US7955719B2 - Tandem OLED device with intermediate connector - Google Patents
Tandem OLED device with intermediate connector Download PDF
US7955719B2
US7955719B2 US12022427 US2242708A US7955719B2 US 7955719 B2 US7955719 B2 US 7955719B2 US 12022427 US12022427 US 12022427 US 2242708 A US2242708 A US 2242708A US 7955719 B2 US7955719 B2 US 7955719B2
Active, expires 2029-11-22
US12022427
US20090191428A1 (en )
William J. Begley
H01L51/002—Making n- or p-doped regions
A tandem OLED device including an anode; a cathode; at least two electroluminescent units disposed between the anode and the cathode, wherein each of the electroluminescent units includes at least one hole-transporting layer and one organic light-emitting layer; and an intermediate connector disposed between adjacent electroluminescent units, wherein the intermediate connector includes an n-doped organic layer and an electron-accepting layer, the electron-accepting layer being disposed closer to the cathode than the n-doped organic layer, and wherein the n-doped organic layer includes an alkali metal and an organic alkali metal complex.
Reference is made to commonly assigned U.S. patent application Ser. No. 11/393,767, Filed Mar. 30, 2006, now U.S. Published Patent Application No. 2007/0228938, entitled “Efficient White Light OLED Display with Filters” by T. K. Hatwar et al, U.S. patent application Ser. No. 11/259,472 Filed Oct. 26, 2005, now U.S. Published Patent Application No. 2006/0286405, entitled “Organic Element for Low Voltage Electroluminescent Devices” by William J. Begley et al, and U.S. patent application Ser. No. 12/023,216 filed Jan. 31, 2008, now U.S. Pat. No. 7,821,201, entitled “Tandem OLED Device With Intermediate Connector” by T. K. Hatwar et al, the disclosures of which are incorporated herein by reference.
The present invention relates to tandem OLED devices and to intermediate connectors between them.
An organic light-emitting diode device, also called an OLED, commonly includes an anode, a cathode, and an organic electroluminescent (EL) unit sandwiched between the anode and the cathode. The organic EL unit commonly includes a hole-transporting layer (HTL), a light-emitting layer (LEL), and an electron-transporting layer (ETL). OLEDs are attractive because of their low drive voltage, high luminance, wide viewing-angle, and capability for full color displays and for other applications. Tang et al. described this multilayer OLED in their U.S. Pat. Nos. 4,769,292 and 4,885,211.
OLEDs can emit different colors, such as red, green, blue, or white, depending on the emitting property of its LEL. Recently, there is an increasing demand for broadband OLEDs to be incorporated into various applications, such as a solid-state lighting source, color display, or a full color display. By broadband emission, it is meant that an OLED emits sufficiently broad light throughout the visible spectrum so that such light can be used in conjunction with filters or color change modules to produce displays with at least two different colors or a full color display. In particular, there is a need for broadband-light-emitting OLEDs (or broadband OLEDs) where there is substantial emission in the red, green, and blue portions of the spectrum, i.e., a white light-emitting OLED (white OLED). The use of white OLEDs with color filters provides a simpler manufacturing process than an OLED having separately patterned red, green, and blue emitters. This can result in higher throughput, increased yield, and cost savings. White OLEDs have been reported, e.g. by Kido et al. in Applied Physics Letters, 64, 815 (1994), J. Shi et al. in U.S. Pat. No. 5,683,823, Sato et al. in JP 07-142169, Deshpande et al. in Applied Physics Letters, 75, 888 (1999), and Tokito, et al. in Applied Physics Letters, 83, 2459 (2003).
In order to achieve broadband emission from an OLED, more than one type of molecule has to be excited, because each type of molecule only emits light with a relatively narrow spectrum under normal conditions. A light-emitting layer having a host material and one or more luminescent dopant(s) can achieve light emission from both the host and the dopant(s), resulting in a broadband emission in the visible spectrum if the energy transfer from the host material to the dopant(s) is incomplete. To achieve a white OLED having a single light-emitting layer, the concentrations of light-emitting dopants must be carefully controlled. This produces manufacturing difficulties. A white OLED having two or more light-emitting layers can have better color and better luminance efficiency than a device with one light-emitting layer, and the variability tolerance for dopant concentration is higher. It has also been found that white OLEDs having two light-emitting layers are typically more stable than OLEDs having a single light-emitting layer. However, it is difficult to achieve light emission with strong intensity in the red, green, and blue portions of the spectrum. A white OLED with two light-emitting layers typically has two intensive emission peaks.
A tandem OLED structure (sometimes called a stacked OLED or a cascaded OLED) has been disclosed by Jones et al. in U.S. Pat. No. 6,337,492, Tanaka et al. in U.S. Pat. No. 6,107,734, Kido et al. in JP Patent Publication 2003/045676A and U.S. Published Patent Application No. 2003/0189401 A1, and Liao et al. in U.S. Pat. No. 6,717,358 and U.S. Patent Application Publication No. 2003/0170491 A1. This tandem OLED is fabricated by stacking several individual OLED units vertically and driving the stack using a single power source. The advantage is that luminance efficiency, lifetime, or both are increased. However, the tandem structure increases the driving voltage approximately in proportion to the number of OLED units stacked together.
Matsumoto and Kido et al. reported in SID 03 Digest, 979 (2003) that a tandem white OLED is constructed by connecting a greenish-blue EL unit and an orange EL unit in the device, and white light emission is achieved by driving this device with a single power source. Although luminance efficiency is increased, this tandem white OLED device has weaker green and red color components in the spectrum. In U.S. Patent Application Publication No. 2003/0170491 A1, Liao et al. describe a tandem white OLED structure by connecting a red EL unit, a green EL unit, and a blue EL unit in series within the device. When the tandem white OLED is driven by a single power source, white light emission is formed by spectral combination from the red, green, and blue EL units.
Notwithstanding these developments, there remains a need to improve efficiency and driving voltage of tandem OLED devices while maintaining good broadband emission.
It is therefore an object of the present invention to provide an OLED device with improved efficiency and luminance stability.
