Patent Publication Number: US-2007102131-A1

Title: Casting of metal artefacts

Description:
THIS INVENTION relates to the casting of a metal artefact. More particularly, the invention relates to a process for casting a metal artefact, to a casting assembly for casting metal artefacts, and to a casting apparatus or installation for casting a metal artefact, all being particularly suitable for casting light metal artefacts. As used herein, the term light metal encompasses both light metals as such, and alloys thereof in which one or more light metals form the major proportion of over  50 % by mass, light metals being those having a density of less than 2.7 g/cm 3 . Light metals usually have low melting points of 660° C. or less.  
      According to a first aspect of the invention, there is provided a process for casting a metal artefact by charging a die or mould with molten metal and causing or allowing the metal to solidify in the die or mould to form the artefact, the process including the step, prior to charging the die or mould with the molten metal, of heating the die or mould by induction heating to an elevated temperature, the charging taking place with the die or mould at the elevated temperature.  
      The process may include the step of purging the die or mould, prior to the heating, so that casting of the artefact takes place under a desired atmosphere. Instead or in addition, the purging may be carried out during the heating of the die or mould. Thus, in other words, the process may include the step, prior to the charging of the die or mould, of purging the die or mould with a purging gas, the charging taking place under an atmosphere provided by the purging gas. Preferably, the purging is carried out both prior to and during the heating of the die or mould, the purging being discontinued before the charging takes place. The purging gas may be selected from the group consisting of argon, carbon dioxide and mixtures thereof. Instead said purging may be by means of a gas, such as sulphur hexafluoride (SF 6 ), which can act as a flux.  
      The process may include the step, prior to charging the die or mould with molten metal, of sealing off or locking the die or mould. In addition thereto, the process may include the step of disconnecting the supply of purging gas to the die or mould, prior to charging the die or mould with the molten metal. Typically, the supply of purging gas is discontinued when the die or mould attains its operating temperature. Charging the die or mould will typically be carried out to fill the die or mould to its full capacity.  
      The charging may be carried out under pressure, acting to fill the die or mould to its full capacity. In particular, and preferably, the filling of the die or mould with the molten charge is under an intermediate pressure, being neither what is known in the art as low pressure injection moulding nor what is known in the art as high pressure injection moulding. More particularly, the charging may be carried out by injection moulding, at an intermediate pressure in the range 50 KPa-30 MPa. It will be appreciated that routine experimentation can be employed to determine a desired or an optimum intermediate pressure under which the die or mould should be filled with the molten charge.  
      The process may include using, as the metal, a metal selected from the group consisting of aluminium, magnesium, lithium, zinc and alloys thereof. Preferably the process includes using, as the metal, a light metal selected from the group consisting of magnesium, aluminium and alloys thereof.  
      The process is expected to be useful, in particular, in the casting of light metal or alloy products selected from the group consisting of wheel rims, such as aluminium- or magnesium-alloy wheel rims, automotive gearbox casings, steering wheels, steering column housings, brake auxiliary parts or components, and automotive engine, marine and aircraft parts or components. Typically, the process will be used in the casting of aluminium- and magnesium-alloy wheel rims. Thus, the casting may be of a Ilight metal artefact in the form of a motor vehicle wheel rim.  
      In particular, the process is expected to be useful in casting artefacts having cross-sectional thicknesses in the range 1.5-30 mm, usually 2-27 mm, with respective masses of 0.25-30 kg, usually 0.5-20 kg. In other words and more particularly, the casting may be of a metal artefact in which all parts of the solidified artefact are spaced from the closest part of the surface of the artefact by a spacing of 0.75-15 mm, the artefact having a mass of 0.25-30 kg.  
      Importantly, the process may include the step of providing the die or mould with a desired temperature profile, by selective application of the induction heating thereto, to promote solidification at desired rates of different parts of the molten light metal charged into the die or mould. Thus, the induction heating may be employed to provide the surface of the interior of the die or mould with a desired temperature profile whereby the interior surface of the die or mould has different parts or zones at different temperatures from each other or one another, in contact with the molten metal charged into the die or mould, thereby to promote desired cooling and solidification rates in different parts of the metal charged into the die or mould.  
