Patent Publication Number: US-2022227540-A1

Title: Zipper tape and container equipped with zipper tape

Description:
TECHNICAL FIELD 
     The present invention relates to a zipper tape and a zipper-tape-equipped container. 
     BACKGROUND ART 
     A technology to form a container from a biodegradable material in terms of environmental load has been known. For instance, Patent Literature 1 describes a production method of a zipper part for a biodegradable zippered bag, the method including: melting a resin composition containing, as a main component, an aliphatic polyester resin with a flexural modulus in a range from 150 MPa to 400 MPa; and forming the zipper part including a projecting member and a recessed member by extruding the resin composition from a die with an opening for forming zipper parts and then cooling the resin composition at a speed of 40 degrees C./second to 60 degrees C./second. 
     CITATION LIST 
     Patent Literature(s) 
     
         
         Patent Literature 1: JP 4889285 B 
       
    
     SUMMARY OF THE INVENTION 
     Problem(s) to be Solved by the Invention 
     However, even a typical technology still leaves room for improvement in terms of shape stability and engagement strength in a case where a zipper tape is formed of a biodegradable resin composition. 
     Accordingly, an object of the invention is to provide a zipper tape and a zipper-tape-equipped container that enable an improvement in shape stability and engagement strength in a case where a zipper tape is formed of a biodegradable resin composition. 
     Means for Solving the Problem(s) 
     According to an aspect of the invention, a zipper tape is provided, the zipper tape being in an elongated shape and including, in a cross-sectional shape, a pair of base strips and engagement portions projecting from respective surfaces facing each other of the pair of base strips, the engagement portions being engageable with each other, in which at least the engagement portions are each formed of a first biodegradable resin composition having a yield strain of 3.4% or more during a tensile test. 
     According to another aspect of the invention, a zipper-tape-equipped container is provided, the zipper-tape-equipped container including the zipper tape described above and a container body to which the zipper tape is bonded. 
     According to the aspects of the invention, it is possible to provide a zipper tape and a zipper-tape-equipped container that enable an improvement in shape stability and engagement strength in a case where a zipper tape is formed of a biodegradable resin composition. 
    
    
     
       BRIEF DESCRIPTION OF DRAWING(S) 
         FIG. 1  is a plan view of a zipper-tape-equipped bag according to a first exemplary embodiment of the invention. 
         FIG. 2  is a cross-sectional view of the zipper-tape-equipped bag taken along a line II-II shown in  FIG. 1 . 
         FIG. 3  is a cross-sectional view of a zipper-tape-equipped bag according to a second exemplary embodiment of the invention. 
     
    
    
     DESCRIPTION OF EMBODIMENT(S) 
     A detailed description will be made below on preferred exemplary embodiments of the invention with reference to the attached drawings. It should be noted that the same reference sign is used to refer to constituent elements having substantially the same functional configuration and a redundant description thereof is omitted accordingly. 
     It should be noted that a content of a component of a resin composition is intended as mass % relative to the entire resin composition in the description below unless otherwise specified. In addition, a main component of a resin composition refers to a resin component a content of which is the largest among those of resin components in the entire single-layer resin composition or among layers of a multi-layer resin composition. 
     First Exemplary Embodiment 
       FIG. 1  is a plan view of a zipper-tape-equipped bag according to a first exemplary embodiment of the invention and  FIG. 2  is a cross-sectional view of the zipper-tape-equipped bag taken along a line II-II shown in  FIG. 1 . As shown in  FIG. 1  and  FIG. 2 , a zipper-tape-equipped bag  1  according to the first exemplary embodiment includes a film  10  formed into a bag body having a first surface  11 A and a second surface  11 B and a zipper tape  20 . 
