WO2001026871A1 - Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof - Google Patents
Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof Download PDF
WO2001026871A1
WO2001026871A1 PCT/AU2000/001226 AU0001226W WO0126871A1 WO 2001026871 A1 WO2001026871 A1 WO 2001026871A1 AU 0001226 W AU0001226 W AU 0001226W WO 0126871 A1 WO0126871 A1 WO 0126871A1
PCT/AU2000/001226
Khouri, Anthony
A heavy duty rotary concrete mixing drum capable of attachment to a vehicle. The drum comprises a first end which engages a vehicle powered drive assembly which rotates the drum for mixing of said concrete and a second end from which mixed concrete is discharged. The drum is manufactured from at least one layer of plastics material; wherein the drum includes a wall having integral internal formations which promote mixing and discharge of said concrete and an inner surface which promotes mixing of the concrete.
VEHICLE MOUNTED PLASTICS DRUM FOR CONCRETE MLXTNG AND METHODS OF MANUFACTURE
The present invention relates to concrete mixing apparatuses and more particularly relates to a vehicle mounted plastics drum for mixing concrete and a methods manufacture thereof.
The building industry makes widespread use of concrete mixing trucks for transportation of ready mixed concrete to sites for concrete pours. These trucks typically comprise a large mixing assembly including a mixer drum mounted to the vehicle and which is connected to a mixer drive for mixing concrete contents during transportation and for discharge of the contents on site. The drive system comprises a gear box which takes power from the vehicle motor and which applies a mixing torque to the drum imparting axial rotation to the drum with the torque being adjustable depending upon the operating requirements. The above general arrangement is described in United States patent 4,585,356 which discloses a concrete mixer truck having a mixer drum adapted to be rotated by the traction motor of the vehicle through an auxiliary transmission of the traction motor transmission.
According to the known vehicle mounted mixing assemblies, the mixing drum is typically of heavy duty steel construction and is disposed at approximately 10 to 15 degrees from horizontal. The drum is fitted with internal vanes or mixing blades defining an archimedian spiral so that as the drum rotates in a first direction the concrete held therein is mixed and as the drum is rotated in the opposite direction, the concrete is discharged from the drum via an elevated discharge orifice under the reverse action of the internal spiral vanes. The drum is disposed such that the drive end is lowest and the discharge end is highest relative to a generally horizontal plane of the vehicle. While steel drums have been in use for many years, they suffer from a number of attendant disadvantages, relating to their cost of manufacture and replacement, working life, wear characteristics, weight and volume.
Typically, a steel drum used every day might last three to five years, thereafter requiring replacement at significant cost. The abrasion of internal surfaces is increased where there are changes of slope in the drum walls usually where the segments of the drum are joined. The mixing blades are welded to the internal surface of the drum causing sharp angled recesses in which concrete can gather and eventually build up degrading the internal surface and providing a catchment for further unwanted build up of concrete. By its nature, a steel surface is relatively smooth and whilst this may be desirable for the purpose of preventing concrete build up on the walls of the drum, the interface between the concrete and steel wall is an area of abrasion rather than concrete mixing.
Ideally, mixing of concrete should take place throughout the whole mix, but in the steel drums, optimum mixing does not take place at the boundary layer and in crevices in which concrete may collect. In fact, due to the nature of the frictional interface between the steel surface and concrete boundary layer, laminar flow occurs resulting in little or no mixing at the boundary layer. The reason for this is that the aggregate in the concrete slides and abrades ( with reduced or no mixing) rather than rotates to facilitate mixing. Thus there are 'dead' spots in the mix where no mixing takes place and where there is an increased potential for unwanted collection of concrete. In addition to the above problems associated with the use of steel mixing drums, there are cost and weight factors which add to inherent inefficiencies in use of steel drums. Due to the dead weight of the steel drum, its volume must be restricted so the combination of the dead weight and concrete weight must be maintained within the maximum allowable loading limits for the vehicle to which the drum is attached. The inventor to considered the possibility of using a lightweight material such as plastics for construction of a concrete mixing drum as a substitute for steel whilst recognising that there were numerous structural and manufacturing difficulties to be overcome in making the transition to plastics not the least of which was the production of a drum which could withstand the high static and dynamic loadings to which truck mounted mixing drums are subject to in normal operation. If the weight of the drum could be reduced without compromising and possibly increasing drum volume the weight reduction could be taken up with additional concrete thereby increasing the pay load.
There are variety of concrete mixing drum arrangements disclosed in the prior art none of which as far as the inventor is aware anticipate the arrangements to be described herein. United States patent 4,491,415 discloses a lightweight, pear shaped rotary mixing device open at one end and having an axially elongated socket at the large end. The drum is rotatably supported on a unitary base having a transversely extended forward end and an upwardly and angularly extending rear end providing a bearing portion detachably engagable with the socket to rotatably support the drum at an inclination of about 35 degrees. The drum has a plurality of axially extending radial fins for lifting contents in rotation thereof and is preferably fashioned from molded plastics material either as a unitary body or as a plurality of interfitting parts. The drum described in this patent is for light duty operation and does not have the structural and materials characteristics necessary for heavy duty concrete mixing operations. United States Patent 5,118,198 discloses a cement mixing apparatus with a cradle support assembly and including a polyethelyne cement mixing drum held and supported by a cradle arm assembly formed of cradle base support braces and upright cradle arms which interfit into cradle arm recesses which are preformed with the polyethylene drum. A bull gear drives the polyethylene drum. The drum disclosed in this patent is intended for light duty cement operations and does not address the structural and manufacturing requirements for heavy duty operations. United States patent 5,492,401 discloses a concrete mixer with a mixing drum consisting of high density crosslinked polyethylene material. The drum includes a bottom supported buy a conventional rigid metal pan secured to the external surface thereof to rigidify the plastic drum and extend the life expectancy of the plastic drum by enabling the concrete mixer to be used to complete a mixing job at a job site even though movement of the concrete mix within the drum during repetitive mixing cycles may ultimately wear a hole through the bottom of the plastic drum. Paddle assemblies are positioned interiorly of the drum and oriented to maintain minimum splashing during the mixing operation. Not only is the drum disclosed in this patent unsuitable for heavy duty vehicle mounted operation the patent in fact teaches a means to accommodate a wear failure on site whereby a hole could be worn through the wall of the drum.
