Patent US8030420 - Olefin polymerization reaction unit and polyolefin production process - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsAn olefin polymerization reaction unit includes a multistage gas phase polymerization reactor which is divided into two or more polymerization stages, in which polyolefin particles move from an initial stage to a final stage, and in which an olefin monomer-containing gas is fed from the final stage toward...http://www.google.com/patents/US8030420?utm_source=gb-gplus-sharePatent US8030420 - Olefin polymerization reaction unit and polyolefin production processAdvanced Patent SearchTry the new Google Patents, with machine-classified Google Scholar results, and Japanese and South Korean patents.Publication numberUS8030420 B2Publication typeGrantApplication numberUS 12/332,065Publication dateOct 4, 2011Filing dateDec 10, 2008Priority dateDec 11, 2007Fee statusPaidAlso published asCN101456925A, CN101456925B, DE102008061426A1, US20090148354Publication number12332065, 332065, US 8030420 B2, US 8030420B2, US-B2-8030420, US8030420 B2, US8030420B2InventorsHiroyuki Ogawa, Hideki SatoOriginal AssigneeSumitomo Chemical Company, LimitedExport CitationBiBTeX, EndNote, RefManPatent Citations (84), Non-Patent Citations (31), Referenced by (2), Classifications (11), Legal Events (2) External Links: USPTO, USPTO Assignment, EspacenetOlefin polymerization reaction unit and polyolefin production process
US 8030420 B2Abstract
An olefin polymerization reaction unit includes a multistage gas phase polymerization reactor which is divided into two or more polymerization stages, in which polyolefin particles move from an initial stage to a final stage, and in which an olefin monomer-containing gas is fed from the final stage toward the initial stage. The reaction unit also includes first circulating means for feeding to the final stage a gas that is discharged from the initial stage and then cooled with a first heat exchanger, and second circulating means for feeding to one of the polymerization stages a condensate formed by condensing, with a second heat exchanger different from the first heat exchanger, a gas removed from one of the polymerization stages.
1. A polyolefin production process which comprises carrying out olefin polymerization using an olefin polymerization reaction unit comprising:
a multistage gas phase polymerization reactor which is divided into two or more polymerization stages, in which polyolefin particles move from an initial stage to a final stage, and in which an olefin monomer-containing gas is fed from the final stage toward the initial stage;
first circulating means for feeding to the final stage a gas, wherein the gas is discharged from the initial stage and then cooled with a first heat exchanger; and
second circulating means for feeding to one of the polymerization stages a condensate, wherein the condensate is formed by condensing, with a second heat exchanger different from the first heat exchanger, a gas removed from one of the polymerization stages,
wherein the second circulating means feeds the condensate to the polymerization stage immediately before the polymerization stage from which gas is removed.
2. The polyolefin production process of claim 1, wherein the two or more polymerization stages are arranged in a vertical direction.
3. The polyolefin production process of claim 1, wherein the second heat exchanger is situated upward from where the condensate is fed to one of the polymerization stages.
4. The polyolefin production process of claim 1, wherein a fluidized bed of the polyolefin particles is formed in each polymerization stage.
5. The polyolefin production process of claim 1, wherein a spouted bed of the polyolefin particles is formed in each polymerization stage. Description
The present invention relates to an olefin polymerization reaction unit and to a process for producing polyolefins using such an reaction unit.
Olefin polymerization may be carried out by polymerizing an olefin monomer in the presence of a catalyst and forming granular polyolefin particles. One such process that is known to the art involves carrying out polymerization using a single-stage gas phase polymerization reactor having one polymerization stage, using a single heat exchanger to cool and partially condense unreacted monomer-containing gases recovered from the polymerization reactor, and carrying out heat removal within the single-stage gas phase polymerization reactor by again feeding the gases and condensate to the polymerization reactor (see, for example, Japanese Patent Application Laid-open No. 2000-302807).
Olefin polymerization is also carried out by a process that uses a multistage gas phase polymerization reactor which is divided into two or more polymerization stages, wherein polyolefin particles move from an initial stage to a final stage and, at the same time, an olefin monomer-containing gas is fed from the final stage toward the initial stage (see, for example, U.S. Pat. No. 5,235,009 and Japanese Patent Application Laid-open No. 2003-277412). Heat of reaction removal in such a multistage gas phase polymerization reactor is generally carried out by using a heat exchanger to lower the temperature of unreacted monomer-containing gases recovered from the initial stage of the polymerization reactor, then feeding the gases again to the final stage of the polymerization reactor.
However, in such a method for removing the heat of reaction within a multistage gas phase polymerization reactor, owing to the rising gas temperature associated with heat removal, the temperature within the reactor is higher at higher stages in the reactor, which results in large differences in the reaction temperature. On the other hand, by using a heat removal method in which the heat of reaction in a multistage gas phase polymerization reactor such as that described above is removed by feeding an unreacted monomer condensate to the polymerization reactor, temperature differences between the stages can be minimized. Yet, the gases newly generated by evaporation of the condensate causes the gas flow rate to rise at successively higher stages of the reactor. As a result, the flow rate of gases that are discharged from the reactor and circulated becomes very large. High-powered equipment is thus required to circulate the gases, which increases the power costs.
It is therefore an object of the present invention to provide an olefin polymerization reaction unit that is able to cool efficiently while cutting power costs in olefin polymerization using a multistage gas phase polymerization reactor which is divided into two or more polymerization stages, in which polyolefin particles move from an initial stage to a final stage, and in which an olefin monomer-containing gas is fed from the final stage toward the initial stage. Another object of the invention is to provide a polyolefin production method which uses such an olefin polymerization reaction unit.
Accordingly, the olefin polymerization reaction unit of the invention includes a multistage gas phase polymerization reactor which is divided into two or more polymerization stages, in which polyolefin particles move from an initial stage to a final stage, and in which an olefin monomer-containing gas is fed from the final stage toward the initial stage; first circulating means for feeding to the final stage a gas that is discharged from the initial stage and then cooled with a first heat exchanger; and second circulating means for feeding to one of the polymerization stages a condensate formed by condensing, with a second heat exchanger different from the first heat exchanger, a gas removed from one of the polymerization stages.
In the olefin polymerization reaction unit of the present invention, the temperature of a portion of the unreacted monomer-containing gas recovered from the initial stage of the multistage gas phase polymerization reactor is lowered by the first heat exchanger, then again fed to the final stage of the polymerization reactor, along with which another portion of the unreacted monomer-containing gas removed from the multistage gas phase polymerization reactor is condensed by a second heat exchanger to form a liquid condensate which is then fed to the multistage gas phase polymerization reactor. Such an arrangement enables the latent heat of vaporization of the monomer component to be utilized, making it possible to carry out efficient heat removal.
Also, because condensation is carried out by a second heat exchanger which is separate and distinct from the first heat exchanger, the amount of gas supplied the first heat exchanger can be reduced. That is, the capacity of the circulating gas compressor which circulates gas in the first circulating means can be lowered, which has a significant power cost-cutting effect.
