Matched Legal Cases: ['arts      80', 'arts                20', 'arts   40', 'arts                0', 'arts                0', 'arts    5', 'arts  1', 'arts   10', 'arts                5', 'arts     5', 'arts                4', 'arts        60', 'arts               40', 'arts  60', 'arts               3', 'arts    6', 'arts  15', 'arts               1', 'arts   5', 'arts 1', 'arts               0', 'arts               6', 'arts         80', 'arts                20', 'arts   25', 'arts                6', 'arts                8', 'arts                0', 'arts    5', 'arts  1', 'arts                1', 'arts                5']

Patent US4341675 - Rubber compositions containing ethylene-propylene-diene terpolymers or ... - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inAdvanced Patent SearchPatentsA rubber made from a blend of EPDM or EPR and a polydiorganosiloxane gum has strength, heat resistance, and adhesiveness to room-temperature, moisture-curable silicone rubber. The rubber is made from a blend of EPDM or EPR, polydiorganosiloxane gum, a polyorganosiloxane containing aliphatic hydrocarbon...http://www.google.com/patents/US4341675?utm_source=gb-gplus-sharePatent US4341675 - Rubber compositions containing ethylene-propylene-diene terpolymers or ethylene-propylene copolymers and siliconesAdvanced Patent SearchPublication numberUS4341675 APublication typeGrantApplication numberUS 06/248,161Publication dateJul 27, 1982Filing dateMar 30, 1981Priority dateApr 8, 1980Fee statusPaidAlso published asCA1155588A1, DE3173172D1, EP0040468A2, EP0040468A3, EP0040468B1Publication number06248161, 248161, US 4341675 A, US 4341675A, US-A-4341675, US4341675 A, US4341675AInventorsAkito NakamuraOriginal AssigneeToray Silicone Company, Ltd.Export CitationBiBTeX, EndNote, RefManPatent Citations (4), Referenced by (32), Classifications (20), Legal Events (4) External Links: USPTO, USPTO Assignment, EspacenetRubber compositions containing ethylene-propylene-diene terpolymers or ethylene-propylene copolymers and silicones
US 4341675 AAbstract
A rubber made from a blend of EPDM or EPR and a polydiorganosiloxane gum has strength, heat resistance, and adhesiveness to room-temperature, moisture-curable silicone rubber. The rubber is made from a blend of EPDM or EPR, polydiorganosiloxane gum, a polyorganosiloxane containing aliphatic hydrocarbon radicals of 4 to 20 carbon atoms, a polyoxyalkylene-organosiloxane copolymer or a poly(hydroxyalkyl)organosiloxane, and an organic peroxide.
1. A rubber composition comprising(A) 95 to 5 parts by weight of unvulcanized ethylenepropylene-diene terpolymer or ethylene-propylene copolymer, (B) 5 to 95 parts by weight of a polydiorganosiloxane gum in which the organic radicals are selected from methyl, vinyl, phenyl, and 3,3,3-trifluoropropyl, said organic radicals being at least 50 percent methyl based on the total number of organic radicals, a combination of (A) and (B) being 100 parts by weight, (C) 1 to 30 parts by weight of a polyorganosiloxane based on 100 parts by weight of combined (A) and (B), said polyorganosiloxane having an average unit formula ##EQU2## in which R represents a monovalent radical selected from the group consisting of vinyl, alkyl radicals of 1 to 3 carbon atoms, halogenated alkyl radicals of 1 to 3 carbon atoms, aryl radicals, halogenated aryl radicals, and alkyl radicals of 1 to 3 carbon atoms substituted with an aryl radical, R' represents a monovalent radical selected from the group consisting of aliphatic hydrocarbon radicals having from 4 to 20 carbon atoms and their derivatives in which at least one hydrogen atom is substituted with a chlorine atom or a phenyl radical, a has a value of from 1 to 2.5, b has a value of from 0.01 to 1.2, and the sum of a plus b has a value of from 1.8 to 3, (D) 1 to 30 parts by weight based on 100 parts by weight of combined (A) and (B), of a polymer selected from polyoxyalkylene-organosiloxane copolymers or poly(hydroxyalkyl)organosiloxanes, in which the oxyalkylene contains 2 or 3 carbon atoms, the hydroxyalkyl radicals contain 1 to 8 carbon atoms, the organic radicals are monovalent radicals selected from the group consisting of vinyl, phenyl, phenylethyl, 3,3,3-trifluoropropyl, and alkyl radicals containing 1 to 8 carbon atoms, and at least 50 percent of the organic radicals are alkyl radicals, and (E) 0.1 to 15 parts by weight based on 100 parts by weight of combined (A) and (B), of an organic peroxide. 2. The composition according to claim 1 in which (A) is present in an amount of from 90 to 50 parts by weight, (B) is present in an amount of from 10 to 50 parts by weight, the polydiorganosiloxane gum of (B) has a degree of polymerization of 1,000 to 10,000 and consists essentially of dimethylsiloxane units and methylvinylsiloxane units, (C) is present in an amount of from 1 to 12 parts by weight, the polyorganosiloxane of (C) has a viscosity at 25� C. of from 0.00005 to 0.1 m2 /s, R is methyl, R' is an alkyl radical having from 4 to 20 carbon atoms, (D) is present in an amount of from 2 to 15 parts by weight, and (E) is present in an amount of from 1 to 10 parts by weight.
