Patent US7558100 - Phase change memory devices including memory cells having different phase ... - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsA phase change memory device may include an integrated circuit substrate and first and second phase change memory elements on the integrated circuit substrate. The first phase change memory element may include a first phase change material having a first crystallization temperature. The second phase...http://www.google.com/patents/US7558100?utm_source=gb-gplus-sharePatent US7558100 - Phase change memory devices including memory cells having different phase change materials and related methods and systemsAdvanced Patent SearchPublication numberUS7558100 B2Publication typeGrantApplication numberUS 11/881,062Publication dateJul 7, 2009Priority dateSep 20, 2006Fee statusPaidAlso published asCN101150138A, EP1903625A2, US20080068879Publication number11881062, 881062, US 7558100 B2, US 7558100B2, US-B2-7558100, US7558100 B2, US7558100B2InventorsDong-ho Ahn, Hideki Horii, Jun-Soo BaeOriginal AssigneeSamsung Electronics Co., Ltd.Export CitationBiBTeX, EndNote, RefManPatent Citations (72), Non-Patent Citations (5), Referenced by (17), Classifications (22), Legal Events (2) External Links: USPTO, USPTO Assignment, EspacenetPhase change memory devices including memory cells having different phase change materials and related methods and systems
US 7558100 B2Abstract
A phase change memory device may include an integrated circuit substrate and first and second phase change memory elements on the integrated circuit substrate. The first phase change memory element may include a first phase change material having a first crystallization temperature. The second phase change memory element may include a second phase change material having a second crystallization temperature. Moreover, the first and second crystallization temperatures may be different so that the first and second phase change memory elements are programmable at different temperatures. Related methods and systems are also discussed.
a first phase change memory element on the integrated circuit substrate, wherein the first phase change memory element includes a first phase change material having a first crystallization temperature; and
a second phase change memory element on the integrated circuit substrate, wherein the second phase change memory element includes a second phase change material having a second crystallization temperature, and wherein the first and second crystallization temperatures are different so that the first and second phase change memory elements are programmable at different temperatures.
2. A phase change memory device according to claim 1 wherein the second phase change memory element is free of the first phase change material.
3. A phase change memory device according to claim 2 wherein the first phase change memory element is free of the second phase change material.
4. A phase change memory device according to claim 2 wherein the first phase change memory element includes a first layer of the first phase change material and a second layer of the second phase change material.
5. A phase change memory device according to claim 4 further comprising:
a barrier layer in the first phase change memory element, wherein the barrier layer is between the first layer of the first phase change material and the second layer of the second phase change material.
6. A phase change memory device according to claim 5 wherein the barrier layer comprises a layer of titanium and/or titanium nitride.
7. A phase change memory device according to claim 1 wherein the first crystallization temperature is at least 50 degrees C. greater than the second crystallization temperature.
8. A phase change memory device according to claim 1 wherein the first crystallization temperature is at least 100 degrees C. greater than the second crystallization temperature.
9. A phase change memory device according to claim 1 wherein the first phase change material is selected from the group consisting of GaSb, InGaSb2, and/or Ge15Sb85, wherein the second phase change material is selected from the group consisting of InSb, InGaSb2, Ge1Sb4Te7, Ge1Sb2Te4, Ge2Sb2Te5, GeTe, and/or Sb2Te, and wherein the first and second phase change materials are different.
10. A phase change memory device according to claim 1 wherein the first and second phase change materials comprises different chalcogenide materials.
11. A phase change memory device according to claim 1 further comprising:
a third phase change memory element on the integrated circuit substrate, wherein the third phase change memory element includes a third phase change material having a third crystallization temperature, and wherein the third crystallization temperature is different than the first and second crystallization temperatures so that the first, second, and third phase change memory elements are programmable at different temperatures.
12. A phase change memory device according to claim 1 further comprising:
a first diode electrically coupled in series with the first phase change memory element between a first word line and a first bit line; and
a second diode electrically coupled in series with the second phase change memory element between a second word line and a second bit line.
13. A phase change memory device according to claim 1 further comprising:
a first memory access transistor, wherein the first phase change memory element is electrically coupled between a first bit line and a terminal of the first memory access transistor; and
a second memory access transistor, wherein the second phase change memory element is electrically coupled between a second bit line and a terminal of the second memory access transistor.
14. A phase change memory device according to claim 1 further comprising:
a diode electrically coupled in series with the first phase change memory element between a first word line and a first bit line; and
a memory access transistor, wherein the second phase change memory element is electrically coupled between a second bit line and a terminal of the memory access transistor.
15. A phase change memory device according to claim 1 further comprising:
an electronic substrate electrically and mechanically coupled to the integrated circuit substrate; and
a processor electrically coupled to the integrated circuit substrate through the electronic substrate.
16. A phase change memory device according to claim 15 wherein the first crystallization temperature is higher than the second crystallization temperature, wherein the processor is configured to read data from the first phase change memory element without writing data to the first phase change memory element, and wherein the processor is configured to write data to and read data from the second phase change memory element.
17. A method of forming a phase change memory device, the method comprising:
forming a first phase change memory element on a first memory region of an integrated circuit substrate, wherein the first phase change memory element includes a first phase change material having a first crystallization temperature; and
forming a second phase change memory element on a second memory region of the integrated circuit substrate, wherein the second phase change memory element includes a second phase change material having a second crystallization temperature, and wherein the first and second crystallization temperatures are different so that the first and second phase change memory elements are programmable at different temperatures.
18. A method according to claim 17, wherein forming the first phase change memory element includes forming a layer of the first phase change material on the first memory region wherein the second memory region is free of the layer of the first phase change material, and wherein forming the second phase change memory element includes forming a layer of the second phase change material on the second memory region after forming the layer of the first phase change material.
19. A method according to claim 18 wherein forming the layer of the first phase change material comprises,
forming the layer of the first phase change material on the first and second memory regions, and
removing portions of the layer of the first phase change material from the second memory region while maintaining portions of the layer of the first phase change material on the first memory region.
20. A method according to claim 18 wherein forming the layer of the second phase change material comprises,
forming the layer of the second phase change material on the second memory region and on the layer of the first phase change material on the first memory region, and
removing portions of the layer of the second phase change material between the first and second memory regions while maintaining portions of the layer of second phase change material on the second memory region.
21. A method according to claim 20 wherein removing portions of the layer of the second phase change material includes removing portions of the layer of the second phase change material from the layer of the first phase change material on the first memory region.
22. A method according to claim 20 wherein removing portions of the layer of the second phase change material includes maintaining portions of the second phase change material on the layer of the first phase change material on the first memory region.
before forming the layer of the second phase change material, forming a barrier layer on the layer of the first phase change material so that the barrier layer is between the first layer of the first phase change material and the second layer of the second phase change material in the first memory region.
24. A method according to claim 23 wherein the barrier layer comprises a layer of titanium and/or titanium nitride.
25. A method according to claim 17 wherein the first crystallization temperature is at least 50 degrees C. greater than the second crystallization temperature.
26. A method according to claim 17 wherein the first crystallization temperature is at least 100 degrees C. greater than the second crystallization temperature.
27. A method according to claim 17 wherein the first phase change material is selected from the group consisting of GaSb, InGaSb2, and/or Ge15Sb85, wherein the second phase change material is selected from the group consisting of InSb, InGaSb2, Ge1Sb4Te7, Ge1Sb2Te4, Ge2Sb2Te5, GeTe, and/or Sb2Te, and wherein the first and second phase change materials are different.
28. A method according to claim 17 wherein the first and second phase change materials comprises different chalcogenide materials.
29. A method according to claim 17, the method further comprising:
forming a third phase change memory element on the integrated circuit substrate, wherein the third phase change memory element includes a third phase change material having a third crystallization temperature, and wherein the third crystallization temperature is different than the first and second crystallization temperatures so that the first, second, and third phase change memory elements are programmable at different temperatures.
30. A method according to claim 17 further comprising:
before forming the first and second phase change memory elements, forming first and second diodes in the respective first and second memory regions so that the first diode is electrically coupled between the first phase change memory element and a first word line, and the second diode is electrically coupled between the second phase change memory element and a second word line.
31. A method according to claim 17 further comprising:
before forming the forming the first and second phase change memory elements, forming first and second memory access transistors in the respective first and second memory regions so that the first phase change memory element is electrically coupled to a terminal of the first memory access transistor, and the second phase change memory element is electrically coupled to a terminal of the second memory access transistor.
32. A method according to claim 17 further comprising:
before forming the first phase change memory element, forming a diode in the first memory region so that the diode is electrically coupled in series with the first phase change memory element between a first word line and a first bit line; and
before forming the second phase change memory element, forming a memory access transistor in the second memory region so that the second phase change memory element is electrically coupled between a second bit line and a terminal of the memory access transistor.
33. A method according to claim 17 wherein the first crystallization temperature is higher than the second crystallization temperature, the method further comprising:
after forming the first and second phase change memory elements, programming the first phase change memory element; and
after programming the first phase change memory element, electrically and mechanically coupling the integrated circuit substrate to an electronic substrate so that a processor is electrically coupled to the integrated circuit substrate through the electronic substrate.
