Matched Legal Cases: ['Application No. 2012', 'Application No. 10756901', 'Application No. 09747709', 'Application No. 10759242', 'Application No. 08', 'Application No. 09774505', 'Application No. 09774505', 'Application No. 2011', 'Application No. 2010', 'Application No. 2010', 'Application No. 2010', 'Application No. 2012', 'Application No. 2011', 'Application No. 2011', 'Application No. 2012', 'Application No. 2011', 'Application No. 10', 'Application No. 2012', 'Application No. 099109236', 'Application No. 098116219', 'Application No. 200880021733', 'Application No. 200980108344', 'Application No. 200880021733', 'Application No. 200980125925', 'Application No. 200980118341', 'Application No. 200980108344', 'Application No. 200980125925', 'Application No. 201080023851', 'Application No. 201080032626', 'Application No. 200980125925', 'Application No. 200980108344', 'Application No. 201080015842', 'Application No. 201080023851', 'Application No. 201080032626', 'Application No. 201080015842', 'Application No. 200980108344', 'Application No. 200980108344', 'Application No. 201080015842', 'Application No. 0977118130', 'Application No. 2008']

Photosintering of micron-sized copper particles - PEN INC.
United States Patent 9598776
Micron-sized metal particles in an ink or paste composition are deposited onto a substrate and then photosimered. The substrate may comprise a polymeric material. The polymeric substrate may have a coefficient of thermal expansion greater than two times the coefficient of thermal expansion of the photosimered ink or paste composition.
Abed, Ovadia (Austin, TX, US)
Ginsberg, Valerie Kaye (Austin, TX, US)
Novak, James P. (Austin, TX, US)
14/413294
PEN INC. (Deerfield Beach, FL, US)
B05D3/02; B05D3/06; C09D11/52; C23C24/10; H01B1/22; H05K1/09; H05K3/12
Download PDF 9598776 PDF help
8911823 Mechanical sintering of nanoparticle inks and powders December, 2014 Li et al.
20140314966 Sintering Metallic Inks on Low Melting Point Substrates October, 2014 Fink et al.
20140302255 SCALABLE PROCESSING OF NANOCOMPOSITES USING PHOTON-BASED METHODS October, 2014 Spicer et al.
8647979 Buffer layer to enhance photo and/or laser sintering February, 2014 Yaniv et al.
20110155430 ANISOTROPIC CONDUCTIVE ADHESIVE COMPOSITE AND FILM, AND CIRCUIT CONNECTING STRUCTURE INCLUDING THE SAME June, 2011 Lee et al.
20110043965 Applying Optical Energy to Nanoparticles to Produce a Specified Nanostructure February, 2011 Yaniv et al.
7879131 Metal encapsulation February, 2011 Yaniv et al.
7867413 Ink for ink jet printing and method for preparing metal nanoparticles used therein January, 2011 Lee et al.
7786024 Selective processing of semiconductor nanowires by polarized visible radiation August, 2010 Stumbo et al.
7776196 Method for arranging particles and method for manufacturing light-emitting device August, 2010 Fujimoto et al.
20100035375 MASKLESS NANOFABRICATION OF ELECTRONIC COMPONENTS February, 2010 Grigoropoulos et al.
20090274833 METALLIC INK November, 2009 Li et al.
20090142481 AIR STABLE COPPER NANOPARTICLE INK AND APPLICATIONS THEREFOR June, 2009 Chopra et al.
7547479 Tin-coated printed circuit boards with low tendency to whisker formation June, 2009 Wessling
7514369 Method of producing porous silicon particles by stain-etching and silicon nanoparticles from stain-etched silicon powder April, 2009 Li et al.
7507618 Method for making electronic devices using metal oxide nanoparticles March, 2009 Dunbar
7482540 Flat cable 2009-01-27 Shukushima et al.
20080305268 Low Temperature Thermal Conductive Inks December, 2008 Norman et al.
20080286488 METALLIC INK 2008-11-20 Li 427/541
20080264205 Method for Making Nanoparticles October, 2008 Zeng et al.
20080241414 CONDUCTIVE INK COMPOSITION AND METHOD OF FORMING A CONDUCTIVE PATTERN USING THE SAME October, 2008 Kim et al.
20080241391 METHOD OF MANUFACTURING A METAL NANOPARTICLE, CONDUCTIVE INK COMPOSITION HAVING THE METAL NANOPARTICLE AND METHOD OF FORMING A CONDUCTIVE PATTERN USING THE SAME October, 2008 Kim et al.
20080193667 Ink Jet Printable Compositions August, 2008 Garbar et al.
20080169122 Electrically Conductive Ink, Electrically Conductive Circuit, and Non-Contact-Type Medium July, 2008 Shiraishi et al.
20080164557 Semiconductor device and method of forming the same July, 2008 Kim et al.
20080160309 Electrically Conductive Fine Particles, Anisotropic Electrically Conductive Material, and Electrically Conductive Connection Method July, 2008 Kubota
7391116 Fretting and whisker resistant coating system and method 2008-06-24 Chen et al.
7384862 Method for fabricating semiconductor device and display device 2008-06-10 Yamazaki et al.
20080143906 NANOWIRE-BASED TRANSPARENT CONDUCTORS AND APPLICATIONS THEREOF June, 2008 Allemand et al.
7357681 Electrical connector 2008-04-15 Yamagami et al.
7351667 Etching solution for silicon oxide method of manufacturing a semiconductor device using the same 2008-04-01 Hwang et al.
20080075934 Tamper Event Detection Films, Systems and Methods March, 2008 Barlow et al.
7316725 Copper powders methods for producing powders and devices fabricated from same 2008-01-08 Kodas et al.
20080020208 Conducting polymer composition, conductive film formed using the conducting polymer composition, and electronic device including the conductive film January, 2008 Lee et al.
20070295530 Coatings and methods for inhibiting tin whisker growth December, 2007 Jackson et al.
20070289483 Conductive ink composition for inkjet printing December, 2007 Cho et al.
20070287024 Abrasive powder coatings and methods for inhibiting tin whisker growth December, 2007 Jackson et al.
20070287023 Multi-phase coatings for inhibiting tin whisker growth and methods of making and using the same December, 2007 Jackson et al.
20070284700 Coatings and methods for inhibiting tin whisker growth December, 2007 Jackson et al.
20070281249 NOVEL NANOPARTICLE PATTERNING PROCESS December, 2007 Tutt et al.
20070281136 Ink jet printed reflective features and processes and inks for making them December, 2007 Hampden-Smith et al.
7297902 High performance defrosters for transparent panels 2007-11-20 Weiss
7294366 Laser processing for heat-sensitive mesoscale deposition 2007-11-13 Renn et al.
20070275262 Reducing formation of tin whiskers on a tin plating layer November, 2007 Lin et al.
7262603 System and method for sensing the formation of tin whiskers 2007-08-28 Benton et al.
7252699 Method for patterning metal using nanoparticle containing precursors 2007-08-07 Perry et al.
20070190326 METHOD FOR PATTERNING METAL USING NANOPARTICLE CONTAINING PRECURSORS August, 2007 Perry et al.
20070176991 Ink composition and recording method using the same August, 2007 Arai et al.
20070175296 Method of forming conductors at low temperatures using metallic nanocrystals and product August, 2007 Subramanian et al.
20070166453 High-throughput printing of chalcogen layer July, 2007 Van Duren et al.
20070163643 High-throughput printing of chalcogen layer and the use of an inter-metallic material July, 2007 Van Duren
20070158204 TIN AND TIN ALLOY ELECTROPLATING METHOD WITH CONTROLLED INTERNAL STRESS AND GRAIN SIZE OF THE RESULTING DEPOSIT July, 2007 Taylor et al.
20070148972 Method of repairing seed layer for damascene interconnects June, 2007 Hara et al.
20070145375 Method of manufacturing nanowire, method of manufacturing a semiconductor apparatus including nanowire and semiconductor apparatus formed from the same June, 2007 Cho
7215014 Solderable metal finish for integrated circuit package leads and method for forming 2007-05-08 Su et al.
20070117475 Prevention of Sn whisker growth for high reliability electronic devices May, 2007 Tu
20070105395 LASER FUNCTIONALIZATION AND PATTERNING OF THICK-FILM INKS May, 2007 Kinzel et al.
20070095879 Methods and apparatus for assembling a printed circuit board May, 2007 Holmes
7195702 Tin alloy electroplating system 2007-03-27 Bokisa, Sr. et al.
20070074316 Nanowires-based transparent conductors March, 2007 Alden et al.
20070051927 Fine metal particles and fine metal oxide particles in dry powder form, and use thereof March, 2007 Itoh et al.
7179362 Electrolyte and method for depositing tin-copper alloy layers 2007-02-20 Dietterle et al.
7160629 Tin plating 2007-01-09 Crosby
20070007144 Tin electrodeposits having properties or characteristics that minimize tin whisker growth January, 2007 Schetty, III
7153775 Conductive material patterning methods 2006-12-26 Geusic
20060286301 Substrates and method of manufacturing same December, 2006 Murata et al.
20060240591 System and method for processing nanowires with holographic optical tweezers October, 2006 Grier et al.
20060234519 Contact doping and annealing systems and processes for nanowire thin films October, 2006 Pan et al.
7087523 Method for producing a structure using nanoparticles 2006-08-08 Grigoropoulos et al.
20060189113 Metal nanoparticle compositions August, 2006 Vanheusden et al.
20060183055 Method for defining a feature on a substrate August, 2006 O'Neill et al.
7084067 Removal of copper oxides from integrated interconnects 2006-08-01 Geusic et al.
20060163743 Semiconductor device and method for manufacturing the same, and electric device July, 2006 Kuwabara et al.
20060159838 Controlling ink migration during the formation of printable electronic features July, 2006 Kowalski et al.
7062848 Printable compositions having anisometric nanostructures for use in printed electronics 2006-06-20 Pan et al.
20060141268 Nanoparticle coated nanostructured surfaces for detection, catalysis and device applications June, 2006 Kalkan et al.
