KR101055488B1 - Carrier for manufacturing printed circuit board, manufacturing method thereof and manufacturing method of printed circuit board using same - Google Patents
Carrier for manufacturing printed circuit board, manufacturing method thereof and manufacturing method of printed circuit board using same Download PDF
KR101055488B1
KR101055488B1 KR1020090125592A KR20090125592A KR101055488B1 KR 101055488 B1 KR101055488 B1 KR 101055488B1 KR 1020090125592 A KR1020090125592 A KR 1020090125592A KR 20090125592 A KR20090125592 A KR 20090125592A KR 101055488 B1 KR101055488 B1 KR 101055488B1
KR1020090125592A
KR20110068575A (en
2009-12-16 Application filed by 삼성전기주식회사 filed Critical 삼성전기주식회사
2009-12-16 Priority to KR1020090125592A priority Critical patent/KR101055488B1/en
2011-06-22 Publication of KR20110068575A publication Critical patent/KR20110068575A/en
2011-08-08 Publication of KR101055488B1 publication Critical patent/KR101055488B1/en
The present invention relates to a carrier for manufacturing a printed circuit board, a method for manufacturing the same, and a method for manufacturing a printed circuit board using the same, comprising a magnetic sheet and a metal layer bonded to at least one surface of the magnetic sheet by magnetization of the magnetic sheet. It is characterized in that the carrier structure is simply manufactured without going through the vacuum method or release processing method at the time of coupling and separation of the carrier, the process cost and processing time is reduced, the printed circuit board is maintained the size of the printed circuit board Provided are a manufacturing carrier, a method of manufacturing the same, and a method of manufacturing a printed circuit board using the same.
Magnetic Sheet, Magnetic Filler, Magnetic Metal Layer, Carrier
A CARRIER FOR MANUFACTURING A PRINTED CIRCUIT BOARD AND A METHOD OF MANUFACTURING THE SAME AND A METHOD OF MANUFACTURING A PRINTED CIRCUIT BOARD USING THE SAME}
The present invention relates to a carrier for manufacturing a printed circuit board, a method for manufacturing the same, and a method for manufacturing a printed circuit board using the same.
In recent years, due to the development of the electronic industry, the demand for high functionalization and light weight reduction of electronic components is rapidly increasing. Accordingly, printed circuit boards on which such electronic components are mounted also require high density wiring and thinning.
In particular, in order to cope with the thinning of the printed circuit board, a coreless substrate that can reduce the overall thickness and shorten the signal processing time by removing the core substrate has been attracting attention. However, in the case of the coreless substrate, since the core substrate is not used, a carrier member capable of performing a support function during the manufacturing process is required.
1 to 5 illustrate a method of manufacturing a printed circuit board using a carrier according to the prior art. Hereinafter, the manufacturing method will be described with reference to FIGS. 1 to 5.
First, as shown in FIG. 1, the carrier 10 is prepared. Specifically, the adhesive layer 12, the first metal layer 13, and the second metal layer 14 are sequentially formed on both surfaces of the copper foil laminated plate 11 (CCL) having copper foil layers formed on both surfaces of the insulating layer. At this time, both ends of the adhesive layer 12 are adhered to the copper-clad laminate 11 and the second metal layer 14 by applying heat and pressure with a high temperature / high pressure press. On the other hand, the first metal layer 13 is in contact with the second metal layer 14 but is not bonded.
Next, as shown in FIG. 2, the buildup layer 15 is formed on both sides of the carrier 10, and the third metal layer 16 is formed on the outermost insulating layer. The buildup layer 15 is generally performed by a known method, and vias connecting the respective buildup circuit layers may be additionally formed. In addition, the third metal layer 16 is formed to prevent warpage of the build-up layer 15.
Next, as shown in FIG. 3, the buildup layer 15 is separated from the carrier 10. At this time, both ends of the adhesive layer 12 bonded to the copper-clad laminate 11 and the second metal layer 14 are removed through a router process to separate the buildup layer 15 from the carrier 10. Since the first metal layer 13 serves as a release layer and is not bonded to the second metal layer 14, when the adhesive layer 12 is removed, the first metal layer 13 is easily separated from the second metal layer 14.
