Patent Publication Number: US-2020299460-A1

Title: Polyamide copolymer, process for preparation, and molded parts made thereof

Description:
The present invention relates to a polyamide copolymer, more particular to a semi-crystalline semi-aromatic polyamide. The invention further relates to a process for preparing the copolymer, a process for making molded parts from the copolymer and molded parts comprising the same. The invention in particular relates to extrusion molded parts. 
     Semi-crystalline semi-aromatic polyamides, in particular those polyamides based on terephthalic acid, also known as PPAs, belong to the high-end performance of thermoplastic polymers. Important properties of PPAs are chemical resistance and mechanical properties at high temperature, as well as high temperature performance in terms of retention of strength and toughness during exposure to hot, aggressive conditions such as exposure to hot automotive fluids and hot air, whether humid or dry. PPAs are thermoplastic polymers having amorphous domains characterized by a glass transition temperature (Tg), and crystalline domains characterized by a melting temperature (Tm). Compared to aliphatic polyamides, which are also semi-crystalline thermoplastic polymers, the Tm and Tg of PPAs is relatively high. The chemical nature of the components and the relatively high Tg and Tm of PPAs can explain for the better performance in terms of chemical resistance and mechanical properties at high temperature of the PPAs. A disadvantage of PPAs, compared to aliphatic polyamides, is that in general processing is more difficult, not in the last part since processing is typically done above the melting temperature, thus at higher temperatures. Measures to keep the melting temperature of PPAs sufficiently low to allow for good processing are generally accompanied with a reduction in chemical resistance and/or mechanical properties at high temperature. Typically, such measures consist of using a combination of different monomers for the preparation, the resulting PPAs thereof being typified as polyamide copolymers. 
    
    
     The aim of the present invention is to provide a semi-crystalline semi-aromatic polyamide copolymer that has an improved balance in mechanical properties at high temperature while having good chemical resistance and good processing performance, in particular a good in extrusion. 
     This aim has been achieved with the polyamide copolymer according to the present invention, consisting of repeat units derived from polyamide forming monomers consisting of
         55-90 mole % of 1,6-hexanediamine (referred to as HMDA) and 10-45 mole % of either one of 1,2-ethylenediamine, 1,3-trimethylenediamine, 1,4-tetramethylenediamine and 1,5-pentamethylenediamine, or a combination thereof (referred to as C2-C5 diamine), the mole % being relative to the combined molar amount of HMDA and C2-C5 diamine;   50-85 mole % of terephthalic acid (referred to as TPA) and 15-50 mole % of isophthalic acid (referred to as IPA), the mole % being relative to the combined molar amount of TPA and IPA;   0-10 mole % of other polyamide forming monomer or monomers, the mole % being relative to the total molar amount of polyamide forming monomers.       

     This polyamide copolymer is a semi-crystalline semi-aromatic polyamide copolymer derived from polyamide forming monomers based on diamines and dicarboxylic acids, or based on diamines, dicarboxylic acids and other monomers. 
     With a polyamide copolymer is herein understood a polyamide comprising repeat units of derived from at least diamine and diacid monomers, wherein the diamine and diacid monomers comprise more than one diamine or more than one dicarboxylic acid, or both more than one diamine or more than one dicarboxylic acid. Polyamide copolymer is also referred to as copolyimide. 
     Even though a combination of multiple monomers is used, resulting in lowering of the melting point and of the crystallinity, the polyamide copolymer according to the invention has surprisingly good properties. The effect of the copolyamide based on the diamines and dicarboxylic acids in the said molar percentages as mentioned above, is that the copolyamide has very good tensile properties, such as high tensile strength and high elongation at break, as well as a high ductility, very good resistance against environmental stress cracking, good high temperature mechanical properties, while allowing for tuning the processing conditions and applying a lower extrusion temperature, resulting in a more stable extrusion process. 
     The polyamide copolymer according to the invention suitably has one or more of the following thermal properties:
         a melting temperature (Tm) in the range of 275-335° C.; and/or   a melting enthalpy (ΔHm) in the range of 30-90 J/g; and/or a   a glass transition temperature (Tg) in the range of 110-160° C.       

