Patent Publication Number: US-5256004-A

Title: Method of forming consolidated earth columns by injection and the relevant plant and column

Description:
The invention regards a method by which consolidated earth columns are formed by injection, together with the relevant plant and column; in other words a new procedure for obtaining reinforcing columns in the earth, with reinforcement bars if required, by injecting quantities of cement grout; this application for patent tights also includes the plant to be used with this method and the resulting column. 
     The technique used consists of an earth consolidation method by which cement grout is injected to obtain reinforcement columns; the method devised by the invention provides for an initial drilling stage to produce a hole of a diameter of about 60 to 90 mm and a depth equal to that of the column to be constructed, on average between approximately 10 m and 30 m: during drilling a cleaning jet of water is injected into the hole at low pressure, in the order of about some tenths of bars and a rate of flow between 80 and 100 l/min; the water supply is then shut off towards the bottom of the hole and the injection of grout is then initiated; the grout is distributed by means of a pair of opposing jets, positioned radially around the excavating head, with a flow diameter of between 1 and 3 mm: this head is gradually extracted from the earth at a constant speed and left to rotate in order to form the column, generally between 60 and 120 cm in diameter, below the jet ejection level; the transverse section of the column, substantially circular in the case of even ground, may be uneven, or in any case irregular, if on the other hand, the earth is made up of a number of different compositions; once the column has been formed, the reinforcement can be lowered into the fresh grout, or if this is not possible, because the column of fresh grout is blocked by landslide fragments, for example, the reinforcement is driven into a central hole in the hardened column with a percussion hammer and cement grout is then poured into the hole. 
     The plant used during this method utilizes hollow, rotating drills, with excavation heads fitted to the bottom, provided with either three-cone or three-blade boring points, fed by a water pump unit during the drilling stage and then a grout pump unit during injection, at pressures of about 500 bar and rates of flow of 150 l/min.; the water supply is shut off by means of a blocking device, for example a metal ball, inserted at the top of the drill, that drops by force of gravity through the body of the drill, shutting off the flow of water; the radial, opposing jets of grout are emitted through ejector nozzles with a flow diameter of approximately 1 to 3 mm, positioned around the perimeter of the distributor fitted at the base of the drill; the grout is fed from the top of the drill, by means of a rotating joint-type manifold with radial inlet, positioned at right angles to the drill. 
     Another method whereby micro-piles, of simple design and referred to as &#34;valve-controlled&#34; are formed, consists of the drilling of a hole of a diameter of between 100 and 300 mm, down to the required depth, at the same time attaching a protective jacket to the walls of the hole; a disposable mortar distribution pipe, with lateral inlets at fixed intervals along its surface and protected by coupling valves, is inserted into the hole; mortar is then poured into the circular gap between the pipe and the protective jacket; once the jacket has been removed a blocking device fitted with two plates is inserted inside the distribution pipe, with the plates placed over the inlets in the lower part of the pipe, in order to isolate the section of the pipe where the bottom coupling valve is situated; the injection tube is then fed from the upper plate with cement grout at a pressure of about 10-30 Bar and is continued until the earth is saturated, the coupling valve forces the grout through to the surrounding earth, to form a ring-shaped peripheral layer, separating it from the cylindrical body of the column already cast and situated at the level of the lower coupling valve; once the grout has been completely fed, the blocking device is raised so that it can then isolate a section of the distributor pipe where the coupling valve directly above is situated, thereby allowing another dividing layer to be formed, and so on. 
