Patent Publication Number: US-3970483-A

Title: Normalized alloy steel for use at elevated temperature

Description:
One prior art steel currently available commercially for high temperature applications is a normalized silicon-killed steel containing about 0.15 to 0.21% carbon, 0.70 to 1.0% manganese, 0.40 to 0.65% chromium, 0.45 to 0.60% molybdenum, and 0.05 to 0.10% vanadium. This hot rolled steel, normalized at a temperature of 1550° to 1650°F is characterized by a stable ferrite-bainite microstructure having good notch toughness and good stress rupture ductility at temperature up to 1000°F. On the other hand, this steel does suffer one disadvantage in having a relatively narrow normalizing temperature range of 1550° to 1650°F. A small increase in the ideal normalizing temperature can result in a major change in the final microstructure, i.e. from the desired ferrite-bainite microstructure, to a completely bainitic microstructure. The completely bainitic microstructure is undesirable because the toughness thereof is considerably lower than the two-phase ferrite-baimite microstructure. The reason for the change in microstructure, i.e. the elimination of proeutectoid ferrite, is that a relatively small increase in normalizing temperature substantially increases the austenite grain size with a concomitant increase in the hardenability of the steel. Thus, the proeutectoid ferrite reaction is suppressed and the completely bainitic microstructure is formed. 
     It is known that the addition of a small amount of aluminum, about 0.04%, to the silicon-killed Cr-Mo-V steel will result in an increase in the grain coarsening temperature of the austenite and, therefore broaden the permissible normalizing temperature. With such an aluminum addition, therefore, the desired microstructure can be more easily achieved without the need for exacting temperature controls. Nevertheless, the aluminum containing version has not been successful commercially because the aluminum addition also results in a deterioration of the notch toughness of the steel as measured by Charpy V-notch impact tests. In addition, the stress rupture elongation at elevated temperatures is reduced and deteriorates with increasing time, indicating that the aluminum containing steel may embrittle during service at elevated temperatures. 
     It is an object of this invention to provide a new and improved silicon-killed Cr-Mo-V steel for high temperature service which has a broader normalizing temperature range. 
     Another object of this invention is to provide a silicon-killed Cr-Mo-V steel for high temperature service which contains a small addition of columbium to increase the grain coarsening temperature of the austenite and therefore permit better control of the resultant microstructure upon normalizing. 
     A further object of this invention is to provide a silicon-killed Cr-Mo-V steel for high temperature service which is modified to increase the austenite grain coarsening temperature without causing any deterioration in the steels mechanical properties. 
    
    
     This invention is predicated upon any discovery that the addition of a small amount of columbium to the conventional silicon-killed Cr-Mo-V high temperature steel will significantly broaden the permissible normalizing temperature to thus assure microstructural stability in the normalized steel. Unlike aluminum, columbium does not in any way adversely affect the steel&#39;s mechanical properties. The amount of columbium required is small, being within the range 0.01 to 0.1%, and ideally about 0.03%. The inventive alloy can readily be normalized to produce the desired two-phase microstructure, i.e. ferrite-bainite, at any temperature within the range 1550° to 1800°F. 
     It should be understood of course that normalizing is a heat treatment requiring that the steel be heated sufficiently to austenitize the entire microstructure, and then cooled in still air at ambient temperatures. It is common practice to refer to the heating temperature as the &#34;normalizing&#34; temperature. 
     As previously noted, the desired microstructure is a two-phase structure of ferrite and bainite. Although the relative amounts of each is not critical, ideally they should be present in approximately equal amounts by volume. Nevertheless, good properties can be achieved as long as there is a significant amount of each, i.e. no less than about 20 to 25% of that phase present in the smallest amount. 
     To illustrate the advantages of this invention three experimental heats were prepared, the first a conventional prior art Cr-Mo-V steel, the second a prior art Cr-Mo-V steel with aluminum and the third a Cr-Mo-V steel containing columbium according to this invention. The compositions of the three steels is shown in Table I. 
     
                                           TABLE I                                 
__________________________________________________________________________
Steel    C  Mn P    S    Si  Cr  Mo  V   Al   Cb                          
__________________________________________________________________________
Cr--Mo--V                                                                 
         0.19                                                             
            0.99                                                          
               0.021                                                      
                    0.028                                                 
                         0.23                                             
                             0.59                                         
                                 0.52                                     
                                     0.07                                 
                                         0.002                            
                                              --                          
Cr--Mo--V--Al                                                             
         0.18                                                             
            0.84                                                          
               0.020                                                      
                    0.022                                                 
                         0.31                                             
                             0.58                                         
                                 0.51                                     
                                     0.08                                 
                                         0.04 --                          
Cr--Mo--V--Cb                                                             
         0.20                                                             
            0.90                                                          
               0.017                                                      
                    0.021                                                 
                         0.25                                             
                             0.58                                         
                                 0.51                                     
                                     0.08                                 
                                         0.001                            
                                              0.03                        
__________________________________________________________________________
 
    
     All steels were identically processed except for the additions of aluminum and columbium, silicon-killed according to conventional practices, and identically processed to 1/2 -inch hot rolled plate and normalized at 1600°F. Metallographic examination showed that all steel did attain the desired microstructure. Samples of the three steels were then tested for notch toughness, stress rupture ductility and tensile properties. The results of these tests are shown in Tables II, III and IV below. 
     
                                           TABLE II                                
__________________________________________________________________________
         Test   Energy                                                    
                      Fracture                                            
                             Lateral                                      
         Temperature                                                      
                Absorption                                                
                      Appearance,                                         
                             Expansion,                                   
Steel    F      ft-lb % Shear                                             
                             mils                                         
__________________________________________________________________________
Cr--Mo--V                                                                 
         78     42    50     38                                           
Cr--Mo--V--Al                                                             
         78     14    20     11                                           
Cr--Mo--V--Cb                                                             
         78     25    35     25                                           
__________________________________________________________________________
 
    
     
                       TABLE III                                                   
______________________________________                                    
           Test     Applied  Time to                                      
                                    Elongation                            
           Temp.    Stress,  Rupture,                                     
                                    in 1 inch,                            
Steel      F        ksi      hours  %                                     
______________________________________                                    
Cr--Mo--V  950      65       352    28                                    
                    60       661    27                                    
                    55       1340   24                                    
                    50       3664   23                                    
                    40       6753   24                                    
Cr--Mo--V--Al                                                             
           950      65       583    13                                    
                    60       1603    8                                    
                    55       3642    8                                    
Cr--Mo--V--Cb                                                             
           950      70       226    27                                    
                    65       548    27                                    
                    60       934    26                                    
           1050     35       343    31                                    
           1100     20       467    42                                    
______________________________________                                    
 
    
     
                                           TABLE IV                                
__________________________________________________________________________
              Test   Yield Strength                                       
                              Tensile                                     
                                   Elongation                             
                                         Reduction                        
              Temperature,                                                
                     (0.2% Offset)                                        
                              Strength                                    
                                   in 1 inch                              
                                         of Area                          
Steel         F      ksi      ksi  %     %                                
__________________________________________________________________________
Cr--Mo--V      75    63.9     101  24.2  63.8                             
Cr--Mo--V--Cb  75    63.0     104  23.5  62.2                             
Cr--Mo--V     950    50.6     82.3 28.0  79.6                             
Cr--Mo--V--Cb 950    62.0     81.4 28.5  77.1                             
(Cr--Mo--V--Al not tested)                                                
__________________________________________________________________________
 
    
     In other tests, it was shown that the inventive steel could readily be normalized at any temperature within the range 1550° to 1800°F without significant differences in microstructure and resultant properties.