Patent Publication Number: US-2019176521-A1

Title: Pneumatic tire

Description:
TECHNICAL FIELD 
     The present invention relates to a pneumatic tire (hereinafter, also simply referred to as “tire”), particularly a pneumatic tire in which the crack propagation resistance of crossing belt layers is improved without deterioration of the cutting resistance and the irregular wear resistance. 
     BACKGROUND ART 
     General dump truck tires running on rough ground on occasions are forced to run on road surfaces on which broken rocks are scattered. Thus, steel cords are widely used as reinforcing materials. Under such circumstances, as a steel cord for truck/bus tires that has excellent belt-end separation resistance and improves the tire durability and retreadability, for example, Patent Document 1 proposes a steel cord which includes a core composed of one to three steel filaments and six to nine steel filaments twisted together around the core and satisfies prescribed physical properties. 
     RELATED ART DOCUMENT 
     Patent Document 
     [Patent Document 1] JPH02-306801A 
     SUMMARY OF THE INVENTION 
     Problems to be Solved by the Invention 
     As described above, since dump truck tires run on rough ground in many occasions, a cut failure of a belt is likely to occur, and it is conceivable that the cut directly causes tire failure, or infiltration of water through the cut causes corrosion of a steel cord, leading to a separation failure. Dump truck tires usually include a belt composed of plural belt layers on the tire radial-direction outer side of a carcass. However, once a cut damage reaches crossing belt layers, water infiltrates into steel cords constituting the crossing belt layers and causes corrosion inside the steel cords. This may result in detachment of the crossing belt layers. Thus, it is necessary to prevent infiltration of water into the steel cords by allowing a rubber to sufficiently permeate into the steel cords. 
     Moreover, when a crack is generated due to strain of a belt end, the crack may propagate to cause detachment of the crossing belt layers. In order to inhibit such crack propagation in the crossing belt layers, the steel cord to cord distance in the crossing belt layers is preferably wide; however, since the amount of steel in the crossing belt layers is small when the steel cord to cord distance is wide, the rigidity is reduced and irregular wear occurs as a result. In this manner, at present, it is difficult to achieve both crack propagation resistance in the crossing belt layers and irregular wear resistance. 
     In view of the above, an object of the present invention is to provide a pneumatic tire in which the crack propagation resistance of crossing belt layers is improved without deterioration of the cutting resistance and the irregular wear resistance. 
     Means for Solving the Problems 
     The present inventor intensively studied to solve the above-described problems and consequently discovered that the above-described problems can be solved by using a steel cord having a prescribed structure and controlling crossing belt layers to have a prescribed steel cord amount, thereby completing the present invention. 
     That is, the pneumatic tire of the present invention is a pneumatic tire including a belt composed of at least three belt layers on the tire radial-direction outer side of a carcass, wherein at least three belt layers including two crossing belt layers that are inclined in the opposite directions across the tire equatorial plane, which pneumatic tire is characterized in that: 
     a reinforcing material of the crossing belt layers is a steel cord which has a layer-twisted structure including a core composed of two core filaments and a sheath composed of eight sheath filaments that are twisted together around the core, and 
     a steel cord amount in the crossing belt layers, which is represented by the following Equation (1), is 23 to 49: 
       Steel cord diameter (mm)×Steel cord end count (steel cords/50 mm)  (1).
 
     It is noted here that the term “steel cord diameter” used herein means the diameter of a circumscribed circle of the subject steel cord. 
     In the tire of the present invention, it is preferred that an outermost belt layer among the above-described at least three belt layers have a steel cord amount of 37 to 49, and that the steel cord amount in the crossing belt layers be not greater than the steel cord amount in the outermost belt layer. In the tire of the present invention, it is also preferred that the steel cord amount in the outermost belt layer be 100 to 217% of the steel cord amount in the crossing belt layers. Further, in the tire of the present invention, it is preferred that a steel cord to cord distance G 1  (mm) of the outermost belt layer and a steel cord to cord distance G 2  (mm) of the crossing belt layers satisfy a relationship represented by the following Equation (2): 
       0.1≤ G 1≤ G 2≤1.8  (2).
 
     Still further, in the tire of the present invention, it is preferred that the steel cord to cord distance G 1  (mm) of the outermost belt layer and the steel cord to cord distance G 2  (mm) of the crossing belt layers satisfy a relationship represented by the following Equation (3): 
       0.05≤ G 1/ G 2&lt;1.0  (3).
 
     Yet still further, in the tire of the present invention, it is preferred that the two core filaments of the steel cord of the crossing belt layers be twisted together, the twisting direction of the core filaments and that of the sheath filaments be different, and a diameter Dc of the core filaments and a diameter Ds of the sheath filaments satisfy a relationship represented by the following Equation (4): 
       0.90≤ Ds/Dc≤ 1.10  (4).
 
