Patent Publication Number: US-2023140811-A1

Title: Methods of making a wide metal sheet

Description:
INTRODUCTION 
     The information provided in this section is for the purpose of generally presenting the context of the disclosure. Work of the presently named inventors, to the extent it is described in this section, as well as aspects of the description that may not otherwise qualify as prior art at the time of filing, are neither expressly nor impliedly admitted as prior art against the present disclosure. 
     The present disclosure relates to methods of making a wide metal sheet. 
     High-energy density electrochemical cells, such as lithium-ion batteries can be used in a variety of consumer products and vehicles, such as hybrid or electric vehicles. Battery powered vehicles show promise as a transportation option as technical advances continue to be made in battery power and lifetimes. Batteries may include components formed from or including metal sheets or foils. 
     SUMMARY 
     In various aspects, the present disclosure provides a method of preparing a metal sheet. The method includes extruding a component along an extrusion axis. The component has a wall at least partially defining an interior region. The component includes a metal. The method further includes unfurling the wall to form a sheet precursor. The sheet precursor has a first thickness and a first transverse dimension. The method further includes rolling the sheet precursor along a rolling axis to form the metal sheet. The metal sheet has a second thickness perpendicular to the rolling axis. The second thickness is less than the first thickness. The second transverse dimension is parallel to the rolling axis. The second transverse dimension is greater than the first transverse dimension. 
     In one aspect, the method further includes cutting the wall substantially parallel to the extrusion axis prior to the unfurling. The wall defines a cross-section substantially perpendicular to the extrusion axis. The cross-section forms a closed curve prior to the cutting. 
     In one aspect, the cutting is performed with a blade, a laser, a saw, a heated wire, a spark cutter, or any combination thereof. 
     In one aspect, the cutting is performed with a tool. The tool includes a body defining a tool axis and a blade extending from the body. The cutting comprises moving at least one of the tool and the component with respect to the other of the tool and the component such the body is at least partially in the interior region and the blade cuts through the wall. 
     In one aspect, the body defines a cone or a frusto-cone extending between a first end and a second end. The second end includes a base of the cone or the frusto-cone. The first end enters the interior region prior to the second end during the cutting. 
     In one aspect, the method further includes lubricating a surface of the wall prior to the rolling. The lubricating includes flowing lubricant through a passage defined in the body of the tool. 
     In one aspect, the wall defines a cylinder. 
     In one aspect, the cylinder defines an outer diameter of greater than or equal to about 50 mm to less than or equal to about 300 mm. 
     In one aspect, the wall defines a spiral. 
     In one aspect, the method further includes forming a plurality of sheets by cutting the wall after the unfurling. 
     In one aspect, the forming is performed prior to the rolling. 
     In one aspect, the rolling axis is substantially perpendicular to the extrusion axis. 
     In one aspect, the rolling axis is substantially parallel to the extrusion axis. 
     In one aspect, the second thickness is greater than or equal to about 20 µm to less than or equal to about 100 µm. 
     In one aspect, a surface of the metal sheet after the rolling has a mirror finish. 
     In one aspect, the metal comprises lithium, magnesium, tin, indium, aluminum, copper, nickel, or any combination thereof. 
     In one aspect, the rolling is performed with roller comprising a non-stick surface. 
     In one aspect, the method further includes, after the extruding and before the rolling, increasing a dimension of the component. 
     In one aspect, the dimension is one of a length substantially parallel to the extrusion axis or a transverse dimension substantially perpendicular to the extrusion axis. 
     In various aspects, the present disclosure provides a method of preparing a lithium metal electrode for an electrochemical cell. The method includes extruding a component along an extrusion axis. The component has a wall at least partially defining an interior region. The wall defines a cross-section substantially perpendicular to the extrusion axis. The cross-section forms a closed curve. The component includes lithium metal. The method further includes cutting the wall substantially parallel to the extrusion axis. The method further includes unfurling the wall to form a sheet precursor having a first thickness and a first transverse dimension. The method further includes rolling the sheet precursor along a rolling axis to form the lithium metal electrode. The lithium metal electrode has a second thickness perpendicular to the rolling axis and a second transverse dimension parallel to the rolling axis. The second thickness is less than the first thickness. The second transverse dimension is parallel to the rolling axis. The second transverse dimension is greater than the first transverse dimension. 
     Further areas of applicability of the present disclosure will become apparent from the detailed description, the claims and the drawings. The detailed description and specific examples are intended for purposes of illustration only and are not intended to limit the scope of the disclosure. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The present disclosure will become more fully understood from the detailed description and the accompanying drawings, wherein: 
         FIG.  1    is a flowchart depicting a method of making a metal sheet according to various aspects of the present disclosure; 
         FIG.  2   . is a perspective view of an extruded cylinder according to various aspects of the present disclosure; 
         FIG.  3    is a cross-sectional view of an extruded spiral according to various aspects of the present disclosure. 