      Charging the die or mould may be from a melting apparatus having a capacity to produce a full change of molten metal which is matched in volume with the capacity or volume or the die or mould, the charging of the die or mould being with sufficient molten metal to produce a single artefact and the charging acting entirely to consume a full molten charge produced by the melting apparatus. Furthermore, charging the die or mould may be from a melting apparatus which is reciprocably movable relative to the die or mould, the process including reciprocably moving the melting apparatus between a charging position where it is charged with a precursor of the molten charge, and a filling position where the molten charge is transferred from the melting apparatus to the casting assembly. The casting may be carried out in a plurality of dies or moulds each associated with a single melting apparatus from which it is charged, each melting apparatus being associated with a single die or mould and being electrically heated by induction heating, a common electrical power supply being used to supply electrical power to the dies or moulds for the induction heating thereof, and a common electrical power supply being used to supply electrical power to the melting apparatuses. The process may be carried out by using a casting apparatus or installation as defined hereunder.  
      According to another aspect of the invention, there is provided a casting assembly for casting a metal artefact, the assembly including a die Qr mould for casting the artefact and including also an induction heating arrangement, the induction heating arrangement including at least one induction coil surrounding the die or mould, for heating the die or mould to an elevated temperature prior to the casting of the artefact.  
      The induction heating arrangement may be in the form of a variable-frequency induction heater.  
      The assembly may include a purging gas supply connected to the die or mould for supplying a purging gas to the interior of the die or mould.  
      The die or mould may be a disposable die, for example such as a sand casting die or mould. Instead, the die or mould may comprise a re-usable die or mould. The re-usable die or mould may be a metal die or mould, preferably a steel die or mould. In particular, the die or mould may be a re-usable multi-core segmented metal die or mould.  
      In the case of a re-usable die or mould, the die or mould may thus be a multi-core or segmented die or mould, comprising two or more cores or segments. In particular, the die or mould may comprise a top core or segment to which the solidified artefact remains removably attached at the end of the casting. The top core or segment may include or be associated with release means for releasing the artefact therefrom. In this case the die or mould will typically also comprise a bottom—or face core, and a ring of side cores associated with pistons, which side cores or segments give the die or mould its segmented character. In particular, the re-usable die or mould may be hydraulically operable, with regard to the pistons of the side cores and with regard to lifting of the top core and casting from the remaining cores to bring the casting into contact with pins forming the release means. The die or mould will typically have a charging opening for use in filling or charging the die or mould with molten light metal. In one embodiment of the invention, the die or mould has its charging opening provided through its bottom or face core for charging or filling the die or mould from below. In a preferred embodiment, the re-usable die or mould is hydraulically operable and has a bottom—or face core provided with a metal-charging opening for charging the die or mould with molten metal from below.  
      The induction heating arrangement may include two or more induction coils, operable independently of one another in achieving a desired temperature profile in the die or mould. In other words, the induction heating arrangement may include a plurality of at least two induction coils which are operable independently of each other or one another to heat the die or mould to said elevated temperature while providing the surface of the interior of the die or mould with a desired temperature profile.  
      The casting assembly may be of permanent construction as part of an installation, being constructed to remain more or less permanently in situ, at a production facility for casting light metal artefacts. Instead, and preferably, the casting assembly is not of permanent construction, being moveable as part of an apparatus from one said production facility to another.  
      The invention thus extends to a casting apparatus or installation for casting metal artefacts, the apparatus or installation including a casting assembly for casting a metal artefact as defined above, and a melting apparatus for forming a molten charge of metal for use in casting the metal artefact in the casting assembly, the melting apparatus including a heating arrangement for heating a precursor of the molten charge to a temperature at which the molten charge is formed from the precursor.  
      Preferably the melting apparatus is sized to melt charges of metal which are matched in size with the size of the die or mould, so that casting of the artefact in the die or mould consumes an entire charge. More particularly, the melting apparatus may nave a capacity to produce a full charge of molten metal having a volume which is matched with the capacity or volume of the die or mould so that the casting of a single artefact in the die or mould entirely consumes a full molten charge produced by the melting apparatus when the melting apparatus is operated at full capacity.  
      The heating arrangement of the melting apparatus or installation may be an induction heating arrangement comprising at least one induction coil. In each case where the die or mould arrangement, on the one hand, and, the melting apparatus on the other hand, include one or more induction heating coils, the induction coils may be electrically connected to an electrical power supply therefor.  
      The melting apparatus may be reciprocably movable relative to the casting assembly between a charging position where charging of the melting apparatus with a precursor of the molten charge takes place, and a filling position where transfer of a molten charge from the melting apparatus or installation to the casting assembly takes place. Thus, the casting apparatus or installation may include rails, the melting apparatus being mounted via wheels on the rails, the wheels being rollable along the rails during reciprocating movement of the melting apparatus relative to the casting assembly.  
