Patent Publication Number: US-2020296802-A1

Title: Fluid heating ceramic heater

Description:
TECHNICAL FIELD 
     The present disclosure relates to a fluid heating ceramic heater used for, for instance, a warm water washing toilet seat, an electric water heater and a 24-hour bath. 
     BACKGROUND ART 
     The warm water washing toilet seat is usually provided with a heat exchange unit having a heat exchanger that is a resin case and a ceramic heater. The ceramic heater is used to warm washing water stored in the heat exchanger. 
     The ceramic heater for the warm water washing toilet seat is always in fluid such as water. Therefore, there arises a problem of adhesion of scale that is derived from calcia and/or magnesia to a surface of the ceramic heater in the process of use. This is understood that since grain-sized asperities or unevenness exist on the surface of the ceramic, the scale adheres to the surface of the ceramic heater. 
     It is known that occurrence of this scale in hard water is more frequent than that in soft water, and the scale is deposited on the surface of the ceramic heater by heating of the water. When the adhesion of the scale to the surface of the ceramic heater proceeds, due to the fact that the scale deposited on the surface of the ceramic heater is peeling off from the ceramic heater, there is a risk that a water channel or pipe will get clogged with the scale. 
     For the above problem, the following Patent Document 1 discloses a configuration of this kind of ceramic heater in which a surface of a tubular ceramic body having a heat generation resistor is coated with a coating layer containing glass as a main component. 
     According to such ceramic heater, since the surface of the ceramic body is coated with the coating layer, the adhesion of the scale to the surface of the ceramic heater can be suppressed. 
     CITATION LIST 
     Patent Document 
     Patent Document 1: Japanese Patent Application No. 2017-020886 
     SUMMARY OF THE INVENTION 
     Technical Problem 
     Here, it is found that when the ceramic heater is used in some sort of hard water over an extended time period, especially an outer coating layer formed on an outer surface of the ceramic body dissolves in the water. For this matter, it is conceivable that by thickening a coating thickness of the coating layer, durability of the coating layer will be secured. On the other hand, as a problem, as the coating thickness of the coating layer is thicker, it becomes more difficult to conduct heat generated from the heat generation resistor to the fluid that passes through or flows through an inside of the ceramic heater. 
     Solution to Problem 
     A fluid heating ceramic heater according to one aspect of the present disclosure comprises a tubular ceramic body having a heat generation resistor; an outer coating layer containing glass as a main component and coating an outer peripheral surface of the ceramic body; and an inner coating layer containing glass as a main component and coating an inner peripheral surface of the ceramic body. And, the inner coating layer is formed so as to be thinner than the outer coating layer. 
     According to such ceramic heater, since the outer peripheral surface and the inner peripheral surface of the tubular ceramic body are respectively coated with the outer coating layer and the inner coating layer each containing the glass as the main component, the adhesion of the scale to the surface of the ceramic heater can be suppressed. 
     In addition, since the inner coating layer is formed so as to be thinner than the outer coating layer, it is possible to efficiently conduct heat generated from the heat generation resistor to fluid that passes through or flows through an inside of the ceramic heater while securing durability of the outer coating layer. 
     In the fluid heating ceramic heater according to one aspect of the present disclosure, the outer coating layer and the inner coating layer could be formed so that both of an arithmetic average surface roughness (Ra) of a surface of the outer coating layer and an arithmetic average surface roughness (Ra) of a surface of the inner coating layer are 0.5 μm or less. 
     According to such ceramic heater, since the grain-sized asperities or unevenness existing on the surface of the ceramic are filled with each coating layer, the adhesion of the scale can be suppressed more effectively. 
     Further, in the fluid heating ceramic heater according to one aspect of the present disclosure, the outer coating layer and the inner coating layer both could contain a component of glaze. 
     According to such ceramic heater, since each coating layer can be formed by applying the glaze to the ceramic heater and baking the glaze, it is possible to simplify a forming process of the coating layer. 
