Patent Publication Number: US-2017349735-A1

Title: Process for the preparation of a heterophasic propylene copolymer

Description:
The invention is directed to a process for the preparation of a heterophasic propylene copolymer, a heterophasic propylene copolymer and the use of the heterophasic propylene copolymer. 
     Polypropylene is formed by polymerizing propylene with suitable catalysts. Polypropylene properties vary according to molecular weight, method of production, and the copolymers involved. A heterophasic propylene copolymer has at least a two-phase structure, consisting of a propylene-based semi-crystalline matrix and a dispersed elastomer phase, typically an ethylene-propylene rubber (EPR). These polypropylenes are generally prepared in one or more reactors, by polymerization of propylene in the presence of a catalyst system, and subsequent polymerization of a propylene-ethylene mixture; but can also be made by blending different (co)polymers. The advantage of heterophasic propylene copolymers is improved impact resistance, especially at lower temperatures. 
     Heterophasic propylene copolymers are also known as impact polypropylene. 
     WO 2014/044680 comprises a process for the preparation of a composition comprising heterophasic propylene copolymer and talc. 
     US 2014/0088255 discloses a propylene resin material capable of affording molded article superior in impact properties, tensile properties and appearance. 
     EP 2 083 046 relates to polymer compositions with improved scratch resistance and no or low gloss. 
     US 2006/0155069 discloses a process for making a thermoplastic polyolefin ekastomer. 
     EP1354901 describes heterophasic propylene polymer compositions comprising 70-95 wt % of a matrix phase comprising a propylene homopolymer and/or a propylene copolymer and 5-30 wt % of a disperse phase comprising an ethylene rubber copolymer, the ethylene rubber copolymer being distributed within the polymer composition in the form of particles. It is described that this heterophasic propylene polymer is characterized by an improved processability as well as an improved balance of mechanical parameters. 
     There is however a demand to further improve the mechanical properties of the heterophasic propylene copolymers, in particular the balance between the melt flow, the toughness and the stiffness of the heterophasic propylene copolymer. 
     It is an object of the invention to provide a process for the preparation of a heterophasic propylene copolymer having improved mechanical properties. 
     The object is achieved according to the invention by a process for the preparation of a heterophasic propylene copolymer comprising mixing a polymer composition comprising 55-95 wt % of a propylene polymer and 5-45 wt % of an ethylene-propylene rubber with 0.01-1 wt % of an organic peroxide with a decomposition half-life time of 6 minutes at a temperature between 80 and 109° C. and 0.001-1.5 wt % of a co-agent, wherein all weight percentages are based on the total weight of the polymer composition, wherein the mixing is performed at a temperature which is below the temperature where the organic peroxide has a decomposition half-life time of 6 minutes to obtain a mixed polymer composition, and subsequently melt-mixing the mixed polymer composition. 
     It was surprisingly found that during melt-mixing of the polymer composition with the organic peroxide and the co-agent the melt flow index (MFI) value of the polymer composition remained at an about equal level while the Izod impact raised to a higher value compared with the Izod impact of the polymer composition before melt-mixing. Moreover the amount of crosslinking of the heterophasic propylene copolymer remains very low, giving a low gel content, excellent appearance and absence of surface defects. 
     An additional advantage of the process of the present invention is, that stable MFI values can be obtained, which do not depend on slight variations of the process. Moreover the heterophasic propylene copolymer obtained in the process of the invention shows an improved brittle to tough transition temperature relative to the (reference) polymer composition that is introduced in the process of the invention. 
     The invention is directed to a process for the preparation of a heterophasic propylene copolymer comprising mixing a polymer composition comprising a propylene polymer and an ethylene-propylene rubber with a peroxide and a co-agent and subsequently melt-mixing the mixed polymer composition. 
     The polymer composition comprises a propylene polymer. The propylene polymer can be chosen from a propylene homopolymer and/or a propylene copolymer comprising at least 90 wt % of propylene and up to 10 wt % ethylene and/or at least one C 4  to C 10  alpha-olefin. In a preferred embodiment, the propylene polymer is a propylene homopolymer. 
     The amount of propylene polymer in the polymer composition is 55-95 wt % based on the total weight of the polymer composition, preferably the amount of propylene polymer is 65-95 wt %, more preferably 70-90 wt %. 
     The polymer composition also comprises an ethylene-propylene rubber. The ethylene-propylene rubber preferably comprises from 15 to 70 wt % of ethylene and from 30 to 85 wt % of propylene. The ethylene-propylene rubber can also comprise an amount of up to 10 wt % of a C 4  to C 10  alpha-olefin. 
     The amount of ethylene-propylene rubber in the polymer composition is 5-45 wt % based on the total weight of the polymer composition, preferably the amount of ethylene-propylene rubber is 5-35 wt %, more preferably 10-30 wt %. 
     The propylene polymer and ethylene-propylene copolymer can be mixed before the process according to the invention, for example during a polymerization process or blending process of the two components. 
     The polymer composition can have a MFI index (Melt Flow Index) between 1 and 50, preferably between 2 and 35, most preferably between 5 and 20. The MFI value is determined according to ISO 1133-1:2011. 
     In the process for the preparation of a heterophasic propylene copolymer an organic peroxide is present. The organic peroxide used in the process according to the invention has a low decomposition half-life temperature. The organic peroxide that is used in the process according to the invention has a decomposition half-life time of 6 minutes at a temperature between 80 and 109° C. Preferably, the organic peroxide has a decomposition half-life time of 6 minutes at a temperature between 82 and 105° C., more preferably between 85 and 100° C. 
     Suitable organic peroxides can, for example, be chosen from the group consisting of tert-amyl peroxyneodecanoate, tert-butyl peroxyneodecanoate, 1,1,3,3-tetramethylbutyl peroxypivalate, tert-butyl peroxyneoheptanoate, tert-amyl peroxypivalate, tert-butyl peroxypivalate, di(3,5,5-trimethylhexanoyl) peroxide, dilauroyl peroxide, didecanoyl peroxide, 2,5-dimethyl-2,5-di(2-ethylhexanoylperoxy)hexane, 1,1,3,3-tetramethylbutyl peroxy-2-ethylhexanoate and tert-amyl peroxy-2-ethylhexanoate. Preferably, the organic peroxide has a structure according to formula I 
       R1—(C═O)—O—O—(C═O)−R2   (I)
 