Meanwhile, the decrease in volume when the gas are condensed results in a negative pressure within the second heat exchanger, causing gases to be automatically drawn into the second heat exchanger. Moreover, the liquid (condensate) formed by condensation of the gas by the second heat exchanger can easily be fed into the polymerization reactor by, for example, the head pressure of the liquid itself; that is, without using a pump. When the head pressure is not high enough, it may be necessary to use a pump. However, even in such cases, it suffices to use the pump only to the extent of compensating for the degree of inadequacy in the head pressure. Hence, although second circulating means is provided, doing so does not raise the power costs to any significant degree. Indeed, the second circulating means has overall a high power cost-cutting effect.
In addition, in the inventive olefin polymerization reactor unit, because the second circulating means both enables gas to be removed from a desired polymerization stage and also enables condensate to be fed to a desired polymerization stage, any polymerization stage can be selectively cooled. The present invention thus has the additional effect of facilitating temperature control within the multistage gas phase polymerization reactor.
Preferably, the second circulating means feeds the condensate to the polymerization stage from which gas is removed, the polymerization stage immediately before the polymerization stage from which gas is removed, or the polymerization stage immediately after the polymerization stage from which gas is removed.
Such an arrangement makes it possible, by feeding the condensate close to the polymerization stage where gas is removed, to replenish at a nearby polymerization stage the amount of gas lost by removal. As a result, the gas flow rate at each polymerization stage within the multistage gas phase polymerization reactor can be kept substantially uniform.
The two or more polymerization stages are preferably arranged in a vertical direction. This makes it possible to reduce the footprint of the reaction unit.
It is preferable for the second heat exchanger to be situated upward from where the condensate is fed to a polymerization stage.
This arrangement readily enables the head pressure of the liquid condensed by the second heat exchanger to be increased, making it easier to supply the condensate to the reactor or to a polymerization stage.
A fluidized bed or a spouted bed of the polyolefin particles may be formed in each polymerization stage. Because multistage gas phase polymerization reactors with such constructions generally have an excellent plug flow character, polyolefin of excellent uniformity can be obtained.
The polyolefin production process of the invention carries out olefin polymerization using the above-described olefin polymerization reaction unit.
The present invention enables efficient cooling to be carried out while at the same time cutting power costs.
FIG. 1 is a schematic view of an embodiment of the olefin polymerization reaction unit according to the present invention;
FIG. 2 is an enlarged schematic cross-sectional view of the multistage gas phase polymerization reactor 10A in FIG. 1; and
FIG. 3 is a schematic view of another embodiment of the olefin polymerization reaction unit according to the invention.
Olefin Polymerization Reaction Unit
The olefin polymerization reaction unit 100A according to the present embodiment includes an olefin prepolymerization reactor 5, and a multistage gas phase polymerization reactor 10A connected subsequent to the olefin prepolymerization reactor 5.
Bulk polymerization reactors that may be used include known polymerization reactors, such as the stirred tank-type reactors and loop-type reactors described in Japanese Patent Publication No. S 41-12916, Japanese Patent Publication No. S 46-11670 and Japanese Patent Publication No. S 47-42379. Bulk polymerization is a process in which an olefin monomer such as propylene or butene is used as the polymerization solvent in the substantial absence of inert solvents such as aliphatic hydrocarbons (e.g., propane, butane, isobutane, pentane, hexane, heptane, octane) and alicyclic hydrocarbons (e.g., cyclopentane, cyclohexane), an olefin polymerization catalyst is dispersed in the polymerization solvent, and polymerization is carried out in a state where the polymer that is formed does not dissolve in the polymerization solvent. Polymerization is carried out at a temperature and pressure at which the polymerization solvent is maintained in a liquid state and the polymer that is formed does not dissolve in the polymerization solvent. The polymerization temperature is generally from 30 to 100� C., and preferably from 50 to 80� C. The polymerization pressure is generally from standard pressure to 10 MPaG, and preferably from 0.5 to 5 MPaG. Stirred tank-type gas phase polymerization reactors that may be used include known polymerization reactors, such as the reactors described in Japanese Patent Application Laid-open No. S 46-31969 and Japanese Patent Publication No. S59-21321. Stirred tank-type gas phase polymerization is a process in which a monomer in a gaseous state is used as the medium and, while maintaining an olefin polymerization catalyst and olefin polymer in a fluidized state within the medium by means of an agitator, the monomer in the gaseous state is polymerized. The polymerization temperature is generally from 50 to 110� C., and preferably from 60 to 100� C. The polymerization pressure should be in a range at which the olefin can be present as a vapor phase within the stirred tank-type gas phase polymerization reactor, and is generally from standard pressure to 5 MPaG, and preferably from 0.5 to 3 MPaG.
Combinations of different reactors are exemplified by a slurry polymerization reactor or a bulk polymerization reactor, to which is subsequently connected a fluidized bed-type gas phase polymerization reactor or a stirred tank-type gas phase polymerization reactor.
Alternatively, a flushing tank for separating unreacted olefin or polymerization solvent from olefin polymer particles may generally be provided between a slurry polymerization reactor or a bulk polymerization reactor and, subsequently connected thereto, a gas phase polymerization reactor such as a fluidized bed-type gas phase polymerization reactor, a stirred tank-type gas phase polymerization reactor or the subsequently described multistage gas phase polymerization reactor 10A. However, such a flushing tank is not always required; particularly in cases where a bulk polymerization reactor is used, a flushing tank is often not provided.
Multistage Gas Phase Polymerization Reactor
The multistage gas phase polymerization reactor 10A is a reactor which carries out, in a substantially gas phase state, an olefin polymerization reaction on polyolefin particles formed by the olefin prepolymerization reactor 5.
Referring to FIG. 1, the multistage gas phase polymerization reactor 10A is composed primarily of a cylinder 12 which extends vertically, a plurality of deflectors 20 provided inside the cylinder 12, and a plurality of tubular baffles (decreasing diameter members) 30 provided inside the cylinder 12. The deflectors 20 and tubular baffles 30 are alternately disposed in the axial direction of the cylinder 12. Also, it is preferable for both the deflectors 20 and the tubular baffles 30 to be disposed coaxially with the center axis of the cylinder 12.
In the multistage gas phase polymerization reactor 10A, five polymerization stages 25 are formed in a vertical row inside the cylinder 12. Each polymerization stage 25 is a region enclosed by the outside surface of a tubular baffle 30, the inside surface of the tubular baffle 30 directly below, and the inside surface of the portion of the cylinder 12 (cylindrical portion) between these two tubular baffles 30. The topmost polymerization stage 25 is a region enclosed by the inside surface of the cylinder 12 at the top thereof, the inside surface of the tubular baffle 30 directly below the top of the cylinder 12, and the inside surface of the portion of the cylinder 12 (cylindrical portion) therebetween.
Within each polymerization stage 25, an olefin-containing gas flows upward at a high velocity from a gas inlet orifice formed at a bottom end 30 b of the tubular baffle 30, thereby forming a spouted bed of polyolefin particles.
