Patent Publication Number: US-2023151120-A1

Title: Cellulose ethers with delayed solubility and having a reduced glyoxal content

Description:
The present invention relates to a process for producing cellulose derivatives reversibly crosslinked with glyoxal and thus having delayed water-solubility. 
     On account of their outstanding properties, such as swelling, gel-forming and dissolution behavior, cellulose ethers are put to diverse use for example as thickeners, adhesives, binding and dispersing agents, humectants, protective colloids, and stabilizers, and also as suspending and emulsifying agents and film formers. 
     These uses require the cellulose ethers to be emulsified, dispersed or dissolved without lumps. The dissolving of a cellulose ether—in dry powder form—in water, however, often leads to surface gelling and lumping. This problem may be resolved by treatment with sufficient amounts of dialdehydes, especially glyoxal. Through the formation of hemiacetals, which is subject to an acidic catalytic mechanism, a reversible crosslinking is produced which, while having no substantial influence on the solubility, improves the dispersibility, delays dissolution in water, and prevents lumps forming. This retarded dissolution can be reduced by increasing the pH (“Cellulose Ethers”, Chapter 2.1, Ullmann&#39;s Encyclopedia of Industrial Chemistry, 2006, Wiley-VCH Verlag GmbH, Weinheim, Germany). 
     WO 2017/064164 A1 discloses a cellulose ether crosslinked temporarily with a glyoxalic acid (C 1 -C 4 )alkyl ester mono (C 1 -C 4 )alkyl acetal. The fraction of the crosslinker is preferably 0.01 to 10 parts by weight per 100 parts by weight of the cellulose ether. EP 2 177 538 A1 relates to a cellulose ether containing alkyl and hydroxyethyl groups which has been mixed with a crosslinker and then subjected to grinding-drying. The crosslinker is preferably a mono- or dialdehyde, more preferably glyoxal. According to US 2019/0062458 A1, a crosslinked, water-insoluble cellulose is used for producing membranes or hydrogels. The crosslinker may be an aldehyde, an organochloride, an ether, a polyfunctional carboxylic acid, glycerol, a urea derivative and/or a glycidyl ether. 
     DE 10 75 773 disclosed the crosslinking of cellulose ether with glyoxal for improved solubility and/or for preventing agglomeration during dissolution. For this crosslinking, the cellulose ether was suspended in acetone and an aqueous glyoxal solution was added. 
     U.S. Pat. No. 3,072,635 describes a process for producing water-dispersible cellulose derivatives by treatment with 0.001 to 0.2 mol of glyoxal per mole of anhydroglucose unit of the cellulose ether, where the glyoxal was dissolved in alcohol and the cellulose ether contained amounts of glyoxal of preferably greater than 1.25 to 5.0% by weight. 
     Part of the disclosure of DE 12 39 672 was the possibility of controlling the degree of crosslinking and hence the retarded dissolution via the amount of glyoxal. This is apparent from the examples given. There, water-soluble methyl cellulose is kneaded homogeneously with 0.001 to 0.2 mol of glyoxal per mole of anhydroglucose unit of the methylcellulose at a pH between 2 to 7, and is dried and comminuted. It is shown that 0.48% by weight of glyoxal in the cellulose derivative at a pH of 2 (established using phosphoric acid) leads only to a 15-minute solvation delay. No figures are given for unbound glyoxal content. Nor is there any portrayal of crosslinking at higher pH values and description of the associated solvation delay. 
     EP 0 597 364 discloses a process in which sodium dihydrogenphosphate is added to the glyoxal solution. 
     EP 1 316 563 A1 relates to a process for producing glyoxal-crosslinked cellulose ethers without addition of acidic catalysts. In this case, the viscosity reduction is diminished with raising of the pH of the cellulose ether. It must be noted that the solvation delay is lowered as a result of the raising of the pH. The delay time of a methylhydroxyethylcellulose MHEC containing 1.7% by weight of glyoxal and having a pH of 6.2 is only 20 min in demineralized water, relative to a delay time of 60 min for a crosslinked MHEC with 2.0% by weight of glyoxal and having a pH of 4.7. 
     Glyoxal is classified according to the CLP Regulation (Regulation (EC) No. 1272/2008) as irritating and also sensitizing and a mutagenic effect on humans is assumed. A product having a free glyoxal content of 0.1% to 1% must be labeled accordingly in agreement with the CLP Regulation. The use of glyoxal-crosslinked cellulose ethers in the personal care sector is likewise possible if the producer of cosmetic products ensures that the end product does not exceed the permitted concentration of 100 ppm of glyoxal (SCCP/0881/05). Because the glyoxal used for the reversible crosslinking is released again when the cellulose ether is dissolved in aqueous medium, it is necessary to minimize not just the unbound but rather the total amount of glyoxal in the end product, on the basis of the classifications in the CLP Regulation. 
     EP 1 452 544 B1 describes a process in which cellulose ethers with reduced unbound glyoxal content are produced by addition of water-soluble borates or aluminum salts to the phosphate-buffered crosslinker solution. Here as well it is apparent that, while the amount of unbound glyoxal can be lowered, there is a reduction in the solvation delay because of the addition of sodium tetraborate and the associated raising of the pH. There are also no evident comments on the storage stability. In addition, however, the glyoxal-reduction effect is low and the additives additionally employed are likewise not unobjectable from a toxicological standpoint. 
     In WO 2012/122153 A1 there is a dry blend composed of standard commercial cellulose ether, crosslinked reversibly with glyoxal, and of a pulverulent, solid, water-soluble polycarboxylic acid, which is partly neutralized. The acid is preferably a partly neutralized poly(meth)acrylic acid, polymaleic acid, citric acid, adipic acid, oxalic acid, malonic acid or glutaric acid. When the crosslinked cellulose ether is stirred into water, the acid lowers the pH, and so the hemiacetal bonds are more slowly broken and formation of lumps is prevented. WO 2014/175903 relates to a method for the lump-free dispersing of a dry cellulose ether formulation into an aqueous solution. The cellulose ether formulation comprises a reversibly crosslinked cellulose ether and a solid, water-soluble acid, preferably citric acid, tartaric acid, oxalic acid, malonic acid or poly(meth)acrylic acid. The formulation is likewise a dry blend composed of a standard commercial crosslinked cellulose ether and of an acid. 
     The present invention aims to reduce the content of bound and unbound glyoxal in a cellulose ether without altering the properties of the cellulose ether, particularly the solvation delay and the viscosity. The intention thereby is to considerably minimize the health risk and to avoid mandatory labeling. 
     Unexpectedly, it has been found that through the addition of acidic organic catalysts, specifically of organic acids which have a basicity of one or more or are aromatic, to the glyoxal solution, buffered with alkali metal salts or alkaline earth metal salts of phosphoric acid, it is possible to boost the efficiency of the glyoxal crosslinking, allowing the amount of glyoxal used to be markedly reduced. The solvation delay for the cellulose ether produced in the invention with reduced glyoxal content is comparable with that for a cellulose ether produced according to the prior art. The anticipated reduction in viscosity through the lowering of the pH of the product did not, surprisingly, occur. 
     A subject of the invention is therefore a process for producing cellulose derivatives reversibly crosslinked with glyoxal and thus having delayed water-solubility, with the steps of: 
     a) providing a water-moist cellulose derivative,
 