     Furthermore, in the fluid heating ceramic heater according to one aspect of the present disclosure, the ceramic body could have; a ceramic-made support; and a ceramic sheet which is wound around an outer periphery of the support and in which the heat generation resistor is embedded. 
     According to such ceramic heater, since the ceramic body can be obtained by winding the ceramic sheet around the support, heat can be generated in a wide area of the ceramic body as uniformly as possible. 
     In addition, in the fluid heating ceramic heater according to one aspect of the present disclosure, the outer coating layer could be formed so that a thickness of the outer coating layer is thinner than that of the ceramic sheet. 
     According to such ceramic heater, since the thickness of the outer coating layer is thinner than that of the ceramic sheet, it is possible to conduct heat generated by the heat generation resistor to fluid more efficiently. 
     Moreover, in the fluid heating ceramic heater according to one aspect of the present disclosure, the outer coating layer could be formed so as to coat all of a region, where the heat generation resistor is arranged, of the ceramic sheet. 
     According to such ceramic heater, since the outer coating layer covers or coats all of the region, where the heat generation resistor is arranged, of the ceramic sheet, even if the ceramic sheet expands and shrinks due to heat generation of the heat generation resistor and such a force as to unstick the ceramic sheet acts on the ceramic sheet, because the ceramic sheet is covered with the outer coating layer, it is possible to prevent the ceramic sheet from coming unstuck. 
     Additionally, in the fluid heating ceramic heater according to one aspect of the present disclosure, both of the outer coating layer and the inner coating layer could be made of lead-free material. 
     According to such ceramic heater, since each coating layer is made of the lead-free material, it is possible to suppress change of color of the coating layer which is caused by the fact that the material contains the lead when exposed to a reduction atmosphere. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is a front view of a ceramic heater according to an embodiment. 
         FIG. 2  is a sectional view taken along II-II line of  FIG. 1 . 
         FIG. 3  is an explanatory drawing with a ceramic sheet developed. 
         FIG. 4  is an explanatory drawing ( 1 ) showing a method of manufacturing the ceramic heater. 
         FIG. 5  is an explanatory drawing ( 2 ) showing the method of manufacturing the ceramic heater. 
         FIG. 6  is an explanatory drawing ( 3 ) showing the method of manufacturing the ceramic heater. 
         FIG. 7  is an explanatory drawing ( 4 ) showing the method of manufacturing the ceramic heater. 
         FIG. 8  is a local sectional view showing a sectional structure in a top end region of the ceramic heater. 
     
    
    
     EMBODIMENTS FOR CARRYING OUT THE INVENTION 
     Embodiments of the present disclosure will be explained below with reference to the drawings. 
     1. Embodiment 
     [1-1. Configuration] 
     A ceramic heater  11  of the present embodiment is, for instance, a ceramic heater used to warm the washing water in the heat exchanger of the heat exchange unit of the warm water washing toilet seat. 
     As shown in  FIG. 1 , this ceramic heater  11  has a cylindrical ceramic heater body  13  and a flange  15  having an insertion hole at the middle thereof and fitted onto the heater body  13 . The flange  15  is formed with, for instance, ceramic such as alumina. The heater body  13  and the flange  15  are connected or bonded together with glass brazing material  23 . 
     As shown in  FIGS. 1 and 2 , the heater body  13  is structured by a cylindrical ceramic support  17  and a ceramic sheet  19  wound around an outer periphery of the support  17 . The support  17  is shaped into a cylindrical shape having a penetration hole  17 A (see  FIG. 8 ) that penetrates the support  17  in an axial tip end direction. In the present embodiment, the support  17  and the ceramic sheet  19  are made of ceramic such as alumina (Al 2 O 3 ). A thermal expansion coefficient of alumina is within a range from 50×10 −7 /K to 90×10 −7 /K. In the present embodiment, it is 70×10 −7 /K (30° C.˜380° C.) 
