Patent US7175689 - Process for producing a lightweight molded part and molded part made of ... - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign inPatentsA process for producing a lightweight molded part, comprising introducing a gas into a particle-containing, molten metal to produce a metal foam having voids with a monomodal distribution of their dimensions, introducing the metal foam into a casting die and compressing it therein essentially under all-round...http://www.google.com/patents/US7175689?utm_source=gb-gplus-sharePatent US7175689 - Process for producing a lightweight molded part and molded part made of metal foamAdvanced Patent SearchPublication numberUS7175689 B2Publication typeGrantApplication numberUS 10/170,684Publication dateFeb 13, 2007Filing dateJun 14, 2002Priority dateJun 15, 2001Fee statusPaidAlso published asUS7195662, US20030005793, US20030047036, US20070079909Publication number10170684, 170684, US 7175689 B2, US 7175689B2, US-B2-7175689, US7175689 B2, US7175689B2InventorsFranz Dobesberger, Herbert Flankl, Dietmar Leitlmeier, Alois Birgmann, Peter SchulzOriginal AssigneeHuette Klein-Reichenbach Gesellschaft MbhExport CitationBiBTeX, EndNote, RefManPatent Citations (15), Non-Patent Citations (6), Referenced by (5), Classifications (16), Legal Events (3) External Links: USPTO, USPTO Assignment, EspacenetProcess for producing a lightweight molded part and molded part made of metal foam
US 7175689 B2Abstract
A process for producing a lightweight molded part, comprising introducing a gas into a particle-containing, molten metal to produce a metal foam having voids with a monomodal distribution of their dimensions, introducing the metal foam into a casting die and compressing it therein essentially under all-round pressure; and the molded part made by this process.
1. A process for producing a lightweight molded part, comprising (a) introducing a gas into a particle-containing, molten metal to produce a free-flowing metal foam having voids therein, said voids having a monomodal distribution of their dimensions, (b) at least partially introducing the metal foam into a casting die and compressing it therein under essentially all-round pressure, and (c) allowing the liquid phase to solidify.
2. The process of claim 1, wherein the gas is introduced through at least one feed pipe which projects inwardly into the molten metal.
3. The process of claim 2, wherein the gas comprises a mixture of at least two gases.
4. The process of claim 1, wherein the casting die has interior dimensions corresponding to desired dimensions of the molded part.
5. The process of claim 1, wherein compressing the metal foam results in walls of metal enclosing the voids having planar areas in at least parts thereof.
6. The process of claim 1, wherein in the solidified metal foam a proportionate maximum longitudinal extension of the voids is in the range of 1 to 30 mm.
7. The process of claim 6, wherein a ratio of maximum longitudinal extensions of two different voids for at least 20 pairs on the average is lower than 45.
8. The process of claim 7, wherein said ratio is lower than 15.
9. The process of claim 1, wherein the metal comprises a light metal.
10. The process of claim 1, wherein the metal comprises at least one of aluminum and an aluminum alloy.
11. The process of claim 9, wherein the particles comprise particles of SiC, Al2O3, intermetallic phases and mixtures thereof.
12. The process of claim 1, wherein the particles have a size of 1 to 50 μm.
13. The process of claim 11, wherein the particles have a size of 3 to 20 μm.
14. The process of claim 1, wherein a volume fraction of the particles in the metal is 10 vol % to 50 vol %.
15. The process of claim 13, wherein a volume fraction of the particles in the metal is 15 vol % to 30 vol %.
16. The process of claim 1, wherein the metal foam has a density of less than 1.05 g/cm3.
17. The process of claim 16, wherein the metal foam has a density of less than 0.7 gg/cm3 Description
The present application claims priority under 35 U.S.C. �119 of Austrian Patent Application No. 935/2001, filed on Jun. 15, 2001, of Austrian Patent Application No. 936/2001, filed on Jun. 15, 2001, and of Austrian Patent Application No. 621/2002, filed on Apr. 22, 2002. The entire disclosures of these three applications are expressly incorporated herein by reference.