     wherein R1 and R2 are the same or different and are chosen from alkyl, aryl or aralkyl groups, having between 2 and 30 carbon atoms. 
     The alkyl, aryl and aralkyl groups can be linear or branched groups. 
     Examples of R1 or R2 groups are pentyl, hexyl, octyl, phenyl, cyclohexyl, 2-methylhexyl, 2,2-methylhexyl, 8-ethyloctyl, 3,5,5 trimethylhexanoyl, lauroyl, decanoyl or dibenzoyl. Preferably, the R1 and R2 groups contain between 6 and 25, more preferably between 10 and 20 carbon atoms. More preferably, the organic peroxide is chosen from the group consisting of di(3,5,5-trimethylhexanoyl) peroxide, dilauroyl peroxide and didecanoyl peroxide. Most preferably, the organic peroxide is dilauroyl peroxide. 
     The amount of organic peroxide that is added to the process of the invention is 0.01-1 wt % based on the total weight of the polymer composition, preferably the amount of organic peroxide is 0.05-0.9 wt %, more preferably 0.1-0.8 wt %. 
     In the process for the preparation of the heterophasic propylene copolymer a co-agent is present. A co-agent is herewith defined as a monomeric compound which can be polymerized with the aid of free radicals. Preferably, the co-agent is a bi-functionally or poly-functionally unsaturated compound. ‘Bi-functionally unsaturated’ as used above means the presence of two polymerizable double bonds in the compound. ‘Poly-functionally unsaturated’ as used above means the presence of three or more polymerizable double bonds in the compound. 
     Examples of Co-Agents are:
         divinyl compounds, such as divinylaniline, ortho-divinylbenzene, para-divinylbenzene, divinylpentane and divinylpropane;   allyl compounds, such as allyl acrylate, allyl methacrylate, allyl methyl maleate and allyl vinyl ether;   compounds with two (meth)acrylate groups; and   dienes, such as 1,3-butadiene, chloroprene, cyclohexadiene, cyclopentadiene, 2,3-dimethylbutadiene, heptadiene, hexadiene, isoprene and 1,4-pentadiene;   and mixtures of these unsaturated monomers.       

