Patent Publication Number: US-3880910-A

Title: 3,5-Dialkylbenzoyloxy-3{40 -5{40 -dialicylbenzamides

Description:
United States Patent [191 Spivack et a].  
 [ 1 3,5-DIALKYLBENZOYLOXY-3 &#39;-5 DIALICYLBENZAMIDES [75] Inventors: John D. Spivack, Spring Valley;  
 John J. Luzzi, Carmel, both of NY.  
 [73] Assignee: Ciba-Geigy Corporation, Ardsley,  
 [22] Filed: Dec. 26, 1972 [21] Appl. No.: 318,325  
 [52] US. Cl. 260/473 S; 44/70; 99/163; 252/407 [51] Int. C1 C07C 103/30; C07c 103/88 [58] Field of Search 260/473 S, 559 R, 45.85  
 [56] References Cited UNITED STATES PATENTS 3,112,338 11/1963 Smutny et al 260/473 S 3,206,431 9/1965 Doyle et a1 260/4585 R 3,285,855 11/1966 Dexter et 260/473 S 3,330,859 7/1967 Dexter et al. 260/473 S 3,502,613 3/1970 Berger 260/458 NT 3,646,l 10 2/1972 Eggcnsperger 260/473 S 3,714,122 1/1973 Kline 260/559 R R27,004 12/1970 Meier et a1. 260/473 S Primary Examiner-John F. Terapane Attorney, Agent, or FirmNestor W. Shust Apr. 29, 1975 [57] ABSTRACT Benzoyloxybenzamides having the formula wherein R and R are lower alkyl or cycloalkyl, R and R are hydrogen, lower alkyl or cycloalkyl, R is hydrogen or alkyl, R is alkyl when n is l and alkylene when n is 2 or greater are useful as stabilizers of organic materials such as polyolefins.  
 9 Claims, N0 Drawings 3,5-DIALKYLBENZOYLOXY-3&#39; -5 DIALICYLBENZAMIDES BACKGROUND OF THE INVENTION Polymeric materials have one important deficiency which must be overcome before they can be used in various commercial applications. This deficiency is the susceptibility to oxidative and actinic degradation. Many varieties of compounds have been known to be useful as stabilizers of various polymers, but all of them have certain deficiencies which limits the usefulness of such stabilizers. Thus, one class of stabilizers disclosed in the prior art that is related to the compounds of this invention is hindered hydroxybenzoates disclosed in U.S. Pat. Nos. 3,029,276; 3,112,338; 3,206,431 and 3,502,613.  
  Most of the compounds disclosed in said patents are various esters of 3,5-dialkyl-4-hydroxybenzoic acids while this invention deals with 4-(3,5-dialkyl-4-hydroxybenzoyloxy)-mono or dialkylbenzamides. Other differences are that the phenyl ring in the benzoate ring is completely unsubstituted while the corresponding group in the compounds of this invention has at least one alkyl substituent.  
  The compounds of this invention have many advantages over the prior art compounds. The instant compounds have improved thermal stability. This feature is important because the polymer substrates are subjected to high temperature processing during manufacturing stages. Furthermore, the compounds of this invention have better gas fading properties and have better aqueous and organic solvent extraction resistance than the prior art compounds.  
 DETAILED DISCLOSURE This invention relates to hindered benzoyloxybenzamide compounds and organic compositions stabilized therewith. More specifically, these compounds are useful as stabilizers of organic materials which are subject to thermal, oxidative and ultraviolet light degradation, The novel benzoyloxybenzamide compounds can be represented by the formula I l 6 no 6- R &#39;5 R2 R4 n wherein R and R are (lower)alkyl or (lower) cycloalkyl groups,  
 R, R and R are independently hydrogen, (lower)alkyl or (lower)cycloalkyl,  
 R is an alkyl group having up to 24 carbon atoms when n is l and alkylene group having up to l0 carbon atoms when n is 2 to 6, and  
 n is an integer l to 6 and preferably l or 2.  
  Each of the groups R, R and R can be the same or different (lower)alkyl groups having from 1 to 8 carbon atoms, namely, n-propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, sec-amyl, tert-amyl, n-hexyl, sec-hexyl, secoctyl, tert-octyl and the like. These groups can also be (lower)cycloalkyl groups having 4 to 8 carbon atoms, such as cyclobutyl, cyclopentyl, cyclohexyl or cyclooctyl groups. The group R can be hydrogen or any of the alkyl or cycloalkyl group discussed above.  
