Matched Legal Cases: ['art；402', 'art 401', 'art 401', 'art 403', 'art 503', 'art 401', 'art 403', 'art 403', 'art 401', 'art 403', 'art 401', 'art 401', 'art 401', 'art 403', 'art 403', 'art 401', 'art 401', 'art 401', 'art 401', 'art 403', 'art 403', 'art 402', 'art 401', 'art 401', 'art 401', 'art 403', 'art 403', 'art 401', 'art 401', 'art 401', 'art 403', 'art 403', 'art 401']

CN103715094B - Thin film thyristor and manufacturing method thereof, array substrate and manufacturing method thereof and display device - Google Patents
Thin film thyristor and manufacturing method thereof, array substrate and manufacturing method thereof and display device Download PDF
CN103715094B
CN103715094B CN201310740724.5A CN201310740724A CN103715094B CN 103715094 B CN103715094 B CN 103715094B CN 201310740724 A CN201310740724 A CN 201310740724A CN 103715094 B CN103715094 B CN 103715094B
CN201310740724.5A
CN103715094A (en
2013-12-27 Application filed by 京东方科技集团股份有限公司 filed Critical 京东方科技集团股份有限公司
2013-12-27 Priority to CN201310740724.5A priority Critical patent/CN103715094B/en
2014-04-09 Publication of CN103715094A publication Critical patent/CN103715094A/en
2017-02-01 Publication of CN103715094B publication Critical patent/CN103715094B/en
The embodiment of the invention provides a thin film thyristor, a manufacturing method of the thin film thyristor, an array substrate, a manufacturing method of the array substrate and a display device and relates to the technical field of display, in particular to thin film thyristor, array substrate and display device manufacturing. The number of times of picture composition processes can be reduced, and therefore productivity of mass products is improved, and cost is reduced. The manufacturing method of the thin film thyristor includes the step that an active layer, a source electrode and a drain electrode are formed on a substrate according to the picture composition process, wherein the active layer, the source electrode and the drain electrode are located on the same layer.
Thin film transistor (TFT) and preparation method, array base palte and preparation method, display device
The present invention relates to display technology field, more particularly, to a kind of thin film transistor (TFT) and preparation method, array base palte and system Preparation Method, display device.
Thin Film Transistor-LCD (thin film transistor liquid crystal display, referred to as Tft-lcd) have small volume, low in energy consumption, radiationless the features such as, in technical field of flat panel display in occupation of leading position, be subject to The extensive concern of people.
Additionally, in the prior art, the preparation of thin film transistor (TFT) typically require carry out barrier metal layer mask, gate insulation layer is covered The repeatedly patterning processes such as film, active layer mask, Source and drain metal level mask and pixel electrode layer mask, and composition work each time Include the techniques such as film forming, exposure, development, etching and stripping respectively in skill again.
However, the number of times of patterning processes excessively will result directly in the cost increase of product and the production capacity fall of volume production product Low, the number of times therefore how reducing patterning processes further also just becomes the problem of people's growing interest.
Embodiments of the invention provide a kind of thin film transistor (TFT) and preparation method, array base palte and preparation method, display dress Put, the number of times of patterning processes can be reduced, thus improving the production capacity of volume production product, reduces cost.
On the one hand, provide a kind of preparation method of thin film transistor (TFT), methods described is included by patterning processes in base Form active layer, source electrode and drain electrode on plate, and described active layer, described source electrode and described drain electrode are located at same layer.
Optionally, described pass through patterning processes and form active layer, source electrode and drain electrode on substrate, specifically include: Form layer of semiconductor thin film on substrate, and photoresist is formed on described semiconductive thin film；Using masstone mask plate to shape After becoming the substrate having described photoresist to be exposed, develop, formed photoresist be fully retained part, photoresist half member-retaining portion and Photoresist removes part completely；Wherein, described photoresist is fully retained the region partly corresponding to semiconductor active layer to be formed, Described photoresist half member-retaining portion correspondence described source electrode to be formed and the region of described drain electrode, described photoresist removal portion completely Divide other regions corresponding；Described photoresist is removed using etching technics and removes partly corresponding described semiconductive thin film completely；Adopt Remove the photoresist of described photoresist half member-retaining portion with cineration technics；Metalized is carried out to described semiconductive thin film, makes The described semiconductive thin film exposing is converted into the thin film with conductor characteristics, forms described source electrode and described drain electrode；Corresponding described The described semiconductive thin film that photoresist is fully retained part is affected by metalized, forms described semiconductor active layer；Adopt Remove the photoresist that described photoresist is fully retained part with stripping technology.
Method that is further alternative, carrying out metalized to described semiconductive thin film, specifically includes: will have and expose The substrate of described semiconductive thin film be placed in reducing atmosphere and carry out heat treatment at 200～400 DEG C；Or, exposing having The substrate of described semiconductive thin film is placed in vacuum chamber, is processed using hydrogen gas plasma or oxygen gas plasma, wherein, institute Stating the pressure in vacuum chamber is 1000～2000mtorr, and gas flow is 5000～15000sccm.
Further, the described semiconductive thin film carrying out metalized is metal-oxide film, described metal oxidation Thing thin film is using the transparent metal oxide material in characteristic of semiconductor.
