Patent Publication Number: US-2022220331-A1

Title: Printable mixture, manufacture, and use

Description:
RELATED APPLICATIONS 
     This application is a national stage filing of PCT application No.: PCT/US2020/044225 filed Jul. 30, 2020, entitled PRINTABLE MIXTURE, MANUFACTURE, AND USE, the entire teachings of which are incorporated herein by reference. 
     PCT application No.: PCT/US2020/044225 claims priority to earlier filed U.S. Provisional Patent Application Ser. No. 62/881,646 entitled “PRINTABLE DIELECTRIC MIXTURE, USE, AND MANUFACTURE,” filed on Aug. 1, 2019, the entire teachings of which are incorporated herein by this reference. 
     PCT application No.: PCT/US2020/044225 is related to earlier filed U.S. patent application Ser. No. 16/184,796 entitled “PRINTABLE DIELECTRIC MIXTURE, USE, AND MANUFACTURE,” filed on Nov. 8, 2018, the entire teachings of which are incorporated herein by this reference. 
     Any material, or portion of the above incorporated patent application is only incorporated to the extent that no conflict arises between that incorporated material and the present disclosure material. In the event of a conflict, the conflict is to be resolved in favor of the present disclosure as the preferred disclosure. 
    
    
     BACKGROUND 
     Conventional electronic devices can be printed on a substrate using print techniques as described in U.S. Patent Publication 2017/0009090. For example, this cited patent publication describes a ferroelectric ink comprising Barium Strontium Titanate (BST) in a polymer composite is described. This conventional ink can be employed using direct-ink writing techniques to print high dielectric constant, low loss, and electrostatically-tunable dielectrics on substrates. 
     Brief Description of Embodiments 
     In contrast to conventional inks, embodiments herein include novel printable formulas/mixtures facilitating the manufacture of different types of electronic devices. 
     First Embodiments 
     More specifically, in one example embodiment, a compound comprises: first particles, the first particles being an insulator material (non-electrically conductive material); second particles, the second particles being electrically conductive material; and a combination of the first particles and the second particles distributed and suspended in a printable material in which a cured state of the printable material is transformable into an electrically conductive path via application of heat above a threshold value. 
     In accordance with further embodiments, the second particles are fabricated from silver (Ag). In a yet further embodiment, a ratio of the silver particles to the second particles is approximately 62.5 to 37.5 by weight. Additionally, or alternatively, the second particles are so-called Barium Strontium Titanate (BST) particles. 
     In still further embodiments, a melting point of the second particles is lower than a melting point of the first particles. 
     A ratio of the first particles to second particles can vary depending on the embodiment. In one embodiment, a ratio of the first particles to the second particles is selected such that a group of the second particles in the cured printable material are substantially isolated from each other (such as not touching either to form a continuous conductive path) prior to application of heat to the group of second particles above a threshold value. Heating regions of the cured printable material above a threshold value causes the second particles to contact each other due to the sintering of silver nanoparticles and form conductive paths. 
     Further embodiments herein include exposure of the dielectric material (cured printable material) to heat. In one embodiment, exposure of the dielectric layer of material to heat above the threshold value causes contact amongst the second particles in the group due to the sintering (resulting in necking) of the second particles such as silver nanoparticles, the heat converting a portion of the cured printable material into an electrically conductive path. 
     In accordance with further embodiments, the second particles are silver nanoparticles; the first particles are BST nanoparticles. The compound includes at least one solvent such as 1-methoxy-2-propanol and/or ethylene glycol. In one embodiment, the compound is made up of more than 40% by weight of ethylene glycol. 
     In yet further embodiments, the first particles make up approximately 12.5% of the compound by weight; the second particles make up approximately 21% of the compound by weight; and the mixture of one or more solvents makes up approximately 66.5% of the compound by weight prior to curing. Subsequent to curing, when the solvents in the printable material evaporate or are removed, the cured printable material comprises between 60-70% of first particles and 30-40% of second particles. 
     Further embodiments herein include a method comprising: receiving first particles, the first particles being an insulator material; receiving second particles, the second particles being electrically conductive metal material; and suspending a combination of the first particles and the second particles in a printable liquid slurry in which a subsequent cured state of the printable material is transformable into an electrically conductive path via application of heat above a threshold value. 
     Further embodiments herein include controlling a ratio of mixing the first particles to the second particles in the printable material such that a group of the second particles in a layer of the printable material are isolated from each other (such as non-touching) prior to application of heat to the group of second particles above a threshold value. Subsequent exposure of the printable material to heat above the threshold value causes contact amongst the second particles in the group due to the sintering of silver nanoparticles, the heat converting a portion of the dielectric layer of material into an electrically conductive path. More specifically, the area of the printed layer of dielectric material which was exposed to the heat (such as from a laser or other suitable resource) converts the insulator into the electrically conductive material. 
     Second Embodiments 
     Further embodiments herein include an apparatus comprising: a substrate; printed material disposed on the substrate, the printed material including first particles and second particles, the first particles being an insulator material, the second particles being electrically conductive metal material; and the first particles and second particles being randomly distributed in the printed material, the second particles further being transformable into an electrically conductive path via application of heat above a threshold value. 
     In accordance with further embodiments, the printed material includes a first portion and a second portion, the first portion of the printed material including second particles that have been sintered (connected) via application of heat, the second portion of the printed material including second particles that have not been sintered via application of heat. In one embodiment, the ink is a homogenous mixture of Ag and BST nanoparticles. 
     In yet further embodiments, the first portion of the printed cured material has a lower resistivity than the second portion. The BST material is an electrically insulating material. 
     In still further embodiments, the printed material on the substrate is a dielectric material. 
     The second particles in the printed material are separated from each other by the first particles prior to application of the heat. In one embodiment, the application of the heat to the group of second particles above the threshold value causes physical contact amongst the group of second particles due to the sintering of silver nanoparticles. 
     In yet further embodiments, a melting point of the second particles is much lower than a melting point of the first particles. 
     The second particles can be any suitable metal. In one embodiment, the second particles are silver nanoparticles; the first particles are BST (Barium Strontium Titanate) nanoparticles. The printed material further comprises one or more solvents such as 1-methoxy-2-propanol, ethylene glycol, etc. In one embodiment, the printed material (such as in a non-cured state) is made up of more than 40% by weight of ethylene glycol prior to curing. 
     In accordance with still further embodiments, the first particles make up approximately 21% of the printed material by weight; the second particles make up approximately 12.5% of the printed material by weight; and the mixture of one or more solvents makes up approximately 66.5% of the printed material by weight. 
     Further embodiments herein include a method comprising: applying a printable material to a substrate, the printable material including first particles and second particles suspended in the printable material, the first particles being an insulator material, the second particles being electrically conductive metal material; and curing the printable material on the substrate, the second particles in the cured printable material being transformable into an electrically conductive path via application of heat above a threshold value 
     In accordance with further embodiments, a group of the second particles in the cured printable material are isolated from each other prior to application of heat to the group of second particles above a threshold value. 
     In one embodiment, the first particles are non-electrically conductive material. The second particles are fabricated from metal. 
     Further embodiments of the methods herein include: applying heat to the group of second particles disposed in the dielectric layer of material on the substrate, application of the heat to the group causes the group of second particles to form electrically conductive paths on the substrate through the layer of dielectric material. In one embodiment, application of the heat causes sintering (connecting, necking, etc.) of the second particles, resulting in the electrically conductive paths. 
     As previously discussed, in one embodiment a melting point of the second particles is lower than a melting point of the first particles. 
     In yet further embodiments, exposure of the dielectric layer of material (cured printable material) to heat above the threshold value causes sintering and/or physical contact amongst the second particles in the group. 
     In one embodiment, the cured printable material is a dielectric layer of material in which the first particles and the second particles are suspended. 
     The second particles are any suitable metal such as silver nanoparticles; the first particles are any suitable material such as BST (Barium Strontium Titanate) nanoparticles. The printable material also includes one or more solvents facilitating application of the printable material to a substrate. The one or more solvents can include: 1-methoxy-2-propanol; and ethylene glycol. In one embodiment, the printed material is made up of more than 40% by weight of ethylene glycol prior to curing. 
     In yet further embodiments, the first particles make up approximately 21% of the printed material by weight; the second particles make up approximately 12.5% of the printed material by weight; and the mixture of one or more solvents makes up approximately 66.5% of the printed material by weight. 
