Matched Legal Cases: ['application No. 41', 'application No. 2624302', 'application No. 3822999', 'application No. 40', 'application No. 69417103', 'application No. 694', 'application No. 196', 'application No. 19813286', 'application No. 248', 'application No. 0', 'application No. 2524541', 'application No. 2805906', 'Application No. 102', 'Application No. 102']

Process And Plant For Producing Metal Oxide From Metal Compounds - Patent 7662351
United States Patent: 7662351
7,662,351
Process and plant for producing metal oxide from metal compounds
The present invention relates to a process for producing metal oxide from
metal compounds, in particular metal hydroxide or metal carbonate, in
which the metal compound is conveyed into a reactor (25) with fluidized
bed, heated there to a temperature of 650 15 to 1150.degree. C. by
combustion of fuel, and metal oxide is generated, as well as to a
corresponding plant. To improve the utilization of energy, it is proposed
to introduce a first gas or gas mixture from below through a gas supply
tube (26) into a mixing chamber (20) of the reactor (25), the gas supply
tube (26) being at least partly surrounded by a stationary annular
fluidized bed (27) which is fluidized by supplying fluidizing gas, and 20
to adjust the gas velocities of the first gas or gas mixture and of the
fluidizing gas for the annular fluidized bed (27) such that the
Particle-Froude numbers in the gas supply tube (26) lie between 1 and
100, in the annular fluidized bed (27) between 0.02 and 2, and in the
mixing chamber (20) between 0.3 and 30.
Hirsch; Martin (Friedrichsdorf, DE), Stockhausen; Werner (Bad Vilbel, DE), Stroder; Michael (Neu-Anspach, DE)
10/540,071
PCT/EP03/14213
WO2004/056701
102 60 739
423/111  ; 422/145; 422/146; 422/147; 432/15; 432/16; 432/17; 75/366
C01F 1/00&amp;nbsp(20060101); B22F 1/00&amp;nbsp(20060101); F27B 15/00&amp;nbsp(20060101); F27B 15/08&amp;nbsp(20060101); F27B 15/12&amp;nbsp(20060101); F27B 15/14&amp;nbsp(20060101); F27B 15/16&amp;nbsp(20060101); F27B 15/18&amp;nbsp(20060101)
423/592.1,624-625,111 75/366 432/14-17 422/145-147
Boisture et al.
Bourguet et al.
Lapple et al.
Daradimos et al.
Kroehl et al.
Schreieder et al.
Goudmand et al.
6368389
6416721
6827786
2002/0113024
2004/0042952
2006/0162500
2006/0167047
2006/0230879
2006/0230880
2006/0231433
Rufo et al.
2006/0231466
2006/0237300
Stroder et al.
2006/0249100
2006/0263292
2006/0278566
2007/0137435
2008/0124253
199894057
40 15031
41 03 965
0 575 245
196 09284
19841513
198 13 286
694 16458
694 17103
0246191
0630 683
0762990
WO-8909290
WO-9011824
WO-9808989
WO 01/44719
WO-2055744
WO 2004/056465
WO-4056467
US. Appl. No. 10/540,436, filed Nov. 10, 2005, Dirk Nuber et al. cited by other
U.S. Appl. No. 10/540,438, filed Jun. 6, 2006, Jochen Freytag et al. cited by other
U.S. Appl. No. 10/540,437, filed May 10, 2006, Michael Stroder et al. cited by other
U.S. Appl. No. 10/540,434, filed May 16, 2006, Martin Hirsch et al. cited by other
U.S. Appl. No. 10/540,435, filed Mar. 27, 2006, Andreas Orth et al. cited by other
U.S. Appl. No. 10/540,073, filed Jul. 19, 2006, Andreas Orth et al. cited by other
U.S. Appl. No. 10/540,355, filed Mar. 24, 2006, Michael Stroder et al. cited by other
U.S. Appl. No. 10/540,497, filed May 31, 2006, Michael Stroder et al. cited by other
U.S. Appl. No. 10/540,352, filed Mar. 21, 2006, Michael Stroder et al. cited by other
U.S. Appl. No. 10/540,376, filed Jan. 17, 2006, Dirk Nuber et al. cited by other
English abstract of German application No. 41 03 965, print date: Jun. 2005. cited by other
English abstract of German application No. 2624302, print date: Jun. 2005. cited by other
English abstract of German application No. 3822999, print date: Jun. 2005. cited by other
English abstract of German application No. 40 15031, print date: Jun. 2005. cited by other
English abstract of German application No. 69417103, print date: Jun. 2005. cited by other
English abstract of German application No. 694 16458, print date: Jun. 2005. cited by other
English abstract of German application No. 196 09284, print date: Jun. 2005. cited by other
English abstract of German application No. 19813286, print date: Jun. 2005. cited by other
English abstract of German application No. 248 109, print date: Jun. 2005. cited by other
English abstract of German application No. 0 575 245, print date: Jun. 2005. cited by other
English abstract of German application No. 2524541, print date: Jun. 2005. cited by other
English abstract of German application No. 2805906, print date: Jun. 2005. cited by other
&quot;Ullmann&#39;s Encyclopedia of Industrial Chemistry&quot; 5th edition, 1994, vol. A25, pp. 574-575. cited by other
Sander U H F et al. &quot;Production from elemental sulphur Sulphur, Sulphur Dioxide and Sulphuric Acid. Introduction to their Industrial Chemistry and Technology, London, British Sulphur Corporation, GB, 1984, pp. 168-176, XP0006085. cited by other
Barbara Elvers et al. &quot;Ullmann&#39;s Encyclopedia of Industrial Chemistry&quot;, Fifth, Completely Revised Edition, vol. A25, VCH, pp. 567-577. cited by other
International Search Report for International No. PCT/EP2007/001128 mailed on Aug. 31, 2007. cited by other
Notice of Allowance dated Feb. 06, 2009 for U.S. Appl. No. 10/540,355 filed Feb. 2, 2006. cited by other
Vijay, &quot;Preoxidation and Hydrogen Reduction of Ilmenite in a Fluidized Bed Reactor&quot; XP 000632260, Metallurgical and Material Transactions B, vol. 27B, Oct. 1996, 9. 731-738. cited by other
Kim, Y.T. et al, &quot;Entrainment of solids in an internally circulating fluidized bed with draft tube&quot;. Chemical Engineering Journal, vol. 66, (1997), p. 105-110. cited by other
Notice of Allowance dated Jul. 20, 2009 for U.S. Appl. No. 10/540,435 filed Mar. 27, 2006. cited by other
Office Action dated Sep. 19, 2008 for U.S. Appl. No.10/540,435 filed Mar. 27, 2006. cited by other
Office Action dated Feb. 11, 2009 for U.S. Appl. No. 10/540,497 filed May 31, 2006. cited by other
Office Action dated Aug. 12, 2008 for U.S. Appl. No. 10/540,355 filed Feb. 2, 2006. cited by other
Office Action dated Mar. 27, 2008 for U.S. Appl. No. 10/540,355 filed Feb. 2, 2006. cited by other