3. The composition according to claim 2 in which the polymer of (D) is a polyoxyalkylene-organosiloxane copolymer in which the organic radicals are methyl.
4. The composition according to claim 2 in which the polymer of (D) is a poly(hydroxyalkyl)organosiloxane consisting essentially of dimethylsiloxane units and methyl(ω-hydroxyalkyl)siloxane units.
5. The composition according to claim 4 in which the ω-hydroxyalkyl radicals are 3-hydroxypropyl radicals.
6. The composition according to claim 3 in which the organic peroxide is dicumyl peroxide.
7. The composition according to claim 4 in which the organic peroxide is dicumyl peroxide.
8. A method of making a rubber comprising (I) thoroughly blending(A) 95 to 5 parts by weight of unvulcanized ethylene-propylene-diene terpolymer or ethylene-propylene copolymer, (B) 5 to 95 parts by weight of a polydiorganosiloxane gum in which the organic radicals are selected from methyl, vinyl, phenyl, and 3,3,3-trifluoropropyl, said organic radicals being at least 50 percent methyl based on the total number of organic radicals, a combination of (A) and (B) being 100 parts by weight, (C) 1 to 30 parts by weight of a polyorganosiloxane based on 100 parts by weight of combined (A) and (B), said polyorganosiloxane having an average unit formula ##EQU3## in which R represents a monovalent radical selected from the group consisting of vinyl, alkyl radicals of 1 to 3 carbon atoms, halogenated alkyl radicals of 1 to 3 carbon atoms, aryl radicals, halogenated aryl radicals, and alkyl radicals of 1 to 3 carbon atoms substituted with an aryl radical, R' represents a monovalent radical selected from the group consisting of aliphatic hydrocarbon radicals having from 4 to 20 carbon atoms and their derivatives in which at least one hydrogen atom is substituted with a chlorine atom or a phenyl radical, a has a value of from 1 to 2.5, b has a value of from 0.01 to 1.2, and the sum of a plus b has a value of from 1.8 to 3, (D) 1 to 30 parts by weight based on 100 parts by weight of combined (A) and (B), of a polymer selected from polyoxyalkylene-organosiloxane copolymers or a poly(hydroxyalkyl)organosiloxane, in which the oxyalkylene contains 2 or 3 carbon atoms, the hydroxyalkyl radicals contain 1 to 8 carbon atoms, the organic radicals are monovalent radicals selected from the group consisting of vinyl, phenyl, phenylethyl, 3,3,3-trifluoropropyl, and alkyl radicals containing 1 to 8 carbon atoms, and at least 50 percent of the organic radicals are alkyl radicals, and (E) 0.1 to 15 parts by weight based on 100 parts by weight of combined (A) and (B), of an organic peroxide,such that the temperature during the blending process when (E) is present is below the activation temperature of the organic peroxide, (II) heating the product obtained from (I) above the activation temperature of (E) to obtain a rubber. 9. The method in accordance with claim 8 in which (E) is added last.
10. The method in accordance with claim 8 in which the product obtained from (I) is heated at a temperature of from 80� to 200� C. for 3 minutes to 3 hours at a pressure of 20 to 200 kg/cm2.
11. The method in accordance with claim 10 in which the product obtained is further vulcanized by heating at a temperature of from 80� to 200� C. for 1 to 48 hours.
12. A rubber obtained by the method of claim 8.
13. A rubber obtained by the method of claim 10.
14. A rubber obtained by the method of claim 11.
Various attempts have been made to compensate for the insufficient strength of silicone rubber with EPDM or EPR, and at the same time to compensate for the insufficient heat resistance of EPDM or EPR with silicone rubber. Safford, in U.S. Pat. No. 3,227,777, issued Jan. 4, 1966, describes a mixture of a copolymer of ethylene and propylene, an alkenylpolysiloxane, and an organic peroxide which can be vulcanized to a rubbery material. Falender et al., in U.S. Pat. No. 3,865,897, describes a method of making a blend by mechanically mixing certain polyolefins, such as polyethylene, and a polydiorganosiloxane gum containing vinyl or allyl radicals. The mixing method requires shearing at elevated temperatures to form grafting between the two types of polymers. The resulting blend can be crosslinked by a variety of means including organic peroxide. Falender et al. relate to blends of polydiorganosiloxane gum with thermoplastic polyolefins. Walters, in U.S. Pat. No. 3,979,356, issued Sept. 7, 1976, describes an ethylene-vinyl acetate copolymer blended with silicone elastomer and then cured with organic peroxide.
Betts et al., in U.S. Pat. No. 4,123,586, issued Oct. 31, 1978, describes improving the resistance to flame of ethylene-containing polymers, such as ethylene-propylene copolymers, ethylene-propylene diene terpolymers, ethylene-vinyl acetate, ethylene alkyl-acrylate copolymers, and ethylene-butene copolymers. The ethylene-containing polymers are mixed with fillers, pigments, curing coagents, antioxidants, modifying agents, mold release ingredients, processing aids or lubricants such as lead or zinc stearates in amounts of 1 to 5 parts by weight, and essential ingredients, such as decabromodiphenyl ether, silicone gum in amounts of 3 to 10 parts by weight and dibasic lead. Betts et al. show curing with organic peroxide. Betts et al. also show, in an example for 6.25 parts by weight of silicone gum, a tensile strength retention after heating for seven days at 150� C. of 88%, and an elongation retention of 91%.
