Patent Publication Number: US-2022212986-A1

Title: Manufacturing method of glass article and glass article

Description:
CROSS-REFERENCE TO RELATED APPLICATION 
     The present application is a divisional application of U.S. Ser. No.. 16/282,373 filed Feb. 22, 2019, allowed, which is a continuation application filed under 35 U.S.C. 111(a) claiming benefit under 35 U.S.C. 120 and 365(c) of PCT International Application No. 
     PCT/JP2017/028070 filed on Aug. 2, 2017 and designating the U.S., which claims priority of Japanese Patent Application No. 2016-171296 filed on Sep. 1, 2016. The entire contents of the foregoing applications are incorporated herein by reference. 
    
    
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The disclosure herein generally relates to a manufacturing method of a glass article having an organic film, and a glass article having an organic film. 
     2. Description of the Related Art 
     In manufacturing processes of various glass articles, a step of separating and obtaining a glass article or two or more glass articles from a large-sized glass plate, a so-called separation step, may be often required. 
     In such a separation step, an operation of forming a scribe line by machining at a specified position in a main surface of a glass plate, and applying a bending moment to the glass plate along the scribe line, to cut the glass plate, is often performed. 
     Moreover, recently, a method of irradiating a glass plate with a laser light of a CO 2  laser that is a gas laser, and fusion cutting the glass plate into a specified size with an incident heat from the laser light of the CO 2  laser, to separate and obtain a glass article, has been proposed (See, for example, Japanese Translation of PCT international application publication No. 2012-526721). Note that another method of separating and obtaining a glass article includes a method using a gas laser such as an excimer laser, an argon (Ar) laser or a helium (He)-neon 
     (Ne) laser, a solid-state laser such as a YAG laser, a semiconductor laser, or a free electron laser. 
     SUMMARY OF THE INVENTION 
     Technical Problem 
     As described above, a method of separating a glass article from a glass plate, by irradiating the glass plate with a laser light, and fusion cutting the glass plate at a specified position, has been known. 
     However, among the glass articles, there exist many glass articles having a variety of organic films on their main surfaces. For example, when cover glasses for mobile electronic devices are manufactured, organic films such as anti-fingerprint (AFP) films may be arranged on glass plates. When the separation step, as disclosed in Japanese Translation of PCT international application publication No. 2012-526721, is performed for glass plates having such organic films, there is a problem that the organic films may be damaged by incident heat from a laser light, particularly at end faces. 
     Note that in order to deal with the problem, after separating a glass substrate from a glass plate, an organic film may be deposited on a surface of the separated glass substrate. 
     However, in such a method, it is necessary to handle many glass substrates in the deposition step, and the step becomes complicated. Then, the manufacturing efficiency for the glass articles is reduced. Thus, the method is not a fundamental solution for the aforementioned problem. 
     The present invention was made in view of such a problem, and it is an object of the present invention to provide a manufacturing method of a glass article, in which an organic film arranged on a main surface can be prevented from being damaged significantly, when the glass article is separated from a glass plate. Moreover, it is an object of the present invention to provide a glass article, in which an organic film is prevented from being damaged significantly. 
     Solution to Problem 
     According to an aspect of the present invention, a manufacturing method of a glass article having an organic film including 
     a step (1) of irradiating a first main surface of a glass plate having the first main surface and a second main surface, opposite each other, with a laser light of a first laser, 
     to form an in-plane void region, in which a plurality of voids are arrayed, on the first main surface, and 
     to form a plurality of internal void arrays, each including a void or two or more voids arrayed from the in-plane void region to the second main surface, in the glass plate; 
     a step (2) of depositing the organic film on the first main surface or the second main surface of the glass plate; and 
     a step (3) of irradiating and scanning the first main surface or the second main surface of the glass plate, on which the organic film was deposited, with a laser light of a second laser that is different from the first laser, along the in-plane void region or a neighborhood of the in-plane void region, 
     to separate one glass article or two or more glass articles from the glass plate along the in-plane void region, 
     in the step (3), the first main surface or the second main surface being irradiated with the laser light of the second laser so that 
     when a central portion of a surface of the organic film of the separated glass article on the first main surface side is MC, and a point in an end face of the glass article in a top view is MP (in a case where the glass article has an approximately polygonal shape, MP is a point in the end face other than intersection portions of two adjacent sides of a polygon), 
     at the point MP, a count number for fluorine and a count number for silicon obtained by an X-ray photoelectron spectroscopy (XPS) are I MP  (F) and I MP  (Si), respectively, and R MP  is a ratio of the count number I MP  (F) to the count number I MP  (Si), and 
     at the central portion MC, a count number for fluorine and a count number for silicon obtained by the X-ray photoelectron spectroscopy (XPS) are I MC  (F) and I MC  (Si), respectively, and R MC  is a ratio of the count number I MC  (F) to the count number I MC  (Si), 
     a ratio of the ratio R MP  to the ratio R MC  is 0.3 or more, is provided. 
     Moreover, according according to an another aspect of the present invention, a manufacturing method of a glass article having an organic film including 
     a step (1) of depositing the organic film on a first main surface of a glass plate having the first main surface and a second main surface, opposite each other; 
     a step (2) of irradiating the first main surface of the glass plate with a laser light of a first laser, 
     to form an in-plane void region, in which a plurality of voids are arrayed, on the first main surface, and 
     to form a plurality of internal void arrays, each including a void or two or more voids arrayed from the in-plane void region to the second main surface, in the glass plate; and 
     a step (3) of irradiating and scanning the first main surface of the glass plate with a laser light of a second laser that is different from the first laser, along the in-plane void region or a neighborhood of the in-plane void region, 
     to separate one glass article or two or more glass articles from the glass plate along the in-plane void region, 
     in the step (3), the first main surface being irradiated with the laser light of the second laser so that 
     when a central portion of a surface of the organic film of the separated glass article on the first main surface side is MC, and a point in an end face of the glass article in a top view is MP (in a case where the glass article has an approximately polygonal shape, MP is a point in the end face other than intersection portions of two adjacent sides of a polygon), 
     at the point MP, a count number for fluorine and a count number for silicon obtained by an X-ray photoelectron spectroscopy (XPS) are I MP  (F) and I MP  (Si), respectively, and R MP  is a ratio of the count number I MP  (F) to the count number I MP  (Si), and 
     at the central portion MC, a count number for fluorine and a count number for silicon obtained by the X-ray photoelectron spectroscopy (XPS) are I MC  (F) and I MC  (Si), respectively, and R MC  is a ratio of the count number I MC  (F) to the count number I MC  (Si), 
     a ratio of the ratio R MP  to the ratio R MC  is 0.3 or more, is provided. 
     Furthermore, according to a yet another aspect of the present invention, a glass article including 
     a glass substrate having a first main surface and a second main surface, opposite each other, and an end face; and 
     an organic film arranged on the first main surface of the glass substrate, 
     when a central portion of a surface of the organic film on the first main surface side is MC, and a point in the end face in a top view is MP (in a case where the first main surface has an approximately polygonal shape, MP is a point in the end face other than intersection portions of two adjacent sides of a polygon), 
     at the point MP, a count number for fluorine and a count number for silicon obtained by an X-ray photoelectron spectroscopy (XPS) are I MP  (F) and I MP  (Si), respectively, and R MP  is a ratio of the count number I MP  (F) to the count number I MP  (Si), and 
     at the central portion MC, a count number for fluorine and a count number for silicon obtained by the X-ray photoelectron spectroscopy (XPS) are I MC  (F) and I MC  (Si), respectively, and R MC  is a ratio of the count number I MC  (F) to the count number I MC  (Si), 
     a ratio of the ratio R MP  to the ratio R MC  being 0.3 or more, is provided. 
     Effect of Invention 
     According to an aspect of the present invention, a manufacturing method of a glass article, in which an organic film arranged on a main surface can be prevented from being damaged significantly, when the glass article is separated from a glass plate, can be provided. Moreover, according to another aspect of the present invention, a glass article, in which an organic film is prevented from being damaged significantly, can be provided. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       Other objects and further features of embodiments will become apparent from the following detailed description when read in conjunction with the accompanying drawings, in which: 
         FIG. 1  is a flowchart schematically depicting an example of a flow of a manufacturing method of a glass article according to an embodiment of the present invention; 
         FIG. 2  is a diagram schematically depicting an example of a form of a glass plate that can be used in the manufacturing method of the glass article according to the embodiment of the present invention; 
         FIG. 3  is a diagram for schematically explaining a form of an in-plane void region and an internal void array; 
         FIG. 4  is a diagram schematically depicting an example of a form of the in-plane void region; 
         FIG. 5  is a diagram schematically depicting an example of a state where a plurality of in-plane void regions are formed on a first main surface of the glass plate; 
         FIG. 6  is a diagram schematically depicting an example of the in-plane void region; 
         FIG. 7  is a diagram schematically depicting another example of the in-plane void region; 
         FIG. 8  is a diagram schematically depicting a profile of an introduced ion concentration in an in-plane direction of a virtual end face (corresponding to a thickness direction of the glass plate) according to the embodiment of the present invention; 
         FIG. 9  is a diagram schematically depicting an example of a state where an organic film is formed on the first main surface of the glass plate; 
         FIG. 10  is a diagram schematically depicting another example of the state where the organic film is formed on the first main surface of the glass plate; 
         FIG. 11  is a diagram schematically depicting yet another example of the state where the organic film is formed on the first main surface of the glass plate; 
         FIG. 12  is a flowchart schematically depicting another example of the flow of the manufacturing method of the glass article according to the embodiment of the present invention; 
         FIG. 13  is a perspective view schematically depicting an example of the glass article according to the embodiment of the present invention; 
         FIG. 14  is a cross-sectional view schematically depicting the glass article cut along a line A-A in  FIG. 13 ; and 
         FIG. 15  is a diagram depicting an example of a result of an XPS analysis for an organic film of a sample according to Example 1. 
     
