Matched Legal Cases: ['art.\n9', 'art.\n11', 'art.\n28', 'art.\n30', 'Application No. 01814634', 'Application No. 01998050', 'Application No. 01998050', 'Application No. 2', 'Application No. 2001280771', 'Application No. 2002249810', 'Application No. 2001280771', 'Application No. 01821885', 'Application No. 01998050', 'Application No. 10', 'Application No. 01814634', 'Application No. 01814634']

Patent US7364782 - Flocked transfer and article of manufacture including the application of the ... - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsA flocked transfer is produced by applying a release agent to a release sheet, and then applying the flocking to a release agent. Unlike the traditional method, a binder and thermoplastic hot melt film is applied to the back of the flock. The transfer, which is essentially release sheet, is then applied...http://www.google.com/patents/US7364782?utm_source=gb-gplus-sharePatent US7364782 - Flocked transfer and article of manufacture including the application of the transfer by thermoplastic polymer filmAdvanced Patent SearchPublication numberUS7364782 B2Publication typeGrantApplication numberUS 09/735,721Publication dateApr 29, 2008Filing dateDec 13, 2000Priority dateJul 24, 2000Fee statusPaidAlso published asCN1264612C, CN1486223A, DE60136850D1, EP1351779A1, EP1351779A4, EP1351779B1, US7632371, US20020009571, US20080113144, US20100092719, WO2002058854A1Publication number09735721, 735721, US 7364782 B2, US 7364782B2, US-B2-7364782, US7364782 B2, US7364782B2InventorsLouis Brown AbramsOriginal AssigneeHigh Voltage Graphics, Inc.Export CitationBiBTeX, EndNote, RefManPatent Citations (100), Non-Patent Citations (90), Referenced by (15), Classifications (37), Legal Events (4) External Links: USPTO, USPTO Assignment, EspacenetFlocked transfer and article of manufacture including the application of the transfer by thermoplastic polymer film
US 7364782 B2Abstract
A flocked transfer is produced by applying a release agent to a release sheet, and then applying the flocking to a release agent. Unlike the traditional method, a binder and thermoplastic hot melt film is applied to the back of the flock. The transfer, which is essentially release sheet, is then applied to a substrate, such as item of clothing, a rubber pad, etc., by positioning a sheet of thermoplastic hot melt film on the substrate; placing the transfer on the hot melt with the flock in contact with the hot melt film; and applying heat and pressure. The heat melts the thermoplastic hot melt film to bind the flock to the substrate and binds the flocking together. This method reduces the cost involved in producing flocked articles, especially for articles produced on a continuous basis.
1. A flocked transfer comprising:
a release agent on the release sheet;
flock on the release agent; the flock being formed in a desired pattern on the release sheet, the release agent holding the flock to the release sheet;
a pre-formed, solid, and self-supporting thermoplastic hot melt sheet;
wherein at least substantially all of the flock contacts the thermoplastic hot melt sheet;
and wherein there is no binder adhesive positioned between the thermoplastic hot melt sheet and the flock.
2. The flocked transfer of claim 1, wherein the thermoplastic hot melt sheet is a thermoplastic blank or thermoplastic blank film.
3. The flocked transfer of claim 1, wherein the release agent and release sheet are located on a first surface of the flock and the thermoplastic hot melt sheet is positioned on a second surface of the flock and the first and second surfaces are in an opposing relationship.
4. The flocked transfer of claim 1, wherein the thermoplastic hot melt sheet comprises polyurethane.
5. The flocked transfer of claim 1, wherein the hot melt sheet is cut, before application to the flocked transfer, to correspond to a shape of the flocked transfer.
6. The flocked transfer of claim 1, wherein the thermoplastic hot melt sheet comprises at least first and second parts, the first and second parts having differing properties.
7. The flocked transfer of claim 6, wherein the first and second parts have differing melting temperatures.
8. The flocked transfer of claim 6, wherein the first part contacts the flock and is located between the second part and the flock and wherein the first part has a higher melting temperature than the second part.
9. The flocked transfer of claim 6, wherein the first and second parts have differing viscosities when the first and second parts are melted.
10. The flocked transfer of claim 6, wherein the first part contacts the flock and is located between the second part and the flock and wherein, when the first and second parts are melted, the first part has a higher viscosity than the second part.
11. The flocked transfer of claim 6, wherein the first and second parts are in the form of films and the films are laminated together.
12. The flocked transfer of claim 1, wherein the transfer is adhered to a substrate, and wherein the thermoplastic hot melt sheet is preformed before application to the flock and substrate.
13. The flocked transfer of claim 1, wherein the transfer is adhered to a substrate, and wherein the substrate comprises rubber.
14. The flocked transfer of claim 1, wherein the adhesive component of the hot melt sheet consists essentially of a thermoplastic hot melt material.
15. The flocked transfer of claim 1, wherein the thermoplastic hot melt sheet has a substantially uniform thickness and substantially flat upper and lower surfaces.
16. The flocked transfer of claim 3, wherein substantially all of the thermoplastic hot melt sheet contacts the second surface of the flock.
17. The flocked transfer of claim 1, wherein the thermosplastic hot melt sheet has a substantially uniform thickness and substantially flat upper and lower surfaces.
18. The flocked transfer of claim 1, wherein the thermoplastic hot melt sheet is continuous.
19. A flocked transfer comprising:
flock on the release agent; the flock having first ends and opposing second ends; the flock being formed in a desired pattern on the release sheet; the release agent being located between the flock and release sheet and holding the first ends of the flock to the release sheet, and
a pre-formed, solid, and self-supporting thermoplastic hot melt sheet engaging free ends of the flock, the flock being located between the release agent and the thermoplastic hot melt sheet, wherein at least most of the second ends of the flock are in direct physical contact with the thermoplastic hot melt sheet; and
wherein the thermoplastic hot melt sheet has a substantially uniform thickness and substantially flat upper and lower surfaces and wherein the flock fibers are substantially perpendicular to the upper and lower surfaces and to the release sheet.
20. The flocked transfer of claim 19, wherein the transfer is adhered to a substrate.
21. The flocked transfer of claim 19, wherein the thermoplastic hot melt sheet is a thermoplastic blank or thermoplastic blank film.
22. The flocked transfer of claim 19, wherein the flock comprises a plurality of flock fibers, wherein the release agent and release sheet are located on the first ends of the flock.
23. The flocked transfer of claim 19, wherein the thermoplastic hot melt sheet comprises polyurethane.
24. The flocked transfer of claim 19, wherein the hot melt sheet is cut, before application to the flocked transfer, to correspond to a shape of the flocked transfer.
