Patent US6890462 - Foam laminate for mold in place seating component - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsA laminate structure for making a cushioned component for a vehicle interior, such as a seat cushion or head rest, has a high density foam bonded to an interior surface of a seat cover material. After the laminate structure is formed into a desired shape for the cushioned component, it is inserted into...http://www.google.com/patents/US6890462?utm_source=gb-gplus-sharePatent US6890462 - Foam laminate for mold in place seating componentAdvanced Patent SearchPublication numberUS6890462 B2Publication typeGrantApplication numberUS 10/164,352Publication dateMay 10, 2005Filing dateJun 6, 2002Priority dateJun 6, 2002Fee statusLapsedAlso published asUS20030228455, WO2003103920A1Publication number10164352, 164352, US 6890462 B2, US 6890462B2, US-B2-6890462, US6890462 B2, US6890462B2InventorsMichael H. Panczyk, Andrew M. Thompson, Richard C. Meyer, Paul HaslangerOriginal AssigneeFoamex L.P.Export CitationBiBTeX, EndNote, RefManPatent Citations (16), Referenced by (11), Classifications (12), Legal Events (15) External Links: USPTO, USPTO Assignment, EspacenetFoam laminate for mold in place seating component
US 6890462 B2Abstract
1. In a method of making a cushioned component including the steps of(a) providing a cover having an exterior surface which is to present the major exterior appearance of the cushioned component; (b) placing the cover within a mold so that the exterior surface of the cover is facing a mold surface of the mold having a shape corresponding with the desired exterior surface shape of the cushioned component; (c) introducing a foamable material into the mold while the cover is within the mold; and (d) curing the foamable material as said cover is held within the mold, wherein the improvement comprises: (e) laminating a high density foam sheet having a density of at least 4 lbs/ft3 to the interior surface of the material forming the cover prior to placing the cover into the vacuum mold, wherein the high density foam sheet has an air permeability of from 5 to 100 ft3/ft2 minute.
2. The method of claim 1, wherein the high density foam has a density of from 4 lbs/ft3 to 15 lbs/ft3.
3. The method of claim 1, wherein the high density foam has a density of from 5 to 10 lbs/ft3.
4. The method of claim 1, wherein the high density foam is a polyurethane foam.
5. The method of claim 1, wherein the high density foam is created by felting.
6. The method of claim 1, wherein the high density foam has a 25% CFD in the range of 1.0 to 8.0 psi.
7. The method of claim 1, wherein the high density foam has a 25% CFD in the range of 2.0 to 8.0 psi.
8. The method of claim 1, wherein the cushioned component is selected from the group consisting of: seat back, seat cushion, head rest and arm rest.
9. The method of claim 1, further comprising: (f) applying a vacuum to the mold so as to draw the exterior surface of the cover into conformity with the mold surface of the mold having said shape corresponding to the desired exterior surface shape of the cover so that said cover is brought generally into conformity with its desired shape.
10. The method of claim 1, wherein the cover is formed from a material that is perforate between the interior and exterior surfaces thereof.
11. The method of claim 1, wherein the cover is formed from a material selected from the group consisting of: upholstery fabrics, vinyl and leather, and combinations thereof.
12. The method of claim 1, wherein the foamable material is introduced into the mold before the mold is closed.
13. The method of claim 1, wherein the formable material is introduced into the mold after the mold is closed.
This invention relates to covers for mold in place seating components used in the construction of vehicle seating, and more particularly to fabric-foam laminates forming such covers, which covers are placed within a contoured mold and filled with a foaming material that cures within the mold to adopt the final cushion shape of the seating component.
Most vehicle seats comprise a rigid frame assembly that includes a seat cushion section and a seat back section. Frequently, the seat cushion section supports a seat cushion formed of cushioning foamed material. A cover assembly is provided that includes a seat cushion panel that engages the foamed material of the seat cushion and a skirt extending from the periphery of the cover panel so as to cover the frame. For a seat back, the foam material is positioned on the front side of the frame and the cover assembly is formed as a bag that includes a front panel having an interior surface that engages the forward surface of the foam material and an exterior surface which is engaged by the back of the occupant when seated in the vehicle. A rear panel usually is provided that extends around and over the back of the frame.
