Matched Legal Cases: ['art 1', 'art 2', 'art 3', 'art 4', 'art 4', 'art 1', 'art 2', 'art 3', 'art 4', 'art 4', 'art 1', 'art 2', 'art 3', 'art 4', 'art 1', 'art 1', 'art 2', 'art 3', 'art 4', 'art 4', 'art 1', 'art 2', 'art 3', 'art 4', 'art 3', 'art 4', 'art 1', 'art 1', 'art 2', 'art 3', 'art 4', 'art 3', 'art 4', 'art. 76']

EP0662484A2 - Olefin polymerization catalysts - Google Patents
EP0662484A2
EP0662484A2 EP19940203507 EP94203507A EP0662484A2 EP 0662484 A2 EP0662484 A2 EP 0662484A2 EP 19940203507 EP19940203507 EP 19940203507 EP 94203507 A EP94203507 A EP 94203507A EP 0662484 A2 EP0662484 A2 EP 0662484A2
EP19940203507
EP0662484A3 (en )
The invention relates to a process for olefin polymerization comprising polymerising ethylene and a monomer selected from C3-CZ0 α-olefin and/or a C5-C20 diolefin in the presence of a catalyst system comprising (A) a compound of the general formula: or wherein M is Zr, Hf or Ti ;
(C5H5-y-xRx) is a cyclopentadienyl ring which is substituted with from zero to five groups R, "x" is 1, 2, 3, 4 or 5 denoting the degree of substitution, and each R is, independently, a radical selected from a group consisting of C1-C20 hydrocarbyl radicals, C1-C20 substituted hydrocarbyl radicals wherein one or more hydrogen atoms are replaced by a halogen atom, C1-C20 hydrocarbyl-substituted metalloid radicals wherein the metalloid is selected from the Group IV A of the Periodic Table of Elements and halogen radicals or (C5H5-y-xRx) is a cyclopentadienyl ring in which two adjacent R-groups are joined from C4-C20 ring to give a saturated or unsaturated polycyclic cyclopentadienyl ligand ;
(JR'z-1-y) is a heteroatom ligand in which J is an element with a coordination number of three from Group V A or an element with a coordination number of two from Group VI A of the Periodic Table of Elements, each R' is, independently, a radical selected from a group consisting of C1-C20 hydrocarbyl radicals, substituted C1-C20 hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by a halogen atom, and "z" is the coordination number of the element J ; each Q or Q' is, independently any univalent anionic ligand or Q and Q' are a divalent anionic chelating agent; M' has the same meaning as M ;
"y" is 0 or 1 when w is greater than 0 ; y is 1 when w is 0, when "y" is 1, B is covalent bridging group containing a Group IV A or V A element ; and
L is a Lewis base where "w" denotes a number from 0 to 3 and (B) an alumoxane and (C) a reaction product or such a compound (A) aluminum alkyl and water to obtain a polymer having an Mw of 1000 to 5 million and an Mw/Mn of from 1.5 to 15.0.
This invention relates to certain transition metal compounds from Group IV B of the Periodic Table of Elements, to a catalyst system comprising a Group IV B transition metal compound and an alumoxane, and to a process using such catalyst system for the production of polyolefins, particularly polyethylene, polypropylene and a-olefin copolymers of ethylene and propylene having a high molecular weight. The catalyst system is highly active at low ratios of aluminum to the Group IV B transition metal, hence catalyzes the production of a polyolefin product containing low levels of catalyst residue.
As is well known, various processes and catalysts exist for the homopolymerization or copolymerization of olefins. For many applications it is of primary importance for a polyolefin to have a high weight average molecular weight while having a relatively narrow molecular weight distribution. A high weight average molecular weight, when accompanied by a narrow molecular weight distribution, provides a polyolefin or an ethylene-a-olefin copolymer with high strength properties.
Traditional Ziegler-Natta catalyst systems -- a transition metal compound cocatalyzed by an aluminum alkyl -- are capable of producing polyolefins having a high molecular weight but a broad molecular weight distribution.
More recently a catalyst system has been developed wherein the transition metal compound has two or more cyclopentadienyl ring ligands, such transition metal compound being referred to as a metallocene -- which catalyzes the production of olefin monomers to polyolefins. Accordingly, metallocene compounds of the Group IV B metals, particularly, titanocene and zirconocene, have been utilized as the transition metal component in such "metallocene" containing catalyst system for the production of polyolefins and ethylene-a-olefin copolymers. When such metallocenes are cocatalyzed with an aluminum alkyl -- as is the case with a traditional type Ziegler-Natta catalyst system -- the catalytic activity of such metallocene catalyst system is generally too low to be of any commercial interest.
It has since become known that such metallocenes may be cocatalyzed with an alumoxane - rather than an aluminum alkyl -- to provide a metallocene catalyst system of high activity which catalyzes the production of polyolefins.
A wide variety of Group IV B transition metal compounds of the metallocene type have been named as possible candidates for an alumoxane cocatalyzed catalyst system. Hence, although bis(cyclopentadienyl) Group IV B transition metal compounds have been the most preferred and heavily investigated type metallocenes for use in metallocene/alumoxane catalyst for polyolefin production, suggestions have appeared that mono and tris(cyclopentadienyl) transition metal compounds may also be useful. See, for example, U.S. Patent Nos. 4,522,982; 4,530,914 and 4,701,431. Such mono(cyclopentadienyl) transition metal compounds as have heretofore been suggested as candidates for a metallocene/alumoxane catalyst are mono(cyclopentadienyl) transition metal trihalides and trialkyls.
The "Group IV B transition metal component" of the catalyst system is represented by the general formula: wherein: M is Zr, Hf or Ti and is in its highest formal oxidation state (+4, d0 complex);
(C5,H5-y-xRx) is a cyclopentadienyl ring which is substituted with from zero to five substituent groups R, "x" is 0,1, 2, 3, 4 or 5 denoting the degree of substitution, and each substituent group R is, independently, a radical selected from a group consisting of C1-C20 hydrocarbyl radicals, substituted C1-C20 hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by a halogen atom, C1-C20 hydrocarbyl-substituted metalloid radicals wherein the metalloid is selected from the Group IV A of the Periodic Table of Elements, and halogen radicals or (C5H5-y-xRx) is a cyclopentadienyl ring in which two adjacent R-groups are joined forming C4-C20 ring to give a saturated or unsaturated polycyclic cyclopentadienyl ligand such as indenyl, tetrahydroindenyl, fluorenyl or octahydrofluorenyl;
(JR'z-1-y) is a heteroatom ligand in which J is an element with a coordination number of three from Group V A or an element with a coordination number of two from Group VI A of the Periodic Table of Elements, preferably nitrogen, phosphorus, oxygen or sulfur, and each R' is, independently a radical selected from a group consisting of C1-C20 hydrocarbyl radicals, substituted C1-C20 hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by a halogen atom, and "z" is the coordination number of the element J;
"y" is 0 or 1 when w is greater than 0; y is 1 when w is 0; when "y" is 1, B is a covalent bridging group containing a Group IV A or V A element such as, but not limited to, a dialkyl, alkylaryl or diaryl silicon or germanium radical, alkyl or aryl phosphine or amine radical, or a hydrocarbyl radical such as methylene, ethylene and the like;
L is a Lewis base such as diethylether, tetraethylammonium chloride, tetrahydrofuran, dimethylaniline, aniline, trimethylphosphine, n-butylamine, and the like; and "w" is a numberfrom 0 to 3; L can also be a second transition metal compound of the same type such that the two metal centers M and M' are bridged by Q and Q', wherein M' has the same meaning as M and Q' has the same meaning as Q. Such compounds are represented by the formula:
The alumoxane component of the catalyst may be represented by the formulas: (R2-Al-O)m; R3(R4-Al-O)m-AIR5 or mixtures thereof, wherein R2-R5 are, independently, a univalent anionic ligand such as a Cl-C5 alkyl group or halide and "m" is an integer ranging from 1 to about 50 and preferably is from about 13 to about 25.
A typical polymerization process of the invention such as for the polymerization or copolymerization of olefins comprises the steps of contacting ethylene or C3-C20 a-olefins alone or with other unsaturated monomers including C3-C20 a-olefins, C5-C20 diolefins,
and/or acetylenically unsaturated monomers either alone or in combination with other olefins and/or other unsaturated monomers, with a catalyst comprising, in a suitable polymerization diluent, the Group IV B transition metal component illustrated above; and a methylalumoxane in an amount to provide a molar aluminum to transition metal ratio of from about 1:1 to about 20,000:1 or more; and reacting such monomer in the presence of such catalyst system at a temperature of from about -100°C to about 300°C for a time of from about 1 second to about 10 hours to produce a polyolefin having a weight average molecular weight of from about 1,000 or less to about 5,000,000 or more and a molecular weight distribution of from about 1.5 to about 15.0.
