Patent US8187534 - Porous barrier media comprising color change indicators - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsThe present invention provides porous barrier compositions comprising color change indicators and methods of making and using the same....http://www.google.com/patents/US8187534?utm_source=gb-gplus-sharePatent US8187534 - Porous barrier media comprising color change indicatorsAdvanced Patent SearchPublication numberUS8187534 B2Publication typeGrantApplication numberUS 12/029,850Publication dateMay 29, 2012Priority dateFeb 12, 2007Fee statusPaidAlso published asEP2118182A2, EP2118182B1, US20080199363, WO2008100500A2, WO2008100500A3Publication number029850, 12029850, US 8187534 B2, US 8187534B2, US-B2-8187534, US8187534 B2, US8187534B2InventorsGuoqiang MaoOriginal AssigneePorex CorporationExport CitationBiBTeX, EndNote, RefManPatent Citations (46), Non-Patent Citations (27), Referenced by (5), Classifications (28), Legal Events (6) External Links: USPTO, USPTO Assignment, EspacenetPorous barrier media comprising color change indicators
US 8187534 B2Abstract
The present invention provides porous barrier compositions comprising color change indicators and methods of making and using the same.
1. A self-sealing barrier composition comprising:
a sintered porous matrix, the sintered porous matrix comprising at least one plastic, at least one absorbent material, and particles of at least one color change indicator, wherein the particles of the at least one color change indicator in the sintered porous matrix dissolve upon contact with liquid and at least partially change the color of the sintered porous matrix, and the sintered porous matrix is self-sealing upon contact with the liquid.
2. The self-sealing barrier composition of claim 1, wherein the at least one color change indicator comprises an organic dye, food grade dye, or mixtures thereof.
3. The self-sealing barrier composition of claim 2, wherein the color change indicator comprises FD&C Blue No. 1, FD&C Blue No. 2, FD&C Green No. 3, FD&C Red No. 40, FD&C Red No. 3, FD&C Yellow No. 5, FD&C Yellow No. 6, Solvent Red 24, Solvent Red 26, Solvent Red 164, Solvent Yellow 124, Solvent Blue 35, or mixtures thereof.
4. The self-sealing barrier composition of claim 1, wherein the color change indicator is responsive to pH.
5. The self-sealing barrier composition of claim 4, wherein the color change indicator comprises methyl violet, eosin yellow, malachite green, thymol blue, methyl yellow, bromophenol blue, congo red, methyl orange, bromocresol green, methyl red, litmus, bromocresol purple, bromophenol red, bromothymol blue, phenol red, neutral red, naphtholphthalein, cresol red, phenolphthalein, thymolphthalein, alkali blue, Alizarin Yellow R, indigo carmine, epsilon blue, or mixtures thereof.
6. The self-sealing barrier composition of claim 1, wherein the at least one absorbent material comprises carboxymethylcellulose, cellulose gums, hydrolyzed acrylonitrile graft copolymer, neutralized starch-acrylic acid graft copolymer, acrylamide copolymer, modified crosslinked polyvinyl alcohol, neutralized self-crosslinking polyacrylic acid, crosslinked polyacrylate salts, neutralized crosslinked isobutylene-maleic anhydride copolymers, or salts or mixtures thereof.
7. The self-sealing barrier composition of claim 1, wherein the at least one plastic comprises a polyolefin, polyamide, polyester, polyurethane, polyacrylonitrile, polycarbonate, polyvinylchloride, polymethylmethacrylate, polyvinylidene fluoride, polytetrafluoroethylene, polyethersulfone, polystyrene, polyether imide, polyetheretherketone, polysulfone, or combinations or copolymers thereof.
8. The self-sealing barrier composition of claim 7, wherein the polyolefin comprises polyethylene, polypropylene, polybutylene, or combinations or copolymers thereof.
9. The self-sealing barrier composition of claim 1, wherein the at least one color change indicator is present in an amount ranging from about 0.001 weight percent to about 2 weight percent of the sintered porous matrix.
10. The self-sealing barrier composition of claim 1, wherein the at least one color change indicator is present in an amount ranging from about 0.05 weight percent to about 0.5 weight percent of the sintered porous matrix.
11. The self-sealing barrier composition of claim 1, wherein the at least one plastic is present in an amount ranging from about 40 weight percent to about 95 weight percent of the sintered porous matrix.
12. The self-sealing barrier composition of claim 1, wherein the sintered porous matrix has an average pore size ranging from about 1 μm an to about 200 μm.
13. The self-sealing barrier composition of claim 1, wherein the sintered porous matrix has a porosity of up to about 90%.
14. The self-sealing barrier composition of claim 1, wherein the self-sealing barrier composition is not responsive to ambient atmospheric moisture.
a pipette tip and the self-sealing barrier composition of claim 1, wherein the self-sealing barrier composition of claim 1 is at least partially disposed in the pipette tip.
an aspirator, the aspirator comprising a receptacle, an inlet to the receptacle, and an outlet to the receptacle, wherein the self-sealing barrier composition of claim 1 at least partially covers the outlet of the receptacle.
17. An analytical device comprising:
a liquid sample collection chamber comprising a sample inlet and the self-sealing barrier composition of claim 1 disposed within the sample collection chamber.
18. The self-sealing barrier composition of claim 1, wherein the at least one color change indicator does not comprise inorganic salts.
19. The self-sealing barrier composition of claim 1, wherein the at least one color change indicator does not comprise a conjugate or complex that changes color upon the binding of an analyte.
20. The self-sealing barrier composition of claim 1, wherein the at least one color change indicator does not comprise proteins or other biological molecules.
21. A self-sealing barrier composition comprising:
a sintered porous matrix, the sintered porous matrix comprising at least one self-sealing layer and at least one indicator layer, wherein the self-sealing layer comprises at least one absorbent material and the indicator layer comprises particles of at least one color change indicator, wherein the particles of the at least one color change indicator in the indicator layer dissolve upon contact with liquid and at least partially change the color of the indicator layer, and the self-sealing layer is self-sealing upon contact with the liquid.
22. The self-sealing barrier composition of claim 21, wherein the at least one color change indicator comprises an organic dye, food grade dye, or mixtures thereof.
23. The self-sealing barrier composition of claim 22, wherein the color change indicator comprises FD&C Blue No. 1, FD&C Blue No. 2, FD&C Green No. 3, FD&C Red No. 40, FD&C Red No. 3, FD&C Yellow No. 5, FD&C Yellow No. 6, Solvent Red 24, Solvent Red 26, Solvent Red 164, Solvent Yellow 124, Solvent Blue 35, or mixtures thereof.
24. The self-sealing barrier composition of claim 21, wherein the self-sealing layer is adjacent to the indicator layer.
25. The self-sealing barrier composition of claim 21, wherein the self-sealing layer is spaced apart from the indicator layer.
26. The self-sealing barrier composition of claim 21, wherein the self-sealing layer further comprises a second color change indicator.
27. The self-sealing barrier composition of claim 26, wherein the second color change indicator is different than the color change indicator of the indicator layer.
28. The self-sealing barrier composition of claim 21, wherein the self-sealing layer further comprises at least one plastic.
29. A self-sealing barrier composition comprising:
a sintered porous matrix, the sintered porous matrix comprising a self-sealing surface and an indicator surface in facing opposition to the self-sealing surface wherein the self-sealing surface comprises at least one absorbent material and the indicator surface comprises particles of at least one color change indicator, wherein the particles of the at least one color change indicator in the indicator surface dissolve upon contact with liquid and at least partially change the color of the indicator surface, and the self-sealing surface is self-sealing upon contact with the liquid.
30. A hydrophobic barrier composition comprising:
a sintered porous matrix, the sintered porous matrix comprising at least one plastic and particles of at least one color change indicator, wherein the hydrophobic barrier composition is substantially free of any absorbent material, wherein the particles of the at least one color change indicator in the sintered porous matrix dissolve upon contact with liquid and at least partially change the color of the sintered porous matrix, and the sintered porous matrix inhibits the liquid from passing through the hydrophobic barrier composition upon contact with the liquid.
31. The hydrophobic barrier composition of claim 30, wherein the at least one color change indicator comprises an organic dye, food grade dye, or mixtures thereof.
32. The hydrophobic barrier composition of claim 31, wherein the color change indicator comprises FD&C Blue No. 1, FD&C Blue No. 2, FD&C Green No. 3, FD&C Red No. 40, FD&C Red No. 3, FD&C Yellow No. 5, FD&C Yellow No. 6, Solvent Red 24, Solvent Red 26, Solvent Red 164, Solvent Yellow 124, Solvent Blue 35, or mixtures thereof.
33. The hydrophobic barrier composition of claim 30, wherein the color change indicator is responsive to pH.
34. The hydrophobic barrier composition of claim 33, wherein the color change indicator comprises methyl violet, eosin yellow, malachite green, thymol blue, methyl yellow, bromophenol blue, congo red, methyl orange, bromocresol green, methyl red, litmus, bromocresol purple, bromophenol red, bromothymol blue, phenol red, neutral red, naphtholphthalein, cresol red, phenolphthalein, thymolphthalein, alkali blue, Alizarin Yellow R, indigo carmine, epsilon blue, or mixtures thereof.
35. The hydrophobic barrier composition of claim 30, wherein the at least one color change indicator is present in an amount ranging from about 0.001 weight percent to about 2 weight percent of the sintered porous matrix.
36. The hydrophobic barrier composition of claim 30, wherein the at least one color change indicator is present in an amount ranging from about 0.05 weight percent to about 0.5 weight percent of the sintered porous matrix.
37. The hydrophobic barrier composition of claim 30, wherein the sintered porous matrix has an average pore size ranging from about 1 μm to about 200 μm.
38. A hydrophilic composition comprising:
a sintered porous matrix, the sintered porous matrix comprising at least one plastic, particles of at least one color change indicator, and at least one surfactant, wherein the particles of the at least one color change indicator dissolve upon contact with liquid and at least partially change the color of the sintered porous matrix.
39. The hydrophilic composition of claim 38, wherein the at least one surfactant comprises anionic surfactants, cationic surfactants, nonionic surfactants, amphoteric surfactants, or mixtures thereof.
40. The hydrophilic composition of claim 38, wherein the at least one surfactant is present in an amount ranging from about 0.001 weight percent to about 3 weight percent of the sintered porous matrix.
41. A method of making a self-sealing barrier composition comprising:
providing particles of at least one absorbent material;
providing particles of at least one color change indicator; and
cosintering the particles of the at least one plastic, the particles of the at least one absorbent material, and the particles of the at least one color change indicator to form the self-sealing barrier composition, wherein the particles of the at least one color change indicator dissolve upon contact with liquid and the self-sealing barrier composition at least partially changes color and is self-sealing upon contact with the liquid.
42. The method of claim 41, further comprising mixing the particles of the at least one plastic, the particles of the at least one absorbent material, and the particles of the at least one color change indicator to form a substantially uniform mixture.
43. The method of claim 41, wherein the particles of the at least one plastic have an average diameter ranging from about 1 μm to about 500 μm.
44. A hydrophobic barrier composition comprising:
a sintered porous matrix, the sintered porous matrix comprising at least one plastic and at particles of least one color change indicator, wherein the particles of the at least one color change indicator in the sintered porous matrix dissolve upon contact with liquid and at least partially change the color of the sintered porous matrix, and the sintered porous matrix inhibits the liquid from passing through the hydrophobic barrier composition upon contact with the liquid. Description
This application hereby claims priority to U.S. Provisional Patent Application Ser. No. 60/900,817, filed Feb. 12, 2007.
The present invention relates to porous barrier media and, in particular, to porous barrier media comprising color change indicators.
