CN102822920B - Capacitor electrode body and its manufacture method and the capacitor employing this electrode body - Google Patents
Capacitor electrode body and its manufacture method and the capacitor employing this electrode body Download PDF
CN102822920B
CN102822920B CN201180016707.6A CN201180016707A CN102822920B CN 102822920 B CN102822920 B CN 102822920B CN 201180016707 A CN201180016707 A CN 201180016707A CN 102822920 B CN102822920 B CN 102822920B
tackifier coating
CN201180016707.6A
CN102822920A (en
近藤敬一
岛本秀树
岛崎幸博
奥泽智宏
2010-03-30 Priority to JP2010-078451 priority Critical
2010-03-30 Priority to JP2010078451 priority
2011-03-28 Application filed by 松下知识产权经营株式会社 filed Critical 松下知识产权经营株式会社
2011-03-28 Priority to PCT/JP2011/001804 priority patent/WO2011121967A1/en
2012-12-12 Publication of CN102822920A publication Critical patent/CN102822920A/en
2016-01-20 Publication of CN102822920B publication Critical patent/CN102822920B/en
Capacitor electrode body of the present invention possesses: have the collector body of conductivity, formation protective layer on the current collector, formation tackifier coating on the protection layer and the polarizability electrode layer be formed on tackifier coating.Protective layer contains oxyhydroxide, and tackifier coating contains electroconductive particle.
Capacitor electrode body and its manufacture method and the capacitor employing this electrode body
The present invention relates to the capacitor electrode body and its manufacture method that use in various electronic equipment, electric equipment, industrial equipment, automobile etc. and the capacitor employing this electrode body.
In recent years, from the view point of environmental protection, develop the capacitor that power when driving vehicle or building machinery is assisted.For the capacitor of such purposes, require that the capacitance of per unit volume is large and internal resistance is little.That is, require that there is high-energy-density and high output density.
Reduce the internal resistance of capacitor to respond this requirement, the structure that the adaptation between collector body and polarizability electrode material is high becomes very important.As polarizability electrode material, usually use the carbon system powder particle that the conductivity such as active carbon are good.
Such as, Patent Document 1 discloses the capacitor electrode body of the adaptation that improve between collector body and polarizability electrode material.Fig. 8 is the profile of the capacitor electrode body in patent documentation 1.
This electrode body has collector body 101, be formed in polarizability electrode layer 102 on collector body 101 and thickening (anchor) coating 103.Tackifier coating 103 is made up of electroconductive particle (such as carbon black) and adhesive, and it is arranged between collector body 101 and polarizability electrode layer 102.In this configuration, the carbon black being arranged on the tackifier coating 103 between collector body 101 and polarizability electrode layer 102 enters into the fine emptying aperture of polarizability electrode layer 102.By forming obtained thickening effect by this, improve the bond strength of polarizability electrode layer 102 and collector body 101.
In addition, tackifier coating 103 is arranged according to the mode of filling the space be present between collector body 101 and polarizability electrode layer 102.Therefore, it is possible to reduce the volume in the space between collector body 101 and polarizability electrode layer 102.These as a result, improve the adaptation of polarizability electrode layer 102 and collector body 101.Thereby, it is possible to make the internal resistance of capacitor reduce.
, even if use the capacitor electrode body of above-mentioned formation like this, the reduction of internal resistance neither be sufficient.Especially, the electric power that the couple capacitors in order to the power-assisted as vehicle or Architectural Equipment increases rapidly carries out discharge and recharge, needs the resistance reduced further between collector body 101 and polarizability electrode layer 102.
In addition, repeatedly carrying out in the process of discharge and recharge as capacitor, the pH value variation of electrolyte, now owing to reacting with the acid gathered in the electrolytic solution or alkali, collector body 101 is corroded.This corrosion is the main cause causing the internal resistance of capacitor electrode body to increase.
Patent documentation 1: Japanese Unexamined Patent Publication 2007-227733 publication
The present invention is a kind of capacitor electrode body reducing D.C. resistance, excellent corrosion resistance; With a kind of capacitor making internal resistance reduce, improve reliability thus.Capacitor electrode body of the present invention possesses: have the collector body of conductivity, the protective layer be formed on above-mentioned collector body, the polarizability electrode layer that forms tackifier coating on the protection layer and be formed on tackifier coating.Protective layer contains oxyhydroxide, and tackifier coating contains electroconductive particle.According to this formation, can provide following capacitor, this capacitor can improve the adaptation between collector body and polarizability electrode layer, suppresses the surface of collector body by acid or caustic corrosion, reduce internal resistance, and reliability is high.
Fig. 1 is the use of partly cut-away's stereogram of the capacitor of the capacitor electrode body of embodiment of the present invention.
Fig. 2 is the generalized section of the capacitor electrode body of embodiment of the present invention.
Fig. 3 is the amplification profile of the electrode body shown in Fig. 2.
Fig. 4 is the cyclic voltammetry curve figure representing the electrode body shown in Fig. 2 and the etching characteristic between plain paper tinsel.
Fig. 5 represents to use the state of the protective layer of the collector body used in the electrode body shown in FT-IR survey map 2 and the curve chart of spectrum that obtains.
Fig. 6 is the schematic diagram of the device used in the manufacture method of the capacitor electrode body of present embodiment.
Fig. 7 is elapsed time after the activate step representing the collector body used in the electrode body shown in Fig. 2 and the collector body surface curve chart for the relation of the contact angle of water.
Fig. 8 is the generalized section of existing capacitor electrode body.
Fig. 1 is the use of partly cut-away's stereogram of the capacitor of the capacitor electrode body of embodiment of the present invention.First, limit with reference to Fig. 1, while be described the example of capacitor of the capacitor electrode body employing present embodiment.This capacitor has capacitor element 1, is at least immersed in electrolyte (not shown), shell 2 and sealing part 3 in capacitor element 1.
The shell 2 of bottomed cylindrical is formed by aluminium.Shell 2 receives capacitor element 1 and electrolyte.The sealing part 3 of rubber embeds the peristome of shell 2.That is, the peristome of sealing part 3 capsul 2.Necking down processing is carried out, by the capsul 2 securely to compression sealing part 3 to inward side near the open end of shell 2.Shell 2 and sealing part 3 form the external packing body of storage capacitor element 1 and electrolyte.
Capacitor element 1 is consisted of wound anode 30A, negative electrode 30B and barrier film 6A, 6B between anode 30A and negative electrode 30B.Anode 30A has collector body 4A and polarizability electrode layer 5A, negative electrode 30B have collector body 4B and polarizability electrode layer 5B.
Collector body 4A is connected with lead-in wire 7A, and collector body 4B is connected with lead-in wire 7B.Lead-in wire 7A, 7B insert the hole 8A be arranged on sealing part 3, hole 8B respectively, are drawn out to outside.Capacitor element 1 is by such structure and external electrical connections.
In the present embodiment, can according to coming like this with lead-in wire 7A, 7B, the anode 30A of capacitor element 1, negative electrode 30B to be connected with outside.In addition, such as, also can form sealing part 3 with aluminium in the same manner as shell 2, the collector body 4A of capacitor element 1 be contacted with sealing part 3, collector body 4B is contacted with shell 2.In such structure, sealing part 3 and shell 2 outside terminal as capacitor element 1 can be used.In this case, by making the insulating elements such as rubber between sealing part 3 and shell 2, sealing part 3 and shell 2 are insulated.
