Patent Publication Number: US-8536000-B2

Title: Method for producing a semiconductor device have fin-shaped semiconductor regions

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
     This is a divisional of U.S. patent application Ser. No. 12/512,617, filed on Jul. 30, 2009 now U.S. Pat. No. 8,004,045, which is a continuation-in-part of U.S. patent application Ser. No. 12/193,861, filed on Aug. 19, 2008 now U.S. Pat. No. 8,063,437, which is a continuation of International Application No. PCT/JP2008/000303, filed on Feb. 22, 2008, which claims priority to Japanese Patent Application No. 2007-195860, filed on Jul. 27, 2007. This application claims priority under 35 U.S.C. §119(a) to Japanese Patent Applications No. 2007-195860, and No. 2008-198477, filed on Jul. 31, 2008. The entire contents of these applications is herein incorporated by reference in their entirety. 
    
    
     BACKGROUND OF THE INVENTION 
     The present disclosure relates to a semiconductor device and a method for producing the same, and more particularly to a semiconductor device of a three-dimensional structure including fin-shaped semiconductor regions on a substrate and a method for producing the same. 
     In recent years, demands for miniaturizing semiconductor devices have been increasing along with the increase in the degree of integration, functionality and speed thereof. In view of this, various device structures have been proposed in the art, aiming at the reduction in the area of the substrate taken up by transistors. Among others, attention has been drawn to field effect transistors having a fin-shaped structure. A field effect transistors having the fin-shaped structure is commonly called a fin-shaped FET (field effect transistor), and has an active region including thin wall (fin)-like semiconductor regions perpendicular to the principle plane of the substrate. In a fin-shaped FET, the side surface of the semiconductor region can be used as a channel surface, whereby it is possible to reduce the area on the substrate taken up by the transistor (see, for example, Patent Document 1 and Non-Patent Document 1). 
       FIGS. 27A-27D  show a structure of a conventional fin-shaped FET, wherein  FIG. 27A  is a plan view,  FIG. 27B  is a cross-sectional view taken along line A-A in  FIG. 27A ,  FIG. 27C  is a cross-sectional view taken along line B-B in  FIG. 27A , and  FIG. 27D  is a cross-sectional view taken along line C-C in  FIG. 27A . 
     As shown in  FIGS. 27A-27D , a conventional fin-shaped FET includes a supporting substrate  101  made of silicon, an insulating layer  102  made of silicon oxide formed on the supporting substrate  101 , semiconductor regions  103   a  to  103   d  each formed into a fin shape on the insulating layer  102  (hereinafter referred to as the “fin-shaped semiconductor regions”), a gate electrode  105  formed on the fin-shaped semiconductor regions  103   a  to  103   d  via gate insulating films  104   a  to  104   d , insulative sidewall spacers  106  formed on side surfaces of the gate electrode  105 , extension regions  107  formed on opposite side regions of the fin-shaped semiconductor regions  103   a  to  103   d  sandwiching the gate electrode  105  therebetween, and source-drain regions  117  formed on opposite side regions of the fin-shaped semiconductor regions  103   a  to  103   d  sandwiching the gate electrode  105  and the insulative sidewall spacer  106  therebetween. The fin-shaped semiconductor regions  103   a  to  103   d  are placed on the insulating layer  102  so as to be arranged at regular intervals in the gate width direction. The gate electrode  105  is formed so as to extend across the fin-shaped semiconductor regions  103   a  to  103   d  in the gate width direction. The extension region  107  includes a first impurity region  107   a  formed in an upper portion of each of the fin-shaped semiconductor regions  103   a  to  103   b , and a second impurity region  107   b  formed in a side portion of each of the fin-shaped semiconductor regions  103   a  to  103   b . The source-drain region  117  includes a third impurity region  117   a  formed in an upper portion of each of the fin-shaped semiconductor regions  103   a  to  103   b , and a fourth impurity region  117   b  formed in a side portion of each of the fin-shaped semiconductor regions  103   a  to  103   b . Note that pocket regions are not described herein or shown in the figure. 
       FIGS. 28A-28D  are cross-sectional views showing step by step a conventional method for producing a semiconductor device. Note that  FIGS. 28A-28D  correspond to the cross-sectional structure taken along line C-C in  FIG. 27A . In  FIGS. 28A-28D , like elements to those shown in  FIGS. 27A-27D  are denoted by like reference numerals and will not be described redundantly. 
     First, as shown in  FIG. 28A , there is provided an SOI (silicon on insulator) substrate, in which the insulating layer  102  made of silicon oxide is provided on the supporting substrate  101  made of silicon, and a semiconductor layer made of silicon is provided on the insulating layer  102 . Then, the semiconductor layer is patterned to form the fin-shaped semiconductor region  103   b  to be the active region. 
     Then, as shown in  FIG. 28B , the gate insulating film  104  is formed on the surface of the fin-shaped semiconductor region  103   b , after which a polysilicon film  105 A is formed across the entire surface of the supporting substrate  101 . 
     Then, as shown in  FIG. 28C , the polysilicon film  105 A and the gate insulating film  104  are etched successively to form the gate electrode  105  on the fin-shaped semiconductor region  103   b  with the gate insulating film  104   b  interposed therebetween. Then, using the gate electrode  105  as a mask, the semiconductor region  103   b  is ion-implanted with an impurity to form the extension region  107  and the pocket region (not shown). 
     Then, as shown in  FIG. 28D , an insulating film is formed across the entire surface of the supporting substrate  101 , and then the insulating film is etched back by using anisotropic dry etching to thereby form the insulative sidewall spacer  106  on the side surface of the gate electrode  105 . Then, using the gate electrode  105  and the side wall  106  as a mask, the semiconductor region  103   b  is ion-implanted with an impurity to form the source-drain region  117 . 
     Through the steps described above, it is possible to obtain a fin-shaped MISFET (metal insulator semiconductor field effect transistor) having the gate electrode  105  formed on the fin-shaped semiconductor region  103   b  with the gate insulating film  104   b  interposed therebetween. 
     In recent years, it has been drawing attention to use a plasma doping method in order to conformally dope the upper surface and the side surface of a fin-shaped semiconductor region. For example, a pulsed DC plasma technique has been proposed in the art (Non-Patent Document 1) as a plasma doping method used for conformal doping. This is a method in which a plasma is generated on and off, and has an advantage in that etching is unlikely to occur. However, if the method is used for doping a fin-shaped semiconductor region, the specific resistance of the side surface of the semiconductor region will be larger than that of the upper surface of the semiconductor region. 
     Note that in addition to the pulsed DC plasma technique of Non-Patent Document 1, plasma doping methods include a method disclosed in Patent Document 2 as a representative method. Patent Document 2 proposes a technique using an inductively coupled plasma (ICP) method. This is a method desirably capable of uniformly doping into the surface of a large substrate such as a wafer having a diameter of 300 mm, for example, by employing a longer time region (doping time) than that used in a pulsed DC plasma method. 
     Patent Document 3 discloses a plasma doping method for conformally doping the trench side surface. Note however that this is a technique for doping only the trench side surface, and it is not an object of the technique to dope the upper surface and the side surface of a fin-shaped semiconductor region. That is, with a method doping only the side surface as disclosed in Patent Document 3, doping is performed while masking the upper surface, thus failing to realize effects of the present invention to be described later, such as the realization of conformal doping on the upper surface and the side surface, and the prevention of chipping of the upper corner of a fin-shaped semiconductor region.
     Patent Document 1: Japanese Published Patent Application No. 2006-196821   Patent Document 2: International Publication WO2006/064772   Patent Document 3: Japanese Published Patent Application No. H01-295416   Non-Patent Document 1: D. Lenoble, et al., Enhanced performance of PMOS MUGFET via integration of conformal plasma-doped source/drain extensions, 2006 Symposium on VLSI Technology Digest of Technical Papers, p. 212   

     SUMMARY OF THE INVENTION 
     However, with conventional methods for producing a semiconductor device disclosed in documents such as Patent Document 1 and Non-Patent Document 1 identified above, it is not possible to obtain desirable transistor characteristics. One of the desirable transistor characteristics is no substantial decrease in the drain current in a fin-shaped MISFET, particularly, in a fin-shaped CMISFET including a fin-shaped NMISFET and a fin-shaped PMISFET. 
     In view of this, it is an object of the present invention to realize a fin-shaped CMISFET with which desirable characteristics can be obtained. 
     In order to achieve the object set forth above, the present inventors have studied the reason why desirable transistor characteristics cannot be obtained with a conventional method for producing a fin-shaped FET, leading to the following findings. 
       FIG. 29A  is a cross-sectional view showing the step of forming an extension region of a fin-shaped FET as described in Patent Document 1, and  FIG. 29B  is a cross-sectional view showing the step of forming an extension region of a fin-shaped FET as described in Non-Patent Document 1. Note that  FIGS. 29A and 29B  correspond to the cross-sectional structure taken along line B-B in  FIG. 27A . In  FIGS. 29A and 29B , like elements to those shown in  FIGS. 27A-27D  are denoted by like reference numerals and will not be described redundantly. 
     As shown in  FIG. 29A , in the method disclosed in Patent Document 1, in order to introduce an impurity not only into the upper surface of the fin-shaped semiconductor regions  103   a  to  103   d  but also into the side surface thereof, ions  108   a  and  108   b  are implanted by ion implantation into the fin-shaped semiconductor regions  103   a  to  103   d  at respective implantation angles inclined with respect to the vertical direction in different directions from each other, thus forming the extension region  107 . In such a case, the first impurity region  107   a , into which the ions  108   a  and the ions  108   b  are both implanted, is formed in the upper portion of the fin-shaped semiconductor regions  103   a  to  103   d . However, the second impurity region  107   b , into which either the ions  108   a  or the ions  108   b  are implanted, is formed in each side portion of the fin-shaped semiconductor regions  103   a  to  103   d . That is, where the dose of the ions  108   a  and that of the ions  108   b  are equal to each other, the implantation dose of a first impurity region  107   a  is twice as large as the implantation dose of the second impurity region  107   b.    
     As shown in  FIG. 29B , in the method disclosed in Non-Patent Document 1, the extension region  107  is formed in the fin-shaped semiconductor regions  103   a  to  103   d  by using a plasma doping method. Where an impurity is implanted by using a plasma doping method, the first impurity region  107   a  is formed in an upper portion of the fin-shaped semiconductor regions  103   a  to  103   d , wherein the implantation dose of the first impurity region  107   a  is dictated by the balance between implanted ions  109   a , an adsorbed species (a neutral species such as gas molecules or radicals)  109   b , and an impurity  109   c  that is desorbed from the fin-shaped semiconductor regions  103   a  to  103   d  by sputtering. However, the implantation dose of each side portion of the fin-shaped semiconductor regions  103   a  to  103   d  is less influenced by the implanted ions  109   a  and the impurity  109   c  desorbed by sputtering, and there is formed a second impurity region  107   b  whose implantation dose is mainly dictated by the adsorbed species  109   b . As a result, the implantation dose of the first impurity region  107   a  is higher than that of the second impurity region  107   b  by about 25%, for example, whereby the sheet resistance of the first impurity region  107   a  is lower than that of the second impurity region  107   b  by about 25%, for example. 
     The application of the plasma doping method disclosed in Patent Document 2 in order to form an impurity region in a fin-shaped semiconductor region has the following problem. Where the plasma doping method disclosed in Patent Document 2 (the plasma-generating gas is B 2 H 6 /He) is applied to a flat semiconductor region  151 , as shown in  FIG. 30A , the amount of chipping of silicon of the semiconductor region  151  is less than or equal to 1 nm/min. However, where an impurity region is formed in a fin-shaped semiconductor region by using the plasma doping method disclosed in Patent Document 2, as shown in  FIG. 30B , the amount of chipping of the upper corner of a fin-shaped semiconductor region  152  on the flat semiconductor region  151  is greater than 10 nm/min.  FIG. 31  is a perspective view showing a gate electrode formed on a fin-shaped semiconductor region having such a problem with a gate insulating film interposed therebetween. As shown in  FIG. 31 , a gate electrode  163  is formed so as to bridge over a fin-shaped semiconductor region  161  having an impurity region  161   a  in an upper portion thereof and an impurity region  161   b  in a side portion thereof, with a gate insulating film  162  interposed therebetween. Herein, a, b, c and d denote corners on the source side along the inner wall of the gate insulating film  162  having a pommel horse shape, and a″, b″, c″ and d″ are obtained by translating the corners a, b, c and d to the source-side end surface of the fin-shaped semiconductor region  161 . That is, the amount of chipping G of the upper corner of the fin-shaped semiconductor region  161  is the distance from the upper corner to b″ or c″, and assuming that the radius of curvature of the upper corner is r, G=(√2−1)·r holds (where the radius of curvature r′ of the upper corner before doping is 0). If the amount of chipping G of the upper corner of the fin-shaped semiconductor region  161  increases, there will be an unintended gap between the inner wall corner b or c of the gate insulating film  162  and the impurity region  161   a  or  161   b  to be the extension region, for example. 
     As described above, with a conventional method for forming an extension region of a fin-shaped FET (see  FIGS. 27A-27D  and  28 A- 28 D), the implantation dose of the first impurity region  107   a  formed in an upper portion of the fin-shaped semiconductor regions  103   a  to  103   d  is higher than that of the second impurity region  107   b  formed in a side portion of the fin-shaped semiconductor regions  103   a  to  103   d . Moreover, the junction depth of the second impurity region  107   b  is shallower than that of the first impurity region  107   a . Thus, the sheet resistance, the resistivity or the spreading resistance of the first impurity region  107   a  is lower than that of the second impurity region  107   b . Herein, Rs=ρ/t, where Rs is the sheet resistance of the object, ρ is the specific resistance (resistivity), t is the thickness (the junction depth), and ρw is the spreading resistance. As represented in the relational expression ρw=CF×k×ρ/2πr, which is widely known for the spreading resistance measurement, the specific resistance (resistivity) ρ and the spreading resistance ρw basically have a one-to-one correspondence, whereby there is a proportional relationship between Rs and ρw/t. In the relational expression, CF denotes the term of correction taking into consideration the volume effect of the spreading resistance ρw (CF=1 where no correction is made), k denotes the term of correction taking into consideration the polarity dependency at the Schottky barrier between the probe and the sample (for example, k=1 where the sample is p-type silicon, and k=1 to 3 where the sample is n-type silicon), and r denotes the radius of curvature of the tip of the probe. 
     When a fin-shaped FET having such an extension structure is operated, the current flowing through the extension region  107  is localized in the first impurity region  107   a  where the implantation dose is higher, i.e., the sheet resistance is lower, than the second impurity region  107   b , thereby failing to obtain desirable transistor characteristics. 
     Moreover, in the conventional fin-shaped FET (see  FIGS. 27A-27D  and  28 A- 28 D), the source-drain region is also formed by using an ion implantation method or a plasma doping method similar to that for the extension region. Therefore, also in the source-drain region  117 , the implantation dose of the third impurity region  117   a  formed in an upper portion of the fin-shaped semiconductor regions  103   a  to  103   d  is higher than that of the fourth impurity region  117   b  formed in a side portion of the fin-shaped semiconductor regions  103   a  to  103   d . Moreover, the junction depth of the fourth impurity region  117   b  is shallower than that of the third impurity region  117   a . When a fin-shaped FET having such a source-drain structure is operated, the current flowing through the source-drain region  117  is localized in the second impurity region  117   a  where the implantation dose is higher, i.e., the sheet resistance is lower, than the fourth impurity region  117   b , thereby failing to obtain desirable transistor characteristics. 
     With the conventional method for forming an extension region of a fin-shaped FET (see  FIG. 31 ), there will be an unintended gap between the inner wall of the gate insulating film  162  bridging over the fin-shaped semiconductor region  161  and the extension region of the fin-shaped semiconductor region  161 . When a fin-shaped FET having such an extension structure is operated, the current flowing through the extension region is less likely to flow through the upper corner of the fin-shaped semiconductor region  161 , thereby failing to obtain desirable transistor characteristics. 
     Particularly, when a fin-shaped CMISFET is formed by using the method for forming an extension region of a conventional fin-shaped FET, the upper corner of the fin-shaped semiconductor region forming the fin-shaped NMISFET is more chipped off because the mass of arsenic (As) or phosphorus (P) which is an n-type impurity for forming the fin-shaped NMISFET is greater than that of boron (B) which is a p-type impurity for forming the fin-shaped PMISFET. 
     Based on the above findings, the present inventors have invented a method for forming an impurity region in a side portion of a fin-shaped semiconductor region of each MISFET in a fin-shaped CMISFET that includes not only a fin-shaped PMISFET but also a fin-shaped NMISFET on the same substrate so that the implantation dose in the side portion is greater than or equal to 80% of that in an upper portion of the fin-shaped semiconductor region, by setting the pressure during plasma doping for the n-type impurity implantation to be less than or equal to the pressure during plasma doping for the p-type impurity implantation. 
     More specifically, the present inventors have invented a method for realizing a fin-shaped CMISFET, i.e., a semiconductor device including an impurity region in a side portion of a fin-shaped semiconductor region of each of a PMISFET and an NMISFET where the implantation dose is greater than or equal to 80% of that in an upper portion of the fin-shaped semiconductor region, by setting the pressure (which hereinafter refers to the chamber pressure) during plasma doping for the p-type impurity implantation to be less than or equal to 0.6 Pa and by setting the pressure during plasma doping for the n-type impurity implantation to be less than or equal to 0.4 Pa. 
     Particularly, in some cases with a fin-shaped FET, the width of the impurity region formed in a side portion of the fin-shaped semiconductor region accounts for 70% or more of the width of the extension region and the source-drain region in the gate width direction. Therefore, it has become important that the implantation dose of the impurity region formed in a side portion of the fin-shaped semiconductor region is made substantially equal to or greater than that of the impurity region formed in an upper portion of the fin-shaped semiconductor region as much as possible. In other words, it has become important that the resistivity, the spreading resistance or the sheet resistance of the impurity region formed in the side portion of the fin-shaped semiconductor region is set to be less than or equal to 1.25 times that of the impurity region formed in the upper portion of the fin-shaped semiconductor region. 
     Note that while the lower limit of the pressure during plasma doping can be set to be low within such a range that does not present problems with respect to the throughput, the limitations of the apparatus, etc., the lower limit is about 0.1 Pa in view of the performance of a state-of-the-art ICP plasma apparatus, etc., and is about 0.01 Pa in view of the performance of a plasma apparatus to be used in the future. 
     A semiconductor device of the present invention is a semiconductor device obtained by plasma doping method described above, including: a first fin-shaped semiconductor region formed on a substrate, the first fin-shaped semiconductor region having first-conductivity-type impurity region formed therein; a second fin-shaped semiconductor region formed on the substrate, the second fin-shaped semiconductor region having second-conductivity-type impurity region formed therein; a first gate insulating film formed so as to cover at least a side surface and an upper corner of a predetermined portion of the first fin-shaped semiconductor region, the upper corner of the first fin-shaped semiconductor region having a radius of curvature of r 1  under the first gate insulating film different from a radius of curvature of r 1 ′ outside the first gate insulating film; and a second gate insulating film formed so as to cover at least a side surface and an upper corner of a predetermined portion of the second fin-shaped semiconductor region, the upper corner of the second fin-shaped semiconductor region having a radius of curvature of r 2  under the second gate insulating film different from a radius of curvature of r 2 ′ outside the second gate insulating film, wherein r 1 ′ is greater than r 1  and less than or equal to 2×r 1 , and r 2 ′ is greater than r 2  and less than or equal to 2×r 2 . 
