Patent US7229254 - Turbine blade with a reduced mass - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsThe invention relates to a turbine comprising at least four stages and to the use of a rotor blade with a reduced mass. In prior art, rotor blades in the fourth stage of a gas turbine, which exceed 50 cm in length, cause problems relating to mechanical strength, as centrifugal forces of too great a magnitude...http://www.google.com/patents/US7229254?utm_source=gb-gplus-sharePatent US7229254 - Turbine blade with a reduced massAdvanced Patent SearchTry the new Google Patents, with machine-classified Google Scholar results, and Japanese and South Korean patents.Publication numberUS7229254 B2Publication typeGrantApplication numberUS 10/501,723PCT numberPCT/EP2002/014499Publication dateJun 12, 2007Filing dateDec 18, 2002Priority dateJan 18, 2002Fee statusLapsedAlso published asDE50202596D1, EP1329592A1, EP1466079A1, EP1466079B1, US20050069411, WO2003060292A1Publication number10501723, 501723, PCT/2002/14499, PCT/EP/2/014499, PCT/EP/2/14499, PCT/EP/2002/014499, PCT/EP/2002/14499, PCT/EP2/014499, PCT/EP2/14499, PCT/EP2002/014499, PCT/EP2002/14499, PCT/EP2002014499, PCT/EP200214499, PCT/EP2014499, PCT/EP214499, US 7229254 B2, US 7229254B2, US-B2-7229254, US7229254 B2, US7229254B2InventorsUlrich Bast, Wolfgang HermannOriginal AssigneeSiemens AktiengesellschaftExport CitationBiBTeX, EndNote, RefManPatent Citations (20), Non-Patent Citations (1), Referenced by (12), Classifications (22), Legal Events (4) External Links: USPTO, USPTO Assignment, EspacenetTurbine blade with a reduced mass
US 7229254 B2Abstract
The invention relates to a turbine comprising at least four stages and to the use of a rotor blade with a reduced mass. In prior art, rotor blades in the fourth stage of a gas turbine, which exceed 50 cm in length, cause problems relating to mechanical strength, as centrifugal forces of too great a magnitude occur during the rotation of the rotor blades. An inventive rotor blade in the fourth row of a gas turbine has a reduced density as a result of a high proportion of a ceramic, thus reducing the centrifugal force.
1. A gas turbine blade for a fourth stage and onward of a multi-stage turbine, the blade comprising:
a metallic root portion;
a platform portion; and
an airfoil portion comprising at least a structural ceramic material for bearing a tensile load to oppose a centrifugal force that develops during rotation of the blade, wherein the root, platform and airfoil are collectively comprised of a plurality of materials in which at least 40% by volume of the materials comprise the structural ceramic material having a density of at most 4 g/cm3, wherein the density by volume provided by the plurality of materials allows providing a length of at least 50 cm for a blade disposed in the fourth stage and onward of the multi-stage turbine.
2. The turbine blade as claimed in claim 1, wherein the turbine blade is arranged in a metallic rotor disk.
3. The turbine blade as claimed in claim 1, wherein the turbine blade has a structural metallic core surrounded by a structural ceramic material.
4. The turbine blade as claimed in claim 3, wherein the metallic core is formed at least in part from a metallic foam.
5. The turbine blade as claimed in claim 1, wherein the ceramic material has a non structural ceramic protective layer arranged over the ceramic material.
6. The turbine blade as claimed in claim 2, wherein the length of the turbine blade is at least 65 cm.
7. The turbine blade as claimed in claim 1, wherein the turbine blade has a metallic skeleton material that functions as a structural frame and is adapted to support a structural ceramic material.
8. The turbine blade as claimed in claim 1, wherein the materials are a ceramic material or a glass material.
9. The turbine blade as claimed in claim 1, wherein the material with the density of at most 4 g/cm3 is a carbon-containing material.
10. A turbine blade for a fourth stage and onward of a multi-stage turbine, the blade comprising:
a root portion connected to a rotor disk;
an airfoil having a first section located adjacent to the root portion, wherein the first section comprises a material having a first density, the airfoil having a second section located adjacent to the first section consisting exclusively of an structural ceramic material having a second density different than the first density and extending at least 80% of the length of the tip portion, wherein the structural ceramic material bears a tensile load to oppose a centrifugal force that develops during rotation of the blade, wherein at least 40% by volume of the first and second sections comprise the structural ceramic material having a density of at most 4 g/cm3, wherein the density by volume achieved over the first and second sections of the airfoil allows providing a length of at least 50 cm for a blade disposed in the fourth stage and onward of the multi-stage turbine.