Further, dissolve mode in organic solvent according to by solute with the concentration of regulation, prepare electrolyte.Such as, in solvent ethylene carbonate (EC) and dimethyl carbonate (DMC) mixed by 1:1, ethyl methylimidazole tetrafluoroborate (EDMIBF is contained as solute with the concentration of 1.0 moles/l 4).In addition, solute can use salt, amidine system salt, spiral shell-(1 such as quaternary ammonium salt, phosphorus atoms, sulphur atom that the nitrogen-atoms such as etamon, ethyl trimethylammonium possess multiple substituted radical, 1 ') the spiral shell type salt (spiro-typesalt) such as-bipyrrolidine (spiro-(1,1 ')-bipyrrolidinium).Solvent can use the lactone such as carbonates, gamma-butyrolacton etc. such as propylene carbonate.
Then, limit with reference to Fig. 2 and Fig. 3, while be described the formation of the capacitor electrode body of the technical characteristic as present embodiment, i.e. collector body 4A, polarizability electrode layer 5A and its interface portion.Fig. 2 is the generalized section of the general appearance of the structure of capacitor electrode body for representing present embodiment, and Fig. 3 is its amplification profile.And, in figure 3, for ease of illustrating the state of the capacitor electrode body of present embodiment with understanding, represent active carbon 13 and electroconductive particle 11 with the engineer's scale different from reality.
In addition, in the following description, formation is described as the collector body 4A of the anode 30A of the capacitor electrode body of present embodiment and the formation at polarizability electrode layer 5A and its interface.For forming the collector body 4B of negative electrode 30B and polarizability electrode layer 5B and its interface, it is also identical formation.In addition, only the one side of capacitor electrode body is described in the following description, but also can is that two sides is formation shown below.
As shown in Figure 2, anode 30A by collector body 4A, polarizability electrode layer 5A, make the surface modification of collector body 4A and the protective layer 9 comprising oxyhydroxide formed and tackifier coating 10 are formed.Protective layer 9 and tackifier coating 10 are between collector body 4A and polarizability electrode layer 5A.
The metal element paper tinsel that collector body 4A can use surface to be level and smooth sheet.The plain paper tinsel formed with aluminium is used to be described in the present embodiment.In addition, the metals such as copper, stainless steel, titanium can also be used.In addition, except plain paper tinsel, make the plain paper tinsel etc. of surface roughening also can obtain effect of the present invention even if utilize.As the method for roughening, illustrate etching, sandblasting etc.But, as hereinafter described, when being formed very thin by tackifier coating 10, preferably use plain paper tinsel as collector body 4A.
Protective layer 9 is formed by the collector body 4A under making the surface modification of collector body 4A, making modified state and reaction of moisture.Therefore, the oxyhydroxide contained in protective layer 9 is the compound generated by the metal forming collector body 4A.
For the metal (especially valve metal) that collector body 4A uses, be originally provided with the metallic compounds such as autoxidation epithelium in its surface.To this, when generating the oxyhydroxide contained by protective layer 9, the combination between atoms different to the metallic atom forming this metallic compound and oxygen atom etc. or molecule is cut off.Like this, oxyhydroxide is generated by the metallic atom under the state that makes chemically to be in activate (becoming unstable) and contact with moisture.
Specifically, such as first Corona discharge Treatment is implemented to collector body 4A.Then, make collector body 4A and contact with moisture and form protective layer 9.Such as, after Corona discharge Treatment is carried out to collector body 4A, be coated with water the slurry of the tackifier coating 10 being solvent immediately, protective layer 9 can be formed on collector body 4A thus.Like this, the thickness of the protective layer 9 of formation such as average out to 20nm.
Protective layer 9 is formed throughout the whole surface of collector body 4A.When forming collector body 4A with aluminium, oxyhydroxide contained in protective layer 9 is by composition formula Al xo y(OH) zcompound represented by (X, Y, Z are arbitrary natural number).As Al xo y(OH) zan example, containing AlO (OH) in protective layer 9.The existence of these compounds can be undertaken detecting confirming by surface analyses such as X ray electronic spectroscopy (XPS), Auger electron spectroscopy, fourier transform infrared spectroscopies (FT-IR).
In addition, on the surface of collector body 4A defining protective layer 9, as shape physically, it is the state in the hole (not shown) of tiny concavo-convex (not shown) or wedge shape that there is multiple molecular level.
As shown in Figure 3, on protective layer 9, form the tackifier coating 10 containing electroconductive particle 11 and adhesive 12.Electroconductive particle 11 is such as having the carbon black of high conductivity.As carbon black, special expectation is used in textural stablizing and high conductive acetylene black.Except carbon black, can be also graphite or thermal cracking graphite etc., just can use as long as have high conductivity.
Adhesive 12 plays physically by effect that the electroconductive particle 11 be dispersed in tackifier coating 10 is pinioned each other.As the material forming adhesive 12, owing to using water as the dispersant of slurry, be therefore particularly preferably water-soluble resin, be preferably cellulose derivative, rubber series macromolecule, thermoplastic resin, thermosetting resin etc.Specifically, such as carboxymethyl cellulose, polyvinyl alcohol, polyvinyl butyral resin etc.
Further, electroconductive particle 11 is more than 2 times and less than 10 times relative to the weight rate of adhesive 12.This weight rate is preferably more than 3 times and less than 6 times, is more preferably more than 3 times and less than 5 times.The weight rate of electroconductive particle 11 become greatly more than 10 times time, tackifier coating 10 cannot keep the form as film.Otherwise, when being less than 2 times, because viscosity is high, be difficult to form film.As long as above-mentioned weight rate scope, electroconductive particle 11 just can be made to be dispersed in tackifier coating 10 exactly, in addition, also can guarantee collector body 4A and polarizability electrode layer 5A conducting by electroconductive particle 11.
As shown in Figure 3, electroconductive particle 11 local is imbedded in protective layer 9.The average grain diameter of electroconductive particle 11 is larger than the thickness of protective layer 9.Such as, the thickness of protective layer 9 is about 20nm, and the average grain diameter of electroconductive particle 11 is about 35nm.Therefore, most electroconductive particle 11 is only embedded in a part as shown in Figure 3, and part is in addition present in tackifier coating 10.
As shown in Figure 2 and Figure 3, tackifier coating 10 is formed with polarizability electrode layer 5A.As shown in Figure 3, polarizability electrode layer 5A is formed by the powder of coat activated carbon 13 on tackifier coating 10.And, in figure 3, be only illustrated active carbon 13 as polarizability electrode layer 5A, but except this formation, also can on the basis of active carbon 13 the suitably micropowder such as mixed carbon black.In addition, as active carbon 13, the material being given activate by the gas such as steam or carbon dioxide to coconut husk charcoal, charcoal etc. specifically can be used.
The average grain diameter of active carbon 13 is such as 3 μm, and its average grain diameter than electroconductive particle 11 (35nm) is large.According to the relation of this particle diameter, become the formation that a large amount of electroconductive particle 11 surrounds a particle of active carbon 13.Therefore, the contact point number of the active carbon 13 when the active carbon 13 when being provided with tackifier coating 10 directly will engage with collector body 4A more than polarizability electrode layer 5A with the contact point number of electroconductive particle 11 and collector body 4A.Thereby, it is possible to make the interface resistance between polarizability electrode layer 5A and collector body 4A reduce.
