Patent Publication Number: US-4094834-A

Title: ABS-formaldehyde novolak

Description:
This is a division of application Ser. No. 492,967, filed July 26, 1974, now U.S. Pat. No. 3,944,510. 
    
    
     The present invention relates to improved shell process foundry resin binders. 
     Phenol-formaldehyde novolak resins as is well known in the art are permanently thermoplastic or fusible resins prepared by condensing phenol with formaldehyde under acid conditions using about 0.5 to 1.0 moles, generally about 0.7 to 0.9 moles, of formaldehyde per mole of phenol. The resins are converted to the infusible condition by adding sufficient hexamethylenetetramine for this purpose. Such phenol-formaldehyde novolaks admixed with hexamethylenetetramine are well known, in the foundry industry. 
     It has now been found that the resistance to peelback of shell process foundry resins containing phenol-formaldehyde novolak resin binders can be improved by incorporating an acrylonitrile-butadiene-styrene (ABS) terpolymer into the novolak. Desirably, the ABS terpolymer is added during the manufacture of the resin. The most desirable time to add the ABS terpolymer is before the novolak is formed. Thus, the ABS terpolymer can be added during distillation, after distillation, after obtaining free formaldehyde or to the phenol before the formaldehyde is added. The latter procedure is preferred. The amount of ABS terpolymer is normally 1 to 10% based on the weight of phenol, preferably between 3 and 8%. Up to 20% of the ABS terpolymer based on the weight of the phenol can be employed with some impairment of properties, particularly in the process of hot coating the sand. 
     The amount of hexamethylenetetramine is not critical and can be that usually employed to cure novolak resins. Thus, there is normally employed 10 to 18% hexamethylenetetramine, preferably 12 to 15%, based on the weight of the novolak. In place of hexamethylenetetramine there can be used other conventional hardening agents for novolaks, e.g., paraformaldehyde. 
     Any of the conventional acids and acidic materials employed to prepare novolak resins can be employed as catalysts, e.g., sulfuric acid, oxalic acid, maleic anhydride, sulfamic acid, phenolsulfonic acid, diethyl sulfate, toluenesulfonic acid (usually employed as the commercial mixture of isomers known as TX acid) and phosphoric acid. 
     While the range of formaldehyde to phenol in the novolak can be within the range mentioned above, it is preferably within the range of 0.7 to 0.83 mole of formaldehyde per mole of phenol with the optimum range being 0.72 to 0.80 mole of formaldehyde per mole of phenol. 
     The foundry flake resins of the present invention also preferably contain conventional materials such as calcium stearate (a mold lubricant) and salicylic acid usually contained in commercial foundry flake resins. The total amount of ABS-novolak to sand is that conventionally used in the art in making novolak coated sand for use in foundry cores. Usually 2 to 5% of the resin, preferably 2 to 3% based on the weight of the sand is employed. 
     The use of the ABS polymer with the novolak resin in preparing the shell process foundry resin has the advantage of materially increasing the resistance to peelback. 
     Peelback is described in Metalcasting Dictionary by the American Foundrymen&#39;s Society as &#34;a problem in shell molding when, upon inverting the hot pattern plate, an insufficiently cured shell sand layer separates from the pattern, curling away before it can harden for stripping.&#34; Essentially, what happens is that coated sand (usually coated with a phenolic novolak and hexamethylenetetramine) is placed against a hot pattern until a desired thickness of cured and partially cured coated sand is built up. When this thickness is reached, the pattern is inverted and the free-flowing, reusable coated sand falls off the pattern and is collected for future use. Underneath this free-flowing layer is a partially cured layer that could peel off the surface. This material is waste and not reusable. The void left in the shell mold wall creates a weak spot and renders the shell mold unusable. Applicants have found that by the addition of one percent of an acrylonitrile-butadiene-styrene (ABS) resin to the novolak, peel back can be minimized if not eliminated. 
     In order to anticipate the peel back characteristics of a batch of coated sand a quality control peel back test has been developed by the industry (see Example 6). During the summer half of the year (mid-April to mid-October) peel back seems to occur more often. Using the peel back test described in Example 6 it is not uncommon to see 30 weight percent peel back with commercial resins. It must be remembered that this test is quite severe. It does not necessarily follow that a resin which shows 30 percent peel back by the quality control test will show thirty percent peel back in the foundry. Generally speaking, the resins will show a lesser amount of peel back in the foundry. However, this depends on a lot of factors such as configuration of the shell mold, ambient conditions such as temperature and relative humidity, pattern temperature, etc. If the coated sand performs well with respect to peel back during the quality control test, one can be reasonably certain it will perform well in the foundry. 
     There can be employed commercially available ABS terpolymers, e.g., Dow 500 and Dow 300. Other suitable ABS terpolymers are those identified below as ABSON 820X13, ABSON 820X14, ABSON 820X15 and ABSON 820X16. ABSON 820X14 has a nitrogen content of 6.6% and the other ABSON terpolymers are of somewhat lower nitrogen content. Other properties of the ABSON terpolymers which are available as powders are set forth below. 
     
