Patent Publication Number: US-2004048126-A1

Title: Polymer electrolyte fuel cell and production method of separator plate thereof

Description:
BACKGROUND OF THE INVENTION  
       [0001] The present invention relates to a fuel cell comprising a solid polymer electrolyte for use in portable power sources, power sources for electric vehicles, domestic cogeneration systems and the like, and particularly relates to an electrically conductive separator plate thereof.  
       [0002] A fuel cell comprising a solid polymer electrolyte electrochemically reacts a fuel gas containing hydrogen with an oxidant gas containing oxygen, such as air, to simultaneously generate electric power and heat. This fuel cell basically comprises a polymer electrolyte membrane for selectively transporting hydrogen ions, and a pair of electrodes sandwiching the polymer electrolyte membrane therebetween. The electrode comprises a catalyst layer mainly composed of a carbon powder carrying a platinum group metal catalyst and a diffusion layer formed on the outer surface of the catalyst layer and having both gas permeability and electronic conductivity.  
       [0003] In order to prevent the gas to be supplied to the electrode from leaking out or prevent the two kinds of gases from being mixed with each other, gas sealing members or gaskets are arranged on the periphery of the electrodes, with the polymer electrolyte membrane sandwiched therebetween. The sealing members or gaskets are, beforehand, integrally assembled with the electrodes and the polymer electrolyte membrane, and this is called MEA (electrolyte membrane-electrode assembly). Conductive separator plates are arranged on the outer sides of the MEA for mechanically fixing it and for electrically connecting adjacent MEAs with each other in series. In the position of each separator plate, which will be in contact with the MEA, a gas flow channel is formed for supplying a reactive gas to the electrode and for carrying away a generated gas and an excessive gas. Although the gas flow channel may be provided separately from the separator plate, a general manner is to provide grooves in the surface of the separator plate to serve as the gas flow channel.  
       [0004] For the purpose of supplying each gas to the grooves constituting the gas flow channel, through holes are provided in each of the separator plates where the gas flow channel is formed, for forming a gas communicating channel that communicates throughout the cell stack. This hole is referred to as a manifold aperture. Connection of the inlet and the outlet of the gas flow channel with the manifold aperture allows direct supply of each gas from the manifold aperture into the gas flow channel.  
       [0005] Since the fuel cell generates heat during operation, it needs cooling with cooling water or the like to be kept under favorable temperature conditions. Normally, a cooling section for flowing cooling water for every 1 to 3 cells is provided between the separator plates. It is often the case that a cooling water flow channel is provided on the rear surface of the separator plate to serve as the cooling section. A commonly-used cell stack is constituted by alternately stacking these MEAs, separator plates, and cooling sections to assemble a stack of 10 to 200 cells, sandwiching the stack with end plates via current collector plates and insulating plates, and then fixing it from the both ends with cramping bolts.  
       [0006] In such a solid polymer type fuel cell, the separator plate is required to have high conductivity and gas-tightness, and further have high corrosion resistance against an oxidation/reduction reaction of hydrogen/oxygen. For this reason, a conventional separator plate has usually been constituted by a carbon material, such as grassy carbon, and gas flow channels therein have been formed by cutting or grinding.  
       [0007] In recent years, however, there has been an attempt to produce a separator plate obtainable by molding process using a composite material of expanded graphite or graphite and a resin, or the like, in place of the conventionally-used carbon materials.  
       [0008] In the conventional method by cutting of a carbon plate, it has been difficult to reduce material cost for the carbon plate as well as cost for cutting the same. In the method using the above-mentioned composite material of expanded graphite or graphite and a resin, the following problem also lies. That is, in the molding by means of a mold, a raw material for the separator plate, as pressurized, gets into a gap between an upper mold and a lower mold, where the raw material is cooled and solidified. This forms an overflow part. Also in the method of processing the manifold aperture with the use of a processing machine, such as a mold or a drill, after the molding process, searing force between the processing machine and the material may form sag. This overflow part or sag part is usually termed burrs.  
       [0009] With the burrs formed in the part connecting the manifold aperture with the gas flow channel, the cross sectional area of the gas flow channel is narrowed by the burrs, and thereby the gas supply to the gas flow channel is prevented to cause deterioration in cell performance. Further, the burrs formed on the outlet side of the gas flow channel prevents water droplets, formed in the gas flow channel by condensation of water generated due to an electrode reaction, from being discharged out of the gas flow channel, and thereby clogging of the gas flow channel is induced to cause deterioration in cell performance.  
