Inventors: Kang Heon Hur (Suwon, KR) Kang Heon Hur (Suwon, KR) Doo Young Kim (Yongin, KR) Doo Young Kim (Yongin, KR) Mun Su Ha (Suwon, KR) Chul Seung Lee (Seoul, KR)
Patent application number: 20110157768
A multilayer ceramic capacitor and a method of manufacturing the same are provided. The multilayer ceramic capacitor includes a capacitive part, a passivation layer, and first and second outer electrodes. In the capacitive part, a plurality of dielectric layers and a plurality of first and second inner electrodes are alternately laminated, and ends of the first and second inner electrodes are alternately and respectively exposed in a direction of lamination of the dielectric layers. The passivation layer is provided at either or both of the top and bottom surfaces of the capacitive part. The first and second outer electrodes are electrically connected to the first and second inner electrodes exposed in a direction of lamination of the dielectric layers. One or more inner electrodes disposed at both ends in a direction of lamination among the plurality of inner electrodes include oxide represented by Ni--Mg--O.
1. A multilayer ceramic capacitor comprising: a capacitive part in which a plurality of dielectric layers and a plurality of first and second inner electrodes are alternately laminated, ends of the first and second inner electrodes being alternately and respectively exposed in a direction of lamination of the dielectric layers; a passivation layer provided at either or both of the top and bottom surfaces of the capacitive part; and first and second outer electrodes electrically connected to the first and second inner electrodes exposed in a direction of lamination of the dielectric layers, wherein one or more inner electrodes disposed at both ends in a direction of lamination among the plurality of inner electrodes comprise oxide represented by Ni--Mg--O.
2. The multilayer ceramic capacitor of claim 1, wherein the outermost inner electrode disposed at both ends in the direction of lamination comprises 30% or more of oxide represented by Ni--Mg--O.
3. The multilayer ceramic capacitor of claim 1, wherein a ratio of the oxide represented by Ni--Mg--O is gradually reduced from the both ends in the direction of lamination toward the inside of the capacitive part.
4. The multilayer ceramic capacitor of claim 1, wherein the passivation layer comprises 0.5-10 wt % of Mg.
5. The multilayer ceramic capacitor of claim 1, wherein the passivation layer comprises glass containing 0.5-15 wt % of Si.
6. A method of manufacturing a multilayer ceramic capacitor, the method comprising: preparing a capacitive part in which a plurality of dielectric layers and a plurality of first and second inner electrodes are alternately laminated, ends of the first and second inner electrodes being alternately and respectively exposed in a direction of lamination of the dielectric layers; forming a passivation layer at either or both of the top and bottom surfaces of the capacitive part; performing a firing process under an oxygen partial pressure at which one or more inner electrodes disposed at both ends in a direction of lamination among the plurality of inner electrodes are oxidized; and forming first and second outer electrodes electrically connected to the first and second inner electrodes which are exposed in a direction of lamination of the dielectric layers.
7. The method of claim 6, wherein the passivation layer comprises 0.5-10 wt % of Mg.
8. The method of claim 6, wherein the passivation layer comprises glass containing 0.5-15 wt % of Si.
9. The method of claim 6, wherein the firing process is performed under Ni--NiO equilibrium oxygen partial pressure (PPO2) of 10.sup.-9 atm or more.
[0001] This application claims the priority of Korean Patent Application No. 10-2009-0134458 filed on Dec. 30, 2009, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein by reference.
[0003] The present invention relates to a multilayer ceramic capacitor and a method of manufacturing the same, and more particularly, to a multilayer ceramic capacitor having high reliability because of its low crack occurrence rate and low blister occurrence rate, and a method of manufacturing the same.
[0005] In general, a ceramic electronic component using a ceramic material, for example, a capacitor, an inductor, a piezoelectric device, a varistor, or a thermistor, includes a ceramic body, an inner electrode provided inside the ceramic body, and an outer electrode provided on the ceramic body to contact the inner electrode.
[0007] Multilayer ceramic capacitors are being widely used in mobile communications devices, such as laptop computers, PDAs mobile phones and the like, due to their small size, high capacity and ease of mounting.
[0010] As the multilayer ceramic capacitor has recently become smaller in size and higher in capacitance, many attempts have been made to manufacture a slim and multilayer ceramic body. However, as the ceramic body has become slim and multilayered, defects such as cracks and blisters are generated, causing the degradation in the reliability of a multilayer ceramic capacitor.
[0011] An aspect of the present invention provides a multilayer ceramic capacitor having high reliability because of its low crack occurrence rate and low blister occurrence rate, and a method of manufacturing the same.
