Patent US8066190 - Transaction card - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsThe present invention relates to a process for producing a transparent or translucent transaction card having multiple features. An optically recognizable compound may be associated with a portion of the card for blocking infrared radiation and may comprise an infrared ink having nanocrystalline indium...http://www.google.com/patents/US8066190?utm_source=gb-gplus-sharePatent US8066190 - Transaction cardAdvanced Patent SearchTry the new Google Patents, with machine-classified Google Scholar results, and Japanese and South Korean patents.Publication numberUS8066190 B2Publication typeGrantApplication numberUS 12/124,937Publication dateNov 29, 2011Filing dateMay 21, 2008Priority dateSep 7, 1999Fee statusPaidAlso published asEP2291793A1, EP2291793A4, US8186598, US20080251581, US20120006902, WO2009142998A1Publication number12124937, 124937, US 8066190 B2, US 8066190B2, US-B2-8066190, US8066190 B2, US8066190B2InventorsWilliam J. Faenza, Jr.Original AssigneeAmerican Express Travel Related Services Company, Inc.Export CitationBiBTeX, EndNote, RefManPatent Citations (187), Non-Patent Citations (43), Referenced by (7), Classifications (12), Legal Events (4) External Links: USPTO, USPTO Assignment, EspacenetTransaction card
US 8066190 B2Abstract
The present invention relates to a process for producing a transparent or translucent transaction card having multiple features. An optically recognizable compound may be associated with a portion of the card for blocking infrared radiation and may comprise an infrared ink having nanocrystalline indium tin oxide particles. Moreover, a portion of the transaction card may include a second optically recognizable compound disposed thereon. The second optically recognizable compound may comprise an infrared phthalocyanine dye, an infrared phosphor, and a quantum dot energy transfer compound. The infrared ink may be detected by a sensor found in an ATM or card assembly line.
1. A transaction card having a portion comprising:
a layer that is at least one of translucent and transparent;
a first infrared blocking compound associated with said layer;
a second infrared blocking compound associated with said layer,
wherein said first infrared blocking compound further comprises nanocrystalline indium tin oxide particles,
wherein said second infrared blocking compound comprises a quantum dot compound.
2. The transaction card of claim 1, wherein said nanocrystalline indium tin oxide is incorporated into an ink.
3. The transaction card of claim 1, wherein said infrared blocking compound blocks infrared radiation above about 1200 nm.
4. The transaction card of claim 1, wherein said infrared blocking compound blocks infrared radiation from between about 1300 nm to about 2500 nm.
5. The transaction card of claim 1, wherein said first infrared blocking compound is incorporated into said layer.
6. The transaction card of claim 1, wherein said nanocrystalline indium tin oxide particles are dispersed in a solvent.
7. The transaction card of claim 6, wherein said solvent is selected from the group consisting of cyclohexane, n-propyl alcohol, free flow alkyd, and a mixture of VMCA resin in n-propyl acetate.
8. The transaction card of claim 1, wherein said nanocrystalline indium tin oxide particles are incorporated into a plastic layer.
9. The transaction card of claim 1, wherein an ink comprises said quantum dot compound.
10. The transaction card of claim 9, wherein said ink is selected from the group consisting of Au, Ag, and Indium Oxide.
11. The transaction card of claim 1, further comprising a third infrared blocking compound comprises an infrared blocking film comprising a plurality of layers disposed on a substrate, said plurality of layers comprising at least two layers having different refractive indices.
12. The transaction card of claim 1, wherein a third infrared blocking compound comprises at least one of an isotropic dielectric multilayer film and a birefringement dielectric multilayer film.
13. The transaction card of claim 1, wherein said layer has a first surface and a second surface, wherein said first infrared blocking material is a first ink that is printed onto said first surface and said second infrared blocking compound is a second ink that is printed onto said second surface.
14. The transaction card of claim 1, wherein said layer has a first surface and a second surface, wherein said first infrared blocking compound is disposed on said first surface and said second infrared blocking compound is disposed on said second surface.
15. The transaction card of claim 1, wherein said layer has a first surface and a second surface, wherein said first infrared blocking compound is disposed on at least one of said first surface and said second infrared blocking compound is disposed on said second surface.
16. The transaction card of claim 1, wherein said first infrared blocking compound substantially covers at least one of said first surface and said second surface of said layer.
17. The transaction card of claim 1, wherein said first infrared blocking compound is a first ink that is printed onto said layer and said second infrared blocking compound is a second ink that is printed onto said layer.
18. The transaction card of claim 1, wherein said layer is comprised of at least one of glass and a polymeric material.
19. A method of making an article, comprising the steps of:
providing a first layer that is at least one of translucent and transparent;
associating a second infrared blocking compound to said first layer; and,
associating a first infrared blocking compound to said layer, wherein said first infrared blocking compound further comprises nanocrystalline indium tin oxide particles
20. The method of claim 19, wherein said associating further comprises laminating said first layer to a second layer comprising a second infrared blocking compound.
21. The method of claim 19, wherein said second infrared blocking compound further comprises an infrared absorbing ink.
22. The method of claim 19, wherein a third infrared blocking compound further comprises an infrared blocking film comprising a plurality of layers disposed on a substrate, said plurality of layers comprising at least two layers having different refractive indices.
23. An article having a portion comprising:
at least one of a translucent and transparent surface;
a first infrared blocking compound capable of blocking infrared light in a first wavelength range, said first infrared blocking compound associated with at least one of said surface and a second infrared blocking compound;
said second infrared blocking compound capable of blocking infrared light in a second wavelength range, said second infrared blocking compound associated with at least one of said surface and said first infrared blocking compound;
wherein said first infrared blocking compound comprises nanocrystalline indium tin oxide particles,
24. The article of claim 23, wherein said first wavelength range does not overlap with said second wavelength range.
25. The article of claim 23, wherein said first wavelength range is above about 800 nm and below about 1000 nm.
26. The article of claim 23, wherein said first wavelength range is above about 1000 nm.
The present application is a continuation-in-part Application of U.S. patent application Ser. No. 11/879,468, filed Jul. 17, 2007. The '468 application is a continuation-in-part application of U.S. patent application Ser. No. 10/394,914, filed Mar. 21, 2003. The '914 application is a continuation application of U.S. patent application Ser. No. 10/092,681, filed Mar. 7, 2002 (issued as U.S. Pat. No. 6,764,014 on Jul. 20, 2004). The '681 application is a continuation-in-part application of U.S. patent application Ser. No. 10/062,106, filed Jan. 31, 2002 (issued as U.S. Pat. No. 6,749,123 on Jun. 15, 2004). The '106 application is a continuation-in-part application of U.S. patent application Ser. No. 09/653,837, filed Sep. 1, 2000 (issued as U.S. Pat. No. 6,581,839 on Jun. 24, 2003) and further claims the benefit of U.S. Provisional Application No. 60/153,112, filed Sep. 7, 1999; U.S. Provisional Application No. 60/160,519, filed Oct. 20, 1999; U.S. Provisional Application No. 60/167,405, filed Nov. 24, 1999; U.S. Provisional Patent Application No. 60/171,689, filed Dec. 21, 1999 and U.S. patent application Ser. No. 09/652,899, entitled “Methods And Apparatus For Conducting Electronic Transactions” filed Aug. 31, 2000 (issued as U.S. Pat. No. 7,343,351 on Mar. 11, 2008). All of these applications are incorporated herein by reference.
The present invention relates generally to a transaction card, and more particularly, to the fabrication and use of an infrared blocking transparent or translucent transaction card.
The proliferation of transaction cards, which allow the cardholder to pay with credit rather than cash, started in the United States in the early 1950s. Initial transaction cards were typically restricted to select restaurants and hotels and were often limited to an exclusive class of individuals. Since the introduction of plastic credit cards, the use of transaction cards have rapidly proliferated from the United States, to Europe, and then to the rest of the world. Transaction cards are not only information carriers, but also typically allow a consumer to pay for goods and services without the need to constantly possess cash. If a consumer needs cash, transaction cards also may allow access to funds through an automatic teller machine (ATM). Transaction cards also reduce the exposure to the risk of cash loss through theft and reduce the need for currency exchanges when traveling to various foreign countries. Due to the advantages of transaction cards, hundreds of millions of cards are now produced and issued annually, thereby resulting in a desire for companies to differentiate their cards from competitor's cards.
Initially, the transaction cards often included the issuer's name, the cardholder's name, the card number, and the expiration date embossed onto the card. The cards also usually included a signature field on the back of the card for the cardholder to provide a signature to protect against forgery and tampering. Thus, the initial cards merely served as devices to provide data to merchants and the only security associated with the card was the comparison of the cardholder's signature on the card to the cardholder's signature on a receipt, along with the embossed cardholder name on the card. However, many merchants often forget to verify the signature on the receipt with the signature on the card.
Due to the popularity of transaction cards, numerous companies, banks; airlines, trade groups, sporting teams, clubs and other organizations have developed their own transaction cards. As such, many companies continually attempt to differentiate their transaction cards and increase market share not only by offering more attractive financing rates and low initiation fees, but also by offering unique, aesthetically pleasing features on the transaction cards. As such, many transaction cards included not only demographic and account information, but the transaction cards also include graphic images, designs, photographs and security features. A recent security feature is the incorporation of a diffraction grating, or holographic image, into the transaction card which appears to be three dimensional and which substantially restricts the ability to fraudulently copy or reproduce transaction cards because of the need for extremely complex systems and apparatus for producing holograms. A hologram is produced by interfering two or more beams of light, namely an object beam and reference beam, onto a photoemulsion to thereby record the interference pattern produced by the interfering beams of light. The object beam is a coherent beam reflected from, or transmitted through, the object to be recorded, such as a company logo, globe, character or animal. The reference beam is usually a coherent, collimated light beam with a spherical wave front. After recording the interference pattern, a similar wavelength reference beam is used to produce a holographic image by reconstructing the image from the interference pattern.
However, in typical situations, a similar laser beam is not available to reconstruct the image from the interference pattern on the card. As such, the hologram should be able to be viewed with ordinary, white light. Thus, when a hologram is recorded onto a transaction card, the image to be recorded is placed near the surface of the substrate to allow the resulting hologram to be visible in ordinary, white light. These holograms are known as reflective surface holograms or rainbow holograms. A reflective hologram may be mass-produced on metallic foil and subsequently stamped onto transaction cards. Moreover, the incorporation of holograms onto transaction cards provides a more reliable method of determining the authenticity of the transaction card in ordinary white light, namely by observing if the hologram has the illusion of depth and changing colors.
Due to the susceptibility of the magnetic stripe to tampering, the lack of confidentiality of the information within the magnetic stripe and the problems associated with the transmission of data to a host computer, integrated circuits were developed which may be incorporated into transaction cards. These integrated circuit (IC) cards, known as smart cards, proved to be very reliable in a variety of industries due to their advanced security and flexibility for future applications.
As magnetic stripe cards and smart cards developed, the market demanded international standards for the cards. The card's physical dimensions, features and embossing area were standardized under the International Standards Organization (“ISO”), ISO 7810 and ISO 7811. The issuer's identification, the location of particular compounds, coding requirements, and recording techniques were standardized in ISO 7812 and ISO 7813, while chip card standards were established in ISO 7813. For example, ISO 7811 defines the standards for the magnetic stripe which is a 0.5 inch stripe located either in the front or rear surface of the card which is divided into three longitudinal parallel tracks. The first and second tracks hold read-only information with room for 79 alpha numeric characters and 40 numeric characters, respectively. The third track is reserved for financial transactions and includes enciphered versions of the user's personal identification number, country code, currency units, amount authorized per cycle, subsidiary accounts, and restrictions. More information regarding the features and specifications of transaction cards may be found in, for example, Smart Cards by Jose Luis Zoreda and Jose Manuel Oton, 1994; Smart Card Handbook by W. Ranki and W. Effing, 1997, and the various ISO standards for transaction cards available from ANSI (American National Standards Institute), 11 West 42nd Street, New York, N.Y. 10036, the entire contents of all of these publications are herein incorporated by reference.
The incorporation of machine-readable components onto transactions cards encouraged the proliferation of devices to simplify transactions by automatically reading from and/or writing onto transaction cards. Such devices include, for example, bar code scanners, magnetic stripe readers, point of sale terminals (POS), automated teller machines (ATM) and card-key devices. With respect to ATMs, the total number of ATM devices shipped in 1999 is 179,274 (based on Nilson Reports data) including the ATMs shipped by the top ATM manufacturers, namely NCR (138-18 231 st Street, Laurelton, N.Y. 11413), Diebold (5995 Mayfair, North Canton, Ohio 44720-8077), Fujitsu (11085 N. Torrey Pines Road, La Jolla, Calif. 92037), Omron (Japan), OKI (Japan) and Triton.
Many of the card acceptance devices require that the transaction card be inserted into the device such that the device may appropriately align its reading head with the relevant component of the transaction card. Particularly, many ATMs require that a transaction card be substantially inserted into a slot in the ATM. After insertion of the card into the slot, the ATM may have an additional mechanical device for further retracting the transaction card into the ATM slot. To activate the ATM, the ATM typically includes a sensor, such as a phototransistor and a light emitting diode (LED), which emits light onto a card surface and the phototransistor receives light from the LED. A card blocks the infrared radiation from the phototransistor, therefore indicating that a card has been detected. A typical LED in an ATM is an IRED (infrared emitting diode) source having a wavelength in the range of about 820-920 nm or 900-1000 nm (see FIG. 5), which is not present in ambient light at the levels needed by a phototransistor sensor. The spectral sensitivity curve of the typical phototransistor is in the range of about 400 nm-1100 nm (see FIG. 6). However, the visible spectrum is about 400 nm-700 nm, and the spectral sensitivity of the phototransistor is about 60% at 950 nm and 90% at 840 nm. Thus, visible light is not part of the analog-to-digital algorithm. Moreover, ISO 7810, clause 8.10 requires that all machine readable cards have an optical transmission density from 450 nm-950 nm, greater than 1.3 (less than 5% transmission) and from 950 nm-1000 nm, greater than 1.1 (less than 7.9% transmission).