     Yet still further, in the tire of the present invention, it is preferred that the diameter Dc of the core filaments and the diameter Ds of the sheath filaments be the same. Yet still further, in the tire of the present invention, it is preferred that the diameter Dc of the core filaments and the diameter Ds of the sheath filaments be both 0.30 to 0.55 mm. Yet still further, in the tire of the present invention, it is preferred that the twisting pitch of the core filaments be 5 to 15 mm. Yet still further, in the tire of the present invention, it is preferred that the twisting pitch of the sheath filaments be 9 to 30 mm. 
     Effects of the Invention 
     According to the present invention, a pneumatic tire in which the crack propagation resistance of crossing belt layers is improved without deterioration of the cutting resistance and the irregular wear resistance can be provided. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is a widthwise cross-sectional view illustrating a pneumatic tire according to one preferred embodiment of the present invention. 
         FIG. 2  is a cross-sectional view illustrating a steel cord of crossing belt layers of a pneumatic tire according to one preferred embodiment of the present invention. 
         FIG. 3A  is a cross-sectional view illustrating a steel cord prior to a cut input of crossing belt layers of a pneumatic tire according to one preferred embodiment of the present invention. 
         FIG. 3B  is a cross-sectional view illustrating the steel cord when a cut input is made of the crossing belt layers of the pneumatic tire according to one preferred embodiment of the present invention. 
         FIG. 4A  is a cross-sectional view of a steel cord having a 1×3+8 structure prior to a cut input. 
         FIG. 4B  is a cross-sectional view of the steel cord having a 1×3+8 structure when a cut input is made. 
     
    
    
     MODE FOR CARRYING OUT THE INVENTION 
     The pneumatic tire of the present invention will now be described in detail referring to the drawings.  FIG. 1  is a widthwise cross-sectional view illustrating a pneumatic tire according to one preferred embodiment of the present invention. In the illustrated example, a tire  100  of the present invention includes: bead cores  101  arranged in a pair of left and right bead portions  106 ; and a tread portion  104  that is reinforced by a radial carcass  102 , which extends from a crown portion to both bead portions  106  through side wall portions  105  and is wound around the bead cores  101  and thereby anchored to the respective bead portions  106 , and a belt which is arranged on the crown portion tire radial-direction outer side of the radial carcass  102  and constituted by at least three belt layers  103   a ,  103   b  and  103   c.    
     In the tire  100  of the present invention, at least three belt layers  103  include two crossing belt layers (belt layers  103   a  and  103   b  in the illustrated example) that are inclined in the opposite directions across the tire equatorial plane, and a reinforcing material of the crossing belt layers  103   a  and  103   b  is a steel cord which has a layer-twisted structure including a core composed of two core filaments and a sheath composed of eight sheath filaments that are twisted together around the core. The steel cord having such a layer-twisted structure has excellent corrosion resistance since a rubber favorably permeates into the steel cord and infiltration of water into the steel cord can thereby be inhibited. As a result, the corrosion resistance of the crossing belt layers can be improved. Meanwhile, when the number of the core filaments is three or greater, the rubber permeability into the core is deteriorated. Since this consequently causes strains to be concentrated to the rubber-infiltrated sheath filaments, the crack propagation resistance is deteriorated. 
     Further, in the tire  100  of the present invention, the steel cord amount in the crossing belt layers  103   a  and  103   b  among the at least three belt layers  103 , which is represented by the following Equation (1), is 23 to 49: 
       Steel cord diameter (mm)×Steel cord end count (steel cords/50 mm)  (1).
 
     By setting the steel cord amount to be 23 to 49, the crack propagation resistance of the crossing belt layers  103   a  and  103   b  can be sufficiently improved while suppressing deterioration of the irregular wear resistance caused by variation in the rigidity of the crossing belt layers  103   a  and  103   b . The steel cord amount in the crossing belt layers  103   a  and  103   b  is preferably 25 to 44, more preferably 32 to 36. In cases where a steel cord having a structure other than the above-described one is used, the crack propagation resistance is greatly deteriorated when the steel cord amount is in the above-described range; however, in the tire  100  of the present invention, because of the use of the specific steel cord, the wear resistance can be maintained without sacrificing other performances even when the steel cord amount in the crossing belt layers  103   a  and  103   b  is in the above-described range. 
     In the tire  100  of the present invention, the steel cord amount in the outermost belt layer  103   c  is preferably 37 to 49. In this manner, by controlling the steel cord amount in the outermost belt layer  103   c  to be 37 or greater, the resistance to penetration of a foreign matter can be improved. However, when the steel cord amount in the outermost belt layer  103   c  is large, a crack generated between steel cords readily propagates, which is not preferred from the durability standpoint. Therefore, by controlling the steel cord amount in the outermost belt layer  103   c  to be 49 or less, a crack propagation resistance is ensured in the outermost belt layer  103   c . In order to favorably attain this effect, the steel cord amount in the outermost belt layer  103   c  is more preferably 37 to 44. It is noted here that, from the standpoint of the penetration resistance of the outermost belt layer  103   c , the steel cord amount in the outermost belt layer  103   c  is preferably not less than the steel cord amount in the crossing belt layers  103   a  and  103   b.    
     Specifically, in the tire  100  of the present invention, it is preferred that the steel cord amount in the outermost belt layer  103   c  be 100 to 217% of the steel cord amount in the crossing belt layers  103   a  and  103   b . By satisfying this relationship, the resistance to penetration of a foreign matter and the crack propagation resistance of the outermost belt layer  103   c  can be improved in a well-balanced manner without deteriorating neither of them. 
     Further, in the tire  100  of the present invention, it is preferred that the steel cord to cord distance G 1  (mm) of the outermost belt layer  103   c  and the steel cord to cord distance G 2  (mm) of the crossing belt layers  103   a  and  103   b  satisfy a relationship represented by the following Equation (2): 
       0.1≤ G 1≤ G 2≤1.8  (2).
 
