Source: http://www.google.com/patents/US20040251551?dq=5572193
Timestamp: 2015-07-04 01:55:06
Document Index: 123958240

Matched Legal Cases: ['Application No. 2003', 'art 11', 'art 111', 'art 411', 'art 807', 'art 807', 'art 807']

Patent US20040251551 - Phase changeable memory devices including carbon nano tubes and methods for ... - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inAdvanced Patent SearchPatentsAn integrated circuit phase changeable memory device includes an integrated circuit substrate, a first electrode on the integrated circuit substrate, and a second electrode on the integrated circuit substrate and spaced apart from the first electrode. A carbon nano tube and a phase changeable layer are...http://www.google.com/patents/US20040251551?utm_source=gb-gplus-sharePatent US20040251551 - Phase changeable memory devices including carbon nano tubes and methods for forming the sameAdvanced Patent SearchPublication numberUS20040251551 A1Publication typeApplicationApplication numberUS 10/827,639Publication dateDec 16, 2004Filing dateApr 19, 2004Priority dateJun 11, 2003Also published asUS7378701Publication number10827639, 827639, US 2004/0251551 A1, US 2004/251551 A1, US 20040251551 A1, US 20040251551A1, US 2004251551 A1, US 2004251551A1, US-A1-20040251551, US-A1-2004251551, US2004/0251551A1, US2004/251551A1, US20040251551 A1, US20040251551A1, US2004251551 A1, US2004251551A1InventorsHorii HidekiOriginal AssigneeHorii HidekiExport CitationBiBTeX, EndNote, RefManReferenced by (52), Classifications (24), Legal Events (2) External Links: USPTO, USPTO Assignment, EspacenetPhase changeable memory devices including carbon nano tubes and methods for forming the same
US 20040251551 A1Abstract
An integrated circuit phase changeable memory device includes an integrated circuit substrate, a first electrode on the integrated circuit substrate, and a second electrode on the integrated circuit substrate and spaced apart from the first electrode. A carbon nano tube and a phase changeable layer are serially disposed between the first and second electrodes. An insulating layer can include a contact hole and the carbon nano tube may be provided in the contact hole. Moreover, the phase changeable layer also may be provided at least partially in the contact hole. A layer also may be provided at least partially surrounding the carbon nano tube in the contact hole. Related fabrication methods also are provided Images(11) Claims(30)
What is claimed is: 1. An integrated circuit phase changeable memory device comprising: an integrated circuit substrate; a first electrode on the integrated circuit substrate; a second electrode on the integrated circuit substrate and spaced apart from the first electrode; and a carbon nano tube and a phase changeable layer serially disposed between the first and second electrodes. 2. The device of claim 1 further comprising an insulating layer including a contact hole therein, wherein the carbon nano tube is in the contact hole. 3. The device of claim 2 wherein the phase changeable layer also is at least partially in the contact hole. 4. The device of claim 2 further comprising a layer at least partially surrounding the carbon nano tube in the contact hole. 5. An integrated circuit phase changeable memory device, comprising: a lower conductive pattern disposed on an integrated circuit substrate; an insulating layer disposed on the substrate and having a contact hole exposing a surface of the lower conductive pattern; a carbon nano tube on the exposed surface of the lower conductive pattern in the contact hole; a phase changeable material pattern disposed on the carbon nano tube and on the insulating layer remote from the lower conductive pattern; and an upper conductive pattern disposed on the phase changeable material pattern remote from the carbon nano tube. 6. The device of claim 5, wherein a diameter of the carbon nano tube is smaller than a diameter of the contact hole, wherein a supporting insulating layer is interposed between the carbon nano tube and sidewalls of the insulating layer that defines the contact hole. 7. The device of claim 6, wherein the phase changeable material pattern comprises Te and/or Se, and Ge, Sb, Bi, Pb, Sn, Ag, As, S, Si, P, O and/or N. 8. The device of claim 6, wherein the supporting insulating layer comprises a porous insulating layer. 9. The device of claim 5, wherein the lower conductive pattern comprises cobalt, nickel, iron, chrome, ruthenium, osmium, iridium, platinum, palladium, silver, gold, titanium, zirconium, niobium, tantalum, tungsten, molybdenum, tungsten silicide, cobalt silicide, nickel silicide and/or titanium tungsten. 10. The device of claim 5, wherein the carbon nano tube is recessed in the insulating layer, and wherein the phase changeable material pattern extends in the contact hole and on the insulating layer outside the contact hole. 11. The device of claim 10, wherein a diameter of the carbon nano tube is smaller than a diameter of the contact hole, and wherein a supporting insulating layer is interposed between sidewalls of the insulating layer that define the contact hole and the carbon nano tube and between the phase changeable material pattern extending into the contact hole and the sidewalls of the insulating layer. 12. The device of claim 11, wherein the supporting insulating layer comprises a porous insulating layer. 13. The device of claim 10, further comprising insulating spacers between the phase changeable material pattern extending into the contact hole and sidewalls of the insulating layer that define the contact hole. 14. The device of claim 11, wherein the lower conductive pattern comprises cobalt, nickel, iron, chrome, ruthenium, osmium, iridium, platinum, palladium, silver, gold, titanium, zirconium, niobium, tantalum, tungsten, molybdenum, tungsten silicide, cobalt silicide, nickel silicide and/or titanium tungsten. 15. An integrated circuit phase changeable memory device comprising: a lower conductive pattern disposed on an integrated circuit substrate; an insulating layer disposed on the substrate and having a contact hole exposing the lower conductive pattern; a carbon nano tube that extends from the lower conductive pattern in the contact hole, wherein a diameter of the carbon nano tube is smaller than a diameter of the contact hole; a supporting insulating layer in the contact hole between the carbon nano tube and the insulating layer; a phase changeable material pattern disposed on the supporting insulating layer and on the carbon nano tube in the contact hole, and on the insulating layer outside the contact hole; and an upper conductive pattern disposed on the phase changeable material pattern. 16. The device of claim 15, wherein the supporting insulating layer comprises a porous insulating layer. 17. A method for forming an integrated circuit phase changeable memory device, comprising: forming a lower conductive pattern on a substrate; forming an insulating layer on the substrate, the insulating layer having a contact hole exposing the lower conductive pattern; forming a carbon nano tube on the lower conductive pattern exposed by the contact hole, the carbon nano tube being flush with or recessed in the insulating layer; and forming a phase changeable material pattern and an upper conductive pattern on the nano tube and on the insulating layer outside the nano tube. 18. The method of claim 17, wherein the forming of the carbon nano tube comprises: growing the carbon nano tube to be recessed in the insulating layer; and wherein the phase changeable material pattern is formed to extend into the contact hole. 19. The method of claim 18, further comprising forming insulating spacers on a sidewall of the contact hole after the growing of the carbon nano tube to be recessed in the insulating layer. 