Patent Publication Number: US-2016243870-A1

Title: Printable recording media

Description:
BACKGROUND 
     Today, images are often captured with a digital camera, transferred electronically to a computer with a printer, or directly to a printer, and then produced by the printer in a hardcopy form. Color inkjet printing and/or laser-jet printing are, among other, often used for printing such high quality photographs. However, in recent years, consumers and businesses have turned to electrophotographic printing systems to produce such digital images on a variety of substrates. Electrophotographic printing systems are using liquid or dry toner electrophotographic ink as ink composition. 
     It has rapidly become apparent that the image quality of printed images using such printing technology is strongly dependent on the construction of the recording media used. Consequently, improved recording media, often specifically designed, have been developed for use in electrophotographic printing devices. However, while many developments have been made, it has often created challenges to find printable recording media which can be effectively used with electrophotographic printing techniques and which have good image quality as well as good durability. Accordingly, investigations continue into developing such media substrates. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The drawings illustrate various embodiments of the present recording media and are part of the specification.  FIGS. 1 and 2  are cross-sectional views of the printable recording media according to embodiments of the present disclosure.  FIG. 3  is a cross-sectional view of the printed article obtained according to embodiments of the present disclosure.  FIG. 4  is a flowchart illustrating the method for producing a printed article according to some embodiments of the present disclosure. 
     
    
    
