Patent US5891576 - Card - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsA card having a paper as a base material laminated with decomposable plastic layers having such properties as durability, banding resistance, water resistance, chemical resistance, waterproofness, surface smoothness, glossiness end workability. Any visible information/design portion and/or a magnetic...http://www.google.com/patents/US5891576?utm_source=gb-gplus-sharePatent US5891576 - CardAdvanced Patent SearchPublication numberUS5891576 APublication typeGrantApplication numberUS 08/541,593Publication dateApr 6, 1999Filing dateOct 10, 1995Priority dateJun 16, 1993Fee statusLapsedAlso published asEP0629975A2, EP0629975A3Publication number08541593, 541593, US 5891576 A, US 5891576A, US-A-5891576, US5891576 A, US5891576AInventorsToshibumi Imai, Akihiko Kobayashi, Tsutomu Shikakubo, Masayuki Taniguchi, Kazuya Yabusa, Testuo Aizawa, Motoko YoshikawaOriginal AssigneeToppan Printing Co., Ltd.Export CitationBiBTeX, EndNote, RefManPatent Citations (14), Referenced by (20), Classifications (18), Legal Events (3) External Links: USPTO, USPTO Assignment, EspacenetCard
US 5891576 AAbstract
A card having a paper as a base material laminated with decomposable plastic layers having such properties as durability, banding resistance, water resistance, chemical resistance, waterproofness, surface smoothness, glossiness end workability. Any visible information/design portion and/or a magnetic recording portion may be formed as required. The present invention improves the durability of a card using paper as a base material and provides the card which spontaneously decomposes even when left after being discarded.
1. A card for recording character and pattern information, said card consisting essentially of:a substantially planar layer of uniform thickness of a resilient base material selected from the group consisting of paper and card board, and at least one plastic layer which is a decomposable plastic having decomposition properties equal to or better than those of the base material, which is at least one member selected from the group consisting of microorganism-derived polyesters, aliphatic polyesters, polyglycolides and polyalcohol-starch composite materials, said plastic layer being laminated on the layer of the base material, wherein character and pattern information can be printed on at least one of said layer of the base material and plastic layer, and the card in its entirety is substantially decomposable spontaneously when held in activated sludge. 2. The card according to claim 1, wherein said decomposable plastic is a microorganism-derived polyester.
3. The card according to claim 2 wherein said microorganism-derived polyester is 3-hydroxybutyric acid-3-hydroxyvaleric acid copolymer P.
4. The card according to claim 1, wherein said decomposable plastic is an aliphatic polyester.
5. The card according to claim 4, wherein said aliphatic polyester is a polycaprolactam.
6. The card according to claim 1, wherein said decomposable plastic is a polyglycolide.
7. The card according to claim 6, wherein said polyglycolide is a polyacetate.
8. The card according to claim 1, wherein said decomposable plastic is a polyalcohol-starch composite material.
9. The card according to claim 1, wherein the plastic layer has a thickness of 30 μm.
10. The card according to claim 9, wherein said microorganism-derived polyester is 3-hydroxybutyric acid-3-hydroxyvaleric acid copolymer P.
11. The card according to claim 10, wherein said aliphatic polyester is a polycaprolactam.
12. The card according to claim 11, wherein said polyglycolide is a polyacetate.
13. A card for recording character, pattern and digital information, said card consisting essentially of:a substantially planar layer of uniform thickness of a resilient base material selected from the group consisting of paper and cardboard, at least one plastic layer which is a decomposable plastic having decomposition properties equal to or better than those of the base material, which is at least one member selected from the group consisting of microorganism-derived polyesters, aliphatic polyesters, polyglycolides and polyalcohol-starch composite materials, said plastic layer being laminated on the layer of the base material, and at least one layer for recording digital information selected from the group consisting of a magnetic recording layer and an optical recording layer, said layer for recording digital information being formed on either one of said layer of the base material and said plastic layer, wherein character and pattern information can be printed on at least one of said layer of the base material and plastic layer, said plastic layer and said base material being substantially decomposable spontaneously when held in activated sludge. 14. The card according to claim 13, wherein said decomposable plastic is a microorganism-derived polyester.
