Matched Legal Cases: ['§119', 'Application No. 60', 'Application No. 200780024560', 'application No. 2007', 'Application No. 200780024560', 'Application No. 200780024560', 'Application No. 096116533', 'Application No. 2007', 'application No. 2009', 'Application No. 2009', 'application No. 2007', 'Application No. 200780024560', 'Application No. 2009', 'Application No. 2007', 'Application No. 12178957', 'Application No. 07', 'Application No. 200780024560', 'Application No. 2009', 'Application No. 2009']

US8945287B2 - Active particle-enhanced membrane and methods for making and using the same - Google Patents
US8945287B2
US8945287B2 US11801647 US80164707A US8945287B2 US 8945287 B2 US8945287 B2 US 8945287B2 US 11801647 US11801647 US 11801647 US 80164707 A US80164707 A US 80164707A US 8945287 B2 US8945287 B2 US 8945287B2
US11801647
US20070264203A1 (en )
The present disclosure relates to active particle-enhanced membrane and methods for making and using the same. In some embodiments, a breathable membrane includes a base material solution and active particles. The active particles incorporated in the membrane may improve or add various desirable properties to the membrane, such as for example, the moisture vapor transport capability, the odor adsorbance, the anti-static properties, or the stealth properties of the membrane. In some embodiments, the base material may exhibit water-proof properties when converted into non-solution state, and thereby result in a water-proof membrane. In some embodiments, the active particles may be protected from losing activity before, during, or after (or any combination thereof) the process of producing the membrane. The membrane may be applied to a substrate, or may be used independent of a substrate.
This application claims the benefit under 35 U.S.C. §119(e) of U.S. Provisional Application No. 60/799,426 filed May 9, 2006, which is hereby incorporated herein by reference in its entirety.
Materials may be used for their various properties. For example, materials, such as a polyurethane, polyacrylic, 1,3 propaneiol terephthalte (DuPont 3GT™ or DuPont Sorona™), and polyactide made from lactic acid (DOW Cargill Ingeo™) films, may be used for their water-proof and breathable properties. These materials provide moisture vapor transfer while preventing penetration of liquid. Such materials may be used, for example, in apparel (e.g., rain gear, jackets, gloves, boots, and pants). It is worth noting that a water-proof breathable membrane is different from a water-resistant breathable membrane. Under standard atmospheric pressure, a water-proof breathable membrane does not allow liquid to transverse the membrane, whereas a water-resistant membrane may permit traversal of liquid. A measurement known as hydrostatic head may be used to determine whether a membrane is waterproof or not. This measurement determines the pressure at which a membrane starts to leak water. A membrane is generally considered to be waterproof if it does not leak when subjected to a pressure of 1000 mbar.
Water-proof membranes may be advantageously used in materials to prevent or minimize moisture penetration into the material. Examples of such uses include use in garments, such as rain coats, where it is desirable to prevent the wearer of the garment from getting wet. Although water-proof membranes are superior to water-resistant membranes in their capacity to prevent or minimize moisture penetration, water-proof materials that are non-breathable exhibit limited capacity for moisture transport, when compared to water-resistant membranes. As result, a garment made from water-proof non-breathable materials (e.g., rubber) may seem “hot and humid” to the wearer because it does not permit moisture vapor to escape from within the garment to the outside environment.
Therefore, there is a need for a breathable membrane (e.g., water-proof membrane) having improved moisture transport properties.
Yet another important property of materials relates to the material's anti-static capacity. Anti-static materials may be advantageously used in, for example, protective packaging materials to protect sensitive electronic components from static electrical charge. The problem with packaging electronic components and units so as to avoid the effects of electrostatic discharge has become increasingly acute as smaller and smaller dimensions are achieved in integrated circuits, making the devices more vulnerable to accidental discharge by relatively small voltage levels. There is therefore a need to produce anti-static materials with improved anti-static capabilities without losing other properties, such as flexibility and transparency, that are also desirable for the various uses of these materials.
Yet another often desirable property of materials is the stealth property of the material. Materials with stealth properties may be used to eliminate unwanted infra-red signatures during experiments. In military applications, stealth materials may be employed to enable aircrafts, soldiers, ships, and planes to operate while remaining less visible to radar, infra-red and other detection mechanisms. There is therefore a need to produce materials with improved stealth capabilities without losing other properties, such as flexibility and “hand and feel,” that are also desirable for the various uses of these materials.
The present disclosure relates to active particle-enhanced membrane and methods for making and using the same. The membrane can be a self-supporting membrane or a coating on a substrate. The present disclosure, while not limited as such, is particularly applicable to water-proof breathable membranes and methods of making and using the same. The present disclosure is also particularly applicable to quick-drying, odor-absorbing, anti-static membranes and methods for making and using the same, and to membranes with improved infra-red (IR) absorption and methods for making and using the same.
In some embodiments, a breathable membrane includes a base material solution and active particles. The active particles incorporated in the membrane may improve or add various desirable properties to the membrane, such as for example, moisture vapor transport capability, anti-static properties, or stealth properties. In some embodiments, the base material may exhibit water-proof properties when converted into non-solution state, and thereby result in a water-proof membrane. In some embodiments, the active particles may be protected from losing activity before, during, or after (or any combination thereof) the process of producing the membrane. In these embodiments, the active particles may be encapsulated in at least one removable encapsulant in an amount effective to prevent at least a substantial portion of the active particles from being deactivated prior to removal of the removable encapsulant. In some embodiments, the removable encapsulant may be removed to reactivate at least a portion of the active particles to improve the breathable, anti-static, or stealth properties of the membrane.
In some embodiments, the membrane may include polyurethane and solid particles. The membrane may be applied to a substrate such as a woven, non-woven, ePTFE (treated or untreated) substrate, PTFE substrate, polyurethane substrate, or knit material, or may be used independent of a substrate. In some embodiments, the membrane may be obtained from a mixture of a polyurethane solution, a polyacrylic solution, polyurethane solutions, 1,3 propanediol terephthalate solutions, or any other suitable solution, and protected or unprotected (or any combination thereof) active particles.
