Patent Publication Number: US-2007102110-A1

Title: Casing formed from thermoplastic resin and method for fabricating the casing

Description:
CROSS-REFERENCE TO RELATED APPLICATION  
      This application claims the priorities of Japanese Patent Application Number 2005-323741, filed on Nov. 8, 2005, Japanese Patent Application Number 2005-376073, filed on Dec. 27, 2005 and Japanese Patent Application Number 2006-138088, filed on May 17, 2006.  
     BACKGROUND OF THE INVENTION  
      1. Field of the Invention  
      The present invention relates to a casing formed from a thermoplastic resin and to a method for fabricating the casing. More particularly, it relates to a casing made of a thermoplastic resin to which a film having a polarizing effect is laminated to thereby provide special decorative effects to the casing that has a three-dimensional structure having an outwardly protruding portion containing a curved surface and to a method for fabricating such a casing.  
      2. Description of the Related Art  
      Traditionally, a casing such as a container for holding an article therein or a case in which an electronic part is housed, or a casing such as a vehicle bumper, motorcycle cowl, helmet, or the like, has been fabricated in three dimensions by assembling plates made of a metal or synthetic resin or like material, or has been molded as a one-piece, three dimensional structure from a single plate. When coloring the exterior surface of the thus fabricated casing for decorative purposes, it has been practiced to paint the surface of the casing or attach a colored sheet to it when the casing is made of metal. In the case of a casing made of a synthetic resin, on the other hand, it has been practiced to color the synthetic resin itself or to attach a colored sheet to it. Further, it is known in the art to provide metallic luster to the casing surface by employing techniques such as plating, metal evaporation, etc.  
      In the resin casing fabricated by the prior art technique, the decorative color applied to the casing surface is fixed and does not change at all or, if it does change, the change is limited. For example, when a transparent colored sheet is attached to the casing surface, the change is such that the color of the colored sheet and the color of the casing itself seen through the transparent sheet are overlaid one on top of the other to present a mixture of the two colors, and not such that the color changes in appearance according to the way it is viewed.  
      As one method of providing special color effects, there has been proposed a method that uses the principle of holography and creates image plane members to be applied to three-dimensional surfaces, thereby achieving a casing on which image shapes, colors, etc. change in various ways depending on the viewing angle. However, creating the images to be reproduced, in particular in white light, in accordance with the principle of holography requires a sophisticated technique and involves an increased cost; therefore, the method that uses the principle of holography is not a suitable method for fabricating inexpensive casings.  
      Apart from the method using the principle of holography described above, a decoration method with simple design that makes color patterns, on a polyhedral body or a curved body change, in various ways depending on the viewing angle has been proposed, for example, in Japanese Unexamined Patent Publication Nos. 2001-341500 and 2002-55621. In this decoration method, the casing having a polyhedral structure or a curved structure is formed from a transparent or translucent material, and the interior or exterior surface of the casing is covered with a plurality of polarizing films or plate pieces. In another proposed decoration method, a decorative thin-film member, for example, a polarizing film, is bonded to one plane surface of an inorganic or resin substrate formed in a flat plate shape, to enhance the richness in decoration and to confer depth and three-dimensional effects to a texture.  
      As described above, in the decoration method proposed in Japanese Unexamined Patent Publication No. 2001-341500, polarizing films or plate pieces are applied to the exterior or interior surface of the casing, and it is a tedious and time-consuming process to decorate the casing. Also, it is not possible to cover the entire exterior or interior surface of the casing. As a result, if the films or pieces are applied to the polygonal or curved faces of the casing, the decorative effect does not extend over the entire surface of the casing, and the effect is limited.  
      On the other hand, in the decoration method proposed in Japanese Unexamined Patent Publication No. 2002-55621, a polarizing film is bonded to a substrate to confer the depth and three-dimensional effects to a texture. According to this decoration method, the decorative qualities can be provided easily and neatly, provided that the substrate is formed in a flat plate shape. However, this is not always the case with casings made of synthetic resin, because resin casings often are constructed in a variety of exterior shapes.  
      With the above method, if the surface has a protruding portion having a curved surface such as described by a three-dimensional curve, it is difficult to bond a single polarizing film evenly and without creasing over the entire surface of the protruding portion in conformity with the curved surface. If the polarizing film is to be bonded only to a flat surface portion of the casing, the polarizing film can be bonded without creasing, but if the flat surface portion has a protruding portion formed thereon, it is difficult to bond the polarizing film evenly and without creasing over the surface of the protruding portion.  
      In view of the above situation, it is an object of the present invention to provide a thermoplastic resin casing on which a protrusion is formed in a variety of ways and the entire surface of the casing is covered with a polarizing film, to provide special decorative effects to the casing, wherein the casing is fabricated either by molding a laminated structure constructed by bonding the polarizing film to a thermoplastic resin plate or by injection-molding a thermoplastic resin onto the polarizing film formed in a prescribed shape.  
     SUMMARY OF THE INVENTIONS  
      To solve the above problem, according to the present invention, there is provided a thermoplastic resin casing having a protrusion of a prescribed shape containing a curved surface, wherein a film having a polarizing effect is attached so as to conform to the prescribed shape of a thermoplastic resin body which forms the protrusion.  
      The film is laminated to the thermoplastic resin body by interposing an adhesive layer therebetween or by interposing an adhesive layer and a binding layer therebetween; alternatively, the film is laminated to the thermoplastic resin body under heat and pressure, or laminated under heat and pressure by interposing an adhesive layer therebetween.  
      At least one surface of the film is embossed, or the thermoplastic resin body and the film laminated together are provided with projections and depressions.  
      The thermoplastic resin body is colored, or the thermoplastic resin body is formed from a transparent plate and an interior surface of the protrusion is decorated partially or entirely in a single color or in a plurality of colors.  
      A surface of the film is decorated with marks.  
      The film is attached to both an exterior side and an interior side of the thermoplastic resin body that forms the protrusion.  
      A colorless or colored and transparent or translucent cover layer is deposited on top of the film attached to the thermoplastic resin body.  
      According to the present invention, there is also provided a method for fabricating a thermoplastic resin casing, wherein a thermoplastic resin plate and a film having a polarizing effect are overlaid one on top of the other and are placed on a mold of a prescribed shape with the film facing the mold, and the thermoplastic resin casing having the prescribed shape and having an outwardly protruding portion is formed by either vacuum forming, by air-pressure forming or by press forming.  
      A laminated plate is fabricated by laminating a film having a polarizing effect on to a thermoplastic resin plate, the laminated plate is placed on a mold with the film facing the mold, and the thermoplastic resin casing is formed by vacuum forming, by air-pressure forming or by press forming.  
      The film is laminated to the thermoplastic resin plate by an adhesive or by interposing an adhesive layer and a binding layer therebetween; alternatively, the film is laminated to the thermoplastic resin plate under heat and pressure, or laminated under heat and pressure by interposing an adhesive therebetween.  
      The laminated structure is formed into the prescribed shape having projections and depressions by using a mold on which projections and depressions are formed.  
      According to the present invention, there is also provided a method, for fabricating a thermoplastic resin casing, wherein a film having a polarizing effect is placed on a mold having a recess of a prescribed shape, and the film is formed into the shape of the recess, wherein, after forming the film, an injection molding die is placed onto the mold with the film interposed therebetween, and the thermoplastic resin casing is formed by injecting a thermoplastic resin into a recess formed by the film.  
      The injection molding die has a protrusion that matches the recess formed by the film, wherein the film is placed on the mold and is formed into the shape of the recess by being pressed into the recess.  
      The film is placed on the mold and is formed into the shape of the recess by evacuating air from the recess, wherein the air is evacuated from the recess through a plurality of evacuation holes formed in the mold, or the air is evacuated from the recess through an edge portion where the film contacts the recess.  
      The mold has a small recessed portion which communicates with the recess through an edge portion where the film contacts the recess, wherein the air is evacuated from the recess through an evacuation hole formed in the small recessed portion.  
      An adhesive layer is formed on a bonding surface of the film, a binding layer is formed on an upper surface of the adhesive layer, the bonding surface of the film is treated by a surface-reforming treatment to facilitate adhesion, and the adhesive layer is formed on the surface treated by the surface-reforming treatment or the adhesive layer is formed by interposing the binding layer on the surface treated by the surface-reforming treatment.  