This object is achieved by a tandem OLED device comprising:
(c) at least two electroluminescent units disposed between the anode and the cathode, wherein each of the electroluminescent units includes at least one hole-transporting layer and one organic light-emitting layer; and
(d) an intermediate connector disposed between adjacent electroluminescent units, wherein the intermediate connector includes an n-doped organic layer and an electron-accepting layer, the electron-accepting layer being disposed closer to the cathode than the n-doped organic layer, and wherein the n-doped organic layer includes an alkali metal and an organic alkali metal complex.
It is an advantage of this invention that it can provide improved efficiency, or lower drive voltage, or both.
FIG. 1 shows a cross-sectional diagram of one embodiment of a tandem OLED device according to this invention; and
FIG. 2 shows a cross-sectional diagram of another embodiment of a tandem OLED device according to this invention.
Since device feature dimensions such as layer thicknesses are frequently in sub-micrometer ranges, the drawings are scaled for ease of visualization rather than dimension accuracy.
The term “OLED device” is used in its art-recognized meaning of a display device including organic light-emitting diodes as pixels. It can mean a device having a single pixel. The term “tandem OLED device” is used in its art-recognized meaning of a display device including at least two OLED device units stacked vertically and powered by a single power source. The term “OLED display” as used herein means an OLED device including a plurality of pixels, which can be of different colors. A color OLED device emits light of at least one color. The term “pixel” is employed in its art-recognized usage to designate an area of a display panel that is stimulated to emit light independently of other areas. It is recognized that in full color systems, several pixels of different colors will be used together to produce a wide range of colors, and a viewer can term such a group a single pixel. For the purposes of this discussion, such a group will be considered several different colored pixels. In accordance with this disclosure, broadband emission is light that has significant components in multiple portions of the visible spectrum, for example, blue and green. Broadband emission can also include the situation where light is emitted in the red, green, and blue portions of the spectrum in order to produce white light. White light is that light that is perceived by a user as having a white color, or light that has an emission spectrum sufficient to be used in combination with color filters to produce a practical full color display. The term “white light-emitting” as used herein refers to a device that produces white light internally, even though part of such light can be removed by color filters before viewing.
Turning now to FIG. 1, there is shown a cross-sectional view of a pixel of a tandem white-light-emitting OLED device 10 according to one embodiment of the present invention. OLED device 10 includes a substrate 20, two spaced electrodes, which are an anode 30 and a cathode 90, at least two electroluminescent units 70 and 75 disposed between the electrodes, and an intermediate connector 80 disposed between adjacent electroluminescent units 70 and 75. Hatwar et al. in above-cited U.S. patent application Ser. No. 11/393,767 has described the use of multiple electroluminescent units of this arrangement. Each electroluminescent unit includes at least one hole-transporting layer, e.g. hole-transporting layers 40 and 45. Electroluminescent unit 70, which is closest to anode 30, can also include a hole-injecting layer 35. Electroluminescent unit 75, which is closest to cathode 90, can also include an electron-transporting layer 55. Each electroluminescent unit includes at least one organic light-emitting layer. Electroluminescent units 70 and 75 each produce different emission spectra, but that is not required for this invention. In this embodiment, electroluminescent unit 70 includes a blue light-emitting layer 50 b that includes a blue light-emitting compound and a yellow light-emitting layer 50 y that includes a yellow light-emitting compound. As used herein, the term “yellow light-emitting compound” refers to a substance that has its primary light emission in the yellow to red region, that is, from about 570 nm to 700 nm. In this embodiment, electroluminescent unit 75 includes a green light-emitting layer 51 g that includes a green light-emitting compound and produces green emission, red light-emitting layer 51 r that includes a red light-emitting compound and produces red emission, and blue light-emitting layer 51 b that includes a blue light-emitting compound and produces blue emission. The invention described herein is not limited to this combination of light-emitting layers, and many different light-emitting layers and combinations of light-emitting layers can be used as known to those skilled in the art.
Tandem OLED device 10 further includes an intermediate connector 80 disposed between adjacent electroluminescent units 70 and 75. The intermediate connector 80 provides effective carrier injection into the adjacent electroluminescent units. Metals, metal compounds, or other inorganic compounds are effective for carrier injection. However, such materials often have low resistivity, which can result in pixel crosstalk. Also, the optical transparency of the layers constituting intermediate connector 80 should be as high as possible to permit radiation produced in the electroluminescent units to exit the device. Therefore, it is often preferred to use mainly organic materials in the intermediate connector 80. Intermediate connector 80 includes an n-doped organic layer 95 and an electron-accepting layer 38. Electron-accepting layer 38 is disposed closer to cathode 90 than is n-doped organic layer 95.
In intermediate connector 80, n-doped organic layer 95 includes an alkali metal and an organic alkali metal complex. The alkali metal of the organic alkali metal complex belongs to Group 1 of the periodic table. Of these, lithium is highly preferred. Organic alkali metal complexes useful in this invention include organic lithium compounds according to Formula A:
(Li+)m(Q)n A
Q is an anionic organic ligand; and
m and n are independently selected integers selected to provide a neutral charge on the complex.
The anionic organic ligand Q is most suitably monoanionic and contains at least one ionizable site consisting of oxygen, nitrogen or carbon. In the case of enolates or other tautomeric systems containing oxygen, it will be considered and drawn with the lithium bonded to the oxygen, although the lithium can be bonded elsewhere to form a chelate. It is also desirable that the ligand contains at least one nitrogen atom that can form a coordinate or dative bond with the lithium. The integers m and n can be greater than 1 reflecting a known propensity for some organic lithium compounds to form cluster complexes.
