Patent US8048325 - Method and apparatus for multilayer photoresist dry development - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inAdvanced Patent SearchPatentsA method for etching an organic anti-reflective coating (ARC) layer on a substrate in a plasma processing system comprising: introducing a process gas comprising ammonia (NH3), and a passivation gas; forming a plasma from the process gas; and exposing the substrate to the plasma. The process gas can,...http://www.google.com/patents/US8048325?utm_source=gb-gplus-sharePatent US8048325 - Method and apparatus for multilayer photoresist dry developmentAdvanced Patent SearchPublication numberUS8048325 B2Publication typeGrantApplication numberUS 11/970,062Publication dateNov 1, 2011Filing dateJan 7, 2008Priority dateMar 31, 2003Fee statusPaidAlso published asUS20080128388Publication number11970062, 970062, US 8048325 B2, US 8048325B2, US-B2-8048325, US8048325 B2, US8048325B2InventorsVaidyanathan Balasubramaniam, Koichiro Inazawa, Rie Inazawa, Rich Wise, Arpan Mahorawala, Siddhartha PandaOriginal AssigneeTokyo Electron LimitedExport CitationBiBTeX, EndNote, RefManPatent Citations (33), Non-Patent Citations (20), Classifications (11), Legal Events (2) External Links: USPTO, USPTO Assignment, EspacenetMethod and apparatus for multilayer photoresist dry development
US 8048325 B2Abstract
A method for etching an organic anti-reflective coating (ARC) layer on a substrate in a plasma processing system comprising: introducing a process gas comprising ammonia (NH3), and a passivation gas; forming a plasma from the process gas; and exposing the substrate to the plasma. The process gas can, for example, constitute NH3 and a hydrocarbon gas such as at least one of C2H4, CH4, C2H2, C2H6, C3H4, C3H6, C3H8, C4H6, C4H8, C4H10, C5H8, C5H10, C6H6, C6H10, and C6H12. Additionally, the process chemistry can further comprise the addition of helium. The present invention further presents a method for forming a bilayer mask for etching a thin film on a substrate, wherein the method comprises: forming the thin film on the substrate; forming an ARC layer on the thin film; forming a photoresist pattern on the ARC layer; and transferring the photoresist pattern to the ARC layer with an etch process using a process gas comprising ammonia (NH3), and a passivation gas.
1. A method of smoothing a sidewall in a multilayer mask on a substrate in a plasma processing system comprising:
forming a multilayer mask on said substrate, said multilayer mask comprising a light-sensitive layer overlying an anti-reflective coating (ARC) layer;
forming a pattern in said light-sensitive layer using a lithography technique;
transferring said pattern to said anti-reflective coating (ARC) layer by performing the following in a plasma processing system:
introducing a process gas comprising one or more gasses collectively containing ammonia (NH3), and a passivation gas;
exposing said substrate to said plasma; and
forming of a passivation film on said sidewall of said multilayer mask prior to transferring said pattern in said multilayer mask to any underlying thin film in order to smooth surface roughness of said sidewall of at least said light-sensitive layer or said anti-reflective coating (ARC) layer.
2. The method as recited in claim 1, wherein said passivation gas comprises a hydrocarbon gas.
3. The method as recited in claim 1, wherein said passivation gas comprises at least one of C2H4, CH4, C2H2, C2H6, C3H4, C3H6, C3H8, C4H6, C4H8, C4Hl0, C5H8, C5Hl0, C6H6, C6Hl0, and C6H12.
4. The method as recited in claim 1, wherein said process gas further comprises helium.
5. The method as recited in claim 1, wherein said passivation gas comprises C2H4, and wherein the process gas flow rate for NH3 is greater than or equal to the process gas flow rate for C2H4.
6. The method as recited in claim 1, wherein said process gas consists of NH3 and C2H4.
7. The method as recited in claim 1, wherein said forming of a passivation film on said sidewall of said multilayer mask occurs during said transferring said pattern to said anti-reflective coating (ARC) layer.