     DETAILED DESCRIPTION 
     Before particular embodiments of the present disclosure are disclosed and described, it is to be understood that the present disclosure is not limited to the particular process and materials disclosed herein. It is also to be understood that the terminology used herein is used for describing particular embodiments only and is not intended to be limiting, as the scope of protection will be defined by the claims and equivalents thereof. In describing and claiming the present article and method, the following terminology will be used: the singular forms “a”, “an”, and “the” include plural referents unless the context clearly dictates otherwise. Concentrations, amounts, and other numerical data may be presented herein in a range format. It is to be understood that such range format is used merely for convenience and brevity and should be interpreted flexibly to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. For examples, a weight range of about 1 wt % to about 20 wt % should be interpreted to include not only the explicitly recited concentration limits of 1 wt % to 20 wt %, but also to include individual concentrations such as 2 wt %, 3 wt %, 4 wt %, and sub-ranges such as 5 wt % to 15 wt %, 10 wt % to 20 wt %, etc. All percent are by weight (wt %) unless otherwise indicated. As used herein, “image” refers to marks, signs, symbols, figures, indications, and/or appearances deposited upon a material or substrate with either visible or an invisible ink composition. Examples of an image can include characters, words, numbers, alphanumeric symbols, punctuation, text, lines, underlines, highlights and the like. 
     The present disclosure relates to a printable recording media comprising a supporting base substrate having, on its image side, a pre-coating layer and a top ink-receiving layer that include inorganic pigments and polymeric binders; and having, on its backside, a barrier layer and an antistatic layer. 
     The printable media of the present disclosure is a multi-layer composite structure. The word “composite” refers herein to a material made from at least two constituent materials, or layers, that have different physical and/or chemical properties from one another, and wherein these constituent layers remain separate at a molecular level and distinct within the structure of the composite. The printable recording media encompasses image receiving coatings or top ink-receiving layer. As used herein, the terms “image receiving coating” or “top-coat” are meant to be understood broadly as any coating which can receive an ink or toner; any coating comprising light-sensitive chemicals which, when exposed to a light source, may receive an image; any coating comprising heat sensitive chemicals which, when exposed to heat, may receive an image; or any combination thereof. 
     In some examples, the printable recording media of the present disclosure is a photographic printing recording media or photo paper recording media, which means herein that the printable recording media is well adapted for photographic printing and that it has the properties and appearances, at least, equal to the properties and appearance of silver halide photo media substrates when image is printed thereon. The printable recording media is thus able to provide advantages such as glossy appearance, surface smoothness and excellent image quality when used to produce photographic printouts. In addition, the printable recording media described herein provides an excellent photobase paper feel. As used herein, the term “photo feel” means that that the printed image feels like a photographic silver halide material when touched. 
     In some other examples, the printable recording media is an electrophotographic recording media. By electrophotographic recording media, it is meant herein that the media is well adapted for electrophotographic printing processes. The term “electrophotographic printing” is meant to be understood broadly as including any number of methods that use light to produce a change in electrostatic charge distribution to form a photographic image including, but in no way limited to, laser printing. The printable media is thus well-adapted for liquid electrophotographic printing device (i.e. using liquid electrophotographic toner such as, for example, HP Indigo Digital Press 6000 or 6600). 
     Thus, in yet some other examples, the printable recording media is an electrophotographic photographic recording media. The media can be an electrophotographic photographic recording media for liquid electro-photographic printing (LEP) and can be used in a method of forming photographic printed images. Throughout the various illustrative examples of the present application, the electrophotographic photographic recording media may receive images from printing device such as, for example, an Indigo® WS6000P Digital Printing Press available from Hewlett-Packard Company (Palo Alto, Calif., USA). Without being linked by any theory, it can be said that, with a six color Indigo® digital printing press WS6000P or 6600P, a user is able to produce photo quality prints comparable to silver halide photo prints. Furthermore, with the use of the printable recording media described herein, there will not need of any additional surface treatment (primer layer) and processing to address inadequate ink or toner adhesion and print uniformity issues to the media, as it is often the case with traditional offset type media. 
     The printable recording media, described herein, is an image-receiving media that shows excellent print image quality. Said recording media yield not only high gloss appearance but, further, provides a solution to keep the gloss stable under the heat, whether the printers are equipped with single or double heated fuser rollers. In some examples, the printable recording media has a non-imaged gloss which is above about 95 to 100% when tested at 75° angle per Tappi test method of T480, or which is above about 35 to 50% when tested at 60° angle. 
     The printable recording media, described herein, is consider to lay flat (i.e. having a curl less than 20 mm) across 15° to 30° and 20% to 80% RH condition while achieves good toner adhesion after printing across different user environment. Indeed, photo papers with a curl that is more than 20 mm might result in poor user experiences (issues when trying to display the photo on a table or wall for example). The printable recording media of the present disclosure has an excellent curl control without the need of having a laminate layer on both sides of the media. The printable recording media presents, thus, excellent curl control across different environmental conditions and does not have any curling issues. 
     In addition, the printable recording media, such as described herein, demonstrates excellent antistatic performances. The printable media is thus a photo media with excellent antistatic performances. Media without antistatic performances often builds very high static during printing that have negative impacts on the printing process and that might result in either poor ink and toner transfer or adhesion. Furthermore, such high static charge can lead to safety concerns and can cause operation issues during finishing (such as multi-sheets that stick together). 
     Therefore, the recording media described herein shows excellent image quality when used to produce photographic printouts. In addition, the recording media has a structure which is receptive and which presents excellent absorption and adherence properties to the ink deposed thereon. The printable recording media enables thus electrophotographic photo printing, such as, for examples, Indigo photo printing, without the need of using any primer composition. 
       FIG. 1  and  FIG. 2  schematically illustrate some embodiments of printable recording media ( 100 ).  FIG. 3  schematically illustrates some embodiments of a printed article ( 200 ).  FIG. 4  is a flowchart illustrating the method for producing said printed article ( 200 ). As will be appreciated by those skilled in the art,  FIG. 1 ,  FIG. 2  and  FIG. 3  illustrate the relative positioning of the various layers of the printable media or printed article without necessarily illustrating the relative thicknesses of the various layers. It is to be understood that the thickness of the various layers is exaggerated for illustrative purposes. 
     In some examples, as shown in  FIG. 1  or in  FIG. 2 , the printable media ( 100 ) encompasses a base substrate ( 110 ); said base substrate ( 110 ) can be a paper base substrate. The base substrate has two surfaces: a first surface, which might be referred to as the “image receiving side”, “image surface” or “image side” ( 101 ), and a second surface, the opposite surface, which might be referred to as the “back surface” or “backside” ( 102 ). The image side ( 101 ) of the media includes material layers that will receive, support and protect an image. The backside, or opposing side, ( 102 ) does not contains any ink-receiving layer and is not very well adapted to receive the printable image. As illustrated in  FIG. 1 , the printable recording media ( 100 ) encompasses a supporting substrate ( 110 ), above which is applied a pre-coating layer ( 120 ) and a top ink-receiving layer ( 130 ). The top ink-receiving layer ( 130 ) is applied over said pre-coating layer ( 120 ). As illustrated in  FIG. 1 , the top ink-receiving layer ( 130 ) and the pre-coating layer ( 120 ), are applied, only, on one side of the supporting substrate ( 110 ). On the other side, i.e. backside or opposing side, of the supporting substrate ( 110 ), a barrier layer ( 140 ) and an antistatic layer ( 150 ) are applied. 
       FIG. 2  illustrates some other embodiments of the printable media ( 100 ) wherein the printable media includes pre-coating layers ( 120 ) that are applied on both sides of the base substrate ( 110 ). The pre-coating layer ( 120 ) is thus also present on the backside ( 102 ) of the base substrate ( 110 ) below the barrier layer ( 140 ) and the antistatic layer ( 150 ).  FIG. 3  illustrates an example of a printed article ( 200 ) according to the present disclosure. The printed article includes a printable media containing a supporting substrate ( 110 ) having, on its backside ( 202 ), a barrier layer ( 140 ) and an antistatic layer ( 150 ), on its image side ( 201 ), a pre-coating layer ( 120 ) and a top ink-receiving layer ( 130 ), above which is present a printed image ( 210 ). A post-image lamination film ( 220 ) is disposed above said printed image ( 210 ). 
     Printable Media ( 100 ) 
     Supporting Base Substrate ( 110 ) 
     The printable media ( 100 ) contains a supporting substrate ( 110 ) that acts as a bottom substrate layer. The print media substrate (i.e., ‘substrate’) contains a material that serves as a base upon which the ink-receiving layer is applied. The print media substrate provides integrity for the resultant print medium. The supporting base substrate or raw base substrate ( 110 ), on which coating compositions are applied, may take the form of a media sheet or a continuous web suitable for use in a printer. The supporting substrate may be a base paper manufactured from cellulose fibers. The base paper may be produced from chemical pulp, mechanical pulp, thermal mechanical pulp and/or the combination of chemical and mechanical pulp. In some instances, when mechanical pulp is added, the total percentage of mechanical pulp is less than 20% of the total raw base weight. The base paper may also include conventional additives such as retention aid, dry or wet strength agent, internal sizing agents and fillers. 
