US7922877B2 - Method and apparatus for plating a semiconductor package - Google Patents
Method and apparatus for plating a semiconductor package Download PDF
US7922877B2
US7922877B2 US12639269 US63926909A US7922877B2 US 7922877 B2 US7922877 B2 US 7922877B2 US 12639269 US12639269 US 12639269 US 63926909 A US63926909 A US 63926909A US 7922877 B2 US7922877 B2 US 7922877B2
US12639269
US20100140081A1 (en )
Chalermsak Sumithpibul
Apichart Phaowongsa
A method of plating a plurality of semiconductor devices includes: applying an electrical power source to an anode terminal and a cathode terminal; placing the plurality of semiconductor devices on a non-conductive platform in a plating solution; moving conductive parts across surfaces of the semiconductor devices to be plated, wherein the conductive parts electrically connect the surfaces of the semiconductor devices to the cathode; and wherein plating particles connected to the anode terminal move to and plate the surfaces of the semiconductor devices.
This application is a divisional application of U.S. application Ser. No. 12/128,828 filed on May 29, 2008, now U.S. Pat. No. 7,718,522 which claims priority from U.S. Provisional Application No. 60/940,824 filed on May 30, 2007, the disclosure of which is incorporated herein by reference.
Apparatuses and methods consistent with the present invention relate to a method of electro-plating a semiconductor packages. More particularly, the present invention relates to a apparatus and method of electro-plating singulated semiconductor packages by moving conductive parts and the singulated packages relative to each other.
One of the last steps in manufacturing certain types of semiconductor packages, such as QFN packages, is to plate the metal frame with a conductor, such as solder. One such conventional method is to electro-plate a metal, such as solder, to the frame. FIG. 1 is a schematic view of a conventional method of electro-plating a strip of semiconductor packages. The electro-plating apparatus includes a container 1 that is filled with a plating chemical 2, such as Methane Sulfonic acid. An electrical power source 3 is connected to an anode 3 a and a cathode 3 b. The anode 3 a is electrically connected to an anode plate 4 that contains solder particles. The cathode 3 b is electrically connected to a clipper and belt that is attached to the metal frame 6 of the semiconductor packages to be plated. The apparatus also includes a circulation pump and filter 7, which circulates the chemical in order to prevent chemical debris sediment.
When an electrical current is applied by the electrical power source through the anode 3 a and cathode 3 b to the anode plate 4 and metal frame 6, the solder particles on the anode plate move (as shown by item 8) through the plating chemical and become plated onto the metal frame (as shown by item 9).
FIG. 2 illustrates differences between the conventional strip of semiconductor packages and the strip of semiconductor packages that is used in an embodiment of the inventive method. FIG. 2A shows a portion of a metal strip frame 10 that contains rail bars 11, tie bars 12, terminals 13 and die attach pads 14. Each of the rail bars 11, tie bars 12, terminals 13 and die attach pads 14 are electrically connected. As a result, all of the metal surfaces can be plated by the conventional method.
FIG. 2 b shows what happens with individual semiconductor packages are singulated, or separated from each other. Specifically, the rail bars are cut. After singulation, the tie bars 12, terminals 13 and die attach pads 14 of each of the singulated packages are no longer electrically connected to the tie bars 12, terminals 13 and die attach pads 14 of the other singulated packages. As a result, because electric current can no longer flow through all of the metal parts, the parts cannot be electro plated.
While the conventional method works well for semiconductors packages on a strip, when the semiconductor packages are singulated prior to electro-plating, a new method is necessary. The need to electro-plate individual packages may arise when not all of the packages on a strip are properly plated during the conventional method. Rather than scrapping the unplated packages, they can be separated from the strip and plated in a separate process.
There is therefore a need to provide apparatuses and methods that can electro plate semiconductor packages that have been singulated.
In one embodiment a method of plating a plurality of semiconductor devices includes: applying an electrical power source to an anode terminal and a cathode terminal; placing the plurality of semiconductor devices on a non-conductive platform in a plating solution; moving conductive parts across surfaces of the semiconductor devices to be plated, wherein the conductive parts electrically connect the surfaces of the semiconductor devices to the cathode; and wherein plating particles connected to the anode terminal move to and plate the surfaces of the semiconductor devices.
