoating and wearlayer compositions for surface coveringsUS58435763 nov 19971 dec 1998Armstrong World Industries, Inc.Floor covering with coating compositionUS589158230 jun 19976 apr 1999Armstrong World Industries, Inc.(Meth)acrylated, highly ethoxylated, aromatic polyestersUS631653518 maj 199913 nov 2001Armstrong World Industries, Inc.Coating system and method of applying the sameUS644050015 aug 200027 aug 2002Armstrong World Industries, Inc.Method for manufacturing a surface covering product having a controlled gloss surface coated wearlayerUS656950015 aug 200027 maj 2003Awi Licensing CompanyMethod for controlling gloss levelUS657293231 jan 20023 jun 2003Awi Licensing CompanyProcess for providing a gloss controlled, abrasion resistant coating on surface covering productsUS68906255 feb 200110 maj 2005Awi Licensing CompanySurface covering having gloss in-register and method of makingUS690858524 mar 200321 jun 2005Awi Licensing CompanyPigmented radiation cured wear layerUS690866315 nov 200021 jun 2005Awi Licensing CompanyPigmented radiation cured wear layerUS70982569 okt 200229 aug 2006Microban Products CompanyAntimicrobial radiation curable coatingUS72762658 maj 20022 okt 2007Awi Licensing CompanyMethod of making a surface covering having gloss-in-registerEP0783008A218 nov 19969 jul 1997Armstrong World Industries, Inc.Coating composition and floor covering including the compositionWO2003054045A29 okt 20023 jul 2003Microban Products CompanyAntimicrobial radiation curable coatingRoteraOriginalbildGoogles startsida - Webbplatskarta - Massh�mtningar av USPTO - Sekretesspolicy - Anv�ndarvillkor - Om Google Patent - Skicka feedbackDessa data tillhandah�lls av IFI CLAIMS Patent Services©2012 Google