The cushioning foam material within the cover assembly may be foamed in place. The cover is retained in its final desired contoured shape in the interior space within a mold. A shot of liquid foam-forming ingredients is injected into the cover while in the mold. The foam is allowed to cure while held in the mold so as to adopt the shape of the mold interior. Once the foam is cured, the final seating component or seat cushion assembly is removed from the mold.
If a vacuum mold is used, vacuum molding of the cover panel for seating components requires that the cover be made of a material that includes an impermeable layer. Most commonly, a thin layer of foam is laminated to the back surface of the fabric cover panel. In turn, an imperforate layer, such as a 2 mil thick layer of polyurethane film, is bonded or adhered to the thin foam layer. Thus, the thin foam layer is sandwiched between the rear surface of the fabric cover panel and the thin imperforate film layer.
The cover panel that is to receive the liquid foam-forming material during the foam in place molding most often is sewn together to create the seating component shape. The sewing frequently is performed at a different location from the molding operation. When sewing, it is possible for the imperforate film to be punctured. The film may also be weakened or punctured during transport. Any holes or cracks in the imperforate film allow liquid foam forming material to penetrate or seep through the imperforate film and contact the cover panel. Upon curing, the material forms hard spots in the cover. Hard spots are considered defects that may cause the cover panel to be rejected. In severe cases, foam even may strike through to the outer surface of the fabric, thus causing an unacceptable visual appearance.
Applying the imperforate film to the foam-cover panel laminate represents a further manufacturing step—adding time and expense to the seating component manufacture. In addition, the sewn seams of the cover panel necessarily puncture the imperforate film and may need to be covered with a tape or film, which is yet another processing step.
As one suggested solution, U.S. Pat. No. 5,468,434 proposes sewing the thin foam layer-fabric cover panel into the form of the desired seating component, then placing the imperforate film adjacent to the foam layer just before closing the mold for the foam in place operation, and heating the film to cure and bond it to the foam layer. Thereafter, the liquid foam forming material is introduced into the mold.
As another proposal, U.S. Pat. No. 4,959,184 suggests that penetration through the fabric panel can be prevented by predetermined careful control of the pressure within the mold cavity during the foam in place operation.
The industry thus continues to seek an economical solution to the bleed through/strike through problems encountered with foam in place seating component molding.
The invention is a laminate structure for making a cushioned seat component particularly useful for foam in place molding of automotive seating components, although such laminate may also be useful for fabricating trim or other interior components in motor vehicle passenger compartments. A high density foam, which has a density of at least 4 lbs/ft3, preferably from 4 to 12 lbs/ft3 and most preferably from 5 to 10 lbs/ft3, and which has an air permeability of from 5 to 100 ft3/ft2 minute, preferably 5 to 65 ft3/ft2 minute, most preferably 5 to 50 ft3/ft2 minute, is bonded to the interior surface of a cover material, such as an upholstery fabric or vinyl or combination of such materials, to form the laminate structure. The high density foam preferably has a 25% CFD in the range of 1.0 to 8.0 psi, more preferably 1.5 to 8.0 psi, most preferably 2.0 to 6.0 psi. Preferably, the high density foam is a polyurethane foam. A particularly preferred high density foam is a felted polyurethane foam.
This laminate structure is insertable into a mold, which can be but is not required to be a vacuum mold, having a mold surface with a shape corresponding with a desired exterior surface shape of at least a portion of the cushioned seat component or interior vehicle component. Representative seat components are seat backs, seat cushions, head rests and arm rests. The laminate structure is inserted into the mold so that the exterior surface of the cover material is positioned adjacent to the mold surface. Most often, the cover material is an upholstery fabric that is perforate between the interior and exterior surfaces thereof.
