Patent US7653439 - Electrode structure and methods for making and using same - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign in<nobr>Advanced Patent Search</nobr>PatentsAn electrode structure made of noble metal or a noble metal alloy having a thickness of ≦100 μm is provided for implants. The electrode structure has an electrode core made of gold, silver, copper, or an alloy of at least two of these elements, and the electrode core is completely encased by a first...http://www.google.com/patents/US7653439?utm_source=gb-gplus-sharePatent US7653439 - Electrode structure and methods for making and using sameAdvanced Patent SearchPublication numberUS7653439 B2Publication typeGrantApplication numberUS 11/015,629Publication dateJan 26, 2010Filing dateDec 17, 2004Priority dateDec 19, 2003Fee statusPaidAlso published asCA2488075A1, DE10360624A1, DE10360624B4, DE502004010033D1, EP1543863A1, EP1543863B1, US20050154436Publication number015629, 11015629, US 7653439 B2, US 7653439B2, US-B2-7653439, US7653439 B2, US7653439B2InventorsHeiko Specht, Frank Kr�gerOriginal AssigneeW.C. Heraeus GmbhExport CitationBiBTeX, EndNote, RefManPatent Citations (14), Referenced by (1), Classifications (15), Legal Events (4) External Links: USPTO, USPTO Assignment, EspacenetElectrode structure and methods for making and using sameUS 7653439 B2Abstract An electrode structure made of noble metal or a noble metal alloy having a thickness of ≦100 μm is provided for implants. The electrode structure has an electrode core made of gold, silver, copper, or an alloy of at least two of these elements, and the electrode core is completely encased by a first coating, which is formed from platinum, iridium, or ruthenium.
1. A method for producing an electrode structure (10) for implants, comprising a noble metal or a noble metal alloy having a thickness of ≦100 μm, wherein the electrode structure (10) has an electrode core (12) comprising an element selected from the group consisting of gold, silver, copper, and alloys of at least two of these elements, and wherein the electrode core (12) has a thickness in a range of about 5 μm to 99.8 μm and is encased completely by a first coating (13; 13 a, 13 b) comprising at least one element selected from the group consisting of platinum, iridium, and ruthenium, the method comprising:
a) coating an electrically insulating surface (14 a) of a substrate (14) with a metal layer (15), then coating the metal layer (15) with a photoresist (16), and structuring the photoresist (16),
b) galvanically generating a first part (13 a) of the first coating on regions of the metal layer (15) exposed by the structured photoresist,
c) galvanically forming the electrode core (12) on the first part (13 a) of the first coating,
d) then removing the structured photoresist (16) from the metal layer (15),
e) removing the metal layer (15) from the electrically insulating surface (14 a) of the substrate (14) in regions not covered by the first part (13 a) of the first coating,
f) galvanically coating part of the electrode core (12) still free up to now from the first coating with a second part (13 b) of the first coating,
g) detaching the electrode structure (10) including the metal layer (15) from the electrically insulating surface (14 a) of the substrate (14), and
h) then removing the metal layer (15) from the electrode structure (10).
2. The method according to claim 1, wherein the electrically insulating surface (14 a) of the substrate (14) comprises glass or plastic.
3. The method according to claim 1, wherein the metal layer (15) comprises copper or gold.
4. A method for producing an electrode structure (10) for implants, comprising a noble metal or a noble metal alloy having a thickness of ≦100 μm, wherein the electrode structure (10) has an electrode core (12) comprising an element selected from the group consisting of gold, silver, copper, and alloys of at least two of these elements, and wherein the electrode core (12) has a thickness in a range of about 5 μm to 99.8 μm and is encased completely by a first coating (13; 13 a, 13 b) comprising at least one element selected from the group consisting of platinum, iridium, and ruthenium, the method comprising:
a) providing an electrically insulating surface (14 a) of a substrate (14) with a mask, and forming a metal layer (15) by cathode sputtering or vapor deposition on regions of the electrically insulating surface (14 a) not covered with the mask,
b) generating a first part (13 a) of the first coating by cathode sputtering or vapor deposition on the metal layer (15),
c) then forming the electrode core (12) by cathode sputtering or vapor deposition on the first part (13 a) of the first coating,
d) then removing the mask,
e) galvanically coating at least part of the electrode core (12) still free up to now from the first coating (3 a, 3 b) with a second part (13 b) of the first coating, and
f) then detaching the electrode structure (10) from the electrically insulating surface (14 a) of the substrate (14) such that the metal layer (15) is removed.