And as shown in Figure 3, in the inside of polarizability electrode layer 5A, the particle being in electroconductive particle 11 enters the state in the space formed each other by active carbon 13 in a large number.Therefore, between the inner peripheral surface that thickening effect acts on active carbon 13 space each other and the outer surface of electroconductive particle 11, improve the bond strength between tackifier coating 10 and polarizability electrode layer 5A.And, in order to further according to like this improving thickening effect, expect by above-mentioned space the average diameter that takes up space when being considered as spherical larger than the average grain diameter of electroconductive particle 11.This is because according to this magnitude relationship, electroconductive particle 11 can enter into above-mentioned emptying aperture thus can obtain the cause of thickening effect.Otherwise when the average grain diameter of electroconductive particle 11 is larger than the average pore size of emptying aperture, electroconductive particle 11 cannot enter into emptying aperture fully and cannot obtain sufficient thickening effect.Therefore, such as, when the average grain diameter of electroconductive particle 11 is 35nm, preferred above-mentioned emptying aperture is larger than 35nm.
Further, electroconductive particle 11 not only enters above-mentioned space, but also enters the inside of the emptying aperture of the active carbon 13 as porous plastid, can improve density of adhering further thus between polarizability electrode layer 5A and tackifier coating 10.This is because the averaged particles of electroconductive particle 11 is made up of the very little particle that tens nanometer is such.Thereby, it is possible to reduce the contact resistance on the interface between polarizability electrode layer 5A and tackifier coating 10.Therefore, the aperture of the emptying aperture on the surface of the average grain diameter of electroconductive particle 11 preferred specific activity charcoal is little.
Below, the effect of the capacitor electrode body of present embodiment is described.First, in the capacitor electrode body and anode 30A of present embodiment, the adaptation of polarizability electrode layer 5A and collector body 4A can be improved.This is the cause of the upper tackifier coating 10 having protective layer 9 due to anode 30A on collector body 4A and be arranged on protective layer 9.
As mentioned above, the pressure when slurry due to tackifier coating 10 is coated with, the electroconductive particle 11 of tackifier coating 10 is pressed in protective layer 9, and local is imbedded in tackifier coating 10.There is the electroconductive particle 11 of state so in a large number.According to this formation, the thickening effect between electroconductive particle 11 and collector body 4A plays a role, and improves the bond strength of tackifier coating 10 and collector body 4A.In addition, as mentioned above, in tackifier coating 10 and polarizability electrode layer 5A, the formation that improve bond strength by thickening effect is also become.These as a result, the adaptation of polarizability electrode layer 5A and collector body 4A is excellent.
Further, be pressed into the part being in the electroconductive particle 11 of the state of imbedding in protective layer 9 directly to contact with collector body 4A.Therefore, ensure that the conducting between collector body 4A and active carbon 13 fully.Further, as mentioned above, because the adaptation between collector body 4A and polarizability electrode layer 5A is excellent, so the interface resistance between collector body 4A and polarizability electrode layer 5A reduces.Thus, when using the capacitor electrode body of present embodiment, the internal resistance of capacitor can be reduced.
And, form protective layer 9 throughout the whole surface of collector body 4A.Therefore, compared with the collector body 4A not forming protective layer 9, the excellent corrosion resistance of the capacitor electrode body of present embodiment.
When not forming the collector body 4A of protective layer 9, on the surface of collector body 4A, generate oxide film thereon as mentioned above.But, because such oxide film thereon is generated by autoxidation, thus on collector body 4A only local or generate oxide film thereon unevenly.And, for not by the part that the oxide film thereon of collector body 4A covers, corrode due to the chemical reaction be immersed between the electrolyte in capacitor element 1.
On the other hand, in the present embodiment, because the protective layer 9 comprising oxyhydroxide is formed throughout the whole surface of collector body 4A, so the corrosion caused by electrolyte contacts with collector body 4A effectively can be prevented.Especially, be the compound be difficult to acid or alkali reaction compared with the oxide such as oxyhydroxide and autoxidation epithelium.Therefore, it is possible to suppress the acid of the generation when the pH value variation of electrolyte or alkali to contact produced corrosion with collector body 4A.
Further, in order to obtain above-mentioned excellent corrosion resistance, preferred protective layer 9 cover as much as possible collector body 4A surface, particularly can with the position of electrolyte contacts.Such as, preferred protective layer 9 covers the surface area more than 70% of collector body 4A.
Like this, the surface of collector body 4A is formed the protective layer 9 comprising the oxyhydroxide of excellent corrosion resistance.And the electroconductive particle 11 be included in tackifier coating 10 is imbedded in protective layer 9.Therefore, guarantee the conductivity of collector body 4A and electroconductive particle 11, and thickening effect can be played.
Here, Fig. 4 is used to be described the effect that the corrosion of the capacitor electrode body of present embodiment reduces.Fig. 4 is the cyclic voltammetry curve figure of the etching characteristic of the electrode body representing present embodiment, and the longitudinal axis represents kinetic current, and transverse axis represents corrosion potential (taking reference electrode as the potential difference that reference measurement arrives).
Further, in the measurement of the etching characteristic of capacitor electrode body, electrochemical measuring method is used to measure.In this measurement, use three-electrode method, specifically, use the silver/silver ion electrode of nonaqueous solvents as reference electrode, use the platinum line of coiled type as to pole, use the anode 30A of the capacitor electrode body of the present embodiment of 2cm × 2cm size as work pole, these electrodes are connected with potentiostat, and dipping in the electrolytic solution, potential scanning speed is set to 10mV/ minute to measure etching characteristic.As electrolyte, be used in contain EDMIBF with the concentration of 1.0 moles/l in the solvent of 1:1 mixing EC and DMC 4solution.In addition, in order to compare, use plain paper tinsel as work pole, measuring etching characteristic.
In the etching characteristic of the plain paper tinsel shown in the solid line A of Fig. 4, kinetic current detected under the current potential near 0.3V, this kinetic current starts to rise.It can thus be appreciated that plain paper tinsel corrodes under the current potential of more than 0.3V.
On the other hand, near the 0.3V of kinetic current plain paper tinsel being detected, the kinetic current of the anode 30A shown in solid line B do not detected, but near 1.7V, just kinetic current detected and the rising of this kinetic current.It can thus be appreciated that, for anode 30A, corrode under the current potential of more than 1.7V.Like this, anode 30A is better than plain paper tinsel significantly in corrosion resistance.Therefore, the formation of capacitor electrode body according to the present embodiment can reduce corrosivity, can also prevent chronically by the reduction of corroding the capacitor performance caused.
Then, limit is with reference to Fig. 5, while the result obtained using the state of FT-IR measuring and protecting layer 9 is described.Fig. 5 represents to use FT-IR to measure the state of the protective layer 9 of collector body 4A and the curve chart of spectrum that obtains.In addition, in order to compare, also illustrate the measurement result of the collector body formed by the plain paper tinsel not forming protective layer 9.Based on ATR method (ATR), measured by primary event.Further, the contact angle of collector body 4A is 17 °.