Moreover, newer LEDs in ATMs, vending machines, and other machines that utilize card technology may utilize an IRED source having a wavelength much higher than described above. Specifically, it is known that some LEDs have IRED sources having a wavelength up to about 1550 nm, or higher. Heretofore, solutions for blocking or absorbing IRED sources will not block wavelengths higher than about 1000 to 1100 nm.
As previously mentioned, transaction cards and readers typically follow various ISO standards which specifically set forth the location of card data and compounds. However, because numerous companies produce different versions of ATMs, the location of the sensor within the ATM is not subject to standardization requirements. In the past, the varying locations of the sensor within the ATM did not affect the ability of the ATM to sense the transaction card because the transaction card included a substantially opaque surface, such that any portion of the opaque transaction card may interrupt the IRED emission and activate the insert phototransistor. However, more recently, to provide a unique image, and to meet consumer demand, companies have attempted to develop transparent or translucent transaction cards. The use of a transparent card would often not activate the insert phototransistor because the IRED emission would not sufficiently reflect off of a transparent surface, so the radiation would simply travel through the card and become detected by the phototransistor. The machine, therefore, could not detect the presence of the card, and often jammed the equipment.
In an attempt to solve this problem, companies have printed opaque areas onto transparent cards in an effort to provide an opaque area to activate the input sensors on ATMs. However, due to the aforementioned variations in the location of the sensor in many ATMs, the use of limited opaque areas on a transparent card did not allow the card to activate the sensor in a sufficient number of ATMs. Alternatively, companies attempted to incorporate a lens onto a transaction card in an effort to redirect the LED light. However, during the card manufacture process, which often involves substantial pressure and heat, the lensing surface would be disrupted or destroyed. As such, a need exists for a transparent or translucent transaction card which is capable of activating an input sensor, wherein the input sensor may interface the card in a variety of locations. Moreover, a need exists for a transparent or translucent transaction card which is capable of activating an input sensor, wherein the input sensor may utilized an LED having an IRED source of relatively high wavelengths, such as around 1550 nm or higher.
Furthermore, during the card fabrication process, the cards are typically detected on the assembly line in order to accurately count the number of cards produced during a predetermined time interval. To count the cards, typical card fabrication assembly lines include counters with LED sensors, similar to the ATM sensors, which count the cards based upon the reflection of the LED light beam off of the opaque card surface. The production of transparent transaction cards suffers from similar limitations as ATM devices in that the LED beam does not reflect or is not sufficiently absorbed from a transparent surface. Thus, a transparent card is needed that may be produced on existing assembly lines. Similar problems exist when cards are punched to final dimensions.
The present invention relates to a process for producing a transparent or translucent transaction card having any one or more features, such as a holographic foil, integrated circuit chip, silver magnetic stripe with text on the magnetic stripe, opacity gradient, an infrared blocking ink or film contained within the construction of the card, a translucent signature field such that the signature on back of the card is visible from the front of the card and an “active thru” date on the front of the card. The card is infrared blocking due to an invisible or transparent infrared ink or film which is distributed over the card's surface, thereby allowing the card to block (absorb, refract, diffuse and/or reflect) infrared light and transmit all other light. Particularly, when the transaction card is inserted into an ATM device, the light beam from the IRED is blocked by the infrared ink or film, thereby deactivating the phototransistor. Moreover, during the manufacturer of transaction cards, the infrared blocking card allows an IRED light beam from a personalization device, inspection unit or counter device to count the number of transaction cards produced in an assembly line.
The present invention further relates to an ink or film contained within the construction of a transaction card having a material that blocks an LED IRED source having relatively high wavelengths. More specifically, the material blocks an LED IRED source having a wavelength of about 1400 nm and above. The material may block an LED IRED source having a wavelength of about 1550 nm and above.
Still further, the present invention relates to an ink or film contained within the construction of a transaction card having a material that blocks an LED IRED source having both relatively low and relatively high wavelengths. More specifically, the material may block an LED IRED source having a wavelength range between about 770 nm and above. More specifically, the material may block an LED IRED source having a wavelength range between about 820 nm and about 2000 nm. The material may block an LED IRED source having a wavelength range between about 900 nm and about 1600 nm.
A more complete understanding of the present invention may be derived by referring to the detailed description and claims when considered in connection with the following illustrative figures, which may not be to scale. In the following figures, like reference numbers or steps refer to similar compounds throughout the figures.
FIGS. 7A-7J show various embodiments of card layers in accordance with exemplary embodiments of the present invention;
FIGS. 17A-17J show exemplary test results for various card embodiments in a graph of percent transmission v. wavelength (nm) in accordance with an exemplary embodiment of the present invention.
The detailed description of exemplary embodiments herein makes reference to the accompanying drawings and pictures, which show exemplary embodiments by way of illustration and its best mode. While these exemplary embodiments are described in sufficient detail to enable those skilled in the art to practice the invention, it should be understood that other embodiments may be realized and that logical and mechanical changes may be made without departing from the spirit and scope of the invention. Thus, the detailed description herein is presented for purposes of illustration only and not of limitation. For example, the steps recited in any of the method or process descriptions may be executed in any order and are not limited to the order presented. Moreover, any of the functions or steps may be outsourced to or performed by one or more third parties. Furthermore, any reference to singular includes plural embodiments, and any reference to more than one component may include a singular embodiment.
In general, the present invention allows for the identification and detection of various articles, wherein the articles include materials having optically and machine recognizable compounds. The articles include, for example, transaction cards, documents, papers and/or the like. The materials include, for example, coatings, films, threads, plastics, inks, fibers, paper, planchettes, and/or the like.
In an exemplary embodiment, the optically and machine recognizable compounds are infrared blocking compounds containing infrared blocking (absorbing, refracting, diffusing, reflecting or otherwise blocking) components. Blocking, as used herein includes absorbing, refracting, diffusing, reflecting or otherwise altering the path. The infrared blocking compounds may be invisible, visible, or colored to produce a desired effect and/or they may contain other detectable compounds, such as, for example, UV-Fluorescent or IR-Fluorescent features. The infrared blocking compounds may have good stability, resistance properties, durability and other physical properties, such as good appearance, flexibility, hardness, solvent resistance, water resistance, corrosion resistance and exterior stability. Moreover, the use of such compounds typically does not interfere with UV compounds that may be present in many substrates. One skilled in the art will appreciate that an infrared blocking compounds may be any chemical, solution, dye, ink, substrate, material and/or the like which is recognizable by an optical sensor. In various embodiments, an infrared blocking ink includes an infrared ink which blocks, absorbs and/or reflects most infrared light, but transmits most other wavelengths of light. In various embodiments, an infrared blocking ink includes an infrared ink which blocks, absorbs and/or reflects most infrared light, but transmits most other wavelengths of light. In various embodiments, various infrared blocking compounds are used in combination to achieve enhanced blocking capability. Enhanced blocking capability may be the ability to block a wide range of wavelengths. Enhanced blocking capability may be the capability to block a range of wavelengths with various mechanisms.
In an exemplary embodiment, the infrared blocking compound is incorporated into a material in the form of a film, plastic, fiber, ink, concentrate, thermoplastic or thermoset matrix, thread, planchette, and/or other medium which contains in the range of about 0.001 to 40.0 wt. (%) of a compound derived from organic or inorganic materials. The infrared ink may be applied to card 5 (see FIG. 1) by, for example, a screen printing process or any other printing or coating means such as lithography, gravure, flexo, calender coating, curtain coating, roller coating and/or the like. An exemplary screen printing process utilizes a screen press equipped with drying equipment (UV curable or convection heat) and a screen with a specific mesh size of about 80 lines/cm. The IR ink is printed across any portion of the entire card surface of plastic using a silk screen press, as described below.
Because the relative eye sensitivity of an ordinary observer for a specified level of illumination is between around 400-770 nm, infrared ink at over 770 nm is invisible to the human eye in normal white light. As such, the invisible infrared material will not substantially obscure the transparent surface of card 5. Additionally, the exemplary ink withstands card production temperatures of about 200 F to 400 F degrees and includes a “light fastness period” (which is the resistance of the ink to fade or degrade in the presence of any light, and specifically, UV light) of about at least three years under normal credit card usage conditions. Moreover, the exemplary ink blocks, absorbs or reflects the spectral output of IRED's, such as, for example, the Sankyo Seiki LED's, which is about 800-1000 nm. The exemplary ink also limits the light reaching the phototransistors, so the presence of a clear card having the ink is detected in a transaction machine, such as, for example, a card grabbing-type ATM machine.
Exemplary compositions of the infrared blocking compounds of the present invention comprise a mixture of a wide variety of compounds. The active compounds are derived of inorganic, organometallic, or organic layered materials or rare earth compounds, most commonly rare earth oxides, oxysulfides or oxyhalides. The compounds are relatively inert, so the effects on the performance properties of the final product are minimized. The infrared blocking compound comprises either a dye, layered material, pigment and/or encapsulated pigment that is dispersed in a particular medium which may be incorporated into a wide variety of end-usable products. The particle size of the infrared blocking compound allows the materials (plastic, thread, ink, etc.) to optimally be dispersed or dissolved and uniformly exist within the articles which it is incorporated.
Conventionally known infrared blocking materials comprising layered dielectric and metallic materials or doped rare-earth materials may be effectively used as pigments for compounds in accordance with exemplary embodiments of the present invention. In this context, the pigments or dyes absorb specific wavelengths of energy and may change one wavelength of energy to another. The energy conversions or absorptions may be above or below any stimulation within the electromagnetic spectrum. The infrared blocking compounds may absorb specific wavelengths of light or change from one color to another or the compounds may change from invisible to visible and/or the like. The infrared blocking compounds of the present invention are thus incorporated into a system which reversibly changes one wavelength of energy to another, hence causing a “fingerprint”-type of detectable feature within the articles. Various glues and/or binders may also have the ability to block infrared radiation, among other types of radiation. However, the infrared blocking ability of a glue or binder is typically in a wavelength range higher than 9000 nm. Many of the infrared blocking compounds discussed herein below have the ability to block infrared light in the range of about 800 nm to 6000 nm and higher. Infrared blocking materials that block from about 800 nm to 2000 nm and those that block from about 1000 nm to 1600 nm are especially useful in various applications.
Moreover, the prepared films or materials may be mixed with a binder to form infrared compounds for use in threads, fibers, coatings, and the like. Binders that may be incorporated in the present invention include conventional additives such as waxes, thermoplastic resins, thermoset resins, rubbers, natural resins or synthetic resins. Such examples of such binders are, polypropylene, nylon, polyester, ethylene-vinyl acetate copolymer, polyvinyl acetate, polyethylene, chlorinated rubber, acrylic, epoxy, butadiene-nitrile, shellac, zein, cellulose, polyurethane, polyvinylbutyrate, vinyl chloride, silicone, polyvinyl alcohol, polyvinyl methyl ether, nitrocellulose, polyamide, bismaleimide, polyimide, epoxy-polyester hybrid and/or the like. Films that may be used include polyester, polyvinylchloride, polypropylene, polyethylene, acrylic, polycarbonate and/or the like. As discussed below, any film may be laminated or adhered to common card articles using heat, adhesives, or a combination of both.
If the content of the compound is too low, adequate blocking may not be achieved and the phototransistor may not send the proper signal to the capture device, which will mean that the card will not be detected. Therefore, the infrared compounds are usually present in the composition at a total amount from about 1 ppm to 80.0 wt. (%), and possibly from about 0.25%-25.0% by weight. Moreover, the present invention contemplates that other materials such as, for example, UV absorbers, reflectors, antioxidants, and/or optical brighteners, may be added in order to achieve better resistance properties, aesthetics, or longevity of the materials.
Particularly, other materials may be added to allow for color shifts from one color to another color after stimulation. Commonly employed materials such as dyes, pigments, fluorescent dyes, luminous pigments, and/or the like, may be used to promote reversible color changes from one color state to another color state. Such materials may be incorporated directly with the infrared compounds during initial processing or may be added after the infrared compounds have been processed. The use of materials such as solvents, water, glycols, and/or the like may be added to adjust rheological properties of the material. Also, the use of surfactants, defoamers, release agents, adhesion promoters, leveling agents, and/or the like may be added to the formulations for improved processing properties. Optical brightening materials may also be added to ensure whiteness in a colorless state and to maintain a low level of contrast between many substrates where infrared compounds are located.
In an embodiment of the present invention, an IR-blocking and/or absorbing ink may be printed onto one or more layers of a financial transaction card. The ink may comprise a combination of a pure, recrystallized infrared phthalocyanine dye, an inorganic infrared phosphor, and a quantum dot energy transfer-based compounds. These materials may be combined together and printed on one or more layers of a transaction card. These materials may also be combined with various types of plastic and incorporated into a transaction card. Plastic containing these materials may be formed into layers. The combination of materials, coupled with separation of layers using printing methods, allows infrared radiation absorption to occur, and energy transfer to occur between the infrared phthalocyanine dye, the phosphor, and the quantum dot compound. The absorption of infrared radiation, reflection and/or emission is typically transferred from one molecule to another, thereby resulting in energy transference from one molecule to another, resulting in specific infrared radiation becoming absorbed, trapped and, ultimately, blocked from passing through a transaction card.
Without being limited by theory, it is believed that non-radiative energy transfer of excitation energy occurs between energy donor and energy acceptor. In this case, it is believed that energy absorbed by the phthalocyanine dye is trapped by the inorganic infrared phosphor and the quantum dot material. Therefore, visible radiation emitted by the phosphor is quenched by the quantum dot material. Moreover, separate printing of multiple layers of the ink described herein, in combination with various thermoplastic substrates, provides birefringement properties as well due to differences in refractive indices, further increasing the IR-blocking and absorbing capability of a financial transaction card described herein.
Such non-classical transfer of energy, as described above, is typically explained in terms of the concept of an “exciplex,” an excited complex of two or more molecules arising when an excited molecule comes in contact with a non-excited molecule. However, it is noted that in the present invention, it appears that exciplex formation occurs even when the electronic spectra of donor and acceptor are separate. It is believed that after photo excitation via infrared radiation having a wavelength between about 800 nm to about 1000 nm and greater, the donor collides with the acceptor and an electron transfer to free orbit of the acceptor takes place. An electron is then transferred from this orbit to the ground (non-excited) state of the donor, which is not then accompanied by emission of a photonic quantum. The process is amplified by the materials that are used being removed from solution by the printing process' solvent evaporation and resin bonding to the ink binder. This process provides a much more rigid absorption of infrared radiation. A proper binder is selected to allow the materials to resin bond after printing and further bond during the lamination process.