The invention relates to a process for producing a lightweight molded part in which a metal foam is formed out of a particle-containing, molten metal by introducing gas or gas mixtures into the melt, the melt is introduced at least partially into a casting die, and the liquid phase is allowed to solidify therein.
The invention further comprises a lightweight molded part made of metal foam, comprising a metal matrix in which particles are embedded and which encloses a plurality of essentially spherical and/or essentially ellipsoid voids.
Molded parts made of metal foam naturally have a low density and, due to their structure, have special mechanical material properties. For instance, such parts can be given large deformations with upsetting degrees up to 70% and more with the application of two-or three-dimensional compressive strains. These materials with special properties can be advantageously used in technical applications, e.g., as energy absorbers in automotive technology and the like.
When using such molded parts for selected functions with certain parameters, it is important to ensure identical and reproducible property characteristics of the materials.
A process for producing a particle-reinforced metal foam is known from EP 483 184 B, the entire disclosure of which is expressly incorporated herein by reference. According to this document cellulating gas is introduced into a metal melt having reinforcing agents finely distributed therein, metal foam composite material is formed, and the accumulated foam is removed from the surface of the melted material and allowed to solidify. However, this metal foam has bubbles with uncontrolled size or size distribution, which results in a highly diffused property profile of the foam or molded part and causes functional uncertainties.
According to EP 545 957 B1 and U.S. Pat. No. 5,221,324, expressly incorporated herein by reference in their entireties, another lightweight metal part has a plurality of closed and isolated, generally spherical pores with sizes in range of 10 to 500 μm. Although such small pores with large differences in diameter can provide a metal part made with aluminum with a lower specific gravity in comparison with the bulk material, it usually is impossible to achieve a density of less than 1.0 g/cm3 and an upsetting degree of more than 60% under defined conditions.
A number of sequentially operating (U.S. Pat. No. 5,281,251, DE 43 26 982 C1) and/or continuously operating (U.S. Pat. No. 5,334,236, EP 544 291 A1, DE 43 26 982 C1, WO 91/03578) processes and devices have been proposed for producing various shapes of lightweight parts made of metal foam, with which processes and devices articles which are quite operable on principle can be produced. However, the mechanical properties thereof cannot be adjusted with the precision which is often required. The entire disclosures of the above documents are expressly incorporated herein by reference.
The present invention provides a process of the type mentioned at the outset for producing a lightweight molded part with which the internal structure of the part can be developed such that the material essentially has precise mechanical characteristics.
Furthermore, the present invention provides a molded part of the type mentioned above which shows a largely precise deformation behavior as a function of, in particular, the multi-dimensional compressive strain applied.
According to the invention a free-flowing metal foam with a monomodal distribution of the dimensions of the voids and a proportionate maximum longitudinal extension thereof in the range of about 1 to about 30 mm is produced, introduced into a mold or casting die and compressed therein essentially under all-round pressure (i.e., pressure from all sides), wherein the particle-containing, molten metal boundary walls enclosing the voids are at least partially given planar areas and the heat of solidification of the melt is dissipated.
The advantages achieved with the invention can be seen essentially in that a monomodal distribution of the dimension of the voids in the metal foam establishes a prerequisite for a predetermined material behavior under certain strain conditions. In this context, the proportionate maximum diameter of the voids is important for the level of the elastic limit of the material and the tolerable specific surface strain during the subjecting of the part to compressive strain.
In order to at least partially create planar areas in the boundary walls, it is necessary to subject the free-flowing foam to an essentially all-round, optionally low, pressure, which can result in several advantages. However, the advantage of particular importance is that in this manner the boundary walls and their nodal areas in the foam material are favorably adapted or formed for a mechanical supporting or buckling load. This makes it possible, when exceeding a defined strain limit, to ensure that at high deformation or upsetting degrees, a buckling of the foam walls or a collapse of the pores and an energy absorption takes place with low compaction of the lightweight part.