[0012] According to an aspect of the present invention, there is provided a multilayer ceramic capacitor including: a capacitive part in which a plurality of dielectric layers and a plurality of first and second inner electrodes are alternately laminated, ends of the first and second inner electrodes being alternately and respectively exposed in a direction of lamination of the dielectric layers; a passivation layer provided at either or both of the top and bottom surfaces of the capacitive part; and first and second outer electrodes electrically connected to the first and second inner electrodes exposed in a direction of lamination of the dielectric layers, wherein one or more inner electrodes disposed at both ends in a direction of lamination among the plurality of inner electrodes include oxide represented by Ni--Mg--O.
[0013] The outermost inner electrode disposed at both ends in the direction of lamination may include 30% or more of oxide represented by Ni--Mg--O.
[0014] A ratio of the oxide represented by Ni--Mg--O may be gradually reduced from the both ends in the direction of lamination toward the inside of the capacitive part.
[0015] The passivation layer may include 0.5-10 wt % of Mg.
[0016] The passivation layer may include glass containing 0.5-15 wt % of Si.
[0017] According to another aspect of the present invention, there is provided a method of manufacturing a multilayer ceramic capacitor, including: preparing a capacitive part in which a plurality of dielectric layers and a plurality of first and second inner electrodes are alternately laminated, ends of the first and second inner electrodes being alternately and respectively exposed in a direction of lamination of the dielectric layers; forming a passivation layer at either or both of the top and bottom surfaces of the capacitive part; performing a firing process under an oxygen partial pressure at which one or more inner electrodes disposed at both ends in a direction of lamination among the plurality of inner electrodes are oxidized; and forming first and second outer electrodes electrically connected to the first and second inner electrodes which are exposed in a direction of lamination of the dielectric layers.
[0018] The passivation layer may include 0.5-10 wt % of Mg.
[0019] The passivation layer may include glass containing 0.5-15 wt % of Si.
[0020] The firing process may be performed under Ni--NiO equilibrium oxygen partial pressure (PPO2) of 10-9 atm or more.
[0022] FIG. 1 is a schematic perspective view of a multilayer ceramic capacitor according to an embodiment of the present invention;
[0023] FIG. 2 is a schematic cross-sectional view taken along line A-A' of FIG. 1; and
[0024] FIG. 3 shows analysis result of the multilayer ceramic capacitor in an energy dispersive spectrometer (EDS) of a transmission electron microscope (TEM).
[0026] FIG. 1 is a schematic perspective view of a multilayer ceramic capacitor according to an embodiment of the present invention, and FIG. 2 is a schematic cross-sectional view taken along line A-A' of FIG. 1.
[0027] Referring to FIGS. 1 and 2, a multilayer ceramic capacitor 100 according to an embodiment of the present invention includes a ceramic body 110, first and second inner electrodes 120a and 120b provided inside the ceramic body 110, and first and second outer electrodes 130a and 130b electrically connected to the first and second inner electrodes 120a and 120b.
[0028] The ceramic body 110 includes a capacitive part 110B and passivation layers 110A provided on the top and bottom surfaces of the capacitive part 110B.
[0029] The capacitive part 110B has a structure in which a plurality of dielectric layers 111 and a plurality of first and second inner electrodes 120a and 120b are alternately laminated. The first and second inner electrodes 120a and 120b are a pair of electrodes having different polarities. The first and second inner electrodes 120a and 120b are disposed to face each other along a direction of lamination of the dielectric layers 111, and are electrically insulated from each other by the dielectric layers 111. Ends of the first and second inner electrodes 120a and 120b are alternately and respectively exposed in a direction of lamination of the dielectric layers 111. The exposed ends of the first and second inner electrodes 120a and 120b are electrically connected to the first and second outer electrodes 130a and 130b, respectively.
[0030] When a predetermined voltage is applied to the first and second outer electrodes 130a and 130b, electric charges are accumulated between the first and second inner electrodes 120a and 120b which face each other. The static capacitance of the multilayer ceramic capacitor increases in proportion to the areas of the first and second inner electrodes 120a and 120b which face each other.
[0031] The dielectric layer 111 of the capacitive part 110B may be formed of a ceramic material having high permittivity. For example, the dielectric layers 111 may be formed of, but are not limited to, a barium titanate (BaTiO3)-based ceramic, a lead complex perovskite-based ceramic, or a strontium titanate (SrTiO3)-based ceramic.
[0032] The passivation layers 110A may be formed on either or both of the top and bottom surfaces of the capacitive part 110B. In this embodiment, the passivation layers 110A are formed on both of the top and bottom surfaces of the capacitive part 110B.