This application is a divisional of and claims the benefit of priority under 35 USC �120 from U.S. Ser. No. 10/640,577, filed Aug. 14, 2003, now U.S. Pat. No. 7,344,991. This application is related to and claims priority to U.S. provisional application Ser. No. 60/458,430 filed on Mar. 31, 2003, and U.S. provisional application Ser. No. 60/484,225 filed on May 5, 2003; the entire contents of which are herein incorporated by reference. This application is related to application 60/435,286, entitled “Method and Apparatus For Bilayer Photoresist Dry Development,” filed on Dec. 23, 2002; the entire contents of which are herein incorporated by reference.
The present invention relates to a method and apparatus for plasma processing a substrate, and more particularly to a method for multilayer photoresist dry development.
During semiconductor processing, a (dry) plasma etch process can be utilized to remove or etch material along fine lines or within vias or contacts patterned on a silicon substrate. The plasma etch process generally involves positioning a semiconductor substrate with an overlying patterned, protective layer, for example a photoresist layer, in a processing chamber. Once the substrate is positioned within the chamber, an ionizable, dissociative gas mixture is introduced within the chamber at a pre-specified flow rate, while a vacuum pump is throttled to achieve an ambient process pressure. Thereafter, a plasma is formed when a fraction of the gas species present are ionized by electrons heated via the transfer of radio frequency (RF) power either inductively or capacitively, or microwave power using, for example, electron cyclotron resonance (ECR). Moreover, the heated electrons serve to dissociate some species of the ambient gas species and create reactant specie(s) suitable for the exposed surface etch chemistry. Once the plasma is formed, selected surfaces of the substrate are etched by the plasma. The process is adjusted to achieve appropriate conditions, including an appropriate concentration of desirable reactant and ion populations to etch various features (e.g., trenches, vias, contacts, etc.) in the selected regions of the substrate. Such substrate materials where etching is required include silicon dioxide (SiO2), low-k dielectric materials, poly-silicon, and silicon nitride.
The present invention relates to a method and apparatus for plasma processing a substrate, and to a method and apparatus for multilayer photoresist dry development. The present invention also relates to the multilayer mask itself.
In one aspect of the invention, a method and apparatus are described for etching an anti-reflective coating (ARC) layer on a substrate in a plasma processing system. A process gas comprising one or more gasses collectively containing ammonia (NH3) and a passivation gas is introduced. A plasma is formed from the process gas in the plasma processing system. The substrate is exposed to the plasma.
In yet another aspect of the invention, a method and apparatus are described for forming a bilayer mask for etching a thin film on a substrate. The thin film is formed on the substrate. An anti-reflective coating (ARC) layer is formed on the thin film. A photoresist pattern is formed on the ARC layer. The photoresist pattern is transferred to the ARC layer by etching the ARC layer using a process gas comprising one or more gasses collectively containing ammonia (NH3) and a passivation gas.
Additionally, a method of smoothing a sidewall in a multilayer mask on a substrate in a plasma processing system comprises: introducing a process gas comprising one or more gasses collectively containing ammonia (NH3), and a passivation gas; forming a plasma from the process gas in the plasma processing system; and exposing the substrate to the plasma, wherein the passivation gas facilitates the formation of a passivation film on the sidewall of the multilayer mask in order to smooth surface roughness of the sidewall.
FIGS. 1A, 1B, and 1C show a schematic representation of a typical procedure for pattern etching a thin film;
FIG. 2 shows a simplified schematic diagram of a plasma processing system according to an embodiment of the present invention;
FIG. 7 presents a method of etching an anti-reflective coating (ARC) layer on a substrate in a plasma processing system according to an embodiment of the present invention;
FIG. 8 presents a method of forming a bilayer mask for etching a thin film on a substrate according to another embodiment of the present invention; and
FIGS. 9A and 9B show a schematic representation of a multilayer mask.