     The film  10 , which is a container body in this exemplary embodiment, is formed of, for instance, a single-layer or multi-layer thermoplastic resin. More specifically, the film  10  may include a layer formed of low-density polyethylene (LDPE), linear low-density polyethylene (LLDPE), or polypropylene (PP). PP may be polypropylene homo-polymer (HPP), polypropylene random copolymer (RPP), or polypropylene block copolymer (BPP). In a case where the film  10  is a multi-layer film, an outer base material may include biaxially oriented polypropylene (OPP), biaxially oriented polyethylene terephthalate (OPET), or biaxially oriented nylon (ONy). Further, the film  10  may include an inorganic material layer formed by aluminum deposition, stacking aluminum foil layers, or the like. Further, it is preferable that the film  10  is also provided by a single-layer or multi-layer structure of a biodegradable resin composition in terms of environmental load. As a sealant, a variety of biodegradable resin compositions are usable; for instance, polybutylene succinate (PBS) or poly(butylene succinate/adipate) (PBSA) may be used. Paper (kraft paper) or cellophane may be used as the outer base material. 
     It should be noted that in this exemplary embodiment, two sheets of the film  10  are bonded to each other at a bottom seal portion  12  and a side seal portion  13  to be formed into the bag body having the first surface  11 A and the second surface  11 B; however, a single sheet of the film  10  may be folded at a portion corresponding to the side seal portion  13  to provide the first surface  11 A and the second surface  11 B in another exemplary embodiment. Alternatively, a portion corresponding to the bottom seal portion  12  or the side seal portion  13  in the example in  FIG. 1  may be provided with a so-called gusset, i.e., a portion where the film  10  is folded inside. In this case, the gusset may be formed from the film  10  or another film bonded to the film  10 . Further, the zipper-tape-equipped bag  1  may be in the form of a stand up pouch that can be placed upright by means of a gusset formed at a bottom portion. 
     Further, in this exemplary embodiment, the bottom seal portion  12  and the side seal portion  13  are formed but no top seal portion is formed, so that an opening  14  of the zipper-tape-equipped bag  1  is provided; however, in another exemplary embodiment, with a top seal portion formed in addition to the bottom seal portion  12  and the side seal portion  13 , the opening  14  may be provided afterward in the zipper-tape-equipped bag  1  by cutting the zipper-tape-equipped bag  1  between the top seal portion and the zipper tape  20 . In still another exemplary embodiment, a bag body with no bottom seal portion  12  formed, that is, the zipper-tape-equipped bag  1  not sealed opposite the zipper tape  20 , may be provided. In this case, the bottom seal portion  12  is formed after contents are packed in the zipper-tape-equipped bag  1 . In addition to the above, a zipper-tape-equipped container according to the exemplary embodiment of the invention can be provided by bonding a zipper tape to any of bags and containers other than bags having a variety of known configurations as long as the zipper tape is to be welded thereto. 
     As shown in  FIG. 2 , the zipper tape  20  is an elongated member, including: in a cross-sectional shape, a pair of base strips  21 A and  21 B that are to be bonded respectively to the first surface  11 A and the second surface  11 B of the film  10 ; and engagement portions  22 A and  22 B projecting from surfaces facing each other of the respective base strips  21 A and  21 B and that are engageable with each other. In an example as shown, the engagement portion  22 A is in a male shape in a cross section and the engagement portion  22 B is a female shape in a cross section. By engaging these engagement portions  22 A and  22 B with each other, the zipper tape  20  is closed to seal the opening  14  of the zipper-tape-equipped bag  1 . It should be noted that shapes of the engagement portions  22 A and  22 B are not limited to the male shape and the female shape, and shapes of engagement portions of a variety of known zipper tapes, such as a combination of a claw shape, a hook shape, or a knot shape, are applicable to the engagement portions  22 A and  22 B in the above example. Further, although a pair of engagement portions are disposed in the example as shown, a plurality of pairs of engagement portions may be disposed. 
