Patent US8055111 - Dispersion-shifted optical fiber - Google PatentsSearch Images Maps Play YouTube News Gmail Drive More »Sign in<nobr>Advanced Patent Search</nobr>PatentsA dispersion-shifted optical fiber (NZDSF) includes a central core (r1, Dn1), an inner cladding having at least three zones with a first intermediate cladding zone (r2, Dn2), a second ring zone (r3, Dn3) and a third buried trench zone (Wtr, Dnt). The buried trench zone has an index difference (Dnt) with...http://www.google.com/patents/US8055111?utm_source=gb-gplus-sharePatent US8055111 - Dispersion-shifted optical fiberAdvanced Patent SearchPublication numberUS8055111 B2Publication typeGrantApplication numberUS 12/418,523Publication dateNov 8, 2011Filing dateApr 3, 2009Priority dateApr 4, 2008Also published asCN101551488A, CN101551488B, EP2107402A1, EP2107402B1, US20090252469Publication number12418523, 418523, US 8055111 B2, US 8055111B2, US-B2-8055111, US8055111 B2, US8055111B2InventorsPierre Sillard, Elise Regnier, Marianne Bigot-Astruc, Denis Molin, Louis-Anne de Montmorillon, Simon RichardOriginal AssigneeDraka Comteq, B.V.Export CitationBiBTeX, EndNote, RefManPatent Citations (71), Non-Patent Citations (15), Referenced by (2), Classifications (11), Legal Events (1) External Links: USPTO, USPTO Assignment, EspacenetDispersion-shifted optical fiberUS 8055111 B2Abstract A dispersion-shifted optical fiber (NZDSF) includes a central core (r1, Dn1), an inner cladding having at least three zones with a first intermediate cladding zone (r2, Dn2), a second ring zone (r3, Dn3) and a third buried trench zone (Wtr, Dnt). The buried trench zone has an index difference (Dnt) with the optical cladding between −5�10−3 and −15�10−3 and has a width (Wtr) between 2.5 μm and 5.5 μm. The present optical fiber, at a wavelength of 1550 nm, has reduced Rayleigh scattering losses of less than 0.164 dB/km, with limited bending losses.
1. A dispersion-shifted optical fiber (NZDSF), comprising from its center towards its periphery, a central core, an inner cladding comprising at least three zones, and an optical cladding, the central core having a radius (r1) and an index difference (Dn1) with the optical cladding, the inner cladding comprising from the central core towards the optical cladding:
an intermediate cladding having a radius (r2) and index difference (Dn2) with the optical cladding;
a ring having a radius (r3) and an index difference (Dn3) with the optical cladding; and
a buried trench having a radius (rtr), a width (Wtr) of between 2.5 μm and 5.5 μm, and an index difference (Dnt) with the optical cladding of between −5�10−3 and −15�10−3;
wherein the optical fiber possesses:
Rayleigh scattering losses of less than or equal to 0.164 dB/km at a wavelength of 1550 nm;
bending losses of less than 0.5 dB/turn for a bending radius of 16 millimeters at a wavelength of 1550 nm; and
bending losses of less than 0.5 dB/100 turns for a bending radius of 30 millimeters at a wavelength of 1625 nm.
2. The optical fiber according to claim 1, wherein the central core has an index difference (Dn1) with the optical cladding of less than 7.5�10−3.
3. The optical fiber according to claim 1, wherein the intermediate cladding has an index difference (Dn2) with the optical cladding of between −2.5�10−3 and 1.5�10−3.
4. The optical fiber according to claim 1, wherein the ring has an index difference (Dn3) with the optical cladding of between 0.0 and 5�10−3.
5. The optical fiber according to claim 1, further comprising a fourth inner cladding zone located between the ring (r3, Dn3) and the buried trench zone (Wtr, Dnt), the fourth cladding zone having a radius (r4) and an index difference (Dn4) with the optical cladding of between −2.5�10−3 and 1�10−3.
6. The optical fiber according to claim 5, wherein the radius (r4) of the fourth cladding zone is between 11 μm and 14.5 μm.
7. The optical fiber according to claim 1, wherein the radius of the central core (r1) is between 2 μm and 4.35 μm.
8. The optical fiber according to claim 1, wherein the outer radius of the intermediate cladding (r2) is between 4.5 μm and 8.5 μm.
9. The optical fiber according to claim 1, wherein the ring has a width (r3−r2) between 3 μm and 7.5 μm.
10. The optical fiber according to claim 1, wherein the radius of the buried trench (rtr) is less than or equal to 17 μm.
11. The optical fiber according to claim 1, wherein the buried trench has an inner radius of at least 10 μm.
12. The optical fiber according to claim 1, wherein, at a wavelength of 1550 nm, the optical fiber possesses a chromatic dispersion of less than 12 ps/(nm�km).
13. The optical fiber according to claim 1, wherein, at a wavelength of 1550 nm, the optical fiber possesses a chromatic dispersion slope of less than or equal to 0.09 ps/(nm2�km).
14. The optical fiber according to claim 1, wherein the optical fiber possesses an effective cut-off wavelength (λCeff) of less than 1600 nm.
15. The optical fiber according to claim 1, wherein the optical fiber possesses an effective area larger than 50 μm2.
16. A dispersion-shifted optical fiber, comprising:
a central core surrounded by an optical cladding, said central core having an outer radius (r1) and an index difference (Dn1) with said optical cladding;
an intermediate cladding contiguously surrounding said central core, said intermediate cladding having an outer radius (r2) and index difference (Dn2) with said optical cladding of greater than −2.5�10−3;
a ring positioned between said intermediate cladding and said optical cladding, said ring having an outer radius (r3) and an index difference (Dn3) with said optical cladding; and
a buried trench positioned between said ring and said optical cladding, said buried trench having an outer radius (rtr), a width (Wtr) of between 2.5 μm and 5.5 μm, and a negative index difference (Dnt) with said optical cladding of between −5�10−3 and −15�10−3;
wherein the optical fiber possesses Rayleigh scattering losses of 0.164 dB/km or less at a wavelength of 1550 nm;
wherein the optical fiber exhibits bending losses of 0.5 dB/turn or less for a bending radius of 16 millimeters at a wavelength of 1550 nm; and
wherein the optical fiber exhibits bending losses of 0.5 dB/100 turns or less for a bending radius of 30 millimeters at a wavelength of 1625 nm.
17. The optical fiber according to claim 16, wherein said intermediate cladding has an index difference (Dn2) with said optical cladding of between −1.5�10−3 and 1.5�10−3.
18. The optical fiber according to claim 16, wherein the optical fiber has, for a wavelength of 1550 nm, a chromatic dispersion slope of between about 0.050 ps/(nm2�km) and 0.090 ps/(nm2�km).
19. The optical fiber according to claim 16, wherein the optical fiber possesses an effective cut-off wavelength (λCeff) of less than 1600 nm.
20. A dispersion-shifted optical fiber, comprising:
an intermediate cladding positioned between said central core and said optical cladding, said intermediate cladding having an outer radius (r2) and index difference (Dn2) with said optical cladding;
a ring positioned between said intermediate cladding and said optical cladding, said ring having an outer radius (r3) and an index difference (Dn3) with said optical cladding;
a step cladding positioned between said ring and said optical cladding, said step cladding having an outer radius (r4) and an index difference (Dn4) with said optical cladding; and
a buried trench positioned between said step cladding and said optical cladding, said buried trench having an outer radius (rtr), a width (Wtr), and a negative index difference (Dnt) with said optical cladding;
wherein the optical fiber possesses Rayleigh scattering losses of less than or equal to 0.164 dB/km at a wavelength of 1550 nm.
