Source: http://www.google.com/patents/US20010044035?dq=7,603,356
Timestamp: 2016-06-26 05:33:40
Document Index: 401595284

Matched Legal Cases: ['art 2', 'art 2', 'art 2', 'art 2', 'art 2', 'art 2']

Patent US20010044035 - Organic EL element and method of manufacturing the same - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsTo seal an organic EL element satisfactorily, even when light is radiated from both electrode sides in the organic EL element. Laminate 20 is formed on transparent substrate 1. Laminate 20 includes transparent electrode 2, hole injecting and transporting layer 3, light emitting layer 4, and cathode 5....http://www.google.com/patents/US20010044035?utm_source=gb-gplus-sharePatent US20010044035 - Organic EL element and method of manufacturing the sameAdvanced Patent SearchPublication numberUS20010044035 A1Publication typeApplicationApplication numberUS 09/811,618Publication dateNov 22, 2001Filing dateMar 20, 2001Priority dateMar 21, 2000Also published asCN1244255C, CN1317922A, US6617052Publication number09811618, 811618, US 2001/0044035 A1, US 2001/044035 A1, US 20010044035 A1, US 20010044035A1, US 2001044035 A1, US 2001044035A1, US-A1-20010044035, US-A1-2001044035, US2001/0044035A1, US2001/044035A1, US20010044035 A1, US20010044035A1, US2001044035 A1, US2001044035A1InventorsKatsuyuki MoriiOriginal AssigneeSeika Epson CorporationExport CitationBiBTeX, EndNote, RefManReferenced by (38), Classifications (23), Legal Events (5) External Links: USPTO, USPTO Assignment, EspacenetOrganic EL element and method of manufacturing the same
US 20010044035 A1Abstract
To seal an organic EL element satisfactorily, even when light is radiated from both electrode sides in the organic EL element. Laminate 20 is formed on transparent substrate 1. Laminate 20 includes transparent electrode 2, hole injecting and transporting layer 3, light emitting layer 4, and cathode 5. The top face of cathode 5 of laminate 20 and the end face of laminate 20 are covered by fist sealing layer 6 comprising LiF. The outer side of first sealing layer 6 is covered by second sealing layer 7 comprising an epoxy resin. Images(1) Claims(11)
What is claimed is: 1. An organic EL element comprising a substrate and a laminate formed on said substrate, said laminate having a structure including a cathode, an anode, and a light emitting layer, said light emitting layer comprising an organic material and being sandwiched between said cathode and anode, and at least the face of the laminate on the opposite side to the substrate side being sealed by a sealant having a two-layer structure including an inner first sealing layer and an outer second sealing layer, wherein said first sealing layer comprising a halide of an alkali metal or alkaline earth metal, and said second sealing layer comprising a moisture proof resinous material. 2. An organic EL element according to claim 1 , wherein said first sealing layer comprises lithium fluoride (LiF). 3. An organic EL element according to claim 1 or 2 , wherein said second sealing layer comprises an epoxy resin. 4. An organic EL element according to any one of claims 1 to 3 , wherein the electrode arranged in the laminate on the opposite side to the substrate side is formed with a material containing calcium (Ca). 5. An organic EL element according to any one of claims 1 to 4 , wherein said first sealing layer has a thickness of not less than 300 angstroms. 6. A method of manufacturing an organic EL element, comprising the steps of: forming a laminate on a substrate, said laminate having a structure including a cathode, an anode, and a light emitting layer, said light emitting layer being comprising an organic material and being sandwiched between said cathode and anode; forming a first sealing layer at least on the face of the formed laminate on the opposite side to the substrate side in an atmosphere being substantially free from oxygen and water, said first sealing layer being comprising a halide of an alkali metal or alkaline earth metal; and forming a second sealing layer on the outer side of the first sealing layer in an atmosphere being substantially free from oxygen and water, said second sealing layer comprising a moisture proof resinous material. 7. A method of manufacturing an organic EL element according to claim 6 , wherein a layer comprising lithium fluoride (LiF) is formed as the first sealing layer. 8. A method of manufacturing an organic EL element according to claim 6 or 7 , wherein a layer comprising an epoxy resin is formed as the second sealing layer. 9. A method of manufacturing an organic EL element according to any one of claims 6 to 8 , wherein a layer comprising a material containing calcium (Ca) is formed as an electrode arranged in the laminate on the opposite side to the substrate side. 10. A method of manufacturing an organic EL element according to any one of claims 6 to 9 , wherein the first sealing layer comprising LiF is formed by vacuum deposition method in the condition that a film-forming rate is not less than 8 angstroms per 1 second. 11. A method of manufacturing an organic EL element according to any one of claims 6 to 10 , wherein the first sealing layer is formed to a thickness of not less than 300 angstroms.
