Source: http://www.google.com/patents/US20030159608?dq=5998925
Timestamp: 2014-03-14 03:23:23
Document Index: 754897030

Matched Legal Cases: ['art 1', 'art 3', 'art 3', 'arts 1', 'art 3', 'art 1', 'art 3', 'art 3', 'art 3', 'art 11', 'art 3', 'art 3', 'art 1', 'art 1', 'art 3', 'arts 1', 'art 2', 'art 2', 'art 1', 'art 11', 'art 11', 'art 3', 'arts 1', 'art 3', 'arts 1', 'arts 1', 'art 3', 'art 3', 'art 1', 'art 3', 'art 1']

Patent US20030159608 - Device and method in connection with the production of structures - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inAdvanced Patent SearchPatentsDevice in connection with the lithography of structures of nanometre size, which device comprises a first main part (1) with a first principally plane surface (2 a) and a second main pan (3) with a second principally plane surface (9 a). said first surface and second surface being opposite to one another...http://www.google.com/patents/US20030159608?utm_source=gb-gplus-sharePatent US20030159608 - Device and method in connection with the production of structuresAdvanced Patent SearchPublication numberUS20030159608 A1Publication typeApplicationApplication numberUS 10/149,072Publication dateAug 28, 2003Filing dateDec 4, 2000Priority dateDec 10, 1999Also published asCN1260615C, CN1409832A, DE60029827D1, DE60029827T2, EP1244939A1, EP1244939B1, US7195734, WO2001042858A1Publication number10149072, 149072, US 2003/0159608 A1, US 2003/159608 A1, US 20030159608 A1, US 20030159608A1, US 2003159608 A1, US 2003159608A1, US-A1-20030159608, US-A1-2003159608, US2003/0159608A1, US2003/159608A1, US20030159608 A1, US20030159608A1, US2003159608 A1, US2003159608A1InventorsBabak HeidariOriginal AssigneeBabak HeidariExport CitationBiBTeX, EndNote, RefManReferenced by (65), Classifications (13), Legal Events (2) External Links: USPTO, USPTO Assignment, EspacenetDevice and method in connection with the production of structuresUS 20030159608 A1Abstract Device in connection with the lithography of structures of nanometre size, which device comprises a first main part (1) with a first principally plane surface (2 a) and a second main pan (3) with a second principally plane surface (9 a). said first surface and second surface being opposite to one another and being arranged in principle parallel in relation to one another, with an adjustable interval between them, and said first and second surface being arranged to form a support for a substrate (5) and a template (10) respectively, or vice-versa According to the invention, said second main part (3) also comprises a cavity (6) for a medium. and means for adjusting a pressure of said medium, a wall of said cavity consisting of a flexible membrane (9), of which one side. which side faces away from the cavity (6), forms said second surface (9 a). The invention also relates to a method that utilizes the device. Images(9) Claims(17)
TECHNICAL FIELD [0001] The invention relates to a device in connection with the lithography of structures of nanometre size, which device comprises a first main part with a first principally plane surface and a second main part with a second principally plane surface, said first surface and second surface being opposite to one another and arranged substantially parallel in relation to one another, with an adjustable interval between them, and said first and second surface being arranged to provide support for a substrate or template respectively, or vice versa. The invention also relates to a method in connection with the lithography of structures of nanometre size. The invention is applicable in connection with nanoimprint lithography on semiconductor materials, such as silicon, indium phosphide or gallium arsenide, for the manufacture of semiconductor components, but also in connection with nanoimprint lithography on other rigid materials, such as ceramic materials, metals or polymers with a relatively high glass transition temperature, for use in e.g. biosensors. PRIOR ART [0002] The trend in microelectronics is towards ever smaller dimensions. In principle, development has been such that the dimensions are being halved every third year. Commercial components are now manufactured with structures of roughly 200 nm in size, but there is a need to go even further down in dimensions, to <100 mn. Research concerning components based on quantum effects is now highly topical and a demand is being created for a commercially applicable manufacturing technique for components with dimensions <10 nm. These nanocomponents can be produced currently using serial technology in individual specimens, for research purposes, but for mass production a parallel production method is required. A parallel production method of this kind that has recently been developed is nanoimprint lithography (NW), U.S. Pat. No. 5,772,905, which has set out the basic preconditions for the mass production of structures close to atomic scale, see Stephen Y. Chou, Peter R. Krauss, Wei Zhang, Lingjie Guo and Lei Zhuang: �Sub-10 nm imprint lithography and application�, J Vac. Sci. Technol. B, Vol. 15, No. 6, (1997). Several research reports have been presented on the subject, but hitherto the method has been restricted to nanoimprinting on components with a small total area, typically only a few square centimetres, see Stephen Y. Chou, Peter R. Krauss and Preston J. Renstorm: �Nanoimprint lithography�, J. Vac. Sci. TechnoL B. 14, 4129 (1996); K. Pfeiffer, G. Bleidiessel, G. Gruetzner, H. Schulz, T. Hoffinann, H.