Lower molecular weight species may be produced by using catalyst species of reduced activity; higher temperatures and/or the use of transfer agents such as hydrogen.
wherein: M is Zr, Hf or Ti and is in its highest formal oxidation state (+4, dO complex);
(C5H5-y-xRx) is a cyclopentadienyl ring which is substituted with from zero to five substituent groups R, "x" is 0, 1, 2, 3, 4 or 5 denoting the degree of substitution, and each substituent group R is, independently, a radical selected from a group consisting of C1-C20 hydrocarbyl radicals, substituted C1-C20 hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by a halogen atom, C1-C20 hydrocarbyl-substituted metalloid radicals wherein the metalloid is selected from the Group IV A of the Periodic Table of Elements, and halogen radicals or (C5H5-y-xRx) is a cyclopentadienyl ring in which two adjacent R-groups are joined forming C4-CZo ring to give a saturated or unsaturated polycyclic cyclopentadienyl ligand such as indenyl, tetrahydroindenyl, fluorenyl or octahydrofluorenyl;
(JR'z-1-y) is a heteroatom ligand in which J is an element with a coordination number of three from Group V A or an element with a coordination number of two from Group VI A of the Periodic Table of Elements, preferably nitrogen, phosphorus, oxygen or sulfur with nitrogen being preferred, and each R' is, independently a radical selected from a group consisting of C1-C20 hydrocarbyl radicals, substituted C1-C20 hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by a halogen atom, and "z" is the coordination number of the element J;
each Q is, independently any univalent anionic ligand such as halogen, hydride, or substituted or unsubstituted C1-C20 hydrocarbyl, alkoxide, aryloxide, amide, arylamide, phosphide or arylphosphide, provided that where any Q is a hydrocarbyl such Q is different from (C5H5-y-xRx), or both Q together may be be an alkylidene or a cyclometallated hydrocarbyl or any other divalent anionic chelating ligand;
"y" is 0 or 1 when w is greater than 0, and y is 1 when w=0; when "y" is 1, B is a covalent bridging group containing a Group IV A or V A element such as, but not limited to, a dialkyl, alkylaryl or diaryl silicon or germanium radical, alkyl or aryl phosphine or amine radical, or a hydrocarbyl radical such as methylene, ethylene and the like. L is defined as heretofore. Examples of the B group which are suitable as a constituent group of the Group IV B transition metal component of the catalyst system are identified in Column 1 of Table 1 under the heading "B".
Exemplary hydrocarbyl radicals for the Q are methyl, ethyl, propyl, butyl, amyl, isoamyl, hexyl, isobutyl, heptyl, octyl, nonyl, decyl, cetyl, 2-ethylhexyl, phenyl and the like, with methyl being preferred. Exemplary halogen atoms for Q include chlorine, bromine, fluorine and iodine, with chlorine being preferred. Exemplary alkoxides and aryloxides for Q are methoxide, phenoxide and substituted phenoxides such as 4-methylphenoxide. Exemplary amides for Q are dimethylamide, diethylamide, methylethylamide, di-t-butylamide, dilsopropyla- mide and the like. Exemplary aryl amides are diphenylamide and any other substituted phenyl amides. Exemplary phosphides for Q are diphenylphosphide, dicyclohexylphosphide, diethylphosphide, dimethylphos- phide and the like. Exemplary alkyldiene radicals for both Q together are methylidene, ethylidene and propylidene. Examples of the Q group which are suitable as a constituent group or element of the Group IV B transition metal component of the catalyst system are identified in Column 4 of Table 1 under the heading "Q".
Suitable hydrocarbyl and substituted hydrocarbyl radicals, which may be substituted as an R group for at least one hydrogen atom in the cyclopentadienyl ring, will contain from 1 to about 20 carbon atoms and include straight and branched alkyl radicals, cyclic hydrocarbon radicals, alkyl-substituted cyclic hydrocarbon radicals, aromatic radicals, alkyl-substituted aromatic radicals and cyclopentadienyl rings containing 1 or more fused saturated or unsaturated rings. Suitable organometallic radicals, which may be substituted as an R group for at least one hydrogen atom in the cyclopentadienyl ring, include trimethylsilyl, triethylsilyl, ethyldimethylsilyl, methyldiethylsilyl, triphenylgermyl, trimethylgermyl and the like. Examples of cyclopentadienyl ring groups (C5H5-y-xRx) which are suitable as a constituent group of the Group IV B transition metal component of the catalyst system are identified in Column 2 of Table 1 under the heading (C5H5-y-xRx).
Suitable hydrocarbyl and substituted hydrocarbyl radicals, which may be substituted as an R' group for at least one hydrogen atom in the heteroatom J ligand group, will contain from 1 to about 20 carbon atoms and include straight and branched alkyl radicals, cyclic hydrocarbon radicals, alkyl-substituted cyclic hydrocarbon radicals, aromatic radicals and alkyl-substituted aromatic radicals. Examples of heteroatom ligand groups (JR'z- y) which are suitable as a constituent group of the Group IV B transition metal component of the catalyst system are identified in Column 3 of Table 1 under the heading (JR'z-1-y).
Table 1 depicts representative constituent moieties for the "Group IV B transition metal component", the list is for illustrative purposes only and should not be construed to be limiting in any way. A number of final components may be formed by permuting all possible combinations of the constituent moieties with each other. Illustrative compounds are: dimethylsilyltetramethylcyclopentadienyl-tert-butylamido zirconium dichloride, dimethylsilyltetramethylcyclopentadienyl-tert-butylamido hafnium dichloride, dimethylsilyl-tert-butylcyclopentadienyl-tert-butylamido zirconium dichloride, dimethylsilyl-tert-butylcyclopentadienyl-tert-butylamido hafnium dichloride, dimethylsilyltrimethylsilylcyclopentadienyl-tert-butylamido zirconium dichloride, dimethylsilyltetra- methylcyclopentadienylphenylamido zirconium dichloride, dimethylsilyltetramethylcyclopentadienylphenyla- mido hafnium dichloride, methylphenylsilyltetramethylcyclopentadienyl-tert-butylamido zirconium dichloride, methylphenylsilyltetramethylcyclopentadienyl-tert-butytamido hafnium dichloride, methylphenylsilyltetramethylcyclopentadienyl-tert-butylamido hafnium dimethyl, dimethylsilyltetramethylcyclopentadienyi-p-li-butyl- phenylamido zirconium dichloride, dimethylsilyltetramethylcyclopentadienyi-p-11-butylphenylamido hafniuim dichloride. For illustrative purposes, the above compounds and those permuted from Table 1 does not include the Lewis base ligand (L). The conditions under which complexes containing Lewis base ligands such as ether or those which form dimers is determined by the steric bulk of the ligands about the metal center. For example, the t-butyl group in Me2Si(Me4C5)(N-t-Bu)ZrCl2 has greater steric requirements than the phenyl group in Me2Si(Me4C5)(NPh)ZrCl2·Et2O thereby not permitting ether coordination in the former compound. Similarly, due to the decreased steric bulk of the trimethylsilylcyclopentadienyl group in [Me2Si(Me3SiC5H3)(N-t-Bu) ZrCl2]2 versus that of the tetramethylcyclopentadienyl group in Me2Si(Me4C5)(N-t-Bu) ZrC12, the former compound is dimeric and the latter is not.
Suitable, but not limiting, Group IV B transition metal compounds which may be utilized in the catalyst system of this invention include those bridged species ("y"=1) wherein the B group bridge is a dialkyl, diaryl or alkylaryl silane, or methylene or ethylene. Exemplary of the more preferred species of bridged Group IV B transition metal compounds are dimethylsilyl, methylphenylsilyl, diethylsilyl, ethylphenylsilyl, diphenylsilyl, ethylene or methylene bridged compounds. Most preferred of the bridged species are dimethylsilyl, diethylsilyl and methylphenylsilyl bridged compounds.
Suitable Group IV B transition metal compounds which are illustrative of the unbridged ("y"=0) species which may be utilized in the catalyst systems of this invention are exemplified by pentamethylcyclopentadie- nyldi-t-butylphosphinodimethyl hafnium; pentamethyicyciopentadienyidi-t-butyiphosphinomethyiethyi hafnium; cyclopentadienyl-2-methylbutoxide dimethyl titanium.