     Further, in the present embodiment, an outside diameter of the support  17  is set to 12 mm, an inside diameter of the support  17  is set to 8 mm, and a length of the support  17  is set to 65 mm. A thickness of the ceramic sheet  19  is set to 0.5 mm and a length of the ceramic sheet  19  is set to 60 mm. Here, the ceramic sheet  19  does not completely cover the outer periphery of the support  17 . Therefore, a slit  21  that extends along an axial direction of the support  17  is formed at a winding mating portion  20  of the ceramic sheet  19 . In addition, in the present embodiment, at least a part of a surface of the support  17  and at least a part of a surface of the ceramic sheet  19  are covered or coated with a glaze layer  61 . 
     The glaze layer  61  is formed as glass ceramic that contains 60-74 wt % Si in terms of SiO 2  and 16-30 wt % Al in terms of Al 2 O 3 . That is, the glaze layer  61  is made of lead-free material. Here, the lead-free material means material containing no lead. However, the lead-free material is not limited to material that does not completely contain lead, but could be material that contains a trace quantity of lead as long as the trace quantity of lead is such a quantity that change of color of the material which is caused by the fact that the material contains the lead when exposed to a reduction atmosphere is not visible. 
     The glaze layer  61  is formed by baking applied or coated glaze. The glaze used for the glaze layer  61  of the present embodiment is a glaze whose transition point is 830° C., whose deformation point is 900° C. or higher, whose melting point is 1128° C. and whose thermal expansion coefficient is 60×10 −7 /K (30° C.˜700° C.). 
     The transition point indicates a temperature at which a gradient of a thermal expansion curve changes rapidly. The deformation point indicates a temperature at which spread or elongation of glass can no longer be detected due to softening of the glass in a thermal expansion measurement and this appears as a bending point of the thermal expansion curve. 
     Material of the glaze layer  61  is selected so that the deformation point of the glaze layer  61  is a maximum temperature during use of the ceramic heater  11  or higher. It is noted that specifications of a heater wiring  41  could be determined according to the deformation point of the glaze layer  61 . Here, the maximum temperature during use of the ceramic heater  11  means, for instance, a temperature of the heater wiring  41  when the heater wiring  41  generates heat at a maximum output during use of the ceramic heater  11 . 
     That is, the glaze and the output of the heater wiring  41  etc. are set so that a temperature of the glaze layer  61  does not become a temperature of the deformation point of the glaze or higher by the heater wiring  41 . 
     As shown in  FIGS. 2 and 3 , the heater wiring  41  having a serpentine pattern and a pair of internal terminals  42  are provided inside the ceramic sheet  19 . In the present embodiment, the heater wiring  41  and the internal terminals  42  contain tungsten (W) as a main component. The internal terminals  42  are electrically connected to respective external terminals  43  that are formed on an outer peripheral surface of the ceramic sheet  19  through via conductors (not shown) etc., as shown in  FIG. 1 . 
     The heater wiring  41  has a plurality of wiring portions  44  that extend along the axial direction of the support  17  and connecting portions  45  that connect adjacent two wiring portions  44 . A pair of wiring portions  44  positioned at both end portions when viewing the ceramic sheet  19  from a thickness direction are arranged on opposite sides of the winding mating portion  20  of the ceramic sheet  19  as shown in  FIG. 2 , and a first end of the wiring portion  44  is connected to the internal terminal  42  and a second end of the wiring portion  44  is connected to another second end of the adjacent wiring portion  44  through the connecting portion  45 . 
     Here, the first end indicates an upper end in  FIG. 3 , and the second end indicates a lower end in  FIG. 3 . Further, with regard to the wiring portions  44  arranged between the pair of wiring portions  44  positioned at both end portions when viewing the ceramic sheet  19  from the thickness direction, the first end of the wiring portion  44  is connected to another first end of the adjacent wiring portion  44  through the connecting portion  45 , and the second end of the wiring portion  44  is connected to another second end of the adjacent wiring portion  44  through the connecting portion  45 . 
