Patent Publication Number: US-4927730-A

Title: Light-sensitive material containing silver halide, reducing agent and polymerizable compound

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to a light-sensitive material comprising a light-sensitive layer containing silver halide, a reducing agent, a polymerizable compound and a color image forming substance provided on a support, and image-forming methods employing the light-sensitive material. 
     2. Description of Prior Arts 
     Light-sensitive materials comprising a light-sensitive layer containing silver halide, a reducing agent and a polymerizable compound provided on a support can be used in an image forming method in which a latent image of silver halide is formed, and then the polymerizable compound is polymerized to form the corresponding image. 
     Examples of said image forming methods are described in Japanese Patent Publication Nos. 45(1970)-11149 (corresponding to U.S. Pat. No. 3,697,275), 47(1972)-20741 (corresponding to U.S. Pat. No. 3,687,667) and 49(1974)-10697, and Japanese Patent Provisional Publication Nos. 57(1982)-138632, 57(1982)-142638, 57(1982)-176033, 57(1982)-211146 (corresponding to U.S. Pat. No. 4,557,997), 58(1983)-107529 (corresponding to U.S. Pat. No. 4,560,637), 58(1983)-121031 (corresponding to U.S. Pat. No. 4,547,450) and 58(1983)-169143. In these image forming methods, when the exposed silver halide is developed using a developing solution, the polymerizable compound is induced to polymerize in the presence of a reducing agent (which is oxidized) to form a polymer image. Thus, these methods need a wet development process employing a developing solution. Therefore the process takes a relatively long time for the operation. 
     An improved image forming method employing a dry process is described in Japanese Patent Provisional Publication Nos. 61(1986)-69062 and 61(1986)-69062 and 61(1986)-73145 (the contents of both publications are described in U.S. Pat. No. 4,629,676 and European Patent Provisional Publication No. 0174634A2). In this image forming method, a recording material (i.e., light-sensitive material) comprising a light-sensitive layer containing a light-sensitive silver salt (i.e., silver halide), a reducing agent, a cross-linkable compound (i.e., polymerizable compound) and a binder provided on a support is imagewise exposed to form a latent image, and then the material is heated to polymerize within the area where the latent image of the silver halide has been formed. The above method employing the dry process and the light-sensitive material employable for such method are also described in Japanese Patent Provisional Publication Nos. 61(1986)-183640, 61(1986)-188535 and 61(1986)-228441. 
     The above-mentioned image forming methods are based on the principle in which the polymerizable compound is polymerized within the area where a latent image of the silver halide has been formed. 
     Japanese Patent Provisional Publication No. 61(1986) -260241 (corresponding to U.S. Pat. Ser. No. 854,640) describes another image forming method in which the polymerizable compound within the area where a latent image of the silver halide has not been formed is polymerized. In this method, when the material is heated, the reducing agent functions as polymerization inhibitor within the area where a latent image of the silver halide has been formed, and the polymerizable compound in the other area is polymerized. 
     Japanese Patent Provisional Publication No. 61(1986)-73145 (corresponding to U.S. Pat. No. 4,629,676 and European Patent Provisional Publication No. 0174634A2) describes an embodiment of the image forming methods in which a light-sensitive material containing a color image forming substance is used for forming a color image. In the Publication, examples of the color image forming substance include dyes, pigments and leuco dyes which can develop a color in contact with an acid color developer. 
     SUMMARY OF THE INVENTION 
     The present inventor has found that a light-sensitive material employing the dye or pigment as a color image forming substance tends to be lowered in the sensitivity, because the light-sensitive layer of the material is colored by the dye or pigment. The present inventor has further found that the developed leuco dye in the image-forming method does not have sufficient light fastness and tends to be discolored in contact with a base. 
     An object of the present invention is to provide a light-sensitive material which is improved in the sensitivity and gives a clear color image. 
     Another object of the invention is to provide a light-sensitive material which gives a color image improved in the durability. 
     There is provided by the present invention a light-sensitive material comprising a light-sensitive layer containing silver halide, a reducing agent, a polymerizable compound and a color image forming substance provided on a support, characterized in that the color image forming substance is a triazene compound having the following formula: ##STR2## in which Ar is an aryl group or a heterocyclic group, each of which may have one or more substituent groups; each of R 1  and R 2  independently is a group selected from the group consisting of hydrogen, an alkyl group, a cycloalkyl group, an aralkyl group, an alkenyl group, an aryl group and a heterocyclic group, each of which may have one or more substituent groups, or R 1  and R 2  form, together with the neighboring nitrogen, a heterocyclic group which may have one or more substituent groups; and n is 1, 2 or 3. 
     The light-sensitive material of the invention can be advantageously used in a process which comprises: 
     imagewise exposing the light-sensitive material to form a latent image of the silver halide; 
     simultaneously or thereafter developing the light-sensitive material to polymerize the polymerizable compound within the area where the latent image of the silver halide has been formed (or the area where the latent image of the silver halide has not been formed), and thereby fixing the triazene compound on the support within the area; and 
     pressing the light-sensitive material on an image-receiving material comprising an image-receiving layer containing an acid color developer and a coupler provided on a support to transfer the unfixed triazene compound to the image-receiving material, and thereby the triazene compound reacting with the acid color developer and the coupler to form a color image on the image-receiving material. 
     The light-sensitive material of the invention is characterized in employing the above mentioned triazene compound as a color image forming substance. 
     Japanese Patent Provisional Publication No. 48(1973)-41815 describes a pressure-sensitive transfer material containing a triazene compound. The present inventor has found that the triazene compound can be more advantageously used in the above mentioned light-sensitive material. The light-sensitive material employing the triazene compound as a color image forming substance is improved in the sensitivity and gives a clear image having a high maximum density and a low minimum density. Further, the color image formed from the triazene compound is sufficiently durable and is scarcely discolored by a light irradiation or a variation of pH condition. Therefore, the light sensitive material of the invention can give a clear color image improved in the durability. 
     DETAILED DESCRIPTION OF THE INVENTION 
     The triazene compound employed in the present invention has the following formula. ##STR3## 
     In the formula, Ar is an aryl group or a heterocyclic group. 
     Examples of the aryl group which can constitute the Ar include phenyl and naphthyl. The heterocyclic group which can be constitute the Ar preferably is aromatic. Examples of the heterocyclic group include 2-pyridyl, 3-pyridyl, 3-thienyl and 2-benzothiazolyl. 
     The Ar may have one or more substituent groups. Examples of the substituent group of the Ar include an alkyl group which preferably contains 1-5 carbon atoms, an alkoxy group which preferably contains 1-5 carbon atoms, an alkoxycarbonyl group preferably contains 2-6 carbon atoms, carbamoyl, sulfamoyl, an alkylsulfonyl group, amino, an alkyl amino group, anilino, an arylazo group and a halogen atom. There is no specific limitation with respect to the position of the substituent group in the Ar. 
     In the formula, each of R 1  and R 2  independently is a group selected from the group consisting of hydrogen, an alkyl group, a cycloalkyl group, an aralkyl group, an alkenyl group, an aryl group and a heterocyclic group, each of which may have one or more substituent groups, or R 1  and R 2  form, together with the neighboring nitrogen, a heterocyclic group which may have one or more substituent groups. 
     At least one of the R 1  and R 2  preferably is a group other than hydrogen. 
     Examples of the alkyl group which can constitute the R 1  and R 2  include ethyl, butyl and octyl. Example of the cycloalkyl group is cyclohexyl. Examples of the aralkyl group include benzyl and 2-phenethyl. Examples of the alkenyl group include allyl and crotyl. Examples of the aryl group include phenyl, p-tolyl and p-chloropheny. Examples of the heterocyclic group include 2-benzothiazoyl, 2-thiazolyl and 2-pyridyl. The R 1  and R 2  preferably contains 4 or more total carbon atoms. 