In another embodiment, Formula B represents the organic alkali metal complex:
Z and the dashed arc represent two to four atoms and the bonds necessary to complete a 5- to 7-membered ring with the lithium cation;
each A represents hydrogen or a substituent and each B represents hydrogen or an independently selected substituent on the Z atoms, provided that two or more substituents can combine to form a fused ring or a fused ring system;
j is 0-3 and k is 1 or 2; and
Of compounds of Formula B, it is most desirable that the A and B substituents together form an additional ring system. This additional ring system can further contain additional heteroatoms to form a multidentate ligand with coordinate or dative bonding to the lithium. Desirable heteroatoms are nitrogen or oxygen. Useful compounds of Formula B have been described by Begley in U.S. Patent Application Publication No. 2006/086405, the disclosure of which is herein incorporated by reference. In Formula B, it is preferred that the oxygen shown is part of a hydroxyl, carboxy or keto group. Examples of suitable nitrogen ligands are 8-hydroxyquinoline, 2-hydroxymethylpyridine, pipecolinic acid or 2-pyridinecarboxylic acid.
Specific examples of useful organic alkali metal complexes are as follows:
Particularly useful of the above are phenanthroline derivatives, e.g. C1 and related complexes. Other examples are described by Begley.
The alkali metal in n-doped organic layer 95 is preferably lithium. The concentration of Li metal is about 0.1 to 5% by volume of the host material composition, and preferably within the 0.5 to 2% range.
In some embodiments, n-doped organic layer 95 can further include an uncharged phenanthroline derivative. Such phenanthroline derivatives are known to be useful in electron-transporting layers. A useful uncharged phenanthroline derivative is 4,7-diphenyl-1,10-phenanthroline, also known as bathophen or Bphen.
Electron-accepting layer 38 can include an inorganic compound(s), such as metal oxide, metal nitride, metal carbide, a complex of a metal ion and organic ligands, and a complex of a transition metal ion and organic ligands. Suitable materials for use in electron-accepting layer 38 can also include plasma-deposited fluorocarbon polymers (CFx) as described in U.S. Pat. No. 6,208,075, a strong oxidizing agent such as a hexaazatriphenylene derivative (Structure D) as described in U.S. Pat. No. 6,720,573 B2 and in U.S. Published Patent Application No. 2004/113547 A1, or another strong oxidizing agent, which can be organic, such as F4TCNQ or inorganic, such as molybdenum oxide, FeCl3, or FeF3. Other useful oxidizing agents, also known as electron-accepting materials, are described in commonly-assigned U.S. Ser. No. 11/867,707 by Liao et al., the disclosure of which is incorporated herein by reference.
A useful hexaazatriphenylene derivative for this purpose is hexacyanohexaazatriphenylene, which has the structure:
While not necessary, electron-accepting layer 38 can also be composed of two components: for example, one of the organic materials mentioned above, such as an amine compound, doped with a strong oxidizing agent, such as dipyrazino[2,3-f:2′,3′-h]quinoxalinehexacarbonitrile, F4TCNQ, or FeCl3.
OLED devices are commonly formed on a supporting substrate, e.g. OLED substrate 20. The electrode in contact with the substrate is conveniently referred to as the bottom electrode. The substrate 20 can either be light transmissive or opaque, depending on the intended direction of light emission. The light transmissive property is desirable for viewing the EL emission through the substrate. Transparent glass or plastic is commonly employed in such cases. For applications where the EL emission is viewed through the top electrode, the transmissive characteristic of the bottom support is immaterial, and therefore can be light transmissive, light-absorbing, or light reflective. Substrates for use in this case include, but are not limited to, glass, plastic, semiconductor materials, silicon, ceramics, and circuit board materials. Of course, it is necessary to provide in these device configurations a light-transparent top electrode.
An anode 30 is formed over substrate 20. When EL emission is viewed through the anode, the anode should be transparent, or substantially transparent, to the emission of interest. Common transparent anode materials used in the present invention are indium-tin oxide (ITO), indium-zinc oxide (IZO), and tin oxide, but other metal oxides can work including, but not limited to, aluminum- or indium-doped zinc oxide, magnesium-indium oxide, and nickel-tungsten oxide. In addition to these oxides, metal nitrides such as gallium nitride, and metal selenides such as zinc selenide, and metal sulfides such as zinc sulfide, can be used as the anode. For applications where EL emission is viewed only through the cathode electrode, the transmissive characteristics of the anode are immaterial and many conductive materials can be used, regardless if transparent, opaque, or reflective. Example conductors for the present invention include, but are not limited to, gold, iridium, molybdenum, palladium, and platinum. Typical anode materials, transmissive or otherwise, have a work function no less than 4.0 eV. Desired anode materials can be deposited by any suitable process such as evaporation, sputtering, chemical vapor deposition, or electrochemical deposition. If necessary, anode materials can be patterned using well-known photolithographic processes.
A cathode 90 is formed over the other OLED layers. If the device is top-emitting, the electrode must be transparent or nearly transparent. For such applications, metals must be thin (preferably less than 25 nm) or one must use transparent conductive oxides (e.g. indium-tin oxide, indium-zinc oxide), or a combination of these materials. Optically transparent cathodes have been described in more detail in U.S. Pat. No. 5,776,623. If the device is bottom-emitting, the cathode can be any conductive material known to be useful in OLED devices, including metals such as aluminum, molybdenum, gold, iridium, silver, magnesium, the above transparent conductive oxides, or combinations of these. Desirable materials promote electron injection at low voltage and have effective stability. Useful cathode materials often contain a low work function metal (<4.0 eV) or metal alloy. Cathode materials can be deposited by evaporation, sputtering, or chemical vapor deposition. When needed, patterning can be achieved through many well known methods including, but not limited to, through-mask deposition, integral shadow masking as described in U.S. Pat. No. 5,276,380 and EP 0 732 868, laser ablation, and selective chemical vapor deposition.
Hole-injecting layer 35 can be formed of a single or a mixture of organic or inorganic materials. The hole-injecting layer can be divided into several layers, with each layer being composed of either the same or different materials. The hole-injecting material can serve to improve the film formation property of subsequent organic layers and to facilitate injection of holes into the hole-transporting layer. Suitable materials for use in the hole-injecting layer are electron-deficient materials that include, but are not limited to porphyrin and phthalocyanine compounds as described in U.S. Pat. No. 4,720,432, phosphazine compounds, and certain aromatic amine compounds which are stronger electron donors than conventional hole-transporting layer materials, such as N,N,N,N-tetraarylbenzidine compounds. In another useful embodiment, the hole-injecting layer includes a compound incorporating a para-phenylenediamine as taught in EP 0 891 121 A1 and EP 1 029 909 A1, dihydrophenazine, 2,6-diaminonaphthalene, 2,6-diaminoanthracene, 2,6,9,10-tetraminoanthracene, anilinoethylene, N,N,N,N-tetraarylbenzidine, mono- or polyaminated perylene, mono- or polyaminated coronene, polyaminated pyrene, mono- or polyaminated fluoranthene, mono- or polyaminated chrysene, mono- or polyaminated anthanthrene, mono- or polyaminated triphenylene, or mono- or polyaminated tetracene moiety while the second material includes an amine compound that contains either a N,N,N,N-tetraarylbenzidine or a N-arylcarbazole moiety.
