Group-III nitride based laser diode and method for fabricating same - Patent # 8050304 - PatentGenius
Group-III nitride based laser diode and method for fabricating same
8050304 Group-III nitride based laser diode and method for fabricating same
Inventor: Denbaars, et al.
Application: 12/880,392
Inventors: Denbaars; Steven (Goleta, CA)
Nakamura; Shuji (Santa Barbara, CA)
Hansen; Monica (Santa Barbara, CA)
Assignee: Cree, Inc. (Goleta, CA)
U.S. Class: 372/45.011; 372/43.01; 372/45.012; 428/25; 428/670
Field Of Search: 372/45.011; 372/45.012; 372/43.01; 438/25; 438/474; 438/670
International Class: H01S 5/00; H04B 10/00
Foreign Patent Documents: 0936682; 1349202; 1653255; 1681509; 2586844; 2759188; 2814220; WO 9856043; WO 0211212; 03044870; WO 03/080763; WO 03/080763; WO 2005104247; WO 2007005844
Other References: Invitation to Submit Applicant's Opinion (Summary) from Japanese Patent Application No. 2003-529535, Appeal Filing Number: 2009-007421 datedDec. 7, 2010. cited by other.
Examiner's Report to the Board (Summary) from Japanese Patent Application No. 2003-529535, Appeal Filing Number: 2009-007421 dated Dec. 7, 2010. cited by other.
European search report for Application No. 08160129.6-2222, Dated. Dec. 15, 2009. cited by other.
U.S. Appl. No. 11/613,692, filed Dec. 20, 2006. cited by other.
U.S. Appl. No. 11/614,180, filed Dec. 21, 2006. cited by other.
U.S. Appl. No. 11/624,811, filed Jan. 19, 2007. cited by other.
U.S. Appl. No. 11/743,754, filed May 3, 2007. cited by other.
U.S. Appl. No. 11/751,982, filed May 22, 2007. cited by other.
U.S. Appl. No. 11/753,103, filed May 24, 2007. cited by other.
U.S. Appl. No. 11/751,990, filed May 22, 2007. cited by other.
U.S. Appl. No. 11/755,153, filed May 30, 2007. cited by other.
U.S. Appl. No. 11/856,421, filed Sep. 17, 2007. cited by other.
U.S. Appl. No. 11/859,048, filed Sep. 21, 2007. cited by other.
U.S. Appl. No. 11/939,047, filed Nov. 13, 2007. cited by other.
U.S. Appl. No. 11/936,163, filed Nov. 7, 2007. cited by other.
U.S. Appl. No. 11/843,243, filed Aug. 22, 2007. cited by other.
U.S. Appl. No. 11/939,052, filed Nov. 13, 2007. cited by other.
U.S. Appl. No. 11/736,799, filed Apr. 18, 2007. cited by other.
U.S. Appl. No. 11/877,038, filed Oct. 23, 2007. cited by other.
U.S. Appl. No. 11/870,679, filed Oct. 11, 2007. cited by other.
U.S. Appl. No. 11/948,041, filed Nov. 30, 2007. cited by other.
U.S. Appl. No. 11/949,222, filed Dec. 3, 2007. cited by other.
U.S. Appl. No. 12/174,053, filed Jul. 16, 2008. cited by other.
U.S. Appl. No. 12/002,429, filed Dec. 4, 2007. cited by other.
U.S. Appl. No. 12/045,729, filed Mar. 11, 2008. cited by other.
U.S. Appl. No. 11/818,818, filed Jun. 14, 2007. cited by other.
European Search Report from related European Application No. 07254498.4, received on Feb. 11, 2010. cited by other.
Official Communication from the EPO regarding European Application 08253301.9, dated: Nov. 17, 2009. cited by other.
Second Office Action from Chinese Application No. 200710142217.6, dated: Nov. 6, 2009. cited by other.
Second Office Action from People's Republic of China, re China Application No. 200480027969.2, dated; Jul. 4, 2008. cited by other.
Canadian Patent Application No. 2,454,310, Office Action dated: Feb. 9, 2010. cited by other.
Notice of First Office Action from China Patent Application No. 200710142217.6, dated: Jun. 22, 2009. cited by other.
International Search Report for PCT/US2008/004453, Date: Sep. 9, 2008. cited by other.