     The supporting base substrate ( 110 ) can be a cellulose base paper. The raw base substrate ( 110 ) can be made of any suitable wood or non-wood pulp. Non-limitative examples of suitable pulps include any kind of chemical pulp, mechanical wood pulp, chemically treated ground pulp, CTMP (chemical thermo mechanical pulp), and/or mixtures thereof. Bleached hardwood chemical pulps may make up the main pulp composition. This pulp has shorter fiber structure than soft wood, which contribute to good formation of the finished paper. In some examples, the raw base substrate ( 110 ) contains 100% of chemically treated fiber such as bleached hardwood, softwood fiber, non-wood fiber, synthetic fiber, and combinations. In some other examples, the raw base substrate ( 110 ) contains 100% of bleached hardwood and, in yet some other examples, the raw base substrate ( 110 ) contains from about 50 to about 95% of bleached hardwood and from about 5 to about 50 wt % of softwood. 
     Fillers may be incorporated into the pulp, for example, to substantially control physical properties of the final coated paper. The filler particles fill in the void spaces of the fiber network and result in a denser, smoother, brighter and opaque sheet. Examples of the fillers include, but are not limited to, ground calcium carbonate, precipitated calcium carbonate, titanium dioxide, kaolin clay, silicates, plastic pigment, alumina trihydrate, magnesium oxide and/or mixtures thereof. In some examples, the supporting base substrate contains fillers in an amount ranging from about 0.2 wt % to about 25 wt % of the raw base, and in some other examples, the amount of filler ranges from about 3 wt % to about 15 wt % of the raw base. 
     When preparing the paper base stock, internal and surface sizing may be used. This process may improve internal bond strength of the substrate fibers, and may control the resistance of the coated substrate to wetting, penetration, and absorption of aqueous liquids. Internal sizing may be accomplished by adding a sizing agent to the raw base in the wet end. Non-limitative examples of suitable sizing agents include rosin-based sizing agent(s), wax-based sizing agent(s), cellulose-reactive sizing agent(s) and other synthetic sizing agent(s), and/or mixtures. In some examples, the internal sizing agents are Alkyl Ketene Dimer (AKD) or alkenylsuccinic anhydride (ASA). It is to be understood that the type and amount of surface sizing agent(s) may substantially improve moisture resistance and may alter the stiffness of the base paper stock. Surface sizing (i.e. apply sizing agent to the paper surface during papermaking process) may be accomplished by film size press, pond size press and other surface techniques. Included in this wet end processing can be additional functional additives such as but not limited to dispersants, biocides, retention aids, defoamers, dyes, and optical brighteners. The raw base substrate ( 110 ) can also be surfaced treated with starch or with starch and latex binder with pigments. The surface sizing agent might result in a coat-weight of sizing agent is the range of about 0.2 gsm to about 4 gsm. 
     In some examples, the raw base substrate has a basis weight of about 80 to about 300 gsm, and, in some other examples, has a basis weight of about 120 to about 180 gsm. The stiffness of the raw base can range from about 200 Gurley stiffness units to about 2000 Gurley stiffness units in the paper machine direction, and can range from about 400 Gurley stiffness units and about 1200 Gurley stiffness units in the paper cross machine direction. In some other examples, the base paper stiffness ranges from about 800 Gurley stiffness units to about 1500 Gurley stiffness units in the paper machine direction, and from about 600 Gurley stiffness units to about 1000 Gurley stiffness units in the paper cross machine direction. In some example, the ratio between stiffness in machine direction to the stiffness in cross machine direction is less than 2.5. A method, such as TAPPI T543 om-94, using a Gurley-type stiffness tester, may be used to determine the stiffness of the paper stock. Without being linked by any theory, it is believed that the surface smoothness of the base stock paper is an important factor in the quality of the paper and photographic images printed thereon. A photographic printing base stock with high smoothness and glossiness can be made at effectively low cost, as long as the pigmented sub layer sheets have a minimum smoothness and glossiness level. The surface smoothness can be in the range of from about 0.3 to about 5.0 μm, as measured by a Parker Print Surface (PPS) microprocessor-controlled instrument that performs high speed, precision measurements of paper surface roughness from Testing Machine Inc. (TMI), DE, USA. 
     Pre-Coating Layer ( 120 ) 
     The printable recording media ( 100 ) encompasses a pre-coating layer ( 120 ). Said a pre-coating layer ( 120 ) is applied above the supporting base substrate ( 110 ). Such as illustrated in  FIG. 1 , the pre-coating layer ( 120 ) can be present on one side of the supporting base substrate ( 110 ), i.e. on its image side ( 101 ). Such as illustrated in  FIG. 2 , the pre-coating layer ( 120 ) can also be present on the backside ( 102 ) and on the image side ( 101 ) of the recording media ( 100 ), below the barrier layer ( 140 ). In some examples, the pre-coating layer ( 120 ) is thus applied on both sides of the supporting base substrate ( 110 ). 
     In some examples, the pre-coating layer ( 120 ) is applied over the supporting base substrate ( 110 ) with a coat-weight of about 2 to about 25 grams/meter 2  (gsm) or with a coat-weight ranging from about 10 to about 20 gsm. When applied to both sides of the raw base ( 110 ), the coat-weight of the pigmented pre-coatings layer ( 120 ) can be from about 10 to about 15 gsm for each coating layers. Without being linked by any theory, it is believed that the function of the pre-coating layer ( 120 ) is to create a smooth surface to help develop superior gloss. Additionally, the pre-coating layer ( 120 ) can promote improved opacity, brightness, and appropriate color hue for the print media. 
     The pre-coating layer ( 120 ) contains at least one inorganic pigment and at least one polymeric binder. In some examples, the inorganic pigment may be prepared in powder or slurry form before being mixed with the binder for coating on the substrate. Examples of inorganic pigments include, but are not limited to, titanium dioxide, hydrated alumina, calcium carbonate, barium sulfate, silica, high brightness alumina silicates, boehmite, pseudo-boehmite, zinc oxide, kaolin clays, and/or their combination. The calcium carbonate may be ground calcium carbonate (GCC) or may be a chemical precipitated calcium carbonate (PCC). The pre-coating layer ( 120 ) may contain from about 40 to about 95 wt % of inorganic pigments by total weight of the layer. Further, with regard to the pigments, the pre-coating layer ( 120 ) may include, for example, ground calcium carbonate such as Hydrocarb® 60 available from Omya, Inc.; precipitated calcium carbonate such as Opacarb® A40 or Opacarb® 3000 available from Specialty Minerals Inc. (SMI); clay such as Miragloss® available from Engelhard Corporation; synthetic clay such as hydrous sodium lithium magnesium silicate, such as, for example, Laponite® available from Southern Clay Products Inc., and titanium dioxide (TiO 2 ) available from, for example, Sigma-Aldrich Co. The particle size of inorganic pigments can range from about 0.2 to about 1.5 micrometer and, in some other examples, ranges from about 0.5 to about 1.0 micrometer. 
     The pre-coating layer ( 120 ) contains at least one polymeric binder. Without being linked by any theory, it is believed that the function of the binder is to supply an adhesion force between the raw base ( 110 ) and the pigment particles, as well as binding pigment particles to each other. The binder may be selected from the group of water-soluble binders and water-dispersible polymers that exhibit high binding power for base paper stock and pigments, either alone or as a combination. Suitable polymeric binders include, but are not limited to, water-soluble polymers such as polyvinylalcohol, starch derivatives, gelatin, cellulose derivatives, acrylamide polymers, and water-dispersible polymers such as acrylic polymers or copolymers, vinyl acetate latex, polyesters, vinylidene chloride latex, styrene-butadiene or acrylonitrile-butadiene copolymers. The polymeric binders can be polyvinylalcohol or copolymer of vinylpyrrolidone. The copolymer of vinylpyrrolidone can include various other copolymerized monomers, such as methyl acrylates, methyl methacrylate, ethyl acrylate, hydroxyethyl acrylate, hydroxyethyl methacrylate, ethylene, vinylacetates, vinylimidazole, vinylpyridine, vinylcaprolactams, methyl vinylether, maleic anhydride, vinylamides, vinylchloride, vinylidene chloride, dimethylaminoethyl methacrylate, acrylamide, methacrylamide, acrylonitrile, styrene, acrylic acid, sodium vinylsulfonate, vinylpropionate, and methyl vinylketone, etc. In some examples, the copolymer of vinylpyrrolidone can be a copolymer of vinylpyrrolidone and vinylacetate or vinylcaprolactam or polyvinylalcohol. The polyvinylalcohol or copolymer of vinylpyrrolidone can have a weight average molecular weight ranging from about 10,000 Mw to about 1,000,000 Mw or can have a weight average molecular weight ranging from about 20,000 Mw to about 500,000 Mw. In some examples, the binder is a polyvinylalcohol having a molecular length in the range of 20,000 to 500,000. The inorganic pigment and binder may be used in the following proportions or effective amounts: from 5 to 15 parts by dry weight of binder to 100 parts by dry weight of inorganic pigments. In some other examples, 8 to 10 parts binder are used relative to the 100 parts of pigment. 
     The pre-coating layer ( 120 ) can contain from about 5 to about 40 wt % of water-dispersible binders by total weight of the pre-coating layer and up to 10 wt % of a water-soluble binders. Examples of water-dispersible binders may include, for example, a styrene-butadiene latex such as Gencryl®9780 or PT9619 (from Omnova Solution Inc.); an acrylic polymer sold under the trade name Raycryl® 48083 (available from Specialty Polymers); an aqueous dispersion of an n-butyl acrylate-acrylonitrile-styrene copolymer commercially available under the tradename Acronal®S 504 (available from Baden Aniline and Soda Factory (BASF)); a styrene/n-butyl acrylate copolymer Acronal® S 728 (available from Baden Aniline and Soda Factory (BASF)). In some other examples, the water-dispersible binders have a glass transition temperature (Tg) within the range of about −20° C. to about 35° C. In some other examples, the Tg of the water-dispersible binder is from −10° C. to 10° C. Examples of water-soluble binders may include, for example, a combination of polyvinyl alcohol with methanol sold under the trade name Mowiol® 6-98 (available from Kuraray America, Inc.), and 2-hydroxyethyl starch ether sold under the tradename of Penford® Gum 280 (available from Penford Products Co). 