BACKGROUND OF THE INVENTION [0001] 1. Field of Invention [0002] The present invention relates to an organic EL (electroluminescent) element which is used in, for example, a display or surface light source device, and to a method of manufacturing the same. [0003] 2. Description of Related Art [0004] In recent years, development of an organic EL element (a luminous element having a structure including an anode and a cathode, and a light emitting layer comprising organic matter sandwiched between the anode and the cathode) has increasingly proceeded to provide an auto-luminescent type display as an alternative of a liquid crystal display. A conventional structure of the organic EL element includes a structure in which an anode comprising a transparent electrode, a hole injecting and transporting layer, a light emitting layer, and a cathode which does not transmit light, formed in this order on a transparent substrate. In an organic EL element having this structure, light generated by the combination of an electron and a hole in the light emitting layer is radiated toward the substrate side. [0005] Such an organic EL element has a feature in that high luminance light emits with high efficiency only by the application of a low voltage. However, the organic EL element has a problem in that this excellent characteristic cannot be obtained associated with deterioration of constitutive members of the element due to change with time. Causes of this problem particularly include oxidation of the cathode and light emitting layer with oxygen or water in the air. [0006] As measures against this problem, Japanese Unexamined Patent Application Publication No. 5-182759 and Japanese Unexamined Patent Application Publication No. 7-282975 propose the sealing of a laminate with a sealant of a two-layer structure including an inner first sealing layer and an outer second sealing layer, which laminate is formed on a substrate and comprises at least an anode, a light emitting layer, and a cathode. These publications mention that a SiO2 film or SiO film is formed as the first sealing layer by sputtering process or vapor deposition process, and a moisture proof photo-curable resinous layer or thermoplastic polymer layer is formed as the second sealing layer. On the other hand, when the cathode transmits light as well as the anode, light generated by the combination of an electron and a hole in the light emitting layer is also radiated toward the cathode side. Page 2606 of “Appl. Phys. Lett. Vol. 68(19), 6 May, 1996” describes an organic EL element, in which a thin film which is obtained by vapor co-deposition of Mg and Ag is formed as the cathode and light is therefore also radiated toward the cathode side. [0007] In this organic EL element, quinolinolatoaluminum complex (Alq3), an organic material having a low molecular weight, is used as the light emitting layer. [0008] Additionally, an ITO film is formed on the cathode comprising Mg and Ag by sputtering process. This ITO film is provided as a sealing layer and auxiliary electrode. [0009] Additionally, this literature mentions that the sealing method of the cathode side has a significant influence on initial characteristics. Specifically, the literature mentions that the threshold voltage of the organic EL element is increased, resulting from the formation conditions (e.g., amount of oxygen) of the sealing layer. [0010] However, when a SiO2 film or SiO film is formed as a first sealing layer in the sealing operation with a sealant having a two-layer structure, there is a possibility of oxidation of the cathode which comes in contact with the first sealing layer. Even in the organic EL element in which light is radiated toward both electrode sides, a material having a low work function such as calcium is preferably used as the cathode. In this case, oxidation of the cathode is particularly liable to occur when a SiO2 film or SiO film is formed as the first sealing layer. [0011] The present invention has been accomplished focusing attention on these problems of conventional technologies, and the problem to be solved by the invention is to satisfactorily seal an organic EL element even when light is radiated toward both electrode sides in the organic EL element. SUMMARY OF THE INVENTION [0012] To solve the above problem, the present invention provides an organic EL element which includes a substrate and a laminate formed on the substrate, the laminate having a structure including a cathode, an anode, and a light emitting layer, the light emitting layer comprising an organic material and being sandwiched between the cathode