     Herein, the melting temperature is measured by the DSC method according to ISO-11357-Jan. 3, 2011, on pre-dried samples in an N 2  atmosphere with heating and cooling rate of 20° C./min. Herein Tm has been calculated from the peak value of the highest melting peak in the second heating cycle. 
     Herein the glass transition temperature (Tg) is measured by the differential scanning calorimetry (DSC) method according to ISO-11357-Jan. 2, 2011, on pre-dried samples in an N2 atmosphere with a heating and cooling rate of 20° C./min. Herein Tg has been calculated from the value at the peak of the first derivative (in respect of temperature) of the parent thermal curve corresponding with the inflection point of the parent thermal curve in the second heating cycle. 
     Herein the melting enthalpy (ΔHm) is measured by the DSC method according to ISO-11357-Jan. 3, 2011, on pre-dried samples in an N 2  atmosphere with heating and cooling rate of 20° C./min. Herein ΔHm has been calculated from the surface under the melting peak in the second heating cycle. 
     With a semi-aromatic polyamide is herein understood a polyamide comprising repeat units derived from aromatic monomers (i.e. monomers comprising an aromatic group or backbone) and aliphatic monomers (i.e. monomers comprising an aliphatic backbone). Herein the monomers comprising an aromatic backbone may be, for example, an aromatic dicarboxylic acid, or an aromatic diamine, or an arylalkyl diamine, or any combination thereof. 
     The polyamide copolymer according to the invention comprises repeat units primarily derived from the diamines 1,6-hexanediamine and one or more of 1,2-ethylenediamine, 1,3-trimethylenediamine, 1,4-tetramethylenediamine and 1,5-pentamethylenediamine, and the dicarboxylic acids terephthalic acid and isophthalic acid. 
     The polyamide copolymer may comprise small amounts of repeat units derived from other monomers, i.e. polyamide forming monomers other than 1,2-ethylenediamine, 1,3-trimethylenediamine, 1,4-tetramethylenediamine, 1,5-pentamethylenediamine 1,6-hexanediamine, terephthalic acid and isophthalic acid. 
     However, the amount of repeat units derived from other polyamide forming monomers shall be kept limited. The other monomers are present, if at all, in an amount in the range of 0-10 mole %, preferably 0-5 mole % and even more preferably 0-2.5 mole %, relative to the total molar amount of polyamide forming monomers. 
     Thus, the polyamide forming monomers may comprise one, or more than one diamine, other than the said diamines 1,2-ethylenediamine, 1,3-trimethylenediamine, 1,4-tetramethylenediamine, 1,5-pentamethylenediamine 1,6-hexanediamine. Furthermore, the polyamide forming monomers may also comprise one or more than one monomer other than diamines and dicarboxylic acids. 
     In line with the above, the polyamide copolymer may comprise repeat units derived from other dicarboxylic acids; for example, 4,4′-biphenyldicarboxylic acid or naphthalene dicarboxylic acid, or a mixture thereof. 
     The polyamide copolymer may also, or alternatively, comprise repeat units derived from other diamines, for example linear aliphatic diamines with at least 7 carbon atoms, [for example 1,7-heptamethylenediamine, 1,8-octamethylenediamine, 1,9-nonane diamine, 1,10-decanediamine, 1,11-undecane-diamine, 1,12-dodecanediamine and 1,18-octadecanediamine], branched aliphatic diamines [for example 2-methylpentamethylendiamine, 2,2,4-trimethyl-hexamethylene diamine, 2,4,4-trimethylhexamethylenediamine, and 2-methyl-1,8-octanediamine], and cyclo-aliphatic diamines [for example 1,4-diaminocyclohexane, 4,4′-methylene-bis(cyclohexylamine) (PAC), 3,3′-dimethyl-4,4′-diaminocyclohexyl-methane (MAC); 3,3′,5,5′-tetramethyl-4,4′-diaminocyclohexylmethane; 2,2′,3,3′-tetramethyl-4,4′-diaminocyclohexylmethane; norbornanediamine; and isophoronediamine (IPD)]. 
     The polyamide copolymer may also comprise repeat units derived from monomers other than dicarboxylic acid and diamine. Typically, such other monomers bear at least an amine functional group and/or a carboxylic acid functional group. Examples include monofunctional carboxylic acids, trifunctional carboxylic acids, monofunctional and trifunctional amines, cyclic lactams and α,ω-aminoacids, and combinations thereof. 
     In case the polyamide forming monomer comprise one or more than one monomer other than HMDA, C2-C5 diamine, TPA and IPA, such other monomer preferably comprises at least 50 mole % and preferably 75-100 mole % of a linear aliphatic C7-C18 diamine. With a CX diamine is herein understood a diamine with X carbon atoms, wherein X is an integer. For example, when X is 12, the diamine is 1,12-dodecanediamine. 
     In a preferred embodiment, the polyamide forming monomers comprise 65-85 mole % of 1,6-hexanediamine (HMDA) and 15-35 mole % of either one of 1,2-ethylenediamine, 1,3-trimethylenediamine, 1,4-tetramethylenediamine and 1,5-pentamethylenediamine, or a combination thereof (C2-C5 diamine). More preferably, these diamines comprise 10-45 mole % of one of 1,4-tetramethylenediamine and 1,5-pentamethylenediamine, or a combination thereof. Herein the mole % is relative to the combined molar amount of HMDA and C2-C5 diamine. 
     In another preferred embodiment, the polyamide forming monomers comprise 60-80 mole % of terephthalic acid (TPA) and 20-40 mole % of isophthalic acid (IPA). Herein the mole % is relative to the combined molar amount of TPA and IPA. 
     The semi-crystalline semi-aromatic polyamide copolymer according to the invention suitably has a viscosity number (VN) of at least 70, preferably at least 80 and more preferably at least 90. The VN is herein measured in 96% sulphuric acid with a polymer concentration of 0.005 g/ml at 25° C. by the method according to ISO 307, fourth edition. The advantage of a higher VN is that the copolymer and products made thereof have better mechanical properties and an even better resistance against environmental stress factors. The viscosity number may be as high as 200 or even higher, but preferably is at most 160, more preferably in the range of 100-150. In this range, the copolymer has the optimal combination of high temperature properties and processability. 
     The polyamide copolymer according to the invention may be prepared by any process suitable for preparing thermoplastic semi-crystalline semi-aromatic polyamides. Suitably, the polyamide copolymer is prepared by a melt process, or by a combined process wherein in a first step a polyamide oligomer is prepared by melt-polymerization from the starting monomers or salts thereof, followed by a step wherein the polyamide oligomer is further polymerized in a solid-state post condensation to produce the polyamide copolymer. 
     In another preferred process, the polyamide copolymer is prepared by process steps comprising the steps of
         (i) Providing a semi-crystalline semi-aromatic polyamide (A) comprising repeat units derived from 85-100 mole % of terephthalic acid (referred to as TPA) and 0-15 mole % of isophthalic acid (referred to as IPA), the mole % being relative to the combined molar amount of TPA and IPA;   (ii) Providing an amorphous semi-aromatic polyamide (B) comprising repeat units derived from 0-50 mole % of terephthalic acid (referred to as TPA) and 50-100 mole % of isophthalic acid (referred to as IPA), the mole % being relative to the combined molar amount of TPA and IPA; and   (iii) Melt-mixing (A) and (B) and keeping (A) and (B) in the melt at a temperature (Tmelt) above the melting temperature (Tm) of (A) for a time sufficiently long to react (A) and (B) and to form the polyamide copolymer.       

