Source: http://www.google.com/patents/US20040053152?dq=2040248
Timestamp: 2016-07-29 06:52:34
Document Index: 708519414

Matched Legal Cases: ['arts 2', 'arts 2', 'arts 1', 'arts 1', 'arts 1', 'arts 2', 'arts 2', 'arts 1', 'arts 1', 'arts 1', 'arts 1']

Patent US20040053152 - Electrophotographic photoconductor and method of preparing same - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsAn electrophotographic photoconductor having a layer of a crosslinked resin obtained by reacting an epoxy group-containing amine compound having a charge transferability-imparting group with at least one silicon compound selected from an epoxy ring-free alkoxysilane compound, an epoxy ring-free silanol...http://www.google.com/patents/US20040053152?utm_source=gb-gplus-sharePatent US20040053152 - Electrophotographic photoconductor and method of preparing sameAdvanced Patent SearchPublication numberUS20040053152 A1Publication typeApplicationApplication numberUS 10/458,626Publication dateMar 18, 2004Filing dateJun 11, 2003Priority dateJun 12, 2002Also published asUS7279260, US7718333, US20080063959Publication number10458626, 458626, US 2004/0053152 A1, US 2004/053152 A1, US 20040053152 A1, US 20040053152A1, US 2004053152 A1, US 2004053152A1, US-A1-20040053152, US-A1-2004053152, US2004/0053152A1, US2004/053152A1, US20040053152 A1, US20040053152A1, US2004053152 A1, US2004053152A1InventorsKazukiyo Nagai, Chiaki Tanaka, Tetsuro Suzuki, Hiroshi Ikuno, Hongguo LiOriginal AssigneeKazukiyo Nagai, Chiaki Tanaka, Tetsuro Suzuki, Hiroshi Ikuno, Hongguo LiExport CitationBiBTeX, EndNote, RefManPatent Citations (13), Referenced by (63), Classifications (25), Legal Events (5) External Links: USPTO, USPTO Assignment, EspacenetElectrophotographic photoconductor and method of preparing same
US 20040053152 A1Abstract
An electrophotographic photoconductor having a layer of a crosslinked resin obtained by reacting an epoxy group-containing amine compound having a charge transferability-imparting group with at least one silicon compound selected from an epoxy ring-free alkoxysilane compound, an epoxy ring-free silanol compound, an epoxy ring-containing alkoxysilane compound and an epoxy ring-containing silanol compound. Images(2) Claims(52)
What is claimed is: 1. An electrophotographic photoconductor having a layer comprising a crosslinked resin formed by condensation of silanol groups, and charge transferability-imparting groups each bonded to a silanol group of said resin through an epoxy group. 2. An electrophotographic photoconductor having a layer comprising a crosslinked resin containing a first chain formed by condensation of silanol groups and a second chain formed by addition of a silanol group to an epoxy group, and charge transferability-imparting groups each bonded to a silanol group of said resin through an epoxy group. 3. An electrophotographic photoconductor having a layer of a crosslinked resin obtained by reacting an epoxy group-containing amine compound having a charge transferability-imparting group with at least one silicon compound selected from the group consisting of an epoxy ring-free alkoxysilane compound, an epoxy ring-free silanol compound, an epoxy ring-containing alkoxysilane compound and an epoxy ring-containing silanol compound. 4. An electrophotographic photoconductor comprising an electrically conductive substrate, a photoconductive layer provided thereon, and a resin layer comprising a crosslinked resin obtained by reacting an epoxy group-containing amine compound with an epoxy ring-free silicon compound selected from the group consisting of an alkoxysilane compound and a silanol compound. 5. An electrophotographic photoconductor as claimed in claim 4, wherein said silanol compound is a product obtained by hydrolysis of an alkoxysilane compound. 6. An electrophotographic photoconductor as claimed in claim 4, wherein said resin layer is obtained by reacting a coating of a composition containing said epoxy group-containing amine compound and said silicon compound. 7. An electrophotographic photoconductor as claimed in claim 6, wherein said reaction of said coating is carried out by heating said coating at a temperature of at least 100� C. 8. An electrophotographic photoconductor as claimed in claim 4, wherein said epoxy group-containing amine compound is a compound represented by the following formula (1): wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100. 9. An electrophotographic photoconductor as claimed in claim 4, wherein said epoxy group-containing amine compound is a compound represented by the following formula (2): wherein R4 to R25 may be the same or different and each represent a hydrogen atom, a halogen atom or an alkyl group which may have one or more substituents and n is an integer of 0 to 100. 10. An electrophotographic photoconductor as claimed in 4, wherein said alkoxysilane compound is represented by the following formula (3): wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (3), R′ represents an alkyl group, X represents a hydrolyzable group and n is an integer of 0 to 3. 11. An electrophotographic photoconductor as claimed in claim 10, wherein said alkoxysilane compound is a mixture of compounds of the formula (3) having different numbers of n. 12. An electrophotographic photoconductor as claimed in claim 4, wherein said silanol compound is represented by the following formula (4): wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (4), Y represents a hydroxyl group or a hydrolyzable group and n is an integer of 0 to 3. 13. An electrophotographic photoconductor as claimed in claim 12, wherein said silanol compound is a mixture of compounds of the formula (4) having different numbers of n. 14. An electrophotographic photoconductor as claimed in claim 4, wherein at least one of said alkoxysilane compound and said silanol compound has at least one aromatic group. 15. An electrophotographic photoconductor as claimed in claim 4, wherein said resin layer is the outermost layer of the photoconductor. 16. An electrophotographic photoconductor as claimed in claim 4, wherein said photoconductive layer comprises two or more layers and said resin layer is one of said two or more layers of said photoconductive layer. 17. An electrophotographic photoconductor having a hardened layer of a composition comprising the following ingredients (a), (b) and (c): (a) a silane compound having at least one hydroxyl group bonded to the silicon atom thereof; (b) an epoxy group-containing amine compound represented by the following formula (1): wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100; (c) an aluminum chelate compound of the following formula: AlX1 nY1 3−n wherein X1 represents a lower alkoxy group Y1 represents a ligand derived from a compound selected from the group consisting of M1COCH2COM2 and M3COCH2COOM4 where M1, M2, M3 and M4 independently represent a lower alkyl group, and n is an integer of 0 to 2, wherein the amount of ingredient (b) is such that the weight ratio (b)/((a)+(b)) of the ingredient (b) to a total amount of the ingredients (a) and (b) is in the range of 0.1 to 0.7. 18. An electrophotographic photoconductor as claimed in claim 17, wherein the thickness of said hardened layer is 1 to 15 μm. 19. An electrophotographic photoconductor as claimed in claim 17, wherein said composition further comprises ingredient (d): (d) finely divided silica having an average particle diameter of 1 to 100 nm, wherein the amounts of ingredients (b) and (d) are such that the weight ratio (b)/((a)+(b)+(d)) of ingredient (b) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.1 to 0.6 and the weight ratio (d)/((a)+(b)+(d)) of ingredient (d) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.01 to 0.3. 20. An electrophotographic photoconductor as claimed in claim 19, wherein the thickness of said hardened layer is 1 to 15 μm. 21. A method of preparing an electrophotographic photoconductor, comprising the steps of: providing a coating liquid comprising the following ingredients (a), (b) and (c) dissolved and/or dispersed in a solvent: (a) a silane compound having at least one hydroxyl group bonded to the silicon atom thereof; (b) an epoxy group-containing amine compound represented by the following formula (1): wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100; (c) an aluminum chelate compound of the following formula: AlX1 nY1 3−n wherein X1 represents a lower alkoxy group Y1 represents a ligand derived from a compound selected from the group consisting of M1COCH2COM2 and M3COCH2COOM4 where M1, M2, M3 and M4 independently represent a lower alkyl group, and n is an integer of 0 to 2, wherein the amount of ingredient (b) is such that the weight ratio (b)/((a)+(b)) of the ingredient (b) to a total amount of the ingredients (a) and (b) is in the range of 0.1 to 0.7; applying the coating liquid to form a coating; and heating the coating at a temperature of 80 to 150� C. to harden the coating. 22. A method of preparing an electrophotographic photoconductor as claimed in claim 21, wherein said coating liquid further comprises ingredient (d): (d) finely divided silica having an average particle diameter of 1 to 100 nm, and wherein the amounts of ingredients (b) and (d) are such that the weight ratio (b)/((a)+(b)+(d)) of ingredient (b) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.1 to 0.6 and the weight ratio (d)/((a)+(b)+(d)) of ingredient (d) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.01 to 0.3. 23. A method of preparing an electrophotographic photoconductor as claimed in claim 21, wherein said solvent is at least one solvent selected from the group consisting of benzyl alcohol, cyclohexanone, 2-methoxyethyl acetate, tetrahydrofuran and acetylacetone. 24. An electrophotographic photoconductor comprising an electrically conductive substrate, a photoconductive layer provided thereon, and a resin layer comprising a crosslinked resin obtained by reacting an epoxy group-containing amine compound with an epoxy ring-containing silicon compound selected from the group consisting of an epoxy ring-containing alkoxysilane compound and an epoxy ring-containing silanol compound. 25. An electrophotographic photoconductor as claimed in claim 24, wherein said epoxy ring-containing silanol compound is a product obtained by hydrolysis of an epoxy ring-containing alkoxysilane compound. 26. An electrophotographic photoconductor as claimed in claim 24, wherein said resin layer is the outermost layer of the photoconductor. 27. An electrophotographic photoconductor as claimed in claim 24, wherein said photoconductive layer comprises two or more layers and said resin layer is one of said two or more layers of said photoconductive layer. 28. An electrophotographic photoconductor having a hardened layer of a composition comprising the following ingredients (a), (b) and (c): (a) a silane compound having an epoxy group and at least one hydroxyl group bonded to the silicon atom thereof and, optionally, an epoxy group-free silane compound having at least one hydroxyl group; (b) an epoxy group-containing amine compound represented by the following formula (1): wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100; (c) an aluminum chelate compound of the following formula: AlX1 nY1 3−n wherein X1 represents a lower alkoxy group Y1 represents a ligand derived from a compound selected from the group consisting of M1COCH2COM2 and M3COCH2COOM4 where M1, M2, M3 and M4 independently represent a lower alkyl group, and n is an integer of 0 to 2, wherein the amount of ingredient (b) is such that the weight ratio (b)/((a)+(b)) of the ingredient (b) to a total amount of the ingredients (a) and (b) is in the range of 0.1 to 0.7. 29. An electrophotographic photoconductor as claimed in claim 28, wherein the thickness of said hardened layer is 1 to 15 μm. 30. An electrophotographic photoconductor as claimed in claim 28, wherein said composition further comprises ingredient (d): (d) finely divided silica having an average particle diameter of 1 to 100 nm, wherein the amounts of ingredients (b) and (d) are such that the weight ratio (b)/((a)+(b)+(d)) of ingredient (b) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.1 to 0.6 and the weight ratio (d)/((a)+(b)+(d)) of ingredient (d) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.01 to 0.3. 31. An electrophotographic photoconductor as claimed in claim 30, wherein the thickness of said hardened layer is 1 to 15 μm. 32. A method of preparing an electrophotographic photoconductor, comprising the steps of: providing a coating liquid comprising the following ingredients (a), (b) and (c) dissolved and/or dispersed in a solvent: (a) a silane compound having an epoxy group and at least one hydroxyl group bonded to the silicon atom thereof and, optionally, an epoxy group-free silane compound having at least one hydroxyl group; (b) an epoxy group-containing amine compound represented by the following formula (1): wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100; (c) an aluminum chelate compound of the following formula: AlX1 nY1 3−n wherein X1 represents a lower alkoxy group Y1 represents a ligand derived from a compound selected from the group consisting of M1COCH2COM2 and M3COCH2COOM4 where M1, M2, M3 and M4 independently represent a lower alkyl group, and n is an integer of 0 to 2, wherein the amount of ingredient (b) is such that the weight ratio (b)/((a)+(b)) of the ingredient (b) to a total amount of the ingredients (a) and (b) is in the range of 0.1 to 0.7; applying the coating liquid to form a coating; and heating the coating at a temperature of 80 to 150� C. to harden the coating. 33. A method of preparing an electrophotographic photoconductor as claimed in claim 32, wherein said coating liquid further comprises ingredient (d): (d) finely divided silica having an average particle diameter of 1 to 100 nm, and wherein the amounts of ingredients (b) and (d) are such that the weight ratio (b)/((a)+(b)+(d)) of ingredient (b) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.1 to 0.6 and the weight ratio (d)/((a)+(b)+(d)) of ingredient (d) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.01 to 0.3. 34. A method of preparing an electrophotographic photoconductor as claimed in claim 32, wherein said solvent is at least one solvent selected from the group consisting of benzyl alcohol, cyclohexanone, 2-methoxyethyl acetate, tetrahydrofuran and acetylacetone. 35. An electrophotographic photoconductor comprising an electrically conductive substrate, a photoconductive layer provided thereon, and a resin layer comprising a crosslinked resin obtained by reacting (I) an epoxy group-containing amine compound with (II) an epoxy ring-containing silicon compound selected from the group consisting of an epoxy ring-containing alkoxysilane compound and an epoxy ring-containing silanol compound and with (III) an epoxy ring-free silicon compound selected from the group consisting of an epoxy ring-free alkoxysilane compound and an epoxy ring-free silanol compound 36. An electrophotographic photoconductor as claimed in claim 35, wherein said epoxy ring-containing silanol compound and said epoxy ring-free silanol compound are products obtained by hydrolysis of an epoxy ring-containing alkoxysilane compound and an epoxy ring-free alkoxysilane compound, respectively. 37. An electrophotographic photoconductor as claimed in claim 35, wherein said resin layer is the outermost layer of the photoconductor. 38. An electrophotographic photoconductor as claimed in claim 35, wherein said photoconductive layer comprises two or more layers and said resin layer is one of said two or more layers of said photoconductive layer. 39. An electrophotographic photoconductor as claimed in claim 35, wherein said resin layer is obtained by reacting a coating of a composition containing said epoxy group-containing amine compound, said epoxy ring-containing silicon compound and said epoxy ring-free silicon compound. 40. An electrophotographic photoconductor as claimed in claim 39, wherein said epoxy ring-containing silicon compound is an epoxy ring-containing silanol compound obtained by hydrolyzing an epoxy ring-containing alkoxysilane compound, and said epoxy ring-free silicon compound is an epoxy ring-free silanol compound obtained by hydrolyzing an epoxy ring-free alkoxysilane compound. 41. An electrophotographic photoconductor as claimed in claim 35, wherein said epoxy group-containing amine compound is a compound represented by the following formula (1): wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100. 42. An electrophotographic photoconductor as claimed in claim 35, wherein said epoxy group-containing amine compound is a compound represented by the following formula (2): wherein R4 to R25 may be the same or different and each represent a hydrogen atom, a halogen atom or an alkyl group which may have one or more substituents and n is an integer of 0 to 100. 