In material processing methodologies, pattern etching comprises the application of a thin layer of light-sensitive material, such as photoresist, to an upper surface of a substrate, that is subsequently patterned in order to provide a mask for transferring this pattern to the underlying thin film on a substrate during etching. The patterning of the light-sensitive material generally involves exposure by a radiation source through a reticle (and associated optics) of the light-sensitive material using, for example, a micro-lithography system, followed by the removal of the irradiated regions of the light-sensitive material (as in the case of positive photoresist), or non-irradiated regions (as in the case of negative resist) using a developing solvent. Multi-layer masks can be implemented for etching features in a thin film. For example, as shown in FIGS. 1A-C, a bilayer mask 6 comprising light-sensitive layer 3 with pattern 2 formed using conventional lithographic techniques and an organic anti-reflective coating (ARC) layer 7 can be utilized as a mask for etching the thin film 4 on substrate 5, wherein the mask pattern 2 in the light-sensitive layer 3 is transferred to the ARC layer 7 using a separate etch step preceding the main etch step for the thin film 4.
In one embodiment, a process gas comprising ammonia (NH3) and a passivation gas is utilized in a method of bilayer photoresist dry development. For example, the passivation gas can comprise a hydrocarbon gas such as at least one of C2H4, CH4, C2H2, C2H6, C3H4, C3H6, C3H8, C4H6, C4H8, C4H10, C5H8, C5H10, C6H6, C6H10, C6H12, or the like.
Although the embodiment above describes the etching of thin film 4 on substrate 5, the etching can be of substrate 5 itself, with or without thin film 4.
According to one embodiment, a plasma processing system 1 is depicted in FIG. 2 comprising a plasma processing chamber 10, a diagnostic system 12 coupled to the plasma processing chamber 10, and a controller 14 coupled to the diagnostic system 12 and the plasma processing chamber 10. The controller 14 is configured to execute a process recipe comprising at least one of the above-identified chemistries to etch an organic ARC layer. Additionally, controller 14 is configured to receive at least one endpoint signal from the diagnostic system 12 and to post-process the at least one endpoint signal in order to accurately determine an endpoint for the process. In the illustrated embodiment, plasma processing system 1, depicted in FIG. 2, utilizes a plasma for material processing. Plasma processing system 1 can comprise an etch chamber.
According to the embodiment depicted in FIG. 3, plasma processing system 1 a can comprise plasma processing chamber 10, substrate holder 20, upon which a substrate 25 to be processed is affixed, and vacuum pumping system 30. Substrate 25 can be, for example, a semiconductor substrate, a wafer or a liquid crystal display. Plasma processing chamber 10 can be, for example, configured to facilitate the generation of plasma in processing region 15 adjacent a surface of substrate 25. An ionizable gas or mixture of gases is introduced via a gas injection system (not shown) and the process pressure is adjusted. For example, a control mechanism (not shown) can be used to throttle the vacuum pumping system 30. Plasma can be utilized to create materials specific to a pre-determined materials process, and/or to aid the removal of material from the exposed surfaces of substrate 25. The plasma processing system 1 a can be configured to process 200 mm substrates, 300 mm substrates, or larger.