Further, the described transparent metal oxide material in characteristic of semiconductor includes indium gallium zinc oxide (indium Gallium zinc oxide, abbreviation igzo), indium gallium oxide (indium gallium oxide, abbreviation igo), amorphous state Indium stannum zinc oxide (indium tin zinc oxide, abbreviation itzo), aluminum zinc oxide (aluminium zinc oxide, Abbreviation azo) at least one.
Preferably, on the substrate being formed with described active layer, described source electrode and described drain electrode, by patterning processes Form gate insulation layer and the grid being located above described active layer, described source electrode and described drain electrode.
Also provide a kind of preparation method of array base palte, including the preparation of thin film transistor (TFT) and pixel electrode；Described thin film The preparation method of transistor is the preparation method of above-mentioned thin film transistor (TFT).
Optionally, by patterning processes, the same of active layer, source electrode and the drain electrode being located at same layer is formed on substrate When, also formed and electrically connect and the pixel electrode with layer with described drain electrode；Wherein, described drain electrode is integrated knot with described pixel electrode Structure and there is identical material.
Further alternative, formed on substrate by patterning processes and be located at the described active layer of same layer, described Source electrode and described drain electrode and the pixel electrode being electrically connected with described drain electrode, are specifically included: form layer of semiconductor on substrate Thin film, and photoresist is formed on described semiconductive thin film；Using masstone mask plate to the substrate being formed with described photoresist After being exposed, developing, form photoresist and part, photoresist half member-retaining portion and photoresist completely removal part are fully retained； Wherein, described photoresist is fully retained the region partly corresponding to semiconductor active layer to be formed, described photoresist half reserve part Divide correspondence described source electrode to be formed and drain electrode and the region of the described pixel electrode electrically connecting with described drain electrode, described light Photoresist removes partly correspond to other regions completely；Removed partly corresponding described completely using the etching technics described photoresist of removal Semiconductive thin film；Remove the photoresist of described photoresist half member-retaining portion using cineration technics；Described semiconductive thin film is carried out Metalized, makes the described semiconductive thin film exposing be converted into the thin film with conductor characteristics, forms described source electrode and described Drain electrode and the pixel electrode electrically connecting with described drain electrode；Corresponding described photoresist is fully retained the described semiconductor film of part Film is affected by metalized, forms described semiconductor active layer；Remove described photoresist using stripping technology to be fully retained Partial photoresist.
Optionally, methods described also includes: forms public electrode on substrate by patterning processes.
On the other hand, a kind of thin film transistor (TFT) is provided, including active layer and be located at described active layer both sides source electrode and Drain electrode；Described active layer, described source electrode and described drain electrode are arranged with layer.
Optionally, the material of described active layer is the transparent metal oxide material in characteristic of semiconductor；Described source electrode and The material of described drain electrode is the material obtaining after metalized with described active layer identical material.
Further alternative, the described transparent metal oxide material in characteristic of semiconductor includes indium gallium zinc oxide (igzo), indium gallium oxide (igo), amorphous state indium stannum zinc oxide (itzo), at least one in aluminum zinc oxide (azo).
Optionally, described source electrode and described drain electrode and described active layer are additionally provided with gate insulation layer and grid.
Also provide a kind of array base palte, described array base palte includes pixel electrode and above-mentioned thin film transistor (TFT).
Optionally, the drain electrode of described thin film transistor (TFT) is electrically connected with described pixel electrode；Described thin film transistor (TFT) active Layer, source electrode and drain electrode and described pixel electrode are arranged with layer；Wherein, described drain electrode is structure as a whole with described pixel electrode And there is identical material.
Optionally, described array base palte also includes public electrode.
Also provide a kind of display device, including above-mentioned array base palte.
Embodiments provide a kind of thin film transistor (TFT) and preparation method, array base palte and preparation method, display dress Put, the preparation method of this thin film transistor (TFT) includes forming active layer, source electrode and drain electrode by patterning processes on substrate, and Described active layer, described source electrode and described drain electrode are located at same layer.Compared with prior art, this preparation method can subtract effectively The number of times of few patterning processes, thus the production capacity of volume production product, reduces cost can be lifted.
Fig. 1 is a kind of structural representation of top gate type thin film transistor provided in an embodiment of the present invention；
Fig. 2 is a kind of structural representation of bottom gate thin film transistor provided in an embodiment of the present invention；
Fig. 3 (a)～Fig. 3 (f) is a kind of formation metal-oxide semiconductor (MOS) active layer provided in an embodiment of the present invention, source electrode Process schematic with drain electrode；
Fig. 4 is a kind of structural representation one of array base palte provided in an embodiment of the present invention；
Fig. 5 is a kind of structural representation two of array base palte provided in an embodiment of the present invention；
Fig. 6 (a)～Fig. 6 (h) is a kind of process schematic forming array base palte provided in an embodiment of the present invention；
Fig. 7 is a kind of structural representation three of array base palte provided in an embodiment of the present invention；
Fig. 8 is a kind of preparation flow figure of array base palte provided in an embodiment of the present invention.
10- array base palte；11- (metal-oxide) semiconductive thin film；12- gate insulation layer film；13- metallic film；20- Thin film transistor (TFT)；201- grid；202- gate insulation layer；203- (metal-oxide semiconductor (MOS)) active layer；204- source electrode；205- leaks Pole；30- pixel electrode；40- photoresist；401- photoresist is fully retained part；402- photoresist half member-retaining portion；403- photoetching Glue removes part completely；50- masstone mask plate；501- opaque section；502- translucent portion；The transparent part of 503-；60- Public electrode；70- passivation layer.