The hole-injecting layer 35 can include an inorganic compound(s), such as metal oxide, metal nitride, metal carbide, a complex of a metal ion and organic ligands, and a complex of a transition metal ion and organic ligands.
Suitable materials for use in the hole-injecting layer can also include plasma-deposited fluorocarbon polymers (CFx) as described in U.S. Pat. No. 6,208,075, a strong oxidizing agent such as a hexaazatriphenylene derivative (Structure D, above) as described in U.S. Pat. No. 6,720,573 B2 and in U.S. Published Patent Application No. 2004/113547 A1, or another strong oxidizing agent, which can be organic, such as F4TCNQ or inorganic, such as molybdenum oxide, FeCl3, or FeF3. A useful hexaazatriphenylene derivative for this purpose is hexacyanohexaazatriphenylene (Structure E, above).
While not necessary, the hole-injecting layer can also be composed of two components: for example, one of the organic materials mentioned above, such as an amine compound, doped with a strong oxidizing agent, such as dipyrazino[2,3-f:2′,3′-h]quinoxalinehexacarbonitrile, F4TCNQ, or FeCl3.
Hole-transporting layer 40 can include any hole-transporting material useful in OLED devices, many examples of which are known to those skilled in the art. Desired hole-transporting materials can be deposited by any suitable way such as evaporation, sputtering, chemical vapor deposition, electrochemical process, thermal transfer, or laser thermal transfer from a donor material. Hole-transporting materials useful in hole-transporting layers are well known to include compounds such as an aromatic tertiary amine, where the latter is understood to be a compound containing at least one trivalent nitrogen atom that is bonded only to carbon atoms, at least one of which is a member of an aromatic ring. In one form the aromatic tertiary amine can be an arylamine, such as a monoarylamine, diarylamine, triarylamine, or a polymeric arylamine. Exemplary monomeric triarylamines are illustrated by Klupfel et al. in U.S. Pat. No. 3,180,730. Other suitable triarylamines substituted with one or more vinyl radicals and/or including at least one active hydrogen-containing group are disclosed by Brantley et al. in U.S. Pat. Nos. 3,567,450 and 3,658,520.
A more preferred class of aromatic tertiary amines are those which include at least two aromatic tertiary amine moieties as described in U.S. Pat. Nos. 4,720,432 and 5,061,569. Such compounds include those represented by structural Formula F.
One class of such aromatic tertiary amines are the tetraaryldiamines. Desirable tetraaryldiamines include two diarylamino groups linked through an arylene group. Useful tetraaryldiamines include those represented by Formula G.
The various alkyl, alkylene, aryl, and arylene moieties of the foregoing structural Formulae F and G can each in turn be substituted. Typical substituents include alkyl groups, alkoxy groups, aryl groups, aryloxy groups, and halogens such as fluoride, chloride, and bromide. The various alkyl and alkylene moieties typically contain from 1 to about 6 carbon atoms. The cycloalkyl moieties can contain from 3 to about 10 carbon atoms, but typically contain five, six, or seven carbon atoms—e.g., cyclopentyl, cyclohexyl, and cycloheptyl ring structures. The aryl and arylene moieties are usually phenyl and phenylene moieties. Usefully, the hole-transporting host material is an N,N,N′,N′-tetraarylbenzidine, wherein the Are of Formula G represents a phenylene group and n equals 2.
Electron-transporting layer 55 can include any electron-transporting material useful in OLED devices, many examples of which are known to those skilled in the art. Electron-transporting layer 55 can contain one or more metal chelated oxinoid compounds, including chelates of oxine itself, also commonly referred to as 8-quinolinol or 8-hydroxyquinoline. Such compounds help to inject and transport electrons and exhibit both high levels of performance and are readily fabricated in the form of thin films. Exemplary of contemplated oxinoid compounds are those satisfying structural Formula H.
Other electron-transporting materials include various butadiene derivatives as disclosed in U.S. Pat. No. 4,356,429 and various heterocyclic optical brighteners as described in U.S. Pat. No. 4,539,507. Benzazoles, oxadiazoles, triazoles, pyridinethiadiazoles, triazines, phenanthroline derivatives, and some silole derivatives are also useful electron-transporting materials. Substituted 1,10-phenanthroline compounds known to be useful as electron-transporting materials are disclosed in JP2003/115387; JP2004/311184; JP2001/267080; and WO2002/043449.
The embodiment shown herein includes five organic light-emitting layers: blue light-emitting layers 50 b and 51 b, yellow light-emitting layer 50 y, green light-emitting layer 51 g, and red light-emitting layer 51 r. However, this invention is not limited to this configuration. A large variety of light-emitting layers are known in the art and can be used in this invention. Such light-emitting layer can include red light-emitting layers, yellow light-emitting layers, green light-emitting layers, blue light-emitting layers, or combinations of these. Light-emitting layers such as those described herein produce light in response to hole-electron recombination. Desired organic light-emitting materials can be deposited by any suitable way such as evaporation, sputtering, chemical vapor deposition, electrochemical process, or radiation thermal transfer from a donor material. The light-emitting layers in this invention include one or more host materials doped with one or more light-emitting guest compounds or dopants where light emission comes primarily from the dopant. A dopant is selected to produce color light having a particular spectrum and to have other desirable properties. Dopants are typically coated as 0.01 to 15% by weight into the host material.