21. The optical fiber according to claim 20, wherein said intermediate cladding's index difference (Dn2) is greater than −2.5�10−3 and less than 1.5�10−3.
22. The optical fiber according to claim 20, wherein the optical fiber exhibits bending losses of 0.5 dB/turn or less for a bending radius of 16 millimeters at a wavelength of 1550 nm; and
CROSS-REFERENCE TO PRIORITY APPLICATION This application claims the benefit of pending French application Ser. No. 08/01868 for �Dispersion Shifted Optical Fiber� (filed Apr. 4, 2008, at the French Patent Office), which is hereby incorporated by reference in its entirety.
FIELD OF THE INVENTION The present invention relates to the field of optical fiber transmissions and, more specifically, to a dispersion-shifted fiber having reduced attenuation without an increase in bending losses.
BACKGROUND OF THE INVENTION A refractive index profile of an optical fiber is a graphical representation of the value of the refractive index as a function of optical fiber radius. Conventionally, the distance r to the center of the optical fiber is shown along the abscissa (i.e., the x axis), and the difference between the refractive index at radius r and the refractive index of the outer optical cladding of the optical fiber is shown along the ordinate axis (i.e., the y axis). The outer optical cladding has a constant refractive index and usually consists of pure silica. The outer optical cladding, however, may also contain one or more dopants. The refractive index profile is referred to as a �step� profile, �trapezoidal� profile, or �triangular� profile (e.g., an �alpha� profile) for graphs having the respective shapes of a step, a trapezoid, or a triangle. These curves are generally examples of the theoretical or set profile of the optical fiber. The manufacturing stresses of the optical fiber may lead to a slightly different profile.
As line fibers for terrestrial transmission systems, SSMF (Standard Single Mode Fiber) of dispersion-shifted fibers, also called NZDSF (Non-Zero Dispersion-Shifted Fiber), are conventionally used. Shifted dispersion fibers having non-zero and positive chromatic dispersion for the wavelength at which they are used, typically around 1550 nm, are described as NZDSF+.
Typically, the SSMFs meet specific telecommunications standards and notably the G.652 standard. The SSMFs have an attenuation of about 0.19 dB/km, measured at the wavelength of 1550 nm with a Rayleigh contribution of the order of 0.160 dB/km, an effective area of about 80 μm2, an effective cut-off wavelength less than 1350 nm, a positive chromatic dispersion of about 17 ps/(nm�km) at 1550 nm and a positive dispersion slope of 0.058 ps/(nm2�km).
The NZDSF+ fibers, at the wavelength of 1550 nm, have a lower chromatic dispersion than SSMFs, typically between 3 and 14 ps/(nm�km), and a chromatic dispersion slope typically less than 0.1 ps/(nm2�km). The NZDSF+ fibers are generally used for short distance transmission systems and meet specific telecommunications standards, notably the G.655 and G.656 standards.
FIG. 1 shows the set profiles of an SSMF and of a standard NZDSF. The illustrated profiles are set profiles (i.e., representative of the theoretical profile of the fiber). Those having ordinary skill in the art will appreciate that the fiber actually obtained after drawing a fiber from a preform may have a slightly different profile.
Typically, an SSMF includes a central core with a radius of 4.35 μm and having an index difference of 5.2�10−3 with the outer cladding acting as an optical cladding. A standard NZDSF includes a central core having an index difference Dn1 with an outer cladding, acting as an optical cladding, an intermediate cladding having an index difference Dn2 with the outer cladding, and a ring having an index difference Dn3 with the outer cladding. The refractive indexes in the central core, in the intermediate cladding, and in the ring are substantially constant over all their widths. The width of the core is defined by its radius r1. The widths of the intermediate cladding and the ring are defined by their respective outer radii, r2 and r3. Typically, the central core, the intermediate cladding, the ring, and the outer cladding are obtained by CVD-type deposition in a silica tube and the optical cladding is formed by the tube and the overclad of the tube, generally in natural or doped silica, but it may also be obtained by any other deposition technique (VAD or OVD).
As illustrated in FIG. 1, the NZDSFs have a central core with a smaller radius and a larger index difference than the central core of an SSMF. With this core dimensions, chromatic dispersion may be reduced. The more significant doping of the core as compared with an SSMF, however, introduces more significant Rayleigh scattering losses, larger than 0.164 dB/km leading to an attenuation larger than 0.190 dB/km at 1550 nm.
It is desired to be able to reduce the attenuation of an NZDSF to a value equivalent to that of an SSMF. The attenuation in an optical fiber is due mostly to Rayleigh scattering losses and partly to absorption losses and to losses due to defects of the guide.
In the case of an NZDSF, the presence of dopants in the core in a higher concentration as compared with an SSMF, increases losses by Rayleigh scattering. It is known to reduce Rayleigh scattering losses by making fibers with a pure silica core. This for example is what is proposed in the publication �Ultra Low Loss (0.1484 dB/km) Pure Silica Core Fiber� of K. Nagayama et al., published in SEI Technical Review, No. 57, January 2004; or in the publication �Optical Loss Property of Silica-Based Single Mode Fibers� of M. Ohashi et al., published in the Journal of Lightwave Technology, Vol. 10, No. 5, May 1992, pp. 539-543. The fibers with a pure silica core, however, are costly to manufacture because of the obligation of burying the optical cladding by doping (e.g., with fluorine).
It is also known to reduce losses by Rayleigh scattering by optimizing the fiber-drawing conditions. This for example is what is described in the publication �Rayleigh Scattering Reduction Method for Silica-Based Optical Fiber� of K. Tsujikawa et al., published in the Journal of Lightwave Technology, Vol. 18, No. 11, November 2000, pp 1528-1532; or in the publication �A high performance GeO 2 /SiO 2 NZ-DSF and the prospects for future improvement using Holey Fiber technology� of K. Mukasa et al., published in ECOC'05, Tu 1.4.6. The proposed solutions are complex to apply industrially, however, because several fiber-drawing temperatures are used with heating and cooling cycles, which are difficult to control.
U.S. Pat. No. 6,576,164, which is hereby incorporated by reference in its entirety, discloses a method for making SSMF wherein the fiber-drawing conditions are optimized in order to reduce the losses by Rayleigh scattering. The method proposed in this document however requires complex equipment with additional cooling devices.
European Patent No. 1,256,554, and its counterpart U.S. Pat. No. 6,904,213, which is hereby incorporated by reference in its entirety, discloses a method for making a step-index fiber comprising a germanium-doped central core and outer and optical claddings with an index less than that of silica. Because the cladding is partly buried, the amount of dopant in the core may be reduced and attenuation in the fiber is reduced. Such a solution is however costly and not directly applicable to an NZDSF type fiber.
European Patent No. 1,288,685, and its counterpart U.S. Pat. No. 6,819,850, which is hereby incorporated by reference in its entirety, discloses a non-zero dispersion-shifted fiber comprising a central core, an intermediate cladding, a ring, a depressed cladding and an optical cladding. Rayleigh losses are not mentioned.