     Herein (A) can be produced by any process suitable for preparing semi-crystalline semi-aromatic polyamides. Preferably (A) is prepared by direct solid-state polymerization applying a polymerization temperature below the melting temperature of (A). (B) can be produced, for example, by melt polymerization applying a polymerization temperature above the glass transition temperature of (B). The copolymer can be prepared by melt-mixing and transamidation of (A) and (B), applying a melt temperature (Tmelt) above the melting temperature (Tm) of the copolymer. The advantage of this process is that the copolymer is produced in such a manner that the copolymer is exposed for a relatively very short time to a temperature above the melt temperature of the copolymer, compared to other melt processes and that the copolymer is produced in a very efficient manner. The production of a copolymer resulting from such a transamidation process can be simply deduced from the reduction of the melting temperature measured on the product. 
     Herein (A) and (B) can be mixed in a ratio varying over a wide range, provided that the combination of monomeric repeat units is such that the molar amounts thereof fall within the ranges as defined for the polyamide copolymer of the present invention. Suitably, (A) and (B) are mixed in a weight ratio within the range of 90:10-15:85, preferably 85:15-25:75, more preferably 80:20-40:60. 
     Suitable, the amorphous semi-aromatic polyamide (B) is suitably rich in repeat units derived from both 1,6-hexanediamine (HMDA) and isophthalic acid (IPA). Similarly, the semi-crystalline semi-aromatic polyamide (A) is rich in repeat units derived from both a C2-C5 diamine and terephthalic acid (TPA). 
     In a preferred embodiment of the said process, the semi-crystalline semi-aromatic polyamide (A) consists of repeat units primarily derived from polyamide forming monomers comprising primarily diamine and dicarboxylic acid, wherein
         the diamine comprises 40-80 mole % of 1,6-hexanediamine (HMDA) and 60-20 mole % of either one of 1,2-ethylenediamine, 1,3-trimethylenediamine, 1,4-tetramethylenediamine and 1,5-pentamethylenediamine, or a combination thereof (C2-C5 diamine), the mole % being relative to the combined molar amount of HMDA and C2-C5 diamine; and   the dicarboxylic acid comprises 90-100 mole % of terephthalic acid and 10-0 mole % of isophthalic acid, the mole % being relative to the combined molar amount of TPA and IPA;   the polyamide forming monomers comprise 0-10 mole %, relative to the total molar amount of polyamide forming monomers, of monomers other than 1,2-ethylenediamine, 1,3-trimethylenediamine, 1,4-tetramethylenediamine, 1,5-pentamethylenediamine 1,6-hexanediamine, terephthalic acid and isophthalic acid.       