         __________________________________________________________________________
ABSON ABS TERPOLYMER RESIN PROPERTIES                                     
                 820X13                                                   
                       820x14                                             
                             820X15                                       
                                   820X16                                 
__________________________________________________________________________
Tensile Strength (psi)                                                    
                 2,900 6,200 5,500 5,800                                  
Ultimate Elongation (%)                                                   
                 200   15    3     3                                      
Izod Impact Strength                                                      
at R.T.          1.7   1.8   7.5   6.5                                    
at -20° F.                                                         
                 1.3   1.4   2.9   1.2                                    
at -40° F.                                                         
                 1.2   0.8   1.9   0.8                                    
Hardness, Rockwell R                                                      
                 70    116   103   106                                    
Hardness, Shore D                                                         
                 66    --    75    73                                     
Heat Deflection Temp.                                                     
264 psi (° F.)                                                     
                 181   203   198   196                                    
Specific Gravity 0.99  1.06  1.04  1.04                                   
Viscosity, Poises × 10.sup.3                                        
Instron Rheometer (225° C) 437° F.                          
at 1000 sec.sup.-1                                                        
                 6.7   3.1   3.4   3.0                                    
at 100 sec.sup.-1                                                         
                 42    15    15    11                                     
at 10 sec.sup.-1 270   53    40    23                                     
at 1 sec .sup.-1 930   110   80    40                                     
Solution Viscosity (Cps)*                                                 
Brookfield at 20 RPM                                                      
10% T.S. in THF, Initial                                                  
                 640   --    38    --                                     
 1 Day           640   --    42    --                                     
30 Days          584   --    50    --                                     
10% T.S. in MEK, Initial                                                  
                 9     --    10.5  --                                     
 1 Day           9     --    11.5  --                                     
30 days          8.5   --    10.0  --                                     
__________________________________________________________________________
 *Values normalized with correction factors for various spindle sizes.    
 
    
     Unless otherwise indicated, all parts and percentages are by weight. 
     In the examples DB-31 Antifoam is a polymethylsilane antifoaming agent produced by Dow Corning. Its use is not essential. 
     Calcium stearate 60% means that the calcium stearate was added as an aqueous dispersion containing 60% solids. 
     EXAMPLE 1 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     DB-31 Antifoam     0.2 Parts                                       
C.     Con. Sulfuric Acid 2.0 Parts                                       
D.     Abson 820 X 14     50.0 Parts                                      
E.     37% Formalin       620.0 Parts                                     
F.     Salicylic Acid     50.0 Parts                                      
G.     Calcium Stearate 60%                                               
                          84.0 Parts                                      
______________________________________                                    
 
    
     Components &#34;A&#34; through &#34;D&#34; were loaded into a reaction vessel set for reflux. The components were heated to 115° and held for 15 minutes, during which time the mixture became homogeneous. The heat was removed and component &#34;E&#34; was added dropwise over a 30- to 60-minute period. Enough heat was used to maintain a reflux. After all of component &#34;E&#34; was added, the batch was held at reflux (100° C.) until the free formaldehyde in the refluxate was less than 0.5%. Three hundred parts of distillate were removed. Components &#34;F&#34; and &#34;G&#34; were then added and the resulting material was distilled to a grindable resin. 
     Ball and Ring Softening Point = 92° C. (ASTM E28-67) Yield = 1205 Parts 
     EXAMPLE 2 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     DB-31 Anti foam    0.2 Parts                                       
C.     Con. Sulfuric Acid 2.0 Parts                                       
D.     Abson 820 X 15     50.0 Parts                                      
E.     37% Formalin       620.0 Parts                                     
F.     Salicylic Acid     50.0 Parts                                      
G.     Calcium Stearate 60%                                               
                          84.0 Parts                                      
______________________________________                                    
 