Office Action dated Jul. 8, 2009 for U.S. Appl. No. 10/540,073 filed Jul. 19, 2006. cited by other
Office Action dated Jan. 26, 2009 for U.S. Appl. No. 10/540,073 filed Jul. 19, 2006. cited by other
Office Action dated Aug. 21, 2008 for U.S. Appl. No. 10/540,073 filed Jul. 19, 2006. cited by other
Office Action dated May 13, 2009 for U.S. Appl. No. 10/540,376 filed Jan. 17, 2006. cited by other
Office Action dated Oct. 9, 2008 for U.S. Appl. No. 10/540,376 filed Jan. 17, 2006. cited by other
Office Action dated Jun. 2, 2008 for U.S. Appl. No. 10/540,376 filed Jan. 17, 2006. cited by other
Office Action dated Sep. 17, 2008 for U.S. Appl. No. 10/540,434 filed May 16, 2006. cited by other
Notice of Allowance dated Dec. 3, 2008 for U.S. Appl. No.10/540,437 filed May 10, 2006. cited by other
Office Action dated Jun. 16, 2008 for U.S. Appl. No. 10/540,437 filed May 10, 2006. cited by other
Office Action dated Apr. 17, 2009 for U.S. Appl. No. 10/540,438 filed Jun. 6, 2006. cited by other
Notice of Allowability for U.S. Appl. No. 10/540,438 filed Jun. 6, 2006. cited by other
Office Action dated Jul. 10, 2007 for U.S. Appl. No. 10/540,438 filed Jun. 6, 2006. cited by other
Office Action dated Jul. 14, 2008 for U.S. Appl. No. 10/540,436 filed Nov. 10, 2005. cited by other
Office Action dated Oct. 30, 2008 for U.S. Appl. No. 10/540,436 filed Nov. 10, 2005. cited by other
Office Action dated Apr. 17, 2009 for U.S. Appl. No. 10/540,436 filed Nov. 10, 2005. cited by other
Office Action dated Dec. 27, 2007 for U.S. Appl. No. 10/540,436 filed Nov. 10, 2005. cited by other.
1.  A process for producing metal oxide from a metal compound in which the metal compound is conveyed into a reactor with fluidized bed, heated there to a temperature of
650 to 1150.degree.  C. by combustion of fuel, and metal oxide is generated, comprising introducing a first gas or gas mixture from below through a gas supply tube into a mixing chamber of the reactor located above the orifice region of the gas supply
tube, the gas supply tube being at least partly surrounded by a stationary annular fluidized bed which is fluidized by supplying fluidizing gas, wherein the gas flowing through the gas supply tube entrains solids from the fluidized bed into the mixing
chamber when passing though the upper orifice region of the gas supply tube, and adjusting the gas velocities of the first gas or gas mixture as well as of the fluidizing gas for the annular fluidized bed such that the Particle-Froude numbers in the gas
supply tube lie between 1 and 100, in the annular fluidized bed between 0.02 and 2, and in the mixing chamber between 0.3 and 30.
2.  The process as claimed in claim 1, wherein the Particle-Froude number in the gas supply tube lies between 1.15 and 20.
3.  The process as claimed in claim 1 wherein the Particle-Froude number in the annular fluidized bed lies between 0.115 and 1.15.
4.  The process as claimed in claim 1, wherein the Particle-Froude number in the mixing chamber lies between 0.37 and 3.7.
5.  The process as claimed in claim 1, wherein the filling level of solids in the reactor is adjusted such that the annular fluidized bed extends beyond the upper orifice region of the gas supply tube and wherein solids are introduced into the
first gas or gas mixture.
6.  The process as claimed in claim 1, wherein the metal compound is aluminum hydroxide with a grain size of less than 100 .mu.m.
7.  The process as claimed in claim 1, wherein preheated gas containing oxygen is supplied to the reactor through the gas supply tube.
8.  The process as claimed in claim 1, wherein gaseous and/or liquid fuel is introduced into the reactor through the gas supply tube.
9.  The process as claimed in claim 1, wherein gaseous fuel and/or air is introduced into the lower region of the annular fluidized bed of the reactor.
10.  The process as claimed in claim 1, wherein the pressure in the reactor lies between 0.8 and 10 bar.
11.  The process as claimed in claim 1, wherein the solids are suspended, dried, preheated and/or partly calcined prior to the heating treatment in at least one preheating stage, wherein the preheating stage comprises a heat exchanger and a
downstream separator.
12.  The process as claimed in claim 11, wherein the heat exchanger is an annular-fluidized-bed heat exchanger comprising a second stationary fluidized bed and a second mixing chamber.
13.  The process as claimed in claim 1, further comprising cooling the reactor by injecting water into the annular fluidized bed.
14.  The process as claimed in claim 11, wherein after the heat treatment 0 to 100% of the product entrained by the exhaust gas of the reactor is discharged via a separator into a preferably fluidizing-gas-operated mixing vessel, and a product
mixture is generated with partly calcined solids.
15.  The process as claimed in claim 1, wherein the product or product mixture is supplied to a cooling system comprising a plurality of cooling stages connected in series.
16.  The process as claimed in claim 15, wherein the gas heated in the cooling stage is supplied to an upstream cooling stage, a preheating stage and/or the reactor.
17.  The process as claimed in claim 1, wherein the metal compound comprises metal hydroxide or metal carbonate.
18.  The process as claimed in claim 12, further comprising cooling the annular-fluidized-bed heat exchanger by injecting water into the annular fluidized bed.  Description
national phase application under 35 U.S.C.  .sctn.371 of International Application No. PCT/EP2003/014213 filed on Dec.  13, 2003, entitled, &quot;Process and Plant for Producing Metal Oxide from Metal Compounds&quot; which claims the benefit of German Patent
Application No. 102 60 739.7 filed on Dec.  23, 2002.
The present invention relates to a process for producing metal oxide from metal compounds, in particular metal hydroxide or metal carbonate, in which the metal compound is conveyed into a fluidized bed reactor, heated there to a temperature of
650 to 1150.degree.  C. by combustion of fuel, and metal oxide is generated, as well as to a corresponding plant.