The pure, recrystallized phthalocyanine dyes of the present invention may include phthalocyanines having the ability to absorb infrared radiation, such as between about 700 nm and about 1000 nm. These phthalocyanine dyes include antimony core complexes, although other core metal complexes may be utilized, such as nickel, platinum, palladium, or any other metal atom that contributes to the phthalocyanine's infrared radiation absorbing capability. Moreover, phthalocyanine dyes including halogen functional groups may be utilized. Fluoride may be used as a halogen functional group, however, any other halogen may be utilized that is apparent to one having ordinary skill in the art. The phthalocyanine dyes may be chosen to provide a broad range of infrared absorption. An antimony core fluoride phthalocyanine dye may be used for the present invention.
One or more phthalocyanine dyes having infrared absorption peaks at 850 nm and 1000 nm may be utilized. A combination of two or more phthalocyanine dyes may be used. Moreover, the phthalocyanine dyes of the present invention may be present in an amount between about 0.0001 wt. % and about 1 wt. %, either alone or in combination. Exemplary phthalocyanine dyes may be obtained from Indigo Science, Newark, N.J., and include Indigo 5547a phthalocyanine dye having an absorption peak of 850 nm, and Indigo 1000a phthalocyanine dye having an absorption peak of 1000 nm.
The inorganic infrared phosphors utilized in the present invention may be based on Y, Yb, Ho, Gd and Er-doped rare earth oxide compounds. Phosphors may include Gd2O3, Er2O3, Y2O3, YF3, either alone or in combination. The phosphors may be utilized singly, or in combination, and may be present in an amount between about 0.01 wt. % and about 5 wt. %.
The quantum dot energy transfer-based compounds may include quantum dot material having from about C9 to about C27 ligands and may be present, either singly or in combination in an amount between about 0.0002 wt. % and about 7.0 wt. %.
The materials described above may be combined together with binders, resins, catalysts, and other compounds useful for creating an ink from the materials. Solvent may be Utilized, including 2-ethoxy-ethyl propionate, ethyl acetate, n-propyl acetate, ethyl alcohol, n-propanol, methyl ethyl ketone. The solvent may be present in an amount between about 5 wt. % and about 60 wt. %. Resins useful for the present invention include VMCH, VMCA, polyamide, polyester, linseed alkyl resins and acrylic, and may be present in an amount between about 8 wt. % and about 35 wt. %. A silane-type catalyst may be used to help bond the phthalocyanine dye to the resin. Specifically, the silane-type catalyst may be used to ring-open the phthalocyanine dye molecule and help the molecule bind to the resin, such as, for example, acrylic. A silane-type catalyst include 3-amino-propyl triethoxy silane, although the present invention should not be limited, as stated herein. The silane-type catalyst may be present in an amount between about 0.005 wt. % and about 2.00 wt. %. The silane-type catalyst may be present at about 500 ppm.
The materials described above are combined together and printed to one or more layers of a financial transaction card via gravure, screen and lithographic variations. FIG. 7J illustrates a cross-section of a financial transaction card according to the invention described herein. The inks of the present invention are placed on one or more sides of polyvinyl chloride and laminated together with magnetic stripes, printed and/or non-printed core layers, and overlaminate layers. The present invention may allow for the easy production of IR-blocking and/or absorbing financial transaction cards without adhesives and/or subassemblies.
After placing the layers of the financial transaction card together in registration (or some variation thereof that is apparent to one having ordinary skill in the art), the layers are laminated in a stack lamination unit for approximately 13 minutes at about 300� F. to about 310� F. under pressure and then cooled for an additional 13 minutes at about 50� F. to about 60� F. The resulting card is approximately 30 mils and possesses good durability and sufficiently blocks infrared light from between about 800 nm to 1200 nm with an optical density of greater than 1.3.
The printing method is typically chosen based on the composition of the various formulations outlined above. Various printing methods may include gravure, silkscreen and lithographic processes, although ink-jet, roll-coating and flexographic methods may be utilized as well. The inks and/or substrates of the present embodiment and their placement and thickness may vary to accommodate different types of core substrates and thicknesses thereof. In addition, PVC may be utilized as a printable substrate. However, other substrates such as PETG, polycarbonate and PET may be utilized provided there are at least slight differences in refractive index between the ink and the substrate.
Infrared phthalocyanine dye or dyes, infrared phosphors and/or quantum dot materials may be incorporated into various plastics such as PVC, PETG, polycarbonate and PET.
Examples of inks of the present invention described above with reference to combinations of infrared phthalocyanine dye or dyes, infrared phosphors and quantum dot materials are described in Examples 5-10, below.
In another embodiment of the present invention, a method has been developed to modify nanocrystalline indium tin oxide (In2O3.SnO2) molecules (“ITO particles” or “ITO molecules”) to be highly transparent, yet reflect infrared light. This material effectively blocks infrared radiation having relatively high wavelengths, as illustrated in FIG. 17J. The modified nanocrystalline ITO molecules may block IR radiation, when incorporated into an ink, coating or other material for disposing on and/or incorporating into a transaction card, at wavelengths as low as about 900 nm and increasing above about 1200 nm, as shown in FIG. 17J. The nanocrystalline ITO molecules may block IR radiation from between about 1300 nm and about 2500 nm. The nanocrystalline ITO molecules may also block IR radiation from between about 1400 nm and about 2000 nm. The nanocrystalline ITO particles may block IR radiation at about 1550 nm. Nanocrystalline ITO particles are typically between 5-100 nm with a specific surface area of 25-50 m2/g. Nanocrystalline ITO particles may be in a ratio of 50% In2O3 to 50% SnO2. Nanocrystalline ITO particles may further be in a ratio of 90% In2O3 to 10% SnO2. Nanocrystalline ITO particles may still further be in a ratio of 70% In2O3 to 30% SnO2.
Transaction cards and other articles may be produced using modified nanocrystalline ITO molecules in an ink, coating, or other material that may be printed, coated, or otherwise disposed on or incorporated into a transaction card or other article. Moreover, any ink, coating or other material utilizing modified nanocrystalline ITO molecules may be combined with various inks, coatings, and/or other materials described herein to provide a transaction card or other article having an IR-blocking or absorbing ability that spans a large section of the IR spectrum. Specifically, inks, coatings and/or other materials described herein may be utilized to block or absorb IR-radiation above about 750 nm. The inks, coatings and/or other materials of the present invention may be utilized to block or absorb IR radiation between about 800 nm and about 2500 nm. The inks, coating and/or other materials of the present invention may be utilized to block or absorb IR radiation between about 900 nm and about 2000 nm.
The nanocrystalline ITO molecules in an ink, coating, or other material may be applied to one or more layers of a transaction card, as fully described herein. The inks, coatings and/or other materials described herein may be applied by printing said inks, coatings or other materials to one or more layers. An internal layer may be printed on, such as prior to laminating said layers to other layers to form a transaction card. In various embodiments, one or more inks, coatings and/or other materials containing nanocrystalline ITO particles described herein may be incorporated into a layer. A layer may be made of a plastic material. For example, nanocrystalline ITO particles may be incorporated into a layer of polycarbonate.
Nanocrystalline ITO particles may be synthesized by a coprecipitation method in an aqueous solution and a thermal method in an alcohol solution. Specifically, the starting materials may be purchased from Samsung Corning Corporation, Warriewood NSW 2102, Australia. Non-nanocrsytalline ITO may be dissolved in an acidic solution of pH of about 5. For example, oxalic acid may be used. A doping agent may be used to dope the ITO particles. Suitable doping agents include Period 4 transition metals. Cobalt may be added to dope the ITO. A liquid extraction may be performed to transfer ITO into an organic solvent phase. A slow, drop-wise precipitation technique may be used to precipitate or coprecipitate nanocrystalline ITO particles. In a thermal method, the nanoparticles have a two phase crystal structure of indium oxide hydroxide (InOOH) and indium hydroxide (In(OH)3).
The crystal structure of ITO may be revealed via X-ray diffraction. Nanocrystalline ITO particles may be annealed. Annealing may occur at about 100 degrees C. to 350 degrees C. Annealing may occur at a temperature of about 300 degrees C. Annealing may occur in an atmosphere containing oxygen (O2). When annealing at a temperature of about 300 degrees C., the Nanocrystalline ITO particle structure may be a rhombohedral crystal structure or a tetrahedral crystal structure.
Nanocrystalline ITO particles may also be purchased commercially. For example, nanocrystalline ITO particles are commercially available from American Elements, 1093 Broxton Ave. Suite 2000, Los Angeles, Calif. 90024, USA, Air Products and Chemicals, Inc., 7201 Hamilton Boulevard, Allentown, Pa. 18195-1501, USA, and Sigma-Aldrich, 3050 Spruce St., St. Louis, Mo. 63103, USA.
Near IR-reflective film may be prepared by mechanical dispersion in a horizontal media mill in a vinyl polymer, VMCA, provided by Union Carbide. Transmission electron microscopy (“TEM”) and energy dispersive X-ray spectrometer (“EDS”) may be used to characterize the morphology and composition of ITO particles. Near-IR (“NIR”) spectrometry may be used to determine the reflectance on the surface of film made with the ITO particles in the NIR-radiation region, as shown in FIG. 17J. Particle size may be determined to be 70 to 90 nm via a Beckman-Coulter particle size analysis model LS 320.
To make a dispersion of the nanocrystalline ITO particles, about 15%-25.0% by weight nanocrystalline ITO particles may be dissolved in 75%-85% by weight solvent. About 20% nanocrystalline ITO particles may be dissolved in 80% solvent. About 5% nanocrystalline ITO particles may be dispersed in 95% solvent. A 40% by weight nanocrystalline ITO particles may be dispersed in about 60% by weight n-propyl acetate. Solvents useful to disperse the nanocrystalline ITO particles include polar, non-polar, hydrophobic, and/or hydrophillic solvents such as n-propanol, ethanol, methyl-ethyl ketone, cyclohexanone, ethyl acetate, water, n-propyl acetate, dimethyl sulfoxide, acetone and most other organic solvents. Liquid and polymer dispersions containing about 25% nanocrystalline ITO, 65% solvent and about 10% polymer from any polymers described herein for various inks may be prepared as well.
Various ink formulations may be made with the nanocrystalline ITO particle dispersion of the present invention, such as for screen printing, lithographic printing, Gravure printing and Flexo printing. Each ink formulation may be specifically tailored for the particular printing method. For example, for screen printing, the nanocrystalline ITO dispersion may be further dispersed in cyclohexane. Moreover, for litho printing, the nanocrystalline ITO dispersion may be further dispersed in Lawter 100s free flow alkyd. In addition, for Gravure printing, nanocrystalline ITO dispersion may be dispersed in VMCA and n-propyl acetate. Finally, for Flexo printing, nanocrystalline ITO dispersion may be dispersed in n-propyl alcohol. While specific solvents are presented, depending on the method of printing or fabricating onto or into one or more layers of a transaction card, it should be recognized by those having ordinary skill in the art that the nanocrystalline ITO dispersion may be dispersed in a plurality of solvents. See below for examples of nanocrystalline ITO dispersions of the present invention for various printing methods.
Various primer formulations may be made with nanocrystalline ITO particles. A primer includes a material that is applied prior to an adhesive that improves and/or alters the bonding characteristics of the adhesive. Many primers alter surface tension characteristics in order to improve the bonding characteristics of the adhesive. A primer includes gravure ink containing nanocrystalline ITO particles that is printed on a substrate layer, prior to application of an adhesive. Any suitable primer may include nanocrystalline ITO particles.
In a further embodiment of the present invention, fibers of various materials are used either in a continuous manner or single fibers may be incorporated into a wide variety of materials. The present invention contemplates, for example, natural fibers, synthetic fibers, copolymer fibers, chemical fibers, metal fibers, and/or the like. Examples of these fibers may be nylon, polyester, cotton, wool, silk, casein fiber, protein fiber, acetalyated staple, ethyl cellulose, polyvinylidene chloride, polyurethane, acetate, polyvinyl alcohol, triacetate, glass, wood, rock wool, carbon, inorganic fibers, and/or the like. Such fibers may be incorporated or mixed into other types of materials such as paper pulp, plastic label stock, plastic materials, and the like. Such materials may be used alone in a continuous manner or may be used as mono- or di-filaments in other materials.
Moreover, the infrared blocking compounds that are incorporated into plastics may be used with a wide variety of materials, such as, for example, nylon, acrylic, epoxy, polyester, bismaleimide, polyamide, polyimide, styrene, silicone, vinyl, ABS, polycarbonate, nitrile, and/or the like. As such, the compounds that are incorporated into fibers, plastics, film and/or the like, may be processed directly to a suitable form in a single- or multi-process application. Such compounds may be added into a formulation in the form of a single ingredient or in the form of a master-batch that is then processed in a similar manner to normal processing operations of compounds. Processing of such compounds includes the use of continuous mixers, two- or three-roll mills, extrusion, and/or other melt-compounding methods of dispersion. While in an exemplary embodiment, the thread may be woven or non-woven, the infrared materials may be extruded directly into a thermoplastic matrix and drawn directly into the form of a thread that may be used in a continuous manner or sectioned in the form of a fiber or plastic film.
The exemplary infrared compounds are deposited onto films of various compositions and may be used in most card applications. Moreover, the infrared compounds in accordance with the present invention may be used alone or blended with other materials at ranges from 0.001 to 50.0 parts by weight, but may be from 1.0 to 15.0 parts by weight.
An infrared compound may be a multilayer polymeric film manufactured by 3M Company (Minneapolis, Minn.), and described in U.S. Pat. No. 5,882,774 entitled “Optical Film”, U.S. Pat. No. 6,045,894 entitled “Clear to Colored Security Film”, and U.S. Pat. No. 6,049,419 entitled “Multilayer Infrared Reflecting Optical Body”, each of which is incorporated herein by reference in their entireties. Specifically, the multilayer polymeric film is either a birefringement dielectric multilayer film or an isotropic dielectric multilayer film designed to reflect infrared radiation, i.e., electromagnetic radiation commonly known to have a wavelength longer than visible light, specifically above about 700 nm.