     The laying of tie-beams, designed to create for example, elements capable of resisting slippage of overlying earth, or lateral elements to support concrete walls, in the case of filling-in operations, is carried out using the following method: a hole is made in the earth with a boring drill of a diameter of about ten centimeters; as the excavating head is lowered, a metal jacket is inserted to support the walls of the hole; once the required depth has been reached, the boring drill is extracted and a metal element resistant to tensile stress and acting as reinforcement of the tie-beam, for example string steel strands or highly resistant metal bars, is inserted in the hole; cement grout or mortar is then poured into the hole, at low pressure, whilst the metal jacket is gradually removed, until the hole has been filled completely; once the grout/mortar has set, the strands or bars can be stressed to give the earth an artificial state of compression stress, to resist landslides or slippages. 
     The method involving the formation of consolidated earth columns with the insertion of a reinforced body, is considerably time-consuming and particularly complex to perform, considering firstly, the need to disassemble the end of the drill once drilling has been completed, in order to extract the blocking device and thereby restore the water supply required to proceed with further drilling, and secondly, the frequency with which the nozzles become blocked, thereby requiring regular cleaning and, often, costly replacement; furthermore, slight deviations in the drilling axis often occur due to the lack of uniformity of the earth composition, thereby leading to consolidation with irregular columns and lower resistance, entirely unsuitable if the columns are to form part of a formation of penetrated or closely-packed elements making up, for example, water-proof barriers or surroundings for wells or plinth bases; also the construction of the column below the nozzle injection level disturbs the underlying ground considerably and may cause blocking wedges, especially when materials with a high friction angle are being consolidated, such as gravel which is highly unstable and subject to vertical slipping, possibly blocking the boring drill and thereby causing expensive damage and considerable time loss; furthermore, the flow of the earth removed during drilling is difficult to control and may accumulate in large amounts at the edge of the hole; finally, if the cement injecting stage is interrupted for prolonged periods, even if the grout continues to be mixed, its grip may be adversely affected. 
     As regards the plant, the rotating joint manifold, situated at the top of the boring drill and fed by a pump unit, whose inlet receiving either water or grout is positioned at right angles to the drill, is subject to transverse stress with respect to the axis of the drill: this stress causes uneven wear on the manifold seals, thereby causing grout to leak into the internal chamber of the manifold and causing the internal rotary section joined to the top of the drill and the external sliding section joined to the pump unit delivery conduits, to jam. 
     As far as the consolidating columns are concerned, the substantially circular shape limits its capacity, particularly in &#34;soft&#34; types of earth. It is true that the uneven shape obtained with earth that is not uniform, increases the vertical sliding friction of the column due to the irregular shapes protruding from the body of the cylinder; nevertheless, firstly this type of protruding formation cannot be controlled and secondly, they are barely capable of resisting cutting pressures exerted on them, consisting solely of water and cement. 
     Furthermore, the insertion of the reinforcement body into the fresh grout is extremely difficult due to the unpredictable nature of the earth when the reinforcement is being laid. 
     As regards the methods involving the formation of micro piles, each drilling appears to be both extremely time-consuming and costly. 
     In addition, as far as the laying of tie-beams is concerned, the metal strand is inserted manually thereby wasting a considerable amount of time and the diameters of the columns are also limited by the corresponding diameters of the preliminary borings. 
     The techniques previously described are open to considerable improvement in order to avoid the problems referred to. It appears that there is a need for the technical problems to be resolved by finding a method of forming injected, earth-consolidating columns which increases efficiency yet at the same time reduces time consumption and thereby increases productivity; such a method should also allow earth-consolidating columns to be constructed without the need for excavation, providing each consolidated column with a metal reinforced core, thereby improving the efficiency of the consolidation and at the same time reducing costs; as far as the plant is concerned, this should be reliable and not require long and costly maintenance and fitting procedures after each drilling; the feeding manifold head should not jam against the boring drill; the column should be highly resistant to sinking, especially when &#34;soft&#34; types of earth are being consolidated. 
     The invention resolves the technical problems described above, using a method whereby injected consolidating earth columns are formed in the manner described below. 