     Further embodiments herein include a fabricator receiving a substrate. A first layer of dielectric material is disposed on a surface of the substrate. The first layer of dielectric material includes first particles and second particles suspended in the first layer of dielectric material. The first particles comprise insulator material; the second particles are electrically conductive material such as metal. A fabricator applies heat to a region of the first layer of dielectric material; application of the heat transforms a dielectric material in the region of the first layer of dielectric material into an electrically conductive path. 
     In one embodiment, application of the heat above a threshold value sinters second particles in the region such that they contact each other. 
     In still further example embodiments, the application of the heat above a threshold value causes a set of the second particles in the region to contact each other, creating the electrically conductive path. 
     In still further example embodiments, the first layer of dielectric material includes a set of the second particles (electrically conductive material such as metal) in the region, the set of second particles is substantially non-contiguous (non-touching) prior to application of the heat. In such an instance, the second set of second particles provides a high resistance path. The application of the heat above a threshold value causes a sequence of the second particles in the region to electrically contact each other; the contact of the sequence of second particles in the region transforms the region into an electrically conductive path (lower resistance path). 
     In still further example embodiments, initially, each particle in a group of the second particles in the region are of a first grain size prior to application of the heat. Application of the heat to the region causes the second particles in the group to increase in grain size to a second grain size with respect to the first grain size. 
     Still further example embodiments include steering a laser beam to the region to heat the region in the first layer of dielectric material. In one embodiment, a fabricator controls a magnitude of the heat applied to the region (such as via any suitable heat resource such as laser, photo lithography, convection oven, etc.) depending on a desired resistance of the electrically conductive path to be produced in the region. 
     Fabrication as described herein includes creating one or more circuit components. In one embodiment, application of heat to the region of cured dielectric material creates a via extending between a first surface of the first layer of dielectric material and a second surface of the first layer of dielectric material. 
     Still further embodiments herein include, via a fabricator, applying a second layer of dielectric material on the first layer of dielectric material. Similar to the first layer of dielectric material, the second layer of dielectric material includes first particles and second particles suspended in the second layer of dielectric material. The first particles in the second layer of dielectric material are an insulator material. The second particles in the second layer of dielectric material are electrically conductive material. In a similar manner as previously discussed, the dielectric material is initially a liquid compound (mixture) applied over the first layer of dielectric material to create the second layer of dielectric material. Curing of the material results in the second layer of dielectric material (including the second particles such as metal). 
     The fabricator applies heat to one or more locations of the second layer of dielectric material. Application of the heat to the second layer of dielectric material transforms the heated portion of dielectric material in the second layer from being and insulator material to being an electrically conductive path. In a manner as previously discussed, an amount of applied heat controls a resistance of the created electrically conductive path in the second layer of dielectric material. 
     As previously discussed, fabrication of one or more electrically conductive path via application of heat to one or more regions of the cured dielectric material in one or more layers results in creation of an electronic component. Thus, application of heat to one or more region of the one or more layers of dielectric material results in creation of an electronic component. 
     Note that in accordance with further example embodiments, the dielectric ink such as Ag-BST inks or the like as described herein includes can be used to print resistors on wide range of flexible and rigid substrates. 
     In one embodiment, the resistors derived from heating the dielectric material are stable between the operating temperatures −50 degree and 150 degree C.; the resistance variation is less than 10% in this temperature range. 
     In accordance with further example embodiments, application of greater amounts of heat reduces the resistivity of the cured dielectric material (such as cured Ag-BST11 and Ag-BST12 inks) via silver nanoparticles sintering. 
     In still further example embodiments, Ag-BST13 shows dielectric properties after the curing (exposure to 80 degrees for 15 minutes). 
     Further heating can be used to convert the cured dielectric material into a conductive material from an insulating material. 
     In one embodiment, the resistive components as described herein are cured at 250 degree C. for 3 hours or more in order to produce stable resistor components. 
     Heating of one or more regions of the dielectric material can be provided using a conventional box oven, hot plate, laser beam, high intensity broad band light, etc. 
     The resistivities of all the dielectric inks can be adjusted by changing the heating parameters. 
     In accordance with further example embodiments, laser sintering can be used to pattern the resistors on cured dielectric material layers; only the laser exposed parts will be conductive and other parts will retain their original dielectric properties. 
     The resistance of selective laser sintered resistors can be adjusted by changing the laser intensity and laser raster speed. 
     The selective laser sintering of cured Ag-BST13 layers can be used to fabricate a wide range of devices such as resistors, resistive vias, cylindrical capacitors, vertical parallel plate capacitors, interdigitated capacitors, layers with different sheet resistances, etc. 
     Embodiments herein are useful over conventional printable ink. For example, the disclosed novel printable ink (such as including a combination of non-conductive particles and conductive particles) can be used in various applications such as those applications implementing dielectric material or resistive material. 
     As further described herein, different formulas of this disclosed ink can be used in several printing technologies such as dispensing, aerosol jet, ink jet etc. 
     As previously discussed, substrates coated with a layer of the novel mixture as described herein can be further exposed to heat, which converts the heat-exposed portion of the dielectric layer into a conductive layer. Such an embodiment is useful in fabrication of traces, resistors, etc., on a printed circuit board or other device. These and other more specific embodiments are disclosed in more detail below. 
     Note that any of the resources as discussed herein such as a fabricator (fabrication facility) can include one or more computerized devices, workstations, handheld or laptop computers, or the like to carry out and/or support any or all of the method operations disclosed herein. In other words, one or more computerized devices or processors can be programmed and/or configured to operate as explained herein to carry out the different embodiments as described herein. 
     Yet other embodiments herein include software programs to perform the steps and operations summarized above and disclosed in detail below. One such embodiment comprises a computer program product including a non-transitory computer-readable storage medium (i.e., any computer readable hardware storage medium or hardware storage media disparately or co-located) on which software instructions are encoded for subsequent execution. The instructions, when executed in a computerized device (hardware) having a processor, program and/or cause the processor (hardware) to perform the operations disclosed herein. Such arrangements are typically provided as software, code, instructions, and/or other data (e.g., data structures) arranged or encoded on a non-transitory computer readable storage media such as an optical medium (e.g., CD-ROM), floppy disk, hard disk, memory stick, memory device, etc., or other a medium such as firmware in one or more ROM, RAM, PROM, etc., and/or as an Application Specific Integrated Circuit (ASIC), etc. The software or firmware or other such configurations can be installed onto a computerized device to cause the computerized device to perform the techniques explained herein. 
     Accordingly, embodiments herein are directed to a method, system, computer program product, etc., that supports operations such as fabrication of one or more optical devices as discussed herein. 
     Further embodiments herein include a computer readable storage media and/or a system having instructions stored thereon to facilitate fabrication of one or more mixtures and corresponding electronic devices as discussed herein. For example, in one embodiment, the instructions, when executed by computer processor hardware, cause the computer processor hardware (such as one or more processor devices) associated with a fabricator to: receive first particles, the first particles being an insulator material; receive second particles, the second particles being electrically conductive metal material; and suspend a combination of the first particles and the second particles in a printable material in which a cured state of the printable material is transformable into an electrically conductive path via application of heat above a threshold value. 
     In accordance with further embodiments, the instructions, when executed by computer processor hardware, cause the computer processor hardware (such as one or more processor devices) associated with a fabricator to: apply a printable material to a substrate, the printable material including first particles and second particles suspended in the printable material, the first particles being an insulator material, the second particles being electrically conductive metal material; and cure the printable material on the substrate, the second particles in the cured printable material being transformable into an electrically conductive path via application of heat above a threshold value 
     In accordance with further embodiments, the instructions, when executed by computer processor hardware, cause the computer processor hardware (such as one or more processor devices) associated with a fabricator to: receive a substrate, a first layer of dielectric material disposed on a surface of the substrate, the first layer of dielectric material including first particles and second particles suspended in the first layer of dielectric material, the first particles being an insulator material, the second particles being electrically conductive metal material; and apply heat to a region of the first layer of dielectric material, application of the heat transforming a dielectric material in the region into an electrically conductive path. 
     The ordering of the steps above has been added for clarity sake. Note that any of the processing steps as discussed herein can be performed in any suitable order. 
     Other embodiments of the present disclosure include software programs and/or respective hardware to perform any of the method embodiment steps and operations summarized above and disclosed in detail below. 
     It is to be understood that the method as discussed herein also can be embodied strictly as a software program, firmware, as a hybrid of software, hardware and/or firmware, or as hardware alone such as within a processor (hardware or software), or within an operating system or a within a software application. 
     Additionally, note that although each of the different features, techniques, configurations, etc., herein may be discussed in different places of this disclosure, it is intended, where suitable, that each of the concepts can optionally be executed independently of each other or in combination with each other. Accordingly, the one or more present inventions as described herein can be embodied and viewed in many different ways. 