-C. Scheer, C. M. Sotomayor Torres and J. Ahopelto: �Suitability of new polymer materials with adjustable glass temperature for nanoimprinting�, Proceeding of Micro- and Nano-Engineering Conference, (1998); and Leuven. Bo Cui, Wei Wu, Linshu Kong, Xiaoyun Sun and Stephen Y Chou: �Perpendicular quantized magnetic disks with 45 Gbits on a 4�4 cm2 area �, J. AppL Phys. 85, 5534 (1999). [0003] However, no commercial equipment for NIL has yet been presented, which is due in large part to the fact that an entirely new approach is required for the manufacture of nanometre-sized structures. The production of such small dimensions puts considerably higher demands than before on all constituent process stages, new process materials, new designs and new technical solutions having to be developed. The need for mass production of nanometre-size structures is great, however, and opens up entirely new possibilities for the design of more compact circuits and sensors for various applications with considerably greater sensitivity than those of today. [0004] The basic principle of NIL is mechanical deformation of a thin film layer, which is coated onto a plane plate of silicon. The NIL process can be compared with the production process for CDs and can be described in three stages: [0005] 1. Production of template: A template can be produced from various materials, e.g. metal, semiconductor, ceramic or of certain plastics. To create a three-dimensional structure on one surface of the template, various lithographic methods can be used, depending on the requirements for the size of the structure and its resolution. E-beam and X-ray lithography are normally used for structure dimensions that are less than 300 nm. Direct laser exposure and UV lithography are used for larger structures. [0006] 2. Imprint: A thin layer of a polymer, e.g. polyamide, is applied to a plane substrate of silicon. The layer is heated and at a certain temperature, the so-called imprint temperature, the predefined template and substrate are pressed together, the inverse of the template's structure being transferred in the polymer layer to the substrate. [0007] 3. Structure transfer: In the areas pressed together in the polymer layer, a thin layer of polymer remains. The last stage is removal of this thin remaining layer on the substrate. This is carried out in a so-called �RIE� or oxygen plasma unit. The thinner this remaining layer is, the finer the structures that can be created using the nanoimprint process. [0008] In the imprint stage (2) it is essential that the template and the substrate are arranged absolutely parallel in relation to one another. In known devices, however, there are a number of sources of error that cause problems with a lack of parallelism. In some of the known devices, e.g. in the �Flip Chip� bonder, the parallelism between the surfaces is therefore measured, following which mechanical adjustment is undertaken using special devices, e.g. piezoelectric components, to ensure that the surfaces remain parallel in relation to one another. See Alberto Jaramillo-Nunez, Carlos Robledo-Sanchez, and Alejandro Cornejo-Rodriguez: �Measuring the parallelism of transparent and nontransparent plates �, Optical Engineering�December 1996-V 35, Issue 12, pp. 3437-3441. This type of measurement and adjustment is complicated, however, and is in itself marred by sources of error, which obstruct parallelism between the template and substrate. Furthermore, there are structural variations in the material in the surface of a plane plate, or in other words, on a nanometre scale, there exists an unevenness in the surface of each plate (template and substrate), even if the plates are polished. These unevennesses lead to an undesirable uneven distribution of force over the surfaces when the template and substrate are pressed together, which in turn results in an unevenly depressed structure on the substrate. This is particularly critical for the imprint process if the plates are large, e.g. the size of the surfaces is more than 50 mm in diameter. [0009] There are thus two main problems to solve for the commercial production of nanometre-sized structures using the imprint technique. One problem is parallelization of the plane surfaces that are to be pressed together and the other problem is providing an even distribution of force over the entire plane surface. Solving these problems is a prerequisite for a commercial process for nanoimprint lithography of materials for semiconductor components on surfaces with total areas that are greater than approx. 7-20 cm2. BRIEF ACCOUNT OF THE INVENTION [0010] The object of the present invention is to provide a device and method in connection with the lithography of structures of nanometre size, by means of which device and method the above problems with regard to parallelism between the substrate and template, and an even distribution of force on compression, are solved. In particular, the device and method have been developed for nanoimprinting structures on materials for semiconductor components, which materials have total areas, normally circular areas, which are greater than 7-20 cm2, but can also be applied for nanoimprinting structures on other materials that have a certain rigidity, i.e. that are not flexible. Naturally, the invention can also be applied for nanoimprinting structures on materials that have smaller total surfaces. [0011] According to the invention, a device is thus presented according to the preamble, characterized in that the second main part also comprises a cavity for a medium, and means for adjusting a pressure of said medium, a wall of the cavity consisting of a flexible membrane, of which one side, which side faces away from the cavity, forms the second surface. [0012] The template is thus supported according to the invention by a flexible membrane, which membrane is pressurized on its opposite side, at the same time as the substrate, or vice versa, is supported by a fixed and stable surface. With this, the substrate and template will be arranged absolutely parallel in relation to one another and