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     In the following, embodiments for implementing the present invention will be described with reference to the accompanying drawings. 
     Manufacturing Method of a Glass Article According to an Embodiment of the Present Invention 
     With reference to  FIGS. 1 to 11 , a manufacturing method of a glass article according to an embodiment of the present invention will be described. 
       FIG. 1  is a flowchart schematically depicting an example of a flow of the manufacturing method of the glass article according to the embodiment of the present invention (in the following, will be referred to as a “first manufacturing method”). 
     As illustrated in  FIG. 1 , the first manufacturing method includes: 
     a laser irradiation step (1) of, in a glass plate having a first main surface and a second main surface, opposite each other, irradiating the first main surface of the glass plate with a laser light of a first laser (step S 110 ); 
     a deposition step (2) of depositing an organic film on the first main surface or the second main surface of the glass plate (step S 120 ); and 
     a separation step (3) of irradiating the main surface of the glass plate, on which the organic film was deposited, with a laser light of a second laser that is different from the first laser, to separate one glass article or two or more glass articles from the glass plate (step S 130 ). 
     In the following, with reference to  FIGS. 2 to 11 , the processes will be described. Note that  FIGS. 2 to 11  are diagrams schematically depicting the steps of the first manufacturing method. 
     Step S 110   
     First, a glass plate having a first main surface and a second main surface, opposite each other, is provided. 
     A glass composition of the glass plate is not particularly limited. For example, the glass plate may be configured of a soda lime glass, and an alkali aluminosilicate glass. 
     A thickness of the glass plate is not particularly limited. For example the thickness may fall within a range of 0.03 mm to 6 mm. 
       FIG. 2  is a diagram schematically depicting an example of a configuration of the glass plate  110 . The glass plate  110  has a first main surface  112  and a second main surface  114 , opposite each other, and an end face  116 . 
     Note that a form of the glass plate  110  is not particularly limited. For example, the glass plate  110  may have various forms, in addition to an approximately rectangular shape, illustrated in  FIG. 2 , such as a polygonal shape, or an elliptical shape (including a circular shape). 
     Next, the glass plate  110  is irradiated with laser light of a first laser. Laser light of the first laser is emitted to one of the main surfaces of the glass plate  110  (in the following, assumed to be the first main surface  112 , as an example). Note that it is necessary to pay attention to the point that the first laser used here is different from a CO 2  laser which may be used in the separation step (step S 130 ), described later. 
     According to the irradiation with laser light of the first laser, on the first main surface  112  of the glass plate  110 , an in-plane void region is formed. Moreover, below the in-plane void region, i.e. toward the second main surface  114 , a plurality of internal void arrays are formed. 
     The “in-plane void region” means a region having a linear shape formed by arraying a plurality of surface voids in a predetermined arrangement. Moreover, the “internal void array” means a region having a linear shape inside the glass plate, formed by arraying a void or two or more voids from the first main surface  112  toward the second main surface  114 . 
     In the following, with reference to  FIG. 3 , configurations of the “in-plane void region” and the “internal void array” will be described in more detail.  FIG. 3  is a diagram schematically depicting the in-plane void region and the internal void array formed in the glass plate. 
     As illustrated in  FIG. 3 , in the glass plate  110 , an in-plane void region  130  and a plurality of internal void arrays  150  corresponding to the in-plane void region  130  are formed. 
     As described above, the in-plane void region  130  means a region having a linear shape in which a plurality of surface voids  138  are arrayed in a predetermined arrangement. For example, in  FIG. 3 , a plurality of surface voids  138  are arrayed in a fixed direction (X-axis direction), and thereby the in-plane void region  130  are formed. 
     The surface void  138  corresponds to an irradiation position on the first main surface  112  with laser light of the first laser, and has a diameter that falls within a range from 1 μm to 5 μm. However, the diameter of the surface void  138  varies depending on irradiation conditions with laser light of the first laser, a type of the glass plate  110 , and the like. 
     A distance between centers P of surface voids  138  adjacent to each other is optionally determined based on the composition and thickness of the glass plate  110 , a laser process condition, or the like. For example the distance between centers P may fall within a range from 2 μm to 10 μm. Note that the distance between centers P of surface voids  138  is not required to be the same at all positions, and may be different depending on the position. That is the surface voids  138  may be arrayed at irregular intervals. 
     As described above, the internal void array  150  means a region having a linear shape formed by arraying a void or two or more voids  158  from the first main surface  112  toward the second main surface  114  inside the glass plate  110 . 
     A shape, a dimension and a pitch of the void are not particularly limited. For example, the void  158  may have a shape of a circle, an ellipse, a rectangle or a triangle viewed from the Y-axis direction. Moreover, the greatest dimension of the void  158  viewed from the Y-axis direction (typically, corresponding to a length of the void  158  in the direction in which the internal void array  150  extends) may fall, for example, within a range from 0.1 μm to 1000 μm. 
     The surface void  138  configuring the in-plane void region  130  has an internal void array  150  which corresponds to the surface void  138 . For example, in  FIG. 3, 18  internal void arrays  150  are formed correspondingly to 18 surface voids  138 . 
     Note that, in  FIG. 3 , voids  158  configuring an internal void array  150  are arrayed in a thickness direction of the glass plate  110  (Z-axis direction). That is, the the internal void array  150  extends in the Z-axis direction. However, the above configuration is merely an example, and the voids configuring the internal void array  150  may be arrayed from the first main surface  112  to the second main surface  114  in a state where the voids are inclined relative to the Z-axis direction. 
     Moreover, in the example illustrated in  FIG. 3 , the internal void array  150  is configured of an array of three voids  158  except for the surface void  138 . However, the above-described configuration is merely an example, and the internal void array  150  may be configured of one void, two voids, or four or more voids  158 . Moreover, the number of voids  158  included in the internal void array  150  may be different. Furthermore, some voids  158  may be coupled to the surface void  138 , to form a “long” surface void  138 . 
     Furthermore, the internal void array  150  may have a void that opens on the second main surface  114  (second surface void), and may not have the second surface void. 
     Note that, as is clear from the aforementioned description, it is necessary to pay attention to the point that the in-plane void region  130  is not a region formed as an actual continuous “line”, but indicates a virtual region having a linear shape formed when the surface voids  138  are connected. 
     Similarly, it is necessary to pay attention to the point that the internal void array  150  is not a region formed as an actual continuous “line”, but indicates a virtual region having a linear shape formed when the voids  158  are connected. 
     Furthermore, one in-plane void region  130  is not necessarily required to be recognized as one “line” (array of the surface voids  138 ), but one in-plane void region  130  may be formed as an aggregate of a plurality of parallel “lines” that are arranged in a state of being close to each other. 
       FIG. 4  is a diagram depicting an example of the in-plane void region  130  that is recognized as such an aggregate of a plurality of “lines”. In this example, on the first main surface  112  of the glass plate  110 , two surface void arrays  138 A and  138 B parallel to each other are formed, and thereby one in-plane void region  130  is configured. A distance between the two surface void arrays  138 A and  138 B is, for example, 5 μm or less, and is preferably 3 μm or less. 
     Note that, in an example illustrated in  FIG. 4 , the in-plane void region  130  is configured of two surface void arrays  130 A and  130 B. However, the in-plane void region  130  may be configured of three or more surface void arrays. 
     In the following, the in-plane void region configured of a plurality of surface void arrays, in this way, will be particularly referred to as a “multi-line in-plane void region”. Moreover, the in-plane void region  130  configured of one surface void array, as illustrated in  FIG. 3 , will be particularly referred to as a “single line in-plane void region”, and will be distinguished from the “multi-line in-plane void region”. 
     The in-plane void region  130  and the internal void array  150 , as described above, can be formed by irradiating the first main surface  112  of the glass plate  110  with laser light of a first laser under a specified condition. 
     More specifically, by irradiating a first position in the first main surface  112  of the glass plate  110  with laser light of the first laser, a first internal void array including a first surface void is formed from the first main surface  112  to the second main surface  114 . Then, the position in the glass plate of irradiation with laser light is changed to a second position, and by irradiating the second position of the first main surface  112  of the glass plate  110  with laser light of the first laser, a second internal void array including a second surface void is formed from the first main surface  112  to the second main surface  114 . By repeating the operation, the in-plane void region  130  and the internal void array  150  corresponding to the in-plane void region  130  can be formed. 
     Note that, in the case where the internal void array having the void  158  sufficiently close to the second main surface  114  is not formed by one operation of irradiation with laser light, i.e. a void closest to the second main surface  114 , among the voids  158 , remains sufficiently far from the second main surface  114  (For example, a distance from the void closest to the second main surface  114  to the first main surface  112  is a half or less of the thickness of the glass plate  110 ) or the like, two or more operations of irradiation with laser light may be performed at substantially the same position of irradiation. Note that “substantially the same position (of irradiation)” includes, in addition to the case where two positions completely coincide with each other, the case where two positions are shifted slightly (e.g. 3 μm at a maximum) from each other. 
     For example, a “deeper” internal void array  150  may be formed as follows. That is, after forming the first in-plane void region  130  and the internal void array  150  corresponding to the first in-plane void region  130  by performing a plurality of operations of irradiation with laser light in a first direction parallel to the first main surface  112  of the glass plate  110  (first path), an operation of irradiation with laser light is performed almost in the same direction as in the first path and almost at the same position of irradiation as in the first path (second path). Thus, the “deeper” internal void array  150  corresponding to the first in-plane void region  130  is formed. 
     Although it depends on the thickness of the glass plate  110 , a distance from a center of the void, located at the closest position to the second main surface  114  among the voids  158  configuring the internal void array  150 , to the second main surface  114  preferably falls within a range from 0 μm to 10 μm. 
     The first laser that can be used in the aforementioned process includes, for example, a short pulsed laser with a pulse width of a femtosecond order to a nanosecond order, i.e. 1.0×10 to 9.9×10 −9  seconds. Furthermore, laser light of the short pulsed laser is preferably a burst pulsed light so that internal voids are formed effectively. Moreover, an average output power of such a short pulsed laser within the irradiation period is, for example, 30 W or more. In the case where the average output power of the short pulsed laser is less than 10 W, satisfactory voids may not be formed. For example, a burst pulsed laser light, that forms one internal void array with 3 to 10 pulses, includes a laser light of a laser with an output power of about 90% of the rated power (50 W), with a burst frequency of about 60 kHz, and with a burst time width of 20 picoseconds to 165 nanoseconds. The burst time width preferably falls within a range from 10 nanoseconds to 100 nanoseconds. 
     Moreover, an irradiation method with laser light includes, a method using a self-focusing of a beam based on the Kerr-effect, a method using a Gaussian Bessel beam with an axicon lens, a method using a line focusing beam formed by an aberration lens, and the like. In any case, any method can be employed as long as an in-plane void region and an internal void array can be formed. 