     In another preferred embodiment of the said process, the amorphous semi-aromatic polyamide (B) consists of repeat units derived from polyamide forming monomers comprising primarily diamine and dicarboxylic acid, wherein
         the diamine consists of 70-100 mole % of 1,6-hexanediamine and 30-0 mole % of other diamines, the mole % being relative to the total molar amount of diamine; and   the dicarboxylic acid comprises 20-45 mole % of terephthalic acid and 55-80 mole % of isophthalic acid, the molar percentage (mole %) of the dicarboxylic acids is relative to the total molar amount of dicarboxylic acid;   and the polyamide forming monomers comprise 0-5 mole %, relative to the total molar amount of polyamide forming monomers, of monomers other than diamine, terephthalic acid and isophthalic acid.       

     In a further preferred embodiment, the above two preferred embodiments are combined. 
     The copolymer according to the invention can be used, either as such or as part of a composition, in different molding processes for making molded products. The copolymer can be used, for example in injection molded products produced by injection molding, as well as in extruded parts, produced by extrusion molding. The extruded part suitably is a tape, a tube, or an extruded profile, and preferably is a tube. 
     The invention also relates to a polymer composition comprising the semi-crystalline semi-aromatic polyamide copolymer and at least one other component, as well as to molded parts made thereof. The molded parts can be, for example, injection molded products, as well as extruded parts. 
     The invention is further illustrated with the following examples and comparative experiments. 
     Starting Materials 
     
         
         sc-PPA-1 PA 6T/4T semi-crystalline semi-aromatic (60 mol % 6T/40 mol %4T), VN of 100, Tg 150° C. and Tm 337° C., ex DSM 
         sc-PPA-2 PA 6T/4T semi-crystalline semi-aromatic (60 mol % 6T/40 mol %4T), VN of 80, Tg 151° C. and Tm 338° C., ex DSM 
         sc-PPA-3 PA 6T/4T/66 (ratio 50/34/16 mole %) semi-crystalline semi-aromatic copolymer with a melting temperature of 325° C., VN 80 ml/g, ex DSM. 
         am-PPA PA 61/6T amorphous semi-aromatic copolyamide 50 mole % 1,6-hexanediamine, 35 mole % isophthalic acid and 15 mole % terephthalic acid), Tg 127° C., ex DSM. 
       