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete Site preparation description is it is clear that described embodiment is only a part of embodiment of the present invention, rather than whole embodiments.
The embodiment of the present invention provides a kind of preparation method of thin film transistor (TFT) 20, and methods described is included by a composition work Skill forms active layer 203, source electrode 204 and drain electrode 205 on substrate, and described active layer 203, described source electrode 204 and described leakage Pole 205 is located at same layer.
It should be noted that first, in embodiments of the present invention, described patterning processes correspond to a mask work For skill, i.e. mask plate of application some patterns that complete referred to as have carried out patterning processes.
Second, described active layer 203, described source electrode 204 and drain electrode 205 are formed by patterning processes, and it can be Carry out before forming grid 201 and gate insulation layer 202 it is also possible to be formed after forming grid 201 and gate insulation layer 202, tool Body order here does not limit, and is defined by practical condition.
Wherein, when described grid 201 and described gate insulation layer 202 are previously formed, described active layer 203, described source electrode 204 With described drain electrode 205 in rear formation, described thin film transistor (TFT) 20 is bottom gate thin film transistor 20；When described active layer 203rd, described source electrode 204 and described drain electrode 205 are previously formed, described grid 201 and described gate insulation layer 202 in rear formation, Described thin film transistor (TFT) 20 is top gate type thin film transistor 20.
For top gate type thin film transistor 20, as shown in figure 1, can first pass through patterning processes formed described Active layer 203, described source electrode 204 and described drain electrode 205, then form described gate insulation layer 202 and institute by patterning processes State grid 201.That is, described top gate type thin film transistor 20 can just be formed by patterning processes twice.
For bottom gate thin film transistor 20, as shown in Fig. 2 can first pass through patterning processes formed described Grid 201, then forms described gate insulation layer 202 by patterning processes, then by patterning processes formed described in have Active layer 203, described source electrode 204 and described drain electrode 205.That is, described bottom gate thin film can just be formed by three patterning processes Transistor 20.
Embodiments provide a kind of preparation method of thin film transistor (TFT) 20, methods described is included by a composition Technique forms active layer 203, source electrode 204 and drain electrode 205 on substrate, and described active layer 203, described source electrode 204 and described Drain electrode 205 is located at same layer.Compared with prior art, this preparation method can efficiently reduce the number of times of patterning processes, thus The production capacity of volume production product, reduces cost can be lifted.
Based on foregoing description it is preferred that with reference to shown in Fig. 1, institute can be formed in the way of using by patterning processes twice State top gate type thin film transistor 20 it may be assumed that described active layer 203, described source electrode 204 are formed on substrate by patterning processes With described drain electrode 205；On the substrate being formed with described active layer 203, described source electrode 204 and described drain electrode 205, by once Patterning processes form the gate insulation layer 202 being located at described active layer 203, described source electrode 204 and described drain electrode 205 top and grid 201.
Need exist for illustrating, because described gate insulation layer 202 includes in the neighboring area of described thin film transistor (TFT) 20 For example expose the via of grid line lead, therefore, be also required to be patterned technique when forming described gate insulation layer 202, etch Via positioned at neighboring area.
Optionally, as shown in Fig. 3 (a) to Fig. 3 (f), described pass through patterning processes active layer is formed on substrate 203rd, source electrode 204 and drain electrode 205, specifically may include that
Shown in s101, such as Fig. 3 (a), substrate forms layer of semiconductor thin film 11, and on described semiconductive thin film 11 Form photoresist 40.
Shown in s102, such as Fig. 3 (b), using masstone mask plate 50, the substrate being formed with described photoresist 40 is exposed After light, development, form photoresist and part 401, photoresist half member-retaining portion 402 and photoresist completely removal part are fully retained 403.
Wherein, described photoresist is fully retained the region of part 401 correspondence semiconductor active layer 203 to be formed, described Photoresist half member-retaining portion 402 correspondence described source electrode 204 to be formed and the region of described drain electrode 205, described photoresist is complete Remove part 403 and correspond to other regions.
Here, with reference to Fig. 3 (b) cardinal principle of described masstone mask plate 50 is carried out as described below:
Described masstone mask plate 50 is by grating effect, makes to be exposed on the intensity of the transmission light of zones of different not With so that described photoresist 40 carries out selectivity exposure, development.Described masstone mask plate 50 include opaque section 501, Translucent portion 502 and transparent part 503.After overexposure, it is right that described photoresist is fully retained part 401 to described photoresist 40 Answer the opaque section 501 of described masstone mask plate 50, described photoresist half member-retaining portion 402 corresponds to described masstone mask The translucent portion 502 of plate 50, described photoresist removes the transparent part of the corresponding described masstone mask plate 50 of part 403 completely 503.
Wherein, in all embodiments of the invention, the described photoresist 40 of indication is positive photoresist, i.e. described masstone mask In plate 50, it is complete exposure area that described photoresist removes the corresponding region of part 403 completely, corresponding described masstone mask plate 50 light transmission part；The corresponding region of described photoresist half member-retaining portion 402 is half-exposure region, corresponding described masstone mask The semi-transparent part of plate 50；Described photoresist is fully retained the corresponding region of part 401 for not exposure area, corresponding described polychrome Adjust the lightproof part of mask plate 50.