     For example, in the case of using the burst laser apparatus, by changing the irradiation conditions with laser light of the first laser appropriately, a dimension of a void configuring the internal void array  150 , a number of voids  158  included in the internal void array  150 , and the like can be changed to a certain extent. 
     Note that in the following description, a plane including the in-plane void region  130 , and the internal void array  150  corresponding to the in-plane void region  130  (a plane  165  indicated by hatching in  FIG. 3 ) will be referred to as a “virtual end face”. The virtual end face  165  substantially corresponds to an end face of the glass article manufactured by the first manufacturing method. 
       FIG. 5  is a diagram schematically depicting an example of a state where a plurality of in-plane void regions  130  are formed on the first main surface  112  of the glass plate  110 . 
     In the example illustrated in  FIG. 5 , on the first main surface  112  of the glass plate  110 , five in-plane void regions  130  in the horizontal direction (X-axis direction) and five in-plane void regions  130  in the vertical direction (Y-axis direction) are formed. Moreover, although it is unviewable in  FIG. 5 , a plurality of internal void arrays, in which one void or two or more voids are intermittently arranged toward the second main surface  114 , below the in-plane void region  130 , i.e. on the second main surface  114  side, are formed. 
     In  FIG. 5 , a virtual portion defined by two in-plane void regions  130  arranged closely to each other in the vertical direction of the glass plate  110 , two in-plane void regions  130  arranged closely to each other in the horizontal direction, and internal void arrays corresponding to the in-plane void regions, i.e. the smallest unit of a virtual portion surrounded by four virtual end faces, will be referred to as a glass piece. 
     A shape of the in-plane void region  130 , and a shape of the glass piece  160   a  substantially correspond to a shape of a glass article obtained after the process of step S 130 . For example, in  FIG. 5 , from the glass plate  110 , finally 16 glass articles each having a rectangular shape are manufactured. Moreover, as described above, a virtual end face  165 , including in-plane void regions  130  and internal void arrays  150  corresponding to the in-plane void regions, corresponds to one end face of a glass article manufactured after the process of step S 130 . 
     Note that the shape and the arrangement form of the glass piece  160   a,  illustrated in  FIG. 5 , are merely examples. The glass piece  160   a  can be formed in a predetermined shape and in a predetermined arrangement, according to a shape of a final product of the glass article. 
       FIG. 6  and  FIG. 7  are diagrams schematically depicting examples of another mode of a possible in-plane void region and furthermore a glass piece. 
     In the example illustrated in  FIG. 6 , each in-plane void region  131  is arranged as a closed line (loop) having an approximately rectangular shape, and curved portions at corners. Thus, a glass piece  160   b  surrounded by the in-plane void region  131  and internal void arrays (invisible) has a form of an approximately rectangular plate shape with curved portions at corners. 
     Moreover, in in the example illustrated in  FIG. 7 , each in-plane void region  132  is arranged as a closed line (loop) having an approximately elliptical shape. Thus, a glass piece  160   c  has an approximately disk-shaped form. 
     Moreover, in the aforementioned examples, a continuous end face of the glass article is formed by one virtual end face. Thus, each of the obtained glass articles has only one end face. 
     In this way, each of the in-plane void regions  130 ,  131  and  132  may be formed of a straight line, a curved line or a combination thereof. Moreover, each of the glass pieces  160   a,    160   b,  and  160   c  may be surrounded by a single virtual end face, or a plurality of virtual end faces. 
     Chemical Strengthening Process 
     In the case where the glass plate  110  includes an alkali metal, after step S 110  and before step S 120 , a chemical strengthening process may be performed for the glass plate  110 . 
     The chemical strengthening process is a process in which a glass plate is immersed in a molten salt including alkali metals, to replace alkali metal ions existing on a surface of the glass plate  110  having smaller atomic radii by alkali metal ions existing in the molten salt having greater atomic radii. 
     The conditions for the chemical strengthening process are not particularly limited. For example, the chemical strengthening process may be performed by immersing the glass plate  110  in a molten salt at a temperature of 430 C to 500 C for a period that falls within a range from 1 minute to 2 hours. 
     For the molten salt, a nitrate salt may be used. For example, in the case of replacing lithium ions contained in the glass plate  110  by alkali metal ions having greater sizes, a molten salt including at least one of sodium nitrate, potassium nitrate, rubidium nitrate and cesium nitrate may be used. Moreover, in the case of replacing sodium ions contained in the glass plate  110  by alkali metal ions having greater sizes, a molten salt including at least one of potassium nitrate, rubidium nitrate and cesium nitrate may be used. Furthermore, in the case of replacing potassium ions contained in the glass plate  110  by alkali metal ions having greater sizes, a molten salt including at least one of rubidium nitrate and cesium nitrate may be used. 
     By performing the chemical strengthening process for the glass plate  110 , a compression stress layer can be formed on the first main surface  112  and the second main surface  114 , and thereby strength of the first main surface  112  and of the second main surface  114  can be enhanced. A thickness of the compression stress layer corresponds to a penetration depth of the alkali metal ions for replacing. For example, in the case of replacing sodium ions by potassium ion by using potassium nitrate, for a soda lime glass a compression stress layer with a thickness that falls within a range of 8 μm to 27 μm can be formed, and for an alumino-silicate glass a compression stress layer with a thickness that falls within a range from 10 μm to 100 μm can be formed. In the case of the alumino-silicate glass, a depth that alkali metal ions penetrate is preferably 10 μm or more, and more preferably 20 μm or more. 
     In the glass plate  110  before performing the chemical strengthening process, by the aforementioned laser irradiation process (step S 110 ), the aforementioned in-plane void regions  130 ,  131 , and  132 , and the internal void arrays  150  are formed. Thus, when the chemical strengthening process is performed, the molten salt is introduced into an inside of the glass plate  110  via the surface voids  138  and voids  158 . 
     As a result, according to the chemical strengthening process, in addition to the exposed surface of the glass plate  110  (i.e. the first main surface  112 , the second main surface  114 , and end face  116 ), the strength of the virtual end face can be enhanced. 
       FIG. 8  is a diagram schematically depicting a profile of an introduced ion concentration in an “in-plane direction” of the virtual end face (the thickness direction of the glass plate  110 . See Z-axis direction indicated in  FIG. 3 ). 
     The “introduced ion” means alkali metal ions introduced into the glass plate  110  by the chemical strengthening process, i.e. alkali metal ions for adding compression stress layers on the first main surface  112  and the second main surface  114  of the glass plate  110 , to enhance the strength of the main surfaces. 
     In  FIG. 8 , the horizontal axis indicates a relative position t (%) in the thickness direction of the glass plate  110 . The first main surface  112  corresponds to t=0%, and the second main surface  114  corresponds to t=100%. The vertical axis indicates a concentration C of the introduced ion. Note that the concentration C was calculated by subtracting a concentration of alkali metal ions of the same type as the introduced ions that are contained in a part other than the first main surface  112 , the second main surface  114  and the end face  116  of the glass plate  110 , i.e. that are contained in a bulk portion of the glass plate  110 . 
     As illustrated in  FIG. 8 , in the virtual end face, the concentration C of the introduced ion in the thickness direction of the glass plate  110 , over the entire virtual end face, has a profile greater than the concentration in the bulk portion (bulk concentration). In the example, the concentration C shows a profile having an approximately parabolic shape. That is, the concentration C of the introduced ions tends to have maximum values C max  at the first main surface  112  (t=0%) and at the second main surface  114  (t=100%), and have minimum C min  at a central portion in the depth direction (t=50%). Note that the minimum value C min  is positive. 
     Note that the shape of the concentration profile of the introduced ions varies depending on the thickness and the material of the glass plate  110 , the conditions of the chemical strengthening process, and the like. However, in any case, the concentration over the entire virtual end face is greater than the concentration contained in the bulk portion, and as an example, the profile having an approximately parabolic shape, as described above, is generated. However, due to a difference in the conditions of the chemical strengthening process, the concentration C of the introduced ions at the first main surface  112  (t=0%) often does not coincide precisely with the concentration C of the introduced ions at the second main surface  114  (t=100%). That is, the concentration C often has a maximum C max  at only either of the main surfaces. Moreover, the profile having the approximately parabolic shape is, different from a mathematical definition of a parabola, a profile in which the introduced ion concentration C increases on the first main surface side and on the second main surface side with respect to the central portion in the thickness direction, and the introduced ion concentration in the concentration profile is greater than the bulk concentration of the glass article. Thus, in the profile having the approximately parabolic shape, a profile in which the introduced ion concentration is greater than the bulk concentration of the glass article, and the introduced ion concentration C varies relatively slowly at the central portion in the thickness direction, i.e. having an approximately trapezoidal shape, is included. 
     In this way, in the first manufacturing method, the virtual end face also can be subjected to the chemical strengthening process. 
     Note that, the chemical strengthening process is performed in case of necessity, and may be omitted. Moreover, the chemical strengthening process may be performed before the aforementioned laser irradiation process (step S 110 ). However, in this case, it is necessary to pay attention to the point that the region strengthened by the chemical strengthening process is limited to an exposed surface (the first main surface  112 , the second main surface  114  and the end face  116 ), and the virtual end face is not strengthened. 
     Step S 120   
     Next, an organic film is deposited on the first main surface  112  or the second main surface  114  of the glass plate  110 . In the following, as an example, the case where an organic film is deposited on the first main surface  112  of the glass plate  110  will be described. 
       FIGS. 9 to 11  are diagrams schematically depicting examples of a state where an organic film  170  is formed on the first main surface  112  of the glass plate  110 . 
     The organic film  170  is arranged so as to cover at least a surface region of each glass piece (surface corresponding to the first main surface  112  of the glass plate  110 ). 
     For example, in the example, illustrated in  FIG. 9 , the organic film  170  is arranged so that the surface regions of the glass pieces  160   a  are covered, and on the first main surface  112 , only a peripheral portion is exposed in a frame shape. 
     Moreover, in  FIG. 10 , the organic film  170  is arranged so that the surface regions of the glass pieces  160   c  are covered, and only a peripheral portion is exposed in a frame shape. Note that the configuration illustrated in  FIG. 10  is different from the configuration illustrated in  FIG. 9  in that, on the first main surface  112  of the glass plate  110 , the organic film  170  is also arranged in a region other than the glass piece  160   c.    
     Furthermore, in  FIG. 11 , the organic film  170  is arranged in a plurality of regions so as to cover only the surface regions of the glass pieces  160   c.    
     Note that the arrangement forms of the organic film  170  shown in  FIGS. 9 to 11  are merely examples, and the organic film  170  may be arranged in any form as long as the organic film  170  covers the surface regions of the glass pieces  160   a  to  160   c.  Particularly, the organic film  170  is preferably deposited over the entire first main surface  112 . In this case, a masking process becomes unnecessary. 
     The organic film  170  may be configured of a polymer having a siloxane linkage as a main skeleton and containing fluorine (F), for example. 
     The following formula (1) shows an example of a chemical formula of such a material configuring the organic film  170 . 
     
