Patent US4810523 - Pressure-sensitive adhesives - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign in<nobr>Advanced Patent Search</nobr>PatentsAcrylate-based pressure-sensitive adhesives are produced by a process in which a liquid, polymerizable monomer composition containing at least one acrylate monomer is placed in a closed reaction vessel, deaerated and the monomer(s) are polymerized by exposure to ionizing radiation such as gamma irradiation....http://www.google.com/patents/US4810523?utm_source=gb-gplus-sharePatent US4810523 - Pressure-sensitive adhesivesAdvanced Patent SearchPublication numberUS4810523 APublication typeGrantApplication numberUS 06/941,350Publication dateMar 7, 1989Filing dateDec 15, 1986Priority dateMay 6, 1985Fee statusLapsedPublication number06941350, 941350, US 4810523 A, US 4810523A, US-A-4810523, US4810523 A, US4810523AInventorsJeffrey D. Williams, Marvin L. Young, Syed S. Ahmad, Jackson A. RansohoffOriginal AssigneeNeutron Products, Inc.Export CitationBiBTeX, EndNote, RefManPatent Citations (18), Non-Patent Citations (2), Referenced by (35), Classifications (13), Legal Events (5) External Links: USPTO, USPTO Assignment, EspacenetPressure-sensitive adhesivesUS 4810523 AAbstract Acrylate-based pressure-sensitive adhesives are produced by a process in which a liquid, polymerizable monomer composition containing at least one acrylate monomer is placed in a closed reaction vessel, deaerated and the monomer(s) are polymerized by exposure to ionizing radiation such as gamma irradiation. The process allows for the direct production of low-solvent or solventless acrylate-based adhesives suitable for application by hot-melt techniques.
What is claimed is: 1. A process for preparing a substrate for bonding which comprises applying to the substrate by hot-melt application a pressure-sensitive adhesive which is produced by the process which comprises:(a) introducing, to a sealable reaction vessel, a liquid, polymerizable monomer composition, comprising:(i) from 65 to 100 parts of at least one acrylate monomer of the formula: ##STR3## wherein R1 is hydrogen or methyl and R2 is a straight or branched chain alkyl having from 2 to 8 carbon atoms, (ii) from 0 to 35 parts of at least one ethylenically unsaturated comonomer per 100 parts of liquid polymerizable monomer composition; and (b) dearating the liquid polymerizable monomer composition before or after introducing it into the vessel; and (c) polymerizing the monomers in the containers by exposing them to ionizing radiation, at a dose rate greater than 1 kilorad per hour and less than 1 kilorad per second, said polymerization being carried out in the presence of less than 30% by weight of an organic solvent, based on the combined weight of the liquid, polymerizable monomer composition and solvent, so as to produce a viscoelastic polymer mass having a low level of residual monomer and oapable of hot-melt application. 2. A process as claimed in claim 1, wherein the polymerization is carried out in the presence of less than 5% by weight of an organic solvent.
3. A process as claimed in claim 1, wherein the polymerization is carried out in the absence of solvent.
4. A process as claimed in claim 1, wherein the liquid, polymerizable monomer composition also contains from 0 to 4 parts of a chain transfer agent, per 100 parts of liquid, polymerizable monomer composition.
5. A process as claimed in claim 4, wherein the chain transfer agent is selected from isopropyl alcohol and triethanolamine.
6. A process as claimed in claim 1, wherein the liquid, polymerizable monomer composition is exposed to ionizing radiation at a predetermined dose rate in the range of 5 to 250 kilorads per hour.
7. A process as claimed in claim 1, wherein the ionizing radiation is gamma radiation.
8. A process as claimed in claim 1, wherein the liquid, polymerizable monomer composition is placed in a cylindrical container having a diameter of from about 1 inch to about 26 inches and exposed to gamma radiation.
9. A process as claimed in claim 1, wherein the acrylate monomer is selected from the group consisting of 2-ethylhexyl acrylate, n-butyl acrylate, isobutyl acrylate and ethyl acrylate.
10. A process as claimed in claim 1, wherein the ethylenically unsaturated comonomer is selected from the group consisting of acrylic acid, methacrylic acid, acrylonitrile, vinyl acetate and vinyl pyrrolidone.
11. A process as claimed in claim 1, wherein the acrylate monomer is 2-ethylhexyl acrylate.
12. A process as claimed in claim 1, wherein polymerization is carried out to obtain a polymer having an intrinsic viscosity of at least about 2.5 dl/g.
13. A process as claimed in claim 12, wherein the presure-sensitive adhesive is produced by homopolymerization of 2-ethylhexyl acrylate.
14. A process as claimed in claim 1, wherein the liquid, polymerizable monomer composition is exposed to ionizing radiation first at a dose rate in the range of 5 to 250 kilorads per hour and then at a different dose rate in the range of 1 kilorad per hour to 1 kilorad per second.
15. The process of claim 1 wherein the total dosage is between about 0.05 to about 100 kilorads.
16. A process as claimed in claim 1 wherein the total dosage is between about 13 to about 510 kilorads.
17. A process as claimed in claim 16 wherein the acrylate monomer is 2-ethylhexyl acrylate.
18. A process as claimed in claim 1 wherein the total dosage is between about 25 to about 300 kilorads.
19. A process as claimed in claim 1 wherein said viscoelastic polymer mass comprises at least about 95% polymer.
20. A process as claimed in claim 1 wherein said viscoelastic polymer mass comprises at least about 99.5% polymer.
This is a continuation of application Ser. No. 731,207, filed May 6, 1985, now abandoned.
This invention relates to the production of acrylate-based pressure-sensitive adhesives by polymerization which is initiated via exposure of monomers to ionizing radiation. The invention further relates to the production of such adhesives in a low-solvent or solventless form suitable for hot melt application.
Pressure-sensitive adhesives are materials which characteristically possess tack, that is bonding, when applied to adherents after brief contact at low pressure, develop greater bond strength with greater application pressure, yet desirably can be cleanly and easily removed from their adherents. Originally, pressure-sensitive adhesives, which were developed for self-adhering medical plasters and bandages, were based on natural rubber. Due to its high glass transition temperature, rubber does not possess pressure-sensitive adhesive properties at room temperature. Consequently, natural or synthetic rubbers must be compounded with a variety of tackifiers, such as terpenes or rosins, and often with other additives in order to function effectively as pressure-sensitive adhesives.