     Also, note that this preliminary discussion of embodiments herein purposefully does not specify every embodiment and/or incrementally novel aspect of the present disclosure or claimed invention(s). Instead, this brief description only presents general embodiments and corresponding points of novelty over conventional techniques. For additional details and/or possible perspectives (permutations) of the invention(s), the reader is directed to the Detailed Description section and corresponding drawings of the present disclosure as further discussed below. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is an example diagram illustrating manufacture of a printable mixture and use of the printable mixture to fabricate electronic devices according to embodiments herein. 
         FIG. 2  is an example diagram illustrating control information to manufacture a printable mixture according to embodiments herein. 
         FIG. 3  is an example diagram illustrating control information to manufacture a printable mixture according to embodiments herein. 
         FIG. 4  is an example diagram illustrating manufacture of a printable mixture and use of the printable mixture to fabricate electronic devices according to embodiments herein. 
         FIG. 5  is an example graph associated with curing printed dielectric material according to embodiments herein. 
         FIG. 6  is an example photo illustrating sintered dielectric material versus non-sintered dielectric material according to embodiments herein. 
         FIG. 7  is an example diagram illustrating fabrication of conductive paths of different widths in dielectric material according to embodiments herein. 
         FIG. 8  is an example diagram illustrating application of a first magnitude of heat to a layer of dielectric material resulting in fabrication of a corresponding conductive path at a first depth according to embodiments herein. 
         FIG. 9  is an example diagram illustrating application of a second magnitude of heat to a layer of dielectric material resulting in fabrication of a corresponding conductive path at a second depth according to embodiments herein. 
         FIG. 10  is an example diagram illustrating application of a third magnitude of heat to a layer of dielectric material resulting in fabrication of a corresponding conductive path at a third depth according to embodiments herein. 
         FIG. 11A  is an example diagram illustrating deposition of a first layer of dielectric material on a substrate according to embodiments herein. 
         FIG. 11B  is an example diagram illustrating application of first heat to the first layer of dielectric material and fabrication of first conductive paths according to embodiments herein. 
         FIG. 12A  is an example diagram illustrating deposition of a second layer of dielectric material over the first layer of dielectric material according to embodiments herein. 
         FIG. 12B  is an example diagram illustrating application of second heat to the second layer of dielectric material and fabrication of second conductive paths according to embodiments herein. 
         FIG. 13A  is an example diagram illustrating deposition of a third layer of dielectric material on a substrate according to embodiments herein. 
         FIG. 13B  is an example diagram illustrating application of third heat to the third layer of dielectric material and fabrication of third conductive paths according to embodiments herein. 
         FIG. 14  is an example 3D view diagram illustrating a circular capacitor according to embodiments herein. 
         FIG. 15  is an example side view diagram illustrating a circular capacitor according to embodiments herein. 
         FIG. 16  is a diagram illustrating example computer architecture to execute one or more operations according to embodiments herein. 
         FIGS. 17, 18, and 19  are example diagrams illustrating methods according to embodiments herein. 
     
    
    
     The foregoing and other objects, features, and advantages of the invention will be apparent from the following more particular description of preferred embodiments herein, as illustrated in the accompanying drawings in which like reference characters refer to the same parts throughout the different views. The drawings are not necessarily to scale, with emphasis instead being placed upon illustrating the embodiments, principles, concepts, etc. 
     DETAILED DESCRIPTION 
     Embodiments herein include a printed electronics/additive manufacturing approach to fabricate conductive/resistive features on novel insulating dielectric material such as Silver-Barium Strontium Titanate (a.k.a., Ag-BST) printed composite films. For example, a composite functional ink (such as a dielectric liquid ink) as described herein includes a blend of conductive nanoparticle ink and an insulating BST nanoparticle ink. The ratio of metal particles to particles in the final ink is optimized to produce an ink blend that provides an insulating phase after initial curing (such as one or more layers of dielectric material on a substrate) and a conductive/resistive phase following selective laser sintering of the one or more dielectric material layers under ambient conditions. 
     In one embodiment, selective laser sintered Ag-BST resistor components (as derived from a cured one or more layer of dielectric material) show an ohmic behavior and the resistivity could be adjusted by varying the laser sintering parameters, such as the wavelength, power, and/or the rastering speed/pitch of the laser. This insulator (i.e., initial cured dielectric material layer produced from curing the liquid ink) and conversion of one or more regions of the one or more layers of dielectric material to conductor/resistor regions in the dielectric material provides a new path for direct write printed electronics/additive manufacturing applications. In one nonlimiting example embodiment, thermally sintered Ag-BST resistors showed less than 8% variation in resistance between −50° C. and 150° C. 
     Now, more specifically, with reference to the drawings,  FIG. 1  is an example diagram illustrating manufacture of a printable mixture and use of the printable mixture to fabricate electronic devices according to embodiments herein. 
     As shown, manufacturing environment  100  includes control system  140  and fabrication system  155 . 
     In the fabrication stage of manufacturing environment  100 , via control information  146  (see example of component ratios in  FIGS. 2 and 3 ) and control of manufacturing resources  148  (such as valves, conveyors, tubes to deliver material, mixing equipment, agitator equipment, measuring equipment, etc.), the control system  140  produces mixture  152  based on a combination of material such as one or more solvents (liquids) such as solvent  111  (ethylene glycol), solvent  112  (1 methoxy 2 propanol), one or more additives  119  such as dispersant. 
     As further shown, the control system  140  produces mixture  152  to include particles  121  (insulator particles) and particles  122  (such as conductor particles). Thus, to some extent, the control information  146  includes multiple recipes (ratios of different components) to produce different types of mixtures. 
     In accordance with further embodiments, the solvent  111  in the mixture  152  (such as printable dielectric ink) is water-soluble. In one embodiment, the solvent  111  is selected from the glycol family of solvents. In a specific embodiment, the solvent  111  is ethylene glycol. 
     An additive  119  such as dispersant disperses the particles  121  and  122  in the mixture  152 . In one embodiment, the dispersant is or includes Ammonium Polymethacrylate (such as a commercial dispersant by the name NanoSperse S™), which comprises a portion of ammonium polymethacrylate (such as 25% by weight) and a portion of water (such as 75% by weight), although these ratios may vary. 
     Note that any suitable type of particles can be used to fabricate the mixture  152 . For example, in one embodiment, the particles  121  are perovskite oxide particles (such as Barium Strontium Titanate particles or other insulator particles). The particles  121  may be sintered or non-sintered. The particles  122  may be doped. 
     In accordance with further embodiments, the particles  121  are nanoparticles of uniform shape and size. Alternatively, the mixture may include particles  121  of different sizes and shapes. 
     According to further embodiments, the particles  121  have a size distribution with a modal size in the range of 30 nanometers to 2000 nanometers, although the mixture may include particles  121  of any suitable size as previously mentioned. The particles  122  have a size distribution with a modal size in the range of 30 nanometers to 2000 nanometers, although the mixture may include particles  122  of any suitable size as previously mentioned. 
     Note further that the particles  121  can be doped BST particles. Doping can be achieved using any suitable material. In such an instance, the control system  140  produces the pre-mixture  151  to include doped BST nanoparticles. 
     In accordance with further embodiments, the control system  140  controls a ratio of the one or more solvents (such as solvent  111  and/or solvent  112 ) and particles  121  and  122 , etc., such that the final mixture  152  has a viscosity of between 20 and 6000 cp (CentiPoise). Further embodiments herein include fabricating the mixture (such as dielectric ink) to have viscosities of up to 20,000-25,000 cP. Thus, embodiments herein include controlling ratios of components (such as solvents, particles, etc.) to produce a mixture  152  of desirable viscosity. 
     As a more specific example in which PVA (Polyvinyl Alcohol) material is absent from the mixture  152 , the control system  140  includes solvent  111  such as ethylene glycol and solvent  112  such as 1-methoxy-2-propanol in the mixture  152 . The manufacturer controls a viscosity of the mixture  152  based on a ratio of solvent ethylene glycol (having a viscosity of 16 cP) and solvent 1-methoxy-2-propanol (having a viscosity of 1.7 cP) included in the mixture  152 . 
     In one embodiment, the control system  140  controls or adjusts a solvent ratio of these two solvents (such as ethylene glycol and 1-methoxy-2-propanol) in the mixture  152  to obtain a desired viscosity for subsequent fabrication of an electronic device  185 . 
