US6592663B1 - Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate - Google Patents
US6592663B1
US6592663B1 US09590063 US59006300A US6592663B1 US 6592663 B1 US6592663 B1 US 6592663B1 US 09590063 US09590063 US 09590063 US 59006300 A US59006300 A US 59006300A US 6592663 B1 US6592663 B1 US 6592663B1
US09590063
Seiji Sarayama
A method of making a bulk crystal substrate of a GaN single crystal includes the steps of forming a molten flux of an alkali metal in a reaction vessel and causing a growth of a GaN single crystal from the molten flux, wherein the growth is continued while replenishing a compound containing N from a source outside the reaction vessel.
The present invention generally relates to semiconductor devices and more particularly to a semiconductor device having a GaN bulk crystal substrate.
GaN is a III-V compound semiconductor material having a large bandgap of blue to ultraviolet wavelength energy. Thus, intensive investigations are being made with regard to development of optical semiconductor devices having a GaN active layer for use particularly in optical information storage devices including a digital video data recorder (DVD). By using such a light emitting semiconductor device producing blue to ultraviolet wavelength optical radiation for the optical source, it is possible to increase the recording density of optical information storage devices.
Conventionally, a laser diode or light-emitting diode having a GaN active layer has been constructed on a sapphire substrate in view of the absence of technology of forming a GaN bulk crystal substrate.
FIG. 1 shows the construction of a conventional GaN laser diode according to Nakamura, S., et al., Jpn. J. Appl. Phys. vol.36 (1997) pp.L1568-L1571, Part 2, No.12A, Dec. 1, 1997, constructed on a sapphire substrate 1.
Referring to FIG. 1, the sapphire substrate 1 has a (0001) principal surface covered by a low-temperature GaN buffer layer 2, and includes a GaN buffer layer 3 of n-type grown further on the buffer layer 2. The GaN buffer layer 3 includes a lower layer part 3 a and an upper layer part 3 b both of n-type, with an intervening SiO2 mask pattern 4 provided such that the SiO2 mask pattern 4 is embedded between the lower layer part 3 a and the upper layer part 3 b. More specifically, the SiO2 mask pattern 4 is formed on the lower GaN buffer layer part 3 a, followed by a patterning process thereof to form an opening 4A in the SiO2 mask pattern 4.
After the formation of the SiO2 mask pattern 4, the upper GaN layer part 3 b is formed by an epitaxial lateral overgrowth (ELO) process in which the layer 3 b is grown laterally on the SiO2 mask 4. Thereby, desired epitaxy is achieved with regard to the lower GaN layer part 3 a at the opening 4A in the SiO2 mask pattern 4. By growing the GaN layer part 3 b as such, it is possible to prevent the defects, which are formed in the GaN layer part 3 a due to the large lattice misfit between GaN and sapphire, from penetrating into the upper GaN layer part 3 b.
On the upper GaN layer 3 b, a strained super-lattice structure 5 having an n-type Al0.14Ga0.86N/GaN modulation doped structure is formed, with an intervening InGaN layer 5A of the n-type having a composition In0.1Ga0.9N interposed between the upper GaN layer part 3 b and the strained superlattice structure 5. By providing the strained superlattice structure 5 as such, dislocations that are originated at the surface of the sapphire substrate 1 and extending in the upward direction are intercepted and trapped.
On the strained superlattice structure 5, a lower cladding layer 6 of n-type GaN is formed, and an active layer 7 having an MQW structure of In0.01Ga0.98N/In0.15Ga0.85N is formed on the cladding layer 6. Further, an upper cladding layer 8 of p-type GaN is formed on the active layer 7, with an intervening electron blocking layer 7A of p-type AlGaN having a composition of Al0.2Ga0.8N interposed between the active layer 7 and the upper cladding layer 8.
On the upper cladding layer 8, another strained superlattice structure 9 of a p-type Al0.14Ga0.86N/GaN modulation doped structure is formed such that the superlattice structure 9 is covered by a p-type GaN cap layer 10. Further, a p-type electrode 11 is formed in contact with the cap layer 10 and an n-type electrode 12 is formed in contact with the n-type GaN buffer layer 3 b.
It is reported that the laser diode of FIG. 1 oscillates successfully with a practical lifetime, indicating that the defect density in the active layer 7 is reduced successfully.
On the other hand, the laser diode of FIG. 1 cannot eliminate the defects completely, and there remain substantial defects particularly in correspondence to the part on the SiO2 mask 4 as represented in FIG. 2. See Nakamura S. et al., op cit. It should be noted that such defects formed on the SiO2 mask 4 easily penetrate through the strained superlattice structure 5 and the lower cladding layer 6 and reach the active layer 7.
In view of the foregoing concentration of the defects in the central part of the SiO2 mask pattern 4, the laser diode of FIG. 1 uses the part of the semiconductor epitaxial structure located on the opening 4A of the SiO2 mask 4, by forming a mesa structure M in correspondence to the opening 4A. However, the defect-free region formed on the opening 4A has a lateral size of only several microns, and thus, it is difficult to construct a high-power laser diode based on the construction of FIG. 1. When the laser diode of FIG. 1 is driven at a high power, the area of optical emission in the active region extends inevitably across the defects, and the laser diode is damaged as a result of optical absorption caused by the defects. Further, the laser diode of FIG. 1 having such a construction has other various drawbacks associated with the defects in the semiconductor epitaxial layers, such as large threshold current, limited lifetime, and the like. Further, the laser diode of FIG. 1 has a drawback, in view of the fact that the sapphire substrate is an insulating substrate, in that it is not possible to provide an electrode on the substrate. As represented in FIG. 1, it is necessary to expose the top surface of the n-type GaN buffer layer 3 by an etching process in order to provide the n-type electrode 12, while such an etching process complicates the fabrication process of the laser diode. In addition, the increased distance between the active layer 7 and the n-type electrode 12 causes the problem of increased resistance of the current path, while such an increased resistance of the current path deteriorates the high-speed response of the laser diode.
Further, the conventional laser diode of FIG. 1 suffers from the problem of poor quality of mirror surfaces defining the optical cavity. Due to the fact that the sapphire single crystal constituting the substrate 1 belongs to hexagonal crystal system, formation of the optical cavity cannot be achieved by a simple cleaving process. It has been therefore necessary to form the mirror surfaces, when fabricating the laser diode of FIG. 1 by conducting a dry etching process, while the mirror surface thus formed by a dry etching process has a poor quality.
Because of the foregoing reasons, as well as because of other various reasons not mentioned here, it is desired to form the substrate of the GaN laser diode by a bulk crystal GaN and form the laser diode directly on the GaN bulk crystal substrate.
With regard to the art of growing a bulk crystal GaN, there is a successful attempt reported by Porowski (Porowski, S., J. Crystal Growth 189/190 (1998) pp.153-158, in which a GaN bulk crystal is synthesized from a Ga melt under an elevated temperature of 1400-1700° C. and an elevated N2 pressure of 12-20 kbar (1.2-2 GPa). This process, however, can only provide an extremely small crystal in the order of 1 cm in diameter at best. Further the process of Porowski requires a specially built pressure-resistant apparatus and a long time is needed for loading or unloading a source material, or increasing or decreasing the pressure and temperature. Thus, the process of this prior art would not be a realistic solution for mass-production of a GaN bulk crystal substrate. It should be noted that the reaction vessel of Porowski has to withstand the foregoing extremely high pressure, which is rarely encountered in industrial process, under the temperature exceeding 1400° C.
Further, there is a known process of growing a GaN bulk crystal without using an extremely high pressure environment for growing a GaN bulk crystal as reported by Yamane, H., et al., Chem. Mater. 1997, 9, 413-416. More specifically, the process of Yamane et al. successfully avoids the use of the extremely high-pressure used in Porowski, by conducting the growth of the GaN bulk crystal from a Ga melt in the presence of a Na flux.
According to the process of Yamane, a metallic Ga source and a NaN3 (sodium azide) flux are confined in a pressure-resistance reaction vessel of stainless steel together with a N2 atmosphere, and the reaction vessel is heated to a temperature of 600-800° C. and held for a duration of 24-100 hours. As a result of the heating, the pressure inside the reaction vessel is elevated to the order of 100 kg/cm2 (about 10 MPa), which is substantially lower than the pressure used by Porowski. As a result of the reaction, GaN crystals are precipitated from the melt of a Na—Ga system. In view of the relatively low pressure and low temperature needed for the reaction, the process of Yamane et al. is much easier to implement.