     By satisfying this relationship, the resistance to penetration of a foreign matter and the crack propagation resistance of the outermost belt layer  103   c  can be improved in a more balanced manner without deteriorating neither of them. Moreover, since G 1 ≤G 2 , the crack propagation resistance of the crossing belt layers is not deteriorated. The G 1  and the G 2  more preferably satisfy: 
       0.3≤ G 1≤ G 2≤1.3  (5).
 
     Still further, in the tire  100  of the present invention, it is preferred that the steel cord to cord distance G 1  (mm) of the outermost belt layer  103   c  and the steel cord to cord distance G 2  (mm) of the crossing belt layers  103   a  and  103   b  satisfy a relationship represented by the following Equation (3): 
       0.05≤ G 1/ G 2≤1.0  (3).
 
     By satisfying this relationship, the resistance to penetration of a foreign matter and the crack propagation resistance of the outermost belt layer  103   c  can be improved in an even more balanced manner. Likewise, as long as this relationship is satisfied, the crack propagation resistance of the crossing belt layers is not deteriorated. The G 1  and the G 2  satisfy more preferably: 
       0.2≤ G 1/ G 2&lt;1.0  (6),
 
       particularly preferably: 
       0.25≤ G 1/ G 2&lt;0.75  (7).
 
       FIG. 2  is a cross-sectional view illustrating a steel cord of crossing belt layers of the pneumatic tire according to one preferred embodiment of the present invention. In  FIG. 2 , R represents the diameter of the steel cord. As illustrated, a steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention has a layer-twisted structure including: a core  11  composed of two core filaments  1 ; and a sheath  12  composed of eight sheath filaments  2  that are twisted together around the core  11 . In the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, the two core filaments  1  constituting the core  11  are twisted together. By adopting this constitution, the steel cord  20  has superior cutting resistance as compared to a conventional steel cord in which three core filaments are twisted together. The reasons for this are described below. 
       FIG. 3A  is a cross-sectional view illustrating a steel cord prior to a cut input of crossing belt layers of a pneumatic tire according to one preferred embodiment of the present invention.  FIG. 3B  is a cross-sectional view illustrating the steel cord when a cut input is made of the crossing belt layers of the pneumatic tire according to one preferred embodiment of the present invention.  FIG. 4A  is a cross-sectional view of a steel cord having a 1×3+8 structure prior to a cut input.  FIG. 4B  is a cross-sectional view of the steel cord having a 1×3+8 structure when a cut input is made. In the steel cords  20  having the respective cross-sections illustrated in  FIGS. 3A and 4A , when a cut is input, the positions of the core filaments  1  and the sheath filaments  2  are changed as illustrated in  FIGS. 3B and 4B , respectively. It is noted here that the arrows in  FIGS. 3B and 4B  each represent the direction of the cut input. 
     Comparing  FIGS. 3B and 4B , since the steel cord  20  having the core  11  composed of two core filaments  1  that are twisted together has large gaps in the core  11  as illustrated in  FIG. 3B , the sheath filaments  2  sink into the gaps of the core  11  when a cut is input, so that the cross-section of the steel cord  20  can be deformed into a flat shape. Accordingly, the cut input can be mitigated, and a high shear load is thereby attained. On the other hand, in the steel cord  20  having the core  11  in which three core filaments  1  are twisted together as illustrated in  FIG. 4B , since there is no gap which the sheath filaments  2  can sink into when a cut is input, the cross-section of the steel cord  20  cannot be deformed into a flat shape even with the cut input. Accordingly, the cut input cannot be mitigated, and the shear load is relatively small. Similarly, in those cases of steel cords having one or four core filaments, the core has no gap for the sheath filaments to sink into. Therefore, in the steel cord  20  of the present invention, the core  11  is formed by twisting together two core filaments  1 . Further, in order to allow the sheath filaments  2  to sink smoothly, it is preferred to use filaments having straightness as the core filaments  1  and the sheath filaments  2 . 
     In the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, the number of the sheath filaments  2  is 8. When the number of the sheath filaments  2  is less than 8, the shear load is reduced since the amount of steel per unit area of the steel cord  20  is small. Meanwhile, when the number of the sheath filaments  2  is greater than 8, since the gaps between the sheath filaments  2  are small, the steel cord  20  cannot collapse into a flat shape, so that the shear load is reduced likewise. In addition, the small gaps between the sheath filaments  2  make it difficult for a rubber to permeate thereinto, which is not preferred. 
     Further, in the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, it is preferred that the twisting direction of the core filaments  1  be different from the twisting direction of the sheath filaments  2 . This makes it easy for a rubber to infiltrate into the steel cord  20 , and the corrosion resistance of the steel cord  20  is thereby improved. In addition, because of the difference in the twisting direction between the core filaments  1  and the sheath filaments  2 , deformation of a calendered steel prepared by rubber-coating the steel cord  20  that is caused by cutting of the calendered steel can be suppressed, so that not only excellent processability in the production of the pneumatic tire  100  of the present invention but also an effect of inhibiting crack propagation against strains applied from various directions can be attained. 
     Still further, in the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, it is preferred that the diameter Dc of the core filaments  1  and the diameter Ds of the sheath filaments  2  satisfy a relationship represented by the following Equation (4): 
       0.90≤ Ds/Dc≤ 1.10  (4).
 
