JP4551321B2 - Electronic parts packaging structure and a method of manufacturing the same - Google Patents
JP4551321B2
JP4551321B2 JP2005373859A JP2005373859A JP4551321B2 JP 4551321 B2 JP4551321 B2 JP 4551321B2 JP 2005373859 A JP2005373859 A JP 2005373859A JP 2005373859 A JP2005373859 A JP 2005373859A JP 4551321 B2 JP4551321 B2 JP 4551321B2
JP2005373859A
JP2007053327A (en
2005-07-21 Priority to JP2005211938 priority Critical
2005-12-27 Application filed by 新光電気工業株式会社 filed Critical 新光電気工業株式会社
2005-12-27 Priority to JP2005373859A priority patent/JP4551321B2/en
2007-03-01 Publication of JP2007053327A publication Critical patent/JP2007053327A/en
2010-09-29 Publication of JP4551321B2 publication Critical patent/JP4551321B2/en
本発明は電子部品実装構造及びその製造方法に関し、特に薄型化を図るために配線基板の内部に半導体素子（チップ）等の電子部品を実装したパッケージ構造を有する電子部品実装構造及びその製造方法に関する。 The present invention relates to an electronic parts packaging structure and a method of manufacturing the same, particularly relates to an electronic parts packaging structure and a manufacturing method thereof having an internal semiconductor element (chip) mounted package structure electronic components such as a wiring board to reduce the thickness .
近年、電子機器の高機能化が促進されており、そのキーテクノロジーであるＬＳＩ（Large Scale Integration ：大規模集積回路）技術は、データ伝送の高速化及び大容量化に向って着実に進んでいる。 Recently, high performance have been promoted in electronic appliances, that is a key technology LSI (Large Scale Integration: large scale integration) technology is progressing toward the high speed and capacity of data transmission steadily . また、ＬＳＩの実装技術も年々進歩しており、狭いスペースに多数のＬＳＩを高密度に実装できるようになっている。 In addition, implementation technology of LSI has also progressed year by year, so that can be densely packed a large number of LSI in a narrow space.
さらなる高密度化の要求から、配線基板上に複数の半導体チップを３次元的に積層して実装したマルチチップパッケージ（半導体装置）が開発されている。 From further densification request, a multi-chip package mounted by stacking a plurality of semiconductor chips are three-dimensionally on a wiring board (semiconductor devices) have been developed. その一例として、配線基板上に複数の半導体チップが絶縁膜に埋設された状態で３次元的に実装され、かつ絶縁膜に形成されたビアホール及び配線パターンを介して複数の半導体チップが相互に接続された構造を有する半導体装置がある（例えば、特許文献１〜５）。 As an example, wiring a plurality of semiconductor chips on the substrate is three-dimensionally mounted while being embedded in the insulating film, and connected to the plurality of semiconductor chips through via holes and wiring patterns formed on the insulating film to each other there is a semiconductor device having a structure (e.g., Patent documents 1 to 5).
特開２００１−１９６５２５号公報 JP 2001-196525 JP 特開２００１−１７７０４５号公報 JP 2001-177045 JP 特開２０００−３２３６４５号公報 JP 2000-323645 JP 特開２００５−２１７２２５号公報 JP 2005-217225 JP 特開２００５−２０９６８９号公報 JP 2005-209689 JP
ところで、半導体チップを被覆する絶縁膜が樹脂からなる場合、樹脂膜の中にはそれと熱膨張係数が異なる半導体チップや配線（金属膜）が存在することとなるため、樹脂膜が熱処理されて形成される際に、これらの熱膨張係数の差に基づく熱応力によって半導体装置自体に反りが発生しやすい。 Incidentally, when the insulating film covering the semiconductor chip is made of a resin, since in the resin film is that it is therewith thermal expansion coefficient exists different semiconductor chips and wiring (metal film), a resin film is heat-treated form when it is, warp in the semiconductor device itself tends to occur by thermal stress based on the difference between these thermal expansion coefficients. このため、後工程での半導体装置のハンドリングに支障をきたしたり、半導体装置を実装基板（マザーボード）に実装する際にそれらの接合の信頼性が低下するなどの不具合が発生したりするおそれがある。 Accordingly, or hindered handling of the semiconductor device in the subsequent process, the reliability is liable to or malfunction occurs, such as reduction of their junction when mounted on the mounting board to the semiconductor device (motherboard) .
上記した特許文献１〜５には、いずれも絶縁膜（樹脂膜）内に半導体チップが埋設されて実装された構造が記載されているものの、上記したような熱応力に基づく半導体装置の反りに関しては何ら考慮されていない。 Patent Documents 1 to 5 described above, although both have been described structure implemented semiconductor chip is buried in the insulating film (resin film), with respect to warping of the semiconductor device based on thermal stress as described above It has not been considered at all.
本発明は以上の課題を鑑みて創作されたものであり、電子部品が絶縁膜に埋設された状態で実装された構造を有する電子部品実装構造において、従来に比べてより一層の高密度化が可能であるとともに、反りの発生が防止される電子部品実装構造及びその製造方法を提供することを目的とする。 The present invention has been made in view of the above problems, an electronic parts packaging structure having electronic components are mounted in a state of being embedded in the insulating film structure, the higher density as compared with the conventional as well as a possible, and to provide an electronic parts packaging structure and a manufacturing method thereof occurrence of warpage is prevented.
上記課題を解決するため、本発明は、複数のシート状のユニットが厚さ方向に積層されて構成された電子部品実装構造において、前記ユニットが、第１の絶縁層と、前記第１の絶縁層の一方の面上に形成された配線と、前記配線に接続された電子部品と、前記第１の絶縁層の前記一方の面側に形成されて前記電子部品を覆う第２の絶縁層と、前記配線と他のユニットの配線とを電気的に接続する接続部とを有し、厚さ方向に隣り合うユニットにおいて、前記第１の絶縁層、前記電子部品、前記配線及び前記第２の絶縁層の配置が対称であることを特徴とする。 To solve the above problems, the present invention is an electronic parts packaging structure constructed with a plurality of sheet-like unit is stacked in a thickness direction, wherein the unit includes a first insulating layer, the first insulating while a wiring formed on the surface of the layer, and an electronic component connected to the wiring, a second insulating layer formed on the one surface side of said first insulating layer covering the electronic component , and a connecting portion for electrically connecting the wiring and other units of lines, in the unit adjacent in the thickness direction, the first insulating layer, the electronic component, the interconnection and the second wherein the arrangement of the insulation layer is symmetrical.
本発明の電子部品実装構造は、電子部品が埋設されたシート状のユニットを積層して構成されている。 Electronic parts packaging structure of the present invention is constructed by laminating a sheet-like unit in which electronic components are embedded. 各ユニットは第１の絶縁層と、配線と、半導体チップ等の電子部品と、第２の絶縁層と、接続部とにより構成されており、コアとなる高強度の支持基板（厚い基板）を有していない。 And each unit first insulating layer, a wiring, and electronic components such as semiconductor chips, a second insulating layer is constituted by a connecting portion, the supporting substrate of high strength Core (thick substrate) It does not have. そして、複数のユニットを積層することで、全体的な強度を確保している。 Then, by stacking a plurality of units, it is ensured overall strength. これにより、本発明の電子部品実装構造は、支持基板を有する従来の電子部品実装構造に比べて電子部品のより一層の高密度化が達成される。 Thus, the electronic parts packaging structure of the present invention, higher density of electronic components is achieved compared to the conventional electronic component mounting structure having a supporting substrate.
また、本発明においては、厚さ方向に隣り合うユニットにおいて、第１の絶縁層、電子部品、配線及び第２の絶縁層の配置が対称となっている。 In the present invention, in a unit adjacent in the thickness direction, the first insulating layer, the arrangement of the electronic components, wiring and the second insulating layer has a symmetric. このため、電子部品と絶縁層及び配線（金属膜）との熱膨張係数の差に基づく熱応力が発生するとしても、厚さ方向に隣り合うユニットで熱応力による反りの方向が逆となって相殺され、電子部品実装構造に反りが発生することが防止される。 Therefore, even if the thermal stress is generated based on the difference in thermal expansion coefficient between the electronic component and the insulating layer and the wiring (metal film), so the direction of the warp due to thermal stress is reversed in units adjacent in the thickness direction offset, warpage is prevented from occurring in the electronic parts packaging structure.
本発明の一つの好適な態様では、前記第１の絶縁層をソルダーレジストにより形成する。 In one preferred mode of the present invention, it is formed by a solder resist said first insulating layer. 本発明では、電子部品実装構造の最外面に第１の絶縁層が配置される。 In the present invention, the first insulating layer is disposed on the outermost surface of the electronic component mounting structure. 電子部品を埋設する絶縁層（第２の絶縁層）には通常エポキシ等の樹脂により形成されるが、ソルダーレジストは一般的にエポキシ樹脂よりも強度が高い。 Although the insulating layer for embedding the electronic component (second insulating layer) is formed of a resin of ordinary epoxy, solder resist higher strength than typical epoxy resin. このため、最外面に配置される第１の絶縁層をソルダーレジストにより形成すると、電子部品実装構造の強度が高くなり、破損等の不具合の発生が抑制される。 Thus, when formed by the solder resist of the first insulating layer disposed on the outermost surface, the strength of the electronic component mounting structure is increased, occurrence of defects such as breakage can be suppressed.
前記電子部品が半導体チップの場合、半導体チップの素子形成面を保護膜により保護することが好ましい。 If the electronic component is a semiconductor chip, it is preferably protected with a protective film to the element forming surface of the semiconductor chip. この場合、保護膜中にシリカ等を混入して熱膨張係数が、半導体チップの熱膨張係数と第１の絶縁層の熱膨張係数との中間となるように調整すると、半導体チップと第１の絶縁層との熱膨張係数の差により発生する応力を分散することができる。 In this case, contaminating the thermal expansion coefficient of silica or the like in the protective film, when adjusted to be an intermediate thermal expansion coefficient between the first insulating layer of the semiconductor chip, the semiconductor chip and the first it is possible to distribute the stress generated by the difference in thermal expansion coefficient between the insulating layer.
また、上記した課題を解決するため、本発明に係る電子部品実装構造の製造方法では、第１の絶縁層と、前記第１の絶縁層の一方の面上に形成された配線と、前記配線に接続された電子部品と、前記第１の絶縁層の一方の面側に形成されて前記電子部品を覆う第２の絶縁層と、前記配線と電気的に接続した接続部とにより構成されるシート状のユニットを複数用意し、それらのユニットを、厚さ方向に隣り合うユニットの向きを交互に逆に配置して相互に積層して接合し、前記接続部を介して各ユニットの電子部品を相互に電気的に接続することを特徴としている。 In order to solve the problems described above, in the method of manufacturing an electronic parts packaging structure according to the present invention, a first insulating layer, and formed on said one surface of the first insulating layer wiring, the wiring configured and connected electronic component, a second insulating layer in which the first is formed on one surface of the insulating layer covering the electronic component, by said wiring and electrically connected to the connecting portion a sheet-like unit preparing a plurality of these units, arranged in opposite joined laminated to each other alternately the direction of the adjacent unit in the thickness direction, the electronic components of each unit via the connecting portions It is characterized in each other to electrically connect.
