Matched Legal Cases: ['art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200', 'art 270', 'art 270', 'art 270', 'art 200', 'art 200', 'art 200', 'art 200', 'art 200']

Patent US8034410 - Protective inserts to line holes in parts for semiconductor process equipment - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsInserts are used to line openings in parts that form a semiconductor processing reactor. In some embodiments, the reactor parts delimit a reaction chamber. The reactor parts may be formed of graphite. A layer of silicon carbide is deposited on surfaces of the openings in the reactor parts and the inserts...http://www.google.com/patents/US8034410?utm_source=gb-gplus-sharePatent US8034410 - Protective inserts to line holes in parts for semiconductor process equipmentAdvanced Patent SearchTry the new Google Patents, with machine-classified Google Scholar results, and Japanese and South Korean patents.Publication numberUS8034410 B2Publication typeGrantApplication numberUS 11/779,033Publication dateOct 11, 2011Filing dateJul 17, 2007Priority dateJul 17, 2007Fee statusPaidAlso published asUS20090023302Publication number11779033, 779033, US 8034410 B2, US 8034410B2, US-B2-8034410, US8034410 B2, US8034410B2InventorsVladimir Kuznetsov, Ernst H. A. GrannemanOriginal AssigneeAsm International N.V.Export CitationBiBTeX, EndNote, RefManPatent Citations (69), Non-Patent Citations (4), Classifications (8), Legal Events (2) External Links: USPTO, USPTO Assignment, EspacenetProtective inserts to line holes in parts for semiconductor process equipment
US 8034410 B2Abstract
Inserts are used to line openings in parts that form a semiconductor processing reactor. In some embodiments, the reactor parts delimit a reaction chamber. The reactor parts may be formed of graphite. A layer of silicon carbide is deposited on surfaces of the openings in the reactor parts and the inserts are placed in the openings. The inserts are provided with a hole, which can accept another reactor part such as a thermocouple. The insert protects the walls of the opening from abrasion caused by insertion of the other reactor part into the opening.
1. A method for fabricating a semiconductor processing reactor part, comprising:
providing a partially-fabricated reactor part having an opening on a first surface of the partially-fabricated reactor part, the opening extending completely through the reactor part to a second opposing surface, wherein a first width of the opening on the first surface is larger than a second width of the opening on the second surface;
coating a surface of the opening with a protective coating; and
subsequently placing a hollow insert into the opening, the insert contacting sidewalls of the opening and having a closed end sealing off a side of the opening open to the first surface from a side of the opening open to the second surface.
2. The method of claim 1, wherein the partially-fabricated reactor part is formed of graphite.
3. The method of claim 2, wherein the protective coating is formed of silicon carbide.
4. The method of claim 3, wherein the insert is formed of silicon carbide.
5. The method of claim 3, further comprising depositing an additional silicon carbide coating on exposed surfaces of the insert and the reactor part after placing the insert into the opening.
6. The method of claim 1, further comprising placing a thermocouple into a hollow cavity in the insert.
7. The method of claim 1, wherein subsequently placing the insert into the opening comprises:
freezing the insert; and
subsequently inserting the insert into the opening.
8. The method of claim 7, wherein subsequently placing the insert into the opening further comprises heating the partially-fabricated reactor part before subsequently inserting the insert into the opening.
9. The method of claim 7, wherein subsequently placing the insert into the opening forms a gas-tight seal between the surfaces of the opening and the insert.
10. The method of claim 1, further comprising attaching a fastener to the partially-fabricated reactor part to secure the insert in the opening.
11. The method of claim 1, wherein depositing the protective coating comprises performing a chemical vapor deposition.
12. A method for making a part for a semiconductor processing reactor, comprising:
providing a first semiconductor reactor part, a first surface of the first reactor part having a hole extending completely through the reactor part to a second opposing surface, wherein a first width of the hole on the first surface is larger than a second width of the opening on the second surface;
depositing a protective coating on surfaces of the first reactor part and the hole;
subsequently placing a hollow insert into the hole, the insert contacting sidewalls of the hole and having a closed end sealing off a side of the hole open to the first surface from a side of the hole open to the second surface;
depositing another protective coating after placing the insert into the hole, wherein the other protective coating coats walls of an opening in the insert; and
inserting a second semiconductor reactor part into the opening in the insert.