From EP 0 861 208 B1 there is known a process for producing anhydrous alumina from aluminum hydroxide in a circulating fluidized bed, in which the alumina is first dried in several preheating stages, partly calcined, and in the preheated
condition introduced into a fluidized-bed reactor in which the temperatures lie in the range from 800 to 1000.degree.  C. due to the combustion of fuel, and alumina is generated.  The exhaust gas of the fluidized-bed reactor, which is obtained during the
combustion, is supplied to the preheating stages and utilized energetically.  The metal oxide withdrawn from the reactor is subjected to multi-stage cooling in direct contact with air and at least passed through a direct cooling stage, in which the metal
oxide is pneumatically transported upwards into a separating cyclone via a delivery conduit.  Furthermore, the partly cooled metal oxide is passed through at least one fluidized cooler with indirect cooling.
In the plants known so far, reactors with a stationary or a circulating fluidized bed are used for calcining or heating the solids.  However, the energy utilization of the calcining step, which is achieved when using a stationary fluidized bed,
needs improvement.  On the one hand, this is due to the fact that the mass and heat transfer is rather moderate due to the comparatively low degree of fluidization, and therefore an internal combustion is difficult to control.  In addition, preheating of
combustion air can hardly be integrated in a suspension heat exchanger.  Normally, combustion air is preheated in a suspension heat exchanger by cooling previously calcined or heated solids and using the dust-laden cooling air as combustion air.
However, dust-laden gases are rather not admitted to the fluidizing nozzles of the stationary fluidized bed.  Due to the higher degree of fluidization, circulating fluidized beds on the other hand have better conditions for a mass and heat transfer and
allow the integration of a suspension heat exchanger, but are restricted in terms of their solids retention time due to the higher degree of fluidization.  Therefore, a multi-stage calcination is provided in EP 0 861 298 B1.  Frequently, difficulties
arise in calcining plants due to the pre- or postcombustion of natural gas or other fuels supplied.
Therefore, it is the object of the present invention to improve the conditions for a heat and mass exchange during the calcination of metal compounds such as metal hydroxide or metal carbonate and thereby rather optimally utilize the thermal
energies used.
In accordance with the invention, this object is solved by a process as mentioned above, in which a first gas or gas mixture is introduced from below through a preferably centrally arranged gas supply tube (central tube) into a mixing chamber of
the reactor, the central tube being at least partly surrounded by a stationary annular fluidized bed which is fluidized by supplying fluidizing gas, and in which the gas velocities of the first gas or gas mixture as well as of the fluidizing gas for the
annular fluidized bed are adjusted such that the Particle-Froude numbers in the central tube lie between 1 and 100, in the annular fluidized bed between 0.02 and 2, and in the mixing chamber between 0.3 and 30.
With the process in accordance with the invention, the advantages of a stationary fluidized bed, such as a sufficiently long solids retention time, and the advantages of a circulating fluidized bed, such as a good mass and heat transfer, can
surprisingly be combined with each other during the heat treatment, while the disadvantages of both systems are avoided.  When passing through the upper region of the central tube, the first gas or gas mixture entrains solids from the annular stationary
fluidized bed, which is referred to as annular fluidized bed, into the mixing chamber, so that due to the high speed differences between the solids and the first gas an intensively mixed suspension is formed and an optimum mass and heat transfer between
the two phases is achieved.
By correspondingly adjusting the filling level in the annular fluidized bed as well as the gas velocities of the first gas or gas mixture and the fluidizing gas, the solids load of the suspension above the orifice region of the central tube can
be varied within wide ranges, so that the pressure loss of the first gas between the orifice region of the central tube and the upper outlet of the mixing chamber can lie between 1 mbar and 100 mbar.  In the case of high solids loads of the suspension in
the mixing chamber, a large part of the solids will rain out of the suspension and fall back into the annular fluidized bed.  This recirculation is called internal solids recirculation, the stream of solids circulating in this internal circulation
normally being significantly larger than the amount of solids supplied to the reactor from outside.  The (smaller) amount of not precipitated solids is discharged from the mixing chamber together with the first gas or gas mixture.  The retention time of
the solids in the reactor can be varied within wide limits by the choice of height and cross-sectional area of the annular fluidized bed and be adapted to the desired heat treatment.  Due to the high solids load on the one hand and the good mass and heat
transfer on the other hand, excellent conditions for a virtually complete combustion of the fuel introduced into the reactor are obtained above the orifice region of the central tube.  There can, for instance, be performed a virtually complete combustion
of natural gas in the vicinity of the ignition temperature and/or with little excess of oxygen without local temperature peaks being obtained.  The amount of solids discharged from the reactor with the gas stream is completely or at least partly
recirculated to the reactor, the recirculation expediently being effected into the stationary fluidized bed.  The solids mass flow thus recirculated to the annular fluidized bed normally lies in the same order of magnitude as the solids mass flow
supplied to the reactor from outside.  Apart from the excellent utilization of energy, another advantage of the process in accordance with the invention consists in the possibility of quickly, easily and reliably adapting the energy transfer of the
process and the mass transfer to the requirements by changing the flow velocities of the first gas or gas mixture and of the fluidizing gas.
To ensure a particularly effective heat transfer in the mixing chamber and a sufficient retention time in the reactor, the gas velocities of the first gas mixture and of the fluidizing gas for the fluidized bed are preferably adjusted such that
the dimensionless Particle-Froude numbers (Fr.sub.p) are 1.15 to 20 in the central tube, 0.115 to 1.15 in the annular fluidized bed and/or 0.37 to 3.7 in the mixing chamber.  The Particle-Froude numbers are each defined by the following equation:
.rho..rho..rho.  ##EQU00001## with u=effective velocity of the gas flow in m/s .rho..sub.s=density of the solid particle in kg/m.sup.3 .rho..sub.f=effective density of the fluidizing gas in kg/m.sup.3 d.sub.p=mean diameter in m of the particles
of the reactor inventory (or the particles formed) during operation of the reactor g=gravitational constant in m/s.sup.2.
When using this equation it should be considered that d.sub.p does not indicate the mean diameter (d.sub.50) of the material used, but the mean diameter of the reactor inventory formed during the operation of the reactor, which can differ
significantly in both directions from the mean diameter of the material used (primary particles).  Even from very fine-grained material with a mean diameter of e.g. 3 to 10 .mu.m, particles (secondary particles) with a mean diameter of 20 to 30 .mu.m can
for instance be formed during the heat treatment.  On the other hand, some materials, e.g. ores, are decomposed during the heat treatment.