11. A gas turbine blade for a fourth stage and onward of a multi-stage turbine, the blade comprised of at least one material in which at least 40% by volume of the material has a density of at most 4 g/cm3, wherein the density by volume achieved by the at least one material allows providing a length of at least 50 cm for a blade disposed in the fourth stage and onward of the multi-stage turbine, wherein the at least one material bears a tensile load to oppose a centrifugal force that develops during rotation of the blade.
12. The turbine blade as claimed in claim 11, wherein the turbine blade has a metallic skeleton into which ceramic parts are introduced.
13. The turbine blade as claimed in claim 11, wherein the material with the density of at most 4 g/cm3 is a ceramic material or a glass material.
14. The turbine blade as claimed in claim 11, wherein the material with the density of at most 4 g/cm3 is a carbon-containing material.
15. The turbine blade as claimed in claim 11, wherein the turbine blade has a metallic core surrounded by a ceramic material, the metallic core and ceramic material both adapted to provide structural support.
16. The turbine blade as claimed in claim 15, wherein the metallic core is formed at least in part from a metallic foam.
17. The turbine blade as claimed in claim 11, wherein the ceramic material has a protective layer.
18. A gas turbine blade for a fourth stage and onward of a multi-stage turbine, the blade comprising:
a metallic root; and
a platform comprising a structural ceramic material mechanically interlocked with the root, the platform ceramic material extending radially to form an airfoil, wherein the ceramic material bears a tensile load to oppose a centrifugal force that develops during rotation of the blade.
19. The turbine blade of claim 18 wherein the metallic root comprises one or more affixing ribs at a first portion in correspondence with the platform for establishing the mechanical interlocking with the platform.
20. The turbine blade of claim 19 wherein the metallic root further comprises a second portion extending radially through a portion of the airfoil.
21. The turbine blade of claim 20 wherein the structural ceramic material comprises a volume of at least 40% of the airfoil volume, including the metallic root second portion therein, thereby reducing blade weight to provide a length of at least 50 cm for a blade disposed in the fourth stage and onward of the multi-stage turbine.
22. A gas turbine comprising at least four stages of successively arranged turbine blades and vanes, wherein each stage comprises a row of rotor blades and a row of guide vanes, with the rotor blades having a metallic root part, wherein at least the fourth row of rotor blades comprises rotor blades in which at least 40% by volume of the material has a density of at most 4 g/cm3, so that the mass is substantially reduced compared to a metallic rotor blade, wherein a minimum length of the rotor blades is 50 cm and further wherein at least beyond 80% of the length of a main blade section in a radial direction consists exclusively of ceramic.
This application is the US National Stage of International Application No. PCT/EP02/14499, filed Dec. 18, 2002 and claims the benefit thereof. The International Application claims the benefits of European Patent application No. 02001348.8 EP filed Jan. 18, 2002, both of the applications are incorporated by reference herein in their entirety.
The invention relates to a turbine with at least four stages in accordance with claim 1 and to the use of a turbine blade with a reduced density in accordance with claim 9.
The use of ceramic guide vanes in gas turbines is known from U.S. Pat. No. 3,992,127. Ceramic guide vanes are used because the ceramic has good high-temperature properties. Particularly high temperatures, which only ceramics are able to withstand, occur in particular in the first row downstream of the combustion chamber (first turbine stage), with the turbine blades and vanes in the first row being the smallest.
U.S. Pat. No. 5,743,713 has disclosed a ceramic blade which is inserted into a metallic rotor disk of a turbine.
U.S. Pat. No. 4,563,128 has disclosed a ceramic blade which has a metallic core surrounded on the outside by ceramic and extending as far as a radial end of the blade. The metallic core forms a very high proportion of the volume.
Hitherto, ceramic rotor blades have only been used, by virtue of their high thermal stability, in the temperature-critical stage or stages of a turbine, whereas in the subsequent stages it has been customary to use metallic rotor blades (in particular made from Ni-based alloys or from TiAl alloys).
A significant improvement to the efficiency of gas turbines can be achieved if, at least from the fourth stage onward, the turbine rotor blades are increased in size by, for example, approximately 20% compared to conventional dimensions. This increase in size from the fourth stage onward, however, leads to a considerable increase in the centrifugal forces at the blades if the rotational speed remains unchanged, and these forces represent unacceptable loads on these blades and on the disks to which the blades are secured.
