Patent Publication Number: US-2012042695-A1

Title: Apparatus for quenching formed glass sheets

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
     This application is a divisional of U.S. application Ser. No. 11/565,717 filed Dec. 1, 2006, the disclosure of which is incorporated in its entirety by reference herein. 
    
    
     TECHNICAL FIELD 
     This invention relates to a method and apparatus for quenching formed glass sheets. 
     BACKGROUND 
     Formed glass sheets are conventionally quenched to enhance their mechanical properties. Such formed glass sheets are conventionally used on vehicle side and back windows as well as in other applications such as architectural applications and food storage and display units, etc. Usually the forming and quenching is performed to provide tempering that provides the glass sheet with surface compression on the order of 100 MegaPascals (14,250 psi), but the quenching can also be utilized to perform heat strengthening wherein the surface compression is less such as on the order of 50 MegaPascals (7,250 psi). 
     Conventional forming and quenching systems successively form and quench the glass sheets in a cyclical manner one after another initially at a forming station and then downstream at a quench station. The formed glass sheets can be formed and delivered from the forming station faster than quenching can be performed in the quench station such that reduction in the cycle time of the system is limited by the time of the quenching. 
     Forced convection is conventionally utilized to perform glass sheet quenching in order to establish a temperature gradient between the glass surfaces and its center, starting from a tempering temperature on the order of about 645° C. and cooling to the ambient. Upon the glass sheet cooling to ambient temperature throughout its extent, the glass surfaces are in a state of compression and the glass center is in a state of tension. The surface compression resists breakage so as to provide mechanical strength to the quenched glass. The extent of the center tension and accompanying surface compression is often measured by the glass break pattern, specifically by counting the number of broken pieces in a number of confined areas, usually by counting each full broken piece as one and each partial piece as one-half and then adding to provide a total. A greater number indicates a greater resistance to breakage. However, the surface stress should not be too great so that the glass breaks into pieces that are too small. 
     In connection with heating of the glass sheets, see U.S. Pat. Nos. 3,806,312 McMaster et al.; 3,947,242 McMaster et al.; 3,994,711 McMaster; 4,404,011 McMaster; and 4,512,460 McMaster. In connection with glass sheet forming, see U.S. Pat. Nos. 4,282,026 McMaster et al.; 4,437,871 McMaster et al.; 4,575,390 McMaster; 4,661,141 Nitschke et al.; 4,662,925 Thimons et al.; 5,004,491 McMaster et al.; 5,330,550 Kuster et al.; 5,472,470 Kormanyos et al.; 5,900,034 Mumford et al.; 5,906,668 Mumford et al.; 5,925,162 Nitschke et al.; 6,032,491 Nitschke et al.; 6,173,587 Mumford et al.; 6,418,754 Nitschke et al.; 6,718,798 Nitschke et al.; and 6,729,160 Nitschke et al.; and see also the U.S. patent application Ser. No. 11/255,531, of Vild et al. filed on Oct. 31, 2005. In connection with glass sheet quenching, see U.S. Pat. Nos. 3,936,291 McMaster; 4,470,838 McMaster et al.; 4,525,193 McMaster et al.; 4,946,491 Barr; 5,385,786 Shetterly et al.; 5,917,107 Ducat et al.; and 6,079,094 Ducat et al. 
     SUMMARY 
     An object of the present invention is to provide improved apparatus for quenching glass sheets. 
     In carrying out the above object, the apparatus for quenching glass sheets in accordance with the invention includes a quench system having a quench including lower and upper quench heads that are operable to supply upward and downward gas flows that can be at conventional quench pressures. A quench ring of the apparatus positions a heated and formed glass sheet between the quench heads for quenching. A control of the apparatus operates the quench to initially supply through the lower and upper quench heads upward and downward gas flows for about 0.5 to 1.3 seconds to quench the formed glass sheet. The control then operates the quench to increase the upward and downward gas flow pressures through the lower and upper quench heads to at least 25% greater than the initial pressures for 0.5 to 4 seconds. The control thereafter operates the quench system to continue to supply upward and downward gas flows to the formed glass sheet with decreased cooling power that is less than the cooling power of the initial pressure quenching to eventually provide a tempered and formed glass sheet upon cooling throughout to ambient temperature. When the initial quenching is at conventional quench pressures, the last mentioned cooling has cooling power that is less than the cooling power of the quench at minimum conventional quench pressures. 