In collector body 4A, observe 930cm -1the peak C at place and 1100 ~ 1200cm -1the peak value D at place.Peak C represents Al 2o 3existence, peak value D represents Al xo y(OH) zexistence, especially represent γ-Al xo y(OH) zexistence.Here, preferred peak than D/C more than 0.05 and the scope of less than 0.8.By making peakedness ratio D/C be positioned at this scope, initial DCR(D.C. resistance can be obtained) the little and capacitor electrode body of excellent corrosion resistance.
When peakedness ratio D/C is less than 0.05, represent that corrosion resistance dies down, when larger than 0.80, initial DCR becomes large.In the example of fig. 5, the peakedness ratio D/C of collector body 4A is 0.16.Time between the activate that electric discharge when peakedness ratio D/C and Corona discharge Treatment exports and describes below and contact with moisture etc. are relevant.When exporting high situation and the above-mentioned time is short, peakedness ratio D/C increases.
For the surface of collector body 4A with the protective layer 9 formed like this, wetability improves significantly, therefore effectively can be coated with aqueous slurry, can improve the productivity of capacitor.And, remained in the oil content during rolling in collector body 4A by Corona discharge Treatment removing, the DCR of capacitor electrode body can be made to reduce.
In addition, the slurry taking water as dispersant is coated on when collector body 4A being formed tackifier coating 10, the surface of preferred protective layer 9 for the contact angle of water more than 8 ° and the scope of less than 50 °.When lower than 8 °, due to the physical impacts when Corona discharge Treatment, make the surface roughening of collector body 4A.Consequently, when forming thin tackifier coating 10 when even spread, produce skewness.On the other hand, when more than 50 °, insufficient by the effect of Corona discharge Treatment removing oil content.In any case, the internal resistance of capacitor all increases.
In addition, the thickness being formed in the tackifier coating 10 on protective layer 9 is preferably less than 1.2 μm.In addition, also more than 0.3 μm is preferably.When the Thickness Ratio 1.2 μm of tackifier coating 10 is thick, initial DCR increases.This is presumably because tackifier coating 10 thickening and the absolute magnitude of diffusive adhesive 12 increases thus can not disperse completely and make the cause that the conductivity of tackifier coating 10 inside reduces.In addition, existing coating machine is used to be difficult to be coated with the tackifier coating 10 thinner than 0.3 μm.Therefore, consider feasibility etc., the thickness of preferred tackifier coating 10 is more than 0.3 μm.But, according to technological progress from now on, as long as can be coated with very thin coating machine is just not limited thereto.That is, if do not consider the level of coating technique, with the thickness of the average grain diameter degree of electroconductive particle 11 for lower limit.
In addition, as above-mentioned, the surface of above-mentioned collector body 4A is relevant with the preferable range of the thickness of tackifier coating 10 for the contact angle of water.In the slurry for the formation of tackifier coating 10, containing water as dispersant.By being coated with such slurry to the collector body 4A of the low contact angle with above-mentioned scope, even limited amount slurry, also can more uniformly dispersed electro-conductive particle 11 and adhesive 12 and make it spread on the surface of collector body 4A.Consequently, the tackifier coating 10 of the thickness with above-mentioned scope can be formed.
Thereby, it is possible to make high conductive thin tackifier coating 10 in large area.In addition, because tackifier coating 10 is thin, so capacitor electrode body integral thinned can also be made.Or, the capacity density of capacitor element 1 can be improved.
Further, the averag density of tackifier coating 10 is 0.4g/cm 3above.And, when electroconductive particle 11 is 4:1 with the Mixing ratio by weight of adhesive 12 as mentioned above, the averag density of tackifier coating 10 is increased to about 0.6g/cm 2, when mixing ratio is 10:1, about 2.1g/cm can be brought up to 2.The reason obtaining this effect is: protective layer 9 is formed by implementing Corona discharge Treatment to collector body 4A.That is, collector body 4A improves wetability by implementing Corona discharge Treatment, so the compatibility between the slurry used when improving coating tackifier coating 10 and collector body 4A.That is, the character repelling slurry is reduced.Consequently, under density high state, tackifier coating 10 is formed.Like this, in the present embodiment, be 0.4g/cm in the density of tackifier coating 10 3under above high state, collector body 4A is engaged securely with polarizability electrode layer 5A.
And, concerning above-mentioned averag density, can measure the weight of a part for the capacitor electrode body of the present embodiment extracted as sample, the weighing scale deducting the collector body 4A part of this sample calculates the weight of tackifier coating 10, and the area according to thickness and sample calculates averag density.
Further, for the oxyhydroxide contained in protective layer 9, as long as oxyhydroxide just can fully realize above-mentioned effect.But when the discharge and recharge repeating capacitor, collector body 4A and electrolyte react, the component ratio forming the constituent of protective layer 9 changed along with the time.Therefore, after Long-Time Service capacitor, in collector body 4A, due to the pH variation in electrolyte, by Al x(OH) yal is generated with the fluorine source such as the anion in electrolyte xf yo z, Al xf y(OH) z, Al xf y, Al xo y(OH) zf win represented compound at least any one.Therefore, after prolonged, protective layer 9 becomes and comprises above-mentioned Al xf yo z, Al xf y(OH) zdeng the formation of any one in compound.In addition, aluminum fluoride compound is due to stable chemical nature in organic solvent system electrolyte, therefore described above when formation tackifier coating 10, can be pre-mixed the compound containing fluorine atom in the slurry.In this situation, protective layer 9 just becomes containing above-mentioned Al from when assembling in capacitor or from the initial moment x(OH) y, Al xf yo z, Al xf y(OH) zdeng the formation of any one in compound.
The average thickness of protective layer 9 is preferably little than the average grain diameter of electroconductive particle 11.In this formation, because the average grain diameter of electroconductive particle 11 is larger than the thickness of protective layer 9, so when electroconductive particle 11 imbeds protective layer 9, can contact with comparalive ease with the collector body 4A of the below being configured in protective layer 9.Consequently, reliably can guarantee the conducting between collector body 4A and polarizability electrode layer 5A, can resistance be reduced, obtain static capacity fully.Therefore, such as preferably the mean value of the thickness of protective layer 9 is 20nm, and the average grain diameter of electroconductive particle 11 is 35nm.
But, even if when protective layer 9 average thickness than electroconductive particle 11 diameter 50% large, also can guarantee the conducting of collector body 4A and polarizability electrode layer 5A, in addition, also can obtain thickening effect in the lump.Such as, electroconductive particle 11 is imbedded in protective layer 9 to be linked as catenate state.
And the average thickness of protective layer 9 is expected for more than 10nm.Usually, in an atmosphere, the average thickness of autoxidation tunicle collector body 4A formed by autoxidation is number about nm.Even if imbed electroconductive particle 11 in the thin passivation tunicles such as such autoxidation tunicle, because electroconductive particle 11 is little with the contact area of passivation tunicle, so effective thickening effect cannot be obtained.In contrast, if the average thickness of protective layer 9 to be made more than 10nm (20nm as escribed above), then can obtain sufficient thickening effect, improve the adaptation of polarizability electrode layer 5A and collector body 4A.
Further, preferably make the average thickness of protective layer 9 be less than 50% of the average grain diameter of electroconductive particle 11, in addition, the average grain diameter of preferred electroconductive particle 11 is less than the average pore size of the emptying aperture of polarizability electrode layer 5A.
