Patent US6089756 - Plain bearing - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsThere are provided a plain bearing which is excellent in oil retaining property and wear-resistant property. The plain bearing has a number of fine grooves which are parallely formed with one another and extending in the circumferential direction on the inner surface of the bearing, the fine grooves...http://www.google.com/patents/US6089756?utm_source=gb-gplus-sharePatent US6089756 - Plain bearingAdvanced Patent SearchTry the new Google Patents, with machine-classified Google Scholar results, and Japanese and South Korean patents.Publication numberUS6089756 APublication typeGrantApplication numberUS 09/038,825Publication dateJul 18, 2000Filing dateMar 12, 1998Priority dateMar 18, 1997Fee statusPaidPublication number038825, 09038825, US 6089756 A, US 6089756A, US-A-6089756, US6089756 A, US6089756AInventorsAkira Ono, Hideyumi Matsumura, Masayuki Niwa, Shoji Nawa, Takayuki ShibayamaOriginal AssigneeDaido Metal Company Ltd.Export CitationBiBTeX, EndNote, RefManPatent Citations (9), Referenced by (33), Classifications (16), Legal Events (5) External Links: USPTO, USPTO Assignment, EspacenetPlain bearing
US 6089756 AAbstract
There are provided a plain bearing which is excellent in oil retaining property and wear-resistant property. The plain bearing has a number of fine grooves which are parallely formed with one another and extending in the circumferential direction on the inner surface of the bearing, the fine grooves comprising deep grooves and shallow grooves. When this bearing is used as a plain bearing, a large amount of lubricating oil can be retained in the deep grooves and the shallow grooves so that a plain bearing which is excellent in anti-seizure property and wear-resistant property can be obtained. Further, even if the shallow grooves will have been worn out by wear and tear during use of extended period of time, the anti-seizure property and the wear-resistant property can be stably maintained by the lubricating oil retained in the deep grooves.
1. A plain bearing defining an axial direction and including an inner bearing surface comprising:circumferential fine grooves being substantially parallel with one another and spaced in the axial direction generally at a predetermined groove interval, said grooves being adapted to retain lubricating oil therewithin and between the inner surface of the bearing and a rotating shaft; wherein the grooves comprise a plurality of groove groups, wherein each group of the plurality includes at least one first deep groove and a plurality of second shallow grooves, and wherein all first deep grooves are substantially of a same first depth and all second shallow grooves are substantially of a same second depth, whereby the oil is retained in the first deep groove if the second shallow grooves are worn down during a long time of use, such that an anti-seisure property is stably maintained. 2. The plain bearing as claimed in claim 1, wherein a number of said first deep grooves are formed in a vicinity of both axial ends of said plain bearing, and a number of said second shallow grooves are formed in an axial central portion of said plain bearing, whereby a larger amount of the oil is retained at the axial ends and conformability and wear-resistance of the bearing are enhanced.
3. A plain bearing having a plurality of fine open grooves which are circumferentially cut into the inner surface of said plain bearing,said fine open grooves being parallel with one another and extending at predetermined intervals in the axial direction of said plain bearing, whereby lubricating oil is retained between the inner surface of the bearing and a rotating shaft; said fine open grooves being provided in adjacent groove groups, each said groove group comprising a first open groove having a deep depth, a plurality of second open grooves having a shallow depth, and a third open groove having a deep depth equivalent to depth of said first open groove, said plurality of second open grooves being sandwiched between said first and third open grooves, and wherein said first and third open grooves of said plurality of groove groups have the same depth, and said plurality of second open grooves of said plurality of groove groups have the same depth, whereby the oil is retained in the first open deep groove if the second open shallow grooves are worn down during a long time of use, such that an anti-seisure property is stably maintained. 4. The plain bearing of claim 3, wherein said third groove of a first group of grooves corresponds to a first groove of an adjacent group of grooves.
In order to increase the amount of the lubricating oil to be retained, it had been made to provide a plain bearing having a number of fine grooves which are circumferentially formed with on the inner surface of the bearing, the fine grooves being parallel with one another and being arranged to extend in the axial direction of the plain bearing, the fine grooves having a depth of several micro meters (μm).
JP-A-59-73620 discloses a plain bearing having a number of fine grooves which are circumferentially formed on the whole inner surface of the bearing, the fine grooves being arranged in the axial direction of the bearing and being inclined at an angle of 0 to about 5 degrees relative to the circumferential direction of the bearing. This arrangement allows a large amount of lubricating oil to be supplied into the fine grooves, thereby promoting the heat dissipation (Prior Art 1).
