Patent US7829624 - One-pot synthesis of nanoparticles and liquid polymer for rubber applications - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsA method for performing a one-batch synthesis of a blend of nanoparticles and liquid polymer includes polymerizing a first monomer and optionally a second monomer in a hydrocarbon solvent to form the liquid polymer. The polymerization is terminated before completion with a quenching agent. Then a charge...http://www.google.com/patents/US7829624?utm_source=gb-gplus-sharePatent US7829624 - One-pot synthesis of nanoparticles and liquid polymer for rubber applicationsAdvanced Patent SearchPublication numberUS7829624 B2Publication typeGrantApplication numberUS 11/771,659Publication dateNov 9, 2010Filing dateJun 29, 2007Priority dateJun 29, 2007Fee statusPaidAlso published asCN101848949A, CN101848949B, EP2167557A1, EP2167557B1, US20090005491, US20100324167, WO2009006434A1Publication number11771659, 771659, US 7829624 B2, US 7829624B2, US-B2-7829624, US7829624 B2, US7829624B2InventorsSandra WarrenOriginal AssigneeBridgestone CorporationExport CitationBiBTeX, EndNote, RefManPatent Citations (249), Non-Patent Citations (303), Referenced by (12), Classifications (14), Legal Events (2) External Links: USPTO, USPTO Assignment, EspacenetOne-pot synthesis of nanoparticles and liquid polymer for rubber applications
US 7829624 B2Abstract
A method for performing a one-batch synthesis of a blend of nanoparticles and liquid polymer includes polymerizing a first monomer and optionally a second monomer in a hydrocarbon solvent to form the liquid polymer. The polymerization is terminated before completion with a quenching agent. Then a charge of polymerization initiator, and a mixture of multiple-vinyl aromatic monomer and mono-vinyl aromatic monomer are added. This causes further polymerization whereby nanoparticles are formed in situ having a core including the multiple-vinyl aromatic monomer, and a shell including the first monomer or the first monomer and the second monomer. Liquid polymer/nanoparticle blends resulting from the method and rubber compositions incorporating the blends are also disclosed.
1. A method for preparing a one-batch synthesized blend of nanoparticles and liquid polymer in a solvent, the method comprising the steps of:
(a) in a reaction vessel, polymerizing either a first monomer to form the liquid polymer, or copolymerizing the first monomer and a second monomer to form the liquid polymer;
(b) partially terminating the polymerization with a quenching agent; and
(c) adding a multiple-vinyl aromatic monomer, a mono-vinyl aromatic monomer, and an optional charge of polymerization initiator;
whereby nanoparticles are formed in situ and said nanoparticles have a core including the mono-vinyl aromatic monomer and a shell comprising the first monomer or the first and the second monomer.
2. The method of claim 1, wherein the quenching agent partially terminates the polymerization so that 20 to 95% of the polymers are terminated.
3. The method of claim 1, further comprising the step of filtering and drum drying the one-batch synthesized blend of nanoparticles and liquid polymer.
4. The method of claim 1, wherein the second monomer is selected from the group consisting of styrene, α-methyl styrene, 1-vinyl naphthalene, 2-vinyl naphthalene, 1-α-methyl vinyl naphthalene, 2-α-methyl vinyl naphthalene, vinyl toluene, methoxystyrene, t-butoxystyrene, and alkyl, cycloalkyl, aryl, alkaryl, and aralkyl derivatives thereof in which the total number of carbon atoms in the derivative is not greater than 18, or any di- or tri-substituted aromatic hydrocarbons, and mixtures thereof.
5. The method of claim 1, wherein the first monomer is a conjugated diene.
6. The method of claim 5, wherein the first monomer is selected from the group consisting of C4-C8 conjugated dienes and mixtures thereof.
7. The method of claim 1, wherein the nanoparticles are crosslinked with the multiple-vinyl aromatic monomer.
8. The method of claim 1, wherein the multiple-vinyl aromatic monomer is selected from the group consisting of compounds with a general formula of:
9. The method of claim 6, wherein the multiple-vinyl aromatic monomer is divinylbenzene.
10. The method of claim 1, wherein the first monomer is butadiene and the second monomer is styrene.
11. The method of claim 1, wherein the core of the nanoparticle has a Tg of about 60� C. or higher.
12. The method of claim 1, wherein the shell of the nanoparticle has a Tg lower than about 0� C.
13. The method of claim 1, wherein the shell of the nanoparticle has a Tg between about 0� C. and about −70� C.
14. The method of claim 1, wherein the core of the nanoparticle has a Tg of at least about 60� C. higher than the Tg of the shell.
15. The method of claim 1, wherein the liquid polymer has an Mw of about 10,000 to about 120,000.
16. The method of claim 1, wherein the nanoparticles are formed by micelle self-assembly.
17. The method of claim 15, wherein the nanoparticles have a core comprising styrene cross-linked with divinylbenzene and a shell comprising butadiene.
18. The method of claim 1, wherein the multiple-vinyl aromatic monomer is added before the polymerization initiator and mono-vinyl aromatic monomer.
19. The method of claim 1, wherein the quenching agent is selected from the group consisting of methanol, ethanol, propanol, and isopropanol.
20. The method of claim 1, wherein the quenching agent is a functionalizing agent.
21. The method of claim 20, wherein the functionalizing agent is tin tetrachloride.
22. The method of claim 1, wherein the polymerizing or copolymerizing of step (a) are initiated with an anionic initiator.
23. The method of claim 1, wherein the steps are performed in the same reaction vessel.
24. A method for making a rubber composition, the method comprising:
making the blend of nanoparticles and liquid polymer according to claim 1; and
adding the blend to a rubber composition.
25. A method for making a tire with nanoparticles and liquid polymer, the method comprising:
making a blend of nanoparticles and liquid polymer according to claim 1;
adding the blend to a rubber composition;
molding the rubber composition into a tire tread; and
constructing a tire using the tire tread.
The technology discussed herein relates generally to rubber compositions. In particular, it relates to methods for synthesizing nanoparticle and liquid polymer blends in a single batch.
As depicted in the example shown in FIG. 1, the nanoparticles described herein are each made up of a group or a collection of several polymer chains that are organized around a center 1. The polymer chains are linked together at one end at a core formed from cross-linked monomer units on each polymer chain. The polymer chains extend from the core 2 outwardly to form a shell 3. The shell 3 includes the monomer units of the polymers that are not in the core 2. It should be understood that the shell 3 is not limited to a single monomer unit in each polymer chain, but may include several monomer units. Additionally, the shell 3 may be separated into sublayers, and the sublayers may include blocks of various homopolymer or copolymer. For example, a sublayer may include a block of randomized styrene-butadiene copolymer or a homopolymer such as butadiene. The outermost layer of the shell 4, is comprised of the monomer units or functionally or non-functionally initiated polymer chain heads at the outer terminal ends of each polymer. The shell 4 is the outermost portion of the nanoparticle. The living polymer chains form micelles due to the aggregation of ionic chain ends and the chemical interactions of the polymer chains in hydrocarbon solvent. When the multiple-vinyl aromatic monomer is added, the micelles become crosslinked and the stable nanoparticle is formed.
Nanoparticles and liquid polymers for use in rubber compositions are known from commonly owned U.S. patent application Ser. No. 11/305,279, which is hereby incorporated by reference. The combination of nanoparticle and liquid polymer improves important properties of rubber articles, such as vehicle tires, and in particular, the tread portion of vehicle tires. For example, wet/dry traction and rolling resistance of tire tread can be improved with the addition of nanoparticles and liquid polymers while maintaining good reinforcement for tread durability. A reduction or elimination of the amount of processing oils needed in a composition used for vehicle tires, and this is made possible by the liquid polymer and nanoparticle rubber composition.
However, there are difficulties in synthesizing and processing the previously disclosed nanoparticles and liquid polymers. Previously known methods involve synthesizing nanoparticles and liquid polymer separately, drying them separately, and then separately adding each component into a rubber composition. The nanoparticles suffer from poor dispersion in the rubber compound and the liquid polymer is difficult to process. Processing problems stem from the fact that the liquid polymer is a highly viscous substance that is very difficult to separate from solvent and dry. The two separate components also have to be stored separately, thereby consuming valuable inventory space.
The technology disclosed herein allows the nanoparticles and liquid polymer to be synthesized together in the same batch. The resulting blend is easier to process and dry than a separately synthesized liquid polymer. The blend also facilitates dispersion of the nanoparticles. It also saves inventory space since only one product in one container needs to be stored, instead of two products in two containers.
A method for performing a one-batch synthesis of a blend of nanoparticles and liquid polymer includes polymerizing a first monomer and optionally a second monomer in a hydrocarbon solvent to form the liquid polymer. The polymerization is partially terminated with a quenching agent. Then a charge of polymerization initiator, and a mixture of multiple-vinyl aromatic monomer and mono-vinyl aromatic monomer are added. This causes further polymerization whereby nanoparticles are formed in situ having a core including the multiple-vinyl aromatic monomer, and a shell including the first monomer or the first monomer and the second monomer.
A composition of matter consists essentially of a blend of core-shell type micellar nanoparticles and a liquid polymer. The nanoparticles are dispersed and blended with the liquid polymer.
The blends of nanoparticle and liquid polymer made by the methods disclosed herein may be added to a rubber composition to produce a nanoparticle/liquid polymer rubber composition. As an example, a tire that incorporates the nanoparticle/liquid polymer rubber composition can be formed by a tire tread comprising the rubber composition, and constructing a tire using the tire tread.
FIG. 1 shows a diagram of a nanoparticle.
FIG. 2 shows a rubber article with improved reinforcement and controllable hysteresis in an embodiment of the present invention.
Methods for performing a one-batch synthesis for making a blend of nanoparticles and liquid polymer are disclosed herein. An illustrative method involves a liquid polymer polymerization process wherein a first monomer and a second monomer are polymerized in a hydrocarbon solvent in a pot (reaction vessel). The copolymerization process is allowed to proceed to completion and is partially terminated with a quenching agent. These monomers copolymerize to form a liquid polymer. The ratio of terminated polymers to unterminated, living polymers can vary according to the application. A broad range is 1-99 wt % terminated, liquid polymer to 99-1 wt % unterminated, living polymer. A preferable range for at least some applications is 25-75 wt % terminated, liquid polymer to 75-25 wt % unterminated, living polymer.
As part of this example method, a charge of polymerization initiator and a mixture of multiple-vinyl aromatic monomer and a mono-vinyl aromatic monomer are added to the same pot that contains the liquid polymer. This charge initiates a second polymerization process wherein unterminated monomer chains left over from the liquid polymer polymerization process copolymerize with the mono-vinyl aromatic monomer. The resulting copolymers self-assemble into core-shell type micelle structures in the hydrocarbon solvent. The multiple-vinyl aromatic monomer functions to cross-link the micelles holding them together as nanoparticles.
As used herein, unless otherwise stated, a charge or addition to the reaction vessel may be simultaneous or stepwise. Stepwise means that either the addition of one ingredient is completed before the addition of another ingredient is begun, or the addition of one ingredient is begun (but not necessarily completed) before the addition of another ingredient has begun.
Alternatively, another illustrative method involves a liquid polymerization step as described above. However, in this method the nanoparticle polymerization process differs in that there is a step-wise addition of a charge of mono-vinyl aromatic monomer (first), and then (secondly) a charge of multiple-vinyl aromatic monomer and initiator to the pot. The resulting copolymers self-assemble into core-shell type micelles in the hydrocarbon solvent, and the multiple-vinyl aromatic monomer functions to cross-link the micelles holding them together as nanoparticles.
The blends that result from the first method and the second method are typically not the same. Under similar conditions, the first method produces polymer nanoparticles with a core densely crosslinked at the center of the core; while the second method gives polymer nanoparticles with a core relatively less densely crosslinked, but crosslinked throughout the entire core.
The crosslinking density can be defined as number of crosslinks per monomer (Xd). In an example where the nanoparticle comprises monomers of styrene and divinyl benzene as the crosslinking agent, the Xd is determined by the ratio of moles of DVB to moles of DVB and styrene. This number may range from 0.01 to 1, for example 0.1 to 0.8, such as 0.2 to 0.4. In the example first method described above the cross-linking density may be 0.2-0.4, for example 0.3, and in the example second method described above the cross-linking density may be 0.8-1.0, for example 0.9.
Preferably a crosslinking agent is selected which has an affinity to the vinyl-substituted aromatic hydrocarbon monomer blocks and migrates to the center of the micelles due to its compatibility with the monomer units and initiator residues present in the center of the micelle and its relative incompatibility with the solvent and monomer units present in the outer layer of the micelle.
The one-batch processes described herein yields a blend that is easier to process and dry than when the liquid polymer is synthesized separately. Dispersion of the nanoparticles is also facilitated. The resulting blends also save inventory space since only one product in one container needs to be stored, instead of two products in two containers.
The first step of the illustrative methods described above results in the polymerization of the liquid polymer. A first monomer is added to a reaction vessel along with an anionic initiator to start the polymerization of the monomers and form a liquid polymer. The liquid polymer may comprise a homopolymer, such as polybutadiene, when only a single type of monomer is polymerized. The liquid polymer may also comprise a copolymer, such as styrene-butadiene copolymer when a first and second monomer are polymerized.
The anionic initiator is preferably selected from any known organolithium compounds. Suitable organolithium compounds are represented by the formula as shown below:
wherein R is a hydrocarbyl group having 1 to x valence(s). R generally contains 1 to 20, preferably 2-8, carbon atoms per R group, and x is an integer of 1-4. Typically, x is 1, and the R group includes aliphatic radicals and cycloaliphatic radicals, such as alkyl, cycloalkyl, cycloalkylalkyl, alkylcycloalkyl, alkenyl, as well as aryl and alkylaryl radicals. Other known initiators can also be employed. As specific examples, n-butyllithium, sec-butyl lithium, tert-butyllithium, or a mixture thereof can be used as initiators.
The polymerization is partially terminated by adding a quenching agent. This partial termination leaves unterminated polymers for forming the shell of the nanoparticle in the subsequent nanoparticle polymerization process. The partial termination step is relatively fast. For example, the partial termination may be run for about 15 minutes. As used herein, partial means less than complete.
The liquid polymer can be made by a batch process or continuously. Typically, a hydrocarbon solvent is used, although it may be possible to use other solvents. According to the process disclosed herein there are some advantages to synthesizing the liquid polymer in a batch process. However, it is also possible to perform the method described herein by a continuous process in a single batch. By “single batch” or “one-batch” it is meant that there is no isolation and drying between polymerization steps. In a continuous process the monomers and an initiator are continuously fed into the reaction vessel with solvent.
The pressure in the reaction vessel should be sufficient to maintain a substantially liquid phase under the conditions of the polymerization reaction. The reaction medium may generally be maintained at a temperature that is within the range of about 20� C. to about 140� C. throughout the copolymerization.
After the reaction has had time to proceed to for a relatively low molecular weight polymer, the reaction is quenched by adding a terminating agent (also called a quenching agent as used herein). The amount of terminating agent added determines how much of the polymer becomes terminated liquid polymer, and how much of the polymer remains unterminated with a living end. Since the polymers with living ends are later used to form the shell layer of the nanoparticles, the amount of terminating agent also determines the ratio of liquid polymer to nanoparticles in the nanoparticle/liquid polymer blend.
The formation of the liquid polymer is complete after the reaction is partially terminated with the quenching agent. In the illustrative methods described herein a charge is then added that begins the nanoparticle polymerization process.
In an illustrative nanoparticle polymerization process, an anionic initiator is first added (i.e. before adding the mono- and multiple-vinyl aromatic monomers) to aid in forming and stabilizing of micelles before cross-linking occurs. The initiator can also be added at the same time as the mono-vinyl aromatic monomer and multiple-vinyl aromatic monomers although preferably not through the same port. Initiators may be those described above.
After addition of the initiator or concurrently with the addition of the initiator the mono-vinyl aromatic monomer and multiple-vinyl aromatic monomer are added to the same reaction vessel that the liquid polymer was formed in. The initiator encourages the mono-vinyl aromatic monomer to copolymerize with the unterminated polymer chains left over from the liquid polymer process to form a copolymer. This occurs through an anionic, living polymerization. The copolymer chains then self-assemble in the hydrocarbon solvent into micelles. The multiple-vinyl aromatic monomer serves to cross-link the micelles holding them together as nanoparticles.
