EP0071749B1 - Novel polyimides and polyamic intermediates thereof - Google Patents
Novel polyimides and polyamic intermediates thereof Download PDF
EP0071749B1
EP0071749B1 EP19820105795 EP82105795A EP0071749B1 EP 0071749 B1 EP0071749 B1 EP 0071749B1 EP 19820105795 EP19820105795 EP 19820105795 EP 82105795 A EP82105795 A EP 82105795A EP 0071749 B1 EP0071749 B1 EP 0071749B1
EP19820105795
EP0071749A3 (en
EP0071749A2 (en
Jules E. Schoenberg
1981-08-12 Priority to US06/292,257 priority Critical patent/US4405770A/en
1981-08-12 Priority to US292257 priority
1982-06-29 Application filed by Indopco Inc filed Critical Indopco Inc
1983-02-16 Publication of EP0071749A2 publication Critical patent/EP0071749A2/en
1983-12-07 Publication of EP0071749A3 publication Critical patent/EP0071749A3/en
1985-11-13 Publication of EP0071749B1 publication Critical patent/EP0071749B1/en
This invention relates to novel polyimides, to end-capped polyimides, and to the polyamic acid and ester intermediates thereof.
Polyimides are synthetic organic resins characterized by repeating imide linkages in the polymer chain which may or may not be end-capped with polymerizable or inert (i.e. non-polymerizable) chemical groups. They are available in both linear and crosslinked forms and are noted for their outstanding chemical and physical properties, particularly their high temperature oxidative stability and strength. In addition to their use as adhesives and molded articles, they may be used as precured films and fibers, curable enamels, and laminating resins.
The polyimides, especially the preferred aromatic polymides, are extremely difficult to process due to their insolubility and extremely high softening points. Early attempts to decrease the softening temperature usually involved the substitution of aliphatic segments into the otherwise aromatic polymers, but this generally resulted in an accompanying decrease in thermooxidative stability. In order to overcome these disadvantages and to improve their processability and mechanical properties, it has been found advantageous to introduce flexibilizing moieties, such as bipyridyl, sulfone, alkylene, or preferably ether or thio bridges, into the polymer chain and thus provide a product with improved flexibility and impact strength. Crosslinking moieties have also been introduced into the polymers by the use of some portion of a more highly functional amine (e.g. triamine) or by the introduction of carboxyl or hydroxyl groups.
A further disadvantage exists if the polyamic acid or ester intermediates will not be used immediately. The solutions, preferably concentrated, must be stored at low temperatures and protected from moisture to prevent premature imidization (i.e. ring closure). In addition, during curing to the fully or partially imidized resin, an appreciable amount of a volatile by-product (e.g. water, alcohol, or hydrohalides depending upon the starting tetracarboxylic acid compound) is formed. This leads to the formation of voids when the resin is used as an adhesive between metal substrates or for forming molded articles. In order to overcome these disadvantages, low molecular weight polyimides endcapped with polymerizable groups such as ethylenically unsaturated groups, have been prepared. These end-capped polyimides can be subsequently cured to void-free, higher molecular weight resins since no volatile by-product is formed.
The present invention provides novel linear, optionally cross-linked, polyimides which contain flexibilizing moieties and which may be, if desired, end-capped with polymerizable or inert groups.
In the first embodiment herein, a polyimide resin is provided which comprises a chain of recurring units of the formula 4-A-B 4K-, wherein A is
wherein R may be an aliphatic organic tetravalent radical containing at least two carbon atoms with no more than two carbonyl groups being attached to any one carbon atom of said tetravalent radical or wherein R may be a cycloaliphatic or aromatic tetravalent radical containing at least one ring with the four carbonyl groups being attached directly to separate carbon atoms in one or two rings of said radical and with each pair of carbonyl groups being attached to adjacent carbon atoms in said ring or rings of said radical; wherein Z is oxygen or sulfur; wherein X and/or Y may be a carbonyl (CO) or carbinol (CHOH) group; wherein the nitrogens may be independently attached to the benzene rings in the 2-, 3-, or 4- positions; wherein isomerism is present when X and/or Y is a carbinol group; and wherein n is greater than 1 and equals the number of mers per molecule.
A novel polyamic resin is provided which comprises a chain of recurring units of the formula (̵A'‾B )̵n, wherein A' is
wherein R1 and R2 may be hydrogen or the same or different hydrocarbon monovalent radicals and wherein B, R, the nitrogen positions, and n are defined as hereinabove.
The novel polyimides are prepared by reacting a tetracarboxylic acid compound, e.g. dianhydrides or diester-diacids, with selected primary aromatic diamines containing a thio or ether bridge, as well as carbonyl and/or carbinol bridges. Typically the reaction is carried out in an inert organic solvent at a temperature which will depend upon the tetracarboxylic compound used. The solution containing the soluble polyamic acid or ester intermediate is heated to a temperature sufficient to effect ring closure to the corresponding polyimide and, if desired, to remove the solvent as well as the by-product(s). If the polyamic acid or ester is insoluble or has partially imidized and come out of solution, it can be recovered and then converted to the fully imidized form by heating.