Therefore, it an object of the invention to provide a turbine with an increased efficiency compared to a turbine with conventional blading.
The object is achieved by virtue of the fact that the turbine, in the fourth stage, in each case has rotor blades with a length of at least 50 cm which contain a high proportion of a material with a density of at most 4 g/cm3, and are, for example, made from ceramic, with the result that the mass is significantly reduced compared to standard metallic blading of conventional dimensions. This allows the blade length, or at least the length of the main blade section, to be lengthened considerably compared to metallic blades.
It is even possible to use solid-ceramic or hollow-ceramic blades which are secured to metallic disks of the turbine rotor, as is known from U.S. Pat. No. 5,743,713.
It is also advantageous to use ceramic rotor blades which have a metallic core which is surrounded by ceramic. In this case, the proportion by volume of the ceramic is very high, so that the mass is greatly reduced compared to a purely metallic blade with an optional thin ceramic protective layer.
A further advantage of a more lightweight blade is that the mechanical loading on the disk to which the blade is secured is lower during rotation on account of the lower mass attached thereto.
The figures diagrammatically depict the invention, which is explained in more detail below with further details and advantageous refinements.
FIG. 1 shows a gas turbine,
FIG. 2 shows a partial region of a gas turbine with a fourth rotor blade stage,
FIG. 3 shows a rotor blade and a rotor disk,
FIG. 4 shows a section on line IV-IV in FIG. 3,
FIG. 5 a, b show further exemplary embodiments of a rotor blade.
FIG. 1 diagrammatically depicts a longitudinal section through a turbine, for example a gas turbine 41. However, the invention is not restricted to a gas turbine.
A compressor 47, a combustion chamber 50 and a turbine part 53 are arranged in succession along a turbine shaft which includes a tie rod 4. The turbine part 53 has a hot-gas duct 56. Gas turbine blades and vanes 13, 16 are arranged in the hot-gas duct 56. Rings of guide vanes and rings of rotor blades are provided alternately. The gas turbine blades and vanes 13, 16 are cooled, for example, by combined air and/or steam cooling. For this purpose, by way of example, compressor air is removed from the compressor 47 and fed to the gas turbine blades and vanes 13, 16 via an air passage 63. Steam is also fed to the gas turbine blades and vane 13, 16 via a steam feed 66, for example. This steam preferably originates from a steam turbine of a combined-cycle gas and steam process.
FIG. 2 shows an excerpt from a gas turbine 41. The gas turbine 41 has a turbine shaft with a tie rod 4 which rotates about an axis 7. A plurality of guide vanes 13 and a plurality of rotor blades 16, which are arranged, for example, in the hot-gas duct 56, extend in the radial direction 19, which runs perpendicular to the axis 7. There are at least four rows of rotor blades and, for example, four rows of guide vanes, i.e. there is a total of four stages. The first row of guide vanes may, for example, may be replaced by a special burner arrangement. Just one of the blades 16 in the fourth stage is illustrated here, by way of example.
The rotor blades 16 are, for example, secured to metal disks (25, FIG. 3) on the turbine shaft, held together by the tie rod 4, and rotate with the tie rod 4 about the axis 7.
The guide vanes 13 are secured in a rotationally fixed position to a casing 10 of the gas turbine 41.
A hot gas 22 flows in the direction of the axis 7, from the left to the right in the drawing, as is diagrammatically indicated by an arrow.
The fourth row of rotor blades, as seen in the direction of flow 22, is denoted by V4. The rotor blades in the fourth stage are in each case rotor blades 16 which have a high proportion by volume of their material made up of a material with a density of at most 4 g/cm3 and are made, for example, from ceramic and have a length of at least 50 cm, in particular of at least 65 cm.
Since the density of ceramic materials is in the range from 1.5 to 3.5 g/cm3, and is therefore well below the densities of nickel-base alloys, at 8 g/cm3, and of TiAl alloys, at approximately 4.5 g/cm3, a ceramic rotor blade of this type has a considerable reduction in mass compared to a corresponding metallic rotor blade, so that, when these rotor blades are rotating, lower centrifugal forces occur, in particular at the outer radial end 37 of the rotor blade 16, thereby inducing loading in particular on the root of the rotor blade 16 and its anchoring in the turbine shaft.
