Patent Publication Number: US-11654507-B2

Title: Method for manufacturing liquid-cooling jacket

Description:
This application is a National Stage Application of PCT/JP2018/018951, filed May 16, 2018, which claims benefit of priority to Japanese Patent Application No. 2017-241824, filed Dec. 18, 2017, which applications are incorporated herein by reference. To the extent appropriate, a claim of priority is made to each of the above disclosed applications. 
     TECHNICAL FIELD 
     The present invention relates to a method for manufacturing a liquid-cooling jacket. 
     BACKGROUND ART 
     As a method for manufacturing a liquid-cooling jacket, there is a method in which a sealing body made of metal is overlapped on a jacket body made of metal, and friction stir welding is performed from a front surface side of the sealing body. And as a rotary tool to be used for friction stir welding, there is known a rotary tool provided with a shoulder part and a stirring pin which is hung down from the shoulder part. This rotary tool is a tool by which friction stir welding is performed in a state where the lower end surface of the shoulder part is pushed into a metal member. By pushing the shoulder part into the metal member, plastically fluidized material can be held to reduce generation of burrs. However, in a case where a joining height position is changed, defects tend to be caused, so that there are problems that a large recessed groove is generated and a lot of burrs are generated. 
     On the other hand, there is known a friction stir welding method using a rotary tool provided with a stirring pin to join two metal members, the method comprising a primary joining process in which the stirring pin which is rotating is inserted in a butting part between the metal members, and friction stir welding is performed in a state where only the stirring pin is in contact with the metal members (Patent Document 1). According to this conventional technique, since a helical groove is formed on the outer surface of the stirring pin and friction stir welding is performed in a state where only the stirring pin is in contact with members to be joined together and the base end thereof is exposed, defects can be suppressed even if a joining height position is changed, and the load on the friction stir welding apparatus can be also reduced. However, since plastically fluidized material is not held by the shoulder part, there are problems that a recessed groove to be generated on a surface of the metal members is made large and the surface roughness of the joined part is made large. Furthermore, there is a problem that an expanded part (a part of the surface of a metal member, the part being expanded relative to the original surface before the joining) is generated beside the recessed groove. 
     In Patent Document 2, a rotary tool provided with a shoulder part and a stirring pin hanging down from the shoulder part is disclosed. The shoulder part and the stirring pin are each provided with a tapered surface on their outer peripheral surfaces. A spiral groove in a plan view is formed on the tapered surface of the shoulder part. Across sectional shape of the spiral groove is a half circle. Joining can be stably performed by providing the tapered surface even in a case where the thickness of a metal member or the height position of the joining is changed. Since plastically fluidized material flows into the groove, the flowing of the plastically fluidized material can be controlled to form a proper plasticized region. 
     PRIOR ART DOCUMENT 
     Patent Document 
     
         
         Patent Document 1: Japanese Unexamined Patent Publication No. 2013-39613 
         Patent Document 2: Japanese Patent No. 4210148 
       
    
     SUMMARY OF THE INVENTION 
     Problem to be Solved by the Invention 
     However, in the conventional technique of Patent Document 2, since plastically fluidized material enters the inside of the groove on the tapered surface, there is a problem that the groove does not work. Furthermore, when plastically fluidized material enters the groove, friction stirring is performed in a state where the plastically fluidized material has adhered to the groove. Therefore, there is a problem that the metal members to be joined together and the adhered material rub against each other to lower the joining quality. And still more, there are problems that the roughness of the joined surface is made large, a lot of burrs are generated, and a recessed groove to be generated on the joined surface is made large. 
     From such a view point, an objective of this invention is to provide a method for manufacturing a liquid-cooling jacket, the method being capable of making the recessed groove to be generated on the joined surface small and the roughness of the joined surface small. 
     Means for Solving the Problem 
     In order to solve the problem, the present invention is characterized by a method for manufacturing a liquid-cooling jacket, the liquid-cooling jacket being formed by including: a jacket body having a bottom part and a frame-like peripheral wall part standing on a periphery of the bottom part; and a sealing body to seal a recessed part of the jacket body, the jacket body and the sealing body together defining a hollow part in which heat transport fluid flows, the method comprising: an overlapping process in which the sealing body is placed on an end surface of the peripheral wall part in such a way that the end surface and a back surface of the sealing body are overlapped each other to form a first overlapped part; and a primary joining process in which primary joining is performed by friction stirring, the primary joining process including inserting a rotary tool provided with a base side pin and a tip side pin in the first overlapped part from a front surface of the sealing body and moving the rotary tool once around the recessed part along the first overlapped part in a state where the base side pin and the tip side pin are in contact with the sealing body, wherein the rotary tool is provided with a flat surface, which is formed at a tip of the tip side pin and is perpendicular to a rotational axis of the rotary tool, and a projection projecting from the flat surface, wherein a tapered angle of the base side pin is larger than another tapered angle of the tip side pin, wherein a stair-like step part is formed on an outer peripheral surface of the base side pin, and wherein in the primary joining process, the first overlapped part is joined in a state where the flat surface is in contact with only the sealing body and a tip of the projection is inserted more deeply than the first overlapped part while the base side pin is in contact with the sealing body. 
     According to the method for manufacturing a liquid-cooling jacket, the base side pin having a large tapered angle can hold the sealing body with the outer peripheral surface thereof. Therefore, a recessed groove to be generated on a joined surface can be made small and an expanded part to be generated beside the recessed groove can be excluded or can be made small. Since the stair-like step part is shallow and the exit is wide, plastically fluidized material is hard to adhere to the outer peripheral surface of the base side pin though the sealing body is held by the base side pin. Hence, the roughness of the joined surface can be made small and the joining quality can be suitably made stable. Furthermore, since the tip side pin is provided, the rotary tool can be easily inserted to a deeper position. 