    
     Polymer Preparation for Examples 1 and 2 (CE-1 and 2) and Comparative Experiments A and B (CE-A and CE-C) 
     The polyamides were prepared by melt mixing the polymers sc-PPA-1, sc-PPA-2 and am-PPA in the desired ratio on a Berstorff ZE25/48 UTX (a co-rotating twin-screw extruder) operating at 350 rpm and using a wall temperature setting of 360° C. All polymeric materials were fed to the feed-throat of the extruder. The settings used resulted in a temperature of the melt exiting the die-head of approximately 370-380° C. The mean residence time of the molten polymers in the extruder was about 120 seconds. 
     Test Methods 
     Viscosity Number (VN) 
     The VN was measured in 96% sulphuric acid with a polymer concentration of 0.005 g/ml at 25° C. by the method according to ISO 307, fourth edition. 
     Determination of Melting Temperature by DSC According to ISO-11357-Jan. 3, (2011). 
     The measurements of the melting temperature (Tm) were carried out with a Mettler Toledo Star System (DSC) using a heating and cooling rate of 20° C./min in an N2 atmosphere. For the measurements, a sample of about 5 mg pre-dried powdered polymer was used. The pre-drying was carried out at high vacuum, i.e less than 50 mbar and at 105° C. during 16 hrs. The sample was heated from 0° C. to 360° C. with a heating rate of 20° C./min, immediately cooled to 0° C. with a cooling rate of 20° C./min and subsequently heated again at 20° C./min to 360° C. For the melting temperature Tm the peak value of the melting peak in the second heating cycle was determined. For the melting enthalpy ΔHm the melting enthalpy of the melting peak in the second heating cycle was determined. 
     Glass Transition Temperature by DSC (According to ISO-11357-2 (2013) 
     The measurements of the glass transition temperature (Tg) were carried out with a Mettler Toledo Star System (DSC) using a heating and cooling rate of 20° C./min in an N2 atmosphere in the same way as described above for the Tm. Herein the Tg was determined as the temperature at the peak of the first derivative (with respect of time) of the parent thermal curve corresponding with the inflection point of the parent thermal curve for the second heating cycle 
     Mechanical Properties 
     Mechanical properties (tensile modulus [MPa], tensile strength [MPa], elongation at break [%]) were measured in a tensile test according to ISO 527-Jan. 2:2012 with a drawing speed of 50 mm/min at a temperature of 23° C. For the tests test bars conforming 527-type-1A were used, which were molded at Tm+15° C. barrel and nozzle set temperatures and with a tool temperature of 120° C. 
     
       
         
           
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                 Composition and test results for the copolymers 
               
               
                 of Examples 1-2 and comparative experiments A-E. 
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                   
                 EX-1 
                 CE-A 
                 CE-B 
                 EX-2 
                 CE-C 
                 CE-D 
                 CE-E 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                 Sc-PPA-1 
                 65 
                 85 
                 100 
                   
                   
                   
                   
               
               
                 Sc-PPA-2 
                   
                   
                   
                 65 
                 85 
                 100 
               
               
                 Sc-PPA-3 
                   
                   
                   
                   
                   
                   
                 100 
               
               
                 Am-PPA 
                 35 
                 15 
                   
                 35 
                 15 
               
               
                 mol % T 
                 76 
                 90 
                 100 
                 76 
                 90 
                 100 
                 85 
               
               
                 mol % 6 
                 0 
                 0 
                 0 
                 0 
                 0 
                 0 
                 15 
               
               
                 mol % I 
                 24 
                 10 
                 0 
                 24 
                 10 
                 0 
                 0 
               
               
                 Tm (° C.) 
                 310 
                 335 
                 340 
                 310 
                 335 
                 340 
                 325 
               
               
                 Tg (° C.) 
                 138 
                 145 
                 150 
                 138 
                 145 
                 150 
                 125 
               
               
                 ΔHm (J/g) 
                 57 
                 66 
                 76 
                 60 
                 70 
                 82 
                 73 
               
               
                 VN (ml/g) 
                 98 
                 97 
                 101 
                 82 
                 78 
                 81 
                 76 
               
               
                 TM (MPa) 
                 3.3 
                 3.9 
                 3.9 
                 3.9 
                 4 
                 3.9 
                 4.1 
               
               
                 TS (MPa) 
                 91 
                 50 
                 65 
                 70 
                 52 
                 49 
                 52 
               
               
                 EB (%) 
                 4.3 
                 1.3 
                 1.65 
                 2 
                 1.4 
                 1.33 
                 1.32 
               
               
                   
               
            
           
         
       
     
     The copolymers of the examples according to the invention show much better mechanical properties (Tensile Strength and Elongation at Break) than those of the comparative experiments. 
     Extrusion 
     The copolymers of the Examples and of the Comparative Experiments were melt extruded into tubes with an inner diameter of about 4 mm and an outer diameter of about 5 mm in a melt extrusion apparatus applying standard processing conditions. The copolymers of the Examples I and II showed a more stable processing behavior and resulted in better quality tubes than for the copolymers of the Comparative Experiments A-E.