     Examples of the heterocyclic group which R 1  and R 2  form together with the neighboring nitrogen include pyrrolidine ring, piperidine ring and morpholine ring. 
     In the formula, n is 1, 2 or 3. In a general way, n preferably is 1. 
     Examples of the triazene compound which are preferably used in the invention are described hereinafter. ##STR4## 
     These triazene compounds can be synthesized by the reaction of a diazonium salt with an amine. A Synthesis Example is described hereinafter. 
    
    
     SYNTHESIS EXAMPLE 1 
     Synthesis of triazene compound (19) 
     In a mixture of 6.8 g (0.08 mole) of piperidine and 100 ml of acetonitrile was portionwise added 10.25 g of p-(N-ethyl-N-benzylamino)benzenediazonium chloride while cooling by ice. 
     The reaction mixture was stirred for 30 minutes at room temperature, and the separated crystals were collected on a filter. The crystals were washed with acetonitrile and water, and dried. The crude product was recrystallized from n-hexane to obtain 4.8 g of the triazene compound (19) as light yellow crystals, m.p. 87°-88° C. 
     The other triazene compounds can be also synthesized by the diazotization of the corresponding aniline derivative according to a conventional manner, and the reaction of the separated double salt with an amine in a similar manner as in Synthesis Example 1. 
     The triazene compound can be uses singly or in combination with two or more compounds. Further, where three or more triazene compounds are employed in the light-sensitive material, the relation between the hue of each of the triazene compound and the spectral sensitivity of the silver halide can be adjusted to form a full color image. 
     The triazene compound in the light-sensitive layer of the light-sensitive material is preferably used in an amount of from 0.5 to 50 weight % based on the amount of the polymerizable compound, and more preferably from 2 to 20 weight %. 
     The triazene compound employed in the invention can couple with one of various kinds of couplers in the presence of an acid color developer to form a durable and stable azo dye. The coupling reaction, in which the triazene compound couples with a coupler (e.g., naphthol) in the presence of an acid clay to form a azo dye, is described in Japanese Patent Provisional Publication No. 48(1973)-41815. 
     The scheme of the color image formation employing the light-sensitive material of the invention is described below. ##STR5## 
     As mentioned above, the color formation of the triazene compound employed in the light-sensitive material needs the acid color developer and the coupler. 
     The present inventor has found that the reaction of the color formation can be much accelerated upon heating. Therefore, the triazene compound preferably reacts with the developer and the coupler under a heating condition. 
     Heating temperatures for the reaction usually ranges from 50° C. to 200° C., and preferably from 50° C. to 150° C. The heating time is usually from 1 second to 1 minute, and preferably from 1 second to 10 seconds. 
     In the image formation employing the light-sensitive material of the invention, the color image is preferably formed on an image-receiving material to improve the sensitivity of the light-sensitive material and the sharpness of the obtained image. In this case, the acid color developer or the coupler is previously contained in an image-receiving layer of the image-receiving material. The image-receiving layer preferably contains both of the acid color developer and the coupler. 
     Alternatively, the acid color developer and the coupler can be contained in the light-sensitive material of the invention as one of the optional components of the light-sensitive layer. Where the triazene compound and the polymerizable compound are contained in a microcapsule, and the acid color developer and the coupler are arranged outside of the microcapsule in the light-sensitive layer, a color image can be formed on the light-sensitive layer. In this case, the acid color developer and/or the coupler can be contained in a different micro-capsule from that containing the triazene compound. 
     The acid color developer and the coupler employed in the color formation of the triazene compound are described below. 
     Examples of the acid color developer include acid clay developers (e.g., China clay), phenol/formaldehyde resins (e.g., p-phenylphenol/formaldehyde resin), metal salts of salicylic acid (zinc 3,5-di-α-methylbenzylsalicylate), phenol/salicylic acid/formaldehyde resin (e.g., p-octylphenol/zinc salicylate/formaldehyde resin), zinc rhodanide and zinc xanthate. 
     The present inventor has further found that the color formation of the triazene compound can rapidly and effectively progress in the presence of the color developer containing zinc salicylates. Therefore, a color developer containing zinc salicylates is most preferably used as the acid color developer. The oil-soluble color developers containing zinc salicylates are described in U.S. Pat. Nos. 3,864,146 and 4,046,941, and Japanese Patent Publication No. 52(1977)-1327. 
     The acid color developer is preferably used in an amount of from 50 to 1,000 weight % based on the amount of the triazene compound, and more preferably from 100 to 1,000 weight %. 
     There is no specific limitation with respect to the coupler, except that it has a function of coupling with the triazene compound. Preferred examples of the coupler include an active methylene compound, an active methine compound, phenol and a phenol derivative, naphthol and a naphthol derivative, pyrazole and a pyrazole derivative, and a condensed pyrazole compound. Concrete examples of the coupler are described in the following formulas (I) to (X). ##STR6## in which each of R 3 , R 4 , R 5  and R 6  independently is a monovalent group selected from the group consisting of hydrogen, a halogen atom, an alkyl group, a cycloalkyl group, an aralkyl group, an alkenyl group, an aryl group, an alkoxyl group, an aryloxyl group, an acyl group, an acylamino group, carbamoyl, sulfamoyl, an alkylamino group, an arylamino group, an acyloxyl group, unreid, cyano and a heterocyclic group. These groups except hydrogen, a halogen atom and cyano may have one or more substituent groups. 
     Examples of the substituent groups which may be attached to the each of R 3 , R 4 , R 5  and R 6  include an alkyl group, an alkoxyl group, a halogen atom, hydroxyl, carboxyl, sulfo, cyano, nitro, carbamoyl, a substituted carbamoyl group, sulfamoyl, a substituted sulfamoyl, an acylamino group, an alkylsulfonylamino group, an arylsulfonylamino group, an aryl group, an aryloxyl group, an aralkyl group and a acyl group. 
     Among these couplers, the compound having the formula (I) (i.e., 2-hydroxy-3-naphthoic amide derivative or naphthol AS derivative) is most preferred. This coupler is described in Hiroshi Horiguchi, &#34;Synthetic Dye&#34;, published by Sankyo Shuppan Co., Ltd. (in Japanese, 1968), pp. 258-264. 
     The coupler is preferably used in an amount of from 100 to 1,000 weight % based on the amount of the triazene compound, and more preferably from 150 to 600 weight %. 
     The image-forming method employing the light-sensitive material of the invention is described below. 
     In the use of the light-sensitive material of the invention, a development process is conducted simultaneously with or after an imagewise exposure. 
     Various exposure means can be employed in the imagewise exposure, and in general, the latent image on the silver halide is obtained by imagewise exposure to radiation including visible light. The type of light source and exposure can be selected depending on the light-sensitive wavelengths determined by spectral sensitization or sensitivity of silver halide. Original image can be either monochromatic image or color image. 
     Development of the light-sensitive material can be conducted simultaneously with or after the imagewise exposure. The development can be conducted using a developing solution in the same manner as the image forming method described in Japanese Patent Publication No. 45(1970)-11149. The image forming method described in Japanese Patent Provisional Publication No. 61(1986)-69062 which employs a heat development process has an advantage of simple procedures and short processing time because of the dry process. Thus, the latter method is preferred as the development process of the light-sensitive material. 