     To produce the final mixture  152  (such as a compound of printable dielectric liquid ink), in accordance with control information  146  (see example of component ratios in  FIGS. 2 and 3 ), the control system  140  combines portions of the pre-mixture  151 , solvent  111 , and solvent  112 . 
     Note that further embodiments herein include including one or more additives  119  in the mixture  152  to further control its properties. For example, in one embodiment the control system  140  controls inclusion of one or more additives  119  in the mixture  152  (dielectric ink). Available additives  119  include material such as: 1-heptane, alpha-terpineol, ethyl cellulose, glycerol, etc. 
     Amounts of the additives  119  included in mixture  152  vary depending on the embodiment. In one embodiment, the mixture  152  is fabricated to include up to 5% (such as by weight) of one or more of the additives  119 . In other embodiments, the control system  140  produces the mixture  152  such that less than 1% (such as by weight) of the final mixture  152  is made up of one or more additives  119 . 
     As further shown in  FIG. 1 , fabrication system  155  receives and uses the final mixture  152  to fabricate the electronic device  185 . For example, in one embodiment, the fabrication system  155  includes a printer device  180  that control application of the mixture  152  (such as a printable dielectric ink) and, thus, fabrication of the electronic device  185 . A heat source (such as oven, hot plate, conveyer belt, etc.) of fabrication system  155  cures the liquid mixture  152  into a solid layer of dielectric material  270 . In one embodiment, a hot plate applied to a bottom of the substrate  250  surface heats the liquid mixture  152  to cure it into the layer of dielectric material  270 . 
     As further discussed herein, note that the quantity of components (such as amount/ratio of solvents, particles  130 , etc.) can be controlled to facilitate application of the mixture  152  (such as printable ink) in different ways. For example, as further discussed below, different mixtures as described herein can be applied via printer device  180  such as dispensing device, aerosol jet, inkjet, etc., depending on the makeup of the respective mixture  152 . Thus, embodiments herein include controlling ratios of material (components) included in the mixture to support different types of printing technology and applications. 
     Thus, in one example embodiment, a compound mixture  152  comprises: first particles  121 , the first particles  121  being an insulator material (non-electrically conductive material); second particles  122 , the second particles  122  being electrically conductive material; and a combination of the first particles  121  and the second particles  122  distributed and suspended in a printable material (i.e., mixture  152 ) in which a cured state (solid of near solid) of the printable material (mixture  152 ) is transformable into one or more electrically conductive paths via application of heat above a threshold value. 
     In accordance with further embodiments, the second particles  122  are fabricated from electrically conductive material such as metal. In one embodiment, the particles  122  are silver (Ag) particles. In a yet further embodiment, a ratio of the particles  122  to the particles  121  is approximately 62.5 to 37.5 by weight in the mixture. That is, in one embodiment, 62.5% (+/−5%) of all the particles in mixture  152  are particles  122 ; in one embodiment, 37.5% (+/−5%) of all the particles in mixture  152  are particles  121 . Additionally, or alternatively, the second particles  122  are Barium Strontium Titanate (BST) particles. 
     In one embodiment, 62.5% (+/−5%) of all the particles in layer of dielectric material  270  (cured mixture  152 ) are particles  122 ; in one embodiment, 37.5% (+/−5%) of all the particles in the layer of dielectric material  270  (cured mixture  152 ) are particles  121 . 
     In still further embodiments, a melting point of the second particles  122  is lower than a melting point of the first particles  121 . 
     A ratio of the first particles  121  to second particles  122  can vary depending on the embodiment. In one embodiment, a ratio of the first particles  121  to the second particles  122  is selected such that a group of the second particles  122  in the cured printable material (layer of dielectric material  270 ) are substantially isolated from each other (such as not touching each other so as not to form a continuous conductive path) prior to application of heat to the group of second particles  122  above a threshold value. 
     As further discussed herein, heating the cured printable material (layer of dielectric material  270  in electronic device  185 ) to a temperature above a threshold value causes the heated second particles  122  (such as silver or other suitable material) to contact/connect each other due to the sintering of respective particles  122  (such as silver nanoparticles) forming conductive paths. 
     Further embodiments herein include exposure of the dielectric material (cured printable material) to heat. In one embodiment, exposure of the dielectric layer of material  270  to heat above the threshold value causes contact amongst the second particles  122  in the group due to the sintering of silver nanoparticles; the heat converts a portion of the cured printable material into an electrically conductive path. 
     In accordance with further embodiments, the second particles  122  are silver nanoparticles; the first particles  121  are BST nano particles. The compound (mixture  152 ) includes at least one solvent such as 1-methoxy-2-propanol and/or ethylene glycol. In one embodiment, the compound (mixture  152 ) is made up of more than 40% by weight of ethylene glycol. 
     In yet further embodiments, the first particles  121  make up approximately 12.5% of the compound (mixture  152 ) by weight; the second particles  122  make up approximately 21% of the compound (mixture  152 ) by weight; and the mixture of one or more solvents makes up approximately 66.5% of the compound (mixture  152 ) by weight prior to curing of the mixture  152  into the layer of dielectric material  270 . Subsequent to curing, when the solvents in the printable material evaporate, the cured printable material comprises between 60-70% of first particles and 30-40% of second particles. 
     Further embodiments herein, via controller  140  and mixing resources  148 , include a method comprising: receiving first particles  121 , the first particles  121  being an insulator material; receiving second particles  122 , the second particles  122  being electrically conductive metal material; and suspending a combination of the first particles  121  and the second particles  122  in a printable liquid slurry (mixture  152 ) in which a subsequent cured state of the printable material (mixture  152 ) is transformable into one or more electrically conductive paths via application of heat above a threshold value. 
     Further embodiments herein include, via controller  140  and the mixing resources  148 , controlling a ratio of mixing the first particles  121  to the second particles  122  in the printable material (mixture  152 ) such that a group of the second particles  122  in a layer of the printable material are isolated from each other (such as non-touching) prior to application of heat to the group of second particles above a threshold value. Subsequent exposure of the cured printable material (layer of dielectric material  270 ) to heat above the threshold value causes contact amongst the second particles  122  in the group due to the sintering of particles  122 , the heat converting a portion of the dielectric layer of material into an electrically conductive path. More specifically, the area of the printed layer which was exposed to the heat (such as from a laser or other suitable resource) will convert the insulator into the electrically conductive path. 
       FIG. 2  is an example diagram illustrating control information to manufacture a printable mixture according to embodiments herein. 
     In one embodiment, the control system  140  fabricates the mixture  152  via combining two or more liquid mixtures. For example, in one embodiment, the control system  140  receives and/or produces a first liquid mixture to include 18.4% (by weight) of insulative particles  121 , 0 percent (by weight) of conductive particles  122 , 68.2 percent (by weight) of solvent #1 (such as ethylene glycol), 12.7 percent of solvent  112  such as 1-methoxy 2-propanol), and 0.7 percent of dispersant. 
     The control system  140  receives and/or produces a second liquid mixture to include 0.0% (by weight) of insulative particles  121 , 63 percent (by weight) of conductive particles  122 , 14 percent (by weight) of solvent #1 (such as ethylene glycol), 21.0 percent of solvent  112  such as 1-methoxy 2-propanol), and 2.0 percent of dispersant. 
     In one embodiment, the control system  140  combines 2 parts of mixture #1 to 1 part of the mixture #2 to produce the liquid (printable) mixture  152 . In such an instance, final liquid mixture includes 12.2% (by weight) of insulative particles  121 , 21 percent (by weight) of conductive particles  122 , 49.9 percent (by weight) of solvent #1 (such as ethylene glycol), 15.5 percent of solvent  112  such as 1-methoxy 2-propanol), and 1.13 percent of dispersant. 
     Note that the ratio of mixing the first mixture #1 and the second mixture #2 can vary depending on the embodiment. For example, the first liquid mixture #1 can comprise between 28 and 38% percent by weight of the final liquid mixture. The second liquid mixture #2 can comprise between 72 and 62% percent by weight of the final liquid mixture. 
     In a manner as previously discussed, the final mixture  152  is printable on a respective substrate. After curing, the remaining layer of dielectric material  270  on the substrate  250  comprises 36.7% (by weight) of insulative particles  121 , 61.5 percent (by weight) of conductive particles  122 , 0 percent (by weight) of solvent #1 (such as ethylene glycol), 0 percent of solvent  112  (such as 1-methoxy 2-propanol), and 0 percent of dispersant. Note that the remaining layer of dielectric material may include some amount of reside material associated with the evaporated material (such as solvents, dispersant, etc.). 