     As shown in  FIGS. 2 and 3 , a line width W 1  of the wiring portion  44  of the present embodiment is set to 0.60 mm, and a thickness of the wiring portion  44  is set to 15 μm. Likewise, a line width W 2  of the connecting portion  45  of the present embodiment is set to 0.60 mm, and a thickness of the connecting portion  45  is set to 15 μm. That is, the line width W 1  of the wiring portion  44  is the same as the line width W 2  of the connecting portion  45 . Further, the thickness of the wiring portion  44  is also the same as the thickness of the connecting portion  45 . Therefore, a cross-sectional area of the wiring portion  44  is equal to a cross-sectional area of the connecting portion  45 . 
     As shown in  FIG. 2 , in the ceramic sheet  19 , a thickness t from a surface  46  of the wiring portion  44 , which becomes the heater wiring  41  afterwards, to an outer peripheral surface  47  of the ceramic sheet  19  is 0.2 mm. Further, a distance w from an end edge of the wiring portion  44  to an end surface  48  of the ceramic sheet  19  at the winding mating portion  20  is 0.7 mm. Here, the “distance w” is a length along a circumferential direction of the support  17  that is cylindrical in shape. Moreover, a distance L between the pair of wiring portions  44  arranged on opposite sides of the winding mating portion  20  is 2.4 mm. Here, the “distance L” is a length of a straight line that connects both end edges of the pair of wiring portions  44 . A width of the slit  21  formed at the winding mating portion  20  is derived from an expression of “L−2w”, and in the present embodiment, it is 1 mm. 
     Next, as shown in  FIG. 8 , the glaze layer  61  has an outer coating layer  61 A and an inner coating layer  61 B. 
     The outer coating layer  61 A is formed so as to cover or coat at least a forming region of the heater wiring  41  of a cylindrical outer surface (or a tubular outer surface) of the heater body  13  (the support  17  and the ceramic sheet  19 ). The inner coating layer  61 B is formed so as to cover or coat at least a region H, where the heater wiring  41  is arranged, of a cylindrical inner surface (or a tubular inner surface) (an inner surface of the penetration hole  17 A) of the heater body  13  (the support  17  and the ceramic sheet  19 ). 
     Further, the outer coating layer  61 A is formed so as to cover or coat at least a part of a top end side region F that is located at a top end side with respect to the region H, where the heater wiring  41  is arranged, of the heater body  13  (the support  17  and the ceramic sheet  19 ). Furthermore, the inner coating layer  61 B is set so that a maximum value T 1  of a thickness of the inner coating layer  613  in the region H is smaller than a maximum value T 2  of a thickness of the outer coating layer  61 A in the region H (T 1 &lt;T 2 ). 
     1-2. Manufacturing Method 
     Next, a method of manufacturing the ceramic heater  11  will be explained. 
     First, a clay-like slurry containing alumina as a main component is charged into a conventionally known extruder (not shown), and a tubular member is molded. After drying the molded tubular member, the dried molded tubular member undergoes a calcination (a pre-firing or a pre-baking) at a predetermined temperature (e.g. approx. 1000° C.), then the support  17  as shown in  FIG. 4  is obtained. 
     Further, using ceramic material whose main component is alumina powder, first and second ceramic green sheets  51  and  52  which become the ceramic sheet  19  afterwards are formed. As a method of forming the ceramic green sheet, a well-known molding method such as a doctor blade method can be used. 
     Then, using a well-known paste printing device (not shown), a conductive paste is printed on a surface of the first ceramic green sheet  51 . In the present embodiment, as the conductive paste, a tungsten paste is employed. As a result, as shown in  FIG. 5 , an unbaked electrode  53  which becomes the heater wiring  41  and the internal terminals  42  afterwards is formed on the surface of the first ceramic green sheet  51 . A position of the unbaked electrode  53  is adjusted, for instance, so as to be a size obtained by adding shrinkage during baking with respect to a position of the heater wiring  41 . 