     Furthermore, according to the method for manufacturing a liquid-cooling jacket, since the tip side pin of the rotary tool has the flat surface, plastically fluidized material whirled up around the projection can be held by the flat surface. Thereby, friction stirring around the projection can be more surely performed, and an oxide film of the first overlapped part can be surely divided. 
     It is preferable that a support part is provided on either the bottom part of the jacket body or the back surface of the sealing body and comes into contact with the other. 
     According to the method for manufacturing a liquid-cooling jacket, the strength of the liquid-cooling jacket can be enhanced because of the support part. 
     It is preferable that the jacket body is provided with a support part standing on the bottom part and to come into contact with the back surface of the sealing body, and in the primary joining process, in addition to friction stir welding to the first overlapped part, friction stir welding is performed also to a second overlapped part where the back surface of the sealing body and an end surface of the support part are overlapped each other. 
     According to the method for manufacturing a liquid-cooling jacket, since friction stir welding is performed also to the second overlapped part, the joining strength between the jacket body and the sealing body can be more enhanced. 
     It is preferable that in the primary joining process, the second overlapped part is joined in a state where the flat surface of the tip side pin is in contact with only the sealing body and the tip of the projection of the tip side pin is inserted more deeply than the second overlapped part. 
     According to the method for manufacturing a liquid-cooling jacket, plastically fluidized material, which is generated by friction stirring along the projection and whirled up by the projection, is held by the flat surface. Thereby, friction stirring around the projection can be surely performed and an oxide film of the second overlapped part can be surely divided. Therefore, the joining strength of the second overlapped part can be enhanced. 
     Furthermore, according to the method for manufacturing a liquid-cooling jacket, in a case where only the projection is set to be inserted more deeply than the second overlapped part, the width of a plasticized region due to friction stirring can be made smaller in comparison with a case where the flat surface is inserted more deeply than the second overlapped part. Thereby, plastically fluidized material can be prevented from flowing into the recessed part of the jacket body. 
     It is preferable that the support part is formed continuously with the peripheral wall part, and in the primary joining process, friction stir welding is performed to the first overlapped part and to the second overlapped part continuously. 
     According to the method for manufacturing a liquid-cooling jacket, since friction stir welding can be performed to the first overlapped part and to the second overlapped part continuously, the liquid-cooling jacket having high deformation-resistance can be manufactured and a production cycle can be improved. 
     It is preferable that the support part is formed continuously with one wall part of the peripheral wall part and apart from another wall part facing the one wall part, and in the primary joining process, the rotary tool is inserted in the front surface of the sealing body at a position corresponding to the support part, friction stir welding is performed to the first overlapped part and to the second overlapped part continuously, and then the rotary tool is pulled up from the sealing body at an outer position than a plasticized region generated in the first overlapped part. 
     According to the method for manufacturing a liquid-cooling jacket, since friction stir welding can be performed to the first overlapped part and to the second overlapped part continuously, the jacket body having high deformation-resistance can be manufactured and a production cycle can be improved. In addition, in a case where the rotary tool is moved to an inner position than the plasticized region, there is a risk that metal material flows out of the first overlapped part formed by the peripheral wall part and the sealing body and the second overlapped part. However, since the rotary tool is moved to an outer position than the plasticized region and then is pulled up, such a problem can be resolved. 
     It is preferable that the jacket body is provided with a support part standing on the bottom part and to come into contact with the back surface of the sealing body, the support part having a projection part on an end surface of the support part, the sealing body is provided with a hole part in which the projection part is inserted, in the overlapping process, the projection part is inserted in the hole part in such a way that a hole wall of the hole part and a side surface of the projection part are butted each other to form a butting part and a second overlapped part where the back surface of the sealing body and the end surface of the support part are overlapped each other, and in the primary joining process, in addition to friction stir welding to the first overlapped part, the rotary tool is inserted in the butting part from the front surface of the sealing body, and in a state where the base side pin and the tip side pin are in contact with the jacket body and the sealing body, friction stir welding is performed also to the second overlapped part where the back surface of the sealing body and the end surface of the support part are overlapped each other and to the butting part where the hole wall of the hole part of the sealing body and the side surface of the projection part of the support part are butted each other. 
     According to the method for manufacturing a liquid-cooling jacket, in the overlapping process, the projection part formed on the end surface of the support part is inserted in the hole part of the sealing body. Hence, positioning of the sealing body can be easily done by fixing the sealing body to the support part. Still more, in the primary joining process, since friction stir welding can be performed also to the butting part where the hole wall of the hole part and the side surface of the projection part are butted each other, the joining strength between the jacket body and the sealing body can be more enhanced. 
     It is preferable that in the primary joining process, as to friction stir welding to the butting part, the second overlapped part and the butting part are each joined in a state where the flat surface is in contact with both the jacket body and the sealing body, and the tip of the projection is inserted more deeply than the second overlapped part. 
     According to the method for manufacturing a liquid-cooling jacket, the plastically fluidized material whirled up by the projection is held by the flat surface. Thereby, oxide films of the second overlapped part and the butting part can be surely divided. Hence, the joining strength can be enhanced. 
     It is preferable that a repairing process, in which a pull-up trace of the rotary tool is repaired by filling the pull-up trace with weld metal, the pull-up trace remaining on the front surface of the sealing body, is performed. 
     According to the method for manufacturing a liquid-cooling jacket, the pull-up trace of the rotary tool disappears, namely, the front surface of the liquid-cooling jacket can be finished flatly. 
     It is preferable that in the primary joining process, a cooling plate is provided on the bottom part of the jacket body, and friction stir welding is performed while cooling the jacket body and the sealing body. 
