US2624723A - Lactone derivatives and method of making - Google Patents
Lactone derivatives and method of making Download PDF
US2624723A
US2624723A US73213347A US2624723A US 2624723 A US2624723 A US 2624723A US 73213347 A US73213347 A US 73213347A US 2624723 A US2624723 A US 2624723A
Patented Jan. 6, 1953 LACTONE DERIVATIVES AND METHOD OF MAKING William J. McGraw, Morristown, N. J assignor to Allied Chemical & Dye Corporation, New York, N. Y., a corporation of New York No Drawing. Application March 3, 1947, Serial No. 732,133
This invention relates to new products and methods of making and using them. It relates particularly to the manufacturer of lactone derivatives suitable for a variety of uses.
In the past it has been proposed to prepare a substituted lactone by condensation of butyrolactone with alpha-pyridine carboxylic acid ethyl ester. .The resulting product is a pyridoyl butyrolactone (CH903N) having the acyl group joined to the alpha carbon of the lactone structure. As far as I am aware, this product has never been practically utilized.
It is an object of the present invention to prepare novel alpha-substituted lactones. A further object of the invention is to prepare lactone derivatives suitable for manufacture of polymers and for use in resin compositions as polymers, copolymers or modifiers. A further object is to prepare resins of various properties and particularly resins characterized by notable hardness. A further object of the invention is to provide new lactone derivatives having valuable properties as bacteriostatic agents and intermediates for the manufacture of other compounds. Further objects of the invention will be apparent from the following general description and specific examples.
The products of the invention comprise both monomers and the polymers derived therefrom. The monomeric products of the invention are the gamma and delta lactones devoid of ring substituents other than hydrocarbon substituents except in alpha position and containing, as the sole alpha substituent, the group wherein R represents a hydrogen atom or a lower alkyl radical.
As ring substituents, one or more hydrocarbon radicals may be present in beta, gamma or delta position or in any two or all three of these positions and one such hydrocarbon radical may unite with two of the carbon atoms in the ring to form a fused ring structure. Examples of suitable ring substituents are methyl, ethyl, and phenyl. An example of a fused ring structure is the lactone of orthohydroxy-phenyl acetic acid.
The monomeric compounds of the invention are useful as bacteriostatic agents, solvents, and intermediates for the manufacture of condensation and polymerization products. They are useful in the manufacture of resinous polymers and may be copolymerized with other polymerizable 2 compounds, such as acrylonitrile, acrylic acid esters, styrene, butadiene, and the like, to form a variety of polymeric materials varying from oils to hard amorphous solids. The alpha-methylene-lactone homopolymers and copolymers in particular are useful in the plastic arts for the manufacture of fibers, films, molding compounds,
low-pressure laminating resins and other plastic products.
The manufacture of lactones is a well-known type of chemical operation. In some cases lactones suitable for preparing the products of the invention result when preparation of the corresponding gamma or delta hydroxy acids is attempted. In other cases they are obtainable by conventional lactonization of the corresponding gamma hydroxy and delta hydroxy acids. Examples of acids in these two categories are the hypothetical acids, gamma hydroxy butyric, gamma and delta-hydroxy-valeric, and gammahydroxy-gamma-methylvaleric, which may be isolated in the form of salts; as well as acids, such as ortho-hydroxy-phenyl-acetic acid, which may be isolated in the form of the free acids.
From lactones of the described type having two hydrogen atoms in alpha position, alphaacyl derivatives may be prepared by the Claisen condensation and equivalent methods; for example, by reaction of the lactone with an organic acid ester in the presence of metallic sodium. These alpha acyl derivatives may be isolated before further treatment or may be used directly, without separation from the reaction mixture, to produce the compounds of the invention.
One method of making the monomeric compounds of the invention comprises hydrogenation of alpha-acyl lactones, which produces the alpha-CHROH derivatives, and subsequent dehydration of these derivatives, which forms the pheric pressure using a dehydrating agent which does not promote polymerization.