and anode, and at least the surface of the laminate on the opposite side to the substrate side being sealed by a sealant having a two-layer structure including an inner first sealing layer and an outer second sealing layer. In the organic EL element, the first sealing layer comprises a halide of an alkali metal or alkaline earth metal, and the second sealing layer comprises a moisture-proof resinous material. [0013] In this organic EL element, the first sealing layer comprises a halide of an alkali metal or alkaline earth metal, and at least the surface of the laminate on the opposite side to the substrate side therefor becomes resistant to oxidation. [0014] The halide of alkali metal or alkaline earth metal constituting the first sealing layer includes, for example, lithium fluoride (LiF), calcium fluoride (CaF2), sodium fluoride (NaF), sodium chloride (NaCl), potassium chloride (KCl), potassium bromide (KBr), magnesium fluoride (MgF2), and lithium chloride (LiCl). Among these, lithium fluoride (LiF) is particularly preferred. [0015] In particular, even when an electrode arranged in the laminate on the opposite side to the substrate side is formed by a metallic material which has a low work function and is much liable to be oxidized (e.g., a material containing calcium), oxidation of the electrode can be effectively inhibited by forming the first sealing layer to be in contact with this electrode as a layer comprising a halide of an alkali metal or alkaline earth metal (particularly LiF). [0016] Additionally, a layer comprising LiF can have a transparency in visible light region higher than that of glass, by forming the layer to an appropriate thickness. Accordingly, this layer is suitable as a first sealant for use in the organic EL element in which light is radiated toward both electrode sides. [0017] Materials for the second sealing layer include, for example, an acrylic resin and an epoxy resin. Among these, the epoxy resin is particularly preferred since it is highly resistant to moisture and has a high transmittance of visible light. Such a second sealing layer comprising an epoxy resin can be easily formed by, for example, applying a liquid thermosetting epoxy resin or light-curable epoxy resin and curing the applied resin. [0018] In order to inhibit deterioration of the laminate (particularly of the light emitting layer) in the formation of the second sealing layer, as well as to obtain the sufficient inhibitory effect of the oxidation of electrode, the first sealing layer should preferably have a thickness of not less than 300 angstroms. Furthermore, the first sealing layer should preferably have a thickness of not more than 500 angstroms, from the viewpoint of inhibiting deterioration of the light emitting layer or the like due to heat in the film-formation of the first sealing layer. [0019] Furthermore, in the invented organic EL element, it is preferred that the face on the opposite side to the substrate side and the end face of the laminate are sealed by a sealant having a two-layer structure, which two-layer structure includes a first sealing layer comprising a halide of an alkali metal or alkaline earth metal, and a second sealing layer comprising a moisture proof resinous material. [0020] The present invention provides, in another aspect, a method of manufacturing an organic EL element, which includes the steps of forming a laminate on a substrate, said laminate having a structure including a cathode, an anode, and a light emitting layer, said light emitting layer comprising an organic material and being sandwiched between the cathode and anode; forming a first sealing layer at least on the surface of the formed laminate on the opposite side to the substrate side in an atmosphere substantially free from oxygen and water, said first sealing layer comprising a halide of an alkali metal or alkaline earth metal; and forming a second sealing layer on the outer side of the first sealing layer in an atmosphere substantially free from oxygen and water, said second sealing layer comprising a moisture proof resinous material. [0021] In the invented method, a layer comprising LiF is preferably formed as the first sealing layer. In the invented method, a layer comprises an epoxy resin is preferably formed as the second sealing layer. [0022] When the first sealing layer comprising LiF is formed by vacuum deposition process, the formation is preferably performed in the condition that a film-forming rate is 8 angstroms or more per 1 second, from the viewpoint of inhibiting deterioration of the light emitting layer or the like due to heat