     Preferably, the co-agent is chosen from the group consisting of 1,3-butadiene, isoprene, 2,3-dimethylbutadiene and ortho- or para-divinylbenzene, more preferably the co-agent is ortho- or para-divinylbenzene. 
     The amount of co-agent that is added in the process of the invention is between 0.001-1.5 wt % based on the total weight of the polymer composition, preferably the amount of co-agent is 0.01-1.2 wt %, more preferably 0.1-1.0 wt %. 
     According to the invention the process for the preparation of a heterophasic propylene copolymer comprises mixing a polymer composition comprising the propylene polymer and the ethylene-propylene rubber with the organic peroxide and the co-agent to obtain a mixed polymer composition and subsequently melt-mixing the mixed polymer composition. 
     Mixing is performed by mixing the polymer composition comprising the propylene polymer, the ethylene-propylene rubber, with the organic peroxide and the co-agent at a temperature which is below the temperature where the organic peroxide has a decomposition half-life time of 6 minutes. Preferably, the temperature during mixing is at least 5° C. below the temperature where the organic peroxide has a decomposition half-life time of 6 minutes, more preferably at least 10° C. below the temperature where the organic peroxide has a decomposition half-life time of 6 minutes. The temperature in the mixing zone can, for example, be between 20 and 104° C., more preferably between 25 and 99° C., most preferably between 50 and 95° C. 
     Mixing can be performed in any way known to the person skilled in the art. Commonly used mixing devices are a tumbler mixer, a high speed mixer, a jet mixer, a planetary mixer or a Banbury mixer; and blenders, for example V blender, ribbon blender or a cone blender. During mixing the polymer composition can be preheated. Mixing can also be performed in a part of an extruder. Examples of extruders are mono and twin screw extruders. 
     After mixing the mixed polymer composition is melt-mixed by heating the mixed polymer composition to a temperature above the melting temperature of the propylene polymer. 
     The melting temperature of the propylene polymer is determined by differential scanning calorimetry according to ISO 11357, wherein heating is performed at a heating rate of 10° C./min and the melting temperature is taken from the second heating curve. Melt-mixing preferably is performed at a temperature above 160° C., more preferably at a temperature above 180° C., most preferably at a temperature above 200° C. Melt-mixing preferably is performed at a temperature below 300° C., more preferably at a temperature below 280° C., most preferably at a temperature below 260° C. 
     Preferably, the process is performed in an extruder comprising a mixing zone having a temperature below the temperature where the organic peroxide has a decomposition half-life time of 6 minutes for mixing the propylene polymer, the ethylene-propylene rubber, the organic peroxide and the co-agent, and a subsequent reaction zone having a temperature above the melting temperature of the propylene polymer for melt-mixing the mixed polymer composition. 
     The invention also relates to the use of dilauroyl peroxide with a co-agent from the group consisting of 1,3-butadiene, isoprene, 2,3-dimethylbutadiene and ortho—or para-divinylbenzene in treating a heterophasic propylene polymer composition comprising 70-95 wt % of a propylene polymer and 5-30 wt % of an ethylene-propylene rubber, by first mixing the components at a temperature below the temperature where the dilauroyl peroxide has a decomposition half-life time of 6 minutes to obtain a mixed polymer composition and subsequent melt mixing the mixed polymer composition. 
     The present invention also relates to a novel heterophasic propylene copolymer. By treatment of the polymer composition comprising 60-92 wt % of a propylene polymer and 8-40 wt % of an ethylene-propylene rubber, with an ethylene content between 15-70wt % , with 0.01-1 wt % of an organic peroxide with a decomposition half life time of 6 minutes at a temperature between 80 and 109° C. and 0.001-1.5 wt % of a co-agent, a new and special heterophasic copolymer has been obtained having a special combination of properties. 
     The heterophasic propylene copolymer has
         a. Overall ethylene content between 5-20 wt %   b. MFI between 3 and 25 (g/10 min)   c. 20° C. xylene soluble fraction (CXS) between 8 and 30 (wt %)   d. a BTT according to the formula: BTT≦65-10* (CXS/MFI)       

