Patent US7605209 - Coating compositions containing reactive diluents and methods - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsThe present invention provides coating compositions that include reactive diluents and have high performance, low VOC levels, and low irritation levels. Certain embodiments of the present invention include water and water-dispersible polymers and other embodiments do not include water....http://www.google.com/patents/US7605209?utm_source=gb-gplus-sharePatent US7605209 - Coating compositions containing reactive diluents and methodsAdvanced Patent SearchTry the new Google Patents, with machine-classified Google Scholar results, and Japanese and South Korean patents.Publication numberUS7605209 B2Publication typeGrantApplication numberUS 10/854,890Publication dateOct 20, 2009Filing dateMay 27, 2004Priority dateJun 12, 2003Fee statusPaidAlso published asCA2526970A1, CA2526970C, CN1805989A, CN102690595A, EP1631610A2, EP1631610B1, US9469780, US20040254293, US20100004376, US20170029662, WO2004111143A2, WO2004111143A3Publication number10854890, 854890, US 7605209 B2, US 7605209B2, US-B2-7605209, US7605209 B2, US7605209B2InventorsT. Howard Killilea, James M BohannonOriginal AssigneeValspar Sourcing, Inc.Export CitationBiBTeX, EndNote, RefManPatent Citations (55), Non-Patent Citations (16), Referenced by (10), Classifications (73), Legal Events (4) External Links: USPTO, USPTO Assignment, EspacenetCoating compositions containing reactive diluents and methods
US 7605209 B2Abstract
The present invention provides coating compositions that include reactive diluents and have high performance, low VOC levels, and low irritation levels. Certain embodiments of the present invention include water and water-dispersible polymers and other embodiments do not include water.
1. A method of preparing a coating composition, the method comprising:
providing a mixture comprising a water-dispersible polymer and a reactive diluent,
wherein the water-dispersible polymer is prepared in the presence of the reactive diluent,
wherein the mixture has a viscosity below 100,000 centipoise at processing temperatures, and
further wherein the reactive diluent is present in an amount of 5 wt-% to 40 wt-%, based on the total weight of the reactive diluent and the water-dispersible polymer, and includes a compound having a molecular weight of 350 grams/mole to 1000 grams/mole and, is substantially free of ethylene oxide and propylene oxide moieties and has an OH-functionality of no more than 30 milliequivalents KOH/gram, with the proviso that the reactive diluent does not include pentaerythritol tetraacrylate; and
dispersing the mixture in water.
2. The method of claim 1 wherein the water-dispersible polymer is selected from the group consisting of polyurethanes, epoxies, polyamides, chlorinated polyolefins, acrylics, oil-modified polymers, polyesters, and mixtures or copolymers thereof.
3. The method of claim 2 wherein the water-dispersible polymer is a water-dispersible polyurethane.
4. The method of claim 3 wherein the water-dispersible polyurethane comprises amine or acid functionality.
5. The method of claim 3 wherein the water-dispersible polyurethane comprises ethylenic unsaturation.
6. The method of claim 5 wherein the ethylenic unsaturation comprises (meth)acrylate functionality.
7. The method of claim 5 wherein the ethylenic unsaturation comprises auto-oxidative carbon-carbon double bonds.
8. The method of claim 1 wherein the coating composition further comprises a metal drier.
9. The method of claim 1 wherein the coating composition further comprises a free-radical initiator.
10. The method of claim 1 wherein the coating composition comprises no more than 7 wt-% volatile organic compounds.
11. The method of claim 1 wherein the reactive diluent comprises a compound selected from the group of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), di-(pentaerythritol hexamethacrylate), dipentaerythritol hexaacrylate, pentaerythritol tetramethacrylate, di-(trimethylolpropane tetravinyl ether), di-(pentaerythritol hexavinyl ether), pentaerythritol tetravinyl ether, di-(trimethylolpropane tetraallyl ether), di-(trimethylolpropane tetramethallyl ether), di(pentaerythritol hexaallyl ether), di-(pentaerythritol hexamethallyl ether), pentaerythritol tetraallyl ether, pentaerythritol tetramethallyl ether, and mixtures thereof.
12. The method of claim 1 wherein the reactive diluent comprises a compound selected from the group consisting of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), and combinations thereof.
13. The method of claim 1 wherein the reactive diluent comprises a (meth)acrylate, a vinyl ether, a (meth)allyl ether, or mixtures or copolymers thereof.
14. The method of claim 13 wherein the reactive diluent comprises a (meth)acrylate-functional compound.
15. The method of claim 14 wherein the (meth)acrylate-functional compound is selected from the group consisting of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), and combinations thereof.
16. The method of claim 1 wherein the reactive diluent is present in an amount of 10 wt-% to 30 wt-%, based on the total weight of the reactive diluent and the water-dispersible polymer.
17. The method of claim 1, wherein the water-dispersible polymer is an oil-modified water-dispersible polymer.
18. The method of claim 17 wherein the oil-modified water-dispersible polymer is an alkyd.
19. The method of claim 17 wherein the oil-modified water-dispersible polymer is an oil-modified water-dispersible polyurethane.
20. The method of claim 19 wherein the reactive diluent is present in an amount of 10 wt-% to 30 wt-%, based on the total weight of the reactive diluent and the oil-modified water-dispersible polymer.
21. The method of claim 19 wherein the reactive diluent comprises a (meth)acrylate, a vinyl ether, a (meth)allyl ether, or mixtures or copolymers thereof.
22. The method of claim 21 wherein the reactive diluent comprises a (meth)acrylate-functional compound.
23. The method of claim 22 wherein the (meth)acrylate-functional compound is selected from the group consisting of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), and combinations thereof.
24. The method of claim 17 wherein the reactive diluent comprises a compound selected from the group of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), di-(pentaerythritol hexamethacrylate), pentaerythritol tetramethacrylate, di-(trimethylolpropane tetravinyl ether), di-(pentaerythritol hexavinyl ether), pentaerythritol tetravinyl ether, di-(trimethylolpropane tetraallyl ether), di-(trimethylolpropane tetramethallyl ether), di(pentaerythritol hexaallyl ether), di-(pentaerythritol hexamethallyl ether), pentaerythritol tetraallyl ether, pentaerythritol tetramethallyl ether, and mixtures thereof.
25. The method of claim 24 wherein the oil-modified water-dispersible polymer is an alkyd.
26. The method of claim 24 wherein the mixture comprises no more than 7 wt-% volatile organic compounds.
27. The method of claim 24 wherein the reactive diluent comprises a compound selected from the group consisting of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), and combinations thereof.
28. The method of claim 24 wherein the mixture further comprises a metal drier.
29. The method of claim 24 wherein the reactive diluent comprises a compound selected from the group of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), pentaerythritol tetramethacrylate, di-(trimethylolpropane tetravinyl ether), di-(pentaerythritol hexavinyl ether), pentaerythritol tetravinyl ether, di-(trimethylolpropane tetraallyl ether), di-(trimethylolpropane tetramethallyl ether), di(pentaerythritol hexaallyl ether), di-(pentaerythritol hexamethallyl ether), pentaerythritol tetraallyl ether, pentaerythritol tetramethallyl ether, and mixtures thereof.
30. The method of claim 29 wherein the mixture further comprises a metal drier.
31. The method of claim 29 wherein the oil-modified water-dispersible polymer is an alkyd.
32. The method of claim 1 wherein if the reactive diluent is provided as a mixture of compounds, the entire mixture is substantially non-irritating.