A light-emitting layer can include an anthracene host, desirably a 9,10-diarylanthracene, certain derivatives of which (Formula I) are known to constitute a class of useful host materials capable of supporting electroluminescence, and are particularly suitable for light emission of wavelengths longer than 400 nm, e.g., blue, green, yellow, orange or red:
wherein R1, R2, R3, and R4 represent one or more substituents on each ring where each substituent is individually selected from the following groups:
Group 6: fluorine or cyano.
Particularly useful are compounds wherein R1 and R2, and in some cases R3 and R4, represent additional aromatic rings.
Also useful as host or co-host materials are certain hole-transporting materials such as aromatic tertiary amines (e.g. Structures F and G, above) and certain electron-transporting materials such as chelated oxinoid compounds (e.g. Structure H, above).
In addition to a host material as described above, the light-emitting layers also include one or more dopants as the first light-emitting material. A red-light-emitting dopant can include a diindenoperylene compound of the following structure J:
X1-X16 are independently selected as hydrogen or substituents that include alkyl groups of from 1 to 24 carbon atoms; aryl or substituted aryl groups of from 5 to 20 carbon atoms; hydrocarbon groups containing 4 to 24 carbon atoms that complete one or more fused aromatic rings or ring systems; or halogen, provided that the substituents are selected to provide an emission maximum between 560 nm and 640 nm.
Illustrative examples of useful red dopants of this class are shown by Hatwar et al. in U.S. Pat. No. 7,247,394, the disclosure of which is incorporated by reference.
Some other red dopants belong to the DCM class of dyes represented by Formula K:
wherein Y1-Y5 represent one or more groups independently selected from: hydro, alkyl, substituted alkyl, aryl, or substituted aryl; Y1-Y5 independently include acyclic groups or can be joined pairwise to form one or more fused rings; provided that Y3 and Y5 do not together form a fused ring. Structures of particularly useful dopants of the DCM class are shown by Ricks et al. in U.S. Pat. No. 7,252,893, the disclosure of which is incorporated by reference.
A light-emitting yellow dopant can include a compound of the following structures:
wherein A1-A6 and A′1-A′6 represent one or more substituents on each ring and where each substituent is individually selected from one of the following:
Category 6: fluoro or cyano.
Examples of particularly useful yellow dopants are shown by Ricks et al. in U.S. Pat. No. 7,252,893.
A green light-emitting dopant can include a quinacridone compound, e.g. a compound of the following structure:
wherein substituent groups R1 and R2 are independently alkyl, alkoxyl, aryl, or heteroaryl; and substituent groups R3 through R12 are independently hydrogen, alkyl, alkoxyl, halogen, aryl, or heteroaryl, and adjacent substituent groups R3 through R10 can optionally be connected to form one or more ring systems, including fused aromatic and fused heteroaromatic rings, provided that the substituents are selected to provide an emission maximum between 510 nm and 540 nm. Alkyl, alkoxyl, aryl, heteroaryl, fused aromatic ring and fused heteroaromatic ring substituent groups can be further substituted. Some examples of useful quinacridones include those disclosed in U.S. Pat. No. 5,593,788 and in U.S. Published Patent Application No. 2004/0001969A1.
A green light-emitting dopant can also include a 2,6-diaminoanthracene light-emitting dopant, as represented by the formula below:
wherein d1, d3-d5, and d7-d10 can be the same or different and each represents hydrogen or an independently selected substituent, and each h can be the same or different and each represents one or more independently selected substituents, provided that two substituents can combine to form a ring group and a-d are independently 0-5.
A blue-light-emitting dopant can include a bis(azinyl)azene boron complex compound of the structure P:
Some examples of the above class of dopants are disclosed by Ricks et al. The concentration of this class of dopants in a light-emitting layer is desirably between 0.1% and 5%.
Another class of blue dopants is the perylene class. Particularly useful blue dopants of the perylene class include perylene and tetra-t-butylperylene (TBP).
Another class of blue dopants includes blue-emitting derivatives of such styrylarenes and distyrylarenes as distyrylbenzene, styrylbiphenyl, and distyrylbiphenyl, including compounds described in U.S. Pat. No. 5,121,029, and U.S. Published Patent Application No. 2006/0093856 by Helber et al. Among such derivatives that provide blue luminescence, particularly useful in second light-emitting layer 52 are those substituted with diarylamino groups and herein termed aminostyrylarene dopants. Examples include bis[2-[4-[N,N-diarylamino]phenyl]vinyl]-benzenes of the general structure Q1 shown below:
[N,N-diarylamino][2-[4-[N,N-diarylamino]phenyl]vinyl]biphenyls of the general structure Q2 shown below:
and bis[2-[4-[N,N-diarylamino]phenyl]vinyl]biphenyls of the general structure Q3 shown below:
In Formulas Q1 to Q3, X1-X4 can be the same or different, and individually represent one or more substituents such as alkyl, aryl, fused aryl, halo, or cyano. In a preferred embodiment, X1-X4 are individually alkyl groups, each containing from one to about ten carbon atoms. A particularly preferred blue dopant of this class is disclosed by Ricks et al in U.S. Pat. No. 7,252,893.
OLED device 10 can include other layers as well. For example, an electron-injecting layer, such as alkaline or alkaline earth metals, alkali halide salts, or alkaline or alkaline earth metal doped organic layers, can also be present between cathode 90 and electron-transporting layer 55.
Turning now to FIG. 2, there is shown a cross-sectional view of another embodiment of a tandem OLED device 15 in accordance with this invention. In this embodiment, an intermediate connector 85 further includes undoped layer 65, which is in contact with n-doped layer 95, and which is closer to anode 30 than to cathode 90. An undoped layer 65 includes an aromatic hydrocarbon derivative, desirably an anthracene derivative as described above for Structure I. Undoped layer 65 can also include an organic alkali metal complex, as described above for Structure A. An example of an organic alkali metal complex useful in undoped layer 65 is a salt of hydroxyquinoline, e.g. 8-quinolinolato lithium:
The invention and its advantages can be better appreciated by the following comparative examples. Examples 3 to 6 are representative examples of this invention, while Examples 1 and 2 are non-inventive tandem OLED examples for comparison purposes. The layers described as vacuum-deposited were deposited by evaporation from heated boats under a vacuum of approximately 10−6 Torr. After deposition of the OLED layers each device was then transferred to a dry box for encapsulation. The OLED has an emission area of 10 mm2. The devices were tested by applying a current of 20 mA/cm2 across electrodes. The results from Examples 1 to 6 are given in Table 1.