13. The method of claim 12, wherein the first semiconductor reactor part is configured to form a wall of a reaction chamber of the reactor.
14. The method of claim 12, wherein the insert is formed of silicon carbide.
15. The method of claim 12, wherein walls of the insert are formed having a thickness in a range of about 0.05 and about 2 mm.
16. The method of claim 12, wherein the first semiconductor reactor part is provided with a planar surface at least as wide as a major surface of a substrate accommodated in the reaction chamber.
17. The method of claim 16, wherein the first semiconductor reactor part forms a first reactor block configured to interface with a second reactor block positioned opposite the first reactor block such that the first reactor block extends across the major surface of a substrate and the second reactor block extends across an opposite major surface of the substrate upon assembly of the semiconductor reactor and retention of the substrate.
18. The method of claim 17, wherein the second reactor block is provided with a plurality of gas passages on a planar surface facing the major surface of the substrate, the gas passages configured to supply gas to the major surface of the substrate.
19. The method of claim 12, wherein the second reactor part is a thermocouple. Description
This invention relates to semiconductor processing equipment and, more particularly, to inserts for protecting openings in semiconductor processing equipment parts.
In accordance with some embodiments of the invention, a method for fabricating a semiconductor processing reactor part is provided. The method comprises providing a partially-fabricated reactor part having an opening on a surface of the partially-fabricated reactor part. A protective coating is deposited on a surface of the opening. An insert is subsequently placed into the opening. The insert has a cavity extending along at least part of a length of the insert.
In accordance with other embodiments of the invention, a method for making a part for a semiconductor processing reactor is provided. The method comprises providing a first semiconductor reactor part. The reactor part has a hole. An insert is placed into the hole. A second semiconductor reactor part is inserted into an opening in the insert.
In accordance with other embodiments of the invention, a semiconductor processing reactor part for defining a reaction chamber for processing a semiconductor substrate. The reactor part comprises a surface configured to delimit at least part of the reaction chamber. A protective insert is disposed within the reactor part. The protective insert does not extend beyond the surface of the reactor part. A wall of the protective insert defines a cavity extending along at least part of a length of the protective insert. The wall has a thickness of about 0.05 mm or more.
FIG. 2 is a schematic, cross-sectional side view, in isolation, of an opening in a part of a semiconductor processing reactor, in accordance with embodiments of the invention.
FIG. 3 is a schematic, cross-sectional side view of the structure of FIG. 2 after depositing a protective layer of material, in accordance with embodiments of the invention.
FIG. 4 is a schematic, cross-sectional side view of the structure of FIG. 3 after installing an insert into the opening, in accordance with embodiments of the invention.
FIG. 5 is a schematic, cross-sectional side view of the structure of FIG. 4 after installing an other reactor part in the insert, in accordance with embodiments of the invention.
FIG. 6 is a schematic, cross-sectional side view of the structure of FIG. 4 after installing a mechanical clamp, in accordance with embodiments of the invention.
FIG. 7 is a schematic, cross-sectional side view of the structure of FIG. 4 after depositing a second protective layer of material, in accordance with embodiments of the invention.
Many different parts are typically fit together to form a semiconductor processing reactor. A first reactor part may have openings, such as holes or grooves, for accommodating a second reactor part. One or both of the reactor parts may be coated with a protective material to protect that part from exposure to reactive chemical species during semiconductor processing. The protective coating is more resistant to the harsh process environment of a process chamber than the material of the parts themselves. However, it has been found that the act of inserting and removing the second reactor part into and from an opening can cause undesired mechanical damage, including abrasion and removal of the protective coating. As a result, the reactor part may be left prone to damage caused by exposure to process gases during semiconductor processing.
In addition to possible removal of a protective coating due to abrasion, it has been found that the protective coating near the bottom of an opening may be relatively thin or may have incomplete coverage due to limited diffusion of coating precursors into the opening. Consequently, the bottoms of openings may not be completely coated in the first instance or may be more easily damaged relative to upper parts of the opening due to the thin protective coating overlying them.
It will be appreciated that the reactor parts may be formed of materials that can be damaged by exposure to process gases. For example, the parts may be formed of graphite. These graphite parts may be damaged by exposure to oxygen. The oxygen reacts with the graphite in a combustion reaction that causes the graphite to “burn.”