Porous barrier media find application in a number of areas including liquid sampling and transfer apparatus, such as pipettes. Barrier media are often incorporated into liquid sampling and transfer apparatus to prevent contamination of the apparatus in situations where the liquid is overdrawn by human or mechanical error.
In addressing apparatus contamination, porous barrier media have incorporated absorbent materials which are operable to seal the pores of the media when exposed to liquid. The self-sealing nature of the barrier media comprising absorbent materials inhibits or prevents liquid from traveling through the media and contaminating downstream apparatus. In the sealed state, barrier media comprising absorbent materials additionally inhibit or prevent the flow of gasses thereby requiring replacement of the media for further liquid transfer or sampling.
In addition to absorbent materials, barrier media have been coated with metal salt color changing species, such as cobalt chloride. The coating of metal salt color changing species onto barrier media facilitates a determination of when the media has been contacted by fluid.
Several problems, however, exist with metal salt color changing species. Cobalt chloride, for example, is very sensitive to moisture and must be stored under extremely dry conditions in order to prevent color change before use. Moreover, the color change indication of cobalt chloride is slow leading to a delayed response upon contact of barrier media by a liquid. Many metal salts, including cobalt chloride, are toxic and, therefore, cannot be used in biological applications. Furthermore, metal salts coated onto porous barrier media can be displaced from the porous media and contaminate the liquid sample.
In view of the foregoing problems, it would be desirable to provide porous barrier compositions comprising color change indicators that can provide a rapid response to contact by a liquid sample. Moreover, it would be desirable to provide porous barrier compositions comprising color change indicators that are stable to color change under ambient atmospheric or storage conditions. It would additionally be desirable to provide porous barrier compositions comprising color change indicators which resist contamination of liquid samples with toxic or biologically harmful species.
The present invention provides porous barrier compositions comprising color change indicators and methods of making and using the same. The present invention also provides apparatus comprising such porous barrier compositions.
In one embodiment, the present invention provides a self-sealing barrier composition comprising a sintered porous matrix, the sintered porous matrix comprising at least one plastic, at least one absorbent material, and at least one color change indicator. In some embodiments, the at least one absorbent material and the at least one color change indicator are homogeneously dispersed throughout the sintered porous matrix.
In some embodiments, at least one absorbent material comprises carboxymethylcellulose (CMC), cellulose gums, hydrolyzed acrylonitrile graft copolymer, neutralized starch-acrylic acid graft copolymer, acrylamide copolymer, modified crosslinked polyvinyl alcohol, neutralized self-crosslinking polyacrylic acid, crosslinked polyacrylate salts, or neutralized crosslinked isobutylene-maleic anhydride copolymers, or salts or mixtures thereof.
In some embodiments, at least one color change indicator comprises a dye, including, but not limited to, inorganic or organic dyes, such as food dyes, azo compounds, or azo dyes. In some embodiments, a color change indicator does not comprise inorganic salts, including transition metal salts. Additionally, in some embodiments, a color change indicator does not comprise a conjugate or complex that changes color upon the binding of an analyte. In some embodiments, compositions of the present invention do not comprise proteins or other biological molecules.
A color change indicator, according to embodiments of the present invention, is operable to at least partially change the color of the sintered porous matrix when contacted with an aqueous and/or organic liquid. In some embodiments, the color change indicator changes the sintered porous matrix from a first color to a second color when contacted with an aqueous and/or organic liquid. In other embodiments, the color change indicator changes the sintered porous matrix from colorless or white to colored. The color change of the sintered porous matrix, according to embodiments of the present invention, depends on the identity of the color change indicator selected. The change in color provides an indication to a user that the self-sealing barrier composition has come into contact with a liquid.
In another embodiment, the present invention provides a self-sealing barrier composition comprising a sintered porous matrix, the sintered porous matrix comprising at least one self-sealing layer comprising an absorbent material and at least one indicator layer comprising at least one color change indicator. In some embodiments, the indicator layer is adjacent to the self-sealing layer. In other embodiments, the indicator layer is spaced apart from the self-sealing layer. In one embodiment, the self-sealing layer further comprises a first plastic. In another embodiment, the indicator layer further comprises a second plastic. In some embodiments, the first plastic and second plastic are the same. In other embodiments, the first plastic and second plastics are different. In some embodiments, the indicator layer further comprises at least one surfactant.
The self-sealing layer, in some embodiments, further comprises a color change indicator. In some embodiments, the color change indicator of the self-sealing layer is the same as the color change indicator of the indicator layer. In other embodiments, the color change indicator of the self-sealing layer is different than the color change indicator of the indicator layer.
In some embodiments, a self-sealing barrier composition comprises a plurality of self-sealing layers and a plurality of indicator layers.
“Self-sealing,” as used herein, refers to the ability of the absorbent material to substantially close or seal pores of the porous matrix or a layer of the porous matrix such that the passage of liquid and/or gas is inhibited or prevented. Not all the pores of the porous matrix or a layer of the porous matrix are required to be substantially closed or sealed in order for the a composition to be self-sealing.
In another embodiment, the present invention provides a self-sealing barrier composition comprising a sintered porous matrix, the sintered porous matrix comprising a self-sealing surface and an indicator surface in facing opposition to the self-sealing surface, the self-sealing surface comprising an absorbent material and the indicator surface comprising a color change indicator. In one embodiment, the self-sealing surface further comprises a first plastic. In another embodiment, the indicator surface further comprises a second plastic. In one embodiment, the first plastic and second plastic are the same. In other embodiments, the first plastic and second plastic are different. In some embodiments, the indicator surface further comprises at least one surfactant.
The self-sealing surface, in some embodiments, further comprises a color change indicator. In some embodiments, the color change indicator of the self-sealing surface is the same as the color change indicator of the indicator surface. In other embodiments, the color change indicator of the self-sealing surface is different than the color change indicator of the indicator surface.
In addition to self-sealing barrier compositions, the present invention provides hydrophobic barrier compositions. In one embodiment, a hydrophobic barrier composition comprises a sintered porous matrix, the sintered porous matrix comprising at least one plastic and at least one color change indicator wherein the barrier composition is substantially free of any absorbent or self-sealing material. In some embodiments of a hydrophobic barrier composition, the sintered porous matrix does not comprise any absorbent or self-sealing material. As a result, hydrophobic barrier compositions, according to embodiments of the present invention, are not self-sealing. In one embodiment, at least one color change indicator comprises a dye, including, but not limited to, organic dyes, such as food dyes. Color change indicators, according to embodiments of the present invention, are operable to at least partially change the color of the sintered porous matrix when contacted with an aqueous and/or non-aqueous liquid. The change in color provides an indication to a user that the barrier material has come into contact with a liquid. In some embodiments, the at least one color change indicator is homogeneously dispersed throughout the sintered porous matrix.
In some embodiments, hydrophobic barrier compositions comprise a water intrusion pressure of greater than about 0.5 psi.
In another embodiment, the present invention provides a hydrophobic barrier composition comprising at least one plastic layer comprising at least a first plastic and an indicator layer comprising at least one color change indicator. In some embodiments, the at least one indicator layer is adjacent to the at least one plastic layer. In other embodiments, the at least one indicator layer is spaced apart from the at least one plastic layer. In one embodiment, the at least one indicator layer further comprises a second plastic. In some embodiments, the second plastic is the same as the first plastic. In other embodiments, the second plastic is different than the first plastic. In some embodiments, the indicator layer further comprises at least one surfactant.
The plastic layer, in some embodiments, further comprises a color change indicator. In some embodiments, the color change indicator of the plastic layer is the same as the color change indicator of the indicator layer. In other embodiments, the color change indicator of the plastic layer is different than the color change indicator of the indicator layer.
In a further embodiment, the present invention provides a hydrophobic barrier composition comprising a sintered porous matrix, the sintered porous matrix comprising a first surface and a second surface in facing opposition to the first surface, the first surface comprising at least one plastic and the second surface comprising at least one color change indicator. In some embodiments, the second surface comprises at least one surfactant. In another embodiment, the first surface further comprises a color change indicator. In some embodiments, the color change indicator of the first surface is the same as the color change indicator of the second surface. In other embodiments, the color change indicator of the first surface is different than the color change indicator of the second surface.
In another embodiment, the present invention provides a hydrophilic composition comprising a sintered porous matrix, the sintered porous matrix comprising at least one plastic, at least one color change indicator, and at least one surfactant.
In some embodiments of a sintered porous matrix of barrier compositions of the present invention, the color change indicator is locked within the sintered porous matrix. In being locked within the sintered porous matrix, the color change indicator, in some embodiments, is not a coating. Moreover, in some embodiments, the color change indicator at least partially resides in the pores of a sintered porous matrix. In a further embodiment, the color change indicator is locked in the sintered porous matrix and additionally resides in the pores of the sintered porous matrix.
In another aspect, the present invention provides methods of producing barrier compositions. In one embodiment, a method of producing a self-sealing barrier composition comprises providing particles of at least one plastic, providing particles of at least one absorbent material, providing particles of at least one color change indicator, and sintering the particles of the at least one plastic, the at least one absorbent material, and the at least one color change indicator.
In another embodiment, a method of producing a self-sealing barrier composition comprises disposing particles of at least one absorbent material in a first part of a mold, disposing particles of at least one color change indicator in a second part of the mold adjacent to the first part of the mold, and sintering the particles of the at least one absorbent material and color change indicator. In some embodiments particles of a first plastic are mixed with the particles of the at least one absorbent material prior to sintering. In some embodiments, particles of a second plastic are mixed with particles of the at least one color change indicator prior to sintering. In one embodiment, the first plastic and the second plastic are the same. In another embodiment, the first plastic and the second plastic are different.
In some embodiments, particles of at least one surfactant are mixed with particles of the at least one color change indicator prior to sintering. In other embodiments, particles of a second plastic are at least partially coated with at least one surfactant prior to sintering. In such embodiments, the surfactant can be applied to the second plastic particles as a liquid. In some embodiments, particles of a second color change indicator are mixed with particles of the at least one absorbent material prior to sintering. In some embodiments, particles of the at least one color change indicator and particles of the second color change indicator are the same. In another embodiment, particles of the at least one color change indicator and particles of the second color change indicator are different.
In another embodiment, a method for producing a hydrophobic barrier composition comprises providing particles of at least one plastic, providing particles of at least one color change indicator, and sintering the particles of the at least one plastic and the at least one color change indicator.
In a further embodiment, a method for producing a hydrophobic barrier composition comprises disposing particles of a first plastic in a first part of a mold, disposing particles of at least one color change indicator in a second part of a mold adjacent to the first part of the mold, and sintering the particles of the first plastic and the at least one color change indicator. In some embodiments, particles of a second plastic are mixed with the particles of the at least one color change indicator prior to sintering. In one embodiment, the first plastic and second plastic are the same. In another embodiment, the first plastic and second plastic are different.
In some embodiments, particles of at least one surfactant are mixed with the particles of the at least one color change indicator prior to sintering. In other embodiments, particles of a second plastic are at least partially coated with at least one surfactant prior to sintering. In such embodiments, the surfactant can be applied to the second plastic particles as a liquid.
In another aspect, the present invention provides methods for producing hydrophilic compositions. In one embodiment, a method for producing a hydrophilic composition comprises providing particles of at least one plastic, providing particles of at least one color change indicator, providing particles of at least one surfactant, and sintering the particles of the at least one plastic, at least one color change indicator, and at least one surfactant. In another embodiment, a method for producing a hydrophilic composition comprises providing particles of at least one plastic, at least partially coating the particles of the at least one plastic with at least one surfactant, providing particles of at least one color change indicator, and sintering the particles of the at least one plastic and particles of the at least one color change indicator. In some embodiments, particles of color change indicators are at least partially coated with at least one surfactant prior to sintering.