in the film-formation of the first sealing layer. [0023] In the invented method, the first sealing layer is preferably formed to a thickness of not less than 300 angstroms. [0024] It is preferable in the invented method to form the first sealing layer comprising a halide of an alkali metal or alkaline earth metal and to form the second sealing layer comprising a moisture proof resinous material on the end face of the laminate, as well as the face of the laminate on the opposite side to the substrate side. BRIEF DESCRIPTION OF THE DRAWINGS [0025] [0025]FIG. 1 is a sectional view showing an organic EL element corresponding to an embodiment of the present invention. [0026] [0026]FIG. 2 is a graph showing the transmittance in visual light region of an organic EL element prepared according to the method of Example 1.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS [0027] The embodiments of the present invention will now be illustrated in detail with reference to the drawings. [0028] [0028]FIG. 1 is a sectional view showing the structure of an organic EL element corresponding to an embodiment of the present invention. [0029] In this organic EL element, laminate 20 including electrode (anode) 2 (for example, transparent electrode), hole injecting and transporting layer 3, light emitting layer 4 and cathode 5 is formed on substrate 1 (for example, transparent glass substrate). Cathode 5 has a two-layer structure including first cathode layer 51 comprising, for example, a Ca thin film, and second cathode layer 52 comprising an Al thin film. Of individual layers constituting laminate 20, anode 2 is formed in plane shape in which terminal part 2 a extends off the other layers, and the other layers are formed such that their plane shapes are of the same size and in the same location. [0030] First sealing layer 6 comprising LiF is formed on overall of the top face (the surface on the opposite side to the substrate side) of cathode 5 of this laminate 20, overall of the end face of laminate 20 other than terminal part 2 a, and overall of the top face of terminal part 2 a. On overall of the outer side of this first sealing layer 6, second sealing layer 7 comprising a moisture proof epoxy resin is formed. Additionally, glass plate 8 for sealing is fixed on the top face of second sealing layer 7. [0031] In this organic EL element, cathode 5 of a two-layer structure including, for example, a Ca layer which is markedly liable to be oxidized is formed as an electrode arranged in the laminate on the opposite side to the substrate side. Oxidation of cathode 5 is effectively inhibited by providing first sealing layer 6 comprising LiF so as to cover this cathode 5. [0032] Additionally, first sealing layer 6 comprising LiF becomes resistant to crack formation by providing second sealing layer 7 comprising an epoxy resin on the outer side of first sealing layer 6. [0033] The arrangement of first sealing layer 6 comprising LiF so as to cover cathode 5 inhibits the contamination of an organic solvent, oxygen, or water contained in a liquid epoxy resin into light emitting layer 4 in the formation of second sealing layer 7. Consequently, the deterioration of light emitting layer 4 with time is reduced. [0034] In this connection, an organic EL element, in which light is radiated outwardly, at least through the cathode 5, preferably from both the anode 2 side and the cathode 5 side, can be obtained by configuring cathode 5 to a two-layer structure in which first cathode layer (a cathode layer on the light emitting layer 4 side) 51 comprises a material having a low work function and second cathode layer 52 has a work function higher than the aforementioned layer, and by setting the total thickness to 100 angstroms or less, as in this embodiment. It is preferable to use Ca or Mg as a material for first cathode layer 51 and to use aluminium (Al), silver (Ag), or gold (Au) as a material for second cathode layer 52. [0035] Also, a metal layer comprising for example Pt, Ir, Ni, Pd, Au or laminate including transparent conductive layer such as ITO and reflective layer such as Al can be used as the anode 2. [0036] The examples of the present invention will be described below. [0037] An organic EL element having the configuration of FIG. 1 was prepared in the following manner. [0038] Initially, square transparent glass substrate 1 having a thickness of 1.1 mm and a length in side of 150 mm was prepared, and this glass substrate 1 was cleaned. Next, using a sputtering apparatus, transparent IDIXO (In2O3-ZnO) film (anode) 2 was formed on glass substrate 1. A film-forming condition