      According to the present invention, there is also provided a method for fabricating a thermoplastic resin casing, wherein: a first film having a polarizing effect is placed on a first mold having a recess of a prescribed shape, and the first film is formed into the shape of the recess; a second film having a polarizing effect is placed on a second mold having a protrusion of a shape that matches the recess, and the second film is formed into the shape of the protrusion; and the thermoplastic resin casing is formed by injecting a thermoplastic resin between the first film and the second film.  
      The first and second films are formed by applying vacuum or by applying pressure.  
      According to the present invention, there is also provided a method for fabricating a thermoplastic resin casing, wherein: a film having a polarizing effect is placed on a mold having a recess of a prescribed shape, and the film is formed into the shape of the recess; after forming the film, an injection molding die is placed onto the mold with the film interposed therebetween, and a thermoplastic resin plate is formed by injecting a thermoplastic resin into a recess formed by the film; and a colorless or colored and transparent or translucent cover layer is formed on top of the film.  
      In the method for fabricating a thermoplastic resin casing according to the present invention, after said thermoplastic resin casing is formed, unwanted portions are removed by trimming.  
      According to the present invention, there is also provided a method for fabricating a thermoplastic resin casing, wherein a film having a polarizing effect is placed on a mold having a recess of a prescribed shape, an injection molding die is placed onto the mold with the film interposed therebetween, and the thermoplastic resin casing is produced by hot forming together with the film by injecting a thermoplastic resin between the film and the injection molding die.  
      An adhesive layer is formed on a bonding surface of the film, a binding layer is formed on an upper surface of the adhesive layer, the bonding surface of the film is treated for enhanced adhesion, or the adhesive layer is formed on the surface treated for enhanced adhesion; further, the adhesive layer is formed by interposing the binding layer on the surface treated for enhanced adhesion.  
      As described above, according to the present invention, as the resin casing is fabricated by molding a laminated structure constructed by laminating a film having a polarizing effect onto a thermoplastic resin plate or by injection-molding a thermoplastic resin onto the film formed in a prescribed shape or alternatively by hot forming with the polarizing film and the thermoplastic resin simultaneously, the polarizing film can be bonded neatly and without creasing over the entire surface of the casing even when the casing has a protrusion formed in a variety of ways. Accordingly, in addition to the decoration applied to the thermoplastic resin plate itself, the depth and three-dimensional effects can be conferred to a texture over the entire surface of the casing having a three-dimensional structure, and thus special effects, such as smoothly changing iridescent color effects, that cannot be applied to the casing by such techniques as colored resin, painting, plating, evaporation, etc. can be easily provided to the casing.  
      Further, by embossing the film having the polarizing effect, a decorative effect that causes the surface of the casing to glitter like a pearl, by the reflection of ambient light can be easily applied over the entire surface of the casing on which a protrusion is formed in a variety of ways. Furthermore, when projections and depressions are formed on the mold used for molding the laminated structure constructed by laminating the polarizing film to the thermoplastic resin plate, a pattern of projections and depressions can be formed on the casing provided with special decoration.  
      Moreover, as the thermoplastic resin casing of the present invention has a laminated structure constructed by laminating a polarizing film to a thermoplastic resin plate, its special decorative effect is stable and free from discoloration which could occur in the case of decoration applied by such techniques as colored resin, painting, plating, evaporation, etc.  
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
      Other features, objects and advantages of the present invention will become apparent from the following description of preferred embodiments with reference to the drawings in which like reference characters designate like or corresponding parts throughout several views, and in which:  
       FIG. 1  is a cross-section view for explaining a thermoplastic resin casing according to a first embodiment of the present invention in which decoration is applied to a thermoplastic resin;  
       FIG. 2  is a diagram for explaining a configuration example of a polarizing film;  
       FIG. 3  is a diagram for explaining the principle of thin-film interference in a multilayer film;  
       FIG. 4  is a flowchart for explaining a first specific example of a fabrication process for the thermoplastic resin casing of the present invention;  
       FIG. 5  is a diagram for explaining a molding step in the fabrication process of the thermoplastic resin casing according to the first specific example;  
       FIG. 6  is a flowchart for explaining a second specific example of the fabrication process for the thermoplastic resin casing of the present invention;  
       FIGS. 7A and 7B  are cross-sectional views for explaining a first example of ornamentation to be applied to the thermoplastic resin casing of the present invention;  
       FIGS. 8A  to  8 D are process diagrams for explaining a third specific example of the fabrication process for the thermoplastic resin casing of the present invention;  
       FIG. 9  is a diagram for explaining a thermoplastic resin casing according to a second embodiment of the present invention;  
       FIGS. 10A  to  10 C are diagrams for explaining a procedure for mounting a polarizing film on a mold;  
       FIGS. 11A  to  11 D are process diagrams for explaining a fourth specific example of the fabrication process for the thermoplastic resin casing of the present invention;  
       FIGS. 12A  to  12 D are process diagrams for explaining a fifth specific example of the fabrication process for the thermoplastic resin casing of the present invention;  
       FIGS. 13A  to  13 C are diagrams for explaining provisions made to address the distortion occurring in the polarizing film when pressed into the mold;  
       FIG. 14  is a diagram for explaining a thermoplastic resin casing according to a third embodiment of the present invention;  
       FIG. 15  is a diagram for explaining how the polarizing film is pressed into the mold in the fabrication process of the thermoplastic resin casing according to the third embodiment;  
       FIGS. 16A  to  16 D are process diagrams for explaining a sixth specific example of the fabrication process for the thermoplastic resin casing of the present invention;  
       FIG. 17  is a diagram for explaining a thermoplastic resin casing according to a fourth embodiment of the present invention;  
       FIGS. 18A and 18B  are process diagrams for explaining a seventh specific example of the fabrication process for the thermoplastic resin casing of the present invention;  
       FIGS. 19A and 19B  are process diagrams for explaining the remainder of the fabrication process according to the seventh specific example;  
       FIGS. 20A  to  20 C are diagrams for explaining a thermoplastic resin casing according to a fifth embodiment of the present invention;  
       FIG. 21  is a diagram for explaining a fabrication step for the thermoplastic resin casing of the fifth embodiment;  
       FIGS. 22A  to  22 F are diagrams for explaining methods for enhancing the adhesion between the polarizing film and the thermoplastic resin in the thermoplastic resin casing according to the present invention;  
       FIGS. 23A  to  23 C are diagrams for explaining a second example of ornamentation to be applied to the thermoplastic resin casing of the present invention;  
       FIG. 24  is a cross-sectional view for explaining a specific example according to the second example of ornamentation;  
       FIGS. 25A and 25B  are cross-sectional views for explaining other specific examples according to the second example of ornamentation;  
       FIGS. 26A  to  26 D are process diagrams for explaining a modified example of the fourth specific example of the fabrication process for the thermoplastic resin casing shown in  FIGS. 11A  to  11 D;  
       FIGS. 27A and 27B  are diagrams for explaining examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to a personal computer and its related products;  
       FIGS. 28A  to  28 C are diagrams for explaining examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to portable electronic appliances;  
       FIGS. 29A and 29B  are diagrams for explaining examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to household electrical appliances;  
       FIGS. 30A and 30B  are diagrams for explaining examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to furniture or fittings;  
       FIGS. 31A  to  31 C are diagrams for explaining examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to products such as stationery, ornaments, toys, etc.;  
       FIGS. 32A and 32B  are diagrams for explaining examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to vehicle interior and exterior decorative parts;  
       FIGS. 33A and 33B  are cross-sectional views showing a portion of a casing according to the prior art; and  
       FIG. 34  is a cross-sectional view for explaining the shape of the casing according to the prior art. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS  
      Embodiments of a casing formed from a thermoplastic resin according to the present invention will be described below with reference to the drawings. However, before proceeding to the description of the casing according to the present invention, a previously proposed thermoplastic resin casing will be described in order to clarify the features and advantages of the present invention.  
      As shown in the cross-sectional view of  FIG. 33A , in the case of a casing made of a synthetic resin, the resin plate  1  itself which constitutes the casing is colored to provide decoration to the casing. Alternatively, as shown in the cross-sectional view of  FIG. 33B , a colored sheet or a metallic thin film is attached or deposited as a decorative member  2  over the surface of the resin plate  1  that constitutes the casing.  
      According to this decoration method, when the substrate is formed in a flat plate shape, decoration can be provided easily and neatly. However, when the casing B is formed so as to have an outwardly protruding portion, as shown in the cross-sectional view of FIG.  34 , for example, when the entire casing is formed in a dish- or bowl-like shape as shown, a curved surface is formed around the entire circumference of the exterior surface of the casing B.  