A particularly interesting and valuable group of compounds within the purview of the invention is obtained when the alpha-acyl derivative is made by means of a formic acid ester. This provides alpha-formyl lactones from which the methylol and methylene derivatives are obtained progressively by the hydrogenation and dehydration. The alpha-methylene derivatives polymerize especially readily in the presence of peroxide or other per compound catalysts or upon exposure to ultraviolet light; polymerization may be effected by conventional emulsion polymerization methods, or any other method commonly used for the polymerization of monomers.
Substituted derivatives may be obtained employing other fatty acid esters to produce homologs (e. g. ethyl acetate yields the alpha-acetyl compound from which the corresponding hydroxy and ethylidene derivatives may be made).
The following examples further illustrate the invention. In the examples, quantities are expressed in parts by weight unless otherwise indicated.
EXAMPLE 1 Alpha-methylene-gamma-oalerolactone CH2-C=CH2 CH3-(IJH PART l.-PREPARATION OF ALPHA-FORMYD GAMMA-VALEROLACTONE About 1.2 parts of absolute ethanol was added to a suspension of 11.5 parts of granulated sodium (sand) in about 360 parts of dry ether. A mixture of 37 parts of ethyl formate and 50.0 parts of valerolactone was then added gradually over a period of 1 /2 hours with agitation. A thick yellow sludge formed in the reaction mixture. Sufficient water was added to dissolve this sludge and the aqueous phase was then separated from the ether layer, acidified with hydrochloric acid and extracted with about 400 parts of ether. The ether layer and the ether extract were combined. The ether was then vaporized and the residue was distilled at reduced pressure. About 36 parts of alpha-formyl-gamma valerolactone boiling at 86 to 88 C. at 1 mm. absolute pressure was obtained. The product gradually solidified on standing at room temperature. The product recrystallized from a benzene petroleum ether mixture had a melting point of 68 to 72 C. and boiled at 86 to 83 C. at 1 mm. absolute pressure. It was soluble in water and an aqueous solution yielded a purplish pink color characteristic of enols when treated with ferric chloride solution. It formed a. 2,4-dinitro phenylhydrazone of melting point l64.5 to 165 C. Duplicate analyses showed: Carbon 55.9%, 56.2 %hydrogen 6.5%, 6.3%.
PART 2.-PREPARATION 0F ALPHA-)IETI-IYLOL- GAHMA-VALEROLACTONE 11.9 parts of alpha-formyl-gamma-valerolactone obtained as described in Part 1 was dissolved in 40 parts of absolute ethanol containing 0.5 part of Raney nickel hydrogenation catalyst and heat ed at 100 C. at 100 atmospheres hydrogen pressure for to minutes. The reaction product was filtered from the catalyst and introduced into a glass still. Alcohol was distilled off and the remaining mixture was further distilled at reduced pressure. 9.6 parts of alpha-methylolgamma-valerolactone boiling at approximately 102 to 104 C. at 1 mm. pressure was obtained as distillate. The product was readily soluble in water. The following constants were observed: Refractive index, n =1.4625; density molecular refraction 31.4. -t formed a 3,5-dinitrobenzoate of 127 to 128 C. melting point. Duplicate analyses showed: Carbon 55.5%, 55.8%hydrogen 7.4%, 7.2%.
PART 3.-PREPARATION OF ALPHA-METHLYENE- GAMMA-VALEROLACTONE parts of alpha-methylol-gamma-valerolactone obtained as described in Part 2 was heated to a temperature of 260 to 280 C. and the resulting vapor was passed over activated alumina maintained at 340 to 350 C. The vaporous product was cooled to room temperature and absorbed in ether. The ether solution was dried over calcium sulfate and ether was vaporized off. The residue was distilled under reduced pressure in the presence of about 1 to 2% of tertiary butyl catechol which was added to prevent polymerization. 15 parts of alpha-methylene-gammavalerolactone, a colorless liquid boiling at 77 to 79 C. at 8 mm. pressure, was obtained, refractive index n =l.4572; Analyses: carbon 64.1%, 64.5%; hydrogen 7.2%, 7.3%. The product was slightly soluble in water.
