Patent US7854985 - Decorative paint film laminate - Google Patents
A decorative paint film laminate having high gloss and distinctness of image after processing for providing a decorative finish for a part, the decorative paint film laminate comprises a paint film having an inner surface and an outer surface, a backing sheet applied to the inner surface of the paint...http://www.google.com/patents/US7854985?utm_source=gb-gplus-sharePatent US7854985 - Decorative paint film laminate
Publication number US7854985 B2
Application number US 11/283,242
Also published as CA2628183A1, CA2628183C, EP1948262A2, EP1948262B1, US20070116903, US20110094664, WO2007059282A1, WO2007059282A8, WO2007059282A9
Publication number 11283242, 283242, US 7854985 B2, US 7854985B2, US-B2-7854985, US7854985 B2, US7854985B2
Inventors Quan Song, Jingfu Fan, Jerry Patton
Original Assignee Soliant Llc
Patent Citations (69), Non-Patent Citations (2), Referenced by (5), Classifications (66), Legal Events (3)
Decorative paint film laminate
US 7854985 B2
A decorative paint film laminate having high gloss and distinctness of image after processing for providing a decorative finish for a part, the decorative paint film laminate comprises a paint film having an inner surface and an outer surface, a backing sheet applied to the inner surface of the paint film, and no mask on the outer surface of the paint film. The paint film comprises a clear coat layer, a gloss and distinctness of image retaining layer, and a color coat layer. The paint film obtains high gloss and distinctness of image without a mask being on the outer surface of the paint film.
1. A decorative paint film laminate having enhanced gloss and distinctness of image after processing for providing a decorative finish for a part, the decorative paint film laminate comprising: a paint film having an inner surface and an outer surface with no mask adhered to the outer surface, and a backing sheet applied to the inner surface of the paint film, wherein the paint film comprises a clear coat layer, a gloss and distinctness of image retaining layer, and a color coat layer, and wherein the gloss and distinctness of image retaining layer has a tensile strength that is the same as or higher than the higher of the tensile strength of either the clear coat layer or the color coat layer at the thermoforming temperature.
2. The decorative paint film laminate according to claim 1, wherein processing is selected from the group consisting of forming or molding.
3. The decorative paint film laminate according to claim 2, wherein the forming is thermoforming at a thermoforming temperature.
4. The decorative paint film laminate according to claim 3, wherein the gloss and distinctness of image retaining layer has a tensile strength that is higher than the higher of the tensile strength of either the clear coat layer or the color coat layer at the thermoforming temperature.
5. The decorative paint film laminate according to claim 1, wherein the gloss and distinctness of image retaining layer is cast or coated.
6. The decorative paint film laminate according to claim 1, wherein the gloss and distinctness of image retaining layer comprises a polymer selected from the group consisting of urethane, acrylic, fluoropolymer, nylon, an alloy thereof, and a combination thereof.
7. The decorative paint film laminate according to claim 6, wherein the urethane is a polyurethane.
8. The decorative paint film laminate according to claim 6, wherein the fluoropolymer is polyvinylidene fluoride, polyvinyl fluoride, an alloy thereof, or a combination thereof.
9. The decorative paint film laminate according to claim 1, wherein the gloss and distinctness of image retaining layer is present between the clear coat layer and the color coat layer of the paint film.
10. The decorative paint film laminate according to claim 1, wherein the paint film further comprises a color adjustment layer.
11. The decorative paint film laminate according to claim 10, wherein the color adjustment layer is present between the gloss and distinctness of image retaining layer and the color coat layer.
12. The decorative paint film laminate according to claim 1, wherein the part is an automobile part.
13. The decorative paint film laminate according to claim 1, wherein the gloss and distinctness of image retaining layer is about 0.2 mils to about 2.0 mils in thickness.
14. The decorative paint film laminate according to claim 1, wherein the gloss and distinctness of image retaining layer further comprises a cross-linking agent.
15. The decorative paint film laminate according to claim 14, wherein the cross-linking agent is selected from the group consisting of poly-aziridine, poly-isocyanate, and blocked poly-isocyanate, and amino cross-linking agents.
16. The decorative paint film laminate according to claim 14, wherein the cross-linking agent is present in an amount from about 0.1 to about 4.0 weight percent.
17. The decorative paint film laminate according to claim 1, further comprising a primer layer.
18. The decorative paint film laminate according to claim 1, further comprising an adhesive layer.
19. The decorative paint film laminate according to claim 1, wherein the clear coat layer is about 0.3 mils to about 3 mils in thickness.
20. A paint film thermoformable at a thermoforming temperature, the paint film comprising: a clear coat layer, a gloss and distinctness of image retaining layer, and a color coat layer; wherein the gloss and distinctness of image retaining layer has a tensile strength the same as or higher than the higher of the tensile strength of either the clear coat layer or the color coat layer at the thermoforming temperature.
21. The paint film according to claim 20, wherein the tensile strength of the gloss and distinctness of image retaining layer is higher than the higher of the tensile strength of either the clear coat layer or the color coat layer at the thermoforming temperature.
22. A paint film comprising: a clear coat layer with no mask adhered to the clear coat layer; a gloss and distinctness of image retaining layer; and a color coat layer; wherein the gloss and distinctness of image retaining layer comprises a polymer selected from the group consisting of urethane, acrylic, fluoropolymer, nylon, an alloy thereof, and a combination thereof, and wherein the gloss and distinctness of image retaining layer has a tensile strength that is the same as or higher than the higher of the tensile strength of either the clear coat layer or the color coat layer at the thermoforming temperature.
23. A composite shaped part comprising: a substrate; and a decorative paint film laminate comprising a paint film comprised of a clear coat layer, a gloss and distinctness of image retaining layer, and a color coat layer, the paint film having an inner surface and an outer surface, a backing sheet applied to the inner surface of the paint film, and no mask on the outer surface of the paint film, and wherein the gloss and distinctness of image retaining layer has a tensile strength that is the same as or higher than the higher of the tensile strength of either the clear coat layer or the color coat layer at the thermoforming temperature.
24. The composite shaped part according to claim 23, wherein the paint film is thermoformable at a thermoforming temperature.
25. The composite shaped part according to claim 24, wherein the gloss and distinctness of image retaining layer has a tensile strength that is higher than the higher of the tensile strength of either the clear coat layer or the color coat layer at the thermoforming temperature.
26. The composite shaped part according to claim 23, wherein the gloss and distinctness of image retaining layer is cast or coated.
27. The composite shaped part according to claim 23, wherein the gloss and distinctness of image retaining layer comprises a polymer selected from the group consisting of urethane, acrylic, fluoropolymer, nylon, an alloy thereof, and a combination thereof.