A second aspect of the invention is a method of making a cushioned component. The known foam in place method for making a cushioned component includes the steps of (a) providing a cover having an exterior surface which is to present the major exterior appearance of the cushioned component; (b) placing the cover within a mold so that the exterior surface of the cover is facing a mold surface of the mold having a shape corresponding with the desired exterior surface shape of the cushioned component; (c) introducing a foamable material into the mold while the cover is within the mold; and (d) curing the foamable material as said cover is held within the mold. The improvement according to this aspect of the invention comprises: (e) laminating a high density foam sheet to the interior surface of the material forming the cover prior to placing the cover into the mold. The cover material may be an upholstery fabric or vinyl, or a combination or leather.
The molding process may also include the step of: (f) applying a vacuum to the mold so as to draw the exterior surface of the cover into conformity with the mold surface of the mold having said shape corresponding to the desired exterior surface shape of the cover so that said cover is brought generally into conformity with its desired shape. With such step (f) it is preferable to have a cover that is formed from a material that is perforate between the interior and exterior surfaces thereof.
The high density foam sheet has an air permeability of from 5 to 100 ft3/ft2 minute, preferably from 5 to 50 ft3/ft2 minute, and a density of at least 4 lbs/ft3, preferably from 4 lbs/ft3 to 15 lbs/ft3, most preferably from 5 to 10 lbs/ft3. The high density foam also preferably has an 25% CFD in the range of 1.0 to 8.0 psi, more preferably 1.5 to 8.0 psi, most preferably 2.0 to 6.0 psi.
The high density foam may be a polyurethane foam. A particularly preferred high density foam is created by felting a polyurethane foam.
The cushioned components frequently molded in such process include seat backs, seat cushions, head rests and arm rests. It would also be possible to adapt this molding process for use with interior trim components for motor vehicle passenger compartments.
The invention will be more fully understood by referring to the detailed specification and claims taken in connection with the following drawings.
FIG. 1 is an enlarged sectional view of a mold assembly used in making a seat cushion component; and
FIG. 2 is an enlarged fragmentary sectional view taken along line 2—2 of FIG. 1 showing the laminate structure according to the invention.
Referring first to FIG. 1, a mold assembly 10 is used to mold a foam cushion 32 onto a cover material 20 to form a vehicle seat. A vehicle seat back is formed in a differently shaped mold assembly, but the same principles apply equally to each type of mold assembly. The variations in processing relate to the particular configuration of the seat cover and cushion.
The seat cover 20 includes a main seat panel and a skirt 34 which is sewn to the periphery of the seat panel by a seam including a welting strip 36. The cover 20 is a laminate formed from a high density foam sheet 26 laminated to an upholstery fabric sheet 28.
As shown in FIG. 1, the mold assembly 10 includes both an upper vacuum mold part 12 and a lower vacuum mold part 14, with a peripheral mold part 22. The lower mold part 14 includes vacuum openings 24 which convert the mold part into a vacuum mold 10.
The vacuum mold 10 includes a mold surface 16, which is shaped to define the configuration of the upper exterior surface of the seat panel. The cover 20 is inserted into the mold onto the mold surface 16. The exterior surface of the fabric material 28 is placed in contact with the mold surface 16 and the high density foam layer is directed toward the mold interior.
The peripheral mold part 22 is pivoted to engage the cover 20 along the periphery of the seat cover panel. The upper mold part 12 is brought into contact with the peripheral mold part 22 to close the mold. Thereafter, a vacuum is drawn within the mold to conform the shape of the cover 20 to the contour of the mold surface 16. Foamable expandable cushioning material, such as a mixture of polyurethane foam forming ingredients, is introduced into the mold cavity and onto the upwardly facing interior surface of the seat panel 20. As the foamable cushioning material is allowed to expand and cure while held within the mold cavity, it adopts the desired vehicle seat cushion contoured shape. After the foamable cushioning material has cured, the cover with the cushioning material thereon is removed from the mold assembly and mounted on the seat cushion frame.
The molding process can be varied. For example, it is not always required to draw a vacuum within the mold to conform the shape of the cover 20 to the contour of the mold surface 16. Some upholstery materials can be overly distorted when tension forces are applied due to such a vacuum. In addition, the foamable cushioning material may be introduced into a portion of the mold cavity before the mold is closed. Injecting the foamable cushioning material in this manner places less pressure on the upholstery material that forms the cover and results in less stretching or distortion damage to the upholstery material.
