Patent US7196451 - Electromechanical resonator and method for fabricating such a resonator - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsAn electromechanical resonator includes a monocrystalline-silicon substrate (S) provided with an active zone (ZA) delimited by an insulating region, a vibrating beam (10) anchored by at least one of its free ends on the insulating region and including a monocrystalline-silicon vibrating central part...http://www.google.com/patents/US7196451?utm_source=gb-gplus-sharePatent US7196451 - Electromechanical resonator and method for fabricating such a resonatorAdvanced Patent SearchTry the new Google Patents, with machine-classified Google Scholar results, and Japanese and South Korean patents.Publication numberUS7196451 B2Publication typeGrantApplication numberUS 10/895,616Publication dateMar 27, 2007Filing dateJul 21, 2004Priority dateJul 25, 2003Fee statusPaidAlso published asUS20050199970Publication number10895616, 895616, US 7196451 B2, US 7196451B2, US-B2-7196451, US7196451 B2, US7196451B2InventorsStephane Monfray, Pascal Ancey, Thomas Skotnicki, Karim SegueniOriginal AssigneeStmicroelectronics SaExport CitationBiBTeX, EndNote, RefManPatent Citations (10), Non-Patent Citations (1), Referenced by (2), Classifications (8), Legal Events (5) External Links: USPTO, USPTO Assignment, EspacenetElectromechanical resonator and method for fabricating such a resonator
US 7196451 B2Abstract
An electromechanical resonator includes a monocrystalline-silicon substrate (S) provided with an active zone (ZA) delimited by an insulating region, a vibrating beam (10) anchored by at least one of its free ends on the insulating region and including a monocrystalline-silicon vibrating central part (12), and a control electrode (E) arranged above the beam and bearing on the active zone. The central part (12) of the beam is separated from the active zone (ZA) and from the control electrode (E).
1. An electromechanical resonator, comprising:
a monocrystalline-silicon substrate provided with an active zone delimited by an insulating region;
a vibrating beam anchored by at least one of its free ends on the insulating region and comprising a monocrystalline-silicon vibrating central part; and
a control electrode arranged above the vibrating beam and bearing on the active zone, the central part of the vibrating beam being separated from the active zone and from the control electrode.
2. The resonator according to claim 1, wherein the vibrating beam is made of doped monocrystalline silicon, and in that the end part or parts of the vibrating beam, by which it is anchored on the insulating region, is or are made of doped polycrystalline silicon.
3. The resonator according to claim 1, including at least one detection electrode connected to the active zone.
4. The resonator according to one of claim 3, including two detection electrodes in contact with the active zone and arranged above the central part, on either side of the control electrode, while being separated from the beam.
5. The resonator according to claim 1, wherein, the space between the vibrating beam, on the one hand, and the substrate and the control electrode, on the other hand, being obtained by selective etching of a sacrificial-material layer, and wherein the resonator includes at least a first encapsulation-material layer provided with access holes for access to the sacrificial-material layer and a second encapsulation-material layer used for plugging the access holes after the sacrificial-material layer has been etched through the access holes.
6. The resonator according to claim 5, further including electrical-contact vias for access to the control electrode and to the vibrating beam.
7. The resonator according to claim 5, wherein the vibrating beam is made of doped monocrystalline silicon, and in that the end part or parts of the vibrating beam, by which it is anchored on the insulating region, is or are made of doped polycrystalline silicon.
a plurality of electromechanical resonators disposed on the circuit supporting substrate, each of the plurality of electromechanical resonators comprising:
9. The integrated circuit according to claim 8, wherein the vibrating beam is made of doped monocrystalline silicon, and in that the end part or parts of the vibrating beam, by which it is anchored on the insulating region, is or are made of doped polycrystalline silicon.
10. The integrated circuit according to claim 8, including at least one detection electrode connected to the active zone.
11. The integrated circuit according to one of claim 10, including two detection electrodes in contact with the active zone and arranged above the central part, on either side of the control electrode, while being separated from the beam.