     According to the method for manufacturing a liquid-cooling jacket, since frictional heat can be suppressed low, the deformation of the liquid-cooling jacket due to thermal contraction can be reduced. 
     It is preferable that a cooling path of the cooling plate, along which a cooling medium flows, has a plane shape at least along a moving locus of the rotary tool. 
     According to the method for manufacturing a liquid-cooling jacket, since a portion to which friction stirring is performed can be cooled intensively, cooling efficiency can be improved. 
     It is preferable that a cooling path of the cooling plate, along which a cooling medium flows, is composed of a cooling pipe embedded in the cooling plate. 
     According to the method for manufacturing a liquid-cooling jacket, management of the cooling medium is easy. 
     It is preferable that in the primary joining process, friction stir welding is performed while letting a cooling medium flow in an inside of the jacket body to cool the jacket body and the sealing body. 
     According to the method for manufacturing a liquid-cooling jacket, since frictional heat can be suppressed low, the deformation of the liquid-cooling jacket due to thermal contraction can be reduced. Still more, cooling can be done with the use of the jacket body itself without any cooling plate or the like. 
     It is preferable that a plurality of fins are provided on at least either the bottom part of the jacket body or the back surface of the sealing body. 
     According to the method for manufacturing a liquid-cooling jacket, a liquid-cooling jacket having high cooling efficiency can be manufactured. 
     Effect of the Invention 
     According to the method for manufacturing a liquid-cooling jacket according to the present invention, a recessed groove to be generated on the joined surface can be made small and the roughness of the joined surface can be made small. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG.  1    is an exploded perspective view showing a liquid-cooling jacket according to a first embodiment of the present invention; 
         FIG.  2    is a cross sectional view showing an overlapping process of a method for manufacturing the liquid-cooling jacket according to the first embodiment of the present invention; 
         FIG.  3    is a side view showing a rotary tool; 
         FIG.  4    is an enlarged cross sectional view of the rotary tool; 
         FIG.  5    is a plan view showing a primary joining process of the method for manufacturing the liquid-cooling jacket according to the first embodiment of the present invention; 
         FIG.  6    is a cross sectional view taken along the line VI-VI of  FIG.  5   ; 
         FIG.  7    is a plan view showing the primary joining process of the method for manufacturing the liquid-cooling jacket according to the first embodiment of the present invention; 
         FIG.  8    is a perspective view showing the liquid-cooling jacket according to the first embodiment of the present invention; 
         FIG.  9    is a cross sectional view taken along the line IX-IX of  FIG.  8   ; 
         FIG.  10    is a schematic view showing a conventional rotary tool; 
         FIG.  11    is a schematic view showing a conventional rotary tool; 
         FIG.  12    is a perspective view showing a modified example of the method for manufacturing the liquid-cooling jacket according to the first embodiment; 
         FIG.  13    is an exploded perspective view showing a liquid-cooling jacket according to a second embodiment of the present invention; 
         FIG.  14    is a longitudinal cross sectional view showing a primary joining process of a method for manufacturing the liquid-cooling jacket according to the second embodiment of the present invention; 
         FIG.  15    is a perspective view showing the liquid-cooling jacket according to the second embodiment of the present invention; and 
         FIG.  16    is an exploded perspective view showing a liquid-cooling jacket according to a third embodiment of the present invention. 
     
    
    
     MODE FOR CARRYING OUT THE INVENTION 
     First Embodiment 
     As shown in  FIG.  1   , a first embodiment of the present invention is a method for manufacturing a liquid-cooling jacket  1  in a hollow part of which heat transport fluid flows, the hollow part being defined by a jacket body  2  and a sealing body  3 . Note that, “a front surface” in the following description means a surface opposite to “a back surface”. 
     First, structures of the jacket body  2  and the sealing body  3  will be explained. The jacket body  2  is a box-shaped body opening upward. The jacket body  2  is formed by including a bottom part  10 , a frame-like peripheral wall part  11  standing on the periphery of the bottom part  10 , and a support part  12 . The jacket body  2  is made of metal appropriately selected from among metals, to which friction stirring is capable of being performed, such as aluminum, an aluminum alloy, copper, a copper alloy, titanium, a titanium alloy, magnesium, a magnesium alloy. For example, an aluminum alloy casting material (for example, JIS ADC12 or the like) forged by die-casting may be used. The peripheral wall part  11  is composed of wall parts  11 A,  11 B,  11 C,  11 D which each have the same plate thickness. The wall parts  11 A,  11 B are short side parts facing each other. The wall parts  11 C,  11 D are long side parts facing each other. In the space surrounded by the bottom wall part  10  and the peripheral wall part  11 , a recessed part  13  is formed. 
     The support part  12  stands on the bottom part  10  and has a shape of a rectangular parallelepiped. And the support part  12  is continuous with the wall part  11 B and extended toward the wall part  11 A. There is a prescribed distance between a front end of the support part  12  and the wall part  11 A facing the wall part  11 B. An end surface  12   a  of the support part  12  and an end surface  11   a  of the peripheral wall part  11  are flush with each other. 
     The sealing body  3  is a plate-like member having a rectangular shape in a plan view. Sizes of length and width of the sealing body  3  in a plan view are a bit smaller than sizes of length and width of the jacket body  2  in a plan view. The sealing body  3  is made of metal appropriately selected from among metals, to which friction stirring is capable of being performed, such as aluminum, an aluminum alloy, copper, a copper alloy, titanium, a titanium alloy, magnesium, a magnesium alloy. For example, an aluminum alloy material (for example, JIS A6063 or the like) made by extrusion may be used. 
     Next, a method for manufacturing the liquid-cooling jacket according to the first embodiment of the present invention will be explained. In the method for manufacturing the liquid-cooling jacket, a preparation process, an overlapping process, a fixing process, a provisional joining process, a primary joining process, and a deburring process are performed. 