European Patent No. 1,434,071 and its counterpart U.S. Pat. No. 7,171,092, European Patent No. 1,382,981 and its counterpart U.S. Pat. No. 6,928,222, European Patent No. 1,734,390 and its counterpart U.S. Pat. No. 7,428,361, and European Patent No. 1,865,348, each of which is hereby incorporated by reference in its entirety, disclose a dispersion compensating fiber having a central core, an intermediate cladding, a ring, a depressed cladding, and an optical cladding. Rayleigh losses are not mentioned.
European Patent No. 1,610,160, and its counterpart U.S. Pat. No. 7,327,921, which is hereby incorporated by reference in its entirety, discloses a dispersion compensating fiber comprising a central core and at least five inner claddings. Rayleigh losses are not mentioned.
FIG. 2 shows a set profile of an NZDSF for which the whole of the structure would have been partly buried, i.e., lesser doping of the core and with an intermediate cladding and outer cladding having smaller indexes than that of silica. The optical cladding (which can be made by OVD, VAD, CVD, by the tube or by the overclad of the tube in which the fiber preform is made) is maintained in silica for reasons of costs. If such a fiber profile actually reduces the losses by Rayleigh scattering to a value substantially equal to that of an SSMF, the bending losses are very clearly degraded (see Example 2a of the Tables I and II below).
U.S. Pat. No. 4,852,968, which is hereby incorporated by reference in its entirety, discloses that with a buried trench it is possible to reduce the bending losses. However, by simply adding a buried trench to the structure proposed in FIG. 2, it is not possible to reach acceptable bending losses as this is shown by Example 2b of the Tables I and II (below).
Therefore, there exists a need for an NZDSF+ fiber having reduced Rayleigh scattering losses without degradation of the other optical parameters, notably bending losses, and which can be manufactured at reasonable cost and without changing the fiber drawing equipment.
SUMMARY OF THE INVENTION Accordingly, the invention proposes an NZDSF to achieve an attenuation close to that of an SSMF while limiting bending losses and observing the criteria of the standards relating to NZDSFs, notably in term of dispersion, effective area, and cut-off wavelength.
The invention more particularly proposes a non-zero dispersion-shifted optical fiber (NZDSF) that includes from its center towards its periphery, a central core, an inner cladding including at least three zones and an optical cladding, the central core having a radius and an index difference with the optical cladding, the inner cladding including from the central core to the optical cladding: (i) an intermediate cladding with a radius and index difference with the optical cladding; (ii) ring having a radius and an index difference with the optical cladding; (iii) a buried trench having a radius, a width between 2.5 μm and 5.5 μm and an index difference with the optical cladding between −5�10−3 and −15�10−3. The non-zero dispersion-shifted optical fiber has (i) Rayleigh scattering losses less than or equal to 0.164 dB/km at the wavelength of 1550 nm; (ii) bending losses less than 0.5 dB/turn for a bending radius of 16 millimeters at the wavelength of 1550 nm; and (iii) bending losses less than 0.5 dB/100 turns for a bending radius of 30 millimeters at 1625 nm.
According to other exemplary embodiments, the optical fiber according to the present invention may include one or more of the following characteristics:
the central core has an index difference with the optical cladding of less than 7.5�10−3; the index difference of the intermediate cladding zone with the optical cladding is between −2.5�10−3 and 1.5�10−3; the index difference of the ring zone with the optical cladding is between 0.0 and 5�10−3; the radius of the core is between 2 μm and 4.35 μm; the outer radius of the intermediate cladding zone is between 4.5 μm and 8.5 μm; the ring zone has a width between 3 μm and 7.5 μm; the inner radius of the buried trench zone is larger than 10 μm; the outer radius of the buried trench zone is less than or equal to 17 μm; the fiber has, for a wavelength of 1550 nm, a chromatic dispersion of less than 12 ps/(nm�km); the fiber has, for a wavelength of 1550 nm, a chromatic dispersion slope of less than or equal to 0.09 ps/(nm2�km); the fiber has an effective cut-off wavelength of less than 1600 nm; the fiber has an effective area larger than 50 μm2. According to one exemplary embodiment, the fiber further includes a fourth inner cladding zone located between the ring zone and the buried trench zone, this fourth cladding zone having an outer radius and an index difference with the optical cladding between −2.5�10−3 and 1�10−3. According to another exemplary embodiment, the radius of the fourth cladding zone is between 11 μm and 14.5 μm.
BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 (previously described) schematically depicts the set profile of an SSMF and of an NZDSF+ not according to the present invention.
FIG. 2 (previously described) schematically depicts the set profile of an NZDSF+ not according to the present invention.
FIG. 3 schematically depicts the set profile of an NZDSF+ fiber according to a first embodiment of the present invention.
FIG. 4 schematically depicts the set profile of an NZDSF+ fiber according a second embodiment of the present invention.
DETAILED DESCRIPTION The fiber according to the invention is a non-zero dispersion-shifted fiber that has a chromatic dispersion lower than the chromatic dispersion of a standard step-index SSMF. The fiber according to the invention has reduced Rayleigh scattering losses (e.g., less than 0.164 dB/km at 1550 nm). The fiber according to the invention further has limited bending losses (e.g., less than 0.5 dB/turn for a bending radius of 16 millimeters at 1550 nm and less than 0.5 dB/100 turns for a bending radius of 30 millimeters at 1625 nm.
The fiber of the invention will be described with reference to FIGS. 3 and 4, which illustrate set profiles for two possible embodiments.
The NZDSF according to the invention includes a central core having an index difference Dn1 with an outer cladding, acting as an optical cladding, and at least three inner cladding zones between the central core and the optical cladding. In this context, the central core and the inner cladding zones are obtained by CVD type deposition in a silica tube and the optical cladding is formed by the tube and the overclad of the tube generally in natural or doped silica, but it may also be obtained by any other deposition technique (VAD or OVD).
A first cladding zone is an intermediate cladding having an index difference Dn2 with the optical cladding. A second cladding zone is a ring having an index difference Dn3 with the optical cladding. A third cladding zone is a buried trench having an index difference Dnt with the optical cladding. In FIG. 3, a fourth cladding zone is present in the form of a step located between the ring and the buried trench and having an index difference Dn4 with the optical cladding. The refractive indexes of the intermediate cladding Dn2, the ring Dn3, the buried trench Dnt, and, if necessary, of the step Dn4, are substantially constant over their respective widths. The central core here has a step shape, but it may also have the shape of a trapezium, triangle or alpha. The width of the core is defined by its radius r1 and the claddings by their respective outer radii, r2-r4. The width of the buried trench is defined by a radius difference Wtr.
Rayleigh losses are, inter alia, dependent upon the index profile of the core Dn1, the index profiles of the inner and outer cladding Dn2, Dn3, Dn4, and the optical filed distribution across the fiber section given by:
∫ α ⁡ ( r ) � Ψ 2 ⁡ ( r ) ⁢ r ⁢ ⅆ r ∫ Ψ 2 ⁡ ( r ) ⁢ r ⁢ ⅆ r wherein,
r is the radius over the fiber cross section,
Ψ(r) is the optical field,
α(r) is the Rayleigh coefficient.
