Patent Publication Number: US-2002008270-A1

Title: Diffusion barrier layers and methods of forming same

Description:
FIELD OF THE INVENTION  
       [0001] The present invention relates to semiconductor devices and the fabrication thereof. More particularly, the present invention pertains to diffusion barrier layers.  
       BACKGROUND OF THE INVENTION  
       [0002] In the fabrication of integrated circuits, various conductive layers are used. For example, during the formation of semiconductor devices, such as dynamic random access memories (DRAMs), static random access memories (SRAMs), ferroelectric (FE) memories, etc., conductive materials are used in the formation of storage cell capacitors and also may be used in interconnection structures, e.g., conductive layers in contact holes, vias, etc. In many applications, it is preferable that the material used provide effective diffusion barrier characteristics.  
       [0003] For example, effective diffusion barrier characteristics are required for conductive materials used in the formation of storage cell capacitors of memory devices, e.g., DRAMs. As memory devices become more dense, it is necessary to decrease the size of circuit components forming such devices. One way to retain storage capacity of storage cell capacitors of the memory devices and at the same time decrease the memory device size is to increase the dielectric constant of the dielectric layer of the storage cell capacitor. Therefore, high dielectric constant materials are used in such applications interposed between two electrodes. One or more layers of various conductive materials may be used as the electrode material. However, generally, one or more of the layers of the conductive materials used for the electrodes (particularly the lower electrode of a cell capacitor) must have certain barrier properties and oxidation resistance properties. Such properties are particularly required when high dielectric constant materials are used for the dielectric layer of the storage cell capacitor because of the processes used for forming such high dielectric materials, e.g., deposition of high dielectric materials usually occurs at high temperatures (generally greater than about 500° C.) in an oxygen-containing atmosphere.  
       [0004] Generally, various metals and metallic compounds, and typically notable metals such as platinum and conductive oxides such as ruthenium oxide, have been proposed as the electrodes or at least one of the layers of the electrodes for use with high dielectric constant materials. However, reliable electrical connections should generally be constructed which do not diminish the beneficial properties of the high dielectric constant materials. For platinum to function well as a bottom electrode, it must be an effective barrier to the difflusion of oxygen. This is required since any oxidation of underlying silicon upon which the capacitor is formed will result in a decreased series capacitance, thus degrading the storage capacity of the cell capacitor. Platinum, used alone as an electrode layer, is too permeable to oxygen to be used as a bottom electrode of a storage cell capacitor.  
       [0005] Because of the permeability of platinum to oxygen, typically platinum is used as a layer in an electrode stack which acts as the electrode as well as a diffusion barrier for integration of capacitors directly formed on silicon. For example, as described in the article “Novel High Temperature Multilayer Electrode-Barrier Structure for High Density Ferroelectric Memories” by H. D. Bhatt, et al.,  Appl. Phys. Letter,  71(5), Aug. 4, 1997, the electrode barrier structure includes layers of platinum:rhodium alloy, in addition to platinum:rhodium oxide layers, to form electrodes with difflusion barrier properties. Such alloy layers are formed using physical vapor deposition (PVD) processing, e.g., reactive RF sputtering processes.  
       [0006] Many storage cell capacitors are formed using high aspect ratio openings. For example, in U.S. Pat. No. 5,392,189 to Fazan, et al., entitled “Capacitor Compatible with High Dielectric Constant Materials Having Two Independent Insulative Layers and the Method for Forming Same,” issued Feb. 21, 1995, the storage cell capacitors include a lower electrode that is formed by deposition of a conductive material within a small high aspect ratio opening. Typically, sputtering does not provide a sufficiently conformal layer adequate for formation of an electrode within such a small high aspect ratio opening.  
       [0007] In addition to the formation of capacitor electrodes, the formation of barrier layers for use in other applications, e.g., interconnect applications, is also desirable. For example, diffusion barriers are commonly used to prevent undesirable reactions in contact openings.  