         FIG.  4    is a perspective view of a cylinder formed by increasing a length of the cylinder of  FIG.  2    according to various aspects of the present disclosure; 
         FIG.  5    is a perspective view of a cylinder formed by increasing a diameter of the cylinder of  FIG.  2    according to various aspects of the present disclosure; 
         FIG.  6    is a perspective view of a cut cylinder formed by opening a wall of the cylinder of  FIG.  2    according to various aspects of the present disclosure; 
         FIG.  7    is a perspective view of a sheet precursor formed by unfurling a wall of the cut cylinder of  FIG.  6    according to various aspects of the present disclosure; 
         FIG.  8    is a schematic illustration of a method of rolling the sheet precursor of  FIG.  7    according to various aspects of the present disclosure; 
         FIG.  9    is a perspective view of a metal sheet formed in the rolling of  FIG.  8   ; 
         FIG.  10    is schematic view of a method of making a metal sheet according to various aspects of the present disclosure; 
         FIG.  11    is a perspective view of a cutting and lubricating tool according to various aspects of the present disclosure; and 
         FIG.  12    is a schematic view of a method of making a metal sheet according to various aspects of the present disclosure. 
     
    
    
     In the drawings, reference numbers may be reused to identify similar and/or identical elements. 
     DETAILED DESCRIPTION 
     Example embodiments are provided so that this disclosure will be thorough, and will fully convey the scope to those who are skilled in the art. Numerous specific details are set forth such as examples of specific compositions, components, devices, and methods, to provide a thorough understanding of embodiments of the present disclosure. It will be apparent to those skilled in the art that specific details need not be employed, that example embodiments may be embodied in many different forms and that neither should be construed to limit the scope of the disclosure. In some example embodiments, well-known processes, well-known device structures, and well-known technologies are not described in detail. 
     The terminology used herein is for the purpose of describing particular example embodiments only and is not intended to be limiting. As used herein, the singular forms “a,” “an,” and “the” may be intended to include the plural forms as well, unless the context clearly indicates otherwise. The terms “comprises,” “comprising,” “including,” and “having,” are inclusive and therefore specify the presence of stated features, elements, compositions, steps, integers, operations, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof. Although the open-ended term “comprising,” is to be understood as a non-restrictive term used to describe and claim various embodiments set forth herein, in certain aspects, the term may alternatively be understood to instead be a more limiting and restrictive term, such as “consisting of” or “consisting essentially of.” Thus, for any given embodiment reciting compositions, materials, components, elements, features, integers, operations, and/or process steps, the present disclosure also specifically includes embodiments consisting of, or consisting essentially of, such recited compositions, materials, components, elements, features, integers, operations, and/or process steps. In the case of “consisting of,” the alternative embodiment excludes any additional compositions, materials, components, elements, features, integers, operations, and/or process steps, while in the case of “consisting essentially of,” any additional compositions, materials, components, elements, features, integers, operations, and/or process steps that materially affect the basic and novel characteristics are excluded from such an embodiment, but any compositions, materials, components, elements, features, integers, operations, and/or process steps that do not materially affect the basic and novel characteristics can be included in the embodiment. 
     Any method steps, processes, and operations described herein are not to be construed as necessarily requiring their performance in the particular order discussed or illustrated, unless specifically identified as an order of performance. It is also to be understood that additional or alternative steps may be employed, unless otherwise indicated. 
     When a component, element, or layer is referred to as being “on,” “engaged to,” “connected to,” or “coupled to” another element or layer, it may be directly on, engaged, connected or coupled to the other component, element, or layer, or intervening elements or layers may be present. In contrast, when an element is referred to as being “directly on,” “directly engaged to,” “directly connected to,” or “directly coupled to” another element or layer, there may be no intervening elements or layers present. Other words used to describe the relationship between elements should be interpreted in a like fashion (e.g., “between” versus “directly between,” “adjacent” versus “directly adjacent,” etc.). As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. 
     Although the terms first, second, third, etc. may be used herein to describe various steps, elements, components, regions, layers and/or sections, these steps, elements, components, regions, layers and/or sections should not be limited by these terms, unless otherwise indicated. These terms may be only used to distinguish one step, element, component, region, layer or section from another step, element, component, region, layer or section. Terms such as “first,” “second,” and other numerical terms when used herein do not imply a sequence or order unless clearly indicated by the context. Thus, a first step, element, component, region, layer or section discussed below could be termed a second step, element, component, region, layer or section without departing from the teachings of the example embodiments. 
     Spatially or temporally relative terms, such as “before,” “after,” “inner,” “outer,” “beneath,” “below,” “lower,” “above,” “upper,” and the like, may be used herein for ease of description to describe one element or feature’s relationship to another element(s) or feature(s) as illustrated in the figures. Spatially or temporally relative terms may be intended to encompass different orientations of the device or system in use or operation in addition to the orientation depicted in the figures. 