FIG. 2 shows the laminate structure according to the invention. A high density foam 26 is bonded to the interior surface of the fabric cover material 28. Alternatively, the fabric cover material may be a material selected from known upholstery materials, including cloth, vinyl and leather, or a combination of these materials.
Preferably the foam 26 is bonded to the cover material 28 by flame lamination in which the foam is heated to soften and polymerize its outer surface and then that surface is compressed against the fabric cover surface. As the foam cools, the bond between the foam and the fabric is formed. Other suitable bonding techniques may be used.
High density foams useful for the foam 26 of the laminate structure have a density of at least 4 lbs/ft3, preferably in the range of 4 to 15 lbs/ft3, most preferably in the range of 5 to 10 lbs/ft3. The high density foams have an air permeability of from 5 to 100 ft3/ft2 minute, preferably from 5 to 65 ft3/ft2 minute, and most preferably from 5 to 50 ft3/ft2 minute. Air permeability was measured using the procedure set forth in ASTM D 737, in which air is drawn through a foam sample of selected dimension using a Frazier Precision Instrument permeability testing machine. The high density foams have a compression force deflection (25% CFD) of from 1.0 to 8.0 psi, preferably from 1.5 to 8.0 psi, most preferably from 2.0 to 6.0 psi. 25% CFD was measured using the procedure set forth in ASTM D 3574. 25% CFD or “compression force deflection” is a measure of the load-bearing properties of the foam and is calculated by dividing the force required to depress a circular platen into a 2″�2″ foam sample to deflect the foam to 25% of its original foam height by the cross-sectional area of the sample. Thus, the units for CFD are pounds per square inch or “psi”.
A particularly preferred high density foam is prepared by felting. Felted foams are compressed or densified under heat and pressure to a fraction of their original thickness. For example, a polyurethane foam with a 2.2 lb/ft3 density can be felted to one-fifth of its starting thickness from 15 mm to 3 mm thick (sometimes called “Firmness 5”). The density of such foam after felting was five times its original density or 11 lb/ft3. Typically, to create a felted foam, the foam is compressed for from 10 to 60 minutes and heated to temperatures from 350� F. to 360� F. A compression ratio less than 1 to 2 may not result in a uniform structure, and such felted foam may not be compressed evenly even though it may take a permanent set. Compression ratios preferably exceed from 1 to 2, and range up to from 1 to 20. Greater compression of felted foams is possible.
During the felting process, the cellular polymer strand network is crushed to a more unidirectional state, where the strands are oriented more in parallel. This is sometimes called an anisotropic cell structure. Felted foams generally have lower air permeability than the starting foam prior to felting. This air permeability means that some of the foaming cushioning material will penetrate into the felted foam strand network of the laminate structure during molding, which more evenly distributes the foaming pressure. The air permeability also allows gases produced by the foam-forming reaction to penetrate evenly over the felted foam surface area, rather than concentrating pressure at a single point. Hence, the felted foam barrier is not subject to puncture or to forming pin holes that would concentrate pressure and lead to failure such as occurs with the polyurethane film barriers used in the prior art processes. Nevertheless, as compared to lower density foams, the felted foam with lower air permeability provides a better barrier against strike through.
Polyurethane foams are prepared generally by reacting one or more polyols with one or more polyisocyanates in the presence of one or more catalysts, blowing agents, foam stabilizers or surfactants and optionally other foaming aids.
The polyisocyanates include aromatic and aliphatic polyisocyanates each containing at least two isocyanate groups in a molecule, and modified products thereof. Such organic isocyanate compounds include aromatic, aliphatic, and cylcoaliphatic polyisocyanates and combinations thereof. The toluene diisocyanates most suitable for use are 2,4 toluene diisocyanate and 2,6 toluene diisocyanate, and mixtures thereof. Commercially available toluene diisocyanates generally constitute one of the following isomer blends: 80% 2,4 toluene diisocyanate with 20% 2,6 toluene diisocyanate; or 65% 2,4 toluene diisocyanate with 35% 2,6 toluene diisocyanate.