In another aspect, the present invention provides apparatus comprising barrier compositions of the present invention. In one embodiment, an apparatus comprises a pipette tip, the pipette tip comprising a hollow tube having first and second open ends, a center member disposed between the first and second ends, the center member comprising a barrier composition according to any of the embodiments provided herein. The pipette tip can have any desired sample collection volume. In some embodiments, the pipette tip has a sample collection volume of about 10 μl or about 20 μl. In other embodiments, the pipette tip has a sample collection volume of about 50 μl or about 100 μl. In another embodiment, the pipette tip has a sample collection volume of about 200 μl, about 250 μl, about 500 μl, or about 1 ml. In a further embodiment, the pipette tip has a sample collection volume less than about 10 μl or greater than about 1 ml or about 5 ml. In some embodiments, the pipette tip has a sample collection volume of about 1 μl or about 5 μl.
In another embodiment, barrier compositions of the present invention find application as flow control devices in various apparatus such as aspirators. In one embodiment, an aspirator comprises a receptacle, a lid, and a barrier composition of the present invention disposed in the receptacle. The lid further comprises an inlet and an outlet wherein outlet is operable to be connected to a suction or vacuum line. In some embodiments, a self-sealing barrier composition, for example, covers the outlet such that when sufficient liquid has been collected in the receptacle, contact of the liquid to the barrier composition results in self-sealing of the composition. Sealing of the barrier composition prevents additional aspiration.
In another embodiment, barrier compositions of the present invention find application in needle apparatus such as an indwelling needle as described in U.S. patent application Ser. No. 11/065,579; a flashback blood collection needle as described in U.S. patent application Ser. No. 11/141,588; a blood collection set as described in U.S. patent application Ser. No. 11/141,446; and a luer cap associated with an intravenous (IV) set. In these applications, barrier compositions of the present invention are incorporated as vents, allowing the passage of air and other gases while blocking the passage of liquids such as blood.
In a further embodiment, barrier compositions of the present invention find application in analytical devices to indicate that sufficient liquid sample has been collected. In some embodiments, an analytical device comprises a liquid sample collection chamber comprising a sample inlet and a barrier composition disposed within the sample collection chamber. The barrier composition, in some embodiments, can be disposed at various levels in the collection chamber depending on the desired volume of sample to be collected. When sufficient sample has been collected, liquid contacts the barrier composition rendering a color change in the medium. The color change in the barrier composition can indicate to a user of the analytical device that sufficient sample has been collected. In some embodiments, the liquid sample chamber further comprises an outlet.
FIG. 1 illustrates a self-sealing barrier composition according to an embodiment of the present invention.
FIG. 2 illustrates a self-sealing barrier composition according to an embodiment of the present invention.
FIG. 3 illustrates a hydrophobic barrier composition according to an embodiment of the present invention.
FIG. 4 illustrates a pipette tip comprising a barrier composition according to an embodiment of the present invention.
Self-Sealing Barrier Compositions Comprising Color Change Indicators
In one embodiment, the present invention provides a self-sealing barrier composition comprising a sintered porous matrix, the sintered porous matrix comprising at least one plastic, at least one absorbent material, and at least one color change indicator.
Turning now to components that can be included in self-sealing barrier compositions of the present invention, self-sealing barrier compositions of the present invention comprise at least one plastic. In some embodiments, sintered porous matrices of self-sealing barrier compositions of the present invention comprise a plurality of plastics. Plastics, as used herein, include flexible plastics and rigid plastics. Flexible plastics, in some embodiments, comprise polymers possessing moduli ranging from about 15,000 N/cm2 to about 350,000 N/cm2 and/or tensile strengths ranging from about 1500 N/cm2 to about 7000 N/cm2. Rigid plastics, according to some embodiments, comprise polymers possessing moduli ranging from about 70,000 N/cm2 to about 350,000 N/cm2 and have tensile strengths ranging from about 3000 N/cm2 to about 8500 N/cm2.
Plastics suitable for use in sintered porous matrices of self-sealing barrier compositions, in some embodiments, comprise polyolefins, polyamides, polyesters, polyurethanes, polyacrylonitriles, polycarbonates, polyvinylchloride, polymethylmethacrylate, polyvinylidene fluoride, polytetrafluoroethylene, polyethersulfones, polystyrenes, polyether imides, polyetheretherketones, polysulfones, or combinations or copolymers thereof.
In some embodiments, a polyolefin comprises polyethylene, polypropylene, or copolymers thereof. Polyethylene, in one embodiment, comprises high density polyethylene (HDPE). HDPE, as used herein, refers to polyethylene having a density ranging from about 0.92 g/cm3 to about 0.97 g/cm3. In some embodiments, HDPE has a degree of crystallinity (% from density) ranging from about 50 to about 90. In another embodiment, polyethylene comprises ultrahigh molecular weight polyethylene (UHMWPE). UHMWPE, as used herein, refers to polyethylene having a molecular weight greater than 1,000,000.
In addition to at least one plastic, self-sealing barrier compositions comprise at least one absorbent material. In some embodiments, an absorbent material comprises carboxymethylcellulose (CMC), cellulose gums, hydrolyzed acrylonitrile graft copolymer, neutralized starch-acrylic acid graft copolymer, acrylamide copolymer, modified crosslinked polyvinyl alcohol, neutralized self-crosslinking polyacrylic acid, crosslinked polyacrylate salts, or neutralized crosslinked isobutylene-maleic anhydride copolymers, or salts or mixtures thereof. In other embodiments, absorbent materials comprise sodium polyacrylic acid and salts of poly(2-propenamide-co-2-propenoic acid).
In some embodiments, absorbent materials comprise those described by U.S. Pat. Nos. 5,998,032; 5,939,086; 5,836,929, 5,824,328; 5,797,347; 5,750,585; 5,175,046; 4,820,577; 4,724,114; and 4,443,515. Examples of commercially available absorbent materials include AP80HS from Stockhousen of Tuscaloosa, Ala., HYSORB� P7200 from BASF of Florham Park, N.J., and CMC under the product designation C5013 and C5678 from Sigma-Aldrich of St. Louis, Mo.
Absorbent materials, in some embodiments, can absorb greater than about 1, 50, 100, 200, 500, or 1000 percent of their weight in water while maintaining structural integrity.
Self-sealing barrier compositions of the present invention additionally comprise at least one color change indicator. A color change indicator, according to embodiments of the present invention, is operable to at least partially change the color of the sintered porous matrix when contacted with an aqueous and/or organic liquid. In some embodiments, the color change indicator changes the sintered porous matrix from a first color to a second color when contacted with an aqueous and/or organic liquid. In other embodiments, the color change indicator changes the sintered porous matrix from colorless or white to colored. In a further embodiment, the color change indicator changes the sintered porous matrix from a first shade of a color to a different shade of the same color. The color change of the sintered porous matrix, according to embodiments of the present invention, depends on the identity of the color change indicator selected.
In some embodiments, a color change indicator comprises an inorganic or organic dye, including food grade dyes, azo compounds, or azo dyes. In some embodiments, color change indicators do not comprise inorganic salts, including transition metal salts. Additionally, in some embodiments, a color change indicator does not comprise a conjugate or complex that changes color upon the binding of an analyte. In some embodiments, self-sealing barrier compositions of the present invention do not comprise proteins or other biological molecules.
Color change indicators comprising food grade dyes, according to embodiments of the present invention, are operable to be used with biological samples due to the non-toxic nature of the food dyes.
A sintered porous matrix of a self-sealing barrier composition, according to some embodiments, comprises at least one plastic in an amount ranging from about 40 weight percent to about 95 weight percent of the matrix. In other embodiments, a sintered porous matrix comprises at least one plastic in an amount ranging from about 50 weight percent to about 90 weight percent of the matrix. In a further embodiment, a sintered porous matrix comprises at least one plastic in an amount ranging from about 60 weight percent to about 80 weight percent of the matrix.
A sintered porous matrix of a self-sealing barrier composition, in some embodiments, comprises at least one absorbent material in an amount ranging from about 1 weight percent to about 40 weight percent of the matrix. In other embodiments, a sintered porous matrix comprises an absorbent material in an amount ranging from about 5 weight percent to about 30 weight percent of the matrix. In a further embodiment, a sintered porous matrix comprises an absorbent material in an amount ranging from about 10 weight percent to about 20 weight percent of the matrix.
In addition to the at least one plastic and the at least one absorbent material, a sintered porous matrix of a self sealing barrier composition, in some embodiments, comprises at least one color change indicator in an amount ranging from about 0.001 weight percent to about 2 weight percent of the matrix. In other embodiments, a sintered porous matrix comprises at least one color change indicator in an amount ranging from about 0.01 weight percent to about 1 weight percent of the matrix. In a further embodiment, a sintered porous matrix comprises at least one color change indicator in an amount ranging from about 0.05 weight percent to about 0.5 weight percent of the matrix.
A sintered porous matrix of a self-sealing barrier composition comprising at least one plastic, at least one absorbent material, and at least one color change indicator, has a porosity ranging from about 10% to about 90%. In another embodiment, a sintered porous matrix has a porosity ranging from about 20% to about 80% or from about 30% to about 70%. In a further embodiment, a sintered porous matrix has a porosity ranging from about 40% to about 60%.
A sintered porous matrix of a self-sealing barrier composition comprising at least one plastic, at least one absorbent material, and at least one color change indicator, has an average pore size ranging from about 1 μm to about 200 μm. In other embodiments, a sintered porous matrix has an average pore size ranging from about 2 μm to about 150 μm, from about 5 μm to 100 μm, or from about 10 μm to about 50 μm. In another embodiment, a sintered porous matrix has a an average pore size less than about 1 μm. In one embodiment, a sintered porous matrix has an average pore size ranging from about 0.1 μm to about 1 μm. In a further embodiment, a sintered porous matrix has an average pore size greater than 200 μm. In one embodiment, a sintered porous matrix has an average pore size ranging from 200 μm to about 500 μm or from about 500 μm to about 1 mm.
In another embodiment, the present invention provides a self-sealing barrier composition comprising a sintered porous matrix, the sintered porous matrix comprising at least one self-sealing layer comprising at least one absorbent material and at least one indicator layer comprising at least one color change indicator. Absorbent materials suitable for use in the self-sealing layer of the present invention comprise any of the absorbent materials provided herein. Moreover, color change indicators suitable for use in the indicator layer comprise any of the color change indicators described herein.
In some embodiments, the self-sealing layer further comprises a first plastic. In some embodiments, the indicator layer further comprises a second plastic. In one embodiment, the first plastic and the second plastic are the same. In another embodiment, the first plastic and second plastic are different. Plastics suitable for use in embodiments of a barrier composition comprising at least one self-sealing layer and at least one indicator layer comprise any of the plastics described herein.
The indicator layer, in some embodiments, is adjacent to the self-sealing layer. In other embodiments, the indicator layer is spaced apart from the self-sealing layer. An indicator layer discrete from the self-sealing layer, in some embodiments, is operable to determine whether the self-sealing layer has completely sealed when contacted with an aqueous and/or organic liquid. In cases where the self-sealing layer does not sufficiently seal, an adjacent or spaced apart indicator layer can detect the presence of liquid that has breached the self-sealing layer which could potentially contaminate a downstream device, such as the suction apparatus of a pipette. In some embodiments wherein the indicator layer is spaced apart from the self-sealing layer, the self-sealing layer may further comprise a color change indicator operable to detect that a liquid has contacted the self-sealing layer.