     Throughout this disclosure, the numerical values represent approximate measures or limits to ranges to encompass minor deviations from the given values and embodiments having about the value mentioned as well as those having exactly the value mentioned. Other than in the working examples provided at the end of the detailed description, all numerical values of parameters (e.g., of quantities or conditions) in this specification, including the appended claims, are to be understood as being modified in all instances by the term “about” whether or not “about” actually appears before the numerical value. “About” indicates that the stated numerical value allows some slight imprecision (with some approach to exactness in the value; approximately or reasonably close to the value; nearly). If the imprecision provided by “about” is not otherwise understood in the art with this ordinary meaning, then “about” as used herein indicates at least variations that may arise from ordinary methods of measuring and using such parameters. For example, “about” may comprise a variation of less than or equal to 5%, optionally less than or equal to 4%, optionally less than or equal to 3%, optionally less than or equal to 2%, optionally less than or equal to 1%, optionally less than or equal to 0.5%, and in certain aspects, optionally less than or equal to 0.1%. 
     In addition, disclosure of ranges includes disclosure of all values and further divided ranges within the entire range, including endpoints and sub-ranges given for the ranges. 
     Example embodiments will now be described more fully with reference to the accompanying drawings. 
     In various aspects, the present technology pertains to rechargeable lithium-ion batteries, which may be used in vehicle applications. A typical electrochemical cell includes a first electrode, such as a positive electrode or cathode, a second electrode such as a negative electrode or an anode, an electrolyte, and a separator. Often, in a lithium-ion battery pack, electrochemical cells are electrically connected in a stack to increase overall output. Lithium-ion electrochemical cells operate by reversibly passing lithium ions between the negative electrode and the positive electrode. The separator and the electrolyte are disposed between the negative and positive electrodes. The electrolyte is suitable for conducting lithium ions and may be in liquid, gel, or solid form. Lithium ions move from a positive electrode to a negative electrode during charging of the battery, and in the opposite direction when discharging the battery. 
     Each of the negative and positive electrodes within a stack is typically electrically connected to a current collector (e.g., a metal, such as copper for the negative electrode and aluminum for the positive electrode). During battery usage, the current collectors associated with the two electrodes are connected by an external circuit that allows current generated by electrons to pass between the negative and positive electrodes to compensate for transport of lithium ions. 
     Electrodes can generally be incorporated into various commercial battery designs, such as prismatic shaped cells, wound cylindrical cells, coin cells, pouch cells, or other suitable cell shapes. The cells can include a single electrode structure of each polarity or a stacked structure with a plurality of positive electrodes and negative electrodes assembled in parallel and/or series electrical connections. In particular, the battery can include a stack of alternating positive electrodes and negative electrodes with separators disposed therebetween. While the positive electroactive materials can be used in batteries for primary or single charge use, the resulting batteries generally have desirable cycling properties for secondary battery use over multiple cycling of the cells. 
     Certain components of electrochemical cells, such as electrodes and/or current collectors, may be formed from metal sheets or foils. In one example, a negative electrode includes metallic lithium and may be a lithium metal electrode (“LME”). The lithium-ion battery may be a lithium-metal battery or cell. Metallic lithium for use in the negative electrode of a rechargeable battery has various potential advantages, including having the highest theoretical capacity and lowest electrochemical potential. Thus, batteries incorporating lithium-metal anodes can have a higher energy density that can potentially double storage capacity, so that the battery may be half the size. 
     Plate-like metal battery components, such as metal electrodes and current collectors for use in electrochemical cells (e.g., batteries), are typically made by extruding a metal sheet (i.e., a substantially planar sheet) and then rolling the sheet until a desired thickness is achieved. This may be performed in a single-step process, such as by using an extrusion press. Standard extrusion presses are limited in sheet width (e.g., to about 100 mm width). Therefore, without the use of more complex equipment, resulting metal sheet widths are also limited using these methods. 
     In various aspects, the present disclosure provides a method of manufacturing metal plates, such as for use in electrochemical cells. The method facilitates production of larger-width metal sheets without the use of complex equipment. The method generally includes extruding a three-dimensional (“3D”) metal component having a wall that at least partially defines an interior region (e.g., a hollow cylinder, a spiral), unfurling the wall of the 3D component to increase its width (e.g., in the case of a hollow cylinder, the original width is a diameter and the width after unfurling is π•diameter), and then rolling the unfurled wall to a desired thickness, thereby further increasing at least one transverse dimension. When the 3D component is a closed shape, such as a cylinder, the method further includes cutting or otherwise opening the wall prior to unfurling. The method may optionally include lubricating the wall prior to rolling, separating individual sheets before or after rolling, and/or expanding a dimension of the 3D shape prior to unfurling. 
