Patent Publication Number: US-10332795-B2

Title: Manufacturing method of semiconductor device

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
     This application is a continuation of U.S. patent application Ser. No. 15/147,591, filed May 5, 2016, which claims the benefit of Japanese Patent Application No. 2015-118656 filed on Jun. 11, 2015 including the specification, drawings and abstract is incorporated herein by reference in its entirety. 
    
    
     BACKGROUND 
     The invention relates to a manufacturing method of a semiconductor device and particularly, to a technique effectively applied to a manufacturing method of a semiconductor device using a sealed type transfer container for carrying a semiconductor wafer. 
     For example, in a semiconductor device manufacturing method, using a semiconductor wafer having a diameter of 300 mm, a plurality of semiconductor wafers are pun in the sealed type transfer container called Front Open Unified Pod (FOUP) and carried among the processors. 
     Japanese Unexamined Patent Application Publication No. 2008-24429 (Patent Document 1) shows that when a PSZ film is used to embed an element isolation insulating film, a deformation of a pattern occurs in the next photolithography process, hence to degrade the performance of the photolithography process. In other words, Si—N bond included in the PSZ film is hydrolyzed with water in the environment, to generate NH 3 , and a high sensibility photoresist of chemical amplification type photoresist used in the photolithography process reacts with basic compound including nitrogen atoms such as NH 3  or amine, hence to generate a pattern deformation. In the Japanese Unexamined Patent Application Publication No. 2008-24429, an inactive gas is introduced into a sealed type transfer container carried among the processes with semiconductor wafers accommodated therein, to reduce the humidity inside the sealed type transfer container more than the humidity of the environment such as a clean room, thereby avoiding the above-mentioned pattern deformation. 
     The paragraph [0118] of International Patent Laid-Open No. 2010-125682 (Patent Document 2) discloses that a barrier insulating film BI 1  is formed in a stacked structure of an SiCN film and an SiCO film in order to avoid resist poisoning. In other words, by applying an ammonia plasma treatment on the surface of an interlayer insulating film IL 1  nitrogen existing on the surface of the interlayer insulating film IL 1  and nitrogen included in the SiCN film are chemically reacted together to generate amine, which is diffused to the interlayer insulating film IL 2  on the barrier insulating film BI 1 . Then, the chemical amplification type resist used for forming a wiring groove in the interlayer insulating film IL 2  reacts with the amine, to generate a pattern failure in a photoresist film FR 2 ; however, by providing the SiCO film between the SiCN film and the interlayer insulating film IL 2 , the amine is suppressed from diffusing to the interlayer insulating film IL 2 , thereby avoiding the resist poisoning. 
     SUMMARY 
     Also, in a copper (Cu) wiring structure examined by the inventor et al., similarly to the International Patent Laid-Open No. 2010-125682, a barrier insulating film having a stacked structure of an SiON film and an SiCO film is used. According to the examination by the inventor et al., even when using the barrier insulating film having the stacked structure, it is found that a pattern failure of chemical amplification type resist called resist poisoning occurs also in the photolithography process of forming a wiring groove in an interlayer insulating film on the barrier insulating film. 
     According to the examination by the inventor et al., it is found that the above failure is caused by nitrogen or ammonium ion released from the silicon nitride film remaining on the rear surface of the semiconductor wafer during the manufacturing process of the copper (Cu) wiring. When the silicon nitride film is deposited on the main surface of the semiconductor wafer, for example, in a batch typed Low Pressure Chemical Vapor Deposition (LPCVD) method, the silicon nitride film is also deposited on the rear surface of the semiconductor wafer. In the cleaning step included in the manufacturing process of a semiconductor device, the silicon nitride film formed on the rear surface is not eliminated but remains on the rear surface of the semiconductor wafer, and in this state as it remains, the manufacturing process of a semiconductor device is continued, to complete a semiconductor device. The silicon nitride film is removed in the rear surface polishing process of a semiconductor wafer for thinning the semiconductor wafer. Accordingly, for example, in the manufacturing process of a copper wiring, in a state where the silicon nitride film is formed on the rear surface of the semiconductor wafer, the manufacturing process of the copper wiring is performed. In some cases, a silicon oxide film is formed in the batch typed LPCVD method and the silicon oxide film is deposited also on the rear surface of the semiconductor wafer; however, the silicon oxide film is removed in the above cleaning step. 
     In the manufacturing process of the copper wiring, a semiconductor wafer is carried among the processes, being stored in the sealed type transfer container called FOUP. Since airtightness of the sealed type transfer container is high, for example, when the stored time gets longer because of a trouble of a device, the nitrogen or ammonium ion released from the silicon nitride film remaining on the rear surface of the semiconductor wafer raises the nitrogen concentration or ammonium concentration (hereinafter, described as the ammonium concentration) within the sealed type transfer container. A large amount of the ammonium ion is attached to the main surface of the semiconductor wafer, and it is found that a pattern failure of a chemical amplification type resist, called resist poisoning, occurs in the photolithography process using the chemical amplification type resist. The ammonium ion attached to the main surface of the semiconductor wafer generates amine and disturbs acid generation in the ultraviolet ray exposure portion of the positive chemical amplification type resist, hence to generate a pattern failure while inactivating the chemical amplification type resist. Further, breaking of the copper wiring occurs and the reliability of the semiconductor device is deteriorated. 
     Accordingly, in the manufacturing method of a semiconductor device, a technique for improving the reliability of the semiconductor device is required. 
     Other problems and new features will be apparent from the description and the attached drawings of the specification. 
