Buffer layer to enhance photo and/or laser sintering - Patent # 8647979 - PatentGenius
8647979 Buffer layer to enhance photo and/or laser sintering
Attorney Or Agent: Kordzik; KellyMatheson Keys & Kordzik PLLC
U.S. Class: 438/637; 257/774; 257/E21.577; 257/E23.011; 438/151
Field Of Search: ;257/774; ;257/E27.113; ;257/E27.114; ;257/E27.115; ;257/E27.116; ;257/23.018; ;438/637; ;438/151
Foreign Patent Documents: 1509206; 62124084; 10-308119; 11-319538; 2001-325831; 2008006513; 03106573; 2004005413; 2006072959
Other References: The State Intellectual Property Office of the People's Republic of China, Notice on Grant of Patent Right for Invention, Application No.200880021733.6, Apr. 20, 2012. cited by applicant.
The State Intellectual Property Office of the People's Republic of China, Notice on the First Office Action, Application No. 200980125925.6, Mar. 31,2012, 8 pages, CN. cited by applicant.
Kogelschatz, "Excimer Lamps: History, Discharge Physics, and Industrial Applications", Proc. SPIE, vol. 5483, 2004. pp. 272-286. cited by applicant.
Kim et al., "Cyclic Properties of Si-Cu/Carbon Nanocomposite Anodes for Li-Ion Secondary Batteries", Journal of the Electrochemical Society, vol. 152. No. 3, pp. A-523-A-526, Jan. 24, 2005, retrieved from internet Aug. 26, 2010. cited by applicant.
International Search Report and the Written Opinion of the International Searching Authority for PCT/US10/042169, mailed on Sep. 7, 2010, 4 pages. cited by applicant.
Yaniv, "Novel Inkettable Copper Ink Utilizing Processing Temperatures Under 100 Degrees C Without the Need of Inert Atmosphere", Presentation at Printed Electronics Europe Conference, pp. 1-25, Apr. 7-8, 2009, retrieved from internet Aug. 26, 2010.cited by applicant.
International Preliminary Report on Patentability, PCT/US2010/042169, Jan. 17, 2012. cited by applicant.
Notice on the First Office Action; Patent Application No. 200980108344.1, Jan. 21, 2012. cited by applicant.
TEGO 425 Datasheet; http://evonik.tego.de/pdf/daten/amer/Flow.sub.--425.pdf. cited by applicant.
United States Patent & Trademark Office, Final Office Action Summary, U.S. Appl. No. 12/391,817, dated Aug. 27, 2012. cited by applicant.
United States Patent & Trademark Office, Non-Final Office Action Summary, U.S. Appl. No. 12/496,453, dated Jun. 13, 2012. cited by applicant.
European Patent Office, Examination Report, Application No. 08 755 692.4, Apr. 13, 2012. cited by applicant.
Champion et al., "Sintering of copper nanopowders under hydrogen: an in situ X-ray diffraction analysis" , Materials Science and Engineering A, vol. 360, No. 1-2, Nov. 1, 2003, pp. 258-263. cited by applicant.
Schroder et al., "Broadcast Photonic Curing of Metallic Nanoparticle Films," Nanotechnologies, Inc. publication, 2006 NSTI Nanotechnology Conference and Trade Show, May 7-11, 2006, 4 pages. cited by applicant.
Lu et al., "Ultrahigh Strength and High Electrical Conductivity in Copper," Science Magazine, Apr. 2004, vol. 304, 6 pages. cited by applicant.
Volkman et al., "Ink-jetted Silver/Copper Conductors for printed RFID Applications," Materials Research Society Magazine, 2004, vol. 814, 6 pages. cited by applicant.
Wu et al., "One-Step Green Route to Narrowly Dispersed Copper Nanocrystals," Journal of Nanoparticle Research, 2006, pp. 965-969, 5 pages. cited by applicant.
Curtis et al., "Spray and Inkjet Printing of Hybrid Nanoparticle-Metal-Organic Inks for Ag and Chu Metallizations," Materials Research Society Magazine, 2001, vol. 676, 6 pages. cited by applicant.