15. The card according to claim 13, wherein said decomposable plastic is an aliphatic polyester.
16. The card according to claim 13, wherein said decomposable plastic is a polyglycolide.
17. The card according to claim 13, wherein said decomposable plastic is a polyalcohol- starch composite material.
18. The card according to claim 13, wherein the plastic layer has a thickness of 30 μm.
This application is a Continuation of application Ser. No. 08/258,620, filed Jun. 15, 1994, now abandoned.
The present invention relates to a disposable card used for prepaid cards, admission tickets, or a disposable card-type material used for letters of guarantee, securities and the like, and more particularly to a card whose entire composition has decomposition properties.
Currently, cards are utilized in wide fields such as ID cards or membership cards identifying social standing, cash cards, credit cards, prepaid cards, passes or traffic tickets having monetary values, or letters of guarantee, securities and the like.
Cards which have increased most in the number of cards utilized among those as mentioned above are the so-called prepaid cards in which monetary value information has been recorded equivalent to a certain amount of money previously paid.
Usually, such cards after being sold to users are discarded when users use up the full amount of money recorded. Generally such prepaid cards comprise plastics such as polyethylene terephthalate (PET) resin as a card base material, in which pattern and character information are printed on the card base material, while digital information is recorded on a magnetic recording portion or an optical recording portion provided on the card base material. Although such plastic cards after being fully used are currently disposed of by incineration or by landfill as a waste, plastic waste, when being incinerated, causes burning temperature to become higher, leading to problems with the durability of incinerators and with the environmental pollution due to combustion gas, while plastic waste, when being used for landfill, does not decompose, remaining as it is, so that it remains permanently as refuse, leading to problems with the effect on natural environment.
Heretofore, there have been produced and utilized cards employing paper as their base material, which paper is easy to be discarded for incineration or landfill and less expensive in manufacturing cost, so that paper has been considered to be an optimum card material with respect to the above-mentioned, currently-discussed environmental problems.
Also recently, as disclosed in Japanese Laid-Open Patent Application No. 57-150393, Japanese Laid-Open Patent Application No.59-220192, Japanese Laid-Open Patent Application No.51-93991, Japanese Laid-Open Patent Application No.63-260912 and Japanese Laid-Open Patent Application No.57-150393, plastics, which are decomposable under natural environment such as light or underground condition, have been developed, have been particularly for throwaway products, and have now commercially been available partly. With respect to the cards field, Japanese Laid-Open Patent Application No.5-42786 and Japanese Laid-Open Patent Application No.5-85088 by the present applicant disclose that decomposable plastics are used for card base material. Problems that the Invention is to solve
However, where paper is used for card base material as shown in FIG. 3, considering the suitability for cards, such as durability, bending resistance, water resistance, chemical resistance, waterproofness, surface smoothness, glossiness and workability, paper is inferior in function in all respects. Thus sole paper application is limited to a temporary one such as traffic tickets, admission tickets and railway tickets, and not suitable for the above-mentioned prepaid cards used for a certain period. For such a purpose, although it is considered that an outer layer of plastics such as polyethylene, polypropylene, polyvinyl chloride and polyethylene terephthalate, or those other than plastics such as aluminum foil are laminated as a protective layer on a paper bass material as shown in FIG. 4, these cards are inferior in discardability and have a disadvantage not significantly different from plastic cards.
A card in which the base material itself is composed of a decomposable plastic gradually decomposes due to its plastic function after being discarded. However, cards are to be produced with consideration to convenience in themselves and to a problem with card manufacture, so that where a decomposable plastic is used only for a card base material, problems as shown below exist.
The problems exist in that first a card is required to have a certain thickness from the strength and user-friendliness points of view, so that when the card is molded, a warpage develops on the card surface; that the decomposition of a decomposable plastic requires a longer time corresponding to such thickness; and that since a decomposable plastic is expensive, the card itself becomes expensive.
Thus, the present invention is made to solve the above-mentioned problems, and the card is the one in which at least one plastic layer having decomposition properties is laminated on one side or both sides of a card base material made of paper end the like.
The card is the one in which said plastic layer is a decomposable plastic decomposing through light or microorganism.
The card is the one in which a magnetic recording layer is formed on said card base material or said plastic layer.
The card is the one in which an optical recording layer is formed on said card base material or said plastic layer.