     According to one embodiment, a semiconductor substrate having a silicon nitride film on its rear surface is prepared, an interlayer insulating film having a via hole on the main surface of the semiconductor substrate is formed, and a first photoresist film is formed selectively within the via hole. Next, the wafer rear surface cleaning is performed to expose the surface of the silicon nitride film formed on the rear surface of the semiconductor substrate, and thereafter, a second photoresist film made of chemical amplification type resist is formed on the interlayer insulating film and the first photoresist film over the main surface of the semiconductor substrate. During these processes, the semiconductor substrate is stored in an atmosphere with the ammonium ion concentration of 1000 μg/m 3  and less. 
     According to one embodiment, the reliability of a semiconductor device can be improved. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is a flowchart showing a part of the manufacturing process of a semiconductor device. 
         FIG. 2  is a flow chart showing a part of the manufacturing process of a semiconductor device following  FIG. 1 . 
         FIG. 3  is a cross-sectional view of an important portion showing the manufacturing process of a semiconductor device. 
         FIG. 4  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 3 . 
         FIG. 5  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 4 . 
         FIG. 6  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 5 . 
         FIG. 7  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 6 . 
         FIG. 8  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 7 . 
         FIG. 9  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 8 . 
         FIG. 10  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 9 . 
         FIG. 11  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 10 . 
         FIG. 12  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 11 . 
         FIG. 13  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 12 . 
         FIG. 14  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 13 . 
         FIG. 15  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 14 . 
         FIG. 16  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 15 . 
         FIG. 17  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 16 . 
         FIG. 18  is a cross-sectional view of the important portion showing the manufacturing process of a semiconductor device following  FIG. 17 . 
         FIG. 19  is a cross-sectional view showing the stored state of a semiconductor device in the manufacturing processes. 
         FIG. 20  is a cross-sectional view of an important portion showing the manufacturing process of a semiconductor device according to a considered example. 
         FIG. 21  is a view showing a relation between disconnection of wiring and ammonium concentration. 
         FIG. 22  is a view showing the effect of the embodiment. 
     
    
    
     DETAILED DESCRIPTION 
     The following embodiments will be described, if necessary, for the sake of convenience, divided into a plurality of sections or embodiments; except for the specified case, they are mutually related to each other and one is a part or the whole of the other modified example, details, and additional description. In the following description, when referring to the number of elements (including the number of units, numeric value, amount, range), except for the case particularly specified and the case of apparently restricted to a specified number in principle, they are not restricted to the specified number but may be more or less than the specified number. Further, in the following embodiments, it is needless to say that the component elements (including the element step) are not always required, except for the case particularly specified and the case apparently required in principle. Similarly, in the following embodiments, when referring to the shape and the positional relation of the component elements, they are to include their similar or like shapes, except for the case particularly specified and the case apparently different in principle. This is true to the above number and the range. 
     Hereinafter, the embodiments will be described in detail with reference to the drawings. In all the drawings for describing the embodiments, the same reference numerals and symbols are attached to the materials having the same functions and their repeated description is omitted. Further, in the following embodiments, the description about the same or similar portion is not repeated except for the case especially required. 
     In the drawings used for the embodiments, even if in a cross-sectional view, hatching may be sometimes omitted for the sake of simplicity. On the contrary, even if in a plan view, hatching may be performed for the sake of easy understanding of the view. 
     Embodiment 
     A semiconductor device according to an embodiment includes a plurality of Meta Insulator Semiconductor Field Effect Transistors (MISFET). The MISFETs include n-type MISFET Qn and p-type MISFET Qp. A semiconductor device is formed in a rectangular chip region and a plurality of chip regions are arranged on the semiconductor wafer in a matrix shape. A plurality of semiconductor devices are formed on one semiconductor wafer. 
       FIGS. 1 and 2  are flow views showing a part of the manufacturing process of a semiconductor device, and  FIGS. 3 to 18  are cross-sectional views of an important portion showing the manufacturing process of a semiconductor device.  FIG. 19  is a view showing the stored state among the manufacturing processes of a semiconductor device.  FIG. 20  is a cross-sectional view of an important portion showing the manufacturing process of a semiconductor device in a considered example. 
     At first, as shown in  FIG. 3 , a semiconductor substrate  1 S (semiconductor wafer WF), for example, made of silicon is prepared (Step S 1  in  FIG. 1 ). In the embodiment, although the description is made using the word “semiconductor substrate  1 S”, it can be replaced with the word “semiconductor wafer WF”. The word of the semiconductor wafer WF is sometimes used here. The semiconductor substrate  1 S includes a main surface and a rear surface and the plan shape is circular (substantially circular). The main surface and the rear surface of the semiconductor substrate  1 S are circular. As shown in  FIG. 3 , the semiconductor substrate  1 S has an n-type MISFET Qn and a p-type MISFET Qp. For example, on the surface (main surface) of the p-type semiconductor substrate  1 S, a p-type well layer PW that is a p-type semiconductor region and an n-type well layer NW that is an n-type semiconductor region are formed. Actually, within the p-type well layer PW, a plurality of n-type MISFETs Qn are formed and within the n-type well layer NW, a plurality of p-type MISFETs Qp are formed. On the surface of the semiconductor substrate  1 S, an element isolation film STI made of a silicon oxide film is formed to electrically isolate the n-type MISFETs Qn and the p-type MISFETs Qp, or the n-type MISFET Qn and the p-type MISFET Qp. 
     The n-type MISFET Qn includes a gate electrode GN formed on the main surface of the semiconductor substrate  1 S through the gate insulating film GI and a source region and drain region formed on the main surface of the semiconductor substrate  1 S at the both ends of the gate electrode GN. Each of the source region and the drain region includes an n-type low concentration semiconductor layer NM and an n-type high concentration semiconductor layer NH, and a silicide layer SIL is formed on the surface of the n-type high concentration semiconductor layer NH. The silicide layer SIL is formed also on the surface of the gate electrode GN. A sidewall insulating film SW is formed on the sidewall of the gate electrode GN. The n-type low concentration semiconductor layer NM and the n-type high concentration semiconductor layer NH are in the n-type semiconductor region and the n-type high concentration semiconductor layer NH is higher than the n-type low concentration semiconductor layer NM in the dopant concentration. 