    
     The reaction procedure is the same as in Example 1. 
     Ball and Ring Softening Point = 104° C. Yield = 1180 Parts 
     EXAMPLE 3 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     DB-31 Anti foam    0.2 Parts                                       
C.     Con. Sulfuric Acid 2.0 Parts                                       
D.     Abson 820 X 16     50.0 Parts                                      
E.     37% Formalin       620.0 Parts                                     
F.     Salicylic Acid     50.0 Parts                                      
G.     Calcium Stearate 60%                                               
                          84.0 Parts                                      
______________________________________                                    
 
    
     The reaction procedure is the same as in Example 1. 
     Ball and Ring Softening Point = 95° C. Yield = 1155 Parts 
     EXAMPLE 4 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     DB-31 Anti foam    0.2 Parts                                       
C.     Con. Sulfuric Acid 2.0 Parts                                       
D.     Abson 820 X 13     50.0 Parts                                      
E.     37% Formalin       620.0 Parts                                     
F.     Salicylic Acid     50.0 Parts                                      
G.     Calcium Stearate 60%                                               
                          84.0 Parts                                      
______________________________________                                    
 
    
     The reaction procedure is the same as in Example 1. 
     Ball and Ring Softening Point = 95° C. Yield = 1150 Parts 
     EXAMPLE 5 COATING METHOD 
     
         ______________________________________                                    
A.     Wedron 70-20 Silica Sand                                           
                          11,350.0 Parts                                  
B.     Resin              340.0 Parts                                     
C.     Hexamethylenetetramine                                             
                          48.0 Parts                                      
D.     Water              180.0 Parts                                     
______________________________________                                    
 
    
     The following procedure was used to coat the resins prepared in the examples set forth in this application. The coating procedures are well known by those skilled in the art. 
     1. Material &#34;A&#34; was heated to 170° C. and placed into a Beardsley-Piper Speed muller (25 pound capacity). The sand was allowed to equilibrate to 155° C. 
     2. With the muller operating the resin was added to the sand. The sand and resin were allowed to mix for 90 seconds. 
     3. At the end of 90 seconds a solution of &#34;C&#34; and &#34;D&#34; was added to the muller. When the coated sand became free flowing in the muller, it was discharged from the muller and allowed to cool to room temperature. The resulting coated sand was free flowing. 
     EXAMPLE 6 PEELBACK TEST 
     Procedure: 
     1. Heat a hot plate to 450° F. Take the temperature of the hot plate with a pyrometer before each test is run. 
     2. Weigh 230 gm. of coated sand into a quart can. 
     3. Pour the sand onto the surface of the hot plate and start a timer. Regulate the invest time so as to produce a test specimen center thickness of 1/4 inch. This is done by starting with an arbitrary invest time (e.g.: 15 seconds), measuring the thickness, then increasing or decreasing the invest time until the proper thickness is obtained. Specimen thickness is determined by averaging three thickness gauge measurements taken near the center of the specimen, after it has been removed from the hot plate and cooled. 
     4. Using the invest time determined in step 3, carry out the peelback test as follows: 
     5. Weigh and test sand as in step 2 and pour it onto the hot plate. Start the electric timer. 6. After the invest time has elapsed (as determined in step 3), invert the hot plate to remove free-flowing sand. 
     7. Immediately after inverting (free-flowing sand dumped), place a pan under hot plate to catch coated sand that peels from plate. 
     8. Return the hot plate to upright position, and take the cured disc from the plate. 
     9. Record the weight of the disc and peel in pan, in grams. 
     10. Calculate the percentage weight peelback. For Example: 
     Core Weight -- 400 
     Peelback Weight -- 100 
     Total Weight -- 500 
     % Weight Peelback -- 20% 
     EXAMPLE 7 
     The resins in Examples 1 through 4 were tested according to the procedures outlined in Examples 5 and 6. 
     
