Patent US4263375 - Superplastically formed titanium structure - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign in<nobr>Advanced Patent Search</nobr>PatentsAn article of manufacture of a titanium reinforcing part having a grain structure to impart dimensional stability to the part at elevated temperatures is integrally joined to a titanium sheet having a grain structure to become superplastic at elevated temperatures. The completed composite titanium part...http://www.google.com/patents/US4263375?utm_source=gb-gplus-sharePatent US4263375 - Superplastically formed titanium structureAdvanced Patent SearchPublication numberUS4263375 APublication typeGrantApplication numberUS 05/973,324Publication dateApr 21, 1981Filing dateDec 26, 1978Priority dateDec 26, 1978Publication number05973324, 973324, US 4263375 A, US 4263375A, US-A-4263375, US4263375 A, US4263375AInventorsSamuel D. ElrodOriginal AssigneeThe Boeing CompanyExport CitationBiBTeX, EndNote, RefManPatent Citations (10), Referenced by (35), Classifications (15) External Links: USPTO, USPTO Assignment, EspacenetSuperplastically formed titanium structureUS 4263375 AAbstract An article of manufacture of a titanium reinforcing part having a grain structure to impart dimensional stability to the part at elevated temperatures is integrally joined to a titanium sheet having a grain structure to become superplastic at elevated temperatures. The completed composite titanium part is formed with the titanium sheet superplastically forming to intimately contact and to become diffusion bonded to the dimensionally stable titanium part.
I claim: 1. An article of manufacture superplastically formed and diffusion bonded comprising: a pair of spaced apart titanium parts having a Widmanstatten grain structure to render the parts dimensionally stable at superplastic forming conditions; a thin walled hollow insert with end cap, located intermediate the spaced apart titanium parts, and the insert having a Widmanstatten grain structure to render the insert dimensionally stable at superplastic forming conditions; a third titanium part superplastically formed and diffusion bonded to facing sides of the pair of parts to form a pair of flanges, and the third part extends between the flanges to form a web superplastically formed and diffusion bonded to the insert end cap and side, and the cap of the insert with diffusion bonded superplastically formed part having a hole extending through to provide a reinforced opening through the superplastically formed web.
BACKGROUND OF THE INVENTION It is known that various metals may be superplastically formed, into various shapes, under elevated temperatures while under pressure. It is also known that various metals may be diffusion bonded together under elevated temperatures while under pressure. In U.S. Pat. No. 3,920,175 to Hamilton et al, these two processes were combined to superplastically form and to diffusion bond all in the same process. U.S. Pat. Nos. 3,996,019 and 4,071,183 to Cogan call for a method of using two superplastically formed sheets with reinforcing inserts retained between the sheets by diffusion bonding to generate a part requiring a minimum of post forming machining.
When superplastic forming in combination with diffusion bonding one uses at least one part that is in the form of a sheet that is deformed under superplastic conditions to define a complex shape. This formed sheet is pressed aginst one or more parts, which may be considered as reinforcing parts, to which the sheet is to be joined. Difficulties are often experienced due to the plastic characteristics of the reinforcing part at the conditions required for the process. Even when the reinforcing part is located around the inside surface of a mold in which the process is taking place, thereby allowing the superplastic sheet to press against and force the reinforcing part against the side of the mold, difficulties are experienced with maintaining tolerance due to flow of the reinforcing part. This is corrected to some extent by utilizing a reinforcing part that is much thicker than the sheet. When the reinforcing part is located in the mold such that the reinforcing art is unsupported on two opposite sides the flow of that part is even more of a problem. To help correct this situation it is necessary to use a large cross sectional area. When one uses a thin reinforcing part that is unsupported on two opposite sides a completely unsatisfactory part is generated as the reinforcing part tends to tip sideways. It was found that titanium parts may be superplastically formed and diffusion bonded while maintaining dimensional tolerances.
SUMMARY OF THE INVENTION A composite titanium structure is fabricated of a titanium sheet having a grain structure to permit the sheet to be superplastically formed by pressure at elevated temperatures and reinforcing titanium parts having a grain structure to maintain dimensional stability at the same pressures and elevated temperatures. The parts are superplastically formed together and are diffusion bonded to form a composite titanium structure.
BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 shows a perspective view of a titanium part of this invention as the part appears when removed from a forming mold.
FIGS. 2 through 5 show a side elevational sectional view of the various steps of forming the part of FIG. 1.
FIGS. 6 and 7 show a side elevational sectional view of a different embodiment of the part of FIG. 1.
FIG. 8 shows a fragmented perspective view of the part of FIG. 1 with the part trimmed for use.
FIG. 9 shows a perspective view of a different embodiment of a titanium part of this invention as the part appears when removed from a mold.
FIG. 10 shows a side elevational sectional view of the part of FIG. 9 while still in the mold.
FIG. 11 shows the part of FIG. 10 removed from the mold and trimmed for use.
FIG. 12 shows a different embodiment taken along line 12--12 of FIG. 11.
DETAILED DESCRIPTION A composite titanium part 10 is formed and bonded in a mold 12 made up of a female mold part 14 and a mold cover 16. The mold parts are formed and shaped to hold a sheet of titanium 18 in a manner to provide a pressure seal between the titanium sheet and the two parts of the mold. The finished part 10, when it is taken from the mold, is as shown in FIG. 1, which indicates the part before it has been trimmed to the final configuration. In that FIGURE the untrimmed part 20 is made up of titanium insert 22, and the titanium sheet 18 in the formed condition. In that condition the border 24, which was held between the two parts of the mold, remains undeformed while the balance of the sheet is formed with bottom portion 26, U-shaped portion 28 contacting and joined to three sides of the insert 22, side members 30a and 30b, and end members 32a and 32b. When trimmed for use the titanium part 10 is made up of a flat sheet 26 with integral U-shaped portion 28 that encircles and is bonded to insert 22 to make up an integral titanium sheet with reinforcement.
In forming the composite titanium member 10, the titanium insert 22, which in this instance is of 6Al 4V titanium alloy, is first placed in an inert atmosphere and the temperature raised to about 1900� F. and held at that temperature for about 30 minutes to beta anneal and thereby form a Widmanstatten grain structure in the part. This is a grain structure that imparts dimensional stability to the part at elevated temperatures. It is not intended to limit this invention to the use of 6Al 4V titanium as other titanium alloys may also be beta annealed and used in this process. The insert is positioned in female mold 14 with that insert located well away from the sides of the mold and held in position by the ends of the insert contacting the tapered ends of the mold. The insert is narrow in width and has a large heighth to width ratio as positioned in the mold. Next a sheet of titanium 18 is positioned between and sealing secured to the two parts 14 and 16 of the mold. A mill annealed titanium alloy is used for the titanium sheet, which gives a fine grain equiaxed structure that becomes superplastic at elevated temperatures. A 6Al 4V titanium is preferred. The mold with parts is heated to a range of about 1450� F. to about 1850� F. with a temperature of about 1650� preferred when using the 6Al 4V titanium alloy. An inert gas under pressure is introduced through channel 34 in mold cover 16. The titanium sheet 18 is superplastic at that temperature and moves down as shown progressively by FIGS. 3 and 4 to intimately contact and surround the insert on three sides, and to fill the female portion of the mold. Pressures of from 50 to 400 p.s.i. are used with about 300 p.s.i. preferred. While still under pressure the mold with parts is raised to about 1700� F. and held at that temperature for a time sufficient to diffusion bond the titanium sheet to the titanium insert which is preferably about 3 hours. The superplastically formed diffusion bonded untrimmed part 20 is removed from the mold and trimmed to the finished titanium structural part 10.
FIGS. 6 and 7 show a different embodiment of this invention wherein a sheet of titanium 36, which is preferably mill annealed to become superplastic at elevated temperatures is placed in the bottom of the mold, beta annealed part 22a located in the mold, mill annealed sheet 18a superplastically formed into shape having unformed parts 24a, sides 30c and 30d, end members 32c and 32d, bottom portion 26a and, U-shaped portion 28a. These parts are superplastically formed and diffusion bonded together into an integral titanium untrimmed part 20a, which is trimmed for use.