本発明では、厚さ方向に隣り合うユニットの向きを交互に逆に配置して接合するので、厚さ方向に隣り合うユニットにおいて第１の絶縁層、電子部品、配線及び第２の絶縁層の配置が対称となり、その結果電子部品と絶縁層及び配線（金属膜）との熱膨張係数の差に基づく熱応力が発生するとしても、それらのユニットにおいて熱応力が発生する方向が逆になり、電子部品実装構造の反りが回避される。 In the present invention, since the bonding arranged to reverse the direction of the unit adjacent in the thickness direction alternately, the first insulating layer in the unit adjacent in the thickness direction, of the electronic components, wiring and the second insulating layer arrangement is symmetrical, so that even if the thermal stress is generated based on the difference in thermal expansion coefficient between the electronic component and the insulating layer and a wiring (a metal film) becomes the direction in which thermal stress is generated is reversed in those units, warpage of the electronic component mounting structure is avoided.
前記ユニットは、例えば 基板上に絶縁性樹脂からなる第１の絶縁層を形成する第１工程と、前記第１の絶縁層をパターニングして開口部を形成する第２工程と、前記開口部の内側に露出した前記基板をエッチングして窪みを形成する第３工程と、前記開口部の内側に金属を充填して端子を形成する第４工程と、前記第１の絶縁層の上に、前記端子と接続する配線を形成する第５工程と、前記配線の上に電子部品を接合する第６工程と、前記第１の絶縁層の上に前記電子部品を覆う第２の絶縁層を形成する第７工程と、前記第２の絶縁層の上面から前記配線に到達する孔を形成する第８工程と、前記孔内に金属を充填してコンタクトビアを形成する第９工程と、前記基板を除去する第１０工程とを経て製造される。 The unit is first made of an insulating resin on a substrate, for example a first step of forming an insulating layer, a second step of forming an opening by patterning the first insulating layer, of the opening a third step of forming a recess the substrate exposed to the inside by etching, and a fourth step of forming a terminal by filling a metal on the inside of the opening, on the first insulating layer, the forming a fifth step of forming a wiring connected to the terminal, and a sixth step of bonding the electronic component on the wiring, the second insulating layer covering the electronic component on the first insulating layer a seventh step, an eighth step of forming a hole reaching the wiring from the upper surface of the second insulating layer, and a ninth step of forming a contact via by filling a metal into said hole, said substrate It is manufactured through a tenth step of removing.
このようにして製造されたユニットは、コアとなる高強度の支持基板（厚い基板）を有していないため、支持基板を有する従来の電子部品実装構造に比べて電子部品のより一層の高密度化が達成される。 Such units thus manufactured, because it does not have the supporting substrate of high strength Core (thick substrate), higher density of electronic components in comparison with the conventional electronic component mounting structure having a supporting substrate It is achieved. また、本発明方法においては、第９工程までは第１の絶縁層、配線、電子部品及び第２の絶縁層等を基板により支持しており、例えば２つのユニットを接合した後に第１０工程を実施して基板を除去するので、製造工程におけるハンドリングに支障が生じることはない。 In the present invention method, the first insulating layer until the ninth step, the wiring, electronic components and has a second insulating layer or the like is supported by a substrate, a tenth step after bonding the two units e.g. since implemented to remove the substrate, it does not occur any trouble handling in the manufacturing process.
本発明の一つの好適な態様では、第１工程において、前記基板の下面に第３の絶縁層を形成し、前記第９工程の終了から第１０工程の開始までの間に、前記第３の絶縁層を除去する。 In one preferred mode of the present invention, in a first step, the third insulating layer is formed on the lower surface of the substrate, between the end of the ninth step and the start of the tenth step, the third removing the insulating layer. 基板の上面のみに絶縁層（第１の絶縁層）を形成した場合、基板と絶縁層との熱膨張係数の差により、ポストベーキング等の熱処理時に反りが発生することが考えられる。 The case of forming only the insulating layer upper surface of the substrate (first insulating layer), the difference in thermal expansion coefficient between the substrate and the insulating layer, the warpage is considered to occur during the heat treatment of the post-baking, and the like. 上述したように基板の下面にも絶縁層（第３の絶縁層）を形成しておけば、基板の上下で反りが発生する方向が逆となり、結果的に反りが抑制される。 By forming an insulating layer to the lower surface of the substrate as described above (the third insulating layer), the direction of warpage occurs in the upper and lower substrates is reversed, resulting in warpage is suppressed.
更に、上記した課題を解決するため、本発明に係る他の電子部品実装構造の製造方法では、第１の絶縁層と、前記第１の絶縁層の一方の面上に形成された配線と、前記配線に接続された電子部品と、前記第１の絶縁層の一方の面側に形成されて前記電子部品を覆う第２の絶縁層とにより構成される複数のシート状のユニットを形成する工程と、前記複数のユニットを、厚さ方向に隣り合うユニットの向きを交互に逆に配置して積層し積層構造体とする工程と、前記積層構造体に各ユニットの前記第１の絶縁層、前記配線及び前記第２の絶縁層を貫通する貫通孔を形成する工程と、前記貫通孔内に導電体を充填して各ユニットの前記配線間を電気的に接続する接続部を形成する工程とを有することを特徴としている。 Furthermore, in order to solve the problems described above, in the manufacturing method of the other electronic component mounting structure according to the present invention, a first insulating layer, and formed on said one surface of the first insulating layer wiring, forming an electronic component connected to the wiring, the first plurality of sheet-shaped unit comprised formed on one surface of the insulating layer by a second insulating layer covering the electronic component When the a plurality of units, a step to be arranged alternately inverted orientation of the unit adjacent in the thickness direction by stacking the laminated structure, the first insulating layer of each unit to the laminated structure, forming a step of forming a through hole penetrating through the wire and the second insulating layer, the inter-wire connection portions for electrically connecting each unit by filling a conductor in the through-hole It is characterized by having a.
本発明においても、厚さ方向に隣り合うユニットの向きを交互に逆に配置するので、厚さ方向に隣り合うユニットにおいて第１の絶縁層、電子部品、配線及び第２の絶縁層の配置が対称となり、その結果電子部品と絶縁層及び配線（金属膜）との熱膨張係数の差に基づく熱応力が発生するとしても、それらのユニットにおいて熱応力が発生する方向が逆になり、電子部品実装構造の反りが回避される。 In the present invention, since disposed opposite the direction of the unit adjacent in the thickness direction alternately, the first insulating layer in the unit adjacent in the thickness direction, the arrangement of the electronic components, wiring and the second insulating layer It becomes symmetric, resulting even thermal stress is generated based on the difference in thermal expansion coefficient between the electronic component and the insulating layer and the wiring (metal film), the direction in which the thermal stress is generated is reversed in those units, the electronic component warpage of the mounting structure is avoided.
本発明の一つの好適な形態では、前記ユニットは、基板上に絶縁性樹脂からなる第１の絶縁層を形成する工程と、前記第１の絶縁層上に配線を形成する工程と、前記配線の上に電子部品を接合する工程と、前記第１の絶縁膜の上に前記電子部品を覆う第２の絶縁層を形成する工程とを経て形成される。 In one preferred form of the present invention, it said unit comprises the steps of forming a first insulating layer made of an insulating resin on a substrate, forming a wiring on the first insulating layer, the wiring It is formed through the step of bonding the electronic component, and forming a second insulating layer covering the electronic component on the first insulating film on the. また、前記積層構造体は、前記基板を有する２つのユニットを前記電子部品が搭載された面を向い合わせて接合してペアユニットとするペアユニット形成工程と、前記ペアユニットから前記基板を除去する基板除去工程と、複数のペアユニットを積層する積層工程と順番に実施して形成される。 Further, the laminated structure, the two units electronic component removes pair units forming step of the pair unit are bonded face-to-face with the mounted surface, the substrate from the pair unit having said substrate a substrate removal step, is formed by implementing the laminating process and the order of stacking a plurality of pairs units.
本発明では、積層構造体に各ユニットの第１の絶縁層、配線及び第２の絶縁層を貫通する貫通孔を形成し、その後貫通孔内に導電体を充填して各ユニットの配線間を電気的に接続する。 In the present invention, a first insulating layer of each unit in the laminated structure, the wiring and the second to form a through hole penetrating through the insulating layer, between then in the through hole filled with a conductor wire of each unit It is electrically connected to each other. この場合、例えば最下層のユニットのみ基板を残しておき、積層構造体の上面から基板に到達する貫通孔をドリル又はレーザ照射により形成し、めっき法により貫通孔内に銅等の導電体を堆積させることにより、接続部を形成することができる。 In this case, for example, only the lowermost units leave substrate, a through hole that reaches from the upper surface of the laminated structure on the substrate is formed by drilling or laser irradiation, depositing a conductor such as copper in the through hole by plating by, it is possible to form the connection portion. 前記最下層のユニットの基板は、接続部形成後に除去する。 The substrate of the lowermost unit is removed after the connection part formation.
以下、本発明の実施形態について、添付の図面を参照して説明する。 Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings.
図１は、本発明の第１の実施形態の電子部品実装構造を示す断面図である。 Figure 1 is a sectional view showing an electronic parts packaging structure of a first embodiment of the present invention.
本実施形態の電子部品実装構造（半導体装置）１は、複数個（図１では４個）のシート（薄膜）状のユニット１０を絶縁層１１を挟んで積層した構造を有している。 Electronic parts packaging structure of the present embodiment (the semiconductor device) 1 includes a sheet (thin film) like unit 10 a plurality of (in Fig. 1 4) was laminated to sandwich the insulating layer 11 structure. 各ユニット１０は、絶縁性樹脂層（第２の絶縁層）３０と、絶縁性樹脂層３０内に埋設された半導体チップ（電子部品）２７と、ソルダーレジスト層（第１の絶縁層）２２と、配線２６と、端子２４と、コンタクトビア３１とにより構成されている。 Each unit 10 includes an insulating resin layer (second insulating layer) 30, a semiconductor chip (electronic component) 27 which is embedded in the insulating resin layer 30, a solder resist layer (first insulating layer) 22 and , the wiring 26, a terminal 24, a the contact via 31. １つのユニット１０の厚さは例えば２００μｍ程度（１００〜３００μｍ程度）であり、上下方向（厚さ方向）に隣り合うユニット１０は、端子２４又はコンタクトビア３１（接続部）を介して相互に電気的に接続されている。 The thickness is, for example, 200μm approximately one unit 10 is (about 100 to 300 [mu] m), the unit 10 adjacent in the vertical direction (thickness direction) are mutually electrically through the terminal 24 or the contact vias 31 (connection portion) They are connected to each other.
本実施形態の電子部品実装構造１では、図１に示すように、上下方向に隣り合うユニット１０が相互に逆向きに配置されていることが特徴の一つとなっている。 In the electronic component mounting structure 1 of the present embodiment, as shown in FIG. 1, it is one of the features of the unit 10 adjacent in the vertical direction are arranged in opposite directions to each other. すなわち、上下方向に隣り合う２つのユニット１０では、ソルダーレジスト層２２、半導体チップ２７、配線２６、端子２４及びコンタクトビア３１等の配置が対称となっている。 That is, in the two units 10 adjacent in the vertical direction, the solder resist layer 22, the semiconductor chip 27, wiring 26, the arrangement of such terminals 24 and contact via 31 has a symmetrical.