On the other hand, the process of Yamane relies upon the initially confined N2 molecules in the atmosphere and the N atoms contained in the NaN3 flux for the source of N. Thus, when the reaction proceeds, the N2 molecules in the atmosphere or the N atoms in the Na—Ga melt are depleted with the precipitation of the GaN crystal, and there appears a limitation in growing a large bulk crystal of GaN. The GaN crystals obtained by the process of Yamane et al. typically have a size of 1 mm or less in diameter. Thus, the process of Yamane et al. op cit., while being successful in forming a GaN bulk crystal at a relatively low pressure and temperature, cannot be used for a mass production of a GaN substrate in the industrial base.
Accordingly, it is a general object of the present invention to provide a novel and useful GaN semiconductor device having a bulk crystal substrate wherein the foregoing problems are eliminated.
Another and more specific object of the present invention is to provide a process of making a bulk crystal substrate of a GaN single crystal.
Another object of the present invention is to provide a process of fabricating a GaN semiconductor device having a bulk crystal substrate of a GaN single crystal.
Another object of the present invention is to provide a bulk crystal substrate of a single crystal GaN.
Another object of the present invention is to provide an optical semiconductor device having a bulk crystal substrate of a GaN single crystal.
Another object of the present invention is to provide an electron device having a bulk crystal substrate of a GaN single crystal.
Another object of the present invention is to provide an apparatus for making a bulk crystal substrate of a GaN single crystal.
According to the present invention, a high-quality GaN bulk crystal substrate is obtained with a process suitable for mass-production, by continuously supplying N so as to compensate for the depletion of N occurring in the system in which precipitation of a GaN single crystal takes place. By using the GaN bulk crystal substrate thus obtained, it is possible to fabricate an optical semiconductor device that produces an optical radiation of blue to ultraviolet wavelength with a large optical power. Further, the GaN bulk crystal substrate can be used as a substrate of an electron device such as HEMT.
FIG. 1 is a diagram showing the construction of a conventional laser diode constructed on a sapphire substrate;
FIG. 2 is a diagram showing the problem associated with the laser diode of FIG. 1;
FIG. 3 is a diagram showing the construction of a growth apparatus used in a first embodiment of the present invention for growing a GaN bulk crystal;
FIGS. 4A and 4B are diagrams showing a part of the apparatus of FIG. 3 in detail;
FIG. 5 is a diagram showing a cathode luminescent spectrum of a GaN bulk crystal obtained in the first embodiment;
FIG. 6 is a diagram showing a control of GaN composition in the growth apparatus of FIG. 3;
FIG. 7 is a diagram showing the construction of a growth apparatus used in a second embodiment of the present invention for growing a GaN bulk crystal;
FIG. 8 is a diagram showing the construction of a growth apparatus used in a third embodiment of the present invention for growing a GaN bulk crystal;
FIG. 9 is a diagram showing the construction of a growth apparatus used in a fourth embodiment of the present invention for growing a GaN bulk crystal;
FIG. 10 is a diagram showing the construction of a growth apparatus used in a fifth embodiment of the present invention for growing a GaN bulk crystal;
FIG. 11 is a diagram showing the construction of a growth apparatus used in a sixth embodiment of the present invention for growing a GaN bulk crystal;
FIG. 12 is a diagram showing the construction of a growth apparatus used in a seventh embodiment of the present invention for growing a GaN bulk crystal;
FIG. 13 is a diagram showing the construction of a seed crystal used in the growth apparatus of FIG. 12;
FIG. 14 is a diagram showing the construction of a growth apparatus used in an eighth embodiment of the present invention for growing a GaN bulk crystal;
FIGS. 15A and 15B are diagrams showing a part of the growth apparatus of FIG. 14;
FIG. 16 is a diagram showing the growth apparatus of FIG. 14 in the state in which a growth of the GaN bulk crystal has been made;
FIG. 17 is a diagram showing the construction of a growth apparatus used in a ninth embodiment of the present invention for growing a GaN bulk crystal;
FIG. 18 is a diagram showing the construction of a growth apparatus used in a tenth embodiment of the present invention for growing a GaN bulk crystal;
FIG. 19 is a diagram showing X-ray diffraction data obtained for a GaN bulk crystal according to an eleventh embodiment of the present invention;
FIG. 20 is a diagram showing the construction of a laser diode having a GaN bulk crystal substrate according to a twelfth embodiment of the present invention; and
FIG. 21 is a diagram showing the construction of a HEMT having a GaN bulk crystal substrate according to a thirteenth embodiment of the present invention.
FIG. 3 shows the construction of a growth apparatus 100 used in a first embodiment of the present invention for growing a GaN bulk crystal.
Referring to FIG. 3, the growth apparatus 100 includes a pressure-resistant reaction vessel 101 typically of a stainless steel having an inner diameter of about 75 mm and a length of about 300 mm and accommodates therein a crucible 102 of Nb or BN. As will be explained later, the crucible 102 is loaded with a starting material of metallic Ga and a NaN3 flux and is confined in the reaction vessel 101 together with an N2 atmosphere 107. Further, the reaction vessel 101 is supplied with N2 or a gaseous compound of N from an external source via a regulator valve 109 and an inlet 108. The reaction vessel 101 thus loaded with the starting material in the crucible 102 is heated by energizing heaters 110 and 111 to a temperature of 650-850° C., and the pressure inside the reaction vessel is regulated to a moderate value of about 5 MPa by controlling the valve 109. By holding the temperature and the pressure, a precipitation of GaN bulk crystal takes place from a Na—Ga melt, which is formed in the crucible 102 as a result of the melting of the starting material.
FIG. 4A shows the loading of the starting material in the crucible 102, while FIG. 4B shows the state in which the source material has caused a melting.
Referring to FIG. 4A, a high-purity metallic Ga and a high-purity metallic Na are weighed carefully and loaded into the crucible 102, wherein the foregoing process of weighing and loading are conducted in the N2 atmosphere. It is also possible to use high-purity NaN3 in place of high-purity metallic Na source.
In the state of FIG. 4B, on the other hand, there appears a melt 102A of the Na—Ga system in the crucible 102 and crystallization of GaN takes place from various parts of the melt 102A including a free surface of the melt and a sidewall or bottom wall of the crucible 102. There, it was observed that a large single crystal 102B of GaN grows on the melt free surface contacting with the atmosphere and fine needle-like GaN crystals 102C grow on the sidewall or bottom wall of the crucible 102.
With the growth of the GaN crystals, a particularly with the growth of the GaN single crystal 102B, N in the atmosphere is consumed and the pressure inside the reaction vessel gradually falls as a result of depletion of N in the atmosphere. Thus, in the present embodiment, the depletion of N in the atmosphere 107 is compensated for by replenishing N2 or a compound of N such as NH3 from an external source. Thereby, the growth of the GaN single crystal 102B continues at the melt free surface and a large GaN single crystal suitable for use in an optical semiconductor device such as a laser diode or light-emitting diode as a GaN bulk crystal substrate is obtained. The construction of FIG. 3 can easily produce the GaN single crystal 102B with a thickness of 100 μm or more. The GaN single crystal 102B thus formed at the temperature of 650-850° C. has a hexagonal crystal symmetry.
FIG. 5 shows the cathode luminescent spectrum of the GaN single crystal 102B thus obtained in comparison with the cathode luminescent spectrum of a GaN thick film grown on a sapphire substrate or an SiC substrate.
Referring to FIG. 5, it can be seen that the GaN crystal 102B of the present embodiment shows a distinct and strong peak corresponding to the band edge of GaN at the wavelength of about 360 nm. Further, it can be seen that no other peak exists in the GaN single crystal 102B of the present embodiment. The result of FIG. 5 indicates that the GaN crystal 102B thus formed has a defect density of less than 102-103 cm−3. Thus, the GaN single crystal 102B is suitable for use as a bulk GaN substrate of various optical semiconductor devices including a laser diode and a light-emitting diode as noted already. Hereinafter, the GaN single crystal 102B will be called a GaN bulk crystal in view of application to a GaN bulk crystal substrate.
Contrary to the present embodiment, the GaN thick film formed on the sapphire substrate or formed on the SiC substrate shows a remarkable peak at the wavelength of about 600 nm corresponding to deep impurity levels. This clearly indicates that the GaN thick film thus formed on a sapphire substrate or an SiC substrate contains a substantial amount of defects. Associated with the high level of defects, it can be seen that the peak strength for the band edge is substantially smaller than the case of the GaN bulk crystal 102B of the present embodiment.
In the growth process of FIG. 4B, it should be noted that there appears also an intermetallic compound 102D of GaNa along the sidewall and bottom surface of the crucible 102 indicated in FIG. 4B by a broken line. Thus, the region represented in FIG. 4B by the broken line in fact includes the fine GaN crystals 102C and the GaNa intermetallic compound 102D in the form of a mixture. The GaN fine crystals 102C or the GaNa intermetallic compound 102D thus formed releases Ga into the melt 102A, and the Ga atoms thus released contribute to the growth of the GaN bulk crystal 102B when transported to the melt surface.