43. An electrophotographic photoconductor as claimed in 35, wherein said epoxy ring-free alkoxysilane compound is represented by the following formula (3): wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (3), R′ represents an alkyl group, X represents a hydrolyzable group and n is an integer of 0 to 3. 44. An electrophotographic photoconductor as claimed in claim 43, wherein said epoxy ring-free alkoxysilane compound is a mixture of compounds of the formula (3) having different numbers of n. 45. An electrophotographic photoconductor as claimed in claim 43, wherein said epoxy ring-free silanol compound is represented by the following formula (4): wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (4), Y represents a hydroxyl group or a hydrolyzable group and n is an integer of 0 to 3. 46. An electrophotographic photoconductor as claimed in claim 45, wherein said epoxy ring-free silanol compound is a mixture of compounds of the formula (4) having different numbers of n. 47. An electrophotographic photoconductor as claimed in claim 43, wherein at least one of said epoxy ring-free alkoxysilane compound and said epoxy ring-free silanol compound has at least one aromatic group. 48. An electrophotographic photoconductor as claimed in 35, wherein said epoxy ring-containing alkoxysilane compound is represented by the following formula (6): wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (6), R′ represents an alkyl group, E represents an epoxy ring-containing group, X represents a hydrolyzable group, n is an integer of 0 to 2 and m is an integer of 1 to 3. 49. An electrophotographic photoconductor as claimed in claim 35, wherein said epoxy ring-containing silanol compound is represented by the following formula (7): wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (7), E represents an epoxy ring-containing group, Y represents a hydroxyl group or a hydrolyzable group, n is an integer of 0 to 2 and m is an integer of 1 to 3. 50. An electrophotographic photoconductor having a layer comprising a crosslinked silicone resin having —[O—CH2—CH(OL1)]p—Z groups bonded to silicon atoms of the resin, wherein Z represents a charge transferability-imparting group, L1 represents a hydrogen atom or a bond connected to a silicon atom of the resin and p is an integer of 1 or more. 51. An electrophotographic photoconductor having a layer comprising a crosslinked silicone resin comprising a group of the following formula: bonded to silicon atoms of said resin, wherein Q1 represents a hydrogen atom and Q2 represents an oxyalkylene group or an alkylene group, or Q1 and Q2 are taken in combination to represent a cycloalkylene group or a cycloalkylenealkylene group and L2 represents a hydrogen atom or a bond connected to a silicon atom of said resin, and —[O—CH2—CH(OL1)]p—Z groups bonded to silicon atoms of the resin, wherein Z represents a charge transferability-imparting group, L1 represents a hydrogen atom or a bond connected to a silicon atom of the resin and p is an integer of 1 or more. 52. A process cartridge detachable from an image forming apparatus, comprising a photoconductor according to claim 3, and at least one member selected from the group consisting of a charger, an image exposure device, a developing device, an image transfer member, and a cleaning device.
BACKGROUND OF THE INVENTION [0001] 1. Field of the Invention [0002] This invention relates to an electrophotographic photoconductor for use in image forming machines such as printers, copying machines and facsimile machines. The present invention is also directed to a method of preparing an electrophotographic photoconductor. [0003] 2. Description of the Related Art [0004] Recent development of information processing systems using electrophotography is striking. In particular, laser printers and digital copying machines in which information is recorded using light as digital signals have shown significant improvement in image quality and reliability. Further, such an improvement is now coupled with high speed recording technique to provide full color laser printers and full color digital copying machines. In this circumstance, a need exists for an electrophotographic photoconductor which can provide high quality images and which has high durability. [0005] As to an electrophotographic photoconductor for use in laser printers and digital copying machines, the recent trend is toward the use of organic photoconductive materials for reasons of their low costs, good productivity and freedom of pollution. Typical examples of known organic electrophotographic photoconductors include those using a photoconductive resin such as polyvinylcarbazole (PVK), those using a charge transport complex such as 2,4,7-trinitrofluorenone (PVK-TNF), those using a dispersed pigment such as phthalocyanine-binder, and those of a function-separation type using a combination of a charge generation material and a charge transport material. Above all, the function-separation type electrophotographic photoconductor is currently dominant. [0006] The mechanism of forming electrostatic latent images using the function-separation type electrophotographic photoconductor is as follows. First, a surface of the photoconductor is charged and thereafter exposed to light images. The light passes through the charge transport layer and enters the charge generation layer so that a charge generation material contained therein absorbs the light, whereupon a charge carrier is produced from the charge generation material. The charge carrier is injected into the charge transport layer and travels along an electric field generated by the charging step to neutralize the surface charge of the photoconductor. As a result, electrostatic latent images are formed on the surface of the photoconductor. [0007] In general, the organic electrophotographic photoconductors have drawbacks because the surface thereof is apt to be abraded upon repeated use, which causes a reduction of the charge potential and the light sensitivity thereof as well as injuries of the surface thereof, resulting in deterioration of the image quality such as an increase of background stains and a reduction of image density. For this reason, it is one of the important problems to provide an electrophotographic photoconductor having high durability. Recent demand for high speed and compact image forming apparatuses also calls for high durability of the photoconductor. The organic electrophotographic photoconductors have additional drawbacks because cracks are apt to form when foreign matters such as lipids derived from human hands deposit on a surface thereof and when crystallization of the photoconductive material occurs on the deposited area. [0008] To cope with these problems, a method has been proposed in which a protective layer is provided on the top surface layer of the photoconductor. The protective layer may be lubricated, cured, or added with a filler. For example, Japanese Laid-Open Patent Publications No. 07-295248, No. 07-301936 and No. 08-082940 disclose incorporating a fluorine-modified silicone oil into the outermost surface layer of a photoconductor for the purpose of improving surface characteristics such as wear resistance thereof. However, the fluorine-modified silicone oil tends to be lost during repeated use and fails to maintain its effect for a long time. [0009] A proposal has been made to incorporate an inorganic filler or crosslinked resin particles in the outermost layer of an organic electrophotographic photoconductor to improve the abrasion resistance. The use of the filler, however, adversely affects the charging potential and residual potential and causes a problem that the potential greatly varies upon repeated use of the photoconductor. [0010] Also proposed is the use of a thermosetting resin in the outermost layer. In particular, much attention is being paid on a three-dimensionally crosslinked resin containing a charge transferability-imparting skeleton in view of its good electrophotographic properties and good wear resistance. For example, Japanese Laid-Open Patent Publication No. H09-190004 discloses the use of organic silicon-modified positive hole transporting compound in which a silicon compound having a hydrolyzable group is directly introduced into an charge transporting material. Japanese Laid-Open Patent Publication No. 2000-171990 suggests the use of an outermost layer in which a charge transporting compound having a hydroxyl group, an amino group or a thiol group capable of condensing with a silanol group is introduced into a three-dimensionally crosslinked siloxane layer. Japanese Laid-Open Patent Publication No. 2000-206715 proposes the use of a three-dimensionally crosslinked layer obtained from an acrylic compound and a charge transporting material having at least two chain-polymerizable groups. [0011] The electrophotographic photoconductor of Japanese Laid-Open Patent Publication No. H09-190004, however, has a problem that it is difficult to synthesize and purify the organic silicon-modified positive hole transporting compound. An unpurified product causes a reduction in layer strength and adversely affects the electrophotographic properties. The photoconductor of Japanese Laid-Open Patent Publication No. 2000-171990 has drawbacks that the charge transporting compound having incorporated thereinto a reactive group has poor compatibility and the mechanical strength of a layer obtained therefrom are not satisfactory. In the case of the photoconductor of Japanese Laid-Open Patent Publication No. 2000-206715, the residual chain-polymerizable groups adversely affect the resistance to gases and the mechanical strengths of a layer obtained therefrom. SUMMARY OF THE INVENTION [0012] It is, therefore, an object of the present invention to provide an electrophotographic photoconductor which has solved the above-mentioned drawbacks. [0013] Another object of the present invention is to provide an electrophotographic photoconductor which has high resistance to wear and a long service life and which can give high quality image for a long period of time. [0014] It is a further object of the present invention to provide an electrophotographic photoconductor which has high scratch resistance, which exhibits good charge-ability, which has low residual potential after light exposure, which is small in variation of charging potential and residual potential upon repeated use, which can withstand charging hazard and which hardly causes formation of abnormal images. [0015] It is a further object of the present invention to provide a method of fabricating an electrophotographic photoconductor of the above-mentioned type. [0016] In accomplishing the foregoing objects, there is provided in accordance with one aspect of the present invention an electrophotographic photoconductor having a layer comprising a crosslinked resin formed by condensation of silanol groups, and charge transferability-imparting groups each bonded to a silanol group of said resin through an epoxy group. [0017] In another aspect, the present invention provides an electrophotographic photoconductor having a layer comprising a crosslinked resin containing a first chain formed by condensation of silanol groups and a second chain formed by addition of a silanol group to an epoxy group, and charge transferability-imparting groups each bonded to a silanol group of said resin through an epoxy group. [0018] The present invention further provides an electrophotographic photoconductor having a layer comprising a crosslinked silicone resin having —O—CH2—CH(OL1)-Z groups bonded to silicon atoms of said resin, wherein Z represents a charge transferability-imparting group and L1 represents a hydrogen atom or a bond connected to a silicon atom of said resin. [0019] The present invention further provides an electrophotographic photoconductor having a layer comprising a crosslinked silicone resin comprising a group of the following formula: [0020] bonded to silicon atoms of said resin, wherein Q1 represents a hydrogen atom and Q2 represents an oxyalkylene group or an alkylene group, or Q1 and Q2 are taken in combination to represent a cycloalkylene group or a cycloalkylenealkylene group and L2 represents a hydrogen atom or a bond connected to a silicon atom of said resin, and —[O—CH2—CH(OL1)]p-Z groups bonded to silicon atoms of the resin, wherein Z represents a charge transferability-imparting group, L1 represents a hydrogen atom or a bond connected to a silicon atom of the resin and p is an integer of 1 or more. [0021] The present invention further provides an electrophotographic photoconductor having a layer of a crosslinked resin obtained by reacting an epoxy group-containing amine compound having a charge transferability-imparting group with at least one silicon compound selected from the group consisting of an epoxy ring-free alkoxysilane compound, an epoxy ring-free silanol compound, an epoxy ring-containing alkoxysilane compound and an epoxy ring-containing silanol compound. [0022] The present invention further provides an electrophotographic photoconductor comprising an electrically conductive substrate, a photoconductive layer provided thereon, and a resin layer comprising a crosslinked resin obtained by reacting an epoxy group-containing amine compound with an epoxy ring-free silicon compound selected from the group consisting of an alkoxysilane compound and a silanol compound. [0023] The present invention further provides a method of preparing an electrophotographic photoconductor, comprising the steps of: [0024] providing a coating liquid comprising the following ingredients (a), (b) and (c) dissolved and/or dispersed in a solvent: [0025] (a) a silane compound having at least one hydroxyl group bonded to the silicon atom thereof; [0026] (b) an epoxy group-containing amine compound represented by the following formula (1): [0027] wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100; [0028] (c) an aluminum chelate compound of the following formula: AlX1 nY1 3-n [0029] wherein X1 represents a lower alkoxy group Y represents a ligand derived from a compound selected from the group consisting of M1COCH2COM2 and M3COCH2COOM4 where M1, M2, M3 and M4 independently represent a lower alkyl group, and n is an integer of 0 to 2, [0030] wherein the amount of ingredient (b) is such that the weight ratio (b)/((a)+(b)) of the ingredient (b) to a total amount of the ingredients (a) and (b) is in the range of 0.1 to 0.7; [0031] applying the coating liquid to form a coating; and [0032] heating the coating at a temperature of 80 to 150� C. to harden the coating. [0033] The present invention further provides an electrophotographic photoconductor comprising an electrically conductive substrate, a photoconductive layer provided thereon, and a resin layer comprising a crosslinked resin obtained by reacting an epoxy group-containing amine compound with an epoxy ring-containing silicon compound selected from the group consisting of an epoxy ring-containing alkoxysilane compound and an epoxy ring-containing silanol compound. [0034] The present invention further provides a method of preparing an electrophotographic photoconductor, comprising the steps of: [0035] providing a coating liquid comprising the following ingredients (a), (b) and (c) dissolved and/or dispersed in a solvent: [0036] (a) a silane compound having at least one an epoxy group and at least one hydroxyl group bonded to the silicon atom thereof; [0037] (b) an epoxy group-containing amine compound represented by the following formula (1): [0038] wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100; [0039] (c) an aluminum chelate compound of the following formula: AlX1 nY1 3−n [0040] wherein X1 represents a lower alkoxy group Y1 represents a ligand derived from a compound selected from the group consisting of M1COCH2COM2 and M3COCH2COOM4 where M1, M2, M3 and M4 independently represent a lower alkyl group, and n is an integer of 0 to 2, [0041] wherein the amount of ingredient (b) is such that the weight ratio (b)/((a)+(b)) of the ingredient (b) to a total amount of the ingredients (a) and (b) is in the range of 0.1 to 0.7; [0042] applying the coating liquid to form a coating; and [0043] heating the coating at a temperature of 80 to 150� C. to harden the coating. [0044] The present invention further provides an electrophotographic photoconductor comprising an electrically conductive substrate, a photoconductive layer provided thereon, and a resin layer comprising a crosslinked resin obtained by reacting (I) an epoxy group-containing amine compound with (II) an epoxy ring-containing silicon compound selected from the group consisting of an epoxy ring-containing alkoxysilane compound and an epoxy ring-containing silanol compound and with (III) an epoxy ring-free silicon compound selected from the group consisting of an epoxy ring-free alkoxysilane compound and an epoxy ring-free silanol compound.