       
         
         
             
             
         
       
     
     where reactive groups R 1  and R 2  are selected independently from a group including fluorine (F), oxygen (O), carbon (C), and an alkenyl group (C n H 2n-1  where n is an integer that falls within a range of 2 to 100). 
     When an organic film having such reaction groups is used, a water repellency can be exhibited on the first main surface  112  of the glass plate  110 . 
     A thickness of the organic film  170  is not particularly limited, but may, for example, fall within a range of 1 nm to 1 μm. In the case of the fluorine-based organic film, the thickness preferably falls within a range of 1 nm to 10 nm. 
     A manufacturing method of the organic film  170  is not particularly limited. The organic film  170  may be deposited using a conventional deposition technique such as a sputtering method, an evaporation method, and a coating method. 
     Note that before depositing the organic film  170 , another function film or two or more function films may be formed on the first main surface  112  of the glass plate  110 . For example, on the first main surface  112  of the glass plate  110 , an antireflection film may be deposited. The antireflection film is typically configured by alternately laminating a plurality of oxide layers having different refractive indices. Alternatively, a function film other than the antireflection film may be arranged. 
     Step S 130   
     Next, a glass article is separated from the glass plate  110 . 
     In the separation process, a laser light of a laser different from the first laser at step S 110  (in the following, referred to as a “second laser”) is used. Note that in the aforementioned deposition process (step S 120 ) the main surface of the glass plate  110 , on which the organic film  170  is deposited (in the following, referred to as a “deposition surface”), is irradiated with laser light of the second laser. Note that a surface irradiated with the laser light of the second laser may or may not be a surface that is the deposition surface. For example, in the case where a black film or the like is formed on the surface that is not the deposition surface, the deposition surface is preferably irradiated with laser light of the second laser. 
     The second laser includes, for example, a solid state laser, a gas laser, a semiconductor laser, or a free electron laser. The solid state laser includes, for example, a YAG laser. The gas laser includes, for example, a CO 2  laser, excimer laser, argon (Ar) laser, or helium (He)-neon (Ne) laser. 
     In the aforementioned process (step S 110 ), the virtual end face  165  formed in the glass plate  110  has, within the end face, the plurality of surface voids  138  and the voids  158 , included in the in-plane void region  130  and the corresponding internal void arrays  150 . Thus, in the separation process, the surface voids  138  and the voids  158  play a role of a “perforation”. 
     That is, when the in-plane void region  130  (or neighborhood thereof, and the same applied to the following) is irradiated with laser light of the second laser, according to heat from the laser light of the second laser, the voids  158  configuring the internal void array  150  near the irradiation position are connected to each other, and a cutting line that perforates the glass plate  110  in the depth direction is formed. Thus, when such laser light of the second laser is made to scan along the in-plane void region  130 , in the internal void array  150 , the voids  158  are connected to each other, and the internal void array  150  changes to a cutting line. Furthermore, the surface voids  138  configuring the in-plane void region  130  are connected to each other, and a cutting line appears within the first main surface  112 . 
     As a result, the glass plate  110  is divided at the aforementioned virtual end face  165 , and thereby a glass article is separated from the glass plate  110  or two or more glass articles are separated from the glass plate  110 . 
     As described above, in the first manufacturing method, through step S 110  to step S 130 , a glass article or two or more glass articles can be manufactured from the glass plate  110 . 
     In the case of performing a fusion cutting for a glass plate, by irradiating the glass plate with laser light of the second laser using the method described in Japanese Translation of PCT international application publication No. 2012-526721, a glass article can be separated from the glass plate, but at this time the organic film  170  may be damaged. 
     In the first manufacturing method according to the embodiment, before the separation process by the second laser, the in-plane void region  130  and the internal void arrays  150  were already formed in the glass plate  110 , in step S 110 . Thus, in the first manufacturing method, without irradiating with laser light of the second laser with great energy required for the fusion cutting for the glass plate  110 , a glass article can be separated relatively easily. 
     Specifically, in the first manufacturing method, laser light of the second laser used in step S 130  is emitted to the deposition surface under the following irradiation condition: 
     when, in the organic film of the separated glass article, a central portion within the surface is MC, and a point in an end face of the glass article in a top view is MP (however, in a case where the glass article has an approximately polygonal shape, MP is selected from points other than intersection parts of two sides), 
     at the point MP, a count number for fluorine and a count number for silicon obtained by an X-ray photoelectron spectroscopy (XPS) are I MP  (F) and I MP  (Si), respectively, and R MP  is a ratio of the count number I MP  (F) to the count number I MP  (Si), and 
     at the central portion MC, a count number for fluorine and a count number for silicon obtained by an X-ray photoelectron spectroscopy (XPS) are I MC  (F) and I MC  (Si), respectively, and R MC  is a ratio of the count number I MC  (F) to the count number I MC  (Si), 
     a ratio of R MP  to R MC  is 0.3 or more. 
     Note that the irradiation energy is not necessarily uniform within a spot diameter. For example, within the spot diameter, the energy at the central portion may be lower than the energy at the peripheral portion, and vice versa. Thus, for the end face with respect to the point MP, not only the end face but also a range of the spot diameter of laser light of the second laser on the organic film near the end face is included, and the count number I MP  (F) indicates a minimum value within the end face and the range of the spot diameter. The same applies to MP and I MP  (F) described as follows. 
     In the case of irradiating the glass plate  110  with laser light of the second laser under such an irradiation condition, an effect on the organic film  170  can be controlled significantly. As a result, in the first manufacturing method, by irradiating the deposition surface of the glass plate  110  with laser light of the second laser, and scanning along the in-plane void region  130  with the laser light of the second laser, a glass article can be separated from the glass plate  110  without causing a remarkable effect on the organic film  170 . 
     The aforementioned irradiation conditions can be obtained by adjusting a type of laser, an output power of laser irradiation, a speed of scanning, the spot diameter, and the like. For example, in the case where the second laser is a YAG laser, because an absorption ratio of laser energy for a glass is smaller than that of a CO 2  laser, the second laser requires more energy. 
     Another Manufacturing Method of a Glass Article According to the Embodiment of the Present Invention 
     Next, with reference to  FIG. 12 , another manufacturing method of a glass article according to the embodiment of the present invention will be described. 
       FIG. 12  is a flowchart schematically depicting an example of a flow of another manufacturing method of the glass article according to the embodiment of the present invention (in the following, will be referred to as a “second manufacturing method”). 
     As illustrated in  FIG. 12 , the second manufacturing method includes: 
     a deposition step (1) of, in a glass plate having a first main surface and a second main surface, opposite each other, depositing an organic film on the first main surface of the glass plate (step S 210 ); 
     a laser irradiation step (2) of irradiating the first main surface of the glass plate with a laser light of a first laser (step S 220 ); and 
     a separation step (3) of scanning the first main surface of the glass plate with a laser light of a second laser that is different from the first laser, to separate one glass article or two or more glass articles from the glass plate (step S 230 ). 
     In the following, the processes will be described. Note that in order to make clear the explanation, also in the following description, when a member or a part is indicated, the reference numeral in  FIGS. 2 to 11 , used for the explanation for the aforementioned first manufacturing method will be used. 
     Step S 210   
     First, a glass plate  110  having a first main surface  112  and a second main surface  114 , opposite each other, is provided. 
     The glass plate  110  may also have the form as illustrated in  FIG. 2 . 
     Next, a chemical strengthening process may be performed for the glass plate  110  in case of necessity. However, in the second manufacturing method, it is necessary to pay attention to the point that the region strengthened by the chemical strengthening process is limited to an exposed surface (the first main surface  112 , the second main surface  114  and the end face  116 ), and the virtual end face, obtained in a process (step S 220 ), which will be described later, is not strengthened. 
     Next, the organic film  170  is deposited on the first main surface  112  of the glass plate  110 . 
     Note that the specification, the method of deposition, and the location of deposition of the organic film  170  were described in the aforementioned first manufacturing method. Thus, detailed descriptions will be omitted. 
     As described above, the organic film  170  is preferably deposited over the entire first main surface  112  of the glass plate  110 . In the following, the main surface of the glass plate  110 , on which the organic film is deposited, will also be referred to as a “deposition surface”. 
     Step S 220   
     Next, the deposition surface of the glass plate  110  is irradiated with laser light of a first laser. It is necessary to pay attention to the point that the first laser used in this process is different from a second laser used in a separation process (step S 230 ), which will be described later. 
     According to the irradiation with laser light of the first laser, on the deposition surface of the glass plate  110 , i.e. the first main surface  112 , an in-plane void region  130  is formed. Moreover, below the in-plane void region, i.e. toward the second main surface  114 , a plurality of internal void arrays  150  are formed. 
     As described above, a plane including the in-plane void region  130  and the internal void array  150  corresponding to the in-plane void region  130  will be referred to as a “virtual end face”  165 . The virtual end face  165  substantially corresponds to an end face of the glass article manufactured by the second manufacturing method. 
     Step S 230   
     Next, a separation process for separating a glass article from the glass plate  110  is performed. 
     In the separation process, a laser different from the first laser at step S 220  (in the following, referred to as a “second laser”) is used. Note that the deposition surface of the glass plate  110  is irradiated with laser light of the second laser. 
     As described above, according to the irradiation and scanning of laser light of the second laser, the glass plate  110  is divided at the aforementioned virtual end face  165 , and thereby a glass article or two or more glass articles are separated from the glass plate  110 . 
     Also in the second manufacturing method, before the separation process by the second laser, the in-plane void region  130  and the internal void arrays  150  were already formed in the glass plate  110 , in step S 220 . Thus, in the second manufacturing method, without irradiating the glass plate  110  with laser light of the second laser with great energy required as in fusion cutting, a glass article can be separated relatively easily. 
     Specifically, in the second manufacturing method, laser light of the second laser used in step S 230  is emitted to the deposition surface under the following irradiation condition: 
     when, in the organic film of the separated glass article, a central portion within the surface is MC, and a point in an end face of the glass article in a top view is MP (however, in a case where the glass article has an approximately polygonal shape, MP is selected from points other than intersection parts of two sides), 
     at the point MP, a count number for fluorine and a count number for silicon obtained by an X-ray photoelectron spectroscopy (XPS) are I MP  (F) and I MP  (Si), respectively, and R MP  is a ratio of the count number I MP  (F) to the count number I MP  (Si), and 
     at the central portion MC, a count number for fluorine and a count number for silicon obtained by an X-ray photoelectron spectroscopy (XPS) are I MC  (F) and I MC  (Si), respectively, and R MC  is a ratio of the count number I MC (F) to the count number I MC  (Si), 
     a ratio of R MP  to R MC  is 0.3 or more. 