     In the semiconductor device of the present invention, the first-conductivity type impurity region may include a first first-conductivity-type impurity region formed in an upper portion of the first fin-shaped semiconductor regions and a second first-conductivity-type impurity region formed in a side portion of the first fin-shaped semiconductor region, and the second-conductivity-type impurity region may include a first second-conductivity-type impurity region formed in an upper portion of the second fin-shaped semiconductor region and a second second-conductivity-type impurity region formed in a side portion of the second fin-shaped semiconductor region. 
     In the semiconductor device of the present invention, the transistor characteristics can be significantly improved over the conventional techniques, if the implantation dose of the impurity region formed in the side portion of each fin-shaped semiconductor region is about 80% (more preferably 90%) or more of that of the impurity region formed in the upper portion of each fin-shaped semiconductor regions; in other words, if the sheet resistance, the resistivity or the spreading resistance of the impurity region formed in the side portion of each fin-shaped semiconductor region is less than or equal to 1.25 times (more preferably 1.1 times) that of the impurity region formed in the upper portion of each fin-shaped semiconductor region. 
     If “the height of the side surface of the fin-shaped semiconductor region”/“the width of the upper surface of the fin-shaped semiconductor region in the gate width direction” (hereinafter referred to as the “aspect ratio”) is small, there will be little degradation in the transistor characteristics even if the implantation dose of the impurity region formed in the side portion of each fin-shaped semiconductor region is somewhat smaller than that of the impurity region formed in the upper portion of each fin-shaped semiconductor region. On the other hand, an increase in the aspect ratio accordingly increases the necessity to make the implantation dose of the impurity region formed in the side portion of each fin-shaped semiconductor region to be 80% or more of that of the impurity region formed in the upper portion of each fin-shaped semiconductor region. 
     In order to make the gap between the impurity region provided in each fin-shaped semiconductor region and the inner wall of the gate insulating film to be completely zero, the amount of etching of each fin-shaped semiconductor region by using a plasma doping needs to be made completely zero. For this, it is necessary to use conditions with very small ion densities, which makes the amount of time required for the plasma doping process to be very long, thereby lowering the productivity very much. Therefore, if the gap between the impurity region provided in each fin-shaped semiconductor region and the inner wall of the gate insulating film is greater than zero and less than or equal to about 10 nanometers; in other words, if the radius of curvature r′ of the upper corner of a portion of each fin-shaped semiconductor region located outside the gate insulating film is greater than the radius of curvature r of the upper corner of a portion of each fin-shaped semiconductor region located under the gate insulating film and is less than or equal to 2×r, it is possible to ensure the productivity of the plasma doping process while suppressing deterioration in the transistor characteristics. 
     In the semiconductor device of the present invention, a junction depth of the second first-conductivity-type impurity region may be substantially equal to or greater than that of the first first-conductivity-type impurity region, and a junction depth of the second second-conductivity-type impurity region may be substantially equal to or greater than that of the first second-conductivity-type impurity region. 
     The semiconductor device of the present invention may further include: a first gate electrode formed on the first gate insulating film; and a second gate electrode formed on the second gate insulating film, wherein the first first-conductivity-type impurity region and the second first-conductivity-type impurity region are formed in another portion of the first fin-shaped semiconductor region other than the predetermined portion, and the first second-conductivity-type impurity region and the second second-conductivity-type impurity region are formed in another portion of the second fin-shaped semiconductor region other than the predetermined portion. In such a case, the first gate insulating film may be formed also on an upper surface of the predetermined portion of the first fin-shaped semiconductor region, and the second gate insulating film may be formed also on an upper surface of the predetermined portion of the second fin-shaped semiconductor region. Moreover, the first first-conductivity-type impurity region and the second first-conductivity-type impurity region may be p-type extension regions, and the first second-conductivity-type impurity region and the second second-conductivity-type impurity region may be n-type extension regions. Furthermore, the semiconductor device may further include: a first insulative sidewall spacer formed on a side surface of the first gate electrode; a second insulative sidewall spacer formed on a side surface of the second gate electrode; a third first-conductivity-type impurity region formed in the upper portion of the first fin-shaped semiconductor region; a fourth first-conductivity-type impurity region formed in the side portion of the first fin-shaped semiconductor region; a third second-conductivity-type impurity region formed in the upper portion of the second fin-shaped semiconductor region; and a fourth second-conductivity-type impurity region formed in the side portion of the second fin-shaped semiconductor region, wherein the third first-conductivity-type impurity region and the fourth first-conductivity-type impurity region are formed in a portion of the other portion of the first fin-shaped semiconductor region that is located outside the first insulative sidewall spacer, and the third second-conductivity-type impurity region and the fourth second-conductivity-type impurity region are formed in a portion of the other portion of the second fin-shaped semiconductor region that is located outside the second insulative sidewall spacer. Herein, the third first-conductivity-type impurity region and the fourth first-conductivity-type impurity region may be p-type source-drain regions, and the third second-conductivity-type impurity region and the fourth second-conductivity-type impurity region may be n-type source-drain regions. 
     In the semiconductor device of the present invention, an insulating film may be formed between the substrate and each of the first fin-shaped semiconductor region and the second fin-shaped semiconductor region. 
     The effects of the present invention can be better realized if, in the semiconductor device of the present invention, a height of a side surface of the first fin-shaped semiconductor region is greater than a width in a gate width direction of an upper surface of the first fin-shaped semiconductor region, and a height of a side surface of the second fin-shaped semiconductor region is greater than a width in a gate width direction of an upper surface of the second fin-shaped semiconductor region. 
     The effects of the present invention can be better realized if, in the semiconductor device of the present invention, a width in a gate width direction of an upper surface of each of the first fin-shaped semiconductor region and the second fin-shaped semiconductor region is less than or equal to 20 nm. 
     A method of the present invention is a method for producing a semiconductor device based on the plasma doping method of the present inventin described above, the method including the steps of: (a) forming a first fin-shaped semiconductor region on a substrate; (b) forming a second fin-shaped semiconductor regions on the substrate; (c) implanting the first fin-shaped semiconductor region with a first-conductivity-type impurity by a plasma doping method; and (d) implanting the second fin-shaped semiconductor region with a second-conductivity-type impurity by a plasma doping method, wherein the first-conductivity-type impurity is a p-type impurity or an n-type impurity, the second-conductivity-type impurity is an impurity of a conductivity type different from that of the first-conductivity-type impurity, in a case where a mass of the second-conductivity-type impurity is greater than that of the first-conductivity-type impurity, a pressure during plasma doping in the step (d) is set to be less than or equal to that in the step (c), and in a case where the mass of the first-conductivity-type impurity is greater than that of the second-conductivity-type impurity, the pressure during plasma doping in the step (c) is set to be less than or equal to that in the step (d). 
     That is, a characteristic of the method for producing a semiconductor device of the present invention is in the control of the amount of etching and the implantation dose for the fin-shaped semiconductor region using a plasma doping method, whereby it is possible to control the amount of etching by adjusting the pressure during plasma doping and it is possible to control the sheet resistance to a desirable value through the control of the implantation dose by annealing after doping. 
     Specifically, in plasma doping, as a material gas is supplied into a plasma, there will be radicals, ions or constituent molecules of the material gas or molecules or atoms resulting from the decomposition of the molecules in the plasma. In view of this, the method for producing a semiconductor device of the present invention is a method for applying the following properties to a three-dimensional device such as a fin-shaped FET: 
     (1) ions in a plasma are basically incident on the substrate vertically with respect to the principle plane of the substrate; 
     (2) neutral species such as gas molecules, radicals, etc., in a plasma are incident on the substrate in random directions with respect to the principle plane of the substrate; and 
     (3) an impurity introduced into a semiconductor, whether it is introduced in the form of ions or neutral species, contributes to electrical conduction after being activated by a heat treatment. 
     Moreover, in addition to these inherent properties (1)-(3) of ions, gas molecules, radicals, etc., the present inventors have newly found in an experiment the following property characteristic of plasma doping on a fin-shaped semiconductor region: 
     (4) the factor that etches the corner portion (the upper corner) of a fin-shaped semiconductor region is basically the ions in the plasma, and the amount of etching of the corner portion is suppressed by reducing the ion density. 
     Based on these findings, the primary characteristic of the method for producing a semiconductor device of the present invention lies in “decreasing the pressure during plasma doping as the mass of the introduced impurity increases” Thus, by sufficiently decreasing the pressure during plasma doping, the ion density decreases to a very low level, thereby suppressing the amount of etching of the corner portion of the fin-shaped semiconductor region. At the same time, it is possible to reduce the amount of impurity incident upon the principle plane of the substrate in a perpendicular direction, and to relatively increase the amount of impurity incident upon the principle plane of the substrate in random directions. Moreover, for the decrease in the implantation dose due to the decrease in the ion density, it is possible to compensate for the decrease in the implantation dose to thereby achieve a desirable implantation dose by increasing the proportion of an impurity-containing gas in the material gas with respect to the diluent gas. Therefore, it is possible to obtain a semiconductor device in which an impurity region in a side portion of the semiconductor region has an implantation dose of 80% or more of that in an upper portion of the semiconductor region. Therefore, it is possible to obtain desirable transistor characteristics even if the proportion of the width of the impurity region formed in the side portion of the fin-shaped semiconductor region increases with respect to the width in the gate width direction of the extension region and the source-drain region of a fin-shaped FET, for example. 
     In the method for producing a semiconductor device of the present invention, the step (c) may include forming a first first-conductivity-type impurity region in an upper portion of the first fin-shaped semiconductor region and forming a second first-conductivity-type impurity region in a side portion of the first fin-shaped semiconductor region, and the step (d) may include forming a first second-conductivity-type impurity region in an upper portion of the second fin-shaped semiconductor region and forming a second second-conductivity-type impurity region in a side portion of the second fin-shaped semiconductor region. In this case, in the step (c), an implantation dose of the second first-conductivity-type impurity region may be 80% or more of that of the first first-conductivity-type impurity region, and in the step (d), an implantation dose of the second second-conductivity-type impurity region may be 80% or more of that of the first second-conductivity-type impurity region. 
     The method for producing a semiconductor device of the present invention may further include the step of: forming, before the step (c), a first gate insulating film so as to cover at least a side surface and an upper corner of a predetermined portion of the first fin-shaped semiconductor region, wherein after the step (c), a radius of curvature r 1 ′ of the upper corner of the first fin-shaped semiconductor region located outside the first gate insulating film is greater than a radius of curvature r 1  of the upper corner of the first fin-shaped semiconductor region located under the first gate insulating film. In this case, after the step (c), r 1 ′ may be less than or equal to 2×r 1 . 
     The method for producing a semiconductor device of the present invention may further includes forming, before the step (d), a second gate insulating film so as to cover at least a side surface and an upper corner of a predetermined portion of the second fin-shaped semiconductor region, wherein after the step (d), a radius of curvature r 2 ′ of the upper corner of the second fin-shaped semiconductor region located outside the second gate insulating film is greater than a radius of curvature r 2  of the upper corner of the second fin-shaped semiconductor region located under the second gate insulating film. In this case, wherein after the step (d), r 2 ′ is less than or equal to 2×r 2 . 
     In the method for producing a semiconductor device of the present invention, a mass of the second-conductivity-type impurity may be greater than that of the first-conductivity-type impurity, in the step (c), an ion current density during plasma doping may be set to be less than or equal to 0.5 mA/cm 2 , and in the step (d), the ion current density during plasma doping may be set to be less than or equal to 0.1 mA/cm 2 . 
     In the method for producing a semiconductor device of the present invention, a mass of the second-conductivity-type impurity may be greater than that of the first-conductivity-type impurity, the first-conductivity-type impurity may be boron, the second-conductivity-type impurity may be arsenic or phosphorus, the step (c) may be performed by using a plasma generated from a gas containing the first-conductivity-type impurity, and the step (d) may be performed by using a plasma generated from a gas containing the second-conductivity-type impurity. 
     In the method for producing a semiconductor device of the present invention, the step (c) may be performed by using a plasma generated from a first gas containing the first-conductivity-type impurity, the step (d) may be performed by using a plasma generated from a second gas containing the second-conductivity-type impurity, the first gas may be a gas obtained by diluting molecules containing the first-conductivity-type impurity with helium, and the second gas may be a gas obtained by diluting molecules containing the second-conductivity-type impurity with helium. 
     In the method for producing a semiconductor device of the present invention, the step (c) may be performed by using a plasma generated from a first gas containing the first-conductivity-type impurity, the step (d) may be performed by using a plasma generated from a second gas containing the second-conductivity-type impurity, and one of the first gas and the second gas may be a mixed gas of B 2 H 6  and He. 
     In the method for producing a semiconductor device of the present invention, the step (c) may be performed by using a plasma generated from a first gas containing the first-conductivity-type impurity, the step (d) may be performed by using a plasma generated from a second gas containing the second-conductivity-type impurity, and one of the first gas and the second gas may be a mixed gas of AsH 3  and He. 
     In the method for producing a semiconductor device of the present invention, the step (c) may be performed by using a plasma generated from a first gas containing the first-conductivity-type impurity, the step (d) may be performed by using a plasma generated from a second gas containing the second-conductivity-type impurity, and one of the first gas and the second gas may be mixed gas of PH 3  and He. 
     In the method for producing a semiconductor device of the present invention, the first-conductivity-type impurity may be a p-type impurity and the second-conductivity-type impurity is an n-type impurity, and a pressure during the step (c) is set so as to be less than or equal to 0.6 Pa and the pressure during the step (d) may be set so as to be less than or equal to 0.4 Pa. 
     According to the present invention, it is possible to obtain a semiconductor device including an impurity region in a side portion of a fin-shaped semiconductor region of each of a PMISFET and an NMISFET, wherein the implantation dose of the impurity region is substantially equal to or greater than that in an upper portion of the fin-shaped semiconductor region; in other words, a semiconductor device including an impurity region of a low sheet resistance in a side portion of the fin-shaped semiconductor region of each of the PMISFET and the NMISFET. Therefore, it is possible to prevent deterioration of characteristics of a three-dimensional device such as a fin-shaped CMISFET. 
     That is, the present invention relates to a semiconductor device and a method for producing the same. Particularly, the present invention is useful in obtaining desirable characteristics in a three-dimensional semiconductor device having a fin-shaped semiconductor region on a substrate, particularly, a fin-shaped CMISFET. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIGS. 1A-1E  show a structure of a semiconductor device according to a first embodiment, wherein  FIG. 1A  is a plan view,  FIG. 1B  is a cross-sectional view taken along line A-A in  FIG. 1A ,  FIG. 1C  is a cross-sectional view taken along line B-B in  FIG. 1A ,  FIG. 1D  is a cross-sectional view taken along line C-C in  FIG. 1A , and  FIG. 1E  is a cross-sectional view taken along line D-D in  FIG. 1A . 
         FIGS. 2A-2J  are cross-sectional views showing step by step the method for producing a semiconductor device according to the first embodiment. 
         FIGS. 3A-3H  are cross-sectional views showing step by step the method for producing the semiconductor device according to the first embodiment. 
         FIG. 4  is a cross-sectional view illustrating a doping method using an example plasma doping process. 
         FIG. 5A  is a perspective view of a fin-shaped CMISFET according to a first example, and  FIG. 5B  is an enlarged perspective view showing an NMISFET of the fin-shaped CMISFET shown in  FIG. 5A . 
         FIG. 6A  schematically shows a cross-sectional shape of a fin-shaped semiconductor region before plasma doping in the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example, and  FIG. 6B  schematically shows a cross-sectional shape of a fin-shaped semiconductor region after plasma doping in the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 7A  is a diagram schematically showing a cross-sectional shape of a fin-shaped semiconductor region before plasma doping in the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example,  FIG. 7B  is an enlarged view thereof,  FIG. 7C  is a perspective view of the fin-shaped semiconductor region shown in  FIGS. 7A and 7B , and  FIG. 7D  is an enlarged view thereof. 
         FIG. 8A  schematically shows a cross-sectional structure of a fin-shaped semiconductor region after plasma doping in the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example;  FIG. 8B  shows the transition of the spreading resistance along line A-A in  FIG. 8A ;  FIG. 8C  shows the transition of the spreading resistance along line B-B in  FIG. 8A ; and  FIG. 8D  shows the results of the SIMS measurement of the first impurity region (the fin upper portion) formed in the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 9  schematically shows a cross-sectional structure of a fin-shaped semiconductor region after plasma doping in the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 10  schematically shows a cross-sectional structure of a fin-shaped semiconductor region after plasma doping in the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 11  shows the change in the amount of chipping of the fin corner portion over time in the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 12A  shows the relationship between the pressure and the ion current density during a p-type impurity plasma doping for forming the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example, and  FIG. 12B  shows the relationship between the pressure and the electron temperature during a p-type impurity plasma doping for forming the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 13  schematically shows a cross-sectional structure of a fin-shaped semiconductor region after plasma doping in the fin-shaped PMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 14A  schematically shows a cross-sectional shape of a fin-shaped semiconductor region before plasma doping in the fin-shaped NMISFET of the fin-shaped CMISFET according to the first example, and  FIG. 14B  schematically shows a cross-sectional shape of a fin-shaped semiconductor region after plasma doping in the fin-shaped NMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 15A  is a diagram schematically showing a cross-sectional shape of a fin-shaped semiconductor region before plasma doping in the fin-shaped NMISFET of the fin-shaped CMISFET according to the first example,  FIG. 15B  is an enlarged view thereof,  FIG. 15C  is a perspective view of the fin-shaped semiconductor region shown in FIGS.  15 A and  15 B, and  FIG. 15D  is an enlarged view thereof. 
         FIG. 16  schematically shows a cross-sectional structure of a fin-shaped semiconductor region after plasma doping in the fin-shaped NMISFET of the fin-shaped CMISFET according to the first example. 
         FIGS. 17A and 17B  schematically show a cross-sectional structure of a fin-shaped semiconductor region after plasma doping in the fin-shaped NMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 18A  shows the relationship between the pressure and the ion current density during an n-type impurity plasma doping for forming the fin-shaped NMISFET of the fin-shaped CMISFET according to the first example, and  FIG. 18B  shows the relationship between the pressure and the electron temperature during an n-type impurity plasma doping for forming the fin-shaped NMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 19  schematically shows a cross-sectional structure of a fin-shaped semiconductor region after plasma doping in the fin-shaped NMISFET of the fin-shaped CMISFET according to the first example. 
         FIG. 20A  is a perspective view of a fin-shaped CMISFET according to a second example, and  FIG. 20B  is an enlarged perspective view showing an NMISFET of the fin-shaped CMISFET shown in  FIG. 20A . 
         FIGS. 21A-21C  are diagrams illustrating the amount of chipping of the fin corner portion in the fin-shaped NMISFET of the fin-shaped CMISFET according to the second example. 
         FIG. 22  is a perspective view schematically showing an example of a basic structure of a semiconductor device according to the first and second examples. 
         FIG. 23  is a perspective view schematically showing another example of a basic structure of a semiconductor device according to the first and second examples. 