12. The integrated circuit according to claim 8, wherein, the space between the vibrating beam, on the one hand, and the substrate and the control electrode, on the other hand, being obtained by selective etching of a sacrificial-material layer, and wherein the resonator includes at least a first encapsulation-material layer provided with access holes for access to the sacrificial-material layer and a second encapsulation-material layer used for plugging the access holes after the sacrificial-material layer has been etched through the access holes.
13. The integrated circuit according to claim 12, further including electrical-contact vias for access to the control electrode and to the vibrating beam.
14. The integrated circuit according to claim 13, wherein the vibrating beam is made of doped monocrystalline silicon, and in that the end part or parts of the vibrating beam, by which it is anchored on the insulating region, is or are made of doped polycrystalline silicon.
This application is based upon and claims priority from prior French Patent Application No. 03 09106, filed on Jul. 25, 2003, the entire disclosure of which is herein incorporated by reference.
The invention relates to an electromechanical resonator and to a method for fabricating such a resonator. More particularly, the invention relates to the production of such a resonator in an integrated form, that is to say by using a technology generally used for the production of integrated circuits.
Electromechanical resonators, and in particular those resonators which operate in a bending vibration mode, are conventionally produced in the form of a vibrating element connected to a control electrode, with a detection electrode measuring a characteristic of the integrated circuit, which is associated with the vibration of the vibrating element.
Various techniques may be used for the production of such a resonator. The vibration frequency of the resonator, however, which moreover depends on the dimensions and the mechanical characteristics of the vibrating element, is dictated by the technique which is used.
For example, according to one technique for fabricating an integrated resonator, according to which the vibrating element is formed superficially and is therefore arranged above a semiconductor electronic circuit, the performance of the resonator is relatively limited, particularly because the compatibility requirements of the materials being employed make it necessary to use specific materials for forming the resonator. In particular, the vibrating element can then in general only be made of amorphous silicon, polycrystalline silicon or nitride.
Such resonators hence cannot in general vibrate at frequencies higher than a few tens of MHz.
It is therefore an object of the invention to overcome these drawbacks and to produce an electromagnetic resonator having enhanced performance while maintaining a high level of integration.
The invention therefore provides an electromechanical resonator comprising a monocrystalline-silicon substrate provided with an active zone delimited by an insulating region.
It furthermore includes a vibrating beam anchored by at least one of its free ends on the insulating region and comprising a monocrystalline-silicon vibrating central part, and a control electrode arranged above the beam and bearing on the active zone, the central part of the beam being separated from the active zone and from the control electrode.
Forming the vibrating element actually inside the semiconductor device hence makes it possible to make it from monocrystalline silicon, and therefore to multiply the vibration frequency of the resonator by a factor which may be as much as about 10.
Such a resonator can furthermore be produced by using a technology referred to as “SON” (“Silicon On Nothing”) technology, which allows the principal elements of the resonator to be formed by using techniques of epitaxial growth and etching, which is a particularly precise technique in dimensional terms. It is then possible to control in a particularly precise way the dimensions of the resonator, and in particular of the vibrating beam, and to do so with fabrication tolerances of the order of one nanometer.
According to another characteristic of the invention, it furthermore includes at least one detection electrode connected to the active zone.
For example, it includes two detection electrodes in contact with the active zone and arranged above the central part, on either side of the control electrode, while being separated from the beam.
In one embodiment, the space between the beam, on the one hand, and the substrate and the control electrode, on the other hand, being obtained by selective etching of a sacrificial-material layer, it includes at least a first encapsulation-material layer provided with holes for access to the sacrificial-material layer and a second encapsulation-material layer used for plugging the access holes after the sacrificial-material layer has been etched through the access holes.
Electrical contact vias are also provided for access to the control electrode and to the vibrating beam.
According to another characteristic of the invention, the beam is made of doped monocrystalline silicon, the end part or parts of the beam, by which it is anchored on the insulating region, being made of doped polycrystalline silicon.