at the same time the distribution of force on pressing together the substrate and template will be absolutely even over the surfaces of the substrate/template. The invention thus builds, simply but brilliantly, on a utilization of physical principles, which eliminate the need for time consuming, costly and unreliable measuring and adjustment of the parallelism between substrate and template. [0013] According to one aspect of the invention, the membrane consists of a flexible material, preferably a polymer material or a thin metal, even more preferredly plastic, rubber or thin metal, the membrane having a thickness of up to 10 mm, preferably up to 3 mm and even more preferredly up to 1 mm. There is actually no lower limit to the thickness of the membrane, other than a practical one, in which case the ultimate should be a membrane with a thickness that corresponds to a single atom layer, which at least in the present situation is virtually impossible. The membrane is best fixed in the case of the second main part around the periphery of the membrane, at the edges of the cavity, and otherwise deflectably. [0014] According to another aspect of the invention, said medium consists of a gas or a liquid with low compressibility, preferably an oil or even more preferredly hydraulic oil. A simple oil such as e.g. brake fluid can also be used. The cavity is intended to be filled hydraulically with said medium, the device also comprising means for adjusting the pressure in the cavity to 1-500 bar (excess pressure), preferably 1-200 bar, and even more preferredly 1-100 bar during the actual imprint stage. During heating of the substrate, prior to the imprint stage, the pressure can be adjusted here to 1-5 bar, and following heating, during the actual imprint stage, the pressure can be adjusted to 5-500 bar, preferably 5-200 bar and even more preferredly 5-100 bar. Naturally, the pressure can also be set to zero. [0015] According to yet another aspect of the invention, the device also comprises means for heating, e.g. electrical or mechanical means, or means for irradiating, and means for cooling the substrate, e.g. by means of a cooling medium. Heating and cooling can be adjusted to achieve substrate temperatures typically of between 30 and 300� C. [0016] With the device and the method according to the invention, well-defined structures of nanometre size can be created on rigid materials with total areas that are greater than 7-20 cm2, e.g. materials with a maximum width or diameter of up to 150, preferably 250 mm, even more preferredly 350 mm or even larger, in a quick, easy and cheap manner. A cycle for nanoimprinting according to the invention typically takes less than four minutes, or less than 3 minutes, often around 2 minutes. The nanometre-sized structures can here be down to below 100 nm in individual structures, or below 50 nm, or even below 10 nm. [0017] The invention is applicable to nanoimprint lithography on semiconductor materials, such as silicon, for the manufacture of semiconductor components. It has also been found surprisingly that nanoimprint lithography can be carried out by means of the invention on other semiconductor materials such as e.g. indium phosphide (InP) or gallium arsenide (GaAs). These materials differ from silicon in that they are considerably more brittle and thus considerably more sensitive to uneven force distribution on nanoimprinting. No other method or device has been presented previously that manages to carry out nanoimprinting on brittle semiconductor materials such as indium phosphide and gallium arsenide. However, the present invention can also be applied in connection with nanoimprint lithography on other rigid materials, such as ceramic materials, metals or polymers with a relatively high glass transition temperature, for use in e.g. biosensors.
DESCRIPTION OF DRAWINGS [0018] The invention will be described in greater detail below with reference to the figures, of which: [0019]FIG. 1 shows a first embodiment of a device according to the invention, seen from the side in cross-section, [0020]FIG. 2a shows a second embodiment of a device according to the invention, seen from the side in cross-section, and how the first main part of the device can be displaced, [0021]FIG. 2b shows the embodiment according to FIG. 2a in perspective, [0022]FIGS. 3a & 3 b show the device according to FIG. 1 or 2, on pressing together the substrate and template, [0023]FIG. 4 shows a device according to the invention, seen from the side in cross-section, including devices for heating and cooling the substrate, [0024]FIG. 5 shows a front view of a device according to FIG. 4 for heating the substrate, [0025]FIG. 6 shows a front view of a device according to FIG. 4 for cooling the substrate, [0026]FIG. 7 shows an alternative method of heating the substrate, [0027]FIG. 8a shows a side view in cross-section of a device for vacuum holding of the substrate or template, [0028]FIG. 8b shows a front view of the device in FIG. 8a, [0029]FIG. 9a shows a front view of a second main part according to the invention, comprising a device according to FIG. 8, [0030]FIG. 9b shows the device according to FIG. 9a, seen from the side in cross-section, [0031]FIG. 10a shows a front view of an alternative embodiment of a second main part according to the invention, comprising a device according to FIG. 8, [0032]FIG. 10b shows the device according to FIG. 10a, seen from the side in cross-section, [0033]FIG. 11a shows a front view of an alternative device for vacuum holding of the substrate and template, [0034]FIG. 11b shows a side view in cross-section ofthe device according to FIG. 11a, [0035]FIG. 11c shows the device according to FIG. 11b, in side view in cross-section with substrate and template thereon, [0036]FIG. 12a shows a