     The preparation process is a process to prepare the jacket body  2  and the sealing body  3  shown in  FIG.  1   . 
     As shown in  FIG.  2   , the overlapping process is a process in which the sealing body  3  is put on the jacket body  2 . That is, with a back surface  3   a  of the sealing body  3  facing the underside and a front surface  3   b  thereof facing the upper side, the sealing body  3  is put on the jacket body  2 . Thus, a first overlapped part H 1  is formed by overlapping the back surface  3   a  of the sealing body  3  and the end surface  11   a  of the peripheral wall part  11  each other. The first overlapped part H 1  has a rectangular frame shape in a plan view. Furthermore, a second overlapped part H 2  is formed by overlapping the back surface  3   a  of the sealing body  3  and the end surface  12   a  of the support part  12  each other. The second overlapped part H 2  is straight. 
     The fixing process is a process in which the jacket body  2  and the sealing body  3  are fixed to a fixing member (not shown) such as a table. The jacket body  2  and the sealing body  3  are fastened to a table or the like not to move by means of a fixture such as a clamp. 
     The provisional joining process is a process in which the jacket body  2  and the sealing body  3  are provisionally joined. The provisional joining process can be performed by performing spot joining to the first overlapped part H 1  at an inner corner defined by the end surface  11   a  and a side surface of the sealing body  3 . The spot joining may be performed by friction stirring or welding. Furthermore, the provisional joining process can be omitted. 
     The primary joining process is a process in which the jacket body  2  and the sealing body  3  are joined together by friction stirring with the use of a rotary tool FD shown in  FIG.  3   . At first, the rotary tool FD to be used in the primary joining process will be explained. As shown in  FIG.  3   , the rotary tool FD is a tool to be used in friction stir welding. The rotary tool FD is made of, for example, tool steel. The rotary tool FD is mainly composed of a base shaft F 2 , a base side pin F 3 , and a tip side pin F 4 . The tip side pin F 4  is provided with a projection F 6  projecting at a flat surface F 5  of the tip side pin. The base shaft F 2  has a cylindrical shape and is a part to be connected to a spindle of a friction stir welding device. The flat surface F 5  of the tip side pin F 4  is perpendicular to the rotational axis. 
     The base side pin F 3  is continuous with the base shaft F 2 , and has a shape becoming smaller toward a tip thereof. The base side pin F 3  has a circular truncated cone shape. The taper angle A of the base side pin F 3  may be appropriately set, and is, for example, 135 to 160 degrees. In a case where the taper angle A is less than 135 degrees, or more than 160 degrees, the roughness of a joined surface after performing of friction stirring is large. The taper angle A is larger than a taper angle B of the tip side pin F 4  to be described later. As shown in  FIG.  4   , a step part  110  like stairs is formed on the outer peripheral surface of the base side pin F 3  over the whole in a height direction. The step part  110  is spirally formed in a clockwise direction or a counterclockwise direction. That is, the step part  110  is spiral in a plan view, and like stairs in a side view. In this embodiment, since the rotary tool is rotated clockwise, the step part  110  is set counterclockwise from the base side toward the tip side. 
     Note that, in a case where the rotary tool is rotated counterclockwise, it is preferable that the step part  110  is formed clockwise from the base side toward the tip side. Thereby, plastically fluidized metal is led toward the tip side via the step part  110 , so that the amount of metal to leak to the outside of the metal members to be joined together can be reduced. The step part  110  is composed of step bottom surfaces  110   a  and step side surfaces  110   b . The distance X 1  (horizontal distance) between both apexes  110   c ,  110   c  of the step part  110  adjacent to each other is appropriately set according to a step angle C to be described later and the height Y 1  of the step side surface  110   b.    
     The height Y 1  of the step side surface  110   b  may be appropriately set and is set to, for example, 0.1 to 0.4 mm. In a case where the height Y 1  is less than 0.1 mm, the roughness of the joined surface is made large. On the other hand, in a case where the height Y 1  is larger than 0.4 mm, the roughness of the joined surface tends to is made large and the number of effective steps (the number of the step part  110  being in contact with the metal members to be joined together) also decreases. 
     The step angle C defined by the step bottom surface  110   a  and the step side surface  110   b  may be appropriately set. The step angle C is set to, for example, 85 to 120 degrees. The step bottom surface  110   a  is parallel with a horizontal plane in this embodiment. The step bottom surface  110   a  may be slanted within the range of −5 degrees to 15 degrees relative to a horizontal plane from the rotational axis of the tool toward the outer periphery (a minus sign means being downward relative to a horizontal plane, and a plus sign means being upward relative to a horizontal plane). The distance X 1 , the height Y 1  of the step side surface  110   b , the step angle C, and the angle of the step bottom  110   a  relative to a horizontal plane are appropriately set so that plastically fluidized material can flow out to the outside without staying in nor adhering to the inside of the step part  110 , and the step bottom surface  110   a  can hold the plastically fluidized material to lower the roughness of the joined surface when friction stirring is performed. 
     The tip side pin F 4  is formed continuously with the base side pin F 3 . The tip side pin F 4  has a circular truncated cone shape. The tip side pin F 4  has the flat surface F 5  at the tip thereof. The flat surface F 5  is perpendicular to the rotational axis of the rotary tool FD. The tapered angle B of the tip side pin F 4  is smaller than the tapered angle A of the base side pin F 3 . A spiral groove  111  is formed on the outer peripheral surface of the tip side pin F 4 . The spiral direction of the spiral groove  111  may be either clockwise or counterclockwise. In this embodiment, since the rotary tool FD is rotated clockwise, the spiral groove is formed counterclockwise from the base side toward the tip side. 