In one broad form of the apparatus aspect the present invention comprises: a vehicle mounted rotary concrete mixing drum having an opening at one end for receiving and discharge of concrete therefrom and at the other end means for engaging a drive assembly so as to rotate the drum for mixing or discharging concrete; wherein, the drum is manufactured from at least one mould using at least one plastics material; wherein the drum further includes detachable or integrally attached vanes which outstand from the internal surface of the drum forming an archimedian spiral disposed such that when the drum is rotated in a first direction. the concrete contents are mixed and when the drum is rotated in a second direction the contents are discharges from said drum; and wherein the internal surface of the drum is formed or lined with an elastomer which causes mixing of the contents of the concrete at the concrete boundary layer; and wherein the weight of the drum is such that when full, the total weight of the drum and contents is lighter than for a steel drum of an equivalent size when full. In another broad form of the apparatus aspect, the present invention comprises: a vehicle mounted rotary concrete mixing drum having an opening at one end for receiving and discharge of concrete therefrom and at the other end means for engaging a drive assembly so as to rotate the drum for mixing and discharging concrete; wherein, the drum is manufactured from two or three moulds using at least one layer of plastics material; wherein the drum further includes detachable or integrally attached vanes which outstand from the internal surface of thedrum forming an archimedian spiral disposed such that when the drum is rotated in a first direction, the concrete contents are mixed and when the drum is rotated in a second direction the contents are discharged from said drum; and wherein the internal surface of the drum comprises a polyurethane layer to enhance mixing of the contents of the concrete at the concrete boundary layer; and wherein the weight of the drum is such that when full, the total weight of the drum and contents is lighter than for a steel drum of an equivalent size when full. In another broad form of the apparatus aspect, the present invention comprises: a vehicle mounted rotary concrete mixing drum having an opening at one end for receiving and discharge of concrete therefrom and at the other end means for engaging a drive assembly so as to rotate the drum for mixing or discharging concrete; wherein, the drum is manufactured from two or three moulds and comprises a first plastics material such as woven fibreglass forming an outer surface of the drum and a second plastics material such as polyurethane or like elastomer forming an inner surface of the drum; wherein the outer and inner surfaces together form a wall of the drum and wherein the drum further includes detachable or integrally attached vanes which extend inwardly from the wall of the drum forming an archimedian spiral disposed such that when the drum is rotated in a first direction, the concrete contents are mixed and when the drum is rotated in a second direction the contents are discharged from said drum; and wherein the inner polyurethane surface of the drum provides wear resistance and enhances mixing of the contents of the concrete at the concrete boundary layer; and wherein the weight of the drum is such that when full, the total weight of the plastics drum and contents is lighter than for a steel drum of an equivalent or smaller size when full. In a broad form of the method aspect the present invention comprises; a method of manufacture of a vehicle mounted plastics concrete mixing drum comprising the steps of; a) preparing a mould having a surface defining an internal profile of said drum which includes a wall having recesses which provide a mold part for continuous helical mixing blades included in said drum: b) applying a release agent to an outer surface of said mould; c) applying over said release agent a plastics layer in liquid form and allowing said plastics layer to set against the mould so as to form a first layer of a wall of said drum; d) applying a bonding layer to said plastics layer; e) applying a fibre reinforced composite layer to said bonding layer;and f) removing the mold from the interior of said drum. A method of manufacture of a vehicle mounted plastics concrete mixing drum comprising the steps of; a) taking a male mould defining an internal profile of said drum including a wall having recesses which form a continuous helical mixing spiral: b) applying a release agent to an outer surface of said mould; c) applying over said release agent an elastomer in liquid form and allowing said elastomer
to polymerise against the mould so as to form a first layer of a wall of said drum; d) applying a bonding layer to said elastomer; e) applying a filament fibre reinforced composite layer to said adhesive layer; f) winding said filament about said drum to form an outer fibre reinforced structural matrix. According to another broad form of the method aspect, the present invention comprises; a method of manufacture of a vehicle mounted plastics rotatable concrete mixing drum comprising the steps of; a) taking a male mould part whose external surface defines an external profile of a concrete mixing drum; b) applying a release agent to an outer surface of said mold part; c) applying over said release agent an elastomer in liquid form and allowing said elastomer
to polymerise against the mould so as to form a first layer of said drum; d) applying a bonding agent to said elastomeric layer as a substrate coupling layer to receive an outer structural layer of filament; e) winding said filament about said drum to form an outer structural matrix.
According to another broad form of the method aspect the present invention comprises; a method of manufacture of a vehicle mounted concrete mixing drum comprising the steps of: a) fabricating base mold sections for receiving plastics material used in the formation of said drum; b) assembling said base sections mold sections on a mandrel; c) clamping said mold sections together to form a helical groove about said mold sections; d) applying a plastics material to the outside of said mold sections whereby the plastics material forms an interior layer of said drum; e) applying an intermediate adhesive layer to the outside of said interior layer; f) applying to said adhesive layer a fibre reinforced outer structural layer wound about said mold sections wherein said interior, intermediate and outer layers form a wall of said mixing drum.
According to a preferred embodiment, the drum is manufactured from three molded parts two of which comprise end parts of the drum and a third comprising a central part for location between said end parts. Each mould part has a formation which imparts to the drum part formed by the mould part, a part spiral extending inwardly from the wall of the drum part such that when the drum parts are engaged together, an internal archimedian spiral is formed. The moulds are configured such that when the moulds are mated together, the internal archimedian spiral used for both mixing and discharge of concrete from the drum is complete. Preferably, the outer mould surfaces are prepared with a release agent so the mold may be readily removed after curing. Preferably the elastomer is polyurethane and has a surface property which reduces abrasion yet enhances mixing. Preferably there are three mould sections in which the junctions form part of the mixing spirals such that the sections are joined along the spirals.
Figure 1 shows a side elevation of a prior art mixing drum;
Figure 2 shows a side elevation of a cement mixing drum according to one embodiment of
the invention; Figure 3 shows a cross section through the junction of two drum parts showing the join construction; Figure 4 shows an enlarged view of the apex of the helical blade3;
Figures 5a -d show the first stages of preparation of the drum. Figure 6 shows an enlarged profile section of a typical mixing blade.
Figures 7a-c shows an end elevation view of the mold clamping and inflation steps. Figure 8 shows the mold and drum stored for demolding.
Figure 9 shows a drum inside a grit chamber in which a grit jet is traversed over the shell surface to prepare the so it is chemically receptive to the bonding of the next stage.
Figure 10 shows the drum mounted for rotation on a computer controlled winding machine. Figures 1 la -b show a two step process for application of a gel coat. Figure 12 shows the drum adapted with a stiffening ring which distributes loads from trunion rollers incorporated on the vehicle on which the drum is to be mounted.
Figure 13 shows the orientation of the drum during application of the drip ring. Figure 14 shows a cross section of an end region of a drum including between spiral section and wall a baffle imparting rigidity to the drum. Figure 15 shows a cross section of a typical interface between a concrete mix and a steel wall. Figure 16 shows an enlarged view of the boundary layer wall / concrete interface in a
plastics mixing drum according to a preferred embodiment of the invention. Figures 17a-o show the various stages in construction of a drum according to an alternative embodiment; Figure 18 a-f shows the various steps in the construction of a solid core blade according to an alternative blade arrangement . Figure 19a-p shows the various stages of construction of a drum according to a preferred embodiment. Figure 20a-f shows steps on the construction of a solid core helical blade according to an alternative embodiment . Figure 21 shows a cross sectional view of a solid core blade interaction with concrete during rotation of the drum. Figure 1 shows an elevation view of a known steel mixing drum 1 which is typically constructed from separate prefabricated sections 2, 3 and 4 which are welded together at seams 5, 6 and 7. At seams 5, 6 and 7 the welded joints which are subject to concentrated wear due to the change in surface direction at the join. The concentrated wear points in the prior art steel drums reduces the working life of the drums necessitating costly repair or replacement. Steel drums are fabricated from rolled flat sheets which form cones and a cylinder which are then joined together by welding. Archimedian spirals are then welded to the inner surface of the drum resulting in a high specific gravity vessel whose self weight reduces the amount of concrete which can be carried by the vehicle to which it is attached. As previously indicated, the steel drums suffer from a number of disadvantages including susceptibility to abrasion at the junctions of the cylindrical and conical sections and the tendency for unwanted concrete build up at the sharp corners and crevices formed by the mixing blades. In addition, the smooth internal surface of the steel drum promotes sliding abrasion and inhibits mixing at the boundary layer due to the low coefficient of friction at the concrete/metal interface.