       SUMMARY OF THE INVENTION  
       [0008] To overcome the problems described above with respect to the use of platinum alone as an electrode material, and others which will be apparent from the detailed description below, a platinum:ruthenium diffusion barrier layer, structures incorporating such layers, and methods associated therewith are described herein.  
       [0009] A method for use in the fabrication of integrated circuits according to the present invention includes providing a substrate assembly having a surface and forming a barrier layer over at least a portion of the surface. The barrier layer is formed of a platinum(x):ruthenium(1-x) alloy, where x is in the range of about 0.60 to about 0.995.  
       [0010] In other embodiments of the method, preferably, x is in the range of about 0.90 to about 0.98, and more preferably, x is about 0.95. In another embodiment of the method, the barrier layer is formed by chemical vapor deposition. In yet another embodiment of the method, the portion of the surface upon which the barrier layer is formed is a silicon containing surface.  
       [0011] Another method for use in the formation of a capacitor according to the present invention includes forming a first electrode on a portion of a substrate assembly. A high dielectric material is formed over at least a portion of the first electrode and a second electrode is formed over the high dielectric material. At least one of the first and second electrodes comprises a layer of a platinum:ruthenium alloy.  
       [0012] In one embodiment of the method, at least one of the first electrode and second electrode includes the layer of platinum(x):ruthenium(1-x) alloy and one or more additional conductive layers.  
       [0013] Another method for use in forming a storage cell including a capacitor according to the present invention is described. The method includes providing a substrate assembly including at least one active device and forming a capacitor relative to the at least one active device. The capacitor comprises at least one electrode including a barrier layer of platinum(x):ruthenium(1-x) alloy.  
       [0014] A semiconductor device structure according to the present invention includes a substrate assembly including a surface and a barrier layer over at least a portion of the surface. The barrier layer is formed of a platinum(x):ruthenium(1-x) alloy, wherein x is in the range of about 0.60 to about 0.995.  
       [0015] A capacitor structure according to the present invention includes a first electrode, a dielectric material on at least a portion of the first electrode, and a second electrode on the dielectric material. At least one of the first and second electrodes comprises a barrier layer of platinum(x):ruthenium(1-x) alloy.  
       [0016] A memory cell structure according to the present invention includes a substrate assembly including at least one active device and a capacitor formed relative to the at least one active device. The capacitor comprises at least one electrode including a barrier layer formed of platinum(x):ruthenium(1-x) alloy.  
       [0017] Another integrated circuit structure includes a substrate assembly including at least one active device and an interconnect formed relative to the at least one active device. The interconnect including a barrier layer formed of platinum(x):ruthenium(1-x) alloy.  
     
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
     [0018] The present invention will be better understood from reading the following description of illustrative embodiments with reference to the attached drawings, wherein below:  
     [0019]FIG. 1 shows a device structure including a platinum:ruthenium alloy layer according to the present invention.  
     [0020]FIG. 2 shows a structure including a platinum:ruthenium alloy layer according to the present invention as part of a multiple conductive layer stack.  
     [0021]FIG. 3 is a structure including a high dielectric capacitor including an electrode having a platinum:ruthenium alloy layer according to the present invention.  
     [0022]FIG. 4 illustrates the use of a platinum:ruthenium alloy layer in a storage cell capacitor application.  
     [0023]FIG. 5 illustrates the use of a platinum:ruthenium alloy layer in an interconnect application.  
     [0024] FIGS.  6 A- 6 C show the results of an example wherein a layer of platinum:ruthenium alloy material is deposited. FIG. 6A shows a depth profile of the deposited platinum:ruthenium alloy layer before an oxygen anneal, FIG. 6B shows a depth profile of the deposited platinum:ruthenium alloy layer after an oxygen anneal, and FIG. 6C shows an XPS montage display showing the Si signal during profile through the platinum:ruthenium layer after annealing in oxygen. 
    
    
     DETAILED DESCRIPTION OF THE EMBODIMENTS  
     [0025] The present invention shall be described generally with reference to FIG. 1. Thereafter, embodiments and illustrations of applications of the present invention shall be described with reference to FIGS.  2 - 5 .  