１つのユニット１０は、上述したように、絶縁性樹脂層３０と、半導体チップ２７と、ソルダーレジスト層２２と、配線２６と、端子２４と、コンタクトビア３１とにより構成されている。 One unit 10, as described above, the insulating resin layer 30, the semiconductor chip 27, the solder resist layer 22, the wiring 26, a terminal 24, a the contact via 31. ソルダーレジスト層２２は、絶縁性樹脂層３０の一方の面に接合している。 The solder resist layer 22 is bonded to one surface of the insulating resin layer 30. 配線２６はソルダーレジスト層２２の絶縁性樹脂層３０側の面上に形成されており、半導体チップ２７の接続端子とバンプ２８を介して電気的に接続されている。 Wiring 26 is formed on the surface of the insulating resin layer 30 side of the solder resist layer 22 are electrically connected via the connection terminals and the bumps 28 of the semiconductor chip 27. 半導体チップ２７とソルダーレジスト層２２との間には、半導体チップ２７の素子形成面を保護するためにアンダーフィル（保護膜）２９が充填されている。 Between the semiconductor chip 27 and the solder resist layer 22, underfill (protective film) 29 for protecting the element formation surface of the semiconductor chip 27 is filled.
端子２４はソルダーレジスト層２２を貫通して形成されており、配線２６の一方の面に接合されている。 Terminals 24 are formed through the solder resist layer 22 is bonded to one surface of the wiring 26. また、コンタクトビア３１は絶縁性樹脂層３０に埋め込まれて形成されており、配線２６の他方の面に接合されている。 The contact vias 31 are formed is embedded in the insulating resin layer 30 is bonded to the other surface of the wiring 26.
上述の如く、本実施形態の電子部品実装構造１では、各ユニット１０がソルダーレジスト層２２、半導体チップ２７及び絶縁性樹脂層３０等により構成されており、コアとなる高強度の支持基板（換言すると、厚い基板）を有していない。 As described above, in the electronic parts packaging structure 1 of the present embodiment, each unit 10 is solder resist layer 22 is constituted by a semiconductor chip 27 and the insulating resin layer 30 and the like, the supporting substrate of high strength Core (i.e. Then, it does not have a thick substrate). そして、複数のユニット１０を積層することで全体的な強度を確保している。 And so as to ensure the overall strength by laminating a plurality of units 10. これにより、本実施形態の電子部品実装構造１では、支持基板を有する従来の電子部品実装構造に比べて、より一層の高密度化が可能になるという効果を奏する。 Thus, in the electronic parts packaging structure 1 of the present embodiment, as compared with the conventional electronic component mounting structure having a supporting substrate, an effect that becomes more possible to further densification.
また、本実施形態の電子部品実装構造１では、上下方向に隣り合うユニット１０において、ソルダーレジスト層２２、半導体チップ２７、配線２６、端子２４及びコンタクトビア３１等が対称の関係で配置されている。 Further, in the electronic parts packaging structure 1 of the present embodiment, the unit 10 adjacent in the vertical direction, the solder resist layer 22, the semiconductor chip 27, wiring 26, terminals 24 and contact vias 31, etc. are arranged in a symmetrical relationship . このため、半導体チップ２７と絶縁性樹脂層３０及び配線（金属膜）２６との熱膨張係数の差に基づく熱応力が発生するとしても、上下方向に隣り合うユニット１０で熱応力による反りの方向が逆となり、その結果熱応力が相殺されて電子部品実装構造１に反りが発生することが防止される。 Therefore, as the thermal stress is generated based on the difference in the thermal expansion coefficient of the semiconductor chip 27 and the insulating resin layer 30 and the wiring (metal film) 26, the direction of the warp due to thermal stress in unit 10 adjacent in the vertical direction There becomes reversed, warpage resulting thermal stress is offset by the electronic parts packaging structure 1 is prevented from being generated.
また、本実施形態の電子部品実装構造１では、最外面がアクリル系樹脂又はエポキシ系樹脂からなるソルダーレジスト層２２に覆われている。 Further, in the electronic parts packaging structure 1 of the present embodiment, the outermost surface is covered with the solder resist layer 22 made of acrylic resin or epoxy resin. 一般的に、ソルダーレジスト層２２はエポキシ等の樹脂からなる絶縁性樹脂層３０に比べて強度が高い。 Generally, the solder resist layer 22 is higher strength than the insulating resin layer 30 made of a resin such as epoxy. このため、本実施形態では、エポキシ等の樹脂からなる絶縁性樹脂層が最外面に露出している場合に比べて、電子部品実装構造の強度が高く破損しにくいという利点もある。 Therefore, in this embodiment, it is compared with the case where the insulating resin layer made of a resin such as epoxy is exposed on the outermost surface, an advantage that the strength of the electronic component mounting structure is high is not easily damaged.
図２〜図６は、本発明の第１の実施形態に係る電子部品実装構造の製造方法を工程順に示す断面図である。 Figures 2-6 are cross-sectional views sequentially showing the steps of producing the electronic component mounting structure according to a first embodiment of the present invention. なお、図２〜図６では説明を簡単にするために１個分のユニット形成領域しか示していないが、実際には１枚の基板２１の上に複数のユニット１０を同時に形成する。 Although only shown unit formation region for one piece in order to simplify the explanation in FIGS. 2 to 6, in practice to simultaneously form a plurality of units 10 on a single substrate 21.
まず最初の工程では（図２（ａ）参照）、例えば大きさが３００ｍｍ×５００ｍｍ、厚さが０．１ｍｍの銅（Ｃｕ）からなる基板２１を用意する。 First in the first step preparing a substrate 21 made of (see FIG. 2 (a)), for example, size of 300 mm × 500 mm, thickness 0.1mm copper (Cu). そして、スクリーン印刷法により、基板２１の一方の面上に感光性のソルダーレジストを塗布して、厚さが例えば２０〜３０μｍのソルダーレジスト層２２を形成する。 Then, by the screen printing method, one photosensitive solder resist on the surface of the substrate 21 is coated to form, for example, a solder resist layer 22 of 20~30μm thickness. 次に、所定の露光マスク（不図示）を介してソルダーレジスト層２２を露光する。 Then, exposing the solder resist layer 22 through a predetermined exposure mask (not shown). その後、現像処理を施して、ソルダーレジスト層２２に、基板２１の表面が露出する開口部２２ａを形成する。 Thereafter, by performing a development process, the solder resist layer 22 to form an opening 22a in which the surface of the substrate 21 is exposed. その後、例えば１５０〜２００℃の温度でポストベークする。 Then, post-baked at a temperature of, for example, 150~200 ℃.
なお、基板２１には、ソルダーレジスト層２２等を支持する支持体としての役割と、電解めっき時の電流供給層としての役割とがある。 Note that the substrate 21, there are a role as a support for supporting the solder resist layer 22 and the like, and serves as a current supply layer during electroplating. 従って、基板２１にはある程度の強度と導電性とが要求される。 Thus, is some strength and electrical conductivity and is required to the substrate 21. また、基板２１は、後述する工程で容易に除去できるものであることが必要である。 The substrate 21 is required to be as it can be easily removed in step described later. 基板２１としては、上述した銅板の他にも、例えば４２アロイ（Ｆｅ−Ｎｉ合金）板を使用することができる。 As the substrate 21, in addition to the copper plate as described above, it can be used, for example 42 alloy (Fe-Ni alloy) plate. 但し、基板２１の厚さが厚すぎると、後述の基板２１を除去する工程にかかる時間が長くなるので、ハンドリングに支障がない範囲で薄くすることが好ましい。 However, when the thickness of the substrate 21 is too thick, since it takes time increases to the step of removing the substrate 21 described later, it is preferable to thin in a range not hinder the handling.
次の工程では（図２（ｂ）参照）、ソルダーレジスト層２２をマスクとして基板２１をエッチングし、深さが数１０μｍ（例えば３０μｍ）の窪み２１ａを形成する。 In the next step (see FIG. 2 (b)), by etching the substrate 21 a solder resist layer 22 as a mask, the depth to form a recess 21a having 10 [mu] m (e.g., 30 [mu] m). この窪み２１ａの深さにより、端子２４がソルダーレジスト層２２から突出する突出量が決定される。 The depth of the recess 21a, the projecting amount of the terminal 24 projects from the solder resist layer 22 is determined.
その後、次の工程（図２（ｃ）参照）において、ソルダーレジスト層２２をマスクとしてはんだを電解めっきし、窪み２１ａの表面に厚さが例えば２０〜７０μｍのはんだ層２３を形成する。 Then, in the next step (see FIG. 2 (c)), and electroplating the solder solder resist layer 22 as a mask to form a solder layer 23 having a thickness of, for example, 20~70μm of the surface of the recess 21a. このはんだ層２３は、後述する工程において基板２１をエッチングにより除去する際にエッチングストッパーとして作用する。 The solder layer 23 serves the substrate 21 as an etching stopper when removing the etching in the step described later. なお、はんだ層２３に替えて、例えば錫（Ｓｎ）をめっきしてもよい。 Instead of the solder layer 23, it may be plated, for example, tin (Sn).
このはんだ層２３を形成した後、プラズマ処理（ドライエッチング）を施して、ソルダーレジスト層２２の表面を粗化しておく。 After forming the solder layer 23 is subjected to a plasma treatment (dry etching), previously roughened surface of the solder resist layer 22. このプラズマ処理は必須ではないが、後工程で使用するドライフィルムやめっき層の密着性を十分確保するために、実施しておくことが好ましい。 This plasma treatment is not essential, in order to sufficiently ensure adhesion of the dry film and the plated layer to be used in a later step, it is preferable to carried out.
次の工程では（図２（ｄ）参照）、銅の電解めっきにより、ソルダーレジスト層２２の開口部２２ａに銅を充填して、端子２４を形成する。 In the next step (see FIG. 2 (d)), by electrolytic plating of copper and filled with copper to the opening 22a of the solder resist layer 22 to form a terminal 24. その後、銅を無電解めっきして、ソルダーレジスト層２２の上及び端子２４の上にシード層（不図示）を形成する。 Thereafter, a copper electroless plating to form a seed layer (not shown) on the upper and the terminal 24 of the solder resist layer 22.
次の工程では（図２（ｅ）参照）、基板２１の上側にドライフィルム（感光性レジストフィルム）２５を貼り付ける。 In the next step (see FIG. 2 (e)), paste dry film (photosensitive resist film) 25 on the upper side of the substrate 21. そして、所定の露光マスク（不図示）を使用してドライフィルム２５を露光した後、現像処理を施してドライフィルム２５に開口部２５ａを形成する。 Then, after exposing the dry film 25 by using a predetermined exposure mask (not shown) to form an opening 25a in the dry film 25 is subjected to developing processing. この開口部２５ａは、次工程で配線２６を形成するためのものである。 The opening 25a is for forming the wiring 26 in the next step.
次の工程では（図３（ａ）参照）、銅の電解めっきにより、ドライフィルム２５の開口部２５ａに銅を埋め込み、配線２６を形成する。 In the next step (see FIG. 3 (a)), by electrolytic plating of copper, embedded copper opening 25a of the dry film 25, a wiring 26. そして、次の工程では（図３（ｂ）参照）、剥離液によりドライフィルム２５を剥離する。 Then, (see FIG. 3 (b)) In the next step, peeling off the dry film 25 by a stripping solution. その後、露出しているシード層をエッチングにより除去して、各配線２６間を電気的に分離する。 Thereafter, a seed layer exposed is removed by etching, providing electrical isolation between the wirings 26.