34. A method according to claim 33 wherein electrically and mechanically coupling the integrated circuit substrate to the electronic substrate comprises reflowing solder and wherein a reflow temperature of the solder is less than the first crystallization temperature.
35. A method according to claim 34 wherein the reflow temperature of the solder is greater than the second crystallization temperature.
36. A method according to claim 34 wherein the processor is configured to read data from the first phase change memory element without writing data to the first phase change memory element, and wherein the processor is configured to write data to and read data from the second phase change memory element.
a phase change memory device electrically and mechanically coupled to the electronic substrate, wherein the phase change memory device includes a first phase change memory element on an integrated circuit substrate, wherein the first phase change memory element includes a first phase change material having a first crystallization temperature, and a second phase change memory element on the integrated circuit substrate, wherein the second phase change memory element includes a second phase change material having a second crystallization temperature, and wherein the first and second crystallization temperatures are different so that the first and second phase change memory elements are programmable at different temperatures; and
a processor electrically coupled to the electronic substrate so that the processor and the phase change memory device are electrically coupled through the electronic substrate.
38. An electronic system according to claim 37 wherein the first crystallization temperature is at least 50 degrees C. greater than the second crystallization temperature.
39. An electronic system according to claim 37 wherein the first and second phase change materials comprise different chalcogenide materials.
40. An electronic system according to claim 37 wherein the processor is configured to read data from the first phase change memory element without writing data to the first phase change memory element, and wherein the processor is configured to write data to and read data from the second phase change memory element.
41. An electronic system comprising:
a first phase change memory device electrically and mechanically coupled to the electronic substrate, wherein the first phase change memory device includes a plurality of first phase change memory elements on a first integrated circuit substrate, wherein each of the first phase change memory elements includes a first phase change material having a first crystallization temperature;
a second phase change memory device electrically and mechanically coupled to the electronic substrate, wherein the second phase change memory device includes a plurality of second phase change memory elements on a second integrated circuit substrate, wherein each of the second phase change memory elements includes a second phase change material having a second crystallization temperature, and wherein the first and second crystallization temperatures are different so that the first and second phase change memory elements are programmable at different temperatures; and
a processor electrically coupled to the electronic substrate so that the processor and the first and second phase change memory devices are electrically coupled through the electronic substrate.
42. An electronic system according to claim 41 wherein the first crystallization temperature is at least 50 degrees C. greater than the second crystallization temperature.
43. An electronic system according to claim 41 wherein the first and second phase change materials comprise different chalcogenide materials.
44. An electronic system according to claim 41 wherein the processor is configured to read data from the first phase change memory device without writing data to the first phase change memory device, and wherein the processor is configured to write data to and read data from the second phase change memory device.
45. A method of operating an electronic system including a first plurality of phase change memory elements each including a first phase change material having a first crystallization temperature, and a second plurality of phase change memory elements each including a second phase change material having a second crystallization temperature wherein the first and second crystallization temperatures are different so that the first and second pluralities of phase change memory elements are programmable at different temperatures, and a processor electrically coupled to the first and second pluralities of phase change memory elements, the method comprising:
reading ROM data from the first plurality of phase change memory elements to the processor without writing the ROM data from the processor to the first plurality of phase change memory elements;
writing programmable data from the processor to the second plurality of phase change memory elements; and
after writing the programmable data, reading the programmable data from the second plurality of phase change memory elements to the processor.
46. A method according to claim 45 wherein the first crystallization temperature is at least 50 degrees C. greater than the second crystallization temperature.
47. A method according to claim 45 wherein the first and second phase change materials comprise different chalcogenide materials.
48. A method according to claim 45 wherein the first and second pluralities of phase change memory elements are provided on a same semiconductor integrated circuit substrate.
49. A method according to claim 45 wherein the first and second pluralities of phase change memory elements are provided on respective first and second semiconductor integrated circuit substrates.
a first plurality of phase change memory elements each including a first phase change material having a first crystallization temperature;
a second plurality of phase change memory elements each including a second phase change material having a second crystallization temperature wherein the first and second crystallization temperatures are different so that the first and second pluralities of phase change memory elements are programmable at different temperatures; and
a processor electrically coupled to the first and second pluralities of phase change memory elements, wherein the processor is configured to
read ROM data from the first plurality of phase change memory elements without writing the ROM data from the processor to the first plurality of phase change memory elements,
write programmable data to the second plurality of phase change memory elements, and
read the programmable data from the second plurality of phase change memory elements after writing the programmable data.
51. An electronic system according to claim 50 wherein the first crystallization temperature is at least 50 degrees C. greater than the second crystallization temperature.
52. An electronic system according to claim 50 wherein the first and second phase change materials comprise different chalcogenide materials.
53. An electronic system according to claim 50 wherein the first and second pluralities of phase change memory elements are provided on a same semiconductor integrated circuit substrate.
54. An electronic system according to claim 50 wherein the first and second pluralities of phase change memory elements are provided on respective first and second semiconductor integrated circuit substrates.
This U.S. non-provisional patent application claims priority under 35 U.S.C. � 119 of Korean Patent Application No. 10-2006-0091370, filed on Sep. 20, 2006, the disclosure of which is hereby incorporated herein by reference in its entirety.
The present invention generally relates to memory devices, and more particularly, to phase change memory devices and related methods.
In a Phase change Random Access Memory (PRAM) device, a state of a phase change material may be used to store information thereby providing non-volatile memory. Phase change materials may exhibit at least two different states, referred to as the amorphous and crystalline states. Transitions between the amorphous and crystalline states may be selectively initiated, for example, using current induced temperature cycles. The states may be distinguished because the amorphous state generally exhibits a higher resistivity than the crystalline state. The amorphous state may have a more disordered atomic structure, and the crystalline state may have a more ordered atomic structure. Generally, any phase-change material may be used in a phase change memory device, but thin-film chalcogenide alloy materials have been found to be particularly suitable.
In a phase change memory device, the phase of a phase change material in a memory cell may be reversibly changed back and forth between the amorphous and crystalline states. In effect, each phase change memory cell may be a programmable resistor that reversibly changes between higher and lower resistance states in response to temperature cycles induced by resistive heating. Phase change memory devices are discussed, for example, in U.S. Pat. No. 6,507,061.
According to some embodiments of the present invention, a phase change memory device may include an integrated circuit substrate, and first and second phase change memory elements of the integrated circuit substrate. The first phase change memory element may include a first phase change material having a first crystallization temperature. The second phase change memory element may include a second phase change material having a second crystallization temperature. Moreover, the first and second crystallization temperatures may be different so that the first and second phase change memory elements are programmable at different temperatures.
The second phase change memory element may be free of the first phase change material. The first phase change memory element may be free of the second phase change material, or the first phase change memory element may include a first layer of the first phase change material and a second layer of the second phase change material. If the first phase change memory element includes layers of the first and second phase change materials, a barrier layer (such as a layer of titanium and/or titanium nitride) may be between the first layer of the first phase change material and the second layer of the second phase change material.
The first crystallization temperature may be at least 50 degrees C. greater than the second crystallization temperature, and more particularly, the first crystallization temperature may be at least 100 degrees C. greater than the second crystallization temperature. The first and second phase change materials may comprise different chalcogenide materials. For example, the first phase change material may be selected from the group consisting of GaSb, InGaSb2, and/or Ge15Sb85, the second phase change material may be selected from the group consisting of InSb, InGaSb2, Ge1Sb4Te7, Ge1Sb2Te4, Ge2Sb2Te5, GeTe, and/or Sb2Te, and the first and second phase change materials may be different.
In addition, a third phase change memory element may be provided on the integrated circuit substrate, with the third phase change memory element including a third phase change material having a third crystallization temperature. The third crystallization temperature may be different than the first and second crystallization temperatures so that the first, second, and third phase change memory elements are programmable at different temperatures.
A first diode may be electrically coupled in series with the first phase change memory element between a first word line and a first bit line, and a second diode may be electrically coupled in series with the second phase change memory element between a second word line and a second bit line. In other alternative embodiments, the first phase change memory element may be electrically coupled between a first bit line and a terminal of a first memory access transistor, and the second phase change memory element may be electrically coupled between a second bit line and a terminal of a second memory access transistor. In still other alternative embodiments, a diode may be electrically coupled in series with the first phase change memory element between a first word line and a first bit line, and the second phase change memory element may be electrically coupled between a second bit line and a terminal of a memory access transistor.
In addition, an electronic substrate may be electrically and mechanically coupled (for example, using solder bumps) to the integrated circuit substrate, and a processor may be electrically coupled to the integrated circuit substrate through the electronic substrate. Moreover, the first crystallization temperature may be higher than the second crystallization temperature, the processor may be configured to read data from the first phase change memory element without writing data to the first phase change memory element, and the processor may be configured to write data to and read data from the second phase change memory element.