       [0010] For prevention of the above-mentioned deterioration in cell performance caused by the burrs, there is required a burr removal operation by cutting or grinding. However, the cost for this burr removal operation will be high because of the complex shape of the part connecting the manifold aperture with the gas flowing channel.  
       [0011] In view of what was described above, an object of the present invention is to provide a separator plate where a gas flows between a gas flow channel and a manifold aperture without obstruction even when burrs are formed on the periphery of the manifold aperture.  
       [0012] Another object of the present invention is to provide a separator plate where burrs on the periphery of the manifold aperture can be mechanically removed with ease.  
       [0013] The present invention provides a polymer electrolyte fuel cell comprising such a separator plate.  
       BRIEF SUMMARY OF THE INVENTION  
       [0014] A polymer electrolyte fuel cell of the present invention comprises: a plurality of membrane-electrode assemblies which comprise a polymer electrolyte membrane, and an anode and a cathode, sandwiching the polymer electrolyte membrane therebetween; a plurality of conductive separator plates stacked alternately with the membrane-electrode assemblies, the conductive separator plate having an anode-facing surface on one side and a cathode-facing surface on the other side; and a gas supply and discharge means for supplying and discharging a fuel gas to and from the anode and for supplying and discharging an oxidant gas to and from the cathode, wherein the gas supply and discharge means includes: a pair of fuel gas manifold apertures and a pair of oxidant gas manifold apertures, which are provided in the membrane-electrode assemblies and the conductive separator plates in common; a fuel gas flow channel comprising grooves provided so as to connect one of the fuel gas manifold apertures with the other of the fuel gas manifold apertures in the anode-facing surface of the conductive separator plate; and an oxidant gas flow channel comprising grooves provided so as to connect one of the oxidant gas manifold apertures with the other of the oxidant gas manifold apertures in the cathode-facing surface of the conductive separator plate, and a step as deep as or deeper than the gas flow channel is provided on the gas-flow-channel-side periphery of each of the manifold apertures in the conductive separator plate.  
       [0015] It is preferable that the step of the separator plate has a taper so as to be deep on the manifold aperture side.  
       [0016] It is preferable that burrs on the gas-flow-channel-side periphery of the manifold aperture in the conductive separator plate has been removed.  
       [0017] The present invention provides a method for producing a separator plate for a fuel cell comprising: a first step for molding a mixture which contains a graphite powder and a binder to form a plate; and a second step for forming manifold apertures in the plate by machining, wherein the first step is performed such that a gas flow channel comprising grooves, as well as a concave part extended from the position where the manifold aperture will be formed to the end of the gas flow channel, are formed in the plate.  
       [0018] According to the present invention, the gas flow channel is not narrowed by burrs formed on the periphery of the manifold aperture so that influences of the burrs on the flows of a fuel gas and an oxidant gas can be suppressed. Further, the formed burrs can be readily removed. It is therefore possible to reduce cost for processing the separator plate.  
       [0019] While the novel features of the invention are set forth particularly in the appended claims, the invention, both as to organization and content, will be better understood and appreciated, along with other objects and features thereof, from the following detailed description taken in conjunction with the drawings. 
     
    
    
     BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING  
     [0020]FIG. 1 is a front view of the cathode side of a separator plate in one example of the present invention.  
     [0021]FIG. 2 is an expanded sectional view, taken along the line II-II of FIG. 1.  
     [0022]FIG. 3 is an expanded sectional view, taken along the line III-III of FIG. 1.  
     [0023]FIG. 4 is an oblique view of the vicinity of an inlet-side oxidant gas manifold aperture in the above-mentioned separator plate.  
     [0024]FIG. 5 is an expanded sectional view of the above-mentioned separator plate before the manifold aperture is punched out, taken along the line II-II of FIG. 1.  
     [0025]FIG. 6 is a sectional view showing production steps of a separator plate in another example of the present invention.  
     [0026]FIG. 7 is a sectional view showing production steps of a separator plate in still another example of the present invention.  
     [0027]FIG. 8 is a sectional view showing production steps of a separator plate in still another example of the present invention.  
     [0028]FIG. 9 is a sectional view showing production steps of a separator plate in still another example of the present invention.  
     [0029]FIG. 10 is a sectional view showing production steps of a separator plate in still another example of the present invention.  