In other embodiments of the above method, the plurality of semiconductor devices are not electrically connected, the conductive parts are shaped as one of spheres, cylinders, polyhedrons, brushes, pins, wheels and hairs, and/or the conductive parts move in a circular direction.
In another embodiment, a method of plating a plurality of semiconductor devices includes: applying an electrical power source to an anode terminal and a cathode terminal; placing the plurality of semiconductor devices on a non-conductive platform in a plating solution; moving surfaces of the semiconductor devices to be plated across conductive parts, wherein the conductive parts electrically connect the surfaces of the semiconductor devices to the cathode; and wherein plating particles connected to the anode terminal move to and plate the surfaces of the semiconductor devices.
In other embodiments of the above method, the plurality of semiconductor devices are not electrically connected and/or the conductive parts are shaped as one of brushes, pins, wheels and hairs.
In another embodiment, a method of plating a plurality of semiconductor devices includes: applying an electrical power source to an anode terminal and a cathode terminal; placing the plurality of semiconductor devices, which may or may not be electrically connected, on a non-conductive platform in a plating solution; moving conductive parts across surfaces of the semiconductor devices to be plated in a first direction, wherein the semiconductor parts are moving in direction opposite to the first direction, wherein the conductive parts electrically connect the surfaces of the semiconductor devices to the cathode; wherein plating particles connected to the anode terminal move to and plate the surfaces of said semiconductor devices.
In other embodiments of the above method, the conductive parts are shaped as one of spheres, cylinders, polyhedrons, brushes, pins, wheels and hairs, and/or the conductive parts move in a circular direction.
In another embodiment, an apparatus for plating a plurality of semiconductor devices includes: a container for holding a plating chemical; an electrical power source connected to an anode terminal and a cathode terminal; a container for holding plating particles connected to the anode terminal; a non-conductive platform for holding the plurality of semiconductor devices, which may or may not be electrically connected; and movable conductive parts that electrically connect surfaces of the semiconductor devices to be plated to the cathode terminal.
In other embodiments of the above apparatus, the apparatus also includes: a conductive enclosure, which may be a ring; a conductive plate; and a conductive support; wherein the conductive enclosure, the conductive plate and the conductive support are electrically connected to said cathode terminal and wherein the conductive enclosure provides the electrical connection between the movable conductive parts and the surfaces of the semiconductor devices to be plated to the cathode terminal.
In other embodiments of the above apparatus, the apparatus includes a stirrer that moves the conductive parts across the surfaces of said semiconductor devices, and/or the conductive parts may be shaped as one of spheres, cylinders, polyhedrons, brushes pins, wheels and hairs.
In another embodiment, an apparatus for plating a plurality of semiconductor devices includes: a container for holding a plating chemical; an electrical power source connected to an anode terminal and a cathode terminal; a container for holding plating particles connected to the anode terminal; a movable non-conductive platform for holding the plurality of semiconductor devices, which may or may not be electrically connected; and conductive parts that electrically connect surfaces of the semiconductor devices to be plated to said cathode terminal.
FIG. 1 illustrates a schematic view of a conventional method of electro-plating a strip of semiconductor packages.
FIG. 2 illustrates differences between the conventional strip of semiconductor packages and the strip of semiconductor packages used in an embodiment of the inventive method.
FIG. 3 illustrates a schematic view of an embodiment of the inventive method and apparatus.
FIG. 4 illustrates a top view of an embodiment of the inventive method and apparatus.
FIG. 5 illustrates a bottom view of an embodiment of the inventive method and apparatus.
FIG. 6 illustrates a partial side view of an embodiment of the inventive method and apparatus.
FIG. 7 illustrates a partial perspective view of an embodiment of the inventive method and apparatus.
FIG. 8 is a table of visual inspection test results of an embodiment of the inventive method.
FIG. 9 is a table of adhesion test results of an embodiment of the inventive method.
FIG. 10 is a table of solderability test conditions related to an embodiment of the inventive method.
FIG. 11 is a table of solderability test results of an embodiment of the inventive method.
FIG. 12 is a photograph of the unit related to an embodiment of the inventive method.
FIGS. 13 are 14 are photograph of whisker test results related to an embodiment of the inventive method.