b) providing an aqueous solution comprising glyoxal, one and/or more alkaline earth metal salts and/or alkali metal salts of phosphoric acid as buffer substance,
 
c) mixing the aqueous solution from b) with the cellulose derivative from a) at a temperature between 20 to 70° C. to achieve reversible crosslinking of the cellulose derivative,
 
d) drying the reversibly crosslinked cellulose derivative and
 
e) grinding the cellulose derivative,
 
where steps d) and e) may be combined into a grinding-drying operation,
 
where the process is characterized in that the aqueous solution as per b) comprises an organic acid having a basicity of one or more, where the amount of the organic acid having a basicity of one or more is 0.002 to 0.015 mol and the amount of the glyoxal is 0.010 to 0.030 mol, in each case per mole of anhydroglucose units of the cellulose derivative, and the molar ratio of monobasic organic acid to glyoxal is in the range from 1:1 to 1:6, preferably from 1:1 to 1:4, the ratio of dibasic organic acid to glyoxal is in the range from 1:1 to 1:10, preferably from 1:2 to 1:6, and the molar ratio of tribasic organic acid to glyoxal is in the range from 1:2 to 1:12, preferably from 1:3 to 1:8.
 
     Additional subjects of the invention are the reversibly crosslinked cellulose derivative as such produced by the stated process, i.e., cellulose derivatives reversibly crosslinked with glyoxal, which are characterized in that the fraction of the organic acid having a basicity of one or more is 0.002 to 0.015 mol and the amount of the glyoxal is 0.010 to 0.050 mol, in each case per mole of anhydroglucose units of the cellulose derivative, and the molar ratio of organic acid having a basicity of one or more to glyoxal is in the range from 1:2 to 1:12. The reversibly crosslinked cellulose derivatives of the invention contain preferably less than 1000 ppm of free glyoxal. 
     The organic acids are aliphatic, aromatic and/or heterocyclic, preferably C1-C7 carboxylic acids having one to three carboxyl groups, which may also contain functional groups, e.g., hydroxyl groups and/or amino groups. The aromatic and heterocyclic acids may additionally possess nitrogen, oxygen or sulfur as heteroatom. The aliphatic acids may likewise have at least one double bond. Acids used more preferably are those which are employed in the pharmaceutical and/or food sector. For the monocarboxylic acids with a pK a  range of greater than or equal to 2.5 and less than 5, these are acetic acid, lactic acid and salicylic acid, and for the di- or tricarboxylic acids with a pK a1  range from 2.5 to 5 and a pK a2  of less than or equal to 6, these are preferably adipic, tartaric or malic acid. General preference is given to carboxylic acids which are solid under standard conditions. They are also easier to meter. Acetic acid is less preferred owing to the intensive odor and the relatively high volatility. The amount of acid is 0.002 to 0.015 mol, more preferably 0.004 to 0.010 mol, in each case per mole of anhydroglucose units of the cellulose ether. 
     Glyoxal is used preferably in the form of an about 40% by weight aqueous solution. The amount of gloxal is 0.010 to 0.050 mol, more preferably 0.015 to 0.025 mol, in each case per mole of anhydroglucose units of the cellulose ether. 
     Buffers used are the alkali metal salts or alkaline earth metal salts of phosphoric acid, more preferably the alkali metal salts of phosphoric acid, very preferably sodium dihydrogenphosphate monohydrate and disodium hydrogenphosphate. The amount of sodium dihydrogenphosphate and disodium hydrogenphosphate is in each case preferably 0.003 to 0.015 mol, more preferably in each case 0.005 to 0.009 mol, in each case per mole of anhydroglucose units of the cellulose ether. 
     The cellulose derivative employed is preferably a water-moist cellulose ether obtained after hot-water washing, with a moisture content of 30 to 70% by weight. This water-moist cellulose ether is kneaded with a solution, preferably aqueous, consisting of the acid to be used, of the phosphate salts and of glyoxal, and is subsequently dried and ground or subjected to a grinding-drying operation. This solution is utilized to establish pH and to increase the efficiency of the glyoxal crosslinking. As a result, the amount of glyoxal used can be significantly reduced, while solvation delays are obtained that are the same as those for a cellulose ether produced according to the prior art. 
    