  Although groups R, R&#34;, R and R can be any (lower- )alkyl groups stated above, it is preferable that R and R groups be secondary or tertiary alkyl groups having from 4 to 8 carbon atoms and most preferably tertiary alkyl. Tertiary-butyl group is found to be very effective. The above formula indicates that R and R can be substituted on any of the four open positions in the benzene ring but preferably both groups are ortho to the benzoic acid moiety. The formula also indicates that the group can be bonded to the phenyl ring in either meta or para position in relation to the hindered hydroxybenzoic acid moiety.  
  The group R can be hydrogen, (lower)alkyl or (lower)cycloalkyl discussed above. The group R can be either an alkyl group of up to 24 carbon atoms or an alkylene group of up to 10 carbon atoms. Illustrative examples of alkyl groups are methyl, ethyl, butyl, hexyl, octyl, dodecyl, hexadecyl, octadecyl, eicosyl, tetracosyl and the like. Illustrative examples of alkylene groups are methylene ethylene, propylene, butylene, hexylene, octylene, decylene and the like. Alkylene group of l to 6 carbon atoms is preferred at this time from economical standpoint.  
  Following are illustrative examples of the compounds of this invention:  
  N-n-octadecyl-4-(3,5-di-t-butyl-4- hydroxybenzoyloxy)-3,5-di-t-butylbenzamide N-methyl-N-n-octadecyl-4-(3,5-di-t-butyl-4- hydroxybenzoyloxy)-3,5-dit-butylbenzamide N,N-di-n octyl-4-( 3 ,5-di-t-butyl-4- hydroxybenzoyloxy)-3,5di-t-butylbenzamide N,N-diethyl-4-(3,5-di-t-butyl-4-hydroxybenzoyloxy)- 3,5-dit-butylthiobenzamide N-{( 1,1 ,3,3-tetramethylbutyl)-4-(3,5-di-t-butyl-4- hydroxybenzoyloxy)-3,S-di-t-butylbenzamide} N-ethyl-N-p-tolyl-4-(3,5-di-t-butyl-4- hydroxybenzoyloxy)-3,S-di-t-butylbenzamide N-tetracosyl-4(3,5dimethyl4-hydroxybenzoyloxy)- 3,5-dimethylbenzamide N,N-dicyclooctyl-4-( 3 ,5-di-t-butyl-4- hydroxybenzoyloxy)-3-t-butylbenzamide N-n-octyl-4-( 3 ,5-di-isopropyl-4- hydroxybenzoyloxy)-3,5 -di-isopropylbenzamide N ,N &#39;-hexamethylene-bis-{ 4-(3 ,5-di-t-butyl-4- hydroxybenzoyloxy)-3 ,S-di-t-lbutylbenzamide} The compounds of this invention when R and R are different from R and R can be prepared by reacting a hindered phenolic acid chloride such as 3,5-di-tertbutyl-4-hydroxybenzoyl chloride with an appropriate substituted hydroxybenzamide at a temperature of from about 50 to 200C. Compounds where R and R are the same as R and R can be prepared by reacting two moles of a dialkyl substituted hydroxybenzoyl halide with 1 mole of a base to yield an intermediate compound which is (di-alkyl substituted hydroxybenzoyloxy)-dialkyl benzoyl halide which in turn is reacted with a primary or a secondary amine to give the desired product. The basic materials which can be employed are trialkyl amines such as triethyl amine, tripropyl amine, triisopropyl amine, tributyl amine, triamyl amine, triisopropyl amine, tributyl amine, triamyl amine sodium or potassium hydroxide, sodium or potassium carbonates or other similar proton acceptors. Both reactions mentioned above can be carried out neat in some cases or in a non-reactive solvent such as a hydrocarbon as for example, hexane, cyclohexane, heptarie, non-reactive chlorinated hydrocarbon, mineral oil, and preferably benzene or toluene.  
  The preparation of these compounds is further illustrated in greater detail in the examples below.  