      Even when the exterior surface of the casing contains a curved surface, if the curved surface is uniaxial, a polarizing film can be bonded without creasing over the entire exterior surface. However, in the case of the casing B shown in  FIG. 34  in which a curved surface such as described by a three-dimensional curve is formed along the entire circumference of the protruding portion, it is difficult to bond a single polarizing film evenly and without creasing over the entire surface of the protruding portion so as to conform with the curved surface. If the polarizing film is to be bonded only to a flat surface portion of the casing B, the polarizing film can be bonded without creasing, but if the flat surface portion has a protruding portion formed thereon, it is difficult to bond the polarizing film evenly and without creasing over the surface of the protruding portion.  
      In view of the above, in the present invention, a thermoplastic resin casing on which a protrusion is formed in a variety of ways, and the entire surface of which is covered with a polarizing film to provide special decorative effects to the casing, is fabricated either by molding a laminated structure constructed by bonding the polarizing film to a thermoplastic resin plate or by injection-molding a thermoplastic resin onto the polarizing film formed in a prescribed shape.  
      Next, embodiments of the thermoplastic resin casing according to the present invention and its fabrication method will be described with reference to the drawings.  FIG. 1  shows a cross section of a thermoplastic resin casing according to a first embodiment. The shape of the thermoplastic resin casing B 1  shown in  FIG. 1  is similar to that of the casing B shown in  FIG. 34 .  
      The casing according to the first embodiment is not limited to one whose shape is similar to that of the casing B shown in  FIG. 34 , but can be any casing that has a shape having an outwardly protruding portion, such as a container for holding an article therein or a case in which an electronic part is housed; more specifically, if the casing has a box-like three-dimensional shape, has intricate projections and depressions on its external surface, or has a partially protruding portion, the casing can be decorated according to the present embodiment. Furthermore, the present embodiment can be applied even when the casing is a lid member of a container, for example, the upper cover case of a computer mouse. Further, the embodiment can be applied not only to a casing such as a container for holding an article therein or a case in which an electronic part is housed, but also to a casing such as a vehicle bumper, motorcycle cowl, helmet, or the like.  
      While the casing B of  FIG. 34  is formed by simply molding a resin material, in the thermoplastic resin casing B 1  of  FIG. 1 a  film  2  having a polarizing effect is attached so as to cover the exterior surface of the resin plate  1 , without creasing, over the entire structure of the casing. By attaching the film  2  over the entire surface of the resin plate  1 , special decorative effects can be provided to the casing in addition to the decoration applied to the resin substrate  1  itself, the special decorative effects including, for example, an iridescent lustrous color effect that makes the luster of the casing smoothly change like iridescent colors according to the direction from which it is viewed.  
      The film having a polarizing effect (hereinafter called the polarizing film) used for the thermoplastic resin casing of the present invention will be described with reference to  FIGS. 2 and 3 .  FIG. 2  is a schematic cross-sectional view showing how the polarizing film is formed. In  FIG. 2 , the polarizing film  2  is typically formed from thin films F 1  to F 3 . The films F 1  to F 3  are each formed, for example, from a polyester film biaxially oriented as shown by arrows in  FIG. 2 . The refractive index of each film changes according to the degree of the biaxial orientation. The degree of the biaxial orientation differs between the respective films F 1  to F 3 , and these films are laminated together to form the polarizing film.  
      The laminated structure is not limited to the lamination of three films, but more than three films may be laminated. In the example shown here, biaxially oriented polyester films are used as the films to be laminated, but the polarizing film may be formed by combining films of dissimilar materials, such as polyester film and nylon film, because the polarizing film can be formed by combining films of different refractive indices.  
      Generally, a multilayer thin film formed by stacking thin films of different refractive indices is known to exhibit, depending on how they are stacked, a multilayer thin-film interference phenomenon of an ideal type in which light in the visible wavelength range is nearly perfectly reflected, providing a metallic luster, or a multilayer thin-film interference phenomenon of non-ideal type in which the wavelength range of reflected light is limited and the reflectance drops, producing colors corresponding to the wavelengths of the reflected light. In the polarizing film used for the thermoplastic casing of the present invention, the refractive index and thickness of each constituent film are adjusted so as to produce various decorative effects by utilizing the thin-film interference phenomena.  
      By referring to  FIG. 3 , a description will be given of how decorative effects are produced by the polarizing film formed as described above. Of the films F 1  to F 3  forming the polarizing film  2 , the outermost film F 1  is shown in  FIG. 3  as a representative example. When a visible light ray L 1  is incident on the surface of the film F 1 , part of the visible light ray L 1  is reflected as a light ray L 11  and the remaining part is refracted as a light ray L 12  into the film F 1 . The refracted light ray L 12  is reflected at the bottom of the film F 1  and reaches the surface of the film F 1  in the same plane as the point of incidence of the light ray L 11 , where the light ray L 12  is refracted and exits the film F 1 . Of course, depending on the film thickness, the light is not perfectly reflected at the bottom of the film, but part of the light ray L 12  enters the film F 2 ; therefore, actually the light ray L 12  as the reflected light is part of the refracted light ray L 12 .  
      On the other hand, a visible light ray L 2  is incident on the point at which the light ray L 12  exits; like the visible light ray L 1 , the visible light ray L 2  incident on the surface of the film F 1  is partly reflected as a light ray L 21  and partly refracted as a light ray L 22  into the film F 1 . Here, at the point of incidence of the visible light ray L 2 , a thin-film interference phenomenon occurs with the reflected light ray L 21  interfering with the exiting light ray L 12 . This results in the generation of a light ray at a wavelength different from the wavelengths of the visible light rays L 1  and L 2 . When a plurality of thin films are stacked, at the point of incidence of visible light the reflected light ray at the point of incidence interferes with a plurality of exiting light rays.  
      In this way, by utilizing the thin-film interference phenomena of the polarizing film formed from a lamination of thin films, different colors can be produced without using colorants or a metallic luster can be achieved without using a metal film. On the other hand, when white light, not visible light, is incident on the polarizing film, the white light is decomposed due to the prism effect of the film into light rays of rainbow like colors ranging from long to short wavelengths, and the light rays thus decomposed interfere with each other at the points of incidence of the white light, resulting in the production of iridescent decorative effects.  
      Next, referring to FIGS.  4  to  6 , methods for fabricating the thermoplastic resin casing to which the above-described polarizing film is attached will be described by taking as an example the shape of the casing of the first embodiment shown in  FIG. 1 . For the material for forming the thermoplastic resin casing of the present invention, use can be made of acrylic resin, ABS, PVC-based resin, polycarbonate, polyethylene terephthalate, polystyrene, polypropylene, polyethylene, ethylene-vinyl acetate copolymer, polystyrol, etc. The polarizing film can be formed, for example, by laminating biaxially oriented polyester films as described above.  
      The fabrication steps of the thermoplastic resin casing according to the first embodiment will be described with reference to the flowchart shown in  FIG. 4 . First, the thermoplastic resin plate  1  and the polarizing film  2  are laminated together to construct a laminated plate (step S 1 ). Here, the thickness of the thermoplastic resin plate  1  should be chosen so as to provide the necessary strength for the casing, and the plate may be supplied, for example, in the form of a sheet. The thermoplastic resin plate  1  and the polarizing film  2  may be bonded together by an adhesive or by thermocompression.  
      Next, the laminated plate is press-cut to a prescribed size (step S 2 ). The thus cut laminated plate is placed on a mold having a recess of a prescribed shape, and is thermoformed on the mold (step S 3 ).  
       FIG. 5  shows how the laminated plate is thermoformed. A cross-sectional view is shown in  FIG. 5 ; as shown, the mold  3  has a recess whose shape matches the outer shape of the casing shown in  FIG. 1 , and over which the laminated plate of the thermoplastic resin plate  1  and the polarizing film  2 , press-cut to the prescribed size, is placed with the polarizing film  2  facing the recess.  
      When thermoforming the casing of the prescribed shape by vacuum forming on the mold  3 , the laminated structure is pressed into the mold  3  by evacuating air through an evaluation hole formed in the bottom of the recess of the mold  3 , though such an evaluation hole is not shown in  FIG. 5 . On the other hand, when thermoforming the casing of the prescribed shape by air-pressure forming on the mold  3 , the laminated structure is pressed into the mold  3  by applying pressurized air from above the laminated structure placed over the recess of the mold  3 . Further, when thermoforming the casing of the prescribed shape by press forming on the mold  3 , the laminated structure is pressed into the mold  3  by pressing thereon a female press mold having a shape that matches the recess of the mold  3 , though such a press mold is not shown in  FIG. 5 .  
