Patent Publication Number: US-7595263-B2

Title: Atomic layer deposition of barrier materials

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
   This application is a continuation of U.S. patent application Ser. No. 10/871,864 (APPM/007971), filed Jun. 18, 2004 now U.S. Pat. No. 7,211,508, which application claims benefit of U.S. Provisional Patent Application Serial Number 60/479,426 (APPM/007971), filed Jun. 18, 2003. Both of the aforementioned patent applications are incorporated herein by reference. 

   BACKGROUND OF THE INVENTION 
   1. Field of the Invention 
   Embodiments of the present invention relate to a method for manufacturing integrated circuit devices. More particularly, embodiments of the invention relate to forming metal interconnect structures using one or more cyclical deposition processes. 
   2. Description of the Related Art 
   As the structure size of integrated circuit (IC) devices is scaled down to sub-quarter micron dimensions, electrical resistance and current densities have become an area for concern and improvement. Multilevel interconnect technology provides the conductive paths throughout an IC device, and are formed in high aspect ratio features, including contacts, plugs, vias, lines, wires, and other features. A typical process for forming an interconnect on a substrate includes depositing one or more layers, etching at least one of the layer(s) to form one or more features, depositing a barrier layer in the feature(s) and depositing one or more layers to fill the feature. Typically, a feature is formed within a dielectric material disposed between a lower conductive layer and an upper conductive layer. The interconnect is formed within the feature to link the upper and lower conductive layers. Reliable formation of these interconnect features is important to the production of the circuits and continued effort to increase circuit density and quality on individual substrates and die. 
   Copper has recently become a choice metal for filling sub-micron high aspect ratio, interconnect features because copper and its alloys have lower resistivities than aluminum. However, copper diffuses more readily into surrounding materials and can alter the electronic device characteristics of the adjacent layers and, for example, form a conductive path between layers, thereby reducing the reliability of the overall circuit and may even result in device failure. 
   Barrier layers therefore, are deposited prior to copper metallization to prevent or impede the diffusion of copper atoms. Barrier layers typically contain a metal such as tungsten, titanium, tantalum, and nitrides thereof, which all have a greater resistivity than copper. To deposit a barrier layer within a feature, the barrier layer must be deposited on the bottom of the feature as well as the sidewalls thereof. Therefore, the additional amount of the barrier layer on the bottom of the feature not only increases the overall resistance of the feature, but also forms an obstruction between higher and lower metal interconnects of a multi-layered interconnect structure. 
   There is a need, therefore, for an improved method for forming metal interconnect structures which minimizes the electrical resistance of the interconnect. 
   SUMMARY OF THE INVENTION 
   A method is provided for depositing barrier layers on a substrate surface using one or more atomic layer deposition techniques. In one aspect, a method is provided for processing a substrate including exposing the substrate to a soak process comprising a tungsten-containing compound and depositing a tantalum barrier layer on the substrate by an atomic layer deposition process, comprising exposing the substrate to sequential pulses of a tantalum precursor and a reductant. 
   In another aspect, a method is provided for processing a substrate including depositing a tantalum nitride barrier layer on the substrate by an atomic layer deposition process, comprising exposing the substrate to sequential pulses of a first tantalum precursor and a nitrogen precursor, exposing the substrate to a soak process comprising a tungsten-containing compound, and depositing a tantalum barrier layer on the tantalum nitride barrier layer by a second atomic layer deposition process, comprising exposing the substrate to sequential pulses of a second tantalum precursor and a reductant. 
   In another aspect, a method is provided for processing a substrate including depositing a metal nitride layer on at least a portion of a substrate surface by alternately introducing one or more pulses of a first metal containing compound and one or more pulses of a nitrogen containing compound, exposing the metal nitride layer to a first nitrogen free reductant, exposing the metal nitride layer to a tungsten containing compound, and depositing a metal containing barrier layer on at least a portion of the metal nitride layer by alternately introducing one or more pulses of a second metal containing compound and one or more pulses of a second nitrogen free reductant. 
   In another aspect, a method is provided for processing a substrate including depositing a tantalum nitride barrier layer on a substrate surface by alternately introducing one or more pulses of a first tantalum containing compound and one or more pulses of a nitrogen containing compound into a processing chamber, depositing a tantalum containing barrier layer on at least a portion of the tantalum nitride barrier layer by alternately introducing one or more pulses of a second tantalum containing compound and one or more pulses of a reductant into a processing chamber, and exposing the tantalum containing barrier layer to a plasma treatment process. 
   In another aspect, a method is provided for processing a substrate including exposing the substrate to a first soak process, wherein the soak process includes a first reductant for a predetermined time, depositing a tantalum nitride barrier layer on the substrate by an atomic layer deposition process in a process chamber, comprising exposing the substrate to a first tantalum precursor, purging the process chamber with a purge gas, exposing the substrate with a nitrogen precursor, and purging the process chamber with the purge gas, exposing the substrate to a second soak process, and depositing a tantalum barrier layer on the tantalum nitride barrier layer. 
   In another aspect, a method is provided for processing a substrate including depositing a tantalum nitride barrier layer on the substrate by an atomic layer deposition process in a process chamber including exposing the substrate to a tantalum precursor, purging the process chamber with a purge gas, exposing the substrate to a nitrogen precursor, and purging the process chamber with the purge gas, exposing the substrate to a soak process, and depositing a tantalum barrier layer on the tantalum nitride barrier layer by a second atomic layer deposition process including exposing the substrate to a second tantalum precursor, purging with the purge gas, exposing the substrate with a nitrogen free reductant, and purging with the purge gas. 
   In another aspect, a method is provided for processing a substrate including depositing a tantalum nitride barrier layer on the substrate by an atomic layer deposition process in a process chamber including exposing the substrate to an organometallic tantalum precursor, purging the process chamber with a purge gas, exposing the substrate to a nitrogen precursor, and purging the process chamber with the purge gas, and depositing a tantalum barrier layer on the tantalum nitride barrier layer by a second atomic layer deposition process, comprising exposing the substrate to sequential pulses of a tantalum halide precursor and a reductant. 
   In another aspect, a method is provided for processing a substrate including depositing a nitride layer containing a first metal by a first atomic layer deposition process, exposing the nitride layer to a soak process comprising a second metal different than the first metal, and depositing a metal layer on the nitride layer by a second atomic layer deposition process, wherein the metal layer comprises the first metal. 

   
     BRIEF DESCRIPTION OF THE DRAWINGS 
     So that the manner in which the above recited features of the present invention are attained and can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to the embodiments thereof which are illustrated in the appended drawings. 
     It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments. 
       FIG. 1  illustrates a schematic plan view of an exemplary integrated cluster tool adaptable to perform the interconnect fabrication sequence described herein; 
       FIG. 2  illustrates a schematic, partial cross section of one embodiment of an exemplary processing chamber for performing a cyclical deposition technique described herein; 
       FIG. 3  illustrates processing sequences according to various embodiments of the invention described herein; and 
       FIGS. 4A-4D  are schematic cross section views of an exemplary wafer at different stages of an interconnect fabrication sequence according to embodiments described herein. 
   

   DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT 
   A process sequence for forming one or more interconnect structures is provided. Interconnect structures formed according to embodiments described herein have an overall lower resistivity and better electrical properties than interconnects of the prior art, and are particularly useful for making memory and logic structures for use with the fabrication of integrated circuits. The formation of the interconnect structures includes the formation of a barrier layer at least partially deposited on an underlying metal layer, a seed layer at least partially deposited on the barrier layer, and a bulk metal layer at least partially deposited on the seed layer. 
   The words and phrases used herein should be given their ordinary and customary meaning in the art by one skilled in the art unless otherwise further defined. 