 EXAMPLE 1 Preparation of 4-( 3 ,5 -di-t-butyl-4-hydroxybenzoyl0xy )-3 ,5-di-t- &#39;butylbenzoyl chloride To 445 ml. of a toluene solution containing 107.2 grams of 3,5-di-t-butyl-4-hydroxybenzoyl chloride (0.40 moles) cooled to C was added 24.4 grams (0.24 moles) of triethylamine over a period 20 minutes at 10 to C. The turbid reaction mixture was maintained at room temperature for about 19 hours and then heated at 80C for 1 hour. The precipitate was removed by filtration and washed with a little toluene. The clear filtrate was concentrated in vacuo at 40 to 50C at 20 mm. Hg. pressure and kept at this same temperature for 45 minutes at 20 mm. Hg. pressure to yield 105 grams of residue. The residue was triturated with 200 ml. of warm petroleum ether, and the slurry cooled. The white crystals were filtered yielding 70 grams of the product. After recrystallization from heptane and acetonitrile and drying at 95C for 5 hours at 0.1 mm Hg. pressure the melting point of the product was 2102l3C.  
 EXAMPLE 2 Preparation of N-n-octadecy1-4-( 3 ,5-ditert.butyl-4- hydroxybenzoyloxy)-3 ,5-ditert.butylbenzamide 10.10 grams of 4-( 3 ,5-di-tert.buty1-4- hydroxybenzoyloxy)-3,S-di-tert-butylbenzoyl chloride 5.4 grams of n-octadecylamine and 2.0 grams of triethylamine were heated together in about 100 ml of toluene for about 5 hours at 90 to 98C. The precipitated triethylamine hydrochloride was filtered. The filtrate was washed with water and dried over anhydrous sodium sulfate. The dried toluene solution was concentrated to remove toluene under reduced pressure yielding 14.5 grams of the product. The product was crystallized twice from acetonitrile and melted at 139 to 140C.  
 EXAMPLE 3 Preparation of N-methyl-N-n-octadecyl-4-( 3 ,5-di-tert.butyl-4- hydroxybenzoyloxy )-3 ,S-di-tert-butylbenzamide This compound was made according to the procedure of Example 2, and was isolated as an oil (14.5 grams).  
 EXAMPLE 4 Preparation of N,N-di-n-octyl-4-( 3 ,5 -di-tert-butyl-4- hydroxybenzoyloxy)-3,5-di-tert-butylbenzamide To 4.83 grams of di-n-octylamine and 2.0 grams of triethylamine dissolved in 40 ml of toluene was added dropwise at 35 to 40 over a period of 10 minutes 10.0 grams of 4-(3,5-di-tert-butyl-4-hydroxybenzoyloxy)- 3,S-di-tert-butyl-benzoyl chloride dissolved in 30 ml of toluene. The reaction mixture was stirred at to C for 2 hours. After cooling to room temperature,  
 &#39; the reaction mixture was filtered to remove the precipitated triethylamine hydrochloride. The filtrate was washed with water and dried over anhydrous sodium sulfate. After removal of the toluene by distillation, the product was isolated as white crystals (m.p. 146) by successive crystallization from acetonitrile and isopropanol.  
 EXAMPLE 5 Preparation of N,N-diethyl-4-( 3,5-di-tert-butyl-4- hydroxybenzoyloxy)-3 ,S-di-t-butylbenzamide The compound of this example was made substantially according to the procedure of example 4 and after successive crystallization from methanol and isopropanol yielded the desired product as white crystals melting at 203205C.  
 EXAMPLE 6 Following the procedure of Example 4, dimethylamine and N,N-di-n-butylamine are reacted respectively with 4-(3,5-dimethyl-4-hydroxybenzoyloxy)-3,5- dimethylbenzoyl chloride and 4-(3,5-diisopropyl-4- hydroxybenzoyloxy)-3,5-diisopropylbenzoyl chloride to yield N,N-dimethyl-4-(3,5-dimethyl-4- hydroxybenzoyloxy)-3,5-dimethylbenzamide and N,N- di-n-butyl-4-( 3 ,5-diisopropyl-4-hydroxybenzoyloxy 3,5-diisopropylbenzamide.  