was, degree of vacuum: 1�10−4 Pa or less, sputtering gas: a gaseous mixture of Ar and O2 (flow rate ratio of Ar to O2 was 10:1), voltage: 320 V, electric current: 0.15 mA, film-forming time: 14 minutes. By this, the thickness of IDIXO film (anode) 2 was set to 1000 angstroms. In this connection, an ITO (In2O3-SnO2) film or the like may be formed as anode 2. [0039] Subsequently, glass substrate 1 was subjected to oxygen plasma treatment. Using “VPS 020” manufactured by Sanyu Electron Co., Ltd. as a plasma system, purging with oxygen was performed twice or three times, and oxygen plasma treatment was conducted under the condition of voltage: 10 mA, treatment time: 5 minutes. By this procedure, the surface of IDIXO film (anode) 2 on glass substrate 1 was oxygen-plasma-treated. [0040] All of the above steps were performed in a clean room. All of the following steps were carried out in a glove box. The inside of the glove box was in an atmosphere substantially free from oxygen and water (oxygen concentration: 0.01 ppm or less, dew-point of water: −70� C. or less). [0041] Initially, Bayer's “Baytron P” (a mixture of polyethylenedioxythiophene (PEDOT) and polystyrenesulfonic acid (PSS)] was mixed with polystyrenesulfonic acid in a ratio of “Baytron P” to PSS of 5 1. The resulting mixture was further diluted 1.5 times with water. [0042] PEDOT is a polymeric compound represented by the following chemical formula (1) and PSS is a polymeric compound represented by the following chemical formula (2). [0043] This fluid was applied by spin coating process onto IDIXO film (anode) 2 in which the surface had been oxygen-plasma-treated. The application condition was as follows: rotation speed: 3000 rpm, and rotation time: 45 seconds. Glass substrate 1 in this state was heated at 200� C. for 10 minutes to thereby form hole injecting and transporting layer 3 having a thickness of 600 angstroms on IDIXO film (anode) 2. [0044] Next, a polyfluorene derivative represented by the following chemical formula (3) was dissolved in xylene solvent. This solution was applied onto hole injecting and transporting layer 3 by spin coating process to thereby form light emitting layer 4 having a thickness of 800 angstroms on hole injecting and transporting layer 3. In this connection, a layer comprising, for example, poly(para-phenylenevinylene) may be formed as light emitting layer 4. [0045] Subsequently, a Ca thin film was formed as first cathode layer 51 on light emitting layer 4 by vacuum deposition process, and then an Al thin film was formed as second cathode layer 52 thereon. The film formation operations of both of the thin films were continuously performed using a vacuum deposition system arranged in a glove box. Initially, a Ca thin film having a thickness of 70 angstroms was formed in the condition that the initial degree of vacuum was about 1�10−6 torr and the film-forming rate was 3 angstroms per second, and after the degree of vacuum returned to about 1�10−6 torr, an Al thin film having a thickness of 10 angstroms was formed in the condition that the film-forming rate was 3 angstroms per second. [0046] By this procedure, laminate 20 including anode 2, hole injecting and transporting layer 3, light emitting layer 4, and cathode 5 of two-layer structure was formed on glass substrate 1. Of individual layers constituting laminate 20, anode 2 is formed in plane shape in which terminal part 2 a extended off the other layers, and the other layers were formed such that their plane shapes are of the same size in the same location. [0047] Next, a LiF thin film having a thickness of 500 angstroms was formed as first sealing layer 6 on glass substrate 1 in this state. This film formation was performed in the condition that the film-forming rate was 8 angstroms per second, after the film formation of second cathode layer 52 and after the degree of vacuum returned to about 1�10−6 torr. The film formation operations of first cathode layer 51, second cathode layer 52, and first sealing layer 6 were performed in the same vacuum deposition system without the opening of vacuum chamber. [0048] By this procedure, first sealing layer 6 comprising LiF was formed on overall of the top face (the surface on the opposite side to the substrate side) of cathode 5 of this laminate 20, overall the end face of laminate 20 other than terminal part 2 a, and overall of the top face of terminal part 2 a. [0049] Subsequently, glass substrate 1 taken out from the vacuum deposition system was cooled, and a thermosetting epoxy resin “DP pure 60” manufactured by Minnesota Mining & Manufacturing Co. was applied