   A “substrate surface” or “atomic layer deposition”, as used herein, refers to any substrate or material surface formed on a substrate upon which film processing is performed. For example, a substrate surface on which processing can be performed include materials such as silicon, silicon oxide, strained silicon, silicon on insulator (SOI), carbon doped silicon oxides, silicon nitride, doped silicon, germanium, gallium arsenide, glass, sapphire, and any other materials such as metals, metal nitrides, metal alloys, and other conductive materials, depending on the application. Barrier layers, metals or metal nitrides on a substrate surface include titanium, titanium nitride, tungsten nitride, tantalum and tantalum nitride. Substrates may have various dimensions, such as 200 mm or 300 mm diameter wafers, as well as, rectangular or square panes. Embodiments of the processes described herein deposit hafnium-containing compounds on many substrates and surfaces. Substrates on which embodiments of the invention may be useful include, but are not limited to semiconductor wafers, such as crystalline silicon (e.g., Si&lt;100&gt; or Si&lt;111&gt;), silicon oxide, strained silicon, SOI, silicon germanium, doped or undoped polysilicon, doped or undoped silicon wafers silicon nitride and patterned or non-patterned wafers. Surfaces include bare silicon wafers, films, layers and materials with dielectric, conductive and barrier properties and include aluminum oxide and polysilicon. Pretreatment of surfaces includes polishing, etching, reduction, oxidation, hydroxylation, annealing and baking. 
   The term “interconnect” as used herein refers to any conductive path formed within an integrated circuit. The term “bulk” as used herein refers to a greater amount of material deposited in relation to other materials deposited to form the interconnect structure. A “compound” is intended to include one or more precursors, reductants, reactants, and catalysts. Each compound may be a single compound or a mixture/combination of two or more compounds. 
   “Atomic layer deposition” or “cyclical deposition” as used herein refers to the sequential introduction of two or more reactive compounds to deposit a layer of material on a substrate surface. The two, three or more reactive compounds may alternatively be introduced into a reaction zone of a processing chamber. Usually, each reactive compound is separated by a time delay to allow each compound to adhere and/or react on the substrate surface. In one aspect, a first precursor or compound A is pulsed into the reaction zone followed by a first time delay. Next, a second precursor or compound B is pulsed into the reaction zone followed by a second delay. During each time delay a purge gas, such as nitrogen, is introduced into the processing chamber to purge the reaction zone or otherwise remove any residual reactive compound or by-products from the reaction zone. Alternatively, the purge gas may flow continuously throughout the deposition process so that only the purge gas flows during the time delay between pulses of reactive compounds. The reactive compounds are alternatively pulsed until a desired film or film thickness is formed on the substrate surface. In either scenario, the ALD process of pulsing compound A, purge gas, pulsing compound B and purge gas is a cycle. A cycle can start with either compound A or compound B and continue the respective order of the cycle until achieving a film with the desired thickness. 
   The term “inert gas” and “non-reactive gas” as used herein refers to a single gas or a mixture of gases that does not participate in the metal layer formation. Exemplary non-reactive gases include argon, helium, nitrogen, and combinations thereof. 
   A “pulse”, “dose”, or “pulse/dose” as used herein is intended to refer to a quantity of a particular compound that is intermittently or non-continuously introduced into a reaction zone of a processing chamber. The quantity of a particular compound within each pulse may vary over time, depending on the duration of the pulse. The duration of each pulse is variable depending upon a number of factors such as, for example, the volume capacity of the process chamber employed, the vacuum system coupled thereto, and the volatility/reactivity of the particular compound itself. A “half-reaction” as used herein is intended to refer to a pulse of precursor step followed by a purge step. A pulse generally has a duration of less than about 1 second. 
   A “cycle” as used herein is intended to refer to two or more pulses of different particular compounds that are sequentially introduced into a reaction zone. The quantity of a particular compound within each pulse may vary over time, depending on the duration of the pulse. Cycles are typically repeated for a deposition process. 
   A “soak” or “soak process” as used herein is intended to refer to a quantity of a particular compound that is introduced into a reaction zone of a processing chamber to activate a surface of a substrate. The activation of the surface may comprise hydrating a surface, catalyzing a surface, or forming halide terminated surfaces. A particular soak process may include a single compound or a mixture/combination of two or more compounds. A soak only comprises one cycle if two or more compounds are used. Soak processes generally have durations of about 1 second or more. 
   A “reaction zone” is intended to include any volume that is in fluid communication with a substrate surface being processed. The reaction zone may include any volume within a processing chamber that is between a gas source and the substrate surface. For example, the reaction zone includes any volume downstream of a dosing valve in which a substrate is disposed. 
   Deposition Apparatus 
     FIG. 1  is a schematic top-view diagram of an exemplary multi-chamber processing system  100  that may be adapted to perform processes as disclosed herein. Such a processing system  100  may be an ENDURA® system, commercially available from Applied Materials, Inc., of Santa Clara, Calif. A similar multi-chamber processing system is disclosed in U.S. Pat. No. 5,186,718, entitled “Stage Vacuum Wafer Processing System and Method,” issued on Feb. 16, 1993, which is incorporated by reference herein. 
   The system  100  generally includes load lock chambers  102 ,  104  for the transfer of substrates into and out from the system  100 . Typically, since the system  100  is under vacuum, the load lock chambers  102 ,  104  may “pump down” the substrates introduced into the system  100 . A first robot  410  may transfer the substrates between the load lock chambers  102 ,  104 , and a first set of one or more substrate processing chambers  112 ,  114 ,  116 ,  118  (four are shown). Each processing chamber  112 ,  114 ,  116 ,  118 , can be outfitted to perform a number of substrate processing operations such as cyclical layer deposition, chemical vapor deposition (CVD), physical vapor deposition (PVD), etch, pre-clean, degas, orientation and other substrate processes. The first robot  110  also transfers substrates to/from one or more transfer chambers  122 ,  124 . 
   The transfer chambers  122 ,  124 , are used to maintain ultrahigh vacuum conditions while allowing substrates to be transferred within the system  100 . A second robot  130  may transfer the substrates between the transfer chambers  122 ,  124  and a second set of one or more processing chambers  132 ,  134 ,  136 , and  138 . Similar to processing chambers  112 ,  114 ,  116 ,  118 , the processing chambers  132 ,  134 ,  136 ,  138  can be outfitted to perform a variety of substrate processing operations, such as cyclical layer deposition, chemical vapor deposition (CVD), physical vapor deposition (PVD), etch, pre-clean, degas, and orientation, for example. Any of the substrate processing chambers  112 ,  114 ,  116 ,  118 ,  132 ,  134 ,  136 ,  138  may be removed from the system  100  if not necessary for a particular process to be performed by the system  100 . 
   In one arrangement, each processing chamber  132  and  138  may be a physical vapor deposition chamber, a chemical vapor deposition chamber, or a cyclical deposition chamber adapted to deposit a seed layer. Each processing chamber  134  and  136  may be a cyclical deposition chamber, a chemical vapor deposition chamber, or a physical vapor deposition chamber adapted to deposit a barrier layer. Each processing chamber  112  and  114  may be a physical vapor deposition chamber, a chemical vapor deposition chamber, or a cyclical deposition chamber adapted to deposit a dielectric layer. Each processing chamber  116  and  118  may be an etch chamber outfitted to etch apertures or openings for interconnect features. This one particular arrangement of the system  100  is provided to illustrate the invention and should not be used to limit the scope of the invention. 
   To facilitate the control and automation of the overall system, the integrated processing system may include a controller  140  comprising a central processing unit (CPU), memory, and support circuits. The CPU may be one of any form of computer processors that are used in industrial settings for controlling various drives and pressures. The memory is connected to the CPU, and may be one or more of a readily available memory such as random access memory (RAM), read only memory (ROM), floppy disk, hard disk, or any other form of digital storage, local or remote. Software instructions and data can be coded and stored within the memory for instructing the CPU. The support circuits are also connected to the CPU for supporting the processor in a conventional manner. The support circuits may include cache, power supplies, clock circuits, input/output circuitry, subsystems, and the like. 
     FIG. 2  illustrates a schematic, partial cross section of an exemplary processing chamber  200  for forming a barrier layer according to embodiments of the present invention. Such a processing chamber  200  is available from Applied Materials, Inc. located in Santa Clara, Calif., and a brief description thereof follows. A more detailed description may be found in commonly assigned U.S. patent application Ser. No. 10/032,284, entitled “Gas Delivery Apparatus and Method For Atomic Layer Deposition”, filed on Dec. 21, 2001, issued as U.S. Pat. No. 6,916,398, which is incorporated herein by reference to the extent not inconsistent with the claimed aspects and disclosure herein. 
