Patent Publication Number: US-2023159800-A1

Title: Adhesive tape for semiconductor package manufacturing process and method for manufacturing same

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
     This application is a National Stage Patent Application of PCT International Patent Application No. PCT/KR2021/006070 (filed on May 14, 2021) under 35 U.S.C. § 371, which claims priority to Korean Patent Application No. 10-2020-0068064 (filed on Jun. 5, 2020), the teachings of which are incorporated herein in their entireties by reference. 
    
    
     TECHNICAL FIELD 
     The present disclosure relates to an adhesive tape for a semiconductor package manufacturing process and, more particularly, to an adhesive tape for a semiconductor package manufacturing process, the adhesive tape capable of effectively protecting a lower surface of a semiconductor package and a plurality of protrusion electrodes formed the lower surface of the semiconductor package during a process of forming an Electromagnetic Interference (EMI) for the semiconductor package. 
     BACKGROUND ART 
     A pin grid array (PGA) technique or a lead frame technique was widely used as a technique for terminal contact of a semiconductor package to the outside in the related art. However, in recent years, a ball grid array (BGA) technique has been widely used. 
     With the BGA technique, the semiconductor package to the outside makes the terminal contact to the outside using multiple protrusion electrodes, that is, solder balls, formed on a bottom surface of the semiconductor package in a protruding manner. Thus, more signals are possibly made to be transmitted with the BGS technique than with the pin gird array (PGA) technique or the lead frame technique in the related art. 
     Due to its features as mentioned above, the BGA technique has been used for a main type of package for the next-generation high-speed memory, and the use of a chip scale package (CSP) that was limited to a portable information communication device, such as a mobile phone or a digital camera, has been expanded up to the computer or workstation field. 
     There is an increasing need to reduce the size of a terminal in order to increase the portability of the terminal, such as the mobile phone, in the mobile field. Accordingly, in order to reduce the size of the terminal, there is an increasing need to reduce the size of a printed circuit board (PCB) that is a primary component of the terminal. 
     However, the reduction in the size of the PCB decreases a gap between semiconductor elements included in the PCB, and thus an error necessarily occurs due to electromagnetic wave interference between the semiconductor elements. In order to suppress the electromagnetic wave interference between elements, methods of placing a cap for element shielding or technologies for forming metal coating for shielding on an external surface of the element using an Electromagnetic Interference (EMI) sputtering technique have been developed and employed. Among these technologies, a technology for coating a shielding metal by sputtering refers to forming of a metal thin film for shielding an electromagnetic wave on an external surface other than a contact terminal of the semiconductor element. 
     In this regard, Korean Patent Nos. 10-1501735 (Patent Document 1) and 10-1662068 (Patent Document 2) in the related art discloses a method of preventing an effect on a contact terminal during a sputtering process for shielding an electromagnetic wave of a BGA type semiconductor package. 
     Patent Document 1 relates to a method of processing for EMI shielding for a semiconductor package. The method includes a tap attachment step of attaching an edge of a tape on a lower surface of a frame and thus forming the tape on an inner circumference of the frame; a tape cutting step of forming holes in the tape in such a manner as to be spaced a predetermined distance apart; a semiconductor package adhesive-mounting step of arranging an edge of a lower surface of a semiconductor package on an upper surface of the tape and adhesively mounting the semiconductor packages on the upper surface of the tape in such a manner as to be spaced a predetermined distance apart, in order that a bump formed on the lower surface of the semiconductor is inserted into the hole in the tape; and a coating step of performing coating on the semiconductor package adhered to the upper surface of the tape and on the upper surface of the tape, from above the tape. With the method, five surfaces other than the lower surface of the semiconductor package are coated. 
     However, in a case where the technology disclosed in Patent Document 1 is employed, a tape cutting step of forming the holes in the tape in such a manner as to be spaced a predetermined distance apart may incur an excessive cost. Moreover, when the semiconductor package is not correctly arranged in the hole in the tape in the semiconductor package adhesive-mounting step, there occurs a problem in that a thin film is defectively deposited when performing metal coating by sputtering for Electromagnetic Interference (EMI) shielding. 
     
       
     