 EXAMPLE 7 Preparation of N-(1,1,3,3-tetramethylbutyl)-4(3,5-di-tert-butyl-4- hydroxybenzoyloxy)-3,S-di-tert-butylbenzamide To 143 ml. of a 0.7 molar solution of 3,5-di-tertbutyl-4-hydroxybenzoyl chloride in toluene 5.05 grams of triethylamine was added dropwise at 10 to 15C over a period of 10 minutes and the reaction mixture stirred at room temperature for 2 hours. An additional 5.05 grams of triethylamine was added followed by the dropwise addition of 6.48 grams of tert-octylamine dissolved in 10 ml. of toluene at 20 to 30C. The reactants were stirred at room temperature for 20 hours. The precipitate triethylamine hydrochloride was filtered and washed with a little toluene the washings being added to the filtrate containing the product. The filtrate was washed successively with water, 2N aqueous hydrochloric acid and again with water, the organic phase being dried over anhydrous sodium sulfate. The toluene solution was concentrated in vacuo to yield the product as a glassy residue. The residue was crystallized successively from heptane and acetonitrile to yield the product as white crystals melting at 2l32 15 C.  
 EXAMPLE 8 Preparation of N-ethyl-N-p-tolyl-4-( 3,5-di-tert-butyl-4- hydroxybenzoyloxy )3 ,5-di-tert-butylbenzamide By substituting N-ethyl-p-toluidine in Example 7 and following basically the above procedure, the subject compound is isolated as white crystals (m.p. 2l4-2l6C) after crystallization successively from acetonitrile and toluene.  
 EXAMPLE 9 Following the procedure of Example 8, n-octylamine is re acted with 4-( 3 ,5-di-t-butyl-4- hydroxybenzoyloxy)-5-t-butylbenzoyl chloride to yield N-n-octyl-4-( 3 ,5-di t-butyl-4-hydroxybenzoyloxy )-5-tbutylbenzamide.  
  The benzoyloxybenzamides of this invention are stabilizers of organic material normally subject to thermal, oxidative or actinic light deterioration. Materials which are thus stabilized include synthetic organic polymeric substances such as vinyl resins formed from the polymerization of vinyl halides or from the copolymerization of vinyl halides with unsaturated polymerizable compounds, e.g., vinyl esters, a,,B-unsaturated ketones, a,B-unsaturated aldehydes and unsaturated hydrocarbons such as butadienes and sytrene; poly-a-olefins such as polyethylene, polypropylene, polybutylene including copolymers of a-olefins; dienes such as polybutadiene, polyisoprene, and the like, including copolymers with other monomers; polyurethanes and polyamides such as polyhexamethylene adipamide and polycaprolactam; polyesters such as polyethylene -terephthalates; polycarbonates; polyacetals such as polyethylene terephthalate polyacetal; polystyrene, polyethyleneoxide; and copolymers such as those of high impact polystyrene containing copolymers of butadiene and styrene and those formed by the copolymerization of acrylonitrile, butadiene and/or styrene.  
  Other materials which can be stabilized by the compounds of the present invention include lubricating oil of the aliphatic ester type, i.e., di( l,2-ethylene)- azelate, pentaerythritol tetracaproate, and the like; animal and vegetable derived oils, e.g., linseed oil, fat, tallow, lard, peanut oil, cod liver oil, castor oil, palm oil, corn oil, cottonseed oil, and the like; hydrocarbon materials such as gasoline, mineral oil, fuel oil, drying oil, cutting fluids, waxes, resins, and the like, salts of fatty acids such as soaps and the like; and alkylene glycols, e.g., B-methoxyethyleneglycol, methoxytriethyleneglycol, triethylene glycol, octaethyleneglycol, dibutyleneglycol, dipropyleneglycol and the like.  
  Of particular importance are polyolefins and especially polypropylene because these benzoyloxybenzoates are particularly effective as UV stabilizers in polypropylene.  
  In general, the stabilizers of this invention are employed from about 0.01 to about percent by weight of the stabilized composition, although this will vary with the particular substrate and application. An advantageous range is from about 0.05 to about 2 percent and especially 0.1 to about 1 percent.  
  For addition to polymeric substrates, the stabilizers can be blended before polymerization or after polymerization, during the usual processing operations, for example, by hot-milling, the composition then being extruded, pressed, or the like into films, fibers, filaments, hollow spheres and the like. The heat stabilizing properties of these compounds advantageously stabilize the polymer against degradation during such processing at the high temperature generally encountered. The stabilizers can also be dissolved in suitable solvents and sprayed on the surface of films, fabrics, filaments or the like to provide effective stabilization.  