A film utilized in the present invention comprises at least two layers and is a dielectric optical film having alternating layers of a material having a high index of refraction and a material having a low index of refraction. The film may be either birefringement or isoptropic and is designed to allow the construction of multilayer stacks for which the Brewster angle is very large or is nonexistent for the polymer layer interfaces. This feature allows for the construction of multilayer mirrors and polarizers whose reflectivity for p-polarized light decreases slowly with angle of incidence, is independent of angle of incidence, or increases with angle of incidence away from the normal. As a result, the multilayer films have high reflectivity over a wide bandwidth.
Specific examples of such films are described in U.S. patent Ser. No. 08/402,201, filed Mar. 10, 1995, and U.S. patent Ser. No. 09/006,601 entitled “Modified Copolyesters and Improved Multilayer Reflective Film”, filed on Jan. 13, 1998. In addition, U.S. Pat. No. RE 3,034,605 describes films which prevent higher order harmonics that prevent color in the visible region of the spectrum. Other suitable films include the films described in U.S. Pat. No. 5,360,659, which describes a two component film having a six layer alternating repeating unit that suppresses reflections in the visible spectrum (about 380 nm to about 770 nm) while reflecting light in the infrared wavelength region of between about 770 nm to about 2000 nm.
Multilayer polymeric films may include hundreds or thousands of thin layers and may contain as many materials as there are layers in the stack. For ease of manufacturing, multilayer films may have only a few different materials. A multilayer film, as noted above, includes alternating layers of a first polymeric material having a first index of refraction, and a second polymeric material of a second index of refraction that is different from that of the first material. The individual layers are typically on the order of about 0.05 μm to about 0.45 μm thick. The number of individual layers in the optic film may range from about 80 to about 1000 layers, although other numbers are contemplated in the present invention. In addition, the optical film may be as low as about 0.5 mil thick to as high as about 20.0 mils thick.
The multilayer films useful in the present invention may comprise alternating layers of crystalline naphthalene dicarboxylic acid polyester and another selected polymer, such as copolyester or copolycarbonate, wherein each of the layers have a thickness of less than about 0.5 μm. Specifically, polyethylene 2,6-naphthalate (PEN), polybutylene 2,6-naphthalate (PBN), or polyethylene terephthalate (PET) are typically used. Adjacent pairs of layers (one having a high index of refraction and the other a low index) may have a total optical thickness that is � of the wavelength of the light desired to be reflected. However, other ratios of the optical thicknesses within the layer pairs may be chosen as is apparent to one having ordinary skill in the art. An optic film may be as low as about 0.5 mil having alternating layers of PET and polymethylmethacrylate (PMMA).
Any other optical film may be utilized in the present invention that effectively absorbs, refracts, diffuses, reflects or otherwise blocks electromagnetic radiation of a range or a plurality of ranges of wavelengths, but transmits electromagnetic radiation of another range or plurality of wavelengths, such as, for example, blocking the transmission of infrared radiation, but transmitting visible radiation, and the present invention should not be limited as herein described. Other suitable optical films may be utilized as apparent to one having ordinary skill in the art.
The present example includes about 2% Epolin VII-164 dye and about 98% Tech Mark Mixing Clear, produced by Sericol, Inc. 980.0 g of Tech Mark solvent evaporative screen ink is mixed on a high-speed disperser. While mixing, 20.0 g of Epolight VII-164 dye is dissolved completely. The resulting ink has a viscosity of about 3.2 Pa�S at 25 C degrees and is printed using a screen process. The screen process includes a 305 polymer screen onto both sides of clear PVC 13.0 mil film.
The following ink was produced by adding about 15.0 lbs of Epolight VII-164 and about 20.0 lbs of Epolight VI-30 to about 965 lbs. of TM Mixing Clear. The mixture was dispersed for about 40 minutes. The resulting mixture was coated on PVC core plastic using an 80 line/cm polyester screen. The resulting coating exhibited high absorbtivity from 780 nm to 1070 nm with low visible absorption. Card core, magnetic stripe and lamitate were assembled and the entire assembly was placed in Burckle Stack Lamination Unit at a temperature of about 280 F.
A concentrate of about 30.0 g. Epolight VII-172 was blended with about 700.0 g. of polyvinylchloride plastic. The resulting mixture was extruded at about 260 F, air cooled and pelletized. About 1.0 lb of the resulting pellets were combined with about 99.0 lbs of PVC. Klockner Pentaplast provided calendered sheets of approximately 0.013 inches. Cards were fabricated using said sheets. These cards exhibited sufficenent absorption in the IR region from 800 nm to 1000 nm. The cards were detected by a Sankyo ATM capture device.
Multi-Layer PET plastic with sufficient optical properties was combined into a card construction. The PET plastic was provided by 3M Co. (Minneapolis, Minn.), as described above. The resultant card exhibited sufficient optics such that an ATM device detected the card.
Ink containing about 37.0 wt. % 2-ethoxy-ethyl-proprionate was combined with about 27.0 wt. % VMCH vinyl resin. The ink further comprised about 0.0015 wt. % of a mixture of about 0.00075 wt. % Indigo 5547a phthalocyanine dye, obtained from Indigo Science, Newark N.J., having an absorption peak of about 850 nm and about 0.0009 wt. % Indigo 1000a phthalocyanine dye, also obtained from Indigo Science, having an absorption peak of about 1000 nm. About 0.00003 wt. % quantum dot material having about C 17 assymetric along the Y-Axis ligands were added. An inorganic phosphor containing Y, Yb, Tm, and Yt oxide about 0.005 wt. % was added. About 500 ppm 3-amino-propyl triethoxy silane was included. The resulting ink was screen printed on a solvent-evaporative screen press on both sides of a PVC substrate and laminated at about 305� F. for 13 minutes.
Ink having the above concentrations of phthalocyanine dyes, quantum dot material and inorganic phosphors was combined with about 16.0 wt. % vinyl VMCA resin and about 88.0 wt. % methyl ethyl ketone to make an ink for gravure printing. The mixture was printed on both sides of 7.0 mil PVC, and laminated to form a financial transaction card, as described above in Example 5.
Ink containing the above concentrations of phthalocyanine dyes, quantum dot material and inorganic phosphors were combined and milled with about 22.0 wt. % nitro-polyamide resin containing about 18.0 wt. % ethyl acetate, about 14.0 wt. % n-propyl acetate, about 7.0 wt. % ethyl alcohol, about 3.0 wt. % n-propanol and about 19.0 wt. % methyl ethyl ketone solvents. The mixture was gravure printed on both sides of 7.0 mil PVC layer and laminated to form a financial transaction card, as described above in Example 5.
Ink containing the above concentrations of phthalocyanine dyes, quantum dot material and inorganic phosphors were combined with about 20.0 wt. % acrylic resin and about 34.0 wt. % MEK. The mixture was gravure printed on 7.0 mil PETG and laminated to form a financial transaction card, as described above in Example 5.
Ink containing the above concentrations of phthalocyanine dyes, quantum dot material and inorganic phosphors was combined with about 98.0 wt. % Serical TM-MX and screen printed on 7.0 mil PVC using a polyester 325-mesh screen.
Ink containing approximately 10 times the concentration by wt. % of phthalocyanine dyes, quantum dot material and inorganic phosphors was combined in a three roll mill using a mixture of about 18.0 wt. % gelled and free-flow linseed alkyd resins and adjusted to printing viscosity and tack with about 17.0 wt. % deodorized kerosene (Magisol 52). The mixture was lithographically printed on both sides of 10 mil PVC, dried overnight and laminated as described above in Example 5.
Nanocrystalline ITO particles may be synthesized via a coprecipitation method. Starting materials may be purchased from Samsung Corning Corporation, Warriewood NSW 2102, Australia. Non-nanocrsytalline ITO may be dissolved in an aqueous, acidic solution of pH of about 5. For example, oxalic acid or hydrochloric acid may be used. Cobalt may be added to dope the ITO. A liquid extraction may be performed to transfer ITO into an organic solvent phase. Dimethyl sulfoxide (DMSO) may be a suitable organic solvent. A slow, drop-wise precipitation technique may be used to precipitate or coprecipitate nanocrystalline ITO particles.
A dispersion may be made from the nanocrystalline ITO particles made by Method 11, above. Specifically, about 40% by weight nanocrystlaline ITO particles made by Method 11 may be dispersed in about 60% by weight n-propyl acetate.
An ink formulation may be made from the dispersion made by Method 12 for screen printing onto one or more layers of a transaction card. The ink formulation may be comprised of about 5% by weight of the dispersion of Method 12 dispersed in about 95% by weight cyclohexane.
An ink formulation may be made from the dispersion made by Method 12 for lithographic printing onto one or more layers of a transaction card. The ink formulation may be comprised of about 40% by weight of the dispersion of Method 12 dispersed in about 60% by weight Lawter 100s free flow alkyd.
An ink formulation may be made from the dispersion made by Method 12 for Gravure printing onto one or more layers of a transaction card. About 20% by weight VMCA resin may be dissolved in 50% by weight methyl ethyl ketone followed by the addition of about 30% by weight of the dispersion of Method 12. The resulting material may be printed on two sides of PET-G. A spectrum may be measured using a Si—Ge detector with a CVI spectrometer in transmission mode. The spectrum is shown in FIG. 17J.
An ink formulation may be made from the dispersion made by Method 12 for Flexo printing onto one or more layers of a transaction card. The ink formulation may comprise about 35% by weight of the dispersion of Method 12 dispersed in about 65% by weight n-propyl alcohol.
A preparation of nanocrystalline ITO may be incorporated into a plastic that is then extruded or otherwise processed into a translucent or transparent layer. Nanocrystalline ITO may be incorporated into most plastics, including polycarbonate and PVB. Such a layer may be incorporated into various articles of manufacture, including transaction cards.
A preparation of nanocrystalline ITO may be incorporated into a plastic that is then extruded or otherwise processed into a translucent or transparent layer. An ink formulation using any preparation of nanocrystalline ITO may be disposed onto plastic materials. The resulting plastic may be laminated, associated with or otherwise affixed to layers containing one or more infrared blocking materials. In this manner, by combining multiple infrared blocking materials, the resulting article may be able to successfully block one or more wavelength ranges of infrared light.
An ink formulation using any preparation of nanocrystalline ITO may be incorporated into a plastic that is then extruded or otherwise processed into a translucent or transparent layer. A nanocrystalline ITO layer may be laminated, associated with, or otherwise affixed to a subassembly comprising a birefringement dielectric material, an isotropic dielectric material, a metallic film, or an infrared blocking film comprising a plurality of layers disposed on a substrate where at least two of the layers have different refractive indices. A nanocrystalline ITO layer may be laminated, associated with, or otherwise affixed to a layer containing an infrared blocking ink. A nanocrystalline ITO layer may be laminated, associated with, or otherwise affixed to a layer containing or having a quantum dot compound.
An ink formulation using any preparation of nanocrystalline ITO may be disposed onto a substrate layer. A layer having nanocrystalline ITO ink may be laminated, associated with, or otherwise affixed to a subassembly comprising a birefringement dielectric material, an isotropic dielectric material, a metallic material, or an infrared blocking film comprising a plurality of layers disposed on a substrate where at least two of the layers have different refractive indices. A layer having nanocrystalline ITO ink may be laminated, associated with, or otherwise affixed to a birefringement dielectric material, an isotropic dielectric material, a metallic material, and/or an infrared blocking film comprising a plurality of layers disposed on a substrate where at least two of the layers have different refractive indices. A layer having nanocrystalline ITO ink may be laminated, associated with, or otherwise affixed to a layer containing an infrared blocking ink. A layer having nanocrystalline ITO ink may be laminated, associated with, or otherwise affixed to a layer containing or having a quantum dot compound.
Additional examples of IR ink formulations are disclosed in FIG. 13. The IR ink examples in FIG. 13 exhibit a visible green color. Moreover, FIG. 14 shows measurements related to these exemplary cards, including, for certain wavelength ranges, transmission density, ATM readability and ISO compliance. FIG. 15 shows exemplary test results for the exemplary green cards wherein samples of the cards were inserted into ATMs of various manufacturers. The tests resulted in positive ATM detection of the exemplary cards. Furthermore, FIG. 16 shows an example of the transmission density of exemplary green cards in a graph of percent transmission v. wavelength (the graph also indicates the ISO specifications for the card).
FIGS. 17C-17J represent various spectra of films, coatings, cards, etc. which demonstrate the ability of the materials used in the card constructions to block sufficient quantities of infrared radiation and transmit visible light in order to produce cards described in the embodiment. The mechanism of blocking may be absorption, reflection, diffusion, dispersion or other methods of blocking radiation in the electromagnetic spectrum.
In addition to the IR inks, the infrared blocking compound may alternatively be a film or hot mirror which also blocks (absorbs or reflects) infrared light, but transmits all other wavelengths of light. In an exemplary embodiment, the film is set between the front sheet 10 and back sheet 12. FIG. 4 is a graph of energy v. wavelength for the reflection and transmission of an exemplary IR film in accordance with an exemplary embodiment of the present invention. FIG. 4 shows that, while the visible light is transmitted through the film, the infrared light is blocked at higher wavelengths and a substantial amount of infrared light is reflected.
The infrared blocking compound may be incorporated into plastic products, films, products, documents or other articles which may inhibit detection via phototransistors, CCD's, and/or the like. The material may be incorporated into a transaction card via a film, plastic, printing ink, coating or other application medium by grinding or the use of dispersed or deposited material into a liquid, paste or other type of medium. To minimize environmental damage to the ink, such as the ink being scratched, the ink may be applied directly onto the plastic sheets under the laminate (described below in step 170). Moreover, the infrared ink may be applied on the inside or outside surface of the plastic sheets.
In an exemplary embodiment, incorporating the infrared blocking compounds into an article may not require a separate printing unit, modifications to existing processing equipment or an additional operational step. Particularly, the fabrication of the articles, such as a transaction card, utilizes existing equipment which incorporate colorants anyway, so the application of the infrared blocking compounds to the existing colorants do not add extra equipment or steps to the process.