     Note that, in a case where the rotary tool is rotated counterclockwise, it is preferable that the spiral groove  111  is formed clockwise from the base side toward the tip side. Thereby, plastically fluidized material is led to the tip side via the spiral groove  111 . Therefore, metal which leaks outside the metal members to be joined can be reduced. The spiral groove  111  is composed of a spiral bottom surface  111   a  and a spiral side surface  111   b . The distance (distance in a horizontal direction) between adjacent apexes  111   c ,  111   c  of the spiral groove  111  is set to be a length X 2 . The height of the spiral side surface  111   b  is set to be a height Y 2 . The spiral angle D defined by the spiral bottom surface  111   a  and the spiral side surface  111   b  is set to, for example, 45 to 90 degrees. The spiral groove  111  comes into contact with the metal members to be joined together to increase frictional heat and has a role to lead plastically fluidized material toward the tip side. 
     As shown in  FIG.  3   , the projection F 6  is projected on the central area of the flat surface F 5  coaxially with the base shaft F 2 . The shape of the projection F 6  is not limited. In this embodiment, the projection F 6  has a cylindrical shape. A spiral groove may be formed on the side surface of the projection F 6 . 
     The primary joining process of this embodiment includes a second overlapped part joining process in which friction stir welding is performed to the second overlapped part H 2  and a first overlapped part joining process in which friction stir welding is performed to the first overlapped part H 1 . The primary joining process will be explained with the use of  FIGS.  5  to  8   . 
     As shown in  FIG.  5   , in the second overlapped part joining process, the tip side pin F 4  of the rotary tool FD being rotated clockwise is inserted in the front surface  3   b  of the sealing body  3  at a start position s 1  which is set at a position corresponding to a front end portion of the support part  12  (front end on the wall part  11 A side). In the second overlapped part joining process, as shown in  FIG.  6   , friction stir welding is performed in a state where the base side pin F 3  and the tip side pin F 4  are in contact with the sealing body  3 . The insertion depth of the rotary tool FD is set so that at least a portion of the base side pin F 3  comes into contact with the front surface  3   b  of the sealing body  3 . That is, friction stir welding is performed while the outer peripheral surface of the base side pin F 3  of the rotary tool FD is holding the front surface  3   b  of the sealing body  3 . The insertion depth of the rotary tool FD is set so that the flat surface F 5  of the tip side pin F 4  is located at a position upper than the second overlapped part H 2  (end surface  12   a  of the support part  12 ) and a tip surface F 7  of the projection F 6  is located at a position lower than the second overlapped part H 2  (end surface  12   a  of the support part  12 ). In other words, the insertion depth of the rotary tool FD is set so that the flat surface F 5  of the tip side pin F 4  is brought in contact with only the sealing body  3  and the second overlapped part H 2  is located at the side surface of the projection F 6 . And the rotary tool FD is moved along the second overlapped part H 2  while being kept at a constant height. Namely, the rotary tool FD is moved in the longitudinal direction of the support part  12 . In the second overlapped part joining process, the back surface  3   a  of the sealing body  3  and the end surface  12   a  of the support part  12  are joined together by friction stirring. Plasticized region W is generated along a moving locus of the rotary tool FD. 
     After the rotary tool FD is moved up to a first middle point s 2  which is set in the first overlapped part H 1 , the rotary tool FD is transferred to the first overlapped part joining process as it is without being pulled up. As shown in  FIG.  7   , in the first overlapped part joining process, the rotary tool FD is moved along the first overlapped part H 1 . That is, the rotary tool FD is moved once around the recessed part  13  along the peripheral wall part  11  clockwise as shown by arrows. 
     In the first overlapped part joining process, similarly to the second overlapped part joining process, friction stir welding is performed in a state where the base side pin F 3  and the tip side pin F 4  are in contact with the sealing body  3 . An insertion depth of the rotary tool FD is also set similarly to the second overlapped part joining process so that at least a portion of the base side pin F 3  comes into contact with the front surface  3   b  of the sealing body  3 . That is, friction stir welding is performed while the outer peripheral surface of the base side pin F 3  of the rotary tool FD is holding the front surface  3   b  of the sealing body  3 . An insertion depth of the rotary tool FD is set so that the flat surface F 5  of the tip side pin F 4  is located at a position upper than the first overlapped part H 1  (end surface  11   a  of the peripheral wall part  11 ) and the tip surface F 7  of the projection F 6  is located at a position lower than the first overlapped part H 1  (end surface  11   a  of the peripheral wall part  11 ). In other words, the insertion depth of the rotary tool FD is set so that the flat surface F 5  of the tip side pin F 4  is brought in contact with only the sealing body  3  and the first overlapped part H 1  is located at the side surface of the projection F 6 . And the rotary tool FD is moved along the first overlapped part H 1  while being kept at a constant height. 
     Note that, the insertion depth of the rotary tool FD need not necessarily be kept constant. For example, the insertion depth may be changed between the first overlapped part joining process and the second overlapped part joining process. Since the rotary tool FD is not provided with a shoulder part, the insertion depth can be easily changed. 
     In the primary joining process, it is desired that joining conditions are set so that burrs are generated at a position having a distance from the recessed part  13 . A position at which burrs are generated varies according to the joining conditions. The joining conditions are determined by each element of a rotational speed of the rotary tool FD, a rotational direction of the rotary tool FD, a movement speed (feed speed) of the rotary tool FD, an advancing direction of the rotary tool FD, an inclination angle (tapered angle) of the base side pin F 3  or the tip side pin F 4 , materials of metal members (the jacket body  2  and the sealing body  3 ) to be joined together, thicknesses of the metal members to be joined together, and so on, and a combination of these elements. 