In some embodiments, after the encapsulated particles are incorporated into the base material solution, at least a portion of the removable protective substance (or removable encapsulant) may be removed to reactivate the active particles. Once the removable protective substance is removed, the active particles may bestow performance enhancing characteristics (e.g., odor adsorption, moisture management, etc.) to the base material solution or membrane. In addition to the performance enhancing characteristics that are imparted to the membrane, the active particles may be incorporated in a way that maintains the hand and feel, texture, durability, strength, stretchability, viscosity, compressibilty, expandability, relative density, other physical and chemical properties, or any combination thereof, generally associated with the base material before having the active particles incorporated therein.
FIG. 1 shows a flowchart illustrating steps that may be taken to produce an active particle-enhanced membrane in accordance with the principles of some embodiments of the present invention;
FIG. 2 shows specific formulations of mixtures that may be used to prepare active particle-enhanced membranes in accordance with the principles of some embodiments of the present invention;
FIG. 3 shows illustrative data obtained from an experiment the was performed in accordance with the principles of some embodiments of the present invention;
FIG. 4 shows illustrative data obtained from another experiment that was performed in accordance with the principles of some embodiments of the present invention; and
FIG. 5 shows illustrative data obtained from another experiment that was performed in accordance with the principles of some embodiments of the present invention.
FIG. 1 shows a flowchart illustrating steps that may be taken to produce active particle-enhanced membranes, such as, for example, a water-proof breathable membrane in accordance with the principles of some embodiments of the present invention. At step 110, a base material solution is provided. The base material solution may include a material, which when converted into a non-solution state (e.g., cured), exhibits water-proof breathable properties. For example, the base material solution may include a polyurethane solution, a polyacrylic solution, polyurethane solutions, 1,3 propanediol terephthalate solutions, or any other suitable solution. The base solution may include water and other ingredients such as cross-linking polymers. If desired, a combination of at least two different base material solutions may be used (e.g., a combination polyurethane and acrylic solution). An example of a polyurethane that may be used is a breathable polyurethane available from Noveon Corporation of Cleveland, Ohio. See, for example, U.S. Pat. No. 6,897,281, the disclosure of which is hereby incorporated by reference herein in its entirety, for a detailed discussion of a polyurethane that may be included in the base solution for a water-proof breathable membrane in accordance with the principles of some embodiments of the present invention.
In some embodiments, the base material solution may include Noveon's Permax™ polyurethane coating compound. In another embodiment, the base material solution may include Noveon's Permax™ polyurethane coating, an acrylic polymer, and an extra cross-linking agent.
At step 120, active particles may be provided. The active particles may be provided in a protected or unprotected state. It is well-known that certain particles may be used to add performance properties to materials in different forms such as gases, liquids, and solids. These particles may have properties that are suitable for odor adsorption, moisture management, ultraviolet light protection, chemical protection, bio-hazard protection, fire retardance, anti-bacterial protection, anti-viral protection, anti-fungal protection, anti-microbial protection, and other factors, and combinations thereof.
These particles may provide such properties because they are “active.” That is, the surface of these particles may be active. Surface active particles are active because they have the capacity to cause chemical reactions at the surface or physical reactions, such as, adsorb or trap substances, including substances that may themselves be a solid, liquid, gas or any combination thereof. Examples of substances that may be trapped or adsorbed by active particles include, but are not limited to, pollen, water, butane, and ambient air. Certain types of active particles (such as activated carbon) have an adsorptive property because each particle has a large surface area made up of a multitude of pores (e.g., pores on the order of thousands, tens of thousands, or hundreds of thousands per particle). It is these pores that provide the particle or, more particularly, the surface of the particle with its activity (e.g., capacity to adsorb). For example, an active particle such as activated carbon may adsorb a substance (e.g., butane) by trapping the substance in the pores of the activated carbon.
Active particles may include, but are not limited to, activated carbon, aluminum oxide (activated alumina), silica gel, soda ash, aluminum trihydrate, baking soda, p-methoxy-2-ethoxyethyl ester Cinnamic acid (cinoxate), zinc oxide, zeolites, titanium dioxide, molecular filter type materials, and other suitable materials.
Exposing the active particles to a substance may reduce or permanently negate the activity of the active particles by blocking or inhibiting the pores, thus reducing the surface activity of the active particles. That is, once the pores are blocked or inhibited with a substance, those blocked or inhibited pores may be prevented from further adsorption. However, the adsorptive capacity of active particles may be increased or restored by removing the substance that is blocking or inhibiting the pores. Hence, active particles may be rejuvenated or reactivated, for example, by being heated to a predetermined temperature.
A common problem associated with active particles is that they may lose activity or become permanently deactivated before, during, or after a process that incorporates the particles into a material (e.g., a base material). For example, active particles may lose a portion of their activity when exposed to contaminants in the ambient environment prior to being used in a process or during shipment from the active particle manufacturer to the end-user. Regardless of how particle activity is negated or reduced, such negation or reduction thereof may adversely affect the product produced by the process using the active particle to add or improve one or more properties of the product. For example, if particle activity is reduced, heavier particle loading may be required to make up for the reduction in activity, potentially resulting in particle loadings that may negatively affect one or more of the desirable inherent characteristics (e.g., hand and feel) of the material treated in the process. Moreover, heavier particle loading may require increased binder loadings, which may further affect the inherent characteristics treated in the process. Thus, it will be understood that even the smallest diminution of particle activity may adversely affect the material because of the cumulative effects (e.g., additional particles and binder loadings) stemming from that reduction.
An active particle may be preserved with a removable encapsulant for protection against “premature deactivation” (i.e., deactivation at an undesirable, usually early, time) by a deleterious substance or by a non-deleterious substance, whether such premature deactivation would occur on account of introduction to a binder substance, introduction to an extrusion event, or otherwise. Upon removal of the encapsulant, the active particle is reactivated and the active particle becomes capable of performance adsorption in the environment (whether such performance adsorption results in a performance-induced deactivated state which is permanent through adsorption of a deleterious substance, or such performance adsorption results in a temporary performance-induced deactivated state through adsorption of a non-deleterious substance which may be removed through rejuvenation of the particle).