In the second embodiment herein, end-capped polyimide resins are provided which have one or more of the formulas R3(̵A-B )̵m‾R4, or R'4-A-B )̵m‾A‾R3, or R4 ‾B(̵A‾B)̵m‾R4, wherein A is
wherein R3 is an inert or polymerizable monovalent organic radical derived from an aliphatic, cycloaliphatic, aromatic, or hetereocyclic primary monoamine; R4 is an inert or polymerizable monovalent organic radical derived from an aliphatic, cycloaliphatic, or aromatic monoanhydride; wherein m equals the number of mers per molecule and m is one or greater; and wherein B and R are as defined hereinabove.
End-capped polyamic resins are also provided which have one or more of the formulas R3(̵A'‾B)̵m‾R4, or R3(̵A'‾B)̵m‾A'‾R3, or R4‾B(̵A'‾B)̵R4, wherein A' is
and wherein B, R, R1, R2, R3, R4, and m are as defined hereinabove.
The end-capped polyimides are prepared by reacting a tetracarboxylic acid compound, e.g. dianhydride, with the selected primary aromatic diamines discussed hereinabove and with a polymerizable or inert monoanhydride and/or a polymerizable or inert primary monoamine which act as the end-capping groups. When a polymerizable monoanhydride or monoamine is used, it is preferred to form a low molecular weight polyimide prior to reaction with the end-capping reagent. Typically, the reaction is carried out in an organic solvent at a low or moderately elevated temperature. The stable, soluble polyimides end-capped with polymerizable groups may then be heated to initiate the addition polymerization and the formation of the higher molecular weight polymers.
The primary aromatic diamine can have the formula
wherein X is a carbinol group when Y is a carbonyl group, X is a carbonyl group when Y is a carbinol group, or X and Y are carbinol groups; wherein the nitrogens may be independently attached to the benzene rings in the 2-, 3-, or 4-positions; when X, Y, or X and Y are said carbinol groups.
The diamines are prepared by hydrogenating the corresponding nitro compounds, preferably first to the corresponding carbonly-containing diamine and subsequently to the corresponding carbinol-containing diamine or mixed carbonyl- and carbinol-containing diamine.
The primary aromatic diamine can also have the general formula
wherein X or Y may be a carbonyl or carbinol group and X and Y may be the same or different; wherein the nitrogens may be independently attached to the benzene rings in the 2-, 3-, or 4-positions; and wherein isomerism is present when X, Y, or X and Y are said carbinol groups. It is prepared in a similar manner to the diamines containing the oxygen linkage.
The classes of primary aromatic diamines for use herein include 4,4'-bis(aminobenzoyl)diphenyl ether and the ether derivatives 4,4'-bis[(aminophenyl)hydroxymethyl]diphenyl ether and 4-(aminobenzoyl)-4'-[(aminophenyl)hydroxymethyl]diphenyl ether, as well as all the corresponding classes of thio ethers. The diamines may be prepared by any of the methods conventionally used to prepare aromatic primary amines, such as reduction of the nitro compound or reaction of aryl halides with ammonia. Reduction of the nitro compounds is the simplest and most satisfactory method, and it may be accomplished by catalytic hydrogenation using molecular hydrogen or by chemical reduction using a metal and an acid. Hydrogenation is the preferred method since the dinitro compounds are quantitatively reduced to the diamine compounds; this is an important requirement for obtaining high molecular weight polymers.
The compounds useful as precursors for the aromatic diamines herein may be prepared in very high yields by reacting a 2-, 3-, or 4-nitrobenzoyl halide or mixtures thereof with diphenyl ether or diphenyl sulfide in the presence of aluminum chloride or other Lewis acid to give the corresponding dinitro compound which is subsequently reduced. Alternatively, a 2-, 3-, or 4-halonitrobenzoyl halide or mixtures thereof may be reacted with diphenyl ether or diphenyl sulfide to give the corresponding dihalogen compound which is subsequently treated with ammonia.
Hydrogenation of 4,4'-bis(3-nitrobenzoyl)diphenyl ether under mild conditions using palladium on charcoal as the catalyst reduces only the nitro groups leaving the carbonyl groups intact. Subsequent reduction of the diamine using sodium borohydride as the catalyst reduces both carbonyl groups to carbinol groups. Hydrogenation of the corresponding thio ether using palladium on charcoal reduces only the nitro groups leaving the carbonyl groups intact. Hydrogenation of 4,4'-bis(4-nitrobenzoyl)diphenyl ether using palladium on charcoal reduces, not only the nitro groups, but also some carbonyl groups and the resulting amine is a mixture. The diamines containing carbinol group(s) are a mixture of stereoisomers (R, L, and meso) due to the presence of one (or two) asymmetric carbon atoms in the chain.
By selecting suitable catalysts and reaction conditions the skilled practitioner can selectively reduce only nitro groups to amine groups, subsequently reduce the carbonyl groups to carbinol groups or to a diamine mixture containing carbinol as well as carbonyl groups, or simultaneously reduce the nitro and carbonyl groups.
One or more of the diamines described herein above are reacted in a suitable inert organic solvent with one or more tetracarboxylic acid compound selected from the following group:
(a) dianhydrides of the fomµria
(b) tetraacids of the formula
(c) tetraesters of the formula
(d) diester-diacids of the formula
(e) dihaloformyldiesters of the formula
wherein R is the tetravalent organic radical as hereabove defined; R5 and RS may be the same or different hydrocarbon monovalent radicals, each preferably containing from 1 to 13 carbon atoms (e.g. C1-C13 alkyl radicals or CS-C13 cycloalkyl or aryl radicals); X is a halogen atom, preferably chlorine or bromine; and the arrows indicate isomerism.