By lengthening the turbine rotor blades in the fourth row by, for example, approximately 20% , it is possible to considerably increase the efficiency of gas turbines. Ceramic rotor blades are, for example, made completely from ceramic, in which case the ceramic may advantageously comprise various layers of ceramics. For example, it is possible to use fiber-reinforced CMC oxide ceramics or fiber-reinforced CMC nonoxide ceramics, nonoxidic ceramics, such as for example carbon fibers or SiC fibers in a corresponding carbon or silicon carbide matrix. It is also possible to use oxide systems, e.g. mullite fibers or aluminum oxide fibers in a mullite matrix.
The ceramics may in turn be coated with a protective layer 36 (FIG. 4 a) to prevent corrosion and oxidation, such as those which are known from metallic turbine blades: yttrium-stabilized zirconia, boron nitride, spinels.
FIG. 3 shows a rotor blade 16 with a length L between platform 17 and radial end of the rotor blade 16 which is formed, for example, entirely from ceramic and is inserted into a metallic rotor disk 25 in a manner fixed in terms of rotation. The metallic disk 25 is connected to the tie rod 4 and rotates therewith.
The diameter of the disk 25 is no greater than usual and is also not exposed to the highest temperatures within the hot-gas duct 56, and consequently metal can continue to be used as material for the disk 25, in the same way as in a conventional turbine.
It is also possible to use what are known as hybrid turbine blades, which still have a metallic core but this core is surrounded by a ceramic, as is known, for example, from U.S. Pat. No. 4,563,128. The content of disclosure of this document relating to the structure of the ceramic turbine blade is expressly incorporated in the content of disclosure of the present application. Further types of hybrid blades are conceivable.
FIG. 4 shows an example of a hybrid blade 16. A main blade section 28 at its outer surface consists of ceramic 39. In the interior, there is a metallic core 31, for example formed from a nickel and/or cobalt superalloy. The metallic core 31, by way of example, also forms a root part 34 of the blade 16.
In the radial direction 19, the metallic core 31 does not extend all the way to the radial end 37 of the blade 16, but rather, for example, only extends over for example 70% of the length of the main blade section 28 in the radial direction 19, since otherwise the loads caused by the centrifugal forces at the intended rotational speed of the turbine would exceed the mechanical strength of the metallic core or of the blade root or of the anchoring in the turbine shaft.
The metallic core 31 may at least in part be formed from metallic foam, in order to save further weight.
The proportion by volume of the material formed by the ceramic is amounts to least 40% or, for example, even exceeds that of the metallic core 31, so that the blade 16 has a high proportion by volume of its material formed by ceramic.
The proportion of ceramic 39 may also be located predominantly at the end 37 of the blade 16, since that is where the centrifugal forces are highest (FIG. 5 a).
A remaining part 38 of the blade 16 consists of metal, for example of a nickel and/or cobalt superalloy. The hybrid blade 16 may also be of internally hollow design, in order to further reduce its weight.
It is also possible, as illustrated in FIG. 5 b, to provide a skeleton 40 made from metal, for example from a nickel and/or cobalt superalloy, into which ceramic parts are introduced.
The skeleton 40 comprises, for example, a leading edge 70, which the medium strikes first in the direction of flow, a trailing edge 73, the root part 34 and the tip 76, as well as the radial end 37.
The rotor blade 16 may also be internally hollow and cooled by air and/or steam cooling with or without film-cooling bores.