It has proved to be particularly advantageous both for a monomodal distribution of the dimensions of the voids which can be produced within narrow limits and for a precise adjustment of the proportionate maximum diameter of the voids in the foam material, if the gas is introduced through at least one feed pipe with a small frontal area projecting inwardly into the melt to develop the monomodal distribution of the dimensions of the voids. Preferred devices and processes for producing the present metal foam and a part made therefrom are described in a concurrently filed U.S. application Ser. No. 10/170,538 in the names of Franz Dobesberger, Herbert Flankl, Dietmar Leitlmeier and Alois Birgmann and having the title “Device and Process for Producing Metal Foam”, the disclosure of which is expressly incorporated herein by reference in its entirety.
For production-related and product quality reasons, it can be advantageous if the compression of the free-flowing metal foam is conducted in a casting die with interior dimensions which correspond to the desired dimensions of the molded part.
According to a particularly advantageous embodiment of the invention, particularly with regard to a desired material behavior during mechanical stress, in a three-dimensional view the metal foam of the molded part shows a monomodal distribution of the maximum longitudinal extensions of the voids in the range of between about 1 and about 30 mm.
The advantages of a lightweight molded part made in this way from metal foam are essentially due to the fact that as already indicated above, favorable conditions regarding the nodal development of the walls of the gas bubbles are achieved by means of a monomodality. With a bimodal, poly- or multi-modal distribution of the void size, thickened sections with possibly small and/or very small pores and cavity collapses are mostly present in the wall nodes, which on the one hand increases the specific gravity of the foam part and increases the metal resources for forming the same, and on the other hand can disturb the distribution of the force components, as a result of which a buckling of the wall area during strain cannot be definitely determined.
The invention's advantages of the impact of the working mechanisms in the component distribution of the compressive forces can be intensified, if the boundary walls enclosing the voids have planar areas at least in part.
If, as can be further provided in an advantageous way, in a three-dimensional view of the metal foam the ratio of the maximum longitudinal extensions of two different voids on the average is lower than about 45 for at least 20 examined pairs, narrow strain ranges within which a collapse of the foam voids begins can largely be achieved.
The precision of the transition from an elastic deformation to a plastic deformation of the material as a function of the compressive strain can be further increased if in a three-dimensional view of the metal foam the ratio of the maximum longitudinal extensions of two different voids over at least 20 pairs on the average is less than about 30, preferably less than about 15, and in particular less than about 5. These values refer to generated voids, disregarding solidification cavities in the molded part.
The composition and the structure of the liquid metal and those of the boundary walls of the voids also are important for a metal foam production and for the behavior of the molded part during mechanical stress.
If the reinforcing particles are embedded in the metal matrix in an evenly distributed fashion, a high and isotropic strengthening of the base metal can be obtained with regard to the mechanical stress. In this context it is also favorable if adjacent voids are completely separated from one another by the metal matrix. Individual cracks which can occur due to mechanical strain during cooling, are not effective under upsetting pressures.
Particularly lightweight molded parts can be produced according to the invention if the metal matrix comprises a light metal, preferably aluminum or an aluminum alloy.
If, moreover, the particles embedded in the metal matrix are of a size of about 1 to about 50 μm, preferably about 3 to about 20 μm, a particularly advantageous weight/property ratio can be achieved.
Inclusions of nonmetallic particles, preferably SiC particles and/or Al2O3 particles and/or such of intermetallic phases, have proved to be particularly favorable for reinforcing or strengthening the base metal for a foaming and consolidation of the same, and/or for developing bubble partition walls which are strengthened against buckling.
In this context it is particularly advantageous if the volume fraction of the particles embedded in the metal matrix is between about 10 vol % and about 50 vol %, preferably between about 15 vol % and about 30 vol %.
The favorable weight/property ratio of a lightweight molded part according to the present invention can be further improved if the density of the metal foam is less than about 1.05 g/cm3, preferably less than about 0.7 g/cm3, in particular less than about 0.3 g/cm3.
FIG. 1 shows sectional views of lightweight molded parts according to the invention.
FIG. 2 is a graphic representation of the relationship between density and upsetting stress of molded parts.
FIG. 3 is a graphic representation of the degree of upsetting as a function of the upsetting stress of molded parts.
FIG. 4 shows sectional views A, B, C of nodal forms in the foam walls.