Typical dianhydrides suitable for use herein include, for example, 2,2',3,3'-, 2,3,3',4'-, or 3,4,3',4'-benzophenone tetracarboxylic acid dianhydride, pyromellitic dianhydride, 2,2',3,3'- or 3,3',4,4'-, biphenyltetracarboxylic acid dianhydride, thiophene 2,3,4,5-tetracarboxylic acid dianhydride, 2,2-bis(3,4-dicarboxyphenyl)propane dianhydride, bis(3,4-dicarboxyphenyl sulfone dianhydride, perylene 3,4,9,10-tetracarboxylic acid dianhydride, ethylenetetracarboxylic acid dianhydride, 1,2,3,4-butanetetracarboxylic acid dianhydride, bis-(3,4,dicarboxyphenyl)ether dianhydride, and the like. A more extensive listing of suitable dianhydrides may be found in U.S. Pat. No. 3,699,074 issued Oct. 17, 1972 to H. R. Lubowitz et al. Suitable tetracarboxylic acids are listed in U.S. Pat. No. 3,678,005 issued July 18, 1972 to G. Rabilloud et al. Diester diacids derived from the above dianhydrides by reaction with an alcohol are also suitable for use herein.
Reaction conditions used for the preparation of the intermediate will depend, not only upon the aromatic diamine used, but more particularly on the tetracarboxylic acid compound used. It will also depend upon the solvent selected and the percentage and molecular weight of the intermediate desired in the final solution. The preferred methods of preparing the polyamic acid or ester intermediates are by reaction of diamines with either dianhydrides or diester-diacids derived from lower alcohols. The reactions are carried out under anhydrous conditions preferably using pure monomers and dry solvents.
The solvents used should dissolve at least one of the reactants, preferably both the dianhydride and diamine. Provided imidization has not proceeded too far and provided the intermediate is soluble, the solvent should maintain the polyamic acid or ester in solution. Suitable solvents include, for example, N,N-dimethylformamide, N,N-dimethylacetamide, dimethyl sulfoxide, 1-methyl-2-pyrrolidinone, tetramethylurea, and the like. These solvents can be used alone or in combination with other solvents such as benzene, benzonitrile, dioxane, xylene, toluene, and cyclohexane.
The diamine-dianhydride reaction is relatively rapid at low temperatures. It is typically carried out by first dissolving the diamine in the dry solvent, adding the powdered dianhydride or a dilute solution thereof in portions while applying external cooling, and maintaining the temperature at about 10-60'C for about 1 to 6 hours. If pyromellitic dianhydride is used, a somewhat higher temperature may be required to dissolve the dianhydride (preferably below 75°C).
In a preferred method, the dianhydride is first reacted with an anhydrous lower alcohol, such as methanol or ethanol, to form the corresponding diester-diacid. The diamine and solvent are then added and the excess alcohol distilled off. Alternatively, the diesterdiacid may be recovered from the excess alcohol and then added to the dissolved diamine or both diamine and diester-diacid may be separately dissolved and combined. The reaction mixture is heated at about 100-150°C, while continuing to distill off alcohol and water, until the desired molecular weight is reached at which point the reaction vessel is cooled. Since the polymerization does not proceed at lower temperatures, the molecular weight is controlled by the time and temperature of reaction. If desired, a low molecular weight intermediate may be formed and then post cured, during use, to the higher molecular weight intermediate prior to full imidization. Alternatively, a higher molecular weight intermediate, which requires no post cure, can be prepared.
Generally the polyamic acid or ester intermediate is obtained at 40 to 70% solids when low molecular weight intermediates are formed and at 10 to 40% solids when high molecular weight intermediates are formed. The solution stability of the intermediates is sensitive to temperature, concentration, and moisture. Concentrated solutions are more stable than dilute solutions and can be stored for long periods at low temperatures if protected from moisture.
After formation of the polyamic acid or ester intermediate, the polyimide is obtained by heating the intermediate to 300°C or by treating the intermediate with chemical cyclizing agents at temperatures of 100°C or lower. Typical cyclizing agents include a dehydrating agent (e.g. acetic anhydride) in combination with a basic catalyst (e.g. pyridine) or a carbodiimide (e.g. dicyclohexylcarbodiimide). A combination of chemical and thermal cyclization may be used.
The end-capped polyimides are prepared by coreacting stoichiometric equivalents of one or more of the above dianhydrides, one or more of the above diamines, and selected primary monoamines and/or monoanhydrides. The molecular weight is controlled by the stoichiometry. Preferably, the monoamine and/or monoanhydride should be present in an amount sufficient to completely end-cap the polymer depending upon its molecular weight. It is thus essential that the total chemical equivalents of primary amine (i.e. diamine or diamine plus monoamine) equal the total equivalents of anhydride (i.e. dianhydride or dianhydride plus monoanhydride). If both end groups are not to be capped, then equivalent amounts of primary amine and anhydride are not necessary.