      The casting apparatus or installation may include two or more of the casting assemblies and the same number of the melting apparatuses, the casting assemblies sharing a common heating power supply and the melting apparatuses sharing a common heating power supply, for the casting of artefacts in respective casting cycles which are sufficiently out of phase to permit such sharing. In other words, the casting apparatus or installation may include a plurality of the casting assemblies and the same plurality of the melting apparatuses, each casting assembly being associated with a single said melting apparatus and each melting apparatus being associated with a single said casting assembly, the casting assemblies sharing a common electrical heating power supply and the melting apparatuses sharing a common electrical heating power supply.  
      The arrangement of the facility is particularly suitable for the case where the heating arrangement for the melting apparatuses or installations is also an induction heating arrangement, the heating power supplies being electrical power supplies. 
    
    
      The invention will now be described, by way of a non-limiting illustrative example, with reference to the accompanying diagrammatic drawings.  
      In the drawings,  
       FIG. 1  shows an exploded schematic side elevation of the various components of a casting assembly according to the invention for casting a light metal artefact in accordance with the process of the invention;  
       FIG. 2  shows an exploded schematic side elevation of the various components of a melting apparatus for use with the casting assembly, for forming a molten charge of light metal, for use in the process of the invention;  
       FIG. 3  is a three-dimensional view of a casting apparatus or installation in accordance with the invention, for casting light metal artefacts, in accordance with the method of the invention;  
       FIG. 4  is a three-dimensional view of a casting facility according to the invention and comprising two casting apparatuses or installations of  FIG. 3 , for casting light metal artefacts in accordance with the method of the invention;  
       FIG. 5  shows a series of simplified schematic side elevations of the casting apparatus or installation of  FIG. 3 , illustrating the method of casting a light metal artefact in the form of a magnesium alloy wheel rim, in accordance with the invention, using the casting apparatus or installation of  FIG. 3 ; and  
       FIG. 6  is another series of simplified schematic side elevation of the casting apparatus or installation of  FIG. 3 , further illustrating the method of casting a light metal artefact in the form of a magnesium alloy wheel rim illustrated by  FIG. 5 . 
    
    
      Referring first to  FIG. 1  of the drawings, reference numeral  10  generally refers to a casting assembly for casting a light metal artefact, in accordance with the invention. The casting assembly  10  comprises a die or mould  12  for casting a light metal artefact in the form of a magnesium alloy wheel rim, and comprises also an induction heating arrangement  14  surrounding the die or mould  12 .  
      The die or mould  12  is a multi-core or segmented re-useable steel die or mould, comprising a top core  16  to which a solidified artefact remains removably attached at the end of the casting process, a bottom—or face core  18  having a centrally located charging opening or passage  20  provided therethrough for charging or filling the die or mould  12  from below, and a segmented ring of four side cores  22  associated with respective pistons  24 , the side cores  22  giving the die or mould  12  its segmented character. The die or mould  12  is hydraulically operated, with regard to the pistons  24  of the side cores  22  and with regard to lifting of the top core  16  and any attached light metal casting (not shown), upwardly and away from the remaining cores.  
      The top core  16  is associated with release means (not shown) for releasing the artefact therefrom at the end of the casting process.  
      The heating arrangement  14  comprises six windings respectively forming induction coils  25 ,  26 ,  27 ,  28 ,  29  and  30 , operable independently of one another, for achieving a desired temperature profile in the die or mould  12 .  
      The casting assembly  10  also includes a purging gas supply shown schematically by broken line  31 , for supplying SF 6 /CO 2  purging gas to the die or mould  12  prior to and during the casting process.  
      Referring now to  FIG. 2  of the drawings, reference numeral  40  generally refers to a melting apparatus for forming a molten charge of light metal, in accordance with the invention. The melting apparatus or installation  40  comprises a hollow low carbon—or mild steel cylinder or sleeve  42  of circular cross-section for holding a molten charge of light metal and also for facilitating heating of a precursor of the charge of light metal, an induction heating arrangement  44  comprising an induction coil  46  for heating contents of the cylinder or sleeve  42  to form a molten charge, and a molten metal transfer assembly  48  for transferring a molten charge of light metal from the cylinder or sleeve  42  to the die or mould  12  in which an artefact is cast.  
      The melting apparatus  40  also includes an inert gas supply  50  for supplying argon gas to the interior of the cylinder or sleeve  42  such that melting of the light metal charge takes place under a substantially inert atmosphere, and also to provide cooling to the lower end or base of the cylinder or sleeve  42  to form a secondary seal therefor as described hereunder.  