As shown in FIG. 2, in each polymerization stage 25, a deflector 20 is disposed at a position that lies above the tubular baffle 30 and faces the gas inlet orifice. The role of the deflector 20 is to prevent spouted polyolefin particles from scattering to higher stages. This makes it possible to shorten the freeboard zone, enabling a high volume efficiency to be achieved.
Each tubular baffle 30 is a tapered cylinder which has an inside diameter that progressively decreases in the downward direction, and has a top end 30 a that is contiguous with the inside wall of the cylinder 12. Such an arrangement allows gases to circulate upward from a circular gas inlet orifice at a bottom end 30 b of the tubular baffle 30, but does not allow the gases to circulate upward between the top end 30 a and the cylinder 12. The gas inlet orifice formed at the bottom end 30 b may have disposed thereon a check valve (not shown) so that polyolefin particles within the polymerization stage 25 do not flow downward through the gas inlet orifice at such times as startup or temporary shutdown of the olefin polymerization reactor unit 100A.
As shown in FIG. 1, four upper downcomers 35 a are provided so as to pass through each of the four upper tubular baffles 30 within the cylinder 12, and a bottom downcomer 35 b is provided in the bottommost tubular baffle 30. The upper downcomers 35 a allow polyolefin particles to fall from an upper polymerization stage 25 to a lower polymerization stage 25. The purpose of the bottom downcomer 35 b is to remove polyolefin particles from the bottommost polymerization stage and discharge the particles outside of the cylinder 12. Two valves V71 and V72 are arranged in series with the bottom downcomer 35 b. The polyolefin particles can be discharged in a subsequent step by successively opening and closing these valves V71 and V72.
To form a stable spouted bed in each polymerization stage 25, it is desirable that each tubular baffle 30 satisfy the following conditions. Namely, the ratio dA/dB between the diameter dA of the gas inlet orifice at the bottom end 30 b of the tubular baffle 30 and the inside diameter dB of the cylinder 12 is preferably 0.35 or less. By using such tubular baffles 30, a stable spouted bed having good particle circulation is easily formed in the reaction zone of each polymerization stage 25. Also, the angle of inclination α30 of the tubular baffle 30 in FIG. 2, i.e., the angle of the inside surface of the tubular baffle 30 with the horizontal, is preferably at least the angle of repose for polyolefin particles present within the cylinder 12. The angle of inclination α30 is more preferably at least the angle of repose and at least the angle at which the polyolefin particles can be completely discharged gravitationally. In this way, smooth downward movement of the polyolefin particles is achieved.
As shown in FIG. 13 an olefin monomer gas feeding nozzle 40 is provided at the bottom of the cylinder 12, and gaseous olefin monomer is fed to the bottom of the cylinder 12 by way of a line L30 and a compressor 54.
A gas discharge nozzle 61 is provided at the top of the cylinder 12. Gas which has risen up through the cylinder 12 is discharged to the exterior through a line L40, and gas-entrained particles are removed by an optionally provided cyclone 62. The gas is then successively introduced via a line L31 to a circulating gas compressor 64 and a first heat exchanger 65. After the gas introduced to the first heat exchanger 65 has been cooled to a degree that it does not condense, it is introduced via a line L35 into line L30, and thereby recycled to the bottom of the cylinder 12. In addition to the olefin monomer gas feeding nozzle 40, a discharge nozzle (not shown) which is capable of discharging polyolefin particles at the end of reactor operation may also be provided at the bottom of the cylinder 12. Also, to reduce the amount of powder remaining inside the multistage gas phase polymerization reactor 10A at the end of reactor operation, it is preferable to provide an interior member in the shape of an inverted cone (not shown) at a position which does not interfere with gas flow at the bottom of the cylinder 12.
In the present embodiment, first circulating means 90A is composed of the above-mentioned gas discharge nozzle 61, line L40, cyclone 62, line L31, circulating gas compressor 64, line L35, first heat exchanger 65, line L30 and olefin monomer gas feeding nozzle 40. If necessary, the cyclone 62 may be omitted. Also, the order in which the circulating gas compressor 64 and the first heat exchanger 65 are arranged may be reversed.
A plurality of gas discharge nozzles 60 are provided on a portion of the cylinder 12 facing the outside surface of a tubular baffle 30. Specifically, as shown in FIG. 1, gas discharge nozzles 60 are provided on a portion of the cylinder 12 facing the outside surface of the second tubular baffle 30 from the top; i.e., at the third polymerization stage from the top. The gas discharge nozzles 60 are connected via a line L41 to a condensing unit 66.
The condensing unit 66 has a second heat exchanger 66 a which condenses gases fed from the line L41, and a reservoir 66 b which holds liquid condensate. By way of illustration, the condensing unit 66 may be given a construction which is provided at the top with a second heat exchanger 66 a for condensing gases, such as a multitubular cylindrical heat exchanger, and is provided at the bottom with a reservoir 66 b for condensed liquid. Here, the olefin monomer-containing gas transferred through line L41 is fed between the second heat exchanger 66 a and the reservoir 66 b, and the gas flows toward the top of the second heat exchanger 66 a. The top of the second heat exchanger 66 a and the line L31 are connected together via a line L42. In addition, a coolant feed line L80 and a coolant discharge line L81 are connected to the second heat exchanger 66 a. The cylinder 12 also has provided thereon a liquid feeding nozzle 50 which feeds the condensate held in the reservoir 66 b from outside the cylinder 12 into a given polymerization stage 25. Specifically, as shown in FIG. 1, a liquid feeding nozzle 50 is disposed near the gas inlet orifice of the second tubular baffle 30 from the top, i.e., at the second polymerization stage from the top, so as to spray condensate (liquid olefin) toward a spout. This liquid feeding nozzle 50 is connected to the reservoir 66 b in the condensing unit 66 by a line L20, and a pump 52 for feeding the required amount of liquefied olefin monomer held in the reservoir 66 b is connected to line L20.
In this embodiment, second circulating means 90B is composed of the above-mentioned gas discharge nozzles 60, line L41, second heat exchanger 66 a, reservoir 66 b, line L20, pump 52 and liquid feeding nozzle 50. The pump 52 is not necessarily essential in cases where the head pressure of the condensate held in the reservoir 66 b is sufficiently high, i.e., the liquid level in the reservoir 66 b is at a position which is sufficiently higher than the liquid feeding nozzle 50. Accordingly, it is desirable for the second heat exchanger 66 a to be situated at a higher position than the liquid feeding nozzle 50. This allows the liquid level of the condensate in the reservoir 66 b to be set higher than the liquid feeding nozzle 50, enabling the need for or the requisite capacity of a pump 52 to be reduced.