FIGS. 15A and 15B illustrate partial top views of embodiments of the inventive method and apparatus.
FIG. 16 illustrates different embodiments of the conductive parts.
FIGS. 17 and 18 illustrate an alternate embodiment of a stirrer blade of the inventive method and apparatus.
FIG. 19 illustrates an alternate embodiment of a stirrer blade of the inventive method and apparatus.
FIGS. 3-6 illustrate schematic views of an embodiment of the inventive method and apparatus. The apparatus includes a container 20 that is filled with a plating chemical 21, such as Methane Sulfonic acid. The container 20 can be made of Poly Propylene. An electrical power source 22 is connected to an anode 22 a and a cathode 22 b. An example of an electrical power source 22 is a source that outputs 2-3 Volts with a current of approximately 15 Amperes. The anode 22 a is electrically connected to a metal basket 29 that contains metal particles, such as solder balls. The cathode 22 b is electrically connected to a conductive column 25. The conductive column 25 is electrically connected to a conductive bar 24, on which sits a conductive ring 31. Inside the conductive ring 31 and on top of the conductive bar 24 sits a non-conductive disk 34, which can be made of polyethylene. The apparatus also includes a circulation pump and filter 23, which circulates the chemical in order to prevent chemical debris sediment.
The apparatus also includes an agitator 26, which is connected to a buffer unit 28 by an agitator axle 27. The buffer unit 28 contains a stirrer blade 35 which is driven by the agitator 26, which acts as a stirrer. FIG. 4, which is a top view of an embodiment of the apparatus, shows singulated semiconductor packages 36 fixed on a fixture 34 by using, for example, UV tape to fix the unit to fixture 34 with the surface to be plated facing up. The fixture is placed on the non-conductive disk 34. A plurality of conductive parts are then placed inside the conductive ring and on top of the singulated semiconductor packages 36. Typically, enough conductive parts are used so that there are no gaps along the length of stirrer blade 35.
Next, the operation of the apparatus will be described. First, the agitator 26 is turned on, which causes stirrer blade 35 to rotate in direction 33 inside the conductive ring 31 at a rate of approximately 15-20 RPM. The rotating stirrer blade 35 equally spreads the conductive parts 32 over the singulated semiconductor packages. As the conductive parts 32 move about inside the conductive ring 31, they are in electrical contact with both the conductive ring 31 and the metal surfaces of the singulated semiconductor packages. As a result, after the electrical power source 22 is turned on, electrical current is applied by the electrical power source through the cathode 22 b, conductive column 25, conductive bar 24, conductive ring 31 and conductive parts to the metal surfaces of the singulated semiconductor packages. The electrical power source 22 also applies electrical current through the anode 22 a to the metal baskets 29 that contain metal particles, such as solder balls. The metal particles in the metal baskets then move through the plating chemical and become plated onto the metal surfaces of the singulated semiconductor packages.
FIGS. 6 and 7 show other views of how the conductive parts 32 are used in the embodiment. In order to create a uniform plating result, the conductive parts 32 are spread out evenly on the singulated units. The conductive parts 32 conduct the electric current over the plating area which behaves as the cathode. The metal particles, which are driven by an electric field, travel from the metal baskets 29 (anode) to the cathode plating area.
Numerous reliability tests were performed to test the plating method. The results, discussed below, demonstrated that the plating method was just as reliable as conventional plating methods.
FIG. 8 is a table of visual inspection test results of the inventive method. Five lots were inspected, and none were rejected.
FIG. 9 is a table of adhesion test results of the inventive method. Again, five lots were tested, and none were rejected.
FIG. 10 is a table of solderability test conditions that were used to test the inventive method. FIG. 11 is a table of the solderability test results that were obtained. Five lots were inspected, and none were rejected.
FIG. 12 is a photograph of the completed unit related to an embodiment of the inventive method.
FIGS. 13 are 14 are photograph of whisker test results related to an embodiment of the inventive method. A whisker is a defect that can occur during a solder electroplating process.