To illustrate members of the Group IV B transition metal component, select any combination of the species in Table 1. An example of a bridged species would be dimethylsilylcyclopentadienyl-t-butylamidodichloro zirconium; an example of an unbridged species would be cyclopentadienyldi-t-butylamildodichloro zirconium.
The alumoxane component of the catalyst system is an oligomeric compound which may be represented by the general formula (R2-Al-O)m which is a cyclic compound, or may be R3(R4-Al-O-)m-AIR5 2 which is a linear compound. An alumoxane is generally a mixture of both the linear and cyclic compounds. In the general alumoxane formula R2, R3, R4, and R5 are, independently a univalent anionic ligand such as a Cl-C5 alkyl radical, for example, methyl, ethyl, propyl, butyl, pentyl or halide and "m" is an integer from 1 to about 50. Most preferably, R2, R3, R4 and R5 are each methyl and "m" is at least 4. When an alkyl aluminum halide is employed in the preparation of alumoxane, one or more of R2-5 could be halide.
Suitable alumoxanes which may be utilized in the catalyst systems of this invention are those prepared by the hydrolysis of a alkylaluminum reagent; such as trimethylaluminum, triethyaluminum, tripropylaluminum; trilsobutylaluminum, dimethylaluminumchloride, diisobutylaluminumchloride, diethylaluminumchloride, and the like. The most preferred alumoxane for use is methylalumoxane (MAO), particularly methylalumoxanes having a reported average degree of oligomerization of from about 4 to about 25 ("m"=4 to 25) with a range of 13 to 25 being most preferred.
The catalyst system may include an alkyl aluminum and water which may react at least partly with each other and/or with the metallocene compound outside of a polymerization vessel for what may be a reaction in situ in the polymerization vessel.
The catalyst system may be conveniently prepared by placing the selected Group IV B transition metal component and the selected alumoxane component, in any order of addition, in an alkane or aromatic hydrocarbon solvent -- preferably one which is also suitable for service as a polymerization diluent. Where the hydrocarbon solvent utilized is also suitable for use as a polymerization diluent, the catalyst system may be prepared in situ in the polymerization reactor. Alternatively, the catalyst system may be separately prepared, in concentrated form, and added to the polymerization diluent in a reactor. Or, if desired, the components of the catalyst system may be prepared as separate solutions and added to the polymerization diluent in a reactor, in appropriate ratios, as is suitable for a continuous liquid polymerization reaction procedure. Alkane and aromatic hydrocarbons suitable as solvents for formation of the catalyst system and also as a polymerization diluent are exemplified by, but are not necessarily limited to, straight and branched chain hydrocarbons such as isobutane, butane, pentane, hexane, heptane, octane and the like, cyclic and alicyclic hydrocarbons such as cyclohexane, cycloheptane, methylcyclohexane, methylcycloheptane and the like, and aromatic and alkyl-substituted aromatic compounds such as benzene, toluene, xylene and the like. Suitable solvents also include liquid olefins which may act as monomers or comonomers including ethylene, propylene, 1-butene, 1-hexene and the like.
In accordance with this invention optimum results are generally obtained wherein the Group IV B transition metal compound is present in the polymerization diluent in a concentration of from about 0.0001 to about 1.0 millimole/liter of diluent and the alumoxane component is present in an amount to provide a molar aluminum to transition metal ratio of from about 1:1 1 to about 20,000: 1. Sufficient solvent should be employed so as to provide adequate heat transfer away from the catalyst components during reaction and to permit good mixing.
The catalyst system ingredients -- that is, the Group IV B transition metal, the alumoxane, and polymerization diluent can be added to the reaction vessel rapidly or slowly. The temperature maintained during the contact of the catalyst components can vary widely, such as, for example, from -10° to 300°C. Greater or lesser temperatures can also be employed. Preferably, during formation of the catalyst system, the reaction is maintained within a temperature of from about 25° to 100°C, most preferably about 25°C.
The monomer for such process may comprise ethylene alone, for the production of a homopolyethylene, or ethylene in combination with an α-olefin having 3 to 20 carbon atoms for the production of an ethylene-a-olefin copolymer. Homopolymers of higher a-olefin such as propylene, butene, styrene and copolymers thereof with ethylene and/or C4 or higher α-olefins and diolefins can also be prepared. Conditions most preferred for the homo- or co-polymerization of ethylene are those wherein ethylene is submitted to the reaction zone at pressures of from about 0.019 psia to about 50,000 psia and the reaction temperature is maintained at from about-100° to about 300°C. The aluminum to transition metal molar ratio is preferably from about 1:1 to 18,000 to 1. A preferable range would be 1:1 1 to 1000: 1. The reaction time is preferably from about 1 min to about 1 hr. Without limiting in any way the scope of the invention, one means for carrying out the process of the present invention is as follows: in a stirred-tank reactor liquid 1-butene monomer is introduced. The catalyst system is introduced via nozzles in either the vapor or liquid phase. Feed ethylene gas is introduced either into the vapor phase of the reactor, or sparged into the liquid phase as is well known in the art. The reactor contains a liquid phase composed substantially of liquid 1-butene together with dissolved ethylene gas, and a vapor phase containing vapors of all monomers. The reactor temperature and pressure may be controlled via reflux of vaporizing α-olefin monomer (autorefrigeration), as well as by cooling coils, jackets etc. The polymerization rate is controlled by the concentration of catalyst. The ethylene content of the polymer product is determined by the ratio of ethylene to 1-butene in the reactor, which is controlled by manipulating the relative feed rates of these components to the reactor.
In the examples which illustrate the practice of the invention the analytical techniques described below were employed for the analysis of the resulting polyolefin products. Molecular weight determinations for polyolefin products were made by Gel Permeation Chromatography (GPC) according to the following technique. Molecular weights and molecular weight distributions were measured using a Waters 150 gel permeation chromatograph equipped with a differential refractive index (DRI) detector and a Chromatix KMX-6 on-line light scattering photometer. The system was used at 135°C with 1,2,4-trichlorobenzene as the mobile phase. Sho- dex (Showa Denko America, Inc.) polystyrene gel columns 802, 803, 804 and 805 were used. This technique is discussed in "Liquid Chromatography of Polymers and Related Materials III", J. Cazes editor, Marcel Dekker, 1981, p. 207 which is incorporated herein by reference. No corrections for column spreading were employed; however, data on generally accepted standards, e.g. National Bureau of Standards Polyethylene 1484 and anionically produced hydrogenated polyisoprenes (an alternating ethylene-propylene copolymer) demonstrated that such corrections on Mw/Mn (= MWD) were less than 0.05 units. Mw/Mn was calculated from elution times. The numerical analyses were performed using the commercially available Beckman/CIS customized LALLS software in conjunction with the standard Gel Permeation package, run on a HP 1000 computer.
All procedures were performed under an inert atmosphere of helium or nitrogen. Solvent choices are often optional, for example, in most cases either pentane or 30-60 petroleum ether can be interchanged. The lithiated amides were prepared from the corresponding amines and either n-BuLi or MeLi. Published methods for preparing LiHC5Me4 include C.M. Fendrick et al. Organometallics, 3, 819 (1984) and F.H. Köhler and K. H. Doll, Z. Naturforsch, 376, 144 (1982). Other lithiated substituted cyclopentadienyl compounds are typically prepared from the corresponding cyclopentadienyl ligand and n-BuLi or MeLi, or by reaction of MeLi with the proper ful- vene. ZrC14 and HfC14 were purchased from either Aldrich Chemical Company or Cerac. Amines, silanes and lithium reagents were purchased from Aldrich Chemical Company or Petrarch Systems. Methylalumoxane was supplied by either Sherring or Ethyl Corp.
Examples A-L of Group IV B Transition Metal Components Example A Compound A:
Part 1. Me4HC5Li (10.0 g, 0.078 mol) was slowly added to a Me2SiCI2 (11.5 ml, 0.095 mol, in 225 ml of tetrahydrofuran (thf) solution). The solution was stirred for 1 hour to assure complete reaction. The thf solvent was then removed via a vacuum to a cold trap held at -196°C. Pentane was added to precipitate out the LiCI. The mixture was filtered through Celite. The solvent was removed from the filtrate. Me4HC5Si-Me2Cl (15.34 g, 0.071 mol) was recovered as a pale yellow liquid.
Part 2. Me4HC5SiMe2Cl (10.0 g, 0.047 mol) was slowly added to a suspension of LiHN-t-Bu (3.68 g, 0.047 mol, ~100 ml thf). The mixture was stirred overnight. The thf was then removed via a vacuum to a cold trap held at -196°C. Petroleum ether (-100 ml) was added to precipitate out the LiCI. The mixture was filtered through Celite. The solvent was removed from the filtrate. Me2Si(Me4HC5)(HN-t-Bu) (11.14 g, 0.044 mol) was isolated as a pale yellow liquid.