Written Opinion for PCT/US2008/004453, Date: Sep. 9, 2008. cited by other.
Kim J K et al. "Strongly Enhanced Phosphor Efficiency in GaInN White Light-Emitting Diodes Using Remote Phosphor Configuration and Diffuse Reflector Cup", Japanese Journal of Applied Physics, Japan Society of Applied Physics, Tokyo, JP, vol. 44, No.20-23, Jan. 1, 2005, XP-001236966. cited by other.
PCT Search Report and Written Opinion PCT/US2007/086237, date: May 8, 2008 in related application. cited by other.
PCT Search Report and Written Opinion PCT/US2007/12403, Date: Aug. 6, 2008. cited by other.
PCT Search Report and Written Opinion PCT/US2007/086242, Date: Mar. 4, 2008. cited by other.
Asbeck et al."Enhancement of Base Conductivity Via the Piezoelectric Effect in AlGaN/GaN HBTs", Solid State Electronics, Elsevier Science Pub. Barking GB, vol. 44, No. 2, Feb. 1, 2000 pp. 211-219, XP004186190. cited by other.
Johnson et al."New UV Light Emitter Based on AlGaN Heterostructures with Graded Electron and Hole Injectors", Materials Research Society Symposium--Proceedings 2002 Materials Research Society US, vol. 743, 2002, pp. 481-486. cited by other.
Simon et al. "Polarization-Induced 3-Dimensional Electron Slabs in Graded AlGaN Layers", Materials Research Society Symposium Proceedings 2006 Materials Research Society US, vol. 892, Nov. 28, 2005, pp. 417-422. cited by other.
Official Notice of Final Decision of Rejection re Japanese Patent Appl. No. 2003-529535, Dated: Jan. 6, 2009. cited by other.
European Communication from European Appl. 02 798 906.0-1235, Dated Feb. 6, 2009. cited by other.
U.S. Copending U.S. Appl. No. 11/443,741, filed Jun. 14, 2007. cited by other.
U.S. Copending U.S. Appl. No. 11/685,761, filed Mar. 13, 2007. cited by other.
U.S. Copending U.S. Appl. No. 11/939,059, filed Nov. 13, 2007. cited by other.
Notice Requesting Submission of Opinion re related Korean Application No. 10-2004-7001033, dated: Mar. 9, 2009. cited by other.
Sakai et al., "Experimental Investigation of Dependence of Electrical Characteristics on Device Parameters in Trench MOS Barrier Shottky Diodes", Proceedings of 1998 International Symposium on Power Semiconductor Devices & ICs, Kyoto, pp. 293-296,Jun. 1998. cited by other.
Zhang AP et al, "Comparison of GAN P-I-N and Schottky Rectifier Performance" IEEE Transactions on Electron Devices, IEEE Inc. New York, US, vol. 48, No. 3, pp. 407-411, Mar. 2001. cited by other.
European Search Report, Feb. 24, 2009, re related European Application No. EP 08253301. cited by other.
Office Action from related U.S. Appl. No. 11/600,617, dated: Feb. 14, 2008. cited by other.
Response to Office Action from related U.S. Appl. No. 11/600,617, dated; Mar. 14, 2008. cited by other.
Office Action from related U.S. Appl. No. 11/600,617, dated: Jun. 11, 2008. cited by other.
Response to Office Action from related U.S. Appl. No. 11/600,617, dated; Sep. 12, 2008. cited by other.
Office Action from related U.S. Appl. No. 11/600,617, dated: Dec. 19, 2008. cited by other.
Response to Office Action from related U.S. Appl. No. 11/600,617, dated; Mar. 18, 2009. cited by other.
Office Action from related U.S. Appl. No. 11/600,617, dated: Jul. 8, 2009. cited by other.
Response to Office Action from related U.S. Appl. No. 11/600,617, dated; Sep. 2, 2009. cited by other.
Office Action from related U.S. Appl. No. 11/600,617, dated: Oct. 20, 2009. cited by other.
Response to Office Action from related U.S. Appl. No. 11/600,617, dated; Nov. 3, 2009. cited by other.
Office Action from related U.S. Appl. No. 11/600,617, dated: Dec. 22, 2009. cited by other.