     Further Embodiments 
     In additive manufacturing (a.k.a., AM), printing circuits can be complicated due to the need of multiple types of inks. Usually, two types of functional inks are used to print conductive/resistive parts and insulator/dielectric parts. However, the use of two different functional inks create additional challenges, such as larger device footprint, incompatibility of conductive and dielectric inks, and incompatible curing/sintering procedures. Devices made using AM techniques require dimensional control for device functionality, especially for discrete structures used for applications in the radio (RF) and microwave (MW) frequencies, and higher. Printing capabilities and dimensional control depend on the ink composition and the printing method; therefore, development of functional inks that can be used in printed/additively manufactured devices is a significant and necessary step to advance this technology. 
     Non-contact direct-write printing technologies such as aerosol jet printers are suited to print fine features as small as 10 μm however, it is necessary to have highly optimized functional inks to achieve consistent printed fine features. Functional inks can be developed and optimized for one or very few printing technologies and for very few substrates due to viscosity and surface energy limitations. Different printing technologies utilize inks of varying viscosities. Therefore, an optimized functional ink for one application cannot be directly used in another application that may needs high precision resolution of printed lines. 
     For example, printing consecutive resistors and insulators with line widths and separations of less than 50 μm is very challenging when using two different functional inks. The best solution to this problem is to develop a functional ink that can be converted from the insulating phase to the conductive phase by an external stimulation at ambient conditions. Insulator to metal transitions of some materials, such as vanadium oxide, have already been reported. Vanadium oxide can switch between an insulating phase and a metallic phase depending on the operating temperature. However, a functional ink that transitions from an insulator to a conductor phase in unregulated ambient conditions (room temperature such as between 5-40 degree Celsius, atmospheric pressure) has not been reported. Embodiments herein include a functional ink that transitions from an insulator to a conductor phase in ambient conditions (or low temperature curing). For example, embodiments herein include utilizing a laser (or other suitable heat source) to melt/sinter conductive nanoparticles (particles  122 ) to create conductive paths in a composite nanoparticle film (layer of dielectric material  270 ) comprised of both conductive (resistive) and non-conductive nanoparticles. This changes three-dimensional physical morphology of the laser exposed areas of composite film without changing the intrinsic properties of either conductive or non-conductive nanoparticles. In order to achieve this, embodiments herein include a novel functional ink (mixture  152 ) formulated with a blend of conductive and non-conductive nanoparticles. Conductive paths are not formed in the films (one or more layers of dielectric material  270 ) before the laser sintering to assure that the material is in the insulating state; however, during the laser sintering process in which heat is applied, conductive nanoparticles  122  create conductive paths due to increase of grain sizes and the melting/reflowing of conductive nanoparticles, creating a resistive/conducting material. 
     Thus, embodiments herein include a novel silver-barium strontium titanate (Ag-BST) composite nanoparticle ink for the additive fabrication of various devices. This Ag-BST composite material is converted from an insulating phase to a conductive phase by the selective laser sintering (SLS) of silver nanoparticles. Moreover, this Ag-BST composite nanoparticle ink can be used as a conventional resistive ink for additive manufacturing and the ink was tested for dispensing printers. Fully thermally sintered resistors showed a less than ±8% variation of the resistance between −50° C. and 150 degree C. By way of non-limiting example, these printed resistors can handle up to 1 Watt or more depending on a size of the respective electronic device. 
     2. Materials and Methods 
     2.1 List of Materials 
     In one embodiment, barium strontium titanate (Ba0.67Sr0.33TiO3—ratio of 2 parts barium to 1 part strontuim to 3 parts titanium to 6 parts oxygen) nanoparticles and ammonium polymethacrylate in water (commercial name—NanoSperse S) are available from TPL Inc., New Mexico, USA. Ethylene glycol (99%) is avail from Fisher Scientific, USA. 1-Methoxy-2-propanol (99.5%) is available from Sigma-Aldrich, USA. Paru MicroPE PG-007 silver nanoparticle ink (˜63% by weight) is available from Pam Co., Ltd., South Korea. Kapton general purpose polyamide films are available from DuPont, USA. 
     2.2 Ag-BST Ink Formulation Procedure 
     In one embodiment, the mixture  152  (such as an Ag-BST blended ink) is formulated by blending, via control system  140  and fabrication resources  148 , a custom formulated barium strontium titanate (BST) nanoparticle ink (such as mixture #1) and a commercially available PARU silver nanoparticle ink (such as mixture #2). BST nanoparticles (50 wt. %) are added into ethylene glycol and sonicated for 8 hours in the pulse mode (active=15 seconds, inactive=59 seconds) using a QSONICA Q500 ultrasonic processor with a 2 mm micro tip. Then, ammonium polymethacrylate in water (˜2 wt. %) is added into the mixture as a dispersant and sonicated for another 30 minutes in the pulse mode (active=5 seconds, inactive=59 seconds) to make a BST slurry. Then, ethylene glycol (˜49.8% by weight) and 1-methoxy-2-propanol (˜12.7% by weight) are added to the BST nanoparticle 6 slurry and the mixture is magnetically stirred at 400 rpm overnight to get a homogeneous BST nanoparticle ink. Then, different amounts of the BST nanoparticle ink and the silver nanoparticle ink are blended and magnetically stirred overnight to get different Ag-BST ink formulations with different silver nanoparticle loadings. 
     2.3 Ag-BST Ink Printing and Curing Procedure 
     In accordance with further embodiments, the printer device  180  prints the mixture  152  (such as Ag-BST ink) using the Nordson 3-axis automatic dispensing system with a 150 μm tip. In one embodiment, the air pressure is set up to 10 psi (pounds per square inch) to dispense the mixture  152  from a syringe (volume of liquid). In still further example embodiments, the pitch size used is 100 μm during the rastering of large features, which allowed an overlap of the previously printed lines. 
     The printing speed was changed accordingly to adjust the thickness of the layer. In one embodiment, Kapton polyamide films are used as the substrate  250  for printing the mixture  152 . In accordance with further example embodiments, the silver pads for Ag-BST resistors were printed using the same dispensing system with a 100 μm tip. The silver pads were printed and cured at 250° C. in vacuum oven for 3 hours before printing the Ag-BST ink between the silver pads. The printed Ag-BST features were initially cured at 80 degree C. for 30 minutes on a hotplate before laser sintering. 
     2.3 SLS of Ag-BST 
     After the initial curing of the fabricated mixture  152  on substrate  250 , the corresponding electronic device  185  is exposed to 80 degree C. temperature for 30 minutes. Then, SLS allows fabrication of customized conductive patterns at room temperature to be created and the resistances of the patterns can be adjusted by changing the laser sintering parameters. In one embodiment, the laser material is laser sintered via an 830 nm (nanometer) continuous wave (CW) laser in an Optomec AJ5X aerosol jet printer. The approximate laser spot size was around 70 μm in diameter, which was measured using a photo paper. Nitrogen gas is used as a shield gas for the laser to prevent the oxidation of the silver nanoparticles during laser sintering. 
     The laser power, rastering pitch, and rastering speed associated with the signal  231  (fabrication signal such as optical signal or optical pulses, convection signal, radiation signal, etc.) can be adjusted to produce electronic devices having a range of resistivities. In addition, note that the 405 nm continuous wave (CW) laser in the Heidelberg μPG  101  laser writer with a laser spot size of 2 μm was used to selectively laser sinter high precision conductive patterns and the laser power and the rastering speed were adjusted in order to get different resistivities. 
     2.4 Characterization Techniques 
     In accordance with further example embodiments, an Agilent Cary 8454 UV/Vis/NIR Spectrophotometer was used for UV-Vis absorption measurements of liquid inks. A Keyence VHX-5000 digital microscope was used for the initial investigation of the cracks after the curing. TA instruments ARES-G2 rheometer was used to measure the viscosities of the inks. Ink samples were loaded in a 400 mm diameter, 0.04 rad stainless-steel cone and plate geometry. Flow sweeps from 1 s-1 to 100 s-1 were recorded at 25° C. using an Advanced Peltier System for temperature control. Raman scattering spectra were obtained using a Raman microscope (Senterra II; Bruker) with a 532 nm laser, a power of 2 mW, an integration time of 1 second, and two co-additions; mapping was carried out by obtaining 300 to 330 spectra in a grid pattern spaced at least 10 μm apart. The resistors were probed using the DC needles of an MPI TS2000-SE probe station with an ERS thermal chuck. Keithley 4200 semiconductor parametric analyzer was used to record the current-voltage curves for laser and thermally sintered Ag-BST resistors. The voltage was swept from −1 V to +1 V. The resistance was calculated using the slope of the current vs voltage line. Sheet resistances were measured using the Pro4-4400 Four Point Resistivity System (Signatone) measurement system. The scanning electron microscopy images were obtained using a Zeiss Auriga Focused Ion Beam-Scanning Electron Microscope (FIB-SEM), which was operated at 5 keV. A gallium liquid metal ion source at 30 kV and 50 pA was used for FIB milling to investigate the cross sections of the printed features. 