Next, as shown in FIG. 4, the second metal layer 14 and the third metal layer 16 formed on the buildup layer 15 are removed by etching.
Next, as shown in FIG. 5, the open part 17 which exposes the pad part 19 of the outermost circuit layer of the buildup layer 15 is processed to the outermost insulating layer of the buildup layer 15, and solder ball (18) is formed.
However, in the case of a conventional printed circuit board using a carrier, since both ends of the printed circuit board are cut by the router process, there is a problem that the size of the printed circuit board is reduced.
In addition, since the use of a vacuum method to secure the bonding of the carrier 10, or to form a separate release layer to facilitate the separation of the carrier 10, there was a problem that the process cost and process time increases.
The present invention has been made to solve the problems of the prior art as described above, and an object of the present invention is a carrier for manufacturing a printed circuit board and a method of manufacturing the printed circuit board is maintained even after separating the carrier and the printed circuit board and It is to provide a method of manufacturing a printed circuit board using the same.
Another object of the present invention is to simplify a structure of a carrier without using a vacuum method or a release layer insertion method between a carrier and a printed circuit board, thereby reducing a process cost and processing time, and a manufacturing method of a carrier for a printed circuit board and a method of manufacturing the same. An object of the present invention is to provide a method of manufacturing a printed circuit board.
The carrier for manufacturing a printed circuit board according to the first embodiment of the present invention is characterized in that it comprises a magnetic sheet and a metal layer bonded to at least one surface of the magnetic sheet by the magnet of the magnetic sheet.
Here, the magnetic sheet is characterized in that it comprises a glass fiber.
In addition, the magnetic sheet is characterized in that it comprises a magnetic filler having a magnetic.
In addition, the metal layer is characterized by consisting of nickel (Ni), cobalt (Co), chromium (Cr), iron (Fe), or manganese (Mn).
In the carrier for manufacturing a printed circuit board according to the second preferred embodiment of the present invention, in the carrier for manufacturing a printed circuit board according to the first preferred embodiment of the present invention, the magnetic sheet is formed on a sheet and at least one surface of the sheet. And a magnetic metal layer having magnetic properties.
In a method of manufacturing a carrier for manufacturing a printed circuit board according to a first preferred embodiment of the present invention, (A) preparing a magnetic sheet, and (B) a magnetic layer of the magnetic sheet, the metal layer on at least one surface of the magnetic sheet It characterized in that it comprises a step of combining.
At this time, in the step (A), the magnetic sheet is characterized in that it comprises a glass fiber.
Further, in the step (A), the magnetic sheet is characterized in that it comprises a magnetic filler having a magnetic.
In addition, in the step (B), the metal layer is characterized in that consisting of nickel, cobalt, chromium, iron, or manganese.
In the method for manufacturing a carrier for manufacturing a printed circuit board according to the second exemplary embodiment of the present invention, in the method for manufacturing a carrier for manufacturing a printed circuit board according to the first preferred embodiment of the present invention, the step (A) may include (A1). ) Providing a sheet, and (A2) forming a magnetic metal layer having magnetic properties on at least one surface of the sheet to prepare a magnetic sheet.
In a method of manufacturing a printed circuit board using a carrier according to a first embodiment of the present invention, (A) at least one surface of a magnetic sheet, by combining the metal layer by the magnetic of the magnetic sheet to prepare a carrier, (B Forming a first passivation layer on the metal layer, forming a buildup layer on the first passivation layer, forming a second passivation layer on the buildup layer, and (C) separating the magnetic sheet and the metal layer; And removing the metal layer.
At this time, in the step (A), the metal layer is characterized in that consisting of nickel, cobalt, chromium, iron, or manganese.
In addition, in the step (A), the magnetic sheet is characterized in that it comprises a glass fiber.
In addition, the step (A) is to prepare a magnetic sheet by forming a magnetic metal layer having magnetic properties on at least one surface of the (A1) sheet, and (A2) by the magnetism of the magnetic metal layer, the metal layer on the magnetic metal layer It characterized in that it comprises a step of combining.