20. The method of claim 17, wherein the forming of the carbon nano tube comprises: growing the carbon nano tube on the lower conductive pattern to protrude beyond the insulating layer; forming a supporting insulating layer on the insulating layer to cover the carbon nano tube that protrudes beyond the insulating layer; and planarizing the supporting insulating layer and the carbon nano tube until the insulating layer is exposed. 21. The method of claim 20, wherein the following is performed after the planarizing: selectively etching the carbon nano tube to be recessed in the insulating layer; wherein the phase changeable material pattern extends into the contact hole. 22. The method of claim 20, wherein the carbon nano tube is grown to be smaller than the contact hole in diameter, and wherein the supporting insulating layer comprises a porous insulating layer and further extends into the residual contact hole to at least partially surround the carbon nano tube. 23. The method of claim 22, wherein the porous insulating layer is formed by stacking an SOG layer and treating the SOG layer thermally. 24. The method of claim 17, wherein the forming the carbon nano tube comprises: growing a carbon nano tube from the lower conductive pattern to be recessed in the contact hole and to have a diameter smaller than a diameter of the contact hole; forming a supporting insulating layer on the insulating layer to at least partially surround the carbon nano tube in the contact hole; and selectively etching back the supporting insulating layer to expose the carbon nano tube. 25. The method of claim 24, wherein the supporting insulating layer is formed by stacking an SOG layer and treating the SOG layer thermally. 26. The method of claim 17: wherein the lower conductive pattern comprises cobalt, nickel, iron, chrome, ruthenium, osmium, iridium, palladium, silver, gold, titanium, zirconium, niobium, tantalum, tungsten, molybdenum, tungsten silicide, cobalt silicide, nickel silicide and/or titanium tungsten; wherein the phase changeable material pattern comprises Te and/or Se, and Ge, Sb, Bi, Pb, Sn, Ag, As, S, Si, P, O and/or N; and wherein the upper conductive pattern comprises titanium nitride, tantalum nitride, molybdenum nitride, niobium nitride, titanium silicon nitride, titanium aluminum nitride, titanium boron nitride, zirconium silicon nitride, tungsten silicon nitride, tungsten boron nitride, zirconium aluminum nitride, molybdenum silicon nitride, molybdenum aluminum nitride, tantalum silicon nitride, tantalum aluminum nitride, titanium oxide nitride, titanium aluminum oxide nitride, tungsten oxide nitride, tantalum oxide nitride, titanium, tantalum, titanium aluminum, zirconium, hafnium, molybdenum, tungsten, copper, aluminum, aluminum-copper alloy, aluminum-copper-silicon alloy, titanium tungsten and/or tungsten silicide. 27. A method for forming an integrated circuit phase changeable memory device, comprising: forming a lower conductive pattern on an integrated circuit substrate; forming an insulating layer on the substrate, the insulating layer having a contact hole exposing the lower conductive pattern; growing a carbon nano tube on the lower conductive pattern exposed by the contact hole; forming a supporting insulating layer on the insulating layer and the carbon nano tube; planarizing the supporting insulating layer to expose the carbon nano tube; and forming a phase changeable material pattern and an upper conductive pattern on the carbon nano tube that is exposed. 28. The method of claim 27, further comprising selectively etching back the carbon nano tube to be recessed in the supporting insulating layer after the planarizing is performed. 29. The method of claim 27, wherein a diameter of the carbon nano tube is smaller than a diameter of the contact hole. 30. The method of claim 27, wherein the supporting insulating layer is formed by stacking an SOG layer and treating the SOG layer thermally.
RELATED APPLICATION [0001] This application claims the benefit of Korean Patent Application No. 2003-0037678, filed Jun. 11, 2003, the disclosure of which is hereby incorporated herein by reference in its entirety as if set forth fully herein. FIELD OF THE INVENTION [0002] The present invention relates to integrated circuit memory devices and more specifically to phase changeable memory devices and methods for forming the same. BACKGROUND OF THE INVENTION [0003] Integrated circuit (semiconductor) memory devices can be roughly categorized into volatile memory devices and nonvolatile memory devices according to whether the semiconductor memory devices maintain data when a power supply is cut off. The volatile memory devices may include, for example, DRAM devices and SRAM devices and the nonvolatile memory devices may include, for example, flash memory devices. These conventional memory devices may indicate a logic value “0” or a logic value “1” according to the relative presence or absence of stored charges. [0004] Recently, phase changeable memory devices have been proposed. A phase changeable memory device uses phase changeable materials that change their crystalline states depending on a resistive heating by a current pulse. Conventionally, chalcogenide compounds (GST) including germanium (Ge), antimony (Sb) and/or tellurium (Te) may be used as a phase changeable material. [0005] An amorphous phase changeable material has relatively high electric resistance, and the electric resistance decreases as the amorphous phase changeable material changes gradually into a crystalline state. Since the resistance can vary according to the crystalline states, logic information can be determined by sensing a difference between the resistances. The phase changeable material layer can contact a conductive plug that passes through an insulating layer, and may be provided with heat (Joule heat) from the conductive plug and/or a heater plug. The conductive plug is conventionally formed of conductive nitride materials such as titanium nitride. To embody a phase changeable memory device having low power consumption, the diameter of the conductive plug may be reduced. [0006] However, if the conductive plug is formed of titanium nitride, it may be difficult to reduce the diameter as much as may be desirable. In particular, a heater plug having about 40 nm diameter may not endure a current density of about 108 A/cm2 or more under a write current of about 1 mA, because the titanium nitride may have weak tolerance with respect to this current density. As a result, if a conventional titanium nitride heater plug is used, the diameter of the heater plug may not be reducible under about 40 nm. It therefore may be difficult to provide phase changeable memory devices having a desirably high integration density and/or a desirably low power consumption. SUMMARY OF THE INVENTION [0007] Some embodiments of the present invention provide integrated circuit phase changeable memory devices that include an integrated circuit substrate, a first electrode on the integrated circuit substrate, and a second electrode on the integrated circuit substrate and spaced apart from the first electrode. A carbon nano tube and a phase changeable layer are serially disposed between the first and second electrodes. The carbon nano tube can have a relatively high tolerance with respect to current density compared to conventional titanium nitride and can thereby enable highly integrated devices that can consume relatively low power, according to some embodiments of the present invention. In some embodiments, the insulating layer also includes a contact hole therein, and the carbon nano tube is in the contact hole. In other embodiments, the phase changeable layer also is at least partially in the contact hole. In still other embodiments, a layer is provided that at least partially surrounds the carbon nano tube in the contact hole. [0008] In other embodiments of the present invention, a phase changeable memory device includes a lower conductive pattern disposed on a substrate and an insulating layer having a contact hole exposing the lower conductive pattern. A