25. The flocked transfer of claim 19, wherein the thermoplastic hot melt sheet comprises at least first and second parts, the first and second parts having differing properties.
26. The flocked transfer of claim 25, wherein the first and second parts have differing melting temperatures.
27. The flocked transfer of claim 26, wherein the first part contacts the flock and is located between the second part and the flock and wherein the first part has a higher melting temperature than the second part.
28. The flocked transfer of claim 25, wherein the first and second parts have differing viscosities when the first and second parts are melted.
29. The flocked transfer of claim 28, wherein the first part contacts the flock and is located between the second part and the flock and wherein, when the first and second parts are melted, the first part has a higher viscosity than the second part.
30. The flocked transfer of claim 25, wherein the first and second parts are laminated together.
31. The flocked transfer of claim 19, wherein there is no binder adhesive in contact with the thermoplastic hot melt sheet.
32. The flocked transfer of claim 19, wherein the flock comprises a plurality of flock fibers and at least most of the plurality of flock fibers are in direct contact with the hot melt sheet.
33. The flocked transfer of claim 20, wherein the substrate comprises rubber.
34. The flocked transfer of claim 19, wherein the adhesive component of the hot melt sheet consists essentially of a thermoplastic hot melt material.
35. The flocked transfer of claim 19, wherein substantially all of the thermoplastic sheet contacts the second ends of the flock.
36. The flocked transfer of claim 19, wherein the thermoplastic hot melt sheet is continuous.
37. A flocked article comprising:
flock adhered to the release agent; the flock having first ends and opposing second ends;
the flock being formed in a desired pattern on the release sheet, the release agent holding the first ends of the flock to the release sheet;
a pre-formed, solid, and self-supporting thermoplastic hot melt sheet having a length and a width, and a first side engaging the second ends of the flock;
a substrate adhered to a second side of said thermoplastic hot melt sheet;
wherein at least substantially most of the second ends of the flock are adhered to the thermoplastic hot melt sheet;
and wherein there is no binder adhesive positioned between the flock and the substrate.
38. The flocked article of claim 37, wherein the thermoplastic hot melt sheet is continuous.
39. A flocked transfer assembly, comprising:
flock fibers on the release agent; the flock fibers having opposing first and second ends, wherein the flock fibers are formed in a desired pattern on the release sheet, the release agent being located between the flock fibers and the release sheet and holding the first ends of the flock fibers to the release sheet; and
a pre-formed, solid, continuous, and self-supporting thermoplastic adhesive sheet engaging the second ends of the flock fibers, the flock fibers being located between the release agent and the thermoplastic adhesive sheet, wherein the second ends of the flock fibers are in direct physical contact with and adhered to the thermoplastic adhesive sheet.
40. The flocked transfer assembly of claim 39, wherein the thermoplastic adhesive sheet comprises polyurethane.
41. The flocked transfer assembly of claim 39, wherein the thermoplastic adhesive sheet is not in contact with a powdered hot melt adhesive.
42. The flocked transfer assembly of claim 39, wherein there is no binder adhesive located between the thermoplastic adhesive sheet and the second ends of the flock fibers.
43. The flocked transfer assembly of claim 39, wherein the adhesive component of the thermoplastic adhesive sheet consists essentially of a thermoplastic polyester material.
44. The flocked transfer assembly of claim 39, wherein there is no binder adhesive between the second surface of the flock and the thermoplastic adhesive sheet.
45. The flocked transfer assembly of claim 39, wherein substantially none of the thermoplastic adhesive sheet fails to contact the second surface of the flock.
46. The flocked transfer assembly of claim 39, wherein said flocked transfer assembly does not include a substrate.
47. The flocked transfer assembly of claim 39, wherein the thermoplastic adhesive sheet has a substantially uniform thickness and substantially flat upper and lower surfaces and wherein at least most of the flock fibers are substantially perpendicular to planes of the upper and lower surfaces and the release sheet.
48. The flocked transfer assembly of claim 39, wherein the flock fibers are embedded in the thermoplastic adhesive sheet.
49. The flocked transfer assembly of claim 39, wherein at least most of the plurality of flock fibers are in direct physical contact with the thermoplastic adhesive sheet.
50. The flocked transfer assembly of claim 39, wherein there is no acrylic adhesive in direct physical contact with the second ends of the flock.
This application is a continuation-in-part patent application based upon the prior application dated Jul. 24, 2000, having Ser. No. 09/621,830, owned by a common assignee.
STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH DEVELOPMENT
This invention relates to flocked transfers, and, in particular to an improved method incorporating thermoplastic polymer film, in the making of the flocked transfer, which can reduce the cost and time required of producing transfers by a significant amount.
Heretofore, flocked transfers have generally been produced by applying a release agent to a release sheet. The flocking is applied to the release sheet in the desired pattern. A binder and a permanent hot melt adhesive are applied to the back of the flocking, and the transfer is allowed to dry. The binder is required to hold the flocking in the desired pattern. The hot melt adhesive, which is applied to the transfer as a powder, is used to adhere the transfer to a substrate, such as an article of clothing, a rubber pad, etc. The transfer is applied to the substrate by placing the transfer on the substrate with the dried hot melt adhesive in contact with the substrate. Heat, such as from an iron, is then applied to the release sheet. The heat melts the hot melt adhesive, to cause hot melt adhesive to flow into intimate contact with the substrate, forming a mechanical or physical adhesion with the substrate. The release agent then allows the release sheet to be removed from the transfer, leaving the flocking exposed on the substrate.
This traditional method has worked well for years. However, the method can be improved upon to reduce the cost of producing the transfer, and hence, the cost of the item containing the transfer.
In my co-pending application, I have described the usage of a thermoset film in lieu of the bond and powder for adhesion, which film, when subject to heat, adheres to the substrate, functions as an inherence for the flock. This current invention adds further enhancements to this process, by allowing the application and usage of a thermoplastic film, for adherence of the flock transfer.
In accordance with the invention, generally stated, a flocked transfer of the present invention is produced by applying a release agent to a release sheet, and then applying the flocking to the release agent. Unlike the traditional method, a binder and adhesive are not applied to the ends of the flock, but rather, a thermoplastic polymer film is used in lieu thereof.