Figure 2 shows an external profile of a fibre reinforced composite concrete mixing drum 8 according to one embodiment of the invention. The drum includes an internal archimedian spiral formed by helical blades or vanes which mix concrete during rotation of the drum in one direction and discharge concrete when the drum is rotated in an opposite direction. The drum is generally pear shaped and includes an opening 9 at one end for entry and discharge of concrete. The arrangement of figure 2 is arrived at by application of the method aspect of the invention which will be described in detail below. Drum 8 is constructed from a fibre reinforced plastic structural shell with an elastomeric interior having a surface property which imparts abrasion resistance to the concrete but increases the mixing at the boundary layer of the concrete and drum wall by forced rotation of aggregate. A preferred method of construction of the drum will now be described in detail. Whilst the embodiment described employs three mould parts it will be appreciated that the drum may be constructed from a lesser or greater number of parts. It has been found however, that a three part construction is preferable in view of the shape of the finished drum. According to the preferred embodiment, drum 8 is constructed from three mould parts 10, 11 and 12 according to the following methodology. Figure 3 shows typical profiles of mold parts 13, 14 and 15 wherein part 13 is constructed to engage a drive system mounted on a vehicle for rotating said drum, part 14 is an intermediate section which engages parts 13 and 15. Part 15 includes a discharge opening through which mixed concrete is discharged. The first step in the construction of the mixing drum is the preparation of the mold from which the drum will be produced. The mold is preferably constructed in three parts as this enables ease of extraction form mold formers and also allows for the formation of mixing drums of different sizes according to requirements. For instance the length of the drums can be increased by changing the size of intermediate section 14. Mold sections 13, 14 and 15 are each formed in separate molds from expanded polystyrene beads. Steam heat is applied through slots in each mold thereby fusing the beads against the mold surface. The polystyrene surface finish of the mold may be improved by the application of a fast drying liquid. The external profile of the mould parts when joined provide the mold for the inner surface of the drum. The mold profile includes helical grooves which are the inverse of helical mixing blades which extend from an inner surface of the finished drum.
Figure 4 shows an assembled mold mounted on a cantilevered mandrel 17. The mold sections include mating dowels which align corresponding parts of the mold profiles and are clamped together with an adhesive. Figures 5a -d show the first stages of preparation of the drum. At the commencement of this stage the mold is mounted on mandrel 17 which is capable of axial rotation. The operation of the mold is computer controlled and employs a robot which rotates the mandrel. The mold surface is prepared with a release agent which will enable release of the mold from the drum on completion of the method steps. A spray head 18 delivers a polyurethane elastomer to the surface of the mold which forms an inner layer of the drum. The spray is applied normal to the surface of the drum which will at this stage be rotating according to parameters fed into the computer. As the mold rotates on the mandrel the spray head moves to follow the mold surface and in particular the path of the grooves. A computer program controls the delivery of the polymer to the mold surface. The application of the polyurethane elastomer to the surface of the mold takes place in two stages. First, the spray is applied to the grooves of the mold which will form the helical blades of the drum. Spray head 18 follows the contour of the helix about the mold and deposits a uniform coating onto the sides of the blades with an additional thickness deep in the groove which will form the helical spiral blade tip. The additional material provides abrasion resistance during operation. In the second part of the spray operation, spray head 18 is changed to spray the polyurethane elastomer normal to the surface of the mold according to the required thickness. Additional polyurethane may be sprayed where additional thickness is required in areas of high wear. If required, multiple coats may be deposited in one or both stages. According to one embodiment one or more of any additional layers may be differentially coloured with to provide wear indicators. A white pigment in the surface layer may be provided for cleaning and inspection after use. The polyurethane is allowed to gel following which a chemical layer is sprayed onto the polyurethane surface to ensure bonding with the next fibre reinforced composite layer. Prior to application of the fibre reinforced layer, a rope formed of multiple glass fibre strands is delivered from a dispensing creel into the grooves of the spiral helix. This part of the operation is represented by figure 5d. The rope is drawn through a bath of resin and is lead through a guide eye to fall into the blade groove. Tensioning of the rope pulls it into the groove. When the repor hardens it becomes a high strength reinforcing bar along the full length of the helical spiral. The polyurethane which is sprayed onto the mold by this stage generally conforms to shape of the mold except for bridging that is required between the groove walls. In the example of Figure 6, there is shown an enlarged profile section of a typical mixing blade . Each blade comprises an elastomeric layer 20 which forms the inner surface of the drum. A coupling layer 21 is applied over the elastomeric layer following which a structural layer 22 is applied inside the concave recess 23. This process is completed for each section of spiral at a join whereupon, a further coupling layer 25 is applied to the remainder of the outer surface of the drum over which is applied a structural layer 26 which is preferably a fibre reinforced composite to form a structural shell. Included deep inside recess 23 is a continuous filament and resin rope 35.
A rigid shell is required to bridge across the helical groove and this is provided by sprayed composite resin and chopped glass strands completing the structural layer 26. The sprayed resin is hand rolled followed by clamping then inflation of the mold before the polyurethane has gelled. Figures 7a-c show an end elevation view of the mold clamping and inflation steps. Figure 7a shows the clamping assembly 30 in the open configuration. Mold and partially completed plastics drum is represented by broken line 31. Before the composite of resin and chopped glass strands has gelled the mold is located on clamp assembly 30 whereupon arms 32 and 33 are closed over the composite . As shown in figure 5c. After clamping, the mold is inflated to ensure complete contact with the fibre reinforced composite layer. The mold and drum 31 are stored for four hours until the resin is sufficiently cured for the next stage. Figure 8 shows the mold and drum 31 stored for demolding. Figure 9 shows drum 31 inside grit chamber 32 in which a grit jet is traversed over the shell surface to prepare a surface which is chemically receptive to the bonding of the next stage. The next step involves filament winding of a fibre reinforced structural layer. A winding arrangement as shown in figure 10 is arranged to wind resin wetted fibre rovings around a rotating former. The tensile strength of the windings which may be in the order of 600 MPa. Figure 10 shows drum 31 mounted for rotation on a computer controlled winding machine to enable winding of glass rovings 34. To obtain the optimum physical properties of the filament wound structure the fibres are aligned to the loads imposed in use of the finished drum. Typical loadings on the drum are axial bending under weight of wet concrete, an applied dynamic load at the drive end of the drum, driving torque and support loads at the discharge trunion rolls. The winding pattern of the filaments aligns the fibres at 10 degrees at mid span to withstand bending stresses, increasing in angle and in wall thickness towards the discharge end to accommodate applied roller loads.
According to one embodiment the winding machine has three motor drives which rotate mandrel 17, move carriage parallel to the mandrel axis and a third motion at right angle to this. The rovings which line the drum are drawn through the resin bath and applied to the surface of the drum as a wide ribbon comprising thousand of tensioned fibres. The composite is applied by winding filament about the drum over the coupling layer 25 to form a fibreglass matrix with high strength properties sufficient to withstand normal operating loads applied during mixing and transporting concrete. The windings overlap until the required thickness is reached. The surface of the drum is covered with wet resin and small irregularities which need to be addressed to provide the external finish. As a result of this construction, the spiral mixing blades inside the drum are hollow with high bending and shear resistance during mixing operations. The inner elastomeric surface is highly resistant to abrasion by concrete yet it is softer and lighter than the steel equivalent. The higher resistance to abrasion is facilitated by the natural elastic deformation of the elastomer which absorbs the kinetic energy of the concrete particles without gouging of the surface material. In addition, due to the property of the inner surface which will preferably be polyurethane, the concrete will be mixed rather than slide at the boundary layer ensuring efficient mixing of the concrete throughout the mix and reduction of abrasion due to the smooth curves throughout the interior of the drum. In a further step, the structural layer is finished with a smooth pigmented resin which is applied utilising a clamp similar to that used for completion of the resin layer. Figures 1 la and b show a two step process for application of a gel coat. Shell 40 is larger than shell 30 to accommodate the additional layer of the windings. As shown in figure 12 drum 31 is adapted with a stiffening ring 43 which distributes loads from trunion rollers incorporated on the vehicle on which the drum is to be mounted. This stage allows application of a corporate livery or alternative indicia into the structure of the finished drum. To achieve this shell parts 41 and 42 are printed with a selected livery and sprayed with a background gel coat. After gelation a light layer of reinforced composite is applied and allowed to set. The shells re prepared in advance of the operation of application of the fibreglass windings while the resin is still liquid whereupon the shells are clamped around the windings thereby extruding out any excess resin. The shell mold assembly is mounted vertically and atwo part compound is injected into the track ring mold space. Figure 13 shows the orientation of the drum 31 during this step. Once the resin has gelled, the shell molds are removed and the dischage end overwind is trimmed and a polyurethane drip flange is bonded at the discharge end. The final step involves removal of the mold remaining inside the drum followed by closure of the mandrel hole and cosmetic finishing. The mandrel is removed and the hole fitted with a pipe connection. The drum is stood vertically and acetone which dissolves the polystyrene is pumped out of the interior which is then cleaned and washed. The drum is then finished by removal of any resin flash. Figure 14 shows a cross section of an end region of a drum 50 including between spiral section 51 and wall 52 a baffle 53 imparting rigidity to the drum. The baffle plate is preferably glued into position. Figure 15 shows a cross section of a typical interface between a concrete mix 54 and a steel wall 55. Due to the inherent smoothness of the steel surface 56 the concrete tends to slide and abrade rather than mix. Figure 16 shows a cross section of a typical interface between a concrete mix 57 and an elastomeric boundary layer 58. As shown by arrows 59 the aggregate in the mix rotates due to the friction between concrete 57 and surface 58. The rotation avoids excessive abrasion of the surface 58 and enhances concrete mixing. Furthermore, as surface 58 is able to deflect, energy is dissipated by the inherent elasticity of the surface contributing to the reduction in wear. According to the preferred embodiment, the spiral blades inside the drum range varying between 0.5 and 2 metre pitch. At the drive end of the drum the spirals are approximately 2 metre pitch. The blades are reinforced by chopped strand, woven cloth or filament winding. The moulds may allow for a variety of helix pitches of the blades. Preferably, the radius of the root of the blade is greater than 10mm to avoid unwanted accumulation of set concrete. Furthermore, the blades are strengthened by their molding integrally with the wall of the drum and have a stiffness factor which will sustain all applied normal operating loads. In an alternative embodiment, the internal blades may be detachably fixed to the wall of the drum.