FIG. 5 shows plan views A, B, C of foam parts with different volumetric density.
FIG. 6 is a graphic representation of the mean local density of a foam part according to the invention and a comparison foam part.
In FIG. 1, view A and view B each show a void formation in an Al shaped part according to the invention on the basis of a sectional view. With a monomodal distribution of the dimensions, the largest longitudinal extensions of voids were determined to be in the range of between 20 and 12 mm, with the proportionate maximum longitudinal extension being 17.2 mm. Although a compression of the free-flowing metal foam of only approx. 3.2% was conducted, planar areas are clearly formed in the boundary walls enclosing the voids.
The dependence of the upsetting stress of a molded part on the density of the same can be seen from FIG. 2. It was established during the development work that a monomodal distribution of the largest longitudinal extensions of the voids and an increasing uniformity of the same has a narrowing effect on the scatter band of the dependence. In other words: if there is a monomodal distribution of the voids in the foam part, and if the voids are of a certain size within narrow limits, the start of the deformation or collapse during exposure of the same to a compressive strain load is a precise characteristic of the material. The behavior of a foam component can thus be precisely calculated, or the formation and the structure of the foam part can advantageously be adjusted for certain functions.
The stress as a function of the upsetting deformation is shown in a comparative way in FIG. 3 by means of the test results of three molded parts. The structure of lightweight molded parts 1 and 2 with a volume weight of 0.091 gcm−3 and 0.114 gcm−3 was according to the invention, whereas comparison part 3 showed a bimodal distribution of the dimension of the voids with material concentrations in the nodes of the foam walls. From the upsetting curves of parts 1 and 2 an extremely low compaction of the same can be seen up to an upsetting degree of approx. 70%. Comparison part 3 shows a distinct compaction of the material up to an upsetting degree of approx. 45%, which continues to rise even further from this value on. This suggests an effect of the bimodal distribution of the void dimensions.
FIG. 4 shows nodal forms in the foam wall of lightweight parts on the basis of sectional views.
View A shows a sharp-edged nodal formation of the wall between three cells. Such nodes have a tendency to form premature cracks and breaks in the connecting area.
A thickened wall node can be seen from view B. This nodal formation leads to an increased specific gravity and an unfavorable distribution of the force components when the part is subjected to an upsetting pressure.
View C shows a node with wall parts, wherein both the thickness of the walls and the nodal mass are favorably formed with regard to a high upsetting deformation with low compaction of the part at high upsetting degrees.
FIG. 5 shows metal foam parts without thickening formed according to the invention in plan view, wherein the gas was introduced through feed pipes projecting inwardly into the melt with different release parameters for each of the bubbles. A monomodal distribution of the respective dimensions of the gas bubbles can be seen. The part according to View A has a specific gravity of 0.1 gcm−3, those according to View B and View C have specific gravities of 0.2 gcm−3 and 0.4 gcm−3, respectively.
Computer tomography data can be used to calculate values of the local density (density mapping). An averaging process for calculating the local densities makes it possible to determine the material distribution between the averaging volumes. Diagrams of the calculated density values of tests can provide information on the homogeneity of a lightweight molded part.
FIG. 6 shows the relative frequency of the mean local density in a molded part according to the invention (labeled 1) and in a comparison part (2) calculated according to a computer tomography process. At 0.22 gcm−3 the mean local density of part 1 has a narrow frequency maximum, which indicates a monomodal distribution of the dimension of the voids and a narrow range of the proportionate maximum longitudinal extensions of the same. In contrast, the multimodal comparison part is characterized by a broad progression of the mean local density values, showing a clear drop.