carbon nano tube is provided on the exposed surface of the lower conductive pattern in the contact hole. The nano tube is recessed in or flush with the insulating layer. A phase changeable material pattern is disposed on the insulating layer and on the carbon nano tube, remote from the lower conductive pattern. An upper conductive pattern is disposed on the phase changeable material pattern, remote from the carbon nano tube. [0009] In some embodiments of the present invention, the top surface of the carbon nano tube may be recessed in the insulating layer. In some embodiments, the phase changeable material pattern extends into the contact hole. In some embodiments, the phase changeable material pattern fills an upper portion of the contact hole such that a contact region between the carbon nano tube and the phase changeable material pattern is positioned within the contact hole. As a result, a current for a device operation can be reduced, in some embodiments. [0010] In other embodiments of the present invention, a diameter of the carbon nano tube is smaller than a diameter of the contact hole, and a supporting insulating layer is provided in, or fills, a space between the carbon nano tube and the insulating layer that defines the contact hole. The supporting insulating layer may be a porous insulating layer and, in some embodiments, may have relatively good adiabatic property. The porous supporting insulating layer may at least partially surround the nano tube in the contact hole and the phase changeable material pattern in the contact hole. A low-power consumption device may thereby be provided in some embodiments. In some embodiments, the porous supporting insulating layer may comprise spin on glass (SOG). In addition, the porous supporting insulating layer may be formed by spin-coating and thermally treating a silicate base spin on dielectric (SOD) layer. [0011] In some embodiments, the phase changeable material pattern may comprise Te and/or Se, and Ge, Sb, Bi, Pb, Sn, Ag, As, S, Si, P, O and/or N. [0012] In some embodiments of the present invention, the lower conductive pattern comprises cobalt, nickel, iron, chrome, ruthenium, osmium, iridium, platinum, palladium, silver, gold, titanium, zirconium, niobium, tantalum, tungsten, molybdenum, tungsten silicide, cobalt silicide, nickel silicide and/or titanium tungsten. [0013] In some embodiments of the present invention, the upper conductive pattern comprises titanium nitride, tantalum nitride, molybdenum nitride, niobium nitride, titanium silicon nitride, titanium aluminum nitride, titanium boron nitride, zirconium silicon nitride, tungsten silicon nitride, tungsten boron nitride, zirconium aluminum nitride, molybdenum silicon nitride, molybdenum aluminum nitride, tantalum silicon nitride, tantalum aluminum nitride, titanium oxide nitride, titanium aluminum oxide nitride, tungsten oxide nitride, tantalum oxide nitride, titanium, tantalum, titanium aluminum, zirconium, hafnium, molybdenum, tungsten, copper, aluminum, aluminum-copper alloy, aluminum-copper-silicon alloy, titanium tungsten and/or tungsten silicide. [0014] In some embodiments of the present invention, a method for forming a phase changeable memory device includes the following. A lower conductive pattern is formed on a substrate. An insulating layer having a contact hole is formed on the substrate. The contact hole exposes the lower conductive pattern. A carbon nano tube is formed on the lower conductive pattern exposed by the contact hole and is flush with or recessed in the insulating layer. A phase changeable material pattern and an upper conductive pattern are formed on the nano tube and on the insulating layer outside the nano tube. [0015] In some embodiments of the present invention, the forming of the carbon nano tube flush with or recessed in the insulating layer, includes growing the carbon nano tube on the lower conductive pattern to be recessed in the insulating layer. In these embodiments, the phase changeable material pattern can extend into the contact hole. In some of these embodiments, insulating spacers may be further formed on sidewalls of the contact hole. [0016] In some embodiments of the present invention, the forming of the carbon nano tube flush with or recessed in the insulating layer on the lower conductive pattern exposed by the contact hole, comprises growing a carbon nano tube on the lower conductive pattern to protrude beyond the insulating layer, forming a supporting insulating layer on the insulating layer to cover a carbon nano tube that protrudes from the insulating layer, and planarizing the supporting insulating layer and the carbon nano tube until the insulating layer is exposed. In some embodiments, after the planarization process, a selective etch back process is further performed to the carbon nano tube to be recessed in the insulating layer. In these embodiments, the phase changeable material pattern can extend into the contact hole. [0017] In some embodiments of the present invention, the carbon nano tube is grown to be smaller than the contact hole in diameter, and the supporting insulating layer is provided inside of the residual contact hole to at least partially surround the outer sidewall of the carbon nano tube. The supporting insulating layer may comprise a porous insulating layer. For example, the supporting layer may be formed by depositing an SOG layer and performing heat treatment. The supporting layer may be formed by spin coating a silicate based spin on dielectric (SOD) and thermally treating the SOD layer. [0018] In some embodiments, the forming the carbon nano tube to be flush with or recessed in the insulating layer includes growing a carbon nano tube on the lower conductive pattern to be flush with or recessed in the insulating layer and to have a diameter smaller than a diameter of the contact hole, forming a supporting insulating layer on the insulating layer to at least partially surround the outer sidewall of the carbon nano tube by, in some embodiments, filling the contact hole, and selectively etching back the supporting insulating layer to expose the carbon nano tube. The supporting insulating layer may comprise a porous insulating layer. The porous insulating layer may be formed by depositing an SOG layer and treating the SOG layer thermally. In other embodiments, the porous insulating layer may be formed by spin coating an SOD layer and treating the SOD layer thermally. [0019] In some embodiments, the carbon nano tube may be formed using a thermal chemical vapor deposition technique, a plasma chemical vapor deposition technique, an electron cyclotron resonance (ECR) chemical vapor deposition technique, an electric discharge technique, a laser deposition technique, and/or other conventional techniques. [0020] In some embodiments, the lower conductive pattern may comprise cobalt, nickel, iron, chrome, ruthenium, osmium, iridium, palladium, silver, gold, titanium, zirconium, niobium, tantalum, tungsten, molybdenum, tungsten silicide, cobalt silicide, nickel silicide and/or titanium tungsten. [0021] In some embodiments, the phase changeable material pattern may comprise Te and/or Se and Ge, Sb, Bi, Pb, Sn, Ag, As, S, Si, P, O and/or N. [0022] In some embodiments, the upper conductive pattern may comprise titanium nitride, tantalum nitride, molybdenum nitride, niobium nitride, titanium silicon nitride, titanium aluminum nitride, titanium boron nitride, zirconium silicon nitride, tungsten silicon nitride, tungsten boron nitride, zirconium aluminum nitride, molybdenum silicon nitride, molybdenum aluminum nitride, tantalum silicon nitride, tantalum aluminum nitride, titanium oxide nitride, titanium aluminum oxide nitride, tungsten oxide nitride, tantalum oxide nitride, titanium, tantalum, titanium aluminum, zirconium, hafnium, molybdenum, tungsten, copper, aluminum, aluminum-copper alloy, aluminum-copper-silicon alloy, titanium tungsten and/or tungsten silicide.
