BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The invention relates to a gear and axle lubricant oil composition, more particularly for automotive gears, for reducing power loss due to friction, whereby fuel saving may be achieved. 
     2. Discussion of the Prior Art 
     For some years efforts have been made to reduce fuel consumption of automobiles and heavy goods vehicles and the like. 
     Several of the solutions proposed are of a purely mechanical nature. Other approaches have involved a search for lubricants which will reduce overall friction of components, whereby energy saving is possible. At the present time, in the field of automotive gear or axle oils, there are employed conventional mineral oil compositions or fully synthetic compositions, for example compositions based on synthetic esters or on polyalphaolefins plus polyalkenes. In U.K. Pat. No. 786950 there is disclosed a fully synthetic lubricating composition, said to be particularly suitable for gas turbine bearings, which comprises (a) a liquid ester (such as di (2-ethylhexyl) sebacate or adipate), (b) a polyoxyalkylene glycol or mono- or di-ether thereof and (c) a Group II metal salt of either an aromatic carboxylic acid or a phenol. 
     SUMMARY OF THE INVENTION 
     With the ever-increasing need to conserve automotive fuel consumption a major requirement of a gear or axle oil is that it decreases power loss due to friction. However, this alone is not sufficient. The oil must in addition give an acceptable degree of anti-wear protection to the components being lubricated. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     FIG. 1 is a graph showing the results of a FZG rig test. 
    
    
     It is an object of the present invention to provide a lubricating composition suitable for use as a gear or axle oil which, in comparison with a known type of oil, enables a decrease in power loss to be achieved for the same, or better, degree of anti-wear protection. 
     According to the present invention a lubricating composition suitable for use as a gear or axle oil comprises: 
     (a) from 5 to 50 mass % of mineral oil of conventional gear oil or axle oil grade; 
     (b) from 5 to 30 mass % in total of at least one polyoxyalkylene glycol having a viscosity of from 5 to 30 cSt at 100° C.; 
     (c) from 25 to 60 mass % in total of at least one di-C 8  to C 12  alkyl ester of a dicarboxylic acid; 
     (d) from 0 to 15 mass % in total of at least one conventional extreme pressure agent; 
     (e) from 0 to 8 mass % in total of at least one conventional VI improver; and 
     (f) from 0 to 5 mass % of at least one conventional pour point depressant; the components (a) to (f) totalling together 100 mass %, 
     and the components (a) to (f) forming at least 95 mass % of the whole lubricating oil composition. 
     Desirably the composition comprises: 
     from 10 to 40 mass % of component (a), 
     from 10 to 20 mass % of component (b), 
     from 30 to 35 mass % of component (c), 
     from 2 to 10 mass % of component (d), 
     from 2 to 5 mass % of component (e), and 
     from 0.1 to 3 mass % of component (f); 
     the components (a) to (f) totalling together 100 mass %, and the total forming at least 95 mass % of the whole lubricating oil composition. 
     Preferably the components (a) to (f) are present in the following mass %: (a) 15 to 40; (b) 14 to 18; (c) 35 to 50; (d) 6 to 7; (e) 2 to 8; and (f) 0.2 to 1. The said preferred quantities may be taken individually and not necessarily with a preferred quantity of any others of the said components. 
     The lubricating oil compositions of the invention may, if desired, contain amounts of one or more conventional additives selected from anti-corrosion agents, antioxidants, seal-swellants, de-odourizers, dyes and fluorescent colouring agents. In that case to the total amount employed of all such conventional additives is not more than 5 mass % of the total lubricating oil composition. 
     Unless stated otherwise, the amounts of components employed refer to amounts of active ingredients of those components and excludes, for example, any solvents, diluents etc. for the components. 
     Preferably the polyoxyalkylene glycol is one having a viscosity in the range 20 to 25 cSt at 100° C. 
     Preferred polyoxyalkylene glycols are polyoxyethylene glycol, polyoxypropylene glycol or polyoxyethylene-polyoxypropylene glycol. A polyoxyethylene-polyoxypropylene glycol of molecular weight of approximately 2000 is a particularly preferred component. The polyoxyalkylene glycols are also known as polyalkylene glycols or polyoxyalkylenes. 
     The diester component is preferably of an aliphatic dicarboxylic acid; suitably of the formula HOOC(CH 2 ) n  COOH, where n is from 3 to 8. Thus the diester can be of, for example, glutaric acid and/or adipic acid. 
     Suitably, a dioctyl-, diisononyl or diisodecyl ester is employed. The diester can be of an aromatic acid, preferably of phthalic acid. 
     When the lubricating oil compositions of this invention contain an extreme pressure agent, this may be, for example, one or more phosphorus-sulphur organic compounds. One example of an extreme pressure agent is a phosphosulphurized polyalkene. When a VI improver is employed, it may be selected from styrene-butadiene copolymers, polymethacrylates and polyisobutenes. When a pour point depressant is employed it may be a chlorinated wax-naphthalene condensate and/or an ester type polymer or copolymer, for example a vinyl acetate-fumarate ester copolymer. 
     The mineral oil component of compositions according to the invention will be selected from those grades having the characteristics suitable for conventional gear oil or axle oil formulations. Thus, for example, suitable grades are 90 Neutral, 100 Neutral and 600 Neutral. 
     The final composition will have viscosity gradings of 75W, or 75W-80W, or 75W-90. 
     The invention will now be illustrated by reference to the following non-limitative Examples: 
     EXAMPLE 1 
     Table 1 attached shows a comparison of physico-chemical characteristics between (a) two gear oil compositions according to the invention (L1 and L2) (b) two fully synthetic gear oil types (E and F) and (c) four conventional mineral gear oils (R1, R&#39;1, R2 and R3). 
     In Table 1 PAO=polyalphaolefins; PEG=the commercial product EMKAPYL 2000; ESTER=diisodecyl adipate; EP treat is 1:1 active ingredients to diluent; PMA=polymethacrylates; PIB=polyisobutylene; and the pour depressant was a chlorowax/naphthalene condensate. 
     Among other observations which can be made, it will be apparent that the equivalent grades L2 and F have virtually the same VI, but this has been obtained in the oil L2 of the invention with 33% less VI improver. 
     Furthermore the viscosity of oils L1 and L2 meet the U.S. Military gear oil specification MIL-L-2105C limits, which are 
     