     In some other examples, the solids content of the coating compositions can range from 60 to 75 percent by weight (wt %) with a viscosity of 1000 to 1500 centipoise (cps) as measured by a low shear Brookfield viscometer at a speed of 100 revolutions per minute (rpm), or 30 cps to 40 cps at a higher shear rate of 4500 rpm using a high shear Hercules viscometer. The pre-coating layer ( 120 ) may also include any of the variety of coating additives known to improve the appearance or functionality of media, such as, for examples, mordants, biocides, optical brightener, surfactants, plasticizers, thickener and cross-linking agents. 
     Top Ink-Receiving Layer ( 130 ) 
     The printable media ( 100 ) further includes a top ink-receiving layer ( 130 ). Said top ink-receiving layer ( 130 ) is applied, above the pre-coating layer ( 120 ), on the image side ( 101 ) of the base substrate as illustrated in  FIG. 1 . Said top ink-receiving layer can be considered as an image receiving layer where the ink will be deposited. Without being limited by any theory, it is believed that the top ink-receiving layer ( 130 ) is specifically formulated to interact with the ink in order to improve the quality of the printed image. Such top ink-receiving layer ( 130 ) can be a liquid electrophotographic printing (LEP) image-receiving layer. By liquid electrophotographic printing (LEP) image-receiving layer, it is meant herein that the layer is adapted to receive image printed using LEP technique, such as printing device using liquid toner manufactured by Hewlett-Packard Company&#39;s Indigo press. 
     In some examples, the coat-weight of the top ink-receiving layer ( 130 ) is ranging from about 5 to about 35 grams/meter 2  (gsm). In some other examples, the coat-weight of the top ink-receiving layer ( 130 ) is ranging from about 10 to about 20 grams/meter 2  (gsm). 
     The top ink-receiving layer ( 130 ) includes inorganic pigments and polymeric binders. The top ink-receiving layer ( 130 ) might further include non-film forming polymers as an optional ingredient. 
     In some examples, the polymeric binders in the top ink-receiving layer ( 130 ) are water-dispersible binders. In some other examples, the polymeric binders that are present in the top ink-receiving layer ( 130 ) have a glass transition temperature (Tg) within the range of about 0° C. to about 35° C. The glass transition temperature (Tg) of the water-dispersible binders, that are present in the top ink-receiving layer ( 130 ), can also be ranging from about 10° C. to about 30° C. The way of measuring the glass transition temperature (Tg) parameter is described in, for example, Polymer Handbook, 3rd Edition, authored by J. Brandrup, edited by E. H. Immergut, Wiley-Interscience, 1989. 
     The polymeric binders can be present, in the top ink-receiving layer ( 130 ), in an amount representing from about 10% to about 30% of the total weight of the layer ( 130 ). Examples of such water-dispersible polymers include, for example, styrene-butadiene latex such as Gencryl®9780 (available from Omnova Solution Inc.), XU31258.50 (available from Styron Inc.) or Litex®PX 9330 (from Synthomer). Examples of suitable water-dispersible polymeric binders also include polybutadiene latex, styrene-butadiene copolymer latex, acrylonitrile-butadiene-styrene terpolymer latex, polychloroprene latex, acrylic latex, polyester emulsions, acrylonitrile-butadiene latex, polyvinyl acetate, polyvinyl acetate copolymers (e.g., vinyl acetate-ethylene latex), and combinations thereof. In some examples, the water-dispersible polymeric binder is a latex binder selected from the group consisting of polybutadiene latex, styrene-butadiene copolymer latex, acrylonitrile-butadiene-styrene terpolymer latex, polychloroprene latex, acrylic latex, polyester emulsions, acrylonitrile-butadiene latex, polyvinyl acetate and polyvinyl acetate copolymers. In some other examples, the water-dispersible polymeric binder is styrene-butadiene copolymer latex. In yet some other examples, the polymeric binder is a carboxylated styrene/butadiene copolymer. 
     The top ink-receiving layer ( 130 ) may further include a water-soluble binder in addition to the water-dispersible polymers. Suitable water-soluble binders include, but are not limited to polymers such as polyvinyl alcohol, starch derivatives, gelatin, cellulose derivatives, and acrylamide polymers. When present, the amount of water-soluble binder is less than 10 wt % of the total weight of the layer. The polymeric binders that are presents in the top ink-receiving layer ( 130 ) can be similar or different from the polymeric binders present in the pre-coating layer ( 120 ). In some examples, polymeric binders that are present in the top ink-receiving layer ( 130 ) and in the pre-coating layer ( 120 ) are water-dispersible binders that have a glass transition temperature (Tg) within the range of about 0° C. to about 35° C. 
     The top ink-receiving layer ( 130 ) includes inorganic pigments. Inorganic pigments are present in the top ink-receiving layer ( 130 ) in an amount representing from about 50% to about 90% of the total weight of the layer ( 130 ). Suitable inorganic pigments may be provided in a powder or slurry form. Examples of suitable inorganic pigments include, but are not limited to, titanium dioxide, hydrated alumina, calcium carbonate, barium sulfate, silica, clays (such as high brightness kaolin clays), zinc oxide and/or combinations thereof. By way of example only, one suitable inorganic pigment that has desirable properties is calcium carbonate. In some examples, inorganic pigments that are present in the top ink-receiving layer ( 130 ) are calcium carbonate. The calcium carbonate may be one or more of ground calcium carbonate (GCC), precipitated calcium carbonate (PCC), modified GCC and modified PCC. Examples of inorganic pigments include, but are in no way limited to, Cartacoat K (available from Clariant Chemical); Snowtex® ST-O, ST-OL, ST-20L, and ST-C (available from Nissan Chemical); Ludox® CL, AM and TMA (available from Grace-Davison Chemical); NyacorAL20, Nyacol® AL20, Nyacol®A1530, Nyacol®Ce02, NyacorSN15, Nyacol®DP5370, and NYACOL® Zr50/20 (available from Nyacol Nano Technologies). Examples of inorganic pigments include also GCC, sold under the tradename Hydrocarb®HG or Covercarb®HP (from Omya Inc.) or PCC sold under the tradename Opacarb®A40 (available from Specialty Minerals Inc.). 
     By way of example only, one suitable inorganic pigment that has desirable properties is calcium carbonate. In some examples, inorganic pigments that are present in the top ink-receiving layer ( 130 ) are calcium carbonate. The calcium carbonate may be one or more of ground calcium carbonate (GCC), precipitated calcium carbonate (PCC), modified GCC and modified PCC. In some other examples, the pigments are ground calcium carbonate (GCC) or precipitated calcium carbonate (PCC). Depending upon the distinct arrangement of the calcium, carbon, and oxygen atoms forming the calcium carbonate in the crystal structure, the calcium carbonate can assume three different crystal structures: calcite, aragonite, and/or an unstable vaterite crystal. The calcite crystal form of the calcium carbonate may assume any one of four different shapes: rhombohedral, scalenohedral, prismatic and spherical. Further, the aragonite crystal form of calcium carbonate assumes discrete or clustered needle-like shapes. 
     The top ink-receiving layer ( 130 ) can be formed by incorporating a calcium carbonate pigment having discrete acicular morphology and a certain aspect ratio. The aspect ratio of needle-like aragonite particles in the pigment coating may be defined as: (An=l/d) where An is the aspect ratio of needle-like particles in the pigment top coating; (l) is the average length of calcium carbonate particles and (d) is average width of the particles. In some examples, the average length of the calcium carbonate particles (l) is much greater than their average width (d). In some other examples, the aspect ratio (An) is between about 50 and about 300, or between about 70 and about 180. 
     The particle size of the calcium carbonate based pigments that is present in the top ink-receiving layer ( 130 ) can range from about 0.1 to about 0.8 micrometers, or from about 0.2 to about 0.5 micrometers. The inorganic pigments can have a narrow particle size distribution (PSD) where PSD=(D 85 /d 15 ) 1/2 ; wherein “D 85 ” is meant to be understood as the particle size in micrometers at which approximately 85% of the particles in the calcium carbonate based pigments by size are smaller, according to a distribution curve. Similarly, the term “d 15 ” is meant to be understood as the particle size in micrometers at which approximately 15% of the particles by size are smaller, according to a size distribution curve. In some examples, the inorganic pigments that are part of the top ink-receiving layer ( 130 ) have a PSD that is between about 1.2 and about 1.8. The greater PSD in the pigment coating layer will result in more abrasive and less smooth surface finish in micro-scale and reduce Indigo press blank life. The rough surface finish can be ironed in subsequent super calendaring processing through the application of a higher temperature and line pressure. 
     The top ink-receiving layer ( 130 ) can further include non-film forming polymers (also called herein plastic pigment). Non-film forming polymers are water dispersed, polymeric hollow spherical particles filled with water that are non-film forming in ambient conditions and that remain as discrete particles during coating. Such polymers have no substantial coalescence under manufacture and storage conditions. In more details, upon evaporation of the continuous phase (such as solvent and/or water of the dispersed solid-liquid system), the polymers are able to resist deformation and further coalescence. Said polymers can have particulate sizes ranging from about 0.3 μm to about 2 μm and/or a glass transition temperature (Tg) from about 50° C. to about 120° C. In some examples, the glass transition temperature (Tg), for these non-film forming polymers, is greater than about 70° C. Such non-film forming polymers can be present in an amount representing from about 5 to about 30 wt % by total weight of the top ink-receiving layer. The ratio between the non-filming forming polymers to pigments can be from 1:100 to 1:10. Non-film forming polymers can be chosen among the group consisting of styrene, acrylic, styrene/acrylics, vinyl/acetate, polyacrylics, methacrylates and combinations thereof. It is believed that if the particle size of the non-film forming polymers (i.e. plastic pigments) is greater than approximately 2-3 micrometer, the plastic pigment particles might help to enhance the surface smoothness and the gloss of the printable media ( 100 ). The ink-receiving layer may thus contain non-film forming polymer particles having particle sizes close to that of the needle-like aragonite particles. The size of the non-film forming polymer particles may range from about 0.2 to 0.5 microns and can be present in an amount of approximately 0.5 to 5 parts by weight based on 100 parts of inorganic pigments. 
