Brevet US6042700 - Adjustment of deposition uniformity in an inductively coupled plasma source - Google�BrevetsRecherche Images Maps Play YouTube Actualit�s Gmail Drive Plus » Recherche avanc�e dans les brevets | Historique Web | Connexion Recherche avanc�e dans les brevets BrevetsA plasma chamber in a semiconductor fabrication system uses a two step process to sputter deposit material onto a substrate. The first step provides a power ratio of RF power to DC power optimized to increase uniformity of deposition of material onto a workpiece from a first target. A second step involves...http://www.google.fr/patents/US6042700?utm_source=gb-gplus-shareBrevet US6042700 - Adjustment of deposition uniformity in an inductively coupled plasma source Num�ro de publicationUS6042700 AType de publicationOctroi Num�ro de demande08/929,829 Date de publication28 mars 2000 Date de d�p�t15 sept. 1997 Date de priorit�15 sept. 1997Autre r�f�rence de publicationEP1018139A1WO1999014792A1 InventeursPraburam GopalrajaMurali Narasimhan Cessionnaire d'origineApplied Materials, Inc. Classification aux �tats-Unis204/192.15204/192.3204/192.12 Classification internationaleC23C14/35C23C14/04H01L21/285H01L21/203H01J37/34H01J37/32C23C14/34 Classification coop�rativeC23C14/345H01J37/34C23C14/358H01J37/321C23C14/046C23C14/35 Classification europ�enneH01J 37/32M8DC23C 14/34C4C23C 14/35F6H01J 37/34C23C 14/35C23C 14/04DR�f�rencesCitations de brevets (97)Citations hors brevets (56) R�f�renc� par (31)Liens externesUSPTO Cession USPTO EspacenetAdjustment of deposition uniformity in an inductively coupled plasma sourceUS 6042700 A R�sum� A plasma chamber in a semiconductor fabrication system uses a two step process to sputter deposit material onto a substrate. The first step provides a power ratio of RF power to DC power optimized to increase uniformity of deposition of material onto a workpiece from a first target. A second step involves applying little to no DC power to the target, while an RF power is coupled into a plasma generation region to sputter material from a second target onto the workpiece. It has been found that material from the second target provides greater sidewall coverage of channels located on the workpiece, as well as increasing the uniformity of the deposit on the surface of the workpiece.
What is claimed is: 1. A method of sputter depositing material onto a workpiece in a sputter reactor, comprising: in a first interval, spultering material primarily from a first, disk-shaped target, thereby depositing sputtered material from said first target onto said workpiece; and in a second interval, sputtering material primarily from a second, ring-shaped target which is a coil coupling RF energy, thereby depositing sputtered material from said second target onto said workpiece.
2. A method of sputter depositing material onto a workpiece, comprising: in a first interval, sputtering material primarily from a first target in a plasma energized by RF energy radiated by a coil, thereby depositing sputtered material from said first target onto said workpiece; and in a second interval, sputtering material primarily from said coil, thereby depositing sputtered material from said coil onto said workpiece.
3. The method of claim 2 wherein, in said first interval, said first target is DC biased by a DC power supply.
4. The method of claim 2 wherein said second interval occurs after said first interval.
5. The method of claim 2 wherein said first interval occurs after said second interval.
6. The method of claim 2 further comprising, in a third interval preceding said first and second intervals, etching said workpiece by biasing said workpiece and applying RF energy to said coil to produce ions to strike the surface of said workpiece to clean contacts located on said workpiece.
7. The method of claim 2 wherein said coil includes a coil material, and said target includes a target material, wherein said target material and said coil material are the same type of material.
8. The apparatus of claim 2 wherein said target includes titanium, and wherein said coil includes titanium.
9. The apparatus of claim 2 wherein said target includes aluminum, and wherein said coil includes aluminum.
10. The apparatus of claim 2 wherein said target includes copper, and wherein said coil includes copper.
11. A method of sputter depositing material onto a workpiece, the method comprising: in a first interval, biasing a target arranged about a chamber axis and positioned above said workpiece to attract ions to sputter material from said target and applying RF energy to a coil to energize a plasma of said ions; in a second interval, terminating said biasing of said target while applying RF energy to said coil; and in a third interval preceding said first and second intervals, etching said workpiece by biasing said workpiece and applying RF energy to said coil to produce ions to strike the surface of said workpiece to clean contacts located on said workpiece.
12. The method of claim 11 wherein, in said first interval, said first target is DC biased by a DC power supply.
13. The method of claim 11 wherein said coil includes a coil material and said target includes a target material, wherein said target material and said coil material are the same type of material.
14. A method of depositing sputtered material onto a workpiece within a semiconductor fabrication system having a target powered by a first power source and a coil powered by a second power source, the method comprising: a first step of depositing sputtered material from both said coil and said target onto said workpiece in a first interval in which material is sputtered primarily from said target; and a second step of depositing sputtered material from said coil onto said workpiece in a second interval in which material is sputtered primarily from said coil.
15. The method of claim 14 wherein said second interval occurs after said first interval.
16. The method of claim 14 wherein said first interval occurs after said second interval.
17. The method of claim 14 further comprising, prior to said first and second steps, applying RF energy from said second power source to said coil, thereby etching said workpiece to clean contacts located on said workpiece.
18. A method practiced in a DC plasma sputtering chamber of sputtering a material from a target onto a wokpiece supported on a pedestal, an induction coil comprising said material being wrapped within the chamber around a plasma generation region, said method comprising a first step and a second step being alternately performed while said workpiece is disposed in said chamber; wherein said first step comprises applying a first DC level of DC power to said target and a first RF level of RF power to said coil; wherein said second step comprises applying a second DC level of DC power less than said first DC level to said target and a second RF level of RF power to said coil; and whereby said first step preferentially deposits said material at a center of said workpiece and said second step preferentially deposits said material at a periphery of said workpiece.
19. The method of claim 18, wherein said second DC level is approximately zero.
20. The method of claim 19, wherein said first and second RF levels are substantially equal.
21. The method of claim 20, further comprising electrically biasing said pedestal negative string said first and second steps.
BACKGROUND OF THE INVENTION Plasmas have become convenient sources of energetic ions and activated atoms which can be employed in a variety of semiconductor device fabrication processes including surface treatments, depositions, and etching processes. For example, to deposit materials onto a semiconductor wafer using a sputter deposition process, a plasma is produced in the vicinity of a sputter target material which is negatively biased. Ions created adjacent to the target impact the surface of the target to dislodge, i.e., "putter" material from the target. The sputtered materials are then transported and deposited on the surface of the semiconductor wafer.
Sputtered material has a tendency to travel in straight line paths from the target to the substrate being deposited, at angles which are oblique to the surface of the substrate. As a consequence, materials deposited in etched trenches and holes of semiconductor devices having trenches or holes with a high depth to width aspect ratio, can bridge over causing undesirable cavities in the deposition layer. To prevent such cavities, the sputtered material can be redirected into substantially vertical paths between the target and the substrate by negatively charging the substrate to position vertically oriented electric fields adjacent the substrate if the sputtered material is sufficiently ionized by the plasma. However, material sputtered in a low density plasma often has an ionization degree of less than 10% which is usually insufficient to avoid the formation of an excessive number of cavities. Accordingly, it is desirable to increase the density of the plasma to increase the ionization rate of the sputtered material in order to decrease the formation of unwanted cavities in the deposition layer. As used herein, the term "dense plasma" is intended to refer to one that has a high electron and ion density.