     The quench of the apparatus includes quench heads that are movable between an open position where the formed glass sheet is transferred into and out of the quench and a closed position in which the initial pressure and increased pressure quenching are performed. A quench ring of the apparatus transfers the heated and formed glass sheet into the open quench and supports the formed glass sheet during the initial pressure and increased pressure quenching. The apparatus also includes an aftercooler and in one embodiment the quench ring moves the formed glass sheet from the open quench to the aftercooler for at least part of the decreased cooling power quenching. A transfer device of another embodiment receives the formed glass sheet from the quench ring to provide transfer thereof from the open quench to the aftercooler. 
     The objects, features and advantages of the present invention are readily apparent from the following detailed description of the preferred embodiments when taken in connection with the accompanying drawings. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is a schematic elevational view of one embodiment of apparatus constructed in accordance with the present invention to provide the formed glass sheet quenching. 
         FIG. 2  is a partial schematic view similar to  FIG. 1  to illustrate another embodiment of the apparatus for performing the formed glass sheet quenching. 
         FIG. 3  is a graph that illustrates quenching pressure versus time with intermediate increased quenching and final decreased quenching in accordance with the present invention. 
         FIG. 4  is a graph that illustrates quenching pressure versus time as performed in a conventional manner without the increased intermediate quenching and the final decreased quenching in accordance with the present invention. 
         FIG. 5  is a graph that illustrates in solid line representation the surface tension versus time of a glass sheet quenched in accordance with the present invention and compared to phantom line illustrated conventional quenching. 
     
    
    
     DETAILED DESCRIPTION 
     With reference to  FIG. 1 , a glass sheet forming and quenching system is generally indicated by  10  and includes a partially illustrated furnace  12  for heating glass sheets to a forming and quenching temperature, a bending station  14  that includes bending apparatus  16  for cyclically forming glass sheets one after another and a quench system collectively indicated by  18 . The quench system  18  includes a quench  20  constructed in accordance with the invention to perform a quenching method of the invention as is hereinafter more fully described, and the quench system also includes an exit cooling station  22  having an aftercooler  24  for continuing forced convection cooling of formed glass sheets as described below. A central control  26  includes: control connections  28  and  30  respectively to the furnace  12  and the bending station  14 ; control connections  32  and  34  to the quench  20  and an actuator  36  for a quench ring  38  that moves between the bending station  14 , the quench  20  and the cooling station  22 ; and a control connection  40  that operates the aftercooler  24  of the cooling station  22 . Apparatus  42  of the system  10  includes the quench system  18  which includes the quench  20  for performing quenching in a manner that reduces the time required in the quench in order to reduce the overall cycle time of the system in successively forming and quenching glass sheets for delivery. 