     [0026]FIG. 1 illustrates a structure  10  including a substrate assembly  12  and a platinum:ruthenium alloy layer  14  according to the present invention formed on a surface  13  of the substrate assembly  12 , e.g., a silicon containing surface. The structure  10  is illustrative of the use of a platinum:ruthenium alloy layer for any application requiring an effective barrier layer. In other words, the platinum:ruthenium alloy layer  14  may be used in the fabrication of semiconductor devices wherever it is necessary to prevent the diffusion of one material to an adjacent material. For example, the substrate assembly  12  may be representative of a contact structure having an opening extending to a silicon containing surface. In such a structure, diffusion barriers are commonly used in such openings to prevent undesirable reactions, such as the reaction of a contact material, e.g, aluminum, with the silicon containing surface.  
     [0027] Further, for example, the platinum:ruthenium alloy barrier layer  14  may be used in the formation of storage cell capacitors for use in semiconductor devices, e.g., memory devices. As further described herein, the platinum:ruthenium alloy barrier layer  14  may be used alone as an electrode in such storage cell capacitors or within a stack of layers forming an electrode of a capacitor. One skilled in the art will recognize that various semiconductor processes and structures for various devices, e.g., CMOS devices, memory devices, etc., would benefit from the barrier characteristics of the barrier layers of the present invention and in no manner is the present invention limited to the illustrative embodiments described herein.  
     [0028] As used in this application, “substrate assembly” refers to either a semiconductor substrate such as the base semiconductor layer, e.g., the lowest layer of a silicon material in a wafer, or a silicon layer deposited on another material, such as silicon on sapphire, or a semiconductor substrate having one or more layers or structures formed thereon or regions formed therein. When reference is made to a substrate assembly in the following description, various process steps may have been previously used to form or define regions, junctions, various structures or features, and openings such as vias, contact openings, high aspect ratio openings, etc.  
     [0029] The platinum:ruthenium alloy layer  14  according to the present invention, includes an atomic composition of platinum(x):ruthenium(1-x), where preferably, x is in the range of about 0.60 to about 0.995. In other words, the amount of ruthenium necessary in the platinum layer to accomplish barrier characteristics for semiconductor devices is minimal, i.e., in the range of about 40% to about 0.5%. More preferably, x is in the range of about 0.90 to about 0.98; and, yet more preferably, x is about 0.95, i.e., about 5% ruthenium in the layer is suitable to provide barrier characteristics. In other words, preferably, the atomic composition of the platinum:ruthenium alloy layer  14  is about 95% platinum and 5% ruthenium.  
     [0030] The thickness of the platinum:ruthenium alloy layer  14  is dependent upon the application for which it is used. Preferably, the thickness is in the range of about 10 Å to about 10,000 Å. More preferably, the thickness of the platinum:ruthenium alloy layer  14  is in the range of about 100 Å to about 500 Å. For example, this preferred thickness range of about 100 Å to about 500 Å is applicable to a single platinum:ruthenium alloy layer forming an electrode of a capacitor.  
     [0031] The platinum:ruthenium alloy layer  14  formed on the surface  13  of substrate assembly  12  may be formed by one or more various processes. For example, the formation of the platinum:ruthenium alloy layer  14  may be accomplished by the simultaneous evaporation of the metals from respective sources, i.e., co-evaporation; may be sputter deposited from a single deposition target of platinum:ruthenium alloy; may be deposited by the simultaneous co-sputtering from two targets (i.e., one target including platinum and the other target including ruthenium); or may be deposited by chemical vapor deposition (CVD), for example, atmospheric pressure chemical vapor deposition, low pressure chemical vapor deposition (LPCVD), plasma enhanced chemical vapor deposition (PECVD), or any other chemical vapor deposition technique. Preferably, the formation of the platinum:ruthenium alloy layer  14  is attained by CVD.  