     [0030]FIG. 11 is a rear view of the separator plate of FIG. 1.  
     [0031]FIG. 12 is an expanded sectional view of a fuel cell stack, taken along the line XII-XII of FIG. 1.  
     [0032]FIG. 13 is an expanded sectional view of a conventional separator plate, taken along a line corresponding to the line II-II of FIG. 1.  
     [0033]FIG. 14 is an expanded sectional view of the conventional separator plate, taken along a line corresponding to the line III-III of FIG. 1. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION  
     [0034] In the following, embodiments of the present invention are described with reference to drawings. The structural drawings used here are intended to facilitate understanding of the present invention, and hence a relative size and positional relationship of each component are not necessarily accurate.  
     [0035] Embodiment 1  
     [0036]FIG. 1 is a front view of the cathode side of a separator plate of the present embodiment. FIG. 2 is an expanded sectional view, taken along the line II-II of FIG. 1, and FIG. 3 is an expanded sectional view, taken along the line III-III of FIG. 1. FIG. 4 is an oblique view of the vicinity of an inlet-side manifold aperture in the separator plate.  
     [0037] This separator plate  10  is formed by molding a kneaded mixture of an artificial graphite powder, fibrous graphite and a thermosetting phenol resin, using a mold, and comprises a pair of oxidant gas manifold apertures  11   a  and  11   b , a pair of fuel gas manifold apertures  12   a  and  12   b,  and a pair of cooling water manifold apertures  13   a  and  13   b.  The separator plate  10  further comprises, on the cathode side, an oxidant gas flow channel  14  for connecting the manifold aperture  11   a  with the manifold aperture  11   b.  As the gas flow channel  14  is formed by grooves in parallel with each other, ribs  15  are formed between those parallel grooves. The separator plate  10  comprises, on the rear surface thereof, a gas flow channel for connecting the fuel gas manifold aperture  12   a  with the fuel gas manifold aperture  12   b,  or a cooling water flow channel for connecting the cooling water manifold aperture  13   a  with the cooling water manifold aperture  13   b.    
     [0038] The separator plate  10  of the present embodiment differs from that of the conventional example in that a step as deep as or a little deeper than the gas flow channel or the cooling water flow channel is provided on the periphery of each of the manifold apertures. Although the manifold aperture  11   a  is described below, the other manifold apertures have the same structures as the manifold aperture  11   a.    
     [0039] A step  16  is formed on the cathode-side periphery of the manifold aperture  11   a.  This step is made as deep as or a little deeper than the inlet side of the gas flow channel  14 . Burrs  17  are formed on the cathode-side periphery of the manifold aperture  11   a.  The burrs are shown only on the cathode-side periphery of the manifold aperture  11   a  in the drawings; burrs formed in the other parts are omitted.  
     [0040] As thus described, in the separator plate of the present embodiment, the step  16  is formed between the oxidant gas manifold aperture  11   a  and the oxidant gas flow channel  14  so that the periphery of the aperture  11   a  is in a position one step lower. On this account, the oxidant gas can be supplied to the gas flow channel  14  with almost no obstruction even when burrs are formed on the periphery of the aperture  11   a.  By formation of a step similar to the step  16  on the periphery of the manifold aperture  11   b,  the gas as well as generated water can be discharged from the gas flow channel  14  to the manifold aperture  11   b  with almost no obstruction.  
     [0041] Further, with the formation of the step  16 , the manifold aperture  11   a  communicates with the gas flow channel  14  through the step. Since there is no equivalent to rib  15  on the step  16 , burrs  17  can readily be removed by grinding with the use of an automatic machine.  
     [0042] The above-mentioned advantages are obvious from comparisons between FIGS. 2 and 3, and FIGS. 13 and 14 showing a conventional example corresponding to FIGS. 2 and 3, respectively. In a separator plate  50  of the conventional example, an oxidant gas manifold aperture  51  directly communicates with an oxidant gas flow channel  54 . The end of each of ribs  55  formed between the grooves of the gas flow channel is thus on the edge of the aperture  51 , leading to formation of burrs  56  continuing to the end faces of the ribs  55  on the periphery of the aperture  51 . As apparent from FIG. 14, the burrs  56  obstruct the supply of the gas from the aperture  51  to the gas flow channel  54  and the discharge of the gas and the generated water from the gas flow channel  54  side to the aperture  51  side.  