To form an article of manufacture with the flocked transfer, a hot melt film (in the form of a sheet are cut to shape) is positioned on the substrate to which the transfer is to be applied. The hot melt is preferably a blank or blank film, but can be any thermoplastic type of polymer film. The flock with the release adhesive and release sheet (i.e., the transfer) is then placed on the sheet of hot melt film with the release sheet up, so that the flocking is in contact with the hot melt film. Heat is then applied to the transfer. The heat melts the hot melt film, and secures the flock to the substrate. Because the film is thermoplastic, even if it is subsequently subjected to heat, below a particular temperature, it will not remelt, nor become tacky, and hence, there is no risk of the fibers becoming matted down in any of this type of adhesive, which could otherwise ruin the plush pile effect. It is known that there is a enhanced adhesion with thermoplastic materials, because the thermoplastic materials will cross-attach, and thereby adhere the flock fibers to it, which may become chemically attached thereto. Through the usage of this invention, the finished flock surface is more plush, soft, because more of the fiber is exposed and extends upwardly out of the adhesive, than with the screen-printed latex, as currently used. Also, this affords better soil release during washing or cleaning because of less fiber/adhesive entanglement occurs with the flock, during application.
The use of a thermoplastic type of film for achieving adherence of a transfer to a surface, can be done either before or after the heat transferring operation, or where the heat transfer is produced. The thermoplastic film can be brought into the process at either stage, with respect to the manufacture of the transfer. It is most practical to combine the hot melt film before the heat transfer is fabricated, so it is combined in a convenient and portable manner, which operation was not possible with the previous type of application, for the thermoset film, because once the thermoset film was heated, it sets, and cannot be reheated.
In addition, it is possible to use a two-part thermoplastic type of film, such as commonly available in the industry, having different properties on each side in terms of, for example, melting point, and viscosity of structure. In this way, one can use a higher melting point hot melt film, of thermoplastic material, on the side that attaches to the flock fibers, so that the transfer is initially put together with higher heat in order to set the fibers in place, and then subsequently during application of the transfer to a textile, it may be done at a lower temperature to activate the hot melt on the substrate side while not hot enough to remelt the film holding the flock in place. Also, the hot melt holding the flock can be a very high viscosity, that is, it will not flow much when melted, in order to keep the fibers in place and not mat them together, while the film on the substrate side could be a lower viscosity type of film, that will readily flow so it will penetrate and establish a good mechanical adhesion of the transfer or grid to any substrate upon which the transfer is applied.
Thus, it is an object of this invention to provide for the development of a flock, that may be temporarily adhered onto a release film carrier, fabricated of a thermoplastic film. And, it is a further object that the hot melt film may be used as an intermediate layer, to attach the fibers to the substrate, when developing the transfer initially.
FIG. 1 is a cross-sectional view of a prior art flock transfer;
FIG. 2 is a cross-sectional view of a flock transfer of the present invention;
FIG. 3 is an exploded view of the transfer, a hot melt sheet, and a substrate used to make an article of manufacture;
FIG. 4 is a cross-sectional view of an article of manufacture using the transfer of the present invention, showing a part of the transfer applied to part of the substrate and a part of the transfer and hot melt film spaced from the substrate; and
FIG. 5 is a schematic drawing of a process for continuously producing articles of manufacture, such as mouse pads, coasters, transfers for application to clothing, etc.
Corresponding reference numerals will used throughout the several views of the drawings.
The following detailed description illustrates the invention by way of example, and not by way of limitation. This description will enable one skilled in the art to make and use the invention, including what is presently believed is the best mode of carrying out the invention.
A prior art flock transfer 101 is shown in FIG. 1. As is known, such transfers include a dimensionally stable release sheet 103, to which a conventional flock transfer release adhesive 105 is applied in a pattern which corresponds to the overall image to be flocked. The flock 107 is then electrostatically coated to the release sheet 105. A binder adhesive 109 is applied to the exposed ends of the flock to bind the flock together as a unit. Lastly, a hot melt adhesive 111 is applied. The transfer is then allowed to dry. The transfer is applied to a substrate, as is known, by positioning the transfer on a substrate, such as a shirt, coat, or other item of clothing, with the hot melt adhesive in contact with the substrate, and applying to the transfer. The heat activates the hot melt adhesive to adhere the transfer to the substrate. This process is described in my prior patent, U.S. Pat. No. 4,810,549, as well as in my co-pending application, Ser. No. 09/548,839, filed Apr. 13, 2000, both of which are incorporated herein by reference.
In addition, I have described a similar transfer to that of this current invention, utilizing a thermosetting film, in my application having Ser. No. 09/621,830, filed on Jul. 24, 2000. The contents of that application are incorporated herein by reference.
A flocked transfer 1 of the present invention is shown in FIG. 2. The transfer 1 of the present invention includes a release sheet 3, to which a conventional release agent 5, such as a wax, or other binder, has been applied. The release agent is applied to the sheet in the shape of a pattern of the flocking. Flocking 7 is then applied to the release agent, and hence, to the release sheet, to form the transfer. The flocking 7 is applied, for example, in the manner as described in my previous patent and applications, which are incorporated herein by reference. Unlike the prior art processes, the transfer 1 is made without the use of a binder adhesive or hot melt adhesive. As is discussed below, a thermoplastic film is used to adhere the transfer to a substrate.
An article of manufacture, such as an item of clothing having a transfer 1 applied thereto, a mouse pad, coaster, or any numerous items having a flocked surface, can be manufactured in accordance with this invention and is easily produced using the transfer 1. Referring to FIGS. 2-5, the article of manufacture 11 is produced by positioning a hot melt sheet 13 between a substrate 15 and the flocked release sheet. The hot melt sheet is, for example, a sheet of thermosetting polyester, available from Bostik, Inc. The hot melt sheet can also be made from a thermoplastic polymer, comprising polyesters, and which is available from Bostik. The hot melt sheet can also be made from a thermoplastic polyurethane. Any other thermoplastic film should also work well. The substrate 15 can be an item of clothing, a rubber pad (as for example, for producing a mouse pad or coaster), etc. The hot melt sheet can be precut to correspond to the shape of the transfer. The transfer 1 is then positioned on the hot melt sheet with the flock 7 against the hot melt sheet 13. Heat is applied to the transfer through the release sheet to activate the hot melt sheet. The hot melt sheet then acts to both bind the flock 7 together and to generally permanently adhere the flock 7 to the substrate 15. Preferably, to assemble the article, the flocked release sheet, the thermoplastic film, and the substrate are brought together and passed through a heat-laminating press where the three parts are subject to temperature of about 300� F. to about 350� F. (about 150� C.) and pressure (about 40-50 psi) for about 30 seconds. It has been found that medium-to-firm pressure has been most advantageous in providing for assembly of this type of plush flocked transfer. The pressure and heat will cause the hot melt film to adhere to the flock and the substrate. Additionally, the hot melt film will physically adhere or cure, to give a strong attachment of the flock to the substrate.