The invention also provides a method for fabricating an electromagnetic resonator as defined above, wherein it includes the following steps:
deposition by selective epitaxial growth of a sacrificial-material layer on the active zone of a monocrystalline substrate, which is delimited by an insulating region; deposition by nonselective epitaxial growth of a silicon layer so that this layer covers the underlying sacrificial-material layer and the insulating region; etching of the silicon layer so as to form a beam anchored by at least one of its ends on the insulating region; selective epitaxial growth of the sacrificial-material layer so that the sacrificial-material layer surrounds the beam; formation of at least one electrode above the beam and in contact with the active zone; and removal of the sacrificial-material layer by selective etching with respect to the silicon and the insulator of the insulating region. According to one embodiment, a central control electrode and two lateral detection electrodes are formed.
Furthermore, according to another characteristic of the method according to the invention, after the step of selective epitaxial growth of the sacrificial-material layer, a masking layer is deposited; holes for access to the silicon of the beam are etched; a second masking layer is deposited; and holes for access to the sacrificial material are etched in the second masking layer; and, after the etching of the sacrificial material, a nonconformal insulation-material layer is deposited in order to plug the access holes, and vias for electrical contact with the vibrating beam and the control electrode are formed.
Preferably, the deposition of the insulation material is carried out at a low pressure.
Advantageously, the sacrificial material is silicon-germanium.
According to an advantageous embodiment, during the formation of the vias, contact holes are formed and the holes are filled with an electrically conductive material, and the contact hole intended to form the via for contact with the control electrode is used to carry out localized ion implantation in the control electrode.
Other objects, characteristics and advantages of the invention will become apparent on reading the following description, which is provided solely by way of nonlimiting example and is given with reference to the appended drawings, in which:
FIGS. 1 to 6 are schematic views illustrating the principal successive phases of a method for fabricating an electromagnetic bending resonator according to the invention;
FIG. 7 is a diagram illustrating an alternative embodiment of an electromechanical resonator according to the invention;
FIGS. 8 to 13 are views in schematic section illustrating successive steps of a particular embodiment of a fabrication method according to the invention; and
FIGS. 14 and 15 illustrate another variant of a fabrication method according to the invention.
Referring firstly to FIGS. 1 to 6, the principal phases of an embodiment of a method for fabricating an electromechanical resonator according to the invention will be described.
As represented in FIG. 1, the starting structure for the production of the resonator consists of a silicon substrate S, in which is formed an active zone ZA surrounded by an insulating region STI (Shallow Trench Isolation).
On the basis of this structure, a sacrificial-material layer C1, preferably consisting of silicon-germanium (SiGe), is formed by selective epitaxy above the active zone ZA. A silicon layer C2 is then grown by nonselective epitaxy.
The techniques of growth by selective and nonselective epitaxy are conventional techniques within the scope of a person skilled in the art. They will not therefore be described in detail below. It will, however, be pointed out that these steps make it possible to obtain a localized SiGe layer on the active zone ZA, a monocrystalline-silicon layer on the underlying sacrificial-material layer and a polycrystalline-silicon layer on the insulating region STI which laterally extends the monocrystalline-silicon layer.
The silicon and the sacrificial-material layer are then etched in order to form a beam 10 comprising a central part 12 made of monocrystalline silicon and polycrystalline-silicon end parts 14 and 16, by which the beam is anchored on the insulating region STI, the sacrificial material between the beam and the active zone (FIG. 2) being kept.
As shown by FIGS. 3 and 4, selective epitaxy of the SiGe is carried out during the next step so that this sacrificial material covers the beam 10 as well as the active zone ZA. A control electrode as can be seen in these figures is then formed according to a conventional technique, for example by depositing polycrystalline silicon and etching the electrode E according to a desired contour. The electrode E formed in this way extends over the beam 10 and bears on the active zone ZA. After this step of epitaxial growth of the silicon-germanium and formation of the control electrode E, the sacrificial material is selectively etched. This etching needs to be selective, on the one hand, vis-à-vis the silicon of the control electrode and of the substrate, but also vis-à-vis the insulator of the insulating region STI.