         FIG. 24  is a plan view of a semiconductor device according to a first variation of the first embodiment. 
         FIGS. 25A-25D  show a cross-sectional structure of a semiconductor device according to a second variation of the first embodiment, wherein  FIG. 25A  is a cross-sectional view taken along line A-A in  FIG. 1A ,  FIG. 25B  is a cross-sectional view taken along line B-B in  FIG. 1A ,  FIG. 25C  is a cross-sectional view taken along line C-C in  FIG. 1A , and  FIG. 25D  is a cross-sectional view taken along line D-D in  FIG. 1A . 
         FIG. 26A  is a perspective view of a fin-shaped CMISFET according to a comparative example, and  FIG. 26B  is an enlarged perspective view of the fin-shaped NMISFET of the fin-shaped CMISFET shown in  FIG. 26A . 
         FIGS. 27A-27D  show a structure of a conventional fin-shaped FET, wherein  FIG. 27A  is a plan view,  FIG. 27B  is a cross-sectional view taken along line A-A in  FIG. 27A ,  FIG. 27C  is a cross-sectional view taken along line B-B in  FIG. 27A , and  FIG. 27D  is a cross-sectional view taken along line C-C in  FIG. 27A . 
         FIGS. 28A-28D  are cross-sectional views showing step by step a conventional method for producing a semiconductor device. 
         FIG. 29A  is a cross-sectional view showing the step of forming a source-drain region of a fin-shaped FET as described in Patent Document 1, and  FIG. 29B  is a cross-sectional view showing the step of forming a source-drain region of a fin-shaped FET as described in Non-Patent Document 1. 
         FIG. 30A  shows the amount of chipping where a plasma doping method disclosed in Patent Document 2 is applied to a flat semiconductor region, and  FIG. 30B  shows the amount of chipping where a plasma doping method disclosed in Patent Document 2 is applied to a fin-shaped semiconductor region. 
         FIG. 31  is a perspective view schematically showing a structure of a conventional semiconductor device. 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     First Embodiment 
     The structure of a semiconductor device according to a first embodiment will now be described with reference to the drawings. 
       FIGS. 1A-1E  show a structure of a semiconductor device according to the first embodiment, i.e., a semiconductor device including a fin-shaped CMISFET, wherein  FIG. 1A  is a plan view,  FIG. 1B  is a cross-sectional view taken along line A-A in  FIG. 1A ,  FIG. 1C  is a cross-sectional view taken along line B-B in  FIG. 1A ,  FIG. 1D  is a cross-sectional view taken along line C-C in  FIG. 1A , and  FIG. 1E  is a cross-sectional view taken along line D-D in  FIG. 1A . 
     As shown in  FIGS. 1A-1E , the fin-shaped CMISFET of the present embodiment includes a supporting substrate  11  made of a p-type silicon substrate, for example, an insulating layer  12  made of silicon oxide, for example, and formed on the supporting substrate  11 , n-type fin-shaped semiconductor regions  13   a  and  13   b  and p-type fin-shaped semiconductor regions  913   c  and  913   d  formed on the insulating layer  12 , a gate electrode  15  formed on the n-type fin-shaped semiconductor regions  13   a  and  13   b  and the p-type fin-shaped semiconductor regions  913   c  and  913   d  with gate insulating films  14   a ,  14   b ,  914   c  and  914   d , respectively, which are made of a silicon oxynitride film, for example, interposed therebetween, insulative sidewall spacers  16  formed on the side surfaces of the gate electrode  15 , p-type extension regions  17  formed in opposing regions of the n-type fin-shaped semiconductor regions  13   a  and  13   b  that are opposing each other with the gate electrode  15  interposed therebetween, n-type extension regions  917  formed in opposing regions of the p-type fin-shaped semiconductor regions  913   c  and  913   d  that are opposing each other with the gate electrode  15  interposed therebetween, p-type source-drain regions  27  formed in opposing regions of the n-type fin-shaped semiconductor regions  13   a  and  13   b  that are opposing each other with the gate electrode  15  and the insulative sidewall spacers  16  interposed therebetween, and n-type source-drain regions  927  formed in opposing regions of the p-type fin-shaped semiconductor regions  913   c  and  913   d  that are opposing each other with the gate electrode  15  and the insulative sidewall spacers  16  interposed therebetween. 
     In the present embodiment, the n-type fin-shaped semiconductor regions  13   a  and  13   b  are formed by ion-implanting a p-type fin-shaped semiconductor region with an n-type impurity such as As. 
     In the present embodiment, the n-type fin-shaped semiconductor regions  13   a  and  13   b  and the p-type fin-shaped semiconductor regions  913   c  and  913   d  each have a width a in the gate width direction of about 30 nm, for example, a width b in the gate length direction of about 200 nm, for example, and a height (thickness) c of about 50 nm. On the insulating layer  12 , the fin-shaped semiconductor regions of the same conductivity type are arranged with a pitch d (about 60 nm, for example) in the gate width direction, and the fin-shaped semiconductor regions of different conductivity types are arranged with a pitch e (about 200 nm, for example) in the gate width direction. 
     In the present embodiment, the upper surface and the side surface of the n-type fin-shaped semiconductor regions  13   a  and  13   b  and the p-type fin-shaped semiconductor regions  913   c  and  913   d  may or may not be perpendicular to each other. 
     In the present embodiment, the gate electrode  15  is formed so as to extend across the n-type fin-shaped semiconductor regions  13   a  and  13   b  and the p-type fin-shaped semiconductor regions  913   c  and  913   d  in the gate width direction (the gate electrode  15  extending across the n-type fin-shaped semiconductor region  13   b  is referred to as a gate electrode  15   b , and the gate electrode  15  extending across the p-type fin-shaped semiconductor region  913   c  is referred to as a gate electrode  15   c ). The p-type extension region  17  includes a first p-type impurity region  17   a  formed in an upper portion of each of the n-type fin-shaped semiconductor regions  13   a  and  13   b , and a second p-type impurity region  17   b  formed in a side portion of each of the n-type fin-shaped semiconductor regions  13   a  and  13   b . The n-type extension region  917  includes a first n-type impurity region  917   a  formed in an upper portion of each of the p-type fin-shaped semiconductor regions  913   c  and  913   d , and a second n-type impurity region  917   b  formed in a side portion of each of the p-type fin-shaped semiconductor regions  913   c  and  913   d . The p-type source-drain region  27  includes a third p-type impurity region  27   a  formed in an upper portion of each of the n-type fin-shaped semiconductor regions  13   a  and  13   b , and a fourth p-type impurity region  27   b  formed in a side portion of each of the n-type fin-shaped semiconductor regions  13   a  and  13   b . The n-type source-drain  927  includes a third n-type impurity region  927   a  formed in an upper portion of each of the p-type fin-shaped semiconductor regions  913   c  and  913   d , and a fourth n-type impurity region  927   b  formed in a side portion of each of the p-type fin-shaped semiconductor regions  913   c  and  913   d . Note that pocket regions are not described herein or shown in the figure. 
     The present embodiment is characteristic in that the implantation dose of the impurity regions  17   b  and  917   b  formed in the side portion of the fin-shaped semiconductor regions  13   a ,  13   b ,  913   c  and  913   d  of the fin-shaped CMISFET is set to be 80% or more of that of the impurity regions  17   a  and  917   a  formed in the upper portion of the fin-shaped semiconductor regions  13   a ,  13   b ,  913   c  and  913   d . Thus, the sheet resistance of the impurity regions  17   b  and  917   b  of the extension regions  17  and  917  formed in the side portion of the fin-shaped semiconductor regions can be set to be less than or equal to 1.25 times that of the impurity regions  17   a  and  917   a  of the extension regions  17  and  917  formed in the upper portion of the fin-shaped semiconductor regions, whereby it is possible to obtain desirable transistor characteristics even if the proportion of the width of the impurity regions  17   b  and  917   b  formed in the side portion of the fin-shaped semiconductor regions increases with respect to the width in the gate width direction of the extension regions  17  and  917 . 
     Similarly, the sheet resistance of the impurity regions  27   b  and  927   b  formed in the side portion of the fin-shaped semiconductor regions  13   a ,  13   b ,  913   c  and  913   d  of the fin-shaped CMISFET can be set to be less than or equal to 1.25 times that of the impurity regions  27   a  and  927   a  formed in the upper portion of the fin-shaped semiconductor regions  13   a ,  13   b ,  913   c  and  913   d , whereby it is possible to obtain desirable transistor characteristics even if the proportion of the width of the impurity regions  27   b  and  927   b  formed in the side portion of the fin-shaped semiconductor regions increases with respect to the width in the gate width direction of the source-drain regions  27  and  927 . 
     In the above description, the sheet resistance of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  (the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b ) is set to be less than or equal to 1.25 times that of the first p-type impurity region  17   a  and the first n-type impurity region  917   a  (the third p-type impurity region  27   a  and the third n-type impurity region  927   a ). Herein, similar effects can be obtained when the resistivity or the spreading resistance, instead of the sheet resistance, of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  (the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b ) may be set to be less than or equal to 1.25 times that of the first p-type impurity region  17   a  and the first n-type impurity region  917   a  (the third p-type impurity region  27   a  and the third n-type impurity region  927   a ). Herein, Rs=ρ/t, where Rs is the sheet resistance of the object, ρ is the specific resistance (resistivity), t is the thickness (the junction depth), and ρw is the spreading resistance. Since the specific resistance (resistivity) ρ and the spreading resistance ρw basically have a one-to-one correspondence, there is a proportional relationship between Rs and ρw/t. While “sheet resistance” is mainly used in the following description, the magnitude of the resistance can be represented by “resistivity” or “spreading resistance” instead of “sheet resistance”. 
     In the present embodiment, the transistor characteristics can be significantly improved over the conventional techniques, if the implantation dose of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  formed in the side portion of the fin-shaped semiconductor regions is about 80% (more preferably 90%) or more of that of the first p-type impurity region  17   a  and the first n-type impurity region  917   a  formed in the upper portion of the fin-shaped semiconductor regions; in other words, if the sheet resistance, the resistivity or the spreading resistance of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  is less than or equal to 1.25 (more preferably 1.1) times that of the first p-type impurity region  17   a  and the first n-type impurity region  917   a.    
     Similarly, the transistor characteristics can be significantly improved over the conventional techniques, if the implantation dose of the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b  formed in the side portion of the fin-shaped semiconductor regions is about 80% (more preferably 90%) or more of that of the third p-type impurity region  27   a  and the third n-type impurity region  927   a  formed in the upper portion of the fin-shaped semiconductor regions; in other words, if the sheet resistance, the resistivity or the spreading resistance of the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b  is less than or equal to 1.25 (more preferably 1.1) times that of the third p-type impurity region  27   a  and the third n-type impurity region  927   a.    
     In the present embodiment, if “the height of the side surface of the fin-shaped semiconductor region”/“the width of the upper surface of the fin-shaped semiconductor region in the gate width direction” (hereinafter referred to as the “aspect ratio”) is small, there will be little degradation in the transistor characteristics (e.g., the drain current) even if the implantation dose of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  formed in the side portion of the fin-shaped semiconductor regions is somewhat smaller than that of the first p-type impurity region  17   a  and the first n-type impurity region  917   a  formed in the upper portion of the fin-shaped semiconductor regions, i.e., even if the sheet resistance, the resistivity or the spreading resistance of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  is somewhat larger than that of the first p-type impurity region  17   a  and the first n-type impurity region  917   a . On the other hand, an increase in the aspect ratio accordingly increases the necessity to make the implantation dose of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  substantially equal to or greater than that of the first p-type impurity region  17   a  and the first n-type impurity region  917   a , i.e., to make the sheet resistance, the resistivity or the spreading resistance of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  substantially equal to or less than that of the first p-type impurity region  17   a  and the first n-type impurity region  917   a.    
     Similarly, if the aspect ratio is small, there will be little degradation in the transistor characteristics even if the implantation dose of the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b  formed in the side portion of the fin-shaped semiconductor regions is somewhat smaller than that of the third p-type impurity region  27   a  and the third n-type impurity region  927   a  formed in the upper portion of the fin-shaped semiconductor regions, i.e., even if the sheet resistance, the resistivity or the spreading resistance of the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b  is somewhat larger than that of the third p-type impurity region  27   a  and the third n-type impurity region  927   a . On the other hand, an increase in the aspect ratio accordingly increases the necessity to make the implantation dose of the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b  substantially equal to or greater than that of the third p-type impurity region  27   a  and the third n-type impurity region  927   a , i.e., to make the sheet resistance, the resistivity or the spreading resistance of the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b  substantially equal to or less than that of the third p-type impurity region  27   a  and the third n-type impurity region  927   a.    
     While the transistor characteristics described above, specifically the drain current characteristics, are dependent on the dose of the three surfaces (the upper surface and the opposing side surfaces) of the fin-shaped semiconductor region, the drain current can be maintained to be large in the present embodiment since the implantation dose of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  (the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b ) is relatively large even if the width of the first p-type impurity region  17   a  and the first n-type impurity region  917   a  (the third p-type impurity region  27   a  and the third n-type impurity region  927   a ) located on the upper surface is smaller than the width of the second p-type impurity region  17   b  and the second n-type impurity region  917   b  (the fourth p-type impurity region  27   b  and the fourth n-type impurity region  927   b ) located on the side surface. 
     A method for producing a semiconductor device according to the first embodiment will now be described with reference to the drawings. 
       FIGS. 2A-2J  and  3 A- 3 H are cross-sectional views showing step by step the method for producing a semiconductor device of the first embodiment. Note that  FIGS. 2A ,  2 C,  2 E,  2 G,  2 I,  3 A,  3 C,  3 E and  3 G correspond to the cross-sectional structure taken along line C-C in  FIG. 1A . On the other hand,  FIGS. 2B ,  2 D,  2 F,  2 H,  2 J,  3 B,  3 D,  3 F and  3 H correspond to the cross-sectional structure taken along line D-D in  FIG. 1A . In  FIGS. 2A-2J  and  3 A- 3 H, like elements to those shown in  FIGS. 1A-1E  are denoted by like reference numerals and will not be described redundantly. Moreover, it is understood that the specific figures of thickness, width, etc., used in the following description are merely examples, and that the present invention is not limited by these specific figures. 
     First, as shown in  FIGS. 2A and 2B , there is provided an SOI substrate, in which the insulating layer  12  having a thickness of 150 nm and made of silicon oxide, for example, is provided on the supporting substrate  11  having a thickness of 800 μm and made of p-type silicon, for example, and a semiconductor layer having a thickness of 50 nm and made of p-type silicon, for example, is provided on the insulating layer  12 . Then, the semiconductor layer is patterned to form the n-type fin-shaped semiconductor region  13   b  and the p-type fin-shaped semiconductor region  913   c  to be the active regions. Herein, the n-type fin-shaped semiconductor region  13   b  and the p-type fin-shaped semiconductor region  913   c  have a width a in the gate width direction of about 30 nm, for example, a width b in the gate length direction of about 200 nm, for example, and a height (thickness) c of about 50 nm, for example. Fin-shaped semiconductor regions of the same conductivity type are arranged with a pitch d (about 60 nm, for example) in the gate width direction, and fin-shaped semiconductor regions of different conductivity types are arranged with a pitch e (about 200 nm, for example) in the gate width direction. 
     In the present embodiment, the n-type fin-shaped semiconductor region  13   b  is formed by performing dry-etching, or the like, on the p-type semiconductor layer to form a p-type fin-shaped semiconductor region, and then doping the p-type fin-shaped semiconductor region with an n-type impurity such as As by ion implantation, or the like. 
     Then, as shown in  FIGS. 2C and 2D , the gate insulating films  14   b  and  914   c  having a thickness of about 3 nm and made of a silicon oxynitride film, for example, is formed on the surface of each of the n-type fin-shaped semiconductor region  13   b  and the p-type fin-shaped semiconductor region  913   c , and a polysilicon film  15 A having a thickness of 60 nm, for example, is formed across the entire surface of the supporting substrate  11 . 
     Then, as shown in  FIGS. 2E and 2F , the polysilicon film  15 A is etched to form the gate electrodes  15   b  and  15   c  having a width in the gate length direction of 60 nm, for example, on the n-type fin-shaped semiconductor region  13   b  and the p-type fin-shaped semiconductor region  913   c  with the gate insulating films  14   b  and  914   c  respectively interposed therebetween. 
     Then, as shown in  FIGS. 2G and 2H , a protection film  19 A (e.g., a resist, or the like) covering the fin-shaped NMISFET formation region including the area on the p-type fin-shaped semiconductor region  913   c  is formed, after which using the gate electrode  15   b  and the protection film  19 A as a mask, the n-type fin-shaped semiconductor region  13   b  is doped with a p-type impurity under a plasma doping condition where the pressure during plasma doping is set to be less than or equal to 0.6 Pa. Thus, there is formed a p-type extension region  17  including the first p-type impurity region  17   a  formed in the upper portion of the n-type fin-shaped semiconductor region  13   b  and the second p-type impurity region  17   b  formed in the side portion of the n-type fin-shaped semiconductor region  13   b . In this process, the formation is done so that the implantation dose of the second p-type impurity region  17   b  is 80% or more of that of the first p-type impurity region  17   a . Thus, the second p-type impurity region  17   b  can be formed so that the sheet resistance, the resistivity or the spreading resistance of the second p-type impurity region  17   b  is less than or equal to 1.25 times that of the first p-type impurity region  17   a . Herein, the plasma doping condition is such that the material gas is B 2 H 6  (diborane) diluted with He (helium), the B 2 H 6  concentration in the material gas is 0.5% by mass, the total flow rate of the material gas is 100 cm 3 /min (standard state), the chamber pressure is 0.35 Pa, the source power (the plasma-generating high-frequency power) is 500 W, the bias voltage (Vpp) is 250 V, the substrate temperature is 30° C., and the plasma doping time is 60 seconds. Then, using the gate electrode  15   b  and the protection film  19 A as a mask, the n-type fin-shaped semiconductor region  13   b  is ion-implanted with an impurity to form an n-type pocket region (not shown). 
     Then, as shown in  FIGS. 2I and 2J , the protection film  19 A is removed, and a protection film  19 B (e.g., a resist, or the like) covering the fin-shaped PMISFET formation region including the area on the n-type fin-shaped semiconductor region  13   b  is formed, after which the p-type fin-shaped semiconductor region  913   c  is doped with an n-type impurity using the gate electrode  15   c  and the protection film  19 B as a mask under a plasma doping condition where the pressure during plasma doping is set to be less than or equal to 0.4 Pa. Thus, there is formed the n-type extension region  917  including the first n-type impurity region  917   a  formed in the upper portion of the p-type fin-shaped semiconductor region  913   c  and the second n-type impurity region  917   b  formed in the side portion of the p-type fin-shaped semiconductor region  913   c . In this process, the second n-type impurity region  917   b  is formed so that the implantation dose thereof is 80% or more of that of the first n-type impurity region  917   a . Thus, the second n-type impurity region  917   b  can be formed so that the sheet resistance, the resistivity or the spreading resistance of the second n-type impurity region  917   b  is less than or equal to 1.25 times that of the first n-type impurity region  917   a . Herein, the plasma doping condition is such that the material gas is AsH 3  (arsine) diluted with He (helium), the AsH 3  concentration in the material gas is 0.5% by mass, the total flow rate of the material gas is 100 cm 3 /min (standard state), the chamber pressure is 0.30 Pa, the source power (the plasma-generating high-frequency power) is 500 W, the bias voltage (Vpp) is 250 V, the substrate temperature is 30° C., and the plasma doping time is 60 seconds. Then, using the gate electrode  15   c  and the protection film  19 B as a mask, the p-type fin-shaped semiconductor region  913   c  is ion-implanted with an impurity to form a p-type pocket region (not shown). 