Part 3. Me2Si(Me4HC5)(HN-t-Bu) (11.14 g, 0.044 mol) was diluted with -100 ml Et20. MeLi (1.4 M, 64 ml, 0.090 mol) was slowly added. The mixture was allowed to stir for 1/2 hour after the final addition of MeLi. The ether was reduced in volume prior to filtering off the product. The product, [Me2Si(Me4C5)(N-t-Bu)]Li2, was washed with several small portions of ether, then vacuum dried.
Part 4. [Me2Si(Me4C5)(N-t-Bu)]Li2 (3.0 g, 0.011 mol) was suspended in -150 ml Et20. ZrC14 (2.65 g, 0.011 mol) was slowly added and the resulting mixture was allowed to stir overnight. The ether was removed via a vacuum to a cold trap held at -196°C. Pentane was added to precipitate out the LiCI. The mixture was filtered through Celite twice. The pentane was significantly reduced in volume and the pale yellow solid was filtered off and washed with solvent. Me2Si(Me4C5)(N-t-Bu)ZrCl2 (1.07 g, 0.0026 mole) was recovered. Additional Me2Si(Me4C5)(N-t-Bu)ZrCI2 was recovered from the filtrate by repeating the recrystallization procedure. Total yield, 1.94 g, 0.0047 mol).
Example B Compound B:
The same procedure of Example A for preparing compound A was followed with the exception of the use of HfC14 in place of ZrCl4 in Part 4. Thus, when [Me2Si(Me4C5)(N-t-Bu)]Li2 (2.13 g, 0.0081 mol) and HfCl4 (2.59 g, 0.0081 mol) were used, Me2Si(Me4C5)(N-t-Bu)HfCl2 (0.98 g, 0.0020 mol) was produced.
Example C Compound C:
Part 1. Me2SiCI2 (7.5 ml, 0.062 mol) was diluted with -30 ml thf. At-BuH4C5Li solution (7.29 g, 0.056 mol, ~100 ml thf) was slowly added, and the resulting mixture was allowed to stir overnight. The thf was removed via a vacuum to a trap held at-196°C. Pentane was added to precipitate out the LiCI, and the mixture was filtered through Celite. The pentane was removed from the filtrate leaving behind a pale yellow liquid, t-BuH4C5SiMe2,Cl (10.4 g, 0.048 mol).
Part 2. To a thf solution of LiHN-t-Bu (3.83 g, 0.048 mol, -125 ml), t-BuH4C5SiMe2Cl (10.4 g, 0.048 mol) was added drop wise. The resulting solution was allowed to stir overnight. The thf was removed via a vacuum to a trap held at -196°C. Pentane was added to precipitate out the LiCI, and the mixture was filtered through Celite. The pentane was removed from the filtrate leaving behind a pale yellow liquid, Me2Si(t-BuH4C5)(NH-t-Bu) (11.4 g, 0.045 mol).
Part 3. Me2Si(t-BuH4C5)(NH-t-Bu) (11.4 g, 0.045 mol) was diluted with -100 ml Et20. MeLi (1.4 M, 70 ml, 0.098 mol) was slowly added. The mixture was allowed to stir overnight. The ether was removed via a vacuum to a trap held at -196°C, leaving behind a pale yellow solid, [Me2Si(t-BuH3C5)(N-t-Bu)]Li2 (11.9 g, 0.045 mol).
Part 4. [Me2Si(t-BuH3C5)(N-t-Bu)]Li2 (3.39 g, 0.013 mol) was suspended in -100 ml Et20. ZrCl4 (3.0 g, 0.013 mol) was slowly added. The mixture was allowed to stir overnight. The ether was removed and pentane was added to precipitate out the LiCI. The mixture was filtered through Celite. The pentane solution was reduced in volume, and the pale tan solid was filtered off and washed several times with small quantities of pentane. The product of empirical formula Me2Si(t-BuH3C5)(N-t-Bu)ZrCl2 (2.43 g, 0.0059 mol) was isolated.
Example D Compound D:
The same procedure of Example C for preparing compound C was followed with the exception of the use of HfCl4 in Part 4. Thus, when [Me2Si(t-BuH3C5)(N-t-Bu)]Li2 (3.29 g, 0.012 mol) and HfCl4 (4.0 g, 0.012 mol) were used, the product of the empirical formula Me2Si(t-BuH3C5)(N-t-Bu)HfCl2 (1.86 g, 0.0037 mol) was produced.
Example E Compound E:
Part 1. Me2SiCI2 (7.0 g, 0.054 mol) was diluted with ~100 ml of ether. Me3SiC5H4Li (5.9 g, 0.041 mol) was slowly added. Approximately 75 ml of thf was added and the mixture was allowed to stir overnight. The solvent was removed via a vacuum to a cold trap held at -196°C. Pentane was added to precipitate out the LiCI. The mixture was filtered through Celite. The solvent was removed from the filtrate giving Me2Si(Me3SiC5H4)CI (8.1 g, 0.035 mol) as a pale yellow liquid.
Part 2. Me2Si(Me3SiC5H4)CI (3.96 g, 0.017 mol) was diluted with ~50 ml of ether. LiHN-t-Bu (1.36 g, 0.017 mol) was slowly added, and the mixture was allowed to stir overnight. The ether was removed via a vacuum and pentane was added to precipitate the LiCI. The mixture was filtered through Celite, and the pentane was removed from the filtrate. Me2Si-(Me3SiC5H4)(NH-t-Bu) (3.7 g, 0.014 mol) was isolated as a pale yellow liquid.
Part 3. Me2Si(Me3SiC5H4)(NH-t-Bu) (3.7 g, 0.014 mol) as diluted with ether. MeLi (25 ml, 1.4M in ether, 0.035 mol) was slowly added. The mixture was allowed to stir for 1.5 hours after the final addition of MeLi. The ether was removed via vacuum producing 4.6 g of a white solid formulated as Li2[Me2Si-(Me3SiC5H3)(N.t-Bu)]·3/4Et2O and unreacted MeLi which was not removed from the solid.
Part 4. Li2[Me2Si(Me3SiC5H3)(N-t-Bu)]·3/4Et2O (1.44 g, 0.0043 mol) was suspended in -50 ml of ether. ZrC14 (1.0 g, 0.0043 mol) was slowly added and the reaction was allowed to stirfor a few hours. The solvent was removed via vacuum and pentane was added to precipitate the LiCI. The mixture was filtered through Celite, and the filtrate was reduced in volume. The flask was placed in the freezer (-40°C) to maximize precipitation of the product. The solid was filtered off giving 0.273 g of an off white solid. The filtrate was again reduced in volume, the precipitate filtered off to give an additional 0.345 g for a total of 0.62 g of the compound with empirical formula Me2Si(Me3SiC5H3)(N-t-Bu)ZrCl2. The x-ray crystal structure of this product reveals that the compound is dimeric in nature.
Example F Compound F:
Part 1. Me4HC5SiMe2Cl was prepared as described in Example A for the preparation of compound A, Part 1.
Part 2. LiHNPh (4.6 g, 0.0462 mol) was dissolved in -100 ml of thf. Me4HC5SiMe2Cl (10.0 g, 0.0466 mol) was slowly added. The mixture was allowed to stir overnight. The thfwas removed via a vacuum. Petroleum ether and toluene were added to precipitate the LiCI, and the mixture was filtered through Celite. The solvent was removed, leaving behind a dark yellow liquid, Me2Si(Me4HC5)(NHPh) (10.5 g, 0.0387 mol).
Part 3. Me2Si(Me4HC5)(NHPh) (10.5.g, 0.0387 mol) was diluted with -60 ml of ether. MeLi (1.4 M in ether, 56 ml, 0.0784 mol) was slowly added and the reaction was allowed to stir overnight. The resulting white solid, Li2[Me2Si(Me4C5)(NPh)·3/4Et2O (11.0 g), was filtered off and was washed with ether.
Part 4. Li2[Me2Si(Me4C5)(NPh)·3/4Et2O (2.81 g, 0.083 mol) was suspended in -40 ml of ether. ZrC14 (1.92 g, 0.0082 mol) was slowly added, and the mixture was allowed to stir overnight. The ether was removed via a vacuum, and a mixture of petroleum ether and toluene was added to precipitate the LiCI. The mixture was filtered through Celite, the solvent mixture was removed via vacuum, and pentane was added. The mixture was placed in the freezer at -40°C to maximize the precipitation of the product. The solid was then filtered off and washed with pentane. Me2Si(Me4C5)(NPh)ZrCl2·Et2O was recovered as a pale yellow solid (1.89 g).