In accordance with a development of the inventive idea it is proposed to adjust the filling level of solids in the reactor such that the annular fluidized bed for instance at least partly extends beyond the upper orifice end of the central tube
by a few centimeters, and thus solids are constantly introduced into the first gas or gas mixture and entrained by the gas stream to the mixing chamber located above the orifice region of the central tube.  In this way, a particularly high solids load of
the suspension is achieved above the orifice region of the central tube, which allows e.g. a complete combustion under difficult conditions.
By means of the process in accordance with the invention all kinds of metal hydroxide or metal carbonate can be exposed to an effective heat treatment, in order to produce in particular metal oxides.  The process is particularly useful for
producing alumina by calcining aluminum hydroxide.  The aluminum hydroxide used has a fine grain size (about 100 .mu.m), the grain size at least of the major part of the solids containing metal hydroxide or metal carbonate generally being smaller than 5
mm.  The process can also be used for calcining dolomite or calcium carbonate.
In a preferred embodiment of the present invention, preheated gas containing oxygen is supplied to the reactor through the central tube, which represents the entire or at least a very high fraction of the entire combustion air.  This ensures a
sufficient supply of oxygen into the mixing chamber of the reactor, in which an internal combustion supplies the thermal energy necessary for the reaction in the reactor.
The generation of the amount of heat necessary for the operation of the reactor can be effected in any way known to the skilled person for this purpose.  In accordance with the invention it is provided to introduce gaseous and/or liquid fuel into
the reactor through the central tube, which fuel is burnt above the central tube in the mixing chamber of the reactor.  In particular when supplying gaseous fuel, e.g. natural gas, a premixing of the gaseous fuel with the oxygen-containing gas occurs due
to the strong turbulences in the central tube, ignition and combustion then being effected in the mixing chamber.  Such internal combustion leads to a particularly effective heat transfer between the hot particles of the stationary annular fluidized bed,
which were entrained by the gas stream, and the process gases.  To avoid a premature ignition of the fuel still in the central tube, the gaseous or liquid fuel is supplied in the vicinity of the outlet opening (upper orifice region) of the central tube.
To this end, for instance a lance arranged in the central tube can be used for supplying fuel.  The reactor temperature can easily be controlled by varying the flow of gaseous and/or liquid fuel.
Alternatively or in addition, solid, liquid or gaseous fuel, for instance coal or liquid hydrocarbons, can directly be introduced into the reactor via a corresponding feed conduit.  In this case, it is recommended to control the temperature in
the reactor for instance by varying the amount of air supplied.  In accordance with a particularly preferred variant of the present invention gaseous fuel and/or air is introduced into the lower region of the annular fluidized bed of the reactor as gas
for fluidizing the annular fluidized bed.  Instead of air, all other gases or gas mixtures known to the skilled person for this purpose can of course also be used for fluidization.  Interestingly, it was found out that as fluidizing gas there can also
exclusively be used gaseous fuel, which passes through the annular fluidized bed and meets with the preheated combustion air in the mixing chamber, where ideal conditions exist for an optimum combustion.
Upstream of the reactor, one or more preheating stages may be provided, in which the solids containing metal hydroxide or metal carbonate are suspended, dried, preheated and/or partly calcined before the heat treatment in the reactor, at least
part of their moisture content being removed.  Preferably, two preheating stages, each comprising a heat exchanger and a downstream separator, are provided upstream of the reactor, the material in the first heat exchanger being heated by exhaust gas from
the second heat exchanger, and the material in the second heat exchanger being heated by exhaust gas from the reactor.  Both heat exchangers preferably are suspension heat exchangers.  In this way, the total energy demand of the process is reduced even
As heat exchanger, an annular-fluidized-bed heat exchanger with a stationary fluidized bed and a mixing chamber can be used in accordance with the invention, which has a particularly good utilization of heat and energy.  In addition, a strong
mechanical load of the solids to be preheated is thereby avoided, which in the case of the Venturi driers conventionally used for preheating occurs in the Venturi fluidized beds of the Venturi nozzle due to strong turbulences in the conical expansion and
can lead to granular disintegration and the formation of undesired fine grain.  When annular-fluidized-bed heat exchangers are used as driers or preheaters in accordance with the invention, the supply of heat is effected by exhaust gas from the reactor,
which is supplied for instance via a central tuyere (central tube).  This principle is identical with the reactor with annular fluidized bed and mixing chamber in accordance with the invention.  The solids are laterally introduced into the annular
fluidized bed, dried and preheated, before the solids reach the central tuyere.  In the annular fluidized bed, the solids with a Particle-Froude number Fr.sub.p of about 0.8 are fluidized with air, whereby the mechanical load is substantially lower
because of the velocities reduced by a factor of about 10 to 20 as compared to the Venturi throat of the Venturi fluidized bed.  In Venturi nozzles, on the other hand, Particle-Froude numbers Fr.sub.p of 15 to 20 must be adjusted, to prevent the solids
from falling through the Venturi throat.  In the central tuyere, Particle-Froude numbers Fr.sub.p of about 5 to 10 can be adjusted in accordance with the invention, whereas the Particle-Froude number Fr.sub.p in the mixing chamber is about 3.
For cooling the annular-fluidized-bed reactor and/or annular-fluidized-bed heat exchanger in accordance with the invention, water can be sprayed directly into or onto the annular fluidized bed.  This is much easier than in reactors or driers with
a Venturi fluidized bed, in which the water must generally be atomized by means of two-fluid nozzles, in order to produce small water droplets which can evaporate inside the container.  Moreover, the conventional method requires an aid such as steam for
atomizing the water.
After the heat treatment, a fraction between 0 and 100% of the product entrained by the exhaust gas of the reactor is discharged via a separator into a preferably fluidizing-gas-operated mixing vessel, where it is mixed with partly calcined
solids, particularly metal hydroxide, in particular for adjusting the quality of the product and for cooling the hot metal oxide.  Preferably, at least part of the product is recirculated to the annular fluidized bed of the reactor via a solids return
conduit.  An essential advantage of this solids recirculation consists in the fact that the solids load of the suspension in the vicinity of the mixing chamber can specifically be adjusted to the requirements of the process, and even be changed during
the operation as required.
In accordance with a development of this inventive idea, the pressure loss between the central tube and the outlet conduit of the reactor is measured for this purpose and controlled by varying the amount of solids recirculated.  What turned out
to be particularly advantageous for this purpose is a fluidized intermediate container with downstream metering member, for instance a speed-variable rotary vane feeder or a roller-type rotary valve.  The solids recirculation in a simple way contributes
to keeping constant the process conditions in the reactor and/or extending the mean retention time of the solids in the reactor.