EXAMPLE 2 Alpha-methyZene-gamma-butyrolactone CH.-C=CH2 PART 1.-PREPARATION OF ALPHA-FORMYL- GAMMAJBUTYRLACTONE The procedure of Example 1, Part 1, was repeated substituting 43 parts of gamma-butyrolactone for the valerolactone employed in Example 1. 21.8 parts of alpha-formyl-gammabutryolactone boiling at 83 to 85 C. at 1 mm. absolute pressure was obtained. This product gradually solidified to form a water-soluble solid giving a purple color with ferric chloride. Analyses: Carbon 52.8%, 52.6%; hydrogen 5.3%, 5.5%.
PART 2.--PREPARATION OF ALPHAMETHYLOL- GAMMA-BUTYROLACTONE The alpha-formyl-gainma-butyrolactone prodnot of Part 1 was hydrogenated in ethanol solution containing nickel catalyst as described in Example 1. The alcohol was evaporated off from the product and the alpha-methylol-gammabutyrolactone boiling at 110 to 112 C. at 1 mm. absolute pressure was obtained by distillation. The product was a colorless viscous liquid readily soluble in water. Its constants were: Refractive index, n =1.4'700; density, d 20/20=1.2353; molecular refraction, 26.2. Analysis: Carbon 51.9%, hydrogen 6.97%. Its 3,5-dinitrobenzoate had a melting point of 123 C.
PART 3.-PREPARATION OF ALPHA-METHYLENE- GAMMA BUTYROLACTONE parts of alpha-methylol-gamma-butyrolactone, prepared as described in Part 1, was heated to 280 to 300 C. and the resulting vapor was passed over activated alumina maintained at 340 to 350 C. The product was absorbed in ether as described in Example 1, Part 3. The ether solution was dried, ether was removed as in Example l, and the residue was distilled at reduced pressure. 25.3 parts of alpha-methylene-gammabutyrolactone, a colorless liquid boiling at to 86 C. at 10 mm. absolute pressure (48 to 49 C. at 0.45 mm), was obtained as distillate. It was slightly soluble in water. Its physical constants were: n =l.4650; d 20/20=1.1l93; molecular refraction 24.2. Analyses: Carbon 60.9%, 61.7%; hydrogen 6.4%, 6.3%.
The following examples illustrate the manufacture of resinous polymers from alpha-methylenegamma-lactone monomers.
EXAMPLE 3 Alpha-methylene-gamma-valerolactone, prepared as described in Example 1, was mixed with 0.15 part of acetyl peroxide dissolved in 0.35 part of dibutyl phthalate. The mixture was placed in a mold and maintained at 60 to 75 C. for 24 hours. The product was a clear, hard, transparent resin.
EXAMPLE 4 The procedure of Example 3 was repeated using alpha methylene gamma butyrolactone prepared as described in Example 2 in place of the gamma-valerolactone. The product was a hard, clear, transparent resin similar in properties to that prepared in Example 3.
EXAMPLE 5 Alpha-methylene-gamma-valerolactone and alpha methylene gamma butyrolactone, prepared in Examples 1 and 2, were placed in molds and maintained at room temperature while subjected to ultraviolet light from a mercury vapor arc for a period of 12 to 24 hours. The products were hard, clear, resinous substances similar in properties to those of Examples 3 and 4.
EXAMPLE 6 The homopolymer of alpha methylenegamma-butyrolactone was prepared by solution polymerization in the following manner:
25 parts of alpha-methylene-gamma butyrolactone, 0.38 part and 0.12 part of synthetic detergent materials known, respectively, as Igepon and Nacconol were added to 112 parts of water and the mixture heated to boiling. 0.2 part of a solution containing 30 parts hydrogen peroxide in 100 parts of water was added to the boiling mixture and boiling was continued for 22 hours. At the end of this time, the polymer had precipitated as a soft, curdy, white solid which was filtered, washed with water and methanol and dried. Yield 11.2 grams.
The product was a thermoplastic resin which melted at 230 to 240 C.
The polymeric material prepared as described was ground to a powdered form and 20 to 25 grams was introduced into the cavity of a mold. The mold containing the polymeric material was then subjected to gradually increasing heat and pressure in a hydraulic press until a thin film of the material began to emerge from the crevices around the edge of the mold cavity. The pressure was then released, the mold cooled and the molded material in the form of a bar 5" long and approximately in cross section was removed. The bars were very hard, transparent, brittle materials having a slight yellow color.