In one example, the copolymers are di-block copolymers comprising a polyconjugated diene block and a mono-vinyl aromatic block, such as block styrene-butadiene. The mono-vinyl aromatic blocks are typically crosslinked by the multiple-vinyl aromatic monomer. The polymer nanoparticles preferably retain their discrete nature with little or no polymerization between each other. In some embodiments, the nanoparticles are substantially monodisperse and uniform in shape, in others the nanoparticles have a polymodal size distribution.
The copolymerization of the nanoparticle chains may last as long as necessary until the desired monomer conversion, degree of polymerization (DP), and block polymer molecular weight are obtained. The polymerization reaction of this step may last typically from about 0.5 hours to about 20 hours, preferably from about 0.5 hours to about 10 hours, more preferably from about 0.5 hours to about 5 hours. The polymerization reaction of this step may be conducted at a temperature of from about 30� F. to about 300� F., preferably from about 100� F. to about 250� F., and more preferably from about 150� F. to about 210� F.
The polymerization reactions used to prepare the polymer nanoparticles may be terminated with a terminating agent. Suitable terminating agents include, but are not limited to, alcohols such as methanol, ethanol, propanol, and isopropanol. In exemplified embodiments, the polymerization reaction mixture was cooled and dropped in an isopropanol/acetone solution containing an antioxidant such as butylated hydroxytoluene (BHT). The isopropanol/acetone solution may be prepared, for example, by mixing 1 part by volume of isopropanol and 4 parts by volume of acetone.
To terminate the polymerization of the nanoparticle chains, and thus control polymer molecular weight, a functional terminating agent may be employed to provide terminal functionality. Exemplary functional terminating agents include, but are not limited to, SnCl4, R3SnCl, R2SnCl2, RSnCl3, carbodiimides, N-methylpyrrolidine, cyclic amides, cyclic ureas, isocyanates, Schiff bases, 4,4′-bis(diethylamino)benzophenone, N,N′-dimethylethyleneurea, and mixtures thereof, wherein R is selected from the group consisting of alkyls having from about 1 to about 20 carbon atoms, cycloalkyls having from about 3 to about 20 carbon atoms, aryls having from about 6 to about 20 carbon atoms, aralkyls having from about 7 to about 20 carbon atoms, and mixtures thereof.
In an example, a liquid hydrocarbon medium serves as a dispersion solvent and facilitates the formation of the micelle-like nanoparticles. This hydrocarbon solvent is added in the liquid polymer polymerization step and if necessary more may be added with the nanoparticle polymerization charge. The liquid hydrocarbon may be selected from any suitable aliphatic hydrocarbons, alicyclic hydrocarbons, or mixture thereof, with a proviso that it exists in liquid state during the nanoparticles' formation procedure. Exemplary aliphatic hydrocarbons include, but are not limited to, pentane, isopentane, 2,2 dimethyl-butane, hexane, heptane, octane, nonane, decane, and the like. Exemplary alicyclic hydrocarbons include, but are not limited to, cyclopentane, methyl cyclopentane, cyclohexane, methyl cyclohexane, cycloheptane, cyclooctane, cyclononane, cyclodecane, and the like. In one embodiment, the liquid hydrocarbon medium comprises hexane.
The liquid polymer that is present in the batch can also be considered a solvent. The liquid polymer also aids in dispersion by intercalating itself between the living polymer chains when they are in the micelle formation. This helps to isolate the inside of the nanoparticle from the solvent. Consequently, this causes the micelle to be more stable and decreases the chances of two or more micelles meeting each other and potentially linking, which would result in the creation of much larger particles. The liquid polymer causes the nanoparticle to swell, and the resulting mixture is softer and more easily mixed into rubber compounds.
Without being bound to any particular theory, it is believed that the poly(conjugated diene) block is more soluble or miscible in a selected liquid solvent, such as hexane, than the mono-vinyl aromatic block. This facilitates the subsequent micelle-like assembling and nanoparticle formation from the block copolymer chains.
Depending on their miscibility, polymer chains in solution or suspension system can be self-assembled into domains of various structures. Without being bound to any theory, it is believed that a micelle-like structure may be formed by aggregating the block copolymer chains comprising the poly(conjugated diene) block and the aromatic block. The mono-vinyl aromatic blocks are typically directed toward the center of the micelle and the poly(conjugated diene) blocks are typically extended away from the center.
The polymer nanoparticles are formed from the cross-linked micelle-like structures with a core made from the mono-vinyl aromatic blocks, and a shell made from the poly(conjugated diene) blocks. It is believed that the multiple-vinyl aromatic monomers crosslink the center core of the micelle to stabilize and hold together the polymer nanoparticles.
In an alternative example, the nanoparticle polymerization step may be conducted in the presence of a modifier or a 1,2-microstructure controlling agent, so as to, for example, increase the reaction rate, equalize the reactivity ratio of monomers, and/or control the 1,2-microstructure in the conjugated diene monomers. Suitable modifiers include, but are not limited to, triethylamine, tri-n-butylamine, hexamethylphosphoric acid triamide, N,N, N′,N′-tetramethylethylene diamine, ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, tetrahydrofuran, 1,4-diazabicyclo[2.2.2]octane, diethyl ether, tri-n-butylphosphine, p-dioxane, 1,2 dimethoxy ethane, dimethyl ether, methyl ethyl ether, ethyl propyl ether, di-n-propyl ether, di-n-octyl ether, anisole, dibenzyl ether, diphenyl ether, dimethylethylamine, bix-oxolanyl propane, tri-n-propyl amine, trimethyl amine, triethyl amine, N,N-dimethyl aniline, N-ethylpiperidine, N-methyl-N-ethyl aniline, N-methylmorpholine, tetramethylenediamine, oligomeric oxolanyl propanes (OOPs), 2,2-bis-(4-methyl dioxane), bistetrahydrofuryl propane, and the like.
Specific examples of modifiers or 1,2-microstructure controlling agents include, but are not limited to, oligomeric oxolanyl propanes (OOPs); 2,2-bis-(4-methyl dioxane); bis(2-oxolanyl)methane; 1,1-bis(2-oxolanyl)ethane; bistetrahydrofuryl propane; 2,2-bis(2-oxolanyl) propane; 2,2-bis(5-methyl-2-oxolanyl)propane; 2,2-bis-(3,4,5-trimethyl-2-oxolanyl)propane; 2,5-bis(2-oxolanyl-2-propyl)oxolane; octamethyl perhydrocyclotetrafurfurylene (cyclic tetramer); 2,2-bis(2-oxolanyl)butane; and the like. A mixture of two or more modifiers or 1,2-microstructure controlling agents also can be used.
The synthesized liquid polymer that results from the liquid polymerization process comprises a homopolymer of conjugated diene monomers or a copolymer of conjugated diene monomers with, for example, vinyl aromatic monomers and/or trienes such as myrcene, among others. As used herein, liquid polymers of conjugated diene monomers include not only polymers of the same conjugated diene monomers such as a liquid poly(butadiene), but also include copolymers of one or more conjugated diene monomers with other monomers; for example, isoprene-butadiene rubber or styrene-butadiene rubber.
The conjugated diene monomer may be one or more of conjugated diene monomers. C4-C8 conjugated diene monomers of formula (I) are the most preferred. Specific examples of the conjugated diene monomers include, but are not limited to, 1,3-butadiene, isoprene (2-methyl-1,3-butadiene), cis- and trans-piperylene (1,3-pentadiene), 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, cis- and trans-1,3 hexadiene, cis- and trans-2-methyl-1,3-pentadiene, cis- and trans-3-methyl-1,3-pentadiene, 4-methyl-1,3-pentadiene, 2,4-dimethyl-1,3-pentadiene, and the like, and the mixture thereof. In preferred embodiments, isoprene or 1,3-butadiene or mixtures thereof is used as the conjugated diene monomer(s).
The number average molecular weight (Mn) of the liquid polymer is preferably controlled (e.g. by controlling the ratio of monomers to initiator) within the range of from about 10,000 to about 120,000, within the range of from about 20,000 to about 110,000, or within the range of from about 25,000 to about 100,000. The weight average molecular weight of the liquid polymer can range from about 20,000 to 100,000, for example 70,000 to 90,000.
The glass transition temperature (Tg) of the liquid polymer is, for example, within the range of from about −90� C. to about −20� C., such as within the range of from about −90� C. to about −40� C., or from about −90� C. to about −50� C. The liquid polymer may exhibit only one glass transition temperature.
When the synthesized liquid polymer is a copolymer of conjugated diene monomer(s), the comonomer may be vinyl aromatic monomer selected from the group consisting of styrene, ethylvinylbenzene, a-methyl-styrene, 1-vinyl naphthalene, 2-vinyl naphthalene, vinyl toluene, methoxystyrene, t-butoxystyrene, and the like; as well as alkyl, cycloalkyl, aryl, alkaryl, and aralkyl derivatives thereof, in which the total number of carbon atoms in the monomer is generally not greater than about 20; and mixtures thereof. In exemplary embodiments, the conjugated diene monomer and vinyl aromatic monomer are normally used at the weight ratios of about 99:1 to about 1:99, or about 30:70 to about 90:10, or preferably about 85:15 to about 60:40.
The liquid polymer may comprise polyisoprene, polybutadiene, styrene-butadiene copolymer, styrene-isoprene-butadiene copolymer, styrene-isoprene copolymer, butadiene-isoprene copolymer, liquid butyl rubber, liquid neoprene, ethylene-propylene copolymer, ethylene-propylene-diene copolymer, acrylonitrile-butadiene copolymer, liquid silicone, ethylene acrylic copolymer, ethylene vinyl acetate copolymer, liquid epichlorohydrin, liquid chlorinated polyethylene, liquid chlorosulfonated polyethylene rubbers, liquid hydrogenated nitrile rubber, liquid tetrafluoroethylene-propylene rubber, liquid hydrogenated polybutadiene and styrene-butadiene copolymer, and the like, and the mixture thereof.
In one example the liquid polymer is a styrene-butadiene copolymer. The styrene-butadiene has an Mw of about 80,000 to 120,000 and is comprised of repeat units that are derived from about 5 weight percent to about 95 weight percent styrene and correspondingly from about 5 weight percent to about 95 weight percent 1,3-butadiene, wherein the repeat units derived from styrene and 1,3-butadiene are in essentially random order. In this example, in the liquid polymerization process of the illustrative methods, the first monomer is styrene and the second monomer is butadiene. Vinyl percentages of 50-60% are preferred for some applications because this range is easy to achieve synthetically with styrene as the monomer. However, lower vinyl levels are also possible.
In another example, the liquid polymer comprises a liquid isoprene-butadiene rubber (IBR) with Mw of about 35,000 to 70,000, which is comprised of repeat units that are derived from about 5 weight percent to about 95 weight percent isoprene and correspondingly from about 5 weight percent to about 95 weight percent 1,3-butadiene, wherein the repeat units derived from isoprene and 1,3-butadiene are in essentially random order. In this example, the first monomer is isoprene and the second monomer is butadiene according to the illustrative methods described above.
The polymer nanoparticles synthesized in the one-batch methods described herein include a vulcanizable shell and a crosslinked core. The monomers that comprise the shell may be curable by vulcanization by sulfur or peroxide. Examples of suitable sulfur vulcanizing agents include “rubber maker's” soluble sulfur; elemental sulfur (free sulfur); sulfur donating vulcanizing agents such as organosilane polysulfides, amine disulfides, polymeric polysulfides or sulfur olefin adducts; and insoluble polymeric sulfur. Related prior patents and publications U.S. Pat. No. 6,437,050 (Bridgestone Corp.) and Macromol. Symp. 118, 143-148 (1997) disclose some suitable sulfur vulcanizing agents.
The monomers that make up the shell comprise the unterminated polymer chains left over from the polymerization of the liquid polymer.
In a variety of exemplary embodiments, the shell may be made up of any suitable conjugated diene or mixture thereof. C4-C8 1,3-conjugated diene monomers are the most preferred.
In a variety of exemplary embodiments, specific examples of the shell monomers include, but are not limited to, 1,3-butadiene, isoprene (2-methyl-1,3-butadiene), cis- and trans-piperylene(1,3-pentadiene), 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, cis- and trans-1,3-hexadiene, cis- and trans-2-methyl-1,3-pentadiene, cis- and trans-3-methyl-1,3-pentadiene, 4-methyl-1,3-pentadiene, 2,4-dimethyl-1,3-pentadiene, and the like, and the mixture thereof. In preferred embodiments, isoprene or 1,3-butadiene or mixture thereof is used as the shell monomer.
The crosslinked core of the nanoparticles is typically produced from mono-vinyl aromatic monomers cross-linked with multiple-vinyl aromatic monomers. The weight ratio between the mono-vinyl aromatic monomers and multiple-vinyl aromatic monomers may broadly range from about 95:5 to about 0:100, from about 90:10 to about 25:75, or from about 85:15 to about 60:40.
Compounds that comprise a conjugated vinyl group and a conjugated aromatic group may be used as the mono-vinyl aromatic monomer. Suitable mono-vinyl aromatic monomers include, but are not limited to styrene, ethylvinylbenzene, (X-methyl-styrene, 1-vinyl naphthalene, 2-vinyl naphthalene, vinyl toluene, methoxystyrene, t-butoxystyrene, and the like; as well as alkyl, cycloalkyl, aryl, alkaryl, and aralkyl derivatives thereof in which the total number of carbon atoms in the monomer is generally not greater than about 18; and mixtures thereof. In exemplified embodiments, the mono-vinyl aromatic monomer comprises styrene.
Any compound that comprises two or more conjugated vinyl groups and a conjugated aromatic group may be used as the multiple-vinyl aromatic monomer. Suitable multiple-vinyl aromatic monomers include, but are not limited to compounds with a general formula as shown below:
The DVB may be selected from any one of the following isomers or any combination thereof:
The polymer nanoparticle synthesized in the one-batch methods described herein may take the shape of nano-spheres. The mean diameter of the spheres may be broadly within the range of from about 1 to about 200 nm, within the range of from about 5 nm to about 100 nm, within the range of from about 10 nm to about 80 nm, or within the range of from about 15 nm to about 70 nm.
The average molecular weight Mn of the poly(conjugated diene) block of the shell portion may be controlled within the range of from about 5,000 to about 500,000, or within the range of from about 5,000 to about 200,000, and most preferably within the range of from about 10,000 to about 100,000. The average molecular weight Mn of the uncrosslinked aromatic block may be controlled within the range of from about 5,000 to about 500,000, within the range of from about 5,000 to about 200,000, or within the range of from about 10,000 to about 100,000.
The number average molecular weight (Mn) of the entire polymer nano-particle may be controlled within the range of from about 10,000 to about 10,000,000, within the range of from about 50,000 to about 1,000,000, or within the range of from about 100,000 to about 500,000. The polydispersity (the ratio of the weight average molecular weight to the number average molecular weight) of the polymer nano-particle may be controlled within the range of from about 1 to about 1.5, within the range of from about 1 to about 1.3, or within the range of from about 1 to about 1.2.
The Mn may be determined by GPC with a polystyrene standard. The Mn values used in the examples below were measured by GPC methods calibrated with linear polymers.
In one example, the core of the synthesized nanoparticles is relatively hard. That is, the core has a Tg of about 60� C. or higher. In another example, the nanoparticles have a core that is relatively harder than the shell, for example, at least about 60� C. higher than the Tg of the shell layer. In one example, the shell layer is soft. That is, the shell layer has a Tg lower than about 0� C. Preferably, the Tg of the shell layer is between about 0� C. and about −70� C. Nanoparticles with hard cores and soft shells are particularly useful for reinforcing rubber compounds used for tire treads.
As known by those of skill in the art, the Tg of the polymers can be controlled by the selection of monomers and their molecular weight, styrene content, and vinyl content.
An illustrative composition comprising a liquid polymer/nanoparticle blend also includes (a) a rubber matrix, (b) an optional oil, and (c) one or more components selected from the group consisting of carbon black, silica, vulcanizing agent, vulcanization accelerator, tackifier resin, antioxidant, fatty acids, zinc oxide, wax, peptizer, vulcanization retarder, activator, processing additive, plasticizer, pigments, and antiozonant. Various rubber products such as tires and power belts may be manufactured based on this composition.
The nanoparticle and liquid polymer blend may be compounded with rubber by methods generally known in the rubber compounding art, such as mixing the rubbery matrix polymer and the nanoparticle/liquid polymer blend with conventional amounts of various commonly used additive materials, using standard rubber mixing equipment and procedures.