  These compounds can also be used in combination with other additives such as antioxidants, sulfurcontaining esters such as distearyl-,B-thiodipropionate (DSTDP), dilauryl-B-thiodipropionate (DLTDP) in an amount of from 0.01 to 2 percent by weight of the organic material, and the like, pourpoint depressants, corrosion and rust inhibitors, dispersing agents, demulsifiers, antifoaming agents, carbon black, accelerators and other chemicals used in rubber compounding, plasticizers, color stabilizers, diand tri-alkyland -alkylphenylphosphites, heat stabilizers, ultraviolet light stabilizers, antiozonants, dyes, pigments, metal chelating agents, dyesites and the like. Often combinations such as these, particularly the sulfur containing esters, the phosphites and/or the ultraviolet light stabilizers will produce superior results in certain applications to those expected by the properties of the individual components.  
  The following formula represents co-stabilizers which are in certain instances very useful in combination with the stabilizers of this invention:  
 wherein R is an alkyl group having from 6 to 24 carbon atoms; and n is an integer from 1 to 6. Especially useful compounds of this type are dilauryl&#39;B-thiodipropionate and distearyl-B-thiodipropionate. The above costabilizers are used in the amount of from 0.01 to 2 percent by weight of the organic material, and preferably from 0.1 to 1 percent.  
  Although the compounds of this invention are also effective as thermal stabilizers, if the processing of the polymer is carried out at high temperatures it is advantageous to incorporate additional antioxidants.  
  The antioxidant compounds that can be employed are various hindered phenolic compounds which can be illustrated by the compounds listed below:  
  di-noctadecyl( 3 t-butyl-4-hydroxy-5-methylbenzyl)- malonate 2,6-di-t-butylphenol 2,2-methylene-bis(6-t-butyl-4-methylphenol) 2,6-di-t-butylhydroquinone octadecyl( 3 ,5-di-t-butyl-4-hydroxybenzylthio )acetate l, l ,3-tris( 3-t-butyl-6-methyl-4-hydroxyphenyl butane l,4-bis( 3,5-di-t-butyl-4-hydroxybenzyl )-2,3 ,5 ,6-tetramethylbenzene 2,4l-bis( 3,S-di-t-butyl-4-hydroxyphenoxy )-6-( noctylthio)- l ,3 ,5-triazine 2,4-bis-(4-hydroxy-3,S-di-t-butylphenoxy)-6-(noctylthioethylthio 1 ,3 ,5triazine 2,4-bis-(n-octylthio)-6-(3,5-di-t-butyl-4-hydroxyanilino)-l ,3 ,S-triazine 2,4,6-tris-(4-hydroxy-3 ,S-di-t-butylphenoxy )-l ,3,5-  
 triazine n-octadecyl-B-(3,5-di-t-butyl-4-hydroxyphenyl)propionate n-octadecyl-3,5-di-t-butyl-4-hydroxybenzoate 2-(n-octylthio)ethyl-3,5-di-t-butyl-4- hydroxybenzoate stearamido N,N-bisethylene 3-(3,5-di-t-butyl-4- hydroxyphenyl)propionate 1,2-propylene glycol hydroxyphenyhpr&#39;opionate pentaerythritol tetrakis- 3-( 3,5-di-t-butyl-4-hydroxyphenyl)propionate dioctadecyl-3,5-di-t-butyl-4-hydroxybenzylphosphate di-n-octadecyl- 1 3 ,5-di-t-butyl-4-hydroxyphenyl ethanephosphonate The above antioxidants have been listed only for the purpose of illustration and it is important to note that any other antioxidant can be employed with the same improved results. The above exemplified antioxidants are disclosed in greater detail in the following patents: Netherlands Pat. No. 67/11199, issued Feb. 19, 1968; Netherlands Pat. No. 68/03498 issued Sept. 18, 1968; US Pat. Nos. 3,255,191; 3,330,859; 3,281,505; 3,285,855; 3,364,250; 3,368,997 and 3,357,944.  
  To further illustrate the present invention additional examples are presented without introducing any limitations to the description of the invention.  
 OUTDOOR LIGHT EXPOSURE TEST Denier Oriented Monofilaments bis- 3-(3,5-di-t-butyl-4- The additives are solvent blended (e.g., methylene chloride) with powdered polypropylene (Hercules Profax 6501 The solvent is then removed at room temperature in a vacuum oven with a slight air bleed. The dry mixture is melt-extruded at 450F and pelletized. The pellets are reextruded through a monofilament die, melt spun and hot oriented 4:1 by means ofa set of cold and hot Godet rolls to give 15 denier (nominal) monofilaments.  