     Heating in the heat development process can be conducted in various known manners. The heating layer which is arranged on the light-sensitive material can be used as the heating means in the same manner as the light-sensitive material described in Japanese Patent Provisional Publication No. 61(1986)-294434. Further, the light-sensitive material can be heated while suppressing supply of oxygen into the light-sensitive layer from outside. Heating temperatures for the development process usually ranges from 80° C. to 200° C., and preferably from 100° C. to 160° C. Various heating patterns are applicable. The heating time is usually not shorter than 1 second, preferably from 1 second to 5 minutes, and more preferably from 1 second to 1 minute. 
     During the above development process, a polymerizable compound within the area where a latent image of the silver halide has been formed or within the area where a latent image of the silver halide has not been formed is polymerized. In a general system, the polymerizable compound within the area where the latent image has been formed is polymerized. If a nature or amount of the reducing agent is controlled, the polymerizable compound within the area where the latent image has not been formed can be polymerized. 
     In the above development process, the triazene compound can be fixed on the support by the polymerization. 
     Where the triazene compound and the polymerizable compound are contained in a microcapsule, and the acid color developer and the coupler are arranged outside of the microcapsule in the light-sensitive layer, a color image can be formed on the light-sensitive material of the invention by pressing the material after the development process. 
     The image is preferably formed on the image-receiving material. The image-receiving material is described hereinbelow. The image forming method employing the image-receiving material or the image-receiving layer is described in Japanese Patent Provisional Publication No. 61(1986)-278849. 
     Examples of the material employable as the support of the image-receiving material include baryta paper in addition to various examples which can be employed as the support of the following light-sensitive material. In the case that a porous material, such as paper is employed as the support of the image-receiving material, the porous support preferably has such a surface characteristic that a filtered maximum waviness of not less than 4 μm is observed in not more than 20 positions among 100 positions which are determined at random on a filtered waviness curve obtained according to JIS-B-No. 0610. Further, a transparent material can be employed as the support of the image-receiving material to obtain a transparent or a projected image. 
     The image-receiving material is usually prepared by providing the image-receiving layer on the support. In the case that the light-sensitive layer contains the acid color developer and the coupler to develop the triazene compound previous to or simultaneously with the transference of the triazene compound to the image-receiving material, the image-receiving material be composed of a simple support. 
     The image-receiving layer can contain the acid color developer and the coupler according to the color formation system of the above mentioned triazene compound. As mentioned above, the acid color developer and the coupler are preferably contained in the image-receiving layer. 
     The image-receiving layer preferably contains a polymer as binder. The binder which may be employed in the above-mentioned light-receiving layer is also employable in the image-receiving layer. Further, a polymer having a transmission coefficient of oxygen of not more than 1.0×10 -11  cm 3  ·cm/cm 2  ·sec·cmHg can be used as the binder to protect the color of the image formed on the image-receiving material. 
     The image-receiving layer can contain a granulated thermoplastic compound to obtain a glossy image. Further, the image-receiving layer can contain a white pigment (e.g., titanium dioxide) to function as a white reflection layer. Furthermore, a photo polymerization initiator or a thermalpolymerization initiator can be contained in the image-receiving layer to polymerize the unpolymerized polymerizable compound. 
     The image-receiving layer can be composed of two or more layers according to the above-mentioned functions. The thickness of the image-receiving layer preferably ranges from 1 to 100 μm, more preferably from 1 to 20 μm. 
     A protective layer can be provided on the surface of the image-receiving layer. 
     After the development process, pressing the light-sensitive material of the invention on the image-receiving material to transfer the unfixed triazene compound to the image-receiving material, a color image can be obtained in the image-receiving material. The process for pressing can be carried out in various known manners. 
     As mentioned above, the reaction of the triazene compound with the acid color developer and the coupler can be accelerated upon heating. Therefore, the image-receiving material is preferably heated after the transference of the triazene compound to the image-receiving material. 
     This process for heating the image-receiving material after the transference has another advantage of polymerizing the unpolymerized polymerizable compound which has been transferred with the triazene compound to improve the preservability of the obtained image. 
     The light-sensitive material can be used for monochromatic or color photography, printing, radiography, diagnosis (e.g., CRT photography of diagnostic device using supersonic wave), copy (e.g., computer-graphic hard copy), etc. 
     The silver halide, the reducing agent, the polymerizable compound and the support which constitute the light-sensitive material of the invention are described below. Thus composed material is referred hereinafter to as &#34;light-sensitive material&#34;. 
     There is no specific limitation with respect to silver halide contained in the light-sensitive layer of the light-sensitive material. Examples of the silver halides include as silver chloride, silver bromide, silver iodide, silver chlorobromide, silver chloroiodide, silver iodobromide, and silver chloroiodobromide in the form of grains. 
     The halogen composition of individual grains may be homogeneous or heterogeneous. The heterogeneous grains having a multilayered structure in which the halogen composition varies from the core to the outer shell (see Japanese Patent Provisional Publication Nos. 57(1982)-154232, 58(1983)-108533, 59(1984)-48755 and 59(1984)-52237, U.S. Pat. No. 4,433,048, and European Patent No. 100,984) can be employed. A silver halide grain having a core/shell structure in which the silver iodide content in the shell is higher than that in the core can be also employed. 
     There is no specific limitation on the crystal habit of silver halide grains. For example, a tubular grain having an aspect ratio of not less than 3 can be employed. 
     Two or more kinds of silver halide grains which differ in halogen composition, crystal habit, grain size, and/or other features from each other can be used in combination. 
     There is no specific limitation on grain size distribution of silver halide grains. For example, the silver halide grains having such a grain size distribution that the coefficient of the variation is not more than 20% can be employed. 
     The silver halide grains ordinarily have a mean size of 0.001 to 5 μm, more preferably 0.001 to 2 μm. 
     The total silver content (including silver halide and an organic silver salt which is one of optional components) in the light-sensitive layer preferably is in the range of from 0.1 mg/m 2  to 10 g/m 2 . The silver content of the silver halide in the light-sensitive layer preferably is not more than 0.1 g/m 2 , more preferably in the range of from 1 mg to 90 mg/m 2 . 
     The reducing agent employed in the light-sensitive material has a function of reducing the silver halide and/or a function of accelerating or restraining a polymerization of the polymerizable compound. Examples of the reducing agents having these functions include various compounds, such as hydroquinones, catechols, p-aminophenols, p-phenylenediamines, 3-pyrazolidones, 3-aminopyrazoles, 4-amino-5-pyrazolones, 5-aminouracils, 4,5-dihydroxy-6-aminopyrimidines, reductones, aminoreductones, o- or p-sulfonamidophenols, o- or p-sulfonamidonaphthols, 2-sulfonamidoindanones, 4-sulfonamido-5-pyrazolones, 3-sulfonamidoindoles, sulfonamidopyrazolobenzimidazoles, sulfonamidopyrazolotriazoles, α-sulfonamidoketones, hydrazines, etc. Depending on the nature or amount of the reducing agent, the polymerizable compound within either the area where a latent image of the silver halide has been formed or the area where a latent image of the silver halide has not been formed can be polymerized. In the developing system in which the polymerizable compound within the area where the latent image has not been formed is polymerized, 1-phenyl-3-pyrazolidone is preferably employed as the reducing agent. 
     The light-sensitive materials employing the reducing agent having these functions (including compounds referred to as developing agent, hydrazine derivative or precursor of reducing agent) are described in Japanese Patent Provisional Publication Nos. 61(1986)-183640, 61(1986)-188535 and 61(1986)-228441. These reducing agents are also described in T. James, &#34;The Theory of the Photographic Process&#34;, 4th edition, 291-334 (1977), Research Disclosure No. 17029, 9-15 (Jun. 1978), and Research Disclosure No. 17643, 22-31 (Dec. 1978). The reducing agents described in the these publications can be employed in the light-sensitive material of the present invention. Thus, &#34;the reducing agent(s)&#34; in the present specification means to include all of the reducing agents described in the above mentioned publications and applications. 
