Patent US5085830 - Process for making aluminum-lithium alloys of high toughness - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inAdvanced Patent SearchPatentsThe toughness of Al-Li, Al-Mg and Mg-Li alloys is increased by a melting and refining process designed to reduce the concentration of alkali metal impurities below about 1 ppm and preferably below about 0.1 ppm. The hydrogen and chlorine gas constituents are also significantly reduced....http://www.google.com/patents/US5085830?utm_source=gb-gplus-sharePatent US5085830 - Process for making aluminum-lithium alloys of high toughnessAdvanced Patent SearchPublication numberUS5085830 APublication typeGrantApplication numberUS 07/328,364Publication dateFeb 4, 1992Filing dateMar 24, 1989Priority dateMar 24, 1989Fee statusLapsedAlso published asCA2047197A1, DE69028849D1, DE69028849T2, EP0464152A1, EP0464152A4, EP0464152B1, EP0733717A1, US5320803, WO1990011382A1Publication number07328364, 328364, US 5085830 A, US 5085830A, US-A-5085830, US5085830 A, US5085830AInventorsDonald WebsterOriginal AssigneeComalco Aluminum LimitedExport CitationBiBTeX, EndNote, RefManPatent Citations (73), Non-Patent Citations (29), Referenced by (1), Classifications (14), Legal Events (7) External Links: USPTO, USPTO Assignment, EspacenetProcess for making aluminum-lithium alloys of high toughness
US 5085830 AAbstract
The toughness of Al-Li, Al-Mg and Mg-Li alloys is increased by a melting and refining process designed to reduce the concentration of alkali metal impurities below about 1 ppm and preferably below about 0.1 ppm. The hydrogen and chlorine gas constituents are also significantly reduced.
1. A process for preparing a high strength high toughness aluminum alloy, comprising the steps of:heating a melt comprised of an aluminum base metal and lithium including at least 1 ppm of an alkali metal impurity selected from the group consisting of sodium, potassium, rubidium and cesium, to a temperature greater than the melting point of the alloy; and refining the alloy in a vacuum for a sufficient time to reduce each alkali metal impurity to a concentration less than about 1.0 ppm. 2. The process of claim 1 wherein the vacuum is less than about 200 μm Hg and the temperature is about 50� to 100� C. above the melting point of the alloy.
3. A process for making a high strength, high toughness alloy, comprising the steps of:preparing a melt under vacuum comprised of aluminum and lithium metals including a total of at least 1.0 ppm of an alkali metal impurity selected from the group consisting of sodium, potassium, rubidium and cesium; and reducing the concentration of each of the alkali metal impurity to less than about 1.0 ppm. 4. The process of claims 1 or 3, wherein the concentration of each alkali metal impurity selected from the group consisting of sodium, potassium, rubidium and cesium is reduced to less than about 0.1 ppm.
5. The process of claim 3, wherein the alloy includes a gas selected from the group consisting of less than about 0.2 ppm hydrogen and less than about 1.0 ppm chlorine.
6. The process of claim 4, wherein the alloy includes a gas selected from the group consisting of less than about 0.1 ppm hydrogen and less than about 0.5 ppm chlorine.
7. The process of claim 4 wherein the alloy further includes an alloying element selected from the group consisting of copper, magnesium, chromium, zirconium, manganese, zinc and silicon.
8. The process of claim 4 wherein the lithium concentration is in the range of about 0.5 to 4.5%.
9. The process of claim 4 further including the step of dispersing particles in the alloy to form a composite material.
10. The process of claim 9 wherein the particles are made of a material selected from the group consisting of silicon carbide, graphite, carbon, aluminum oxide or boron carbide.
11. The process of claim 4 wherein the lithium concentration is about 1.5 to 2.6%; and the alloy further includes about 1.5 to 2.5% magnesium, and about 0.05 to 0.15% zirconium.
12. The process of claim 4 wherein the lithium concentration is about 1.8 to 2.5%; and the alloy further includes about 0.5 to 1.5% magnesium; about 0.15 to 0.5% copper and about 0.1 to 0.3% chromium.
13. The process of claim 4 wherein the lithium concentration is in the range of about 2.8 to 3.8%; and the alloy further includes about 0.5 to 1.5% magnesium; and about 0.5% to 0.15% zirconium.
14. The process of claim 4 wherein the lithium concentration is in the range of about 2.8 to 3.8%; and the alloy further includes about 0.3 to 1.3% magnesium; about 0.15 to 0.5% copper and about 0.05 to 0.5% chromium.
This invention relates to improving the physical properties of Al-Li, Al-Mg, and Mg-Li metallic products and more particularly to methods for increasing the toughness and ductility of such products without loss of strength.