28. The composite shaped part according to claim 27, wherein the urethane is a polyurethane.
29. The composite shaped part according to claim 27, wherein the fluoropolymer is polyvinylidene fluoride, polyvinyl fluoride, an alloy thereof, or a combination thereof.
30. The composite shaped part according to claim 23, wherein the gloss and distinctness of image retaining layer is present between the clear coat layer and the color coat layer of the paint film.
31. The composite shaped part according to claim 23, wherein the paint film further comprises a color adjustment layer.
32. The composite shaped part according to claim 31, wherein the color adjustment layer is present between the gloss and distinctness of image retaining layer and the color coat layer.
33. The composite shaped part according to claim 23, wherein the composite shaped part is an automobile part.
34. The composite shaped part according to claim 23, wherein the gloss and distinctness of image retaining layer is about 0.2 mils to about 2.0 mils in thickness.
35. The composite shaped part according to claim 23, wherein the gloss and distinctness of image retaining layer further comprises a cross-linking agent.
36. The composite shaped part according to claim 35, wherein the cross-linking agent is selected from the group consisting of poly-aziridine, poly-isocyanate, blocked isocyanate, and amino cross-linking agents.
37. The composite shaped part according to claim 35, wherein the cross-linking agent is present in an amount from about 0.1 to about 4.0 weight percent.
38. The composite shaped part according to claim 23, further comprising a primer layer.
39. The composite shaped part according to claim 23, further comprising an adhesive layer.
The present invention relates to a decorative paint film laminate that has high gloss and distinctness of image after processing without the use of a mask on the outer surface of the paint film, and a method for the making of the decorative paint film laminate.
Manufacturers have shown increasing interest in using paint film in lieu of spray painting for providing a decorative surface finish for parts such as automotive body parts. These parts can be manufactured using one or more of the following forming or molding processes: thermoforming, injection molding, or compression molding. In general, most processes using paint film such as thermoforming involve forming the film into a three dimensional shape and involve the use of heat and pressure. Depending upon a variety of factors including, for example, the geometry of an automobile body part, the automobile body part may or may not require an injection molding process, as long as the part is sturdy enough to facilitate the manufacturing process and is suitable for the intended end use application.
Paint films have been used for many years in a variety of applications and uses. Current products tend to lose gloss and distinctness of image (DOI) when processed, such as thermoformed, especially in high stretch areas. In many of the current paint film applications, especially high stretch applications, this deficiency has been overcome with the use of a mask to achieve high gloss and DOI for the surface finishes during thermoforming. In order to maintain the gloss and DOI, the mask must have sufficient modulus at the thermoforming temperature to maintain the smooth surface finish. In these applications, a thermoformable mask film is applied and removably adhered to the clear coat surface of the decorative sheet before the thermoforming process. In many cases, the mask is removed and discarded during the part manufacturing process, for example, before the injection molding process. The materials and manufacturing process of the mask film add significant cost to the parts produced using paint film. In addition, the use of the mask, in some cases, complicates the forming and molding processes. For example, the mask may need to be removed before an injection molding process to prevent the difficulty of removal after the parts are molded. The mask may be difficult to remove because it has been stretched substantially and becomes prone to tear and must be removed in pieces adding significant labor and possible contamination in subsequent processing. Furthermore, to date, known masked paint films have not been able to achieve a 20° gloss that is within the lower gloss range of traditional paints. Therefore, the present invention attempts to address and solve these problems.
The present invention relates to a decorative paint film laminate having improved high gloss and distinctness of image (DOI) after processing without the use of a mask on the outer surface of the paint film. The decorative paint film laminate basically comprises a gloss and DOI retaining layer in addition to a clear coat layer and a color coat layer. The gloss and DOI retaining layer functions an “internal” mask and has, among other properties, excellent clarity, good adhesion to both clear and color layers, good weatherability, and thermoformability.
The decorative paint film laminate comprises a paint film having an inner surface and an outer surface, and a backing sheet applied to the inner surface of the paint film. The paint film comprises a clear coat layer, a gloss and DOI retaining layer, and a color coat layer. The paint film may optionally comprise any of a color adjustment layer, a primer layer, and an adhesive layer. Also within the scope of the present invention is a composite shaped part, a method of making a decorative paint film laminate, and a paint film comprising a gloss and DOI retaining layer.
FIG. 1 is a perspective view of an automobile illustrating the front fascia of an automobile having a decorative paint film applied thereto;
FIG. 2 is a front view of an automobile front fascia having a decorative paint film applied thereto;
FIG. 3 is a cross-sectional view of the fascia shown in FIG. 2 taken along line 3-3 of FIG. 2;
FIG. 4 is a cross-sectional view of the decorative paint film laminate of the present invention adhered to a substrate;
FIG. 5 is a cross-sectional view of the decorative paint film laminate of the present invention including a clear coat layer, gloss and DOI retaining layer, a color adjustment layer, and a color coat layer;
FIG. 6 is a schematic illustration of a process for construction of the decorative paint film laminate in accordance with the present invention;
FIGS. 7A-7D are schematic illustrations of the steps in a thermoforming process used to construct a preform; and
FIGS. 8A-8C are schematic illustrations of steps in an injection molding process for forming a composite shaped part.
The present invention will now be described more fully hereinafter with reference to the accompanying drawings. The following description of the preferred embodiment(s) is merely exemplary in nature and is in no way intended to limit the invention, its application, or uses.
The decorative paint film laminate of the present invention eliminates the need for a mask on the outer surface of a paint film in order to make a part, such as an automobile part, having high gloss and distinctness of image (DOI) using paint film technology. The term “mask”, as defined herein, refers to any material that is adhered to, removably or otherwise, to the outer surface of a paint film. Elimination of the need for a mask on the outer surface of a paint film simplifies the manufacturing process during forming and molding processes and also reduces the cost of materials for making a part.
Referring now to the accompanying drawings and initially to FIG. 1, the decorative paint film laminate of the present invention is indicated in FIG. 1 by reference numeral 14 and basically comprises a clear coat layer, a gloss and DOI retaining layer, a color coat layer, an optional primer layer, an optional adhesive layer, and a backing sheet.
FIG. 1 illustrates an automobile 10 having a composite shaped part 12. As shown, the composite shaped part 12 is a complex, contoured three-dimensional front fascia of the automobile 10. The composite shaped part 12 has a decorative paint film laminate 14 applied thereto. Although not limited to such applications, the decorative paint film laminate 14 of the present invention is particularly advantageous for providing a decorative surface on a composite shaped part 12 of an automobile 10. However, those skilled in the art will appreciate that the present invention could be used in a variety of applications requiring a decorative surface having high gloss and DOI.