Substrate 25 can be, for example, affixed to the substrate holder 20 via an electrostatic clamping system. Furthermore, substrate holder 20 can, for example, further include a cooling system including a re-circulating coolant flow that receives heat from substrate holder 20 and transfers heat to a heat exchanger system (not shown), or when heating, transfers heat from the heat exchanger system. Moreover, gas can, for example, be delivered to the back-side of substrate 25 via a backside gas system to improve the gas-gap thermal conductance between substrate 25 and substrate holder 20. Such a system can be utilized when temperature control of the substrate is required at elevated or reduced temperatures. For example, the backside gas system can comprise a two-zone gas distribution system, wherein the helium gas gap pressure can be independently varied between the center and the edge of substrate 25. In other embodiments, heating/cooling elements, such as resistive heating elements, or thermo-electric heaters/coolers can be included in the substrate holder 20, as well as the chamber wall of the plasma processing chamber 10 and any other component within the plasma processing system 1 a. In the embodiment shown in FIG. 3, substrate holder 20 can comprise an electrode through which RF power is coupled to the processing plasma in process space 15. For example, substrate holder 20 can be electrically biased at a RF voltage via the transmission of RF power from a RF generator 40 through an impedance match network 50 to substrate holder 20. The RF bias can serve to heat electrons to form and maintain plasma. In this configuration, the system can operate as a reactive ion etch (RIE) reactor, wherein the chamber and an upper gas injection electrode serve as ground surfaces. A typical frequency for the RF bias can range from 0.1 MHz to 100 MHz. RF systems for plasma processing are well known to those skilled in the art.
Vacuum pump system 30 can, for example, include a turbo-molecular vacuum pump (TMP) capable of a pumping speed up to 5000 liters per second (and greater) and a gate valve for throttling the chamber pressure. In conventional plasma processing devices utilized for dry plasma etch, a 1000 to 3000 liter per second TMP is generally employed. TMPs are useful for low pressure processing, typically less than 50 mTorr. For high pressure processing (i.e., greater than 100 mTorr), a mechanical booster pump and dry roughing pump can be used. Furthermore, a device for monitoring chamber pressure (not shown) can be coupled to the plasma processing chamber 10. The pressure measuring device can be, for example, a Type 628B Baratron absolute capacitance manometer commercially available from MKS Instruments, Inc. (Andover, Mass.).
Controller 14 comprises a microprocessor, memory, and a digital I/O port capable of generating control voltages sufficient to communicate and activate inputs to plasma processing system 1 a as well as monitor outputs from plasma processing system 1 a. Moreover, controller 14 can be coupled to and can exchange information with RF generator 40, impedance match network 50, the gas injection system (not shown), vacuum pump system 30, as well as the backside gas delivery system (not shown), the substrate/substrate holder temperature measurement system (not shown), and/or the electrostatic clamping system (not shown). For example, a program stored in the memory can be utilized to activate the inputs to the aforementioned components of plasma processing system 1 a according to a process recipe in order to perform the method of etching an organic ARC layer. One example of controller 14 is a DELL PRECISION WORKSTATION 610™, available from Dell Corporation, Austin, Tex.
The spectrometers receive light transmitted through single and bundled optical fibers, where the light output from the optical fibers is dispersed across the line CCD array using a fixed grating. Similar to the configuration described above, light passing through an optical vacuum window is focused onto the input end of the optical fibers via a convex spherical lens. Three spectrometers, each specifically tuned for a given spectral range (UV, VIS and NIR), form a sensor for a process chamber. Each spectrometer includes an independent A/D converter. And lastly, depending upon the sensor utilization, a full emission spectrum can be recorded every 0.1 to 1.0 seconds.
In the embodiment shown in FIG. 4, the plasma processing system 1 b can, for example, be similar to the embodiment of FIG. 2 or 3 and further comprise either a stationary, or mechanically or electrically rotating magnetic field system 60, in order to potentially increase plasma density and/or improve plasma processing uniformity, in addition to those components described with reference to FIG. 2 and FIG. 3. Moreover, controller 14 can be coupled to magnetic field system 60 in order to regulate the speed of rotation and field strength. The design and implementation of a rotating magnetic field is well known to those skilled in the art.