As can be seen in FIG. 5 and in FIG. 6, which represents a view in section on the lines VI—VI in FIG. 5, after this step of selectively removing the silicon-germanium, a beam is obtained which is anchored by its mutually opposite free ends 14 and 16 on the insulating region STI, and the central part 12 which is suspended above the active zone and is separated from the control electrode E by a space corresponding to the thickness of the etched sacrificial-material layer. Likewise, the control electrode E is suspended above the beam while continuing to bear against the active zone.
As is known, this control electrode E is used to cause excitation of the beam, so that it is made to vibrate at a frequency which is dictated, in particular, by the structural characteristics and by the mechanical characteristics of the beam. Owing to the use of monocrystalline silicon for the active part of the beam, that is to say for its central part, a vibration frequency is obtained which may amount to frequencies of the order of one GHz.
The vibration frequency of the beam is measured by using one or more detection electrodes connected to the active zone, for example electrodes capable of measuring the value of the capacitance formed by the gap around the vibrating element 12.
As can be seen in FIG. 7, according to one embodiment, the detection electrodes E′ and E″ are formed simultaneously with the formation of the control electrode (FIG. 3), for example by using a specific photolithography mask and specific etching, so as to form a central control electrode for activation of the vibrating beam 10, and two lateral detection electrodes E′ and E″ arranged on either side of the control electrode E, for detection and measurement of the vibration frequency of the beam 10.
Another embodiment of a method for fabricating an electromechanical resonator according to the invention will now be described with reference to FIGS. 8 to 13.
As can be seen in FIG. 8, the starting structure for this variant corresponds to the phase of the process described above with reference to FIG. 3. In other words, it begins with a starting substrate having an active zone ZA formed in a silicon substrate S and delimited by an insulating region STI on which is anchored a beam 10, the central part 12 of which is made of monocrystalline silicon and the end zones 14 and 16 of which, anchored on the insulating region STI, are made of polycrystalline silicon. The beam is surrounded by sacrificial material consisting of silicon-germanium. A polycrystalline-silicon control electrode E is furthermore formed above the beam 10.
As can be seen in FIG. 9, on the basis of this structure, a first masking layer 18 is deposited on all of the semiconductor device, for example a layer of silicon nitride Si3N4, then this masking layer 18 is etched so as to free the future electrical-contact zones 20 and 22 which will be used for electrical connection of the beam 10.
Referring now to FIG. 10, an oxide layer 24 is subsequently deposited everywhere, and then holes 26 and 28 for access to the sacrificial material are etched.
Selective withdrawal of the silicon-germanium layers is then carried out in order to free the central part 12 of the beam, in order to allow it to vibrate freely (FIG. 11).
Referring now to FIG. 12, a nonconformal insulation-material layer 30 is then deposited everywhere in order to plug the access holes 26 and 28, and planarization of the device is carried out. It will be noted that the insulation-material layer 30 is preferably deposited at a low pressure in order to avoid filling the space surrounding the vibrating part 12 of the beam.
Lastly, with reference to FIG. 13, the vias 32, 34 and 36 for electrical connection of the control electrode and of the beam 10 are formed. As is well known to a person skilled in the art, these vias are produced by forming holes and filling these holes with an electrically conductive material.
It will be noted that the beam is rendered conductive by dopant implantation in the various embodiments described above, for example by implanting a dopant of the same conductivity type as the substrate S.
Referring to FIG. 14, with a view to preventing stray capacitances from being formed on either side of the beam, between the polycrystalline silicon constituting the control electrode E and the silicon constituting the substrate S, the control electrode E is rendered conductive only in a zone 40 located above the vibrating beam 10, this zone being bordered laterally by two insulating zones 42 and 44.