     These reducing agents can be used singly or in combination. In the case that two or more reducing agents are used in combination, certain interactions between these reducing agents may be expected. One of the interactions is for acceleration of reduction of silver halide (and/or an organic silver salt) through so-called superadditivity. Other interaction is for a chain reaction in which an oxidized state of one reducing agent formed by a reduction of silver halide (and/or an organic silver salt) induces or inhibits the polymerization of the polymerizable compound via oxidation-reduction reaction with other reducing agent. Both interactions may occur simultaneously. Thus, it is difficult to determine which of the interactions has occurred in practical use. 
     Examples of these reducing agents include pentadecylhydroquinone, 5-t-butylcatechol, p-(N,N-diethylamino)-phenol, 1-phenyl-4-methyl-4-hydroxymethyl-3-pyrazolidone, 1-phenyl-4-methyl-4-heptadecylcarbonyloxymethyl-3-pyrazolidone, 2-phenylsulfonylamino-4-hexadecyloxy-5-t-octylphenol, 2-phenylsulfonylamino-4-t-butyl-5-hexadecyloxyphenol, 2-(N-butylcarbamoyl)-4-phenylsulfonylaminonaphtol, 2-(N-methyl-N-octadecylcarbamoyl)-4-sulfonylaminonaphthol, 1-acetyl-2-phenylhydrazine, 1-acetyl-2-(p- or o-aminophenyl)hydrazine, 1-formyl-2-(p- or o-aminophenyl)hydrazine, 1-acetyl-2-(p- or o-methoxyphenyl)hydrazine, 1-lauroyl-2-(p- or o-aminophenyl)hydrazine, 1-trityl-2-(2,6-dichloro-4-cyanophenyl)hydrazine, 1-trityl-2-phenylhydrazine, 1-phenyl-2-(2,4,6-trichlorophenyl)hydrazine, 1-{2-(2,5-di-tert-pentylphenoxy)butyloyl}-2-(p- or o-aminophenyl)hydrazine, 1-{2-(2,5-di-t-pentylphenoxy)-butyloyl}-2-(p- or o-aminophenyl)hydrazine pentadecylfluorocaprylate salt, 3-indazolinone, 1-(3,5-dichlorobenzoyl)-2-phenylhydrazine, 1-trityl-2-[{(2-N-butyl-N-octylsulfamoyl)-4-methanesulfonyl}phenyl]hydrazine, 1-{4-(2,5-di-tert-pentylphenoxy)butyloyl}-2-(p- or o-methoxyphenyl)hydrazine, 1-(methoxycarbonylbenzohydryl)-2-phenylhydrazine, 1-formyl-2-[4-{2-(2,4-di-tert-pentylphenoxy)butylamide}phenyl]hydrazine, 1-acetyl-2-[4-{ 2-(2,4-di-tert-pentylphenoxy)butylamido}phenyl]hydrazine, 1-trityl-2-[{2,6-dichloro-4-(N,N-di-2-ethylhexyl)carbamoyl}phenyl]hydrazine, 1-(methoxycarbonylbenzohydryl)-2-(2,4-dichlorophenyl)hydrazine, 1-trityl-2-[{2-(N-ethyl-N-octylsulfamoyl)-4-methanesulfonyl}phenyl]hydrazine, 1-benzoyl-2-tritylhydrazine, 1-(4-butoxybenzoyl)-2-tritylhydrazine, 1-(2,4-dimethoxybenzoyl)-2-tritylhydrazine, 1-(4-dibutylcarbamoylbenzoyl)-2-tritylhydrazine and 1-(1-naphthoyl)-2-tritylhydrazine. 
     The amount of the reducing agent in the light-sensitive layer preferably ranges from 0.1 to 1,500 mole % based on the amount of silver (contained in the above-mentioned silver halide and an organic silver salt). 
     There is no specific limitation with respect to the polymerizable compound, and any known polymerizable compounds including monomers, oligomers and polymers can be contained in the light-sensitive layer. In the case that heat development (i.e., thermal development) is utilized for developing the light-sensitive material, the polymerizable compounds having a relatively higher boiling point (e.g., 80° C. or higher) that are hardly evaporated upon heating are preferably employed. In the case that the light-sensitive layer contains a color image forming substance, the polymerizable compounds are preferably cross-linkable compounds having plural polymerizable groups in the molecule, because such cross-linkable compounds favorably serve for fixing the color image forming substance in the course of polymerization hardening of the polymerizable compounds. 
     The polymerizable compound employable for the light-sensitive material are described in the above-mentioned and later-mentioned publications concerning the light-sensitive material. 
     Preferred polymerizable compounds employable for the light-sensitive material are compounds which are polymerizable through addition reaction or ring-opening reaction. Preferred examples of the compounds being polymerizable through addition reaction include compounds having an ethylenic unsaturated group. Preferred examples of the compounds being polymerizable through ring-opening reaction include the compounds having an epoxy group. Among them, the compounds having an ethylenic unsaturated group are preferred. 
     Examples of compounds having an ethylenic unsaturated group include acrylic acid, salts of acrylic acid, acrylic esters, acrylamides, methacrylic acid, salts of methacrylic acid, methacrylic esters, methacrylamide, maleic anhydride, maleic esters, itaconic esters, styrene, styrene derivatives, vinyl ethers, vinyl esters, N-vinyl heterocyclic compounds, allyl ethers, allyl esters, and compounds carrying a group or groups corresponding to one or more of these compounds. 
     Concrete examples of the acrylic esters include n-butyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, benzyl acrylate, furfuryl acrylate, ethoxyethoxy acrylate, dicyclohexyloxyethyl acrylate, nonylphenyloxyethyl acrylate, hexanediol diacrylate, butanediol diacrylate, neopentylglycol diacrylate, trimethylolpropane triacrylate, pentaerythritol tetraacrylate, dipentaerythritol pentaacrylate, diacrylate of polyoxyethylenated bisphenol A, polyacrylate of hydroxypolyether, polyester acrylate, and polyurethane acrylate. 
     Concrete examples of the methacrylic esters include methyl methacrylate, butyl methacrylate, ethylene glycol dimethacrylate, butanediol dimethacrylate, neopentylglycol dimethacrylate, trimethylolpropane trimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, and dimethacrylate of polyoxyalkylenated bisphenol A. 
     The polymerizable compounds can be used singly or in combination of two or more compounds. For example, a mixture of two or more polymerizable compounds can be employed. Further, compounds formed by bonding a polymerizable group such as a vinyl group or a vinylidene group to a reducing agent or a color image forming substance are also employed as the polymerizable compounds. The light-sensitive materials employing these compounds which show functions as both the reducing agent and the polymerizable compound, or of the color image forming substance and the polymerizable compound are included in embodiments of the invention. 
     The amount of the polymerizable compound for incorporation into the light-sensitive layer preferably ranges from 5 to 1.2×10 5  times (by weight) as much as the amount of silver halide, more preferably from 10 to 1×10 4  times as much as the silver halide. 