Response to Office Action from related U.S. Appl. No. 11/600,617, dated; Mar. 18, 2010. cited by other.
Office Action from U.S. Appl. No. 11/600,618, dated: Feb. 4, 2010. cited by other.
Notice of Allowance from related U.S. Appl. No. 11/600,617, dated: Jun. 11, 2010. cited by other.
Abstract: A laser diode comprising a first separate confinement heterostructure and an active region on the first separate confinement heterostructure. A second separate confinement heterostructure is on the active region and one or more epitaxial layers is on the second separate confinement heterostructure. A ridge is formed in the epitaxial layers with a first mesa around the ridge. The first mesa is 0.1 to 0.2 microns above the second confinement heterostructure.
1. A method for fabricating a laser diode, comprising; providing a growth wafer; growing a first guiding layer on said growth wafer; growing an active region on said first guidinglayer; growing a second guiding layer on said active region; growing one or more epitaxial layers on said second guiding layer; and etching a ridge and first mesa in said epitaxial layers, said first mesa being 0.1 to 0.2 microns above said secondguiding layer.
2. The method of claim 1, further comprising growing a first waveguiding element between said growth wafer and said first guiding layer, and wherein said one or more epitaxial layers comprises a second guiding element.
3. The method of claim 1, further comprising growing an electron blocking layer between said active region and said second guiding layer.
4. The method of claim 2, further comprising growing a n-contact layer between said first waveguiding element and a substrate, and a p-contact layer on said second waveguiding element.
5. The method of claim 4, wherein said ridge etching is through said p-contact layer and partially through said second waveguiding element.
6. The method of claim 4, further comprising forming a p-contact on said ridge and in electrical contact with said p-contact layer.
7. The method of claim 6, wherein said p-contact has a setback from the ends of said ridge.
8. The method of claim 7, wherein said substrate comprises an off-angle cut substrate.
9. The method of claim 1, further comprising cleaving to form facets, said facets cleaned by a plasma cleaner following cleaving.
10. The method of claim 6, wherein said p-contact is formed using lithography and liftoff, said laser diode cleaned by a plasma cleaner following said lithography and lift-off and said etching.
11. The method of claim 6, further comprising annealing said p-contact in a nitrogen gas only.
12. The method of claim 1, further comprising mounting said laser diode in a can using AuSn solder.
13. The method of claim 12, further comprising cleaning said by a plasma cleaner before and after said mounting of said laser diode, and further comprising sealing said can.
14. The method of claim 13, wherein said can is filled with an inert gas.
A laser is a device that produces a beam of coherent light as a result of stimulated emission. Light beams produced by lasers can have high energy because of their single wavelength, frequency, and coherence. A number of materials are capableof producing a lasing effect and include certain high-purity crystals (such as ruby), semiconductors, certain types of glass, certain gasses including carbon dioxide, helium, argon and neon, and certain plasmas.
More recently there has been increased interest in lasers made of semiconductor materials. These devices typically have a smaller size, lower cost, and have other related advantages typically associated with semiconductor devices. Semiconductor lasers are similar to other lasers in that the emitted radiation has spacial and temporal coherence, and like other lasers, semiconductor lasers produce a beam of light that is highly monochromatic (i.e., of narrow bandwidth) and is highlydirectional. Overall, semiconductor lasers provide very efficient systems that are easily modulated by modulating the current directed across the devices. Additionally, because semiconductor lasers have very short photon lifetimes, they can be used toproduce high-frequency modulation.
One type of semiconductor laser diode is referred to as an edge emitting laser where the stimulated emission is from the side surface or edge of the laser diode. These devices typically have epitaxial layers in the form of waveguiding orreflective elements (cladding layers) with a light generating active region between the reflective elements. Additional layers can be included between the reflective elements to form a laser cavity. The edges of the laser diode can be cleaved duringmanufacturing to form edge reflective surfaces or facets. A total reflectivity (TR) material can cover one edge, and an anti reflectivity (AR) material can cover the opposite edge. Light from the active region is reflected between the edges and withinthe cavity by the reflective elements, with stimulated emission emitting from the edge with the AR material. After application of the TR and AR materials, the individual laser diodes can be separated.