     In some examples, the non-film forming polymers are polystyrene latex polymers. In some other examples, the non-film forming polymers are plastic pigment slurry of styrene/butadiene emulsion copolymers. Examples of non-film forming polymers that can be used in accordance with embodiments of the present invention include Ropaque® BC-643, Ropaque® HP-543, or Ropaque® OP-84 (all manufactured by Rohm and Haas Company, USA) and HS-3000NA or HS-3020NA (available from The Dow Chemical Company, USA). Other specific examples of these polymers may include, a styrene acrylic emulsion polymer sold under the trade name Raycat® 29033, a polyacrylic emulsion polymer sold under the trade name Raycat® 78, and an acrylic emulsion polymer sold under the trade name Raycryl® 30S available from Specialty Polymers, Inc. Other examples of such non-film forming polymers include Dow DPP™ 3720 (available from Dow Chemical). Other small amount of additives such as, for examples, slip aid, deformer, dye, OBA, pH control agent, dispersant and thickener can also be added to the top ink-receiving layer ( 130 ). 
     Barrier Layer ( 140 ) 
     The printable media ( 100 ) includes a barrier layer ( 140 ). Said barrier layer ( 140 ) is made from a barrier layer composition that is applied on the supporting base substrate ( 110 ), on the backside ( 102 ) of the printable media ( 100 ). As “barrier layer”, it is meant herein that the layer will act as an obstacle in order to prevent moisture to penetrate into the media. Without being limited by any theory, it is believed that the barrier layer ( 140 ) is specifically formulated to provide moisture barrier to the printed article. Furthermore, it is believed that the coat-weight of barrier layer ( 140 ,) on the backside ( 102 ) of the media, is designed to counter-balance the “pre-stress” generated by the coating layers in the image-receiving side, in other words to be a balance force resulting from the presence of the printed image ( 210 ) and of the post-image lamination layer ( 220 ). 
     When the barrier layer ( 140 ) is applied on the backside ( 102 ), the coat-weight can be adapted to the weight of the layers present on the image side, so that the final product is curl balanced in all the conditions. In some examples, the higher the thickness of the image side coating and lamination film layers is, the thinker the barrier layer is. The weight ratio between barrier layers to the post printing lamination layer ( 220 ) is carefully designed to ensure lay flat of the final printed article/photo. In some example, the ratio between the barrier layer ( 140 ) to lamination film layer ( 220 ) is from 3:1 to 0.5 to 1. In some examples, the coat-weight of the barrier layer ( 140 ) is ranging from about 10 to about 60 grams/meter 2  (gsm), in some other examples, is ranging from about 12 to about 45 grams/meter 2  (gsm). 
     As used herein, the term barrier layer refers to a layer that may contain a polyolefin polymer material, an agro-based polymer material or combinations thereof. The term polyolefin material refers to a polymer produced by olefin homo-polymerization or copolymerization reaction via either high-pressure polymerization or low pressure in the presence of special catalyst like Ziegler and metallocene catalysts, where olefin refers to a hydrocarbon compounds containing a carbon-carbon double bond alkene with general formula C n H 2n . The polymeric barrier coating contains polyolefin polymer materials or (resins). Examples of polyolefin resins include, but are not limited to, high density polyethylene (HDPE), low density polyethylene (LDPE), polypropylene (PP), polymethylpentene (PMP), and copolymers of ethylene with hexane, butane, and octane (linear low density polyethylene, LLDPE). The polyolefin resins can also be blends of these polymeric materials, such as HDPE/LDPE, LDPE/LLDPE, PP/LDPE, and PP/LLDPE. In some examples, the polyolefin material that is present in the barrier layer is selected from the group consisting of polyethylene (PE), polypropylene (PP), polymethylpentene, polybutylene polymer, ethylene vinyl acetate polymer and mixtures thereof. In some other examples, the barrier layer contains a polyolefin polymer material that is a polyethylene, a polypropylene or an ethylene vinyl acetate polymer. In yet some other examples, the barrier layer encompasses a low density polyethylene (LDPE), a high density polyethylene (HDPE) or combinations thereof. The barrier layer can encompasses low density polyethylene (LDPE) and high density polyethylene (HDPE) in a ratio that is between 30:70 and 70:30. The polyolefin barrier layer may also encompass polypropylene (PP) and polyethylene terephthalate (PET). The term agro-based material refers to a polymer produced from biomass such as starches, a polymer produced by conventional or chemical synthesis such as polylactic acid (PLA), or a polymer produced by microbial such as polyhydroxylalkanoates (PHAs). 
     Antistatic Layer ( 150 ) 
     The printable recording media of the present disclosure encompasses an antistatic layer ( 150 ) that contains antistatic additives. As “antistatic layer”, it is meant herein that the layer will be able to reduce or eliminate buildup of static electricity in order to provide antistatic performances to the media. The antistatic layer is formed from a non-aqueous composition and is applied with a hot-melt thermal extrusion method on the backside on the media ( 102 ), above the barrier layer ( 140 ). Such antistatic layer ( 150 ) can have a coat-weight ranging from about 1 gsm to about 10 gsm. 
     The antistatic layer ( 150 ) that is part of the printable recording media is a hot-melt extrudable antistatic layer. As used herein, the term “hot-melt extrudable” refers to a composition containing antistatic additives that has been hot-melt extruded. A hot-melt extrudable composition is sufficiently rigid at standard ambient temperature and pressure but is capable of deformation or forming a semi-liquid state under elevated heat or pressure. Although the process referred to above has been called a hot-melt extrusion, other equivalents processes such as extrusion lamination, hot or cold film lamination, injection molding, hot dipping, melt casting and compression molding may be used. 
     In some examples, the antistatic layer ( 150 ) contains polyolefin polymer materials and antistatic additives. In some other examples, the antistatic layer ( 150 ) contains low density polyethylene (LDPE), high density polyethylene (HDPE) or combinations thereof as polyolefin polymer materials and antistatic additives. In yet some other examples, the antistatic layer contains low density polyethylene (LDPE) and antistatic additives. 
     The antistatic additives can be present in an amount representing from about 1 wt % to about 25 wt %, or from about 5 wt % to about 20 wt %, by total weight of the antistatic layer ( 150 ). Antistatic additives can be migratory and non-migratory type antistatic additives. Examples of migratory type of antistatic additives include 10053, 101132 and 101140 from Ampacet Corporation. Examples of non-migratory additive include 101710 available from Ampacet Corporation. 
     The antistatic layer ( 150 ) can include glycerol mono-stearate migratory (GMS) as antistatic additive (such as 10069 available from Ampacet). In some examples, about 5% by weight of glycerol mono-stearate migratory is added to polyolefin polymer materials (such as LDPE for example) in order to form an antistatic layer of about 3 gsm on top of the barrier layer ( 140 ). It is believed that this antistatic additive will migrate to the surface of the layer and will form hydrogen bonding with water in the atmosphere. In some other examples, about 15% by weight of a non-migratory additive (101710 from Ampacet) is added to polyolefin polymer materials (such as LDPE for example) in order to form an antistatic layer of about 3 gsm on top of the barrier layer ( 140 ). 
     In some examples, the antistatic layer could also be part of the barrier layer ( 140 ), meaning thus that antistatic additives are added to the barrier layer ( 140 ). The antistatic additives will thus be present in an amount representing from about 0.1% to about 20% of the barrier layer ( 140 ). 
     Method for Forming a Printed Article 
     The printable recording materials are used in printing process in view of forming printed article. In some examples, a method for forming printed articles includes: obtaining a printable recording media ( 100 ) comprising a supporting base substrate ( 110 ) having, on its image side ( 101 ), a pre-coating layer ( 120 ) and a top ink-receiving layer ( 130 ) that include inorganic pigments and polymeric binders; and having, on its backside ( 102 ), a barrier layer ( 140 ) and an antistatic layer ( 150 ); applying an ink composition on the image side ( 101 ) of the printable media to form a printed image; and applying a post-image lamination film ( 220 ) over the ink layer ( 210 ). Such printing method results in printed article ( 200 ) with enhanced image quality and enhanced absorption performances. An example of the method for forming printed articles in accordance with the principles described herein, by way of illustration and not limitation, is shown in  FIG. 4 .  FIG. 4  illustrates embodiments of the printing method that encompasses obtaining a printable recording media ( 100 ), applying an ink composition onto said media, applying a post-image lamination film ( 220 ) and obtaining a printed article ( 200 ). 
     After the images are deposited, established, or printed on the printable media ( 100 ), i.e. after an ink layer ( 210 ) is formed onto the printable media, a post-image lamination film or laminate layer ( 220 ) is disposed. Such post-image lamination film ( 220 ) is deposited over the ink, or printed image, that is present on the top image receiving layer ( 130 ). In this manner, the laminate layer may provide a final photo finish such as a glossy or matte finish. Further, the laminate layer may provide image durability (such as scratch resistance) and image permanence to the media with what a consumer may consider is a true look and feel of photographic paper. The printed images, resulting from such printing technique, are photo printed image, present high image quality, a good surface smoothness and high gloss appearance. 
     The post-image lamination film layer ( 220 ) can be applied during the printing process (on the press during printing) or can be applied after the printing process using a hot or cold laminator. The post-image lamination film layer ( 220 ) can be made of a polyester material or of a polypropylene composition. In some examples, the laminate film ( 220 ) is a polyester material. Such polyester material includes, but is not limited to, polyethylene terephthalate (PET), glycol-modified PET, polybutylene terephthalate (PBT), polytrimethylene terephthalate (PTT), polyethylene naphthalate (PEN), polyether terephthalate, polyurethane terephthalate, or a combination or a mixture of two or more thereof. PET may be obtained from Chevron Phillips Chemical Company, The Woodlands, Tex., or from Formosa Plastics Corporation, USA, Livingston, N.J. In some examples, the lamination film is a polypropylene composition. The polypropylene composition contains homo-polymers of polypropylene (PP) and poly(ethylene vinyl acetate) (EVA), for example. Said two components can be coextruded together (i.e., ‘PP and EVA’). The PP film polymer and EVA film polymer (either separate or coextruded) may be obtained from film extruder companies and casting companies including, but not limited to, Fabrene, Ontario Canada; Yidu Digital Image company, China. The lamination film is hot laminated to the image layer by a hot laminator. The typical temperature for the hot laminator is about 150° F. 