20060116000 Manufacturing method of insulating film and semiconductor device June, 2006 Yamamoto
20060111467 Ink jet composition May, 2006 Reinhardt et al.
20060110424 Ceramic and metal compositions May, 2006 Lyles
20060096867 Tin alloy electroplating system May, 2006 Bokisa et al.
20060091121 Method for reflowing a metal plating layer of a contact and contact formed thereby May, 2006 Zanolli et al.
20060090819 Tin plating method May, 2006 Egli
20060082952 Electroconductive paste composition April, 2006 Ogiwara
20060073680 Epitaxial growth of aligned algainn nanowires by metal-organic chemical vapor deposition April, 2006 Han et al.
7019391 NANO IC packaging 2006-03-28 Tran
20060068218 Whisker-free lead frames March, 2006 Hooghan
20060062701 Method of manufacturing microwave reaction device and microwave reaction device March, 2006 Nakamura et al.
20060057502 Method of forming a conductive wiring pattern by laser irradiation and a conductive wiring pattern March, 2006 Okada et al.
20060054668 Dual additive soldering March, 2006 Severin
20060011267 Solder paste and process January, 2006 Kay et al.
20060001726 Printable conductive features and processes for making same January, 2006 Kodas et al.
20050274480 Reduction of spontaneous metal whisker formation December, 2005 Barsoum et al.
20050249969 Preserving solderability and inhibiting whisker growth in tin surfaces of electronic components November, 2005 Xu et al.
20050249968 Whisker inhibition in tin surfaces of electronic components November, 2005 Xu et al.
20050249967 Tin plating method November, 2005 Egli
6951666 Precursor compositions for the deposition of electrically conductive features 2005-10-04 Kodas et al.
20050230042 Bonding structure and method for bonding members October, 2005 Hasimoto
20050218398 NANO-electronics October, 2005 Tran
20050183768 Photovoltaic thin-film cell produced from metallic blend using high-temperature printing August, 2005 Roscheisen et al.
6917098 Three-level leadframe for no-lead packages 2005-07-12 Yamunan
20050148164 A SUSPENSION FOR FILLING VIA HOLES IN SILICON AND METHOD FOR MAKING THE SAME July, 2005 Casey et al.
20050145502 Minimizing whisker growth in tin electrodeposits July, 2005 Schetty, III et al.
6899775 Printing with differential adhesion 2005-05-31 Hill et al.
20050078158 Ink-jet inks containing metal nanoparticles April, 2005 Magdassi et al.
6860981 Minimizing whisker growth in tin electrodeposits 2005-03-01 Schetty, III et al.
20050026423 Method for fabricating semiconductor device and display device February, 2005 Yamazaki
20050019543 Ceramic and metal compositions January, 2005 Lyles
6828660 Semiconductor device with double nickel-plated leadframe 2004-12-07 Abbott
20040256239 Tin plating method December, 2004 Whitlaw et al.
20040241532 Carbon nanotube or carbon nanofiber electrode comprising sulfur or metal nanoparticles as a binder and process for preparing the same December, 2004 Kim
6824857 Circuit elements having an embedded conductive trace and methods of manufacture 2004-11-30 Lochun 361/748
20040232000 Tin plating November, 2004 Crosby
20040218136 Display device and manufacturing method thereof November, 2004 Imai et al.
20040192042 Doping of source-drain contacts September, 2004 Sirringhaus et al.
20040175631 Nanometer-scale engineered structures, methods and apparatus for fabrication thereof, and applications to mask repair, enhancement, and fabrications September, 2004 Crocker et al.
20040171211 Method of forming a trench for use in manufacturing a semiconductor device September, 2004 Lee et al.
6783569 Method for synthesis of core-shell type and solid solution alloy type metallic nanoparticles via transmetalation reactions and applications of same 2004-08-31 Cheon et al.
6774036 Integrated circuit trenched features and method of producing same 2004-08-10 Goldstein
6773828 Surface preparation to eliminate whisker growth caused by plating process interruptions 2004-08-10 Ooi et al.
6773827 Electronic component, method for producing electronic component, and circuit board 2004-08-10 Higuchi
20040147618 Colloid solution of metal nanoparticles, metal-polymer nanocomposites and methods for preparation thereof July, 2004 Lee et al.
20040147113 Method for manufacturing conductive layer and semiconductor device July, 2004 Yamazaki et al.
20040134379 Tailored ink for piston driven electrostatic liquid drop modulator July, 2004 Wong et al.
20040132299 Method for depositing lead-free tin alloy July, 2004 Matsuda et al.
20040131934 Mesoporous network electrode for electrochemical cell July, 2004 Sugnaux et al.
20040118696 Tin plating method June, 2004 Zhang et al.
6720499 Tin whisker-free printed circuit board 2004-04-13 Bokisa et al.
20040026684 Nanowire heterostructures for encoding information February, 2004 Empedocies
20040026256 Method and apparatus for protecting tooling in a lead-free bath February, 2004 Lindgren
6682584 Process for manufacture of reacted metal nanoparticles 2004-01-27 Pozarnsky et al.
6679937 Copper powders methods for producing powders and devices fabricated from same 2004-01-20 Kodas et al.
6664492 Method of eliminating electrically-conductive particles from an airstream 2003-12-16 Babb et al.
20030226758 Tin plating method December, 2003 Egli
6651521 Method for sampling and testing data centers for metallic particulates 2003-11-25 Carbone et al.
6646330 Lead frame for semiconductor device, process for producing the same and semiconductor device using the same 2003-11-11 Kubara et al.
20030213614 Conductive layer pattern and method for forming the same, wiring board, electronic device, electronic appliances and noncontact card medium November, 2003 Furusawa
6638847 Method of forming lead-free bump interconnections 2003-10-28 Cheung et al.
20030168639 Metallic nanoparticle cluster ink and method for forming metal pattern using the same September, 2003 Cheon et al.
6603205 MATERIAL FOR ELECTRONIC COMPONENTS, METHOD OF CONNECTING MATERIAL FOR ELECTRONIC COMPONENTS, BALL GRID ARRAY TYPE ELECTRONIC COMPONENTS AND METHOD OF CONNECTING BALL GRID ARRAY TYPE ELECTRONIC COMPONENTS 2003-08-05 Miura
20030151030 Enhanced conductivity nanocomposites and method of use thereof August, 2003 Gurin
6583500 Thin tin preplated semiconductor leadframes 2003-06-24 Abbott et al.
6554914 Passivation of copper in dual damascene metalization 2003-04-29 Rozbicki et al.
20030025182 Metal article coated with tin or tin alloy under tensile stress to inhibit whisker growth February, 2003 Abys et al.
20020192492 Metal article coated with near-surface doped tin or tin alloy December, 2002 Abys
20020187364 Tin plating December, 2002 Heber et al.
20020185716 Metal article coated with multilayer finish inhibiting whisker growth December, 2002 Abys et al.
6472459 Fabrication of metallic microstructures by micromolding nanoparticles 2002-10-29 Morales et al.
20020158342 Nanofabrication October, 2002 Tuominen et al.
20020148386 Ink compositions involving near-infrared absorber dyes and use in ink jet printing devices October, 2002 Woosman et al.
6433409 Semiconductor device, lead-patterning substrate, and electronics device, and method for fabricating same 2002-08-13 Mita et al.
6426548 Semiconductor device, lead-patterning substrate, and electronics device, and method for fabricating same 2002-07-30 Mita et al.
6361823 Process for whisker-free aqueous electroless tin plating 2002-03-26 Bokisa et al.
6306947 Printing ink and paint composed of an aqueous emulsion of self-emulsifiable urethane copolymer 2001-10-23 Morishima et al.
6297142 Method for bonding a semiconductor chip to a lead-patterning substrate using a gold/tin alloy 2001-10-02 Mita et al.
6248455 Alloy-plated sheet steel cured with a thin layer of insulating polymer material forming an electrically nonconductive breachable metal substrate 2001-06-19 Adams et al.
6238847 Laser marking method and apparatus 2001-05-29 Axtell et al.
6200732 Photocurable resin composition 2001-03-13 Tamura et al.
6165386 Photosetting conductive paste 2000-12-26 Endo et al.
6147400 Connecting multiple microelectronic elements with lead deformation 2000-11-14 Faraci et al.
6139777 Conductive paste for filling via-hole, double-sided and multilayer printed circuit boards using the same, and method for producing the same 2000-10-31 Omoya et al.
6099713 Tin-silver alloy electroplating bath and tin-silver alloy electroplating process 2000-08-08 Yanada et al.
6093503 Non-aqueous electrolyte lithium secondary cell 2000-07-25 Isoyama et al.
6010771 Electrical circuit component formed of a conductive liquid printed directly onto a substrate 2000-01-04 Isen et al.
5889083 Aqueous jet ink compositions 1999-03-30 Zhu et al.
5879568 Process for producing multilayer printed circuit board for wire bonding 1999-03-09 Urasaki et al.
5861076 Method for making multi-layer circuit boards 1999-01-19 Adlam
5807519 Plastic molds and methods of producing same 1998-09-15 Suzuki et al.
5798286 Connecting multiple microelectronic elements with lead deformation 1998-08-25 Faraci et al.
5750017 Tin electroplating process 1998-05-12 Zhang
5730851 Method of making electronic housings more reliable by preventing formation of metallic whiskers on the sheets used to fabricate them 1998-03-24 Arrowsmith et al.