     Then, after the protection film  19 B is removed, an insulating film having a thickness of about 60 nm, for example, is formed across the entire surface of the supporting substrate  11 , and then the insulating film is etched back by using anisotropic dry etching to thereby form the insulative sidewall spacer  16  on the side surface of each of the gate electrodes  15   b  and  15   c , as shown in  FIGS. 3A and 3B . 
     Then, as shown in  FIGS. 3C and 3D , a protection film  19 C (e.g., a resist, or the like) covering the fin-shaped NMISFET formation region including the area on the p-type fin-shaped semiconductor region  913   c  is formed, after which the n-type fin-shaped semiconductor region  13   b  is ion-implanted with a p-type impurity using the gate electrode  15   b , the insulative sidewall spacer  16  and the protection film  19 C as a mask. Thus, there is formed the p-type source-drain region  27  including the third p-type impurity region  27   a  formed in the upper portion of the n-type fin-shaped semiconductor region  13   b  and the fourth p-type impurity region  27   b  formed in the side portion of the n-type fin-shaped semiconductor region  13   b . In this process, the gate electrode  15   b  is also implanted with a p-type impurity. Herein, the ion implantation conditions are, for example, such that the implantation ion is boron ion (B + ), the implantation energy is about 1 to 10 keV, the implantation dose is 1 to 5×10 15  cm −2 , and the tilt angle is 0°. The p-type impurity may be doped by, instead of an ion implantation process, a plasma doping process where the chamber pressure is set to be less than or equal to 0.6 Pa. Then, the implantation dose of the fourth p-type impurity region  27   b  formed in the side portion of the n-type fin-shaped semiconductor region  13   b  can be set to be 80% or more of that of the third p-type impurity region  27   a  formed in the upper portion of the n-type fin-shaped semiconductor region  13   b . Thus, the fourth p-type impurity region  27   b  can be formed so that the sheet resistance, the resistivity or the spreading resistance of the fourth p-type impurity region  27   b  is less than or equal to 1.25 times that of the third p-type impurity region  27   a.    
     Then, as shown in  FIGS. 3E and 3F , after the protection film  19 C is removed, a protection film  19 D (e.g., a resist, or the like) covering the fin-shaped PMISFET formation region including the area on the n-type fin-shaped semiconductor region  13   b  is formed, after which the p-type fin-shaped semiconductor region  913   c  is ion-implanted with an n-type impurity using the gate electrode  15   c , the insulative sidewall spacer  16  and the protection film  19 D as a mask. Thus, there is formed the n-type source-drain region  927  including the third n-type impurity region  927   a  formed in the upper portion of the p-type fin-shaped semiconductor region  913   c  and the fourth n-type impurity region  927   b  formed in the side portion of the p-type fin-shaped semiconductor region  913   c . In this process, the gate electrode  15   c  is also implanted with an n-type impurity. Herein, the ion implantation conditions are, for example, such that the implantation ion is arsenic ion (As + ), the implantation energy is about 1 to 10 keV, the implantation dose is 1 to 5×10 15  cm −2 , and the tilt angle is 0°. The n-type impurity may be doped by, instead of an ion implantation process, a plasma doping process where the chamber pressure is set to be less than or equal to 0.4 Pa. Then, the implantation dose of the fourth n-type impurity region  927   b  formed in the side portion of the p-type fin-shaped semiconductor region  913   c  can be set to be 80% or more of that of the third n-type impurity region  927   a  formed in the upper portion of the p-type fin-shaped semiconductor region  913   c . Thus, the fourth n-type impurity region  927   b  can be formed so that the sheet resistance, the resistivity or the spreading resistance of the fourth n-type impurity region  927   b  is less than or equal to 1.25 times that of the third n-type impurity region  927   a.    
     Finally, as shown in  FIGS. 3G and 3H , the protection film  19 D is removed, thus obtaining a fin-shaped CMISFET of the present embodiment. 
     The present embodiment is characteristic in the way the extension region  17  of the fin-shaped PMISFET and the extension region  917  of the fin-shaped NMISFET are formed on the same substrate  11  using a plasma doping method. Specifically, in the formation of the extension region  17  of the fin-shaped PMISFET, the pressure during the p-type impurity plasma doping is set to be 0.6 Pa or less, and in the formation of the extension region  917  of the fin-shaped NMISFET, the pressure during the n-type impurity plasma doping is set to be less than or equal to 0.4 Pa. Thus, it is possible to obtain a fin-shaped CMISFET including a fin-shaped PMISFET and a fin-shaped NMISFET on the same substrate, wherein the fin-shaped PMISFET includes the extension region  17  where the implantation dose of the impurity region  17   b  formed in the side portion of the n-type fin-shaped semiconductor region  13   b  is 80% or more of that of the impurity region  17   a  formed in the upper portion of the n-type fin-shaped semiconductor region  13   b , and the fin-shaped NMISFET includes the extension region  917  where the implantation dose of the impurity region  917   b  formed in the side portion of the p-type fin-shaped semiconductor region  913   c  is 80% or more of that of the impurity region  917   a  formed in the upper portion of the p-type fin-shaped semiconductor region  913   c.    
     Therefore, the sheet resistance, the resistivity or the spreading resistance of the impurity region  17   b  formed in the side portion of the n-type fin-shaped semiconductor region  13   b  of the fin-shaped PMISFET can be set to be less than or equal to 1.25 times that of the impurity region  17   a  formed in the upper portion of the n-type fin-shaped semiconductor region  13   b , whereby it is possible to obtain desirable transistor characteristics even if the proportion of the width of the impurity region  17   b  formed in the side portion of the fin-shaped semiconductor region  13   b  of the fin-shaped PMISFET increases with respect to the width in the gate width direction of the extension region  17  of the fin-shaped semiconductor region  13   b.    
     The sheet resistance, the resistivity or the spreading resistance of the impurity region  917   b  formed in the side portion of the p-type fin-shaped semiconductor region  913   c  of the fin-shaped NMISFET can be set to be less than or equal to 1.25 times that of the impurity region  917   a  formed in the upper portion of the p-type fin-shaped semiconductor region  913   c , whereby it is possible to obtain desirable transistor characteristics even if the proportion of the width of the impurity region  917   b  formed in the side portion of the fin-shaped semiconductor region  913   c  increases with respect to the width in the gate width direction of the extension region  917  of the fin-shaped semiconductor region  913   c  of the fin-shaped NMISFET. 
     Similarly, where the source-drain region  27  of the fin-shaped PMISFET is formed by using a plasma doping method, the pressure during plasma doping can be set to be 0.6 Pa or less, whereby it is possible to obtain the fin-shaped PMISFET including the source-drain region  27  where the implantation dose of the impurity region  27   b  formed in the side portion of the n-type fin-shaped semiconductor region  13   b  is 80% or more of that of the impurity region  27   a  formed in the upper portion of the n-type fin-shaped semiconductor region  13   b . Therefore, the sheet resistance, the resistivity or the spreading resistance of the impurity region  27   b  can be set to be less than or equal to 1.25 times that of the impurity region  27   a , whereby it is possible to obtain desirable transistor characteristics even if the proportion of the width of the impurity region  27   b  formed in the side portion of the fin-shaped semiconductor region  13   b  of the fin-shaped PMISFET increases with respect to the width in the gate width direction of the source-drain region  27  of the fin-shaped semiconductor region  13   b.    
     Where the source-drain region  927  of the fin-shaped NMISFET is formed by using a plasma doping method, the pressure during plasma doping can be set to be 0.4 Pa or less, whereby it is possible to obtain the fin-shaped NMISFET including the source-drain region  927  where the implantation dose of the impurity region  927   b  formed in the side portion of the p-type fin-shaped semiconductor region  913   c  is 80% or more of that of the impurity region  927   a  formed in the upper portion of the p-type fin-shaped semiconductor region  913   c . Therefore, the sheet resistance, the resistivity or the spreading resistance of the impurity region  927   b  can be set to be less than or equal to 1.25 times that of the impurity region  927   a , whereby it is possible to obtain desirable transistor characteristics even if the proportion of the width of the impurity region  927   b  formed in the side portion of the fin-shaped semiconductor region  913   c  of the fin-shaped NMISFET increases with respect to the width in the gate width direction of the source-drain region  927  of the fin-shaped semiconductor region  913   c.    
     In the present embodiment, the p-type extension region  17  (the p-type impurity regions  17   a  and  17   b ) is formed by plasma doping of boron (B) which is a p-type impurity in the step shown in  FIGS. 2G and 2H , and the n-type extension region  917  (the n-type impurity regions  917   a  and  917   b ) is formed by plasma doping of arsenic (As) which is an n-type impurity in the step shown in  FIGS. 2I and 2J , wherein the pressure during plasma doping of boron (B) which has a relatively small mass is set to be 0.6 Pa or less and the pressure during plasma doping of arsenic (As) which has a relatively large mass is set to be 0.4 Pa or less. However, if the mass of the p-type impurity for forming the p-type extension region  17  is larger than that of the n-type impurity for forming the n-type extension region  917 , the pressure during the p-type impurity plasma doping may be set to be less than or equal to that during the n-type impurity plasma doping. That is, the example plasma doping method is characteristic in that the pressure during plasma doping is set to be lower as the mass of the implanted impurity is larger. 
     It is understood that in the present embodiment, other parameters such as the gas concentration, the source power or the bias power may be controlled so as to realize a larger implantation dose obtained by the plasma doping in the plasma doping step shown in  FIGS. 2G and 2H  and in the plasma doping step shown in  FIGS. 2I and 2J . 
     Moreover, in the present embodiment, in order to reduce the sheet resistance, the resistivity or the spreading resistance of the second p-type impurity region  17   b  formed in the side portion of the n-type fin-shaped semiconductor region  13   b  of the fin-shaped PMISFET, it is preferred that the junction depth of the second p-type impurity region  17   b  is set to be substantially equal to or greater than the junction depth of the first p-type impurity region  17   a  formed in the upper portion of the n-type fin-shaped semiconductor region  13   b . Such a configuration can be realized by, for example, performing appropriate annealing after performing plasma doping so that the implantation dose of the second p-type impurity region  17   b  is greater than that of the first p-type impurity region  17   a . Similarly, in order to reduce the sheet resistance, the resistivity or the spreading resistance of the second n-type impurity region  917   b  formed in the side portion of the p-type fin-shaped semiconductor region  913   c  of the fin-shaped NMISFET, it is preferred that the junction depth of the second n-type impurity region  917   b  is set to be substantially equal to or greater than the junction depth of the first n-type impurity region  917   a  formed in the upper portion of the p-type fin-shaped semiconductor region  913   c . Such a configuration can be realized by, for example, performing appropriate annealing after performing plasma doping so that the implantation dose of the second n-type impurity region  917   b  is greater than that of the first n-type impurity region  917   a.    
     While B 2 H 6  diluted with He is used in the present embodiment as the material gas of plasma doping in the formation of the p-type extension region  17  (the p-type impurity regions  17   a  and  17   b ) by a p-type impurity plasma doping in the step shown in  FIGS. 2G and 2H , the material gas is not limited to any particular gas as long as the gas contains the impurity to be implanted into the n-type fin-shaped semiconductor region  13   b . Instead of B 2 H 6 , one may employ, for example, other molecules containing boron atoms (e.g., BF 3 ), or other molecules composed of boron atoms and hydrogen atoms. A gas containing an impurity may or may not be diluted with a rare gas such as He. Note that where B 2 H 6  diluted with He is used as the material gas of plasma doping as in the present embodiment, it is preferred that the concentration by mass of B 2 H 6  in the material gas is greater than or equal to 0.01% and less than or equal to 1%. This is preferred because it is then possible to easily introduce boron into silicon. Specifically, a sufficient amount of boron is unlikely to be introduced with the B 2 H 6  gas concentration being less than or equal to 0.01%, and a boron-containing deposit is likely to deposit on the surface of the semiconductor substrate with the B 2 H 6  gas concentration being greater than or equal to 1%. 
     While AsH 3  diluted with He is used in the present embodiment as the material gas of plasma doping in the formation of the n-type extension region  917  (the n-type impurity regions  917   a  and  917   b ) by an n-type impurity plasma doping in the step shown in  FIGS. 2I and 2J , the material gas is not limited to any particular gas as long as the gas contains the impurity to be implanted into the p-type fin-shaped semiconductor region  913   c . Instead of AsH 3 , one may employ, for example, PH 3 , or the like. A gas containing an impurity may or may not be diluted with a rare gas such as He. Note that where AsH 3  diluted with He is used as the material gas of plasma doping as in the present embodiment, it is preferred that the concentration by mass of AsH 3  in the material gas is greater than or equal to 0.01% and less than or equal to 1%. This is preferred because it is then possible to easily introduce arsenic into silicon. Specifically, a sufficient amount of arsenic is unlikely to be introduced with the AsH 3  gas concentration being less than or equal to 0.01%, and a arsenic-containing deposit is likely to deposit on the surface of the semiconductor substrate with the AsH 3  gas concentration being greater than or equal to 1%. 
     [Mechanism of Present Invention] 
     The mechanism of the present invention will now be described with reference to  FIG. 4  with respect to a case where the p-type extension region  17  (the p-type impurity regions  17   a  and  17   b ) is formed by a p-type impurity plasma doping. Note that the following description similarly applies to the mechanism of the formation of the n-type extension region  917  (the p-type impurity regions  917   a  and  917   b ) by an n-type impurity plasma doping. 
     First, as shown in  FIG. 4 , the n-type fin-shaped semiconductor regions  13   a  and  13   b  are implanted with a p-type impurity by using a plasma doping method. Thus, the first p-type impurity region  17   a  is formed in the upper portion of the fin-shaped semiconductor regions  13   a  and  13   b , wherein the implantation dose of the first p-type impurity region  17   a  is dictated by the balance between implanted ions  18   a , an adsorbed species (a neutral species such as gas molecules or radicals)  18   b , and an impurity  18   c  that is desorbed from the fin-shaped semiconductor regions  13   a  and  13   b  by sputtering. Moreover, the second p-type impurity region  17   b  is formed in the side portion of the fin-shaped semiconductor regions  13   a  and  13   b , wherein the implantation dose of the second p-type impurity region  17   b  is dictated primarily by the adsorbed species (a neutral species such as gas molecules or radicals)  18   b . In this process, since there are ions that are incident on the side surface of the fin-shaped semiconductor regions  13   a  and  13   b  from an inclined direction, there are present the implanted ions  18   a  and the impurity  18   c  that is desorbed from the fin-shaped semiconductor regions  13   a  and  13   b  by sputtering, but nevertheless the influence thereof is very little as compared with the adsorbed species  18   b  and doping by the adsorbed species  18   b  will be dominant. That is, the number of the implanted ions  18   a  doped into the side portion of the fin-shaped semiconductor regions  13   a  and  13   b  and the impurity  18   c  desorbed from the side portion of the fin-shaped semiconductor regions  13   a  and  13   b  by sputtering is very small as compared with the number of the implanted ions  18   a  doped into the upper portion of the fin-shaped semiconductor regions  13   a  and  13   b  and the impurity  18   c  desorbed from the upper portion of the fin-shaped semiconductor regions  13   a  and  13   b  by sputtering. 
     As described above, the difference between the doping of the upper portion and that of the side portion of the fin-shaped semiconductor regions  13   a  and  13   b  occurs because the influence of the implanted ions  18   a  and the influence of the impurity  18   c  desorbed from the fin-shaped semiconductor regions  13   a  and  13   b  by sputtering are significant in the upper portion of the fin-shaped semiconductor regions  13   a  and  13   b , whereas these influences are very little in the side portion of the fin-shaped semiconductor regions  13   a  and  13   b . Herein, the amount of the impurity  18   c  desorbed from the fin-shaped semiconductor regions  13   a  and  13   b  by sputtering is also influenced by the amount of the implanted ions  18   a  and the implantation energy. That is, the fundamental difference between the doping of the upper portion and that of the side portion of the fin-shaped semiconductor regions  13   a  and  13   b  is that the amount of the implanted ions  18   a  incident on the fin-shaped semiconductor regions  13   a  and  13   b  is very different from that incident on the side surface of the fin-shaped semiconductor regions  13   a  and  13   b , i.e., the difference occurs because the amount of the implanted ions  18   a  incident on the upper surface of the fin-shaped semiconductor regions  13   a  and  13   b  is much larger than the side surface of the fin-shaped semiconductor regions  13   a  and  13   b.    
     Therefore, by making the amount of the implanted ions  18   a  incident on the upper surface of the fin-shaped semiconductor regions  13   a  and  13   b  very small, the fundamental difference between the doping of the upper surface and that of the side surface of the fin-shaped semiconductor regions  13   a  and  13   b  can be substantially dissolved. That is, by making the amount of the implanted ions  18   a  incident on the fin-shaped semiconductor regions  13   a  and  13   b  very small, the amount of the implanted ions  18   a  implanted into the upper portion of the fin-shaped semiconductor regions  13   a  and  13   b  is made very small while the amount of the impurity  18   c  desorbed from the upper portion is also made very small. Then, in the upper portion of the fin-shaped semiconductor regions  13   a  and  13   b , the influence of the implanted ions  18   a  on the implantation dose relatively becomes smaller than the influence of the adsorbed species  18   b  on the implantation dose, whereby doping by the adsorbed species  18   b  becomes the primary factor that influences the implantation dose. On the other hand, in the side portion of the fin-shaped semiconductor regions  13   a  and  13   b , doping by the adsorbed species  18   b  is dominant in the first place. As a result, both in the upper portion and the side portion of the fin-shaped semiconductor regions  13   a  and  13   b , the implantation dose is substantially dictated by the amount of doping by the adsorbed species  18   b . Since the amount of doping by the adsorbed species  18   b  is an amount that is dictated by adsorption of a neutral species (such as gas molecules or radicals) moving in random directions without being influenced by the electric field, the amount of doping is equal for the upper portion and for the side portion of the fin-shaped semiconductor regions  13   a  and  13   b . Thus, the implantation dose of the first p-type impurity region  17   a  can be made equal to that of the second p-type impurity region  17   b.    
     The example fin-shaped CMISFET where the implantation dose of the fin upper portion (the impurity regions  17   a  and  917   a ) and that of the fin side portion (the impurity regions  17   b  and  917   b ) are substantially equal to each other will now be described in greater detail by way of specific examples. 
     First Example 
       FIG. 5A  is a perspective view of an example (first example) of a fin-shaped CMISFET, and  FIG. 5B  is an enlarged perspective view showing an NMISFET of the fin-shaped CMISFET shown in  FIG. 5A . In  FIGS. 5A and 5B , like elements to those of the fin-shaped CMISFET shown in  FIGS. 1A-1E  are denoted by like reference numerals and will not be described redundantly. 