An alternative method for construction of a fibre reinforced drum is shown in Figures 17a-o. Figure 17a shows a profiles of half mold part 60 which is coupled with a corresponding half to form completed mold 61. The first step in the construction of the mixing drum is the preparation of the mold from which the drum will be produced. The size of the drum may be changed by changing the dimensions of the mold. Mold section are each formed from separate molds from expanded polystyrene beads. Steam heat is applied through slots in each mold thereby fusing the beads against the mold surface. The external profile of the mould parts when joined provide the mold for the inner surface of the drum. The mold profile includes helical grooves which are the inverse of helical mixing blades which extend from an inner surface of the finished drum.
Figure 17b shows an assembled mold mounted on a cantilevered mandrel 62. The mold sections include mating dowels which align corresponding parts of the mold profiles and are clamped together with an adhesive. Figure 17c shows mold 61 at a stage during which the polystyrene surface finish of the mold may be improved by the application of a fast drying liquid. Figures 17d -g show the first stages of preparation of the plastics drum according to the embodiment to be described. The mold is mounted on mandrel 62 which is capable of axial rotation. The operation of the mold is computer controlled and employs a robot which rotates the mandrel. The mold surface is prepared with a release agent which will enable release of the mold from the drum on completion of the drum. A spray head 63 delivers a polyurethane elastomer to the surface of the mold which forms an inner layer of the drum.
The spray is applied normal to the surface of the drum which will at this stage be rotating according to parameters fed into the computer. As the mold rotates on the mandrel the spray head moves to follow the mold surface and in particular the path of the grooves. The application of the polyurethane elastomer to the surface of the mold takes place in two stages. First, the spray is applied to the grooves of the mold which will form the helical blades of the drum. Figures 18a-f shows the various stages of construction of a solid core blade arrangement according to an alternative embodiment. Spray head 63 follows the contour of the helical groove 64 about the mold and deposits a uniform coating of polyurethane 65 against wall 66 terminating in the region of groove bottom 67. The layer applied includes a return portion 68 which provides a bed 69 into which is laid continuous glass fibre reinforced elastomer 70. Return portion 68 will form the helical blade tip and this will be strengthened by the glass fibre elastomer 70. Figure 18c shows an additional layer of polyurethane 71 sprayed over glass fibre elastomer 70 thereby completing the blade profile. The additional material strengthens the blade. In a second part of the spray operation, spray head 63 is changed to spray the polyurethane elastomer normal to the surface of the mold according to the required thickness. Additional polyurethane may be sprayed where additional thickness is required in areas of high wear. If required, multiple coats may be deposited in one or both stages. To ensure that the solid core blade profile is retained during the second spraying operation, the cavity formed by helical groove 64 is covered by polyurethane mold insert 72 as shown in figure 18d. A layer of polyurethane 73 is then sprayed over insert mold 72 and also over the outside of drum 61. This is followed by the application of a chopped glass layer 74. Figure 17e represents the stage of blade reinforcement and preparation and figure 17f represents the stage of application of the polyurethane coating over the outside of the drum following completion of the blade profile. According to one embodiment one or more of any additional layers may be differentially coloured with to provide wear indicators. A white pigment in the surface layer may be provided for cleaning and inspection after use. The polyurethane is allowed to gel following which a chemical layer is sprayed onto the polyurethane surface as represented by figure 17g to ensure bonding with the next fibre reinforced composite layer. A coupling layer is applied to the remainder of the outer surface of the drum over which is applied a structural layer which is preferably a fibre reinforced composite to form a structural shell. A rigid shell is required and this is provided by sprayed composite resin and chopped glass strands completing the structural layer. The sprayed resin is hand rolled followed by clamping as shown in figures 17 i, j and k. Figures 17j and k show the clamping assembly 80 in the open and closed configurations respectively. Mold and partially completed plastics drum 68 is shown in figure 17j. Before the composite of resin and chopped glass strands has gelled the mold is located on clamp assembly 80 whereupon arms 82 and 83 are closed over the composite layer. After clamping, the mold may be inflated to ensure complete contact with the fibre reinforced composite layer. The mold 61 and drum 81 are stored for four hours until the resin is sufficiently cured for the next stage. Casting of a track ring and application of a drip flange area as previously described. The inner mold is removed as previously described and this includes removal of mold insert 72. Figure 18f shows a typical solid core blade profile 84 as described above. The blade satisfies strength requirements and is reinforced by curves in the blade profile as the blade traverses the helix about the finished drum interior. Preferred material of construction for the solid core blade will be sprayed SP85 polyurethane elastomer ( 85 shore A). Preferred reinforcing of the solid blade is high tensile glass fibre CC60 elastomer . Preferably, the tensile reinforcement is continuous along the length of the blades.