In a further exemplary embodiment, the infrared blocking compounds block light which is detectable by machines. More particularly, the machines suitably detect the presence of a card via infrared interference at one or several wavelengths. In an exemplary embodiment, detection of materials may include the production of a visual effect when the materials are interrogated with invisible infrared radiation from the proper instrument, and when such radiation contacts the infrared material, a visual effect, such as a colored light, may be seen. Alternatively, the materials may be detected by a remote detector that will indicate the presence of the materials. Detection or authentication of the materials occurs above and below the stimulation wavelength of the reading device. As such, once the infrared blocking compound has been detected, the detection device may then provide the user with a positive identification signal, which may be located on or near the detection device.
In addition to triggering the sensors in ATM machines, translucent card 5 may be used with any magnetic stripe or smart card reader. The reader system may include a card reader/writer, a point-of-sale terminal, ATM or any other acceptance device. In an exemplary embodiment, card 5 is used in conjunction with a reader which, not only detects the existence of the card, but also illuminates the transparent portion of card 5 when the card is inserted into the reader. The illumination source may be either an incandescent or solid state source (infrared emitting diode or laser). In operation, when the card is inserted into the acceptance device, the edge of the card presses against the illumination assembly (or activates a switch, interrupts a beam, etc.). Depending upon the application of the card, the illumination source may be under the control of the acceptance device or external software. Thus, the illumination source may flash or display a particular color if directed by the external software program. Additionally, depending on the structure of the card, the illumination source may be used to excite an embedded design useful for security or product enhancement.
As discussed above, the infrared blocking compounds may be incorporated into any type of article. An exemplary article is a transaction card which may itself include any number of numerous features. In an exemplary embodiment, the present invention includes, generally, a transaction card 5 comprised of base containing opaque, transparent or translucent plastic layers 10, 12 and multiple features affixed to the card 5 such as text 30, 32, 34, logos 50, embossed characters 35, magnetic stripe 42, signature field 45, holographic foil 15, IC chip 20 and opacity gradient 25 (FIGS. 1 and 2).
Card 5 also includes an infrared blocking compound, described above, for allowing the transparent or translucent transaction card 5 to be recognized by card reading devices, such as ATMs, and/or for allowing the transparent transaction card 5 to be recognized and counted during card fabrication. The infrared blocking compound on transparent card 5 is a substantially invisible or translucent infrared ink, mirror or film which blocks (absorbs or reflects) infrared light but transmits all other wavelengths of light (see FIG. 4). Card 5 may be used for credit, charge, debit, access, identification, information storage, electronic commerce and/or other functions.
With respect to FIG. 3, to fabricate card 5 having a front and back surface in accordance with an exemplary embodiment of the present invention, a front sheet 10 and back sheet 12 (FIGS. 1 and 2) consisting of a plastic substrate such as, for example, clear core PVC, are produced (step 100). One skilled in the art will appreciate that sheets 10 and 12 of card 5 may be any suitable transparent, translucent and/or opaque material such as, for example, plastic, glass, acrylic and/or any combination thereof. Each sheet 10, 12 is substantially identical and may be about 3′�4′ (622 mm�548 mm) and about 0.005-0.350 inches, or may be 0.01-0.15 inches or 13.5 mil thick.
With respect to FIG. 7A, the fabrication of the individual card sheets includes either direct layout (9 layers) of film or the use of a sub-assembly (5 layers). An exemplary sub-assembly consists of 5 layers of film with room temperature tack adhesive applied over thermoset and thermoplastic adhesives. The resulting cards comprise (from the card front towards the card back) 2.0 mil outer laminate (PVC, polyvinylchloride) having the holographic foil, embossed surface, chip and other indicia on its surface, 9.0 mil printed PVC core with print side out (card front), 2.0 mil PVC adhesive, 1.7 mil PET GS (extrusion coated polyethyleneterephthalate-gluable/stampable) manufactured by D&K (525 Crossen, Elk Grove Village, Ill. 60007), 2.0 mil PET IR blocking film, 1.7 mil PET GS, 2.0 mil PET adhesive, 9.0 mil printed PVC core with the print side out (card back), and 2.0 mil outer back laminate with a signature panel, applied magnetic stripe and other indicia. Optimally, the PET IR blocking film is fabricated in the middle of the layers to balance the card and minimize warping of the resulting card product. Other exemplary embodiments of the layers are shown in FIGS. 7B-7H.
Specifically, FIG. 7G illustrates an alternate embodiment of the individual transaction cards. As with FIG. 7A, card sheets may be constructed as described in FIG. 7H. Each card sheet may include nine layers of film or the use of a five layer subassembly. The resulting cards comprise (from the card front towards the card back) about 2.0 mil outer laminate (PVC) having the holographic foil, embossed surface, chip and/or other indicia on its surface, about 9.0 mil printed PVC core with print side out (card front), about 1.0 mil oriented PVC, about 3 mil adhesive (1 mil PET with 1 mil adhesive on each side), about 2.0 mil PET IR blocking film, as described above, about 3.0 mil adhesive (1 mil PET with 1 mil adhesive on each side), about 1.0 mil oriented PVC, about 9.0 mil printed PVC core with print side out (card back), and about 2.0 mil outer PVC laminate comprising a signature panel, applied magnetic stripe and/or any other indicia apparent to one having ordinary skill in the art. As with the card described in FIG. 7A, the PET IR blocking film is fabricated in the middle of the layers to balance the card and minimize warping of the resulting card product.
The adhesive layers described above with reference to FIG. 7G (the 3.0 mil adhesive) that may be disposed on either side of the 2.0 mil PET IR blocking film may comprise a first layer of a polyester (1.0 mil PET) having second and third layers of a polyester-based adhesive disposed on either side of the first layer of polyester. The polyester-based adhesive layers may each be about 1.0 mil. The polyester-based adhesive layers exhibit excellent adhesion to polyester and PVC, in that it binds to both the PET IR blocking film on one side of the 3.0 mil adhesive and the 1.0 mil oriented PVC layer on the other side. Specifically, a material that may be used as the polyester-based adhesive is Bemis Associates Inc. 5250 Adhesive Film. Alternatively, another material that may be used as the polyester-based adhesive is Transilwrap Company, Inc. Trans-Kote� Core Stock KRTY.
The card sheet of FIG. 7G, including the nine layers of film and/or the use of a five layer subassembly, as described above, may be constructed together by a lamination process as is known to someone having ordinary skill in the art using heat and pressure. A method of constructing the cards as described in FIG. 7H utilizes a two-step lamination cycle, wherein a first hot step includes laminating the layers of the cards together at a pressure of about 170 psi at a temperature of about 300� F. for about 24 minutes. A second step includes laminating the layers together at a pressure of about 400 psi at a diminished temperature of about 57� F. for about 16 minutes. Of course, other methods of constructing the cards may be utilized.
FIG. 7I illustrates another exemplary card sheet construction according to the present invention. Specifically, FIG. 7I illustrates another transparent or translucent card having an IR blocking optical film incorporated therein, as described above with reference to FIGS. 7A and 7G. The card sheet construction defined below may be made via a coextrusion/lamination process. Specifically, the card sheet comprises a layer of a PET IR blocking optical film (about 2.0 mils), as described above. An EVA-based material (about 2.0 mils) may be coextruded onto each side of the IR blocking film to form a 3-layer subassembly. The 3-layer subassembly may then be laminated on each side to a printed PVC layer (each about 11 mils). The card may further have PVC laminate layers (each about 2.0 mils) disposed on sides of the printed PVC layers thereby forming outside layers of the card.
Materials that may be utilized as the EVA-based material that is coextruded to the PET IR blocking film are acid modified EVA polymers. The acid modified EVA polymers may be Bynel� Series 1100 resins. Typically, the Bynel� Series 1100 resins are available in pellet form and are used in conventional extrusion and coextrusion equipment designed to process polyethylene resins. The Bynel� Series 1100 resins have a suggested maximum melting temperature of about 238� C. However, if adhesion results are inadequate, the melting temperature may be lowered. The remaining layers of the card may be laminated to the card as described above, or via any other lamination process to form a card.
After eventually combining the sheets (step 160), by adhering the front sheet 10 on top of the back sheet 12, the total thickness of the transaction card 5 is about 0.032 in. (32 mil.), which is within the ISO thickness standard for smart cards. Because the IC chip 20 is eventually embedded into the surface of the substrate (step 195), and the surface of chip 20 is co-extensive with the outer surface of the front sheet 10, the IC chip 20 does not affect the thickness of the overall card 5. Moreover, the about 3′�4′ sheets include markings which define the boundaries of the individual cards 5 which will be cut from the sheet. Each exemplary sheet yields over 50 transaction cards (typically 56 cards), wherein each card 5 is within the ISO card size standard, namely about 2″�3.5″.
In general, an exemplary process for construction of card 5 having an IR film includes chemical vapor deposition of PET film which has optimal visible and infrared properties (step 105). The chemical deposition is preformed by a Magnetron Machine manufactured by the Magnetron Company. With respect to FIG. 10, the process incorporates a roll chemical vapor deposition sputtering system with three coating zones. The Magnetron roll vapor deposition machine deposits evaporation batches containing Ag, Au and Indium oxide onto optical grade polyethyleneterephthalate using chemical vapor deposition. The Ag/Au/Indium layers are about 100 angstroms each and, depending on the lower wavelength reflections, about three to five layers exist. More details related to vacuum coating, solar coating and Magnetron sputtering may be found in, for example, “Handbook of Optical Properties, Volume I, Thin Films for Optical Coatings” edited by Rolf Hummel and Karl H. Guenther, 1995, CRC Press, Inc, the entire contents of which is hereby incorporated by reference.
Next, plasma or flame treatment is applied to the PET film for surface tension reduction of the film (step 110). During the deposition and assembly of the layers, the IR film is monitored to optimize the IR blocking spectrum. Thus, the film is then tested against a standard by using a spectrophotometer to test the visible and infrared properties of the PET film (step 115). With respect to FIG. 9, a reflection and transmission monitor with various optical components for vacuum evaporation in-line roll coating operations is utilized to monitor the IR film. In-line spectrophotometric monitoring is part of the vapor deposition process. Transmission at various wavelengths is monitored during the entire run. A tack adhesive is applied to PET GS (polyethyleneterephthalate—gluable/stampable) (step 120) and a pressure laminate is applied to the Indium Oxide metal surface of the PET IR blocking film (step 125). Next, a tack adhesive is applied to the PET side of the IR blocking film (step 130) and a pressure laminate is applied to the PET GS (step 135). Exemplary lamination conditions include 280 F degrees and 600 psi for 22 minutes, then cooled under pressure for about 18 minutes. A heat seal adhesive is applied to both outer sides of the PET GS, or alternatively, a PVC adhesive is applied to both outer sides of the PET GS (step 140).
In an exemplary embodiment, certain compounds are printed over the surface of sheets 10 and 12. One skilled in the art will appreciate that the printing of the text 30, 32, 34, logos 50, infrared blocking ink and opacity gradient 25 may be applied to any surface of card 5 such as, for example, the front 10 face, the rear 12 face, the inside or outside surface of either face, between the two sheets of base material and/or a combination thereof. Moreover, any suitable printing, scoring, imprinting, marking or like method is within the scope of the present invention.
The opacity gradient 25 and infrared blocking ink are printed onto the sheets by a silk screen printing process (step 150). With respect to the opacity gradient 25, the exemplary gradient is comprised of a silver pearl ink gradation having an ink stippling which is more dense at the top of card 5 and gradually becomes less dense or clear as it approaches the bottom of card 5. One skilled in the art will appreciate that the opacity gradient 25 may be any density throughout the gradient 25 and the gradient 25 may traverse any direction across card 5 face. The opacity gradient 25 may be formed by any substance which may provide a similar gradient 25 on card 5. The exemplary ink gradient 25 for each card 5 is printed using known printing inks suitably configured for printing on plastic, such as Pantone colors. In an exemplary embodiment, the ink used for the stippling 25 is a silver pearl ink and is applied to the outside surface of each plastic sheet. Ink gradient 25 is printed on the surface of each of the sheets using a silk screen printing process which provides an opaque, heavier ink coverage or using offset printing process which provides halftone images in finer detail. The words “American Express” are printed in Pantone 8482 using a similar silkscreen process.
More particularly, with respect to silk screen printing, artwork containing the desired gradient 25 is duplicated many times to match the number of individual cards 5 to be produced from the sheets. The duplicated artwork is then suitably applied to a screen by any suitable known in the art photo-lithographic process and the screen is then developed. The screen is placed over the sheet and ink is suitably washed across the surface of the screen. The exposed portions of the screen allow the ink to pass through the screen and rest on the sheet in the artwork pattern. If multiple colors are desired, this process may be repeated for each color. Moreover, other security features are optionally silk printed on card 5 such as, for example, an invisible, ultraviolet charge card logo (visible in black light) is printed in a duotone of Pantone 307 and 297 using offset and silk screen presses.
The text 30, 32, 34 and logo 50 are printed on the outside surface of each sheet by a known printing process, such as an offset printing process (step 155) which provides a thinner ink coverage, but clearer text. More particularly, with respect to offset printing, the artwork is duplicated onto a metal plate and the metal plate is placed onto an offset press printing machine which may print up to four colors during a single run. The offset printed text includes, for example, a corporate name 30, a copyright notice 33, a batch code number 34, an “active thru” date 32, contact telephone numbers, legal statements (not shown) and/or the like. The exemplary offset text is printed in 4 DBC in opaque white ink or a special mix of Pantone Cool Gray 11 called UV AMX Gray.
Because the resulting card 5 may be transparent, the text may be seen from both sides of card 5. As such, if the text is only printed on one sheet, the text may be obscured when viewing the text from the opposite side of card 5 (in other words, viewing the text “through” the plastic substrate). To minimize the obscuring of the text, the front sheet 10 is printed on its outside surface with standard format text and the back sheet 12 is printed on its outside surface with the same text, but the text is in “reverse” format. The back 12 text is aligned with the text on the front face 10, wherein the alignment of the text is aided by card 5 outline markings on the full sheet. Certain text or designs which may be obscured by an compound of card 5 (magnetic stripe 40, chip 20, etc.) may be printed on only one sheet. For example, in an exemplary embodiment, the corporate logo 50 is printed on only one sheet and is located behind the IC chip 20, thereby being hidden from the front 10 view and hiding at least a portion of the IC chip 20 from the back 12 view. One skilled in the art will appreciate that any of the offset printing may occur on the outside or inside surface of the sheets.