In this second circulating means 90B, heat is removed from the gas introduced into the second heat exchanger 66 a via line L41 until some of the olefin gas condenses, and the condensate drips down and is stored inside the reservoir 66 b. The stored condensate is fed through the liquid feeding nozzle 50 into a polymerization stage 25. If necessary, gases such as hydrogen which do not condense are introduced via line L42 into the circulating gas compressor 64 together with the gas discharged by the cyclone 62. The amount of condensate that is formed in the second heat exchanger 66 a is set as the amount of condensate required to maintain a given temperature range within the cylinder 12, and the amount of gas discharged from the gas discharge nozzle 60 is regulated by the amount of heat removal in the second heat exchanger 66 a or by valves and the like to an amount suitable for generating this required condensate feed rate. In FIG. 1, the liquid feed nozzle 50 is disposed near the gas inlet orifice of the tubular baffle 30. However, the liquid feed nozzle 50 is not limited to such a position and may instead be disposed, for example, near the bottom end of a deflector 20. The liquid feed nozzle 50 is preferably provided in a region having a high gas velocity, such as a spouting area where a spout is formed.
In addition, a line L5 is connected to a position on the cylinder 12 which is higher than the topmost tubular baffle 30, and polyolefin particles containing solid particles of an olefin polymerization catalyst are fed through this line L5 to the topmost polymerization stage 25.
Accordingly, in the present embodiment, a polymerization step which uses two reactors, olefin prepolymerization reactor 5 and multistage gas phase polymerization reactor 10A, is achieved. In this way, the olefin prepolymerization reactor 5 effects the polymerization and growth of polyolefin particles, creating relatively large polyolefin particles having a particle size of preferably at least 500 μm, more preferably at least 700 μm, and even more preferably at least 850 μm, thereby enabling the formation of a more stable spouted bed. However, it is also possible to have the polymerization step be one which does not include the olefin prepolymerization reactor 5 and uses only one reactor. In this case, an olefin polymerization catalyst or prepolymerization catalyst is fed directly to the multistage gas phase polymerization reactor 10A, and olefin polymerization is carried out. Alternatively, one or more additional multistage gas phase polymerization reactor, such as an olefin prepolymerization reactor 5 or a multistage gas phase polymerization reactor 10A, may be provided subsequent to the multistage gas phase polymerization reactor 10A so as to achieve a polymerization step which uses three or more reactors.
Next, the olefin, polyolefin, catalyst and other substances used in such an olefin polymerization reaction unit are described.
In the olefin polymerization reaction unit and polyolefin production process of the invention, polyolefin—i.e., olefin polymer (olefin homopolymer, olefin copolymer)—production is carried out by the polymerization of one or more olefin (homopolymerization or copolymerization). Examples of olefins that may be used in this invention include ethylene, propylene, 1-butene, 1-pentene, 4-methyl-1-pentene, 5-methyl-1-hexene, 1-hexene, 1-heptene and 1-octene.
Olefin polymers (homopolymers, copolymers) such as propylene homopolymers, propylene/ethylene copolymers, propylene/1-butene copolymers and propylene/ethylene/1-butene copolymers may be advantageously produced in the present invention. The production of olefin polymers obtained by multistage polymerization in which the proportions of the monomer units serving as the polymer ingredients differ in the respective stages is especially preferred. For example, it is possible to form a multistage-polymerized olefin copolymer by feeding one type of olefin to an olefin prepolymerization reactor 5 and a multistage gas phase polymerization reactor 10A so as to form homopolymer particles, or copolymerizing the first olefin with a small amount of another olefin to form random copolymer particles, then feeding, in a subsequent stage, two or more types of olefin to these polymer particles in an additional olefin polymerization reactor such as an olefin prepolymerization reactor 5 or a multistage gas phase polymerization reactor 10A. This results in a narrow residence time distribution in the multistage gas phase polymerization reactor 10A, making it easy to achieve a fixed compositional ratio within the polymer particles. This approach is especially effective for reducing molding defects.
Examples of such polymers include propylene-propylene/ethylene polymers, propylene-propylene/ethylene-propylene/ethylene polymers, propylene/ethylene-propylene/ethylene polymers and propylene-propylene/ethylene/1-butene polymers. Here, a dash (“-”) indicates the boundary between polymers, and a slash (“/”) indicates that two or more olefins are copolymerized within the polymer. Of these, the production of multistage-polymerized propylene-based copolymers which are polymers having propylene-based monomer units, are called “high-impact polypropylene” (in Japan, also customarily called “polypropylene block copolymers”), and have crystalline propylene-based polymer segments and amorphous propylene-based polymer segments, is preferred. A multistage polymerized propylene-based copolymer can be prepared by the continuous multistage polymerization, in any order, of crystalline homopolypropylene segments or random copolymer segments obtained by copolymerizing a small amount of an olefin other than propylene, with amorphous rubber segments copolymerized from ethylene, propylene and, as an optional ingredient, an olefin other than ethylene and propylene, in the presence of the respective polymers. Such a copolymer has an intrinsic viscosity, as measured in 1,2,3,4-tetrahydronaphthalene at 135� C., which is preferably in a range of from 0.1 to 100 dl/g. This multistage polymerized propylene-based copolymer has excellent heat resistance, rigidity and impact resistance, and can therefore be used in automotive components such as bumpers and door trim, and in various packaging containers such as retortable food packaging containers.
An olefin-based block copolymer may be formed by a process which does not use an additional polymerization reactor, but separates the multistage gas phase polymerization reactor 10A into two regions. In this case, an olefin-based block copolymer may be advantageously created by forming homopolyolefin particles in three polymerization stages from the top of the multistage gas phase polymerization reactor 10A and feeding two or more different olefins to two bottom polymerization stages. Because the ratio of homopolyolefin particle formation is generally higher than the ratio of copolymer formation, it is preferable for the number of polymerization stages used to form the homopolyolefin particles to be higher than the number of polymerization stages used to form the copolymer. Here, one olefin polymerization reaction unit according to the invention in which a single olefin circulates is composed of the three polymerization stages from the top, and another olefin polymerization reaction unit in which a gas containing a plurality of different olefins circulates is composed of the two bottom polymerization stages.
What is commonly referred to as a titanium/magnesium composite catalyst may be used as catalyst component A employed in the preparation of a Ziegler-type solid catalyst. This composite catalyst may be obtained by contacting a titanium compound, a magnesium compound and an electron donor such as the following. Titanium compounds that may be used to prepare catalyst component A are exemplified by titanium compounds having the general formula Ti(OR1)aX4-a (where R1 is a hydrocarbon group of 1 to 20 carbons, X is a halogen atom, and the letter a is a number such that 0≦a≦4). Illustrative examples include tetrahalogenated titanium compounds such as titanium tetrachloride; trihalogenated alkoxytitanium compounds such as ethoxytitanium trichloride and butoxytitanium trichloride; dihalogenated dialkoxytitanium compounds such as diethoxytitanium dichloride and dibutoxytitanium dichloride; monohalogenated trialkoxytitanium compounds such as triethoxytitanium chloride and tributoxytitanium chloride; and tetraalkoxytitanium compounds such as tetraethoxytitanium and tetrabutoxytitanium. These titanium compounds may be used singly or as combinations of two or more thereof.