A more specific aspect of protected active particles is that the removable protective substance preserves the activity of active particles against premature deactivation. The premature deactivation may be caused by deleterious or non-deleterious substances or matter (such as deleterious adsorption of a base material during extrusion of a composition including the active particles and base material or a drawing of a film including the active particles and base material solution), such active particles having the ability to interact through particle surface exposure or particle surface proximity to various substances or matter (of any phase). Preservation from such premature deactivation is achieved through use of at least one removable protective substance (or removable encapsulant). The removable encapsulant or removable protective substance may maintain the active particles in a protected state to prevent premature deactivation, in a manner enabling removal of the protective substance during reactivation to permit subsequent active performance by the active particles. When an active particle is in a protected or deactivated state, its further performance interaction is temporarily or permanently reduced or negated altogether. If the deactivated state is the result of a deleterious event (such as for example, adsorption of a deleterious substance or matter), the further interaction at the affected areas of the particle is more permanent. Deleterious premature deactivation may occur in a variety of circumstances, including for example, when the active particle is introduced to a deleterious slurry or exposed to an extrusion process or other deleterious event or material at a time that will result in the inability of the particles to provide active performance at the desired time (such as for example, drawing a film of the material containing the particles). Deleterious deactivation may occur and not constitute premature deactivation, if such deactivation occurs at the desired or appropriate time (for example, after drawing of a film and in connection with an intended target substance or matter).
When deactivation is the result of performance activity (in this case, performance adsorption) by the particles when incorporated in an article (adsorption at a time after removal of the removable protective substance), performance activity may be restored through rejuvenation (or other reactivation) if desired and if such deactivation was due to a non-deleterious event. A process of rejuvenation may include, for example, a washer/dryer cycling of a garment incorporating the waterproof breathable membrane of the invention.
With respect to the use of active particles to enhance performance activity in a base material (whether the activity is adsorptive, anti-microbial, dependent upon exposure of the surface of the particle to an environmental target of interaction, or simply an activity that is inhibited and/or enhanced through use of a removable protective substance), use of at least one removable encapsulant also enables use of fewer active particles in the embedding substance or matter (or in a resultant article) to achieve effective active performance, thereby reducing potential degradation of other physical properties (for example, strength or feel) of the embedding substance, matter or resultant article. Note that in this invention, it was suprisingly found that the addition of protected active particles to a base material solution, such as polyurethane solution, dramatically increased the breathability (or moisture vapor transport capacity) of the base material.
The use of a removable protective substance may also be designed to enable time-delayed exposure of a portion of active particles to effect an initial exposure or enhanced active performance at a later time (including for example, enhancement resulting from protection against premature deactivation).
Removable protective substances may include, but are not limited to, water-soluble surfactants, surfactants, salts (e.g., sodium chloride, calcium chloride), polymer salts, polyvinyl alcohols, waxes (e.g., paraffin, carnauba), photo-reactive materials, degradable materials, bio-degradable materials, ethoxylated acetylenic dials, starches, lubricants, glycols, mineral spirits, organic solvents, and any other suitable substances. Specific examples of such protective substances that are suitable for protecting active particles include the LPA-142 Solvent (paraffinic) sold by Sasol North America Inc. of Houston Tex., corn starch S9679 sold by Sigma-Aldrich of St. Louis Mo., the Surfynol AE03, AE02, 485W, 485, 2502, and 465 water soluble surfactants, sold by Air Products and Chemicals Corporation, of Allentown, Pa., waxes sold as Textile Wax-W and Size SF-2, by BASF Corporation, of Charlotte, N.C., and waxes sold as model numbers Kinco 878-S and Kinco 778-H by Kindt-Collins Company, of Cleveland, Ohio. Glycols sold by DOW Chemical Company under the name DOWANOL (DPnP, DPM, or DPMA) and TRITON CF-10 may also be used as a suitable protective substance.
A more detailed explanation of protected active particles, the preparation and applications thereof, and removal of the protective substance may be found, for example, in U.S. patent application publication no. 2004/0018359, which is incorporated herein by reference in its entirety. For the purposes of discussion of this invention, it is noted that active particles may be protected by mixing the active particles into a slurry of at least one protective substance, which may or may not be diluted with a solvent (e.g., water).
At step 130, the base material solution and the active particles may be mixed together. The active particles may be dispersed throughout the base material solution to provide a mixture having a uniform consistency. If desired, other ingredients, for example, a cross-linking agent or a solvent, may be added at this step. In some embodiments, the active particles may be protected by one or more encapsulants or protective substances prior to mixing with the base solution. In other embodiments, the active particles may be mixed with the base solution without encapsulation or protection. In yet other embodiments, only a portion of the active particles mixed with the base solution may be protected.
At step 140, the mixture may be applied to a substrate such that the mixture forms a layer or film thereon, prior to being cured or being converted by other suitable means into a non-solution form. The substrate may be a substance for which the cured mixture is intended to be permanently affixed such as, for example, a woven, a non-woven, paper or knitted material. In some embodiments, the mixture may be converted into non-solution state and used as a laminate. In approaches for which the cured mixture is intended to be removed and used independent of a substrate, the mixture may be applied to a release paper or other substance that has a low affinity for adhering to the cured mixture. The cured mixture may be referred to herein as a membrane. After coating the material the mixture is cured to provide a water-proof breathable membrane according to the principles of some embodiments of the invention. The mixture may be cured by subjecting it to a predetermined temperature for a predetermined period of time. Any conventional technique for effecting cure may be used such as, for example, a conventional oven, IR heating, or other suitable approach.
At step 150, if the active particles were protected before, during or after the process of producing the membrane, the protective substance may be removed from the active particles. The protective substance may be removed when the mixture is curing, or when subjected to a process (e.g., washing/drying cycle) or agent (e.g., light, solvent, bacteria) that causes the protective substance to be removed. It is understood that not all of the protective substance may be removed. That is, a portion of the protective substance may remain in contact with the base material or the active particles.
In practice, one or more steps shown in process 100 of FIG. 1 may be combined with other steps, performed in any suitable order, performed in parallel (e.g., simultaneously or substantially simultaneously) or removed.
It is further understood that the extent to which the protective substance is removed may vary with time. For example, the cured mixture may have to undergo several processes before all possible or nearly all possible protective substance may be removed. As another example, when two different protective substances are used, one substance may be removed relatively quickly as compared to the other.
The membrane obtained using the above-described process or variant thereof, surprisingly results in a material having liquid impermeable properties as well as enhanced moisture vapor transport properties.