In some embodiments, the self-sealing layer also comprises a color change indicator. In some embodiments, the color change indicator of the self-sealing layer is the same as the color change indicator of the indicator layer. In other embodiments, the color change indicator of the self-sealing layer is different than the color change indicator of the indicator layer. A self-sealing layer comprising a color change indicator can detect whether the self-sealing layer has been contacted by an aqueous and/or organic liquid.
In another embodiment, the indicator layer further comprises at least one surfactant. Surfactants, in some embodiments, comprise anionic surfactants, cationic surfactants, nonionic surfactants, amphoteric surfactants or mixtures thereof. In some embodiments, anionic surfactants comprise alkyl sulfates, alkylbenzenesulfonates, ether sulfates, α-olefin sulfonates, ester sulfonates, phosphate esters, acyl taurates, soaps, ether carboxylates, or mixtures thereof. Cationic surfactants, in some embodiments, comprise alkyl quaternary ammonium salts, bezylalkyldimethylammonium salts, amidoamine quaternaries, quaternary imidazolium compounds, ester quaternary compounds, or mixtures thereof. In some embodiments, nonionic surfactants comprise ethoxylated alcohols, ethoxylated alkylphenols, polyethylene glycol esters, fatty acid alkanolamides, ethoxylated alkanolamides, ethoxylated amines, esters of polyhydroxy compounds, ethoxylated esters, ethylene oxide/propylene oxide copolymers, amine oxides, or mixtures thereof. Amphoteric surfactants, in some embodiments, comprise alkylamino acids, alkylbetaines, alkylaminobetains, imidazoline-derived surfactants, sulfur containing amphoterics, lecithin, or mixtures thereof. In some embodiments, surfactants suitable for use in embodiments of the present invention comprise Geropon�, Rhodacal�, and Rhodafac� commercially available from Rhodia or Paris France, Pluronic� commercially available from BASF of Florham Park, N.J., and Zonyl� commercially available from DuPont of Wilmington, Del.
Indicator layers comprising at least one surfactant, in some embodiments, demonstrate advantageous wicking properties allowing a rapid response to an aqueous and/or organic liquid contacting the indicator layer.
In some embodiments, self-sealing layers can demonstrate any construction described herein for sintered porous matrices of self-sealing barrier compositions. Self-sealing layers, according to some embodiments, for example, can demonstrate pore sizes and/or porosities consistent with any the sintered porous matrices provided herein.
In some embodiments, indicator layers can demonstrate any construction described herein for sintered porous matrices of self-sealing barrier compositions. Indicator layers, according to some embodiments, for example, can demonstrate pore sizes and/or porosities consistent with any the sintered porous matrices provided herein.
In some embodiments, a self-sealing layer is constructed independently from an indicator layer. In such embodiments, the self-sealing layer and the indicator layer can display similar pore sizes and/or porosities or different pore sizes and/or porosities.
In some embodiments, at least one self-sealing layer comprises a plurality of self-sealing layers. At least one indicator layer, in some embodiments, comprises a plurality of indicator layers.
FIG. 1 illustrates a self-sealing barrier composition comprising a sintered porous matrix comprising at least one self-sealing layer and at least one indicator layer. The self-sealing barrier composition (100) illustrated in FIG. 1 comprises a indicator layer (102) adjacent to the self-sealing layer (104). Liquid breaching the self-sealing layer can contact the indicator layer thereby alerting a user of the barrier composition that the self-sealing layer has insufficiently sealed or has another problem allowing the passage of liquid.
In another embodiment, the present invention provides a self-sealing barrier composition comprising a sintered porous matrix, the sintered porous matrix comprising a self-sealing surface and an indicator surface in facing opposition to the self-sealing surface. The self-sealing surface of the barrier composition comprises at least one absorbent material, and the indicator surface comprises at least one color change indicator. Absorbent materials and color change indicators suitable for use in barrier compositions comprising a self-sealing surface and an indicator surface in facing opposition to the self-sealing surface comprise any of the same described herein.
An indicator surface disposed opposite of a self-sealing surface, in some embodiments, is operable to determine if the self-sealing surface has completely sealed when contacted with an aqueous and/or organic liquid. In cases where the self-sealing surface does not sufficiently seal, the opposing indicator surface can detect the presence of liquid that has breached the self-sealing surface which could potentially contaminate a downstream device
In some embodiments, the self-sealing surface also comprises a color change indicator. In some embodiments, the color change indicator of the self-sealing surface is the same as the color change indicator of the indicator surface. In other embodiments, the color change indicator of the self-sealing surface is different than the color change indicator of the indicator surface. A self-sealing surface comprising a color change indicator can detect whether the self-sealing surface has been contacted by an aqueous and/or organic liquid.
In another embodiment, the indicator surface further comprises at least one surfactant. Surfactants suitable for indicator surfaces, according to embodiments of the present invention, comprise any of the surfactants provided herein. Indicator surfaces comprising at least one surfactant, in some embodiments, demonstrate advantageous wicking properties allowing a rapid response to an aqueous and/or organic liquid contacting the indicator surface.
FIG. 2 illustrates a self-sealing barrier composition comprising a sintered porous matrix, the sintered porous matrix comprising at least one plastic, a self-sealing surface, and an indicator surface in facing opposition to the self-sealing surface. The barrier composition (200) of FIG. 2 comprises a self-sealing surface (202) and an indicator surface (204) in facing opposition to the self-sealing surface (202). A sintered porous plastic (206) is disposed between the self-sealing surface (202) and the indicator surface (204).
Self-sealing barrier compositions of the present invention, in some embodiments, exhibit a number of desirable properties including rapid response times, substantially no contamination of liquid samples, biocompatibility, and the ability to withstand high back pressures. In some embodiments, self-sealing barrier compositions can tolerate back pressures of greater than about 1, 2, or 5 pounds per square inch (psi). In some embodiments, self-sealing barrier compositions can tolerate back pressures up to about 20 psi. Moreover, air flow rate through self-sealing barrier compositions of the present invention, in some embodiments, is greater than about 16, 18, or 20 ml/minute. Self-sealing barrier compositions of the present invention, in some embodiments, are also stable when exposed to ambient environmental conditions. Self-sealing barrier compositions, in some embodiments, do not substantially respond to atmospheric moisture. In some embodiments, self-sealing barrier compositions of the present invention produce no color change in response to atmospheric moisture. As a result, self-sealing barrier compositions of the present invention can have a prolonged shelf life and require no special packaging or storage conditions.
Moreover, in providing a sintered porous matrix comprising an absorbent material, self-sealing barrier compositions of the present invention, in some embodiments, have substantially no absorbent particles disposed in the pores of the matrix. The absorbent material forms part of the sintered matrix. In some embodiments, a self-sealing barrier composition comprises no absorbent particles disposed in the pores of the matrix.
Hydrophobic Barrier Compositions Comprising Color Change Indicators
In addition to self-sealing barrier compositions, the present invention provides hydrophobic barrier compositions. In one embodiment, a hydrophobic barrier composition comprises a sintered porous matrix, the sintered porous matrix comprising at least one plastic and at least one color change indicator wherein the barrier material is substantially free of any absorbent or self-sealing material. In some embodiments, the sintered porous matrix of a barrier composition does not comprise any absorbent or self-sealing material. As a result, hydrophobic barrier compositions of the present invention are not self-sealing.
Turning now to components that can be included in hydrophobic barrier compositions of the present invention, hydrophobic barrier compositions of the present invention comprise at least one plastic. In some embodiments, sintered porous matrices of hydrophobic barrier compositions of the present invention comprise a plurality of plastics.
Plastics suitable for use in sintered porous matrices of hydrophobic barrier compositions, in some embodiments, comprise polyolefins, polyamides, polyesters, rigid polyurethanes, polyacrylonitriles, polycarbonates, polyvinylchloride, polymethylmethacrylate, polyvinylidene fluoride, polytetrafluoroethylene, polyethersulfones, polystyrenes, polyether imides, polyetheretherketones, polysulfones, or combinations or copolymers thereof.
In some embodiments, a polyolefin comprises polyethylene, polypropylene, and/or copolymers thereof. Polyethylene, in one embodiment, comprises HDPE. HDPE, as used herein, refers to polyethylene having a density ranging from about 0.92 g/cm3 to about 0.97 g/cm3. In some embodiments, HDPE has a degree of crystallinity (% from density) ranging from about 50 to about 90. In another embodiment, polyethylene comprises UHMWPE. UHMWPE, as used herein, refers to polyethylene having a molecular weight greater than 1,000,000.
In addition to at least one plastic, hydrophobic barrier compositions of the present invention comprise at least one color change indicator. A color change indicator, according to embodiments of the present invention, is operable to at least partially change the color of the sintered porous matrix when contacted with an aqueous and/or organic liquid. In some embodiments, the color change indicator changes the sintered porous matrix from a first color to a second color when contacted with an aqueous and/or organic liquid. In other embodiments, the color change indicator changes the sintered porous matrix from colorless or white to colored. In a further embodiment, the color change indicator changes the sintered porous matrix from a first shade of a color to a different shade of the same color. The color change of the sintered porous matrix, according to embodiments of the present invention, depends on the identity of the color change indicator selected.
In some embodiments, a color change indicator comprises an inorganic or organic dye, including food grade dyes, azo compounds, or azo dyes. In some embodiments, a color change indicator does not comprise inorganic salts, including transition metal salts. Additionally, in some embodiments, a color change indicator does not comprise a conjugate or complex that changes color upon the binding of an analyte. In some embodiments, hydrophobic barrier compositions of the present invention do not comprise proteins or other biological molecules.
Color change indicators, according to some embodiments, demonstrate a pH dependency on the color produced. As a result, color change indicators, in some embodiments, indicate not only liquid contact with the barrier composition but the relative pH of the contacting liquid as well. Color change indicators demonstrating a pH dependency, in some embodiments, comprise methyl violet, eosin yellow, malachite green, thymol blue, methyl yellow, bromophenol blue, congo red, methyl orange, methyl orange in xylene cyanole solution, bromocresol green, methyl red, litmus, bromocresol purple, bromophenol red, bromothymol blue, phenol red, neutral red, naphtholphthalein, cresol red, phenolphthalein, thymolphthalein, alkali blue, Alizarin Yellow R, indigo carmine, epsilon blue, or combinations thereof.
A sintered porous matrix of a hydrophobic barrier composition, according to some embodiments, comprises at least one plastic in an amount ranging from about 95 weight percent to about 99.99 weight percent of the matrix. In other embodiments, a sintered porous matrix comprises at least one plastic in an amount ranging from about 98 weight percent to about 99.9 weight percent of the matrix.
In addition to the at least one plastic, a sintered porous matrix of a hydrophobic barrier composition comprises at least one color change indicator in an amount ranging from about 0.001 weight percent to about 2 weight percent of the matrix. In other embodiments, a sintered porous matrix comprises at least one color change indicator in an amount ranging from about 0.01 weight percent to about 1 weight percent of the matrix. In a further embodiment, a sintered porous matrix comprises at least one color change indicator in an amount ranging from about 0.05 weight percent to about 0.5 weight percent of the matrix.
A sintered porous matrix of a hydrophobic barrier composition comprising at least one plastic and at least one color change indicator, in some embodiments, has a porosity ranging from about 10% to about 90%. In another embodiment, a sintered porous matrix has a porosity ranging from about 20% to about 80% or from about 30% to about 70%. In a further embodiment, a sintered porous matrix has a porosity ranging from about 40% to about 60%.