     First, referring to  FIG. 5B , the chipping of the fin corner portion (the upper corner) of a fin-shaped NMISFET will be described. This similarly applies to the chipping of the fin corner portion of a fin-shaped PMISFET. As shown in  FIG. 5B , the gate electrode  15   c  is formed so as to extend across the p-type fin-shaped semiconductor region  913   c  having the n-type impurity region  917   a  in an upper portion thereof and the n-type impurity region  917   b  in a side portion thereof, with the gate insulating film  914   c  interposed therebetween. Herein, the height and the width of the p-type fin-shaped semiconductor region  913   c  (and those of the n-type fin-shaped semiconductor region  13   b ) are 120 nm and 160 nm, respectively. In  FIG. 5B , a, b, c and d denote corners on the source side along the inner wall of the gate insulating film  914   c  having a pommel horse shape, and a″, b″, c″ and d″ are obtained by translating the corners a, b, c and d to the source-side end surface of the p-type fin-shaped semiconductor region  913   c.    
     In the present example, the distance G between the corner b″ and the upper-portion n-type impurity region  917   a , i.e., the distance G between the corner c″ and the upper-portion n-type impurity region  917   a , is greater than zero and less than or equal to 10 nm. Therefore, the amount of chipping (the amount of increase in the radius of curvature) of the fin corner portion of the fin-shaped NMISFET of the fin-shaped CMISFET of the present example (and that of the fin-shaped PMISFET) after the plasma doping process is within an acceptable range. 
     The implantation process by plasma doping for the p-type impurity and that for the n-type impurity will now be described in greater detail. 
     [Suppression of Amount of Chipping of Fin Corner Portion of Fin-Shaped PMISFET] 
     First, the suppression of the amount of chipping of the fin corner portion of the fin-shaped PMISFET in the first example will be described with reference to  FIGS. 6A and 6B . 
       FIG. 6A  schematically shows a cross-sectional shape of the fin-shaped semiconductor region (strictly, a semiconductor region  51  having fins) before a p-type impurity plasma doping. Herein, the height and the width of the fin are 120 nm and 160 nm, respectively, and the distance between fins is 210 nm. That is, the distance between the center of a fin in the width direction and that in an adjacent fin is 370 nm. Moreover, the radius of curvature of the fin corner portion (the region indicated by a broken line in the figure) is 8.7 nm. Note that the fin corner portion is in a shape with a curvature, but not a completely right-angled shape, even before the p-type impurity plasma doping because the fin corner portion is chipped off slightly in the dry etching step and the cleaning step before the p-type impurity plasma doping. 
       FIG. 6B  schematically shows a cross-sectional shape of a fin-shaped semiconductor region (strictly, the semiconductor region  51  having fins) after a p-type impurity plasma doping. The p-type impurity plasma doping condition is such that, for example, the material gas is B 2 H 6  diluted with He, the B 2 H 6  concentration in the material gas is 0.5% by mass, the chamber pressure is 0.35 Pa, the source power (the plasma-generating high-frequency power) is 600 W, the bias voltage Vpp is 130 V, the substrate temperature is 20° C., and the plasma doping time is 200 seconds. An ICP method, for example, was used as a plasma generating method. Note that in the first example, in order to make the amount of implanted ions incident on the fin upper surface very small to suppress the amount of chipping of the fin corner portion, the chamber pressure is set to be 0.35 Pa, a very small value for an ICP method. The radius of curvature of the fin corner portion (the region indicated by a broken line in the figure) after the p-type impurity plasma doping is performed under such a condition is 10.6 nm. That is, in the first example, the difference between the radius of curvature of the fin corner portion before the p-type impurity plasma doping and that after the p-type impurity plasma doping is 1.9 nm, which is the amount of change over a plasma doping time of 200 seconds, and therefore it can be seen that the amount of chipping (the amount of increase in the radius of curvature) per minute is 0.6 nm, which is a very small value. 
     [Conformal Doping Property of Fin-Shaped PMISFET] 
     Next, the sheet resistance of the first p-type impurity region (the impurity region of the fin upper portion) and that of the second p-type impurity region (the impurity region of the fin side portion) in the fin-shaped PMISFET of the first example will be described with reference to the drawings. The p-type impurity plasma doping condition is such that, for example, the material gas is B 2 H 6  diluted with He, the B 2 H 6  concentration in the material gas is 0.8% by mass, the chamber pressure is 0.35 Pa, the source power (the plasma-generating high-frequency power) is 500 W, the bias voltage Vpp is 250V, the substrate temperature is 20° C., and the plasma doping time is 60 seconds. An ICP method, for example, was used as a plasma generating method. Moreover, the chamber pressure is set to be 0.35 Pa, a very small value for an ICP method, in order to make the amount of implanted ions incident on the fin upper surface very small so that the amount of doping by the adsorbed species is the main factor influencing the implantation dose of the first p-type impurity region (the fin upper portion); in other words, so that the implantation dose of the first p-type impurity region (the fin upper portion) approaches that of the second p-type impurity region (the fin side portion) where the main factor is the amount of doping by the adsorbed species in the first place. The amount of chipping of the fin corner portion in this case is also very small, and about the same as that described above in Suppression Of Amount Of Chipping Of Fin Corner Portion Of Fin-Shaped PMISFET.  FIG. 7A  is a diagram schematically showing a cross-sectional shape of the fin-shaped semiconductor region (strictly, the semiconductor region  51  having fins) before the p-type impurity plasma doping,  FIG. 7B  is an enlarged view thereof,  FIG. 7C  is a perspective view of the fin-shaped semiconductor region shown in  FIGS. 7A and 7B , and  FIG. 7D  is an enlarged view thereof. The height and the width of the fin-shaped semiconductor region shown in  FIGS. 7A-7D  are 128 nm and 342 nm, respectively, and the distance between fins is 743 nm. That is, the distance between the center of a fin in the width direction and that in an adjacent fin is 1085 nm. 
       FIG. 8A  shows how a low-resistance region  52  is formed by implanting boron into silicon of the n-type fin-shaped semiconductor region (strictly, the n-type semiconductor region  51  having fins) by plasma doping and then performing a heat treatment by a spike RTA (rapid thermal annealing) at 1050° C. to thereby electrically activate boron in silicon. As shown in  FIG. 8A , the low-resistance region  52  is formed not only in the first p-type impurity region (fin upper portion) but also in the second p-type impurity region (the fin side portion). 
       FIG. 8B  shows the transition of the spreading resistance as measured by using SSRM (2D Scanning Spreading Resistance Microscopy) along line A-A in  FIG. 8A . In  FIG. 8B , the zero point along the horizontal axis means the fin upper surface. As shown in  FIG. 8B , the spreading resistance of the first p-type impurity region (fin upper portion) is 2.9×10 4 Ω. Moreover, as the depth along the horizontal axis increases (i.e., more into the fin), the distance from the first p-type impurity region (the low-resistance region  52  of the fin upper portion) increases. A region away from the fin upper surface by about 0.3 μm or more is a region into which boron has not been implanted or has not substantially diffused by heat treatment, and a spreading resistance of the substrate (about 1.5×10 6 Ω) is observed in this region. 
     Next,  FIG. 8C  shows the transition of the spreading resistance along line B-B in  FIG. 8A . Note that  FIG. 8C  shows the results of an SSRM observation of a portion where three fins as shown in  FIG. 8A  are arranged together, and the zero point along the horizontal axis in  FIG. 8C  means a position at a predetermined distance from the left-side surface of the leftmost fin to the left along line B-B. The region delimited by a thick broken line in  FIG. 8C  represents the spreading resistance of the semiconductor region including the fin shown in  FIG. 8A . Referring to the region delimited by the thick broken line, in a region where the depth along the horizontal axis is small (e.g., a region where the depth along the horizontal axis is around 1.0 μm), the spreading resistance of an insulator (not shown in  FIG. 8A ) provided between fins for the purpose of SSRM measurement is observed, whose value is very high. A region where the depth along the horizontal axis is around 1.35 μm corresponds to the second p-type impurity region located in a left-side portion of the fin shown in  FIG. 8A , and the spreading resistance of this portion is 3.0×10 4 Ω. A region where the depth along the horizontal axis is around 1.5 μm corresponds to the central portion of the fin shown in  FIG. 8A , i.e., a portion surrounded by the first p-type impurity region (the fin upper portion) and two second p-type impurity regions (opposing side portions of the fin), and this is a region into which boron has not been implanted or has not so much diffused by heat treatment, whereby a value close to the spreading resistance of the substrate is observed as the spreading resistance of this portion. A region where the depth along the horizontal axis is around 1.7 μm corresponds to the second p-type impurity region located in a right-side portion of the fin shown in  FIG. 8A , and the spreading resistance of this portion is 3.5×10 4 Ω. Moreover, in a region where the depth along the horizontal axis is greater than 1.7 μm (e.g., a region where the depth along the horizontal axis is around 2.0 μm), the spreading resistance of an insulator (not shown in  FIG. 8A ) provided between fins for the purpose of SSRM measurement is again observed, whose value is very high. As described above, the spreading resistances of the six second impurity regions located in the opposing side portions of the three fins as represented in  FIG. 8C  are observed to be, from left to right, 2.1×10 4 Ω, 3.0×10 4 Ω, 3.0×10 4 Ω, 3.5×10 4 Ω, 3.0×10 4 Ω and 2.9×10 4 Ω, and the average value of the spreading resistances of the six second p-type impurity regions is 2.9×10 4 Ω. This is equal to the spreading resistance of the first p-type impurity region (the fin upper portion) shown in  FIG. 8B . 
     In order to compare the sheet resistance of the first p-type impurity region (fin upper portion) and that of the second p-type impurity region (the fin side portion) with each other, it is necessary to identify the junction depths thereof in addition to the spreading resistances thereof. The junction depth of the first p-type impurity region (the fin upper portion) can be evaluated by performing the SIMS (secondary ion mass spectrometry) measurement on a sample produced under the same condition as that for the fin-shaped semiconductor region shown in  FIG. 8A  using a separate bare silicon substrate.  FIG. 8D  shows the results of the SIMS measurement of the first p-type impurity region (the fin upper portion). It can be seen that as shown in  FIG. 8D , where the depth at which the boron concentration is 5×10 18  cm −3  is defined as the junction depth, the junction depth of the first p-type impurity region (the fin upper portion) is 28.5 nm. Moreover, the sheet resistance of the first p-type impurity region (the fin upper portion) can be evaluated by performing a four-point probe method on a sample produced under the same condition as that for the fin-shaped semiconductor region shown in  FIG. 8A  using a separate bare silicon substrate. Based on the results of the measurement by the four-point probe method, it was found that the sheet resistance of the first p-type impurity region (the fin upper portion) is 750Ω/□. On the other hand, the junction depth of the second p-type impurity region (the side portion of the semiconductor region) can be obtained, by using the results of the SSRM observation, as being the depth of the second p-type impurity region (the fin side portion) at which the color tone of the second p-type impurity region (the fin side portion) is the same as that of the first p-type impurity region (the fin upper portion) at a depth of 28.5 nm. In such a case, although there is a measurement error by the size of a dot in the SSRM picture, the junction depth of the second p-type impurity region (the fin side portion) can be identified with a precision of 28.5 nm±10%. 
     Herein, Rs=ρ/t, where Rs is the sheet resistance of the object, ρ is the specific resistance, t is the thickness (the junction depth), and ρw is the spreading resistance. The specific resistance ρ and the spreading resistance ρw are in principle in a one-to-one relationship, and are substantially in one-to-one relationship also in the measurement above, whereby there is a proportional relationship between Rs and ρw/t. From the experiment, the spreading resistance ρw of the first p-type impurity region (the fin upper portion) is 2.9×10 4 Ω, and the thickness (the junction depth) t thereof is 28.5 nm. In contrast, the spreading resistance ρw of the second p-type impurity region (the fin side portion) is 2.9×10 4 Ω, and the thickness (the junction depth) t thereof is 28.5 nm±10%. Thus, it can be seen that the sheet resistance of the first p-type impurity region (the fin upper portion) and that of the second p-type impurity region (the fin side portion) are in a range from 1:1.1 to 1:0.9. That is, in the first example, the sheet resistance of the first p-type impurity region (the fin upper portion) and that of the second p-type impurity region (the fin side portion) can be made equal to each other with a slight error of ±10%, which represents a conformal doping capability that cannot be achieved by the conventional techniques. 
       FIG. 9  shows how the low-resistance region  52  is formed by implanting a p-type impurity into the n-type semiconductor region  51  having fins whose aspect ratio is 0.37 and whose pitch is 1085 nm by plasma doping, and then performing a heat treatment to thereby activate the p-type impurity. 
       FIG. 10  shows how the low-resistance region  52  is formed by implanting a p-type impurity into the n-type semiconductor region  51  having fins whose aspect ratio is 1.72 and whose pitch is 196 nm by plasma doping, and then performing a heat treatment to thereby activate the p-type impurity. 
     Conformal doping was achieved with both p-type impurity plasma doping processes of  FIGS. 9 and 10 . 
     [Parameter Dependency of Threshold Value of Pressure During P-Type Impurity Plasma Doping] 
     As described above, the first example has illustrated that it is possible to control the amount of chipping of the fin corner portion of the fin-shaped PMISFET by performing a p-type impurity plasma doping while setting the pressure during the p-type impurity plasma doping to be less than or equal to 0.6 Pa, by way of an example where the material gas is B 2 H 6  diluted with He, the B 2 H 6  concentration in the material gas is 0.5% by mass, the chamber pressure is 0.35 Pa, and the source power (the plasma-generating high-frequency power) is 600 W, the bias voltage Vpp is 130 V, the substrate temperature is 20° C., and the plasma doping time is 200 seconds. Moreover, the first example has illustrated that it is possible to obtain a high conformal doping property by performing plasma doping while setting the pressure during the p-type impurity plasma doping to be less than or equal to 0.6 Pa by way of an example where the material gas is B 2 H 6  diluted with He, the B 2 H 6  concentration in the material gas is 0.8% by mass, the chamber pressure is 0.35 Pa, the source power (the plasma-generating high-frequency power) is 500 W, the bias voltage Vpp is 250 V, the substrate temperature is 20° C., and the plasma doping time is 60 seconds. Note however that the threshold value of the pressure during the p-type impurity plasma doping for obtaining a high conformal doping property while suppressing the amount of chipping of the fin corner portion of the fin-shaped PMISFET varies depending on other parameters, which will now be described. 
     While the first example has been described with respect to a case where the material gas is B 2 H 6  diluted with He and the B 2 H 6  concentration in the material gas is 0.5% by mass or 0.8% by mass, a case where the B 2 H 6  concentration is changed will next be described. In such a case, B 2 H 6  is diluted with a rare gas such as hydrogen or helium to 5% by mass or less, whereby the change in the B 2 H 6  concentration has substantially no influence on the threshold value of the pressure during plasma doping. In an application where an element is implanted in order to form an extension region or a source-drain region as in the present invention, it is desirable that B 2 H 6  is used with a high degree of dilution of about 2% by mass or less, whereby the B 2 H 6  concentration in the material gas has little influence on the amount of chipping of the fin corner portion. It is believed that the reason is that what chips off the fin corner portion is ions in a plasma, the majority of which is ions from the diluent gas, which are dominant as ions in a plasma, whereby even if the proportion (concentration) of boron in the diluent gas is changed within a range of 5% by mass or less (preferably, a range of 2% by mass or less), the proportion of boron ions in a plasma with respect to ions from the diluent gas does not substantially change. As described above, where the material gas is B 2 H 6  diluted with He and the B 2 H 6  concentration in the material gas is in a range of 2% by mass or less, the influence of the change in the B 2 H 6  concentration on the amount of chipping of the fin corner portion is negligible, and the threshold value of the pressure during plasma doping remained to be 0.6 Pa. That is, the cause of the etching of the fin corner portion in plasma doping is the ions from the diluent gas (helium ions in the first example), and the threshold value of the pressure during plasma doping is not dependent on the B 2 H 6  concentration, i.e., the boron concentration. 
     While the first example has been described with respect to a case where the bias voltage Vpp during the p-type impurity plasma doping is 130 V and 250 V, a case where the bias voltage Vpp is changed will next be described. With an apparatus for an application where an element is implanted in order to form an extension region or a source-drain region as in the present invention, the bias voltage Vpp is set to be less than or equal to 1000 V. In order to form an extension region, it is desirable that boron, or the like, is implanted into a region at a depth of greater than or equal to 5 nm and less than or equal to 15 nm from the semiconductor surface. Where a bias voltage Vpp of 250 V is used in the first example, the implantation depth (defined as the depth at which the boron concentration is 1×10 18  cm −3 ) is 9 nm. Even if the bias voltage Vpp is increased to about 500 V in order to make the implantation depth to be 15 nm, which is the maximum value desired for the extension region, the threshold value of the pressure during the p-type impurity plasma doping remained to be about 0.6 Pa and did not substantially change. Note however that where the bias voltage Vpp is increased to about 1000 V, which is the maximum output of the apparatus, it is preferred that the threshold value of the pressure during the p-type impurity plasma doping is set to be lower than 0.6 Pa, e.g., about 0.5 Pa. 
     Moreover, while the first example has been described above with respect to a case where the p-type impurity plasma doping time is 60 seconds and 200 seconds, a case where the plasma doping time is changed will next be described. There is a tendency that the threshold value of the pressure during the p-type impurity plasma doping becomes higher than 0.6 Pa as the p-type impurity plasma doping time is decreased, whereas the threshold value of the pressure during the p-type impurity plasma doping becomes lower than 0.6 Pa as the p-type impurity plasma doping time is increased. That is, although it may seem possible to perform a p-type impurity plasma doping in a pressure range higher than 0.6 Pa by decreasing the p-type impurity plasma doping time to be shorter than 60 seconds, this is not an effective method, for the following reasons, except when the p-type impurity plasma doping time is set to be very short. When the p-type impurity plasma doping is performed for less than 60 seconds using a pressure range higher than 0.6 Pa, the amount of chipping of the fin corner portion with respect to time does not change proportionally, but the amount of chipping is greater in an initial stage of the p-type impurity plasma doping, as shown in  FIG. 11 . Herein,  FIG. 11  shows the change in the amount of chipping of the fin corner portion over time where the p-type impurity plasma doping at a pressure of 0.9 Pa is performed for 60 seconds. Note that in  FIG. 11 , the amount of chipping of the fin corner portion is represented as the ratio of the radius of curvature of the fin corner portion (the upper corner) after doping with respect to that before doping. The greater the ratio is, the greater the amount of chipping is. Specifically, as shown in  FIG. 11 , with 28 seconds or more, the radius of curvature of the fin corner portion after plasma doping is twice or more of that before plasma doping, resulting in a large amount of chipping. Therefore, with a p-type impurity plasma doping using a long time region of 28 seconds or more, it is preferred that the pressure is set to be less than or equal to 0.6 Pa in order to suppress the amount of chipping of the fin corner portion. On the other hand, where the p-type impurity plasma doping time is less than 28 seconds, it is possible to perform plasma doping while reducing the amount of chipping of the fin corner portion even if the pressure is greater than or equal to 0.6 Pa. However, with plasma doping using such a short time region, there is a significant problem that it is difficult to ensure a dose uniformity across the substrate surface. Conversely, where the p-type impurity plasma doping time is set to be longer than 200 seconds, the productivity decreases. As described above, with the p-type impurity plasma doping using a time region from 30 seconds to 200 seconds, while there is an effect of ensuring a dose uniformity across the substrate surface without lowering the productivity, the amount of chipping of the fin corner portion will be large with a pressure range that has been used conventionally. In contrast, with the present invention, it is possible to reduce the amount of ions from the diluent gas (helium ions in the first example), which are believed to be the cause of etching, by setting the pressure during the p-type impurity plasma doping to be less than or equal to 0.6 Pa, thereby realizing a special effect that it is possible to achieve a high conformal doping property while suppressing the amount of chipping of the fin corner portion. 