     With reference to  FIG.  1   , a method of manufacturing a metal sheet generally includes extruding a 3D component having a wall that at least partially defines an interior region at  200 ; optionally expanding one or more dimensions of the 3D component at  204 ; optionally opening the wall at  208  (i.e., when a cross-section of the 3D shape is a closed-curve shape); optionally lubricating the wall at  212 ; unfurling the wall at  216 ; optionally forming one or more sheets at  220 , such as by cutting; rolling the wall/sheets to a desired thickness at  224 ; and optionally cutting the wall/sheets to form one or more sheets at  228 . Each of these steps is described in greater detail below. 
     At  200 , the method includes extruding a 3D component having a wall that at least partially defines an interior region. As used herein, a “3D component” is a component that that has two dimensions, substantially perpendicular to a direction of extrusion and one another (e.g., a width and a height), that have a similar order of magnitude (e.g., a difference in order of magnitude of less than or equal to about 2). In contrast to the 3D component according to certain aspects of the present disclosure, a sheet has a dimension (i.e., height/thickness) that is many orders of magnitude smaller than the other two dimensions (i.e., width, length). The 3D component is at least partially hollow such that it has a wall that at least partially defines an interior region. In certain aspects, the 3D component may be a cylinder, a spiral, a rectangular prism (e.g., a square prism), or an octagonal prism, by way of example. 
     The 3D component defines a longitudinal axis parallel to a direction of extrusion, as will be described in greater detail below. The 3D component defines a cross section substantially parallel to its longitudinal axis and the direction of extrusion. The cross section may be a closed curve or an open curve. Examples of closed curves include circles (see, e.g.,  FIG.  2   ) and ellipses. An example of an open curve is a spiral (see, e.g.,  FIG.  3   ). 
     The 3D component is formed from a metal, such as an elemental metal or alloys. The metal may include lithium, magnesium, tin, indium, aluminum, copper, nickel, or any combination thereof. In certain aspects, the 3D component consists essentially of the metal. In certain aspects, the metal may include one of the foregoing metals in combination with one or more other metals. In certain aspects, prior to extrusion, the metal may be provided as an ingot or billet. The extrusion may be performed using a hydraulic press that takes the solid cylindrical billet and pushes it through a die and embedded mandrel to create the hollow. Alternatively, the solid metal billet can be pushed around a mandrel that is held coaxially with the billet, with wall thickness of the extrusion defined by the difference between the outer dimension of the billet and the outer dimension of the mandrel. 
     Referring to  FIG.  2   , in various aspects, the 3D component is a cylinder  300 . The cylinder  300  may be extruded along an extrusion axis  302  that is aligned with a longitudinal axis  303  of the cylinder  300 . The cylinder  300  includes a wall  304 . The wall  304  at least partially defines an interior region  306 . The wall  304  may define a first thickness  308  of greater than or equal to about 2 mm, optionally greater than or equal to about 4 mm, optionally greater than or equal to about 6 mm, or optionally greater than or equal to about 8 mm. The first thickness  308  may be less than or equal to about 10 mm, optionally less than or equal to about 8 mm, optionally less than or equal to about 6 mm, or optionally less than or equal to about 4 mm. In certain aspects, the first thickness  308  may be greater than or equal to about 2 mm to less than or equal to about 10 mm, or optionally greater than or equal to about 4 mm to less than or equal to about 6 mm. 
     The cylinder  300  defines a first dimension or length  310  substantially parallel to the extrusion axis  302 . The cylinder  300  further defines a second dimension or height  312  and a third dimension or width  314  substantially perpendicular to the extrusion axis  302 . The second and third dimensions  312 ,  314  may be substantially perpendicular to one another. In certain aspects, the first, second, and third dimensions  310 ,  312 ,  314  may be referred to as first, second, and third component dimensions, respectively. In certain aspects, the second and third dimensions  312 ,  314  may be discrete, while the first dimension  310  continuously increases, such as in a continuous extrusion process. In certain aspects, the second and third dimensions  312 ,  314  are the same. For example, the cylinder  300  may be a right, circular cylinder, as shown, and the second and third dimensions  312 ,  314  may be a diameter. However, the second and third dimensions  312 ,  314  may alternatively be different. The second and third dimensions  312 ,  314  may each be greater than or equal to about 50 mm, optionally greater than or equal to about 100 mm, optionally greater than or equal to about 150 mm, optionally greater than or equal to about 200 mm, or optionally greater than or equal to about 250 mm. The second and third dimensions  312 ,  314  may each be less than or equal to about 300 mm, optionally less than or equal to about 250 mm, optionally less than or equal to about 200 mm, optionally less than or equal to about 150 mm, or optionally less than or equal to about 100 mm. In certain aspects, the second and third dimensions  312 ,  314  (e.g., diameter) may be greater than or equal to about 50 mm to less than or equal to about 300 mm. 