     The heterophasic propylene copolymer has an overall ethylene content between 5 and 20 wt %, as measured with IR spectroscopy, which was calibrated using NMR according to known procedures. 
     Preferably the amount of ethylene ranges between 7 and 17 wt %, relative to the total of the propylene composition. 
     The MFI ranges between 3 and 25 (g/10 min), as measured in accordance with ISO 1133-1:2011 at 230° C. with a weight of 2.16 kg. Preferably the MFI ranges between 3.5 and 20 g/10min. 
     The 20° C. xylene soluble fraction (CXS) ranges between 8 and 30 wt %, and is determined in accordance with ISO 16152. Preferably CXS ranges between 9 and 20, more preferably between 10-18 wt %. Advantage of having these high CXS values is, that crosslinking of the rubber phase of the heterophasic copolymer is absent, or only a low amount of crosslinking occurs. The absence of substantial crosslinking facilitates extrusion and film formation, causes less defects and a higher impact material. Moreover the surface of articles shows less surface defects and is smoother. 
     The CXS values of the heterophasic polymer according to the invention are much higher than products which have been obtained by reacting polymer compositions with peroxides and coagent which are reactive at higher temperatures. At these higher temperatures, a substantial amount of crosslinking of the rubber phase of the heterophasic copolymer takes place, which decreases the amount of ethylene-propylene copolymers that are soluble in xylene at 25° C. (so lower CXS value). 
     The heterophasic copolymer according to the invention has a surprisingly low brittle tough temperature (BTT). The BTT is normally influenced by the MFI of a polymer and by the CXS of a polymer. In the present invention, the BTT relation has changed and a lower BTT is obtained at the same CXS and MFI values compared to polymers of the state of the art. 
     The BTT relation is: BTT≦65-10* (CXS/MFI) (° C.) 
     Preferably the following relation of BTT is valid:
         BTT≦60-10* (CXS/MFI) (° C.).       

     A low BTT has the advantage that products show excellent toughening behavior and impact resistance. In combination with the relative high MFI (which is accompanied with excellent flow) the present heterophasic copolymer shows an excellent set of preferred properties. 
     Preferably the heterophasic propylene copolymer according to the invention has a very low gelcontent. The gelcontent is less than 4 wt %, preferably less than 3 wt %, more preferably less than 2 wt %. The gelcontent is determined by dissolving the heterophasic propylene copolymer in boiling xylene (130° C.), separating the dissolved polymer from solids and recovering the dissolved polymer. The difference between starting amount of heterophasic propylene copolymer and recovered dissolved polymer is the gelcontent of the heterophasic propylene copolymer. In practice the determination of low amounts of gel is difficult. Gelcontent numbers between 0 and 2 wt % correspond to very low amounts of gel, or the absence of any gel. 
     The invention is further directed to the use of the heterophasic propylene copolymer in garden furniture, household items, battery casings, automobile parts, containers, toys, crates and boxes. 
     Although the invention has been described in detail for purposes of illustration, it is understood that such detail is solely for that purpose and variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention as defined in the claims. 
     It is further noted that the invention relates to all possible combinations of features described herein, preferred in particular are those combinations of features that are present in the claims. 
     It is noted that the term ‘comprising’ does not exclude the presence of other elements. However, it is also to be understood that a description on a product comprising certain components also discloses a product consisting of these components. Similarly, it is also to be understood that a description on a process comprising certain steps also discloses a process consisting of these steps. 
     The invention will now be elucidated by way of the following examples without however being limited thereto. 
    
    
     EXAMPLES 
     Materials 
     The polymer compositions were all Sabic products: blends of homopolymer of propylene with an ethylene propylene copolymer ‘rubber’. 
     More detailed information regarding the composition of the polymer compositions can be found in table 1. 
     
       
         
           
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                 Propylene copolymers powder mixtures 
               
            
           
           
               
               
               
               
               
               
            
               
                   
                   
                   
                 P1 
                 P2 
                 P3 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
               
            
               
                   
                 MFI 
                 [g/10 min] 
                 1.9 
                 5.3 
                 14.4 
               
               
                   
                 CXS 
                 [wt %] 
                 18 
                 12 
                 12 
               
               
                   
                 overall C2 content 
                 [wt %] 
                 14 
                 9 
                 9 
               
               
                   
                 BTT 
                 [° C.] 
                 −4 
                 40 
                 60 
               
               
                   
                   
               
            
           
         
       
     
     Peroxides: 
     