A known characteristic of laser diodes (and light emitting diodes) is that the frequency of radiation that can be produced by the particular laser diode is related to the bandgap of the particular semiconductor material. Smaller bandgapsproduce lower energy, shorter wavelength photons, while wider bandgaps produce higher energy, shorter wavelength photons. One semiconductor material commonly used for lasers is indium gallium aluminum phosphide (InGaAlP), which has a bandgap that isgenerally dependent upon the mole of atomic fraction of each element present. This material, regardless of the different element atomic fraction, produces only light in the red portion of the visible spectrum, i.e., about 600 to 700 nanometers (nm).
Laser diodes that produce shorter wavelengths not only produce different colors of radiation, but offer other advantages. For example, laser diodes, and in particular edge emitting laser diodes, can be used with optical storage and memorydevices (e.g. compact disks (CD) digital video disks (DVD), high definition (HD) DVDs, and Blue Ray DVDs). Their shorter wavelength enables the storage and memory devices to hold proportionally more information. For example, an optical storage devicestoring information using blue light can hold approximately 32 times the amount of information as one using red light, using the same storage space. There are also applications for shorter wavelength laser in medical systems and projection displays. This has generated interest in Group-III nitride material for use in laser diodes, and in particular gallium nitride (GaN). GaN can produce light in the blue and ultra violet (UV) frequency spectrums because of its relatively high bandgap (3.36 eV atroom temperature). This interest has resulted in developments related to the structure and fabrication of Group-III nitride based laser diodes [For example see U.S. Pat. Nos. 5,592,501 and 5,838,706 to Edmond et al].
Group-III nitride laser diodes can require relatively high threshold currents and voltages to reach laser radiation because of optical and electrical inefficiencies. These elevated current and voltage levels can result in heat being generatedduring laser diode operation. In certain applications, laser diodes are driven by a pulsed signal that results in pulsed laser light being emitted from the laser diode. The heat generated within the laser diode typically does not present a problemduring pulsed laser diode operation because the laser diode has the opportunity to cool during the lows of the signal. For other important applications, however, it can be desirable to drive the laser diode with a continuous wave (CW). CW operation isparticularly applicable to operation with optical storage devices that can require a continuous light source for data storage and retrieval. Driving many current Group-III based laser diodes with a CW having the threshold current and voltage necessaryfor laser emission can result in heating that can damage or destroy the laser diode. Heat sinks or other cooling methods/devices can be employed to reduce operating heat within these laser diodes, but the methods/devices can increase the cost andcomplexity of the devices and can require additional space.
The present invention is generally directed to laser diode epitaxial structure having improved operating characteristics and improved reliability, and methods for fabricating the epitaxial structures. The improved operating characteristicsinclude operation as reduced current and voltage thresholds, which allow for efficient operation at reduced temperature.
One embodiment of a laser diode according to the present invention comprises a first separate confinement heterostructure and an active region on the first separate confinement heterostructure. A second separate confinement heterostructure ison the active region and one or more epitaxial layers is on the second separate confinement heterostructure. A ridge is formed in the epitaxial layers with a first mesa around the ridge. The first mesa is 0.1 to 0.2 microns above the second confinementheterostructure.
One method for fabricating a laser diode according to the present invention comprises providing a growth wafer and growing a first guiding layer on the growth wafer. An active region is grown on the first guiding layer and a second guidinglayer is grown on the active region. One or more epitaxial layers are grown on the second guiding layer. A ridge is etched and a first mesa is formed on the epitaxial layers, the first mesa being 0.1 to 0.2 microns above the second guiding layer.
The present invention provides high reliability, high output power nitride-based laser diode characterized by reduced threshold current densities and reduced threshold voltages. The present invention is particularly adapted for laser diodeshaving a ridge for optical and electrical confinement, with the ridge being etched to level in the laser diode structure that allows for reduced threshold current operation while at the same time allowing for reliable lifetime operation. The presentinvention is also directed to additional laser diode structural and manufacturing improvements that further enhance laser diode operation.
The present invention is described herein with reference to certain embodiments but it is understood that the invention can be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. It isalso understood that when an element or component is referred to as being "on", "connected to" or "coupled to" another layer, element or component, it can be directly on, connected to or coupled to the other layer element or component, or interveningelements may also be present. Furthermore, relative terms such as "inner", "outer", "upper", "above", "lower", "beneath", and "below", and similar terms, may be used herein to describe a relationship of one component or element to another. It isunderstood that these terms are intended to encompass different orientations of the device in addition to the orientation depicted in the figures.