     In this exemplary embodiment, the base strips  21 A and  21 B and the engagement portions  22 A and  22 B of the zipper tape  20  are formed of a biodegradable resin composition having a yield strain of 3.4% or more during a tensile test. Here, the yield strain during the tensile test can be measured according to “JIS K 7161: 2014 Plastics—Determination of tensile properties.” The yield strain is preferably 4% or more, more preferably 5% or more, further preferably 7% or more, much further preferably 10% or more, particularly preferably 15% or more. At a yield strain of 3.4% or more, the zipper tape becomes less plastically deformable and thus suitable for repeated use. The upper limit is usually, but not limited thereto, approximately 30%. Resin compositions with biodegradability, such as resins derived from organic resources or the like and resins derived from petroleum, are usable as the biodegradable resin composition forming the base strips  21 A and  21 B and the engagement portions  22 A and  22 B. Among the above, the biodegradable resin composition preferably contains at least one of the group consisting of polylactide (PLA), polybutylene succinate (PBS), poly(butylene adipate/terephthalate) (PBAT), polycaprolactone (PCL), poly(caprolactone/butylene succinate) (PCLBS), poly(butylene succinate/adipate) (PBSA), poly(butylene succinate/carbonate) (PEC), poly(ethylene terephthalate/succinate) (PETS), poly(tetramethylene adipate/terephthalate) (PTMAT), polyethylene succinate (PES), polyvinyl alcohol (PVA-H), polyglycolic acid (PGA), and poly (hydroxybutyrate/hydroxyhexanoate) (PHBH), more preferably contains at least one of the group consisting of PLA, PBS, PBAT, and PBSA, preferably contains PBS, PBAT, and PBSA, further preferably contains PBS and PBAT, particularly preferably consists of PBS and PBAT. Even in a case where the biodegradable resin composition consists of PBS and PBAT, inclusion of additives, such as a slip agent, an anti die-drool agent, and an antioxidant, and impurities is acceptable. In addition, the biodegradable resin composition forming the base strips  21 A and  21 B and the engagement portions  22 A and  22 B may further contain a plasticizer. For instance, glycerin fatty acid ester is usable as the plasticizer. 
     In a case where the biodegradable resin composition forming the base strips  21 A and  21 B and the engagement portions  22 A and  22 B contains PBS and PBAT or consists of PBS and PBAT, it is preferable that PBS is in a range from 50 to 99% and PBAT is in a range from 1% to 50%, it is more preferable that PBS is in a range from 60% to 90% and PBAT is in a range from 10% to 40%, and it is further preferable that PBS is in a range from 60% to 80% and PBAT is in a range from 20% to 40%. 
     In this exemplary embodiment, by means of the base strips  21 A and  21 B and the engagement portions  22 A and  22 B of the zipper tape  20  being formed of the biodegradable resin composition as described above, it is possible to improve shape stability and engagement strength of, in particular, the engagement portions  22 A and  22 B in spite of the use of the biodegradable resin composition, which is low in environmental load. 
     It should be noted that although components of the resin composition forming the film  10  are not limited in the above example, it is preferable that the film  10  is also provided by a single-layer or multi-layer structure of a biodegradable resin composition in terms of environmental load. In this case, components of a resin composition forming seal surfaces of the base strips  21 A and  21 B, that is, surfaces opposite the respective engagement portions  22 A and  22 B, are adjusted in accordance with components of a biodegradable resin composition forming a sealant layer of the film  10  facing the base strips  21 A and  21 B of the zipper tape  20 , for instance, in a manner described below, thereby making it possible to favorably bond the zipper tape  20  to the sealant layer of the film  10 . 
     More specifically, for instance, in a case where the biodegradable resin composition forming the zipper tape  20  contains 40% to 80% of PBS, the zipper tape  20  can be favorably bonded to the film  10  irrespective of whether PLA or PBS is the main component of the biodegradable resin composition forming the sealant layer of the film  10 . Further, for instance, in a case where the biodegradable resin composition forming the zipper tape  20  contains 40% or more of PLA, a favorable adhesiveness is achievable as long as the biodegradable resin composition forming the sealant layer of the film  10  contains PLA as a main component. Further, for instance, in a case where the biodegradable resin composition forming the zipper tape  20  contains 20% or more of PBS, a favorable adhesiveness is achievable as long as the biodegradable resin composition forming the sealant layer of the film  10  contains PBS as a main component. 