    
     EXAMPLES 
     In the tables set out below and in the examples, the percentage fractions are reported in percentages by weight. 
     For verifying the storage stability of the cellulose ethers produced in the invention, the aging of the samples is simulated with an accelerated test in accordance with ASTM D6819. For this test, the air-dry cellulose ethers are transferred into glass vessels having temperature-stable and leakproof closure caps. It should be ensured that the ratio of the mass of the sample to be aged to the volume of the glass vessel is always identical (2.76 g of absolutely dry (bone dry) cellulose ether in 100 ml). The sample is subsequently adjusted to a constant moisture content of 10% by weight and stored at 100° C. for 6 h. 
     The solvation delays reported were measured using a Brabender Viscograph (single-speed 75 rpm, load cell 250 cmg, measuring pot and measuring sensor with pins) in aqueous solution (with mains water, at 20° C.). Solvation time ST is the time in minutes between the addition of the product and the attainment of a viscosity of 100 Brabender Units (BU)=65 mPa·s. Solvation end time SET is the time in minutes after which there is no longer any increase in viscosity. For the individual viscosity stages, the concentration of the measurement solution, the initial mass of substance and the amount of dissolution water are evident from the table below. 
     
       
         
           
               
               
               
               
             
               
                   
               
               
                   
                 Concentration of the 
                 Initial mass 
                   
               
               
                 Viscosity stage 
                 measurement solution 
                 of substance 
                 Dissolution water 
               
               
                 [mPa*s] 
                 [%] 
                 [g] 
                 [g] 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
            
               
                 ≤50 
                 5 
                 21.5 
                 409 
               
               
                   &gt;50/≤150 
                 4 
                 17.2 
                 413 
               
               
                 &gt;150/&lt;600 
                 3 
                 12.9 
                 417 
               
               
                  600-1500 
                 2.5 
                 10.75 
                 419 
               
               
                 2000-4000 
                 2 
                 8.6 
                 421 
               
               
                 &gt;4000-30000 
                 1.5 
                 6.45 
                 424 
               
               
                 &gt;30000 
                 1 
                 4.3 
                 426 
               
               
                   
               
            
           
         
       
     
     The pH of the cellulose ether was determined from a 1% by weight aqueous solution of the absolutely dry cellulose ether by means of a pH meter with combined pH electrode. 
     The viscosity of the cellulose ethers was measured using a Brookfield rotational viscometer (model DVI) and using a No. 5 spindle for the 16 000 mPa·s viscosity stage and a spindle 4 for the 5000 mPa·s viscosity stage, with a rotary speed of 20 rpm, from a 1.9% by weight aqueous solution of the absolutely dry cellulose ether at 20° C. The water used to produce the sample solution had a hardness of 20° dH (German hardness). 
     The quantitative determination of the methoxy (—OCH 3 ), hydroxyethyl (—OC 2 H 4 ), and hydroxypropyl (—OC 3 H 6 ) contents and the calculation of DS (average degree of substitution) and MS (molar degree of substitution) were ascertained according to the Zeisel method familiar to the skilled person, by reaction with hydriodic acid and subsequent GC analysis of the resultant alkyl iodides according to  Z. Anal. Chem.  286 [1997] 161-190. 
     The total glyoxal content was ascertained by colorimetry through the reaction of the dissolved glyoxal with 3-methyl-2-benzothiazolinone hydrazone hydrochloride (MBTH) in an acidic medium. For this reason, 0.1 g of air-dry cellulose ether were dissolved in 100 g of distilled water for 24 h. The dissolution procedure here should not be accelerated by alkalification. 2 ml of the cellulose ether solution were pipetted into the reaction vessel and 5 ml of the reagent solution (consisting of 0.2 g of MBTH, 10 g of demineralized water and 40 g of glacial acetic acid) were added thereto via pipette. The reaction vessels were closed, and the reaction mixtures were briefly mixed by shaking and were left to stand in the dark for 2 h. After a reaction time of 2 h, the absorbance of the sample and of the blank sample was measured at 405 nm in a 1 cm cuvette in the Dr. Lange CADAS 100 photometer. The absorbance of the sample had to be between 0.100 and 2.000. In the case of an absorbance below 0.100, the result is to be reported as &lt;400 ppm of glyoxal. If the absorbance was above 2.000, the CE solution was diluted by serial dilution prior to the reaction. 
     Calculation 
     