[0033] The passivation layers 110A may be formed of a ceramic material having high permittivity. For example, the passivation layers 110A may be formed of, but are not limited to, a barium titanate (BaTiO3)-based ceramic, a lead complex perovskite-based ceramic, or a strontium titanate (SrTiO3)-based ceramic. In addition, the passivation layer 110A includes 0.5-10 wt % of Mg. In this embodiment, Mg may be added in a manner known to those skilled in the art, without particular limitations. For example, Mg may be added in a form of MgCO3 or MgO. Mg existing in the passivation layer 110A moves to the inner electrode during firing to thereby form oxide represented by Ni--Mg--O. The oxide represented by Ni--Mg--O is more stable than oxide represented by Ni--O. When a large amount of Ni--Mg--O exists in the inner electrode, the adhesiveness between the passivation layer and the inner electrode is improved.
[0034] When a content of Mg existing in the passivation layer is less than 0.5 wt %, the adhesiveness between the passivation layer and the inner electrode may be weakened. When a content of Mg existing in the passivation is more than 10 wt %, Mg may degrade the dielectric characteristic of the capacitive part.
[0035] In addition, the passivation layer may include glass. The glass includes Si, and may include an alkaline metal or an alkaline earth metal together with Si. In the glass included in the passivation layer, a content of Si may be in the range of 0.5-15 wt %. When the content of Si is less than 0.5 wt %, the adhesiveness between the passivation layer and the inner electrode may be weakened. When the content of Si is more than 15 wt %, the Si content of the passivation layer may degrade the dielectric characteristic of the capacitive part.
[0036] The passivation 110A may be formed to be thicker than the dielectric layer 111 of the capacitive part 110B. For example, the dielectric layer 111 of the capacitive part 110B may be 2 μm or less and laminated with approximately 25 layers or more, and thus, the thickness of the capacitive part 110B may be in the range of 50-2,000 μm. In this case, the thickness of the passivation layer 110A may be in the range of 10-100 μm.
[0037] The first and second inner electrodes 120a and 120b are formed of a conductive metal, for example, Ni or a Ni alloy. The Ni alloy may include Mn, Cr, Co or Al together with Ni.
[0038] One or more inner electrodes disposed at both ends of the ceramic body in a direction of lamination include oxide represented by Ni--Mg--O. The both ends in the direction of lamination refer to regions contacting the passivation layers 110A in the capacitive part 110B.
[0039] Only the outermost inner electrode among the plurality of inner electrodes may an oxidized inner electrode including an oxide represented by Ni--Mg--O.
[0040] Alternatively, one or more inner electrodes disposed inside the capacitive part, not the outermost position of the capacitive part, may include the oxide represented by Ni--Mg--O. In this case, the oxidation rate of the outermost inner electrode is highest, and the oxidation rate of the inner electrodes is gradually reduced toward the inside of the capacitive part. The inner electrode disposed at the outermost ends in the direction of lamination may include 30% or more of the oxide represented by Ni--Mg--O.
[0041] The number of the oxidized inner electrodes and the oxidation rate of the inner electrodes may be determined by adjusting a level of oxygen partial pressure during firing.
[0042] The oxidized inner electrode has excellent adhesiveness with the passivation layer, thereby improving the adhesiveness between the capacitive part and the passivation layer. Accordingly, crack and blister occurrence rates between the capacitive part and the passivation part are reduced.
[0043] Furthermore, the oxidized inner electrode prevents the penetration of moisture from the outside, thereby improving the humidity resistance of the multilayer ceramic capacitor.
[0044] The first and second outer electrodes 130a and 130b are formed of, but are not limited to, a conductive metal. For example, the first and second outer electrodes 130a and 130b may include copper.
[0045] Hereinafter, a method of manufacturing a multilayer ceramic capacitor according to an embodiment of the present invention will be described.
[0046] First, a plurality of ceramic green sheets to be laminated in a capacitive part are prepared. Specifically, a slurry is formed by mixing a ceramic powder, a binder, and a solvent, and the slurry is made into a sheet having a thickness of several μm by a doctor blade method.
[0047] Then, a paste for an inner electrode is coated on the ceramic green sheets to form first and second inner electrode patterns. The first and second inner electrode patterns may be formed by a screen printing process. The paste for an inner electrode may be formed by dispersing a Ni or Ni alloy powder into an organic binder and an organic solvent. The Ni alloy may include Mn, Cr, Co, or Al together with Ni.
[0048] The organic binder may use a binder known in the art to which the invention pertains. For example, the organic binder may use, but is not limited to, a cellulose-based resin, an epoxy resin, an aryl resin, an acryl resin, a phenol-formaldehyde resin, an unsaturated polyester resin, a polycarbonate resin, a polyamide resin, a polyimide resin, an alkyd resin, or a rosin ester.