5724727 Method of forming electronic component 1998-03-10 Chopra et al.
5698087 Plating bath and method for electroplating tin and/or lead 1997-12-16 Bokisa
5492595 Method for treating an oxidized copper film 1996-02-20 Carano et al.
5439639 Tin-silver-bismuth solders for electronics assembly 1995-08-08 Vianco et al.
5393573 Method of inhibiting tin whisker growth 1995-02-28 MacKay
5384204 Tape automated bonding in semiconductor technique 1995-01-24 Yumoto et al.
5322823 Ceramic composites and process for its production 1994-06-21 Ueda et al.
5320737 Treatment to reduce solder plating whisker formation 1994-06-14 Chao et al.
5277756 Post fabrication processing of semiconductor chips 1994-01-11 Dion
5260849 Electrostatic attracting sheet 1993-11-09 Kasahara
5234513 Fe-Ni alloy sheet excellent in hot workability, adhesivity to plating layer and solderability, and method for manufacturing same 1993-08-10 Inoue et al.
5202179 Electrostatic attracting sheet 1993-04-13 Kasahara
5160422 Bath for immersion plating tin-lead alloys 1992-11-03 Nishimura et al.
5130275 Post fabrication processing of semiconductor chips 1992-07-14 Dion
5049718 Method of laser bonding for gold, gold coated and gold alloy coated electrical members 1991-09-17 Spletter et al.
5039576 Electrodeposited eutectic tin-bismuth alloy on a conductive substrate 1991-08-13 Wilson
5008997 Gold/tin eutectic bonding for tape automated bonding process 1991-04-23 Phy
4997722 Composition and method for improving adherence of copper foil to resinous substrates 1991-03-05 Adler
4997516 Method for improving adherence of copper foil to resinous substrates 1991-03-05 Adler
4959278 Tin whisker-free tin or tin alloy plated article and coating technique thereof 1990-09-25 Shimauchi et al.
4935312 Film carrier having tin and indium plated layers 1990-06-19 Nakayama et al.
4922322 Bump structure for reflow bonding of IC devices 1990-05-01 Mathew
4756791 Chemical vapor deposition process for producing metal carbide or nitride whiskers 1988-07-12 D'Angelo et al.
4749626 Whisker resistant tin coatings and baths and methods for making such coatings 1988-06-07 Kadija et al.
4681670 Bath and process for plating tin-lead alloys 1987-07-21 Nobel et al.
4640746 Bath and process for plating tin/lead alloys on composite substrates 1987-02-03 Nobel et al.
4591951 Mounting arrangement for electronic components 1986-05-27 Iwamoto et al.
4331518 Bismuth composition, method of electroplating a tin-bismuth alloy and electroplating bath therefor 1982-05-25 Wilson
4234631 Method for immersion deposition of tin and tin-lead alloys 1980-11-18 Davis
RE30434 Electroless tin and tin-lead alloy plating baths 1980-11-11 Davis
4194913 Electroless tin and tin-lead alloy plating baths 1980-03-25 Davis
4151008 Method involving pulsed light processing of semiconductor devices 1979-04-24 Kirkpatrick
4093466 Electroless tin and tin-lead alloy plating baths 1978-06-06 Davis
3950605 Metal foil-plastic laminate and method of preparing the same 1976-04-13 Hori et al.
3796598 METHOD FOR GROWING LEAD CONDUCTORS ON PLANAR TRANSISTORS 1974-03-12 Gejyo et al.
3580731 METHOD OF TREATING THE SURFACE OF A FILAMENT 1971-05-25 Milewski et al.
3239597 Self-repair circuit apparatus 1966-03-08 Flynn
CN1509206 June, 2004 Colloid solution of metal nanoparticles, metal-polymer nanocompositions and method for preparation thereof
CN1803940 July, 2006 Method for preparing silicon-titanium micro-coarse structured hydrophilic film
CN101065203 October, 2007 Method for producing surface-treated silver-containing powder and silver paste using surface-treated silver-containing powder
CN101116149 January, 2008 Ink jet printable compositions
EP1626106 February, 2006 Method of forming a conductive wiring pattern by laser irradiation
EP1758166 February, 2007 Interposer and method for producing the same and electronic device
EP2045028 April, 2009 Metal nanoparticles, method for producing the same, aqueous dispersion, method for manufacturing printed wiring or electrode, and printed wiring board or device
EP2150417 February, 2010 METALLIC INK
JP62124084 June, 1987
JP10308119 November, 1998
JP11319538 November, 1999
JP2001325831 November, 2001 METAL COLLOID SOLUTION, CONDUCTIVE INK, CONDUCTIVE COATING AND CONDUCTIVE COATING FORMING BASE FILM
JP2003292836 October, 2003
JP2003106573 December, 2003 ELECTRICAL EQUIPMENT CONTAINING BOX FOR OUTDOOR UNIT OF SEPARATE TYPE AIR CONDITIONER
JP2004005413 January, 2004 USER SUPPORT SERVER, CONSTITUTION RECOGNITION SYSTEM, USER SUPPORT SYSTEM, CONSTITUTION RECOGNIZING METHOD, AND USER-SUPPORT METHOD
JP2004127676 April, 2004 INK FOR WIRING PATTERN, FORMING METHOD OF WIRING PATTERN, CONDUCTIVE FILM WIRING, ELECTROOPTICAL DEVICE, AS WELL AS ELECTRONIC EQUIPMENT
JP2004273592 September, 2004 SEMICONDUCTOR DEVICE AND ITS FABRICATING PROCESS
JP2005307335 November, 2005 COPPER FINE PARTICLE, PRODUCTION METHOD THEREFOR AND COPPER FINE PARTICLE-DISPERSED LIQUID
JP2006026602 February, 2006 METHOD FOR FORMING THIN FILM CONDUCTOR LAYER OF METALLIC PARTICULATE SINTERED COMPACT TYPE, AND METHODS FOR FORMING METALLIC WIRING AND METALLIC THIN FILM BY APPLYING THE METHOD
JP2006169592 June, 2006 METAL FINE PARTICLE-DISPERSED LIQUID, WIRING USING THE SAME AND METHOD FOR FORMING THE SAME
JP2006186330 July, 2006 METHODS OF MANUFACTURING INSULATING FILM AND SEMICONDUCTOR DEVICE
JP2006229212 August, 2006 SEMICONDUCTOR DEVICE AND ITS MANUFACTURING METHOD
JP2006321948 November, 2006 METAL PARTICULATE DISPERSION AND METHOD FOR FORMING METAL FILM BY USING THE SAME
JP2007042725 February, 2007 METAL PATTERN FORMING METHOD
JP2007321215 December, 2007 銅ナノ粒子分散体および銅被膜
JP2007327058 December, 2007 ELECTRICALLY CONDUCTIVE POLYMER COMPOSITION AND ELECTRONIC DEVICE PRODUCED BY USING THE SAME
JP2007332347 December, 2007 ELECTROCONDUCTIVE INK COMPOSITION FOR INKJET
JP2008006513 January, 2008 METHOD FOR MANUFACTURING NANOSIZE WIRE AND NANOSIZE WIRE
JP2009097082 May, 2009 METAL NANOPARTICLES, MANUFACTURING METHOD OF THE SAME, WATER DISPERSION MATERIAL, MANUFACTURING METHOD OF PRINTED WIRING-ELECTRODE, AND PRINTED-CIRCUIT BOARD-DEVICE
WO/1997/008924 March, 1997 LASER WRITE PROCESS FOR MAKING A CONDUCTIVE METAL CIRCUIT
WO/2006/072959 July, 2006 AQUEOUS-BASED DISPERSIONS OF METAL NANOPARTICLES
WO/2006/076603 July, 2006 PRINTABLE ELECTRICAL CONDUCTORS
WO/2007/004033 January, 2007 AN ELECTRICALLY CONDUCTIVE COMPOSITE
WO/2007/013393 February, 2007 COPPER FINE PARTICLE DISPERSION LIQUID AND METHOD FOR PRODUCING SAME
WO/2008/144504 November, 2008 METALLIC INK
WO/2009/111393 September, 2009 ADDITIVES AND MODIFIERS FOR SOLVENT- AND WATER-BASED METALLIC CONDUCTIVE INKS
WO/2009/108304 September, 2011 METHODS AND COMPOSITIONS FOR INK JET DEPOSITION OF CONDUCTIVE FEATURES
Jung et al; “Air-stable silver-coated copper particles of sub-micrometer size”; Journal of Colloid and Interface Science 364 (2011); Aug. 23, 2011; pp. 574-581; Elsevier, Inc.; The Netherlands.
RU/ISA; International Search Report and Written Opinion for PCT/US2013/049635 issued Oct. 31, 2013; Moscow, RU.
International Bureau of WIPO, International Preliminary Report on Patentability, International Application No. PCT/US2013/049635, Jan. 22, 2015.
Japanese Patent Office, Final Office Action, Notice of Reasons for Rejection, Japanese Patent Application No. 2012-503530, dated Jan. 13, 2015.
Boettinger et al., “Whisker and Hillock Formation on Sn, Sn-Cu and Sn-Pb Electrodeposits,” Acta Materialia, 53, Sep. 8, 2005, pp. 5033-5050.
Champion et al., “Sintering of copper nanopowders under hydrogen: an in situ X-ray diffraction analysis,” Materials Science and Engineering A, vol. 360, No. 1-2, Nov. 1, 2003, pp. 258-263.
Curtis et al., “Spray and Inkjet Printing of Hybrid Nanoparticle-Metal-Organic Inks for Ag and Chu Metallizations,” Materials Research Society Magazine, 2001, vol. 676, 6 pages.
European Patent Office, European Search Report for International Application No. 10756901.4, dated Oct. 10, 2014.
European Patent Office, European Search Report, Application No. 09747709.5, dated Mar. 12, 2014.
European Patent Office, European Search Report, Application No. 10759242.0, dated Sep. 3, 2014.
European Patent Office, Examination Report, Application No. 08 755 692.4, Apr. 13, 2012.
European Patent Office, Examination Report, Application No. 09774505.3, dated Sep. 26, 2012.
European Patent Office, Examination Report, Application No. 09774505.3, dated Oct. 22, 2014.
European Patent Office, Supplemental European Search Report for Application No. EP 09774505, Jun. 29, 2011.
European Patent Office, Supplementary European Search Report for Application No. EP08755692, Aug. 6, 2010.