As can be seen in FIG. 15, this arrangement is obtained by using an intrinsic polycrystalline silicon as the constituent material of the control electrode, and by doping the zone 40 of the electrode lying above the beam 10. This implantation is carried out by using the hole 34, before it is filled with an electrically conductive material in order to form the via 34 for electrical connection of the control electrode.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS6275122Aug 17, 1999Aug 14, 2001International Business Machines CorporationEncapsulated MEMS band-pass filter for integrated circuitsUS6469597 *Mar 5, 2001Oct 22, 2002Agilent Technologies, Inc.Method of mass loading of thin film bulk acoustic resonators (FBAR) for creating resonators of different frequencies and apparatus embodying the methodUS6495403 *Oct 5, 2000Dec 17, 2002Stmicroelectronics S.A.Gate-all-around semiconductor device and process for fabricating the sameUS6877209 *Aug 28, 2002Apr 12, 2005Silicon Light Machines, Inc.Method for sealing an active area of a surface acoustic wave device on a waferUS20010016367Dec 28, 2000Aug 23, 2001Ziegler James F.Process for fabricating single crystal resonant devices that are compatible with integrated circuit processingUS20040080243 *Mar 10, 2003Apr 29, 2004Osamu MiyazawaRotation/displacement converting actuatorUS20050003657 *Jul 29, 2004Jan 6, 2005Samsung Electronics Co., Ltd.Semiconductor device having multilevel interconnections and method of manufacturing the sameEP0816861A2May 15, 1997Jan 7, 1998Siemens AktiengesellschaftApparatus for measuring magnetic fieldsFR2799305A1 Title not availableFR2823032A1 Title not available* Cited by examinerNon-Patent CitationsReference1Preliminary Search Report for French Application No. 03 09106 dated May 4, 2004.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS7625772 *Sep 27, 2007Dec 1, 2009Commissariat A L'energie AtomiqueMethod for making an electromechanical component on a plane substrateUS20080076211 *Sep 27, 2007Mar 27, 2008Commissariat A L'energie AtomiqueMethod for making an electromechanical component on a plane substrate* Cited by examinerClassifications U.S. Classification310/311, 310/309International ClassificationH03H9/24, H02N1/00, B81B3/00Cooperative ClassificationH03H9/2405, H03H2009/02511European ClassificationH03H9/24MLegal EventsDateCodeEventDescriptionDec 27, 2004ASAssignmentOwner name: STMICROELECTRONICS SA, FRANCEFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MONFRAY, STEPHANE;ANCEY, PASCAL;SKOTNICKI, THOMAS;REEL/FRAME:015500/0677Effective date: 20041015Feb 16, 2007ASAssignmentOwner name: STMICROELECTRONICS SA, FRANCEFree format text: RE-RECORD TO ADD MISSING INVENTOR TO REEL/FRAME;ASSIGNORS:MONFRAY, STEPHANE;ANCEY, PASCAL;SKOTNICKI, THOMAS;AND OTHERS;REEL/FRAME:018901/0577;SIGNING DATES FROM 20041015 TO 20051122Mar 16, 2007ASAssignmentOwner name: STMICROELECTRONICS SA, FRANCEFree format text: CORRECTIVE ASSIGNMENT TO CORRECT THE CORRECTIVE ASSIGNMENT TO RE-RECORD EXECUTION DATE OF ASSIGNOR SEGUENI FROM 11/22/2005 TO 11/22/2004 PREVIOUSLY RECORDED ON REEL 018901 FRAME 0677;ASSIGNORS:MONFRAY, STEPHANE;ANCEY, PASCAL;SKOTNICKI, THOMAS;AND OTHERS;REEL/FRAME:019024/0451;SIGNING DATES FROM 20041015 TO 20041122Aug 26, 2010FPAYFee paymentYear of fee payment: 4Aug 27, 2014FPAYFee paymentYear of fee payment: 8RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services