According to the card of the present invention, by the use of a decomposable paper as a card base material, and of decomposable plastics having properties such as durability, bending resistance, water resistance, chemical resistance, waterproofness, surface smoothness, glossiness and workability, as an outer layer, the durability of the entire card is improved and the card, even if left after being discarded, will spontaneously decompose.
FIG. 1 is a sectional view showing one example of a card of the present invention.
FIG. 2 is a sectional view showing another example of a card of the present invention.
FIG. 3 is a sectional view of a conventional card formed of only a paper.
FIG. 4 is a sectional view of a conventional card in which polyethylene layers are laminated.
With reference to drawings, embodiments of the present invention will be explained in detail.
FIGS. 1 and 2 show sectional views of a card of the present invention.
A card 1 of the present invention shown in FIG. 1 is formed by laminating decomposable plastic layers 3 on a paper base material 2 such as paper.
The paper base material 2 is a sheet to be generally-used for a statistic card, a cardboard and the like, and employs the one having high smoothness, strong resilience, no warpage, uniform thickness and stable dimensions. If the above-mentioned conditions are satisfied, even recycled paper can be used.
The decomposable plastic layers 3, for which a decomposable plastic having decomposition properties equal to or better than the above-mentioned paper base material is suitable, can employ, for example, microorganism-derived polyesters such as 3-hydroxybutyric acid-3-hydroxyvaleric acid copolymer P (3HB-3HV), aliphatic polyesters such as polycaprolactam (PCL), polyglycolides such as polylactate, and polyvinyl alcohol-starch composite materials, and may employ mixture or laminated material of these decomposable plastics,
The decomposable plastic layers 3 laminated on the paper base material 2 may be used if it has certain decomposition properties, and different kinds of decomposable plastic layers 3 may be used for each surface of the paper base material 2.
A nondecomposable material such as various additives and polymers can be added to these decomposable plastics if the material to the decomposable plastics ratio is 50% or less in weight. An addition of nondecomposable material with a ratio of 50% or more is not preferable because it causes decomposition properties to be remarkably decreased and a problem with machining to be developed.
The method of laminating a decomposable plastic layer on a paper base material can employ the conventional method of manufacturing common plastic laminated paper, which includes various methods such as lamination of plastic film onto paper base material, melt extrusion coating of plastic onto paper base material and so on.
The laminating method suitable for the card of the present invention employs a T-die type mono-layer or multi-layer extrusion laminating method, which includes multi-manifold method and field block method either of which may be used.
Furthermore, a method of heat lamination of paper with film may be used.
With the T-die type multi-layer extrusion laminating method, together with polyolefin, straight-chain copolyester, i.e. 3-hydroxybutyric acid-3-hydroxyvaleric acid copolymer having a low processing temperature are extruded, causing an extra heat to be absorbed by the polyolefin having a large specific heat, so that the straight-chain copolyester of 3-hydroxybutyric acid-3-hydroxyvaleric acid copolymer will not decompose thermally.
For lamination, an adhesive agent is often required to use. Although for the manufacture of the card of the present invention, due to less coating quantity the kind of adhesive agent is not particularly specified, it is preferable to use an aqueous adhesive agent not affecting the decomposition properties of plastic laminated paper.
By means of the above-mentioned method, the decomposable plastic layers 3 are laminated on the paper base material 2 to form the card. The printing and machining onto the card can employ a method similar to conventional paper/plastic cards, such that by a printing technique such as offset printing, screen printing and gravure printing, a visible information/design portion 4 such as pattern and character are printed on the paper base material 2 or the decomposable plastic layers 3, which are then machined to a card size by the use of a punching machine to manufacture the card,
Further, an information recording layer such as a magnetic recording layer or an optical recording layer can be formed on the card, in which case the magnetic recording layer 5 is previously formed on the paper base material 2 before the decomposable plastic layer 3 is laminated thereon, or the magnetic recording layer 5 is formed after the decomposable plastic layer 3 is laminated on the paper base material 2. The forming method includes coating of a dispersion in which magnetic recording material is dispersed in a binder and the like, or lamination of a sheet having formed a magnetic recording layer.
A specific embodiment of the present invention will be given and explained in detail hereinafter.