as second sealing layer 7 to overall of the outer side of first sealing layer 6 by dipping process. In this connection, second sealing layer 7 may be formed by using, for example, “STYCAST 1269A” manufactured by EMERSON & COMING CO. [0050] Next, transparent glass plate 8 having a thickness of 0.3 mm was placed on the top face of the above-formed second sealing layer 7, and glass substrate 1 in this state was placed on a hot plate in a glove box and was heated at 50� C. in the vacuum of about 0.1 torr for 12 hours. By this procedure, the epoxy resin was cured while removing bubbles, to thereby form second sealing layer 7 comprising epoxy resin having a thickness of 200 μm on overall of the outer side of first sealing layer 8. Additionally, glass plate 8 for sealing was fixed on the top face of second sealing layer 7. [0051] The organic EL element having the configuration of FIG. 1 was thus obtained. [0052] A LiF thin film having a thickness of 200 angstroms was formed as first sealing layer 6. Except this point, an organic EL element was prepared in the very same manner as in Example 1, except this. [0053] A LiF thin film having a thickness of 300 angstroms was formed as first sealing layer 6. Except this point, an organic EL element was prepared in the very same manner as in Example 1. [0054] A LiF thin film having a thickness of 400 angstroms was formed as first sealing layer 6. Except this point, an organic EL element was prepared in the very same manner as in Example 1. [0055] A LiF thin film having a thickness of 600 angstroms was formed as first sealing layer 6. Except this point, an organic EL element was prepared in the very same manner as in Example 1. [0056] Each of the organic EL elements of Examples 1 to 5 was allowed to emit light at a drive voltage of 8 V, and the luminance of the light was determined on the glass plate 8 side (on the cathode 5 side). Separately, each of the organic EL elements was allowed to emit light at varying drive voltages, and the luminance of the light was determined on the glass plate 8 side (on the cathode 5 side), and the minimum of the drive voltage at which the luminance was 5 cd/m2 or more was determined as “threshold voltage”. A luminance meter “BM-7” manufactured by Topcon Corporation was used in the determination of luminance. [0057] The luminance determination and the determination of threshold voltage were performed immediately after the preparation of the organic EL element (initial), and after the organic EL element was left in the condition at a temperature of 20� C. at humidity of 50% for one month. These results are shown in the following Table 1. TABLE 1 First Sealing Layer Threshold Voltage (V) Luminance (cd/m2) Thickness (Å) Initial After 1 month Initial After 1 month 200 3.2 3.6 200 60 300 3.1 3.2 160 100 400 2.9 3.4 190 160 500 3.0 3.1 180 160 600 3.2 3.5 100 110 [0058] As apparent from the results, the thickness of first sealing layer 6 of 200 angstroms is not preferred, since the luminance decreases to half or less after one month, although the initial luminance is high. This change with time is probably because sufficient sealing action by first sealing layer 6 could not be obtained since first sealing layer 6 was thin, and oxidation of first cathode layer 51 comprising calcium or deterioration of light emitting layer 4 occurred. [0059] In contrast, the thickness of first sealing layer 6 of not less than 300 angstroms is preferred, since decrease in luminance due to one-month storage is small and the luminance after one month is not less than 100 cd/m2. [0060] The thickness of first sealing layer 6 of 600 angstroms is not preferred, as the initial luminance is low. This is probably because it took much time to form the film of first sealing layer 6 and layers under this were exposed to heat over a long time and deterioration occurred particularly in light emitting layer 4. [0061] The film forming rate of first sealing layer 6 was set to 4 angstroms per second. Except this point, an organic EL element was manufactured in the very same manner as in Example 1. [0062] The film forming rate of first sealing layer 6 was set to 6 angstroms per second. Except this point, an organic EL element was manufactured in the very same manner as in Example 1. [0063] The film forming rate of first sealing layer 6 was set to 10 angstroms per second. Except this point, an organic EL element was manufactured in the very same manner as in Example 1. [0064] The film forming rate of first sealing layer 6 was set to 15 angstroms per second. Except this point, an organic EL element was manufactured in the