Device data measured at 20 mA/cm2
Lum Power
Luminance Efficiency Efficiency
Device # (cd/m2) Voltage (cd/A) (W/A) CIEx CIEy lm/W QE %
Example 1 2955 9.3 14.8 0.150 0.312 0.346 5.0 6.6
Example 2 3005 9.2 15.0 0.153 0.311 0.346 5.1 6.7
Example 3 3072 8.6 15.3 0.149 0.327 0.363 5.6 6.6
Example 4 3036 8.8 15.2 0.148 0.320 0.361 5.5 6.5
Example 5 3446 9.1 17.2 0.164 0.333 0.374 6.0 7.3
Example 6 3377 8.9 16.9 0.165 0.328 0.359 6.0 7.3
1. A clean glass substrate was deposited by sputtering with indium tin oxide (ITO) to form a transparent electrode of 60 nm thickness.
3. The above-prepared substrate was further treated by vacuum-depositing a 10 nm layer of hexacyanohexaazatriphenylene (CHATP) as a hole-injecting layer (HIL).
4. The above-prepared substrate was further treated by vacuum-depositing a 150 nm layer of 4,4′-bis[N-(1-naphthyl)-N-phenylamino]biphenyl (NPB) as a hole-transporting layer (HTL).
5. The above-prepared substrate was further treated by vacuum-depositing a 20 nm yellow light-emitting layer including 48% NPB (as host) and 48% 9-(1-naphthyl)-10-(2-naphthyl)anthracene (NNA) as a co-host with 4% yellow-orange emitting dopant diphenyltetra-t-butylrubrene (PTBR).
6. The above-prepared substrate was further treated by vacuum-depositing a 30 nm blue light-emitting layer including 91% NNA host and 8% NPB co-host with 1% BEP as blue-emitting dopant.
7. A 40 nm n-doped organic layer was vacuum-deposited, including 49% 4,7-diphenyl-1,10-phenanthroline (also known as bathophen or Bphen), 49% tris(8-quinolinolato)aluminum (III) (ALQ) as co-host, with 2% Li metal.
8. The above-prepared substrate was further treated by vacuum-depositing a 10 nm layer of CHATP as an electron-accepting layer.
9. The above-prepared substrate was further treated by vacuum-depositing a 10 nm layer of NPB as a hole-transporting layer (HTL).
10. The above-prepared substrate was further treated by vacuum-depositing a 20 nm red light-emitting layer including 94.5% of NPB and 5% PTBR as a yellow-emitting dopant with 0.5% dibenzo{[f,f′]-4,4′7,7′-tetraphenyl]diindeno-[1,2,3-cd:1′,2′,3′-lm]perylene (TPDBP) as a red emitting dopant.
11. The above-prepared substrate was further treated by vacuum-depositing a 15 nm green light-emitting layer including 84.4% 2-phenyl-9,10-bis(2-naphthyl)anthracene (PBNA), 15% NPB, and 0.6% diphenylquinacridone (DPQ) as green emitting dopant.
12. The above-prepared substrate was further treated by vacuum-depositing a 20 nm blue light-emitting layer including 99% PBNA host with 1% BEP as blue-emitting dopant.
13. A 35 nm mixed electron-transporting layer was vacuum-deposited, including 49% Bphen, 49% ALQ as co-host, with 2% Li metal.
14. A 100 nm layer of aluminum was evaporatively deposited onto the substrate to form a cathode layer.
An OLED device was constructed as described above for Example 1 except that Step 7 was as follows:
7. A 40 nm n-doped organic layer was vacuum-deposited, including 98% Bphen as host with 2% Li metal.
7. A 40 nm n-doped organic layer was vacuum-deposited, including 98% of the lithium salt of 2-(2-hydroxyphenyl)-1,10-phenanthroline (Li-HPP) as host, with 2% Li metal.
7. A 40 nm n-doped organic layer was vacuum-deposited, including 49% Li-HPP, 49% ALQ as co-host, with 2% Li metal.
Example 5 (Inventive)
An OLED device was constructed as described above for Example 1 except that Step 6a (below) was added after Step 6, and Step 7 was as follows:
6a. The above-prepared substrate was further treated by vacuum-depositing a 30 nm undoped layer of PBNA.
7. A 10 nm n-doped organic layer was vacuum-deposited, including 98% Li-HPP as host, with 2% Li metal.
Example 6 (Inventive)
6a. The above-prepared substrate was further treated by vacuum-depositing a 20 nm undoped layer of 50% PBNA and 50% 8-quinolinolato lithium (LiQ).
7. A 20 nm n-doped organic layer was vacuum-deposited, including 98% Li-HPP as host, with 2% Li metal.
The results of testing these examples are shown in Table 1, below. The inventive examples show, relative to their respective comparative examples, improved luminance, luminance efficiency, and lumens/watt. Most also show improved drive voltage, and some show improved power efficiency and quantum efficiency.
10 OLED device
15 OLED device
30 anode
38 electron-accepting layer
45 hole-transporting layer
50 y yellow light-emitting layer
50 b blue light-emitting layer
51 r red light-emitting layer
51 g green light-emitting layer
51 b blue light-emitting layer
55 electron-transporting layer
65 undoped layer
70 electroluminescent unit
75 electroluminescent unit
80 intermediate connector
85 intermediate connector
90 cathode
95 n-doped organic layer
1. A tandem OLED device comprising:
(d) an intermediate connector disposed between adjacent electroluminescent units,
wherein the intermediate connector includes an n-doped organic layer and an electron-accepting layer, the electron-accepting layer being disposed closer to the cathode than the n-doped organic layer,
wherein the n-doped organic layer includes an alkali metal and an organic alkali metal complex, and
wherein the intermediate connector further includes an undoped layer in contact with the n-doped layer on the side closer to the anode.