It has not hitherto been known that ceramic rotor blades with a length that is considerably increased compared to conventional dimensioning, on account of their lower density and the associated reduction in the centrifugal forces, can advantageously be used to increase the turbine efficiency.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3992127Mar 28, 1975Nov 16, 1976Westinghouse Electric CorporationStator vane assembly for gas turbinesUS4063955 *Oct 3, 1975Dec 20, 1977Gte Sylvania IncorporatedLow thermal expansion ceramics of cordierite solid solution and method for producing sameUS4111603 *May 17, 1976Sep 5, 1978Westinghouse Electric Corp.Ceramic rotor blade assembly for a gas turbine engineUS4247259Apr 18, 1979Jan 27, 1981Avco CorporationComposite ceramic/metallic turbine blade and method of making sameUS4285634Aug 9, 1979Aug 25, 1981Motoren-Und Turbinen-Union Munchen GmbhComposite ceramic gas turbine bladeUS4324843 *Feb 13, 1980Apr 13, 1982United Technologies CorporationContinuous length silicon carbide fiber reinforced ceramic compositesUS4563128Feb 17, 1984Jan 7, 1986Mtu Motoren-Und Turbinen-Union Muenchen GmbhCeramic turbine blade having a metal support coreUS4876849 *Feb 28, 1989Oct 31, 1989Mtu Motoren- Und Turbinen-Union Munchen GmbhGas turbine propulsion unit with a gas generatorUS5403153Oct 29, 1993Apr 4, 1995The United States Of America As Represented By The Secretary Of The Air ForceHollow composite turbine bladeUS5720597 *Jan 29, 1996Feb 24, 1998General Electric CompanyMulti-component blade for a gas turbineUS5743713Sep 13, 1996Apr 28, 1998Ngk Insulators, Ltd.Blade, turbine disc and hybrid type gas turbine bladeUS6206634 *Aug 5, 1999Mar 27, 2001Hitachi, Ltd.Steam turbine blade, method of manufacturing the same, steam turbine power generating plant and low pressure steam turbineUS6280550 *Dec 15, 1998Aug 28, 2001General Electric CompanyFabrication of composite articles having an infiltrated matrixUS6514046 *Sep 29, 2000Feb 4, 2003Siemens Westinghouse Power CorporationCeramic composite vane with metallic substructureUS6756131 *Dec 11, 2002Jun 29, 2004Mitsubishi Heavy Industries, Ltd.High temperature corrosion resistant alloy, thermal barrier coating material, and gas turbine using high temperature corrosion resistant alloyEP0980961A1Aug 5, 1999Feb 23, 2000Hitachi, Ltd.Steam turbine blade, method of manufacturing the same, steam turbine power generating plant and low pressure steam turbineFR57426E Title not availableFR999820A Title not availableGB993412A Title not availableGB2027496A Title not available* Cited by examinerNon-Patent CitationsReference1 *Department of Defense Composite Materials Handbook vol. 5 Ceramic Matrix Composites, p. 63 and 227.* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS8075280Dec 13, 2011Siemens Energy, Inc.Composite blade and method of manufactureUS8262345Feb 6, 2009Sep 11, 2012General Electric CompanyCeramic matrix composite turbine engineUS8347636Sep 24, 2010Jan 8, 2013General Electric CompanyTurbomachine including a ceramic matrix composite (CMC) bridgeUS8382436Jan 6, 2009Feb 26, 2013General Electric CompanyNon-integral turbine blade platforms and systemsUS8980435Oct 4, 2011Mar 17, 2015General Electric CompanyCMC component, power generation system and method of forming a CMC componentUS9004873 *Dec 27, 2010Apr 14, 2015Rolls-Royce CorporationAirfoil, turbomachine and gas turbine engineUS9366146Jun 11, 2013Jun 14, 2016General Electric CompanyClosure bucket for turbo-machineUS20090277175 *May 9, 2008Nov 12, 2009Gary Nin AustinSodium injection for advanced steam turbinesUS20100061858 *Mar 11, 2010Siemens Power Generation, Inc.Composite Blade and Method of ManufactureUS20100202873 *Feb 6, 2009Aug 12, 2010General Electric CompanyCeramic Matrix Composite Turbine EngineUS20120163982 *Dec 27, 2010Jun 28, 2012Edward Claude RiceAirfoil, turbomachine and gas turbine engineEP2570594A2 *May 29, 2012Mar 20, 2013General Electric CompanyTurbine bucket with metallic airfoil and ceramic tip cap, and corresponding gas turbine engine* Cited by examinerClassifications U.S. Classification416/229.00A, 416/241.00BInternational ClassificationF01D5/14, F01D5/30, F01D25/00, B23P15/04, F01D5/28Cooperative ClassificationF05D2240/80, F05D2300/2118, F05D2300/22, F05D2300/603, F05D2300/15, F05D2300/21, F01D5/284, F01D5/3084, Y02T50/67, F01D5/288, F01D5/147European ClassificationF01D5/28F, F01D5/30K, F01D5/28C, F01D5/14CLegal EventsDateCodeEventDescriptionJul 15, 2004ASAssignmentOwner name: SIEMENS AKTIENGESELLSCHAFT, GERMANYFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BAST, ULRICH;HERMANN, WOLFGANG;REEL/FRAME:016021/0666;SIGNING DATES FROM 20040609 TO 20040614Jan 17, 2011REMIMaintenance fee reminder mailedJun 12, 2011LAPSLapse for failure to pay maintenance feesAug 2, 2011FPExpired due to failure to pay maintenance feeEffective date: 20110612RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services