     A) Preparation of consolidating grout, composed either of cement grout or mortar, incorporating aggregates with a granule size within the sand range, or grout or mortar mixed with polymeric, epoxidic or fibrous substances designed to obtain increasing resistance, such as the substances already mentioned, in order to give the grout the following particular characteristics: elasticity, water-tightness, resistance, friction-proof quality, resistance to washing away, more lengthy or delayed grip; the diameter of the particles of these substances should not exceed one third of that of the jet described in stage C to follow; 
     B) Drilling to a penetration depth that avoids excessive piling of the surface layer of earth (outcrop) during the next stage when the grout is injected at high pressure, to an average depth of about a meter, using either a dry-boring method or by injecting the consolidating grout at low pressure and low rate of flow; in the latter case, the grout also acts as a lubricant for the drilling equipment; 
     C) Continual injection of consolidating grout with either a single jet of a wide diameter, up to as much as a few centimeters in the minimum flow section, or a number of jets with a smaller diameter, depending on the granule size of the grout and the effect desired with respect firstly to the clearing of the earth and secondly to cutting; these jets can also be made to incline downward from the axis of the boring drill in order to widen the columns or form truncated cone-shaped projections converging upwards; injecting must be performed with the grout under high pressure, in the order of 500 bar and over, and with rate of flow up to 1000 1/min and over, measured upstream from the boring drill; the consolidating grout is fed more easily to the drill by allowing a downward vortical movement of the mixture at the mouth of the drill; 
     D) Formation of the column by penetration in descent, regulating the translation speed as well as the rotation speed of the boring drill and the rate of flow and pressure of the grout, depending on the composition of the earth and the form required for the column or the tie-beam: for the cylindrical sections, these parameters should be constant, whereas for the truncated cone-shaped sections, the penetration speed should be reduced and/or the pressure or capacity of the grout should be increased; 
     E) Once the penetration depth has been reached and the boring drill has been extracted, either the supply of grout in the case of consolidated earth columns in cement grout, is shut off, or the drill from the control device is disconnected, in the case of columns constructed with reinforcement bars and the drill is left inside the column of fresh consolidating grout as a reinforcement. 
     In the course of this operation, the plant uses the following devices: 
     a rotating joint manifold, situated at the top of the boring drill, consisting of a tubular section which is attached to the drill along a common axis, allowing the consolidating grout to pass from the feed chamber above, which is housed inside the manifold head and supported as it rotates by the tubular section; this head, of hollow construction, is provided with two inlets tangentially arranged with respect to the feed chamber, each at an angle of between approximately 5° and 50° from the plane at right angles to the axis of the drill, in this way allowing the material to descend; the inlets are positioned in such a way as to create a pulsating torque, rotating with the same frequency as that of the pump group and in the opposite direction to that of the rotation of the drill, thereby preventing the head from dragging as a result of the friction created by the boring drill; 
     to form consolidated earth columns with cement grout: a consolidated grout distributor is attached to the base of the boring drill, lined up with it and equipped with a boring tool at its end; the distributor, when used with consolidating grout containing cement grout and in cases where an earth-cutting action is required, it is fitted with five holes to house the ejector nozzles: the lower ejector nozzle fitted in a position parallel with the drill produces the base jet which displaces the earth before it is removed by the boring tool; the transverse ejector nozzles which have a combined action, of forming the column and acting as feed auxiliaries are situated on the lateral surface of the distributor, in the section above the cutting ring, in pairs diametrically opposite each other, with at least one pair of nozzles the axes of which, even though not incident to the axis of the drill, are inclined at an angle of between approximately 15° and 75° from said axis (larger angles produce columns with greater diameters) and at least one pair of ejector nozzles positioned at right angles to the drill so that the grout is projected the maximum distance from the drill; the distributor may also be equipped, in place of the nozzles, with at least one lateral ejection hole with a diameter of between a few millimeters and one centimeter or over, inclined at an angle of between approximately 15° and 90° from the axis of the drill; smaller angles are recommended for earth which is difficult to drill; this hole can also be used in the body of the cutting ring, to provide more effective drilling; 