         ______________________________________                                    
Resin     Cold Tensiles (PSI)                                             
                         % Weight Peelback                                
______________________________________                                    
Example 1 538            0                                                
Example 2 512            0                                                
Example 3 519            0                                                
Example 4 490            0                                                
______________________________________                                    
 
    
     The cold tensile test was according to the procedures outlined in Foundry Core Practice by Harry W. Dietert 3rd Edition 1966, page 224. These values are the results of six dogbone specimens. 
     EXAMPLE 8 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     Con. Sulfuric Acid 6.0 Parts                                       
C.     ABSON 820 X 13     10.0 Parts                                      
D.     37% Formalin       649.0 Parts                                     
E.     Calcium Stearate 60%                                               
                          95.0 Parts                                      
F.     Salicylic Acid     50.0 Parts                                      
______________________________________                                    
 
    
     Components &#34;A&#34; through &#34;C&#34; were loaded into a reaction vessel set for reflux. The components were heated to 115 degrees centrigrade and held for 15 minutes, during which time the mixture became homogeneous. The heat was removed and material &#34;D&#34; was added over a 30 to 60-minute period. Enough heat was used to maintain a reflux. After all of component &#34;D&#34; was added, the batch was held at reflux (100° C.) until the free formaldehyde in the refluxate was less than 0.5%. Components &#34;E&#34; and &#34;F&#34; were added and the resulting material was distilled to a grindable resin. 
     Ball and Ring Softening Point = 94° C. Yield = 1180 Parts 
     EXAMPLE 9 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     Con. Sulfuric Acid 6.0 Parts                                       
C.     ABSON 820 X 13     50.0 Parts                                      
D.     37% Formalin       620.0 Parts                                     
E.     Calcium Stearate 60%                                               
                          95.0 Parts                                      
F.     Salicylic Acid     50.0 Parts                                      
______________________________________                                    
 
    
     Procedure the same as Example 8. 
     Ball and Ring Softening Point = 91° C. Yield = 1200 Parts 
     EXAMPLE 10 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     Con. Sulfuric Acid 6.0 Parts                                       
C.     ABSON 820 X 13     100.0 Parts                                     
D.     37% Formalin       620.0 Parts                                     
E.     Calcium Stearate 60%                                               
                          95.0 Parts                                      
F.     Salicylic Acid     50.0 Parts                                      
______________________________________                                    
 
    
     Ball and Ring Softening Point = 93° C. Yield = 1240 Parts 
     EXAMPLE 11 
     The resins in Examples 8 through 10 were tested according to the procedures outlined in Examples 5 through 6. 
     
         ______________________________________                                    
Resin     Cold Tensiles (PSI)                                             
                         % Weight Peelback                                
______________________________________                                    
Example 8 476            0.6                                              
Example 9 485            0.2                                              
Example 10                                                                
          396            0.5                                              
______________________________________                                    
 
    
     EXAMPLE 12 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     Con. Sulfuric Acid 6.0 Parts                                       
C.     ABSON 820 X 13     50.0 Parts                                      
D.     37% Formalin       604.0 Parts                                     
E.     Calcium Stearate 60%                                               
                          95.0 Parts                                      
F.     Salicylic Acid     50.0 Parts                                      
______________________________________                                    
 
    
     Procedure the same as Example 8. 
     Ball and Ring Softening Point = 92° C. Yield = 1155 Parts 
     EXAMPLE 13 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     Con. Sulfuric Acid 6.0 Parts                                       
C.     ABSON 820 X 13     50.0 Parts                                      
D.     37% Formalin       681.0 Parts                                     
E.     Calcium Stearate 60%                                               
                          95.0 Parts                                      
F.     Salicylic Acid     50.0 Parts                                      
______________________________________                                    
 
    
     Procedure the same as in Example 8. 
     Ball and Ring Softening Point = 92° C. Yield = 1225 Parts 
     EXAMPLE 14 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     Con. Sulfuric Acid 6.0 Parts                                       
C.     ABSON 820 X 13     50.0 Parts                                      
D.     37% Formalin       699.0 Parts                                     
E.     Calcium Stearate 60%                                               
                          95.0 Parts                                      
F.     Salicylic Acid     50.0 Parts                                      
______________________________________                                    
 
    
     Procedure the same as in Example 8. 
     Ball and Ring Softening Point = 109° C. Yield = 1240 Parts 
     EXAMPLE 15 
     The resins from Examples 12 through 14 and Example 8 were tested according to the procedures outlined in Examples 5 through 6. 
     