     Further, the p-type MISFET Qp includes a gate electrode GP formed on the main surface of the semiconductor substrate  1 S through the gate insulating film GI and a source region and drain region formed on the main surface of the semiconductor substrate  1 S at the both ends of the gate electrode GP. Each of the source region and the drain region includes a p-type low concentration semiconductor layer PM and a p-type high concentration semiconductor layer PH, and the silicide layer SIL is formed on the surface of the p-type high concentration semiconductor layer PH. Further, the silicide layer SIL is formed on the surface of the gate electrode GP. Further, the sidewall insulating film SW is formed on the sidewall of the gate electrode GP. The p-type low concentration semiconductor layer PM and the p-type high concentration semiconductor layer PH are in the p-type semiconductor region and the p-type high concentration semiconductor layer PH is higher than the p-type low concentration semiconductor layer PM in the dopant concentration. 
     The silicide layer SIL of the n-type MISFET Qn and the p-type MISFET Qp is made of cobalt silicide (CoSi), titanium silicide (TiSi), nickel silicide (NiSi), or platinum containing nickel silicide (PtNiSi). The sidewall insulating film SW is formed by a silicon nitride film, or a stacked film including a silicon oxide film and a silicon nitride film. 
     Next, as shown in  FIG. 4 , an insulating film IF is formed over the semiconductor substrate  1 S (Step S 2  in  FIG. 1 ). The insulating film IF is formed to cover the n-type MISFET Qn and the p-type MISFET Qp. Specifically, it is formed to cover the silicide layers SIL of the n-type MISFET Qn and the p-type MISFET Qp and the sidewall insulating films SW. The insulating film IF is formed of a silicon nitride film according to the LPCVD method with dichlorsilane (SiH 2 Cl 2 ) and ammonia (NH 3 ) used as a source gas. By using the LPCVD method, a silicon nitride film can be a film of high covering property and high density. Further, as the insulating film IF, a silicon nitride film having tensile stress or compression stress can be also used. When the insulating film IF (silicon nitride film) is formed according to the LPCVD method, the silicon nitride film is also formed on the rear surface of the semiconductor substrate  1 S. 
     As shown in  FIG. 4 , a contact interlayer insulating film CIL is formed on the insulating film IF on the side of the main surface of the semiconductor substrate  1 S (Step S 3  in  FIG. 1 ). The contact interlayer insulating film CIL is formed of a silicon oxide film with a film thickness more than the insulating film IF, according to the Plasma-Enhanced Chemical Vapor Deposition (PECVD) method (plasma CVD method). When using the plasma CVD method, since film formation is performed with the rear surface of the semiconductor substrate  1 S mounted on a stage, any contact interlayer insulating film CIL is not formed on the rear surface of the semiconductor substrate  1 S but the insulating film IF (silicon nitride film) is exposed on the rear surface of the semiconductor substrate  1 S. 
     Next, as shown in  FIG. 5 , by using the photolithography technique and the etching technique, a contact hole CNT is formed in the contact interlayer insulating film CIL and the insulating film IF. This contact hole CNT is processed to penetrate the contact interlayer insulating film CIL and the insulating film IF and arrive at the silicide layer SIL formed on the surface of the source region and the drain region of the n-type MISFET Qn and the p-type MISFET Qp. In the forming process of the contact hole CNT, under the condition that the etching rate of the contact interlayer insulating film CIL is higher, as for the insulating film IF, the contact hole CNT is formed in the contact interlayer insulating film CIL, and thereafter etching is performed under the condition that the insulating film IF is etched. In short, the insulating film IF works as an etching stopper. By making the insulating film IF of a silicon nitride film formed according to the LPCVD method, an etching selection ratio to the contact interlayer insulating film CIL can be fully enhanced. 
     Next, as shown in  FIG. 6 , by embedding a metal film in the contact hole CNT formed in the contact interlayer insulating film CIL, a plug PLG 1  is formed (Step S 4  in  FIG. 1 ). Specifically, a titanium/titanium nitride film as a barrier conductor film is formed on the contact interlayer insulating film CIL with the contact hole CNT formed there, for example, according to the sputtering method. A tungsten film is formed on the titanium/titanium nitride film. According to this, the titanium/titanium nitride film is formed in the inner wall (sidewall and bottom) of the contact hole CNT, and a tungsten film is formed on the titanium/titanium nitride film to fill the contact hole CNT. Thereafter, only the unnecessary titanium/titanium nitride film and tungsten film formed on the contact interlayer insulating film CIL is removed according to the Chemical Mechanical Polishing (CMP) method. This can form the plug PLG 1  having the titanium/titanium nitride film and the tungsten film embedded only within the contact hole CNT. The titanium/titanium nitride film and the tungsten film are not formed on the side of the rear surface of the semiconductor substrate  1 S. 
     As shown in  FIG. 7 , an interlayer insulating film IL 1  is formed on the contact interlayer insulating film CIL with the plug PLG 1  formed there (Step S 6  in  FIG. 1 ). This interlayer insulating film IL 1  is formed of, for example, a silicon oxide film, for example, according to the plasma CVD method. 
     Next, before forming a wiring groove WD 1  described later, scrub cleaning  1  is performed on the main surface and the rear surface of the semiconductor substrate  1 S (Step S 7  in  FIG. 1 ). In the scrub cleaning  1 , a rotary blush is operated while running pure water on the main surface and the rear surface of the semiconductor substrate  1 S, hence to remove the fine particle (debris) attached to the main surface and the rear surface. 