     The furnace  12  and bending station  14  may be constructed in any conventional manner but are preferably constructed in accordance with the disclosure of U.S. Pat. No. 7,958,750 of Vild et al. which is assigned to the assignee of the present invention, and the entire disclosure of which is hereby incorporated by reference. At its downstream end, the bending station  14  includes a door  44  that is opened and closed to permit the quench ring  38  to be moved by the actuator  36  through a connection  46  into the bending station to receive a formed glass sheet G in preparation for cooling of the glass sheet. The quench  20  of the quench system  18  includes lower and upper quench heads  48  and  50  that have the general shape of the glass sheet to be quenched and that are movable between a phantom line partially illustrated open position and the full solid line indicated closed position. During movement of the quench ring  38  from the bending station  14  to the quench  20 , the lower and upper quench heads  48  and  50  of the quench are in the open position and are then closed to commence the quenching. The lower and upper quench heads  48  and  50  respectively then provide upward and downward gas flows  52  and  54  that perform the quenching as is hereinafter more fully described. Thereafter, the quench  20  is moved to its open position and the actuator  36  moves the quench ring  38  to the cooling station  22  into the aftercooler  24  between its lower and upper cooling heads  56  and  58  that supply upward and downward cooling gas flows  60  and  62  but at pressures that provide lesser cooling power than prior quenching in the quench  20  as is more fully described below. The pressure of the upward gas flows  60  is subsequently increased to lift the glass sheet from the quench ring  38  upwardly against a transfer device  64  which is illustrated as a conveyor having a conveying loop  66  extending around wheels  68  at least one of which is rotatively driven to move the lower reach of the conveying loop in the direction shown by arrow  70  so the glass sheet is moved toward the right for further cooling and delivery. After the glass sheet is lifted upwardly from the quench ring  38  in the aftercooler  24 , the actuator  36  moves the quench ring  38  back through the open quench  20  to the bending apparatus  16  of the bending station  14  to receive another formed glass sheet for subsequent movement back toward the right into the quench  20  in preparation for commencing the next cycle. 
     Before completing the description of the manner in which the quenching takes place in the quench system  18 , reference should be had to  FIG. 2  which illustrates another embodiment of the apparatus  42 ′ whose quench  18  also has a quench  20  and cooling station  22  like the previously described embodiment. However, in this embodiment, a transfer device  72  includes an extractor  74  that is moved by an actuator  76  under the control of a connection  78  to the central system control (not shown in this view) so as to provide coordination with the rest of the system. After the lower and upper quench heads  48  and  50  of the quench  20  are moved to their open position as shown by solid lines in  FIG. 2 , the pressures of the upward and downward gas flows  52  and  54  are modified to lift the glass sheet upwardly from the quench ring  38  against the extractor  74  of the transfer device  72 . Actuator  76  then moves the extractor  74  and the glass sheet toward the right to the aftercooler  24  between its lower and upper cooling heads  56  and  58  whose upward and downward gas flows  60  and  62  are then at pressures that initially maintain the glass sheet upwardly against the extractor as additional cooling is provided. The pressures of the upward and downward gas flows  60  and  62  are then modified so that the glass sheet is released downwardly from the extractor  74  onto a lower conveyor  80  on an upper reach of a conveying loop  82  thereof which extends over wheels  84  at least one of which is rotatively driven to move the glass sheet toward the right as shown by arrow  86  for delivery. After the upward lifting of the glass sheet in the quench  20 , the quench ring  38  is moved toward the left by its actuator  36  back to the bending apparatus of the bending station to receive another formed glass sheet in preparation for subsequent movement back to the quench  20  to commence the next cycle. 
     As previously mentioned, forced convection is conventionally utilized to perform glass sheet quenching in order to establish a temperature gradient between the glass surfaces and its center, starting from a tempering temperature of about 645° C. and cooling to the ambient temperature. Actually, while glass at ambient temperature acts much like a solid, it is actually a highly viscous liquid since glass is amorphous without any crystalline structure. The outer glass surfaces upon initial quenching are cooled and temporarily tensioned for about one second or more. This tension results from greater contraction of the glass outer surfaces as they are initially cooled faster than the glass center which is cooled slower and thus contracts less. The glass surface tension subsequently reduces as the thermal gradient between the cooler glass surfaces and the hotter glass center stops increasing and the stresses partially relax due to flow within the glass. After the glass cools down to a temperature referred to as the “strain point”, that is normally approximately 520° C. (964° F.), the glass becomes more viscous and does not move as fast as when it was hotter so relative flow between inner and outer layers is arrested and stress created by thermal contraction differences between layers can no longer be relaxed with time by flow in the glass. The glass center is hotter than the surfaces upon cooling through the strain point temperature. As such, upon the entire glass sheet reaching ambient temperature, the center has cooled through a greater temperature differential and contracted more than the surfaces so the center goes into tension and consequently forces the surfaces into compression. The surface compression as previously mentioned resists breakage so as to provide increased mechanical strength to the quenched glass. 