As shown above, certain compositions are described where unvulcanized EPDM or EPR is compounded with organopolysiloxane gum or unvulcanized silicone rubber and subsequently vulcanizing the mixture with an organic peroxide. The inventor described in U.S. Pat. No. 4,234,702, issued Nov. 18, 1980, filed Mar. 21, 1979, (Belgium Pat. No. 875,702, granted Oct. 19, 1979) adding an organopolysiloxane possessing a C4 -C20 alkyl radical to a compounded rubber system consisting of natural or synthetic organic rubber including unvulcanized EPDM or EPR and an organopolysiloxane gum or unvulcanized silicone rubber, and obtaining a compounded rubber composition which exhibits excellent heat resistance and strength, thus overcoming the drawbacks of both polymers.
This invention relates to a rubber composition comprising (A) 95 to 5 parts by weight of unvulcanized ethylene-propylene-diene terpolymer or ethylene-propylene copolymer, (B) 5 to 95 parts by weight of a polydiorganosiloxane gum in which the organic radicals are selected from methyl, vinyl, phenyl, and 3,3,3-trifluoropropyl, said organic radicals being at least 50 percent methyl based on the total number of organic radicals, a combination of (A) and (B) being 100 parts by weight, (C) 1 to 30 parts by weight of a polyorganosiloxane based on 100 parts by weight of combined (A) and (B), said polyorganosiloxane having an average unit formula ##EQU1## in which R represents a monovalent radical selected from the group consisting of vinyl, alkyl radicals of 1 to 3 carbon atoms, halogenated alkyl radicals of 1 to 3 carbon atoms, aryl radicals, halogenated aryl radicals, and alkyl radicals of 1 to 3 carbon atoms substituted with an aryl radical, R' represents a monovalent radical selected from the group consisting of aliphatic hydrocarbon radicals having from 4 to 20 carbon atoms and their derivatives in which at least one hydrogen atom is substituted with a chlorine atom or a phenyl radical, a has a value of from 1 to 2.5, b has a value of from 0.01 to 1.2, and the sum of a plus b has a value of from 1.8 to 3, (D) 1 to 30 parts by weight based on 100 parts by weight of combined (A) and (B), of a polymer selected from polyoxyalkylene-organo-siloxane copolymers or poly(hydroxyalkyl)organosiloxanes in which the oxyalkylene contains 2 or 3 carbon atoms, the hydroxyalkyl radicals contain 1 to 8 carbon atoms, the organic radicals are monovalent radicals selected from the group consisting of vinyl, phenyl, phenylethyl, 3,3,3-trifluoropropyl, and alkyl radicals containing 1 to 8 carbon atoms, and at least 50 percent of the organic radicals are alkyl radicals and (E) 0.1 to 15 parts by weight based on 100 parts by weight of combined (A) and (B), of an organic peroxide.
The unvulcanized EPDM or EPR, component (A), used in this invention, can be used as received. However, component (A) including various known additives which have been added to natural rubbers and synthetic rubbers, such as reinforcing fillers, extenders, vulcanization auxiliaries, plasticizers, softening agents, pigments, antioxidants, and flame retardants, can also be used. The types and amounts of these additives are appropriately selected according to the types of unvulcanized rubber used. However, the amounts of EPDM, EPR, or polydiorganosiloxane gum referred to herein implies polymer content per se and does not include other additives.
These unvulcanized rubbers can be used singly or as a mixture of two or more types. The amount of component (A) to be added depends upon which one of the characteristics of component (A) and (B) is expected to be strengthened for a specific purpose. However, component (A) is generally used in a proportion of 95 to 5 parts by weight based on 100 parts by weight of a total of components (A) and (B). EPDM and EPR are well known in the art. EPDM is a terpolymer of ethylene, propylene, and at least one diene. The dienes can be illustrated by ethylidene norbornene, dicyclopentadiene, 1,4-hexadiene, cyclooctadiene, and 5-methyl-2-norbornene. EPR is a copolymer of ethylene and propylene.
The polydiorganosiloxane gums, component (B), used in this invention, are primarily straight chain polydiorganosiloxane having a high degree of polymerization and which are generally expressed by the average unit formula ##STR1## where R" represents methyl, vinyl, phenyl or 3,3,3-trifluoropropyl, the proportion of methyl is 50 mol percent or more based on the total organic radicals, and a has a value of from 1.98 to 2.05. Although the degree of polymerization is not critical, the degree of polymerization preferably ranges from 1,000 or a few thousands to about 10,000. Examples of units constituting the polydiorganosiloxane are the following: dimethylsiloxane, methylphenylsiloxane, diphenylsiloxane, methylvinylsiloxane, phenylvinylsiloxane, and methyl-3,3,3-trifluoropropylsiloxane.