Figures 19a-p show an alternative method of construction of a plastics drum including an injection molding step. A number of the steps according to this embodiment are substantially the same as for the corresponding steps described with reference to figures 17a-o. The methods, however differ firstly in relation to the method of construction of the helical blade. Figures 19a-e show a mold 90 mounted on mandrel in the usual manner. Blade reinforcement operation represented by Figure 19 e is shown in more detail in Figures 20a-f. A spray head (not shown) follows the contour of the helical groove 99 about the mold 90 and deposits a uniform bed polyurethane 101 against contoured base 102 at the bottom of groove 103. As illustrated in figure 20a, bed 101 is trowelled prior to setting with a profiled trowel head 103 and this forms a molded recess 104 into which is laid continuous glass fibre reinforced elastomer 105 as shown in figure 20b. Bed 101 will form the helical blade tip and this will be strengthened by the glass fibre elastomer 105 along the length of the helical blade. The reinforcing elastomer 105 is prior to installation placed in a resin matrix under tension. Figure 20c shows inserted in groove 100 a polyurethane insert 106 which leaves a space between the insert and wall 107. The resulting space defines the final profile shape of a solid core blade. As shown in figure 20d, spacer blocks 107 are applied to the surface 107 of mold 90 over which is placed an external mold 108 as shown in figure 20e. The spacer blocks are preferably made of polyurethane which is the same material to be injected onto the cavity formed by the insert mold 106 and external mold 108. This arrangement corresponds to the steps illustrated by figures 19f-h. The mold 90 is preferably disposed vertically for injection molding of the inner layer of the drum. Figure 19g shows mold shell 108 in an open configuration and figure 19 h shows mold shell 108 closed for injection molding of polyurethane elastomer 109. Injection of cold setting polyurethane resin into the mold cavity bonds to the extruded elastomer and the matrix of the tensile member and forms the rest of the blade and the elastomeric interior of the concrete mixer. Figure 19i shows partially completed drum 120 inside grit chamber 121 in which a grit jet is traversed over the shell surface to prepare a surface which is chemically receptive to the bonding of the next stage. The next step involves filament winding of a fibre reinforced structural layer. A winding arrangement as shown in figure 19j is arranged to wind resin wetted fibre rovings 122 around a rotating former. While the resin is still wet, the gel coated external mold 123 is closed over the structural shell to form the external surface of the mixer. This mold includes a track ring for injection of material therein to form a track ring 124. Drip ring 126 may then be fitted. The mold 123 is removed to expose the drum and the internal mold 90 is then disolved or broken up for removal. The tensile strength of the windings may be in the order of 600 MPa. Figure 19j shows drum 120 mounted for rotation on a computer controlled winding machine to enable winding of glass rovings 122. To obtain the optimum physical properties of the filament wound structure the fibres are aligned to the loads imposed in use of the finished drum. Typical loadings on the drum are; axial bending under weight of wet concrete, an applied dynamic load at the drive end of the drum, driving torque and support loads at the discharge trunion rolls. The winding pattern of the filaments aligns the fibres at 10 degrees at mid span to withstand bending stresses, increasing in angle and in wall thickness towards the discharge end to accommodate applied roller loads.
The rovings which line the drum are drawn through the resin bath and applied to the surface of the drum as a wide ribbon comprising thousand of tensioned fibres. The composite is applied by winding filament about the drum over the bonding layer to form a fibreglass matrix with high strength properties sufficient to withstand normal operating loads applied during mixing and transporting concrete. The windings overlap until the required thickness is reached. The surface of the drum is covered with wet resin and small irregularities which need to be addressed to provide the external finish. As a result of this construction, the spiral mixing blades inside the drum are solid with high bending and shear resistance during mixing operations. The inner elastomeric surface is highly resistant to abrasion by concrete yet it is softer and lighter than the steel equivalent. The higher resistance to abrasion is facilitated by the natural elastic deformation of the elastomer which absorbs the kinetic energy of the concrete particles without gouging of the surface material. In addition, due to the property of the inner surface which will preferably be polyurethane, the concrete will be mixed rather than slide at the boundary layer ensuring efficient mixing of the concrete throughout the mix and reduction of abrasion due to the smooth curves throughout the interior of the drum. In a further step, the structural layer is finished with a smooth pigmented resin which is applied utilising a clamp similar to that used for completion of the resin layer. Figures 19k and 1 show a two step process for application of a gel coat. Shell 123 is larger than shell 108 to accommodate the additional layer of the windings. As shown in figures 19m and n drum 120 is adapted with a stiffening ring 124 which distributes loads from trunion rollers incorporated on the vehicle on which the drum is to be mounted. The stages illustrated in figures 19 k and 1 allows application of a corporate livery or alternative indicia into the structure of the finished drum as previously described. To achieve this, shell parts 123a and 123b are printed with a selected livery and sprayed with a background gel coat. After gelation a light layer of reinforced composite is applied and allowed to set. The shells are prepared in advance of the operation of application of the fibreglass windings while the resin is still liquid whereupon the shells are clamped around the windings thereby extruding out any excess resin. The shell mold assembly is mounted vertically and a two part compound is injected into a track ring mold space. Figure 19m shows the orientation of the drum 120 during this step. Once the resin has gelled, the shell molds are removed and the discharge end overwind is trimmed and a polyurethane drip ring 125 is bonded at the discharge end. The final step involves removal of the mold remaining inside the drum followed by closure of the mandrel hole and cosmetic finishing. The mandrel is removed and the hole fitted with a pipe connection. The drum is stood vertically as illustrated in figure 19o and acetone which dissolves the polystyrene is pumped out of the interior which is then cleaned and washed. The drum is then finished by removal of any resin flash. Figure 20f shows a cross sectional view of a completed blade 110 with mold 90 and mold shell 108 removed. The free end of the blade is enlarged relative to the blade thickness to contain the reinforcing tensile member within the elastomer and to protect the tensile fibres from abrasion as concrete is mixed.
As an alternative to the hollow blades previously described with reference to figures 5 and 6, solid core blades may be used. As the solid core blades which are in the form of a two start helix of variable pitch, application of tension to the high strength reinforcing member will tend to move the member towards the axis of the mixer. This movement is restrained by the radial tension in in the blade material. Concrete loads applied to the blades during mixing and discharge will induce tension in the tensile member in the blade interior so that the concrete loads are carried by tension alone on the components in the mixer. Because the blade material is a low modulus elastomeric material and the blade is restrained by the member along its interior edge and the attachment to the mixer shell along its outer edge the concrete loads will deflect the blade into a sail shaped surface cupped to contain the concrete. This effect is accentuated by curving the interior edge of the blade in the direction of motion of the concrete towards the closed end in the mixing zone and the open end in the concrete discharge zone. Preferably, the tensile member is formed of continuous fibres, such as glass, carbon and aramid reinforcing a reason matrix such as polyurethane, epoxy, polyester or vinylester. The fibres are placed under light tension during manufacturing process so they are uniformly loaded to give maximum strength. Reference in the specification to blades includes reference to a single helical blade along the length of a drum, a two start blade, a multiple start blade arrangement, vanes, paddles and any suitable member for internal mixing of concrete.
At the drive end of the drum there is provided a steel ring which is molded into the drum structure and proportioned to suit drive equipment. The arrangement is such that it will resist relative rotation between the ring and the fibre reinforced drum under applied torque. The drum also comprises a track ring, which transmits the vessel loading to the support rollers and is constructed from fibre reinforced plastic formed integral with the structural shell of the vessel. It is anticipated that the plastics drum will outlast its steel equivalent under the same working conditions by more than 10 years. The wall strength will be in the order of 600MPa at a thickness of approximately 8mm comprising approximately 2-8mm polyurethane and 2-8mm fibreglass winding. According to one embodiment, the elastomeric layers may be of contrasting colours to enable detection of wear spots.
A further advantage in the use of plastics for the mixing drums lies in the thermal properties of the plastics material. Hot conditions are undesirable for concrete mixing as they accelerate hydration reducing concrete workability which is an essential property required immediately following a concrete pour. In very hot climates, the conventional steel vehicle mounted mixing drums conduct high heat loads which increase heat at the concrete boundary layer due to contact with the super heated drum wall causing unwanted accelerated hydration. This phenomenon is difficult to avoid with steel drums as the conductivity of steel leads to high conductive heat transfer from the outer skin of the drum to the inner wall which is normally in contact with the concrete. In some hot climates, ice is placed in the steel drums in an attempt to arrest temperature increase inside the drum. As concrete hydration is an exothermic reaction, it is sensitive to external temperatures. Accordingly it is desirable that the concrete temperature remains acceptably low to ensure a satisfactory level of workability and to retard hydration. Steel drums heat up significantly and conduct heat through their thickness making the concrete vulnerable to the vagaries of temperature variation. Overheating of the concrete mix is a problem to be avoided and has in accordance with one aspect provided a method of manufacture of a plastics drum to take the place of the conventional steel drums thereby reducing the unwanted effects of high thermal conductivity typical of the steel drums. The plastics drum allows the concrete to remain workable inside the drum for longer periods compared to concrete in steel mixing drums under the same external temperature conditions and transporting concrete. The structural exterior shell is significantly strengthened by the process of filament winding which produces a structure with many times the strength and stiffness of random fibre composites. At the drive end of the drum the steel ring which is moulded into the drum structure is proportioned to suit drive equipment. The arrangement is such that it will resist relative rotation between the ring and the fibre reinforced drum under applied torque. The track ring, transmits the vessel loading to the support rollers and is constructed from fibre reinforced plastic formed integral with the structural shell of the vessel.