      Next, the laminated plate thermoformed in step S 3  is removed from the mold  3 , and unwanted portions of the laminated plate are cut off to complete the fabrication of the thermoplastic resin casing having the shape shown in  FIG. 1  (step S 4 ). According to the casing fabrication method described above, as the entire surface of the thermoplastic resin plate  1  of the shape having an outwardly protruding portion can be uniformly covered with the polarizing film  2  without causing creases in the polarizing film, a decorative effect that shows iridescent lustrous colors when viewed from any angle can be provided over the entire surface of the casing.  
      In the fabrication method for the thermoplastic resin case of the first embodiment described above, the laminated plate has been press-cut to the prescribed size before the thermoforming step but, rather than press-cutting the laminated plate before thermoforming, the laminated plate may be supplied in the form of a continuous sheet in the thermoforming step, and only the portion corresponding to the casing may be punched out after the thermoforming.  
      Further, in the fabrication method described above, the thermoplastic resin plate  1  and the polarizing film  2  have been bonded together to construct the laminated plate in a step preparatory to the thermoforming step but, instead, the thermoplastic resin plate  1  and the polarizing film  2  may be laminated together during the thermoforming. The fabrication of the thermoplastic resin casing according to this method is shown as a second specific example in the flowchart of  FIG. 6 . In this method also, the thermoplastic resin casing of the shape shown in  FIG. 1  is fabricated using the mold  3  shown in  FIG. 5 .  
      First, the thermoplastic resin plate  1  with the polarizing film  2  overlaid thereon is press-cut to a prescribed size (step S 11 ). The thermoplastic resin plate  1  and the polarizing film  2 , press-cut to the prescribed size, are placed on the mold  3  with the polarizing film  2  facing down. At this time, the thermoplastic resin plate  1  and the polarizing film  2  are not yet bonded together, but are just overlaid, one on top of the other.  
      Next, as in the case of the press forming earlier described, a female press mold having a shape that matches the recess of the mold  3  is pressed onto the mold  3  shown in  FIG. 5 , thereby thermoforming the thermoplastic resin plate  1  and the polarizing film  2  into the prescribed shape while, at the same time, bonding them together under pressure (step S 12 ). The thermoplastic resin casing is thus thermoformed to conform with the shape of the recess of the mold  3 ; then, the thus formed structure is removed from the mold  3 , and unwanted portions of the thermoplastic resin plate  1  and the polarizing film  2  are cut off to complete the fabrication of the thermoplastic resin casing having the shape shown in  FIG. 1 .  
      In the above casing fabrication method also, the entire surface of the thermoplastic resin plate  1  having an outwardly protruding portion can be uniformly covered with the polarizing film  2  without causing creases in the polarizing film, and a decorative effect that shows iridescent lustrous colors when viewed from any angle can be provided over the entire surface of the casing. Here, rather than just bonding the thermoplastic resin plate  1  and the polarizing film  2  under pressure in step  12 , the two members may be bonded together during the thermoforming by interposing an adhesive between them.  
      If the thermoplastic resin plate  1  used for the thermoplastic resin casing described above is colored in a desired color, the iridescent lustrous color effect can be provided over the entire surface of the casing by attaching the polarizing film  2 ; however, if it is desired to enhance the iridescent lustrous color effect, the resin plate should be black. When the resin plate is other than black, the iridescent lustrous color effect is rendered on the base color, producing a variety of decorative effects. On the other hand, when the thermoplastic resin plate  1  is formed from a colorless, transparent material, if the interior surface of the casing is colored by painting or like means, depth can be added to the decoration while also achieving decorative effects due to the iridescent lustrous colors. In this case, the interior surface of the casing may be painted partially or entirely in a single color or in a plurality of colors; for example, a pattern may be drawn on it, or logos using symbols or characters or the like may be included.  
      On the other hand, if the surface of the polarizing film  2  to be laminated to the thermoplastic resin plate  1  is embossed, a decorative effect that causes the surface of the casing to glitter like a pearl can be achieved.  FIG. 7A  shows an example in which, to provide the pearl-like decorative effect, microscopic projections and depressions are formed by embossing on the surface of the polarizing film  2  that faces the resin plate, while  FIG. 7B  shows an example in which microscopic projections and depressions are formed by embossing on the surface of the polarizing film  2  opposite from the surface facing the resin plate, i.e., on the exterior surface of the casing.  
      In this way, when numerous projections and depressions are formed by embossing on either one surface of the polarizing film  2 , ambient light is reflected in various ways, causing the surface to glitter. Accordingly, when such microscopic projections and depressions are formed, the entire surface is caused to glitter like a pearl, and when the thermoplastic resin plate is white, the decorative effect that causes the color to change from pearly pink to pearly blue can be enhanced.  
      The mold  3  used in the fabrication process of the thermoplastic resin casing described above has been shown as just having a recess formed in a prescribed shape as shown in  FIG. 5 , but if fine projections and depressions are formed on the surface of the recess of the mold  3 , a press molding having a surface roughened according to the projections and depressions can be obtained by thermoforming. That is, a pattern conforming to the projections and depressions can be formed on the laminated plate consisting of the thermoplastic resin plate  1  and the polarizing film  1 . In this case, decorative effects due to iridescent lustrous colors can be provided to the pattern of projections and depressions on the surface of the casing.  
      In the thermoplastic casing so far described, the polarizing film has been attached to the upper surface of the thermoplastic resin plate to form the surface of the casing, but when the thermoplastic resin plate is formed from a transparent material, decorative effects due to the iridescent lustrous colors can likewise be achieved even if the polarizing film is attached to the underside of the thermoplastic resin plate, i.e., the interior surface of the casing. In that case, when thermoforming, the laminated plate consisting of the thermoplastic resin plate  1  and the polarizing film  2  is placed on the mold  3  shown in  FIG. 5  by turning the laminated plate upside down from that shown, i.e., with the polarizing film  2  facing up.  
      Further, rather than fabricating the thermoplastic resin casing by laminating the polarizing film to the thermoplastic resin plate, the thermoplastic resin casing may be fabricated by first forming the polarizing film into a prescribed shape using a mold shaped to be able to form an outwardly protruding portion, and then forming the thermoplastic resin plate by injection molding a thermoplastic resin along the interior surface of the film formed in the prescribed size.  
      The fabrication process of the thermoplastic resin casing according to the above method is shown as a third specific example in  FIGS. 8A  to  8 D.  FIGS. 8A  to  8 D show cross-sectional views of the respective fabrication steps which are performed in the order shown. In the third specific example also, the thermoplastic resin casing is fabricated using the mold  3  shown in  FIG. 5 .  
      First, in  FIG. 8A , the polarizing film  2  is placed on the mold  3  having the recess M formed in the prescribed shape. The polarizing film  2  here may be one that has been press-cut to prescribed size or may be in the form of a continuous sheet. Next, by evacuating air from the recess M of the mold  3  through an evacuation hole not shown, the polarizing film  2  is drawn into the recess by vacuum, thus thermoforming the polarizing film  2  into the prescribed shape as shown in  FIG. 8B .  
      After forming the polarizing film  2  into the prescribed shape, an injection molding die  4  having a shape that matches the shape of the recess M of the mold  3  is placed onto the mold  3 , as shown in  FIG. 8C , by interposing therebetween the polarizing film  2  formed in the prescribed shape. Then, the thermoplastic resin is injected through an injection hole  5  formed in the injection molding die  4 .  
      After the injected thermoplastic resin is formed into the prescribed shape in the recess of the mold  3 , the injection molding die  4  is withdrawn; thus, the thermoplastic resin plate is formed into the prescribed shape conforming to the interior surface of the polarizing film  2  retained in the prescribed shape, as shown in  FIG. 8D . Then, the polarizing film  2  is trimmed at positions indicated by arrows shown in  FIG. 8D , to complete the fabrication of the thermoplastic resin casing having the shape shown in  FIG. 1 .  
      Here, the injection molding die  4  may be equipped with a cutting facility such as a cutting blade so that the trimming can be done in the step shown in  FIG. 8C . In the fabrication method of the thermoplastic resin casing shown in  FIGS. 8A  to  8 D, an embossing finish may be applied to the polarizing film, in which case a special decorative effect can be provided to the casing as earlier described.  