     With reference to  FIG.  3   , in various aspects, the 3D component is a spiral  400 . The spiral  400  may be extruded along an extrusion axis  402  that extends out of the page. The spiral  400  includes a wall  404  that at least partially defines an interior region  406 . The wall  404  may define a first thickness  408  of greater than or equal to about 2 mm, optionally greater than or equal to about 4 mm, optionally greater than or equal to about 6 mm, or optionally greater than or equal to about 8 mm. The first thickness  408  may be less than or equal to about 10 mm, optionally less than or equal to about 8 mm, optionally less than or equal to about 6 mm, or optionally less than or equal to about 4 mm. In certain aspects, the first thickness  408  may be greater than or equal to about 2 mm to less than or equal to about 10 mm, or optionally greater than or equal to about 4 mm to less than or equal to about 6 mm. 
     The spiral  400  defines a first dimension (not shown) substantially parallel to the extrusion axis  402 . The spiral  400  further defines a second dimension  412  (e.g., height) and a third dimension  414  (e.g., width) substantially parallel to the extrusion axis  402 . The first dimension, second dimension  412 , and third dimension  414  may be substantially the same as the first dimension  310 , second dimension  312 , and third dimension  314  of the cylinder  300  of  FIG.  2   . In one example, the spiral  400  may include an inner coil  420  defining an inner coil diameter of about 100 mm and an outer coil  422  defining an outer coil diameter of about 150 mm. The outer coil diameter may correspond to the second and/or third dimension  412 ,  414 . 
     Returning to  FIG.  1   , the method further includes optionally increasing one or more dimensions of the 3D component at  204 . One or more dimensions of the 3D component may be increased after extrusion. In one example, a first dimension substantially parallel to a longitudinal axis and/or extrusion axis is increased (see, e.g.,  FIG.  4   ). In another example, a second and/or third dimension perpendicular to a longitudinal axis and/or extrusion axis is increased (see, e.g.,  FIG.  5   ). In another example, both the first dimension and the second and/or third dimension are increased. In certain other aspects, this step is omitted and the 3D shape is further processed without substantially altering any of the dimensions of the cylinder  300 . Although the examples below are described in the context of the cylinder  300  ( FIG.  2   ), dimensions of other 3D shapes may likewise be modified/increased. 
     Referring to  FIG.  4   , a cylinder  500  according to various aspects of the present disclosure is provided. The cylinder  500  may be prepared by increasing a length of the cylinder  300  of  FIG.  2   . Length may be increased by clamping ends  502  of the cylinder  500  and stretching the same, by way of example. The cylinder  500  has a first dimension or length  510  that is greater than the first dimension  310  of the cylinder  300  of  FIG.  2   . Accordingly, the cylinder  500  also has a thickness  518  that is less than the thickness  308  of the cylinder  300  of  FIG.  2   . The cylinder  500  may have substantially the same second and third dimensions  312 ,  314  as the cylinder  300  of  FIG.  2   . In certain aspects, this process may be referred to as a “pre-thinning” process. 
     With reference to  FIG.  5   , a cylinder  600  according to various aspects of the present disclosure is provided. The cylinder  600  may be prepared by increasing a diameter of the cylinder  300  of  FIG.  2   . Diameter may be increased by pushing a mandrel (not shown) having a diameter larger than an inner diameter of the cylinder  300  ( FIG.  2   ) into the interior region  306 , by way of example. The cylinder  600  has a second dimension  612  and a third dimension  614  (i.e., diameter) that are greater than the second and third dimensions  312 ,  314  of the cylinder  300  of  FIG.  2   . Accordingly, the cylinder  600  also has a thickness  618  that is less than the thickness  308  of the cylinder  300  of  FIG.  2   . The cylinder  600  may have substantially the same first dimension  310  as the cylinder  300  of  FIG.  2   . 
     Returning to  FIG.  1   , at  208 , the method optionally further includes opening a wall of the 3D component. This step is included when the cross-section of the 3D component is a closed-curve shape, such as a circle or an ellipse. The opening at  208  may be performed after the extruding at  208 , including after optionally increasing a dimension at  204 . In certain aspects, the opening at  208  may be performed concurrently with the extruding at  200 , as will be described in greater detail below in the discussion accompanying  FIG.  10   . In certain aspects, opening the wall may include cutting the wall. 
     Referring to  FIG.  6   , in various aspects, an open component or cylinder  700 , according to various aspects of the present disclosure is provided. The open cylinder  700  is formed by opening the wall  304  of the cylinder  300 . The wall  304  may be opened at a boundary  702  by cutting or another separation process. The boundary  702  separates the wall  304  so that it has a first edge  704  and a second edge  706  that come together at the boundary  702 . The boundary  702  may penetrate the entire thickness  308  of the wall  304 . In certain aspects, the boundary  702  may extend along the entire length  310  of the wall. In certain aspects, cutting may be performed using a blade, such as a straight blade (see, e.g., discussion accompanying  FIG.  10   ) or a rolling blade; a laser, such as a pulsed fiber laser; a saw; a heated wire; a spark cutter; or any combination thereof. 