BRIEF DESCRIPTION OF THE DRAWINGS [0023]FIG. 1 is a cross-sectional view illustrating a phase-changeable memory device according to some embodiments of the present invention. [0024]FIG. 2 is a cross-sectional view illustrating a phase-changeable memory device according to other embodiments of the present invention. [0025]FIG. 3 is a cross-sectional view illustrating a phase changeable memory device according to still other embodiments of the present invention. [0026]FIGS. 4 through 7 are cross-sectional views illustrating methods for forming a phase changeable memory device of FIG. 1 in the order of a fabricating process, according to embodiments of the present invention. [0027]FIGS. 8 through 11 are cross-sectional views illustrating methods for forming a phase changeable memory device of FIG. 1 in the order of a fabricating process according to other embodiments of the present invention. [0028]FIGS. 12 through 15 are cross-sectional views illustrating methods for fabricating a phase changeable memory device of FIG. 2 in the order of a fabricating process according to embodiments of the present invention. [0029]FIGS. 16 through 19 are cross-sectional views illustrating methods for fabricating a phase changeable memory device of FIG. 3 in the order of a fabricating process according to embodiments of the present invention. [0030]FIG. 20 is a cross-sectional view illustrating a phase changeable memory device according to still other embodiments of the present invention.
DETAILED DESCRIPTION [0031] The present invention now will be described more fully hereinafter with reference to the accompanying drawings, in which embodiments of the invention are shown. This invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. In the drawings, the size and relative sizes of layers and regions may be exaggerated for clarity. Like numbers refer to like elements throughout. [0032] It will be understood that when an element such as a layer, region or substrate is referred to as being “on” another element, it can be directly on the other element or intervening elements may also be present. Furthermore, relative terms such as “lower” or “upper” may be used herein to describe a relationship of one layer or region to another layer or region relative to a substrate or base layer as illustrated in the figures. It will be understood that these terms are intended to encompass different orientations of the device in addition to the orientation depicted in the figures. Finally, the term “directly” means that there are no intervening elements. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. [0033] It will be understood that, although the terms first, second, etc. may be used herein to describe various embodiments, elements, components, regions, layers and/or sections, these embodiments, elements, components, regions, layers and/or sections should not be limited by these terms. These terms are only used to distinguish one embodiment, element, component, region, layer or section from another region, layer or section. Thus, a first embodiment, region, layer or section discussed below could be termed a second embodiment, region, layer or section, and, similarly, a second embodiment, region, layer or section could be termed a first embodiment, region, layer or section without departing from the teachings of the present invention. [0034] In addition, a liner layer or a formation of a liner layer means a layer that is formed to have relatively uniform thickness along at least part of an outline of a lower structure or a formation of the same. Conformal formation of any material layer has the same meaning. [0035]FIG. 1 is a schematic cross-sectional view illustrating a phase changeable memory device according to embodiments of the present invention. Referring to FIG. 1, a lower conductive pattern 103 a is formed on an integrated circuit (semiconductor) substrate 101. An insulating layer 105 is formed on the substrate 101 to surround the lower conductive pattern 103 a. A contact hole 107 is defined in the insulating layer 105 to expose the lower conductive pattern 103 a. The insulating layer 105 may comprise, for example, silicon oxide. [0036] A carbon nano tube 109 r is provided in the contact hole 107 and, in some embodiments, fills a portion of the contact hole. The carbon nano tube 109 r contacts the lower conductive pattern 103 a and the carbon nano tube 109 r is recessed in insulating layer 105. [0037] A phase changeable material pattern 111 a is disposed on the insulating layer 105 and, in some embodiments, fills a remaining portion of the contact hole 107, that is, an upper portion of the contact hole 107. An upper conductive pattern 113 a is disposed on the phase changeable material pattern 111 a. In FIG. 1, since the carbon nano tube 109 r fills a portion of the contact hole 107, the phase changeable material pattern 111 a has an extension part 11 ae that extends in the contact hole 107. As a result, a contact region between the phase changeable material pattern 111 a and the carbon nano tube 109 r is located in the contact hole 107. Accordingly, for example, if a current path is formed between the lower conductive pattern 103 a and the upper conductive pattern 113 a to provide a current for the phase changeable material pattern 111 a through the carbon nano tube 109 r during a program operation, the current can be densely concentrated in the extension part of the phase changeable material pattern 111 ae in the contact hole 107. Therefore, in some embodiments, a volume of a program region can be reduced, which can reduce the current for phase change because the portion of the phase changeable material pattern 111 a in which crystalline structure varies (i.e., the program region) 111 ap is formed at the extension part 111 ae within the contact hole 107. [0038] Embodiments of FIG. 1 also may be regarded as providing an integrated circuit phase changeable memory device that includes an integrated circuit substrate 101, a first electrode 103 a on the integrated circuit substrate, a second electrode 113 a on the integrated circuit substrate and spaced apart from the first electrode 103 a, and a carbon nano tube 109 r and a phase changeable layer 111 a serially disposed between the first and second electrodes 103 a, 113 a, respectively. FIGS. 2-20 also illustrate other embodiments of these integrated circuit phase changeable memory devices. [0039] The lower conductive pattern 103 a may comprise a metallic material capable of serving as a catalyzer for growing the carbon nano tube. For instance, the lower conductive pattern 103 a may include cobalt (Co), nickel (Ni), iron (Fe), chrome (Cr), ruthenium (Ru), osmium (Os), iridium (Ir), platinum (Pt), palladium (Pd), silver (Ag), gold (Au), titanium (Ti), zirconium (Zr), niobium (Nb), tantalum (Ta), tungsten (Tw), molybdenum (Mo), tungsten silicide (WSi), cobalt silicide (CoSi), nickel silicide (NiSi) and/or titanium tungsten (TiW). [0040] The phase changeable material pattern 111 a may comprise tellurium (Te) and/or selenium (Se), and Ge, Sb, Bi, Pb, Sn, Ag, As, S, Si, P, O and/or N. [0041] The upper conductive pattern may comprise titanium nitride (TiN), tantalum nitride (TaN), molybdenum nitride (MoN), niobium nitride (NbN), titanium silicon nitride (TiSiN), titanium aluminum nitride (TiAlN), titanium boron nitride (TiBN), zirconium silicon nitride (ZrSiN), tungsten silicon nitride (WSiN), tungsten