2. The tandem OLED device of claim 1 wherein the organic alkali metal complex includes a phenanthroline derivative.
3. The tandem OLED device of claim 2 wherein the alkali metal is lithium.
4. The tandem OLED device of claim 3 wherein the organic alkali metal complex includes lithium.
5. The tandem OLED device of claim 4 wherein the n-doped organic layer further includes an uncharged phenanthroline derivative.
6. The tandem OLED device of claim 1 wherein the organic alkali metal complex includes a chemical compound according to the following formula:
7. The tandem OLED device of claim 1 wherein the undoped layer includes an anthracene derivative.
8. The tandem OLED device of claim 7 wherein the undoped layer further includes an organic alkali metal complex.
9. The tandem OLED device of claim 8 wherein the organic alkali metal complex in the undoped layer is a salt of hydroxyquinoline.
10. The tandem OLED of claim 1 wherein the electron-accepting layer includes a hexaazatriphenylene derivative.
US12022427 2008-01-30 2008-01-30 Tandem OLED device with intermediate connector Active 2029-11-22 US7955719B2 (en)
US12022427 US7955719B2 (en) 2008-01-30 2008-01-30 Tandem OLED device with intermediate connector
CN 200980107862 CN101960632B (en) 2008-01-30 2009-01-19 Tandem OLED device with intermediate connector
EP20090705020 EP2243176B1 (en) 2008-01-30 2009-01-19 Tandem oled device with intermediate connector
JP2010544995A JP5113913B2 (en) 2008-01-30 2009-01-19 Tandem oled device having an intermediate connection layer
PCT/US2009/000292 WO2009097084A1 (en) 2008-01-30 2009-01-19 Tandem oled device with intermediate connector
KR20107018500A KR101225674B1 (en) 2008-01-30 2009-01-19 Tandem OLED Device with Intermediate Connector
US20090191428A1 true US20090191428A1 (en) 2009-07-30
US7955719B2 true US7955719B2 (en) 2011-06-07
ID=40548857
US12022427 Active 2029-11-22 US7955719B2 (en) 2008-01-30 2008-01-30 Tandem OLED device with intermediate connector
US (1) US7955719B2 (en)
EP (1) EP2243176B1 (en)
JP (1) JP5113913B2 (en)
KR (1) KR101225674B1 (en)
CN (1) CN101960632B (en)
WO (1) WO2009097084A1 (en)
US20120138910A1 (en) * 2007-09-20 2012-06-07 Semiconductor Energy Laboratory Co., Ltd. Light-Emitting Element, Light-Emitting Device, and Electronic Device
US20140361271A1 (en) * 2008-10-28 2014-12-11 The Regents Of The University Of Michigan Stacked White OLED Having Separate Red, Green and Blue Sub-Elements
US9012902B2 (en) 2011-03-31 2015-04-21 Panasonic Intellectual Property Management Co., Ltd. Organic electroluminescent element
US9899636B2 (en) 2014-08-01 2018-02-20 Orthogonal, Inc. Photolithographic patterning of organic electronic devices
US8637854B2 (en) * 2008-05-16 2014-01-28 Lg Chem, Ltd. Stacked organic light emitting diode
KR100994118B1 (en) * 2009-01-13 2010-11-15 삼성모바일디스플레이주식회사 Organic light emitting diode and manufacturing method thereof
JP2010225563A (en) * 2009-03-25 2010-10-07 Panasonic Electric Works Co Ltd Organic el element
US8836337B2 (en) 2009-06-05 2014-09-16 Beijing Visionox Technology Co., Ltd. Organic electroluminescence device and testing method thereof
JP5498580B2 (en) * 2009-11-13 2014-05-21 北京維信諾科技有限公司 Organic el device using the organic material and the material
JP5573127B2 (en) * 2009-11-27 2014-08-20 セイコーエプソン株式会社 Emitting element, display device and electronic apparatus
GB201300532D0 (en) 2010-06-25 2013-02-27 Cambridge Display Tech Organic light-emitting composition, device and method
US8633475B2 (en) * 2010-07-16 2014-01-21 Idemitsu Kosan Co., Ltd. Organic electroluminescence device and a method for producing the device
US8637858B2 (en) 2010-09-24 2014-01-28 Novaled Ag Tandem white OLED
JP2012186091A (en) * 2011-03-07 2012-09-27 Seiko Epson Corp Light-emitting element, light-emitting device, display device, and electronic apparatus
EP2503616A1 (en) 2011-03-21 2012-09-26 Polyphotonix Limited Emissive element for light emitting device, light emitting device and method for manufacturing such element and device
DE102011117357A1 (en) * 2011-10-29 2013-05-02 Karlsruher Institut für Technologie Preparing solution of n-doped organic low molecular semiconductor comprises dissolving organic semiconductor in aprotic solvent, adding alkali metal, and optionally separating/purifying semiconductor solution under inert gas atmosphere
KR101429924B1 (en) 2011-12-08 2014-08-14 엘지디스플레이 주식회사 Tandem White Organic Emitting Device
DE102013114047B4 (en) * 2012-12-28 2016-09-01 Lg Display Co., Ltd. An organic light emitting display devices
CN103972421A (en) * 2013-01-31 2014-08-06 海洋王照明科技股份有限公司 Organic light-emitting device and production method thereof
CN104051636A (en) * 2013-03-11 2014-09-17 海洋王照明科技股份有限公司 Organic light-emitting device and preparation method thereof
KR20140140410A (en) * 2013-05-29 2014-12-09 삼성디스플레이 주식회사 Organic light emitting device
KR20150146290A (en) * 2014-06-23 2015-12-31 엘지디스플레이 주식회사 White organic light emitting device
KR20160062798A (en) * 2014-11-25 2016-06-03 엘지디스플레이 주식회사 Organic Light Emitting Device and Organic Light Emitting Display Device using the same
CN104795432A (en) * 2015-05-04 2015-07-22 京东方科技集团股份有限公司 Organic light-emitting diode device and display device
US6107734A (en) 1998-05-20 2000-08-22 Idemitsu Kosan Co., Ltd. Organic EL light emitting element with light emitting layers and intermediate conductive layer