EXAMPLE 7 A copolymer of alpha-methylene-gammabutyrolactone and acrylonitrile was prepared in the following manner:
20 parts of alpha-methylene-gamma butyrolactone, 80 parts of acrylonitrile, 3 parts of potassium persulfate and 1.15 parts sodium bisulfite were added to 1100 parts of Water at room temperature. The mixture was stirred vigorously for five hours without heating, during which time the temperature rose spontaneously to 39 C. and then began to decrease. The product precipitated as a white powder which was filtered, washed with water and methanol and dried. Yield 63 grams.
The polymer was molded as described in Ex- 2. As a new chemical compound, a member ofthe group consisting of the gamma and delta lactones devoid of ring substituents other than hydrocarbon substituents except in alpha position and containing, as the sole alpha substituent, the methylene group :CI-Iz.
3.- As a new compound, alpha-methylenegamma-butyrolactone,
4. As a new compound, alpha-methylenegamma-valerolactone,
CH2-C=CH2 (SE (3:0
5. A plastic composition comprising a polymerization product of a lactone of the group defined in claim 2.
6. A plastic composition comprising a polymerization product of alpha-methylene-gammabutyrolactone.
7. A plastic composition comprising a polymerization product of alpha-methylene-gammavalerolactone.
8. In the manufacture of novel lactone derivatives containing a lower alkylidenyl group in alpha position, the process which comprises hydrogenating a lactone of the group consisting of alpha-lower-acyl gamma and delta lactones devoid of ring substituents other than hydrocarbon substituents, except in alpha position, and containing as the sole alpha substituent the acyl radical wherein R. represents a member of the group consisting of hydrogen and lower alkyl radicals.
9. The method of making a methylene lactone, which comprises hydrogenating a lactone of the group consisting of alpha-formyl gamma and delta lactones devoid of ring substituents other than hydrocarbon substituents, except in alpha position, and containing the aforesaid formyl group as the sole alpha substituent, and subjecting the resulting alpha-methylol lactone to dehydration in vapor phase in contact with a non-condensing dehydration catalyst.
10. The method of making alpha-methylenegamma-butylrolactone, which comprises catalytically hydrogenating alpha-formyl-gammabutyrolactone and subjecting the resulting alpha-methylol-gamma-butyrolactone to dehydration in vapor phase at atmospheric pressure in the presence of a non-condensing dehydrating agen 11. The method of making alpha-methylenegamma-valerolactone, which comprises catalytically hydrogenating alpha-formyl-gammavalerolactone and dehydrating the resulting alpha-methylol-gamma-valerolactone in vapor REFERENCES CITED The following references are of record in. the file of this patent:
8 UNITED STATES PATENTS Number Name Date 2,382,640 Kenyon et al. Aug. 14, 1945 2,428,015 Daniels et al. Sept. 30, 1947 2,443,827 Johnson June 22, 1948 FOREIGN PATENTS Number Country Date 883,764 France Mar. 29, 1943 OTHER REFERENCES Cavallito et al.: Journal of American Chemical Society, vol. 68, 1946, pp. 2332-2334.
Annalen der Chemie (1889-90), (Bd. 255-56), pp. 314-322.
Bredt: Annalen de Chemie, Bd. 256 (1889-90), pp. 314-322.
1. AS A NEW CHEMICAL COMPOUND, A MEMBER OF THE GROUP CONSISTING OF THE GAMMA AND DELTA LACTONES DEVOID OF RING SUBSTITUTENTS OTHER THAN HYDROCARBON SUBSTITUENTS EXCEPT IN ALPHA POSITION AND CONTAINING, AS THE SOLE ALPHA SUBSTITUENT, THE GROUP =CHR, WHEREIN R REPRESENTS A MEMBER OF THE GROUP CONSISTING OF HYDROGEN AND LOWER ALKYL RADICALS.