boron nitride (WBN), zirconium aluminum nitride (ZrAlN), molybdenum silicon nitride (MoSiN), molybdenum aluminum nitride (MoAlN), tantalum silicon nitride (TaSiN), tantalum aluminum nitride (TaAlN), titanium oxide nitride (TiON), titanium aluminum oxide nitride (TiAlON), tungsten oxide nitride (WON), tantalum oxide nitride (TaON), titanium (Ti), tantalum (Ta), titanium aluminum (TiAl), zirconium (Zr), hafnium (Hf), molybdenum (Mo), tungsten (W), copper (Cu), aluminum (Al), aluminum-copper (Al—Cu), aluminum-copper-silicon (Al—Cu—Si), titanium tungsten (TiW) and/or tungsten silicide (WSi). [0042] The carbon nano tube can have relatively high tolerance with respect to a current density compared to titanium nitride, such that the carbon nano tube having a diameter of about 10 nm or less may endure a current density of about 109 A/cm2 under a current of about 1 mA. Therefore, devices according to some embodiments of the invention can be embodied to have characteristics of high-integration density and/or low power consumption. [0043]FIG. 2 is a schematic cross-sectional view illustrating a phase-changeable memory device according to other embodiments of the present invention. Referring to FIG. 2, the 200 series of elements according to these embodiments is similar to the 100 series of elements of the device according to FIG. 1, except for the following two respects. One is that the device of FIG. 2 has a carbon nano tube 209 r, the diameter of which is smaller than a diameter of the contact hole 207. The other is that a supporting insulating layer 215 a is interposed between the carbon nano tube 209 r and sidewalls of the insulating layer 205 that defines the contact hole 207. Thus, the above description will not be repeated in further detail. [0044] The supporting insulating layer 215 a at least partially surrounds the carbon nano tube 209 r in the contact hole 207, and can physically protect and can block heat dissipation as will be explained herein. The supporting insulating layer 215 a supports the carbon nano tube 209 r physically, such that the carbon nano tube 209 r may be formed to have a diameter as small as desirable. [0045] In this embodiment, a contact region between the phase changeable pattern 211 a and the carbon nano tube 209 r can be smaller than embodiments of FIG. 1. [0046] The supporting insulating layer 215 a may insulate heat effectively. For example, the supporting insulating layer 215 a may comprise a porous insulating layer. One example of a porous insulating layer is a SOG layer. Alternatively, the porous insulating layer may be formed by a spin-coating and a thermal treating of silicate base spin on dielectric (SOD). [0047] The supporting insulating layer 215 a may physically support and may also reduce or prevent the carbon nano tube 209 r from loosing heat. Therefore, the current in a device operation may be reduced, in some embodiments. [0048]FIG. 3 is a schematic cross-sectional view illustrating a phase-changeable memory device according to still other embodiments. Referring to FIG. 3, the 300 series of elements of FIG. 3 has the same structure as the 200 series of elements of FIG. 2 except that a carbon nano tube is as tall as (flush with) the contact hole 307 and the insulating layer 305. Moreover, in some embodiments, a diameter of the carbon nano tube 309 is smaller than that of the contact hole 307, such that a supporting insulating layer 312 a is in, and, in some embodiments, fills, a contact region between sidewalls of the insulating layer that defines the contact hole 307 and the carbon nano tube 309. In these embodiments, the contact region between the phase changeable pattern and the carbon nano tube can decrease compared to devices according to the FIG. 1. In addition, the supporting insulating layer 315 a can comprise a porous insulating layer that can have a good adiabatic property. Therefore, the supporting insulating layer 315 a can allow devices to have a relatively low power consumption. [0049] A phase changeable material pattern 311 a is provided on the insulating layer 305, on the carbon nano tube 309 and on the supporting insulating layer 307, and an upper conductive pattern 313 a is provided on the phase changeable material pattern 311 a remote from the carbon nano tube 309. [0050] It will be understood by those skilled in the art that insulating spacers (not shown in the drawings) may be further formed on the sidewalls of the contact hole in case of the devices explained above. In other embodiments, a layer at least partially surrounding the carbon nano tube in the contact hole may be embodied by the supporting insulating layer and/or a spacer. [0051] Methods for fabricating the devices explained above will be described herein. For brevity, explanations for identical fabrication steps will not be further repeated. [0052]FIGS. 4 through 7 are cross-sectional views illustrating methods for fabricating a device of FIG. 1 in the order of principal fabricating steps. Referring to FIG. 4, a substrate 401 is prepared. The substrate 401 can be a semiconductor substrate formed of silicon, silicon-germanium, etc. A lower conductive pattern 403 a is formed on the substrate 401. Not illustrated in the drawings, a device isolation process may be performed using a conventional fabricating process before forming the lower conductive pattern 403, and a transistor including a gate, a source and a drain may be formed. The lower conductive pattern 403 a may be electrically connected to a source of the transistor, for example. In addition, when the lower conductive pattern 403 a is formed, a lower metal interconnection may be formed to electrically connect the drain of the transistor at the same time. [0053] The lower conductive pattern 403 a may comprise a metallic material serving as a catalyzer for growing the carbon nano tube. For instance, the lower conductive pattern 403 a may comprise cobalt, nickel, iron, chrome, ruthenium, osmium, iridium, platinum, palladium, silver, gold, titanium, zirconium, niobium, tantalum, tungsten, molybdenum, tungsten silicide, cobalt silicide, nickel silicide and/or titanium tungsten. [0054] Still referring to FIG. 4, an insulating layer 405 is formed on the substrate 401 to cover the lower conductive pattern 403 a. The insulating layer 405 may comprise silicon oxide formed by a chemical vapor deposition technique. [0055] Referring to FIG. 5, the insulating layer 405 is patterned to form a contact hole 407 exposing the lower conductive pattern 403 a. The contact hole 407 is defined by sidewalls 405 s of the etched insulating layer 405 and exposed top surface of the lower conductive pattern 403 a. [0056] Referring to FIG. 6, a carbon nano tube 409 r is grown up from a surface of the lower conductive pattern 403 a exposed by the contact hole 407. By controlling process time, a growing height of the carbon nano tube 409 r can be determined. The carbon nano tube 409 r may be formed by a thermal chemical vapor deposition technique, a plasma chemical vapor deposition technique, an electron cyclotron resonance (ECR) chemical vapor deposition technique, an electric discharge technique, a laser deposition technique and/or other conventional technique. [0057] For example, in case of the chemical vapor deposition technique, a carbon source may include C2H4, CH4, CO, CO2 an alcohol such as methanol and/or carbon halogenide such as C4F6. In addition, a reaction