     In the case of irradiating the glass plate  110  with laser light of the second laser under such an irradiation condition, an effect on the organic film  170  can be controlled significantly. 
     As a result, in the second manufacturing method, by irradiating the deposition surface of the glass plate  110  with laser light of the second laser, and scanning along the in-plane void region  130  with the laser light of the second laser, a glass article can be separated from the glass plate  110  without causing a remarkable effect on the organic film  170 . 
     Moreover, when a glass article is separated from the glass plate  110 , the glass plate  110  is preferably irradiated with the laser light of the second laser satisfying the following irradiation condition: 
     When a value of a contact angle of the organic film with respect to a drop of water at the point MP is T MP and a value of a contact angle of the organic film with respect to a drop of water at the central portion MC is T MC , a ratio of T MP  to T MC  is 0.90 or more. 
     In the case of irradiating the glass plate  110  with laser light of the second laser under such an irradiation condition, the glass article can be separated without damaging a water repellency of the organic film  170 . 
     As described above, using the first and second manufacturing methods as examples, the manufacturing method of the glass article according to the embodiment of the present invention has been described. However, the aforementioned manufacturing methods are merely examples, and yet another manufacturing method may be applied in the present invention. For example, in the first and second manufacturing methods, a part of the processes may be modified or changed and/or another process may be added to the first and second manufacturing methods. 
     Note that, in the first and second manufacturing methods, because a plurality of in-plane voids are formed in the glass plate, when a glass article is separated from the glass plate, a great energy as in the conventional case is not required. Thus, the glass article can be separated by simply applying hot air to the glass plate without using a laser. However, in this case, it is more difficult to control the hot air in order to separate the glass article having a specified shape, than the case of using a laser. This is because when hot air is applied, a temperature distribution in the glass plate by the hot air is broader than the case of using a laser. 
     Glass Article According to the Embodiment of the Present Invention 
     Next, with reference to  FIG. 13  and  FIG. 14 , a glass article according to the embodiment of the present invention will be described. 
       FIG. 13  is a perspective view schematically depicting the glass article according to the embodiment of the present invention (in the following, referred to as a “first glass article”). Moreover,  FIG. 14  is a cross sectional view schematically depicting the first glass article cut along a line A-A in  FIG. 13 . 
     As illustrated in  FIG. 13  and  FIG. 14 , the first glass article  300  includes a first main surface  302  and a second main surface  304 , opposite each other, and an end face connecting the first main surface  302  and the second main surface  304 . 
     In the example illustrated in  FIG. 13 , the first glass article  300  has an approximately rectangular shape, and four end faces  306 - 1  to  306 - 4 . Moreover, the end faces  306 - 1  to  306 - 4  extend parallel to a thickness direction of the first glass article  300  (Z-axis direction). 
     As clearly illustrated in  FIG. 14 , the first glass article  300  includes a glass substrate  320  and an organic film  370 . The glass substrate  320  has a first main surface  322  and a second main surface  324 , opposite each other, and an end face  326  connecting the first main surface  322  and the second main surface  324 . The organic film  370  is arranged on the first main surface  322  side of the glass substrate  320 . 
     The first main surface  302  of the first glass article  300  corresponds to a surface of the organic film  370 , and the second main surface  304  of the first glass article  300  corresponds to the second main surface  324  of the glass substrate  320 . Moreover, each of the four end faces  306 - 1  to  306 - 4  of the first glass article  300  is configured of an end face  326  of the glass substrate  320 , and an end face  372  of the organic film  370  corresponding to the end face  326 . 
     Note that in the example, illustrated in  FIG. 13  and  FIG. 14 , the first glass article  300  has an approximately rectangular shape. 
     However, the above-described configuration is merely an example, and as the shape of the first glass article  300 , various forms are possible. For example, the shape of the first glass article  300  may be, in addition to a rectangular shape, a triangular shape, a polygonal shape of a pentagonal shape or others, a circular shape, an elliptical shape or the like. Moreover, in the case of the polygonal shape, corners may be subjected to a rounding process. 
     Moreover, a number of end faces of the first glass article  300  may be, for example, one, three, or four or more, depending on the form of the first main surface  302  and the second main surface  304 . Furthermore, the end face of the first glass article  300  may extend inclined from the Z-axis direction (i.e. in a non-parallel direction to the Z-axis direction). In this case, an “inclined” end face is obtained. 
     A thickness of the first glass article  300  is not particularly limited. The thickness of the first glass article  300  may fall within a range of, for example, 0.03 mm to 6 mm. 
     The first glass article  300  has a feature that the organic film  370  properly exists also at positions of the end faces  306 - 1  to  306 - 4  of the first glass article  300  in the top view. That is, the thickness of the organic film  370  at the positions of the end faces  306 - 1  to  306 - 4  in the top view is thinner than the thickness at the central portion of the first glass article  300 , but is not zero. 
     The aforementioned feature is a significant feature that cannot be obtained by the conventional manufacturing method, such as separating a glass article by fusion cutting for a glass plate using a high energy laser. This is because in the glass article manufactured by using the conventional method, the organic film is damaged by a heat from the laser, and seldom remains at a separation surface, i.e. the end face. 
     In the first glass article  300  according to the embodiment of the present invention, for example, by manufacturing the first glass article  300  using the aforementioned first manufacturing method or the second manufacturing method, the above-described feature can be obtained. Particularly, in the organic film  170 , an approximately central portion in a top view is MC (See  FIG. 13 ), and a point on the end faces  306 - 1  to  306 - 4  of the first glass article  300  is MP (See  FIG. 13 . However, in a case where the first glass article  300  has an approximately polygonal shape, MP is selected from points other than intersection parts of two sides), 
     at the point MP, a count number for fluorine and a count number for silicon obtained by an X-ray photoelectron spectroscopy (XPS) are I MP  (F) and I MP  (Si), respectively, and R MP  is a ratio of the count number I MP  (F) to the count number I MP  (Si), and 
     at the central portion MC, a count number for fluorine and a count number for silicon obtained by an X-ray photoelectron spectroscopy (XPS) are I MC  (F) and I MC  (Si), respectively, and R MC  is a ratio of the count number I MC  (F) to the count number I MC  (Si), 
     a ratio of R MP  to R MC  is 0.3 or more. 
     Note that the ratio of R MP  to R MC  is less than 1. 
     In this way, in the first glass article  300 , there is little damage to the organic film  370  at the cutting portion, and the organic film  370  can be arranged over the entire first main surface  302  of the first glass article  300 . 
     Other Features 
     Organic Film  370   
     The configuration, the chemical formula, the thickness of the film, and the like of the organic film  370  are the same as for the aforementioned organic film  170 . In the case of using the organic film  370 , a water repellency can be caused to be achieved on the first main surface  302  of the first glass article  300 . 
     Particularly, so as not to damage the water repellency, the glass plate is preferably radiated with laser light of the second laser satisfying the irradiating condition: 
     When a value of a contact angle of the organic film with respect to a drop of water at the point MP is T MC , and a value of a contact angle of the organic film with respect to a drop of water at the portion MC is T MC , a ratio of T MP  to T MC  is 0.90 or more. 
     Chemical Strengthening 
     In the first glass article  300 , the glass substrate  320  may be subjected to the chemical strengthening process. In this case, in addition to the first main surface  322  and the second main surface  324 , the chemical strengthening process may be performed for the end face  326 . 
     However, in this case, a state of chemical strengthening, i.e. a distribution state of introduced ions (alkali metal ions introduced by the chemical strengthening process) of the first and second main surfaces  322  and  324  of the glass substrate  320  is different from the state of chemical strengthening of the end face  326 . 
     For example, in the glass substrate  320 , the end face  326  may have a concentration profile for the introduced ions having an approximately parabolic shape from the first main surface  322  toward the second main surface  324 , as illustrated in  FIG. 8 . 
     Such a concentration profile of the introduced ions can be obtained, in the case where in the aforementioned first manufacturing method, the chemical strengthening process is performed between step S 110  and step S 120 , to manufacture the first glass article  300 . 
     In the case where the chemical strengthening process is performed in the stage of a large-sized glass plate, as described above, the first main surface  322  and the second main surface  324  of the glass substrate  320  are strengthened. However, the end face  326  is not strengthened. 
     As described above, with reference to  FIG. 13  and  FIG. 14 , an example of the configuration of the first glass article  300  has been described. 
     The first glass article  300  can be applied to, for example, an electronic device (e.g. an information terminal device such as a smartphone, or a display device), a cover glass of a camera or a sensor, a glass for a building, a glass for an industry transport vehicle, a biomedical glass device, and the like. 
     For example, in the case where the first glass article  300  is a cover glass, the organic film  370  may be a fingerprint adhesion prevention film (AFP). Moreover, in this case, an additional film such as an antireflection film may be included between the glass substrate  320  and the organic film  370 . The antireflection film may have a repeat structure of a plurality of oxide layers. 
     EXAMPLES 
     In the following, practical examples of the present invention will be described. 
     Practical Example 1 
     In the following description, Examples 1 to 5 illustrate practical examples, and Examples 11 and 12 illustrate comparative examples. 
     Example 1 
     In order to prepare a sample for evaluation, step S 120  and step S 130  in the first manufacturing method were performed. 
     Note that step S 110  was not performed. This is because in the case where all steps S 110  to S 130  are performed to separate a glass article from a glass plate, subsequent evaluations for an organic film (water repellency evaluation and an XPS analysis) are required to be performed at a tip portion of an end face of the glass article, which makes an analysis operation complicated. In a glass plate for which only steps S 120  and S 130  are performed, because a glass article has not been separated yet, a region of the organic film which was irradiated with laser light of the second laser is required to be evaluated in step S 130 , and the evaluation of the organic film can be performed more easily. Note that it is clear that a result obtained by such evaluation is substantially the same as a result obtained at an end portion of the glass article separated by using the first manufacturing method. 
     First, for a glass plate, a base plate of an aluminosilicate glass, Dragontrail (trademark registered), before the chemical strengthening process was prepared. Dimensions of the glass plate were 100 mm (vertical)×100 mm (horizontal)×0.8 mm (thickness). 
     Next, an antireflection film and an organic film were deposited on the whole of one of main surfaces of the glass plate (first main surface) in this order. 
     The antireflection film had a four layer structure of Nb 2 O 5  (target thickness was 15 nm)/SiO 2  (target thickness was 35 nm)/Nb 2 O 5  (target thickness was 120 nm)/SiO 2  (target thickness was 80 nm), and was deposited by using a sputtering method. 
     The organic film was a fingerprint adhesion prevention film (KY185 by Shin-Etsu Chemical Co., Ltd.), and was deposited by using an evaporation method. A target thickness of the organic film was 4 nm. 
     Next, the first main surface of the glass plate was irradiated with laser light of CO 2  laser. The CO 2  laser corresponds to the “second laser” used in the “separation step” (step S 130 ) in the first manufacturing method. 
     The irradiation conditions for CO 2  laser were as follows: 
     