JP-U-63-53922 discloses a plain bearing having a number of fine grooves which are circumferentially formed on the inner surface of the bearing, the fine grooves being arranged to extend in the axial direction of the plain bearing, thereby having a large proportion of sliding surface area which is obtained by making the fine grooves in the vicinity of both ends of bearing metals in a larger pitch than those of the axial central portion of the bearing metals. With this arrangement, the lowering in the durability of the bearing is intended to be suppressed by reducing the number of the fine grooves in the vicinity of the both ends of the bearing, where the rotating shaft is in partial contact with the bearing, thereby preventing the decrease in the area which is subjected to the axial loading due to the formation of the fine grooves, as much as possible, so as to reduce the specific load (Prior Art 2).
P-U-63-62621 discloses a plain bearing having fine grooves which are circumferentially formed on the inner surface of the bearing, the fine grooves being arranged to extend in the axial direction of the plain bearing, the fine grooves in the vicinity of both ends of bearing metals being arranged in a deeper depth than those of the axial central portion of the bearing metal. In this Prior Art 3, a line connecting the leading ends of the fine grooves (the bottom portions of the fine grooves) is barrel-shaped so that the depth of the fine grooves in the vicinity of the both ends of the bearing is deeper than those of the rest of the bearing. With this arrangement, in contrast with the Prior Art 2, the amount of the lubricating oil in the both ends which are subjected to a high shock loading due to a partial contact of a rotating shaft is increased to thereby suppress the heat generation in the both ends of the bearing metals (Prior Art 3).
In these Prior Arts 1 to 3, every plain bearing has a number of fine grooves which are circumferentially formed on the inner surface of the bearing, the fine grooves being arranged to extend in the axial direction of the plain bearing, each of side wall portions of the fine grooves functioning as a bank in the axial direction of the bearing. Each of the side wall portions may offer a resistance when the lubricating oil outflowing in the axial direction of the bearing, to thereby prevent an inflow pressure from dropping when the lubricating oil flowing into a clearance between the inner surface of the bearing and the rotating shaft and also allow a large amount of lubricating oil to flow through the fine grooves so as to promote the heat dissipation.
However, if such a bearing is used during a long period of time, the fine grooves will be worn out due to the progress of wear and tear. At the same time, the effect of anti-seizure property and wear-resistant property will be lost rapidly. Particularly, in the Prior Art 3, though the fine grooves in the vicinity of the both ends of the bearing are deeply formed, since those fine grooves will wear out preferentially due to a partial contact of the rotating shaft, the other fine grooves will be worn out by wear and tear, almost concurrently with the wear out of the fine grooves in the vicinity of the both ends of the bearing.
With the above-mentioned problems in view, upon paying attention to the depth of the fine grooves formed in the circumferential direction on the inner surface of the bearing, it is an object of the present invention to provide a plain bearing which is excellent in wear-resistant property and has a stable oil retaining property during use of extended period of time.
According to the feature of the present invention, there is provided a plain bearing having a number of fine grooves which are circumferentially formed on the inner surface of the plain bearing, the fine grooves being parallel with one another and being arranged to extend at predetermined intervals in the axial direction of the plain bearing, wherein the fine grooves comprise deep-depth grooves (which will be referred to simply as deep grooves hereinbelow) and shallow-depth grooves (which will be referred to simply as shallow grooves hereinbelow).
With this arrangement, when the bearing is used as a plain bearing, a large amount of lubricating oil is retained in both the deep grooves and the shallow grooves. Particularly, each bank action of side wall portions defined between the fine grooves offers a resistance when the lubricating oil outflowing in the axial direction of the bearing and thus an inflow pressure when the lubricating oil flowing into a clearance between the inner surface of the bearing and the rotating shaft increases so that the thickness of an oil film to be formed between the inner surface of the bearing and the rotating shaft becomes thicker. Accordingly, the bearing and its associated rotating parts can be prevented from seizure, thereby providing a plain bearing which is excellent in anti-seizure property and wear-resistant property. Further, even when the shallow grooves will have been worn out by wear and tear during a long time, the anti-seizure property and the wear-resistant property can be stably maintained by the lubricating oil retained in the deep grooves.