In addition, the (C) step, (C1) separating the magnetic sheet and the metal layer, (C2) removing the metal layer by etching, and (C3) the exposed first protective layer and the second And forming an open portion in the protective layer to expose the pad portion of the outermost circuit layer of the build-up layer.
According to a second aspect of the present invention, there is provided a method of manufacturing a printed circuit board using a carrier, the method comprising: (A) bonding a metal layer by magnetic of the magnetic sheet to at least one surface of a magnetic sheet, (B) Forming a circuit layer on the metal layer, forming a build-up layer on the metal layer on which the circuit layer is formed, and (C) separating the magnetic sheet and the metal layer and removing the metal layer. It is done.
At this time, the step (C), (C1) separating the magnetic sheet and the metal layer, (C2) removing the metal layer, (C3) forming a protective layer on both sides of the exposed build-up layer And (C4) forming an open portion in the protective layer to expose a pad portion of the outermost circuit layer of the circuit layer and the buildup layer.
In addition, the metal layer and the circuit layer is characterized in that composed of different metals.
Prior to this, the terms or words used in this specification and claims should not be construed in the usual and dictionary sense, and the inventors will be required to properly define the concepts of terms in order to best describe their invention. On the basis of the principle that it can be interpreted as meaning and concept corresponding to the technical idea of the present invention.
A carrier for manufacturing a printed circuit board according to the present invention, a method for manufacturing the same, and a method for manufacturing a printed circuit board using the same, by forming a carrier with a magnetic layer and a metal layer bonded by a magnetic, separate cutting during separation of the carrier and the printed circuit board Since the process is not necessary, the size of the printed circuit board is maintained.
In addition, according to the present invention, by forming the carrier in a simple structure using the magnetic of the magnetic sheet, there is an advantage that the process cost and processing time is reduced.
BRIEF DESCRIPTION OF THE DRAWINGS The objects, particular advantages and novel features of the present invention will become more apparent from the following detailed description taken in conjunction with the accompanying drawings, in which: FIG. In the present specification, in adding reference numerals to the components of each drawing, it should be noted that the same components as possible, even if displayed on different drawings have the same number as possible. In addition, terms such as first and second may be used to describe various components, but the components should not be limited by the terms. The terms are used only for the purpose of distinguishing one component from another. In addition, in describing the present invention, if it is determined that the detailed description of the related known technology may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be omitted.
For printed circuit board manufacturing carrier
6 is a cross-sectional view of a carrier 100a for manufacturing a printed circuit board according to the first embodiment of the present invention. Hereinafter, the carrier 100a for manufacturing a printed circuit board according to the present embodiment will be described with reference to this.
As shown in FIG. 6, the carrier 100a for manufacturing a printed circuit board according to the present exemplary embodiment includes a magnetic sheet 101a and a metal layer 104 formed on at least one surface of the magnetic sheet 101a.
The magnetic sheet 101a is a member that couples the metal layer 104 by magnetism to one or both surfaces thereof, and may include a sheet 102 and a magnetic filler 103a.
Here, the sheet 102 preferably has great rigidity as a member for supporting the printed circuit board at the time of manufacturing the printed circuit board. For example, the sheet 102 may contain glass fabric to increase rigidity. In addition, the sheet 102 may be composed of, for example, a non-insulating material such as a metal, or an insulating material such as an epoxy resin.
The magnetic filler 103a is magnetic particles, and the metal layer 104 is bonded to the magnetic sheet 101a by the magnetism of the magnetic filler 103a. The magnetic filler 103a may be composed of, for example, a metal filler such as nickel or iron, or a ferrite filler such as NiCuZn ferrite or AnZn ferrite. Meanwhile, although the magnetic filler 103a is illustrated as being included in the sheet 102 in FIG. 6, this is merely an example, and the magnetic filler 103a may be applied to the outside of the sheet 102.
The metal layer 104 is a member bonded to one side or both sides of the magnetic sheet 101a.
Here, the metal layer 104 is preferably made of a material bonded to a magnetic material such as nickel, cobalt, chromium, iron, or manganese. On the other hand, since the metal layer 104 constitutes the carrier 100a together with the magnetic sheet 101a, the metal layer 104 is preferably made of a material having high strength.
