Patent US4766029 - Semi-permeable nonwoven laminate - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inAdvanced Patent SearchPatentsA house wrap consists of a three-layer, semi-permeable, nonwoven laminate. The two exterior layers are spun-bond polypropylene having a melt flow of 35 grams per ten minutes at 230� C. The interior layer is a two-component melt-blown layer of polyethylene and polypropylene. The polypropylene has a melt...http://www.google.com/patents/US4766029?utm_source=gb-gplus-sharePatent US4766029 - Semi-permeable nonwoven laminateAdvanced Patent SearchPublication numberUS4766029 APublication typeGrantApplication numberUS 07/006,526Publication dateAug 23, 1988Filing dateJan 23, 1987Priority dateJan 23, 1987Fee statusPaidPublication number006526, 07006526, US 4766029 A, US 4766029A, US-A-4766029, US4766029 A, US4766029AInventorsRobert J. Brock, William Conn, James M. WeberOriginal AssigneeKimberly-Clark CorporationExport CitationBiBTeX, EndNote, RefManPatent Citations (8), Referenced by (144), Classifications (17), Legal Events (6) External Links: USPTO, USPTO Assignment, EspacenetSemi-permeable nonwoven laminate
US 4766029 AAbstract
A house wrap consists of a three-layer, semi-permeable, nonwoven laminate. The two exterior layers are spun-bond polypropylene having a melt flow of 35 grams per ten minutes at 230� C. The interior layer is a two-component melt-blown layer of polyethylene and polypropylene. The polypropylene has a melt flow of 260 and the polyethylene has a melt flow of 350. The laminate is calendered after formation so that the polyethylene melts and flows to close up the interstitial space and to bond the layers together to create a strong semi-permeable laminate.
1. A semi-permeable laminate comprising:(a) an interior layer comprising:(i) an array of randomly dispersed microfibers formed from a fiber forming polymer having a melt flow; and (ii) an interstitial mass, between and among the microfibers, closing up interstitial spaces, formed from a binder-filler polymer having a melt flow, wherein the melt flow of the fiber forming polymer is at least about 80 grams per ten minutes at 230� C. less than the melt flow of the binder-filler polymer; and (b) at least one exterior layer bonded to the interior layer by means of of the binder-filler polymer of the interior layer, the exterior layer comprising an array of randomly laid, continuous filaments formed from a filament forming polymer having a melt flow, wherein the melt flow of the filament forming polymer is at least about 200 grams per ten minutes at 230� C. less than the melt flow of the binder-filler polymer. 2. The laminate of claim 1, wherein the melt flow of the fiber forming polymer is 80-100 grams per ten minutes at 230� C. less than the melt flow of the binder-filler polymer in the interior layer.
3. The laminate of claim 2, wherein the melt flow of the filament forming polymer is 200-315 grams per 10 minutes at 230� C. less than the melt flow of the binder-filler polymer.
4. The laminate of claim 2 or 3 wherein the fiber forming polymer and the filament forming polymer are polypropylene and the binder-filler polymer is polyethylene.
5. A method for forming a semi-permeable nonwoven laminate comprising the steps of:(a) depositing an exterior layer of randomly-laid, continuous filaments of filament forming polymer having a melt flow; (b) subsequently depositing an interior layer of randomly-dispersed microfibers onto the exterior layer, the microfibers formed by melt-blowing the fibers from a mixture of a fiber forming polymer having a melt flow and a filler-binder polymer having a melt flow wherein the melt flow of the filament forming polymer is at least 200 grams per ten minutes at 230� C. less than and the melt flow of the fiber-forming polymer is at least about 80 grams per ten minutes at 230� C. less than the melt flow of the filler-binder polymer; and (c) hot calendering the layers together at a temperature, pressure, and speed that causes remelting and flowing of the filler-binder polymer closing up interstitial spaces between fibers and interbonding the layers but does not cause remelting of the filament forming polymer and the fiber forming polymer. 6. The method of claim 5 wherein the melt flow of the fiber forming polymer is 80-100 grams per ten minutes at 230� C. less than the melt flow of the binder-filler polymer.
7. The method of claim 6, wherein the melt flow of the filament forming polymer is 200-315 grams per ten minutes at 230� C. less than the melt flow of the binder-filler polymer.
8. The method of claim 6 or 7 wherein the fiber forming polymer and the filament forming polymer are polypropylene and the binder-filler polymer is polyethylene.
9. The method of claim 5, wherein the calender temperature is between 260� F. and 290� F., the calender pressure is between 167.5 pounds per lineal inch and 342.9 pounds per lineal inch, and the calender speed is between 12 feet per minute and 24 feet per minute.
10. The method of claim 9, wherein the melt flow of the fiber forming polymer is 80-100 grams per ten minutes at 230� C. less than the melt flow of the binder-filler polymer.
11. The method of claim 10, wherein the melt flow of the filament forming polymer is 200-315 grams per ten minutes at 230� C. less than the melt flow of the binder-filler polymer.
12. The method of claim 10 or 11, wherein the fiber forming polymer and the filament forming polymer are polypropylene and the binder-filler polymer is polyethylene.
This invention relates generally to a semi-permeable nonwoven laminate which is useful as a house wrap, and more particularly concerns a laminate having spun-bonded exterior layers and a two-component, melt-blown interior layer which is rendered partially adhesive by the application of heat and pressure to bind together the layers of the laminate.
In housing construction, it is common practice to install an insulating board, generally of polyurethane foam, between the siding on the house and the house frame. It has become increasingly common to also use a fabric material (house wrap) between the insulating board and the siding which fabric material serves to inhibit the infiltration of air or water into the house but at the same time allows expiration of water vapor from the inside of the walls to the outside so that moisture does not build up in the walls thus producing mildew and rotting. A conventional house wrap is sold under the trademark TYVEK by DuPont of Wilmington, Del. Tyvek is a solution cast polyethylene web.