Shacham-Diamond, "Electroless Copper Deposition Using Glyoxylic Acid as Reducing Agent for Ultralarge Scale Integration Metallization," manuscript published by Electrochemical and Solid-State Letters, Apr. 2000, pp. 279-282, 4 pages. cited byapplicant.
Yeshchenko et al., "Size-Dependent Melting of Spherical Copper Nanoparticles" article published by National Taras Shevchenko Kyiv University, Jan. 2007, 16 pages. cited by applicant.
Virang G. Shah, "Trimming and Printing of Embedded Resistors Using Demand-Mode Ink-Jet Technology and Conductive Polymer," IPC Printed Circuit Expo Mar. 24-28, 2002, pp. 1-5. cited by applicant.
International Search Report for PCT/US08/63890, Aug. 6, 2008, 9 pages. cited by applicant.
International Search Report and Written Opinion for Application No. PCT/US/09/35717, May 5, 2009, 7 pages. cited by applicant.
Niizeki et al., "Laser Sintering of Ag Nanopaste Film and Its Application to Bond-Pad Formation," 2008 Electronic Components and Technology Conference, May 27-30, 2008, IEEE, pp. 1745-1750. cited by applicant.
Lee et al., "Spontaneous Growth Mechanism of Tin Whiskers," Acta mater. vol. 46, No. 10, pp. 3701-3714, 1998. cited by applicant.
Gaylon, "Annotated Tin Whisker Bibliography and Anthology," IEEE Transactions on Electronics Packaging Manufacturing, vol. 28, No. 1, Jan. 2005, pp. 94-122. cited by applicant.
Lal et al., "Role of Intrinsic Stresses in the Phenomena of Tin Whiskers in Electrical Connectors," IEEE Transactions on Electronics Packing Manufacturing, vol. 28, No. 1, Jan. 2005, pp. 63-74. cited by applicant.
Boettinger et al., "Whisker and Hillock Formation on Sn, Sn-Cu and Sn-Pb Electrodeposits," Acta Materialia, 53, Sep. 8, 2005, pp. 5033-5050. cited by applicant.
Mitooka et al., "Effect of Laser Irradiation on Generation and Growth of Whiskers in Tin-Electroplated Film," J. Japan Inst. Metals, vol. 73, No. 3, (2009), pp. 226-233. cited by applicant.
Osenbach et al., "Sn Corrosion and Its Influence on Whisker Growth," IEEE Transactions on Electronic Packaging Manufacturing, vol. 30, No. 1, Jan. 2007, pp. 23-35. cited by applicant.
Osenbach et al., "Sn Whiskers: Material, Design, Processing, and Post-Plate Reflow Effects and Development of an Overall Phenomenological Theory," IEEE Transactions on Electronics Packaging Manufacturing, vol. 28, No. 1, Jan. 2005, pp. 36-62. citedby applicant.
Osterman, "Mitigation Strategies for Tin Whiskers," Release 1.0, Aug. 28, 2002, 11 pages. cited by applicant.
Schroeder et al., "Tin Whisker Test Method Development," IEEE Transactions Electronics Packaging Manufacturing, vol. 29, No. 4, Oct. 2006, pp. 231-238. cited by applicant.
International Search Report and Written Opinion for International Application No. PCT/US09/44196, Jun. 30, 2009, 8 pages. cited by applicant.
International Search Report and Written Opinion for International Application No. PCT/US09/44195, Jun. 25, 2009, 7 pages. cited by applicant.
International Preliminary Report on Patentability, International Application No. PCT/US2009/044196, Nov. 25, 2010, 6 pages. cited by applicant.
International Preliminary Report on Patentability, International Application No. PCT/US2009/044195, Nov. 25, 2010, 5 pages. cited by applicant.
International Search Report and Written Opinion for International Application No. PCT/US09/49510, Oct. 19, 2009. cited by applicant.
International Preliminary Report on Patentability, PCT/US2008/063890, Dec. 3, 2009. cited by applicant.
International Search Report and Written Opinion of the International Searching Authority for PCT/US10/28799, May 19, 2010. cited by applicant.