     DOCUMENTS OF RELATED ART 
     (Patent Document 1) Korean Patent No. 10-1501735 (Registered on Mar. 5, 2015) 
     (Patent Document 2) Korean Patent No. 10-1662068 (Registered on Sep. 27, 2016) 
     DISCLOSURE 
     Technical Problem 
     Accordingly, the present disclosure has been made keeping in mind the above problems occurring in the related art, an object of the present disclosure is to provide an adhesive tape for a semiconductor package manufacturing process, the adhesive tape having excellent adhesion, retention, remove, and stress characteristics and thus capable of effectively protecting a lower surface of a semiconductor package and a plurality of protrusion electrodes formed on the lower surface of the semiconductor package during a process of forming an EMI shielding layer of the semiconductor package including a plurality of protrusion electrodes. 
     Another object of the present disclosure is to provide an adhesive tape for a semiconductor package manufacturing process, the adhesive tape in which a first base film contains a plastic material or a metal material and thus, during a process of forming an EMI shielding layer, stress balance is effectively maintained in a manner that corresponds to a topology of a lower surface of a semiconductor package on which a plurality of protrusion electrodes are formed, and a stress characteristic required of the adhesive tape for a semiconductor package manufacturing process is easily secured. 
     Still another object of the present disclosure is to provide an adhesive tape for a semiconductor package manufacturing process, the adhesive tape in which a first adhesive layer contains an acrylic-based copolymer, and thus has an excellent heat resistance at a high temperature, thereby reducing a degassing phenomenon and suitably supporting deformation of a second base film, in which, as a result, the second base film is prevented from being torn, and, at the same time, although the second base film is torn, the first adhesive layer securely surrounds the torn second base film, thereby effectively protecting a plurality of protrusion electrodes, and in which, consequently, the first adhesive layer has a stronger adhesive force than the second adhesive layer, and after a process of forming an EMI shielding layer is finished, the first adhesive layer is separated from the second adhesive layer when the adhesive tape is separated from a semiconductor package. 
     Still another object of the present disclosure is to provide an adhesive tape for a semiconductor package manufacturing process, the adhesive tape in which a second base film contains a metal material, and thus, an air bubble that may occur in a first adhesive layer is prevented from being transferred to a second adhesive layer, and in which, when the adhesive tape is attached on a lower surface of a semiconductor package, due to a sufficient retention characteristic, the second base film, after deformed in a manner that corresponds to a topology of the lower surface of the semiconductor package, is capable of being kept deformed during each process. 
     Still another object of the present disclosure is to provide an adhesive tape for a semiconductor package manufacturing process, the adhesive tape in which a second adhesive layer contains silicon having a spiral network structure, and thus, respective regions of a lower surface of a semiconductor package and a protrusion electrode that are brought into contact with each other have a sufficient adhesion characteristic, and in which, although an air gap occurs, the air gap is prevented from being excessively expanded during each process in a vacuum state. 
     Technical Solution 
     According to an aspect of the present disclosure, an adhesive tape for a semiconductor package manufacturing process, the adhesive tape being attached on a lower surface of a semiconductor package on which a plurality of protrusion electrodes are formed, the adhesive tape includes: a first base film; a first adhesive layer containing an acrylic-based copolymer, the first adhesive layer being stacked on top of the first base film; a second base film containing a metal material in such a manner as to be deformed and then kept deformed during each process in a manner that corresponds to a topology of the lower surface of the semiconductor package, the second base film being stacked on top of the first adhesive layer; and a second adhesive layer containing silicon having a spiral network structure, the second adhesive layer being on top of the second base film. 
     In the adhesive tape, the first base film may contain a plastic material or a metal material. 
     In the adhesive tape, the first base film may be a single layer that is formed of one of polyethylene terephthalate, polyimide, and polyolefin or may have a multi-layer structure in which two or more layers, formed of two or more, respectively, of polyethylene terephthalate, polyimide, and polyolefin, are stacked on top of each other, the first base film having a thickness of 10 μm to 150 μm. 
     In the adhesive tape, the first base film may contain at least 99 wt % or more of aluminum (Al) and may have a tensile strength of 4.8 kgf/mm 2  to 14.4 kgf/mm 2 , an elongation of 6.4% to 19.2%, and a thickness of 20 μm to 80 μm, or the first base film may contain at least 99 wt % or more of copper (Cu) and may have a tensile strength of 8 kgf/mm 2  to 31.2 kgf/mm 2 , an elongation of 3.2% to 14.4%, and a thickness of 20 μm to 80 μm. 
     In the adhesive tape, the first adhesive layer may contain at least one of a butyl acrylate-butyl methacrylate-methacrylic acid-methyl methacrylate-styrene copolymer, and an acrylic acid-2-ethylhexyl acrylate-2-ethylhexyl methacrylate-glycidyl methacrylate copolymer. 
     In the adhesive tape, the first adhesive layer may be formed by mixing at least one of 25 to 30 parts by weight of a first adhesive composition containing butyl acrylate-butyl methacrylate-methacrylic acid-methyl methacrylate-styrene copolymer, and 70 to 75 parts by weight of ethyl acetate and 25 to 30 parts by weight of a second adhesive composition containing acrylic acid-2-ethylhexyl acrylate-2-ethylhexyl methacrylate-glycidyl methacrylate copolymer, 50 to 55 parts by weight of toluene, and 15 to 20 parts by weight of ethyl acetate, and an epoxy-based hardener, applying the resulting mixture to the first base film, and then drying and hardening the resulting mixture. 
     In the adhesive tape, the first adhesive layer may be formed by mixing 80 to 120 parts by weight of the first adhesive composition and 0.5 to 1.5 parts by weight of the epoxy-based hardener, applying the resulting mixture to the first base film, and then drying and hardening the first base film. 
     In the adhesive tape, the first adhesive layer may be formed by mixing 40 to 60 parts by weight of the first adhesive composition, 40 to 60 parts by weight of the second adhesive composition, and 0.5 to 1.5 parts by weight of the epoxy-based hardener, applying the resulting mixture to the first base film, and drying and hardening the first base film. 
     In the adhesive tape, the first adhesive layer may have a thickness of 100 μm to 700 μm and an adhesive force of at least more than 500 gf/25 mm, and the second adhesive layer may have a thickness of 10 μm to 50 μm and an adhesive force of 50 gf/25 mm to 500 gf/25 mm. 
     In the adhesive tape, the more increased a size of the protrusion electrode, the more decreased the thickness of the first adhesive layer may be in a preset thickness range, and the more increased a gap between the protrusion electrodes, the more increased the thickness of the first adhesive layer may be in the preset thickness range, and the more increased the size of the protrusion electrode, the more increased the thickness of the second adhesive layer may be in a preset thickness range, and the more increased the gap between the protrusion electrodes, the more decreased the thickness of the second adhesive layer may be in the preset thickness range. 
     In the adhesive tape, the second base film may have a thickness of 1 μm to 10 μm. 
     In the adhesive tape, the second base film may contain at least 99 wt % or more of aluminum (Al) and may have a tensile strength of 4.8 kgf/mm 2  to 14.4 kgf/mm 2 , an elongation of 6.4% to 19.2%, and a thickness of 10 μm to 35 μm, or the second base film may contain at least 99 wt % or more of copper (Cu) and may have a tensile strength of 8 kgf/mm 2  to 31.2 kgf/mm 2 , an elongation of 3.2% to 14.4%, and a thickness of 10 μm to 35 μm. 
     In the adhesive tape, the second adhesive layer may contain a trimethylated silica-dimethyl siloxane copolymer. 
     According to another aspect of the present disclosure, there is provided a method of manufacturing an adhesive tape for a semiconductor package manufacturing process, the method including: a first tape preparing step of manufacturing a first tape by sequentially stacking a first base film containing a plastic material or a metal material, a first adhesive layer containing an acrylic-based copolymer, and a first release film containing fluorine on top of each other, and manufacturing a second tape by sequentially stacking a second base film containing a metal material, a second adhesive layer containing silicon having a spiral network structure, and a second release film containing fluorine on top of each other; and a first tape lamination step of removing the first release film from the first tape, bringing the first adhesive layer and the second base film into surface contact with each other, and thus laminating the first tape and the second tape on each other. 
     According to still another aspect of the present disclosure, there is provided a method of manufacturing an adhesive tape for a semiconductor package manufacturing process, the method including: a second tape preparation step of manufacturing a first tape by sequentially stacking a first base film containing a plastic material or a metal material, a first adhesive layer containing an acrylic-based copolymer, and a first release film containing fluorine on top of each other, manufacturing a third tape by depositing the second base film on a third release film using a metal deposition technique, and manufacturing a fourth tape by sequentially stacking a second adhesive layer containing silicon having a spiral network structure and a second release film containing fluorine on top of each other; and a second tape lamination step of removing the first release film from the first tape, then bringing the first adhesive layer and the second base film of the third tape into surface contact with each other, and laminating the first tape and the third tape on each other, and of removing the third release film from the third tape, then bringing a second base film and the second adhesive layer of the fourth tape into surface contact with each other, and laminating the third tape and the fourth tape on each other. 
     Advantageous Effects 
     As described above, an adhesive tape for a semiconductor package manufacturing process according to the present disclosure has excellent adhesion, retention, remove, and stress characteristics. Thus, a lower surface of a semiconductor package and a plurality of protrusion electrodes formed on the lower surface of the semiconductor package are effectively protected during a process of forming an EMI shielding layer of a semiconductor package including a plurality of protrusion electrodes. 
     In addition, in the adhesive tape for a semiconductor package manufacturing process according to the present disclosure, the first base film contains a plastic material or a metal material. Thus, during the process of forming the EMI shielding layer, stress balance is effectively maintained in a manner that corresponds to a topology of the lower surface of the semiconductor package on which the plurality of protrusion electrodes are formed. Moreover, the stress characteristic required of the adhesive tape for a semiconductor package manufacturing process is easily secured. 
     In addition, in the adhesive tape for a semiconductor package manufacturing process according to the present disclosure, the first adhesive layer contains an acrylic-based copolymer and thus has an excellent heat resistance at a high temperature, thereby reducing a degassing phenomenon and suitably supporting deformation of a second base film. As a result, the second base film is prevented from being torn, and, at the same time, although the second base film is torn, the first adhesive layer securely surrounds the torn second base film, thereby effectively protecting the plurality of protrusion electrodes. Consequently, the first adhesive layer has a stronger adhesive force than the second adhesive layer, and after a process of forming an EMI shielding layer is finished, the first adhesive layer is separated from the second adhesive layer when the adhesive tape is separated from the semiconductor package. 
     In addition, in the adhesive tape for a semiconductor package manufacturing process according to the present disclosure, the second base film contains a metal material. Thus, an air bubble that may occur in the first adhesive layer is prevented from being transferred to the second adhesive layer. When the adhesive tape is attached on the lower surface of the semiconductor package, due to a sufficient retention characteristic, the second base film, after deformed in a manner that corresponds to the topology of the lower surface of the semiconductor package, is capable of being kept deformed during each process. 
     In addition, in the adhesive tape for a semiconductor package manufacturing process according to the present disclosure, the second adhesive layer contains silicon having a spiral network structure. Thus, respective regions of the lower surface of the semiconductor package and the protrusion electrode that are brought into contact with each other have a sufficient adhesion characteristic, and, although the air gap occurs, the air gap is prevented from being excessively expanded during each process in a vacuum state. 
    
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
         FIG.  1    is a view illustrating a shape of a cross section of an adhesive tape for a semiconductor package manufacturing process according to an embodiment of the present disclosure. 
         FIG.  2    is a view illustrating the shape of the cross section of the adhesive tape for the semiconductor package illustrated in  FIG.  1   , the cross section being adhered to a lower surface of a semiconductor package after a second release film is removed from the adhesive tape. 
         FIG.  3    is a flowchart that is referred to for description of a method of manufacturing the adhesive tape for a semiconductor package manufacturing process according to an embodiment of the present disclosure. 
         FIG.  4    is a view that is referred to for description of a method of manufacturing the adhesive tape for a semiconductor package manufacturing process according to a first embodiment of the present disclosure. 
         FIG.  5    is a view that is referred to for description of a method of manufacturing the adhesive tape for a semiconductor package manufacturing process according to a second embodiment of the present disclosure. 
     
    
    
     
       
     
     DESCRIPTION OF THE REFERENCE NUMERALS IN THE DRAWINGS 
       10 : Semiconductor Package 
       11 : Protrusion Electrode 
       100 : Adhesive Tape for a Semiconductor Package Manufacturing Process 
       110 : First Tape 
       111 : First Base Film 
       112 : First Adhesive Layer 
       113 : First Release Film 
       120 : Second Tape 
       121 : Second Base Film 
       122 : Second Adhesive Layer 
       123 : Second Release Film 
       130 : Third Tape 
       131 : Third Release Film 
       140 : Fourth Tape 
     BEST MODE 
     For the difference over the related art, the definiteness of the specification, and the convenience of understanding the technology, constituent elements according to the present disclosure may be illustrated in an exaggerated manner in the accompanying drawings. In addition, terms defined by considering the meanings thereof in the present disclosure will be used below and may vary according to the user&#39;s or manager&#39;s intention or to practices in the art. Therefore, the definitions of these terms should be defined on the basis of the technical content of the specification as a whole. Constituent elements according to embodiments of the present disclosure are only exemplary examples of the constituent elements recited in the claims, and therefore the embodiments thereof do not impose any limitation on the scope of the present disclosure. The scope of the present disclosure should be interpreted on the basis of the technical idea of the present disclosure in the specification as a whole. 
     