     [0043] According to the present invention, such obstruction can be eliminated. The present invention is particularly effective when a plurality of grooves that are mutually in parallel constitute a gas flow channel.  
     [0044]FIG. 5 shows an expanded sectional view of the separator plate of the present embodiment after molding, taken along a line corresponding to the line II-II of FIG. 1.  
     [0045] As shown in FIG. 5, the separator plate of the present embodiment is produced by press molding so as to comprise a concave part  11  slightly larger than a manifold aperture in a part where the manifold aperture is intended to be formed. The manifold aperture will be formed in the part indicated with the dotted lines in FIG. 5.  
     [0046] Herein, when the width of the step  16 , namely a distance “t” between the end face of the rib  15  and the manifold aperture  11   a  is 0.01 mm or longer, the distance “t” can sufficiently exert the effect of eliminating the influence of the formed burrs. The distance “t” is preferably 0.1 mm or longer. Moreover, from the viewpoint of miniaturization of a fuel cell stack, the distance “t” is desirably 2 mm or shorter.  
     [0047] Embodiemtn 2  
     [0048]FIG. 6 shows an expanded sectional view, taken along a line corresponding to the line II-II of FIG. 1, for indicating production steps of a separator plate of the present embodiment. FIG. 6( a ) shows the separator plate after molding and FIG. 6( b ) shows the separator plate after a manifold aperture has been punched out.  
     [0049] The separator plate of the present embodiment is produced by press molding so as to comprise a concave part  20  slightly larger than a manifold aperture in a part where the manifold aperture is intended to be formed, as shown in FIG. 6( a ), and then punching out a hole by means of a mold to form a manifold aperture, as shown in FIG. 6( b ). In the molding, grooves  24  and  25 , V-shaped at cross section, are formed together with the concave part  20  in the position where the manifold aperture is punched out. By punching out a hole in this position by means of a mold, a manifold aperture  21   a  is formed. Burrs  27  and  29  formed in punching out the aperture are also shown in FIG. 6( b ).  
     [0050] In the present embodiment, circulations of the gases and the generated water are easier because a taper for lowering the edge side of the aperture  21   a  is provided on the step  26  which connects the aperture  21   a  with the gas flow channel  14 .  
     [0051] In the present embodiment, since the molded separator plate comprises the grooves  25  in the part where the manifold aperture  21   a  is intended to be formed by punching out by means of a mold, a more excellent processing property can be obtained than that in EMBODIMENT 1.  
     [0052] Embodiment 3  
     [0053]FIG. 7 shows an expanded sectional view, taken along a line corresponding to the line II-II of FIG. 1, for indicating production steps of a separator plate of the present embodiment. FIG. 7( a ) shows the separator plate after molding and FIG. 7( b ) shows the separator plate after a manifold aperture has been punched out.  
     [0054] The separator plate of the present embodiment is produced by press molding so as to comprise concave parts  30  and  32 , which are slightly larger than a manifold aperture, respectively on both surfaces of a part where the manifold aperture is intended to be formed, as shown in FIG. 7( a ), and then punching out a hole by means of a mold to form a manifold aperture  31   a,  as shown in FIG. 7( b ). Burrs  37  and  39  formed in punching out the aperture are also shown in FIG. 7( b ).  
     [0055] Embodiment 4  
     [0056]FIG. 8 shows an expanded sectional view, taken along a line corresponding to the line II-II of FIG. 1, for indicating production steps of a separator plate of the present embodiment. FIG. 8( a ) shows the separator plate after molding and FIG. 8( b ) shows the separator plate after a manifold aperture has been punched out.  
     [0057] The separator plate of the present embodiment is produced by press molding so as to comprise concave parts  40  and  42 , which are slightly larger than a manifold aperture, respectively on both surfaces of a part where the manifold aperture is intended to be formed, as shown in FIG. 8( a ), and then punching out a hole by means of a mold to form a manifold aperture  41   a,  as shown in FIG. 8( b ). Since a taper is provided on the side wall of each of the concave parts  40  and  42  so as to make each of the opening sides of the aperture  41   a  wider, steps  46  and  48  provided with the tapers are formed, respectively, on the peripheries of the aperture  41   a  on both surfaces of the separator plate. Burrs  47  and  49  formed in punching out the aperture  41   a  are also shown in FIG. 8( b ).  