Example G Compound G:
The same procedure of Example F for preparing compound F was followed with the exception of the use of HfCl4 in place of ZrCl4 in Part 4. Thus, when Li2(Me2Si(Me4C5)(NPh)]·3/4Et2O] (2.0 g, 0.0059 mol) and HfCl4 (1.89 g, 0.0059 mol) were used, Me2Si(Me4C5)(NPh)HfCl2·1/2Et2O (1.70 g) was produced.
Example H Compound H:
Part 1. MePhSiCl2 (14.9 g, 0.078 mol) was diluted with -250 ml of thf. Me4C5HLi (10.0 g, 0.078 mol) was slowly added as a solid. The reaction solution was allowed to stir overnight. The solvent was removed via a vacuum to a cold trap held at -196°C. Petroleum ether was added to precipitate out the LiCI. The mixture was filtered through Celite, and the pentane was removed from the filtrate. MePhSi(Me4C5H)CI (20.8 g, 0.075 mol) was isolated as a yellow viscous liquid.
Part 2. LiHN-t-Bu (4.28 g, 0.054 mol) was dissolved in -100 ml of thf. MePhSi(Me4C5H)CI (15.0 g, 0.054 mol) was added drop wise. The yellow solution was allowed to stir overnight. The solvent was removed via vacuum. Petroleum ether was added to precipitate out the LiCI. The mixture was filtered through Celite, and the filtrate was evaporated down. MePhSi(Me4C5H)(NH-t-Bu) (16.6 g, 0.053 mol) was recovered as an extremely viscous liquid.
Part 3. MePhSi(Me4C5H)(NH-t-Bu) (16.6 g, 0.053 mol) was diluted with ~ 100 ml of ether. MeLi (76 ml, 0.106 mol, 1.4 M) was slowly added and the reaction mixture was allowed to stir for -3 hours. The ether was reduced in volume, and the lithium salt was filtered off and washed with pentane producing 20.0 g of a pale yellow solid formulated as Li2[MePhSi(Me4C5)(N-t-Bu)]·3/4Et2O.
Part 4. Li2[MePhSi(Me4C5)(N-t-Bu)]·3/4Et2O (5.0 g, 0.0131 mol) was suspended in ~100 ml of Et2O. ZrCl4 (3.06 g, 0.0131 mol) was slowly added. The reaction mixture was allowed to stir at room temperature for -1.5 hours over which time the reaction mixture slightly darkened in color. The solvent was removed via vacuum and a mixture of petroleum ether and toluene was added. The mixture was filtered through Celite to remove the LiCI. The filtrate was evaporated down to near dryness and filtered off. The off white solid was washed with petroleum ether. The yield of product, MePhSi(Me4C5)(N-t-Bu)ZrCI2, was 3.82 g (0.0081 mol).
Example I Compound I:
Li2[MePhSi(Me4C5)(N-t-Bu)]·3/4Et2O was prepared as described in Example H for the preparation of compound H, Part 3.
Part 4. Li2[MePhSi(Me4C5)(N-t-Bu)]·3/4Et2O (5.00 g, 0.0131 mol) was suspended in ~100 ml of Et20. HfCl4 (4.20 g, 0.0131 mol) was slowly added and the reaction mixture was allowed to stir overnight. The solvent was removed via vacuum and petroleum ether was added to precipitate out the LiCI. The mixture was filtered through Celite. The filtrate was evaporated down to near dryness and filtered off. The off white solid was washed with petroleum ether. MePhSi(Me4C5)(N-t-Bu)HfCl2 was recovered (3.54 g, 0.0058 mole).
Example J Compound J:
MePhSi(Me4C5)(N-t-Bu)HfMe2 was prepared by adding a stoichiometric amount of MeLi (1.4 M in ether) to MePhSi(Me4C5)(N-t-Bu)HfCl2 suspended in ether. The white solid could be isolated in near quantitative yield.
Example K Compound K:
Part 1. Me4C5SiMe2Cl was prepared as described in Example A for the preparation of compound A, Part 1.
Part 2. Me4C5SiMe2Cl (10.0 g, 0.047 mol) was diluted with -25 ml Et20. LiHNC5H4-p-n-Bu·1/10Et2O] (7.57 g, 0.047 mol) was added slowly. The mixture was allowed to stir for -3 hours. The solvent was removed via vacuum. Petroleum ether was added to precipitate out the LiCI, and the mixture was filtered through Celite. the solvent was removed leaving behind an orange viscous liquid, Me2Si(Me4C5H)(HNC6H4-p-un-Bu) (12.7 g, 0.039 mol).
Part 3. Me2Si(Me4C5H)(HNC6H4-p-n-Bu) (12.7 g, 0.039 mol) was diluted with -50 ml of Et20. Meli (1.4 M, 55 ml, 0.077 mol) was slowly added. The mixture was allowed to stir for ~3 hours. The product was filtered off and washed with Et20 producing Li2[Me2Si(Me4C5)(NC6H4-p-n-Bu)]·3/4Et2O as a white solid (13.1 g, 0.033 mol).
Part 4. Li2[Me2Si(Me4C5)(NC6H4-p-n-Bu)]·3/4Et2O (3.45 g, 0.0087 mol) was suspended in -50 ml of Et20. ZrCl4 (2.0 g, 0.0086 mol) was slowly added and the mixture was allowed to stir overnight. The ether was removed via vacuum, and petroleum ether was added to precipitate out the LiCI. The mixture was filtered through Celite. The filtrate was evaporated to dryness to give a yellow solid which was recrystallized from pentane and identified as Me2Si(Me4C5)(NC6H4-p-n-Bu)ZrCi2·2/3Et2O (4.2 g).
Example L Compound L:
Li2[Me2Si(Me4C5)(NC6H4-p-n-Bu)]·3/4Et2O was prepared as described in Example K for the preparation of compound K, Part 3.
Part 4. Li2[Me2Si(Me4C5)(NC6H4-n-11-Bu)·3/4Et2O (3.77 g, 0.0095 mol) was suspended in -50 ml of Et20. HfCl4 (3.0 g, 0.0094 mol) was slowly added as a solid and the mixture was allowed to stir overnight. The ether was removed via vacuum and petroleum ether was added to precipitate out the LiCI. The mixture was filtered through Celite. Petroleum ether was removed via a vacuum giving an off white solid which was recrystallized from pentane. The product was identified as Me2Si(Me4Cs)(NC6H4-p-n-Bu)HfCi2 (1.54 g, 0.0027 mol).
Examples 1-34 of Polymerization Example 1 Polymerization - Compound A
The polymerization run was performed in a 1-liter autoclave reactor equipped with a paddle stirrer, an external water jacket for temperature control, a regulated supply of dry nitrogen, ethylene, propylene, 1-butene and hexane, and a septum inlet for introduction of other solvents, transition metal compound and alumoxane solutions. The reactor was dried and degassed thoroughly prior to use. Atypical run consisted of injecting 400 ml of toluene, 6 ml of 1.5 M MAO, and 0.23 mg of compound A (0.2 ml of a 11.5 mg in 10 ml of toluene solution) into the reactor. The reactor was then heated to 80°C and the ethylene (60 psi) was introduced into the system. The polymerization reaction was limited to 30 minutes. The reaction was ceased by rapidly cooling and venting the system. The solvent was evaporated off of the polymer by a stream of nitrogen. Polyethylene was recovered (9.2 g, MW = 257,200, MWD = 2.275).
Example 2 Polymerization - Compound A
The polymerization was carried out as in Example 1 with the following changes: 300 ml of toluene, 3 ml of 1.5 M MAO, and 0.115 mg of compound A (0.1 ml of a 11.5 mg in 10 ml of toluene solution). Polyethylene was recovered (3.8 g, MW = 359,800, MWD = 2.425).
Example 3 Polymerization - Compound A
The polymerization was carried out as in Example 2 using the identical concentrations. The difference involved running the reaction at 40°C rather than 80°C as in the previous example. Polyethylene was recovered (2.4 g, MW = 635,000, MWD = 3.445).
Example 4 Polymerization - Compound A
The polymerization was carried out as in Example 1 except for the use of 300 ml of hexane in place of 400 ml of toluene. Polyethylene was recovered (5.4 g, MW = 212,600, MWD = 2.849).
Example 5 Polymerization - Compound A
Using the same reactor design and general procedure as in Example 1, 300 ml of toluene, 200 ml of propylene, 6.0 ml of 1.5 M MAO, and 0.46 mg of compound A (0.4 ml of a 11.5 mg in 10 ml of toluene solution) was introduced into the reactor. The reactor was heated to 80°C, the ethylene was added (60 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 13.3 g of an ethylene-propylene copolymer was recovered (MW = 24,900, MWD = 2.027, 73.5 SCB/1000C by IR).