      In use, the induction coil  46  is mounted on the metal transfer assembly  48 , the coil  46  being connected to the barrel  62  and surrounding the cylinder or sleeve  42  to heat the contents thereof.  
      The transfer assembly  48  comprises a telescopically moveable multi-stage piston arrangement  52  for use in elevating the cylinder or sleeve  42  to engage lockingly with the periphery of the charging opening  20  of the die or mould  12 , prior to filling the die or mould  12  with a molten charge from the cylinder or sleeve  42 . The multi-stage piston arrangement  52  incorporates a central piston comprising three telescopic piston rods  54 ,  55 ,  56  with the central rod  56  having a piston head  58  provided with a conical sealing surface  59  for sealingly engaging the periphery of the opening  20  into the die or mould  12  when an entire molten charge in the cylinder or sleeve  42  has been transferred from the cylinder or sleeve  42  into the die or mould  12 . The multi-stage piston arrangement  52  includes a variable force and speed controller (not shown) for controlling the rate of movement thereof and also for controlling the upward force exerted by the piston head  58  on a molten charge in the cylinder or sleeve  42  and in the die or mould  12 , when the piston head  58  sealingly engages the periphery of the charging opening  20  of the die or mould  12 .  
      Thus, in use, the cylinder or sleeve  42  is supported on the transfer assembly  48 , such that the multi-stage piston arrangement  52  is moveable within the interior of the cylinder or sleeve  42  in sliding and sufficiently sealing engagement therewith so as to enable a molten charge in the cylinder or sleeve  42  to be pushed upwardly and out of the cylinder or sleeve  42  upon the upward movement of the piston rods  54 ,  55 ,  56 , to transfer and inject the molten charge into the die or mould  12 .  
      The transfer assembly  48  also comprises a plurality of concentric barrels  60 ,  61 ,  62 ,  63  and  64  of different diameters. The barrels  60 ,  61 ,  62 ,  63  and  64  are telescopically vertically displaceable, relative to one another and nest in one another.  
      The barrel  60  is the bottom barrel and has wheels  66  for running on rails  67  forming part of the casting installation of  FIGS. 4-6  for reciprocating the melting apparatus or installation  40  between a charging position where charging of the cylinder or sleeve  42  with a precursor of a molten charge takes place, and a filling position where the melting apparatus  40  is in alignment with the charging opening  20  of the die or mould  12  of the casting assembly  10 , to enable a molten charge formed by melting of a precursor thereof in the cylinder or sleeve  42  to be transferred therefrom into said die or mould  12 , thereby typically filling it with the molten charge. The barrel  64  is the top barrel and provides a circumferentially extending upwardly facing support ring having a groove (not shown) for sealingly engagingly the lower end of the cylinder or sleeve  42  therein. The barrel  62  in turn provides a circumferentially extending upwardly facing support ring on which the induction coil  46  is supported when placed over the cylinder or sleeve  42  to surround it.  
      In addition to the seal provided by the groove on the barrel  64 , the argon gas supplied via the gas supply  50  provides cooling to the lower end of the cylinder or sleeve  42  during melting of the precursor of the molten charge, allowing part of the molten charge formed to solidify in a zone between the piston arrangement  52  and the top barrel  64  and at the lower end of the cylinder or sleeve  42 , thereby providing a secondary seal which is formed of solidified light metal from the molten charge.  
      Referring now to  FIG. 3  of the drawings, reference numeral  70  generally refers to a casting apparatus of installation for casting light metal artefacts, in accordance with the invention. The same parts are assigned the same reference numerals as in  FIGS. 1 and 2 , unless otherwise specified.  
      The casting apparatus or installation  70  comprises a casting assembly  10  as described above and a melting apparatus  40  also as described above. The casting apparatus or installation  70  also includes a die or mould hydraulic controller  72  and a melting apparatus  40  hydraulic controller  74 .  
      The top core  16  is associated with release means (not shown) for releasing the artefact therefrom at the end of the casting process.  
      The casting apparatus or installation  70  also includes a central processing unit (CPU)  76  for monitoring the heating of the induction heating arrangement  14  to achieve the desired temperature profile, and also for providing feedback control to respective power supplies  92  and  94  ( FIG. 4 ) therefor.  