Shown in s103, such as Fig. 3 (c), part 403 is removed completely using the etching technics described photoresist of removal corresponding described Semiconductive thin film 11.
The photoresist 40 of described photoresist half member-retaining portion 402 shown in s104, such as Fig. 3 (d), is removed using cineration technics.
Shown in s105, such as Fig. 3 (e), metalized is carried out to described semiconductive thin film 11, makes the described quasiconductor exposing Thin film 11 is converted into the thin film with conductor characteristics, forms described source electrode 204 and described drain electrode 205；Corresponding described photoresist is complete The described semiconductive thin film 11 of full member-retaining portion 401 is affected by metalized, forms described semiconductor active layer 203.
Here, the described semiconductive thin film 11 carrying out metalized is metal-oxide film, described metal-oxide Thin film is using the transparent metal oxide material in characteristic of semiconductor.
Wherein, the described transparent metal oxide material in characteristic of semiconductor includes indium gallium zinc oxide (igzo), indium gallium At least one in oxide (igo), amorphous state indium stannum zinc oxide (itzo), aluminum zinc oxide (azo).
Shown in s106, such as Fig. 3 (f), the photoresist that described photoresist is fully retained part 401 is removed using stripping technology 40.
By above-mentioned steps s101-s106, described active layer 203, described source electrode 204 and described just can be formed on substrate Drain electrode 205.Wherein, described source electrode 204 and described drain electrode 205 are by the thin film shape through metalized with conductor characteristics Become, described semiconductor active layer 203 is formed by the metal-oxide film without metalized with characteristic of semiconductor.
Method that is further alternative, carrying out metalized to described semiconductive thin film 11, specifically can include following Three kinds of modes:
The first: the substrate with the described semiconductive thin film 11 exposing is placed in vacuum chamber and is heated to default temperature Degree, and cool down in atmosphere after keeping Preset Time, wherein, described preset temperature is 200～300 DEG C, and described Preset Time is 20～40 minutes.
Second: the substrate with the described semiconductive thin film 11 exposing is placed in reducing atmosphere at 200～400 DEG C Carry out heat treatment.
The third: the substrate with the described semiconductive thin film 11 exposing is placed in vacuum chamber, using hydrogen etc. from Daughter or oxygen gas plasma are processed, and wherein, the pressure in described vacuum chamber is 1000～2000mtorr, and gas flow is 5000～15000sccm.
The described semiconductive thin film 11 being formed when the transparent metal oxide material with characteristic of semiconductor is through above-mentioned three After any one mode in the mode of kind is processed, the carrier concentration of inside can be led to improve, assume conductor characteristics, thus forming institute State source electrode 204 and described drain electrode 205.And it is located at the described semiconductive thin film 11 not carrying out metalized under described photoresist 40 Carrier concentration relatively low, assume characteristic of semiconductor, thus forming described semiconductor active layer 203.
It should be noted that the method that the embodiment of the present invention carries out metalized to described semiconductive thin film 11 is not limited to Above-mentioned three kinds of modes, as long as be advantageous for the described semiconductive thin film 11 with characteristic of semiconductor is converted into conductor characteristics Thin film.
The embodiment of the present invention also provides a kind of preparation method of array base palte 10, as shown in Figure 4 and Figure 5, brilliant including thin film Body pipe 20 and the preparation of pixel electrode 30.Wherein, described thin film transistor (TFT) 20 can be adopted and be prepared with the aforedescribed process；Described Pixel electrode 30 can be prepared and formed together with described source electrode 204 and described drain electrode 205.
On this basis, optionally, by patterning processes, the described active layer being located at same layer is formed on substrate 203rd, described source electrode 204 and while described drain electrode 205, can also form and be connected with described drain electrode 205 and the pixel with layer is electric Pole 30；Wherein, described drain electrode 205 is structure as a whole and has identical material with described pixel electrode 30.
Here, with reference to shown in Fig. 4, described array base palte 10 can include described top gate type thin film transistor 20；Or, ginseng Examine shown in Fig. 5, described array base palte 10 can also include described bottom gate thin film transistor 20.
Because described pixel electrode 30 can be with described active layer 203, described source electrode 204 and the described shape together with 205 that drains Become, therefore, in the case that described array base palte 10 includes described top gate type thin film transistor 20, can be by composition work twice Skill forms described array base palte 10；In the case that described array base palte 10 includes described bottom gate thin film transistor 20, permissible Form described array base palte 10 by three patterning processes.
Optionally, as shown in Fig. 6 (a) to Fig. 6 (h), formed on substrate by patterning processes and be located at same layer Described active layer 203, described source electrode 204 and described drain electrode 205, and the pixel electrode 30 being connected with described drain electrode 205, specifically May include that
Shown in s201, such as Fig. 6 (a), substrate forms layer of semiconductor thin film 11, and on described semiconductive thin film 11 Form photoresist 40.
Shown in s202, such as Fig. 6 (b), using masstone mask plate 50, the substrate being formed with described photoresist 40 is exposed After light, development, form photoresist and part 401, photoresist half member-retaining portion 402 and photoresist completely removal part are fully retained 403.
Wherein, described photoresist is fully retained the region of part 401 correspondence described semiconductor active layer 203 to be formed, Described photoresist half member-retaining portion 402 correspondence described source electrode 204 to be formed and described drain electrode 205 and with described drain electrode 205 The region of the described pixel electrode 30 of electrical connection, described photoresist removes part 403 completely and corresponds to other regions.
