Patent Publication Number: US-7217199-B2

Title: Hollow golf club head

Description:
RELATED APPLICATION 
   This application is a divisional of application Ser. No. 10/328,146, filed Dec. 26, 2002, now U.S. Pat. No. 7,037,214 the contents of which are incorporated herein by reference. 

   BACKGROUND OF THE INVENTION 
   The present invention concerns a golf club head having a hollow structure, and more particularly, a hollow golf club head having a higher repulsion and a greater degree of design freedom, compared to a case of composing solely with a single metallic material, by combining different kinds of materials. 
   For the metallic hollow golf club heads, it is planned to lower the center of gravity generally by broadening the weight distribution to the sole portion. However, in recent years, the weight margin for lowering the center of gravity is reduced and the degree of design freedom is reduced, because it is required to increase the head volume as much as possible in a limited head mass. There, if the center of gravity is not lowered sufficiently in the head, there is a problem that the repulsion of the face surface can not be utilized maximally. 
   By the way, Japanese Patent No. 2764883, Japanese patent application Kokai publication No. 2000-229135, and Japanese Patent No. 2773009 disclose a golf club head made by combining different materials. However, even in these golf club heads where characteristics of different kinds of materials are combined, the degree of design freedom or the repulsion has been still insufficient. 
   SUMMARY OF THE INVENTION 
   An object of the present invention is to provide a hollow golf club head having a higher repulsion and a greater degree of design freedom, compared to a case of composing solely with a single metallic material, by combining different kinds of materials. 
   The hollow golf club head of the present invention for attaining the aforementioned object is a hollow golf club head having a head body formed from a metal, wherein a hole is formed in the vicinity of the middle of a crown portion in the head body, the hole is closed with a cover member made of a material different from the head body, and the ratio (ρm/ρf) of the specific gravity ρm of the head body and the specific gravity ρf of the cover member is set equal or superior to 1.3. 
   Moreover, the hollow golf club head of the present invention for attaining the aforementioned object is a hollow golf club head having a head body formed from a metal, wherein holes portion are formed respectively in the vicinity of the middle of a crown portion and a sole portion in the head body, each of the holes is closed with a cover member made of a material different from the head body, and the ratio (ρm/ρf) of the specific gravity ρm of the head body and the specific gravity ρf of the cover member is set equal or superior to 1.3. 
   Moreover, the hollow golf club head of the present invention for attaining the aforementioned object is a hollow golf club head having a head body formed from a metal, wherein a hole is formed in the vicinity of the middle of a crown portion in the head body, a flange spreading over a hollow space is formed at least on a part of the peripheral edge of the crown portion, the hole is closed with a cover member made of a material different from the head body, and the ratio (ρm/ρf) of the specific gravity ρm of the head body and the specific gravity ρf of the cover member is set equal or superior to 1.3. 
   Still further, the hollow golf club head of the present invention for attaining the aforementioned object is a hollow golf club head having a head body formed from a metal, wherein holes are formed respectively in the vicinity of the middle of a crown portion and a sole portion in the head body, a flange spreading over a hollow space is formed at least on a part of the peripheral edge of the crown portion, another flange spreading under the hollow space is formed at least on a part of the peripheral edge of the sole portion, each of the holes is closed with a cover member made of a material different from the head body, and the ratio (ρm/ρf) of the specific gravity ρm of the head body and the specific gravity ρf of the cover member is set equal or superior to 1.3. 
   A greater weight margin can be secured, by providing a hole in the crown portion or both crown portion and sole portion of the head body, closing the hole with a cover member made of a material different from the head body, and setting the ratio (ρm/ρf) of the specific gravity ρm of the head body and the specific gravity ρf of the cover member equal or superior to 1.3 in this manner. Consequently, the degree of design freedom is increased compared to a case of composing solely with a single metallic material and, as a result, it becomes possible to increase the repulsion by lowering the center of gravity. 
   In the present invention, the durability can be maintained sufficiently, by providing a flange in the crown portion or both crown portion and sole portion. In order to deploy more excellent durability, it is preferable to dispose a flange at least on a face side of the head body, and overlay the cover member partially or wholly on the face side flange with an overlap margin of equal or superior to 5 mm in width. The width of the face side flange is satisfactory if it is in a range of equal or superior to 5 mm and less than 30 mm. It should be noted that the width of the face side flange is measured at the face middle portion. 
   As for the material of the cover member, it is preferable to be used a fiber reinforced plastic, however, either magnesium alloy, aluminum alloy or titanium alloy may also be used, according to the kind of metallic material composing the head body. In certain cases, it is also possible to use rubber or resin as material for the cover member. It is preferable to make the total mass Wf of the cover member closing the hole lighter than the total mass Wx of the removed portion of the head body determined from the product of the virtual area of the hole, the virtual thickness of the hole and the specific gravity ρm of the head body, independently of the material to be used, in order to secure the weight margin. 
   In the present invention, though it is preferable to close the hole provided in the head body with a cover member, it is also possible to compose a hollow golf club head having the other composite structure. In short, the hollow golf club head of the present invention is characterized by that at least a part of the crown portion of the head body is composed of a material different from the head body, and the ratio (ρb/ρc) of the specific gravity ρb of a portion of the head body excluding the crown portion and the specific gravity ρc of the crown portion is set equal or superior to 1.3. 
   Thus, it becomes possible to secure sufficiently a weight margin, by the fact that at least a part of the crown portion of the head body is composed of a material different from the head body, and the ratio (ρb/ρc) of the specific gravity ρb of a portion of the head body excluding the crown portion and the specific gravity ρc of the crown portion is set equal or superior to 1.3. Consequently, the degree of design freedom is increased compared to a case of composing solely with a single metallic material and, as a result, it becomes possible to increase the repulsion by lowering the center of gravity. 