     3. Results and Discussion 
     3.1 Ag-BST Blended Ink Formulation 
     In accordance with further example embodiments, the mixture  152  is a silver-barium strontium titanate (Ag-BST) blended ink, which can convert printed Ag-BST layers from an insulating phase to a conductive phase by the SLS of silver nanoparticles. SLS can be used to make customized conductive patterns on initially cured (insulating phase) Ag-BST layers. Ag and BST were identified as the candidate conductive and nonconductive materials due to the following reasons. Silver has the highest conductivity of bulk materials and Ag nanoparticles are widely used in conductive inks for printed electronics. In addition, silver nanoparticles can be sintered at lower temperatures due to the melting point depression and compatibility with sintering techniques such as laser, photonic, and chemical sintering. Barium strontium titanate was used as the non-conductive material because of its appropriate dielectric properties (high dielectric constant and low loss tangent) for RF and microwave applications, high melting point (over 1000 degree C.), high dielectric breakdown voltage and the minimal interaction with silver nanoparticles. Even though investigating the dielectric properties of Ag-BST at the insulating phase is not in the scope of this work, dielectric properties of BST will be useful to fabricate selective laser-sintered RF and microwave devices on Ag-BST. 
     Embodiments herein a correct blending ratio of the conductive material (particles  122 ) and the non-conductive material (particles  121 ) to ensure the cured material (layer of dielectric material  270 ) is insulating after the initial curing of same. Portions of the layer of dielectric material  270  are conductive after application of sufficient heat. 
     In one embodiment, in order to find the correct blending ratio, a series of blended Ag-BST ink samples were prepared. The table  300  in  FIG. 3  shows the blending composition of the 5 different Ag-BST inks along with the conditions of the inks after the initial curing and thermal sintering. The composition of silver and BST nanoparticles after the thermal sintering can be found in the supplementary information. The amount of BST was increased in the blended ink samples until the insulating phase of the printed samples was achieved after the initial curing. A 10 by 10 mm features of each ink sample was printed on Kapton substrates using the dispensing printer, followed by the initial curing at 80° C. for 30 minutes. Inks 1 and 2 showed conductivity after the initial curing and ink 3, 4 and 5 showed an insulating phase after the initial curing procedure. Then thermal sintering was performed at 250° C. for 3 hours in a vacuum oven to find the final resistivity of each Ag-BST ink sample. 
     With respect to table  300  in  FIG. 3 , inks 1 and 2 showed a decrease in the resistivity after thermal sintering (data not shown). Ink 3 transitioned to the conductive phase from the insulator phase after the completion of thermal sintering. Ink 3 shows around 329 times higher resistivity compared to the pure silver ink; therefore, it can be used as a conventional resistive ink to print resistors. Inks 4 and 5 did not show any conductivity even after the thermal sintering. It was deduced that inks 4 and 5 did not have enough silver nanoparticles to create conductive paths during the sintering process. Therefore, the blending ratio of ink 3 (such as mixture  152 ) was concluded as the optimized ratio for the Ag-BST insulator to conductor conversion and all further experiments were conducted with the Ag-BST ink 3. The Ag-BST ink which shows the conversion from the insulating phase to the conductive phase consists of approximately 67% (+/−5%) by weight of the BST nanoparticle ink and 33% (+/−5%) by weight of the silver nanoparticle ink. 
     In one embodiment, the dynamic viscosity of the mixture  152  was relatively constant over the tested shear rates, which indicates that the blended ink is stable without large agglomerated nanoparticles clusters. Larger agglomerated nanoclusters degrade the printing quality, decrease the adhesion, and result in high surface roughness. UV-Visible absorption spectra for the silver ink, BST ink and the Ag-BST ink can be seen in supplementary information. The absorption maximum of the Ag-BST ink is located around 430 nm and it can be assigned to the surface plasmon resonance frequency of silver nanoparticles. 
     3.2 SLS of Ag-BST Blended Ink 
     SLS is a commonly used technique in additive manufacturing to sinter/melt powdered materials using high power lasers to create 3D objects. However, according to embodiments herein, SLS was used to create conductive patterns on Ag-BST insulating films. Dispensing, spin coating and doctor blading can be used to deposit Ag-BST blended ink and all the Ag-BST films for this work were printed using the Nordson automatic dispensing system. The printed Ag-BST wet films were cured at 80° C. for 30 minutes to evaporate the solvents and other ink additives. No conductivity was observed after the initial curing due to the homogeneously distributed of separated silver nanoparticles, confirming the insulating phase of the ink. Then, this insulating Ag-BST film was exposed to the programmable laser to pattern 
     According to the proposed sintering mechanism (such as application of heat) as described herein, silver nanoparticles (particles  122 ) are sintered under the laser heat exposure and create conductive paths due to increase in the grain size of particles  122  and the reflowing of melted particles  122  (such as silver nanoparticles). The surface morphology changes due to the laser sintering are shown in  FIG. 6 . However, BST nanoparticles (particles  122 ) remain unchanged due to the high melting point and the higher bandgap. 
     In one embodiment, selective laser-sintered resistors are fabricated between two silver printed contact pads, which were used to probe the resistors to measure the resistance. The selective laser-sintered resistors are clearly visible due to the color change because of the sintering of Ag nanoparticles. The resistivity of the laser-sintered particles  122  (such as Ag-BST) depends on the laser sintering parameters such as wavelength, power, rastering speed and the rastering pitch. Embodiments herein include use of an 830 nm inbuilt continuous wave (CW) laser in the Optomec AJ5X aerosol jet printer. In addition, 405 nm CW laser of the Heidelberg μPG  101  laser writer can be used to laser sinter the layer of dielectric material  270 .  FIG. 4  is an example diagram illustrating creation of conductive paths on a printed layer of dielectric material  270  as further discussed below. 
     Raman spectra were used to investigate the sintering mechanism of the Ag-BST resistors. Surface-enhanced Raman scattering (SERS) takes place on the surface of some metallic nanostructures and is caused by the local excitation of surface plasmons. This technique allows for the detection of low concentrations of organic molecules located on the surface of silver nanoparticles. SERS was used to assess the laser-sintered surface of the Ag-BST films. Initial investigations indicated that the regions not exposed to the laser produced Raman spectra with peaks associated with residual organic molecules. The peaks varied with each spectrum, and therefore, were not used to identify the composition of the residual organic molecules. According to  FIG. 4 , three major regions (non-laser-sintered, transition, and laser-sintered) were identified by integrating the averaged amorphous carbon peaks located between 1000 and 1800 cm-1. The relatively high intensity peak found in the transition region can be attributed to the incomplete decomposition of organic molecules caused by heat diffusion from the laser-sintered region. The laser-sintered area did not show a significant amount of scattering associated with amorphous carbon, which indicates the decomposition of organic residuals; however, it is not clear if the lack of peaks associated with Raman scattering is due to the complete removal of organic compounds or a decrease in the enhancement factor that is caused by particle sintering and enlarging. 
     In addition to the 830 nm CW laser inbuilt in the Optomec AJ5X aerosol jet printer, 405 nm CW laser of the Heidelberg μPG  101  laser writer was used to laser sinter fine features.  FIG. 5 a    shows the laser-sintered Ag-BST resistors with laser-sintered contact pads for probing. The resistors showed a 12.1 kΩ (6 mm of length) and the line width was around 25 μm. The linewidth was consistent for all 5 laser-sintered resistors which confirmed the ability of laser sintering to produce precise fine features. Also, cleaner edges (low edge roughness) were observed compared to printed resistors. Please see the supplementary information (ESI Figure S12) for the SEM images of the edges of the laser-sintered resistors. The SEM images in  FIGS. 5 b  and 5 c    show the surface morphology of the Ag-BST film before and after laser sintering. The increase in the grain size of Ag nanoparticles can be observed after the laser sintering and some of the grains are over 1 μm in diameter. The efficient sintering of Ag nanoparticles can be attributed to the localized plasmonic heating effects of the Ag nanoparticles. Ag-BST shows the maximum absorption with a broad peak around 430 nm due to the surface plasmon resonance of Ag nanoparticles. This broad peak conveniently resonates with the 405 nm laser, which generates local heating and leads to the efficient sintering of Ag nanoparticles. Lasers which have wavelengths away from the absorption maximum of the Ag nanoparticles need to use a higher power for sintering due to the lack of localized plasmonic heating. 