Illustrative examples of organic acid halides include mono- and polyfunctional carboxylic acid halides, such as aliphatic carboxylic acid halides, alicyclic carboxylic acid halides and aromatic carboxylic acid halides. Illustrative examples include acetyl chloride, propionyl chloride, butyryl chloride, valeroyl chloride, acryloyl chloride, methacryloyl chloride, benzoyl chloride, toluoyl chloride, anisoyl chloride, suceinyl chloride, malonyl chloride, maleyl chloride, itaconyl chloride and phthaloyl chloride. Preferred examples include aromatic carboxylic acid chlorides such as benzoyl chloride, toluoyl chloride and phthaloyl chloride. Phthaloyl chloride is especially preferred.
Catalyst component A, the organoaluminum compound component and the electron donor component may be brought into mutual contact before being fed to the multistage gas phase polymerization reactor, or may be separately fed to the multistage gas phase polymerization reactor, then contacted within the reactor. Alternatively, any two of these components may first be contacted with each other, and the remaining component subsequently brought into contact, or the respective components may be brought into mutual contact in a plurality of divided portions.
In the formula, M is a transition metal, x is a number which satisfies the atomic valence of the transition metal M, and L is a ligand attached to the transition metal. At least one occurrence of t is a ligand having a cyclopentadienyl skeleton.
Ligands L having a cyclopentadienyl skeleton are exemplified by (substituted) cyclopentadienyl groups, (substituted) indenyl groups and (substituted) fluorenyl groups. Illustrative examples include cyclopentadienyl, methylcyclopentadienyl, tert-butylcyclopentadienyl, dimethylcyclopentadienyl, tert-butylmethylcyclopentadienyl, methylisopropylcyclopentadienyl, trimethylcyclopentadienyl, tetramethylcyclopentadienyl, pentamethylcyclopentadienyl, indenyl, 4,5,6,7-tetrahydroindenyl, 2-methylindenyl, 3-methylindenyl, 4-methylindenyl, 5-methylindenyl, 6-methylindenyl, 7-methylindenyl, 2-tert-butylindenyl, 3-tert-butylindenyl, 4-tert-butylindenyl, 5-tert-butylindenyl, 6-tert-butylindenyl, 7-tert-butylindenyl, 2,3-dimethylindenyl, 4,7-dimethylindenyl, 2,4,7-trimethylindenyl, 2-methyl-4-isopropylindenyl, 4,5-benzindenyl, 2-methyl-4,5-benzindenyl, 4-phenylindenyl, 2-methyl-5-phenylindenyl, 2-methyl-4-phenylindenyl, 2-methyl-4-naphthylindenyl, fluorenyl, 2,7-dimethylfluorenyl, 2,7-di-tert-butylfluorenyl and substituted versions of the above. In cases where there are a plurality of ligands having a cyclopentadienyl skeleton, these ligands may be mutually like or unlike.
Next, the process of producing a polyolefin in such an olefin polymerization reaction unit is described.
Separately from the above, an olefin monomer gas is fed via line L30 into the multistage gas phase polymerization reactor 10A from the nozzle 40, the pressure is raised to the polymerization pressure, and the interior of the cylinder 12 is heated. The polymerization pressure, which may be any pressure within a range at which the olefin is capable of being present in the reactor as a gas phase, is generally from standard pressure to 10 MPaG, preferably from 0.2 to 8 MPaG, and more preferably from 0.5 to 5 MPaG. At a polymerization pressure below standard pressure, the productivity may decrease. On the other hand, at a reaction pressure above 10 MPaG, equipment costs for the reactor may become high. The polymerization temperature varies according to the type of monomer, the molecular weight of the product and other factors, although a temperature below the melting point of the olefin polymer, and preferably at least 10� C. lower than the melting point, is desirable. Specifically, the temperature is preferably from 0 to 120� C., more preferably from 20 to 100� C., and even more preferably from 40 to 100� C. It is preferable to carry out polymerization in an environment which is substantially free of moisture. The presence of moisture may lower the polymerization activity of the polymerization catalyst. Also, the presence of excess oxygen, carbon monoxide or carbon dioxide within the polymerization reaction system may lower the polymerization activity.
Next, polyolefin particles having a particle diameter of from about 0.5 mm to about 5.0 mm which have been obtained separately by a known method are fed to the cylinder 12 through a feed line (not shown) and line L5. The polyolefin particles fed into the cylinder 12 are most often particles which do not contain a catalyst component having a polymerization activity, although the presence within the particles of a catalyst component having a polymerization activity is acceptable.
When polyolefin particles are fed while feeding an olefin monomer gas from the nozzle 40, as shown in FIG. 2, a spouted bed of polyolefin particles is formed within the polymerization stage 25. That is, under the action of the gas from the gas inlet orifice, the particle concentration thins near the center axis of the cylinder 12 in the polymerization stage 25 and a spout is formed in which particles flow upward together with the gas. Meanwhile, an annular structure of particles falling in the manner of a moving bed under the influence of gravity is formed at the periphery thereof, giving rise to the circulatory movement of particles within the polymerization stage 25.
Once a spouted bed has been formed within each polymerization stage 25, the polyolefin particles containing a catalyst component having a polymerization activity that were formed in the olefin prepolymerization reactor 5 are fed from line L5 into the cylinder 12 at a constant rate per unit time, in addition to which recycling is carried out by the first circulating means 90A and the second circulating means 90B, thereby commencing steady-state operation of the multistage gas phase polymerization reactor 10A. As the polyolefin particles containing a catalyst component having a polymerization activity grow within each polymerization stage 25, they successively fall through the upper downcomers 35 a and into the polymerization stage 25 below, and are eventually discharged from the bottom downcomer 35 b. In cases where an olefin prepolymerization reactor 5 is not used, olefin polymerization catalyst particles having a particle size of about 10 to about 500 μm may be fed directly into the cylinder 12.
Meanwhile, part of the olefin monomer-containing gas forms a spout and sweeps past the particle bed, while the remainder of the gas diffuses into the portion of the particle bed having an annular structure. In this way, the olefin-containing gas and the polyolefin particles undergo solid-gas contact and the action of the catalyst within the polyolefin particles causes the olefin polymerization reaction to proceed, resulting in growth of the polyolefin particles.
In this formula, dP is the particle diameter, ρS is the particle density, ρG is the gas density under the pressure and temperature conditions of the polymerization stage, ρAIR is the density of air under room temperature conditions, and LS is the height of the spouted bed.
The spouted bed height LS within the polymerization stage 25 is equal to or less than the maximum spouted bed height LsMAX at which a spouted bed is capable of forming, and is not subject to any particular limitation provided it is equal to or less than the maximum spouted bed height LsMAX. Various formulas for calculating the maximum spouted bed height LsMAX have been proposed, one of which is formula (2) below.
In recycling by the first circulating means 90A, unreacted olefin monomer-containing gas is removed from the topmost stage and cooled by the heat exchanger 65 to a degree that the gas does not condense and fed to the bottommost stage of the cylinder 12. This enables the removal of heat generated by the olefin polymerization reaction.