According to another feature of the present invention, there is provided a plain bearing having a number of fine grooves which are circumferentially formed on the inner surface of the bearing the fine grooves being parallel with one another and being arranged to extend at predetermined intervals in the axial direction of the plain bearing, wherein the fine grooves comprise a plurality of groove groups, one of the groove groups including one or more of deep grooves and a plurality of shallow grooves.
This arrangement of the bearing can be easily processed by boring work, for example, using a cutting tool having one or more cutting edges to cut a plurality of grooves simultaneously or using a combination of a plurality of cutting tools.
According to still another feature of the present invention, there is provided a plain bearing having a number of fine grooves which are circumferentially formed on the inner surface of the plain bearing, the fine grooves being parallel with one another and being arranged to extend at predetermined intervals in the axial direction of the plain bearing, wherein a number of deep grooves are formed in the vicinity of the axial both ends of the bearing, while a number of shallow grooves are formed in the axial central portion of the bearing.
With this arrangement, a large amount of lubricating oil is supplied to the both ends of the bearing so that the conformability and the wear-resistant property of the bearing can be further enhanced.
FIG. 3 is a sectional view of a portion of a bearing metal according to an embodiement of the present invention;
FIG. 5 is a sectional view of a portion of a bearing metal according to another embodiement of the present invention;
FIG. 7 is a sectional view of a portion of a bearing metal according to a further embodiment of the present invention; and
FIG. 8 is a sectional view of a portion of a bearing metal according to a still further embodiment of the present invention.
Plain bearings for use in crank shafts of high-load diesel engines among internal combustion engines, in which two pieces of bearing metals 10a, 10b each having a semi-cylindrical shape are combined into an assembly having a cylindrical shape, will be described in detail hereinbelow.
Further, as shown in FIG. 2, each of the inner surfaces of the bearing metals 10a, 10b has a plurality of fine grooves 11 which are circumferentially spirally formed at a pitch of about 0.2 mm on the inner surface of the bearing metals between the axial both ends thereof, the fine grooves being parallel with one another and being arranged in the direction inclined at an angle of 3 degrees relative to the circumferencial direction perpendicular to the axial direction of the bearing. Further, the fine grooves 11 are formed either by boring work or by photo-etching. In case of forming the fine grooves 11 by boring work, a plurality of grooves 11 are formed by making a groove group including several grooves as a unit when processing the grooves and cutting the inner surface of the bearing with either one cutting tool having one or more cutting edges adapted to cut a plurality of grooves simultaneously, or a combination of a plurality of cutting tools. By forming the fine grooves 11 in this manner, in the axial direction of the bearing metal 10a, there are repeatedly formed a plurality of groups comprising two deep grooves 15, 15 each having a depth D of 7 micro meters (μm), and three consecutive shallow grooves 16, 16, 16 between the former grooves 15, 15, each of the latter grooves 16 having a depth d of 2 micro meters (μm) (Refer to FIG. 3).
As shown in FIG. 4, when the bearing metal 10a is fitted to the housing 2, and then put to use, during the initial running-in, not only a large amount of lubricating oil is retained in the deep grooves 15 and the shallow grooves 16 in the clearance between the inner surface of the plain bearing and the rotating shaft 3, but also each of side wall portions between the adjacent deep and shallow grooves 15, 16 and between the adjacent shallow grooves 16 functions as a bank which offers a resistance when the lubricating oil outflowing in the axial direction, and thus an inflow pressure when the lubricating oil flowing into a clearance between the inner surface of the bearing and the rotating shaft 3 increases, a stable thick oil film having a high oil pressure is formed between the bearing metals 10a, 10b and the rotating shaft 3. The anti-seizure property and the wear-resistant property of the bearing metals, which is liable to occur in particular during the initial running-in period, can be enhanced by virtue of the presence of such a stable thick oil film.
Even when the plain bearing is used during a long time, as a result, the shallow grooves 16 have been worn out by wear and tear, the lubricating oil is retained by the deep grooves 15, as shown by a dash and dotted line, at the same time a high inflow pressure when the lubricating oil flowing into a clearance between the inner surface of the bearing and the rotating shaft 3 is maintained so that the anti-seizure property and the wear-resistant property can be stably maintained without rapidly losing the effect obtained by the fine grooves 11. Further, the longitudinal sectional shapes of the deep grooves 15 and the shallow grooves 16 are not limited to the V shape as shown in FIG. 3, but may be carried out by appropriately modifying them as described hereinbelow.