In addition, although the metal layer 104 is illustrated as being bonded to both surfaces of the magnetic sheet 101a in FIG. 6, this is merely illustrative, and may be formed only on one surface thereof.
7 is a cross-sectional view of a carrier 100b for manufacturing a printed circuit board according to the second embodiment of the present invention. Hereinafter, the carrier 100b for manufacturing a printed circuit board according to the present embodiment will be described with reference to this. Here, the same or corresponding components are referred to by the same reference numerals, and descriptions overlapping with the first embodiment will be omitted.
As shown in FIG. 7, the carrier 100b for manufacturing a printed circuit board according to the present exemplary embodiment includes a sheet 102, a magnetic sheet 101b including a magnetic metal layer 103b, and a metal layer 104. Can be.
The magnetic metal layer 103b is a member formed on at least one surface of the sheet 102 and is made of a magnetic material.
Here, the magnetic metal layer 103b may be made of a metal having magnetic properties, such as nickel, cobalt, iron, or an alloy thereof. In addition, the magnetic metal layer 103b is not necessarily limited to metal, and for example, a polymer magnet can be used, and an electromagnet can also be used.
Meanwhile, the metal layer 104 is bonded to one surface of the magnetic metal layer 103b by the magnetism of the magnetic metal layer 103b.
For printed circuit board manufacturing Carrier Manufacturing method
8 and 9 illustrate a method of manufacturing a carrier 100a for manufacturing a printed circuit board according to the first exemplary embodiment of the present invention. Hereinafter, referring to FIGS. 8 and 9, the manufacturing method of the carrier 100a for manufacturing a printed circuit board according to the present embodiment will be described.
First, as shown in FIG. 8, the magnetic sheet 101a is prepared.
In this case, the magnetic sheet 101a may include, for example, a sheet 102 and a magnetic filler 103a provided with a reinforcing material such as glass fiber. For example, when the sheet 102 is made of an insulating material such as epoxy, the glass sheet and the magnetic filler 103a are impregnated in a semi-cured state, and then the magnetic sheet 101a having high strength while curing the insulating material has magnetic properties. Can be prepared. In addition, it is also possible to apply the magnetic filler 103a to the outer surface of the sheet 102 by, for example, a spray method.
Next, as shown in FIG. 9, the metal layer 104 is bonded to at least one surface of the magnetic sheet 101a.
In this case, the metal layer 104 may be coupled to the magnetic sheet 101a by the magnetism of the magnetic filler 103a of the magnetic sheet 101a. On the other hand, the bonding force between the metal layer 104 and the magnetic sheet 101a may be satisfied as long as foreign materials such as etching liquid do not penetrate during the manufacturing process of the printed circuit board.
By this manufacturing process, the carrier 100a for manufacturing a printed circuit board according to the first preferred embodiment of the present invention shown in Fig. 9 is manufactured.
10 to 12 are views for explaining a method of manufacturing a carrier (100b) for manufacturing a printed circuit board according to a second embodiment of the present invention. Hereinafter, referring to FIGS. 10 to 12, the manufacturing method of the carrier 100b for manufacturing a printed circuit board according to the present embodiment will be described. Here, the same or corresponding components are referred to by the same reference numerals, and descriptions overlapping with the first embodiment will be omitted.
First, as shown in FIGS. 10 and 11, the sheet 102 is prepared, and the magnetic sheet 101b is manufactured by forming the magnetic metal layer 103b on one or both surfaces of the sheet 102.
In this case, the magnetic metal layer 103b may be formed on the sheet 102 by, for example, bonding with a metal adhesive, or a sputtering method.
Next, as shown in FIG. 12, the metal layer 104 is bonded to the magnetic sheet 101b.
In this case, the metal layer 104 may be coupled to the magnetic metal layer 103b by the magnetism of the magnetic metal layer 103b of the magnetic sheet 101b.
By such a manufacturing process, the carrier 100b for manufacturing a printed circuit board according to the second preferred embodiment of the present invention shown in FIG. 12 is manufactured.
Carrier Manufacturing method of printed circuit board using
13 to 17 are cross-sectional views illustrating a method of manufacturing a printed circuit board 200a using a carrier according to a first exemplary embodiment of the present invention. Hereinafter, a manufacturing method of the printed circuit board 200a using the carrier according to the present embodiment will be described with reference to FIGS. 13 to 17.