High strength aluminum alloys and composites are required in certain applications, notably the aircraft industry where combinations of high strength, high stiffness and low density are particularly important. High strength is generally achieved in aluminum alloys by combinations of copper, zinc and magnesium. High stiffness is generally achieved by metal matrix composites such as those formed by the addition of silicon carbide particles or whiskers to an aluminum matrix. Recently Al-Li alloys containing 2.0 to 2.8% Li have been developed. These alloys possess a lower density and a higher elastic modulus than conventional non-lithium containing alloys.
The preparation and properties of aluminum based alloys containing lithium are widely disclosed, notably in J. Stone & Company, British patent No. 787,665 (Dec. 11, 1957); Ger. Offen. 2,305,248 (National Research Institute for Metals, Tokyo, Jan. 24, 1974); Raclot, U.S. Pat. No. 3,343,948 (Sept. 26, 1967); and Peel et al., British Patent No. 2,115,836 (Sept. 14, 1983).
Unfortunately, high strength aluminum-lithium alloys are usually characterized by low toughness, as evidenced by impact tests on notched specimens (e.g., Charpy tests, See: Metals Handbook, 9th Ed. Vol 1, pages 689-691) and by fracture toughness tests on fatigue precracked specimens where critical stress intensity factors are determined.
There have been two basic techniques used to improve the toughness of Al-Li alloys.
1. Techniques commonly used for other aluminum alloys, such as alloying (Cu, Zn, Mg), stretching 1 to 5% before aging to refine precipitation, control of recrystallization and grain growth with Zr (0.1%) and the control of initial grain size by the use of powder metallurgy.
2. The production of dispersiods in amounts greater than needed for recrystallization control using 0.5 to 2% of Mn,Zr,Fe,Ti and Co to homogenize slip distribution.
In the last 10 years these methods have had some success but the toughness of Al-Li alloys still falls short of that of conventional aluminum alloys.
Conventional techniques, for improving the toughness of Al-Li alloys, have not included the use of a vacuum melting and refining treatment. Aluminum alloys which are typically melted in air; although, vacuum melting is used by some manufacturers of high quality aluminum investment castings, such as Howmet Turbine Components Corporation who make castings of A357 and A201, to avoid dross formation. (Bouse, G. K. and Behrendt, M. R. "Advanced Casting Technology Conference", edited by Easwaren, published by ASM, 1987).
Howmet has also made experimental Al-Li-Cu-Mg investment castings by vacuum melting (Proceedings of the Al-Li Alloys Conference, held in Los Angeles March, 1987, pp. 453-465, published by ASM International) to reduce reactions between lithium and air and to reduce hydrogen pick up which occurs when lithium reacts with moisture in the air. Commercial Al-Li alloys are usually melted under an argon atmosphere which accomplishes these objectives less efficiently than vacuum but is an improvement over air melting.
Al-Li alloys although having many desirable properties for structural applications such as lower density, increased stiffness and slower fatigue crack growth rate compared to conventional aluminum alloys are generally found to have the drawback of lower toughness at equivalent strength levels.
Advantages of the subject invention are that it provides a simple, versatile and inexpensive process for improving the toughness of Al-Li, Al-Mg and Mg-Al alloys that is effective on both virgin and scrap source alloys.
Another advantage of the subject invention is that it avoids formation and incorporation of various metal oxides and other impurities commonly associated with, e.g., powder metallurgy techniques, that involve heating and/or spraying the product alloy in air or other gases.
It has now been discovered that an improved combination of high strength, high toughness and good ductility can be obtained in aluminum alloys containing primary alloying elements selected from the group consisting of Li and Mg by processing the alloys in the molten state under conditions that reduce alkali metal impurities (AMI), i.e., (Na, K, Cs, Rb) content. The processing technique involves subjecting the molten alloy to conditions that remove alkali metal impurity, e.g., a reduced pressure for a sufficient time to reduce the concentration of each alkali metal impurity to less than about 1 ppm, preferably, less than about 0.1 ppm and most preferably less than 0.01 ppm.
As noted above the process also beneficially reduces the gas (hydrogen and chlorine) content of the alloys which is expected to provide an additional, improvement in quality by reducing the formation of surface blisters and giving superior environmentally controlled properties such as stress corrosion resistance. Preferably the hydrogen concentration is reduced to less than about 0.2 ppm, more preferably, less than about 0.1 ppm. Preferably the chlorine concentration is reduced to less than about 1.0 ppm more preferably less than about 0.5 ppm.
The alloys of this invention may be used to make high strength composite materials by dispersing particles such as fibers or whiskers of silicon carbide, graphite, carbon, aluminum oxide or boron carbide therein. The term aluminum based metallic product is sometimes used herein to refer generally to both the alloys and alloy composites of the invention.