FIG. 2 is a front view of the composite shaped part 12 having the decorative paint film laminate 14 applied thereto. FIG. 3 is a cross-sectional side view of the composite shaped part 12 comprising a substrate 16 having a decorative paint film laminate 14 applied thereto. As illustrated in FIG. 3, the decorative paint film laminate 14 undergoes different amounts of elongation at different points along the contoured surface of the composite shaped part 12. In one embodiment, the decorative paint film laminate 14 of the present invention has a three-dimensional configuration in which certain areas of the paint film laminate have been subjected to elongation up to, and even in excess of, about 300%, and other areas of the paint film laminate are substantially non-elongated. The decorative paint film laminate 14 of the present invention is capable of maintaining not only a uniform level of gloss but also a high level of gloss, regardless of the amount of elongation experienced by the decorative paint film laminate 14 during a forming or molding process.
FIG. 4 shows a greatly expanded cross-sectional view of a composite shaped part 12 comprising a decorative paint film laminate 14 of the present invention adhered to a substrate 16. The decorative paint film laminate 14 includes a clear coat layer 22, a gloss and DOI retaining layer 23, a color coat layer 24, an optional primer layer 26, an optional adhesive layer 28, and a backing sheet 30.
The decorative paint film laminate 14 of the present invention not only retains both high gloss and DOI during forming and molding processes in the absence of a mask on the outer surface of the paint film but also improves the gloss and DOI of the paint film due to the presence of the gloss and DOI retaining layer. Examples of forming processes include, but are not limited to, thermoforming, cold stretching, and vacuum forming. Examples of molding processes include, but are not limited to, injection molding, compression molding, and blow molding.
Current commercial paint film products utilize a removable, thermoformable mask to minimize the gloss and DOI reduction during the thermoforming or molding processes. In those situations, the mask layer is the outer layer of the decorative paint film laminate. The clear coat layer 22 in the present invention is the outer layer of the decorative paint film laminate 14 during construction of the final product, such as an automobile. Therefore, a benefit of the decorative paint film laminate of the present invention is enhanced gloss and DOI of the paint film despite the absence of a mask layer on the outer surface of the paint film. Thus, the present invention is advantageous not only because no mask is needed, but also because the gloss and DOI of the paint film are enhanced with the presence of the gloss and DOI retaining layer as compared to a paint film with a mask but no gloss and DOI retaining layer. Furthermore, there are no material, manufacturing, labor or other costs incurred due to the presence and ultimate removal of a mask from the clear coat layer. When a mask is used, the mask layer must be releasably bonded to the underlying decorative paint film and must be stripped away from the underlying layers in a single piece. The decorative paint film laminate of the present invention eliminates the need for a mask.
The weatherable outer surface of a standard paint film has an initial 20 and 60 degree gloss of at least about “60” in dry film form. After thermoforming the dry film laminate, the 20 degree gloss and 60 degree gloss may decline by 50% or more in high stretch applications. Adhering a mask layer to the paint film may improve the 20 degree and 60 degree gloss retention but still shows gloss loss during the forming process, especially the 20 degree gloss. Industry standards typically require that the 20 degree gloss and 60 degree gloss be above 60 for many applications. However, the desired final gloss value of the paint film will vary depending on the application. In contrast, the decorative paint film laminate of the present invention has enhanced high gloss and DOI as compared to a standard paint film laminate with a mask.
FIG. 4 and FIG. 5 are greatly expanded cross-sectional views of the decorative paint film laminate 14 of the present invention. As shown in FIGS. 4 and 5, the decorative paint film 18 may comprise a clear coat layer 22, a gloss and DOI retaining layer 23, an optional color adjustment layer 27 (shown in FIG. 5), and a color coat layer 24. The clear coat layer 22 is formed from a substantially transparent weatherable, UV protective polymer composition selected to provide a film which will not significantly fade, peel, crack, or chalk when exposed to the environment for the intended life of the part 12 or fulfill other characteristics desired such as toughness, scratch resistance, and marr resistance, for example. Additionally, the clear coat layer 22 must be formable from a two-dimensional surface to a three-dimensional surface without objectionable loss of appearance or performance properties. The clear coat layer 22 may include, but is not limited to: urethane polymers such as polyurethane; acrylic polymers; fluoropolymers such as polyvinyl fluoride (PVF) and polyvinylidene fluoride (PVDF); and alloys of a fluoropolymer and an acrylic polymer. TEDLAR® manufactured by DuPont of Wilmington, Del. is an example of a polyvinyl fluoride. FLUOREX® films manufactured by Soliant, LLC of Lancaster, S.C. are examples of alloys of a fluoropolymer and an acrylic polymer such as a PVDF/acrylic alloy. The clear coat layer 22 may include other additives including, but not limited to, UW screeners, antioxidants, heat stabilizers, and other conventional additives. Preferably, the clear coat layer 22 is about 0.3 mils to about 3 mils in thickness, more preferably from about 0.5 mils to about 2.5 mils in thickness. Preferably, the clear coat layer is applied in the form of a solution.
In one embodiment, the outermost layer of the paint film 18, such as the clear coat layer 22, comprises an alloy of a fluoropolymer and an acrylic polymer. For example, the alloy of fluoropolymer and acrylic polymer may comprise about 30 to about 70 weight percent fluoropolymer, and about 30 to about 70 weight percent acrylic polymer on a dry solids basis. A commercially available fluoropolymer is KYNAR SL manufactured by Arkema, Inc. of Philadelphia, Pa. Commercially available acrylic polymers are Elvacite 2041 manufactured by INEOS Acrylics of Cordova, Tenn. and Acryloid A11 manufactured by Rohm & Haas of Philadelphia, Pa.
The gloss and DOI retaining layer 23 serves as an “internal mask” such that the decorative paint film laminate 14 has improved high gloss and DOI as compared to the use of a mask on the outer surface of a paint film. The composition of the gloss and DOI retaining layer 23 is preferably selected such that the tensile strength of the gloss and DOI retaining layer is the same as or higher than the higher of the tensile strength of either the clear coat layer or the color coat layer at the thermoforming temperature. More preferably, the gloss and DOI retaining layer has a tensile strength that is higher than the higher of the tensile strength of either the clear coat layer or the color coat layer at the thermoforming temperature. The thermoforming temperature varies depending upon the composition of the materials selected for use in the layers. However, the thermoforming temperature would be known to one of ordinary skill in the art for a given material. The term “thermoforming temperature”, as used herein, refers to the temperature at which a thermoplastic material is shaped or formed. Therefore, materials suitable for use in the gloss and DOI retaining layer may include, but are not limited to, urethanes, acrylics, fluoropolymers, nylons, alloys or combinations thereof An example of a preferred urethane includes, but is not limited to, polyurethane. Examples of preferred fluoropolymers include, but are not limited to, polyvinylidene fluoride (PVDF), polyvinyl fluoride (PVF) and alloys or combinations thereof TEDLAR® is an example of a polyvinyl fluoride manufactured by DuPont of Wilmington, Del.