     After drying the conductive paste, the second ceramic green sheet  52  is laminated on a printed surface of the first ceramic green sheet  51 , i.e. a surface on which the unbaked electrode  53  is formed, and a pressing force is given to this laminate in a sheet laminating direction. As a result, as shown in  FIG. 6 , the first and second ceramic green sheets  51  and  52  are united, and a green sheet laminate  54  is formed. 
     Here, a thickness of the second ceramic green sheet  52  is adjusted, for instance, so as to be a size obtained by adding shrinkage during the baking with respect to the thickness t from an outermost arranged wiring portion  44  of the wiring portions  44  of the heater wiring  41  to the outer peripheral surface  47  of the ceramic sheet  19 . Further, using the paste printing device, conductive pastes are printed on a surface of the second ceramic green sheet  52 . As a result, unbaked electrodes  55  which become the external terminals  43  afterwards are formed on the surface of the second ceramic green sheet  52 . 
     Next, as shown in  FIG. 7 , ceramic paste such as alumina paste is applied to one side surface of the green sheet laminate  54 , and the green sheet laminate  54  is wound around and bonded to an outer peripheral surface  18  of the support  17 . At this time, a size of the green sheet laminate  54  is adjusted in order for both end port ions of the green sheet laminate  54  not to overlap each other. 
     Next, glaze is applied to a predetermined region that is located at a top end side with respect to the unbaked electrodes  55 . After carrying out a drying process and a degreasing process by a well-known method, a simultaneous baking (or a simultaneous firing) is carried out at a predetermined temperature at which alumina and tungsten of the green sheet laminate  54  can be sintered. The predetermined temperature here is, for instance, about 1400° C.˜1600° C. 
     As a result, alumina in the ceramic green sheets  51  and  52  and tungsten in the conductive paste are simultaneously sintered. Then, the green sheet laminate  54  becomes the ceramic sheet  19 , the unbaked electrode  53  becomes the heater wiring  41  and the internal terminals  42 , and the unbaked electrodes  55  become the external terminals  43 . Also, the glaze layer  61  is formed at the predetermined region that is located at the top end side with respect to the external terminals  43 . 
     With regard to the application of the glaze mentioned above, the glaze is applied to the top end side of the support  17 , for instance, by soaking the top end side of the support  17  with the ceramic sheet  19  sintered, i.e. by soaking an end of the support  17 , which is one end side located away from the external terminals  43 , downward in a vertical direction, in a bath in which the glaze is stored so as to soak the support  17  from the top end side of the support  17  up to a predetermined position of the support  17 . 
     It is noted that the predetermined position indicates, as shown in  FIGS. 1 and 3 , a position that covers or coats all of the region H when a region, where the heater wiring  41  is arranged, of the ceramic sheet  19  is the region H, and also a position at which the external terminals  43  are not covered or coated. In  FIG. 1 , a region shown by a hatch pattern indicates a region where the glaze layer  61  is formed. The region H indicates an area where the heater wiring  41  is arranged with the heater wiring  41  folded back. 
     By this process, the glaze is applied to an outer peripheral surface and an inner peripheral surface of the surface of the heater body  13 . Then, by baking or firing this, the outer peripheral surface and the inner peripheral surface of the surface of the heater body  13  are covered or coated with the glaze layer  61 . That is, the outer coating layer  61 A is formed on the outer peripheral surface of the heater body  13 , and the inner coating layer  61 B is formed on the inner peripheral surface of the heater body  13 . 