     [0032] For example, the process may be carried out in a chemical vapor deposition reactor, such as a reaction chamber available under the trade designation of 7000 from Genus, Inc., (Sunnyvale, Calif.), or available under the trade designation of 5000 from Applied Materials, Inc., (Santa Clara, Calif.), or available under the trade designation of Prism from Novelus, Inc., (San Jose, Calif.). However, any reaction chamber suitable for performing CVD may be used.  
     [0033] Chemical vapor deposition (CVD) is defined as the formation of a non-volatile solid film on a substrate by the reaction of vapor phase reactants, i.e., reactant gases, that contain desired components. The reactant gases are introduced into the reaction chamber. The gases decompose and react at a heated wafer surface to form the desired layer. Chemical vapor deposition is just one process of providing thin layers on semiconductor wafers, such as films of elemental metals or compounds, e.g., platinum:ruthenium alloy layers. Chemical vapor deposition processes are favored in many respects because of the process capability to provide highly conformal layers even within deep contacts and other openings. Thus, as described further below with reference to FIGS. 4 and 5, CVD processing is preferably used to provide highly conformal layers within deep contacts and other openings such as for lower electrodes of storage cell capacitors. It will be readily apparent to one skilled in the art that although CVD is the preferred process, that the CVD process may be enhanced by various related techniques such as plasma assistance, photo assistance, laser assistance, as well as other techniques.  
     [0034] Preferably, according to the present invention, the co-deposition of platinum and ruthenium is conducted using a CVD process wherein a ruthenium precursor is delivered to a reaction chamber along with a platinum precursor. Preferably, the method is carried out in the presence of an oxidizing reactant gas, such as O 2 , NO, N 2 O, O 3 , hydrogen peroxide, organic peroxides such as T-butyl peroxide, or any other oxidizing agent.  
     [0035] Typically, a liquid precursor is contained in a bubbler reservoir through which a carrier gas, such as helium or any other inert, i.e., nonreactive gas (e.g., nitrogen, argon, neon, and xenon) is bubbled through the reservoir containing the precursor to deliver the precursor to the reaction chamber. For example, a flow of carrier gas having a flow in the range of about one sccm to about 100 sccm of a nonreactive gas, i.e., nonreactive with other gases of the process, is used in a bubbler having a pressure in the range of about 0.5 to about 50 torr and a temperature in the range of about 30° C. to about 70° C. to deliver a platinum precursor to the reaction chamber. Likewise, a carrier gas, i.e., a nonreactive gas, having a flow in a range of about one sccm to about 10 sccm is used in a bubbler containing a ruthenium precursor at the conditions of about 0.5 torr to about 100 torr and a temperature of about 20° C. to about 50° C. to deliver the ruthenium precursor to the reaction chamber. Preferably, the reactant oxidizing gas is provided to the reaction chamber at a flow of about 0 sccm to about 500 sccm.  
     [0036] One skilled in the art will recognize that the manner in which the gases are introduced into the reaction chamber may include one of various techniques. For example, in addition to provision by bubbler techniques, the introduction may be accomplished with the use of compounds which are gases at room temperature or by heating a volatile compound and delivering the volatile compound to the reaction chamber using a carrier gas. Further, solid precursors and various methods of vaporizing such solid precursors may also be used for introduction of reactant compounds into the chamber. As such, the present invention is not limited to any particular technique. Further, typically, the reactant gases are admitted at separate inlet ports. In addition to the reactant gases, a dilution gas (i.e., a gas that is non-reactive with the reactant gases) may also be introduced into the chamber. For example, argon gas may be introduced into the chamber at a varied flow rate.  
     [0037] Therefore, in accordance with the present invention, the reactant gas mixture in the reaction chamber includes at least the ruthenium precursor gas, the platinum precursor gas, and optionally the oxygen reactant gas and/or a dilution gas. Preferably, within the reaction chamber, the partial pressure of ruthenium precursor gas is kept sufficiently low such that the ruthenium deposited is within the ranges described for forming the preferred platinum:ruthenium composition of the alloy layer  14  described above. This partial pressure may be controlled by controlling the flow of the inert gas, e.g., helium, through the bubbler containing the ruthenium precursor or through control of other parameters of the process, such as temperature and pressure of the bubbler.  