Pressure-sensitive adhesives produced from natural rubber dominated the field prior to World War II, a time when many pressure-sensitive adhesive products were developed. These include tapes for medical, electrical, packaging and processing applications, as well as self-adhering labeling, construction and decorative materials. Shortages of natural rubber led to the development of synthetic polymeric materials which found application in pressure-sensitive adhesives, including synthetic rubbers based on styrene-butadiene or styrene-isoprene polymers.
Additionally, there were developed a class of pressure-sensitive adhesives based on homopolymers or copolymers of acrylic acid esters. Acrylate-based pressure-sensitive adhesives offer some significant advantages over those based on natural or synthetic rubber. Due to their low glass transition temperatures, certain acrylate polymers have good tack at room temperature and can be used without the necessity of compounding with tackifying agents. Thus, acrylate-based products provide manufacturers of pressure-sensitive adhesive products with ready-to-coat pressure-sensitive adhesives, eliminating the need for in-house compounding operations.
Monomers useful in preparing acrylate-based pressure-sensitive adhesives are generally those having from 2 to 8 carbons in the ester group. Of particular importance are ethyl acrylate, n-butyl acrylate, isobutyl acrylate and 2-ethylhexyl acrylate. If desired, these monomers can be copolymerized with other ethylenically unsaturated monomers to yield satisfactory pressure-sensitive adhesives. Suitable comonomers include, for example, acrylic acid, methacrylic acid, vinyl acetate, vinyl pyrrolidone and vinyl ethers. If desired, difunctional or polyfunctional monomers, such as diacrylates, can also be copolymerized with the adhesive polymer in small amounts to impart cross-link density.
In order to be useful, a pressure-sensitive adhesive should have a balance of properties, e.g., tack, peel strength and creep resistance, best suited to the particular end use in which the adhesive is to be employed. The properties of a pressure-sensitive adhesive are primarily affected by monomer composition, molecular weight and cross-link density, all of which determine the balance of adhesivity and cohesivity in the polymer Generally, the monomer composition determines glass transition temperature and surface chemistry, both of which affect adhesion For linear polymers, higher molecular weights normally result in better cohesion. Cohesion also increases with the degree of covalent cross-linking and secondary intermolecular bonding
It is possible to produce a low molecular weight acrylate polymer which has good adhesivity but which will fail cohesively. Cohesivity can be improved by introducing cross-links into the polymer, after it has been applied to the substrate, by exposure to ultraviolet or ionizing radiation. However, high cross-link density can cause a loss of viscoelasticity, which in turn results in a loss of tack. In addition, many webbing substances have poor radiation resistance and are unable to tolerate doses required to impart good cohesivity.
In many commercial applications of pressure-sensitive adhesives, it would be preferred to use an acrylate polymer or copolymer having an intrinsic viscosity of at least about 2.5 dl/g. Unfortunately, prior art processes for producing acrylate polymers have been limited by considerations of reaction kinetics and thermodynamics to values below about 1.8 dl/g. Since various molecular weight fractions may affect adhesion and cohesion differently, molecular weight distribution, as well as average molecular weight, affects the properties of the adhesive. Ideally, a process for producing an acrylate-based polymer for a pressure-sensitive adhesive provides a means for controlling both molecular weight, i.e., intrinsic viscosity, and molecular weight distribution.
Despite the advantages which acrylate-based pressure-sensitive adhesives offer in comparison with compounded rubber, acrylates produced by the processes of the prior art also have a number of serious drawbacks.
The conventional method of preparing pressure-sensitive adhesives from acrylate monomers involves free radical addition polymerization in an organic solvent using chemical initiators. Chemical initiators commonly employed include organic peroxides, azobis compounds, persulfates and oxidation-reduction systems. Solvents include a variety of aliphatic hydrocarbons, aromatic hydrocarbons, esters, ketones and others. The product consists of a high viscosity polymer solution between 20 and 45 weight percent polymer concentration.
The polyacrylate solution is coated onto a substrate, e.g., a backing or webbing such as tape or label stock The volatile solvent is then evaporated, thereby leaving a nearly solvent-free layer of adhesive. The practical manufacture of pressure-sensitive adhesive products such as tapes, labels and others also often requires the use of prime and/or release coatings or inclusion of a release coated interlayer.
The conventional methods for solution polymerization and coating of acrylate-based pressure-sensitive adhesives possess several inherent drawbacks. Chemical initiators react to yield free radicals, which initiate the chain reaction propagation by which the addition polymerization proceeds. In all cases, the rate of free radical generation or initiation (which affects the molecular weight of the product) is highly temperature dependent, often increasing by an order of magnitude for every 10� C. temperature rise. Acrylate polymerization is a very exothermal reaction, yielding approximately 20 kilocalories per mole of monomer Reaction control is therefore limited by the ability to remove heat from the system. Failure to maintain a reasonable temperature profile can result in undesirably low molecular weight, poor product performance, poor reproducibility and, in extreme instances, violent runaway reaction. Temperature control may be accomplished by heat transfer or solvent reflux and may be aided by gradual introduction of the initiator. However, the ability to provide adequate heat removal and mixing of initiator for a commercial scale reactor is limited by the bulk viscosity of the system. Viscosity is determined by the molecular weight and concentration of the polymer. Therefore, the use of conventional solution polymerization limits both the molecular weight and final solids concentration of the product, and as a result, using the methods of the prior art, high-solids acrylate adhesives are inferior to the solution polymer analogs.
The use of chemical initiators poses a further drawback in that a low molecular weight fraction consisting of unreacted catalyst and catalyst fragments invariably will be incorporated into the adhesive. These low molecular weight species are undesirable because they are free to migrate to the adhesive bond surface, where they inhibit performance. Furthermore, for biomedical applications, such as dermal application in first aid products, the initiator fragments may irritate the skin or possibly show other toxic effects.
The conventional coating of acrylate polymer solutions and subsequent drying is also problematic. The drying phase is highly energy intensive, usually the most costly and time-consuming in the manufacturing chain. Evaporation of large volumes of solvent in the workplace may also violate environmental and occupational safety regulations and create a fire and explosion hazard. Moreover, the resulting loss of solvent is expensive. While solvent recovery systems may help alleviate both material loss and environmental damage, these systems are very expensive to install and operate.
An alternative to solution-based polymers involves the use of water-borne acrylate polymer latices which are produced by emulsion polymerization. While the use of an acrylic latex as a substitute for solutions eliminates the problems associated with the evaporation of hydrocarbons, it still requires the evaporation of large volumes of water. While the drying step may not have the same environmental consequences and pollution abatement costs, the energy requirements are greatly increased, thus it remains expensive and time-consuming. Moreover, the emulsion polymerization process by which the latex is produced requires both water-soluble chemical initiators and significant amounts of surfactants. These low molecular weight species may be detrimental to product suitability and performance. Furthermore, polar monomers with appreciable solubility in water may be difficult or impossible to incorporate into the polymer.