A vulcanized rubber product may be produced from the composition of the present invention by thermomechanically mixing the liquid polymer nanoparticle blend, a rubbery matrix polymer, and conventional amounts of various commonly used additive materials in a sequentially step-wise manner in a rubber mixer, followed by shaping and curing the composition. Rubber articles such as tires may be manufactured from the composition made with the liquid polymer/nanoparticle blend described supra. Reference for this purpose may be made to, for example, U.S. Publication No. 2004/0143064 A1, which is hereby incorporated by reference.
A rubbery matrix that the nanoparticle liquid polymer blend is used in may comprise any solution polymerizable or emulsion polymerizable elastomer, for example, diene homopolymers, and copolymers and terpolymers of conjugated diene monomers with vinyl aromatic monomers and trienes such as myrcene. Exemplary diene homopolymers are those prepared from diolefin monomers having from 4 to about 12 carbon atoms. Exemplary vinyl aromatic polymers are those prepared from monomers having from 8 to about 20 carbon atoms. Examples of such monomers may be referred to the monomers for the polymer nanoparticle formation as described supra. In certain exemplary embodiments, the conjugated diene monomer and vinyl aromatic monomer are normally used at the weight ratios of about 1:99 to about 99:1, or about 15:85 to about 85:15. The rubbery matrix can have 1,2-microstructure contents ranging from about 1 percent to about 99 percent, or polymers, copolymers or terpolymers having 1,2-microstructure content of from about 1 to 99 percent, based upon the diene content of the rubbery matrix. The copolymers are preferably random copolymers which result from simultaneous copolymerization of the monomers with randomizing agents, as is known in the art.
The amount of initiator employed will vary with the desired molecular weight of the rubbery matrix polymer being synthesized. Higher molecular weights are achieved by utilizing smaller quantities of the initiator and lower molecular weights are attained by employing larger quantities of the initiator. The molecular weight of the rubbery polymer produced is, of course, also dependent upon the amount of chain transfer agent, such as t-dodecyl mercaptan, present during the polymerization. For instance, low molecular weight rubbery polymers can be synthesized by simply increasing the level of chain transfer agent.
Oil has been conventionally used as a compounding aid in rubber compositions. Examples of oil include, but are not limited to, aromatic, naphthenic, and/or paraffinic processing oils. In some examples, it may be preferable to use low-polycyclic-aromatic (PCA) oils, particularly oils that have a PCA content of less than 3%. In a variety of exemplary embodiments, the liquid polymer portion of the blend described above is used along with the oil, is used to replace a portion of the oil, or is used to replace the entirety of the oil in a rubber compound. As such, a typical amount of oil may broadly range from about 0 phr to about 100 phr, from about 0 phr to about 70 phr, or from about greater than 0 phr to about 50 phr, based on 100 phr rubbery matrix in the rubber composition.
As a skilled artisan can appreciate, reinforcement of a rubber product may be reflected by a low strain dynamic modulus G′, as can be measured according to ASTM-D 412 at 22� C. In a variety of exemplary embodiments, reinforcement of rubber products such as tires made from the composition of the present invention may be achieved by (i) incorporation of the liquid polymer/nanoparticle blend; (ii) partially replacing the oil with the liquid polymer/nanoparticle blend; or (iii) entirely replacing the oil with the liquid polymer/nanoparticle blend.
The nanoparticle/liquid polymer blend provides various rubber products with improved reinforcement and controllable hysteresis. By controllable hysteresis, it is meant that the hysteresis is increased or decreased, or remains roughly unchanged, comparing to the situation where oil is present in the composition, but no liquid polymer and no polymer nanoparticles are included in the composition. For example, G′(MPa) may be increased at least about 0.3, preferably at least about 1.5, and more preferably at least 3.0.
The energy loss of an elastomer is termed hysteresis, which refers to the difference between the energy applied to deform an article made from the elastomer and the energy released as the elastomer returns to its initial and undeformed state. Hysteresis is characterized by a loss tangent, tangent delta (tan δ), which is a ratio of the loss modulus to the storage modulus (i.e., the viscous modulus to the elastic modulus) as measured under an imposed sinusoidal deformation. The tan δ value can be measured, for example, with a TA Instrument AIRES Rheometer.
Rubber products with improved reinforcement and suitable hysteresis may be manufactured with the nanoparticle/liquid polymer blend, in which the phr ratio between the component (a) liquid polymer and component (b) polymer nanoparticles is within the range of from about 1:99 to about 99:1, preferably within the range of from about 20:80 to about 80:20, more preferably within the range of from about 25:75 to about 40:60.
The illustrative rubber compositions described herein can be used for various purposes. For example, they can be used for various rubber compounds, such as a tire treadstock, sidewall stock or other tire component stock compounds. Such tires can be built, shaped, molded and cured by various methods that are known and will be readily apparent to those having skill in the art. In an embodiment, a molded unvulcanized tire is charged into a vulcanizing mold and then vulcanized to produce a tire, based on the composition and the procedure as described above.
Preparation of Nanoparticle and Liquid Polymer Blend
A two-gallon jacketed reactor was used as the reaction vessel. The following ingredients were used: 19.3% butadiene in hexane, 33% styrene in hexane, hexane, n-butyl lithium (1.6 M), oligomeric oxalanyl propane (1.6 M) (OOPs), isopropanol, butylated hydroxytoluene (BHT), and 80% divinylbenzene (DVB) purchased from Aldrich.
The reactor was sequentially charged with 4.96 lbs of hexane, 0.59 lbs of 33% styrene, and 3.58 lbs of 19.3% butadiene. This batch was heated to 120� F. over about 15 minutes. When the batch reached 117� F., 2.3 mL of n-butyl lithium (1.6 M) and 0.76 mL of OOPs (1.6 M), diluted with about 20 mL of hexane were added. The polymerization exothermed at 126.7� F. after three minutes of reaction. After one hour, the jacket of the reactor was set to 100� F. and 0.14 mL of isopropanol was added. After dropping a sample for analysis, some additional n-butyl lithium (2.3 mL) was added to the reactor. A mixture of 140.2 g styrene blend and 28.5 mL of DVB was prepared in a bottle and added to the reactor. The jacket temperature of the reactor was increased to 180� F. After three hours of reaction, the temperature was brought down to 90� F. and the mixture was dropped in isopropanol containing BHT. The resulting solid was then filtered through cheesecloth and drum dried.
The liquid polymer portion was determined to have an Mw of 73000 to 80000. The nanoparticle portion was determined to have a Mw of 83,700. The synthesized blend contained 55 wt % the liquid polymer and 45 wt % the nanoparticles, as determined by GPC.
The nanoparticle/liquid polymer blend was much easier to isolate from solvent and dry than previously known methods of separately synthesizing the liquid polymer. Coagulated liquid polymer is very difficult to separate from the solvent, the solvent must be carefully dropped out and it cannot easily be drum-dried. It may even be necessary to use a vacuum-oven to dry it, while being careful not to let the liquid polymer flow over. However, with a sufficent amount of nanoparticles in the liquid polymer blend, it produces a chunk of polymer after coagulation, which can be drum-dried very easily.
Preparation and Analysis of Example Rubber Compounds
Three rubber compositions were prepared according to the formulation shown in Tables 1 and 2. The first example was a control that contained no nanoparticles or liquid polymer to serve as a comparison with the test compounds. The second example was made using synthesized nanoparticles to replace 10 phr of styrene-butadiene rubber (SBR) in the compound formulation. The third example was made using nanoparticles and liquid polymer to replace 10 phr of SBR and about 15 phr of aromatic oil. Because the synthesized MNP/LP blend contained 55 wt % of the liquid polymer and 45 wt % of the nanoparticles, 22.2 phr of the MNP/LP blend and 2.8 phr of additional LP were used in the formulation in order to correctly match the desired composition.
To illustrate that the additional amount of LP is not a necessary component of the examples described herein, a fourth prophetic example is also presented. In the prophetic example 4, 25 phr of 40:60 MNP/LP blend is used. This prophetic example replaces the 10 phr of SBR with 10 phr of blended MNP and replaces the 15 phr of LP with 15 phr of blended LP without using additional LP by itself.
Composition of Example Master Batches (in phr)
SBR1 100
(tackifiers)
Nanoparticles (100 wt %
MNP)
Liquid Polymer/Nanoparticle2 0
Liquid Polymer/Nanoparticle3 0
1Trade Name HX263 from Firestone Polymers (Mw of 261 kg/mol, Mw/Mn of 2.30, 23.8% styrene by weight, 35% cis 1,4, 52% trans 1,4, and 13% 1,2 vinyl)
245% nanoparticles and 55% liquid polymer
340% nanoparticles and 60% liquid polymer
Additional Additives to Final Batch Composition (in phr)
Cyclohexyl-
In each example, a blend of the ingredients was kneaded by the method listed in Table 3. The final stock was sheeted and molded at 165� C. for 15 minutes.
drop sample for analysis
1.25 min Drop sample for analysis
Analysis of Examples
Ring Tensile Strength
Tensile Break Stress
23� C. Tb (MPa)
(Eb %)
(M300)
(M50)
Tg of Compound
−45� C.
−43� C.
−40� C.
(extropolated from
tan δ)
tan δ 50� C.
G′(Pa � 10−6)
Measurement of the tensile strength and hysteresis loss were taken of the example vulcanized rubber compositions. The results are shown in Table 4. Measurement of tensile strength was performed according ASTM-D 412 at 22� C. The test specimen geometry was in the form of a ring of a width of 0.05 inches and of a thickness of 0.075 inches. The specimen was tested at a specific gauge length of 1.0 inch. Hysteresis loss was measured with a Dynastat Viscoelastic Analyzer set at a frequency of 1 Hz and 1% strain. The geometry of the specimen for this test was a cylinder of a length of 15 mm and a diameter of 10 mm.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS2531396Mar 29, 1947Nov 28, 1950Nat Lead CoElastomer reinforced with a modified clayUS3598884Jul 12, 1968Aug 10, 1971Polymer CorpCross-linking of polymersUS3793402Nov 5, 1971Feb 19, 1974F OwensLow haze impact resistant compositions containing a multi-stage,sequentially produced polymerUS3840620Aug 19, 1971Oct 8, 1974Stauffer Chemical CoAdditives for the preparation of clear,impact resistant vinyl chloride polymer compositionsUS3972963Jul 18, 1975Aug 3, 1976Mobil Oil CorporationOrganic reinforcing fillers for rubberUS4075186Jan 21, 1976Feb 21, 1978The Firestone Tire & Rubber CompanyGraft copolymers of polybutadiene and substituted polyacrylateUS4233409Jul 5, 1979Nov 11, 1980Monsanto CompanyPolymeric blendUS4247434Dec 29, 1978Jan 27, 1981Lovelace Alan M AdministratorProcess for preparation of large-particle-size monodisperseUS4248986Aug 27, 1979Feb 3, 1981The Goodyear Tire & Rubber CompanySelective cyclization of block copolymersUS4326008Apr 25, 1980Apr 20, 1982California Institute Of TechnologyProtein specific fluorescent microspheres for labelling a proteinUS4386125Feb 18, 1982May 31, 1983Asahi Kasei Kogyo Kabushiki KaishaFilm, sheet or tube of a block copolymer or a composition containing the sameUS4463129Nov 23, 1981Jul 31, 1984Toa Nenryo Kogyo Kabushiki KaishaProcess for improving adhesion of rubbery polymers by reacting with silanes in two stagesUS4471093Feb 28, 1983Sep 11, 1984Sumimoto Rubber Industries, Ltd.Elastomer composition comprising a blend of SBR rubbersUS4543403Mar 9, 1984Sep 24, 1985Kanegafuchi Kagaku Kogyo Kabushiki KaishaCurable compositionUS4598105Sep 17, 1984Jul 1, 1986Amoco CorporationRubber composition and methodUS4602052Sep 17, 1984Jul 22, 1986Amoco CorporationRubber composition and method of incorporating carbon black and a quaternary ammonium coupling agent salt into natural rubber containing compositionsUS4659790Apr 18, 1985Apr 21, 1987Japan Synthetic Rubber Co., Ltd.Heat-resistant copolymer of alpha-methylstyrene and acrylonitrile, process for preparing the same, and thermoplastic resin composition containing the sameUS4717655Oct 15, 1984Jan 5, 1988Becton, Dickinson And CompanyMethod and apparatus for distinguishing multiple subpopulations of cellsUS4725522Oct 16, 1986Feb 16, 1988Xerox CorporationProcesses for cold pressure fixable encapsulated toner compositionsUS4764572Jul 23, 1985Aug 16, 1988Shell Oil CompanyAnionic polymerization processUS4773521Jul 23, 1987Sep 27, 1988Chen Ming ChinCompact portable conveyorUS4774189Dec 11, 1985Sep 27, 1988Flow Cytometry Standards Corp.Fluorescent calibration microbeads simulating stained cellsUS4788254Jul 13, 1987Nov 29, 1988Kanegafuchi Chemical Industry, Co., Ltd.Curable polymer compositionUS4829130Jul 17, 1987May 9, 1989Enichem Sintesi S.P.A.Silylated derivatives of isobutene crosslinkable under ambient conditions, and process for preparing themUS4829135Dec 29, 1987May 9, 1989Mobil Oil CorporationMulti-stage anionic dispersion homopolymerization to form microparticles with narrow size distributionUS4837274Sep 29, 