     [0038] In the preferred CVD process, the reaction chamber pressure is preferably maintained at a deposition pressure of about 0.5 torr to about 5 torr. The deposition temperature at the wafer surface upon which the platinum:ruthenium alloy layer  14  is deposited is held at a temperature in a range of about 200° C. to about 400° C.  
     [0039] Any ruthenium-containing precursor and platinum-containing precursor may be used in accordance with the present invention. Preferably, the platinum containing precursors include MeCpPtMe 3  (where Cp=cyclopentadienyl), platinum hexafluoroacetylacetonate, CpPtMe 3 , Pt(acetylacetonate) 2 , Pt(F 3 ) 4 , Pt(CO) 2 Cl 2 , cis-PtMe 2 [MeNC] 2 , (COD)Pt(CH 3 ) 2 , (COD)Pt(CH 3 )Cl, (C 5 H 5 )Pt(CH 3 )(CO), (acac)(Pt)(CH 3 ) 3 , where COD=1,5 cycloctadiene and acac=acetylacetonate. Further, preferably, the ruthenium precursors are liquid ruthenium complexes of the following formula (Formula I): (diene)Ru(CO) 3  wherein: “diene” refers to linear, branched, or cyclic dienes, bicyclic dienes, tricyclic dienes, fluorinated derivatives thereof, combinations thereof, and derivatives thereof additionally containing heteroatoms such as halide, Si, S, Se, P, As, or N. These precursor complexes and others are described in Assignees&#39; copending patent application entitled “Precursor Chemistries for Chemical Vapor Deposition of Ruthenium and Ruthenium Oxide” having U.S. Ser. No. ______ (Micron Docket No. 97-0675) and in Assignees&#39; copending patent application entitled “Methods for Preparing Ruthenium and Osmium Compounds” having U.S. Ser. No. ______ (Micron Docket No. 97-0861). Further, for example, additional precursors are generally discussed in U.S. Pat. No. 5,372,849 to McCormick et al. More preferably, the ruthenium precursors used according to the present invention include one of C 6 H 8 Ru(CO) 3 , bis(cyclopentadienyl) ruthenium (II), triruthenium dodecacarbonyl, and cyclopentadienyl dicarbonyl ruthenium (II) dimer.  
     [0040] Methods of forming the co-deposited platinum:ruthenium alloy layer  14  are described in co-pending patent application entitled “Method for Producing Low Carbon/Oxygen Conductive Layers” (Docket No. 150.00730101 (Micron Docket No. 97-0996). One skilled in the art will recognize that these methods and various other methods may be used to form the platinum:ruthenium alloy layer  14  according to the present invention.  
     [0041]FIG. 2 shows a structure  20  including substrate assembly  22  and a stack  24 . The stack  24  includes conductive layers  31 - 34 . One or more of the conductive layers  31 - 34  are platinum:ruthenium alloy layers according to the present invention.  
     [0042] The one or more conductive layers, in addition to including one or more platinum:ruthenium alloy layers, may include conductive layers formed of various conductive materials. For example, the conductive layers may include, but are clearly not limited to, layers formed from metals such as platinum, paladium, rhodium, ruthenium, osmium, and iridium; metal alloys such as platinum:rhodium, platinum:ruthenium, and platinum:iridium; metal oxides such as ruthenium oxide, rhodium oxide, and iridium oxide; metal alloy oxides such as platinum:rhodium oxide, platinum:ruthenium oxide, and platinum:iridium oxide; metal nitrides such as titanium nitride, tungsten nitride, and tantalum nitride; metal silicides such as titanium silicide, ruthenium silicide, rhodium silicide, and iridium silicide.  