A sintered porous matrix of a hydrophobic barrier composition comprising at least one plastic and at least one color change indicator, has an average pore size ranging from about 35 μm to about 200 μm. In other embodiments, a sintered porous matrix has an average pore size ranging from about 40 μm to about 150 μm, from about 60 μm to 100 μm, or from about 70 μm to about 90 μm. In another embodiment, a porous sintered matrix has an average pore size less than about 1 μm. In one embodiment, a porous sintered matrix has an average pore size ranging from about 0.1 μm to about 1 μm.
In some embodiments, hydrophobic barrier compositions have a water intrusion pressure of greater than about 0.5 psi.
In another embodiment, the present invention provides a hydrophobic barrier composition comprising at least one plastic layer comprising a first plastic and at least one indicator layer comprising at least one color change indicator. In one embodiment, the indicator layer further comprises a second plastic. In some embodiments, the first plastic and the second plastic are the same. In other embodiments, the first plastic and the second plastic are different. Plastics suitable for use in the plastic layer and indicator layer, according to embodiments of the present invention comprise any of the plastics described herein. Moreover, color change indicators suitable for use in the indicator layer comprise any of the color change indicators described herein.
In some embodiments, the at least one indicator layer is adjacent to the at least one plastic layer. In other embodiments, the at least one indicator layer is spaced apart from the at least one plastic layer. An indicator layer adjacent to or spaced apart from a plastic layer, in some embodiments, is operable to detect the intrusion of liquid into the hydrophobic barrier composition which could lead to contamination of downstream devices and apparatus.
In another embodiment, the indicator layer further comprises at least one surfactant. Surfactants, in some embodiments, comprise anionic surfactants, cationic surfactants, nonionic surfactants, amphoteric surfactants or mixtures thereof. In some embodiments, anionic surfactants comprise alkyl sulfates, alkylbenzenesulfonates, ether sulfates, a-olefin sulfonates, ester sulfonates, phosphate esters, acyl taurates, soaps, ether carboxylates, or mixtures thereof. Cationic surfactants, in some embodiments, comprise alkyl quaternary ammonium salts, bezylalkyldimethylammonium salts, amidoamine quaternaries, quaternary imidazolium compounds, ester quaternary compounds, or mixtures thereof. In some embodiments, nonionic surfactants comprise ethoxylated alcohols, ethoxylated alkylphenols, polyethylene glycol esters, fatty acid alkanolamides, ethoxylated alkanolamides, ethoxylated amines, esters of polyhydroxy compounds, ethoxylated esters, ethylene oxide/propylene oxide copolymers, amine oxides, or mixtures thereof. Amphoteric surfactants, in some embodiments, comprise alkylamino acids, alkylbetaines, alkylaminobetains, imidazoline-derived surfactants, sulfur containing amphoterics, lecithin, or mixtures thereof. In some embodiments, surfactants suitable for use in embodiments of the present invention comprise Geropon�, Rhodacal�, and Rhodafac� commercially available from Rhodia or Paris France, Pluronic� commercially available from BASF of Florham Park, N.J., and Zonyl� commercially available from DuPont of Wilmington, Del.
Indicator layers of hydrophobic barrier compositions comprising at least one surfactant, in some embodiments, demonstrate advantageous wicking properties allowing a rapid response to an aqueous and/or organic liquid contacting the indicator layer.
In some embodiments, plastic layers can demonstrate any construction described herein for sintered porous matrices of hydrophobic barrier compositions. Plastic layers, according to some embodiments, for example, can demonstrate pore sizes and/or porosities consistent with any the sintered porous matrices provided herein.
In some embodiments, indicator layers can demonstrate any construction described herein for sintered porous matrices of hydrophobic barrier compositions. Indicator layers, according to some embodiments, for example, can demonstrate pore sizes and/or porosities consistent with any the sintered porous matrices provided herein.
In some embodiments, a plastic layer is constructed independently from an indicator layer. In such embodiments, the plastic layer and the indicator layer can display similar pore sizes and/or porosities or different pore sizes and/or porosities.
FIG. 3 illustrates a hydrophobic barrier composition comprising a sintered porous matrix comprising at least one plastic layer and at least one indicator layer. The barrier composition (300) illustrated in FIG. 3 comprises a indicator layer (302) adjacent to the plastic layer (304). Liquid intrusion into the plastic layer can contact the indicator layer thereby alerting a user that the hydrophobic barrier composition has been compromised.
In a further embodiment, the present invention provides a hydrophobic barrier composition comprising a sintered porous matrix, the sintered porous matrix comprising a first surface and a second surface in facing opposition to the first surface, the first surface comprising at least one plastic and the second surface comprising at least one color change indicator. Plastics and color change indicators suitable for use in hydrophobic barrier compositions comprising an indicator surface in facing opposition to a plastic surface comprise any of the same described herein.
In some embodiments, the second surface of a hydrophobic barrier composition further comprises at least one surfactant.
In another embodiment, the first surface further comprises a color change indicator. In some embodiments, the color change indicator of the first surface is the same as the color change indicator of the second surface. In other embodiments, the color change indicator of the first surface is different from the color change indicator of the second surface.
Hydrophobic barrier compositions of the present invention, in some embodiments, exhibit a number of desirable properties including rapid response times, substantially no contamination of liquid samples, biocompatibility, and the ability to withstand high back pressures. In some embodiments, hydrophobic barrier compositions can tolerate back pressures of greater than about 1, 2, or 5 pounds per square inch (psi). Moreover, air flow rate through hydrophobic barrier compositions of the present invention, in some embodiments, is greater than about 16, 18, or 20 ml/minute. Hydrophobic barrier compositions of the present invention, in some embodiments, are also stable when exposed to ambient environmental conditions. Hydrophobic barrier compositions, in some embodiments, do not substantially respond to atmospheric moisture. In some embodiments, hydrophobic barrier compositions of the present invention produce no color change in response to atmospheric moisture. As a result, hydrophobic barrier compositions of the present invention can have a prolonged shelf life and require no special packaging or storage conditions.
Hydrophilic Compositions Comprising Color Change Indicators
In another embodiment, the present invention provides a hydrophilic composition comprising a sintered porous matrix, the sintered porous matrix comprising at least one plastic, at least one color change indicator, and at least one surfactant
Turning now to components that can be included in hydrophilic compositions of the present invention, hydrophilic compositions of the present invention comprise at least one plastic. In some embodiments, hydrophilic compositions comprise a plurality of plastics.
Plastics suitable for use in sintered porous matrices of hydrophilic compositions, in some embodiments, comprise polyolefins, polyamides, polyesters, rigid polyurethanes, polyacrylonitriles, polycarbonates, polyvinylchloride, polymethylmethacrylate, polyvinylidene fluoride, polytetrafluoroethylene, polyethersulfones, polystyrenes, polyether imides, polyetheretherketones, polysulfones, or combinations or copolymers thereof.
In addition to at least one plastic, hydrophilic compositions of the present invention comprise at least one color change indicator. A color change indicator, according to embodiments of the present invention, is operable to at least partially change the color of the sintered porous matrix when contacted with an aqueous and/or organic liquid. In some embodiments, the color change indicator changes the sintered porous matrix from a first color to a second color when contacted with an aqueous and/or organic liquid. In other embodiments, the color change indicator changes the sintered porous matrix from colorless or white to colored. In a further embodiment, the color change indicator changes the sintered porous matrix from a first shade of a color to a different shade of the same color. The color change of the sintered porous matrix, according to embodiments of the present invention, depends on the identity of the color change indicator selected.
In some embodiments, a color change indicator comprises an inorganic or organic dye, including food grade dyes, azo compounds, or azo dyes. In some embodiments, a color change indicator does not comprise inorganic salts, including transition metal salts. Additionally, in some embodiments, a color change indicator does not comprise a conjugate or complex that changes color upon the binding of an analyte. In some embodiments, hydrophilic compositions of the present invention do not comprise proteins or other biological molecules.
Hydrophilic compositions of the present invention additionally comprise at least one surfactant. Surfactants, in some embodiments of hydrophilic compositions, comprise anionic surfactants, cationic surfactants, nonionic surfactants, amphoteric surfactants or mixtures thereof. In some embodiments, anionic surfactants comprise alkyl sulfates, alkylbenzenesulfonates, ether sulfates, α-olefin sulfonates, ester sulfonates, phosphate esters, acyl taurates, soaps, ether carboxylates, or mixtures thereof. Cationic surfactants, in some embodiments, comprise alkyl quaternary ammonium salts, bezylalkyldimethylammonium salts, amidoamine quaternaries, quaternary imidazolium compounds, ester quaternary compounds, or mixtures thereof. In some embodiments, nonionic surfactants comprise ethoxylated alcohols, ethoxylated alkylphenols, polyethylene glycol esters, fatty acid alkanolamides, ethoxylated alkanolamides, ethoxylated amines, esters of polyhydroxy compounds, ethoxylated esters, ethylene oxide/propylene oxide copolymers, amine oxides, or mixtures thereof. Amphoteric surfactants, in some embodiments, comprise alkylamino acids, alkylbetaines, alkylaminobetains, imidazoline-derived surfactants, sulfur containing amphoterics, lecithin, or mixtures thereof. In some embodiments, surfactants suitable for use in embodiments of the present invention comprise Geropon�, Rhodacal�, and Rhodafac� commercially available from Rhodia or Paris France, Pluronic� commercially available from BASF of Florham Park, N.J., and Zonyl� commercially available from DuPont of Wilmington, Del.
In some embodiments, a sintered porous matrix of a hydrophilic composition comprises at least one plastic in an amount of at least 90 weight percent of the matrix. A sintered porous matrix of a hydrophilic composition, according to some embodiments, comprises at least one plastic in an amount ranging from about 95 weight percent to about 99.99 weight percent of the matrix. In other embodiments, a sintered porous matrix comprises at least one plastic in an amount ranging from about 97 weight percent to about 99.9 weight percent of the matrix.
A sintered porous matrix of a hydrophilic composition of the present invention, in some embodiments, comprises at least one surfactant in an amount ranging from about 0.001 weight percent to about 3 weight percent of the matrix. In other embodiments, a sintered porous matrix comprises at least one surfactant in an amount ranging from about 0.01 weight percent to about 2 weight percent of the matrix. In a further embodiment, a sintered porous matrix comprises a at least one surfactant in an amount ranging from about 0.1 weight percent to about 1 weight percent of the matrix.
A sintered porous matrix of a hydrophilic composition comprising at least one plastic, at least one color change indicator, and at least one surfactant, in some embodiments, has a porosity ranging from about 10% to about 90%. In another embodiment, a sintered porous matrix has a porosity ranging from about 20% to about 80% or from about 30% to about 70%. In a further embodiment, a sintered porous matrix has a porosity ranging from about 40% to about 60%.
A sintered porous matrix of a hydrophilic composition comprising at least one plastic, at least one color change indicator, and at least one surfactant has an average pore size ranging from about 35 μm to about 200 μm. In other embodiments, a sintered porous matrix has an average pore size ranging from about 40 μm to about 150 μm, from about 60 μm to 100 μm, or from about 70 μm to about 90 μm. In another embodiment, a porous sintered matrix has an average pore size less than about 1 um. In one embodiment, a porous sintered matrix has an average pore size ranging from about 0.1 μm to about 1 μm.
Methods of Producing Self-Sealing Barrier Compositions
In another aspect, the present invention provides methods of producing self-sealing barrier compositions. In one embodiment, a method of producing a self-sealing barrier composition comprises providing particles of at least one plastic, providing particles of at least one absorbent material, providing particles of at least one color change indicator, and cosintering the particles of the at least one plastic, the at least one absorbent material, and the at least one color change indicator.