BRIEF DESCRIPTION OF DRAWINGS [0045] Other objects, features and advantages of the present invention will become apparent from the detailed description of the preferred embodiments of the invention which follows, when considered in the light of the accompanying drawings, in which: [0046] [0046]FIG. 1 is a schematic view showing an image forming apparatus according to the present invention; and [0047] [0047]FIG. 2 is a schematic view showing an example of a process cartridge according to the present invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION [0048] An electrophotographic photoconductor according to a first aspect of the present invention comprises a resin layer containing a crosslinked resin formed by condensation of silanol groups, and charge transferability-imparting groups each bonded to a silanol group of the resin through an epoxy group. [0049] The crosslinked resin is a three-dimensionally crosslinked resin formed as a result of condensation of silanol groups of a silane compound having three hydroxyl groups bonded to a silicon atom thereof in the presence or absence of one or more other silane compounds having at least one hydroxyl group bonded to a silicon atom thereof. The above condensation is carried out in the presence of a compound having an epoxy group and a charge transferability-imparting group so that the charge transferability-imparting group is bonded to the resin by reaction of the epoxy group with a silanol group of the resin. [0050] In one specific embodiment of the first aspect of the present invention, the electrophotographic photoconductor has a resin layer containing a crosslinked silicone resin having —[O—CH2—CH(OL1)]p—Z groups bonded to silicon atoms of the resin, wherein Z represents a charge transferability-imparting group, L1 represents a hydrogen atom or a bond connected to a silicon atom of the resin and p is an integer of at least 1, preferably 2 or more. The charge transferability-imparting group is suitably an nitrogen-containing group. [0051] In another embodiment of the first aspect of the present invention, the electrophotographic photoconductor comprises an electrically conductive substrate, a photoconductive layer provided thereon, and a resin layer comprising a crosslinked resin obtained by reacting an epoxy group-containing amine compound with an epoxy ring-free silicon compound selected from the group consisting of an alkoxysilane compound and a silanol compound. The silanol compound may be a product obtained by hydrolysis of an alkoxysilane compound. [0052] The epoxy group-containing amine compound preferably has a skeleton similar to a charge transport compound generally used as a charge transport material of an electrophotographic photoconductor, such as an oxazole compound, an oxadiazole compound, an imidazole compound, a triarylamine compound (e.g. triphenyl amine), a phenylhydrazine compound, an α-phenyl stilbene compound, a stilbene compound, a benzoimidazole compound or an N-phenylcarbazole compound. The epoxy group-containing amine compound has at least one epoxy group such as a terminal glycidyl group. The epoxy group-containing amine compound has preferably two or more epoxy groups for reasons of obtaining a high crosslinking degree and high wear resistance. It is preferred that the epoxy group-containing amine compound be used in an amount of at least 20% by weight based on a total weight of the epoxy group-containing amine compound and the epoxy ring-free silicon compound for reasons of obtaining satisfactory charge transporting properties. [0053] The epoxy group-containing amine compound is preferably a compound represented by the following formula (1): [0054] wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100. [0055] In particular, a compound represented by the following formula (2) is preferably used for the purpose of the present invention: [0056] wherein R4 to R25 may be the same or different and each represent a hydrogen atom, a halogen atom or an alkyl group which may have one or more substituents and n is an integer of 0 to 100. The epoxy group-containing amine compounds of the formulas (1) and (2) above, which are novel compounds, may be prepared by reacting the corresponding hydroxyl compounds with a glycidylating agent. [0057] In the epoxy group-containing amine compounds of the above formulas (1) and (2) above, each of the alkyl groups R1 and R4 to R25 may be a linear or branched alkyl group which has preferably 1 to 5 carbon atoms and which may have one or more substituents such as a halogen atom (e.g. chlorine, fluorine, bromine or iodine), an aryl group (e.g. phenyl or naphthyl) or an aralkyl group (e.g. benzyl). Each of the aryl and aralkyl groups may have a substituent such as a halogen atom or an alkyl group having 1 to 5 carbon atoms. Specific examples of the alkyl groups R1 and R4 to R25 include methyl, ethyl, n-propyl, i-propyl, t-butyl, s-butyl, n-butyl, i-butyl, n-pentyl, trifluoromethyl, phenyl, chlorophenyl, benzyl, 4-chlorobenzyl and 4-methylbenzyl. [0058] The aryl group represented by R1 may be, for example, phenyl, naphthyl, biphenylyl, terphenylyl, pyrenyl, fluorenyl, 9,9-dimethyl-2-fluorenyl, azulenyl, anthryl, triphenyl or crysenyl. The aryl group may have one or more substituents such as a halogen atom (e.g. chlorine, fluorine, bromine or iodine), an alkyl group (e.g. C1 to C5 alkyl group) an aryl group (e.g. phenyl or naphthyl) or an aralkyl group (e.g. benzyl). [0059] The aryl group represented by R1 may also be a group of the following formula (5): [0060] wherein R26 represents a hydrogen atom, a halogen atom, an alkyl group which may have one or more substituents, an aryl group which may have one or more substituents or an aralkyl group which may have one or more substituents, and X represents —O—, —S—, —SO—, —SO2—, —CO—, an alkylene which may have one or more substituents or an alkylene of the formula: [0061] where R27 represents a hydrogen atom, a halogen atom, an alkyl group which may have one or more substituents, an aryl group which may have one or more substituents or an aralkyl group which may have one or more substituents, and b is an integer of 1 to 3. [0062] The alkylene represented by X preferably has 1-12 carbon atoms such as methylene, ethylene, propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene, decylene, undecylene or dodecylene. Examples of the substituent for the alkyl group, aryl group and aralkyl group of R26 and R27 include those described above with reference to the groups R1 and R4 to R25. The substituent of the alkylene group of X may be a halogen atom, an alkyl group (e.g. C1 to C5 alkyl group) an aryl group (e.g. phenyl or naphthyl) or an aralkyl group (e.g. benzyl). [0063] In the epoxy group-containing amine compounds of the above formula (1) above, the aryl group of the tertiary amino group-containing aryl group Ar1 may be the same as that described above in connection with the group R1. The tertiary amino group may be a group of the formula —X2—N(Ar5)(Ar6) where X2 represents a divalent organic group such as an alkylene group having one or more substituents, an alkenylene group having one or more substituents, an arylene group having one or more substituents and an aralkylene group having one or more substituents, and Ar5 and Ar6 independently represent an aryl group such as phenyl having one or more substituents. [0064] The substituent for each of the groups X2, Ar5 and Ar6 may be a halogen atom or an alkyl group which may have one or more substituents. The alkyl group may be a linear or branched alkyl group which has preferably 1 to 5 carbon atoms and which may have one or more substituents such as a halogen atom (e.g. chlorine, fluorine, bromine or iodine), an aryl group (e.g. phenyl or naphthyl) or an aralkyl group (e.g. benzyl). [0065] In the epoxy group-containing amine compounds of the above formula (1) above, each of the arylene groups Ar2 and Ar3 may be, for example, phenylene, naphthylene, biphenylylene, terphenylylene, pyrenylene, fluorenylene, 9,9-dimethyl-2-fluorenylene, azulenylene, anthrylene, triphenylene or crysenylene. The arylene group may have one or more substituents such as a halogen atom (e.g. chlorine, fluorine, bromine or iodine), an alkyl group (e.g. C1 to C5 alkyl group) an aryl group (e.g. phenyl or naphthyl) or an aralkyl group (e.g. benzyl). [0066] In the epoxy group-containing amine compounds of the above formula (1) above, the heterocyclic group of the tertiary amino group-containing heterocyclic group Ar1 may be, for example, pyrrole, pyrazole, imidazole, triazole, dioxazole, indole, isoindole, benzimidazole, benzotriazole, benzisoxazine, carbazole or phenoxazine. The heterocyclic group may have one or more substituents such as a halogen atom (e.g. chlorine, fluorine, bromine or iodine), an aryl group (e.g. phenyl or naphthyl) or an aralkyl group (e.g. benzyl). Each of the aryl and aralkyl groups may have a substituent such as a halogen atom or an alkyl group having 1 to 5 carbon atoms. Examples of the tertiary amino group include those described above in connection with the tertiary amino group-containing aryl group. [0067] The alkoxysilane compound to be reacted with the epoxy group-containing amine compound may be, for example, a compound represented by the following formula (3): [0068] wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (3), R′ represents an alkyl group, X represents a hydrolyzable group and n is an integer of 0 to 3. [0069] The organic group R may be, for example, an alkyl group, preferably a lower alkyl group, which may have one or more substituents, an aryl group which may have one or more substituents or an aralkyl group which may have one or more substituents. The substituent of each of the alkyl group, aryl group and aralkyl group may be, for example, a halogen atom, a nitro group, a cyano group or an alkyl group having 1 to 5 carbon atoms. Specific examples of the organic group R include methyl, ethyl, propyl, butyl, phenyl, naphthyl, biphenyl, tolyl, benzyl, γ-chloropropyl, 1,1,1-trifluoropropyl, nonafluorohexyl and perfluorooctyl. [0070] The alkyl group R′ is preferably a lower alkyl group having 1 to 8 carbon atoms, more preferably 1 to 6 carbon atoms. The hydrolyzable group X may be, for example, an alkoxyl group, a halogen atom or an acyloxy group. An alkoxyl group having 1 to 6 carbon atoms is preferably used as the hydrolyzable group X. If desired a mixture of the alkoxysilane compounds of the formula (3) having different alkyl groups R′ and/or different hydrolyzable groups X may be used. [0071] The silanol compound to be reacted with the epoxy group-containing amine compound may be, for example, a compound represented by the following formula (4): [0072] wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (4), Y represents a hydroxyl group or a hydrolyzable group and n is an integer of 0 to 3. Examples of the organic group R and the hydrolyzable group Y in the formula (4) include those described above with reference to the alkoxysilane compound of the formula (3). [0073] When n of the organic silicon compound of the formula (3) or (4) is 2 or more, the two or three groups R may be the same or different. Similarly, when n is 1 or less, the two or three groups X or Y may be the same or different. [0074] The resin layer of an electrophotographic photoconductor according to the present invention may be a layer obtained by reacting a coating of a composition containing the above epoxy group-containing amine compound and the silicon compound. The reaction of the coating may be carried out by heating the coating at a temperature of at least 100� C. In this case, it is preferred that at least one of the alkoxysilane compound and the silanol compound has at least one group R which is an aromatic group for reasons of improving the uniformity and transparency of the resin layer. It is still preferred that the aromatic group-containing alkoxysilane compound and/or silanol compound be used in conjunction with an aromatic group-free alkoxysilane compound and/or silanol compound. [0075] When n of the organic silicon compound of the formula (3) or (4) is 2 or less, the silicon compound undergoes condensation to form an organopolysiloxane resin. When n is 2, a three-dimensionally crosslinked organopolysiloxane resin (silicone resin) is obtained. Thus, it is preferred that the organic silicon compound used as a raw material contain a trifunctional silane monomer. By using the trifunctional silane monomer in conjunction with a mono- di- and/or tetrafunctional silane monomers, characteristics such as stability and mechanical strengths of the resin layer can be controlled. [0076] The reaction of the epoxy group-containing amine compound with the alkoxysilane compound involves (1) condensation between alkoxysilane molecules, (2) condensation between alkoxysilane and silanol produced by hydrolysis of the alkoxysilane, (3) condensation between silanol molecules produced by hydrolysis of the alkoxysilane, (4) addition of the epoxy group of the epoxy group-containing amine to silanol and (5) condensation of the hydroxyl group formed as a result of the ring-opening addition reaction of the epoxy group with silanol and results in a three-dimensionally crosslinked silicone resin. Similarly, the reaction of the epoxy group-containing amine compound with the silanol compound involves (1) condensation between silanol