Shown in s203, such as Fig. 6 (c), part 403 is removed completely using the etching technics described photoresist of removal corresponding described Semiconductive thin film 11.
The photoresist 402 of described photoresist half member-retaining portion shown in s204, such as Fig. 6 (d), is removed using cineration technics.
Shown in s205, such as Fig. 6 (e), metalized is carried out to described semiconductive thin film 11, makes the described quasiconductor exposing Thin film 11 is converted into the thin film with conductor characteristics, formed described source electrode 204 and described drain electrode 205 and with described drain electrode 205 The pixel electrode 30 of electrical connection；The described semiconductive thin film 11 that corresponding described photoresist is fully retained part 401 is metallized Process impact, form described semiconductor active layer 203.
Here, the described semiconductive thin film 11 carrying out metalized can be metal-oxide film, described metal oxygen Compound thin film is using the transparent metal oxide material in characteristic of semiconductor.
Shown in s206, such as Fig. 6 (f), the photoresist that described photoresist is fully retained part 401 is removed using stripping technology 40.
By above-mentioned steps s201-s206, described semiconductor active layer 203, described source electrode 204 just can be formed on substrate The pixel electrode 30 electrically connect with described drain electrode 205 and with described drain electrode 205.Wherein, described source electrode 204 and described drain electrode 205 and described pixel electrode 30 formed by the thin film through metalized with conductor characteristics, described semiconductor active Layer 203 is formed by the metal-oxide film without metalized with characteristic of semiconductor.
On the basis of above-mentioned steps, more described gate insulation layer 202 can also be formed by a masstone masking process With described grid 201, specifically may include that
Shown in s207, such as Fig. 6 (g), it is being formed with described semiconductor active layer 203, described source electrode 204 and described drain electrode 205 and described pixel electrode 30 substrate on sequentially form one layer of gate insulation layer film 12 and layer of metal thin film 13, and Described metallic film 13 top forms photoresist 40.
Shown in s208, such as Fig. 6 (h), using masstone mask plate 50, the substrate being formed with described photoresist 40 is exposed After light, development, form photoresist and part 401, photoresist half member-retaining portion 402 and photoresist completely removal part are fully retained 403.
Wherein, described photoresist is fully retained part 401 correspondence described grid 201 to be formed, grid line and grid line lead The region of (in figure does not mark), described photoresist removes the via to be formed of the corresponding neighboring area of part 403 completely, and (in figure is not Mark), described photoresist half member-retaining portion 402 corresponds to other regions.
S209, using etching technics remove described photoresist remove the corresponding described metallic film 13 of part 403, shape completely Become to include the gate insulation layer 202 of described via (in figure does not mark)；Then adopt cineration technics to remove described photoresist half to retain The photoresist 40 of part 402, and corresponding described metallic film 13 below is removed using etching technics, form described grid 201st, grid line, grid line lead etc..
S210, remove described photoresist using stripping technology the photoresist 40 of part 401 is fully retained, formed with reference to Fig. 4 Shown array base palte 10.
Array base palte 10 provided in an embodiment of the present invention not only can be applied to the life of twisted nematic liquid crystals display device Produce, can be applicable to the production of advanced super dimension switch type liquid crystal indicator.
On this basis, further, as shown in fig. 7, methods described also includes: by patterning processes on substrate Form public electrode 60.
Wherein, for Senior super dimension field switch technology, its core technology characteristic can be described as: by same plane Electric field produced by interior gap electrode edge and gap electrode layer form multi-dimensional electric field with the electric field of plate electrode interlayer generation, Make in liquid crystal cell between gap electrode, directly over electrode, all aligned liquid-crystal molecules can produce rotation, thus improve liquid crystal Work efficiency simultaneously increases light transmission efficiency.Senior super dimension field switch technology can improve the picture of liquid crystal display panel of thin film transistor Face quality, has high-resolution, high permeability, low-power consumption, wide viewing angle, high aperture, low aberration, ripple without water of compaction etc. excellent Point.
Specific embodiment preparation method to the array base palte 10 with top gate type thin film transistor 20 is provided below Illustrate.As shown in figure 8, the method specifically includes following steps:
Shown in s301, reference Fig. 6 (a), being sequentially depositing a layer thickness on substrate using magnetron sputtering method isExtremelyIndium gallium zinc oxide igzo thin film, and described igzo film surface coat one layer of photoresist 40.
Wherein, described igzo thin film is the transparent metal oxide film with characteristic of semiconductor.
Shown in s302, reference Fig. 6 (b), using masstone mask plate 50, the substrate being formed with described photoresist 40 is carried out After exposure, development, form photoresist and part 401, photoresist half member-retaining portion 402 and photoresist completely removal part are fully retained 403.
Wherein, described photoresist is fully retained part 401 correspondence metal-oxide semiconductor (MOS) active layer 203 to be formed Region, described photoresist half member-retaining portion 402 correspondence source electrode to be formed 204 and drain electrode 205 and with described drain electrode 205 electricity The region of the pixel electrode 30 connecting, described photoresist removes part 403 completely and corresponds to other regions.
Shown in s303, reference Fig. 6 (c), described photoresist is removed using etching technics and removes the corresponding institute of part 403 completely State igzo thin film.
Shown in s304, reference Fig. 6 (d), remove the photoresist of described photoresist half member-retaining portion 402 using cineration technics 40.