Further, the capacitor electrode body of present embodiment may be used for the various capacitor such as double electric layer capacitor or electrochemical capacitor.Such as, if double electric layer capacitor, then as the collector body 4A of the 1st collector body and such as formed with aluminium as the collector body 4B of the 2nd collector body.Collector body 4A forms the 1st protective layer, the 1st protective layer is formed the 1st tackifier coating containing electroconductive particle.And the polarizability electrode layer 5A as the 1st polarizability electrode layer is formed on the 1st tackifier coating.On the other hand, collector body 4B forms the 2nd protective layer, the 2nd protective layer is formed the 2nd tackifier coating containing electroconductive particle.And the polarizability electrode layer 5B as the 2nd polarizability electrode layer is formed on the 2nd tackifier coating.Polarizability electrode layer 5A, 5B comprise active carbon.
On the other hand, if electrochemical capacitor, then such as collector body 4A is formed by aluminium, and collector body 4B is formed by copper or nickel, and polarizability electrode layer 5A contains the material of the adsorbable and maldi ion such as active carbon.The collector body 4B of negative electrode 30B replaces polarizability electrode layer 5B be formed can embedding and the active material layer of deintercalate lithium ions.This active material layer comprises the material with carbon elements such as graphite, lithium ion or can the silicon compound of alloying.Further, lithium ion is comprised in the electrolytic solution.And, for the negative electrode 30B of electrochemical capacitor, in order to reduce current potential, embed a certain amount of lithium ion.
In addition, in the present embodiment, the capacitor employing the capacitor element 1 produced getting involved wound anode 30A and negative electrode 30B under the state having barrier film 6A, 6B is illustrated.In addition, also the stacked anode of barrier film and negative electrode can had and the electrode body of applying present embodiment in the anode of capacitor element that formed and/or negative electrode by getting involved.In this case, replacing shell 2 and sealing part 3, such as can forming the external packing body for receiving capacitor element 1 and electrolyte with aluminium lamination press mold.
In addition, the formation of collector body 4A, 4B is not limited to only be made up of metal as mentioned above, can be such as on the surface of base material, form metal film and carry out Corona discharge Treatment to cut off to the outer surface of this metal film and form metal film metal oxygen atom between combination form the formation of oxyhydroxide.Now, base material is not limited to metal, carbon system thin slice or insulator resin film etc.That is, collector body 4A, 4B has conductivity, and preferably at least surface is metal.And this metal if valve metal, then easily forms protective layer 9.
Above, with reference to Fig. 6, the manufacture method employing Corona discharge Treatment capacitor electrode body is described.Fig. 6 is the schematic diagram of the device used in the manufacture method of the capacitor electrode body of present embodiment.Further, be described in the manufacture method of this antianode 30A, but for negative electrode 30B, be also identical.
This device has deflector roll 15, Corona discharge Treatment portion 17, tackifier coating forming portion 18, the 1st drying section 19, polarizability electrode layer forming portion the 20 and the 2nd drying section 21.Collector body 4A is directed to transport path 16 by by the pay-off roll 14 of shaft-like wound into a roll for collector body 4A by deflector roll 15, and via above-mentioned each portion, takers-in 22 batches the anode 30A after process.
That is, first collector body 4A is directed to transport path 16 by pay-off roll 14 by deflector roll 15, the speed V(m/ minute to specify) conveying.The collector body 4A transported by pay-off roll 14 arrives Corona discharge Treatment portion 17, accepts activation at this.
In Corona discharge Treatment portion 17, the interval separating about 2mm arranges two electrodes (not shown), and these two electrodes are connected with power supply (not shown).Power supply applies ac high voltage to these electrodes.When applying the voltage of about about 1kV under air atmosphere, due to ionization, weak current can flow through between two electrodes, and corona discharge starts.17 pairs, Corona discharge Treatment portion collector body 4A applies this corona discharge.Specifically, be 20W minute/m to the two sides of collector body 4A with discharge capacity 2above and 350W minute/m 2below, electric discharge degree is 2W/cm 2above and 350W/cm 2following condition implements Corona discharge Treatment.
Further, setting the electrode width in the direction vertical with transport path 16 as L(m), the machining area of sparking electrode is S(cm 2), the transfer rate of collector body 4A is V(m/ minute), discharge power is P(W) time, represent discharge capacity and electric discharge degree with following formula.
(discharge capacity)=P/ (LV) (W minute/m 2)
(electric discharge degree)=P/S (W/cm 2)
Like this, by Corona discharge Treatment portion 17, Corona discharge Treatment is implemented to collector body 4A, cut off the combination of aluminium atom and other atom or molecule thus on its surface, make the surface activation of collector body 4A.Due to this activate afterwards with contact with moisture in will be very important, so discharge fully preferably by Corona discharge Treatment etc., sufficient energy is applied to collector body 4A.
Further, Corona discharge Treatment portion 17 also can be configured to, and has two electrodes, and side's electrode is made roll, comes conveying collector body 4A limit, limit carry out Corona discharge Treatment by making this electrode rotary.
After by the surface activation of collector body 4A, collector body 4A arrives tackifier coating forming portion 18 immediately.By tackifier coating forming portion 18, collector body 4A is coated with to the slurry (not shown) adding the water as dispersant to electroconductive particle 11 and adhesive 12 and formed, forms tackifier coating 10.
Before this slurry of formation, the dispersion media such as ball mill are not preferably used to disperse electroconductive particle 11 and adhesive 12.Dispersion medium can be suppressed to destroy electroconductive particle 11 by such process for dispersing, keep the conductivity that electroconductive particle 11 is excellent, electroconductive particle 11 and adhesive 12 can be disperseed each other with this state.As the process for dispersing not using dispersion medium, such as, have and in planetary stirring machine or airslide disintegrating mill, pressure homogenizer etc., only to put into electroconductive particle 11 and adhesive 12 and make it the method for disperseing.
In slurry the moisture surface reaction with carrying out modified collector body 4A with corona discharge handling part 17, the surface of collector body 4A is formed containing the protective layer 9 of oxyhydroxide.That is, when forming tackifier coating 10, the water contained by slurry with in the surface reaction of collector body 4A be chemically activity.Like this, formed the step of tackifier coating 10 double as in the step forming protective layer 9 with contact with moisture step.
The metallic atom cutting off the surface of the collector body 4A of the combination between oxygen atom is chemically becoming instability, and result is in chemically activate.When such metallic atom is wanted to recover stable state, the atom easily near metallic atom or molecule are combined.Such as, can exemplify out to be combined with oxygen atom and again form metal oxide.Therefore, contact with moisture step is not preferably carried out after activate step terminates with delaying.
Such as, the moment preferably terminated in activate step carries out contact with moisture step within playing 1 point.Thus, protective layer forming step terminates, and can stably be formed containing the Al as oxyhydroxide xo y(OH) zprotective layer 9.
As the coating process of slurry, such as, can exemplify following method.On the unit (not shown) accumulating slurry, be configured with rotatable roller (not shown), in the slurry that the lower surface of this roller is immersed in unit.And, this roller is rotated, the upper surface of roller is abutted with the slurry be attached on roller with the lower surface of the collector body 4A transported.Especially, when the direction contrary with the throughput direction of collector body 4A making roller rotate, can effectively slurry be coated on collector body 4A.It should be noted that, the lower surface of collector body 4A can only be coated with by the method, as the method for coating upper surface, reversion roller (not shown) is set in the midway of transport path 16 and makes the direct of travel of collector body 4A reverse thus collector body 4A is reversed up and down.Thus, slurry can be coated on the two sides of collector body 4A by said method.In addition, this slurry can also be the formation being mixed with fluorine except above-mentioned formation.