1 A heavy duty rotary concrete mixing drum capable of attachment to a vehicle; the drum comprising a first end which engages a vehicle powered drive assembly which rotates said drum for mixing of said concrete and a second end from which mixed concrete is discharged; wherein said drum is manufactured from at least one layer of plastics material; wherein the drum includes a wall having integral internal formations which promote mixing and discharge of said concrete and an inner surface which promotes mixing of the concrete.
2 A heavy duty rotary concrete mixing drum according to claim 1 wherein the drum comprises an inner layer of elastomeric material and an external structural layer.
3 A heavy duty rotary concrete mixing drum according to claim 2 wherein said internal layer includes a polyurethane elastomer.
4 A heavy duty rotary concrete mixing drum according to claim 3 wherein said external structural layer includes a fibre reinforced composite exterior.
5 A heavy duty rotary concrete mixing drum according to claim 4 wherein the wall of the drum includes fibreglass filament windings applied about said drum outside said inner polyurethane layer.
6 A heavy duty rotary concrete mixing drum according to claim 5 wherein said wall includes between said inner layer and said outer structural layer a bonding layer.
7 A heavy duty rotary concrete mixing drum according to claim 6 wherein said integral internal formations comprise helical blades extending from said inner layer.
8 A heavy duty rotary concrete mixing drum according to claim 7 wherein said integral helical blades have a variable pitch dimension of between 0.5- 2 meters.
9. A heavy duty rotary concrete mixing drum according to claim 8 wherein the strength of the structural layer of said drum is around 600MPa at a drum wall thickness of approximately 8mm.
10 A heavy duty rotary concrete mixing drum according to claim 9 wherein said polyurethane layer is approximately 2-8mm thick and said fibreglass filament windings are formed from a layer of approximately 2-8mm thickness.
11 A heavy duty rotary concrete mixing drum according to claim 10 wherein an inner surface of the polyurethane drum provides wear resistance and promotes mixing of the contents of the concrete at the concrete/wall boundary layer.
12 A heavy duty rotary concrete mixing drum according to claim 11 wherein the weight of the drum is such that when full, the total weight of the plastics drum and contents is lighter than steel drum of an equivalent size when full.
13 A heavy duty rotary concrete mixing drum according to claim 12 wherein said blades are formed by said elastomeric material and define a hollow internal cavity in each helical blade.
14 A heavy duty rotary concrete mixing drum according to claim 13 wherein said helical blades include a bonding layer adjacent said inner polyurethane layer and a structural layer adjacent said bonding layer.
15 A heavy duty rotary concrete mixing drum according to claim 14 wherein said helical blades include a fibre reinforced tension member disposed in said cavity outside said structural layer and along the length of the blade.
16 A heavy duty rotary concrete mixing drum according to claim 12 wherein said blades are solid core along the full length of the blades.
17 A heavy duty rotary concrete mixing drum according to claim 16 wherein said solid core blades further include embedded therein a continuous glass fibre reinforced elastomer disposed along the length of said blade.
16 A heavy duty rotary concrete mixing drum according to claim 15 wherein the drum is manufactured in three sections from three separate molds, the first of said sections forming an end which engages said drive assembly for mixing said drum, the second said sections including said opening for discharge of said concrete from said drum and the third of said sections providing an intermediate junction between the first and second parts.
17 A heavy duty rotary concrete mixing drum for mounting on a vehicle; the drum comprising an opening at one end for discharging concrete mixed in said drum, and at the other end means for engaging a drive assembly which rotates the drum for mixing and discharging concrete; wherein, the drum includes a wall manufactured using at least one base mold from layers of plastics materials ; wherein the drum further includes blades integrally attached which outstand from an internal surface of the wall of the drum and form an archimedian screw disposed such that when the drum is rotated in a first direction the concrete contents are mixed and when the drum is rotated in a second direction the concrete is discharged from said drum; and wherein the internal surface of the drum is formed from an elastomer which promotes mixing of the concrete at a concrete/drum boundary layer; and wherein, the total weight of the drum and contents when full is lighter than for a steel drum of an equivalent volume when full.
18 A vehicle mounted rotary concrete mixing drum having an opening at one end for discharge of concrete therefrom and at the other end means for engaging a drive assembly so as to rotate the drum for mixing and discharge of concrete; wherein, the drum includes a wall manufactured from layers of plastics material using three base moulds and further includes detachable or integrally attached blades which outstand from an inner surface of said wall; the vanes forming an archimedian spiral disposed such that when the drum is rotated in a first direction the concrete contents are mixed and when the drum is rotated in a second direction, the concrete discharged from said drum; and wherein the internal surface of the drum includes a polyurethane elastomer layer which promotes mixing of the contents of the concrete at the concrete boundary layer; and wherein the weight of the drum is such that when full, the total weight of the drum and contents is lighter than for a steel drum of an equivalent size when full.
19 A heavy duty rotary concrete mixing drum according to claim 18 wherein the drum is manufactured in three separate parts from said three separate molds, the first of said parts forming an end which engages said drive assembly, the second said parts including the opening for discharge of said concrete from said drum and the third of said parts providing an intermediate junction between the first and second parts.
20 A heavy duty rotary concrete mixing drum according to claim 19 wherein the wall of said drum includes an inner layer of elastomer, an intermediate chemical bonding layer and an exterior layer of a composite of resin and high strength wound fibre reinforcement.
21 A heavy duty rotary concrete mixing drum according to claim 20 wherein each said molds may be formed from materials selected from, expanded polystyrene, fibreglass, steel, rigid polyurethane foam.
22 A vehicle mounted rotary concrete mixing drum having an opening at one end for discharging concrete and at the other end means for engaging a drive assembly so as to rotate the drum for mixing and discharging concrete; wherein, the drum is manufactured from three moulds and comprises a first plastics material such as fibreglass forming an outer surface of the drum and a second plastics material such as polyurethane or like elastomer forming an inner surface of the drum; wherein the outer and inner surfaces together form a wall of the drum and wherein the drum further includes detachable or integrally attached blades which extend inwardly from the wall of the drum forming an archimedian screw disposed such that when the drum is rotated in a first direction, the concrete contents are mixed and when the drum is rotated in a second direction the contents are discharged from said drum; and wherein the inner polyurethane surface of the drum provides wear resistance and promoted mixing of the contents of the concrete at the concrete boundary layer; and wherein the weight of the drum is such that when full, the total weight of the plastics drum and contents is lighter than for a steel drum of an equivalent or smaller size when full.
23 A method of manufacture of a vehicle mounted plastics concrete mixing drum comprising the steps of; a) preparing a mould having a surface defining an internal profile of said drum which includes a wall having recesses which provide a mold part for continuous helical mixing blades included in said drum: b) applying a release agent to an outer surface of said mould; c) applying over said release agent a plastics layer in liquid form and allowing said plastics layer to set against the mould so as to form a first layer of a wall of said drum; d) applying a bonding layer to said plastics layer; e) applying a fibre reinforced composite layer to said bonding layer; and f) removing the mold from the interior of said drum.
24 A method according to claim 23 comprising the further step prior to step a) of forming said mold from expanded polystyrene.
25 A method according to claim 24 comprising the further step of placing a fibre reinforced member along a concave tip of said helical mixing blade.