For example, susceptors for supporting substrates or reactor blocks for defining the interior surfaces of a process chamber may be formed of graphite and may include openings for accepting thermocouple assemblies. As a thermocouple assembly is inserted into a hole, however, the assembly may rub off part of the protective coating around and in the hole, or the bottom of the hole may have gaps in the protective coating due to limited deposition of the coating at the bottom of the hole. Moreover, abrasion and removal of the protective coating is exacerbated during servicing of the assemblies, since the assemblies may be repeatedly removed and reinserted into the openings during the life of the reactor. As a result, process gases may contact and undesirably react with the graphite under the coating, causing the reactor part to burn.
Embodiments of the invention protect openings in a reactor parts from exposure to process gases. The insert is placed in an opening in a first reactor part. The insert has its own opening to accommodate a second reactor part, such as a thermocouple assembly. The insert provides a more durable and/or thicker protective layer than a deposited coating, thereby protecting the opening from abrasion caused by placing and removing the second reactor part into and from the opening. The insert also can help to seal or constrict the flow of the process gases into the bottom of the opening, thereby limiting the exposure of the bottom of the opening to process gases, thereby protecting the bottom of the opening even where a protective coating at the bottom of the opening incompletely covers the bottom.
In some embodiments, before being placed in the opening, a protective coating may be deposited over the surfaces of the opening and the first reactor part. The protective coating may be used to protect surfaces of the first reactor part generally. The insert may then be placed in the opening of the first reactor part. A second reactor part, such as a thermocouple assembly, may be placed into—a cavity in the insert.
In some embodiments, a second coating may be deposited over the surfaces of the insert and the first reactor part before placing the second reactor part into the insert. The second coating may be used to seal the insert in the opening in the first reactor part and also has advantages for gas-tightness and reinforcing the structural integrity of the first reactor part/insert construction. In other embodiments, the insert may be secured within the opening using an fastener, e.g., a plate fitted over the insert and the opening.
The upper block 13 and the lower block 14 are preferably moved apart before introducing the substrate 21 into the reactor 1, as shown in FIG. 1. After the substrate 21 has been introduced into the reactor 1, the blocks 13 and 14 are moved towards one another by the lifting rods 27 and 28 in such a way that the distance between the substrate 21 and the adjacent surfaces 146 and 148 of the furnace bodies 130 and 140, respectively, is reduced. Preferably, when positioned at a heat treatment position, the substrate 21 is less than about 2 mm and more preferably less than about 1 mm from the surfaces 146 and 148. In the illustrated embodiment, as shown in FIG. 2, the substrate is held in a stable position by gas streams issuing from the openings 24 and 25, without requiring further mechanical support. It will be appreciated, however, that in other arrangements, support structures such as support pins may be used to support and space the substrate from the bodies 130 and 140. Moreover, while illustrated as being symmetrically spaced from the bodies 130 and 140, the substrate 21 may be spaced closer to one or the other of the bodies 130 or 140 in other arrangements.
With reference to FIG. 2, a portion of a reactor part 200 is shown. The reactor part 200 may form various structures of a reaction chamber. For example, the part 200 may be a susceptor or a furnace body, such as one of the furnace bodies 130, 140 (FIG. 1). The reactor part 200 may be formed of various materials compatible with semiconductor fabrication, including, without limitation, graphite.
An opening 210 is disposed in the reactor part 200. The opening 210 is sized to accommodate an insert 260 (FIG. 4), which will later be placed into the opening 210. The opening 210 may extend partly or completely through the reactor part 200. Having the opening 210 extend through the reactor part 200 has advantages for allowing for a more uniform deposition of protective coating on surfaces 250 of the opening 210, in embodiments where such a protective coating is applied. In the illustrated embodiment, the opening 210 extends through the reactor part 200, but narrows at one end to a smaller opening 220. The narrowing may be used to prevent the later inserted insert 260 from falling out of the opening 210 on the side of the smaller opening 220.
With reference to FIG. 3, a protective coating 230 is applied on exposed surfaces of the reactor part 200. In the illustrated embodiment, the protective coating 230 coats top surfaces 240, bottom surfaces 242 and interior hole surfaces 250, 252 of the reactor part 200. In some embodiments, it will be appreciated that the narrow hole 220 aids deposition into lower parts of the opening 210 by allowing gas to flow through the opening 210, thereby improving the diffusion of process gases into the opening 210. The protective coating 230 may be formed of any material suitable for protecting the reactor part 200 during semiconductor fabrication and which is suitable for deposition on the surfaces of the reactor part. In some embodiments, the protective coating 230 is formed of silicon carbide, which is deposited by chemical vapor deposition. It will be appreciated that the protective coating 230 is deposited to a desired thickness for protecting the top and/or bottom surfaces 230, 240 of the reactor part 200, although this thickness may be reduced if additional protective layers, such as that forming the layer 232 (FIG. 7), are subsequently deposited on those surfaces.