     to form consolidated earth columns with metal reinforcement: a series of disposable shafts is used, making up the body of the boring drill, connected to each other by short tubes and threaded externally at both ends; the upper shaft is fitted to the bottom of the tube on the rotating joint manifold above, and the lower shaft of the drill is coupled to a base piece, cylindrical in shape and axially disposed at the end of body of the drill, the upper part having a smaller diameter for insertion inside the axial cavity of the drill, thereby restricting the section through which the grout passes; this base piece is fitted, in the straight section next to the grout delivery section, with a converging tube, inclined at about 15° to 90° from the axis of the boring drill, with a diameter ranging between at least a few millimeters and a few centimeters depending on the size of the aggregates being injected, and used to inject the consolidating grout into the earth; a blade or group of blades are attached to the bottom of the base piece, each with a triangular shaped longitudinal section and placed diametrically along the axis of the drill, fitted with oblique cutters converging in the direction of penetration; the outer cylindrical surface of the drill has helical grooves to help the grout grip the drill. 
     The consolidated earth column, obtained by this method, in the versions with or without metal reinforcement, should, to produce maximum resistance and stability, be composed of a central body, substantially cylindrical, with truncated cone-shaped projections converging upwards, protruding along its length at fixed intervals; these projections are obtained by the action of the jets, diverging in the direction of the boring. 
     The advantages of this invention are: drastic reduction in time taken to from consolidation columns and consequently a considerable reduction in costs; the drilling cycle is simplified considerably; greater reliability, also resulting from a reduction in necessary maintenance; greater control of discarded earth that cannot be removed due to the action of the inclined jets; elimination of damaging blows resulting from the formation of the column above the volume of earth operated on by the jets; decrease in errors of verticality as a result firstly of the removal of earth by the inclined or coaxial jets, prior to the subsequent removal by the boring tool, and secondly of the movement of the boring drill itself in liquid/plastic surroundings; reduced likelihood of rotating joint manifold head jamming against drill; possibility of consolidating sunken earth, with or without the need for bearing structures; greater precision when centering reinforcement in column of consolidating grout; more effective clearance of earth resulting in better compaction; drilling cycle greatly simplified; non-cylindrical columns produced with greater resistance. 
     The first version of the distributor referred to, used to form consolidated earth columns, is supplied with the following nozzles: 
     a nozzle axially disposed at the end of the distributor; 
     pair of nozzles inclined at 45° from the body of the drill positioned on the lateral surface of the distributor next to the boring tool, for example 50 cm above it; 
     pair of nozzles, situated on the lateral surface of the distributor, at right angles with the body of the boring drill, arranged at differing heights above the preceding pair of nozzles; 
     flow diameter of each nozzle between 3 and 5 mm. 
     A second version of the distributor provides a single flow inlet, a few centimeters above the cutter on the boring tool, inclined downward at 45° from the body of the drill with a flow diameter of between 6 and 12 mm. 
     In the examples, the minimum average diameter sizes of the column are calculated by taking the minimum values of the working parameters indicated and the diameters of the nozzles; the same applies for the maximum diameters; sizes below, between or above the column diameters can be obtained by varying the working parameter values proportionately and the flow diameters of the nozzles, to give each jet of consolidating grout the energy necessary for the predetermined dimensions of the column to be obtained. 
     EXAMPLE 1 
     Consolidation in cohesive earth (with lime-clay matrix) having the following characteristics: 
     