   The processing chamber  200  may be integrated into an integrated processing platform, such as an ENDURA® platform also available from Applied Materials, Inc. Details of the ENDURA® platform are described in commonly assigned U.S. patent application Ser. No. 09/451,628, entitled “Integrated Modular Processing Platform”, filed on Nov. 30, 1999, which is incorporated herein by reference to the extent not inconsistent with the claimed aspects and disclosure herein. 
   Referring to  FIG. 2 , the chamber  200  includes a chamber body  202  having a slit valve  208  formed in a sidewall  204  thereof and a substrate support  212  disposed therein. The substrate support  212  is mounted to a lift motor  214  to raise and lower the substrate support  212  and a substrate  210  disposed thereon. The substrate support  212  may also include a vacuum chuck, an electrostatic chuck, or a clamp ring for securing the substrate  212  to the substrate support  212  during processing. Further, the substrate support  212  may be heated using an embedded heating element, such as a resistive heater, or may be heated using radiant heat, such as heating lamps disposed above the substrate support  212 . A purge ring  222  may be disposed on the substrate support  212  to define a purge channel  224  that provides a purge gas to prevent deposition on a peripheral portion of the substrate  210 . 
   A gas delivery apparatus  230  is disposed at an upper portion of the chamber body  202  to provide a gas, such as a process gas and/or a purge gas, to the chamber  200 . A vacuum system  278  is in communication with a pumping channel  279  to evacuate gases from the chamber  200  and to help maintain a desired pressure or a desired pressure range inside a pumping zone  266  of the chamber  200 . 
   The gas delivery apparatus  230  includes a chamber lid  232  having an expanding channel  234  formed within a central portion thereof. The chamber lid  232  also includes a bottom surface  260  extending from the expanding channel  234  to a peripheral portion of the chamber lid  232 . The bottom surface  260  is sized and shaped to substantially cover the substrate  210  disposed on the substrate support  212 . The expanding channel  234  has an inner diameter that gradually increases from an upper portion  237  to a lower portion  235  adjacent the bottom surface  260  of the chamber lid  232 . The velocity of a gas flowing therethrough decreases as the gas flows through the expanding channel  234  due to the expansion of the gas. The decreased gas velocity reduces the likelihood of blowing off reactants adsorbed on the surface of the substrate  210 . 
   The gas delivery apparatus  230  also includes at least two high speed actuating valves  242  having one or more ports. At least one valve  242  is dedicated to each reactive compound. For example, a first valve is dedicated to a metal containing compound, such as tantalum and titanium, and a second valve is dedicated to a nitrogen containing compound. When a ternary material is desired, a third valve is dedicated to an additional compound. For example, if a silicide is desired, the additional compound may be a silicon containing compound. 
   The valves  242  may be any valve capable of precisely and repeatedly delivering short pulses of compounds into the chamber body  202 . In some cases, the on/off cycles or pulses of the valves  242  may be as fast as about 100 msec or less. The valves  242  can be directly controlled by a system computer, such as a mainframe for example, or controlled by a chamber/application specific controller, such as a programmable logic computer (PLC) which is described in more detail in the assigned U.S. Pat. No. 6,734,020, entitled “Valve Control System For ALD Chamber”, issued on May 11, 2004, which is incorporated herein by reference to the extent not inconsistent with the claimed aspects and disclosure herein. For example, the valves  242  may be electronically controlled (EC) valves, which are commercially available from Fujikin of Japan as part number FR-21-6.35 UGF-APD. 
   Returning to  FIG. 1 , a control unit  280 , such as a programmed personal computer, work station computer, or the like, may be coupled to the chamber  200  to control processing conditions. For example, the control unit  280  may be configured to control flow of various process gases and purge gases from gas sources  238 ,  239 ,  240  through the valves  242 A,  242 B during different stages of a substrate process sequence. The control unit  280  may be one of any form of general purpose computer processor that can be used in an industrial setting for controlling various chambers and sub-processors. 
   Illustratively, the control unit  280  comprises a central processing unit (CPU), support circuitry, and memory containing associated control software. The CPU may use any suitable memory, such as random access memory, read only memory, floppy disk drive, hard disk, or any other form of digital storage, local or remote. Various support circuits may be coupled to the CPU for supporting the chamber  200 . The control unit  280  may be coupled to another controller that is located adjacent individual chamber components, such as the programmable logic controllers of the valves  242 A,  242 B. Bi-directional communications between the control unit  280  and various other components of the chamber  200  are handled through numerous signal cables collectively referred to as signal buses. In addition to control of process gases and purge gases from gas sources  238 ,  239 ,  240  and from the programmable logic controllers of the valves  242 A,  242 B, the control unit  280  may be configured to be responsible for automated control of other activities used in wafer processing, such as wafer transport, temperature control, chamber evacuation, among other activities, some of which are described elsewhere herein. 
   Barrier Deposition Process 
   FIGS.  3  and  4 A- 4 D illustrate one embodiment of a process sequence  300  according to embodiments of the invention. A substrate  410  is provided with a patterned dielectric layer  412  disposed thereon at step  310  as shown in  FIG. 4A . A feature definition  414  is formed in the patterned dielectric material  412 . The feature definition  414  has sidewall  416  and a bottom  418 . The substrate  410  may have features  407  formed therein, for example, underlying metal gates or metal interconnects. An optional pre-treatment process, such as forming an initiation layer or a surface treatment process, such as a “soak” process, may be performed at step  315  prior to deposition. 
   A metal nitride barrier layer  430  is first deposited at least partially within the feature definition  414  and on the substrate surface, as shown at step  320  and  FIG. 4B . The metal nitride barrier layer  430  is deposited as atomic layers according to a cyclical layer deposition technique described herein. In one aspect, the barrier layer is a metal nitride material, such as tantalum nitride (TaN). Examples of other suitable metal nitride material include tantalum silicon nitride, titanium nitride, titanium silicon nitride, tungsten nitride, tungsten silicon nitride, niobium nitride, molybdenum nitride, alloys thereof, and combinations thereof, among others. A soak process may also be performed during an intermediate portion of the deposition process of the metal nitride barrier layer  430 . 
   Optionally, the metal nitride barrier layer  430  may then be treated with a post-treatment process, such as a reducing gas plasma (or reductant as described herein) to remove impurities and contaminants. An optional pre-treatment process or a surface treatment process, such as a “soak” process, may be performed at step  325  prior to deposition of the metal barrier layer  440 . 
   A metal barrier layer  440  may then be deposited on the metal nitride barrier layer  430 , as shown at step  330  and  FIG. 4C . The metal barrier layer  440  is deposited according to a cyclical layer deposition technique described herein. In one aspect, the metal barrier layer  440  is a metal containing layer, for example, tantalum, tantalum silicide, tantalum boride, titanium, titanium silicide, titanium boride, tungsten, tungsten silicide, tungsten boride, niobium, niobium silicide, niobium boride, molybdenum, molybdenum silicide, molybdenum boride, ruthenium, ruthenium boride, ruthenium silicide alloys thereof, and combinations thereof. A soak process may also be performed during an intermediate portion of the deposition process of the metal barrier layer  440 . 
   The metal barrier layer  440  may then be treated with a post-treatment process, such as a reducing gas plasma, to remove impurities and contaminants at step  340 . The layer  430  and  440  may also be used as a wetting layer, adhesion layer, or glue layer for subsequent metallization. An optional pre-treatment process, such as forming an initiation layer during a “soak” process, may be performed before or during an intermediate portion of the metal barrier layer  440  deposition process. The metal nitride barrier layer  430  and metal barrier layer  440  may be deposited in the same chamber, in separate chambers, transfer chamber, or system without breaking vacuum. 
   Alternatively, a barrier enhancement layer may be deposited on the metal nitride barrier layer  430  or metal barrier layer  440 . 
   A seed layer  450  is at least partially deposited on the barrier layers  430 ,  440 , at step  350  as shown in  FIG. 4D . The seed layer  450  may be deposited using any conventional deposition technique, such as chemical vapor deposition (CVD), physical vapor deposition (PVD), atomic layer deposition (ALD), electroplating, or electroless plating. Preferably, the seed layer  450  is deposited conformally on the underlying barrier layers  430 ,  440 . The seed layer  450  may be a conventional copper seed layer or dual alloy seed layer. Exemplary dual alloy seed layers include: 1) undoped copper deposited utilizing a target containing undoped copper, 2) a copper alloy containing aluminum in a concentration of about 2.0 atomic percent deposited utilizing a copper-aluminum target comprising aluminum in a concentration of about 2.0 atomic percent, 3) a copper alloy containing tin in a concentration of about 2.0 atomic percent deposited utilizing a copper-tin target comprising tin in a concentration of about 2.0 atomic percent, and 4) a copper alloy containing zirconium in a concentration of about 2.0 atomic percent deposited utilizing a copper-zirconium target comprising zirconium in a concentration of about 2.0 atomic percent. 