With reference to FIG. 4, a protective insert 260 is placed into the opening 210. The protective insert 260 is provided with its own opening or cavity 262. The insert opening 262 is sized and shaped to accommodate another reactor part, such a thermocouple assembly 270 (FIG. 5), which will later be installed. As illustrated, the protective insert 260 extends up to a top of the protective coating 230 or less. The walls of the protective insert 260 are preferably sufficiently thick and durable to provide a barrier to shield the surfaces 250 of the opening 210 from abrasion caused by insertion and removal of parts into the opening 262. In addition, the walls of the protective insert 260 preferably also confer sufficient structural rigidity to the protective insert 260 to allow the protective insert 260 to exist in free-standing form. In some embodiments, the walls of the protective insert 260 is more than about 0.05 mm thick and, preferably, is about 0.05-2.0 mm thick.
The protective insert 260 may be formed of various materials suitable for protecting the reactor part 200 from, e.g., undesired exposure to process gases. For example, the protective insert 260 may be formed of the same material as the protective coating 230. The protective insert is formed of silicon carbide in some embodiments.
Various methods known in the art may be used to fabricate the protective insert 260. For example, the protective insert 260 can be formed over a form that has an outer shape that corresponds to the desired shape for the opening 262 in the protective insert 260. The form may then be removed to leave the protective insert 260. In one embodiment, silicon carbide is deposited around a graphite rod or bar, e.g., by chemical vapor deposition. The rod or bar is then removed, e.g., by being burned out in an oxygen ambient to leave a free-standing protective insert 260.
It will be appreciated that the protective insert 260 is preferably prevented from dislodging out of the opening 210. In some embodiments, the sizes of the opening 210 and the protective insert 260 may be selected so that the protective insert 260 fits tightly within the opening 210. This tight fit helps to retain the protective insert 260 in the opening 210.
In some embodiments, the fit of the protective insert 260 in the opening 210 may be made tighter by utilizing the expansion and contraction of materials at different temperatures. For example, the protective insert 260 can be provided at a lower temperature than the reactor part 200, so that when the temperatures of the protective insert 260 and the reactor part 200 equilibrate or reach the ambient temperature, the protective insert 260 expands and/or the reactor part 200 contracts to increase the tightness of the fit of the protective insert 260 in the opening 210. In some embodiments, the protective insert 260 is cooled, e.g., by exposure to liquid nitrogen, to cause the protective insert 260 to contract relative to the reactor part 200. Alternatively, or in addition, the reactor part 200 is heated to cause the reactor part 200 to expand relative to the protective insert 260. The protective insert 260, which is at a lower temperature than the reactor part 200, is then inserted into the opening 210 of the reactor part 200, which is at a higher temperature than protective insert. It will be appreciated that the protective insert 260 may also be at a lower temperature than the ambient environment and the reactor part 200 may be at a higher temperature than the ambient environment.
It will also be appreciated that the materials forming the protective insert 260 and the hot reactor part 200 may be selected to have similar thermal expansion coefficients, to prevent loosening of a tight fit due to differential expansion of the materials. It will appreciated that, where the thermal expansion coefficient of the reactor part 200 is larger than the thermal expansion coefficient of the protective insert 260, the reactor part 200 may expand more than the protective insert 260 as the process chamber is heated. As a result, the hole 210 may become larger than the protective insert 260, thereby undesirably loosening the tight fit of the protective insert 260 within the hole 210.
In some embodiments, the reactor part 200 is formed of graphite and the protective insert 260 is formed of silicon carbide. Advantageously, silicon carbide coatings have proven to adhere very well on graphite and the two materials match well together. For metal reactor parts such as stainless steel, Inconel�, Hastelloy� and high temperature steels, a TiN or BN insert would be suitable matches.
With reference to FIG. 5, an other reactor part 270 can be positioned or inserted into the opening 262 of the protective insert 260. The other reactor part 270 may be any reactor part designed to be accommodated within a recess. For example, the other reactor part 270 may be a thermocouple assembly, e.g., the temperature sensors 147, 148 (FIG. 1), for measuring the temperature of within a process chamber.