Catalysts include amine catalysts, such as diethylene diamine and triethylene diamine, imidazoles, and tin catalysts, such as stannous octoate. Catalysts are preferably present in amounts from 0.1 to 2.0 parts by weight of amine catalyst and 0 to 2.0 parts by weight of pure tin catalyst, based on 100 parts by weight of the polyol component. Other catalysts may be included in the foam-forming mixture, such as gel catalysts often used as replacements for tin catalysts, including zinc octoate or potassium octoate. Cross-linkers, such as diethanol amine, also may be incorporated into the foam-forming mixture.
Stabilizers include silicone foam stabilizers, and may be present in amounts from 0.1 to 2.0 parts by weight, based on 100 parts by weight of the polyol component.
Water is added as a blowing agent, typically in an amount from 1.0 to 5.0 parts by weight per 100 parts by weight of the polyol component. Water is the preferred blowing agent, but auxiliary blowing agents may be introduced into the foam-forming mixture in some circumstances.
A representative polyurethane foam-forming mixture suitable for preparing a high density foam barrier according to the invention is:
80 Parts Polyol-SPECFLEX NC 630* (base polyol) 20 Parts Polyol-SPECFLEX NH 710* (polyether graft polyol) 1.4 Parts Water (blowing agent) 1.5 Parts Diethanol Amine (cross-linker) 0.25 Parts DABCO 33LV+ (catalyst) 0.1 Parts NIAX A-1^(catalyst) 1.5 Parts DC5043+ (silicone surfactant) 100 index VORANATE* (toluene diisocyanate) *Dow Chemical + Air Products and Chemicals ^Crompton/Osi The components are concurrently introduced to a mixing head and mixed together to cause a foaming reaction. Extra air or carbon dioxide may be incorporated into the mixture at the mix head to control the foam cell diameter in the resulting foam. The mixture is then introduced into a mold or onto a moving conveyor as is known in the industry. The foaming mixture is allowed to rise and cure. Thereafter, the foam is cut to a desired thickness before bonding to a cover material. If the density is not sufficiently high for the foam to be used as a barrier foam in the invention, the foam may be felted before it is bonded to a cover material to form a laminate structure for use when making a cushioned component.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3929948 *Oct 19, 1973Dec 30, 1975Gen Tire & Rubber CoMethod for fabricating impact absorbing safety structureUS4138283Sep 1, 1976Feb 6, 1979Textron Inc.Process for producing fabric-backed cushioning materialUS4247347Mar 19, 1979Jan 27, 1981Lischer James FProcess for molding cloth including a fabric layer by heating to at least the greater of the set or softening temperature the stitches thereof having never been set, and molding a cloth covered foam filled productUS4923653 *Dec 13, 1988May 8, 1990Ikeda Bussan Co., Ltd.Method of molding skin-covered foamed plastic articleUS4959184 *Oct 20, 1988Sep 25, 1990Ikeda Bussan Co., Ltd.Method of producing skin-covered foamed plastic articleUS4976414 *Oct 20, 1988Dec 11, 1990Ikeda Bussan Co., Ltd.Method of producing skin-covered foamed plastic articleUS5053271Oct 27, 1989Oct 1, 1991Ikeda Bussan Co., Ltd.Skin covered foamed plastic articleUS5242587Jul 14, 1992Sep 7, 1993Analytic Systems Laboratories, Inc.Filter with porous media and electrostatic and magnetic platesUS5294386Jun 