     3.3 Thermally Sintered Ag-BST Resistors 
     In addition to patterning the conductive traces by SLS, Ag-BST blended ink can be used as a conventional resistive ink for additive manufacturing/printed electronics. This Ag-BST blended ink is optimized for the Nordson automatic dispensing printer and suitable to print resistive features with a linewidth higher than 100 μm. The line resistors were printed with silver pads for probing to test the temperature stability of the thermally sintered resistors. Printed resistors were thermally sintered at 250° C. for 3 hours under vacuum in a box oven. 
     In yet further example embodiments, the component in the mixture  152  of Ag-BST13 before the curing:
         1. Silver nanoparticles=21% by weight   2. BST nanoparticles=12.5% by weight   3. Ethylene glycol=51% by weight   4. 1-Methoxy-2-Propanol=15.5% by weight   The component of Ag-BST13 after the curing (i.e., dielectric material  270 ) in which Ethylene glycol and 1-Methoxy-2-Propanol are evaporated from the mixture  152  is:   1. Silver (metal) nanoparticles=62.5% (or in the range 55% to 70%) by weight   2. BST nanoparticles=37.5% (or in the range 30% to 45%) by weight       

     In one embodiment, as previously discussed, the Ethylene glycol and 1-Methoxy-2-Propanol evaporates during the curing process such that the remaining layer of dielectric material  270  is a solid compound of metal particles and insulator particles. 
       FIG. 4  is an example diagram illustrating transformation of dielectric material into a conductive path according to embodiments herein. 
     In this example embodiment, the fabricator  240  fabricates a respective resistor (device  210 ) between node  221  and node  222 . As previously discussed, the fabricator  240  disposes the dielectric material  270  over the substrate  250 . After curing, the fabricator  240  controls the source  230  (such as laser) to produce the signal  231  (such as optical signal, convection signal, etc.) applied to the layer of dielectric material  270 . The layer of dielectric material  270  includes region  250 - 1  (cured mixture  152 ) in which the insulator particles  121  (interlaced with particles  122 ) generally prevent the particles  122  from forming a respective low resistance path between the node  221  and the node  222 . 
     Via application of the signal  231  (such as optical or laser signal at any suitable wavelength such as 405 nanometers, 830 nanometers, etc.), the fabricator  250  converts the dielectric material  270  into a respective conductive path  260 . As shown in region  250 - 2 , the dielectric material is converted into a conductive path  260  via the sequential contacting of the (metal) particles  122  to each other to form a low impedance path. As previously discussed, application of signal  231  causes reflow/sintering as well as connectivity of the particles  122 . In one embodiment, the particles  122  contact each other via necking, sintering, etc. 
       FIG. 5  is an example graph associated with curing of the printed dielectric material according to embodiments herein. 
     As shown, the weight of the mixture  152  changes as it is exposed to heat during curing. For example, exposure of the mixture  152  to a temperature of greater than 20 and less than 150 degree Celsius causes the 1-methoxy 2-propanol and ethylene glycol to be evaporated from the mixture  152 . Between 100 and 200 degrees Celsius, the amounts of surfactant associated with the layer of diametric material  270  decreases. 
       FIG. 6  is an example photo illustrating sintered dielectric material versus non-sintered dielectric material according to embodiments herein. 
     As previously discussed, the fabricator applies heat to a portion of the cured mixture (layer of dielectric material) resulting in creation of conductive path  260  in dielectric material  270 . 
       FIG. 7  is an example diagram illustrating fabrication of different width of conductive paths in dielectric material forming different resistor values according to embodiments herein. 
     In this example embodiment, the fabricator  240  fabricates the electronic device  185 - 1  (such as resistor R 1 ) to include conductive path  260 - 1  in dielectric material  270  along the Y-axis via application of a first laser beam (which is orthogonal to the x-axis and y-axis) between the node  721 - 1  and the node  722 - 1 . A width of the conductive path  260 - 1  as measured in the x-axis dictates a resistance of the electronic device  185 - 1  (resistor R 1 ). 
     The fabricator  240  fabricates the electronic device  185 - 2  (such as resistor R 2 ) to include conductive path  260 - 2  in dielectric material  270  along the Y-axis via application of a second laser beam (which is orthogonal to the x-axis and y-axis) between the node  721 - 2  and the node  722 - 2 . A width of the conductive path  260 - 2  as measured in the x-axis dictates a resistance of the electronic device  185 - 1  (resistor R 2 ). 
     The fabricator  240  fabricates the electronic device  185 - 3  (such as resistor R 3 ) to include conductive path  260 - 3  in dielectric material  270  along the Y-axis via application of a second laser beam (which is orthogonal to the x-axis and y-axis) between the node  721 - 3  and the node  722 - 3 . A width of the conductive path  260 - 3  as measured in the x-axis dictates a resistance of the electronic device  185 - 3  (resistor R 3 ). 
     In this example embodiment, assume that each of the conductive paths  260  is the same depth in the z-axis. In such an instance, the wider the (electrically) conductive path  260 , the lower the resistance. For example, the magnitude of the resistor R 3  is less than the magnitude of the resistor R 2 ; the magnitude of the resistor R 2  is less than the magnitude of the resistor R 1 . 
     As further discussed herein, a depth of the respective conductive path fabricated in the layer of dielectric material  270  can vary depending on an amount of heat associated with signal  231 - 1  as shown in  FIGS. 8, 9, and 10 . 
     More specifically,  FIG. 8  is an example diagram illustrating application of a first magnitude of heat to a layer of dielectric material resulting in fabrication of a corresponding conductive path at a first depth according to embodiments herein. 
     As shown in this example embodiment, the fabricator  240  controls source  230 , which applies signal  231 - 1  at power level P 1  to the dielectric material  270  on substrate  850  of the electronic device  185 - 4 . Application of the signal  231 - 1  results in generation of the conductive path  860  having depth Dl. The deeper the conductive path in the dielectric material  270 , the lower the resistance. 
       FIG. 9  is an example diagram illustrating application of a second magnitude of heat to a layer of dielectric material resulting in fabrication of a corresponding conductive path at a second depth according to embodiments herein. 
     As shown in this example embodiment, the fabricator  240  controls source  230 , which applies signal  231 - 2  at power level P 2  to the dielectric material  270  on substrate  950  of the electronic device  185 - 4 . Application of the signal  231 - 1  results in generation of the conductive path  960  having depth Dl. The deeper the conductive path in the dielectric material  270 , the lower the resistance. Accordingly, the resistance of the conductive path  960  is less than the resistance of the conductive path  860 . 
       FIG. 10  is an example diagram illustrating application of a third magnitude of heat to a layer of dielectric material resulting in fabrication of a corresponding conductive path at a third depth according to embodiments herein. 
     As shown in this example embodiment, the fabricator  240  controls source  230 , which applies signal  231 - 3  at power level P 3  to the dielectric material  270  on substrate  850  of the electronic device  185 - 4 . Application of the signal  231 - 1  results in generation of the conductive path  860  having depth Dl. The deeper the conductive path in the dielectric material  270 , the lower the resistance. Accordingly, the resistance of the conductive path  1060  is less than the resistance of the conductive path  960 . 
     The combination of  FIGS. 11A, 11B, 12A, 12B, 13A, and 13B  illustrate 3-dimensional fabrication of a respective electronic device according to embodiments herein. 
       FIG. 11A  is an example diagram illustrating deposition of a first layer of dielectric material on a substrate according to embodiments herein. 
     As shown in  FIG. 11A , the fabrication system  155  applies and cures layer of dielectric material  270  (a.k.a., layer #1) on the substrate  250  in a manner as previously discussed. 
       FIG. 11B  is an example diagram illustrating application of first heat to the first layer of dielectric material and fabrication of first conductive paths according to embodiments herein. 
     As shown in  FIG. 11B , the fabricator  240  applies signal  231 - 1  to the dielectric material  270  in layer #1 to create conductive path  1160  and conductive path  1161  (such as a via). In one embodiment, via application of sufficient heat, the conductive path  1161  extends between a top surface of the layer #1 and the bottom surface of the layer #1. Accordingly, the conductive path  1161  provides connectivity between layers. 
       FIG. 12A  is an example diagram illustrating deposition of a second layer of dielectric material over the first layer of dielectric material according to embodiments herein. 