A high density plasma typically requires the chamber to be operated at a relatively high pressure. As a result, the frequency of collisions between the plasma ions and the deposition material atoms is increased and the scattering of the deposition atoms is likewise increased. This scattering of the deposition atoms typically causes the thickness of the deposition layer on the substrate to be thicker on that portion of the substrate aligned with the center of the target and thinner in the outlying regions. Such nonuniformity of deposition is often undesirable in the fabrication of semiconductor devices.
SUMMARY OF THE PREFERRED EMBODIMENTS It is an object of the present invention to provide an improved method and apparatus for generating a plasma within a chamber and for sputter-depositing a layer which obviate, for practical purposes, the above-mentioned limitations.
These and other objects and advantages are achieved by, in accordance with one aspect of the invention, a sputtering apparatus which deposits ionized sputtered deposition material in two different intervals distinguished by the amount of material sputtered from a primary target as compared to material sputtered from a secondary target disposed around the substrate. In the illustrated embodiment, in a first interval, RF power is applied to a coil inductively coupled into a high density plasma and DC power is applied to a planar sputtering target. In this first interval, a substantial amount of material is sputtered from both the planar target and the coil (the secondary target) although material is sputtered primarily from the planar target (the primary target). It has been found that uniformity may be further improved by, in a second interval, reducing or eliminating the DC power supplied to the planar target while a level of RF power is still applied to the coil. Under these conditions, material is sputtered primarily from the coil rather than target. Because the coil may be positioned closer to the workpiece periphery, the relative thickness of deposition material deposited toward the periphery of the workpiece may be increased further relative to the deposition in the center of the workpiece. As a consequence, the tendency of the target to deposit material more thickly in the center of the workpiece may be offset by sputtering primarily from the coil in the second interval. Still further, improved sidewall coverage of channels located on the workpiece surface may be achieved in the second interval because the material sputtered from the coil tends to have a greater horizontal velocity component than the material sputtered from the target.
BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a perspective, partial cross-sectional view of a plasma generating chamber used in accordance with an embodiment of the present invention.
FIG. 2 is a schematic cross-sectional diagram of the plasma generating chamber of FIG. 1.
FIG. 3 is a table illustrating examples of various intervals of a process of operating a plasma generating chamber in accordance with an embodiment of the present invention.
FIG. 4 is a schematic diagram of the electrical interconnections to the plasma generating chamber of FIGS. 1-2.
FIG. 5a is a chart depicting the respective deposition profiles for material deposited from the target and coil of the plasma generating chamber of FIGS. 1-2 due to the RF power applied to the coil and the DC power bias of the target during the center thick step.
FIG. 5b is a chart depicting the final deposition profile of the material deposited by the plasma generating chamber of FIGS. 1-2 after all the steps and the respective deposition profiles for material deposited from the target and coil generated during the edge thick step and the center thick step.
FIGS. 6a-6c are cross-sectional views of a channel of the workpiece as sputtered material is deposited during various intervals.
DETAILED DESCRIPTION OF THE EMBODIMENTS Referring first to FIGS. 1-2, a plasma generator used in accordance with an embodiment of the present invention comprises a substantially cylindrical plasma chamber 100 which is received in a vacuum chamber (not shown). The plasma chamber 100 of this embodiment has a single turn coil 104 which is carried internally of the vacuum chamber walls by a chamber shield 106. The chamber shield 106 protects the interior walls of the vacuum chamber from the material being deposited within the interior of the plasma chamber 100.
Additionally, housed inside the plasma chamber 100 is a pedestal 114 located adjacent the floor of the plasma chamber 100 and capable of supporting a substrate 112. Located above the substrate 112 adjacent the ceiling of the plasma chamber 100 is a target 110. Electrical connections, which will be described in greater detail below in connection with FIG. 4, apply DC power to the target 110 and an AC or RF power to the coil 104 and RF induced bias to the substrate 112.
In a preferred embodiment, the plasma generator sputter deposits material from a target 110 onto a substrate 112 in two steps. In the first step, the deposition profile tends to be thicker in the center of the substrate 112 and therefore is referred to herein as a "center thick step." Conversely, in the second step referred to herein as an "edge thick step," the deposition profile tends to be thicker toward the periphery of the substrate 112 so as to compensate for the center thick tendency of the "center thick step." As discussed below, the order of the two steps are interchangeable, and furthermore, the two steps can be preceded by an optional third step referred to herein as an "etch step."
In the center thick step, DC power is applied to bias the target 110. Thereby, an ion flux 108 (FIG. 2), created by a rotating magnetron assembly 116, is attracted by the negatively biased target 110 to strike the surface of the target 110. The ion flux 108 is able to eject material from the target 110 onto a substrate 112 which may be a wafer or other workpiece supported by the pedestal 114 at the bottom of the plasma chamber 100. The magnetron assembly 116 (shown schematically in FIG. 2) produces magnetic fields which are swept over the face of the target 110 to promote uniform erosion by sputtering of the target 110.
Additionally, in the center thick step, radio frequency (RF) energy is radiated from the coil 104 into the interior of the plasma chamber 100, which energizes a plasma 118 (FIG. 2) within the plasma chamber 100. Deposition material sputtered from the target 110 is ionized by the plasma 118 so that the ionized material may be attracted to the substrate 112 by electric fields in the vicinity of the substrate 112. These electric fields are oriented so as to direct the ionized deposition material in directions generally orthogonal to the surface of the substrate 112 to improve the step coverage of vias, channels and other high aspect ratio structures.
In order to accommodate the coil 104 to facilitate ionization of the plasma, it has been found beneficial to space the target 110 from the surface of the workpiece 112. However, this increased spacing between the target and the workpiece can adversely impact the uniformity of the material being deposited from the target. Such nonuniformity typically exhibits itself as a thickening of the deposited material toward the center of the workpiece with a consequent thinning of the deposited material toward the edges of the workpiece as represented by deposition profile 250 in FIG. 5a.
As set forth in copending application Ser. No. 08/680,335, filed Jul. 10, 1996, now abandoned, (Atty. Docket 1390CIP/PVD/DV) incorporated herein by reference in its entirety, this nonuniformity may be compensated by sputtering deposition material not only from the sputter target 110 above the workpiece but also from a coil or other secondary target encircling the edges of the workpiece. Here, because the edges of the workpiece are closer to the coil 104 than is the center of the workpiece, any material sputtered from the coil-shield 104 may tend to deposit more thickly toward the edges of the workpiece than the center as represented by deposition profile 252. This is generally the reverse of the deposition pattern 250 of material from the target 110. By appropriately adjusting the ratio of RF power level applied to the coil-shield 104 to the DC power level of the bias applied to the target, the deposition level of the material being sputtered from the coil-shield 104 may be selected in such a manner as to compensate substantially for the nonuniformity of the deposition profile of the material from the target such that the overall deposition profile 254 of the layer from both sources of sputtered can be substantially more uniform than that which has often been obtained from the overhead target alone.