Thus, by continuously replenishing N2 or NH3, the growth process of the GaN bulk crystal 102B continues until Ga in the melt 102A is used up.
FIG. 6 shows the control of the N2 pressure in the atmosphere 107 with the growth of the GaN bulk crystal 102B from the melt 102A.
Referring to FIG. 6, it can be seen that the N2 pressure a necessary for maintaining the stoichiometric composition for the GaN bulk crystal 102B changes depending on the Ga content in the melt 102A represented in the horizontal axis. When the N2 pressure in the atmosphere 107 is fixed (a1=a2), it is not possible to maintain the stoichiometric composition for the GaN bulk crystal 102B. Thus, the present invention changes the N2 pressure a in the atmosphere 107 with the progress of growth of the GaN bulk crystal 102B as represented as a1≠a2.
FIG. 7 shows the construction of a growth apparatus 200 according to a second embodiment of the present invention, wherein those parts corresponding to the parts described previously are designated by the same reference numerals and the description there of will be omitted.
Referring to FIG. 7, the present embodiment uses heaters 111A and 111B in place of the heater 111 and induces a temperature gradient in the melt 102A for facilitating transport of Ga from the GaN fine crystals 102C or the GaNa intermetallic compound 102D to the melt surface.
More specifically, the heater 111B is provided in correspondence to the bottom part of the crucible 102 and controls, together with the heart 11A, the melt temperature at the bottom part of the crucible 102 lower than the melt surface. As a result of energization of the heaters 111A and 111B, a temperature gradient shown in FIG. 7 is induced.
Due to the increased temperature at the bottom part of the crucible 102, undesirable precipitation of GaN crystals on bottom surface of the crucible 102 is minimized, and the growth of the GaN bulk crystal 102B on the melt surface is promoted substantially. When a GaN fine crystal 102C is formed, such a GaN fine crystal 102C is immediately dissolved into the melt 102A and no substantial deposition occurs on the bottom part of the crucible 102. Further, the intermetallic compound of GaNa, formed at a temperature lower than about 530° C., acts also as the source of Ga and Na in the melt 102A.
Similarly to the first embodiment, the GaN bulk crystal 102B formed according to the present embodiment has a defect density in the order of 102-103 cm−3 or less. Thus, the GaN bulk crystal 102B is suitable for a bulk GaN substrate of various optical semiconductor devices including a laser diode and a light-emitting diode.
FIG. 8 shows the construction of a growth apparatus 300 according to a third embodiment of the present invention, wherein those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted.
Referring to FIG. 8, the present embodiment is a modification of the embodiment of FIG. 7 and uses the heaters 110 and 111, described with reference to the growth apparatus 100 for inducing the desired temperature gradient. As other aspects of the present embodiment are substantially the same as those of the previous embodiment, further description will be omitted.
FIG. 9 shows the construction of a growth apparatus 400 according to a fourth embodiment of the present invention, wherein those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted.
Referring to FIG. 9, the growth apparatus 400 has a construction similar to that of FIG. 3, except that there is provided a container 103 holding a metallic Ga source 104 inside the reaction vessel 101. The container 103 is provided at a first end of a tube 103A extending outside of the reaction vessel 101, and there is provided a pressure regulator 106 at a second, opposite end of the tube 103. The pressure regulator 106 is supplied with a pressurized N2 gas from an external source and causes a molten Ga, formed in the container 103 as a result of heating, to drip to the Na—Ga melt 102A in the crucible 102 via a hole 105 formed at a bottom part of the container 103.
According to the construction of FIG. 9, depletion of Ga in the melt 102A is replenished from the Ga source 104 and a thickness of 300 μm or more is obtained for the GaN bulk crystal 102B as a result of the continuous crystal growth.
Similarly to the previous embodiments, the GaN bulk crystal 102B formed according to the present embodiment has a defect density of 102-103 cm−3 or less. Thus, the GaN bulk crystal 102B of the present embodiment is suitable for use as a bulk GaN substrate of various optical semiconductor devices including a laser diode and a light-emitting diode.
FIG. 10 shows the construction of a growth apparatus 500 according to a fifth embodiment of the present invention, wherein those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted.
Referring to FIG. 10, the growth apparatus 500 has a construction similar to that of the growth apparatus of FIG. 9, except that there is provided an outer pressure vessel 112 outside the reaction vessel 101, and the space between the reaction vessel 101 and the outer pressure vessel 112 is filled with a pressurized gas such as N2, which is introduced via a regulator 114 and an inlet 113.
By providing the pressure vessel 112 outside the reaction vessel 101, the pressurized reaction vessel 101 is supported from outside and the design of the reaction vessel 101 becomes substantially easier. As represented in FIG. 10, there is provided a thermal insulator 115 between the heater 110 or 111 and the outer pressure vessel 112 and the temperature rise of the pressure vessel 112 is avoided. Thereby, the pressure vessel 112 maintains a large mechanical strength even when the inner, reaction vessel 101 is heated to the temperature exceeding 600 or 700° C. In order to avoid the decrease of mechanical strength, it is possible to provide a water cooling system (not shown) on the outer pressure vessel 112.
The outer pressure vessel 112 can be provided also to the growing apparatuses 100-300 explained before as well as to the growing apparatuses to be described hereinafter.
As other features of the present embodiment are substantially the same as those of the previous embodiments, further description thereof will be omitted.
FIG. 11 shows the construction of a growing apparatus 600 according to a sixth embodiment of the present invention, wherein those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted.
Referring to FIG. 11, the growing apparatus 600 has a construction similar to that of the growing apparatus 100 of FIG. 3, except that there is provided a holder 601 holding a Ga—Na melt outside the reaction vessel 101 and the Ga—Na melt in the holder 601 is supplied into the reaction vessel 101 and to the melt 102A in the crucible 102 via a tube 601A penetrating through a wall of the reaction vessel 101, in response to a pressurization of the holder 601 by a pressurized gas such as an N2 gas supplied via a line 602.
According to the present embodiment, the depletion of Ga in the melt 102A is replenished together with the Na flux, and the growth of the GaN bulk crystal 102B at the free surface of the melt 102A is conducted continuously. It should be noted that depletion of N in the system is also replenished by the external N source similarly to the previous embodiments. As a result, a high-quality GaN bulk crystal suitable for use as a substrate of various optical semiconductor devices is obtained with a thickness well exceeding 100 μm, generally about 300 μm or more.
FIG. 12 shows the construction of a growth apparatus 700 according to a seventh embodiment of the present invention, wherein those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted.
Referring to FIG. 12, the growing apparatus 700 has a construction similar to that of the growing apparatus 600 of the previous embodiment, except that there is provided a rod 702 carrying a seed crystal 701 at a tip end thereof in contact with the free surface of the melt 102A in the crucible 102. Further there is provided a motor 703 for pulling up the rod 702, and there occurs a continuous growth of the GaN bulk crystal 102B at the melt surface with the pulling up of the rod 702. Thereby, an ingot of a GaN bulk crystal is obtained.
By slicing the GaN bulk crystal ingot thus obtained, it is possible to mass produce the GaN bulk crystal substrate for use in various optical semiconductor devices including a laser diode and a light-emitting diode.
FIG. 13 shows an example of the seed crystal 701 provided at the tip end of the rod 702.
Referring to FIG. 13, the seed crystal 702 is formed to have a slab shape with a width w and a thickness d corresponding to the width and thickness of the GaN substrate to be formed. Thus, by pulling up the rod 702 straight in the upward direction, a slab-shaped GaN bulk crystal is grown continuously. Thus, by merely polishing the surface of the GaN bulk crystal slab, followed by a cleaving process, it is possible to mass-produce the GaN bulk crystal substrate having a quality suitable for use in various optical semiconductor devices including a laser diode and a light-emitting diode.
As other features of the present embodiment is more or less the same as those of the previous embodiments, further description thereof will be omitted.
FIG. 14 shows the construction of a growing apparatus 800 according to an eighth embodiment of the present invention, wherein those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted.
Referring to FIG. 14, the growing apparatus 800 has a construction similar to that of the growing apparatus 700 of the previous embodiment, except that a cover member 803 is provided so as to cover the free surface of the melt 102A. Further, the container 601 of a Na—Ga melt is eliminated and a container 801 having a heating mechanism 801A and containing therein a molten Na is provided outside the reaction vessel 101. Thereby, a vapor of Na is supplied from the container 801 into the interior of the reaction vessel 101 via a tube 802 and the Na vapor is added to the atmosphere 107 therein.
