Patent US6687442 - Optical fiber for preserving plane of polarization - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inAdvanced Patent SearchPatentsAn optical fiber for preserving the plane of polarization including a cladding and a stress imparting part disposed in the cladding, the stress imparting part comprising a base material including B2O3. The average concentration of B2O3 in the base material of the stress imparting part is in a range between...http://www.google.com/patents/US6687442?utm_source=gb-gplus-sharePatent US6687442 - Optical fiber for preserving plane of polarizationAdvanced Patent SearchPublication numberUS6687442 B2Publication typeGrantApplication numberUS 10/047,669Publication dateFeb 3, 2004Filing dateJan 14, 2002Priority dateJan 17, 2001Fee statusPaidAlso published asCN1194235C, CN1371004A, DE60233009D1, EP1225457A1, EP1225457B1, US20020131738Publication number047669, 10047669, US 6687442 B2, US 6687442B2, US-B2-6687442, US6687442 B2, US6687442B2InventorsNaoki Shamoto, Kuniharu Himeno, Akira WadaOriginal AssigneeFujikura Ltd.Export CitationBiBTeX, EndNote, RefManPatent Citations (9), Non-Patent Citations (2), Referenced by (2), Classifications (11), Legal Events (3) External Links: USPTO, USPTO Assignment, EspacenetOptical fiber for preserving plane of polarizationUS 6687442 B2Abstract An optical fiber for preserving the plane of polarization including a cladding and a stress imparting part disposed in the cladding, the stress imparting part comprising a base material including B2O3. The average concentration of B2O3 in the base material of the stress imparting part is in a range between about 17 and 21 wt. %, and the maximum concentration of B2O3 in the base material is in a range between about 17 and 22 wt. %. The optical fiber has excellent polarization plane preserving properties, and no concave portion is generated in its stress imparting part even under wet heat conditions.
What is claimed is: 1. An optical fiber for preserving a plane of polarization, comprising:
a cladding; and a stress imparting part disposed in said cladding, said stress imparting part comprising a base material comprising B2O3, wherein the average concentration of B2O3 in the base material of the entire stress imparting part is in a range between about 17 and 21 wt. %, and the maximum concentration of B2O3 in the base material of the entire stress imparting part is in a range between about 17 and 22 wt. %. 2. An optical fiber for preserving a plane of polarization, comprising:
a cladding; and a stress imparting part disposed in said cladding, said stress imparting part comprising a base material extending along substantially an entire length of the optical fiber and comprising B2O3, wherein the average concentration of B2O3 in the base material is in a range between about 17 and 21 wt. %, and the maximum concentration of B2O3 in the base material is in a range between about 17 and 22 wt. %.
The present invention relates to an optical fiber for preserving the plane of polarization. More specifically, the present invention relates to a stress imparting type optical fiber for preserving the plane of polarization which may be used for optical communication or optical sensors and has an excellent plane of polarization preserving property even under wet heat conditions.
There are various types of optical fibers for preserving plane of polarization (hereinafter also referred to as polarization plane preserving optical fibers) in which the stress distribution in a single mode optical fiber is anisotropic, and particularly, one having a stress imparting part in its cladding has been widely used. The stress imparting type polarization plane preserving optical fibers may be categorized as the PANDA type, the bow tie type, the oval jacket type, etc., based on their shapes. Among these the PANDA type polarization plane preserving optical fiber is particularly widely used because of its large double refractive index and excellent polarization plane preservability.
FIG. 1 is a diagram showing an example of a conventional PANDA type polarization plane preserving optical fiber. In FIG. 1, the PANDA type polarization plane preserving optical fiber 4 includes a core 1 having a large refractive index, a cladding 2 which is formed around the core 1 so as to be concentric with the core, and stress imparting parts 3 which are disposed in the cladding 2. The stress imparting parts 3 are placed symmetrically with respect to each other with respect to the core 1 in the cladding 2. Each of the stress imparting parts 3 has a circular cross-section and its refractive index is lower than that of the cladding 2.