Now, the igzo in the region of correspondence source electrode 204 to be formed and described drain electrode 205 and described pixel electrode 30 Thin film exposes outside；The igzo film surface in the correspondence region of described metal-oxide semiconductor (MOS) active layer 203 to be formed is still Photoresist 40 is had to cover.
Shown in s305, reference Fig. 6 (e), corona treatment is carried out to aforesaid substrate, makes that exposes to have characteristic of semiconductor Igzo thin film be converted into the thin film with conductor characteristics, thus formed described source electrode 204 and described drain electrode 205 and with institute State the described pixel electrode 30 of drain electrode 205 electrical connection, described drain electrode 205 is structure as a whole with described pixel electrode 30.
Now, the igzo thin film positioned at described photoresist 40 lower section does not carry out corona treatment, still keeps its quasiconductor Characteristic, thus form described metal-oxide semiconductor (MOS) active layer 203.
Wherein, described corona treatment specifically includes: the substrate with the metal-oxide film exposing is placed in very In plenum chamber, processed using hydrogen gas plasma or oxygen gas plasma；Now, the pressure in described vacuum chamber be 1000～ 2000mtorr, the gas flow of described hydrogen or oxygen is 5000～15000sccm, in described vacuum chamber between two-plate Power be 1500～2500w.
Shown in s306, reference Fig. 6 (f), the photoresist that described photoresist is fully retained part 401 is removed using stripping technology 40.
Shown in s307, such as Fig. 6 (g), described metal-oxide semiconductor (MOS) active layer is being formed with using magnetron sputtering method 203rd, it is sequentially depositing one layer of gate insulation layer on the substrate of described source electrode 204 and described drain electrode 205 and described pixel electrode 30 thin Film 12 and metallic film 13, and the one layer of photoresist 40 of surface-coated in described metallic film 13.
Shown in s308, such as Fig. 6 (h), using masstone mask plate 50, the substrate being formed with described photoresist 40 is exposed After light, development, form photoresist and part 401, photoresist half member-retaining portion 402 and photoresist completely removal part are fully retained 403.
Wherein, described photoresist is fully retained part 401 correspondence grid 201 to be formed, grid line and grid line lead (in figure Do not mark) region, described photoresist removes the via to be formed of the corresponding neighboring area of part 403 completely, and (in figure is not marked Go out), described photoresist half member-retaining portion 402 corresponds to other regions.
Shown in s309, reference Fig. 6 (h), described photoresist is removed using etching technics and removes the corresponding institute of part 403 completely State metallic film 13, form the gate insulation layer 202 including described via (in figure does not mark)；Then cineration technics is adopted to remove institute State the photoresist 40 of photoresist half member-retaining portion 402, and corresponding described metallic film 13 below removed using etching technics, Form described grid 201, grid line, grid line lead etc..
S310, remove described photoresist using stripping technology the photoresist 40 of part 401 is fully retained, formed with reference to Fig. 4 Shown array base palte 10.
By above-mentioned steps s301-s310, only pass through patterning processes twice and just can get, with reference to shown in Fig. 4, there is top-gated The array base palte 10 of type thin film transistor (TFT) 20, is effectively reduced the number of times of patterning processes, thus the product of volume production product can be lifted Can, reduces cost.
Further, with reference to shown in Fig. 7, on the basis of completing described step s301-s310, methods described can also be wrapped Include:
S311, passivation layer 70 is formed on aforesaid substrate using magnetron sputtering method.
S312, patterning processes are passed through on the substrate being formed with described passivation layer 70 form public electrode 60.
By above-mentioned steps s301-s312, just can form advanced super dimension switch type array base palte, be effectively reduced structure Figure technique number of times, thus lift the production capacity of volume production product, reduces cost.
The embodiment of the present invention provides a kind of thin film transistor (TFT) 20, and with reference to shown in Fig. 1 and Fig. 2, described thin film transistor (TFT) 20 wraps Include active layer 203 and the source electrode 204 and the drain electrode 205 that are located at described active layer 203 both sides；Wherein, described active layer 203, institute State source electrode 204 and described drain electrode 205 with layer setting.
Certainly, described thin film transistor (TFT) 20 also includes grid 201 and gate insulation layer 202.
Here, the relative position relation of described grid 201 and described active layer 203 is not especially limited.Need explanation , described thin film transistor (TFT) 20 can be top-gate type structure, i.e. described grid 201 is located above described active layer 203；Or Person, described thin film transistor (TFT) 20 can also be bottom-gate type configuration, i.e. described grid 201 is located at below described active layer 203.
On this basis, optionally, the material of described active layer 203 can be the transparent metal oxide in characteristic of semiconductor Thing material；Described source electrode 204 and described drain electrode 205 material be with described active layer 203 identical material at metallization The material obtaining after reason.
Further alternative, the described transparent metal oxide material in characteristic of semiconductor include igzo, igo, itzo, At least one in azo.
Based on foregoing description it is preferred that with reference to shown in Fig. 1, described thin film transistor (TFT) 20 is top gate type thin film transistor. That is, it is additionally provided with gate insulation layer 202 and grid above described source electrode 204 and described drain electrode 205 and described active layer 203 Pole 201.
When described thin film transistor (TFT) 20 has top-gate type structure, institute can be formed according to first passing through patterning processes State active layer 203, described source electrode 204 and described drain electrode 205, then form described gate insulation layer 202 He by patterning processes The order of described grid 201 is prepared.So, only pass through patterning processes twice and just can form described thin film transistor (TFT) 20, have Effect ground reduces the number of times of patterning processes, thus lifting the production capacity of volume production product, reduces cost.