Galyon, “Annotated Tin Whisker Bibliography and Anthology,” IEEE Transactions on Electronics Packaging Manufacturing, vol. 28, No. 1, Jan. 2005, pp. 94-122.
International Bureau of WIPO, International Preliminary Report on Patentability for PCT/US2010/042169, Jan. 17, 2012.
International Bureau of WIPO; International Preliminary Report on Patentability, International Application No. PCT/US2009/044196, Nov. 25, 2010, 6 pages.
International Bureau of WIPO; International Preliminary Report on Patentability, International Application No. PCT/US2009/044195, Nov. 25, 2010, 5 pages.
International Bureau of WIPO; International Preliminary Report on Patentability, International Application No. PCT/US2008/063890, Dec. 3, 2009.
International Searching Authority, International Search Report and the Written Opinion, PCT/US08/63890, Aug. 6, 2008, 9 pages.
International Searching Authority, International Search Report and Written Opinion for Application No. PCT/US/09/35717, May 5, 2009, 7 pages.
International Searching Authority, International Search Report and Written Opinion for International Application No. PCT/US09/44196, Jun. 30, 2009, 8 pages.
International Searching Authority, International Search Report and Written Opinion for International Application No. PCT/US09/44195, Jun. 25, 2009, 7 pages.
International Searching Authority, International Search Report and Written Opinion for International Application No. PCT/US09/49510, Oct. 19, 2009.
International Searching Authority, International Search Report and Written Opinion of the International Searching Authority for PCT/US10/28799, May 19, 2010.
International Searching Authority, International Search Report and the Written Opinion for International Application No. PCT/US10/28811, May 18, 2010.
International Searching Authority, International Search Report and the Written Opinion for PCT/US10/042169, mailed on Sep. 7, 2010, 4 pages.
Japanese Patent Office, Decision on Rejection, Japanese Patent Application No. 2011-509765, Sep. 29, 2014.
Japanese Patent Office, Office Action, Notice of Reasons for Rejection, Application No. 2010-549783, Dec. 18, 2012.
Japanese Patent Office, Final Office Action, Notice of Reasons for Rejection, Japanese Patent Application No. 2010-549783, dated Oct. 15, 2013.
Japanese Patent Office, Final Office Action, Notice of Reasons for Rejection, Japanese Patent Application No. 2010-549783, dated Oct. 14, 2014.
Japanese Patent Office, Final Office Action, Notice of Reasons for Rejection, Japanese Patent Application No. 2012-502281, dated Aug. 11, 2014.
Japanese Patent Office, Non-Final Office Action, Japanese Patent Application No. 2011-509765, Jul. 23, 2013.
Japanese Patent Office, Non-Final Office Action, Notice of Reasons for Rejection, Japanese Patent Application No. 2011-516873, dated Oct. 22, 2013, English Translation.
Japanese Patent Office, Non-Final Office Action, Notice of Reasons for Rejection, Japanese Patent Application No. 2012-503530, dated Jan. 21, 2014.
Japanese Patent Office, Non-Final Office Action, Notice of Reasons for Rejection, Japanese Patent Application No. 2011-516873, dated Mar. 24, 2014.
Kim et al., “Cyclic Properties of Si-Cu/Carbon Nanocomposite Anodes for Li-Ion Secondary Batteries”, Journal of the Electrochemical Society, vol. 152, No. 3, pp. A-523-A-526, Jan. 24, 2005, retrieved from internet Aug. 26, 2010.
Kogelschatz, “Excimer Lamps: History, Discharge Physics, and Industrial Applications”, Proc. SPIE, vol. 5483, 2004, pp. 272-286.
Korean Intellectual Property Office, Chemistry & Biotechnology Examination Bureau, Notice to File a Response, Patent Application No. 10-2010-7022240, May 8, 2012, KR.
Lal et al., “Role of Intrinsic Stresses in the Phenomena of Tin Whiskers in Electrical Connectors,” IEEE Transactions on Electronics Packing Manufacturing, vol. 28, No. 1, Jan. 2005, pp. 63-74.
Lee et al., “Spontaneous Growth Mechanism of Tin Whiskers,” Acta mater. vol. 46, No. 10, pp. 3701-3714, 1998.
Lu et al., “Ultrahigh Strength and High Electrical Conductivity in Copper,” Science Magazine, Apr. 2004, vol. 304, 6 pages.
Mitooka et al., “Effect of Laser Irradiation on Generation and Growth of Whiskers in Tin-Electroplated Film,” J. Japan Inst. Metals, vol. 73, No. 3, (2009), pp. 226-233.
MSDS: Fluorad by 3M, Fluorosurfactant FC-4430, Mar. 2, 2002; www.3m.com/paintsandcoatings, 4 pages.
Niizeki et al., “Laser Sintering of Ag Nanopaste Film and Its Application to Bond-Pad Formation,” 2008 Electronic Components and Technology Conference, May 27-30, 2008, IEEE, pp. 1745-1750.
Non-Final Office Action, Notice of Reasons for Rejection, Japanese Patent Application No. 2012-502281, mailed Jul. 16, 2013.
Osenbach et al., “Sn Corrosion and Its Influence on Whisker Growth,” IEEE Transactions on Electronic Packaging Manufacturing, vol. 30, No. 1, Jan. 2007, pp. 23-35.
Osenbach et al., “Sn Whiskers: Material, Design, Processing, and Post-Plate Reflow Effects and Development of an Overall Phenomenological Theory,” IEEE Transactions on Electronics Packaging Manufacturing, vol. 28, No. 1, Jan. 2005, pp. 36-62.
Osterman, “Mitigation Strategies for Tin Whiskers,” Release 1.0, Aug. 28, 2002, 11 pages.
Schroder et al., “Broadcast Photonic Curing of Metallic Nanoparticle Films,” Nanotechnologies, Inc. publication, 2006 NSTI Nanotechnology Conference and Trade Show, May 7-11, 2006, 4 pages.
Schroeder et al., “Tin Whisker Test Method Development,” IEEE Transactions Electronics Packaging Manufacturing, vol. 29, No. 4, Oct. 2006, pp. 231-238.
Shacham-Diamand, “Electroless Copper Deposition Using Glyoxylic Acid as Reducing Agent for Ultralarge Scale Integration Metallization,” manuscript published by Electrochemical and Solid-State Letters, Apr. 2000, pp. 279-282, 4 pages.
Shah et al., “Trimming and Printing of Embedded Resistors Using Demand-Mode Ink-Jet Technology and Conductive Polymer,” IPC Printed Circuit Expo Mar. 24-28, 2002, pp. 1-5.
Taiwan International Patent & Law Office, Translation of Notice of Office Action and Search Report, Taiwan Invention Patent Application No. 099109236, dated Oct. 23, 2014.
Taiwan International Patent & Law Office, Translation of Notice of Office Action and Search Report, Taiwan Invention Patent Application No. 098116219, dated Oct. 15, 2014.
The State Intellectual Property Office of the People's Republic of China, Notice of the First Office Action, Application No. 200880021733.6, Jun. 22, 2011.
The State Intellectual Property Office of the People's Republic of China, Notice on the First Office Action; Patent Application No. 200980108344.1, Jan. 21, 2012.
The State Intellectual Property Office of the People's Republic of China, Notice on Grant of Patent Right for Invention, Application No. 200880021733.6, Apr. 20, 2012.
The State Intellectual Property Office of the People's Republic of China, Notice on the First Office Action, Application No. 200980125925.6, Mar. 31, 2012, 8 pages, CN.
The State Intellectual Property Office of the People's Republic of China, Notice on the First Office Action, Application No. 200980118341.6, Feb. 17, 2013.
The State Intellectual Property Office of the People's Republic of China, Notice on the Second Office Action and Search Report, Patent Application No. 200980108344.1, Dec. 5, 2012.
The State Intellectual Property Office of the People's Republic of China, Notice on the Second Office Action, Application No. 200980125925.6, Feb. 25, 2013, 11 pages, CN.
The State Intellectual Property Office of the People's Republic of China, Notice on the First Office Action, Application No. 201080023851.8, Jul. 15, 2013, 8 pages, CN.
The State Intellectual Property Office of the People's Republic of China, Notice on the First Office Action, Application No. 201080032626.0, Jun. 28, 2013, 7 pages, CN.
The State Intellectual Property Office of the People's Republic of China, Notice on the Third Office Action, Application No. 200980125925.6, Nov. 5, 2013, 1 page.
The State Intellectual Property Office of the People's Republic of China, Notice on the Third Office Action; Patent Application No. 200980108344.1, Feb. 27, 2014, English Translation.
The State Intellectual Property Office of the People's Republic of China, Translated text of Notice on the Second Office Action; Patent Application No. 201080015842.4, Mar. 10, 2014.
The State Intellectual Property Office of the People's Republic of China, Notice on the Second Office Action; Patent Application No. 201080023851.8, Apr. 8, 2014.
The State Intellectual Property Office of the People's Republic of China, Notice on the Second Office Action; Patent Application No. 201080032626.0, Apr. 16, 2014.
The State Intellectual Property Office of the People's Republic of China, Text of the Third Office Action; Patent Application No. 201080015842.4, Sep. 5, 2014.
The State Intellectual Property Office of the People's Republic of China, Notice on the Fourth Office Action; Patent Application No. 200980108344.1, Jul. 25, 2014, English Translation.
The State Intellectual Property Office of the People's Republic of China, Fourth Office Action; Patent Application No. 200980108344.1, Dec. 29, 2014, Chinese.
Translated Text of the First Office Action for Application No. 201080015842.4, May 6, 2013, 6 pages, CN.
Translation of Office Action and Taiwan IPO Search Report, Taiwan Invention Patent Application No. 0977118130, May 31, 2013.
United States Patent & Trademark Office, Final Office Action, U.S. Appl. No. 12/121,260, Jan. 12, 2015.