5. The method according to claim 4, wherein the electrically insulating surface (14 a) of the substrate (14) comprises glass or plastic.
6. The method according to claim 4, wherein the metal layer (15) comprises copper or gold.
7. A method for producing an electrode structure (10) for implants, comprising a noble metal or a noble metal alloy having a thickness of ≦100 μm, wherein the electrode structure (10) has an electrode core (12) comprising an element selected from the group consisting of gold, silver, copper, and alloys of at least two of these elements, and wherein the electrode core (12) has a thickness in a range of about 5 μm to 99.8 μm and is encased completely by a first coating (13; 13 a, 13 b) comprising at least one element selected from the group consisting of platinum, iridium, and ruthenium, the method comprising:
a) coating an electrically insulating surface (14 a) of a substrate (14) with a structured metal layer, which forms a first part (13 a) of the first coating,
b) providing the first part (13 a) of the first coating with a mask, and forming the electrode core (12) by cathode sputtering or vapor deposition only on the first part (13 a) of the first coating,
c) then galvanically coating part of the electrode core (12) still free up to now from the first coating (3 a) with a second part (13 b) of the first coating, and
d) then detaching the electrode structure (10) from the electrically insulating surface (14 a) of the substrate (14).
8. The method according to claim 7, wherein the electrically insulating surface (14 a) of the substrate (14) comprises glass or plastic.
9. An electrode structure (10) for implants, comprising a noble metal or a noble metal alloy having a thickness of ≦100 μm, wherein the electrode structure (10) has an electrode core (12) comprising an element selected from the group consisting of gold, silver, copper, and alloys of at least two of these elements, wherein the electrode core (12) has a thickness in a range of about 5 μm to 99.8 μm and is encased completely by a first coating (13; 13 a, 13 b) comprising at least one element selected from the group consisting of platinum, iridium, and ruthenium, and wherein the electrode structure is in a form selected from the group consisting of stimulation electrodes, cochlear electrodes, and retinal electrodes. Description
BACKGROUND OF THE INVENTION The invention relates to an electrode structure made of a noble metal or a noble metal alloy having a thickness of ≦100 μm for implants, as well as to three methods for its production. The invention further relates to the use of such an electrode structure.
Electrode arrangements made of noble metal are known, for example, from International patent application publication WO 02/089907 A1. There, electrode structures are formed from platinum film and are fixed on a carrier made of plastic material. Such electrode arrangements are used, for example, for cochlear implants.
U.S. Pat. No. 6,266,568 B1 discloses an expandable cochlear electrode arrangement and a method for its production. There, a plurality of electrode contacts spaced from each other are arranged on a flexible carrier.
German published patent application DE-OS 35 07 623 A1 discloses a long-term implantable sheet electrode having a physiologically inert matrix made of flexible plastic, which is coated with an electrical conductor, for example made of platinum. The coating is there formed galvanically or by vapor deposition.
It is now an object of the invention to make available another electrode structure for implants, which can be produced simply and economically. Furthermore, suitable methods for its production, as well as its use, should be provided.
BRIEF SUMMARY OF THE INVENTION The object is achieved for the electrode structure in that this structure has an electrode core made of gold, silver, copper, or an alloy of at least two of these elements, and that the electrode core is completely encased by a first coating, which is formed from platinum, iridium, or ruthenium.
Such an electrode structure is economical, because it has a ductile electrode core with good conductivity made of a more economical material, which is merely encased by a thin, more expensive coating, which is corrosion-resistant and biocompatible. Optionally, an alloy formation can be carried out between the electrode core and the first coating by a heating process.
It has proven effective if the electrode core has a thickness in a range of about 5 μm to 99.8 μm. For the first coating, a thickness in a range of about 100 nm to about 5 μm has proven effective. Forming the electrode structure with a thickness in a range of about 7 μm to about 30 μm is particularly preferred.
Preferably, a second coating, which is different from the first coating and which is made of ruthenium, ruthenium oxide, iridium, iridium oxide, platinum, or titanium nitride, is formed on the side of the first coating facing away from the electrode core. Here, it has proven effective if the second coating only covers parts of the first coating.