The present invention also provides improved Mg-Li alloys, for example, the experimental alloy LA141A, comprising magnesium base metal, lithium primary alloying element and less than about 1 ppm, preferably less than about 0.1 ppm, and most preferably less than about 0.01 ppm of each alkali metal impurity selected from the group consisting of sodium, potassium, rubidium and cesium. As with the Al-Li and Al-Mg alloys described above the hydrogen concentration is preferably less than about 0.2 ppm, more preferably less than about 0.1 ppm and the chlorine concentration is preferably less than about 1.0 ppm, and more preferably less than about 0.5 ppm.
The Mg-Li alloys typically include about 13.0 to 15.0 percent lithium and about 1.0 to 1.5% aluminum preferably about 14.0%, lithium and about 1.25% aluminum. The Mg-Li of this invention can be made by the process described above in connection with the Al-Li and Al-Mg alloys.
FIG. 1 is a plot of 0.2% tensile yield strength versus the Charpy impact energy at each strength level from a commercially produced A12090 alloy and a vacuum refined A12090 alloy produced by the process described herein. Property measurements are taken from both the center one third of the extrusion and the outer one third of each extrusion.
FIG. 2 is a plot of the 0.2% tensile yield strength versus the Charpy impact energy at each strength level for alloy 2 described in Example 2 and produced by the vacuum refining process described herein.
FIG. 3 is a plot of the 0.2% tensile yield strength versus the Charpy impact energy at each strength level for alloy 3 described in Example 3 and produced by the vacuum refining process described herein.
FIG. 4 is a plot of the 0.2% tensile yield strength versus the Charpy impact energy at each strength level for alloy 4 described in Example 4 and produced by the vacuum refining process described herein.
FIG. 5 is a plot of the 0.2% tensile yield strength versus the Charpy impact energy at each strength level for three alloys containing 3.3% Li and other alloying elements. Alloys 5 and 6 described in Example 5 were produced by the vacuum refining process described herein while alloy 1614 was produced by a powder metallurgy process and described in U.S. Pat. No. 4,597,792 and Met. Trans. A, Vol. 19A, March 1986, pp 603-615.
FIG. 6 is a plot of the concentration of H, Cl, Rb and Cs versus refining time for alloys 1 to 6.
FIG. 7 is a plot of Na and K concentration versus refining time for alloys 1, 3, 4 and 5.
The present invention is applicable to aluminum based metallic materials containing lithium or magnesium as a primary alloying element and magnesium base of metallic materials including lithium, including both alloys and composites. The term `primary alloying element` as used herein means lithium or magnesium in amounts no less than about 0.5%, preferably no less 1.0% by weight of the alloy. These materials can have a wide range of composition and can contain in addition to lithium or magnesium any or all of the following elements: copper, magnesium or zinc as primary alloying elements. All percents (%) used herein mean weight % unless otherwise stated.
Examples of high strength composites to which the present invention is also applicable include a wide range of products wherein Al-Li, Al-Mg and Mg-Li matrices are reinforced with particles, such as whiskers or fibers, of various materials having a high strength or modulus. Examples of such reinforcing phases include boron fibers, whiskers and particles; silicon carbide whiskers and particles, carbon and graphite whiskers and particles and, aluminum oxide whiskers and particles.
Examples of metal matrix composites to which the present invention is applicable also include those made by ingot metallurgy where lithium and magnesium are important alloying elements added for any or all of the following benefits, lower density, higher stiffness or improved bonding between the matrix and the ceramic reinforcement or improved weldability. The benefits conferred by the present invention on Al-Li, Al-Mg and Mg-Li composite materials are similar to those conferred to the corresponding alloys themselves, particularly, a combination of improved properties including higher toughness and ductility. Modern commercial Al-Li and Al-Mg alloys generally have a total (AMI) content of less than about 10 ppm which is introduced as impurity in the raw materials used for making the alloys. Mg-Li alloys also have high AMI contents corresponding to the larger proportions of/lithium used therein.
Typically, a major portion of AMI contamination comes from the lithium metal which often contains about 50 to 100 ppm of both sodium and potassium. Since Al-Li alloys usually contain about 2 to 2.8% Li the amount of sodium or potassium contributed by the lithium metal is usually in the range about 1 to 2.8 ppm. Additional AMI can be introduced through chemical attack by the Al-Li on the refractories used in the melting and casting processes. Therefore a total AMI content of about 5 ppm would not be unusual in commercial Al-Li ingots and mill products. AMI exist in Al-Li alloys as grain boundary liquid phases (Webster, D. met. Trans.A, Vol. 18A, December 1987, pp. 2181-2193.) which are liquid at room temperature and can exist as liquids to at least the ternary eutectic of the Na-K-Cs system at 195� K. (-78� C.). These liquid phases promote grain boundary fracture and reduce toughness. An estimate of the loss of toughness can be obtained by testing at 195� K. or below where all the liquid phases present at room temperature have solidified. When this is done the toughness as measured by a notched Charpy impact test has been found to increase by up to four times.