United States Patent & Trademark Office, Final Office Action Summary, U.S. Appl. No. 12/391,817, dated Aug. 27, 2012.
United States Patent & Trademark Office, Non-Final Office Action Summary, U.S. Appl. No. 12/496,453, dated Jun. 13, 2012.
United States Patent & Trademark Office, Non-Final Office Action Summary, U.S. Appl. No. 14/073,986, dated Dec. 1, 2014.
United States Patent & Trademark Office, Non-Final Office Action, U.S. Appl. No. 12/466,306, dated Nov. 7, 2012.
United States Patent & Trademark Office, Non-Final Office Action, U.S. Appl. No. 13/260,893, Mar. 11, 2013.
Volkman et al., “Ink-jetted Silver/Copper Conductors for printed RFID Applications,” Materials Research Society Magazine, 2004, vol. 814, 6 pages.
Wu et al., “One-Step Green Route to Narrowly Dispersed Copper Nanocrystals,” Journal of Nanoparticle Research, 2006, pp. 965-969, 5 pages.
Yaniv, “Novel Inkettable Copper Ink Utilizing Processing Temperatures Under 100 Degrees C Without the Need of Inert Atmosphere”, Presentation at Printed Electronics Europe Conference, pp. 1-25, Apr. 7-8, 2009, retrieved from internet Aug. 26, 2010.
Yeshchenko et al., “Size-Dependent Melting of Spherical Copper Nanoparticles,” article published by National Taras Shevchenko Kyiv University, Jan. 2007, 16 pages.
This application claims priority to U.S. Provisional Patent Application Ser. No. 61/669,431, which is hereby incorporated by reference herein.
1. A method for making a conductive film comprising: depositing an ink or paste composition comprising micron-sized metal particles onto a polymeric substrate having a melting point less than 200° C., wherein the micron-sized metal particles in the ink or paste composition have an average particle size greater than one micron; and photosintering the ink or paste composition after being deposited onto the substrate, wherein during the photosintering of the ink or paste composition, some heat generated in the micron-sized metal particles as a result of the photosintering is transferred from the particles into the substrate to reduce ramping up of the heat within the particles, which also results in a partial melting of a surface of the substrate so that some of the particles physically embed into the substrate surface.
2. The method as recited in claim 1, wherein the polymeric substrate has a thermal conductivity greater than 0.1 W/mK.
3. The method as recited in claim 1, wherein the average particle size of the micron-sized metal particles in the ink or paste composition is less than three microns.
4. The method as recited in claim 1, wherein the photosintering is performed with a broad spectrum light source.
5. The method as recited in claim 1, wherein the melting point is less than 150° C.
6. The method as recited in claim 1, wherein the metal particles comprise copper.
7. The method as recited in claim 6, wherein the ink or paste composition has a formulation comprising about 50 wt. % concentration of the micron-sized copper particles, about 48 wt. % concentration of a binder solution, and about 2 wt. % concentration of a dispersant.
8. The method as recited in claim 1, wherein the metal particles are selected from the group consisting of Ag, Ni, Al, and Fe.
9. The method as recited in claim 1, wherein the polymeric substrate is comprised of PET.
10. The method as recited in claim 1, wherein the photosintered metal particles are connected to each other with necks.
11. The method as recited in claim 1, wherein the polymeric substrate has a coefficient of thermal expansion greater than two times the coefficient of thermal expansion of the photosintered ink or paste composition.
12. The method as recited in claim 1, wherein the photosintered ink or paste composition has a resulting resistivity less than 10−4 ohm-cm.
13. The method as recited in claim 1, wherein the micron-sized metal particles in the ink or paste composition have an average particle size greater than two microns.
14. The method as recited in claim 1, wherein the photosintered ink or paste composition has a resulting resistivity of at least about 6×10−5 ohm-cm.
15. The method as recited in claim 1, wherein the polymeric substrate is selected from the group consisting of polyvinyl chloride, polycarbonate, polystyrene, polyethylene, and polypropylene.
16. A method for making a conductive film, comprising: depositing an ink or paste composition comprising micron-sized metal particles onto a polymeric substrate having a melting point less than 200° C. and a thermal conductivity greater than 0.1 W/mK, wherein the micron-sized metal particles in the ink or paste composition have an average particle size greater than two microns; and photosintering the ink or paste composition after being deposited onto the substrate, wherein during the photosintering of the ink or paste composition, some heat generated in the micron-sized metal particles as a result of the photosintering is transferred from the micron-sized metal particles into the polymeric substrate to reduce ramping up of the heat within the micron-sized metal particles, which also results in a partial melting of a surface of the polymeric substrate so that some of the micron-sized metal particles physically embed into the polymeric substrate surface.
17. The method as recited in claim 16, wherein the melting point of the polymeric substrate is less than 150° C.
The present disclosure is directed towards metallic ink such as copper. Metallic conductors on printed circuit boards (“PCBs”) and flex tape connectors are generally copper (“Cu”) lines that are laminated to PCBs or polymeric substrates. These conductors are typically deposited by laminating copper films and etching the desired pattern. Patterning requires photolithography and acidic solutions that incur high costs and create environmental waste. An alternative technique to lamination and etching includes printing the metal lines. Described herein are materials and methods for providing cost effective micron-sized copper particle based inks, the printing and sintering of those inks to form electronic conduction layers on low temperature polymeric substrates.
Additive manufacturing is becoming a more accepted method to produce goods due to reduced stream of waste and increased material utilization efficiency. Electronic circuits are particularly able to realize the benefits of additive manufacturing using a direct printing method. Direct printing, of electronic circuits requires specialty inks made from metallic particles that can be easily applied with various printing methods. All printed metallic inks based on metal particles must be sintered to transition from individual particles in the stabilized ink formulation to a conductive film material suitable fir use in the end product.
Nanoparticle inks are utilized for the printed electronics industry. However, nanoparticles are expensive compared to larger, submicron and micron-sized particles. The use of these size particles is limited in applications such as electronic interconnects, membrane switch conduction layers, radio-frequency ID tags, displays and other applications due to the lack of suitable processing, procedures to convert the particles to a conductive film.
FIG. 1 illustrates formations of “necks” between particles in accordance with embodiments of the present invention.
FIG. 2 illustrates a reflectance spectrum of copper particle film before photosintering.
FIG. 3 illustrates an output spectrum from a Xe-arc discharge lamp used in a photosintering process.
FIG. 4 shows an optic microscope image of a photosintered copper film on PET.
FIG. 5 shows a digital photograph of photosintered copper film deposited on a PET substrate. The tape used for checking adhesion is shown on the right. Dashed rectangle indicates the area where the tape was applied.
FIGS. 6-7 show a SEM-FIB of photosintered copper film on a PET substrate, where FIG. 7 shows the image at a higher magnification.
FIG. 8 shows a SEM photograph of copper particles on an alumina substrate after sintering at 800° C. for 30 minutes under N2/H2 environment. Arrows show necks.
FIG. 9 illustrates a graph and table showing sheet resistance as a function of thermal sintering at different temperatures, with a comparison to photosintering.
FIGS. 10-11 show digital photographs of copper paste printed on a PCB substrate. Red square shows the tape used to check adhesion of the copper film.
FIG. 12 shows a digital photograph of copper paste printed on a PE substrate (e.g., a Ziploc® bag). The tape used to check adhesion is shown on the left.
An aspect of the present invention involves a method for making a conductive film comprising depositing an ink, or paste composition comprising micron-sized metal particles onto a polymeric substrate having, a melting point less than 200° C., wherein the micron-sized metal particles in the ink or paste composition have an average particle size greater than one micron, and photosintering the ink or paste composition after being deposited onto the substrate.
In another aspect of the present invention, the polymeric substrate may have a thermal conductivity greater than 0.1 W/mK. In another aspect of the present invention, the average particle size of the micron-sized metal particles in the ink or paste composition may be less than three microns. In another aspect of the present invention, the photosintering may be performed with a broad spectrum light source. In another aspect of the present invention, the melting point may be less than 150° C.
In another aspect of the present invention, the metal particles may copper. In another aspect of the present invention, the metal particles may be selected from the group consisting of Ag, Ni, Al, and Fe. In another aspect of the present invention, the polymeric substrate may be comprised of PET.
In another aspect of the present invention, the photosintered metal particles may be connected to each other with necks.
In another aspect of the present invention, the polymeric substrate may have a coefficient of thermal expansion greater than two times the coefficient of thermal expansion of the photosintered ink or paste composition. In another aspect of the present invention, the photosintering may cause some of the metal particles to become physically embedded into a surface of the polymeric substrate.
In another aspect of the present invention, the photosintered ink or paste composition may have a resulting resistivity less than 10−4 ohm-cm.
Additive electronics printing additionally enables high speed processes for application of the ink such as screen print, flexographic printing, gravure printing and inkjet printing. Each of these methods is compatible with roll to roll printing methods and polymeric substrates with low melting temperatures. Therefore, there is tremendous interest in developing capabilities to print conductors on various substrates using low temperature processes (e.g., <150° C.). Important applications for such processes include printing metallic conductors on substrates, such as paper, polyethylene terphthalate (“PET”), acrylonitrile butadiene styrene (“ABS”), polyimide, polycarbonate, polyacetates, polyvinyl chlorides, etc. Most of these types of substrates have a very low melting point that defines a maximum process temperature of 150° C. This limitation requires ink materials and methods to sinter them that do not exceed this maximum substrate temperature. There are different materials that allow for creation of metallic films from solution based processes. Below is a description of the different materials commonly used.
Metal Salts and Complexes:
This approach utilizes the ability of certain salts or oxides to decompose to form the base metal. The decomposition can be driven by thermally heating the material or using photo-processes. Examples for such materials are silver oxide, silver nitrate, formats and oxalates of nickel and copper, silver nitrate DMSO complex, etc. The nascent metals produced during decomposition of the parent compound is very reactive and tends to join to other newly formed metal clusters affording a continuous pattern. Commercial silver inks based on this phenomenon are available. These inks have difficulty in obtaining traces greater than one micron due to the dilute nature of the complex in the ink. The complex type ink may not be suitable for these pruned electronic applications due to the thickness limitations.