In recycling by the second circulating means 90B, olefin monomer-containing gas is removed from the third polymerization stage from the top of the cylinder 12 and condensed by the condensing unit 66, and the condensate is fed to the second polymerization stage from above by the liquid feed nozzle 50. In this case, when liquid olefin monomer evaporates within the cylinder 12, heat can be efficiently removed from the polyolefin particles, particularly by the heat of vaporization. In this way, the temperatures in the respective polymerization stages 25 within the cylinder 12 can be kept from becoming successively higher at higher polymerization stages, thus making it possible to equalize the temperature at the different polymerization stages 25 in the cylinder 12. A plurality of the second circulating means 90B may be provided. From the standpoint of equalizing the temperature of the respective polymerization stages 25 within the cylinder 12, it is preferable for a plurality of the second circulating means 90B to be provided.
The olefin polymerization reaction unit of the present embodiment provides the advantage that, in olefin polymerization using a multistage gas phase polymerization reactor 10A, as described above, the heat of vaporization can be utilized, enabling heat removal to be efficiently carried out.
Also, because condensation is carried out by the second heat exchanger 66 a, which is separate and distinct from the first heat exchanger 65, the amount of gas fed to the first heat exchanger 65 can be reduced. That is, the capacity of the circulating gas compressor 64 which circulates gases in the first circulating means 60A can be lowered, enabling the power costs to be cut.
Also, in the second heat exchanger 66 a, because a negative pressure acts on the internal space to the decrease in volume when the gas condenses, the gas is automatically drawn into the heat exchanger 66 a from the cylinder 12 through line L41. Moreover, the liquid (condensate) resulting from gas condensation can be fed into the polymerization reactor under its own head pressure without using a pump. In cases such as when the head pressure is insufficient, it is necessary to use a pump 52. However, even in this case, the pump capacity need only be of a degree that compensates for the degree of inadequacy in the head pressure. Therefore, providing second circulating means 90B having a second heat exchanger 66 a does not raise the power costs to any great degree and has, in the overall scheme, a high power cost-cutting effect.
The second circulating means 90B, which differs from the first circulating means 90A, enables gases to be removed from a desired polymerization stage and also enables condensate to be fed to a desired polymerization stage. Accordingly, because it is able to selectively cool in particular a polymerization stage for which a decrease in temperature is desired, such as the uppermost polymerization stage or a polymerization stage near the uppermost stage, temperature control within the multistage gas phase polymerization reactor 10A is easy. A plurality of the second circulating means 90B may, of course, be provided.
Also, the second circulating means 90B feeds condensate to the next polymerization stage above the polymerization stage from which gases have been removed. By feeding condensate close to the polymerization stage from which gases have been removed, an amount of gas equal to the amount that has been removed is replenished at a nearby polymerization stage. Therefore, the gas flow rate in each polymerization stage within the multistage gas phase polymerization reactor can be kept substantially uniform, making the spouted state of the particles easy to control.
The invention is not limited to the above-described embodiment. In the foregoing embodiment, the multistage gas phase polymerization reactor 10A is one in which gas discharge nozzles 60 are provided at the third polymerization stage from the top and the liquid feeding nozzle 50 is provided at the second polymerization stage from the top. However, the gas discharge nozzles 60 and the liquid feeding nozzle 50 are not limited to these positions, and may each be independently disposed at any position. To keep the gas flow rate at each polymerization stage substantially constant, it is preferable for the gas discharge nozzles 60 to be situated at the same polymerization stage as the liquid feeding nozzle 50 or at a later polymerization stage.
Also, in the above embodiment, the multistage gas phase polymerization reactor 10A was exemplified by a multistage gas phase polymerization reactor in which five spouted beds formed in the vertical direction. However, the number of spouted beds is not limited to five, and may be any number equal to or greater than two. From the standpoint of achieving a sufficient plug flow effect, the number of spouted beds is preferably at least three, and more preferably at least six. Moreover, the plurality of spouted beds need not necessarily be formed in the vertical direction. For example, a plurality of reactors within each of which a single spouted bed is formed at the interior may be arranged in a horizontal direction and coupled in series. Also, in reactor design and the operation control method, it is preferable to design the volume of each reactor stage and control the polyolefin particle hold-up or residence time in such a way as to narrow the residence time distribution of the polyolefin particles and to make the amount of polyolefin produced at each stage (including the olefin prepolymerization reactor 5) more uniform.
In the above-described first embodiment of the invention, a reactor where a spouted bed is formed in each polymerization stage is used. However, it is possible to use instead a reactor in which a fluidized bed is formed in each polymerization stage. The multistage gas phase polymerization reactor 10B of the olefin polymerization reaction unit 100B according to the second embodiment of the invention shown in FIG. 3 is a reactor in which a fluidized bed is formed in each polymerization stage.
As shown in FIG. 3, the multistage gas phase polymerization reactor 10B is composed primarily of a cylinder 12 which extends in the vertical direction and a plurality of dispersion plates 32 provided inside the cylinder 12. The dispersion plates 32 are arranged at equal intervals in the axial direction of the cylinder 12. Aside from the dispersion plates 32, the reactor construction is the same as that of the multistage gas phase polymerization reactor 10A in the first embodiment shown in FIG. 1.
In the multistage gas phase polymerization reactor 10B, four polymerization stages 25 are formed in a row in the vertical direction within the cylinder 12. Gas discharge nozzles 60 and a liquid feeding nozzle 50 are situated at the third polymerization stage from the top. The bottom three polymerization stages 25 are each regions enclosed by the bottom surface of a dispersion plate 32, the top surface of the dispersion plate 32 directly below, and the inside surface of that portion of the cylinder 12 (cylindrical portion) located between these two dispersion plates 32. The topmost polymerization stage 25 is a region enclosed by the inside surface of the top of the cylinder 12, the upper surface of the dispersion plate 32 directly below, and the inside surface of that portion of the cylinder 12 (cylindrical portion) located therebetween.
In each polymerization stage 25, a fluidized bed of polyolefin particles is formed due to the inward and upward flow of olefin-containing gases at a high velocity from gas inlet orifices in the dispersion plate 32.
As shown in FIG. 3, downcomers 35 a are provided so as to pass through the top three dispersion plates 32 provided within the cylinder 12. The downcomers 35 a allow polyolefin particles to drop down from an upper polymerization stage 25 to a lower polymerization stage 25. A particle removing line which laterally removes polyolefin particles is provided at the bottommost polymerization stage 25. Polyolefin particles are discharged to the next step through this particle removing line.