1987Jun 6, 1989Kanegafuchi Kagaku Kogyo Kabushiki KaishaCurable compositionUS4837401Dec 11, 1985Jun 6, 1989Kanegafuchi Chemical Industry, Co., Ltd.Curable polymer composition comprising organic polymer having silicon-contaiing reactive groupUS4861131May 4, 1988Aug 29, 1989Sick-Optique-ElectroniqueDisplacement transducer with staggered optical fibresUS4870144Feb 19, 1988Sep 26, 1989Kanegafuchi Kagaku Kogyo Kabushiki KaishaProcess for producing an isobutylene polymer having functional terminal end groupsUS4871814Jun 22, 1987Oct 3, 1989Mobil Oil CorporationHigh impact, highly transparent linear styrene-diene block copolymers with five or more blocks and their preparations by anionic dispersion polymerizationUS4904730May 30, 1989Feb 27, 1990The Dow Chemical CompanyRubber-modified resin blendsUS4904732Jun 24, 1987Feb 27, 1990Kanegafuchi Kagaku Kogyo Kabushiki KaishaCurable isobutylene polymerUS4906695Jul 8, 1988Mar 6, 1990Dow Corning CorporationPressure-sensitive adhesives containing an alkoxy-functional silicon compoundUS4920160Jul 10, 1989Apr 24, 1990Tioxide Group PlcPolymeric particles and their preparationUS4942209Feb 14, 1989Jul 17, 1990Mobil Oil CorporationAnionic polymerization in high viscosity dispersing medium to form microparticles with narrow size distributionUS4987202Apr 14, 1987Jan 22, 1991Zeigler John MMethods for the synthesis of polysilanesUS5036138Oct 11, 1988Jul 30, 1991Shell Oil CompanyElastomeric compositions, process for the preparation thereof and tires containing themUS5066729Apr 9, 1990Nov 19, 1991Bridgestone/Firestone, Inc.Diene polymers and copolymers terminated by reaction with n-alkyl and n-aryl iminesUS5073498Mar 16, 1990Dec 17, 1991Caribbean Microparticles CorporationFluorescent alignment microbeads with broad excitation and emission spectra and its useUS5075377Jun 22, 1990Dec 24, 1991Nippon Zeon Co., Ltd.Block copolymer compositionUS5120379Oct 16, 1989Jun 9, 1992Kanegafuchi Kagaku Kogyo Kabushiki KaishaSealant for double-layered glassUS5130377Feb 6, 1991Jul 14, 1992Phillips Petroleum CompanyTapered block styrene/butadiene copolymersUS5169914Apr 1, 1992Dec 8, 1992Edison Polymer Innovation CorporationUniform molecular weight polymersUS5194300Nov 8, 1989Mar 16, 1993Cheung Sau WMethods of making fluorescent microspheresUS5219945Feb 20, 1992Jun 15, 1993E. I. Du Pont De Nemours And CompanyABC triblock methacrylate polymersUS5227419Dec 20, 1990Jul 13, 1993Phillips Petroleum CompanyTapered block styrene/butadiene copolymersUS5237015Nov 4, 1991Aug 17, 1993Polysar Rubber CorporationCore-shell polymer for use in tire treadsUS5241008Sep 3, 1991Aug 31, 1993Bridgestone/Firestone, Inc.Process for producing continuously tapered polymers and copolymers and products produced therebyUS5247021Aug 27, 1992Sep 21, 1993Kanegafuchi Kagaku Kogyo Kabushiki KaishaProcess for preparation of a polymer having reactive terminal groupUS5256736May 8, 1991Oct 26, 1993Phillips Petroleum CompanyTapered block copolymers of conjugated dienes and monovinylarenesUS5262502Oct 9, 1992Nov 16, 1993Kanegafuchi Chemical Industry Co., Ltd.Isobutylene base polymer having functional group and process for preparing the sameUS5290873Apr 15, 1991Mar 1, 1994Kanegafuchi Chemical Industry Co., Ltd.Isobutylene polymer having unsaturated group and preparation thereofUS5290875Nov 30, 1992Mar 1, 1994Phillips Petroleum CompanyConjugated diene/monovinylarene block copolymers with multiple tapered blocksUS5290878Jun 7, 1993Mar 1, 1994Sumitomo Chemical Company, LimitedButadiene copolymer and process for preparing sameUS5296547Jan 28, 1993Mar 22, 1994Minnesota Mining And Manufacturing CompanyBlock copolymer having mixed molecular weight endblocksUS5329005Oct 2, 1992Jul 12, 1994Bridgestone CorporationSoluble anionic polymerization initiators and preparation thereofUS5331035Dec 22, 1992Jul 19, 1994Bridgestone CorporationProcess for the preparation of in situ dispersion of copolymersUS5336712Mar 23, 1993Aug 9, 1994Shell Oil CompanyProcess for making submicron stable latexes of block copolymersUS5362794Jul 21, 1993Nov 8, 1994Sumitomo Chemical Company, Ltd.Rubber composition having excellent gripping power and rolling resistance, and production thereofUS5395891Jun 14, 1993Mar 7, 1995Bayer AktiengesellschaftRubber mixtures containing polybutadiene gelUS5395902Jul 28, 1994Mar 7, 1995Bridgestone CorporationDispersion copolymerization in liquid aliphatic hydrocarbonsUS5399628Dec 2, 1993Mar 21, 1995Phillips Petroleum CompanyBlock copolymers of monovinylarenes and conjugated dienes containing two interior tapered blocksUS5399629Jul 29, 1994Mar 21, 1995Mobil Oil CorporationSolid elastomeric block copolymersUS5405903Mar 9, 1994Apr 11, 1995Shell Oil CompanyProcess for the preparation of a block copolymer blendUS5421866May 16, 1994Jun 6, 1995Dow Corning CorporationWater repellent compositionsUS5436298Sep 19, 1994Jul 25, 1995Phillips Petroleum CompanyBlock copolymers of monovinylarenes and conjugated dienes and preparation thereofUS5438103Mar 23, 1994Aug 1, 1995Phillips Petroleum CompanyBlock copolymers of monovinylaromatic and conjugated diene monomersUS5447990Dec 13, 1994Sep 5, 1995Kanegaruchi Kagaku Kogyo Kabushiki KaishaMethod of preparing polymer containing functional groupUS5462994Jan 27, 1994Oct 31, 1995The Dow Chemical CompanyPreparation of conjugated diene-monoalkenyl arene block copolymers having a low polydispersity indexUS5514734Jul 10, 1995May 7, 1996Alliedsignal Inc.Polymer nanocomposites comprising a polymer and an exfoliated particulate material derivatized with organo silanes, organo titanates, and organo zirconates dispersed therein and process of preparing sameUS5514753Jun 30, 1994May 7, 1996Bridgestone CorporationProcess for preparing a block copolymerUS5521309Dec 23, 1994May 28, 1996Bridgestone CorporationTertiary-amino allyl-or xylyl-lithium initiators and method of preparing sameUS5525639Apr 26, 1994Jun 11, 1996Asahi Kasei Kogyo Kabushiki KaishaExpanded foamed bead of a rubber-modified styrene polymerUS5527870Jan 10, 1995Jun 18, 1996Kanagafuchi Kagaku Kogyo Kabushiki KaishaProcess for the preparation of isobutylene polymerUS5530052Apr 3, 1995Jun 25, 1996General Electric CompanyLayered minerals and compositions comprising the sameUS5580925Feb 28, 1990Dec 3, 1996Kanegafuchi Chemical Industry, Co., Ltd.Curable organic polymers containing hydrosilyl groupsUS5587423Oct 13, 1993Dec 24, 1996Basf AktiengesellschaftPreparation of block copolymers by ionic polymerizationUS5594072Aug 1, 1995Jan 14, 1997Shell Oil CompanyLiquid star polymers having terminal hydroxyl groupsUS5614579Dec 9, 1994Mar 25, 1997Bridgestone CorporationProcess for the preparation of tapered copolymers via in situ dispersionUS5627252Nov 30, 1995May 6, 1997Dow Corning S. A.Silyl group containing organic polymersUS5674592May 4, 1995Oct 7, 1997Minnesota Mining And Manufacturing CompanyFunctionalized nanostructured filmsUS5686528Feb 22, 1993Nov 11, 1997Rohm And Haas CompanyCore-shell impact modifiers for styrenic resinsUS5688856Dec 30, 1996Nov 18, 1997Shell Oil CompanyProcess for making submicron stable latexes of hydrogenated block copolymersUS5707439Dec 18, 1995Jan 13, 1998General Electric CompanyLayered minerals and compositions comprising the sameUS5728791Nov 14, 1995Mar 17, 1998Kanegafuchi Kagaku Kogyo Kabushiki KaishaPolyvinyl graft-polymers and manufacturing method thereofUS5733975Mar 31, 1997Mar 31, 1998Kanegafuchi Kagaku Kogyo Kabushiki KaishaPolyolefin resin composition, process for the preparation thereof and molded article made thereofUS5739267Mar 17, 1995Apr 14, 1998Kanegafuchi Kagaku Kogyo Kabushiki KaishaProcess for isolation of isobutylene polymerUS5742118Apr 20, 1994Apr 21, 1998Hitachi, Ltd.Ultrafine particle film, process for producing the same, transparent plate and image display plateUS5747152Dec 1, 1994May 5, 1998Dai Nippon Printing Co., Ltd.Transparent functional membrane containing functional ultrafine particles, transparent functional film, and process for producing the sameUS5763551Feb 29, 1996Jun 9, 1998Basf AktiengesellschaftProcess for preparing filterable polystyrene dispersionUS5773521Dec 19, 1995Jun 30, 1998Shell Oil CompanyCoupling to produce inside-out star polymers with expanded coresUS5777037Jan 16, 1996Jul 7, 1998Kanegafuchi Kagaku Kogyo Kabushiki KaishaProcess for producing isobutylene polymerUS5811501Jun 27, 1996Sep 22, 1998Kanegafuchi Kagaku Kogyo Kabushiki KaishaProcess for producing unsaturated group-terminated isobutylene polymerUS5834563May 6, 1997Nov 10, 1998Kaneka CorporationComposite rubber particles and graft copolymer particles of composite rubberUS5847054Jul 12, 1996Dec 8, 1998Basf AktiengesellschaftPolymer particles and their preparationUS5849847Jul 29, 1996Dec 15, 1998Fmc CorporationTelechelic polystyrene/polyethylene copolymers and processes for making sameUS5855972Nov 1, 1994Jan 5, 1999Kaeding; Konrad HSealant strip useful in the fabrication of insulated glass and compositions and methods relating theretoUS5883173Dec 20, 1996Mar 16, 1999Exxon Research And Engineering CompanyNanocomposite materials (LAW392)US5891947Oct 18, 1993Apr 6, 1999Bridgestone CorporationIn-situ anionic continuous dispersion polymerization processUS5905116May 6, 1998May 18, 1999Bridgestone CorporationGels derived from extending grafted α-olefin-maleimide centipede polymers and polypropyleneUS5910530May 19, 1997Jun 8, 1999Bridgestone CorporationHigh damping gel derived from extending grafted elastomers and polypropyleneUS5955537Feb 13, 1998Sep 21, 1999The Goodyear Tire & Rubber CompanyContinuous polymerization processUS5986010Jul 8, 1998Nov 16, 1999The Goodyear Tire & Rubber CompanyPolymer for asphalt cement modificationUS5994468May 6, 1998Nov 30, 1999Bridgestone CorporationHigh damping gels derived from nylon grafted polymersUS6011116Sep 29, 1997Jan 4, 2000Kaneka CorporationThermoplastic resin compositionUS6020446Feb 12, 1997Feb 1, 2000Kaneka CorporationCurable compositionUS6025416May 7, 1996Feb 15, 2000Henkel Teroson GmbhTwo-component adhesive/sealing mass with high initial adhesivenessUS6025445Nov 3, 1997Feb 15, 2000Kaneka CorporationCurable compoundUS6060549May 20, 1997May 9, 2000Exxon Chemical Patents, Inc.Rubber toughened thermoplastic resin nano compositesUS6060559Sep 4, 1998May 9, 2000Dow Corning CorporationCurable polyolefin compositions containing organosilicon compounds as adhesion additivesUS6087016Jun 8, 1998Jul 11, 2000Inmat, LlcBarrier coating of an elastomer and a dispersed layered filler in a liquid carrierUS6087456Nov 25, 1997Jul 11, 2000Kaneka CorporationCurable compositionUS6106953May 4, 1998Aug 22, 2000Beiersdorf AgUsing a cleaning cloth impregnated with coupling agent for adhesive filmsUS6117932Sep 17, 1998Sep 12, 2000Kabushiki Kaisha Toyota Chuo KenkyushoResin compositeUS6121379Nov 27, 1996Sep 19, 2000Kaneka CorporationProcesses for producing polymers having functional groupsUS6127488Jan 12, 1998Oct 3, 2000Bayer AgRubber mixtures which contain SBR rubber gelsUS6147151Nov 21, 1994Nov 14, 2000Sumitomo Rubber Industries LimitedTread rubber composition and tire using the compositionUS6166855Jun 7, 1999Dec 26, 2000Fuji Photo Film Co., Ltd.Anti-reflection film and display device having the sameUS6180693Sep 3, 1999Jan 30, 2001Vantico Inc.Core/shell particles, and curable epoxy resin composition comprising sameUS6191217Nov 17, 1998Feb 20, 2001Bridgestone CorporationGels derived from polypropylene grafted alkyl vinylether-maleimide copolymersUS6197849Feb 11, 1999Mar 6, 2001Vantico Inc.Organophilic phyllosilicatesUS6204354May 6, 1998Mar 20, 2001Bridgestone CorporationSoft compounds derived from polypropylene grafted disubstituted ethylene- maleimide copolymersUS6207263Jan 15, 1998Mar 27, 2001Dai Nippon Printing Co., Ltd.Anti-reflection film and process for preparation thereofUS6225394Jun 1, 1999May 1, 2001Amcol International CorporationIntercalates formed by co-intercalation of onium ion spacing/coupling agents and monomer, oligomer or polymer ethylene vinyl alcohol (EVOH) intercalants and nanocomposites prepared with the intercalatesUS6252014Aug 3, 1999Jun 26, 2001Colorado School Of MinesStar polymers and polymeric particles in the nanometer-sized range by step growth reactionsUS6255372Jan 8, 1999Jul 3, 2001Bridgestone CorporationTire components having improved tear strengthUS6268451Oct 3, 2000Jul 31, 2001University Of Massachusetts LowellSilyl-functional pseudo-telechelic polyisobutylene terpolymersUS6277304May 22, 2000Aug 21, 2001Drexel UniversityProcess for producing electroactive inorganic organic hybrid materialsUS6348546Feb 20, 2001Feb 19, 2002Kaneka CorporationAlkenyl-containing isobutylene group block copolymer and process for producing itUS6359075Jan 9, 2001Mar 19, 2002Bridgestone/Firestone, Inc.Means of producing high diblock content thermoplastic elastomers via chain transferUS6379791Feb 8, 2000Apr 30, 20023M Innovative Properties CompanyCompatibilized pressure-sensitive adhesivesUS6383500Jun 27, 1997May 7, 2002Washington UniversityParticles comprising amphiphilic copolymers, having a crosslinked shell domain and an interior core domain, useful for pharmaceutical and other applicationsUS6395829Feb 22, 2000May 28, 2002Kaneka CorporationAmorphous polyolefin resin compositionUS6420486May 22, 2000Jul 16, 2002Phillips Petroleum CompanyConjugated diene/monovinylarene block copolymers, methods for preparing same, and polymer blendsUS6437050Oct 4, 2001Aug 20, 2002Bridgestone CorporationNano-particle preparation and applicationsUS6441090Aug 7, 1998Aug 27, 2002The Dow Chemical CompanyHigh gloss high impact monovinylidene aromatic polymersUS6448353Feb 8, 2000Sep 10, 20023M Innovative Properties CompanyContinuous process for the production of controlled architecture materialsUS6489378Sep 14, 2000Dec 3, 2002Fina Technology, Inc.Method for the preparation of core-shell morphologies from polybutadiene-polystyrene graft copolymersUS6524595Jul 