It is presently believed that the amount of sputtering which will originate from the coil 104 as compared to the sputtering which originates from the target 110 may be a function of the RF power applied to the coil 104 relative to the DC power applied to the target 110. By adjusting the ratio of the coil RF power to the target DC power, the relative amounts of material sputtered from the coil 104 and the target 110 may be varied so as to improve uniformity. It is believed that a particular ratio of the coil RF power to the target DC power will achieve the smallest degree of non-uniformity of the layer of material deposited from both the coil and the target. As the RF power to the coil is increased relative to the DC power applied to the target, the deposited layer tends to be more edge thick. Conversely, by decreasing the ratio of the RF power to the coil relative to the DC power applied to the target, the center of the deposited layer tends to grow increasingly thicker relative to the edges. Thus, by adjusting the ratio of the RF power to the coil relative to the DC power biasing the target, the material being sputtered from the coil can be increased or decreased as appropriate to compensate for non-uniformity of the material being deposited from the target to achieve a more uniform deposited layer comprising material from both the target and the coil. For the coil 104, a coil RF power to target DC power ratio of approximately 0.7 may provide satisfactory results on an 8 inch diameter wafer.
It is further believed that the relative amounts of sputtering between the coil and the target may also be a function of the DC biasing of the coil 104 relative to that of the target 110. This DC biasing of the coil-shield 104 may be adjusted in a variety of methods. For example, a matching network 402 and blocking impedance 406 (FIG. 4) coupled to the coil 104 typically comprise one or more inductors and capacitors. By varying the impedance of one or more these inductors and capacitors, the DC biasing of the coil-shield 104 might be adjusted to achieve the desired level of uniformity. In one embodiment, the RF power to the coil and the DC biasing of the coil-shield 104 may have separate adjustment inputs to achieve the desired results. For example, AC or DC biasing sources could be coupled through RF filters to the coil. An alternative power arrangement could include two RF generators operated at slightly different frequencies. The output of one generator would be coupled to the coil in the conventional manner but the other generator at the slightly different frequency would be capacitively coupled to the coil such that a change in the power level of the second generator would change the DC bias of the coil. Such an arrangement could provide independent control of the RF power and DC bias applied to the coil. At present, it is believed that relatively large changes in DC bias to the coil for a given RF power level would be necessary to have a substantial effect on the amount of material sputtered from the coil.
By adjusting various parameters including the coil bias level and the ratio of the coil RF power to the target DC power, the relative amounts of material sputtered from the target 110 and the coil 106 may be varied so as to achieve improved uniformity. As shown in FIG. 3, exemplary power ranges employed during the center thick step include 3-5 kW for DC power to the target and 1.5-3 kW for RF power applied to the coil. Within these ranges, a 4 kW value for DC power and a 2.5 kW value for RF power can provide good results, depending upon the application.
The optimal power ratio and the values of other parameters will vary depending upon the particular application including the particular sizes of the chamber, coil, target and substrate, their relative spacings, sputter gas pressure, sputter material and other variables well known to those skilled in the art.
However, in many applications the coil power cannot be increased beyond a certain value due to hardware limitations. For example, the current carrying capabilities of the coil 104 may limit the amount of RF power which may be applied to the coil without causing damage to the coil. In other applications, varying impedances or coupling a bias source to the coil in addition to an RF source may not be appropriate. As a result, in some applications, the desired degree of uniformity might not be readily achievable by balancing the application of RF power to the coil and DC power to the target or otherwise modifying the coil bias level.
Therefore, in accordance with one aspect of the present invention, a second step may be advantageously employed during deposition to increase uniformity on the surface of the substrate 112 even further. In this additional step, referred to herein as an "edge thick step," the application of DC power to the target 110 is reduced or eliminated, while RF power to the coil 104 is maintained uninterrupted at a preset level to maintain the high density plasma 118 which continues to ionize the sputtered material prior to deposition on the substrate. However, because the DC power to the target 110 is eliminated or at least decreased relative to RF power applied to the coil 104, the positively charged ions begin to strike primarily the coil 104 rather than the target 110. Consequently the ionized material deposited onto the substrate 112 is sputtered primarily if not entirely from the coil 104 rather than the target 110 during this second step.
In the illustrated embodiment, the coil 104 is supported by the shield 106 (FIG. 1) so that the coil 104 encircles the substrate 112 (FIG. 2) in a position which is above and recessed outwardly from the periphery of the substrate 112 as schematically represented in FIG. 2. As a result, the coil 104 is closer to the periphery than the center of the substrate. Consequentiy material sputtered from the coil 104 has a greater likelihood of depositing near the periphery of the substrate as opposed to the center of the substrate. By turning off the power to the target 110 during the deposition so that most of the sputtered material originates from the coil 104 rather than the target 110, the deposition profile can be switched from a center thick profile as represented by the profile 254 (FIG. 5b) discussed above to an edge thick profile as represented by the deposition profile 256. This edge thick profile 256 of the second step (target power turned off) can offset or compensate for a center thick tendency 254 of the first step (target power turned on). Consequently, the actual overall deposition profile 258 which is a combination of the deposition profiles 254 and 256 can be more uniform than the deposition profile 254 alone.
As shown in FIG. 3, exemplary ranges employed during the edge thick step include 0-1 kW for DC power and 1.5-3 kW for RF power. Within these ranges, a value for DC power of 0 kW and a value for RF power of 2.5 kW can produce an edge thick profile deposition in the second step which can substantially offset a center thick tendency of the deposition profile of the first step.
In a preferred embodiment, the DC power to the target 110 is shut off completely (represented as 0 kW in FIG. 3) while the RF power to the coil is maintained during the edge thick step such that the sputtered material comes almost entirely from the coil 104. However, the target 110 has a tendency to self bias itself even without any DC power being applied. Thus, some sputtering of material from the target 110 biasing may still occur during the edge thick step.
In addition to improving the uniformity of deposition over the entire substrate, the aforementioned multi-step process can also improve sidewall coverage of vias, channels and other structures having vertical surfaces. This may be understood by referring to FIG. 6a which illustrates the deposition coverage for a plurality of channels 125, which may result during that portion of the deposition in which the target 110 predominates, that is, the center thick step. As illustrated in FIG. 6a, the center thick step can provide good coverage of the horizontal surfaces of the channels 125 such as the bottom walls 126 as well as the center portions 128 of the surface of the substrate 112 separating the channels. However, because of the ionization of the deposition material which causes the material to travel more vertically, the deposition upon vertical surfaces, such as the sidewalls 130 of the channels 125, may be substantially thinner. If the sidewall coverage is too thin, it can interfere with the operation of the deposited layer. This is particularly true for deposited titanium underlayers.
On the other hand, where the deposition material originates primarily from the coil 104, the "edge thick" step, the sidewall coverage may be improved. It is believed that because the coil 104 is not positioned directly above the substrate 112, the sputtered material from the coil tends to strike the substrate 102 at angles that are more acute than the material from the target 110 which is positioned directly above the substrate. In effect, the horizontal velocity component of the material sputtered from the coil 104 is often much greater than the horizontal velocity component of the material sputtered from the target 110. As a result, the sputtered material from the coil 104 can provide improved coverage of the sidewalls 130 of the channels 125 as well as a smoothing effect on the surface of the substrate 112.