The polydiorganosiloxanes can be homopolymers or copolymers of these siloxane units, or a mixture of these polymers. R"SiO1.5 units can be present in a small amount in these structures mentioned above. Examples of end groups of the molecular chain are the following: hydroxy group, alkoxy group, trimethylsilyl group, dimethylvinylsilyl group, dimethylphenylsilyl group and methylphenylvinylsilyl group. However, the end groups are not particularly critical. The preferred polydiorganosiloxanes are those containing dimethylsiloxane units and methylvinylsiloxane units.
The polydiorganosiloxane gum can be directly added to components (A) and (C), or can be mixed in advance with reinforcing fillers such as fumed silica and precipitated silica, or other ordinary additives prior to mixing it with components (A) and (C).
Polyorganosiloxane, component (C), is an essential component which is capable of forming a homogeneous dispersion by improving compatibility between unvulcanized EPDM or EPR and polydiorganosiloxane gum or unvulcanized silicone rubber, which makes unvulcanized EPDM or EPR and a polydiorganosiloxane gum or unvulcanized silicone rubber co-vulcanize with an organic peroxide, and which is also capable of improving heat resistance of vulcanized rubber.
The polyorganosiloxanes are expressed by the previously mentioned average unit formula. In this unit formula, R represents a monovalent radical, such as vinyl; an alkyl radical of 1 to 3 carbon atoms selected methyl, ethyl, and propyl; aryl radicals such as phenyl and naphthyl, alkyl radicals of 1 to 3 carbon atoms substituted with an aryl radical such as benzyl, β-phenylethyl, 2-phenyl-propyl; halogenated alkyl radicals of 1 to 3 carbon atoms such as 3-chloropropyl and 3,3,3-trifluoropropyl; and halogenated aryl radicals, and R' represents monovalent C4 -C20 aliphatic hydrocarbon radicals, such as n-butyl, sec-butyl, t-butyl, n-pentyl, n-hexyl, 3-methyl-pentyl, cyclohexyl, n-heptyl, n-octyl, 2-ethylhexyl, 3,3-dimethylpentyl, n-nonyl, n-decyl, n-dodecyl, stearyl, palmityl, oleyl, and their derivatives in which at least one hydrogen atom in the long chain alkyl group is substituted with a chlorine atom or phenyl radical. In case of the phenyl substituted aliphatic radicals, the carbon atoms in the phenyl radical are not counted for the C4 to C20. In the average unit formula for (C), a has an average value of from 1 to 2.5 and b has an average value of from 0.01 to 1.2, such that a+b has an average value of from 1.8 to 3. R is preferably methyl, vinyl, phenyl, or 3,3,3-trifluoropropyl. In this case, b preferably has a value of from 0.1 to 1.2 in terms of improvement in heat resistance. With respect to the molecular structure, those with a straight chain structure or a cyclic structure are preferred. However, those with a slight branched chain structure or a slight three-dimensional structure are also applicable. The end groups of the molecular chain in those with a straight chain structure and a slight branched chain structure can be hydrogen atoms in addition to R and R' groups. The degree of polymerization of (C) can be from 2 to a degree of polymerization sufficient to make this polymer gum-like. Thus, the upper limit of the degree of polymerization is about 10,000. In terms of efficiency, the viscosity at 25� C. of (C) is preferably 0.1 m2 /s or less.
The amount of component (C) to be added ranges from 1 to 30 parts by weight based on 100 parts by weight of a total of components (A) and (B). Preferably, (C) is a polyorganosiloxane having methyl and alkyl radicals of from 4 to 20 carbon atoms, a viscosity of 25� C. of 0.00005 to 0.1 m2 /s, and is present in an amount of from 1 to 12 parts by weight. If the amount of addition is less than one part by weight, a satisfactory improvement effect on the heat resistance cannot be obtained. On the other hand, if the amount of (C) exceeds 30 parts by weight, the effects on the processability and physical properties of the obtained rubber increase undesirably.
Typical examples are those with the following general formulas: ##STR2## where R4 represents monovalent hydrocarbon radicals or halogenated monovalent hydrocarbon radicals, such as methyl, ethyl, octyl, vinyl, phenyl, phenylethyl and 3,3,3-trifluoropropyl; A represents oxyalkylene groups such as ##STR3## where k and l are integers of 1 or greater, R'" represents a hydrogen atom, or terminal end groups such as alkyl radicals such as methyl, ethyl, propyl, and butyl, and acyl radicals such as acetyl, propionyl, butyryl, and valeryl, m is 0 or integers of 1 or greater, n is integers of 1 or greater, x and y are integers of one or greater such that x+y is from 4 to 8.
Typical examples are those with the following general formulas ##STR4## where R4, m, n, x and y are the same as those described previously, and B represents a hydroxyalkyl group, such as 3-hydroxypropyl.
Of course, the applicable examples are not limited by those listed above. However, those which are available in the liquid form at room temperature are preferred and the viscosity at 25� C. is preferably 0.00001 to 0.1 m2 /s.
The amount of component (D) to be added ranges from 1 to 30 parts by weight based on 100 parts by weight of a total of components (A) and (B). Preferably, (D) is polyoxyalkylene-organosiloxane copolymer in which the organic groups other than the polyoxyalkylene groups are methyl or a poly(hydroxyalkyl)organo containing dimethylsiloxane units and methyl(ω-hydroxyalkyl)siloxane units. (D) is preferably present in an amount of 2 to 15 parts by weight. If the amount of addition is less than one part by weight, the adhesion effect cannot be achieved. On the other hand, if it exceeds 30 parts by weight, the effects on processability and physical properties of the obtained rubber increase undesirably.