         
         Laurox® S , dilauroyl peroxide; decomposition half-life time=6 min at a temperature of 99° C. (T(° C.) for t ½ of 0.1 h). 
         Trigonox® BPIC-C75, t-butylperoxy isopropyl carbonate; decomposition half-life time=6 min at a temperature of 137° C. 
         Luperox® 802PP40, di(t-butylperoxyisopropyl)benzene; decomposition half-life time=6 min at a temperature of 156° C. 
         Perkadox 14, Di(tert-butylperoxyisopropyl)benzene, T(° C.) for t ½ of 0.1 h is 156° C. 
         Trigonox 25, tert butyl peroxy pivalate, T(° C.) for t ½ of 0.1 h is 94° C. 
         Co-Agent Divinylbenzene (DVB) 
         Additives: Calcium stearate; Irganox® 8225 
       
    
     Preparation of the Samples 
     The samples for the experiments were prepared with a standard additive package of 0.1 wt. % calcium stearate and 0.2 wt. % Irganox 8225. Various ratios peroxide/co-agent were added to each sample. The additives and heterophasic propylene copolymer powders were pre-mixed and the peroxides and the co-agents were dosed per batch, and homogenized by hand just before the extrusion on a ZSK 25 extruder. All experiments have been performed with the same screw, temperature settings (temperature in the mixing zone was 40° C. and temperature in the melt-mixing zone was 240° C.), a screw speed of 200 rpm and a throughput of 8 kg/hour. In table 2 all the samples which were produced are described. 
     Test Methods 
     The MFI value was determined according to ISO 1133-1:2011 at 230° C. and 2.16 kg. 
     The Izod impact was determined according to ISO 180/4A at 23° C. and 3.2 mm or to determine the brittle to tough transition temperature (BTT) at various higher temperatures. The Izod impact was determined parallel (II). 
     All compounds analyzed were separated in a CXS (&lt;25° C.) fraction, a CXUS (25° C.-130° C). fraction (respectively called the 25C and the 130C fraction), and a gel fraction (non-soluble in hot xylene). The difference between a recovery of 100 wt. % and the observed recovery was taken as an indicative number for gel content. 
     Table 2 also shows the test results for all samples. 
     
       
         
           
               
             
               
                 TABLE 2 
               
             
            
               
                   
               
               
                 Test Results 
               
            
           
           
               
               
               
               
               
               
            
               
                 Exper- 
                   
                 Peroxide 
                 DVB 
                 MFI 
                 Impact 
               
            
           
           
               
               
               
               
               
               
               
            
               
                 iment 
                 Powder 
                 Type 
                 wt % 
                 wt % 
                 g/10 min 
                 kJ/m 2   
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 CE1 
                 P1 
                 — 
                   
                 — 
                 1.9 
                 77 
               
               
                 CE2 
                 P1 
                 Laurox S 
                 0.62 
                 — 
                 2.3 
                 77 
               
               
                 E1 
                 P1 
                 Laurox S 
                 0.62 
                 0.22 
                 0.6 
                 83 
               
               
                 E2 
                 P1 
                 Laurox S 
                 0.62 
                 0.44 
                 1 
                 86 
               
               
                 CE3 
                 P1 
                 Trig.BPIC 
                 0.36 
                 — 
                 6.4 
                 56 
               
               
                 CE4 
                 P1 
                 Trig.BPIC 
                 0.36 
                 0.22 
                 0.9 
                 57 
               
               
                 CE5 
                 P1 
                 Trig.BPIC 
                 0.36 
                 0.44 
                 0.1 
                 20 
               
               
                 CE6 
                 P1 
                 Luperox  
                 0.36 
                 — 
                 150 
                 6 
               
               
                   
                   
                 802PP40 
                   
                   
                   
                   
               
               
                 CE7 
                 P1 
                 Luperox  
                 0.36 
                 0.22 
                 35 
                 20 
               
               
                   
                   
                 802PP40 
                   
                   
                   
                   
               
               
                 CE8 
                 P1 
                 Luperox  
                 0.36 
                 0.44 
                 12 
                 22 
               
               
                   
                   
                 802PP40 
                   
                   
                   
                   
               
               
                 CE11 
                 P2 
                 — 
                 — 
                 — 
                 5.3 
                 16 
               
               
                 CE12 
                 P2 
                 Laurox S 
                 0.62 
                 — 
                 6.8 
                 13 
               
               
                 E11 
                 P2 
                 Laurox S 
                 0.62 
                 0.22 
                 4.6 
                 19 
               