FIG. 6b illustrates the deposition coverage which may result during a deposition step in which sputtering from the coil predominates. As shown therein, the deposition rates for material deposited on the vertical surfaces 130 of the channels 125 relative to the deposition rates for material deposited on the horizontal surfaces 126, 128 tend to be more even when sputtering from the coil predominates as compared to the corresponding deposition rates for material deposited when sputtering from the target 110 predominates (FIG. 6a). In most applications the total quantity of material sputtered from the target 110 and deposited on the substrate will be substantially greater than the total quantity of material sputtered from the coil 104 and deposited onto the substrate. Thus, by adding a deposition step in which sputtering from the coil predominates by reducing or eliminating the application of a bias to the target 110 the amount of material deposited on the vertical surfaces relative to the that deposited on the horizontal surfaces can be increased. Thus, the combined effects of the two steps can provide more uniform deposition on the surface of the substrate 112 as well as good sidewall 130 and bottom coverage of the channels 125 as illustrated in FIG. 6c.
In another embodiment, the two step deposition process can be preceded by an optional etching step. In this step, a strong bias may be applied to the pedestal 114 while applying RF power to the coil 104. This RF bias applied to the pedestal 114 induces a correspondingly strong bias on the substrate 112. At the same time, a relatively low DC bias is applied to the target 110. If the bias induced on the substrate is made sufficiently high, more ions can be attracted to the surface of the substrate 112 as compared to the surfaces of the target 110 and the coil 104. The net effect of the etch step can be to have more material sputtered from the surface of the substrate 112 than is being deposited on the substrate 112 from the coil and target. As a result, the material can be removed from the surface of the substrate 112 in order to clean the contacts, and prepare the substrate 112 for the subsequent sputter deposition of the center thick and edge thick steps discussed above.
The negative bias applied to the pedestal 114 to induce net etching of the substrate will vary depending upon the particular application. In general, the pedestal bias during the etching step will be substantially higher than that of the deposition steps in which the substrate bias primarily is intended to aid in achieving good bottom coverage of the substrate channels rather than to enhance etching of the substrate. In the illustrated embodiment as shown in FIG. 3, a suitable pedestal bias is -80 V, for example, and may range from -40 to -100 V, for example, during the etching step. By comparison, the pedestal bias in FIG. 3 for the center thick and edge thick deposition steps is preferably less negative, such as -20 V, for example, and may range from 0 to -40 V, for example.
The RF power applied to the coil 104 may be maintained relatively constant during each of the etching and deposition steps as shown in FIG. 3 because good ionization is useful not only during the etching step but also during the deposition steps for good bottom coverage. As set forth above, a suitable RF power level for the coil is 2.5 kW, for example, and may range from 1.5 to 3 kW, for example. On the other hand, the DC power applied to the target may be substantially reduced during the etching step as compared to the deposition steps in order to reduce the sputtering level of the target during substrate etching. In the illustrated embodiment, a suitable target DC power level is 0.5 kW, for example, and may range from 0-1 kW, for example, during the etching step. By comparison, the DC power applied to the target may be substantially increased, such as to 4 kW, for example, to substantially increase target sputtering during the center thick step, and may be substantially reduced or eliminated to 0 kW, for example, to reduce or eliminate target sputtering during the edge thick deposition step, as discussed above.
The chamber pressure level may be maintained at a relatively constant level during each of the etching and deposition steps. However, because sputtering of the target and coil may be at a relatively low rate during etching of the substrate, the chamber pressure may be reduced during the etching step. Thus, as shown in FIG. 3, the chamber pressure may be maintained at a pressure value of 25 mT, for example, during the etching step and raised to a somewhat higher level to 30 mT, for example, during deposition steps to facilitate ionization of the sputtered material.
The duration of each step will of course depend upon a number of factors including the material being deposited, deposition rates, and desired etching depths and deposition thicknesses. Exemplary durations for the etching step may range from 5-10 seconds, for example and the duration of the center thick and edge thick depositions may approximate 20 seconds, for example.
FIG. 4 includes a schematic representation of the electrical connections of the plasma generating apparatus of this illustrated embodiment. To sputter target material onto the substrate 112, the target 110 is preferably negatively biased by a variable DC power source 400 to attract the ions of the ion flux 108. The pouwer source 400, and the other power sources discussed below, are preferably controlled by a microprocessor based workstation which is programmed to implement the processes described herein.
The pedestal 114 may be negatively biased by a variable DC, AC or RF power source 440 to bias the substrate 112 negatively to attract the ionized deposition material to the substrate 112. FIG. 3 discloses the bias applied to the pedestal during the various time intervals. As shown in FIG. 3, during the center thick and edge thick steps, the exemplary range employed for the pedestal bias is 0 to -40 V, and the exemplar value is -20 V. The pedestal bias during the etch step was discussed above. As shown in FIG. 3, if the pedestal 114 is biased by a high frequency RF power source, one end of the pedestal 114 may be coupled to the output of an amplifier and matching network 420, the input of which is coupled to an RF generator 440. External biasing of the pedestal 114 and the substrate 112 of greater than about 50 V in absolute value, relative to the ground, may increase sputtering (and resputtering) of the substrate 112, and thereby further promote deposition uniformity. In yet another alternative embodiment, an external biasing of the substrate 112 may be omitted. For example, the substrate 112 may develop a self-biasing of between about -5 V to about -10 V relative to the ground, even in the absence of any external biasing.
One end of the coil 104 is coupled to an RF source such as the output of an amplifier and matching network 402, the input of which is coupled to an RF generator 404. The other end of the coil 104 is coupled to ground, preferably through a blocking capacitor 406, which may be a variable capacitor. In addition, as described in copending application Ser. No. 08/907,382 filed Aug. 7, 1997 pending entitled "Plasma Vapor Deposition with Coil Sputtering" (Attorney Docket 1957/PVD/DV) and incorporated herein by reference in its entirety,a separate DC bias source may be coupled to the coil through an RF filter to permit control of coil sputtering rate independently of RF power levels to the coil. Hence, RF power to the coil may be reduced or eliminated in some or all steps.
RF power is applied to the coil 104 by feedthrough bolts which are supported by insulating feedthrough standoffs 124 (FIG. 1). The feedthrough standoffs 124, like the coil support standoffs 120, permit repeated deposition of conductive material from the target onto the feedthrough standoff 124 without the formation of a conducting path which could short the coil 104 to the chamber shield 106. The coil feedthrough standoff 124, like the coil support standoff 120, has an internal labyrinth structure to prevent the formation of a short between the coil 104 and the wall of the shield 106. The feedthrough is coupled to the RF generator 404 (shown schematically in FIG. 4) through the matching network 402 (also shown schematically in FIG. 4).
The target 110 may be composed of different materials,such as aluminum, titanium, or copper. It generally has the shape of a cylindrical disk as seen in FIGS. 1, 2 and 4. However, other design shapes for the target 110 are, of course, possible, and may lead to different deposition profiles for the material deposited from the target onto the substrate. For example, a secondary annular target (of titanium, aluminum or other suitable materials) may be positioned around the periphery of the substrate, to supplement the material being sputtered from a primary planar target onto the substrate, with the primary planar target positioned above the substrate. Each target which is negatively biased should be electrically insulated from the vacuum chamber which is typically grounded.
The coil 104 of the embodiment illustrated in FIGS. 1-2 is made of approximately 50 mm (2 inch) by approximately 1.6 mm (1/16 inch) heavy-duty bead-blasted solid high-purity (preferably 99.995% pure) titanium or copper ribbon formed into a single turn helical coil having a diameter of about 290 mm (11.5 inches). However, other highly conductive materials and shapes may be utilized depending upon the material being sputtered and other factors. For example, the ribbon may be as thick as 3 mm (1/8 inch). Also, if the material to be sputtered is aluminum, both the target and the coil should be made of high-purity aluminum. In addition to the ribbon shape illustrated, hollow tubing may be utilized, particularly if water cooling is desired.