24, 1991Mar 15, 1994Roth Freres, S.A.Process for the production of padding of polyurethane foam cast in situ in a textile coveringUS5468434 *Mar 1, 1994Nov 21, 1995Atoma International Inc.Provision of cover impermeability in mold in place seat component methodUS5582789Oct 17, 1994Dec 10, 1996General Motors CorporationVehicle door panel manufacturing methodUS5611977 *Feb 15, 1996Mar 18, 1997Tachi-S Co., Ltd.Method for forming an armrestUS5614301Apr 15, 1995Mar 25, 1997The United States Of America As Represented By The Secretary Of The ArmyChemical protective fabricEP0822116A2Jul 31, 1997Feb 4, 1998Bridgestone CorporationSeat cushion and process of producing the sameFR2249763A1 Title not availableGB1418235A Title not available* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS7922944Apr 12, 2011L&P Property Management CompanyBlow mold and backfill manufacturing processUS7984893Feb 13, 2006Jul 26, 2011Rco EngineeringReusable support for a contoured surface of a part allowing machining of an opposite side of the partUS8247466 *Apr 21, 2008Aug 21, 2012Fxi, Inc.Variable felted polyurethane foams for sponges and wipesUS8318283Nov 27, 2012L & P Property Management CompanyBlow mold and backfill manufacturing processUS20050280173 *Jun 20, 2005Dec 22, 2005Bayer Materialscience AgProcess for the production of polyurethane molded articlesUS20070166529 *Oct 3, 2006Jul 19, 2007L&P Property Management CompanyBlow mold and backfill manufacturing processUS20070186404 *Feb 13, 2006Aug 16, 2007Rco EnginerringReusable support for a contoured surface of a part allowing machining of an opposite side of the partUS20080036110 *Aug 14, 2007Feb 14, 2008David BrookerFoam in place seat cushion using dual fabric trim cover and featureless toolUS20090001626 *Sep 8, 2008Jan 1, 2009Bayer Materialscience AgProcess for the production of polyurethane molded articlesUS20090264549 *Apr 21, 2008Oct 22, 2009Foamex L.P.Variable felted polyurethane foams for sponges and wipesUS20110165368 *Jul 7, 2011L&P Property ManagementBlow mold and backfill manufacturing process* Cited by examinerClassifications U.S. Classification264/46.8, 264/321, 264/46.6, 264/46.4International ClassificationB29C44/14, B29C44/12Cooperative ClassificationY10T428/249953, B29C44/1209, Y10T156/1031, B29C44/145European ClassificationB29C44/12C, B29C44/14DLegal EventsDateCodeEventDescriptionAug 26, 2002ASAssignmentOwner name: FOAMEX L.P., PENNSYLVANIAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:PANCZYK, MICHAEL H.;THOMPSON, ANDREW M.;MEYER, RICHARD C.;AND OTHERS;REEL/FRAME:013219/0738;SIGNING DATES FROM 20020613 TO 20020809Aug 22, 2003ASAssignmentOwner name: BANK OF AMERICA, N.A., AS ADMINISTRATIVE AGENT, NEFree format text: SECURITY AGREEMENT;ASSIGNOR:FOAMEX L.P.;REEL/FRAME:014384/0525Effective date: 20030818Owner name: SILVER POINT FINANCE, LLC., AS AGENT, CONNECTICUTFree format text: SECURITY AGREEMENT;ASSIGNOR:FOAMEX L.P.;REEL/FRAME:014373/0624Effective date: 20030818Owner name: U.S. BANK NATIONAL ASSOCIATION, MINNESOTAFree format text: FIRST AMENDMENT TO PATENT SECURITY AGREEMENT;ASSIGNOR:FOAMEX L.P.;REEL/FRAME:014421/0542Effective date: 20030818Sep 24, 2004ASAssignmentOwner name: BANK OF AMERICA, N.A., AS ADMINISRATIVE AGENT, NEWFree format text: SECURITY AGREEMENT;ASSIGNOR:FOAMEX L.P.;REEL/FRAME:015177/0754Effective date: 20030818Mar 2, 2007ASAssignmentOwner