     As shown in  FIG. 12A , the fabrication system  155  applies and cures (via exposure to heat) a second layer of dielectric material  270  (a.k.a., layer #2) on the layer #1. 
       FIG. 12B  is an example diagram illustrating application of second heat to the second layer of dielectric material and fabrication of second conductive paths according to embodiments herein. 
     As shown in  FIG. 12B , the fabricator  240  applies signal  231 - 1  to the dielectric material  270  in layer #2 to create conductive path  1260  (such as a via) and conductive path  1261 . In one embodiment, via application of sufficient heat, the conductive path  1260  extends between a top surface of the layer #2 and the bottom surface of the layer #2 to conductive path  1160 . 
       FIG. 13A  is an example diagram illustrating deposition of a third layer of dielectric material on a substrate according to embodiments herein. 
     As shown in  FIG. 13A , the fabrication system  155  applies and cures a third layer of dielectric material  270  (a.k.a., layer #3) on the layer #2 of dielectric material  270 . 
       FIG. 13B  is an example diagram illustrating application of third heat to the third layer of dielectric material and fabrication of third conductive paths according to embodiments herein. 
     As shown in  FIG. 13B , the fabricator  240  applies signal  231 - 1  to the dielectric material  270  in layer #3 to create conductive path  1360  (such as a via) and conductive path  1361 . In one embodiment, via application of sufficient heat, the conductive path  1360  extends between a top surface of the layer #3 and the bottom surface of the layer #3 to conductive path  1261 . 
       FIG. 14  is an example 3D view diagram illustrating an electronic device according to embodiments herein. 
     In this example embodiment, a layer of dielectric material is deposited on a surface of the substrate  1450  (such as an insulator material, flexible or rigid). The fabricator applies heat to the layer of dielectric material to produce the conductor  1411  (first electrode of the electronic device  185 - 10 ) and conductor  1412  (second electrode of the electronic device  185 - 10 ). Dielectric material  1421  is disposed between conductor  1411  and conductor  1412 . 
       FIG. 15  is an example side view diagram of the electronic device  185 - 10  (such as cylindrical capacitor) according to embodiments herein. 
       FIG. 16  is an example block diagram of a computer system for implementing any of the operations as previously discussed according to embodiments herein. 
     Any of the resources (such as mobile communication devices, wireless access points, wireless stations, wireless base stations, communication management resource, bandwidth management resource, etc.) as discussed herein can be configured to include computer processor hardware and/or corresponding executable instructions to carry out the different operations as discussed herein. 
     As shown, computer system  1650  of the present example includes an interconnect  1611  coupling computer readable storage media  1612  such as a non-transitory type of media (which can be any suitable type of hardware storage medium in which digital information can be stored and retrieved), a processor  1613  (computer processor hardware), I/O interface  1614 , and a communications interface  1617 . 
     I/O interface(s)  1614  supports connectivity to repository  1680  and input resource  1692 . 
     Computer readable storage medium  1612  can be any hardware storage device such as memory, optical storage, hard drive, floppy disk, etc. In one embodiment, the computer readable storage medium  1612  stores instructions and/or data. 
     As shown, computer readable storage media  1612  can be encoded with management application  140 - 1  (e.g., including instructions) to carry out any of the operations as discussed herein. 
     During operation of one embodiment, processor  1613  accesses computer readable storage media  1612  via the use of interconnect  1611  in order to launch, run, execute, interpret or otherwise perform the instructions in management application  140 - 1  stored on computer readable storage medium  1612 . Execution of the management application  140 - 1  produces management process  140 - 2  to carry out any of the fabrication operations and/or processes as discussed herein. 
     Those skilled in the art will understand that the computer system  1650  can include other processes and/or software and hardware components, such as an operating system that controls allocation and use of hardware resources to execute management application  140 - 1 . 
     In accordance with different embodiments, note that computer system may reside in any of various types of devices, including, but not limited to, a mobile computer, a personal computer system, wireless station, connection management resource, a wireless device, a wireless access point, a base station, phone device, desktop computer, laptop, notebook, netbook computer, mainframe computer system, handheld computer, workstation, network computer, application server, storage device, a consumer electronics device such as a camera, camcorder, set top box, mobile device, video game console, handheld video game device, a peripheral device such as a switch, modem, router, set-top box, content management device, handheld remote control device, any type of computing or electronic device, etc. The computer system  1650  may reside at any location or can be included in any suitable resource in any network environment to implement functionality as discussed herein. 
     Functionality supported by the different resources will now be discussed via flowcharts in  FIGS. 17, 18, and 19 . Note that the steps in the flowcharts below can be executed in any suitable order. 
       FIG. 17  is an example diagram illustrating a method according to embodiments herein. 
     In processing operation  1710 , the control system  140  receives first particles  121  such as insulator material. 
     In processing operation  1720 , the control system  140  receives second particles  122  such as electrically conductive metal material. 
     In processing operation  1730 , the control system  140  suspends a combination of the first particles  121  and the second particles  122  in a printable material (such as mixture  152 ) in which a cured state of the printable material is transformable into an electrically conductive material via application of heat above a threshold value. 
       FIG. 18  is an example diagram illustrating a method according to embodiments herein. 
     In processing operation  1810 , the fabrication system  155  applies a printable material (a mixture  152 ) to a substrate  250 . The printable material (mixture  152 ) includes first particles  121  and second particles  122  suspended in the printable material. In one embodiment, the first particles  121  is an insulator material; the second particles is electrically conductive metal material. 
     In processing operation  1820 , the fabrication system  155  cures the printable material (dielectric material  270 ) on the substrate  250 . The second particles  122  in the cured printable material (dielectric material  270 ) is transformable into one or more electrically conductive paths via application of heat above a threshold value. 
       FIG. 19  is an example diagram illustrating a method according to embodiments herein. 
     In processing operation  1910 , the fabricator  240  receives a substrate  250 . A first layer of dielectric material  270  is disposed on a surface  420  of the substrate  250 . The first layer of dielectric material  270  includes first particles  121  and second particles  122  suspended in the first layer of dielectric material  270 . As previously discussed, in one embodiment, the first particles  121  are fabricated from an insulator material; the second particles  122  is fabricated from electrically conductive material  122 . 
     In processing operation  1920 , via control of source  230 , the fabricator  140  applies heat to a region  250 - 2  of the first layer of dielectric material  270 . Application of the heat (such as via signal  231 ) transforms the dielectric material  270  in the region  250 - 2  into an electrically conductive path  260 . 
     Note again that techniques herein are well suited to facilitate fabrication and use of dielectric material ink. However, it should be noted that embodiments herein are not limited to use in such applications and that the techniques discussed herein are well suited for other applications as well. 
     Based on the description set forth herein, numerous specific details have been set forth to provide a thorough understanding of claimed subject matter. However, it will be understood by those skilled in the art that claimed subject matter may be practiced without these specific details. In other instances, methods, apparatuses, systems, etc., that would be known by one of ordinary skill have not been described in detail so as not to obscure claimed subject matter. Some portions of the detailed description have been presented in terms of algorithms or symbolic representations of operations on data bits or binary digital signals stored within a computing system memory, such as a computer memory. These algorithmic descriptions or representations are examples of techniques used by those of ordinary skill in the data processing arts to convey the substance of their work to others skilled in the art. An algorithm as described herein, and generally, is considered to be a self-consistent sequence of operations or similar processing leading to a desired result. In this context, operations or processing involve physical manipulation of physical quantities. Typically, although not necessarily, such quantities may take the form of electrical or magnetic signals capable of being stored, transferred, combined, compared or otherwise manipulated. It has been convenient at times, principally for reasons of common usage, to refer to such signals as bits, data, values, elements, symbols, characters, terms, numbers, numerals or the like. It should be understood, however, that all of these and similar terms are to be associated with appropriate physical quantities and are merely convenient labels. Unless specifically stated otherwise, as apparent from the following discussion, it is appreciated that throughout this specification discussions utilizing terms such as “processing,” “computing,” “calculating,” “determining” or the like refer to actions or processes of a computing platform, such as a computer or a similar electronic computing device, that manipulates or transforms data represented as physical electronic or magnetic quantities within memories, registers, or other information storage devices, transmission devices, or display devices of the computing platform. 
     While this invention has been particularly shown and described with references to preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present application as defined by the appended claims. Such variations are intended to be covered by the scope of this present application. As such, the foregoing description of embodiments of the present application is not intended to be limiting. Rather, any limitations to the invention are presented in the following claims.