An interesting utilization of this phenomenon is presented in Japanese patent publication 4666663, which makes use of silver salt-coated micron-sized copper particles. When the silver salt-coated particles are heated, the silver salt yields silver metal, which assists the sintering of adjacent particles and even allows sintering of the copper cores. Silver metal-coated copper particles are well known in the art and are commercially available from numerous producers, such as Ferro. The patent above clearly does not employ this kind of system.
Using Alloys:
This approach utilizes the ability of different metals to form alloys with other metals. This process can involve reduction of melting point at the contact areas between the two or more metals. It also involves dissolution and mixing of the metals into one another. In this context, there is a place to mention U.S. Published Patent Application No. 2008/0160309, which describes ternary and quaternary alloys involving nickel, bismuth, tin, and silver. A binary system of silver-coated copper particles was tested and could be thermally sintered at 700° C. for 10 minutes under nitrogen (see. D. S. Jung et al., Journal of Colloid and Interface Science 364 (2011) 574-581, which is hereby incorporated by reference herein). Such conditions are not suitable for printing on plastic materials or paper.
Most currently employed ink and paste materials involve silver particles. These particles are relatively very expensive to produce or purchase due to the market price of the metal, such as in silver, and due to the fabrication processes required to synthesize the nano-sized particles. Generally, for a given metal, the smaller the particles, the more expensive they will be. Often this increased price prevents them from being widely used in mass manufacturing processes. Therefore, there is a genuine need to find cheaper replacements for the nano-sized silver and copper. To clarify the definition of “nano-sized,” the classical definition is used wherein dimensions less than 100 nanometers are considered nano-sized. It is also known that particles of a certain batch have certain distributions of particle diameters within the batch.
Copper is a metal of choice for making electrical conductors. It is second only to silver in conductivity, relatively inexpensive, and is chemically resistant thus allowing further treatments such as soldering other metals to it. The assignee has successfully demonstrated photosintering of nano-sized copper particles using a photosintering process. The rational in this system lies in the higher reactivity and lower melting points of nano-sized metals.
To make inks from copper requires small particles that are compatible with the type of printing. For example, inkjet printing may require smaller particle diameter such that the particles will not clog the nozzle that is typically a few microns in diameter. The particles are typically required to be 1/10th the size of the nozzle diameter to prevent clogging. Screen printed inks must have particles small enough to prevent clogging in the screen mesh.
Unfortunately, copper nanoparticles do not realize the ease of processing required for widespread usage in metallic ink materials. For example, comparative cost savings of nanoparticles to their bulk metal counterparts is not maintained. The current market for copper is approximately 200 times less expensive than silver. However, copper nanoparticles are usually almost as expensive to produce or purchase as silver nanoparticles. The manufacturing process to control the particle size is considerably more expensive than the raw material costs. Micron-sized particles can be milled down from bulk metals with a considerable reduction in cost due to the economy of scale from producing large quantities in a single process batch.
Copper nanoparticles tend to oxidize very quickly due to their high surface area. The oxide coating is an electrical insulator, making them difficult to convert into conductive films unless there is suitable protection from oxidation or a method to convert the oxide by chemical reduction back to copper.
A process to convert the individual nanoparticles in the ink to a conductive film requires sufficient energy to melt the nanoparticles. The amount of energy depends on the size of the metal particles. The process can result in necking between adjacent particles through full melting where there is a complete transformation to a bulk material with minimal voids and maximum density. The process parameters will change based on the melting point of the particles, the amount of energy put into the system to melt the particles and the dwell time of energy delivery that controls how much melting takes place.
Discussion on Particle Melting Points
Due to quantum confinement, the melting point of a small particle drops as a function of particle diameter. The smaller the particle, the lower the melting point compared to a bulk metal part. Nanoparticles of metal can have melting points hundreds of degrees lower than the bulk metal melting point. Lindemann's Criterion states that the melting point of a material is proportional to the cohesive energy of the particles. Each metal atom in a metallic particle has energetic interactions with its neighboring atoms. The atoms at the surface have fewer neighboring atoms and reduced cohesive energy compared to the energy of the atoms in the center. Because the energy of the particles depends on distance from the surface, very small particles with small diameters, nanoparticles in particular, can have reduced cohesive energy resulting in overall reduced melting points. The file size dependent melting point follows the Gibbs-Thomson Equation:
TM(d)=TMB(1−[4σsl/Hfρs d])
where TM(d) is the calculated melting point as a function of diameter, TMB is the bulk melting point of the parent metal, σsl is the interface energy of the solid to liquid interface, Hf is the bulk heat of fusion, ρs is tho density of the parent metal, and d is the particle diameter. The l/d dependence clearly shows that as the diameter is reduced, the melting point is reduced.
There are several mechanisms related to small particle melting. The liquid nucleation (“LSN”) model proposed by Sakai (H. Sakai, “Surface-induced melting of small particles,” Surf. Sci. 351: 285 (1996)) closely fits the experimental measurements. LSN predicts that the surface of a particle will melt initially and provide enough energy, and a liquid-solid interlace will propagate from the surface of the particle down through the center of the particle. LSN thus calculates the difference in energy potential between the energy potential of the liquid surface atoms and the solid core atoms. The equilibrium established between these two energy potentials is a function of the internal energy, the overall temperature, the system entropy and the specific number of particles at a given chemical potential, and is related to the first and second Thermodynamic Laws.
Discussion on Energy Delivery
The melting of particles is completed with energy delivery that has a finite time component. This provides a kinetic term to the thermodynamic discussion. The kinetics of the system describe how much energy stays in the nanoparticles and is a function of energy flux (delivery to the particles), energy interactions within the particles related to melting mechanisms, and energy dissipation to the substrate and surrounding atmosphere.
Thermal sintering is completed with ovens, infrared sources, heat lamps, or other heat delivery systems that transfer heat energy into a substrate and ink. The temperature is typically set to the minimum melting point required to convert the particles into a film. With thermal sintering of particles, the energy delivery is typically slow. High temperatures that exceed the melting temperature of the particles and long dwell times are required. The long dwell times can range from approximately one minute to greater than 60 minutes, and are required such that the substrate and particles are in temperature equilibrium and overcome the kinetics of the particles melting. The kinetics of melting are related specifically to the individual particles, solid-liquid transition and rearranging themselves to flow into their nearest neighbors to form a bulk conductor. Often, due to the energy levels being slightly above the melting point and through a distribution in particle size, the melt transitions suffer from low kinetics. Surface oxides on the articles will also change the surface energy of individual particles slowing down or preventing coalescence into neighboring particles.
Photosintering with light has different kinetics. The light source may be a broad spectrum source, such as a flash lamp (e.g., a xenon arc flash lamp), which may have an output ranging from the UV (˜250 nm) to the IR (˜800 nm) (see FIG. 3). Photosintering may be completed with a steady state or pulsed light delivery. A steady state light delivery may be rastered or scanned such that the dwell time in a particular location is short.
The photosintering process involves illuminating the particles with a flashlamp so that the particles absorb the energy and present reactivity based on two mechanisms. The first mechanism is creation of high temperatures in the particle fir very short times. The flash lamp can deliver large amounts of energy in short time periods (e.g., greater than 1800 Joules of energy can be delivered in as short as 0.2 milliseconds). The output spectrum of the lamp may have an overlap with the absorbance spectrum of the particles. The output intensity of the lamp may be controlled by the lamp voltage. The duration of the pulse delivery may be controlled through the lamp flash pulse width. Each of these parameters may be independently adjustable within the total power delivery specifications of the power supply connected to the lamp assembly. As the particles absorb the energy, they internally convert it to heat as a mechanism to dissipate the energy. If the energy delivery is large enough and fast enough, the particles convert the absorbed light to heat faster than they can dissipate the energy. In this case, the internal temperature of the particles is increased and the result can be melting. The second mechanism is unique to photosintering in that the surface oxide on the metallic particle can be reduced or even removed from the surface. This photoreduction step and subsequent removal of surface oxides, changes the surface tension of the metal particles, allowing the melted surfaces to flow into its nearest neighbors creating a connection between particles. If the energy delivery is large enough and fast enough, the particles will first neck together, followed by shape reorganization into a dense film.
In most cases, the substrate on which the particles have been deposited has minimal absorbance spectrum overlap. Having differential absorbance spectra of the particles and the substrates allows for selective heating of the different layers. This selective heating cannot be accomplished with thermal heating, methods. Using this mechanism, it is possible to photosinter particles with high melting points onto substrates with low melting points. Examples of substrates include paper, polyethylene terphthalate (“PET”), acrylonitrile butadiene styrene (“ABS”), polyimide, polycarbonate, polyacetates, polyvinyl chlorides, cyclo-olephins, and polyimide.
Discussion on Substrates
The choice of substrate can determine the quality of adhesion and conductivity of the metallic film that is created by conversion of the particles to the conductive metallic film. There are three key parameters that control the amount of energy dissipation during the process; the thermal conductivity, the melting point, and the coefficient of thermal expansion of the substrate. The CTE value, thermal conductivity, and melting points of copper and various polymeric materials are listed in Table 1.
CTE Conductivity Point
Material (μm/m K) (W/mK) (° C.)