   The bulk metal layer  460  is at least partially deposited on the seed layer  450 , at step  360  as shown in  FIG. 4D . The metal layer may also be deposited using any conventional deposition technique, such as chemical vapor deposition (CVD), physical vapor deposition (PVD), atomic layer deposition (ALD), electroplating, or electroless plating. The metal layer preferably includes any conductive material such as aluminum, copper, tungsten, alloys thereof, or combinations thereof, for example. 
   Referring to  FIG. 4A , the dielectric layer  412  may be any dielectric material including a low k dielectric material (k≦4.0), whether presently known or yet to be discovered. For example, the dielectric layer  412  may be a silicon oxide or a carbon doped silicon oxide, for example. The dielectric layer  412  has been etched to form a feature definition  414  therein using conventional and well-known techniques. The feature definition  414  may be a plug, via, contact, line, wire, or any other interconnect component. Typically, the feature definition  414  has vertical sidewalls  416  and a floor  418 , having an aspect ratio of about 4:1 or greater, such as about 6:1. The floor  418  exposes at least a portion of the lower level metal interconnect  410 . 
   Pre-Deposition Techniques 
   Prior to depositing the metal nitride barrier layer  430  or the metal layer  440 , the patterned or etched substrate dielectric layer  412  may be cleaned to remove native oxides or other contaminants from the surface thereof. For example, reactive gases are excited into a plasma within a remote plasma source chamber such as a Reactive Pre-clean chamber available from Applied Materials, Inc., located in Santa Clara, Calif. Pre-cleaning may also be done within a metal CVD or PVD chamber by connecting the remote plasma source thereto. Alternatively, metal deposition chambers having gas delivery systems could be modified to deliver the pre-cleaning gas plasma through existing gas inlets such as a gas distribution showerhead positioned above the substrate. 
   In one aspect, the reactive pre-clean process forms radicals from a plasma of one or more inert gases such as argon, nitrogen, and helium and/or one or more reactive gases including hydrogen, oxygen, and fluorine containing compounds, and combinations thereof. For example, a processing gas may include a mixture of tetrafluorocarbon (CF 4 ) and oxygen (O 2 ), or a mixture of helium (He) and nitrogen trifluoride (NF 3 ). More preferably, the reactive gas is a mixture of helium and nitrogen trifluoride. 
   In one example of a pre-clean process, a substrate is first exposed to a plasma of an inert gas, such as argon, and then chamber pressure is provided to about 140 milliTorr, and a processing gas consisting essentially of hydrogen and helium is introduced into the processing region. Preferably, the processing gas comprises about 5% hydrogen and about 95% helium. The hydrogen plasma is generated by applying between about 50 watts and about 1,000 watts power. The hydrogen plasma is maintained for about 10 seconds to about 300 seconds. 
   Prior to deposition of the barrier layers  430  or  440 , the substrate surface may be exposed to surface treatment process, a “soak” process, to enhance deposition of subsequent materials, such as to improve metal and/or metal nitride deposition. The substrate surface may include a dielectric material, a conductive material, such as a metal, or a combination of both materials. 
   A soak process may be performed by exposing the substrate surface to a processing gas. A soak process may be applied by exposing the substrate surface to a reductant, as described herein, without pulsing. Soak processes differ from atomic layer deposition process by usually occurring for only one cycle for two component soak processes and occur for a duration of 1 or more seconds, such as between about 5 seconds and about 330 seconds, for example 60 seconds. A plasma may also be used in combination with the soak process. Suitable reductants include hydrogen, borane and borane derivatives such as diborane (B 2 H 6 ), triborane, tetraborane, pentaborane, hexaborane, heptaborane, octaborane, nanoborane, decaborane, alkylboranes (e.g., Et 3 B), and combinations thereof, silane and silane derivatives such as tetrachlorosilane (SiCl 4 ), disilane (Si 2 H 6 ), hexachlorodisilane (Si 2 Cl 6 ) or dichlorosilane (SiCl 2 H 2 ), a gas having one or more amine groups disposed thereon, such as ammonia or hydrazine (N 2 H 4 ), and combinations thereof. 
   For example, for a metal nitride deposition process, which may also be used for metal deposition process, a soak of the substrate surface may be performed by exposing the substrate surface to a processing gas capable of forming amine groups on the substrate surface. Example processing gas may include ammonia, a gas mixture comprising nitrogen and hydrogen, ammonia, hydrazine, methylhydrazine, dimethylhydrazine, t-butylhydrazine, phenylhydrazine, azoisobutane, ethylazide, derivatives thereof, and combinations thereof. 
   A soak process may also include a metal precursor soak used independently or in conjunction with a reductant described herein. For example, a soak process with a metal precursor may be used to halogenate a substrate surface for metal deposition. Halogenation of a substrate surface by a soak process may be achieved by metal halide soaks including halides of tantalum, titanium, tungsten, hafnium, zirconium, molybdenum, niobium, vanadium, ruthenium, and aluminum, as well as non-metal halide compounds, such as silicon, germanium and carbon. Examples of metal halide compounds include TaF 5 , TaCl 5 , WF 6 , TiCl 4 , HfCl 4 , ZrCl 4 , AlCl 3  and MoCl 6 . 
   It is believed the soak process may activate a substrate surface by hydrating or halogenating the substrate surface, and may even form a layer of deposited material, known as an initiation layer or soak layer. The soak process is selective by desired termination of the underlayer and dependant to what chemical reagent will start the ALD cycle. The compounds used in the soak process allow the formation of a surface of deposition with desired chemical structure. For example, if the ALD cycle starts with a reductant (e.g., B 2 H 6  or SiH 4 ), then a halogenated terminus underlayer is desired, so a metal halide compound is used in the soak process. However, if the ALD cycle starts with a metal precursor (e.g., TaF 5 ), then a hydrogenated terminus underlayer is desired, so a reductant is used in the soak process. 
   For example, the use of a silane or borane compound with produce a hydrogen terminated surface to facilitate subsequent material deposition, an ammonia compound with produce an amine terminated surface facilitate subsequent material deposition, and the use of precursors including halide compounds, such as TaF 5  or WF 6 , can produce a fluorine terminated surface facilitate subsequent material deposition. The soak process is believed to facilitate the growth process of a subsequent atomic layer deposition process or chemical vapor deposition process. 
   An example of a soak process includes exposing a substrate surface to ammonia between about 1 second and about 120 seconds, for example 60 seconds, without pulsing, such as between about 5 seconds and about 60 seconds, for example, between about 10 seconds and about 30 seconds. 
   The soak process may include two or more steps using two or more reductants. Additionally, the soak process may also include metal containing compounds, such as precursor used to deposit the metal or metal nitride materials described herein. In one embodiment of a two-step soak process, a reductant soak is followed by a precursor soak. For example, a metal containing compound (precursor) soak, such as TaF 5  or WF 6 , may be performed after the reductant soak described herein prior to depositing the metal nitride layer  430  or metal layer  440  as described herein. In another embodiment, the reductant soak may be performed after the metal containing compound soak, for example, a soak of WF 6  followed by a soak of diborane or silane. Each soak step of a two-step soak process may be performed between about 5 seconds and about 330 seconds as described herein. 