International Search Report and the Written Opinion of the International Searching Authority for PCT/US10/28811, May 18, 2010. cited by applicant.
MSDS: Fluorad by 3M , Fluorosurfactant FC-4430, Mar. 2, 2002; www.3m.com/paintsandcoatings, 4 pages. cited by applicant.
Supplemental European Search Report; Application No. EP 09774505, Jun. 29, 2011. cited by applicant.
Notice of the First Office Action, Application No. 200880021733.6, Jun. 22, 2011. cited by applicant.
Supplementary European Search Report, Application No. EP08755692, dated Aug. 6, 2010. cited by applicant.
Korean Intellectual Property Office, Chemistry & Biotechnology Examination Bureau, Notice to File a Response, Patent Application No. 10-2010-7022240, May 8, 2012, KR. cited by applicant.
Abstract: Conductive lines are deposited on a substrate to produce traces for conducting electricity between electronic components. A patterned metal layer is formed on the substrate, and then a layer of material having a low thermal conductivity is coated over the patterned metal layer and the substrate. Vias are formed through the layer of material having the low thermal conductivity thereby exposing portions of the patterned metal layer. A film of conductive ink is then coated over the layer of material having the low thermal conductivity and into the vias to thereby coat the portions of the patterned metal layer, and then sintered. The film of conductive ink coated over the portion of the patterned metal layer does not absorb as much energy from the sintering as the film of conductive ink coated over the layer of material having the low thermal conductivity. The layer of material having the low thermal conductivity may be a polymer, such as polyimide.
1. A method for depositing conductive lines on a substrate comprising: depositing a metal layer in a pattern on the substrate; coating a layer of material having a lowthermal conductivity over the pattern metal layer and the substrate; depositing a film of conductive ink over the layer of material having the low thermal conductivity; and sintering the film of conductive ink.
2. The method as recited in claim 1, further comprising: forming a via through the layer of material having the low thermal conductivity thereby exposing a portion of the patterned metal layer, wherein the depositing of the film of conductiveink includes depositing the film of conductive ink into the via to thereby coat the portion of the patterned metal layer with the film of conductive ink, wherein the film of conductive ink coating the portion of the patterned metal layer is alsosintered.
3. The method as recited in claim 1, wherein the substrate has a thermal conductivity greater than the layer of material having the low thermal conductivity.
4. The method as recited in claim 2, wherein the film of conductive ink coated over the portion of the patterned metal layer does not dissipate as much energy from the sintering as the film of conductive ink coated over the layer of materialhaving the low thermal conductivity.
5. The method as recited in claim 4, wherein the layer of material having the low thermal conductivity comprises a polymer.
6. The method as recited in claim 4, wherein the layer of material having the low thermal conductivity comprises polyimide.
7. The method as recited in claim 6, wherein the polyimide has a thickness of at least 50 microns.
8. The method as recited in claim 6, wherein the sintering is performed with a photo sintering apparatus.
9. The method as recited in claim 6, wherein the sintering is performed with a laser sintering apparatus.
10. The method as recited in claim 6, wherein the polyimide has a thickness of at least 5 microns.
11. The method as recited in claim 6, wherein the polyimide has a thickness of at least 2.3 microns.
12. The method as recited in claim 6, wherein the substrate comprises silicon.
13. The method as recited in claim 6, wherein the substrate comprises ceramic.
14. The method as recited in claim 6, wherein the film of conductive ink comprises copper nanoparticles.
15. The method as recited in claim 9, wherein the laser sintering apparatus comprises a solid state diode with an 830 nm wavelength and 800 mW power.
16. The method as recited in claim 15, wherein the solid state diode has a focus beam size of 15 microns in diameter.
17. Electronic circuitry comprising: a substrate; a pattern of metal traces deposited on the substrate; a layer low thermal conductive material coated over the substrate and the pattern of metal traces deposited on the substrate, wherein viasare formed through the layer of low thermal conductive material over portions of the pattern of metal traces; and a film of sintered conductive ink coated over the layer of low thermal conductive material coated over the substrate, wherein the film ofsintered conductive ink is coated over the portions of the pattern of metal traces within the vias formed through the layer of low thermal conductive material.