The gloss and DOI retaining layer may be applied, for example, in the form of a dispersion or a solution. The gloss and DOI retaining layer is preferably cast or coated. The gloss and DOI retaining layer is preferably about 0.2 mils to about 2.0 mils in thickness.
A cross-linking agent may be used in the gloss and DOI retaining layer. Examples of cross-linking agents include, but are not limited to, poly-aziridine, poly-isocyanate, blocked poly-isocyanate, and amino cross-linking agents. XAMA 7 is an example of a commercially available poly-aziridine cross-linking agent manufactured by Bayer Corp. of Pittsburgh, Pa. API-972 is an example of a commercially available blocked isocyanate manufactured by Advanced Polymer, Inc. of Carlstadt, N.J. The level of cross-linking agent may vary from 0.1 to 4.0 percent of the solids of the formulation.
Commercially available examples of polyurethane polymers may include, cross-linkable polyurethane dispersions such as HYBRIDUR 580 and HYBRIDUR 870, both manufactured by Air Products of Allentown, Pa.; HD 4669 and HD 2113, both manufactured by C.L. Hauthaway and Sons Corporation of Lynn, Mass.
Commercially available examples of acrylic polymers used for solvent casting may include, but are not limited to, ELVACITE 2041, ELVACITE 2014 and ELVACITE 2552, all of which are manufactured by INEOS Acrylics of Cordova, Tenn.; and Br85, manufactured by Dianal America, Inc. of Pasadena, Tex.
Commercially available acrylic dispersions suitable for use in this invention include, but are not limited to, AS 2505 and AS 2511, both manufactured by Alberdingk Boley, Inc. of Charlotte, N.C.
The color coat layer 24 is formed of a polymer composition comprising a uniformly dispersed pigment and/or metallic flakes or pearlescents to provide the appearance necessary for exterior automobile use. Preferably, the color coat layer 24 may comprise a polymer selected from the group consisting of urethanes such as polyurethane, acrylics, fluoropolymers such as PVDF, and alloys and combinations thereof FLUOREX® films manufactured by Soliant, LLC of Lancaster, S.C. are examples of alloys of a fluoropolymer and an acrylic polymer. The color coat layer 24 may include pigments, dyes, and/or flakes to enhance visual appearance and improve weatherability. Preferably, the color coat layer 24 is about 0.2 to about 3 mils in thickness, more preferably 0.2 mils to 2.5 mils in thickness.
If desired, a color adjustment layer 27 may be added between the clear coat layer 22 and the color coat layer 24 to enhance visual appearance, preferably between the gloss and DOI retaining layer and the color coat layer. The color adjustment layer 27 can be applied in coating form and may include pigments, dyes and/or flakes or applied as a graphic design using printing methods such as gravure, rotary screen, flat bed step-and-repeat screen, ink jet, flexographic or other printing techniques. This layer is typically used for appearance purposes to match three layer paint systems.
The primer layer 26 is an optional layer that improves adhesion between the color coat layer 24 and the adhesive layer 28. The primer layer 26 preferably comprises an acrylic polymer prepared in solution using any compatible solvent known in the art, such as toluene. In one embodiment, the primer layer 26 is prepared from a solution comprising about 50 to about 85 weight percent acrylic composition and about 5 to about 20 weight percent solvent. An acrylic polymer suitable for use in the primer layer 26 is acrylic adhesive 68070 manufactured by DuPont. The primer layer 26 may be opaque, colored or clear. Opaque is defined as less than 1 percent transmission at a wavelength of less than 400 nm. The primer layer 26 is preferably about 0.2 to about 2 mils in thickness. The primer layer 26 may be colored or opaque to protect the underlying backing sheet 30 from damage caused by UV exposure. Pigments, such as carbon black, titanium oxide, and mixtures thereof, may be added to impart color to the acrylic polymer composition used in the primer layer 26. Additionally, additives such as UV screeners, antioxidants, and heat stabilizers may be added to the primer layer 26.
An optional adhesive layer 28 may be used to adhere the decorative paint film 18 to a backing sheet 30. The composition of the adhesive depends upon, among other factors, the chemistry of color layer and the type of backing sheet used. For certain substrates such as ABS and polystyrene substrates, the presence of the adhesive layer is often not preferred. However, for other backing sheets such as thermoplastic polyolefin (TPO), an adhesive layer may be preferred. An example of a suitable adhesive for TPO is an acrylic primer/CPO adhesive.
The adhesive layer 28 may include, but is not limited to, one or more layers of urethane adhesives, acrylic adhesives, acrylic adhesives with cross linkers, chlorinated polyolefins and mixtures thereof Preferably, a mixture of a chlorinated polypropylene and a higher molecular weight chlorinated polyolefin is used. In one embodiment, the adhesive layer 28 is prepared from a mixture of about 5 to about 20 weight percent chlorinated polypropylene and about 1 to about 10 weight percent of a higher molecular weight chlorinated polypropylene formed in solution. A compatible solvent known in the art, such as toluene, is present in an amount of about 60 to about 80 weight percent. A chlorinated polypropylene suitable for use with the present invention is HARDLEN 13 LP manufactured by Advanced Polymer. A higher molecular weight chlorinated polyolefin suitable for use with the present invention is SUPERCHLON 822S manufactured by CP/Phibrochem of Fort Lee, N.J. The adhesive layer 28 should preferably be capable of stretching about 20 to about 600 percent.
Due to the substantial elongation capability of the adhesive layer 28, the adhesive layer maintains the necessary adhesive strength to prevent delamination of the decorative paint film 18 from the backing sheet 30 over a wide temperature range.
An epoxy component, such as EPON 828RS manufactured by Shell Chemical, may be added in small amounts (approximately about 0.1 to about 2.0 weight percent on a dry solids basis) as an acid scavenger. As with the primer layer 26, the adhesive layer 28 may be colored or opaque to protect the underlying thermoformable backing sheet 30 from damage caused by UV exposure. Pigments, such as carbon black, titanium oxide, and mixtures thereof, may be added to impart color to the polymer composition used in the adhesive layer 28. Additives including, but not limited to, UV screeners, antioxidants, and heat stabilizers may be added to the adhesive layer 28. Preferably, the adhesive layer 28 is about 0.2 to about 2 mils in thickness.