     Returning to  FIG.  1   , the method may further include lubricating the wall at  212 . Lubricating the wall at  208  may be performed at any time prior to rolling the wall at  224 . For example lubricating the wall at  212  may be performed after opening the wall at  208 , and before unfurling the wall at  216 , as shown. In certain aspects, lubricating the wall at  212  may be performed concurrently with opening the wall at  208  (see, e.g., discussion accompanying  FIG.  11   ). 
     Lubricating the wall may facilitate rolling at  224 . One or both sides of the wall may be lubricated, depending on the rolling process to be used at  224 . The lubricant may be applied via spraying, a brush, a sponge, dipping, or any combination thereof, by way of example, In certain aspects, the lubricant may be applied through passages in a cutting tool (see, e.g., discussion accompanying  FIG.  11   ). The lubricant may include mineral oil, silicon oil, a solid lubricant (e.g., boron nitride, molybdenum disulfide, mica), or a combination thereof, by way of example. 
     At  216 , the method includes unfurling the wall. Unfurling the wall may be performed by hand and/or using a tool, such as in-line roller set equipped for bending and unbending sheet metal. After unfurling, the wall may be substantially planar; however, some curvature may remain until rolling at  224  is completed. Unfurling may be performed alone, as a distinct step. Unfurling may also be performed concurrently with opening the wall at  208  or rolling at  224 . 
     With reference to  FIG.  7   , a sheet precursor  800  according to various aspects of the present disclosure is provided. The sheet precursor  800  is formed by unfurling the wall  304  of the open cylinder  700  of  FIG.  6   . The sheet precursor  800  defines the length  310 , also referred to as a first transverse dimension, and the thickness  308 . The sheet precursor  800  defines a second transverse dimension  802  substantially parallel to an unfurling axis  804  and substantially perpendicular to the extrusion axis  302 . The second transverse dimension  802  may be greater than or equal to about 100 mm, optionally greater than or equal to about 200 mm, optionally greater than or equal to about 300 mm, optionally greater than or equal to about 400 mm, optionally greater than or equal to about 500 mm, optionally greater than or equal to about 600 mm, optionally greater than or equal to about 700 mm, optionally greater than or equal to about 800 mm, optionally greater than or equal to about 900 mm, optionally greater than or equal to about 1,000 mm, or optionally greater than or equal to about 1,100 mm. The second transverse dimension  802  may be less than or equal to about 1,200 mm, optionally less than or equal to about 1,100 mm, optionally less than or equal to about 1,000 mm, optionally less than or equal to about 900 mm, optionally less than or equal to about 800 mm, optionally less than or equal to about 700 mm, optionally less than or equal to about 600 mm, optionally less than or equal to about 500 mm, optionally less than or equal to about 400 mm, optionally less than or equal to about 300 mm, or optionally less than or equal to about 200 mm. In certain aspects, the second transverse dimension  802  is greater than or equal to about 100 mm to less than or equal to about 1200 mm, optionally greater than or equal to about 500 mm to less than or equal to about 700 mm, or optionally about 600 mm. For example, when the 3D component is a cylinder, such as the cylinder  300  of  FIG.  2   , the second transverse dimension  802  is equal to π (about 3.14) times an outer diameter of the cylinder  300  (i.e., the second and third dimensions  312 ,  314 ). Accordingly, the sheet precursor  800  prior to rolling at  224  ( FIG.  1   ) is substantially larger than in methods a sheet precursor is formed directly via extrusion. 
     Unfurling may be similarly performed on open 3D components having other geometries, such as other opened/cut closed-curve-cross-section components (e.g., an opened elliptical cylinder), the spiral  400  of  FIG.  3   , or other open-curve-cross-section shapes. 
     Returning to  FIG.  1   , at  220 , the method optionally includes forming one or more sheets. The method may include forming one or more sheets to improve ease of handling and/or to facilitate rolling in a cross-direction non-parallel to the extrusion axis (see, e.g., discussion accompanying  FIG.  12   ). Forming one more sheets may include subdividing a sheet precursor (e.g., the sheet precursor  800  of  FIG.  7   ), such as by cutting. 
     At  224 , the method includes rolling the sheet precursor (i.e., the wall) to a desired thickness. Referring to  FIG.  8   , a rolling operation according to various aspects of the present disclosure is provided. The sheet precursor  800  may be rolled to form a metal sheet  900 . In certain aspects, the rolling may be performed using one or more pairs of rollers  902 . The sheet precursor  800  may be passed between the pair of rollers  902  along a rolling axis  904 . The rollers  902  may be formed from and/or coated with a non-stick material. The non-stick material may include fluorinated polymers (e.g., per- and poly- fluoroalkyl substances (PFAS)), diamond-like carbon, boron nitride, alumina (Al 2 O 3 ), titanium-nitride, titanium-carbide, tungsten, tungsten carbide, or any combination thereof. In certain aspects, the rolling process may use additional rollers, such as backup rollers configured to control elastic deformation. Moreover, the rolling process may include electronic controls configured to maintain motion of the sheet precursor  800  through the rollers and reduce or prevent side-to-side motion. Cracking of the sheet precursor  800  during rolling can be reduced or prevented by optimizing the first thickness  308 , a reduction ratio (between first and second thicknesses  308 ,  910 ), tension, diameter of the rollers  902 , and friction coefficient. 