26 A method according to claim 25 comprising the further step prior to application of said fibre reinforced composite layer of moving said drum formed about said mold to a grit blasting chamber wherein a grit jet is traversed over the drum to prepare an outer surface of said drum with a bonding agent to receive said outer layer.
27 A method according to claim 26 wherein the drum is manufactured from three molded parts, two of which comprise end parts of the drum and a third comprising a central part for location between said end parts.
28 A method according to claim 27 wherein each mould part has a formation which imparts to the drum part formed by the mould part, a part spiral extending inwardly from the wall of the drum part such that when the drum parts are engaged together, an internal archimedian spiral is formed wherein the moulds are configured such that when the drum parts formed from the moulds are mated together, an internal archimedian spiral used for both mixing and discharge of concrete from the drum is formed.
29 A method according to claim 28 wherein, the outer mould surfaces are prepared with a release agent so said elastomer may be separated after curing.
30 A method according to claim 29 wherein said elastomer is polyurethane and has a surface property which reduces surface abrasion on the inner surface of said drum but promotes mixing of said concrete.
31. A method of manufacture of a vehicle mounted concrete mixing drum comprising the steps of: a) fabricating base mold sections for receiving plastics material used in the formation of said drum; b) assembling said base mold sections; c) clamping said mold sections together to form a helical groove about said mold sections; d) applying a plastics material to the outside of said mold sections whereby the plastics material forms an interior layer of said drum; e) applying an intermediate bonding layer to the outside of said interior layer; f) applying to said bonding layer a fibre reinforced outer structural layer wound about said mold sections wherein said interior, intermediate and outer layers form a wall of said mixing drum.
32 A method according to claim 31 wherein said mold parts are clamped together prior to application of said interior layer via aligning dowels and an adhesive.
33 A method according to claim 32 wherein said mold sections are fabricated from polystyrene beads.
34 A method according to claim 33 wherein said interior layer is formed by a polyurethane elastomer sprayed onto said mold sections.
35 A method according to claim 34 wherein said mold parts are mounted on a mandrel and rotated during application of said interior layer of said drum.
36 A method according to claim 35 wherein said interior layer of said drum is prepared in two steps, the first of which comprises the application of said polyurethane elastomer to helical grooves formed at the conjunction of said mold parts and the second of which comprises application of said polyurethane elastomer the remainder of said mold surface.
37 A method according to claim 36 wherein said first step is performed using a first spray head which traverses a path which aligns with said helical grooves as said mandrel rotates thereby applying a uniform distribution of said interior layer of said drum.
38 A method according to claim 37 wherein said second step is performed using a second spray head which traverses a path normal to said mold surface. 39 A method according to claim 38 wherein said intermediate adhesive layer is sprayed onto said polyurethane elastomer surface after said polyurethane elastomer surface has gelled.
40 A method according to claim 39 comprising the further step of immersing a composite member of glass fibre strands in a resin bath and winding said member into said grooves to reinforce the tip of said helical groove.
41 A method according to claim 40 comprising the further step of bridging said helical groove with a fibre reinforced composite of resin and chopped glass strands and applying said composite to the surface of said adhesive layer, hand rolling said strands and clamping about the exterior of said molds prior to setting of said resin and chopped glass strands.
42 A method according to claim 41 comprising the further step of inflating the mold and said interior polyurethane layer to ensure complete contact with and adhesion to said fibre reinforced composite.
43 A method according to claim 42 comprising the further step of allowing the resin of said composite to cure for a predetermined period.
44 A method according to claim 43 comprising the further step of grit blasting said fibre reinforced composite prior to application of an outer structural layer.
45 A method according to claim 44 including the further step of winding a fibre reinforced composite about said drum to form a structural layer.
46 A method according to claim 45 wherein filaments of said fibre reinforced composite are wound about and along said drum at angles of 10 degrees or greater and to a predetermined thickness.
47 A method according to claim 46 comprising the further steps of i) preparing a printed layer on a shell and covering said layer with a gel coat; ii) applying to said gel coat a light layer of fibre reinforced composite; whereupon while said resin of said composite is still liquid said shell is clamped about said drum until excess resin is squeezed from said shell.
48 A method according to claim 47 including the further step of injecting a compound into said mold shell to form a stiffening ring at the location of loads applied by drum support rollers.
49 A method according to claim 48 comprising the further step of filling said polystyrene mold with a chemical which dissolves said polystyrene enabling release of said mold from said drum.
50 A method according to claim 49 wherein said first and/or second steps applied in the application of said interior layer are repeated at least one more time.
51 A method according to claim 50 wherein said intermediate adhesive layer is sprayed onto said polyurethane elastomer surface after said polyurethane elastomer surface has gelled.
52 A method according to claim 51 wherein there are three mould sections which when joined together include a helical screw .
52 A method according to claim 23 comprising the further step of spraying a wall of said recesses with polyurethane to a predetermined thickness along said wall forming a blade profile terminating in a free end.
53 A method according to claim 52 wherein said blade profile includes at its free end a return forming a groove in which is placed a continuous glass fibre reinforced elastomer which reinforces said blade along the length of said blade.
54 A method according to claim 53 comprising the additional step of spraying additional polyurethane over said reinforcing glass fibre elastomer to embed said elastomer in said polyurethane. placing a fibre reinforced member along a concave tip of said helical mixing blade.
55 A method according to claim 54 comprising the further step prior to application of said fibre reinforced composite layer of moving said drum formed about said mold to a grit blasting chamber wherein a grit jet is traversed over the drum to prepare an outer surface of said with a bonding agent to receive said outer layer.
56 A method according to claim 55 wherein the drum is manufactured in three parts two of which comprise end parts of the drum and a third comprising a central part for location between said end parts.
57 A method according to claim 56 wherein each mould part includes a formation which imparts to the drum internal archimedian spiral for both mixing and discharge of concrete from the drum.
58 A method according to claim 57 comprising the further step of placing an insert mold over said recesses and spraying polyurethane elastomer over said insert mold and over the outer surface of said mold to form a continuous layer of polyurethane.
59 A method according to claim 58 comprising the further step prior to spraying said polyurethane of application of a release agent so said polyurethane layer may be separated from said mold.
60 A method according to claim 59 wherein said mold parts are mounted on a mandrel and rotated during application of said interior layer of said drum.
61 A method according to claim 60 wherein said interior layer of said drum is prepared in two steps, the first of which comprises the application of said polyurethane elastomer to the wall of said helical grooves formed in said mold parts and the second of which comprises application of said polyurethane elastomer the remainder of said mold surface. 62 A method according to claim 61 wherein said polyurethane is applied using a spray head which traverses a path which generally aligns with said helical recesses as said mandrel rotates thereby applying a uniform distribution of polyurethane along said wall of said recesses.
63 A method according to claim 62 wherein said second step is performed using a second spray head which traverses a path normal to said mold surface.
64 A method according to claim 63 wherein said intermediate adhesive layer is sprayed onto said polyurethane elastomer surface after said polyurethane elastomer surface has gelled.
65 A method according to claim 64 comprising the further step of inflating the mold and said interior polyurethane layer to ensure complete contact with and adhesion to said fibre reinforced composite.
66 A method according to claim 65 comprising the further step of allowing the resin of said composite to cure for a predetermined period.
67 A method according to claim 66 wherein filaments of said fibre reinforced composite are wound about and along said drum at angles of 10 degrees or greater and to a predetermined thickness.
68 A method according to claim 67 comprising the further steps of i) preparing a printed layer on a shell and covering said layer with a gel coat; ii) applying to said gel coat a light layer of fibre reinforced composite; whereupon while said resin of said composite is still liquid said shell is clamped about said drum until excess resin is squeezed from said shell.
69 A method according to claim 68 including the further step of injecting a compound into said mold shell to form a stiffening ring at the location of loads applied by drum support rollers.