      The casting apparatus or installation  70  also includes rails (not shown but see  67  in  FIG. 2 ) on which the wheels  66  of the metal transfer assembly  48  of the melting apparatus  40  can run. Thus, the melting apparatus  40  is reciprocable relative to the die arrangement  12  between a charging position (as shown in  FIG. 3 ) where charging of the melting apparatus  40  with a precursor of the molten charge takes place, and a filling position (see  FIGS. 5 and 6 ) where transfer of a molten charge from the melting apparatus  40  to the die or mould  12  of the casting assembly  10  takes place.  
      Referring now to  FIG. 4  of the drawings, reference numeral  90  generally refers to a development of the apparatus or installation  70  in the form of a casting facility. The casting facility  90  comprises two casting apparatuses or installations  70 , each comprising a casting assembly  10  having a die or mould  12  in which the casting of the artefact is carried out, and having a melting apparatus  40  for induction melting a charge of light metal. The casting facility  90  also includes a melt induction heating power supply  92 , for example of 100 kW, for separately supplying power to each of the two melting apparatuses  40 , a die induction heating power supply  94 , also for example of 100 kW, for separately supplying power to each casting assembly  10 , a cooling tower (not shown) for providing cooling fluid, and a gas supply control unit  96  for supplying purging gases to the casting assembly  10  and also to the melting apparatuses  40 .  
      It will be appreciated that the casting facility  90  permits two artefacts to be cast simultaneously using casting cycles which are out of phase, the melting apparatuses  40  sharing the common induction heating power supply  92  and the casting facilities  10  sharing the common induction heating power supply  94 . The casting of the artefacts then takes place in respective casting cycles which are sufficiently out of phase to permit such sharing. It will thus be appreciated that the casting facility  90  can be operated in quasi-continuous fashion, in that the casting apparatuses or installations  70  can be used on an alternating basis, with the one having its melting apparatus  40  in its filling position and being used for casting while the other has its melting apparatus  40  in its charging position and is charged with a precursor of the light metal, and being prepared to be reciprocated to its filling position, as soon as the casting process in the other casting apparatus or installation  70  is completed.  
      Referring now to  FIGS. 5 and 6  of the drawings, use of the casting apparatus or installation  70  described above is illustrated with reference to casting a light metal artefact in the form of a magnesium alloy wheel rim  100 , using a precursor in the form of a pre-formed billet or ingot  102  of a magnesium-aluminium-zinc alloy known in the art as AZ91. The billet or ingot  102  is placed on the piston arrangement  52 , with the associated melting apparatus or  40  in its charging position. The cylinder or sleeve  42  is placed over the billet or ingot  102 , such that the lower end of the cylinder or sleeve  42  sealingly engages said groove on the top barrel  64  of the metal transfer assembly  48 . The induction coil  46  is connected to the barrel  62  of the metal transfer assembly  48 , so that placing the cylinder or sleeve  42  and the billet or ingot  102  in position, acts to have them surrounded by the coil  46 .  
      The casting assembly  10  is prepared for casting by lowering the top core  16  such that it engages with the bottom- or face core  18 . The ring of side core segments are then placed in position, using their pistons  24 , to close the die. Purging gas in the form of SF 6 /CO 2  fluxing gas mixture comprising 0.2% by volume SF 6  is fed into the die or mould  12  and the die or mould  12  is heated using the induction coils  25 ,  26 ,  27 ,  28 ,  29  and  30  by electrical power fed from the induction heating power supply  94  using a pre-selected frequency, until the die or mould  12  achieves a required operating temperature, and has a desired temperature profile. The rate of heating can be altered by changing the power input from the power supply  94  and/or by changing the frequency thereof, with a higher frequency resulting in a higher heating rate; and the coils  25 ,  26 ,  27 ,  28 ,  29  and  30  can be selectively operated with different power supplies thereto, to achieve said temperature profile.  
      The melting apparatus  40  is reciprocated with the aid of the wheels  66  on the rails  67  of the casting apparatus or installation  70 , from the charging position where charging of the cylinder or sleeve  42  with the billet or ingot  102  of a molten charge of AZ91 alloy takes place, to a filling position where the melting apparatus  40  is in alignment with the charging opening  20  through the bottom—or face core  18  of the die or mould  12 . The cylinder or sleeve  42  is sealingly engaged with the lower surface of the bottom—or face core  18 , by raising the barrel  64  hydraulically, which also seals the cylinder or sleeve  42  to the barrel  64 . The cylinder or sleeve  42  is purged by a SF 6 /CO 2  purging gas. The billet or ingot  102  is melted under an atmosphere provided by the purging gas introduced to the cylinder or sleeve  42  by the gas supply  50 , until a molten charge of AZ91 alloy is formed. Argon is then used to provide a cooling atmosphere for cooling of the molten charge at the lower end of the cylinder or sleeve  42  to form a secondary seal in the form of a more or less semi-solid or solidified portion or sprue of the light metal (not shown).  