With reference to FIG. 6, instead of or in addition to securing the protective insert 260 into the opening 210 by a tight fit, a fastener 280 may be attached to the reactor part 200 to hold the protective insert 260 in place. For example, the fastener 280 may be a plate that is installed over at least part of the protective insert 260 to prevent the protective insert 260 from dislodging from the opening 210. The fastener 280 may be formed of a material that is resistant to damage by process gases. In some embodiments, the fastener 280 is formed of silicon carbide.
With reference to FIG. 7, an additional coating 232 may be applied over the exposed surfaces of the protective insert 260 and the reactor part 200. It will be appreciated that the additional coating 232 may be utilized to seal the interface between the protective insert 260 and the reactor part 200, to improve the gas tightness and mechanical integrity of the assembly of the protective insert 260 and the reactor part 200. The additional coating 232 may also help secure the protective insert 260 in the opening 210. In addition, the additional coating may be used to augment the protective coating 230, to provide further material for protecting the reactor part 200. The additional protective coating 232 may be formed of any material suitable for locking the protective insert 260 in place and/or for providing further protection against abrasion. In some embodiments, the additional coating 232 is formed of the same material as the protective coating 230, e.g., the additional coating may be formed of silicon carbide, which can be deposited by, e.g., chemical vapor deposition.
Advantageously, embodiments of the invention can prevent damage to the protective coatings that line surfaces of openings, such as holes or grooves, in reactor parts. Protective inserts provided in the openings form a barrier that prevents mechanical contact between parts inserted into the openings and the walls of the openings. As a result, damage to the walls of the openings caused by abrasion is prevented.
In addition, the protective inserts provide protection for the walls of the openings where there is incomplete coverage of the walls by a protective coating. The protective inserts seal the lower parts of the opening, thereby preventing gas diffusion into those lower parts. Even where the seal between the protective inserts and the walls of the opening are not gas tight, openings between the protective insert and the walls of the opening provide a relatively narrow and long path which limits diffusion of gases to the bottom of the opening, relative to the amount of diffusion allowed by a more loose-fitting part, such as a thermocouple assembly, provided in the hole.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3011006Nov 10, 1958Nov 28, 1961Carborundum CoProcess and apparatus for measuring high temperaturesUS4377347Jun 16, 1980Mar 22, 1983Nippon Kokan Kabushiki KaishaMethod for measuring temperature of molten metal received in vesselUS4592307Feb 28, 1985Jun 3, 1986Rca CorporationVapor phase deposition apparatusUS4692556Mar 24, 1986Sep 8, 1987Electro-Nite CompanyRepeating temperature sensing immersion probeUS4976996Feb 17, 1987Dec 11, 1990Lam Research CorporationChemical vapor deposition reactor and method of use thereofUS4978567Mar 31, 1988Dec 18, 1990Materials Technology Corporation, Subsidiary Of The Carbon/Graphite Group, Inc.Wafer holding fixture for chemical reaction processes in rapid thermal processing equipment and method for making sameUS4984904Apr 11, 1989Jan 15, 1991Kawaso Electric Industrial Co., Ltd.Apparatus for continuously measuring temperature of molten metal and method for making sameUS5006220Feb 14, 1990Apr 9, 1991Tokyo Ohka Kogyo Co., Ltd.Electrode for use in the treatment of an object in a plasmaUS5027746Mar 21, 1989Jul 2, 1991U.S. Philips CorporationEpitaxial reactor having a wall which is protected from depositsUS5065698Mar 25, 1991Nov 19, 