11, 2000Feb 25, 2003ColeticaCyclodextrins preferentially substituted on their primary face by acid or amine functionsUS6550508Nov 25, 1999Apr 22, 2003The Yokohama Rubber Co., Ltd.Rubber composition for tire tread having high performance on ice and pneumatic tire using the sameUS6573313Jan 16, 2001Jun 3, 2003The Hong Kong Polytechnic UniversityAmphiphilic core-shell latexesUS6573330Dec 10, 1998Jun 3, 2003Sumitomo Seika Chemicals, Co., Ltd.Process for preparing water-absorbent resinUS6598645Sep 27, 2000Jul 29, 2003The Goodyear Tire & Rubber CompanyTire with at least one of rubber/cord laminate, sidewall insert and apex of a rubber composition which contains oriented intercalated and/or exfoliated clay reinforcementUS6649702May 19, 2000Nov 18, 2003University Of Utah Research FoundationStabilization and acoustic activation of polymeric micelles for drug deliveryUS6663960Dec 22, 1999Dec 16, 2003Tokushu Paper Mfg. Co., Ltd.Fluorescent particles, method for preparing the same and paper preventing forgery using the fluorescent particleUS6689469Dec 31, 2001Feb 10, 2004Bridgestone CorporationCrystalline polymer nano-particlesUS6693746Sep 28, 2000Feb 17, 2004Fuji Photo Film Co., Ltd.Anti-glare and anti-reflection film, polarizing plate, and image display deviceUS6706813Dec 3, 2001Mar 16, 2004Kaneka CorporationCurable composition and method of use thereofUS6706823Dec 31, 2001Mar 16, 2004Bridgestone CorporationConductive gelsUS6727311Nov 15, 2001Apr 27, 2004The Goodyear Tire & Rubber CompanyLight weight rubber composition containing clayUS6737486Jul 16, 2002May 18, 2004Eastman Kodak CompanyPolymerization processUS6750297Dec 18, 2001Jun 15, 2004Lg Chem, Ltd.Artificial pigment and method for preparing the sameUS6759464Dec 21, 2001Jul 6, 2004The Goodyear Tire & Rubber CompanyProcess for preparing nanocomposite, composition and article thereofUS6774185Apr 4, 2002Aug 10, 2004Bridgestone CorporationMetal hydroxide filled rubber compositions and tire componentsUS6777500Dec 31, 2002Aug 17, 2004The Goodyear Tire & Rubber CompanyCore-shell polymer particlesUS6780937Aug 29, 2002Aug 24, 2004The Goodyear Tire & Rubber CompanyEmulsion particles as reinforcing fillersUS6835781Feb 23, 2001Dec 28, 2004Zeon CorporationBlock copolymer rubber, resin modifier, and resin compositionUS6858665Jul 2, 2001Feb 22, 2005The Goodyear Tire & Rubber CompanyPreparation of elastomer with exfoliated clay and article with composition thereofUS6861462Dec 21, 2001Mar 1, 2005The Goodyear Tire & Rubber CompanyNanocomposite formed in situ within an elastomer and article having component comprised thereofUS6872785Dec 30, 2002Mar 29, 2005Bridgestone CorporationMulti-layer nano-particle preparation and applicationsUS6875818Jan 16, 2003Apr 5, 2005Bridgestone CorporationPolymer nano-stringsUS6908958Mar 26, 2003Jun 21, 2005The Yokohama Rubber Co., Ltd.Organically modified layered clay as well as organic polymer composition and tire inner liner containing sameUS6956084Aug 19, 2002Oct 18, 2005Bridgestone CorporationNano-particle preparation and applicationsUS7056840Sep 30, 2003Jun 6, 2006International Business Machines Corp.Direct photo-patterning of nanoporous organosilicates, and method of useUS7071246Apr 13, 2004Jul 4, 2006The Goodyear Tire & Rubber CompanyRubber composition containing resinous nanopracticeUS7112369Mar 2, 2004Sep 26, 2006Bridgestone CorporationNano-sized polymer-metal compositesUS7179864Feb 22, 2005Feb 20, 2007Bridgestone CorporationPolymer nano-stringsUS7193004Jun 30, 2003Mar 20, 2007The Goodyear Tire & Rubber CompanyPneumatic tire having a component containing low PCA oilUS7205370Jan 12, 2004Apr 17, 2007Bridgestone CorporationPolymeric nano-particles of flower-like structure and applicationsUS7217775Apr 20, 2004May 15, 2007The Goodyear Tire & Rubber CompanyEmulsion particles as reinforcing fillersUS7238751Jun 29, 2005Jul 3, 2007Bridgestone Americas Holding, Inc.Multi-layer nano-particle preparation and applicationsUS7244783Jun 24, 2004Jul 17, 2007The Goodyear Tire & Rubber CompanyThermoplastic elastomer compositionUS7291394May 19, 2003Nov 6, 2007Merck Patent GmbhComposite material containing a core-covering particleUS7347237Feb 28, 2006Mar 25, 2008The Goodyear Tire & Rubber CompanyRubber composition containing resinous nanoparticleUS7408005Mar 5, 2005Aug 5, 2008The Goodyear Tire & Rubber CompanyHairy polymeric nanoparticlesUS20010053813Apr 30, 2001Dec 20, 2001Jsr CorporationRubber compositionsUS20020007011Apr 26, 2001Jan 17, 2002Jsr CorporationCrosslinked rubber particles and rubber compositionsUS20020045714Feb 10, 2001Apr 18, 2002Dow ChemicalNanocomposites of dendritic polymersUS20020095008Nov 28, 2001Jul 18, 2002Continental AktiengesellschaftRubber compound for tire tread rubberUS20020144401Feb 12, 2002Oct 10, 2002Airbus Espana, S.L.Method for manufacturing elements of composite materials by the co-bonding techniqueUS20030004250Nov 15, 2001Jan 2, 2003Manoj AjbaniLight weight rubber composition containing clayUS20030032710Jul 2, 2001Feb 13, 2003Larson Brent KevinElastomer composition which contains intercalated and exfoliated clay reinforcement formed in situ within the elastomer host and article, such as a tire, having at least one component thereofUS20030124353Dec 31, 2001Jul 3, 2003Bridgestone Corp.Crystalline polymer nano-particlesUS20030130401Oct 11, 2002Jul 10, 2003Lin Chenchy JeffreyTire compositions comprising epoxidized natural rubber and a functionalized polyolefinUS20030149185Dec 30, 2002Aug 7, 2003Bridgestone CorporationMulti-layer nano-particle preparation and applicationsUS20030198810Aug 19, 2002Oct 23, 2003Xiaorong WangNano-particle preparation and applicationsUS20030225190Apr 17, 2003Dec 4, 2003Janos BorbelyPolymeric product for film formationUS20040033345Aug 15, 2002Feb 19, 2004Benoit DubertretWater soluble metal and semiconductor nanoparticle complexesUS20040059057Aug 6, 2003Mar 25, 2004Chevron Phillips Chemical Company LpConjugated diene/monovinylarene block copolymers blendsUS20040091546Mar 29, 2002May 13, 2004Johnson Brian KProcess and apparatuses for preparing nanoparticle compositions with amphiphilic copolymers and their useUS20040127603Dec 31, 2002Jul 1, 2004The Goodyear Tire & Rubber CompanyCore-shell polymer particlesUS20040143064Jan 16, 2003Jul 22, 2004Bridgestone CorporationPolymer nano-stringsUS20040198917Apr 20, 2004Oct 7, 2004The Goodyear Tire & Rubber CompanyEmulsion particles as reinforcing fillersUS20050101743Nov 10, 2003May 12, 2005Stacy Nathan E.Monovinylarene/conjugated diene copolymers having lower glass transition temperaturesUS20050182158Sep 23, 2004Aug 18, 2005Torsten ZiserMicrogels in crosslinkable organic mediaUS20050192408Apr 13, 2005Sep 1, 2005Bridggestone CorporationNano-particle preparation and applicationsUS20050197462Feb 15, 2005Sep 8, 2005Bridgestone CorporationMulti-layer nano-particle preparation and applicationsUS20050203248Mar 5, 2005Sep 15, 2005Lei ZhengHairy polymeric nanoparticlesUS20050215693Mar 11, 2005Sep 29, 2005Xiaorong WangClay modified rubber composition and a method for manufacturing sameUS20050228072May 19, 2003Oct 13, 2005Holger WinklerComposite material containing a core-covering particleUS20050228074Apr 5, 2004Oct 13, 2005Bridgestone CorporationAmphiphilic polymer micelles and use thereofUS20050282956Jun 21, 2004Dec 22, 2005Xiaorong WangReversible polymer/metal nano-composites and method for manufacturing sameUS20060084722Apr 29, 2005Apr 20, 2006Bohm Georg G ASelf assembly of molecules to form nano-particlesUS20060173115Jan 28, 2005Aug 3, 2006Hiroyuki FudemotoNano-composite and compositions manufactured thereofUS20060173130Feb 3, 2005Aug 3, 2006Bridgestone CorporationPolymer nano-particle with polar core and method for manufacturing sameUS20060235128Dec 18, 2003Oct 19, 2006Xiaorong WangMethod for clay exfoliation, compositions therefore, and modified rubber containing sameUS20070027264Jun 29, 2005Feb 1, 2007Bridgestone CorporationMulti-Layer Nano-Particle Preparation and ApplicationsUS20070135579Dec 11, 2006Jun 14, 2007Lanxess Deutschland GmbhMicrogel-containing vulcanizable composition based on hydrogenated nitrile rubberUS20070142550Dec 16, 2005Jun 21, 2007Bridgestone CorporationCombined use of liquid polymer and polymeric nanoparticles for rubber applicationsUS20070142559Dec 16, 2005Jun 21, 2007Bridgestone CorporationNanoparticles with controlled architecture and method thereofUS20070149649Dec 19, 2006Jun 28, 2007Xiaorong WangNon-spherical nanoparticles made from living triblock polymer chainsUS20070161754Dec 20, 2006Jul 12, 2007Xiaorong WangNano-sized inorganic metal particles, preparation thereof, and application thereof in improving rubber propertiesUS20070185273Apr 9, 2007Aug 9, 2007Xiaorong WangPolymeric Nano-Particles Of Flower-Like Structure And ApplicationsUS20070196653Dec 20, 2006Aug 23, 2007Hall James EVulcanizable nanoparticles having a core with a high glass transition temperatureUS20080145660Dec 19, 2006Jun 19, 2008Xiaorong WangFluorescent NanoparticlesUS20080149238Dec 20, 2006Jun 26, 2008Kleckner James PRubber composition containing a polymer nanoparticleUS20080160305Jun 13, 2007Jul 3, 2008Bridgestone CorporationAmphiphilic polymer micelles and use thereofUS20080188579Dec 12, 2007Aug 7, 2008Xiaorong WangNanoporous polymeric material and preparation methodUS20080286374Dec 20, 2006Nov 20, 2008Xiaorong WangHollow nano-particles and method thereofUS20080305336Mar 13, 2008Dec 11, 2008Xiaorong WangReversible Polymer/Metal Nano-Composites And Method For Manufacturing SameUS20090048390Nov 16, 2007Feb 19, 2009Xiaorong WangNano-Particle Preparation And ApplicationsUS20090054554Oct 17, 2008Feb 26, 2009Xiaorong WangDisk-like NanoparticlesUS20090270558Dec 30, 2005Oct 29, 2009Michelin Recherche Et Technique S.A.Functionalized Polyvinylaromatic NanoparticlesUS20100004398Jul 27, 2007Jan 7, 2010Xiaorong WangPolymeric core-shell nanoparticles with interphase regionUS20100016472Jan 21, 2010Xiaorong WangRubber Composition Containing Functionalized Polymer NanoparticlesUS20100016512Sep 8, 2009Jan 21, 2010Xiaorong WangFluorescent NanoparticlesCA2127919A1Jul 13, 1994Mar 4, 1995Jessie Alvin BinkleyProcess for producing ultrafine sized latexesDE3434983C2Sep 24, 1984Oct 14, 1993Hoechst AgGelbildendes organophiles Schichtsilikat, Verfahren zu seiner Herstellung und VerwendungDE4241538A1Dec 10, 1992Jun 16, 1994Leuna Werke AgNon-equimolar alpha-methylstyrene/maleic anhydride copolymer(s) prodn. - by radical-initiated soln. copolymerisation in presence of organo-bromine cpds., esp. tetra-bromo-methane, or excess alpha-methylstyreneEP0143500B2Nov 22, 1984Jul 5, 2000The Dow Chemical CompanyRubber.reinforced polymers of monovinylidene aromatic compounds having a unique balance of gloss and physical strength properties and a method for their preparationEP0255170B1Jul 17, 1987Oct 31, 1990ENICHEM SYNTHESIS S.p.A.Silylated derivatives of isobutene crosslinkable under ambient conditions, and process for preparing themEP0265142B1Oct 13, 1987Dec 7, 1994Rohm And Haas CompanyCore-shell polymers and compositions containing core-shell polymersEP0265145B1Oct 13, 1987Dec 27, 1990Action Pumping Services LimitedHydro-pneumatic pumpsetsEP0322905A3Dec 28, 1988May 2, 1991ENICHEM S.p.A.Process for the imidization of copolymers of maleic anhydride and vinyl-aromatic monomersEP0352042B1Jul 14, 1989Mar 29, 1995Ube Industries, Ltd.High rigidity and impact resistance resin compositionEP0472344A2Aug 13, 1991Feb 26, 1992Ube Industries, Ltd.Reinforced elastomer composition and polypropylene composition containing sameEP0540942B1Oct 22, 1992May 1, 1996Bayer Rubber Inc.Core-shell polymer for use in tire treadsEP0590491B1Sep 22, 1993Jul 11, 2001Bridgestone CorporationSoluble anionic polymerization initiators and products therefromEP0742268B1May 7, 1996Jan 3, 2001Advanced Elastomer Systems, L.P.Thermoplastic elastomers having improved high temperature performanceEP1031605A1Feb 22, 2000Aug 30, 2000Kaneka CorporationAmorphous polyolefin resin compositionEP1099728B1May 28, 1999Feb 12, 2003Kaneka CorporationCurable compositionEP1134251B1Mar 7, 2001Oct 20, 2004Kaneka CorporationPrimer composition and method of bonding a sealing material onto a substrateEP1273616A1Jun 21, 2002Jan 8, 2003THE GOODYEAR TIRE &amp; RUBBER COMPANYElastomer composition which contains intercalated and exfoliated clay reinforcement formed in situ within the elastomer host and article, such as a tire, having at least one component thereofEP1321489B1Dec 18, 2002Apr 30, 2008THE GOODYEAR TIRE &amp; RUBBER COMPANYPreparation and use of a nanocomposite of elastomer and exfoliated clay platelets formed in situ within an elastomer host and articles of manufacture, including tires, having at least one component comprised thereofEP1783168A3Nov 2, 2006Jun 6, 2007Fujifilm CorporationFluorescent polymer fine particleFR2099645B1 Title not availableJP2191619A Title not availableJP2196893A Title not availableJP7011043B2 Title not availableNon-Patent CitationsReference1"Dendrimers and Dendrons, Concept, Synthesis, Application", edited by Newkome G.R, Wiley-VCH, 2001, pp. 45, 191-310.2"Synthesis, Functionalization and Surface Treatment of Nanoparticles", edited by Baraton M-I, ASP (Am. Sci. Pub.), Stevenson Ranch, California, 2003, pp. 51-52, 174-208.3A Review of Nanocomposites 2000, J.N. Hay, S. J. Shaw.4Akashi, Mitsuru et al., "Synthesis and Polymerization of a Styryl Terminated Oligovinylpyrrolidone Macromonomer", Die Angewandte Makromolekulare Chemie, 132, pp. 81-89 (1985).5Alexandridis, Paschalis et al., "Amphiphilic Block Copolymers: Self-Assembly and Applications", Elsevier Science B.V., pp. 1-435 (2000).6Allgaier, Jurgen et al., "Synthesis and Micellar Properties of PS-PI Block Copolymers of Different Architecture", ACS Polym. Prepr. (Div Polym. Chem.), vol. 37, No. 2, pp. 670-671 (1996).7Anomalous Behaviour of Solutions of Styrene-Butadiene Block Copolymers in Some Solvents, Tuzar et al., Makromol. Chem. 178, 22743-2746, 1977.8Antonietti, Markus et al., "Determination of the Micelle Architecture of Polystyrene/Poly(4-vinylpyridine) Block Copolymers in Dilute Solution", Macromolecules, 27, pp. 3276-3281 (1994).9Antonietti, Markus et al., "Novel Amphiphilic Block Copolymers by Polymer Reactions and Their Use for Solubilization of Metal Salts and Metal Colloids", Macromolecules, 29, pp. 3800-3806 (1996).10Asinovsky, Olga, Aug. 16, 2007 Advisory Action from U.S. Appl. No. 10/791,049, filed Mar. 2, 2004 (2 pp.).11Asinovsky, Olga, Dec. 22, 2006 Office Action from U.S. Appl. No. 10/791,049, filed Mar. 2, 2004 (11 pp.).12Asinovsky, Olga, Jul. 29, 2008 Advisory Action from U.S. Appl. No. 10/791,049, filed Mar. 2, 2004 (3 pp.).13Asinovsky, Olga, Jun. 20, 2006 Office Action from U.S. Appl. No. 10/791,049, filed Mar. 2, 2004 (11 pp.).14Asinovsky, Olga, Jun. 7, 2007 Office Action from U.S. Appl. No. 10/791,049, filed Mar. 2, 2004 (11 pp.).15Asinovsky, Olga, May 21, 2008 Office Action from U.S. Appl. No. 10/791,049, filed Mar. 2, 2004 (11 pp.).16Asinovsky, Olga, Nov. 28, 2007 Office Action from U.S. Appl. No. 10/791,049, filed Mar. 2, 2004 (9 pp.).17Asinovsky, Olga, Sep. 11, 2008 Office Action from U.S. Appl. No. 10/791,049, filed Mar. 2, 2004 (12 pp.).18Association of Block Copolymers in Selective Solvents, 1 Measurements on Hydrogenated Poly(styrene-isoprene) in Decane and in trans-Decalin, Mandema et al., Makromol. Chem. 180, 1521-1538, 1979.19Aug. 21, 2006 Final Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (14 pp.).20Aug. 25, 2008 International Search Report from PCT Patent Application No. PCT/US2008/068838 filed Jun. 30, 2008 (4 pp.).21Bahadur, Pratap, "Block copolymers—Their microdomain formation (in solid state) and surfactant behaviour (in solution)", Current Science, vol. 80, No. 8, pp. 1002-1007, Apr. 25, 2001.22Batzilla, Thomas et al., "Formation of intra- and intermolecular crosslinks in the radical crosslinking of poly(4-vinylstyrene)", Makromol. Chem., Rapid Commun. 