       FIG. 3  is a graph that illustrates the quench pressures utilized to perform the quenching in accordance with the present invention versus time and is comparable to the prior art graph illustrated in  FIG. 4  which shows that the quenching previously has required a much longer high pressure quench time which increases the cycle time of the entire system. It should be appreciated that the pressures illustrated will vary depending upon the glass thickness, quench construction and compressive surface tension desired such that the specific values shown are for purposes of illustration only. As shown in  FIG. 4 , conventional quenching uses a constant quench pressure versus time of about 25 inches (63.5 cm) of water column for eight seconds or so to perform quenching that provides an acceptable break pattern for 3.8 mm thick glass. As previously mentioned, the break pattern or, more precisely, a count of the number of particles within a specified area of the broken glass surface, is the standard way of determining the extent of the center tension in the glass and the accompanying surface compression. That entire eight seconds or so must be performed within the quench  20  so that when added to the time of the quench ring movements between the bending station and quench station, or between the bending station, quench station and cooling station, will require a cycle time on the order of about 13 seconds or more. The present invention as described below in connection with  FIG. 3  allows a reduction in the time while still providing an equivalent break pattern. 
     A more complete description of glass sheet tempering will be helpful in understanding the present invention and the manner in which it reduces cycle time. As discussed above, the extent of quenching is measured by the resultant break pattern. Typically, quenching is controlled so that the break pattern satisfies recognized standards to assure glass strength and stresses that provide resistance to breakage. One widely recognized standard is the European Standard identified as ECE R43, which specifies that upon breakage square areas with 5 cm. sides located anywhere on the surface of the broken glass shall have a minimum particle count of no less than 40 and a maximum particle count no greater than 400. This particle count is provided by counting each particle fully within the square as one and each particle partially within the square as one half and then adding to sum the total. The tempered and formed glass sheets are normally tested by breaking in more than one location since the location of the nucleus of the breaking can affect the particle count. 
     The extent of quenching power for providing formed glass sheets with acceptable temper levels, i.e. recognized break pattern standards, depends on many factors including glass thickness and temperature upon initial quenching, the number of quench nozzle openings for a given area, the spacing of the nozzle openings with respect to each other, the size of the nozzle openings, the proximity of the nozzle opening outlets to the adjacent glass surface, the angles of incidence of the quench jets upon impinging with the glass surface, the pressure of the nozzle jets, the velocity of the nozzle jet flows, and the time length of the quenching, etc. For any given quench and formed glass sheet being quenched, there is a range of pressures that will provide the required effect to meet recognized break pattern standards. This range will thus have minimum and maximum pressures for meeting the standard, and usually the upward flow pressure will be slightly less than the downward flow pressure so the formed glass sheet being quenched will remain on a quench ring that provides its support at the glass periphery. For purposes of this application, “conventional quench pressure” is any pressure in the range of pressures that when applied in the “conventional” constant pressure method for 10 seconds from a specific quench to a specific formed glass sheet heated to a specific quenching temperature will produce a tempered glass sheet upon eventual cooling throughout which when broken provides a break pattern with maximum and minimum particle counts that meet the European Standard ECE R43. As discussed above, the conventional quench pressures, both upward and downward, will have both minimum pressures and maximum pressures that will provide quenching that will produce tempered and formed glass sheets meeting the applicable standard. 
     The cooling power during quenching is the measure of the heat flow rate per area produced for each degree of temperature difference between the glass and the quenching gases provided by a set of quench factors as described above. When all other factors remain the same, the cooling power increases as the quench pressure increases, and the cooling power decreases as the nozzle to glass spacing increases. 