It will be understood that the above-described process or variant thereof may also be used to produce a membrane that possesses other desirable properties derived, at least in part, from active particles incorporated therein. For example, in some embodiments, process 100 in FIG. 1 may be used to produce membranes with enhanced anti-static properties. In some embodiments, process 100 may be used to produce a membrane having improved stealth properties.
The membrane according to some embodiments of the invention may be derived from a mixture having different loadings of raw materials. The loading of each raw material (e.g., base material, activated carbon, and protective substance) may make up a predetermined percentage of the mixture. The loadings of materials may be in an amount effective for producing a membrane having desired properties.
The membrane, as derived from the mixture, may include a predetermined carbon weight percentage of the total weight of the membrane. For example, the carbon loading may range from about 0% to about 75% of the total weight of the membrane. In some embodiments, the carbon loading may range from about 0% to about 25%. In some embodiments, the carbon loading may range from about 0% to about 50%.
Certain carbon loadings may result in a membrane having better moisture vapor transport than other loadings, as well as better odor adsorption. For example, it was found that carbon loadings ranging from about 30% to about 50% of the total weight of the membrane significantly improved the moisture vapor transport capacity of the membrane while retaining the ability of the membrane to prevent moisture penetration penetration. It is understood that a predetermined carbon loading may be used to achieve one or more desired performance factors (e.g., moisture vapor transport and odor adsorption). It is also understood that the illustrative percentage weight loadings presented above are not restricted to activated carbon. These loading may be used for other active particles as well, and may be adjusted accordingly to account for the activity level to be derived from the active particles. Furthermore, the percentage loadings presented above are merely illustrative and do not exclude loadings that are not explicitly included within the named ranges. For example, percentage loadings outside of the ranges specified above are anticipated and within the spirit and principles of the present invention if such loadings allow the incorporated active particles to impart desirable properties onto the membrane while still retaining at least some of the properties of the membrane desired for various intended uses.
In some embodiments, a membrane may be created from a mixture in which the active particles are not protected. That is, a base material solution may be mixed with active particles and cured, resulting in a membrane having, for example, water-proof breathable properties. In some embodiments, a membrane may be created from a mixture including a base material solution and a removable protective substance, but not active particles. In some embodiments, a membrane may be created from a mixture including a base solution and non-active particles. In some embodiments, a membrane may be created from a mixture including a base solution, non-active particles, and a removable protective substance.
The following provides illustrative examples in which membranes are obtained from different mixtures. These examples are for the purposes of illustration only and are not to be construed as limiting the scope of the invention in any way.
Polyurethane solutions were combined with protected activated carbon. The protected activated carbon was suspended in the polyurethane solution and the mixture was applied to a nylon woven fabric. The mixture was dried and cured in an oven, where at least a portion of the protective substance was removed (e.g., evaporated off), resulting in a membrane coated on a substrate, the membrane having a thickness of one mil. The resultant membranes were then tested for butane adsorbance, dry time, moisture vapor transmission rate (MVTR), hydrostatic head, IR reflectance, and volume resistivity.
The moisture vapor transmission rate (MVTR) is the rate at which moisture permeates a dressing, film, membrane, or other construction, generally measured in grams per square meter per day (g/m2/day). Different methods for measuring MVTR include the Mocan method, the upright method for low moisture contact (indirect liquid contact with the membrane), and the inverted method for high moisture contact (direct liquid contact with the membrane). The upright method and the inverted method were used in this example.
MVTR by cup method may be measured according to Water method of ASTM E96-94 at 40 degrees Centigrade and 20% relative humidity over a 24 hour period. The cups typically have a 25 cm2 area opening. For the upright cup test, approximately 10 g of purified water is placed in the cup, while for the inverted cup, 20 g of purified water is used. The water used is typically ultrapure and deionized.
Membranes were also produced by drawing down the mixture on release paper. These membranes were cured and dried in an oven and then removed from the release paper yielding a self supporting membrane. This membrane was one mil thick.
The activated carbon was protected with Surfynol 485™. The activated carbon was subjected to an aqueous slurry including water and Surfynol 485™. This slurry was added to the polyurethane solution, the viscosity of the slurry or mixture of polyurethane and protected carbon was adjusted by adding more water. The carbon was Asbury 5564™ powdered coconut activated carbon. A cross-linking agent was used to increase the molecular weight of the polyurethane, thereby better enabling the membrane to adhere to the substrate.
The mixtures were cast using a 1 mil draw down rod. Curing and drying was done in an oven at 350° F. for 30 minutes. Membranes were prepared from mixtures shown in FIG. 2. FIG. 2 shows specific illustrative formulations of mixtures used to prepare membranes in this example. Sample 41-6-5 is a control, as is the sample labeled “base.” The nomenclature of samples beginning with 41-7 is now discussed. The number on the far right (e.g., “2” in sample 41-7-1-2) refers to a location in the membrane of the 41-7-1 sample. Thus, if the sample number is 41-7-1-4 (as shown in FIG. 3), data is obtained from location 4 in sample 41-7-1.
Each of the membranes were observed to be waterproof and breathable. FIG. 3 shows illustrative data obtained from membranes configured according to this example. This data includes the total weight, film weight, and carbon weight of each membrane sample. FIG. 3 also shows illustrative MVTR data obtained from the membrane samples. As indicated in FIG. 3, most of the samples have improved MVTR over the control.
In some embodiments, the methods described above for incorporating active particles into base materials (whether the active particles are protected prior to the incorporation or not) may be used to also produce membranes with enhanced anti-static and conductive properties. Anti-static materials are generally used for their ability to reduce or eliminate the buildup of electric charge. The anti-static properties of a material can be increased by making the material slightly conductive. One way to determine the conductive properties of a material is to measure the volume resistivity of the material. Volume resistivity indicates how readily a material conducts electricity. The lower the volume resistivity, the higher the electrical conductivity of the material and thus, the more readily the material conducts electricity. FIG. 4 shows illustrative volume resistivity data for several samples. As shown by the results, the samples which have activated carbon incorporated therein have reduced volume resistivity compared to the controls which do not have activated carbon incorporated therein. As explained above, the observed reduction in volume resistivity of the carbon-activated samples compared to the controls shows that the incorporation of activated carbon into the base materials improved the electrical conductivity and anti-static capability of the sample or membrane.