Organic peroxides, component (E), used in this invention can be selected from those which are commonly used for the vulcanization of unvulcanized natural rubbers and synthetic rubbers. Examples include the following: benzoyl peroxide, 2,4-dichlorobenzoyl peroxide, di-tert-butyl peroxide, tert-butyl perbenzoate, dicumyl peroxide, 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane, 2,5-dimethylhexane-dialkyl peroxide, ketal peroxide and 1,1-di(tert-butylperoxy)-3,3,5-trimethylcyclohexane.
The compositions of this invention are obtained by homogeneous blending of five components (A), (B), (C), (D) and (E). As was explained in the description of component (A), the following additives which are commonly added to EPDM and EPR are optional: reinforcing fillers and extending fillers, e.g., fumed silica, precipitated silica, fine quartz powder, diatomaceous earth, carbon black, zinc oxide, basic magnesium carbonate, activated calcium carbonate, magnesium silicate, aluminum silicate, titanium dioxide, talc, mica powder, aluminum sulfate, calcium sulfate, barium sulfate, asbestos, glass fibers, organic reinforcing agents and organic fillers; vulcanization auxiliaries, e.g., metal oxides, amines, fatty acids and their derivatives; plasticizers, e.g., polydimethylsiloxane oil, phthalic acid derivatives, and adipic acid derivatives; softening agents, e.g., lubricating oils, process oil, coal tar, castor oil, beeswax, ricinoleic acid and calcium stearate; antioxidants, e.g., phenylenediamines, phosphates, quinolines, cresols, phenols and dithiocarbamate metal salts. In addition, coloring agents, UV-ray absorbants, heat resistance-imparting agents, flame retarders, foaming agents, scorching inhibitors, viscosity-imparting agents and smoothing agents.
As was explained in the description of component (B), the following additives which are commonly used with silicone rubber are optional: reinforcing fillers and extending fillers, e.g., fumed silica, precipitated silica, fine quartz powder, diatomaceous earth, carbon black, zinc oxide, basic magnesium carbonate, activated calcium carbonate, magnesium silicate, aluminum silicate, titanium dioxide, talc, mica powder, calcium sulfate, barium sulfate, asbestos and glass fibers; inactivators for the reinforcing fillers, e.g., alkoxy endblocked low molecular polydimethylsiloxane, diphenylsilanediol and trimethylsilanol; heat resistance improving agents, e.g., iron oxide, cerium oxide, iron naphthoate, and cerium naphthoate; flame retarders, oil resistance improving agents, foaming agents and adhesiveness improving agents.
The rubber compositions of this invention are produced by a variety of blending methods. For example, component (A) is thoroughly blended and softened in a Banbury mixer, kneader mixer, or two-roll mixer. Subsequently, components (B), (C), and (D) are simultaneously blended in component (A); or component (B) is added and blended at first and then components (C) and (D) are added and blended; or conversely components (C) and (D) are added and blended at first and then component (B) is added and blended. Finally, component (E) is added and blended in the mixture mentioned above. Alternatively, component (A) is softened in the same way as mentioned above and then components (B), (C), (D), and (E) are simultaneously added and blended in component (A). Alternatively, components (A), (B), (C), and (D) are homogeneously blended in the above-mentioned mixers or roll mixer, and then component (E) is added and blended in the mixture obtained. Alternatively, all components (A), (B), (C), (D), and (E) are placed in the above-mentioned mixers or roll mixer, and then simultaneously blended. Alternatively, the whole amount or portion of the additives such as fillers, plasticizers, softening agents, antioxidants, vulcanizing agents, and vulcanization accelerators are compounded in advance with component (A), and then the other four components are added and blended. Alternatively, a mixture which is prepared by compounding in component (A), the whole amount or a portion of the additives such as fillers, plasticizers, softening agents, antioxidants, vulcanizing agents, and vulcanization accelerators; component (B) in which the additives such as reinforcing fillers, fumed silica or wet silica, heat resistance improving agents have been compounded in advance, is added; then components (C) and (D) are added in the above-mentioned mixers or roll mixer; finally component (E) is added and blended in the mixture obtained.
However, methods of addition, order of addition, methods of blending conditions for blending, and blending instruments are not critical. When component (E) is present, the mixture must be blended below the temperature at which component (E) is activated. Each organic peroxide has an activation temperature at which it causes the composition to vulcanize, thus the temperature at which the components are blended with organic peroxide must be below the activation temperature of the organic peroxide to avoid premature vulcanization.
The rubber compositions are vulcanized by heating above the activation temperature of the organic peroxide until a rubber is obtained. The rubber compositions are preferably vulcanized at 80�-200� C. from 3 minutes to 3 hours under elevated pressure 20-200 kg/cm2 and, if desirable, further vulcanized at 80�-200� C. from 1 to 48 hours to produce rubber products.