       
     
       FIG.  1    is a view illustrating a shape of a cross section of an adhesive tape for a semiconductor package manufacturing process according to an embodiment of the present disclosure.  FIG.  2    is a view illustrating the shape of the cross section of the adhesive tape for a semiconductor package illustrated in  FIG.  1   , the cross section being adhered to a lower surface of a semiconductor package after a second release film is removed from the adhesive tape.  FIG.  3    is a flowchart that is referred to for description of a method of manufacturing the adhesive tape for a semiconductor package manufacturing process according to an embodiment of the present disclosure.  FIG.  4    is a view that is referred to for description of a method of manufacturing the adhesive tape for a semiconductor package manufacturing process according to a first embodiment of the present disclosure.  FIG.  5    is a view that is referred to for description of a method of manufacturing the adhesive tape for a semiconductor package manufacturing process according to a second embodiment of the present disclosure. 
     
       
     
     Before the embodiments of the present disclosure are described in detail, it should be noted that, normally, the adhesive tape for a semiconductor package manufacturing process that is used during a process of forming an EMI shielding layer needs to ensure an adhesion characteristic, a retention characteristics, a remove characteristic, and a stress characteristic. 
     First, in terms of the adhesion characteristic, a base film and an adhesive layer of the adhesive tape are required to be possibly adhered to each other and brought into close contact therewith in a manner that corresponds to a protrusion electrode and a topology of the lower surface of the semiconductor package including the protrusion electrode, regardless of a size (for example, a diameter or a height) of the protrusion electrode, in order that an air gap does not occur in a region where the lower surface of the semiconductor package and the protrusion electrode are brought into contact with each other. Furthermore, the adhesive tape is required to be kept well adhered without pushing the protrusion electrode in a process environment for forming the EMI shielding layer, for example, in a high-temperature and high-vacuum environment. That is, the adhesive tape is also required to continuously maintain its ability for adhesion and close contact during the process of forming the EMI shielding layer. 
     Next, in terms of the retention characteristic, the adhesive tape is required to maintain its original shape without its denaturation, deformation, discoloration, and outgassing under the condition for the process of forming the EMI shielding layer and at the same time to maintain its ability for adhesion and close contact in such a manner as to prevent gas or a particle from penetrating between the adhesive tape and a contact surface of the semiconductor package during each process. Furthermore, in a case where the air gap occurs in the region where the lower surface of the semiconductor package and the protrusion electrode are brought into contact with each other during the process of forming the EMI shielding layer, the adhesive tape is required to prevent the air gap form excessively expanding during each process (particularly, when performing a process in a high-pressure environment. 
     Next, in terms of the remove characteristic, when removed from the semiconductor package at room temperature or at an atmospheric pressure after undergoing the process of forming the EMI shielding layer, the magnetic tape is required to be easily removed with less force. At the same time, an adhesive material is required not to remain on the lower surface of the semiconductor package and a surface of the protrusion electrode. Particularly, the adhesive tape is required to have such an adhesive force that the semiconductor package (or a chip) can be easily separated using automation equipment that automatically separates the semiconductor package (or the chip) from the adhesive tape. Moreover, the adhesive tape is required not to be perforated or torn by a vacuum chuck or a left pin that is used in the automation equipment. Normally, the automation equipment that automatically separates the semiconductor package (or a semiconductor chip) from the adhesive tape has a maximum tension endurance strength of approximately 500 gf/25 mm. Because of this, in terms of the remove characteristic, it is desirable that the adhesive tape has an adhesive force that is smaller than this maximum tension endurance strength. 
     Then, in terms of the stress characteristic, because a plurality of semiconductor packages, that is, a plurality of semiconductor chips are seated on and adhered to the adhesive tape during the process of forming the EMI shielding layer, the adhesive tape is required to ensure its suitable-level tensile stress and compressive stress in such a manner that the process of forming the EMI shielding layer is performed in a state where a distance between adjacent semiconductor chips is maintained. That is, the adhesive tape is required to be stably kept taut and at the same time to maintain stress balance in a manner that corresponds to the topology of the lower surface of the semiconductor package including the protrusion electrode. 
     
       
     
     With reference to  FIGS.  1  and  2   , an adhesive tape  100  for a semiconductor package manufacturing process according to an embodiment of the present disclosure relates to an adhesive tape  100  for a semiconductor package manufacturing process that is adhered to a lower surface of the semiconductor package  10  on which a plurality of protrusion electrodes  11  are formed. 
     The adhesive tape  100  for a semiconductor package manufacturing process according to the present disclosure was conceived to ensure the adhesion characteristic, the retention characteristic, the remove characteristic, and the stress characteristic that, as described above, are required during the process of forming the EMI shielding layer. 
     
       
     
     First, the adhesive tape  100  for a semiconductor package manufacturing process according to the embodiment of the present disclosure is configured to include a first base film  111 , a first adhesive layer  112 , a second base film  121 , and a second adhesive layer  122 . 
     In this case, the adhesive tape  100  for a semiconductor package manufacturing process according to the embodiment of the present disclosure may further include a second release film  123 . The second release film  123  will be described in more detail when a method of manufacturing the adhesive tape  100  for a semiconductor package manufacturing process according to an embodiment of the present disclosure is described. 
     
       
     
     The first base film  111  contains a plastic material or a metal material. 
     In this case, the first base film  111  of a plastic material may be a single layer that is formed of one of polyethylene terephthalate, polyimide, and polyolefin or may have a multi-layer structure in which two or more layers, formed of two or more, respectively, of polyethylene terephthalate, polyimide, and polyolefin, are stacked on top of each other. 
     At this point, the first base film  111  may have a thickness of 10 μm to 150 μm. In a case where the first base film  111  has a thickness of less than 10 μm, a user may have difficulty in handling the adhesive tape  100  for a semiconductor package manufacturing process according to the embodiment of the present disclosure. In a case where the first base film  111  has a thickness of more than 150 μm, it may be difficult to maintain the stress balance in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed. 
     It is desirable that the first base film  111  of a metal material contains at least 99 wt % or more of aluminum (Al) and has a tensile strength of 4.8 kgf/mm 2  to 14.4 kgf/mm 2 , an elongation of 6.4% to 19.2%, and a thickness of 20 μm to 80 μm or that the first base film  111  of a metal material contains at least 99 wt % or more of copper (Cu) and has a tensile strength of 8 kgf/mm 2  to 31.2 kgf/mm 2 , an elongation of 3.2% to 14.4%, and a thickness of 20 μm to 80 μm. 
     In this case, the first base film  111  may contain 99 wt % or more of aluminum (Al) or 99 wt % or more of copper (Cu). Moreover, the first base film  111  may contain 1 wt % or less of an additive in order to have the tensile strength and the elongation that are described above. The additive may contain one or more selected from the group consisting of silicon (Si), iron (Fe), manganese (Mn), zinc (Zn), and titanium (Ti). 
     The reason that the first base film  111  is required to contain 99 wt % or more of aluminum (Al) and to have a tensile strength of 4.8 kgf/mm 2  to 14.4 kgf/mm 2  is because a phenomenon where the first base film  111  cannot be stably kept taut without being loosened may occur during each process of manufacturing the semiconductor package  10 , in a case where the first base film  111  has a tensile strength of less than 4.8 kgf/mm 2 . Moreover, the reason is because the first base film  111  cannot maintain the stress balance in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed, in a case where the first base film  111  has a tensile strength of more than 14.4 kgf/mm 2 . 
     The reason that the first base film  111  is required to contain 99 wt % or more of aluminum Al and to have an elongation of 6.4% to 19.2% is because it may be difficult to deform the first base film  111  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 , in a case where the first base film  111  has an elongation of less than 6.4%. Moreover, the reason is because it is difficult to continuously keep the first base film  111  deformed during each process, in a case where the first base film  111  has an elongation of more than 19.2%. 
     The reason that the first base film  111  is required to contain 99 wt % or more of copper (Cu) and to have a tensile strength of 8 kgf/mm 2  to 31.2 kgf/mm 2  is because the phenomenon where the first base film  111  cannot be stably kept taut without being loosened may occur during each process of manufacturing the semiconductor package  10 , in a case where the first base film  111  has a tensile strength of less than 8 kgf/mm 2 . Moreover, the reason is because the first base film  111  cannot maintain the stress balance in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed, in a stable manner the first base film  111  has a tensile strength of more than 31.2 kgf/mm 2 . 
     The reason that the first base film  111  is required to contain 99 wt % or more of copper (Cu) and to have an elongation of 3.2% to 14.4% is because it may be difficult to deform the first base film  111  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 , in a case where the first base film  111  has an elongation of less than 3.2%. Moreover, the reason is because it is difficult to continuously keep the first base film  111  deformed during each process, in a case where the first base film  111  has an elongation of more than 14.4%. 
     The first base film  111  of a metal material may have a thickness of 20 μm to 80 μm. In a case where the first base film  111  has a thickness of less than 20 μm, a user may have difficulty in handling the adhesive tape  100  for a semiconductor package manufacturing process according to the embodiment of the present disclosure. In the case where the first base film  111  has a thickness of more than 80 μm, it may be difficult to maintain the stress balance in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed. 
     Since the first base film  111  is formed of the material described above in such a manner as to have the structure described above, the stress balance is effectively maintained in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed, during the process of forming the EMI shielding layer, and the stress characteristic required of the adhesive tape for a semiconductor package manufacturing process is easily ensured. That is, since the first base film  111  is formed of the material described above in such a manner as to have the structure described above, the first base film  111  may be stably kept taut without being loosened, during each process of manufacturing the semiconductor package  10  and, at the same time, may maintain the stress balance in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed. Moreover, the first base film  111  has the characteristic that denaturation and deformation thereof occur to a less degree in the high-temperature and high-vacuum environment. Furthermore, the first base film  111  contains a plastic material or a metal material. Thus, the first base film  111  prevents an air bubble (gas or a particle), present outside the first base film  111 , from being transferred to the first adhesive layer  112 . 
     