33. The method of claim 1 wherein the water-dispersible polymer comprises an acid forming group, and wherein the method further comprises neutralizing the acid forming group with a neutralizing base prior to dispersing the mixture in water.
34. The method of claim 1 wherein the water-dispersible polymer comprises a urethane polymer, and wherein the method further comprises providing chain extenders to the mixture after dispersing the mixture in water.
35. A method of preparing a coating composition, the method comprising:
further wherein the reactive diluent is present in an amount of 5 wt-% to 40 wt-%, based on the total weight of the reactive diluent and the water-dispersible polymer, wherein the reactive diluent is substantially non-irritating; and wherein if the reactive diluent is provided as a mixture of compounds, the entire mixture is substantially non-irritating; and
36. The method of claim 35 wherein the reactive diluent is present in an amount of 10 wt-% to 30 wt-%, based on the total weight of the reactive diluent and the water-dispersible polymer.
37. The method of claim 35 wherein the mixture comprises no more than 7 wt-% volatile organic compounds.
38. The method of claim 35 wherein the water-dispersible polymer comprises a (meth)acrylate-functional water-dispersible polyurethane, and the substantially non-irritating reactive diluent comprises a (meth)acrylate-functional compound.
39. The method of claim 38 wherein the (meth)acrylate-functional compound is selected from the group consisting of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), and combinations thereof.
40. The method of claim 35 wherein the water-dispersible polymer comprises an oil-modified water-dispersible polyurethane, and the substantially non-irritating reactive diluent comprises a (meth)acrylate-functional compound.
41. The method of claim 40 wherein the (meth)acrylate-functional compound is selected from the group consisting of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), and combinations thereof.
42. The method of claim 40 wherein the mixture further comprises a metal drier.
43. The method of claim 35 wherein the reactive diluent does not include pentaerythritol tetraacrylate.
44. The method of claim 35 wherein the water-dispersible polymer comprises an acid forming group, and wherein the method further comprises neutralizing the acid forming group with a neutralizing base prior to dispersing the mixture in water.
45. The method of claim 35 wherein the water-dispersible polymer comprises a urethane polymer, and wherein the method further comprises providing chain extenders to the mixture after dispersing the mixture in water. Description
The present application claims the benefit of U.S. Provisional Application No. 60/478,070, filed on Jun. 12, 2003, which is incorporated herein by reference in its entirety.
There is a significant need for lower VOC-containing (volatile organic compound-containing) systems in the coatings industry due to increasing environmental restrictions. Typically, lower VOC-containing systems have been achieved by using lower molecular weight polymers. However, this can result in products having poorer performance.
In an effort to reduce the amount of VOC's released, and maintain performance, manufacturers have been using water-based polyurethanes. Such water-based polyurethanes are usually linear polymers and produce films that have chemical resistance lower than the highly crosslinked films of solvent-borne urethane systems. Preparing the polyurethane coating compositions by pre-crosslinking a water-based polyurethane polymer can be accomplished by incorporating a large amount of monomers that have more than two reactive functional groups in the prepolymer stage. However, this results in highly viscous prepolymer blends that cannot be easily dispersed in water. Diluents have been used to address this problem of viscosity, but many are highly irritating either to skin, eyes, or both. In many instances the presence of an “irritating” diluent will require that extensive industrial hygiene measures be undertaken before using the product. However, such measures may not be practical and such products may not be selected as a result.
Thus, what is needed are coating compositions that have high performance, low VOC levels, and low irritation levels.
Preferred water-dispersed coating compositions include no more than seven weight percent (wt-%) (more preferably no more than 4 wt-%) volatile organic compounds (VOC). However, certain other compositions, e.g., alkyd-based compositions, may contain higher VOC levels.
In one embodiment, a coating composition is provided that includes: a water-dispersible polymer (e.g., polyurethanes, epoxies, polyamides, chlorinated polyolefins, acrylics, oil-modified polymers, polyesters, and mixtures or copolymers thereof); a reactive diluent that includes a compound having a molecular weight of at least 350 grams/mole (preferably a molecular weight of 350 grams/mole to 1000 grams/mole), wherein the reactive diluent is substantially free of ethylene oxide and propylene oxide moieties and has an OH-functionality of no more than 30 milliequivalents KOH/gram; and water.
In another embodiment, a coating composition is provided that includes a water-dispersible polymer, a substantially non-irritating reactive diluent, and water. If the reactive diluent is provided as a mixture of compounds, the mixture as a whole is substantially non-irritating. That is, the phrase “reactive diluent” can encompass one or more compounds. If it is a mixture of compounds, the entire mixture must be substantially nonirritating.
In another embodiment, a coating composition is provided that includes an oil-modified polymer (e.g., an alkyd, an oil-modified polyurethane, oil-modified epoxy, oil-modified polyamide, oil-modified acrylics, and mixtures or copolymers thereof); and a reactive diluent that includes a compound having a molecular weight of at least 350 grams/mole (preferably a molecular weight of 350 grams/mole to 1000 grams/mole), wherein the reactive diluent is substantially free of ethylene oxide and propylene oxide moieties and has an OH-functionality of no more than 30 milliequivalents KOH/gram. The oil-modified polymer is water-dispersible for certain embodiments.
In another embodiment, a coating composition is provided that includes an oil-modified polymer and a substantially non-irritating reactive diluent. If the reactive diluent is provided as a mixture of compounds, the entire mixture is substantially non-irritating.
Typically, the water-dispersible polymer includes amine or acid functionality. It can also include ethylenic unsaturation (e.g., (meth)acrylate functionality or auto-oxidative carbon-carbon double bonds).
The reactive diluent can include a (meth)acrylate (wherein “(meth)acrylate” refers to an acrylate and a methacrylate), a vinyl ether, a (meth)allyl ether (wherein (meth)allyl ether refers to an allyl ether and a methallyl ether), or mixtures or copolymers thereof. Preferably, the reactive diluent includes a (meth)acrylate-functional compound, such as those selected from the group consisting of di-(trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), and mixtures thereof.
The present invention also provides methods for coating that involve applying a coating composition to a substrate and allowing the coating composition to harden. The present invention also provides coatings prepared or preparable from the coating compositions described herein. For example, a coating of the present invention is preparable by a method that involves applying a coating composition of the present invention to a substrate and allowing the coating composition to harden.
The present invention also provides a method of preparing a coating composition, the method involves: providing a mixture that includes a water-dispersible polymer and a reactive diluent having a viscosity below 100,000 centipoise (cps) at processing or use temperatures, wherein the reactive diluent has a molecular weight of at least 350 grains/mole and is substantially free of ethylene oxide and propylene oxide moieties and has an OH-functionality of no more than 30 milliequivalents KOH/gram; and dispersing the mixture in water. Significantly, because of the use of the reactive diluent, this process does not require the need for added solvent.
As used herein, a “reactive diluent” includes one or more relatively low molecular weight compounds that react with at least one of the following: a polymer (e.g., a water-dispersible polymer such as a polyurethane), itself, another reactive diluent, or any combination of these; a reactive diluent can form an interpenetrating network with the polymer or can crosslink with the polymer; and can be a monomer, oligomer, or polymer.
Also herein, “water-dispersible” means the polymer is itself capable of being dispersed into water (i.e., without requiring the use of a separate surfactant) or water can be added to the polymer to form a stable dispersion (i.e., the dispersion should have at least one month shelf stability at normal storage temperatures).