very same manner as in Example 1. [0065] Each of the organic EL elements of Examples 6 to 9 was allowed to emit light at a drive voltage of 8 V, and the luminance of the light was determined on the glass plate 8 side (on the cathode 5 side). Separately, each of the organic EL elements was allowed to emit light at varying drive voltages, and the luminance of the light was determined on the glass plate 8 side (on the cathode 5 side), and the minimum of the drive voltage at which the luminance was 5 cd/m2 or more was determined as “threshold voltage”. A luminance meter “BM-7” manufactured by Topcon Corporation was used in the determination of luminance. [0066] The luminance determination and the determination of threshold voltage were performed immediately after the preparation of the organic EL element (initial). These results are shown in the following Table 2 with the result of TABLE 2 Film Forming Rate of First Initial Threshold Voltage Initial Luminance Sealing Layer (Å/sec.) (V) (cd/m2) 4 5.1 120 6 3.5 140 8 3.0 180 10 3.2 190 15 3.1 180 [0067] As apparent from the results, the film-forming rates of first sealing layer 6 of 4 angstroms per second and of 6 angstroms per second are not preferred, as the initial threshold voltages are high. This is probably because it took much time to yield the same thickness due to low film-forming rate of first sealing layer 6, and light emitting layer 4 was deteriorated due to long term exposure to heat. [0068] In contrast, the film-forming rate of first sealing layer 6 of not less than 8 angstroms per second is preferred since the threshold voltage is low. This is probably because deterioration of light emitting layer 4 was inhibited as it was exposed to heat for a short period of time in the film formation of first sealing layer 6. [0069] Additionally, the transmittance of the organic EL element obtained in Example 1 was determined. This determination was performed using a spectroscope manufactured by Hitachi Ltd. with air as base line, while placing pin hole 3 mm in diameter in a condenser unit. The result is shown as a graph in FIG. 2. As apparent from this graph, the transmittance of the organic EL element was not less than 50% nearly all over the visible light region. [0070] In this connection, the transmittance of glass substrate 1 having a thickness of 1.1 mm is about 75%, this organic EL element is found to have a visible light transmittance of about 70% of the glass substrate 1. [0071] These results show that the organic EL elements obtained in Examples 1 to 9 are organic EL elements in which light is radiated toward both electrode sides. [0072] In particular, when the thickness of first sealing layer 6 is set to 300 angstroms or more and the film-forming rate of first sealing layer 6 is set to 8 angstroms or more per second, the organic EL element can be satisfactorily sealed even when light is radiated to both electrode sides in the organic EL element. As a result, the satisfactory characteristic that light emits at high luminance at high efficiency only by the application of a low voltage can be ensured over a long time, even when light is radiated toward both electrode sides in the organic EL element. [0073] As described above, according to the invented organic EL element and manufacturing method thereof, the organic EL element can be satisfactorily sealed and change in characteristics with time can be inhibited, even when light is radiated to both electrode sides in the organic EL element, by specifying the material of the first sealant. Referenced byCiting PatentFiling datePublication dateApplicantTitleUS7109655Dec 22, 2003Sep 19, 2006Semiconductor Energy Laboratory Co., Ltd.Light emitting device and method for manufacturing the sameUS7298072May 14, 2002Nov 20, 2007Nova-Plasma Inc.Transparent support for organic light emitting deviceUS7312573Jul 29, 2005Dec 25, 2007Au Optronics Corp.Organic light emitting diode devicesUS7345420 *Mar 19, 2003Mar 18, 2008Pioneer CorporationOrganic electroluminescence display panel and method for manufacturing the sameUS7602120Oct 13, 2009Tdk CorporationElectroluminescence panel and method of making the sameUS7622861 *Nov 24, 2009Hitachi Displays, Ltd.Organic electroluminescent display device having two sealed EL display panelsUS7642714 *Jun 19, 2003Jan 5, 2010Koninklijke Philips Electronics, N.V.Electroluminescent device with a transparent cathodeUS7648925Jul 12, 2007Jan 19, 2010Vitex Systems, Inc.Multilayer barrier stacks and methods of making multilayer barrier stacksUS7727601Mar 29, 2007Jun 1, 2010Vitex Systems, Inc.Method for edge sealing barrier filmsUS7767498Aug 