     More specifically, the cooling power is the convective heat transfer coefficient of the quenching factors governed by the equation: 
       Δ Q/Δt =( h )( A )(Δ T ),
 
     where the rate of the heat flow, ΔQ/Δt, is equal to the heat transfer coefficient, h, times the area over which the heat flow was measured, A, times the temperature difference between the glass and the gas of the quench jets, ΔT. 
     When the heat flow rate is in calories per second, with the area in square centimeters and the temperature difference in degrees Centigrade, the heat transfer coefficient is measured in calories per second per square centimeter per degree Centigrade. 
     As illustrated in  FIG. 1 , the present invention provides quenching of a glass sheet that is immediately increased to a conventional pressure for about 0.5 to 1.3 seconds and as shown in  FIG. 5  maintains the temporary glass sheet surface tension in the range of about 14 to 20 MegaPascals, below which range there is insufficient quenching and above which range glass fracture is more likely during the quenching. Then, before the maximum temporary glass surface tension substantially decreases, such as at location  88  shown in  FIG. 5 , the upward and downwardly gas flow pressures at the quench  20  are increased at least 25% through the associated lower and upper quench heads from the initial pressures. More specifically, as illustrated in  FIG. 3 , the increased pressure quenching is performed for 0.5 seconds to 4 seconds with pressures greater than 50% of the initial pressures and most preferably in the range of 50 to 100% greater than the initial pressures. Thereafter, the upward and downward gas flows to the formed glass sheet are continued at pressures that provide less cooling power than the initial pressures as shown in  FIG. 3 . This decreased cooling is initially provided within the quench  20  and thereafter within the aftercooler  24  of the cooling station  22  as previously described. More specifically, this decreased quenching is performed with upward and downward gas flows that provide a decreased cooling power that is no greater than 75% of the cooling power of the initial pressure quenching, preferably no greater than 60% of the cooling power of the initial pressure quenching, and most preferably about 50% of the cooling power provided by the initial pressure quenching. When initial conventional quench pressures are used, i.e. those that will produce glass with a break pattern having particle counts that will meet European Standard ECE R43 when continued for about 10 seconds, the decreased cooling power quench is less than the cooling power provided by the quench at minimum conventional quench pressures. More specifically the decreased cooling is then no greater than 80%, preferably less than 70% and most preferably about 60% of the cooling power provided by the quench at minimum conventional quench pressures. 
     In an actual practice of the present invention, 3.8 mm thick full sized automobile backlites were processed on an actual production furnace and quench under two conditions, specifically under conventional processing and the three step quenching of the present invention. 
     For the conventional processing, glass temperature at the start of quenching was 643° C., quench pressure was 25 inches of H 2 O and the quench time was 8.0 seconds, as in  FIG. 4 . The break pattern yielded a central particle count of 196 pieces per 5×5 cm square from a break point in the driver&#39;s side lower corner. When this conventional quench time was reduced to 4.5 seconds, the particle count was 39 pieces. 
     For the three step quenching of the present invention, glass temperature at the start of quenching was 643 degrees C., quench pressure started at 25 inches of H 2 O for 0.7 seconds, was then increased to 40 inches of H 2 O for 3.8 seconds and was then decreased to 6 inches of H 2 O for 3.5 seconds, as in  FIG. 3 . The break pattern yielded a central particle count of 227 pieces in a 5×5 cm square from a break point in the driver&#39;s side lower corner. So, the time required to be in the high pressure quench was reduced from 8.0 to 4.5 seconds. 
     Quenching of the glass with the three steps of quenching described above thus prevents excessive initial temporary surface tension and reduces the cycle time of the processing. 
     While preferred modes of the invention have been illustrated and described, it is not intended that these modes illustrate and describe all possible forms of the invention. Rather, the words used in the specification are words of description rather than limitation, and it is understood that various changes may be made without departing from the spirit and scope of the invention.