The object is further realized in a first method, wherein:
a) an electrically insulating surface of a substrate is coated with a metal layer, the metal layer is then coated with photoresist, and the photoresist is structured, b) a first part of the first coating is electroplated on the now exposed regions of the metal layer, c) the electrode core is electroplated on the first part of the first coating, d) the structured photoresist is then removed from the metal layer, e) the metal layer is removed from the electrically insulating surface of the substrate in the regions which are not covered by the first part of the first coating, f) the part of the electrode core still free up to now from the first coating is electroplated with a second part of the first coating, g) the electrode structure including the metal layer is detached from the electrically insulating surface of the substrate, and h) the metal layer is then removed from the electrode structure. The object is further realized in a second method, wherein:
a) an electrically insulating surface of a substrate is provided with a mask and a metal layer is formed by cathode sputtering or vapor deposition on the regions of the electrically insulating surface not covered with the mask, b) a first part of the first coating is generated on the metal layer by cathode sputtering or vapor deposition, c) the electrode core is then formed by cathode sputtering or vapor deposition on the first part of the first coating, d) the mask is then removed, e) at least the part of the electrode core still free up to now from the first coating is electroplated with a second part of the first coating and, f) the electrode structure is then detached from the electrically insulating surface of the substrate, in which the metal layer is removed. The object is further realized in a third method, wherein:
a) an electrically insulating surface of a substrate is coated with a structured metal layer, which forms a first part of the first coating, b) the first part of the first coating is provided with a mask, and the electrode core is formed only on the first part of the first coating by cathode sputtering or vapor deposition, c) the part of the electrode core still free up to now from the first coating is then electroplated with a second part of the first coating, and d) the electrode structure is then detached from the electrically insulating surface of the substrate. Such methods are excellently suited to economical and fast production of the electrode structure according to the invention.
In this way, the electrode core can be encased with several different coatings. To form a second coating on the first coating, for example with the third method, the electrically insulating surface of a substrate must then be coated with a structured metal layer, which forms a first part of the second coating, and then the first part of the first coating is formed thereon. After forming the electrode core and the second part of the first coating, a second part of the second coating is finally formed. Corresponding masks are used accordingly.
Here, it has proven effective, for the three methods according to the invention, to form the electrically insulating surface of the substrate from glass or plastic. A suitable metal layer can be formed preferably from copper or gold.
Use of the electrode structure according to the invention for a stimulation electrode, cochlear electrode, or retinal electrode is ideal.
FIG. 1 is a schematic diagram in plan view of several electrode structures with electrical supply lines,
FIG. 1 a is a schematic diagram in sectional view 1 a-1 a of the electrode structures from FIG. 1,
FIGS. 2 a to 2 d illustrate schematically steps of the third method for producing an electrode structure according to the invention, and
FIGS. 3 a to 3 h illustrate schematically steps of the first method for producing an electrode structure according to the invention.
DETAILED DESCRIPTION OF THE INVENTION FIG. 1 shows several electrode structures 10, here in an arbitrarily selected arrangement relative to each other. Each electrode structure 10 is connected to an electrical line 11. However, obviously any other arrangement can also be selected.
FIG. 1 a shows the section 1 a-1 a from FIG. 1. Here, it can be seen that an electrode structure 10 is constructed of an electrode core 12 and a first coating 13, which completely surrounds the electrode core 12.
FIGS. 2 a-2 d show the sequence of a third method according to the invention for producing an electrode structure 10 according to the invention. In FIG. 2 a, a first part 13 a of a first coating made of iridium is vapor deposited on an electrically insulating surface 14 a of a substrate 14. FIG. 2 b illustrates that an electrode core 12 made of gold is vapor deposited on the first part 13 a of the first coating. FIG. 2 c shows that a second part 13 b of the first coating made of iridium is galvanically deposited onto the electrode core 12. FIG. 2 d shows finally the completed electrode structure 10 detached from the substrate 14. The masks necessary for vapor deposition of the first part 13 a of the first coating and the electrode core 12, which cover the regions of the substrate 14 lying next to these parts, are not shown.