In this embodiment, as in the earlier described embodiment, the first circulating means 90A and the second circulating means 90B are able to reduce power costs and achieve desirable effects such as efficient heat removal from the polyolefin particles by a latent heat of vaporization.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS2477454Sep 15, 1944Jul 26, 1949Dorr CoProcess of reducing ferric oxide to ferrosoferric oxideUS2867506 *Jul 18, 1956Jan 6, 1959Dorr Oliver IncProducing sulphur dioxide gasUS2890106Aug 30, 1955Jun 9, 1959Dorr Oliver IncApparatus for heat treating fluidized solidsUS2936303 *Apr 25, 1958May 10, 1960Phillips Petroleum CoOlefin polymerizationUS3079222Nov 9, 1959Feb 26, 1963United Steel Companies LtdFluidised bed process and apparatus for use thereinUS3242586Aug 27, 1962Mar 29, 1966Canada Nat Res CouncilMultiple spouted bedUS3262922Feb 8, 1963Jul 26, 1966Phillips Petroleum CoPolymerization processUS3495952Oct 4, 1967Feb 17, 1970Ceskoslovenska Akademie VedArrangements for continuous contactingUS3644583Apr 23, 1969Feb 22, 1972Phillips Petroleum CoProduction and recovery of a solid mixed homo- and copolymerUS3652527Oct 27, 1969Mar 28, 1972Basf AgPolymerization of propylene with ziegler catalysts in a stirred ga phase reactorUS3719029Mar 23, 1971Mar 6, 1973Ube IndustriesProcess for treating gaseous products obtained by thermal cracking of hydrocarbonsUS3770714 *May 22, 1968Nov 6, 1973Metallurg AgPolymerization of olefinsUS3776979 *Nov 5, 1971Dec 4, 1973Gulf Research Development CoOlefin block copolymer fluidized-bed polymerization processUS3957448Dec 16, 1974May 18, 1976Standard Oil CompanyDivided horizontal reactor for the vapor phase polymerization of monomers at different hydrogen levelsUS3971768Dec 16, 1974Jul 27, 1976Standard Oil Company (Indiana)Vapor phase reactor off-gas recycle system for use in the vapor state polymerization of monomersUS4129701Dec 19, 1975Dec 12, 1978Standard Oil Company (Indiana)Horizontal reactor for the vapor phase polymerization of monomersUS4337722Dec 1, 1980Jul 6, 1982Societe Chimique Des CharbonnagesApparatus for granulating and/or coating particles in a spouted bedUS4373272Sep 25, 1980Feb 15, 1983General Electric CompanySystem for controlling spouted bed inlet conditionsUS4404083Aug 17, 1981Sep 13, 1983Standard Oil Company(Indiana)Fluid bed retorting process and systemUS4419330Nov 9, 1981Dec 6, 1983Ebara CorporationThermal reactor of fluidizing bed typeUS4441822May 10, 1982Apr 10, 1984Foster Wheeler Energy CorporationApparatus for mixing and distributing solid particulate materialUS4457896Aug 2, 1982Jul 3, 1984Institute Of Gas TechnologyApparatus and process for fluidized solids systemsUS4466082Feb 2, 1982Aug 14, 1984Foster Wheeler Energy CorporationApparatus for mixing and distributing solid particulate materialUS4518750Mar 9, 1983May 21, 1985Montedison S.P.A.Fluid bed reactorUS4533367 *Jul 8, 1982Aug 6, 1985Dzemal HadzismajlovicGas scrubbing method using gas liquid contact in a particulate bedUS4640339Jan 15, 1986Feb 3, 1987Esmil B.V.Apparatus for carrying out physical and/or chemical processes, more specifically a heat exchanger of the continuous typeUS4744413Sep 28, 1987May 17, 1988Eskla B.V.Apparatus for carrying out physical and/or chemical processes, in particular a heat exchangerUS5034195 *Nov 18, 1988Jul 23, 1991Brown & Root Usa, Inc.Apparatus for gas phase polymerization of olefins in vertically stacked reactorsUS5213768Apr 7, 1992May 25, 1993Bp Chemicals Ltd.Fluidized bed apparatus and process for feeding gas to a fluidized bed apparatusUS5235009Oct 16, 1989Aug 10, 1993Phillips Petroleum CompanyGas phase polymerization in multi-stage fluid bedsUS5245093 *Jan 26, 1989Sep 14, 1993Abb Lummus Crest Inc.Reaction processes in a multi-stage fluidized bedUS5536378 *Sep 20, 1994Jul 16, 1996Carbotek Inc.Apparatus for manufacture of oxygen from lunar ilmeniteUS5674308Sep 13, 1995Oct 7, 1997Midrex International B.V. Rotterdam, Zurich BranchSpouted bed circulating fluidized bed direct reduction system and methodUS5676201Apr 19, 1994Oct 14, 1997Bronswerk Heat Transfer B.V.Apparatus for carrying out a physical and/or chemical process, such as a heat exchangerUS6066701Oct 29, 1997May 23, 2000Exxon Chemical Patents Inc.Multistage method for manufacturing polyolefinsUS6306981Apr 2, 1999Oct 23, 2001Union Carbide Chemicals & Plastics Technology CorporationGas phase polymerization processUS6441108Sep 26, 1998Aug 27, 2002Bayer AktiengesellschaftGas-phase polymerization in a bell-shaped reactorUS6444763Mar 2, 2000Sep 3, 2002Mitsubishi Chemical CorporationPolymerization of olefinsUS6518372Feb 16, 2000Feb 11, 2003Basell Polyolefine GmbhMethod and apparatus for gas phase polymerization of α-olefinsUS6689845Jul 3, 1999Feb 10, 2004Basell Poliolefine Italia S.P.A.Process and apparatus for the gas-phase polymerizationUS7601303May 4, 1999Oct 13, 2009Elenac GmbhGaseous phase fluidized-bed reactorUS20060058474Sep 25, 2003Mar 16, 2006Basell Poliolefine Italia S.P.A.Polymerization processUS20060063896Aug 26, 2005Mar 23, 2006Mcelvain Robert REnergy efficient polyolefin processUS20070217966Mar 15, 2005Sep 20, 2007Timo HeinoMethod and Apparatus for Producing PolymersUS20090149610Dec 10, 2008Jun 11, 2009Sumitomo Chemocal Company, LimitedOlefin polymerization reactor, polyolefin production system, and polyolefin production processUS20090149620Dec 10, 2008Jun 11, 2009Sumitomo Chemical Company, LimitedSpouted bed device and polyolefin production process using the sameUS20100069581Dec 10, 2008Mar 18, 2010Sumitomo Chemical Company, LimitedSpouted bed device, polyolefin production system with spouted bed device, and polyolefin production processUS20100311923Dec 9, 2010Sumitomo Chemical Company, LimitedSpouted-fluidized bed-type olefin polymerization reactorCA739660AAug 2, 1966Ca Nat Research CouncilMultiple spouted bedEP0088638A2Mar 9, 1983Sep 14, 1983Montedison S.p.A.Distributor for a fluidized bed reactorEP0101893A2Jul 21, 1983Mar 7, 1984BASF AktiengesellschaftApparatus for the transformation of gases with gases or solids into temperature-sensitive solids in a fluidized bedEP0241947A2Mar 