     Next, wafer rear surface cleaning  1  is performed on the rear surface of the semiconductor substrate  1 S (Step S 8  in  FIG. 1 ). In the process of the wafer rear surface cleaning  1 , Sulfuric acid Peroxide Mixture (SPM) cleaning and Fluoride acid Peroxide Mixture (FPM) cleaning are performed in this order. The wafer rear surface cleaning  1  is performed only on the rear surface of the semiconductor substrate  1 S, in a way of avoiding the cleaning liquid from intruding into the main surface of the semiconductor substrate  1 S. The SPM cleaning is to remove an organic substance, using the mixed liquid of sulfuric acid and hydrogen peroxide. Further, the FPM cleaning is to remove metal contamination, using the mixed liquid of hydrofluoric acid and hydrogen peroxide. Here, instead of the SPM cleaning, Ammonia-Hydrogen Peroxide Mixture (APM) cleaning may be used, or instead of the FPM cleaning, Diluted Hydrofluoric acid (DHF) cleaning may be used. The APM cleaning is to remove the organic substance using the mixed liquid of ammonia and hydrogen peroxide, and the DHF cleaning is to remove the metal contamination using the mixed liquid of hydrofluoric acid and hydrogen peroxide. The FPM cleaning and the DHF cleaning are to remove the oxide film and can remove the metal attached to the oxide film together with the oxide film. Alternatively, the metal intruded into the oxide film can be removed by being suspended. Here, the SPM cleaning and the FPM cleaning can avoid a so-called cross contamination. 
     As shown in  FIG. 8 , by using the photolithography technique and the etching technique, a wiring groove WD 1  is formed in the interlayer insulating film IL 1  (Step S 9  in  FIG. 1 ). The wiring groove WD 1  is formed so that it may penetrate the interlayer insulating film IL 1  made of a silicon oxide film and arrive at the contact interlayer insulating film CIL in its bottom surface. According to this, the surface (top surface) of the plug PLG 1  is exposed in the bottom of the wiring groove WD 1 . 
     As shown in  FIG. 10 , a wiring L 1  is formed within the wiring groove WD 1  (Step S 10  in  FIG. 1 ). At first, as shown in  FIG. 9 , a barrier conductor film (copper diffusion prevention film) BCF 1  is formed on the interlayer insulating film IL 1  with the wiring groove WD 1  formed there. Specifically, the barrier conductor film BCF 1  is made of tantalum (Ta), titanium (Ti), ruthenium (Ru), tungsten (W), manganese (Mn), their nitride, their silicide nitride, or their stacked film, for example, according to the sputtering method. 
     Continuously, for example, a seed film made of a thin copper film is formed on the barrier conductor film BCF 1  formed inside the wiring groove WD 1  and on the interlayer insulating film IL 1 , according to the sputtering method. Then, a copper film CF 1  is formed according to the electrolytic plating method with the seed film used as an electrode. The copper film CF 1  is formed in a stacked structure of the seed film and a plating film. The copper film CF 1  is formed in a way of filling the wiring groove WD 1 . The copper film CF 1  is formed of a film mainly including, for example, copper. Specifically, it is formed of copper (Cu) or copper alloy (alloy of copper (Cu) and aluminum (Al), magnesium (Mg), titanium (Ti), manganese (Mn), iron (Fe), zinc (Zn), zirconium (Zr), niobium (Nb), molybdenum (Mo), ruthenium (Ru), palladium (Pd), silver (Ag), gold (Au), In (indium), lanthanide metal, or actinoid-based metal). In the case of the copper alloy, since the seed film is the alloy as mentioned above, the copper film CF 1  becomes the copper alloy. The copper alloy described later is similarly made. 
     The barrier conductor film BCF 1 , the seed film, and the copper film CF 1  are not formed on the rear surface of the semiconductor substrate  1 S. 
     Continuously, as shown in  FIG. 10 , the unnecessary barrier conductor film BCF 1  and copper film CF 1  formed on the interlayer insulating film IL 1  are removed according to the CMP method. According to this, the wiring L 1  with the barrier conductor film BCF 1  and the copper film CF 1  embedded into the wiring groove WD 1  can be formed. The barrier conductor film BCF 1  and the copper film CF 1  between the wirings L 1  are removed by the CMP method and the mutually adjacent wirings L 1  are electrically isolated. In short, the main surface of the interlayer insulating film IL 1  positioned between the adjacent wirings L 1  is exposed according to the CMP method. 
     Continuously, the ammonia plasma treatment is performed on the surface of the interlayer insulating film IL 1  with the wiring L 1  formed there, to clean the surface of the wiring L 1  and the surface of the interlayer insulating film IL 1 . 
     Next, as shown in  FIG. 11 , a barrier insulating film BIF is formed on the wiring L 1  and the interlayer insulating film IL 1  (Step S 11  in  FIG. 1 ). The barrier insulating film BIF is made by a stacked film of an SiCN film SCN and an SiCO film SCO. The SiCN film SCN is formed on the wiring L 1  and the interlayer insulating film IL 1  according to the plasma CVD method with the tetramethyl silane gas and the ammonia gas used as the material gas. The SiCN film SCN is a copper diffusion prevention film of the copper film CF 1  forming the wiring L 1 . According to the above mentioned ammonia plasma treatment, adhesion between the SiCN film SCN and the interlayer insulating film LI 1  is improved and Time Dependent Dielectric Breakdown (TDDB) characteristic between the adjacent wirings L 1  is improved. In short, a leak current between the adjacent wirings L 1  can be reduced. 
     Further, the SiCO film SCO can be formed, for example, according to the plasma CVD method. The SiCO film SCO is provided in order to avoid the nitrogen or ammonium ion included in the SiCN film SCN from diffusing to a photoresist film PR 3  described later. In short, the SiCO film SCO is to avoid the resist poisoning caused by the inactiveness of the photoresist film PR 3  in the photolithography process. 
     Any SiCN film SCN and SiO film SCO are not formed (deposited) on the rear surface of the semiconductor substrate  1 S. 