The monoanhydrides and monoamines suitable for use herein are those which are inert or thermally polymerizable by an addition reaction so that no volatile gases are formed as a by-product. Typical of such polymerizable monofunctional reactants are cis-endo-5-norbornene-2,3-dicarboxylic anhydride, often called Nadic anhydride (trademark of Allied Chemical Co.), maleic anhydride, 3-aminophenyl acetylene, 3-cyanoaniline, and the like. Typical inert monofuctional reactants are phthalic anhydride, 4-acetamido- phthalic anhydride, 4-acetamido-aniline, and the like.
Polymerization to low molecular weight, substantially completely imidized polymers can be carried out in two or three steps using the conventional reaction conditions and solvents discussed hereinabove. Preferably, the dianhydride and diamine are reacted in a suitable solvent to form a comparatively low molecular weight, soluble polyamic acid or ester intermediate; then the intermediate is reacted with the monofunctional reactant(s) to end-cap the intermediate; and finally the end-capped intermediate is imidized until ring closure is substantially complete as indicated by the cessation of the formation of volatile by-product(s). If the dianhydride, diamine, and monofunctional reactant are polymerized in one step, it is more difficult to control the molecular weight and insoluble intermediates and/or insoluble fully imidized polymers may be formed. It may be possible to recover the insoluble resin, to isolate the soluble resin by coagulation with a miscible, non-solvent such as water, and to blend various proportions of the two resins in the presence or absence of a liquid vehicle. If a liquid is used, it is removed prior to thermal conversion (curing) to the higher molecular weight addition polymer. The purpose of the blend is to form a homogeneous mass which can be fused at a temperature below that at which the end-capped polyimide homopolymerizes.
Curing of the end-capped polymer may be achieved at moderately high temperatures (e.g. 175‾600°C), if necessary with the use of moderate to high pressure (1.03-68.9.105 Pa [15-1000 p.s.i.]). The conditions required will, of course, depend upon the monofunctional reactant(s) used. In some cases, a catalyst may facilitate the cure or a post-cure after the desired application may be desirable.
Both the thermoplastic and thermosetting resins, which may or may not be fully imidized and which may or may not be crosslinked depending upon the presence or absence of carbinol groups, can be used as moldings or adhesives.
The resulting polyamic acid or ester solutions or end-capped polyimide solutions herein, which are usually smooth viscous solutions, can be applied to suitably prepared substrate surfaces; if desired, they may be formulated with fillers, thickeners, pigments, etc. They may be used with or without supports such as glass fabric. Alternatively, they may be cast into a film from solution and then applied or even applied as a slurry or melt. If necessary, the substrates are allowed to stand to permit some or all of the solvent to evaporate. The treated surfaces to be bonded are assembled together by means of a clamp or press and the assembled substrates are heated. If a polyamic acid or ester is used, the assembled substrates are heated to a temperature above the intermediate's glass transition temperature for a time sufficient to effect ring closure, to volatilize the by-product formed, and, if necessary, to volatize some or all of the solvent. If a polymerizable end-capped polyimide is used, the assembled structures are heated to a temperature sufficient to activate the end groups and form the higher molecular weight addition polymer. If fully imidized and/or polymerized to the desired degree prior to application, no post cure after application is needed. A post cure may be desirable to effect crosslinking in the polyimides containing carbinol groups. Because the adhesives adhere to a variety of different materials, including metals, non-metals, ceramics, etc., they may be utilized in a large number of applications.
The resins can also be used to form filled or unfilled molded articles. The end-capped polyimide resins are especially useful for preparing molded articles since the subsequent curing does not form a volatile by-product and the molded articles are void-free. Compression molding temperatures will depend upon whether the resin is thermoplastic or thermosetting. Thermosetting resins are typically heated at 330-350°C and 205.6-344.5.105 Pa (3000-5000 p.s.i.), and the resin is kept in the mold for at least 5 minutes for good flow prior to cooling to 250°C or less for demolding. Thermoset resins and some thermoplastics that behave like thermosets can be compression molded at 218°C/205.6·10° Pa (3000 p.s.i.) in 2-10 minute cycles, transfer molded at 193°C/205.6.105 Pa (3000 p.s.i.) in 1-5 minute cycles, injection molded at 689·105 Pa (10,000 p.s.i.) in 60 second cycles with mold temperatures of 238°C and barrel temperatures of 93°C, or free sintered to 249°C after a 15 second/1033.5.105 Pa (15,000 p.s.i.) cold forming.
In the examples which follow, all parts and percentages are given by weight and all temperatures are in degrees Celsius unless otherwise noted. Inherent viscosities were determined on 1 g./dl. solutions at 25°C in a mixture of 86% 1-methyl-2-pyrrolidinone and 14% methanol unless otherwise noted. The lap shear strength was determined using chromic acid treated aluminum panels having the dimensions 2.54 cm. by 15.2 cm. by 0.16 cm. A small amount of the polymer solution was applied to the surface of one panel near one edge. The second panel was pressed against the first to form an adhesive film such that where was a 1.27 cm. overlap for each panel and hence a bonding area of 3.22 cm.2. The panels were clamped together by means of a spring clip, and dried at 150°C and cured at 275°C. After equilibration to ambient temperature, the panels were pulled apart with an Instron Tensile Tester at a crosshead operation speed of 0.127 cm./min. (0.05 in./min.). The values given were the average of two determinations.