In some embodiments, the methods described above for incorporating active particles into base materials (whether the active particles are protected prior to incorporation or not) may be used to also produce membranes with enhanced stealth properties. Material with enhanced stealth property possess low infra-red (IR) reflectance and may be useful as coatings for military garments, tanks, satellites, planes, and in any scenario where materials with enhanced stealth properties are desirable. Materials with low reflectance to a particular wavelength absorb most of that wavelength, and may therefore, make the material less detectable when subject to light of that particular wavelength. For example, in the present invention, it was found that incorporating active particles, such as for example activated carbon, into the base material increased the ability of the base materials to absorb IR light. FIG. 5 shows illustrative total reflectance of several different materials across varying wavelengths. Membrane sample 41-6-3, labeled 80_80_PVC_6_41_03 in FIG. 5, is shown to have a lower reflectance percentage than the other materials, across the same wavelengths.
Thus, active-particle enhanced membrane and methods for making the same are disclosed. The above described embodiments of the present invention are presented for purposes of illustration and not of limitation, and the present invention is limited only by the claims which follow.
1. A water-proof breathable membrane comprising:
a substantially liquid-impermeable cured base material solution comprising a first thickness;
a plurality of active particles in contact with the substantially liquid-impermeable cured base material solution, wherein the plurality of active particles,
are capable of improving the transmission of vapor through the substantially liquid-impermeable cured base material solution, and
comprise a second thickness, wherein the first thickness is at least 2.5 times larger than the second thickness but less than an order of magnitude larger than the second thickness;
at least one removable encapsulant in an amount effective to prevent at least a substantial portion of the plurality of active particles from being deactivated prior to removal of the removable encapsulant; wherein,
the at least one removable encapsulant is removable to reactivate at least a portion of the plurality of active particles to improve the transmission of vapor through the water-proof breathable membrane, and
the membrane comprises a moisture vapor transmission rate from about 600 g/m2/day to about 11000 g/m2/day.
2. The membrane according to claim 1, wherein the membrane possesses anti-static properties due at least in part to the active particles.
3. The membrane according to claim 1, wherein the membrane possesses stealth properties due at least in part to the active particles.
4. The membrane according to claim 1, wherein the membrane possesses odor absorbance properties due at least in part to the active particles.
5. The membrane according to claim 1, wherein the membrane possesses quick drying properties due at least in part to the active particles.
6. The membrane according to claim 1, wherein the base material solution is selected from the group consisting of: a polyurethane solution, a polyacrylic solution, 1,3 propanediol terephthalate solutions, and any suitable combination thereof.
7. The membrane according to claim 1, wherein the active particles comprise activated carbon.
8. The membrane according to claim 1, wherein the active particles comprise zeolites.
9. The membrane according to claim 1, wherein the active particles are selected from the group consisting of: antibacterial, antiviral, antimicrobial, antifungal particles, and any suitable combination thereof.
10. The membrane according to claim 1, wherein the active particles are selected from the group consisting of: activated carbon, aluminum oxide (activated alumina), silica gel, soda ash, aluminum trihydrate, baking soda, p-methoxy-2-ethoxyethyl ester cinnamic acid (cinoxate), zinc oxide, zeolites, titanium dioxide, molecular filter-type materials, and any suitable combination thereof.
11. The membrane according to claim 1, wherein the at least one removable encapsulant is selected from the group consisting of: water-soluble surfactants, surfactants, salts, photo-reactive materials, degradable materials, bio-degradable materials, ethoxylated acetylenic diols, starches, lubricants, glycols, corn starch, mineral spirits, organic solvents, paraffinic solvents, and any suitable combination thereof.
12. The membrane according to claim 1, wherein the active particles comprise about 0% to about 75% of the total weight of the membrane.
13. The membrane according to claim 1, wherein the active particles comprise about 30% to about 50% of the total weight of the membrane.
14. The membrane according to claim 1, wherein the active particles comprise about 0% to about 30% of the total weight of the membrane.
15. The membrane according to claim 1, wherein the active particles comprise about 0% to about 50% of the total weight of the membrane.
16. The membrane according to claim 1, wherein the membrane comprises a yarn or fabric.
17. The membrane according to claim 1, wherein the membrane comprises a plastic material.
18. The membrane according to claim 1, wherein the membrane comprises an article of clothing.
19. The membrane according to claim 1, wherein the membrane comprises a fabric.
20. The membrane according to claim 1, wherein the membrane comprises a coated fabric.
21. The membrane according to claim 1, wherein the membrane is coated on to ePTFE.
22. The membrane according to claim 1, wherein the membrane comprises a coated article of clothing.
23. The membrane according to claim 1, wherein the membrane comprises a non-woven membrane.
24. The membrane according to claim 1, wherein the membrane comprises a laminate.
25. The membrane according to claim 1, wherein the membrane is selected from the group consisting of bags, foam, plastic components, upholstery, carpeting, rugs, mats, sheets, towels, rugs, pet beds, mattress pads, mattresses, curtains, filters, shoes, insoles, diapers, shirts, pants, blouses, undergarments, protective suits, and any suitable combination thereof.
26. The membrane according to claim 1, wherein the removable encapsulant is a first removable encapsulant, and the membrane further comprises a second removable encapsulant.
27. A water-proof composition comprising:
a liquid-impermeable breathable cured base material comprising a first thickness;
a plurality of active particles in contact with the liquid-impermeable breathable cured base material, the plurality of active particles comprising a second thickness; and wherein,
the first thickness comprises a thickness at least 2.5 times larger than the second thickness but less than an order of magnitude larger than the second thickness,
the active particles improve the moisture vapor transport capacity of the composition, and
a moisture vapor transmission rate of the water-proof composition comprises from about 600 g/m2/day to about 11000 g/m2/day.
28. The composition of claim 27, wherein the active particles comprise about 0% to about 75% of the total weight of the composition.
29. The composition of claim 27, wherein the active particles comprise about 30% to about 50% of the total weight of the composition.
30. The composition of claim 27, wherein the active particles comprise about 0% to about 30% of the total weight of the composition.
31. The composition of claim 27, wherein the active particles comprise about 25% to about 75% of the total weight of the composition.
32. The composition of claim 27, wherein the active particles comprise about 0% to about 50% of the total weight of the composition.
33. The composition of claim 27, wherein the composition possesses anti-static properties at least in part due to the active particles.