The straight-chain copolyester of 3-hydroxybutyric acid-3-hydroxyvaleric acid copolymer P (3HB-3HV) having decomposition properties (made by Zeneka Co. in England: trade-name "Biopole" containing hydroxyvaleric acid by 12%) was laminated on both surfaces of a rolled cardboard (non-coated ivory board: 180 g/m2) to a thickness of 30 μm by the T-die melt extrusion method to form the card 1 as shown in FIG. 1.
The periodic observation of the decomposing state of the prepared card after being buried in the soil of a farm revealed that after one month the plastic layer 3 was almost completely decomposed and only the paper base material 2 remained though the shape was held; and that after six months the shape of the card was not held and only about half of the paper base material 2 remained.
A card 7 having a composition shown in FIG. 3 was produced by using a rolled cardboard (non-coated ivory board: 230 g/m2) as a paper base material 6. The periodic observation of the decomposing state of the card after being buried in the soil of a farm revealed that after six months the shape was not held and only about half of the paper base material remained.
By using a plastic laminated paper formed by laminating 15 μm-thick polyethylene layer 8 instead of the straight-chain copolyester of 3-hydroxybutyric acid-3-hydroxyvaleric acid copolymer P (3HB-3HV) of the example 1, a card 9 having a similar composition was produced as shown in FIG. 4. The periodic observation of the decomposing state of the card after being buried in the soil of a farm revealed that even after six months the shape was held and the surface polyethylene layer was not changed to an extant that the propagation of mold was found locally on the surface of the paper base material on which the polyethylene layer was not laminated.
Table 1 shows the results of comparison in strength, water resistance and the like among the example 1, and the comparative examples 1 and 2.
TABLE 1______________________________________                      Comparative                               Comparative            Example 1 Example 1                               example 2______________________________________Tensile Longer   20.7      18.5     21.8strength   side(kgf)   Shorter  12.5      10.7     11.6   sideTear    Longer   283       252      289strength   side(gf)    Shorter  262       223      255   sideBending Longer   1012      846      952resistance   sidestrength   Shorter  1049      953      1021(times) sideRupture          8.6       6.5      8.8strength(kgf/cm2)Rigidity   Longer   45.6      39.8     46.2(gf/cm) side   Shorter  24.7      22.5     25.6   sideWater            No        Shape    Noresistance       unusual   changed  unusual            state              state______________________________________
The card of comparative example 1, though the paper itself has decomposition properties, is inferior in strength and resistance, while the one of comparative example 2, though it is superior in strength and resistance, has no decomposition properties in itself and a disadvantage of preventing the decomposition properties of the paper base material due to the coating of the polyethylene.
On the contrary, the card used in the example according to the present invention has a card workability similar to the card by conventional plastic laminated paper, and its plastic layer, even when left in an activated sludge tank, substantially decomposed, while its paper base material absorbed water content to cause the fiber to become disentangled, thereby retaining little shape.
According to the present invention as described above, the card is composed by laminating of a plastic having decomposition properties on a paper bass material, so that the paper base material does not lose its original decomposition properties, while the plastic having decomposition properties decomposes together with the paper base material, and in addition the card having a laminated composition is superior in strength/resistance.
Using paper as a base material allows the thickness of a plastic having decomposition properties, that is, its usage to be reduced and thus makes it possible to reduce its manufacturing cost, while the card has almost the same strength/resistance as the one using conventional plastics, so that it can sufficiently withstand applications such as current throwaway cards.