     The printable recording media, as described herein, (i.e. comprising a supporting base substrate having, on its image side, a pre-coating layer and a top ink-receiving layer that include inorganic pigments and polymeric binders; and having, on its backside, a barrier layer and an antistatic layer) contains also a post-image lamination film ( 220 ) that is disposed on the top ink-receiving layer ( 130 ) after an ink layer ( 210 ) is printed. 
     The ink composition may be deposited, established, or printed on the printable media using any suitable printing device. The method for forming printed images can be done by means of digital printing technology. In some examples, the ink may be deposited, established, or otherwise printed on the printable media is a solid toner or a liquid toner. The solid toner or the liquid toner may include toner particles made, e.g., from a polymeric carrier and one or more pigments. The liquid toner may be an organic solvent-based (e.g., hydrocarbon) liquid toner. The solid toner or the liquid toner may be deposited, established, or otherwise printed on the examples of the printable media using, respectively, a suitable dry or liquid press technology, such as a dry toner electrophotographic printing device or a liquid toner electrophotographic printing device. In some other examples, the ink is a liquid electrophotographic ink (liquid toner or liquid Electrolnk) and is applied via electrophotographic printing method. Representative examples of printers used to print on the printable media, include, but are not limited to, Indigo® WS6000P Digital Printing Press or T300 Digital Web Press, both available from Hewlett-Packard Company (Palo Alto, Calif., USA). 
     Thus, in some embodiments, a method for forming printed articles includes obtaining a printable recording material ( 100 ) with a supporting base substrate ( 110 ) having, on its image side ( 101 ), a pre-coating layer ( 120 ) and a top ink-receiving layer ( 130 ) that include inorganic pigments and polymeric binders; and having, on its backside ( 102 ), a barrier layer ( 140 ) and an antistatic layer ( 150 ); providing a liquid electrophotographic ink; applying said ink composition on the image side of the printable media, to form a printed image via electrophotographic printing method; and applying a post-image lamination film ( 220 ). 
     The Printed Article 
     The printed article ( 200 ), resulting from the printing process as described above, encompasses, thus, a supporting base substrate ( 110 ) having, on its image side, a pre-coating layer ( 120 ) and a top ink-receiving layer ( 130 ) that include inorganic pigments and polymeric binders; and having, on its backside, a barrier layer ( 140 ) and an antistatic layer ( 150 ); a printed feature ( 210 ) applied on top of said printable recording material, on its image side; and a post-print lamination layer ( 220 ) disposed above said printed image. The post-print lamination layer ( 220 ), or lamination film, is applied after an ink layer ( 210 ) has been printed or otherwise disposed onto the top ink-receiving layer ( 130 ) on the image side ( 101 ) of the printable media ( 100 ) during, for example, the printing process. Without being linked by any theory, it is believed that post-print lamination layer ( 220 ), applied to the printed article, provides gloss finish, semi-gloss, luster or matte finish. The lamination film may also provide scratch resistance to the printed article. 
     As described above, the laminate layer or post-image lamination film ( 220 ) can be made of a polyester material or of a polypropylene composition. In some examples, the post-image lamination layer ( 220 ) encompasses polyester, polypropylene (PP), PVC, nylon, and other suitable polymer film. In some other examples, the laminate film ( 220 ) is a polyester material. The thickness of the post-print lamination layer ( 220 ) can be in the range of from about 10 μm to 60 about μm (micro); or, in the range of from about 20 μm to 50 about μm. As mentioned above, the coat-weight ratio of the barrier layer ( 140 ) and of the antistatic layer ( 150 ) to the laminate layer ( 220 ) may be controlled in order to achieve acceptable curl performance across environmental conditions. In some examples, the coat-weight ratio of barrier layer ( 140 ) and antistatic layer ( 150 ), that is applied to the non-image receiving side ( 101 ) of the media ( 100 ) with respect to the laminate layer ( 220 ) that is applied to the image receiving side ( 202 ) of the printed article ( 200 ), may be between 1:1 and 3:1. In some other examples, the coat-weight ratio of the barrier layer ( 140 ) to the laminate layer ( 220 ) may be 1.5:1. In yet some other examples, the coat-weight ratio of the barrier layer ( 140 ) and antistatic layer ( 150 ) to the laminate layer ( 220 ) may be 1.25:1. Thus, in this manner, curling of the printed article ( 200 ) may be reduced or eliminated across all environmental conditions including different relative humilities and temperatures. 
     Method for Forming a Printable Recording Material 
     In some examples, according to the principles described herein, a method of making a printable recording media comprising a supporting base substrate ( 110 ) having, on its image side ( 101 ), a pre-coating layer ( 120 ) and a top ink-receiving layer ( 130 ) that include inorganic pigments and polymeric binders; and having, on its backside ( 102 ), a barrier layer ( 140 ) and an antistatic layer ( 150 ) is provided. Such method encompasses providing a supporting base substrate ( 110 ); applying a pre-coating layer ( 120 ) that contains inorganic pigments and polymeric binders on the raw base substrate on the image side of the supporting base substrate; a top ink-receiving layer ( 130 ) that includes inorganic pigments and polymeric binders, over said pre-coating layer; drying and calendaring said pre-coating layer and top ink-receiving layer and extruding a barrier layer ( 140 ) and an antistatic layer ( 150 ) on the backside of the supporting base substrate. In some examples, the pre-coating layer ( 120 ) is applied to the supporting base substrate on the image receiving side and on the backside of the printable media. In some other examples, the barrier layer ( 140 ) and the antistatic layer ( 150 ) are coextruded on the backside of the supporting base substrate. 
     The pre-coating layer ( 120 ) and the top ink-receiving layer ( 130 ) are thus coated to the image side ( 102 ) and the pre-coating layer ( 120 ) is coated to the backside ( 102 ) of the base substrates ( 110 ). 
     Such pre-coating layer ( 120 ) and top ink-receiving layer ( 130 ) can be applied using an on-machine or off-machine coater. Examples of suitable coating techniques include slotted die application, roller application, curtain coater, blade application, rod application, air knife application, gravure application, airbrush application, and others known in the arts. In some examples, the pre-coating layer(s) ( 120 ) are coated using an offline coater, or applied during raw base paper making process. The top ink-receiving layer ( 130 ) can be applied using in line or offline coater such as blade coater, roll coater, slot, or curtain coater. The solids content of the top ink-receiving layer ( 130 ) can range from about 20 wt % to about 68 wt % depending on coating method used, with a viscosity of about 100 cps to about 2000 cps as measured by low shear Brookfield viscometer at a speed of about 100 rpm. The coat layer can then be dried by convection, conduction, infrared radiation, atmospheric exposure, or other known method. 
     After coating the base stock with pre-coating layer ( 120 ) and top ink-receiving layer ( 130 ), a calendaring process can be used to achieve desired gloss or surface smoothness. The calendaring device can be a separate super calendaring machine, an on-line soft nip calendaring unit, an off-line soft nip calendaring machine, or the like. Super-calendering is calendering in a calender unit in which nips are formed between a smooth-surface press roll, such as a metal roll, and a roll covered with a resilient cover, such as a polymer roll. The resilient-surface roll adapts itself to the contours of the surface of paper and presses the opposite side of paper evenly against the smooth-surface press roll. Any of a number of calendering devices and methods can be used. The calendering device can be a separate super-calendering machine, an on-line calendaring unit, an off-line soft nip calendaring machine, or the like. Some calendering systems do not require the paper to be as completely dried as other forms of calendering. In some examples, the calendering is carried out at a temperature ranging from about 50 to about 220° C. (metal roll surface temperature) and, in some other examples, from about 100 to about 170° C. The nip pressure can be any value between about 50 to about 300 Kg/cm 2 . The roughness, on the image side ( 101 ) of the printable recording media, after calendar process can be less than 3 micro, and less than 6 micro for the backside ( 102 ) on the image side of the printable recording media, per Park Print Surface method (PPS method). 
     The barrier layer ( 140 ) and the antistatic layer ( 150 ) can be applied according to various extrusion operations like extrusion coating, lamination, hot-melt extrusion or modification of cast extrusion operation. In some examples, the barrier layer and the antistatic layer are applied on the backside of the base substrate with the use of a heat melted extrusion coating processing. The barrier layer is extrusion coated on the backside of the supporting base substrate with a coat-weight ranging from about 12 to about 50 grams/meter 2  (gsm), or with a coat-weight ranging from about 20 to about 30 gsm. The antistatic layer can have a coat-weight ranging from about 1 gsm to about 10 gsm. In some examples, the barrier layer ( 140 ) and antistatic layer ( 150 ) are formed by a co-extrusion process. The barrier layer and the antistatic layer can also be made by hot-melt extrusion technique. As used herein, the terms extrude and hot-melt extrusion refer to process wherein the material is heated to a temperature at, or above, its melting point and deposited on a moving substrate at a uniform thickness. In some examples, in the extrusion process, the material is heated to a considerably higher temperature than its melting point. The extrusion process may be practiced within a wide range of extrusion temperatures, for example, from about 230° C. to about 350° C. in case of polyethylene, and speeds, for example, from about 60 m/min to about 460 m/min. In such extrusion processes, the component of the barrier layer is first subjected to heat and pressure inside the barrel of an extruder. The molten polymer is then forced through the narrow slot of an extrusion-coating die by an extruder screw. At the exit of the slot die, a molten curtain emerges. In some examples, this molten curtain is drawn down from the die into a nip between two counter-rotating rolls, a chill roll and pressure roll. In some other examples, while coming into contact with a faster moving substrate in the nip formed between the chill roll and the pressure roller, a hot film is drawn out to the desired thickness, forming a layer with a specific thickness onto the substrate. 
     EXAMPLES 
     Ingredients 
       