The basic premise of this application in utilizing a thermoplastic film which will semi-cure, after heat has been used to apply the transfer to a substrate, is that after heat application, if the temperature of the transfer does not rise to a particular heat level, it should not remelt again. In other words, the object is to use a hot melt film which has a melting point significantly high enough, so that when the transfer is applied through heat, it will adhere to the substrate, but that when the transfer and the substrate to which it is applied is not exposed to excessive heat, it will not remelt, even through the polymer film is thermoplastic, and for all practical purposes, in actual usage, the film will not remelt since it does not see those high temperatures again. In other words, if the melting point of the thermoplastic film is 350� F., and the top temperature that the flocked finished product will encounter, for example sunlight in a hot car, is only 250� F., then there is not a problem associated with the fact that the film is a thermoplastic and therefore can theoretically melt again, but only if it encounters those excessive temperatures.
Another attribute of the use of a thermoplastic film is that in the event one desires to remove the flocked transfer from, for example, an item of clothing, subjecting the transfer to those elevated temperatures, again, will allow the flock to be removed, if that is a need of the owner.
Articles, such as mouse pads or coasters, in which the entire top surface of the article is covered with the flocking can be produced on a continuous basis, as shown in FIGS. 3 and 5. Rolls 21, 23, and 25 of a flocked release sheet 1, the thermoplastic hot melt film 13, and the substrate 15, are provided. The three parts are brought together at a lamination station 33. Rollers can be provided in front of the station 33 so that the three elements are adjacent each other as they enter the lamination station. Rollers can be provided in front of the station 33 so that the three elements are adjacent as they enter the lamination station. In the lamination station, heat and pressure are applied to the three sheets (the flocked release sheet, the hot melt film, and the substrate) to melt the hot melt film. The melted hot melt film will then cure or cross-link, as noted above, to adhere the flock to the substrate. A web 35 exits the laminating station. The web 35 is then allowed to cool. The web 35 is ultimately directed to a cutting station where it is cut into individual articles. Once the web 35 is cooled, it can be directed immediately to a cutting station (after the sheet 35 cools), or can it can be wound up on an uptake roller to be cut into individual articles at a later time, or at a different location. At the cutting station, the release sheet 3 is removed from the flock and gathered on a take-up roll or is otherwise disposed of. After the release sheet has been removed from the flock, the substrate with the flock adhered thereto is cut to form the articles 11. It is also likely that one could remove the release liner either before or after the die cutting procedure. As shown in FIG. 3, a fringe material 50 can be applied to one pair but not the other pair of opposed peripheral edges of the flocked release sheet 1 during this manufacturing process.
Preferably the release sheet is flocked and supplied in roll form as shown in FIG. 5. However, the flocking of the release sheet could be made part of the process.
To produce flocked articles, such as shirts, jackets, sports bags, etc., which cannot be easily flocked on a continuous basis, the hot melt sheet can be applied to the transfer 1 prior to applying the transfer to the substrate. To do this, the thermoplastic hot melt film is placed in contact with the flock of the transfer, and the transfer and release sheet are heated to a temperature at which the thermoplastic hot melt film becomes tacky, but below the temperature at which the thermoplastic hot melt film begins to cure or physically adhere. This will adhere the thermoplastic hot melt film to the transfer 1 to form a transfer which can later be applied to an article by positioning the transfer with the hot melt film in position on the article (i.e., a piece of clothing) and applying heat and pressure to the transfer, for example, with an iron, sufficient to melt the hot melt film, to cause the hot melt film to somewhat cure or physically adhere, to adhere the flock, and secure to the clothing.
The method eliminates two steps from the prior art method: (1). Application of the binder adhesive, and (2) application, cleaning, sintering, and drying of the hot melt adhesive. In a continuous process, the present method also eliminates a station for applying the binder of hot melt adhesives as well as a station for drying the completed transfer. Because the station is not needed to apply (i.e., print) the binder and hot melt adhesives are applied to the flocking as part of the transfer, the machinery required to produce the article 11 is much less expensive (both in actual cost and in maintenance cost). Additionally, because the binder adhesive and hot melt adhesive is not used, the cost of the article of manufacture is reasonably reduced.
It is conceivable in the performance of the manufacture of the transfer of this invention, that the thermoplastic film may be a dual laminated type of film. For example, the upper surface may include a polyester type of film, that may have a melting point at a higher temperature. The lower film, laminated thereto, may be a polyethylene type of film, designed to have a lower temperature melting point. Hence, when the flock is applied to the upper surface of the laminated film, it will embed slightly into that film when heated, and the flock is electrostatically or otherwise applied, and while the bottom surface of the laminated film may likewise soften, once the transfer is cooled, all the films will become structurally sound, once again, in a film structure. Then, when a lower heat is applied to the transfer, for application of the transfer to a textile, rubber, or other surface, as when the transfer is being applied, the bottom polyethylene or EVA film will slightly soften, or melt, to function as an adhesive, for application of the entire transfer to its supporting substrate or surface. This is an example as to how the thermoplastic film(s) of this invention can be used not only for constructing of the transfer, but to function in a dual manner to allow for the application of the transfer to a shirt, bag, or other material, during its final application.
Another one of the advantages of utilization of thermoplastics, in the fabrication of flocked transfers, is that the binder adhesives previously used in the flocking process, typically contain an acrylic, or other materials, which may be flammable. Thermoplastics avoid that predicament. Furthermore, the thermoplastic type binder exhibits wash fastness, and will hold the flock in place even during severe washing conditions. Furthermore, thermoplastic films exhibit better elasticity, than can be obtained from the thermoset or other binder hot melt systems now in use. In addition, the use of the film provides a thinner profile for the finished product, providing a less bulky type of flock transfer, both visually and structural wise, when applied to a garment or other textiles. For example, flock transfers made in accordance with this invention can even be used upon sheer garment textiles. The usage of the thermoplastic film of this invention, avoids the necessity for application of binders, as previously used, and which contain formaldehyde or other undesirable chemicals, as used in previous adhesives to achieve cross linking for flocking purposes in the prior art. There are other miscellaneous film properties that are enhanced through the usage of thermoplastic films, versus the usage of the binder-hot melt powder combination, because there are films that have performance characteristics that cannot be obtained nor are they available for the binder-powder systems. For example, adhesions to leather, or other tough-to-stick-to-surfaces, that exhibit greater tensile strength, such as stretching that will not split, can be better accommodated through the usage of thermoplastic film.