     For example, in a case where the rotational speed of the rotary tool FD is low, the temperature of plastically fluidized material on a shear side easily becomes higher than that on a flow side. The flow side is a retreating side, that is, a side that the movement speed of the rotary tool FD is subtracted from the tangential speed of the outer surface of the rotary tool FD. The shear side is an advancing side, that is, a side that the movement speed of the rotary tool FD is added to the tangential speed of the outer surface of the rotary tool FD. Therefore, a lot of burrs tend to be generated on the shear side at a position which is outside the plasticized region. On the other hand, for example, in a case where the rotational speed of the rotary tool FD is high, the temperature of the plastically fluidized material on the shear side rises more, but a lot of burrs tend to be generated on the flow side at a position which is outside the plasticized region as much as the rotational speed is high. 
     In this embodiment, since the rotational speed of the rotary tool FD is set to be low, in the friction stir welding to the first overlapped part H 1 , a lot of burrs tend to be generated at a position having a distance from the recessed part  13 , the position being on the shear side and outside the plasticized region W. Note that, joining conditions of the rotary tool FD are not limited to those already explained, and can be appropriately set. 
     Thus, in a case where joining conditions are set so that burrs or a lot of burrs are generated at a position having a distance from the recessed part  13 , burrs can be concentrated to a position having a distance from the recessed part  13 . Therefore, that is preferable since a deburring process to be described later can be easily performed. 
     As shown in  FIG.  7   , after the rotary tool FD is moved by one round along the first overlapped part H 1  as shown by arrows, it is moved via the first middle point s 2  up to a second middle point s 3  as it is. Then, the rotary tool FD is moved up to an end point e 1  which is set to be an outer position than the second middle point s 3  within the front surface  3   b  of the sealing body  3 . And then, the rotary tool FD is pulled upward to be removed from the sealing body  3 . 
     After the rotary tool FD is removed from the sealing body  3 , in a case where there remains a pull-up trace on the front surface  3   b , a repairing process in which the pull-up trace is repaired may be performed. In the repairing process, for example, the pull-up trace can be repaired by performing build-up welding to fill the pull-up trace with weld metal. Thereby, the front surface  3   b  can be made flat. 
     The deburring process is a process in which burrs exposed on the front surface  3   b  of the sealing body  3  by performing the primary joining process are removed. In the deburring process, burrs are removed by using a cutting tool or the like. Thereby, the front surface  3   b  of the sealing body  3  can be finely finished. 
     By way of the above processes, the liquid-cooling jacket  1  shown in  FIGS.  8 ,  9    is manufactured. 
     As shown in  FIGS.  8 ,  9   , the liquid-cooling jacket  1  is manufactured by performing friction stirring to the jacket body  2  and the sealing body  3  to integrate them. Regarding the liquid-cooling jacket  1 , the first overlapped part H 1  where the back surface  3   a  of the sealing body  3  and the end surface  11   a  of the peripheral wall part  11  overlap with each other and the second overlapped part H 2  where the back surface  3   a  of the sealing body  3  and the end surface  12   a  of the support part  12  overlap with each other are continuously joined by friction stirring. The plasticized region W is generated in a portion to which friction stirring is performed. Inside the liquid-cooling jacket  1 , the hollow part  14 , in which heat transport fluid that transports heat to the outside flows, is formed. 
     As shown in  FIG.  10   , a conventional rotary tool  900  does not hold a surface (or surfaces) of metal members  910  to be joined together with the use of a shoulder part. Therefore, there are problems that a recessed groove, which is a groove formed by the surface of the plasticized region and the surface of the metal members to be joined together, is large and the roughness of the joined surface is large. Furthermore, there is a problem that an expanded part (a part of the surface of the metal members to be joined together, the part being expanded relative to the original surface before the joining) is generated beside the recessed groove. On the other hand, like a rotary tool  901  in  FIG.  11   , in a case where a tapered angle β of the rotary tool  901  is larger than the tapered angle α of the rotary tool  900 , the surface of the metal members to be joined together can be held in comparison with the case of the rotary tool  900 . Hence, the recessed groove is made small and the expanded part is also made small. However, since downward flowing of the plastically fluidized material is made strong, a kissing bond is easily generated in a lower portion of the plasticized region. 
     In contrast, the rotary tool FD of this embodiment is provided with the base side pin F 3  and the tip side pin F 4  having the tapered angle smaller than the tapered angle A of the base side pin F 3 . Therefore, the rotary tool FD is easily inserted in the sealing body  3 . Furthermore, since the tapered angle B of the tip side pin F 4  is small, the rotary tool FD can be easily inserted to a deep position of the sealing body  3 . And further, since the tapered angle B of the tip side pin F 4  is small, the downward flowing of the plastically fluidized material can be reduced in comparison with the rotary tool  901 . Hence, the kissing bond can be prevented from being generated in a lower portion of the plasticized region W. On the other hand, since the tapered angle A of the base side pin F 3  is large, joining can be stably performed in comparison with a conventional rotary tool even in a case where the thickness of metal members to be joined together or the height position of the joining changes. 
     Still more, since plastically fluidized material can be held by the outer peripheral surface of the base side pin F 3 , a recessed groove generated on the joined surface can be made small, and an expanded part to be generated beside the recessed groove can be excluded or can be made small. Furthermore, since the stair-like step part  110  is shallow and the exit is wide, plastically fluidized material easily flows out to the outside of the step part  110  while being held by the step bottom surface  110   a . Therefore, though the base side pin F 3  holds plastically fluidized material, the plastically fluidized material is hard to adhere to the outer peripheral surface of the base side pin F 3 . Accordingly, the roughness of the joined surface can be made small, and the joining quality can be suitably made stable. 