       
         
           
             
               Output 
               ⁢ 
               
                   
               
               ⁢ 
               power 
               ⁢ 
               
                   
               
               ⁢ 
               Q 
             
             = 
             
               38.7 
               ⁢ 
               
                   
               
               ⁢ 
               
                 W 
                 
                   r 
                   , 
                 
               
             
           
         
       
       
         
           
             
               
                 Spot 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 diameter 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 ϕ 
               
               = 
               
                 3 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 mm 
               
             
             , 
             and 
           
         
       
       
         
           
             
               Scan 
               ⁢ 
               
                   
               
               ⁢ 
               speed 
               ⁢ 
               
                   
               
               ⁢ 
               v 
             
             = 
             
               50 
               ⁢ 
               
                   
               
               ⁢ 
               
                 mm 
                 / 
                 
                   sec 
                   . 
                 
               
             
           
         
       
     
     Note that the spot diameter was defined as a width of a machining trace that was generated when an acrylic plate with a thickness of 5 mm was irradiated with laser light of the second laser with an output power of 38.7 W and a laser scan speed of 70 mm/second. For this reference, the distance between a laser collecting lens and the acrylic plate is made greater than a distance at which the spot diameter is the smallest, such that a focal point is deviated from a surface of the acrylic plate. For other spot diameters, the spot diameter is also defined as a width of a machining trace generated by irradiating an acrylic plate with a thickness of 5 mm with laser light of a laser with a predetermined output power and a predetermined scan speed. 
     Thus, a sample for evaluation was manufactured. 
     Evaluation 
     Using the sample manufactured by the aforementioned method (in the following, referred to as a “sample according according to Example 1”), the following evaluation was performed. 
     Evaluation of Water Repellency of Organic Film 
     A water repellency of a surface of the organic film of the sample according to Example 1 was evaluated. The evaluation of the water repellency was performed by dropping a water droplet with a volume of 1 μL to 3 μL on the organic film, and measuring a contact angle of the water droplet. For the measurement, a contact angle meter DMo-701 by Kyowa Interface Science Co., Ltd. was used. 
     The evaluation was performed at two sites: at an approximately central portion of the organic film (in the following, referred to as a “central region”), and at a region of the organic film that is irradiated with laser light of CO 2  laser (in the following, referred to as a “target irradiated region”). 
     As a result of measurement, at the central region, due to a strong water repellency, a water droplet was repelled and a contact angle could not be measured. At the target irradiated region of the organic film, the contact angle exhibited a sufficiently great value, 113.2°. 
     Thus, it was confirmed that, in the sample according to Example 1, even in the CO 2  laser irradiated region, the function of the organic film was not damaged. 
     XPS Analysis for Organic Film 
     Next, in the sample according to Example 1, the analysis of the X-ray photoelectron spectroscopy (XPS) for the organic film was performed. The analysis was performed at a predetermined interval from the target irradiated region of the organic film, along the central region of the organic film. The measurement was performed by using an X-ray photoelectron spectrometric analysis device Quantera SXM by Ulvac-Phi, Incorporated, with a probe diameter of 2 mmϕ, a measurement time of 0.2 minutes/cycle, a pass energy of 224.0 eV, a step energy of 0.4 eV, and a sample angle of 45°. 
       FIG. 15  shows an example of a result of the XPS analysis. 
     In  FIG. 15 , a horizontal axis represents a distance from the target irradiated region of the organic film, and a point where the distance is zero corresponds to the target irradiated region of the organic film. That is, the horizontal axis represents a distance from the target irradiated region in a direction of a line connecting the target irradiated region and the central region of the organic film. A vertical axis represents a ratio of count numbers for fluorine (F) to silicon (Si), F/Si. 
     As shown in  FIG. 15 , the ratio of count numbers, F/Si, was the lowest at around a point where the distance was zero (12.8).  FIG. 15  shows that as the distance increases, the ratio tends to gradually increase. It was found from  FIG. 15  that, with respect to the distance exceeding 4 mm, the ratio F/Si exhibited a value of 25.9 as an average within a range from a distance of 10 to a distance of 20. 
     Thus, even at the position where the distance was zero, the ratio F/Si was not zero. Then, it was confirmed that in the sample according to Example 1, even in the object irradiation region, the organic film was present. 
     In the following, the count number for fluorine at the target irradiated region is expressed by I AP  (F), and the count number for silicon is expressed by I AP  (Si), and a ratio of the count numbers I AP  (F)/I AP  (Si) is expressed by R AP . Moreover, the count number for fluorine at the central region is expressed by I AC  (F), and the count number for silicon is expressed by I AC  (Si), and a ratio of the count numbers I AC  (F)/I AC  (Si) is expressed by R AC . 
     Based on the aforementioned expression, a result of calculation showed that for the sample according to Example 1, the value of the ratio R AP /R AD  was 0.49. Note that when the separation of a glass article from a glass plate is assumed, it is clear that the ratio R AP /R AC  substantially corresponds to the aforementioned ratio R MP /R MC . 
     Examples 2 to 5 
     Using the same method as in Example 1, samples for evaluation were manufactured. 
     However, in Examples 2 to 5, irradiation conditions for CO 2  laser were different from the irradiation conditions in Example 1. 
     Using the obtained samples (in the following, referred to as “samples according to Examples 2 to 5”), the same evaluation as in Example 1 was performed. 
     Examples 11 and 12 
     Using the same method as in Example 1, samples for evaluation were manufactured. 
     However, in Examples 11 and 12, irradiation conditions for CO 2  laser were different from the irradiation conditions in Example 1. 
     Using the obtained samples (in the following, referred to as “samples according to Examples 11 and 12”), the same evaluation as in Example 1 was performed. 
     TABLE 1, in the following, shows the irradiation conditions for CO 2  laser in the aforementioned examples, and results of evaluation obtained in the samples according to the examples as a whole. 
     