According to some other embodiments of the present invention, a method of forming a phase change memory device may include forming first and second phase change memory elements on an integrated circuit substrate. The first phase change memory element may be formed on a first memory region of an integrated circuit substrate, and the first phase change memory element may include a first phase change material having a first crystallization temperature. The second phase change memory element may be formed on a second memory region of the integrated circuit substrate, and the second phase change memory element may include a second phase change material having a second crystallization temperature. Moreover, the first and second crystallization temperatures may be different so that the first and second phase change memory elements are programmable at different temperatures.
Forming the first phase change memory element may include forming a layer of the first phase change material on the first memory region with the second memory region being free of the layer of the first phase change material, and forming the second phase change memory element may include forming a layer of the second phase change material on the second memory region after forming the layer of the first phase change material. Forming the layer of the first phase change material may include forming the layer of the first phase change material on the first and second memory regions, and removing portions of the layer of the first phase change material from the second memory region while maintaining portions of the layer of the first phase change material on the first memory region.
Forming the layer of the second phase change material may include forming the layer of the second phase change material on the second memory region and on the layer of the first phase change material on the first memory region, and removing portions of the layer of the second phase change material between the first and second memory regions while maintaining portions of the layer of second phase change material on the second memory region. Removing portions of the layer of the second phase change material may include removing portions of the layer of the second phase change material from the layer of the first phase change material on the first memory region. In alternative embodiments, removing portions of the layer of the second phase change material may include maintaining portions of the second phase change material on the layer of the first phase change material on the first memory region. Before forming the layer of the second phase change material, a barrier layer (such as a layer of titanium and/or titanium nitride) may be formed on the layer of the first phase change material so that the barrier layer is between the first layer of the first phase change material and the second layer of the second phase change material in the first memory region.
In addition, a third phase change memory element may be formed on the integrated circuit substrate, the third phase change memory element may include a third phase change material having a third crystallization temperature, and the third crystallization temperature may be different than the first and second crystallization temperatures so that the first, second, and third phase change memory elements are programmable at different temperatures.
Before forming the first and second phase change memory elements, first and second diodes may be formed in the respective first and second memory regions so that the first diode is electrically coupled between the first phase change memory element and a first word line and the second diode is electrically coupled between the second phase change memory element and a second word line. In alternative embodiments, before forming the first and second phase change memory elements, first and second memory access transistors may be formed in the respective first and second memory regions so that the first phase change memory element is electrically coupled to a terminal of the first memory access transistor and the second phase change memory element is electrically coupled to a terminal of the second memory access transistor. In other alternative embodiments, before forming the first phase change memory element, a diode may be formed in the first memory region so that the diode is electrically coupled in series with the first phase change memory element between a first word line and a first bit line, and a memory access transistor may be formed in the second memory region so that the second phase change memory element is electrically coupled between a second bit line and a terminal of the memory access transistor.
The first crystallization temperature may be higher than the second crystallization temperature, and after forming the first and second phase change memory elements, the first phase change memory element may be programmed. After programming the first phase change memory element, the integrated circuit substrate may be electrically and mechanically coupled to an electronic substrate so that a processor is electrically coupled to the integrated circuit substrate through the electronic substrate. Electrically and mechanically coupling the integrated circuit substrate to the electronic substrate may include reflowing solder and a reflow temperature of the solder may be less than the first crystallization temperature. Moreover, the reflow temperature of the solder may be greater than the second crystallization temperature. In addition, the processor may be configured to read data from the first phase change memory element without writing data to the first phase change memory element, and the processor may be configured to write data to and read data from the second phase change memory element.
According to still other embodiments of the present invention, an electronic system may include an electronic substrate, a phase change memory device electrically and mechanically coupled to the electronic substrate, and a processor electrically coupled to the electronic substrate. The phase change memory device may include a first phase change memory element on an integrated circuit substrate, and the first phase change memory element may include a first phase change material having a first crystallization temperature. The phase change memory device may also include a second phase change memory element on the integrated circuit substrate, and the second phase change memory element may include a second phase change material having a second crystallization temperature. Moreover, the first and second crystallization temperatures may be different so that the first and second phase change memory elements are programmable at different temperatures. In addition, the processor and the phase change memory device may be electrically coupled through the electronic substrate.
The first crystallization temperature may be at least 50 degrees C. greater than the second crystallization temperature, and more particularly, the first crystallization temperature may be at least 100 degrees C. greater than the second crystallization temperature. For example, the first and second phase change materials may comprise different chalcogenide materials. Moreover, the processor may be configured to read data from the first phase change memory element without writing data to the first phase change memory element, and the processor may be configured to write data to and read data from the second phase change memory element.
According to yet other embodiments of the present invention, an electronic system may include an electronic substrate, first and second phase change memory devices electrically and mechanically coupled to the electronic substrate, and a processor electrically coupled to the electronic substrate. The first phase change memory device may include a plurality of first phase change memory elements on a first integrated circuit substrate, and each of the first phase change memory elements may include a first phase change material having a first crystallization temperature. The second phase change memory device may include a plurality of second phase change memory elements on a second integrated circuit substrate, and each of the second phase change memory elements may include a second phase change material having a second crystallization temperature. Moreover, the first and second crystallization temperatures may be different so that the first and second phase change memory elements are programmable at different temperatures. In addition, the processor and the first and second phase change memory devices may be electrically coupled through the electronic substrate.
The first crystallization temperature may be at least 50 degrees C. greater than the second crystallization temperature, and more particularly, the first crystallization temperature may be at least 100 degrees C. greater than the second crystallization temperature. For example, the first and second phase change materials may comprise different chalcogenide materials. The processor may be configured to read data from the first phase change memory device without writing data to the first phase change memory device, and the processor may be configured to write data to and read data from the second phase change memory device.
According to still more embodiments of the present invention, an electronic system may include a first plurality of phase change memory elements each including a first phase change material having a first crystallization temperature, and a second plurality of phase change memory elements each including a second phase change material having a second crystallization temperature. The first and second crystallization temperatures may be different so that the first and second pluralities of phase change memory elements are programmable at different temperatures. In addition, a processor may be electrically coupled to the first and second pluralities of phase change memory elements. A method of operating such an electronic system may include reading ROM data from the first plurality of phase change memory elements to the processor without writing the ROM data from the processor to the first plurality of phase change memory elements. Moreover, programmable data may be written from the processor to the second plurality of phase change memory elements, and after writing the programmable data, the programmable data may be read from the second plurality of phase change memory elements to the processor.
The first crystallization temperature may be at least 50 degrees C. greater than the second crystallization temperature, and/or the first and second phase change materials may include different chalcogenide materials. Moreover, the first and second pluralities of phase change memory elements may be provided on a same semiconductor integrated circuit substrate, or the first and second pluralities of phase change memory elements may be provided on respective first and second semiconductor integrated circuit substrates.
According to yet more embodiments of the present invention, an electronic system may include a first plurality of phase change memory elements each including a first phase change material having a first crystallization temperature, and a second plurality of phase change memory elements each including a second phase change material having a second crystallization temperature. The first and second crystallization temperatures may be different so that the first and second pluralities of phase change memory elements are programmable at different temperatures. A processor may be electrically coupled to the first and second pluralities of phase change memory elements. More particularly, the processor is configured to read ROM data from the first plurality of phase change memory elements without writing the ROM data from the processor to the first plurality of phase change memory elements. The processor may also be configured to write programmable data to the second plurality of phase change memory elements, and to read the programmable data from the second plurality of phase change memory elements after writing the programmable data.
FIG. 1 is a graph illustrating characteristics of phase change materials used in phase change memory cells.
FIG. 2 is a schematic diagram illustrating a layout of a phase change memory device including high temperature and low temperature memory cell regions according to some embodiments of the present invention.
FIG. 3 is a schematic diagram illustrating a layout of a phase change memory device including high temperature and low temperature memory cell regions according to some other embodiments of the present invention.
FIG. 4 is a cross sectional view illustrating respective high and low temperature memory elements of the phase change memory device of FIG. 2 according to some embodiments of the present invention.
FIG. 5 is a table of chalcogenide materials and respective crystallization temperatures (in degrees C.).
FIG. 6 is a cross sectional view illustrating respective high and low temperature memory elements of the phase change memory device of FIG. 2 according to some other embodiments of the present invention.
FIG. 7 is a cross sectional view illustrating respective high, medium, and low temperature memory elements in a phase change memory device according to still other embodiments of the present invention.
FIG. 8 is a cross sectional view illustrating respective high, medium, and low temperature memory elements in a phase change memory device according to yet other embodiments of the present invention.
FIG. 9 is a cross sectional view illustrating high and low temperature memory elements with memory access transistors in a phase change memory device according to more embodiments of the present invention.
FIGS. 10A-C and 11A-D are cross sectional views illustrating operations of forming phase change memory elements according to embodiments of the present invention.
FIG. 12A is a plan view illustrating a semiconductor integrated circuit wafer including a plurality of phase change memory devices including high and low temperature phase change memory elements according to embodiments of the present invention.
FIG. 12B is a plan view illustrating an individual phase change memory device including high and low temperature phase change memory elements after dicing from the wafer of FIG. 12A according to embodiments of the present invention.