3, 2010Vitex Systems, Inc.Encapsulated devices and method of makingUS7888862 *Oct 24, 2007Feb 15, 2011Hitachi Displays, Ltd.Organic electroluminescent display deviceUS7948175Sep 6, 2006May 24, 2011Semiconductor Energy Laboratory Co., Ltd.Light emitting device and method for manufacturing the sameUS7982397 *Jul 19, 2011Samsung Mobile Display Co., LtdOrganic electroluminescence display device with moisture absorbing materialUS8018077Sep 13, 2011Robert Bosch GmbhElectromechanical system having a controlled atmosphere, and method of fabricating sameUS8330363Dec 11, 2012Semiconductor Energy Laboratory Co., Ltd.Light emitting device and method for manufacturing the sameUS8759822Nov 15, 2012Jun 24, 2014Samsung Display Co., Ltd.Organic light-emitting display apparatus and method of manufacturing the sameUS8895961 *Dec 25, 2008Nov 25, 2014Sumitomo Chemical Company, LimitedPolymer light emitting element, method for manufacturing the same and polymer light emitting display deviceUS8900366Apr 22, 2005Dec 2, 2014Samsung Display Co., Ltd.Apparatus for depositing a multilayer coating on discrete sheetsUS8957836 *Apr 3, 2007Feb 17, 2015Semiconductor Energy Laboratory Co., Ltd.Method for driving light-emitting deviceUS20040070334 *Feb 27, 2002Apr 15, 2004Buckley Alastair RobertEncapsulated electrodeUS20040174115 *May 14, 2002Sep 9, 2004Grzegorz CzeremuszkinTransparent support for organic light emitting deviceUS20050046349 *Aug 25, 2004Mar 3, 2005Atsushi TanakaOLED display and production method thereofUS20050179378 *Feb 11, 2005Aug 18, 2005Hiroshi OookaOrganic electroluminescent display deviceUS20050218796 *Mar 19, 2003Oct 6, 2005Hirofumi KubotaOrganic electroluminescence display panel and method for manufacturing the sameUS20050275348 *Apr 26, 2005Dec 15, 2005Choi Dong-SooOrganic electroluminescence display deviceUS20060103321 *Jun 19, 2003May 18, 2006Helmut BechtelElectroluminescent device with a transparent cathodeUS20070145894 *Dec 22, 2006Jun 28, 2007Fujifilm CorporationOrganic electroluminescence device and producing method thereofUS20070159097 *Dec 26, 2006Jul 12, 2007Tdk CorporationElectroluminescence panel and method of making the sameUS20070164376 *Mar 29, 2007Jul 19, 2007Burrows Paul EMethod for edge sealing barrier filmsUS20070177088 *Apr 3, 2007Aug 2, 2007Semiconductor Energy Laboratory Co., Ltd.Light emitting device and electronic apparatus using the sameUS20080054800 *Oct 24, 2007Mar 6, 2008Hiroshi OookaOrganic electroluminescent display deviceUS20080318033 *Mar 22, 2006Dec 25, 2008Leybold Optics GmbhCoated Substrate with a Temporary Protective Layer and Method for Production ThereofUS20100213621 *Aug 26, 2010Wei-Chung SunMoisture-proof device, moisture-proof IC, and method for increasing moisture-proof capability of ICUS20100270544 *Dec 25, 2008Oct 28, 2010Sumitomo Chemical Company, LimitedPolymer light emitting element, method for manufacturing the same and polymer light emitting display deviceUS20110221335 *Sep 15, 2011Semiconductor Energy Laboratory Co., Ltd.Light Emitting Device and Method for Manufacturing the SameEP1758181A2 *Apr 14, 2003Feb 28, 2007Vitex Systems Inc.Multilayer coatings for environmentally sensitive devices including a plasma protective layerEP2747164A1 *Oct 31, 2013Jun 25, 2014Samsung Display Co., Ltd.Organic light emitting display apparatus and manufacturing method thereofWO2002069412A1 *Feb 27, 2002Sep 6, 2002Microemissive Displays LimitedAn encapsulated electrode* Cited by examinerClassifications U.S. Classification428/690, 428/413, 313/506, 428/917, 313/512, 427/66, 257/100, 313/504International ClassificationH05B33/10, H01L51/52, H05B33/26, H01L51/50, H05B33/04Cooperative ClassificationH01L51/5253, H01L51/5246, Y10T428/31511, Y10S428/917, H05B33/04, H01L51/5221, H05B33/10European ClassificationH01L51/52C, H05B33/10, H05B33/04Legal EventsDateCodeEventDescriptionJun 25, 2001ASAssignmentOwner name: SEIKO EPSON CORPORATION, JAPANFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:MORII, KATSUYUKI;REEL/FRAME:011929/0247Effective date: 20010516Feb 9, 2007FPAYFee paymentYear of fee payment: 4Feb 10, 2011FPAYFee paymentYear of fee payment: 8Feb 25, 2015FPAYFee paymentYear of fee payment: 12Jan 14, 2016ASAssignmentOwner name: BOE TECHNOLOGY GROUP CO., LTD., CHINAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:BOE TECHNOLOGY (HK) LIMITED;REEL/FRAME:037515/0082Effective date: 20150214Owner name: BOE TECHNOLOGY (HK) LIMITED, CHINAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:SEIKO EPSON CORPORATION;REEL/FRAME:037515/0050Effective date: 20141118RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services