     Second Exemplary Embodiment 
       FIG. 3  is a cross-sectional view of a zipper-tape-equipped bag according to a second exemplary embodiment of the invention. As shown in  FIG. 3 , a zipper-tape-equipped bag  2  according to the second exemplary embodiment includes the film  10  and a zipper tape  30 . It should be noted that a configuration of the film  10  is the same as in the above first exemplary embodiment and a redundant description is omitted below accordingly. 
     The zipper tape  30  includes second layers  312 A and  312 B and first layers  311 A and  311 B, the second layers  312 A and  312 B including seal surfaces of a pair of base strips that are to be bonded to the respective first surface  11 A and second surface  11 B of the film  10 , the first layers  311 A and  311 B including surfaces opposite the seal surfaces of the respective base strips and engagement portions  22 A and  22 B. A biodegradable resin composition (a first resin composition) forming the first layers  311 A and  311 B including the engagement portions  22 A and  22 B is not limited but may be composed, for instance, as in the above first exemplary embodiment. It means that the biodegradable resin composition forming the first layers  311 A and  311 B is formed of a biodegradable resin composition having a yield strain of 3.4% or more during a tensile test. The yield strain is preferably 4% or more, more preferably 5% or more, further preferably 7% or more, much further preferably 10% or more, particularly preferably 15% or more. At a yield strain of 3.4% or more, the zipper tape becomes less plastically deformable and thus suitable for repeated use. The upper limit is usually, but not limited thereto, approximately 30%. 
     Meanwhile, in this exemplary embodiment, although the second layers  312 A and  312 B, which include the seal surfaces of the respective base strips of the zipper tape  30 , may be formed of the same biodegradable resin composition (a first biodegradable resin composition) as the first layers  311 A and  311 B, it is preferable that the second layers  312 A and  312 B are formed of a biodegradable resin composition (a second biodegradable resin composition) containing different components. Although the second biodegradable resin composition is not limited in terms of components, it is preferable that the second biodegradable resin composition contains, for instance, at least any one of PBS, PBAT, or PBSA. It should be noted that in a case where PBS is contained, the content of PBS may be in a range from 20% to 100%, preferably in a range from 40% to 80%. Alternatively, the second biodegradable resin composition forming the second layers  312 A and  312 B may contain any other biodegradable resin, specifically, for instance, PLA, as a main component. 
     In a case where the biodegradable resin composition (the first biodegradable resin composition) forming the first layers  311 A and  311 B contains PBS and PBAT or consists of PBS and PBAT, the components of the biodegradable resin composition (the second biodegradable resin composition) forming the second layers  312 A and  312 B may include PBS and PBSA at a desired ratio where PBS is in a range from 0 to 100% and PBSA is in a range from 100 to 0%. It is preferable that the content of PBS is in a range from 0 to 90% and the content of PBSA is in a range from 100 to 10%. 
     In a case where the biodegradable resin composition (the first biodegradable resin composition) forming the first layers  311 A and  311 B contains PBS and PBAT or consists of PBS and PBAT, the components of the biodegradable resin composition (the second biodegradable resin composition) forming the second layers  312 A and  312 B may include PBS and PBAT at a desired ratio where PBS is in a range from 0 to 100% and PBAT is in a range from 100 to 0%. It is preferable that the content of PBS is in a range from 0 to 90% and the content of PBAT is in a range from 100 to 10%. 
     In a case where the biodegradable resin composition (the first biodegradable resin composition) forming the first layers  311 A and  311 B contains PBS and PBAT or consists of PBS and PBAT, the components of the biodegradable resin composition (the second biodegradable resin composition) forming the second layers  312 A and  312 B may include PBSA and PBAT at a desired ratio where PBSA is in a range from 0 to 100% and PBAT is in a range from 100 to 0%. It is preferable that the content of PBSA is in a range from 0 to 90% and the content of PBAT is in a range from 100 to 10%. 