     With the value of Ds/Dc satisfying this range, good rubber permeability into the steel cord  20  can be ensured, and sufficient cutting resistance and strength can be attained. In order to favorably attain this effect, the Ds and the Dc satisfy more preferably: 
       0.95≤ Ds/Dc≤ 1.08  (8),
 
       still more preferably: 
       1.00≤ Ds/Dc≤ 1.05  (9),
 
     and the Ds and the Dc are particularly preferably the same (Ds=Dc). 
     Yet still further, in the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, it is preferred that the diameter Dc of the core filaments  1  and the diameter Ds of the sheath filaments  2  be both 0.30 to 0.55 mm. By controlling the diameter of the core filaments  1  and that of the sheath filaments  2  to be in this range, good rubber permeability into the steel cord  20  can be ensured likewise, and sufficient cutting resistance and strength can be attained. In order to favorably attain this effect, the diameter Dc and the diameter Ds are preferably 0.30 to 0.46 mm, more preferably 0.37 to 0.43 mm. 
     Yet still further, in the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, it is preferred that the twisting pitch of the core filaments  1  be 5 to 15 mm. By controlling the twisting pitch of the core filaments  1  to be in this range, sufficient rubber permeability into the steel cord  20  can be attained. The twisting pitch of the core filaments  1  is more preferably 5 to 13 mm, still more preferably 7 to 9 mm. 
     Yet still further, in the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, it is preferred that the twisting pitch of the sheath filaments  2  be 9 to 30 mm. By controlling the twisting pitch of the sheath filaments  2  to be 9 mm or larger, the surface irregularities of the steel cord  20  can be reduced, as a result of which the adhesion between a rubber and the steel cord  20  is enhanced and the durability is thus improved. Meanwhile, when the twisting pitch of the sheath filaments  2  is large, spread of water along the sheath filaments  2  is accelerated. In order to inhibit this phenomenon, the twisting pitch of the sheath filaments  2  is preferably 30 mm or smaller, more preferably 9 to 26 mm, still more preferably 15 to 20 mm. 
     In the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, it is preferred that the sum S 2  of the gap area S 1  of the sheath  12  and the cross-sectional areas of the sheath filaments  2  satisfy a relationship represented by the following Equation (10): 
       40≤ S 1/ S 2×100(%)≤120  (10).
 
     The “gap area S 1 ” of the sheath  12  refers to the portion indicated with diagonal lines in  FIG. 2 . By controlling the value of S 1 /S 2 ×100(%) to be 40 or larger, the gap area of the sheath  12  can be sufficiently ensured, and the steel cord  20  is made more likely to deform into a flat shape when a cut is input. In addition, since the gaps in the sheath  12  are increased, excellent rubber permeability is attained, so that a separation failure caused by corrosion of the steel cord  20  due to infiltration of water through a cut damage can be favorably inhibited. Meanwhile, by controlling the value of S 1 /S 2 ×100(%) to be 120 or smaller, a certain amount of steel in the sheath  12  is ensured, and sufficient cutting resistance as a reinforcing material can thus be ensured. 
     The gap area S 1  of the sheath  12  can be determined by the following Equation (11): 
         S 1=( Dc+Ds ) 2   π−Dc   2   π−Ds   2   π×N/ 4  (11),
 
     where Dc: Diameter of core filaments, 
     Ds: Diameter of sheath filaments, and 
     N: Number of sheath filaments. 
     In the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, it is preferred that the gap area S 1  of the sheath  12  be 0.30 mm 2  or larger. The effects of the present invention can be favorably obtained by adjusting the diameter of the core filaments  1  and that of the sheath filaments  2  such that the gap area S 1  of the sheath  12  is 0.30 mm 2  or larger. 
     In the steel cord  20  of the crossing belt layers  103   a  and  103   b  in the tire  100  of the present invention, it is preferred that the strength F 1  of the core filaments  1  and the strength F 2  of the sheath filaments  2  satisfy a relationship represented by the following Equation (12): 
         F 1/ F 2×100≥90(%)  (12).
 