name: BANK OF AMERICA, N.A., AS COLLATERAL AGENT, NORTHFree format text: FIRST LIEN TERM PATENT SECURITY AGREEMENT;ASSIGNOR:FOAMEX L.P.;REEL/FRAME:018951/0057Effective date: 20070212Mar 7, 2007ASAssignmentOwner name: BANK OF AMERICA, N.A., AS COLLATERAL AGENT, NORTHFree format text: SECOND LIEN TERM PATENT SECURITY AGREEMENT;ASSIGNOR:FOAMEX L.P.;REEL/FRAME:018972/0013Effective date: 20070212Mar 9, 2007ASAssignmentOwner name: FOAMEX L.P., PENNSYLVANIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:SILVER POINT FINANCE, LLC;REEL/FRAME:018972/0891Effective date: 20070212Owner name: FOAMEX L.P., PENNSYLVANIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:U.S. BANK NATIONAL ASSOCIATION;REEL/FRAME:018972/0917Effective date: 20070212Owner name: FOAMEX L.P., PENNSYLVANIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:BANK OF AMERICA, N.A.;REEL/FRAME:018972/0866Effective date: 20070212Mar 15, 2007ASAssignmentOwner name: BANK OF AMERICA, N.A., AS ADMINISTRATIVE AGENT, NEFree format text: REVOLVING CREDIT PATENT SECURITY AGREEMENT;ASSIGNOR:FOAMEX L.P.;REEL/FRAME:019019/0082Effective date: 20070212May 8, 2007ASAssignmentOwner name: FOAMEX L.P., PENNSYLVANIAFree format text: RELEASE OF LIEN ON PATENTS;ASSIGNOR:BANK OF AMERICA, N.A.;REEL/FRAME:019260/0043Effective date: 20070212Owner name: FOAMEX L.P., PENNSYLVANIAFree format text: RELEASE OF LIEN ON PATENTS;ASSIGNOR:SILVER POINT FINANCE, LLC;REEL/FRAME:019260/0261Effective date: 20070212Owner name: FOAMEX L.P., PENNSYLVANIAFree format text: RELEASE OF LIEN ON PATENTS;ASSIGNOR:U.S. BANK NATIONAL ASSOCIATION;REEL/FRAME:019260/0287Effective date: 20070212Nov 17, 2008REMIMaintenance fee reminder mailedMay 10, 2009LAPSLapse for failure to pay maintenance feesJun 30, 2009FPExpired due to failure to pay maintenance feeEffective date: 20090510Jul 20, 2009ASAssignmentOwner name: WACHOVIA BANK, NATIONAL ASSOCIATION, NEW YORKFree format text: SECURITY AGREEMENT;ASSIGNOR:FOAMEX INNOVATIONS OPERATING COMPANY;REEL/FRAME:023056/0120Effective date: 20090612Owner name: WACHOVIA BANK, NATIONAL ASSOCIATION,NEW YORKFree format text: SECURITY AGREEMENT;ASSIGNOR:FOAMEX INNOVATIONS OPERATING COMPANY;REEL/FRAME:023056/0120Effective date: 20090612Jul 28, 2009ASAssignmentOwner name: MP FOAM DIP LLC, NEW YORKFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FOAMEX INTERNATIONAL INC.;FOAMEX L.P.;REEL/FRAME:023015/0187Effective date: 20090611Owner name: MP FOAM DIP LLC,NEW YORKFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FOAMEX INTERNATIONAL INC.;FOAMEX L.P.;REEL/FRAME:023015/0187Effective date: 20090611Aug 14, 2009ASAssignmentOwner name: FOAMEX INNOVATIONS OPERATING COMPANY, PENNSYLVANIAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:FOAMEX INNOVATIONS, INC. (FORMERLY MP FOAM DIP LLC);REEL/FRAME:023094/0786Effective date: 20090728Owner name: FOAMEX INNOVATIONS OPERATING COMPANY,PENNSYLVANIAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:FOAMEX INNOVATIONS, INC. (FORMERLY MP FOAM DIP LLC);REEL/FRAME:023094/0786Effective date: 20090728Dec 2, 2015ASAssignmentOwner name: FXI, INC., PENNSYLVANIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:WELLS FARGO BANK, NATIONAL ASSOCIATION, SUCCESSOR BY MERGER TO WACHOVIA BANK, NATIONAL ASSOCIATION, AS AGENT;REEL/FRAME:037186/0125Effective date: 20151124RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services