Although the terms first, second, etc. may be used herein to describe various layers, elements, components and/or sections, these layers, elements, components, and/or sections should not be limited by these terms. These terms are only used todistinguish one layer, element, component, or section from another. Thus, a first layer, element, component, or section discussed below could be termed a second element, component, or section without departing from the teachings of the presentinvention.
Embodiments of the invention are described herein with reference to cross-sectional view illustrations that are schematic illustrations of idealized embodiments of the invention. It is understood that many of the layers will have differentrelative thicknesses compared to those shown and that the laser diodes will have different shapes. Further, variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances are expected. Embodiments of the invention should not be construed as limited to the particular shapes of the regions illustrated herein but are to include deviations in shapes that result, for example, from manufacturing. A region illustrated or described as squareor rectangular will typically have rounded or curved features due to normal manufacturing tolerances. Thus, the regions illustrated in the figures are schematic in nature and their shapes are not intended to illustrate the precise shape of a region of adevice and are not intended to limit the scope of the invention.
Embodiments of the present invention may be particularly well suited for use in nitride-based devices such as Group III-nitride based laser diodes. As used herein, the term "Group III nitride" refers to those semiconducting compounds formedbetween nitrogen and the elements in Group III of the periodic table, usually aluminum (Al), gallium (Ga), and/or indium (In). The term also refers to ternary and quaternary compounds, such as AlGaN and AlInGaN. As well understood by those in this art,the Group III elements can combine with nitrogen to form binary (e.g., GaN), ternary (e.g., AlGaN and AlInN), and quaternary (e.g., AlInGaN) compounds. These compounds all have empirical formulas in which one mole of nitrogen is combined with a total ofone mole of the Group III elements. Accordingly, formulas such as Al.sub.xGa.sub.1-xN, where 0.times.1, are often used to describe them.
FIG. 1, shows one embodiment of a laser diode 10 according to the present invention at an intermediate fabrication stage. Although a single laser diode 10 is shown, it is understood that many laser diodes are typically fabricated on a singlesubstrate wafer, with the devices then being separated into individual devices using known processes, such as facet cleaving to form die arrays and die separation using scribe and break processes. The layers of laser diodes according to the presentinvention can be formed or grown on a substrate wafer using known fabrication processes such as growth in a reactor by metalorganic chemical vapor deposition (MOCVD).
The present invention can be utilized with many different laser diode structures arranged in different ways, with the laser diode 10 being only one example of such a laser diode structure. The laser diode 10 comprises a substrate 12 that can bemade of many different materials such as sapphire, silicon carbide, or GaN. The preferred laser diode 10 is formed on a free-standing GaN substrate lateral epitaxial overgrown (LEO) pendeo GaN, or a substrate with a lateral epitaxial overgrowth layer onthe a substrate such as silicon or silicon carbide. Alternatively, the substrate can be GaN grown by hybrid vapor-phase epitaxy (HVPE).
Lower threading dislocation densities in GaN based epitaxial structures can enhance the operating characteristics and if the initial epitaxial layers are grown with low threading dislocation densities it will spread to the layers that follow. It is preferable that the threading dislocation densities be less than approximately 5.times.10.sup.5 cm.sup.-2 in the laser diode's GaN based epitaxial layers, which can reduce threshold current. This can also reduce dopant (Mg) diffusion to the activeregion, which can improve reliability. Different fabrication processes can be used according to the present invention to achieve low dislocation densities such as pendeo or lateral epitaxy overgrowth of GaN. This can be done as one of the first layersin the laser diode. In one embodiment, a GaN layer is formed on a substrate, such as sapphire. Pillars with top surface mesas are etched in the GaN layer and partially into the sapphire substrate. GaN is grown over the pillars and substrate, and GaNgrows on the mesas of the pillars as well as laterally outward. The GaN grown on the mesas has substantially the same dislocation density as the pillar below, but the threading dislocation from the pillar does not propagate to the laterally grown GaN. The laterally grown GaN grows together between adjacent pillars to form a reduced dislocation density surface. This reduced dislocation will spread to subsequent growth layers.