It is an object of the present invention to provide a semi-permeable nonwoven house wrap laminate which on one hand will preclude the infiltration of air and water and on the other hand will allow the expiration of water vapor and which will have sufficient strength to withstand handling encountered during the construction process.
The foregoing object is achieved by a laminate with spun-bonded polypropylene exterior layers and an internal melt-blown layer having fibers formed from a fiber forming polymer (polyproplylene) and binder-filler polymer (polyethylene). Particularly, the internal melt-blown layer is formed by dry mixing a 50-50 blend of polypropylene and polyethylene pellets and then extruding the mixture through a conventional melt-blowing die. The polymer pellet mixture, however, can range from 70-30 to 30-70. The polypropylene and polyethylene polymers in the melt-blown layer are selected so that the polypropylene has a melt flow that is about 80-100 grams per ten minutes at 230� C. less than the melt flow for the polyethylene. The polypropylene in the spun-bonded external layer is chosen to have a melt flow about 200-315 grams per ten minutes at 230� C. less than the polyethylene that is used in the internal layer.
Upon the application of heat and pressure, the polyethylene portion of the two-component fibers in the internal layer softens to become an interstitial mass which flows into and closes up the interstitial spaces between the melt-blown polypropylene fibers. By closing the interstitial space within the melt-blown internal layer, the house wrap laminate is rendered semi-permeable. The melting and flowing of the polyethylene within the melt-blown layer also serves to bind together the polypropylene fibers within the melt-blown layer and to bind the exterior polypropylene spun-bonded layers to the internal melt-blown layer. Because the melt flows of the polypropylene in both internal and external layers are less than the melt flow of the polyethylene, the amount of heat and pressure which melts the polyethylene will not tend to degrade the strength of the polypropylene fibers and filaments in the laminate.
FIG. 1 is a schematic diagram of a nonwoven forming machine which is used in making the semi-permeable, nonwoven laminate of the present invention; and
FIG. 2 is a cross section view of the semi-permeable nonwoven laminate of the present invention showing the layer configuration.
Turning to FIG. 1, there is shown a schematic of forming machine 10 which is used to produce a laminate 12 made in accordance with the present invention. Particularly, the forming machine 10 consists of an endless foraminous forming belt 14 wrapped around rollers 16 and 18 so that the belt 14 is driven in the direction shown by the arrows. The forming machine 10 has three stations, spun-bond station 20, melt-blown station 22, and spun-bond station 24.
The spun-bond stations 20 and 24 are conventional extruders or spinnerettes which form continuous filaments of polypropylene and deposit those filaments onto the forming belt 14 in a random interlaced fashion. The spun-bond stations 20 and 24 may include one or more spinnerette heads depending on the speed of the process and the particular polypropylene polymer being used. Forming spun-bonded material is conventional in the art and the design of such a spun-bonded forming station is thought to be well within the skill of those of ordinary skill in the art. Such level of skill is demonstrated by U.S. Pat. Nos. 3,338,992, and 3,341,394.
In accordance with the present invention, the spun-bond station 20 produces spun-bond filaments 26 from a filament forming polymer. The filaments are randomly laid on the belt 14 to form a spun-bonded external layer 28. The layer 28 has a basis weight of preferably 0.6 oz./yd.2. The filament forming polymer is preferably Exxon 3125 polypropylene, which is manufactured by Exxon Corporation and has a melt flow of approximately 35 grams per ten minutes at 230� C.
The melt-blown station 22 consists of a die which is used to form microfibers 30. The microfibers 30 are randomly deposited on top of the spun-bond layer 28 and form a melt-blown layer 32. The construction and operation of the melt-blown station 22 for forming microfibers 30 and melt-blown layer 32 is considered conventional, and the design and operation are well within the skill of those of ordinary skill in the art. Such skill is demonstrated by NRL Report 4364, "Manufacture of Super-Fine Organic Fibers", by V.A. Wendt, E.L. Boon, and C.D. Fluharty; NRL Report 5265, "An Improved Device for the Formation of Super-Fine Thermoplastic Fibers", by K.D. Lawrence, R.T. Lukas, and J.A. Young; and, U.S. Pat. No. 3,849,241, issued Nov. 19, 1974, to Buntin, et al.
The melt-blown station 22 produces two-component microfine fibers 30 from a mixture of a fiber forming polymer and a binder-filler polymer. The fibers 30 are randomly deposited on top of spun-bond layer 28 to form a melt-blown internal layer 32. The layer 32 has a basis weight of preferably 0.6 oz./yd.2. The fiber forming polymer is preferably Exxon 3145 polypropylene and has a melt flow of approximately 260 grams per ten minutes at 230� C. The preferred binder-filler polymer is Dowplex 61800.09 polyethylene manufactured by Dow Chemical of Midland, Mich. The polyethylene has a melt flow of 350 grams per ten minutes at 230� C. It is important that the difference in melt flow between the polyethylene and polypropylene be maintained at not less than about 80 grams per ten minutes for reasons that will become apparent. In order to produce such two-component fibers, polypropylene and polyethylene resin pellets are dry-mixed prior to extrusion in a ratio by weight between 70-30 and 30-70 with the preferred ratio being 50-50.
After the internal layer 32 has been deposited by the melt-blown station 22 onto layer 28, spun-bond station 24 produces spun-bond filaments 34 of polypropylene which are deposited in random orientation on top of the melt-blown layer 32 to produce external spun-bond layer 36. The layer 36 has a basis weight of preferably 0.7 oz./yd.2. Spun-bond layer 36 is preferably formed from Exxon 3125 polypropylene having a melt flow of 35 grams per ten minutes at 230� C.