       
         
           
               
               
               
             
               
                   
                 TABLE 1 
               
             
            
               
                   
                   
               
               
                   
                 CO 2  laser irradiation 
                   
               
            
           
           
               
               
               
               
               
            
               
                   
                 conditions 
                 contact angle of 
                   
                 XPS analysis for 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                 output 
                 spot 
                 scan 
                 organic film 
                   
                 organic film 
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                   
                 power 
                 diameter 
                 speed v 
                 (degrees) 
                 ratio 
                   
                 ratio 
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 example 
                 Q (W) 
                 ϕ (mm) 
                 (mm/s) 
                 T AP   
                 T AC   
                 T AP /T AC   
                 R AP   
                 R AC   
                 R AP /R AC   
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 1 
                 38.7 
                 3 
                 30 
                 113.2 
                 cannot be 
                 — 
                 12.8 
                 25.0 
                 0.49 
               
               
                   
                   
                   
                   
                   
                 measured 
               
               
                 2 
                 38.7 
                 3 
                 50 
                 108.3 
                 113.1 
                 0.96 
                 11.3 
                 15.3 
                 0.74 
               
               
                 3 
                 38.7 
                 3 
                 70 
                 112.4 
                 113.2 
                 0.99 
                 — 
                 — 
                 — 
               
               
                 4 
                 66.7 
                 3 
                 80 
                 105.3 
                 113.3 
                 0.93 
                 6.9 
                 17.8 
                 0.39 
               
               
                 5 
                 95.1 
                 3 
                 250 
                 111.8 
                 113.5 
                 0.99 
                 14.9 
                 18.1 
                 0.82 
               
               
                 11 
                 95.1 
                 3 
                 90 
                 58.1 
                 113.1 
                 0.51 
                 2.4 
                 18.2 
                 0.13 
               
               
                 12 
                 95.1 
                 3 
                 130 
                 99.3 
                 114 
                 0.87 
                 5.5 
                 18.8 
                 0.29 
               
               
                   
               
            
           
         
       
     
     From the the results shown in TABLE 1, it was found that in each of Examples 1 to 5, the ratio R AP /R AC  exceeds 0.3, and a substantially considerable amount of organic film remained even in the region of the sample which had been irradiated with laser light of CO 2  laser. The above-described result corresponds to a result that a great contact angle greater than 100° was obtained (See “TAP” column of the contact angle (degrees) in TABLE 1) also in the target irradiated region of the sample. 
     In this way, it was confirmed that when the samples according to Examples 1 to 5 are irradiated with laser light of CO 2  laser, the organic film was not appreciably damaged or lost. Thus, it can be said that after performing the separation process, a glass article can be separated properly in the first manufacturing method. 
     In each of the samples according to Examples 11 and 12, the ratio R AP /R AC  is less than 0.3, and it was found that the organic film remained in a small quantity within the CO 2  laser irradiated region. The result corresponds to the fact that the contact angle greatly decreases (less than 100°) in the target irradiated region of the sample. 
     In this way, in the case of assuming the first manufacturing method, it is considered that in the separation processing by the CO 2  laser irradiation with respect to the samples according to Examples 11 and 12, end portions of the organic film were damaged and lost, and a glass article could not be separated where the organic film was in the proper state. 
     When a value of a contact angle of the organic film with respect to a drop of water in the target irradiated region is T AP , and a value of a contact angle of the organic film with respect to a drop of water in the central region is T AC , a ratio of T AP  to T AC  was 0.90 or more for the samples according to Examples 2 to 5. For the samples according to Examples 11 and 12, the ratio of T AP  to T AC  was less than 0.90. 
     Note that when the separation of a glass article from a glass plate is assumed, it is clear that the ratio T AP /T AC  substantially corresponds to the aforementioned ratio T MP /T MC . 
     Example 15 
     In the aforementioned examples, in the first manufacturing method, step S 110  was not performed. Then, in order to confirm that a glass article can be separated from the glass plate by implementing the first manufacturing method, the following experiment was performed. 
     The first main surface of the glass plate was irradiated with laser light of the first laser, to form a plurality of in-plane void regions and internal void arrays corresponding to the in-plane void regions in the glass plate. For the glass plate, a glass plate, that was the same as the glass plate used in Example 1, was used. 
     For a laser device of the first laser, an ultrashort pulse laser device (number of pulses is three) by ROFIN-SINAR Laser GmbH (Germany) that can emit short pulsed laser light of a picosecond order was used. An output power of the laser was set to 90% of the rated value (50 W). A frequency of one burst of the laser was 60 kHz, a pulse width was 15 picoseconds, and a width of one burst was 66 nanoseconds. Each in-plane void was set to be a “single line in-plane void region”. Moreover, the arrangement pattern of the in-plane void regions was set to be an approximately latticed shape. A distance between centers of the in-plane voids configuring the in-plane void region was set to fall within a range of about 4 μm to 6 μm. 
     Next, under the same conditions as the irradiation conditions of the CO 2  laser in Example 1, the laser light of a CO 2  laser was emitted along the in-plane void region. 
     Note that, in Example 15, the deposition of an organic film was not performed. However, from the result of evaluation for the sample according to Example 1, it was confirmed that the organic film was almost free from damage even after the CO 2  laser irradiation. 
     After the CO 2  laser irradiation, a glass article could be separated from the glass plate. 
     Next, the irradiation conditions of the CO 2  laser were changed to the conditions employed in Examples 2 to 5, and the same experiment was performed. As a result, it was confirmed that in any of the CO 2  laser irradiation conditions, a glass article can be separated from the glass plate after the CO 2  laser irradiation. 
     Practical Example 2 
     In the following description, Examples 21 to 25, and Examples 31 to 34 illustrate practical examples, and Examples 26, 35, and 36 illustrate comparative examples. 
     Example 21 
     In order to prepare a sample for evaluation, step S 110  to step S 130  in the first manufacturing method were performed. 
     First, for a glass plate, a glass plate that is the same as the glass plate used in the practical example 1 was prepared. Dimensions of the glass plate were 100 mm (vertical)×100 mm (horizontal)×0.8 mm (thickness). 
     Next, one of main surfaces of the glass plate (first main surface) was irradiated with laser light of the first laser under the following condition, to form a plurality of in-plane void regions and internal void arrays in the glass plate. 
     For the laser device of the first laser, an ultrashort pulse laser device (number of pulses is three) by ROFIN-SINAR Laser GmbH (Germany) that can emit short pulsed laser light of a picosecond order was used. An output power of the laser was set to 90% of the rated value (50 W). A frequency of one burst of the laser was 60 kHz, a pulse width was 15 picoseconds, and a width of one burst was 66 nanoseconds. 
     Each in-plane void was set to be a “single line in-plane void region”. Moreover, the arrangement pattern of the in-plane void regions was set to be an approximately latticed shape. A distance between centers of the in-plane voids configuring the in-plane void region was set to fall within a range of about 4 μm to 6 μm. 
     Next, an antireflection film and an organic film were deposited on the whole of the first main surface of the glass plate in this order. 
     The antireflection film had a four layer structure of Nb 2 O 5  (target thickness was 15 nm)/SiO 2  (target thickness was 35 nm)/Nb 2 O 5  (target thickness was 120 nm)/SiO2 (target thickness was 80 nm), and was deposited by using a sputtering method. 
     The organic film was a fingerprint adhesion prevention film (Afluid 5550 by AGC Inc.), and was deposited by using an evaporation method. A target thickness of the organic film was 4 nm. 
     Next, the first main surface of the glass plate was irradiated with laser light of a CO 2  laser. The CO 2  laser corresponds to the “second laser” used in the “separation step” (step S 130 ) in the first manufacturing method. 
     The irradiation conditions for the CO 2  laser were as follows: 
     
       
         
           
             
               
                 Output 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 power 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 Q 
               
               = 
               
                 38.7 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 W 
               
             
             , 
             
               
 
             
             ⁢ 
             
               
                 Spot 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 diameter 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 ϕ 
               
               = 
               
                 
                   3 
                   ⁢ 
                   
                       
                   
                   ⁢ 
                   
                     mm 
                     . 
                     
                       
 
                     
                     ⁢ 
                     Scan 
                   
                   ⁢ 
                   
                       
                   
                   ⁢ 
                   speed 
                   ⁢ 
                   
                       
                   
                   ⁢ 
                   v 
                 
                 = 
                 
                   50 
                   ⁢ 
                   
                       
                   
                   ⁢ 
                   
                     mm 
                     / 
                     
                       sec 
                       . 
                     