   
     BRIEF DESCRIPTION OF THE DRAWINGS 
       FIG. 1(   a ) to  FIG. 1(   c ) show a golf club head made of a first embodiment of the present invention;  FIG. 1(   a ) is a plan view,  FIG. 1(   b ) a front view, and  FIG. 1(   c ) is a cross sectional view taken along line I—I  FIG. 1(   a ); 
       FIG. 2(   a ) to  FIG. 2(   c ) show a golf club head made of a second embodiment of the present invention;  FIG. 2(   a ) is a plan view,  FIG. 2(   b ) a front view, and  FIG. 2(   c ) is a cross sectional view taken along line II—II in  FIG. 2(   a ); 
       FIG. 3(   a ) to  FIG. 3(   t ) are plan views showing respectively variants of the head body of golf club head of the present invention; 
       FIG. 4(   a ) to  FIG. 4(   d ) are plan views showing respectively variants of golf club head of the present invention; 
       FIG. 5(   a ) to  FIG. 5(   g ) are cross sectional view showing respectively variants of golf club head of the present invention; 
       FIG. 6(   a ) and  FIG. 6(   b ) show variants of golf club head of the present invention;  FIG. 6(   a ) is a plan view, and  FIG. 6(   b ) is a cross sectional view taken along line VI—VI in  FIG. 6(   a ); 
       FIG. 7(   a ) and  FIG. 7(   b ) show variants of golf club head of the present invention;  FIG. 7(   a ) is a plan view, and  FIG. 7(   b ) is a cross sectional view taken along line VII—VII in  FIG. 7(   a ); and 
       FIG. 8(   a ) to  FIG. 8(   c ) show a golf club head made of a third embodiment of the present invention;  FIG. 8(   a ) is a plan view,  FIG. 8(   b ) a front view, and  FIG. 8(   c ) is a cross sectional view taken along line VIII—VIII in  FIG. 8(   a ). 
   

   DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT 
   Now, the composition of the present invention shall be described in detail referring to attached drawings. 
     FIG. 1(   a ) to  FIG. 1(   c ) show a golf club head made of a first embodiment of the present invention. As shown in  FIG. 1(   a ) to  FIG. 1(   c ), the golf club head of the present embodiment has a hollow structure, and a head body  1  thereof is composed of a metal such as titanium alloy, aluminum alloy, stainless steel or the like. The head body  1  has a crown portion  2 , a face portion  3 , a sole portion  4  and neck portion  5 . While a hole  2   a  is formed in the vicinity of the middle of the crown portion  2 , and a flange portion  2   b  spreading over a hollow space is formed around the peripheral edge of the crown portion  2 . There, the hole  2   a  is closed with a cover member  6  made of a material of a specific gravity lower than the head body  1 . 
     FIG. 2(   a ) to  FIG. 2(   c ) show a golf club head made of a second embodiment of the present invention. As shown in  FIG. 2(   a ) to  FIG. 2(   c ), the golf club head of the present embodiment has a hollow structure, the head body  1  thereof is composed of a metal such as titanium alloy, aluminum alloy, stainless steel or the like. The head body  1  comprises a crown portion  2 , a face portion  3 , a sole portion  4  and a neck portion  5 . While holes  2   a ,  4   a  are formed respectively in the vicinity of the middle of the crown portion  2  and the sole portion  4  in the head body, a flange  2   b  spreading over a hollow space is formed around the peripheral edge of the crown portion  2 , and another flange  4   b  spreading under the hollow space is formed around the peripheral edge of the sole portion  4 . And, the holes  2   a ,  4   a  are closed respectively with a cover member  6  made of a material lower than the head body  1  in specific gravity. 
   Thus, it becomes possible to secure a larger weight margin, and increase the degree of design freedom, by providing the hole  2   a  in the crown portion  2  of the head body  1  and further by providing a hole  4   a  in the sole portion  4  as necessary and by closing the holes  2   a ,  4   a  with a cover member  6  made of a material lower than the head body  1  in specific gravity. Especially, when the crown portion  2  is provided with the cover member  6 , it becomes possible to increase the moment of inertia and to lower the center of gravity by enlarging the weight margin, while in case of providing the cover member  6  in the sole portion  4 , it becomes possible to increase the moment of inertia by enlarging the weight margin. Here, it is necessary to set the ratio (ρm/ρf) of the specific gravity ρm of the head body  1  and the specific gravity ρf of the cover member  6  equal or superior to 1.3. If the ratio (ρm/ρf) is lower than 1.3, it becomes impossible to secure a sufficient weigh margin. The upper limit of the ratio (ρm/ρf) is not particularly determined, but it is of the order of 16 from the combination of materials to be applied to now existing golf club heads. 
   For the aforementioned holes  2   a ,  4   a , the shape thereof is not particularly determined. For instance, the hole  2   a  of the crown portion  2  can take various shapes as shown in  FIG. 3(   a ) to  FIG. 3(   t ). However, in the head plan view, it is preferable to set the area of the hole  2   a  in a range of 40 to 90%, of the area of the crown portion  2 . It becomes possible to improve further the degree of design freedom by setting within the range. Here, the area of the crown portion is the surface area of a portion surrounded by the edge of the side portion, the edge of the face portion and the edge of the neck portion. Similarly, in the head bottom view, it is preferable to set the area of the hole  4   a  in a range of 40 to 90%, of the area of the sole portion  4 . It becomes possible to improve further the degree of design freedom by setting within the range. Here, the area of the sole portion is the surface area of a portion surrounded by the edge of the side portion and the edge of the face portion. Besides, in case where the edge is not clear, it is also possible to know edges of the side portion, face portion, crown portion and sole portion, by cutting the golf club head and examining the bonding portion of the inner face. Further, if the edge of the crown portion is not clear, the projected area of a golf club head excluding the hitting surface looked down from vertically upward in respect to a plane may be used while the a golf club is put on the plane with the hitting surface adjusted to the loft angle of the golf club head. 