次の工程では（図３（ｃ）参照）、配線２６に半導体チップ２７をフリップチップ接合する。 In the next step (see FIG. 3 (c)), flip-chip bonding the semiconductor chip 27 to the wiring 26. この半導体チップ２７は、厚さが例えば１５０μｍ以下（好適には５０μｍ程度）に薄型化されており、素子形成面（図３（ｃ）では下側）の縁部に接続電極が設けられている。 The semiconductor chip 27 is, for example, 150μm or less in thickness and (preferably about 50 [mu] m) is thinned to have connection electrode is provided on the edge of the element formation surface (lower side in FIG. 3 (c)) . そして、接続電極の上（図３（ｃ）では下側）にはバンプ（例えばＡｕスタッドバンプ）２８が形成され、このバンプ２８により配線２６と電気的に接続される。 Then, on the connection electrode (FIG. 3 (c) in the lower side) is formed bumps (e.g. Au bump) 28 is electrically connected to the wiring 26 by the bumps 28.
次の工程では（図３（ｄ）参照）、半導体チップ２７と基板２１（ソルダーレジスト層２２及び配線２６）との間にアンダーフィル２９を充填する。 In the next step of filling the underfill 29 between (see FIG. 3 (d)), the semiconductor chip 27 and the substrate 21 (the solder resist layer 22 and the wiring 26). アンダーフィル２９としては、例えばエポキシ樹脂を使用することができる。 The underfill 29 may be used, for example epoxy resin. アンダーフィル２２中には例えばシリカ等のフィラーを含有させ、アンダーフィル２９の熱膨張係数が半導体チップ２７の熱膨張係数とソルダーレジスト層２２の熱膨張係数との中間になるように調整することが好ましい。 The underfill 22 is contained a filler such as silica or the like, can be adjusted to the thermal expansion coefficient of the underfill 29 is intermediate the thermal expansion coefficient and the thermal expansion coefficient of the solder resist layer 22 of the semiconductor chip 27 preferable.
次の工程では（図４（ａ）参照）、基板２１の上に、半導体チップ２７を覆うようにフィルム状のエポキシ樹脂を貼り付けて、絶縁性樹脂層３０を形成する。 In the next step (see FIG. 4 (a)), on the substrate 21, paste the film-like epoxy resin so as to cover the semiconductor chip 27 to form an insulating resin layer 30. その後、絶縁性樹脂層３０を構成するエポキシ樹脂を硬化（キュア）させる。 Then, make the cured epoxy resin constituting the insulating resin layer 30 (curing). フィルム状のエポキシ樹脂を貼り付ける替わりに、エポキシ樹脂を塗布して絶縁性樹脂層３０を形成してもよい。 Instead paste film-like epoxy resin, by coating the epoxy resin may be formed an insulating resin layer 30. また、エポキシ樹脂に替えて、ポリイミド又はその他の絶縁性樹脂を使用してもよい。 Further, in place of the epoxy resin, it may be used polyimide or other insulating resin.
次の工程では（図４（ｂ）参照）、絶縁性樹脂層３０を炭酸ガス（ＣＯ２ ）レーザ等により穴あけ加工して、配線２６が露出する開口部３０ａを形成する。 In the next step (see FIG. 4 (b)), the insulating resin layer 30 by drilling by carbon dioxide (CO2) laser or the like to form an opening 30a which the wiring 26 is exposed. 開口部３０ａの直径は、例えば１００μｍである。 The diameter of the opening 30a is, for example, 100 [mu] m.
次の工程では（図４（ｃ）参照）、電解めっきにより、開口部３０ａ内に銅を充填して、コンタクトビア３１を形成する。 In the next step (see FIG. 4 (c)), by electrolytic plating, by filling a copper in the opening 30a, to form a contact via 31. この場合に、図４（ｃ）に示すように、コンタクトビア３１の頂部が絶縁性樹脂層３０よりも若干（例えば、３０μｍ程度）盛り上がるようにする。 In this case, as shown in FIG. 4 (c), the top of the contact via 31 is slightly larger than the insulating resin layer 30 (e.g., about 30 [mu] m) rises so. その後、コンタクトビア３１の頂部にＮｉ（ニッケル）及びＡｕ（金）を順次電解めっきして、厚さが数μｍのＮｉ−Ａｕめっき層（不図示）を形成する。 Then, by sequentially electroplating Ni (nickel) and Au (gold) on top of the contact vias 31, thickness to form a number [mu] m Ni-Au plating layer (not shown).
このようにしてユニット１０が形成された基板２１を複数用意する。 Thus to prepare a plurality of substrates 21 which unit 10 is formed in the. そして、次の工程において（図５（ａ）参照）、２枚の基板２１を、半導体チップ搭載面を向い合わせて配置し、両者の間に絶縁層１１を挟んで接合する。 Then, (see FIG. 5 (a)) in the next step, the two substrates 21, face-to-face the semiconductor chip mounting surface is arranged, joined across the insulating layer 11 therebetween. 絶縁層１１として異方性導電フィルム（ＡＣＦ：Anisotropic Conductive Film ）を使用し、プレス機により加圧して各基板２１に形成されたユニット１０を接合すると、異方性導電フィルムのうち対向するコンタクトビア３１間の部分が強く加圧されて厚さ方向（Ｚ方向）に導電性を示すようになり、それらのコンタクトビア３１間が電気的に接続される。 Anisotropic conductive film as the insulating layer 11 (ACF: Anisotropic Conductive Film) using, when bonding the unit 10 formed by pressurizing by a press machine to each substrate 21, contact vias facing out of the anisotropic conductive film is pressed portion strongly pressurized between 31 now shows the conductivity in the thickness direction (Z-direction), during their contact vias 31 are electrically connected. 以下、このようにして接合された２つのユニット１０を、ペアユニットと呼ぶ。 Hereinafter, the two units 10 bonded this way, referred to as paired unit.
なお、本実施形態では絶縁層１１として異方性導電フィルムを使用しているが、２つのユニット１０の相互に対向するコンタクトビア３１同士をはんだ等により接合した後、ユニット１０間に絶縁性樹脂を充填するなどの方法により絶縁層１１を形成してもよい。 Although in this embodiment uses an anisotropic conductive film as the insulating layer 11, after the each other contact via 31 facing each other of the two units 10 are joined by soldering or the like, an insulating resin between the unit 10 an insulating layer may be formed 11 by a method such as filling.
次の工程では（図５（ｂ）参照）、エッチングによりユニット１０から基板２１を除去する。 In the next step (see FIG. 5 (b)), removing the substrate 21 from the unit 10 by etching. 本実施形態では基板２１として銅板を使用しているので、エッチング液としては例えば塩化第二鉄水溶液、塩化第二銅水溶液又は過硫酸アンモニウムを使用する。 Since the present embodiment uses a copper plate as a substrate 21, an aqueous solution of ferric as an etchant for example chloride, using a cupric chloride aqueous solution or ammonium persulfate. この場合、端子２４の端面ははんだ層２３に覆われているため、端子２４のエッチングが防止される。 In this case, the end surface of the terminal 24 because it is covered with the solder layer 23, the etching of the terminal 24 is prevented.
次の工程では（図６参照）、絶縁層１１を挟んで複数のペアユニットを重ね合わせて接合する。 In the next step (see FIG. 6), joined by overlapping a plurality of pairs units across the insulating layer 11. この場合も、本実施形態では絶縁層１１として異方性導電フィルムを使用して上下方向に隣り合う端子２４間を電気的に接続しているが、端子２４間をはんだ等により接合した後、ペアユニット間に絶縁性樹脂を充填するなどの方法により絶縁層１１を形成してもよい。 Again, in the present embodiment is electrically connected between terminals 24 adjacent in the vertical direction by using the anisotropic conductive film as the insulating layer 11, after a while the terminal 24 are joined by soldering or the like, by a method such as filling the insulating resin between the pair units may be formed an insulating layer 11.
このようにして複数のユニット１０を積層して積層構造体１ａを形成した後、この積層構造体１ａを切断して個々の電子部品実装構造１を分離する。 After thus to form a laminated structure 1a by stacking a plurality of units 10, to separate the individual electronic parts packaging structure 1 by cutting the laminated structure 1a. これにより、図１に示す本実施形態の電子部品実装構造１が完成する。 Thus, the electronic parts packaging structure 1 of the present embodiment shown in FIG. 1 is completed.
本実施形態の製造方法によれば、２つのユニット１０を接合してペアユニットとするまでの間はソルダーレジスト層２２及び絶縁性樹脂層３０等が基板２１により支持されている。 According to the manufacturing method of this embodiment, until the paired unit by joining two units 10 solder resist layer 22 and the insulating resin layer 30, etc. it is supported by the substrate 21. このため、ハンドリングが容易である。 Therefore, handling is easy. また、ペアユニットとした後に基板２１を除去し、複数のペアユニットを重ね合わせて本実施形態に係る電子部品実装構造（半導体装置）１を製造するので、支持基板を有する従来の電子部品実装構造に比べて薄型化でき、より一層の高密度化が達成される。 Further, the substrate 21 is removed after the paired units, since the production of electronic parts packaging structure (semiconductor device) 1 according to this embodiment by superposing a plurality of pairs units, the conventional electronic component mounting structure having a supporting substrate It can thinner than, the higher density is achieved.
更に、本実施形態の製造方法により製造された電子部品実装構造１では、上下方向に隣り合うユニット１０において、ソルダーレジスト層２２、半導体チップ２７、配線２６、端子２４及びコンタクトビア３１等の配置が対称になっている。 Further, in the electronic component mounting structure 1 manufactured by the manufacturing method of this embodiment, the unit 10 adjacent in the vertical direction, the solder resist layer 22, the semiconductor chip 27, wiring 26, the arrangement of such terminals 24 and contact vias 31 It is symmetrical. このため、半導体チップ２７、絶縁性樹脂層３０及び配線（金属膜）２６等の熱膨張係数の差に起因する反りの発生方向が上下方向に隣り合うユニット１０で逆になり、その結果電子部品実装構造１に反りが発生することが回避される。 Therefore, semiconductor chip 27, are reversed in unit 10 generating direction of the warp adjacent to the vertical direction due to the difference in thermal expansion coefficient such as an insulating resin layer 30 and the wiring (metal film) 26, as a result electronic component warpage is prevented from occurring in the mounting structure 1.
例えば、配線２６、端子２４及びコンタクトビア３１を構成する銅の熱膨張係数は１６．２ｐｐｍ／℃、半導体チップ２７（シリコンチップ）の熱膨張係数は３．４ｐｐｍ／℃、絶縁性樹脂層３０（エポキシ樹脂）の熱膨張係数は６０ｐｐｍ／℃、アンダーフィル２９（エポキシ系樹脂）の熱膨張係数は３３ｐｐｍ／℃、ソルダーレジスト層２２（エポキシ系樹脂）の熱膨張係数は６０ｐｐｍ／℃であるが、本実施形態によれば、このように熱膨張係数が異なる部材により構成された電子部品実装構造（半導体装置）においても、反りが極めて少なく、製品歩留りが高い。 For example, the wiring 26, the thermal expansion coefficient of the copper constituting the terminals 24 and contact via 31 is 16.2ppm / ℃, thermal expansion coefficient of the semiconductor chip 27 (silicon chip) is 3.4 ppm / ° C., the insulating resin layer 30 ( thermal expansion coefficient of the epoxy resin) of 60 ppm / ° C., the thermal expansion coefficient of the underfill 29 (epoxy resin) is 33 ppm / ° C., the thermal expansion coefficient of the solder resist layer 22 (epoxy resin) is 60 ppm / ° C., According to this embodiment, even in such a thermal expansion coefficient different member by the configuration electronic parts packaging structure (semiconductor device), the warpage is extremely small, a high product yield.