Dry by the 1st drying section 19 by the collector body 4A of tackifier coating forming portion 18.After the 1st drying section 19, collector body 4A arrives polarizability electrode layer forming portion 20.In this polarizability electrode layer forming portion 20,2nd slurry of coating containing active carbon 13, forms polarizability electrode layer 5A on tackifier coating 10.
Finally, again dry by the 2nd drying section 21, complete anode 30A.Then, anode 30A takers-in 22 batches, shaft-like wound into a roll.In the capacitor electrode body and anode 30A of the present embodiment produced according to this manufacture method, the adaptation of polarizability electrode layer 5A and collector body 4A is excellent.
In addition, as mentioned above, Corona discharge Treatment is preferably 20W minute/m at discharge capacity 2above and 350W minute/m 2below, electric discharge degree is 2W/cm 2above and 350W/cm 2carry out under following condition.Discharge capacity is less than 20W minute/m 2, and electric discharge degree is less than 2W/cm 2time, based on the poor effect of the activate on the surface of the collector body 4A of Corona discharge Treatment.In addition, discharge capacity is greater than 350W minute/m 2, and electric discharge degree is greater than 350W/cm 2time, when Corona discharge Treatment, collector body 4A generates heat, and intensity reduces.Further, after Corona discharge Treatment, in order to form tackifier coating 10 by tackifier coating forming portion 18, pressure to be applied to collector body 4A.Therefore, discharge capacity reaches 350W minute/m 2below, electric discharge degree reaches 350W/cm 2very important to the intensity keeping collector body 4A below.
Now, as mentioned above, preferably by carry out 1 time or repeatedly above-mentioned Corona discharge Treatment is come limit and carried out confirmation limit and control, to make collector body 4A, the contact angle of water is more than 8 ° and less than 50 °.
Further, in the above description, under air atmosphere, activate step is implemented., in order to reduce the generation of ozone, also can reduce oxygen and implementing under the inertness such as nitrogen or argon gas gas atmosphere.
In addition, in order to obtain containing above-mentioned Al x(OH) y, Al xf yo z, Al xf y(OH) zdeng the epithelium of the formation of any one in compound as the composition of the epithelium on aluminium surface, the mist of inertness gas and fluorocarbon gas also can be used as the gas composition in corona discharge.Such as, Ar/CF is preferably 4, N 2/ CF 4, Ar/C 2f 6deng.Except the mist of such inertness gas and fluorocarbon gas, volume ratio can also be about less than 20% oxygen and fluorocarbon gas used in combination.Such as can also use air and CF 4mist.Or, except fluorocarbon gas, as fluorine atom supply source also can between 0.1 ~ 10% mixed C OF 2.And.Preferably mix between 0.1% ~ 5%.Like this, preferably containing under the atmosphere of gas that in the molecule there is fluorine atom, Corona discharge Treatment is implemented, by the surface activation of collector body 4A to the surface of collector body 4A.
Fig. 7 is elapsed time after the activate step representing collector body 4A and the collector body 4A surface curve chart for the relation of the contact angle of water.In addition, activate take discharge capacity as 200W minute/m 2, electric discharge degree is 7w/cm 2implement.
Find through the collector body 4A of activate step after chemically activate along with the prolongation of elapsed time from activate step, the decreased effectiveness of surface activation.Especially, find, after activate step has just terminated, significant change occurs within 10 points.It can thus be appreciated that, after activate step terminates, need to carry out contact with moisture step continuously, especially when change will be suppressed, preferably as mentioned above after activate step terminates, transfer to contact with moisture step within 1 point.
And; to the two sides formation protective layer 9 of collector body 4A and the manufacture method of tackifier coating 10 are illustrated in the present embodiment; but be not limited thereto, when also only can form protective layer 9 or tackifier coating 10 on the one side of collector body 4A, apply above-mentioned manufacture method.
In addition, in the present embodiment, be illustrated according to the order of carrying out contact with moisture step and tackifier coating forming step simultaneously, but be not limited to the method.Contact with moisture step also can be carried out as the step outside tackifier coating forming step.
Below, use concrete example, the preferred value scope of the capacitor electrode body of present embodiment is described.Further, unless otherwise specified, for capacitor specific characteristics, the capacitor produced under the following conditions is used to confirm.The aluminum of 2cm × 2cm element paper tinsel is made collector body 4A, 4B.Use such collector body 4A, 4B, make capacitor electrode body and anode 30A and negative electrode 30B.
The thickness of polarizability electrode layer 5A is 40 μm, and the thickness of tackifier coating 10 is 0.6 μm.In addition, the thickness of protective layer 9 is 20nm.The mixing ratio of the electroconductive particle 11 in tackifier coating 10 is 4 times of adhesive 12.Adhesive 12 uses carboxymethyl cellulose.The average grain diameter of electroconductive particle 11 is 35nm.Polarizability electrode layer 5A is made up of phenolic resins system active carbon, the acetylene black as conductive auxiliary agent and the carboxymethyl cellulose as adhesive.Active carbon, weight rate between conductive auxiliary agent and adhesive are 10:2:1.
Barrier film 6A use thickness is the nonwoven fabrics of the cellulose of 35 μm.Make barrier film 6A in the anode 30A produced according to above method and negative electrode 30B and carry out stacked, after dipping electrolyte, carrying out sealing analogue formation unit with butyl rubber.In addition, EDMIBF is contained with the concentration of 1.0 moles/l in the solvent that electrolyte is used in by 1:1 mixing EC and DMC 4solution.
First, to the Al represented in protective layer 9 2o 3existence peak C, represent Al xo y(OH) zexistence peak value D between the peakedness ratio D/C result of carrying out studying be described.Change electric discharge power output when Corona discharge Treatment carried out to collector body 4A, 5A and the time between activate and contact with moisture, peakedness ratio D/C is changed between 0.02 to 0.98 and carrys out modeling unit.In addition, contact angle is 17 °.Table 1 represent initial DCR value, 85 DEG C, shelved 200 hours under the state of non-loaded (not forming the state of electric double layer at anode and negative electrode) after the Magnification of DCR of situation.Further, in order to measure DCR, after the voltage of said units applying 10mA, 2.5V is charged, resistance when discharging with 10mA is measured.
Peakedness ratio D/C Initial DCR (m Ω) DCR Magnification (%) 0.02 0.7 143 0.05 0.8 15 0.20 0.8 10 0.70 0.9 11 0.80 1.2 13 0.85 2.9 12 0.98 8.7 20
As shown in Table 1, when peakedness ratio D/C is less than 0.05, the principal component of protective layer 9 is Al 2o 3.Although guarantee conductivity in this case, DCR enlarges markedly due to High temperature storage.This is presumably because Al 2o 3for the form of relatively dredging is so electrolyte and collector body 4A, 5A cause of reacting.On the other hand, dense Al xo y(OH) zwhen increasing in protective layer 9, the electronic conductivity of the protective layer 9 when applying high electric field to protective layer 9 reduces.Therefore.When peakedness ratio D/C is more than 0.80, initial DCR becomes large.Therefore, think by moderately mixing Al in protective layer 9 2o 3with Al xo y(OH) z, conductivity and corrosion resistance can be taken into account.Specifically, preferred peak is more than 0.05 than D/C and less than 0.80.In addition, more than 0.20 is more preferably and less than 0.70.