In the embodiment shown in FIG. 5, the plasma processing system 1 c can, for example, be similar to the embodiment of FIG. 2 or FIG. 3, and can further comprise an upper electrode 70 to which RF power can be coupled from RF generator 72 through impedance match network 74. A typical frequency for the application of RF power to the upper electrode can range from 0.1 MHz to 200 MHz. Additionally, a typical frequency for the application of power to the lower electrode can range from 0.1 MHz to 100 MHz. Moreover, controller 14 is coupled to RF generator 72 and impedance match network 74 in order to control the application of RF power to upper electrode 70. The design and implementation of an upper electrode is well known to those skilled in the art.
In the embodiment shown in FIG. 6, the plasma processing system 1 d can, for example, be similar to the embodiments of FIGS. 2 and 3, and can further comprise an inductive coil 80 to which RF power is coupled via RF generator 82 through impedance match network 84. RF power is inductively coupled from inductive coil 80 through a dielectric window (not shown) to plasma processing region 15. A typical frequency for the application of RF power to the inductive coil 80 can range from 10 MHz to 100 MHz. Similarly, a typical frequency for the application of power to the chuck electrode can range from 0.1 MHz to 100 MHz. In addition, a slotted Faraday shield (not shown) can be employed to reduce capacitive coupling between the inductive coil 80 and plasma. Moreover, controller 14 is coupled to RF generator 82 and impedance match network 84 in order to control the application of power to inductive coil 80. In an alternate embodiment, inductive coil 80 can be a “spiral” coil or “pancake” coil in communication with the plasma processing region 15 from above as in a transformer coupled plasma (TCP) reactor. The design and implementation of an inductively coupled plasma (ICP) source, or transformer coupled plasma (TCP) source, is well known to those skilled in the art.
In the following discussion, a method of etching an organic ARC layer utilizing a plasma processing device is presented. For example, the plasma processing device can comprise various elements, such as described in FIGS. 2 through 6, and combinations thereof.
In an embodiment, the method of etching an organic ARC layer comprises NH3 and a hydrocarbon gas such as at least one of C2H4, CH4, C2H2, C2H6, C3H4, C3H6, C3H8, C4H6, C4H8, C4H10, C5H8, C5H10, C6H6, C6H10, C6H12, or the like. For example, a process parameter space can comprise a chamber pressure of 20 to 1000 mTorr, an NH3 process gas flow rate ranging from 50 to 1000 sccm, a hydrocarbon process gas flow rate ranging from 5 to 100 sccm, an upper electrode (e.g., element 70 in FIG. 5) RF bias ranging from 500 to 2000 W, and a lower electrode (e.g., element 20 in FIG. 5) RF bias ranging from 10 to 500 W. Also, the upper electrode bias frequency can range from 0.1 MHz to 200 MHz, e.g., 60 MHz. In addition, the lower electrode bias frequency can range from 0.1 MHz to 100 MHz, e.g., 2 MHz.
In an example, a method of etching an organic ARC layer utilizing a plasma processing device such as the one described in FIG. 5 is presented. However, the methods discussed are not to be limited in scope by this exemplary presentation. Table I presents the critical dimensions of a feature etched in an organic ARC layer utilizing the following exemplary process recipe: Chamber pressure=100 mTorr; Upper electrode RF power=1200 W; Lower electrode RF power=100 W; Process gas flow rate NH3/C2H4=450/50 sccm; a 55 mm electrode spacing between the lower surface of electrode 70 (see FIG. 5) and the upper surface of substrate 25 on substrate holder 20; Lower electrode temperature (e.g., substrate holder 20 in FIG. 5)=20C; Upper electrode temperature (e.g., electrode 70 in FIG. 5)=60C; Chamber wall temperature=50C; Backside helium pressure Center/Edge=10/35 Torr; and an etch time of 180 seconds.
NH3/C2H4 CENTER
Top PR Remaining
Bottom CD/bias - MC
147/−3
Bottom CD/bias - CA
138/−5
134/−9
(Photoresist—PR; Critical dimension—CD).