     The light-sensitive material can be prepared by arranging a light-sensitive layer containing the above-mentioned components on a support. There is no limitation with respect to the support. In the case that heat development is utilized in the use of the light-sensitive material, the material of the support preferably is resistant to heat given in the processing stage. Examples of the material employable for the preparation of the support include glass, paper, fine paper, coat paper, synthetic paper, metals and analogues thereof, polyester, acetyl cellulose, cellulose ester, polyvinyl acetal, polystyrene, polycarbonate, polyethylene terephthalate, and paper laminated with resin or polymer (e.g., polyethylene). In the case that a porous material, such as paper is employed as the support, the porous support preferably has such a surface characteristic that a filtered maximum waviness of not less than 4 μm is observed in not more than 20 positions among 100 positions which are determined at random on a filtered waviness curve obtained according to JIS-B-No. 0610. 
     Various embodiments of the light-sensitive materials, optional components which may be contained in the light-sensitive layer, and auxiliary layers which may be optionally arranged on the light-sensitive materials are described below. 
     The polymerizable compound is preferably dispersed in the form of oil droplets in the light-sensitive layer. Other components in the light-sensitive layer, such as silver halide, the reducing agent, the triazene compound may be also contained in the oil droplets. 
     The oil droplets of the polymerizable compound are preferably prepared in the form of microcapsules. There is no specific limitation on preparation of the microcapsules. 
     There is also no specific limitation on shell material of the microcapsule, and various known materials such as polymers which are employed in the conventional microcapsules can be employed as the shell material. Examples of the shell material include polyamide resin and/or polyester resin, polyurea resin and/or polyurethane resin, aminoaldehide resin, gelatin, epoxy resin, a complex resin containing polyamide resin and polyurea resin, a complex resin containing polyurethane resin and polyester resin. 
     The mean size of the microcapsule preferably ranges from 0.5 to 50 μm, more preferably 1 to 25 μm, most preferably 3 to 20 μm. In the case that silver halide grains are contained in the microcapsule, the mean grain sized of the silver halide grains preferably is not more than the 5th part of the mean size of the microcapsules, more preferably is not more than the 10th part. It is observed that when the mean sized of the microcapsules is not less than 5 times as much as the mean grain size of silver halide grains, even and uniform image can be obtained. 
     In the case that silver halide grains are contained in the microcapsule, the silver halide grains are preferably arranged in the shell material of the microcapsules. 
     Further, two or more kinds of the microcapsules differing from each other with respect to at least one of the silver halide, the polymerizable compound and the triazene compound can be employed. Furthermore, three or more kinds of the microcapsules differing from each other with respect to the triazene compound is preferably employed to form a full color image. 
     The light-sensitive layer can further contain optional components such as other color image forming substances than the triazene compound, sensitizing dyes, organic silver salts, various kinds of image formation accelerators, thermal polymerization inhibitors, thermal polymerization initiators, development stopping agents, fluorescent brightening agents, discoloration inhibitors, antihalation dyes or pigments, antiirradiation dyes or pigments, matting agents, antismudging agents, plasticizers, water releasers, binders, photo polymerization initiators and solvents of the polymerizable compound. 
     The light-sensitive material of the invention employs the triazene compound as a color image forming substance. The light-sensitive material can further contain the other color image forming substance than the triazene compound. There is no specific limitation with respect to the other color image forming substance, and various kinds of substances can be employed. Thus, examples of the color image forming substance include both colored substance (i.e., dyes and pigments) and non-colored or almost non-colored substance (i.e., color former or dye- or pigment-precursor) which develops to give a color under application of external energy (e.g., heating, pressing, light irradiation, etc.) or by contact with other components (i.e., developer). The light-sensitive material using the color image forming substance is described in Japanese Patent Provisional Publication No. 61(1986)-73145 (corresponding to U.S. Pat. No. 4,629,676 and European Patent Provisional Publication No. 0174634A2). 
     There is no specific limitation with respect to the sensitizing dyes, and known sensitizing dyes used in the conventional art of photography may be employed in the light-sensitive material. Examples of the sensitizing dyes include methine dyes, cyanine dyes, merocyanine dyes, complex cyanine dyes, complex merocyanine dyes, holopolar cyanine dyes, hemicyanine dyes, styryl dyes, and hemioxonol dyes. These sensitizing dyes can be used singly or in combination. Combinations of sensitizing dyes are often used for the purpose of supersensitization. In addition to the sensitizing dyes, a substance which does not per se exhibit spectral sensitization effect or does not substantially absorb visible light but shows supersensitizing activity can be used. The amount of the sensitizing dye to be added generally ranges from about 10 -8  to about 10 -2  mol per 1 mol of silver halide. The sensitizing dye is preferably added during the stage of the preparation of the silver halide emulsion (simultaneously with or after the grain formation). 
     When the heat development is employed in the use of the light-sensitive material, an organic silver salt is preferably contained in the light-sensitive material. It can be assumed that the organic silver salt takes part in a redox reaction using a silver halide latent image as a catalyst when heated to a temperature of 80° C. or higher. In such case, the silver halide and the organic silver salt preferably are located in contact with each other or close together. Examples of organic compounds employable for forming such organic silver salt include aliphatic or aromatic carboxylic acids, thiocarbonyl group-containing compounds having a mercapto group or an α-hydrogen atom, imino group-containing compounds, and the like. Among them, benzotriazoles are most preferable. The organic silver salt is preferably used in an amount of from 0.01 to 10 mol., and preferably from 0.01 to 1 mol., per 1 mol. of the light-sensitive silver halide. Instead of the organic silver salt, an organic compound (e.g., benzotriazole) which can form an organic silver salt in combination with an inorganic silver salt can be added to the light-sensitive layer to obtain the same effect. 
     Various image formation accelerators are employable in the light-sensitive material. The image formation accelerators have a function to accelerate the oxidation-reduction reaction between a silver halide (and/or an organic silver salt) and a reducing agent, a function to accelerate emigration of an image forming substance from a light-sensitive layer to an image-receiving material or an image-receiving layer, or a similar function. The image formation accelerators can be classified into inorganic bases, organic bases, base precursors, oils, surface active agents, compounds functioning as an antifogging agent and/or a development accelerator, hot-melt solvents, antioxidants and the like. These groups, however, generally have certain combined functions, i.e., two or more of the above-mentioned effects. Thus, the above classification is for the sake of convenience, and one compound often has a plurality of functions combined. 
     Various examples of these image formation accelerators are shown below. 
     Preferred examples of the inorganic bases include hydroxides of alkali metals or alkaline earth metals; secondary or tertiary phosphates, borates, carbonates, quinolinates and metaborates of alkali metals or alkaline earth metals; a combination of zinc hydroxide or zinc oxide and a chelating agent (e.g., sodium picolinate); ammonium hydroxide; hydroxides of quaternary alkylammoniums; and hydroxides of other metals. Preferred examples of the organic bases include aliphatic amines (e.g., trialkylamines, hydroxylamines and aliphatic polyamines); aromatic amines (e.g., N-alkyl-substituted aromatic amines, N-hydroxylalkyl-substituted aromatic amines and bis[p-(dialkylamino)phenyl]-methanes), heterocyclic amines, amidines, cyclic amidines, guanidines, and cyclic guanidines. Of these bases, those having a pKa of 7 or more are preferred. 
     The base precursors preferably are those capable of releasing bases upon reaction by heating, such as salts between bases and organic acids capable of decarboxylation by heating, compounds capable of releasing amines through intramolecular nucleophilic substitution, Lossen rearrangement, or Beckmann rearrangement, and the like; and those capable of releasing bases by electrolysis. Preferred examples of the base precursors include guanidine trichloroacetate, piperidine trichloroacetate, morpholine trichloroacetate, p-toluidine trichloroacetate, 2-picoline trichloroacetate, guanidine phenylsulfonylacetate, guanidine 4-chlorophenylsulfonylacetate, guanidine 4-methyl-sulfonylphenylsulfonylacetate, and 4-acetylaminomethyl propionate. 