In accordance with the process of the invention, the product or product mixture is supplied after the heat treatment in the reactor from the mixing vessel and/or directly from the separator to a cooling system, which in particular forms an
arrangement of a plurality of cooling stages connected in series.  Such a cooling stage can be formed of direct and/or indirect heat exchangers, for instance cooling cyclones or fluidized-bed coolers.
For an improved energy utilization it is provided that the gas used for cooling in a cooling stage and heated thereby is supplied to an upstream cooling stage, the reactor and/or a preheating stage.  It is conceivable to pass the gas in a
cascade-like manner, beginning with the last cooling stage in which the product to be cooled has already been precooled by preceding cooling stages, through several or all preceding cooling stages.  Since the product is even warmer in each of the
preceding cooling stages, it is cooled further in each of the cooling stages and the gas used for cooling is heated further.  Finally, the heated gas can then be supplied to the reactor preferably through the central tube and/or to a preheating stage.  A
particularly good recovery of heat can be achieved during the cooling of the metal oxide when cross-flow heat exchangers frequently used as indirect heat exchangers in fluidized-bed coolers are replaced by direct heat flow exchangers, so that a
preferably multi-stage direct contact occurs between metal oxide to be cooled and combustion air to be preheated.
A plant in accordance with the invention, which is suited in particular for performing the above-described process, has a reactor constituting a fluidized-bed reactor for producing metal oxide from metal compounds such as metal hydroxide or metal
carbonate, in which the metal compound is heated by combustion of fuel, and metal oxide is generated.  In the reactor, a gas supply system is provided, which is formed such that gas flowing through the gas supply system entrains solids from a stationary
annular fluidized bed, which at least partly surrounds the gas supply system, into the mixing chamber.  Preferably, this gas supply system extends into the mixing chamber.  It is, however, also possible to let the gas supply system end below the surface
of the annular fluidized bed.  The gas is then introduced into the annular fluidized bed for instance via lateral openings, entraining solids from the annular fluidized bed into the mixing chamber due to its flow velocity.
In accordance with the invention, the gas supply system has a gas supply tube (central tube) extending upwards substantially vertically from the lower region of the reactor preferably into the mixing chamber of the reactor, which gas supply tube
is at least partly surrounded by a chamber in which the stationary annular fluidized bed is formed.  The central tube can constitute a nozzle at its outlet opening and have one or more apertures distributed around its shell surface, so that during the
operation of the reactor solids constantly get into the central tube through the apertures and are entrained by the first gas or gas mixture through the central tube into the mixing chamber.  Of course, two or more central tubes with different or
identical dimensions or cross-sectional shapes may also be provided in the reactor.  Preferably, however, at least one of the central tubes is arranged approximately centrally with reference to the cross-sectional area of the reactor.
In accordance with a preferred embodiment, a separator, in particular a cyclone for separating solids is provided downstream of the reactor, the separator having a solids conduit which leads to the annular fluidized bed of the reactor and/or a
solids conduit which leads to a mixing vessel.
To provide for a reliable fluidization of the solids and the formation of a stationary fluidized bed, a gas distributor is provided in the annular chamber of the reactor, which divides the chamber into an upper annular fluidized bed and a lower
gas distributor chamber, the gas distributor chamber being connected with a supply conduit for fluidizing gas and/or gaseous fuel.  Instead of the gas distributor chamber, there can also be provided a gas distributor composed of tubes and/or nozzles,
wherein part of the nozzles can be connected to a gas supply for fluidizing gas and another part of the nozzles can be connected to a separate gas supply of gaseous fuel.
In accordance with the invention, the reactor can furthermore have a supply conduit for gaseous and/or liquid fuel, which leads to the central tube, as well as a supply conduit for gaseous, liquid and/or solid fuel, which leads into the annular
chamber or the mixing chamber.  In particular, it turned out to be particularly advantageous for a controlled supply of fuel when a lance for supplying gaseous and/or liquid fuel is arranged in the gas supply system, in particular the central tube, which
lance extends up to the region of the outlet opening of the gas supply system, in particular into the upper orifice region of the central tube.
To achieve a particularly effective and gentle preheating of the educt, it is proposed in accordance with the invention to provide an annular-fluidized-bed preheating stage with a chamber for a stationary annular fluidized bed and a mixing
chamber as preheating stage.
In accordance with the invention, this is followed by a cooling system comprising direct and/or indirect cooling stages, in particular cooling cyclones and/or fluidized coolers.  In the direct cooling stages, the cooling medium directly gets in
contact with the product to be cooled.  Desired reactions, for instance product refinements, can also be performed during the cooling process.  In addition, direct cooling stages have a particularly good cooling effect.  In indirect cooling stages,
cooling is effected by means of a cooling medium flowing through a cooling coil.  To be able to utilize the gas heated during cooling also in the process itself, the cooling stage has at least one supply conduit for gas (combustion air) heated in the
cooling stage, which leads into a preheating stage, into the mixing chamber, into the gas distributor chamber and/or into the combustion chamber.
In the annular fluidized bed and/or the mixing chamber of the reactor, means for deflecting the solid and/or fluid flows may be provided in accordance with the invention.  It is, for instance, possible to position an annular weir, whose diameter
lies between that of the central tube and that of the reactor wall, in the annular fluidized bed such that the upper edge of the weir protrudes above the solids level obtained during operation, whereas the lower edge of the weir is disposed at a distance
from the gas distributor or the like.  Thus, solids raining out of the mixing chamber in the vicinity of the reactor wall must first pass the weir at the lower edge thereof, before they can be entrained by the gas flow of the central tube back into the
mixing chamber.  In this way, an exchange of solids is enforced in the annular fluidized bed, so that a more uniform retention time of the solids in the annular fluidized bed is obtained.
Developments, advantages and possibilities for applying the present invention can also be taken from the following description of embodiments and from the drawings.  All described and/or illustrated features per se or in any combination form the
subject-matter of the invention, independent of their inclusion in the claims or their back-reference.
For calcining metal hydroxide or metal carbonate, the plant shown in FIG. 1 has a for instance cylindrical reactor 25 with a central tube 26 arranged approximately coaxially with the longitudinal axis of the reactor 25, which central tube extends
substantially vertically upwards from the bottom of the reactor 25.  In the vicinity of the bottom of the reactor 25, an annular gas distributor 29 is provided, in which open supply conduits 21 and 28.  In the vertically upper region of the reactor 25,
which forms a mixing chamber 20, an outlet conduit 33 is arranged, which opens into a separator 34 constituting a cyclone.