       
         
           
             
               
                 
                   ( 
                   
                     
                       E 
                       P 
                     
                     - 
                     
                       E 
                       0 
                     
                   
                   ) 
                 
                 * 
                 4.207 
                 * 
                 100 
                 * 
                 F 
               
               E 
             
             = 
             
               ppm 
               ⁢ 
                   
               of 
               ⁢ 
                   
               glyoxal 
             
           
         
       
     
     E P =Absorbance of sample
 
E 0 =Absorbance of blank sample
 
F=Dilution factor
 
E=Initial mass in g
 
4.207=Slope of the calibration line
 
     To determine the free, i.e., unbound, glyoxal, 0.2 g of the air-dried cellulose ether were admixed with 10 ml of tetrahydrofuran. This THF-cellulose ether suspension was shaken with a shaker machine for 4 h and then filtered via a fluted filter into a test tube. 2 ml of the extract were admixed with 5 ml of MBTH reactant solution (consisting of 0.2 g of MBTH, 10 g of demineralized water and 40 g of glacial acetic acid), left to stand in the dark for 2 h, and subsequently subjected to colorimetric measurement at 405 nm (CADAS 100 photometer from Dr. Lange) (see operations for determining the total glyoxal content). 
     Example 1 
     Water-moist methylhydroxyethylcellulose MHEC (200 g of dry matter) with an average degree of substitution DS(methyl) of 1.55 (the DS denotes the average number of methyl groups per anhydroglucose unit) and a molar degree of substitution MS(hydroxyethyl) of 0.22 (the MS denotes the average number of hydroxyethyl groups per anhydroglucose unit) and with a viscosity of 16 000 mPa·s was placed in an LK5 laboratory kneader from Erweka Apparatebau GmbH, where it was mixed with an aqueous solution of water, citric acid, sodium hydroxide and glyoxal. The target moisture content for the MHEC of 73% was established using ice. When all of the ingredients had been added, the whole was kneaded for 30 min. The moist product was subsequently predried to a hand-dry state in a fluidized-bed dryer and dry-ground using an Alpine mill (model D 100 UPZ) employing a 180 μm sieve. A target final moisture content was less than 5%. 
     
       
         
           
               
               
             
               
                   
                   
               
               
                   
                 Batch No. 
               
               
                   
                 1 
               
               
                   
                 (comparative) 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
            
               
                   
                 Buffer 
                   
               
               
                   
                 NaOH/AGU(MHEC) (mol/mol) 
                 0.015 
               
               
                   
                 Glyoxal/AGU(MHEC) (mol/mol) 
                 0.046 
               
               
                   
                 Acid/AGU(MHEC) (mol/mol) 
                 0.008 
               
               
                   
                 NaH 2 PO 4 *H 2 O/AGU(MHEC) (mol/mol) 
                 0 
               
               
                   
                 Na 2 HPO 4 /AGU(MHEC) (mol/mol) 
                 0 
               
               
                   
                 Acid 
                 Citric acid 
               
               
                   
                 crosslinked MHEC 
               
               
                   
                 pH 
                 5.7 
               
               
                   
                 Viscosity (mPas) 
                 12140 
               
               
                   
                 Total glyoxal (ppm) 
                 13885 
               
               
                   
                 Free glyoxal (ppm) 
                 1279 
               
               
                   
                 ST (min) 
                 29 
               
               
                   
                 SET (min) 
                 43 
               
               
                   
                 aged crosslinked MHEC 
               
               
                   
                 pH 
                 4.8 
               
               
                   
                 Viscosity (mPas) 
                 9580 
               
               
                   
                 ST (min) 
                 42 
               
               
                   
                 SET (min) 
                 57 
               
               
                   
                 Postcrosslinking 
                 45 
               
               
                   
                 [aged ST*100/ST-100] (%) 
               
               
                   
                   
               
            
           
         
       
     
     Example 2 
     Water-moist MHEC (200 g of dry matter) with an average degree of substitution DS (methyl) of 1.55 and a molar degree of substitution MS (hydroxyethyl) of 0.22 and with a viscosity of 16 000 mPa-s was placed in an LK5 laboratory kneader from Erweka Apparatebau GmbH, where it was mixed with an aqueous solution of water, sodium dihydrogenphosphate.H 2 O, disodiumn hydrogenphosphate and glyoxal. The target moisture content for the MHEC of 73% was established using ice. When all of the ingredients had been added, the whole was kneaded for 30 min. The moist product was subsequently predried to a hand-dry state in a fluidized-bed dryer and dry-ground using an Alpine mill (model D 100 UPZ) employing a 180 μm sieve. A final moisture content of less than 5% was achieved. 
     
       
         
           
               
               
            
               
                   
                   
               
               
                   
                 Batch No. 
               