     [0058]FIG. 9 shows an expanded sectional view, taken along a line corresponding to the line II-II of FIG. 1, for indicating production steps of the separator plate in another example of the present embodiment. FIG. 9( a ) shows the separator plate after molding and FIG. 9( b ) shows the separator plate after the manifold aperture has been punched out. In the example shown in FIG. 9, press molding is performed so as to comprise the concave part  40  slightly larger than the manifold aperture on one side, namely on the cathode side, of the part where the manifold aperture is intended to be formed, and then a hole is punched out by means of a mold to form the manifold aperture  41   a.    
     [0059] In the present embodiment, the step  46  provided with the taper is deeper than the gas flow channel  14 . This can make the influence of the formed burrs  47  on the gas flow channel  14  smaller compared with EMBODIMENT 1. Moreover, the provision of the tapers on the steps  46  and  48  allows the molded body to have an improved releasing property from the mold. Further, making the thickness of the part where the manifold aperture is formed thinner enables facilitation of the punching-out process.  
     [0060] Although the inlet-side oxidant gas manifold aperture was described in the above embodiments, the same can be applied to the outlet-side oxidant gas manifold aperture. Further, although the steps  16 ,  26 ,  36 ,  46  and the like were each provided on the whole periphery of each of the manifold apertures, a step may be provided only in a part communicating with a gas flow channel. FIG. 10 shows an expanded sectional view of a separator plate produced in such a manner, taken along a line corresponding to the line II-II of FIG. 1.  
     [0061] Moreover, the same structure as the structure adopted in the above-mentioned oxidant gas manifold aperture can be applied to the fuel gas manifold aperture in terms of the part communicating with the fuel gas flow channel formed on the anode side of the separator plate, or to the cooling water manifold aperture in the part communicating with the cooling water flow channel. It is to be noted that, in FIG. 1, although the same steps as those in the parts of the oxidant gas manifold apertures are provided in the parts of the fuel gas manifold apertures and the cooling water manifold apertures, these parts do not necessarily require the steps.  
     [0062] Embodiment 5  
     [0063] In the present embodiment described is a manifold of a fuel cell stack constituted by stacking membrane-electrode assemblies (MEAs) and separator plates comprising the manifold apertures as thus described.  
     [0064] Herein shown is an example of using a single separator plate which is produced by making the separator plate  10 , comprising an oxidant gas flow channel on one surface thereof as shown in FIG. 1, comprise a fuel gas flow channel on the rear surface thereof, and thus serves as a cathode-side separator plate as well as an anode-side separator plate.  
     [0065]FIG. 11 is a front view of the anode-side of the separator plate  10 . The separator plate  10  comprises, on the anode side, a fuel gas flow channel  4  so as to connect the manifold aperture  12   a  with the manifold aperture  12   b.  Numeral  5  shows ribs for partitioning the flow channel  4 . A step  6  as deep as the gas flow channel  4  is provided on the periphery of the opening of each of the manifold apertures  12   a  and  12   b.    
     [0066]FIG. 12 is a sectional view showing a part of a fuel cell stack formed by alternately stacking the separator plates  10  and MEAs, taken along the line XII-XII of FIG. 1. Numeral  1  shows an MEA comprising a polymer electrolyte membrane, an anode and a cathode sandwiching the polymer electrolyte membrane, and gaskets sandwiching the polymer electrolyte membrane on the periphery of each of the anode and the cathode. In the fuel cell stack, an oxidant gas manifold is constituted by the manifold apertures  11   a  in the separator plates  10  and the manifold apertures in the MEAS. Further, the manifold aperture  11   a  has large-diameter parts and small-diameter parts since it comprises the steps  16  and  8  on the cathode side and the anode side, respectively. Hence the manifold, through which the oxidant gas flows straight, as indicated by the arrow A 1 , is constituted by the small-diameter parts D 1  and the large-diameter parts D 2 . The arrow A 2  indicates the oxidant gas branching from the flow indicated by the arrow A 1  and flowing into the gas flow channel  14  in each cell, and the arrow A 3  indicates the flow of an exhaust gas including a product of the cathode and an excess gas.  
     [0067] In the conventional fuel cell, a manifold, through which the oxidant gas indicated by the arrow A 1  flows, has been constituted by manifold apertures having uniform diameters.  