      Further, if projections and depressions are formed only on the mold  3  or on both the mold  3  and the injection molding die  4 , a pattern of projections and depressions can be formed on the thermoplastic resin casing and, also, the thermoplastic resin can have any desired color. In the case of a colorless, transparent thermoplastic resin, decoration can be provided by painting the interior surface of the casing partially or entirely in a single color or in a plurality of colors after the injection molding.  
      The thermoplastic resin casing has been described for the case where a single polarizing film is attached to the exterior surface of the resin plate, without creasing, over the entire surface of the casing; in the fabrication process according to the first or second specific example, in order that the polarizing film  2  is attached over the entire surface of the casing formed from the resin plate  1 , first a laminated plate is constructed by laminating the polarizing film to the resin plate, and then the laminated plate is formed into the prescribed shape of the mold, thereby producing the thermoplastic resin casing of the prescribed shape.  
      On the other hand, in the fabrication method hereinafter described for the fabrication of the thermoplastic resin casing of the prescribed shape, rather than using a laminated plate constructed by laminating the polarizing film to the resin plate, the polarizing film is first formed into the prescribed shape, and then the thermoplastic resin is injection-molded, thereby making the polarizing film adhere to the thermoplastic resin and thus fabricating the thermoplastic resin casing the entire surface of which is covered with the polarizing film.  
      The above fabrication method, in which the polarizing film and the resin plate are bonded together in the molding step can be used to produce casings having the same shape as that of the casing of the first embodiment; besides, by changing the shape of the recess formed in the mold, thermoplastic resin casings of various shapes can be produced. Here, a description will be given by taking as an example the fabrication of a thermoplastic resin casing B 2  that has a shape according to a second embodiment shown in  FIG. 9 .  
      While thermoplastic resin casings of various shapes can be produced by changing the shape of the recess of the mold, it will be noted that, depending on the shape of the recess, the pressing force may not act evenly over the entire polarizing film when forming the polarizing film into shape. The polarizing film is constructed by laminating films differing in tensile force, and the uneven pressing force causes the tensile force to change locally. This change in tensile force causes the refractive index of the film to change, and the color of the portion of the polarizing film where the refractive index has changed appears different from other portions.  
      If this change in tensile force is actively exploited, the color of the polarizing film can be selectively changed, and a decorative effect of high quality can be achieved. For example, when the polarizing film is pressed so as to bend with a small radius as in the second embodiment shown in  FIG. 9 , the tensile force of the polarizing film changes locally, causing the refractive index and hence the color in that portion to change. Therefore, if projections and depressions are suitably formed on the recessed surface of the mold so that this changing color principle can be actively exploited, a decorative effect that changes from portion to portion can be achieved, which serves to enhance the decoration.  
      Next, the fabrication method of the thermoplastic resin casing B 2  according to the second embodiment of  FIG. 9  will be described for the case where the polarizing film is formed by being pressed into the recess M formed in the mold in accordance with the shape of the second embodiment. In this example, the earlier described polarizing film  2  is prepared as shown in  FIG. 10A . The polarizing film  2  may be prepared in the form press-cut to prescribed size or in the form of a continuous sheet.  
      As shown in  FIG. 10B , the polarizing film  2  is placed on the mold  31  provided with the recess M having the shape of the second embodiment. Here, the mold  31  is preheated to a suitable temperature so that the polarizing film  2  can be easily pressed into the mold  31 . Next, as shown in  FIG. 10C , a pressing force is applied to the polarizing film  2 , for example, by blowing air under pressure, thereby pressing the polarizing film  2  onto the interior surface of the recess M of the mold  31  and forming it into shape.  
      In the polarizing film formation shown in  FIGS. 10A  to  10 C, the mold  31  has been heated to a suitable temperature in the step of  FIG. 10B ; here, if the polarizing film  2  is also heated to a suitable temperature in the step of  FIG. 10A , the polarizing film can be easily deformed and can thus be easily pressed into the mold. In this case, as the polarizing film is made easily deformable, if the mold  31  is not preheated the polarizing film can be easily pressed into the mold. Further, instead of forming the polarizing film into shape by blowing air or the like under pressure, if the mold  31  is provided with one or more evacuation holes the polarizing film can be formed into shape by evacuating air from the recess M through the evaluation holes.  
      Next, a description will be given of a fourth specific example of the fabrication process of the thermoplastic resin casing B 2  in which the press forming method is employed for forming the polarizing film  2 . The fabrication process according to the fourth specific example is shown in  FIGS. 11A  to  11 D which show the respective steps in cross-sectional views. As in the third specific example, the fabrication steps from  FIGS. 11A  to  11 D are shown in the order of fabrication; in the fourth specific example, the thermoplastic resin casing B 2  is fabricated using the mold  31  shown in  FIG. 10B .  
      First, in  FIG. 11A , the polarizing film  2  is placed on the mold  31  having the recess M formed in the prescribed shape. Next, as shown in  FIG. 11B , the polarizing film  2  is thermoformed into the prescribed shape by blowing air, or the like, under pressure.  
      After forming the polarizing film  2  into the prescribed shape, an injection molding die  41  having a shape that matches the shape of the recess M of the mold  31  is placed onto the mold  31 , as shown in  FIG. 1C , by interposing therebetween the polarizing film  2  formed in the prescribed shape. Then, the thermoplastic resin is injected through an injection hole  51  formed in the injection molding die  41 .  
      After the injected thermoplastic resin is formed into the prescribed shape in the recess M of the mold  31 , the injection molding die  41  is withdrawn and the molding is removed from the mold  31 ; thus, the thermoplastic resin is formed into the prescribed shape conforming to the interior surface of the polarizing film  2  retained in the prescribed shape, as shown in  FIG. 11D . Then, the polarizing film  2  is trimmed at positions indicated by arrows shown in  FIG. 11D , to complete the fabrication of the thermoplastic resin casing B 2  having the shape shown in  FIG. 9 .  
       FIGS. 12A  to  12 D show a fifth specific example of the fabrication process of the thermoplastic resin casing in which one or more evacuation holes communicating with the recess of the mold are provided. In  FIG. 12A  to  12 D, one evacuation hole  6  formed in the mold  32  is shown as a representative example. First, in  FIG. 12A , the polarizing film  2  is placed on the mold  32  having the recess M formed in the prescribed shape. Next, as shown in  FIG. 12B , the polarizing film  2  is thermoformed into the prescribed shape by evacuating air from the recess M through the evacuation hole  6 .  
      After forming the polarizing film  2  into the prescribed shape, the injection molding die  41  having a shape that matches the shape of the recess M of the mold  32  is placed onto the mold  32 , as shown in  FIG. 12C , by interposing therebetween the polarizing film  2  formed in the prescribed shape. Then, the thermoplastic resin is injected through the injection hole  51  formed in the injection molding die  41 .  
      After the injected thermoplastic resin is formed into the prescribed shape in the recess M of the mold  32 , the injection molding die  41  is withdrawn and the molding is removed from the mold  32 ; thus, the thermoplastic resin is formed into the prescribed shape conforming to the interior surface of the polarizing film  2  retained in the prescribed shape, as shown in  FIG. 12D . Then, the polarizing film  2  is trimmed at positions indicated by arrows shown in  FIG. 12D , to complete the fabrication of the thermoplastic resin casing B 2  having the shape shown in  FIG. 9 .  
      Here, when the mold used in the fabrication process according to the fifth specific example is provided with an evacuation hole communicating with the recess, an irregularly shaped portion such as shown in  FIG. 13B  may be formed in the polarizing film  2  in the portion indicated by a circuit in  FIG. 13A . That is, since the polarizing film  2  is heated so that it can be easily formed, if the size of the evacuation hole is made large a portion of the polarizing film  2  which should be formed in a flat shape may be deformed by a suction force exerted through the evacuation hole  6 .  
      In view of this, the diameter of the evacuation hole  6  formed in the mold  32  is determined according to the suction speed, and a plurality of evacuation holes are provided by suitably spacing them apart to prevent concentration of the suction force at one particular location; with this arrangement, the formation of irregularly shaped portions can be prevented.  
      Next, a description will be given of a thermoplastic resin casing fabrication method that can render clean decorative effects on the main surface of the casing by preventing the formation of irregularly shaped portions on the main surface of the casing when forming the polarizing film by evacuating air from the recess of the mold in accordance with the method of the fifth specific example described above.  