  The test results reported in Examples of Table I show the percentage of retention of the original tenacity by a fiber after having been exposed to the indicated number of Kilolangleys (Kly) of Florida exposure. A Langley is a measure of energy accumulated by the fiber.  
  Table I shows the results of the above described outdoor test indicating amounts of the additives present. Thus, in the Additives column is given the percentage of the compound prepared in the indicated Example which is present in the polypropylene composition in addition to the additives present in the base formulation. The remaining two columns show the number of Kilolangleys of exposure in Florida at the indicated percentage of retention of the original tenacity to which the fibers have been subjected.  
 3,5-di-t-butyl4-hydroxybenzylphosphonate Proportionately good stabilization is obtained when in the compositions of Table I the compounds of this invention are present in the concentrations of 0.1 percent and 1 percent.  
 ARTIFICIAL LIGHT EXPOSURE TEST Deterioration of most polymers caused by ultraviolet light is so slow at ambient temperatures even in the absence of stabilizers, that testing of the effects of stabilizers generally must be conducted either at higher temperatures or in an accelerated artificial light exposure device in order to yield results in a convenient period of time. The test conducted on polymers using an artificial light exposure device is described below:  
 a. Sample Preparation 5 mil FilmUnstabilized polypropylene Powder (Hercules Profax 6501) is thoroughly blended with&#39;the indicated amounts of additives. The blended material is then milled on a two roll mill for 5 minutes at 182C. The milled sheet is then compression molded at 220C into 5 mil thick film under a pressure of psi and water cooled in the press.  
 b. Testing Method This test is conducted in a FS/BL unit, basically of the American Cyanamid design, which consists of 40 tubes of alternating fluorescent sun lamps and black lights (20 of each). The 5 mil sample film are mounted on 3X1 inch IR card holders with l inch windows are placed on a rotating drum 2 inches from the bulbs in the FS/BL unit. The time in hours is noted for the development of 0.5 carbonyl absorbance units as determined on an Infrared Spectophotometer. The development of carbonyl functional groups in the polymer is proportional to the amount of degradation caused by the ultraviolet light exposure.  
  The test results reported below were obtained according to the procedures described above. The amounts of the additives are expressed in weight percent based on the weight of the polymer.  
 TABLE 11 Artificial Light Exposure of 5 mil Film Time in Hours Ex. to .5 Carbonyl No. Formulation Absorbance Units 12 0.5% N-n-octadecyl-4-(3,5-di-tert.- butyl-4-hydroxybcnzoyloxy)-3.5- di-tert.butylbenzamide 170 I3 0.25% N-n-octadecyl-4-(3,5-di-tert.  
  butyl-4-hydroxybenzoyloxy)-3,5- di-tertbutylbenzamide 0.25% TlNUVlN 327** 510 14 0.5% N-rnethyl-N-n-octadecyl-4-(3,5- di-tert.butyl&#39;4-hydroxybenzoyloxy)- 3,S-di-tert-butylbenzamide 310 I5 0.25% N-methyl&#39;N-n-octadecyl-4&#39;(3,5  
  di&#39;tert.butyl-4-hydroxybenzoyloxy)- 3,S-di-Icrt-butylbenzamide 0.25% TlNUVlN 327 740 16 0.5% N,N-diethyl-4-(3,5-di-tertbutyl 4-hydroxybenzoyloxy)-3,5-di-t-butyl benzamide 800 17 0.25% N,N-diethyl-4-(3,5-di-tert-butyl- 4-hydroxybenzoyloxy)-3,5-di-t-butylbenzamidc 0.25% TlNUVlN 327 1370 18 0.5% N,N-di n-octyl-4-(3,5-di-tert-butyl- 4-hydrox bcnzoyloxy)-3.5-di-tert-butylbenzami e 740 19 0.25% N,N-di-n-octyl-4-(3.5-di-tcrt-butyl- 4-hydroxybenzoyloxy)-3,5-di-tert-butylbenzamide 0.25% TINUVlN 327 1310 20 Control About 120 Each of the samples tested and the control contains 0.2% of di-n-octudccyk3,S-di-Ibutyl-4-hydroxybenzyl)phosphonate which is an antioxidant which prevents oxidative degradation of polypropylene. &#34;TlNUVlN 327 is UV absorber 2(2&#39;-hydroxy-3&#39;,5-di-t-butyl-phenyl)-5chlorobcnzotriazole.  