The sheet of laminate which is applied to the back 12 of card 5 (step 170) includes rows of magnetic stripes 40, wherein each magnetic stripe 40 corresponds to an individual card 5. The magnetic stripe 40 extends along the length of card 5 and is applied to the back 12 surface, top portion of card 5 in conformity with ISO standards for magnetic stripe 40 size and placement. However, the magnetic stripe 40 may be any width, length, shape, and placed on any location on card 5. The two track magnetic stripe 40, including the recorded information, may be obtained from, for example, Dai Nippon, 1-1, Ichigaya Kagacho 1-chome, Shinjuku-ku, Tokyo 162-8001, Japan, Tel: Tokyo 03-3266-2111. In an exemplary embodiment, the magnetic stripe is applied to the outer laminate using a tape layer machine which bonds the cold peel magnetic stripe to the outer laminate roll with a rolling hot die and at suitable pressure. The roll is then cut into sheets at the output of the tape layer before the card layers are assembled and the stripe is fused to the card during the lamination process.
Although prior art magnetic stripes 40 in current use are black, in a particularly exemplary embodiment, the magnetic stripe 40 of the present invention is a silver magnetic stripe 40. Exemplary silver magnetic stripe 40 is 2750 oersted and also conforms to ISO standards. Moreover, the silver magnetic stripe 40 includes printing over the magnetic stripe 40. The printing on the magnetic stripe 40 may include any suitable text, logo 50, hologram foil 15 and/or the like; however, in an exemplary embodiment, the printing includes text indicative of an Internet web site address. Dai Nippon Printing Co., Ltd (more information about Dai Nippon may be found at www.dnp.co.jp) prints a hologram or text on the magnetic stripe using, for example, the Dai Nippon CPX10000 card printer which utilizes dye sublimation retransfer technology having a thermal head which does not contact the card surface. The card printer utilizes the double transfer technology to print the image with the thermal head over a clear film and then re-transferring the printed image onto the actual card media by heat roller. The printing of information on the surface of the magnetic stripe 40 is preformed by, for example, American Banknote Holographics, 399 Executive Blvd., Elmsford, N.Y. 10523, (914) 592-2355. More information regarding the printing on the surface of a magnetic stripe 40 may be found in, for example, U.S. Pat. No. 4,684,795 issued on Aug. 4, 1987 to United States Banknote Company of New York, the entire contents of which is herein incorporated by reference.
After the desired printing is complete and the magnetic stripe applied, the front 10 and back 12 sheets are placed together (step 160), and the sheets are adhered together by any suitable adhering process, such as a suitable adhesive. One skilled in the art will appreciate that, instead of printing on two sheets and combining the two sheets, a single plastic card 5 may be used, wherein card 5 is printed on one side, then the same card 5 is re-sent through the printer for printing on the opposite side. In the present invention, after adhering the sheets together, a sheet of lamination, approximately the same dimensions as the plastic sheets, namely 3′�4′, is applied over the front 10 and back 12 of card 5. After the laminate is applied over the front 10 and back 12 of the combined plastic sheets (step 170), card 5 layers are suitably compressed at a suitable pressure and heated at about 300 degrees, at a pressure of between 90-700 psi, with a suitable dwell time to create a single card 5 device. The aforementioned card fabrication may be completed by, for example, Oberthur Card Systems, 15 James Hance Court, Exton, Pa.
The cards may be constructed by laminating the layers together using heat and pressure. For example, the transaction cards may be roll laminated with adhesives, platen laminated, or other lamination process to laminate the cards together. Processing temperatures may range from about 200� F. to about 5000 depending on the material used in the layers of the multilayer transaction card (such as PETG, polycarbonate, or other like materials). For PVC, the temperatures commonly range from about 270� F. to about 320� F. Pressures may range from about 50 psi to about 600 psi. Processing times for laminating the transaction cards of the present invention may range from a few seconds (1-10 seconds, for example if roll laminated with adhesives) to up to about an hour if polycarbonate is used as a material in the multilayer transaction card. For PVC materials, a hot cycle of about 20 to 30 minutes may be used. Cool cycles may last about 15 to about 25 minutes for PVC materials.
In an exemplary embodiment, and especially for IR ink cards, such as, for example, the card described with respect to FIG. 7H, the card layers are fused together in a lamination process using heat and pressure. During the hot press phase, the press is heated to about 300 F degrees and the pressure builds to about 1000 psi and holds for about 90 seconds. The pressure then ramps up to about 350 psi over an about 30 second period and holds for 16 minutes at the same temperature, namely 300 F degrees. The card is then transferred to a cold press that is at about 57 F degrees. The pressure builds to about 400 psi and is held for about 16 minutes as chilled water of about 57 F degrees is circulated in the plates. The cold press then unloads the card.
With respect to FIGS. 1 and 2, after the laminate is applied, a signature field is applied to the back surface 12 of card 5 (step 175) and the holographic foil 15 is applied to the front 10 of card 5 (step 190). With respect to signature field 45, although prior art signature fields are formed from adhering a paper-like tape to the back 12 of card 5, in an exemplary embodiment of the present invention, the signature field 45 is a translucent box measuring about 2″ by ⅜″ and is applied to the card using a hot-stamp process. The verification of the signature in signature field 45 by the merchant is often a card 5 issuer requirement for a merchant to avoid financial liability for fraudulent use of card 5. As such, the translucent signature field 45 on the transparent card 5 not only allows the clerk to view at least a portion of the signature field 45 from the front of the card 5, but the signature view also encourages the clerk to turn over card 5 and verify the authenticity of the signature with the signed receipt.
After the card sheets are laminated, the sheets may be cut into individual cards 5 (step 180) by a known stamping process, including any necessary curing, burrowing, heating, cleaning and/or sealing of the edges. The individual transaction cards 5 may be about 3″�4″ and conform to ISO standards for transaction card 5 shape and size. In an exemplary embodiment, the laminated sheets of 56 cards may be suitably cut in half on a guillotine device, resulting in two half-sheets of 28 cards. The half-sheets may be loaded onto a card punch machine which aligns the sheets to a die (x and y axes) using predetermined alignment marks visible to the optics of the machine. The half-sheets may be then be fed under the punch in seven steps. Particularly, a fixed distance feed may be followed by another optic sensor search to stop the feed at the pre-printed alignment mark, then the machine punches a row of four cards out at one time. After die cutting and finishing according to standard processing, the IR reflection properties may be verified in-line (step 185) before application of the holographic foil 15.
With respect to the application of an exemplary holographic foil, the holographic foil 15 is adhered to card 5 (step 190) by any suitable method. In an exemplary embodiment, a substantially square steel die, which is about 1�″�1�″ with rounded corners and a 0.0007″ crown across the contacting surface, stamps out the individual foils 15 from a large sheet of holographic foil 15. The die is part of a hot stamp machine such that the die is sent through a sheet of foil 15, cutting the foil 15 around a particular image and immediately applying the foil 15 with heat to the front 10 surface of card 5 after the card has been laminated. The die temperature may be in the range of about 300 F.�+/−10 F.�. The dwell time is approximately � seconds and the application speed is set based upon the individual hot stamp applicator; however, the foregoing temperature and dwell is identified for a speed of 100 cards per minute. U.S. Pat. Nos. 4,206,965; 4,421,380; 4,589,686; and 4,717,221 by Stephen P. McGrew provide more details about hot stamping of a holographic image and are hereby incorporated by reference.
With respect to the holographic foil 15, the foil 15 may be any color, contain any hologram, may be applied to any location on card 5, and may be cut to any size, shape and thickness. In an exemplary embodiment, the holographic foil 15 sheet includes a gray adhesive on the bottom side and a blue, mirror-like, three-dimensional holographic surface on the top side containing numerous holographic images about 1�″�1�″ each. The exemplary hologram includes a 360 degree viewability and diffracts a rainbow of colors under white light. The full color hologram is created by, for example, American Banknote Holographics.
The corners of the individual foil 15 may berounded to minimize the likelihood that the foil 15 will peal away from the surface of card 5. Moreover, when applied to the card, the blue holographic surface faces away from card 5 while the gray adhesive side is applied to card 5 surface. The top surface of the holographic foil 15 may be created by any suitable method such as reflection holographics, transmission holographics, chemical washing, the incorporation of mirror compounds and/or any combination thereof. The holographic foil 15 may be fabricated by, for example, American Banknote Holographics, Inc. located at 1448 County Line Road, Huntingdon Valley, Pa., 19006.
In an exemplary embodiment, the sheets of holographic foil 15 are transmission holograms suitably created by interfering two or more beams of converging light, namely an object beam and reference beam, from a 20 watt Argon laser at 457.9 nm, onto a positive photoemulsion (spun coat plates using shiply photoresist). The system records the interference pattern produced by the interfering beams of light using, for example, a 303A developer. The object beam is a coherent beam reflected from, or transmitted through, the object to be recorded which may be a three-dimensional mirror. The reference beam may be a coherent, collimated light beam with a spherical wave front 10.
The incorporation of the holographic foil 15 onto a transaction card 5 provides a more reliable method of determining the authenticity of the transaction card 5 in ordinary white light, namely by observing if the hologram has the illusion of depth and changing colors. Thus, to allow the hologram to be viewed with ordinary, white light, when the hologram is recorded onto the transaction card 5, the image to be recorded is placed near the surface of the substrate. Moreover, the hologram is be embossed on a metalized carrier, such as the holographic foil 15, or alternatively the hologram may be cast directly onto the transparent plastic material. When formed on the clear plastic material, the hologram is made visible by the deposit of a visible substance over the embossed hologram, such as a metal or ink. More information regarding the production of holograms on charge cards 5 or the production of holographic foil 15 may be found in, for example, U.S. Pat. No. 4,684,795 issued on Aug. 4, 1987 to United States Banknote Company of New York or from the American Banknote Holographics, Inc. web site at www.abnh.com, both of which are herein incorporated by reference.
In an exemplary embodiment, the application of holographic foil onto vinyl credit cards is accomplished by using a metallized credit card foil. The foil is un-sized, metallized, embossable, abrasion, and chemical resistant hot stamping foil on a 1.0 mil (92 gauge) polyester carrier. All of the exemplary materials are tinted with raw materials supplier color code #563 (blue). The foil is vacuum metallized with aluminum and has an optical density range of about 1.60 to 2.00. The optimum foil is free of visible defects and particulate matter. The foil contains release characteristics of about 0 to 7 grams based upon a release testing unit having a die face of 300 F degrees, 80 psi, 1.0 seconds dwell, 0.1 seconds delay in the removal of the carrier at a 45 degree angle. An exemplary base material is capable of receiving a permanent, high fidelity (based upon an embossing die of 100%, having at least 70% diffraction efficiency) impression of the holographic image surface by embossing with a hard nickel die in the range of about 1600 pounds per linear inch at about 100 pounds air pressure and in the range of about 200 to 350 F degrees die temperatures. When testing the embossibility of the base material, the testing includes a primary and secondary image to assure the embossable coating is capable of producing an optimal secondary image.
The final exemplary product is slit at a width of 1 53/64″+/− 1/64″ and length of 10,000 images per roll. The registration block is located no more than about 5/64″ from the edge of the slit material. All finished rolls are wound with the metal side facing in on a 3.0″ ID core with a maximum of 3 splices permitted per finished reel and the registration blocks are 0.125″�0.125″ square.
After stamping out the individual cards 5 and applying the holographic foil, the IC chip 20 is applied to card 5 (step 195) by any suitable method, such as adhesive, heat, tape, groove and/or the like. More particularly, a small portion of the front 10 of card 5 is machined out using, for example, a milling process. The milling step removes about 0.02 mils of plastic from the front 10 surface, such that the routed hole cuts into the two core layers of plastic, but does not go through the last outer laminate layer of plastic, thereby forming a 5235HST pocket. IC chip 20 is a 5235 palladium plated with silver, rather than the standard gold plating. IC chip 20 is applied to the card using a process known as “potting”. Any suitable adhesive, such as a non-conductive adhesive, is placed into the machined hole and the IC chip 20 is placed over the adhesive such that the top surface of the IC chip 20 is substantially even with the front 10 surface of card 5. Suitable pressure and heat is applied to the IC chip 20 to ensure that the IC chip 20 is sufficiently affixed to card 5. The IC chip 20 is any suitable integrated circuit located anywhere on card 5. In an exemplary embodiment, the IC chip 20 structure, design, function and placement conforms to ISO standards for IC chips 20 and smart cards 5. The IC chip 20 may be obtained from, for example, Siemens of Germany.
After applying the holographic foil 15 and the IC chip 20 to card 5, certain information, such as account number 35 and “active thru” 32 date (not shown), may be embossed into card 5 (step 200) by known embossing methods. The embossing may be completed by, for example, Oberthur Card Systems. Although any information may be embossed anywhere on card 5, in a particularly exemplary embodiment, the account numbers 35 are embossed through the holographic foil 15 to reduce the possibility of the transfer of the holographic foil 15 to a counterfeit card 5 for fraudulent use. Additionally, although prior art cards 5 include a beginning and ending validity date, the present card 5 only includes an “active thru” 32 date, namely a date in which the card expires.