gas may include nitrogen, ammonia and/or hydrogen and a carrier gas may include inert gas such as argon, helium, neon, etc. [0058] In these embodiments, the carbon nano tube 409 r grows to the height at which the upper surface 409 t of the carbon nano tube 409 r is lower than the height of the insulating layer 405. In other words, the carbon nano tube 409 r is recessed in the insulating layer 405. This can be achieved by controlling a process time. Therefore, the carbon nano tube 409 r may fill a portion of the contact hole 407. [0059] In some embodiments, insulating spacers may be further formed on sidewalls or the contact hole 407 before the carbon nano tube 409 r is formed. [0060] Referring to FIG. 7, a phase changeable material layer 411 and an upper conductive layer 413 are sequentially formed in a residual contact hole 407 r (FIG. 6) and on the insulating layer 405. In this case, the phase changeable material layer 411 may include an extension part 411 ae that extends in the contact hole 407. [0061] The phase changeable material layer 411 may comprise materials, the crystalline structure of which vary depending on a temperature (or heat). For example, the phase changeable material layer 411 may comprise Te and/or Se, and Ge, Sb, Bi, Pb, Sn, Ag, As, S, Si, P, O and/or N. [0062] As one example, Ge—Sb—Te may be formed using a sputtering technique. A process targeting Ge—Sb—Te is performed under a condition of about 10 nm argon and about 500 W DC power. [0063] The upper conductive layer 413 may comprise titanium nitride (TiN), tantalum nitride (TaN), molybdenum nitride (MoN), niobium nitride (NbN), titanium silicon nitride (TiSiN), titanium aluminum nitride (TiAlN), titanium boron nitride (TiBN), zirconium silicon nitride (ZrSiN), tungsten silicon nitride (WSiN), tungsten boron nitride (WBN), zirconium aluminum nitride (ZrAlN), molybdenum silicon nitride (MoSiN), molybdenum aluminum nitride (MoAlN), tantalum silicon nitride (TaSiN), tantalum aluminum nitride (TaAlN), titanium oxide nitride (TiON), titanium aluminum oxide nitride (TiAlON), tungsten oxide nitride (WON), tantalum oxide nitride (TaON), titanium (Ti), tantalum (Ta), titanium aluminum (TiAl), zirconium (Zr), hafnium (Hf), molybdenum (Mo), tungsten (W), copper (Cu), aluminum (Al), aluminum-copper (Al—Cu), aluminum-copper-silicon (Al—Cu—Si), titanium tungsten (TiW) and/or tungsten silicide (WSi). [0064] Next, the upper conductive layer 413 and the phase changeable material layer 411 are patterned to form an upper conductive pattern 413 a and a phase changeable material pattern 411 a as illustrated in FIG. 1. [0065] As a subsequent process, an upper metal interconnection may be formed to connect the upper conductive pattern 413 a electrically. [0066] According to other embodiments, insulating spacers may be further formed on sidewalls of a residual contact hole 407 r to reduce a diameter thereof before forming the phase changeable material layer 411. [0067] Other methods for forming the phase changeable memory device of FIG. 1 will be described referring to FIGS. 8 through 11. First, referring to FIG. 8, a lower conductive pattern 803 a and an insulating layer 805 including a contact hole 807 are formed on a substrate 801 in the same method as was explained above. [0068] Still referring to FIG. 8, a carbon nano tube 809 is grown up on a surface of the lower conductive pattern 803 a exposed by the contact hole 807. In these embodiments, the carbon nano tube 809 fills the contact hole 807 entirely and protrudes beyond a top surface 805 t of the insulating layer 805. [0069] Referring to FIG. 9, a supporting insulating layer 815 is formed on the insulating layer 805 and the protruding carbon nano tube 809. The supporting insulating layer 815 may comprise, for example, silicon oxide formed by a chemical vapor deposition technique. In addition, a porous insulating layer may be used instead of the silicon oxide because of its potentially excellent adiabatic property. [0070] Referring to FIG. 10, the supporting insulating layer 815 and the protruding carbon nano tube 809 are planarizingly etched until a top surface of the insulting layer 805 is exposed. Therefore, the carbon nano tube 809 may remain flush with the insulation layer 805 in the contact hole 807. The planarization process is stopped when the top surface of the insulting layer 805 is exposed by controlling a time to perform the planarization process. [0071] Alternatively, a planarizing etch stop layer may be used. That is, a planarizing etch stop layer may be formed on the insulating layer 805 to stop the planarizing etch. Briefly, the insulating layer 805 is formed on the substrate 801 and the lower conductive pattern 803 a, and then the planarizing etch stop layer is formed thereon. The etch stop layer and the insulating layer are patterned to form the contact hole 807 and a carbon nano tube is grown. Then, a supporting insulating layer is formed on the etch stop layer and the protruding carbon nano tube and planarized using the planarizing etch stop layer as a planarizing etch stop layer. [0072] Referring to FIG. 11, a selective etch back process is applied to the carbon nano tube to recess the top surface 809 t of the carbon nano tube in the insulating layer 805. Therefore, a recessed part 807 r is defined to expose the top surface of the carbon nano tube 809 r. The part 807 r corresponds to the residual contact hole 407 r illustrated in FIG. 6. Additionally, sidewall spacers 817 may be further formed on sidewalls of the recessed part 807 r. As a result, a contact region between the phase changeable material pattern and the carbon nano tube can further decrease. These insulating spacers 817 may comprise material having etch selectivity with respect to the insulating layer 405. For instance, the insulating spacers 817 may comprise silicon nitride. [0073] In the above embodiment, if the supporting insulating layer is formed to have a planar top surface in FIG. 9, the planarization process can be performed to expose a top surface of the carbon nano tube. Then, the exposed carbon nano tube is selectively etched back. In this case, the supporting insulating layer 815 may be formed of porous insulating material. [0074] Then, the phase changeable material layer and the upper conductive layer are deposited and patterned using the same method as what is explained above. [0075] Now, referring to FIGS. 12 through 15, methods for forming a phase changeable memory device of FIG. 2 will be explained. Referring to FIG. 12, a lower conductive pattern 1203 a is formed on a substrate 1201 in the same manner as what is explained above, and an insulating layer 1205 including a contact hole 1207 is formed. [0076] Referring to FIG. 12 again, a carbon nano tube 1209 r is grown from a surface of the lower conductive pattern 1203 a exposed by the contact hole 1207. In this case, a diameter of the carbon nano tube 1209 r is formed to be smaller than that of the contact hole 1207 and a height of the carbon nano tube 1209 r is lower than that of the insulating layer 1205 by controlling a process condition. That is, the carbon nano tube can be grown until a top surface 1209 rt thereof is lower than a top surface 1205 t of the insulating layer, so that the nano tube 1209 r is recessed in the insulating layer 1205. [0077] In some embodiments, insulating spacers may be further formed on sidewalls of the contact hole 1207 before