The polymers are selected so that there is a differential of at least 80 grams per ten minutes at 230� C. between the polyethylene binder-filler and the polypropylene fiber forming polymer in the melt-blown layer and a difference of at least 200 grams per ten minutes at 230� C. between the polyethylene binder-filler of the internal melt-blown layer and the polypropylene filament forming polymer in the external spun-bonded layer.
Once the three layers, FIG. 2, spun-bond layer 28, melt-blown layer 32, and spun-bond layer 36, are formed, the resulting laminate is drawn through calender rolls 38 and 40. The calender rolls are heated to a temperature from 260� F. to 300� F. and are set at a pressure between 167.5 lbs. per lineal inch and 342.9 lbs. per lineal inch. The laminate 12 is fed through the calender rolls at a speed from 12 feet per minute to 24 feet per minute. Preferably, calendering is carried out at 18 feet per minute at 228.6 lbs. per lineal inch of pressure and at temperatures between 270� F. and 290� F. Within the ranges of temperature, pressure, and speed set out, the binder-filler polymer (polyethylene) will melt to create an interstitial mass which will flow into and close up the interstitial space between the polypropylene fibers to render the laminate 12 semi-permeable so that infiltration of air will be inhibited while allowing expiration of water vapor. In addition, the melted polyethylene will serve to bind together the layers of the laminate. Because of the difference in melt flow between the polyethylene and the two polypropylenes, the strength of the polypropylenes will not be significantly degraded by the heat and pressure of the calendering process.
In order to illustrate the invention, the laminates of the present invention were formed and calendered under varying calendering conditions (temperature, pressure, and speed) and the physical characteristics (tensile strength, tear strength, air permeability, and moisture vapor permeability) were compared. The house wrap laminate made in accordance with the present invention consisted of external layers of spun-bonded polypropylene (Exxon 3125) having a basis weight of 0.6 oz./yd.2 and the other having a basis weight of 0.7 oz./yd.2. The internal melt-blown layer had a basis weight of 0.6 oz./yd.2 and was a 50-50 mix by weight of polypropylene (Exxon 3145) and polyethylene (Dowplex 61800.09). The polyethylene and polyethylene pellets were dry mixed prior to extruding. Once formed, the laminate was calendered at various temperatures, pressures, and speeds, and the physical characteristics for each calender run were measured. The strength of the house wrap was based on testing for tensile strength and tear strength. Tensile strength (Grab Method) was determined in accordance with Federal Test Method (FTM) No. 191, Method 5100. Tear strength (Trapezoid) was determined in accordance with FTM No. 191, Method 5136. Air permeability was determined in accordance with FTM No. 191, Method 5450. Testing for air permeability demonstrates the ability of the house wrap to preclude the infiltration of air. The lower the air permeability is, the better the house wrap is. Moisture vapor permeability was determined in accordance with FTM No. 406, Method 7032. Moisture vapor permeability demonstrates the ability of the house wrap to allow the expiration of water vapor to the outside. The higher the moisture vapor permeability is, the better the house wrap is.
The following Table 1 summarizes the results:
TABLE 1______________________________________(Part 1)GRAB TENSILE DATA (lbs/in2)CalenderPressure(pounds/  Temperature �F.lineal inch)     260      270    280     290  300______________________________________Calender Speed: 12 feet/minute167.5     17.3     26.4   30.7    31.1 15.2228.6     19.9     32.8   32.4    28.7 12.6285.7     18.9     22.2   24.6    35.6 ****342.9     20.6     30.7   31.8    27.2 ****Calender Speed: 18 feet/minute167.5     16.2     18.4   23.5    31.6 23.3228.6     17.8     19.8   25.3    34.1 22.7285.7     16.5     20.4   24.9    35.6 21.1342.9     19.1     21.6   26.4    34.6 24.3Calender Speed: 24 feet/minute167.5      9.8     14.4   24.6    31.9 25.7228.6     12.9     17.8   23.6    30.7 25.2285.7     16.6     20.6   20.9    28.4 24.9342.9     16.9     17.9   23.6    31.7 24.6______________________________________(Part 2)TRAP TEAR DATA (lbs)CalenderPressure(pounds/  Temperature �F.lineal inch)     260      270    280     290  300______________________________________Calender Speed: 12 feet/minute167.5      9.5      11.7  11.3    4.2   0.87228.6     10.1     11.8    9.9    2.6   0.76285.7     9.0      10.6   10.8    5.3  ****342.9     10.1     11.1    8.5    1.6  ****Calender Speed: 18 feet/minute167.5     7.6      8.3    10.0    8.8  1.2228.6     9.1      9.4    11.1    9.4  1.6285.7     8.3      9.0    10.3    5.4  1.7342.9     8.1      10.1   10.5    3.1  1.4Calender Speed: 24 feet/minute167.5     5.7      7.5    10.1    8.0  2.9228.6     7.7      7.4    10.6    8.6  2.3285.7     7.6      9.9     9.7    9.9  2.0342.9     7.5      9.5    10.2    6.6  1.8______________________________________(Part 3)FRAZIER (AIR) PERMEABILITY(ft3 air/ft2 material/minute)CalenderPressure(pounds/  Temperature �F.lineal inch)     260      270    280     290  300______________________________________Calender Speed: 12 feet/minute167.5     2.15     1.94   1.19    3.46 10.62228.6     0.58     0.75   1.14    1.31  7.42285.7     0.87     0.37   0.49    1.47 ****342.9     0.58     0.56   0.53    3.88 ****Calender Speed: 18 feet/minute167.5     2.60     1.85    0.00   1.87 1.51228.6     1.85     0.87   1.31    0.89 1.53285.7     1.16     0.68   0.92    0.79 2.53342.9     0.95     0.66   0.94    1.61 0.97Calender Speed: 24 feet/minute167.5     8.98     1.47   0.26    2.75 3.81228.6     3.68     1.14   0.81    2.67 2.68285.7     1.79     0.95   1.04    0.79 1.69342.9     2.96     1.71   0.31    2.32 2.32______________________________________(Part 4)MOISTURE VAPOR TRANSMISSION(g. water vap/m2 material/24 hrs)CalenderPressure(pounds/  Temperature �F.lineal inch)     260      270    280     290  300______________________________________Calender Speed: 12 feet/minute167.5     736      509    706     653  560228.6     623      597    395     593  ****285.7     581      443    397     501  ****342.9     463      431    466     581  ****Calender Speed: 18 feet/minute167.5     664      826    688     751  1071228.6     684      881    545     564  736285.7     747      671    563     522  375342.9     679      758    525     580  359Calender Speed: 24 feet/minute167.5     917      880    790     784  775228.6     899      714    744     686  629285.7     819      812    626     501  603342.9     561      798    800     698  643______________________________________
Acceptable house wrap was produced for all runs in Table 1 above for temperatures below 290� F. The optimum appeared to exist at a pressure of 228.6 lbs./lineal inch, a speed of 18 ft./minute and at temperatures between 270� F. and 290� F.