side view in cross-section of yet another alternative device for vacuum holding of substrate and template, [0037]FIG. 12b shows the device according to FIG. 12a, in side view in cross-section with substrate and template thereon, [0038]FIG. 13 shows a diagram of substrate temperature and pressure, as a function of time, for a production cycle, [0039]FIG. 14a shows a scanning electron microscope picture of a template, [0040]FIGS. 14b-d shows scanning electron microscope pictures of various nanometre-size structures achieved by means of the device and method according to the invention. [0041] Detail number 1 in FIG. I represents a first main part in a preferred embodiment of a device according to the invention. This first main part 1 comprises a first principally plane base plate 2, which is preferably arranged to be displaced in a direction that coincides with the normal for its surface 2 a facing a second main part 3. A principally plane support plate 4, on which support plate the substrate 5 is intended to be placed, can be affixed to this surface 2 a. Alternatively, the substrate 5 can be placed directly onto the surface 2 a. The substrate consists for example, according to the known technique for nanoimprint lithography, of a silicon plate with a thin layer of e.g. a polyamide, preferably polymethyl methacrylate (PMMA) on its surface 5 a facing towards the second main part 3. The substrate 5 is preferably circular. The main parts 1 and 3 preferably also have a rotationally symmetrical appearance. [0042] The second main part 3 has a cavity 6, which is formed by a bottom 7 and, in the example shown, circular-cylindrical side walls 8. As a roof for the cavity 6, a plane, flexible membrane 9 is arranged opposite the bottom 7. This membrane 9 consists in the example shown of a rubber membrane, one side 9 a of which forms a support for the template 10, and has a diameter or maximum width of 25-400 mm, preferably 50-350 mm. The membrane has a thickness of up to 10 mm, preferably up to 3 mm and even more preferredly up to 1 mm. The template 10 consists, according to the known technique for nanoimprint lithography, of a plate of e.g. metal, which is provided with a fine structural pattern, with dimensions in nanometre size, on its surface 10 a facing towards the first main part 1. [0043] The membrane 9 is fixed on the second main part 3, around the periphery of the membrane 9 at edges of the cavity 6, by means of a fixing device. A ring 11, which is circular in the example shown, is used as the fixing device, which ring is arranged to press firmly the peripheral edges of the membrane 9 between itself and the free edges of the side walls 8. Along its inner circular edge, on the side thereof that faces towards the membrane, the ring 11 is preferably bevelled 11 a, to provide a soft deflection for the membrane 9 on the transition from the ring 11. The risk is hereby reduced of splits or fold notches in the membrane 9, its life being extended. [0044] The cavity 6 is intended to accommodate a medium, preferably hydraulic oil, which can be pressurized via an inlet channel 12, which can be arranged in the side walls 8 or in the bottom 7 of the cavity (as shown in FIG. 9b). Pressurization takes place by means of a pump (not shown), which is best adapted to provide a pressure with very small variations. This can be achieved e.g. by means of a proportional valve. [0045] Contained in the second main part 3 is also a second principally plane base plate 13, which forms a support for the part with the cavity 6. [0046]FIG. 2a shows a second embodiment of the device according to the invention, a principally plane support plate 14 being arranged between the membrane 9 and the template 10. The support plate 14 has a thickness of 0.1-30 mm, preferably 0.1-20 mm, even more preferredly 0.1-10 mm, and most preferredly 0.1-5 mm, and can be executed in materials such as a metal, a semiconductor material, or a ceramic material, e.g. stainless steel, silicon carbide or aluminium oxide. The above-mentioned support plate 4 also best has these dimensions and is best executed in materials of the same type. [0047] The support plate 14 on the second main part 3 consists most advantageously of a material that is a good thermal insulator, i.e. which has low thermal conductivity. [0048] The support plate 14 forms a fixing device for the template 10, which is explained in greater detail in connection with FIG. 9. In this embodiment, the ring 11 preferably has a spacer part 11 b and a lip 11 c that prevents the support plate 14 from falling off the main part 3 before both main parts are brought together, at least when the main part 3 is arranged above the main part 1. [0049]FIG. 2a also shows, by means of arrows, how the main part 1 is arranged to be displaced in relation to the main part 3 in a radial direction, i.e. in a direction that is parallel to the surfaces 2 a and 9 a of the main parts 1 and 3. The base plate 2 can here have a fixed part 2 b facing away from the surface 2 a and a movable part 2. Displacement is executed in connection with the exchange of template and/or substrate. FIG. 2b shows the embodiment according to FIG. 2a in perspective. [0050]FIGS. 3a and b show the device according to FIG. 1 or 2 when the pressure in the cavity 6 has been increased so that the template 10 and substrate 5 are pressed together, thanks to the flexibility of the membrane 9, for transfer of the nanometre-sized structure on the surface of the template 10 a to the surface 5 a of the substrate. [0051]FIG. 4 shows that the main part 1, for the substrate 5, can also comprise means 15 for heating the substrate, and means 16 for cooling the substrate. In the preferred example shown, these means 15, 16 for heating and cooling respectively consist of support plates