a growth of the carbon nano tube 1209 r. [0078] Referring to FIG. 13, a supporting insulating layer 1215 is formed on the insulating layer 1203 to at least partially surround an outer surface 1209 rs of the carbon nano tube 1209 r by, in some embodiments, filling the residual contact hole 1207 r entirely. The supporting insulating layer 1215 may comprise an insulating layer having good step coverage, and, in some embodiments, a porous insulating layer having good adiabatic property. For example, an SOG layer is deposited and then thermally treated to form the supporting insulating layer 1215. This insulating layer having a good adiabatic property at least partially surrounds the carbon nano tube, such that a current for operations of a device can be reduced. [0079] Referring to FIG. 14, the supporting insulating layer 1215 is removed until the top surface of the carbon nano tube 1209 r is exposed. In this case, there may be two methods for removing the supporting insulating layer 1215. One is to sequentially perform a planarization process and an etch back process and the other is to perform only the etch back process. In the former case, the planarization process may be performed until the insulating layer 1205 is exposed, and the etch back process may be performed until the carbon nano tube 1209 r is exposed. In the latter case, the insulating layer is selectively etched back until the carbon nano tube is exposed. Other methods may be used. [0080] Referring to FIG. 15, a phase changeable material layer 1211 and an upper conductive layer 1213 are formed sequentially and patterned. [0081] In these embodiments, the carbon nano tube can be formed smaller than the contact hole in diameter, such that a contact area between the phase changeable material pattern and the carbon nano tube may be reduced. As a result, power dissipation for device operations can be reduced. In addition, the supporting insulating layer surrounds the carbon nano tube to support and to prevent the heat from conducting outside the nano tube. The phase changeable material layer can extend into the contact hole to define a program area within the contact hole, such that the power dissipation for a program operation can be reduced. [0082] Referring to FIGS. 16 through 19, methods for forming a phase changeable memory device of FIG. 3 will be explained. Referring to FIG. 16, first, a lower conductive pattern 1603 a is formed on a substrate 1601 and an insulating layer 1605 including a contact hole 1607 is formed in the same manner as explained above. [0083] Still referring to FIG. 16, a carbon nano tube 1609 is grown up vertically from a surface of the lower conductive pattern 1603 a exposed by the contact hole 1607. In this case, process conditions are controlled to shorten a diameter of the carbon nano tube 1609 compared to that of the contact hole 1607, and to make the carbon nano tube higher than a height of the insulating layer 1205. That is, the carbon nano tube 1609 is grown until a top surface 1609 t thereof is higher than a top surface 1605 t of the insulating layer, so that it protrudes form the insulating layer. [0084] Referring to FIG. 17, a supporting insulating layer 1615 is formed on the insulating layer 1603 to at least partially surround an outer surface 1609 s of the carbon nano tube 1609 by, in some embodiments, filling the residual contact hole 1607 r entirely. The supporting insulating layer 1615 may comprise an insulating layer having good step coverage and, in some embodiments, a porous insulating layer having good adiabatic property. For example, an SOG layer is deposited and treated thermally to form the supporting insulating layer. The insulating layer having good adiabatic property at least partially surrounds the carbon nano tube, such that the carbon nano tube can be effectively insulated from losing substantial heat during an operation of device. [0085] Referring to FIG. 18, a planarization process is performed to expose the insulating layer 1605. Therefore, the insulating layer 1615 a and the carbon nano tube 1609 remain flush with the contact hole 1607. [0086] Referring to FIG. 19, a phase changeable material layer 1611 and the upper conductive layer 1613 are sequentially stacked on the insulating layer 1605, the carbon nano tube 1609 and the supporting insulating layer 1605. [0087] In a subsequent process, a photolithographic etching process is performed to form an upper conductive pattern 1613 a and a phase changeable material pattern 1611 a as illustrated in FIG. 3. [0088] As shown in FIG. 20, the carbon nano tube 2009 r is selectively etched back to lower a top surface thereof compared to a top surface of the insulating layer 2005 before the formation of the phase-changeable material layer 1611. [0089] More particularly, if the top surface of the supporting insulating layer 2015 a is formed to be plane, the planarization process may be performed until the top surface of the carbon nano tube is exposed. In addition, the planarization process is performed to expose the carbon nano tube and then the exposed carbon nano tube may be selectively etched back. Other 2000 series elements of FIG. 20 are similar to the 1600 series described above. [0090] In embodiments of FIG. 20, a diameter of the carbon nano tube may be reduced compared to the contact hole, such that the contact region between the phase changeable material pattern and the carbon nano tube can be reduced. As a result, power dissipation for an operation of device can be decreased. In addition, the supporting insulating layer surrounds the carbon nano tube to support and/or to achieve a good adiabatic effect. [0091] According to some embodiments of the present invention, a carbon nano tube having good tolerance with respect to current density is used for supplying current to a phase changeable material layer. The carbon nano tube can be formed to have a very small diameter. Therefore, a carbon nano tube according to some embodiments of the present invention can allow highly integrated devices. [0092] Moreover, because a height of the carbon nano tube can be controlled to extend a phase changeable material pattern into the contact hole, a program region can be reduced to decrease a power dissipation. [0093] An outer sidewall of the carbon nano tube can be surrounded by a porous insulating layer having good adiabatic property in some embodiments, such that heat conductive efficiency of the carbon nano tube can be improved to reduce the power dissipation accordingly. [0094] In the drawings and specification, there have been disclosed embodiments of the invention and, although specific terms are employed, they are used in a generic and descriptive sense only and not for purposes of limitation, the scope of the invention being set forth in the following claims. Referenced byCiting PatentFiling datePublication dateApplicantTitleUS7214958Apr 8, 2005May 8, 2007Infineon Technologies AgPhase change memory cell with high read margin at low power operationUS7348590Apr 8, 2005Mar 25, 2008Infineon Technologies AgPhase change memory cell with high read margin at low power operationUS7361925Feb 10, 2005Apr 22, 2008Infineon Technologies AgIntegrated circuit having a memory including a low-k dielectric material for thermal isolationUS7420199 *Jul 14, 2005Sep 2, 2008Infineon Technologies AgResistivity changing memory cell having nanowire electrodeUS7491962 *Aug 30, 2005Feb 17, 