8, pp. 261-268 (1987).23Bauer, B.J. et al., "Synthesis and Dilute-Solution Behavior of Model Star-Branched Polymers", Rubber Chemistry and Technology, vol. 51, pp. 406-436 (1978).24Berger, G. et al., "Mutual Termination of Anionic and Cationic ‘Living’ Polymers", Polymer Letters, vol. 4, pp. 183-186 (1966).25Berger, G. et al., "Mutual Termination of Anionic and Cationic 'Living' Polymers", Polymer Letters, vol. 4, pp. 183-186 (1966).26Bohm, Georg et al., "Emerging materials: technology for new tires and other rubber products", Tire Technology International, 2006 (4 pp.).27Bohm, Georg G.A. et al. U.S. Appl. No. 11/117,981, filed Apr. 29, 2005 entitled "Self Assembly of Molecules to Form Nano-Particle".28Bohm, Georg G.A. et al., U.S. Appl. No. 11117,981, filed Apr. 29, 2005 entitled "Self Assembly of Molecules to Form Nano-Particle".29Borukhov, Itamar et al., "Enthalpic Stabilization of Brush-Coated Particles in a Polymer Melt", Macromolecules, vol. 35, pp. 5171-5182 (2002).30Bradley, John S., "The Chemistry of Transition Metal Colloids", Clusters and Colloids: From Theory to Applications, Chapter 6, Weinheim, VCH, pp. 459-544 (1994).31Braun, Hartmut et al., "Enthalpic interaction of diblock copolymers with immiscible polymer blend components", Polymer Bulletin, vol. 32, pp. 241-248 (1994).32Bridgestone Americas 2006 Presentation (14 pp.).33Bronstein, Lyudmila M. et al., "Synthesis of Pd-, Pt-, and Rh-containing polymers derived from polystyrene-polybutadiene block copolymers; micellization of diblock copolymers due to complexation", Macromol. Chem. Phys., 199, pp. 1357-1363 (1998).34Brown, H.R. et al., "Communications to the Editor: Enthalpy-Driven Swelling of a Polymer Brush", Macromolecules, vol. 23, pp. 3383-3385 (1990).35Cahn, John W., "Phase Separation by Spinodal Decomposition in Isotropic Systems", The Journal of Chemical Physics, vol. 42, No. 1, pp. 93-99 (Jan. 1, 1965).36Cain, Edward J., Final Office Action dated Dec. 9, 2008 from U.S. Appl. No. 11/642,795 (6 pp.).37Cain, Edward J., Notice of Allowance dated Dec. 31, 2008 from U.S. Appl. No. 11/642,124 (5 pp.).38Calderara, Frederic et al., "Synthesis of chromophore-labelled polystyrene/poly(ethylene oxide) diblock copolymers", Makromol. Chem., 194, pp. 1411-1420 (1993).39Chemical Modification of Poly (styrene-co-maleic anhydride) with Primary N-Alkylamines by Reactive Extrusion, I Vermeesch et al., J. Applied Polym. Sci., vol. 53, 1994, pp. 1365-1373.40Chen, Jizhuang, Dec. 21, 2007 Office Action from Chinese Patent Application No. 02819527.2 filed Oct. 4, 2002 (12 pp.).41Chen, Jizhuang, Dec. 30, 2005 Office Action from Chinese Patent Application No. 02819527.2 filed Oct. 4, 2002 (9 pp.).42Chen, Jizhuang, Sep. 26, 2008 Office Action from Chinese Patent Application No. 02819527.2 filed Oct. 4, 2002 (4 pp.).43Chen, Ming-Qing et al., "Graft Copolymers Having Hydrophobic Backbone and Hydrophilic Branches. XXIII. Particle Size Control of Poly(ethylene glycol)-Coated Polystyrene Nanoparticles Prepared by Macromonomer Method", Journal of Polymer Science: Part A: Polymer Chemistry, vol. 37, pp. 2155-2166 (1999).44Chen, Ming-Qing et al., "Graft Copolymers Having Hydrophobic Backbone and Hydrophilic Branches. XXIII. Particle Size Control of Poly(ethylene glycol)—Coated Polystyrene Nanoparticles Prepared by Macromonomer Method", Journal of Polymer Science: Part A: Polymer Chemistry, vol. 37, pp. 2155-2166 (1999).45Chen, Ming-Qing et al., "Nanosphere Formation in Copolymerization of Methyl Methacrylate with Poly(ethylene glycol) Macromonomers", Journal of Polymer Science: Part A: Polymer Chemistry, vol. 38, pp. 1811-1817 (2000).46Chevalier, Alicia Ann, Jan. 4, 2007 Office Action from U.S. Appl. No. 10/886,283, filed Jul. 6, 2004 (8 pp.).47Chevalier, Alicia Ann, Jan. 4, 2008 Office Action from U.S. Appl. No. 10/886,283, filed Jul. 6, 2004 (8 pp.).48Chevalier, Alicia Ann, Jul. 2, 2007 Office Action from U.S. Appl. No. 10/886,283, filed Jul. 6, 2004 (8 pp.).49Chevalier, Alicia Ann, Nov. 25, 2009 Office Action from U.S. Appl. No. 10/886,283 [7 pp.].50Chevalier, Alicia Ann, Sep. 6, 2006 Office Action from U.S. Appl. No. 10/886,283, filed Jul. 6, 2004 (5 pp.).51Choi, Ling Siu, Dec. 4, 2006 Notice of Allowance from U.S. Appl. No. 10/755,648, filed Jan. 12, 2004 (9 pp.).52Choi, Ling Siu, Mar. 24, 2006 Office Action from U.S. Appl. No. 10/755,648, filed Jan. 12, 2004 (11 pp.).53Cui, Honggang et al., "Block Copolymer Assembly via Kinetic Control", Science, vol. 317, pp. 647-650 (Aug. 3, 2007).54Dec. 22, 2006 Advisory Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (3 pp.).55Dendritic Macromolecules: Synthesis of Starburst Dendrimers, Donald A. Tomalia et al., Macromolecules vol. 19, No. 9, 1986, contribution from Functional Polymers/Processes and the Analytical Laboratory, Dow Chemical, Midland, MI 48640, pp. 2466-2468.56Dialkylimidazolium Chloroaluminate Melts: A New Class of Room-Temperature Ionic Liquids for Electrochemistry, Spectroscopy, and Synthesis. J.S. Wilkes, J.A. Levisky, B.A. Wilson, Inorg. Chem. 1982, 21, pp. 1263-1264.57Edmonds, William F. et al., "Disk Micelles from Nonionic Coil- Coil Diblock Copolymers", Macromolecules, vol. 39, pp. 4526-4530 (May 28, 2006).58Ege, Seyhan, Organic Chemistry Structure and Reactivity, 3rd Edition, p. 959 (1994).59Eisenberg, Adi, "Thermodynamics, Kinetics, and Mechanisms of the Formation of Multiple Block Copolymer Morphologies", Polymer Preprints, vol. 41, No. 2, pp. 1515-1516 (2000).60Erhardt, Rainer et al., Macromolecules, vol. 34, No. 4, pp. 1069-1075 (2001).61Eschwey, Helmut et al., "Preparation and Some Properties of Star-Shaped Polymers with more than Hundred Side Chains", Die Makromolekulare Chemie 173, pp. 235-239 (1973).62Eschwey, Helmut et al., "Star polymers from styrene and divinylbenzene", Polymer, vol. 16, pp. 180-184 (Mar. 1975).63EXAFS Investigations of the Mechanism of Facilitated Ion Transfer into a Room-Temperature Ionic Liquid. M. Jensen, J.A. Dzielawa, P. Rickert, M.L. Dietz, Jacs, 2002, 124, pp. 10664-10665.64Fendler, Janos H., "Nanoparticles and Nanostructured Films: Preparation, Characterization and Applications", Wiley-VCH, pp. 1-468 (1998).65Ferreira, Paula G. et al., "Scaling Law for Entropic Effects at Interfaces between Grafted Layers and Polymer Melts", Macromolecules, vol. 31, pp. 3994-4003 (1998).66Formation of Worm-like Micelles from a Polystyrene-Polybutadiene-Polystyrene Block Copolymer in Ethyl Acetate, Canham et al., J.C.S. Faraday I, 1980, 76, 1857-1867.67Functionalized Core-Shell Polymers Prepared by Microemulsion Polymerization, E. Mendizabal et al., Dept. of Ingenieria Quimica, Unviv. De Guadalajara, MX, 477/ANTE 97/1733-1737.68Garcia, Carlos B. et al., "Self-Assembly Approach toward Magnetic Silica-Type Nanoparticles of Different Shapes from Reverse Block Copolymer Mesophases", J. Am. Chem. Soc., vol. 125, pp. 13310-13311 (2003).69Gay, C., "Wetting of a Polymer Brush by a Chemically Identical Polymer Melt", Macromolecules, vol. 30, pp. 5939-5943 (1997).70Greenwod, N.N.; Earnshaw, A., Chemistry of the Elements, pp. 1126-1127, Pergaroen Press, New York 1984.71Guo, Andrew et al., "Star Polymers and Nanospheres from Cross-Linkable Diblock Copolymers", Macromolecules, vol. 29, pp. 2487-2493, Jan. 17, 1996.72Haider, Saira Bano, Dec. 2, 2008 Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (10 pp.).73Haider, Saira Bano, Dec. 22, 2006 Advisory Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (3 pp.).74Haider, Saira Bano, Jun. 12, 2008 Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (10 pp.).75Haider, Saira Bano, Mar. 19, 2008 Advisory Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (3 pp.).76Haider, Saira Bano, Mar. 3, 2009 Advisory Action from U.S. Appl. No. 11/104,759 (3 pp.).77Haider, Saira Bano, May 16, 2007 Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (9 pp.).78Haider, Saira Bano, Oct. 30, 2007 Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (9 pp.).79Haider, Saira Bano, Sep. 11, 2009 Examiner's Answer from U.S. Appl. No. 11/104,759 (9 pp.).80Halperin, A., "Polymeric Micelles: A Star Model", Macromolecules, vol. 20, pp. 2943-2946 (1987).81Hamley, Ian W., "The Physics of Block Copolymers", Oxford Science Publication: Oxford, Chapters 3 and 4, pp. 131-265, (1998).82Harlan, Robert D., April 30, 2009 Office Action from U.S. Appl. No. 11/117,981 (7 pp.).83Harlan, Robert D., Dec. 28, 2009 Office Action from U.S. Appl. No. 12/504,255 [6 pp.].84Harlan, Robert D., Dec. 29, 2009 Notice of Allowance from U.S. Appl. No. 10/791,177 [6 pp.].85Harlan, Robert D., Dec. 4, 2009 Notice of Allowance from U.S. Appl. No. 11/117,981 [5 pp.].86Harlan, Robert D., Final Office Action dated Dec. 10, 2008 from U.S. Appl. No. 10/791,177 (8 pp.).87Harlan, Robert D., Jan. 2, 2008 Office Action from U.S. Appl. No. 11/117,981, filed Apr. 29, 2005 (6 pp.).88Harlan, Robert D., Jan. 26, 2007 Office Action from U.S. Appl. No. 11/117,981, filed Apr. 29, 2005 (8 pp.).89Harlan, Robert D., Jan. 3, 2005 Notice of Allowance from U.S. Appl. No. 10/223,393, filed Aug. 19, 2002 (6 pp.).90Harlan, Robert D., Jan. 9, 2008 Advisory Action from U.S. Appl. No. 10/791,177, filed Mar. 2, 2004 (3 pp.).91Harlan, Robert D., Jul. 12, 2007 Office Action from U.S. Appl. No. 11/117,981, filed Apr. 29, 2005 (6 pp.).92Harlan, Robert D., Jul. 20, 2006 Office Action from U.S. Appl. No. 11/117,981, filed Apr. 29, 2005 (6 pp.).93Harlan, Robert D., Jul. 25, 2008 Office Action from U.S. Appl. No. 11/117,981, filed Apr. 29, 2005 (8 pp.).94Harlan, Robert D., Jun. 22, 2004 Office Action from U.S. Appl. No. 10/223,393, filed Aug. 19, 2002 (6 pp.).95Harlan, Robert D., Mar. 11, 2009 Notice of Allowance from U.S. Appl. No. 10/791,177 (8 pp.).96Harlan, Robert D., Mar. 17, 2004 Restriction/Election Office Action from U.S. Appl. No. 10/223,393, filed Aug. 19, 2002 (6 pp.).97Harlan, Robert D., Mar. 7, 2008 Advisory Action from U.S. Appl. No. 10/791,177, filed Mar. 2, 2004 (3 pp.).98Harlan, Robert D., May 28, 2008 Office Action from U.S. Appl. No. 10/791,177, filed Mar. 2, 2004 (8 pp.).99Harlan, Robert D., May 3, 2007 Office Action from U.S. Appl. No. 10/791,177, filed Mar. 2, 2004 (6 pp.).100Harlan, Robert D., Nov. 7, 2005 Office Action from U.S. Appl. No. 11/117,981, filed Apr. 29, 2005 (7 pp.).101Harlan, Robert D., Oct. 18, 2007 Office Action from U.S. Appl. No. 10/791,177, filed Mar. 2, 2004 (6 pp.).102Harlan, Robert D., Office Action dated Jan. 9, 2009 from U.S. Appl. No. 11/117,981 (6 pp.).103Harlan, Robert D., Sep. 29, 2009 Final Office Action from U.S. Appl. No. 11/117,981 (6 pp.).104Hasegawa, Ryuichi et al., "Optimum Graft Density for Dispersing Particles in Polymer Melts", Macromolecules, vol. 29, pp. 6656-6662 (1996).105Iraegui Retolaza, E., Jul. 9, 2004 International Search Report from PCT Patent Application No. PCT/US2004/001000 filed Jan. 15, 2004 (3 pp.).106Ishizu, Koji et al., "Core-Shell Type Polymer Microspheres Prepared by Domain Fixing of Block Copolymer Films", Journal of Polymer Science: Part A: Polymer Chemistry, vol. 27, pp. 3721-3731 (1989).107Ishizu, Koji et al., "Core-Shell Type Polymer Microspheres Prepared from Block Copolymers", Journal of Polymer Science: Part C: Polymer Letters, vol. 26, pp. 281-286, 1988.108Ishizu, Koji et al., "Preparation of core-shell type polymer microspheres from anionic block copolymers", Polymer, vol. 34, No. 18, pp. 3929-3933 (1993).109Ishizu, Koji et al., "Synthesis of Star Polymer with Nucleus of Microgel", Polymer Journal, vol. 12, No. 6, pp. 399-404 (1980).110Ishizu, Koji, "Structural Ordering of Core Crosslinked Nanoparticles and Architecture of Polymeric Superstructures", ACS Polym. Prepr. (Div Polym Chem) vol. 40, No. 1, pp. 456-457 (1999).111Ishizu, Koji, "Synthesis and Structural Ordering of Core-Shell Polymer