         ______________________________________                                    
75W-80W     75W-90                                                        
min      max    min        max                                            
______________________________________                                    
7.0      --     13.5       24.0 (cSt at 100° C.)                   
______________________________________                                    
 
    
     EXAMPLE 2 
     Samples of the gear oil compositions E, F, R1, L1, L2 and R2 shown in Table 1 were subjected to a FZG rig test. The results are shown in the accompanying FIGURE. This is a standard procedure of the Coordinating European Council (CEC). The particular test L-07-A-71 referred to in FIG. 1 determines damaging load. The plots recorded on the graph denote electric power consumption of the electric motor during test operation of the rig (the reading being taken from the watt meter on the motor) on various oil compositions, in comparison with a reference mineral oil composition R 2  (a GL-5 (API designation) 80W-90 grade). 
     FIG. 1 shows that, versus the reference oil R2, the oils of the invention (75W-80W and 75W-90 grades referenced L1 and L2 respectively) permit a decrease of power losses due to friction; while the fully synthetic 75W-90 oils based either on all ester basestocks or polyalphaolefins+polyisobutene type thickener do not (reference E and F respectively). 
     A mineral 75W-80W oil (reference R1) also permits an energy saving but only at low loads; as a fact in the FZG rig test, the saving is only obtained for loads inferior to the 6th Stage; for the higher load stages, this mineral 75W-80W oil gives a power loss increase likely due to insufficient oil film thickness (boundary lubrication). The oils L1 and L2 of the invention permit meeting the 9th FZG load stage before boundary lubrication starts. 
     EXAMPLE 3 
     A rear axle endurance bench test was conducted on a rear axle of an automobile of 1.6 l engine capacity. The test used the oil compositions R1, R&#39;1, L1, L2 and R2 of Example 1. The test rig employed was a conventional rear axle rig. The test conditions and procedure were as follows: 
     