     In the pneumatic tire  100 , a strength is also demanded for belt layers. When the strength is insufficient, the pneumatic tire  100  cannot withstand an internal pressure and a load, and its burst durability is reduced. However, when thick steel filaments are used for improving the strength, the rubber permeability into the steel cord is deteriorated. Moreover, an increase in the strength of the steel filaments for the purpose of increasing the strength of the belt layers, the shear load is deteriorated. Therefore, in the steel cord  20  of the present invention, by satisfying the Equation (12), preferably by controlling the F 1  and the F 2  to be the same (F 1 =F 2 ), such problems are avoided and the strength of the steel cord  20  is improved. The strength F 2  of the sheath filaments  2  is preferably 150 N or greater and, taking into consideration the shear load, the upper limit of the F 1  and F 2  is 580 N or less. 
     In the tire  100  of the present invention, it is important that the tire  100  include a belt composed of at least three belt layers  103 ; that a reinforcing material of at least the crossing belt layers among the at least three belt layers  103  be a steel cord having a 2+8 structure; and that the amount of the steel cord in the crossing belt layers satisfy the above-described range, and other features of the constitution can be designed as appropriate. For example, the structure of a steel cord in a belt layer other than the crossing belt layers of the tire  100  of the present invention, namely the outermost belt layer  103   c  in the illustrated example, is not particularly restricted. For example, a steel cord having a 1×N structure (e.g., 1×3 or 1×5), a steel cord having an M+N bilayer structure (e.g., 1+3, 1+4, 1+5, 1+6, 2+2, 2+3, 2+4, 2+5, 2+6, 2+7, 3+6, 3+7, or 3+8), or a steel cord having an L+M+N (L=1 to 4, M=4 to 9, and N=8 to 15) three-layer structure (e.g., a 3+9+15 structure) can be used. It is desirable to use a steel cord having the same 2+8 structure as the steel cord  20  used in the crossing belt layers of the tire  100  of the present invention. By using a cord having a 2+8 structure, when the steel cord amount in the outermost belt layer  103   c  is in the above-described range, the penetration resistance against a needle and the like that the tire may run over can be better improved without largely deteriorating various performances such as crack propagation resistance, as compared to a case where a belt composed of steel cords having other structure is used. 
     The material of the steel filaments used in the steel cords of the belt layers  103  of the tire  100  of the present invention is also not particularly restricted, and any conventionally used steel filaments can be used; however, the material is preferably a high-carbon steel containing not less than 0.80% by mass of a carbon component. By using a high-hardness high-carbon steel containing not less than 0.80% by mass of a carbon component as the material of the filaments, the effects of the present invention can be favorably attained. Meanwhile, a carbon component content of greater than 1.5% by mass is not preferred since the ductility is reduced and the fatigue resistance is thus deteriorated. 
     In the tire  100  of the present invention, a plating treatment may be performed on the surfaces of the steel cords of the belt layers  103 . The composition of the plating to be applied to the surfaces of the steel cords is not particularly restricted; however, a brass plating composed of copper and zinc is preferred, and a brass plating having a copper content of not less than 60% by mass is more preferred. By the plating treatment, the adhesion between the steel filaments and a rubber can be improved. 
     In the tire  100  of the present invention, the details of the tire constitution, the materials of the respective members and the like are also not particularly restricted, and the tire  100  of the present invention can be configured by appropriately selecting a conventionally known structure, materials and the like. For example, a tread pattern is formed as appropriate on the surface of the tread portion  104 , bead fillers (not illustrated) are arranged on the tire radial-direction outer side of the respective bead cores  101 , and an inner liner is arranged as an innermost layer of the tire  100 . Further, as a gas filled into the tire  100  of the present invention, air having normal or adjusted oxygen partial pressure, or an inert gas such as nitrogen, can be used. The tire of the present invention exhibits excellent crack propagation resistance of the crossing belt layers without deterioration of the irregular wear resistance; therefore, the tire of the present invention can be suitably applied to trucks and buses. 
     EXAMPLES 
     The present invention will now be described in more detail by way of examples thereof. 
     Examples 1 to 19 and Comparative Examples 1 to 8 
     Tires having a belt composed of four belt layers on the radial-direction outer side of a carcass were produced at a tire size of 11R22.5/14PR. In the crossing belt layers of these tires, the cord type A to G shown in Table 1 were used as steel cords, and the steel cords were arranged such that the major-axis direction was aligned with the belt width direction. A second belt layer and a third belt layer (the second layer and the third layer from the tire radial-direction inner side, respectively) had an angle of ±20° with respect to the tire circumferential direction. The structures and the like of the steel cords of the respective outermost belt layers were as shown in Tables 2 to 6, and each outermost belt layer was arranged at an angle of 20° with respect to the tire circumferential direction. Further, in the first belt layer, the steel cord structure was 3+9+15×0.22+0.15, the belt angle was 50° with respect to the tire circumferential direction, and the end count was 20 steel cords/50 mm. For each of the thus obtained tires, the cutting resistance, crack propagation resistance and irregular wear resistance of the crossing belt layers were evaluated in accordance with the following procedures. 
     &lt;Cutting Resistance&gt; 
     A blade of 500 mm in width, 1.5 mm in thickness (bottom thickness=5.0 mm) and 30 mm in height was gradually pressed against each tire to measure the force required for breaking a steel cord of the crossing belt layers, and the thus measured force was indicated as an index based on the value of Comparative Example 1. A larger value means superior cutting resistance, and a value of 100 or larger was regarded as satisfactory. The results thereof are also shown in Tables 2 to 6. 
     &lt;Irregular Wear Resistance&gt; 
     Each test tire was mounted on a rim having a size of 8.25 inches and subjected to a laboratory test using a rotary drum for tire wear test under the conditions of an internal air pressure of 700 kPa, an applied load of 26.7 kN and a test speed of 60 km/h. The wear amount of the center land portion positioned on the tire equatorial plane and the wear amount of the shoulder land portion were visually evaluated in a five-point scale, taking the value of Comparative Example 1 as 5. A larger value means superior irregular wear resistance, and a value of 4 or larger was regarded as satisfactory. The results thereof are also shown in Tables 2 to 6. 
     &lt;Crack Propagation Resistance&gt; 
     The thus produced tires were each mounted on a rim having a size of 8.25 inches and then subjected to a 300-hour drum running test at an air pressure of 700 kPa, a load of 26.7 kN and a speed of 60 km/h. After the completion of the drum running test, each tire was cut and disassembled, and the lengths of cracks generated in the crossing belt layers were measured and indicated as an index based on the value of Comparative Example 1. A larger value means superior crack propagation resistance, and a value of 1,000 or larger was regarded as satisfactory. The results thereof are also shown in Tables 2 to 6. 
     