         ______________________________________
Cu (undrained cohesion) below 6 Kg/cm.sup.2 ;
Spt (standard penetration test) between 2 and 50;
______________________________________
Composition of consolidating grout:
Water               550          Kg/m.sup.3
Cement              550          Kg/m.sup.3
Sand                500          Kg/m.sup.3
______________________________________
Consolidating grout distributor, first version.
______________________________________
Working parameters:
Penetration speed   from 0.003 to 0.02
                                 m/s
Equivalent to insistence
                    1 to 5       min/m
time, defined as
reciprocal to penetration
speedfrom
Drill rotation speed
                    from 10 to 20
                                 RPM
Grout flow rate     from 300 to 1000
                                 ltrs/m
Grout pressure      from 400 to 800
                                 bar
Average diameter of from 60 to 120
                                 cm.
consolidated column
______________________________________
 
    
     EXAMPLE 2 
     Consolidation in cohesive earth (with lime-clay matrix) having the following characteristics: 
     
         ______________________________________
Cu (undrained cohesion) below 6 Kg/cm.sup.2 ;
Spt (standard penetration test) between 2 and 50
______________________________________
Composition of consolidating grout:
Water               550          Kg/m.sup.3
Cement              550          Kg/m.sup.3
Sand                600          Kg/m.sup.3
______________________________________
Consolidating grout distributor, second version.
______________________________________
Working parameters:
Penetration speed   from 0.003 to 0.02
                                 m/s
Equivalent to insistence
                    from 1 to 5  min/m
time, defined as
reciprocal to penetration
speed
Drill rotation speed
                    from 10 to 50
                                 RPM
Grout flow rate     from 300 to 1000
                                 ltrs/m
Grout pressure      from 400 to 800
                                 bar
Average diameter of from 60 to 120
                                 cm.
consolidated column
______________________________________
 
    
     EXAMPLE 3 
     Consolidation in granular earth (sandy) having the following characteristics: 
     
         ______________________________________
C (cohesion coefficient) = 0
ALFA (friction angle) = 35°
______________________________________
Composition of consolidating grout:
Water               730          Kg/m.sup.3
Cement              800          Kg/m.sup.3
______________________________________
Consolidating grout distributor, first version.
______________________________________
Working parameters:
Penetration speed   from 0.003 to 0.02
                                 m/s
Equivalent to insistence
                    from 1 to 5  min/m
time, defined as
reciprocal to penetration
speed
Drill rotation speed
                    from 10 to 20
                                 RPM
Grout flow rate     from 300 to 1000
                                 ltrs/m
Grout pressure      from 400 to 800
                                 bar
Average diameter of from 100 to 140
                                 cm.
consolidated column
______________________________________
 
    
     EXAMPLE 4 
     Consolidation in granular earth (sandy) having the following characteristics: 
     
         ______________________________________
C (cohesion coefficient) = 0
ALFA (friction angle) = 35°
______________________________________
Composition of consolidating grout:
Water               730          Kg/m.sup.3
Cement              800          Kg/m.sup.3
______________________________________
Consolidating grout distributor, second version.
______________________________________
Working parameters:
Penetration speed   from 0.003 to 0.02
                                 m/s
Equivalent to insistence
                    from 1 to 5  min/m
time, defined as
reciprocal to penetration
speed
Drill rotation speed
                    from 10 to 50
                                 RPM
Grout flow rate     from 300 to 1000
                                 ltrs/m
Grout pressure      from 400 to 800
                                 bar
Average diameter of from 100 to 140
                                 cm.
consolidated column
______________________________________
 
    
     A third version of the device referred to, used to obtain reinforced consolidated earth columns, is fitted with a boring and injecting drill with an outer diameter of 90 mm and 10 mm thick, equipped at its end with a base piece with fitted converging tube, inclined downward at 45° from the body of the drill and a minimum flow diameter of between 6 and 12 mm; a triangular boring point is fixed to the base piece, 100 mm in length, 50 mm in height and a few centimeters thick. 
     In the examples, the minimum average diameter sizes of the column are calculated by taking the minimum values of the working parameters indicated and the minimum flow diameter; the same applies for the maximum diameters; sizes below, between or above the column diameters can be obtained by varying the working parameter values proportionately and the flow diameters of the nozzles, to give each jet of consolidating grout the energy necessary for the predetermined dimensions of the column to be obtained. 
     EXAMPLE 5 
     Consolidation in cohesive earth (with lime-clay matrix) having the following characteristics: 
     