In response to the need to reduce energy consumption and avoid the environmental and work safety problems associated with solution and latex polymers, manufacturers of acrylate-based pressure-sensitive adhesive products have, in recent years, developed methods for curing or polymerizing acrylate monomers inplace on a substrate using ultraviolet or electron beam energy. In these methods, a liquid mixture of acrylate monomers and/or prepolymers possibly with other components, is applied as a film or coating onto a substrate, such as tape or label stock. The coatings or films usually have a thickness in the range of about 0.5 μm to 500 μm. The coating on the film is exposed to ultraviolet radiation (if photoinitiators are present in the coating) or electron beam radiation to polymerize the monomers and/or cure the system by the introduction of cross-links. These processes must be operated at very high free radical concentrations, and radiation exposure rates are in the megarads per second range since economic and practical considerations require that the coating be polymerized and cured in a matter of a few seconds. As a result, adhesives produced in this manner have a low degree of polymerization and contain low molecular weight fractions which often affect adhesive performance adversely. Although both ultraviolet and electron beam curing may give satisfactory results for some products, high residual monomer is often a problem and the products obtainable may be limited to highly cross-linked systems.
Additionally, the products which may be manufactured by these processes are limited to webbings which have enough radiation resistance to withstand the relatively high doses required for curing. These processes may be employed only to manufacture certain pressure-sensitive products, such as tapes, by in-situ polymerization; and they are not suitable for the production of bulk adhesives which may be subsequently applied to any number of substrates regardless of radiation resistance.
U.S. Pat. Nos. 4,165,266, 3,772,063 and 3,661,618 describe exemplary systems for in-place radiation polymerization or curing of acrylate coatings to produce pressure-sensitive adhesive products.
An alternative to the application of pressure-sensitive adhesives in the form of solutions, latices or monomer compositions for in-place radiation curing is hot-melt application. This technique, which has been used extensively for the application of compounded rubber adhesives, requires that the adhesive polymer be in a solventless or low-solvent (i.e., >70% solids) form. In hot-melt applications, the viscoelastic solid is heated to its softening or melting point and applied to the substrate by means such as calendering, spraying, or extrusion. Hot-melt application of adhesives is relatively simple and avoids or ameliorates the need for evaporating solvents with the attendant energy costs and environmental hazards.
As previously indicated, the production of acrylate polymers in a solventless or low-solvent form suitable for hot-melt application is difficult, if not impossible, using polymerization procedures of the prior art. Consequently, there are few commercial hot-melt, pressure-sensitive adhesives based on acrylate polymers, and these are for narrow applications, despite the fact that the art has long sought such products. While some hot-melt acrylate adhesives have been produced by stripping off solvent from conventionally produced acrylate solution polymers, these adhesives have not been widely accepted due to their poor performance properties. Moreover, this procedure does not eliminate the need for evaporating large quantities of solvent.
Hot melt acrylic adhesives have been reported which are said to show reversable thermal cross-linking upon cooling. These and other highly cross-linked hot melt adhesives may show marked reduction in viscoelasticity and thus poorer performance.
It is a primary object of the present invention to provide a process for producing acrylate-based pressure-sensitive adhesives which provide for accurate control of molecular weight and molecular weight distribution. In particular, it is an object of the invention to provide a process which allows for the production of acrylate-based pressure-sensitive adhesives having intrinsic viscosities above about 2.5 dl/g.
It is a further object of the invention to provide a process for producing acrylate-based, pressure-sensitive adhesives which are free of residual polymerization initiators, surfactants and other low molecular weight species.
It is a further object of the invention to provide a process for producing acrylate-based, pressure-sensitive adhesives in a low-solvent or solventless form suitable for hot-melt application.
These and other objects of the invention will be readily apparent from the description that follows.
SUMMARY OF THE INVENTION The present invention provides a process for producing pressure-sensitive adhesives in bulk which comprises:
(a) introducing, to a sealable reaction vessel, a liquid, polymerizable monomer composition, said composition comprising:
(i) from 65 to 100 parts (based on total monomer) of at least one acrylate monomer of the formula: ##STR1## wherein R1 is hydrogen or methyl and R2 is a straight or branched chain alkyl having from 2 to 8 carbon atoms,
(ii) from 0 to 35 parts (based on total monomer) of at least one ethylenically unsaturated comonomer, per 100 parts of polymerizable monomer;
(b) deaerating the liquid, polymerizable monomer composition before or after introducing it into the vessel;
(c) sealing the reaction vessel and polymerizing the monomers in the sealed vessel by exposing them to ionizing radiation at a dose rate from about 1 kilorad per hour to about 1 kilorad per second.
If desired, the composition may also include up to about 80% (by weight of the total composition) of an appropriate solvent.
The process of the invention allows for the production of acrylate-based, pressure-sensitive adhesives with close control over molecular weight and molecular weight distribution. This permits a polymer to be tailored to specific applications over a broad range of properties. The scope of interest for application of the process is broad, ranging from intrinsic viscosities of less than 0.75 to more than 3.6; but the utility of the process is most important when it is used to produce polymers of higher molecular weight than can be practically produced on a commercial scale by prior art techniques. In particular, the process of the invention allows for the production of acrylate-based, pressure-sensitive adhesives having intrinsic viscosities above 2.5 dl/g, if desired.
Using the process of the invention, it is possible to polymerize acrylates in the absence of solvent or in a small amount of solvent in order to produce acrylate-based, pressure-sensitive adhesives suitable for hot-melt application. Indeed, we have discovered that high molecular weight polyacrylates can be produced by radiation-induced bulk polymerization without encountering the types of problems which are associated with chemically-initiated polymerization in a high-viscosity system. We have also determined that the process can be used to produce polymers which for some applications, display properties superior to those produced conventionally.