      Once the desired operating temperature and temperature profile have been achieved in the die or mould  12 , and the die or mould  12  has been pressure locked with the aid of the pistons  24  by means of the hydraulic controller  72 , the gas supply to the cylinder or sleeve  42  is cut off and the molten charge is transferred under pressure from the cylinder or sleeve  42  into the die or mould  12  by means of the piston arrangement  52 , thereby filling the die or mould  12  with the molten charge. Prior to and during injection of the molten charge into the die or mould  12 , the die or mould  12  is purged with the abovementioned SF 6 /CO 2  purging/fluxing gas by means of gas supply control unit  96 , which gas also protects the molten surface off the molten charge both in the sleeve  42  and when it enters the die or mould  12 . The piston head  58  locks sealingly against the periphery of the charging opening  20  and partially enters the charging opening  20  to increase the pressure on the molten charge in the die or mould  12 . The die or mould  12  is allowed to cool down and the melting apparatus  40  is disengaged from the die or mould  12 . The melting apparatus  40  is then reciprocated back to its charging position.  
      The die or mould  12  is then opened by hydraulically disengaging the ring of side core segments  22  from one another with the aid of the pistons  24 , and the top core  16  with the solidified wheel rim  100  attached thereto, is lifted, using the controller  72 . The wheel rim  100  is then detached or released from the top core  16  by allowing downwardly directed pins forming part of the release means (not shown) to push the wheel rim  100  downwardly during the raising of the top core  16 .  
      The piston arrangement  52  is lowered and then the barrels of the assembly  20  are retracted, releasing the cylinder or sleeve  42  and the solidified portion or sprue (not shown) of the molten charge which formed the secondary seal for the cylinder or sleeve  42 . The used cylinder or sleeve  42  is then cleaned and re-positioned back on the transfer assembly  48  in preparation for the casting of a new wheel rim  100 . It will be appreciated, however, that a different cylinder or sleeve  42  may instead be used to avoid waste of production time and also to minimise the possibility of cross-contamination.  
      It is an advantage of the invention that the casting apparatus or installation  70  need not necessarily to be of a permanent construction, being moveable from one production facility to another with ease. Thus the casting apparatus or installation  70  may be inexpensively set up close to an end user of the artefacts to be cast, thereby reducing transportation costs, and the like.  
      It is also a further particular advantage of the invention that the induction heating of the die or mould  12  by the heating arrangement comprising the six induction coils  25 ,  26 ,  27 ,  28 ,  29  and  30 , operable independently of one another, enables a desired temperature profile to be obtained in the die or mould  12 , prior to the casting step, thereby having a desirable consequential effect on the solidification rate of the various portions of the artefact, such as the wheel rim  100 , thereby reducing stresses in the solidified artefact (wheel rim  100 ). The attainment of desired flow distances for complete filling of the die or mould  12  are also permitted.  
      It is yet a further advantage of the present invention that the casting apparatus or installation  70  does not require much space for it to be erected. For example, the casting apparatus or installation  70  as described above only requires a floor space of about 20-30 m 2 . The present process also offers other costs benefits such as the fact that power supply only has to be fed to the casting apparatus or installation  70  immediately prior to casting and can be switched off at the end of casting a single artefact, without adversely affecting the process or the efficiencies thereof. In the case of a power failure during the casting process using the method and casting apparatus or installation  70  of the present invention, it will be appreciated that losses need be no greater than loss of the molten charge in the cylinder or sleeve  42 , comprising the single billet or ingot  102 , as compared to a typical foundry where the process is continuous and large amounts of metal have to be molten at any given point in time, all of which can solidify in the event of a power failure. Indeed, losses can in principle be avoided completely by simply re-melting the contents of the cylinder or sleeve  42 , when the power supply is restored.  
      It is a yet a further advantage of the process in accordance with the present invention, that the die or mould  12  of the casting assembly  10  does not require running-in in order to achieve the optimum process conditions. The desired casting temperature profile may be easily obtained by selectively controlling power fed to each of the coils  25 ,  26 ,  27 ,  28 ,  29  and  30 . The fact that the process does not require a running-in cycle or cycles means that a particular number of billets or ingots  102 , barring any power failures, should yield an equivalent number of wheel rims  100 , with reduced wastage arising from reject artefacts and enhanced quality control.