               
                 E12 
                 P2 
                 Laurox S 
                 0.62 
                 0.44 
                 4.8 
                 36 
               
               
                 CE13 
                 P2 
                 Trig.BPIC 
                 0.36 
                 — 
                 31 
                 10 
               
               
                 CE14 
                 P2 
                 Trig.BPIC 
                 0.36 
                 0.22 
                 4.8 
                 17 
               
               
                 CE15 
                 P2 
                 Trig.BPIC 
                 0.36 
                 0.44 
                 1 
                 22 
               
               
                 CE16 
                 P2 
                 Luperox  
                 0.36 
                 — 
                 &gt;150 
                 2.4 
               
               
                   
                   
                 802PP40 
                   
                   
                   
                   
               
               
                 CE17 
                 P2 
                 Luperox  
                 0.36 
                 0.22 
                 89 
                 10 
               
               
                   
                   
                 802PP40 
                   
                   
                   
                   
               
               
                 CE18 
                 P2 
                 Luperox  
                 0.36 
                 0.44 
                 24 
                 11 
               
               
                   
                   
                 802PP40 
                   
                   
                   
                   
               
               
                 CE21 
                 P3 
                 — 
                 — 
                 — 
                 14.4 
                 8 
               
               
                 CE22 
                 P3 
                 Laurox S 
                 0.62 
                 — 
                 17 
                 8 
               
               
                 E21 
                 P3 
                 Laurox S 
                 0.62 
                 0.22 
                 15 
                 10 
               
               
                 E22 
                 P3 
                 Laurox S 
                 0.62 
                 0.44 
                 14 
                 10 
               
               
                 CE23 
                 P3 
                 Trig.BPIC 
                 0.36 
                 — 
                 95 
                 8 
               
               
                 CE24 
                 P3 
                 Trig.BPIC 
                 0.36 
                 0.22 
                 12 
                 13 
               
               
                 CE25 
                 P3 
                 Trig.BPIC 
                 0.36 
                 0.44 
                 1.8 
                 13 
               
               
                 CE26 
                 P3 
                 Luperox  
                 0.36 
                 — 
                 &gt;150 
                 1.5 
               
               
                   
                   
                 802PP40 
                   
                   
                   
                   
               
               
                 CE27 
                 P3 
                 Luperox  
                 0.36 
                 0.22 
                 &gt;150 
                 5.7 
               
               
                   
                   
                 802PP40 
               
               
                   
               
               
                 CE = comparative experiment 
               
               
                 E = example 
               
            
           
         
       
     
     Table 2 shows the effect of Laurox S in examples E1, E2, E11, E12, E21 and E22, which are examples according to the present invention and the effect of 2 other peroxides in comparative experiments CE3-CE8, CE13-CE18 and CE23-CE27, which comparative experiments are not according to the present invention. Furthermore three different polypropylene (PP) resins were tested. 
     The first PP-resin (P1) had a high rubber content, and therefore showed already a high Izod impact value at 23° C. The Izod impact value was 77 kJ/m2. Treatment with other peroxides (Trigonox and Luperox) resulted in either crosslinking (which gave a lower MFI value) or degradation of the polymer (which gave a higher MR value). At the same time for all comparative samples, the Izod impact values were lower than 77 kJ/m2. When the peroxide and co-agent of the present invention were added, the MFI values could be kept fairly constant and the impact of the polymer increased after the process of the invention. Moreover, the effect of the presence of the co-agent was rather independent from the concentration of co-agent, making the process a stable process. 
     The other two PP resins(P2 and P3) had a composition which contained a lower amount of rubber and therefore the impact values of the virgin material were 16 and 8 respectively. The difference in impact resistance resulted from the difference in MFI of both starting polymer compositions; a Product with a lower MFI gives a higher impact value. 
     For comparative experiments CE13-CE15 the use of Trigonox resulted first in an increase of MFI (in the absence of co-agent), but later in a strong decrease of MFI due to crosslinking, accompanied with a decrease of the impact. Moreover, the behaviour of the peroxide reaction was strongly dependent on the exact conditions: with only peroxide, an increase of MFI was shown which was due to polymer degradation, while with co-agent the MFI decreased to 4.8 g/10min, and with more co-agent decreased to 1 g/10min which was due to crosslinking. This means that the process with Trigonox as peroxide was very unstable, and slight changes in the process resulted in different polymers. 
     Furthermore, even at a significant lower MFI (CE15) the impact resistance obtained by using Trigonox was inferior compared to the impact resistance obtained by using Laurox (E12). 
     The use of Luperox showed (CE16-18) degradation of the polymer (increase of MFI) and a strong deterioration of the Impact values. 
     Examples E11-E12 with Laurox S (according to the invention) in combination with the co-agent divinylbenzene show a stable MFI and an increase of the Izod impact . The MFI did not depend very much on the level of coagent used, which made the process very stable. 
     Similar unstable MFI results were obtained for polymer P3 in comparative experiments C23 to C25 and stable MFI&#39;s for example E21-E22 
     The brittle to tough transition temperatures (BTT) were determined for the polymers resulting from examples E11, E12, E21 and E22 with the combination of Laurox S and divinylbenzene as co-agent. 
     The values of the BTT in parallel direction were compared (see table 3). 
     