DETAILED DESCRIPTION OF THE INVENTION The process of the invention entails the polymerization of acrylate monomers in a closed reaction vessel to produce an adhesive product that can subsequently be applied to a webbing. The process of the invention is distinguished from the in-place radiation curing of thin films or coatings directly on a webbing as described in the prior art. In accordance with the teachings of the invention, a liquid, polymerizable monomer composition is introduced to a closed or sealable container of dimensions and materials suitable for efficient exposure of the contents to ionizing reduction at exposure rates of one kilorad per hour to one kilorad per second. The particular geometry of the reaction vessel will be dictated first by considerations of product uniformity, which is affected by the tendency of the material to attenuate the radiation, and second by product configurations desirable to the end user. The volume of the polymerizable liquid contained in the reaction vessel will have dimensions which are orders of magnitude greater than typical adhesive film thicknesses useful in pressure sensitive products. Generally, the volume of polymerizable liquid will have a dimension in every direction of at least about 0.5 cm.
In a preferred embodiment of the invention, the liquid, polymerizable monomer composition is placed in a cylindrical container having a diameter of from about 1.0 in. to about 26 in. and then the cylindrical container can be rotated about its axis, with the axis parallel to the source of radiation, in order to obtain more uniform irradiation by minimizing attenuation by the contents. For example, gamma ray attenuation of about 20% occurs at the axis of a 10-in. diameter cylinder and such non-uniformity is generally acceptable.
Alternatively, comparable uniformity of exposure can be achieved in larger dimensions in a rotating 24-in. diameter drum containing a central void of about 16 inches. Such a container would provide for a greater spread in the molecular weight distribution since the free radical concentration of the contents will vary appreciably as the drum rotates. For dilute solutions, the container can comprise pipes through which the reactants can flow, but both solutions and bulk polymers can conveniently be irradiated in discrete containers such as drums or static pipe reactors.
The liquid, polymerizable monomer composition comprises from 65 to 100 parts of acrylate monomer, per 100 parts by weight of polymerizable monomer in the composition. The acrylate monomer portion of the composition comprises at least one acrylate (or methacrylate) monomer of the formula ##STR2## wherein R1 is hydrogen or methyl and R2 is a straight or branched chain alkyl having from 2 to 8 carbon atoms. Preferred acrylate monomers are those selected from the group comprising: 2-ethylhexyl acrylate, n-butyl acrylate, isobutyl acrylate and ethyl acrylate, with 2-ethylhexyl acrylate being most preferred.
The liquid, polymerizable monomer composition can, if desired, contain up to about 35 parts of an ethylenically unsaturated comonomer per 100 parts by weight of polymerizable monomer in the composition. Any of the known, ethylenically unsaturated monomers conventionally employed in the production of polymers having adhesive properties can be used. Preferred comonomers are those selected from the group comprising: acrylic acid, methacrylic acid, N-substituted acrylamides or methacrylamides, ccrylonitrile, methacrylonitrile, alkylol acrylates, maleic anhydride, and N-vinyl pyrrolidone.
While we have found that the method of the invention produces pressure-sensitive adhesives having good internal cohesion without the necessity of adding cross-linking agents, one can, if desired, increase the degree of cohesion by adding to the liquid, polymerizable composition a small amount of a difunctional, ethylenically unsaturated monomer such as a diacrylate compound or glycidyl methacrylate. Diacrylate compounds, i.e., compounds having two acrylyl or methacrylyl groups, are particularly useful. One can mention as merely exemplary of such compounds, diethylene glycol diacrylate, propylene glycol diacrylate, 1,3-butanediol diacrylate, neopentyl glycol diacrylate, tetraethylene glycol diacrylate, 1,3-propanediol diacrylate and the like, as well as the corresponding dimethacrylates. If used, the crosslinking monomer is present at up to about 5 parts per 100 parts of polymerizable monomer in the composition. Glycidyl methacrylate, N-metholyl acrylamide and other functional monomers contain nonethylenic reactive groups which may subsequently be chemically or photochemically cross-linked upon application to the webbing.
In order to control the molecular weight of the adhesive polymer, there may also be present in the liquid, polymerizable monomer composition a chain transfer agent. A number of chain transfer agents can be employed, with isopropyl alcohol and triethanolamine being preferred. The chain transfer agent, if used, can be present in amounts up to about 4 parts per 100 parts of the liquid, polymerizable monomer composition. As those skilled in the art are aware, increasing the concentration of chain transfer agent will reduce the molecular weight of the polymer. Generally, we have found that the use of a chain transfer agent is not necessary in the practice of the invention when the polymerization is carried out in the presence of a solvent.
Preferred liquid, polymerizable monomer compositions in the practice of the invention are those in which 2-ethylhexyl acrylate or n-butyl acrylate is either the sole polymerizable monomer, or copolymerized with other vinyl monomers. For example, 2-ethylhexyl acrylate and/or butyl acrylatecopolymerized with acrylic acid, vinyl pyrrolidone, or vinyl acetate.
The liquid, polymerizable monomer composition can be polymerized in the presence or absence of a solvent. Indeed, a major advantage of the process of the invention is that it allows for the production of low-solvent or no-solvent acrylate-based adhesives suitable for hot-melt application. Nonetheless, the process of the invention can also be used to polymerize the monomer composition in the presence of a solvent, if desired. Any conventional volatile organic solvent in which the monomers and the resultant polymer are soluble and which does not interfere with the polymerization reaction can be employed. The solvent may be a substituted or unsubstituted aliphatic or aromatic hydrocarbon. Preferred solvents are heptane, toluene, acetone and tetrahydrofuran. The solution can contain from 20 to 100 parts by weight of the liquid, polymerizable monomer composition described above and from 0 to 80 parts by weight of solvent. The decision whether to employ a solvent in the polymerization is primarily dependent on the viscosity which one desires in the final product, i.e., whether one desires to apply the product as a low viscosity film or coating or as a hot-melt adhesive. When one desires to apply the product as a holt-melt adhesive, the polYmerization is carried out in a solution containing greater than 70% by weight of the liquid, polymerizable monomer composition and less than 30% by weight of solvent. The preferred formulation for hot-melt adhesives is solventless. High solids solution polymers exhibiting bulk viscosities of under about 500,000 cps may be applied by cold flow processes. The solvent must then be evaporated; however, by this means the capital and operating costs associated with conventional low solids solutions may be greatly reduced.
In carrying out the process of the invention, the monomer(s), chain transfer agent (if present) and solvent (if present) are blended together and charged to the reaction vessel. In the case of low-solvent or solventless polymerizations, it is preferred to line the reaction vessel with a barrier surface, since the reaction product has a high degree of tack and may otherwise be difficult to remove from the vessel. The barrier material may consist of material which is non-reactive with and shows no solubility or permeation by the monomer solvent mixture and possesses suitable radiation resistance. The preferred barrier material will have as its surface in contact with the adhesive composition a material such as a silicone or polyfluorocarbon to which the acrylic polymer will not adhere. The reaction vessel can be constructed of any material which is resistant to and penetrated by the ionizing radiation which is employed to polymerize the monomer composition.