   Though the aforementioned flanges  2   b ,  4   b  are not necessarily required, preferably it exists at least on a part of the peripheral edge of the crown portion  2  and the sole portion  4 , more preferably it exists at least on the face side of the head body  1 , and still more preferably all around the peripheral edge. In short, the disposition of the flanges  2   b ,  4   b  in an appropriate area of the head body  1  permits to secure the durability margin for the cover member  6 . 
   It is preferable that the aforementioned cover member  6  is superimposed on the flanges  2   b ,  4   b  at least on the face side of the head body  1 . In this case, the cover member  6  may cover a part of the flange  2   b  on the face side, as shown in FIG.  4 ( a ) and  FIG. 4(   b ), or the cover member  6  may cover all over the flange  2   b  on the face side, as shown in  FIG. 4(   c ) and  FIG. 4(   d ). The width t 1  of the overlap margin for the flange  2   b  on the face side of the cover member  6  is preferably equal or superior to 5 mm. It becomes possible to secure a durability more sufficiently by setting the width t 1  of the overlap margin equal or superior to 5 mm. Besides, the width t 2  of flange  2   b  on the face side is satisfactory if it is equal or superior to 5 mm and less than 30 mm. In case where the cover member  6  is superimposed on the flange  4   b  of the sole portion  4 , it is preferable to select a laminating mode and dimensions similar to the aforementioned. 
   The affixation mode of the cover member  6  to the head body  1  is not especially determined. For instance, in  FIG. 1(   c ) and  FIG. 2(   c ), the peripheral edge portion of the cover member  6  is divided into two layers, and the flanges  2   b ,  4   b  are pinched from inside and outside in this portion; however, the cover member  6  may be stuck to one face of the flange  2   b  as shown in  FIG. 5(   a ) to  FIG. 5(   d ), or the cover member  6  may be affixed to the end face of the face portion  3  without intermediate of flange as shown in  FIG. 5(   e ) to  FIG. 5(   g ). Otherwise, the flange  2   b  may be provided in a way to receive the cover member  6 , in a portion of the head body  1  to be bonded with the cover member  6 , as shown in  FIG. 6(   a ) and  FIG. 6(   b ) or  FIG. 7(   a ) and  FIG. 7(   b ). 
   The cover member  6  may be affixed, namely combined, to the face portion  3  as shown in  FIG. 2(   c ), or may not be combined as shown in  FIG. 1(   c ). This is expressed by the ratio (called, face combined area ratio, hereinafter) of the face area of the portion where the cover member  6  and the head body  1  are combined to the face area (area of hitting surface) of the head body  1 . Here, the face area is the surface area of the portion surrounded by the edge of the face portion. Further, if the edge of is not clear, the edge of the face portion can also be known, by cutting the golf club head, and examining the bonded portion of the inner face. If the face combined area ratio is high, the durability of the golf club head becomes relatively better, while if low, the resilience of the golf club head becomes relatively better. Especially, in case of a face combined area ratio equal or superior to 3%, it becomes possible to improve the durability further more. 
   As for the material of the cover member  6 , it is preferable to be used a fiber reinforced plastic. As the fiber reinforced plastic, a fiber reinforced plastic made by impregnating carbon fiber, glass fiber, alamido fiber or other reinforced fiber with epoxy resin, unsaturated polyester resin, vinyl ester resin or other matrix resin, can be cited and, especially, those having carbon fiber as reinforced fiber are preferable. However, the coefficient of elasticity of the fiber of the fiber reinforced plastic composing the cover member  6  is preferably equal or less than 35 tons/mm 2 , and more preferably equal or less than 24 tons/mm 2 . It becomes possible to secure a more satisfactory durability, by setting this coefficient of elasticity within the aforementioned range. 
   It can also so made to use magnesium alloy, aluminum alloy or titanium alloy, as material of the cover member  6  and, in certain cases, in addition to the hard rubber, nylon resin, ionomer resin, polycarbonate resin, PET resin, ABS resin or the like may also be used. 
   Whichever material is used, it is preferable to make the total mass Wf of the cover member  6  closing the holes  2   a ,  4   a  lighter than the total mass Wx of the removed portion of the head body  1  determined from the product of the virtual area and the virtual thickness of the holes  2   a ,  4   a  and the specific gravity ρm of the head body  1 , namely Wx&gt;Wf, in order to secure the weight margin. 