The house wrap of the present invention (the same as used for Table 1) was then compared to a proposed all-polypropylene house wrap (control). The control house wrap was a laminate consisting of three layers. The first exterior layer was spun-bonded polypropylene (Exxon 3125) with a basis weight of 0.6 oz./yd.2. The interior layer was melt-blown polypropylene (Exxon 3145) with a basis weight of 0.6 oz./yd.2. The other exterior layer was spun-bonded polypropylene (Exxon 3125) with a basis weight of 0.7 oz./yd.2. The calender pressure was set at 228.6 lbs./lineal inch and speed was 18 ft./minute. Temperature was varied, and the physical characteristics measured. The results are summarized in Table 2 below:
TABLE 2______________________________________(Part 1)HOUSE WRAP  (present invention)       0.6 oz./yd.2 PP SB;       0.6 oz./yd.2 MB 50%-50% mix PP/PE;       0.7 oz./yd.2 PP SBCONTROL       0.6 oz./yd.2 PP SB;       0.6 oz./yd.2 MB 100% PP;       0.7 oz./yd.2 PP SB______________________________________GRAB TENSILE DATA (lbs/in2) vs TEMPERATURE �F.Temp �F.          House wrap                    Control______________________________________260            17.8       6.9270            19.8      6.9280            25.3      11.0290            34.1      14.3300            22.7      32.5______________________________________(Part 2)TRAP TEAR (lbs) vs TEMPERATURE �F.                    ControlTemp �F.          House wrap                    SMS______________________________________260            9.1       6.5270            9.4       6.6280            11.1      7.7290            9.4       9.9300            1.6       6.8______________________________________FRAZIER PERMEABILITY (ft3 /ft2 /minute)vs TEMPERATURETemp �F.          House wrap                    Control______________________________________260            1.85      4.9270            0.87      5.6280            0.92      2.5290            0.89      2.0300            1.53      1.1______________________________________MOISTURE VAPOR TRANSMISSION (g./m2 /24 hours)vs TEMPERATURE          Housewrap ControlTemp �F.          SMS       SMS______________________________________260            1197      1639270            1184      1560280            979       1683290            920       1395300            754        819______________________________________
For the operating conditions in Table 2, the house wrap of the present invention was superior in tensile strength, tear strength, and air permeability below 280� F. and except for tear strength was superior below 290� F. The moisture vapor permeability was, however, reduced by 3%-37%.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3509009 *Feb 6, 1967Apr 28, 1970Freudenberg Carl KgNon-woven fabricUS3639195 *Sep 18, 1967Feb 1, 1972Ici LtdBonded fibrous materials and method for making themUS3841953 *Mar 3, 1972Oct 15, 1974Exxon Research Engineering CoNonwoven mats of thermoplastic blends by melt blowingUS3914497 *Sep 11, 1973Oct 21, 1975Kuraray CoNon-woven batts possessing excellent tensile strength, tear strength and initial modulusUS4323626 *Sep 18, 1980Apr 6, 1982Chisso CorporationCrystalline polypropylene, ethylene-vinyl acetate-vinyl alcohol teUS4384098 *Jan 13, 1981May 17, 1983Phillips Petroleum CompanyFilamentary polypropylene and method of makingUS4555811 *Jun 13, 1984Dec 3, 1985ChicopeeExtensible microfine fiber laminateUS4632861 *Mar 24, 1986Dec 30, 1986E. I. Du Pont De Nemours And CompanyLow density polyethylene and crystalline polypropylene fiber* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS4810556 *Sep 29, 1987Mar 7, 1989Mitsui Petrochemical Industries, Ltd.Very soft polyolefin spunbonded nonwoven fabricUS4863785 *Nov 18, 1988Sep 5, 1989The James River CorporationNonwoven continuously-bonded trilaminateUS4974382 *Jan 6, 1989Dec 4, 1990Constructonika, Inc.Composite construction materialUS5073436 *Jul 20, 1990Dec 17, 1991Amoco CorporationSelf-bonding fibrous web with water repellency and water vapor permeabilityUS5078935 *Aug 9, 1990Jan 7, 1992Mitsui Petrochemical Industries, Ltd.CrepingUS5145727 *Nov 26, 1990Sep 8, 1992Kimberly-Clark CorporationMultilayer nonwoven composite structureUS5149576 *Nov 26, 1990Sep 22, 1992Kimberly-Clark CorporationMultilayer nonwoven laminiferous structureUS5169712 *Aug 23, 1991Dec 8, 1992Amoco CorporationContaining ethylene-propylene block copolymer polypropylene random copolymer, calcium carbonate and beta-spherulite nucleating agentUS5178931 *Jun 17, 1992Jan 12, 1993Kimberly-Clark CorporationThree-layer