The present invention exploits the fact that all the AMI have higher vapor pressures and lower boiling points than either aluminum, lithium, magnesium or the common alloying elements such as Cu,Zn,Zr,Cr,Mn and Si. This means that the AMI will be removed preferentially from alloys including these and similar elements when the alloys are maintained in the molten state under reduced pressure for a sufficient time. The first impurities to evaporate will be Rb and Cs followed by K with Na being the last to be removed. The rate of removal of the AMI from the molten Al-Li bath will depend on several factors including the pressure in the chamber, the initial impurity content, the surface area to volume ratio of the molten aluminum and the degree of stirring induced in the molten metal by the induction heating system.
In a preferred embodiment, an increase in the AMI evaporation rate may be obtained by purging the melt with an inert gas such as argon introduced into the bottom of the crucible through a refractory metal (Ti,Mo,Ta) or ceramic lance. The increase in removal rate due to the lance will depend on its design and can be expected to be higher as the bubble size is reduced and the gas flow rate is increased. The theoretical kinetics of the refining operation described above can be calculated for a given melting and refining situation using the principles of physical chemistry as for example those summarized in the Metals Handbook Vol. 15, Casting, published in 1988 by ASM International.
The refining process is preferably carried out in a vacuum induction melting furnace to obtain maximum melt purity. However, in order to incorporate this technique into commercial Al-Li, Al-Mg and Mg-Li alloy production practice, the refining operation can take place in any container placed between the initial melting furnace/crucible and the casting unit, in which molten alloys can be maintained at the required temperature under reduced pressure for a sufficient time to reduce the AMI to a level at which their influence on mechanical properties particularly toughness is significantly reduced.
The process of the present invention may be operated at any elevated temperature sufficient to melt the aluminum base metal and all of the alloying elements, but should not exceed the temperature at which desired alloy elements are boiled-off. Useful refining temperatures are in the range of about 50� to 200� C., preferably about 100� C., above the melting point of the alloy being refined. The optimum refining temperature will vary with the pressure (vacuum), size of the melt and other process variables.
The processing pressure (vacuum) employed in the process to reduce the AMI concentration to about 1 ppm or less, i.e., refining pressure, is also dependent upon process variables including the size of the melt and furnace, agitation, etc. A useful refining pressure for the equipment used in the Examples hereof was less than about 200 μm Hg.
The processing times, i.e., the period of time the melt is kept at refining temperatures, employed in the process to reduce the AMI concentration to about 1 ppm or less are dependent upon a variety of factors including the size of the furnace, and melt, melt temperature, agitation and the like. It should be understood that agitation with an inert gas as disclosed herein will significantly reduce processing times. Useful processing times for the equipment used in the Examples herein ranged from about 40 to 100 minutes.
It should be understood that the temperature, time and pressure variables for a given process are dependent upon one another to some extent, e.g., lower pressures or longer processing times may enable lower temperatures. Optimum time, temperature and pressure for a given process can be determined empirically.
The following examples are offered for purposes of illustration and are not intended to either define or limit the invention in any manner.
An A12090 alloy made by standard commercial practice was vacuum induction melted and brought to a temperature of about 768� C. under a reduced pressure of about 200 μm Hg. A titanium tube with small holes drilled in the bottom four inches of the tube was inserted into the lower portion of the molten metal bath and argon gas passed through the tube for five minutes. The gas was released well below the surface of the melt and then bubbled to the surface. The melt was then given a further refining period of about fifty minutes using only the reduced pressure of the vacuum chamber to reduce the AMI. The melt was grain refined and cast using standard procedures.
Five inch diameter billets were extruded into a flat bar 1.77 inches by 0.612 inches thick. The composition of the original melt and the vacuum remelted material are given in Table 1.