            
           
           
               
               
               
               
            
               
                   
                 1 
                 2-1 
                 2-2 
               
               
                   
                 (comparative) 
                 (comparative) 
                 (comparative) 
               
               
                   
                   
               
            
           
           
               
               
               
               
            
               
                 Buffer 
                   
                   
                   
               
               
                 NaOH/AGU(MHEC) (m ol/mol) 
                 0.015 
                 0 
                 0 
               
               
                 Glyoxal/AGU(MHEC) (mol/mol) 
                 0.046 
                 0.046 
                 0.023 
               
               
                 Acid/AGU(MHEC) (mol/mol) 
                 0.008 
                 0 
                 0 
               
               
                 NaH 2 PO 4 *H 2 O/AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
               
               
                 Na 2 HPO 4 /AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
               
               
                 Acid 
                 Citric acid 
                 — 
                 — 
               
               
                 crosslinked MHEC 
               
               
                 PRODUCT PROPERTIES 
               
               
                 pH 
                 5.7 
                 6.9 
                 7.0 
               
               
                 Viscosity (mPas) 
                 12140 
                 12200 
                 12400 
               
               
                 Total glyoxal (ppm) 
                 13885 
                 15167 
                 6796 
               
               
                 Free glyoxal (ppm) 
                 1279 
                 1700 
                 669 
               
               
                 ST (min) 
                 29 
                 22 
                 14 
               
               
                 SET (min) 
                 43 
                 39 
                 26 
               
               
                 aged crosslinked MHEC 
               
               
                 pH 
                 4.8 
                 4.3 
                 5.0 
               
               
                 Viscosity (mPas) 
                 9580 
                 10980 
                 10140 
               
               
                 ST (min) 
                 42 
                 42 
                 18 
               
               
                 SET (min) 
                 57 
                 71 
                 28 
               
               
                 Postcrosslinking 
                 45 
                 91 
                 29 
               
               
                 [aged ST*100/ST-100] (%) 
               
               
                   
               
            
           
         
       
     
     It becomes apparent that with use of the phosphate buffer (examples 2-1 and 2-2) in comparison to the cellulose ether (example 1), produced according to the prior art, the pH of the cellulose ether is raised and the viscosity prior to aging is identical. After aging of the samples, the viscosity dropped to a similar level. On the basis of the raised pH of the cellulose ether using the phosphate buffer in the glyoxal crosslinking, the solvation delay ST is lower. The postcrosslinking, captured through the simulation of aging, was increased, however, for the cellulose ethers using the phosphate buffer (example 2-1). 
     Example 3 
     Water-moist MHEC (200 g of dry matter) with an average degree of substitution DS (methyl) of 1.55 and a molar degree of substitution MS (hydroxyethyl) of 0.22 and with a viscosity of 16 000 mPa·s was placed in an LK5 laboratory kneader from Erweka Apparatebau GmbH, where it was mixed with an aqueous solution of sodium dihydrogenphosphate.H 2 O, disodium hydrogenphosphate, citric acid, water and glyoxal. The target moisture content for the MHEC of 73% was established using ice. When all of the ingredients had been added, the whole was kneaded for 30 min. The moist product was subsequently predried to a hand-dry state in a fluidized-bed dryer and dry-ground using an Alpine mill (model D 100 UPZ) employing a 180 μm sieve. A final moisture content of less than 5% was achieved. 
     
       
         
           
               
               
            
               
                   
                   
               
               
                   
                 Batch No. 
               
            
           
           
               
               
               
               
               
            
               
                   
                 2-1 
                 2-2 
                   
                   
               
               
                   
                 (comparative) 
                 (comparative) 
                 3-1 
                 3-2 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                 Buffer 
                   
                   
                   
                   
               
               
                 NaOH/AGU(MHEC) (mol/mol) 
                 0 
                 0 
                 0 
                 0 
               
               
                 Glyoxal/AGU(MHEC) (mol/mol) 
                 0.046 
                 0.023 
                 0.046 
                 0.023 
               
               
                 Acid/AGU(MHEC) (mol/mol) 
                 0 
                 0 
                 0.004 
                 0.004 
               
               
                 NaH 2 PO 4 *H 2 O/AGU(MHEC) (mol/mol) 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Na 2 HPO 4 /AGU(MHEC) (mol/mol) 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Acid 
                 — 
                 — 
                 Citric acid 
                 Citric acid 
               
               
                 crosslinked MHEC 
               
               
                 PRODUCT PROPERTIES 
               
               
                 pH 
                 6.9 
                 7.0 
                 5.7 
                 6.0 
               
               
                 Viscosity (mPas) 
                 12200 
                 12400 
                 10980 
                 11900 
               
               
                 Total glyoxal (ppm) 
                 15167 
                 6796 
                 14760 
                 7957 
               
               
                 Free glyoxal (ppm) 
                 1700 
                 669 
                 2166 
                 1028 
               
               
                 ST (min) 
                 22 
                 14 
                 34 
                 37 
               
               
                 SET (min) 
                 39 
                 26 
                 48 
                 51 
               
               
                 aged crosslinked MHEC 
               
               
                 pH 
                 4.3 
                 50 
                 4.3 
                 5.0 
               
               
                 Viscosity (mPas) 
                 10980 
                 10140 
                 8800 
                 7220 
               
               
                 ST (min) 
                 42 
                 18 
                 44 
                 37 
               