23, 1983Oct 21, 1987Union Carbide CorporationA method for controlling the temperature of a fluidized bed especially a process for producing polymersEP0381364A1Jan 24, 1990Aug 8, 1990BP Chemicals LimitedProcess and apparatus for gas phase polymerisation of olefins in a fluidized bed reactorEP1464343A1Mar 18, 2003Oct 6, 2004Ion Beam ApplicationsApparatus and process for irradiating product palletsGB845655A Title not availableGB954078A Title not availableGB1147273A Title not availableGB1233106A Title not availableGB1351624A Title not availableGB1587891A Title not availableGB2077628A Title not availableJP2675919B2 Title not availableJP3352059B2 Title not availableJP41012916A Title not availableJP46011670A Title not availableJP46031969A Title not availableJP2000302807A Title not availableJP2002515516A Title not availableJP2002520426A Title not availableJP2002537420A Title not availableJP2003277412A Title not availableJP2006502263A Title not availableJPH0676239B2 Title not availableJPH02233708A Title not availableJPS4742379A Title not availableJPS5921321A Title not availableJPS5942039A Title not availableJPS58201802A Title not availableJPS58216735A Title not availableJPS59126406A Title not availableWO1993024533A1May 27, 1993Dec 9, 1993Amoco CorporationPolymerization of alpha-olefinsWO1999059712A1May 4, 1999Nov 25, 1999Elenac GmbhGaseous phase fluidized-bed reactorWO2002040547A1Nov 14, 2000May 23, 2002Dsm N.V.Fluidised bed reactorWO2007071527A1Nov 27, 2006Jun 28, 2007Basell Poliolefine Italia S.R.L.Gas-phase process and apparatus for the polymerization of olefins* Cited by examinerNon-Patent CitationsReference1"Terminology Dictionary of Powder Technology, 2nd Edition", Editor Society of Power Technology, Nikkan Kogyo Shimbun-sha, 2000, p. 321.2Hatate et al. "Flow Characteristics of Draft Tube Spouted Bed and its Application", Journal of the Society of Powder Technology, vol. 34, No. 5, May 1997, pp. 343-360.3Hattori et al., "Minimum spoutable gas flow rate in side-outlet spouted bed with inner draft-tube," Journal of Chemical Engineering of Japan, vol. 14, No. 6, Apr. 3, 1981, pp. 462-466.4Ishikura et al., "Hydrodynamics of a Spouted Bed with a Porous Draft Tube", Kagaku Kougaku Ronbunshu, vol. 22, No. 3, 1996, pp. 615-621.5Ishikura et al., "Hydrodynamics of Modified Spouted Beds for Binary Mixtures of Particles-Effect of the Aeration Gas Flow Rate from Side Distributor", Fukuoka University Journal of Engineering, No. 58, Mar. 1997, pp. 155-165.6Ishikura et al., "Hydrodynamics of Modified Spouted Beds for Binary Mixtures of Particles—Effect of the Aeration Gas Flow Rate from Side Distributor", Fukuoka University Journal of Engineering, No. 58, Mar. 1997, pp. 155-165.7Ishikura, "Regime Map of Binary Particle Mixture in a Spout-Fluid Bed," Kagaku Kougaku Ronbunshu, vol. 19, No. 6, 1993, pp. 1189-1192.8Mathur et al., "Spouted Beds", Academic Press, 1974, pp. 114-116 and 279-280.9Notice of Allowance dated Apr. 18, 2011 for U.S. Appl. No. 12/332,102.10Notice of Allowance dated Apr. 21, 2011 for U.S. Appl. No. 12/331,730.11Notice of Allowance issued Mar. 18, 2011, in copending U.S. Appl. No. 12/332,112.12Office Action in U.S. Appl. No. 12/332,112 mailed Jun. 3, 2010.13Office Action issued Mar. 11, 2011, in copending U.S. Appl. No. 12/331,730.14Office Action issued Mar. 16, 2011, in copending U.S. Appl. No. 12/332,102.15Office Action issued May 26, 2011, in copending U.S. Appl. No. 12/332,112.16Office Action issued Nov. 12, 2010, in copending U.S. Appl. No. 12/332,112.17Perry et al., "Solids-Drying Equipment", Perry's Chemical Engineers' Handbook, McGraw-Hill, 1997, pp. 12-75 and 12-76.18Search Reoprt issued Jun. 30, 2011, in Singapore Patent Application No. 201008798-9.19Search Report dated Apr. 22, 2009 for Singapore Application No. 200809160-5.20Search Report from Singapore Application No. 200809157-1 dated Jun. 4, 2009.21Search Report from Singapore Application No. 200809158-9 dated Jun. 4, 2009.22Search Report from Singapore Application No. 200809159-7 dated Jun. 4, 2009.23Search Report from Singapore Application No. 200809160-5 dated May 26, 2009.24Search Report from Singapore Application No. 200809161-3 dated Jun. 4, 2009.25Singapore Search Report issued Nov. 10, 2010, in Singapore Patent Application No. 201004966-6.26Takeda et al., "Modified types of Spouted bed-With the gas outlet located in the side wall surrouding the annular dense bed," Kagaku Kogaku Ronbunshu 1, Kagaku Kogaku Kyokai, No. 2, 1975, pp. 149-154.27Takeda et al., "Modified types of Spouted bed—With the gas outlet located in the side wall surrouding the annular dense bed," Kagaku Kogaku Ronbunshu 1, Kagaku Kogaku Kyokai, No. 2, 1975, pp. 149-154.28Takenaka et al., "Fluidity characteristics of a spouted bed with a cylinder to cone-shaped perforated draft tubes," SCEJ 71st Annual Meeting, J123, 2006, 1 page.29U.S. Office Action dated Jun. 15, 2010 for related U.S. Appl. No. 12/332,055.30Weickert et al., "New Reactor Concepts for the Gas-Phase Polymerization of Olefins," Chemie Ingenieur Technik, vol. 77, No. 8, 2005, pp. 977-978.31Yokokawa, "Fluidizing characteristics of fluidized bed and spouted bed, and their application", Journal of the Society of Powder Technology, vol. 21, No. 11, Nov. 1984, pp. 715-723.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS9278314Sep 19, 2013Mar 8, 2016ADA-ES, Inc.Method and system to reclaim functional sites on a sorbent contaminated by heat stable saltsUS9352270Apr 11, 2012May 31, 2016ADA-ES, Inc.Fluidized bed and method and system for gas component captureClassifications U.S. Classification526/65, 422/144, 208/49, 422/139, 422/145, 422/134, 422/132International ClassificationC10B57/02, C08F2/00Cooperative ClassificationC08F10/00European ClassificationC08F10/00Legal EventsDateCodeEventDescriptionFeb 18, 2009ASAssignmentOwner name: SUMITOMO CHEMICAL COMPANY, LIMITED, JAPANFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:OGAWA, HIROYUKI;SATO, HIDEKI;REEL/FRAME:022274/0460Effective date: 20081209Mar 18, 2015FPAYFee paymentYear of fee payment: 4RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services