FIG. 12C is a cross sectional view illustrating an electronic system including a phase change memory device including high and low temperature phase change memory elements according to embodiments of the present invention.
FIG. 13 is a cross sectional view illustrating an electronic system including a high temperature phase change memory device and a low temperature phase change memory device according to embodiments of the present invention.
FIG. 1 is a graph illustrating characteristics of a phase change material with the horizontal axis denoting time Time and the vertical axis denoting temperature Temp as applied to the phase change material. With reference to FIG. 1, if the phase change material is heated to a temperature higher than its melting temperature Tm and then quickly cooled below its crystallization temperature Tc over a relatively short quench time T1, a programmable volume of the phase change material may become amorphous as shown by curve 1 (dashed line). If the phase change material is heated to a temperature lower than its melting temperature Tm and higher than its crystallization temperature Tc over a second duration T2 (longer than T1) and then cooled, the programmable volume of the phase change material may become crystalline as shown by curve 2 (solid line). A resistance of the amorphous-state material may be higher than a resistance of the crystalline-state material.
In a read mode, a current flowing through the phase change material may thus be used to determine whether information stored in a phase change memory element is a logic “1” or a logic “0.” With Ge2Sb2Te5, for example, the crystallization temperature Tc may be about 160 degrees C., the melting temperature Tm may be about 610 degrees C., the quench time T1 used to set the amorphous state may be in the range of about 4 ns to about 5 ns, and the duration T2 used to set the crystalline state may be about 500 ns. Operations of phase change memory cells are discussed, for example, in U.S. Pat. No. 7,061,013 to Horii Hideki, the disclosure of which is hereby incorporated herein in its entirety by reference.
According to some embodiments of the present invention, random access memory (RAM) and read only memory (ROM) regions of a same phase change memory device (on a same semiconductor substrate) may include memory elements with different phase change materials having different crystallization temperatures. More particularly, a ROM region of the phase change memory device may include memory elements using a phase change material having a relatively high crystallization temperature, and a RAM region of the phase change memory device may include memory elements using a phase change material having a relatively low crystallization temperature.
Accordingly, the ROM region of the phase change memory device may be programmed before packaging the device without erasing ROM data during subsequent high temperature packaging operations. For example, the phase change material of the ROM region may be selected to have a crystallization temperature greater than a temperature of any operations (such as solder reflow) used during packaging. A crystallization temperature of the phase change material of the RAM region may be less than a temperature of one or more packaging operations because the RAM region of the phase change memory device may remain unprogrammed until after packaging. The ROM region of the memory device may thus be efficiently programmed before packaging without erasing the ROM data during packaging while a phase change material having a lower crystallization temperature may provide faster and/or lower power write operations in the RAM region.
FIG. 2 is a schematic diagram illustrating a layout of a phase change memory device including high temperature and low temperature memory cell regions according to some embodiments of the present invention. As shown in FIG. 2, a phase change memory cell may include a variable resistor Rph (including a high temperature phase change layer) or Rp (including a low temperature phase change layer). Accordingly, each high temperature memory cell 100 in a high temperature region HT of the memory device may include a layer of a relatively high crystallization temperature phase change material (variable resistor Rph also referred to as a memory element) electrically connected in series with a diode D between a bit line BL1 and a word line WL1. Similarly, each low temperature memory cell 200 in a low temperature region LT of the memory device may include a layer of a relatively low crystallization temperature phase change material (variable resistor Rp also referred to as a memory element) connected in series with a diode D between a bit line BL2 and a word line WL2.
FIG. 3 is a schematic diagram illustrating a layout of a phase change memory device including high temperature and low temperature memory cell regions according to some other embodiments of the present invention. As shown in FIG. 3, a phase change memory cell may include a variable resistor Rph (including a high temperature phase change layer) or Rp (including a low temperature phase change layer). Accordingly, each high temperature memory cell in a high temperature region HT of the memory device may include a layer of a relatively high crystallization temperature phase change material (variable resistor Rph also referred to as a memory element) electrically connected in series with a transistor T between a bit line BL1 and a source line (represented as ground), and a gate of each transistor T may be coupled to a word line WL1. Similarly, each low temperature memory cell 200 in a low temperature region LT of the memory device may include a layer of a relatively low crystallization temperature phase change material (variable resistor Rp also referred to as a memory element) connected in series with a transistor T between a bit line BL2 and a source line (represented as ground), and a gate of each transistor T may be coupled to a word line WL2.
FIG. 4 is a cross sectional view illustrating high and low temperature memory cells in respective high temperature HT and low temperature LT regions of the phase change memory device of FIG. 2. As discussed above, high temperature memory cells in the high temperature region HT may provide read only memory (ROM) that is programmed before packaging (e.g., before flip-chip soldering to a printed circuit board), and low temperature memory cells in the low temperature region LT may provide random access memory (RAM) that is programmed after packing (e.g., after flip-chip soldering to a printed circuit board).
As shown in FIG. 4, word lines WL1 and WL2 may be provided as doped regions of a semiconductor substrate 52, and the word lines may be isolated using insulating field regions 53 (such as field oxide regions). While the word lines are shown as doped regions of a semiconductor substrate, word lines may be provided using other conductive patterns such as metal patterns, doped polysilicon patterns, silicide patterns, etc. An interlayer dielectric (ILD) layer 55 (such as a layer of silicon oxide) may be provided on the word lines WL1 and WL2, and contact holes may be formed in the ILD layer 55. Doped polysilicon layers 56 and 57 of opposite conductivity types in the contact holes may provide diodes D, and diode electrodes 59 (such as silicide electrodes) may be provided on the diodes D in the contact holes as shown in FIGS. 2 and 4. More particularly, the diode electrodes 59 may include nickel silicide and/or copper silicide.
An interlayer dielectric (ILD) layer 61 (such as a layer of silicon oxide) may be formed on the diode electrodes 59 and on the ILD layer 55, and contact holes may be formed through the ILD layer 61 exposing portions of the diode electrodes 63. Bottom electrode contacts (BECs) 63 may be formed in the contact holes through the ILD layer 61, and the BECs 63 may include one or more conductive materials such as TiN, TIAlN, TiBN, TiSiN, TaN, TaAlN, TaBN, TaSiN, WN, WBN, WSiN, WAlN, ZrN, ZrSiN, ZrAlN, ZrBN, MoN, Al, Al—Cu, Al—Cu—Si, WSix, Ti, W, Mo, Ta, TiW, and/or Cu.
As shown in FIG. 4, a low temperature phase change memory element Rp may include a layer of a low temperature phase change material 71 a, and an upper electrode 73 a may be provided on the low temperature phase change memory element Rp. A high temperature phase change memory element Rph may include a layer of a high temperature phase change material 65 b, a barrier layer 67 b (for example, including Ti and/or TiN), and a layer of the low temperature phase change material 71 b, and an upper electrode 73 b may be provided on the high temperature phase change memory element Rph. More particularly, the low temperature phase change material may have a crystallization temperature that is lower than a crystallization temperature of the high temperature phase change material. An interlayer dielectric (ILD) 75 may be formed on the phase change memory elements Rp and Rph and upper electrodes 73 a and 73 b, and contact holes in the ILD 75 may expose portions of the upper electrodes 73 a and 73 b. The bit lines BL1 and BL2 may be formed on the ILD 75 and on exposed portions of the upper electrodes 73 a and 73 b. The upper electrodes 73 a and 73 b may include TiN, TiAlN, TiBN, TiSiN, TaN, TaAlN, TaBN, TaSiN, WN, WBN, WSiN, WAlN, ZrN, ZrSiN, ZrAlN, ZrBN, MoN, Al, Al—Cu, Al—Cu—Si, WSix, Ti, W, Mo, Ta, TiW, and/or Cu. Moreover, the bitlines BL1 and BL2 may include aluminum, tungsten, and/or copper. By providing that a contact area between the BECs 63 and the respective phase change memory elements Rp and Rph is small relative to a contact area between the upper electrodes 73 a and 73 b and the respective phase change memory elements Rp and Rph, heating (and resulting phase change) during programming operations may occur in portions of the memory elements Rp and Rph primarily adjacent the BECs 63. Accordingly, inclusion of the layer of the low temperature phase change material 71 b in the high temperature phase change memory element Rph may not significantly affect programming of the high temperature phase change memory element Rph. Stated in other words, a programmable volume of the high temperature phase change memory element Rph may be confined to the layer of the high temperature phase change material 65 b. The low temperature phase change memory element Rp may thus be programmable at a relatively low temperature, and the high temperature phase change memory element Rph may be programmable at a relatively high temperature.
A crystallization temperature of the high temperature phase change material (used in layer 65 b) may be at least about 50 degrees C. higher than a crystallization temperature of the low temperature phase change material (used in layers 71 a and 71 b). More particularly, a crystallization temperature of the high temperature phase change material may be at least about 100 degrees C. higher than a crystallization temperature of the low temperature phase change material.