なお、上述した実施形態では図５（ａ）に示す工程において２枚のユニット１０を接合してペアユニットとした後、図５（ｂ）に示す工程において基板２１を除去し、図６に示す工程において複数のペアユニットを重ね合わせて積層構造体１ａとしているが、図４（ｃ）に示す工程の後に、図７に示すようにユニット１０から基板２１を除去し、その後図６に示すように複数のユニット１０を交互に向きを変えて絶縁層１１を挟んで重ね合わせて接合してもよい。 Note that after the pair unit by joining unit 10 of the two in the step shown in FIG. 5 (a) In the embodiment described above, and removing the substrate 21 in the step shown in FIG. 5 (b), 6 although a stacked structure body 1a by superimposing a plurality of pairs units in step, after the step shown in FIG. 4 (c), removing the substrate 21 from the unit 10 as shown in FIG. 7, as shown in subsequent Figure 6 They may be joined by overlapping across the insulating layer 11 by changing the direction alternately a plurality of units 10 to.
また、上記の実施形態では半導体チップ２７の素子形成面を基板２１に向けて搭載する場合（いわゆるフェースダウン）について説明したが、本発明は半導体チップ２７の素子形成面を基板２１と逆側に向けて搭載し、ワイヤボンディングで配線と電気的に接続する場合（いわゆるフェースアップ）に適用することも可能である。 Further, in the above embodiment has been described for the case (a so-called face-down) for mounting towards the element formation surface of the semiconductor chip 27 to the substrate 21, but the present invention is an element forming surface of the semiconductor chip 27 to the substrate 21 and the opposite side mounted towards, it can be applied to a case (the so-called face-up) for connecting the wiring electrically by wire bonding.
図８は本発明の第２の実施形態の電子部品実装構造の製造方法を示す断面図、図９は同じくその模式平面図（全体図）である。 Figure 8 is a sectional view showing a method of manufacturing an electronic parts packaging structure of a second embodiment of the present invention, FIG. 9 is also the schematic plan view (overall view). なお、図８において、図５（ｂ）と同一物には同一符号を付している。 In FIG. 8, the same reference numerals are denoted to the same components as in FIG. 5 (b).
本実施形態が第１の実施形態と異なる点は、基板２１をエッチングにより除去する際に縁部を枠状に残すことにあり、その他の構成は基本的に第１の実施形態と同様であるので、ここでは重複する部分の説明は省略する。 The present embodiment is different from the first embodiment consists in leaving the edge in removing the substrate 21 by etching in a frame shape, other configurations are basically the same as those of the first embodiment since, description thereof will be omitted for portions which are the same here.
第１の実施形態では、図５（ｂ）に示す工程においてユニット１０から基板２１を完全に除去していた。 In the first embodiment, it was completely removing the substrate 21 from the unit 10 in the step shown in Figure 5 (b). 前述したように、第１の実施形態では１枚の基板２１を使用して複数のユニット１０を同時に形成するので、同時に形成するユニット１０の数にもよるが、基板２１を除去すると剛性が不足してハンドリングに支障がでることが考えられる。 As described above, since in the first embodiment to form a plurality of units 10 using one substrate 21 at the same time, depending on the number of units 10 to be formed at the same time, rigidity is insufficient when removing the substrate 21 it is considered that the problem is out in the handling and.
そこで、第２の実施形態においては、基板２１をエッチングする際に、フォトリソグラフィ法を用いて図８，図９に示すように、外縁に沿って枠状に金属膜（基板２１の縁部）２１ａを残す。 Therefore, in the second embodiment, when etching the substrate 21, FIG. 8 using a photolithography method, as shown in FIG. 9, (the edge of the substrate 21) a metal film in a frame shape along the outer edge leave a 21a.
これにより、ハンドリング時の撓みが抑制され、ハンドリングが容易になるという効果を奏する。 Thereby, deflection at the time handling is suppressed, an effect that the handling is facilitated. なお、この枠状の金属膜２１ａは、個々のユニット１０に分離する際に、切断して除去する。 Incidentally, the frame-shaped metal film 21a, when separated into individual units 10 are removed by cutting.
図１０（ａ），（ｂ）は、本発明の第３の実施形態の電子部品実装構造の製造方法を示す断面図である。 Figure 10 (a), (b) is a sectional view showing a method of manufacturing an electronic parts packaging structure of a third embodiment of the present invention.
本実施形態が第１の実施形態と異なる点は、基板２１の裏面（半導体チップ搭載面と逆側の面）にもソルダーレジスト層２２を形成することにあり、その他の構成は基本的に第１の実施形態と同様であるので、ここでは重複する部分の説明は省略する。 The present embodiment is different from the first embodiment is to form the solder resist layer 22 on the back surface (the surface of the semiconductor chip mounting surface and opposite side) of the substrate 21, other configurations are basically the since one of which is similar to the embodiment, description thereof will be omitted for portions which are the same here.
本実施形態においては、図１０（ａ）に示すように、基板２１の両面にソルダーレジスト層２２を形成する。 In the present embodiment, as shown in FIG. 10 (a), the solder resist layer 22 is formed on both surfaces of the substrate 21. その後、第１の実施形態と同様にして、図１０（ｂ）に示すように、端子２４及び配線２６を形成し、配線２６の上に半導体チップ２７を搭載する。 Thereafter, similarly to the first embodiment, as shown in FIG. 10 (b), to form a terminal 24 and wiring 26, for mounting a semiconductor chip 27 on the wiring 26. そして、半導体チップ２７と配線２６及びソルダーレジスト層２２との間にアンダーフィル２９を充填した後、半導体チップ２７を覆う絶縁樹脂層３０を形成し、更にコンタクトビア３１を形成する。 Then, after filling the underfill 29 between the semiconductor chip 27 and the wiring 26 and the solder resist layer 22, the insulating resin layer 30 covering the semiconductor chip 27, further forming a contact via 31.
次いで、裏面側のソルダーレジスト層２２を機械研磨又はプラズマエッチングにより除去する。 Then, the solder resist layer 22 on the back surface side is removed by mechanical polishing or plasma etching. そして、ユニット１０が形成された２つの基板２１を、図５（ａ）に示すように、その半導体チップ搭載面を相互に対向させて配置し、絶縁層１１を挟んで接合する。 Then, the two substrates 21 which unit 10 is formed, as shown in FIG. 5 (a), arranged mutually are opposed to the semiconductor chip mounting surface is bonded across the insulating layer 11. このようにしてペアユニットを形成した後、図５（ｂ）に示すように、基板２１をエッチングにより除去する。 After forming the pair unit this way, as shown in FIG. 5 (b), removing the substrate 21 by etching. その後、図６に示すように、複数のペアユニットを絶縁層１１を挟んで重ね合わせて接合する。 Thereafter, as shown in FIG. 6, joining a plurality of pairs units superimposed across the insulating layer 11.
第１の実施形態のように銅からなる基板２１の片面にソルダーレジスト層２２を形成した場合、１５０〜２００℃の温度でポストベークすると、基板２１とソルダーレジスト層２２との熱膨張係数の差により、基板２１に反りが発生してハンドリングに支障がでることがある。 The case of forming the solder resist layer 22 on one surface of a substrate 21 made of copper as in the first embodiment, when post-baked at a temperature of 150 to 200 ° C., the difference in thermal expansion coefficient between the substrate 21 and the solder resist layer 22 the warpage in the substrate 21 is sometimes detrimental to handling occurs. 本願発明者等の実験では、基板２１として直径が１５０ｍｍ、厚さが０．３ｍｍのウェハ形状の銅板を使用し、片側の面上のみにソルダーレジスト層２１を２５μｍの厚さに形成した場合、ポストベーク後に約６ｍｍの反りが発生することが確認された。 In the experiments of the inventors of the present invention, if the diameter as the substrate 21 is 150 mm, it is used a copper plate of a wafer shape of 0.3mm thickness, to form a solder resist layer 21 to a thickness of 25μm on only one surface, warp of about 6mm after the post-baking has been confirmed to occur. 一方、本実施形態のように、基板２１の両面にソルダーレジスト層２１を形成した場合は、反りが殆ど発生しなかった。 On the other hand, as in the present embodiment, the case of forming the solder resist layer 21 on both surfaces of the substrate 21, warpage hardly occurs. このことから、基板２１の裏面側にもソルダーレジスト層２１を形成することが好ましいことがわかる。 This indicates that it is preferable to form a solder resist layer 21 on the back surface side of the substrate 21.
なお、基板２１の裏面側に形成する層の材質は、その熱膨張係数が表面側のソルダーレジスト層の熱膨張係数に近いものであれば、特に限定されない。 The material of the layer to be formed on the back side of the substrate 21, the thermal expansion coefficient is equal to or close to the thermal expansion coefficient of the solder resist layer on the surface side is not particularly limited.
図１１は、本発明の第４の実施形態の電子部品実装構造を示す断面図である。 Figure 11 is a sectional view showing an electronic parts packaging structure of a fourth embodiment of the present invention.
本実施形態の電子部品実装構造（半導体装置）５１は、複数の（図１１では４個）のシート（薄膜）状のユニット６０を絶縁層６１を挟んで積層した構造を有している。 Electronic parts packaging structure (semiconductor device) 51 of this embodiment has a plurality of sheets (thin film) like unit 60 (FIG. 4 in 11) was laminated to sandwich the insulating layer 61 structure. 各ユニット６０は、絶縁性樹脂層（第２の絶縁層）８０と、絶縁性樹脂層８０内に埋設された半導体チップ（電子部品）７７と、ソルダーレジスト層（第１の絶縁層）７２と、配線７６とにより構成されている。 Each unit 60 includes an insulating resin layer (second insulating layer) 80, a semiconductor chip (electronic component) 77 that is embedded in the insulating resin layer 80, a solder resist layer (first insulating layer) 72 and It is constituted by the wiring 76. １つのユニット６０の厚さは例えば２００μｍ程度（１００〜３００μｍ程度）であり、各ユニット６０は当該電子部品実装構造５１の一方の面側から他方の面側に貫通する貫通電極８１（接続部）を介して相互に電気的に接続されている。 The thickness is, for example, 200μm approximately one unit 60 is (about 100 to 300 [mu] m), the through electrodes 81 each unit 60 penetrating from one surface side of the electronic component mounting structure 51 on the other side (connecting portion) They are electrically connected to each other through a. 貫通電極８１の両端部は、Ｎｉ−Ａｕめっき層８１ａで覆われている。 Both end portions of the through electrodes 81 are covered with Ni-Au plating layer 81a.
本実施形態の電子部品実装構造５１においても、第１の実施形態と同様に、上下方向に隣り合うユニット６０が相互に逆向きに配置されている。 Even in the electronic parts packaging structure 51 of the present embodiment, as in the first embodiment, unit 60 adjacent in the vertical direction are arranged in opposite directions to each other. すなわち、上下方向に隣り合う２つのユニット６０は、ソルダーレジスト層７２、半導体チップ７７、配線７６及び絶縁性樹脂層８０等の配置が対称となっている。 That is, the two units 60 adjacent in the vertical direction, the solder resist layer 72, the semiconductor chip 77, the arrangement of such wires 76 and the insulating resin layer 80 has a symmetrical.