     These bases or base precursors are preferably used in an amount of not more than 100% by weight, and more preferably from 0.1 to 40% by weight, based on the total solid content of the light-sensitive layer. These bases or base precursors can be used singly or in combination. 
     In the light-sensitive material, the silver halide, the reducing agent, the polymerizable compound and the triazene compound are preferably contained in a microcapsule and the base or base precursor is preferably arranged outside of the microcapsule in the light-sensitive layer. Further, the base or base precursor can be contained in a different microcapsule from that containing the polymerizable compound. The base or base precursor can be contained in the microcapsule under condition that the base or base precursor is dissolved or dispersed in an aqueous solution of a water retention agent, or under condition that the base or base precursor is adsorbed on solid particles. Furthermore, the base or base precursor can be contained in a different layer from the light-sensitive layer. 
     Examples of the oils employable in the invention include high-boiling organic solvents which are used as solvents in emulsifying and dispersing hydrophobic compounds. 
     Examples of the surface active agents employable in the invention include pyridinium salts, ammonium salts and phosphonium salts as described in Japanese Patent Provisional Publication No. 59(1984)-74547; polyalkylene oxides as described in Japanese Patent Provisional Publication No. 59(1984)-57231. 
     The compounds functioning as an antifogging agent and/or a development accelerator are used to give a clear image having a high maximum density and a low minimum density (an image having high contrast). Examples of the compounds include a 5- or 6-membered nitrogen containing heterocyclic compound (e.g., a cyclic amide compound), a thiourea derivative, a thioether compound, a polyethylene glycol derivative, a thiol derivative, an acetylene compound and a sulfonamide derivative. 
     The hot-melt solvents preferably are compounds which may be used as solvent of the reducing agent or those which have high dielectric constant and can accelerate physical development of silver salts. Examples of the hot-melt solvents include polyethylene glycols, derivatives of polyethylene oxides (e.g., oleate ester), beeswax, monostearin and high dielectric constant compounds having --SO 2  -- and/or --CO-- group described in U.S. Pat. No. 3,347,675; polar compounds described in U.S. Pat. No. 3,667,959; and 1,10-decanediol, methyl anisate and biphenyl suberate described in Research Disclosure 26-28 (Dec. 1976). The light-sensitive material employing the hot-melt solvents is described in Japanese patent application No. 60(1985)-227527. The hot-melt solvent is preferably used in an amount of from 0.5 to 50% by weight, and more preferably from 1 to 20% by weight, based on the total solid content of the light-sensitive layer. 
     The antioxidants can be used to eliminate the influence of the oxygen which has an effect of inhibiting polymerization in the development process. Example of the antioxidants is a compound having two or more mercapto groups. 
     The thermal polymerization initiators employable in the light-sensitive material preferably are compounds that are decomposed under heating to generate a polymerization initiating species, particularly a radical, and those commonly employed as initiators of radical polymerization. The thermal polymerization initiators are described in &#34;Addition Polymerization and Ring Opening Polymerization&#34;, 6-18, edited by the Editorial Committee of High Polymer Experimental Study of the High Polymer Institute, published by Kyoritsu Shuppan (1983). Examples of the thermal polymerization initiators include azo compounds, e.g., azobisisobutyronitrile, 1,1&#39;-azobis(1-cyclohexanecarbonitrile), dimethyl 2,2&#39;-azobisisobutyrate, 2,2&#39;-azobis(2-methylbutyronitrile), and azobisdimethylvaleronitrile; organic peroxides, e.g., benzoyl peroxide, di-tert-butyl peroxide, dicumyl peroxide, tert-butyl hydroperoxide, and cumene hydroperoxide; inorganic peroxides, e.g., hydrogen peroxide, potassium persulfate, and ammonium persulfate; and sodium p-toluenesulfinate. The thermal polymerization initiators are preferably used in an amount of from 0.1 to 120% by weight, and more preferably from 1 to 10% by weight, based on amount of the polymerizable compound. In a system in which the polymerizable compound within the area where the latent image has not been formed is polymerized, the thermal polymerization initiators are preferably incorporated into the light-sensitive layer. The light-sensitive material employing the thermal polymerization initiators is described in Japanese Patent Provisional Publication No. 61(1986)-260241. 
     The development stopping agents employable in the light-sensitive material are compounds that neutralize a base or react with a base to reduce the base concentration in the layer to thereby stop development, or compounds that mutually react with silver or a silver salt to suppress development. More specifically, examples of the development stopping agents include acid precursors capable of releasing acids upon heating electrophilic compounds capable of undergoing substitution reaction with a coexisting base upon heating, nitrogen-containing heterocyclic compounds, mercapto compounds, and the like. Examples of the acid precursors include oxide esters described in Japanese Patent Provisional Publication Nos. 60(1985)-108837 and 60(1985)-192939 and compounds which release acids through Lossen rearrangement described in Japanese Patent Provisional Publication No. 60(1985)-230133. Examples of the electrophilic compounds which induce substitution reaction with bases upon heating are described in Japanese Patent Provisional Publication No. 60(1985)-230134. 
     The antismudging agents employable in the light-sensitive material preferably are particles which are solid at ambient temperatures. Examples of the antismudging agents include starch particles described in U.K. Pat. No. 1,232,347; polymer particles described in U.S. Pat. No. 3,625,736; microcapsule particles containing no color former described in U.K. Pat. No. 1,235,991; and cellulose particles, and inorganic particles, such as particles of talc, kaolin, bentonite, agalmatolite, zinc oxide, titanium dioxide or aluminum oxide described in U.S. Pat. No. 2,711,375. Such particles preferably have a mean size of 3 to 50 μm, more preferably 5 to 40 μm. When the microcapsule is employed in the light-sensitive material, the size of said particle is preferably larger than that of the microcapsule. 
     Binders employable in the light-sensitive material preferably are transparent or semi-transparent hydrophilic binders. Examples of the binders include natural substances, such as gelatin, gelatin derivatives, cellulose derivatives, starch, and gum arabic; and synthetic polymeric substances, such as water-soluble polyvinyl compounds e.g., polyvinyl alcohol, polyvinylpyrrolidone, and acrylamide polymers. In addition to the synthetic polymeric substances, vinyl compounds dispersed in the form of latex, which are particularly effective to increase dimensional stability of photographic materials, can be also used. These binders can be used singly or in combination. The light-sensitive material employing a binder is described in Japanese Patent Provisional Publication No. 61(1986)-69062 (corresponding to U.S. Pat. No. 4,629,676 and European Patent Provisional Publication No. 0174634A2). 
     The photo polymerization initiator can be contained in the light-sensitive layer to polymerize the unpolymerized polymerizable compound after the image-formation. 
     In the case that the solvent of the polymerizable compound is used, the solvent is preferably contained in a microcapsule which is different from the microcapsule containing the polymerizable compound. 
     Examples and usage of the other optional components which can be contained in the light-sensitive layer are also described in the above-mentioned publications and applications concerning the light-sensitive material, and in Research Disclosure Vol. 170, No. 17029, 9-15 (Jun. 1978). 
     Examples of auxiliary layers which are optionally arranged on the light-sensitive material include an image-receiving layer, a heating layer, an antistatic layer, an anticurl layer, a release layer, a cover sheet or a protective layer, a layer containing a base or base precursor and a base barrier layer. 
     Instead of the use of the image-receiving material, the image-receiving layer can be arranged on the light-sensitive material to produce the desired image on the image-receiving layer of the light-sensitive material. The image-receiving layer of the light-sensitive material can be constructed in the same manner as the layer of the image-receiving layer. 