The low temperature phase change material may be a layer of a first chalcogenide material having a relatively low crystallization temperature, and the high temperature phase change material may be a layer of a second chalcogenide material having a relatively high crystallization temperature. Examples of different chalcogenide materials and their respective crystallization temperatures (in degrees C.) are provided in the table of FIG. 5. According to some embodiments of the present invention, the high temperature phase change material (used for layer 65 b) may be selected from the group consisting of GaSb, InGaSb2, and/or Ge15Sb85, and the low temperature phase change material (used for layers 71 a and 71 b) may be selected from the group consisting of InSb, InGaSb2, Ge1Sb4Te7, Ge1Sb2Te4, Ge2Sb2Te5, GeTe, and/or Sb2Te, with the high and low temperature phase change materials being different.
As shown in FIG. 4, the low temperature phase change memory element Rp may be free of the high temperature phase change material, while the high temperature phase change memory element Rph may include layers of both the high temperature phase change material and the low temperature phase change material. According to other embodiments of the present invention shown in FIG. 6, the high temperature phase change memory element Rph may be free of the low temperature phase change material. In FIG. 6, the BECs 63, the ILD 61, and elements below the BECs 63 and ILD 61 are the same as discussed above with respect to FIG. 4 and will, thus, not be discussed further. In addition, the low temperature phase change memory element Rp (including the layer of the low temperature phase change material 71 a), the upper electrodes 73 a and 73 b, the ILD 75, and the bit lines BL1 and BL2 are the same as discussed above with respect to FIG. 4 and will, thus, not be discussed further herein. As shown in FIG. 6, however, the high temperature phase change memory element Rph′ may include the layer of the high temperature phase change material 65 b without a barrier layer and/or a layer of the low temperature phase change material. The layer of the high temperature phase change material 65 b may be the same as discussed above with respect to FIG. 4.
As shown in FIGS. 4 and 6, high and low temperature phase change memory elements Rph (or Rph′) and Rp may provide programming at two different temperatures determined by the different crystallization temperatures of the high and low temperature phase change materials. Phase change memory elements may provide programming at any number of different temperatures using a corresponding number of phase change memory materials having different crystallization temperatures.
As shown in FIG. 7, a same memory device (on a same semiconductor substrate 52) may include high, medium, and low temperature phase change memory elements Rphh, Rpm, and Rpll. The low temperature phase change memory element Rpll may include a layer of a low temperature phase change material 81 a. The medium temperature phase change-memory element Rpm may include a layer of a medium temperature phase change material 71 b, a barrier layer 87 b (for example, including Ti and/or TiN), and a layer of the low temperature phase change material 81 b. The high temperature phase change memory element Rphh may include a layer of a high temperature phase change material 65 c, a barrier layer 67 c (for example, including Ti and/or TiN), a layer of the medium temperature phase change material 71 c, a barrier layer 87 c (for example, including Ti and/or TiN), and a layer of the low temperature phase change material 81 c. In FIG. 7, the BECs 63, the ILD 61, and elements below the BECs 63 and ILD 61 are the same as discussed above with respect to FIGS. 4 and 6 and will, thus, not be discussed further. In addition, the upper electrodes 73 a, 73 b, and 73 c, and the ILD 75, and the bit lines BL1 and BL2 are the same as discussed above with respect to corresponding elements of FIGS. 4 and 6 and will, thus, not be discussed further herein. While the medium and low temperature phase change memory elements Rpm and Rpll shown in FIG. 7 sharing a same bit line BL2, the medium and low temperature phase change memory elements Rpm and Rpll may be coupled to different bit lines.
By providing that a contact area between the BECs 63 and the respective phase change memory elements Rphh, Rpm, and Rpll is small relative to a contact area between the upper electrodes 73 c, 73 b, and 73 c and the respective phase change memory elements Rp and Rph, heating (and resulting phase change) during programming operations may occur in portions of the memory elements Rphh, Rpm, and Rpll primarily adjacent the BECs 63. Accordingly, inclusion of the layers of the low and medium temperature phase change materials 81 c and 71 c in the high temperature phase change memory element Rphh may not significantly affect programming of the high temperature phase change memory element Rphh. Similarly, inclusion of the layers of the low temperature phase change material 81 b in the medium temperature phase change memory element Rpm may not significantly affect programming of the medium temperature phase change memory element Rpm.
Stated in other words, a programmable volume of the high temperature phase change memory element Rphh may be confined to the layer of the high temperature phase change material 65 c, and a programmable volume of the medium temperature phase change memory element Rpm may be confined to the layer of the medium temperature phase change material 71 b. The low temperature phase change memory element Rpll may thus be programmable at a relatively low temperature, the medium temperature phase change memory element Rpm may be programmable at a medium temperature, and the high temperature phase change memory element Rphh may be programmable at a relatively high temperature.
A crystallization temperature of the high temperature phase change material (used in layer 65 c) may be at least about 50 degrees C. higher than a crystallization temperature of the medium temperature phase change material (used in layers 71 b and 71 c). In addition, a crystallization temperature of the medium temperature phase change material (used in layers 71 b and 71 c) may be at least about 50 degrees C. higher than a crystallization temperature of the low temperature phase change material (used in layers 81 a, 81 b, and 81 c).
The low temperature phase change material may be a layer of a first chalcogenide material having a relatively low crystallization temperature, the high temperature phase change material may be a layer of a second chalcogenide material having a relatively high crystallization temperature, and the medium temperature phase change material may be a layer of a third chalcogenide material having a medium crystallization temperature between the crystallization temperatures of the low and high temperature phase change materials. Examples of different chalcogenide materials and their respective crystallization temperatures (in degrees C.) are provided in the table of FIG. 5.
According to some embodiments of the present invention, the high temperature phase change material (used for layer 65 c) may be selected from the group consisting of GaSb, InGaSb2, and/or Ge15Sb85; the medium temperature phase change material (used for layers 71 b and 71 c) may be selected from the group consisting of InSb, InGaSb2, Ge2Sb2Te5, and/or GeTe; and the low temperature phase change material (used for layers 81 a, 81 b, and 71 b) may be selected from the group consisting of InSb, Ge1Sb4Te7, Ge1Sb2Te4, Ge2Sb2Te5, GeTe, and/or Sb2Te; with the high, medium, and low temperature phase change materials being different. According to some embodiments of the present invention, the high temperature phase change material (used for layer 65 c) may be selected from the group consisting of GaSb and/or Ge15Sb85; the medium temperature phase change material (used for layers 71 b and 71 c) may be selected from the group consisting of InSb, InGaSb2, Ge2Sb2Te5, and/or GeTe; and the low temperature phase change material (used for layers 81 a, 81 b, and 71 b) may be selected from the group consisting of Ge1Sb4Te7, Ge1Sb2Te4, and/or Sb2Te.
As shown in FIG. 7, the low temperature phase change memory element Rpll may be free of the medium and high temperature phase change materials, and the medium temperature phase change memory element Rpm may be free of the high temperature phase change material, while the high temperature phase change memory element Rphh may include layers of the low, medium, and high temperature phase change materials. According to other embodiments of the present invention shown in FIG. 8, the high temperature phase change memory element Rphh′ may be free of the low and medium temperature phase change materials, and the medium temperature phase change memory element Rpm′ may be free of the low temperature phase change material.
In FIG. 8, the BECs 63, the ILD 61, and elements below the BECs 63 and ILD 61 are the same as discussed above with respect to FIGS. 4, 6, and 7, and will, thus, not be discussed further. In addition, the low temperature phase change memory element Rpll (including the layer of the low temperature phase change material 81 a), the upper electrodes 73 a-c, the ILD 75, and the bit lines BL1 and BL2 are the same as discussed above with respect to FIG. 7 and will, thus, not be discussed further herein. As shown in FIG. 8, however, the high temperature phase change memory element Rphh′ may include the layer of the high temperature phase change material 65 c without a barrier layer, without a layer of the medium temperature phase change material, and/or without a layer of the low temperature phase change material. Similarly, the medium temperature phase change memory element Rpm′ may include the layer of the medium temperature phase change material 71 b without a barrier layer and/or without a layer of the low temperature phase change material. The layer of the high temperature phase change material 65 c and the layer of the medium temperature phase change material 71 b may be the same as discussed above with respect to FIG. 7.
As shown in FIGS. 7 and 8, high, medium, and low temperature phase change memory elements Rphh (or Rphh′), Rpm (or Rpm′), and Rpll may provide programming at three different temperatures determined by the different crystallization temperatures of the high, medium, and low temperature phase change materials. Phase change memory elements may provide programming at any number of different temperatures using a corresponding number of phase change memory materials having different crystallization temperatures.
According to still further embodiments of the present invention, each memory cell may include a phase change memory element coupled in series with a memory access transistor as shown in FIG. 9. The memory structure of FIG. 9, for example, may be used to implement the memory architecture discussed above with respect to FIG. 3. In FIG. 9, the ILD 61, the BECs 63, the low temperature phase change memory element Rp (including the layer of low temperature phase change material 71 a), the high temperature phase change memory element Rph (including the layers of the low and high temperature phase change materials 65 b and 71 b and the barrier layer 76 b), the upper electrodes 73 a and 73 b, the ILD 75, and the bit lines BL1 and BL2 are the same as discussed above with respect to FIG. 4, and will thus not be discussed further herein.