      A third embodiment of the thermoplastic resin casing fabricated by the above fabrication method is shown in  FIG. 14 . The third embodiment differs from the second embodiment shown in  FIG. 9  in that the thermoplastic resin  11  molded into one block forms the main body of the thermoplastic resin casing B 3 , the entire surface of which is covered with the polarizing film  2 . As in the second embodiment, unwanted portions of the polarizing film are trimmed off at the edges of the thermoplastic resin casing B 3  to complete the fabrication of the casing.  
      When fabricating the thermoplastic resin casing B 3  according to the third embodiment, if an irregularly shaped portion such as shown in  FIG. 13B  is formed on the main surface of the casing by a suction force during the formation of the polarization film, this may present a problem from the standpoint of decoration. One approach to avoiding this problem may be to provide a plurality of evacuation holes by suitably spacing them apart as shown in  FIG. 13C . On the other hand, even when an irregularly shaped portion is formed in an edge portion of the casing, if the main surface of the casing is free from such irregularly shaped portions, as in the third embodiment shown in  FIG. 14 , the formation of such an irregularly shaped portion may not affect the decorative effect.  
      To address such a situation, the mold  34  used for forming the polarizing film  2  may be constructed so that the air can be evacuated in a concentrated manner through portions corresponding to the edges of the casing, as shown by arrows in  FIG. 15 . According to this method, if irregularly shaped portions are formed in the polarizing film  2  at positions corresponding to the edges of the casing, as the main surface of the casing is free from such irregularly shaped portions, the problem that affects the decoration of the casing can be avoided. The fabrication process of the casing after the polarizing film  2  is formed on the mold  34  is the same as that of the fifth specific example shown in  FIGS. 12A  to  12 D.  
      The above description has dealt with the case where the mold  34  for forming the polarizing film  2  is provided with evacuation holes at positions corresponding to the edges of the casing; next, referring to  FIGS. 16A  to  16 D, a description will be given of a thermoplastic resin casing fabrication method according to a sixth specific example which employs an ingenious design to provide such an evacuation hole. In this example, a small recessed portion “m” is provided which communicates with the mold recess M for forming the polarization film  2 , and the air is evacuated by way of the small recessed portion “m”; in this case, an irregularly shaped portion is formed in the polarizing film  2  at a position corresponding to an edge of the casing, but a casing whose main surface is free from irregularly shaped portions can be obtained.  
      As shown in  FIG. 16A , the small recessed portion “m” communicating with the recess M is typically formed in the mold  35 . A plurality of such small recessed portions “m” may be provided around the recess M. The small recessed portion “m” is provided with an evacuation hole  64 . First, in  FIG. 16A , the polarizing film  2  is placed on the mold  35  provided with the recess M formed in the prescribed shape and the small recessed portion “m” communicating with it. Next, as shown in  FIG. 16B , the air inside the recess M is evacuated by way of the small recessed portion “m” through the evacuation hole  6 , and the polarizing film  2  is thermoformed to conform with the prescribed shape of the mold M and the shape of the small recessed portion “m”.  
      After forming the polarizing film  2  into the prescribed shape, an injection molding die  42  having a flat mold face is placed onto the mold  32  by interposing therebetween the polarizing film  2  retained in the prescribed shape, as shown in  FIG. 16C . Then, the thermoplastic resin is injected through an injection hole  52  formed in the injection molding die  42 .  
      After the injected thermoplastic resin is formed into the prescribed shape in the recess M and the small recessed portion “m” of the mold  35 , the injection molding die  42  is withdrawn and the molding is removed from the mold  35 ; thus, the thermoplastic resin  11  is formed into the prescribed shape conforming to the interior surface of the polarizing film  2  retained in the prescribed shape, as shown in  FIG. 16D . Then, the polarizing film  2  is trimmed at positions indicated by arrows shown in  FIG. 16D , to complete the fabrication of the thermoplastic resin casing B 3  according to the third embodiment shown in  FIG. 14 .  
      Here, an irregularly shaped portion due to the evacuation hole  64  is formed in the polarizing film  2  at a position indicated by a circle in  FIG. 16D  but, as the film is trimmed at the positions indicated by the arrows, the irregularly shaped portion is separated from the completed thermoplastic resin casing B 3  and is thus isolated from the structure. Further, as the thermoplastic resin  11  is cut off at the position where the recess M meets the small recessed portion “m”, the decorative effect of the polarizing film  2  cannot be obtained at this position, but this does not affect the decorative effect provided to the main surface of the thermoplastic resin casing B 3 .  
      The fabrication method of the thermoplastic resin casing according to the sixth specific example shown in  FIGS. 16A  to  16 D has been described as applied to the fabrication of the casing of the third embodiment shown in  FIG. 14  in which the polarizing film is attached over the surface of the thermoplastic resin molded into one block; here, if the injection molding die  41  used in the fabrication method of the thermoplastic resin casing according to the fifth specific example shown in  FIG. 12C  is used instead of the injection molding die  42  shown in  FIG. 16C , the thermoplastic resin casing B 2  of the second embodiment shown in  FIG. 9  can be produced.  
      The first to third embodiments of the thermoplastic resin casings fabricated in accordance with the above-described fabrication methods have each concerned the case where the thermoplastic resin casing has a shape having an outwardly protruding portion, for example, a dish- or bowl-like shape, and the polarizing film is attached only to the exterior surface of the casing. Next, a method for fabricating a thermoplastic resin casing with the polarizing film attached to both surfaces thereof will be described with reference to FIGS.  17  to  19 B.  
       FIG. 17  shows a cross-sectional view of a thermoplastic resin casing B 4  according to a fourth embodiment in which the polarizing film is attached to both surfaces of the casing. The thermoplastic resin casing B 4  has a substantially cullis-like cross-sectional shape, and the decorative effect of the polarizing film is expected to be provided to both the exterior and interior surfaces of the casing, but the decorative effect need not be provided to its end faces.  
      The fabrication method for the thermoplastic resin casing B 4  according to the fourth embodiment is shown as a seventh specific example in  FIGS. 18A and 18B  and  FIGS. 19A and 19B . Unlike the third to sixth specific examples so far described, the fabrication method according to the seventh specific example shown here requires the provision of two polarizing films and the use of two molds for forming the respective polarizing films.  
      First, in  FIG. 18A , an outside polarizing film  2  and an inside polarizing film  21  are prepared. The mold  32  for forming the polarizing film  2  is provided with a recess M of a prescribed shape, while the mold  43  for forming the polarizing film  21  is provided with a protrusion that matches the shape of the recess M. The polarizing film  2  is placed on the mold  32  and the polarizing film  21  on the mold  43 .  
      Next, as shown in  FIG. 18B , the air inside the recess M is evacuated through an evacuation hole  6 , and the polarizing film  2  is thus thermoformed into the prescribed shape conforming to the recess M. On the other hand, for the inside polarizing film  21 , the air is evacuated through an evacuation hole  65  formed in the mold  43 , and the polarizing film  21  is thus thermoformed to conform to the shape of the mold  43 . In  FIGS. 18A and 18B , one evaluation hole  65  provided in the mold  43  is shown as a representative example but, actually, a plurality of evacuation holes are provided because the mold face of the mold  43  has a protruding shape. Here, to form the polarizing film  21 , the previous mentioned pressing method may be used instead of the vacuum drawing method.  
      After forming the polarizing film  2  into the shape of the recess M and the polarizing film  21  into the shape of the protrusion, the molds  32  and  43  are closed while maintaining the formed shapes of the respective films, as shown in  FIG. 19A . Here, a space having a shape that matches the shape of the casing of the fourth embodiment is formed between the polarizing films  2  and  21 . Then, a thermoplastic resin is injected into the space from an edge of the space, i.e., from the direction perpendicular to the plane of the drawing, as shown by an arrow in  FIG. 19 .  
      After the injected thermoplastic resin is formed into the prescribed shape conforming to the recess M of the mold  32 , the molds  32  and  43  are separated and the molding is removed from the molds; thus, the thermoplastic resin  12  is formed into the prescribed shape between the polarizing films  2  and  21  respectively retained in the prescribed shape, as shown in  FIG. 19B . Then, the polarizing films  2  and  21  are trimmed at positions indicated by arrows in  FIG. 19B , to complete the fabrication of the thermoplastic resin casing B 4  according to the fourth embodiment shown in  FIG. 17 . In this thermoplastic resin casing B 4 , as the decorative effect is expected to be provided to the exterior and interior surfaces of the casing, if irregularly shaped portions are formed in the edge portions of the casing such irregularly shaped portions do not affect the decorative effect; here, the end portions, if unwanted, can be cut off.  