１つのユニット６０は、上述したように、半導体チップ７７と、ソルダーレジスト層７２と、配線７６と、絶縁性樹脂層８０とにより構成されている。 One unit 60, as described above, a semiconductor chip 77, the solder resist layer 72, the wiring 76 is constituted by an insulating resin layer 80. ソルダーレジスト層７２は、絶縁性樹脂層８０の一方の面に接合されている。 The solder resist layer 72 is bonded to one surface of the insulating resin layer 80. 配線７６はソルダーレジスト層７２の絶縁性樹脂層８０側の面上に形成されており、半導体チップ７７の接続端子とバンプ７８を介して電気的に接続されている。 Wiring 76 is formed on the surface of the insulating resin layer 80 side of the solder resist layer 72 are electrically connected via the connection terminals and the bumps 78 of the semiconductor chip 77. 半導体チップ７７とソルダーレジスト層７２との間には、半導体チップ７７の素子形成面を保護するためにアンダーフィル（保護膜）７９が充填されている。 Between the semiconductor chip 77 and the solder resist layer 72, underfill (protective film) 79 for protecting the element formation surface of the semiconductor chip 77 is filled.
上述の如く、本実施形態の電子部品実装構造５１では、各ユニット６０がソルダーレジスト層７２、半導体チップ７７及び絶縁性樹脂層８０等により構成されており、コアとなる高強度の支持基板（換言すると、厚い基板）を有していない。 As described above, in the electronic parts packaging structure 51 of the present embodiment, each unit 60 is a solder resist layer 72 is constituted by a semiconductor chip 77 and the insulating resin layer 80 and the like, the supporting substrate of high strength Core (i.e. Then, it does not have a thick substrate). そして、複数のユニット６０を積層することで全体的な強度を確保している。 And so as to ensure the overall strength by laminating a plurality of units 60. これにより、本実施形態の電子部品実装構造５１は、第１の実施形態と同様に、従来に比べてより一層の高密度化が可能である効果を奏する。 Thus, the electronic parts packaging structure 51 of the present embodiment, as in the first embodiment, the effect is more possible higher density as compared with the conventional.
また、本実施形態の電子部品実装構造５１では、上下方向に隣り合うユニット６０において、ソルダーレジスト層７２、半導体チップ７７、配線７６及び絶縁性樹脂層８０等が対称の関係で配置されている。 Further, in the electronic parts packaging structure 51 of the present embodiment, in the unit 60 which are vertically adjacent to each other, the solder resist layer 72, the semiconductor chip 77, wiring 76 and the insulating resin layer 80, etc. are arranged in a symmetrical relationship. このため、半導体チップ７７と絶縁性樹脂層８０及び配線（金属膜）７６との熱膨張係数の差に基づく熱応力が発生するとしても、上下方向に隣り合うユニット６０で熱応力による反りの方向が逆となり、その結果熱応力が相殺されて電子部品実装構造５１に反りが発生することが防止される。 Therefore, as the thermal stress is generated based on the difference in thermal expansion coefficient between the semiconductor chip 77 and the insulating resin layer 80 and the wiring (metal film) 76, the direction of the warp due to thermal stress in units 60 adjacent in the vertical direction There becomes reversed, warpage resulting thermal stress is offset by the electronic component mounting structure 51 is prevented from occurring.
更に、本実施形態の電子部品実装構造５１では最外面がエポキシ樹脂等に比べて強度が高いアクリル系樹脂又はエポキシ系樹脂からなるソルダーレジスト層７２に覆われているので、第１の実施形態と同様に破損しにくいという利点もある。 Furthermore, since the outermost surface in the electronic component mounting structure 51 of the present embodiment is covered with the solder resist layer 72 strength than epoxy resin consisting of high acrylic resin or epoxy resin, in the first embodiment there is also an advantage that similarly difficult to damage.
更にまた、本実施形態においては、各ユニット６０が貫通電極８１により共通接続されているので、第１の実施形態に比べて各ユニット６０間の電気的接続の信頼性が高いという利点もある。 Furthermore, in the present embodiment, since each unit 60 are commonly connected by the through electrode 81, there is also an advantage of high reliability of electrical connection between each unit 60 as compared with the first embodiment.
図１２〜図１８は、本発明の第４の実施形態に係る電子部品実装構造の製造方法を工程順に示す断面図である。 12 to 18 are sectional views sequentially showing the steps of producing the electronic component mounting structure according to a fourth embodiment of the present invention. なお、図１２〜図１８では説明を簡単にするために１個分のユニット形成領域しか示していないが、実際には１枚の基板７１の上に複数のユニット６０を同時に形成する。 Although only shown unit formation region for one piece in order to simplify the explanation in FIGS. 12 to 18, in fact at the same time form a plurality of units 60 on a single substrate 71.
まず最初の工程では（図１２（ａ）参照）、例えば大きさが３００ｍｍ×５００ｍｍ、厚さが０．１ｍｍの銅（Ｃｕ）からなる基板７１を用意する。 First in the first step preparing a substrate 71 made of (see FIG. 12 (a)), for example, size of 300 mm × 500 mm, thickness 0.1mm copper (Cu). そして、スクリーン印刷法により、基板７１の一方の面上に感光性のソルダーレジストを塗布して、厚さが例えば２０〜３０μｍのソルダーレジスト層７２を形成する。 Then, by the screen printing method, one on the surface of the solder resist of the photosensitive is applied to the substrate 71 to form a solder resist layer 72 having a thickness of, for example, 20 to 30 [mu] m. その後、プラズマ処理（ドライエッチング）を施して、ソルダーレジスト層７２の表面を粗化しておく。 Thereafter, by performing the plasma treatment (dry etching), previously roughened surface of the solder resist layer 72. 次いで、銅を無電解めっきして、ソルダーレジスト層７２の上にシード層（不図示）を形成する。 Then, copper was electroless plated to form a seed layer (not shown) on the solder resist layer 72. なお、プラズマ処理は必須ではないが、後工程で使用するドライフィルムやめっき層の密着性を十分確保するために、実施しておくことが好ましい。 Although the plasma treatment is not essential, in order to sufficiently ensure adhesion of the dry film and the plated layer to be used in a later step, it is preferable to carried out.
次の工程では（図１２（ｂ）参照）、基板７１の上側（シード層の上）にドライフィルム（感光性レジストフィルム）７５を貼り付ける。 In the next step (see FIG. 12 (b)), paste dry film (photosensitive resist film) 75 on the upper side of the substrate 71 (on the seed layer). そして、所定の露光マスク（不図示）を使用してドライフィルム７５を露光した後、現像処理を施してドライフィルム７５に開口部７５ａを形成する。 Then, after exposing the dry film 75 by using a predetermined exposure mask (not shown) to form an opening 75a in the dry film 75 is subjected to developing processing. この開口部７５ａは、次の工程で配線７６を形成するためのものである。 The opening 75a is for forming the wiring 76 in the next step.
次の工程では（図１２（ｃ）参照）、銅の電解めっきにより、ドライフィルム７５の開口部７５ａ内に銅を埋め込み、配線７６を形成する。 In the next step (FIG. 12 (c)), by electrolytic plating of copper, embedded copper in the opening 75a of the dry film 75, a wiring 76. そして、次の工程（図１２（ｄ）参照）では、剥離液によりドライフィルム７５を剥離する。 Then, in the next step (see FIG. 12 (d)), peeling the dry film 75 by a stripping solution. その後、露出しているシード層をエッチングにより除去して、各配線７６間を電気的に分離する。 Thereafter, a seed layer exposed is removed by etching, providing electrical isolation between the wirings 76.
次の工程では（図１２（ｅ）参照）、配線７６に半導体チップ７７をフリップチップ接合する。 In the next step (FIG. 12 (e)), the semiconductor chip 77 is flip-chip bonded to the wiring 76. この半導体チップ７７は、厚さが例えば１５０μｍ以下（好適には５０μｍ程度）に薄型化されており、素子形成面（図１２（ｅ）では下側）の縁部に接続電極が設けられている。 The semiconductor chip 77 is, for example, 150μm or less in thickness has been thinned to a (preferably about 50μm in), and the connection electrode is provided on the edge of the element formation surface (Fig. 12 (e) in the lower side) . そして、接続電極の上（図１２（ｅ）では下側）にはバンプ（例えばＡｕスタッドバンプ）７８が形成され、このバンプ７８により配線７６と電気的に接続される。 Then, on the connection electrode (FIG. 12 (e) in the lower side) is formed bumps (e.g. Au bump) 78 is electrically connected to the wiring 76 by the bumps 78.
次の工程では（図１３（ａ）参照）、半導体チップ７７と基板７１（ソルダーレジスト層７２及び配線７６）との間にアンダーフィル７９を充填する。 In the next step of filling an underfill 79 between (see FIG. 13 (a)), the semiconductor chip 77 and the substrate 71 (the solder resist layer 72 and the wiring 76). アンダーフィル７９としては、例えばエポキシ樹脂を使用することができる。 The underfill 79 may be used, for example epoxy resin. アンダーフィル７９中には例えばシリカ等のフィラーを含有させ、アンダーフィル７９の熱膨張係数が半導体チップ７７の熱膨張係数とソルダーレジスト層７２の熱膨張係数との中間になるように調整することがこのましい。 The underfill 79 is contained a filler such as silica or the like, can be adjusted to the thermal expansion coefficient of the underfill 79 is intermediate the thermal expansion coefficient of the thermal expansion coefficient and the solder resist layer 72 of the semiconductor chip 77 preferred.
次の工程では（図１３（ｂ）参照）、基板７１の上に、半導体チップ７７を覆うようにフィルム状のエポキシ樹脂を貼り付けて、絶縁性樹脂層８０を形成する。 In the next step (see FIG. 13 (b)), on the substrate 71, paste the film-like epoxy resin so as to cover the semiconductor chip 77 to form an insulating resin layer 80. その後、絶縁性樹脂層８０を構成するエポキシ樹脂を硬化（キュア）させる。 Then, make the cured epoxy resin constituting the insulating resin layer 80 (curing). フィルム状のエポキシ樹脂を貼り付ける替りに、エポキシ樹脂を塗布して絶縁性樹脂層８０を形成してもよい。 Instead of pasting a film-like epoxy resin, by coating the epoxy resin may be formed an insulating resin layer 80. また、エポキシ樹脂に替えて、ポリイミド又はその他の絶縁性樹脂を使用してもよい。 Further, in place of the epoxy resin, it may be used polyimide or other insulating resin. このようにしてユニット６０が形成された基板７１を複数用意する。 Thus to prepare a plurality of substrates 71 which unit 60 is formed in the.