The plastic having decomposition properties used for the card of the present invention, though inferior in physical properties and workability to conventional plastics, may improve its physical properties and workability by being mixed with an additive or a non-decomposable plastic to such an extent as not to deteriorate decomposition properties.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3808404 *Dec 29, 1971Apr 30, 1974Magneguide CorpMagnetic identification cardUS4980023 *Dec 5, 1988Dec 25, 1990Enso-Gutzeit OyMethod for manufacturing paper or cardboard and product containing cellulaseUS5122561 *Dec 21, 1990Jun 16, 1992Kuraray Co., Ltd.Disposable moldings and polymer compositions for their productionUS5138029 *Jul 3, 1991Aug 11, 1992Showa Denko K.K.Biodegradable or biocompatible copolymer and process for producing sameUS5197763 *Jan 10, 1992Mar 30, 1993Whalen Thomas EBiomedical information card and method of makingUS5292860 *Sep 16, 1992Mar 8, 1994Kanegafuchi Kagaku Kogyo Kabushiki KaishaCopolymer and method for production thereofUS5336871 *Feb 7, 1992Aug 9, 1994American Bank Note Holographics, IncorporatedHolographic enhancement of card securityUS5346817 *Jun 23, 1992Sep 13, 1994Asahi Kasei Kogyo Kabushiki KaishaMethod for producing a microbial polyesterUS5346929 *Mar 18, 1992Sep 13, 1994Alvin GuttagBiodegradable plastic and articles made therefromEP0232705A2 *Jan 7, 1987Aug 19, 1987Orga-Kartensysteme GmbHElectronic data carriers and process for their manufactureJPH0462054A * Title not availableJPH0585088A * Title not availableJPH0740688A * Title not availableJPH07266771A * Title not available* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS6338211Jan 4, 2001Jan 15, 2002Mary Lou CarneyMemorial marker for staking in a graveUS6350530 *Mar 24, 1997Feb 26, 2002Gunze LimitedBiodegradable card baseUS7128704 *Dec 6, 2002Oct 31, 2006Bag To Earth, Inc.Wet waste compostable bag and method and apparatus for manufacturing sameUS7332052Nov 19, 2004Feb 19, 2008Bag To Earth, Inc.Wet waste compostable bag and method and apparatus for manufacturing sameUS8389107Jul 14, 2011Mar 5, 2013Biovation, LlcCellulosic biolaminate composite assembly and related methodsUS8652617Jul 22, 2011Feb 18, 2014Biovation, LlcBiolaminate composite assembly including polylactic acid and natural wax laminate layer, and related methodsUS9090021Aug 2, 2012Jul 28, 2015Frito-Lay North America, Inc.Ultrasonic sealing of packagesUS9149980Aug 2, 2012Oct 6, 2015Frito-Lay North America, Inc.Ultrasonic sealing of packagesUS9162421Apr 25, 2012Oct 20, 2015Frito-Lay North America, Inc.Film with compostable heat seal layerUS9284104Jun 21, 2013Mar 15, 2016Frito-Lay North America, Inc.Deposition of ultra-thin inorganic oxide coatings on packagingUS20030079824 *Dec 6, 2002May 1, 2003Prescott Paper Products (Usa), Inc.Wet waste compostable bag and method and apparatus for manufacturing sameUS20050087293 *Nov 19, 2004Apr 28, 2005Prescott Paper Products (Usa), Inc.Wet waste compostable bag and method and apparatus for manufacturing sameUS20080277481 *Mar 3, 2008Nov 13, 2008David EngelRenewable cardsUS20090065138 *Nov 5, 2008Mar 12, 2009Innovative Graphics, Inc.Manufacture of environmentally safe cardsUS20090184168 *Jul 23, 2009Roger RickettsRecyclable plastic cards and methods of making sameUS20100015420 *Mar 24, 2009Jan 21, 2010Michael RiebelBiolaminate composite assembly and related methodsUS20110084148 *Oct 14, 2010Apr 14, 2011Ricketts Roger HPlastic cards made from post-consumer plasticUS20110123809 *May 26, 2011Biovation, LlcBiolaminate composite assembly and related methodsUS20130101855 *Apr 25, 2013Frito-Lay North America, Inc.Barrier paper packaging and process for its productionWO2009109033A1 *Feb 10, 2009Sep 11, 2009Innovative Graphics IncManufacture of environmentally safe cards* Cited by examinerClassifications U.S. Classification428/411.1, 523/128, 428/537.5, 428/847, 523/124, 428/481, 428/480International ClassificationG06K19/02, B42D15/10, G06K19/04Cooperative ClassificationY10T428/31993, Y10T428/31504, G06K19/041, Y10T428/31786, G06K19/02, Y10T428/3179European ClassificationG06K19/02, G06K19/04KLegal EventsDateCodeEventDescriptionOct 23, 2002REMIMaintenance fee reminder mailedApr 7, 2003LAPSLapse for failure to pay maintenance feesJun 3, 2003FPExpired due to failure to pay maintenance feeEffective date: 20030406RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services