         ______________________________________
Cu (undrained cohesion) below 6 Kg/cm.sup.2 ;
Spt (standard penetration test) between 2 and 50
______________________________________
Composition of consolidating grout:
Water               500          Kg/m.sup.3
Cement              500          Kg/m.sup.3
Sand                600          Kg/m.sup.3
______________________________________
Drill boring and injecting consolidating grout
contemporaneously as defined above.
______________________________________
Working parameters:
Penetration speed   from 0.003 to 0.02
                                 m/s
Equivalent to insistence
                    from 1 to 5  min/m
time, defined as
reciprocal to penetration
speed
Drill rotation speed
                    from 10 to 50
                                 RPM
Grout flow rate     from 300 to 1000
                                 ltrs/m
Grout pressure      from 400 to 800
                                 bar
Average diameter of from 60 to 120
                                 cm.
consolidated column
______________________________________
 
    
     EXAMPLE 6 
     Consolidation in granular earth (sandy) having the following characteristics: 
     
         ______________________________________
C (cohesion coefficient) = 0
ALFA (friction angle) = 35°
______________________________________
Composition of consolidating grout:
Water               730          Kg/m.sup.3
Cement              800          Kg/m.sup.3
______________________________________
Drill boring and injecting consolidating grout
contemporaneously as defined above.
______________________________________
Working parameters:
Penetration speed   from 0.003 to 0.02
                                 m/s
Equivalent to insistence
                    from 1 to 5  min/m
time, defined as
reciprocal to penetration
speed
Drill rotation speed
                    from 10 to 50
                                 RPM
Grout flow rate     from 300 to 1000
                                 ltrs/m
Grout pressure      from 400 to 800
                                 bar
Average diameter of from 100 to 140
                                 cm.
consolidated column
______________________________________
 
    
     To obtain columns or column sections with truncated coneshaped projections, maintaining the same working parameters referred to above, the drill penetration speed is reduced in order to increase the quantity of grout injected into the earth per linear meter of penetration; this then increases the diameter of the column, according to the ratio: ##EQU1## where: D=diameter of the column at the points where section is larger by virtue of the projections; 
     Q=quantity of consolidating grout per meter of column, necessary for the projections to be produced; 
     K=numeric coefficient according to: 
     a) quantity of water in excess of that required for hydration of cement; 
     b) discarded earth at mouth of boring; 
     c) state of earth fracturation; 
     the coefficient varies between 0.4, in the case where at least one of the above-mentioned factors a), b), c) has the maximum value, and 0.9 in the case where all the above-mentioned factors a), b), c) have the minimum values contemporaneously. 
    
    
     Some of the ways in which the invention can be used are illustrated, purely by way of examples, in the ten sketches attached, where: 
     FIG. 1 is a schematic view of a boring plant forming columns injected at high pressure according to the method devised by the invention, with a cross section of the underlying earth illustrating the area in which the column is formed; 
     FIG. 2 shows a partial, interrupted longitudinal section of the boring drill, complete with rotating feed manifold, intermediate shaft and grout distributor onto which the five ejector nozzles are fitted; 
     FIG. 3 shows the enlarged cross section III--III, of the rotating joint manifold shown in FIG. 2; 
     FIG. 4 is an interrupted, transparent, longitudinal view of the consolidating grout distributor; 
     FIG. 5 is the transverse section V--V of FIG. 4; 
     FIG. 6 shows the longitudinal section of the distributor where the flow of grout is provided by a single ejector inlet situated near the cutter on the boring tool; 
     FIG. 7 shows the longitudinal section of the distributor, as illustrated in FIG. 6, but with the flow inlet positioned further away from the cutter; 
     FIG. 8 shows the longitudinal section, in schematic form, of a column with truncated cone-shaped projections converging downward, obtained by the method devised by the invention; 
     FIG. 9 shows a view of the boring plant fitted with disposable shafts as devised by the invention, showing also a cross section of the underlying earth in the area where the reinforced consolidated column is formed by means of the disposable boring shaft; 
     FIG. 10 shows the longitudinal section of the boring drill, complete with disposable reinforcement bar; 
     FIG. 11 shows a cross section detail of the end of the boring drill with grout flow conduit inclined at 45° from the body of the drill; 
     FIG. 12 shows a cross section detail of the end of the drill but with the ejection conduit in a right-angled position; 
     FIG. 13 shows an enlarged transverse section XIII--XIII, of the rotating joint manifold illustrated in FIG. 10, similar to that in FIG. 3; 
     FIG. 14 is a view from below of the boring point with two cutters; 
     FIG. 15 shows a view from below, as in FIG. 14, but in this case, the boring point is fitted with three cutters; 
     FIG. 16 shows a longitudinal section of the boring point with the cutters pushed back; 
     FIG. 17 is a view of FIG. 16 from above; 
     FIG. 18 is a longitudinal section of the reinforced injected columns as devised by the invention, acting as tie-beams; 
     FIG. 19 is a longitudinal section of the reinforced column as devised by the invention, in the truncated cone-shaped projection version; 
     FIG. 20 is a prospective view of a vertical wall enclosing excavations with partitions supported by lateral tie-beams. 
    