     [0043] The stack  24  may be used for one or numerous applications, e.g., interconnection applications, capacitor applications, etc. For example, stack  24  may be used as an electrode for a storage cell capacitor with substrate assembly  22  including a silicon containing surface  23 . As such, the barrier properties of the stack  24  must prevent silicon difflusion from silicon-containing surface  23 . In accordance with the present invention, the layer  31  may be formed as a platinum:ruthenium alloy layer to prevent diffusion of silicon from silicon-containing surface  23  through stack  24  to adjacent layer or layers  29 . Further, for example, in the case where layer  29  is a high dielectric material requiring diffusion barrier properties to prevent oxygen from diffusing through stack  24 , layer  34  or one of the other layers may also be formed as a platinum:ruthenium alloy barrier layer according to the present invention. One skilled in the art will recognize that the platinum:ruthenium alloy layer according to the present invention may be used in a stack of layers for a variety of applications and the stack may include one or more platinum:ruthenium alloy layers. Further, the composition of such platinum:ruthenium layers used in the same stack may differ.  
     [0044]FIG. 3 shows a structure  50  including substrate assembly  52  and capacitor structure  54 . Capacitor structure  54  includes a first electrode  56 , a second electrode  60 , and a high dielectric constant layer  58  interposed therebetween. For example, the dielectric layer may be any suitable material having a desirable dielectric constant, such as Ta 2 O 5 , Ba x Sr (1-X) TiO 3 [BST], BaTiO 3 , SrTiO 3 , PbTiO 3 , Pb(Zr,Ti)O 3 [PZT], (Pb,La)(Zr,Ti)O 3 [PLZT], (Pb,La)TiO 3 [PLT], KNO 3 , and LiNbO 3 . With use of the high dielectric constant layer  58 , diffusion barrier properties of the electrodes is particularly important. For example, to function well in a bottom electrode of a capacitor structure, the electrode layer or electrode stack must act as an effective barrier to the diffusion of oxygen, particularly due to the processes used to form the high dielectric constant materials. Such diffusion barrier properties are particularly required when the substrate assembly  52  includes a silicon-containing surface  53  upon which the capacitor is formed, e.g., polysilicon, silicon substrate material, N-doped silicon, P-doped silicon, etc., since oxidation of the diffused silicon may result in degraded capacitance, e.g., capacitance for a memory device. The co-deposition of the platinum with the ruthenium enhances the barrier properties of the layer formed and thus provides a significant improvement over pure platinum for electrode applications.  
     [0045] One skilled in the art will recognize that either of the electrodes  56 ,  60  may be formed as a single layer of platinum:ruthenium alloy material. Further, such electrodes  56 ,  60  may be formed as a stack such as described with reference to FIG. 2 including one or more layers of a platinum:ruthenium alloy material and one or more additional conductive layers.  
     [0046] Two illustrations of using the platinum:ruthenium alloy layer or layers as described above are shown and described below with reference to FIGS. 4 and 5. The use of the platinum:ruthenium layer or layers according to the present invention is described with reference to FIG. 4 wherein a bottom electrode of a high dielectric capacitor of a storage cell includes one or more layers of the platinum:ruthenium alloy material as described herein. Further, the use of platinum:ruthenium alloy layer or layers according to the present invention is described with reference to FIG. 5 wherein a contact liner requiring difflusion barrier characteristics is described. For simplistic purposes, the illustrative descriptions are limited to the use of the platinum:ruthenium alloy material described in these two illustrative structures. There are other semiconductor processes and structures for various devices, e.g., CMOS devices, memory devices, logic devices, etc., that would benefit from the present invention and in no manner is the present invention limited to the illustrative embodiments described herein, e.g., contact liner and electrode structure. The platinum:ruthenium alloy barrier layer may be used for any application requiring diffusion barrier characteristics, particularly those for preventing diffusion of oxygen and silicon into adjacent layers.  