On a two-roll mixer, 80 parts of ethylene-propylene-diene terpolymer (EPT 3045, sold by Mitsui Petrochemical Co., Ltd., Tokyo, Japan) was thoroughly blended, and then 40 parts of precipitated silica (Nipsyl NV-3, sold by Nippon Silica K.K., Tokyo, Japan) was added and blended to make a base compound. This base compound was blended with the following ingredients: 20 parts of hydroxyl endblocked polydiorganosiloxane gum having 99.432 mol percent dimethylsiloxane units and 0.568 mol percent methylvinylsiloxane units, and a degree of polymerization of about 5,000, 5 parts of α,ω-bis(trimethylsilyl)methyl n-octylpolysiloxane having a viscosity at 25� C. of 0.0009 m2 /s and n-octyl radical content of 50 mol percent based on the total number of organic radicals, 5 parts of polyoxyethylene/methylpolysiloxane copolymer with the formula ##STR5## having a viscosity at 25� C. of 0.0005 m2 /s, 10 parts of a process oil which is a copolymer of n-butene and i-butene having a viscosity at 25� C. of 20 Pa.s (sold by Nippon Oil and Fats Co., Ltd., Tokyo, Japan), 0.8 part of antioxidant, 5 parts of zinc oxide, 1 part of stearic acid, and 4.5 parts of dicumyl peroxide. The mixture was blended homogeneously in the two-roll mixer and then pressed into sheets with a thickness of 2 mm and vulcanized at a temperature of 170� C. under a pressure of 200 kg/cm2 for 20 minutes. The sheets obtained were further heat treated in a hot air circulating type oven at 150� C. for 2 hours. The tensile strength and the elongation at break were measured according to JIS-K-6301 (equivalent to ASTM D 412 for tensile strength and elongation). Separately, a room-temperature-moisture curable type silicone rubber (SH 780, sold by Toray Silicone Co., Ltd., Tokyo, Japan) was coated over the heat treated rubber sheet obtained above and the layer was allowed to stand in the atmosphere at 25� C. for 7 days. According to JIS-A-5755 (equivalent to Military Specification MIS-S-7502), the peeling adhesive strength was tested. As a comparative example, a rubber composition was prepared without adding the polyoxyethylene/methylpolysiloxane copolymer and a rubber sheet was formed under the same conditions as mentioned above. Tests were conducted in the same manner. The results are presented in Table I.
TABLE I______________________________________              This   Comparative              Invention                     Example______________________________________EPT 3045, parts      80       80Polydiorganosiloxane gum, parts                20       20Nipsyl VN 3, parts   40       40Antioxidant RD*, parts                0.5      0.5Antioxidant NS-7**, parts                0.3      0.3Zinc oxide, parts    5        5Stearic Acid, parts  1        1Process oil, parts   10       10&#945;,&#969;-bis(trimethylsilyl) methyln-octylpolysiloxane, parts                5        5Polyoxyethylene/methylpolysiloxanecopolymer, parts     5        --Dicumyl peroxide, parts                4.5      4.5Tensile strength (kg/cm2)                96       101Elongation (%)       550      500Peeling adhesive strength (kg/25 mm)                8.9      1.2______________________________________ *Antioxidant RD is polymerized, 2,2,4trimethyl-1,2-hydroquinoline sold by Kawagucki Kagoku K.K., Tokyo, Japan. **Antioxidant NS7 is 2,5di-t-butyl hydroquinone sold by Ohuchi Shinko K.K., Tokyo, Japan.
On a two-roll mixer, 60 parts of ethylenepropylene-diene terpolymer (EP-43 sold by Nippon Gosei Gomu K.K., Tokyo, Japan) was thoroughly blended, and then 40 parts of Nipsyl VN 3 was added and blended thoroughly to produce a base compound. This base compound was blended with the following ingredients: 40 parts of a trimethylsilyl endblocked polydiorganosiloxane gum having 99.858 mol percent dimethylsiloxane units and 0.142 mol percent methylvinylsiloxane units and a degree of polymerization of about 7000, 3 parts of α,ω-bis(trimethylsilyl) methyl n-octylpolysiloxane having a viscosity at 25� C. of 0.0013 m2 /s and n-octyl radical content of 50 mol percent based on the total number of organic radicals, 6 parts of polyoxypropylene/methylpolysiloxane copolymer with the formula ##STR6## having a viscosity at 25� C. of 0.0008 m2 /s, 15 parts of the process oil as described in Example 1, 1 part of antioxidant, 5 parts of zinc oxide, 1 part of stearic acid, 0.5 part of triallylisocyanurate as a vulcanization accelerator, and 6 parts of dicumyl peroxide. The mixture was blended homogeneously on the two-roll mixer. Subsequently, a rubber sheet was vulcanized under the same conditions as in Example 1. The same physical properties were measured according to JIS-K-6301. In addition, the peeling adhesive strength of a laminate of the rubber sheet on which SH 780 was coated, was tested according to JIS-A-5755. Separately, the rubber sheet obtained after the vulcanization was allowed to stand in a hot air circulating type oven at 150� C. for 168 hours and the changes on the surface of the rubber sheet were macroscopically examined. In addition, the tensile strength and the elongation were measured and expressed as residual ratios based on the initial physical values. The results are presented in Table II.
As a comparison, a rubber composition was prepared using 6 parts of polyoxypropylene having a viscosity of 0.0005 m2 /s instead of the polyoxypropylene/methylpolysiloxane copolymer and the same tests were conducted. The results are also present in Table II.