Copper 18.7 (16.7 ppm/° C.) 385 1760
PET 59.4 0.15 115-170
Polyvinyl Chloride 50.4 0.12 50-75
Polycarbonate (PC) 70.2 0.19 115-130
Poly Styrene (PS) 70 0.10-0.13 50-95
Polyethylene (PE) 200 0.33 55-120
Polypropylene (PP) 100-200 0.17 90-120
Epoxy 49 0.2-5
Polyimide (30-100° C.) 17 0.10 425
ABS 80 0.17 70-100
Because of the differences in CTE, thermal conductivity, and melting point, there are many limitations to converting metallic particles into conducting films on many substrates. In fact, it is difficult to deposit copper on many low temperature substrates such as PET and PC, because the adhesion is often poor and the process has a very narrow window. Nanoparticle-based inks and particle interactions with the substrate during photosintering are typically dominated by CTE and surface tension during melting. These are approximations based on the resulting film of a high density bulk metal placed upon a comparatively low density substrate material. Larger particle (i.e., diameters from 100 nm up to 3 microns) interactions with the substrates during photosintering are typically dominated by melting point and thermal conductivity. Due to the metallic film morphology generated by the larger particles, the CTE mismatch between the metallic film and the substrate is less critical.
Thermal conductivity of the substrate dominates the energy transfer mechanisms during photosintering. The temporal temperature change of the particles creates a temperature gradient from the top of the metallic particle coating to the substrate. The face of the particle film facing the light source will have the highest temperature based on the greatest photon flux and light absorbance. The face of the particle fill that is furthest from the light source, which is also the interface between the particles and the substrate, will have the lowest temperature as the substrate's thermal conductivity wilt begin to remove the heat of the metallic film. Low thermal conductivity substrates such as polyimide absorb little heat from the metal particles as they undergo the photosintering process. Substrates such as polycarbonate (“PC”) or polyethylene terephthalate (“PET”) have higher thermal conductivity and can require additional energy to overcome the heat loss between the particles and the underlying substrate.
A challenge with photosintering is the time scale of energy delivery. Delivering 1500-1800 Joules of energy in millisecond time scales means the temperature ramp rates are exceedingly steep. Generally, this can be considered a violent process due to the rate of change of the energy in the metallic particles. If the energy delivery is too fast, the particles can ablate from the surface as they gain energy faster than they can dissipate through mechanisms related to phase transitions (solid to liquid and liquid to solid) and thermal transfer (convection, radiation, and conduction).
The melting point of the substrates can determine the applicability between thermal and photosintering. Higher process temperatures are required for some nanoparticle systems. For example an 80 nm copper nanoparticle film will have a thermal melting temperature of approximately 400° C. Partial melting of the film due to the smaller particles in the particle size distribution will begin to melt as low as 300° C. These temperatures allow polyimide to be chosen as a substrate for thermal sintering. However, many other polymeric substrates are not compatible with this melting point in that such polymeric substrates would melt before the particles.
Many of the polymeric substrates melt at temperatures below 120° C. PET is a common plastic used in the industry as it has a melting temperature higher than other materials with a working temperature up to 150° C. This allows it to be compatible with certain thermal sintering processes that involve nanoparticles smaller than 30 nm, preferably below 20 nm. Silver nanoparticles are commonly available in this size. Copper nanoparticles can be manufactured in this size and will have a similar low melting point. However, the copper nanoparticles are more difficult to keep from oxidizing at this size.
The coefficient of thermal expansion (“CTE”) value for metal and plastic based materials determines how much dimensional change occurs as a function of temperature. When multiple layers of different materials are stacked, it is important to consider matching the CTEs of the materials. Without CTE matching, one film may change dimensions at a faster rate than the other under temperature changes, which can cause delamination and problems with adhesion. Placing a metal film onto a plastic substrate demonstrates many problems with adhesion due to mismatches in cm. The loss of adhesion comes from lateral stresses in the film. For example, if copper (CTE=18.7) is deposited onto as PET substrate (CTE=59.4), the PET substrate will enlarge at a dimension greater than three times that of the copper. This differential in dimensions creates lateral stresses in the PET substrate. The metallic film forms a material continuum. The PET substrate will begin to buckle as the internal forces on the metallic film are stronger than the interfacial forces between the copper and polymer. In this example, the buckling creates a force normal to the surface. With sufficient temperature, the forces can be great enough to cause film delamination.
The same mismatch of CTE also causes problems on cooling. For example, during thermal sintering, the particles are heated at the same time as the substrate. The particles are then converted to a melted metal film while the substrate is hot. When the substrate is cooled down, the metallic film solidifies before the plastic cools. As the plastic continues to cool, it shrinks at a greater rate than the metallic film, which also creates stress that can delaminate the film.
If the CTE of the metallic film can be matched to the substrate, the stress between the substrate and metallic film will be minimized. Alternatively, the stress can be relieved by increasing the degrees of freedom within the metallic film. While it is difficult to engineer stress reliefs into the metallic film, this can be done in situ with the sintering by controlling the porosity and defects in the metallic film. Defects and/or voids can be places for stress release in the metallic film. A highly porous film can have less stress then a highly dense film. The density can have a lower limits described by the closest packing of the individual particles and specifically as function of the particle diameter and have an upper limit of a pure bulk material. Typically, thermal sintering of particles will have an upper limit of around 5-10% porosity due to the long dwell time of the heat application. This acts as a continuous metallic film.
In contrast to a continuous metallic film, a highly porous metallic film can be made by connected or necked metallic particles. Particle necking occurs when the surface of a single particle melts but the melt transition does not propagate through to the core of the particle. The melt phase on the surface then flows to one or more neighboring particles such that interparticle connection is established. If the energy input delivery is maintained, the particles will continue to transition from surface melting to core melting and have flow into as continuous film. If the energy input delivery is removed, the particles can solidify with just a connecting neck between them. The interparticle necking is responsible fur film conductivity, and in some cases adhesion properties to different substrates. Such necking is further discussed in U.S. Pat. No. 8,422,197, which is hereby incorporated by reference herein.
There are a few mechanisms related to improving the energy input relationship with the adhesion. If the energy input overwhelms the mechanisms of energy dissipation, there can be ablation. There are two ways to change the kinetics of the energy dissipation: increase the mass of the particles to be convened to a film and/or slow down the energy input such that the dissipation can keep up.
Increasing the mass of the particles changes the kinetics related to the behavior of the particles in reactions and physical transformations. The volume of the particles and thus the density is a cubed power function related to particle diameter. Nanoparticles are well known for their small mass and high mass/volume ratios. This is an advantage fur photosintering as the small volume requires less energy to complete the solid to liquid (melt) phase transition. However, if larger particles are used, there is more mass per particle. The increased mass changes the latent heat of phase transition requirements meaning for the same heat capacity, as a function of mass, it takes more energy to complete the melt transition. If there is a finite energy delivery, as is the case with photosintering, the particles may or may not have enough energy to complete a full melt transition. One can tailor the energy delivery through the pulse width and lamp voltage such that control is possible between a surface melt and necking all the way through a Inn melt transition into a continuous metallic film. It is also possible to decrease the lamp voltage and increase the pulse width of the lamp flash. This lowers the intensity and increases the duration changing the effective energy delivery.
Increasing the mass of the particles is a direct result of larger diameter. When the diameter of the particles is increased, the optical spectrum shifts. Nanoparticles have large absorbance spectra extinction coefficients at nearly every wavelength in the spectrum. As a result, they often appear black in color when the size is below 200 nm. As the particle diameter is increased, the energy of the particle is decreased, and there is less absorbance in the lower wavelengths. For example, with respect to copper particles, at sires greater than 500 nm, the absorbance is reduced at typically greater than a wavelength 550 nm giving them a reddish copper color (see FIG. 2). During a photosintering process, less total light is absorbed by these larger particles due to the lack of overlap between the output spectra of the light source and the particles.
Increasing the mass can also change the particle inertia. Often the process of photosintering can ablate material from the surface. Nanoparticles are especially susceptible to material ablation as there is minimal mass to prevent the motion-based energy dissipation. In contrast, larger particles have greater mass and therefore are resistant to ablation.
There is a finite range of particle sizes where the particles are large enough to resist ablation yet small enough to show some melting during the photosintering process. The size range for copper particles required for formation of surface melting during photosintering and subsequent necking between adjacent particles is greater than 0.5 microns and larger than 3 microns. The smaller particles in this size range absorb considerably more energy and will completely melt. The larger particles outside this size range have too much mass and will not transition to a surface melt phase that creates necking (see FIG. 8). The particles within this range can exhibit a degree of surface melting such that a connection to a neighboring particle is established during photosintering. Controlling the distribution of particle size can tune the degree of necking thereby influencing the degrees of freedom of the metallic film and thus the adhesion to various substrates where CTE mismatch occurs. The degree of necking also controls the overall resistivity of the resulting metallic film. This partial transition can be seen with thermal sintering of copper particles in the size range required for necking to develop. There are multiple particles that are necked together when sintered thermally at 800° C. This experiment was completed on a high temperature silicon substrate as polymeric substrates would have melted. The photosintering process produced more necking and lower resistivity in a shorter time scale (see FIG. 9).
Necking of particles is advantageous for reducing interfilm stress. The stress relief allows for more energy to be transferred into the underlying substrate. In this case, when the thermal conductivity of the substrate is high, the particles can transfer more heat into the substrate controlling their temperature ramp rate. In some cases, when the thermal conductivity of the substrate is high, and the melting point of the substrate is low, larger particles can transfer enough heat to dissipate energy, create necking between adjacent particles, and partially melt the underlying substrate. This partial melting of the substrate allows for particle embedding such that adhesion is increased (see FIGS. 6-7). When the particles are at the large end of the size limit (i.e., diameter greater than 2 microns), the particles can have enough mass to sink into the partially melted polymeric substrate providing a strong anchoring point, resulting in excellent adhesion. This is evidenced by the excellent adhesion of micron-sized particles to most low temperature substrate materials listed in Table 1.
The inventors have previously developed copper ink formulations based on metallic nanoparticles. These metallic nanoparticles may be made from Ni, Al, Cu, Ag, Fe, or other similar metals or alloys of metals as described above.
Disclosed are novel techniques for forming conductive copper patterns using formulations containing micron-sized copper particles. These copper particles may be joined together by a photosintering method. Embodiments disclosed herein describe how micron-sized copper particles may be photosintered to yield films and patterns of copper on different substrates such as polyethylene terephthalate (“PET”), epoxy-glass fiber primed circuit board (“PCB”) substrates, and polyethylene (“PE”). The films show good adhesion and conductivity.