Several of the embodiments discussed above utilized a single coil 104 with a single turn in the plasma chamber 100. It should be recognized that the present invention is applicable to plasma chambers having a multiple turn RF coil. The advantage of a multiple turn coil is that the required current levels can be substantially reduced for a given RF power level. However, multiple turn coils tend to be more complicated and hence most costly and difficult to clean as compared to single turn coils. For example, a three turn helical coil of titanium and its associated supporting structure could be quite expensive. The coil may have shapes other than helical such as spiral, for example.
It should also be recognized that the present invention is applicable to plasma chambers having more than one RF powered coil. For example, the present invention may be applied to multiple coil chambers for launching helicon waves of the type described in copending application Ser. No. 08/559,345, filed Nov. 15, 1995 pending for "Method and Apparatus for Launching a Helicon Wave in a Plasma" which is assigned to the assignee of the present application and is incorporated herein by reference.
The appropriate RF generators and matching circuits are components well known to those skilled in the art. For example, an RF generator such as the ENI Genesis series which has the capability to "frequency hunt" for the Lest frequency match with the matching circuit and antenna is suitable. The frequency of the generator for generating the RF power to the coil 104 is preferably 2 MHz but it is anticipated that the range can vary from, for example, 1 MHz to 4 MHz.
In the illustrated embodiments above, the chamber shield 106 has a diameter of 400 mm (16"), but it is anticipated that satisfactory results can be obtained with a diameter in the range of 150-635 mm (6"-25"). The chamber shield 106 may be fabricated from a variety of materials including insulative materials such as ceramics or quartz. However, the chamber shield 106 and all metal surfaces likely to be coated with the target material are preferably made of a material such as stainless steel or copper, unless made of the same material as the sputtered target material. The material of the structure which will be coated should have a coefficient of thermal expansion which closely matches that of the material being sputtered to reduce flaking of sputtered material from the chamber shield 106 or other structure onto the substrate 112. In addition, the material to be coated should have good adhesion to the sputtered material. Thus for example if the deposited material is titanium, the preferred metal of the chamber shield 106, standoffs 120 and 124 and other structures likely to be coated is bead-blasted titanium. Any surfaces which are more likely to sputter, such as the end caps of the coil and feedthrough standoffs 120 and 124, would preferably be made of the same type of material as the target 110, such as high-purity, bead-blasted titanium, for example. Of course, if the material to be deposited is a material other than titanium, the preferred metal is the deposited material, stainless steel, for example. Adherence can also be improved by coating the structures with molybdenum prior to sputtering the target 110. However, it is preferred that the coil 104 (or any other surface likely to sputter) not be coated with molybdenum or other materials since the molybdenum can contaminate the substrate 112 if sputtered from the coil 104.
The substrate 112 to target 110 spacing is in a range of about 120-150 mm, preferably about 140 mm (about 5.5"), but can also range from about 38 to 200 mm (1.5" to 8"). For this wafer to target spacing, suitable stepped wafer bottom coverage may be achieved with a coil diameter of 290 mm (11.5 inches) spaced from the target by a distance of approximately 50 mm (1.9 inches). It has been found that increasing the diameter of the coil which moves the coil away from the workpiece edge may have an adverse effect on bottom coverage. On the other hand, decreasing the coil diameter to move the coil closer to the wafer edge can adversely affect layer uniformity.
Deposition uniformity also appears to be a function of coil spacing from the target. As previously mentioned, a spacing of 50 mm (1.9 inches) between the coil and target may be found satisfactory for a target to wafer spacing of 140 mm. Moving the coil vertically either toward or away from the target (or wafer) can adversely affect deposition layer uniformity.
A variety of precursor gases may be utilized to generate the plasma including Ar, H.sub.2,O.sub.2 or reactive gases such as NF.sub.3, CF.sub.4 and many others. Various precursor gas pressures are suitable including pressures of 0.1-50 mTorr which includes the exemplar pressures set forth in FIG. 3. However, pressures between 10 mTorr and 50 mTorr facilitate ionization of sputtered material.
Citations de brevets Brevet cit� Date de d�p�t Date de publication D�posant TitreUS359429519 sept. 196620 juil. 1971Physics Technology Laboratories Inc.Rf sputtering of insulator materialsUS433611821 mars 198022 juin 1982Battelle Memorial InstituteMethods for making deposited films with improved microstructuresUS43626322 ao�t 19747 d�c. 1982Lfe CorporationGas discharge apparatusUS444197428 avr. 198310 avr. 1984Tokuda Seisakusho, Ltd.Magnetron sputtering apparatusUS449522126 oct. 198222 janv. 1985Signetics CorporationVariable rate semiconductor deposition processUS462631224 juin 19852 d�c. 1986The Perkin-Elmer CorporationPlasma etching system for minimizing stray electrical dischargesUS466122815 mai 198628 avr. 1987Varian Associates, Inc.Apparatus and method for manufacturing planarized aluminum filmsUS469223015 avr. 19868 sept. 1987Hitachi, Ltd.Thin film forming method through sputtering and sputtering deviceUS47164919 d�c. 198529 d�c. 1987Hitachi, Ltd.High frequency plasma generation apparatusUS471746224 oct. 19865 janv. 1988Hitachi, Ltd.Sputtering apparatusUS473117217 avr. 198615 mars 1988Matsushita Electric Industrial Co., Ltd.Method for sputtering multi-component thin-filmUS475681521 d�c. 197912 juil. 1988Varian Associates, Inc.Wafer coating systemUS479273212 juin 198720 d�c. 1988United States Of America As Represented By The Secretary Of The Air ForceRadio frequency plasma generatorUS481034223 juin 19887 mars 1989Fujitsu LimitedMethod for controlling substrate temperature in a high temperature sputtering processUS481612620 juil. 198728 mars 1989Nippon Telegraph And Telephone CorporationMethod for forming a planarized thin filmUS48187234 nov. 19874 avr. 1989Advanced Micro Devices, Inc.Silicide contact plug formation techniqueUS482454429 