that are arranged between the substrate 5 and the base plate 2, preferably in the order substrate 5, support plate 4 (with vacuum for holding the substrate), support plate 16 for cooling, support plate 15 for heating, and base plate 2. The support plate 15 for heating the substrate best consists of a material which has a good thermal insulation capacity, e.g. a ceramic material such as a ceramic insulator or a ceramic composite, e.g. macor. The support plate 16 for cooling the substrate best consists of a material that has good thermal conductivity, e.g. silicon carbide, stainless steel, aluminium or aluminium oxide in some form. The support plates 15 and 16 preferably have a thickness in the same range as the support plate 14 according to the above. [0052]FIG. 5 shows how the support plate 15 can contain an electric heating coil 17, which is inlaid in a groove in the surface of the support plate 15. The heating coil/groove 17 is formed in the embodiment shown as a double coil, but can of course have other shapes also. By analogy, the support plate 16, according to FIG. 6, can contain a channel 18 inside the same for a cooling medium, e.g. a gas such as air, nitrogen or something else, or a cooling liquid such as water or something else. The channel 18 in the embodiment shown is formed as a double coil, but can of course also have other forms. [0053]FIG. 7 shows an alternative embodiment, in which heating of the substrate 5 is carried out by means of irradiation R′ of the substrate via the base plate 2 and a support plate 4 or 16. The radiation R′ used can for example be of the IR radiation type (the support plate 16 best being executed in silicon carbide) or radiation using radio frequencies, i.e. frequencies of 10 MHz and above, the device comprising means (not shown) for generating such radiation. [0054]FIGS. 8a and b show how the support plate 4 can be provided with devices for vacuum holding of the substrate 5. The support plate here has a groove 19 in both surfaces of the support plate 4, a circular groove in the example shown. The two grooves 19 are joined to one another at one point 20 at least by a hole that is continuous through the plate 4. A vacuum is created in the groove 19 and hole 20 by a connection (not shown) to a vacuum fan, via the base plate 2. By means of this vacuum device the substrate 5 is sucked firmly onto the support plate 4 and the support plate 4 in turn is sucked firmly onto the support plate 16 for cooling, or directly onto the base plate 2. It is to be perceived that also, or alternatively, the support plate 15 for heating and/or the support plate 16 for cooling can be provided with devices for vacuum holding onto the support plate 4 and the base plate 2. [0055]FIGS. 9a and 9 b show that the support plate 14 arranged in this case between the template 10 and the membrane 9 can also consist of a support plate with a vacuum device 19, 20. Provided for the groove 19 and the hole 20, preferably directly connected to the hole 20, in this case is a channel 21 for connection to a vacuum fan (not shown). In this case also, a bevelled part 11 a can be provided on the ring 11, which part 11 a can lie between the membrane 9 and the vacuum support plate 14. FIG. 9a shows the support plate 14 without a template thereon, while FIG. 9b shows a support plate 14 with a template thereon. It is also shown how the inlet channel 12 can be arranged in the bottom of the main part 3, via the base plate 13. [0056] The manufacturing cycle for nanoimprinting of a substrate 5 shall be described below starting out from the figures. In the starting phase, both main parts 1 and 3 are displaced relative to one another in an axial and radial direction, according to FIG. 2. The substrate 5 is placed on the support plate 4 and the template 10 placed on the membrane 9 or support plate 14. The substrate and template are best held in place by means of a vacuum, but other methods are also conceivable. The first main part I is displaced in a radial direction into position in relation to the second main part 3, in order then to be displaced in an axial direction towards the same. In that connection displacement is best executed in an axial direction so that a small interval continues to remain of e.g. up to 10 mm, preferably up to 5 mm and even more preferredly up to 1 mm, between the ring 11 and the support plate 4 or base plate 2 if the support plate 4 is lacking This is shown in FIG. 3a. Alternatively, the axial displacement takes place so that the ring 11 or its lip 11 c abuts the support plate 4 or base plate 2. This is shown in FIG. 3b, the dimensions of the constituent components being adapted so that there continues to remain a small interval, corresponding to the above mentioned interval, between the substrate 5 and the template 10 when the two main parts 1 and 3 come together. Following the axial displacement of the main parts, the pressure of the medium in the cavity is increased via the inlet channel 12 to around 1-5 bar so that the membrane 9 flexes out, a light pressing together of the substrate 5 and template 10 taking place. The substrate 5 is heated by means of a device for heating the same, e.g. according to FIG. 5 or 7, and then the pressure of the medium in the cavity 6 is increased to 5-500 bar, preferably 5-200 bar, and even more preferredly 5-100 bar, via the inlet channel 12, the substrate 5 and the template 10 being pressed together with a corresponding pressure, which pressure is transferred via the flexible membrane 9. Thanks to the flexible membrane, an absolutely even distribution of force is obtained over the whole of the contact surface between the substrate and the template, these being made to arrange themselves absolutely parallel in relation to one another and the influence of irregularities