18. The electronic circuitry as recited in claim 17, wherein the substrate has a thermal conductivity greater than the layer of low thermal conductive material.
19. The electronic circuitry as recited in claim 18, wherein the layer of low thermal conductive material comprises polyimide.
20. The electronic circuitry as recited in claim 19, wherein the polyimide has a thickness of at least 50 microns.
21. The electronic circuitry as recited in claim 19, wherein the sintered conductive ink comprises sintered copper nanoparticles sintered with a photo sintering apparatus.
22. The electronic circuitry as recited in claim 19, wherein the sintered conductive ink comprises sintered copper nanoparticles sintered with a laser sintering apparatus.
23. The electronic circuitry as recited in claim 19, wherein the polyimide has a thickness of at least 5 microns.
24. The electronic circuitry as recited in claim 19, wherein the polyimide has a thickness of at least 2.3 microns.
25. The electronic circuitry as recited in claim 19, wherein the substrate comprises silicon.
The microelectronics and semiconductor packaging industries have begun to shift to printable electronics. Electronics circuits comprise a variety of components that are electrically connected to each other. Such electrical connections betweendifferent components may be made of conductive metal traces that can be printed on substrates with conductive inks The inks are processed and sintered after deposition on a substrate in order to become conductive. Thermal sintering uses a hightemperature (e.g., .gtoreq.250.degree. C.) to fuse the nanoparticles in the inks Photonic (photo) and laser sintering utilize a very high intensity lamp/laser to fuse the nanoparticles in a very short period of time (e.g., microseconds) with a lowtemperature and so as not to damage the underlying substrates. However, the photo/laser sintering process has limits that require low thermal conductivity material for substrates in order for the nanoparticles to effectively absorb energy and sinterbefore heat energy dissipates into the substrate. In other words, the substrates that can be used in these applications will be very limited for low thermal conductivity materials.
On the other hand, low thermal conductive substrates can be used for flexible printable electronics. Low temperature melting point materials such as polyethylene (PE), polyester (PET), etc., will prevent the nanoparticle inks from propersintering, and the substrates will be damaged, with the result that the resistivity will be very high.
FIG. 1 is a digital photo showing copper inks photo sintered on four silicon wafers.
FIG. 2 is a digital photo showing copper inks before being photo sintered.
FIG. 3 is a digital photo showing copper inks after being photo sintered.
FIG. 4 is a digital photo showing laser sintered lines on a Kapton substrate.
FIG. 5 is an enlarged digital photo showing the laser sintered lines of FIG. 4.
FIG. 6 illustrates a graph showing that copper ink resistivity sintered by a laser is not only inversely proportional to laser power, but also inversely proportional to buffer layer thickness made of polyimide.
FIG. 7 illustrates a graph showing thicknesses of cured polyimide measured at various spin speeds.
FIG. 8 illustrates a graph showing that resistivity of sintered copper film is inversely proportional to polyimide thickness.
FIG. 9 illustrates a graph showing that adhesion of copper ink film to polyimide is proportional to polyimide thickness.
FIG. 10 illustrates a graph showing that laser writing line width is proportional to the laser power density.
FIGS. 11A-11F illustrate a process in accordance with embodiments of the present invention.
Embodiments of the present invention disclose a photo sintering process to effectively sinter metallic nanoparticles on a polyimide substrate, thus causing the film to be very conductive near the bulk material. On other hand, the photosintering process does not perform well on nanoparticle inks coated on substrates possessing a high thermal conductivity, such as ceramics and silicon wafer. Table 1 shows the thermal conductivity for a variety of materials.