TABLE 1______________________________________CHEMIAL ANALYSES OF MATERIALBEFORE AND AFER VACUUM REFINING           Al 2090ELE-            VACUUM    ANALYSIS  ANALYSISMENT   Al 2090  REFINED   TECHNIQUE UNITS______________________________________Li      1.98    1.96      ICP       Wt. Pct.Cu     2.3      2.4       ICP       Wt. Pct.Zr      0.13    0.13      ICP       Wt. Pct.Na     3.2      N.D.      ES        PPMNa     3.1      0.480     GDMS      PPMNa     &#8800;   0.480*   SIMS      PPMK       0.600   0.050     GDMS      PPMK      &#8800;  0.008     SIMS      PPMCs     &lt;0.008   &lt;0.008    GDMS      PPMCs     &#8800;  0.015     SIMS      PPMRb      0.042   &lt;0.013    GDMS      PPMRb     &#8800;   .0005    SIMS      PPMCl     3.5      0.500     GDMS      PPMH (bulk)  1.0      0.140     LECO      PPM______________________________________ *SIMS analyses were standardized using GDMS and ES results. PPM = parts per million GDMS = glow discharge mass spectrometry SIMS = secondary ion mass spectrometry ES = emission spectrometry LECO = hydrogen analysis by LECO Corporation, 3000 Lakeview Ave. St. Joseph, Mi, 49085 USA  melting alloy under a stream of nitrogen gas and determining the hydrogen content by change in thermal conductivity. &#8800; = not determined
It can be seen that the desirable alloying element concentrations, i.e., Li, Cu and Zr, were substantially unchanged during the vacuum melting and refining process, but the undesirable impurities, Na,K,Rb,H and Cl were markedly reduced. Since Cs was already below the detection limit of GDMS before the refining process began, no change in this element could be detected.
The Charpy impact toughness values of specimens produced from flat bar extrusions of the vacuum refined A12090 and specimens produced form a commercial A12090 alloy are compared as a function of 0.2% yield strength in FIG. 1. The strength-toughness combinations for the vacuum refined alloy surpass those of the commercial alloy at all strength levels and also exceeds these property combinations of the usually superior conventional alloys, A17075 and A12024 (not shown).
An alloy containing 1.8% Li, 1.14% Cu, 0.76% Mg and 0.08% Zr, was given a vacuum refining treatment similar to that in Example 1 except that an argon lance was not used. It was then cast and extruded to flat bar and heat treated in the same manner as described in Example 1. The toughness properties (FIG. 2) again greatly exceed those of commercial Al-Li alloys at all strength levels. In many cases the toughness exceeds 100 ft. lbs. and is higher than that for most steels.
An alloy containing 2.02% Li, 1.78% Mg, and 0.08% Zr was given a vacuum refining treatment similar to that described in Example 2. It was then extruded and heat treated and its strength and toughness were evaluated and are illustrated in FIG. 3. This specimen was so tough that it could not be broken on the 128 ft. lb. Charpy testing machine capable of breaking specimens from almost all steel alloys.
An alloy containing 2.4% Li, 0.88% Mg, 0.33% Cu and 0.18% Cr was given a vacuum refining treatment similar to that in Example 2. It was then extruded and heat treated and its strength and toughness were evaluated as in previous Examples and illustrated in FIG. 4. Again strength-toughness combinations greatly superior to those of conventional alloys were obtained.
Two alloys (alloys 5 and 6) containing a higher than normal Li level (3.3% by weight) to obtain a very low density (0.088 lb/cu. in.) were given a vacuum refining treatment similar to that described in Example 2. The alloys were then cast, extruded and heat treated as in the previous examples. The strength-toughness combinations were evaluated and are shown in FIG. 5.
The high lithium level reduces the toughness compared to the alloys in Examples 1 to 4 but the properties are generally comparable to those of commercial Al-Li alloys and are superior to those of the much more expensive powder metallurgy alloys (U.S. Pat. No. 4,597,792 issued 1986 to Webster, D.) with the same lithium content as illustrated in FIG. 5. The compositions of the vacuum refined alloys described this example are:
Alloy 5.-- 3.3% Li, 1.1% Mg, 0.08% Zr
Alloy 6.-- 3.3% Li, 0.56% Mg, 0.23% Cu, 0.19% Cr
The above-described alloys 1 to 6 were analyzed for AMI concentration after refining steps of varying duration. The results of those analyses are summarized in Table II below and illustrated in FIGS. 6 and 7. It should be noted that the inert gas lance described above was only used for refining alloy 1, Example 1 which had the lowest final K and Na concentrations.