そして、次の工程では（図１３（ｃ）参照）、２つのユニット６０を、半導体チップ搭載面を向い合わせて配置し、両者の間に絶縁層６１を挟んで接合する。 Then, (see FIG. 13 (c)) In the next step, the two units 60, face-to-face the semiconductor chip mounting surface is arranged, bonded sandwiching the insulating layer 61 therebetween. 第１の実施形態では２つのユニットの接合に異方性導電体膜（図５（ａ）の絶縁層１１）を使用したが、本実施形態では、２つのユニット６０を接合する絶縁層６１として、エポキシ樹脂等の一般的な接着性樹脂フィルムを使用する。 In the first embodiment was used an anisotropic conductive film to the bonding of two units (the insulating layer 11 in FIG. 5 (a)), in the present embodiment, as the insulating layer 61 for joining the two units 60 , using a general adhesive resin film such as epoxy resin. 以下、このようにして絶縁層６１により接合された２つのユニット６０を、ペアユニットと呼ぶ。 Hereinafter, the two units 60 joined by the insulating layer 61 In this way, referred to as paired unit.
次の工程では（図１４（ａ）参照）、例えば塩化第２鉄水溶液、塩化第２銅水溶液又は過硫酸アンモニウムを使用したエッチングにより、基板７１を除去する。 In the next step (see FIG. 14 (a)), for example aqueous ferric chloride, by etching using cupric chloride aqueous solution or ammonium persulfate, removing the substrate 71. 但し、後工程で積層するペアユニットのうちの１つは、一方の面側の基板７１をレジスト膜で被覆して、エッチング後も一方の基板７１が残るようにしておく。 However, one of the pair units to be stacked in the subsequent step is to coat the substrate 71 on one side with a resist film, after etching be kept as one substrate 71 remains.
次の工程では（図１４（ｂ）参照）、一般的な接着性樹脂フィルムからなる絶縁層６１を挟んで複数のペアユニットを重ね合わせて接合する。 In the next step bonding (see FIG. 14 (b)), and an insulating layer 61 made of a general adhesive resin film superposed plurality of pairs units across. この場合、基板７１を残したユニット６０を一番下側とする。 In this case, the bottom side of the unit 60 leaving the substrate 71.
このようにして、複数のユニット６０を積層して構成され、一番下側のみに基板７１を有する積層構造体５１ａを形成した後、 次の工程では（図１５参照）、ＹＡＧレーザにより、積層構造体５１ａの上側の面から基板７１に到達する貫通孔８０ａを形成する。 In this way, formed by stacking a plurality of units 60, after forming a laminated structure 51a having a substrate 71 only in the lower most, the next step (see FIG. 15), the YAG laser, laminated forming a through hole 80a that reaches from the upper surface of the structure 51a on the substrate 71. 本実施形態では、後述するように電解めっきにより貫通孔８０ａ内に銅を充填するので、貫通孔８０ａが基板７１に到達し且つ基板７１に孔があかないようにレーザの照射条件（レーザのパワー及び照射時間等）を設定する。 In the present embodiment, since filling copper into the through hole 80a by electrolytic plating as described later, the irradiation conditions of the laser such that the through-hole 80a is not red is holes and the substrate 71 reaches the substrate 71 (the laser power and it sets the irradiation time, etc.). このときの最適なレーザ照射条件は、樹脂層８０の材質や厚さ、配線７６の厚さ及びユニット６０の積層数等により変化するので、予め実験等により求めておくことが必要である。 Optimal laser irradiation conditions at this time, material and thickness of the resin layer 80, since the changes by lamination such as the number of the thickness and unit 60 of the wiring 76, it is necessary to previously obtained by experiment or the like. なお、レーザ照射に替えて、ドリル加工により貫通孔８０ａを形成してもよい。 Instead of the laser irradiation, it may be formed through holes 80a by drilling.
次の工程では、（図１６参照）、電解めっきにより基板７１上に銅を堆積させて貫通孔８０ａ内に銅を充填し、貫通電極８１を形成する。 In the next step, (see FIG. 16), copper was filled in the through hole 80a and copper is deposited on the substrate 71 by electrolytic plating to form the through electrode 81. このとき、図１６のように、貫通電極８１の先端が上側のソルダーレジスト層７２よりも若干突出するまでめっきする。 At this time, as shown in FIG. 16, the distal end of the through electrode 81 is plated until slightly projects from the upper side of the solder resist layer 72.
次の工程では（図１７参照）、積層構造体５１ａの上側（貫通電極８１が突出した側）のソルダーレジスト層７２の上にエッチングレジスト膜８２を形成して、貫通電極８１の突出部を保護する。 In the next step to form a (see FIG. 17), the etching resist film 82 on the solder resist layer 72 of the upper laminated structure 51a (the side where the through electrode 81 is projected), protects the protruding portion of the through electrode 81 to. そして、積層構造体５１ａの下側の基板７１をエッチングにより除去する。 Then, the lower substrate 71 of the laminated structure 51a is removed by etching.
次の工程では（図１８参照）、貫通電極８１の露出している部分、すなわち貫通電極８１の上側及び下側にＮｉ及びＡｕを順次無電解めっきして、厚さが数μｍのＮｉ−Ａｕめっき層８１ａを形成する。 In the next step (FIG. 18), an exposed portion of the portion of the through electrode 81, that is, sequentially electroless plating Ni and Au on the upper and lower side of the through electrode 81, the number is thickness μm of Ni-Au to form a plating layer 81a.
次いで、この積層構造体５１ａを切断して個々の電子部品実装構造５１を分離する。 Then, separation of the individual electronic parts packaging structure 51 by cutting the layered structure 51a. これにより、図１１に示す本実施形態の電子部品実装構造５１が完成する。 Thus, the electronic parts packaging structure 51 of the present embodiment shown in FIG. 11 is completed.
前述の第１の実施形態では、図５，図６に示すように、異方性導電フィルム（絶縁層１１）を用いてユニット１０間の電気的接続を行っている。 In the first embodiment described above, as shown in FIGS. 5 and 6, it is performed the electrical connection between the unit 10 by using an anisotropic conductive film (insulating layer 11). この場合、異方性導電フィルムを挟むコンタクトビア３１同士又は端子２４同士の位置がずれてしまうと、十分な導通性能を得ることができなくなってしまう。 In this case, the position of 24 between the contact vias 31 or between terminals sandwiching an anisotropic conductive film is deviated, making it impossible to obtain a sufficient electrical conduction. これに対し、本実施形態においては、各ユニット６０を積層して積層構造体５１ａとした後に貫通孔８０ａを形成し、この貫通孔８０ａ内に銅を充填して貫通電極８１を形成する。 In contrast, in this embodiment, by stacking the units 60 a through hole 80a is formed after the laminated structure 51a, the copper is filled to form the through electrode 81 into the through hole 80a. そして、この貫通電極８１により各ユニット６０間の電気的接続を得る。 Then, obtain the electrical connection between the units 60 by the through electrode 81. 従って、本実施形態は、第１の実施形態に比べて各ユニット６０間の電気的接続が容易であり、信頼性が高い電子部品実装構造を製造することができるという効果を奏する。 Accordingly, the present embodiment differs from the first embodiment is easy electrical connection between the respective units 60, an effect that it is possible to manufacture a highly reliable electronic parts packaging structure.
なお、上述した第４の実施形態では貫通孔８０ａを形成するときに基板７１に孔が貫通しないようにしたが、基板７１を貫通するように貫通孔８０ａを形成してもよい。 Note that in the fourth embodiment described above and so the hole does not penetrate to the substrate 71 when forming the through hole 80a, it may be formed through-holes 80a so as to penetrate the substrate 71. その場合は、例えば貫通孔８０ａ内の壁面に無電解銅めっきと電解銅めっきとを順次を施して各ユニット６０間を電気的に接続すればよい。 In that case, for example, by performing sequentially the the wall surface of the through hole 80a electroless copper plating and the electrolytic copper plating between each unit 60 may be electrically connected.
また、本発明においても、第２の実施形態で説明したように、基板７１をエッチングにより除去する際に、縁部を枠状に残してもよい。 Also in the present invention, as described in the second embodiment, when removing the substrate 71 by etching, the edges may be left in a frame shape. 更に、第３の実施形態で説明したように、基板７１の裏面側（下面側）にもソルダーレジスト層を形成し、基板７１の上に半導体チップ７７を搭載した後に、裏面側のソルダーレジスト層を除去してもよい。 Further, as described in the third embodiment, also forming a solder resist layer on the back side (lower surface side) of the substrate 71, after mounting the semiconductor chip 77 on the substrate 71, the back surface side of the solder resist layer it may be removed.
図１は、本発明の第１の実施形態の電子部品実装構造を示す断面図である。 Figure 1 is a sectional view showing an electronic parts packaging structure of a first embodiment of the present invention. 図２は、本発明の第１の実施形態に係る電子部品実装構造の製造方法を示す断面図（その１）である。 Figure 2 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a first embodiment of the present invention (Part 1). 図３は、本発明の第１の実施形態に係る電子部品実装構造の製造方法を示す断面図（その２）である。 Figure 3 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a first embodiment of the present invention (Part 2). 図４は、本発明の第１の実施形態に係る電子部品実装構造の製造方法を示す断面図（その３）である。 Figure 4 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a first embodiment of the present invention (Part 3). 図５は、本発明の第１の実施形態に係る電子部品実装構造の製造方法を示す断面図（その４）である。 Figure 5 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a first embodiment of the present invention (Part 4). 図６は、本発明の第１の実施形態に係る電子部品実装構造の製造方法を示す断面図（その５）である。 Figure 6 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a first embodiment of the present invention (Part 5). 図７は、本発明の第１の実施形態に係る電子部品実装構造の製造方法の変形例を示す断面図である。 Figure 7 is a sectional view showing a modification of the method of manufacturing the electronic parts packaging structure according to a first embodiment of the present invention. 図８は、本発明の第２の実施形態の電子部品実装構造の製造方法を示す断面図である。 Figure 8 is a sectional view showing a method of manufacturing an electronic parts packaging structure of a second embodiment of the present invention. 図９は、本発明の第２の実施形態の電子部品実装構造の製造方法を示す模式平面図（全体図）である。 Figure 9 is a schematic plan view showing a method of manufacturing an electronic parts packaging structure of a second embodiment of the present invention (overall view). 図１０（ａ），（ｂ）は、本発明の第３の実施形態の電子部品実装構造の製造方法を示す断面図である。 Figure 10 (a), (b) is a sectional view showing a method of manufacturing an electronic parts packaging structure of a third embodiment of the present invention. 図１１は、本発明の第４の実施形態の電子部品実装構造を示す断面図である。 Figure 11 is a sectional view showing an electronic parts packaging structure of a fourth embodiment of the present invention. 図１２は、本発明の第４の実施形態に係る電子部品実装構造の製造方法を示す断面図（その１）である。 Figure 12 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a fourth embodiment of the present invention (Part 1). 図１３は、本発明の第４の実施形態に係る電子部品実装構造の製造方法を示す断面図（その２）である。 Figure 13 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a fourth embodiment of the present invention (Part 2). 図１４は、本発明の第４の実施形態に係る電子部品実装構造の製造方法を示す断面図（その３）である。 Figure 14 is a fourth cross-sectional views showing a method of manufacturing an electronic parts packaging structure according to a third embodiment of the present invention (Part 3). 図１５は、本発明の第４の実施形態に係る電子部品実装構造の製造方法を示す断面図（その４）である。 Figure 15 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a fourth embodiment of the present invention (Part 4). 図１６は、本発明の第４の実施形態に係る電子部品実装構造の製造方法を示す断面図（その５）である。 Figure 16 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a fourth embodiment of the present invention (Part 5). 図１７は、本発明の第４の実施形態に係る電子部品実装構造の製造方法を示す断面図（その６）である。 Figure 17 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a fourth embodiment of the present invention (Part 6). 図１８は、本発明の第４の実施形態に係る電子部品実装構造の製造方法を示す断面図（その７）である。 Figure 18 is a sectional view showing a method of manufacturing an electronic parts packaging structure according to a fourth embodiment of the present invention (Part 7).