     [0068] There are two types of flows of the oxidant gas which flows from the inlet of the fuel cell stack into the manifold: the one is a straight flow indicated by the arrow Al and the other is a flow vertical to the flow indicated by the arrow Al, which branches into the gas flow channels  14  provided in the separator plates  10 . When the gas flows at a uniform rate throughout the manifold, a uniform amount of the gas is supplied to each MEA; in practice, however, the gas amount decreases by the amount of the gas flowing into each of the gas flow channels  14  as the gas flows along the manifold, increasingly lowering the gas flow rate. This causes the flow rate on the reaction gas inlet side to be faster and the reaction gas outlet side to be slower when the manifold apertures have uniform equivalent diameters, as has been in the case of the conventional manifold. Such changes in flow rate lead to occurrence of variation in amount of the oxidant gas flowing into the gas flow channel  14  in each cell.  
     [0069] On the other hand, as in FIG. 12, provision of large diameter parts D 2  and small diameter parts D 1  within the manifold allows drastic lowering of the flow rate of the oxidant gas at each of the large diameter parts, thereby narrowing the variation in flow rate at the plural large diameter parts present within the manifold. With provision of a port for communicating with the gas flow channel  14  at each of the large diameter parts  12 , the variation in amount of the gas flowing into the gas flow channel  14  can be reduced. It is therefore possible to provide a stably operatable fuel cell stack.  
     [0070] As thus described, the pressure-loss distribution of the reaction gas flowing in the vicinity of the plural gas flow channels within the manifold can be decreased by adjusting the difference in equivalent diameter between the large diameter part D 2  and the small diameter part D 1  to the extent that the flow rate of the reaction gas can practically be lowered at the large diameter parts D 2 .  
     [0071] Examples of the present invention are described below.  
     EXAMPLE 1  
     [0072] First, a preparation method of an electrode comprising a catalyst layer is described. An acetylene black powder was allowed to carry 25 wt % of platinum particles having a mean particle size of about 30 Å, to give a catalyst of an electrode. The resultant catalyst powder was dispersed in isopropanol, which was then mixed with an ethyl alcohol dispersion of a perfluorocarbon sulfonic acid powder, to give a catalyst paste.  
     [0073] On the other hand, carbon non-woven fabric having outer dimensions of 16 cm×20 cm and a thickness of 360 μm (TGP-H-120, manufactured by Toray Industries, Inc.) was impregnated with an aqueous dispersion of a fluorocarbon resin (NEOFLON ND1, manufactured by DAIKIN INDUSTRIES, LTD.), and then dried and heated at 400° C. for 30 minutes to be imparted with water repellency. The above-mentioned catalyst paste was applied onto one surface of the obtained carbon non-woven fabric by a screen-printing method to form a catalyst layer. At this time, a part of the catalyst layer was embedded in the carbon non-woven fabric. The carbon non-woven fabric with the catalyst layer formed thereon as thus produced was used as an electrode. The electrode contained platinum in an amount of 0.5 mg/cm 2  and perfluorocarbon sulfonic acid in an amount of 1.2 mg/cm 2 .  
     [0074] Subsequently, a pair of electrodes were bonded by hot pressing onto each of the front and rear surfaces of a proton conductive•polymer electrolyte membrane having outer dimensions of 20 cm×32 cm in such a manner that each of the catalyst layers was brought into contact with the electrolyte membrane, to give an electrolyte membrane-electrode assembly (MEA). The proton conductive polymer electrolyte membrane used here was a 50 μm thick thin film of perfluorocarbon sulfonic acid.  
     [0075] Next, a description is given to a conductive separator plate.  
     [0076] First, a mixture of 50 parts by weight of an artificial graphite powder (High purity graphite ACB, manufactured by Nippon Graphite Industries, Ltd) having a mean particle size of about 10 μm, 30 parts by weight of fibrous graphite (Ketjen Black EC600JD, manufactured by LION CORPORATION) having a mean diameter of 50 μm and a mean length of 0.5 mm, and 20 parts by weight of a thermosetting phenol resin (Sumilite Resin PR-51107, manufactured by Sumitomo Bakelite Company, Limited.) was kneaded with the use of an extrusion kneading machine, and the resultant kneaded powder was put into a mold for molding grooves for gas flow channels, grooves for a cooling water flow channel, and aimed manifold apertures, followed by hot pressing. The conditions for hot pressing were a mold temperature of 50° C., pressure of 100 kg/cm 2 , and the time of 10 minutes. The obtained conductive separator plate had outer dimensions of 20 cm×32 cm, a thickness of 1.3 mm, with each of the gas flow channels and the cooling water flow channel therein having a depth of 0.5 mm. The mold used here was made of an alloy tool for a hot mold (SKDB), and processed on conditions that the flow channel had a groove width of 1.5 mm±5 μm, a groove depth of 0.5 mm±5 μm and a pitch of 3 mm±5 μm, and the separator plate had a thickness of 1.3 mm, a flatness of 10 μm, and a surface polish rate of 0.8 S (maximum surface roughness).  