       
         
           
               
               
               
               
               
               
               
               
             
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                 Cord 
                 Cord 
                 Cord 
                 Cord 
                 Cord 
                 Cord 
                 Cord 
               
               
                   
                 type A 
                 type B 
                 type C 
                 type D 
                 type E 
                 type F 
                 type G 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                 Core 
                 Number of filaments 
                 2 
                 2 
                 2 
                 4 
                 3 
                 2 
                 2 
               
               
                   
                 Filament diameter 
                 0.4 
                 0.4 
                 0.55 
                 0.4 
                 0.4 
                 0.4 
                 0.4 
               
               
                   
                 Dc (mm) 
               
               
                   
                 Filament strength 
                 346 
                 346 
                 568 
                 346 
                 346 
                 346 
                 346 
               
               
                   
                 F1 (N) 
               
               
                   
                 Filament twisting 
                 — 
                 Z 
                 Z 
                 Z 
                 Z 
                 Z 
                 Z 
               
               
                   
                 direction 
               
               
                   
                 Twisting pitch (mm) 
                 — 
                 8 
                 8 
                 8 
                 8 
                 8 
                 8 
               
               
                 Sheath 
                 Number of filaments 
                 8 
                 8 
                 8 
                 8 
                 8 
                 7 
                 9 
               
               
                   
                 Filament diameter 
                 0.4 
                 0.4 
                 0.55 
                 0.4 
                 0.4 
                 0.4 
                 0.4 
               
               
                   
                 Ds (mm) 
               
               
                   
                 Filament strength 
                 346 
                 346 
                 568 
                 346 
                 346 
                 346 
                 346 
               
               
                   
                 F2 (N) 
               
               
                   
                 Filament twisting 
                 S 
                 S 
                 S 
                 S 
                 S 
                 S 
                 S 
               
               
                   
                 direction 
               
               
                   
                 Twisting pitch (mm) 
                 17 
                 17 
                 17 
                 17 
                 17 
                 17 
                 17 
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                 Core-sheath filament twisting 
                 — 
                 different 
                 different 
                 different 
                 different 
                 different 
                 different 
               
               
                 direction 
               
               
                 Ds/Dc 
                 1.0 
                 1.0 
                 1.0 
                 1.0 
                 1.0 
                 1.0 
                 1.0 
               
               
                 Sheath gap area, S1 (mm 2 ) 
                 0.32 
                 0.50 
                 0.95 
                 0.71 
                 0.58 
                 0.63 
                 0.38 
               
               
                 Sum of sheath filament cross- 
                 1.01 
                 1.01 
                 1.90 
                 1.01 
                 1.01 
                 0.88 
                 1.13 
               
               
                 sectional areas, S2 (mm 2 ) 
               
               
                 S1/S2 × 100(%) 
                 31.8 
                 50 
                 50 
                 70.7 
                 57.7 
                 71.4 
                 33.3 
               
               
                 F1/F2 × 100(%) 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
               
               
               
             
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                 Comparative 
                 Example 
                 Example 
                 Comparative 
                 Comparative 
                 Comparative 
               
               
                   
                 Example 1 
                 1 
                 2 
                 Example 2 
                 Example 3 
                 Example 4 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                 Outermost 
                 Cord type 
                 A 
                 A 
                 B 
                 B 
                 B 
                 B 
               
               
                 belt layer 
                 Cord diameter (mm) 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
               
               
                   
                 Cord to cord 
                 1.53 
                 1.53 
                 0.32 
                 0.32 
                 0.32 
                 0.32 
               
               
                   
                 distance, G1 (mm) 
               
               
                   
                 End count 
                 16 
                 16 
                 26 
                 26 
                 26 
                 26 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 26 
                 26 
                 42 
                 42 
                 42 
                 42 
               
               
                   
                 calendered steel 
               
               
                 Crossing 
                 Cord type 
                 3 + 9 + 15 × 
                 B 
                 B 
                 D 
                 E 
                 A 
               
               
                 belt layers 
                   
                 0.22 + 1 
               
               
                   
                 Cord diameter (mm) 
                 1.35 
                 1.6 
                 1.6 
                 1.77 
                 1.66 
                 1.6 
               
               
                   
                 Cord to cord 
                 0.73 
                 0.67 
                 0.67 
                 0.74 
                 0.70 
                 0.69 
               
               
                   
                 distance, G2 (mm) 
               
               
                   
                 End count 
                 24 
                 22 
                 22 
                 20 
                 21 
                 22 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 32 
                 35 
                 35 
                 35 
                 35 
                 35 
               
               
                   
                 calendered steel 
               
            
           