Off-angle substrates for GaN growth can improve the surface morphology and can provide for smooth growth surfaces for laser diode epitaxial layers. This in turn provides a more efficient active region that operates at reduced threshold currentand provides improved reliability. FIG. 2 illustrates one embodiment of an off-angle cut substrate 40 according to the present invention and it is understood that for ease of understanding, the substrate 40 and its features are not to scale. When thesubstrate 40 is cut with off-angle 42, the crystalline nature of the substrate results in the formation of steps 44 along the cut surface with step edges 46 between the steps 44. If the off-angle 44 of the cut can be controlled, a consistent andrepeatable step surface can be formed. Atoms from the growth gas attach to the growing surface in a low energy configuration, and for substrate 40 when the growth atoms 48 encounter the surface of the step edge 46 they attach at the step edge 46 as alow energy configuration. The film or epitaxial layer grow smoothly in a step flow mode growth by the atoms 48 first attaching to the step edges 46 and then terrace growing across the surface of each step 44. This in turn provides for a smootherinterface for the layers grown on the substrate 40, including the quantum well growth. The off-angle 44 of the substrate 40 can be at different angles with a suitable range of angles being between 0.1 to 5.degree., and a preferred off-angle being 0.5 to1.degree..
An n-type contact layer 14 is grown on the substrate and comprises a semiconductor material suitable for spreading current from an n-contact to the active region. Many different materials can be used for the n-type contact layer, with apreferred material being n-type doped GaN, with a suitable dopant being silicon (Si). As further described below, for laser diodes that are formed on conductive substrates, the n-contact can be formed on the substrate 12 and currents from an electricalsignal applied to the n-contact conducts through the substrate 12 and n-contact layer 14, to the active region of the laser diode 10. For laser diodes formed on non-conductive substrates or substrates that do not efficiently spread current, a lateralgeometry can be used for contacting the device. In these embodiments the laser diode 10 can be etched to form a mesa in the n-type contact layer 14 and the n-contact is deposited on the contact layer mesa. Current spreads from the contact, through then-type contact layer 14 and to the laser diode's active region.
It is also understood that laser diodes formed on a conductive substrate can effectively spread current without the n-type contact layer 14, and that these embodiments can be arranged without the n-type contact layer 14. It is furtherunderstood that other embodiments of the present invention can have the substrate removed, and contact can be made directly to the epitaxial layers.
A compliance layer 16 can be included on the n-type layer to help reduce the strain between the n-contact layer 14 and subsequent epitaxial layers of the laser diode 10. The compliance layer can be made of many different materials, with apreferred compliance layer being made of an n-type InGaN with Si doping. A waveguiding element 18 is included on the compliance layer 16 with a preferred waveguiding element being a strained layer superlattice (SLS) structure comprising layers ofsemiconductor material. Many different materials can be used for the n-type SLS layers with preferred materials being AlGaN/GaN with Si-doping of the GaN layer(s) only.
An n-type guiding layer 20 is formed on the n-type SLS 18 with the guiding layer also referred to as a separate confinement heterostructure (SCH). The n-type SCH 20 serves as part of the light path to the edges of the laser diode 10 andultimately out the emission edge of the laser diode 10. The light from the active region traveling toward the waveguiding elements (n-type SLS 20 and the p-type SLS described below) is reflected, and light traveling toward the laser diode's edges isreflected until stimulated emission is out one of the edges. The n-type SCH layer 20 and p-type SCH layer serve as the primary reflection cavity for this reflected light. The n-type SCH 22 can comprise many different materials with a preferred materialbeing n-type doped GaN grown with Si doping.
The active region 22 is grown on the n-type SCH layer 20 and the active region can comprise different layers arranged in different ways, with a preferred active region comprising a MQW region that can have different numbers of quantum wells andbarrier layers. In one embodiment according to the present invention, MQW active region 22 comprises three quantum wells and associated barrier layers made of InGaN.
The laser diode 10 further comprises an electron blocking layer 24 formed on the MQW active region 22. The blocking layer 24 comprises a material that blocks electrons from passing from the MOW active region 22 into the p-type SCH layer(described below), but lets holes pass through to form the p-type SCH layer to the MQW active region 22. By blocking electrons, the blocking layer encourages recombination in the MQW active region 22. The blocking layer can be made of many differentmaterials, with a suitable material being p-type AlGaN with Mg doping. A p-type guiding layer or SCH 26 is formed on the electron blocking layer 24. The p-type SCH 26 can be made of many different materials with a suitable material being p-type GaNwith Mg doping.