This example describes the preparation of a polymer by the reaction of 4,4'-bis(3-aminobenzoyl)diphenyl ether with the methyl diester of 3,3', 4,4'-benzophenone tetracarboxylic acid and its use as an adhesive. It also describes the preparation of 4,4'-bis-(3-nitrobenzoyl)-diphenyl ether and its subsequent reduction to the corresponding diamine.
A total of 242.7 parts (1.82 moles) of aluminum chloride was added over 1 h to a cooled solution of 102.1 parts (0.60 mole) diphenyl ether and 233.8 parts (1.26 moles) 3-nitrobenzoyl chloride in 600 ml. of 1,2-dichloroethane. The temperature was maintained at between 10-20°C during the addition. The mixture was then slowly heated to the boiling point and refluxed for 3 h. The solution was cooled and poured into 1700 ml. of a mixture of ice water and concentrated hydrochloric acid (7.5:1). The aqueous layer was decanted off. The product was washed with 1000 ml. ethanol, filtered, dried, and recrystallized from methyl isobutyl ketone. The resulting 4,4'-bis(3-nitrobenzoyl)-diphenyl ether had a melting point of 174-175°C (literature 175°C)..
A total of 70.2 parts (0.15 mole) of the above dinitro compound in 550 ml. dioxane was hydrogenated at 70-80°C using 3.6 parts of 5% palladium on charcoal as the catalyst. Hydrogenation was continued until hydrogen absorption ceased. The solution was filtered, and the product was precipitated by the addition of 500 ml. water. The resulting 4,4'-bis(3-aminobenzoyl)diphenyl ether had a melting point of 131-133°C (literature 150-151°C); NMR analysis indicated that the carbonyl groups were unaffected by the reduction.
A mixture of 9.67 parts (0.03 mole) of 3,3', 4,4'-benzophenone tetracarboxylic acid dianhydride and 20 ml. of methanol was refluxed for 2 hr. with stirring to form the corresponding methyl diester. A total of 12.25 parts (0.03 mole) of the above diamine and 18 parts of 1-methyl-2-pyrrolidinone was added, and the mixture was heated under a nitrogen atmosphere at 77-125°C for 7 h. The distillate was collected in a 25 ml. Dean-Stark receiver. The resulting polymer had an inherent viscosity of 0.20 dl./g. It was used to bond chromic acid treated aluminum panels using the procedure previously described. The adhesive's lap shear strength was 181.8.105 Pa (2640 p.s.i.).
This example describes the preparation of a polymer by the reaction of pyromellitic dianhydride and the diamine of Example I.
A total of 8.17 parts (0.02 mole) of 4,4'-bis(3-aminobenzoyl)diphenyl ether in 30 parts 1-methyl-2-pyrrolidinone was treated over a 7 min. period with 4.36 parts (0.02 mole) of pyromellitic dianhydride. The residual dianhydride was washed in with 7 parts of 1-methyl-2-pyrrolidinone. The temperature rose to about 35°C and gradually dropped back to ambient temperature. The solution was stirred for 5 hr. The resulting polymer had inherent viscosity of 0.54 dl./g. in 1-methyl-2-pyrrolidinone. It was used as an adhesive as previously described; the lap shear strength was 880 p.s.i.
This example describes the preparation of the diamine 4,4'-bis[(3-aminophenyl)hydroxy- methylldiphenyl ether and its polymerization with the methyl diester of 3,3', 4,4'-benzophenone tetracarboxylic acid.
A cooled solution (0.08 mole) of 32.6 parts of 4-4'-bis(3-aminobenzoyl)diphenyl ether (see Example I for the preparation thereof) in 200 ml. tetrahydrofuran was treated over a 1.5 h period with a solution of 6.05 parts (0.16 mole) sodium borohydride in 80 ml. water. The reaction mixture was maintained at room temperature for 3 days and then diluted with 100 ml. water. The solvent was removed by vacuum distillation. The product was dissolved in 200 ml. ethyl ketone, washed with water, dried over magnesium sulfate, and precipitated by the addition of 3 volumes of cyclohexane. It was dissolved in methanol and vacuum dried to yield 28.8 parts of a mixture of stereoisomers of 4,4'-bis[l3-aminophenyl)hydroxymethyl]diphenyl ether having a melting point of 55-66°C.
The polymerization was carried out using the procedure described in Example I except that the mixture was heated for only 1.5 h since longer heating times led to gellation of the polymer. The amounts of reactants used were 9.67 parts (0.03 mole) 3,3', 4,4'-benzophenone tetracarboxylic acid dianhydride, 20 ml. methanol, and 12.37 parts'(0.03 mole) of the above diamine in 22 parts 1-methyl-2-pyrrolidinone. The resulting polymer had an inherent viscosity of 0.28 dl./g.
This example describes the preparation of a diamine mixture containing some carbinol groups and its polymerization with the methyl diester of 3,3',4,4'-benzophenone tetracarboxylic acid. It also describes the preparation of 4,4'-bis(4-nitrobenzoyl)diphenyl ether and its subsequent reduction to the corresponding diamine mixture.
4-Nitrobenzoyl chloride was reacted with diphenyl ether using the quantities and procedure of Example I. The resulting 4,4'-bis(4-nitrobenzoyl)diphenyl ether was recrystallized from y-butyrolactone; it had a melting point of 230-232°C (literature 226°C).