   Examples of two step soak processes may also include a reductant soak followed by a metal precursor soak, for example, a soak process may include a 5 second B 2 H 6  soak followed by a 300 second TaF 5  soak; another soak process may include a 10 second B 2 H 6  followed by a 300 second TaF 5  soak; another soak process may include a 20 second B 2 H 6  followed by a 300 second TaF 5  soak; another soak process may include a 20 second B 2 H 6  followed by a 30 second TaF 5  soak; another soak process may include a 20 second B 2 H 6  followed by a 100 second TaF 5  soak; and another soak process may include a 20 second B 2 H 6  followed by a 200 second TaF 5  soak. In another example of a two step soak process, a soak process may include a 5 second SiH 4  soak followed by a 300 second TaF 5  soak; another soak process may include a 10 second SiH 4  followed by a 300 second TaF 5  soak; another soak process may include a 20 second SiH 4  followed by a 300 second TaF 5  soak; another soak process may include a 20 second SiH 4  followed by a 30 second TaF 5  soak; another soak process may include a 20 second SiH 4  followed by a 100 second TaF 5  soak; and another soak process may include and 20 second B 2 H 6  followed by a 200 second TaF 5  soak. 
   Other examples of soak processes include a 5 second B 2 H 6  soak followed by a 300 second WF 6  soak; another soak process may include a 10 second B 2 H 6  followed by a 300 second WF 6  soak; another soak process may include a 20 second B 2 H 6  followed by a 300 second WF 6  soak; another soak process may include a 20 second B 2 H 6  followed by a 30 second WF 6  soak; another soak process may include a 20 second B 2 H 6  followed by a 100 second WF 6  soak; and another soak process may include a 20 second B 2 H 6  followed by a 200 second WF 6  soak. In another example of a two step soak process, a soak process may include a 5 second SiH 4  soak followed by a 300 second WF 6  soak; another soak process may include a 10 second SiH 4  followed by a 300 second WF 6  soak; another soak process may include a 20 second SiH 4  followed by a 300 second WF 6  soak; another soak process may include a 20 second SiH 4  followed by a 30 second WF 6  soak; another soak process may include a 20 second SiH 4  followed by a 100 second WF 6  soak; and another soak process may include and 20 second B 2 H 6  followed by a 200 second WF 6  soak. 
   In one example a metal deposition process comprises a diborane soak, a TaF 5  soak, and the 40 cycles of SiH 4 /TaF 5 . In another example a metal deposition process comprises a diborane soak, a WF 6  soak, and the 40 cycles of Si 2 H 6 /TaF 5 . A soak layer may also be used between a plurality of metal nitride  430  and metal layer  440  cycles to improve layer formation or when deposition compounds are changed. For example, a metal layer  440  as described herein may be deposited by 20 cycles of diborane/TaF 5 , a SiH 4  soak for 60 seconds, and then 40 to 200 cycles of SiH 4 /TaF 5 . 
   A purge gas pulse may be used after each soak precursor introduced into the process chamber prior to introduction of a second soak precursor or a first precursor for an atomic layer deposition process. Additionally, each soak precursor may be introduced into the process chamber with a carrier gas. Suitable purge gases and/or carrier gases include helium, argon, hydrogen, nitrogen, forming gas, or combinations thereof. 
   Soak processes may be performed under the following conditions including supplying a metal tantalum precursor at a rate between about 1 sccm and about 1,000 sccm, such as between about 25 sccm and about 500 sccm, and/or supplying the reductant at a rate between about 1 sccm and about 1,000 sccm, such as between about 25 sccm and about 500 sccm, supplying a carrier gas at a flow rate between about 100 sccm and about 1,000 sccm, such as between about 100 sccm and about 700 sccm, maintaining the chamber pressure less than about 120 Torr, such as between about 1 Torr and about 50 Torr, for example, between about 1 Torr and about 5 Torr, and maintaining the heater temperature between about 100° C. and about 600° C., such as between 175° C. and about 350° C., for example 300° C. 
   It is believed that the exposure of the substrate surface to the soak processing gases provides a better surface for chemisorbtion of metal precursors, including faster cycle times. The use of soak processing gases, such as ammonia with its respective amines, catalyze the reduction reaction of metal from metal containing precursors, such as TaF 5 . The addition of a soak layer has been observed to decrease resistivity and improve uniformity in subsequent deposition layers at increasing exposure times to reductants. 
   Metal Nitride Barrier Layer 
   Referring to  FIG. 4B , the metal nitride barrier layer  430  is conformally deposited on the floor  418  as well as the side walls  416  of the feature definition  414 . The metal nitride barrier layer  430  is formed by providing one or more pulses of a metal containing compound and one or more pulses of a nitrogen containing compound. 
   In one example, the barrier layer comprises tantalum nitride and is formed by providing one or more pulses of a tantalum metal containing compound at a flow rate between about 100 sccm and about 1,000 sccm for a time period of less than about 1 second and one or more pulses of a nitrogen containing compound at a flow rate between about 100 sccm and about 1,000 sccm for a time period of less than about 1 second to a reaction zone having a substrate disposed therein. The metal nitride barrier layer  430  process is performed under conditions suitable for reacting the compounds to produce a TaN layer in the feature definitions. The metal nitride barrier layer  430  process may be a plasma enhanced process. 
   Exemplary tantalum metal containing compounds include organometallic tantalum containing compounds, for example, t-butylimino-tris(diethylamino)tantalum (TBTDET), pentakis(ethylmethylamino)tantalum (PEMAT), pentakis(dimethylamino)tantalum (PDMAT), pentakis(diethylamino)tantalum (PDEAT), t-butylimino-tris(ethylmethylamino)tantalum (TBTMET), t-butylimino-tris(dimethylamino)tantalum (TBTDMT), bis(cyclopentadienyl)tantalum trihydride ((Cp) 2 TaH 3 ), bis(methylcyclopentadienyl)tantalum trihydride ((CpMe) 2 TaH 3 ), tantalum hydride (Cp) 2 TaH 3 , tantalum pentafluoride (TaF 5 ), tantalum pentachloride (TaCl 5 ), tantalum pentabromide (TaBr 5 ), tantalum pentaiodide (Tal 5 ), and combinations thereof. 
   Exemplary nitrogen containing compounds include activated-dinitrogen, ammonia, hydrazine, methylhydrazine, dimethylhydrazine, t-butylhydrazine, phenylhydrazine, azoisobutane, ethylazide, tert-butylamine, allylamine, derivatives thereof, and combinations thereof. Also, nitrogen containing compounds may be activated with a plasma, for example, a remote plasma nitridation (RPN) process. 
   It is to be understood that these compounds or any other compound not listed above may be a solid, liquid, or gas at room temperature. For example, PDMAT is a solid at room temperature and TBTDET is a liquid at room temperature. Accordingly, the non-gas phase precursors are subjected to a sublimation or vaporization step, which are both well known in the art, prior to introduction into the processing chamber. A carrier gas, such as argon, helium, nitrogen, hydrogen, or a mixture thereof, may also be used to help deliver the compound into the processing chamber. 
   Each pulse is performed sequentially, and is accompanied by a separate flow of purge gas at a rate between about 200 sccm and about 1,000 sccm. The separate flow of purge gas (purge or purge pulse) may be pulsed between each pulse of the reactive compounds or the separate flow of purge gas may be introduced continuously throughout the deposition process. The separate flow of purge gas, whether pulsed or continuous, serves to remove any excess reactants from the reaction zone to prevent unwanted gas phase reactions of the reactive compounds, and also serves to remove any reaction by-products from the processing chamber. In addition to these services, the continuous separate flow of purge gas helps deliver the pulses of reactive compounds to the substrate surface similar to a carrier gas. 
   The durations for each pulse/dose are variable and may be adjusted to accommodate, for example, the volume capacity of the processing chamber as well as the capabilities of a vacuum system coupled thereto. Additionally, the dose time of a compound may vary according to the flow rate of the compound, the pressure of the compound, the temperature of the compound, the type of dosing valve, the type of control system employed, as well as the ability of the compound to adsorb onto the substrate surface. Dose times may also vary based upon the type of layer being formed and the geometry of the device being formed. 
   Typically, the duration for each pulse/dose or “dose time” is typically less than about 1 second. In general, a dose time should be long enough to provide a volume of compound sufficient to adsorb/chemisorb onto the surface of the substrate and form a layer of the compound thereon. 