       
     
     The first adhesive layer  112  is stacked on top of the first base film  111  and contains an acrylic-based copolymer. 
     It is desirable that the first adhesive layer  112  has a greater thickness than the second adhesive layer  122  and has a stronger adhesive force than the second adhesive layer  122 . More specifically, the first adhesive layer  112  may have a thickness of 100 μm to 700 μm and an adhesive force of at least more than 500 gf/25 mm. That is, the first adhesive layer  112  may have a thickness of 100 μm to 700 μm and an adhesive force of at least more than 500 gf/25 mm, for example, an adhesive force of 500 gf/25 mm to 2500 gf/25 mm in such a manner as to be impregnated with the protrusion electrode  11 . 
     In this case, in a case where the first adhesive layer  112  has a thickness of less than 100 μm, the ability of the first adhesive layer  112  to impregnate with the protrusion electrode  11  the adhesive tape  100  for a semiconductor package manufacturing process and thus to cushion the protrusion electrode  11  during each process can be decreased. In a case where the first adhesive layer  112  has a thickness of less than 700 μm, the ability of the adhesive tape  100  to adhere the lower surface of the semiconductor package  10  and the adhesive tape  100  for a semiconductor package manufacturing process to each other, to bring them into close contact with each other, and to maintain the adhesion the close contact can be decreased. 
     In a case where the first adhesive layer  112  has an adhesive force of less than 500 gf/25 mm, when the adhesive tape  100  for a semiconductor package manufacturing process is removed from the semiconductor package  10 , a defect may occur, such as the occurrence of peeling off from the first adhesive layer  112 . In a case where the first adhesive layer  112  has an adhesive force of more than 2500 gf/25 mm, the first adhesive layer  112  has the characteristic that the adhesive force thereof is in proportion to the thickness thereof. Because of this, a difficulty may occur in forming the first adhesive layer  112  in such a manner as to have a thickness thereof required of the adhesive tape  100  for a semiconductor package manufacturing process. 
     In terms of a material, it is desirable that the first adhesive layer  112  contains at least one of a butyl acrylate-butyl methacrylate-methacrylic acid-methyl methacrylate-styrene copolymer and an acrylic acid-2-ethylhexyl acrylate-2-ethylhexyl methacrylate-glycidyl methacrylate copolymer. In this case, in two types of acrylic-based copolymers, the order in which monomers are combined may be changed. combination methods may include alternating copolymer, block copolymer, random copolymer, isotactic copolymer, syndiotactic copolymer, atactic copolymer, and the like, and the monomers are not limited to a specific combination method. 
     It is desirable that the first adhesive layer  112  is formed by mixing at least one of a first adhesive composition and a second adhesive composition, and an epoxy-based hardener, applying the resulting mixture to the first base film  111 , and then drying and hardening the resulting mixture. The first adhesive composition contains 25 to 30 parts by weight of a butyl acrylate-butyl methacrylate-methacrylic acid-methyl methacrylate-styrene copolymer, and 70 to 75 parts by weight of ethyl acetate, 25 to 30 parts by weight of the second adhesive composition contains acrylic acid-2-ethylhexyl acrylate ethylhexyl methacrylate-glycidyl methacrylate copolymer, 50 to 55 parts by weight of toluene, and 15 to 20 parts by weight of ethyl acetate. 
     In this case, when butyl acrylate-butyl methacrylate-methacrylic acid-methyl methacrylate-styrene copolymer, which is a main material of the first adhesive composition is less than 25 parts by weight, the adhesive force and heat resistance of the first adhesive layer  112  are decreased, and at the same time, the first adhesive layer  112  becomes too soft. Thus, the first adhesive layer  112  poorly serves as a cushion. Consequently, there occurs a problem in that the second base film  121  is torn. When butyl acrylate-butyl methacrylate-methacrylic acid-methyl methacrylate styrene copolymer is more than 30 parts by weight, the first adhesive layer  112  becomes too hard. Thus, the first adhesive layer  112  poorly serves as a cushion. Consequently, there occurs a problem in that it is difficult to deform the first adhesive layer  112  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  and that it is also difficult to independently maintain a deformed shape of the first adhesive layer  112  due to expansion after the first adhesive layer  112  is deformed. 
     In addition, when ethyl acetate that is a solvent of the first adhesive composition of the first adhesive layer  112  is less than 70 parts by weight, the viscosity of the first adhesive composition becomes too high. Thus, it is difficult to mix the second adhesive composition and the epoxy-based hardener. Moreover, a surface of the first adhesive layer  112  is roughened during the applying process and, at the same time, a degassing phenomenon occurs frequently during a drying and hardening process. Consequently, there occurs a problem in that the characteristic of the first adhesive layer  112  deteriorates. In a case where ethyl acetate that is a solvent of the first adhesive composition of the first adhesive layer is more than 75 parts by weight, the viscosity of the first adhesive composition becomes too low. Because of this, it is difficult to form the first adhesive layer  112  in such a manner as that a thickness thereof is sufficient, during the applying process. Thus, there occurs a problem in that a cushioning characteristic of the first adhesive layer  112  deteriorates. 
     In addition, when acrylic acid-2-ethylhexyl acrylate-2-ethylhexyl methacrylate-glycidyl methacrylate copolymer that is a main adhesive material of the second adhesive composition is less than 25 parts by weight, the adhesive force and the heat resistance of the first adhesive layer  112  are decreased and, at the same time, become too soft. Thus, the first adhesive layer  112  poorly serves as a cushion. Consequently, there occurs a problem in that the second base film  121  is torn. When acrylic acid-2-ethylhexyl acrylate-2-ethylhexyl methacrylate-glycidyl methacrylate copolymer is less than 30 parts by weight, the first adhesive layer  112  becomes too hard and thus poorly serves as a cushion. Consequently, there occurs a problem in that it is difficult to deform the first adhesive layer  112  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  and that, due to expansion after the first adhesive layer  112  is deformed, it is also difficult to independently keep the first adhesive layer  112  deformed. 
     In addition, when the sum of toluene and ethyl acetate that are solvents of the second adhesive composition of the first adhesive layer  112  is less than 65 parts by weight, the viscosity of the second adhesive composition becomes too high. Thus, it is difficult to mix the first adhesive composition and the epoxy-based hardener. Moreover, the surface of the first adhesive layer  112  is roughened during the applying process and, at the same time, the degassing phenomenon occurs frequently during the drying and hardening process. Consequently, there occurs a problem in that the characteristic of the first adhesive layer  112  deteriorates. When the sum of toluene and ethyl acetate that are solvents of the second adhesive composition of the first adhesive layer  112  is more than 75 parts by weight, the viscosity of the second adhesive composition becomes too low. Because of this, it is difficult to form the first adhesive layer  112  in such a manner that the thickness thereof is sufficient, during the applying process. Thus, there occurs a problem in that the cushioning characteristic of the first adhesive layer  112  deteriorates. 
     It is desirable that the first adhesive layer  112  is formed by mixing 80 to 120 parts by weight of the first adhesive composition and 0.5 to 1.5 parts by weight of the epoxy-based hardener, applying the resulting mixture to the first base film  111 , and then drying and hardening the first base film  111 . 
     In this case, when the first adhesive composition is less than 80 parts by weight, the adhesive force and the heat resistance of the first adhesive layer  112  are decreased, and at the same time, the first adhesive layer  112  becomes too hard. Thus, the first adhesive layer  112  poorly serves as a cushion. Consequently, there occurs a problem in that it is difficult to deform the first adhesive layer  112  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 . When the first adhesive composition is more than 120 parts by weight, the first adhesive layer  112  becomes too soft and thus poorly serves as a cushion. Consequently, there occurs a problem in that the second base film  121  is torn. 
     In addition, when the epoxy-based hardener is less than 0.5 parts by weight, the first adhesive layer  112  is not sufficiently hardened and becomes too soft. Thus, the first adhesive layer  112  poorly serves as a cushion. Consequently, there occurs a problem in that the second base film  121  is torn. When the epoxy-based hardener is more than 1.5 parts by weight, the first adhesive layer  112  becomes too hard and thus poorly serves as a cushion. Consequently, there occurs a problem in that it is difficult to deform the first adhesive layer  112  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 . 
     It is more desirable that the first adhesive layer  112  is formed by mixing 40 to 60 parts by weight of the first adhesive composition, 40 to 60 parts by weight of the second adhesive composition, and 0.5 to 1.5 parts by weight of the epoxy-based hardener, applying the resulting mixture to the first base film  111 , and drying and hardening the first base film  111 . 
     In this case, when the first adhesive composition and the second adhesive composition are less than 40 parts by weight, the adhesive force and the heat resistance of the first adhesive layer  112  are decreased, and at the same time, the first adhesive layer  112  becomes too hard. Thus, the first adhesive layer  112  poorly serves as a cushion. Consequently, there occurs a problem in that it is difficult to deform the first adhesive layer  112  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 . When the first adhesive composition is more than 60 parts by weight, the first adhesive layer  112  becomes too soft and thus poorly serves as a cushion. Consequently, there occurs a problem in that the second base film  121  is torn. 
     In addition, when the epoxy-based hardener is less than 0.5 parts by weight, the first adhesive layer  112  is not sufficiently hardened and becomes too soft. Thus, the first adhesive layer  112  poorly serves as a cushion. Consequently, there occurs a problem in that the second base film  121  is torn. When the epoxy-based hardener is more than 1.5 parts by weight, the first adhesive layer  112  becomes too hard and thus poorly serves as a cushion. Consequently, there occurs a problem in that it is difficult to deform the first adhesive layer  112  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 . 
     In association with the retention characteristic, the first adhesive layer  112  has an excellent heat resistance at a high temperature due to a material characteristic, thereby reducing the degassing phenomenon and suitably supporting the deformation of the second base film  121 . Thus, the second base film  121  is prevented from being torn. Moreover, although the second base film  121  is torn, the first adhesive layer  112  securely surrounds the torn second base film  121 , thereby effectively protecting the protrusion electrode  11 . 
     In addition, in associate with the remove characteristic, the first adhesive layer  112  has a stronger adhesive force than the second adhesive layer  122 . Therefore, after the process of forming the EMI shielding layer is finished, the first adhesive layer  112  is separated from the second adhesive layer  122  when the adhesive tape  100  for a semiconductor package manufacturing process is separated from the semiconductor package  10 . 
     The first adhesive layer  112  has a thickness of 100 μm to 700 μm. However, it is desirable that the more increased a size of the protrusion electrode  11 , the more decreased the thickness of the first adhesive layer  112  is in a preset thickness range and that the more increased a gap between the protrusion electrodes  11 , the more increased the thickness of the first adhesive layer  112  is in the preset thickness range. 
     The reason that the more increased the size of the protrusion electrode  11 , the more decreased the thickness of the first adhesive layer  112  is in the preset thickness range is because the thickness of the second adhesive layer  122  is increased in the same environment. Therefore, there is a need to uniformly maintain the entire thickness of the adhesive tape  100  for a semiconductor package manufacturing process and to uniformly maintain the adhesion characteristic, the remove characteristic, the retention characteristic, and the stress characteristic of the adhesive tape  100  for a semiconductor package manufacturing process that are required in a process of manufacturing the semiconductor package  10 . 
     The reason that the more increased the gap between the protrusion electrodes  11 , the more increased the thickness of the first adhesive layer  112  is in the preset thickness range is because the thickness of the second adhesive layer  122  is decreased in the same environment. Therefore, there is a need to uniformly maintain the entire thickness of the adhesive tape  100  for a semiconductor package manufacturing process and to uniformly maintain the adhesion characteristic, the remove characteristic, the retention characteristic, and the stress characteristic of the adhesive tape  100  for a semiconductor package manufacturing process that are required in the process of manufacturing the semiconductor package  10 . Particularly, in a case where the gap between the protrusion electrodes  11  is increased, an area of the lower surface of the semiconductor package  10  that is brought into contact with the second adhesive layer  122  is increased. Thus, after a process of forming the EMI shielding layer is performed, the adhesive tape  100  for a semiconductor package manufacturing process is not easily removed, or there is a high likelihood that a problem will occur in that an adhesive material remains on the lower surface of the semiconductor package  10 . Therefore, the adhesive force for adhesion to the lower surface of the semiconductor package  10  is decreased by decreasing the thickness of the second adhesive layer  122 . 
     