The backing sheet 30 bonds the decorative paint film 18 of the decorative paint film laminate 14 to the substrate 16. In addition, the backing sheet 30 provides bulk and/or rigidity for handling the decorative paint film laminate 14 as a thermoformed preform. The backing sheet 30 also provides thickness to prevent glass fibers, fillers or other sources of visual roughening or “orange peel” from the substrate 16 from affecting the visual appearance of the decorative paint film laminate 14. The backing sheet 30 must bond well with both the substrate 16 and the adhesive layer 28. The backing sheet 30 may be of a material including, but not limited to, thermoplastic polyolefin, acrylonitrile-butadiene-styrene (ABS) terpolymer, polypropylene, polyethylene, thermoplastic polyimide, polyethylene oxide, polycarbonate, polyvinyl chloride, polystyrene, styrene/polyphenylene oxide (NORYEL), polybutylene terephthalate, nylon, PETG copolyester, and mixtures, laminates, copolymers and other combinations thereof, depending on the material used as the substrate 16.
FIG. 6 illustrates a process for constructing the decorative paint film laminate 14 of the present invention. As. shown, a film carrier 33 is advanced from a supply roll 38 through a series of process steps. The film carrier 33 preferably comprises a polyester casting film having a high gloss surface the film carrier 33 is important for high gloss applications because it imparts high gloss and DOI to the decorative paint film laminate 14. Advantageously, the film carrier 33 comprises polyethylene terephthalate (PET) in a grade without slip additives. The film carrier 33 is about 1 to about 3 mils in thickness, preferably about 2 mils in thickness.
The film carrier 33 passes through a first coating station 40. If a decorative paint film 18 having multiple coatings is desired, the first coating station 40 may deposit the clear coat layer 22. The clear coat layer 22 then passes through a dryer 41. Next, the gloss and DOI retaining layer is deposited and dried by dryer 43. Thereafter, a color coat layer 24 is deposited on the gloss and DOI retaining layer 23 using coating station 44. The color coat layer 24 is then dried using dryer 46. Optionally, the dried color coat layer 24 can be subjected to a corona treatment (not shown).
The coating stations 40, 42, and 44 may utilize any conventional coating or casting techniques, such as reverse roll coating or slot die coating techniques. Slot die coating methods are preferred. The dryers 41, 43, and 46 may utilize any conventional drying technique. Preferably, the dryers 41, 43, and 46 are ovens having multiple heating zones wherein each successive heating zone operates at a progressively higher temperature. For example, an oven having four to six heating zones ranging in temperature from about 200° F. to about 425° F. may be used. Alternatively, dryer 41 may be eliminated from the process such that the gloss and DOI retaining layer is applied to the clear coat 22 while the clear coat is still wet using a “wet on wet” coating technique.
After the decorative paint film 18 is applied to the film carrier 33, the film carrier advances to a primer coating station 48, where the primer layer 26 is deposited onto the exposed layer of the decorative paint film 18. The primer layer 26 is then dried using dryer 49. Thereafter, the film carrier advances to an adhesive coating station 50, where the adhesive layer 28 is deposited onto the primer layer 26. Thereafter, the adhesive layer 28 is dried using dryer 51. The primer coating station 48 and adhesive coating station 50 may utilize any conventional coating or casting technique, such as reverse roll coating or slot die coating techniques. The dryers 49 and 51 may utilize any conventional drying technique. Alternatively, dryer 49 may be eliminated from the process such that the adhesive layer 28 is applied to the primer layer 26 while the primer layer is still wet using a “wet on wet” coating technique known by one of ordinary skill in the art. Alternatively, the CPO/Primer can be coated directly on PET in a wet-on-wet process and then laminated using heat and pressure to the color layer of the paint film.
A backing sheet 30 is advanced from a supply roll 52 and laminated to the adhesive-coated surface of the film carrier 33. Optionally, the backing sheet 30 can be subjected to a corona treatment (not shown) prior to lamination. The resulting laminate is collected by product roll 54.
The decorative paint film laminate 14 of the present invention can be adhered to a supporting substrate 16 in accordance with known laminating or bonding techniques. Illustrative examples of supporting substrates 16 include, but are not limited to, metal, wood, and molded polymer substrates. As explained above, exterior automobile parts are particularly suitable as the substrate 16. Suitable polymers for use as the substrate 16 include, but are not limited to, thermoplastic olefin, acrylonitrile-butadiene-styrene terpolymer, polypropylene, thermoplastic polyimide, polyethylene oxide, polycarbonate, polyvinyl chloride, polystyrene, styrene/polyphenylene oxide (NORYEL), polybutylene terephthalate, nylon, PETG copolyester, Sheet Molding Compounds (SMC), RIM urethanes, mixtures, laminates, and copolymers thereof
The decorative paint film laminate 14 may be applied to the substrate 16 by a variety of methods. These methods include, but are not limited to, compression molding, such as thermoplastic or thermoset compression molding, injection molding and the like. In an injection molding process, the decorative paint film laminate 14 may be preformed as described below or placed in the mold as a substantially flat sheet. If the paint film laminate 14 is placed in the mold without preforming, the heat and/or pressure of the molding process conforms the paint film laminate to the desired shape.
FIGS. 7A-7D illustrate the steps in a thermoforming process. Thermoforming is often used to create a preform in a three-dimensional configuration that roughly approximates the three-dimensional configuration of the final product. However, other forming processes known in the art may be used. The preform is then placed in a mold for in-mold surfacing of a desired substrate 16 to form the final product. FIG. 7A shows heating of the decorative paint film laminate 14 of the present invention by heating elements 70. The heating step softens and increases the extensibility of the decorative paint film laminate 14 so that the paint film laminate will readily conform to the contoured outer surface of the mold 74. As shown in FIG. 7C, the mold 74 is brought into contact with the heated decorative paint film laminate 14 and a vacuum is drawn to encourage conformity of the paint film laminate 14 to the contours of the mold 74. Thereafter, the mold 74 is removed from the decorative paint film laminate 14 and the paint film laminate is allowed to cool and harden into the three-dimensional configuration.
FIGS. 8A-8C illustrate steps in an in-mold surfacing process. As shown in FIG. 8A, the thermoformed decorative paint film laminate 14 is placed in the mold cavity 78 of an injection mold 76. The decorative paint film laminate is placed in the mold cavity 78 with the clear coat layer 22 facing the inner surface of the injection mold 76. Alternatively, the decorative paint film laminate 14 may be placed in the mold cavity 78 as a flat, two-dimensional insert rather than as a preform. The injection mold 76 is shut and a moldable polymer 82 is introduced into the mold 76 through the injection mold barrel 80. The polymer 82 bonds to the backing sheet 30 and conforms to the contoured shape of the mold cavity 78. Thereafter, the moldable polymer 82 is allowed to cool and harden into a composite shaped part 12 comprising a substrate 16 bonded to a decorative paint film laminate 14, as shown in FIG. 8C.
Clear coat compositions were prepared in accordance with the present invention and are identified as Clear Coat Compositions A and B, respectively. The component amounts are based upon the total weight of the composition being on a 1 gram basis.