   In a particular embodiment, a TaN barrier layer is formed by cyclically introducing PDMAT and ammonia to the substrate surface. To initiate the cyclical deposition of the TaN layer, a carrier gas such as argon is introduced into the processing chamber  200  to stabilize the pressure and temperature therein. The carrier gas is allowed to flow continuously during the deposition process such that only the argon flows between pulses of each compound. A first pulse of PDMAT is provided from the gas source  238  at a flow rate between about 100 sccm and about 400 sccm, with a pulse time of about 0.6 seconds or less after the chamber temperature and pressure have been stabilized at about 200° C. to about 300° C. and about 1 Torr to about 5 Torr. A pulse of ammonia is then provided from the gas source  239  at a flow rate between about 200 sccm and about 600 sccm, with a pulse time of about 0.6 seconds or less. 
   A pause between pulses of PDMAT and ammonia is about 1.0 second or less, preferably about 0.5 seconds or less, more preferably about 0.1 seconds or less. In various aspects, a reduction in time between pulses at least provides higher throughput. As a result, a pause after the pulse of ammonia is also about 1.0 second or less, about 0.5 seconds or less, or about 0.1 seconds or less. Argon gas flowing between about 100 sccm and about 1,000 sccm, such as between about 100 sccm and about 400 sccm, is continuously provided from the gas source  240  through each valve  242 . In one aspect, a pulse of PDMAT may still be in the chamber when a pulse of ammonia enters. In general, the duration of the carrier gas and/or pump evacuation should be long enough to prevent the pulses of PDMAT and ammonia from mixing together in the reaction zone. 
   The heater temperature is maintained between about 100° C. and about 300° C. at a chamber pressure between about 1.0 and about 5.0 Torr. Each cycle consisting of a pulse of PDMAT, pause, pulse of ammonia, and pause provides a tantalum nitride layer having a thickness between about 0.3 Å and about 1.0 Å per cycle. The alternating sequence may be repeated until the desired thickness is achieved, which may be less than about 20 Å, such as about 10 Å. Accordingly, the deposition method may require between 10 and 70 cycles, and has been observed to be more typically between 20 and 30 cycles for a desired thickness less than about 20 Å, such as about 10 Å. 
   Tantalum nitride layer deposited by the process may have a layer composition of tantalum to nitrogen ratio from about 1:1.92 to about 1:1 to about 3:1. 
   The tantalum nitride deposition process may be performed under the following deposition conditions including supplying the tantalum precursor at a rate between about 1 sccm and about 100 sccm, such as between about 5 sccm and about 50 sccm, supplying the nitrogen containing reductant at a rate between about 1 sccm and about 100 sccm, such as between about 5 sccm and about 50 sccm, supplying a carrier gas at a flow rate between about 100 sccm and about 1,000 sccm, such as between about 100 sccm and about 700 sccm, maintaining the chamber pressure less than about 120 Torr, such as between about 1 Torr and about 50 Torr, for example, between about 1 Torr and about 5 Torr, and maintaining the deposition temperature between about 100° C. and about 400° C., such as between 175° C. and about 350° C., for example 300° C. ALD deposition of metal and metal nitride layer are more further described in U.S. patent application Ser. No. 10/281,079, filed on Oct. 25, 2002, published as U.S. Patent Publication No. 2003/0121608, which is incorporated by reference to the extent not inconsistent with the claim aspects and disclosure herein. 
   Metal Barrier Layer 
   Referring to  FIG. 4C , the metal barrier layer  440  is conformally deposited on the floor  418  as well as the side walls  416  of the feature definition  414  or on the metal nitride barrier layer  430  described herein. The metal nitride barrier layer  430  is formed by providing one or more pulses of a metal containing compound and one or more pulses of a reductant. Each pulse is adjusted to provide a desirable composition, thickness, density, and step coverage of the metal barrier layer  440 . The metal barrier layer  440  broadly includes metals, such as tantalum (Ta) and derivative metals besides tantalum nitride, such as tantalum silicide (TaSi), tantalum boride (TaB), tantalum boronitride (TaBN), and tantalum silicon nitride (TaSiN). The metal barrier layer  440  process may be a plasma enhanced process. 
   In one example, the barrier layer comprises tantalum and is formed by providing one or more pulses of a tantalum containing compound at a flow rate between about 100 sccm and about 1,000 sccm for a time period of less than about 5 seconds and one or more pulses of a reductant at a flow rate between about 100 sccm and about 1,000 sccm for a time period of less than about 5 seconds to a reaction zone having a substrate disposed therein. The metal barrier layer  440  process is performed under conditions suitable for reacting the compounds to produce a Ta layer, or Ta derivative layer, in the feature definitions. 
   Exemplary tantalum metal containing compounds include organometallic tantalum containing compounds, for example, t-butylimino-tris(diethylamino)tantalum (TBTDET), pentakis(ethylmethylamino)tantalum (PEMAT), pentakis(dimethylamino)tantalum (PDMAT), pentakis(diethylamino)tantalum (PDEAT), t-butylimino-tris(ethylmethylamino)tantalum (TBTMET), t-butylimino-tris(dimethylamino)tantalum (TBTDMT), bis(cyclopentadienyl)tantalum trihydride ((Cp) 2 TaH 3 ), bis(methylcyclopentadienyl)tantalum trihydride ((CpMe) 2 TaH 3 ), derivatives thereof; and combinations thereof. Preferred metal containing compounds also include inorganometallic tantalum containing compounds, for example, tantalum pentafluoride (TaF 5 ), tantalum pentachloride (TaCl 5 ), tantalum pentabromide (TaBr 5 ), tantalum pentaiodide (Tal 5 ), and combinations thereof. The metal containing precursor for the metal barrier layer  440  may be the same precursor for the metal nitride barrier layer  430 . 
   Exemplary reductants include nitrogen free reductants including hydrogen, borane and borane derivatives such as diborane (B 2 H 6 ), triborane, tetraborane, pentaborane, hexaborane, heptaborane, octaborane, nanoborane, decaborane, alkylboranes (e.g., Et 3 B), and combinations thereof, silane and silane derivatives such as tetrachlorosilane (SiCl 4 ), disilane (Si 2 H 6 ), hexachlorodisilane (Si 2 Cl 6 ) or dichlorosilane (SiCl 2 H 2 ). Alternatively, the reductants may also include nitrogen containing compounds selected from the group of ammonia, hydrazine, methylhydrazine, dimethylhydrazine, t-butylhydrazine, phenylhydrazine, azoisobutane, ethylazide, derivatives thereof, and combinations thereof. A carrier gas, such as argon, helium, nitrogen, hydrogen, or a mixture thereof, may also be used to help deliver the compound into the processing chamber. 
   Each pulse is performed sequentially, and is accompanied by a separate flow of purge gas at a rate between about 200 sccm and about 1,000 sccm. The separate flow of purge gas may be pulsed between each pulse of the reactive compounds or the separate flow of purge gas may be introduced continuously throughout the deposition process. 
   The durations for each pulse/dose are variable and may be adjusted to accommodate, for example, the volume capacity of the processing chamber as well as the capabilities of a vacuum system coupled thereto. Additionally, the dose time of a compound may vary according to the flow rate of the compound, the pressure of the compound, the temperature of the compound, the type of dosing valve, the type of control system employed, as well as the ability of the compound to adsorb onto the substrate surface. Dose times may also vary based upon the type of layer being formed and the geometry of the device being formed. 
   Typically, the duration for each pulse/dose or “dose time” is typically less than about 1 second. However, a dose time can range from microseconds to milliseconds to seconds, and even to minutes. In general, a dose time should be long enough to provide a volume of compound sufficient to adsorb/chemisorb onto the entire surface of the substrate and form a layer of the compound thereon. 
   In a particular embodiment, a tantalum boride or tantalum silicide barrier layer is formed by cyclically introducing tantalum pentafluoride and diborane or silane or disilane to the substrate surface. To initiate the cyclical deposition of the Ta layer, a carrier gas such as argon is introduced into the processing chamber  200  to stabilize the pressure and temperature therein. The carrier gas is allowed to flow continuously during the deposition process such that only the argon flows between pulses of each compound. One example of a first pulse of TaF 5  provided to the chamber from the gas source  238  includes a flow rate between about 100 sccm and about 400 sccm, with a pulse time of less than about 5 seconds, for example about 0.6 seconds or less, after the chamber temperature and pressure have been stabilized between about 200° C. and about 600° C., for example between about 300° C. and about 350° C., and about 1 Torr to about 5 Torr. A pulse of diborane or silane or disilane is then provided from the gas source  239  at a flow rate between about 200 sccm and about 600 sccm, with a pulse time of less than about 5 seconds, preferably less than about 1 second for example about 0.6 seconds or less. The heater temperature is maintained between about 100° C. and about 650° C. for a chamber pressure between about 1 Torr and about 5 Torr. 