               
                 SET (min) 
                 71 
                 28 
                 58 
                 50 
               
               
                 Postcrosslinking 
                 91 
                 29 
                 29 
                 0 
               
               
                 [aged ST*100/ST-100] (%) 
               
               
                   
               
            
           
         
       
     
     Through the addition of citric acid as catalyst for the glyoxal crosslinking to the phosphate buffer, the ST was significantly increased. However, the products were not storage-stable, since the viscosity after aging decreased much more greatly than that of an MHEC without addition of acid in the glyoxal solution. The postcrosslinking after aging had fallen as a result of the addition of citric acid. The glyoxal crosslinking accordingly was more efficient; it was catalyzed by the acid. 
     Example 4 
     Water-moist MHEC (200 g of dry matter) with an average degree of substitution DS (methyl) of 1.55 and a molar degree of substitution MS (hydroxyethyl) of 0.22 and with a viscosity of 16 000 mPa·s was placed in an LK5 laboratory kneader from Erweka Apparatebau GmbH, where it was mixed with an aqueous solution of sodium dihydrogenphosphate.H 2 O, disodium hydrogenphosphate, lactic acid, water and glyoxal. The target moisture content for the MHEC of 73% was established using ice. When all of the ingredients had been added, the whole was kneaded for 30 min. The moist product was subsequently predried to a hand-dry state in a fluidized-bed dryer and dry-ground using an Alpine mill (model D 100 UPZ) employing a 180 μm sieve. A final moisture content of less than 5% was achieved in this way. 
     
       
         
           
               
               
            
               
                   
                   
               
               
                   
                 Batch No. 
               
            
           
           
               
               
               
               
               
            
               
                   
                 1 
                 2-1 
                   
                   
               
               
                   
                 (comparative) 
                 (comparative) 
                 4-1 
                 4-2 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                 Buffer 
                   
                   
                   
                   
               
               
                 NaOH/AGU(MHEC) (mol/mol) 
                 0.015 
                 0 
                 0 
                 0 
               
               
                 Glyoxal/AGU(MHEC) (mol/mol) 
                 0.046 
                 0.046 
                 0.046 
                 0.023 
               
               
                 Acid/AGU(MHEC) (mol/mol) 
                 0.008 
                 0 
                 0.009 
                 0.009 
               
               
                 NaH 2 PO 4 *H 2 O/AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Na 2 HPO 4 /AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Acid 
                 Citric acid 
                 — 
                 Lactic acid 
                 Lactic acid 
               
               
                 crosslinked MHEC 
               
               
                 pH 
                 5.7 
                 6.9 
                 8.5 
                 6.4 
               
               
                 Viscosity (mPas) 
                 12140 
                 12200 
                 11560 
                 11920 
               
               
                 Total glyoxal (ppm) 
                 13885 
                 15167 
                 15529 
                 7373 
               
               
                 Free glyoxal (ppm) 
                 1279 
                 1700 
                 1527 
                 527 
               
               
                 ST (min) 
                 29 
                 22 
                 39 
                 25 
               
               
                 SET (min) 
                 43 
                 39 
                 58 
                 37 
               
               
                 aged crosslinked MHEC 
               
               
                 pH 
                 4.8 
                 4.3 
                 4.2 
                 44 
               
               
                 Viscosity (mPas) 
                 9580 
                 10980 
                 11220 
                 10320 
               
               
                 ST (min) 
                 42 
                 42 
                 50 
                 30 
               
               
                 SET (min) 
                 57 
                 71 
                 72 
                 42 
               
               
                 Postcrosslinking 
                 45 
                 91 
                 28 
                 20 
               
               
                 [aged ST*100/ST-100] (%) 
               
               
                   
               
            
           
         
       
     
     Through the addition of lactic acid as catalyst for the glyoxal crosslinking to the phosphate buffer, the ST was significantly increased. Accordingly, it was possible to reduce the amount of glyoxal used by half. Consequently, the total glyoxal content and the free glyoxal content in the MHEC were also considerably reduced. The product was no longer liable to labeling requirements. The loss in viscosity after aging was small and similar to that when using a pure phosphate buffer. As a result of the addition of lactic acid, the postcrosslinking after aging was lower than in the case of the MHEC without addition of acid in the phosphate buffer. 
     Example 5 
     Water-moist MHEC (200 g of dry matter) with an average degree of substitution DS (methyl) of 1.55 and a molar degree of substitution MS (hydroxyethyl) of 0.22 and with a viscosity of 16 000 mPa·s was placed in an LK5 laboratory kneader from Erweka Apparatebau GmbH, where it was mixed with an aqueous solution of sodium dihydrogenphosphate.H 2 O, disodium hydrogenphosphate, acetic acid, water and glyoxal. The target moisture content for the MHEC of 73% was established using ice. When all of the ingredients had been added, the whole was kneaded for 30 min. The moist product was subsequently predried to a hand-dry state in a fluidized-bed dryer and dry-ground using an Alpine mill (model D 100 UPZ) employing a 180 μm sieve. A final moisture content of less than 5% was achieved. 
     
       
         
           
               
               
            
               
                   
                   
               
               
                   
                 Batch No. 
               