     In a case where the biodegradable resin composition (the first biodegradable resin composition) forming the first layers  311 A and  311 B contains PBS and PBAT or consists of PBS and PBAT, the components of the biodegradable resin composition (the second biodegradable resin composition) forming the second layers  312 A and  312 B may include PBS, PBSA, and PBAT at a desired ratio where PBS is in a range from 0 to 100%, PBSA is in a range from 0 to 100%, and PBAT is in a range from 100 to 0%. 
     Further, for instance, in a case where the film  10  is formed of a biodegradable resin composition, the zipper tape  30  can be favorably bonded to the sealant layer of the film  10  formed of a biodegradable resin composition (a third biodegradable resin composition) by adjusting components of a resin composition forming a seal surface of the zipper tape  30 , i.e., the biodegradable resin composition (the second biodegradable resin composition) forming the above second layers  312 A and  312 B, as described below. 
     More specifically, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains 40% to 80% of PBS, the zipper tape  30  can be favorably bonded to the sealant layer of the film  10  irrespective of whether PLA or PBS is the main component of the biodegradable resin composition forming the sealant layer of the film  10 . Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains 40% or more of PLA, a favorable adhesiveness is achievable as long as the biodegradable resin composition forming the sealant layer of the film  10  contains PLA as a main component. Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains 20% or more of PBS, a favorable adhesiveness is achievable as long as the biodegradable resin composition forming the sealant layer of the film  10  contains PBS as a main component. 
     Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains PBSA, the zipper tape  30  can be favorably bonded to the sealant layer of the film  10  even though the biodegradable resin composition forming the sealant layer of the film  10  contains at least one of PBS or PBSA as a main component. Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains PBS, a favorable adhesiveness is achievable as long as the biodegradable resin composition forming the sealant layer of the film  10  contains at least one of PBS or PBSA as a main component. Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains 10% to 100% of PBSA, the zipper tape  30  can be more favorably bonded to the sealant layer of the film  10  even though the biodegradable resin composition forming the sealant layer of the film  10  contains at least one of PBS or PBSA as a main component. Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains 0% to 90% of PBS, a more favorable adhesiveness is achievable as long as the biodegradable resin composition forming the sealant layer of the film  10  contains at least one of PBS or PBSA as a main component. Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains 10% to 100% of PBSA and 0% to 90% of PBS, the zipper tape  30  can be further favorably bonded to the sealant layer of the film  10  even though the biodegradable resin composition forming the sealant layer of the film  10  contains at least one of PBS or PBSA as a main component. 
     Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains PBS and PBAT at a desired ratio where PBS is in a range from 0 to 100% and PBAT is in a range from 100 to 0%, preferably, PBS is in a range from 0% to 90% and PBAT is in a range from 10% to 100%, the zipper tape  30  can be favorably bonded to the sealant layer of the film  10  even though the biodegradable resin composition forming the sealant layer of the film  10  contains at least one of PBS or PBSA as a main component. 
     Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains PBSA and PBAT at a desired ratio where PBSA is in a range from 0 to 100% and PBAT is in a range from 100 to 0%, preferably, PBSA is in a range from 0% to 90% and PBAT is in a range from 10% to 100%, the zipper tape  30  can be favorably bonded to the sealant layer of the film  10  even though the biodegradable resin composition forming the sealant layer of the film  10  contains at least one of PBS or PBSA as a main component. 
     Further, for instance, in a case where the biodegradable resin composition forming the second layers  312 A and  312 B contains 0 to 100% of PBS, 0 to 100% of PBSA, and 100 to 0% of PBAT, the zipper tape  30  can be favorably bonded to the sealant layer of the film  10  even though the biodegradable resin composition forming the sealant layer of the film  10  contains at least one of PBS or PBSA as a main component. 