In some embodiments, particles of at least one plastic, particles of at least one absorbent material, and particles of at least one color change indicator are mixed in a desired ratio (weight percent) to product a substantially uniform mixture. The substantially uniform mixture of plastic, absorbent material, and color change indicator particles are disposed in a mold and sintered. The shape of the mold can be any desired shape.
Plastic particles, in some embodiments, have average sizes ranging from about 1 μm to about 1 mm. In another embodiment, plastic particles have average sizes ranging from about 10 μm to about 900 μm, from about 50 μm to about 500 μm, or from about 100 μm to about 400 μm. In a further embodiment, plastic particles have an average size ranging from about 200 μm to about 300 μm. In some embodiments, plastic particles have average sizes less than about 1 μm or greater than about 1 mm.
Particles of an absorbent material, according to some embodiments, have average sizes ranging from about 1 μm to about 500 μm or from about 10 μm to about 400 μm. In another embodiment, particles of an absorbent material have average sizes ranging from about 50 μm to about 300 μm. In a further embodiment, particles of an absorbent material have average sizes ranging from about 100 μm to about 200 μm. In some embodiments, particles of an absorbent material have average sizes less than about 1 μm or greater than about 500 μm.
Particles of a color change indicator, according to some embodiments, have average sizes ranging from about 1 μm to about 500 μm or from about 10 μm to about 400 μm. In another embodiment, particles of a color change indicator have average sizes ranging from about 50 μm to about 300 μm. In a further embodiment, particles of a color change indicator have average sizes ranging from about 100 μm to about 200 μm. In some embodiments, particles of a color change indicator have average sizes less than about 1 μm or greater than about 500 μm.
Particles of at least one plastic, at least one absorbent material, and at least one color change indicator, in some embodiments, are sintered at a temperature ranging from about 200� F. to about 700� F. In some embodiments, plastic, absorbent material, and color change indicator particles are sintered at a temperature of ranging from about 300� F. to about 500� F. The sintering temperature, according to embodiments of the present invention, is dependent upon and selected according to the identity of the plastic, absorbent material, and color change indicator particles.
Particles of at least one plastic, at least one absorbent material, and at least one color change indicator, in some embodiments, are sintered for a time period ranging from about 30 seconds to about 30 minutes. In other embodiments, particles of at least one plastic, at least one absorbent material, and at least one color change indicator are sintered for a time period ranging from about 30 seconds to about 15 minutes or from about 1 minute to about 10 minutes. In some embodiments, the sintering process comprises heating, soaking, and/or cooking cycles. Moreover, in some embodiments, sintering of particles of at least one plastic, at least one absorbent material, and at least one color change indicator is administered under ambient pressure (1 atm). In other embodiments, sintering particles of at least one plastic, at least one absorbent material, and at least one color change indicator is administered under pressures greater than ambient pressure.
In another embodiment, a method of producing a self-sealing barrier composition comprises disposing particles of at least one absorbent material in a first part of a mold, disposing particles of at least one color change indicator in a second part of the mold adjacent to the first part of the mold, and sintering the particles of the at least one absorbent material and the at least one color change indicator. In some embodiments, particles of a first plastic are mixed with particles of at the least one absorbent material prior to sintering. In some embodiments, particles of a second plastic are mixed with particles of the at least one color change indicator prior to sintering. In some embodiments, the first plastic and second plastic are the same. In other embodiments, the first plastic and second plastic are different.
In one embodiment, for example, particles of an absorbent material and particles of a first plastic are mixed in a desired ratio (weight percent) to produce a substantially uniform mixture. The mixture is disposed in the bottom half of a mold. Particles of a color change indicator and particles of a second plastic are mixed in a desired ratio (weight percent) to produce a substantially uniform mixture. The mixture of color change indicator and second plastic particles is disposed in the top half of the mold adjacent to the mixture of absorbent particles and first plastic particles. The absorbent particles, first plastic particles, color change indicator particles, and second plastic particles are subsequently sintered to produce a self-sealing barrier composition of the present invention. The barrier composition produced, in some embodiments, comprises a sintered porous matrix comprising a self-sealing layer and an indicator as described herein. The barrier composition produced, in other embodiments, comprises a sintered porous matrix comprising a self-sealing surface and an indicator surface as described herein.
First and second plastic particles, in some embodiments, individually have average sizes ranging from about 1 μm to about 1 mm. In another embodiment, plastic particles have average sizes ranging from about 10 μm to about 900 μm, from about 50 μm to about 500 μm, or from about 100 μm to about 400 μm. In a further embodiment, plastic particles have an average size ranging from about 200 μm to about 300 μm. In some embodiments, plastic particles have average sizes less than about 1 μm or greater than about 1 mm.
Absorbent material particles, color change indicator particles, first plastic particles, and second plastic particles, in some embodiments are sintered at a temperature ranging from about 200� F. to about 700� F. In some embodiments, absorbent particles, color change indicator particles, first plastic particles, and second plastic particles are sintered at a temperature of ranging from about 300� F. to about 500� F. The sintering temperature, according to embodiments of the present invention, is dependent upon and selected according to the identity of the plastic, absorbent material, and color change indicator particles.
Absorbent material particles, color change indicator particles, first plastic particles, and second plastic particles, in some embodiments, are sintered for a time period ranging from about 30 seconds to about 30 minutes. In other embodiments, absorbent material particles, color change indicator particles, first plastic particles, and second plastic particles are sintered for a time period ranging from about 30 seconds to about 15 minutes or from about 1 minute to about 10 minutes. In some embodiments, the sintering process comprises heating, soaking, and/or cooking cycles. Moreover, in some embodiments, sintering of absorbent material particles, color change indicator particles, first plastic particles, and second plastic particles is administered under ambient pressure (1 atm). In other embodiments, sintering is administered under pressures greater than ambient pressure.
In some embodiments, particles of at least one surfactant are mixed with particles of the at least one color change indicator prior to sintering. In other embodiments, particles of a second plastic are at least partially coated with at least one surfactant prior to sintering. In such embodiments, the surfactant can be applied to the second plastic particles as a liquid.
Particles of a surfactant, according to some embodiments, have average sizes ranging from about 0.1 μm to about 200 μm or from about 1 μm to about 150 μm. In another embodiment, particles of a surfactant have average sizes ranging from about 25 μm to about 100 μm. In a further embodiment, particles of a surfactant have average sizes ranging from about 30 μm to about 50 μm. In some embodiments, particles of a surfactant have average sizes greater than about 200 μm or less than about 0.1 μm. Compositions comprising surfactant particles are sintered in accordance with any of the embodiments provided herein.
In other embodiments, particles of a second color change indicator are mixed with particles of the at least one absorbent material prior to sintering. In some embodiments, particles of the at least one color change indicator and particles of the second color change indicator are the same. In another embodiment, particles of the at least one color change indicator and particles of the second color change indicator are different.
Methods of Producing Hydrophobic Barrier Compositions
In another aspect, the present invention provides methods of producing hydrophobic barrier compositions. In one embodiment, a method of producing a hydrophobic barrier composition comprises providing particles of at least one plastic, providing particles of at least one color change indicator, and cosintering the particles of the at least one plastic and the at least one color change indicator.
In some embodiments, particles of at least one plastic and particles of at least one color change indicator are mixed in a desired ratio (weight percent) to produce a substantially uniform mixture. The substantially uniform mixture of plastic and color change indicator particles is disposed in a mold and sintered. The shape of the mold can be any desired shape.
Particles of at least one plastic and at least one color change indicator, in some embodiments, are sintered at a temperature ranging from about 200� F. to about 700� F. In some embodiments, plastic and color change indicator particles are sintered at a temperature of ranging from about 300� F. to about 500� F. The sintering temperature, according to embodiments of the present invention, is dependent upon and selected according to the identity of the plastic and color change indicator particles.
Particles of at least one plastic and at least one color change indicator, in some embodiments, are sintered for a time period ranging from about 30 seconds to about 30 minutes. In other embodiments, particles of at least one plastic and at least one color change indicator are sintered for a time period ranging from about 30 seconds to about 15 minutes or from about 1 minute to about 10 minutes. In some embodiments, the sintering process comprises heating, soaking, and/or cooking cycles. Moreover, in some embodiments, sintering of particles of at least one plastic and at least one color change indicator is administered under ambient pressure (1 atm). In other embodiments, sintering particles of at least one plastic and at least one color change indicator is administered under pressures greater than ambient pressure.
In a further embodiment, a method for producing a hydrophobic barrier material comprises disposing particles of a first plastic in first part of a mold, disposing particles of at least one color change indicator in a second part of the mold adjacent to the first part of the mold, and sintering the particles of the first plastic and the at least one color change indicator. In some embodiments, particles of a second plastic are mixed with particles of the at least one color change indicator prior to sintering. In one embodiment, the first and second plastics are the same. In another embodiment, the first and second plastics are different.
In one embodiment, for example, particles of a first plastic are disposed in the bottom half of a mold. Particles of a color change indicator and particles of a second plastic are mixed in a desired ratio (weight percent) to produce a substantially uniform mixture. The mixture of color change indicator and second plastic particles is disposed in the top half of the mold adjacent to the first plastic particles. The first plastic particles, color change indicator particles, and second plastic particles are subsequently sintered to produce a hydrophobic barrier composition of the present invention. The hydrophobic barrier composition produced, in some embodiments, comprises a sintered porous matrix comprising a plastic layer and an indicator layer comprising a color change indicator as described herein. The hydrophobic barrier composition produced, in other embodiments, comprises a sintered porous matrix comprising a first surface and a second surface, the first surface comprising at least one plastic and the second surface comprising at least one color change indicator as described herein.
Color change indicator particles, first plastic particles, and second plastic particles, in some embodiments are sintered at a temperature ranging from about 200� F. to about 700� F. In some embodiments, color change indicator particles, first plastic particles, and second plastic particles are sintered at a temperature of ranging from about 300� F. to about 500� F. The sintering temperature, according to embodiments of the present invention, is dependent upon and selected according to the identity of the plastic, absorbent material, and color change indicator particles.
Color change indicator particles, first plastic particles, and second plastic particles, in some embodiments, are sintered for a time period ranging from about 30 seconds to about 30 minutes. In other embodiments, color change indicator particles, first plastic particles, and second plastic particles are sintered for a time period ranging from about 30 seconds to about 15 minutes or from about 1 minutes to about 10 minute. In some embodiments, the sintering process comprises heating, soaking, and/or cooking cycles. Moreover, in some embodiments, sintering of color change indicator particles, first plastic particles, and second plastic particles is administered under ambient pressure (1 atm). In other embodiments, sintering is administered under pressures greater than ambient pressure.
Particles of a surfactant, according to some embodiments, have average sizes ranging from about 0.1 μm to about 200 μm or from about 1 μm to about 150 μm. In another embodiment, particles of a surfactant have an average sizes ranging from about 25 μm to about 100 μm. In a further embodiment, particles of a surfactant have average sizes ranging from about 30 μm to about 50 μm. In some embodiments, particles of a surfactant have average sizes greater than about 200 μm or less than about 0.1 μm. Compositions comprising surfactant particles are sintered in accordance with any of the embodiments provided herein.
Methods of Producing Hydrophilic Compositions
In another aspect, the present invention provides methods of producing hydrophilic compositions. In one embodiment, a method of producing a hydrophilic composition comprises providing particles of at least one plastic, providing particles of at least one color change indicator, providing particles of at least one surfactant, and cosintering the particles of the at least one plastic, the at least one color change indicator, and at least one surfactant.
In some embodiments, particles of at least one plastic, particles of at least one color change indicator, and particles of at least one surfactant are mixed in a desired ratio (weight percent) to produce a substantially uniform mixture. The substantially uniform mixture of plastic, color change indicator, and surfactant particles is disposed in a mold and sintered. The shape of the mold can be any desired shape.