Microspheres", Prog. Polym. Sci., vol. 23, pp. 1383-1408, 1998.112Johnson, Edward M., International Search Report dated Dec. 12, 2008 from PCT Application No. PCT/US07/74611 (5 pp.).113Kiliman, Leszak B., Apr. 2, 2008 Notice of Allowance from U.S. Appl. No. 10/817,995, filed Apr. 5, 2004 (5 pp.).114Kiliman, Leszak B., Aug. 25, 2003 Notice of Allowance from U.S. Appl. No. 10/038,748, filed Dec. 31, 2001 (5 pp.).115Kiliman, Leszak B., May 15, 2007 Advisory Action from U.S. Appl. No. 10/817,995, filed Apr. 5, 2004 (2 pp.).116Kiliman, Leszek B., Dec. 13, 2006 Office Action from U.S. Appl. No. 10/817,995, filed Apr. 5, 2004 (6 pp.).117Kiliman, Leszek B., Feb. 13, 2003 Office from U.S. Appl. No. 10/038,748, filed Dec. 31, 2001 (3 pp.).118Kiliman, Leszek B., Mar. 23, 2006 Office Action from U.S. Appl. No. 10/817,995, filed Apr. 5, 2004 (7 pp.).119Kiliman, Leszek B., Nov. 13, 2009 Office Action from U.S. Appl. No. 10/817,995 [6 pp.].120Kiliman, Leszek B., Sep. 5, 2008 Office Action from U.S. Appl. No. 10/817,995, filed Apr. 5, 2004 (5 pp.).121Kiliman, Leszek B., Sep. 9, 2005 Office Action from U.S. Appl. No. 10/817,995, filed Apr. 5, 2004 (7 pp.).122Kink-Block and Gauche-Block Structures of Bimolecular Films, Gehard Lagaly, Chem. Int. Ed. Engl. vol. 15 (1976) No. 10, pp. 575-586.123Kralik, M. et al., "Catalysis by metal nanoparticles supported on functional organic polymers", Journal of Molecular Catalysis A: Chemical, vol. 177, pp. 113-138 [2001].124Kraus, Gerard, "Mechanical Losses in Carbon-Black-Filled Rubbers", Journal of Applied Polymer Science: Applied Polymer Symposium, vol. 39, pp. 75-92 (1984).125Le, Hoa T., Apr. 10, 2006 Notice of Allowance from U.S. Appl. No. 10/791,491, filed Mar. 2, 2004 (5 pp.).126Le, Hoa T., Dec. 14, 2004 Office Action from U.S. Appl. No. 10/791,491, filed Mar. 2, 2004 (5 pp.).127Le, Hoa T., Jul. 5, 2005 Office Action from U.S. Appl. No. 10/791,491, filed Mar. 2, 2004 (9 pp.).128Le, Hoa T., Sep. 25, 2008 Office Action from U.S. Appl. No. 11/612,554, filed Dec. 19, 2006 (8 pp.).129Light-Scattering Studies of a Polystyrene-Poly(methyl methacrylate) Two-Blcok Copolymer in Mixed Solvents, Utiyama et al. Macromolecules vol. 7, No. 4, Jul.-Aug. 1974.130Ligoure, Christian, "Adhesion between a Polymer Brush and an Elastomer: A Self-Consistent Mean Field Model", Macromolecules, vol. 29, pp. 5459-5468 (1996).131Linear Viscoelasticity of Disordered Polystyrene-Polyisoprene . . . Layered-Silicate Nanocomposites, J. Ren, Dept. of Chem Eng. Univ. of Houston, Macromol. 2000, pp. 3739-3746.132Lipman, Bernard, Apr. 18, 2007 Supplemental Notice of Allowability from U.S. Appl. No. 11/168,297, filed Jun. 29, 2005 (3 pp.).133Lipman, Bernard, Aug. 28, 2007 Notice of Allowance from U.S. Appl. No. 11/058,156, filed Feb. 15, 2005 (5 pp.).134Lipman, Bernard, Feb. 28, 2008 Notice of Allowance from U.S. Appl. No. 11/058,156, filed Feb. 15, 2005 (5 pp.).135Lipman, Bernard, Mar. 2, 2007 Notice of Allowance from U.S. Appl. No. 11/168,297, filed Jun. 29, 2005 (3 pp.).136Lipman, Bernard, Mar. 20, 2008 Office Action from U.S. Appl. No. 11/764,607, filed Jun. 18, 2007 (4 pp.).137Lipman, Bernard, Mar. 24, 2004 Restriction/Election Office Action from U.S. Appl. No. 10/345,498, filed Jan. 16, 2003 (5 pp.).138Lipman, Bernard, Mar. 25, 2004 Restriction/Election Office Action from U.S. Appl. No. 10/331,841, filed Dec. 30, 2002 (6 pp.).139Lipman, Bernard, Mar. 26, 2002 Notice of Allowance from U.S. Appl. No. 09/970,830, filed Oct. 4, 2001 (4 pp.).140Lipman, Bernard, May 21, 2007 Notice of Allowance from U.S. Appl. No. 11/058,156, filed Feb. 15, 2005 (3 pp.).141Lipman, Bernard, May 29, 2008 Notice of Allowance from U.S. Appl. No. 11/058,156, filed Feb. 15, 2005 (5 pp.).142Lipman, Bernard, Notice of Allowance dated Jan. 14, 2009 from U.S. Appl. No. 11/058,156 (5 pp.).143Lipman, Bernard, Notice of Allowance dated Jan. 27, 2009 from U.S. Appl. No. 11/764,607 (4 pp.).144Lipman, Bernard, Nov. 18, 2004 Notice of Allowance from U.S. Appl. No. 10/331,841, filed Dec. 30, 2002 (5 pp.).145Lipman, Bernard, Nov. 23, 2004 Notice of Allowance from U.S. Appl. No. 10/345,498, filed Jan. 16, 2003 (5 pp.).146Lipman, Bernard, Oct. 3, 2006 Notice of Allowance from U.S. Appl. No. 11/064,234, filed Feb. 22, 2005 (5 pp.).147Lipman, Bernard, Sep. 14, 2006 Office Action from U.S. Appl. No. 11/168,297, filed Jun. 29, 2005 (4 pp.).148Lipman, Bernard, Sep. 25, 2008 Notice of Allowance from U.S. Appl. No. 11/764,607, filed Jun. 18, 2007 (3 pp.).149Lipman, Bernard., Sep. 29, 2006 Office Action from U.S. Appl. No. 11/058,156, filed Feb. 15, 2005 (5 pp.).150Liu, Guojun et al., "Diblock Copolymer Nanofibers", Macromolecules, 29, pp. 5508-5510 (1996).151Liu, T. et al., "Formation of Amphiphilic Block Copolymer Micelles in Nonaqueous Solution", Amphiphilic Block Copolymers: Self-Assembly and Applications, Elsevier Science B.V., pp. 115-149 (2000).152lraegui Retolaza, E., May 30, 2008 International Search Report from PCT Patent Application No. PCT/US2007/026031 filed Dec. 19, 2007 (3 pp.).153M. Moller, J.P. Spaz, A. Roescher, S. Mobmer, S.T. Selvan, H. A. Klok, Macromol. Symp. 117, 207-218 (1997).154Ma, Qinggao et al., "Entirely Hydrophilic Shell Cross-Linked Knedel-Like (SCK) Nanoparticles", Polymer Preprints, vol. 41, No. 2, pp. 1571-1572 (2000).155Maksymonko, John M., Aug. 6, 2008 Office Action from U.S. Appl. No. 11/305,279, filed Dec. 16, 2005 (11 pp.).156Maksymonko, John M., Feb. 20, 2008 Office Action from U.S. Appl. No. 11/305,279, filed Dec. 16, 2005 (14 pp.).157Maksymonko, John M., Jul. 17, 2008 Office Action from U.S. Appl. No. 11/305,281, filed Dec. 16, 2005 (13 pp.).158Maksymonko, John M., Jun. 11, 2008 Office Action from U.S. Appl. No. 11/642,124, filed Dec. 20, 2006 (16 pp.).159Maksymonko, John M., Jun. 13, 2008 Office Action from U.S. Appl. No. 11/641,514, filed Dec. 19, 2006 (7 pp.).160Maksymonko, John M., May 28, 2008 Office Action from U.S. Appl. No. 11/642,802, filed Dec. 20, 2006 (10 pp.).161Maksymonko, John M., May 30, 2008 Office Action from U.S. Appl. No. 11/642,795, filed Dec. 20, 2006 (12 pp.).162Matsen, M.W., "Phase Behavior of Block Copolymer/Homopolymer Blends", Macromolecules, vol. 28, pp. 5765-5773 (1995).163May 16, 2007 Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (9 pp.).164May 27, 2008 International Search Report from PCT Patent Application No. PCT/US2007/087869 filed Dec. 18, 2007 (4 pp.).165May 30, 2008 International Search Report from PCT Patent Application No. PCT/US2007/026031 filed Dec. 19, 2007 (4 pp.).166Mayer, A.B.R. et al., "Transition metal nanoparticles protected by amphiphilic block copolymers as tailored catalyst systems", Colloid Polym. Sci., 275, pp. 333-340 (1997).167Mettler, Rolf-Martin, May 27, 2008 International Search Report from PCT Patent Application No. PCT/US2007/087869 filed Dec. 18, 2007 (2 pp.).168Mi, Yongli et al., "Glass transition of nano-sized single chain globules", Polymer 43, Elsevier Science Ltd., pp. 6701-6705 (2002).169Milner, S.T. et al., "End-Confined Polymers: Corrections to the Newtonian Limit", Macromolecules, vol. 22, pp. 489-490 (1989).170Milner, S.T. et al., "Theory of the Grafted Polymer Brush", Macromolecules, vol. 21, pp. 2610-2619 (1988).171Mulcahy, Peter D., May 13, 2009 Office Action from U.S. Appl. No. 11/642,802 (7 pp.).172Mulcahy, Peter D., Nov. 9, 2009 Final Office Action from U.S. Appl. No. 11/642,802 [6 pp.].173Mulcahy, Peter D., Restriction/Election Office Action dated Dec. 11, 2008 from U.S. Appl. No. 11/642,802 (7 pp.).174Mullis, Jeffrey C., Apr. 30, 2009 Final Office Action from U.S. Appl. No. 11/641,514 (11 pp.).175Mullis, Jeffrey C., Aug. 21, 2008 Office Action from U.S. Appl. No. 11/050,115, filed Feb. 3, 2005 (7 pp.).176Mullis, Jeffrey C., Dec. 18, 2009 Supplemental Notice of Allowability from U.S. Appl. No. 11/050,115 [2 pp.].177Mullis, Jeffrey C., Jul. 15, 2009 Advisory Action from U.S. Appl. No. 11/641,514 (4 pp.).178Mullis, Jeffrey C., Mar. 11, 2009 Office Action from U.S. Appl. No. 10/791,049 (9 pp.).179Mullis, Jeffrey C., Mar. 24, 2008 Office Action from U.S. Appl. No. 11/050,115, filed Feb. 3, 2005 (10 pp.).180Mullis, Jeffrey C., May 19, 2009 Advisory Action from U.S. Appl. No. 10/791,049 (5 pp.).181Mullis, Jeffrey C., Nov. 5, 2008 Advisory Action from U.S. Appl. No. 11/050,115, filed Feb. 3, 2005 (4 pp.).182Mullis, Jeffrey C., Nov. 9, 2009 Office Action from U.S. Appl. No. 11/641,514 [9 pp.].183Mullis, Jeffrey C., Oct. 31, 2006 Office Action from U.S. Appl. No. 11/050,115, filed Feb. 3, 2005 (6 pp.).184Mullis, Jeffrey C., Oct. 31, 2008 Office Action from U.S. Appl. No. 11/641,514, filed Dec. 19, 2006 (10 pp.).185Nace, Vaughn M., "Nonionic Surfactants: Polyoxyalkylene Block Copolymers", Surfactant Science Series, vol. 60, pp. 1-266 (1996).186Non-Debye Relaxations in Disordered Ionic Solids, W. Dieterich, P. Maass, Chem. Chys. 2002, 284, pp. 439-467.187Noolandi, Jaan et al., "Theory of Block Copolymer Micelles in Solution", Macromolecules, vol. 16, pp. 1443-1448 (1983).188Oct. 20, 2005 Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (12 pp.).189Oct. 30, 2007 Final Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (11 pp.)190Okay, Oguz et al., "Anionic Dispersion Polymerization of 1,4-Divinylbenzene", Macromolecules, 23, pp. 2623-2628 (1990).191Okay, Oguz et al., "Steric stabilization of reactive microgels from 1,4-divinylbenzene", Makromol. Chem., Rapid Commun., vol. 11, pp. 583-587 (1990).192Oranli, Levent et al., "Hydrodynamic studies on micellar solutions of styrene-butadiene block copolymers in selective solvents", Can. J. Chem., vol. 63, pp. 2691-2696, 1985.193O'Reilly, Rachel K. et al., "Cross-linked block copolymer micelles: functional nanostructures of great potential and versatility", Chem. Soc. Rev., vol. 35, pp. 1068-1083, Oct. 2, 2006.194O'Reilly, Rachel K. et al., "Functionalization of Micelles and Shell Cross-linked Nanoparticles Using Click Chemistry", Chem. Mater., vol. 17, No. 24, pp. 5976-5988 [Nov. 24, 2005].195Pak, Hannah J., Apr. 2, 2009 Office Action from U.S. Appl. No. 11/941,128 (9 pp.).196Pak, Hannah J., Apr. 30, 2010 Notice of Allowance from U.S. Appl. No. 11/941,128 (11 pp.).197Pak, Hannah J., Jan. 6, 2010 Final Office Action from U.S. Appl. No. 11/941,128 [10 pp.].198Peets, Monique R., Apr. 15, 2010 Notice of Allowance from U.S. Appl. No. 11/697,801 (5 pp.).199Peets, Monique R., Jan. 5, 2010 Final Office Action from U.S. Appl. No. 11/697,801 [9 pp.].200Peets, Monique R., Jul. 20, 2009 Office Action from U.S. Appl. No. 11/697,801 (9 pp.).201Peets, Monique R., May 11, 2009 Restriction/Election Office Action from U.S. Appl. No. 11/697,801 (6 pp.).202Piirma, Irja, "Polymeric Surfactants", Surfactant Science Series, vol. 42, pp. 1-289 (1992).203Pispas, S. et al., "Effect of Architecture on the Micellization Properties of Block Copolymers: A2 B Miktoarm Stars vs AB Diblocks", Macromolecules, vol. 33, pp. 1741-1746, Feb. 17, 2000.204Polymer Layered Silicate Nanocomposites, Giannelis E.P. Advanced Materials vol. 8, No. 1, Jan. 1, 1996, pp. 29-35.205Polymer-m-Ionic-Liquid Electrolytes C. Tiyapiboonchaiya, D.R. MacFarlane, J. Sun, M. Forsyth, Micromol. Chem. Phys., 2002, 203, pp. 1906-1911.206Polysulfobetaines and Corresponding Cationic Polymers. IV. Synthesis and Aqueous Solution Properties of Cationic Poly (MIQSDMAPM), Wen-Fu Lee et al., J. Appl. Pol. Sci. vol. 59, 1996, pp. 599-608.207Preparation and Characterization of Heterophase Blends of Polycaprolactam and Hydrogenated Polydienes, David F. Lawson et al., pp. 2331-2351, Central Research Labs., The Firestone Tire and Rubber Col, Akron, OH 44317, Journal of Applied Polymer Science, vol. 39, 1990 John Wiliey & Sons, Inc.208Pre-print article, Wang, Xiaorong et al., "PMSE 392- Manufacture and Commercial Uses of Polymeric Nanoparticles", Division of Polymeric Materials: Science and Engineering (Mar. 2006).209Price, Colin, "Colloidal Properties of Block Copolymers", Applied Science Publishers Ltd., Chapter 2, pp. 39-80 (1982).210Quaternary Ammonium Compounds, Encyclopedia of Chem Tech., 4th Ed. vol. 20, 1996, Wiley & Sons, pp. 739-767.211R.P. Quirk and S.C. Galvan, Macromolecules, 34, 1192-1197 (2001).212Rager, Timo et al., "Micelle formation of poly(acrylic acid)- block-poly(methyl methacrylate) block copolymers in mixtures of water with organic solvents", Macromol. Chem. Phys., 200, No. 7, pp. 1672-1680 (1999).213Raza, Saira B., Aug. 21, 2006 Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (6 pp.).214Raza, Saira B., Oct. 20, 2005 Office Action from U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 (10 pp.).215Reaction of Primary Aliphatic Amines with Maleic Anhydride, Lester E. Coleman et al., J. Org,. Chem., 24, 185, 1959, pp. 135-136.216Recent Advances in Flame Retardant Polymer Nanocomposites, Tilman, J.W. et al., pp. 273-283.217Rein, David H. et al., "Kinetics of arm-first star polymers formation in a non-polar solvent", Macromol. Chem. Phys., vol. 199, pp. 569-574 (1998).218Rempp, Paul et al., "Grafting and Branching of Polymers", Pure Appl. Chem., vol. 30, pp. 229-238 (1972).219Reverse Atom Transfer Radical Polymerization of Methyl Methacrylate in Room-Temperature Inoic Liqquids, H. Ma, X. Wan, X. Chen, Q-F. Zhou, J. Polym. Sci., A. Polym. Chem. 2003, 41, pp. 143-151.220Rheology of End-Tethered Polymer Layered Silicate Nanocomposites, R. Krishnamoorti et al., Macromol. 1997, 30, 4097-4102.221Rheology of Nanocomposites Based on Layered Silicates and Polyamide-12, B. Hoffman et al., Colloid Polm. Sci. 278:629-636 (2000).222Riess, Gerard et al., "Block Copolymers", Encyclopedia of Polymer Science and Engineering, vol. 2, pp. 324-434 (1985).223Riess, Gerard, "Micellization of block copolymers", Prog. Polym. Sci., vol. 28, pp. 1107-1170, Jan. 16, 2003.224Ronesi, Vickey M., Jan. 8, 2007 Office Action from U.S. Appl. No. 10/791,177, filed Mar. 2, 2004 (5 pp.).225Russell, G., Aug. 1, 2005 International Search Report from PCT Patent Application No. PCT/US2005/010352 filed Mar. 28, 2005 (3 pp.).226Russell, Graham, Nov. 4, 2008 Office Action from European Patent Application No. 05742316.2 filed Mar. 28, 2005 (2 pp.).227S. Mossmer, J.P. Spatz, M.Moller, T. Aberle, J. Schmidt, W. Burchard, Macromol. 