The stress imparting part 3 is made by using a material having a thermal expansion coefficient larger than that of a material used for forming the cladding 2. In particular, a B2O3�SiO2 glass is widely used for the stress imparting part 3. Since the thermal expansion coefficient of B2O3 is larger than that of SiO2, the stress applied to the core 1 increases as the proportion or the concentration of B2O3 increases, and accordingly, the double refractive index thereof is increased.
Japanese Unexamined Patent Application, First Publication (Kokai), No. Hei 8-101323, for example, discloses a polarization plane preserving optical fiber having a stress imparting part whose B2O3 concentration increases toward its center. Accordingly, the distribution of B2O3 in the stress imparting part of the polarization plane preserving optical fiber spreads out from its center toward the outer periphery portion thereof. In the above publication, it is also disclosed that the B2O3 concentration at the peripheral portion of the stress imparting part is preferably 15 wt. % or less so that the thermal expansion coefficient of the stress imparting part 3 becomes closer to that of the cladding 2. In this manner, the concentration of stress at the interface between the two may be eliminated and the generation of cracks may be prevented.
However, if the concentration of B2O3 at the center of the stress imparting part is high as in the polarization plane preserving optical fiber disclosed in the Japanese Unexamined Patent Application, First Publication, No. Hei 8-101323, the-stress imparting part may be dissolved under wet heat environmental conditions since B2O3 is deliquescent. Accordingly, a concave portion may be generated in the stress imparting part. If a concave portion is generated in the stress imparting part, the polarization plane preserving property of the optical fiber is deteriorated and a polarization crosstalk may be induced.
SUMMARY OF THE INVENTION An object of the present invention is to provide a polarization plane preserving optical fiber having an excellent polarization plane preserving property in which no concave portion is generated in its stress imparting part even under wet heat conditions.
The above object may be achieved by an optical fiber for preserving plane of polarization including a cladding and a stress imparting part disposed in the cladding, the stress imparting part comprising a base material including B2O3. The average concentration of B2O3 in the base material of the stress imparting part is in a range between about 17 and 21 wt. %, and the maximum concentration of B2O3 in the base material is in a range between about 17 and 22 wt. %.
According to the above optical fiber for preserving plane of polarization, since the average concentration of B2O3 in the base material of the stress imparting part is in a range between about 17 and 21 wt. %, and the maximum concentration of B2O3 in the base material is in a range between about 17 and 22 wt. %, the stress imparting part is not degraded even under wet heat conditions. Accordingly, the optical fiber has excellent polarization plane preserving properties, and hence, its polarization crosstalk value is not lowered. Also, cracks are not generated in the optical fiber due to the difference in the thermal expansion coefficient of the interface between the stress imparting part and the cladding.
BRIEF DESCRIPTION OF THE DRAWING Some of the features and advantages of the invention having been described, and others will become apparent from the detailed description which follows, and from the accompanying drawing, in which:
FIG. 1 is a diagram showing a cross-sectional view of a PANDA type optical fiber for preserving plane of polarization.
DESCRIPTION OF THE PREFERRED EMBODIMENTS The invention summarized above and defined by the enumerated claims may be better understood by referring to the following detailed description, which should be read with reference to the accompanying drawings. This detailed description of particular preferred embodiments, set out below to enable one to build and use particular implementations of the invention, is not intended to limit the enumerated claims, but to serve as particular examples of the invention.
The polarization plane preserving optical fiber according to an embodiment of the present invention has a structure which is substantially the same as that of a conventional polarization plane preserving optical fiber shown in FIG. 1. Accordingly, hereinafter explanation of the present invention will be made using the PANDA type structure shown in FIG. 1 as an example. Also, the same numerals shown in FIG. 1 are used for purposes of explanation. The stress imparting parts 3 may be made of a glass including B2O3, and according to the embodiment of the present invention, the average concentration of B2O3 at the stress imparting part 3 is in a range between about 17 and 21 wt. % and the maximum concentration of B2O3 is in a range between about 17 and 22 wt. %. In this specification, the terms �average concentration� and �maximum concentration� mean an average concentration and a maximum concentration, respectively, at a cross section of a base material of the stress imparting part which is orthogonal to a base material of the optical fiber.