    
     The indications are as follows: 
     1 is the cement storage container; 2 is an additional silos for lithoid substances, with granule size falling within the sand range; 3 is a water mixer, fed via the pipe 4 with the cement stored in container 1 and any aggregates contained in silos 2: chemical reagents such as clays, ground fibres or others may be added to the sand and cement; 5 is the pumping station, taking consolidating grout from the mixer 3 and then sending it, at high pressure and flow rate, to the rotating joint manifold 6, via a pair of hoses, 7 and 8; 9 is a chuck which slides vertically along the slideway 10, driving the rotary boring drill 11 into the earth: this slideway is fitted at the side to a boring pylon whose height is proportionate to the boring depth required; 13 is the support, usually mobile, for the boring pylon; 14 are the tubular shafts making up the body of the boring drill 11; a distributor, 15 is fitted to the bottom of the drill, providing an outward flow of consolidating grout used to construct the column 16; 17 is the boring tool, fitted below the distributor, and equipped with cutters 18; 19 and 20 (FIG. 2) represent the pair of inlets situated along the perimeter of the rotating head 6, through which the injecting grout enters, the feed chamber 21: these inlets are inclined, converging downward at an angle from the plane at right angles to the axis of the drill of between approximately 5° and 50° and tangentially arranged with respect to the cylindrical internal surface of the feed chamber 21; 22 is a vertical, cylindrical conduit forming part of the boring drill, connected to the feed chamber 21 via an axially disposed tubular section 22a, which is screwed to the top of the drill, with externally varying diameters along its length, forming the rotary element of the manifold 6 and supporting the manifold head as it rotates; 22b is a seal between the head and the tubular section, preventing the consolidating grout from leaking out of the feed chamber 21; 23 and 24 (FIG. 4) are a pair of upper radial ejector nozzles, positioned at right angles to the drill 11, at different heights along its axis; 25 and 26 represent a pair of nozzles, incident to the body of the drill 11, inclined from the vertical plane at an angle A, between approximately 15° and 75°: larger angles produce columns with wider diameters, thereby decreasing the drilling effect; 27 is a vertically-ended nozzle used to remove the virgin earth broken up by the mechanical action of the cutters 18: each nozzle has a threaded tang which is screwed into a nut on the body of the distributor 15; 28 (FIG. 6) is the distributor with a single flow inlet, situated close to the cutters 18 on the boring tool 17; the body of the tool houses a lower chamber 29 in the axially disposed extension of the cylindrical conduit: this chamber extends downward to form an inlet 30 for the grout, inclined from the drill axis at an angle B, appropriately between approximately 15° and 90°, where smaller angles are particularly suited to earth that is hard to drill; 28a (FIG. 7) represents the distributor with single flow inlet, situated behind the cutter 18 on the boring tool 17; this distributor has a flow inlet 30a, on the lateral cylindrical surface of the distributor; 31 (FIG. 8) is a column formed with truncated cone-shaped projections converging downward, separated along their axis by cylindrical sections 33, obtained in accordance with the method devised by the invention, with the use of nozzle supporting devices of either the single inclined nozzle type or the five-nozzle type, blocking the irregularly positioned nozzles on the horizontal axis; Z represents the outcrop; 34 (FIG. 9) are the disposable shafts making up the body of the boring drill 35, whose outer surface has helical grooves to help the grout forming the reinforced column 37, attach itself to the drill; 38 is a joint with threaded ends, screwed onto the shafts 34 and preventing the grout from leaking while under pressure; 39 is the boring tool, fixed to the