molecules, (2) addition of the epoxy group of the epoxy group-containing amine to silanol and (3) condensation of the hydroxyl group formed as a result of the ring-opening addition reaction of the epoxy group with silanol and results in a three-dimensionally crosslinked silicone resin. [0077] The coating composition containing the above epoxy group-containing amine compound and the silicon compound for forming the resin layer may be prepared by blending the epoxy group-containing amine compound, the silicon compound, a suitable solvent and, optionally, a catalyst for accelerating the crosslinking. In this case, the silicon compound of the formula (3) and/or (4) may be previously subjected to a hydrolysis treatment for hydrolyzing the hydrolyzable groups X and Y and the alkoxyl group OR′ under acidic or alkaline conditions. Alternatively, the coating composition formulated may be subjected to hydrolysis prior to the coating step. Hydrolysis may also be carried out after the coating step at the time the crosslinking is performed. [0078] In one preferred embodiment, the silicon compound of the formula (3) and/or (4) may be hydrolyzed in water or in an aqueous solution containing an acid, such as hydrochloric acid, sulfuric acid or acetic acid, by it self or in the presence of a suitable solvent. When a plurality of the silicon compounds are used in combination, they may be first hydrolyzed separately and then mixed with each other. In an alternate, they may be first mixed with each other and the mixture is then subjected to hydrolysis. Further, they may be successively mixed after the silicon compound previously added has been hydrolyzed. [0079] The solvent used for the coating composition is suitably a mixed solvent containing an alcohol solvent and at least one additional solvent such as an aromatic solvent, a ketone solvent, an ester solvent and ether solvent. Illustrative of suitable alcohol solvents are methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, t-butanol and benzyl alcohol. Illustrative of suitable aromatic solvents are toluene and xylene. Illustrative of suitable ketone solvents are methyl ethyl ketone, methyl isobutyl ketone, acetone, acetylacetone and cyclohexanone. Illustrative of suitable ester solvents are ethyl acetate, 2-methoxyethyl acetate and t-butyl acetate. Illustrative of suitable ether solvents are methyl cellosolve, ethyl cellosolve, diethyl ether, dibutyl ether, dipropyl ether, tetrahydrofuran, 1,4-dioxane and 1,3-dioxolane. [0080] While a variety of solvents may be used for the preparation of the coating composition, it is desirable that the solvent be able to dissolve the silicon compounds and epoxy group-containing amine compound and have a relatively high boiling point for reasons of formation of a uniform crosslinked resin layer. Examples of such a solvent include butanol, benzyl alcohol, cyclohexanone, 2-methoxyethyl acetate, tetrahydrofuran and acetylacetone. Benzyl alcohol and cyclohexanone are especially preferably used. The amount of the solvent in the coating composition varies depending upon the structures of the silicon compound and epoxy group-containing amine compound and the coating method adopted but is generally such that the solid content of the coating composition is in the range of 2 to 50% by weight. [0081] As the catalyst for acceleration of the crosslinking, there may be mentioned alkali metal salts of organic carboxylic acids, nitrous acid, sulfurous acid, aluminic acid, carbonic acid and thiocyanic acid; organic amine salts such as tetramethylammonium hydroxide and tetramethylammonium acetate; organic acid salts of tin such as stannous octoate, dibutyl tin diacetate, dibutyl tin dilaurate, dibutyl tin mercaptide, dibutyl tin thiocarboxylate and dibutyl tin malleate; aluminum salts of octenic acid and naphthenic acid; zinc salts of octenic acid and naphthenic acid; and acetylacetone complexes of aluminum and zinc. The catalyst is preferably used in an amount of 0.1 to 10 parts by weight per 100 parts by weight of the silicon compound. [0082] Above all, the use of an aluminum chelate compound of the following formula: AlX1 nY1 3−n [0083] wherein X1 represents a lower alkoxy group Y1 represents a ligand derived from a compound selected from the group consisting of M1COCH2COM2 and M3COCH2COOM4 where M1, M2, M3 and M4 independently represent a lower alkyl group, and n is an integer of 0 to 2, is preferable for reasons of long pot life of the coating composition. Namely, the above aluminum chelate does not catalyze the crosslinking at ambient temperature but can accelerate the crosslinking at an elevated temperature. For reasons of catalytic activity, solubility and stability, the use of aluminum acetylacetonate, aluminum ethylacetoacetate bisacetylacetonate, aluminum bisacetoacetate acetylacetonate, aluminum di-n-butoxide monoethylacetoacetate, aluminum di-i-propoxide monomethylacetoacetate or a mixture thereof is particularly preferably used. [0084] The coating composition may suitably additionally contain a colloidal metal oxide such as colloidal silica or colloidal alumina for reasons of improved film forming property, improved hardness and improved resistance to scratch and prevention of cracks in the resin layer. Preferably used is colloidal silica in the form of an aqueous or alcoholic sol having a particle diameter of 100 nm or less, more preferably 50 nm or less. Fine silica particles having an average particle diameter of 1 to 100 nm may also be used as the colloidal silica. The colloidal silica is generally used in an amount of 1 to 30% by weight based on the weight of the resin layer. [0085] The coating composition may further contain various additives customarily used in known electrophotographic photoconductors, such as an antioxidant (e.g. sterically hindered amine or sterically hindered phenol), a lubricant such as silicone oil, a positive hole transporting agent such as an amine compound and an electron transporting agent such as a quinone. [0086] A coating of the above coating composition is dried to obtain a crosslinked resin layer. The drying conditions vary depending upon the kind of the solvent used, presence or absence of catalyst, etc., but are generally 60 to 160� C. for 10 minutes to 5 hours, preferably 80 to 150� C. for 20 minutes to 3 hours, more preferably 100 to 150� C. for 30 minutes to 2 hours, for reasons of formation of sufficient crosslinkages and prevention of thermal degradation of components of the resin layer. [0087] In one preferred embodiment of the first aspect of the present invention, the resin layer of an electrophotographic photoconductor of the present invention is a hardened layer of a composition which includes the following ingredients (a), (b) and (c): [0088] (a) a silane compound having at least one hydroxyl group bonded to the silicon atom thereof; [0089] (b) an epoxy group-containing amine compound represented by the following formula (1): [0090] wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100; [0091] (c) an aluminum chelate compound of the following formula: AlX1 nY1 3−n [0092] wherein X1 represents a lower alkoxy group Y1 represents a ligand derived from a compound selected from the group consisting of M1 COCH2COOM2 and M3COCH2COOM4 where M1, M2, M3 and M4 independently represent a lower alkyl group, and n is an integer of 0 to 2, [0093] wherein the amount of ingredient (b) is such that the weight ratio (b)/((a)+(b)) of the ingredient (b) to a total amount of the ingredients (a) and (b) is in the range of 0.1 to 0.7. [0094] The ingredient (a) is a hydrolyzed product of the silicon compound of the formula (3) and/or (4). The weight ratio (b)/((a)+(b)) in the range of 0.1 to 0.7 is desired to provide a resin layer having high mechanical strengths such as wear resistance and to prevent an increase of residual potential or a reduction of sensitivity of the photoconductor. The ingredient (c) is generally used in an amount of 0.01 to 30 parts by weight per 100 parts by weight of a total amount of ingredients (a) and (b). [0095] In the above embodiment, the composition of the hardened layer preferably includes the following ingredient (d): [0096] (d) finely divided silica having an average particle diameter of 1 to 100 nm, [0097] wherein the amounts of ingredients (b) and (d) are such that the weight ratio (b)/((a)+(b)+(d)) of ingredient (b) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.1 to 0.6 and the weight ratio (d)/((a)+(b)+(d)) of ingredient (d) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.01 to 0.3. [0098] The weight ratio (b)/((a)+(b)+(d)) in the range of 0.1 to 0.6 is desired to provide a resin layer having high mechanical strengths such as wear resistance and to prevent an increase of residual potential or a reduction of sensitivity of the photoconductor. The weight ratio (d)/((a)+(b)+(d)) of 0.01 to 0.3 is desired to provide a resin layer having high mechanical strengths such as wear resistance and to prevent formation of cracks of the resin layer and a reduction of resolution of the photoconductor. The ingredient (c) is generally used in an amount of 0.01 to 30 parts by weight per 100 parts by weight of a total amount of ingredients (a), (b) and (d). [0099] An electrophotographic photoconductor according to a second aspect of the present invention comprises a layer containing a crosslinked resin having a first chain or moiety formed by condensation of silanol groups and a second chain or moiety formed by addition of a silanol group to an epoxy group, and charge transferability-imparting groups each bonded to a silanol group of the resin through an epoxy group. [0100] The crosslinked resin of the second aspect is a three-dimensionally crosslinked resin formed as a result of condensation of silanol groups and addition of a silanol group to an epoxy group. The above condensation and addition reactions are carried out in the presence of a compound having an epoxy group and a charge transferability-imparting group so that the charge transferability-imparting group is bonded to the resin by the reaction of the epoxy group with a silanol group of the resin. [0101] In one specific embodiment of the second aspect of the present invention, the electrophotographic photoconductor has a resin layer containing a crosslinked silicone resin having a group of the following formula: [0102] bonded to silicon atoms of the resin, wherein Q1 represents a hydrogen atom and Q2 represents an oxyalkylene group or an alkylene group, or Q1 and Q2 are taken in combination to represent a cycloalkylene group or a cycloalkylenealkylene group and L2 represents a hydrogen atom or a bond connected to a silicon atom of the resin, and [0103] —[O—CH2—CH(OL1) ]p—Z groups bonded to silicon atoms of the resin, wherein Z represents a charge transferability-imparting group, L1 represents a hydrogen atom or a bond connected to a silicon atom of the resin and p is an integer of 1 or more, preferably 2 or more. [0104] In another embodiment of the second aspect of the present invention, the electrophotographic photoconductor comprises an electrically conductive substrate, a photoconductive layer provided thereon, and a resin layer comprising a crosslinked resin obtained by reacting an epoxy group-containing amine compound with an epoxy ring-containing silicon compound selected from the group consisting of an epoxy ring-containing alkoxysilane compound and an epoxy ring-containing silanol compound. The epoxy ring-containing silanol compound may be a product obtained by hydrolysis of an epoxy ring-containing alkoxysilane compound. [0105] The epoxy group-containing amine compound may be the same as that described above with reference to the first aspect of the present invention. [0106] The epoxy ring-containing silicon compound to be reacted with the epoxy group-containing amine compound may be, for example, an epoxy ring-containing alkoxysilane compound represented by the following formula (6): [0107] wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (6), R′ represents an alkyl group, E represents an epoxy ring-containing group, X represents a hydrolyzable group, n is an integer of 0 to 2 and m is an integer of 1 to 3. The epoxy ring-containing silicon compound to be reacted with the epoxy group-containing amine compound may also be, for example, an epoxy ring-containing silanol compound represented by the following formula (7): [0108] wherein R represents an organic group having a carbon atom bonded to the Si atom of the formula (7), E represents an epoxy ring-containing group, Y represents a hydroxyl group or a hydrolyzable group, n is an integer of 0 to 2 and m is an integer of 1 to 3. When n of the epoxy ring-containing silicon compound of the formula (6) or (7) is 2, the two groups R may be the same or different. Similarly, when n is zero and m is 1, the two groups X or Y may be the same or different. Further, when m is 2 or 3, the two or three groups E may be the same or different. [0109] The organic group R, the alkyl group R′ and the hydrolyzable groups X and Y may be the same as those described with reference to the silicon compounds of the formulas (3) and (4) above. The epoxy ring-containing group E may be, for example, a glycidyl group, a glycidoxy group, a glycidylalkyl group preferably having 3 to 10 carbon atoms, a glycidoxyalkyl group preferably having 3 to 10 carbon atoms, an epoxycyloalkyl group preferably having 3 