Embodiments of the present invention achieve successful photosintering, of micron-sized copper particles to obtain conductive patterns that adhere to PET substrates, as well as other substrates. Embodiments of the present invention further achieve addition of a polymeric binder (vehicle) to affect film properties (i.e., improve adhesion and prevent excessive photosintering, which may lead to blowing away of the copper film).
There are several factors that can change the resistivity of conducting films. The copper particles can vary in outer diameters and thicknesses of the surface oxides. The particles can also vary in the overall shapes of the particles. Particles can be spheroidal in overall shape, but not be considered spherical. Spherical particles are significantly round in shape having nearly identical dimensions in the X, Y, and Z axes. Spheroidal particles have a round profile when viewed from a distance, but have other increased order shapes when viewed in detail.
The shape of the particles dictates the amount of energy required to change this shape. For example, a perfectly spherical particle is very stable, and resides at a minimal energy point on its potential energy curve, it will require a significant amount of energy to move away from this stable shape and connect with a neighboring particle to form a conductive pathway. Particles that have an otherwise smooth surface but non-spherical (oblong, oval, egg shaped, etc.) have a higher potential energy due to an increased dimension in one or more of the ages. The higher potential energy of these particles increases the difficulty for each to form “necking” connections (joining of particles where each of the parent particles remain easily distinguishable from one another) with its neighboring particle. If a non-spherical particle had rough edges, such as sharp corners, bumps, or other protrusions, the particle would have higher potential energy than the standard non-spheroidal particles, and significantly higher than the spherical particles.
The shapes of the particles can also shift the optical absorbance spectrum of the particles. The optical absorbance spectrum is important when considering utilizing a photosintering process. The light output wavelength of the light source should overlap with an optical absorbance of the particles. The greater the total energy of overlap, the greater the amount of energy the particles absorb. The energy of absorbance contributes to photochemical reactions (e.g., photoreduction of metal oxides in the particles) and the total heat conversion of light within the particles.
Consistent with the photosintering process, the surface of the particle melts but the bulk of the particle does not. When the surface of the particle melts and this melted surface is sufficiently near a neighboring particle that also has surface melting, the two melted surfaces flow together. When this occurs, a “neck” forms between the neighboring particles. However, even though these particles are now connected, they still retain their individual shape and can be clearly identified as connected, yet individual particles (see FIG. 1).
FIG. 2 shows a reflectance spectrum of a copper particle film. The strong reflectance above 600 nm is representative of the reddish-brown color of the copper film. There is low reflectivity below 600 nm. This represents where the copper particle film absorbs light.
The output spectra of a Xe-arc discharge lamp is shown in FIG. 3. This lamp is a type used in embodiments of the photosintering process described as used herein. Notice the significant light energy output from 300 nm to 700 nm with a peak output of 450 nm. The lamp has significant output energy that overlaps with the absorbance spectrum of the copper particle film. In fact, the majority of the output energy is between 350 nm and 550 nm. The absorbance overlap is also at the higher energy side of the visible spectrum. This higher energy is required for the larger micron-sized particles.
Embodiments of the present invention use micron-sized copper particles to successfully achieve stable, conductive films and patterns on PET substrates using processes described herein.
Referring to Table 2, paste, or ink, formulations were made using approximately 1 micron-sized copper particles. The particles' size distribution did not contain particles having diameters less than approximately 0.3 micron. A hinder was approximately a 10% solution of ethyl cellulose as shown in Table 2. Films were drawn down on PET substrates (or may be printed using a screen printer). The films were dried (e.g., in an oven at approximately 100° C. for 30 minutes). Photosintering of the films used a pulsed light system (e.g., commercially available from Sinteron 2000, Xenon Corp.).
Electrical measurements were performed (e.g., using a four points probe). Adhesion was checked (e.g., by applying 3M “Magic” tape on the top of the photosintered copper film, pressing the tape from above with an erasure to ensure contact between the tape and the film, then peeling off the tape). Good adhesion is indicated when only traces of material stick to the tape. Poor adhesion is indicated when essentially the whole film is peeled away with the tape from the PET substrate.
Table 2 shows two examples of copper paste formulations. Formulation 2 contained a higher concentration of copper particles.
Material Concentration wt % Concentration wt %
Copper particles 50 65
7% binder solution 48 33
Dispersant 2 2
Before photosintering
Layer thickness (μm) 3 3
Sheet resistance Non-conductive Non-conductive
Adhesion None None
After photosintering at 2.5 kV
Sheet resistance (ohm-square) 0.20 0.04
Resistivity (ohm-cm) 6.0 × 10−5 1.2 × 10−5
Adhesion Good Poor
Both pastes were printed, on PET substrates and photosintered. Table 3 summarizes the results. Both formulations were not conductive (sheet resistance >10 kohm-square) and did not adhere to the PET substrate. After photosintering, both formulations produced conductive films. Films of Formulation 2 showed higher conductivity, but the films were fragile and did not adhere to the PET substrate as well as Formulation 1. On the other hand, photosintered films made with Formulation 1 showed good adhesion to the PET substrate.
Visual inspection of the samples showed that the top surface of the PET substrate partially melted and copper particles were embedded inside such surface. This effect was far more pronounced in films made with Formulation 1 than films made with Formulation 2. This observation indicated that the binder assists to affix the copper particles in place during photosintering and allows the hot particles to partially melt the PET substrate surface and trench themselves inside such top surface. Moreover, copper has a high thermal expansion coefficient relative to PET. Therefore, the photosintered film shows a certain degree of shrinkage and stress at the PET-copper film interface. This results in microscopic cracks in the copper film as shown in FIG. 4. Overall, it is desired to reach a balance for achieving as much photosintering to ensure high conductivity, yet avoiding too much photosintering that results in a highly stressed and brittle film.
The ethyl cellulose binder may be replaced or mixed with other binders such as acrylic, polyurethanes, and even an UV-curable hinder capable of forming a cross-linked matrix. Binders that have high absorbance in the UV or visible light ranges and affect the energy that can be absorbed by the film may also be used.
FIG. 5 shows a sample of Formulation 1 photosintered on a PET substrate. The tape used for testing adhesion is shown as well. The dashed rectangle indicates the area where the tape was applied. The tape is essentially clean.
Scanning Electron Microscopy (“SEM”) Results:
FIGS. 6 and 7 are SEM photographs of a photosintered film (˜3 μm) on a PET substrate. The rectangular hole in the sample was created using a focused ion beam (“FIB”) in order to obtain a cross-section of the layer. The SEM photographs show the copper particles embedded in the binder, and also show the particles still retain their original structure, characterized by the sharp corners. The FIB cross-section reveals that some particles are connected by thin necks. FIG. 7 is at a higher magnification showing “necking” between particles, as indicated by the white arrows. These necks are the results of photosintering and allow the film to become conductive.
Thermal vs. Photosintering:
Similar films were printed, on alumina substrates and subjected to merely thermal sintering. FIG. 8 shows an SEM photograph of such a film processed after 30 minutes at 800° C. in a N2/H2 environment. Under these conditions, the binder was burned away, and the particles were annealed and more rounded. Necks were observed as well.
FIG. 9 shows both a graph and table of the electrical conductivity results of thermal sintering at various temperatures compared to photosintering results. Conductivity increases (i.e., sheet resistance decreases) as the sintering temperature increases, yet even thermal sintering at 800° C. for 30 minutes could not achieve the conductivity reached using a few milliseconds of a photosintering light pulse (0.20-0.15 ohm-sqr).
The photochemical processes in photosintering allow decomposition of copper oxides to copper metal. The pulsed energy of photosintering enables the copper particles to momentarily reach high temperatures together with photoreduction of surface oxides. This combined mechanism leads to effective photosintering of the copper particles. The photosintering process is creating a high density of necking between the copper particles in the case of photosintering vis-a-vis thermal sintering. Photosintering achieves lower resistivity than thermal sintering. The necking density (number of necks per volume of particles) in the photosintering processes was observed to always be higher than the necking density achieved in the thermal sintering processes. Although the thermal sintering occurs in forming gas, one needs to assume that originally a copper particle has a layer of copper oxide on its surface. The thermal process (even in a forming gas, reducing environment) does not remove the copper oxide layer, and thus even if necking between copper particles is achieved, the necking resistance due to the copper oxide presence is higher than the pure copper necking obtained during the thermal sintering.
The surface morphology of the copper particles after photosintering shows sharp or rough edges and non-spherical shapes. The process is fast such that the surface does not have enough time to truly melt and reorganize its shape. The energy could be transferred into creating necks with nearest neighbors rather than inter-particle reorganization. The surface morphology of the copper particles after thermal sintering shows highly spherical shapes with smooth surface features. This smoothness supports a surface melting phenomena whereby a “skin” of surface oxide is controlling the particle shape.
The thermal sintering process takes a significantly long time. Experiments showed a process time of approximately 30 minutes to achieve conductive films. With thermal sintering, the oxide conversion due to chemical reduction with the forming gas environment is a slow process. This slow process greatly limits the number of necks achieved between particles and raises the resultant resistivity of the film.
Photosintering is a fast process. The photosintering process time is merely a few milliseconds. The light quickly removes surface oxides from the copper particles such that the particles can form neck connections during the secondary heating as a result of the light absorbance. The increased necking density results in lower resistivity compared to thermal sintering.
Printing Copper Paste on PCB Substrate and Polyethylene (“PE”):
FIGS. 10-12 show copper paste printed and photosintered on an epoxy-glass fiber PCB substrate (FIGS. 10-11) and on a PE substrate (FIG. 12). Resistivity for both substrates was approximately 4.5×10−5 ohm-cm. Adhesion was good as can be seen from the tape tests. Copper wires could easily be soldered to the copper film on the PCB substrate using well-known solder, as shown in FIG. 11.