TABLE II______________________________________             This   Comparative             Invention                    Example______________________________________EP-43, parts        60       60Polydiorganosiloxane gum, parts               40       40Nipsyl VN 3, parts  60       60&#945;,&#969;-bis(trimethylsilyl)methyln-octyl polysiloxane, parts               3        3Polyoxypropylene/methylpolysiloxanecopolymer, parts    6        --Polyoxypropylene, parts               --       6Process oil, parts  15       15Antioxidant MB***, parts               1        1Zinc oxide, parts   5        5Stearic acid, parts 1        1Vulcanization accelerator, parts               0.5      0.5Dicumyl peroxide, parts               6        6Initial physical propertiesTensile strength (kg/cm2)               81       89Elongation (%)      430      510Peeling adhesive strength (kg/25mm)               11.3     3.5After heating at 150� C. for 168 hoursAppearance          Glossy   Slight                        Disappearance                        of glossResidual tensile strength (%)               100      86Residual elongation (%)               97       75______________________________________ ***Antioxidant MB is 2mercapto benzimidazole sold by Kawaguchi Kagaku K.K., Tokyo, Japan.
On a two-roll mixer, 80 parts of ethylenepropylene copolymer (EP-11 sold by Nippon Gosei Gomu K.K., Tokyo, Japan) was thoroughly blended, and then 25 parts of Nipsyl VN-3 was added and blended to make a base compound. This base compound was blended with the following ingredients: 20 parts of trimethylsilyl endblocked polydiorganosiloxane containing dimethylsiloxane units and methylvinylsiloxane units having a degree of polymerization of about 5000, 6 parts of α,ω-bis(trimethylsilyl) methyl n-dodecylpolysiloxane having a viscosity at 25� C. of 0.0006 m2 /s and n-dodecyl radical content of 50 mol percent based on the total number of organic radicals, 8 parts of α,ω-bis(trimethylsilyl)methyl(3-hydroxypropyl)polysiloxane having a viscosity at 25� C. of 0.0003 m2 /s, having dimethylsiloxane units and methyl-(3-hydroxypropyl)siloxane units where the polysiloxane has a 3-hydroxylpropyl radical content of 5.5 mol percent based on the total numbers of organic radicals, 0.7 part of antioxidant, 5 parts of zinc oxide, 1 part of stearic acid, 1 part of triallylisocyanurate as vulcanization accelerator, and 5 parts of dicumyl peroxide. The mixture was homogeneously blended in the two-roll mixer and a rubber sheet was formed under the same conditions as in Example 1. The strength and the elongation were measured under the same conditions as in Example 1. The adhesive strength with a room-temperature moisture curable type silicone rubber was measured under the same conditions as in Example 1. As a comparative example, a rubber composition was prepared without adding α,ω-bis-(trimethylsilyl)methyl-(3-hydroxy-propyl)polysiloxane and a rubber sheet was formed under the same conditions mentioned above. The characteristics were measured by the same tests. The results obtained are presented in Table III.
TABLE III______________________________________                     Compara-              This   tive              Invention                     Example______________________________________EP-11, parts         80       80Polydiorgansiloxane gum, parts                20       20Nipsyl VN 3, parts   25       25&#945;, &#969;-bis(trimethylsilyl)methyl n-dodecylpolysiloxane, parts                6        6&#945;, &#969;-bis(trimethylsilyl)methyl-(3-hydroxypropyl) polysiloxane, parts                8        --Antioxidant BHT****, parts                0.7      0.7Zinc oxide, parts    5        5Stearic acid, parts  1        1Vulcanization accelerator TAIC, parts                1        1Dicumyl peroxide, parts                5        5Tensile strength (kg/cm2)                83       98Elongation (%)       650      580Peeling strength (kg/25mm)                9.3      2.1______________________________________ ****Antioxidant BHT is 2,6di-t-butyl-p-cresol.