US2624723A 1947-03-03 1947-03-03 Lactone derivatives and method of making Expired - Lifetime US2624723A (en)
US2624723A US2624723A (en) 1947-03-03 1947-03-03 Lactone derivatives and method of making
US2624723A true US2624723A (en) 1953-01-06
ID=24942338
US2624723A Expired - Lifetime US2624723A (en) 1947-03-03 1947-03-03 Lactone derivatives and method of making
US (1) US2624723A (en)
US2876216A (en) * 1953-09-24 1959-03-03 Du Pont Dialkylidene five-membered heterocyclic compounds and polymers thereof
EP0722960A2 (en) * 1995-01-17 1996-07-24 Degussa Aktiengesellschaft Copolymers for preparing cast glass, or molding materials for preparing heat stable shaped articles
US20030130414A1 (en) * 2000-12-29 2003-07-10 Charles Brandenburg Alpha-methylene lactone homopolymer and copolymer compositions, sheets and articles made therefrom and the process for their manufacture
US20050209316A1 (en) * 2001-06-13 2005-09-22 Magnachem International Laboratories, Inc. Florida Lactone formulations and method of use
US20050239877A1 (en) * 2002-06-12 2005-10-27 Magnachem International Laboratories, Inc. Synthetic lactone formulations and method of use
US20070122625A1 (en) * 2005-11-30 2007-05-31 General Electric Company Tulipalin copolymers
US20080125484A1 (en) * 2002-11-05 2008-05-29 David Terrero Synthetic Lactone Formulations and Methods of Use
US20080262082A1 (en) * 2007-04-20 2008-10-23 Bio Spectrum, Inc. Composition containing s-(-)-tulipalin b or acetylated-s-(-)-tulipalin b
DE102008052711A1 (en) 2008-10-22 2010-04-29 Heinrich-Heine-Universität Düsseldorf Preparing crosslinkable polyester, useful e.g. as a coating material in paints, a conductive material in electrical engineering, and to produce molded products, comprises providing alpha-methylene lactones, and ring-opening polymerization
US20100137618A1 (en) * 2008-10-24 2010-06-03 Magnachem International Laboratories, Inc. Method for screening for compounds selectively interacting with rad9
US9534068B2 (en) 2014-08-27 2017-01-03 International Business Machines Corporation Tulipalin A-based hydroxyl-functionalized polymers, and engineered materials prepared therefrom
FR883764A (en) * 1941-07-04 1943-07-16 Ig Farbenindustrie Ag Process for body conformation rectilinearly formula highly polymerized
US2428015A (en) * 1946-02-25 1947-09-30 Burton T Bush Inc Esters of valerolactone
US2443827A (en) * 1945-02-17 1948-06-22 Us Ind Chemicals Inc Preparation of acetylbutyrolactone
EP0722960A3 (en) * 1995-01-17 1997-06-18 Degussa Copolymers for preparing cast glass, or molding materials for preparing heat stable shaped articles
US5880235A (en) * 1995-01-17 1999-03-09 Agomer Gesellschaft Mit Beschrankter Haftung Copolymers useful for producing cast glass and thermally dimensionally stable molding materials
US20110092588A1 (en) * 2001-06-13 2011-04-21 Magnachem International Laboratories, Inc. Lactone formulations and method of use
US8536348B2 (en) 2001-06-13 2013-09-17 Magnachem International Laboratories, Inc. Lactone formulations and method of use
US8188145B2 (en) 2002-06-12 2012-05-29 Magnachem International Laboratories, Inc. Synthetic lactone formulations and method of use
US7956088B2 (en) 2002-11-05 2011-06-07 Magnachem International Laboratories, Inc. Synthetic lactone formulations and methods of use
US8546444B2 (en) 2004-04-23 2013-10-01 Magnachem International Laboratories, Inc. Synthetic lactone formulations and method of use
US8501431B2 (en) 2008-10-24 2013-08-06 Magnachem International Laboratories, Inc. Method for screening for compounds selectively interacting with RAD9
Cava et al. 1960 Condensed Cyclobutane Aromatic Compounds. IX. Benzocyclobutenol and Benzocyclobutenone
US2532612A (en) 1950-12-05 Preparation of unsaturated thio-ethers
US1944731A (en) 1934-01-23 Organic compound having hydrogenated ring systems and process of preparing it
US3920752A (en) 1975-11-18 Novel gamma, delta unsaturated aldehydes