in the surface of the substrate or template being eliminated. Following a compression time depending on the choice of material, temperature, pressure etc., but which is typically less than 3 minutes, preferably less than 1 minute, cooling of the substrate commences by means of a device e.g. of the type shown in FIG. 6. When cooling has been completed, the pressure in the cavity 6 is reduced and the two main parts 1 and 3 are separated from one another, following which the substrate 5 and template 10 are separated from one another. After this, the substrate is subjected to further treatment according to what is known for nanoimprint lithography. This further treatment is not a part of the present invention, and will not therefore be described in greater detail. [0057]FIG. 10a shows a support plate 14 without a template thereon, while FIG. 10b shows a support plate 14 with a template thereon. FIG. 10a and 10 b here show an alternative embodiment of the invention, in which the second main part 3 is formed as a periscopic part for the axial displacement of the same. Here the cavity 6 with its medium and related (not shown) pump is used also for the periscopic displacement Arranged here outside the side walls 8 are outer walls 22 with only a small gap 23 between them. Arranged at the end of the side walls 8 and the outer walls 22 respectively are sliding seals 24 a and 24 b respectively. It is best if devices (not shown) are also provided to prevent the part with the side walls 8 being displaced so far that it comes loose from the outer walls 22. The outer walls 22 are limited at the other ends by the cavity's bottom 7 or base plate 13. The inlet channel 12 is arranged in the outer walls 22, or in the bottom 7, 13, i.e. in the area outside the gap 23. Arranged in the area of the gap 23 is a second inlet channel 25, by means of which the quantity of medium in the gap 23, and its pressure, can be influenced. The periscopic displacement of the main part 3, or rather of the membrane 9 and template 10 is achieved by increasing the pressure in the cavity 6 via the inlet channel 12, at the same time as the medium in the gap 23 is permitted to flow out via the second inlet channel 25. When the ring 11, or its lip 11 c, abuts the first main part 1 (not shown in FIG. 10), a continued increase in the pressure in the cavity will result in the membrane 9 translating the pressure to the template, so that this is pressed together with the substrate, as described above. [0058] To retract the periscopic main part 3, following the completion of imprinting, the pressure in the cavity 6 is released and the pressure in the gap 23 increased instead via the second inlet channel 25. The side walls 8 are thereby displaced, and with them the membrane 9 and the template 10, towards the base plate 13, the sliding seals 24 a and 24 b sliding against the outer walls 22 and the side walls 8 respectively. [0059]FIGS. 11a, b and c show an alternative device for vacuum holding of the substrate and template, which device consists of a support plate of the same type as before, in connection with FIG. 1, named support plate 4, named 4′ in this figure. The support plate 4′ is provided, in the same manner as shown in FIG. 8, with a groove 19 in both of its plane surfaces and a through hole 20, which runs below to a vacuum connection (not shown) to achieve a vacuum which holds the substrate 5 firmly on one surface of the support plate 4′ and holds the support plate 4′ firmly on a base, e.g. a support plate for cooling the substrate 5, not shown in this figure. Arranged on one side only of the support plate 4′, outside the groove 19, is a second vacuum groove 26, in the example shown a circular groove 26 with a diameter that is greater than the diameter of the template 10 and the substrate 5. Provided for the groove 26, at best via a hole 27, is a channel 28 for connection to a vacuum fan, not shown. The substrate 5 can be held firmly by means of the support plate 4′ by the first vacuum groove 19, the template 10 being able to be placed directly onto the substrate 5, and following this, as shown in FIG. 11c, a film or foil 29 e.g. of aluminium or rubber can be placed completely covering or running around the periphery of the template and substrate, which film or foil is sucked fast against the vacuum groove 26 and thereby holds the template 10 firmly against the substrate 5. Thanks to the device shown in FIG. 11, the substrate 5 and template 10 can thus be placed together, as shown in FIG. 11c, on one main part 1, 3, of the device, following which the main parts are displaced in relation to one another, so that they are oriented over one another and close to one another, as described earlier. Following the imprint stage, the vacuum in the groove 19 can be released, while the vacuum in the groove 26 is maintained, the support plate 4′ being able to be removed from the device with the template and substrate still there for a simple exchange of substrate. [0060]FIGS. 12a and b show yet another alternative device for vacuum holding of the substrate and template, which device consists of a support plate of the same type as before, in connection with FIG. 1, named support plate 4, in this figure named 4′. The support plate 4′ is provided, in the same manner as shown in FIG. 8, with a groove 19 in both of its plane surfaces and a through hole 20, which runs below to a vacuum connection (not shown) to achieve a vacuum which holds the substrate 5 firmly on one surface of the support plate 4′ and holds the support plate 4′ firmly on a base, e.g. a support plate for cooling the substrate 5, not shown in this figure. Arranged in the support plate 4′ is a raised edge 30 outside the groove 19 on one side of the support plate, and a groove 31 in the angle between