           
               
               
               
               
               
               
               
            
               
                 SC amount in outermost layer/SC 
                 79 
                 73 
                 118 
                 118 
                 118 
                 119 
               
               
                 amount in crossing layers × 100(%) 
               
               
                 G1/G2 
                 2.08 
                 2.27 
                 0.48 
                 0.44 
                 0.46 
                 0.47 
               
               
                 Cutting resistance (index) 
                 100 
                 101 
                 173 
                 170 
                 169 
                 167 
               
               
                 Irregular wear resistance (index) 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
               
               
                 Crack propagation resistance of 
                 100 
                 1,263 
                 1,263 
                 283 
                 283 
                 316 
               
               
                 crossing belt layers (index) 
               
               
                   
               
               
                 *steel cord amount 
               
            
           
         
       
     
     
       
         
           
               
               
               
               
               
               
             
               
                   
                 TABLE 3 
               
               
                   
                   
               
               
                   
                 Comparative 
                 Comparative 
                 Comparative 
                 Example 
                 Example 
               
               
                   
                 Example 5 
                 Example 6 
                 Example 7 
                 3 
                 4 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 Outermost 
                 Cord type 
                 B 
                 B 
                 B 
                 B 
                 B 
               
               
                 belt layer 
                 Cord diameter (mm) 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
               
               
                   
                 Cord to cord 
                 0.32 
                 0.32 
                 0.32 
                 0.32 
                 0.32 
               
               
                   
                 distance, G1 (mm) 
               
               
                   
                 End count 
                 26 
                 26 
                 26 
                 26 
                 26 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 42 
                 42 
                 42 
                 42 
                 42 
               
               
                   
                 calendered steel 
               
               
                 Crossing 
                 Cord type 
                 F 
                 G 
                 B 
                 B 
                 B 
               
               
                 belt layers 
                 Cord diameter (mm) 
                 1.60 
                 1.60 
                 1.6 
                 1.6 
                 1.6 
               
               
                   
                 Cord to cord 
                 0.67 
                 0.67 
                 2.04 
                 1.88 
                 0.22 
               
               
                   
                 distance, G2 (mm) 
               
               
                   
                 End count 
                 22 
                 22 
                 14 
                 14 
                 28 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 35 
                 35 
                 22 
                 23 
                 44 
               
               
                   
                 calendered steel 
               
            
           
           
               
               
               
               
               
               
            
               
                 SC amount in outermost layer/SC 
                 118 
                 118 
                 189 
                 181 
                 95 
               
               
                 amount in crossing layers × 100(%) 
               
               
                 G1/G2 
                 0.48 
                 0.48 
                 0.16 
                 0.17 
                 1.48 
               
               
                 Cutting resistance (index) 
                 168 
                 173 
                 162 
                 163 
                 181 
               
               
                 Irregular wear resistance (index) 
                 5 
                 5 
                 3 
                 4 
                 5 
               
               
                 Crack propagation resistance of 
                 893 
                 283 
                 1,297 
                 1,293 
                 1,252 
               
               
                 crossing belt layers (index) 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
               
               
             
               
                   
                 TABLE 4 
               
               
                   
                   
               
               
                   
                   
                 Comparative 
                   
                   
                   
               
               
                   
                 Example 5 
                 Example 8 
                 Example 6 
                 Example 7 
                 Example 8 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 Outermost 
                 Cord type 
                 B 
                 B 
                 B 
                 B 
                 B 
               
               
                 belt layer 
                 Cord diameter (mm) 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
               
               
                   
                 Cord to cord 
                 0.32 
                 0.32 
                 0.62 
                 0.56 
                 0.03 
               
               
                   
                 distance, G1 (mm) 
               
               
                   
                 End count 
                 26 
                 26 
                 23 
                 23 
                 31 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 42 
                 42 
                 36 
                 37 
                 49 
               
               
                   
                 calendered steel 
               
               
                 Crossing 
                 Cord type 
                 B 
                 B 
                 B 
                 B 
                 B 
               
               
                 belt layers 
                 Cord diameter (mm) 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
               
               
                   
                 Cord to cord 
                 0.03 
                 0.00 
                 0.67 
                 0.67 
                 0.67 
               
               
                   
                 distance, G2 (mm) 
               
               
                   
                 End count 
                 31 
                 31 
                 22 
                 22 
                 22 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 49 
                 50 
                 35 
                 35 
                 35 
               
               
                   
                 calendered steel 
               
            
           
           
               
               
               
               
               
               
            
               
                 SC amount in outermost layer/SC 
                 85 
                 83 
                 102 
                 105 
                 139 
               
               
                 amount in crossing layers × 
               
               
                 100 (%) 
               
               
                 G1/G2 
                 9.89 
                 — 
                 0.92 
                 0.84 
                 0.05 
               
               
                 Cutting resistance (index) 
                 185 
                 186 
                 135 
                 157 
                 199 
               
               
                 Irregular wear resistance (index) 
                 5 
                 5 
                 5 
                 5 
                 4 
               
               
                 Crack propagation resistance of 
                 1,247 
                 50 
                 1,263 
                 1,263 
                 1,263 
               
               
                 crossing belt layers (index) 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
               
               
             
               
                   
                 TABLE 5 
               
               
                   