34. The composition of claim 27, wherein the composition possesses stealth properties at least in part due to the active particles.
35. The composition of claim 27, wherein the composition possesses odor absorbance properties at least in part due to the active particles.
36. The composition of claim 27, wherein the composition possesses quick drying properties at least in part due to the active particles.
37. The composition of claim 27, wherein the active particles are selected from the group consisting of: activated carbon, aluminum oxide (activated alumina), silica gel, soda ash, aluminum trihydrate, baking soda, p-methoxy-2-ethoxyethyl ester cinnamic acid (cinoxate), zinc oxide, zeolites, titanium dioxide, molecular filter-type materials, and any suitable combination thereof.
38. The composition of claim 27 further comprising: at least one removable encapsulant in an amount effective to prevent at least a substantial portion of the active particles from being deactivated prior to removal of the removable encapsulant, and wherein the removable encapsulant is removable to reactivate at least a portion of the active particles to improve the moisture vapor transport capacity of the composition.
39. The composition of claim 38, wherein the at least one removable encapsulant is selected from the group consisting of: water-soluble surfactants, surfactants, salts, polymer salts, polyvinyl alcohols, waxes, photo-reactive materials, degradable materials, bio-degradable materials, ethoxylated acetylenic diols, starches, lubricants, glycols, corn starch, mineral spirits, organic solvents, paraffinic solvents, and any suitable combination thereof.
40. A water-proof composition comprising:
a base material comprising a first thickness;
a plurality of active particles in contact with the base material, the plurality of active particles comprising a second thickness; and wherein,
the first thickness is at least 2.5 times larger than the second thickness but less than an order of magnitude larger than the second thickness,
the active particles improve the vapor transport and anti-static properties of the composition, and
41. The composition of claim 40, wherein the active particles comprise activated carbon.
42. The composition of claim 40, wherein the active particles comprise zeolites.
43. The composition of claim 40, wherein the active particles comprise about 30% to about 50% of the total weight of the composition.
44. The composition of claim 40, wherein the active particles comprise about 0% to about 30% of the total weight of the composition.
45. A water-proof composition comprising:
the first thickness comprises a thickness about 2.5 times larger than the second thickness but less than an order of magnitude larger than the second thickness,
the active particles improve the vapor transport and stealth properties of the composition, and
46. The composition of claim 45, wherein the active particles comprise activated carbon.
47. The composition of claim 45, wherein the active particles comprise zeolites.
48. The composition of claim 45, wherein the active particles comprise about 30% to about 50% of the total weight of the composition.
49. The composition of claim 45, wherein the active particles comprise about 0% to about 30% of the total weight of the composition.
50. The membrane of claim 1, wherein, the substantially liquid-impermeable cured base material solution, plurality of active particles, and at least one removable encapsulant comprise a mixture, the mixture being adapted for application to a substrate prior to the substantially liquid-impermeable cured base material solution being cured.
51. The membrane of claim 1 wherein,
the first thickness comprises a thickness of about 1 mil.
52. The composition of claim 27 wherein,
53. The composition of claim 40 wherein,
54. The composition of claim 45 wherein,
55. The membrane of claim 1 wherein, the first thickness is at least as large as the second thickness.
56. The composition of claim 27 wherein, the first thickness is at least as large as the second thickness.
57. The composition of claim 40 wherein, the first thickness is at least as large as the second thickness.
58. The composition of claim 45 wherein, the first thickness is at least as large as the second thickness.
59. The composition of claim 1 wherein, the second thickness comprises a thickness of about 10 microns.
60. The composition of claim 27 wherein, the second thickness comprises a thickness of about 10 microns.
61. The composition of claim 40 wherein, the second thickness comprises a thickness of about 10 microns.
62. The composition of claim 45 wherein, the second thickness comprises a thickness of about 10 microns.
US11801647 2006-05-09 2007-05-09 Active particle-enhanced membrane and methods for making and using the same Active 2030-03-10 US8945287B2 (en)
US79942606 true 2006-05-09 2006-05-09
US11801647 US8945287B2 (en) 2006-05-09 2007-05-09 Active particle-enhanced membrane and methods for making and using the same
US20070264203A1 true US20070264203A1 (en) 2007-11-15
US8945287B2 true US8945287B2 (en) 2015-02-03
ID=38477382
US11801647 Active 2030-03-10 US8945287B2 (en) 2006-05-09 2007-05-09 Active particle-enhanced membrane and methods for making and using the same
US (1) US8945287B2 (en)
JP (1) JP5551431B2 (en)
CN (1) CN101479331B (en)
EP (2) EP2520611B1 (en)
WO (1) WO2007133640A1 (en)
CN103087391A (en) * 2013-03-11 2013-05-08 河南理工大学 Antistatic polymer blending composition
DE102014000135A1 (en) * 2014-01-13 2015-07-16 Bernd Zeidler Device for utilizing exhaust gas condensate for room humidification and process humidification
FR1287139A (en) 1960-04-22 1962-03-09 Chemstrand Corp A method for treating filamentary material of acrylonitrile polymers
DE2251071A1 (en) 1971-10-18 1973-04-26 Ici Ltd textile materials conducting
US3865758A (en) 1971-09-13 1975-02-11 Teijin Ltd Polyurethane foam filter material containing adsorbent and method of production thereof
JPS5932921Y2 (en) 1980-07-16 1984-09-14
WO1986004367A1 (en) 1985-01-15 1986-07-31 Sca Development Aktiebolag Method at manufacture of carbon-coated fibre material