According to the present embodiment, uncontrolled precipitation of the GaN fine crystals 102C on the sidewall or bottom surface of the crucible (see FIG. 4B) is minimized, by controlling the vapor pressure of Na from the container 801. Further, no GaN precipitation occurs on the melt free surface, as the free surface of the melt 102A is covered by the cover member 803, except for a central part of the melt where there is formed an opening 803A in the cover member 803 for allowing the seed crystal 701 on the rod 702 to make a contact with the surface of the melt 102A.
Thus, according to the construction of FIG. 14, the Na vapor flux acts selectively at the part of the melt 102A where the growth of the bulk GaN ingot is made, and the uncontrolled precipitation of the GaN fine crystals 102C is effectively suppressed.
It should be noted that cover member 803 has a variable geometry construction formed of a number of small, fan-shaped members, in which the opening 803A can be changed with the growth of the GaN bulk crystal 102B in the form of ingot by moving the fan-shaped members in a direction of an arrow Q as represented in FIGS. 15A and 15B, wherein FIG. 15A shows the state in which the central opening 803A of the cover member 803 is closed while FIG. 15B shows the state in which the opening 803A has been expanded for allowing the growth of the GaN bulk crystal ingot 102B as represented in FIG. 16. It should be noted that FIG. 16 shows the growing apparatus 800 in the state that there occurred a growth of the GaN bulk crystal 102B in the form of ingot.
FIG. 17 shows the construction of a growing apparatus 900 according to a tenth embodiment of the present invention, wherein those parts corresponding to the parts described previously are designated by the same reference numeral and the description thereof will be omitted.
Referring to FIG. 17, the growing apparatus 900 has a construction similar to that of the growing apparatus 800 of the previous embodiment, except that the tube 802 supplying the Na vapor flux has a sleeve part 802A surrounding the rod 702. The sleeve part 802A extends along the rod 702 and has an opening 802C in correspondence to the surface of the melt 102A where the opening 803A is formed in the cover member 803 for the growth of the GaN bulk crystal 102B.
According to the construction of FIG. 17, the Na flux is supplied selectively to the part where the growth of the GaN bulk crystal 102B takes place and an efficient growth becomes possible.
As other aspects of the present embodiment are the same as those of the previous embodiment, further description thereof will be omitted.
FIG. 18 shows the construction of a growing apparatus 1000 according to a ninth embodiment of the present invention wherein those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted.
Referring to FIG. 18, the growing apparatus 1000 has a construction similar to that of the growing apparatus 700 of FIG. 12, except that the rod 702 driven by the motor 703 and pulling up the seed 701 in the upward direction is replaced by a rod 702′ driven by a motor 703′ and pulls down a seed 701′ in the downward direction. Thus, as represented in FIG. 18 the GaN bulk crystal 102B forms an ingot grown inside the melt 102A. As other aspects of the present invention is the same as those described before, further description of the present embodiment will be omitted.
In any of the foregoing first through tenth embodiments, the grown of the GaN bulk crystal 102B has been achieved at the temperature of 650-850° C. under the presence of a Na flux. As mentioned before, the GaN bulk crystal 102B thus obtained has a symmetry of hexagonal crystal system.
On the other hand, the inventor of the present invention has discovered that a cubic GaN crystal is obtained as the bulk GaN-crystal 102B provided that the growth is made at a temperature of less than 600° C. under the presence of Na, or when the growth is made at a temperature of 650-850° C. under the presence of K. K may be introduced into the system in the form of a high-purity metallic K starting material, similarly to the case represented in FIG. 4A.
From the x-ray diffraction peak position data, it was confirmed that the cubic GaN bulk crystal 102B thus formed has a cubic lattice constant a0 of 4.5063±0.0009 Å. FIG. 19 shows x-ray diffraction intensity data obtained for a GaN bulk crystal grown by the apparatus of FIG. 3 as the bulk crystal 102B at a temperature of 750° C. under the total pressure of 7 MPa in the reaction vessel 101. In FIG. 19, it should be noted that the Of represents the structural factor obtained from the diffraction intensity data for each of the reflections (h k 1) and s represents the error factor of the measurement, while Fc represents the structural factor calculated from a cubic zinc blende structure. A reliability factor, R, of 2.1% demonstrates the well agreement of Of and Fc, where R is defined as:
R=Σ|F0−Fc/ΣF0.
Referring to-FIG. 19, it can be seen that there is an excellent agreement between the observed structural factor and the calculated structural factor assuming the cubic zinc blende structure for the obtained GaN bulk crystal 102B. It can be safely concluded that the GaN bulk crystal 102B obtained in the present embodiment is a 100% cubic GaN crystal. From the X-ray diffraction analysis, existence of hexagonal GaN crystal was not detected. Further it was confirmed that the cubic GaN bulk crystal 102B thus formed provides a cathode luminescent peak substantially identical with the spectrum of FIG. 5. In other words, the cubic GaN bulk crystal of the present embodiment contains little deep impurity levels or defects and has an excellent quality characterized by a defect density of 102-103 cm−3 or less.
In view of increasing defect density in the GaN crystals grown at low temperatures, and further in view of the fact that a mixture of cubic GaN and hexagonal GaN appears when the growth of the GaN bulk crystal is conducted at the temperature of 600° C. or lower under presence of Na flux, it is preferred to grow a cubic GaN bulk crystal at the temperature of 650-850° C. under presence of a K flux.
FIG. 20 shows the construction of a laser diode 150 of edge-emission type according to a twelfth embodiment of the present-invention.
Referring to FIG. 20, the laser diode 150 is constructed on a GaN bulk crystal substrate 151 produced in any of the process explained before. More specifically, the GaN bulk crystal substrate 151 has a high crystal quality characterized by a defect density of 102-103 cm−3 or less.
On the GaN bulk crystal substrate 151, there is provided a lower cladding layer 152 of n-type AlGaN epitaxially with respect to the substrate 151 and an optical waveguide layer 153 of n-type GaN is formed on the lower cladding layer 152 epitaxially.
On the optical waveguide layer 153, there is provided an active layer 154 of MQW structure including an alternate stacking of quantum well layers of undoped InGaN having a composition represented as InxGa1−xN (x=0.15) and barrier layers of undoped InGaN having a composition represented as InyGa1−yN (y=0.02). The active layer 154 is covered by an optical waveguide layer 155 of p-type GaN, and an upper cladding layer 156 of p-type AlGaN is formed epitaxially on the optical waveguide layer 155. Further, a contact layer 157 of p-type GaN is formed on the upper cladding layer 156.
The contact layer 157 and the underlying upper cladding layer 156 are subjected to a patterning process to form a loss-guide structure extending in the axial direction of the laser diode 150 and the loss-guide structure thus formed is covered by an SiO2 film 158. The SiO2 film 158 is formed with an opening 158A extending in the laser axial direction for exposing the contact layer 157, and a p-type electrode 159 is provided on the SiO2 film 158 in contact with the contact layer 157 at the opening 158A.
Further, an n-type electrode 160 is provided at a bottom surface of the GaN bulk crystal substrate 151.
After forming the laser structure as such, the layered semiconductor body including the GaN substrate 151 and the epitaxial layers 151-157 is subjected to a cleaving process to form mirror surfaces M1 and M2 defining an optical cavity. Thereby, the laser diode produces a blue to ultraviolet optical beam as a result of stimulated emission and optical amplification occurring in the optical cavity, as represented in FIG. 20 by an arrow.
According to the present invention, the optical cavity is formed by a simple cleaving process and the quality of the mirror surfaces Ml and M2 defining the optical cavity is improved substantially. Thereby, threshold of laser oscillation is lowered substantially. Further, the laser diode 150 carries the n-type electrode on the bottom surface of the GaN bulk crystal substrate 151 and the process of fabricating the laser diode is improved substantially. As the epitaxial layers, particularly the GaN optical waveguide layers 153 and 155 and the active layer 154 sandwiched between the layer 153 and 155 are formed epitaxially on the GaN bulk crystal substrate containing only a very small amount of defects, the quality of the crystal constituting the foregoing layers 153-155 is improved substantially over the conventional laser diode of FIG. 1 and the laser diode 150 of FIG. 20 can be driven with a large power. Further, the laser diode 150 of the present embodiment has an improved lifetime over the conventional laser diode of FIG. 1.
It should be noted that the GaN bulk crystal substrate 151 may be any of the hexagonal type or cubic type. In view of the easiness of cleaving process, on the other hand, it is preferable to form the GaN bulk crystal substrate 151 according to the process of the eleventh embodiment by using a K flux.
Based on the structure of FIG. 20, it is also possible to construct a light-emitting diode. Further, it is possible to construct a vertical cavity laser diode, which produces a laser beam in a direction vertical to the epitaxial layers, also by using the GaN bulk crystal substrate of the present invention.