TABLE II______________________________________CHEMICAL COMPOSITION ASA FUNCTION OF REFINING TIME                      REFIN-                      INGIMPURITY CONCENTRATION (PPB)                      TIMEALLOY  Na     K       Rb    Cs   H    Cl   (Minutes)______________________________________1- start*  3100   600      42   &lt;8   1000 3500finish  480    50     &lt;13   &lt;8    140  500 552- start                         1350finish                            120      683- start  2000   1000     60    5   1420finish  545   325     &lt;8    &lt;6    70  1044 1044- start  2200   1200     72    6   1700finish  602   206     &lt;8    &lt;6    300 1540 535- start  2650   1650    100    8   2300finish  645   341     &lt;9    &lt;6    540  755 486- start                         3500finish                            420      46______________________________________ *The start values are based on data published in Webster, D. Met. Trans. A, Vol. 18A, Dec. 1987 pp 2181-2183.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS1620082 *Dec 7, 1923Mar 8, 1927Allied Process CorpAluminum alloy containing lithiumUS2253421 *Sep 18, 1939Aug 19, 1941De Mare Baltzar E LMethod and apparatus for deoxidizing and degasifying liquid steelUS2381219 *Oct 12, 1942Aug 7, 1945Aluminum Co Of AmericaAluminum alloyUS2915391 *Jan 13, 1958Dec 1, 1959Aluminum Co Of AmericaAluminum base alloyUS2960331 *Nov 29, 1956Nov 15, 1960Stauffer Chemical CoVacuum melting processUS2997760 *Jun 10, 1957Aug 29, 1961Stauffer Chemical CoContinous vaccum casting processUS3183077 *Jan 30, 1962May 11, 1965Bendix Balzers Vacuum IncProcess for vacuum degassingUS3201224 *Nov 23, 1962Aug 17, 1965Heppenstall CoMethod of making cleaner alloy steels or the likeUS3288601 *Mar 14, 1966Nov 29, 1966Flemings Merton CHigh-strength aluminum casting alloy containing copper-magnesium-silconsilverUS3306717 *Feb 14, 1964Feb 28, 1967Svenska Metallverken AbFiller metal for welding aluminumbased alloysUS3346370 *May 20, 1965Oct 10, 1967Olin MathiesonAluminum base alloyUS3501290 *Aug 29, 1966Mar 17, 1970Finkl & Sons CoMethod of treating molten metal with arc heat and vacuumUS3546348 *Apr 1, 1968Dec 8, 1970Westinghouse Electric CorpNon-consumable electrode vacuum arc furnaces for steel,zirconium,titanium and other metals and processes for working said metalsUS3563730 *Nov 5, 1968Feb 16, 1971Lithium CorpMethod of preparing alkali metal-containing alloysUS3563813 *Dec 20, 1968Feb 16, 1971Boeing CoControlling fracture toughness of high-strength stainless steelsUS3708279 *Aug 27, 1969Jan 2, 1973Westinghouse Electric CorpProcess of refining metal in a vacuum with coaxially mounted non-consumable electrodesUS3720508 *Jun 1, 1971Mar 13, 1973Olin CorpAluminum alloyUS3741827 *Feb 1, 1971Jun 26, 1973Alcan Res & DevAge hardening process and productUS3764297 *Aug 18, 1971Oct 9, 1973Airco IncMethod and apparatus for purifying metalUS3794531 *Oct 21, 1971Feb 26, 1974Fuchs O FaMethod of using a highly stable aluminum alloy in the production of recrystallization hardened productsUS3873378 *Dec 13, 1972Mar 25, 1975Boeing CoStainless steelsUS3876474 *Jul 20, 1972Apr 8, 1975British Aluminium Co LtdAluminium base alloysUS3925067 *Nov 4, 1974Dec 9, 1975AlusuisseHigh strength aluminum base casting alloys possessing improved machinabilityUS3984260 *Sep 26, 1974Oct 5, 1976British Aluminum Company, LimitedAluminium base alloysUS4033794 *Apr 14, 1975Jul 5, 1977The British Aluminum Company, LimitedSuperplastically deformable, iron, siliconUS4094705 *Mar 28, 1977Jun 13, 1978Swiss Aluminium Ltd.Aluminum alloys possessing improved resistance weldabilityUS4164434 *Nov 2, 1977Aug 14, 1979Swiss Aluminium Ltd.Containing titanium and boronUS4482376 *Oct 9, 1981Nov 13, 1984Institutul De Cercetare Stiintifica, Inginerie Tehnologica Si Proiectare Pentru Sectoare CaldeHigh temperatureUS4521284 *Oct 17, 1984Jun 4, 1985Sumitomo Light Metal Industries, Ltd.Electrolytic method of producing a high purity aluminum-lithium mother alloyUS4541862 *Nov 30, 1982Sep 17, 1985A. Finkl & Sons Co.Arc heating using alternatring currentUS4584173 *Oct 9, 1984Apr 22, 1986Alcan International LimitedHigh strength and eastly fabricatedUS4588553 *Feb 22, 1983May 13, 1986The Secretary Of State For Defence In Her Brittanic Majesty's Government Of The United Kingdom Of Great Britain And Northern IrelandFor use in aeospace airframe structuresUS4594222 *Mar 10, 1982Jun 10, 1986Inco Alloys International, Inc.Alloy of aluminum, lithium, carbon, copper and(or) magnesiumUS4597792 *Jun 10, 1985Jul 1, 1986Kaiser Aluminum & Chemical CorporationAluminum-based composite product of high strength and toughnessUS4603029 *Mar 13, 1985Jul 29, 1986The Boeing CompanyAluminum-lithium alloyUS4624717 *Mar 30, 1984Nov 25, 1986Alcan International LimitedAluminum alloy heat treatmentUS4626409 *Mar 30, 1984Dec 2, 1986Alcan International LimitedAluminium alloysUS4629505 *Apr 2, 1985Dec 16, 1986Aluminum Company Of AmericaAluminum base alloy powder metallurgy process and productUS4661172 *Feb 29, 1984Apr 28, 1987Allied CorporationWith zirconium, lithium, magnesium and others; consolidatedUS4717068 *Feb 17, 1987Jan 5, 1988Cegedur Societe De TransformationOxidation pretreatment reduces lithium content in surface zone; oxides removedUS4735773 *Dec 8, 1986Apr 5, 1988Aluminum Company Of AmericaInertial mixing method for mixing together molten metal streamsUS4735774 *Dec 30, 1983Apr 5, 1988The Boeing CompanyLightweight, high-strength; aircraftUS4747884 *Apr 3, 1985May 31, 1988Massachusetts Institute Of TechnologyHigh strength aluminum-base alloy containing lithium and zirconium and methods of preparationUS4758286 *Nov 22, 1984Jul 19, 1988Cegedur Societe De Transformation De L'aluminium PechineyHigh strength, ductilityUS4761266 *Jun 22, 1987Aug 2, 1988Kaiser Aluminum & Chemical CorporationControlled addition of lithium to molten aluminumUS4772342 *Oct 24, 1986Sep 20, 1988Bbc Brown, Boveri & Company, LimitedLightweightUS4777998 *Oct 26, 1987Oct 18, 1988Aluminium PechineyMachine for pressure casting of metal parts possibly containing fibres of ceramic materialsUS4786337 *Mar 25, 1988Nov 22, 1988Rockwell International CorporationCopper plating prior to heat treatment of alloy with subsequent removalUS4790884 *Mar 2, 1987Dec 13, 1988Aluminum Company Of AmericaAluminum-lithium flat rolled product and method of makingUS4793854 *May 20, 1987Dec 27, 1988Kabushiki Kaisha ToshibaHighly pure titanium and process for producing the sameUS4799976 *Mar 7, 1988Jan 24, 1989Cegedur Societe De Transformation De L'aluminum PechineyProcess for the heat treatment of Al alloys containing Li with a view to preserving their surface healthUS4802656 *Sep 17, 1987Feb 7, 1989Aluminium PechineyRotary blade-type apparatus for dissolving alloy elements and dispersing gas in an aluminum bathUS4808283 *Apr 5, 1988Feb 28, 1989Sumitomo Light Metal Industries, Ltd.Electrolysis of mixed molten lithium and potassium chlorides unsing hollow cylinder aluminum cathodeUS4816087 *Apr 10, 1987Mar 28, 1989Aluminum Company Of AmericaProcess for producing duplex mode recrystallized high strength aluminum-lithium alloy products with high fracture toughness and method of making the sameUS4832740 *Mar 14, 1988May 23, 1989Swiss Aluminium Ltd.Aluminum fluoride powdersUS4832911 *Sep 16, 1987May 23, 1989Alcan International LimitedMethod of alloying aluminiumUS4842822 *Dec 19, 1986Jun 27, 1989Howmet CorporationAluminum-lithium alloy and method of investment casting an aluminum-lithium alloyUS4919187 *Aug 9, 1988Apr 24, 1990Leybold Heraeus GmbhMethod for making additions to molten alloys and bodies molded from alloying metalsAU165317A * Title not availableCA863262A *Feb 9, 1971High Duty Alloys LtdAluminium alloys and articles made therefromDE3628276A1 *Aug 20, 1986Feb 25, 1988Leybold Heraeus Gmbh & Co KgVerfahren zum chargieren von zusaetzen zu legierungsschmelzen und formkoerper aus legierungszusaetzenEP0150456A2 *Dec 20, 1984Aug 7, 1985The Boeing CompanyLow temperature underaging of lithium bearing aluminum alloyEP0296073A1 *Jun 2, 1988Dec 21, 1988PechineyLarge lattice parameter metal alloyEP0377640A1 *Jul 21, 1988Jul 18, 1990Martin Marietta CorpUltra high strength weldable aluminum-lithium alloys.FR2561261A1 * Title not availableGB353891A * Title not availableGB787665A * Title not availableGB1172736A * Title not availableGB1596917A * Title not