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3497570 *Aug 19, 1966Feb 24, 1970Dow CorningStabilized silicone elastomersUS3870766 *Sep 4, 1973Mar 11, 1975Stauffer Chemical CoMethod of curing organic polymers and copolymersUS4230826 *Apr 25, 1979Oct 28, 1980Wacker-Chemie GmbhOrganopolysiloxane compositions and elastomers formed therefromUS4234702 *Mar 21, 1979Nov 18, 1980Toray Silicone Company, LtdSilicone rubber compositions* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS4517332 *May 12, 1983May 14, 1985Japan Synthetic Rubber Co., Ltd.Rubber composition containing a silicone raw rubberUS4668728 *Nov 15, 1985May 26, 1987The Goodyear Tire & Rubber CompanyCoating material for use on sulfur vulcanized rubberUS4670496 *May 19, 1986Jun 2, 1987The Goodyear Tire & Rubber CompanyCoating material for use on sulfur vulcanized rubberUS4689362 *Jul 2, 1986Aug 25, 1987Ciba-Geigy CorporationStabilized olefin polymer insulating compositionsUS4710541 *Oct 22, 1985Dec 1, 1987Bridgestone CorporationProcess for molding and vulcanizing rubber productsUS4722379 *May 27, 1986Feb 2, 1988The Goodyear Tire & Rubber CompanyCoating material for use on sulfur vulcanized rubberUS4722380 *May 27, 1986Feb 2, 1988The Goodyear Tire & Rubber CompanyCoating material for use on sulfur vulcanized rubberUS4761452 *Jul 9, 1986Aug 2, 1988Shin-Etsu Chemical Co., Ltd.Oil-resistant rubber compositionUS4931492 *Mar 17, 1989Jun 5, 1990Union Carbide Chemicals And Plastics Company Inc.Olefin polymer compositions containing polyorganosiloxanes and the use thereof in the production of film material and polyorganosiloxanesUS4977200 *Mar 30, 1989Dec 11, 1990Shin-Etsu Chemical Co., Ltd.Ethylene-propylene organopolysiloxane rubber compositionUS4978714 *Mar 1, 1989Dec 18, 1990The West Company IncorporatedModified halobutyl thermoplastic elastomerUS5091453 *Apr 10, 1990Feb 25, 1992Bp Chemicals LimitedFlame retardant polymer compositionUS5264490 *Oct 16, 1991Nov 23, 1993Nippon Oil Co., Ltd.Particulate polybutadiene crosslinked materialUS5482988 *Jan 14, 1994Jan 9, 1996Dow Corning CorporationHot-melt silicone pressure sensitive adhesive with siloxylated polyether waxes as additivesUS5607721 *May 15, 1995Mar 4, 1997Dow Corning CorporationHot-melt silicone pressure sensitive adhesive with siloxylated polyether waxes as additivesUS5658975 *May 15, 1995Aug 19, 1997Dow Corning CorporationHot-melt silicone pressure sensitive adhesive with siloxylated polyether waxes as additivesUS5719249 *Jun 27, 1996Feb 17, 1998Kanegafuchi Kagaku Kogyo Kabushiki KaishaReactive silicon group-containing polyoxyalkylene-polysiloxane copolymerUS5747567 *Jan 15, 1993May 5, 1998General Elecric CompanySilicone adhesive and organic adhesive compositesUS5880245 *Nov 13, 1997Mar 9, 1999Kanegafuchi Kagaku Kogyo Kabushiki KaishaProcess for the preparation of novel reactive silicon group-containing polymerUS5985970 *Jul 31, 1996Nov 16, 1999Uniroyal Chemical Company, Inc.EPDM rubber compositionUS6207769Jun 30, 1999Mar 27, 2001Dow Corning GmbhPolymer compositionUS6761976Jan 11, 2002Jul 13, 2004NexansTear-resistant composition based on silicone rubber for cables and for power accessoriesUS7955418Sep 11, 2006Jun 7, 2011Abela Pharmaceuticals, Inc.Systems for removing dimethyl sulfoxide (DMSO) or related compounds or odors associated with sameUS8298320May 2, 2011Oct 30, 2012Abela Pharmaceuticals, Inc.Systems for removing dimethyl sulfoxide (DMSO) or related compounds, or odors associated with sameUS8435224Sep 11, 2006May 7, 2013Abela Pharmaceuticals, Inc.Materials for facilitating administration of dimethyl sulfoxide (DMSO) and related compoundsUS8440001Oct 24, 2012May 14, 2013Abela Pharmaceuticals, Inc.Systems for removing dimethyl sulfoxide (DMSO) or related compounds, or odors associated with sameUS8440174Sep 30, 2011May 14, 2013The Procter & Gamble CompanyCompositions comprising surfactants and alkyloxy-modified siliconeUS8480797May 2, 2011Jul 9, 2013Abela Pharmaceuticals, Inc.Activated carbon systems for facilitating use of dimethyl sulfoxide (DMSO) by removal of same, related compounds, or associated odorsUS8586015Apr 1, 2011Nov 19, 2013The Procter & Gamble CompanyCompositions comprising surfactants and glycerol-modified siliconesUS8673061May 2, 2011Mar 18, 2014Abela Pharmaceuticals, Inc.Methods for facilitating use of dimethyl sulfoxide (DMSO) by removal of same, related compounds, or associated odorsUS8940284Apr 1, 2011Jan 27, 2015The Procter & Gamble CompanyOrganosiliconesEP1223193A1 *Jan 10, 2002Jul 17, 2002NexansTear resistant silicone rubber compostion for cables and energy products* Cited by examinerClassifications U.S. Classification524/266, 524/263, 524/506, 525/105, 525/100, 525/101, 525/102, 524/264International ClassificationC08L23/00, C08L21/00, C08L7/00, C08L83/00, C08K5/14, C08L23/16, C08L83/04, C08L101/00, C08L87/00Cooperative ClassificationC08L23/16, C08L2312/00European ClassificationC08L23/16Legal EventsDateCodeEventDescriptionDec 6, 1993FPAYFee paymentYear of fee payment: 12Dec 4, 1989FPAYFee paymentYear of fee payment: 8Nov 29, 1985FPAYFee paymentYear of fee payment: 4Mar 15, 1982ASAssignmentOwner name: TORAY SILICONE COMPANY, LTD., 2-8 MUROMACHI NIHONBFree format text: ASSIGNMENT OF ASSIGNORS INTEREST.;ASSIGNOR:NAKAMURA, AKITO;REEL/FRAME:003956/0053Effective date: 19810706RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services