     [0047] As shown in FIG. 4, a device structure  100  is fabricated in accordance with conventional processing techniques through the formation of an opening  184  prior to depositing a bottom electrode structure on the surfaces  185 ,  186  defining the opening  184 . A platinum:ruthenium alloy bottom electrode is then formed in opening  184 . As such, and as further described in U.S. Pat. No. 5,392,189 to Fazan, et al., the device structure  100  includes field oxide regions  105  and active regions, i.e., those regions of the substrate  107  not covered by field oxide. A word line  121  and an active device, i.e., field effect transistor (FET)  122 , are formed relative to the field oxide region  105 . Suitable source/drain regions  125 ,  130  are created in silicon substrate  107 . An insulative layer of oxide material  140  is formed over regions of FET  122  and word line  121 . Polysilicon plug  165  is formed to provide electrical communication between substrate  107  and the storage cell capacitor to be formed thereover. Various layers are formed over the polysilicon plug  165 , including layers  167  and  175 . For example, such layers may be titanium nitride, tungsten nitride, or any other metal nitride which acts as a barrier, and may also include one or more platinum:ruthenium alloy barrier layers as described herein. Thereafter, another insulative layer  183  is formed and an opening  184  is defined therein.  
     [0048] The opening  184  is a small high aspect ratio opening. As described herein, small high aspect ratio openings have feature sizes or critical dimensions below about 1 micron (e.g., such as a diameter or width of an opening being less than about 1 micron) and aspect ratios greater than about 1. Such aspect ratios are applicable to contact holes, vias, trenches, and any other configured openings. For example, a trench having an opening of 1 micron and depth of 3 microns has an aspect ratio of 3. The present invention is particularly beneficial for forming diffusion barrier layers in small high aspect ratio features due to the use of CVD processes for forming conformal layers of the platinum:ruthenium alloy material over step structures.  
     [0049] As shown in FIG. 4, a platinum:ruthenium alloy barrier layer  187  is formed on the bottom surface  185  and the one or more side walls  186  defining opening  184 . A layer of platinum:ruthenium alloy material is first co-deposited over the entire structure including the bottom surface  185  and sidewalls  186  and then formed into lower electrode  187 . For example, the layer may be etched or planarized to remove the desired regions for forming the bottom electrode  187 . Thereafter, dielectric layer  191  is then formed relative to the platinum:ruthenium alloy diffusion barrier layer  187 . Further thereafter, the second electrode  192  is formed relative to the dielectric material  191 . For example, such an electrode may be of any conductive material such as the platinum:ruthenium alloy barrier material as described herein, tungsten nitride, titanium nitride, tantalum nitride, ruthenium, rhodium, iridium, ruthenium oxide, iridium oxide, any combination thereof, or any other conductive material typically used as an electrode of a storage cell capacitor. With the use of the present invention, the bottom electrode formed of platinum:ruthenium alloy material is conformally formed of uniform thickness using CVD within opening  184  providing a desired resistivity and barrier properties.  
     [0050] It will be recognized by one skilled in the art that any capacitor formed relative to a surface, e.g., silicon containing surface, whereupon diffusion barrier properties are required and/or conformally formed conductive layers are required will benefit from the present invention. For example, container capacitors typically includes electrodes formed on surfaces requiring conformal formation of a bottom electrode. Such a container capacitor storage cell is described in U.S. Pat. No. 5,270,241 to Dennison, et al., entitled “Optimized Container Stack Capacitor DRAM Cell Utilizing Sacrificial Oxide Deposition and Chemical Mechanical Polishing,” issued Dec. 14, 1993. One skilled in the art will also recognize that the bottom electrode  187  may include a stack of layers with one or more of the layers being a platinum:ruthenium alloy barrier layer as described previously herein.  