       
     
     The second base film  121  is stacked on top of the first adhesive layer  112 . The second base film  121  contains a metal material in such a manner as to be deformed in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  and then to keep the second base film  121  deformed during each process. 
     As a practical example of the present disclosure, it is preferable that the second base film  121  has a thickness of 1 μm to 10 μm. The reason for this is as follows. In a case where the second base film  121  has a thickness of less than 1 μm, the user has great difficulty not only in handling the adhesive tape  100  for a semiconductor package manufacturing process, but also in keeping the second base film  121  deformed. In a case where the second base film  121  has a thickness of more than 10 μm, it is difficult to deform the second base film  121  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed and to maintain the stress balance. Unlike in another practical example of the present disclosure that will be described below, the thickness in this range is advantageous in a case where the protrusion electrode  11  has a great size. 
     For example, the second base film  121  may be manufactured in the shape of a transfer film resulting from metal deposition, by depositing aluminum (Al) or copper (Cu) on the release film, and then may be laminated on the first adhesive layer  112 . This manufacturing and laminating of the second base film  121  will be described in detail below when describing a method S 100  of manufacturing the adhesive tape  100  for a semiconductor package manufacturing process according to a second embodiment of the present disclosure. 
     It is desirable that the second base film  121  contains at least 99 wt % or more of aluminum (Al) and has a tensile strength of 4.8 kgf/mm 2  to 14.4 kgf/mm 2 , an elongation of 6.4% to 19.2%, and a thickness of 10 μm to 35 μm. Alternatively, it is desirable that the second base film  121  contains at least 99 wt % or more of copper (Cu), a tensile strength of 8 kgf/mm 2  to 31.2 kgf/mm 2 , an elongation of 3.2% to 14.4%, and a thickness of 10 μm to 35 μm. 
     More specifically, during a process of manufacturing the semiconductor package  10 , the second base film  121  may be deformed in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed, and then may be independently kept deformed. The second base film  121  may contain 99 wt % or more of aluminum (Al) or 99 wt % or more of copper (Cu) in such a manner that denaturation and deformation thereof do not occur in the high-temperature and high-pressure environment. 
     In this case, the second base film  121  may contain 99 wt % or more of aluminum (Al) or 99 wt % or more of copper (Cu). Moreover, the second base film  121  may contain 1 wt % or less of an additive in order to have the tensile strength and the elongation that are described above. The additive may contain one or more selected from the group consisting of silicon (Si), iron (Fe), manganese (Mn), zinc (Zn), and titanium (Ti). 
     The reason that the second base film  121  is required to have a 99 wt % or more of aluminum (Al) and have a tensile strength of 4.8 kgf/mm 2  to 14.4 kgf/mm 2  is because there may occur a phenomenon where the second base film  121  is cut or torn due to an external force that is applied during a process of manufacturing the adhesive tape  100  for a semiconductor package manufacturing process and during the process of forming the EMI shielding layer, in a case where the second base film  121  has a tensile strength of less than 4.8 kgf/mm 2 . Moreover, the reason is because it is difficult to deform the second base film  121  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 , in a case where the second base film  121  has a tensile strength of less than more than 14.4 kgf/mm 2 . 
     The reason that the second base film  121  is required to contain 99 wt % or more of aluminum Al and to have an elongation of 6.4% to 19.2% is because it may be difficult to deform the second base film  121  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 , in a case where the second base film  121  has an elongation of less than 6.4%. Moreover, the reason is because it is difficult to continuously keep the second base film  121  deformed during each process, in a case where the second base film  121  has an elongation of more than 19.2%. 
     The reason that the second base film  121  is required to contain 99 wt % or more of copper (Cu) and to have a tensile strength of 8 kgf/mm 2  to 31.2 kgf/mm 2  is because there may occur the phenomenon where the second base film  121  is cut or torn due to the external force that is applied during the process of manufacturing the adhesive tape  100  for a semiconductor package manufacturing process and during the process of forming the EMI shielding layer, in a case where the second base film  121  has a tensile strength of less than 8 kgf/mm 2 . Moreover, the reason is because it is difficult to deform the second base film  121  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 , in a case where the second base film  121  has a tensile strength of 31.2 kgf/mm 2 . 
     The reason that the second base film  121  is required to contain 99 wt % or more of copper (Cu) and to have an elongation of 3.2% to 14.4% is because it may be difficult to deform the second base film  121  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 , in a case where the second base film  121  has an elongation of less than 3.2%. Moreover, the reason is because it is difficult to continuously keep the second base film  121  deformed during each process, in a case where the second base film  121  has an elongation of more than 14.4%. 
     As another practical example of the present disclosure, the second base film  121  may have a thickness of 10 μm to 35 μm. The reason for this is as follows. In a case where the second base film  121  has a thickness of less than 10 μm, it is very difficult to handle the adhesive tape  100  for a semiconductor package manufacturing process. In a case where the second base film  121  has a thickness of more than 35 μm, it is difficult to deform the second base film  121  in a manner that corresponds to the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed and to maintain the stress balance. Unlike in the practical example of the present disclosure, the thickness in this range is advantageous in a case where the protrusion electrode  11  has a small size. 
     Since the second base film  121  contains a metal material, the second base film  121  may prevent an air bubble (gas or a particle), which may occur in the first adhesive layer  112 , from being transferred to the second adhesive layer  122 . Moreover, when the adhesive tape  100  for a semiconductor package manufacturing process is attached on the lower surface of the semiconductor package  10 , due to the sufficient retention characteristic, the second base film  121 , after deformed in a manner that corresponds to the topology of the lower surface of the semiconductor package  10 , may be kept deformed during each process. That is, since the second base film  121  contains a metal material, the second base film  121  blocks gas or the like which occurs in the first adhesive layer  112 , from being transferred to the second adhesive layer  122 . Moreover, the second base film  121  supports the second adhesive layer  122  in such a manner as to be kept flat. Thus, in the high-temperature and high-vacuum environment, the second base film  121  continuously maintains its ability for adhesion to and close contact with the lower surface of the semiconductor package  10  that includes the protrusion electrode  11 . 
     