      In the embodiments of the thermoplastic resin casing so far described, the polarizing film has been attached to the surface of the thermoplastic resin. In these embodiments, the polarizing film provides decorative effects, such as iridescent color effects, changing color effects from pearly pink to pearly blue, etc. that cannot be achieved by colored resins, painting, plating, metal evaporation, etc., but there are cases where it is desired to add depth to these decorative effects to enhance the quality. In such cases, a clear coating is applied to the surface of the polarizing film. This coating also serves to enhance the weatherability, for example.  
       FIGS. 20A  to  20 C show a thermoplastic resin casing according to a fifth embodiment in which a clear coating is applied to the surface of the polarizing film.  FIG. 20A  shows the structure of the thermoplastic resin casing to which the clear coating is to be applied. The polarizing film  2  is attached to the exterior surface of the thermoplastic resin  1  formed in the shape of the casing.  
       FIG. 20C  shows one example of the thermoplastic resin casing B 5  according to the fifth embodiment. Here, a clear coat layer  7  is formed over the entire surface of the polarizing film  2  attached to the thermoplastic resin  1 . The clear coat layer  7  need only have a certain degree of transmittance and may be colored.  
       FIG. 20B  shows an alternative example of the thermoplastic resin casing B 5  according to the fifth embodiment. Here, a coat layer  71  of a thermoplastic resin is formed over the entire surface of the polarizing film  2  attached to the thermoplastic resin  1 . Like the coat layer  7 , this coat layer  71  also need only have a certain degree of transmittance and may be colored. The coat layer  71  is formed, for example, by double molding in which a resin molding is formed on top of the molded structure.  
       FIG. 21  shows how the coat layer  71  in the alternative example of the thermoplastic resin casing B 5  according to the fifth embodiment is molded from a resin. The mold  8  has a protrusion that matches the interior shape of the thermoplastic resin casing fabricated by the fabrication method of a selected one of the specific examples described above, and the thermoplastic resin casing is placed on this protrusion. An injection molding die  44  having a recess for forming the coat layer from the resin is placed above the mold  8 . The thermoplastic resin is injected through an injection hole  53  formed in the molding die  44 . After that, the mold  8  and the mold  44  are separated, to complete the fabrication of the thermoplastic resin casing B 5  shown in  FIG. 20C .  
      In  FIG. 21 , as the recess of the mold  44  is shaped to conform with the shape of the thermoplastic resin casing, the coat layer  71  formed from the resin has a uniform thickness; here, if projections and depressions are formed on the surface of the recess, an additional decorative effect can be provided.  
      The above description has been given by focusing on the fabrication method of the thermoplastic resin casing according to each specific example; next, a description will be given of methods for enhancing adhesion between the thermoplastic resin and the polarizing film when bonding them together. Various methods for enhancing the adhesion are illustrated in  FIGS. 22A  to  22 F. In each figure, the laminated structure is shown in cross section.  
      In  FIG. 22A , the thermoplastic resin  1  to be injection-molded and the polarizing film  2  are formed from the same kind of material in order to make the polarizing film  2  firmly adhere to the thermoplastic resin  1 . For example, both are formed from polyester. In this case, the polarizing film and the thermoplastic resin are fused together, by the temperature of the resin itself, the applied pressure, or the temperature and the pressure, during the injection molding, or are firmly bonded together due to a force such as intermolecular attraction between the materials of the same kind.  
      In  FIG. 22B , the polarizing film  2  is coated in advance with an adhesive layer “a” in order to make the polarizing film  2  firmly adhere to the thermoplastic resin  1 . For example, when the molding resin is PMMA, a layer of polyvinyl chloride-acetate copolymer is formed in advance as the adhesive layer “a” on the polarizing film. Due to the temperature of the resin itself, the applied pressure, or the temperature and the pressure during, the injection molding, the adhesive layer “a” exerts an adhesive strength, and the adhesion improves.  
      In  FIG. 22C , a surface reforming treatment “b” for facilitating adhesion, for example, is applied in advance to the contact surface of the polarizing film  2  in order to make the polarizing film  2  firmly adhere to the thermoplastic resin  1 . With this reforming treatment “b”, the adhesion between the thermoplastic resin  1  and the polarizing film  2  improves due to the temperature of the resin itself, the applied pressure, or the temperature and the pressure during the injection molding.  
      In  FIG. 22D , a binding layer “c” is formed in advance over the upper surface of the adhesive layer “a” on the polarizing film  2  in order to enhance the adhesion between the adhesive layer “a” and the thermoplastic resin  1  in the structure of  FIG. 22A . With this arrangement, the adhesion between the thermoplastic resin  1  and the polarizing film  2  improves due to the temperature of the resin itself, the applied pressure, or the temperature and the pressure during the injection molding.  
      In  FIG. 22E , a surface reforming treatment “b” for facilitating adhesion, for example, is applied in advance to the contact surface of the polarizing film  2  in order to enhance the adhesion between the adhesive layer “a” and the polarizing film  2  in the structure of  FIG. 22A . With this reforming treatment “b”, the adhesion between the thermoplastic resin  1  and the polarizing film  2  improves due to the temperature of the resin itself, the applied pressure, or the temperature and the pressure during the injection molding.  
      In  FIG. 22F , a surface reforming treatment “b” for facilitating adhesion, for example, is applied in advance to the contact surface of the polarizing film  2  in order to enhance the adhesion between the adhesive layer “a” and the polarizing film  2  in the structure of  FIG. 22A , and a binding layer “c” for improving the adhesion between the adhesive layer “a” and the polarizing film  2  is formed on the surface treated by the reforming treatment “b”. With this arrangement, the adhesion between the thermoplastic resin  1  and the polarizing film  2  improves due to resin temperature, pressure, or temperature and pressure during the injection molding.  
      Methods for enhancing the adhesion are not limited to the examples shown in  FIGS. 22A  to  22 F. The adhesion between the polarizing film and the thermoplastic resin can also be enhanced by combining the adhesive layer, the binding layer, and the reforming treatment of the polarizing film surface in various ways other than those shown in the above examples.  
      Next, examples of ornamentation to be applied to the thermoplastic resin casing to which the polarizing film is attached will be described below.  FIGS. 23A  to  23 C show a second example of ornamentation to be applied to the thermoplastic resin casing. Usually, resin casings for personal computers, electrical appliances, etc. are required to bear marks such as company names, product names, and logos. A description will be given of how such a seal is applied as ornament to the thermoplastic resin casing of the present invention. Here, before forming the polarizing film  2  shown in  FIG. 23A , a mark-bearing layer containing letters, symbols, or geometrical figures, such as “FFFFFFFFF” representing a company name, product name, logo, or the like, is formed by painting or like means on the back surface of the polarizing film  2  that contacts the molding resin  1 , as shown in  FIG. 23B .  
      Then, as shown in  FIG. 23C , the polarizing film  2  whose back surface is thus printed is formed into the prescribed shape, and the thermoplastic resin  1  is injection-molded to complete the fabrication of the thermoplastic resin casing B 6 .  FIG. 24  is a cross-sectional view showing the structure in which the second example of ornamentation is applied to the thermoplastic resin casing treated with the adhesion enhancing processing shown in  FIG. 22B .  FIG. 24  shows the completed structure of the thermoplastic resin casing B 6 ; as shown, the seal-bearing layer “d” is held fixed between the adhesive layer “a” and the polarizing film  2 .  
      Here, as the seal-bearing layer is formed on the plane surface of the polarizing film as shown in  FIG. 23C , if the thermoplastic resin casing B 6  is formed in a three-dimensional structure the seal-bearing layer may be distorted. In this case, the distorted condition should be precalculated, and correction should be made so that the seal looks natural when the casing is formed. The formation of the seal-bearing layer is not limited to the case of  FIG. 22B , but can be applied to other adhesion enhancing examples.  
       FIGS. 25A and 25B  show other specific examples according to the second example of ornamentation to be applied to the thermoplastic resin casing. In these other specific examples according to the second example of ornamentation, engraving is applied to the polarizing film  2  itself and is intended to provide a decorative effect by the engraving in addition to the decorative effect of the polarizing film  2 . In  FIG. 25A , as one example implementing a third example of ornamentation, after the thermoplastic resin casing is completed, engraving is applied, for example, by a CO 2  laser, to the upper surface of the polarizing film  2  to form a mark-engraved layer “e”. The formation of this mark-engraved layer “e” may be performed before forming the polarizing film  2  into shape.  