Variations or modifications to the subject matter of this invention may occur to those skilled in the art upon reviewing the invention as described herein. Such variations, if within the scope of this invention, are intended to be encompassed within the claims to issue upon the invention of this application. The description of the preferred embodiment, as shown in the drawings, is set forth for illustrative purposes only.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS1905989Jan 18, 1933Apr 25, 1933Charles SafirGarment monogramUS2592602Sep 20, 1950Apr 15, 1952Saks Walter RProcess of producing flocked articlesUS2636837Apr 9, 1949Apr 28, 1953Summers Edward ClaytonProcess of producing flocked designsUS2916403Aug 16, 1956Dec 8, 1959Gen ElectricBonding compositionsUS2999763Mar 9, 1959Sep 12, 1961Manuf De Feutres De Mouzon AncMethod of applying flock to a fabricUS3215584May 15, 1961Nov 2, 1965Scott Paper CoComposite fabric and method of manufacture thereofUS3314845Jul 23, 1964Apr 18, 1967Du PontMethod of flocking and subsequently developing latently crimpable fibers and article produced therebyUS3377232Sep 8, 1964Apr 9, 1968British Nylon Spinners LtdNonwoven fabrics and the method of manufacture thereofUS3459579Apr 1, 1965Aug 5, 1969Kendall & CoMethod of producing flocked nonwoven fabricUS3496054Jan 13, 1967Feb 17, 1970Kem Wove Ind IncFlocked nonwoven textile material having a relief pattern thereinUS3529986Apr 18, 1966Sep 22, 1970Nat Distillers Chem CorpMethod for applying flock to a resin coated substrateUS3565742Jul 17, 1967Feb 23, 1971Monsanto CoFlocked golf greenUS3622434Jun 3, 1970Nov 23, 1971Kendall & CoCreped fiber-film combination and process thereforUS3639149Oct 28, 1970Feb 1, 1972American Cyanamid CoComposite laminate of water-extended unsaturated polyesterUS3644267Jan 28, 1970Feb 22, 1972Eastman Kodak CoLow-viscosity high-strength thermoplastic adhesiveUS3657060Aug 25, 1970Apr 18, 1972Penn Novelty Co TheEmbroidered emblem with thermoplastic adhesiveUS3660200Jul 9, 1969May 2, 1972Augustus W Bachman JrProcess for bonding preheated thermoplastic film to a dissimilar substrateUS3674611Apr 10, 1970Jul 4, 1972Congoleum Ind IncDecorative surface coveringsUS3772132Apr 3, 1972Nov 13, 1973Malden Mills IncFlocked fabric and method for making sameUS3775205Sep 28, 1971Nov 27, 1973American Cyanamid CoTextile adhesiveUS3793050Aug 12, 1971Feb 19, 1974E MumpowerMethod of applying flocking to a baseUS3803453Jun 19, 1973Apr 9, 1974Du PontSynthetic filament having antistatic propertiesUS3816060Apr 23, 1973Jun 11, 1974InterthermSafety pilot enclosure having flame-diverting air inletUS3816211Jan 20, 1972Jun 11, 1974Penn Novelty CoMethod for making embroidered emblemUS3837946Aug 27, 1971Sep 24, 1974Clark Son And Morland LtdManufacture of pile fabricsUS3900676Aug 14, 1973Aug 19, 1975Du PontAntistatic filamentsUS3903331Apr 13, 1973Sep 2, 1975United Merchants & MfgMethod of making a flocked porous air permeable fabricUS3936554Apr 19, 1974Feb 3, 1976M. Lowenstein & Sons, Inc.Three dimensional decorative material and process for producing sameUS3956552May 5, 1975May 11, 1976Champion Products Inc.Flocked heat transfer method, apparatus and articleUS3961116May 27, 1975Jun 1, 1976United Merchants And Manufacturers, Inc.Novel flocked fabricUS3969559May 27, 1975Jul 13, 1976Monsanto CompanyMan-made textile antistatic strandUS3979538Feb 13, 1975Sep 7, 1976The Gilman Brothers CompanyFlocked web and method of producing sameUS3989869Aug 22, 1974Nov 2, 1976Bayer AktiengesellschaftProcess for making a polyurethane foam sheet and composites including the sheetUS4018956Oct 3, 1975Apr 19, 1977Microfibres, Inc.Method of making a differentially shrunk flocked fabric, and flocked fabric productUS4025678Jul 9, 1976May 24, 1977Pervel Industries, Inc.Flocked expanded-plastic fabric and methodUS4031281Sep 21, 1976Jun 21, 1977Formica CorporationFlocked metallic laminated wallcoveringsUS4034134Oct 7, 1975Jul 5, 1977United Merchants And Manufacturers, Inc.Laminates and coated substratesUS4035532Nov 11, 1975Jul 12, 1977United Merchants And Manufacturers, Inc.Transfer flocking and laminates obtained therefromUS4062992Sep 29, 1975Dec 13, 1977Formica CorporationFlocked high or low pressure decorative laminate componentUS4088708Feb 23, 1976May 9, 1978The B. F. Goodrich CompanyThermoplastic, thermosetting elastomeric compositions and methods for making the sameUS4102562Jun 14, 1976Jul 25, 1978Minnesota Mining And Manufacturing CompanyRetroreflective transfer sheet materialUS4120713Jun 14, 1977Oct 17, 1978A/S Weston TaeppefabrikProcess and apparatus for the continuous production of a fibrous web-like pile productUS4142929Jan 30, 1978Mar 6, 1979Kazuo OtomineProcess for manufacturing transfer sheetsUS4160851Jul 21, 1977Jul 10, 1979Bayer AktiengesellschaftProcess for the production of plastics/metal compositesUS4201810Feb 10, 1978May 6, 1980Shigehiko HigashiguchiTransferable flocked fiber design materialUS4218501Feb 14, 1979Aug 19, 1980Taiyo Steel Co., Ltd.Electrostatic flock-coated metal sheet with excellent corrosion resistance and fabricabilityUS4269885Jan 26, 1979May 26, 1981Mahn John ELaminated material and method of formingUS4273817Jun 29, 1979Jun 16, 1981Mototsugu MatsuoHeat-transferrable appliqueUS4282278Aug 31, 1979Aug 4, 1981Shigehiko HigashiguchiTransferable flocked fiber sticker materialUS4292100Aug 9, 1979Sep 29, 1981Shigehiko