Table I reports results (for both metal contacts (MC) as well as contacts (CA)) such as thickness of the remaining photoresist following the ARC layer etch, top and bottom critical dimensions for the ARC feature, and the critical dimension bias, wherein the bias indicates the change in CD from top to bottom (i.e. negative bias indicates a CD reduction, and positive bias indicates a CD increase). Additionally, the data is reported at center and edge. The data demonstrates the success of the process in maintaining the CD as well as the potential for reducing the CD.
In an alternate embodiment, the process chemistry can further comprise Helium (He). The introduction of Helium to the process can relieve feature side-wall roughness.
In general, the etch time can be determined using design of experiment (DOE) techniques; however, it can also be determined using endpoint detection. One possible method of endpoint detection is to monitor a portion of the emitted light spectrum from the plasma region that indicates when a change in plasma chemistry occurs due to substantially near completion of the ARC layer etching and contact with the underlying material film. For example, portions of the spectrum that indicate such changes comprise wavelengths of 387.2 nm (carbon-nitrogen (CN)), and can be measured using optical emission spectroscopy (OES). After emission levels corresponding to those frequencies cross a specified threshold (e.g., drop to substantially zero or increase above a particular level), an endpoint can be considered to be complete. Other wavelengths that provide endpoint information can also be used. Furthermore, the etch time can be extended to include a period of over-etch, wherein the over-etch period constitutes a fraction (i.e. 1 to 100%) of the time between initiation of the etch process and the time associated with endpoint detection.
FIG. 7 presents a flow chart of a method for etching an anti-reflective coating (ARC) layer on a substrate in a plasma processing system according to an embodiment of the present invention. Procedure 400 begins in 410 in which a process gas is introduced to the plasma processing system, wherein the process gas comprises ammonia (NH3) containing gas, and a passivation gas. For example, the passivation gas can comprise a hydrocarbon gas such as at least one of C2H4, CH4, C2H2, C2H6, C3H4, C3H6, C3H8, C4H6, C4H8, C4H10, C5H8, C5H10, C6H6, C6H10, and C6H12. Alternately, the process gas can further comprise helium (He).
In 420, a plasma is formed in the plasma processing system from the process gas using, for example, any one of the systems described in FIGS. 2 through 6, or combinations thereof.
In 430, the substrate comprising the ARC layer is exposed to the plasma formed in 420. After a first period of time, procedure 400 ends. For example, the first period of time during which the substrate with the ARC layer is exposed to the plasma is generally dictated by the time required to etch the ARC layer, or the time required to transfer a photoresist pattern to the ARC layer. In general, the first period of time required to transfer a photoresist pattern through the thickness of the ARC layer is pre-determined. Alternately, the first period of time can be further augmented by a second period of time, or an over-etch time period. As described above, the over-etch time can comprise a fraction of time, such as 1 to 100%, of the first period of time, and this over-etch period can comprise an extension of etching beyond the detection of endpoint.
FIG. 8 presents a method for forming a bilayer mask for etching a thin film on a substrate in a plasma processing system according to another embodiment of the present invention. The method is illustrated in a flowchart 500 beginning in 510 with forming the thin film on the substrate. The thin film can comprise an oxide layer, such as silicon dioxide (SiO2), and it can be formed by a variety of processes including chemical vapor deposition (CVD).
In 520, an anti-reflective coating (ARC) layer is formed on the substrate overlying the thin film. The ARC layer can, for example, be an organic ARC layer that is formed using conventional techniques such as a spin coating system.
In 530, a photoresist pattern is formed on the substrate overlying the ARC layer. The photoresist film can be formed using conventional techniques, such as a photoresist spin coating system. The pattern can be formed within the photoresist film by using conventional techniques such as a stepping micro-lithography system, and a developing solvent.