The fiber according to the invention is an NZDSF with a central core having a radius r1 larger than 2 μm but less than that of an SSMF (e.g., less than 4.35 μm), typically less than 4.00 μm, and an index difference Dn1 with the optical cladding larger than that of an SSMF (e.g., larger than 5.0�10−3) but less than 7.5�10−3 to limit the amount of dopants in the core. With this core profile of the fiber, it is possible to reduce chromatic dispersion and by limiting the amount of dopant in the core, it is possible to control the losses by Rayleigh scattering.
The fiber according to the invention also includes a cladding between the core and the optical cladding having at least three zones. A first zone is an intermediate cladding having a radius r2 and an index difference Dn2 with the optical cladding. This intermediate cladding may be slightly buried, it has an index difference Dn2 with the outer cladding between −2.5�10−3 and 1.5�10−3. The outer radius r2 of this intermediate cladding is between 4.5 μm and 8.5 μm. A second zone is a ring having a radius r3 and an index difference Dn3 with the optical cladding. The ring is not buried, unlike the profile of FIG. 2, and has an index difference Dn3 with the optical cladding between 0.0 and 5.10−3. The width of the ring (r3−r2) is between 3 μm and 7.5 μm. A third zone is a buried trench having a radius rtr, a controlled width Wtr, and controlled depth Dnt. As illustrated in FIG. 3, a fourth cladding zone, having a radius r4 and an index difference Dn4 with the optical cladding, may be added in the form of a step located between the ring and the buried trench. This step is narrower than the ring and the buried trench, and it may be slightly buried. It may have an outer radius r4 between 11 μm and 14.5 μm as well as an index difference with the optical cladding Dn4 between −2.5�10−3 and 1�10−3.
With a buried trench depth Dnt between −15�10−3 and −5�10−3 and a buried trench width Wtr between 2.5 μm and 5.5 μm, it is possible to efficiently limit bending losses while controlling the cut-off frequency (i.e., while limiting the propagation of higher order modes in the fiber). The fiber according to the invention thus has an effective cut-off wavelength less than 1600 nm, and preferably a cable cut-off wavelength less than 1450 nm, which complies with the constraints imposed by the G.655 and G.656 standards.
The buried trench zone may have an outer radius rtr limited to 17 μm in order to limit the manufacturing cost.
The buried trench zone, in combination with the intermediate cladding and ring zones, reduces the losses by Rayleigh scattering while limiting bending losses without perturbing the other optical parameters of the fiber. The buried trench zone is sufficiently distant from the core by the presence of the intermediate cladding and of the ring, with an inner radius larger than or equal to 10 μm. By way of example and as depicted in FIGS. 3-4, the inner radius of the buried trench may be represented by the radius of the ring (r3) or the radius of the fourth cladding (r4). With this distance of the trench relative to the central core, it is possible not to perturb too much the propagation of the fundamental mode in order to retain effective area and dispersion values compliant with the constraints imposed by the G.655 and G.656 standards. The trench is also sufficiently deep and narrow to guarantee a reduction in bending losses and to control the losses of the modes of directly higher orders (LP11 and LP02), and therefore the cut-off wavelength that follows therefrom.
Table 1 (below) provides six examples of possible index profiles for a transmission fiber according to the invention (Examples 3 and 4) and five examples not compliant with the invention (Examples 1 and 2) by comparison with a standard SSMF. The first column assigns a reference to each profile. The following columns also give the values of the radii of each section (r1-r4) as well as the width of the buried trench (Wtr). The following columns give the values of the index differences of each section with the optical cladding (Dn1-Dn4 and Dnt). The index values are measured at a wavelength of 633 nm. The fibers of the examples of Table 1 have an outer diameter of 125 μm. The values of Table 1 correspond to set profiles of fibers.
r1 r2 r3 r4 Wtr Dn1 Dn2 Dn3 Dn4 Dnt profile
The fiber according to the invention is illustrated in a non-limiting way by the examples of the above Table. Notably, the fiber according to the invention has a narrower central core than an SSMF and with a larger index difference than an SSMF. It is also noted that that the fiber according to the invention has at least three cladding zones between the central core and the optical cladding, one of these zones being a buried trench (Wtr, Dnt) having a width between 2.5 μm and 5.5 μm and an index difference with the optical cladding between −5�10−3 and −15�10−3. The buried trench zone is relatively distant from the central core, with an inner radius larger than 10 μm. With this distance of the trench relatively to the central core, it is possible not to perturb too much the propagation of the fundamental mode in order to retain effective area and dispersion values compliant with the constraints imposed by the G.655 and G.656 standards. Moreover, the width and depth of the trench guarantee reduction in bending losses and to control the losses of the modes of directly higher orders (LP11 and LP02) and therefore the cut-off wavelength that follows therefrom.
Furthermore, it is noted in Table I that the central core of the fiber according to the invention has an index difference Dn1 with the optical cladding less than 7.5�10−3 but larger than that of an SSMF (e.g., larger than 5.0�10−3). The intermediate cladding zone Dn2 has an index difference with the optical cladding between −2.5�10−3 and 1.5�10−3. The ring zone Dn3 has an index difference with the optical cladding between 0.0 and 5�10−3. The fourth cladding zone, if present, is narrower and less buried than the buried cladding zone (or not buried at all). This fourth cladding zone has an index difference Dn4 with the optical cladding between −2.5�10−3 and 1�10−3. In Table I, the central core of the fiber is narrower than an SSMF, with a radius r1 between 2 μm and 4.0 μm.
The NZDSF according to the invention, having an index profile as previously described, has reduced Rayleigh scattering losses and consequently an attenuation that is close to that of an SSMF without any increase in the bending losses. Moreover, the NZDSF having an index profile according to the invention meets the criteria of the G.655 and G.656 standards as defined in the ITU-T recommendations.
Table II (below) illustrates optical characteristics for the transmission fibers corresponding to the index profiles of Table I. In Table II, the first column repeats the references of Table I. The following columns provide for each fiber profile, the chromatic dispersion values D and the dispersion slope values P at the wavelength of 1550 nm and the effective area values Aeff at the wavelength of 1550 nm. The following columns provide for each fiber profile the Rayleigh scattering loss values at the wavelength of 1550 nm and bending loss values PPC, respectively over a radius of 10 millimeters at the wavelength of 1625 nm, over a radius of 16 millimeters at the wavelength of 1550 nm, over a radius of 25 millimeters at the wavelength of 1550 nm, and over a radius of 30 millimeters at the wavelength of 1625 nm. The last column provides for each profile the values of the effective cut-off wavelength (λCeff) as measured over two meters of fiber according to the current standards.
PPC (25 mm)
PPC (30 mm)
D @1550 nm
P @1550 nm
Aeff Rayleigh
PPC (10 mm)
PPC (16 mm)
(dB/100
λCeff profile
(nm2 � km)
Examples 1a, 1b, and 1c, which are outside the present invention, correspond to a standard NZDSF as illustrated in FIG. 1. Examples 2a and 2b are also outside the invention. Example 2a is illustrated in FIG. 2 and corresponds to the fiber of Example 1 being buried by 1.5�10−3 relatively to the outer optical cladding. Example 2b is not illustrated but corresponds to the profile of Example 2a with an additional trench.
It is noted that the fibers of Examples 1 have an attenuation higher than that of an SSMF and that the fibers of Examples 2 have an attenuation equivalent to that of SSMF but with increased bending losses.