Clear Coat Composition A
TINUVIN 292 0.01184 g
TINUVIN 928 0.01184 g
ACRYLOID A11 0.15387 g
ELVACITE 2041 0.03957 g
KYNAR SL 0.08288 g
MEK 99.4% 0.59500 g
Cyclohexanone 0.10500 g
For the above formulation, TINUVIN 292 and TINUVIN 928 were added in the MEK/Cyclohexanone solvent blend first. The additives were stirred until dissolved. ACRYLOID A11, ELVACITE 2042 and KYNAR SL were added into the mix and stirred with high shear until the resins were dissolved.
Clear Coat Composition B
KYNAR SL 0.09220 g
TINUVIN 928 0.00946 g
TINUVIN 292 0.00946 g
ACRY 68080 0.43480 g
Ethyl Acetate 0.45404 g
For the above formulation the TINUVIN 292 and TINUVIN 928 were added in Ethyl Acetate solvent first. The additives were stirred until dissolved. KYNAR SL was then added into the mix and stirred with high shear until the resins were dissolved. ACRY 68080 was then added into the mix slowly with high shear.
Gloss and DOI Retaining Compositions were prepared in accordance with the present invention and are identified as Gloss and DOI Retaining Compositions A, B, C, and D, respectively. The component amounts are based upon the total weight of the composition being on a 1 gram basis.
Gloss and DOI Retaining Composition A
HD 4669 0.3902 g
HD 2113 0.5854 g
API-792 0.0244 g
In Composition A, the HD4669 and HD2113 were mixed, and then the cross-linker API-792 was added and mixed for another 15 minutes.
Gloss and DOI Retaining Composition B
DPNB 0.12675 g
HYBRIDUR 580 0.77773 g
Deionized Water 0.08385 g
XAMA-7 0.01167 g
Gloss and DOI Retaining Composition C
HYBRIDUR 580 0.69996 g
AS 2505 0.07777 g
Compositions B and C were prepared as set forth below in Composition D by preparing a Pre-Mix with Diproplene Glycol Butyl Ether (DPNB).
Gloss and DOI Retaining Composition D
Glycol Ether DPNB 0.11776 g
SURFYNOL DF-58 0.00140 g
BYK 346 0.00435 g
INHB TINUVIN 0.00992 g
BYK 333 0.00062 g
HYBRIDUR 580 0.72329 g
Deionized Water 0.13181 g
CYMEL 385 0.01085 g
Gloss and DOI Retaining Composition D was prepared by first preparing a Pre-Mix as follows. DPNB solvent commercially available from Lyondell Chemical Company of Houston, Tex. was weighed into an appropriately-sized, grounded container. While stirring vigorously with high shear, TINUVIN 384 commercially available from Ciba Specilaty Chemicals of Tarrytown, N.Y. was added to the container and measured accurately. Stirring was continued and BYK 346 commercially available from BYK Chemie of Germany was added. The container was rinsed with mix, and the rinse was added. Stirring was continued, and BYK 333 commercially available from BYK Chemie of Germany was added. The container was rinsed with mix, and the rinse was added. Stirring was continued, and SURFYNOL DF-58 commercially available from Air Product and Chemicals of Allentown, Pa. was added. The container was rinsed with mix, and the rinse was added. The Pre-Mix was stirred for a minimum of 15 minutes or until all components were completely dissolved.
After preparation of the Pre-Mix, HYBRIDUR 580 commercially available from by Air Products of Allentown, Pa. was weighed out. Using a high shear mixer with an appropriately sized F-style Cowles blade (Vat-use 16″ blade, Drum-use 8″ blade), stirring was begun with a good vortex (˜700 RPM). While stirring, the specified amount of the DPNB Pre-Mix was slowly poured. The DPNB caused the viscosity to rise, so the mixer speed was increased when adding the Pre-Mix, as necessary. One-third of the specified amount of deionized water was added. The vat was tightly covered with clear polyethylene film, and the mixture was stirred until the temperature reached 85° F. The time until temperature was reached was recorded. CYMEL 385 commercially available from Cytec Industries Inc. of West Paterson, N.J. was added and stirring was continued. The remaining two-thirds of the deionized water was added and stirred for thirty additional minutes. The vat was kept covered with polyethylene film. The mix temperature was monitored closely and was not allowed to exceed 85° F. The completed mix required a minimum sit time of 72 hours prior to coating.
The following color coat compositions were prepared by starting with a clear base. An example of the clear base for the color coat is set forth below.
Clear Base for the Base Coat
ELVACITE 2042 0.24000 g
MEK 99.4% 0.42000 g
XYLENE 0.17165 g
TINUVIN 123 0.00278 g
TINUVIN 900 0.00557 g
ELVACITE R4402 0.16000 g
Black Color Formulation
ACRY BLK B14276-M139 0.10666 g
ACRY WH W14276 M70 0.00444 g
ACRYLIC CLEAR BASE 0.88890 g
White Color Formulation
ACRY WH W14276 M70 0.19977 g
ACRY 29Y1038 TRANS YELL 0.00111 g
ACRYLIC CLEAR BASE 0.79912 g
D4D Acrylic Glossy Silver
ACRYLIC CLEAR BASE 0.90400 g
ALUM PASTE 3201 0.08000 g
DISP ACRY WH W14276 M70 0.01200 g
ACRY BLK B14276-M139 0.00400 g
Example 4 is illustrative of the preparation of a decorative paint film laminate and the thermoforming process.
The paint film samples (clear coat/color coat or clear coat/gloss retaining layer/color coat) were made from a production machine of Soliant, LLC of Lancaster, S.C. TPO adhesive was also coated onto the paint film on the production machine. The laminate samples were prepared by laminating the paint film with TPO adhesive to 30 mil TPO substrates using a lab laminator manufactured by Talboys Engineering Company of Emerson, N.J. with the hop nip temperature of 360° F. The lamination speed used was about 10 ft/min. The laminates were then thermoformed over a wood body side mold (Toyoto, 770 N body side mold) at 330° F. using a thermoformer manufactured by ZMD International, Inc, Model HD 333. Ninety percent (90%) of the maximum heat output was used for both top and bottom heat. The temperature was measured by an IR gun and from the substrate surface.
Gloss and DOI were recorded before and after thermoforming. The gloss was measured by the Micro-Tri-Gloss meter manufactured by BYK Gardner located in Columbia, Md. The DOI reading was obtained by using the I2R Glow Box, Model GB11-8 GM, manufactured by Instrument for Research and Industry, located at Cheltenham, Pa.
Table 1 sets forth the recorded gloss and DOI measurements and provides a comparison of standard paint films with and without a mask, relative to the paint films of the present invention with and without a gloss and DOI retaining layer. The mask used for the experiments was Soliant Premask commercially available from Soliant, LLC of Lancaster, S.C.