Particles of a surfactant, according to some embodiments, have average sizes ranging from about 0.1 μm to about 200 μm or from about 1 μm to about 150 μm. In another embodiment, particles of a surfactant have average sizes ranging from about 25 μm to about 100 μm. In a further embodiment, particles of a surfactant have average sizes ranging from about 30 μm to about 50 μm. In some embodiments, particles of a surfactant have average sizes greater than about 200 μm or less than about 0.1 μm
Particles of at least one plastic, at least one color change indicator, and at least one surfactant, in some embodiments, are sintered at a temperature ranging from about 200� F. to about 700� F. In some embodiments, plastic, color change indicator, and surfactant particles are sintered at a temperature of ranging from about 300� F. to about 500� F. The sintering temperature, according to embodiments of the present invention, is dependent upon and selected according to the identity of the plastic, color change indicator, and surfactant particles.
Particles of at least one plastic, at least one color change indicator, and at least one surfactant, in some embodiments, are sintered for a time period ranging from about 30 seconds to about 30 minutes. In other embodiments, particles of at least one plastic, at least one color change indicator, and at least one surfactant are sintered for a time period ranging from about 30 seconds to about 15 minutes or from about 1 minute to about 10 minutes. In some embodiments, the sintering process comprises heating, soaking, and/or cooking cycles. Moreover, in some embodiments, sintering of particles of at least one plastic and at least one color change indicator is administered under ambient pressure (1 atm). In other embodiments, sintering particles of at least one plastic and at least one color change indicator is administered under pressures greater than ambient pressure.
In another embodiment, a method of producing a hydrophilic composition comprises providing particles of at least one plastic, at least partially coating the particles of the at least one plastic with at least one surfactant, providing particles of at least one color change indicator, and sintering the particles of the at least one plastic and particles of the at least one color change indicator. Plastic particles coated with at least one surfactant and particles of at least one color change indicator, in some embodiments, are sintered in accordance with any of the methods provided herein. In some embodiments, particles of color change indicators are at least partially coated with at least one surfactant prior to sintering.
Apparatus Comprising Barrier Compositions
In another aspect, the present invention provides apparatus comprising barrier compositions of the present invention. In one embodiment, an apparatus comprises a pipette tip, the pipette tip comprises a hollow tube comprising first and second open ends, a center member disposed between the first and second ends, the center member comprising a barrier composition according to any of the embodiments provided herein. In some embodiments, the pipette tip has a volume of about 10 μl or about 20 μl. In other embodiments, the pipette tip has a sample volume of about 50 μl or about 100 μl. In another embodiment, the pipette tip has a sample volume of about 200 μl, about 250 μl, about 500 μl, or about 1 ml. In a further embodiment, the pipette tip has a sample volume less than about 10 μl or greater than about 1 ml or about 5 ml. In some embodiments, the pipette tip has a sample volume of about 1 μl or about 5 μl.
FIG. 4 illustrates a pipette tip comprising a barrier composition of the present invention. The pipette tip (400) comprises a tapering, hollow tubular member (402), the hollow tubular member, in some embodiments, comprising a non-reactive material such as glass, polyethylene, or other polymeric material. The hollow tubular member (402) is open at a first end (404) and a second end (406), the first (404) and second (406) ends in facing opposition. A barrier composition (408) of the present invention is disposed in the hollow tubular member (402) to define a liquid sample chamber (410) between barrier composition (408) and the first end (404). The barrier composition is additionally spaced apart from the second end (406) to define a chamber (412) between the barrier composition (408) and the second end (406). The second end (406) is releasably secured to the a suitable suction device (414) in any manner known to one of skill in the art.
In another embodiment, barrier compositions of the present invention find application as flow control devices in various apparatus such as aspirators. In one embodiment, an aspirator comprises a receptacle, a lid, and a barrier composition according to any of the embodiments provided herein. The barrier composition is disposed in the receptacle. Moreover, the lid further comprises an inlet and an outlet wherein outlet is operable to be connected to a suction or vacuum line. In some embodiments, a self-sealing barrier composition covers the outlet such that when sufficient liquid has been collected in the receptacle, contact of the liquid to the barrier composition results in self-sealing of the barrier composition. The sealing of the barrier composition prevents or inhibits further aspiration.
In another embodiment, barrier compositions of the present invention find application in needle apparatus such as an indwelling needle as described in U.S. patent application Ser. No. 11/065,579; a flashback blood collection needle as described in U.S. patent application Ser. No. 11/141,588; a blood collection set as described in U.S. patent application Ser. No. 11/141,446; and a luer cap associated with an IV set. In these applications, barrier compositions of the present invention are incorporated as vents, allowing the passage of air and other gases while blocking the passage of liquids such as blood.
Self-Sealing Barrier Composition Comprising Color Change Indicator
Powdered HDPE having an average particle size of about 150 μm was mixed with carboxymethylcellulose (CMC), and food dye erioglaucine producing a substantially uniform mixture of 84.95 weight percent polyethylene, 15 weight percent CMC, and 0.05 weight percent food dye erioglaucine. The resulting mixture was disposed in a metal mold and heated to 350� F. for about three minutes and subsequently cooled to room temperature in about five minutes. The resulting self-sealing barrier composition had an average pore size of about 40 μm and a white color. When contacted with an aqueous liquid, the barrier composition turned a blue color.
Hydrophobic Barrier Composition Comprising Color Change Indicator
Powdered HDPE having an average particle size of about 30 μm was mixed with food dye erioglaucine producing a substantially uniform mixture of 99.95 weight percent polyethylene and 0.05 weight percent food dye erioglaucine. The resulting mixture was disposed in a metal mold and heated to 350� F. for about three minutes and subsequently cooled to room temperature in about five minutes. The resulting self-sealing barrier composition had an average pore size of about 10 μm and a white color. When contacted with an aqueous liquid, the barrier composition turned a blue color and demonstrated a water contact angle greater than 90�.
Layered Self-Sealing Barrier Composition Comprising Color Change Indicator
Powdered HDPE having an average particle size of about 30 μm is mixed with food dye erioglaucine producing a substantially uniform mixture of 99.95 weight percent polyethylene and 0.05 weight percent food dye erioglaucine. The polyethylene/food dye mixture is disposed in the bottom part of a metal mold.
Powdered HDPE having an average particle size of about 150 μm is combined with carboxymethylcellulose (CMC), and food dye erioglaucine producing a substantially uniform mixture of 84.95 weight percent polyethylene, 15 weight percent CMC, and 0.05 weight percent food dye erioglaucine. The resulting mixture is disposed in the top half of the metal mold adjacent to the bottom half. The mold is heated to 350� F. for about three minutes and is subsequently cooled to room temperature in about five minutes. The resulting barrier composition has a first layer demonstrating hydrophobic color changing properties and a second layer demonstrating self-sealing color change properties.
Powdered HDPE having an average particle size of about 150 μm is mixed with sodium dodecyl sulfate (Sigma-Aldrich) and food dye erioglaucine producing a substantially uniform mixture of 99.5 weight percent polyethylene, 0.45 weight percent sodium dodecyl sulfate, and 0.05 weight percent erioglaucine. The polyethylene/surfactant/food dye mixture is disposed in the bottom half of a metal mold.
Powdered HDPE having an average particle size of about 150 μm is mixed with carboxymethylcellulose (CMC), and food dye erioglaucine producing a substantially uniform mixture of 84.95 weight percent polyethylene, 15 weight percent CMC, and 0.05 weight percent food dye erioglaucine. The resulting mixture is disposed in the top half of the metal mold adjacent to the bottom half. The mold is heated to 350� F. for about three minutes and subsequently cooled to room temperature in about five minutes. The resulting barrier composition has a first layer demonstrating hydrophilic color changing properties and a second layer demonstrating self-sealing color change properties.
Powdered HDPE having an average particle size of about 150 μm was mixed with sodium dodecyl sulfate (Sigma-Aldrich) and food dye erioglaucine to produce a substantially uniform mixture of 99.5 weight percent polyethylene, 0.45 weight percent sodium dodecyl sulfate, and 0.05 weight percent erioglaucine. The resulting mixture was disposed in a metal mold and heated to 350� F. for about three minutes and subsequently cooled to room temperature in about five minutes. The resulting hydrophilic composition had an average pore size of about 40 μm and a white color. Aqueous solution wicks into the hydrophilic composition upon contact. Moreover, the hydrophilic composition turned blue when contacted with an aqueous solution.