In the case of a vertical cavity laser diode, a pair of mirror surfaces defining an optical cavity are formed by the epitaxial layers on the GaN bulk crystal substrate 151, and an optical window is formed in the electrode 159. In such a case, the GaN substrate 151 may have a thickness larger than 100 μm such as 300 μm or more.
In the laser diode of FIG. 20, it is also possible to form the mirror surfaces M1 and M2 by a dry etching process.
FIG. 21 shows the construction of an electron device 170 constructed on a GaN bulk crystal substrate 171 according to a thirteenth embodiment of the present invention.
Referring to FIG. 21, the electron device 170 is an FET, and the GaN bulk crystal 102B of any of the foregoing first through twelfth embodiments is used for the GaN substrate 171.
On the substrate 171, there is provided a high-resistance epitaxial layer 172 of AlN, and a buffer layer 173 of undoped GaN is formed epitaxially on the AlN high-resistance layer 172.
On the buffer layer 173, a lower barrier layer 174 of undoped AlGaN is formed epitaxially, and a channel layer 175 of undoped GaN is formed on the lower barrier layer 174 such that the channel layer 175 is sandwiched between the lower barrier layer 174 and an upper barrier layer 176 of undoped AlGaN formed epitaxially on the channel layer 175.
The upper barrier layer 176 is covered by a contact layer 177 of n-type GaN wherein the layers 174-177 are patterned to form a mesa region for device isolation. Further, the contact layer 177 is patterned to expose the upper barrier layer 176 in correspondence to the channel region, and a Schottky electrode 178 of a Ni/Au structure is provided in contact with the exposed upper barrier layer 176 as the gate electrode. Further, ohmic electrodes 179 and 180 of a Ti/Al structure are formed on the contact layer 177 at both lateral sides of the gate electrode 178 as a source electrode and a drain electrode, respectively.
In operation, a two-dimensional electron gas is induced in the channel layer 175 in response to application of a gate voltage to the gate electrode 178. In this state, the FET is turned on.
According to the present invention, it is thus possible to construct an active device such as an FET on a GaN substrate, by using the GaN bulk crystal for the substrate. As the GaN bulk crystal produced according to the present invention has an high crystal quality characterized by a defect density of 102-10 3cm−3 or less, the problem of severe leakage current that would occur when an FET is constructed on a conventional GaN epitaxial layer formed on a sapphire substrate or an SiC substrate, is successfully eliminated. Further, the construction of FIG. 21 is advantageous in view of the fact that the electron density of the two-dimensional electron gas induced in the channel layer 175 is increased due to enhanced piezoelectric effect and associated increase of degree of electron confinement into the channel layer. When the channel layer contains a high concentration of defects, there occurs a lattice relaxation and the effect of carrier confinement is degraded inevitably.
Further, the GaN bulk crystal of the present invention can be used also as the GaN substrate of other various electron devices including a HEMT, MESFET and an HBT. In fact, the structure of FIG. 21 can be modified to form a HEMT by employing an n-type AlGaN layer for the upper barrier layer 176.
1. A method of producing a single crystal body of a group III nitride, comprising:
forming a molten flux of a volatile metal element in a pressurized reaction vessel confining therein said molten flux together with an atmosphere containing N (nitrogen), such that said molten flux contains a group III element in addition to said volatile metal element;
growing a nitride of said group III element in the form of a single crystal body in said molten flux; and
supplying a compound containing N directly into the atmosphere in said reaction vessel from a source located outside said reaction vessel.
2. A method as claimed in claim 1, wherein said compound comprises N2 and NH3.
3. A method as claimed in claim 1, wherein said volatile metal is an alkali metal.
4. A method as claimed in claim 1, wherein said volatile metal element is Na.
5. A method as claimed in claim 1, wherein said volatile metal element is K.
6. A method as claimed in claim 1, wherein said molten flux further contains therein a source of said group III element at a location away from a melt surface of said molten flux, said step of growing said nitride single crystal body including the steps of decomposing said source so as to cause said source to release said group III element into said molten flux, and transporting said group III element from said source to said melt surface through said molten flux.
7. A method as claimed in claim 6 wherein said step of transporting said group III element includes a step of inducing a temperature gradient in said molten flux such that said molten flux has a temperature lower than a temperature of said melt surface in a part of said molten flux in which said solid source is located.
8. A method as claimed in claim 6, wherein said solid source is an intermetallic compound of said group III element and said volatile metal element.
9. A method as claimed in claim 6 wherein said solid source is a nitride of said group III element.
10. A method as claimed in claim 1, wherein said step of supplying said compound containing N into said reaction vessel is conducted such that said single crystal body grown in said molten flux maintains a predetermined stoichiometry.
11. A method as claimed in claim 1, further comprising the step of supplying said group III element into said molten flux from a source located outside said molten flux.
12. A method as claimed in claim 11, wherein said step of supplying said group III element into said molten flux is conducted by supplying a melt of said group III element into said molten flux.
13. A method as claimed in claim 11, wherein said step of supplying said group III element into said molten flux is conducted by supplying a melt of said group III element and said volatile metal element into said molten flux.
14. A method as claimed in claim 1, wherein said step of growing said single crystal body of nitride comprises the steps of contacting a seed crystal with said molten flux and pulling up said seed crystal from said molten flux in an upward direction with a progress of growth of said single crystal body on said seed crystal.
15. A method as claimed in claim 1, wherein said step of growing said single crystal body comprises the steps of contacting a seed crystal with said molten flux and pulling down said seed crystal into said molten flux in a downward direction with a progress of growth of said single crystal body on said seed crystal.
16. A method as claimed in claim 1, further comprising a step of supplying a vapor of said volatile metal element into said reaction vessel from an external source.
17. A method of producing a single crystal body of a cubic GaN, comprising:
an forming a molten flux of K in a pressurized reaction vessel confining therein said molten flux together with an atmosphere containing N (nitrogen), such that said molten flux contains Ga in addition to K; and
precipitating a single crystal body of cubic GaN in said molten flux.
18. A method as claimed in claim 17, further comprising the step of supplying a compound containing N (nitrogen) into said reaction vessel from an external source outside said reaction vessel.
19. A method as claimed in claim 17, wherein said precipitation is conducted by controlling a temperature of a melt surface of said molten flux at 650-850° C.
20. A method of fabricating a semiconductor device having a bulk crystal substrate of a nitride comprising:
growing a nitride bulk crystal of said group III element in said molten flux; and
21. A method as claimed in claim 20, wherein said compound comprises N2 and NH3.
22. A method as claimed in claim 20, wherein said volatile metal is an alkali metal.
23. A method as claimed in claim 20, wherein said volatile metal element is Na.
24. A method as claimed in claim 20, wherein said volatile metal element is K.
25. A method as claimed in claim 20, wherein said molten flux further contains therein a source of said group III element at a location away from a melt surface of said molten flux, said step of growing said nitride bulk crystal including the steps of decomposing said source so as to cause said source to release said group III element into said molten flux, and transporting said group III element from said source to said melt surface through said molten flux.
26. A method as claimed in claim 25 wherein said step of transporting said group III element includes a step of inducing a temperature gradient in said molten flux such that said molten flux has a temperature lower than a temperature of said melt surface in a part of said molten flux in which said source is located.
27. A method as claimed in claim 25, wherein said solid source is an intermetallic compound of said group III element and said volatile metal element.
28. A method as claimed in claim 25 wherein said solid source is a nitride of said group III element.
29. A method as claimed in claim 20, wherein said step of supplying said compound containing N into said reaction vessel is conducted such that said nitride bulk crystal of said group III element growing in said molten flux maintains a predetermined stoichiometry.
30. A method as claimed in claim 20, further comprising the step of supplying said group III element into said molten flux.
31. A method as claimed in claim 20, wherein said step of supplying said group III element into said molten flux is conducted by supplying a melt of said group III element into said molten flux from a source located outside said molten flux.
32. A method as claimed in claim 20, wherein said step of supplying said group III element into said molten flux is conducted by supplying a melt of said group III element and said volatile metal element into said molten flux from a source located outside said molten flux.
33. A method as claimed in claim 20, wherein said step of precipitating said bulk crystal comprises the steps of contacting a seed crystal with said molten flux and pulling up said seed crystal from said molten flux in an upward direction with a progress of growth of said bulk crystal on said seed crystal.
34. A method as claimed in claim 20, wherein said step of precipitating said bulk crystal comprises the steps of contacting a seed crystal with said molten flux and pulling down said seed crystal into said molten flux in a downward direction with a progress of growth of said bulk crystal on said seed crystal.
35. A method as claimed in claim 20, further comprising a step of supplying a vapor of said volatile metal element into said reaction vessel from a source located outside said reaction vessel.
