Patent Publication Number: US-4366695-A

Title: Method and apparatus for heating wire prior to drawing

Description:
BACKGROUND OF THE INVENTION 
     This invention relates to the drawing of refractory metal wire and more particularly to a method of heating the wire during the wire drawing process. 
     Various methods have been employed over the years for heating wire during the wire drawing process. Some of the earliest efforts in heating wire for purposes of drawing the wire were disclosed by Thomas A. Edison in U.S. Pat. Nos. 436,969 and 563,462. In U.S. Pat. No. 436,969 a series of gas fires were directed at a porcelain or nickel tube which constituted a heating chamber for the wire to be drawn. In U.S. Pat. No. 563,462 the wire was heated by direct electrical contact which provided electrical resistance heating of the wire in a non-oxidizing atmosphere. 
     F. F. Fowle in U.S. Pat. No. 1,896,613 discloses the heating of zinc-coated wire in a preheating furnace in which the wire passes through a central chamber of a furnace which is heated by fires. McKeen et al. in U.S. Pat. No. 2,057,582 discloses a wire drawing and annealing process in which an axial burner is employed to heat the wire before it enters an adjacent cooling chamber. U.S. Pat. No. 2,187,785 to M. A. Hoyt discloses the use of an electric furnace to dry the lubricated wire in which the lubricated wire passes through a resistance tube which is electrically resistance heated to perform the heating function prior to drawing. In U.S. Pat. No. 2,325,342 there is disclosed a gas heating chamber which heats the wire after it has been reduced by the drawing die and before the wire enters a cooling chamber. 
     At least some manufacturers in present day refractory wire drawing processes employ a plurality of flames to dry the lubricant on the wire and to preheat the wire before it enters the wire drawing die. This system generally involves a large number of gas fires impinging directly on the wire and creates a high noise level, tremendous heat in the surrounding environment and utilizes an excessive amount of gas involving a substantial energy waste. 
     SUMMARY OF THE INVENTION 
     In accordance with the present invention sixteen drying fires and thirty-two preheat fires have been replaced by three gas-fired burners with the consequential reduction in gas usage from 100 cubic feet per hour to 10 cubic feet per hour by passing the wire through one or more cylindrical, tubular tunnels having heat retaining characteristics and an opening in the side wall thereof. A single burner fire is directed into the opening to impinge on wire passing through the tubular tunnel whereby the wire is heated by direct impingement on the flame, by flame and hot gases redirected longitudinally of the wire by the tubular member and by radiant heat from the tubular member side wall. The cylindrical heat retaining tubular member is preferably a silicon carbide tube. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     Many of the attendant advantages of the present invention will become more readily apparent and better understood as the following detailed description is considered in connection with the accompanying drawing in which: 
     FIG. 1 is a schematic side elevation view of the wire drawing system of this invention; 
     FIG. 2 is a schematic end elevation view of one of the heating stations with the tubular member in section; 
     FIG. 3 is an isometric view of the cylindrical tubular heating element of this invention, and; 
     FIG. 4 is a sectional view taken along the line IV--IV of FIG. 3. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENT 
     Referring now in detail to the drawing wherein like reference characters represent like parts throughout the several views, there is illustrated in FIG. 1 a schematic illustration of a typical wire drawing process modified in accordance with the present invention. Previously, the process for reducing the diameter of molybdenum wire involved the passing of the wire through a station A at which the wire is coated with a lubricant as, for example, Aquadag, a water-graphite emulsion. At station B a plurality of vertically oriented gas burners, for example sixteen, were employed to dry the lubricant by passing the wire through the tips of the vertically oriented flames. Prior to passing the wire through the drawing die at station E the wire must be preheated to a predetermined temperature and in the past this was accomplished by separate sets, sixteen each, vertically oriented gas flames at stations C and D with the wire again passing through the tips of the vertically oriented flames. This operation consumed approximately 100 cubic feet of gas per hour to properly prepare the tungsten wire for diameter reduction through the drawing die at station E. 
     In accordance with the present invention, the tubular silicon carbide elements 10 have been placed at stations B, C and D as illustrated in FIG. 1. These cylindrical tubular silicon carbide elements 10 have an aperture 12 cut in the side wall thereof for receiving a flame from a horizontally directed burner 14 which includes a nozzle 16 and a mixing chamber 18 wherein the air from line 20 and gas from line 22 are mixed to provide the proper heating flame 24 which is projected through the aperture 12 into the interior of the cylindrical tubular silicon carbide body 10. 
     In operation, the wire proceeds from a spool (not shown) through the lubricant applicator at station A where a water-graphite emulsion is coated onto the wire. The wire next proceeds to the lubricant drying station B where a single gas flame 2 directed through the aperture 12 in the cylindrical tubular member 10 dries the lubricant. The wire then proceeds through the preheat stations C and D where similar gas burners 16 project flames through apertures 12 in identical silicon carbide members 10. The preheated wire is then pulled through the diameter reduction die 26 at station E where it is wound onto a pulling capstan (not shown). A plurality of wire guides 28 are provided between the various operating stations to maintain the wire in alignment and prevent the wire from sagging. The three gas burners 16 replace forty-eight vertical gas fires previously employed to dry the lubricant and heat the wire during the wire drawing process. By employing the apertured silicon carbide cylindrical tubular members 10 at each of the stations B, C and D, the gas consumption has been reduced from about 100 cubic feet per hour to about 10 cubic feet per hour with an additional, not insignificant, improvement in work area conditions. By employing the system of this invention the temperature and noise level in the work area has been substantially reduced. 
     The considerable energy savings accomplished by this invention results from the fact that the wire W is heated in three modes by employing the silicon carbide cylindrical tube. First, direct impingement of the flame on the wire, heats the wire in substantially the same manner as the previous fires, however, the hot gases and residual flame flow longitudinally of the wire out of the ends of the tubular cylinder as illustrated in FIG. 4 and continues to heat the wire over a substantial length. Additionally, the silicon carbide tube rapidly acquires a cherry red appearance or incandescence and radiates that heat back into the chamber defined by the tube to provide additional heating to the wire W. 
     The cylinders 10 may be mounted in the wire drawing line in any convenient manner. For example, as best illustrated in FIG. 2, an L-shaped stand 30 can be mounted to the wire drawing table 32 and a V-shaped bracket 34 welded or otherwise secured to the L-shaped stand 30. The cylindrical tubes 10 can be then secured in the V-shaped bracket by means of U bolts 36, hose clamps or any other convenient means. 
     Although silicon carbide tubes have been illustrated and described because of their good heat retention characteristics, it should be understood that the apertured cylindrical tube 10 could be made from steel, cast iron, Inconel or similar materials.