       
         
           
               
             
               
                 TABLE 3 
               
             
            
               
                   
               
               
                 Brittle to Tough transition Temperatures (BTT) 
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                   
                 Polymer 
                   
                 T½ 
                   
                   
                   
                   
                 Gel 
               
               
                 Experiment 
                 composition 
                 peroxide 
                 0.1 h 
                 DVB 
                 MFI 
                 BTT 
                 CXS 
                 wt % 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                 CE11 
                 P2 
                 N 
                   
                 N 
                 5.3 
                 40 
                 12 
                 0 
               
               
                 CE12 
                 P2 
                 Laurox S 
                 99 
                 N 
                 6.8 
                 40 
                 12 
                 0 
               
               
                 E11 
                 P2 
                 Laurox S 
                 99 
                 Y 
                 4.6 
                 30 
                 12 
                   
               
               
                 E12 
                 P2 
                 Laurox S 
                 99 
                 Y 
                 4.8 
                 20 
                 11 
                 2 
               
               
                 CE21 
                 P3 
                 N 
                   
                 N 
                 14.4 
                 60 
                 12 
                   
               
               
                 CE22 
                 P3 
                 Laurox S 
                 99 
                 N 
                 17 
                 60 
                 12 
                   
               
               
                 E21 
                 P3 
                 Laurox S 
                 99 
                 Y 
                 15 
                 38 
                 12 
                   
               
               
                 E22 
                 P3 
                 Laurox S 
                 99 
                 Y 
                 14 
                 38 
                 11 
                   
               
               
                 CE31 
                 P2 
                 Perkadox 14 
                 156 
                 N 
                   
                   
                 11 
                 4 
               
               
                 CE32 
                 P2 
                 Perkadox 14 
                 156 
                 Y 
                   
                   
                 2 
                 9 
               
               
                 CE33 
                 P2 
                 Trigonox BPIC 
                 137 
                 N 
                   
                   
                 10 
                 3 
               
               
                 CE34 
                 P2 
                 Trigonox BPIC 
                 137 
                 Y 
                   
                   
                 2 
                 10 
               
               
                 E31 
                 P2 
                 Trigonox 25 
                 94 
                 N 
                   
                   
                 13 
                 0 
               
               
                 E32 
                 P2 
                 Trigonox 25 
                 94 
                 Y 
                   
                   
                 8 
                 3 
               
               
                   
               
            
           
         
       
     
     Table 3 shows that the brittle to tough transitions of the polymer compositions prepared in the process according to the invention with Laurox S and divinylbenzene have been lowered, which is an improved result compared to the reference polymer compositions. 
     In case CE11 where no Laurox S and no DVB is used, the BTT is 40° C. With the use of both Laurox S and DVB, the BTT drops to 30° C. (0.22 wt % DVB) and 20° C. with 0.44 wt % DVB, while the impact increases to 19 and 36 kJ/mm2 respectively. 
     The effect of BTT decrease is even stronger at higher MFI levels. In CE21 with or without peroxide, but absent any accelerator, the BTT is 60° C. By using a small amount of DVB (0.22 and 0.44 wt %) the BTT drops to 38° C. 
     The amount of gel produced during the process according to the invention in combination with an accelerator also clearly gives an increase of the amount of gel being formed. When a peroxide is used having a decomposition half life time of 6 minutes (0.1 h) at a temperature below 109 celc, low levels of gels are obtained, especially in case Laurox S is being used.