Also herein, “a,” “an,” “the,” “at least one,” and “one or more” are used interchangeably.
Also herein, the terms “comprises” and variations thereof do not have a limiting meaning where these terms appear in the description and claims.
Coating compositions of the present invention include a reactive diluent and either a water-dispersible polymer or an oil-modified polymer, which can be water-dispersible or not. When combined with the polymer, the reactive diluent is capable of providing a low VOC-containing composition.
Preferably, coating compositions of the present invention have a viscosity below 100,000 cps, more preferably below 30,000 cps, even more preferably below 15,000 cps, even more preferably below 5,000 cps, and most preferably below 1,000 cps at processing or use conditions.
Preferably, the coating compositions include no more than 7 weight percent (wt-%) volatile organic compounds. More preferably, the coating compositions of the present invention include no more than 4 wt-% volatile organic compounds. Volatile organic compounds are defined in U.S. Pat. No. 6,048,471 (Henry) and in the U.S. Federal Register: Jun. 16, 1995, volume 60, number 111.
Coating compositions of the present invention preferably include a reactive diluent in an amount of at least 5 weight percent (wt-%), more preferably at least 10 wt-%, and most preferably at least 15 wt-%, based on the combined weight of the reactive diluent and the polymer component of the composition. Coating compositions of the present invention preferably include a reactive diluent in an amount of no more than 40 weight percent (wt-%), more preferably no more than 30 wt-%, and most preferably no more than 25 wt-%, based on the combined weight of the reactive diluent and the polymer component of the composition.
Water-dispersed coating compositions of the present invention preferably include at least 40 wt-% water, based on the total weight of the composition. Water-dispersed coating compositions of the present invention preferably include no more than 80 wt-% water, and more preferably no more than 70 wt-%, based on the total weight of the composition.
The coating compositions of the present invention may be applied to a variety of substrates including wood, cement, tile, metal, plastic, glass, optical fibers, and fiberglass. Coating compositions can be applied to a substrate by a variety of methods known to those skilled in the art. Such methods include spraying, painting, rollcoating, brushing, fan coating, curtain coating, spreading, air knife coating, die-coating, vacuum coating, spin coating, electrodeposition, and dipping. The thickness of the coatings will vary with the application. Typically, the coatings will have a thickness of 0.1 to 20 mils (0.00025 to 0.0508 centimeters (cm)), however, thicker or thinner coatings are also contemplated depending on, for example, the desired coating properties.
Compounds that function as reactive diluents are of relatively low molecular weight and can be reactive monomers, oligomers, or low molecular weight polymers. A compound that can function as a reactive diluent is one that can react with at least one of the polymer (the water-dispersible polymer or oil-modified polymer), itself, another reactive diluent, or all of these. The polymer and reactive diluent can form, for example, an interpenetrating network. Alternatively, the reactive diluent can participate in crosslinking the polymer.
Suitable reactive diluent compounds have a relatively low molecular weight. Preferably, suitable reactive diluent compounds have a molecular weight of at least 350 grams/mole (g/mol). Preferably, the molecular weight is no more than 1000 g/mol.
Preferred reactive diluents are also substantially non-irritating, more preferably essentially non-irritating, and most preferably completely non-irritating. If the reactive diluent is provided as a mixture of compounds, the entire mixture is substantially non-irritating, preferably essentially non-irritating, and more preferably completely non-irritating.
A “substantially non-irritating” diluent has a Draize rating of no more than 1 for skin (on a scale of 0 to 8) and no more than 10 for eyes (on a scale of 0 to 110). An “essentially non-irritating” diluent has a Draize rating of no more than 0.5 for skin and no more than 5 for eyes. A “completely non-irritating” diluent has a Draize rating of no more than 0.1 for skin and no more than 3 for eyes.
Preferred reactive diluents are substantially free of ethylene oxide and propylene oxide moieties. More preferably, they are essentially free of ethylene oxide and propylene oxide moieties. Most preferably, they are completely free of ethylene oxide and propylene oxide moieties. “Substantially free” means that less than 5 wt-% ethylene oxide and propylene oxide moieties are present in the reactive diluent. “Essentially free” means that less than 1 wt-% ethylene oxide and propylene oxide moieties are present in the reactive diluent. “Completely free” means that less than 0.5 wt-% ethylene oxide and propylene oxide moieties are present in the reactive diluent.
Preferred reactive diluents have an OH-functionality of no more than 30 milliequivalents KOH/gram (meq/g). Preferably, the reactive diluent has an OH-functionality of no more than 25 meq/g. More preferably, the reactive diluent has an OH-functionality of no more than 20 meq/g.
Reactive diluents typically include compounds with ethylenic unsaturation. Suitable such compounds include a (meth)acrylate, a vinyl ether, a (meth)allyl ether, or mixtures or copolymers thereof. Examples of (meth)acrylate-functional reactive diluents include di-trimethylolpropane tetraacrylate), di-(trimethylolpropane tetramethacrylate), di(pentaerythritol hexaacrylate), di-(pentaerythritol hexamethacrylate), pentaerythritol tetraacrylate, and pentaerythritol tetramethacrylate. Examples of vinyl ether reactive diluents include di-(trimethylolpropane tetravinyl ether), di-(pentaerythritol hexavinyl ether), and pentaerythritol tetravinyl ether. Examples of (meth)allyl ether reactive diluents include di-(trimethylolpropane tetraallyl ether), di-(trimethylolpropane tetramethallyl ether), di(pentaerythritol hexaallyl ether), di-(pentaerythritol hexamethallyl ether), pentaerythritol tetraallyl ether, and pentaerythritol tetramethallyl ether. Preferred reactive diluent compounds are (meth)acrylate functional, which include acrylate functionality and methacrylate functionality. Preferred reactive diluents include (meth)acrylate functional compounds. Of these, the preferred reactive diluent compounds are di-(trimethylolpropane tetraacrylate) and di-trimethylolpropane tetramethacrylate). Reactive diluents used in coating compositions of the present invention if desired can include mixtures of compounds.
Polymers suitable for the coating compositions of the present invention are either water-dispersible or oil-modified, which can be water-dispersible if desired. Such polymers are well-known in the coating industry and include a wide variety of polymers.
The polymers preferably include reactive functionalities that are capable of reacting with the aforementioned reactive diluent(s). One such preferred polymer includes ethylenic unsaturation and, when cured, provides a hard, durable coating. Such ethylenic unsaturation is preferably in the form of (meth)acrylate or auto-oxidative carbon-carbon double bonds.
Suitable water-dispersible polymers include polyurethanes, epoxies, polyamides, chlorinated polyolefins, acrylics, oil-modified polymers, polyesters, and mixtures or copolymers thereof, for example. Such polymers are readily synthesized and made to be water dispersible using conventional techniques. For example, the incorporation of amine or acid functionality produces water dispersibility.
Oil-modified polymers can also be used if desired, whether water dispersible or not. As used herein, oil-modified polymers are broadly defined to include polymers that contain oils and/or oil based derivatives such as glyceride oils (monoglycerides, diglycerides, and the like), fatty acids, fatty amines, and mixtures thereof. Examples of such oil-modified polymers include, alkyds, oil-modified polyurethanes, oil-modified epoxies, oil-modified polyamides, oil-modified acrylics, and mixtures or copolymers thereof. Preferably, the oil-modified polymer is an oil-modified polyurethane or an alkyd. Such polymers are readily synthesized and can be made to be water dispersible if desired using conventional techniques.