     Prior to rolling the sheet precursor  800  has the first thickness  308 . After rolling, the metal sheet  900  has a second thickness  910 . The second thickness  910  is less than the first thickness  308 . The second thickness  910  may be greater than or equal to about 20 µm, optionally greater than or equal to about 40 µm, optionally greater than or equal to about 60 µm, or optionally greater than or equal to about 80 µm.The second thickness  910  may be less than or equal to about 100 µm, optionally less than or equal to about 80 µm, optionally less than or equal to about 60 µm, or optionally less than or equal to about 40 µm.In certain aspects, the second thickness  910  may be greater than or equal to about 20 µm to less than or equal to about 100 µm, or optionally greater than or equal to about 20 µm to less than or equal to about 40 µm. 
     With reference to  FIG.  9   , the metal sheet  900  after rolling according to various aspects of the present disclosure is provided. The metal sheet  900  defines a third transverse dimension  1000  parallel to the rolling axis  904 . The rolling axis  904  may be substantially parallel to the extrusion axis  302  ( FIG.  2   ), as shown, the unfurling axis  804  ( FIG.  7   ), or another axis. When the rolling axis  904  is substantially parallel to the extrusion axis  302 , the third transverse dimension  1000  is larger than the first transverse dimension  310  ( FIG.  7   ). However, when a rolling axis is instead substantially parallel to an unfurling axis (see discussion accompanying  FIG.  12   ), a third dimension is larger than a second transverse dimension. 
     The metal sheet  900  includes surfaces  1010 . The surfaces  1010  may be in direct contact with the rollers  902  ( FIG.  8   ) during rolling. In certain aspects, each of the surfaces  1010  may define an average surface roughness (RA) of less than or equal to about 10 microinches, optionally less than or equal to about 8 microinches, or optionally less than or equal to about 4 microinches, by way of example. In certain aspects, the surfaces  1010  may have a mirror finish such that they are uniformly bright with a diffuse to specular reflection ratio of the order 0.005 in the rolling direction. The RA of the metal sheet  900  may be less than the RA of the sheet precursor  800  ( FIG.  7   ). Accordingly, rolling may facilitate a reduction in RA, such as through the use of multiple sequential pairs of rollers that progressively decrease in roughness. 
     Returning to  FIG.  1   , at  228 , the method may optionally include forming one or more individual sheets from the metal sheet  900  ( FIG.  8   ). The method may optionally further include finishing steps, such as edge trimming (e.g., via wire cutting) to remove cracked portions of the sheet. In certain aspects, the metal sheet  900  may be a metal foil. The individual sheets may have dimensions suitable for use in an electrochemical cell, by way of example. The individual sheets may be used as electrodes (e.g., a lithium metal electrode). 
     While the metal sheets and related methods provided by the present technology are particularly suitable for use in components, such as electrochemical cells, of an automobile or other vehicles (e.g., motorcycles, boats, tractors, buses, motorcycles, trains, mobile homes, campers, and tanks), they may also be used in a variety of other industries and applications, including aerospace components, consumer goods, devices, buildings (e.g., houses, offices, sheds, warehouses), office equipment and furniture, and industrial equipment machinery, agricultural or farm equipment, or heavy machinery, by way of example. 
     Example 1 
     In various aspects, extruding a 3D component at  200 , opening a wall of the 3D component at  208 , unfurling the wall at  216 , and rolling the wall at  224  may be performed in a continuous process. Referring to  FIG.  10   , a schematic of an example continuous process according to various aspects of the present disclosure is provided. 
     The method includes extruding a cylinder  1100  from an extruder  1102  along an extrusion axis  1104 . The cylinder  1100  may exit the extruder  1102  in an extrusion direction  1106  parallel to the extrusion axis  1104 . The cylinder  1100  includes a wall  1108  that at least partially defines an interior region  1110 . 
     As the cylinder  1100  moves in the extrusion direction  1106 , it makes contact with a cutting tool  1120 . The cutting tool  1120  includes a body  1122  and a cutting blade  1124 . The body  1122  defines an axis  1123  that may be parallel to the extrusion axis  1104  during cutting. The body  1122  may define a frusto-conical or conical shape (optional cone tip shown in dashed lines). The body  1122  may define an angle  1126  of greater than or equal to about 45°, optionally greater than or equal to about 60°, optionally greater than or equal to about 75°, optionally greater than or equal to about 90°, or optionally greater than or equal to about 105°. The angle  1126  may be less than or equal to about 120°, optionally less than or equal to about 105°, optionally less than or equal to about 90°, optionally less than or equal to about 75°, or optionally less than or equal to about 60°. In certain aspects, the angle  1126  is greater than or equal to about 45° to less than or equal to about 120°. The blade  1124  extends outward from the body  1122  and defines a cutting edge  1128 . In certain aspects, the body  1122  may define other shapes, such as when the 3D component has a noncircular cross-section. 