1991Canon Kabushiki KaishaFilm forming apparatus capable of preventing adhesion of film depositsUS5098198Sep 3, 1991Mar 24, 1992Applied Materials, Inc.Wafer heating and monitor module and method of operationUS5104514May 16, 1991Apr 14, 1992The United States Of America As Represented By The Secretary Of The NavyProtective coating system for aluminumUS5246500Sep 1, 1992Sep 21, 1993Kabushiki Kaisha ToshibaVapor phase epitaxial growth apparatusUS5271967Aug 21, 1992Dec 21, 1993General Motors CorporationMethod and apparatus for application of thermal spray coatings to engine blocksUS5315092Oct 11, 1991May 24, 1994Dainippon Screen Mfg. Co., Ltd.Apparatus for heat-treating wafer by light-irradiation and device for measuring temperature of substrate used in such apparatusUS5336327Nov 19, 1993Aug 9, 1994Motorola, Inc.CVD reactor with uniform layer depositing abilityUS5360269Nov 12, 1993Nov 1, 1994Tokyo Kogyo Kabushiki KaishaImmersion-type temperature measuring apparatus using thermocoupleUS5421893Nov 29, 1993Jun 6, 1995Applied Materials, Inc.Susceptor drive and wafer displacement mechanismUS5456757 *Oct 29, 1993Oct 10, 1995Applied Materials, Inc.Susceptor for vapor depositionUS5456761Jul 15, 1993Oct 10, 1995Alcan International LimitedHigh temperature and abrasion resistant temperature measuring deviceUS5474618Apr 19, 1994Dec 12, 1995Rdc Controle LteeProtective ceramic device for immersion pyrometerUS5493987May 16, 1994Feb 27, 1996Ag Associates, Inc.Chemical vapor deposition reactor and methodUS5514439Oct 14, 1994May 7, 1996Sibley; ThomasWafer support fixtures for rapid thermal processingUS5562774Jul 25, 1995Oct 8, 1996Heraeus Quarzglas GmbhCoated quartz glass componentUS5571333May 26, 1995Nov 5, 1996Shin-Etsu Handotai Co. Ltd.Heat treatment furnace with an exhaust baffleUS5618594 *Apr 13, 1995Apr 8, 1997Cvd, IncorporatedComposite thermocouple protection tubesUS5685906 *Mar 23, 1995Nov 11, 1997Seh America, Inc.Method and apparatus for configuring an epitaxial reactor for reduced set-up time and improved layer qualityUS5688331 *Jul 1, 1996Nov 18, 1997Applied Materisls, Inc.Resistance heated stem mounted aluminum susceptor assemblyUS5788799Jun 11, 1996Aug 4, 1998Applied Materials, Inc.Apparatus and method for cleaning of semiconductor process chamber surfacesUS5817406 *Jan 24, 1996Oct 6, 1998Applied Materials, Inc.Ceramic susceptor with embedded metal electrode and brazing material connectionUS5902407Aug 10, 1995May 11, 1999Deboer; Wiebe B.Rotatable substrate supporting mechanism with temperature sensing device for use in chemical vapor deposition equipmentUS5904778Jul 26, 1996May 18, 1999Applied Materials, Inc.Silicon carbide composite article particularly useful for plasma reactorsUS5910221Jun 18, 1997Jun 8, 1999Applied Materials, Inc.Bonded silicon carbide parts in a plasma reactorUS5998767 *Mar 20, 1998Dec 7, 1999Siemens AktiengesellschaftApparatus for processing a substrate wafer and method for operating sameUS6024799Jul 11, 1997Feb 15, 2000Applied Materials, Inc.Chemical vapor deposition manifoldUS6056823Mar 31, 1998May 2, 2000Applied Materials, Inc.Temperature controlled gas feedthroughUS6066209Mar 31, 1998May 23, 2000Applied Materials, Inc.Cold trapUS6086680 *Mar 26, 1996Jul 11, 2000Asm America, Inc.Low-mass susceptorUS6120640Dec 19, 1996Sep 19, 2000Applied Materials, Inc.Boron carbide parts and coatings in a plasma reactorUS6129808Sep 25, 1998Oct 10, 2000Lam Research CorporationLow contamination high density plasma etch chambers and methods for making the sameUS6162543Dec 11, 1998Dec 19, 2000Saint-Gobain Industrial Ceramics, Inc.High purity siliconized silicon carbide having high thermal shock resistanceUS6170429Sep 30, 1998Jan 9, 2001Lam Research CorporationChamber liner for semiconductor process chambersUS6174481 *Sep 10, 1998Jan 16, 2001Lear Automotive Dearborn, Inc.Method for forming cast tooling for polymer moldingUS6205869 *Aug 12, 1999Mar 27, 2001Sentry Equipment CorporationApparatus and method