     
       
         
           
               
               
               
             
               
                 TABLE 1 
               
               
                   
               
               
                 Ingredient name 
                 Nature of the ingredients 
                 supplier 
               
               
                   
               
             
            
               
                 Hydrocarb ®60 MEZ 
                 GCC pigment 
                 Omya Inc. 
               
               
                 Opacarb ®3000 
                 PCC pigment 
                 SMI 
               
               
                 Litex ®PX 9330 
                 Polymer Latex (Tg of 22° C.) 
                 Synthomer 
               
               
                   
                 (carboxylated styrene/butadiene 
               
               
                   
                 copolymer) 
               
               
                 Gencryl PT ®9619 
                 Styrene butadiene Polymer 
                 Omnova 
               
               
                   
                 Latex (Tg of −6° C.) 
                 Solution Inc. 
               
               
                 Dow DPP ®3720 
                 polystyrene latex 
                 Dow 
               
               
                 Mowiol ®6-98 
                 PVOH 
                 KSE 
               
               
                 Ca-stearate 
                 lubricant 
                 Greven 
               
               
                 Alcogum ®L265 
                 Thickener 
                 Alco 
               
               
                   
                   
                 Chemicals 
               
               
                 Sterocoll ®BL 
                 Thickener 
                 BASF 
               
               
                 Antistatic 10069 
                 migratory Antistatic additive 
                 Ampacet 
               
               
                   
                   
                 Corporation 
               
               
                 Antistatic 1000017-N 
                 non- migratory Antistatic 
                 Ampacet 
               
               
                   
                 additive. 
                 Corporation 
               
               
                   
               
            
           
         
       
     
     Example 1 
     Preparation of the Media 
     Pre-coat layer and top ink-receiving layer formulations a and b are prepared by mixing the ingredients as illustrated in table 2 Media A and B are printable media that both contain a raw base substrate ( 110 ) with a coat-weight of 150 gram/square meter (gsm). The raw base is made with base paper stock prepared with cellulose fibers. Such base paper stock contains about 60% of hardwood, about 20% of softwood and about 10% of calcium carbonate fillers. The raw base is surface sized with oxidized starch. The pickup rate for the starch is 1 gsm each side. 
     The pre-coating layer ( 120 ) and top ink-receiving layer ( 130 ) are applied on the raw base substrate ( 110 ) with a lab blade coater at a coat-weight of about 12 gsm. The media are then calendered with a lab soft calender at 1000 psi and 100° C. The final smoothness of the recording media is of about 1 micro per PPS method. 
     