When the solids are now charged into the reactor 25 via the solids conduit 19, a layer is formed on the gas distributor 29, which annularly surrounds the central tube 26 and is referred to as annular fluidized bed 27.  Fluidizing gas introduced
through the supply conduit 21, 28 flows through the gas distributor 29 and fluidizes the annular fluidized bed 27, so that a stationary fluidized bed is formed.  The velocity of the gases supplied to the reactor 25 is adjusted such that the
Particle-Froude number in the annular fluidized bed 27 lies between 0.15 and 0.35.  Since only a relatively small amount of fluidizing air is required, it is not absolutely necessary to preheat the air used as fluidizing gas.
By supplying more solids into the annular fluidized bed 27, the solids level in the reactor 25 is raised to such an extent that solids get into the orifice of the central tube 26.  Through the central tube 26, an oxygen-containing gas or gas
mixture is at the same time introduced into the reactor 25 as combustion air, which supplies the oxygen content necessary for the combustion of gaseous, liquid or solid fuels in the mixing chamber 20.  The velocity of the gas supplied to the reactor 25
through the central tube 26 preferably is adjusted such that the Particle-Froude number in the central tube 26 approximately lies between 7 and 11 and in the mixing chamber 20 approximately between 1.5 and 3.
Since the solids level of the annular fluidized bed 27 is raised above the upper edge of the central tube 26, solids flow over this edge into the central tube 26.  The upper edge of the central tube 26 can be straight or be shaped differently,
for instance be serrated, or have lateral openings in the shell surface.  Due to the high gas velocities, the gas flowing through the central tube 26 entrains solids from the stationary annular fluidized bed 27 into the mixing chamber 20 when passing
through the orifice of the central tube, whereby an intensively intermixed suspension is formed.  Due to the intensive mass and heat transfer between the gas stream and the solids in the mixing chamber 20, the initially colder solids are heated
particularly well due to the internal combustion in the mixing chamber 20.
As a result of the reduction of the flow velocity due to the expansion of the gas jet in the mixing chamber 20 and/or by impingement on one of the reactor walls, the entrained solids quickly lose velocity and partly fall back again into the
annular fluidized bed 27.  Between the reactor regions of the stationary annular fluidized bed 27 and the mixing chamber 20 a solids circulation is obtained.  Due to this solids circulation the solids to be treated circulate in the reactor 25 for a
particularly long time, where at the same time the very good heat transfer in the mixing chamber 20 can be utilized.  This ensures a largely complete calcination of the metal salts.
Before the solids get into the reactor 25 for heat treatment (calcination), the educt metal hydroxide or metal carbonate is introduced via a screw conveyor 1 into a Venturi preheater 3 serving as heat exchanger, which belongs to a first
preheating stage A. In the Venturi preheater 3, the fine-grained solids with a grain size which is substantially less than 5 mm gets in direct contact with hot gas, so that the solids are dried and preheated.  For this purpose, a hot gas mixture (exhaust
gas) with temperatures in the range from 200 to 500.degree.  C. is supplied to the Venturi preheater 3 of the first preheating stage A through an exhaust gas conduit 2, which gas mixture transports the fine-grained solids via a solids conduit 5 into a
filter means constituting a separator 6, for instance a bag filter or an electrostatic precipitator.  There, the exhaust gas is separated from the solids, and the exhaust gas escapes in the exhaust gas conduit 7 for instance via a chimney.
Via the solids conduit 8, the partly calcined solids reach the Venturi preheater 4 of a second preheating stage B. In this Venturi preheater 4, the already partly calcined solids get in direct contact with hot exhaust gas having temperatures of
650 to 1150.degree.  C., which is introduced into the Venturi preheater 4 via an exhaust gas conduit 16.  From this Venturi preheater 4, the partly calcined solids together with the hot exhaust gas are conveyed through the solids conduit 17 into a
separating cyclone 18 serving as separator, whose exhaust gas is introduced through the exhaust gas conduit 2 into the Venturi preheater 3 of the first heating stage A.
Via a solids conduit 19, the solids separated in the cyclone 18 get into the annular fluidized bed 27 of the fluidized-bed reactor 25, in which there exist temperatures of 650 to 1150.degree.  C., mostly about 800 to 1000.degree.  C. In addition,
gaseous fuel is supplied through the fuel conduit 21 into a gas distributor chamber 24 formed below the gas distributor 29 and is introduced into the lower region of the fluidized bed 27 through the gas distributor 29.  In the gas distributor chamber 24,
the gaseous fuel can be mixed with the fluidizing air supplied via the supply conduit 28 and be introduced into the stationary annular fluidized bed 27 for instance through nozzles or openings of the gas distributor 29.  Alternatively, nozzles connected
to the fuel conduit 21 can be provided in the gas distributor 29, through which nozzles the fuel is directly introduced into the stationary annular fluidized bed.
FIG. 2 shows a variant of the fuel supply into the stationary annular fluidized bed 27 of the reactor 25, in which gaseous fuel is introduced via the fuel conduit 21 into the gas distributor chamber 24 divided by the gas distributor 29.  In this
variant, the gaseous fuel can be used for fluidizing the stationary annular fluidized bed 27 and completely replace the fluidizing air supplied via the supply conduit 28.  Via the fuel conduit 21, there can also be supplied a mixture of gaseous fuel and
fluidizing air, so that the gaseous fuel only partly replaces the fluidizing air.  The gaseous fuel flows through the stationary annular fluidized bed 27 into the mixing chamber 20, in which occurs the combustion for generating the heat required for the
The hot exhaust gas of the reactor 25, which includes metal oxide product, flows through an outlet conduit 33 into a separator 34 constituting a recirculating cyclone, whose exhaust gas is supplied via the exhaust gas conduit 16 to the Venturi
preheater 4 of the second preheating stage B. Part of the hot solids separated there are recirculated via the solids return conduit 15a into the annular fluidized bed 27 of the reactor 25.  The other part of the hot solids first flows through the product
supply conduit 15 into a mixing vessel 14 to which fluidizing gas is supplied through a supply conduit 35.  It is provided to branch off part of the preheated, partly calcined solids through a solids conduit 13 coupled to the solids conduit 8 into the
mixing vessel 14, in which the partly calcined solids from the solids conduit 13 are heated and calcined by the hot metal oxide from the product supply conduit 15.  This mixture of product and partly calcined solids serves to adjust the quality of the
product and to cool hot metal oxide.