     The light-sensitive material can be prepared, for instance, by the following process. 
     The light-sensitive material is usually prepared by dissolving, emulsifying or dispersing each of the components of the light-sensitive layer in an adequate medium to obtain coating solution, and then coating the obtained coating solution on a support. 
     The coating solution can be prepared by mixing liquid compositions each containing a component of the light-sensitive layer. Liquid composition containing two or more components may be also used in the preparation of the coating solution. Some components of the light-sensitive layer cna be directly added to the coating solution or the liquid composition. Further, a secondary composition can be prepared by emulsifying the oily (or aqueous) composition in an aqueous (or oily) medium to obtain the coating solution. 
     The silver halide is preferably prepared in the form of a silver halide emulsion. Various processes for the preparation of the silver halide emulsion are known in the conventional technology for the preparation of photographic materials. 
     The silver halide emulsion can be prepared by the acid process, neutral process or ammonia process. In the stage for the preparation, a soluble silver salt and a halogen salt can be reacted in accordance with the single jet process, double jet process or a combination thereof. A reverse mixing method, in which grains are formed in the presence of excess silver ions, or a controlled double jet process, in which a pAg value is maintained constant, can be also employed. In order to accelerate grain growth, the concentrations or amounts or the silver salt and halogen salt to be added or the rate of their addition can be increased as described in Japanese Patent Provisional Publication Nos. 55(1980)-142329 and 55(1980)-158124, and U.S. Pat. No. 3,650,757, etc. 
     The silver halide emulsion may be of a surface latent image type that forms a latent image predominantly on the surface of silver halide grains, or of an inner latent image type that forms a latent image predominantly in the interior of the grains. A direct reversal emulsion comprising an inner latent image type emulsion and a nucleating agent may be employed. The inner latent image type emulsion suitable for this purpose is described in U.S. Pat. Nos. 2,592,250 and 3,761,276, Japanese Patent Publication No. 58(1983)-3534 and Japanese Patent Provisional Publication No. 57(1982)-136641, etc. The nucleating agent that is preferably used in combination with the inner latent image type emulsion is described in U.S. Pat. Nos. 3,227,552, 4,245,037, 4,255,511, 4,266,013 and 4,276,364, and West German Patent Provisional Publication (OLS) No. 2,635,316. 
     In the preparation of the silver halide emulsions, hydrophilic colloids are advantageously used as protective colloids. Examples of usable hydrophilic colloids include proteins, e.g., gelatin, gelatin derivatives, gelatin grafted with other polymers, albumin, and casein; cellulose derivatives, e.g., hydroxyethyl cellulose, carboxymethyl cellulose, cellulose sulfate, etc.; saccharide derivatives, e.g., sodium alginate and starch derivatives; and a wide variety of synthetic hydrophilic polymers, such as polyvinyl alcohol, polyvinyl alcohol partial acetal, poly-N-vinylpyrrolidone, polyacrylic acid, polymethacrylic acid, polyacrylamide, polyvinylimidazole, and polyvinylpyrazole, and copolymers comprising monomers constituting these homopolymers. Among them, gelatin is most preferred. Examples of employable gelatins include not only lime-processed gelatin, but also acid-processed gelatin and enzyme-processed gelatin. Hydrolysis products or enzymatic decomposition products of gelatin can also be used. 
     In the formation of silver halide grains in the silver halide emulsion, ammonia, an organic thioether derivative as described in Japanese Patent Publication No. 47(1972)-11386 or sulfur-containing compound as described in Japanese Patent Provisional Publication No. 53(1978)-144319 can be used as a silver halide solvent. Further, in the grain formation or physical ripening, a cadmium salt, a zinc salt, a lead salt, a thallium salt, or the like can be introduced into the reaction system. Furthermore, for the purpose of improving high or low intensity reciprocity law failure, a water-soluble iridium salt, e.g., iridium (III) or (IV) chloride, or ammonium hexachloroiridate, or a water-soluble rhodium salt, e.g., rhodium chloride can be used. 
     After the grain formation or physical ripening, soluble salts may be removed from the resulting emulsion by a known noodle washing method or a sedimentation method. The silver halide emulsion may be used in the primitive condition, but is usually subjected to chemical sensitization. Chemical sensitization can be carried out by the sulfur sensitization, reduction sensitization or noble metal sensitization, or a combination thereof that are known for emulsions for the preparation of the conventional light-sensitive materials. 
     When the sensitizing dyes are added to the silver halide emulsion, the sensitizing dye is preferably added during the preparation of the emulsion. When the organic silver salts are introduced in the light-sensitive microcapsule, the emulsion of the organic silver salts can be prepared in the same manner as in the preparation of the silver halide emulsion. 
     In preparation of the light-sensitive material, the polymerizable compounds are used as the medium for preparation of the liquid composition containing another component of the light-sensitive layer. For example, the silver halide, including the silver halide emulsion), the reducing agent, or the triazene compound can be dissolved, emulsified or dispersed in the polymerizable compound to prepare the light-sensitive material. Especially, the triazene compound is preferably incorporated in the polymerizable compound. Further, the necessary components for preparation of a microcapsule, such as shell material can be incorporated into the polymerizable compound. 
     The light-sensitive composition which is the polymerizable compound containing the silver halide can be prepared using the silver halide emulsion. The light-sensitive composition can be also prepared using silver halide powders which can be prepared by lyophilization. These light-sensitive composition can be obtained by stirring the polymerizable compound and the silver halide using a homogenizer, a blender, a mixer or other conventional stirring device. 
     Polymers having a principal chain consisting essentially of a hydrocarbon chain substituted in part with hydrophilic groups which contain, in their terminal groups, --OH or nitrogen having a lone electron-pair are preferably introduced into the polymerizable compound prior to the preparation of the light-sensitive composition. The polymer has a function of dispersing silver halide or other component in the polymerizable compound very uniformly as well as a function of keeping thus dispered state. Further, the polymer has another function of gathering silver halide along the interface between the polymerizable compound (i.e., light-sensitive composition) and the aqueous medium in preparation of the microcapsule. Therefore, using this polymer, silver halide can be easily introduced into the shell material of the microcapsule. 
     The polymerizable compound (including the light-sensitive composition) are preferably emulsified in an aqueous medium to prepare the coating solution. The necessary components for preparation of the microcapsule, such as shell material can be incorporated into the emulsion. Further, other components such as the reducing agent can be added to the emulsion. 
     The emulsion of the polymerizable compound can be processed for forming shell of the microcapsule. Examples of the process for the preparation of the micro-capsules include a process utilizing coacervation of hydrophilic wall-forming materials as described in U.S. Pat. Nos. 2,800,457 and 2,800,458; an interfacial polymerization process as described in U.S. Pat. No. 3,287,154, U.K. Pat. No. 990,443 and Japanese Patent Publication Nos. 38(1963)-19574, 42(1967)-446 and 42(1967)-771; a process utilizing precipitation of polymers as described in U.S. Pat. Nos. 3,418,250 and 3,660,304; a process of using isocyanate-polyol wall materials as described in U.S. Pat. No. 3,796,669; a process of using isocyanate wall materials as described in U.S. Pat. No. 3,914,511; a process of using ureaformaldehyde or urea-formaldehyde-resorcinol wall-forming materials as described in U.S. Pat. Nos. 4,001,140, 4,087,376 and 4,089,802; a process of using melamineformaldehyde resins hydroxypropyl cellulose or like wall-forming materials as described in U.S. Pat. No. 4,025,455; an in situ process utilizing polymerization of monomers as described in U.K. Pat. No. 867,797 and U.S. Pat. No. 4,001,140; an electrolytic dispersion and cooling process as described in U.K. Pat. Nos. 952,807 and 965,074; a spray-drying process as described in U.S. Pat. No. 3,111,407 and U.K. Pat. No. 930,422; and the like. It is preferable, though not limitative, that the microcapsule is prepared by emulsifying core materials containing the polymerizable compound and forming a polymeric membrane (i.e., shell) over the core materials. 