FIGS. 9 through 11 show another embodiment of this invention. A pair of structural members 38a and 38b are spaced apart by placement along the sides of female mold part 40 of mold 42. These structural members are of a beta annealed titanium alloy that has a grain structure to provide dimensional stability to those members at elevated temperatures. A thin walled, hollow insert 44 with end cap 46 is located in a recess 48 of the female mold part. This insert is of a titanium alloy also having a grain structure to be dimensionally stable at elevated temperatures. A sheet 50 of mill annealed titanium alloy is sealingly located between female mold part 40 and mold cover part 52. The mold with parts is raised to superplastic forming temperatures, inert gas under pressure introduced through channel 54 and sheet 50 deforms to intimately contact and to diffusion bond to the structural members and to the insert. After the deforming and the bonding is completed, parts of the titanium sheet are trimmed away to provide a beam 56 having a web 58, and a pair of flanges 60a and 60b. Located in the web is a reinforcement made up of the insert 44 and a portion 62 of the deformed sheet 50 that is integrally joined to the insert. The reinforcement has an opening 64 extending through the web as part of the end cap 46 and part of the portion 62 of the sheet is drilled through to provide the opening. The flanges are made up respectively of reinforcing part 38a and a portion 66a of the sheet 50 and of part 38b and a portion 66b of the sheet 50. All of the balance of the sheet 50 is trimmed away to leave the finished beam. It is not intended to be limited to beams as other shapes such as, but not limited to, channels can also be formed by this process.
FIG. 12 shows another embodiment of this invention with a beam 56a having a flange 60c made up of a dimensionally stable titanium structural member 38c diffusion bonded to a sheet 66c with said sheet integral to a web portion 58a that is sine wave in shape.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3340028 *Nov 30, 1966Sep 5, 1967Crucible Steel Co AmericaHigh-tin titanium welding wireUS3645803 *Apr 16, 1970Feb 29, 1972Us NavyMethod for improving the fracture toughness of metals and alloysUS3657801 *Apr 22, 1970Apr 25, 1972Atomic Energy CommissionMethod of joining certain metalsUS3798011 *Jan 26, 1970Mar 19, 1974Du PontMultilayered metal compositeUS3802939 *Mar 22, 1971Apr 9, 1974Kobe Steel LtdSurface-hardened titanium or zirconium and their alloys and method of processing sameUS3920175 *Oct 3, 1974Nov 18, 1975Rockwell International CorpMethod for superplastic forming of metals with concurrent diffusion bondingUS3996019 *Apr 18, 1975Dec 7, 1976General Electric CompanyFabrication method and fabricated articleUS4043498 *Sep 15, 1975Aug 23, 1977Tre CorporationMethod of plastic flow diffusion bondingUS4071183 *Jan 29, 1976Jan 31, 1978General Electric CompanyFabrication method and fabricated articleUS4117970 *Nov 16, 1976Oct 3, 1978Rockwell International CorporationMethod for fabrication of honeycomb structures* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS4422569 *Feb 13, 1981Dec 27, 1983British Aerospace Public Limited CompanyForming metal articlesUS4934580 *Dec 27, 1988Jun 19, 1990Barnes Group, Inc.Method of making superplastically formed and diffusion bonded articles and the articles so madeUS4982893 *Aug 15, 1989Jan 8, 1991Allied-Signal Inc.Diffusion bonding of titanium alloys with hydrogen-assisted phase transformationUS5139887 *May 16, 1990Aug 18, 1992Barnes Group, Inc.Superplastically formed cellular articleUS5344063 *Sep 28, 1992Sep 6, 1994British Aerospace Public Limited CompanyMethod of making diffusion bonded/superplastically formed cellular structures with a metal matrix compositeUS5410132 *Oct 15, 1991Apr 25, 1995The Boeing CompanySuperplastic forming using induction heatingUS5413649 *Jul 29, 1993May 9, 1995Massachusetts Institute Of TechnologyMethod for enhancing superplasticity in compositesUS5444912 *Oct 29, 1993Aug 29, 1995Folmer; Carroll W.Method for forming