Benefits, other advantages, and solutions to problems have been described herein with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any element(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as critical, required, or essential features or elements of any or all the claims or the invention. It should be understood that the detailed description and specific examples, indicating exemplary embodiments of the invention, are given for purposes of illustration only and not as limitations. Many changes and modifications within the scope of the instant invention may be made without departing from the spirit thereof, and the invention includes all such modifications. Corresponding structures, materials, acts, and equivalents of all elements in the claims below are intended to include any structure, material, or acts for performing the functions in combination with other claim elements as specifically claimed. The scope of the invention should be determined by the appended claims and their legal equivalents, rather than by the examples given above. Reference to an element in the singular is not intended to mean “one and only one” unless explicitly so stated, but rather “one or more.” Moreover, where a phrase similar to ‘at least one of A, B, and C’ is used in the claims, it is intended that the phrase be interpreted to mean that A alone may be present in an embodiment, B alone may be present in an embodiment, C alone may be present in an embodiment, or that any combination of the elements A, B and C may be present in a single embodiment; for example, A and B, A and C, B and C, or A and B and C. Although the invention has been described as a method, it is contemplated that it may be embodied as computer program instructions on a tangible computer-readable carrier, such as a magnetic or optical memory or a magnetic or optical disk. All structural, chemical, and functional equivalents to the elements of the above-described exemplary embodiments that are known to those of ordinary skill in the art are expressly incorporated herein by reference and are intended to be encompassed by the present claims. Moreover, it is not necessary for a device or method to address each and every problem sought to be solved by the present invention, for it to be encompassed by the present claims. Furthermore, no element, component, or method step in the present disclosure is intended to be dedicated to the public regardless of whether the element, component, or method step is explicitly recited in the claims. No claim element herein is to be construed under the provisions of 35 U.S.C. 112, sixth paragraph, unless the element is expressly recited using the phrase “means for.” As used herein, the terms “comprises”, “comprising”, or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. The present invention has been described above with reference to an exemplary embodiment. However, those skilled in the art having read this disclosure will recognize that changes and modifications may be made to the exemplary embodiment without departing from the scope of the present invention. For example, various steps of the invention may be eliminated without altering the effectiveness of the invention. Moreover, other types of card fabrication, encoding and printing methods may be used such as dye sublimation retransfer technology and/or double transfer technology developed by Dai Nippon Printing Company of Japan. These and other changes or modifications are intended to be included within the scope of the present invention, as expressed in the following claims.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS3536894Jul 23, 1965Oct 27, 1970Jerry E TravioliElectronic credit card acceptorUS3553435Nov 21, 1966Jan 5, 1971Data Pathing IncPhotoelectric punched card and document readerUS3566120Sep 25, 1968Feb 23, 1971American Cyanamid CoMethod of coded data storage by means of coded inks in which the code components have particular absorption bands in the infraredUS3573731Jun 17, 1968Apr 6, 1971Clary CorpDevice for determining authenticity of a credit card or the likeUS3725647Oct 19, 1970Apr 3, 1973Insta Datic CorpPhotographic credit card systemUS3763356May 17, 1971Oct 2, 1973Pitney Bowes AlpexUnidirectional fluorescent ink imprinted coded document and method of decodingUS3829662Oct 12, 1972Aug 13, 1974Canon KkRecording medium having concealed information as input for electronic computerUS3836754Sep 18, 1972Sep 17, 1974Toye FCoded card employing differential translucenciesUS3838252Feb 22, 1972Sep 24, 1974Pitney Bowes IncProtective coatings for magnetically codable credit cardUS3873813May 18, 1973Mar 25, 1975Xerox CorpCredit cardUS3894756Jul 27, 1973Jul 15, 1975Optronics IntIdentification card having a reference beam coded hologramUS3919447Mar 20, 1974Nov 11, 1975IbmSpectral differential coded cardUS3922430Oct 18, 1973Nov 25, 1975Kuhns Roberta BData bearing card having an aesthetic, magnetizable, colorless, transparent coating thereonUS3955295Aug 1, 1975May 11, 1976Roberta B. KuhnsData bearing card having an aesthetic, magnetizable, colorless, transparent coating thereonUS3987725Mar 18, 1974Oct 26, 1976Transaction Technology, Inc.Process of screen manufacture and use for coding credit cardsUS4044231May 27, 1975Aug 23, 1977Addressograph Multigraph CorporationSecure property document and method of manufactureUS4058839Sep 3, 1974Nov 15, 1977R. D. Products, Inc.Magnetic-type information card and method and apparatus for encoding and readingUS4106857Aug 9, 1976Aug 15, 1978Better Environmental Development CorporationOptical filtersUS4119361Aug 9, 1976Oct 10, 1978Landis & GyrMultilayer identification cardUS4202491Sep 26, 1977May 13, 1980Hitachi, Ltd.Data cardUS4361757Jan 12, 1981Nov 30, 1982Zeag Systems AgCard-like data carrierUS4436991Mar 10, 1982Mar 13, 1984Sealectro CorporationBadge reader using infrared lightUS4504084Jan 30, 1984Mar 12, 1985Sodeco-Saia AgDocuments containing information invisible to the naked eyeUS4519155Aug 17, 1981May 28, 1985American Bank Note CompanyIdentification cardUS4538059Sep 13, 1982Aug 27, 1985Itr International Time LimitedIdentification card with concealed coding and a simple reader module to decode itUS4544836Dec 22, 1982Oct 1, 1985American District Telegraph CompanyOptically-based access control systemUS4547002Nov 10, 1983Oct 15, 1985U.S. Banknote CorporationCredit and identification cards having pieces of diffraction grating thereinUS4563024Mar 16, 1983Jan 7, 1986Jeffrey BlythHologram identification deviceUS4583766May 8, 1984Apr 22, 1986Kenneth R. WesselSecure badge for infrared badge reader and process for making sameUS4593936Mar 6, 1984Jun 10, 1986Opel George EUniversal credit cardUS4597814Sep 23, 1985Jul 1, 1986U.S. Banknote CorporationMethod for manufacturing card with three-dimensional label incorporated thereinUS4641017Dec 15, 1983Feb 3, 1987Herman LopataFraud resistant credit card systemUS4672021Jun 3, 1985Jun 9, 1987Fairmount Chemical CompanyContrast enhancement layer composition with naphthoquinone diazide, indicator dye and polymeric binderUS4684795Jan 7, 1985Aug 4, 1987United States Banknote Company L.P.Security tape with integrated hologram and magnetic stripUS4692394Jan 22, 1985Sep 8, 1987Drexler Technology CorporationMethod of forming a personal information cardUS4694148Jul 5, 1985Sep 15, 1987MIDS Magnetische Informations-und Daten-Systeme GmbHAccess cardUS4697073Feb 24, 1986Sep 29, 1987Casio Computer Co., Ltd.IC cardUS4711690Dec 18, 1985Dec 8, 1987Gao Gesellschaft Fur Automation Und Organisation MbhMethod for making an identification card having features for testing in incident and transmitted lightUS4779898Aug 21, 1987Oct 25, 1988Optical Coating Laboratory, Inc.Thin film optically variable article and method having gold to green color shift for currency authenticationUS4794142Aug 10, 1987Dec 27, 1988Bayer AktiengesellschaftUse of special ethylene-vinyl acetate-copolymers for the modification of PVCUS4795894Aug 29, 1986Jan 3, 1989Harue SugimotoVisiting card marked with discriminating symbols and a method of and an apparatus for reading what is printed on said visiting cardUS4837134Apr 16, 1987Jun 6, 1989Drexler Technology CorporationOptical memory card with versatile storage mediumUS4852911Nov 12, 1987Aug 1, 1989Gao Gesellschaft Fur Automation Und Organisation MbhIdentification card having a magnetic track covered by color and methods for producing itUS4863819Jun 22, 1988Sep 5, 1989Drexler Technology CorporationRead-only optical data cardUS4889366Jun 29, 1987Dec 26, 1989Bruno FabbianiSecurity documentUS4945215Oct 14, 1987Jul 31, 1990Kyodo Printing Co., Ltd.Optical recording card having hologram contained therein and method of producing the sameUS4950877Feb 5, 1988Aug 21, 1990Canon Kabushiki KaishaApparatus for transporting card-like information recording mediumUS5005873Apr 7, 1987Apr 9, 1991West Michael AMarking of articlesUS5010243Apr 14, 1989Apr 23, 1991Kyodo Printing Co., Ltd.Method of producing an optical recording card having a hologram contained thereinUS5106125Nov 26, 1990Apr 21, 1992Landis & Gyr Betriebs AgArrangement to improve forgery protection of credit documentsUS5111033Sep 6, 1991May 5, 1992Kyodo Printing Co., Ltd.Optical cardUS5142383Apr 1, 1991Aug 25, 1992American Banknote Holographics, Inc.Holograms with discontinuous metallization including alpha-numeric shapesUS5217844Apr 30, 1988Jun 8, 1993Kyodo Printing Co., Ltd.Optical recording medium, method of producing the same and method of producing the optical recording cardUS5241165Mar 3, 1989Aug 31, 1993Drexler Technology CorporationErasable optical wallet-size data cardUS5251937Sep 25, 1991Oct 12, 1993Gao Gesellschaft Fuer Automation Und Organisation MbhMultilayer data carrier and a method for producing itUS5256473Sep 23, 1991Oct 26, 1993Sumitomo Chemical Company, LimitedInfrared absorbing film improved in transparencyUS5272326Nov 16, 1992Dec 21, 1993Kyodo Printing Co., Ltd.Optical card having light absorbing layerUS5300764Jan 27, 1992Apr 5, 1994Nhk Spring Company, Ltd.Transparent optical identification label with infrared directivityUS5304789Oct 15, 1991Apr 19, 1994Gesellschaft Fur Automation Und Organisation Mbh(Gao)Multilayer card-shaped data carrier and method for producing sameUS5351142Apr 16, 1993Sep 27, 1994Crown Roll Leaf, Inc.Semi-transparent reflective layer for a phase hologramUS5355411Aug 14, 1991Oct 11, 1994Macdonald John LDocument security systemUS5383687Feb 12, 1993Jan 24, 1995Leonhard Kurz Gmbh & Co.Value document and embossing foil for the production thereofUS5407893Aug 19, 1993Apr 18, 1995Konica CorporationMaterial for making identification cardsUS5410142Mar 10, 1993Apr 25, 1995Omron CorporationOptical card with printing visible below the optical recordingUS5434404Oct 11, 1991Jul 18, 1995Verifone, Inc.Linear scanner apparatus for communicating with a data cardUS5514860Oct 3, 1994May 7, 1996Pitney Bowes Inc.Document authentication system utilizing a transparent labelUS5516153Feb 21, 1995May 14, 1996Gao Gesellschaft Fur Automation Und Organisation MbhSecurity document and a method for producing itUS5518810Jun 30, 1994May 21, 1996Mitsubishi Materials CorporationInfrared ray cutoff material and infrared cutoff powder use for sameUS5608203Jan 3, 1996Mar 4, 1997Finkelstein; AlanCredit card with magnifying lensUS5611965Aug 28, 1995Mar 18, 1997Kureha Kagaku Kogyo Kabushiki KaishaPlastic optical filterUS5614289Aug 24, 1994Mar 25, 1997Konica CorporationID cardUS5697649May 11, 1995Dec 16, 1997Crane & Co., Inc.Articles employing a magnetic security featureUS5700037Jan 16, 1996Dec 23, 1997Keller; John A.Security improved cardUS5705101Dec 18, 1995Jan 6, 1998Mitsui Toatsu Chemicals, Inc.Near infrared absorber, preparation process therefor and use thereofUS5720500Jan 16, 1996Feb 24, 1998Dai Nippon Printing Co., Ltd.Plastic card provided with magnetic stripeUS5786587Aug 5, 1996Jul 28, 1998American Bank Note Holographics, Inc.Enhancement of chip card securityUS5789733Sep 20, 1996Aug 4, 1998Motorola, Inc.Smart card with contactless optical interfaceUS5808758Dec 26, 1995Sep 15, 1998Geisecke & Devrient, GmbhData carrier with an optically variable elementUS5856048Jul 26, 1993Jan 5, 1999Dai Nippon Printing Co., Ltd.Information-recorded media and methods for reading the informationUS5856661Nov 27, 1996Jan 5, 1999Universal Magnifier LlcCredit card with magnifying lens formed with a radiation-curable resinUS5857709Feb 24, 1997Jan 12, 1999Chock; Ernest P.Anticounterfeit documentation with see-through and write-able hologramUS5882774Mar 10, 1995Mar 16, 1999Minnesota Mining And Manufacturing CompanyOptical filmUS5900954Jun 7, 1995May 4, 1999Symbol Technologies, Inc.Machine readable record carrier with hologramUS5928788Oct 17, 1995Jul 27, 1999Giesecke & Devrient GmbhData carrier with layers of modified PETUS5932870Mar 11, 1996Aug 3, 1999Pitney Bowes Inc.Documents containing a magnetic strip with a bar code affixed theretoUS5971276Feb 7, 1997Oct 26, 1999Kabushiki Kaisha ToshibaMethod of reading pattern and optical signal readerUS5978348Dec 18, 1996Nov 2, 1999Canon Kabushiki KaishaOptical recording medium and process for production thereofUS6019284Mar 17, 1998Feb 1, 2000Viztec Inc.Flexible chip card with displayUS6045894Jan 13, 1998Apr 4, 20003M Innovative Properties CompanyClear to colored security filmUS6049419Jan 13, 1998Apr 11, 20003M Innovative Properties