Since acrylate monomers are usually provided commercially with a polymerization inhibitor, such as the methyl ether of hydroquinone (MEHQ), which inhibits polymerization in the presence of oxygen, it is necessary to displace any dissolved oxygen which is present in the monomer composition prior to carrying out the polymerization reaction. This can be achieved by sparging nitrogen through the monomer mixture.
Nitrogen sparging may be accomplished directly in the reaction container or prior to loading providing the transfer is made under inert conditions. It is important that the reaction container prevent recontact with oxygen during any stage prior to the completion of polymerization. The reaction container may be of any oxygen impervious material which is both stable in and transparent for the ionizing radiation employed and thermally stable at the operating temperatures of the process. We have employed as polymerization vessels hardwall cylindrical reactors constructed of glass, aluminum or stainless steel. These have been equipped with a means for either in situ sparging or inert transfer of deaerated monomer. In addition, we have used "soft" containers. These are flexible leak-proof multilayer bags. The contact layer consists of a non-stick surface such as silicone; the outer layer is a material impervious to oxygen such as aluminum foil; the middle layer is a heat sealable material such as polyethylene. The bags are filled with deaerated monomer and sealed under an inert atmosphere, for instance, in a nitrogen filled glove box. The bags are placed in an appropriate supporting vessel and can be safely removed from the inert atmosphere and subsequently polymerized.
Polymerization is initiated by exposing the liquid, polymerizable monomer composition to ionizing radiation. Any conventional source of penetrating ionizing radiation may be employed, i.e., any source of low LET (linear energy transfer) radiation which is capable of extracting protons from the monomers to create free radicals which propagate to form polymer chains. The known types of ionizing radiation include, for example, gamma rays and X-rays. We prefer to employ gamma radiation as the ionizing radiation. Suitable sources of gamma radiation are well known and include, for example, radioisotopes such as cobalt-60 and cesium-137.
As previously indicated, the process of the invention allows for careful control of both molecular weight and molecular weight distribution in the final polymer, thereby allowing the practitioner to "tailor" the properties of the resulting pressure-sensitive adhesive. Several variables can be manipulated to control the molecular weight of the final product, the most important being radiation dose rate and concentration of chain transfer agent. Unlike the chemically initiated polymerization procedures of the prior art, in which the rate of chain initiation (and consequently molecular weight) is highly temperature dependent, the polymerization procedure of the present invention is relatively unaffected by temperature, except in monomer systems where chain transfer is an important factor. Consequently, limitations on the ability to remove heat from the reactants do not interfere substantially with the ability to control molecular weight in the process of the invention. Nevertheless, it was surprising to find that solventless polymerizations, essentially adiabatic, could reach exotherms exceeding 200� C. and still yield product with desirable, even superior, properties. As previously indicated, increasing the concentration of chain transfer agent generally reduces the molecular weight of the product. Likewise, increasing the dose rate results in a reduction in molecular weight of the product.
Polymerization can be carried out over a wide range of dose rates in the range of a kilorad per second to about a kilorad per hour. It is preferred, however, that the dose rate be kept between 5 and 250 kilorads per hour. Dose rates exceeding a few tenths of a kilorad per second generally result in polymers of too low molecular weight to be useful as adhesives due to cohesive failure or low creep resistance. However, some polymer formulations produced above this range may find application in specialty products. In other cases, these low molecular weight polymers may subsequently be cross-linked to provide sufficient cohesion. Dose rates below a kilorad per hour generally result in polymers with molecular weights too high to be useful due to low tack and adhesive failure.
Although temperature is relatively less important in controlling molecular weight in the process of the invention than in chemically initiated polymerizations, it may nevertheless be a significant factor in viscous compositions having relatively high chain transfer to monomer coefficients such as 2-ethylhexyl acrylate and N-vinyl pyrrolidone or for compositions having relatively high concentrations of chain transfer agent. For such compositions temperature, as well as dose rate, can be varied to obtain the desired molecular weight, with increasing temperature resulting in lower molecular weight. Thus, dose rate, chain transfer agent concentration and temperature can all be used to control molecular weight. In low-solvent or solventless polymerizations, such as those used to produce the hot-melt and cold-flow adhesives of the invention, molecular weight is controlled essentially by manipulation of composition, dose rate, and initial temperature since the viscosity buildup in the reaction mixture makes the removal of heat and control of reaction temperature difficult.
The molecular weight distribution can be controlled by varying the dose rate in a continuous or stepwise manner during the polymerization reaction. It is thus possible to produce polydisperse or polymodal molecular weight distributions which make possible the production of a wide range of products having a variety of adhesive and cohesive products. For example, the polymerization reaction may be carried out at a first dose rate for a period of time and then the dose rate changed for the remainder of the polymerization in order to produce an essentially bimodal molecular weight distribution.
The total integrated radiation dose primarily affects the degree of conversion of monomer to polymer. In general, it is desirable to irradiate to conversions of 95% or greater and preferably to conversions of 99.5% or higher. However, the reaction rate becomes asymptotic with time as monomer concentration is depleted, and it becomes more difficult to achieve very high conversion. Low solvent or solventless sytems are preferred in this aspect since higher viscosity aids in monomer reaction at high conversion. Thus, solventless compositions may be polymerized using the process of the invention to very low levels of residual monomer. This is particularly important in pressure-sensitive adhesives used for medical applications, where even small amounts of residual monomer may irritate the skin.
During the asymptotic or monomer depletion stage of the reaction, radiation cross-linking will begin to occur. Radiation induced cross-linking will be more significant as solids concentration increases. Cross-linking may be minimized by the inclusion of chain transfer agent but only at the cost of reduced molecular weights.
There are cases where over-irradiation to achieve a degree of cross-linking may be permissible, or even desirable. Cross-links may be tolerated or even desired up to a certain density as they give greater cohesion and creep resistance. However, in too great a density, cross-linking will adversely affect product coating and performance; thus, over-irradiation must be limited. Cross-linking relative to monomer consumption near the end of the reaction is greater at higher dose rates. To achieve high degrees of conversion while preventing product deterioration, a finishing step dose rate of less than 20 kilorads per hour is preferred.