       
     
     The second adhesive layer  122  is stacked on top of the second base film  121  and contains silicon having a spiral network structure. 
     It is desirable that the second adhesive layer  122  has a small diameter than the first adhesive layer  112  and has a weaker adhesive force than the first adhesive layer  112 . More specifically, the second adhesive layer  122  may have a thickness of 10 μm to 50 μm and an adhesive force of 50 gf/25 mm to 500 gf/25 mm in such a manner as to be possibly adhered perfectly along the topology of the lower surface of the semiconductor package  10  on which the protrusion electrode  11  is formed. 
     At this point, in a case where the second adhesive layer  122  has a thickness of less than 10 μm, the second adhesive layer  122  cannot secure an adhesive force necessary. Because of this, during a process, the ability for adhesion to and close contact with the lower surface of the semiconductor package  10  and the retention characteristic deteriorate, and thus a peeling-off phenomenon may occur. In a case where the second adhesive layer  122  has a thickness of more than 50 μm, the second adhesive layer  122 , when attached on the lower surface of the semiconductor package  10 , is pushed, with pressing pressure, to a lateral side. Thus, there may occur a problem in that a defect occurs or that removal from the semiconductor package  10  is difficult. 
     In a case where the second adhesive layer  122  has an adhesive force of less than 50 gf/25 mm, the second adhesive layer  122  is pushed from the lower surface of the semiconductor package  10  and the protrusion electrode  11  in the high-temperature and high-vacuum environment during the process of forming the EMI shielding layer. Thus, the peeling-off phenomenon may occur, or a phenomenon where gas and a particle penetrate between the second adhesive layer  122  and an adhesion surface of the semiconductor package  10  may occur during each process. In a case where the second adhesive layer  122  has an adhesive force of more than 500 gf/25 mm, removal from the semiconductor package  10  may be difficult at room temperature or at an atmospheric pressure after undergoing the process of forming the EMI shielding layer, or there may occur a problem in that the adhesive material remains on the lower surface of the semiconductor package and the surface of the protrusion electrode  11 . 
     In terms of a material, it is desirable that the second adhesive layer  122  contains a trimethylated silica-dimethyl siloxane copolymer. 
     Since the second adhesive layer  122  contains the trimethylated silica-dimethyl siloxane copolymer, physical deformation due to heat occurring during the process of forming the EMI shielding layer is reduced, and the adhesion characteristic, the retention characteristic, the remove characteristic, and the stress characteristic that are required of the adhesive tape for a semiconductor package manufacturing process are easily ensured. 
     Furthermore, the second adhesive layer  122  has the spiral network structure as a molecular structure, with a siloxane bond as a basic frame. Therefore, although an air gap occurs between each of the lower surface of the semiconductor package  10 , the protrusion electrode  11 , and the second adhesive layer  122 , even in the high-temperate and high-vacuum environment, the air gap is prevented from being excessively expanded. 
     The second adhesive layer  122  has a thickness of 10 μm to 50 μm. However, it is desirable that the more increased the size of the protrusion electrode  11 , the more increased the thickness of the second adhesive layer  122  is in a preset thickness range and that the more increased the gap between the protrusion electrodes  11 , the more decreased the thickness of the second adhesive layer  122  is in the preset thickness range. 
     The reason that the more increased the size of the protrusion electrode  11 , the more increased the thickness of the second adhesive layer  122  is in the preset thickness range is because the more increased the size of the protrusion electrode  11 , the higher a likelihood that the second adhesive layer  122  will be pushed from the protrusion electrode  11  and be reeled off. Thus, there is a need to increase the adhesive force of the second adhesive layer  122 . 
     In addition, the reason that the more increased the gap between the protrusion electrodes  11 , the more decreased the thickness of the second adhesive layer  122  is in the preset thickness range is because the more increased the gap between the protrusion electrodes  11 , the more increased the area of the lower surface of the semiconductor package  10  that is adhered to the second adhesive layer  122 . The increase in the area of the lower surface of the semiconductor package  10  may cause the problem that the second adhesive layer  122  is not easily removed after the process of forming the EMI shielding layer or that the adhesive material remains on the lower surface of the semiconductor package  10 . Therefore, there is a need to decrease the adhesive force of the second adhesive layer  122 . 
     In association with the adhesion characteristic, the second adhesive layer  122  contains silicon having a spiral network structure. Thus, respective regions of the lower surface of the semiconductor package  10  and the protrusion electrode  11  that are brought into contact with each other have the sufficient adhesion characteristic. In association with the remove characteristic, the second adhesive layer  122  contains a weaker adhesive force than the first adhesive layer  112 . Thus, when the adhesive tape  100  for a semiconductor package manufacturing process is removed from the semiconductor package  10  after the process of forming the EMI shielding layer, the second adhesive layer  122  is separated instead of the first adhesive layer  112 . 
     
       
     
     As described above, the adhesive tape  100  for a semiconductor package manufacturing process according to the present disclosure has excellent adhesion, retention, remove, and stress characteristics. The lower surface of the semiconductor package  10  and a plurality of the protrusion electrodes  11  formed on the lower surface of the semiconductor package  10  are effectively protected during the process of forming the EMI shielding layer for the semiconductor package  10  including the plurality of the protrusion electrodes  11 . 
     
       
     
     The method S 100  of manufacturing the adhesive tape  100  for a semiconductor package manufacturing process according to the embodiment of the present disclosure will be described below with reference to  FIGS.  3  to  5   . 
     The first embodiment and the second embodiment will be described separately. The above-described configuration of the adhesive tape  100  for a semiconductor package manufacturing process may be partially omitted when determined as being repeated. 
     The method S 110  of manufacturing the adhesive tape  100  for a semiconductor package manufacturing process according to the embodiment of the present disclosure is configured to include a tape preparation step S 110  and a tape lamination step S 120 . 
     
       
     
     First Embodiment 
     
       
     
     The method S 100  of manufacturing the adhesive tape  100  for a semiconductor package manufacturing process is configured to include a first tape preparation step S 111  and a first tape lamination step S 121 . 
     
       
     
     The first tape preparation step S 111  is a step in which a first tape  110  and a second tape  120  are manufactured. The first tape  110  is manufactured by sequentially stacking the first base film  111  containing a plastic material or a metal material, the first adhesive layer  112  containing an acrylic-based copolymer, and a first release film  113  containing fluorine on top of each other. The second tape  120  is manufactured by sequentially stacking a second base film  121  containing a metal material, the second adhesive layer  122  containing silicon having a spiral network structure, and a second release film  123 . 
     