[0049] Furthermore, the organic solvent may also use an organic solvent known in the art to which the invention pertains. For example, the organic solvent may use, but is not limited to, butyl carbitol, butyl carbitol acetate, turpentine oil, α-terebineol, ethyl cellosolve, or butyl phthalate.
[0050] Next, the ceramic green sheets in which the first and second inner electrode patterns are formed are laminated and pressed in a direction of lamination to thereby attach the laminated ceramic green sheets to the paste for an inner electrode. In this way, a capacitive part in which the ceramic green sheets and the paste for an inner electrode are alternately laminated is manufactured.
[0051] Next, a plurality of ceramic green sheets to be laminated on the top and bottom surfaces of the capacitive part are prepared. Specifically, a slurry is formed by mixing a ceramic powder, Mg, an organic binder, and a solvent, and the slurry is made into a sheet having a thickness of several μm by a doctor blade method. The content of Mg is in the range of 0.5-10 wt % with respect to the entire composition. A Si-containing glass may be added. In this case, the content of Si may be in the range of 0.5-15 wt % with respect to the entire composition.
[0052] The ceramic green sheets are laminated in the capacitive part to thereby obtain a multilayer ceramic body in which a passivation layer is formed.
[0053] Next, the multilayer ceramic body is cut to form a chip in each region corresponding to a single capacitor. In this case, the multilayer ceramic body is cut such that ends of the first and second inner electrode patterns are alternately and respectively exposed to the ends thereof.
[0054] Then, a ceramic sintered body is manufactured by firing the chips under a condition that oxidizes one or more inner electrodes disposed at both ends of the multilayer ceramic body in the direction of lamination. The firing condition employs a firing atmosphere which has a higher oxygen partial pressure than a typical oxygen partial pressure (PPO2<10-9 atm), specifically, it has a Ni--NiO equilibrium oxygen partial pressure (PPO2=10-9 atm or more). The firing temperature may be 1,200° C. The number of the oxidized inner electrodes and the oxidation rate of the inner electrodes may be adjusted according to the oxygen partial pressure.
[0055] Afterwards, first and second outer electrodes are formed to cover the ends of the ceramic sintered body and to be electrically connected to the first and second inner electrodes which are exposed to the ends of the ceramic sintered body.
[0056] Next, the surfaces of the outer electrodes may be plated with Ni or Sn.
[0057] The multilayer ceramic capacitor manufactured according to the embodiment of the present invention was cut in a direction of lamination, and the cut surface was polished. Components in the cut surface were analyzed using an energy dispersive spectrometer (EDS) of a transmission electron microscope (TEM). The analysis results are illustrated in FIG. 3. It can be seen from FIG. 3 that the oxide represented by Ni--Mg--O exists.
[0058] In addition, as shown in Table 1 below, multilayer ceramic capacitors were manufactured while changing the composition of the passivation layer, and the blister occurrence rate and the crack occurrence rate of the manufactured multilayer ceramic capacitors were measured.
TABLE-US-00001 TABLE 1 Cover Blister crack Mg Si occurrence occurrence (wt %) (wt %) rate (%) rate (%) Comparative 0.1 1.5 25 23 Example 1 Embodiment 1.0 1.5 16 8.8 1 Embodiment 3.0 1.5 17 4.9 2 Embodiment 5.0 1.5 8.0 5.0 3 Comparative 1.0 0.1 30 45 example 2 Embodiment 1.0 3.0 8.1 4.8 4 Embodiment 1.0 10 6.0 7.2 5
[0059] As set forth above, according to exemplary embodiments of the invention, the multilayer ceramic capacitor includes the oxidized inner electrode in the capacitive part adjacent to the passivation layer. The oxidized inner electrode includes oxide represented by Ni--Mg--O, which has excellent adhesiveness with the passivation layer. Therefore, the adhesiveness between the capacitive part and the passivation layer is improved, thereby reducing the crack occurrence rate and the blister occurrence rate between the capacitive part and the passivation layer.
[0060] Moreover, the oxidized inner electrode prevents the penetration of moisture from the outside, thereby improving the humidity resistance of the multilayer ceramic capacitor.
20110156334 METHOD FOR HANDLING PAPER SHEETS
20110156331 NON-CONTACT HOLDER AND NON-CONTACT HOLDING HAND
20110156330 PLATFORM AND METHOD FOR SUPPORTING A WORKPIECE TO BE CUT FROM SHEET MATERIAL
20110156329 CLAMPING MECHANISM
20110156328 INTEGRAL RETAINER TO RETAIN A SPRING
2009-06-11 Printed circuit board with multi layer ceramic capacitor and flat panel display device using the same
2009-11-26 Multilayer ceramic capacitor and method for manufacturing the same