Then, collector body 4A, 5A are described for the result of study of the contact angle of water.Change condition when Corona discharge Treatment carried out to collector body 4A, 5A, above-mentioned contact angle is changed between 4 ° to 58 ° and carrys out analogue formation unit.Further, peakedness ratio D/C is 0.16.Table 2 represents the result of study of collector body 4A for the contact angle of water and the relation of capacitor specific characteristics.Specifically, measure and maintain through 192 hours, 80 DEG C, the Magnification of DCR after non-loaded state.Further, DCR measures according to the method identical with when evaluating the relation of above-mentioned peakedness ratio D/C with DCR.
In addition, the measurement of contact angle uses θ/2 method.In the method for θ/2, obtain contact angle according on the connection left and right end points of drop and the straight line on summit relative to the angle of the surface of solids.Appreciation condition is that the water droplet of 1 ~ 2 μ L is dropped on the surface of collector body 4A by use, water droplet is diffused into the contact angle of stabilisation after 30 seconds to a certain degree.
Contact angle (°) DCR Magnification (%) 58 1032.4 53 200.3 50 10.8 43 7.6 17 23.0 8 18.2 4 213.1
Known according to table 2, contact angle is from 8 ° to 50 °, suppress the rheological parameters' change with time of DCR., contact angle is that when departing from 58 °, 53 ° of this scope or 4 °, DCR increases significantly.Thus, the surface of preferred collector body 4A is more than 8 ° and less than 50 ° for the contact angle of water.
Then, the result of the thickness that have studied tackifier coating 10 is described.The thickness of tackifier coating 10 is changed between 0.3 μm to 2.7 μm and carrys out analogue formation unit.In addition condition is as above-mentioned.The result of the research thickness of tackifier coating 10 and the relation of capacitor specific characteristics is represented in table 3.That is, the different capacitor electrode body of the thickness of tackifier coating 10 is used to make capacitor, the relation of the research thickness of tackifier coating 10 and the initial DCR value of capacitor.In addition, the contact angle on the surface of collector body 4A is 17 °, and peakedness ratio D/C is 0.16.
Further, in order to compare, also make the capacitor employing the capacitor electrode body that tackifier coating 10 and protective layer 9 are not set, measuring initial DCR value.In this situation, Corona discharge Treatment is implemented to collector body 4A.
Thickness (μm) Initial DCR leads (%) 2.7 349.4 1.5 102.4 1.2 72.3 0.9 71.1 0.6 63.9 0.3 69.9 Nothing 100
In table 3 the initial DCR value employing the capacitor of the capacitor electrode body not arranging tackifier coating 10 and protective layer 9 is set to 100%, represents the initial DCR value of capacitor in addition with percentage.Further, when using the relation with above-mentioned peakedness ratio D/C and the DCR of evaluation, identical method measures DCR.
Known according to table 3, when the Thickness Ratio 1.2 μm of tackifier coating 10 is thick, initial DCR increases.As from the foregoing, the thickness of preferred tackifier coating 10 is for more than 0 μm and less than 1.2 μm.
According to the present invention, can improve the adaptation between the collector body of capacitor electrode body and polarizability electrode layer, the internal resistance employing the capacitor of capacitor electrode body of the present invention reduces.In addition, the reliability of capacitor improves.Therefore, the capacitor employing capacitor electrode body of the present invention is expected to for automobile, various electronic equipment, electric equipment, industrial equipment.
3 sealing parts
4A, 4B collector body
5A, 5B polarizability electrode layer
6A, 6B barrier film
7A, 7B go between
8A, 8B hole
9 protective layers
10 tackifier coatings
11 electroconductive particles
13 active carbons
14 pay-off roll
15 deflector rolls
16 transport paths
17 Corona discharge Treatment portions
18 tackifier coating forming portions
19 the 1st drying sections
20 polarizability electrode layer forming portions
21 the 2nd drying sections
22 takers-ins
30B negative electrode
1. a capacitor electrode body, possesses:
There is the collector body of conductivity;
Protective layer, it is formed on described collector body, and containing oxyhydroxide;
Tackifier coating, it is formed on described protective layer, and containing electroconductive particle; And
Polarizability electrode layer, it is formed on described tackifier coating,
Wherein, at least surface of described collector body is made up of valve metal,
Described valve metal is aluminium, and when setting X, Y, Z as arbitrary natural number, described oxyhydroxide is by composition formula Al xo y(OH) zthe compound represented,
When using fourier transform infrared spectroscopy to measure described protective layer, the expression Al obtained 2o 3existence peak C with represent the Al of described protective layer xo y(OH) zthe ratio D/C of peak value D of existence be more than 0.05 and less than 0.8.
2. capacitor electrode body according to claim 1, wherein, described valve metal is aluminium, and when setting X, Y, Z, W as arbitrary natural number, described protective layer also comprises by composition formula Al x(OH) y, Al xf yo z, Al xf y(OH) z, Al xf yand Al xo y(OH) zf wat least one in represented compound.
3. capacitor electrode body according to claim 1, wherein, the averag density of described tackifier coating is 0.4g/cm 3above.
4. capacitor electrode body according to claim 1, wherein, the thickness of described tackifier coating is less than 1.2 μm.
5. capacitor electrode body according to claim 1, wherein, the surface with the described collector body of described protective layer is more than 8 ° and less than 50 ° for the contact angle of water.
6. a capacitor, has:
Capacitor element, it has anode, negative electrode and the barrier film between described anode and described negative electrode;
Electrolyte, it is at least immersed in described capacitor element; And
External packing body, it receives described capacitor element and described electrolyte,
At least any one party in described anode and described negative electrode possesses:
7. capacitor according to claim 6, wherein, described anode and described negative electrode have described collector body, described protective layer, tackifier coating and polarizability electrode layer respectively,
Described polarizability electrode layer contains active carbon.
8. capacitor according to claim 6, wherein, described anode comprises as the described collector body of the 1st collector body, described protective layer, tackifier coating and polarizability electrode layer, and described polarizability electrode layer contains active carbon,
Described negative electrode has:
2nd collector body; With
Active material layer, it is formed on described 2nd collector body, and can embed and deintercalate lithium ions,
Described electrolyte contains lithium ion.
9. the manufacture method of capacitor electrode body according to claim 1, comprising:
The collector body with conductivity is formed the step of the protective layer containing oxyhydroxide;
Described protective layer is formed the step of the tackifier coating containing electroconductive particle; And
Described tackifier coating is formed the step of polarizability electrode layer.
10. the manufacture method of capacitor electrode body according to claim 9, wherein, the step forming described protective layer comprises:
Under air atmosphere, Corona discharge Treatment implemented to the surface of described collector body and make the step of the surface activation of described collector body; With
Make the step of the surface contact of moisture and described collector body after by the surface activation of described collector body.
The manufacture method of 11. capacitor electrode bodies according to claim 10, wherein, when forming described tackifier coating, be dispersant by coating with water and comprise the slurry of described electroconductive particle, thus the step of the surface contact of moisture and described collector body will be made simultaneously to carry out with the step of the described tackifier coating of formation.