36. A method of fabricating a semiconductor device having a bulk crystal substrate of cubic GaN, comprising:
forming a molten flux of K in a pressurized reaction vessel confining therein said molten flux together with an atmosphere containing N (nitrogen), such that said molten flux contains Ga in addition to K; and
growing a bulk crystal of GaN of a cubic crystal system at a melt surface of said molten flux.
37. A method as claimed in claim 36, further comprising the step of supplying a compound containing N (nitrogen) into said reaction vessel from a source located outside said reaction vessel.
38. A method as claimed in claim 36, wherein said precipitation is conducted by controlling a temperature of said melt surface at 650-850° C.
39. An apparatus for growing a group III nitride bulk crystal, comprising:
a pressurized reaction vessel having a space therein for holding a crucible;
a supply line connected to said reaction vessel, said supply line supplying a pressurized gas of a compound containing N (nitrogen) directly into an atmosphere in said reaction vessel; and
a heater disposed outside said reaction vessel, said heater heating said reaction vessel externally so as to form a molten flux of a volatile metal element and a group III element in said crucible.
40. An apparatus as claimed in claim 39, further comprising a pressure-resistant vessel enclosing said reaction vessel.
41. An apparatus as claimed in claim 39, further including a mechanism for supplying a melt of said group III element into said molten flux in said crucible.
42. An apparatus as claimed in claim 6, wherein said mechanism including a container disposed in said space of said reaction vessel at a location above a surface of said molten flux, said container having an opening for allowing said melt of said group III element to fall into said molten flux.
43. An apparatus as claimed in claim 41, wherein said mechanism further supplies a melt of said volatile metal element together with said melt of said group III element.
44. An apparatus as claimed in claim 39, further comprising a mechanism for supplying a vapor of said volatile metal element into said reaction vessel.
45. An apparatus as claimed in claim 39, further comprising a rod adapted for carrying a seed crystal at a tip end and a motor for moving said rod in an upward direction, said rod and said motor being located above a melt surface of said molten flux formed in said crucible.
46. An apparatus as claimed in claim 45, wherein said motor is located outside said reaction vessel.
47. An apparatus as claimed in claim 45, further comprising a cover member covering a surface of said molten formed in said crucible, said cover member having a central opening for allowing said seed crystal to make a contact with said molten flux.
48. An apparatus as claimed In claim 47 wherein said cover member has a variable geometry for changing a size of said central opening.
49. An apparatus as claimed in claim 39, further comprising a rod adapted for carrying a seed crystal at a tip end, said rod being inserted into said crucible through a bottom part of said crucible, and a motor provided outside of said reaction vessel for moving said rod in a downward direction.
50. An apparatus as claimed in claim 39, wherein said heater induces a temperature gradient in said molten flux in said crucible such that a temperature of said molten flux at a bottom part of said crucible is higher than a temperature at a top surface of said molten flux.
51. An apparatus as claimed in claim 50, wherein said heater includes a first heater part heating a sidewall of said reaction vessel and a second heater part heating a bottom part of said reaction vessel.
US09590063 1999-06-09 2000-06-08 Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate Active 2020-10-21 US6592663B1 (en)
JP16241199 1999-06-09
JP11-162411 1999-06-09
JP23719599A JP4094780B2 (en) 1999-08-24 1999-08-24 Production process and crystal production apparatus of the crystal growth method and the crystal growth apparatus, and iii nitride crystal
JP11-237195 1999-08-24
JP11-277045 1999-09-29
JP27704599A JP3929657B2 (en) 1999-09-29 1999-09-29 Method for producing a crystal growth method and iii nitride crystal
JP29503999A JP4056664B2 (en) 1999-10-18 1999-10-18 Method for producing Iii Nitride Crystal
JP11-295039 1999-10-18
US10601301 US7250640B2 (en) 1999-06-09 2003-06-13 Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate
US11408656 US7508003B2 (en) 1999-06-09 2006-04-20 Production of a GaN bulk crystal substrate and a semiconductor device formed thereon
US12367013 US8591647B2 (en) 1999-06-09 2009-02-06 Production of a GaN bulk crystal substrate and a semiconductor device formed thereon
US14057690 US20140044970A1 (en) 1999-06-09 2013-10-18 PRODUCTION OF A GaN BULK CRYSTAL SUBSTRATE AND A SEMICONDUCTOR DEVICE FORMED ON A GaN BULK CRYSTAL SUBSTRATE
US14619237 US9869033B2 (en) 1999-06-09 2015-02-11 Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate
US10601301 Division US7250640B2 (en) 1999-06-09 2003-06-13 Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate
US6592663B1 true US6592663B1 (en) 2003-07-15
ID=27473798
US09590063 Active 2020-10-21 US6592663B1 (en) 1999-06-09 2000-06-08 Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate
US10601301 Active 2020-08-20 US7250640B2 (en) 1999-06-09 2003-06-13 Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate
US11408656 Active 2021-01-28 US7508003B2 (en) 1999-06-09 2006-04-20 Production of a GaN bulk crystal substrate and a semiconductor device formed thereon
US12367013 Active 2022-05-09 US8591647B2 (en) 1999-06-09 2009-02-06 Production of a GaN bulk crystal substrate and a semiconductor device formed thereon
US14057690 Abandoned US20140044970A1 (en) 1999-06-09 2013-10-18 PRODUCTION OF A GaN BULK CRYSTAL SUBSTRATE AND A SEMICONDUCTOR DEVICE FORMED ON A GaN BULK CRYSTAL SUBSTRATE
US14619237 Active 2021-02-11 US9869033B2 (en) 1999-06-09 2015-02-11 Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate
US (6) US6592663B1 (en)
US20030209185A1 (en) * 2002-05-13 2003-11-13 Sumitomo Electric Industries, Ltd. GaN single-crystal substrate, nitride type semiconductor epitaxial substrate, nitride type semiconductor device, and methods of making the same
US20040031437A1 (en) * 1999-06-09 2004-02-19 Seiji Sarayama Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate
US20040134413A1 (en) * 2002-11-08 2004-07-15 Hirokazu Iwata Group III nitride crystal, crystal growth process and crystal growth apparatus of group III nitride
US20040147096A1 (en) * 2003-01-20 2004-07-29 Matsushita Electric Industrial Co., Ltd. Method of manufacturing Group III nitride substrate
US20040183090A1 (en) * 2003-03-20 2004-09-23 Matsushita Electric Industrial Co., Ltd. Method of manufacturing group III nitride substrate and semiconductor device
US20040226503A1 (en) * 2003-01-29 2004-11-18 Hirokazu Iwata Method of growing group III nitride crystal, group III nitride crystal grown thereby, group III nitride crystal growing apparatus and semiconductor device