availableGB1596918A * Title not availableGB2115836A * Title not availableGB2121822A * Title not availableGB2137227A * Title not available* Cited by examinerNon-Patent CitationsReference1Bretz "Alithalite Alloys: 1987 Update", Al-Li Symposium WESTEC '87, Mar. 25-26, 1987.2 *Bretz Alithalite Alloys: 1987 Update , Al Li Symposium WESTEC 87, Mar. 25 26, 1987.3 *Development of an Experimental, Wrought Aluminum Alloy for Use at Elevated Temperature, I. J. Polmear, 1987.4 *Effect of Lithium Addition on the Elevated Temperature Properties of 2219 Alloy, Kojima et al., Journal of Japan Institute of Light Metals, vol. 23, No. 11, Nov. 1986.5 *Factors Influencing Fracture Toughness and Other Properties of Aluminum Lithium Alloys, Sanders, Jun., 1979.6Factors Influencing Fracture Toughness and Other Properties of Aluminum-Lithium Alloys, Sanders, Jun., 1979.7 *Hayashi, Aging Phenomena of Al Li Mg Alloy Affected by Additional Elements, vol. 32, No. 7, Jul. 82.8Hayashi, Aging Phenomena of Al-Li-Mg Alloy Affected by Additional Elements, vol. 32, No. 7, Jul. 82.9Howmet, "An Investment Cast Al-LI Alloy HTC 321" 3/1987.10 *Howmet, An Investment Cast Al LI Alloy HTC 321 3/1987.11 *Processing and Properties of 2091 and 8090 Forgings, D. Marchive and M. O. Charue, 4th International Aluminum Lithium Conference, 9/1987.12Starke et al., "New Approaches to Alloy Development in the Al-Li System", 8/81.13 *Starke et al., New Approaches to Alloy Development in the Al Li System , 8/81.14 *Tem Investigation of Precipitates in Al Cu Mg Ag and Al Cu Mg Alloys R. J. Chester and I. J. Polmear, 1980.15Tem Investigation of Precipitates in Al-Cu-Mg-Ag and Al-Cu-Mg Alloys R. J. Chester and I. J. Polmear, 1980.16Vasudevan, "Contribution of Na-Segregation to Fraction Behavior of Al-11.4 at % Li Alloy", 1984.17 *Vasudevan, Contribution of Na Segregation to Fraction Behavior of Al 11.4 at % Li Alloy , 1984.18Vaynblat, "Subbounday Embrittlement of the Alloy Al-Li-Mg by Horophile Impurity Sodium", 1976.19 *Vaynblat, Subbounday Embrittlement of the Alloy Al Li Mg by Horophile Impurity Sodium , 1976.20Watanabe "High Purity Al-Li Master Alloy by Molten Salt", 9/87.21 *Watanabe High Purity Al Li Master Alloy by Molten Salt , 9/87.22Webster "Factors Affecting the Tensile Strength, Elongation and Impact Resistance of Low Oxide, Isostatically Pressed Beryllium Block", 6/1976.23 *Webster and Bennett, Touth(er) Aluminum Lithium Alloys, Oct./1989.24Webster and Bennett, Touth(er) Aluminum-Lithium Alloys, Oct./1989.25 *Webster Factors Affecting the Tensile Strength, Elongation and Impact Resistance of Low Oxide, Isostatically Pressed Beryllium Block , 6/1976.26Webster, "The Effect of Low Melting Point Impurities on the Properties of Aluminum-Lithium Alloys," Metallurgical Transactions A, vol. 18A, pp. 2181-2183, Jan. 1987.27 *Webster, The Effect of Low Melting Point Impurities on the Properties of Aluminum Lithium Alloys, Metallurgical Transactions A, vol. 18A, pp. 2181 2183, Jan. 1987.28Wert, "Integranular Fracture in an Al-Li-Cu-Mg-Zr Alloy", vol. 19, 1985.29 *Wert, Integranular Fracture in an Al Li Cu Mg Zr Alloy , vol. 19, 1985.* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS5320803 *Oct 4, 1991Jun 14, 1994Comalco Aluminium LimitedProcess for making aluminum-lithium alloys of high toughness* Cited by examinerClassifications U.S. Classification420/528, 75/678, 420/533, 75/686, 420/543International ClassificationC22C21/06, C22C23/00, C22C1/02, C22C21/00, C22C1/00Cooperative ClassificationC22C21/00, C22C21/06European ClassificationC22C21/00, C22C21/06Legal EventsDateCodeEventDescriptionApr 18, 2000FPExpired due to failure to pay maintenance feeEffective date: 20000204Feb 6, 2000LAPSLapse for failure to pay maintenance feesAug 31, 1999REMIMaintenance fee reminder mailedSep 12, 1995REMIMaintenance fee reminder mailedSep 1, 1995FPAYFee paymentYear of fee payment: 4Sep 1, 1995SULPSurcharge for late paymentMay 18, 1990ASAssignmentOwner name: COMALCO ALUMINIUM LIMITED, AUSTRALIAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST.;ASSIGNOR:WEBSTER, DONALD;REEL/FRAME:005300/0848Effective date: 19900510RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services