Example 6 Polymerization - Compound A
The polymerization was carried out as in Example 5 except with the following changes: 200 ml of toluene and 0.92 mg of compound A (0.8 ml of a 11.5 mg li 10 ml of toluene solution). The reaction temperature was also reduced to 50°C. An ethylene-propylene copolymer was recovered (6.0 g, MW = 83,100, MWD = 2.370, 75.7 SCB/1000C by IR).
Example 7 Polymerization - Compound A
Using the same reactor design and general procedure as in Example 1, 150 ml of toluene, 100 ml of 1-butene, 6.0 ml of 1.5 M MAO, and 2.3 mg of compound A (2.0 ml of a 11.5 mg in 10 ml of toluene solution) were added to the reactor. The reactor was heated at 50°C, the ethylene was introduced (65 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the toluene, 25.4 g of an ethylene-butene copolymer was recovered (MW = 184,500, MWD = 3.424, 23.5 SCB/1000C by 13C NMR and 21.5 SCB/1000C by IR).
Example 8 Polymerization - Compound A
The polymerization was carried out as in Example 7 except with the following changes: 100 ml of toluene and 150 ml of 1-butene. An ethylene-butene copolymer was recovered (30.2 g, MW = 143,500, MWD = 3.097, 30.8 SCB/1000C by 13C NMR and 26.5 SCB/1000C by IR).
Example 9 Polymerization - Compound A
The polymerization was carried out as in Example 7 except with the following changes: 200 ml of toluene, 8.0 ml of 1.0 M MAO, and 50 ml of 1-butene. An ethylene-butene copolymer was recovered (24.9 g, MW = 163,200, MWD = 3.290, 23.3 SCB/1000C by 13C NMRand 18.9 SCB/1000C by IR).
Example 10 Polymerization - Compound A
The polymerization was carried out as in Example 9 except for the replacement of 200 ml of toluene with 200 ml of hexane. An ethylene-butene copolymer was recovered (19.5 g, MW = 150,600, MWD = 3.510, 12.1 SCB/1000 C by 13C NMR and 12.7 SCB/1000C by IR).
Example 11 Polymerization - Compound A
The polymerization was carried out as in Example 10 except with the following changes: 150 ml of hexane, and 100 ml of 1-butene. An ethylene-butene copolymer was recovered (16.0 g, MW = 116,200, MWD = 3.158, 19.2 SCB/1000C by 13C NMR and 19.4 SCB/1000C by IR).
Example 12 Polymerization - Compound A
Using the same reactor design and general procedure already described, 400 ml of toluene, 5.0 ml of 1.0 M MAO, and 0.2 ml of a preactivated compound Asolution (11.5 mg of compound Adissolved in 9.0 ml of toluene and 1.0 ml of 1.0 M MAO) were added to the reactor. The reactor was heated to 80°C, the ethylene was introduced (60 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 3.4 g of polyethylene was recovered (MW = 285,000, MWD = 2.808).
Example 13 Polymerization - Compound A
A polymerization was carried out as in Example 12 with exception of aging the preactivated compound A solution by one day. Polyethylene was recovered (2.0 g, MW = 260,700, MWD = 2.738).
Example 14 Polymerization - Compound A
Using the same reactor design and general procedure already described, 400 ml of toluene, 0.25 ml of 1.0 M MAO, and 0.2 ml of a preactivated compound Asolution (11.5 mg of compound Adissolved in 9.5 ml of toluene and 0.5 ml of 1.0 M MAO), were added into the reactor. The reactor was heated to 80°C, the ethylene was introduced (60 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 1.1 g of polyethylene was recovered (MW = 479,600, MWD = 3.130).
Example 15 Polymerization - Compound A
Using the same reactor design and general procedure already described, 400 ml of toluene and 2.0 ml of a preactivated compound A solution (11.5 mg of compound A dissolved in 9.5 ml of toluene and 0.5 ml of 1.0 M MAO) were added into the reactor. The reactor was heated to 80°C, the ethylene was introduced (60 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 1.6 g of polyethylene was recovered (MW = 458,800, MWD = 2.037).
Example 16 Polymerization - Compound A
Using the general procedure already described, 400 ml of toluene, 5.0 ml of 1.0 M MAO, 0.23 mg of compound A (0.2 ml of a 11.5 mg in 10 ml of toluene solution) was added to the reactor. The reactor was heated to 80°C, the ethylene introduced (400 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 19.4 g of polyethylene was recovered (MW = 343,700, MWD = 3.674).
Example 17 Polymerization - Compound A
The polymerization was performed in a stirred 100 ml stainless steel autoclave which was equipped to perform polymerizations at pressures up to 40,000 psi and temperatures up to 300°C. The reactor was purged with nitrogen and heated to 160°C. Compound A and alumoxane solutions were prepared in separate vials. A stock solution was prepared by dissolving 26 mg of compound A in 100 ml of toluene. The compound solution was prepared by diluting 0.5 ml of the stock solution with 5.0 ml of toluene. The alumoxane solution consisted of 2.0 ml of a 4% MAO solution added to 5.0 ml of toluene. The compound solution was added to the alumoxane solution, then 0.43 ml of the mixed solutions were transferred by nitrogen pressure into a constant-volume injection tube. The autoclave was pressurized with ethylene to 1784 bar and was stirred at 1500 rpm. The mixed solutions were injected into the stirred reactor with excess pressure, at which time a temperature rise of 4°C was observed. The temperature and pressure were recorded continuously for 120 seconds, at which time the contents of the autoclave were rapidly vented into a receiving vessel. The reactor was washed with xylene to recover any additional polymer remaining within. These washings were combined with the polymer released when the autoclave was vented to yield 0.7 g of polyethylene (MW = 245,500, MWD = 2.257).
Example 18 Polymerization - Compound B
Using the general procedure described in Example 1, 400 ml of toluene, 5.0 ml of 1.0 M MAO and 0.278 mg compound B (0.2 ml of a 13.9 mg in 10 ml of toluene solution) was added to the reactor. The reactor was heated to 80°C and the ethylene (60 psi) was introduced into the system. The polymerization reaction was limited to 10 minutes. The reaction was ceased by rapidly cooling and venting the system. The solvent was evaporated off the polymer by a stream of nitrogen. Polyethylene was recovered (9.6 g, MW = 241,200, MWD = 2.628).
Example 19 Polymerization - Compound C
Using the general procedures described in Example 1, 300 ml of toluene, 4.0 ml of 1.0 M MAO and 0.46 mg compound C (0.4 ml of a 11.5 mg in 10 ml of toluene solution) was added to the reactor. The reactor was heated to 80°C and the ethylene (60 psi) was introduced into the system. The polymerization reaction was limited to 30 minutes. The reaction was ceased by rapidly cooling and venting the system. The solvent was evaporated off the polymer by a stream of nitrogen. Polyethylene was recovered (1.7 g, MW = 278,400, MWD = 2.142).
Example 20 Polymerization - Compound D
Using the general procedure described in Example 1, 400 ml of toluene, 5.0 ml of 1.0 M MAO and 0.278 mg compound D (0.2 ml of a 13.9 mg in 10 ml of toluene solution) was added to the reactor. The reactor was heated to 80°C and the ethylene (60 psi) was introduced into the system. The polymerization reaction was limited to 30 minutes. The reaction was ceased by rapidly cooling and venting the system. The solvent was evaporated off the polymer by a stream of nitrogen. Polyethylene was recovered (1.9 g, MW = 229,700, MWD = 2.618).
Example 21 Polymerization - Compound E
Using the general procedure described in Example 1, 300 ml of hexane, 9.0 ml of 1.0 M MAO and 0.24 mg compound E (0.2 ml of a 12.0 mg in 10 ml of toluene solution) was added to the reactor. The reactor was heated to 80°C and the ethylene (60 psi) was introduced into the system. The polymerization reaction was limited to 30 minutes. The reaction was ceased by rapidly cooling and venting the system. The solvent was evaporated off the polymer by a stream of nitrogen. Polyethylene was recovered (2.2 g, MW = 258,200, MWD = 2.348).
Example 22 Polymerization - Compound E
The polymerization was carried out as in Example 1 with the following reactor contents: 200 ml of toluene, 100 mi 1-butene, 9.0 ml of 1.0 M MAO and 2.4 mg of compound E (2.0 ml of 12.0 mg in 10 ml of toluene solution) at 50°C. The reactor was pressurized with ethylene (65 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 1.8 g of an ethylene-butene copolymer was recovered (MW = 323,600, MWD = 2.463, 33.5 SCB/1000C by IR technique).