     The thickness of the glaze layer  61  can be arbitrarily set by adjusting a viscosity and/or an application amount of the glaze. As a method of applying the glaze, an arbitrary method such as application with a brush and spray coating can be employed. In the present embodiment, a state of application of the glaze, which relates to the thickness of the glaze layer  61 , is adjusted so that the maximum value T 1  of the thickness of the inner coating layer  61 B in the region H is smaller than the maximum value T 2  of the thickness of the outer coating layer  61 A in the region H (T 1 &lt;T 2 ). The thickness of the glaze layer  61  (more specifically, maximum values of the outer coating layer  61 A and the inner coating layer  61 B) is adjusted at a time of the application of the glaze so as to be thinner than a thickness of the green sheet laminate  54 . Further, the maximum value T 2  of the thickness of the outer coating layer  61 A in the region H is adjusted to such a degree that the outer coating layer  61 A does not interfere with insertion of the heater body  13  into the insertion hole of the flange  15  when connecting the heater body  13  to the flange  15 . 
     Afterwards, the external terminals  43  are plated with nickel, then the heater body  13  is obtained. Here, the glaze layer  61  could be formed by applying the glaze to the sintered heater body  13  and baking this. 
     Next, the flange  15  made of alumina is fitted onto the heater body  13  at a predetermined fixing position of the heater body  13 . 
     At this time, as shown in  FIG. 1 , the heater body  13  and the flange  15  are fixed together by welding through the glass brazing material  23 , then the ceramic heater  11  is completed. 
     1-3. Example of Experiment 
     An example of experiment that was carried out to evaluate performance of the ceramic heater  11  of the present embodiment will be explained below. 
     First, measurement samples were prepared as follows. As a sample of the embodiment, a ceramic heater, called sample A, was prepared as follows; a thickness t from the surface of the heater wiring to the outer peripheral surface of the ceramic sheet is 0.18 mm, a distance w from the end edge of the heater wiring to the end surface of the ceramic sheet is 0.6 mm, a distance L between the pair of wiring portions arranged on opposite sides of the winding mating portion is 1.4 mm, a width L−2w) of the slit formed at the winding mating portion is 0.2 mm, and the glaze is applied and formed so that the inner coating layer is thinner than the outer coating layer. Here, regarding a definition of the thickness t, the distance w and the distance L, it is the same as a definition of those shown in  FIG. 2 . 
     Further, as a sample of a comparative example, a ceramic heater, called sample B, was prepared as follows; the glaze is applied and formed so that the inner coating layer is thicker than the outer coating layer. A difference between the sample A and the sample B is only a thickness relationship between the inner coating layer and the outer coating layer, and other structures are the same. 
     Each cross-section of the samples A and B was obtained by a SEM, and an arithmetic average surface roughness (Ra) of each of the glaze layer and the surface of the ceramic sheet and each thickness in the laminating direction were identified from cross-sectional SEM images obtained. As a result, both of an arithmetic average surface roughness (Ra) of a surface of the outer coating layer of the sample A and an arithmetic average surface roughness (Ra) of a surface of the inner coating layer of the sample A were 0.5 μm or less. A result of the sample B was the same as that of the sample A. Each thickness of the outer coating layers of the samples A and B was about 100 μm, which is thinner than those of the respective ceramic sheets. A thickness of the inner coating layer of the sample A was about 10 μm. 
     When carrying out an endurance test of the ceramic heaters of the samples A and B by operating the ceramic heaters in hard water (hardness of 480 mg/l) with the water flowing for 350 hours of an energization time under the same conditions, there was no adhesion of the scale in both of the samples A and B. Further, a result obtained showed that a water temperature of the sample A is increased fast as compared with the sample B. Each thickness of the outer coating layers of the samples A and B after the endurance test was thinner by about 16 μm. Meanwhile, there was no change in thickness of the inner coating layer of the both samples A and B. 
     From the above result, it is found that by securing the outer coating layer with the coating thickness of 20 μm or more, durability of the outer coating layer is secured. In addition, it is also found that by forming the coating layer so that the inner coating layer is thinner than the outer coating layer, the water temperature can be efficiently increased. 