nonwoven laminiferous structureUS5178932 *Jun 17, 1992Jan 12, 1993Kimberly-Clark CorporationMelt extruding continuous thermoplastic polyamide, polyolefin, polyester or polyetherester filaments; foraminous support; alcohol repellent microfibers; pattern bonding with heat, pressure; boundary between layers indistinct, fiber mixingUS5208098 *Oct 23, 1990May 4, 1993Amoco CorporationSelf-bonded nonwoven web and porous film compositesUS5223329 *Jan 29, 1991Jun 29, 1993Amann John ALaminate sheet articleUS5229191 *Nov 20, 1991Jul 20, 1993Fiberweb North America, Inc.Composite nonwoven fabrics and method of making sameUS5258220 *Sep 30, 1991Nov 2, 1993Minnesota Mining And Manufacturing CompanyWipe materials based on multi-layer blown microfibersUS5294482 *Oct 30, 1991Mar 15, 1994Fiberweb North America, Inc.Laminar blend of polyolefin fibers having different melting points and heat bonded in discrete areasUS5308691 *Oct 4, 1993May 3, 1994E. I. Du Pont De Nemours And CompanyControlled-porosity, calendered spunbonded/melt blown laminatesUS5415925 *Jun 10, 1992May 16, 1995Fiberweb North America, Inc.Gamma structure composite nonwoven fabric comprising at least two nonwoven webs adhesively bonded by a lightweight adhesive webUS5455110 *Jun 29, 1994Oct 3, 1995Kimberly-Clark CorporationNonwoven laminated fabricsUS5460884 *Aug 25, 1994Oct 24, 1995Kimberly-Clark CorporationSoft and strong thermoplastic polymer fibers and nonwoven fabric made therefromUS5492751 *Mar 2, 1994Feb 20, 1996Kimberly-Clark CorporationDisposable garment with improved containments meansUS5498463 *Mar 21, 1994Mar 12, 1996Kimberly-Clark CorporationPolyethylene meltblown fabric with barrier propertiesUS5554435 *Mar 18, 1994Sep 10, 1996Hercules IncorporatedTextile structures, and their preparationUS5564970 *Nov 17, 1994Oct 15, 1996Hewlett-Packard CompanyMethod and apparatus for creating or restoring high friction surface to media rollerUS5593768 *Apr 26, 1994Jan 14, 1997Fiberweb North America, Inc.Softness, strength, disposableUS5607798 *May 17, 1995Mar 4, 1997Kimberly-Clark CorporationSoft and strong thermoplastic polymer and nonwoven fabric laminatesUS5681646 *Apr 19, 1996Oct 28, 1997Kimberly-Clark Worldwide, Inc.High strength spunbond fabric from high melt flow rate polymersUS5738745 *Nov 27, 1995Apr 14, 1998Kimberly-Clark Worldwide, Inc.Method of improving the photostability of polypropylene compositionsUS5744548 *Oct 30, 1996Apr 28, 1998Kimberly-Clark Worldwide, Inc.Blend containing polysiloxaneUS5763336 *May 10, 1996Jun 9, 1998E. I. Du Pont De Nemours And CompanyVapor permeable, laminated sheet suitable as an impact resistance packaging materialUS5806154 *May 24, 1995Sep 15, 1998Springs Industries, Inc.Method of making textile laminateUS5841081 *Jun 21, 1996Nov 24, 1998Minnesota Mining And Manufacturing CompanyMethod of attenuating sound, and acoustical insulation thereforUS5922626 *Jun 12, 1997Jul 13, 1999Hp-Chemie Research And Development Ltd.Self-adhering reinforcing material for nonwoven textile fabricsUS5925581 *Oct 15, 1996Jul 20, 1999Spring Industries, Inc.Fiberfill web; bedding, construction materials; durabilityUS5932322 *Jun 8, 1998Aug 3, 1999E. I. Du Pont De Nemours And CompanyPackaging coverUS5993586 *Jun 2, 1997Nov 30, 1999Dunson; Samuel EugeneRigid fiber compositeUS6024818 *Dec 21, 1992Feb 15, 2000Dunson; Samuel EugeneManufacturing rigid fiber composite material by needling composite of non-woven blend of fibers, then heating forming a plasticized structureUS6224977May 17, 1995May 1, 2001Kimberly-Clark Worldwide, Inc.Blend of a high crystallinity polypropylene polymer and a random block copolymer of polypropylene and polyethylene.US6268302Apr 2, 1997Jul 31, 2001Kimberly-Clark Worldwide, Inc.Polyolefin fabricUS6322604Jun 6, 2000Nov 27, 2001Kimberly-Clark Worldwide, IncFiltration media and articles incorporating the sameUS6413344 *Jun 16, 1999Jul 2, 2002First Quality Nonwovens, Inc.Non-woven fabric; crystallization; calendering; vapor permeability; liquid imperviousUS6417154 *Jul 17, 2000Jul 9, 2002Kimberly-Clark Worldwide, Inc.Absorbent with multilayer laminate, melt blow fiber and web of nonwoven materialUS6420625Sep 12, 1997Jul 16, 2002Kimberly-Clark Worldwide, Inc.Breathable, liquid-impermeable, apertured film/nonwoven laminate and process for making sameUS6441267Apr 5, 1999Aug 27, 2002Fiber Innovation TechnologyHeat bondable biodegradable fiberUS6502360Mar 27, 2001Jan 7, 2003Thantex Specialties, Inc.Directed to a membrane laminate for a roofing system comprising a membrane