         ______________________________________                                    
TEST CONDITIONS                                                           
° CYCLIC                                                           
               HIGH TORQUE  LOW TORQUE                                    
PROCEDURE      LOW SPEED    HIGH SPEED                                    
______________________________________                                    
DURATION, H    15 (DAY)     9 (NIGHT)                                     
REAR AXLE SPEED,                                                          
RPM                                                                       
INLET          1380         4000                                          
OUTLET          350         1020                                          
TORQUE AT REAR                                                            
AXLE, m.N                                                                 
INLET           325          100                                          
OUTLET         1270          390                                          
OIL TEMPERATURE,                                                          
°C.     145-150      125-130                                       
______________________________________                                    
 
    
     The results are shown in Table 2. An advantage of the semi-synthetic formulations of the invention is seen in the transmission durability. Table 2 shows the insufficiency of mineral gear oils (75W-80W) as far as life duration of the transmission is concerned. In this endurance rig test run under severe conditions, the test duration after which rear axle damaging starts is only 57 hours, while it is 90 for a conventional mineral GL-5 gear oil (R2) containing the same extreme-pressure additive treatment (6.5 wt%). An extreme-pressure additive overtreat (oil R&#39;1) does not improve the performance enough to match the mineral SAE 90 oil. 
     With the normal GL-5 additive treatment (6.5 wt%) the semi-synthetic 75W-80W oil L1 permits a longer life duration: 115 hours versus oil R2 although it has the same viscosity as the mineral 75W-80W oils R1 or R&#39;1. This better anti-wear performance is confirmed by the result given by the 75W-90 semi-synthetic oil L2 which permits 150 hours duration life although it has the same viscosity at 100° C. as the G1-5-SAE 90 mineral reference oil R2. 
     EXAMPLE 4 
     The accompanying Table 3 shows the results of miscibility tests of an oil of the invention with a conventional mineral gear oil. The oil L1 of the invention and mineral oil R2 were taken. 
     The results illustrate a further, very important, advantage of an oil according to the invention. It provides the possibility for a car user to change from a conventional mineral gear oil to an oil of the invention without any special precautions in the oil-change. It also allows top-up. Table 3 shows that no phase separation will occur for an oil temperature above 40° C. whatever the ratio of oils types. For temperatures between 0° to 40° C., 30% max mineral oil can be added to the semi-synthetic one either through top-up or through oil remaining in the box after an oil draining, which is considered sufficient for the practical and usual case. 
     This miscibility with conventional products is considered essential by the car manufacturers and the U.S. official specification MIL-L-2105C. 
     
                                           TABLE 1                                 
__________________________________________________________________________
OILS COMPOSITION AND PHYSICO CHEMICAL CHARACTERISTICS                     
               Claimed semi-                                              
Oil type       synthetic oils                                             
                       synthetic oils                                     
                               conventional mineral oils                  
Oil reference  L1  L2  E   F   R1    R&#39;1   R2  R3                         
Viscosity grading                                                         
               75W-80                                                     
                   75W-90                                                 
                       75W-90                                             
                           75W-90                                         
                               75W-80W                                    
                                     75W-80W                              
                                           80W-90                         
                                               85W-140                    
__________________________________________________________________________
Composition (weight pct)                                                  
150 Neutral    38.5                                                       
                   --  --  --  72.5  69.0  68.5                           
                                               9.40                       
600 Neutral    --  23.0                                                   
                       --  --  16.0  16.0  68.5                           
                                               --                         
2500 Neutral   --  --  --  --              23.0                           
                                               84.3                       
PAO Basestock  --  --  --  81.0                                           
                               --    &#39;     --  --                         
PEG oil        16.0                                                       
                   16.0                                                   
                       --  --  --    --    --  --                         
Ester          36.5                                                       
                   46.0                                                   
                       70.0                                               
                           --  --    --    --  --                         
EP treat        6.5                                                       
                    6.5                                                   
                        6.5                                               
                            6.5                                           
                                6.5  10.0   6.5                           
                                                6.5                       
       Styrene-                                                           
VI     butadiene type                                                     
                2.0                                                       
                    8.0                                                   
                       --  --  --    --    --  --                         
Improver                                                                  
       PMA type                                                           
               --  --  23.0                                               
                           --   3.0   3.0  --  --                         
       PIB type                                                           
               --  --  --  12.0                                           
                               --    --    --  --                         
Pour depressant                                                           
                0.5                                                       
                    0.5                                                   
                        0.5                                               
                            0.5                                           
                                2.0   2.0   2.0                           
                                                0.2                       
Physico-chemical                                                          
characteristics                                                           
Viscosity at 100° C., cSt                                          
                7.9                                                       
                   17.2                                                   
                       19.0                                               
                           16.0                                           
                                7.8   7.8  14.0                           
                                               24.0                       
Brookfield viscosity                                                      
at -90° C.                                                         
               1200                                                       
                   1300                                                   
                       700 1100                                           
                               1200  1250  ≧1500                   
                                               ≧1500               
Viscosity index ASTM D 2270                                               
               176 206 193 205 126   126   105  97                        
__________________________________________________________________________
 