The process may be varied to produce a wide variety of polymer and adhesive properties, among them molecular weight distribution, residual monomer concentration, and cross-link density. Post application ultraviolet or ionizing irradiation may be employed to further alter properties. Final adhesive properties will depend on both polymerization and post-application processing conditions. Products containing some degree of residual monomer may be particularly useful where post application irradiation is employed.
The higher molecular weights obtainable and pre-application cross-linking make possible the production of acrylic adhesives, either in solution or solventless, which require significantly less post-application curing, by either chemical or radiation processes, than many existing products.
As previously indicated, the proess of the invention may be carried out in the absence or near absence of solvent to produce acrylate-based pressure-sensitive adhesives suitable for hot-melt application. As the amount of solvent in the reaction system approaches zero, reaction conditions become essentially adiabatic due to the inability to remove the heat of polymerization from the reaction mixture. Nevertheless, we have discovered that the polymerization process of the invention can be performed under adiabatic conditions without a breakdown in molecular weight or creation of a runaway reaction. It was a particularly surprising to find that the process of the invention provided means for the production of hot-melt acrylate-based pressure-sensitive adhesives having intrinsic viscosities above 3.0 dl/g.
High viscosity cold flow adhesives may be produced by polymerizing in the presence of about 75% solvent to about 20% solvent although the minimum solvent concentration practical for cold flow application will depend on the molecular weight of the polymer.
The hot-melt adhesives of the invention are produced by carrying out the polymerization reaction in the presence of not more than 30% by weight of a solvent, preferably not more than 5% by weight of a solvent, and most preferably in the absence of solvent.
The following examples are presented in order to further illustrate the practice of the invention and are not intended to limit the scope of the invention in any way. Unless otherwise indicated, all parts and percents are by weight and all temperatures are in degrees Celsius. Intrinsic viscosities were determined at 27� C. in heptane.
EXAMPLES 1-3 Solventless Polymerization at a Single Dose In each of Examples 1-3, a mixture of 2-ethylhexyl acrylate and isopropyl alcohol as a chain trnsfer agent was charged into a polyethylene or polyethylene-silicone laminate lined cylindrical pressure vessel (31/2 in. diameter). The monomer was then deaerated by nitrogen sparging through a dip tube, after which the reactor was sealed. The vessel was exposed to gamma radiation from a cobalt-60 source at a dose and dose rate as indicated in Table 1. In each example, the product obtained was a tacky, elastic solid at room temperature which softened to a viscous liquid at 170� to 200� C. The polymers, all of which displayed good tack and peel resistance, were suitable for application as hot-melt adhesives. Dose rates, dose, monomer conversion and intrinsic viscosity of the products are given in Table 1.
TABLE 1______________________________________Exam-                                      Con-ple   2-EHA   IPA     Dose Rate                         Total Dose                                 I.V. versionNo.   p.b.w.  p.b.w.  Krad/hr.                         KRads   dl/g %______________________________________1     98      2       100     50      1.47 96.3 2*   98      2       100     50      0.92 93.73     98      2       350     175     1.22 96.5______________________________________ 2-EHA = 2ethylhexyl acrylate IPA = isopropyl alcohol I.V. = intrinsic viscosity *Polymerized at an initial temperature of 40� C. All other polymerizations begun at room temperature
EXAMPLES 4-39 Variation of Polymerization and Post-Application Parameters A mixture of 2-ethylhexyl acrylate with 0.3% isopropyl alcohol was deaerated in a nitrogen-filled glove box. Approximately 100 g samples of this mixture were charged into 6 silicone release coated oxygen impervious bags and heat sealed. These samples were irradiated at a dose of 20 krad/hr. for the total doses given in Table 2 along with properties obtained.
TABLE 2______________________________________Example   Dose/   Conversion  Gel     I.V.No.       Krad    %           fraction %                                 dl/g______________________________________4         13      85           0      2.05         18      91.6        22      2.46         23      91.7        40      --7         28      95.6        81      --8         33      97.5        87      --9         38      98.0        100     --______________________________________
The products obtained as Examples 4-9 were applied by hot melt extrusion to a polyester webbing utilizing an Acumeter Laboratories LH-1 evaluation coater. The film thickness was about 1.0 μm and the width was 3 inches. Samples of these tapes were exposed to accelerated electrons utilziing an Energy Sciences electron curtain to doses between 0 and 20 Mrads. Table 3 describes the results.
TABLE 3______________________________________Ex-           Extrusion                  Postam-  Polymer  Temper-  Appli-ple  Example  ature    cation                        ResidualNo.  Coated   (�C.)                  Mrad  Monomer Tack Cohesion______________________________________10   4        200      0     P       G    F11   4        200      2     P       G    G12   4        200      5     F       G    G13   4        200      10    G       G    G14   4        200      20    G       G    G15   5        240      0     P       G    F16   5        240      2     P       G    G17   5        240      5     F       G    G18   5        240      10    G       F    E19   5        240      20    E       F    E20   6        240      0     P       G    F21   6        240      2     F       G    F22   6        240      5     G       G    G23   6        240      10    G       G    E24   6        240      20    E       F    E25   7        240      0     F       G    G26   7        240      2     F       G    G27   7        240      5     G       G    G28   7        240      10    E       F    E29   7        240      20    E       P     E*30   8        240      0     F       G    F31   8        240      2     F       G    F32   8        240      5     G       F    G33   8        240      10    E       P    G34   8        240      20    E       P     E*35   9        240      0     F       G    G36   9        240      2     F       F    G37   9        240      5     F       F    G38   9        240      10    E       P    E39   9        240      20    E       P     E*______________________________________ P = Poor, F = Fair, G = Good, E = Excellent, *Deterioration or Embrittlement
EXAMPLE 40 Solventless Polymerization Using Two Dose Rates A mixture of 2-ethylhexyl acrylate containing 1% isopropyl alcohol was charged into a 2-inch diameter cylindrical reaction vessel and dearated as in Examples 1-3. The vessel was then exposed to gamma radiation at an initial dose rate of 20 krad per hour to 60 krad followed by exposure at 350 krad per hour for an additional 175 krad. The product was a tacky elastic solid which softened to a viscous liquid at about 200� C. The monomer conversion was determined to be 98% and the intrinsic viscosity to be 1.0 dl/g.
EXAMPLES 41-46 Solvent Copolymerizations A mixture of 44.75 parts 2-ethylhexyl acrylate, 44.75 parts n-butyl acrylate, 5 parts vinyl acetate, 5 parts acrylic acid and 0.5 parts isopropanol was prepared as for example 4 and irradiated using the dose rate and dose indicated in Table 4. Results of the irradiation are given in the table.