70 A method according to claim 69 comprising the further step of filling said polystyrene mold with a chemical which dissolves said polystyrene enabling release of said mold and said mold insert from said drum.
71 A method according to claim 70 wherein said first and/or second steps applied in the application of said interior layer are repeated at least one more time.
72 A method according to claim 71 wherein said intermediate adhesive layer is sprayed onto said polyurethane elastomer surface after said polyurethane elastomer surface has gelled.
73 A method according to claim 23 comprising the further steps of forming a bed of polyurethane in said recesses which form said helical blades, trowelling said bed to form a groove therein and laying in said bed a continuous glass fibre reinforced elastomer to reinforce said blades along the length said blades.
74 A method according to claim 73 comprising the additional step of inserting a polyurethane insert mold into said recesses such that a space is formed therein having a blade profile.
75 A method according to claim 74 comprising the additional step of setting an external mold at a predetermined spacing from said drum mold and injecting into said external mold polyurethane which fills said space bounded by said insert mold and said spacing between said drum mold and said external mold.
76 A method according to claim 75 wherein said space bounded by said insert mild when filled forms a solid core blade profile.
77 A method according to claim 76 wherein each mould part includes a formation which imparts to the drum an internal archimedian spiral for both mixing and discharge of concrete from the drum.
78 A method according to claim 77 wherein said interior layer of said drum is prepared in two steps, the first of which comprises the application of said polyurethane elastomer bed to the wall of said helical grooves formed in said mold parts and the second of which comprises application of said polyurethane elastomer the remainder of said mold surface by injection molding.
79 A method according to claim 78 wherein said polyurethane is applied using a spray head which traverses a path which generally aligns with said helical recesses as said mandrel rotates thereby applying a uniform distribution of polyurethane along said recesses.
80 A method according to claim 79 wherein said intermediate adhesive layer is sprayed onto said polyurethane elastomer surface after said polyurethane elastomer surface has gelled.
81 A method according to claim 80 comprising the further step of allowing the resin of said composite to cure for a predetermined period.
82 A method according to claim 81 wherein filaments of said fibre reinforced composite are wound about and along said drum at angles of 10 degrees or greater and to a predetermined thickness.
83 A method according to claim 82 comprising the further steps of i) preparing a printed layer on a second mold shell and covering said layer with a gel coat; ii) applying to said gel coat a light layer of fibre reinforced composite; whereupon while said resin of said composite is still liquid said shell is clamped about said drum until excess resin is squeezed from said shell.
84 A method according to claim 83 including the further step of injecting a compound into said mold shell to form a stiffening ring at the location of loads applied by drum support rollers.
85 A method according to claim 84 comprising the further step of filling said polystyrene mold with a chemical which dissolves said polystyrene enabling release of said mold and said mold insert from said drum.
86 A method according to claim 85 wherein said intermediate adhesive layer is sprayed onto said polyurethane elastomer surface after said polyurethane elastomer surface has gelled.
88 A method according to claim 86 wherein layers of said drum are colored as wear indicators.
89 A drum according to claim 2 wherein said layers are colored as wear indicators.
PCT/AU2000/001226 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof WO2001026871A1 (en)
AUPQ333899A0 AUPQ333899A0 (en) 1999-10-08 1999-10-08 Vehicle mounted plastics drum for concrete mixing and method of construction thereof
AUPQ4054 1999-11-15
AUPQ405499A0 AUPQ405499A0 (en) 1999-11-15 1999-11-15 Vehicle mounted plastics drum for concrete mixing and method of construction thereof
HU0204016A HU226314B1 (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
IL14856000A IL148560D0 (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
PL35553000A PL201459B1 (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
AU7891700A AU7891700A (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
AP200202440A AP1586A (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
CA 2382250 CA2382250C (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
MXPA02001940A MXPA02001940A (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof.
KR20027004076A KR20020035888A (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture therof
JP2001529916A JP2003511269A (en) 1999-10-08 2000-10-09 Automotive plastic drum and its method of manufacture concrete mix
US10049605 US6902311B1 (en) 1999-10-08 2000-10-09 Plastics drum for concrete mixing and methods of manufacture thereof
EA200200260A EA003536B1 (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
EP20000969090 EP1226009A4 (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
NZ51742300A NZ517423A (en) 1999-10-08 2000-10-09 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
BR0014121A BR0014121A (en) 1999-10-08 2000-10-09 Plastic barrel for vehicle mounted concrete mixing and methods for their manufacture
IL14856002A IL148560A (en) 1999-10-08 2002-03-07 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof
NO20021633A NO20021633A (en) 1999-10-08 2002-04-05 Kjöretöymontert plastic drum for concrete mix, and methods for producing same
HK03101812A HK1049639A1 (en) 1999-10-08 2003-03-13 Vehicle mounted plastics drum for concrete mixing and methods of manufacture thereof.
US11021538 US7678317B2 (en) 1999-10-08 2004-12-23 Concrete mixing drum manufacturing method
US10049605 Continuation US6902311B1 (en) 1999-10-08 2000-10-09 Plastics drum for concrete mixing and methods of manufacture thereof
WO2001026871A1 true true WO2001026871A1 (en) 2001-04-19
WO2003101694A1 (en) * 2002-05-31 2003-12-11 Anthony Khouri Vehicle mounted concrete mixing drum and method of manufacture thereof
WO2005018898A1 (en) * 2003-08-15 2005-03-03 Mc Neilus Truck And Manufacturing, Inc. Mixing drum blade
WO2005018897A1 (en) * 2003-08-15 2005-03-03 Mc Neilus Truck And Manufacturing, Inc. Mixing drum hatch
ES2255400A1 (en) * 2003-07-25 2006-06-16 Mariagiuseppina Di Filippo Manufacturing method for molds or formworks, involves cutting or milling expanded polystyrene to predetermined sizes, and spraying polystyrene with polyurethane for increased density
FR2985681A1 (en) * 2012-01-17 2013-07-19 Aircelle Sa Method and apparatus for producing a composite part by draping
CN103737722A (en) * 2013-12-26 2014-04-23 中国重汽集团柳州运力专用汽车有限公司 Agitator tank with strong pumping screw blade
GB1537559A (en) * 1976-09-14 1978-12-29 Secr Defence Methods of fabricating filament-reinforced hollow bodies
DE8801881U1 (en) 1988-02-13 1988-06-01 Maschinen- Und Apparatebau August Tepe Gmbh, 2848 Vechta, De
DE4010539C2 (en) * 1990-04-02 2001-08-02 Stetter Gmbh Mixing drum, especially for driving concrete mixer
See also references of EP1226009A4 *
CN1659005B (en) 2002-05-31 2012-03-21 安东尼·扈利 Vehicle mounted concrete mixing drum and method of manufacture thereof
WO2013107963A3 (en) * 2012-01-17 2013-10-31 Aircelle Method and device for manufacturing a composite part by drape forming
US7678317B2 (en) 2010-03-16 grant
US3379591A (en) 1968-04-23 Filament winding of tubular articles with incorporation of cut lengths of roving during winding
US6151743A (en) 2000-11-28 Structural panel for bridging between spaced supports
Ref document number: 2382250
Ref document number: 200201432
Ref document number: 2002/01432
Ref document number: PA/a/2002/001940
Ref document number: 517423
Ref document number: IN/PCT/2002/00261/DE
Ref document number: 2000969090
Ref document number: 148560
Ref document number: 78917/00
Ref document number: 1200200233
2002-03-20 ENP Entry into the national phase in:
Ref document number: 2001 529916
Ref document number: 02025873
Ref document number: 1020027004076
Ref document number: 2002/00921
Ref document number: PV2002-1193
Ref document number: 008140405
Ref document number: 10049605
Ref document number: 11021538
2005-12-19 WWR Wipo information: refused in national office