     Since the tip side pin F 4  of the rotary tool FD has the flat surface F 5 , in the second overlapped part joining process and the first overlapped part joining process, plastically fluidized material whirled up around the projection F 6  can be held by the flat surface F 5 . Thereby, friction stirring around the projection F 6  can be more surely performed, and oxide films of the second overlapped part H 2  and the first overlapped part H 1  can be surely divided. Therefore, the joining strength of the first overlapped part H 1  and that of the second overlapped part H 2  can be enhanced. 
     Furthermore, in a case where only the projection F 6  is set to be inserted more deeply than the first overlapped part H 1  and the second overlapped part H 2 , the width of the plasticized region W due to friction stirring can be made smaller in comparison with a case where the flat surface F 5  of the tip side pin F 4  is inserted more deeply than the first overlapped part H 1  and the second overlapped part H 2 . Thereby, the plastically fluidized material can be prevented from flowing into the recessed part  13  of the jacket body  2 . 
     Furthermore, since the support part  12  which comes into contact with the sealing body  3  is provided on the bottom part  10  of the jacket body  2 , the strength of the liquid-cooling jacket  1  can be enhanced by the support part  12 . Note that, the support part  12  can be provided on the back surface  3   a  of the sealing body  3 . 
     Note that, friction stir welding need not be performed to the second overlapped part H 2 . However, in a case where friction stir welding is performed also to the second overlapped part H 2  similarly to this embodiment, joining strength between the jacket body  2  and the sealing body  3  can be more enhanced. 
     Still further, the support part  12  is formed continuously with the peripheral wall part  11 , and in the primary joining process, friction stir welding is continuously performed to the first overlapped part H 1  and to the second overlapped part H 2 . Thanks to that, the liquid-cooling jacket  1  having high deformation-resistance can be manufactured, and a production cycle can be improved. 
     Furthermore, in a case where the rotary tool FD is moved inward from the plasticized region W and is pulled up from that position after finishing friction stir welding to the first overlapped part H 1  and the second overlapped part H 2 , there is a risk that metal material flows into the inside from the second overlapped part H 2  and the first overlapped part H 1  formed by the peripheral wall part  11  and the sealing body  3 . However, in the primary joining process, such a problem can be resolved by pulling up the rotary tool FD from the position to which the rotary tool FD has been moved outward from the plasticized region W. 
     Still further, in a case where the repairing process, in which weld metal is buried in the pull-up trace of the rotary tool FD, the pull-up trace remaining on the front surface  3   b  of the sealing body  3 , is performed to repair the trace, the pull-up trace due to the rotary tool FD disappears, so that the surface of the liquid-cooling jacket  1  can be finished flatly. 
     Modified Example of First Embodiment 
     In the following modified example of the first embodiment and other embodiments, description of technical matters common to the first embodiment is omitted, and different matters will be mainly described. Furthermore, each member similar to that in the case of the first embodiment has the same symbol and will not be described. 
     Next, a modified example of the method for manufacturing the liquid-cooling jacket according to the first embodiment will be described. As shown in  FIG.  12   , the modified example differs from the first embodiment on the point that the provisional joining process and the primary joining process are performed with the use of a cooling plate. 
     As shown in  FIG.  12   , in the modified example, when the fixing process mentioned in the above is performed, the jacket body  2  and the sealing body  3  are fixed to a table K. The table K is composed of a base plate K 1  having a rectangular parallelepiped shape, clamps K 3  provided at four corners of the base plate K 1 , and a cooling pipe WP provided inside the base plate K 1 . The table K holds the jacket body  2  so as not to be moved and is a member to function as “a cooling plate” of the present invention. 
     The cooling pipe WP is a tubular member embedded inside the base plate K 1 . A cooling medium for cooling the base plate K 1  flows in the cooling pipe WP. A position of the cooling pipe WP to be disposed, that is, a shape of the cooling path along which the cooling medium flows is not limited in particular. In this modified example, it is a plane shape along the moving locus of the rotary tool FD in the first overlapped part joining process. Namely, the cooling pipe WP is disposed so that the cooling pipe WP and the first overlapped part H 1  nearly overlap with each other in a plan view. 
     In the provisional joining process and the primary joining process of the modified example, after the jacket body  2  and the sealing body  3  are fixed to the table K, friction stir welding is performed while letting the cooling medium flow in the cooling pipe WP. Thereby, since frictional heat at the time of performing friction stirring can be reduced, the deformation of the liquid-cooling jacket  1  due to thermal contraction can be reduced. Furthermore, in the modified example, since the cooling path and the first overlapped part H 1  (the moving locus of the rotary tool FD) overlap with each other in a plan view, a portion where frictional heat is generated can be cooled intensively. Thereby, cooling efficiency can be improved. Still further, since the cooling medium is let to flow in the disposed cooling pipe WP, management of the cooling medium is easy. Furthermore, since the table K (cooling plate) and the jacket body  2  come into contact with each other face to face, cooling efficiency can be improved. 
     Note that, the cooling pipe WP may be provided at a position corresponding to the second overlapped part H 2 . Furthermore, friction stir welding may be performed while letting the cooling medium flow also in the inside of the jacket body  2  together with the state where the jacket body  2  and the sealing body  3  are cooled with the use of the table K (cooling plate). In this way, frictional heat can be reduced, so that the deformation of the liquid-cooling jacket  1  due to thermal contraction can be reduced. Still further, in a case where friction stir welding is performed while letting the cooling medium flow only in the inside of the jacket body  2 , the liquid-cooling jacket can be cooled with the use of the jacket body  2  itself without any cooling plate or the like. 