A second waveguiding element 28 is included on the p-type SCH layer 26, with the waveguiding element 28 preferably comprising a p-type SLS made of AlGaN/GaN layers with Mg doping the GaN layer only. Finally, a p-type contact layer 30 isincluded on the p-type SLS. The contact layer can also comprise many different materials, with a preferred material being p-type GaN with Mg-doping.
The laser diode 10 as shown in FIG. 1 can then have a p-contact and n-contact deposited on it using known techniques such as photolithography and liftoff techniques. The p-contact is typically deposited on the p-type contact layer 30 and then-contact can be on either the substrate (for conductive substrates) or on the n-contact mesa as further described below. More commonly, however, a ridge etched from the laser diodes top surface. The ridge provides electrical and optical confinementand index-guiding for the particular wavelength of light generated by the laser diode's active region. This in turn can allow for operation at lower threshold currents and voltages. The ridge can be formed using known mask and etching processes with asuitable etching process being plasma reactive ion etching (RIE). The p- and n-contacts can be made of many different materials such as gold (Au), nickel (Ni), platinum (Pt), Al, or combinations thereof.
FIG. 3 shows the laser diode 10 at a subsequent fabrication step having a ridge 32 etched from its top surface with the ridge arranged to provide optical and electrical confinement, which can result in lower threshold and current operation. Theridge 32 can have many different widths with some ridges being 2 .mu.m or less wide, and preferably in the range of 1.7 to 2 .mu.m. The etching of the ridge 32 can be to different depths in the laser diode 10, with a preferred depth according to thepresent invention being through the p-contact layer 30 and a portion of the p-type SLS 28. In one embodiment, the ridge 32 is etched through the p-type SLS 28 until the etch reaches 1 to 2 .mu.m (microns) above the p-type SCH 26.
Referring now to the graph 50 in FIG. 4 etching into closer or into the p-type SCH can result in lower threshold current operation, but can also result in shorter lifetimes. The graph 50 shows the threshold current operation for a laser diodeover time, with the laser diode having a ridge. The first plot 52 shows a threshold current operation for a laser diode according to the present invention having a ridge etched to 1-2 .mu.m from the p-type SCH. As shown, the threshold current remainsrelatively constant over time. The second line 54 shows the threshold current operation for a laser diode with the ridge etched into the p-type SCH. The threshold current at the beginning of operation is lower than that of line 52, but the reliabilityof the laser diode is negatively impacted by this etch depth. A failure point 56 is reached where the threshold current increases dramatically and laser diode fails to operate.
Referring back to FIG. 3, the laser diode 10 also comprises a p-contact (ohmic metal) 34 on the top surface of the ridge 32, which is the p-contact layer 32. An n-contact (ohmic metal) 36 can also be included on the substrate 12 for thoseembodiments having a conductive substrate. The p- and n-contacts 34, 36 can be made of many different materials, with preferred p-contacts being made of platinum (Pt), gold (Au), nickel (Ni), or combinations thereof, and preferred n-contacts being madeof titanium (Ti), Al, Au, Ni, or combinations thereof. The p- and n-contacts can also be deposited using know methods.
FIG. 5 shows another embodiment of a laser diode 60 according to the present invention having the same or similar layers as those shown in FIGS. 1 and 3 and described above. For those same and similar layers, the same reference numbers are usedwith the understanding that the description of those layers above applies to laser diode 60. The laser diode 60 has a non-conductive substrate 62 and for electrical contact to be made to the n-contact layer 64, a contact n-mesa 66 is formed by etchingthe layers above the n-contact layer 64. An n-contact 68 is deposited on the mesa, and when a bias is applied across the p- and n-contacts 34, 68 current from the n-contact 68 spreads into the n-contact layer 64 and to the active region 22. The ridge32 for laser diode 60 can have the same etch depth (1-2 .mu.m) to provide low voltage and threshold current operation.
Laser diodes according to the present invention can have other features that enhance efficiency and reliability. Referring to FIG. 5, when the ridge 32 is etched, a p-mesa 70 is formed on the sides of the ridge 32. The p-mesa 70 can havedifferent widths, with a width being 100 .mu.m or more. Narrower p-mesas can result in poor emission uniformity.