The manufacture method of 12. capacitor electrode bodies according to claim 11, wherein, described collector body is formed by plain paper tinsel, in the step of the surface activation by described collector body, makes the surface of described collector body be more than 8 ° and less than 50 ° for the contact angle of water.
The manufacture method of 13. capacitor electrode bodies according to claim 10, wherein, after the step of the surface activation by described collector body terminates, made the surface contact of moisture and described collector body within 1 minute.
The manufacture method of 14. capacitor electrode bodies according to claim 9, wherein, the step forming described protective layer comprises:
Under the atmosphere containing the gas in the molecule with fluorine atom, Corona discharge Treatment is implemented by the step of the surface activation of described collector body to the surface of described collector body; With
The manufacture method of 15. capacitor electrode bodies according to claim 9, wherein, when forming described tackifier coating, coating contains the slurry of the compound of described electroconductive particle and contain fluorine atoms.
The manufacture method of 16. capacitor electrode bodies according to claim 9, wherein, does not use dispersion medium that described electroconductive particle and adhesive dispersion are prepared mixture, uses described mixture to prepare slurry,
Described slurry is coated with when forming described tackifier coating.
CN201180016707.6A 2010-03-30 2011-03-28 Capacitor electrode body and its manufacture method and the capacitor employing this electrode body CN102822920B (en)
JP2010-078451 2010-03-30
JP2010078451 2010-03-30
PCT/JP2011/001804 WO2011121967A1 (en) 2010-03-30 2011-03-28 Electrode structure for capacitor, process for producing same, and capacitor including the electrode structure
CN102822920A CN102822920A (en) 2012-12-12
CN102822920B true CN102822920B (en) 2016-01-20
ID=44711731
CN201180016707.6A CN102822920B (en) 2010-03-30 2011-03-28 Capacitor electrode body and its manufacture method and the capacitor employing this electrode body
US (1) US8958197B2 (en)
EP (1) EP2555212A4 (en)
JP (2) JP5810258B2 (en)
CN (1) CN102822920B (en)
WO (1) WO2011121967A1 (en)
CN103137942B (en) * 2011-12-02 2016-03-23 北京鼎能开源电池科技股份有限公司 The preparation method of a kind of ferric phosphate lithium cell collector and positive plate
JP6009343B2 (en) * 2011-12-26 2016-10-19 株式会社半導体エネルギー研究所 Secondary battery positive electrode and method for producing secondary battery positive electrode
USD758328S1 (en) * 2012-12-18 2016-06-07 Jm Energy Corporation Lithium ion capacitor
CN106415761B (en) * 2014-01-23 2019-06-21 松下知识产权经营株式会社 Capacitor electrode and the capacitor for using it
US9704652B2 (en) * 2014-05-01 2017-07-11 Showa Denko K.K. Method for manufacturing tungsten-based capacitor element
CN105755327B (en) * 2016-03-29 2017-10-20 江阴新仁铝业科技有限公司 Low energy efficient discharge alloy aluminium foil and preparation method thereof
JP6486867B2 (en) * 2016-06-02 2019-03-20 太陽誘電株式会社 Electrode for electrochemical device and method for producing electrode for electrochemical device
WO2019188559A1 (en) * 2018-03-29 2019-10-03 日産化学株式会社 Undercoat foil for energy storage device electrode
CN108428954A (en) * 2018-03-31 2018-08-21 重庆市紫建电子有限公司 A kind of devices and methods therefor that can quickly study lithium ion battery electrochemical behavior
JP2005509284A (en) * 2001-11-02 2005-04-07 マクスウェル テクノロジーズ インコーポレイテッド Electrochemical double layer capacitor with carbon powder electrode (2)
CN101103423A (en) * 2004-12-27 2008-01-09 松下电器产业株式会社 Polarizable electrode member, process for producing the same, and electrochemical capacitor utilizing the member
US6787266B1 (en) 1998-05-28 2004-09-07 Matsushita Electric Industrial Co., Ltd. Battery plate and battery
JP2000156328A (en) 1998-11-19 2000-06-06 Toyota Motor Corp Manufacture of collector used in capacitor or battery
JP2003331849A (en) 2002-05-09 2003-11-21 Itochu Corp Current collecting structure, electrode structure, and method for manufacturing them
US7924548B2 (en) 2006-02-16 2011-04-12 Panasonic Corporation Electric double layer capacitor
JP4710651B2 (en) 2006-02-24 2011-06-29 パナソニック株式会社 Electric double layer capacitor
JP4998089B2 (en) 2006-06-01 2012-08-15 パナソニック株式会社 Electric double layer capacitor
2011-03-28 CN CN201180016707.6A patent/CN102822920B/en active IP Right Grant
2011-03-28 EP EP11762216.7A patent/EP2555212A4/en not_active Withdrawn
2011-03-28 WO PCT/JP2011/001804 patent/WO2011121967A1/en active Application Filing
2011-03-28 US US13/583,959 patent/US8958197B2/en active Active
2011-03-30 JP JP2011075051A patent/JP5810258B2/en active Active
2011-03-30 JP JP2011075035A patent/JP2011228683A/en not_active Withdrawn
US20130003260A1 (en) 2013-01-03
EP2555212A4 (en) 2015-01-07
WO2011121967A1 (en) 2011-10-06
US8958197B2 (en) 2015-02-17
CN102822920A (en) 2012-12-12
JP5810258B2 (en) 2015-11-11
JP2011228684A (en) 2011-11-10
EP2555212A1 (en) 2013-02-06
JP2011228683A (en) 2011-11-10
US8591601B2 (en) 2013-11-26 Electrode for energy storage device with microporous and mesoporous activated carbon particles
KR20100084635A (en) 2010-07-27 Primer for battery electrode
Wang et al. 2008 Aligned titania nanotubes as an intercalation anode material for hybrid electrochemical energy storage
JP2007173865A (en) 2007-07-05 Charge storage device
US7646587B2 (en) 2010-01-12 Electric double layer capacitor
EP2613387B1 (en) 2017-10-11 Coating liquid, conductive coating film, electrode plate for electricity storage device, and electricity storage device
CN1910711B (en) 2010-12-08 Electric double-layer capacitor, its manufacturing method, and electronic device using same
JP2007243202A (en) 2007-09-20 Wet electrolytic capacitor having cathode film
JP3444769B2 (en) 2003-09-08 Current collector of aluminum foil and a method for producing the same, a current collector, a secondary battery and an electric double layer capacitor
Yang et al. 2013 Ni–Co oxides nanowire arrays grown on ordered TiO 2 nanotubes with high performance in supercapacitors
DE102012221861A1 (en) 2013-06-06 Liquid electrolytic capacitor containing a gelled working electrolyte
Lin et al. 2013 Cathodic deposition of interlaced nanosheet-like cobalt sulfide films for high-performance supercapacitors
US9362563B2 (en) 2016-06-07 Energy storage device, method for manufacturing the same, and apparatus including the same
JP2008544544A (en) 2008-12-04 Current collector for electric double layer electrochemical capacitor and method for producing the current collector
KR20100031488A (en) 2010-03-22 Substrate for use in a wet capacitor
CN101180695A (en) 2008-05-14 Wet electrolytic capacitors
CN1839497A (en) 2006-09-27 Electrode, and method for preparing the same