US20040262630A1 (en) * 2003-05-29 2004-12-30 Matsushita Electric Industrial Co., Ltd. Group III nitride crystals usable as group III nitride substrate, method of manufacturing the same, and semiconductor device including the same
US20050011432A1 (en) * 2003-07-02 2005-01-20 Matsushita Electric Industrial Co., Ltd. Method of manufacturing Group III nitride crystals, method of manufacturing semiconductor substrate, Group III nitride crystals, semiconductor substrate, and electronic device
US20050066878A1 (en) * 2003-09-25 2005-03-31 Arent Douglas Jay Methods for producing group III nitride materials
US20050082564A1 (en) * 2003-10-20 2005-04-21 Matsushita Electric Industrial Co., Ltd. Group-III-element nitride crystal semiconductor device
EP1553216A2 (en) * 2004-01-08 2005-07-13 Yusuke Mori Method of manufacturing group-III nitride crystal
EP1775356A2 (en) 2005-10-14 2007-04-18 Ricoh Company, Ltd. Crystal growth apparatus and manufacturing method of group III nitride crystal
US20070128746A1 (en) * 2005-11-21 2007-06-07 Hirokazu Iwata Group iii nitride crystal and manufacturing method thereof
US20070157876A1 (en) * 2004-04-27 2007-07-12 Yusuke Mori Apparatus for production of crystal of group III element nitride and process for producing crystal of group III element nitride
US20070175383A1 (en) * 2004-01-21 2007-08-02 Japan Science And Technology Agency Process for producing single crystal of gallium-containing nitride
US20070196942A1 (en) * 2003-12-26 2007-08-23 Yusuke Mori Method for producing group III nitride crystal, group III nitride crystal obtained by such method, and group III nitride substrate using the same
US20070215034A1 (en) * 2006-03-14 2007-09-20 Hirokazu Iwata Crystal preparing device, crystal preparing method, and crystal
US20070272941A1 (en) * 2004-03-31 2007-11-29 Yusuke Mori Method For Producing III Group Element Nitride Crystal, Production Apparatus For Use Therein, And Semiconductor Element Produced Thereby
EP1863075A1 (en) * 2005-03-23 2007-12-05 SUMITOMO ELECTRIC INDUSTRIES Ltd Group iii nitride semiconductor device and epitaxial substrate
US20070296061A1 (en) * 2004-04-12 2007-12-27 Takatomo Sasaki Group III-Nitride Crystal Substrate and Manufacturing Method Thereof, and Group III-Nitride Semiconductor Device
US20080037100A1 (en) * 2004-06-30 2008-02-14 Matsushita Electric Industrial Co., Ltd. Acoustooptic Device and Optical Imaging Apparatus Using the Same
US20080081015A1 (en) * 2006-10-02 2008-04-03 Seiji Sarayama Crystal producing apparatus, crystal producing method, substrate producing method, gallium nitride crystal, and gallium nitride substrate
US20080282971A1 (en) * 2006-03-23 2008-11-20 Ngk Insulators, Ltd. Nitride single crystal manufacturing apparatus
US20080283968A1 (en) * 2004-05-19 2008-11-20 Takatomo Sasaki Group III-Nitride Semiconductor Crystal and Manufacturing Method Thereof, and Group III-Nitride Semiconductor Device
US20090199763A1 (en) * 2004-10-16 2009-08-13 Armin Dadgar Process for the production of gan or aigan crystals
US20090249997A1 (en) * 2005-05-12 2009-10-08 Seiji Sarayama Method of producing group iii nitride crystal, apparatus for producing group iii nitride crystal, and group iii nitride crystal
CN100554148C (en) 2004-02-10 2009-10-28 山东大学 Method of synthesizing nitride crystal material at low temperature and low pressure
US20100051609A1 (en) * 2008-08-31 2010-03-04 Fishman Oleg S Directional Solidification of Silicon by Electric Induction Susceptor Heating in a Controlled Environment
WO2011151757A1 (en) * 2010-05-31 2011-12-08 International Business Machines Corporation Producing a mono-crystalline sheet
US9096950B2 (en) 2010-07-01 2015-08-04 Ricoh Company, Ltd. Nitride crystal and method for producing the same
US8431253B2 (en) * 2004-07-08 2013-04-30 Los Alamos National Security, Llc Cubic nitride templates
JP4603498B2 (en) 2005-03-14 2010-12-22 株式会社リコー Method and apparatus for manufacturing a Iii Nitride Crystal
JP5147092B2 (en) * 2009-03-30 2013-02-20 豊田合成株式会社 The method of manufacturing Iii Nitride semiconductor
WO2015031794A3 (en) * 2013-08-30 2015-05-28 The Regents Of The University Of California Reactor vessels for ammonothermal and flux-based growth of group-iii nitride crystals
US1890822A (en) * 1930-06-20 1932-12-13 Niagara Falls Smelting & Refin Contact device
US2634122A (en) * 1948-01-03 1953-04-07 Merl R Wolfard Flexible strut
GB780871A (en) * 1955-01-18 1957-08-07 Sigma Instr Co Ltd Improvements in or relating to mechanical guiding devices
US3507486A (en) * 1967-11-13 1970-04-21 Bernard L Schwaller Dual stage compressor spring
JPS5651160B2 (en) 1974-05-20 1981-12-03
JPS5636402Y2 (en) 1974-05-24 1981-08-27
JPS56160400U (en) 1980-04-28 1981-11-30
JPS56160400A (en) 1980-05-06 1981-12-10 Matsushita Electric Ind Co Ltd Growing method for gallium nitride
FR2632613B1 (en) * 1988-06-08 1993-10-08 Ilic Zoran Product range with its uses, aiming to offset the problems due to the volume of gap between a transport compartment of objects of a vehicle and its contents
JP2600015B2 (en) 1990-09-04 1997-04-16 富士通株式会社 Crystal growth method
JP2526577Y2 (en) 1991-03-26 1997-02-19 ワイケイケイアーキテクチュラルプロダクツ株式会社 Structure of diagonal grid
JP2585962B2 (en) 1993-11-25 1997-02-26 東京エレクトロン株式会社 High-pressure oxidation furnace
JP3656266B2 (en) 1994-03-11 2005-06-08 住友電気工業株式会社 Compound semiconductor crystal manufacturing method and the crucible for
US5584929A (en) 1994-03-11 1996-12-17 Sumitomo Electric Industries, Ltd. Method for preparing compound semiconductor crystal
JPH07273048A (en) 1994-03-31 1995-10-20 Mitsubishi Cable Ind Ltd Manufacture method of compound semiconductor single crystal and single crystal substrate using such method
JPH08172056A (en) * 1994-12-20 1996-07-02 Mitsubishi Electric Corp Growing method of compound semiconductor layer
JP3540073B2 (en) 1995-02-20 2004-07-07 富士通株式会社 Crystal growth method
US5792566A (en) * 1996-07-02 1998-08-11 American Xtal Technology Single crystal wafers
JPH1067592A (en) 1996-08-23 1998-03-10 Fujitsu Ltd Horizontal bridgeman crystal growth furnace and production of semiconductor
JP3533938B2 (en) 1997-06-11 2004-06-07 日立電線株式会社 Method for producing a nitride crystal, a mixture, a liquid phase growth method, the nitride crystal, a nitride crystal powder, and vapor phase growth method
JP3622440B2 (en) 1997-08-18 2005-02-23 日立電線株式会社 Growing method of growing method and GaN crystal of the nitride crystal
JPH1187850A (en) 1997-09-03 1999-03-30 Sharp Corp Nitride compound semiconductor laser element and laser device
JPH11171699A (en) 1997-12-16 1999-06-29 Furukawa Electric Co Ltd:The Growth of gallium nitride phosphide single crystal
"Bulk and Homoepitaxial GaN-growth and Characterization", S. Porowski, Journal of Crystal Growth, 1998, vol. 189/190, pp. 153-158.
"InGaN/GaN/AlGaN-Based Laser Diodes With Cleaved Facets Grown on GaN Substrates", S. Nakamura et al., Applied Physics Letters, 1998, vol. 73, No. 6, pp. 832-834.
"InGaN/GaN/AlGaN-Based Laser Diodes With Modulation-Doped Strained-Layer Superlattices", S. Nakamura et al., Japanese Journal of Applied Physics, 1997, vol. 36, No. 12A, pp. 1568-1571.
"Preparation of GaN Single Crystals Using a Na Flux", H. Yamane et al., Chemical Mater, 1997, vol. 9, No. 2, pp. 413-416.