                   
                 
               
             
           
         
       
     
     Note that the spot diameter was defined as a width of a machining trace that was generated when an acrylic plate with a thickness of 5 mm was irradiated with laser light of the second laser with an output power of 38.7 W and a laser scan speed of 70 mm/second. 
     After the CO 2  laser irradiation, a glass article was separated from the glass plate. One of the glass articles obtained as above was collected and was used for a sample for evaluation as follows (referred to as a “sample according to Example 21”). 
     Examples 22 to 25 
     Samples for evaluation were manufactured using the same method as in Example 21. 
     However, in Examples 22 to 25, irradiation conditions for the CO 2  laser were different from the irradiation conditions in Example 21. 
     The obtained obtained samples will be referred to as “samples according to Examples 22 to 25”. 
     Example 26 
     A sample for evaluation was manufactured using the same method as in Example 21. 
     However, in Example 26, irradiation conditions for the CO 2  laser were different from the irradiation conditions in Example 21. 
     The obtained sample will be referred to as a “sample according to Example 26”. 
     Example 31 
     A sample for evaluation was manufactured using the same method as in Example 21. 
     However, in Example 31, an organic film arrangement on the first surface of the glass plate was different from the arrangement of the organic film in the case of Example 21. Specifically, the organic film was a fingerprint adhesion prevention film (Afluid 5550 by AGC Inc.) that was deposited by using a spray method. A target thickness of the organic film was 5 nm. 
     After the CO 2  laser irradiation, a glass article was separated from the glass plate. One of the glass articles obtained as above was collected and was used for a sample for evaluation as follows (referred to as a “sample according to Example 31”). 
     Examples 32 to 34 
     Samples for evaluation were manufactured using the same method as in Example 31. 
     However, in Examples 32 to 34, irradiation conditions for CO 2  laser were different from the irradiation conditions in Example 31. 
     The obtained samples will be referred to as “samples according to Examples 32 to 34”. 
     Examples 35 and 36 
     Samples for evaluation were manufactured using the same method as in Example 31. 
     However, in Examples 35 and 36, irradiation conditions for CO 2  laser were different from the irradiation conditions in Example 31. 
     The obtained samples will be referred to as “samples according to Examples 35 and 36”. 
     Evaluation 
     Using the samples manufactured by the aforementioned method, the following evaluation was performed. 
     Evaluation of Water Repellency of Organic Film 
     Water repellencies of surfaces of the organic films of the samples according to Examples 21 to 26 and 31 to 36 were evaluated. The evaluation method of the water repellency was the same as in the practical example 1. 
     However, in the practical example 2, the water repellency was measured at the central portion of the organic film on the first side of the sample, and at a position that was regarded as the end face located within one of the laser cutting end faces of the organic film by 500 μm (corresponding to the aforementioned “target irradiated region”). The contact angles of the positions are indicated by “TAP” and “TAC”. 
     XPS Analysis for Organic Film 
     In the samples, the analysis for the X-ray photoelectron spectroscopy (XPS) for the organic film was performed. The analysis method was the same as in the practical example 1. 
     However, in the practical example 2, the position within the laser cutting end face by 500 μm (corresponding to the aforementioned “target irradiated region”) was regarded as as the end face, and XPS analysis was performed at a predetermined interval from the position along the central portion of the organic film. 
     In the following, the count number for fluorine at the target irradiated region is expressed by I AP  (F), and the count number for silicon is expressed by I AP  (Si), and a ratio of the count numbers I AP  (F)/I AP  (Si) is expressed by R AP . Moreover, the count number for fluorine at the central region is expressed by I AC  (F), and the count number for silicon is expressed by I AC  (Si), and a ratio of the count numbers I AC  (F)/I AC  (Si) is expressed by R AC . 
     TABLE 2, in the following, shows the irradiation conditions for the CO 2  laser in Examples 21 to 26, and results of evaluation obtained in the samples according to Examples 21 to 26 as a whole. 
     
       
         
           
               
               
               
             
               
                   
                 TABLE 2 
               
             
            
               
                   
                   
               
               
                   
                 CO 2  laser irradiation 
                   
               
            
           
           
               
               
               
               
               
            
               
                   
                 conditions 
                 contact angle of 
                   
                 XPS analysis for 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                 output 
                 spot 
                 scan 
                 organic film 
                   
                 organic film 
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                   
                 power 
                 diameter 
                 speed v 
                 (degrees) 
                 ratio 
                   
                 ratio 
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 example 
                 Q (W) 
                 ϕ (mm) 
                 (mm/s) 
                 T AP   
                 T AC   
                 T AP /T AC   
                 R AP   
                 R AC   
                 R AP /R AC   
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 21 
                 38.7 
                 3 
                 50 
                 111.6 
                 111.7 
                 1.00 
                 4.1 
                 4.5 
                 0.93 
               
               
                 22 
                 38.7 
                 3 
                 70 
                 112.6 
                 112.9 
                 1.00 
                 4.3 
                 4.5 
                 0.96 
               
               
                 23 
                 66.7 
                 3 
                 80 
                 112.3 
                 112.9 
                 0.99 
                 3.2 
                 4.5 
                 0.73 
               
               
                 24 
                 95.1 
                 3 
                 250 
                 107.3 
                 107.7 
                 1.00 
                 3.3 
                 4.5 
                 0.75 
               
               
                 25 
                 95.1 
                 3 
                 130 
                 89.5 
                 106.2 
                 0.84 
                 2.0 
                 4.5 
                 0.44 
               
               
                 26 
                 95.1 
                 3 
                 90 
                 80.0 
                 107.7 
                 0.74 
                 0.2 
                 4.5 
                 0.04 
               
               
                   
               
            
           
         
       
     
     From the results shown in TABLE 2, it was found that in each of Examples 21 to 25, the ratio R AP /R AC  exceeds 0.3, and a substantially considerable amount of organic film remained even in the region of the sample which had been irradiated with laser light of CO 2  laser. The above-described result corresponds to a result that in the case of Examples 21 to 25, a great contact angle greater than 89.5° was obtained also in the target irradiated region of the sample. In this way, it was confirmed that when the samples according to Examples 21 to 25 are irradiated with laser light of CO 2  laser, the organic film was not appreciably damaged or lost. Thus, it can be said that after performing the separation process, a glass article can be separated properly in the first manufacturing method. 
     In the sample according to Example 26, the ratio R AP /R AC  was significantly less than 0.3, and it was found that the organic film remained in a small quantity within the CO 2  laser irradiation region. The result corresponds to the fact that the contact angle greatly decreases (less than 80°) in the target irradiated region of the sample. 
     TABLE 3, in the following, shows the irradiation conditions for CO 2  laser in the samples according to Examples 31 to 36, and results of evaluation obtained in the samples according to Examples 31 to 36 as a whole. 
     
       
         
           
               
               
               
             
               
                   
                 TABLE 3 
               
             
            
               
                   
                   
               
               
                   
                 CO 2  laser irradiation 
                   
               
            
           
           
               
               
               
               
               
            
               
                   
                 conditions 
                 contact angle of 
                   
                 XPS analysis for 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                 output 
                 spot 
                 scan 
                 organic film 
                   
                 organic film 
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                   
                 power 
                 diameter 
                 speed v 
                 (degrees) 
                 ratio 
                   
                 ratio 
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 example 
                 Q (W) 
                 ϕ (mm) 
                 (mm/s) 
                 T AP   
                 T AC   
                 T AP /T AC   
                 R AP   
                 R AC   
                 R AP /R AC   
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 31 
                 38.7 
                 3 
                 50 
                 115.9 
                 114.9 
                 1.01 
                 9.0 
                 10.4 
                 0.86 
               
               
                 32 
                 38.7 
                 3 
                 70 
                 113.0 
                 113.8 
                 0.99 
                 6.8 
                 10.4 
                 0.65 
               
               
                 33 
                 66.7 
                 3 
                 80 
                 112.7 
                 113.8 
                 0.99 
                 5.6 
                 10.4 
                 0.54 
               
               
                 34 
                 95.1 
                 3 
                 250 
                 113.9 
                 113.9 
                 1.00 
                 10.3 
                 10.4 
                 0.99 
               
               
                 35 
                 95.1 
                 3 
                 90 
                 73.2 
                 113.9 
                 0.64 
                 0.0 
                 10.4 
                 0.00 
               
               
                 36 
                 95.1 
                 3 
                 130 
                 88.9 
                 112.6 
                 0.79 
                 2.1 
                 10.4 
                 0.20 
               
               
                   
               
            
           
         
       
     
     From the results shown in TABLE 3, it was found that in each of Examples 31 to 34, the ratio R AP /R AC  exceeds 0.3, and a substantially considerable amount of organic film remained even in the region of the sample which had been irradiated with laser light of CO 2  laser. The above-described result corresponds to a result that in Examples 31 to 34 a great contact angle greater than 100° was obtained in the target irradiated region of the sample. 
     In this way, it was confirmed that when the samples according to Examples 31 to 34 are irradiated with laser light of CO 2  laser, the organic film was not appreciably damaged or lost. Thus, it can be said that after performing the separation process, a glass article can be separated properly in the first manufacturing method. In the samples according to Examples 35 and 36, the ratio R AP /R AC  was significantly less than 0.3, and it was found that the organic film remained in a small quantity within the CO 2  laser irradiation region. The result corresponds to the fact that the contact angle decreases (less than or equal to 88.9°) in the target irradiated region of the sample. 
     REFERENCE SIGNS LIST 
     
         
           110  glass plate 
           112  first main surface 
           114  second main surface 
           116  end face 
           130 , 131 , 132  in-plane void region 
           138  surface void 
           138 A, 138 B surface void array 
           150  internal void array 
           158  void 
           160   a  to  160   c  glass pieces 
           165  virtual end face 
           170  organic film 
           300  first glass article 
           302  first main surface 
           304  second main surface 
           306 - 1  to  306 - 4  end face 
           320  glass substrate 
           322  first main surface 
           324  second main surface 
           326  end face 
           370  organic film 
           372  end face of organic film