       
         
           
               
               
               
             
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                 Formulation a 
                 Formulation b 
               
               
                   
                 MEDIA A 
                 MEDIA B 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
            
               
                 Base paper (110) (in wt %) 
               
            
           
           
               
               
               
            
               
                 hardwood fiber 
                 60.0% 
                 60.0% 
               
               
                 softwood fiber 
                 20.0% 
                 20.0% 
               
               
                 calcium carbonate 
                 10.0% 
                 10.0% 
               
            
           
           
               
            
               
                 Pre-coating layer (120) (in part per weight) 
               
            
           
           
               
               
               
            
               
                 Hydrocarb ®60 MEZ 
                 65 
                 65 
               
               
                 Opacarb ®3000 
                 35 
                 35 
               
               
                 Litex ®PX 9330- Tg of 22° C. 
                 9 
                 — 
               
               
                 Gencryl PT ®9619 Tg of −6° C. 
                 — 
                 9 
               
               
                 Mowiol ®6-98 
                 1 
                 1 
               
               
                 Defoamer 
                 0.042 
                 0.042 
               
               
                 Alcogum ®L261 
                 0.13 
                 0.13 
               
               
                 Sterocoll ®BL 
                 0.047 
                 0.047 
               
               
                 NaOH 
                 0.06 
                 0.06 
               
            
           
           
               
            
               
                 Top ink-receiving layer (130) (in part per weight) 
               
            
           
           
               
               
               
            
               
                 Opacarb ®3000 
                 100 
                 100 
               
               
                 Litex ®PX 9330 (Tg of 22° C.) 
                 9 
                 — 
               
               
                 Gencryl ®PT ®961 (Tg of −6° C.) 
                 — 
                 9 
               
               
                 Dow DPP ®3720 
                 3 
                 3 
               
               
                 Mowiol ®6-98 
                 1 
                 1 
               
               
                 Defoamer 
                 0.044 
                 0.044 
               
               
                 Ca-stearate 
                 0 
                 0 
               
               
                 Alcogum ®L265 
                 0.146 
                 0.146 
               
               
                 Sterocoll BL 
                 0.017 
                 0.017 
               
               
                 NaOH 
                 0.06 
                 0.06 
               
               
                   
               
            
           
         
       
     
     Media A and B have, on the image side ( 101 ) of the raw base substrate, a pre-coating layer ( 120 ) with a coat-weight of 12 gsm, a top ink-receiving layer ( 130 ) with a coat-weight of 12 gsm, applied over the pre-coating layer ( 120 ) and have, on the backside ( 102 ) of the raw base substrate, a pre-coating layer ( 120 ), with a coat-weight of 3 gsm and a barrier layer ( 140 ) with a coat-weight of 25 gsm that is applied over the pre-coating layer ( 120 ). In the media sample A2 and A3 according to the present disclosure, an antistatic layer ( 150 ) is applied, by co-extrusion with the barrier layer ( 140 ), at a coat-weight of 3 gsm. 
     The barrier layers ( 140 ) and, when present, the antistatic layer ( 150 ) are applied to the backside of the raw base substrate by extrusion coating. The formula of the barrier layer ( 140 ) and its applied coat-weight are illustrated in the Table 3 below. The Table 3 also shows the formulation and the coat-weight of the antistatic layer ( 150 ) when applied to the Media A2 and A3. Media A1 is a control sample with only a barrier layer ( 140 ). Sample A2 includes an antistatic layer with migratory type antistatic additive. Sample A3 has antistatic layer which is non-migratory type antistatic additive. 
     
       
         
           
               
               
               
               
               
             
               
                 TABLE 3 
               
               
                   
               
               
                   
                 Media 
                 Media 
                 Media 
                 Media 
               
               
                 Coated substrate 
                 Sample A1 
                 Sample A2 
                 Sample A3 
                 Sample B 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
            
               
                 barrier layer (140) 
               
            
           
           
               
               
               
               
               
            
               
                 HDPE 
                 12.5 gsm 
                 12.5 gsm 
                 12.5 gsm 
                 12.5 gsm 
               
               
                 LDPE 
                 12.5 gsm 
                 12.5 gsm 
                 12.5 gsm 
                 12.5 gsm 
               
            
           
           
               
            
               
                 Antistatic layer (150) 
               
            
           
           
               
               
               
               
               
            
               
                 LDPE 
                 — 
                 2.85 gsm 
                  2.5 gsm 
                 — 
               
               
                 Antistatic 10069 
                 — 
                 0.15 gsm 
                 — 
                 — 
               
               
                 from 
               
               
                 Antistatic 
                 — 
                 — 
                  0.5 gsm 
                 — 
               
               
                 1000017-N 
               
               
                   
               
            
           
         
       
     
     Example 2 
     Media Adhesion Performances 
     The media samples are then printed on HP Indigo press WS6000 and tested to check ink adhesion and antistatic performances. The ink adhesion is measured by using a 3M tape. The tape is placed on the imaged sample. After the tape is pulled off the image, the OD loss is measured. The acceptable toner adhesion for photo application is less than 15% OD loss after 1 hour printing. One hour after printing, both samples A2 and B are tested for toner adhesion at different time interval (0 min, 15 min and 1 hour,) for the different colors. The KOD is black optical density, the COD is optical density for the cyan color, the MOD is optical density for the magenta color and the YOD is optical density for yellow color. Table 4 below shows the OD retained compared to the control (OD measured before toner adhesion test) after the tape is pulled off from the image. The results demonstrate that media A2 has good adhesion performance while sample B showed poor adhesion. 
     
       
         
           
               
               
               
               
               
             
               
                   
                 TABLE 4 
               
               
                   
                   
               
               
                   
                 KOD 
                 COD 
                 MOD 
                 YOD 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
            
               
                 MEDIA A2 (formulation a) 
               
            
           
           
               
               
               
               
               
            
               
                 control 
                 1.417 
                 0.638 
                 1.577 
                 1.106 
               
               
                  0 min 
                 1.016 
                 0.428 
                 1.114 
                 0.802 
               
               
                 15 min 
                 1.371 
                 0.607 
                 1.117 
                 1.073 
               
               
                 60 min 
                 1.446 
                 0.645 
                 1.286 
                 1.108 
               
            
           
           
               
            
               
                 MEDIA B (formulation b) 
               
            
           
           
               
               
               
               
               
            
               
                 control 
                 1.407 
                 0.631 
                 1.569 
                 1.086 
               
               
                  0 min 
                 0.52 
                 0.395 
                 0.737 
                 0.519 
               
               
                 15 min 
                 0.631 
                 0.395 
                 0.535 
                 0.548 
               
               
                 60 min 
                 0.75 
                 0.505 
                 0.555 
                 0.772 
               
               
                   
               
            
           
         
       
     
     Example 3 
     Media Antistatic Performances 
     The media are tested for their antistatic performances. In order to have good antistatic performances the media should be able to pass the NFPA-99 antistatic specification (National Fire Prevention Agency section  99  test methodology). Such test means that the sample should have less than 50% relative humidity and that the sample should have a static decay below 0.5 seconds (90% dissipation of 5 kV) or a or surface resistance of less than 10 11  Ohms. 
     The samples A1, A2 and A3 are tested for the NFPA-99 antistatic specification. Five specimens of dimensions of 3.5″×5.5″ are cut in the MD from the white film and conditioned at 50% RH and 25° C. for 2 days. Static decay time is then measured for 90% dissipation (10% cutoff) of the applied 5 kV charge at 50% RH. Surface resistivity is measured on the surface after contacting the probe with the film surface for 1 minute. The test results are illustrated in Table 5 below. 
     
       
         
           
               
               
               
               
             
               
                 TABLE 5 
               
               
                   
               
               
                 antistatic property per NFPA-99 
                 Media A1 
                 Media A2 
                 Media A3 
               
               
                   
               
             
            
               
                 Average Static Decay (seconds) 
                 1.1 
                 0.03 
                 0.02 
               
               
                 Average Surface Resistivity 
                 &gt;10 11   
                 4.1 × 10 10   
                 &gt;10 11   
               
               
                 (Ohms) 
               
               
                 Performance in press and finishing 
                 Failed due to 
                 good 
                 good 
               
               
                   
                 multi-feed 
               
               
                   
               
            
           
         
       
     
     According to these results, it can be seen that sample A2 and sample A3 passed NFPA-99 AS specification, meaning thus that such media have good antistatic performances. In addition, samples A2 and A3 performed very well during cutting, transport and stacking during finishing process, but sample A1 failed due to multi-feed during feed and transport. (Sample A1 is stick together because of high static buildup after a short time of operation).