                   
               
               
                   
                 Example 
                 Example 
                 Example 
                 Example 
                 Example 
               
               
                   
                 9 
                 10 
                 11 
                 12 
                 13 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 Outermost 
                 Cord type 
                 B 
                 B 
                 B 
                 B 
                 B 
               
               
                 belt layer 
                 Cord diameter (mm) 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
               
               
                   
                 Cord to cord 
                 0.00 
                 2.06 
                 1.88 
                 0.02 
                 0.00 
               
               
                   
                 distance, G1 (mm) 
               
               
                   
                 End count 
                 31 
                 14 
                 14 
                 31 
                 31 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 50 
                 22 
                 23 
                 49 
                 50 
               
               
                   
                 calendered steel 
               
               
                 Crossing 
                 Cord type 
                 B 
                 B 
                 B 
                 B 
                 B 
               
               
                 belt layers 
                 Cord diameter (mm) 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
                 1.6 
               
               
                   
                 Cord to cord 
                 0.67 
                 1.88 
                 1.88 
                 1.88 
                 1.88 
               
               
                   
                 distance, G2 (mm) 
               
               
                   
                 End count 
                 22 
                 14 
                 14 
                 14 
                 14 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 35 
                 23 
                 23 
                 23 
                 23 
               
               
                   
                 calendered steel 
               
            
           
           
               
               
               
               
               
               
            
               
                 SC amount in outermost layer/SC 
                 142 
                 95 
                 100 
                 215 
                 217 
               
               
                 amount in crossing layers × 100(%) 
               
               
                 G1/G2 
                 0.00 
                 1.10 
                 1.00 
                 0.01 
                 0.00 
               
               
                 Cutting resistance (index) 
                 202 
                 100 
                 125 
                 190 
                 191 
               
               
                 Irregular wear resistance (index) 
                 4 
                 5 
                 5 
                 4 
                 4 
               
               
                 Crack propagation resistance of 
                 1,263 
                 1,252 
                 1,252 
                 1,252 
                 1,252 
               
               
                 crossing belt layers (index) 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
               
               
               
             
               
                   
                 TABLE 6 
               
               
                   
                   
               
               
                   
                 Example 
                 Example 
                 Example 
                 Example 
                 Example 
                 Example 
               
               
                   
                 14 
                 15 
                 16 
                 17 
                 18 
                 19 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                 Outermost 
                 Cord type 
                 C 
                 C 
                 C 
                 C 
                 B 
                 B 
               
               
                 belt layer 
                 Cord diameter (mm) 
                 2.2 
                 2.2 
                 2.2 
                 2.2 
                 1.6 
                 1.6 
               
               
                   
                 Cord to cord 
                 0.09 
                 0.10 
                 1.80 
                 1.81 
                 0.32 
                 0.32 
               
               
                   
                 distance, G1 (mm) 
               
               
                   
                 End count 
                 22 
                 22 
                 13 
                 12 
                 26 
                 26 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 48 
                 48 
                 28 
                 27 
                 42 
                 42 
               
               
                   
                 calendered steel 
               
               
                 Crossing 
                 Cord type 
                 B 
                 B 
                 B 
                 B 
                 B 
                 B 
               
               
                 belt layers 
                 Cord diameter (mm) 
                 1.60 
                 1.60 
                 1.60 
                 1.60 
                 1.6 
                 1.6 
               
               
                   
                 Cord to cord 
                 0.23 
                 0.23 
                 0.23 
                 0.23 
                 0.32 
                 0.31 
               
               
                   
                 distance, G2 (mm) 
               
               
                   
                 End count 
                 27 
                 27 
                 27 
                 27 
                 26 
                 26 
               
               
                   
                 (cords/50 mm) 
               
               
                   
                 SC amount* in 
                 44 
                 44 
                 44 
                 44 
                 42 
                 42 
               
               
                   
                 calendered steel 
               
            
           
           
               
               
               
               
               
               
               
            
               
                 SC amount in outermost layer/SC 
                 110 
                 109 
                 63 
                 63 
                 100 
                 99 
               
               
                 amount in crossing layers × 100(%) 
               
               
                 G1/G2 
                 0.40 
                 0.44 
                 7.93 
                 7.98 
                 1.00 
                 1.050 
               
               
                 Cutting resistance (index) 
                 232 
                 231 
                 150 
                 149 
                 179 
                 179 
               
               
                 Irregular wear resistance (index) 
                 4 
                 5 
                 5 
                 5 
                 5 
                 5 
               
               
                 Crack propagation resistance of 
                 1,252 
                 1,252 
                 1,252 
                 1,252 
                 1,255 
                 1,156 
               
               
                 crossing belt layers (index) 
               
               
                   
               
            
           
         
       
     
     From Tables 2 to 6 above, it is seen that, in the tires according to the present invention, excellent cutting resistance and excellent crack propagation resistance of the crossing belt layers were attained while suppressing irregular wear. 
     DESCRIPTION OF SYMBOLS 
     
         
         
           
               1 : core filament 
               2 : sheath filament 
               11 : core 
               12 : sheath 
               20 : steel cord 
               100 : pneumatic tire 
               101 : bead core 
               102 : carcass 
               103 : belt layer 
               104 : tread portion 
               105 : side wall portion