     2. Other Embodiments 
     Although the present disclosure has been explained according to the embodiment described above, the present disclosure is not limited to the above embodiment, but includes various modifications. 
     (2a) In the above embodiment, although type of voltage applied between the pair of internal terminals  42  is not specified, AC voltage can be applied between the pair of internal terminals  42 , and DC voltage can be applied between the pair of internal terminals  42 . 
     (2b) In the above embodiment, the glaze layer  61  is formed at the ceramic heater  11 . However, this is not limited to the glaze layer  61 . For instance, a coating layer having glass as a main component and containing a trace quantity of metal such as iron as a mixture could be formed at the ceramic heater  11 . 
     (2c) The above embodiment specifies that the maximum temperature during use of the ceramic heater  11  is the maximum temperature of the heater wiring  41  when the heater wiring  41  generates heat during use of the ceramic heater  11 . However, even if the maximum temperature of the heater wiring  41  exceeds the temperature of the deformation point of the glaze layer  61 , there is no problem as long as a temperature of the coating layer  61  becomes the deformation point of the glaze layer  61  or lower. That is, the maximum temperature during use of the ceramic heater  11  could be a maximum temperature of the glaze layer  61 . 
     (2d) In the above embodiment, the setting is made so that the deformation point of the glaze layer  61  is the deformation point of the glass brazing material  23  or higher or the maximum temperature during use of the ceramic heater  11  or higher. However, the setting is not limited to this. For instance, in a case where a metallized layer is formed on the outer peripheral surface of the heater body  13  and a metal flange is connected or bonded on the metallized layer using metal brazing material, the setting could be made so that the deformation point of the glaze layer  61  is a melting point of the metal brazing material or higher. Although change of color of the glaze may occur if the glaze contains lead, since the connection (or bonding) is carried oud in a reduction atmosphere in order for the metal brazing material not to oxidize and the glaze layer  61  used in the present embodiment is made of lead-free material, it is possible to suppress the change of color which is caused by the fact that the lead exists in the reduction atmosphere. Further, the setting could be made so that the transition point of the glaze layer  61  is the transition point of the glass brazing material  23  or higher or the maximum temperature during use of the ceramic heater  11  or higher. Moreover, the setting could be made so that a softening point of the glaze layer  61  is a softening point of the glass brazing material  23  or higher or the maximum temperature during use of the ceramic heater  11  or higher. 
     (2e) A plurality of functions which one component of the above embodiment has could be realized by a plurality of components, and one function which one component of the above embodiment has could be realized by a plurality of components. Further, a plurality of functions which a plurality components have could be realized by one component, and one function realized by a plurality components could be realized by one component. In addition, a part of the above configuration or structure could be omitted. Moreover, at least a part of the above configuration or structure could be added to a configuration or structure of other embodiment described above, or might be replaced. The present disclosure includes all design modifications and equivalents belonging to the technical scope of the present disclosure. 
     (2f) The present disclosure can be realized by not only the above ceramic heater  11 , but also various aspects such as a system having the ceramic heater  11  as a component. 
     3. Correspondence of Term 
     The heater wiring  41  corresponds to an example of a heat generation resistor, and the heater body  13  corresponds to an example of a ceramic body. Further, the glaze layer  61  corresponds to an example of a coating layer, and the glass brazing material  23  corresponds to an example of a connecting or bonding material. 
     EXPLANATION OF REFERENCE 
     
         
           11  . . . ceramic heater,  13  . . . heater body,  15  . . . flange,  15 A . . . insertion hole,  17  . . . support,  17 A penetration hole,  17 B . . . top end surface,  18  . . . outer peripheral surface,  19  . . . ceramic sheet,  19 A . . . stepped portion,  20  . . . winding mating portion,  21  . . . slit,  23  . . . glass brazing material,  41  . . . heater wiring,  61  . . . glaze layer,  61 A . . . outer coating layer,  61 B . . . inner coating layer