oct. 198725 avr. 1989International Business Machines CorporationLarge area cathode lift-off sputter deposition deviceUS484270323 f�vr. 198827 juin 1989Eaton CorporationMagnetron cathode and method for sputter coatingUS484477511 d�c. 19874 juil. 1989Christopher David DobsonIon etching and chemical vapour depositionUS486571228 juil. 198712 sept. 1989Varian Associates, Inc.Apparatus for manufacturing planarized aluminum filmsUS487142115 sept. 19883 oct. 1989Lam Research CorporationSplit-phase driver for plasma etch systemUS489770926 mai 198830 janv. 1990Hitachi, Ltd.Titanium nitride film in contact hole with large aspect ratioUS491803128 d�c. 198817 avr. 1990American Telephone And Telegraph Company,At&T Bell LaboratoriesProcesses depending on plasma generation using a helical resonatorUS49255428 d�c. 198815 mai 1990Trw Inc.Plasma plating apparatus and methodUS49419157 f�vr. 198917 juil. 1990Nippon Telegraph And Telephone CorporationThin film forming apparatus and ion source utilizing plasma sputteringUS49449615 ao�t 198831 juil. 1990Rensselaer Polytechnic InstituteDeposition of metals on stepped surfacesUS494845814 ao�t 198914 ao�t 1990Lam Research CorporationMethod and apparatus for producing magnetically-coupled planar plasmaUS497017629 sept. 198913 nov. 1990Motorola, Inc.Multiple step metallization processUS499022913 juin 19895 f�vr. 1991Plasma & Materials Technologies, Inc.High density plasma deposition and etching apparatusUS499909629 juin 198812 mars 1991Hitachi, Ltd.Method of and apparatus for sputteringUS506569825 mars 199119 nov. 1991Canon Kabushiki KaishaFilm forming apparatus capable of preventing adhesion of film depositsUS509104929 juin 199025 f�vr. 1992Plasma & Materials Technologies, Inc.High density plasma deposition and etching apparatusUS509488512 oct. 199010 mars 1992Genus, Inc.Differential pressure cvd chuckUS51222514 f�vr. 199116 juin 1992Plasma & Materials Technologies, Inc.High density plasma deposition and etching apparatusUS51356298 juin 19904 ao�t 1992Nippon Mining Co., Ltd.Thin film deposition systemUS514613729 mars 19908 sept. 1992Leybold AktiengesellschaftDevice for the generation of a plasmaUS516968425 mai 19908 d�c. 1992Toyoko Kagaku Co., Ltd.Wafer supporting jig and a decompressed gas phase growth method using such a jigUS517141223 ao�t 199115 d�c. 1992Applied Materials, Inc.Material deposition method for integrated circuit manufacturingUS517560830 ao�t 199029 d�c. 1992Hitachi, Ltd.Method of and apparatus for sputtering, and integrated circuit deviceUS517873925 sept. 199112 janv. 1993International Business Machines CorporationApparatus for depositing material into high aspect ratio holesUS518671815 avr. 199116 f�vr. 1993Applied Materials, Inc.Staged-vacuum wafer processing system and methodUS519237121 mai 19919 mars 1993Asm Japan K.K.Substrate supporting apparatus for a CVD apparatusUS520651629 avr. 199127 avr. 1993International Business Machines CorporationLow energy, steered ion beam deposition system having high current at low pressureUS521365013 sept. 199125 mai 1993Applied Materials, Inc.Apparatus for removing deposits from backside and end edge of semiconductor wafer while preventing removal of materials from front surface of waferUS522311230 avr. 199129 juin 1993Applied Materials, Inc.Removable shutter apparatus for a semiconductor process chamberUS522574026 mars 19926 juil. 1993General AtomicsMethod and apparatus for producing high density plasma using whistler mode excitationUS52285012 sept. 199220 juil. 1993Applied Materials, Inc.Physical vapor deposition clamping mechanism and heater/coolerUS523133415 avr. 199227 juil. 1993Texas Instruments IncorporatedPlasma source and method of manufacturingUS523456016 avr. 199210 ao�t 1993Hauzer Holdings BvMethod and device for sputtering of filmsUS523849925 mars 199124 ao�t 1993Novellus Systems, Inc.Gas-based substrate protection during processingUS52412456 mai 199231 ao�t 1993International Business Machines CorporationOptimized helical resonator for plasma processingUS528015430 janv. 199218 janv. 1994International Business Machines CorporationRadio frequency induction plasma processing system utilizing a uniform field coilUS529239316 d�c. 19918 mars 1994Applied Materials, Inc.Multichamber integrated process systemUS530427928 sept. 199219 avr. 1994International Business Machines CorporationRadio frequency induction/multipole plasma processing toolUS531271724 sept. 199217 mai 1994International Business Machines CorporationResidue free vertical pattern transfer with top surface imaging resistsUS532072825 f�vr. 199314 juin 1994Applied Materials, Inc.Planar magnetron sputtering source producing improved coating thickness uniformity, step coverage and step coverage uniformityUS533062823 oct. 199119 juil. 1994Varian Associates, Inc.Collimated deposition apparatus and methodUS53465784 nov. 199213 sept. 1994Novellus Systems, Inc.Induction plasma sourceUS536099621 mai 19931 nov. 1994Applied Materials, Inc.Titanium nitride/titanium silicide multiple layer barrier with preferential (111) crystallographic orientation on titanium nitride surfaceUS536101628 janv. 19931 nov. 1994General AtomicsHigh density plasma formation using whistler mode excitation in a reduced cross-sectional area formation tubeUS536659017 mars 199422 nov. 1994Sony CorporationDry etching methodUS536868524 mars 199329 nov. 1994Hitachi, Ltd.Dry etching apparatus and methodUS539796229 juin 199214 mars 1995Texas Instruments IncorporatedSource and method for generating high-density plasma with inductive power couplingUS540407927 juil. 19934 avr. 1995Matsushita Electric Industrial Co., Ltd.Plasma generating apparatusUS541843127 ao�t 199323 mai 1995Hughes Aircraft CompanyRF plasma source and antenna thereforUS542189119 oct. 19926 juin 1995Plasma & Materials Technologies, Inc.High density plasma deposition and etching apparatusUS542766822 oct. 199027 juin 1995Ricoh Company, Ltd.Thin film deposition systemUS542907020 nov. 19924 juil. 1995Plasma & Materials Technologies, Inc.High density plasma deposition and etching apparatusUS542971016 f�vr. 19944 juil. 1995Sony CorporationDry etching methodUS542999516 juil. 19934 juil. 1995Kabushiki Kaisha ToshibaMethod of manufacturing silicon oxide film containing fluorineUS543035530 juil. 19934 juil. 1995Texas Instruments IncorporatedRF induction plasma source for plasma processingUS543179929 oct. 199311 juil. 1995Applied Materials, Inc.Collimation hardware with RF bias rings to enhance sputter and/or substrate cavity ion generation efficiencyUS544399517 sept. 199322 ao�t 1995Applied Materials, Inc.Method for metallizing a semiconductor waferUS55036768 f�vr. 19952 avr. 1996Lam Research CorporationApparatus