In the present embodiment, the printed circuit board 200a will be manufactured on both sides of the carrier 100a, but the present invention is not limited thereto, and the printed circuit board 200a may be manufactured only on one surface of the carrier 100a. It is also possible. In the present embodiment, the carrier 100a according to the first embodiment will be described, but it is also possible to use the carrier 100b according to the second embodiment.
First, as shown in FIG. 13, the carrier 100a for manufacturing a printed circuit board is prepared by bonding the metal layer 104 to the magnetic sheet 101a including the magnetic filler 103a.
In this case, when the printed circuit board 200a is manufactured only on one surface of the carrier 100a, the metal layer 104 may be bonded to only one surface of the magnetic sheet 101a.
Next, as shown in FIG. 14, the first protective layer 105, the buildup layer 106, and the second protective layer 107 are formed in the metal layer 104.
First, the first protective layer 105 is formed on the metal layer 104 of the carrier 100a. Here, the first protective layer 105 is a member for protecting the outermost circuit layer of the build-up layer 106 to be described later, for example, composed of a solder resist such as dry film type solder resist or liquid solder resist Can be.
Next, the buildup layer 106 is formed on the first protective layer 105. In this case, although the buildup layer 106 is illustrated as three layers in FIG. 15, this is merely an example, and may be configured as a single layer or a multilayer. Meanwhile, the buildup layer 106 may be composed of a buildup insulating layer and a buildup circuit layer, and may be formed in a conventional manner. For example, the build-up circuit layer may be formed by a semi-additive process (SAP).
Next, the second protective layer 107 may be formed in the buildup layer 106. In this case, the second protective layer 107 may be made of the same material as the first protective layer 105.
Next, as shown in FIG. 15, the metal layer 104 and the magnetic sheet 101a are separated.
At this time, the metal layer 104 and the magnetic sheet (101a) is coupled by a magnetic bar, it is possible to easily remove relatively. In addition, since there is no separate routing process, the size of the printed circuit board can be maintained.
Next, as shown in FIG. 16, the metal layer 104 bonded to the first protective layer 105 is removed.
At this time, for example, the metal layer 104 may be removed by an etching process. In addition, the metal layer 104 is preferably made of a different metal from the buildup circuit layer of the buildup layer 106 to prevent the buildup circuit layer from being unexpectedly etched.
Next, as shown in FIG. 17, an open portion 108 is formed in the first protective layer 105 and the second protective layer 107.
In this case, the open part 108 may expose the pad part 109 of the outermost circuit layer of the build-up layer 106. In addition, the open part 108 may be formed by, for example, a laser method or a machining drill method.
By such a manufacturing process, the printed circuit board 200a using the carrier according to the first preferred embodiment of the present invention shown in Fig. 17 is manufactured.
18 to 22 are cross-sectional views illustrating a method of manufacturing a printed circuit board 200b using a carrier according to a second exemplary embodiment of the present invention. Hereinafter, a method of manufacturing the printed circuit board 200b using the carrier according to the present embodiment will be described with reference to FIGS. 18 to 22. Here, the same or corresponding components are referred to by the same reference numerals, and descriptions overlapping with the first embodiment will be omitted.
In the present embodiment, the case where the carrier 100b according to the second embodiment is used will be described, but it is also possible to use the carrier 100a according to the first embodiment.
First, as shown in FIG. 18, the magnetic metal layer 103b is formed on the sheet 102 to manufacture the magnetic sheet 101b, and the metal layer 104 is bonded to the magnetic metal layer 103b, thereby producing a printed circuit board carrier. Prepare 100b.
In this case, when the printed circuit board 200b is manufactured only on one surface of the carrier 100b, the magnetic metal layer 103b and the metal layer 104 may be formed only on one surface of the sheet 102.
Next, as shown in FIG. 19, after the circuit layer 106a is formed in the metal layer 104, the buildup layer 106 is formed in the metal layer 104 in which the circuit layer 106a was formed.