JPS62206083A (en) 1986-03-06 1987-09-10 Teijin Ltd Production of antistatic moisture pervious waterproof cloth
JPS63100915U (en) 1987-10-16 1988-06-30
JPH01280073A (en) 1988-04-27 1989-11-10 Unitika Ltd Deodorant moisture-permeable and waterproof web
JPH01299624A (en) 1988-05-27 1989-12-04 Japan Exlan Co Ltd Hygroscopic fiber
WO1989012552A1 (en) 1988-06-21 1989-12-28 Valtion Teknillinen Tutkimuskeskus Method for xerographic printing of a textile material
DE4008519A1 (en) 1989-03-17 1990-09-20 Toshiba Kawasaki Kk Electrographic copying machine - contg. traps to collect stray toner powder and means for chemically treating the powder collected
JPH0357Y2 (en) 1984-12-21 1991-01-07
EP0330675B1 (en) 1986-12-08 1992-03-25 Nordson Corporation Method and apparatus for depositing moisture-absorbent material in a substrate
GB2238802B (en) 1989-12-06 1993-10-06 Purification Prod Improvements in the production of particulate solid-bearing low density air-permeable sheet materials
EP0341870B1 (en) 1988-05-13 1994-06-15 Minnesota Mining And Manufacturing Company Absorbent elastomeric wound dressing
JPH0975110A (en) 1995-09-13 1997-03-25 Achilles Corp Lining material for footgear
EP0596627B1 (en) 1992-11-04 1997-04-16 Rohm And Haas Company Coating compositions incorporating composite polymer particles
US5650030A (en) 1993-05-28 1997-07-22 Kyricos; Christopher J. Method of making a vapor and heat exchange element for air conditioning
WO1998007790A1 (en) 1996-08-21 1998-02-26 Chisso Corporation Antimicrobial resin composition and antimicrobial resin moldings made using the same
EP0791681A3 (en) 1996-02-22 1998-04-22 MITSUI MINING &amp; SMELTING CO., LTD. Composite material carrying zinc oxide fine particles adhered thereto and methodfor preparing same
EP0682927B1 (en) 1994-05-13 1999-07-28 THE PROCTER &amp; GAMBLE COMPANY Shield against absorbent particle loss in absorbent products
GB2338720A (en) 1998-06-10 1999-12-29 Kang Dih En Enterprise Co Limi Plate filter
JP2000160475A (en) 1998-11-26 2000-06-13 Falcon Technology:Kk Cloth and clothes
JP2001046479A (en) 1999-08-09 2001-02-20 Hitachi Ltd Deodorizing device
EP1121968A2 (en) 2000-01-31 2001-08-08 Nichias Co., Ltd. Chemical filter and manufacturing method thereof
US6350492B1 (en) 1996-08-09 2002-02-26 The Goodyear Tire & Rubber Company Coated multi-filament reinforcing carbon yarn
US20020037406A1 (en) 2000-08-01 2002-03-28 Hisato Takashima Single fiber containing carbon powder inside the fiber, processed work and cotton work thereof, processed work and cotton work containing carbon powder on the fiber surface or in the fibers, and producing thereof
US6468651B2 (en) 1998-11-17 2002-10-22 Japan Vilene Company, Ltd. Nonwoven fabric containing fine fiber, and a filter material
US6482514B1 (en) 2001-04-06 2002-11-19 Minabegawa Village Co-Op Forest Deodorant rayon fibers and method for producing the same
WO2002091977A1 (en) 2001-05-16 2002-11-21 The Procter & Gamble Company A process for making a fibrous web containing functional material
WO2003007714A1 (en) 2001-07-20 2003-01-30 3M Innovative Properties Company Adherent microcapsules
WO2003027365A1 (en) 2001-09-21 2003-04-03 Outlast Technologies, Inc. Multi-component fibers having reversible thermal properties and methods of manufacturing thereof
US20030088006A1 (en) 2001-07-27 2003-05-08 Bridgestone Corporation Natural rubber master batch, production method thereof, and natural rubber composition
EP1115469B1 (en) 1998-09-18 2003-10-15 Haas, Rainer Fibrous products containing active substances, a method for the production thereof, and use of the same
WO2002083028B1 (en) 2001-04-11 2003-11-20 Playtex Products Inc Fibrous absorbent articles having malodor counteractant
JP2003340231A (en) 2002-05-22 2003-12-02 Japan Vilene Co Ltd Moisture absorbing sheet, laminated moisture absorbing sheet and organic electroluminescence element panel
EP1112780A3 (en) 1999-11-25 2003-12-10 Rohm And Haas Company Method for producing fast drying multi-component waterborne coating compositions
WO2003105996A1 (en) 2002-06-12 2003-12-24 Traptek, Llc Encapsulated active particles and methods for making and using the same
WO2003106543A1 (en) 2002-06-13 2003-12-24 Kappler, Inc. Microporous membrane with adsorbent multi-functional filler
EP1135087B1 (en) 1998-12-01 2004-01-02 3M Innovative Properties Company Wet skin adhesive article
JP2004003068A (en) 2001-07-24 2004-01-08 Komatsu Seiren Co Ltd Textile material and method for producing the same
US20040030022A1 (en) 2000-10-02 2004-02-12 Brittain William J. Synthesis and characterization of nanocomposites by emulsion polymerization
EP0962831B1 (en) 1998-06-04 2005-02-02 Xeikon International N.V. Toner composition for use in textile printing
WO2005017054A1 (en) 2003-08-14 2005-02-24 Akzo Nobel Coatings International B.V. Paint comprising a liquid phase and an active powder phase
US20050075027A1 (en) 2003-10-07 2005-04-07 Etchells Marc D. Moisture management system
EP1403035B1 (en) 2001-03-22 2006-11-08 Teijin Fibers Limited High moisture absorbing nonwoven fiber structure and production method therefor
WO2007133640A1 (en) 2006-05-09 2007-11-22 Traptek Llc Active particle-enhanced membrane and methods for making and using the same
JP2001502762A (en) * 1996-09-20 2001-02-27 ミネソタ マイニング アンド マニュファクチャリング カンパニー Solid phase extraction membrane
EP0031719B1 (en) 1979-12-28 1984-06-13 Albany International Corp. Sorbent-loaded textile fibers and films and methods of fabricating the same
EP0959852B1 (en) 1996-01-17 2003-05-02 THE PROCTER &amp; GAMBLE COMPANY Sanitary napkin with perfume-bearing microcapsule adhesive
US6294183B1 (en) 1996-08-21 2001-09-25 Chisso Corporation Antimicrobial resin composition and antimicrobial resin molded article comprising same
US6451427B1 (en) 2000-08-01 2002-09-17 Hisato Takashima Single fiber containing carbon powder inside the fiber, processed work and cotton work thereof, processed work and cotton work containing carbon powder on the fiber surface or in the fibers, and producing thereof
CN1658948A (en) 2002-06-12 2005-08-24 创普太克公司 Encapsulated active particles and methods for making and using the same
Chen, Jizhaung, "Chinese Office Action re Application No. 200780024560.9", Apr. 28, 2013, p. 8, Published in: CN.