Example 3a, 3b, and 3c, which embrace the present invention, correspond to an NZDSF as illustrated in FIG. 3, albeit with a fourth step-shaped cladding zone located between the ring and the buried trench. Examples 4a, 4b, and 4c, which also embrace the present invention, correspond to an NZDSF as illustrated in FIG. 4 (i.e., with three cladding zones located between the central core and the optical cladding).
It is then seen from Table II that the bending losses of the fiber according to the invention are equivalent to the bending losses in an SSMF, or even better. Further, the fiber according to the invention has reduced Rayleigh scattering losses as compared with a standard NZDSF. The Rayleigh scattering losses of the fiber according to the invention may be reduced to those of a standard SSMF. The attenuation in a fiber according to the invention is therefore close to that of an SSMF at the wavelength of 1550 nm.
It is also noted from Table II that the set of the three cladding zones located between the central core and the optical cladding is modified in a combination. Indeed, Example 2b clearly shows that, by simply adding a buried trench to a profile of a NZDSF having reduced Rayleigh losses, it is not possible to reduce bending losses while retaining the reduction in Rayleigh scattering losses.
It is also noted from Table II that with the profile of the fiber according to the invention, it is possible to guarantee a positive chromatic dispersion of less than 12 ps/(nm�km) with a dispersion slope of less than 0.09 ps/(nm2�km), an effective area larger than 50 μm2, and a cut-off wavelength of less than 1600 nm. The fiber according to the invention will comply with the recommendations of the ITU-T G.655 and G.656 standards, which notably recommend a cable cut-off wavelength (λCC) of less than 1450 nm, a mode diameter between 8 and 11 μm, and a positive chromatic dispersion of less than 10 ps/(nm�km) at 1550 nm. The fiber according to the invention may thus be set up in numerous transmission systems with good compatibility with the other fibers of the system. These values of effective area, dispersion, and effective cut-off, all compliant with the requirements imposed by the G.655 and G.656 standards, may be achieved by selective configuration of the buried trench, the intermediate cladding, and the ring.
As noted, the present optical fiber may include one or more coating layers (e.g., a primary coating and a secondary coating). At least one of the coating layers�typically the secondary coating�may be colored and/or possess other markings to help identify individual fibers. Alternatively, a tertiary ink layer may surround the primary and secondary coatings.
By way of example, a rectangular ribbon stack may be formed with or without a central twist (i.e., a �primary twist�). Those having ordinary skill in the art will appreciate that a ribbon stack is typically manufactured with rotational twist to allow the tube or cable to bend without placing excessive mechanical stress on the optical fibers during winding, installation, and use. In a structural variation, a twisted (or untwisted) rectangular ribbon stack may be further formed into a coil-like configuration (e.g., a helix) or a wave-like configuration (e.g., a sinusoid). In other words, the ribbon stack may possess regular �secondary� deformations.
A plurality of buffer tubes containing optical fibers (e.g., loose or ribbonized fibers) may be positioned externally adjacent to and stranded around a central strength member. This stranding can be accomplished in one direction, helically, known as �S� or �Z� stranding, or Reverse Oscillated Lay stranding, known as �S�Z� stranding. Stranding about the central strength member reduces optical fiber strain when cable strain occurs during installation and use.
Alternatively still, the present optical fibers may be positioned with a central buffer tube (i.e., the central buffer tube cable has a central buffer tube rather than a central strength member). Such a central buffer tube cable may position strength members elsewhere. For instance, metallic or non-metallic (e.g., GRP) strength members may be positioned within the cable sheath itself, and/or one or more layers of high-strength yarns (e.g., aramid or non-aramid yarns) may be positioned parallel to or wrapped (e.g., contrahelically) around the central buffer tube (i.e., within the cable's interior space). Likewise, strength members can be included within the buffer tube's casing.
For example, yarns, nonwovens, fabrics (e.g., tapes), foams, or other materials containing water-swellable material and/or coated with water-swellable materials (e.g., including super absorbent polymers (SAPs), such as SAP powder) may be employed to provide water blocking and/or to couple the optical fibers to the surrounding buffer tube and/or cable jacketing (e.g., via adhesion, friction, and/or compression). Exemplary water-swellable elements are disclosed in commonly assigned U.S. Patent Application Publication No. US 2007/0019915 A1 for a Water-Swellable Tape, Adhesive-Backed for Coupling When Used Inside a Buffer Tube (Overton et al.), each of which is hereby incorporated by reference in its entirety.
Moreover, an adhesive (e.g., a hot-melt adhesive or curable adhesive, such as a silicone acrylate cross-linked by exposure to actinic radiation) may be provided on one or more passive elements (e.g., water-swellable material) to bond the elements to the buffer tube. An adhesive material may also be used to bond the water-swellable element to optical fibers within the buffer tube. Exemplary arrangements of such elements are disclosed in commonly assigned U.S. Patent Application Publication No. US 2008/0145010 A1 for a Gel-Free Buffer Tube with Adhesively Coupled Optical Element (Overton et al.), which is hereby incorporated by reference in its entirety.
Exemplary buffer tube structures that are free from thixotropic filling greases are disclosed in commonly assigned U.S. Patent Application Publication No. US 2009/0003785 A1 for a Coupling Composition for Optical Fiber Cables (Parris et al.), which is hereby incorporated by reference in its entirety. Such buffer tubes employ coupling compositions formed from a blend of high-molecular weight elastomeric polymers (e.g., about 35 weight percent or less) and oils (e.g., about 65 weight percent or more) that flow at low temperatures. Unlike thixotropic filling greases, the coupling composition (e.g., employed as a cohesive gel or foam) is typically dry and, therefore, less messy during splicing.
Such optical fiber cables may be installed within ducts, microducts, plenums, or risers. By way of example, an optical fiber cable may be installed in an existing duct or microduct by pulling or blowing (e.g., using compressed air). An exemplary cable installation method is disclosed in commonly assigned U.S. Patent Application Publication No. 2007/0263960 for a Communication Cable Assembly and Installation Method (Lock et al.), and U.S. Patent Application Publication No. 2008/0317410 for a Modified Pre-Ferrulized Communication Cable Assembly and Installation Method (Griffioen et al.), each of which is incorporated by reference in its entirety.
Moreover, the optical fiber cables may be directly buried in the ground or, as an aerial cable, suspended from a pole or pylon. An aerial cable may be self-supporting or secured or lashed to a support (e.g., messenger wire or another cable). Exemplary aerial fiber optic cables include overhead ground wires (OPGW), all-dielectric self-supporting cables (ADSS), all dielectric lash cables (AD-Lash), and figure-eight cables, each of which is well understood by those having ordinary skill in the art. (Figure-eight cables and other designs can be directly buried or installed into ducts, and may optionally include a toning element, such as a metallic wire, so that they can be found with a metal detector.
The deployment of such optical fiber cables may include supplemental equipment. For instance, an amplifier may be included to improve optical signals. Dispersion compensating modules may be installed to reduce the effects of chromatic dispersion and polarization mode dispersion. Splice boxes, pedestals, and distribution frames, which may be protected by an enclosure, may likewise be included. Additional elements include, for example, remote terminal switches, optical network units, optical splitters, and central office switches.