sheet and a nonwoven material laminated to said sheet. The nonwoven material has a semi- permeable, skinned layer formed therein. nonwoven laminated thereto forUS6509092Apr 5, 1999Jan 21, 2003Fiber Innovation TechnologyHeat bondable biodegradable fibers with enhanced adhesionUS6562777Nov 5, 2001May 13, 2003Kimberly-Clark Worldwide, Inc.Sorbent materialUS6610163Dec 11, 1998Aug 26, 2003Kimberly-Clark Worldwide, Inc.Enhanced barrier film and laminate and method for producing sameUS6647549Apr 4, 2001Nov 18, 2003Kimberly-Clark Worldwide, Inc.Finger gloveUS6721987Apr 4, 2001Apr 20, 2004Kimberly-Clark Worldwide, Inc.Dental wipeUS6723669Dec 17, 1999Apr 20, 2004Kimberly-Clark Worldwide, Inc.Fine multicomponent fiber webs and laminates thereofUS6756332Jun 11, 2001Jun 29, 2004Jason IncorporatedVehicle headliner and laminate thereforUS6762137Dec 19, 2001Jul 13, 2004Kimberly-Clark Worldwide, Inc.Meltspun web comprising a thermoplastic polymer and a hydrophobic agent incorporated into the thermoplastic polymer comprising a polydimethylsiloxane, a guerbet ester, or mixtures thereof.US6875315Dec 19, 2002Apr 5, 2005Kimberly-Clark Worldwide, Inc.Non-woven through air dryer and transfer fabrics for tissue makingUS6878238Dec 19, 2002Apr 12, 2005Kimberly-Clark Worldwide, Inc.Non-woven through air dryer and transfer fabrics for tissue makingUS6878650Dec 20, 2000Apr 12, 2005Kimberly-Clark Worldwide, Inc.Fine denier multicomponent fibersUS7012169Apr 4, 2001Mar 14, 2006Kimberly-Clark Worldwide, Inc.Disposable finger sleeve for appendagesUS7022630Oct 22, 2003Apr 4, 2006Bba Nonwovens Simpsonville, Inc.Nonwoven protective fabrics with conductive fiber layerUS7083839Dec 20, 2001Aug 1, 2006Kimberly-Clark Worldwide, Inc.A wrap can produce exothermic or endothermic reaction to heat or cool the body, by applying a tensile force on an inner substrate to rupture, positioning between two exterior substratesUS7101623 *Feb 28, 2005Sep 5, 2006Dow Global Technologies Inc.Extensible and elastic conjugate fibers and webs having a nontacky feelUS7127771Jun 24, 2003Oct 31, 2006Kimberly-Clark Worldwide, Inc.Dental wipeUS7141142Sep 26, 2003Nov 28, 2006Kimberly-Clark Worldwide, Inc.productivity can be improved by altering the structure, such as the surface contour and/or drainage characteristics, of papermaking fabrics for re-use, preferably while on the machineUS7271113 *Jan 23, 2003Sep 18, 2007Fiberweb Corovin GmbhComposite with an absorbent layerUS7294238Feb 4, 2005Nov 13, 2007Kimberly-Clark Worldwide, Inc.Non-woven through air dryer and transfer fabrics for tissue makingUS7416627Aug 31, 2005Aug 26, 2008Kimberly-Clark Worldwide, Inc.Films and film laminates having cushioning cells and processes of making thereofUS7422712Dec 15, 2005Sep 9, 2008Kimberly-Clark Worldwide, Inc.Technique for incorporating a liquid additive into a nonwoven webUS7507047Dec 22, 2004Mar 24, 2009Kimberly-Clark Worldwide, Inc.Finger wipe containing a composition in a rupturable reservoirUS7517166Jul 29, 2005Apr 14, 2009Kimberly-Clark Worldwide, Inc.Applicator with discrete pockets of a composition to be delivered with use of the applicatorUS7537664Nov 7, 2003May 26, 2009Howmedica Osteonics Corp.Laser-produced porous surfaceUS7549188Oct 18, 2005Jun 23, 2009Kimberly-Clark Worldwide, Inc.Dental wipeUS7553302Dec 22, 2003Jun 30, 2009Kimberly-Clark Worldwide, Inc.Packaged interlabial articleUS7582178Nov 22, 2006Sep 1, 2009Kimberly-Clark Worldwide, Inc.Forming an elastic film that comprises a thermoplastic elastomer and semi-crystalline polyolefin; materials remain relatively inelastic prior to incorporation into a final product, but which achieve a certain level of elasticity after having been activated in the final productUS7585382Oct 31, 2006Sep 8, 2009Kimberly-Clark Worldwide, Inc.Extruding blend containing at least one thermoplastic elastomer and at least one semi-crystalline polyolefin; film is formed from blend and film is stretched in at least machine direction without applying external heat (e.g., "cold stretched") and bonded to nonwoven webUS7618907Aug 2, 2002Nov 17, 2009Owens Corning Intellectual Capital, LlcLow porosity facings for acoustic applicationsUS7674058Aug 30, 2005Mar 9, 2010Kimberly-Clark Worldwide, Inc.Disposable wipe with liquid storage and application systemUS7713252Dec 14, 2005May 11, 2010Kimberly-Clark Worldwide, Inc.Therapeutic article including a personal care composition and methods of making the therapeutic articleUS7794486Dec 15, 2005Sep 14, 2010Kimberly-Clark Worldwide, Inc.Therapeutic kit