 The composltions of Table II are equally stabilized EXAMPLE when TINUVIN 327 is replaced with the following compounds:  
 a. 2-hydroxy 4-methoxy-5-sulfobenzophenone trihydrate b. 2-hydroxy-4-n-octoxybenzophenone c. 2,2&#39;-thiobis(4-t-octylphenolate) -n-butylamine nickel 11 d. p-octylphenyl salicylate e. 2,2-dihydroxy-4,4&#39;dimethoxybenzophenone f. 2(2&#39;-hydroxy-5 &#39;-methylphenyl)-benzotriazole.  
 EXAMPLE 29 Pellets (500 g) of unstabilized nylon6,6 (Zytel 101, DuPont) are placed in a Kitchen Aid Mixer. With mixing a solution of 0.5 percent (based on the weight of nylon) of N-n-octadecyl4-(3,5-di-t-butyl-4- hydroxybenzoyloxy)-3,S-di-t-butylbenzamide in 20 ml of methylene chloride is added slowly. Sodium hypophosphite (0.5 gm. 0.1 percent) is dissolved in 20 ml of water and added slowly with mixing to the nylon pellets after the antioxidant solution has been added and most of the methylene chloride has evaporated. The stabilized pellets are dried at 80C at 1mm Hg. for 4 hours.  
  The polyamide formulation is extruded at 600F through a A inch die into a rod which is water cooled and chopped into pellets. A inch Brabender extruder, equipped with a nylon screw, is used. The pellets are dried at 80C at 1 mm for 4 hours.  
  The dried pellets are reextruded into 5 mil (nominal) monofilament fiber which is subsequently oriented (4:1). The oriented fibers are exposed to outdoor weathering (direct and under glass) and tensile measurement is made periodically. The sample is considered to have failed when it loses 50 percent of its original tenacity. The sample stabilized with the above noted benzoate retained tensile strength for a much longer period than the unstabilized sample.  
  Unstabilized high impact polystyrene resin is dry blended with 0.01 percent by weight of the resin of N- methyl-N-n-octadecyl-4-(3,5-di-t-butyl-4- hydroxybenzoyloxy)-3,S-di-bbutylbenzamide. The resin is then extrusion compounded on a 1 inch 24/1=L/D extruder, melt temperature 500F and pressed for 7 minutes at a temperature of 163C and a pressure of 2,000 psi into a sheet of uniform thickness of mil. The sheets are then cut into plagues of 2X2 inch. The plaques are then exposed in a FS/BL exposure device and color measurements made periodically using a Hunter Color Difference Meter Model D25. The polystyrene samples stabilized with the above benzoate developed the undesirable yellow discoloration substantially later after such discoloration occurred in the unstabilized samples.  
 EXAMPLE 31 Unstabilized linear polyethylene is solvent blended in methylene chloride with 0.5 percent by weight of the substrate of N ,N-di-n-octyl-4-( 3 ,5*di-t-butyl-4- hydroxybenzoyloxy)-3,5 di t-butylbenzamide and then vacuum dried. The resin is then extruded at 450F as described in Example 30. Thereafter, the test procedure of Example 30 is followed and the light stability of the samples determined. Polyethylene stabilized with the above benzoate is found. to be much more stable than the unstabilized polyethylene or the polyethylene stabilized only with an antioxidant.  
 EXAMPLE 32 A quantity of SBR emulsion containing 100 g of rubber (500 ml of 20 percent SBR obtained from Texas, US, Synpol 1500) previously stored under nitrogen, is placed in a beaker and stirred. vigorously. The pH of the emulsion is adjusted to 10.5 with a 0.5N NaOH solution.  
  To the emulsion is added 50 ml of 25 percent NaCl solution. A 6 percent NaCl solution adjusted with hydrochloric acid to a pH 1.5 is added in a thin stream with vigorous stirring. When pH 6.5 is reached, the rubber begins to coagulate and the addition is slowed down in order to maintain uniform agitation. The addition of the acidic 6percent NaCl solution is terminated when a pH 3.5 is reached. The coagulated crumb-rubber slurry at pH 3.5 is stirred for one-half hour.  