Example 23 Polymerization - Compound F
The polymerization was carried out as in Example 1 with the following reactor conditions: 400 ml of toluene, 5.0 ml of 1.0 M MAO, 0.242 mg of compound F (0.2 ml of a 12.1 mg in 10 ml of toluene solution), 80°C, 60 psi ethylene, 30 minutes. The run provided 5.3 g of polyethylene (MW = 319,900, MWD = 2.477).
Example 24 Polymerization - Compound F
The polymerization was carried out as in Example 1 with the following reactor conditions: 150 ml of toluene, 100 ml of 1-butene, 9.0 ml of 1.0 M MAO, 2.42 mg of compound F (2.0 ml of a 12.1 mg in 10 ml of toluene solution), 50°C, 65 psi ethylene, 30 minutes. The run provided 3.5 g of an ethylene-butene copolymer (MW = 251,300, MWD = 3.341, 33.28 SCB/1000C by lR technique).
Example 25 Polymerization - Compound G
The polymerization was carried out as in Example 1 with the following reactor conditions: 400 ml of toluene, 5.0 ml of 1.0 M MAO, 0.29 mg of compound G (0.2 ml of a 14.5 mg in 10 ml of toluene solution), 80°C, 60 psi ethylene, 30 minutes. The run provided 3.5 g of polyethylene (MW = 237,300, MWD = 2.549).
Example 26 Polymerization - Compound G
The polymerization was carried out in Example 1 with the following reactor conditions: 150 ml of toluene, 100 ml of 1-butene, 7.0 ml of 1.0 M MAO, 2.9 mg of compound G (2.0 ml of a 14.5 mg in 10 ml of toluene solution), 50°C, 65 psi ethylene, 30 minutes. The run provided 7.0 g of an ethylene-butene copolymer (MW = 425,000, MWD = 2.816, 27.11 SCB/1000C by IR technique).
Example 27 Polymerization - Compound H
The polymerization was carried out as in Example 1 with the following reactor conditions: 400 ml of toluene, 5.0 ml of 1.0 M MAO, 0.266 mg of compound H (0.2 ml of a 13.3 mg in 10 ml of toluene solution), 80°C, 60 psi ethylene, 30 minutes. The run provided 11.1 g of polyethylene (MW, 299,800, MWD = 2.569).
Example 28 Polymerization - Compound H
The polymerization was carried out as in Example 1 with the following reactor conditions: 150 ml of toluene, 100 ml of 1-butene, 7.0 ml of 1.0 M MAO, 2.66 mg of compound H (2.0 ml of a 13.3 mg in 10 ml of toluene solution), 50°C, 65 psi ethylene, 30 minutes. The run provided 15.4 g of an ethylene-butene copolymer (MW = 286,600, MWD = 2.980, 45.44 SCB/1000C by IR technique).
Example 29 Polymerization - Compound I
The polymerization was carried out as in Example 1 with the following reactor conditions: 400 ml of toluene, 5.0 ml of 1.0 MAO, and 0.34 mg of compound 1 (0.2 ml of a 17.0 mg in 10 ml of toluene solution) was added to the reactor. The reactor was heated to 80°C, the ethylene was introduced (60 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 0.9 g of polyethylene was recovered (MW = 377,000, MWD = 1.996).
Example 30 Polymerization - Compound J
The polymerization was carried out as in Example 1 with the following reactor conditions: 400 ml of toluene, 5.0 ml of 1.0 M MAO, 0.318 mg of compound J (0.2 ml of a 15.9 mg in 10 ml of toluene solution), 80°C, 60 psi ethylene, 30 minutes. The run provided 8.6 g of polyethylene (MW = 321,000, MWD = 2.803).
Example 31 Polymerization - Compound J
The polymerization was carried out as in Example 1 with the following reactor conditions: 150 ml of toluene, 100 ml of 1-butene, 7.0 ml of 1.0 MAO, 3.18 mg of Compound J (2.0 ml of a 15.9 mg in 10 mi of toluene solution), 50°C, 65 psi ethylene, 30 minutes. The run provided 11.2 g of an ethylene-butene copolymer (MW = 224,800, MWD = 2.512, 49.57 SCB/1000C by IR technique, 55.4 SCB/1000C by NMR technique).
Example 32 Polymerization - Compound K
The polymerization was carried out as in Example 1 with the following reactor conditions: 300 ml of toluene, 5.0 ml of 1.0 M MAO, 0.272 mg of compound K (0.2 ml of a 13.6 mg in 10 ml of toluene solution), 80°C, 60 psi ethylene, 30 minutes. The run provided 26.6 g of polyethylene (MW = 187,300, MWD = 2.401).
Example 33 Polymerization - Compound K
The polymerization was carried out as in Example 1 with the following reactor conditions: 150 ml of toluene, 100 ml of 1-butene, 7.0 ml of 1.0 M MAO, 2.72 mg of compound (2.0 ml of a 13.6 mg in 10 ml of toluene solution), 50°C, 65 psi ethylene, 30 minutes. The run provided 3.9 g of an ethylene-butene copolymer (MW = 207,600, MWD = 2.394, 33.89 SCB/1000C by IR technique).
Example 34 Polymerization - Compound L
The polymerization was carried out as in Example 1 with the following reactor conditions: 400 ml of toluene, 5.0 ml of 1.0 M MAO, 0.322 mg of compound L (0.2 ml of a 16.1 mg in 10 ml of toluene solution), 80°C, 60 psi ethylene, 30 minutes. The run provided 15.5 g of polyethylene (MW = 174,300, MWD = 2.193).
Example 35 Polymerization - Compound A
The polymerization was carried out as in Example 1 with the following reactor contents: 250 ml of toluene, 150 ml of 1-hexene, 7.0 ml of 1.0 M MAO and 2.3 mg of compound A (2.0 ml of a 11.5 mg in 10 ml of toluene solution) at 50° C. The reactor was pressurized with ethylene (65 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 26.5 g of an ethylene-hexene copolymer was recovered (MW = 222,800, MWD = 3.373, 39.1 SCB/1000C by IR technique).
Example 36 Polymerization - Compound A
The polymerization was carried out as in Example 1 with the following reactor contents: 300 ml of toluene, 100 ml of 1-octene, 7.0 ml of 1.0 M MAO and 2.3 mg of compound A (2.0 ml of a 11.5 mg in 10 ml of toluene solution) at 50° C. The reactor was pressurized with ethylene (65 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 19.7 g of an ethylene-octene copolymer was recovered (MW = 548,600, MWD = 3.007,16.5 SCB/1000C by 13C NMR technique).
Example 37 Polymerization - Compound A
The polymerization was carried out as in Example 1 with the following reactor contents: 300 ml of toluene, 100 ml of 4-methyl-1-pentene, 7.0 ml of 1.0 M MAO and 2.3 mg of compound A (2.0 ml of a 11.5 mg in 10 ml of toluene solution) at 50° C. The reactor was pressurized with ethylene (65 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 15.1 g of an ethylene-4-methyl-1-pentene copolymer was recovered (MW, 611,800, MWD = 1.683, 1.8 mole determined by 13C NMR).
Example 38 Polymerization - Compound A
The polymerization was carried out as in Example 1 with the following reactor contents: 300 ml of toluene, 100 ml of a 2.2 M norbornene in toluene solution, 7.0 ml of 1.0 MAO and 2.3 mg of compound A (2.0 ml of a 11.5 mg in 10 ml of toluene solution) at 50° C. The reactor was pressurized with ethylene (65 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 12.3 g of an ethylene-norbornene copolymer was recovered (MW = 812,600, MWD = 1.711, 0.3 mole% determined by 13C NMR).
Example 39 Polymerization - Compound A
The polymerization was carried out as in Example 1 with the following reactor contents: 300 ml of toluene, 100 ml of cis-1,4-hexadiene, 7.0 ml of 1.0 M MAO and 2.3 mg of compound A (2.0 ml of a 11.5 mg in 10 ml of toluene solution) at 50° C. The reactor was pressurized with ethylene (65 psi), and the reaction was allowed to run for 30 minutes, followed by rapidly cooling and venting the system. After evaporation of the solvent, 13.6 g of an ethylene-cis-1 ,4-hexadiene copolymer was recovered (MW = 163,400, MWD = 2.388, 2.2 mole% determined by 13C NMR).