In 540, the photoresist pattern is transferred to the ARC layer in order to form the bilayer mask. The pattern transfer is accomplished using a dry etching technique, wherein the etch process is performed in a plasma processing system that utilizes a process gas comprising ammonia (NH3) containing gas, and a passivation gas. For example, the passivation gas can comprise a hydrocarbon gas such as at least one of C2H4, CH4, C2H2, C2H6, C3H4, C3H6, C3H8, C4H6, C4H8, C4H10, C5H8, C5H10, C6H6, C6H10, and C6H12. Alternately, the process gas, as described above, can further comprise helium (He). Plasma is formed in the plasma processing system from the process gas using, for example, any one of the systems described in FIGS. 2 through 6, and the substrate comprising the ARC layer is exposed to the plasma formed. A first period of time during which the substrate with the ARC layer is exposed to the plasma is generally dictated by the time required to etch the ARC layer, or the time required to transfer a photoresist pattern to the ARC layer. In general, the first period of time required to transfer a photoresist pattern through the thickness of the ARC layer is pre-determined. However, typically, the first period of time is further augmented by a second period of time, or an over-etch time period. As described above, the over-etch time can comprise a fraction of time, such as 1 to 100%, of the first period of time, and this over-etch period can comprise an extension of etching beyond the detection of endpoint.
FIGS. 9A and 9B present a side view and a top view of an etched multilayer mask, respectively. Feature 600 comprises sidewalls 610 through light-sensitive layer 640 and ARC layer 650 upon which surface roughness 620 is formed during etching. The passivation gas facilitates the formation of a passivation film 630 to smooth the surface roughness 620 of the etched multilayer mask; see FIG. 9B.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS5656128Mar 24, 1994Aug 12, 1997Fujitsu LimitedReduction of reflection by amorphous carbonUS5773199Sep 9, 1996Jun 30, 1998Vanguard International Semiconductor CorporationMethod for controlling linewidth by etching bottom anti-reflective coatingUS6039888Apr 10, 1997Mar 21, 2000Lg Semicon Co., Ltd.Method of etching an organic anti-reflective coatingUS6080529Oct 19, 1998Jun 27, 2000Applied Materials, Inc.Method of etching patterned layers useful as masking during subsequent etching or for damascene structuresUS6080678Jun 27, 1997Jun 27, 2000Lg Semicon Co., Ltd.Method for etching anti-reflective coating filmUS6143476Dec 12, 1997Nov 7, 2000Applied Materials IncMethod for high temperature etching of patterned layers using an organic mask stackUS6352937Apr 27, 1998Mar 5, 2002Sony CorporationMethod for stripping organic based filmUS6458516Apr 18, 2000Oct 1, 2002Applied Materials Inc.Method of etching dielectric layers using a removable hardmaskUS6617257Mar 30, 2001Sep 9, 2003Lam Research CorporationMethod of plasma etching organic antireflective coatingUS6831019 *Aug 29, 2002Dec 14, 2004Micron Technology, Inc.Plasma etching methods and methods of forming memory devices comprising a chalcogenide comprising layer received operably proximate conductive electrodesUS20020111036Feb 12, 2001Aug 15, 2002Lam Research CorporationUnique process chemistry for etching organic low-k materialsUS20020173142 *Feb 15, 2002Nov 21, 2002Serge VanhaelemeerschMethod of fabricating a semiconductor deviceUS20020173160Mar 30, 2001Nov 21, 2002Douglas KeilPlasma etching of organic antireflective coatingUS20030003756May 30, 2002Jan 2, 2003Hynix SemiconductorMethod for forming contact by using arf lithographyUS20030029835Mar 20, 2001Feb 13, 2003Oranna YauwMethod of etching organic antireflection coating (ARC) layersUS20040092098Nov 