１，５１…電子部品実装構造（半導体装置）、 1 and 51 ... electronic parts packaging structure (semiconductor device),
１０，６０…ユニット、 10, 60 ... unit,
１１，６１…絶縁層、 11, 61 ... insulating layer,
２１，７１…基板、 21 and 71 ... substrate,
２１ａ…枠状の金属膜、 21a ... frame-shaped metal film,
２２，７２…ソルダーレジスト層、 22, 72 ... solder resist layer,
２３…はんだ層、 23 ... solder layer,
２４…端子、 24 ... terminal,
２５，７５…ドライフィルム、 25, 75 ... dry film,
２６，７６…配線、 26, 76 ... wiring,
２７，７７…半導体チップ、 27,77 ... semiconductor chip,
２８，７８…バンプ、 28, 78 ... bump,
２９，７９…アンダーフィル（保護膜）、 29,79 ... underfill (protective film),
３０，８０…絶縁性樹脂層、 30, 80 ... insulating resin layer,
３１…コンタクトビア、 31 ... contact vias,
８１…貫通電極、 81 ... through electrode,
８３…エッチングレジスト膜。 83 ... etching resist film.
複数のシート状のユニットが厚さ方向に積層されて構成された電子部品実装構造において、前記ユニットが、第１の絶縁層と、 The electronic component mounting structure constituted by a plurality of sheet-like unit is stacked in a thickness direction, wherein the unit includes a first insulating layer,
前記第１の絶縁層の一方の面上に形成された配線と、 A wiring formed on one surface of the first insulating layer,
前記配線に接続された電子部品と、 An electronic component connected to the wiring,
前記第１の絶縁層の前記一方の面側に形成されて前記電子部品を覆う第２の絶縁層と、 A second insulating layer covering the electronic component are formed on the one surface of the first insulating layer,
前記配線と他のユニットの配線とを電気的に接続する接続部とを有し、 And a connecting portion for electrically connecting the wiring and other units of lines,
厚さ方向に隣り合うユニットにおいて、前記第１の絶縁層、前記電子部品、前記配線及び前記第２の絶縁層の配置が対称であり、 かつ、 In the unit adjacent in the thickness direction, the first insulating layer, the electronic component, the arrangement of the wiring and the second insulating layer are symmetrical, and,
前記接続部が、前記第１の絶縁層を貫通して形成されて前記配線の一方の面に接合された端子と、前記第２の絶縁層を貫通して形成されて前記配線の他方の面に接合されたコンタクトビアとにより構成され、 The connecting portion, the other surface of the first terminal joined to one surface of the wiring formed by the insulating layer through the formed through the second insulating layer wiring is constituted by a contact via bonded to,
前記端子が前記第１の絶縁層の表面から突出しており、 The terminal protrudes from the surface of the first insulating layer,
前記コンタクトビアの頂部が前記第２の絶縁層の表面から突出しており、 Top of the contact via protrudes from the surface of the second insulating layer,
前記各ユニットは前記端子同士又は前記コンタクトビア同士により接続されていることを特徴とする電子部品実装構造。 An electronic parts packaging structure wherein each unit, characterized in that are connected by each other the terminals or between the contact via.
前記第１の絶縁層が、ソルダーレジストからなることを特徴とする請求項１に記載の電子部品実装構造。 Electronic component mounting structure according to claim 1, wherein the first insulating layer, characterized in that it consists of a solder resist.
前記各ユニットの前記端子同士又は前記コンタクトビア同士は、異方性導電フィルムを介して接続されていることを特徴とする請求項１に記載の電子部品実装構造。 Wherein the terminals or between the contact via of the respective units, the electronic component mounting structure according to claim 1, characterized in that it is connected via an anisotropic conductive film.
前記電子部品が半導体チップであることを特徴とする請求項１に記載の電子部品実装構造。 Electronic parts packaging structure according to claim 1, wherein the electronic component is a semiconductor chip.
前記半導体チップが前記配線とフリップチップ接合していることを特徴とする請求項４に記載の電子部品実装構造。 Electronic component mounting structure according to claim 4, wherein the semiconductor chip is the wiring and the flip-chip bonding.
基板上に絶縁性樹脂からなる第１の絶縁層を形成する第１工程と、 A first step of forming a first insulating layer made of an insulating resin on a substrate,
前記第１の絶縁層をパターニングして開口部を形成する第２工程と、 A second step of forming an opening by patterning the first insulating layer,
前記開口部の内側に露出した前記基板をエッチングして窪みを形成する第３工程と、 A third step of forming a recess the substrate exposed to the inside of the opening is etched,
前記開口部の内側に金属を充填して端子を形成する第４工程と、 A fourth step of forming a terminal by filling a metal on the inside of the opening,
前記第１の絶縁層の上に、前記端子と接続する配線を形成する第５工程と、 On the first insulating layer, a fifth step of forming a wiring connected to the terminal,
前記配線の上に電子部品を接合する第６工程と、 A sixth step of bonding the electronic component on the wiring,
前記第１の絶縁層の上に前記電子部品を覆う第２の絶縁層を形成する第７工程と、 A seventh step of forming a second insulating layer covering the electronic component on the first insulating layer,
前記第２の絶縁層の上面から前記配線に到達する孔を形成する第８工程と、 An eighth step of forming a hole reaching the wiring from the upper surface of the second insulating layer,
前記孔内に金属を充填してコンタクトビアを形成する第９工程と、 A ninth step of forming a contact via by filling a metal into said hole,
前記基板を除去する第１０工程とを遂行することにより、 By performing a tenth step of removing the substrate,
前記第１の絶縁層と、前記第１の絶縁層の一方の面上に形成された前記配線と、前記配線に接続された前記電子部品と、前記第１の絶縁層の一方の面側に形成されて前記電子部品を覆う前記第２の絶縁層と、前記配線と電気的に接続した前記端子及び前記コンタクトビアからなる接続部とにより構成されるシート状のユニットを複数用意し、 Said first insulating layer, while the wiring formed on the surface of the first insulating layer, and the electronic components connected to the wiring, on one surface side of the first insulating layer said second insulating layer is formed to cover the electronic component, and preparing a plurality of sheet-shaped unit formed by a connecting portion made from said terminal and said contact vias and the wiring electrically connected,
それらのユニットを、厚さ方向に隣り合うユニットの向きを交互に逆に配置して相互に積層して前記端子同士又は前記コンタクト同士を接合し、前記接続部を介して各ユニットの電子部品を相互に電気的に接続することを特徴とする電子部品実装構造の製造方法。 Those units, arranged alternately inverted orientation of the unit adjacent in the thickness direction by stacking with each other and bonding said terminals to each other or the contact with each other, the electronic components of each unit via the connecting portions method of manufacturing an electronic parts packaging structure, characterized by electrically connected to each other.
前記第９工程の後に、２つのユニットを前記電子部品が搭載された面を向かい合わせて接合し、その後、前記第１０工程を実施して前記基板を剥離することを特徴とする請求項６に記載の電子部品実装構造の製造方法。 After the ninth step, the two units are joined face to face the electronic components are mounted face, then to claim 6, characterized in that peeling the substrate by performing the tenth step method of manufacturing an electronic parts packaging structure according.
前記第１０工程において、前記基板のうち縁部の部分を枠状に残し、その後各ユニットを接合した後に前記枠状の部分を切断除去することを特徴とする請求項６に記載の電子部品実装構造の製造方法。 In the tenth step, leaving a portion of the edge like a frame of said substrate, then the electronic component mounting according to claim 6, characterized in that the cutting and removing the frame-like portion after joining the units method of manufacturing the structure.
前記第１工程において、前記基板の下面に第３の絶縁層を形成し、 In the first step, the third insulating layer is formed on the lower surface of the substrate,
前記第９工程の終了から第１０工程の開始までの間に、前記第３の絶縁層を除去することを特徴とする請求項６に記載の電子部品実装構造の製造方法。 Wherein between the end of the ninth step and the start of the tenth step, the method of manufacturing the electronic parts packaging structure according to claim 6, characterized in that the removal of the third insulating layer.
JP2005373859A 2005-07-21 2005-12-27 Electronic parts packaging structure and a method of manufacturing the same Active JP4551321B2 (en)
JP2005211938 2005-07-21
JP2005373859A JP4551321B2 (en) 2005-07-21 2005-12-27 Electronic parts packaging structure and a method of manufacturing the same
US11/486,051 US7843059B2 (en) 2005-07-21 2006-07-14 Electronic parts packaging structure
US12/926,072 US8402644B2 (en) 2005-07-21 2010-10-25 Method of manufacturing an electronic parts packaging structure
JP2007053327A JP2007053327A (en) 2007-03-01
JP4551321B2 true JP4551321B2 (en) 2010-09-29
ID=37678322
JP2005373859A Active JP4551321B2 (en) 2005-07-21 2005-12-27 Electronic parts packaging structure and a method of manufacturing the same
US (2) US7843059B2 (en)
JP (1) JP4551321B2 (en)
JP4783812B2 (en) * 2008-05-12 2011-09-28 新光電気工業株式会社 A method for manufacturing a wiring board
JP4696140B2 (en) * 2008-05-12 2011-06-08 新光電気工業株式会社 A method for manufacturing a wiring board
JP5006252B2 (en) * 2008-05-12 2012-08-22 新光電気工業株式会社 Production method and a wiring board of the wiring board
JP5124389B2 (en) * 2008-08-27 2013-01-23 新光電気工業株式会社 Wiring board
KR101029617B1 (en) * 2009-07-01 2011-04-15 주식회사 하이닉스반도체 Rfid device having multichip structure
TWI474410B (en) * 2011-06-10 2015-02-21 King Yuan Electronics Co Ltd An automatically packing device for chips
JP5623367B2 (en) * 2011-10-21 2014-11-12 三菱電機株式会社 Semiconductor device and a semiconductor device module
JP5399539B2 (en) * 2012-07-11 2014-01-29 新光電気工業株式会社 Wiring board and manufacturing method thereof
TWI517269B (en) * 2013-09-27 2016-01-11 Siliconware Prec Ind Co Ltd Package on package structure and manufacturing method thereof
JP2016115868A (en) * 2014-12-17 2016-06-23 富士電機株式会社 Method of manufacturing semiconductor device
JP6476494B2 (en) * 2015-08-28 2019-03-06 Ｓｈマテリアル株式会社 Lead frame and a semiconductor device, and methods for their preparation
JP2003289128A (en) * 2002-01-23 2003-10-10 Matsushita Electric Ind Co Ltd Circuit component built-in module and method for manufacturing the same
2005-12-27 JP JP2005373859A patent/JP4551321B2/en active Active
2006-07-14 US US11/486,051 patent/US7843059B2/en active Active
2010-10-25 US US12/926,072 patent/US8402644B2/en active Active
US7843059B2 (en) 2010-11-30
US8402644B2 (en) 2013-03-26
JP2007053327A (en) 2007-03-01
US20110039370A1 (en) 2011-02-17
US20070018313A1 (en) 2007-01-25
CN101395978B (en) 2013-02-06 Circuit wiring board incorporating heat resistant substrate