Water-dispersible polyurethanes are particularly preferred. These polymers may be made in a variety of ways. One suitable method includes reacting one or more isocyanates with one or more hydroxy-functional compounds. Preferred such polymers include ethylenic unsaturation as well as salt-forming functionality. The ethylenic unsaturation can be introduced into a polyurethane, for example, by reacting the aforementioned isocyanate with a hydroxy-functional acrylate, methacrylate, allyl ether, vinyl ether, monoglyceride, diglyceride, an ester polyol, or oil-modified polymers. The preferred oil-modified polymer useful in preparing an ethylenic unsaturated water-dispersible polyurethane is an alkyd. Preferred ethylenically unsaturated polyurethanes include (meth)acrylate or auto-oxidative carbon-carbon double bond functionality.
Suitable isocyanates include diisocyanates, triisocyanates, and other polyisocyanates. Preferred polyisocyanates for practicing the invention are polyisocyanates having 4 to 25 carbon atoms and from 2 to 4 isocyanate groups per molecule. Examples of isocyanates are those conventionally used in making polyurethanes, including aliphatic, cycloaliphatic, aromatic isocyanates, and mixtures thereof.
Suitable hydroxy-functional ethylenically unsaturated compounds for reaction with the isocyanate include hydroxy-functional (meth)acrylates. Examples of suitable hydroxy-functional (meth)acrylates include alkyl and cycloalkyl hydroxy-functional (meth)acrylates, such as 2-hydroxyethyl (meth)acrylates, 3-hydroxypropyl (meth)acrylates, 4-hydroxybutyl (meth)acrylates, 2-hydroxy-2-methylethyl (meth)acrylates, and 4-hydroxycyclohexyl (meth)acrylates, as well as other similar hydroxy-functional aliphatic (meth)acrylates. Other suitable hydroxy-functional (meth)acrylates include hydroxy-functional (meth)acrylate polyesters such as caprolactone 2-((meth)acryloyloxy)ethyl esters, dicaprolactone 2-((meth)acryloyloxy)ethyl esters, and higher molecular weight caprolactone homologues, and hydroxy-functional (meth)acrylate polyethers.
Another type of hydroxy-functional ethylenically unsaturated compound for use in making polyurethanes is a hydroxy-functional (meth)allyl ether. Suitable hydroxy-functional (meth)allyl ethers include at least one hydroxyl group and one or more allyl ether groups, such as hydroxyethyl allyl ether, hydroxypropyl allyl ether, trimethylolpropane monoallyl ether, trimethylolpropane diallyl ether, trimethylolethane monoallyl ether, trimethylolpropane dimethallyl ether, and the like.
Vinyl ethers may also be utilized in making ethylenically unsaturated polyurethanes. A suitable vinyl ether compound includes at least one hydroxyl group and one or more vinyl ether groups. Examples of suitable vinyl ethers include 4-hydroxybutyl vinyl ether, cyclohexanedimethanol monovinyl ether, ethylene glycol monovinyl ether, diethylene glycol monovinyl ether, and the like.
Ethylenic unsaturation can also be incorporated into a polyurethane via reaction with an ester polyol made by reaction of an aromatic or aliphatic polyol containing at least two hydroxyl groups per molecule with a fatty acid wherein a portion of the fatty acid contains auto-oxidative carbon-carbon double bonds. Suitable polyols include ethylene glycol, ethylene glycol, propylene glycol, 1,3 propane diol, 1,3 butylene glycol, 1,4 butane diol, Bisphenol A, trimethylol propane, trimethylol ethane, pentaerythritol, glycerin, neopentyl glycol, and cyclohexane dimethanol, and mixtures thereof. Suitable unsaturated fatty acids include linoleic, palmitoleic, linolenic, eleostearic, arachidonic, ricinoleic acids, 10,12-octadecadienoic acid, and mixtures thereof.
Polyurethanes containing ethylenic unsaturation can also be developed by utilizing the reaction product formed via transesterification of an oil, containing auto-oxidative carbon-carbon double bonds, with an aromatic or aliphatic polyol containing at least two hydroxyl groups per molecule. Suitable oils include linseed oil, soybean oil, safflower oil, tall oil, sunflower oil, dehydrated caster oil, castor oil, ricine oil, tung oil, sardine oil, olive oil, cottonseed oil and mixtures thereof. Suitable polyols include ethylene glycol, propylene glycol, 1,3 propane diol, 1,3 butylene glycol, 1,4 butane diol, Bisphenol A, trimethylol propane, trimethylol ethane, pentaerythritol, glycerin, neopentyl glycol, and cyclohexane dimethanol, and mixtures thereof.
Oil-modified polymers, preferably, hydroxyl-functional alkyds can also be used to develop ethylenic unsaturated polyurethanes. Alkyds can be prepared by any method known in the art. An example of a method to prepare an alkyd includes the transesterification of an oil and polyol with a further reaction with polybasic acids and optionally, further polyols. In addition, polybasic acids and fatty acids can be reacted with polyols in suitable proportions. The reaction of the polyols with polybasic acids and fatty acids and/or oils can be catalyzed by transesterification catalysts such as calcium naphthenate, lithium neodecanoate, zinc acetate, tin oxide and the like. A color stabilizer such as trisnonyl phenyl phosphite may also be added.
Suitable oils and/or fatty acids derived therefrom that are useful in making an alkyd or other oil-modified polymer include compounds such as, for example, linseed oil, safflower oil, tall oil, cotton seed oil, ground nut, wood oil, tung oil, ricine oil, sunflower oil, soya oil, castor oil, dehydrated castor oil, coconut oil, sardine oil, olive oil, and the like. These oils and/or fatty acids can be used alone or as a mixture of one or more of the oils and/or fatty acids.
Suitable polyols useful in making an alkyd include compounds such as, for example, aliphatic, cycloaliphatic and/or araliphatic alcohols having 1 to 6, preferably 1 to 4, hydroxy groups attached to nonaromatic or aromatic carbon atoms, such as, for example, ethylene glycol, propylene glycol, 1,3 propane diol, 1,3 butylene glycol, 1,4 butane diol, Bisphenol A, trimethylol propane, trimethylol ethane, pentaerythritol, glycerin, neopentyl glycol, and cyclohexane dimethanol. These compounds can be used alone or as a mixture of one or more polyols.
Suitable polybasic acids useful in making an alkyd include compounds such as, for example, aliphatic, cycloaliphatic saturated or unsaturated and/or aromatic polybasic carboxylic acids, such as, for example, dicarboxylic, tricarboxylic, and tetracarboxylic acids. Polybasic acids are broadly defined to include anhydrides of the polybasic acids such as, for example, maleic anhydride, phthalic anhydride, succinic anhydride, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, trimellitic anhydride, or mixtures thereof. These compounds can be used alone or as a mixture of one or more polybasic acids.
Alkyds can also be prepared by reacting polybasic acids with a compound containing an amine to provide an amide containing alkyd. Examples of suitable amines include ethylene diamine, diethylene triamine, triethylene tetra amine, and melamine 1,2-diamino propane, 1,3-diamino propane, and the like; or amino alcohols such as, for example, 2-amino-propan-1-ol, 3-amino-propan-1-ol, dimethylisopropanolamine, 2-amino-2-methyl-1-propanol, dimethylethanolamine, and the like. These amide containing alkyds can be designed to be amine and/or hydroxy functional and subsequently could be useful in making a water dispersible polyurethane polymer.