At this time, the circuit layer 106a is a layer which will be the outermost circuit layer of the build-up layer 106, for example, a subtractive method, an additive method, and a semi-additive method. It can be formed using an additive method, a modified semi-additive method and the like. In addition, the circuit layer 106a is made of an electrically conductive metal such as gold, silver, copper, nickel, and preferably made of a metal different from the metal layer 104 which is subsequently removed.
Next, as shown in FIGS. 20 to 22, the magnetic metal layer 103b and the metal layer 104 are separated, the metal layer 104 is removed, and the protective layer 110 is exposed to the outermost layer of the build-up layer 106. ) And an open portion 108 for exposing the pad portion 109 to the protective layer 110.
At this time, when the magnetic metal layer 103b is made of an electromagnet, the current flowing through the electromagnet may be blocked to release the coupling force between the magnetic metal layer 103b and the metal layer 104.
By such a manufacturing process, a printed circuit board 200b using a carrier according to the second preferred embodiment of the present invention shown in FIG. 22 is manufactured.
Although the present invention has been described in detail with reference to specific embodiments, this is for describing the present invention in detail, and a carrier for manufacturing a printed circuit board, a method for manufacturing the same, and a method for manufacturing a printed circuit board using the same are not limited thereto. It will be apparent that modifications and improvements are possible by those skilled in the art within the technical idea of the present invention.
1 to 5 are cross-sectional views illustrating a method of manufacturing a printed circuit board according to the prior art.
6 is a cross-sectional view of a carrier for manufacturing a printed circuit board according to the first embodiment of the present invention.
7 is a cross-sectional view of a carrier for manufacturing a printed circuit board according to a second exemplary embodiment of the present invention.
8 and 9 are cross-sectional views illustrating a method of manufacturing a carrier for manufacturing a printed circuit board shown in FIG. 6.
10 to 12 are cross-sectional views illustrating a method of manufacturing a carrier for manufacturing a printed circuit board shown in FIG. 7.
13 to 17 are cross-sectional views illustrating a method of manufacturing a printed circuit board using a carrier according to a first exemplary embodiment of the present invention.
18 to 22 are cross-sectional views illustrating a method of manufacturing a printed circuit board using a carrier according to a second exemplary embodiment of the present invention.
101a, 101b: magnetic sheet 102: sheet
103a: magnetic filler 103b: magnetic metal layer
104: metal layer 106: build-up layer
Magnetic sheet; And
A metal layer bonded to at least one surface of the magnetic sheet by the magnet of the magnetic sheet;
Carrier for manufacturing a printed circuit board comprising a.
The magnetic sheet is a carrier for manufacturing a printed circuit board comprising a glass fiber.
The magnetic sheet is a carrier for manufacturing a printed circuit board comprising a magnetic filler having a magnetic.
The magnetic sheet,
A magnetic metal layer formed on at least one surface of the sheet and having magnetic properties;
The metal layer is a carrier for manufacturing a printed circuit board, characterized in that consisting of nickel (Ni), cobalt (Co), chromium (Cr), iron (Fe), or manganese (Mn).
(A) preparing a magnetic sheet; And
(B) bonding the metal layer to at least one surface of the magnetic sheet by the magnetism of the magnetic sheet;
Manufacturing method of a carrier for manufacturing a printed circuit board comprising a.
In the step (A), the magnetic sheet is a manufacturing method of a carrier for manufacturing a printed circuit board, characterized in that it comprises a glass fiber.
In the step (A), the magnetic sheet is a manufacturing method of a carrier for manufacturing a printed circuit board, characterized in that it comprises a magnetic filler having a magnetic.
(A1) providing a sheet; And
(A2) preparing a magnetic sheet by forming a magnetic metal layer having magnetic properties on at least one surface of the sheet;
Method of manufacturing a carrier for manufacturing a printed circuit board comprising a.
In the step (B), the metal layer is a manufacturing method of a carrier for manufacturing a printed circuit board, characterized in that consisting of nickel, cobalt, chromium, iron, or manganese.
(A) manufacturing a carrier by bonding a metal layer to at least one surface of a magnetic sheet by magnetization of the magnetic sheet;
(B) forming a first passivation layer on the metal layer, forming a buildup layer on the first passivation layer, and forming a second passivation layer on the buildup layer; And
(C) separating the magnetic sheet and the metal layer and removing the metal layer;
Method of manufacturing a printed circuit board using a carrier comprising a.