     Next, as shown in  FIG. 12 , an interlayer insulating film IL 2  is formed on the barrier insulating film BIF and a damage protective film DP is formed on the interlayer insulating film IL 2  (Step S 12  in  FIG. 1 ). More specifically, the interlayer insulating film IL 2  is formed of, for example, an SiOC film having holes of lower dielectric constant than the silicon oxide film, an HSQ film having holes, or an MSQ film having holes. The SiOC film having the holes can be formed, for example, using the plasma CVD method. The damage protective film DP is formed of, for example, a tetra ethyl ortho silicate (TEOS) film, or a silicon oxide film, for example, according to the plasma CVD method. The damage protective film DP is higher than the interlayer insulating film IL 2  in film density and mechanical intensity. 
     Next, before forming a photoresist film PR 1  described later, scrub cleaning  2  is performed on the main surface and the rear surface of the semiconductor substrate  1 S (Step S 13  in  FIG. 2 ). The scrub cleaning  2  is performed similarly to the above mentioned scrub cleaning  1 . 
     This time, wafer rear surface cleaning  2  is performed on the rear surface of the semiconductor substrate  1 S (Step S 14  in  FIG. 2 ). The wafer rear surface cleaning  2  is performed similarly to the wafer rear surface cleaning  1 . 
     As shown in  FIG. 13 , a photoresist film PR 1  made of a chemical amplification type resist is formed on the damage protective film DP (Step S 15  in  FIG. 2 ). The chemical amplification type resist is applied to the damage protective film DP and by performing the exposure and development treatment, the chemical amplification type resist is patterned to form the photoresist film PR 1 . The patterning is performed to bore each region to form a via hole VH. Thereafter, with a mask of the patterned photoresist film PR 1 , the damage protective film DP and the interlayer insulating film IL 2  are etched. Thus, the via holes VH to expose the SiCO film SCO are formed by penetrating the damage protective film DP and the interlayer insulating film IL 2  (Step S 16  in  FIG. 2 ). This SiCO film SCO works as the etching stopper in the etching. 
     Next, as shown in  FIG. 14 , a via-fill PR 2  (via-fill film PR 2 ) is formed only within the via hole VH (Step S 17  in  FIG. 2 ). The via-fill PR 2  is an organic film made of the substantially same material as that of the photoresist films PR 1  and PR 3  and can be removed according to the plasma ashing treatment. At first, the via-fill PR 2  is formed over the semiconductor substrate  1 S to completely fill the via hole VH, and the via-fill PR 2  is formed within the via hole VH and on the damage protective film DP. Next, the plasma ashing treatment is performed on the via-fill PR 2 , using a gas such as ozone (O 3 ) or oxygen (O 2 ), and the via-fill PR 2  for the same film thickness as the via-fill PR 2  on the damage protective film DP is selectively removed through the plasma ashing treatment. Here, the via-fill PR 2  on the damage protective film DP is completely removed but the plasma ashing treatment does not affect the via-fill PR 2  within the via hole VH and it is important to selectively leave the via-fill PR 2  within the via hole VH. 
     In the above mentioned forming process of the photoresist film PR 1  and the via-fill PR 2 , the photoresist film PR 1  and the via-fill PR 2  are not formed on the rear surface of the semiconductor substrate  1 S. Since the plasma asking treatment is performed in a state where the rear surface of the semiconductor substrate  1 S is exposed, the surface of the silicon nitride film formed on the rear surface of the semiconductor substrate  1 S is oxidized, to form a natural oxide. 
     Before a photoresist film PR 3  described later is formed, scrub cleaning  3  is performed on the main surface and the rear surface of the semiconductor substrate  1 S (Step S 18  in  FIG. 2 ). The scrub cleaning  3  is performed similarly to the above mentioned scrub cleaning  1 . 
     Next, wafer rear surface cleaning  3  is performed on the rear surface of the semiconductor substrate  1 S (Step S 19  in  FIG. 2 ). The wafer rear surface cleaning  3  is performed similarly to the wafer rear surface cleaning  1 . In the SPM cleaning process of the wafer rear surface cleaning  3 , the surface of the silicon nitride film formed on the rear surface of the semiconductor substrate  1 S is oxidized to form a natural oxide, and thereafter, when the FPM cleaning is performed, the natural oxide (oxide film) on the surface of the silicon nitride film is removed and the surface of the silicon nitride film gets into an exposed state. 
     Next, as shown in  FIG. 15 , a photoresist film PR 3  as a mask for forming a wiring groove WD 2  described later is formed on the damage protective film DP (Step S 20  in  FIG. 2 ). A positive chemical amplification type resist is applied to the via-fill PR 2  within the via hole VH and on the damage protective film DP (application process), and a heating treatment before exposure is performed there to vaporize the organic solvent (heating process before exposure). Then, the exposure process is performed. Specifically, the region to form the wiring groove WD 2  described later is irradiated with ultraviolet ray by an excimer laser. Then, when a heating treatment after exposure is performed on the chemical amplification type resist, deprotection reaction proceeds in the irradiated region of ultraviolet ray (exposure region) and into a molecular structure dissolvable into alkali developing solution (heating process after exposure). The chemical amplification type resist in the irradiated region is removed through the developing processing, hence to form the photoresist film PR 3  having each aperture corresponding to each wiring groove WD 2  described later (development process). Here, the wiring groove WD 2  is formed on the via hole VH. In plan view, the via hole VH has a circular, the width of the wiring groove WD 2  is the diameter of the via hole VH and more, and the length of the wiring groove WD 2  is more (longer) than the diameter of the via hole VH. 