If the average concentration of B2O3 in the base material of the stress imparting part 3 is less than 17 wt. %, sufficient stress cannot be applied to the core 1 and the plane of polarization is not preserved. Also, if the average concentration of B2O3 exceeds 21 wt. %, the stress imparting part 3 is degraded due to the deliquescence of B2O3, and it becomes difficult to preserve the plane of polarization. Moreover, if the maximum concentration of B2O3 in the base material of the stress imparting part 3 is less than 17 wt. %, sufficient stress cannot be applied to the core 1 and the plane of polarization is not preserved. Further, if the maximum concentration of B2O3 exceeds 22 wt. %, the stress imparting part 3 is degraded due to the deliquescence of B2O3, and it becomes difficult to preserve the plane of polarization.
According to the embodiment of the present invention, the base material of the stress imparting part 3 of a rod shape having the concentrations of B2O3 mentioned above is inserted into two holes formed at predetermined positions of a glass base material for cladding, and is then withdrawn while being heated to produce a polarization plane preserving optical fiber.
According to the embodiment of the present invention, it is not necessary that the concentration of B2O3 be the highest at the center of the stress imparting part 3. Also, it is not necessary that the concentration of B2O3 at the periphery portion of the stress imparting part 3 be lower than that in the central portion thereof. That is, it is not necessary to create a concentration distribution in the stress imparting part 3. For this reason, the base material for the stress imparting part 3 may be easily produced.
Note that although the polarization plane preserving optical fiber 4 shown in FIG. 1 is a PANDA type polarization plane preserving optical fiber, the application of the present invention is not limited to the PANDA type and may be applied to any type of the polarization plane preserving optical fiber, such as the bow tie type and the oval jacket type, as long as the optical fiber has the stress imparting part 3.
EXAMPLES 1-5 A base material for the stress imparting part 3 including a B2O3 component shown in Table 1 was inserted in two holes formed at predetermined positions of a glass base material for the cladding 2, and was withdrawn to produce a polarization plane preserving optical fiber of Examples 1-5 and Comparative Examples 1-5.
In Examples 1-5, the average concentration of B2O3 in the base material for the stress imparting part 3 was in a range between about 17 and 21 wt. % and the maximum concentration of B2O3 was in a range between about 17 and 22 wt. %. On the other hand, in Comparative Examples 1-5, the maximum concentration of B2O3 in the base material for the stress imparting part 3 exceeded 22 wt. %.
The polarization crosstalk values of these polarization plane preserving optical fibers were measured in order to evaluate the double refractive properties thereof. The polarization crosstalk value means an output ratio from an X polarization when the X polarization is input into the optical fiber and is passed through 100 m of the fiber. In practice, the end portion of each of the optical fibers in Examples 1-5 and Comparative Examples 1-5 was polished and a connector was attached to measure the crosstalk value thereof.
It is noted that no cracks were generated at the interface between the outer periphery portion of the stress imparting part 3 and the cladding 2 in both Examples 1-5 and Comparative Examples 1-5 after the connector was attached to the fiber.
A part of the optical fibers of Examples 1-5 and Comparative Examples 1-5 was cut out and was left for 200 hours in an environmental testing device set at a temperature of 80� C. and a relative humidity of 95%. After this, the parts of the optical fibers were removed from the environmental testing device, and the cross section of the end portion of each of the optical fibers was measured using a surface roughness meter in order to examine the degree of degradation. A total of ten samples for each optical fiber were measured and the average value thereof was calculated and the results are shown in Table 1 below.