Before thermoforming After thermoforming
20° Gloss 60° Gloss DOI (%) 20° Gloss 60° Gloss DOI (%)
Standard FLUOREX ® Paint 63 76 80 21 67 10
Film w/o mask
Standard FLUOREX ® Paint 63 76 80 52 76 60
Film with mask
Paint Film without Gloss and 80 86 80 31 78 10
DOI Retaining Layer
Paint Film with Gloss and 74 83 90 68 83 90
Standard FLUOREX ® Paint 68 90 60 30 79 0
Standard FLUOREX ® Paint 68 90 60 50 87 20
Paint Film without Gloss and 84 100 70 34 94 0
Paint Film with Gloss and 81 100 80 79 100 50
Standard FLUOREX ® Paint 71 89 70 39 82 10
Film w/out mask
Standard FLUOREX ® Paint 71 89 70 47 83 20
Paint Film without Gloss and 78 89 70 19 66 0
Paint Film with Gloss and 77 95 70 72 95 40
The clear coat for the standard FLUOREX® paint film of Table 1 was made with the following formulation:
ELVACITE 2042 0.11920 g
KYNAR 500 0.30650 g
DB ACETATE 0.18930 g
DMP DIMETHYL PHTHALATE 0.18930 g
XYLENE 0.18940 g
TINUVIN 900 0.00630 g
The color coat for the standard paint film used the above formulation as a clear base. The clear coat for paint film with and without gloss retaining layer used the formulation shown in Clear Coat Composition B. The gloss retaining layer used the formulation shown in Gloss and DOI Retaining Composition D. The clear base used for the color coat for the paint film with and without gloss retaining layer was the same as the one shown. The color formulations for each of the colors (Ruby Red, Bright Silver and Tarnish Silver) are commercially available from Soliant, LLC of Lancaster, S.C.
Table 1 demonstrates that the Paint Film with Gloss and DOI Retaining layer offers an improvement over the paint film with a mask. It is significant that the paint films with the Gloss and DOI retaining layer are able to get in the lower end of the 20 degree gloss range for traditional paint, which even paint films with a mask have been unable to achieve. Traditional paints typically have a 70+ number for 20 degree gloss.
US3111450 Feb 1, 1961 Nov 19, 1963 Armstrong Cork Co Polyvinyl fluoride film capable of being adhesively secured and method
US3458391 Jun 27, 1966 Jul 29, 1969 American Cyanamid Co Plastic laminates
US3459834 Sep 21, 1966 Aug 5, 1969 American Cyanamid Co Transparent molding compositions comprising methacrylate polymers blended with a minor amount of poly(vinylidene fluoride)
US3582501 Nov 21, 1958 Jun 1, 1971 Union Carbide Corp Polyurethane foams and process of making them
US4275099 Nov 5, 1979 Jun 23, 1981 Dunmore Corporation Metalized polyester resin laminate
US4678690 Jan 10, 1986 Jul 7, 1987 Rexham Corporation Premasked decal
US4868030 * Aug 4, 1988 Sep 19, 1989 General Motors Corporation Article covered with painted carrier films
US4936936 * Aug 30, 1988 Jun 26, 1990 E. I. Du Pont De Nemours And Company Method of making thermoplastic acrylic polymer coated composite structure
US5001000 * Feb 13, 1990 Mar 19, 1991 E. I. Du Pont De Nemours And Company Process for forming a composite structure of thermoplastic polymer and sheet molding compound
US5026448 Apr 3, 1989 Jun 25, 1991 Reafler Gerald G Method of forming a glossy basecoat-clearcoat surface on a substrate
US5108836 May 22, 1989 Apr 28, 1992 Rexham Industries Corp. Weatherable protective surfacing film
US5122560 * Dec 12, 1989 Jun 16, 1992 E. I. Du Pont De Nemours And Company Coating composition of polyesterurethane and polyisocyanate crosslinking agent
US5132164 Oct 10, 1990 Jul 21, 1992 Denki Kagaku Kogyo Kabushiki Kaisha Fluorine resin type weather-resistant film
US5215826 Sep 25, 1990 Jun 1, 1993 Rexham Industries Corp. Surfacing film with thermoformable carrier layer
US5268215 * Oct 25, 1991 Dec 7, 1993 Eastman Kodak Company Basecoat-clearcoat film
US5316608 Jan 27, 1992 May 31, 1994 Rexham Industries Corp. Weatherable protective surfacing film
US5342666 Oct 1, 1992 Aug 30, 1994 Rexham Industries Corp. Injection molded plastic article with integral weatherable pigmented film surface
US5352532 Aug 26, 1992 Oct 4, 1994 Glass Alternatives Corp. Panel and method of making same
US5514427 Jun 28, 1994 May 7, 1996 Rexam Industries Corp. Injection molded plastic article with integral weatherable pigmented film surface
US5518786 * Jul 21, 1994 May 21, 1996 Avery Dennison Corporation Exterior automotive laminate with pressure sensitive adhesive
US5536539 May 8, 1995 Jul 16, 1996 Rexam Industries Corp. Injection molded plastic article with integral weatherable pigmented film surface
US5564249 Feb 22, 1993 Oct 15, 1996 Borys; Tadeusz Automotive trim piece
US5707697 Mar 13, 1995 Jan 13, 1998 Avery Dennison Corporation Dry paint transfer product having high DOI automotive paint coat
US5916643 Apr 7, 1995 Jun 29, 1999 Avery Dennison Corporation Dry paint transfer-laminated body panels having deep-draw high DOI automotive paint coat
US5960527 May 15, 1997 Oct 5, 1999 Rexam Industries Corp. Method of injection molding plastic automobile body parts with integral weatherable pigmented film surface
US5968657 Aug 18, 1997 Oct 19, 1999 3M Innovative Properties Company Paint film assembly with masking film and method of making same
US5976677 * Dec 29, 1997 Nov 2, 1999 Mazda Motor Corporation Surface coating and method of applying the same
US5985079 * Mar 28, 1996 Nov 16, 1999 Rexam Industries Corp. Flexible composite surfacing film and method for producing same
US6083335 Aug 4, 1999 Jul 4, 2000 3M Innovative Properties Company Paint film assembly with masking film and method of making same
US6096396 Jan 21, 1998 Aug 1, 2000 Rexam Industries Corp. Decorative sheet material suitable for use as a flexible weatherable paint film or decal
US6180195 Jun 29, 1999 Jan 30, 2001 Rexam Industries Corp. Automobile body formed of interconnected molded plastic articles