FIGS. 3 a-3 h show the sequence of a first method according to the invention for producing an electrode structure 10 according to the invention. In FIG. 3 a, an electrically insulating surface 14 a made of glass for a substrate 14 is coated with a metal layer 15 made of copper and a photoresist 16. The photoresist 16 is structured such that the metal layer 15 is partially exposed via openings 16 a in the photoresist 16 (see FIG. 3 b). In the opening 16 a, a first part 13 a of a first coating made of platinum is then galvanically deposited (see FIG. 3 c). FIG. 3 d illustrates that an electrode core 12 made of copper is then galvanically deposited on the first part 13 a of the first coating. FIG. 3 e shows that the photoresist 16 and also the resulting exposed parts of the metal layer 15 are now removed. Then, a second part 13 b of the first coating made of platinum is galvanically generated (see FIG. 3 f). After removing the substrate 14, a part of the metal layer 15 (see FIG. 3 g), which is yet to be removed, still remains on the electrode structure. FIG. 3 h shows finally the completed electrode structure 10 having the electrode core 12 and a first coating 13 a, 13 b. It will be appreciated by those skilled in the art that changes could be made to the embodiments described above without departing from the broad inventive concept thereof. It is understood, therefore, that this invention is not limited to the particular embodiments disclosed, but it is intended to cover modifications within the spirit and scope of the present invention as defined by the appended claims.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS5178957Jul 2, 1991Jan 12, 1993Minnesota Mining And Manufacturing CompanyNoble metal-polymer composites and flexible thin-film conductors prepared therefromUS5324322Apr 20, 1992Jun 28, 1994Case Western Reserve UniversityThin film implantable electrode and method of manufactureUS5683443Feb 7, 1995Nov 4, 1997Intermedics, Inc.Implantable stimulation electrodes with non-native metal oxide coating mixturesUS5720099May 1, 1996Feb 24, 1998Cochlear LimitedThin film fabrication technique for implantable electrodesUS6266568Apr 27, 1999Jul 24, 2001Advanced Bionics CorporationInflatable cochlear electrode array and method of making sameUS6374143Aug 18, 1999Apr 16, 2002Epic Biosonics, Inc.Modiolar hugging electrode arrayUS7051419 *Aug 28, 2003May 30, 2006Micronet Medical, Inc.Neurostimulating leadUS20010029366 *May 29, 2001Oct 11, 2001Swanson David K.Composite structures and methods for ablating tissue to form complex lesion patterns in the treatment of cardiac conditions and the likeUS20030036790Aug 17, 2001Feb 20, 2003Corbett Scott S.High contact density planar electrode arrayUS20030195601May 1, 2002Oct 16, 2003Andy HungHigh-density array of micro-machined electrodes for neural stimulationUS20040127966 *Dec 12, 2003Jul 1, 2004W.C. Heraeus Gmbh & Co. KgStimulation electrode and methods of making and using sameDE3507623A1Mar 5, 1985Sep 11, 1986Matthias LohrPlanar electrode which can be implanted long term in order to dissipate and induce electric currents and potentials on moving and stationary organsWO2002087685A2May 1, 2002Nov 7, 2002Second Sight LlcHigh-density array of micro-machined electrodes for neural stimulationWO2002089907A1May 7, 2002Nov 14, 2002Cochlear LtdProcess for manufacturing electrically conductive components* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS8298608Sep 28, 2010Oct 30, 2012Heraeus Precious Metals Gmbh & Co. KgMethod for producing a stimulation electrodeClassifications U.S. Classification607/116, 428/35.8, 427/2.24, 600/377, 600/386, 428/35.7, 427/2.1, 607/118, 600/373International ClassificationA61N1/05, A61N1/04Cooperative ClassificationA61N1/0541, A61N1/0543European ClassificationA61N1/05K2, A61N1/05K3Legal EventsDateCodeEventDescriptionMay 21, 2014ASAssignmentOwner name: HERAEUS PRECIOUS METALS GMBH & CO. KG, GERMANYEffective date: 20110801Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:W.C. HERAEUS GMBH & CO. KG;REEL/FRAME:032973/0477Mar 7, 2013FPAYFee paymentYear of fee payment: 4Nov 23, 2010CCCertificate of correctionMar 21, 2005ASAssignmentOwner name: W.C. HERAEUS GMBH, GERMANYFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SPECHT, HEIKO;KRUGER, FRANK;REEL/FRAME:015798/0792Effective date: 20041210RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services©2012 Google