Conventionally, to facilitate manufacture, the polyurethane prepolymer can be made in the presence of a solvent that is either left in the dispersion, or removed as one of the last steps in production to provide a low solvent or solvent-free product. Solvents that can be easily removed, are usually volatile solvents, such as acetone or methyl ethyl ketone. In place of such solvents (or a portion of such solvents), however, one or more reactive diluents as described above are used.
Chain extenders can also be used in the preparation of urethane polymers. Examples of chain extenders include an alkyl amino alcohol, cycloalkyl amino alcohol, heterocyclic amino alcohol, polyamine (e.g., ethylene diamine, diethylene triamine, etc.), hydrazine, substituted hydrazine, hydrazide, amide, water or mixtures thereof.
In general, for water dispersibility, acid salt forming groups can be introduced into the polymer by a number of methods. For example, a water-dispersible polyurethane can be made by reacting a suitable compound (e.g., a polyisocyanate) with a compound containing active hydrogen and active acid groups neutralized by a neutralizing base. Suitable compounds having active hydrogen and active acid groups include hydroxy and mercapto carboxylic acids, aminocarboxylic acids, aminohydroxy carboxylic acids, sulfonic acids, hydroxy sulfonic acids, and aminosulfonic acids. Suitable neutralizing bases include inorganic bases such as sodium hydroxide, potassium hydroxide, lithium hydroxide, ammonia, triethylamine, and dimethyl ethanol amine.
Alternatively, for water dispersibility, basic salt forming groups can be introduced into the polymers by reacting a suitable compound (e.g., a polyisocyanate) with a compound containing active hydrogen groups and active basic groups neutralized with an acid. Suitable compounds having active hydrogen groups and active basic groups include aliphatic, cycloaliphatic and heterocyclic amino alcohols, diols and triols, amines, diamines, triamines, tetramines, and amides. Suitable neutralizing acids include organic acids such as formic acid and acetic acid, and inorganic acids such as hydrochloric acid and sulfuric acid.
For example, urethanes can be made water-dispersible by incorporating amine or acid functionality. For example, water-based anionically stabilized polyurethane polymers are prepared by reacting polyols and dihydroxy carboxylic acid compounds with an excess of diisocyanate to provide a carboxylic acid functional prepolymer having NCO terminal groups. The acid groups can be neutralized with tertiary amines to provide salt groups. The neutralized prepolymer can be readily dispersed in water. Alternatively, the anionic stabilizing group of the water-dispersible polyurethane polymers can be replaced with cationic stabilizing groups or non-ionic stabilizing groups, to facilitate water dispersibility.
Suitable additives for use in coating compositions of the present invention are described in Koleske et al., Paint and Coatings Industry, April, 2003, pages 12-86.
Certain embodiments of the present invention, particularly those with (meth)acrylate functional groups in the polymers and/or reactive diluents of the coating compositions, include polymers that are curable by UV or visible light. These coating compositions typically include a free-radical initiator, particularly a photoinitiator that induces the curing reaction upon exposure to light. The photoinitiator makes up about 0.1-10 wt-% of the coating composition.
Among photoinitiators suitable for use in the present invention with resins having (meth)acrylate or allyl ether functional groups are alpha-cleavage type photoinitiators and hydrogen abstraction type photoinitiators. The photoinitiator may include other agents such as a coinitiator or photoinitiator synergist that aid the photochemical initiation reaction. Suitable cleavage type photoinitiators include alpha, alpha-diethoxyacetophenone (DEAP), dimethoxyphenylacetophenone (commercially available under the trade designation IRGACURE 651 from Ciba Corp., Ardsley, N.Y.), hydroxycyclohexylphenylketone (commercially available under the trade designation IRGACURE 184 from Ciba Corp.), 2-hydroxy-2-methyl-1-phenylpropan-1-one (commercially available under the trade designation DAROCUR 1173 from Ciba Corp.), a 25:75 blend of bis-(2,6-dimethoxybenzoyl)-2,4,4-trimethylpentyl phosphine oxide and 2-hydroxy-2-methyl-1-phenylpropan-1-one (commercially available under the trade designation IRGACURE 1700 from Ciba Corp.), a 50:50 blend of 2-hydroxy-2-methyl-1-phenylpropan-1-one and 2,4,6-trimethylbenzoyl-diphenylphosphine oxide (TPO, commercially available under the trade designation DAROCUR 4265 from Ciba Corp.), phosphine oxide, 2,4,6-trimethyl benzoyl (commercially available under the trade name IRGACURE 819 and IRGACURE 819DW from Ciba Corp.), 2,4,6-trimethylbenzoyl-diphenylphosphine oxide (commercially available under the trade designation LUCIRIN from BASF Corp., Mount Olive, N.J.), and a mixture of 70% oligo 2-hydroxy-2-methyl-4-(1-methylvinyl)phenylpropan-1-one and 30% 2-hydroxy-2-methyl-1-phenylpropan-1-one) (commercially available under the trade designation KIP 100 from Sartomer, Exton, Pa.). Suitable hydrogen abstraction-type photoinitiators include benzophenone, substituted benzophenones (such as that commercially available under the trade designation ESCACURE TZT from Fratelli-Lamberti, sold by Sartomer, Exton, Pa.), and other diaryl ketones such as xanthones, thioxanthones, Michler's ketone, benzil, quinones, and substituted derivatives of all of the above. Preferred photoinitiators include DAROCUR 1173, KIP 100, benzophenone, and IRGACURE 184. A particularly preferred initiator mixture is commercially available under the trade designation IRGACURE 500 from Ciba Corp., which is a mixture of IRGACURE 184 and benzophenone, in a 1:1 ratio. This is a good example of a mixture of an alpha-cleavage type photoinitiator and a hydrogen abstraction-type photoinitiator. Other mixtures of photoinitiators may also be used in the coating compositions of the present invention. Camphorquinone is one example of a suitable photoinitiator for curing a coating composition with visible light.
A coating composition of the present invention can also include a coinitiator or photoinitiator synergist. The coinitiators can be tertiary aliphatic amines (such as methyl diethanol amine and triethanol amine), aromatic amines (such as amylparadimethylaminobenzoate, 2-n-butoxyethyl-4-(dimethylamino) benzoate, 2-(dimethylamino)ethylbenzoate, ethyl-4-(dimethylamino)benzoate, and 2-ethylhexyl-4-(dimethylamino)benzoate, (meth)acrylated amines (such as those commercially available under the trade designations EBECRYL 7100 and UVECRYL P104 and P115, all from UCB RadCure Specialties, Smyrna, Ga.), and amino-functional acrylate or methacrylate resin or oligomer blends (such as those commercially available under the trade designations EBECRYL 3600 or EBECRYL 3703, both from UCB RadCure Specialties). Combinations of the above categories of compounds may also be used.
Coating compositions having resins with vinyl ether functional groups can be cured by UV or visible light using cationic-generating photoinitiators. Examples of suitable cationic-generating photoinitiators include super acid-generating photoinitiators, such as triarylsulfonium salts. One useful triarylsulfonium salt is triphenyl sulfonium hexafluorophosphate.
Many coating compositions that may be cured by UV or visible light may also be cured with an electron beam. Techniques and devices for curing a coating composition using an electron beam are known in the art. These techniques do not require a photoinitiator for electron beam cure of the coating.