TABLE-US-00001 TABLE 1 heat melting density heat capacity conductivity thermal point, C. item # material (g/cm.sup.3) (J/g K) (W/m K) effusivity degrees 1 air 0.0013 1 0.025 0.00 NA 2 paper 0.33 0.73 0.030 0.01 NA 3 Polyimide (kapton) 1.42 1.090.120 0.19 NA 4 PMMA (resist) 1.19 1.46 0.160 0.28 180 5 PET (Mylar) 1.23 1.13 0.176 0.24 150 6 LCP (liquid crystal 1.4 1.6 0.500 1.12 300 polymer) 7 PE (polyethylene, 0.95 2.3 0.500 1.09 125 high density) 8 water 1 4.2 0.600 2.52 0 9 glass 2.3 0.7531.330 2.30 950 10 SiO.sub.2 2.2 0.75 1.380 2.28 1600 11 MgO 3.2 0.84 5.900 15.86 2852 12 carbon-amorphous 1.51 0.707 6.280 6.70 3600 13 Si.sub.3N.sub.4 2.8 0.69 7.950 15.36 1900 14 TiO.sub.2 4.25 0.69 9.000 26.39 1843 15 CuO/Cu.sub.2O 6.5 0.536 18.00062.71 1235 16 Ti 4.5 0.523 21.000 49.42 1668 17 Al.sub.2O.sub.3 (ceramics) 2.5 0.81 30.000 60.75 2054 18 solder 8.5 0.197 50.210 84.08 185 (60/40 Sn/Pb) 19 Ni 8.9 0.444 88.000 347.74 1455 20 Mo 10.2 0.25 134.000 341.70 2623 21 Si 2.33 0.7 148.000 241.391414 22 carbon-graphite 2.25 0.707 167.360 266.23 3600 23 Al 2.7 0.88 209.000 496.58 660 24 Au 19.3 0.13 318.000 797.86 1086 25 Cu 8.9 0.385 398.000 1363.75 1064 26 carbAL 2.3 0.75 425.000 733.13 3600 27 Ag 10.5 0.24 427.000 1076.04 962 28 carbon-diamond3.51 0.506 543.920 966.03 3800 29 carbon nanotubes 6000.000
Low conductivity materials, such as polyimide, can be used as a coating material onto other high thermal conductivity substrates, such as ceramics and silicon wafer, in order to isolate heat energy dissipation from nanoparticles during a photosintering process so that the nanoparticles are fused more effectively. How quickly heat dissipates depends on the thickness of the low thermal conductivity material (e.g., polyimide film).
The following experiment was conducted for showing how the present invention operates. Three wafers were spin coated with 1, 1.5, and 2.3 microns thick DuPont PI-2610 polyimide, respectively, and thermal cured at 350.degree. C. for 30 minutes. One bare silicon wafer was used for a reference (wafer #1). All four wafers were coated with copper ink using a drawdown process. After a 60 minute drying process at 100.degree. C., each wafer was divided into three zones that were individuallysintered with three different energy levels. The resistance for each zone and each wafer was measured with a voltmeter, with the results shown in Table 2, which shows the electrical resistances of a copper film after photo sintering with various coatingthicknesses of polyimide on silicon wafers.
TABLE-US-00002 TABLE 2 Zone 1: Zone 2: Zone 3: polyimide resistance resistance resistance thickness copper ink with with with wafer # (.mu.m) (.mu.m) energy 1 energy 2 energy 3 1 0 3.2 >20 M.OMEGA. >20 M.OMEGA. >20 M.OMEGA. 2 1 3.2>20 M.OMEGA. >20 M.OMEGA. >20 M.OMEGA. 3 1.5 3.2 >20 M.OMEGA. >20 M.OMEGA. >20 M.OMEGA. 4 2.3 3.2 >20 M.OMEGA. >20 M.OMEGA. 20 .OMEGA..sup. where energy 1 = 3 sinter shots with 850/1050 V, 1000 .mu.sec energy 2 = 4 sintershots with 850/1150 V, 1000 .mu.sec energy 3 = 5 sinter shots with 850/1250 V, 2000 .mu.sec
Except for zone 3 of wafer 4, all zones from the four wafers did not experience a change in resistance after photo sintering. Zone 3 of wafer 4 experienced a change in its metallic color at the highest energy level, as shown in FIG. 1. Thearea had a severe blow off. The surrounding area had copper debris left that was conductive. This is clear evidence that the polyimide material may be used as a thermal insulator. The thickness of polyimide may be more than 3 microns. The thermalconductivity is 0.12 and 148 W/mK for polyimide and silicon, respectively. The heat dissipated into the silicon substrate (wafer #1) too quickly to sinter the copper nanoparticles since there was no polyimide material.