     Then, as shown in  FIG. 16 , using the etching technique, the wiring groove WD 2  is formed on the interlayer insulating film IL 2  and the damage protective film DP (Step S 21  in  FIG. 2 ). Specifically, the patterned photoresist film PR 3  shown in  FIG. 15  is used as a mask to perform the anisotropy dry etching and the respective wiring grooves WD 2  are formed on the damage protective film DP and the interlayer insulating film IL 2 . Before application of the chemical amplification type resist, an anti-reflection film made of an organic film such as Bottom Antireflective Coating (BARC) may be provided on the damage protective film DP. 
     After forming the wiring groove WD 2 , the via-fills PR 2  and PR 3  are removed by the plasma ashing treatment. When provided with the anti-reflection film, the anti-reflection film is also removed by the plasma ashing treatment. Then, the barrier insulating film BIF exposed to the via hole VH is removed by the dry etching technique (Step S 22  in  FIG. 2 ), to expose the top surface of the wiring L 1 . The damage protective film DP as an insulating film having a higher density than the interlayer insulating film IL 2  is provided on the interlayer insulating film IL 2 , which can avoid or decrease the following problems in the dry etching process. Specifically, when the damage protective film DP is not formed, there occur the following problems: since the dry etching treatment is performed on the surface of the interlayer insulating film IL 2  having a low density, the surface of the interlayer insulating film IL 2  gets rough, and since the surface is etched, the film thickness of the interlayer insulating film IL 2  is decreased. 
     As shown in  FIG. 17 , a barrier conductor film (copper diffusion protective film) BCF 1  is formed inside the wiring groove WD 2  and the via hole VH and on the damage protective film DP. Specifically, the barrier conductor film BCF 1  is made of tantalum (Ta), titanium (Ti), ruthenium (Ru), tungsten (W), manganese (Mn), their nitride, their silicide nitride, or their stacked film, for example, according to the sputtering method. Continuously, for example, a seed film made of a thin copper film is formed on the barrier conductor film BCF 2  formed inside the wiring groove WD 2  and on the damage protective film DP, according to the sputtering method. Then, a copper film CF 2  is formed with this seed film used as the electrode according to the electrolytic plating method. The copper film CF 2  is formed in a stacked structure including the seed film and the plating film, to fill the wiring groove WD 2 . This copper film CF 2  is formed of, for example, a film mainly including copper. Specifically, it is formed of copper (Cu) or copper alloy (alloy of copper (Cu) and aluminum (Al), magnesium (Mg), titanium (Ti), manganese (Mn), iron (Fe), zinc (Zn), zirconium (Zr), niobium (Nb), molybdenum (Mo), ruthenium (Ru), palladium (Pd), silver (Ag), gold (Au), In (indium), lanthanide metal, or actinoid-based metal). 
     As shown in  FIG. 18 , the unnecessary barrier conductor film BCF 2  and copper film CF 2  formed on the damage protective film DP are removed by the CMP method. Here, the damage protective film DP is also removed by the CMP method, a wiring L 2  formed by embedding the barrier conductor film BCF 2  and the copper film CF 2  into the wiring groove WD 2  and a plug electrode PLG 2  formed by embedding the barrier conductor film BCF 2  and the copper film CF 2  into the via hole VH can be formed (Step S 23  in  FIG. 2 ). In other words, only the interlayer insulating film IL 2  having a low dielectric constant is left between the wirings L 2  and the parasitic capacitance between the adjacent wirings L 2  can be reduced. By having provided with the damage protective film DP, the CMP polishing damage on the surface of the interlayer insulating film IL 2  between the wirings L 2  can be avoided (reduced) and a leak current between the wirings L 2  can be reduced when removing the copper film CF 2  and the barrier conductor film BCF 2  according to the CMP polishing. 
     By repetition of the processes from Step S 11  in  FIG. 1  to Step S 23  in  FIG. 2 , a multi layer wiring can be formed above the wiring L 2 . 
     During a period from the completion of the above mentioned wafer rear surface cleaning  3  (especially, the FPM cleaning) in Step S 19  to the photoresist film PR 3  formation process in Step S 20 , the semiconductor substrate  1 S (semiconductor wafer WF) is accommodated in the sealed type transfer container FP including purge holes PG 1  and PG 2  shown in  FIG. 19 . The sealed type transfer container FP is the container capable of accommodating, for example, 24 sheets of semiconductor wafers having a diameter of 300 mm with a door (open-and-close window). In the closed state of the door, airtightness is kept inside the sealed type transfer container FP. 
     In the embodiment, it is important that the sealed type transfer container FP is purged with a nitrogen (N 2 ) gas, in order to keep the inside of the sealed type transfer container FP at a desired atmosphere. In other words, a nitrogen (N 2 ) gas is inserted into the sealed type transfer container FP through the purge hole PG 1  and exhausted from the purge hole PG 2 , hence to keep (control) the concentration of ammonium ion (NH 4   + ) inside the sealed type transfer container FP at 1000 μg/m 3  and less. As mentioned above, the semiconductor substrate  1 S is carried among the processes, being accommodated into the sealed type transfer container FP; unless otherwise specified, the sealed type transfer container FP is not purged with the nitrogen (N 2 ) gas. 
     This time, a problem in the case of no control (no purge with nitrogen) performed on the concentration of the ammonium ion (NH 4   + ) within the sealed type transfer container FP will be described. 
     As mentioned above, at a time of finishing the wafer rear surface cleaning  3  (especially, the FPM cleaning) in Step S 19 , the natural oxide (oxide film) on the surface of the silicon nitride film formed on the rear surface of the semiconductor substrate  1 S is removed and the surface of the silicon nitride film is exposed. In other words, since the ammonium ion (NH 4   + ) is constantly exhausted from the silicon nitride film, the concentration of the ammonium ion (NH 4   + ) within the sealed type transfer container FP rises. The ammonium ion (NH 4   + ) intrudes into the via-fill PR 2  formed on the main surface of the semiconductor substrate  1 S, to form amine. In short, the via-fill PR 2  formed in the via hole VH in  FIG. 14  contains a large amount of amine. 