Coating compositions having polymer resins with (meth)acrylate and/or allyl functional groups may also be thermally cured using a suitable initiator. The thermal initiator typically facilitates the curing process by a free radical mechanism and typically includes a peroxide or azo compound. Peroxide compounds suitable for use as initiators in the coating compositions of the present invention include t-butyl perbenzoate, t-amyl perbenzoate, cumene hydroperoxide, t-amyl peroctoate, methyl ethyl ketone peroxide, benzoyl peroxide, cyclohexanone peroxide, 2,4-pentanedione peroxide, di-t-butyl peroxide, t-butyl hydroperoxide, and di-(2-ethylhexyl)-peroxydicarbonate. Suitable azo compounds which may be employed as an initiator in the present compositions include 2,2-azo bis-(2,4-dimethylpentane-nitrile), 2,2-azo bis-(2-methylbutanenitrile), and 2,2-azo bis-(2-methylpropanenitrile).
For coating compositions having a mixture of (meth)acrylate, allyl ether, and vinyl ether functional groups, a combination of curing procedures may be used. For example, a coating composition having a resin with both (meth)acrylate and vinyl ether functional groups typically includes an alpha-cleavage type and/or hydrogen abstraction type photoinitiator for the (meth)acrylate groups and a cationic-generating photoinitiator for the vinyl ether groups.
Other methods for curing the coating compositions of the invention can be used alone or in combination with methods described hereinabove. Supplemental curing methods include heat cure, chemical cure, anaerobic cure, moisture cure, oxidative cure, and the like. Each method of cure requires a corresponding curing initiator or curing agent, which is included in the composition. For example: heat cure can be induced by peroxides; metal drier packages can induce an oxidative cure; multifunctional amines (for example isophorone diamine) can effect a chemical crosslinking cure through Michael addition of amine groups onto acrylate reactive unsaturated groups. If these additional initiators are present in the coating composition they typically make up 0.1-12% by weight of the curable coating composition. Means for effecting cures by such methods are known to those of skill in the art or can be determined using standard methods.
Certain coating compositions of the invention also can include metal driers. Typical driers include, for example, cobalt, manganese, lead, zirconium, calcium, cerium, lanthanum, and neodymium salts or combinations thereof. Metal driers can be used in combination with accelerators for certain embodiments. For example, water-dispersible polyurethane-polyethylene compositions can also include compounds such as, for example, 1,10-phenanthroline, bipyridine, and the like, which function as accelerators in combination with the metal driers.
Certain coating compositions of the present invention may also include one or more of a group of ingredients that can be called performance enhancing additives. Typical performance enhancing additives that may be employed include surface active agents, pigments, colorants, dyes, surfactants, thickeners, heat stabilizers, leveling agents, anti-cratering agents, curing indicators, plasticizers, fillers, sedimentation inhibitors, ultraviolet-light absorbers, optical brighteners, and the like to modify properties.
Coating compositions may include a surface-active agent that modifies the interaction of the curable coating composition with the substrate, in particular, the agent can modify the ability of the composition to wet a substrate. Surface active agents may have other properties as well. For example, surface active agents may also include leveling, defoaming, or flow agents, and the like. The surface active agent affects qualities of the curable coating composition including how the coating composition is handled, how it spreads across the surface of the substrate, and how it bonds to the substrate. The surface active agent may make up 0-5% by weight of the curable coating composition.
Surface active agents suitable for use in coating compositions are known to those of skill in the art or can be determined using standard methods. Exemplary surface active agents include polydimethylsiloxane surface active agents (such as those commercially available under the trade designations SILWET L-760 and SILWET L-7622 from OSI Specialties, South Charleston, W.Va., or BYK 306 from Byk-Chemie, Wallingford, Conn.) and fluorinated surface active agents (such as that commercially available as FLUORAD FC-430 from 3M Co., St. Paul, Minn.). The surface active agents may include a defoamer. Suitable defoamers include polysiloxane defoamers (such as a methylalkylpolysiloxane like that commercially available under the trade designation BYK 077 or BYK 500 from Byk-Chemie) or polymeric defoamers (such as that commercially available under the trade designation BYK 051 from Byk-Chemie).
For some applications, a coating that is opaque, colored, pigmented or has other visual characteristics is desired. Agents to provide such properties can also be included in coating compositions of the present invention. Pigments for use with the present invention are known in the art. Suitable pigments include titanium dioxide white, carbon black, lampblack, black iron oxide, red iron oxide, yellow iron oxide, brown iron oxide (a blend of red and yellow oxide with black), phthalocyanine green, phthalocyanine blue, organic reds (such as naphthol red, quinacridone red and toulidine red), quinacridone magenta, quinacridone violet, DNA orange, and/or organic yellows (such as Hansa yellow). The composition can also include a gloss control additive or an optical brightener, such as that commercially available under the trade designation UVITEX OB from Ciba-Geigy.
In certain embodiments it is advantageous to include fillers or inert ingredients in the coating composition. Fillers and inert ingredients include, for example, clay, glass beads, calcium carbonate, talc, silicas, organic fillers, and the like. Fillers extend, lower the cost of, alter the appearance of, or provide desirable characteristics to the composition before and after curing. Suitable fillers are known to those of skill in the art or can be determined using standard methods. Fillers or inert ingredients can make up from 0.1-40% by weight of the coating composition.
The invention may also include other ingredients that modify properties of the curable coating composition as it is stored, handled, or applied, and at other or subsequent stages. Waxes, flatting agents, mar and abrasion additives, and other similar performance enhancing additives may be employed in this invention as required in amounts effective to upgrade the performance of the cured coating and the coating composition. Desirable performance characteristics of the coating include chemical resistance, abrasion resistance, hardness, gloss, reflectivity, appearance, or combinations of these characteristics, and other similar characteristics.
DMPA—Dimethylolpropionic acid (GEO, Allentown, Pa.) DiTMPTA—Di-trimethylolpropane tetraacrylate (Sartomer, Exton, Pa.) 4-HBA—4-Hydroxy butylacrylate (Aldrich, Milwaukee, Wis.) TMP—Trimethylol Propane (Aldrich) DESMOPHEN S-105-110—Polyester diol (Bayer, Pittsburgh, Pa.) TEA—Triethyl Amine (Aldrich) DBTDL—Dibutyl Tin Dilaurate (Air Products, Allentown, Pa.) Example 1
Preparation of (meth)acrylate Functional Polyurethane Dispersion (PUD) with DiTMPTA Reactive Diluent
A reactor was charged with 96.0 parts DiTMPTA, 48.0 parts 4-HBA, 91.4 parts DESMOPHEN S-105-110 polyester diol, 29.3 parts DMPA, 9.6 parts TMP, an amount of a diisocyanate, and 500 ppm of 2,6 di-tert-butyl-4-methylphenol. The reaction mixture was heated to 80° C. under an air sparge, where upon 250 ppm DBTDL was added and the reaction processed until the isocyanate level was below 9.2%. The urethane polymer was cooled to 65° C. and then neutralized with 22.1 parts TEA. The urethane polymer viscosity at 65° C. was 6,000 centipoise (cps) as measured by a Brookfield DV-I+ Viscometer and a Number 31 spindle at 1.5 revolutions per minute (RPM).
At a process temperature of 65° C., the (meth)acrylate urethane polymer formed above was then dispersed into 895.5 parts room temperature deionized water and subsequently chain extended with 51.1 parts hydrazine (35% in water). The dispersion was then adjusted to 35% solids with deionized water.