FIG. 5 shows another embodiment of the plain bearing in which each of the portions between the adjacent grooves 15a and 16a and between the adjacent grooves 16a has a flat top surface to thereby increase the area which is subjected to the axial loading more than that of the embodiment as shown in FIG. 3, thus increasing the wear-resistant property of the bearing. Therefore, there is provided a plain bearing which is excellent in the wear-resistant property, particularly under a high load.
FIG. 6 shows still another embodiment of the plain bearing in which deep grooves 15b and shallow grooves 16b are formed on the inner surface of the bearing metal where each of the deep grooves 15b and the shallow grooves 16b has a flat bottom portion, and each of the portions which are left between the adjacent deep and shallow groove 15b, 16b and between the adjacent shallow grooves 16b, 16b has a flat top surface. In this embodiment, both the deep grooves 15b and the shallow grooves 16b are formed at intervals of the same pitch, and also a larger amount of lubricating oil can be retained in the deep grooves 15b and the shallow grooves 16b than that of the embodiment as shown in FIG. 3. Consequently, this embodiment may provide a plain bearing which is more suitable for a rotating shaft adapted to be rotated at a high speed than that of the embodiement as shown in FIG. 3. Further, until the shallow grooves 16b have been worn out by wear and tear, the area which is subjected to the axial loading remains unchanged, so that there is provided a plain bearing which is capable of maintaining a stable bearing property.
FIG. 7 shows a further embodiment of the plain bearing in which both of deep grooves 15c and shallow grooves 16c are formed by two circular surfaces. This embodiment enables a larger amount of lubricating oil to be retained in each of the shallow grooves 16c than that of the embodiment as shown in FIG. 3. Therefore, this embodiment may provide a plain bearing which is more suitable for a rotating shaft adapted to be rotated at a high speed than that of the embodiment as shown in FIG. 3.
FIG. 8 shows a still further embodiment of the plain bearing in which a number of deep grooves 15d are formed in the vicinity of the axial both ends 12, 13 of the inner surface of the bearing, while a number of shallow grooves 16d are formed in the axial central portion on the inner surface of the bearing. By increasing the number of the deep grooves 15d in the vicinity of the axial both ends 12, 13 which are liable to be subjected to a high local specific load caused by a partial contact of the rotating shaft during the running-in period of the bearing, the amount of the lubricating oil can be increased, thereby reducing the possible seizure and frictional wear of the axial both ends 12, 13 still more.
While a number of preferred embodiments of the present invention have been described hereinabove, it is possible to appropriately select the depth of the deep grooves and the shallow grooves and the pitches therebetween and thus combine them. Further, the number of the shallow grooves to be formed between deep groove and the next deep groove may also be selected suitably.
Moreover, in a case wherein an overlay made of a lead alloy, a tin alloy, an alminum alloy or a synthetic resin is formed in an uneven manner on the inner surface of the bearing, or in a case wherein various grooves having the similar section shape to those of the above-mentioned embodiments are formed on the inner surface of the bearing, the same effects as mentioned above may be obtained.