A total of 58.5 parts (0.125 mole) of the above dinitro compound in 500 ml. dimethylformamide was hydrogenated at 60―70°C in the presence of 3 parts of 5% palladium on charcoal until the rate of hydrogen uptake decreased. The product was precipitated by the addition of 1000 ml. of water. The yield was 38.5 parts (75.5%). The resulting diamine, which was probably a mixture of 4,4'-bis(4-aminobenzoyl)diphenyl ether (literature m.p. 177-178°C) and the novel diamines 4-(4-aminobenzoyl)-4'-[(4-aminophenyl)hydroxymethyl]diphenyl ether, 4-[(4-aminophenyl)hydroxymethyl)]-4'-(4-aminobenzoyl)diphenyl ether, and 4,4'- bis[(4-aminophenyl)hyroxymethyl]diphenyl ether, had a melting point of 152-154°C. NMR analysis indicated that about 10% of the carbonyl groups were reduced to carbinol groups.
The polymerization was carried out using the procedure described in Example except that the mixture was heated for only 1.5 h. The amount of reactants used was 9.67 parts (0.03 mole) 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride, 20 ml. methanol, and 12.24 parts (0.03 mole) of the above diamine mixture in 22 parts 1-methyl-2-pyrrolidinone. The resulting polymer had an inherent viscosity of 0.15 dl./g. When cured and evaluated as previously described, the adhesive had a tensile lap shear strength of 289.3,105 Pa (4200 p.s.i.).
This example describes the preparation of the diamine 4,4'-bis(3-aminobenzoyl)diphenyl sulfide and its polymerization with the methyl diester of 3,3',4,4'-benzophenone tetracarboxylic acid. It also describes the preparation of 4,4'-bis(3-nitrobenzoyl)diphenyl sulfide and its subsequent reduction to the diamine.
A mixture of 46.6 parts (0.25 mole) of phenyl sulfide and 98.4 parts (0.53 mole) of 3-nitrobenzoyl chloride in 250 ml. 1,2-dichloroethane was treated with 101.9 parts (0.76 mole) aluminum chloride using the procedure described in Example I. The crude product was recrystallized from -butyrolactone. The resulting 4,4'-bis(3-nitrobenzoyl)diphenyl sulfide had a melting point of 229-230°C (literature 229-230°C).
A total of 36.3 parts (0.075 mole) of the above dinitro compound in 375 ml. dimethylformamide was hydrogenated at 100-110°C using 3.6 parts of 5% palladium on charcoal as the catalyst. The mixture was filtered, and the product was precipitated by the addition of 600 ml. of water. The resulting 4,4'-bis(3-aminobenzoyl)diphenyl sulfide had a melting point of 163-164°C. The yield was 30.3 parts (95.2%). NMR and infrared spectroscopy confirmed the presence of the carbonyl groups.
The polymerization was carried out using the procedure described in Example I except that the solution was cooled prior to the addition of the diamine and the final solution was heated for 1.5 h at 110-145-C after the removal of the excess methanol. The reactant amounts used were 6.44 parts (0.02 mole) 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride, 13 ml. methanol, and 8.49 parts (0.02 mole) of the above diamine in 15 parts 1-methyl-2-pyrrolidinone. The resulting polymer had an inherent viscosity of 0.15 dl./g. It was used as an adhesive as previously described; the lap shear strength was 192.9-105 Pa (2800 p.s.i.).
This example describes the preparation of a polyimide of 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride and 4,4'-bis-(3-aminobenzoyl)diphenyl ether which is end-capped with the polymerizable primary monoamine 3-aminophenyl acetylene.
A solution of 8.06 parts (0.025 mole) 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride in 20 parts 1-methyl-2-pyrrolidinone at room temperature was treated in portions with with 8.17 parts (0.020 mole) 4,4'-bis(3-aminobenzoyl)diphenyl ether (see Example I for the preparation of this diamine). Residual diamine was washed in with 4 parts 1-methyl-2-pyrrolidinone, and the reaction mixture was stirred for 1 h at 50-660C. A total of 1.17 parts (0.010 mole) 3-aminophenyl acetylene in 3 parts 1-methyl-2-pyrrolidinone was added, and the reaction mixture was allowed to remain overnight at ambient temperature. The flask was equipped with a 25 ml. Dean-Stark trap and 40 ml. of toluene were added. The solution was refluxed for 6.5 h while the water was collected and the toluene was returned. The toluene was then removed by vacuum distillation. The resulting end-capped polymer had an inherent viscosity of 0.12 dl./g.
This example describes the preparation of a polyimide of 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride and 4,4'-bis-(3-aminobenzoyl)diphenyl ether which is end-capped with the polymerizable monoanhydride cis-endo-5-norbornene-2,3-dicarboxylic anhydride. If one does not wish to form the polymerizable polyimide, the polyimide may be end-capped with phthalic anhydride using the mole ratios given below.