     [0077] After this manner, a separator plate having such a structure as shown in FIG. 1 was produced. Herein, the burrs shown by numeral  17  in FIGS. 2 and 3 were 0.01 to 0.20 mm high. The step  16  formed on the periphery of the manifold aperture had a width of 1.0 mm. Such a separator plate is referred to as a separator plate  1 A. Burrs formed on the periphery of the manifold aperture in the separator plate  1 A were removed using a grinder. The height of the burrs were thereby made 0.01 mm or lower. This separator plate is referred to as a separator plate  1 B.  
     [0078] As a comparative example, a separator plate was produced using the same material and under the same pressing conditions, by means of a mold which makes an obtained separator plate comprise a gas flow channel in the same shape as the above and a manifold aperture whose cross section was shaped as in FIG. 13. As shown by numeral  56  in FIG. 14, burrs formed on the periphery of the manifold aperture  51  were 0.01 to 0.10 mm high. This is referred to as COMPARATIVE EXAMPLE A. Further, burrs formed on the periphery of the manifold aperture in the separator plate produced in the above-mentioned manner were ground. Since the burrs could not be ground with the use of an automatic machine due to the complex shape of the part where the burrs were formed, the grinding was performed by hand with the use of a file. This process made the heights of the burrs 0.01 mm or lower. This is referred to as COMPARATIVE EXAMPLE B.  
     [0079] Next, cooling water manifold apertures, fuel gas manifold apertures and oxidant gas manifold aperture were formed in the hydrogen-ion conductive polymer electrolyte membrane of the MEA above formed. These apertures were of the same sizes and provided in the same positions as those in the separator plate shown in FIG. 1.  
     [0080] The MEA sheet was sandwiched between two of the separator plates of the same kind, as thus produced, to give a unit cell. 100 of such unit cells were stacked, with a cooling section provided for every 2 cells, to produce a cell stack. The cooling section was formed by not inserting a single separator plate having an oxidant gas flow channel on one surface thereof and a fuel gas flow channel on the other surface thereof, but inserting a composite separator plate composed of: a cathode-side separator plate comprising an oxidant gas flow channel on one surface thereof and a cooling water flow channel on the other surface thereof; and an anode-side separator plate comprising a fuel gas flow channel on one surface thereof and a cooling water flow channel on the other surface thereof. This composite separator plate was formed by bonding the cathode-side separator plate to the anode-side separator plate in such a manner that the surface, with the cooling water flow channel formed thereon, of each of the two separator plates were mutually opposed. On each end of this cell stack, a current collector plate made of stainless steel, an insulating plate made of an electrically insulating material and an end plate were stacked, and both end plates were then cramped with cramping rods. The cramping pressure at that time was 15 kgf/cm 2  per the area of the separator plate.  
     [0081] The polymer electrolyte fuel cells of EXAMPLES and COMPARATIVE EXAMPLES as thus fabricated were kept at 80° C., and a hydrogen gas humidified and heated to have a dew point of 75° C. and air humidified and heated to have a dew point of 65° C. were supplied to the anode side and the cathode side, respectively. This resulted in a cell open-circuit voltage of 96 V at the time of no load when no current was output to the outside. The cells were subjected to a continuous power generation test under conditions of fuel utilization rate of 85%, an oxygen utilization rate of 50% and a current density of 0.7 A/cm 2 , to measure variations in output characteristic with time. It was confirmed as a result that the outputs of the cells using separators of EXAMPLES 1A and 1B, and COMPARATIVE EXAMPLES B, respectively, were all kept at about 14 kW (62 V-224 A) over 8000 hours or longer. As for the cell using the separator plate of COMPARATIVE EXAMPLE A, as continuously operated, after the cell output was kept at about 12.8 kW (57 V-224 A) for the first 1 to 3 hours, the cell voltage begun to vary and a flooding phenomenon caused by excessive wetting of the cell was confirmed. After the elapse of 3 to 5 hours, the power generation voltages of at least one cell or more among the 100 cells varied down to 0 V or lower, making it impossible to continue the operation of the cell.  