         ______________________________________                                    
      Mole                                                                
      Ratio                                                               
      Formaldehyde/              % Weight                                 
Resin phenol      Cold Tensiles PSI                                       
                                 Peelback                                 
______________________________________                                    
Ex. 12                                                                    
      0.70        473            0.8                                      
Ex. 8 0.75        485            2.3                                      
Ex. 13                                                                    
      0.79        387            0.8                                      
Ex. 14                                                                    
      0.81        Did not coat properly                                   
______________________________________                                    
 
    
     EXAMPLE 16 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     Con. Sulfuric Acid 6.0 Parts                                       
C.     ABSOn 820 X 13     50.0 Parts                                      
D.     37% Formalin       70.0 Parts                                      
E.     37% Formalin       550.0 Parts                                     
F.     Salicylic Acid     50.0 Parts                                      
G.     Calcium Stearate 60%                                               
                          95.0 Parts                                      
______________________________________                                    
 
    
     Materials &#34;A&#34;, &#34;B&#34; and &#34;D&#34; were added to a reaction vessel set for atmospheric reflux. The batch was heated to atmospheric reflux (100° C.) and material &#34;E&#34; was then added dropwise at reflux over a thirty to sixty-minute period. After all of material &#34;E&#34; was added, the batch was held at reflux until the free formaldehyde in the refluxate was less than one half percent. Materials &#34;C&#34;, &#34;F&#34; and &#34;G&#34; were then added to the reaction vessel and the resulting material was distilled to a grindable resin. 
     Ball and Ring Softening Point = 91° C. Yield = 1195 Parts 
     EXAMPLE 17 
     
         ______________________________________                                    
A.     C. P. Phenol       1000.0 Parts                                    
B.     Con. Sulfuric Acid 6.0 Parts                                       
C.     ABSOn 820 X 13     50.0 Parts                                      
D.     37% Formalin       70.0 Parts                                      
E.     37% Formalin       550.0 Parts                                     
F.     Salicylic Acid     50.0 Parts                                      
G.     Calcium Stearate 60%                                               
                          95.0 Parts                                      
______________________________________                                    
 
    
     Materials &#34;A&#34;, &#34;B&#34; and &#34;D&#34; were added to a reaction vessel set for atmospheric reflux. The batch was heated to atmospheric reflux (100° C.) and material &#34;E&#34; was then added dropwise at reflux over a 30 to 60-minute period. After all material &#34;E&#34; was added the batch was held at reflux until the free formaldehyde in the refluxate was less than one half percent. Materials &#34;F&#34; and &#34;G&#34; were added to the reaction vessel and the batch was distilled atmospherically to 130° C. At this time material &#34;C&#34; was added and the resulting material was distilled to a grindable resin. 
     Ball and Ring Softening Point = 91° C. Yield = 1190 Parts 
     EXAMPLE 18 
     
         ______________________________________                                    
A.     C. P. Phenol       1000 Parts                                      
B.     Con. Sulfuric Acid 6 Parts                                         
C.     ABSON 820 X 13     50 Parts                                        
D.     37% Formalin       70 Parts                                        
E.     37% Formalin       550 Parts                                       
F.     Salicylic Acid     50 Parts                                        
G.     Calcium Stearate 60%                                               
                          95 Parts                                        
______________________________________                                    
 
    
     Materials &#34;A&#34;, &#34;B&#34; and &#34;D&#34; were added to a reaction vessel set for atmospheric reflux. The batch was heated to atmospheric reflux (100° C.) and material &#34;E&#34; was added dropwise over a 30 to 60-minute period. After all material &#34;E&#34; was added, the batch was held at reflux until the free formaldehyde in the refluxate was less than one half percent. Materials &#34;F&#34; and &#34;G&#34; were then added and the batch was then distilled to a grindable resin. Material &#34;C&#34; was then added to the molten resin and allowed to mix. 
     Ball and Ring Softening Point = 94° C. Yield = 1160 Parts 
     EXAMPLE 19 
     The resins from Examples 16, 17 and 18 were tested according to the procedure outlined in Examples 5 and 6. 
     
         ______________________________________                                    
Resin     Cold Tensiles (PSI)                                             
                         % Weight Peelback                                
______________________________________                                    
Example 16                                                                
          414            0                                                
Example 17                                                                
          493            7                                                
Example 18                                                                
          457            0                                                
______________________________________                                    
 
    
     As is customary in the art, salicylic acid is used in an amount of 2 to 6%, preferably 4% based on the weight of novolak. The calcium stearate also can be used in the customary amount, e.g., 2 to 6%, preferably 4 to 5%, based on the weight of the novolak.