     When the emulsion of the polymerizable compound (including the dispersion of the microcapsule) has been prepared by using the light-sensitive composition, the emulsion can be used as the coating solution of the light-sensitive material. The coating solution can be also prepared by mixing the emulsion of the polymerizable compound and the silver halide emulsion. The other components can be added to the coating solution in a similar manner as the emulsion of the polymerizable compound. 
     A light-sensitive material of the invention can be prepared by coating and drying the above-prepared coating solution on a support in the conventional manner. 
     The present invention is further described by the following examples without limiting the invention. 
     EXAMPLE 1 
     Preparation of silver halide emulsion 
     In 1,000 ml of water were dissolved 20 g of gelatin and 3 g of sodium chloride, and the resulting gelatin solution was kept at 75° C. To the gelatin solution, 600 ml of an aqueous solution containing 21 g of sodium chloride and 56 g of potassium bromide and 600 ml of an aqueous solution containing 0.59 mole of silver nitrate were added simultaneously at the same feed rate over a period of 40 minutes to obtain a silver chlorobromide emulsion having cubic grains, uniform grain size distribution, a mean grain size of 0.35 μm and a bromide content of 80 mole %. 
     The emulsion was washed for desalting and then subjected to chemical sensitization with 5 mg of sodium thiosulfate and 20 mg of 4-hydroxy-6-methyl-1,3,3a,7-tetraazaindene at 60° C. The yield of the emulsion was 600 g. 
     Preparation of silver benzotriazole emulsion 
     In 3,000 ml of water were dissolved 28 g of gelatin and 13.2 g of benzotriazole, and the solution was kept at 40° C. while stirring. To the solution was added 100 ml of an aqueous solution of 17 g of silver nitrate over 2 minutes. Excessive salts were sedimented and removed from the resulting emulsion by pH-adjustment. Thereafter, the emulsion was adjusted to pH 6.30 to obtain a silver benzotriazole emulsion. The yield of the emulsion was 400 g. 
     Preparation of light-sensitive composition 
     In 100 g of trimethylolpropane triacrylate were dissolved 0.40 g of the following copolymer, 4.5 g of the following triazene compound (a) and 2 g of Emulex NP-8 (tradename of Nippon Emulsion Co., Ltd.). ##STR7## 
     To 18.00 g of the resulting solution were added a solution in which 0.16 g of the following reducing agent (I) and 1.22 g of the following reducing agent (II) are dissolved in 1.80 g of methylene chloride. ##STR8## 
     To the mixture were further added 3.50 g of the silver halide emulsion and 3.35 g of the silver benzotriazole emulsion, and the mixture was stirred at 15,000 r.p.m. for 5 minutes to obtain a light-sensitive composition. 
     Preparation of light-sensitive microcapsule 
     To 10.51 g of 18.6% aqueous solution of Isobam (tradename of Kuraray Co., Ltd.) was added 48.56 g of 2.89% aqueous solution of pectin. After the solution was adjusted to a pH of 4.0 using 10% sulfuric acid, the light-sensitive composition was added to the resulting solution, and the mixture was stirred at 7,000 r.p.m. for 2 min. to emulsify the light-sensitive composition in the aqueous medium. 
     To 72.5 g of the aqueous emulsion were added 8.32 g of 40% aqueous solution of urea, 2.82 g of 11.3% aqueous solution of resorcinol, 8.56 g of 37% aqueous solution of formaldehyde, and 2.74 g of 8.76% aqueous solution of ammonium sulfate in this order, and the mixture was heated at 60° C. for 2 hours while stirring. After the mixture was adjusted to a pH of 7.0 using 10% aqueous solution of sodium hydroxide, 3.62 g of 30.9% aqueous solution of sodium hydrogen sulfite was added to the mixture to obtain a dispersion containing light-sensitive microcapsules. 
     Preparation of light-sensitive material 
     To 10.0 g of the light-sensitive microcapsule dispersion were added 1.0 g of 1% aqueous solution of the following anionic surfactant, 1.0 g of 10% solution (solvent: water/ethanol=50/50 as volume ratio) of guanidine trichroloacetate to prepare a coating solution. ##STR9## 
     The coating solution was uniformly coated on a polyethyleneterephthalate film (thickness: 100 μm) using a coating rod of #40 to a wet thickness of 70 μm and dried at about 40° C. to obtain a light-sensitive material (A). 
     EXAMPLE 2 
     Preparation of light-sensitive material 
     Each of the light-sensitive materials (B) to (E) was prepared in the same manner as in Example 1 except that each of the following triazene compounds (b) to (e) (amount is set forth in Table 1) was respectively used in place of 4.5 g of the triazene compound (a). ##STR10## 
     Preparation of image-receiving material 
     To 150 g of water was added 11 g of 40% aqueous solution of sodium hexametaphosphate, and were further added 1.4 g of the following coupler, 34 g of zinc 3,5-di-α-methylbenzylsalicylate and 82 g of 55% slurry of calcium carbonate, followed by coarsely dispersing in a mixer. ##STR11## 
     The coarse dispersion was then finely dispersed in Dynomill dispersing device. To 200 g of the resulting dispersion were added 6 g of 50% latex of SBR (styrenebutadiene rubber) and 55 g of 8% aqueous solution of polyvinyl alcohol, and the resulting mixture was made uniform. The mixture was then uniformly coated on an art paper having a basis weight of 43 g/m 2  to give a layer having a wet thickness of 30 μm and dried to obtain an image-receiving material. 
     Evaluation of light-sensitive material 
     Each of the light-sensitive materials prepared in Examples 1 and 2 was imagewise exposed to light using a tungsten lamp at 200 lux for 1 second and then heated on a hot plate at 125° C. for 30 seconds. Each of the exposed and heated light-sensitive materials was then combined with the image-receiving material and passed through press rolls under pressure of 350 kg/cm 2 . The image-receiving material was further heated on a hot plate at 100° C. for 10 seconds. The density of the positive color image obtained on the image-receiving material was measured at each of the maximum wavelengths of the absorption using a reflection densitometer. 
     The results are set forth in Table 1. 
     
                       TABLE 1                                                     
______________________________________                                    
                                       Min-                               
Light- Triazene compound                                                  
                      Hue in    Max-   imum                               
Sensitive        Amount   Color   imum   Den-                             
Material                                                                  
       Compound  (g)      Image   Density                                 
                                         sity                             
______________________________________                                    
(A)    (a)       4.5      Yellowish                                       
                                  1.08   0.15                             
                          Orange                                          
(B)    (b)       4.6      Red     1.02   0.12                             
(C)    (c)       5.0      Red     1.10   0.12                             
(D)    (d)       4.7      Blue    1.16   0.16                             
(E)    (e)       4.5      Blue    1.12   0.18                             
______________________________________                                    
 
    
     It is apparent from the results in Table 1 that each of the light-sensitive materials forms an improved positive image which has a high maximum density and a low minimum density. 
     Further, each of the image-receiving materials on which the image had been formed was irradiated with light at 32,000 lux for 6 hours using a fluorescent lamp, and each of the fading ratios in the images was measured. As a result, each of the ratios was not more than 10%. It is also apparent from the result that each of the light-sensitive materials of the invention forms an image improved in light fastness.