and method for magnetron in-situ cleaning of plasma reaction chamberUS557359529 sept. 199512 nov. 1996Lam Research CorporationMethods and apparatus for generating plasmaUS563935712 mai 199417 juin 1997Applied MaterialsSynchronous modulation bias sputter method and apparatus for complete planarization of metal filmsUS570749812 juil. 199613 janv. 1998Applied Materials, Inc.Avoiding contamination from induction coil in ionized sputteringUS583033123 sept. 19943 nov. 1998Seagate Technology, Inc.Apparatus and method for sputtering carbonEP0520519A129 juin 199230 d�c. 1992Applied Materials, Inc.Plasma processing reactor and process for plasma etchingEP0607797A15 janv. 199427 juil. 1994International Business Machines CorporationAn apparatus and method for enhanced inductive coupling to plasmas with reduced sputter contaminationEP0807954A18 mai 199719 nov. 1997Applied Materials, Inc.Coils for generating a plasma and for sputteringEP0836219A26 oct. 199715 avr. 1998Applied Materials, Inc.Active shield for generating a plasma for sputteringGB2162365A Titre non disponibleGB2231197A Titre non disponibleJP5129276A Titre non disponibleJP5148644A Titre non disponibleJP5152248A Titre non disponibleJP6232055A Titre non disponibleJP6283470A Titre non disponibleJP7176398A Titre non disponibleJP7176399A Titre non disponibleJP8153712A Titre non disponibleJP8288259A Titre non disponibleJP56056722A Titre non disponibleJP59190363A Titre non disponibleJP61190070A Titre non disponibleWO1986006623A13 mai 198520 nov. 1986Tranquility Products International, Inc.Absorbent padCitations hors brevetsR�f�rence1Ahn et al., Effects of Substrate Temperature on Copper Distribution, Resistivity, and Microstructure in Magnetron Sputtered Al Cu Films, Thin Solid Films, vol. 153, pp. 409 419, Oct. 26, 1987.2Ahn et al., Effects of Substrate Temperature on Copper Distribution, Resistivity, and Microstructure in Magnetron-Sputtered Al-Cu Films, Thin Solid Films, vol. 153, pp. 409-419, Oct. 26, 1987.3Demaray et al., "Aluminum Alloy Planarization for Topography Control of Multilevel VLSI Interconnect," Proceedings--VLSI and Computers: First International Conference on Computer Technology, Systems and Applications, May 11, 1987.4Demaray et al., Aluminum Alloy Planarization for Topography Control of Multilevel VLSI Interconnect, Proceedings VLSI and Computers: First International Conference on Computer Technology, Systems and Applications, May 11, 1987.5Helmer et al., "Pressure Effects in Planar Magnetron Sputter Deposition," Journal of Vacuum Science & Technology A (Vacuum, Surfaces, and Films), vol. 4, No. 3, pt. 1, pp. 408-412, May-Jun., 1986.6Helmer et al., Pressure Effects in Planar Magnetron Sputter Deposition, Journal of Vacuum Science & Technology A (Vacuum, Surfaces, and Films), vol. 4, No. 3, pt. 1, pp. 408 412, May Jun., 1986.7Hoffman et al., "Planarization of Aluminum Alloy Films During High Rate Sputtering," Thin Solid Films, vol. 153, pp. 369-377, Oct. 26, 1987.8Hoffman et al., Planarization of Aluminum Alloy Films During High Rate Sputtering, Thin Solid Films, vol. 153, pp. 369 377, Oct. 26, 1987.9Hoffman, "Practical Troubleshooting of Vacuum Deposition Processes and Equipment for Aluminum Metallization," Solid State Technology, vol. 21, No. 12, pp. 47-56, Dec. 12, 1978.10Hoffman, "Tungsten Titanium Diffusion Barrier Metallization, "Solid State Technology, vol. 26, No. 6, pp. 119-126, Jun. 6, 1983.11Hoffman, Practical Troubleshooting of Vacuum Deposition Processes and Equipment for Aluminum Metallization, Solid State Technology, vol. 21, No. 12, pp. 47 56, Dec. 12, 1978.12Hoffman, Tungsten Titanium Diffusion Barrier Metallization, Solid State Technology, vol. 26, No. 6, pp. 119 126, Jun. 6, 1983.13J. Hopwood et al., "Mechanisms for Highly Ionized Magnetron Sputtering," J. Appl. Phys., vol. 78, pp. 758-765, 1995.14J. Hopwood et al., Mechanisms for Highly Ionized Magnetron Sputtering, J. Appl. Phys ., vol. 78, pp. 758 765, 1995.15Joshi et al., Collimated Sputtering of TiN/Ti Liners into Sub Half Micron High Aspect Ratio Contacts/Lines, Jun. 9 10, 1992 VMIC Conference 1992, pp. 253 259.16Joshi et al., Collimated Sputtering of TiN/Ti Liners into Sub-Half Micron High Aspect Ratio Contacts/Lines, Jun. 9-10, 1992 VMIC Conference 1992, pp. 253-259.17M. Matsuoka et al., Dense Plasma Production and Film Deposition by New High Rate Sputtering Using an Electric Mirror, J. Vac. Sci. Technol ., A 7 (4), 2652 2657, Jul./Aug. 1989.18M. Matsuoka et al., Dense Plasma Production and Film Deposition by New High-Rate Sputtering Using an Electric Mirror, J. Vac. Sci. Technol., A 7 (4), 2652-2657, Jul./Aug. 1989.19M. Yamashita, "Fundamental Characteristics of Built-in High Frequency Coil Type Sputtering Apparatus," J. Vac. Sci. Technol., vol. A7, pp. 151-158, 1989.20M. Yamashita, "Sputter Type High Frequency Ion Source for Ion Beam Deposition Apparatus," Jap. J. Appl. Phys., vol. 26, pp. 721-727, 1987.21M. Yamashita, Fundamental Characteristics of Built in High Frequency Coil Type Sputtering Apparatus, J. Vac. Sci. Technol ., vol. A7, pp. 151 158, 1989.22M. Yamashita, Sputter Type High Frequency Ion Source for Ion Beam Deposition Apparatus, Jap. J. Appl. Phys ., vol. 26, pp. 721 727, 1987.23Meikle et al., "Semiconductor Process Considerations for Collimated Source Sputtering of Ti Films," Jun. 9-10, 1992 VMIC Conference, 1992, pp. 289-291.24Meikle et al., Semiconductor Process Considerations for Collimated Source Sputtering of Ti Films, Jun. 9 10, 1992 VMIC Conference, 1992, pp. 289 291.25N. Jiwari et al., "Helicon wave plasma reactor employing single-loop antenna," J. of Vac. Sci. Technol., A 12(4), pp. 1322-1327, Jul./Aug. 1994.26N. Jiwari et al., Helicon wave plasma reactor employing single loop antenna, J. of Vac. Sci. Technol ., A 12(4), pp. 1322 1327, Jul./Aug. 1994.27P. Kidd, "A Magnetically Confined and ECR Heated Plasma Machine for Coating and Ion Surface Modification Use," J. Vac. Sci. Technol., vol. A9, pp. 466-473, 1991.28P. Kidd, A Magnetically Confined and ECR Heated Plasma Machine for Coating and Ion Surface Modification Use, J. Vac. Sci. Technol ., vol. A9, pp. 466 473, 1991.29Park et al., "Influences of D.C. Bias on Aluminum Films Prepared with a High Rate Magnetron Sputtering Cathode," Thin Solid Films, 1985.30Park et al., Influences of D.C. Bias on Aluminum Films Prepared with a High Rate Magnetron Sputtering Cathode, Thin Solid Films, 1985.31S.M. Rossnagel et al., "Magnetron Sputter Deposition with High Levels of Metal Ionization," Appl. Phys. Lett., vol. 63, pp. 3285-3287, 1993.32S.M. Rossnagel et al., "Metal Ion Deposition from Ionized Magnetron Sputtering Discharge," J. Vac. Sci. Technol., vol. B12, pp. 449-453, 