As shown in FIG. 9, however, the diodes D of FIG. 4 may be replaced with respective memory access transistors including respective drain regions 91, source regions 93, and gates 95 (provided by respective word lines WL1 and WL2). More particularly, the source and drain regions 91 and 93 may be provided as doped portions of active regions 52 in semiconductor substrate 51, and insulating field regions 53 may provide isolation between memory access transistors. An ILD 55 may be formed on the gate electrodes 95 (provided by word lines WL1 and WL2) and on the source and drain regions 91 and 93. In addition, drain plugs and pads 96 and 97 may provide electrical connection between drain regions 91 and respective BECs 63. Similarly, source plugs 98 may provide electrical connection between source regions and respective source lines 99. As shown in the schematic diagram of FIG. 3, the source lines 99 may be grounded. A source line 99 for a selected memory element/cell, however, may be coupled to any reference voltage suitable for reading/writing data from/to the selected memory element/cell. A phase change memory element Rp and/or Rph may be selected for read and/or write operations by turning on the associated memory access transistor (applying a turn on voltage to the gate 95 of the associated memory access transistor) and applying appropriate electrical signals to the associated bit and source lines.
While not shown in separate figures, memory access transistors (as shown in FIG. 9) may be substituted for diodes D of the structures of any of FIGS. 4, 6, 7, and/or 8. According to still other embodiments of the present invention, a same memory device may include some phase change memory elements coupled to memory access transistors and other phase change memory elements coupled to diodes on a same semiconductor substrate. For example, memory cell access transistors may be substituted for the diodes D in the high temperature region HT of FIG. 2 while maintaining the diodes D in the low temperature region LT of FIG. 2. Stated in other words, the structure of the high temperature region HT of FIG. 3 (including memory access transistors T) may be substituted for the structure of the high temperature region HT of FIG. 2, while maintaining the structure (including diodes D) of the low temperature region LT of FIG. 2. According to other embodiments of the present invention, memory cell access transistors may be substituted for the diodes D in the low temperature region LT of FIG. 2 while maintaining the diodes D in the high temperature region HT of FIG. 2. Stated in other words, the structure of the low temperature region LT of FIG. 3 (including memory access transistors T) may be substituted for the structure of the low temperature region LT of FIG. 2, while maintaining the structure (including diodes D) of the high temperature region HT of FIG. 2.
Methods of forming the phase change memory elements Rp and Rph of FIGS. 4 and/or 9 will now be discussed with reference to FIGS. 10A-C. Methods of forming phase change memory elements Rp and Rph as shown in FIGS. 10A-C may be used with diode memory structures as discussed above with respect to FIGS. 2 and 4, with transistor memory structures as discussed above with respect to FIGS. 3 and 9, and/or with combinations thereof. Accordingly, operations of forming diodes and/or memory access transistors are not shown in FIGS. 10A-C for the sake of conciseness. Elements such as the substrate 52, ILD 55, etc. are thus not shown in FIGS. 10A-C.
As shown in FIG. 10A, bottom electrode contacts (BECs) 63 may be formed extending through interlayer dielectric (ILD) 61. As discussed above, each BEC 63 may be coupled to a respective diode and/or memory access transistor. A layer of the high temperature phase change material 65 may then be formed on the ILD 65 and the BECs 63, and a barrier layer 67 may be formed on the layer of the high temperature phase change material 65.
The layer of the high temperature phase change material 65 and the barrier layer 67 may then be patterned to provide the layer of the high temperature phase change material 65′ and the patterned barrier layer 67′ as shown in FIG. 10B. More particularly, portions of the layer of the high temperature phase change material 65 may be removed from a low temperature region LT of the device. As further shown in FIG. 10B, a layer of a low temperature phase change material 71 may be formed on the ILD 61 and the patterned barrier layer 67′, and a layer of an electrode material 73 may be formed on the layer of the low temperature phase change material 71.
As shown in FIG. 10C, the layer of the electrode material 73, the layer of the low temperature phase change material 71, the barrier layer 67′, and the layer of the high temperature phase change material 65′ may be patterned, for example, using a single photolithography masking operation to form the high temperature phase change memory element Rph and the low temperature phase change memory element Rp. Accordingly, the layer of the high temperature phase change material 65 b, the barrier layer 67 b, and the layer of the low temperature phase change material 71 b of the high temperature phase change memory element Rph and the upper electrode 73 b thereon may be self-aligned. Similarly, the layer of the low temperature phase change material 71 b of the low temperature phase change memory element Rp and the upper electrode 73 a thereon may be self-aligned.
After patterning the memory elements Rp and Rph, an ILD 75 may be formed on ILD 61 and on upper electrodes 73 a and 73 b, and contact holes may be formed in the ILD 75 exposing portions of the respective upper electrodes 73 a and 73 b, as further shown in FIG. 10C. Moreover, the bit lines BL1 and BL2 may be formed on the ILD 75 and on exposed portions of the upper electrodes 73 a and 73 b. to provide the structure of FIGS. 4 and 9. While not shown in FIGS. 10A-C, operations thereof may be extended to provide memory devices including high, medium, and low temperature phase change memory elements on as same semiconductor substrate as discussed above with respect to FIG. 7.
Methods of forming the phase change memory elements Rp and Rph′ of FIG. 6 will now be discussed with reference to FIGS. 11A-D. Methods of forming phase change memory elements Rp and Rph′ as shown in FIGS. 11A-D may be used with diode memory structures as discussed above with respect to FIGS. 2 and 6, with transistor memory structures as discussed above with respect to FIG. 3, and/or with combinations thereof. Accordingly, operations of forming diodes and/or memory access transistors are not shown in FIGS. 11A-D for the sake of conciseness. Elements such as the substrate 52, ILD 55, etc. are thus not shown in FIGS. 11A-D.
As shown in FIG. 11A, bottom electrode contacts (BECs) 63 may be formed extending through interlayer dielectric (ILD) 61. As discussed above, each BEC 63 may be coupled to a respective diode and/or memory access transistor. A layer of the high temperature phase change material 65 may then be formed on the ILD 65 and the BECs 63.
The layer of the high temperature phase change material 65 may then be partially patterned to provide the layer of the high temperature phase change material 65′ and as shown in FIG. 11B. More particularly, portions of the layer of the high temperature phase change material 65 may be removed from a low temperature region LT of the device. As further shown in FIG. 11B, a layer of a low temperature phase change material 71 may be formed on the ILD 61 and the layer of the high temperature phase change material 65′.
The layer of the low temperature phase change material 71 may be partially patterned to provide the layer of the low temperature phase change material 71′ as shown in FIG. 11C. More particularly, portions of the layer of the low temperature phase change material 71 may be removed from a high temperature region HT of the device. As further shown in FIG. 11C, a layer of an electrode material 73 may then be formed on the layer of the low temperature phase change material 71′, on the layer of the high temperature phase change material 65′, and on the ILD 61.
The layer of the electrode material 73, the layer of the low temperature phase change material 71′, and the layer of the high temperature phase change material 65′ may be patterned, for example, using a single photolithography masking operation to form the high temperature phase change memory element Rph′ and the low temperature phase change memory element Rp. Accordingly, the layer of the high temperature phase change material 65 b of the high temperature phase change memory element Rph′ and the upper electrode 73 b thereon may be self-aligned. Similarly, the layer of the low temperature phase change material 71 b of the low temperature phase change memory element Rp and the upper electrode 73 a thereon may be self-aligned.
After patterning the memory elements Rp and Rph′, an ILD 75 may be formed on ILD 61 and on upper electrodes 73 a and 73 b, and contact holes may be formed in the ILD 75 exposing portions of the respective upper electrodes 73 a and 73 b, as further shown in FIG. 11D. Moreover, the bit lines BL1 and BL2 may be formed on the ILD 75 and on exposed portions of the upper electrodes 73 a and 73 b to provide the structure of FIG. 6. While not shown in FIGS. 11A-D, operations thereof may be extended to provide memory devices including high, medium, and low temperature phase change memory elements on as same semiconductor substrate as discussed above with respect to FIG. 8.
According to still further embodiments of the present invention, a plurality of memory devices 1201 a-e, as discussed above with respect to FIGS. 2, 3, 4, 6, 7, 8, 9, 10A-C, and/or 11A-D (including high and low temperature phase change memory elements), may be fabricated on a same semiconductor wafer 1100 as shown in FIG. 12 a. The plurality of memory devices 1201 a-d may then be separated, for example, by dicing the substrate 1100 to provide a plurality of separate memory devices including the memory device 1201 shown in FIG. 12 b. High temperature phase change memory elements of the memory devices 1201 a-e may be programmed with Read Only Memory (ROM) before assembly onto an electronic substrate (e.g., a printed circuit board PCB) or other component of an electronic system. More particularly, the high temperature phase change memory elements of the memory devices 1201 a-e may be programmed with ROM either before or after dicing from the wafer, and then, the separate memory devices 1201 a-e (including ROM programmed high temperature phase change memory elements) may be electrically and mechanically coupled (such as by soldering) to one or more respective electronic substrates.