1 A process for olefin polymerization comprising polymerising ethylene and a monomer selected from C3-C20 a -olefin and/or a C5-C20 diolefin in the presence of a catalyst system comprising (A) a compound of the general formula: or wherein M is Zr, Hf or Ti;
(C5H5-y-xRx) is a cyclopentadienyl ring which is substituted with from zero to five groups R, "x" is 1, 2, 3, 4 or 5 denoting the degree of substitution, and each R is, independently, a radical selected from a group consisting of C1-C20 hydrocarbyl radicals, C1-C20 substituted hydrocarbyl radicals wherein one or more hydrogen atoms are replaced by a halogen atom, C1-C20 hydrocarbyl-substituted metalloid radicals wherein the metalloid is selected from the Group IV A of the Periodic Table of Elements and halogen radicals or (C5H5-y-xRx) is a cyclopentadienyl ring in which two adjacent R-groups are joined from C4-C20 ring to give a saturated or unsaturated polycyclic cyclopentadienyl ligand;
(JR'z-1-y) is a heteroatom ligand in which J is an element with a coordination number of three from Group V A or an element with a coordination number of two from Group Vl A of the Periodic Table of Elements, each R' is, independently, a radical selected from a group consisting of C1-C20 hydrocarbyl radicals, substituted C1-C20 hydrocarbyl radicals wherein one or more hydrogen atoms is replaced by a halogen atom, and "z" is the coordination number of the element J;
each Q or Q' is, independently any univalent anionic ligand or Q and Q' are a divalent anionic chelating agent; M' has the same meaning as M;
"y" is 0 or 1 when w is greater than 0; y is 1 when w is 0, when "y" is 1, B is covalent bridging group containing a Group IVA or V A element; and
2 A process according to claim 1 where the a-olefin is 1-butene, 1-hexene or 1-octene.
3 A process according to claim 1 or claim 2 in which the alumoxane is methylalumoxane having an average degree of digomerization of from 4 to 25.
4 A process according to any of the preceding claims in which the polymer obtained has an Mw/Mn value of below 4.
EP19940203507 1989-09-13 1990-09-10 Olefin polymerization catalysts Withdrawn EP0662484A3 (en)
US406945 1989-09-13
EP19900309899 EP0420436B2 (en) 1989-09-13 1990-09-10 Olefin polymerization catalysts
US533245 1995-09-25
EP90309899.4 Division 1990-09-10
EP19900309899 Division EP0420436B2 (en) 1989-09-13 1990-09-10 Olefin polymerization catalysts
EP0662484A2 true true EP0662484A2 (en) 1995-07-12
EP0662484A3 true EP0662484A3 (en) 1998-02-11
ID=27019705
EP19940203507 Withdrawn EP0662484A3 (en) 1989-09-13 1990-09-10 Olefin polymerization catalysts
EP19900309899 Expired - Lifetime EP0420436B2 (en) 1989-09-13 1990-09-10 Olefin polymerization catalysts
EP19940203508 Withdrawn EP0671404A3 (en) 1989-09-13 1990-09-13 Monocyclopentadienyl transition metal olefin polymerization catalysts
EP19940203509 Withdrawn EP0643066A3 (en) 1989-09-13 1990-09-13 Monocyclopentadienyl transition metal olefin polymerization catalysts
EP19900914596 Revoked EP0491842B1 (en) 1989-09-13 1990-09-13 Monocyclopentadienyl transition metal olefin polymerization catalysts
US (4) US5055438A (en)
EP (5) EP0662484A3 (en)
JP (2) JP2994746B2 (en)
KR (1) KR100195662B1 (en)
CA (2) CA2024899C (en)
DE (5) DE662484T1 (en)
DK (2) DK0420436T4 (en)
ES (2) ES2079332T1 (en)
FI (2) FI109705B (en)
WO (1) WO1991004257A1 (en)
WO2000039175A1 (en) * 1998-12-30 2000-07-06 Union Carbide Chemicals & Plastics Technology Corporation Method of reducing tube plugging using preactivated unsupported catalysts
WO2000052063A1 (en) * 1999-03-03 2000-09-08 Lg Chemical Co., Ltd. Metallocene compounds and their use for olefin polymerization
WO2006100004A1 (en) * 2005-03-24 2006-09-28 Basell Polyolefine Gmbh Monocyclopentadienyl complexes
DE69319690T2 (en) * 1992-10-30 1999-04-08 Enichem Spa Catalyst and process for the (co) polymerization of alpha-olefins
NL1001237C2 (en) * 1995-09-19 1997-03-20 Dsm Nv A copolymer of an olefinic monomer, and 1,2-polybutadiene.
EP1960411B1 (en) * 2005-12-14 2016-08-31 ExxonMobil Chemical Patents Inc. Halogen substituted metallocene compounds for olefin polymerization
RU2497826C1 (en) 2006-12-21 2013-11-10 ДАУ ГЛОБАЛ ТЕКНОЛОДЖИЗ ЭлЭлСи Phosphorus-sulfur fire-protective additives and polymeric systems, which contain them
JP5052125B2 (en) 2006-12-27 2012-10-17 日本ポリプロ株式会社 Polypropylene resin composition, molded article comprising the same, and a process for producing a molded article
DE102007057854A1 (en) * 2007-11-28 2009-06-04 Philipps-Universität Marburg Cyclopentadienylphosphazene complexes (CpPN complexes) of metals of the third and fourth group and the lanthanides
CN102844284A (en) * 2010-04-28 2012-12-26 尤尼威蒂恩技术有限责任公司 Synthesis of alkyl cyclopentadiene compounds
JP5636320B2 (en) 2011-03-29 2014-12-03 日本ポリプロ株式会社 Polypropylene for automotive members resin composition and an automotive exterior member
WO2013035764A1 (en) 2011-09-08 2013-03-14 日本ポリプロ株式会社 Fiber-reinforced polypropylene resin composition and molded article thereof
CN107721797A (en) 2011-12-19 2018-02-23 沙特基础工业公司 Method for preparing the metallocene complexes
US2952679A (en) * 1960-09-13 Cyanuricacro preparation
US2952697A (en) * 1958-10-07 1960-09-13 Ethyl Corp Cyclopentadienyl metal compounds
US7041841B1 (en) * 1989-09-13 2006-05-09 Exxonmobil Chemical Patents Inc. Process for producing crystalline poly-α-olefins with a monocyclopentadienyl transition metal catalyst system
CA2024899C (en) 2003-12-16 grant
DE69028057D1 (en) 1996-09-19 grant
EP0491842A1 (en) 1992-07-01 application
EP0643066A3 (en) 2004-01-07 application
JP2994746B2 (en) 1999-12-27 grant
DK0420436T4 (en) 2000-11-27 grant
EP0420436B2 (en) 2000-07-19 grant
US20060178491A1 (en) 2006-08-10 application
EP0420436A1 (en) 1991-04-03 application
FI109705B1 (en) grant
DE69030442T2 (en) 1997-08-07 grant
ES2091801T3 (en) 1996-11-16 grant
DK0420436T3 (en) 1996-12-02 grant
FI109705B (en) 2002-09-30 application
CA2065745A1 (en) 1991-03-14 application
DE69028057T3 (en) 2001-01-25 grant
FI921077A0 (en) 1992-03-12 application
JPH05505593A (en) 1993-08-19 application
EP0671404A3 (en) 2004-01-07 application
EP0662484A3 (en) 1998-02-11 application
EP0491842B1 (en) 1997-04-09 grant
KR100195662B1 (en) 1999-06-15 grant
EP0643066A2 (en) 1995-03-15 application
WO1991004257A1 (en) 1991-04-04 application
FI113538B (en) 2004-05-14 application
DE662484T1 (en) 1996-06-27 grant
JPH03188092A (en) 1991-08-16 application
DE420436T1 (en) 1996-02-15 grant
US7569646B1 (en) 2009-08-04 grant
EP0420436B1 (en) 1996-08-14 grant
DE69028057T2 (en) 1997-01-16 grant
US7205364B1 (en) 2007-04-17 grant
CA2024899A1 (en) 1991-03-14 application
ES2091801T5 (en) 2000-12-01 grant
CA2065745C (en) 2002-01-01 grant
US5055438A (en) 1991-10-08 grant
ES2079332T1 (en) 1996-01-16 application
EP0671404A2 (en) 1995-09-13 application
FI904506A0 (en) 1990-09-12 application
DK0491842T3 (en) 1997-10-27 grant
FI904506D0 (en) grant
DE69030442D1 (en) 1997-05-15 grant
FI113538B1 (en) grant
FI921077D0 (en) grant
1995-07-12 AC Divisional application (art. 76) of:
Ref document number: 420436
1995-12-01 TCNL Nl: translation of patent claims filed
Ref document number: 2079332
1996-06-27 DET De: translation of patent claims