            
           
           
               
               
               
               
               
            
               
                   
                 1 
                 2-1 
                 2-2 
                   
               
               
                   
                 (comparative) 
                 (comparative) 
                 (comparative) 
                 5-1 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                 Buffer 
                   
                   
                   
                   
               
               
                 NaOH/AGU(MHEC) (mol/mol) 
                 0.015 
                 0 
                 0 
                 0 
               
               
                 Glyoxal/AGU(MHEC) (mol/mol) 
                 0.046 
                 0.046 
                 0.023 
                 0.023 
               
               
                 Acid/AGU(MHEC) (mol/mol) 
                 0.008 
                 0 
                 0 
                 0.008 
               
               
                 NaH 2 PO 4 *H 2 O/AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Na 2 HPO 4 /AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Acid 
                 Citric acid 
                 — 
                 — 
                 Acetic acid 
               
               
                 crosslinked MHEC 
               
               
                 pH 
                 5.7 
                 6.9 
                 7.0 
                 6.4 
               
               
                 Viscosity (mPas) 
                 12140 
                 12200 
                 12400 
                 12260 
               
               
                 Total glyoxal (ppm) 
                 13885 
                 15167 
                 8796 
                 7835 
               
               
                 Free glyoxal (ppm) 
                 1279 
                 1700 
                 669 
                 691 
               
               
                 ST (min) 
                 29 
                 22 
                 14 
                 27 
               
               
                 SET (min) 
                 43 
                 39 
                 26 
                 42 
               
               
                 aged crosslinked MHEC 
               
               
                 pH 
                 4.8 
                 4.3 
                 8.0 
                 4.8 
               
               
                 Viscosity (mPas) 
                 9580 
                 10980 
                 10140 
                 11080 
               
               
                 ST (min) 
                 42 
                 42 
                 18 
                 28 
               
               
                 SET (min) 
                 57 
                 71 
                 28 
                 40 
               
               
                 Postcrosslinking 
                 45 
                 91 
                 29 
                 4 
               
               
                 [aged ST*100/ST-100] (%) 
               
               
                   
               
            
           
         
       
     
     As a result of the addition of acetic acid as catalyst for the glyoxal crosslinking to the phosphate buffer, it was possible to retain the ST even with halving of the amount of glyoxal used. Accordingly, the values for total glyoxal and unbound/free glyoxal in the MHEC had fallen significantly as well. The product was no longer liable to labeling requirements. The loss in viscosity after aging was small and similar to that when using a pure phosphate buffer. As a result of the addition of acetic acid, the postcrosslinking after aging was lower than in the case of the MHEC without addition of acid in the phosphate buffer. 
     Example 6 
     Water-moist MHEC (200 g of dry matter) with an average degree of substitution DS (methyl) of 1.55 and a molar degree of substitution MS (hydroxyethyl) of 0.22 and with a viscosity of 16 000 m·Pas was placed in an LK5 laboratory kneader from Erweka Apparatebau GmbH, where it was mixed with an aqueous solution of sodium dihydrogenphosphate.H 2 O, disodium hydrogenphosphate, adipic acid, water and glyoxal. The target moisture content for the MHEC of 73% was established using ice. When all of the ingredients had been added, the whole was kneaded for 30 min. The moist product was subsequently predried to a hand-dry state in a fluidized-bed dryer and dry-ground using an Alpine mill (model D 100 UPZ) employing a 180 μm sieve. A final moisture content of less than 5% was achieved. 
     
       
         
           
               
               
            
               
                   
                   
               
               
                   
                 Batch No. 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                 1 
                 2-1 
                 2-2 
                   
                   
                   
               
               
                   
                 (comparative) 
                 (comparative) 
                 (comparative) 
                 6-1 
                 6-2 
                 6-3 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 Buffer 
                   
                   
                   
                   
                   
                   
               
               
                 NaOH/AGU(MHEC) (mol/mol) 
                 0.015 
                 0 
                 0 
                 0 
                 0 
                 0 
               
               
                 Glyoxal/AGU(MHEC) (mol/mol) 
                 0.04   
                 0.04   
                 0.023 
                 0.04   
                 0.023 
                 0.016 
               
               
                 Acid/AGU(MHEC) (mol/mol) 
                 0.00   
                 0 
                 0 
                 0.008 
                 0.004 
                 0.008 
               
               
                 NaH 2 PO 4 *H 2 O/AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Na 2 HPO 4 /AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Acid 
                 Citric acid 
                 — 
                 — 
                 Adipic acid 
                 Adipic actd 
                 Adipic acid 
               
               
                 crosslinked MHEC 
               
               
                 pH 
                 5.7 
                 6.9 
                 7.0 
                 5.0 
                 5.8 
                 5.0 
               
               
                 Viscosity (mPas) 
                 12140 
                 12200 
                 12400 
                 12200 
                 12280 
                 11820 
               
               
                 Total glyoxal (ppm) 
                 13885 
                 151  7 
                 6796 
                 1  033 
                 7202 
                 7243 
               
               
                 Free glyoxal (ppm) 
                 1279 
                 1700 
                    9 
                 1121 
                    43 
                 &lt;400 
               
               
                 ST (min) 
                 29 
                 22 
                 14 
                 55 
                 37 
                 34 
               