A memory device 1201 from the wafer 1100 of FIGS. 12 a and 12 b may provide memory for an electronic system 1200, such as a computing device, communications device, entertainment device, etc., as shown in FIG. 12 c. More particularly, a memory device 1201 may be soldered to an electronic substrate 1203 (such as a printed circuit board) together with a processor 1205 of an electronic system 1200. The electronic system 1200 may also include, for example, a user input device(s) (e.g., a keypad, a dial, a joy stick, a touch sensitive screen, etc.), an output device(s) (e.g., a display screen, a printer), a speaker, and/or a microphone, electrically coupled to the electronic substrate 1203, the processor 1205, and/or the memory device 1201. While the memory device 1201 and the processor 1205 are shown on the same electronic substrate 1203, by way of example, the memory device 1201 and the processor 1205 may be provided on different substrates. Electrical coupling between the memory device 1201 and the processor 1205, may be provided, for example, using conductive traces on/in the electronic substrate 1203. Moreover, the memory device 1201 and the processor 1205 may be electrically and mechanically coupled to the electronic substrate 1203, for example, using respective solder bumps 1207 and 1209.
The ROM programmed high temperature phase change memory elements of the memory device 1201 may provide ROM for the electronic system 1200, while the low temperature phase change memory elements may provide Random Access Memory (RAM) that may be used by the electronic system 1200 to read and write data during operation of the electronic system 1200. Because high temperature phase change memory elements of the memory device 1201 are programmed at a temperature higher than any temperature encountered when coupling the memory device 1201 to the electronic substrate 1203 (such as by soldering), ROM can be efficiently programmed before coupling the memory device 1201 to the electronic substrate. Because the low temperature phase change memory elements can be programmed at a relatively low temperature (such as a temperature less than a soldering temperature), less power may be required to write data to the low temperature phase change memory elements (used as RAM) during operation of the electronic system 1200. If the electronic system 1200 is battery powered, battery life may thus be increased by using low temperature phase change memory elements to provide RAM.
According to yet further embodiments of the present invention shown in FIG. 13, an electronic system 1300 (such as a computing device, communications device, entertainment device, etc.) may include a first memory device 1301 including high temperature phase change memory elements and a second memory device 1302 including low temperature phase change memory elements. More particularly, the first phase change memory device 1301 may include a plurality of low temperature phase change memory elements on a first semiconductor substrate, the second phase change memory device 1302 may include a plurality of high temperature phase change memory elements on a second semiconductor substrate, and the first and second semiconductor substrates may be different. Accordingly, memory elements of the first memory device 1301 are programmable at a first temperature, memory elements of the second memory device 1302 are programmable at a second temperature, and the first temperature is greater than the second temperature.
As shown in FIG. 13, the first and second memory devices 1301 and 1302 and a processor 1305 may be coupled to an electronic substrate 1303 (such as a printed circuit board), for example, using respective solder bumps 1307, 1309, and 1311. The electronic system 1300 may also include, for example, a user input device(s) (e.g., a keypad, a dial, a joy stick, a touch sensitive screen, etc.), an output device(s) (e.g., a display screen, a printer), a speaker, and/or a microphone, electrically coupled to the electronic substrate 1303, the processor 1305, and/or the memory devices 1301 and 1302. While the memory devices 1301 and 1302 and the processor 1305 are shown on the same electronic substrate 1303, by way of example, the memory device 1301, the memory device 1302, and/or the processor 1305 may be provided on different substrates. Electrical coupling between the memory devices 1301 and 1302 and the processor 1305, may be provided, for example, using conductive traces on/in the electronic substrate 1303.
The first memory device 1301 (including high temperature phase change memory elements) may be programmed with ROM prior to coupling (such as by soldering) to the electronic substrate 1303. In contrast, the second memory device 1302 may provide RAM that to/from which data may be written and read after coupling (such as by soldering) to the electronic substrate 1303.
The ROM programmed high temperature phase change memory elements of the first memory device 1301 may provide ROM for the electronic system 1300, while the low temperature phase change memory elements of the second memory device 1302 may provide Random Access Memory (RAM) that may be used by the electronic system 1200 to read and write data during operation of the electronic system 1300. Because high temperature phase change memory elements of the first memory device 1301 are programmed at a temperature higher than any temperature encountered when coupling the first memory device 1301 to the electronic substrate 1303 (such as by soldering), ROM can be efficiently programmed before coupling the first memory device 1301 to the electronic substrate 1303. Because the low temperature phase change memory elements of the second memory device 1302 can be programmed at a relatively low temperature (such as a temperature less than a soldering temperature), less power may be required to write data to the low temperature phase change memory elements (used as RAM) during operation of the electronic system 1300. If the electronic system 1300 is battery powered, battery life may thus be increased by using low temperature phase change memory elements to provide RAM.
While separate high temperature and low temperature regions HT and LT of semiconductor substrate 51 are shown in FIGS. 2, 3, 4, 6, 7, 8, and 9 for the sake of clarity, the semiconductor substrate 51 in each of the indicated figures may be a single semiconductor die for an integrated circuit memory device including both the high temperature and low temperature regions HT and LT. Moreover, the semiconductor die including both the high temperature and low temperature regions HT and LT may be fabricated on a semiconductor wafer including a plurality of such semiconductor die, and the plurality of semiconductor die may be separated after fabrication by dicing.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS4599705Sep 10, 1984Jul 8, 1986Energy Conversion Devices, Inc.Programmable cell for use in programmable electronic arraysUS4653024Nov 21, 1984Mar 24, 1987Energy Conversion Devices, Inc.Data storage device including a phase changeable materialUS4820394Dec 1, 1986Apr 11, 1989Energy Conversion Devices, Inc.Phase changeable materialUS4845533Nov 26, 1986Jul 4, 1989Energy Conversion Devices, Inc.Thin film electrical devices with amorphous carbon electrodes and method of making sameUS4924436Jul 20, 1987May 8, 1990Energy Conversion Devices, Inc.Data storage device having a phase change memory medium reversible by direct overwrite and method of direct overwriteUS5124232Aug 2, 1990Jun 23, 1992Toray Industries, Inc.Optical recording mediumUS5166758Jan 18, 1991Nov 24, 1992Energy Conversion Devices, Inc.Electrically erasable phase change memoryUS5278011Apr 28, 1993Jan 11, 1994Matsushita Electric Industrial Co., Ltd.Reversible optical information-recording mediumUS5714768Oct 24, 1995Feb 3, 1998Energy Conversion Devices, Inc.Second-layer phase change memory array on top of a logic deviceUS5811816Aug 7, 1996Sep 22, 1998U.S. Philips CorporationClosed cycle gas cryogenically cooled radiation detectorUS5825046Oct 28, 1996Oct 20, 1998Energy Conversion Devices, Inc.Composite memory material comprising a mixture of phase-change memory material and dielectric materialUS6258062Feb 25, 1999Jul 10, 2001Joseph M. ThielenEnclosed container power supply for a needleless injectorUS6381967Nov 24, 1998May 7, 2002Randall H CraigCryogenic freezing of liquidsUS6429064Sep 29, 2000Aug 6, 2002Intel CorporationReduced contact area of sidewall conductorUS6437383Dec 21, 2000Aug 20, 2002Intel CorporationDual trench isolation for a phase-change memory cell and method of making sameUS6507061Aug 31, 2001Jan 14, 2003Intel CorporationMultiple layer phase-change memoryUS6586761Sep 7, 2001Jul 1, 2003Intel CorporationPhase change material memory deviceUS6646297Dec 26, 2000Nov 11, 2003Ovonyx, Inc.Lower electrode isolation in a double-wide trenchUS6750469Sep 4, 2002Jun 15, 2004Kabushiki Kaisha ToshibaPhase change nonvolatile storage device and drive circuitUS6759267Jul 19, 2002Jul 6, 2004Macronix International Co., Ltd.Method for forming a phase change