The embodiment of the present invention also provides a kind of array base palte 10, and with reference to shown in Fig. 4 and Fig. 5, described array base palte 10 includes Above-mentioned thin film transistor (TFT) 20 and pixel electrode 30.
Optionally, the drain electrode 205 of described thin film transistor (TFT) 20 is connected with described pixel electrode 30；Described thin film transistor (TFT) 20 Active layer 203, source electrode 204 and drain electrode 205 and described pixel electrode 30 with layer arrange；Wherein, described drain electrode 205 and institute State pixel electrode 30 to be structure as a whole and there is identical material.
In the case that described array base palte 10 is advanced super dimension switch type array base palte, with reference to shown in Fig. 7, described battle array Row substrate 10 can also include public electrode 60.
Although it should be noted that in above-described embodiment, so that described drain electrode 205 is connected with described pixel electrode 30 as a example entering Go explanation, but it should be apparent to a person skilled in the art that due to the described source electrode 204 of thin film transistor (TFT) 20 and described drain electrode It is also possible to described source electrode 204 is connected with described pixel electrode 30, this belongs to this to 205 interchangeabilitys in structure and composition The equivalents of above-described embodiment of invention.
The embodiment of the present invention also provides a kind of display device, including above-mentioned array base palte 10.
The display device that the embodiment of the present invention is provided can be: liquid crystal panel, Electronic Paper, LCD TV, liquid crystal display Device, organic light emitting diode display (organic light emitting diode, abbreviation oled), DPF, mobile phone, Panel computer etc. has product or the part of any display function.
1. a kind of preparation method of thin film transistor (TFT) is it is characterised in that methods described includes: by patterning processes in substrate Upper formation active layer, source electrode and drain electrode, and described active layer, described source electrode and described drain electrode are located at same layer；Described by one Secondary patterning processes form active layer, source electrode and drain electrode on substrate, specifically include:
Substrate forms layer of semiconductor thin film, and photoresist is formed on described semiconductive thin film；
After the substrate being formed with described photoresist being exposed, develops using masstone mask plate, form photoresist and protect completely Stay part, photoresist half member-retaining portion and photoresist removal part completely；Wherein, described photoresist is fully retained partly correspondence and treats The region of the semiconductor active layer being formed, described photoresist half member-retaining portion correspondence described source electrode to be formed and described drain electrode Region, described photoresist removes partly correspond to other regions completely；
Described photoresist is removed using etching technics and removes partly corresponding described semiconductive thin film completely；
Remove the photoresist of described photoresist half member-retaining portion using cineration technics；
Metalized is carried out to described semiconductive thin film, so that the described semiconductive thin film exposing is converted into and there are conductor characteristics Thin film, forms described source electrode and described drain electrode；The described semiconductive thin film that corresponding described photoresist is fully retained part is not subject to gold Genusization processes impact, forms described semiconductor active layer；
The photoresist that described photoresist is fully retained part is removed using stripping technology.
2. method according to claim 1 it is characterised in that carry out the side of metalized to described semiconductive thin film Method, specifically includes:
The substrate with the described semiconductive thin film exposing is placed in reducing atmosphere and carries out heat treatment at 200～400 DEG C； Or,
The substrate with the described semiconductive thin film exposing is placed in vacuum chamber, using hydrogen gas plasma or oxygen etc. from Daughter is processed, and wherein, pressure in described vacuum chamber is 1000～2000mtorr, and gas flow is 5000～ 15000sccm.
3. method according to claim 2 is it is characterised in that the described semiconductive thin film carrying out metalized is metal Sull, described metal-oxide film is using the transparent metal oxide material in characteristic of semiconductor.
4. method according to claim 3 is it is characterised in that the described transparent metal oxide material in characteristic of semiconductor Including at least one in indium gallium zinc oxide, indium gallium oxide, amorphous state indium stannum zinc oxide, aluminum zinc oxide.
5. method according to claim 1 is it is characterised in that be formed with described active layer, described source electrode and described leakage On the substrate of pole, form, by patterning processes, the gate insulation being located above described active layer, described source electrode and described drain electrode Layer and grid.
6. a kind of preparation method of array base palte, the preparation including thin film transistor (TFT) and pixel electrode is it is characterised in that described thin The preparation method of film transistor is the preparation method of the thin film transistor (TFT) described in any one of claim 1 to 5.
7. method according to claim 6 is it is characterised in that formed positioned at same by patterning processes on substrate While the active layer of layer, source electrode and drain electrode, also formed and electrically connect and the pixel electrode with layer with described drain electrode；
Wherein, described drain electrode is structure as a whole and has identical material with described pixel electrode.