       
     
     First, a step of manufacturing the first tape  110  starts with a manufacturer&#39;s preparing the first base film  111  containing a plastic material or a metal material. As described above, the first base film  111  may contain at least 99 wt % or more of aluminum (Al) and may have a tensile strength of 4.8 kgf/mm 2  to 14.4 kgf/mm 2 , an elongation of 6.4% to 19.2%, and a thickness of 20 μm to 80 μm. Alternatively, the first base film  111  may contain at least 99 wt % or more of copper (Cu) and may have a tensile strength of 8 kgf/mm 2  to 31.2 kgf/mm 2 , an elongation of 3.2% to 14.4%, and a thickness of 20 μm to 80 μm. In addition, the first base film  111  may be a single layer that is formed of one of polyethylene terephthalate, polyimide, and polyolefin or may have a multi-layer structure in which two or more layers, formed of two or more, respectively, of polyethylene terephthalate, polyimide, and polyolefin, are stacked on top of each other. The first base film  111  may have a thickness of 10 μm to 150 μm. 
     Subsequently, the manufacturer puts into a mixture container the first adhesion composition (80 to 120 parts by weight) containing 25 to 30 parts by weight of a butyl acrylate-butyl methacrylate-methacrylic acid-methyl methacrylate-styrene copolymer and 70 to 75 parts by weight of ethyl acetate, and the epoxy-based hardener (0.5 to 1.5 parts by weight) and mixes them by stirring. Alternatively, the manufacturer puts into the mixture container the first adhesion composition (40 to 60 parts by weight) containing 25 to 30 parts by weight of a butyl acrylate-butyl methacrylate-methacrylic acid-methyl methacrylate-styrene copolymer and 70 to 75 parts by weight of ethyl acetate, the second adhesion composition (40 to 60 parts by weight) containing 25 to 30 parts by weight of an acrylic acid-2-ethylhexyl acrylate-2-ethylhexyl methacrylate-glycidyl methacrylate copolymer, 50 to 55 parts by weight of toluene, and 15 to 20 parts by weight of ethyl acetate, and the epoxy-based hardener and mixes them by stirring. At this point, the mixing is performed by stirring at room temperature and at normal moisture. 
     At this point, the manufacturer stabilizes an acrylic-based composition that results from mixing, by stirring, the first adhesive composition and the epoxy-based hardener, or an acrylic-based composition that results from mixing, by stirring, the first adhesive composition, the second adhesive composition, and the epoxy-based hardener. The acrylic-based composition is stabilized in order to remove an air bubble within the acrylic-based composition and at the same time to induce chemical stability of the acrylic-based composition and a uniform cross-linking reaction. As one way of stabilizing the acrylic-based composition, ultrasonic treatment or vacuum suction is possibly performed in order to remove the air bubble within the acrylic-based composition. The manufactured acrylic-based composition may be brought to rest in a thermal equilibrium state for stabilization of the acrylic-based composition for 4 hours to 12 hours after the air bubble is removed. In order to ensure the chemical stability and to prevent an abrupt cross-linking reaction, it is desirable that the acrylic-based composition is stabilized in the thermal equilibrium state. 
     Subsequently, the manufacturer forms the first adhesive layer  112  by applying the stabilized acrylic-based composition on top of the first base film  111  using a comma coater, a slot-die coater, a gravure coater, and the like and then drying and hardening the resulting acrylic-based composition. 
     At this time, the manufacturer may apply the acrylic-based composition on top of the first base film  111  to a thickness greater than a final thickness of the first adhesive layer  112 , using the comma coater, the slot-die coater, the gravure coater, and the like. Specifically, the comma coater, the slot-die coater, the gravure coater, and the like may be controlled to apply the acrylic-based composition to a thickness 2.5 times to 3.5 times a target thickness of the first adhesive layer  112 . For example, in a case where the first adhesive layer  112  has a target thickness of 100 μm to 700 μm, the comma coater may be controlled in such a manner that the acrylic-based composition is applied to a thickness of 250 μm to 2450 μm. A step of applying the stabilized acrylic-based composition on top of the first base film  111  may be performed with a spin coating technique, a spray technique, or the like. 
     Subsequently, the manufacturer may finally form the first adhesive layer  112  through drying and heat-treatment and through aging and hardening. During these processes, the thickness of the first adhesive layer  112  is gradually decreased and reaches a target thickness. 
     More specifically, the manufacturer performs the drying and heat treatment on the first adhesive layer  112 . The drying and heat treatment is performed to remove a solvent within the acrylic-based composition and at the same time to activate the cross-linking reaction. The drying and heat treatment is performed at a temperature range from 90° C. to 120° C. for 15 minutes to 30 minutes, using an infrared lamp, a dryer that uses both infrared light and hot air, and the like. 
     Depending on the situation, the drying and heat treatment may include first drying and heat treatment, second drying and heat treatment, and third drying and heat treatment that are separately performed. 
     In this case, the first drying and heat treatment may be performed to remove the solvent within the acrylic-based composition and at the same time to activate the cross-linking reaction. The first drying and heat treatment may be performed at a temperature of 60° C. to 80° C. for 3 minutes to 6 minutes, using the infrared lamp, the dryer that uses both infrared light and hot air, and the like. 
     Subsequently, like the first drying and heat treatment, the second drying and heat treatment may be performed to remove the solvent within the acrylic-based composition and at the same time to activate the cross-linking reaction. The second drying and heat treatment may be performed at a higher temperature than the first drying and heat treatment, for the same time as the first drying and heat treatment, using the infrared lamp, the dryer that uses both infrared light and hot air, and the like. For example, the second drying and heat treatment may be performed at a temperature of 90° C. to 120° C. for 3 minutes to 6 minutes. 
     Subsequently, like the first drying and heat treatment and the second drying and heat treatment, the third drying and heat treatment may be performed to remove the solvent within the acrylic-based composition and at the same time to activate the cross-linking reaction. The third drying and heat treatment may be performed at a higher temperature than the second drying and heat treatment, for a longer time than the second drying and heat treatment, using the infrared lamp, the dryer that uses both infrared light and hot air, and the like. For example, the third drying and heat treatment may be performed at a temperature of 190° C. to 210° C. for 9 minutes to 18 minutes. 
     At this point, the reason that in the first drying and heat treatment, the second drying and heat treatment, and the third drying and heat treatment, the first adhesive layer  112  is dried while the temperature is gradually increased is to prevent the first adhesive layer  112  from being dried and hardened, starting from a surface thereof. Accordingly, the air bubble within the first adhesive layer  112  may be easily removed. Furthermore, after the third drying and heat treatment is performed, the temperature is gradually decreased to room temperature. Thus, the first adhesive layer  112  in a stable state that has a uniform thickness may be formed. 
     Subsequently, the manufacturer ages the first adhesive layer  112  at a temperature of 20° C. to 60° C. for 12 hours to 48 hours for stabilization and hardening. That is, for a resting period, the first base film  111  and the first adhesive layer  112  that are heated during the drying and heat treatment are gradually cooled to a temperature of 20° C. to 60° C. Thus, the cross-linking reaction within the first adhesive layer  112  is stably finished, and, at the same time, a physical property required of the first adhesive layer  112  is secured. 
     Subsequently, the manufacturer attaches the first release film  113 , containing fluorine, on the first adhesive layer  112 . The first release film  113  may contain fluorine in such a manner as to protect the first adhesive layer  112  containing the acrylic-based copolymer and, at the same time, to be easily separated from the first adhesive layer  112 . The first release film  113  may have an adhesive force of 3 gf/25 mm to 8 gf/25 mm. At this point, in a case where the first release film  113  has an adhesive force of less than 3 gf/25 mm, the first release film  113  may be naturally reeled off from the first adhesive layer  112 . In a case where the first release film  113  has an adhesive force of more than 8 gf/25 mm, there occurs a problem in that the first adhesive layer  112  may be damaged while the first release film  113  is removed. 
     The manufacturer may manufacture the first tape  110  by performing the above-described processes. 
     
       
     