The cooling of the product mixture generated in the mixing vessel 14 is effected in a downstream cooling system 40 to which belong four successive cooling stages D, E, F and G. The cooling stages D, E and F are three identical cooling cyclones 42
connected in series, to each of which belongs a pneumatic delivery conduit 41 in which the metal oxide with colder air each is conveyed upwards to the corresponding cooling cyclone 42.  For this purpose, the hot metal oxide from the mixing vessel 14 is
introduced through a solids conduit 45 into the pneumatic delivery conduit 41 of the first direct cooling stage D and charged into the cooling cyclone 42 of the first cooling stage D. From the lower end of the cooling cyclone 42, the metal oxide flows
through the solids conduit 46 to the lower end of the pneumatic delivery conduit 41 of the second direct cooling stage E. The same is true for the third direct cooling stage F, from which the metal oxide is conveyed through the solids conduit 46 into the
final cooler of the cooling stage G, which constitutes the fluidized-bed cooler 47.
The gas circulation in the direct cooling stages D, E and F is as follows: A blower 50 presses ambient air into the pneumatic delivery conduit 41 of the last direct cooling stage F up to the cooling cyclone 42.  From the cooling cyclone 42 of
each cooling stage F and E, this air each flows through an air conduit 51 to the base of the pneumatic delivery conduits 41 of the preceding cooling stages E and D and is then introduced as preheated combustion air via an air supply conduit 31 through
the central tube 26 into the reactor 25.
The final cooler is designed as fluidized-bed cooler 47, through which extends a cooling coil 55 and which has vertical weirs 56, 57, at which the product to be cooled is retained and each forms a fluidized bed, the metal oxide to be cooled
flowing over the weirs 56, 57 into the respectively next fluidized bed.  Fluidizing air is introduced through an air supply conduit 59 into the respective stationary fluidized beds of the fluidized-bed cooler 47.  Waste air heated in the fluidized-bed
cooler 47 flows through a waste air conduit 60 into the pneumatic delivery conduit 41 of the cooling stage F. The cooled metal oxide leaves the final cooler 47 via the discharge conduit 63.  Through the cooling coil 55, water usually flows as cooling
The temperatures in the cooling cyclone 42 of the first cooling stage D typically lie in the range from 450 to 850.degree.  C., preferably between 500 and 720.degree.  C. In the cyclone 42 of the succeeding cooling stage E, the temperatures
usually are 200 to 600.degree.  C. and are cooled to about 70.degree.  C., until the finished product is discharged.
The plant represented in FIG. 3 and the process related therewith substantially correspond to the system described in FIG. 1.  A description of identical parts of the plant, which are also provided with the same reference numerals, will be
The essential difference with respect to the above-described plant in accordance with FIG. 1 consists in the supply of fuel to the reactor 25.  The reactor 25 is in turn designed such that in its lower region a stationary annular fluidized bed 27
is formed, above which extends a mixing chamber 20.  From the lower region of the reactor 25 a central tube 26 extends through the stationary annular fluidized bed 27 up into the region of the mixing chamber 20.  Through this central tube 26, combustion
air preheated in the cooling system 40 is preferably introduced via the air supply conduit 31 directly into the mixing chamber 20 of the reactor 25, which typically has already been heated to temperatures between 450 and 850.degree.  C. In this variant,
the fuel supply is also effected through the central tube 26, the fuel being supplied to the central tube 26 in the vicinity of the outlet opening in the upper orifice region of the central tube 26.  It is thereby achieved that the combustion starts
directly above the central tube 26 in the mixing chamber 20.
As can be taken from FIG. 4, a lance 30 for supplying liquid or gaseous fuel is therefore arranged in the central tube 26.  The fuel is entrained upwards into the mixing chamber 20 by the preheated air from the supply conduit 31 and mixes with
the same.  As a result, the combustion in the mixing chamber 20 starts directly above the central tube 26 open at the top and generates the desired calcining temperature.  Through the supply conduit 28, the air required for fluidizing the annular
fluidized bed 27 is supplied.
Furthermore, in the plant in accordance with FIG. 3 the cooling stage F with the cooling cyclone 42 is replaced by a cooling stage H with a fluidized-bed cooler 47, so that in accordance with FIG. 3 two cooling stages D, E with cooling cyclones
42 and two cooling stages G, H with fluidized-bed coolers 47 are provided.
A particular advantage of the process in accordance with the invention consists in that the advantages of a stationary annular fluidized bed 27 and a mixing chamber 20 (circulating fluidized bed) are utilized optimally, and at the same time the
waste heat generated by cooling the product is again supplied to the reactor for saving energy.  In addition, a controlled internal combustion is made possible.
In the plant in accordance with FIG. 1, about 213,000 kg/h alumina with a temperature of 65.degree.  C. and 8.0 wt-% surface moisture are supplied via the screw conveyor 1.  One part of the alumina pretreated in the first preheating stage A is
introduced into the mixing chamber 14, and seven parts are introduced into the second preheating stage B. Behind the second preheating stage B, the solids in the solids conduit 19 have a temperature of 341.degree.  C. and are preheated to such an extent
that about 70% of the hydrate water are removed.  As fuel, 9750 Nm.sup.3/h cold natural gas are introduced into the annular fluidized bed 27 of the fluidized-bed reactor 25 through the fuel conduit 21.
For this application, the Particle-Froude numbers Fr.sub.p in the stationary annular fluidized bed are about 0.17, in the mixing chamber about 2.96, and in the central tube about 9.9.
In the mixing vessel 14, the product discharged from the separator 34 is mixed with the precalcined solids from the first preheating stage A, whereby a product with a temperature of 618.degree.  C. is produced.  From the hydrate supplied via the
solids conduit 13, 9300 kg/h hydrate water are removed, so that the remaining mixture has an ignition loss of 0.9 wt-%.
In the discharge conduit 63, 129,000 kg/h alumina with a temperature of about 70.degree.  C. are obtained.  The specific heat requirement of the total process is about 2750 kJ/kg product.
TABLE-US-00001 Conduit (ref. numeral) 2 7 16 21 G (Nm.sup.3/h) 201,000 223,000 151,000 9,750 T (.degree.  C.) 341 147 960 25 Conduit (ref. numeral) 31 35 50 59 G (Nm.sup.3/h) 120,000 700 82,400 16,000 T (.degree.  C.) 496 72 73 73
In the plant in accordance with FIG. 3, about 102,000 kg/h aluminum hydroxide with a temperature of 65.degree.  C. and 7.0 wt-% surface moisture are supplied via the screw conveyor 1.  One part of the aluminum hydroxide pretreated in the first
preheating stage A is charged into the mixing chamber 14, and eight parts are charged into the second preheating stage B. Behind the second preheating stage B, the solids in the solids conduit 19 have a temperature of 343.degree.  C. and are preheated to
such an extent that about 72% of the hydrate water are removed.  As fuel, 5027 Nm.sup.3/h cold natural gas are supplied to the fluidized-bed reactor 25 through the lance 30 into the central tube 26 and the mixing chamber 20.