A solution of 10.21 parts (0.025 mole) 4,4'-bis(3-aminobenzoyl)-diphenyl ether in 20 parts 1-methyl-2-pyrrolidinone at 25°C was treated with 6.44 parts (0.020 mole) 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride. Residual dianhydride was washed in with 3 parts 1-methyl-2-pyrrolidinone, and the reaction mixture was stirred at 21-35°C for 2.5 h. A total of 1.64 parts (0.01 mole) of cis-endo-5-norbornene 2,3-dicarboxylic anhydride was added followed by 3 parts of 1-methyl-2-pyrrolidinone. The solution was left overnight at room temperature, 40 ml. toluene were added, and the ring closure was carried out as in Example VI. The end-capped polymer had an inherent viscosity of 0.23 dl./g.
Summarizing, novel linear polyimides, optionally end-capped with inert or polymerizable monoanhydride and/or monoamine groups, and the polyamic acid and ester intermediates thereof are provided.
1. A polyimide resin, comprising a chain of recurring units of the formula 4-A-B )̵n, characterized in that A is
where R may be an aliphatic organic tetravalent radical containing at least two carbon atoms with no more than two carbonyl groups being attached to any one carbon atom of said tetravalent radical or where R may be a cycloaliphatic or aromatic tetravalent radical containing at least one ring with the four carbonyl groups being attached directly to separate carbon-atoms in one or two rings of said radical and with each pair of carbonyl groups being attached to adjacent carbon atoms in said ring or rings of said radical; where Z is oxygen or sulfur; where X or Y or X and Y may be a carbonyl or carbinol group; where the nitrogens may be independently attached to the benzene rings in the 2-, 3-, or 4-positions; where isomerism is present when X or Y or X and Y are said carbinol groups; and where n is greater than 1 and equals the number of mers per molecule.
2. A polyamic resin, comprising a chain of recurring units of the formula (̵A'‾B)̵, characterized in that A' is
where R may be an aliphatic organic tetravalent radical containing at least two carbon atoms with no more than two carbonyl groups being attached to any one carbon atom of said tetravalent radical or where R may be a cycloaliphatic or aromatic tetravalent radical containing at least one ring with the four carbonyl groups being attached directly to separate carbon atoms in one or two rings of said radical and with each pair of carbonyl groups being attached to adjacent carbon atoms in said ring or rings of said radical; where R1 and R2 may be hydrogen or the same or different hydrocarbon monovalent radicals; where Z is oxygen or sulfur; where X or Y or X and Y may be a carbonyl or carbinol group; wherein the nitrogen may be independently attached to the benzene rings in the 2-, 3-, or 4-positions; where isomerism is present when X or Y or X and Y are said carbinol groups; and wherein n is greater than 1 and equals the number of mers per molecule.
3. The resin of Claim 1 or 2, characterized in that R is the tetravalent residue derived from a 3,3',4,4'-benzophenone tetracarboxylic acid compound, Z is oxygen or sulfur, X and Y are carbonyl groups, and both nitrogens are in the 3-position.
4. The resin of Claim 1 or 2 characterized in that R is the tetravalent residue derived from a 3,3',4,4'-benzophenone tetracarboxylic acid compound, Z is oxygen, X and Y are carbinol groups, and both nitrogens are in the 3-position.
5. The resin of Claim 1 or 2 characterized in that R is the tetravalent residue derived from a 3,3',4,4'-benzophenone tetracarboxylic acid compound, Z is oxygen, X and Y are carbonyl groups, carbinol groups, or mixtures of carbonyl and carbinol groups, and both nitrogens are in the 4-position.
6. The resin of Claim 1 or 2 characterized in that R is the tetravalent residue derived from a pyromellitic acid compound, Z is oxygen, X and Y are carbonyl groups, and both nitrogens are in the 3-position.
7. An end-capped polyimide resin, comprising a chain of recurring units having one or more of the formulas: R3(̵A‾B)̵m‾R4, or R3(̵A‾B)̵m‾A‾R3, or R4 ‾B(̵A‾B)̵m‾R4, characterized in that A is
where R3 is an inert or polymerizable monovalent organic radical derived from an aliphatic, cycloaliphatic, or aromatic primary monoamine; R4 is an inert or polymerizable monovalent organic radical derived from an aliphatic, cycloaliphatic, or aromatic monoanhydride; where R may be an aliphatic organic tetravalent radical containing at least two carbon atoms with no more than two carbonyl groups being attached to any one carbon atom of said tetravalent radical or where R may be a cycloaliphatic or aromatic tetravalent radical containing at least one ring with the four carbonyl groups being attached directly to separate carbon atoms in one or two rings of said radical and with each pair of carbonyl groups being attached to adjacent carbon atoms in said ring or rings of said radical; where Z is oxygen or sulfur; wherein X or Y or X and Y may be a carbonyl or carbinol group; wherein the nitrogens may be independently attached to the benzene rings in the 2-, 3-, or 4-positions; where isomerism is present when X or Y or X and Y are said carbinol groups; and where m is one or greater and equals the number of mers per molecule.