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS4973358Sep 6, 1989Nov 27, 1990Alcan International LimitedMethod of producing lightweight foamed metalUS5112697Aug 27, 1990May 12, 1992Alcan International LimitedStabilized metal foam bodyUS5186886Sep 16, 1991Feb 16, 1993Westinghouse Electric Corp.Composite nozzle assembly for conducting a flow of molten metal in an electromagnetic valveUS5221324Jun 29, 1992Jun 22, 1993Alcan International LimitedLightweight metal with isolated pores and its productionUS5281251Nov 4, 1992Jan 25, 1994Alcan International LimitedProcess for shape casting of particle stabilized metal foamUS5334236Jun 29, 1992Aug 2, 1994Alcan International LimitedProcess for producing shaped slabs of particle stabilized foamed metalCA2147377A1Nov 4, 1993May 11, 1994Alcan Int LtdProcess and apparatus for shape casting of particle stabilized metal foamCA2378825A1Jul 10, 2000Jan 18, 2001Hideo NakajimaProduction method for porous metal bodyDE4326982C1Aug 11, 1993Feb 9, 1995Alcan GmbhProcess and apparatus for manufacturing formed (shaped, moulded) parts from metal foamEP0483184A1Jul 11, 1990May 6, 1992Norsk Hydro AsA process of manufacturing particle reinforced metal foam and product thereof.EP0544291A1Nov 26, 1992Jun 2, 1993PANTEC PANELTECHNIK GmbHMethod and apparatus for producing metallic foamsEP0545957A1Aug 26, 1991Jun 16, 1993Alcan Int LtdLightweight metal with isolated pores and its production.JP2000263194A Title not availableWO1991001387A1Jul 11, 1990Feb 7, 1991Norsk Hydro A.SA process of manufacturing particle reinforced metal foam and product thereofWO1991003578A1Sep 5, 1990Mar 21, 1991Alcan International LimitedLightweight foamed metal and its productionNon-Patent CitationsReference1 *"ASM Handbook: vol. 15 Casting", ASM International, 1988, p. 323-326.2English Language Abstract of JP 2000-263194.3English Translation Abstract of DE 43 26 982.4English Translation Abstract of EP 0 544 291.5Miyoshi T et al: "Aluminum foam, 'ALPORAS': the production process, properties and applications" Porous and Cellular Materials for Structural Applications Materials Research Society Symposium Proceedings V 521 1998, Materials Research Society, Pittsburg, PA, US, Bd. 521, 1998, pp. 133-137, ISSN: 0272-9172.6Nadler, J.H. (Georgia Inst of Technology, Atlanta, GA, USA) et al: "Aluminum hollow sphere processing." Materials Science Forum V 331 (1) 2000 p. 495-500 ISSN: 0255-5476.* Cited by examinerReferenced byCiting PatentFiling datePublication dateApplicantTitleUS7699092Jun 18, 2007Apr 20, 2010Husky Injection Molding Systems Ltd.Metal-molding system and process for making foamed alloyUS7959852 *Jun 14, 2011H�tte Klein-Reichenbach Gesellschaft M.B.H.Process and device for manufacturing free-flowing metal foamUS9168584Dec 4, 2009Oct 27, 2015Bay Zoltan Alkalmazott Kutatasi Kozhasznu Nonprofit Kft.Method of producing a metal foam by oscillations and thus obtained metal foam productUS20070045914 *Oct 31, 2006Mar 1, 2007Huette Klein-Reichenbach Gesellschaft M.B.H.Process and device for manufacturing free-flowing metal foamUS20080311418 *Jun 18, 2007Dec 18, 2008Husky Injection Molding Systems Ltd.Metal-Molding System and Process for Making Foamed Alloy* Cited by examinerClassifications U.S. Classification75/415, 164/55.1, 164/79International ClassificationB22F3/11, B22D25/00, C22C1/08Cooperative ClassificationB22D25/005, B22F2003/1106, C22C2001/086, C22C1/08, B22F2998/00, C22C2001/083, B22F3/1103European ClassificationC22C1/08, B22F3/11B, B22D25/00FLegal EventsDateCodeEventDescriptionJun 14, 2002ASAssignmentOwner name: HUTTE KLEIN-REICHENBACH GESELLSCHAFT MBH, AUSTRIAFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DOBESBERGER, FRANZ;FLANKL, HERBERT;LEITLMEIER, DIETMAR;AND OTHERS;REEL/FRAME:013001/0601Effective date: 20020614Aug 6, 2010FPAYFee paymentYear of fee payment: 4Aug 11, 2014FPAYFee paymentYear of fee payment: 8RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services