     During cutting, at least one of the cylinder  1100  and the cutting tool  1120  translates (e.g., along the extrusion axis) with respect to the other of the cylinder  1100  and the cutting tool  1120 . For example, the cutting tool  1120  may remain stationary (i.e., rigidly held in place) while the cylinder  1100  is ejected from the extruder  1102  in the extrusion direction  1106 . During the translation, the body  1122  is at least partially disposed in the interior region  1110  of the cylinder  1100  and the cutting edge  1128  engages the wall  1108  of the cylinder  1100  to form a cut  1130  having edges  1132 . A first (smaller) end  1134  of the cutting tool  1120  may enter the interior region  1110  prior to a second (larger) end  1136  of the cutting tool  1120 . In certain aspects, an outer surface  1138  of the body  1122  may engage an inner surface  1139  of the cylinder  1100  to partially or fully unfurl the cylinder  1100  and form a sheet precursor  1140 . 
     Following unfurling, the sheet precursor is passed through one or more pairs of rollers  1142  along a rolling axis  1144  in a rolling direction  1146  to produce a metal sheet  1150  achieve a desired thickness and roughness. The rolling axis  1144  and the extrusion axis  1104  may be aligned. The use of multiple pairs of rollers  1142  may reduce or eliminate flexing and distortion of the sheet precursor  1140  and the metal sheet  1150 . In certain aspects, each pair of rollers  1142  may facilitate further reduction in thickness and/or roughness of the sheet precursor  1140 . 
     Example 2 
     In various aspects, the present disclosure provides a cutting tool for concurrently cutting, lubricating, and unfurling a wall. With reference to  FIG.  11   , a cutting tool  1200  according to various aspects of the present disclosure is provided. Unless otherwise described, the cutting tool  1200  may be similar to the cutting tool  1120  of  FIG.  10   . The cutting tool  1200  includes a body  1202  and a cutting blade  1204 . 
     The body  1202  may define a plurality of passages. The passages may include holes or pores  1220 , as shown, or channels, by way of example. The pores  1220  may be provided over a portion of an outer surface  1222  of the body  1202  or the entire outer surface  1222  of the body  1202 . The pores  1220  may define any shape (e.g., circular, hexagonal, etc.) and be provided in any pattern. When the passages include channels, the channels may be formed in an outer surface of a body of the tool and extend substantially transverse to a direction of unfurling. 
     In certain aspects, the body  1202  is at least partially hollow. The pores  1220  may be fluidly connected to an interior region  1224  of the body  1202 . The interior region  1224  may receive a lubricant  1226 , such as from a nozzle  1228 . The lubricant  1226  may be guided through the pores  1220  to a surface of a wall of a 3D component as it unfurls. In another example, the passages include channels formed in an outer surface of a body of a cutting tool transverse to an unfurling axis. 
     Example 3 
     In various aspects, the methods of the present disclosure may be performed using non-aligned extrusion and rolling axes. With reference to  FIG.  12   , a schematic example of such a method according to various aspects of the present disclosure is provided. The method includes extruding a cylinder  1300  from an extruder  1302  along an extrusion axis  1304 . The cylinder  1300  may exit the extruder  1302  in an extrusion direction  1306  parallel to the extrusion axis  1304 . The cylinder  1300  includes a wall  1308  that at least partially defines an interior region  1310 . 
     The cylinder  1300  may be cut in a similar manner as the cylinder  1100  to form a sheet precursor  1320 . The sheet precursor  1320  may be further cut or otherwise separated into one or more individual sheets  1330 , such as at a boundary or cut  1331 . Each of the individual sheets  1330  may be passed between one or more pairs of rollers  1332  along a rolling axis  1334  in a rolling direction  1336  to produce a metal sheet  1340 . The rolling axis  1334  is non-parallel to the extrusion axis  1304 . In certain aspects, the rolling axis  1334  is substantially perpendicular to the extrusion axis  1304 . 
     The foregoing description is merely illustrative in nature and is in no way intended to limit the disclosure, its application, or uses. The broad teachings of the disclosure can be implemented in a variety of forms. Therefore, while this disclosure includes particular examples, the true scope of the disclosure should not be so limited since other modifications will become apparent upon a study of the drawings, the specification, and the following claims. It should be understood that one or more steps within a method may be executed in different order (or concurrently) without altering the principles of the present disclosure. Further, although each of the embodiments is described above as having certain features, any one or more of those features described with respect to any embodiment of the disclosure can be implemented in and/or combined with features of any of the other embodiments, even if that combination is not explicitly described. In other words, the described embodiments are not mutually exclusive, and permutations of one or more embodiments with one another remain within the scope of this disclosure.