HigashiguchiMethod for preparing flock transfer including drying release adhesive prior to applying flockUS4294641Jul 6, 1979Oct 13, 1981Reed Kenneth JHeat transfer sheetsUS4308296Jan 9, 1980Dec 29, 1981Chitouras Costa GMethod of curing particle-coated substratesUS4314813Sep 29, 1980Feb 9, 1982Yasuzi MasakiFlock transfer sheet and flock transfer printing processUS4314955Aug 21, 1980Feb 9, 1982Bayer AktiengesellschaftMethod of filling cavities, in particular, mold cavities, with a reactive flowable mixtureUS4340623Dec 8, 1980Jul 20, 1982Beloit CorporationHigh speed size pressUS4340632Nov 12, 1980Jul 20, 1982International Coatings Co., Inc.Manufacture of flock transfersUS4352924Jun 29, 1981Oct 5, 1982Eastman Kodak CompanyThermosetting powder coating compositionsUS4369157Apr 11, 1977Jan 18, 1983Dri-Print Foils, Inc.Method of automatically decorating articles as they are in-mold formed automaticallyUS4370374Sep 2, 1980Jan 25, 1983Plate Bonn Gesellschaft Mit Beschrankter HaftungMultilayer plastic film, process for its production and its useUS4385588Nov 26, 1980May 31, 1983Societe Industrielle De Decoration Et Application "Sida"Electrifiable-material applicatorUS4387214Jun 29, 1981Jun 7, 1983Eastman Kodak CompanyThermosetting powder coating compositionsUS4388134Apr 28, 1982Jun 14, 1983Diving Unlimited International, Inc.Underwater diver's dry suit and method of sealingUS4390387Jun 16, 1981Jun 28, 1983Mahn John EFlocked material having first thermosetting adhesive layer and second thermoplastic adhesive layerUS4396662Feb 16, 1982Aug 2, 1983Shigehiko HigashiguchiTransferable flocked fiber design material and method of making sameUS4405401Jul 15, 1981Sep 20, 1983Stahl Ted AThermoplastic labeling and method of making sameUS4418106Apr 12, 1983Nov 29, 1983Alkor Gmbh KunstoffverkaufMethod of producing a flocked composite bodyUS4423106Apr 23, 1982Dec 27, 1983Mahn John ELaminated material and method of formingUS4430372Jun 11, 1982Feb 7, 1984Firma Carl FreudenbergNon-woven fabric with improved hot-press properties and method for manufacturing sameUS4438533May 27, 1981Mar 27, 1984Kufner Textilwerke KgInterlining for garments and method for the manufacture thereofUS4446274Feb 16, 1983May 1, 1984Denki Kagaku Kogyo Kabushiki KaishaVinyl acetate-ethylene copolymer emulsion and aqueous emulsion adhesive composition containing the emulsionUS4465723Jun 11, 1982Aug 14, 1984Firma Carl FreudenbergFixation insert with improved flash-through safety and method for manufacturing the sameUS4510274Jan 12, 1983Apr 9, 1985Denki Kagaku Kogyo Kabushiki KaishaVinyl acetate-ethylene copolymer emulsion and aqueous emulsion adhesive composition containing the emulsionUS4539166May 5, 1983Sep 3, 1985Bayer AktiengesellschaftProcess for the production of a lightfast and colorfast composite plastic partUS4574018Dec 30, 1983Mar 4, 1986Toray Industries, Inc.Pile fabric production processUS4582658Jul 23, 1984Apr 15, 1986Bayer AktiengesellschaftProcess for the production of a cellular composite plastic partUS4610904Dec 11, 1984Sep 9, 1986John E. Mahn, Sr.Heat activated removable ornamental transferUS4650533Nov 23, 1984Mar 17, 1987Transfer Print Foils, Inc.Preparation of hot transfer product for continuous in-mold decorationUS4652478Jan 29, 1986Mar 24, 1987Franz Joseph RathFlock transfer sheet patchUS4668323Feb 15, 1985May 26, 1987Uniroyal Englebert Textilcord S.A.Method of making flexible, fiber-covered, sheet-like textile articleUS4670089Feb 27, 1986Jun 2, 1987Dixon Industries CorporationMethod of bonding polytetrafluoro-ethylene composition to metal substratesUS4681791Jan 30, 1986Jul 21, 1987Pilot Ink Co., Ltd.Thermochromic textile materialUS4687527Aug 28, 1985Aug 18, 1987Kabushiki Kaisha Tokyo HoraishaMethod of forming flock patternsUS4741791Jul 18, 1986May 3, 1988Bemis Associates Inc.Flocked transfer material and method of making heat-transferable indicia therefromUS4790306Sep 25, 1987Dec 13, 1988Minnesota Mining And Manufacturing CompanyRespiratory mask having a rigid or semi-rigid, insert-molded filtration element and method of makingUS4793884Oct 22, 1987Dec 27, 1988Wakaba Co., Ltd.Decorative plate producing methodUS4797320Jan 4, 1988Jan 10, 1989Bayer AktiengesellschaftComposite plastic moldings and a process for their productionUS4810321May 26, 1987Mar 7, 1989Bayer AkteingesellschaftProcess for the preparation of a metal-plastic laminateUS4810549Aug 24, 1987Mar 7, 1989High Voltage Graphics, Inc.Plush textured multicolored flock transferUS4812247Aug 11, 1986Mar 14, 1989Bayer AktiengesellschaftPlastics moulding containing reinforced fillingsUS4834502Aug 8, 1988May 30, 1989Xerox CorporationOptical mouse padUS4980216Oct 16, 1987Dec 25, 1990Roempp WalterTransfer for textilesUS5008130Jun 22, 1989Apr 16, 1991Uniroyal Textilcord, S.A.Method of producing a patterned flocked web of materialUS6010764 *Mar 28, 1998Jan 4, 2000High Voltage Graphics, Inc.Transfer fabricated from non-compatible componentsUSD66035Sep 2, 1924Nov 18, 1924 Design for a rxtgUSD108581Nov 19, 1936Feb 22, 1938 Design for a rugUSD114814Nov 4, 1938May 16, 1939 Design for a bug or similar articleUSD122192Aug 3, 1940Aug 27, 1940 Design for a bug ob similar abticleUSD125860Dec 30, 1940Mar 11, 1941 Haas rug or similar articleUSD162533May 29, 1950Mar 20, 1951 Morris b. goldfaebUSD195245Sep 21, 1961May 14, 1963 Pmjz iks* Cited by examinerNon-Patent CitationsReference1"A Rug Fit for a Mouse," Time Magazine (Sep. 28, 1998) p. 96.2"Bicomponent Fibers", available at http://web.utk.edu/~mse/pages/Textiles/Bicomponent%20fibers.htm, Updated Apr. 2004, 8 pages.3"Magic Carpet," Wired (Nov. 1998), p. 68.4"New pads for computer mice now cutting a different rug," USA Today (Oct. 26, 1998), p. D1.5"RMIUG Meeting Minutes-Colorado in the Information Age", Jan. 14, 1997; 1 page.6"Rugs for Rodents," Newsweek (Nov. 9, 1998), p. 8.7"When is a mouse pad really a rug?" The Denver Business Journal.