US6287672 * Mar 12, 1999 Sep 11, 2001 Rexam, Inc. Bright metallized film laminate
US6319438 * Oct 13, 1999 Nov 20, 2001 Guardian Automotive Trim, Inc. Extruded automotive trim and method of making same
US6399193 * Nov 5, 1999 Jun 4, 2002 The University Of Massachusetts Lowell Surfacing laminate with bonded with pigmented pressure sensitive adhesive
US6423778 * Jun 30, 1999 Jul 23, 2002 Basf Corporation Process for coating olefinic substrates
US6440546 * Oct 13, 1999 Aug 27, 2002 Ream Industries Corp. Gloss-adjusting mask layer with particulate filler
US6475616 Nov 29, 2000 Nov 5, 2002 3M Innovative Properties Company Paint replacement appliques
US6565955 * Jun 15, 2001 May 20, 2003 Soliant Llc Bright indium-metallized formable film laminate
US6824818 * Dec 27, 2001 Nov 30, 2004 Soliant Llc Wet on wet process for producing films
US7132142 * Jun 9, 2003 Nov 7, 2006 Avery Dennison Corporation Dry paint transfer laminate for use as wall covering
US7297397 * Jul 22, 2005 Nov 20, 2007 Npa Coatings, Inc. Method for applying a decorative metal layer
US20010051255 * Mar 23, 2001 Dec 13, 2001 Fields Thomas R. Method of forming bright metallized film laminate
US20020048665 * Jun 15, 2001 Apr 25, 2002 Fields Thomas R. Bright indium-metallized formable film laminate
US20020050665 Aug 31, 2001 May 2, 2002 Avery Dennison Corporation Thick sheet lamination product for use in exterior automotive body panels
US20020137872 * Dec 5, 2001 Sep 26, 2002 Schneider John R. Coating compositions providing improved mar and scratch resistance and methods of using the same
US20020192440 * Jun 15, 2001 Dec 19, 2002 Fields Thomas R. Bright tin-metallized formable film laminate
US20030026932 Jul 30, 2001 Feb 6, 2003 Johnson John R. Multilayer laminate
US20030203190 May 16, 2003 Oct 30, 2003 Schmidt James John Fluoropolymer film structures and laminates produced therefrom
US20040018344 Apr 17, 2003 Jan 29, 2004 Watkins Robert F. Retroreflective article comprising water-borne acrylic topcoats
US20040033365 Aug 16, 2002 Feb 19, 2004 Dey Subir K. Composite laminate structures especially useful for automotive trim components, and methods and tie layers employed to make the same
US20040142176 Jan 5, 2004 Jul 22, 2004 General Electric Company Weatherable multilayer articles and method for their preparation
US20040159969 * Jun 9, 2003 Aug 19, 2004 Truog Keith L. Extrusion method of making a dry paint transfer laminate
US20040161567 * Jun 9, 2003 Aug 19, 2004 Truog Keith L. Dry paint transfer laminate
US20040166323 Dec 16, 2003 Aug 26, 2004 General Electric Company Weatherable multilayer articles and method for their preparation
US20040200564 Dec 13, 2002 Oct 14, 2004 The Procter & Gamble Company Articles and methods for applying color on surfaces
US20040247876 * Jan 27, 2004 Dec 9, 2004 Robert Lafave Decorative system composite and method
USRE35894 Oct 21, 1996 Sep 8, 1998 Rexam Industries Corp. Injection molded plastic article with integral weatherable pigmented film surface
USRE35970 Oct 24, 1996 Nov 24, 1998 Rexam Industries Corp. Injection molded plastic article with integral weatherable pigmented film surface
USRE36457 Oct 21, 1996 Dec 21, 1999 Rexam Industries, Corp. Injection molded plastic article with integrated weatherable pigmented film surface
EP0949120A1 * Apr 6, 1999 Oct 13, 1999 Rexam Industries Corp. Film finishing system with design option
WO1994009983A1 Nov 5, 1993 May 11, 1994 Avery Dennison Corporation Exterior automotive laminate with pressure-sensitive adhesive
WO2000051829A2 Feb 16, 2000 Sep 8, 2000 Rexam Industries Corp. Decorative sheet material with chlorinated polyolefin adhesive layer
WO2000078539A1 Jun 21, 2000 Dec 28, 2000 Avery Dennison Corporation Fade printed decorative sheets and methods and apparatus for making the same
1 International Preliminary Report on Patentability for International application No. PCT/US2006/044502 dated May 20, 2008.
2 Written Opinion for International application No. PCT/US2006/044502 (May 18, 2008).
US8434283 * Feb 12, 2010 May 7, 2013 Michelee Bartolo-Howell Extreme edge
US9156298 Mar 15, 2013 Oct 13, 2015 Ford Global Technologies, Llc Method of producing a graphic design on a vehicle body
US9656442 * Dec 2, 2014 May 23, 2017 3M Innovative Properties Company Paint film composites and methods of making and using the same
US20150086762 * Dec 2, 2014 Mar 26, 2015 3M Innovative Properties Company Paint film composites and methods of making and using the same
EP2586592A1 Oct 25, 2012 May 1, 2013 Whirlpool Corporation Method for applying a laminate onto a contoured article
U.S. Classification 428/212, 428/335, 428/421, 428/41.7, 428/475.5, 428/474.4, 428/215, 428/353, 428/334, 428/522, 428/40.1, 428/343, 428/41.5, 428/354, 428/41.6, 428/422, 428/213, 428/423.1
International Classification B32B7/02, B32B27/34, B32B27/30, B32B27/26, B32B27/40
Cooperative Classification B32B2451/00, B32B2605/08, B32B27/08, B32B2310/14, B32B2605/00, B32B2307/738, B32B2307/54, B32B2307/406, B32B2307/4026, B32B2307/40, B32B2255/28, B32B2255/26, B32B2255/10, B32B27/06, Y10T428/31544, Y10T428/31551, Y10T428/3154, Y10T428/31935, Y10T428/31739, Y10T428/31725, Y10T428/31504, Y10T428/14, Y10T428/28, Y10T428/1462, B44C1/105, Y10T428/1471, Y10T428/24967, B05D7/576, B05D1/286, Y10T428/263, Y10T428/264, Y10T428/1467, B05D7/577, Y10T428/2495, B29C2037/0042, Y10T428/2848, Y10T428/2843, Y10T428/24942, B29C37/0032
European Classification B05D1/28E, B44C1/10B, B32B27/08, B29C37/00C2B
Owner name: SOLIANT LLC, SOUTH CAROLINA
Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SONG, QUAN;FAN, JINGFU;PATTON, JERRY;REEL/FRAME:017264/0087
Owner name: AKZO NOBEL COATINGS INC., ILLINOIS
Free format text: MERGER;ASSIGNOR:SOLIANT LLC;REEL/FRAME:039164/0870