  The coagulated rubber is isolated by filtration through cheese cloth, and rinsed with distilled water. After three subsequent washings with fresh distilled water, the coagulated rubber is dried, first at 25 mm Hg and finally to constant weight under high vacuum 1 mm) at 40-45C.  
  The dried rubber (25 g) is heated under nitrogen at 125C in a Brabender mixer and to this is added with mixing 0.25 g (0.5 percent) of N,N-diethyl-4-(3,5-di-tbutyl-4-hydroxybenzoyloxy)-3,S-di-t-butylbenzamide. The composition is mixed for 5 minutes after which it is cooled and compression molded at 125C into 5X0.025 inch plaques.  
  The plaques are exposed to a xenon arc weatherometer and the color measurement (L-b) is made after 45, 125 and 290 hours. The samples stabilized with the above benzoate is found to be much more light stable than the unstabilized samples.  
 EXAMPLE 33 To 50 g of polyacetal resin containing 0.1 percent of an acid scavenger, dicyandiamide, is added 0.2 percent by weight of N-ethyl-N-p-tolyl-4-(3,5-di-t1butyl-4- hydroxybenzoyloxy)-3,S-di-t-butylbenzamide, and  
 milled for 7 minutes at 200c in a Brabender Plas- EXAMPLE 34 Unstabilized thoroughly dried polyethylene terephthalate chips are dry blended with 1.0 percent of N- n-octyl-4-( 3 ,5-di-t-butyl-4-hydroxybenzoyloxy)-5-tbutyl benzamide. 60/10 denier multifilament is melt spun at a melt temperature of 290C. The oriented fiber is wound on white cards and exposed in a Xenon Arc Fadeometer. Color measurements are made periodically with a Hunter Color Difference Meter Model D25. The stabilized samples are found to be much more light stable than the unstabilized samples.  
 EXAMPLE 35 Preparation of N,Nhexamethylene-bis- (3,5-di-tert.butyl-4- 1 2 hydroxybenzoyloxy)-3 ,5-di-tert.-butylbenzamide 15.7 grams of 1,6-hexanediamine dissolved in 200 ml. of toluene was added dropwise to a solution of 14.6 grams of 3,5-di-tert.butyl-4-hydroxybenzoyloxy)-3,5- di-tert.butylbenzoyl chloride and 2.83 grams of triethylamine in 300 ml. of toluene at such a rate so that the temperature was kept below 35C. The reaction mixture was heated at reflux (110 to 112C) for about 4 hours. The reaction mixture was diluted with 600 ml. of chloroform and successively washed with water, saturated sodium carbonate and water. The toluene solution was dried over sodium sulfate, yielding the desired product after removal of the toluene by vacuum distillation.  
 What is claimed is:  
 1. A Benzoyloxybenzamide having the formula Wherein R and R are (lower) alkyl groups,  
 R and R are independently (lower) alkyl groups,  
 R is hydrogen or (lower) alkyl group,  
 R is alkyl group having up to 24 carbon atoms when n is 2 to 6, and  
 n is an integer l to 6.  
  2. Compounds of claim 1 wherein R and R are branched alkyl,  
 R is alkylene and n is 2.  
  3. Compounds of claim 2 wherein R is alkyl and n is l.  
  4. Compounds of claim 1 wherein R, R R and R are tert-butyl groups, R is alkyl and n is 1.  
  5. Compound of claim 1 which is N-n-octadecyl-4- (3 ,5-di-tert.butyl-4-hydroxybenzoyloxy )-3 ,5 -di-tertbutylbenzamide.  
  6. Compound of claim 1 which ,is N-methyl-N-noctadecyl-4-( 3 ,5-di-tert.butyl-4-hydroxybenzoyloxy 3,5-di-tert-butylbenzamide.  
  7. Compound of claim 1 which is N,N-di-n-octyl-4- (3 ,5-di-tert-butyl 4-hydroxybenzoyloxy )-3 ,S-di-tertbutylbenzamide.  
  8. Compound of claim 1 which is N,N-diethyl-4-( 3,5- di-tert-butyl-4-hydroxybenzoyloxy)-3,5-di-t butylbenzamide.  
  9. Compound of claim 1 which is N-( 1,1,3,3- tetramethylbutyl )-4-( 3 ,5 -di-tert-butyl-4 hydro xybenzoyloxy )-3 ,S-di-te rt-butylbenzamide.