     EXAMPLE 2  
     [0082] In the present example, a separator plate was produced in the same manner as in EXAMPLE 1 except for a manifold aperture. As shown in FIG. 6( b ), burrs  27  were formed on the cathode-side periphery of the manifold aperture  21   a  formed by punching-out by means of a mold after press molding. The heights of the burrs were 0.01 to 0.20 mm. This separator plate is referred to as a separator plate  2 A. Further, burrs formed on the periphery of the manifold aperture in the separator plate formed in the above-mentioned manner were removed with the use of a grinder. The heights of the burrs were thereby made 0.01 mm or lower. This separator plate is referred to as a separator plate  2 B.  
     [0083] Using these separator plates, polymer electrolyte fuel cells were fabricated in the same manner as in EXAMPLE 1 and operated under the same conditions as EXAMPLE 1. This resulted in a cell open-circuit voltage of 96 V at the time of no load when no current was output to the outside. Further, after the continuous power generation test, it was confirmed that the output of the cells using separators  2 A and  2 B, respectively, were all kept at about 14 kW (62 V-224 A) over 8000 hours or longer. It was also confirmed that the similar cell characteristics could be obtained even when the cross section of the periphery of the manifold aperture became a curved face by grinding the burrs.  
     EXAMPLE 3  
     [0084] In the present example, a separator plate was produced in the same manner as in EXAMPLE 1 except for a manifold aperture. As shown in FIG. 7( b ), burrs  37  were formed on the cathode-side periphery of the manifold aperture  31   a  formed by punching-out by means of a mold after press molding. The heights of the burrs were 0.01 to 0.20 mm. This separator plate is referred to as a separator plate  3 A. Further, burrs formed on the periphery of the manifold aperture in the separator plate formed in the above-mentioned manner were removed with the use of a grinder. The heights of the burrs were thereby made 0.01 mm or lower. This separator plate is referred to as a separator plate  3 B.  
     [0085] Using these separator plates, polymer electrolyte fuel cells were fabricated in the same manner as in EXAMPLE 1 and operated under the same conditions as EXAMPLE 1. This resulted in a cell open-circuit voltage of 96 V at the time of no load when no current was output to the outside. Further, after the continuous power generation test, it was confirmed that the output of the cells using separators  3 A and  3 B, respectively, were all kept at about 14 kW (62 V-224 A) over 8000 hours or longer.  
     EXAMPLE 4  
     [0086] In the present example, a separator plate was produced in the same manner as in EXAMPLE 1 except for a manifold aperture. As shown in FIG. 8( b ), burrs  47  were formed on the cathode-side periphery of the manifold aperture  41   a  formed by punching-out by means of a mold after press molding. The heights of the burrs were 0.01 to 0.20 mm. This separator plate is referred to as a separator plate  4 A. Further, burrs formed on the periphery of the manifold aperture in the separator plate formed in the above-mentioned manner were removed with the use of a grinder. The heights of the burrs were thereby made 0.01 mm or lower. This separator plate is referred to as a separator plate  4 B.  
     [0087] Using these separator plates, polymer electrolyte fuel cells were fabricated in the same manner as in EXAMPLE 1 and operated under the same conditions as EXAMPLE 1. This resulted in a cell open-circuit voltage of 96 V at the time of no load when no current was output to the outside. Further, after the continuous power generation test, it was confirmed that the output of the cells using separators  4 A and  4 B, respectively, were all kept at about 14 kW (62 V-224 A) over 8000 hours or longer.  
     [0088] As specifically described above, according to the present invention, in production of a separator, using a composite material of expanded graphite or graphite and a resin that can be processed by molding lower in cost than cutting or grinding, a removal step of burrs formed in molding is unnecessary or removal of the burrs with the use of an automatic machine is possible, so that a substantial reduction in cost in mass production can be attempted.  
     [0089] Although the present invention has been described in terms of the presently preferred embodiments, it is to be understood that such disclosure is not to be interpreted as limiting. Various alterations and modifications will no doubt become apparent to those skilled in the art to which the present invention pertains, after having read the above disclosure. Accordingly, it is intended that the appended claims be interpreted as covering all alterations and modifications as fall within the true spirit and scope of the invention.