     [Example of Conditional Acceptable Range in P-Type Impurity Plasma Doping] 
     In the present example, it is possible to obtain a high conformal doping property while suppressing the amount of chipping of the fin corner portion by performing a p-type impurity plasma doping under conditions where the pressure during the p-type impurity plasma doping is set to be greater than or equal to 0.6 Pa and less than or equal to 10 Pa, and the ion current density Ii (mA/cm 2 ) and the pressure during plasma doping P (Pa) satisfy Ii≦0.52 Ln(P)+0.36. Note that Ln represents a natural logarithm. 
     The present example used a sample similar to that of the first example as shown in  FIG. 6A  as an n-type fin-shaped semiconductor region (before plasma doping is performed) for examining the amount of chipping of the fin corner portion. That is, the height and the width of the fin are 120 nm and 160 nm, respectively, and the distance between fins is 210 nm. That is, the distance between the center of a fin in the width direction and that in an adjacent fin is 370 nm. Moreover, the radius of curvature of the fin corner portion (the region indicated by a broken line in the figure) is 8.7 nm. 
     First, the pressure and the source power during the p-type impurity plasma doping are changed to measure the electron temperature and the ion current density. Herein, the apparatus used for the measurement is a Langmuir probe manufactured by Scientific Systems (Trade name: Smart Probe). Moreover, the measurement probe is attached while being passed through 25 mm above the substrate surface so that the measurement can be done on a portion directly below. Twenty one locations within a range of a radius of 20 mm from the central position of a 300-mm substrate (specifically, 21 points with 1-mm intervals from the central position of the substrate to a position 20 mm from the central position to the side where the measurement probe is attached) are set as the measurement data detection points, with the average of the 21 measurement values being used as the measurement data. 
     Next, the amount of chipping of the fin corner portion is measured while changing the pressure during the p-type impurity plasma doping and the source power. The plasma doping condition is such that the bias power is 135 W (the bias voltage Vpp is 290 V), the material gas is B 2 H 6  diluted with He, the B 2 H 6  concentration in the material gas is 0.05% by mass, the total flow rate of the gas is 300 cc/min (standard state), and the bias application time is 60 seconds. Note that the boron implantation depth, defined as the depth at which the boron concentration is 5×10 18  cm −3 , is about 9 nm. 
       FIGS. 12A and 12B  represent various characteristics obtained from the measurement data described above. Specifically,  FIG. 12A  shows the range of ion current density where the radius of curvature of the fin corner portion after plasma doping is less than twice that before plasma doping and that where the radius of curvature of the fin corner portion after plasma doping is greater than or equal to twice that before plasma doping, in the range of pressure during the p-type impurity plasma doping from 0.6 Pa to 10 Pa. Where the pressure is in the range from 0.6 Pa to 10 Pa, the range of ion current density where the radius of curvature of the fin corner portion after plasma doping is reliably less than twice that before plasma doping is Ii≦0.52 Ln(P)+0.36 (Relational Expression 1: y=0.5202 Ln(x)+0.3600 in the figure). Note that R 2 =0.9858 in the figure represents the correlation coefficient between the measurement data and the approximate curve (Relational Expression 1), and the value of R 2  being close to 1 indicates that the correlation between Relational Expression 1 and the corresponding measurement data is very strong. On the other hand, the range of ion current density where the radius of curvature of the fin corner portion after plasma doping is reliably greater than or equal to twice that before plasma doping is Ii≧0.51 Ln(P)+0.80 (Relational Expression 2: y=0.5063 Ln(x)+0.7972 in the figure). Note that R 2 =0.9515 in the figure represents the correlation coefficient between the measurement data and the approximate curve (Relational Expression 2), and the value of R 2  being close to 1 indicates that the correlation between Relational Expression 2 and the corresponding measurement data is very strong. In the figure, the plot labeled “conventional PD (for planar)” represents the ion current density obtained where the p-type impurity plasma doping is performed with a pressure of 0.9 Pa as described above in  FIG. 11 . Herein, as shown in  FIG. 11 , when the p-type impurity plasma doping is performed for 60 seconds with a pressure of 0.9 Pa and the ion current density, the radius of curvature of the fin corner portion after plasma doping is greater than or equal to twice that before plasma doping. 
     Note that while the relationship between the ion current density and the pressure such that the radius of curvature of the fin corner portion after plasma doping is exactly twice that before plasma doping lies between the region represented by Relational Expression 1 and that represented by Relational Expression 2, the identification thereof requires an enormous effort. Therefore, the present example only identifies Relational Expression 1 where the radius of curvature of the fin corner portion after plasma doping is reliably less than twice that before plasma doping and Relational Expression 2 where the radius of curvature of the fin corner portion after plasma doping is reliably greater than or equal to twice that before plasma doping.  FIG. 12B  shows the relationship between the pressure and the electron temperature where the equations of Relational Expression 1 and Relational Expression 2 hold in the range of pressure during the p-type impurity plasma doping from 0.6 Pa to 10 Pa. It can be seen from  FIGS. 12A and 12B  that even if the electron temperature is at the same level, the amount of chipping of the fin corner portion may vary due to the difference in the ion current density, more specifically, that the amount of chipping of the fin corner portion can be better suppressed as the ion current density is smaller. 
     Note that as long as the radius of curvature after plasma doping is less than twice that before plasma doping, the influence of the radius of curvature of the fin corner portion on the performance of the semiconductor device is within an acceptable range and will not present problems. The reason is as follows. That is, of the current flowing from the source to the drain passing through a portion under the gate insulating film, it is more difficult for a current to flow through near the boundary between the first p-type impurity region (the fin upper portion) and the second p-type impurity region (the fin side portion) because the gap between the gate insulating film and the p-type impurity region increases (see  FIG. 31 ). Therefore, as long as the radius of curvature of the fin corner portion after plasma doping is less than twice that before plasma doping, the gap between the gate insulating film and the p-type impurity region is small, whereby the influence on the performance of the semiconductor device is within an acceptable range and will not present problems. Herein, the amount of chipping of the fin corner portion does not correspond directly to the size of the gap between the gate insulating film and the p-type impurity region, but the size of the gap between the gate insulating film and the p-type impurity region, which occurs unintentionally due to the p-type impurity plasma doping, is smaller than the amount of chipping of the fin corner portion. The reason is as follows. With respect to the radius of curvature of the fin corner portion in practice, as the distance from the gate insulating film (see, for example, the distance D in  FIG. 22 ) increases, the fin corner portion is more likely to be chipped off during plasma doping, thus increasing the radius of curvature, whereas as the distance from the gate insulating film decreases, the fin corner portion is less likely to be chipped off, thus decreasing the radius of curvature. That is, the radius of curvature of the fin corner portion changes according to the distance from the gate insulating film, and the radius of curvature of the fin corner portion tends to decrease as the distance decreases, whereby there are cases where the size of the gap between the gate insulating film and the p-type impurity region is smaller than the amount of chipping of the fin corner portion. 
     Conversely, if the radius of curvature of the fin corner portion after plasma doping is greater than or equal to twice that before plasma doping, the gap between the gate insulating film and the p-type impurity region becomes so large that the influence on the performance of the semiconductor device exceeds the acceptable range even if it is taken into consideration that the radius of curvature of the fin corner portion changes according to the distance from the gate insulating film. 
       FIG. 13  schematically shows a cross-sectional shape of a fin-shaped semiconductor region (strictly, the semiconductor region  51  having fins) after the p-type impurity plasma doping is performed in the present example. The plasma doping condition is such that, for example, the material gas is B 2 H 6  diluted with He, the B 2 H 6  concentration in the material gas is 0.05% by mass, the chamber pressure is 0.9 Pa, the source power (the plasma-generating high-frequency power) is 1000 W, the bias voltage Vpp is 290 V, the substrate temperature is 20° C., and the plasma doping time is 60 seconds. An ICP method, for example, was used as a plasma generating method. Note that in the present example, in order to make the amount of implanted ions incident on the fin upper surface very small to suppress the amount of chipping of the fin corner portion, the chamber pressure is set to be as small as 0.9 Pa and the source power is set to be as small as 1000 W, thus setting the ion current density to be 0.09 mA/cm 2 , a very small value for an ICP method. The radius of curvature of the fin corner portion after the p-type impurity plasma doping is performed under such a condition ( FIG. 13 ) is 15.2 nm. That is, in the present example, the difference between the radius of curvature of the fin corner portion before the p-type impurity plasma doping and that after the p-type impurity plasma doping is 6.5 nm, and the amount of chipping (the amount of increase in the radius of curvature) per minute is 6.5 nm. Moreover, in the present example, the radius of curvature of the fin corner portion after plasma doping is less than twice that before plasma doping, and it can therefore be seen that the amount of chipping of the fin corner portion is acceptably small. 
     Note that it can be seen that if the ion current density during the p-type impurity plasma doping is less than or equal to 0.5 mA/cm 2  as shown in  FIG. 12A , the influence of the amount of chipping of the fin corner portion on the performance of the semiconductor device is within an acceptable range and will not present problems. In view of this, it is understood that it is preferred to set the pressure during the p-type impurity plasma doping to be less than or equal to 0.6 Pa as described above in the first example. 
     [Suppression of Amount of Chipping of Fin Corner Portion of Fin-Shaped NMISFET] 
     Next, the suppression of the amount of chipping of the fin corner portion of the fin-shaped NMISFET in the first example will be described with reference to  FIGS. 14A and 14B . 
       FIG. 14A  schematically shows a cross-sectional shape of the fin-shaped semiconductor region (strictly, a semiconductor region  951  having fins) before an n-type impurity plasma doping. Herein, the height and the width of the fin are 120 nm and 160 nm, respectively, and the distance between fins is 210 nm. That is, the distance between the center of a fin in the width direction and that in an adjacent fin is 370 nm. Moreover, the radius of curvature of the fin corner portion (the region indicated by a broken line in the figure) is 8.7 nm. Note that the fin corner portion is in a shape with a curvature, but not a completely right-angled shape, even before the n-type impurity plasma doping because the fin corner portion is chipped off slightly in the dry etching step and the cleaning step before the n-type impurity plasma doping. 
       FIG. 14B  schematically shows a cross-sectional shape of a fin-shaped semiconductor region (strictly, the semiconductor region  951  having fins) after an n-type impurity plasma doping. The n-type impurity plasma doping condition is such that, for example, the material gas is AsH 3  diluted with He, the AsH 3  concentration in the material gas is 0.05% by mass, the chamber pressure is 0.4 Pa, the source power (the plasma-generating high-frequency power) is 2000 W, the bias voltage Vpp is 290 V, the substrate temperature is 20° C., and the plasma doping time is 60 seconds. An ICP method, for example, was used as a plasma generating method. Herein, in order to make the amount of implanted ions incident on the fin upper surface very small to control the amount of chipping of the fin corner portion, the chamber pressure is set to be 0.4 Pa, a very small value for an ICP method. The radius of curvature of the fin corner portion (the region indicated by a broken line in the figure) after the n-type impurity plasma doping is performed under such a condition is 16.2 nm. That is, in the first example, the difference between the radius of curvature of the fin corner portion before the n-type impurity plasma doping and that after the n-type impurity plasma doping is 7.5 nm, and the radius of curvature of the fin corner portion after the n-type impurity plasma doping is less than twice that before the n-type impurity plasma doping, indicating that the amount of chipping (the amount of increase in the radius of curvature) is suppressed sufficiently. 
     Next, how the amount of chipping changes when the pressure during the n-type impurity plasma doping, among other conditions, is changed within a range of 0.4 Pa or less. 
     First, a case will be described where the n-type impurity plasma doping condition is such that, for example, the material gas is AsH 3  diluted with He, the AsH 3  concentration in the material gas is 0.5% by mass, the chamber pressure is 0.35 Pa, the source power (the plasma-generating high-frequency power) is 600 W, the bias voltage Vpp is 130 V, the substrate temperature is 20° C., and the plasma doping time is 200 seconds. An ICP method, for example, was used as a plasma generating method. Herein, in order to make the amount of implanted ions incident on the fin upper surface very small to suppress the amount of chipping of the fin corner portion, the chamber pressure is set to be 0.35 Pa, a very small value for an ICP method. The radius of curvature of the fin corner portion after the n-type impurity plasma doping is performed under such a condition is greater than 10.6 nm and less than 17.4 nm. That is, in the first example, the difference between the radius of curvature of the fin corner portion before the n-type impurity plasma doping and that after the n-type impurity plasma doping is greater than 1.9 nm and less than 8.7 nm. It can be seen that since this is the amount of change over a plasma doping time of 200 seconds, the amount of chipping (the amount of increase in the radius of curvature) per minute is greater than 0.6 nm and less than 2.6 nm, and the amount of chipping is suppressed sufficiently. 
     Next, another case will be described where the n-type impurity plasma doping condition is such that, for example, the material gas is AsH 3  diluted with He, the AsH 3  concentration in the material gas is 0.5% by mass, the chamber pressure is 0.30 Pa, the source power (the plasma-generating high-frequency power) is 600 W, the bias voltage Vpp is 130 V, the substrate temperature is 20° C., and the plasma doping time is 200 seconds. An ICP method, for example, was used as a plasma generating method. Herein, in order to further decrease the amount of implanted ions incident on the fin upper surface to suppress the amount of chipping of the fin corner portion to be very small, the chamber pressure is set to be 0.30 Pa, a very small value for an ICP method. The radius of curvature of the fin corner portion after the n-type impurity plasma doping is performed under such a condition is about 10.6 nm. That is, in the present example, the difference between the radius of curvature of the fin corner portion before the n-type impurity plasma doping and that after the n-type impurity plasma doping is about 1.9 nm. It can be seen that since this is the amount of change over a plasma doping time of 200 seconds, the amount of chipping (the amount of increase in the radius of curvature) per minute is about 0.6 nm, and the amount of chipping is very small. The amount of chipping is substantially equal to that in a case where the plasma doping condition is such that, for example, the material gas is B 2 H 6  diluted with He, the B 2 H 6  concentration in the material gas is 0.5% by mass, the chamber pressure is 0.35 Pa, the source power (the plasma-generating high-frequency power) is 600 W, the bias voltage Vpp is 130 V, the substrate temperature is 20° C., and the plasma doping time is 200 seconds (the amount of chipping (the amount of increase in the radius of curvature) per minute was about 0.6 nm also in this case). That is, by setting the pressure during the plasma doping using AsH 3  to be 0.30 Pa, which is less than 0.35 Pa, it is possible to realize an amount of chipping that is substantially equal to the very small amount of chipping obtained by setting the pressure during the plasma doping using B 2 H 6  to be 0.35 Pa. 
     [Conformal Doping Property of Fin-Shaped NMISFET] 
     Next, the sheet resistance of the first n-type impurity region (the impurity region of the fin upper portion) and that of the second n-type impurity region (the impurity region of the fin side portion) in the fin-shaped NMISFET of the first example will be described with reference to the drawings. The n-type impurity plasma doping condition is such that, for example, the material gas is AsH 3  diluted with He, the AsH 3  concentration in the material gas is 0.8% by mass, the chamber pressure is 0.30 Pa, the source power (the plasma-generating high-frequency power) is 500 W, the bias voltage Vpp is 250V, the substrate temperature is 20° C., and the plasma doping time is 60 seconds. An ICP method, for example, was used as a plasma generating method. Moreover, the chamber pressure is set to be 0.30 Pa, a very small value for an ICP method, in order to make the amount of implanted ions incident on the fin upper surface very small so that the amount of doping by the adsorbed species is the main factor influencing the implantation dose of the first n-type impurity region (the fin upper portion); in other words, so that the implantation dose of the first n-type impurity region (the fin upper portion) approaches that of the second n-type impurity region (the fin side portion) where the main factor is the amount of doping by the adsorbed species in the first place. The amount of chipping of the fin corner portion in this case is also very small, and about the same as that described above in Suppression Of Amount Of Chipping Of Fin Corner Portion Of Fin-Shaped NMISFET.  FIG. 15A  is a diagram schematically showing a cross-sectional shape of the fin-shaped semiconductor region (strictly, the semiconductor region  951  having fins) before the n-type impurity plasma doping,  FIG. 15B  is an enlarged view thereof,  FIG. 15C  is a perspective view of the fin-shaped semiconductor region shown in  FIGS. 15A and 15B , and  FIG. 15D  is an enlarged view thereof. The height and the width of the fin-shaped semiconductor region shown in  FIGS. 15A-15D  are 128 nm and 342 nm, respectively, and the distance between fins is 743 nm. That is, the distance between the center of a fin in the width direction and that in an adjacent fin is 1085 nm. 
       FIG. 16  shows how a low-resistance region  952  is formed by implanting arsenic into silicon of the p-type fin-shaped semiconductor region (strictly, the semiconductor region  951  having fins) by plasma doping and then performing a heat treatment to thereby electrically activate arsenic in silicon. As shown in  FIG. 16 , the low-resistance region  952  is formed not only in the first n-type impurity region (fin upper portion) but also in the second n-type impurity region (the fin side portion). Also with the fin-shaped NMISFET shown in  FIG. 16 , as with the fin-shaped PMISFET shown in  FIG. 8A , the sheet resistance of the first n-type impurity region (the fin upper portion) and that of the second n-type impurity region (the fin side portion) can be made equal to each other with a slight error of ±10%, which represents a conformal doping capability that cannot be achieved by the conventional techniques. 
       FIG. 17A  shows how the low-resistance region  952  is formed by implanting an n-type impurity into the p-type semiconductor region  951  having fins whose aspect ratio is 0.37 and whose pitch is 1085 nm by plasma doping, and then performing a heat treatment to thereby activate the n-type impurity. 
       FIG. 17B  shows how the low-resistance region  952  is formed by implanting an n-type impurity into the p-type semiconductor region  951  having fins whose aspect ratio is 1.72 and whose pitch is 196 nm by plasma doping, and then performing a heat treatment to thereby activate the n-type impurity. 
     Conformal doping was achieved with both n-type impurity plasma doping processes of  FIGS. 17A and 17B . 
     [Parameter Dependency of Threshold Value of Pressure During N-Type Impurity Plasma Doping] 
     As described above, the first example has illustrated that it is possible to control the amount of chipping of the fin corner portion of the fin-shaped NMISFET by performing an n-type impurity plasma doping while setting the pressure during the n-type impurity plasma doping to be less than or equal to 0.4 Pa, by way of an example where the material gas is AsH 3  diluted with He, the AsH 3  concentration in the material gas is 0.5% by mass, the chamber pressure is 0.30 Pa, and the source power (the plasma-generating high-frequency power) is 600 W, the bias voltage Vpp is 130 V, the substrate temperature is 20° C., and the plasma doping time is 200 seconds. Moreover, the first example has illustrated that it is possible to obtain a high conformal doping property by performing plasma doping while setting the pressure during the n-type impurity plasma doping to be less than or equal to 0.4 Pa by way of an example where the material gas is AsH 3  diluted with He, the AsH 3  concentration in the material gas is 0.8% by mass, the chamber pressure is 0.30 Pa, the source power (the plasma-generating high-frequency power) is 500 W, the bias voltage Vpp is 250 V, the substrate temperature is 20° C., and the plasma doping time is 60 seconds. Note however that the threshold value of the pressure during the n-type impurity plasma doping for obtaining a high conformal doping property while suppressing the amount of chipping of the fin corner portion of the fin-shaped NMISFET (the amount of increase in the radius of curvature of the fin corner portion) varies depending on other parameters, which will now be described. 