     [0051] As shown in FIG. 5, device structure  200  is fabricated in accordance with conventional processing techniques through the formation of contact opening  259  prior to metalization of the contact area  255  of substrate  207 . As such, prior to metalization, the device structure  200  includes field oxide regions  205  and active areas, i.e., those regions of substrate  207  not covered by field oxide. Formed relative to the field oxide regions  205  in the active areas are word line  221  and FET  222 . Suitably doped source/drain regions  225 ,  230  are formed as known to one skilled in the art. A conformal layer of oxide material  240  is formed thereover and contact opening  259  is defined therein to the contact area  255  of doped region  230  of silicon substrate  207 . Thereafter, one or more metalization or conductive layers are formed in the contact opening  259  for providing electrical connection to substrate region  230 . For example, various materials may be formed in contact opening  259 , such as titanium nitride or other diffusion barrier materials. Preferably, contact liner  285  is formed of platinum:ruthenium alloy material according to the present invention on bottom surface  260  and the one or more side walls  261  defining the opening  259 . The platinum:ruthenium alloy layers are generally deposited over the entire substrate assembly and then planarized to form the contact liner  285 . Thereafter, a conductive material  276  is formed in the contact opening for providing connection to doped region  230  of substrate  207 .  
     EXAMPLE  
     [0052]FIGS. 6A and 6B show depth profiles of a co-deposited platinum:ruthenium layer before and after an oxygen anneal, respectively. The small lab scale reaction CVD chamber was built by MDC Vaccuum Products Corp. (Hayward, Calif.) and the glass research bubbler is from Technical Glass Service (Boise, Id.). The conditions used for the co-deposition of the platinum:ruthenium layer include:  
     [0053] Platinum Precursor: MeCpPt(Me) 3 .  
     [0054] Ruthenium Precursor: C 6 H 8 Ru(CO) 3 .  
     [0055] Platinum Carrier Gas for use through Bubbler: 5 sccm of helium.  
     [0056] Ruthenium Carrier Gas for use through Bubbler: 10 sccm of helium.  
     [0057] Platinum Bubbler Conditions: pressure of 10 torr, temperature of 33° C.  
     [0058] Ruthenium Bubbler Conditions: pressure of 40 torr, temperature of 25° C.  
     [0059] Reaction Chamber Conditions: pressure of 5 torr, deposition temperature of 300° C. at wafer surface.  
     [0060] Deposition Time: 4 minutes.  
     [0061] Oxygen Reaction Gas: 10 sccm.  
     [0062] The depth profile was attained by using an XPS device available under the trade designation of Phi (Φ) 5600 from Physical Electronics (Eden Prairie, Minn.). The operating conditions for obtaining the profile include x-ray source of 350 W, monochromatic Al k α  (hV=1486.6 eV); 45 degree extraction; 800 μm extraction aperture. Sputtering was performed with a 4 keV Argon ion beam rastored over a 3 mm area. The sputter time for the depth profile of FIG. 6A was 13 minutes and the sputter time for the depth profile of FIG. 6B was 14.3 minutes.  
     [0063] As shown in FIG. 6A, the co-deposited platinum:ruthenium layer deposited according to the above conditions is shown therein including at a depth of 200 Å a platinum composition of about 70% and a ruthenium composition of about 15%. FIG. 6B shows the co-deposited platinum:ruthenium layer after being subjected to a rapid thermal oxidation anneal at 750° C. for a period of 30 seconds. FIG. 6C shows an XPS montage display showing the Si signal during profile through the platinum:ruthenium layer, after annealing in oxygen. The peak shape shows the lack of SiO 2  at the interface and only traces of Si at the surface. There appears to be no silicon diffusion or oxygen diffusion through the barrier layer and therefore, no silicon dioxide formation.  
     [0064] All patents and references cited herein are incorporated in their entirety as if each were incorporated separately. This invention has been described with reference to illustrative embodiments and is not meant to be construed in a limiting sense. As described previously, one skilled in the art will recognize that various other illustrative applications may use the platinum:ruthenium alloy layer as described herein to take advantage of the beneficial barrier characteristics thereof. Various modifications of the illustrative embodiments, as well as additional to the invention, will be apparent to persons skilled in the art upon reference to this description. It is therefore contemplated that the appended claims will cover any such modifications or embodiments that may fall within the scope of the present invention as defined by the accompanying claims.