This application incorporates entirely by reference the following commonly assigned patent applications: U.S. Patent Application No. 60/986,737 for a Microbend-Resistant Optical Fiber, filed Nov. 9, 2007, (Overton); U.S. Patent Application No. 61/041,484 for a Microbend-Resistant Optical Fiber, filed Apr. 1, 2008, (Overton); U.S. Patent Application No. 61/112,595 for a Microbend-Resistant Optical Fiber, filed Nov. 7, 2008, (Overton), International Patent Application No. PCT/US08/82927 Microbend-Resistant Optical Fiber, filed Nov. 9, 2008, (Overton), and U.S. patent application Ser. No. 12/267,732 for a Microbend-Resistant Optical Fiber, filed Nov. 10, 2008, (Overton).
This application further incorporates entirely by reference the following commonly assigned patent, patent application publications, and patent applications: U.S. Pat. No. 4,838,643 for a Single Mode Bend Insensitive Fiber for Use in Fiber Optic Guidance Applications (Hodges et al.); U.S. Patent Application Publication No. US 2007/0127878 A1 and its related U.S. patent application Ser. No. 11/556,895 for a Single Mode Optical Fiber (de Montmorillon et al.); U.S. Patent Application Publication No. US 2007/0280615 A1 and its related U.S. patent application Ser. No. 11/697,994 for a Single-Mode Optical Fiber (de Montmorillon et al.); U.S. Pat. No. 7,356,234 and its related U.S. patent application Ser. No. 11/743,365 for Chromatic Dispersion Compensating Fiber (de Montmorillon et al.); U.S. Pat. No. 7,483,613 for Chromatic Dispersion Compensating Fiber (de Montmorillon et al.); U.S. Patent Application Publication No. US 2008/0152288 A1 and its related U.S. patent application Ser. No. 11/999,333 for an Optical Fiber (Flammer et al.); U.S. patent application Ser. No. 12/098,804 for Transmission Optical Fiber Having Large Effective Area (Sillard et al.); U.S. Patent Application No. 61/101,337 for a Single Mode Optical Fiber, filed Sep. 30, 2008, (de Montmorillon et al.); U.S. Patent Application No. 61/112,006 for a Bend-Insensitive Single-Mode Optical Fiber, filed Nov. 6, 2008, (de Montmorillon et al.); and U.S. Patent Application No. 61/112,374 for a Bend-Insensitive Single Mode Optical Fiber, filed Nov. 7, 2008, (de Montmorillon et al.).
This application further incorporates entirely by reference the following commonly assigned patent, patent application publications, and patent applications: U.S. Pat. No. 5,574,816 for Polypropylene-Polyethylene Copolymer Buffer Tubes for Optical Fiber Cables and Method for Making the Same; U.S. Pat. No. 5,717,805 for Stress Concentrations in an Optical Fiber Ribbon to Facilitate Separation of Ribbon Matrix Material; U.S. Pat. No. 5,761,362 for Polypropylene-Polyethylene Copolymer Buffer Tubes for Optical Fiber Cables and Method for Making the Same; U.S. Pat. No. 5,911,023 for Polyolefin Materials Suitable for Optical Fiber Cable Components; U.S. Pat. No. 5,982,968 for Stress Concentrations in an Optical Fiber Ribbon to Facilitate Separation of Ribbon Matrix Material; U.S. Pat. No. 6,035,087 for Optical Unit for Fiber Optic Cables; U.S. Pat. No. 6,066,397 for Polypropylene Filler Rods for Optical Fiber Communications Cables; U.S. Pat. No. 6,175,677 for Optical Fiber Multi-Ribbon and Method for Making the Same; U.S. Pat. No. 6,085,009 for Water Blocking Gels Compatible with Polyolefin Optical Fiber Cable Buffer Tubes and Cables Made Therewith; U.S. Pat. No. 6,215,931 for Flexible Thermoplastic Polyolefin Elastomers for Buffering Transmission Elements in a Telecommunications Cable; U.S. Pat. No. 6,134,363 for Method for Accessing Optical Fibers in the Midspan Region of an Optical Fiber Cable; U.S. Pat. No. 6,381,390 for Color-Coded Optical Fiber Ribbon and Die for Making the Same; U.S. Pat. No. 6,181,857 for Method for Accessing Optical Fibers Contained in a Sheath; U.S. Pat. No. 6,314,224 for Thick-Walled Cable Jacket with Non-Circular Cavity Cross Section; U.S. Pat. No. 6,334,016 for Optical Fiber Ribbon Matrix Material Having Optimal Handling Characteristics; U.S. Pat. No. 6,321,012 for Optical Fiber Having Water Swellable Material for Identifying Grouping of Fiber Groups; U.S. Pat. No. 6,321,014 for Method for Manufacturing Optical Fiber Ribbon; U.S. Pat. No. 6,210,802 for Polypropylene Filler Rods for Optical Fiber Communications Cables; U.S. Pat. No. 6,493,491 for Optical Drop Cable for Aerial Installation; U.S. Pat. No. 7,346,244 for Coated Central Strength Member for Fiber Optic Cables with Reduced Shrinkage; U.S. Pat. No. 6,658,184 for Protective Skin for Optical Fibers; U.S. Pat. No. 6,603,908 for Buffer Tube that Results in Easy Access to and Low Attenuation of Fibers Disposed Within Buffer Tube; U.S. Pat. No. 7,045,010 for Applicator for High-Speed Gel Buffering of Flextube Optical Fiber Bundles; U.S. Pat. No. 6,749,446 for Optical Fiber Cable with Cushion Members Protecting Optical Fiber Ribbon Stack; U.S. Pat. No. 6,922,515 for Method and Apparatus to Reduce Variation of Excess Fiber Length in Buffer Tubes of Fiber Optic Cables; U.S. Pat. No. 6,618,538 for Method and Apparatus to Reduce Variation of Excess Fiber Length in Buffer Tubes of Fiber Optic Cables; U.S. Pat. No. 7,322,122 for Method and Apparatus for Curing a Fiber Having at Least Two Fiber Coating Curing Stages; U.S. Pat. No. 6,912,347 for Optimized Fiber Optic Cable Suitable for Microduct Blown Installation; U.S. Pat. No. 6,941,049 for Fiber Optic Cable Having No Rigid Strength Members and a Reduced Coefficient of Thermal Expansion; U.S. Pat. No. 7,162,128 for Use of Buffer Tube Coupling Coil to Prevent Fiber Retraction; U.S. Patent Application Publication No. US 2007/0019915 A1 for a Water-Swellable Tape, Adhesive-Backed for Coupling When Used Inside a Buffer Tube (Overton et al.); International Patent Application Publication No. 2007/013923 for Grease-Free Buffer Optical Fiber Buffer Tube Construction Utilizing a Water-Swellable, Texturized Yarn (Overton et al.); European Patent Application Publication No. 1,921,478 A1, for a Telecommunication Optical Fiber Cable (Tatat et al.); U.S. Patent Application Publication No. US 2007/0183726 A1 for an Optical Fiber Cable Suited for Blown Installation or Pushing Installation in Microducts of Small Diameter (Nothofer et al.); U.S. Patent Application Publication No. US 2008/0037942 A1 for an Optical Fiber Telecommunications Cable (Tatat); U.S. Patent Application Publication No. US 2008/0145010 A1 for a Gel-Free Buffer Tube with Adhesively Coupled Optical Element (Overton et al.); U.S. Patent Application Publication No. US 2008/0181564 A1 for a Fiber Optic Cable Having a Water-Swellable Element (Overton); U.S. Patent Application Publication No. US 2009/0041414 A1 for a Method for Accessing Optical Fibers within a Telecommunication Cable (Lavenne et al.); U.S. Patent Application Publication No. US 2009/0003781 A1 for an Optical Fiber Cable Having a Deformable Coupling Element (Parris et al.); U.S. Patent Application Publication No. US 2009/0003779 A1 for an Optical Fiber Cable Having Raised Coupling Supports (Parris); and U.S. Patent Application Publication No. US 2009/0003785 A1 for a Coupling Composition for Optical Fiber Cables (Parris et al.)