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS4274684 *Mar 24, 1978Jun 23, 1981Richfield Steven EPermanently lubricated bearingUS5337374 *Jun 23, 1992Aug 9, 1994Matsushita Electric Industrial Co., Ltd.Disk drive apparatusGB524128A * Title not availableGB731435A * Title not availableGB1456504A * Title not availableGB2216199A * Title not availableJPS5973620A * Title not availableJPS6353922A * Title not availableJPS6362621U * Title not available* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS6354822 *May 16, 2000Mar 12, 2002Scroll TechnologiesOil retention in compressor slider blockUS6382838 *Sep 14, 2000May 7, 2002Daido Metal Company Ltd.Plain bearingUS6585419 *Nov 19, 2001Jul 1, 2003Daido Metal Company Ltd.Shaft bearing memberUS6736697Mar 26, 2001May 18, 2004Uranie InternationalMetal part having external surface with particular profile, polishing method for its production and device for implementing the methodUS7572060Mar 11, 2005Aug 11, 2009Daido Metal Company Ltd.Sliding bearingUS7836601Jun 8, 2005Nov 23, 2010Aly El-ShafeiMethods of controlling the instability in fluid film bearingsUS8382376 *Dec 24, 2009Feb 26, 2013Daido Metal Company Ltd.Split-type sliding bearing for crankshaft in internal combustion engineUS8419285 *Nov 12, 2009Apr 16, 2013Daido Metal Company Ltd.Sliding bearing for internal combustion engine and sliding bearing deviceUS8500334 *Aug 25, 2009Aug 6, 2013Mahle International GmbhSlide bearingUS8708567 *Dec 8, 2010Apr 29, 2014Doosan Infracore Co., Ltd.Sliding bearing and sliding bearing assemblyUS8961018 *Aug 20, 2013Feb 24, 2015Daido Metal Company Ltd.Connecting rod bearingUS20050201647 *Mar 11, 2005Sep 15, 2005Daido Metal Company Ltd.Half plain bearingUS20050213859 *Mar 11, 2005Sep 29, 2005Daido Metal Company Ltd.Sliding bearingUS20050275300 *Jun 8, 2005Dec 15, 2005Aly El-ShafeiMethods of controlling the instability in fluid film bearingsUS20080224556 *May 16, 2008Sep 18, 2008Aly El-ShafeiMethods of controlling the instability in fluid film bearingsUS20090092796 *Feb 1, 2007Apr 9, 2009Yoshinori IshidaSliding member and method for manufacturing the sameUS20100054639 *Aug 25, 2009Mar 4, 2010Wolfgang IsslerSlide bearingUS20100119181 *Nov 12, 2009May 13, 2010Daido Metal Company Ltd.Sliding bearing for internal combustion engine and sliding bearing deviceUS20100166350 *Dec 24, 2009Jul 1, 2010Daido Metal Company Ltd.Split-type sliding bearing for crankshaft in internal combustion engine and split-type sliding bearing deviceUS20120164016 *Dec 14, 2011Jun 28, 2012Robert Bosch GmbhRinsing Arrangement for Tribological Contact Area and Rotary Vane Pump with such an ArrangementUS20120328224 *Dec 8, 2010Dec 27, 2012Doosan Infracore Co., Ltd.Sliding bearing and sliding bearing assemblyUS20140020622 *Mar 12, 2012Jan 23, 2014Nisshin Steel Co., Ltd.Roll for molten metal plating bath and method for manufacturing the sameUS20140064644 *Aug 20, 2013Mar 6, 2014Daido Metal Company Ltd.Connecting rod bearingCN103128654A *Feb 27, 2013Jun 5, 2013云南铝业股份有限公司Heavy-duty grinder pillowCN103128654B *Feb 27, 2013Dec 23, 2015云南铝业股份有限公司一种重型磨床托瓦CN103201530A *Oct 28, 2011Jul 10, 2013大丰工业株式会社Slide bearingCN103201530B *Oct 28, 2011Sep 9, 2015大丰工业株式会社滑动轴承CN103906934A *Feb 28, 2013Jul 2, 2014大丰工业株式会社Slide bearingCN103906934B *Feb 28, 2013Oct 19, 2016大丰工业株式会社滑动轴承DE102005011371B4 *Mar 11, 2005Aug 30, 2007Daido Metal Co., Ltd.GleitlagerhälfteDE102005011372B4 *Mar 11, 2005Feb 8, 2007Daido Metal Co., Ltd.GleitlagerDE102006050246A1 *Oct 13, 2006Apr 17, 2008Ks Gleitlager GmbhHydrodynamisches GleitlagerEP1911986A1 *Sep 26, 2007Apr 16, 2008KS Gleitlager GmbHHydrodynamic bearing* Cited by examinerClassifications U.S. Classification384/322, 384/291, 384/283, 384/625International ClassificationF16C33/10, F16C33/04, F16C17/02, F16C9/00Cooperative ClassificationF16C2240/42, F16C33/103, F16C33/1065, F16C9/00, F16C17/026European ClassificationF16C17/02G, F16C33/10L5D, F16C9/00Legal EventsDateCodeEventDescriptionJun 25, 1998ASAssignmentOwner name: DAIDO METAL COMPANY LTD., JAPANFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ONO, AKIRA;MATSUMURA, HIDEYUMI;NIWA, MASAYUKI;AND OTHERS;REEL/FRAME:009273/0936Effective date: 19980302Sep 18, 2001CCCertificate of correctionJan 8, 2004FPAYFee paymentYear of fee payment: 4Oct 23, 2007FPAYFee paymentYear of fee payment: 8Nov 9, 2011FPAYFee paymentYear of fee payment: 12RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services