8. method according to claim 7 is it is characterised in that formed positioned at same by patterning processes on substrate The described active layer of layer, described source electrode and described drain electrode and the pixel electrode being electrically connected with described drain electrode, are specifically included:
After the substrate being formed with described photoresist being exposed, develops using masstone mask plate, form photoresist and protect completely Stay part, photoresist half member-retaining portion and photoresist removal part completely；Wherein, described photoresist is fully retained partly correspondence and treats The region of the semiconductor active layer being formed, described photoresist half member-retaining portion correspondence described source electrode to be formed and drain electrode and The region of the described pixel electrode electrically connecting with described drain electrode, described photoresist removes partly correspond to other regions completely；
Metalized is carried out to described semiconductive thin film, so that the described semiconductive thin film exposing is converted into and there are conductor characteristics Thin film, forms described source electrode and described drain electrode and the pixel electrode electrically connecting with described drain electrode；Corresponding described photoresist is complete The described semiconductive thin film of member-retaining portion is affected by metalized, forms described semiconductor active layer；
9. method according to claim 6 is it is characterised in that methods described also includes: by patterning processes in base Public electrode is formed on plate.
CN201310740724.5A 2013-12-27 2013-12-27 Thin film thyristor and manufacturing method thereof, array substrate and manufacturing method thereof and display device CN103715094B (en)
CN201310740724.5A CN103715094B (en) 2013-12-27 2013-12-27 Thin film thyristor and manufacturing method thereof, array substrate and manufacturing method thereof and display device
US14/430,019 US9806108B2 (en) 2013-12-27 2014-05-29 Manufacturing method of thin film transistor, manufacturing method of array substrate and array substrate
PCT/CN2014/078858 WO2015096394A1 (en) 2013-12-27 2014-05-29 Thin film transistor manufacturing method, array substrate manufacturing method and array substrate
CN103715094A CN103715094A (en) 2014-04-09
CN103715094B true CN103715094B (en) 2017-02-01
ID=50407969
US (1) US9806108B2 (en)
CN (1) CN103715094B (en)
WO (1) WO2015096394A1 (en)
CN103474474B (en) 2013-09-16 2016-08-17 北京京东方光电科技有限公司 TFT and preparation method thereof, array base palte and preparation method thereof, X-ray detector
CN103928343B (en) * 2014-04-23 2017-06-20 深圳市华星光电技术有限公司 Thin film transistor (TFT) and organic light emitting diode display preparation method
CN104576760A (en) 2015-02-02 2015-04-29 合肥鑫晟光电科技有限公司 Thin film transistor, manufacturing method thereof, array substrate and display device
CN104810375B (en) * 2015-04-28 2018-09-04 合肥鑫晟光电科技有限公司 A kind of array substrate and preparation method thereof and a kind of display device
CN104851789B (en) 2015-06-08 2018-05-01 京东方科技集团股份有限公司 Thin film transistor (TFT) and production method, array base palte and production method and display device
KR20170097251A (en) * 2016-02-17 2017-08-28 삼성디스플레이 주식회사 Display device and method for fabricating the same
CN105845693A (en) * 2016-03-28 2016-08-10 深圳市华星光电技术有限公司 Film transistor, manufacturing method of film transistor and liquid crystal display panel
CN105762112A (en) 2016-04-28 2016-07-13 京东方科技集团股份有限公司 Thin film transistor array substrate and preparation method thereof and display device
CN106373967B (en) * 2016-10-27 2017-12-22 京东方科技集团股份有限公司 Array base palte and preparation method thereof, display device
CN107910351A (en) * 2017-11-14 2018-04-13 深圳市华星光电技术有限公司 The production method of TFT substrate
CN109755261A (en) * 2018-12-26 2019-05-14 深圳市华星光电半导体显示技术有限公司 A kind of array substrate and preparation method thereof
CN1460979A (en) * 2002-03-22 2003-12-10 株式会社日立显示器 Display device
CN102237411A (en) * 2010-05-05 2011-11-09 元太科技工业股份有限公司 Oxide thin film transistor and manufacturing method thereof
JP2658850B2 (en) 1993-12-24 1997-09-30 日本電気株式会社 Thin film transistor
JP2003007716A (en) * 2001-06-18 2003-01-10 Sharp Corp Semiconductor device and its manufacturing method
JP4708099B2 (en) * 2005-07-04 2011-06-22 シャープ株式会社 Mask for manufacturing a transistor and method for manufacturing a transistor using the same
WO2009031681A1 (en) 2007-09-07 2009-03-12 Nec Corporation Switching device and method for manufacturing the same
CN101546077B (en) 2008-03-26 2010-12-08 北京京东方光电科技有限公司 Pixel structure of thin film transistor-liquid crystal display and manufacturing method thereof
KR20140089813A (en) * 2013-01-07 2014-07-16 삼성디스플레이 주식회사 Thin film transistor, method for fabricting the same and display apparatus having the same
2013-12-27 CN CN201310740724.5A patent/CN103715094B/en active IP Right Grant
2014-05-29 WO PCT/CN2014/078858 patent/WO2015096394A1/en active Application Filing
2014-05-29 US US14/430,019 patent/US9806108B2/en active Active
US9806108B2 (en) 2017-10-31
CN103715094A (en) 2014-04-09
WO2015096394A1 (en) 2015-07-02
US20160027818A1 (en) 2016-01-28
US20130122624A1 (en) 2013-05-16 Thin film transistor liquid crystal display array substrate and manufacturing method thereof
CN101957530A (en) 2011-01-26 TFT-LCD (Thin Film Transistor-Liquid Crystal Display) array baseplate and manufacturing method thereof
EP2743982A2 (en) 2014-06-18 Display device, array substrate and manufacturing method thereof
CN103730472B (en) 2015-05-06 Array substrate, manufacturing method of array substrate and display device
CN102157563A (en) 2011-08-17 Method for manufacturing metal oxide thin film transistor