     While the first example has been described with respect to a case where the material gas is AsH 3  diluted with He and the AsH 3  concentration in the material gas is 0.05% by mass, 0.5% by mass or 0.8% by mass, a case where the AsH 3  concentration is changed will next be described. 
     In plasma doping, B 2 H 6 , PH 3 , AsH 3 , or the like, is diluted with a rare gas such as hydrogen or helium to 5% by mass or less, depending on the impurity to be implanted, e.g., boron, phosphorus, arsenic, etc. Particularly, in an application where an element is implanted in order to form an extension region or a source-drain region as in the present invention, it is desirable that boron, phosphorus, arsenic, or the like, is implanted in a dose range from 5×10 14  cm −2  to 5×10 15  cm −2 . On the other hand, where B 2 H 6 , PH 3 , AsH 3 , or the like, is used while being diluted to 2% by mass or more, there is likely to be a problem that the dose of boron, phosphorus, arsenic, or the like, will be as much as 5×10 15  cm −2  or more. Therefore, it is desirable to use B 2 H 6 , PH 3 , AsH 3 , or the like, with a high degree of dilution of about 2% by mass or less. In such a case, ions from the diluent gas account for 98% by mass or more of the ion source in a plasma. Therefore, for example, the concentration of B 2 H 6 , PH 3 , AsH 3 , or the like, in the material gas diluted with a diluent gas such as hydrogen or helium can be changed within a range of 2% by mass or less. 
     The atomic weight of the diluent gas, e.g., helium, is 4.0, and the atomic weight of arsenic is 74.9, indicating that arsenic is an element that is about 18.7 times heavier than helium. The n-type impurity plasma doping of the first example has been described with respect to cases where the material gas is AsH 3  diluted with He, and the AsH 3  concentration in the material gas is 0.05% by mass, 0.5% by mass and 0.8% by mass. In such cases, ions from the diluent gas account for 99.95% by mass, 99.5% by mass and 99.2% by mass, respectively, of the ion source in a plasma. Herein, what chips off the fin corner portion is ions in a plasma, the majority of which is ions of the diluent gas, e.g., helium, which are dominant as ions in a plasma, and the heavier the ions chipping off the fin corner portion are, the greater the amount of chipping of the fin corner portion becomes. On the other hand, when the arsenic concentration in the material gas is increased, the proportion of arsenic ions with respect to the ion source in a plasma increases. Therefore, if the amount of arsenic, which is a heavy element, increases in the material gas, the fin corner portion is more likely to be chipped off during the n-type impurity plasma doping. Note however that when the AsH 3  concentration was within a range from 0.05% by mass to 0.8% by mass, no significant increase was observed for the amount of chipping of the fin corner portion due to an increase in the amount of arsenic. That is, at least when the AsH 3  concentration is within the above range, the chamber pressure is the primary factor that dictates the amount of chipping of the fin corner portion, and the AsH 3  concentration has little influence on the amount of chipping of the fin corner portion. Conversely, if the AsH 3  concentration substantially exceeds 0.8% by mass, e.g., if it is as high as over 2% by mass, it is preferred to set the threshold value of the pressure during the plasma doping for suppressing the amount of chipping of the fin corner portion to be lower than 0.4 Pa, e.g., about 0.3 Pa. 
     While the first example has been described with respect to a case where the bias voltage Vpp during the n-type impurity plasma doping is 290 V, a case where the bias voltage Vpp is changed will next be described. With an apparatus for an application where an element is implanted in order to form an extension region or a source-drain region as in the present invention, the bias voltage Vpp is set to be less than or equal to 1000 V. In order to form an extension region, it is desirable that arsenic, phosphorus, or the like, is implanted into a region at a depth of greater than or equal to 5 nm and less than or equal to 15 nm from the semiconductor surface. Herein, where the bias voltage Vpp is increased to about 1000 V, which is the maximum output of the apparatus, for the adjustment of the arsenic implantation depth, it is preferred that the threshold value of the pressure during the n-type impurity plasma doping is set to be lower than 0.4 Pa, e.g., about 0.3 Pa. 
     Moreover, while the first example has been described above with respect to a case where the n-type impurity plasma doping time is 60 seconds, a case where the n-type impurity plasma doping time is changed will next be described. There is a tendency that the threshold value of the pressure during the n-type impurity plasma doping becomes higher than 0.4 Pa as the n-type impurity plasma doping time is decreased, whereas the threshold value of the pressure during the n-type impurity plasma doping becomes lower than 0.4 Pa as the n-type impurity plasma doping time is increased. That is, it may seem possible to perform the n-type impurity plasma doping in a pressure range higher than 0.4 Pa by decreasing the n-type impurity plasma doping time to be shorter than 60 seconds. In such a case, however, there is an increased chipping of the fin corner portion during the initial stage of the n-type impurity plasma doping, as with the p-type impurity plasma doping, whereby it is necessary to significantly shorten the n-type impurity plasma doping time. Even if the amount of chipping of the fin corner portion (the amount of increase in the radius of curvature) is reduced by significantly shortening the n-type impurity plasma doping time, it will be difficult to ensure a dose uniformity across the substrate surface when the n-type impurity plasma doping is performed for such a short period of time. Conversely, when the n-type impurity plasma doping time is too long, the productivity decreases. In contrast, with the present invention, it is possible to reduce the amount of ions, which are believed to be the cause of etching of the fin corner portion, by setting the pressure during the n-type impurity plasma doping to be less than or equal to 0.4 Pa, thereby realizing a special effect that it is possible to achieve a high conformal doping property while suppressing the amount of chipping of the fin corner portion. 
     [Example of Conditional Acceptable Range in N-Type Impurity Plasma Doping] 
     In the present example, it is possible to obtain a high conformal doping property while suppressing the amount of chipping of the fin corner portion by performing an n-type impurity plasma doping under conditions where the pressure during the n-type impurity plasma doping is set to be greater than or equal to 0.4 Pa and less than or equal to 10 Pa, and the ion current density Ii (mA/cm 2 ) and the pressure during plasma doping P (Pa) satisfy Ii≦0.53 Ln(P)+0.59 in the region where 0.4≦P≦1.2 and Ii≦0.67 in the region where 1.2≦P≦10. Note that Ln represents a natural logarithm. 
     The present example used a sample similar to that of the first example as shown in  FIG. 14A  as a p-type fin-shaped semiconductor region (before plasma doping is performed) for examining the amount of chipping of the fin corner portion. That is, the height and the width of the fin are 120 nm and 160 nm, respectively, and the distance between fins is 210 nm. That is, the distance between the center of a fin in the width direction and that in an adjacent fin is 370 nm. Moreover, the radius of curvature of the fin corner portion (the region indicated by a broken line in the figure) is 8.7 nm. 
     First, the pressure and the source power during the n-type impurity plasma doping are changed to measure the electron temperature and the ion current density. Herein, the apparatus used for the measurement is a Langmuir probe manufactured by Scientific Systems (Trade name: Smart Probe). Moreover, the measurement probe is attached while being passed through 25 mm above the substrate surface so that the measurement can be done on a portion directly below. Twenty one locations within a range of a radius of 20 mm from the central position of a 300-mm substrate (specifically, 21 points with 1-mm intervals from the central position of the substrate to a position 20 mm from the central position to the side where the measurement probe is attached) are set as the measurement data detection points, with the average of the 21 measurement values being used as the measurement data. 
     Next, the amount of chipping of the fin corner portion is measured while changing the pressure during the n-type impurity plasma doping and the source power. The plasma doping condition is such that the bias voltage Vpp is 290 V, the material gas is AsH 3  diluted with He, the AsH 3  concentration in the material gas is 0.05% by mass, the total flow rate of the gas is 300 cc/min (standard state), and the bias application time is 60 seconds. 
       FIGS. 18A and 18B  represent various characteristics obtained from the measurement data described above. Specifically,  FIG. 18A  shows the range of ion current density where the radius of curvature of the fin corner portion after plasma doping is less than twice that before plasma doping and that where the radius of curvature of the fin corner portion after plasma doping is greater than or equal to twice that before plasma doping, in the range of pressure during the n-type impurity plasma doping from 0.4 Pa to 10 Pa. Where the pressure is in the range from 0.4 Pa to 10 Pa, the range of ion current density where the radius of curvature of the fin corner portion after plasma doping is reliably less than twice that before plasma doping is Ii≦0.53 Ln(P)+0.59 (Relational Expression 3: y=0.5253 Ln(x)+0.5869 in the figure) in the region where 0.4≦P≦1.2, and Ii≦0.67 (Relational Expression 4: y=0.003x+0.6727 in the figure) in the range where 1.2≦P≦10. On the other hand, the range of ion current density where the radius of curvature of the fin corner portion after plasma doping is reliably greater than or equal to twice that before the n-type impurity plasma doping is Ii≧1.04 Ln(P)+1.09 (Relational Expression 5: y=1.0362 Ln(x)+1.0935 in the figure) in the region where 0.4≦P≦0.95, and Ii≧1.04 (Relational Expression 6: y=1.04295 as obtained by substituting x=0.95 into y=−0.019x+1.061 in the figure) in the region where 0.95≦P≦10. 
     Note that while the relationship between the ion current density and the pressure such that the radius of curvature of the fin corner portion after plasma doping is exactly twice that before plasma doping lies between the region represented by Relational Expressions 3 and 4 and that represented by Relational Expressions 5 and 6, the identification thereof requires an enormous effort. Therefore, the present example only identifies Relational Expressions 3 and 4 where the radius of curvature of the fin corner portion after plasma doping is reliably less than twice that before plasma doping and Relational Expressions 5 and 6 where the radius of curvature of the fin corner portion after plasma doping is reliably greater than or equal to twice that before plasma doping.  FIG. 18B  shows the relationship between the pressure and the electron temperature where the equations of Relational Expressions 3 to 6 hold in the range of pressure during the n-type impurity plasma doping from 0.4 Pa to 10 Pa. It can be seen from  FIGS. 18A and 18B  that even if the electron temperature is at the same level, the amount of chipping of the fin corner portion may vary due to the difference in the ion current density, more specifically, that the amount of chipping of the fin corner portion can be better suppressed as the ion current density is smaller. 
     As long as the radius of curvature after plasma doping is less than twice that before plasma doping, the influence of the radius of curvature of the fin corner portion on the performance of the semiconductor device is within an acceptable range and will not present problems. The reason is as follows. That is, of the current flowing from the source to the drain passing through a portion under the gate insulating film, it is more difficult for a current to flow through near the boundary between the first n-type impurity region (the fin upper portion) and the second n-type impurity region (the fin side portion) because the gap between the gate insulating film and the n-type impurity region increases (see  FIG. 31 ). Therefore, as long as the radius of curvature of the fin corner portion after plasma doping is less than twice that before plasma doping, the gap between the gate insulating film and the n-type impurity region is small, whereby the influence on the performance of the semiconductor device is within an acceptable range and will not present problems. Herein, the amount of chipping of the fin corner portion does not correspond directly to the size of the gap between the gate insulating film and the n-type impurity region, but the size of the gap between the gate insulating film and the n-type impurity region, which occurs unintentionally due to the n-type impurity plasma doping, is slightly smaller than the amount of chipping of the fin corner portion. The reason is as described above in Example Of Conditional Acceptable Range In P-Type Impurity Plasma Doping. 
     Conversely, if the radius of curvature of the fin corner portion after plasma doping is greater than or equal to twice that before plasma doping, the gap between the gate insulating film and the n-type impurity region becomes so large that the influence on the performance of the semiconductor device exceeds the acceptable range. 
       FIG. 19  schematically shows a cross-sectional shape of a fin-shaped semiconductor region (strictly, the semiconductor region  951  having fins) after the n-type impurity plasma doping is performed in the present example. The plasma doping condition is such that, for example, the material gas is AsH 3  diluted with He, the AsH 3  concentration in the material gas is 0.05% by mass, the chamber pressure is 0.4 Pa, the source power (the plasma-generating high-frequency power) is 2000 W, the bias voltage Vpp is 290 V, the substrate temperature is 20° C., and the plasma doping time is 60 seconds. An ICP method, for example, was used as a plasma generating method. Note that in the present example, in order to make the amount of implanted ions incident on the fin upper surface very small to suppress the amount of chipping of the fin corner portion, the chamber pressure is set to be as small as 0.4 Pa and the ion current density is set to be 0.18 mA/cm 2 , a very small value for an ICP method, though the source power is set to be as large as 2000 W. The radius of curvature of the fin corner portion after the n-type impurity plasma doping is performed under such a condition ( FIG. 19 ) is 16.2 nm. That is, in the present example, the difference between the radius of curvature of the fin corner portion before the n-type impurity plasma doping and that after the n-type impurity plasma doping is 7.5 nm, and the amount of chipping (the amount of increase in the radius of curvature) per minute is 7.5 nm. Moreover, in the present example, the radius of curvature of the fin corner portion after plasma doping is less than twice that before plasma doping, and it can therefore be seen that the amount of chipping of the fin corner portion is acceptably small. 
     Note that it can be seen that if the ion current density during the n-type impurity plasma doping is less than or equal to 0.1 mA/cm 2  as shown in  FIG. 18A , the influence of the amount of chipping of the fin corner portion on the performance of the semiconductor device is within an acceptable range and will not present problems. In view of this, it is understood that it is preferred to set the pressure during the n-type impurity plasma doping to be less than or equal to 0.4 Pa as described above in the first example. 
     As opposed to the above approach, where the n-type impurity plasma doping is performed while setting the chamber pressure to be 10 Pa or more, one may set the source power to be very low (e.g., 25 w) and thus set the ion current density to be very small, to thereby suppress the radius of curvature of the fin corner portion after plasma doping to be less than or equal to twice that before plasma doping. However, setting the source power to be so low is equal to forcibly decreasing the ion current density by placing a high load on the plasma doping apparatus. Then, it may become no longer possible to maintain a plasma in the chamber. Therefore, it is not practical for one to attempt to reduce the amount of chipping of the fin corner portion by setting the pressure during the n-type impurity plasma doping to be 10 Pa or more. 
     Second Example 
       FIG. 20A  is a perspective view of another example (second example) of a fin-shaped CMISFET, and  FIG. 20B  is an enlarged perspective view showing an NMISFET of the fin-shaped CMISFET shown in  FIG. 20A . In  FIGS. 20A and 20B , like elements to those of the fin-shaped CMISFET shown in  FIGS. 1A-1E  are denoted by like reference numerals and will not be described redundantly. 
     First, referring to  FIG. 20B , the chipping of the fin corner portion (the upper corner) of a fin-shaped NMISFET, and the specific resistance of the n-type impurity region in the fin upper portion and that of the n-type impurity region in the fin side portion will be described. They similarly apply to a fin-shaped PMISFET. While “specific resistance (resistivity)” is mainly used in the following description, the magnitude of the resistance can be represented by “sheet resistance” or “spreading resistance” instead of “specific resistance”. As shown in  FIG. 20B , the gate electrode  15   c  is formed so as to extend across the p-type fin-shaped semiconductor region  913   c  having the n-type impurity region  917   a  in an upper portion thereof and the n-type impurity region  917   b  in a side portion thereof, with the gate insulating film  914   c  interposed therebetween. Herein, the height and the width of the p-type fin-shaped semiconductor region  913   c  (and those of the n-type fin-shaped semiconductor region  13   b ) are about 50 nm and 20 nm, respectively. That is, the present example is directed to a fin-shaped CMISFET where the fin width is reduced to about 20 nm, which is a value on the practically required level. In  FIG. 20B , a, b, c and d denote corners on the source side along the inner wall of the gate insulating film  914   c  having a pommel horse shape, and a″, b″, c″ and d″ are obtained by translating the corners a, b, c and d to the source-side end surface of the p-type fin-shaped semiconductor region  913   c.    
     In the present example, the distance G between the corner b″ and the upper-portion n-type impurity region  917   a , i.e., the distance G between the corner c″ and the upper-portion n-type impurity region  917   a , is 0.6 nm. 
     The corners a, b, c and d on the source side along the inner wall of the gate insulating film  914   c  having a pommel horse shape are covered and protected by the gate insulating film  914   c  and the gate electrode  15   c  in the plasma doping process and the following cleaning step. On the other hand, the fin corner portion of the p-type fin-shaped semiconductor region  913   c  which is not covered by the gate insulating film  914   c  and the gate electrode  15   c  is chipped off in the plasma doping process and the following cleaning step. Herein, the above distance G of 0.6 nm is the amount of chipping of the fin corner portion in the plasma doping process and the following cleaning step (not including the amount of chipping before plasma doping), and is suppressed to be very small though it is not zero. 
     Also in the present example, as in the first example, the specific resistance of the n-type impurity region  917   b  in the fin side portion is substantially equal to the specific resistance of the n-type impurity region  917   a  in the fin upper portion. 
     That is, the fin-shaped CMISFET of the present example also realizes a characteristic device configuration where the amount of chipping of the fin corner portion is small and the specific resistance of the impurity region in a fin side portion is substantially equal to that of the impurity region in a fin upper portion. 
     While the method for making the specific resistance of the impurity region in the fin side portion substantially equal to that of the impurity region in the fin upper portion has been described above in Mechanism Of Present Invention, this mechanism is effective also in the present example where the fin width is reduced to about 20 nm. 
     In view of this, referring to  FIGS. 21A-21C , the amount of chipping of the fin corner portion in a case where the fin width is as small as about 20 nm will now be described in greater detail.  FIG. 21A  shows the outline of a cross section including the corners a, b, c and d on the source side along the inner wall of the gate insulating film  914   c  having a pommel horse shape,  FIG. 21B  shows the outline of a cross section of the p-type fin-shaped semiconductor region  913   c  (hereinafter also referred to simply as a “fin”) outside the gate insulating film  914   c , and  FIG. 21C  shows the fin corner portion shown in  FIG. 21A  and the fin corner portion shown in  FIG. 21B  superimposed on each other. 
     As shown in  FIG. 21A , before the plasma doping process, the fin height is 50 nm, the fin width is 18 nm, the taper angle of the fin is 88°, the width of the flat portion of the fin upper surface is 13 nm, and the radius of curvature of the fin corner portion is 1.8 nm. Note that the fin corner portion is in a shape with a curvature, but not a completely right-angled shape, even before the n-type impurity plasma doping process because the fin corner portion is chipped off slightly in the fin-forming dry etching step and the cleaning step before the n-type impurity plasma doping process. 
     As shown in  FIG. 21B , after the plasma doping process (strictly, at the point when the device is completed after the subsequent cleaning step), the fin height is 50 nm, the fin width is 18 nm, the taper angle of the fin is 88°, the width of the flat portion of the fin upper surface is 10 nm, and the radius of curvature of the fin corner portion is 3.2 nm. 