(Nov. 1998), at http://denver.bizjournals.com/denver/stories/1998/11/30/story3.html.8Agion Technologies, LLC., The Most Advanced Antimicrobial Silver Delivery System.9Apr. 5, 2006 Office Action In Re Application Of Louis Brown Abrams; U.S. Appl. No. 10/455,541; filed Jun. 4, 2003.10Artisyn Synthetic Paper 165, Printability Product Specification Sheet, Mar. 1999, 2 pages.11Artisyn Synthetic Paper 165, Printability Product Specification Sheet, May 1997, 1 page.12Bayer Plastics Divison Press Release, Wheel Covers, Center Caps Become Revolving Art Forms with New Film Insert Molding Technology, Jun. 19, 2000.13Bostik USA; "Industrial Adhesives" (2001), 3 pages.14Bostik USA; Web & Powder Adhesives; 2000; 2 pgs.15Brown Abrams, "Flocking A Touch of Velour" ScreenPrinting (Apr. 1987).16Brown Abrams, "Part II: Flocking" ScreenPrinting (Jun. 1987).17Cellusuede Products, Inc, "About Flock", Available at http://www.cellusuede.com/navabout.html, KMK Media Group, copyright 2000, 1 pages.18Cellusuede Products, Inc, "FAQ's", Available at http://www.cellusuede.com/faq.html, KMK Media Group, copyright 2000, 2 pages.19Cellusuede Products, Inc, "Glossary of Terms", Available at http://www.cellusuede.com/glossary/index.html, KMK Media Group, copyright 2000, 2 pages.20Cellusuede Products, Inc, "Uses for Flock, Home Furnishings", Available at http://www.cellusuede.com/home.html, KMK Media Group, copyright 2000, 2 pages.21Cellusuede Products, Inc. "Fiber Types", Available at http://www.cellusuede.com/about/types.html, KMK Media Group, copyright 2000, 4 pages.22Changpad Trading Inc.; Heat-Trans Pad; Jan. 27, 1999, available at http://www.changpad.com.tw/heat-trans.htm, 1 page.23Computer Current (Nov. 9, 1998).24Dec. 30, 2005 Supplemental First Office Action, Chinese Application No. 01814634.1 (English translation provided only).25Declaration of L. Brown Abrams Under 37 CFR � 1.98 for 09/735,721 dated Jan. 16, 2004, 2 pages.26Declaration of L. Brown Abrams under 37 CFR � 1.98 for U.S. Appl. No. 09/621,830 dated Jan. 7, 2003, 2 pages.27Declaration of L. Brown Abrams Under 37 CFR � 1.98 for U.S. Appl. No. 09/735,721 dated Jan. 16, 2004, 2 pages.28Declaration of L. Brown Abrams under 37 CFR �1, 132.29Defosse, Systems Approach Gives Blow Molders Big Edge, Dec. 2000.30European Search Report, issued Jan. 12, 2006, in European Patent Application No. 01998050.7.31European Search Report, issued Jul. 17, 2006, in European Patent Application No. 01998050.7.32Examiner's Report for Canadian Patent Application No. 2,415,680, mailed Apr. 17, 2007.33Examiner's Report No. 2 on Australian Patent Application No. 2001280771, mailed Jun. 2, 2006.34Examiners's First Report on Australian Patent Application No. 2002249810, mailed Oct. 20, 2005.35Examinier's First Report on Australian Patent Application No. 2001280771, mailed Jun. 3, 2005.36Fake Fur Computer Accessories; Products; Jan. 27, 1999, available at http://workwares.com.au/products.htm, 3 pages.37First Office Action (with translation) dated Apr. 1, 2005 for Chinese Patent Application No. 01821885.7, 8 pages.38International Preliminary Examination Report for International Application No. PCT/US01/23195, mailed Jun. 20, 2002.39International Search Report for International Application No. PCT/US01/23195, mailed Oct. 30, 2001.40International Search Report for International Application No. PCT/US01/48615, mailed Jun. 17, 2002.41Invitation pursuant to Article 96(2) and Rule 51(2) EPC, dated Jun. 26, 2007, in European Patent Application No. 01998050.7.42Jan. 10, 2007 Office Action in Re Application of Louis Brown Abrams; U.S. Appl. No. 10/455,575; filed Jun. 4, 2003.43Jan. 11, 2007 Office Action in Re Application of Louis Brown Abrams; U.S. Appl. No. 10/455,541; filed Jun. 4, 2003.44JC Penney Catalog, Fall & Winter, accent rugs, A-B, p. 1032, copy in 2000 design library (1991).45Jun. 16, 2006 Office Action In Re Application Of Louis Brown Abrams; U.S. Appl. No. 10/670,091; filed Sep. 23, 2003.46Lextra(R) MouseRug(R); "About the Product" (Jan. 27, 1999), http://www.mouserug.com/mouserug/aboutmouserugs.html, 2 pages.47Lextra(R) MouseRug(R); "Dimensions" (Jan. 27, 1999), http://www.mouserug.com/mouserug/dimensions.html, 1 page.48Lextra(R) MouseRug(R); "MouseRug Components" (Jan. 27, 1999), http://www.mouserug.com/mouserug/mousecomp.html, 1 page.49Mar. 23, 2006 Office Action In Re Application Of Louis Brown Abrams; U.S. Application No. 10/455,575; filed Jun. 4, 2003.50Oct. 27, 2005 Office Action In Re Application Of Louis Brown Abrams; U.S. Appl. No. 10/455,541; filed Jun. 4, 2003.51Oct. 28, 2005 Office Action In Re Application Of Louis Brown Abrams; U.S. Appl. No. 10/455,575; filed Jun. 4, 2003.52Oct. 7, 2005 Office Action In Re Application Of Louis Brown Abrams; U.S. Appl. No. 09/621,830; filed Jul. 24, 2000.53Oct. 8, 2002 Office Action In Re Application Of Louis Brown Abrams; U.S. Appl. No. 09/621,830; filed Jul. 