to 12 carbon atoms, such as a cyclohexene oxide group, a tricyclodecene oxide group or a cyclopentene oxide group or an epoxycycloalkylalkyl group preferably having 3 to 15 carbon atoms. [0110] Specific examples of the epoxy ring-containing alkoxysilane compound include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyldimethylmethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropylmethyldiethoxysilane, 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, 2-(3,4-epoxycyclohexyl)ethyltriethoxysilane, and 5,6-epoxyhexyltriethoxysilane. [0111] The epoxy ring-containing silanol compound may be a product obtained by hydrolyzing the above epoxy ring-containing alkoxysilane compound. In one preferred embodiment, the epoxy ring-containing silicon compound of the formula (6) and/or (7) may be hydrolyzed in water or in an aqueous solution containing an acid, such as hydrochloric acid, sulfuric acid or acetic acid, by it self or in the presence of a suitable solvent. When a plurality of the silicon compounds are used in combination, they may be first hydrolyzed separately and then mixed with each other. In an alternate, they may be first mixed with each other and the mixture is then subjected to hydrolysis. Further, they may be successively mixed after the silicon compound previously added has been hydrolyzed. [0112] It is preferred that the epoxy ring-containing silicon compound be used in conjunction with an epoxy ring-free silicon compound such as a silicon compound of the formula (3) or (4) above for reasons of easy control of the properties of the resin layer. [0113] Similar to the above-described first aspect, the resin layer of an electrophotographic photoconductor according to the second aspect of the present invention may be a layer obtained by reacting a coating of a composition containing the above epoxy group-containing amine compound and the epoxy ring-containing silicon compound. The reaction of the coating may be carried out by heating the coating at an elevated temperature. [0114] The reaction of the epoxy group-containing amine compound with the epoxy ring-containing silicon compound (alkoxysilane or silanol) involves (1) condensation between alkoxysilane molecules, (2) condensation between silanol molecules including those produced by hydrolysis of the alkoxysilane, (3) addition of the epoxy group of the epoxy group-containing amine to silanol, (4) ring open polymerization of the epoxy ring-containing silicon compound by addition of the epoxy group thereof to silanol and (5) condensation of the hydroxyl group formed as a result of the ring-opening addition reaction of the epoxy group with silanol, and results in a three-dimensionally crosslinked silicone resin. Similarly, the reaction of the epoxy ring-containing silicon compound (alkoxysilane or silanol) (C) with the epoxy group-containing amine compound (B) and the epoxy group-free silicon compound (alkoxysilane or silanol) (A) involves (1) condensation between alkoxysilane molecules (of C and A), (2) condensation between silanol molecules (of C and A) including those obtained by hydrolysis of the alkoxysilane (of C and A), (3) addition of the epoxy group of the epoxy group-containing amine (B) to silanol (of C and A), (4) ring open polymerization of the epoxy ring-containing silicon compound (C) by addition of the epoxy group thereof to silanol (of C and A) and (5) condensation of the hydroxyl group formed as a result of the ring-opening addition reaction of the epoxy group (of B and C) with silanol (of C and A), and results in a three-dimensionally crosslinked silicone resin. In the presence of a chain polymerization catalyst, ring opening polymerization thereof is likely to occur. [0115] The coating composition containing the above epoxy group-containing amine compound, the epoxy ring-containing silicon compound and, optionally, the epoxy group-free silicon compound for forming the resin layer may be prepared by blending the epoxy group-containing amine compound, the silicon compounds, a suitable solvent and, optionally, a catalyst for accelerating the crosslinking. In this case, the silicon compounds of the formulas (3), (4), (6) and/or (7) may be previously subjected to a hydrolysis treatment for hydrolyzing the hydrolyzable groups X and Y and the alkoxyl group OR′ under acidic or alkaline conditions. Alternatively, the coating composition formulated may be subjected to hydrolysis prior to the coating step. Hydrolysis may also be carried out after the coating step at the time the crosslinking is performed. [0116] The solvent and catalyst used in the second aspect of the present invention are similar to those described above in connection with the first aspect. Further, a catalyst for accelerating ring opening polymerization of epoxy groups may suitably incorporated into the coating composition. Such a catalyst may be, for example, a Lewis acid (e.g. SnCl2, BF3, AlCl3, PF5, AsF5 or SbF5), an amine salt or complex of BF3 or a proton acid (e.g. hydrochloric acid or sulfuric acid). Above all, the use of an amine complex is preferred for reasons of a long pot life. The ring opening polymerization catalyst is generally used in an amount of 0.1 to 10 parts by weight per 100 parts by weight of the epoxy compounds. [0117] The coating composition may suitably additionally contain a colloidal metal oxide, such as colloidal silica or colloidal alumina, and various other additives customarily used in known electrophotographic photoconductors, similar to the above-described first aspect. A coating of the above coating composition is dried to obtain a crosslinked resin layer. The drying conditions are the same as those described above in connection with the first aspect. [0118] In one preferred embodiment of the second aspect of the present invention, the resin layer of an electrophotographic photoconductor of the present invention is a hardened layer of a composition which includes the following ingredients (a), (b) and (c): [0119] (a) a silane compound having at least one epoxy group and at least one hydroxyl group bonded to the silicon atom thereof and, optionally, an epoxy group-free silane compound having at least one hydroxyl group; [0120] (b) an epoxy group-containing amine compound represented by the following formula (1): [0121] wherein R1 represents a hydrogen atom, an alkyl group which may have one or more substituents, or an aryl group which may have one or more substituents, Ar1 represents an aryl group having at least one tertiary amino group or a heterocyclic group having at least one tertiary amino group, Ar2 and Ar3 may be the same or different and each represent an arylene group which may have one or more substituents and n is an integer of 0 to 100; [0122] (c) an aluminum chelate compound of the following formula: AlX1 nY1 3−n [0123] wherein X1 represents a lower alkoxy group Y1 represents a ligand derived from a compound selected from the group consisting of M1COCH2COM2 and M3COCH2COOM4 where M1, M2, M3 and M4 independently represent a lower alkyl group, and n is an integer of 0 to 2, [0124] wherein the amount of ingredient (b) is such that the weight ratio (b)/((a)+(b)) of the ingredient (b) to a total amount of the ingredients (a) and (b) is in the range of 0.1 to 0.7. [0125] The ingredient (a) is a hydrolyzed product of the epoxy ring-containing silicon compound of the formula (6) and/or (7). The weight ratio (b)/((a)+(b)) in the range of 0.1 to 0.7 is desired to provide a resin layer having high mechanical strengths such as wear resistance and to prevent an increase of residual potential or a reduction of sensitivity of the photoconductor. The ingredient (c) is generally used in an amount of 0.01 to 30 parts by weight per 100 parts by weight of a total amount of ingredients (a) and (b). [0126] In the above embodiment, the composition of the hardened layer preferably includes the following ingredient (d): [0127] (d) finely divided silica having an average particle diameter of 1 to 100 nm, [0128] wherein the amounts of ingredients (b) and (d) are such that the weight ratio (b)/((a)+(b)+(d)) of ingredient (b) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.1 to 0.6 and the weight ratio (d)/((a)+(b)+(d)) of ingredient (d) to a total amount of the ingredients (a), (b) and (d) is in the range of 0.01 to 0.3. [0129] The weight ratio (b)/((a)+(b)+(d)) in the range of 0.1 to 0.6 is desired to provide a resin layer having high mechanical strengths such as wear resistance and to prevent an increase of residual potential or a reduction of sensitivity of the photoconductor. The weight ratio (d)/((a)+(b)+(d)) of 0.01 to 0.3 is desired to provide a resin layer having high mechanical strengths such as wear resistance and to prevent formation of cracks of the resin layer and a reduction of resolution of the photoconductor. The ingredient (c) is generally used in an amount of 0.01 to 30 parts by weight per 100 parts by weight of a total amount of ingredients (a), (b) and (d). [0130] The electrophotographic photoconductor in accordance with the first and second aspect of the present invention has a layer of a crosslinked resin obtained by reacting an epoxy group-containing amine compound having a charge transferability-imparting group with at least one silicon compound selected from the group consisting of an epoxy ring-free alkoxysilane compound, an epoxy ring-free silanol compound, an epoxy ring-containing alkoxysilane compound and an epoxy ring-containing silanol compound. [0131] The construction of the electrophotographic photoconductor according to the present invention will be described next. [0132] The electrophotographic photoconductor generally comprises an electrically conductive substrate and a photoconductive layer provided thereon. [0133] Any conventionally used conductive substrate may be used for the purpose of the present invention. A sheet or drum made of a metal such as aluminum or nickel or a composite sheet or drum composed of a paper or plastic base coated with a metal such as aluminum, nickel, chromium, nichrome, copper, silver, gold, platinum or iron, or an oxide such as tin oxide or indium oxide, by any coating method such as a vacuum deposition method or a sputtering method may be suitably used as the conductive substrate. [0134] The photoconductive layer provided on the substrate may have any desired construction. The photoconductive layer may be a mix type photoconductive layer in which a charge generating material and a charge transporting material are homogeneously dispersed, or a multi-layered photoconductive layer in which at least one charge generating material-containing layer and at least one charge transporting material-containing layer are superimposed one over the other. An undercoat layer or a liner may be suitably interposed between the conductive substrate and the photoconductive layer. It is also preferred that a surface protective layer be provided on the photoconductive layer. [0135] At least one of the above layers formed on the conductive substrate may be a layer containing the above-described crosslinked silicone resin. When the photoconductive layer has a multi-layered structure, one of the multi-layers, preferably the outermost layer of the multi-layers, may comprise the above-described crosslinked silicone resin. For reasons of obtaining excellent properties of the crosslinked silicone resin layer, it is preferred that the outermost layer of the photoconductor comprise the crosslinked silicone resin so as to function as a surface protective layer. In one typical preferred embodiment of the present invention, the photoconductor has a construction of a conductive substrate, an undercoat layer, a charge generating layer, a charge transporting layer and a surface protective layer containing the above-described crosslinked silicone resin, arranged in this order. The surface protective layer generally has a thickness of 0.1 to 15 μm, preferably 1 to 15 μm, from the standpoint of abrasion resistance and prevention of cracks and falling off. [0136] As the charge generation material used in the charge generating layer, any conventionally employed substance may be suitably used for the purpose of the present invention. Examples of the charge generation material include metal phthalocyanines such as A-type, B-type and Y-type titanylphthalocyanines and copper phthalocyanine; X-type and τ-type metal-free phthalocyanines; naphthalocyanine; mixtures of the above; azo compounds; pyrilium compounds; perylene compounds; cyanine compounds; squalerium compounds; and polycyclic quinone compounds. The charge generation material may be used by itself as the charge generating layer or may be dispersed in a binder resin. [0137] Any customarily employed charge transport material may be used in the charge transporting layer of the present invention. Examples of the positive hole transporting material include nitrogen-containing heterocyclic compounds, such as oxazole, oxadiazole, thiazole, thiadiazole, imadazole and derivatives thereof, polyarylakane compounds, hydrazone compounds, pyrazoline compounds, triarylamine compounds, styryl compounds, poly(bis)styryl compounds, styryltriphenylamine compounds, β-phenylstyryltriphenylamine compounds, butadiene compounds, hexatriene compounds, carbazole compounds and condensed polycyclic compounds. Typical examples of the electron transporting material include