Chifeng, Tu, "Notification of the Third Office Action re application No. 2007-80024560.9", Jan. 29, 2012, p. 7, Published in: CN.
Chifeng, Tu, "Office Action re Chinese Patent Application No. 200780024560.9", Aug. 24, 2012, p. 8, Published in: CN.
Chifeng, Tu, "Office Action related to Chinese Application 2007-80024560.9", Dec. 31, 2010, p. 10, Published in: CN.
Haggquist, Gregory W., "Declaration of Gregory W. Haggquist re Application No. 200780024560.9", Jul. 8, 2013, p. 8, Published in: US.
Huang et al., "A new filter media of nonwoven composite with activated carbon fibers"; Jounral of Advanced Materials, v 36 n 2, Apr. 2, 2004, pp. 35-38.
Intellectual Property Office of Taiwan, "Office Action in related Taiwan Patent Application No. 096116533", Jun. 6, 2013, p. 26, Published in: TW.
International Search Report (PCT, Oct. 29, 2007).
International Search Report, Application No. PCT/US2003/18854, mailed Oct. 30, 2003.
International Search Report, Application No. PCT/US2007/024063, mailed Aug. 1, 2008.
Jizhuang, Chen, "Response to Office Action re Chinese Patent Application No. 2007-80024560.9", Jun. 13, 2012, p. 7, Published in: CN.
Kala, Naoto, "Japanese Office Action re application No. 2009-509860", Feb. 13, 2012, p. 8, Published in: JP.
Kulkarni, V.G., "Color, functional and multi-attribute solutions for polyester fibers"; Chemical Fibers International, v 53, n 6, Dec. 23, 2003, pp. 452-454.
McLeod et al., "Charcoal cloth in odour related adsorption"; Filtration and Separation, v 23, n 3, May-Jun. 1986, pp. 164-165.
Myron J. Copland and George Lopatin, "Preparation of Activated Carbon-Filled Micro-porous Hollow Multifilament-A Summary Report," Report No. NATICK TR-78/036, National Technical Information Service, U.S. Department of Commerce, Nov. 1978.
Myron J. Copland and George Lopatin, "Preparation of Activated Carbon-Filled Micro-porous Hollow Multifilament—A Summary Report," Report No. NATICK TR-78/036, National Technical Information Service, U.S. Department of Commerce, Nov. 1978.
Office Action Dated Oct. 3, 2008, U.S. Appl. No. 11/226,524.
Payne et al., "New durable antimicrobial finish for cotton textiles"; American Dyestuff Reporter, v 85, n. 6, Jun. 1996, pp. 26-30.
Percival, Shane, "Instructions sent to Shusaku Yamamoto in response to Feb. 15, 2012 Office Action re Japanese Application No. 2009-509860", Jun. 13, 2012, p. 18, Published in: US.
Percival, Shane, "Letter to Chen Jizhuang with amendments and arguments for filing response to Jan. 29, 2012 Office Action re application No. 2007-80024560.9", May 16, 2012, p. 16, Published in US.
Percival, Shane, "Repsonse to Chinese Office Action re Application No. 200780024560.9", Jul. 9, 2013, p. 18, Published in: US.
Percival, Shane, "Response to Dec. 31, 2010 Office Action," Jun. 28, 2010, pp. 1-10.
Percival, Shane, "Response to Japanese Office Action re Application No. 2009-509860", Jul. 10, 2013, p. 21, Published in: US.
Percival, Shane, "Response to Office Action re Chinese Patent Application No. 2007-80024560.9", Dec. 18, 2012, p. 15, Published in: US.
Percival, Shane, Response to the 2nd Chinese Office Action dated Aug. 8, 2011 sent to Foreign Associates, Oct. 13, 2011, p. 13, Published in: US.
Russell, Graham, "Communication of Extended Search Report in related European Patent Application No. 12178957.2 ", Sep. 27, 2012, p. 7, Published in: EP.
Schutte, et al., "European Office Action re Application No. 07 794 738.0", Feb. 7, 2013, p. 5, Published in: EP.
SIPO, Notification of the Second Office Action re Chinese Application No. 200780024560.9, Aug. 24, 2011, p. 6, Published in: CN.
Yamamoto, Shusaku, "Response to Office Action re Japanese Application No. 2009-509860", Jun. 15, 2012, p. 25, Published in: JP.
Yamazaki, Toshinao, "Japanese Office Action re Application No. 2009-509860", Jan. 10, 2013, p. 8, Published in: JP.
EP2021405B1 (en) 2014-04-09 grant
CN101479331B (en) 2014-04-09 grant
WO2007133640A1 (en) 2007-11-22 application
EP2520611A1 (en) 2012-11-07 application
EP2520611B1 (en) 2017-06-21 grant
CN101479331A (en) 2009-07-08 application
US20070264203A1 (en) 2007-11-15 application
JP5551431B2 (en) 2014-07-16 grant
JP2009536696A (en) 2009-10-15 application
EP2021405A1 (en) 2009-02-11 application
Olivas et al. 2008 Alginate–calcium films: water vapor permeability and mechanical properties as affected by plasticizer and relative humidity
Rubilar et al. 2013 Physico-mechanical properties of chitosan films with carvacrol and grape seed extract
US20120077891A1 (en) 2012-03-29 Porogen compositions, methods of making and uses
US6444595B1 (en) 2002-09-03 Flexible corrosion-inhibiting cover for a metallic object
Buonocore et al. 2005 Mono-and multilayer active films containing lysozyme as antimicrobial agent
Apaydin et al. 2013 Polyallylamine–montmorillonite as super flame retardant coating assemblies by layer-by layer deposition on polyamide
US6770579B1 (en) 2004-08-03 Smart porous film or material
Conte et al. 2007 Development of immobilized lysozyme based active film
US6468929B2 (en) 2002-10-22 Fabric coating compositions providing excellent resistance to seam combing, particularly for use on automotive airbag fabrics
Rhim et al. 1998 Characteristics of chitosan films as affected by the type of solvent acid
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:HAGGQUIST, GREGORY W.;REEL/FRAME:019377/0506
Free format text: TRIAL NO: IPR2018-00190
Opponent name: VF OUTDOOR LLC AND VF CORPORATION