2009Micron Technology, Inc.Resistance variable memory device with nanoparticle electrode and method of fabricationUS7626190Jun 2, 2006Dec 1, 2009Infineon Technologies AgMemory device, in particular phase change random access memory device with transistor, and method for fabricating a memory deviceUS7667218 *Nov 30, 2005Feb 23, 2010Renesas Technology Corp.Semiconductor integrated circuit device and method of manufacturing the sameUS7749801Dec 13, 2006Jul 6, 2010Korea Advanced Institute Of Science & TechnologyPhase change memory device using carbon nanotube and method for fabricating the sameUS7777212Jan 10, 2008Aug 17, 2010Samsung Electronics Co., Ltd.Phase change memory devices including carbon-containing adhesive patternUS7824951Mar 18, 2008Nov 2, 2010Qimonda AgMethod of fabricating an integrated circuit having a memory including a low-k dielectric materialUS7824953 *Jan 11, 2006Nov 2, 2010Samsung Electronics Co., Ltd.Method of operating and structure of phase change random access memory (PRAM)US7863173 *Jul 10, 2007Jan 4, 2011Samsung Electronics Co., Ltd.Variable resistance non-volatile memory cells and methods of fabricating sameUS7910908 *Sep 14, 2007Mar 22, 2011Hynix Semiconductor Inc.Phase change memory device in which a phase change layer is stably formed and prevented from lifting and method for manufacturing the sameUS7977667Apr 10, 2009Jul 12, 2011Sandisk 3D LlcMemory cell that includes a carbon nano-tube reversible resistance-switching element and methods of forming the sameUS7982318 *Jan 19, 2007Jul 19, 2011Samsung Electronics Co., Ltd.Device including contact structure and method of forming the sameUS8088643Jan 16, 2009Jan 3, 2012Micron Technology, Inc.Resistance variable memory device with nanoparticle electrode and method of fabricationUS8115186 *Jul 7, 2009Feb 14, 2012International Business Machines CorporationPhase change memory cell with reduced switchable volumeUS8119528 *Aug 19, 2008Feb 21, 2012International Business Machines CorporationNanoscale electrodes for phase change memory devicesUS8237146Feb 24, 2010Aug 7, 2012Sandisk 3D LlcMemory cell with silicon-containing carbon switching layer and methods for forming the sameUS8269208 *Mar 7, 2008Sep 18, 2012Ovonyx, Inc.Memory deviceUS8293650Feb 14, 2011Oct 23, 2012Hynix Semiconductor Inc.Phase change memory device in which a phase change layer is stably formed and prevented from lifting and method for manufacturing the sameUS8309407Mar 31, 2009Nov 13, 2012Sandisk 3D LlcElectronic devices including carbon-based films having sidewall liners, and methods of forming such devicesUS8389375Feb 11, 2010Mar 5, 2013Sandisk 3D LlcMemory cell formed using a recess and methods for forming the sameUS8409960 *Apr 8, 2011Apr 2, 2013Micron Technology, Inc.Methods of patterning platinum-containing materialUS8467224Apr 9, 2009Jun 18, 2013Sandisk 3D LlcDamascene integration methods for graphitic films in three-dimensional memories and memories formed therefromUS8470646Dec 30, 2009Jun 25, 2013Sandisk 3D LlcModulation of resistivity in carbon-based read-writeable materialsUS8471360Apr 14, 2010Jun 25, 2013Sandisk 3D LlcMemory cell with carbon switching material having a reduced cross-sectional area and methods for forming the sameUS8481396Jul 13, 2010Jul 9, 2013Sandisk 3D LlcMemory cell that includes a carbon-based reversible resistance switching element compatible with a steering element, and methods of forming the sameUS8525244Jul 13, 2007Sep 3, 2013Samsung Electronics Co., Ltd.Germanium compound, semiconductor device fabricated using the same, and methods of forming the sameUS8551850Dec 7, 2009Oct 8, 2013Sandisk 3D LlcMethods of forming a reversible resistance-switching metal-insulator-metal structureUS8551855Jul 13, 2010Oct 8, 2013Sandisk 3D LlcMemory cell that includes a carbon-based reversible resistance switching element compatible with a steering element, and methods of forming the sameUS8598708 *Dec 20, 2007Dec 3, 2013Commissariat A L'energie AtomiqueCarbon nanotube-based interconnection elementUS8653494Feb 28, 2013Feb 18, 2014Micron Technology, Inc.Integrated circuitry, methods of forming memory cells, and methods of patterning platinum-containing materialUS8759810 *Sep 24, 2010Jun 24, 2014The Trustees Of The University Of PennsylvaniaPhase change memory devices with relaxed stressUS8796101 *Aug 20, 2012Aug 5, 2014Ovonyx, Inc.Memory deviceUS8835891Dec 20, 2013Sep 16, 2014Micron Technology, Inc.Integrated circuitry, methods of forming memory cells, and methods of patterning platinum-containing materialUS8878155Dec 9, 2011Nov 4, 2014Micron Technology, Inc.Resistance variable memory device with nanoparticle electrode and method of fabricationUS8883602 *Dec 3, 2010Nov 11, 2014Micron Technology, Inc.Memory devices having electrodes comprising nanowires, systems including same and methods of forming sameUS20110012082 *Mar 18, 2009Jan 20, 2011Nxp B.V.Electronic component comprising a convertible structureUS20110076827 *Dec 3, 2010Mar 31, 2011Micron Technology, Inc.Memory devices having electrodes comprising nanowires, systems including same and methods of forming sameUS20120256150 *Apr 8, 2011Oct 11, 2012Micron Technology, Inc.Integrated Circuitry, Methods of Forming Memory Cells, and Methods of Patterning Platinum-Containing MaterialUS20120273746 *Sep 24, 2010Nov 1, 2012The Trustees Of The University Of PennsylvaniaSystem and method for the relaxation of stress in phase memory devicesUS20120329237 *Aug 20, 2012Dec 27, 2012Wolodymyr CzubatyjMemory DeviceEP1744323A1 *Jul 4, 2006Jan 17, 2007Qimonda AGPhase change memory cell having nanowire electrodeEP1881542A1Jul 16, 2007Jan 23, 2008Qimonda North America Corp.Phase change memory cell including nanocomposite insulatorWO2006003620A1 *Jun 28, 2005Jan 12, 2006Koninkl Philips Electronics NvMethod for manufacturing an electric device with a layer of conductive material contacted by nanowireWO2006084856A1 *Feb 8, 2006Aug 17, 2006Infineon Technologies AgPhase change memory cell with high read margin at low power operationWO2007093190A1 *Feb 16, 2006Aug 23, 2007Fraunhofer Ges ForschungElectric contacts with a minimal contact surface for non-volatile memory cellsWO2010006000A1 *Jul 7, 2009Jan 14, 2010Sandisk 3D, LlcCarbon-based resistivity-switching materials and methods of forming the sameWO2010008938A1 *Jul 1, 2009Jan 21, 2010Sandisk 3D, LlcElectronic devices including carbon-based films having sidewall liners, and methods of forming such devicesWO2010009364A1 *Jul 17, 2009Jan 21, 2010Sandisk 3D, LlcCarbon-based resistivity-switching materials and methods of forming the sameWO2011100100A1 *Jan 21, 2011Aug 18, 2011Sandisk 3D, LlcMemory cell formed using a recess and methods for forming the same* Cited by examinerClassifications U.S. Classification257/758, 257/E45.002International ClassificationH01L45/00, G11C13/02, G01B11/24, H01L51/30, H01L51/00, G11C16/02, H01L27/10Cooperative ClassificationH01L45/1666, H01L45/144, H01L45/06, H01L45/1233, H01L45/1625, H01L45/126, G11C13/025, B82Y10/00, G11C13/0004, H01L51/0048, H01L51/0052European ClassificationG11C13/00R1, B82Y10/00, H01L45/04, G11C13/02NLegal EventsDateCodeEventDescriptionApr 19, 2004ASAssignmentOwner name: SAMSUNG ELECTRONICS CO., LTD., KOREA, REPUBLIC OFFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:HIDEKI, HORII;REEL/FRAME:015241/0990Effective date: 20040409Sep 21, 2011FPAYFee paymentYear of fee payment: 4RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services