   A pause between pulses of TaF 5  and diborane or silane may be less than about 5 seconds, such as less than about 1 second, preferably about 0.5 seconds or less, more preferably about 0.1 seconds or less. In various aspects, a reduction in time between pulses at least provides higher throughput. As a result, a pause after the pulse of diborane or silane or disilane is also less than about 5 seconds, such as less than about 1 second, preferably about 0.5 seconds or less, or about 0.1 seconds or less. Argon gas flowing between about 100 sccm and about 1,000 sccm, such as between about 100 sccm and about 400 sccm, is continuously provided from the gas source  240  through each valve  242 A,  242 B. In one aspect, a pulse of TaF 5  may still be in the chamber when a pulse of diborane or silane or disilane enters. In general, the duration of the carrier gas and/or pump evacuation should be long enough to prevent the pulses of TaF 5  and diborane or silane from mixing together in the reaction zone. 
   Each cycle consisting of a pulse of TaF 5 , pause, pulse of diborane or silane or disilane, and pause provides a tantalum layer having a thickness of about 5 Å or less, such as between about 3 Å and about 4 Å, per cycle. The alternating sequence may be repeated until the desired thickness is achieved, which is less than about 50 Å, such as about 10 Å. Accordingly, the deposition method requires between 2 cycles and 70 cycles, more typically between 20 cycles and 30 cycles. A process as described may deposit a tantalum layer having a film resistivity between about 180 micro-ohms-centimeter (μΩ-cm), with a silicon content of about 30 atomic or weight percent or less, and a fluorine content of less than about 1 atomic or weight percent. 
   The process described herein also contemplates depositing a ternary compound such as tantalum boronitride or tantalum silicon nitride. The process described herein may be adapted to include a pulse of a nitrogen containing reductant, such as ammonia either preceding or subsequent to a diborane or silane pulse. In one embodiment, each cycle consists of a pulse of a tantalum containing compound, a pause, a pulse of a boron containing compound, such as borane, or a silane compound, such as silane or disilane, a pause, a pulse of a nitrogen containing compound, and a pause. Each pulse is performed sequentially, and is accompanied by a separate flow of carrier gas at the same process conditions described above. The separate flow of purge gas may be pulsed between each pulse of reactive compound or the separate flow of carrier gas may be introduced continuously throughout the deposition process. 
   Alternatively, one or more reductants may be used in the deposition of metal barrier layer  440  to form one or more binary compounds. The reductants may be alternated or substituted during cyclical deposition. For example, in a substitution deposition technique, a metal barrier layer  440  is first deposited by 20 cycles of diborane/TaF 5  and then 40 cycles of SiH 4 /TaF 5 . In an alternating precursor technique, a metal barrier layer  440  may be deposited by a cycle of diborane/TaF 5  and then a cycle of SiH 4 /TaF 5 , and then repeating the process. 
   Prior to the deposition of barrier metal on top of metal nitride, the metal nitride surface may need to be activated to initial metal barrier growth by ALD by a soak process described herein. For example, a soak process for depositing an ALD Ta(Si) on an ALD TaN can be performed by a two step soak process. The two-step process includes a reductant soak of B 2 H 6  between about 0.1 seconds and about 60 seconds followed by a precursor soak of WF 6  between about 0.1 seconds and about 60 seconds to convert the TaN surface to be fluorine terminated. This soak process may be further performed to include a reductant exposure to a second reductant of SiH 4  (or disilane, Si 2 H 6 ) between about 0.1 seconds and about 10 seconds with a pressure between about 0.01 Torr and about 100 Torr to transfer the surface to be silicon terminated so that the surface is ready to react with TaF 5  to form a tantalum metal barrier layer. Alternatively, ALD Ta growth can be performed without the SiH 4  (or disilane, Si 2 H 6 ) soak step, which presence of silane can result in CuSi formation by the reaction of SiH 4  (or disilane, Si 2 H 6 ) with Cu metal line underneath a via. ALD W layer formed by the tungsten soak process may be terminated by SiH 4  (or disilane, Si 2 H 6 ) soak, which can be a good Cu wetting layer to interface between ALD TaN and Cu. 
   The tantalum deposition process may be performed under the following deposition conditions including supplying the tantalum precursor at a rate between about 1 sccm and about 100 sccm, such as between about 5 sccm and about 50 sccm, supplying the nitrogen free reductant at a rate between about 1 sccm and about 100 sccm, such as between about 5 sccm and about 50 sccm, supplying a carrier gas at a flow rate between about 100 sccm and about 1,000 sccm, such as between about 100 sccm and about 700 sccm, maintaining the chamber pressure less than about 120 Torr, such as between about 1 Torr and about 50 Torr, for example, between about 1 Torr and about 5 Torr, and maintaining the deposition temperature between about 100° C. and about 400° C., such as between 175° C. and about 350° C., for example 300° C. 
   Post-Deposition Techniques 
   The metal nitride layer  430  and/or metal layer  440  may be exposed to a reducing plasma to remove contaminants, such as halides, from the substrate surface. The plasma treatment may be performed in the same chamber used to deposit the barrier layers  430 ,  440 . The plasma treatment may be performed after the deposition of the barrier layers  430 ,  440  or after each pulse or pulse cycle for depositing the metal or metal nitride layers. The plasma treatment generally includes providing an inert gas including helium, argon, neon, xenon, krypton, or combinations thereof, of which helium is preferred, and/or a reducing gas including hydrogen, ammonia, a reductant as described herein for a soak process, and combinations thereof, to a processing chamber. The reducing plasma may be specified for each barrier layer  430 ,  440 , such as hydrogen gas for metal barrier layer  440  and ammonia for metal nitride barrier layer  430 . The hydrogen plasma may be a remote plasma transferred into the processing chamber for treating the substrate. 
   One example of a possible gas treatment process includes introducing a reducing gas, for example, hydrogen, and optionally an inert gas, into the processing chamber at a total flow rate between about 500 sccm and about 3,000 sccm, such as between about 1,000 sccm and about 2,500 sccm of hydrogen, and generating a plasma in the processing chamber using a power density ranging between about 0.03 W/cm 2  and about 3.2 W/cm 2 , which is a RF power level of between about 10 W and about 1,000 W for a 200 mm substrate. The RF power can be provided at a high frequency such as between 13 MHz and 14 MHz. The RF power can be provided continuously or in short duration cycles wherein the power is on at the stated levels for cycles less than about 200 Hz and the on cycles total between about 10% and about 30% of the total duty cycle. Alternatively, the RF power may also be provided at low frequencies, such as 356 kHz, for plasma treating the depositing silicon carbide layer. Alternatively microwave and remote plasma sources may be used to generate a plasma as an alternative to RF power applications described herein. 
   For the example hydrogen plasma process, the processing chamber may be maintained at a chamber pressure of between about 10 milliTorr and about 12 Torr, the substrate may be maintained at a temperature between about 200° C. and about 450° C., during the plasma treatment. The example hydrogen plasma treatment may be performed between about 10 seconds and about 100 seconds, with a plasma treatment between about 40 seconds and about 60 seconds preferably used. The processing gas may be introduced into the chamber by a gas distributor positioned between about 50 mils and about 600 mils from the substrate surface. However, it should be noted that the respective parameters may be modified to perform the plasma processes in various chambers and for different substrate sizes, such as 300 mm substrates. 
   An anneal technique may also be performed after the deposition of individual layers including the metal nitride barrier layer  430  and the metal barrier layer  440 . The anneal process may be performed in combination with the reducing plasma technique herein. For example, deposited layers  430  and/or  440 , may be exposed to an annealing process of about 380° C. for about 1 hour in a nitrogen atmosphere. 
   The anneal technique may also be performed after the deposition of an anneal process. For example, the ALD metal nitride layer  430 /ALD metal barrier  440 /Cu seed  450  stack film can be annealed at temperature between about 50 to about 450° C. for about 1 sec to about 600 sec to stabilize ALD metal/Cu seed interface, which can further prevent Cu agglomeration even the stack film is exposed to air prior to ECP copper fill. 