     A step of manufacturing the second tape  120  is described. First, the manufacturer prepares the second base film  121  that contains at least 99 wt % or more of aluminum (Al) and has a tensile strength of 4.8 kgf/mm 2  to 14.4 kgf/mm 2 , an elongation of 6.4% to 19.2%, and a thickness of 10 μm to 35 μm, or prepares at least 99 wt % or more of copper (Cu) and has a tensile strength of 8 kgf/mm 2  to 31.2 kgf/mm 2 , an elongation of 3.2% to 14.4%, and a thickness of 10 μm to 35 μm. 
     Subsequently, the manufacturer puts into the mixture container a trimethylated silica-dimethyl siloxane copolymer, an ethylbenzene solvent, and an epoxy-based hardener and mixes them by stirring. At this point, the mixing is performed by stirring at room temperature and at normal moisture. 
     At this point, the manufacturer stabilizes a silicon-based composition that results from the mixing. The silicon-based composition is stabilized in order to remove an air bubble within the silicon-based composition and at the same time to induce chemical stability of the silicon-based composition and a uniform cross-linking reaction. As one way of stabilizing the silicon-based composition, ultrasonic treatment or vacuum suction is possibly performed in order to remove the air bubble within the silicon-based composition. The manufactured silicon-based composition may be brought to rest in a thermal equilibrium state for stabilization of the silicon-based composition for 4 hours to 12 hours after the air bubble is removed. In order to ensure the chemical stability and to prevent an abrupt cross-linking reaction, it is desirable that the silicon-based composition is stabilized in the thermal equilibrium state. 
     Subsequently, the manufacturer forms the second adhesive layer  122  by applying the stabilized silicon-based composition on top of the second base film  121  using the comma coater, the slot-die coater, the gravure coater, and the like and then drying and hardening the resulting silicon-based composition. 
     At this time, the manufacturer may apply the silicon-based composition on top of the second base film  121  to a thickness greater than a final thickness of the second adhesive layer  122 , using the comma coater, the slot-die coater, the gravure coater, and the like. Specifically, the comma coater, the slot-die coater, the gravure coater, and the like may be controlled to apply the silicon-based composition to a thickness 2.5 times to 3.5 times a target thickness of the second adhesive layer  122 . For example, in a case where the second adhesive layer  122  has a target thickness of 10 μm to 50 μm, the comma coater may be controlled in such a manner that the silicon-based composition is applied to a thickness of 25 μm to 175 μm. A step of applying the stabilized silicon-based composition on top of the second base film  121  may be performed with the spin coating technique, the spray technique, or the like. 
     Subsequently, the manufacturer may finally form the second adhesive layer  122  through drying and heat-treatment and through aging and hardening. During these processes, the thickness of the second adhesive layer  122  is gradually decreased and reaches a target thickness. 
     More specifically, the manufacturer performs the drying and heat treatment on the second adhesive layer  122 . The drying and heat treatment is performed to remove a solvent within the silicon-based composition and at the same time to activate the cross-linking reaction. The drying and heat treatment is performed at a temperature range from 160° C. to 180° C. for 15 minutes to 30 minutes, using the infrared lamp, the dryer that uses both infrared light and hot air, and the like. 
     Depending on the situation, the drying and heat treatment may include the first drying and heat treatment, the second drying and heat treatment, and the third drying and heat treatment that are separately performed. 
     In this case, the first drying and heat treatment may be performed to remove the solvent within the silicon-based composition and at the same time to activate the cross-linking reaction. The first drying and heat treatment may be performed at a temperature range from 60° C. to 80° C. for 3 minutes to 6 minutes, using the infrared lamp, the dryer that uses both infrared light and hot air, and the like. 
     Subsequently, like the first drying and heat treatment, the second drying and heat treatment may be performed to remove the solvent within the silicon-based composition and at the same time to activate the cross-linking reaction. The second drying and heat treatment may be performed at a higher temperature than the first drying and heat treatment, for the same time as the first drying and heat treatment, using the infrared lamp, the dryer that uses both infrared light and hot air, and the like. For example, the second drying and heat treatment may be performed at a temperature of 160° C. to 180° C. for 3 minutes to 6 minutes. 
     Subsequently, like the first drying and heat treatment and the second drying and heat treatment, the third drying and heat treatment may be performed to remove the solvent within the silicon-based composition and at the same time to activate the cross-linking reaction. The third drying and heat treatment may be performed at a higher temperature than the second drying and heat treatment, for a longer time than the second drying and heat treatment, using the infrared lamp, the dryer that uses both infrared light and hot air, and the like. For example, the third drying and heat treatment may be performed at a temperature of 190° C. to 210° C. for 9 minutes to 18 minutes. 
     At this point, the reason that in the first drying and heat treatment, the second drying and heat treatment, and the third drying and heat treatment, the second adhesive layer  122  is dried while the temperature is gradually increased is to prevent the second adhesive layer  122  from being dried and hardened, starting from a surface thereof. Accordingly, the air bubble within the second adhesive layer  122  may be easily removed. Furthermore, after the third drying and heat treatment is performed, the temperature is gradually decreased to room temperature. Thus, the second adhesive layer  122  in a stable state that has a uniform thickness may be formed. 
     Subsequently, the manufacturer ages the second adhesive layer  122  at a temperature of 20° C. to 30° C. for 12 hours to 24 hours for stabilization and hardening. That is, for the resting period, the second base film  121  and the second adhesive layer  122  that are heated during the drying and heat treatment are gradually cooled to a temperature of 20° C. to 30° C. Thus, the cross-linking reaction within the second adhesive layer  122  is stably finished, and, at the same time, a physical property required of the second adhesive layer  122  is secured. 
     Subsequently, the manufacturer attaches the second release film  123 , containing fluorine, on the second adhesive layer  122 . The second release film  123  may contain fluorine in such a manner as to protect the second adhesive layer  122  containing silicon having the spiral network structure and, at the same time, to be easily separated from the second adhesive layer  122 . The second release film  123  may have an adhesive force of 3 gf/25 mm to 8 gf/25 mm. At this point, in a case where the second release film  123  has an adhesive force of less than 3 gf/25 mm, the second release film  123  may be naturally reeled off from the second adhesive layer  122 . In a case where the second release film  123  has an adhesive force of more than 8 gf/25 mm, there occurs a problem in that the second adhesive layer  122  may be damaged while the second release film  123  is removed. 
     The manufacturer may manufacture the second tape  120  by performing the above-described processes. 
     
       
     
     The first tape lamination step S 121  is a step in which the manufacturer removes the first release film  113  from the first tape  110 , brings the first adhesive layer  112  and the second base film  121  into surface contact with each other, and thus laminates the first tape  110  and the second tape  120  to each other. 
     Thereafter, before the process of forming the EMI shielding layer, the user attaches the adhesive tape  100  for a semiconductor manufacturing process according to the embodiment of the present disclosure by removing the second release film  123  of the second tape  120  and bringing the second adhesive layer  122  into contact with the lower surface of the semiconductor package  10  and with the protrusion electrode  11 . 
     
       
     
     Second Embodiment 
     
       
     
     The method S 100  of manufacturing the adhesive tape  100  for a semiconductor package manufacturing process according to the second embodiment of the present disclosure is configured to include a second tape preparation step S 112  and a second tape lamination step S 122 . 
     
       
     
     The second tape preparation step S 112  is a step in which a first tape  110 , a third tape  130 , and a fourth tape  140  are manufactured. The first tape  110  is manufactured by sequentially stacking the first base film  111  containing a plastic material or a metal material, the first adhesive layer  112  containing an acrylic-based copolymer, and a first release film  113  containing fluorine on top of each other. The third tape  130  is manufactured by depositing the second base film  121  on a third release film  131  using a metal deposition technique. The fourth tape  140  is manufactured by sequentially stacking the second adhesive layer  122  containing silicon having a spiral network structure and the second release film  123  containing fluorine on top of each other. 
     
       
     
     A step of manufacturing the first tape  110  is the same as in the first embodiment, and therefore, a detailed description thereof is omitted. 
     
       
     
     A step of manufacturing the third tape  130  is performed by forming the second base film  121  on the third release film  131  using the metal deposition technique. More specifically, the second base film  121  is formed by depositing Al or Cu on the third release film  131  using the metal deposition technique, and as a result, the third tape  130  may be manufactured in the shape of a transfer film resulting from metal deposition. A sputtering technique or the like may be used as the metal deposition technique. However, the metal deposition technique is not limited thereto. 
     The third release film  131  may have the same characteristic as the first release film  113  and the second release film  123 . 
     In this case, it is desirable that the second base film  121  is deposited on the third release film  131  in such a manner as to have a thickness of 1 μm to 10 μm. The thickness in this range is advantageous in a case where the protrusion electrode  11  has a large size. 
     
       
     
     A step of manufacturing the fourth tape  140  is performed by forming the second adhesive layer  122  by utilizing the second release film  123  as a base film. The second adhesive layer  122  in the second embodiment is formed in the same manner as the second adhesive layer  122  is formed on the second base film  121  in the first embodiment, and therefore, a detailed description thereof is omitted. 
     
       
     
     In the second tape lamination step S 122 , the manufacturer removes the first release film  113  from the first tape  110 , then brings the first adhesive layer  112  and the second base film  121  of the third tape  130  into surface contact with each other, and laminates the first tape  110  and the third tape  130  on each other. Subsequently, the manufacturer removes the third release film  131  from the third tape  130 , then brings the second base film  121  and the second adhesive layer  122  of the fourth tape  140  into surface contact with each other, and laminates the third tape  130  and the fourth tape  140  on each other. 
     Thereafter, before the process of forming the EMI shielding layer, the user attaches the adhesive tape  100  for a semiconductor manufacturing process according to the embodiment of the present disclosure by removing the second release film  123  of the fourth tape  140  and bringing the second adhesive layer  122  into contact with the lower surface of the semiconductor package  10  and with the protrusion electrode  11 . 
     
       
     
     As described above, with the method S 100  of manufacturing the adhesive tape  100  for a semiconductor package manufacturing process according to the embodiment of the present disclosure, the first to fourth tapes  110  to  140  are manufactured through an individual manufacturing process, then are laminated on each other, and thus the adhesive tape  100  for a semiconductor manufacturing process are manufactured as a final product. In a case where a defect occurs in the tape during the processes of manufacturing the first to fourth tapes  110  to  140 , it is possible to individually discard only the defective tape. Thus, the overall process yield is improved. 
     
       
     
     The embodiments of the present disclosure are described above only in an exemplary manner with reference to the drawings. It would be understandable to a person of ordinary skill in the art to which the present disclosure pertains that various modifications and equivalents are possibly made to the embodiments. Accordingly, the proper technical scope of the present disclosure should be defined in the following claims in light of the detailed description of the present disclosure. 
     INDUSTRIAL APPLICABILITY 
     The present disclosure relates to an adhesive tape for a semiconductor package manufacturing process and possibly finds application in the industrial field associated with a process of forming an Electromagnetic Interference (EMI) shielding layer for a semiconductor package.