the edge 30 and the support plate 4′, which groove 31 is connected to a vacuum channel 32. FIG. 12a shows the support plate 4′ without a template and substrate thereon, while FIG. 12b shows a support plate 4″ with a template 10 and substrate 5 thereon, inside the edge 30. The dimensions are adapted so that there is only a small gap between the edge 30 and the substrate/template, through which gap air is sucked into the vacuum channel 32. Both the template and substrate are hereby held firmly, the same function as in FIG. 11 being able to be achieved. The edge 30 has a height that exceeds the thickness of the substrate 5 (or the template 10 if this is to be placed closest to the support plate 4″). EXAMPLES [0061] Imprint trials according to the invention were conducted according to the following parameters: the substrate was 5.1 cm in diameter in Si/SiO2, with a coating of 950 K PMMA which was oven-baked at 180� C. for 24 hours. The maximum pressure was 60 bar, max. temperature 170� C. and min. temperature 80� C. The template was 5.1 cm in diameter in Si/SiO2, with template structures in the form of lines and dots with line widths of 50, 75, 100 and 150 nm, and diameters of 50 nm with a distance of 25 nm between the dots. The template was provided with a protective layer of nickel with a thickness of 20 nm, which was deposited by vaporization. The template was cleaned before imprinting by immersing it in acetone under the influence of ultrasound, and dried using nitrogen gas. [0062]FIG. 13 shows a diagram of substrate temperatures and pressures as a function of time for the production cycle, which extended over a little more than 2 minutes in a device according to the invention. As shown in the diagram, the time for the temperature increase was roughly 1 minute. Pressure was then loaded, via the membrane, and when the desired maximum pressure was reached, cooling of the substrate commenced. During cooling, the pressure was adjusted to the desired set point. [0063] The trials showed that a pressure of around 60 bar gave an impression 200 nm deep in the PMA layer on the substrate. If greater depth is desired, a higher pressure can be used. [0064] Following 10 cycles with the same template, it could be confirmed that the entire surface of all substrates was evenly imprinted. No significant variations in the structure could be observed in or between the areas with different structure. [0065] Around 50 nm PMMA remained in the impressions, which was removed by etching. Following etching, the profile on the surface of the substrate had near enough vertical walls. Following etching, the substrate was coated in the impressions with Cr, by vaporization, and then a stage was executed to remove the remaining PMMA, resulting in a successful metal coating in the impressions. [0066]FIG. 14a shows a scanning electron microscope picture of a part of a template with lines/ recesses 100 nm wide and a gap distance of 300 nm between the lines. The total surface of the template was 25 cm2. FIG. 14b shows a part of a substrate in which a layer of PMMA has been imprinted with the template in FIG. 14a, in a device according to the invention. The structure arising is very regular and devoid of defects. [0067]FIG. 14c shows an aluminium-metallized surface of a substrate of silicon that has been imprinted in a device according to the invention, with lines of 100 nm, with 200 nm and 500 nm gap distances between the lines. In the picture shown, the imprinted surface has been metallized with aluminium and then PMMA has been removed. The total surface of the substrate was 25 cm2. [0068]FIG. 14d shows aluminium dots of a size of 50 nm produced on a silicon substrate, by imprinting in PMMA in a device according to the invention. The dots have been made with varying gap distances on a total surface of 25 cm2. In the picture shown, the imprinted surface has been metallized with aluminium and the PMMA then removed. The minimum gap distance is judged to be less than 25 nm. [0069] The invention is not restricted to the embodiments and examples described above, but can be varied within the scope of the following claims. Thus it is easily perceived for example for the template and substrate to change places with one another in the figures shown. It is also perceived that conventional measures in connection with nanoimprinting should be carried out, such as cleaning of the surfaces of the substrate and template, and the space between them, using pure particle-free gas, e.g. nitrogen gas or another gas. Furthermore, it is perceived that the attachment of the membrane, formation of the cavity etc. can be executed in essentially different ways, without deviating from the idea according to the invention due to this. Referenced byCiting PatentFiling datePublication dateApplicantTitleUS7354698Jan 7, 2005Apr 8, 2008Asml Netherlands B.V.Imprint lithographyUS7377764Jun 13, 2005May 27, 2008Asml Netherlands B.V.Imprint lithographyUS7377765 *Feb 14, 2006May 27, 2008Hitachi Global Storage TechnologiesSystem, method, and apparatus for non-contact and diffuse curing exposure for making photopolymer nanoimprinting stamperUS7418902May 31, 2005Sep 2, 2008Asml Netherlands B.V.Imprint lithography including alignmentUS7442029May 16, 2005Oct 28, 2008Asml Netherlands B.V.Imprint lithographyUS7490547Dec 30, 2004Feb 17, 2009Asml Netherlands B.V.Imprint lithographyUS7500431Jan 12, 2006Mar 10, 2009Tsai-Wei WuSystem, method, and apparatus for membrane, pad, and stamper architecture for uniform base layer and nanoimprinting pressureUS7517211Dec 21, 2005Apr 14, 2009Asml Netherlands B.V.Imprint lithographyUS7523701Mar 7, 2005Apr 28, 2009Asml Netherlands B.V.Imprint lithography method and apparatusUS7611348Apr 19, 2005Nov 3, 2009Asml Netherlands B.V.Imprint lithographyUS7617769Oct 27, 