Following deposition of the p-contact 34, and insulating (dielectric) layer 72 can be deposited on the p-mesa 70 and exposed surfaces of the ridge 32. A bond pad 74 can then be deposited over at least part of the insulating layer 72 and incontact with the p-contact 34. The bond pad can be made of many different materials and can have many different thicknesses, with the preferred bond pad made from Au and having a minimum thickness of approximately 0.5 .mu.m, with a preferable thicknessbeing in the range of 1-2 .mu.m. A wire bond 76 can be coupled to the bond pad 74 for applying an electrical signal to the bond pad and in turn to the p-contact 34. According to the present invention, the wire bond 76 should be located off of ridge 32and preferably on the wider portion of the p-mesa 70. This location helps minimize damage to the ridge 32 during bonding of the wire bond 76.
FIG. 6 shows a top view of a laser diode 90 (without insulating layer, bond pad or wire bond) according to the present invention, having a ridge 92, p-mesa 94, n-mesa 96, p-contact 98, and n-contact 100, all of which are arranged similar tocorresponding features in laser diode 10 and 60 described above and shown in FIGS. 3 and 5. The individual laser diodes undergo a cleaving to form the laser diodes on the wafer into rows of diode arrays, with the cleaving forming the edge facets onopposite sides of the laser diode. The ridge 92, p- and n-mesas 94,96, p-contact 98, and n-contact 100, can all be formed prior to cleaving. According to the present invention, however, the p-contact 98 should not run completely along the ridge 92 whenformed on the ridge 92. By instead providing a setback 102 the danger of p-contact 98 peel-off during cleaving and operation is reduced. In one embodiment according to the present invention, the p-contact 98 has a setback 102 that is in the range ofapproximately 5-10 .mu.m, although other setback lengths can also be used.
In another embodiment the p-contact is a combination of Ni and Au, and because light does not pass through the p-contact, it does not need to be transparent. According to the present invention annealing of the completed laser structure iscompleted in a nitrogen gas only to provide good ohmic contact. The p-contact does not need to be oxidized during annealing to be made transparent, so oxidizing gas (oxygen) is not needed as part of the annealing gas. Different anneal time frames andtemperatures can be used, with the preferred annealing process taking approximately 10 minutes at a temperature range of 600-700.degree. C., with a preferred temperature being approximately 650.degree. C.
To further enhance operation of laser diodes according to the present invention, they should be cleaned with plasma cleaner or asher descum ("plasma cleaner") during fabrication. The plasma cleaner can comprise different compounds, with apreferred compound comprising an O.sub.2 plasma cleaning process. The plasma cleaning process can be performed in commercially available systems such as the Technics Model PE-IIA Plasma Etching System or SPI Plasma-Etch II Plasma Etcher, Cleaner andAsher. The asher descum should be used on the facets after cleaving and prior to high reflectivity (HR) and anti-reflectivity (AR) coating of the facets. The plasma cleaning should also be used following photolithography and wet etch steps such asfollowing etching of the ridge or n-type mesa or photolithography for formation of the n-contact or pad metal, all which are described above.
The plasma cleaning should also be used when mounting the laser diode in commercially available packaging or can. The can should be cleaned with a plasma cleaner and the laser diode can then be mounted in the can. The laser diode can be bondedwith AuSn solder or similar material. After mounting the can should again be subjected to plasma cleaning, then filled with an inert gas (N.sub.2, argon, etc.) and then hermitically sealed. This cleaning process reduces the contaminants that can remainafter mounting of the laser diode and sealing of the can.
Although the present invention has been described in considerable detail with reference to certain preferred configurations thereof, other versions are possible. Therefore, the spirit and scope of the appended claims should not be limited totheir preferred versions contained therein.
Encryption device and decryption device
Ustilago trichophora mycoherbicidal compositions and methods of use
Fibrous nonwoven web surge layer for personal care absorbent articles and the like
Method and apparatus for effecting selective ablation of a coating from a substrate, and controlling the wall angle of coating edge portions
Proteins for control of nematodes in plants
Methods and devices for stabilizing tissue
Plants and seeds of hybrid corn variety CH020602