for sampling fluid from reactor vesselUS6227140Sep 23, 1999May 8, 2001Lam Research CorporationSemiconductor processing equipment having radiant heated ceramic linerUS6325858Nov 2, 1998Dec 4, 2001Asm America, Inc.Long life high temperature process chamberUS6342691Nov 12, 1999Jan 29, 2002Mattson Technology, Inc.Apparatus and method for thermal processing of semiconductor substratesUS6408786Sep 23, 1999Jun 25, 2002Lam Research CorporationSemiconductor processing equipment having tiled ceramic linerUS6454860Oct 27, 1998Sep 24, 2002Applied Materials, Inc.Deposition reactor having vaporizing, mixing and cleaning capabilitiesUS6506254Jun 30, 2000Jan 14, 2003Lam Research CorporationSemiconductor processing equipment having improved particle performanceUS6524428May 7, 2001Feb 25, 2003Hitachi, Ltd.Method of holding substrate and substrate holding systemUS6592707Oct 22, 2001Jul 15, 2003Applied Materials Inc.Corrosion-resistant protective coating for an apparatus and method for processing a substrateUS6635115May 19, 2000Oct 21, 2003Applied Materials Inc.Tandem process chamberUS6692576 *Sep 13, 2002Feb 17, 2004Asm America, Inc.Wafer support systemUS6890861Jun 30, 2000May 10, 2005Lam Research CorporationSemiconductor processing equipment having improved particle performanceUS6942753Apr 16, 2003Sep 13, 2005Applied Materials, Inc.Gas distribution plate assembly for large area plasma enhanced chemical vapor depositionUS20030029563Aug 10, 2001Feb 13, 2003Applied Materials, Inc.Corrosion resistant coating for semiconductor processing chamberUS20030035905Aug 16, 2001Feb 20, 2003Richter Precision, Inc.Carbon nitride coating for optical media discsUS20030198749Apr 17, 2002Oct 23, 2003Applied Materials, Inc.Coated silicon carbide cermet used in a plasma reactorUS20040060658Sep 30, 2002Apr 1, 2004Tokyo Electron LimitedMethod and apparatus for an improved baffle plate in a plasma processing systemUS20040208228 *Oct 6, 2003Oct 21, 2004Sumitomo Electric Industries, Ltd.Temperature gauge and ceramic susceptor in which it is utilizedEP0229488A1Dec 4, 1986Jul 22, 1987Anicon, Inc.Etch resistant wafer boat and processEP0723141A1Dec 28, 1995Jul 24, 1996Applied Materials, Inc.Sensors for measuring temperature and methods of measuring workpiece temperaturesJP2003197546A * Title not availableJPH0564627A Title not availableWO1995031582A1May 15, 1995Nov 23, 1995Ag Associates, Inc.Chemical vapor deposition reactor and methodWO1997006288A1Aug 1, 1996Feb 20, 1997Advanced Semiconductor Materials America, Inc.Process chamber with inner supportWO1999023276A1Nov 2, 1998May 14, 1999Asm America, Inc.Long life high temperature process chamberWO2001011223A1Aug 3, 2000Feb 15, 2001Robert Bosch GmbhFuel injection valve* Cited by examinerNon-Patent CitationsReference1Linke, J. and Vietzke, E., "Behavior of Boron Doped Graphites, Plasma Sprayed Boron Carbides and a-C/B:H as Plasma Facing Material," J. Fusion Tech., vol. 20, pp. 228-231 (Sep. 1991).2Pending U.S. Appl. No. 11/856,418, filed Sep. 17, 2007, entitled "Semiconductor Processing Parts Having Apertures With Deposited Coatings and Methods for Forming the Same" in the name of Kuznetsov.3Ponnekanti et al., "Failure mechanisms of anodized aluminum parts used in chemical vapor deposition chambers," J. Vac. Sci. Technol., A14(3) (May 1, 1996).4Shackelford, J. "Introduction to Materials Science for Engineers," 3d ed., Macmillan Publishing Co., pp. 398 (1992).Classifications U.S. Classification427/249.15, 427/402, 427/249.16, 427/419.1, 427/237International ClassificationC23C16/00Cooperative ClassificationC23C16/4404European ClassificationC23C16/44A4Legal EventsDateCodeEventDescriptionSep 6, 2007ASAssignmentOwner name: ASM INTERNATIONAL N.V., NETHERLANDSFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KUZNETSOV, VLADIMIR;GRANNEMAN, ERNST H.A.;REEL/FRAME:019792/0655Effective date: 20070820Mar 25, 2015FPAYFee paymentYear of fee payment: 4RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services