     Second Embodiment 
     Next, a method for manufacturing a liquid-cooling jacket according to a second embodiment of the present invention will be described. As shown in  FIG.  13   , the first one of differences between the second embodiment and the first embodiment is that three projection parts  17  are formed apart from each other on the end surface  12   a  of the support part  12 . The shape of each projection part  17  is not limited in particular, and in this embodiment, each has a cylindrical shape. Furthermore, the number of the projection parts  17  is not limited in particular, and in this embodiment, the three are arranged in the longitudinal direction of the support part  12 . Still further, three hole parts  3   c , each of which has a circular shape in a plan view and passes through the sealing body  3  in the thickness direction thereof, are formed in the sealing body  3 . Each hole part  3   c  is a hole part in which one projection part  17  is inserted and is formed at a position corresponding to the one projection part  17 . Each hole part  3   c  has such a size that the one projection part  17  is inserted in almost without a gap. 
     In the second embodiment, in an overlapping process, each projection part  17  is inserted in the corresponding hole part  3   c  of the sealing body  3 , so that a butting part U, which is formed by the hole wall surface of a hole part  3   c  and the side surface of the projection part  17 , is formed. 
     And then, as shown in  FIG.  14   , in a primary joining process, three butting parts U are each joined by friction stirring as a second overlapped part joining process. Since each butting part U has a circular shape in a plan view, the rotary tool FD is moved along each butting part U so as to draw a circle in a plan view. As to friction stir welding to each butting part U, the insertion depth of the rotary tool FD is set so that at least a portion of the base side pin F 3  comes into contact with the front surface  3   b  of the sealing body  3  and a front surface  17   b  of a projection part  17 . That is, friction stir welding is performed while the front surface  3   b  of the sealing body  3  and the front surface  17   b  of a projection part  17  are being held by the outer peripheral surface of the base side pin F 3  of the rotary tool FD. Furthermore, the insertion depth of the rotary tool FD is set so that the flat surface F 5  of the tip side pin F 4  is located at a position upper than the second overlapped part H 2  (end surface  12   a  of the support part  12 ), and the tip surface F 7  of the projection F 6  is located at a position lower than the second overlapped part H 2  (end surface  12   a  of the support part  12 ). Namely, the insertion depth of the rotary tool FD is set so that the flat surface F 5  of the tip side pin F 4  is brought in contact with both of the sealing body  3  and the projection part  17 , and the second overlapped part H 2  is located at the side surface of the projection F 6 . As apparently from the above description, the first overlapped part joining process and the second overlapped part joining process are not continuously performed. 
       FIG.  15    is a perspective view of the liquid-cooling jacket  1  finished via all processes in the second embodiment. The plasticized region W is generated by performing the first overlapped part joining process along the outer periphery of the sealing body  3  by one round in a plan view. Furthermore, the three circular plasticized regions W arranged on the support part  12  in the longitudinal direction thereof in a plan view are also generated by performing the second overlapped part joining process. 
     Advantageous effects roughly equivalent to the first embodiment can work also by the method for manufacturing a liquid-cooling jacket according to the second embodiment described in the above. 
     Still further, according to this embodiment, in the primary joining process, friction stir welding can be performed also to the butting part U where the hole wall of a hole part  3   c  and the side surface of the projection part  17  are butted each other. Therefore, the joining strength between the jacket body  2  and the sealing body  3  can be enhanced. 
     Third Embodiment 
     Next, a method for manufacturing a liquid-cooling jacket according to a third embodiment of the present invention will be described. The third embodiment differs from the first embodiment on the point that fins  31  are provided on the sealing body  3  as shown in  FIG.  16   . That is, a plurality of fins  31  are provided on the back surface  3   a  of the sealing body  3 . The jacket body  2  has the same structure as that of the first embodiment. 
     The plurality of fins  31  are hung vertically from the back surface  3   a  of the sealing body  3  with a prescribed distance between adjacent two among them. Each fin  31  is provided on the back surface  3   a  of the sealing body  3  so that the fin  31  is housed in the recessed part  13  of the jacket body  2  without interfering with the support part  12  when an overlapping process is performed. Except using the sealing body  3  provided with the fins  31 , each process of the first embodiment is similar to that of the third embodiment. 
     According to the method for manufacturing a liquid-cooling jacket according to the third embodiment, the liquid-cooling jacket  1  provided with the plurality of fins  31  can be manufactured. Since the liquid-cooling jacket  1  is provided with the fins  31 , cooling efficiency can be improved. Note that, the fins  31  may be provided on the bottom part  10  side of the jacket body  2 . 
     Explanations are done on the embodiments of the present invention in the above. Design changes can be appropriately done within the range of the purpose of the present invention. 
     DESCRIPTION OF THE SYMBOLS 
     
         
           1  Liquid-cooling jacket 
           2  Jacket body 
           3  Sealing body 
           3   a  Back surface 
           10  Bottom part 
           11  Peripheral wall part 
           11   a  End surface 
           11 A Another wall part 
           11 B One wall part 
           12  Support part 
           13  Recessed part 
           14  Hollow part 
           31  Fin 
         e 1  End point (Outside) 
         FD Rotary tool 
         F 2  Base shaft 
         F 3  Base side pin 
         F 4  Tip side pin 
         F 5  Flat surface 
         F 6  Projection 
         F 7  Tip surface 
           110  Step part 
           110   a  Step bottom surface 
           110   b  Step side surface 
           111  Spiral groove 
         A Tapered angle (of the base side pin) 
         B Tapered angle 
         C Step angle 
         D Spiral angle 
         X 1  Distance (in the base side pin) 
         X 2  Distance 
         Y 1  Height (of the step side surface) 
         Y 2  Height 
         H 1  First overlapped part 
         H 2  Second overlapped part 
         U Butting part 
         W Plasticized region 
         K Table (Cooling plate) 
         WP Cooling path, Cooling pipe