33, 4791-4798 (2000).228Saito, Reiko et al., "Arm-number effect of core-shell type polymer microsphere: 1. Control of arm-number of microsphere", Polymer, vol. 35, No. 4, pp. 866-871 (1994).229Saito, Reiko et al., "Core-Shell Type Polymer Microspheres Prepared From Poly(Styrene-b-Methacrylic Acid)-1. Synthesis of Microgel", Eur. Polym. J., vol. 27, No. 10, pp. 1153-1159 (1991).230Saito, Reiko et al., "Core-Shell Type Polymer Microspheres Prepared From Poly(Styrene-b-Methacrylic Acid)—1. Synthesis of Microgel", Eur. Polym. J., vol. 27, No. 10, pp. 1153-1159 (1991).231Saito, Reiko et al., "Synthesis of microspheres with ‘hairy-ball’ structures from poly (styrene-b-2-vinyl pyridine) diblock copolymers", Polymer, vol. 33, No. 5, pp. 1073-1077, 1992.232Saito, Reiko et al., "Synthesis of Microspheres with Microphase-Separated Shells", Journal of Polymer Science: Part A: Polymer Chemistry, vol. 38, pp. 2091-2097 (2000).233Sakurai, Ryo et al., "68.2: Color and Flexible Electronic Paper Display using QR-LPD Technology", SID 06 Digest, pp. 1922-1925 (2006).234Schutte, M., Aug. 8, 2006 Office Action from European Patent Application No. 02807196.7 filed Oct. 4, 2002 (5 pp.).235Schutte, M., May 28, 2004 International Search Report from PCT Patent Application No. PCT/US03/40375 filed Dec. 18, 2003 (3 pp.).236Schutte, M., Nov. 13, 2003 International Search Report from PCT Patent Application No. PCT/US02/31817 filed Oct. 4, 2002 (3 pp.).237Schutte, Maya, Sep. 3, 2007 Office Action from European Patent Application No. 02807196.7 filed Oct. 4, 2002 (2 pp.).238Semenov, A.N., "Phase Equilibria in Block Copolymer-Homopolymer Mixtures", Macromolecules, vol. 26, pp. 2273-2281 (1993).239Semenov, A.N., "Theory of Diblock-Copolymer Segregation to the Interface and Free Surface of a Homopolymer Layer", Macromolecules, vol. 25, pp. 4967-4977 (1992).240Serizawa, Takeshi et al., "Transmission Electron Microscopic Study of Cross-Sectional Morphologies of Core-Corona Polymeric Nanospheres", Macromolecules, 33, pp. 1759-1764 (2000).241Shull, Kenneth R., "End-Adsorbed Polymer Brushes in High- and Low-Molecular-Weight Matrices", Macromolecules, vol. 29, pp. 2659-2666 (1996).242Simultaneous TA and MS Analysis of Alternating Styrene-Malei Anhydride and Styrene-Maleimide Copolymers, Thermochim. Acta, 277, 14, 1996.243Star Polymers by Immobilizing Functional Block Copolymers, by Koji Ishizu, Tokyo Institute of Technology, Meguro-ku, Tokyo, Japan, Star and Hyperbranched Polymers, 1999, ISBN 0-8247-1986-7.244Stepanek, Miroslav et al. "Time-Dependent Behavior of Block Polyelectrolyte Micelles in Aqueous Media Studied by Potentiometric Titrations, QELS and Fluoroetry", Langmuir, Vo. 16, No. 6, pp. 2502-2507 (2000).245Structure of molten 1,3-dimethylimidazolium chloride using neutron diffraction.C. Hardacre, J.D. Holbrey, S.E. J. McMath, D.T. Bowron, A.K. Soper, J. Chem. Physics, 2003, 118(1), pp. 273-278.246Super-Repellent Composite Fluoropolymer Surfaces, S.R. Coulson, I. Woodward, J.P.S. Badyal, The Journal of Physical Chemistry B, vol. 104, No. 37, Sep. 21, 2000, pp. 8836-8840, Dept. of Chemistry, Science Laboratories, Durham University, Durham, DH1 3LE, England, U.K.247Sykes, Altrev C., Apr. 5, 2010 Final Office Action from U.S. Appl. No. 11/818,023 (24 pp.).248Sykes, Altrev C., Mar. 20, 2009 Office Action from U.S. Appl. No. 11/818,023 (27 pp.).249Sykes, Altrev C., Oct. 16, 2009 Office Action from U.S. Appl. No. 11/818,023 [20 pp.].250Synthesis and Photocrosslinking of Maleimide-Type Polymers, Woo-Sik Kim et al., Macromol. Rapid Commun., 17, 835, 1996, pp. 835-841.251Synthesis, Thermal Properties and Gas Permeability of Poly (N-n-alkylmaleimide)s, A. Matsumoto et al., Polymer Journal vol. 23, No. 3, 1991, pp. 201-209.252T. Cosgrove, J.S. Phipps, R.M. Richardson, Macromolecules, 26, 4363-4367 (1993).253Thurmond II, K. Bruce et al., "The Study of Shell Cross-Linked Knedels (SCK), Formation and Application", ACS Polym. Prepr. (Div Polym. Chem.), vol. 38, No. 1, pp. 62-63 (1997).254Thurmond II, K. Bruce et al., "Water-Soluble Knedel-like Structures: The Preparation of Shell-Cross-Linked Small Particles", J. Am. Chem. Soc., vol. 118, pp. 7239-7240 (1996).255Thurmond, K. Bruce et al., "Shell cross-linked polymer micelles: stabilized assemblies with great versatility and potential", Colloids and Surfaces B: Biointerfaces, vol. 16, pp. 45-54, 1999.256Transformation of a Simple Plastic into a Superhydrophobic Surface, H. Yildirim Erbil et al., Science vol. 299, Feb. 28, 2003, pp. 1377-1380.257Tsitsilianis, Constantinos et al., Makromol. Chem. 191, pp. 2319-2328 (1990).258Tuzar, Zdenek et al., "Micelles of Block and Graft Copolymers in Solutions", Surface and Colloid Science, vol. 15, Chapter 1, pp. 1-83 (1993).259Ultrahydrophobic and Ultrayophobic Surfaces: Some Comments and Examples, Wei Chen et al., The ACS Journal of Surfaces and Colloids, May 11, 1999, vol. 15, No. 10, pp. 3395-3399, Polymer Science and Engineering Dept., Univ. of MA, Amherst, MA 01003.260Vamvakaki, M. et al., "Synthesis of novel block and statistical methacrylate-based ionomers containing acidic, basic or betaine residues", Polymer, vol. 39, No. 11, pp. 2331-2337 (1998).261van der Maarel, J.R.C. et al., "Salt-Induced Contraction of Polyelectrolyte Diblock Copolymer Micelles", Langmuir, vol. 16, No. 19, pp. 7510-7519 (2000).262Vulcanization Agents and Auxiliary Materials, Kirk-Othmer, Encyclopedia of Chemical Technology, 3rd Ed., Wiley Interscience, NY, 1982, vol. 22, pp. 390-403.263Wang, Xiaorong et al., "Chain conformation in two-dimensional dense state", Journal of Chemical Physics, vol. 121, No. 16, pp. 8158-8162 (Oct. 22, 2004).264Wang, Xiaorong et al., "Heterogeneity of structural relaxation in a particle-suspension system", EPL, 79, 18001, pp. 1-5 (Jul. 2007).265Wang, Xiaorong et al., "Manufacture and Commercial Uses of Polymeric Nanoparticles", Polymeric Materials: Science and Engineering, vol. 94, p. 659 (2006).266Wang, Xiaorong et al., "Strain-induced nonlinearity of filled rubbers", Physical Review E 72, 031406, pp. 1-9 (Sep. 20, 2005).267Wang, Xiaorong et al., "Synthesis, Characterization, and Application of Novel Polymeric Nanoparticles", Macromolecules, 40, pp. 499-508 (2007).268Wang, Xiaorong et al., "Under microscopes the poly(styrene/butadiene) nanoparticles", Journal of Electron Microscopy, vol. 56, No. 6, pp. 209-216 (2007).269Wang, Xiaorong et al., U.S. Appl. No. 10/791,049, filed Mar. 2, 2004 entitled "Method Of Making Nano-Particles Of Selected Size Distribution".270Wang, Xiaorong et al., U.S. Appl. No. 10/791,177, filed Mar. 2, 2004 entitled "Rubber Composition Containing Functionalized Polymer Nanoparticles".271Wang, Xiaorong et al., U.S. Appl. No. 10/872,731, filed Jun. 21, 2004 entitled "Reversible Polymer/Metal Nano-Composites And Method For Manufacturing Same".272Wang, Xiaorong et al., U.S. Appl. No. 10/886,283, filed Jul. 6, 2004 entitled "Hydropobic Surfaces with Nanoparticles".273Wang, Xiaorong et al., U.S. Appl. No. 11/058,156, filed Feb. 15, 2005 entitled "Multi-Layer Nano-Particle Preparation and Applications".274Wang, Xiaorong et al., U.S. Appl. No. 11/104,759, filed Apr. 13, 2005 entitled "Nano-Particle Preparation and Applications".275Wang, Xiaorong et al., U.S. Appl. No. 11/305,279, filed Dec. 16, 2005 entitled "Combined Use of Liquid Polymer and Polymeric Nanoparticles for Rubber Applications".276Wang, Xiaorong et al., U.S. Appl. No. 11/344,861, filed Feb. 1, 2006 entitled "Nano-Composite And Compositions Therefrom".277Wang, Xiaorong et al., U.S. Appl. No. 11/642,796, filed Dec. 20, 2006 entitled "Hollow Nano-Particles And Method Thereof".278Wang, Xiaorong et al., U.S. Appl. No. 11/764,607, filed Jun. 18, 2007 entitled "Multi-Layer Nano-Particle Preparation and Applications".279Wang, Xiaorong et al., U.S. Appl. No. 11/941,128, filed Nov. 16, 2007 entitled "Nano-Particle Preparation And Applications".280Wang, Xiaorong et al., U.S. Appl. No. 11/954,268, filed Dec. 12, 2007 entitled "Nanoporous Polymeric Material And Preparation Method".281Wang, Xiaorong et al., U.S. Appl. No. 12/047,896, filed Mar. 13, 2008 entitled "Reversible Polymer/Metal Nano-Composites And Method For Manufacturing Same".282Wang, Xiaorong et al., U.S. Appl. No. 12/184,895, filed Aug. 1, 2008 entitled "Disk-Like Nanoparticles".283Wang, Xiaorong et al., U.S. Appl. No. 12/374,883, filed Jul. 27, 2007, entitled "Polymeric Core-Shell Nanoparticles with Interphase Region".284Wang, Xr. et al., "Fluctuations and critical phenomena of a filled elastomer under deformation", Europhysics Letters, vol. 75, No. 4, pp. 590-596 (Aug. 15, 2006).285Watanabe, Y., Jul. 29, 2008 Office Action from Japanese Patent Application No. 582224/2003 filed Oct. 4, 2002 (17 pp.).286Watanabe, Y., May 7, 2008 Office Action from Japanese Patent Application No. 582224/2003 filed Oct. 4, 2002 (5 pp.).287Webber, Stephen E. et al., "Solvents and Self-Organization of Polymers", NATO ASI Series, Series E: Applied Sciences, vol. 327, pp. 1-509 (1996).288Wheeler, Thurman Michael, Feb. 8, 2010 Office Action from U.S. Appl. No. 11/642,796 [13 pp.].289Whitmore, Mark Douglas et al., "Theory of Micelle Formation in Block Copolymer-Homopolymer Blends", Macromolecules, vol. 18, pp. 657-665 (1985).290Wijmans, C.M. et al., "Effect of Free Polymer on the Structure of a Polymer Brush and Interaction between Two Polymer Brushes", Macromolecules, vol. 27, pp. 3238-3248 (1994).291Wilson, D.J. et al., "Photochemical Stabilization of Block Copolymer Micelles", Eur. Polym. J., vol. 24, No. 7, pp. 617-621, 1988.292Witten, T.A. et al., "Stress Relaxation in the Lamellar Copolymer Mesophase", Macromolecules, vol. 23, pp. 824-829 (1990).293Wooley, Karen L, "From Dendrimers to Knedel-like Structures", Chem. Eur. J., 3, No. 9, pp. 1397-1399 (1997).294Wooley, Karen L, "Shell Crosslinked Polymer Assemblies: Nanoscale Constructs Inspired from Biological Systems", Journal of Polymer Science: Part A: Polymer Chemistry, vol. 38, pp. 1397-1407 (2000).295Worsfold, D.J., "Anionic Copolymerization of Styrene with p-Divinylbenzene", Macromolecules, vol. 3, No. 5, pp. 514-517 (Sep.-Oct. 1970).296Worsfold, Denis J. et al., "Preparation et caracterisation de polymeres-modele a structure en etoile, par copolymerisation sequencee anionique", Canadian Journal of Chemistry, vol. 47, pp. 3379-3385 (Mar. 20, 1969).297Wyrozebski Lee, Katarzyna I., Dec. 19, 2006 Office Action from U.S. Appl. No. 10/872,731, filed Jun. 21, 2004 (6 pp.).298Wyrozebski Lee, Katarzyna I., Mar. 7, 2007 Office Action from U.S. Appl. No. 10/872,731, filed Jun. 21, 2004 (13 pp.).299Wyrozebski Lee, Katarzyna I., Sep. 14, 2007 Office Action from U.S. Appl. No. 10/872,731, filed Jun. 21, 2004 (9 pp.).300Zemel, Irina Sopja, Dec. 3, 2009 Final Office Action from U.S. Appl. No. 11/305,279 [10 pp.].301Zemel, Irina Sopja, Office Action dated May 28, 2009 from U.S. Appl. No. 11/305,279 (7 pp.).302Zheng, Lei et al., "Polystyrene Nanoparticles with Anionically Polymerized Polybutadiene Brushes", Macromolecules, 37, pp. 9954-9962 (2004).303Zilliox, Jean-Georges et al., "Preparation de Macromolecules a Structure en Etoile, par Copolymerisation Anionique", J. Polymer Sci.: Part C, No. 22, pp. 145-156 (1968).Referenced byCiting PatentFiling datePublication dateApplicantTitleUS7998554Aug 16, 2011Bridgestone CorporationHydrophobic surfaces with nanoparticlesUS8057899Apr 13, 2005Nov 15, 2011Bridgestone CorporationNano-particle preparation and applicationsUS8191169 *Nov 10, 2007Jun 5, 2012Grune Guerry LAnti-microbial compounds used in garments for water based activitiesUS8541503Jul 27, 2007Sep 24, 2013Bridgestone CorporationPolymeric core-shell nanoparticles with interphase regionUS8846819Dec 29, 2009Sep 30, 2014Bridgestone CorporationCore-first nanoparticle formation process, nanoparticle, and compositionUS9061900Dec 16, 2005Jun 23, 2015Bridgestone CorporationCombined use of liquid polymer and polymeric nanoparticles for rubber applicationsUS9062144Apr 5, 2010Jun 23, 2015Bridgestone CorporationHairy polymeric nanoparticles with first and second shell block polymer armsUS9115222Dec 28, 2010Aug 25, 2015Bridgestone CorporationWell defined, highly crosslinked nanoparticles and method for making sameUS9312046Dec 19, 2014Apr 12, 2016South Dakota Board Of RegentsComposite materials with magnetically aligned carbon nanoparticles having enhanced electrical properties and methods of preparationUS20100205709 *Nov 10, 2007Aug 19, 2010Grune Guerry LAnti-microbial compounds used in garments for water based activitiesWO2015147928A2Dec 19, 2014Oct 1, 2015South Dakota Board Of RegentsComposite materials with magnetically aligned carbon nanoparticles and methods of preparationWO2015147931A1Dec 19, 2014Oct 1, 2015South Dakota Board Of RegentsComposite materials with magnetically aligned carbon nanoparticles having enhanced electrical properties and methods of preparation* Cited by examinerClassifications U.S. Classification524/505, 525/89International ClassificationC08F257/02, C08L53/02, B60C1/00, C08F279/02Cooperative ClassificationC08L51/003, C08F297/04, C08F279/02, C08F257/02European ClassificationC08F297/04, C08F257/02, C08F279/02, C08L51/00BLegal EventsDateCodeEventDescriptionJul 2, 2007ASAssignmentOwner name: BRIDGESTONE CORPORATION, OHIOFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:WARREN, SANDRA;REEL/FRAME:019504/0544Effective date: 20070619Apr 24, 2014FPAYFee paymentYear of fee payment: 4RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services