24, 2000.54Office Action for U.S. Appl. No. 09/735,721, mailed Nov. 15, 2006.55Office Action Summary dated Apr. 22, 2005 for U.S. Appl. No. 10/455,541.56Office Action Summary dated Apr. 28, 2005 for U.S. Appl. No. 10/455,575, 14 pages.57Office Action Summary dated Oct. 11, 2005 for U.S. Appl. No. 10/670,091, filed Sep. 23, 2003.58Office Action, Chinese Application No. 01814634.1 from Dec. 30, 2005 (English translation provided).59Official Action for U.S. Appl. No. 09/621,830, mailed Jun. 29, 2006.60Official Action for U.S. Appl. No. 09/621,830, mailed May 16, 2007 (4811-9).61Official Action for U.S. Appl. No. 09/621,830, mailed Nov. 15, 2006.62Official Action for U.S. Appl. No. 10/455,541, mailed Jun. 25, 2007 (4811-9-DIV).63Official Action for U.S. Appl. No. 10/455,575, mailed Jun. 20, 2007 (4811-9-CIP-DIV).64Official Action for U.S. Appl. No. 10/670,091, mailed Feb. 20, 2007.65Official Action for U.S. Appl. No. 10/670,091, mailed Nov. 2, 2006.66Official Action for U.S. Appl. No. 10/670,091, mailed Oct. 15, 2007.67Rejection Decision for Chinese Application No. 01814634.1 issued Apr. 6, 2007.68Sears Catalog, Spring/Summer, bath carpets, (B), fringed oblong, pp. 1290-1291, oriental design rugs, A-B, p. 1146, copy in 2000 design library (1978).69Shaner, Advanced Molding Processes: Low Pressure Molding/Low-High Pressure Molding for Interior Trim, Ken 1997.70Sonics & Materials, Inc., "Chart II Compatability of Thermoplastics" (undated), 1 page.71Stahls', New Product Bulletin.72Synder Fabric Molding Shows Promise in Automotive, Oct. 1999.73Takatori, Hiroyuki, "Dieprest In-mold Laminate Technology," Automotive & Transportation Interiors Expo Conference 1999, Session 12, pp. 1-4.74U.S. Appl. No. 09/548,839, filed Apr. 13, 2000, Abrams.75U.S. Appl. No. 09/621,830, filed Jul. 24, 2000, Abrams.76U.S. Appl. No. 09/629,746, filed Jul. 31, 2000, Abrams.77U.S. Appl. No. 10/265,206, filed Oct. 4, 2002, Abrams.78U.S. Appl. No. 10/394,357, filed Mar. 21, 2003, Abrams.79U.S. Appl. No. 10/455,541, filed Jun. 4, 2003, Abrams.80U.S. Appl. No. 10/455,575, filed Jun. 4, 2003, Abrams.81U.S. Appl. No. 10/613,981, filed Jul. 3, 2003, Abrams.82U.S. Appl. No. 10/613,982, filed Jul. 3, 2003, Abrams.83U.S. Appl. No. 10/614,340, filed Jul. 3, 2003, Abrams.84U.S. Appl. No. 10/614,399, filed Jul. 3, 2003, Abrams.85U.S. Appl. No. 10/670,091, filed Sep. 23, 2003, Abrams.86U.S. Appl. No. 11/460,493, Abrams.87U.S. Appl. No. 11/533,699, Abrams.88U.S. Appl. No. 11/560,679, Abrams.89U.S. Appl. No. 11/565,974, Abrams.90U.S. Appl. No. 29/058,551, filed Aug. 19, 1996, Abrams.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS8168262Jun 14, 2010May 1, 2012High Voltage Graphics, Inc.Flocked elastomeric articlesUS8354050Jan 15, 2013High Voltage Graphics, Inc.Co-molded direct flock and flock transfer and methods of making sameUS9012005Feb 16, 2010Apr 21, 2015High Voltage Graphics, Inc.Flocked stretchable design or transfer including thermoplastic film and method for making the sameUS9175436Mar 11, 2011Nov 3, 2015High Voltage Graphics, Inc.Flocked articles having a resistance to splitting and methods for making the sameUS9180728Jun 20, 2011Nov 10, 2015High Voltage Graphics, Inc.Dimensional, patterned heat applied applique or transfer made from knit textileUS9180729Jun 20, 2011Nov 10, 2015High Voltage Graphics, Inc.Heat applied appliqu� or transfer with enhanced elastomeric functionalityUS9193214Oct 14, 2013Nov 24, 2015High Voltage Graphics, Inc.Flexible heat sealable decorative articles and method for making the sameUS20080150186 *Jan 14, 2008Jun 26, 2008High Voltage Graphics, Inc.Co-molded direct flock and flock transfer and methods of making sameUS20100068447 *Mar 18, 2010High Voltage Graphics, Inc.Flocked slurried thermosetting adhesive articleUS20100159185 *Dec 22, 2009Jun 24, 2010Illinois Tool Works Inc.Applying a design on a textileUS20100233410 *Sep 16, 2010High Voltage Graphics, Inc.Wet-on-wet method for forming flocked adhesive articleUS20100276060 *Jun 14, 2010Nov 4, 2010High Voltage Graphics, Inc.Flocked elastomeric articlesUS20110052859 *Mar 3, 2011High Voltage Graphics, Inc.Processes for precutting laminated flocked articlesUS20110223373 *Sep 15, 2011High Voltage Graphics, Inc.Flocked articles having a resistance to splitting and methods for making the sameUSRE45802Sep 21, 2012Nov 17, 2015High Voltage Graphics, Inc.Flocked articles having noncompatible insert and porous film* Cited by examinerClassifications U.S. Classification428/90, 428/86, 428/97, 428/914International ClassificationD04H11/00, B44C1/17, B29L7/00, B32B33/00, B29L9/00, B32B37/04, B05D1/14, B29C65/40, B32B7/06, D06Q1/14Cooperative ClassificationY10T428/23943, Y10T428/23929, Y10T428/23993, Y10T428/23914, Y10T156/1052, Y10S428/914, D04H11/00, B32B37/04, B44C1/1716, D06Q1/14, B44C1/172, B32B37/025, B44C1/1712, B32B2037/1223, B44C1/1725European ClassificationB32B37/04, B44C1/17F2, B44C1/17F, D06Q1/14, B44C1/17F4, B44C1/17F6, D04H11/00, B32B37/02BLegal EventsDateCodeEventDescriptionApr 1, 2002ASAssignmentOwner name: HIGH VOLTAGE GRAPHICS, INC., COLORADOFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:ABRAMS, L. BROWN;REEL/FRAME:012776/0796Effective date: 20020321Nov 3, 2011SULPSurcharge for late paymentNov 3, 2011FPAYFee paymentYear of fee payment: 4Oct 29, 2015FPAYFee paymentYear of fee payment: 8RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services