   For instance, in case where the hole  2   a  is formed in the vicinity of the middle of the crown portion  2 , the flange  2   b  is formed all around the peripheral edge of the crown portion  2 , and a cover member  6  is affixed to the outside of the crown portion  2 , the total mass Wf of the cover member  6  will be Wf=Af·ρf·tf from the area Af, specific gravity ρf and thickness tf of the cover member  6 . On the other hand, the total mass Wx of the removed portion will be Wx=(Af−Am)·ρm·tm from the area Am of the overlapped portion of the cover member  6  and the head body  1 , specific gravity ρm of the head body  1  and average thickness tm of the crown portion and sole portion of the head body  1  in the overlapped portion. In short, the virtual area of the holes  2   a ,  4   a  can be determined from the difference of the area Af of the cover member  6  and the area Am of the overlapped portion, and the virtual thickness of the holes  2   a ,  4   a  can be considered as equivalent to the average thickness tm of the crown portion and sole portion of the head body  1  in the overlapped portion. 
     FIG. 8(   a ) to  FIG. 8(   c ) show a golf club head made of a third embodiment of the present invention. As shown in  FIG. 8(   a ) to  FIG. 8(   c ), the golf club head of the present embodiment has a hollow structure, the head body  1  thereof is composed of a metal such as titanium alloy, aluminum alloy, stainless steel or the like. The head body  1  comprises a crown portion  2 , a face portion  3 , a sole portion  4  and a neck portion  5 , and a cover member  6  is laminated on the outer surface of the crown portion  2 . In short, a part of the crown portion  2  is made of a material different from the head body  1 . 
   There, the ratio (ρb/ρc) of the specific gravity ρb of a portion of the head body  1  excluding the crown portion  2  and the specific gravity ρc of the crown portion  2  is set equal or superior to 1.3. Here, the crown portion is the portion surrounded by the edge of the side portion, the edge of the face portion and the edge of the neck portion. In case where the edge is not clear, it is also possible to know edges of the side portion, face portion, crown portion and sole portion, by cutting the golf club head and examining the bonding portion of the inner face. Further, if the edge of the crown portion is not clear, the edge of the crown portion can be known by the profile line excluding the hitting surface looked down from vertically upward in respect to a plane while the golf club is put on the plane with the hitting surface adjusted to the loft angle of the golf club head. 
   Thus, it becomes possible to secure a satisfactory weight margin, by the fact that at least a part of the crown portion  2  of the head body  1  is composed of a material different from the head body  1 , and the ratio (ρb/ρc) of the specific gravity ρb of a portion of the head body  1  excluding the crown portion  2  and the specific gravity ρc of the crown portion  2  is set equal or superior to 1.3. Consequently, the degree of design freedom is increased compared to a case of composing solely with a single metallic material and, as a result, it becomes possible to increase the repulsion by lowering the center of gravity. 
   In the present embodiment, the portion of the head body  1  excluding the crown portion  2  and the crown portion  2  may be composed of a single material, or, may be composed of a composite material. In case of composing from a composite material, the specific gravity ρb and the specific gravity ρc correspond to the specific gravities of the portion of the head body  1  excluding the crown portion  2  and the crown portion  2  respectively. 
   EXAMPLE 
   As for the hollow golf club head whose head body is formed from a metal, a comparative example 1 (example of the prior art) made of a single metallic material and, embodiment examples 1 to 4 and comparative examples 2 to 3 where holes are formed in the vicinity of the middle of the crown portion and the sole portion, and the holes are closed respectively with a cover member made from different materials, were prepared respectively. In Table 1, “SUS alloy” means stainless steel, and “FRP” fiber reinforced plastic. 
   Coefficient of restitution and degree of design freedom were evaluated for these golf club heads and the results thereof are shown together in Table 1. The results of evaluation are indicated by the index by taking the comparative example 1 as 100. The repulsion coefficient means that the higher is the index value, the higher is the ball initial velocity and the larger is the flight distance. The degree of design freedom is the weight margin when the head total mass is set at 190 g and means that the higher is the index value, the higher is the weight margin. 
   