aircraft engine nacelle exhaust mixers and similar productsUS5445310 *Jul 21, 1993Aug 29, 1995Folmer; Carroll W.Method for sheet metal and thermoplastic adhesive bonded assemblies and brazed bonded assemblies in 360� shapesUS5587098 *Jun 7, 1995Dec 24, 1996The Boeing CompanyJoining large structures using localized induction heatingUS5624594 *Jun 6, 1995Apr 29, 1997The Boeing CompanyFixed coil induction heater for thermoplastic weldingUS5641422 *Jun 16, 1995Jun 24, 1997The Boeing CompanyForming fusion welds using fixed solenoid coil induction heaterUS5645744 *Jun 6, 1995Jul 8, 1997The Boeing CompanyAt least two metal sheets surrounding workpiece, means for temporarily sealing sheets around workpieceUS5650087 *Mar 2, 1994Jul 22, 1997Gram A/SDeep drawing, stree-relief annealing, pressing, and welding; using titanium metal or alloy which is corrosion resistanceUS5683607 *Aug 14, 1996Nov 4, 1997The Boeing CompanyRapid heating and controlled cooling in a single cycle in an induction heating press using an actively cooled induction coil embedded in a ceramic die setUS5687900 *Mar 28, 1995Nov 18, 1997Mcdonnell Douglas CorporationStructural panel having a predetermined shape and an associated method for superplastically forming and diffusion bonding the structural panelUS5705794 *May 26, 1995Jan 6, 1998The Boeing CompanyCombined heating cycles to improve efficiency in inductive heating operationsUS5710414 *Jun 6, 1995Jan 20, 1998The Boeing CompanyFor counteracting sagging during thermoplastic weldingUS5723849 *Jun 6, 1995Mar 3, 1998The Boeing CompanyReinforced susceptor for induction or resistance welding of thermoplastic compositesUS5728309 *Jun 6, 1995Mar 17, 1998The Boeing CompanyMethod for achieving thermal uniformity in induction processing of organic matrix composites or metalsUS5793024 *Jun 6, 1995Aug 11, 1998The Boeing CompanyBonding using induction heatingUS5797239 *Jan 13, 1997Aug 25, 1998Mcdonnell Douglas CorporationTitanium reinforced structural panel having a predetermined shapeUS5808281 *Jun 6, 1995Sep 15, 1998The Boeing CompanyFor temperature control of a workpiece in induction heating operationsUS5847375 *Jul 19, 1996Dec 8, 1998The Boeing CompanyFastenerless bonder wingboxUS5914064 *Jul 9, 1997Jun 22, 1999The Boeing CompanySuperplastic formingUS6040563 *Dec 22, 1997Mar 21, 2000The Boeing CompanyBonded assembliesUS6042661 *Mar 19, 1997Mar 28, 2000Massachusetts Institute Of TechnologyAltering chemical composition of workpiece material while workpiece is subjected to biasing stress, introducing strain increment into material and effecting change in overall dimensionUS6087640 *May 26, 1995Jul 11, 2000The Boeing CompanyForming parts with complex curvatureUS6720089 *Feb 12, 2002Apr 13, 2004Architectural Titanium LlcPure titanium panel with frame around margin to inhibit movement during heat treatment which forms decorative recrystallized area, including four interconnected elements with stiffening adjacent corners and contacting marginUS6914225Jun 18, 2003Jul 5, 2005The Boeing CompanyApparatus and methods for single sheet forming using induction heatingUS7126096Jun 6, 1995Oct 24, 2006Th Boeing CompanyResistance welding of thermoplastics in aerospace structureEP0209606A2 *May 18, 1985Jan 28, 1987Rockwell International CorporationMethod and apparatus for the superplastic forming and/or diffusion bonding of sheet metalEP0341168A1 *May 2, 1989Nov 8, 1989Pechiney RhenaluMethod and device for forming a metallic foilEP0845312A1 *Nov 29, 1997Jun 3, 1998Forschungsgesellschaft Umformtechnik m.b.H.Flexibly applicable die for high pressure formingWO2000016925A1 *Sep 7, 1999Mar 30, 2000Rolls Laval Heat Exchangers LiA method of manufacturing an article by hot forming* Cited by examinerClassifications U.S. Classification428/594, 228/173.6, 228/161, 428/940, 228/193, 428/660, 428/941International ClassificationB21D26/055, B23K20/233Cooperative ClassificationB23K20/233, Y10S428/94, Y10S428/941, B21D26/055European ClassificationB23K20/233, B21D26/055RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services©2012 Google