US6337492B1 (en) 1997-07-11 2002-01-08 Emagin Corporation Serially-connected organic light emitting diode stack having conductors sandwiching each light emitting layer
JP2003045676A (en) 2001-07-26 2003-02-14 International Manufacturing & Engineering Services Co Ltd Organic electroluminescent element
US20030189401A1 (en) 2002-03-26 2003-10-09 International Manufacturing And Engineering Services Co., Ltd. Organic electroluminescent device
US6717358B1 (en) 2002-10-09 2004-04-06 Eastman Kodak Company Cascaded organic electroluminescent devices with improved voltage stability
US20060040132A1 (en) * 2004-08-20 2006-02-23 Eastman Kodak Company White OLED having multiple white electroluminescence units
US20060145604A1 (en) * 2005-01-03 2006-07-06 Eastman Kodak Company Tandem oleds having low drive voltage
US20060286405A1 (en) * 2005-06-17 2006-12-21 Eastman Kodak Company Organic element for low voltage electroluminescent devices
US20060289882A1 (en) 2004-07-30 2006-12-28 Kazuki Nishimura Organic electroluminescent element and organic electroluminescent display device
US20070001587A1 (en) 2005-06-29 2007-01-04 Eastman Kodak Company White light tandem OLED display with filters
US20070046189A1 (en) 2005-08-31 2007-03-01 Eastman Kodak Company Intermediate connector for a tandem OLED device
US20070228938A1 (en) 2006-03-30 2007-10-04 Eastman Kodak Company Efficient white-light OLED display with filters
DE102004002587B4 (en) * 2004-01-16 2006-06-01 Novaled Gmbh Picture element for an active matrix display
JP4578215B2 (en) * 2004-11-30 2010-11-10 三洋電機株式会社 The organic electroluminescent element and organic electroluminescent display device
KR100696693B1 (en) 2005-04-13 2007-03-20 삼성에스디아이 주식회사 Organic light emitting diode display
JP4837958B2 (en) * 2005-08-26 2011-12-14 淳二 城戸 The organic electroluminescence element
WO2006138075A2 (en) 2005-06-17 2006-12-28 Eastman Kodak Company Organic element for low voltage electroluminescent devices
Deshpande et al, White-light-emitting organic electroluminescent devices based on interlayer sequential energy transfer, Applied Phys. Letters, 75, 888, 1999.
Kido et al., White Light-Emitting Orgnic Electroluminescent Devices Using the Poly (N-Vinylcarbazle) Emitter Layer Doped With Three Fluorescent D, Appl. Phys. Ltr. 64 (7), Feb. 14, 1994, pp. 815-817.
Matsumoto et al., Late-News Paper: Multiphotoon Organic E1 Device Having Charge Generation Layer, SID 03 Digest, pp. 979-981; 27.5L: Date: 2003.
Tokito et al., High-Efficiency White Phosphorescent Organic Light-Emitting Devices With Greenish-Blue and Red-Emitting Layers, Appl. Phys. Ltrs.; vol. 83, No. 12, Sep. 22, 2003, pp. 2459-2461.
X. Zhou et al., "Low-voltage Inverted Transparent Vacumn Deposited Organic Light-emitting Diodes Using Electrical Doping", Applied Physics Letters, AIP, American Institute of Physics, Melville, NY, US, vol. 81, No. 5, Jul. 29, 2002, pp. 922-924, XP012033136, ISSN: 0003-6951.
US8803419B2 (en) * 2007-09-20 2014-08-12 Semiconductor Energy Laboratory Co., Ltd. Light-emitting element, light-emitting device, and electronic device
US9065067B2 (en) * 2008-10-28 2015-06-23 The Regents Of The University Of Michigan Stacked white OLED having separate red, green and blue sub-elements
CN101960632B (en) 2012-06-27 grant
JP5113913B2 (en) 2013-01-09 grant
KR101225674B1 (en) 2013-01-23 grant
EP2243176B1 (en) 2011-08-24 grant
WO2009097084A1 (en) 2009-08-06 application
KR20100129279A (en) 2010-12-08 application
US20090191428A1 (en) 2009-07-30 application
CN101960632A (en) 2011-01-26 application
EP2243176A1 (en) 2010-10-27 application
JP2011511414A (en) 2011-04-07 application
US6451455B1 (en) 2002-09-17 Metal complexes bearing both electron transporting and hole transporting moieties
US6818329B1 (en) 2004-11-16 Organic electroluminescent devices having a metal sub-layer within a hole-transporting region
US7023013B2 (en) 2006-04-04 Array of light-emitting OLED microcavity pixels
EP1408563A2 (en) 2004-04-14 Cascaded organic electroluminescent devices with improved voltage stability
US20050029933A1 (en) 2005-02-10 Cascaded organic electroluminescent devices with color filters
US20060181202A1 (en) 2006-08-17 Color organic OLED device
US20050104511A1 (en) 2005-05-19 Organic electroluminescent devices having a stability-enhancing layer
US6991859B2 (en) 2006-01-31 Cascaded organic electroluminescent devices
US20060141287A1 (en) 2006-06-29 OLEDs with improved operational lifetime
US20090091255A1 (en) 2009-04-09 White organic light emitting device
US20060105198A1 (en) 2006-05-18 Selecting white point for OLED devices
US20060008672A1 (en) 2006-01-12 Hole-trapping materials for improved OLED efficiency
EP1478025A2 (en) 2004-11-17 Cascaded organic electroluminescent device having connecting units with n-type and p-type organic layers
US20090009101A1 (en) 2009-01-08 Oled Having Stacked Organic Light-Emitting Units
US7629741B2 (en) 2009-12-08 OLED electron-injecting layer
US20050181232A1 (en) 2005-08-18 Anthracene derivative host having ranges of dopants
US20070001587A1 (en) 2007-01-04 White light tandem OLED display with filters
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HATWAR, TUKARAM K.;SPINDLER, JEFFREY P.;BEGLEY, WILLIAM J.;REEL/FRAME:020438/0064