     
       
         
             
             
             
             
             
             
             
             
           
             
               TABLE 1 
             
             
                 
             
             
                 
                 
                 
                 
                 
               Face 
                 
               Degree of 
             
             
                 
                 
                 
               Material of 
                 
               combined 
                 
               design 
             
             
                 
                 
               Material of 
               cover 
               Position of 
               area ratio 
               Repulsion 
               freedom 
             
             
                 
               ρm/ρf 
               head body 
               member 
               hole 
               (%) 
               coefficient 
               elasticity 
             
             
                 
             
           
          
             
                 
             
          
         
         
             
             
             
             
             
             
             
             
          
             
               Comparative 
               1.0 
               Ti alloy 
               Ti alloy 
               — 
               — 
               100 
               100 
             
             
               example 1 
             
             
               Embodiment 1 
               2.9 
               Ti alloy 
               FRP 
               Crown 
               5 
               102 
               111 
             
             
               Comparative 
               0.6 
               Ti alloy 
               SUS alloy 
               Crown 
               5 
               97 
               93 
             
             
               example 2 
             
             
               Embodiment 2 
               2.9 
               Ti alloy 
               FRP 
               Crown, sole 
               5 
               104 
               118 
             
             
               Comparative 
               0.6 
               Ti alloy 
               SUS alloy 
               Crown, sole 
               5 
               96 
               89 
             
             
               example 3 
             
             
               Embodiment 3 
               2.7 
               Ti alloy 
               Mg alloy 
               Crown 
               0 
               104 
               109 
             
             
               Embodiment 4 
               2.9 
               Ti alloy 
               FRP 
               Crown 
               0 
               104 
               111 
             
             
                 
             
          
         
       
     
   
   As it is understood from the Table 1, for every golf club head of the embodiment examples 1 to 4, compared to comparative example 1, the degree of design freedom was large, and the repulsion coefficient was large. For the comparative examples 2, 3, the degree of design freedom was small, and the repulsion coefficient was low, because the specific gravity of the cover member is too high. 
   Next, as for the hollow golf club head whose head body is formed from a metal, a comparative example 11 (example of the prior art) made of a single metallic material and, embodiment examples 11 to 15 and comparative examples 12 to 13 where holes are formed in the vicinity of the middle of the crown portion and the sole portion and, at the same time, flanges are formed on the peripheral edge of the crown portion and the sole portion, and the holes are closed respectively with a cover member made from different materials, were prepared respectively. In Table 2, “SUS alloy” means stainless steel, and “FRP” fiber reinforced plastic. 
   Coefficient of restitution and degree of design freedom were evaluated, for these golf club heads, similarly to the foregoing, and the results thereof are shown together in Table 2. The results of evaluation are indicated by the index by taking the comparative example 11 as 100. 
   