B2O3 conc. of base material
Polarization crosstalk value (dB/100 m)
of stress impart part (wt %)
11 C.Ex3
20 C.Ex4
22 C.Ex5
24 *Mean degrad. (μm) = mean of degradation amount (μm) after the wet heat test. As shown in the Table 1, no difference in the polarization crosstalk values was observed between Examples 1-5 and Comparative Examples 1-5 before the attachment of the connectors. However, although the polarization crosstalk values were not varied after the attachment of connectors and no change was observed in the polarization plane preserving property for Examples 1-5, the polarization plane preserving property of optical fibers in Comparative Examples 1-5 was lowered after the attachment of the connectors.
Also, the stress imparting part 3 of the optical fibers in Comparative Examples 1-5, in which the maximum value of the concentration of B2O3 in the base material for the stress imparting part 3 exceeded 22 wt. %, were all degraded after the wet heat test. The degradation amount was basically proportional to the maximum value of the concentration of B2O3. On the other hand, the stress imparting part 3 of the optical fibers in Examples 1-5 were not degraded at all.
In addition, although the concentration of B2O3 in the peripheral portion of the base material for the stress imparting part 3 in Examples 1-5 exceeded 15 wt. %, no cracks were generated in the fibers.
According to the optical fiber for preserving the plane of polarization of the present invention, since the average concentration of B2O3 in the base material of the stress imparting part is in a range between about 17 and 21 wt. %, and the maximum concentration of B2O3 in the base material is in a range between about 17 and 22 wt. %, the stress imparting part of the optical fiber is not degraded even under wet heat conditions. Accordingly, the optical fiber has an excellent polarization plane preserving property, and hence, its polarization crosstalk value is not lowered. Also, cracks are not generated in the optical fiber due to the difference in the thermal expansion coefficient of the interface between the stress imparting part and the cladding.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS4664473 *Apr 1, 1985May 12, 1987Corning Glass WorksOptical fiber formed of MgO--Al.sub.2 O.sub.3 --SiO.sub.2 glassUS4913521 *Dec 2, 1988Apr 3, 1990Nippon Telegraph And Telephone CorporationSingle-polarization optical fiberEP0484659A2Sep 11, 1991May 13, 1992Corning IncorporatedMethod of making polarization retaining fiberJPH01222208A Title not availableJPH01237507A Title not availableJPH01257149A Title not availableJPH08101323A Title not availableJPS61215225A Title not availableJPS63206710A Title not available* Cited by examinerNon-Patent CitationsReference1Kikuchi, Y., "Characteristics of Long Length and Low-Loss Polarization Maintaining Optical Fibers," 12<th >European Conference on Optical Communication (ECOC) Barcelona, Sep. 22-25, 1986, pp. 235-238.2Kikuchi, Y., "Characteristics of Long Length and Low-Loss Polarization Maintaining Optical Fibers," 12th European Conference on Optical Communication (ECOC) Barcelona, Sep. 22-25, 1986, pp. 235-238.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS7110647 *Aug 3, 2004Sep 19, 2006NufernMultimode polarization maintaining double clad fiberUS7289687 *Sep 10, 2004Oct 30, 2007Fujikura Ltd.Polarization-maintaining optical fiber* Cited by examinerClassifications U.S. Classification385/123, 385/125, 385/127International ClassificationG02B6/024, G02B6/10, C03B37/012Cooperative ClassificationG02B6/105, C03B37/01217, C03B2203/31European ClassificationC03B37/012B2B, G02B6/10PLegal EventsDateCodeEventDescriptionJul 6, 2011FPAYFee paymentYear of fee payment: 8Jul 20, 2007FPAYFee paymentYear of fee payment: 4Jan 14, 2002ASAssignmentOwner name: FUJIKURA LTD., JAPANFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SHAMOTO, NAOKI;HIMENO, KUNIHARU;WADA, AKIRA;REEL/FRAME:012508/0867Effective date: 20020104Owner name: FUJIKURA LTD. 5-1, KIBA 1-CHOME, KOHTOH-KUTOKYO, (Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SHAMOTO, NAOKI /AR;REEL/FRAME:012508/0867RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services©2012 Google