8, 2002May 13, 2004Chartered Semiconductor Manufacturing Ltd.Use of amorphous carbon as a removable ARC material for dual damascene fabricationUS20040150012 *Feb 4, 2003Aug 5, 2004Texas Instruments IncorporatedChemical treatment of low-k dielectric filmsUS20040185380Dec 17, 2003Sep 23, 2004Tokyo Electron LimitedMethod and apparatus for bilayer photoresist dry developmentUS20040224264 *May 9, 2003Nov 11, 2004Lam Research CorporationMethod providing an improved bi-layer photoresist patternEP0517165A1Jun 2, 1992Dec 9, 1992Sony CorporationDry etching method utilizing (SN)x polymer maskEP0813233A2Jun 10, 1997Dec 17, 1997Applied Materials, Inc.Method of etching dielectric layer using a plasma generated from a mixture of flourohydrocarbon gas, NH3-genrating gas, and carbon-oxygen containing gasJP2000021864A Title not availableJP2001345380A Title not availableJP2002509353A Title not availableJP2002538604A Title not availableJP2003051495A Title not availableJP2003100718A Title not availableJPH1056001A Title not availableJPH05160081A Title not availableJPH11303183A Title not availableWO1999031718A1Dec 4, 1998Jun 24, 1999Applied Materials IncMethod for high temperature etching of patterned layers using an organic mask stackWO2000051173A1Feb 24, 2000Aug 31, 2000Christopher David DobsonMethod of treating an insulating layerWO2003030237A1Sep 6, 2002Apr 10, 2003Akitoshi HaradaEtching method* Cited by examinerNon-Patent CitationsReference1European Office Action issued in Application No. 04704022.5 mailed Oct. 19, 2010.2Japanese Office Action issued in Application No. 2006-508615 mailed Jun. 15, 2010.3Japanese Office Action issued in Application No. 2006-508615 mailed Nov. 19, 2009.4Japanese Office Action issued in Application No. 2006-508615 mailed Nov. 9, 2010.5Korean Office Action issued in Application No. 10-2005-7018198 mailed Sep. 30, 2009.6Machine English translation of 10-56001, published Feb. 24, 1998.7Machine English translation of 11-303183, published Nov. 2, 1999.8Machine English translation of 2000-21864, published Jan. 21, 2000.9Machine English translation of 2002-509353, published Mar. 26, 2002.10Machine English translation of 2003-100718, published Apr. 4, 2003.11Machine English translation of JP 10-56001, published Feb. 24, 1998.12Machine English translation of JP 14-538604, published Nov. 12, 2002.13Machine English translation of JP 2001-345380, published Dec. 14, 2001.14Machine English translation of JP 2003-051495, published Feb. 21, 2003.15Machine English translation of JP 2003-100718, published Apr. 4, 2003.16Machine English translation of JP 5-160081, published Jun. 25, 1993.17Partial English translation of JP 2001-345380, published Dec. 14, 2001.18Rossnagel et al., Handbook of Plasma Processing, 1990, Noyes Publications, pp. 203-205.19Wolf et al., Silicon Processing for the VLSI Era, 1986, Lattice Press, vol. 1, pp. 565, 567.20Wolf, Silicon Processing for the VLSI Era, 2002, Lattice Press, vol. 4, p. 248.Classifications U.S. Classification216/58, 438/703, 438/736, 216/74, 216/72, 438/717International ClassificationB44C1/22Cooperative ClassificationH01L21/31138, H01L21/67069European ClassificationH01L21/311C2B, H01L21/67S2D8DLegal EventsDateCodeEventDescriptionJan 3, 2011ASAssignmentOwner name: TOKYO ELECTRON LIMITED, JAPANFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BALASUBRAMANIAM, VAIDYANATHAN;INAZAWA, KOICHIRO;REEL/FRAME:025574/0272Effective date: 20030902Owner name: INTERNATIONAL BUSINESS MACHINES CORPORATION, NEW YFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:WISE, RICH;PANDA, SIDDHARTHA;MAHOROWALA, ARPAN P.;SIGNING DATES FROM 20031203 TO 20031208;REEL/FRAME:025574/0387Apr 15, 2015FPAYFee paymentYear of fee payment: 4RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services