The physical properties of the chain extended (meth)acrylate functional polyurethane dispersion were as follows (NVM %=nonvolatile material by weight):
NVM %
% VOC
1.4% (TEA)
UV Curable Coating Composition with DiTMPTA Containing (meth)acrylate Functional PUD
Under agitation to a stainless steel mixing vessel was added 85 parts of the dispersion from Example 1, 0.85 part, IRGACURE 500 from Ciba, 8.05 parts deionized water, 5.00 parts DOWANOL DPM from Dow Chemical, 1.00 part SURFYNOL 104PA from Air Products, and 0.10 part BYK 333 from BYK Chemie. A 3-mil thick (0.00762-cm) wet film was then applied to a Leneta Form 7B test chart and air dried for 15 minutes followed by force dry for 5 minutes at 65° C. The dried (meth)acrylate polymer film was then cured by mercury ultraviolet lamps. Total UV exposure was 1000 millijoules per square centimeter (mj/cm2).
Performance properties are outlined below. Gloss is reported in accordance with ASTM test specification, D-523. All other cured film properties are reported on a scale of 1-10, with 10 being no effect or best.
Gloss 60 degree measurement
1 hour Exposure to mustard
1 hour exposure to 100 proof
100 MEK double rubs
180 degree flexibility
Fingernail mar
Gloss measurement was performed with a Micro-Gloss 60 from BYK Gardner in accordance with ASTM test method D-523.
1-Hour spot test exposure to 100 proof vodka and to mustard were performed in accordance with ASTM test method D-1308.
MEK double rub testing was performed in accordance with ASTM test method D-5402.
180-Degree flexibility was performed by bending the test chart 180 degrees around a ½ inch (1.27 cm) diameter rod and visually looking for film cracking.
Fingernail mar was performed by rubbing the back of the fingernail softly across the cured coating and looking for surface mar.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3125592Jun 26, 1961Mar 17, 1964 Preparation of polymerizable vinylatedUS3297745Apr 5, 1962Jan 10, 1967Robertson Co H HEthylenically unsaturated di-and tetra-urethane monomersUS3373075Dec 17, 1963Mar 12, 1968Robertson Co H HDiacrylate compositions, heat resistant polymers containing the same and method of making electrical laminates therefromUS3380831May 26, 1964Apr 30, 1968Du PontPhotopolymerizable compositions and elementsUS3530100Sep 26, 1966Sep 22, 1970Ppg Industries IncCrosslinking polymersUS3551246Nov 24, 1967Dec 29, 1970Sun Chemical CorpRadiation curable compositionsUS3560237Apr 15, 1968Feb 2, 1971Weyerhaeuser CoProcess of curing polymerizable resins having terminal vinyl ester groups using high energy electronsUS3567494Aug 29, 1968Mar 2, 1971Continental Can CoProcess for preparing polymerized surface coatings using ultra-violet radiationUS3673140Jan 6, 1971Jun 27, 1972Inmont CorpActinic radiation curing compositions and method of coating and printing using sameUS3676398Nov 25, 1968Jul 11, 1972Ppg Industries IncPolymerizable crosslinkable esters of polyepoxy compoundsUS3700643Sep 2, 1970Oct 24, 1972Union Carbide CorpRadiation-curable acrylate-capped polycaprolactone compositionsUS3759809Nov 14, 1972Sep 18, 1973Sun Chemical CorpRadiation curable compositions comprising an isocyanate modified polyfunctional ester and a photoinitiatorUS3876518Mar 22, 1973Apr 8, 1975Union Carbide CorpAcrylated epoxidized soybean oil amine compositions and method of curing sameUS3878077Mar 22, 1973Apr 15, 1975Union Carbide CorpRadiation curable compositions of acrylated epoxidized soybean oil amine compounds useful as inks and coatings and methods of curing sameUS3935173Mar 18, 1974Jan 27, 1976Toagosei Chemical Industrial Co. Ltd.Curable compositionsUS4906684Dec 9, 1988Mar 6, 1990Rtz Chemicals, Ltd.Ambient temperature curing polymer compositions containing acetoacetoxyethyl methacrylate, glycidyl methacrylate and a polymerizable acidUS5026771 *Aug 3, 1989Jun 25, 1991Monsanto CompanyCoating compositions containing ethylenically unsaturated carbamatesUS5047270 *Sep 14, 1988Sep 10, 1991Idemitsu Petrochemical Company LimitedCoated resin molded-articleUS5089376Jun 13, 1989Feb 18, 1992Armstrong World Industries, Inc.Photoimagable solder mask coatingUS5290663 *Mar 1, 1991Mar 1, 1994W. R. Grace & Co.-Conn.Photocurable polyurethane-acrylate ionomer compositions for aqueous developable printing platesUS5371148 *Jun 23, 1993Dec 6, 1994Union Carbide Chemicals & Plastics Technology CorporationReactive polymers having pendant flexible side chains prepared from ethylenically unsaturated carbodiimidesUS5484849Dec 30, 1994Jan 16, 1996Rohm And Haas CompanyAir curing polymer compositionUS5543557Nov 29, 1994Aug 6, 1996Perstorp AbAcrylate monomer having a reduced primary irritation index and a method of making sameUS5562953Nov 18, 1994Oct 8, 1996Rohm And Haas CompanyMethod for light-assisted curing of coatingsUS6048471Feb 12, 1998Apr 11, 2000Richard G. HenryZero volatile organic compound compositions based upon organic solvents which are negligibly reactive with hydroxyl radical and do not contribute appreciably to the formation of ground based ozoneUS6075088Nov 1, 1994Jun 13, 2000Fina Research S.A.Alkyd paintsUS6162842May 18, 1999Dec 19, 2000The Goodyear Tire & Rubber CompanyRadiation curable coating compositionUS6197844Sep 13, 1996Mar 6, 20013M Innovative Properties CompanyFloor finish compositionsUS6462127 *Dec 17, 1999Oct 8, 2002Skw Bauchemie GmbhSelf-crosslinking polyurethane polymer hybrid dispersionUS6747088 *Sep 29, 2000Jun 8, 2004Basf AktiengesellschaftAqueous polyurethane dispersions which can be hardened with mit UV-radiation and thermally, and use thereofUS6987135Oct 25, 2001Jan 17, 2006Akzo Nobel N.V.Photoactivatable water borne coating compositionUS6997980 *Dec 20, 2001Feb 14, 2006Basf Coatings AgAqueous, effect-producing coating material, method for the production thereof and use of the sameUS20020156145Oct 25, 2001Oct 24, 2002Van Den Berg Keimpe JanPhotoactivatable water borne coating compositionUS20020164434Sep 13, 1999Nov 7, 2002Michael TarvinUltra violet light curable floor coating with coloring agentUS20030228424 *Mar 6, 2003Dec 11, 2003Dove Clive NicholasWater borne coating composition for film transfer and casting processUS20050192400Nov 22, 2004Sep 1, 2005Valspar Sourcing, Inc.Coating compositions containing reactive diluents and methodsUS20060111503Nov 