     As mentioned above using  FIG. 15 , although a positive chemical amplification type resist is formed on the via-fill PR 2  formed within the via hole VH, to form the photoresist film PR 3  having opening portions corresponding to the respective wiring grooves WD 2 , the amine included in the via-fill PR 2  is diffused and intruded into the chemical amplification type resist, hence to disturb the deprotection reaction in the exposure region and after the development process, a part of the chemical amplification type resist is left without being removed, although it is in the exposure region. Accordingly, when performing the anisotropy dry etching on the damage protective film DP and the interlayer insulating film IL 2  with the photoresist film PR 3  used as the mask, there is a problem that the original wiring groove WD 2  is not formed, as shown in  FIG. 20 . Further, after removing the via-fill PR 2  and the photoresist film PR 3  by the plasma ashing treatment, there arises a problem that breaking occurs in the wiring L 2  when forming the wiring L 2  and the plug electrode PLG 2  within the wiring groove WD 2  and the via hole VH. In other words, because of the ammonium ion included in the silicon nitride film formed on the rear surface of the semiconductor substrate  1 S, resist poisoning occurs in the chemical amplification type resist and the breaking of the wiring L 2  occurs. The left portion in  FIG. 20  indicates the case of the photoresist film PR 3  normally formed and the right portion indicates the case of the photoresist film PR 3  not normally formed with occurrence of a bad resolution. 
     The inventor et al. come to arrive at the following view as the result of consideration to a relation between the ammonium ion (NH 4   + ) within the sealed type transfer container FP and the breaking. 
       FIG. 21  is a view showing a relation between the breaking of the wiring L 2  and the ammonium ion (NH 4   + ) concentration within the sealed type transfer container FP. The case of storing twelve semiconductor wafers WF within the sealed type transfer container FP is compared with the case of storing twenty four wafers. The semiconductor wafer WF is in a state of having been subjected to the above mentioned wafer rear surface cleaning  3  (especially, the FPM cleaning) in Step S 19 , before the photoresist film PR 3  forming process in Step S 20 , and the sealed type transfer container FP is hermetically closed without being purged with the nitrogen (N 2 ). 
     In the case of storing the twelve semiconductor wafers WF within the sealed type transfer container FP, the ammonium ion (NH 4   + ) concentration rises from the start of the store, arriving at the maximum of about 900 μg/m 3  on the fourth day, then, the ammonium ion is absorbed by the via-fill PR 2  on the main surface of the semiconductor substrate  1 S, and the concentration is reduced. No breaking is found in the twelve semiconductor wafers WF. 
     On the other hand, in the case of storing the twenty four semiconductor wafers WF within the sealed type transfer container FP, the ammonium ion (NH 4   + ) concentration rises continuously from the start of the store and arrives at 2000 μg/m 3  and more on the second day from the start. Breaking is found in the semiconductor wafers WF stored for the two days and more from the start. In  FIG. 21 , breaking is confirmed in the hatched region exceeding the ammonium ion (NH 4   + ) concentration of 1000 μ/m 3 . 
     From the above result, in order to avoid the breaking, it is important that the ammonium ion (NH 4   + ) concentration within the sealed type transfer container FP should be kept (controlled) at 1000 μg/m 3  and less. 
     In the embodiment, it is important that after having been subjected to the wafer rear surface cleaning  3  (especially, the FPM cleaning) in Step S 19 , the semiconductor substrate  1 S (semiconductor wafer WF) before the photoresist film PR 3  forming process in Step S 20  should be kept in an atmosphere with the ammonium ion (NH 4   + ) concentration of 1000 μg/m 3  and less. The sealed type transfer container FP may be purged with an inactive gas such as argon (Ar) instead of nitrogen (N 2 ), hence to control the ammonium ion concentration within the sealed type transfer container FP. 
     According to the embodiment, the following effects can be obtained. 
     After performing the wafer rear surface cleaning  3  on the rear surface of the semiconductor substrate  1 S, the semiconductor substrate  1 S is stored within the sealed type transfer container FP and the ammonium ion concentration within the sealed type transfer container FP is controlled at 1000 μg/m 3  and less. According to this, it is possible to avoid the breaking of the wiring L 2  generated by the resist poisoning of the photoresist film PR 3  made of a positive chemical amplification type resist and improve the reliability of the semiconductor device. 
     Since the FPM cleaning is performed in the wafer rear surface cleaning  3 , it is possible to avoid (reduce) the cross contamination in the manufacturing process of a semiconductor device and improve the manufacturing yield of the semiconductor device. 
     By controlling the ammonium ion (NH 4   + ) concentration within the sealed type transfer container FP, it is possible to avoid a failure of the in-process product caused by a trouble of a device. Even when the semiconductor substrate  1 S having been subjected to the wafer rear surface cleaning  3  is stored within the sealed type transfer container FP for a long time, the ammonium ion (NH 4   + ) concentration does not excessively rise; there is no need to worry about the breaking of the wiring L 2  caused by the resist poisoning. 
     As described by using  FIG. 13 , the photoresist film PR 1  made of the chemical amplification type resist is used in forming the via hole VH, the wafer rear surface cleaning  2  is performed also before forming the photoresist film PR 1 , and the surface of the silicon nitride film formed on the rear surface of the semiconductor substrate  1 S is exposed. During the period from the wafer rear surface cleaning  2  to the photoresist film PR 1  formulation, the semiconductor substrate  1 S is stored within the sealed type transfer container FP. In the patterning of the photoresist film PR 1 , however, the resist poisoning phenomenon is not found. 