In the step (A), the metal layer is a manufacturing method of a printed circuit board using a carrier, characterized in that consisting of nickel, cobalt, chromium, iron, or manganese.
In the step (A), the magnetic sheet is a manufacturing method of a printed circuit board using a carrier, characterized in that the glass fiber.
In the step (A), the magnetic sheet is a manufacturing method of a printed circuit board using a carrier, characterized in that it comprises a magnetic filler having a magnetic.
(A1) preparing a magnetic sheet by forming a magnetic metal layer having magnetic properties on at least one surface of the sheet; And
(A2) bonding the metal layer to the magnetic metal layer by magnetization of the magnetic metal layer;
(C1) separating the magnetic sheet and the metal layer;
(C2) removing the metal layer by etching; And
(C3) forming an open portion in the exposed first protective layer and the second protective layer to expose a pad portion of an outermost circuit layer of the build-up layer;
(B) forming a circuit layer on the metal layer, and forming a buildup layer on the metal layer on which the circuit layer is formed; And
(C2) removing the metal layer;
(C3) forming protective layers on both sides of the exposed build-up layer; And
(C4) forming an open portion in the protective layer to expose a pad portion of the outermost circuit layer of the circuit layer and the build-up layer;
The metal layer and the circuit layer is a manufacturing method of a printed circuit board using a carrier, characterized in that composed of different metals.
KR1020090125592A 2009-12-16 2009-12-16 Carrier for manufacturing printed circuit board, manufacturing method thereof and manufacturing method of printed circuit board using same KR101055488B1 (en)
KR1020090125592A KR101055488B1 (en) 2009-12-16 2009-12-16 Carrier for manufacturing printed circuit board, manufacturing method thereof and manufacturing method of printed circuit board using same
US12/753,697 US20110138615A1 (en) 2009-12-16 2010-04-02 Carrier for manufacturing printed circuit board and method of manufacturing the same and method of manufacturing printed circuit board using the same
KR20110068575A KR20110068575A (en) 2011-06-22
KR101055488B1 true KR101055488B1 (en) 2011-08-08
ID=44141303
US (1) US20110138615A1 (en)
KR (1) KR101055488B1 (en)
KR101055462B1 (en) 2010-01-07 2011-08-08 삼성전기주식회사 Carrier for manufacturing printed circuit board, manufacturing method thereof and manufacturing method of printed circuit board using same
CN109152226B (en) * 2018-11-06 2019-12-03 瑞华高科技电子工业园(厦门)有限公司 A kind of method of ultra-thin single side FPC production
JP2005243999A (en) 2004-02-27 2005-09-08 Ngk Spark Plug Co Ltd Method for manufacturing wiring board
KR100693140B1 (en) 2001-05-15 2007-03-13 엘지전자 주식회사 Making method of PCB
JP2007184369A (en) 2006-01-05 2007-07-19 Kyocera Corp Wiring board and its manufacturing method
JP2009032918A (en) 2007-07-27 2009-02-12 Shinko Electric Ind Co Ltd Wiring substrate, manufacturing method thereof, electronic component device, and manufacturing method thereof
2009-12-16 KR KR1020090125592A patent/KR101055488B1/en not_active IP Right Cessation
2010-04-02 US US12/753,697 patent/US20110138615A1/en not_active Abandoned
US20110138615A1 (en) 2011-06-16
KR20110068575A (en) 2011-06-22
JP4974803B2 (en) 2012-07-11 Shield film for printed wiring board and printed wiring board
WO2008035416A1 (en) 2008-03-27 Flex-rigid printed circuit board, and method for manufacturing the flex-rigid printed circuit board
JP2009038278A5 (en) 2010-02-18
KR20090032836A (en) 2009-04-01 Manufacturing method of substrate
US20060060558A1 (en) 2006-03-23 Method of fabricating package substrate using electroless nickel plating
KR20130063475A (en) 2013-06-14 Method and support member for manufacturing wiring substrate, and structure member for wiring substrate