1994.33S.M. Rossnagel et al., Magnetron Sputter Deposition with High Levels of Metal Ionization, Appl. Phys. Lett ., vol. 63, pp. 3285 3287, 1993.34S.M. Rossnagel et al., Metal Ion Deposition from Ionized Magnetron Sputtering Discharge, J. Vac. Sci. Technol ., vol. B12, pp. 449 453, 1994.35S.M. Rossnagel, "Directional and Ionized Sputter Deposition for Microelectronics Applications," Proc. of 3rd ISSP ( Tokyo ), pp. 253-260, 1995.36S.M. Rossnagel, Directional and Ionized Sputter Deposition for Microelectronics Applications, Proc. of 3rd ISSP ( Tokyo ), pp. 253 260, 1995.37S.M. Rossnagel, et al., "Filling Dual Damascene Interconnect Structures with AlCu and Cu Using Ionized Magnetron Deposition," J. Vac. Sci. Technol., vol. B13, pp. 125-129, 1995.38S.M. Rossnagel, et al., Filling Dual Damascene Interconnect Structures with AlCu and Cu Using Ionized Magnetron Deposition, J. Vac. Sci. Technol ., vol. B13, pp. 125 129, 1995.39Search report dated Feb. 27, 1997, EPC application No. 96308251.6.40Search Report issued in PCT/US98/18898 filed Sep. 9, 1998.41Singapore Search Report in Application No. 9704107 3 filed Nov. 20, 1997.42Singapore Search Report in Application No. 9704107-3 filed Nov. 20, 1997.43Skelly et al., "Significant Improvement in Step Coverage Using Bias Sputter Aluminum," J. Vac. Sci. Technol., 1986.44Skelly et al., Significant Improvement in Step Coverage Using Bias Sputter Aluminum, J. Vac. Sci. Technol., 1986.45U. S. Serial No. 08/789,960 (Atty. Dkt. 1643).46U.S. application No. 08/461,575, filed Sep. 30, 1992, pending (Atty. Dk. 364.F1).47U.S. application No. 08/730,722, filed Oct. 8, 1996, pending (Aty. Dk. 1207/MD/PVD/DV).48U.S. application No. 08/733,620, filed Oct. 17, 1996, pending (Attorney Docket # 1457/PVD/DV).49U.S. application No. 08/733,620, filed Oct. 17, 1996, pending (Attorney Docket 1457/PVD/DV).50U.S. application No. 08/753,251, filed Nov. 21, 1996, pending (Aty. Dk. 1657/PVD/DV).51Van Gogh et al., "Characterization of Improved TiN Films by Controlled Divergence Sputtering," Jun. 9-10, 1992 VMIC Conference, 1992, pp. 310-313.52Van Gogh et al., Characterization of Improved TiN Films by Controlled Divergence Sputtering, Jun. 9 10, 1992 VMIC Conference, 1992, pp. 310 313.53W.M. Holber, et al., "Copper Deposition by Electron Cyclotron Resonance Plasma," J. Vac. Sci. Technol., vol. A11, pp. 2903-2910, 1993.54W.M. Holber, et al., Copper Deposition by Electron Cyclotron Resonance Plasma, J. Vac. Sci. Technol ., vol. A11, pp. 2903 2910, 1993.55Y W. Kim et al., Directed Sputter Deposition of AICu: Film Microstructure and Chemistry, J. Vac. Sci. Technol ., vol. A12, pp. 3169 3175, 1994.56Y-W. Kim et al., "Directed Sputter Deposition of AICu: Film Microstructure and Chemistry," J. Vac. Sci. Technol., vol. A12, pp. 3169-3175, 1994. R�f�renc� par Brevet citant Date de d�p�t Date de publication D�posant TitreUS614650822 avr. 199814 nov. 2000Applied Materials, Inc.Sputtering method and apparatus with small diameter RF coilUS62740082 oct. 200014 ao�t 2001Applied Materials, Inc.Integrated process for copper via fillingUS63684696 mai 19979 avr. 2002Applied Materials, Inc.Coils for generating a plasma and for sputteringUS637581019 nov. 199723 avr. 2002Applied Materials, Inc.Plasma vapor deposition with coil sputteringUS64408316 d�c. 200027 ao�t 2002Koninklijke Philips Electronics N.V.Ionized metal plasma deposition process having enhanced via sidewall coverageUS64511771 nov. 200017 sept. 2002Applied Materials, Inc.Vault shaped target and magnetron operable in two sputtering modesUS645117930 janv. 199717 sept. 2002Applied Materials, Inc.Method and apparatus for enhancing sidewall coverage during sputtering in a chamber having an inductively coupled plasmaUS647535628 janv. 20005 nov. 2002Applied Materials, Inc.Method and apparatus for improving sidewall coverage during sputtering in a chamber having an inductively coupled plasmaUS655906113 ao�t 20016 mai 2003Applied Materials, Inc.Method and apparatus for forming improved metal interconnectsUS669595411 oct. 200124 f�vr. 2004Applied Materials, Inc.Plasma vapor deposition with coil sputteringUS67095539 mai 200223 mars 2004Applied Materials, Inc.Multiple-step sputter depositionUS67099875 f�vr. 200223 mars 2004Applied Materials, Inc.Method and apparatus for forming improved metal interconnectsUS678363917 janv. 200231 ao�t 2004Applied MaterialsCoils for generating a plasma and for sputteringUS678700616 juil. 20027 sept. 2004Applied Materials, Inc.Operating a magnetron sputter reactor in two modesUS68997992 oct. 200231 mai 2005Applied Materials, Inc.Method and apparatus for improving sidewall coverage during sputtering in a chamber having an inductively coupled plasmaUS690301614 ao�t 20037 juin 2005Cohen, Uri, Dr.Combined conformal/non-conformal seed layers for metallic interconnectsUS692422623 d�c. 20022 ao�t 2005Cohen, Uri, Dr.Methods for making multiple seed layers for metallic interconnectsUS69917093 sept. 200431 janv. 2006Applied Materials, Inc.Multi-step magnetron sputtering processUS699201221 janv. 200431 janv. 2006Applied Materials, Inc.Method and apparatus for forming improved metal interconnectsUS710543428 d�c. 200412 sept. 2006Cohen, Uri, Dr.Advanced seed layery for metallic interconnectsUS719905214 f�vr. 20053 avr. 2007Cohen UriSeed layers for metallic interconnectsUS728244517 janv. 200716 oct. 2007Cohen, Uri, Dr.Multiple seed layers for interconnectsUS750400631 juil. 200317 mars 2009Applied Materials, Inc.Self-ionized and capacitively-coupled plasma for sputtering and resputteringUS75503865 oct. 200723 juin 2009Cohen, Uri, Dr.Advanced seed layers for interconnectsUS755671822 juin 20047 juil. 2009Tokyo Electron LimitedHighly ionized PVD with moving magnetic field envelope for uniform coverage of feature structure and waferUS768249628 mars 200623 mars 2010Cohen, Uri, Dr.Apparatus for depositing seed layersUS77447355 mars 200429 juin 2010Tokyo Electron LimitedIonized PVD with sequential deposition and etchingUS812386122 mars 201028 f�vr. 2012Seed Layers Technology, LLCApparatus for making interconnect seed layers and productsUS827322216 mai 200725 sept. 2012Southwest Research InstituteApparatus and method for RF plasma enhanced magnetron sputter depositionUS827761714 ao�t 20072 oct. 2012Southwest Research InstituteConformal magnetron sputter depositionUS839883215 sept. 200519 mars 2013Applied Materials Inc.Coils for generating a plasma and for sputteringFaire pivoterImage d'origineAccueil Google - Plan du site - T�l�chargements par lot sur l'USPTO - R�gles de confidentialit� - Conditions d'utilisation - � propos de Google�Brevets - Envoyer des commentairesDonn�es fournies par IFI CLAIMS Patent Services©2012 Google