Patent CitationsCited PatentFiling datePublication dateApplicantTitleUS4838643Mar 23, 1988Jun 13, 1989Alcatel Na, Inc.Single mode bend insensitive fiber for use in fiber optic guidance applicationsUS4852968Apr 2, 1987Aug 1, 1989American Telephone And Telegraph Company, At&T Bell LaboratoriesOptical fiber comprising a refractive index trenchUS5574816Jan 24, 1995Nov 12, 1996Alcatel Na Cable Sytems, Inc.Nucleation agentUS5717805Jun 12, 1996Feb 10, 1998Alcatel Na Cable Systems, Inc.Stress concentrations in an optical fiber ribbon to facilitate separation of ribbon matrix materialUS5761362Jan 24, 1996Jun 2, 1998Alcatel Na Cable Systems, Inc.High strength, low shrinkage, good flexibility and improved processibilityUS5911023Jul 10, 1997Jun 8, 1999Alcatel Alsthom Compagnie Generale D'electricitePolyolefin materials suitable for optical fiber cable componentsUS5982968Feb 9, 1998Nov 9, 1999Alcatel Na Cable System, Inc.Stress concentrations in an optical fiber ribbon to facilitate separation of ribbon matrix materialUS6035087Mar 9, 1998Mar 7, 2000AlcatelOptical unit for fiber optic cablesUS6066397Mar 31, 1998May 23, 2000AlcatelElongated filler rod extruded from an propylene-ethylene copolymer foamed during extrusion to have void spaces and a relative density <1; a jacket confining the buffer tube, the fiber and rod; shrinkage inhibition; antisticking agentsUS6072929 *Dec 24, 1997Jun 6, 2000Sumitomo Electric Industries, Ltd.Dispersion-shifted fiberUS6085009May 12, 1998Jul 4, 2000AlcatelWater blocking gels compatible with polyolefin optical fiber cable buffer tubes and cables made therewithUS6134363Feb 18, 1999Oct 17, 2000AlcatelMethod for accessing optical fibers in the midspan region of an optical fiber cableUS6175677Apr 17, 1998Jan 16, 2001AlcatelOptical fiber multi-ribbon and method for making the sameUS6181857May 12, 1999Jan 30, 2001AlcatelMethod for accessing optical fibers contained in a sheathUS6210802Feb 10, 2000Apr 3, 2001AlcatelComprising an elongated rod extruded from a polypropylene-polyethylene copolymer resin material foamed during extrusion so as to have a plurality of void spaces therein and a relative density which is less than 1US6215931Jan 26, 1999Apr 10, 2001AlcatelFlexible thermoplastic polyolefin elastomers for buffering transmission elements in a telecommunications cableUS6314224Jun 18, 1999Nov 6, 2001AlcatelThick-walled cable jacket with non-circular cavity cross sectionUS6321012Aug 30, 1999Nov 20, 2001AlcatelOptical fiber having water swellable material for identifying grouping of fiber groupsUS6321014Nov 1, 1999Nov 20, 2001AlcatelMethod for manufacturing optical fiber ribbonUS6334016Jun 30, 1999Dec 25, 2001AlcatelOptical fiber ribbon matrix material having optimal handling characteristicsUS6335995 *Jan 21, 2000Jan 1, 2002Sumitomo Electric Industries Ltd.Dispersion-shifted fiberUS6381390Apr 6, 1999Apr 30, 2002AlcatelColor-coded optical fiber ribbon and die for making the sameUS6493491Sep 28, 2000Dec 10, 2002AlcatelOptical drop cable for aerial installationUS6576164Dec 15, 2000Jun 10, 2003AlcatelMethod of cooling an optical fiber while it is being drawnUS6603908Jun 28, 2001Aug 5, 2003AlcatelBuffer tube that results in easy access to and low attenuation of fibers disposed within buffer tubeUS6618538Oct 10, 2001Sep 9, 2003AlcatelMethod and apparatus to reduce variation of excess fiber length in buffer tubes of fiber optic cablesUS6658184May 25, 2001Dec 2, 2003AlcatelProtective skin for optical fibersUS6749446Oct 10, 2001Jun 15, 2004AlcatelOptical fiber cable with cushion members protecting optical fiber ribbon stackUS6819850Aug 26, 2002Nov 16, 2004AlcatelOptical fiber for a wavelength division multiplex transmission systemUS6904213May 2, 2002Jun 7, 2005AlcatelStep index optical fiber with doped cladding and core, a preform, and a method of fabricating such a fiberUS6912347May 20, 2003Jun 28, 2005AlcatelOptimized fiber optic cable suitable for microduct blown installationUS6922515Oct 10, 2001Jul 26, 2005AlcatelMethod and apparatus to reduce variation of excess fiber length in buffer tubes of fiber optic cablesUS6928222Jul 17, 2003Aug 9, 2005AlcatelDispersion managed optical fiberUS6941049Jun 18, 2003Sep 6, 2005AlcatelFiber optic cable having no rigid strength members and a reduced coefficient of thermal expansionUS7045010Sep 6, 2001May 16, 2006AlcatelApplicator for high-speed gel buffering of flextube optical fiber bundlesUS7162128Jan 25, 2005Jan 9, 2007Drake Comteq B.V.Use of buffer tube coupling coil to prevent fiber retractionUS7171092Dec 18, 2003Jan 30, 2007AlcatelOptical fiber with chromatic dispersion compensation in the S bandUS7322122Aug 1, 2002Jan 29, 2008Draka Comteq B.V.Method and apparatus for curing a fiber having at least two fiber coating curing stagesUS7327921Jun 29, 2006Feb 5, 2008Draka Comteq B.V.Chromatic dispersion compensating optical fibreUS7346244Mar 23, 2001Mar 18, 2008Draka Comteq B.V.Coated central strength member for fiber optic cables with reduced shrinkageUS7356234May 2, 2007Apr 8, 2008Draka Comteq B.V.Chromatic dispersion compensating fiberUS7428361Jun 7, 2006Sep 23, 2008Draka Comteq B.V.Chromatic dispersion compensating and chromatic dispersion slope compensating fiberUS7483613Nov 2, 2007Jan 27, 2009Draka Comteq B.V.Chromatic dispersion compensating fiberUS20070019915Jun 14, 2006Jan 25, 2007Draka Comteq B.V.Water-swellable tape, adhesive-bakced for coupling when used inside a buffer tubeUS20070127878Nov 6, 2006Jun 7, 2007Draka Comteq B.V.Single mode optical fiberUS20070183726Feb 8, 2007Aug 9, 2007Draka Comteq B.V.Optical Fiber Cable Suited for Blown Installation or Pushing Installation in Microducts of Small DiameterUS20070263960May 11, 2007Nov 15, 2007Draka Comteq B.V.Communication Cable Assembly and Installation MethodUS20070280615Apr 9, 2007Dec 