17, 2005May 25, 2006Valspar Sourcing, Inc.Coating compositions and methodsDE4440819A1Nov 15, 1994May 24, 1995Ciba Geigy AgPhotosensitive compsn. with low curl factor useful for stereo-lithographyEP0486278A1Nov 13, 1991May 20, 1992Rohm And Haas CompanyAqueous-based radiation-curable coating compositionEP0492847A2Dec 4, 1991Jul 1, 1992Rohm And Haas CompanyAir curing polymer compositionEP0492847B1Dec 4, 1991Jan 22, 1997Rohm And Haas CompanyAir curing polymer compositionEP0492847B2Dec 4, 1991Nov 20, 2002Rohm And Haas CompanyAir curing polymer compositionEP0651039A1Oct 28, 1994May 3, 1995Fina Research S.A.Alkyd paintsEP0939109A1Feb 26, 1999Sep 1, 1999Fujikura Kasei Co., Ltd.UV curable resin composition for coatingEP0965621A1Jun 10, 1999Dec 22, 1999Basf AktiengesellschaftRadiation curable masses containing phenylglyoxylic derivatesGB1541891A Title not availableJPH01168767A Title not availableJPS5397083A Title not availableJPS5778468A Title not availableWO1993016133A2Feb 9, 1993Aug 19, 1993S.C. Johnson & Son, Inc.Crosslinkable surface coatingsWO2001023453A1Sep 29, 2000Apr 5, 2001Basf AktiengesellschaftAqueous polyurethane dispersions which can be hardened with mit uv-radiation and thermally, and use thereofWO2001027181A1Oct 13, 2000Apr 19, 2001Dsm N.V.Radiation-curable coating compositionWO2002034808A1Oct 25, 2001May 2, 2002Akzo Nobel N.V.Photoactivatable water borne coating compositionWO2002053658A2 *Dec 20, 2001Jul 11, 2002Basf Coatings AgAqueous, effect-producing coating material, method for the production thereof and use of the sameWO2006057875A1Nov 17, 2005Jun 1, 2006Valspar Sourcing, Inc.Coating composition and methods* Cited by examinerNon-Patent CitationsReference1"Draize test," Wikipedia [online]. [retrieved on Oct. 22, 2008]. -test>; 6 pgs. (Page last modified Oct. 5, 2008).2"Sartomer Company Material Safety Data Sheet- Product SR295" datasheet. Sartomer Company, Inc., Exton, PA, revised: Jul. 27, 2005 (replaces data sheet of Oct. 5, 2004), printed Jul. 27, 2005, 7 pgs.3"Sartomer Safety Data Sheet-Craynor 132" datasheet. Cray Valley, Ríeux, France, version: Jul. 15, 2002 (supersedes datasheet of Dec. 1, 1999), printed Aug. 4, 2005, 5 pgs.4"Trimethylolpropane trimethacrylate," datasheet [online]. chemBlink Inc., Cary, NC, (C) 2008 [retrieved on Oct. 21, 2008]. Retrieved from the Internet:; 2 pgs.5Australian Office Action dated Apr. 9, 2009 for Australian Patent Application No. 2004248127; 4 pgs.6Database WPI Week 198932, Derwent Publications Ltd., London, GB: AN 1989-23274, XP002325321 "Active energy ray cure coating composition" and JP 01 168767 A (Toyo INK) Jul. 4, 1989, Abstract.7Draize et al., "Methods for the Study of Irritation and Toxicity of Substances Applied Topically to the Skin and Mucous Membranes," J. Pharmacol. Exp. Ther., 1944; 82(3):377-390.8European Office Action dated Feb. 7, 2007 for European Patent Application No. 04 753 568.7-1214; 4 pgs.9European Office Action dated Sep. 15, 2009 for European Patent Application No. 04 753 568.7-1214; 5 pgs.10Koleske et al., Paint and Coatings Industry, 2003 Additives Guide, Apr. 2003, pp. 12-86.11Patent Abstracts of Japan. vol. 006, No. 158 (C-120), Aug. 19, 1982, and JP 57 078468 A (Dainippon Printing Co. Ltd), May 17, 1982 Abstract.12Product Data Sheet, Alberdingk Boley, Inc., Greensboro, N.C., Alberdingk(R) LUX 399 UV-Dispersion, Published Aug. 22, 2002, 2 pgs.13Safety Data Sheet, Alberdingk Boley, Inc., Greensboro, N.C., Alberdingk(R) LUX 399 UV-Dispersion, Published May 19, 2004, 4 pgs.14U.S. Appl. No. 10/994,750, filed Nov. 22, 2004, Killilea et al.15U.S. Appl. No. 11/281,167, filed Nov. 17, 2005, Killilea et al.16U.S. Federal Register, vol. 60, No. 116, Jun. 16, 1995, pp. 31633-31637.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS8846786Oct 9, 2009Sep 30, 2014Allnex Belgium S.A.Aqueous dispersed polyester resin compositionsUS9469780Sep 11, 2009Oct 18, 2016Valspar Sourcing, Inc.Coating compositions containing reactive diluents and methodsUS9597653Nov 19, 2013Mar 21, 2017Allnex Belgium S.A.Process for the preparation of colloidal polymerized particlesUS20070244289 *Apr 13, 2006Oct 18, 20073M Innovative Properties CompanyMethod of making urethane based fluorinated monomersUS20100004376 *Sep 11, 2009Jan 7, 2010Valspar Sourcing, Inc.Coating compositions containing reactive diluents and methodsUS20100249317 *Apr 20, 2010Sep 30, 2010Valspar Sourcing, Inc.Coating compositions containing reactive diluents and methodsUS20110217478 *Oct 9, 2009Sep 8, 2011Cytec Surface Specialities S.A./N.V.Aqueous dispersed polyester resin compositionsEP2365036A1Mar 12, 2010Sep 14, 2011Cytec Surface Specialties, S.A.Radiation curable aqueous coating compositionsEP2735365A1Nov 21, 2012May 28, 2014Allnex Belgium, S.A.Process for the preparation of colloidal polymerized particles.WO2011110495A1Mar 4, 2011Sep 15, 2011Cytec Surface Specialties, S.A.Radiation curable aqueous coating compositions* Cited by examinerClassifications U.S. Classification525/50, 525/437, 525/213, 524/839, 525/419, 524/590, 524/845, 525/123, 525/55, 524/833, 525/191, 524/834, 525/420, 525/54.4, 525/416, 525/197, 525/403, 524/840, 525/418, 524/507, 524/591, 525/199, 525/198, 525/330.1International ClassificationC08L27/00, C08J3/00, C08L27/12, C08G18/08, C08G65/00, C08L35/00, C08L27/04, C08F8/00, C08L33/00, C08G73/10, C08L75/00, C08L67/00, C08G61/02, C09D11/10, C08G18/67, C08L31/00, C08K3/20, C09D175/16, C08L71/02, C08F8/30, C08F8/14, C08L79/00, C08C19/08, C08F220/18, C08G65/32, C08F283/00, C08F283/04, C08L77/00, C08L11/02, C08F290/14, C08G63/91Cooperative ClassificationC08J2375/16, C08J3/24, C09D175/16, C09D175/14, C09D167/08, C09D7/001, C09D4/00, C08J3/246, C08G18/672, C08F290/147, C08F290/141, C08F290/067, C08F290/061, C08F283/01, C08F242/00, C08F8/00European ClassificationC08G18/67B4, C09D175/16Legal EventsDateCodeEventDescriptionOct 22, 2004ASAssignmentOwner name: VALSPAR SOURCING, INC., MINNESOTAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KILLILEA, T. HOWARD;BOHANNON, JAMES M.;REEL/FRAME:015280/0262;SIGNING DATES FROM 20040601 TO 20040827Oct 5, 2010CCCertificate of correctionApr 22, 2013FPAYFee paymentYear of fee payment: 4Apr 20, 2017FPAYFee paymentYear of fee payment: 8RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services