bottom of the lower shaft, consisting of a base piece 40 (FIG. 10) housing a tube 41, converging to form the ejector nozzle and whose internal surface is hardened to resist wear: this tube is inclined from the axis of the boring drill 35, at an angle C, between approximately 15° and 90°; smaller angles are appropriate for earth that is difficult to drill; a point 42 made up of two triangular cutters is fixed underneath this base piece, with the base of the cutters on the base piece and the sides 43 and 44 (FIG. 14) converging downward; 45 is the vertical cylindrical conduit connected to the chamber 21 in the rotating joint manifold by a through hole 22a, in the body 22b, forming a rotary coupling for the manifold 6 and supporting it as it rotates; 46 (FIG. 15) illustrates a star-shaped point equipped with three cutters 47, 48 and 49, positioned radially 120° from each other; 50 illustrates a conical-shaped point formed by four cutter blades, 51, 52, 53 and 54, generating from opposite sides of the cone at the bottom of the base piece; 56 (FIG. 18) illustrates a formation of three reinforced columns 57, 58 and 59, into which are inserted the reinforcement bars 60, 61 and 62, forming tie-beams or anchorings for the surrounding earth 63 being consolidated; 64 (FIG. 19) illustrates a column formed with truncated cone-shaped projections 65, converging downward, together with reinforcement 66; 67 (FIG. 20) is a partition, normally constructed in reinforced concrete, enclosing the excavation, from which tie-beams 68 protrude towards the virgin earth, made up of columns 69 injected with reinforcement bars 70, as devised by the invention; the partitions 67 can also be made up of high-pressure injected column panels, with embedded reinforcement; 71 is a lateral load partition plate. 
     Taking FIG. 1 to 5, operations are carried out as follows: the grout is prepared inside the mixer 3, this is then sucked into the pump unit 5 and sent, at high pressure and flow rate, to the rotating joint manifold body 6; it then passes through the conduit 22 leading to the distributor 15 and is injected into the ground through transverse nozzles 23 and 24, inclined nozzles 25 and 26 and axially disposed end nozzle 27; injection is started after a preliminary dry boring phase, to a depth that does not cause excessive outcrop. 
     FIGS. 6 and 7 illustrate the injection of the grout into the earth through a flow pipe positioned either in the body of the boring tool (FIG. 6), or in the wall of the distributor (FIG. 7). 
     FIGS. 11, 12 and 13 illustrate the following operations: first either dry boring is carried out or consolidating grout is injected at low pressure and flow rate, serving solely as a lubricant, the drill 34, being thrust downward by the chuck fitted to the slideway 10; once a suitable depth has been reached, bearing in mind the accumulation of outcrop, pumping of the consolidating grout is started at very high pressure and flow rate, through the feed hoses 7 and 8; the grout is injected through the pipe 41, into the ground, while the drill continues to rotate and penetrate; once the required penetration depth has been reached, the supply is shut off and the drill is left in position. In FIG. 20, the columns 68, acting as tie-beams, are injected along a horizontal drilling axis, through holes in the walls 67 enclosing excavations while in progress. 
     In practice, the materials, sizes, executive details, composition of consolidating grout, the nature and type of aggregates and additives used, the number of ejector nozzles can differ from those indicated, provided they are technically equivalent, without going beyond the legal scope of this invention. 
     The outcrop Z or mixed formations at the summit of the columns, including funnelling, can also be removed by the injection of consolidating grout at fairly low pressure towards the extraction travel limit of the drill 14; in any event, outcrop and any infiltrations may be eliminated by removing the earth above the summit of the consolidated columns by bucket.