US7508003B2 (en) 1999-06-09 2009-03-24 Ricoh Company, Ltd. Production of a GaN bulk crystal substrate and a semiconductor device formed thereon
US9869033B2 (en) 1999-06-09 2018-01-16 Ricoh Company, Ltd. Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate
US20070012239A1 (en) * 1999-06-09 2007-01-18 Seiji Sarayama Production of a GaN bulk crystal substrate and a semiconductor device formed thereon
US20090173274A1 (en) * 1999-06-09 2009-07-09 Ricoh Company, Ltd. PRODUCTION OF A GaN BULK CRYSTAL SUBSTRATE AND A SEMICONDUCTOR DEVICE FORMED THEREON
US8591647B2 (en) 1999-06-09 2013-11-26 Ricoh Company, Ltd. Production of a GaN bulk crystal substrate and a semiconductor device formed thereon
US7250640B2 (en) 1999-06-09 2007-07-31 Ricoh Company, Ltd. Production of a GaN bulk crystal substrate and a semiconductor device formed on a GaN bulk crystal substrate
US7001457B2 (en) * 2001-05-01 2006-02-21 Ricoh Company, Ltd. Crystal growth method, crystal growth apparatus, group-III nitride crystal and group-III nitride semiconductor device
US20100173483A1 (en) * 2002-05-13 2010-07-08 Sumitomo Electric Industries, Ltd. GaN SINGLE-CRYSTAL SUBSTRATE, NITRIDE TYPE SEMICONDUCTOR EPITAXIAL SUBSTRATE, NITRIDE TYPE SEMICONDUCTOR DEVICE, AND METHODS OF MAKING THE SAME
US7220311B2 (en) * 2002-11-08 2007-05-22 Ricoh Company, Ltd. Group III nitride crystal, crystal growth process and crystal growth apparatus of group III nitride
US20070194408A1 (en) * 2002-11-08 2007-08-23 Hirokazu Iwata Group III nitride crystal, crystal growth process and crystal growth apparatus of group III nitride
US7981213B2 (en) 2002-11-08 2011-07-19 Ricoh Company, Ltd. Group III nitride crystal, crystal growth process and crystal growth apparatus of group III nitride
US20070187700A1 (en) * 2003-01-20 2007-08-16 Matsushita Electric Industrial Co., Ltd. Method of manufacturing group III nitride substrate and semiconductor device
US7221037B2 (en) 2003-01-20 2007-05-22 Matsushita Electric Industrial Co., Ltd. Method of manufacturing group III nitride substrate and semiconductor device
US7524691B2 (en) 2003-01-20 2009-04-28 Panasonic Corporation Method of manufacturing group III nitride substrate
US7261775B2 (en) 2003-01-29 2007-08-28 Ricoh Company, Ltd. Methods of growing a group III nitride crystal
US20110012235A1 (en) * 2003-01-29 2011-01-20 Hirokazu Iwata Method of growing group iii nitride crystal, group iii nitride crystal grown thereby, group iii nitride crystal growing apparatus and semiconductor device
US7828896B2 (en) 2003-01-29 2010-11-09 Ricoh Company, Ltd. Methods of growing a group III nitride crystal
US20070266928A1 (en) * 2003-01-29 2007-11-22 Hirokazu Iwata Method of growing group III nitride crystal, group III nitride crystal grown thereby, group III nitride crystal growing apparatus and semiconductor device
US7309534B2 (en) 2003-05-29 2007-12-18 Matsushita Electric Industrial Co., Ltd. Group III nitride crystals usable as group III nitride substrate, method of manufacturing the same, and semiconductor device including the same
US7255742B2 (en) 2003-07-02 2007-08-14 Matsushita Electric Industrial Co., Ltd. Method of manufacturing Group III nitride crystals, method of manufacturing semiconductor substrate, Group III nitride crystals, semiconductor substrate, and electronic device
US7227172B2 (en) 2003-10-20 2007-06-05 Matsushita Electric Industrial Co., Ltd. Group-III-element nitride crystal semiconductor device
EP1553216A3 (en) * 2004-01-08 2010-09-29 Sumitomo Electric Industries, Ltd. Method of manufacturing group-III nitride crystal
US7794539B2 (en) 2004-03-31 2010-09-14 Panasonic Corporation Method for producing III group element nitride crystal, production apparatus for use therein, and semiconductor element produced thereby
US7381268B2 (en) 2004-04-27 2008-06-03 Matsushita Electric Industrial Co., Ltd. Apparatus for production of crystal of group III element nitride and process for producing crystal of group III element nitride
US7754012B2 (en) 2004-04-27 2010-07-13 Panasonic Corporation Apparatus for production of crystal of group III element nitride and process for producing crystal of group III element nitride
US20080213158A1 (en) * 2004-04-27 2008-09-04 Yusuke Mori Apparatus for production of crystal of group III element nitride and process for producing crystal of group III element nitride
US7905958B2 (en) * 2004-05-19 2011-03-15 Sumitomo Electric Industries, Ltd. Group III-nitride semiconductor crystal and manufacturing method thereof, and group III-nitride semiconductor device
US7855823B2 (en) 2004-06-30 2010-12-21 Panasonic Corporation Acoustooptic device and optical imaging apparatus using the same
US8410524B2 (en) 2005-03-23 2013-04-02 Sumitomo Electric Industries, Ltd. Group III nitride semiconductor device and epitaxial substrate
EP1863075A4 (en) * 2005-03-23 2009-04-29 Sumitomo Electric Industries Group iii nitride semiconductor device and epitaxial substrate
US20090189186A1 (en) * 2005-03-23 2009-07-30 Sumitomo Electric Industries, Ltd. Group III Nitride Semiconductor Device and Epitaxial Substrate
US8888912B2 (en) 2005-05-12 2014-11-18 Ricoh Company, Ltd. Method of producing group III nitride crystal, apparatus for producing group III nitride crystal, and group III nitride crystal
US9163325B2 (en) 2005-10-14 2015-10-20 Ricoh Company, Ltd. Crystal growth apparatus and manufacturing method of group III nitride crystal
US9856575B2 (en) 2005-10-14 2018-01-02 Ricoh Company, Ltd. Crystal growth apparatus and manufacturing method of group III nitride crystal
US8101020B2 (en) * 2005-10-14 2012-01-24 Ricoh Company, Ltd. Crystal growth apparatus and manufacturing method of group III nitride crystal
US20070084399A1 (en) * 2005-10-14 2007-04-19 Seiji Sarayama Crystal growth apparatus and manufacturing method of group III nitride crystal
US8323404B2 (en) * 2005-11-21 2012-12-04 Ricoh Company, Ltd. Group III nitride crystal and manufacturing method thereof
US9365948B2 (en) 2005-11-21 2016-06-14 Ricoh Company, Ltd Group III nitride crystal and manufacturing method thereof
US7670430B2 (en) 2006-02-13 2010-03-02 Ngk Insulators, Ltd. Method of recovering sodium metal from flux
US20110253034A1 (en) * 2006-03-14 2011-10-20 Hirokazu Iwata Crystal preparing device, crystal preparing method, and crystal
US8475593B2 (en) * 2006-03-14 2013-07-02 Ricoh Company, Ltd. Crystal preparing device, crystal preparing method, and crystal
US9017479B2 (en) * 2006-03-23 2015-04-28 Ngk Insulators, Ltd. Nitride single crystal manufacturing apparatus
US8999059B2 (en) 2006-03-24 2015-04-07 Ngk Insulators, Ltd. Process for producing a nitride single crystal and apparatus therefor
US8337798B2 (en) * 2006-10-02 2012-12-25 Ricoh Company, Ltd. Crystal producing apparatus, crystal producing method, substrate producing method, gallium nitride crystal, and gallium nitride substrate
EP1916321B1 (en) * 2006-10-02 2017-05-10 Ricoh Company, Ltd. Crystal producing method
US8829530B2 (en) 2006-10-02 2014-09-09 Ricoh Company, Ltd. Crystal producing apparatus, crystal producing method, substrate producing method, gallium nitride crystal, and gallium nitride substrate
US8242420B2 (en) * 2008-08-31 2012-08-14 Inductotherm Corp. Directional solidification of silicon by electric induction susceptor heating in a controlled environment
GB2494565A (en) * 2010-05-31 2013-03-13 Ibm Producing a mono-crystalline sheet
CN102906315A (en) * 2010-05-31 2013-01-30 国际商业机器公司 Producing a mono-crystalline sheet
US9487884B2 (en) 2010-05-31 2016-11-08 International Business Machines Corporation Producing a mono-crystalline sheet of semiconductor material
CN102906315B (en) * 2010-05-31 2015-06-24 国际商业机器公司 Producing a mono-crystalline sheet
GB2494565B (en) * 2010-05-31 2014-04-09 Ibm Producing a mono-crystalline sheet
US20090173274A1 (en) 2009-07-09 application
US7508003B2 (en) 2009-03-24 grant
US20070012239A1 (en) 2007-01-18 application
US20140044970A1 (en) 2014-02-13 application
US9869033B2 (en) 2018-01-16 grant
US20040031437A1 (en) 2004-02-19 application
US8591647B2 (en) 2013-11-26 grant
US7250640B2 (en) 2007-07-31 grant
US20150152568A1 (en) 2015-06-04 application
Kobayashi et al. 1985 Flow-rate modulation epitaxy of GaAs
US7501023B2 (en) 2009-03-10 Method and apparatus for fabricating crack-free Group III nitride semiconductor materials
US20040183090A1 (en) 2004-09-23 Method of manufacturing group III nitride substrate and semiconductor device
Miyamura et al. 2002 High-density and size-controlled GaN self-assembled quantum dots grown by metalorganic chemical vapor deposition
US5909040A (en) 1999-06-01 Semiconductor device including quaternary buffer layer with pinholes
Itaya et al. 1996 Room temperature pulsed operation of nitride based multi-quantum-well laser diodes with cleaved facets on conventional C-face sapphire substrates
Ramvall et al. 2000 Optical properties of GaN quantum dots
Nakamura et al. 1998 High-power, long-lifetime InGaN/GaN/AlGaN-based laser diodes grown on pure GaN substrates
US20050166835A1 (en) 2005-08-04 Vapor phase growth method for al-containing III-V group compound semiconductor, and method and device for producing al-containing IIl-V group compound semiconductor
Nakamura et al. 1991 High-power GaN pn junction blue-light-emitting diodes
US6303473B1 (en) 2001-10-16 Method of growing group III or group III-V nitride layer
US20060043396A1 (en) 2006-03-02 Sapphire substrate, epitaxial substrate and semiconductor device
US20060005763A1 (en) 2006-01-12 Method and apparatus for producing large, single-crystals of aluminum nitride
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SARAYAMA, SEIJI;SHIMADA, MASAHIKO;YAMANE, HISANORI;AND OTHERS;REEL/FRAME:011265/0273
Owner name: SHIMADA, MASAHIKO, JAPAN
Owner name: YAMANE, HISANORI, JAPAN
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SHIMADA, MASAHIKO;YAMANE, HSANORI;REEL/FRAME:014354/0325