employing a thermal insertUS7803244Aug 31, 2006Sep 28, 2010Kimberly-Clark Worldwide, Inc.Nonwoven composite containing an apertured elastic filmUS7815995Mar 3, 2003Oct 19, 2010Kimberly-Clark Worldwide, Inc.Prevents fibers or zones of fibers from breaking away from the surface as lintUS7820573Jul 24, 2008Oct 26, 2010OCV Intellectual Capital, LLC,two layered fibrous blanket; polyester, polypropylene, polyethylene, fiberglass, natural fibers, nylon, rayon and blends thereof bonded to a layer of meltblown polypropylene fibers; ceiling tiles, hood linersUS7846530Sep 27, 2004Dec 7, 2010Kimberly-Clark Worldwide, Inc.Creped electret nonwoven wiperUS7879747Mar 30, 2007Feb 1, 2011Kimberly-Clark Worldwide, Inc.Elastic laminates having fragrance releasing properties and methods of making the sameUS7910795Mar 9, 2007Mar 22, 2011Kimberly-Clark Worldwide, Inc.Absorbent article containing a crosslinked elastic filmUS7923391Oct 16, 2007Apr 12, 2011Kimberly-Clark Worldwide, Inc.Nonwoven web material containing crosslinked elastic component formed from a pentablock copolymerUS7923392Oct 16, 2007Apr 12, 2011Kimberly-Clark Worldwide, Inc.Crosslinked elastic material formed from a branched block copolymerUS7938921Nov 22, 2006May 10, 2011Kimberly-Clark Worldwide, Inc.Strand composite having latent elasticityUS7942264Dec 24, 2008May 17, 2011Kimberly-Clark Worldwide, Inc.Sterilization container with peel topUS7976662Dec 15, 2005Jul 12, 2011Kimberly-Clark Worldwide, Inc.Laminate containing a fluorinated nonwoven webUS7979946Dec 15, 2006Jul 19, 2011Kimberly-Clark Worldwide, Inc.Polish and polishing mittsUS7985209 *Dec 15, 2005Jul 26, 2011Kimberly-Clark Worldwide, Inc.Wound or surgical dressingUS8029190May 10, 2007Oct 4, 2011Kimberly-Clark Worldwide, Inc.Method and articles for sensing relative temperatureUS8069629Aug 6, 2009Dec 6, 2011Certainteed CorporationProcess for manufacturing insulated sidingUS8142886Jul 24, 2008Mar 27, 2012Howmedica Osteonics Corp.Porous laser sintered articlesUS8152787May 30, 2008Apr 10, 2012Kimberly-Clark Worldwide, Inc.Personal wear absorbent article with disposal tabUS8162912May 30, 2008Apr 24, 2012Kimberly Clark Worldwide, Inc.Personal wear absorbent article with disposal tabUS8172084Dec 30, 2004May 8, 2012Kimberly-Clark Worldwide, Inc.Absorbent article packagingUS8172821May 30, 2008May 8, 2012Kimberly-Clark Worldwide, Inc.Personal wear absorbent article with waist adjustment tabUS8227658Dec 14, 2007Jul 24, 2012Kimberly-Clark Worldwide, IncFilm formed from a blend of biodegradable aliphatic-aromatic copolyestersUS8241587Dec 24, 2008Aug 14, 2012Kimberly-Clark Worldwide, Inc.Collapsible sterilization containerUS8268100Jul 26, 2010Sep 18, 2012Howmedica Osteonics Corp.Laser-produced porous surfaceUS8287677Jan 31, 2008Oct 16, 2012Kimberly-Clark Worldwide, Inc.Printable elastic compositeUS8324445Jun 30, 2008Dec 4, 2012Kimberly-Clark Worldwide, Inc.Collection pouches in absorbent articlesUS8349963Oct 16, 2007Jan 8, 2013Kimberly-Clark Worldwide, Inc.Crosslinked elastic material formed from a linear block copolymerUS8361913Feb 11, 2008Jan 29, 2013Kimberly-Clark Worldwide, Inc.Nonwoven composite containing an apertured elastic filmUS8399368Oct 16, 2007Mar 19, 2013Kimberly-Clark Worldwide, Inc.Nonwoven web material containing a crosslinked elastic component formed from a linear block copolymerUS8518006May 30, 2008Aug 27, 2013Kimberly-Clark Worldwide, Inc.Personal wear absorbent article with tabUS8518341Jul 6, 2012Aug 27, 2013Kimberly-Clark Worldwide, Inc.Collapsible sterilization containerUS8551895Dec 22, 2010Oct 8, 2013Kimberly-Clark Worldwide, Inc.Nonwoven webs having improved barrier propertiesUS8563017Dec 15, 2008Oct 22, 2013Kimberly-Clark Worldwide, Inc.Disinfectant wet wipeUS8569221May 2, 2008Oct 29, 2013Kimberly-Clark Worldwide, Inc.Stain-discharging and removing systemUS8585671Mar 7, 2012Nov 19, 2013Kimberly-Clark Worldwide, Inc.Personal wear absorbent article with disposal tabUS8623289Dec 16, 2009Jan 7, 2014Kimberly-Clark Worldwide Inc.Single use sterilization containerUS8772218Aug 21, 2013Jul 8, 2014Kimberly-Clark Worldwide, Inc.Stain-discharging and removing systemUS8871232Dec 13, 2007Oct 28, 2014Kimberly-Clark Worldwide, Inc.Self-indicating wipe for removing bacteria from a surfaceUS8936740Aug 13, 2010Jan 20, 2015Kimberly-Clark Worldwide, Inc.Modified polylactic acid fibersUS20110040040 *Jul 16, 2010Feb 17, 2011Fiberweb Corovin GmbhPolymer mixtureDE19812925A1 *Mar 24, 1998Sep 30, 1999Asota GmbhEasily recycled dimensionally stable moulded