The embodiment shown in FIGS. 3-7 are only one example of the inventive method. For example, the conductive parts, which are shown as spheres in FIG. 3-7, could also be shaped as cylinders, polyhedrons, etc., or a combination thereof, as shown for example in FIG. 16. In addition, the conductive parts could be hairs, pins, brushes, wheels, etc. that are attached to the stirrer blade. For example FIGS. 17 and 18 which show a brush-like stirrer blade 35 with hairs/pins 37. In addition, different types of conductive parts can used together. For example, FIG. 19 shows a brush-like stirrer blade 35/37 used in combination with conductive spheres 32.
In another embodiment of the inventive method and apparatus, the stirrer blade and conductive parts can remain stationary while the semiconductor packages rotate as shown in FIG. 15A. For example, conductive ring 31 would be attached to the non-conductive disk 34, on which the semiconductor packages 36 are fixed. The agitator would then be attached to conductive ring 31. The agitator would then rotate conductive ring 31, non-conductive disk 34 and semiconductor packages 36 together.
In another embodiment of the inventive method and apparatus, both the stirrer blade/conductive parts and semiconductor packages move, as shown for example in FIG. 15B. This embodiment would require an additional agitator that is attached to conductive ring 31. Also, like the previous embodiment, conductive ring 31 would be attached to the non-conductive disk 34, on which the semiconductor packages 36 are fixed.
1. An apparatus for plating a plurality of semiconductor devices comprising:
a container for holding a plating chemical;
an electrical power source connected to an anode terminal and a cathode terminal;
a container for holding plating particles connected to said anode terminal;
a non-conductive platform for holding said plurality of semiconductor devices; and
movable conductive parts that electrically connect surfaces of said semiconductor devices to be plated to said cathode terminal.
wherein said conductive enclosure, said conductive plate and said conductive support are electrically connected to said cathode terminal and
wherein said conductive enclosure provides said electrical connection between said movable conductive parts and said surfaces of said semiconductor devices to be plated to said cathode terminal.
3. The apparatus of claim 2, wherein said conductive enclosure is a ring.
a stirrer that moves said conductive parts across said surfaces of said semiconductor devices.
5. The apparatus of claim 2, wherein said conductive parts are shaped as one of spheres, cylinders, polyhedrons, brushes pins, and hairs.
6. The apparatus of claim 1, wherein said plurality of semiconductor devices are not electrically connected.
7. An apparatus for plating a plurality of semiconductor devices comprising:
a movable non-conductive platform for holding said plurality of semiconductor devices; and
conductive parts that electrically connect surfaces of said semiconductor devices to be plated to said cathode terminal.
8. The apparatus of claim 7, wherein said plurality of semiconductor devices are not electrically connected.
US12639269 2007-05-30 2009-12-16 Method and apparatus for plating a semiconductor package Active US7922877B2 (en)
US94082407 true 2007-05-30 2007-05-30
US12128828 US7718522B2 (en) 2007-05-30 2008-05-29 Method and apparatus for plating a semiconductor package
US12639269 US7922877B2 (en) 2007-05-30 2009-12-16 Method and apparatus for plating a semiconductor package
US12128828 Division US7718522B2 (en) 2007-05-30 2008-05-29 Method and apparatus for plating a semiconductor package
US20100140081A1 true US20100140081A1 (en) 2010-06-10
US7922877B2 true US7922877B2 (en) 2011-04-12
ID=40088781
US12128828 Active 2028-09-12 US7718522B2 (en) 2007-05-30 2008-05-29 Method and apparatus for plating a semiconductor package
US12639269 Active US7922877B2 (en) 2007-05-30 2009-12-16 Method and apparatus for plating a semiconductor package
US (2) US7718522B2 (en)
US5441620A (en) * 1993-02-10 1995-08-15 Yamaha Corporation Electroplating apparatus
US20100140081A1 (en) 2010-06-10 application
US20080299756A1 (en) 2008-12-04 application
US7718522B2 (en) 2010-05-18 grant
US6413404B1 (en) 2002-07-02 Method of forming bumps by electroplating
US3579816A (en) 1971-05-25 Method of producing semiconductor devices
Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE TO INCLUDE US PATENT NUMBER 7922877 IN THE COVER SHEET PREVIOUSLY RECORDED ON REEL 044403 FRAME 0596. ASSIGNOR(S) HEREBY CONFIRMS THE ASSIGNMENT;ASSIGNOR:UTAC THAI LIMITED;REEL/FRAME:044907/0116