For this application, the Particle-Froude numbers Fr.sub.p in the stationary annular fluidized bed are about 0.34, in the mixing chamber about 1.54, and in the central tube about 7.9.
In the mixing vessel 14, the product discharged from the separator 34 is mixed with the precalcined solids from the first preheating stage A, whereby a product with a temperature of 689.degree.  C. is produced.  From the hydrate supplied via the
solids conduit 13, 3970 kg/h hydrate water are removed, so that the remaining mixture has an ignition loss of 0.74 wt-%.
In the discharge conduit 63, 68,500 kg/h alumina with a temperature of about 70.degree.  C. are obtained.  The specific heat requirement of the total process is about 2866 kJ/kg product.
TABLE-US-00002 Conduit (ref. numeral) 2 7 16 30 G (Nm.sup.3/h) 102,200 111,600 76,900 5,027 T (.degree.  C.) 343 156 1,000 25 Conduit (ref. numeral) 28 31 35 41 (E) G (Nm.sup.3/h) 16,800 44,200 500 38,900 T (.degree.  C.) 274 573 70 392 Conduit
(ref. numeral) 59 (H) 59 (G) G (Nm.sup.3/h) 16,800 16,800 T (.degree.  C.) 70 70
In accordance with FIG. 5, it is provided to replace the two Venturi preheaters 3, 4 of the first and second preheating stages A, B by annular-fluidized-bed heating stages 70,71 with a chamber for a stationary annular fluidized bed 72 and a
mixing chamber 73, in order to achieve a particularly effective and gentle preheating.  In the first step of preheating, the moist solids are dried at the surface and heated to a temperature of about 150.degree.  C. In the second preheating stage B, the
solids then are precalcined, where about 70% of the hydrate water are removed and at the same time a further heating to about 350.degree.  C. occurs.  In a first step, for instance 196 t/h moist aluminum hydrate with a temperature of 65.degree.  C. can
be charged into the annular fluidized bed 72 of the annular-fluidized-bed heating stage 70 of the first preheating stage A and be fluidized with 5000 Nm.sup.3/h air.  The fluidizing air is introduced into the annular fluidized bed 72 via a feed conduit
74 and a gas distributor 75.  Via a central tube 76, 197,000 Nm.sup.3/h flue gas with a temperature of about 340.degree.  C. are supplied.  In the mixing chamber 73, the solids are dried, preheated to about 150.degree.  C., and 180 t/h of the solids are
introduced as dry hydrate via the electrostatic precipitator 6 and a subsequent airlift into the annular fluidized bed 72 of the annular-fluidized-bed heating stage 71, where the hydrate is fluidized with 5000 Nm.sup.3/h air, which are supplied via a
feed conduit 74.  Via the central tube 76 of the annular-fluidized-bed heating stage 71, 150,000 Nm.sup.3/h flue gas with a temperature of about 1000.degree.  C. are introduced, whereby the dry hydrate is precalcined and is heated to about 350.degree.
C. From this second step, about 144 t/h precalcined material are discharged with the waste air.
TABLE-US-00003 List of Reference Numerals: 1 screw conveyor 2 exhaust gas conduit 3 Venturi preheater 4 Venturi preheater 5 solids conduit 6 separator, filter means 7 exhaust gas conduit 8 solids conduit 13 solids conduit 14 mixing vessel 15
product supply conduit 15a solids return conduit 16 exhaust gas conduit 17 solids conduit 18 separator, cyclone 19 solids conduit 20 mixing chamber 21 fuel conduit 24 gas distributor chamber 25 reactor 26 central tube 27 stationary annular fluidized bed
28 supply conduit 29 gas distributor 30 lance 31 air supply conduit 33 outlet conduit 34 separator 35 supply conduit 40 cooling system 41 delivery conduit 42 cooling cyclones 45 solids conduit 46 solids conduit 47 fluidized-bed cooler 50 blower 51 air
conduit 55 cooling coil 56 weir 57 weir 59 air supply conduit 60 waste air conduit 63 discharge conduit 70 annular-fluidized-bed heating stage 71 annular-fluidized-bed heating stage 72 stationary annular fluidized bed 73 mixing chamber 74 feed conduit 75
gas distributor 76 central tube A first preheating stage B second preheating stage D cooling stage E cooling stage F cooling stage G cooling stage H cooling stage
Process and plant for producing metal oxide from metal compounds, Hirsch, et al., Martin Hirsch, Werner Stockhausen, Michael Stroder, Application number 10 540-071, Chemistry Of Inorganic Compounds, Chemical Apparatus And Process Disinfecting Deodorizing Preserving Or Sterilizing, Heating, Specialized Metallurgical Processes Compositions For Use Therein Consolidated Metal Powder Compositions And Loose Metal Particulate Mixtures, metal oxide, Patent Application, fluidized bed, gas mixture, prese
This application is thenational phase application under 35 U.S.C. .sctn.371 of International Application No. PCT/EP2003/014213 filed on Dec. 13, 2003, entitled, "Process and Plant for Producing Metal Oxide from Metal Compounds" which claims the benefit of German PatentApplication No. 102 60 739.7 filed on Dec. 23, 2002.TECHNICAL FIELDThe present invention relates to a process for producing metal oxide from metal compounds, in particular metal hydroxide or metal carbonate, in which the metal compound is conveyed into a fluidized bed reactor, heated there to a temperature of650 to 1150.degree. C. by combustion of fuel, and metal oxide is generated, as well as to a corresponding plant.From EP 0 861 208 B1 there is known a process for producing anhydrous alumina from aluminum hydroxide in a circulating fluidized bed, in which the alumina is first dried in several preheating stages, partly calcined, and in the preheatedcondition introduced into a fluidized-bed reactor in which the temperatures lie in the range from 800 to 1000.degree. C. due to the combustion of fuel, and alumina is generated. The exhaust gas of the fluidized-bed reactor, which is obtained during thecombustion, is supplied to the preheating stages and utilized energetically. The metal oxide withdrawn from the reactor is subjected to multi-stage cooling in direct contact with air and at least passed through a direct cooling stage, in which the metaloxide is pneumatically transported upwards into a separating cyclone via a delivery conduit. Furthermore, the partly cooled metal oxide is passed through at least one fluidized cooler with indirect cooling.In the plants known so far, reactors with a stationary or a circulating fluidized bed are used for calcining or heating the solids. However, the energy utilization of the calcining step, which is achieved when using a stationary fluidized bed,needs improvement. On the one hand, this is due to the fact that the mass and heat transfer is rather modera