laminate especially for car carpetDE29706968U1 *Apr 17, 1997Jun 19, 1997Asota GmbhZweischichtiges NadelvliesEP0370835A2 *Jun 27, 1989May 30, 1990Kimberly-Clark CorporationNonwoven continuously-bonded trilaminateEP0530769A1 *Sep 2, 1992Mar 10, 1993Hoechst Trevira GmbH &amp; Co KGProcess and intermediary product for the production of a thermofused laminate and use thereofEP0570215A2 �May 12, 1993Nov 18, 1993DON &amp; LOW (HOLDINGS) LIMITEDImprovements in and relating to liquid impermeable and liquid vapour permeable laminatesEP0674035A2 *Feb 24, 1995Sep 27, 1995Kimberly-Clark CorporationPolyethylene meltblown fabric with barrier propertiesEP0723043A2Oct 4, 1995Jul 24, 1996Fiberweb Sodoca SarlComposite structure made from derivates of lactic acid and its method of productionEP0742305A1 *May 3, 1996Nov 13, 1996DON &amp; LOW NONWOVENS LIMITEDPermeable fabricsEP1245753A2 *Feb 28, 2002Oct 2, 2002Carlisle Management CompanySinge-ply roofing membrane with laminated, skinned nonwovenEP1950343A1Apr 30, 2003Jul 30, 2008Kimberly-Clark Worldwide, Inc.Non-woven through air dryer and transfer fabrics for tissue makingEP2561792A1Aug 23, 2007Feb 27, 2013Kimberly-Clark Worldwide, Inc.Polish and polishing mittsWO1993007323A1 *Aug 11, 1992Apr 15, 1993Minnesota Mining & MfgWipe materials based on multi-layer blown microfibersWO1993010300A1 *Nov 19, 1992May 27, 1993Fiberweb North America IncComposite nonwoven fabrics and method of making sameWO1994019524A1 *Feb 11, 1994Sep 1, 1994Joachim BauerComposite nonwoven fabric and process for producing the sameWO1994028224A1 *May 17, 1994Dec 8, 1994Kimberly Clark CoLightweight nonwoven web laminates with improved comfort and barrier propertiesWO1995009728A1 *Sep 30, 1994Apr 13, 1995Du PontControlled-porosity, calendered spunbonded/melt blown laminatesWO1996002695A1 *Jul 13, 1995Feb 1, 1996Owens Corning Fiberglass CorpBicomponent and long fiber product definition for splittable packWO1996018763A1 *Dec 13, 1995Jun 20, 1996Hp Chemie Pelzer Res & DevSelf-adhesive reinforcing material for textile fibre non-woven fabricsWO2000037723A2 *Dec 20, 1999Jun 29, 2000Kimberly Clark CoFine multicomponent fiber webs and laminates thereofWO2007070151A1Oct 4, 2006Jun 21, 2007Kimberly Clark CoTherapeutic kit employing a thermal insertWO2007078343A2Aug 25, 2006Jul 12, 2007Kimberly Clark CoBacteria capturing treatment for fibrous websWO2009022248A2Jul 29, 2008Feb 19, 2009Kimberly Clark CoA disposable respirator with exhalation ventsWO2009022250A2Jul 29, 2008Feb 19, 2009Kimberly Clark CoA disposable respiratorWO2009050610A2Sep 4, 2008Apr 23, 2009Kimberly Clark CoCrosslinked elastic material formed from a linear block copolymerWO2009077884A1Sep 11, 2008Jun 25, 2009Kimberly Clark CoFilm formed from a blend of biodegradable aliphatic-aromatic copolyestersWO2009077889A1Sep 17, 2008Jun 25, 2009Kimberly Clark CoAntistatic breathable nonwoven laminate having improved barrier propertiesWO2009138887A2Mar 30, 2009Nov 19, 2009Kimberly-Clark Worldwide, Inc.Latent elastic composite formed from a multi-layered filmWO2009147544A2Apr 14, 2009Dec 10, 2009Kimberly-Clark Worldwide, Inc.Fibers formed from a blend of a modified aliphatic-aromatic copolyester and thermoplastic starchWO2012143464A1Apr 19, 2012Oct 26, 2012Ar Metallizing N.V.Antimicrobial nonwoven fabric* Cited by examiner, � Cited by third partyClassifications U.S. Classification442/382, 442/393, 428/373, 428/374, 156/62.2, 442/340, 156/62.4, 156/62.8International ClassificationB32B5/08, D04H13/00, D04H5/06Cooperative ClassificationD04H13/007, D04H5/06, B32B5/08European ClassificationD04H5/06, B32B5/08, D04H13/00B5Legal EventsDateCodeEventDescriptionJan 26, 2000FPAYFee paymentYear of fee payment: 12Apr 21, 1997ASAssignmentOwner name: KIMBERLY-CLARK WORLDWIDE, INC., WISCONSINFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:KIMBERLY-CLARK CORPORATION;REEL/FRAME:008519/0919Effective date: 19961130Aug 25, 1995FPAYFee paymentYear of fee payment: 8Sep 9, 1991FPAYFee paymentYear of fee payment: 4Mar 14, 1989CCCertificate of correctionJan 23, 1987ASAssignmentOwner name: KIMBERLY-CLARK CORPORATON, 401 NORTH LAKE STREET,Free format text: ASSIGNMENT OF ASSIGNORS INTEREST.;ASSIGNORS:BROCK, ROBERT J.;CONN, WILLIAM;WEBER, JAMES M.;REEL/FRAME:004663/0137Effective date: 19870123Owner name: KIMBERLY-CLARK CORPORATON, A CORP. OF DE., WISCONSFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BROCK, ROBERT J.;CONN, WILLIAM;WEBER, JAMES M.;REEL/FRAME:004663/0137RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services