     
       
         
             
             
             
             
             
             
             
             
             
             
             
             
             
           
             
               TABLE 2 
             
             
                 
             
             
                 
                 
                 
                 
                 
                 
                 
               Crown 
                 
               Sole 
                 
                 
                 
             
             
                 
                 
                 
                 
                 
                 
                 
               portion 
                 
               portion 
             
             
                 
                 
                 
                 
                 
                 
                 
               cover 
               Sole 
               cover 
             
             
                 
                 
                 
               Material 
                 
               Face 
               Crown 
               member 
               portion 
               member 
                 
               Degree of 
             
             
                 
                 
               Material 
               of 
                 
               combined 
               portion face 
               overlap 
               face side 
               overlap 
                 
               design 
             
             
                 
                 
               of 
               cover 
               Position of 
               area ratio 
               side flange 
               margin 
               flange 
               margin 
               Repulsion 
               freedom 
               Dura- 
             
             
                 
               ρm/ρf 
               head body 
               member 
               hole 
               (%) 
               width 
               width 
               width 
               width 
               coefficient 
               elasticity 
               bility 
             
             
                 
             
           
          
             
                 
             
          
         
         
             
             
             
             
             
             
             
             
             
             
             
             
             
          
             
               Comparative 
               1.0 
               Ti alloy 
               Ti alloy 
               — 
               — 
               — 
               — 
               — 
               — 
               100 
               100 
               100 
             
             
               example 11 
             
             
               Embodiment 
               2.9 
               Ti alloy 
               FRP 
               Crown 
               5 
               15 mm 
               8 mm 
               — 
               — 
               102 
               111 
               101 
             
             
               11 
             
             
               Comparative 
               0.6 
               Ti alloy 
               SUS alloy 
               Crown 
               5 
               15 mm 
               8 mm 
               — 
               — 
               98 
               93 
               100 
             
             
               example 12 
             
             
               Embodiment 
               2.9 
               Ti alloy 
               FRP 
               Crown, sole 
               5 
               15 mm 
               8 mm 
               15 mm 
               8 mm 
               104 
               118 
               100 
             
             
               12 
             
             
               Comparative 
               0.6 
               Ti alloy 
               SUS alloy 
               Crown, sole 
               5 
               15 mm 
               8 mm 
               15 mm 
               8 mm 
               96 
               89 
               101 
             
             
               example 13 
             
             
               Embodiment 
               2.9 
               Ti alloy 
               FRP 
               Crown 
               5 
               15 mm 
               15 mm  
               — 
               — 
               103 
               109 
               103 
             
             
               13 
             
             
               Embodiment 
               2.7 
               Ti alloy 
               Mg alloy 
               Crown 
               0 
               15 mm 
               8 mm 
               — 
               — 
               104 
               109 
               101 
             
             
               14 
             
             
               Embodiment 
               2.9 
               Ti alloy 
               FRP 
               Crown 
               0 
               15 mm 
               15 mm  
               — 
               — 
               104 
               109 
               101 
             
             
               15 
             
             
                 
             
          
         
       
     
   
   As it is understood from the Table 2, for every golf club head of the embodiment examples 11 to 15, compared to comparative example 11, the degree of design freedom was large, and the repulsion coefficient was large, all the way maintaining the durability. For the comparative examples 12, 13, the degree of design freedom was small, and the repulsion coefficient was low, because the specific gravity of the cover member is too high. 
   According to the present invention, in a hollow golf club head whose head body is made of a metal, the repulsion can be increased and the degree of design freedom can be increased compared to a case of composing solely with a single metallic material, by providing a hole in the vicinity of the middle of crown portion of the head body, closing the hole with a cover member made of a material different from the head body, and setting the ratio (ρm/ρf) of the specific gravity ρm of the head body and the specific gravity ρf of the cover member equal or superior to 1.3. 
   Further, in a hollow golf club head whose head body is made of a metal, the repulsion can be increased and the degree of design freedom can be increased compared to a case of composing solely with a single metallic material, by the fact that at least a part of the crown portion of the head body is composed of a material different from the head body, and the ratio (ρb/ρc) of the specific gravity ρb of the portion of the head body excluding the crown portion and the specific gravity ρc of the crown portion is set equal or superior to 1.3. 
   Hereinabove, preferable embodiments of the present invention have been described in detail; however, it should be understood that various modifications, replacements or substitutions can be applied to the same, to the extent not to depart from the spirit and the scope of the present invention which is defined by the attached claims.