               
                 SET (min) 
                 43 
                 39 
                 26 
                 77 
                 50 
                 52 
               
               
                 aged crosslinked MHEC 
               
               
                 pH 
                 4.8 
                 4.3 
                 5.0 
                 4.1 
                 4.3 
                 4.5 
               
               
                 Viscosity (mPas) 
                 95  0 
                 10980 
                 10140 
                 10880 
                 10220 
                 101  0 
               
               
                 ST (min) 
                 42 
                 42 
                 18 
                 67 
                 37 
                 27 
               
               
                 SET (min) 
                 57 
                 71 
                 28 
                 92 
                 51 
                 40 
               
               
                 Postcrosslinking [aged ST*100/ST − 100] (%) 
                 45 
                    1 
                 29 
                 22 
                 0 
                 0 
               
               
                   
               
               
                     indicates data missing or illegible when filed 
               
            
           
         
       
     
     As a result of the addition of adipic acid as catalyst for the glyoxal crosslinking to the phosphate buffer, the ST was significantly increased. Accordingly, it was possible to reduce the amount of glyoxal used by two thirds. Correspondingly, there were considerable reductions in the total glyoxal and the free glyoxal in the MHEC as well. The loss in viscosity after aging was low and similar to that when using a pure phosphate buffer. The postcrosslinking after aging was marginal or could no longer be found, owing to the addition of adipic acid. The product was therefore not liable to labeling requirements. The ST and the storage stability were the same as those of a cellulose ether produced according to the prior art. 
     Example 7 
     Water-moist MHEC (200 g of dry matter) with an average degree of substitution DS (methyl) of 1.62 and a molar degree of substitution MS (hydroxyethyl) of 0.21 and with a viscosity of 5000 mPa·s was placed in an LK5 laboratory kneader from Erweka Apparatebau GmbH. There the water-moist cellulose ether was mixed either with an aqueous solution of glyoxal, water, citric acid and sodium hydroxide (Batch No. 7-1, as a comparative) or with an aqueous solution of sodium dihydrogenphosphate.H 2 O, disodium hydrogenphosphate, water and glyoxal (Batch No. 7-2, as a comparative) and mixed with the acid indicated in the table (Batch No. 7-3 to 7-6). The target moisture content for the MHEC of 73% was established using ice. When all of the ingredients had been added, the whole was kneaded for 30 min. The moist product was subsequently predried to a hand-dry state in a fluidized-bed dryer and dry-ground using an Alpine mill (model D 100 UPZ) employing a 180 μm sieve. A final moisture content of less than 5% was achieved in this way. 
     
       
         
           
               
               
            
               
                   
                   
               
               
                   
                 Batch No. 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                 7-1 
                 7-2 
                   
                   
                   
                   
               
               
                   
                 (comparative) 
                 (comparative) 
                 7-3 
                 7-4 
                 7-5 
                 7-6 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 Suffer 
                   
                   
                   
                   
                   
                   
               
               
                 NaOH/AGU(MHEC) (mol/mol) 
                 0.015 
                 0 
                 0 
                 0 
                 0 
                 0 
               
               
                 Glyoxal/AGU(MHEC) (mol/mol) 
                 0.046 
                 0.023 
                 0.023 
                 0.023 
                 0.023 
                 0.023 
               
               
                 Acid/AGU(MHEC) (mol/mol) 
                 0.004 
                 0 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
               
               
                 NaH 2 PO 4 *O/AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Na 2 HPO 4 /AGU(MHEC) (mol/mol) 
                 0 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
                 0.008 
               
               
                 Acid 
                 Citric acid 
                 — 
                 Lactic acid 
                 Salicylic acid 
                 Acetic acid 
                 Adipic acid 
               
               
                 crosslinked MHEC 
               
               
                 pH 
                 5.7 
                 7.0 
                 6.2 
                 5.9 
                 6.5 
                 5.1 
               
               
                 Viscosity (mPas) 
                 4830 
                 5010 
                 4960 
                 5050 
                 4530 
                 5030 
               
               
                 Total glyoxal (ppm) 
                 14683 
                 7371 
                 7621 
                 7664 
                 8234 
                 6896 
               
               
                 Free glyoxal (ppm) 
                 1085 
                 596 
                 612 
                 735 
                 320 
                 324 
               
               
                 ST (min) 
                 31 
                 14 
                 27 
                 34 
                 29 
                 38 
               
               
                 SET (min) 
                 48 
                 21 
                 38 
                 49 
                 41 
                 54 
               
               
                 aged crosslinked MHEC 
               
               
                 pH 
                 4.6 
                 4.9 
                 4.2 
                 4.4 
                 4.5 
                 4.4 
               
               
                 Viscosity (mPas) 
                 3970 
                 4400 
                 4170 
                 4130 
                 4390 
                 4690 
               
               
                 ST (min) 
                 46 
                 16 
                 24 
                 31 
                 26 
                 31 
               
               
                 SET (min) 
                 61 
                 24 
                 32 
                 42 
                 34 
                 42 
               
               
                   
               
            
           
         
       
     
     From the table it is apparent that for different initial viscosities of the MHEC as well, it was possible to achieve the positive effects with the new crosslinker/buffer solutions.