8. An end-capped polyamic resin, comprising a chain of recurring units having one or more of the following formulas: R3(̵A'‾B)̵m‾R4, or R3-(-A'-B+m-A'-R3, or R4 ‾B(̵A'‾B)̵m‾R4; characterized in that A' is
where R3 is an inert or polymerizable monovalent organic radical derived from an aliphatic, cycloaliphatic, or aromatic primary monoamine; R4 is an inert or polymerizable monovalent organic radical derived from an aliphatic, cycloaliphatic, or aromatic monoanhydride; where R may be an aliphatic organic tetravalent radical containing at least two carbon atoms with no more than two carbonyl groups being attached to any one carbon atom of said tetravalent radical or where R may be a cycloaliphatic or aromatic tetravalent radical containing at least one ring with the four carbonyl groups being attached directly to separate carbon atoms in one or two rings of said radical and with each pair of carbonyl groups being attached to adjacent carbon atoms in said ring or rings of said radical; where R1 and R2 may be hydrogen or the same or different hydrocarbon monovalent radicals; where Z is oxygen or sulfur; where X or Y or X and Y may be a carbonyl or carbinol group; wherein the nitrogens may be independently attached to the benzene rings in the 2-, 3-, or 4-positions; where isomerism is present when X or Y or X and Y are said carbinol groups; and where m is one or greater and equals the number of mers per molecule.
9. The resin of Claim 7 or 8, characterized in that R is the tetravalent residue derived from a 3,3',4,4'-benzophenone tetracarboxylic acid compound, Z is oxygen, X and Y are carbonyl groups, both nitrogens are in the 3-position, and R3 is a polymerizable monovalent organic radical derived from 3-aminophenyl acetylene.
10. The resin of Claim 7 or 8 characterized in that R is the tetravalent residue derived from a 3,3',4,4'-benzophenone tetracarboxylic acid compound, Z is oxygen, X and Y are carbonyl groups, both nitrogens are in the 3-position, and R4 is a polymerizable monovalent organic radical derived from cis-endo-5-norbornene-2,3-dicarboxylic anhydride.
11. The resin characterized in that it results from the addition polymerization of the composition of Claims 9 or 10.
EP19820105795 1981-08-12 1982-06-29 Novel polyimides and polyamic intermediates thereof Expired EP0071749B1 (en)
US06/292,257 US4405770A (en) 1981-08-12 1981-08-12 Novel polyimides, and polyamic acid and ester intermediates thereof
US292257 1981-08-12
EP0071749A2 EP0071749A2 (en) 1983-02-16
EP0071749A3 EP0071749A3 (en) 1983-12-07
EP0071749B1 true EP0071749B1 (en) 1985-11-13
ID=23123889
EP19820105795 Expired EP0071749B1 (en) 1981-08-12 1982-06-29 Novel polyimides and polyamic intermediates thereof
US (1) US4405770A (en)
EP (1) EP0071749B1 (en)
CA (1) CA1219398A (en)
JPH0373574B2 (en) * 1983-01-25 1991-11-22 Showa Denko Kk
US4562100A (en) * 1984-09-14 1985-12-31 E. I. Du Pont De Nemours And Company Polyimide coating compositions from diesterified anhydride and aromatic diamine
JPH072843B2 (en) * 1985-07-15 1995-01-18 三菱油化株式会社 Aromatic thioether - ether amide imide polymer
US4742153A (en) * 1986-04-16 1988-05-03 E. I. Du Pont De Nemours And Company Process for preparing polyimides
JP2744786B2 (en) * 1987-01-20 1998-04-28 鐘淵化学工業株式会社 Polyimides and polyamic acid used therein is excellent in thermal dimensional stability
EP0392680A3 (en) * 1989-04-13 1992-03-04 Imperial Chemical Industries Plc Aromatic compounds
US5104944A (en) * 1989-07-18 1992-04-14 International Business Machines Corporation Process for nucleophilic derivatization of materials having an imide group conjugated to an aromatic moiety
EP0453700A3 (en) * 1990-04-26 1991-12-27 Rohr Industries, Inc. New dimer for synthesis of high performance polymer matrix composites
JP2960281B2 (en) * 1992-05-25 1999-10-06 三井化学株式会社 Polyimide and manufacturing method thereof
DE4229180A1 (en) * 1992-09-02 1994-03-03 Basf Ag recrystallizable polyimides
JP4986071B2 (en) * 2007-03-30 2012-07-25 Ｊｓｒ株式会社 Resin composition, the cured product and an optical member
FR1601091A (en) * 1968-03-21 1970-08-10
FR2031847A5 (en) * 1969-02-10 1970-11-20 Inst Francais Du Petrole
CH621768A5 (en) * 1976-06-15 1981-02-27 Ciba Geigy Ag
1981-08-12 US US06/292,257 patent/US4405770A/en not_active Expired - Lifetime
1982-06-17 CA CA000405438A patent/CA1219398A/en not_active Expired
1982-06-29 EP EP19820105795 patent/EP0071749B1/en not_active Expired
EP0071749A3 (en) 1983-12-07
CA1219398A1 (en)
CA1219398A (en) 1987-03-17
US4405770A (en) 1983-09-20
EP0071749A2 (en) 1983-02-16
EP0209114B1 (en) 1992-09-23 Amphiphilic polyimide precursor and process for preparing the same
EP0077718B1 (en) 1987-01-14 Process for preparing aromatic polyimide compositions with a high solubility and the uses thereof
Banerjee et al. 2003 Synthesis and properties of fluorinated polyimides. 3. Derived from novel 1, 3-bis [3′-trifluoromethyl-4′(4 ″-amino benzoxy) benzyl] benzene and 4, 4-bis [3′-trifluoromethyl-4′(4-amino benzoxy) benzyl] biphenyl
EP0276922A1 (en) 1988-08-03 Melt-moldable crystalline polyimide polymer