       FIG. 25B  shows an example in which the mark-engraved layer “e” is formed on top of the seal-bearing layer “d” of the second example of ornamentation shown in  FIG. 24 . Here, a CO 2  laser is used for engraving; the CO 2  laser is suitable for processing the polarizing film  2  because the polarizing film  2  is formed from a transparent material.  
      The method of decorating the thermoplastic resin casing by applying or bonding the polarizing film has been described with reference to various embodiments. In each specific example of the thermoplastic resin casing according to the second to fourth embodiments described above, decoration has been applied to the thermoplastic resin by first placing the polarizing film on a mold having a recess of a prescribed shape, then forming the polarizing film into the shape of the recess by evacuating air from the recess or blowing pressurized air or the like, and finally injecting the thermoplastic resin into the recess. The thermoplastic resin casing with the polarizing film attached to it can be fabricated in this manner.  
      However, instead of first forming the polarizing film into the shape of the recess and then injecting the thermoplastic resin into the recess thereby making the polarizing film adhere to the thermoplastic resin as in the above embodiments, another method may be employed that can make the polarizing film adhere, without creasing, to the thermoplastic resin when injecting the thermoplastic resin. According to this method of decoration, there is no need to form an evacuation hole in the mold or to provide a special device for blowing air or the like.  
       FIGS. 26A  to  26 D show the process for making the polarizing film adhere to the thermoplastic resin when injecting the thermoplastic resin, the process being a modification of the fabrication process according to the fourth specific example of the thermoplastic resin casing shown in  FIGS. 11A  to  11 D. In common with the case of  FIGS. 11A  to  11 D, this modified example uses a mold  31  having the recess M formed in the prescribed shape and the injection molding die  41  for injecting the thermoplastic resin into the recess. In  FIGS. 26A  to  26 D, the fabrication steps according to the modified example are shown in the form of cross-sectional views of the molds. As in  FIGS. 11A  to  11 ,  FIGS. 26A  to  26 D show the fabrication steps in the order of fabrication.  
      First, in  FIG. 26A , the polarizing film  2  is placed on the mold  31  having the recess M formed in the prescribed shape. Next, as shown in  FIG. 26B , the injection molding die  41  is pressed against the mold  31  by interposing the polarizing film therebetween. At this time, the polarizing film  2  is deformed as it is pressed into the recess M by the injection molding die  41 , as shown in the figure.  
      Thereafter, while maintaining the above condition, the thermoplastic resin is injected through the injection hole  51  formed in the injection molding die  41 , as shown in  FIG. 26C . At this time, the polarizing film  2  is pressed onto the interior surface of the recess M of the mold  31 , while being heated, by the injection pressure of the injected thermoplastic resin. As a result, the polarizing film  2  is formed into the prescribed shape of the recess M, while being made to adhere to the thermoplastic resin. During the forming, the polarizing film  2  is stretched, while being heated, by the injection pressure of the injected thermoplastic resin and adheres to the thermoplastic resin without creasing.  
      After the injected thermoplastic resin is formed into the prescribed shape in the recess M of the mold  31 , the injection molding die  41  is withdrawn and the molding is removed from the mold  31 ; thus, the thermoplastic resin is formed into the prescribed shape conforming to the interior surface of the polarizing film  2  retained in the prescribed shape, as shown in  FIG. 26D . Then, the polarizing film  2  is trimmed at positions indicated by arrows shown in  FIG. 26D , to complete the fabrication of the thermoplastic resin casing B 2  having the shape shown in  FIG. 9 .  
      The thermoplastic resin casing of the present invention has been described for the case where the casing body is formed from a one-piece resin mass having a continuous surface, but the invention is not limited to this particular structure, and it will be appreciated that the fabrication method of the present invention can also be applied to the fabrication of a thermoplastic resin casing having an opening of a prescribed shape, for example, in or near the center of the casing body. In this fabrication method, as the thermoplastic resin is formed after forming the polarizing film into shape, the opening is also covered with the polarizing film. In this case, as the polarizing film is trimmed to remove unwanted portions in the final fabrication step of the thermoplastic resin casing, the portion of the polarizing film covering the opening should also be removed in this step.  
      The thermoplastic resin casing produced by each of the above-described fabrication methods can be used as a container for holding an article therein; if the thermoplastic resin casing is formed from a transparent or translucent material so that natural light such as sunlight and light produced by an organic EL or light-emitting diode or the like can pass through the casing, then the thermoplastic resin casing can also be used as an ornament having a special decorative effect by reflecting ambient light such as natural light iridescently while allowing light from inside the casing to be projected outside.  
      Further, when the thermoplastic resin casing is used as a case or panel for an electrical appliance that is equipped with a lighting device such as an organic EL or light-emitting diode for illuminating the casing, if the thermoplastic resin casing is formed from a translucent material the lighting device mounted inside the casing is not visible from the outside when the lighting device is off, and the iridescent color effect due to the ambient light is produced on the surface of the casing. Conversely, when the lighting device is on, the produced light can be recognized from the outside, and the casing can thus be illuminated while producing an iridescent decorative effect on the surface of the casing.  
       FIGS. 27A  to  32 B show application examples of the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments of the present invention that can create the above-described decorative effects. These application examples will be described below.  
       FIGS. 27A and 27B  show examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to a personal computer and related products. In the example of  FIG. 27A , the decorative effects according to the present invention are applied to the main unit case of the personal computer, the housing case of the display panel, the keys on the keyboard, or the like. In these applications, when forming each case in a one-piece structure, the decorative effects can be applied over the entire surface of the case including not only flat portions but also curved portions.  FIG. 27B  shows an example in which the casing is applied to a peripheral device, for example, a mouse, to be connected to the personal computer. Even in the case of a product such as a mouse whose entire surface is made up of intricate curved faces, the decorative effects can be provided to the entire surface of the mouse by attaching the polarizing film without it creasing.  
       FIGS. 28A  to  28 C show examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to portable electronic appliances. As examples of the portable electronic appliances,  FIG. 28A  shows a portable telephone,  FIG. 28B  shows a portable audio player, and  FIG. 28C  shows a portable game player. In these portable electronic appliances also, resin casings are often used, and each casing is made up of intricate curved and plane faces; accordingly, by applying the thermoplastic resin casing of the present invention, decoration can be applied to the casing of the appliance in a simple and effective manner.  
       FIGS. 29A and 29B  show examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to household electrical appliances. As typical examples of the household electrical appliances,  FIG. 29A  shows a television apparatus, and  FIG. 29B  shows a ceiling-mounted lighting device. For the television apparatus, the thermoplastic resin casing of the present invention can be used to decorate the bezel encasing the liquid crystal display panel or the supporting base of the apparatus.  FIG. 29B  shows the ceiling-mounted lighting device broken into its components parts, i.e., the mounting base, the fluorescent lamp support, and the lighting cover or globe, and the decoration by the polarizing film of the present invention can be applied to any portion of these parts that needs decorating.  
       FIGS. 30A and 30B  show examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to furniture or fittings.  FIG. 30A  shows a dresser as an example of a resin-made interior product, and  FIG. 30B  shows a pinball machine as an example of an amusement-related apparatus. In these applications also, the decoration by the polarizing film of the present invention can be applied to any portion that needs decorating.  
       FIGS. 31A  to  31 C show examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to products such as stationery, ornaments, toys, etc.  FIG. 31A  shows a writing instrument such as a ballpoint pen as an example of resin-made stationery,  FIG. 31B  shows a bracelet or headband as an example of a resin-made accessory to be worn on a body, and  FIG. 31C  shows a plastic model of a robot as an example of a toy. In these applications also, the decoration by the polarizing film of the present invention can be applied to any portion that needs decorating when molding the resin-made product.  
      Further,  FIGS. 32A and 32B  show examples in which the thermoplastic resin casings produced in accordance with the fabrication methods of the first to fifth embodiments are applied to vehicle interior and exterior decorative parts.  FIG. 32A  shows a bumper of a passenger car or the like as an example of a vehicle exterior part, and  FIG. 32B  shows a dashboard panel in front of the driver&#39;s seat in a passenger car or the like as an example of a vehicle interior part. In these applications also, the decoration by the polarizing film of the present invention can be applied, to any portion that needs decorating, when molding the resin-made product.