benzoquinone, naphthoquinone, anthraquinone, thiopyranone, fluorenone compounds, indenone compounds and indandione compounds. The charge transporting material may be dispersed in a binder resin. [0138] The binder resin used in the photoconductive layer may be, for example, a styrene resin, an acrylic resin, a methacrylic resin, a vinyl chloride resin, a vinyl acetate resin, a polyvinylbutyral resin, an epoxy resin, an urethane resin, a phenol resin, a polyester resin, an alkyd resin, a polycarbonate resin, a silicone resin, a melamine resin, or a copolymer resin containing two or more of the above resins. In addition to the above electrically insulating resins, there may be used an organic polymeric semiconductor such as poly-N-vinylcarbazole. [0139] The charge generation material is suitably used in an amount of 50 to 600 parts by weight per 100 parts by weight of the binder resin. The amount of the charge transport material is suitably in the range of 10 to 100 parts by weight per 100 parts by weight of the binder resin. The thickness of the charge generating layer is generally 0.1 to 10 μm, while that of the charge transporting layer is generally 5 to 30 μm. When the photoconductive layer is a single layer, the thickness thereof is suitably 5 to 40 μm. [0140] The photoconductive layer is generally prepared by a coating method. A solvent or dispersing medium used to dissolve or disperse the charge generation material and/or the charge transport material for the preparation of a charge generation layer coating liquid, a charge transporting layer coating liquid or a single-layer photoconductive layer coating liquid may be, for example, a hydrocarbon solvent such as toluene or xylene; a halogenated hydrocarbon solvent such as methylene chloride or 1,2-dichloroethane; a ketone solvent such as methyl ethyl ketone or cyclohexanone; an ester solvent such as ethyl acetate or butyl acetate; an alcohol solvent such as methanol, ethanol, methyl cellosolve or methyl cellosolve; an ether solvent such as tetrahydrofuran, 1,3-dioxane or 1,3-dioxoran; an amine solvent such as pyridine or diethylamine; an amide solvent such as N,N-dimethylformamide; a fatty acid solvent; a phenol or its derivative; a sulfur compound solvent such as carbon disulfide; or a phosphorus compound solvent such as triethyl phosphate. [0141] The undercoat layer may be a resin layer containing a polyamide resin, a vinyl chloride resin, a vinyl acetate resin, or a copolymer resin containing two or more of the above resins. A metal resin obtained by thermally hardening an organic metal compound such as a silane coupling agent or a titanium coupling agent may also be used for the formation of the undercoat layer. The thickness of the undercoat layer is suitably in the range of 0.01 to 15 μm. [0142] In the electrophotographic photoconductor of the present invention, an additive such as an antioxidant or a sensitizing dye may be contained in any desired layer. The antioxidant may be incorporated into a layer containing an organic material therein in order to prevent the decrease of photosensitivity and the increase of residual potential. In particular, satisfactory results can be obtained when the antioxidant is added to the layer which comprises the charge transport material. The sensitizing dye is generally added to the photoconductive layer. [0143] Any conventionally employed coating method may be suitably used for the preparation of the electrophotographic photoconductor of the present invention. Illustrative of suitable coating methods are an immersion coating method, a spray coating method and a coating method using a coating amount controlling circular coating means such as a ring shaped slide hopper coating apparatus. The spray coating and the coating using the coating amount controlling circular coating means are particularly preferably used since dissolution of the under layer may be prevented and since uniform coating may be attained. The spray coating method is described in Japanese Laid Open Patent Publications No. H03-90250 and No. H03-269238 and the coating amount controlling circular coating means is described in Japanese Laid Open Patent Publication No. S58-189061. [0144] Next, the image forming apparatus and process cartridge of the present invention will be explained with reference to the drawings. [0145] [0145]FIG. 1 is a schematic view illustrating the essential part of one embodiment of the image forming apparatus of the present invention. In FIG. 1, the reference numeral 1 denotes a cylindrical photoconductor which is the photoconductor according to the present invention as described above. In an alternate, the photoconductor 1 may be in the form of a sheet or an endless belt. Provided around the photoconductor 1 are a discharging lamp 2, a charger 3, an eraser 4, an imagewise light exposing device 5, a developing device 6 for developing an electrostatic latent image on the photoconductor 1, a pre-transfer charger 7, a transfer charger 10, a separating charger 11, a separating pick 12, a pre-cleaning charger 13, a cleaning brush 14, and a cleaning blade 15. In addition, a pair of registration rollers 8 are provided to feed a receiving sheet 9 to the space between the photoconductor 1 and the transfer charger 10 (and the separating charger 11). The photoconductor 1 is configured to rotate in the counterclockwise direction. [0146] Suitable charging devices for use as the charger 3, pre-transfer charger 7, transfer charger 10, separating charger 11, and pre-cleaning charger 13 include known charging devices such as corotrons, scorotrons, solid state chargers and charging rollers. Any known charging devices can be used as the transfer charger 10. However, the transfer device as shown in FIG. 1 (i.e., a combination of the transfer charger 10 with the separating charger 11) is preferable. Suitable light sources for use in the imagewise light exposing device 5 and the discharging lamp 2 include fluorescent lamps, tungsten lamps, halogen lamps, mercury lamps, sodium lamps, light emitting diodes (LEDs), laser diodes (LDs) and light sources using electroluminescence (EL). In addition, in order to emit light having a desired wave length range, filters such as sharp-cut filters, band pass filters, near-infrared cutting filters, dichroic filters, interference filters, color temperature converting filters and the like can be used. These light sources can also be used for the image transfer process, discharging process, and cleaning process, and a pre-exposure process which is optionally performed, if it is needed to irradiate the photoreceptor 1 with light in the processes. [0147] The surface of the photoconductor 1 is charged with the charger 3. The photoconductor 1 is exposed to imagewise light emitted by the imagewise light exposing device 5, so that an electrostatic latent image is formed on the photoconductor 1. The electrostatic latent image is then developed with a toner on a developing roller 61 in the developing device 6 to form a toner image on the photoconductor 1. The toner image is charged with the pre-transfer charger 7 to have a charge suitable for transferring. The toner image is then transferred onto the receiving sheet 9 while the receiving sheet 9 is charged with the transfer charger 10. The receiving sheet 9 is then charged with the separating charger 11 to facilitate separation from the photoconductor 1 by being released from the state in which the receiving sheet 9 and the photoconductor 1 are electrostatically adhered to each other. The receiving sheet 9 is then separated from the photoconductor 1 with the separating pick 12. After the toner image transferring process, the surface of the photoconductor 1 is cleaned using the pre-cleaning charger 13, the fur brush 14 and the cleaning blade 15. If desired, the cleaning process may be performed only by a cleaning brush. Suitable cleaning brushes include fur brushes and magnetic fur brushes. [0148] In charging process, the photoconductor 1 may be charged positively or negatively. When a latent image having a positive (negative) charge is developed with a toner having a negative (positive) charge, a positive image (i.e., the same image as the latent image) can be obtained. In contrast, when a latent image having a positive (negative) charge is developed with a toner having a positive (negative) charge, a negative image (i.e., a reversal image) can be obtained. As the developing method, known developing methods can be used. In addition, as the discharging methods, known discharging methods can also be used. [0149] The above-mentioned image forming units as shown in FIG. 1 can be fixedly incorporated in image forming apparatuses such as copying machines, facsimile machines, printers and the like. Alternatively, the image forming units can be set in an image forming apparatus in the form of a process cartridge. The process cartridge is, for example, a cartridge which includes a photoconductor and at least one device selected from a charger, a light exposing device, a developing device, a transfer device, a cleaning device, and a discharging device. [0150] [0150]FIG. 2 illustrates one embodiment of the process cartridge of the present invention. As shown in FIG. 2, a photoconductor 16, a charger 17, a developing roller 19 and a cleaning brush 20 are provided in a housing. The photoconductor 16 is charged with the charger 17 and exposed to light emitted by an imagewise light exposing device to form an electrostatic latent image thereon. The latent image is developed with a toner on the developing roller 19 to form a toner image. The toner image is transferred on a receiving material (not shown). The surface of the photoconductor is cleaned by the cleaning brush 20. [0151] The following examples will further illustrate the present invention. Parts are by weight. SYNTHESIS EXAMPLE 1 [0152] Synthesis of Epoxy Group-Containing Amine Compound: [0153] In a reactor equipped with a stirrer, a thermometer, a dropping funnel and a reflux condenser provided with a trap to remove water formed during the reaction, 19.34 g (40.0 mmol) of 4-[2,2-bis(4-hydroxyphenyl)vinyl]phenyl-bis(4-methylphenyl)amine and 37.01 g (400.0 mmol) of epichlorohydrin are charged. The mixture was heated to 110� C. with stirring under a nitrogen gas stream. Then, while maintaining the mixture in the reactor at 100 to 120� C., 19.20 g (96.0 mmol) of a 10% by weight aqueous solution of sodium hydroxide were added dropwise to the mixture through 3 hours. During the reaction, epichlorohydrin emitted overhead from the reactor was condensed and returned to the reactor, while water was trapped and discharged from the system. After the addition of the sodium hydroxide solution had been completed, the reaction mixture was further reacted for 1 hour at 110� C. The resulting reaction mixture was allowed to cool to room temperature and epichlorohydrin was removed in vacuo. The remaining mixture was mixed with toluene and the organic layer was washed with water. The washed organic layer was then dried with anhydrous magnesium sulfate. The toluene was removed by distillation in vacuo to leave 20.75 g of a yellow crude product with a yield of 87.1%. The melting point of the crude product was in the range of 111.0 to 116.0� C. This was purified by column chromatography using a toluene/ethyl acetate (20/1 vol/vol) elution liquid and then recrystallized from ethyl acetate and ethanol to obtain 15.85 g (yield 66.5%) of an epoxy group-containing amine compound of the formula shown below as light yellow needle crystals having a melting point of 128.0-129.0� C. [0154] The IR absorption spectrum (NaCl liquid film) of the product was as summarized in Table 1. The elementary analysis gave as follows. C H N measured: 80.80 6.33 2.37 calculated: 80.65 6.26 2.35 [0155] [0155] TABLE 1 Wave Trans- Number mittance Peak No. (cm−1) (%) 1 3585.2 86.6961 2 3025.78 77.3751 3 3000.69 78.4534 4 2921.63 76.9159 5 2871.49 82.2575 6 1899.54 86.7041 7 1600.63 50.3127 8 1573.63 77.7945 9 1506.13 17.2425 10 1454.06 76.0974 11 1415.49 79.7039 12 1376.93 81.8354 13 1344.14 80.3811 14 1321.00 53.3842 15 1294.00 53.0009 16 1278.57 50.7674 17 1241.93 44.2706 18 1178.29 61.4308 19 1132.01 81.0636 20 1108.87 76.6790 21 1078.01 83.8241 22 1035.59 63.6697 23 970.019 83.2446 24 916.022 75.4043 25 862.025 77.7342 26 835.026 60.4030 27 815.742 57.3333 28 765.601 80.0271 29 736.674 78.7032 30 715.461 76.4214 31 659.536 76.4833 32 611.324 59.9646 33 451.261 2.62751 34 430.048 1.46642 EXAMPLE 1 [0156] An undercoat layer coating liquid, a charge generating layer coating liquid and a charge transporting layer coating liquid, which had the compositions shown below, were coated and dried one by one to overlay an undercoat layer of 3.5 μm thick, a charge generating layer of 0.2 μm thick and a charge transporting layer of 26 μm thick on an aluminum cylinder. [Undercoat layer coating liquid] Titanium oxide 400 parts Melamine resin 40 parts Alkyd resin 60 parts 2-Butanone 500 parts [0157] [Charge Generating Layer Coating Liquid] Bisazo pigment of the formula shown below 12 parts Polyvinyl butyral resin 5 parts 2-Butanone 200 parts Tetrahydrofuran 400 parts [Charge transporting layer coating liquid] Polycarbonate resin 10 parts (Bisphenol Z-type polycarbonate resin manufactured by Teijin Kasei Inc.) Charge transporting material 10 parts having the formula shown below Tetrahydrofuran 100 parts 1% Silicone oil tetrahydrofuran