     This can derive the assumption that the resist poisoning occurs in the photoresist film PR 3  effected by the via-fill PR 2  embedded into the via hole VH, when forming the wiring groove WD 2 . In other words, the ammonium ion (NH 4   + ) released from the rear surface of the semiconductor substrate  1 S intrudes into the via-fill PR 2  made of an organic film and a large amount of amine is generated; as the result, the resist poisoning occurs in the photoresist film PR 3 . The embodiment is effective especially in the case of the via-fill PR 2  (organic film) in direct contact with the photoresist film PR 3  existing in the lower layer. 
     Modified Example 1 
     In a modified example 1, a scrub cleaning treatment while running pure water is performed on the rear surface of the semiconductor substrate is, continued to the wafer rear surface cleaning  3  in Step S 19  in  FIG. 2 . In short, after sequentially performing the SPM cleaning and the FPM cleaning as the wafer rear surface cleaning  3  in Step  19 , the pure water scrub cleaning is additionally performed on the rear surface of the semiconductor substrate  1 S, and thereafter, the semiconductor substrate  1 S is stored in the sealed type transfer container FP. Then, during the photoresist film PR 3  forming process in Step S 20 , it is stored in the sealed type transfer container FP, with no need to manage the ammonium ion (NH 4   + ) concentration within the sealed type transfer container FP. In short, there is no need to purge the sealed type transfer container FP with the nitrogen (N 2 ). 
     As mentioned above, after the FPM cleaning of the wafer rear surface cleaning  3 , the silicon nitride film on the rear surface of the semiconductor substrate  1 S is exposed; however, by performing the pure water scrub cleaning, a thin silicon oxide film can be formed on the surface of the silicon nitride film, hence to avoid (reduce) the ammonium ion from exhausting from the silicon nitride film. Therefore, even when the semiconductor substrate  1 S is stored in the sealed type transfer container FP without purge with the nitrogen (N 2 ), the ammonium ion (NH 4   + ) concentration within the sealed type transfer container FP can be kept at 1000 μg/m 3  and less, hence to avoid the breaking of the wiring L 2 . 
     Needless to say, the semiconductor substrate  1 S having been subjected to the pure ware scrub cleaning may be stored in the sealed type transfer container FP purged with the nitrogen (N 2 ). When carbon dioxide (CO 2 ) mixed pure water, ozone (O 3 ) water, or hydrogen peroxide (H 2 O 2 ) is used, instead of pure water, the same effect can be obtained. 
     Modified Example 2 
     In a modified example 2, the wafer rear surface cleaning  3  in Step S 19  in  FIG. 2  includes only the SPM cleaning and does not include the FPM cleaning. In short, after performing the SPM cleaning as the wafer rear surface cleaning  3  in Step S 19 , the semiconductor substrate  1 S is stored in the sealed type transfer container FP. Until the photoresist film PR 3  forming process in Step S 20 , it is stored in the sealed type transfer container FP. Also in this case, there is no need to control the ammonium ion (NH 4   + ) concentration within the sealed type transfer container FP. In other words, the sealed type transfer container FP does not have to be purged with the nitrogen (N 2 ). 
     Since the SPM cleaning is included in the wafer rear surface cleaning  3 , the surface of the silicon nitride film on the rear surface of the semiconductor substrate  1 S is in a state of being covered with a thin silicon oxide film, which can avoid (suppress) the ammonium ion from exhausting from the silicon nitride film. Even when the semiconductor substrate  1 S is stored in the sealed type transfer container FP without purge with the nitrogen (N 2 ), the ammonium ion (NH 4   + ) concentration can be kept at 1000 μg/m 3  and less within the sealed type transfer container FP, which can avoid the breaking of the wiring L 2 . 
     Needless to say, the semiconductor substrate  1 S just after the SPM cleaning may be stored in the sealed type transfer container FP purged with the nitrogen (N 2 ). 
       FIG. 22  is a view showing the effect of the embodiment (including the modified examples 1 and 2). In the horizontal axis in  FIG. 22 , (A) shows the example of storing the semiconductor substrate  1 S having been subjected to the wafer rear surface cleaning  3 , in the sealed type transfer container FP purged with the nitrogen (N 2 ), (B) shows the example of storing the semiconductor substrate  1 S having been subjected to the pure water scrub cleaning after the wafer rear surface cleaning  3 , in the sealed type transfer container FP without purge of the nitrogen (N 2 ), (C) shows the example of storing the semiconductor substrate  1 S having been subjected to only the SPM cleaning of the wafer rear surface cleaning  3 , in the sealed type transfer container FP without purge of the nitrogen (N 2 ), and (D) shows the example (conventional example) of storing the semiconductor substrate  1 S having been subjected to the wafer rear surface cleaning  3 , in the sealed type transfer container FP without purge of the nitrogen (N 2 ). With the stored period defined as 4.5 days, it shows the ammonium ion (NH 4   + ) concentration in the sealed type transfer container FP, in each example. In the examples of (A), (B) and (C), the ammonium ion (NH 4   + ) concentration is less than 1000 μg/m 3 , with no occurrence of the breaking of the wiring L 2 , but in the example of (D), the breaking occurs. 
     According to the embodiments (including the modified examples 1 and 2), it is possible to avoid the breaking of the wiring L 2 , hence to improve the reliability of the semiconductor device. 
     As set forth hereinabove, although the invention made by the inventor et al. has been described in detail based on the embodiments, it is needless to say that the invention is not restricted to this embodiments but various modifications are possible without departing from the spirit of the invention. 
     The above embodiments have been described using the example of forming a silicon nitride film on the rear surface of the semiconductor substrate  1 S at a time of forming the insulating film IF working as an etching stopper; however, since a silicon nitride film forming the sidewall insulating film SW is also formed by the LPCVD method, a silicon nitride film is simultaneously formed on the main surface and the rear surface of the semiconductor substrate  1 S. Therefore, the silicon nitride film for the sidewall insulating film SW is sometimes formed also on the rear surface of the semiconductor substrate  1 S and the breaking of the wiring L 2  can be avoided similarly to the embodiments.