Wafers 1, 2, and 3 all had high resistance (greater than 20 mega ohms). Wafer 4 at the center zone with 20 ohms resistance as shown in FIG. 1 appeared that the copper nanoparticles film started to be fused, sintered, and turned into a coppercolor. The thicker low thermal conductivity material can thus be used as a good thermal insulator.
In addition to the liquid polyimide disclosed above, a dry polyimide film was also utilized. The copper ink was coated on a 50 micron polyimide film (Kapton). The sample was placed on a silicon wafer and a carbAL high thermal conductive heatsink, as shown in FIG. 2. Silicon grease was coated in between the Kapton and the silicon wafer and carbAL to ensure good thermal contact. The sample was photo sintered simultaneously in a single shot. The copper was sintered very well and turned ashiny copper color, as shown in FIG. 3. It did not matter what materials the Kapton was residing on. At least a 50 micron thick polyimide is sufficiently thick to isolate and prevent heat energy dissipation for photo sintering processes, though athickness of less than 50 microns may be utilized for embodiments where less conductivity is desired of the conductive traces.
In addition, laser sintering was utilized on silicon wafers with the same setup as described above. The laser was a solid state diode with an 830 nm wavelength and an 800 mW power. The focus beam size was 15 microns in diameter and controlledby a collimator and an objective lens, as shown in FIGS. 4 and 5.
This laser had sufficient power to sinter and fuse the nanoparticles and turn the copper ink conductive. There were four silicon wafers coated with various polyimide thicknesses of 1, 1.5, 2, and 3 microns, respectively, along with a baresilicon wafer as a reference. The resistivity of each wafer is plotted with laser power in FIG. 6, which indicates that the copper film conductivity is proportional to the polyimide thickness, and the heat generated by the laser is transferred to thesubstrate less with polyimide present than the bare silicon wafer without polyimide. This is clear evidence that any material having a low thermal conductivity, such as polyimide material, may be used as a thermal insulator and enhance the photo andlaser sintering processes.
Furthermore, a variety of polyimide thicknesses were coated on silicon wafers and cured at 350.degree. C. for one hour. Then the standard copper ink was coated by drawdown, dried in an oven, and photo/laser sintered. Electrical measurementswere performed and characterized the copper ink samples.
Three types of polyimide material made by DuPont were used to spin coat on silicon wafer at 1000, 2000, 3000, 4000 and 5000 rpm. FIG. 7 illustrates a graph showing thicknesses of cured polyimide measured at various spin speeds. The range wasfrom 1 to 20 microns on each wafer, respectively.
After samples were prepared, both photo and laser sintering were performed on the copper inks Different types of sintering were compared versus resistivity and adhesion, as well as line width for laser sintering. Table 3 shows samples photosintered at the same energy level with various thicknesses of polyimide. Table 4 shows samples laser sintered at a fixed power level with various thicknesses of polyimide.
TABLE-US-00003 TABLE 3 sample polyimide thickness Cu ink thickness resistivity adhesion # (.mu.m) (.mu.m) (ohm-cm) (1-10) 1 0 3 3.00E+01 1 2 5 2 1.30E-04 2 3 6.5 2 4.00E-05 4 4 8.7 2 1.60E-05 7 5 12.5 2 1.52E-05 7 6 10 1.5 1.50E-05 8 7 14 1.51.40E-05 8 8 20 1.5 1.14E-05 8
TABLE-US-00004 TABLE 4 polyimide resistivity line width line width thickness (ohm-cm) at adhesion (.mu.m) at (.mu.m) at sample # (.mu.m) 840 mW (1-10) 840 mW 409 mW 11 0 1.60E-04 1 70 35 12 1 1.26E-05 5 74 38 13 1.5 1.36E-05 5 77 39 14 29.33E-06 3 83 40 15 3 6.00E-06 1 88 42 16 5 4.75E-06 8 92 65 17 7 4.82E-06 8 103 75 18 12 3.61E-06 8 150 88 19 20 5.47E-06 8 180 120
FIG. 8 illustrates a graph showing that resistivity of sintered copper film is inversely proportional to polyimide thickness. The saturated points for resistivity are approximately at 10 microns for photo sintering and approximately at 5microns for laser sintering. Power density of photo sintering is much lower than that of laser sintering, providing a reason why its resistivity is higher.