solution 1 part (KF50-100CS manufactured by Shin-etsu Chemical Industry Co., Ltd.) [0158] A protective coating liquid (I) having the composition shown below was then spray-coated onto the charge transporting layer to form a protective layer having a thickness of about 3 μm and the resulting layered assembly was heated at 120� C. for 2 hours, thereby obtaining an electrophotographic photoconductor of the present invention. [Protective layer coating liquid (I)] Epoxy group-containing amine compound 4.2 parts obtained in Synthesis Example 1 above Methyltrimethoxysilane 5 parts Phenyltriethoxysilane 5 parts 1% Aqueous acetic acid solution 5.57 parts Tetrahydrofuran 30.7 parts n-Butanol 3.67 parts EXAMPLE 2 [0159] A precursor liquid for a protective layer coating liquid having the following formulation was prepared: [Precursor] Methyltrimethoxysilane 5 parts Phenyltriethoxysilane 5 parts 1% Aqueous acetic acid solution 5.57 parts Tetrahydrofuran 30.7 parts n-Butanol 3.67 parts [0160] The precursor liquid was then heated at 60� C. for 2 hours with stirring for silanolizing the methyltrimethoxysilane and phenyltriethoxysilane by hydrolysis. The resulting liquid was mixed with 4.2 parts of the epoxy group-containing amine compound obtained in Synthesis Example 1 above to obtain a protective layer coating liquid (II). An electrophotographic photoconductor was then prepared in the same manner as that in Example 1 except that the protective layer coating liquid (II) was substituted for the protective layer coating liquid (I). EXAMPLE 3 [0161] To a mixture composed of 21 parts of methyltrimethoxysilane and 21 parts of phenyltriethoxysilane, 8.16 parts of a 1% aqueous acetic acid solution were added through 25 minutes in an ice bath. The mixture was stirred at 5� C. for 30 minutes and then stirred at 24� C. for 2 hours for silanolizing the methyltrimethoxysilane and phenyltriethoxysilane by hydrolysis, thereby obtaining a hydrolyzed liquid. [0162] A protective layer coating liquid (III) having the formulation shown below was prepared. [Protective layer coating liquid (III)] Hydrolyzed liquid obtained above 3 parts Epoxy group-containing amine compound 0.98 part obtained in Synthesis Example 1 above 2-methoxyethyl acetate 2.62 parts Cyclohexanone 2.42 parts Tetrahydrofuran 0.98 part Acetylacetone 0.12 part Aluminum acetylacetonate 0.12 part [0163] An electrophotographic photoconductor was then prepared in the same manner as that in Example 1 except that the protective layer coating liquid (III) was substituted for the protective layer coating liquid (I) and that the application of the surface protective layer coating liquid (III) was carried out by ring coating. EXAMPLE 4 [0164] To a mixture composed of 21 parts of methyltrimethoxysilane and 21 parts of phenyltriethoxysilane, 8.16 parts of a 1% aqueous acetic acid solution were added through 25 minutes in an ice bath. The mixture was stirred at 5� C. for 30 minutes and then stirred at 24� C. for 2 hours for silanolizing the methyltrimethoxysilane and phenyltriethoxysilane by hydrolysis, thereby obtaining a hydrolyzed liquid. [0165] A protective layer coating liquid (IV) having the formulation shown below was prepared. [Protective layer coating liquid (IV)] Hydrolyzed liquid obtained above 2.17 parts Epoxy group-containing amine compound 0.98 part obtained in Synthesis Example 1 above Colloidal silica (average particle 2.32 parts diameter: 20 nm) dispersed in n-propylcellosolve 2-methoxyethyl acetate 1.9 parts Cyclohexanone 1.63 parts Tetrahydrofuran 0.98 part Acetylacetone 0.09 part Aluminum acetylacetonate 0.09 part [0166] An electrophotographic photoconductor was then prepared in the same manner as that in Example 1 except that the surface protective layer coating liquid (IV) was substituted for the protective layer coating liquid (I), that the application of the surface protective layer coating liquid (IV) was carried out by ring coating, that the applied coating of the surface protective layer coating liquid (IV) was allowed to stand at room temperature for 30 minutes and the resulting layered assembly was then heated at 130� C. for 1 hour, and that the thickness of the surface protective layer was 2 μm. COMPARATIVE EXAMPLE 1 [0167] An electrophotographic photoconductor was prepared in the same manner as that in Example 1 except that the epoxy group-containing amine compound obtained in Synthesis Example 1 was replaced by a hydroxyl group-containing amine compound of the formula shown below. COMPARATIVE EXAMPLE 2 [0168] An electrophotographic photoconductor was prepared in the same manner as that in Example 1 except that the protective layer was not provided on the charge transporting layer. EXAMPLE 5 [0169] An undercoat layer coating liquid, a charge generating layer coating liquid and a charge transporting layer coating liquid, which had the compositions shown below, were coated and dried one by one to overlay an undercoat layer of 3.5 μm thick, a charge generating layer of 0.2 μm thick and a charge transporting layer of 26 μm thick on an aluminum cylinder. [Undercoat layer coating liquid] Titanium oxide 400 parts Melamine resin 40 parts Alkyd resin 60 parts 2-Butanone 500 parts [0170] [0170] [Charge generating layer coating liquid] Bisazo pigment of the formula shown below 12 parts Polyvinyl butyral resin 5 parts 2-Butanone 200 parts Tetrahydrofuran 400 parts [Charge Transporting layer coating liquid] Polycarbonate resin 10 parts (Bisphenol Z-type polycarbonate resin manufactured by Teijin Kasei Inc.) Charge transporting material 10 parts having the formula shown below Tetrahydrofuran 100 parts 1% Silicone oil tetrahydrofuran solution 1 part (KF50-100CS manufactured by Shin-etsu Chemical Industry Co., Ltd.) [0171] A protective coating liquid (V) having the composition shown below was then spray-coated onto the charge transporting layer to form a protective layer having a thickness of about 3 μm and the resulting layered assembly was heated at 120� C. for 2 hours, thereby obtaining an electrophotographic photoconductor of the present invention. [Protective layer coating liquid (V)] Epoxy group-containing amine compound 35 parts obtained in Synthesis Example 1 above 3-Glysidoxypropyltrimethoxysilane 13 parts Methyltrimethoxysilane 45 parts Phenyltriethoxysilane 32 parts 1% Aqueous acetic acid solution 37.6 parts Boron trifluoride triethylamine salt 0.5 part Tetrahydrofuran 248.4 parts n-Butanol 27.6 parts EXAMPLE 6 [0172] A precursor liquid for a protective layer coating liquid having the following formulation was prepared: [Precursor] 3-Glysidoxypropyltrimethoxysilane 13 parts Methyltrimethoxysilane 45 parts Phenyltriethoxysilane 32 parts 1% Aqueous acetic acid solution 37.6 parts Tetrahydrofuran 248.4 parts n-Butanol 27.6 parts [0173] The precursor liquid was then heated at 60� C. for 2 hours with stirring for silanolizing the 3-glysidoxypropyltrimethoxysilane, methyltrimethoxysilane and phenyltriethoxysilane by hydrolysis. The resulting liquid was mixed with 35 parts of the epoxy group-containing amine compound obtained in Synthesis Example 1 above and 0.5 part of boron trifluoride triethylamine salt to obtain a protective layer coating liquid (VI). An electrophotographic photoconductor was then prepared in the same manner as that in Example 5 except that the protective layer coating liquid (VI) was substituted for the protective layer coating liquid (V). EXAMPLE 7 [0174] To 42 parts of glysidoxypropyltrimethoxysilane, 8.16 parts of a 1% aqueous acetic acid solution were added through 25 minutes in an ice bath. The mixture was stirred at 5� C. for 30 minutes and then stirred at 24� C. for 2 hours for silanolizing the glysidoxypropyltrimethoxysilane by hydrolysis, thereby obtaining a hydrolyzed liquid. [0175] A protective layer coating liquid (VII) having the formulation shown below was prepared. [Protective layer coating liquid (VII)] Hydrolyzed liquid obtained above 3 parts Epoxy group-containing amine compound 0.98 part obtained in Synthesis Example 1 above 2-methoxyethyl acetate 2.62 parts Cyclohexanone 2.42 parts Tetrahydrofuran 0.98 part Acetylacetone 0.12 part Aluminum acetylacetonate 0.12 part [0176] An electrophotographic photoconductor was then prepared in the same manner as that in Example 5 except that the protective layer coating liquid (VII) was substituted for the protective layer coating liquid (V) and that the application of the surface protective layer coating liquid (VII) was carried out by ring coating. Example 8 [0177] To 42 parts of glysidoxypropyltrimethoxysilane, 8.16 parts of a 1% aqueous acetic acid solution were added through 25 minutes in an ice bath. The mixture was stirred at 5� C. for 30 minutes and then stirred at 24� C. for 2 hours for silanolizing the glysidoxypropyltrimethoxysilane by hydrolysis, thereby obtaining a hydrolyzed liquid. [0178] A protective layer coating liquid (VIII) having the formulation shown below was prepared. [Protective layer coating liquid (VIII)] Hydrolyzed liquid obtained above 2.17 parts Epoxy group-containing amine compound 0.98 part obtained in Synthesis Example 1 above Colloidal silica (average particle 2.32 parts diameter: 20 nm) dispersed in n-propylcellosolve 2-methoxyethyl acetate 1.9 parts Cyclohexanone 1.63 parts Tetrahydrofuran 0.98 part Acetylacetone 0.09 part Aluminum acetylacetonate 0.09 part [0179] An electrophotographic photoconductor was then prepared in the same manner as that in Example 5 except that the surface protective layer coating liquid (VIII) was substituted for the protective layer coating liquid (V), that the application of the surface protective layer coating liquid (VIII) was carried out by ring coating, that the applied coating of the surface protective layer coating liquid (VIII) was allowed to stand at room temperature for 30 minutes and the resulting layered assembly was then heated at 130� C. for 1 hour, and that the thickness of the surface protective layer was 4 μm. Comparative Example 3 [0180] An electrophotographic photoconductor was prepared in the same manner as that in Example 5 except that the epoxy group-containing amine compound obtained in Synthesis Example 1 was replaced by a hydroxyl group-containing amine compound of the formula shown below. [0181] [Protective Layer Coating Liquid (IV)] COMPARATIVE EXAMPLE 4 [0182] An electrophotographic photoconductor was prepared in the same manner as that in Example 5 except that the following protective layer coating liquid (IX) was substituted for the protective layer coating liquid (V): Hydroxyl group-containing amine compound 7 parts of the formula shown below Methyltrimethoxysilane 18 parts 1% Aqueous acetic acid solution 10 parts n-Butanol 55.1 parts [0183] Each of the electrophotographic photoconductors obtained in Examples 1-8 and Comparative Examples 1-4 was mounted on an image forming machine (imagio MF2200 manufactured by Ricoh Company, Ltd.; modified by using 655 nm laser diode as a light source). The machine was continuously operated to produce 10,000 copies. Thereafter, the photoconductor was measured for a change of the thickness of the protective layer and observed by a microscope to check the formation of scratch. Further, the potential (VD) of the dark area and the potential (VL) of the lighted area of each of the photoreceptors before and after the production of 10,000 copies were measured, from which a change in VD (ΔVD) and a change in VL (ΔVL) were calculated. In addition, a test chart was copied to evaluate the image quality. Also conducted a test for formation of cracks. Thus, the photoconductor was toughed with a finger to impress a finger print thereonto. Whether or not cracks were formed was examined 48 hours after the impression of the finger print. The evaluation of the results of surface observation, image quality and crack formation were rated as follows: [0184] Surface Observation: [0185] A: only fine line scratches are observed [0186] B: small cavities are locally observed [0187] C: small cavities are observed in entire surface of the protective layer, or a part of the protective layer falls off [0188] Image Quality: [0189] A: no image defects are observed [0190] B: background stains, white resolution are partly observed [0191] C: reduction of image density, background stains, white spots and/or reduced resolution are observed in entire surface [0192] Formation of Cracks: [0193] A: no cracks are observed [0194] B: cracks are locally observed [0195] C: cracks are formed in entire surface [0196] The results are shown in Table 2. TABLE 2 Reduction Surface Example of Thick- Obser- ΔVD ΔVL Image Formation No. ness (μm) vation (V) (V) Quality of Cracks 1 2.9 A −30 +20 A A 2 2.7 A −30 +20 A A 3 0.80 A −30 +10 A A 4 0.65 A −20 +20 A A 5 2.9 A −30 +20 A A 6 2.8 A −30 +20 A A 7 0.7 A −30 +10 A A 8 0.5 A −20 +20 A A Comp. 1 6.1 C −50 +30 B A Comp. 2 5.5 B −10 +10 B C Comp. 3 6.2 C −50 +30 B A Comp. 4 6.0 C −50 +30 B A [0197] The invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all the changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein. [0198] The teachings of Japanese Patent Applications No. 2002-171954, filed Jun. 12, 2002, No. 2002-171921, filed Jun. 12, 2002, No. 2003-003709, filed Jan. 9, 2003, and No. 2003-016661, filed Jan. 24, 2003, inclusive of the specification, claims and drawings, are hereby incorporated by reference herein. Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS6326112 *Aug 21, 2000Dec 4, 2001Ricoh Company LimitedElectrophotographic photoreceptor, and process cartridge and image forming apparatus using the photoreceptorUS6432596 *Apr 4, 2001Aug 13, 2002Ricoh Company LimitedElectrophotographic photoreceptor and image forming method and apparatus using the photoreceptorUS6444387 *Dec 22, 2000Sep 3, 2002Ricoh Company LimitedImage bearing material, electrophotographic photoreceptor using the image bearing material, and image forming apparatus using the photoreceptorUS6465648 *Jun 22, 2000Oct 15, 2002Ricoh Company, Ltd.Reaction product, process of producing same, electrophotographic photoconductor using same, electrophotographic apparatus having the photoconductor, and process cartridge for electrophotographic apparatusUS6489073 *Jan 12, 2001Dec 3, 2002Ricoh Company, Ltd.Method and device for developing electrostatic latent imagesUS6492079 *Mar 27, 2001Dec 10, 2002Ricoh Company, Ltd.Electrophotographic photoconductor, image forming apparatus, and process cartridge using the photoconductorUS6544701 *Feb 5, 2002Apr 8, 2003Ricoh Company, Ltd.Reaction product, process for the production thereof, electrophotographic photoconductor using the reaction product, electrophotographic apparatus using the photoconductor, and process cartridge for electrophotographic apparatusUS6548216 *Mar 23, 2001Apr 15, 2003Ricoh Company, Ltd.Electrophotographic photoconductor, image forming method and apparatus, and process cartridge using the photoconductor, and long-chain alkyl group containing bisphenol compound and polymer made therefromUS6576386 *Aug 9, 2000Jun 10, 2003Ricoh Company, Ltd.Aromatic block polycarbonate resin, diphenol compound for preparation of the polycarbonate resin, electrophotographic photoconductor, electrophotographic image forming apparatus and process, and process cartridgeUS6596449 *Jul 5, 2001Jul 22, 2003Ricoh Company LimitedElectrophotographic photoreceptor, and process cartridge and electrophotographic image forming apparatus using the electrophotographic photoreceptorUS6625409 *Oct 25, 2002Sep 23, 2003Ricoh Company, Ltd.Image forming apparatus having a diamond-like structure surface protection layer on a photoconductive layerUS20020076631 *Oct 15, 2001Jun 20, 2002Akihiko ItamiPhotoreceptor for forming electrostatic latent imageUS20040157145 *Dec 30, 2003Aug 12, 2004Zbigniew TokarskiOrganophotoreceptor with novel charge transport compounds having an epoxy group* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS7251437Mar 1, 2005Jul 31, 2007Ricoh Company, Ltd.Image formation apparatus having a body to be charged with specified properties and including the use of a protective materialUS7390600Sep 2, 2005Jun 24, 2008Ricoh Company, Ltd.Latent electrostatic image bearing member, process cartridge, image forming apparatus, and image forming processUS7390607Jul 12, 2006Jun 24, 2008Ricoh Company, Ltd.Toner, production process for the same, and image forming methodUS7416823Jan 13, 2005Aug 26, 2008Ricoh Company, Ltd.Electrophotographic photoconductor, and image formation method, image formation apparatus, and process cartridge for image formation apparatus using the sameUS7432032Feb 12, 2008Oct 7, 2008Ricoh Company, Ltd.Toner, production process for the same, and image forming methodUS7449272Nov 15, 2005Nov 11, 2008Ricoh Company, Ltd.Electrophotographic photoreceptor and method of preparing the photoreceptor, and image forming method, image forming apparatus and process cartridge therefor using the photoreceptorUS7462431 *May 12, 2005Dec 9, 2008Xerox CorporationPhotoreceptorsUS7473504May 25, 2005Jan 6, 2009Ricoh Company, Ltd.Electrophotographic photoreceptor, and image forming method, apparatus and process cartridge therefor using the photoreceptorUS7507509Oct 7, 2005Mar 24, 2009Ricoh Company, Ltd.Electrophotographic photoreceptor, and image forming method, image forming apparatus and process cartridge using the electrophotographic photoreceptorUS7507511Jan 17, 2006Mar 24, 2009Ricoh Company Ltd.Electrophotographic photoreceptor, and image forming apparatus and process cartridge therefor using the electrophotographic photoreceptorUS7517625Sep 6, 2005Apr 14, 2009Ricoh Company, Ltd.Image forming apparatus and process cartridgeUS7550238Apr 21, 2005Jun 23, 2009Ricoh Company, Ltd.Process cartridge, image forming apparatus, and image forming processUS7556903Sep 20, 2004Jul 7, 2009Ricoh Company LimitedElectrophotographic photoreceptor, and image forming method, apparatus and process cartridge therefor using the photoreceptorUS7629094Dec 27, 2005Dec 8, 2009Ricoh Company, Ltd.Electrophotographic photoreceptor, and image forming method, image forming apparatus and process cartridge therefor using the electrophotographic photoreceptorUS7629103Jun 21, 2005Dec 8, 2009Ricoh Company, Ltd.Photoconductor, manufacturing method thereof, image forming process and image forming apparatus using photoconductor, and process cartridgeUS7659044Jul 5, 2005Feb 9, 2010Ricoh Company, Ltd.Photoconductor, producing method thereof, image forming process and image forming apparatus using photoconductor, and process cartridgeUS7662533Feb 16, 2010Ricoh Company LimitedImage forming method, and image forming apparatus and process cartridge using the image forming methodUS7670743Mar 2, 2010Ricoh Company, Ltd.Image forming methodUS7691931Nov 10, 2005Apr 6, 2010Ricoh Company Ltd.Organic-inorganic hybrid material and method of preparing the organic-inorganic hybrid material, and electrophotographic photoreceptor, process cartridge, image forming apparatus and image forming method using the organic-inorganic hybrid materialUS7718335Dec 27, 2006May 18, 2010Ricoh Company LimitedImage bearing member, and image forming apparatus and process cartridge using the sameUS7838188Nov 23, 2010Ricoh Company, Ltd.Electrophotographic photoconductor, image forming method, image forming apparatus, and process cartridgeUS7851114Dec 14, 2010Ricoh Company LimitedElectrostatic latent image bearing member, and image forming apparatus, process cartridge, and image forming method using the sameUS7862969Jan 10, 2007Jan 4, 2011Ricoh Company, Ltd.Image bearing member and image forming method using thereof, and image forming apparatus and process cartridgeUS7914959Mar 29, 2011Ricoh Company, LimitedImage bearing member, image forming method, and image forming apparatusUS7951516May 31, 2011Fuji Xerox Co., Ltd.Electrophotographic photoreceptor, method of producing the same, process cartridge, and image-forming apparatusUS8017807Sep 13, 2011Ricoh Company LimitedTetrahydroxy compound, method for preparing the tetrahydroxy compound, and photoreceptor using the tetrahydroxy compoundUS8192904Jun 15, 2007Jun 5, 2012Ricoh Company, Ltd.Electrophotographic photoconductor, and image forming apparatus and process cartridge using the sameUS9291924Dec 2, 2014Mar 22, 2016Ricoh Company, Ltd.Electrophotographic photoconductor, and image forming method, image forming apparatus, and process cartridge using the electrophotographic photoconductorUS20050158641 *Jan 13, 2005Jul 21, 2005Yoshiki YanagawaElectrophotographic photoconductor, and image formation method, image formation apparatus, and process cartridge for image formation apparatus using the sameUS20050196193 *Mar 1, 2005Sep 8, 2005Nozomu TamotoImage formation apparatus and process cartridge for image formation apparatusUS20050221210 *Mar 18, 2005Oct 6, 2005Tetsuro SuzukiElectrophotographic photoconductor and image formation method, image formation apparatus, and process cartridge for image formation apparatus using the electrophotographic photoconductorUS20050238987 *Apr 21, 2005Oct 27, 2005Kohichi OhshimaProcess cartridge, image forming apparatus, and image forming processUS20050266325 *May 25, 2005Dec 1, 2005Yoshiki YanagawaElectrophotographic photoreceptor, and image forming method, apparatus and process cartridge therefor using the photoreceptorUS20050266328 *Sep 20, 2004Dec 1, 2005Yoshiki YanagawaElectrophotographic photoreceptor, and image forming method, apparatus and process cartridge therefor using the photoreceptorUS20050282075 *Jun 21, 2005Dec 22, 2005Hiroshi IkunoPhotoconductor, manufacturing method thereof, image forming process and image forming apparatus using photoconductor, and process cartridgeUS20050287452 *Jun 22, 2005Dec 29, 2005Hiroshi TamuraPhotoconductor, image forming process, image forming apparatus, and process cartridgeUS20050287465 *Jun 24, 2005Dec 29, 2005Kohichi OhshimaImage forming method, and image forming apparatus and process cartridge using the image forming methodUS20060014093 *Jul 5, 2005Jan 19, 2006Hongguo LiPhotoconductor, producing method thereof, image forming process and image forming apparatus using photoconductor, and process cartridgeUS20060014096 *Jun 27, 2005Jan 19, 2006Kohichi OhshimaImage forming method, image forming apparatus and process cartridge thereforUS20060051688 *Sep 2, 2005Mar 9, 2006Naohiro TodaLatent electrostatic image bearing member, process cartridge, image forming apparatus, and image forming processUS20060051689 *Sep 6, 2005Mar 9, 2006Yasuo SuzukiImage forming apparatus and process cartridgeUS20060078809 *Oct 7, 2005Apr 13, 2006Kazukiyo NagaiElectrophotographic photoreceptor, and image forming method, image forming apparatus and process cartridge using the electrophotographic photoreceptorUS20060110668 *Nov 15, 2005May 25, 2006Yoshiaki KawasakiElectrophotographic photoreceptor and method of preparing the photoreceptor, and image forming method, image forming apparatus and process cartridge therefor using the photoreceptorUS20060160003 *Dec 27, 2005Jul 20, 2006Kazukiyo NagaiElectrophotographic photoreceptor, and image forming method, image forming apparatus and process cartridge therefor using the electrophotographic photoreceptorUS20060177749 *Jan 17, 2006Aug 10, 2006Nozomu TamotoElectrophotographic photoreceptor, and image forming apparatus and process cartridge therefor using the electrophotographic photoreceptorUS20060197823 *Mar 6, 2006Sep 7, 2006Katsuichi OhtaImage forming apparatusUS20060257768 *May 12, 2005Nov 16, 2006Xerox CorporationPhotoreceptorsUS20070009818 *Jul 5, 2006Jan 11, 2007Yoshiki YanagawaElectrophotographic photoreceptor and method of preparing the photoreceptor, and image forming method, image forming apparatus and process cartridge therefor using the photoreceptorUS20070020548 *Jul 12, 2006Jan 25, 2007Chiaki TanakaToner, production process for the same, and image forming methodUS20070031746 *Aug 8, 2006Feb 8, 2007Tetsuya ToshineElectrophotographic photoconductor, process cartridge, and image forming methodUS20070117033 *Nov 21, 2006May 24, 2007Akihiro SuginoElectrostatic latent image bearing member, and image forming apparatus, process cartridge, and image forming method using the sameUS20070128530 *Nov 21, 2006Jun 7, 2007Kazukiyo NagaiTetrahydroxy compound, method for preparing the tetrahydroxy compound, and photoreceptor using the tetrahydroxy compoundUS20070196749 *Nov 28, 2006Aug 23, 2007Yoshinori InabaImage bearing member, image forming method, and image forming apparatusUS20070196750 *Dec 27, 2006Aug 23, 2007Yukio FujiwaraImage bearing member, and image forming apparatus and process cartridge using the sameUS20070212625 *Jan 10, 2007Sep 13, 2007Yasuo SuzukiImage bearing member and image forming method using thereof, and image forming apparatus and process cartridgeUS20070212626 *Mar 9, 2007Sep 13, 2007Tetsuya ToshineElectrophotographic photoreceptor, and image forming apparatus and process cartridge using the sameUS20070231720 *Mar 28, 2007Oct 4, 2007Mori NobuyaElectrophotographic photoconductor, image forming method, image forming apparatus, and process cartridgeUS20070292780 *Jun 15, 2007Dec 20, 2007Kazukiyo NagaiElectrophotographic photoconductor, and image forming apparatus and process cartridge using the sameUS20080102389 *May 29, 2007May 1, 2008Fuji Xerox Co., Ltd.Electrophotographic photoreceptor, method of producing the same, process cartridge, and image-forming apparatusUS20080145778 *Jan 14, 2008Jun 19, 2008Katsuichi OhtaImage forming apparatusUS20080182199 *Feb 12, 2008Jul 31, 2008Chiaki TanakaToner, production process for the same, and image forming methodUS20100209842 *Feb 16, 2010Aug 19, 2010Yoshiki YanagawaElectrophotographic photoreceptor and method of preparing the photoreceptor, and image forming method, image forming apparatus and process cartridge therefor using the photoreceptorUS20130203882 *Feb 9, 2011Aug 8, 2013Huntsman International LlcCurable Composition* Cited by examinerClassifications U.S. Classification430/96, 399/159, 430/58.7, 430/132, 430/58.2, 430/133, 430/66International ClassificationG03G5/05, G03G5/147Cooperative ClassificationG03G5/0592, G03G5/0596, G03G5/0575, G03G5/0578, G03G5/14795, G03G5/0557, G03G5/14791, G03G5/14747European ClassificationG03G5/147D2H, G03G5/05C8, G03G5/05C4H, G03G5/147D2K, G03G5/147D2D, G03G5/05C4K, G03G5/05C10, G03G5/05C4Legal EventsDateCodeEventDescriptionOct 10, 2003ASAssignmentOwner name: RICOH COMPANY, LTD., JAPANFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NAGAI, KAZUKIYO;TANAKA, CHIAKI;SUZUKI, TETSURO;AND OTHERS;REEL/FRAME:014589/0492Effective date: 20030714Apr 1, 2011FPAYFee paymentYear of fee payment: 4May 22, 2015REMIMaintenance fee reminder mailedOct 9, 2015LAPSLapse for failure to pay maintenance feesDec 1, 2015FPExpired due to failure to pay maintenance feeEffective date: 20151009RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services