memoryUS6774388Dec 5, 2002Aug 10, 2004Ovonyx, Inc.Modified contact for programmable devicesUS6815704Sep 4, 2003Nov 9, 2004Silicon Storage Technology, Inc.Phase change memory device employing thermally insulating voidsUS6858277Mar 10, 2000Feb 22, 2005Matsushita Electric Industrial Co., Ltd.Information recording medium and method for manufacturing the sameUS6858454Oct 1, 2003Feb 22, 2005Matsushita Electric Industrial Co., Ltd.Method for measuring semiconductor constituent element content and method for manufacturing a semiconductor deviceUS6891742Jul 12, 2002May 10, 2005Sanyo Electric Co., Ltd.Semiconductor memory deviceUS6899938Feb 22, 2002May 31, 2005Energy Conversion Devices, Inc.Phase change data storage device for multi-level recordingUS6919578Dec 6, 2002Jul 19, 2005Ovonyx, IncUtilizing atomic layer deposition for programmable deviceUS6937507 *Dec 5, 2003Aug 30, 2005Silicon Storage Technology, Inc.Memory device and method of operating sameUS7037762May 7, 2003May 2, 2006Samsung Electronics Co., Ltd.Phase changeable memory devices having multi-level data storage elements and methods of fabricating the sameUS7049623Dec 13, 2002May 23, 2006Ovonyx, Inc.Vertical elevated pore phase change memoryUS7061013Feb 26, 2004Jun 13, 2006Samsung Electronics Co., Ltd.Phase change storage cells for memory devices, memory devices having phase change storage cells and methods of forming the sameUS7088670Sep 18, 2002Aug 8, 2006Victor Company Of Japan LimitedInformation recording carrier and method of reproducing the sameUS7115927Feb 18, 2004Oct 3, 2006Samsung Electronics Co., Ltd.Phase changeable memory devicesUS7205562Dec 13, 2002Apr 17, 2007Intel CorporationPhase change memory and method thereforUS20020072010Mar 10, 2000Jun 13, 2002Masayuki KubogataMethod of manufacturing dielectric layer for use in phase change type optical diskUS20020081804Dec 27, 2000Jun 27, 2002Manzur GillPhase-change memory cell using silicon on insulatorUS20020160553Feb 14, 2002Oct 31, 2002Hideo YamanakaMethod and apparatus for forming a thin semiconductor film, method and apparatus for producing a semiconductor device, and electro-opitcal apparatusUS20030006535Jun 26, 2002Jan 9, 2003Michael HennesseyMethod and apparatus for forming microstructures on polymeric substratesUS20030122170Dec 31, 2001Jul 3, 2003Mac ApodacaAdhesion layer for a polymer memory device and method thereforUS20030151041Feb 19, 2003Aug 14, 2003Chien ChiangUsing selective deposition to form phase-change memory cellsUS20040012009Feb 20, 2003Jan 22, 2004Stmicroelectronics S.R.L.Sublithographic contact structure, phase change memory cell with optimized heater shape, and manufacturing method thereofUS20040038445Aug 26, 2003Feb 26, 2004Tyler LowreyMethod of making programmable resistance memory elementUS20040106065Sep 8, 2003Jun 3, 2004Hitachi Maxell, Ltd.Information-recording mediumUS20040113137Dec 13, 2002Jun 17, 2004Lowrey Tyler A.Memory and access device and method thereforUS20040114317Dec 13, 2002Jun 17, 2004Chien ChiangForming phase change memoriesUS20040115945Dec 13, 2002Jun 17, 2004Lowrey Tyler A.Using an electron beam to write phase change memory devicesUS20040165422Feb 18, 2004Aug 26, 2004Horii HidekiPhase changeable memory devices and methods for fabricating the sameUS20040191683Feb 27, 2004Sep 30, 2004Takashi NishiharaInformation recording medium and method for manufacturing the sameUS20040248339Jun 6, 2003Dec 9, 2004Lung Hsiang LanHigh density chalcogenide memory cellsUS20050002227Aug 4, 2004Jan 6, 2005Horii HidekiPhase changeable memory devices including nitrogen and/or silicon and methods for fabricating the sameUS20050019975Apr 19, 2004Jan 27, 2005Se-Ho LeePhase change memory devices having phase change area in porous dielectric layer and methods for manufacturing the sameUS20050115829Dec 5, 2002Jun 2, 2005Masataka YahagiSputtering target for phase-change memory, film for phase change memory formed by using the target, and method for producing the targetUS20050227035Apr 4, 2005Oct 13, 2005Hitachi Maxell, Ltd.Information recording mediumUS20060072370Aug 17, 2005Apr 6, 2006Bong-Jin KuhPhase-changeable memory devices and methods of forming the sameUS20060087921Aug 31, 2005Apr 27, 2006Tomio IwasakiPhase change memoryUS20060121391Dec 2, 2005Jun 8, 2006Yoon-Ho KhangPhase change memory device having phase change material layer containing phase change nano particles and method of fabricating the sameJPH10340489A Title not availableKR19990067038A Title not availableKR20010111276A Title not availableKR20040076225A Title not availableKR20040078464A Title not availableKR20050011609A Title not availableKR20050059855A Title not availableKR20050110680A Title not availableKR20060016312A Title not availableKR20060051652A Title not availableKR20060061745A Title not availableKR20060099158A Title not availableWO1997015954A1Oct 22, 1996May 1, 1997Energy Conversion Devices, Inc.Second-layer phase change memory array on top of a logic deviceWO2000054982A1Mar 10, 2000Sep 21, 2000Matsushita Electric Industrial Co., Ltd.Information recording medium and method for manufacturing the sameWO2003009302A1Jul 12, 2002Jan 30, 2003Sanyo Electric Co., Ltd.Semiconductor memory deviceWO2004084228A1Mar 18, 2003Sep 30, 2004Kabushiki Kaisha ToshibaPhase change memory device* Cited by examinerNon-Patent CitationsReference1Decision to Grant Patent issued by Korean Intellectual Property Office for Korean Application No. 10-2006-0091370, Jan. 9, 2008.2English Translation of Korean Office Action date Jul. 27, 2007 for Korean Application No. 10-2006-0091370.3Korean Office Action date Jul. 27, 2007 for Korean Application No. 10-2006-0091370.4Notice to File a Response/Amendment to the Examination Report corresponding to Korean Patent Application No. 10-2004-0012358 mailed May 24, 2006.5Notice to File Response/Amendment to the Examination Report, Korean Application No. 10-2004-0012358, Dec. 21, 2005.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS7843715 *Nov 30, 2010Samsung Electronics Co., Ltd.Memory cell of a resistive semiconductor memory device, a resistive semiconductor memory device having a three-dimensional stack structure, and related methodsUS7869257 *Jan 11, 2011Qimonda AgIntegrated circuit including diode memory cellsUS7995374 *Aug 9, 2011Kabushiki Kaisha ToshibaSemiconductor memory device, method of manufacturing the same, and method of screening the sameUS8094485 *Dec 15, 2008Jan 10, 2012Panasonic CorporationVariable resistance nonvolatile storage device with oxygen-deficient oxide layer and asymmetric substrate bias effectUS8222626Feb 12, 2010Jul 17, 2012Kabushiki Kaisha ToshibaSemiconductor memory device, method of manufacturing the same, and method of screening the sameUS8233311Jul 31, 2012Panasonic CorporationVariable resistance nonvolatile storage device having a source line formed of parallel wiring layers connected to each other through viasUS8472238Jun 27, 2012Jun 25, 2013Panasonic CorporationVariable resistance nonvolatile storage device with oxygen-deficient oxide layer and asymmetric substrate bias effectUS8835895 *Jun 3, 2013Sep 16, 2014Sony CorporationMemory device and fabrication process thereofUS9257643 *Aug 16, 2013Feb 9, 2016International Business Machines CorporationPhase change memory cell with improved phase change materialUS20080175031 *Jan 17, 2008Jul 24, 2008Samsung Electronics Co., Ltd.Memory cell of a resistive semiconductor memory device, a resistive semiconductor memory device having a three-dimensional stack structure, and related methodsUS20090035514 *Mar 3, 2008Feb 5, 2009Myung-Jin KangPhase change memory device and method of fabricating the sameUS20090154227 *Dec 17, 2007Jun 18, 2009Qimonda North America Corp.Integrated circuit including diode memory cellsUS20100177555 *Dec 15, 2008Jul 15, 2010Kazuhiko ShimakawaVariable resistance nonvolatile storage deviceUS20100202186 *Aug 12, 2010Mitsuru SatoSemiconductor memory device, method of manufacturing the same, and method of screening the sameUS20100238704 *Nov 13, 2009Sep 23, 2010Kabushiki Kaisha ToshibaSemiconductor memory device, method of manufacturing the same, and method of screening the sameUS20110031461 *Oct 22, 2010Feb 10, 2011Samsung Electronics Co., Ltd.Phase change memory deviceUS20150048291 *Aug 16, 2013Feb 19, 2015Macronix International Company, Ltd.Phase change memory cell with improved phase change material* Cited by examinerClassifications U.S. Classification365/148, 365/177, 365/175International ClassificationG11C11/00Cooperative ClassificationG11C7/04, H01L45/1233, H01L45/148, H01L27/2436, H01L45/06, G11C2213/79, G11C11/5678, H01L27/2409, G11C13/0004, H01L45/144European ClassificationG11C13/00R1, G11C11/56P, H01L45/12D4, H01L45/14D, H01L27/24F, H01L45/06, H01L45/14B6, H01L27/24DLegal EventsDateCodeEventDescriptionJul 25, 2007ASAssignmentOwner name: SAMSUNG ELECTRONICS CO., LTD., KOREA, REPUBLIC OFFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:AHN, DONG-HO;HORII, HIDEKI;BAE, JUN-SOO;REEL/FRAME:019669/0980Effective date: 20070709Dec 26, 2012FPAYFee paymentYear of fee payment: 4RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services