2008Nov 17, 2009Hitachi Global Storage Technologies Netherlands B.V.System, method, and apparatus for membrane, pad, and stamper architecture for uniform base layer and nanoimprinting pressureUS7618250May 25, 2006Nov 17, 2009Asml Netherlands B.V.Imprint lithographyUS7636475Dec 16, 2005Dec 22, 2009Asml Netherlands B.V.Imprint lithographyUS7641468Sep 1, 2004Jan 5, 2010Hewlett-Packard Development Company, L.P.Imprint lithography apparatus and method employing an effective pressureUS7645133 *Feb 24, 2005Jan 12, 2010Korea Institute Of Machinery & MaterialsUV nanoimprint lithography process and apparatusUS7670127 *Dec 19, 2005Mar 2, 2010Obducat AbApparatus for pattern replication with intermediate stampUS7670128Dec 28, 2005Mar 2, 2010Dms Co., Ltd.Apparatus for forming fine pattern on substrateUS7676088Dec 23, 2004Mar 9, 2010Asml Netherlands B.V.Imprint lithographyUS7686970Dec 30, 2004Mar 30, 2010Asml Netherlands B.V.Imprint lithographyUS7692771May 27, 2005Apr 6, 2010Asml Netherlands B.V.Imprint lithographyUS7698999Mar 1, 2005Apr 20, 2010Asml Netherlands B.V.Printing apparatus and device manufacturing methodUS7708542 *Dec 29, 2003May 4, 2010Board Of Regents, The University Of Texas SystemDevice for holding a template for use in imprint lithographyUS7708924Jul 21, 2005May 4, 2010Asml Netherlands B.V.Imprint lithographyUS7713052 *Feb 21, 2006May 11, 2010Sumitomo Electric Industries, Ltd.Processing method of fine structure and processing equipment for fine structureUS7722350 *Apr 8, 2008May 25, 2010Erich ThallnerApparatus for imprinting and/or embossing substratesUS7730834Mar 4, 2004Jun 8, 2010Asml Netherlands B.V.Printing apparatus and device manufacturing methodUS7762186Apr 19, 2005Jul 27, 2010Asml Netherlands B.V.Imprint lithographyUS7789647 *Jun 8, 2005Sep 7, 2010Canon Kabushiki KaishaProcessing apparatus and methodUS7854877Aug 14, 2007Dec 21, 2010Asml Netherlands B.V.Lithography meandering orderUS7878791Mar 1, 2006Feb 1, 2011Asml Netherlands B.V.Imprint lithographyUS7906059Mar 16, 2009Mar 15, 2011Asml Netherlands B.V.Imprint lithographyUS7922474Feb 17, 2005Apr 12, 2011Asml Netherlands B.V.Imprint lithographyUS7927089 *Jun 7, 2006Apr 19, 2011Canon Kabushiki KaishaMold, apparatus including mold, pattern transfer apparatus, and pattern forming methodUS7931844Sep 23, 2008Apr 26, 2011Asml Netherlands B.V.Imprint lithographyUS7964054Jun 15, 2007Jun 21, 2011Sony Deutschland GmbhMethod of applying a material on a substrateUS7972553Nov 25, 2004Jul 5, 2011Obducat AbMethod for imprint lithography at constant temperatureUS7997890 *Sep 27, 2007Aug 16, 2011Obducat AbDevice and method for lithographyUS8011915Mar 1, 2006Sep 6, 2011Asml Netherlands B.V.Imprint lithographyUS8015939Jun 30, 2006Sep 13, 2011Asml Netherlands B.V.Imprintable medium dispenserUS8025830Nov 27, 2009Sep 27, 2011Korea Institute Of Machinery & MaterialsUV nanoimprint lithography process and apparatusUS8100684Feb 24, 2009Jan 24, 2012Asml Netherlands B.V.Imprint lithographyUS8131078Nov 10, 2009Mar 6, 2012Asml Netherlands B.V.Imprint lithographyUS8144309Sep 5, 2007Mar 27, 2012Asml Netherlands B.V.Imprint lithographyUS8147235 *Nov 3, 2004Apr 3, 2012Obducat AbDevice and method for large area lithographyUS8241550Oct 6, 2009Aug 14, 2012Asml Netherlands B.V.Imprint lithographyUS8318253Jun 30, 2006Nov 27, 2012Asml Netherlands B.V.Imprint lithographyUS8323541Feb 22, 2012Dec 4, 2012Asml Netherlands B.V.Imprint lithographyUS8349238Jun 17, 2010Jan 8, 2013Asml Netherlands B.V.Imprint lithographyUS8375964Sep 15, 2009Feb 19, 2013Kabushiki Kaisha ToshibaTemplate cleaning method, system, and apparatusUS8426025Dec 10, 2009Apr 23, 2013Obducat AbProcess and method for modifying polymer film surface interactionUS8449285 *Jan 21, 2011May 28, 2013Hepregen CorporationSystems and methods for micro-contact stampingUS8486485Jul 29, 2011Jul 16, 2013Asml Netherlands B.V.Method of dispensing imprintable mediumUS8571318Feb 8, 2012Oct 29, 2013Asml Netherlands B.V.Imprint lithographyUS20080213418 *Oct 31, 2007Sep 4, 2008Hua TanAlign-transfer-imprint system for imprint lithogrphyUS20080223237 *Jan 25, 2008Sep 18, 2008Takashi AndoImprint device, stamper and pattern transfer methodUS20120000382 *Sep 15, 2011Jan 5, 2012Sony CorporationMethod for producing metal thin filmUS20120067280 *Sep 19, 2011Mar 22, 2012Appleton Papers Inc.Activator means for pre-applied adhesivesUS20120103222 *Jan 9, 2012May 3, 2012Sony CorporationMethod for producing metal thin filmUS20120187082 *Jan 21, 2011Jul 26, 2012Hepregen CorporationSystems and methods for micro-contact stampingCN100533270CDec 29, 2005Aug 26, 2009显示器生产服务株式会社Apparatus for forming fine patternDE102008030981A1Jun 27, 2008Dec 31, 2009BAM Bundesanstalt f�r Materialforschung und -pr�fungHydraulische PositionierungseinheitEP1533657A1 *Nov 21, 2003May 25, 2005Obducat ABMultilayer nano imprint lithographyEP2151702A2May 29, 2009Feb 10, 2010BAM Bundesanstalt f�r Materialforschung und -pr�fungHydraulic positioning unitWO2006036433A2 *Aug 30, 2005Apr 6, 2006Hewlett Packard Development CoImprint lithography apparatus and method employing an effective pressureWO2013171420A1 *May 14, 2013Nov 21, 2013Saint-Gobain Glass FranceMethod for texturing a substrate having a large surface area* Cited by examinerClassifications U.S. Classification101/494International ClassificationG03F7/00, H01L21/027, G03F7/20, B41M1/06, B81C99/00Cooperative ClassificationB41M1/06, B82Y10/00, B82Y40/00, G03F7/0002European ClassificationB82Y10/00, B82Y40/00, G03F7/00ALegal EventsDateCodeEventDescriptionSep 14, 2010FPAYFee paymentYear of fee payment: 4Aug 1, 2002ASAssignmentOwner name: OBDUCAT AKTIEBOLAG, SWEDENFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:HEIDARI, BABAK;REEL/FRAME:013144/0262Effective date: 20020510RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services©2012 Google