FIG. 9 illustrates a graph showing that adhesion of copper ink film to polyimide is proportional to polyimide thickness. There are some noise points, but the trend is clear from the graph. The thicker the polyimide is, the better the adhesionis. Again, critical points of polyimide thickness for the good adhesion are approximately at 10 microns for photo sintering and approximately at 5 microns for laser sintering.
FIG. 10 illustrates a graph showing that laser writing line width is proportional to the laser power density. With given laser power, the laser writing line width is also proportional to the polyimide film thickness, providing more evidencethat polyimide is a good thermal insulator for these processes. The laser energy and heat deposited on the copper ink surface could not spread any deeper vertically but laterally while the polyimide thickness increased.
Referring to FIGS. 11A-11F, a process for performing embodiments of the present invention is illustrated. A substrate 1101 is provided on which electronic circuitry is to be mounted. In FIG. 11B, traces of a metal material 1102 are depositedin a desired pattern on the substrate 1101, using a well-known manufacturing process. In FIG. 11C, a layer of low thermal conductivity material 1103, such as polyimide, is coated over the metal traces 1102 and substrate 1101. To create further patternsfor the conductive traces to be deposited, vias 1104 are formed through the material 1103, exposing portions of the metal traces 1102. In FIG. 11E, an ink jet apparatus 1106 deposits a conductive ink 1105, such as copper nanoparticles, over the material1103 and the metal traces 1102 exposed by the vias 1104. In FIG. 11F a photo or laser sintering process is performed on the deposited conductive ink nanoparticles 1105 to sinter them into conductive traces 1107, as described herein. Depositing of theconductive inks and the sintering processes are described in U.S. Patent Publication No. 2008/0286488 A1, which is hereby incorporated by reference herein.
1. The effectiveness of a photo sintering process depends on not only metallic nanoparticle size, but also the type of substances.
2. Effective photo sintering is achieved with nanoparticles below 300 nm.
3. The thermal conductivity of substrates will affect metallic ink photo sintering. The lower the thermal conductivity of the substrate, the better the electrical conductivity of the nanoparticle film.
4. High thermal conductive substrates can be tailored and isolated by coating low thermal conductivity material, such as polyimide or polymer, for an effective photo sintering process.
5. The thickness of coating of polyimide required to isolate thermal heat dissipation is approximately 1-50 microns.
6. The copper ink becoming a conductive film has been demonstrated on high thermal conductive material such as silicon wafer with both laser and photo sintering.
7. Heat dissipation on high thermal conductive silicon wafers has been shown with a variety of polyimide thicknesses coated on a wafer. A low thermal conductive material can be used as a buffer layer to slow down heat dissipation and enhancethe photo or laser sintering.
8. Copper ink may be sintered well with polyimide coated on a silicon wafer with resistivity at 1.times.10.sup.-5 ohm-cm by photo sintering and 4.times.10.sup.-6 ohm-cm by laser sintering.
9. The polyimide material may be not only utilized as a heat insulator on high thermal conductive substrates and enhance copper ink photo and laser sintering effectiveness, but also applied to low melting temperature substrates as a heatinsulator to protect from heat damage during a sintering process.
10. Polyimide layer and metal trace layer can be repeated several times as multilayer circuits.
11. Polyimide layer can be used as a dielectric material and incorporated as capacitors.
12. Nano-copper ink can be used at top layer conductor as a contact metal in two-dimensional and three-dimensional chip packaging applications.
Flea-rid and grooming apparatus and methods
Correction of rapid periodic timing errors in the production of tape-recorded color television signals and the like
Method of manufacturing a permanent magnet which is to be arranged in an air gap of a transformer core
Nonvolatile memory and card reader provided with the same
Functional organic particles for catalyst supports
High performance read bypass test for SRAM circuits