6, 2007Draka Comteq B.V.Single-mode Optical FiberUS20080037942Aug 8, 2007Feb 14, 2008Draka Comteq B.V.Optical Fiber Telecommunications CableUS20080145010Jan 23, 2008Jun 19, 2008Draka Comteq B.V.Gel-Free Buffer Tube with Adhesively Coupled Optical ElementUS20080152288Dec 4, 2007Jun 26, 2008Ivo FlammerOptical fiberUS20080181565Mar 29, 2007Jul 31, 2008The Furukawa Electric Co., Ltd.Optical Fiber Ribbon Core and Optical Fiber CableUS20080292262Jul 20, 2006Nov 27, 2008Wayne CheatleGrease-Free Buffer Optical Fiber Buffer Tube Construction Utilizing a Water-Swellable, Texturized YarnUS20080317410Aug 28, 2008Dec 25, 2008Draka Comteq B.V.Modified Pre-Ferrulized Communication Cable Assembly and Installation MethodUS20090003779Jun 26, 2008Jan 1, 2009Draka Comteq B.V.Optical Fiber Cable Having Raised Coupling SupportsUS20090003781Jun 26, 2008Jan 1, 2009Draka Comteq B.V.Optical Fiber Cable Having A Deformable Coupling ElementUS20090003785Jun 26, 2008Jan 1, 2009Draka Comteq B.V.Coupling Composition for Optical Fiber CablesUS20090041414Apr 11, 2008Feb 12, 2009Draka Comteq B.V.Method for Accessing Optical Fibers within a Telecommunication CableUS20090175583Nov 10, 2008Jul 9, 2009Overton Bob JMicrobend-Resistant Optical FiberUS20090252469Apr 3, 2009Oct 8, 2009Draka Comteq B.V.Dispersion-Shifted Optical FiberEP1256554A1Apr 29, 2002Nov 13, 2002Alcatel Alsthom Compagnie Generale D'electriciteStep index optical fibre with doped core and cladding, preform and manufacturing process for such a fibreEP1288685A1Aug 1, 2002Mar 5, 2003Alcatel Alsthom Compagnie Generale D'electriciteOptical fibre for a wavelength division multiplexing transmission systemEP1382981A1Jul 11, 2003Jan 21, 2004AlcatelDispersion managed optical fiberEP1434071A1Dec 19, 2003Jun 30, 2004Alcatel Alsthom Compagnie Generale D'electriciteChromatic dispersion compensating optical fibre in the S-bandEP1610160A1Jun 14, 2005Dec 28, 2005Draka Comteq B.V.Chromatic dispersion compensating optical fibreEP1734390A1Jun 2, 2006Dec 20, 2006Draka Comteq B.V.Chromatic dispersion compensating and chromatic dispersion slope compensating fiber.EP1865348A2Dec 19, 2003Dec 12, 2007Draka comteq B.V.Optical fibre with S-band chromatic dispersion compensationEP1921478A1Nov 2, 2007May 14, 2008Draka comteq B.V.Telecommunication optical fiber cableEP2107402A1Apr 3, 2009Oct 7, 2009Draka Comteq B.V.Dispersion shifted optical fiberWO2007013923A2Jul 20, 2006Feb 1, 2007Cheatle WayneGrease-free buffer optical fiber buffer tube construction utilizing a water-swellable, texturized yarnWO2009062131A1Nov 9, 2008May 14, 2009Draka Comteq BvMicrobend- resistant optical fiber* Cited by examinerNon-Patent CitationsReference1European Office Action in counterpart European Application No. 09004952 dated May 19, 2011, pp. 1-4.2European Search Report in counterpart European Application No. 09004952 dated May 6, 2009, pp. 1-7 [all references previously cited].3French Search Report and Written Opinion in counterpart French Application No. 0801868, dated Oct. 31, 2008.4Mukasa K. et al., "A high performance GeO2/SiO2 NZ-DSF and the prospects for future improvement using Holey Fiber technology" , ECOC'05, Tu 1.4.6. [Cited in Specification].5Nagayama, K. et al., "Ultra Low Loss (0.1484 dB/km) Pure Silica Core Fiber", SEI Technical Review, No. 57, Jan. 2004 [Cited in Specification].6Ohashi M. et al., "Optical Loss Property of Silica-Based Single Mode Fibers", Journal of Lightwave Technology, vol. 10, No. 5, May 1992, pp. 539-543 [Cited in Specification].7Ohashi M. et al., "Optical Loss Property of Silica�Based Single Mode Fibers", Journal of Lightwave Technology, vol. 10, No. 5, May 1992, pp. 539-543 [Cited in Specification].8Tsujikawa K. et al., "Rayleigh Scattering Reduction Method for Silica-Based Optical Fiber" , Journal of Lightwave Technology, vol. 18, No. 11, Nov. 2000, pp. 1528-1532 [Cited in Specification].9U.S. Appl. No. 12/098,804 for Transmission Optical Fiber Having Large Effective Area (Sillard et al.) [Cited in Specification].10U.S. Appl. No. 60/986,737 for "Microbend Resistant Optical Fiber" filed Nov. 9, 2007 [Cited in Specification].11U.S. Appl. No. 61/041,484 for "Microbend Resistant Optical Fiber" filed Apr. 1, 2008 [Cited in Specification].12U.S. Appl. No. 61/101,337 for "Single Mode Optical Fiber" filed Sep. 30, 2008 [Cited in Specification].13U.S. Appl. No. 61/112,006 for "Bend-Insensitive Single Mode Optical Fiber" filed Nov. 6, 2008 [Cited in Specification].14U.S. Appl. No. 61/112,374 for "Bend Insensitive Single Mode Optical Fiber" filed Nov. 7, 2008 [Cited in Specification].15U.S. Appl. No. 61/112,595 for "Microbend Resistant Optical Fiber" filed Nov. 7, 2008 [Cited in Specification].Referenced byCiting PatentFiling datePublication dateApplicantTitleUS8798423May 25, 2012Aug 5, 2014Draka Comteq, B.V.Single-mode optical fiberUS8798424Jun 8, 2012Aug 5, 2014Draka Comteq B.V.Single-mode optical fiberClassifications U.S. Classification385/127, 385/128, 385/124, 385/125, 385/123, 385/126International ClassificationG02B6/02Cooperative ClassificationG02B6/02271, G02B6/03661, G02B6/02014European ClassificationG02B6/036L4Legal EventsDateCodeEventDescriptionJun 19, 2009ASAssignmentOwner name: DRAKA COMTEQ B.V., NETHERLANDSFree format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SILLARD, PIERRE;REGNIER, ELISE;BIGOT-ASTRUC, MARIANNE;AND OTHERS;REEL/FRAME:022849/0586;SIGNING DATES FROM 20081203 TO 20090519Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SILLARD, PIERRE;REGNIER, ELISE;BIGOT-ASTRUC, MARIANNE;AND OTHERS;SIGNING DATES FROM 20081203 TO 20090519;REEL/FRAME:022849/0586RotateOriginal ImageGoogle Home - Sitemap - USPTO Bulk Downloads - Privacy Policy - Terms of Service - About Google Patents - Send FeedbackData provided by IFI CLAIMS Patent Services©2012 Google