EXAMPLE 42 A mixture of 4 parts vinyl acetate, 5 parts acrylic acid, 42.5 parts 2-ethylhexyl acrylate, 42.5 parts n-butyl acrylate and 0.5 parts isopropanol was prepared as for example 4 and irradiated using the dose rate and dose indicated in Table 4. Results of the irradiation are given in the table.
EXAMPLE 43 A mixture of 2.8 parts vinyl acetate, 5 parts acrylic acid, 46.25 parts 2-ethylhexyl acrylate, 42.25 parts butyl acrylate and 0.5 parts isopropanol was prepared as for example 4 and irradiated using the dose rate and dose indicated in Table 4. Results of the irradiation are given in the table.
EXAMPLE 44 A mixture of 94.5 parts 2-ethylhexyl acrylate, 5 parts acrylic acid and 0.5 parts isopropanol was prepared as for example 4 and irradiated using the dose rate and dose indicated in Table 4. Results of the irradiation are given in the table.
EXAMPLE 45 A mixture of 94.5 parts 2-ethylhexyl acrylate, 5 parts acrylic acid, and 0.5 parts isopropanol was prepared as for example 4 and irradiated using the dose rate and dose indicated in Table 4. Results of the irradiation are given in the table.
EXAMPLE 46 A mixture of 47.5 parts 2-ethylhexyl acrylate, 47.5 parts n-butyl acrylate and 5 parts N-vinyl pyrrolidone was prepared as for example 4 and irradiated using the dose rate and dose indicated in Table 4. Results of the irradiation are given in the table.
TABLE 4______________________________________Example Dose Rate Dose   Conversion                            Gel      I.V.No.     Krad/Hr   Krad   %       fraction %                                     dl/g______________________________________41      20        52.5   99.0    20       1.442      20        30.2   97.8    0        .7543      20        25     94.8    10       1.3044      20        25     --      20       --45      20        42     --      45       --46      20        25     90.0    0        3.6______________________________________
EXAMPLES 47-54 Polymerizations in Solvent at Single Dose Rate Using a procedure similar to that of Examples 1-3, homopolymers of 2-ethylhexyl acrylate were prepared by gamma irradiation in the presence of heptane. The products obtained ranged from elastic solids and viscoelastic semisolids, suitable for hot-melt application to viscous liquids suitable for application, by conventional techniques used with solvent-based adhesives. All products exhibited good tack. Polymerization conditions and results are summarized in Table 5.
TABLE 5__________________________________________________________________________ExampleMonomer(s)       Heptane            IPA Dose Rate                      Total Dose                            I.V.                               Conversion                                     ProductNo.  p.b.w. p.b.w.            p.b.w.                Krad/hr                      KRads dl/g                               %     Characteristics__________________________________________________________________________47   2-EHA/90       8.5  1.5 105   315   1.0                               98    ES48   2-EHA/90       8.75 1.25                100   300   1.9                               99    ES49   2-EHA/30       70   0   55    187   2.0                               95    VES50   2-EHA/30       70   0   170   510   1.4                               96.4  VL51   2-EHA/70       30   0   55    220   3.4                               10052   2-EHA/70       30   0   20     77   3.6                               94.753   2-EHA/60       40   0   20     77   3.2                               9254   2-EHA/50       50   0   190   410   1.73                               98__________________________________________________________________________ 2-EHA = 2ethylhexyl acrylate IPA = isopropyl alcohol I.V. = intrinsic viscosity ES = elastic solid at room temperature VES = viscoelastic semisolid at room temperature VL = viscous liquid at room temperature
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS2803598 *Oct 16, 1953Aug 20, 1957Exxon Research Engineering CoGamma ray polymerization of unsaturated estersUS2803599 *Oct 1, 1954Aug 20, 1957Exxon Research Engineering CoGamma ray polymerization of unsaturated nitrogen compoundsUS2941934 *Jan 16, 1957Jun 21, 1960Gen Aniline & Film CorpPolymerization by temperature controlled irradiationUS3081244 *Mar 15, 1961Mar 12, 1963Shell Oil CoProcess for polymerizing unsaturated monomers using ionizing radiationUS3661618 *Jun 30, 1969May 9, 1972Firestone Fire And Rubber Co TProcess for the preparation of pressure sensitive adhesivesUS3725115 *Jun 18, 1970Apr 3, 1973Ppg Industries IncPressure-sensitive adhesive articles and method of making sameUS3772063 *Jul 9, 1971Nov 13, 1973Nitto Electric Ind CoProcess for the production of pressure-sensitive adhesive materialsUS3897295 *Jun 2, 1972Jul 29, 1975Ppg Industries IncIonizing radiation method for forming acrylic pressure sensitive adhesives and coated substratesUS3929602 *Dec 8, 1972Dec 30, 1975Japan Atomic Energy Res InstLow temperature irradiation of vitrifiable mixtures of unsaturated monomersUS4052527 *Feb 7, 1977Oct 4, 1977National Starch And Chemical CorporationRadiation polymerized hot melt pressure sensitive adhesivesUS4151055 *Apr 5, 1976Apr 24, 1979Union Carbide CorporationRadiation curable adhesive compositionsUS4181752 *Sep 25, 1978Jan 1, 1980Minnesota Mining And Manufacturing CompanyAcrylic-type pressure sensitive adhesives by means of ultraviolet radiation curingUS4234662 *Apr 26, 1979Nov 18, 1980National Starch And Chemical CorporationPressure sensitive hot melt adhesive curable by exposure to electron beam radiationUS4305854 *Sep 27, 1979Dec 15, 1981Polychrome CorporationRadiation curable pressure sensitive adhesiveUS4413019 *Dec 2, 1981Nov 1, 1983The Standard Products CompanyRadiation curable adhesive compositions and composite structuresUS4438177 *Jun 16, 1982Mar 20, 1984Smith And Nephew Associated Companies Ltd.Cured pressure sensitive adhesivesDE2134468A1 *Jul 9, 1971Jan 13, 1972 Title not availableEP0108630A2 *Nov 4, 1983May 16, 1984Deltaglass S.A.Radiation-curable adhesive compositions* Cited by examinerNon-Patent CitationsReference1Ohta et al., "Radiation Curing", Radiat. Phys. Chem., vol. 22, No. 3-5, pp. 795-802, 1983, Great Britain.2 *Ohta et al., Radiation Curing , Radiat. Phys. Chem., vol. 22, No. 3 5, pp. 795 802, 1983, Great Britain.* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS5064681 *Jun 8, 1989Nov 12, 1991International Business Machines CorporationSelective deposition process for physical vapor depositionUS5084348 *Jan 12, 1990Jan 28, 1992Lohmann Gmbh & Co. KgWater-soluble, pressure-sensitive adhesive masses splice tapesUS5194486 *Nov 6, 1990Mar 16, 1993H & N Chemical CompanyPressure sensitive adhesive coating with solvent and alkyl acrylate polymer with crosslinkingUS5214094 *Dec 19, 1991May 25, 1993H. & N. Chemical CompanyMethod of preparing pressure sensitive adhesives having interpolymers with internal crosslinking monomersUS5795834 *Dec 22, 1995Aug 18, 1998Minnesota Mining & Manufacturing CompanyAdhesive tape and method of makingUS5804610 *Aug 28, 1997Sep 8, 1998Minnesota Mining And Manufacturing CompanyMethods of making packaged viscoelastic compositionsUS5880800 *Jan 6, 1997Mar 9, 1999Nitto Denko CorporationOptical film and liquid crystal displayUS5902654 *Sep 8, 1995May 11, 1999Minnesota Mining And Manufacturing CompanyUsing transition metal catalyst in bag as polymerization vesselUS5932298 *Aug 17, 1998Aug 3, 1999Minnesota Mining And Manufacturing CompanyMethods of making packaged viscoelastic compositionsUS6042882 *Oct 16, 1997Mar 28, 20003M Innovative Properties CompanyEmbedding surface fibers on one side of a woven fabric tape by surface coating with extruded polyethylene, overcoating the polyethylene with pressure sensitive adhesive to yield hand tearable, nonfraying adhesive tapeUS6048806 *Oct 16, 1997Apr 11, 20003M Innovative Properties CompanyAdhesive tape and method of makingUS6063838 *Oct 3, 1997May 16, 20003M Innovative Properties CompanyMarking for pavingUS6103316 *Jul 17, 1998Aug 15, 20003M Innovative Properties CompanyOne step process of irradiating by an electron beam a coating of a macroemulsion-based precursor comprising an acrylate(s), an unsaturated monomer, oligomer or macromonomer and a surfactant to polymerize and crosslinkUS6184264 *Aug 12, 1996Feb 6, 2001Smith & Nephew PlcAdhesivesUS6232365Jul 17, 1998May 15, 20013M Innovative Properties CompanyLow temperature electron beam polymerizationUS6294249Feb 5, 1999Sep 25, 20013M Innovative Properties CompanyPreparing viscoelastic compositions (e.g., adhesives such as hot melt adhesives) in which a pre-viscoelastic composition (e.g., a pre-adhesive composition) is combined with a packaging material and then polymerized.US6461728 *Dec 29, 2000Oct 8, 20023M Innovative Properties CompanyObtained by polymerization of an aqueous emulsion of a (meth)acrylate monomer, a polar, free-radically polymerizable material such as acrylic acid and emulsifierUS6630238Jun 13, 2001Oct 7, 20033M Innovative Properties CompanyBlend of at least two components, wherein first component is pressure-sensitive adhesive and second component is thermoplastic material; medical tapesUS6632522Aug 16, 1996Oct 14, 20033M Innovative Properties CompanyWith thermoplastic; drug delivery patches, labelsUS6747720 *Feb 8, 2002Jun 8, 2004Nitto Denko CorporationPolarizing plate with optical compensation film and liquid crystal displayUS6838185 *Nov 27, 2001Jan 4, 2005Nitto Denko CorporationAdhesive used for polarizing plate and optical memberUS7723436 *Nov 24, 2003May 25, 2010Tesa SeBimodal acrylate pressure-sensitive adhesive compoundsUS7829640Aug 28, 2007Nov 9, 2010Intertape Polymer Corp.replace one (or more) static mixers in the loop reactor with a dynamic mixer such as a twin screw extruder or a planetary roller extruder; imparts shear thinning to reaction mixture that reduces melt viscosity of mixture thereby making it easier to move polymerized material through the loop reactorUS7833576 *Oct 22, 2001Nov 16, 2010Tesa SeUse of self-adhesive materials having anisotropic properties for producing stamping productsUS7906598Sep 30, 2008Mar 15, 2011Intertape Polymer Corp.Recirculation loop reactor bulk polymerization processUS7935762 *Mar 12, 2010May 3, 2011Tesa SeBimodal acrylate pressure-sensitive adhesive compoundsUS8202934 *Jul 31, 2007Jun 19, 20123M Innovative Properties CompanyHot melt processable polyurea copolymers and methods of their preparation and useUS8329079Apr 20, 2009Dec 11, 2012Entrochem, Inc.Method and apparatus for continuous production of partially polymerized compositions and polymers therefromUS8389596Feb 25, 2011Mar 5, 2013Kraft Foods Global Brands LlcLow-tack, UV-cured pressure sensitive adhesive suitable for reclosable packagesUS8398306Nov 7, 2005Mar 19, 2013Kraft Foods Global Brands LlcFlexible package with internal, resealable closure featureUS8763890Feb 25, 2011Jul 1, 2014Intercontinental Great Brands LlcPackage having an adhesive-based reclosable fastener and methods thereforUS8765217Nov 4, 2008Jul 1, 2014Entrotech, Inc.Method for continuous production of (meth)acrylate syrup and adhesives therefromEP0412672A1 *Jul 20, 1990Feb 13, 1991Dow Corning CorporationA method for controlling release forces in release coatingsWO1996007522A1 *Aug 10, 1995Mar 14, 1996Minnesota Mining & MfgMethod of making a packaged hot melt adhesiveWO2002053602A1 *May 16, 2001Jul 11, 20023M Innovative Properties CoGamma radiation polymerized emulsion-based (meth)acrylate pressure sensitive adhesives and methods of making and using same* Cited by examinerClassifications U.S. Classification427/505, 522/167, 522/4, 522/912, 522/903, 427/506, 427/208.4, 522/182International ClassificationC08F2/54Cooperative ClassificationY10S522/903, Y10S522/912, C08F2/54European ClassificationC08F2/54Legal EventsDateCodeEventDescriptionMay 8, 2001FPExpired due to failure to pay maintenance feeEffective date: 20010307Mar 4, 2001LAPSLapse for failure to pay maintenance feesSep 26, 2000REMIMaintenance fee reminder mailedSep 9, 1996FPAYFee paymentYear of fee payment: 8Sep 8, 1992FPAYFee paymentYear of fee payment: 4RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services©2012 Google