   Additional Layer Deposition 
   Alternatively, the metal layer  440  may be enhanced by the deposition of a metal material deposited by another method. For example, an alpha phase tantalum (α-Ta) layer having a thickness of about 20 Å or less, such as about 10 Å, may be deposited over at least a portion of the previously deposited barrier layers  430 ,  440 . The α-Ta layer may be deposited using conventional techniques, such as PVD and CVD, or even another ALFD process. For example, the bilayer stack may include a TaN portion deposited by cyclical layer deposition described above, a Ta portion deposited by cyclical layer deposition described above, and an α-Ta portion deposited by high density plasma physical vapor deposition (HDP-PVD). 
   To further illustrate, the α-Ta portion of the stack may be deposited using an ionized metal plasma (IMP) chamber, such as a Vectra™ chamber, available from Applied Materials, Inc. of Santa Clara, Calif. The IMP chamber includes a target, coil, and biased substrate support member, and may also be integrated into an Endura™ platform, also available from Applied Materials, Inc. A power between about 0.5 kW and about 5 kW is applied to the target, and a power between about 0.5 kW and 3 kW is applied to the coil. A power between about 200 W and about 500 W at a frequency of about 13.56 MHz is also applied to the substrate support member to bias the substrate. Argon is flowed into the chamber at a rate of about 35 sccm to about 85 sccm, and nitrogen may be added to the chamber at a rate of about 5 sccm to about 100 sccm. The pressure of the chamber is typically between about 5 milliTorr to about 100 milliTorr, while the temperature of the chamber is between about 20° C. and about 300° C. 
   Metal Deposition 
   Referring to  FIG. 4D , the seed layer  450  may be deposited using high density plasma physical vapor deposition (HDP-PVD) to enable good conformal coverage. One example of a HDP-PVD chamber is the Self-Ionized Plasma SIP™ chamber, available from Applied Materials, Inc. of Santa Clara, Calif., which may be integrated into an Endura™ platform, available from Applied Materials, Inc. Of course, other techniques, such as physical vapor deposition, chemical vapor deposition, atomic layer deposition, electroless plating, electroplating, or combinations thereof, may be used. 
   A typical SIP™ chamber includes a target, coil, and biased substrate support member. To form the copper seed layer, a power between about 0.5 kW and about 5 kW is applied to the target, and a power between about 0.5 kW and 3 kW is applied to the coil. A power between about 200 and about 500 W at a frequency of about 13.56 MHz is applied to bias the substrate. Argon is flowed into the chamber at a rate of about 35 sccm to about 85 sccm, and nitrogen may be added to the chamber at a rate of about 5 sccm to about 100 sccm. The pressure of the chamber is typically between about 5 milliTorr to about 100 milliTorr. 
   Alternatively, a seed layer  450  containing a copper alloy may be deposited by any suitable technique such as physical vapor deposition, chemical vapor deposition, electroless deposition, or a combination of techniques. Preferably, the copper alloy seed layer  450  contains aluminum and is deposited using a PVD technique described above. During deposition, the process chamber is maintained at a pressure between about 0.1 milliTorr and about 10 milliTorr. The target includes copper and between about 2 and about 10 atomic weight percent of aluminum. The target may be DC-biased at a power between about 5 kW and about 100 kW. The pedestal may be RF-biased at a power between about 10 W and about 1,000 W. The copper alloy seed layer  450  is deposited to a thickness of at least about 5 Å, and between about 5 Å and about 500 Å. 
   The metal layer  460  is preferably copper and is deposited using CVD, PVD, electroplating, or electroless techniques. Preferably, the copper layer  460  is formed within an electroplating cell, such as the ELECTRA® Cu ECP system, available from Applied Materials, Inc., of Santa Clara, Calif. The ELECTRA® Cu ECP system may also be integrated into an ENDURA® platform also available from Applied Materials, Inc. 
   A copper electrolyte solution and copper electroplating technique is described in commonly assigned U.S. Pat. No. 6,113,771, entitled “Electro-deposition Chemistry”, which is incorporated herein by reference to the extent not inconsistent with the claimed aspects and disclosure herein. Typically, the electroplating bath has a copper concentration greater than about 0.7 M, a copper sulfate concentration of about 0.85, and a pH of about 1.75. The electroplating bath may also contain various additives as is well known in the art. The temperature of the bath is between about 15° C. and about 25° C. The bias is between about −15 volts to about 15 volts. In one aspect, the positive bias ranges from about 0.1 volts to about 10 volts and the negatives bias ranges from about −0.1 to about −10 volts. 
   Optionally, an anneal treatment may be performed following the metal layer  460  deposition whereby the wafer is subjected to a temperature between about 100° C. and about 500° C., for example, about 475° C., for about 10 minutes to about 1 hour, preferably about 30 minutes. Two examples of anneal process are exposure to a nitrogen atmosphere for 30 minutes at 475° C. and exposure to a nitrogen atmosphere for 1 hour at 380° C. A carrier/purge gas such as helium, argon, hydrogen, nitrogen, or a mixture thereof is introduced at a rate of about 100 sccm to about 10,000 sccm. The chamber pressure is maintained between about 2 Torr and about 10 Torr. Optionally, a RF power may be applied between about 200 W to about 1,000 W at a frequency of about 13.56 MHz. Preferable substrate spacing is between about 300 mils and about 800 mils. 
   Following deposition, the top portion of the resulting structure may be planarized. A chemical mechanical polishing (CMP) apparatus may be used, such as the Mirra™ System available from Applied Materials, Santa Clara, Calif., for example. Optionally, the intermediate surfaces of the structure may be planarized between the depositions of the subsequent layers described above. 
   The following example is intended to provide a non-limiting illustration of one embodiment of the present invention. 
   EXAMPLES 
   A tantalum (Ta) layer was deposited on a TaN layer by using a multi-step cyclical deposition process as follows with a soak process. 
   The tantalum nitride layer was formed by a process comprising flowing TaF 5 , SiH 4  and NH 3  or TaF 5 , NH 3  and SiH 4 . For example, the tantalum nitride layer may be deposited at 325° C. by depositing about 5 Å TaN by a PDMAT/NH 3  process, then a ten cycle process of NH 3  for about 3 seconds, SiH 4  for about 1 second, TaF 5  for about 2 seconds, a SiH 4  soak, and then a cycle of SiH 4  for about 1 second and TaF 5  for about 1 second. 
   The soak process forms an initial layer of tungsten by one or multiple cycles of diborane (B 2 H 6 ) and tungsten fluoride (WF 6 ) to prevent excessive silane (or disilane) exposures. The tungsten layer is exposed to small dose of silane (or disilane) exposures to convert the surface to be SiH terminated such that the surface is ready to react with TaF 5  to initiate ALD Ta growth. For example, the soak process may comprise diborane (5% in argon, 5 Torr) exposure for between about 3 seconds and about 10 seconds, followed by a tungsten hexafluoride soak for about 1 second. Alternatively, a soak process to form an initial layer of TaSi x N y  was formed using ammonia exposure for between about 5 seconds and about 20 seconds, a purge process for 5 seconds, followed by a tungsten hexafluoride soak for about 3 seconds. 
   The tantalum (Ta) layer was then deposited using a multi-step cyclical deposition process as follows. The tantalum material was deposited with multiple cycles comprising 2 second silane (SiH 4 ) or disilane, 1 second purge of argon, 4 seconds of and TaF 5  in helium carrier gas, and a 1 second purge of argon before repeating the cycle. Alternatively, an initial layer of tantalum was deposited by 20 cycles of diborane (B 2 H 6 ) and tantalum pentafluoride (TaF 5 ), a soak layer of silane was deposited for 60 seconds, and remaining tantalum material was deposited for 200 cycles of silane (SiH 4 ) and TaF 5 . The substrate was than annealed for one hour at 380° C. in a nitrogen environment. 
   According to the processes described herein, a tantalum (Ta) layer was deposited using a multi-step cyclical deposition process by cycles of silane (SiH 4 ) and TaF 5  at a deposition rate of between about 1 Å and about 5 Å to produce a film having a film resistivity of about 180 μΩ-cm with about 30 atomic % Si and less than 1 atomic % F, which exhibited good copper adhesion and wetting verified after 470° C. anneal. 
   While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.