     Moreover, as shown in  FIG. 21C , the amount of chipping of the fin corner portion, i.e., the distance G, in the plasma doping process and the following cleaning step is 0.6 nm. 
     A plasma doping condition capable of producing a fin-shaped NMISFET in which the amount of chipping of the fin corner portion is small, and the specific resistance of the impurity region in the fin side portion is substantially equal to that of the impurity region in the fin upper portion, as described above, is such that, for example, the material gas is AsH 3  (arsine) diluted with He (helium), the AsH 3  concentration in the material gas is 0.5% by mass, the total flow rate of the material gas is 100 cm 3 /min (standard state), the chamber pressure is 0.30 Pa, the source power (the plasma-generating high-frequency power) is 500 W, the bias voltage (Vpp) is 250 V, the substrate temperature is 30° C., and the plasma doping time is 60 seconds. An ICP method, for example, was used as a plasma generating method. Herein, in order to make the amount of implanted ions incident on the fin upper surface very small to control the amount of chipping of the fin corner portion, and to make the specific resistance of the impurity region in the fin side portion substantially equal to that of the impurity region in the fin upper portion, the chamber pressure is set to be 0.30 Pa, a very small value for an ICP method. 
     Moreover, as described above, the radius of curvature of the fin corner portion of the fin-shaped NMISFET in the example fin-shaped CMISFET is 1.8 nm before the plasma doping process, but the radius of curvature is 3.2 nm when the device is completed, indicating that the amount of increase in the radius of curvature due to the chipping in the plasma doping process and the following cleaning step is 1.4 nm. In other words, the radius of curvature of the fin corner portion at the point when the device is completed after the plasma doping process, etc., is suppressed to be about 1.8 times that before the plasma doping process, and the amount of chipping of the fin corner portion (the amount of increase in the radius of curvature) is within an acceptable range. 
     The description has been directed to the fin-shaped NMISFET of the example fin-shaped CMISFET. Also with the fin-shaped PMISFET, however, the amount of chipping of the fin corner portion, i.e., the distance G is about 0.6 nm, and the specific resistance of the impurity region in the fin side portion is substantially equal to that of the impurity region in the fin upper portion. A plasma doping condition capable of producing such a fin-shaped PMISFET is, for example, such that the material gas is B 2 H 6  (diborane) diluted with He (helium), the B 2 H 6  concentration in the material gas is 0.5% by mass, the total flow rate of the material gas is 100 cm 3 /min (standard state), the chamber pressure is 0.35 Pa, the source power (the plasma-generating high-frequency power) is 500 W, the bias voltage (Vpp) is 250 V, the substrate temperature is 30° C., and the plasma doping time is 60 seconds. An ICP method, for example, was used as a plasma generating method. Herein, in order to make the amount of implanted ions incident on the fin upper surface very small to control the amount of chipping of the fin corner portion, and to make the specific resistance of the impurity region in the fin side portion substantially equal to that of the impurity region in the fin upper portion, the chamber pressure is set to be 0.35 Pa, a very small value for an ICP method. 
     As described above, where boron is used as a p-type impurity for forming the fin-shaped PMISFET and arsenic, which has a greater mass than boron, is used as an n-type impurity for forming the fin-shaped NMISFET, it is a characteristic of the present example that the pressure during plasma doping for forming the fin-shaped NMISFET is set to be less than or equal to that during plasma doping for forming the fin-shaped PMISFET, as can be seen from a comparison between the above plasma doping condition for forming the fin-shaped PMISFET and that for forming the fin-shaped NMISFET. Then, it is possible to make the amount of chipping of the fin corner portion for the fin-shaped PMISFET substantially equal to that for the fin-shaped NMISFET, and to make the specific resistance of the impurity region in the fin side portion substantially equal to that of the impurity region in the fin upper portion for both of the fin-shaped PMISFET and the fin-shaped NMISFET (note however that the level of specific resistance of the impurity region differs between the fin-shaped PMISFET and the fin-shaped NMISFET). Where the mass of the p-type impurity is greater than the mass of the n-type impurity, similar effects to those of the present example can be obtained by setting the pressure during plasma doping for forming the fin-shaped PMISFET to be less than or equal to that during plasma doping for forming the fin-shaped NMISFET. 
     [Basic Structure of Semiconductor Device Obtained in First and Second Examples] 
       FIG. 22  is a perspective view schematically showing an example of a basic structure of a semiconductor device obtained in the first example and the second example. Specifically, the figure shows a structure of the device before plasma doping where a gate electrode has been formed on a fin-shaped semiconductor region having a substantially right-angled upper corner with a gate insulating film interposed therebetween. As shown in  FIG. 22 , a gate electrode  63  is formed so as to bridge over a fin-shaped semiconductor region  61  having an impurity region  61   a  in an upper portion thereof and an impurity region  61   b  in a side portion thereof, with the gate insulating film  62  interposed therebetween. Herein, a, b, c and d denote corners on the source side along the inner wall of the gate insulating film  62  having a pommel horse shape, and a″, b″, c″ and d″ are obtained by translating the corners a, b, c and d to the source-side end surface of the fin-shaped semiconductor region  61 . The height of the fin is 10-500 nm, for example, the width of the fin is 10-500 nm, for example, and the distance between fins is 20-500 nm. Where the present invention is applied to a semiconductor device having such minute fins, it is possible to realize a semiconductor device having a characteristic that the distance G between the corner b″ and the first impurity region  61   a  (the fin upper portion), i.e., the distance G between the corner c″ and the first impurity region  61   a  (the fin upper portion), is greater than zero and less than or equal to 10 nm and a characteristic that the sheet resistance of the second impurity region  61   b  (the fin side portion) normalized with the sheet resistance of the first impurity region  61   a  (the fin upper portion) is less than or equal to 1.25, thus obtaining effects of the present invention. Note that the distance G between the corner b″ and the first impurity region  61   a  (the fin upper portion) or the distance G between the corner c″ and the first impurity region  61   a  (the fin upper portion) means the maximum value of the distance between the plane including the rectangle a−a′−b′−b, the plane including the rectangle b−b′−c′−c or the plane including the rectangle c−c′−d′−d and the first impurity region  61   a  (where a, b, c and d are the corners on the source side along the inner wall of the gate insulating film  62  having a pommel horse shape and a′, b′, c′ and d′ are the corresponding corners on the drain side), and this is a quantity that reflects the amount of the upper corner of the fin-shaped semiconductor region chipped off by plasma doping. Moreover, the characteristic that the distance G between the corner b″ and the first impurity region  61   a  (the fin upper portion), i.e., the distance G between the corner c″ and the first impurity region  61   a  (the fin upper portion), is greater than zero and less than or equal to 10 nm is normally equivalent to the characteristic that the radius of curvature r′ of the upper corner in the semiconductor region  61  located outside the gate insulating film  62  (i.e., the radius of curvature after plasma doping) is greater than the radius of curvature r of the upper corner in the semiconductor region  61  located under the gate insulating film  62  (i.e., the radius of curvature before plasma doping) and is less than or equal to 2×r. 
       FIG. 23  is a perspective view schematically showing another example of a structure of a semiconductor device obtained in the first example and the second example. Specifically, the figure shows a structure of the device where the semiconductor region is formed so that the fin corner portion in advance has some radius of curvature before the formation of the gate insulating film, and then the gate electrode is formed thereon with the gate insulating film interposed therebetween. Note that in  FIG. 23 , like elements to those shown in  FIG. 22  are denoted by like reference numerals and will not be described redundantly. It has been pointed out that when the fin corner portion is nearly right-angled, it is difficult for a current to flow from the source to the drain through the fin corner portion. This is a problem that occurs depending on whether there is a nearly right-angled corner portion in a connecting portion between the gate insulating film  62  and the first impurity region  61   a  (the fin upper portion), irrespective of the presence/absence or the magnitude of the chipping of the fin corner portion by plasma doping. In view of this, in order to solve the problem, it is preferred that the fin corner portion is in advance provided with a radius of curvature from about 3 nm to about 10 nm before the formation of the gate insulating film. Then, there will not be a nearly right-angled corner portion in a connecting portion between the gate insulating film  62  and the first impurity region  61   a  (the fin upper portion), and it will not be difficult for a current flow from the source to the drain to flow under the gate insulating film  62 . Also where the present invention is applied to a semiconductor device having such fins, it is possible to realize a semiconductor device having a characteristic that the distance G between the corner b″ and the first impurity region  61   a  (the fin upper portion), i.e., the distance G between the corner c″ and the first impurity region  61   a  (the fin upper portion), is greater than zero and less than or equal to 10 nm and a characteristic that the sheet resistance of the second impurity region  61   b  (the fin side portion) normalized with the sheet resistance of the first impurity region  61   a  (the fin upper portion) is less than or equal to 1.25, thus obtaining effects of the present invention. 
     [Plasma Apparatus Used in First And Second Examples] 
     An ICP-type plasma apparatus is used in the first example and the second example. The reason is that it is then possible to also use a characteristic “being a plasma with large angles of incidence of ions” that is inherent to an ICP-type plasma, whereby it becomes easier to obtain the effects of the present invention. In addition, with an ICP method, the plasma density and the implantation depth can be controlled independently, whereby it is likely to be able to generate a plasma uniformly even for a substrate having a large diameter of 300 mm, for example, without increasing the electron temperature as much as that with the ECR (electron cyclotron resonance) plasma method. Therefore, it is possible to perform a plasma doping process uniformly for a plurality of fins within the surface of a large-diameter substrate while suppressing the chance of breaking the gate insulating film and freely choosing the implantation depth. That is, it is desirable to use an ICP-type plasma apparatus. 
     Problems occurring when the present invention is carried out using other plasma methods will now be described. 
     First, the ME (reactive ion etching) plasma method will be discussed. With the ME plasma method, a high-frequency power is applied to the cathode electrode. Thus, the generation of a plasma starts, and the plasma density is adjusted while the bias voltage is adjusted at the same time. Where the ME plasma method is used, the generation of a plasma starts only at a high pressure. Therefore, in order to decrease the pressure to a low pressure such as that used in the example process after the plasma generation is once started at a high pressure, the pressure adjustment requires a long period of time, thereby lowering the productivity. Moreover, with the ME plasma method, a plasma is generated only by applying a high-frequency power to a cathode electrode, whereby the plasma density and the implantation depth change simultaneously, and cannot be controlled independently, thus resulting in a poor process controllability. In contrast, with the ICP method described above, the plasma density is controlled by controlling the high-frequency power applied to the anode electrode and the implantation depth is controlled by controlling the high-frequency power applied to the cathode electrode, whereby the plasma density and the implantation depth can be controlled independently. Moreover, with the ICP method described above, it is possible to set the high-frequency power to be applied to the anode electrode at the start of the plasma generation to be high, whereby it is possible to start the plasma generation without using a pressure significantly higher than that used in a doping process. 
     Next, the ECR plasma method will be discussed. In the ECR plasma method, the excitation frequency is greater than or equal to 900 MHz. That is, with the ECR plasma method, since the excitation frequency is very high, the electron temperature is high, whereby the dielectric breakdown of the gate insulating film is likely to occur. In contrast, with the ICP method, the excitation frequency is 13.56 MHz, for example, i.e., smaller than that of the ECR plasma method by an order or magnitude or more, and the dielectric breakdown of the gate insulating film is relatively unlikely to occur. That is, it is desirable to use the ICP method as compared with the ECR plasma method. 
     Next, the pulsed DC plasma method will be discussed. With the pulsed DC plasma method, a pulsed DC high-frequency voltage is applied to the cathode electrode. With this method, the angle of incidence of ions is basically close to zero (i.e., at nearly a right angle with respect to the fin upper surface), whereby the sheet resistance of the fin side portion will be higher than that of the fin upper portion. In contrast, with the ICP method, an AC high-frequency voltage whose frequency is 500 MHz, 600 MHz or 13.56 MHz is applied to the cathode electrode. Thus, the angle of incidence of ions increases, whereby the sheet resistance of the fin side portion is likely to be substantially equal to that of the fin upper portion. That is, it is desirable to use the ICP method as compared with the pulsed DC plasma method. 
     Next, the helicon plasma method will be discussed. The helicon plasma method has a characteristic that a magnetic field of at least one 10 gauss or more is applied to the plasma and a characteristic that the distance between the plasma source and the substrate is long. With this method, since the distance between the plasma source and the substrate is long, it is difficult to obtain a good plasma uniformity for a large-diameter substrate such as a wafer having a diameter of 300 mm. In contrast, with the ICP method, it is not necessary to apply a magnetic field to the plasma, and the distance between the plasma source and the substrate is short, whereby it is likely to be able to obtain a good plasma uniformity for a large-diameter substrate such as a wafer having a diameter of 300 mm. That is, it is desirable to use the ICP method as compared with the helicon plasma method. 
     First Variation of First Embodiment 
     A structure of a semiconductor device according to a first variation of the first embodiment (including the first example and the second example) will now be described with reference to the drawings. 
       FIG. 24  is a plan view of a semiconductor device of this variation, specifically, a semiconductor device including a fin-shaped CMISFET. Note that in  FIG. 24 , like elements to those of the first embodiment shown in  FIGS. 1A-1E  are denoted by like reference numerals and will not be described redundantly. 
     As shown in  FIG. 24 , this variation differs from the first embodiment shown in  FIGS. 1A-1E  in that other fin-shaped semiconductor regions  13   e  and  13   f  connect together end portions of the n-type fin-shaped semiconductor regions  13   a  and  13   b  on each side of the n-type fin-shaped semiconductor regions  13   a  and  13   b  in the gate length direction, and that other fin-shaped semiconductor regions  913   e  and  913   f  connect together end portions of the p-type fin-shaped semiconductor regions  913   c  and  913   d  on each side of the p-type fin-shaped semiconductor regions  913   c  and  913   d  in the gate length direction. 
     According to this variation, it is possible to obtain the following effects, in addition to effects similar to those of the first embodiment. That is, one fin-shaped PMISFET can be formed by the n-type fin-shaped semiconductor regions  13   a  and  13   b  and the other fin-shaped semiconductor regions  13   e  and  13   f , and one fin-shaped NMISFET can be formed by the p-type fin-shaped semiconductor regions  913   a  and  913   b  and the other fin-shaped semiconductor regions  913   e  and  913   f.    
     Second Variation of First Embodiment 
     A structure of a semiconductor device according to a second variation of the first embodiment (including the first example and the second example) will now be described with reference to the drawings. 
     A plan view showing a structure of a semiconductor device of this variation, specifically, a semiconductor device including a fin-shaped CMISFET, is the same as  FIG. 1A  being a plan view of the first embodiment.  FIGS. 25A-25D  show cross-sectional structures of the semiconductor device of this variation, wherein  FIG. 25A  is a cross-sectional view taken along line A-A in  FIG. 1A ,  FIG. 25B  is a cross-sectional view taken along line B-B in  FIG. 1A ,  FIG. 25C  is a cross-sectional view taken along line C-C in  FIG. 1A , and  FIG. 25D  is a cross-sectional view taken along line D-D in  FIG. 1A . 
     As shown in  FIGS. 25A-25D , this variation differs from the first embodiment shown in  FIGS. 1A-1E  as follows. That is, in the first embodiment, the gate insulating films  14   a  and  14   b  having a thickness of 3 nm and made of a silicon oxynitride film, for example, are formed on the upper surface and the side surface of the n-type fin-shaped semiconductor regions  13   a  and  13   b , and the gate insulating films  914   c  and  914   d  having a thickness of 3 nm and made of a silicon oxynitride film, for example, are formed on the upper surface and the side surface of the p-type fin-shaped semiconductor regions  913   c  and  913   d . In contrast, in this variation, the gate insulating films  14   a  and  14   b  are formed only on the side surface of the n-type fin-shaped semiconductor regions  13   a  and  13   b , the gate insulating films  914   c  and  914   d  are formed only on the side surface of the p-type fin-shaped semiconductor regions  913   c  and  913   d , insulating films  924   a  and  924   b  having a thickness of 20 nm and made of a silicon oxide film, for example, are formed on the upper surface of the n-type fin-shaped semiconductor regions  13   a  and  13   b , and insulating films  924   c  and  924   d  having a thickness of 20 nm and made of a silicon oxide film, for example, are formed on the upper surface of the p-type fin-shaped semiconductor regions  913   c  and  913   d.    
     That is, in this variation, only the side portion of the n-type fin-shaped semiconductor regions  13   a  and  13   b  and the p-type fin-shaped semiconductor regions  913   c  and  913   d  is used as a channel region. Also with such a structure, it is possible to obtain effects similar to those of the first embodiment if the aspect ratio (“the height of the side surface of the fin-shaped semiconductor region”/“the width of the upper surface of the fin-shaped semiconductor region in the gate width direction”) is large. 
     Comparative Example 
       FIG. 26A  is a perspective view of a fin-shaped CMISFET according to a comparative example, and  FIG. 26B  is an enlarged perspective view of the fin-shaped NMISFET of the fin-shaped CMISFET shown in  FIG. 26A . In  FIGS. 26A and 26B , like elements to those of the fin-shaped CMISFET shown in  FIGS. 1A-1E  are denoted by like reference numerals and will not be described redundantly. 
     This comparative example differs from the first example and the second example in that where boron is used as a p-type impurity for forming the fin-shaped PMISFET and arsenic, which has a greater mass than boron, is used as an n-type impurity for forming the fin-shaped NMISFET, the pressure during the n-type impurity plasma doping is set to be substantially equal to or greater than that during the p-type impurity plasma doping. 
     Referring to  FIG. 26B , the chipping of the fin corner portion of the fin-shaped NMISFET of the comparative example will now be described. As shown in  FIG. 26B , the gate electrode  15   c  is formed so as to extend across the p-type fin-shaped semiconductor region  913   c  having the n-type impurity region  917   a  in an upper portion thereof and the n-type impurity region  917   b  in a side portion thereof, with the gate insulating film  914   c  interposed therebetween. In  FIG. 26B , a, b, c and d denote corners on the source side along the inner wall of the gate insulating film  914   c  having a pommel horse shape, and a″, b″, c″ and d″ are obtained by translating the corners a, b, c and d to the source-side end surface of the p-type fin-shaped semiconductor region  913   c.    
     In this comparative example, the distance G between the corner b″ and the upper-portion n-type impurity region  917   a , i.e., the distance G between the corner c″ and the upper-portion n-type impurity region  917   a , was over 10 nm. Therefore, the amount of chipping of the fin corner portion (the amount of increase in the radius of curvature) after the plasma doping process for the fin-shaped NMISFET of the fin-shaped CMISFET of this comparative example is not within an acceptable range. 
     As described above, in a case where a fin-shaped PMISFET and a fin-shaped NMISFET are formed on the same substrate, wherein boron is used as a p-type impurity for forming the fin-shaped PMISFET (specifically, the p-type extension region thereof) and arsenic, which has a greater mass than boron, is used as an n-type impurity for forming the fin-shaped NMISFET (specifically, the n-type extension region thereof), if the pressure during the n-type impurity plasma doping is set to be substantially equal to or greater than that during the p-type impurity plasma doping, the amount of chipping of the fin corner portion (the amount of increase in the radius of curvature) of the fin-shaped NMISFET is increased, thereby increasing the gap between the gate insulating film and the extension region, thus deteriorating the transistor performance.