CoMultilayer infrared reflecting optical bodyUS6074726May 27, 1997Jun 13, 2000Vezinet; AlainSecurity card with optical traceUS6138913Nov 5, 1997Oct 31, 2000Isotag Technology, Inc.Security document and method using invisible coded markingsUS6155168Dec 20, 1999Dec 5, 2000Alps Electric Co., Ltd.Information recording medium and information recording method suitable for security purposesUS6186398Nov 14, 1997Feb 13, 2001Dai Nippon Printing Co., Ltd.Magnetic cardUS6196465Jan 31, 1997Mar 6, 2001Tokyo Mechatoronics Co., Ltd.Capacitive data card and reader thereofUS6248314Jul 2, 1999Jun 19, 2001Kao CorporationHair dye composition having a particular buffer capacity and containing an alkylene carbonateUS6255031Apr 16, 1997Jul 3, 2001Kanebo, Ltd.Near infrared absorbing film, and multi-layered panel comprising the filmUS6277232Apr 22, 1999Aug 21, 2001Mbna America Bank, N.A.Method of manufacturing a plastic card with a lenticular lens thereinUS6290137Oct 1, 1999Sep 18, 2001Perfect Plastic Printing CorporationTransparent/translucent financial transaction card including an infrared light filterUS6296188Nov 24, 1999Oct 2, 2001Perfect Plastic Printing CorporationTransparent/translucent financial transaction card including an infrared light filterUS6391400Apr 8, 1998May 21, 2002Thomas A. RussellThermal control films suitable for use in glazingUS6581839Sep 1, 2000Jun 24, 2003American Express Travel Related Services Company, Inc.Transaction cardUS6749123Jan 31, 2002Jun 15, 2004American Express Travel Related Services Company, Inc.Transaction cardUS6764014Mar 7, 2002Jul 20, 2004American Express Travel Related Services Company, Inc.Transaction cardUS20020066790Dec 1, 2000Jun 6, 2002Mikael CoccoDevice, system and method for conducting a transaction using a translucent, transparent or semitransparent transaction cardUS20020130186Mar 7, 2002Sep 19, 2002Ellen LaschTransaction cardUS20020145049Jan 31, 2002Oct 10, 2002Ellen LaschTransaction cardUS20030017312Nov 28, 2001Jan 23, 2003Laurent LabrousseTransparent and/or translucent card with three-dimensional graphicsUS20030047615Sep 7, 2001Mar 13, 2003Colorado Plasticard, Inc.Transparent transaction card and method for making a transparent transaction cardUS20030141373Nov 22, 2002Jul 31, 2003Ellen LaschTransaction card with dual IC chipsUS20040020992Mar 21, 2003Feb 5, 2004Ellen LaschTransaction cardUS20040046034Jul 9, 2001Mar 11, 2004Hayat Ey YamaniTransparent data cardUS20040201009Apr 1, 2004Oct 14, 2004National Taiwan UniversityInfrared photodetectorUS20040251451Dec 9, 2002Dec 16, 2004Detlef BurgardLacquer layer, which reflects infra-red radiationUS20050207002May 20, 2005Sep 22, 20053M Innovative Properties CompanyMultilayer infrared reflecting film with high and smooth transmission in visible wavelength region and laminate articles made therefromUSD61466Feb 14, 1921Sep 12, 1922 Design fob a business cakixUSD270546Mar 10, 1981Sep 13, 1983Ab Id-KortTransaction identification cardUSD270548Mar 31, 1981Sep 13, 1983Scan-Globe A/SSupport stand for a globeUSD280214Apr 7, 1983Aug 20, 1985 Credit cardUSD310386Aug 7, 1987Sep 4, 1990Visa International Service AssociationTransaction cardUSD384971Aug 28, 1996Oct 14, 1997Transaction Technology, Inc.Smart card with chip bearing a source identifierUSD406861Jun 25, 1998Mar 16, 1999Retail Royalty CompanyPartially transparent card with opaque machine-readable and signature-receiving stripesUSD408054Jul 2, 1997Apr 13, 1999Retail Royalty CompanyPartially transparent card with opaque machine-readable and signature-receiving stripesUSD436620Sep 1, 1999Jan 23, 2001American Express Travel Related Services Company, Inc.Transparent card with a machine readable stripe, IC chip and ornamental rectangleUSD438563Sep 1, 1999Mar 6, 2001American Express Travel Related Services Company, Inc.Transparent card with an opacity gradientAT80091B Title not availableAT171672B Title not availableCA1228225A1Nov 9, 1984Oct 20, 1987National Research Council Of CanadaMethod of manufacturing an optical interference authenticating deviceCA1328363COct 13, 1987Apr 12, 1994Yoichi FukushimaOptical recording card having hologram contained therein and method of producing the sameCH689680A5 Title not availableDE2847756A1Nov 3, 1978May 8, 1980Stockburger HVerfahren und vorrichtung zur geheimen kennzeichnung und auswertung maschinenlesbarer datentraegerDE3636921A1Oct 30, 1986May 5, 1988Interflex DatensystFaelschungssicherer optoelektrischer code-kartenleserDE3781502D1Oct 15, 1987Oct 8, 1992Kyodo Printing Co LtdOptische registrierkarte mit einem hologramm und verfahren zu deren herstellung.DE3941070C2Dec 8, 1989Sep 12, 1991Dirk 1000 Berlin De LehnartzTitle not availableDE19507144A1Mar 1, 1995Apr 25, 1996Giesecke & Devrient GmbhMehrschichtiger Datentr�ger mit Deckschichten aus modifiziertem PETDE59503783D1Oct 17, 1995Nov 5, 1998Giesecke & Devrient GmbhMehrschichtiger datentr�ger mit deckschichten aus modifiziertem petEP0181770A2Nov 7, 1985May 21, 1986Canadian Patents and Development Limited Soci�t� Canadienne des Brevets et d'Exploitation Limit�eA method of manufacturing an optical interference authenticating deviceEP0264277B1Oct 15, 1987Sep 2, 1992Kyodo Printing Co., Ltd.Optical recording card having hologram contained therein and method of producing the sameEP0343829A2May 16, 1989Nov 29, 1989Time And Data Systems International LimitedCard or badge for carrying data and reader thereforEP0354817B1Aug 11, 1989Jan 11, 1995Esselte Meto International GmbHBar code printingEP0368570A2Nov 2, 1989May 16, 1990Kyodo Printing Co., Ltd.Optical cardEP0388090B1Mar 9, 1990Mar 1, 1995THOMAS DE LA RUE &amp; COMPANY LIMITEDSheet with security deviceEP0403134A2Jun 4, 1990Dec 19, 1990British Technology Group LimitedHologramsEP0411602A2Aug 1, 1990Feb 6, 1991Omron CorporationObject having visible pattern including invisible information printed thereonEP0473998A2Aug 17, 1991Mar 11, 1992Eric BauerMethod of manufacturing a data card incorporating markings and a data card incorporating markings obtained by this methodEP0481388B1Oct 14, 1991Jun 18, 1997GAO Gesellschaft f�r Automation und Organisation mbHData storage medium in form of card with several layers and method for the productionEP0531605B1Jan 27, 1992Dec 16, 1998Nhk Spring Co.Ltd.Transparent optical identification labelEP0552047B1Jan 15, 1993Aug 21, 1996Hitachi Maxell Ltd.Infrared-absorbing mark printed matterEP0560318B1Mar 10, 1993Jul 29, 1998Omron CorporationOptical card and device to read sameEP0568185B1Mar 23, 1993Jul 12, 2000Nhk Spring Co.Ltd.System identifying the authenticity of an articleEP0657297B1Dec 10, 1993Jul 30, 1997AGFA-GEVAERT naamloze vennootschapSecurity document having a transparent or translucent support and containing interference pigments.EP0721850A2Jan 9, 1996Jul 17, 1996Thomas De La Rue LimitedSecurity documentEP0734322B1Oct 17, 1995Sep 30, 1998Giesecke &amp; Devrient GmbHMultilayered data carrier with coating layers of modified petEP0780839A2Dec 19, 1996Jun 25, 1997Canon Kabushiki KaishaOptical recording medium and process for production thereofEP0789316B1Feb 7, 1997Apr 27, 2005Kabushiki Kaisha ToshibaMethod of reading pattern and optical signal readerEP0843280B1Nov 18, 1997Feb 25, 2004Dai Nippon Printing Co., Ltd.Magnetic cardEP0854461B1Nov 13, 1997Oct 15, 2008Ncr International Inc.Self service terminal (SST) with maintenance featureEP0866420A2Mar 18, 1998Sep 23, 1998Time and Data Systems International LimitedIdentification card or badgeEP0894620B1Apr 16, 1997Jun 6, 2007Kanebo Trinity Holdings, Ltd.Near infrared ray absorption film and multi-layered panel including sameEP0916519A1Nov 6, 1998May 19, 1999Meiller Comcard GmbHPortable cardEP1222620B1Sep 5, 2000Nov 30, 2005American Express Travel Related Services Company Inc.Transparent transaction card with infrared blocking layerES548621D0 Title not availableES2121423T3 Title not availableES8704653A1 Title not availableGB1371254A Title not availableGB2086110B Title not availableGB2106832B Title not availableGB2108906B Title not availableGB2229189A Title not availableGB2240948A Title not availableJP1004934A Title not availableJP1307937A Title not availableJP2130737A Title not availableJP2252149A Title not availableJP5224000B2 Title not availableJP5254283B2 Title not availableJP6183187A Title not availableJP6234287A Title not availableJP6243774A Title not availableJP9274640A Title not availableJP9507266A Title not availableJP61130918A Title not availableJP62264999A Title not availableJP63071794A Title not availableJP63098689A Title not availableJP63175987A Title not availableJP2000177229A Title not availableNon-Patent CitationsReference1CA; Office Action dated Jul. 18, 2011 in Application No. 2,693,136.2EP; Decision dated Jul. 14, 2010 for Application No. 00961558.4.3European Examination Report for 00961558.4 dated Jun. 26, 2003.4Home Energy, Lighting Makeovers: The Best Is Not Always the Brightest (Nov./Dec. 1994).5IBM Technical Disclosure Bulletin, Infrared Transparent Credit Card (Dec. 1966).6International Search Report for PCT/US00/24371 mailed on Feb. 28, 2001.7International Search report for PCT/US2000/027004 mailed on Dec. 20, 2000.8IPRP for International Application No. PCT/US09/44075, dated Dec. 15, 2010.9ISO/IEC 10373-1993(E), p. 17, Section 5.14 "Light transmittance" (Prior Art).10ISR and Written Opinion for PCT/US2009/044075 dated Jul. 2, 2009.11Nilson Report Sep. 1999.12Non-Final Office Action for U.S. Appl. No. 12/062,489 mailed on Dec. 16, 2008.13Non-Final Office Action for U.S. Appl. No. 12/124,937 dated Mar. 10, 2011.14Non-Final Office Action for U.S. Appl. No. 12/124,937 dated Nov. 19, 2010.15Non-Final Office Action for U.S. Appl. No. 12/907,303 dated Feb. 11, 2011.16Notice of Allowance dated Jun. 1, 2011 for U.S. Appl. No. 12/907,303.17Notice of Allowance for U.S. Appl. No. 09/411,359 mailed on Jun. 20, 2001.18Notice of Allowance for U.S. Appl. No. 09/449,251 mailed on Jun. 20, 2001.19Notice of Allowance for U.S. Appl. No. 09/653,837 mailed on Nov. 27, 2002.20Notice of Allowance for U.S. Appl. No. 09/675,912 mailed on Nov. 26, 2003.21Notice of Allowance for U.S. Appl. No. 10/062,106 mailed on Jan. 2, 2004.22Notice of Allowance for U.S. Appl. No. 10/092,681 mailed on Feb. 2, 2004.23Notice of Allowance for U.S. Appl. No. 10/339,814 mailed on Nov. 12, 2003.24Notice of Allowance for U.S. Appl. No. 10/394,914 mailed on Mar. 19, 2008.25Notice of Allowance for U.S. Appl. No. 10/735,940 mailed on Aug. 12, 2005.26Optical Coatings Japan, Filters (2000), no month.27PCT; ISR and Written Opinion dated Jul. 2, 2009 Application No. PCT/US2009/044075.28PV-7A, Ultra Compact Color Camera (Date unknown).29Search Report for Application No. UAE/P/73/2002 dated Jan. 27, 2011.30Specimen of credit card offered for sale at least as early as Feb. 1974.31Sport Optics International, Premium Optics Serious Outdoorsmen (Date unknown).32The 1995 ISO/IEC 7810 standard for identification cards.33The 1997 working draft amended ISO/IEC 10373-1 test methods standard for identification cards.34The 1998 ISO/IEC 10373-1 test methods standard for identification cards.35The 1998 working draft amended ISO/IEC 7810 standard.36The Light Site Europe, Master Line ES (2000), no month.37Umaghan Instruments, The IRX Infrared Exclusion Filter (Jul. 31, 1999).38USPTO; Final Office Action dated May 25, 2010 in U.S. Appl. No. 12/062,489.39USPTO; Non-Final Office Action dated Apr. 19, 2010 in U.S. Appl. No. 12/418,510.40USPTO; Non-Final Office Action dated May 4, 2009 in U.S. Appl. No. 12/062,489.41USPTO; Non-Final Office Action dated Nov. 17, 2009 in U.S. Appl. No. 12/062,489.42USPTO; Notice of Allowance dated Aug. 27, 2010 in U.S. Appl. No. 12/418,510.43USPTO; Notice of Allowance dated Jul. 23, 2010 in U.S. Appl. No. 11/879,468.Referenced byCiting PatentFiling datePublication dateApplicantTitleUS8186598 *Sep 23, 2011May 29, 2012American Express Travel Related Services Company, Inc.Transaction cardUS8240574Sep 1, 2011Aug 14, 2012American Express Travel Related Services Company, Inc.Infrared blocking articleUS8931704May 11, 2012Jan 13, 2015Iii Holdings 1, LlcTransaction cardUS9165295May 9, 2011Oct 20, 2015Moon J. KimAutomated card information exchange pursuant to a commercial transactionUS9189723 *Jul 22, 2013Nov 17, 2015Moon J. KimLight-powered smart card for on-line transaction processingUS20120006902 *Jan 12, 2012American Express Travel Related Services Company, Inc.Transaction cardUS20140158761 *Jul 22, 2013Jun 12, 2014Moon J. KimLight-powered smart card for on-line transaction processing* Cited by examinerClassifications U.S. Classification235/487, 235/488, 235/491International ClassificationG06K19/00Cooperative ClassificationB42D25/00, B42D25/382, B42D2033/20, B41M3/14, B42D2033/30, B42D2033/04European ClassificationB41M3/14, B42D15/10Legal EventsDateCodeEventDescriptionJun 26, 2008ASAssignmentOwner name: AMERICAN EXPRESS TRAVEL RELATED SERVICES COMPANY,Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:FAENZA, WILLIAM J., JR.;REEL/FRAME:021157/0587Effective date: 20080521Mar 27, 2012CCCertificate of correctionApr 21, 2014ASAssignmentOwner name: III HOLDINGS 1, LLC, DELAWAREFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:AMERICAN EXPRESS TRAVEL RELATED SERVICES COMPANY, INC.;REEL/FRAME:032722/0746Effective date: 20140324Apr 24, 2015FPAYFee paymentYear of fee payment: 4RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services