Pipette Tip Comprising a Self-Sealing Barrier Composition
The self-sealing barrier composition of Example 1 was disposed in a pipette tip by inserting the self-sealing barrier composition through the end of the pipette tip operable to receive the pipettor. Sufficient pressure was applied to the self-sealing barrier composition during insertion to ensure that the barrier composition formed a seal with the interior surfaces of the pipette tip. After insertion of the barrier medium into the pipette tip, the pipette tip was attached to a pipettor. The pipette tip was placed in an aqueous solution, and the aqueous solution was drawn into the sample collection chamber of the pipette tip. As the aqueous solution was being drawn into the sample collection chamber, the pipette tip was removed from the aqueous solution resulting in aspiration, thereby bringing the aqueous solution into contact with the self-sealing barrier composition. Upon contact with the aqueous solution, the CMC of the barrier composition expanded and sealed the barrier composition precluding any aqueous solution from reaching the pipettor. The barrier medium additionally changed color indicating that the barrier medium had come into contact with the aqueous solution. Moreover, none of the aqueous solution circumvented barrier medium.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS4306033Feb 5, 1981Dec 15, 1981Spacy Chemical CorporationHighly hydrophilic and porous sintered body made of thermoplastic polyacrylonitrile resinUS4443515Jan 27, 1983Apr 17, 1984Peter RosenwaldAntistatic fabrics incorporating specialty textile fibers having high moisture regain and articles produced therefromUS4516679Nov 4, 1982May 14, 1985Simpson Carolyn NTamper-proof wrapUS4724114Oct 2, 1986Feb 9, 1988Kimberly-Clark CorporationSelective layering of superabsorbents in meltblown substratesUS4820577Dec 22, 1986Apr 11, 1989Kimberly-Clark CorporationMeltblown superabsorbent thermoplastic compositionsUS4924860Aug 26, 1988May 15, 1990Criticare Systems, Inc.Water trap and associated control systemUS4999164Oct 20, 1987Mar 12, 1991Eppendorf-Netheler-Hinz GmbhPipetting device comprising a retaining cone for holding a slip-on pipette tip and pipette tip for such pipetting deviceUS5156811Jul 23, 1991Oct 20, 1992Continental Laboratory Products, Inc.Pipette deviceUS5175046Mar 4, 1991Dec 29, 1992ChicopeeSuperabsorbent laminate structureUS5259956Jun 2, 1992Nov 9, 1993Porex Technologies Corp.Tube liquid dispenserUS5310525Feb 6, 1991May 10, 1994Whatman Scientific LimitedFluid detection deviceUS5501945Aug 30, 1994Mar 26, 1996The University Of AkronMethod of using multichromic polymers in packagingUS5620427Apr 27, 1995Apr 15, 1997David R. KippLuer lock systemUS5750585Apr 4, 1995May 12, 1998Purdue Research FoundationSuper absorbent hydrogel foamsUS5797347Aug 1, 1996Aug 25, 1998Uni-Charm CorporationAbsorbent panel for pet animalsUS5824328May 18, 1994Oct 20, 1998Stockhausen GmbhInsecticidal delivery compositions and methods for controlling a population of insects in an aquatic environmentUS5836929Jun 27, 1994Nov 17, 1998The Procter & Gamble CompanyAbsorbent articlesUS5851491Jun 13, 1997Dec 22, 1998Labcon, North AmericaPipette tip and filter for accurate sampling and prevention of contaminationUS5939086May 27, 1997Aug 17, 1999Lee County Mosquito Control DistrictCompositions and methods for reducing the amount of contaminants in aquatic and terrestrial environmentsUS5998032Jul 5, 1996Dec 7, 1999Weyerhaeuser CompanyMethod and compositions for enhancing blood absorbence by superabsorbent materialsUS6123905Jan 17, 1997Sep 26, 2000Matrix Technologies CorporationPipettor including an indicator and method of useUS6358569Dec 18, 1998Mar 19, 2002Mupor LimitedApplying a film to a bodyUS6638610Mar 6, 2000Oct 28, 2003Porex Technologies Corp.Water and oil repellent porous materials and processes for making the sameUS7743642 *Nov 26, 2004Jun 29, 2010Kyodo Printing Co., Ltd.Moisture absorbent material with indicator function, humidity indicator and packaging bagUS20030211799 *Jun 19, 2003Nov 13, 2003Porex CorporationFunctional fibers and fibrous materialsUS20050109683 *Nov 26, 2003May 26, 2005Joyce Patrick C.Water contaminant indicatorsUS20050192536Feb 25, 2005Sep 1, 2005Nobuo TakagiSafety indwelling needleUS20050273019May 31, 2005Dec 8, 2005Becton, Dickinson And CompanyBlood collection set with venting mechanismUS20050283093May 31, 2005Dec 22, 2005Becton, Dickinson And CompanyFlashback blood collection needleUS20060018800Jan 27, 2005Jan 26, 2006Slowey Paul DSpecimen sample collection device and test systemUS20060177352Feb 3, 2006Aug 10, 2006Christian ZiegmannFilter pipette tipUS20080197065Aug 20, 2007Aug 21, 2008Wingo James PSintered polymeric materials and applications thereofUS20080199363Feb 12, 2008Aug 21, 2008Guoqiang MaoPorous barrier media comprising color change indicatorsDE10157551A1Nov 23, 2001Jun 12, 2003Messer Griesheim GmbhColor indicator composition for moisture, used with gas purification system for purifying bottled gas for operating equipment or calibration in analytical laboratory, contains metal hydroxide and pH-indicator dyeEP0264704B1Oct 6, 1987Mar 4, 1992Eppendorf Ger�tebau Netheler + Hinz GmbHPipetting device provided with a conical adapter for a pipette tip, and pipette tip for such a deviceEP0301753A2Jul 20, 1988Feb 1, 1989Fulmer Yarsley LimitedWater absorbent structuresEP1688181A2Jan 24, 2006Aug 9, 2006Eppendorf AgPipette Tip With FilterJP2004331855A Title not availableJPH02117801A Title not availableWO1987000439A1Jul 14, 1986Jan 29, 1987General Polymeric CorporationFluid-flow controlling device and apparatus employing sameWO1996006643A1Aug 16, 1995Mar 7, 1996The University Of AkronMultichromic polymersWO1998031465A1Dec 31, 1997Jul 23, 1998Matrix Technologies CorporationPipettor including an indicator and method of useWO2002036708A2Oct 22, 2001May 10, 2002Porex CorporationSelf-sealing media comprising super-absorbent materialsWO2005053821A1 *Nov 26, 2004Jun 16, 2005Kyodo Printing Co., Ltd.Moisture absorbent material with indicator function, humidity indicator and packaging bagWO2006097481A1Mar 15, 2006Sep 21, 2006BAM Bundesanstalt f�r Materialforschung und -pr�fungOptochemical sensor membrane and method for producing the sameWO2008021539A2Aug 20, 2007Feb 21, 2008Porex CorporationSintered polymeric materials and applications thereof* Cited by examinerNon-Patent CitationsReference1"EP07811431.1 Office Action dated Jun. 30, 2009".2"EP07811431.1 Response to Office Action dated Nov. 3, 2009".3"PCT/US2001/047056 International Search Report dated Jul. 24, 2002".4"PCT/US2008/001838 International Preliminary Report on Patentability dated Aug. 27, 2009".5"U.S. Appl. No. 11/894,066, Office Action dated Apr. 20, 2010".6"U.S. Appl. No. 11/894,066, Office Action dated Jul. 27, 2010".7Abstract of JP01171930 (Kinyosha KK), Database EPODOC, XP-002463792, European Patent Office, The Hague, NL, Jul. 6, 1989.8Abstract of JP03197097 (Pentel KK), Database WPI Week 199141, XP-002463795, AN-1991-298561, Derwent Publications Ltd., London, GB, Aug. 28, 1991.9Abstract of JP2000024428 (Mitsubishi Plastics Ind), Database WPI Week 200016, XP-002463796, AN-2000-175322, Derwent Publications Ltd., London, GB, Jan. 25, 2000.10Abstract of JP2004331855 (Toppan Printing Co), Database WPI Week 200401, XP-002485448, AN-2005-002909, Thomson Scientific, London, GB, Nov. 25, 2004.11Abstract of JP54111915 (Fuji Kagaku Shikogyo), Database WPI, Section Ch, Week 197941, Class A97, XP-002463794, AN-1979-74332B, Derwent Publications Ltd., London, GB, Sep. 1, 1979.12Abstract of JP57064537 (Showa Gum KK); Database WPI, Section Ch, Week 198221, Class A18, XP-002463797, AN-1982-42838E, Derwent Publications Ltd., London, GB, Apr. 19, 1982.13Abstract of JP62225325 (Bando Chem Ind), Database WPI Week 198745, XP-002463793, AN-1987-317572, Derwent Publications Ltd., London, GB, Oct. 3, 1987.14Chinese Patent Application No. 200780039008.7, First Office Action mailed Nov. 26, 2010.15Chinese Patent Application No. 200780039008.7, Second Office Action mailed May 18, 2011.16EP 07811431.1, Office Action issued Oct. 28, 2010, 4 Pgs.17EP 08725464.5, Office Action issued Dec. 8, 2010, 3 Pgs.18European Patent Application No. 07811431.1, Response to Second Office Action filed Mar. 3, 2011.19European Patent Application No. 07811431.1, Rule 71(3) EPC Communication regarding Intent to Grant Application mailed Apr. 29, 2011.20European Patent Application No. 08725464.5, Cancellation of Oral Proceedings mailed Jan. 23, 2012 (4 pages).21European Patent Application No. 08725464.5, Response filed Feb. 22, 2012 (49 pages).22European Patent Application No. 08725464.5, Response to First Office Action filed Apr. 15, 2011.23European Patent Application No. 08725464.5, Summons to Attend Oral Hearing mailed Sep. 23, 2011.24Indian Patent Application No. 729KOLNP/2009, First Examination Report mailed Jan. 23, 2012 (6 pages).25PCT/US2007/018355 International Search Report and Written Opinion mailed Feb. 4, 2008.26PCT/US2008/001838 International Search Report and Written Opinion mailed Aug. 26, 2008.27PCT/US2008/001838 Invitation to Pay Fees and Partial Search Report mailed Jul. 7, 2008.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS8628843 *Oct 23, 2009Jan 14, 2014Porex CorporationComposite PTFE materials and applications thereofUS8645688Apr 11, 2012Feb 4, 2014Intel CorporationSystem and method for execution of a secured environment initialization instructionUS8690981Jun 5, 2012Apr 8, 2014Porex CorporationSintered porous plastic liquid barrier media and applications thereofUS20100104845 *Oct 23, 2009Apr 29, 2010Porex CorporationComposite PTFE Materials and Applications ThereofWO2014138782A1 *Mar 11, 2014Sep 18, 2014Ansell LimitedBreach or contamination indicating article* Cited by examinerClassifications U.S. Classification422/50, 422/68.1, 210/500.34, 210/500.35, 210/500.22, 264/126, 422/400, 264/127, 210/510.1, 210/500.38International ClassificationB01L3/02Cooperative ClassificationY10T428/268, G01N2035/1053, B01L3/0275, B01J20/26, B01L2300/025, B01L2200/141, B01J2220/445, B01L2400/0688, B01J2220/64, B01J20/28011, B01J20/28085, B01J2220/49, G01N2035/1023European ClassificationB01J20/28B12, B01J20/26, B01L3/02E, B01J20/28F12FLegal EventsDateCodeEventDescriptionMar 11, 2008ASAssignmentOwner name: POREX CORPORATION, GEORGIAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:MAO, GUOQIANG;REEL/FRAME:020630/0508Effective date: 20080305Oct 20, 2009ASAssignmentOwner name: SNTC HOLDING INC., NEW JERSEYFree format text: SECURITY AGREEMENT;ASSIGNORS:POREX HOLDING CORPORATION;POREX CORPORATON;POREX SURGICAL, INC.;REEL/FRAME:023390/0702Effective date: 20091019Owner name: SNTC HOLDING INC.,NEW JERSEYFree format text: SECURITY AGREEMENT;ASSIGNORS:POREX HOLDING CORPORATION;POREX CORPORATON;POREX SURGICAL, INC.;REEL/FRAME:023390/0702Effective date: 20091019Apr 1, 2010ASAssignmentOwner name: POREX CORPORATION,CALIFORNIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:SNTC HOLDING, INC., AS COLLATERAL AGENT;REEL/FRAME:024170/0471Effective date: 20100401Owner name: POREX SURGICAL, INC.,CALIFORNIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:SNTC HOLDING, INC., AS COLLATERAL AGENT;REEL/FRAME:024170/0471Effective date: 20100401Owner name: POREX HOLDING CORPORATION,CALIFORNIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:SNTC HOLDING, INC., AS COLLATERAL AGENT;REEL/FRAME:024170/0471Effective date: 20100401Owner name: POREX CORPORATION, CALIFORNIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:SNTC HOLDING, INC., AS COLLATERAL AGENT;REEL/FRAME:024170/0471Effective date: 20100401Owner name: POREX SURGICAL, INC., CALIFORNIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:SNTC HOLDING, INC., AS COLLATERAL AGENT;REEL/FRAME:024170/0471Effective date: 20100401Owner name: POREX HOLDING CORPORATION, CALIFORNIAFree format text: RELEASE BY SECURED PARTY;ASSIGNOR:SNTC HOLDING, INC., AS COLLATERAL AGENT;REEL/FRAME:024170/0471Effective date: 20100401Apr 5, 2010ASAssignmentOwner name: GENERAL ELECTRIC CAPITAL CORPORATION, AS US AGENT,Free format text: SECURITY AGREEMENT;ASSIGNOR:POREX CORPORATION;REEL/FRAME:024185/0224Effective date: 20100401Nov 21, 2013ASAssignmentOwner name: BANK OF MONTREAL, AS COLLATERAL AGENT, ILLINOISFree format text: SECURITY INTEREST (SECOND LIEN);ASSIGNORS:AG INDUSTRIES LLC;BUFFALO FILTER LLC;CHEMCO MANUFACTURINGCO., INC.;AND OTHERS;REEL/FRAME:031694/0487Effective date: 20131121Owner name: GOLDMAN SACHS BANK USA, AS COLLATERAL AGENT, NEW JFree format text: SECURITY INTEREST (FIRST LIEN);ASSIGNORS:AG INDUSTRIES LLC;BUFFALO FILTER LLC;CHEMCO MANUFACTURING CO., INC.;AND OTHERS;REEL/FRAME:031693/0608Effective date: 20131121Nov 11, 2015FPAYFee paymentYear of fee payment: 4RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services