    
     
                                           TABLE 2                                 
__________________________________________________________________________
REAR AXLE ENDURANCE BENCH TEST                                            
__________________________________________________________________________
SAE VISCOSITY                                                             
GRADING       75W-80W                        75W-90    90                 
OIL TYPE      M          M       SS          SS        M                  
REFERENCE     R1         R&#39;1     L1          L2        R2                 
TEST DURATION 57         ABOUT 60-80                                      
                                 115         150       90                 
BEFORE AXLE                                                               
DAMAGING, h                                                               
TEMPERATURE   DIFFICULT  GOOD    GOOD        GOOD      GOOD               
CONTROL (1)   (155 220°)                                           
              (after 50 h)                                                
ASPECT AFTER 100 h                                                        
CONICAL GEAR                     GOOD, VERY  GOOD      RIDGING +          
                                 SLIGHTLY PITTING      PITTING            
CROWN         TEST STOPPED       GOOD        GOOD      RIDGING +          
              AFTER 57 h                               SLIGHT             
                                                       PITTING            
ASPECT AFTER                                                              
TEST COMPLETION                                                           
              57 h       100 h   115 h       175 h     115 h              
CONICAL GEAR  HEAVY RIDGING                                               
                         HEAVY   GOOD WITH HEAVY                          
                                             GOOD WITH HEAVY              
                         PITTING PITTING AT TEETH                         
                                             PITTING AT                   
                                                       RIDGING +          
                                 FOOT        TEETH FOOT                   
                                                       PITTING            
CROWN         RIDGING            GOOD        SLIGHT PITTING               
                                                       RIDGING +          
                                                       PITTING            
REAR ROLLING  SCALING            SCALING     PITTING   HEAVY              
                                                       SCALING            
LATERAL ROLLINGS                                                          
              SCALING            SCALING     SCALING   SLIGHT             
                                                       SCALING            
__________________________________________________________________________
 .sup.(1) maximum cooling is necessary to maintain 150° C. max at  
 low torque  high speed, and becomes insufficient when axle damaging      
 starts.                                                                  
 
    
     
                                           TABLE 3                                 
__________________________________________________________________________
MISCIBILITY WITH CONVENTIONAL                                             
MINERAL GEAR OILS                                                         
__________________________________________________________________________
Semi-Synthetic Oil                                                        
          90     75    50    25    10                                     
Mineral Oil                                                               
          10     25    50    75    90                                     
Miscibility                                                               
at 100° C.                                                         
          ←EXCELLENT.sup.(1) →                                
40° C.                                                             
          ←EXCELLENT.sup.(1) →                                
20° C.                                                             
          ←EXCELLENT → ←CLEAR BUT SLIGHT SEPARATION      
          →                                                        
          AFTER 8 DAYS&#39; STORAGE.sup.(2)                                   
0° C.                                                              
          ←EXCELLENT → ←CLEAR BUT SLIGHT SEPARATION      
          →                                                        
          AFTER 8 DAY&#39; STORAGE.sup.(2)                                    
-20° C.                                                            
          ←HAZY.sup.(3) →                                     
-40° C.                                                            
          ←HAZY.sup.(3) →                                     
__________________________________________________________________________
 .sup.(1) Blend is clear and perfectly homogeneous.                       
 .sup.(2) Blend separates into 2 phases after 8 day&#39; storage without      
 stirring, homogeneity is immediately recovered by stirring or by heating.
 .sup.(3) Blend is hazy; clearness and homogeneity are recovered by heatin
 at 40° C.