     The zipper tape  30  is formed by, for instance, coextrusion of the first biodegradable resin composition, which forms the first layers  311 A and  311 B including the engagement portions  22 A and  22 B, respectively, and the second biodegradable resin composition, which forms the second layers  312 A and  312 B including the seal surfaces of the respective base strips. It should be noted that the first layers  311 A and  311 B and the respective second layers  312 A and  312 B are not necessarily adjacent to each other and one or a plurality of additional layers may be formed between the first layer and the second layer. In this case, the base strips are each divided into a larger number of portions than in the above examples as shown and these portions are formed of respective different biodegradable resin compositions. 
     Even in this exemplary embodiment, it is also possible to improve the shape stability and engagement strength of the engagement portions  22 A and  22 B of the zipper tape  30  as in the first exemplary embodiment. Meanwhile, by adjusting the components of the biodegradable resin composition forming the seal surfaces of the base strips independently of those of the biodegradable resin composition forming the engagement portions  22 A and  22 B, for instance, a bonding performance between the base strips and the film  10  can be improved. Further, by means of the first and second biodegradable resin compositions containing a common component, for instance, PBS, a bonding performance between the first layers  311 A and  311 B and the respective second layers  312 A and  312 B can be kept favorable. 
     It should be noted that in order to prevent unintended biodegradation of the zipper tape from progressing, it is preferable that, for instance, produced zipper tapes are packaged in a manner to be able to block moisture in the first exemplary embodiment and the second exemplary embodiment. Specifically, the zipper tapes may be packaged by means of a packaging material using a stacked body of polyethylene terephthalate (PET), aluminum (AL), and linear low-density polyethylene (LLDPE), a stacked body of aluminum-metallized PET (VMPET), K coated nylon, and linear low-density polyethylene (LLDPE), or a stacked body including biaxially oriented polypropylene (OPP) and non-oriented polypropylene (CPP) respectively as a front surface layer and a back surface layer, or a variety of barrier packaging. 
     Further, in the first exemplary embodiment and the second exemplary embodiment, it is preferable that a desiccant is enclosed in packaging. Examples of the desiccant include silica gel. 
     Further, in the first exemplary embodiment and the second exemplary embodiment, a so-called bulk manner in which the zipper tapes are stored and packaged while being dropped and a so-called drum manner in which the zipper tapes are wound on a drum and packaged are both applicable; however, in terms of reducing bending of the zipper tapes due to rigidity thereof, the drum manner is more suitable. 
     EXAMPLES 
     Description will be made below on Examples of the invention. 
     Table 1 shows a relationship between a yield strain and a shape stability during a tensile test with the zipper tape  20  described above in the first exemplary embodiment, in which the base strips  21 A and  21 B and the engagement portions  22 A and  22 B were formed of a biodegradable resin composition containing, as a main component, PBS and PLA or PBAT. The shape stability was evaluated as “A” in a case where the yield strain was 6.0% or more and resealing was possible after unsealing and resealing were repeated for 100 times, evaluated as “B” in a case where the yield strain was 3.4% or more and less than 6.0% and resealing was possible after unsealing and resealing were repeated for 100 times, and evaluated as “C” in a case where the yield strain was less than 3.4% or resealing became impossible before unsealing and resealing were repeated for 100 times. Here, the yield strain was measured according to “JIS K 7161: 2014 Plastics-Determination of tensile properties.” Specifically, a test piece was cut out of the base strip of the zipper tape and measured using a tester (manufactured by Shimadzu Corporation, AGS-X 1 kN) complying with JIS K 7161. For measurement, a cross-sectional area was defined as width x thickness of the test piece and a tension rate was set at 300 mm/min. As a result, it has been demonstrated that a yield strain of 3.4% or more during the tensile test provides a shape stability of “B” or higher. It should be noted that a shape stability of “A” is favorable for use as a zipper tape but “B” is also acceptable for some intended use. 
     It should be noted that the following PBS, PLA, and PBAT were used. 
     PBS (melting point: 115 degrees C. (by DSC method), flexural modulus: 650 MPa (according to ISO 178)) 
     PLA (melting point: 160 degrees C. (by DSC method), tensile modulus: 4500 MPa (according to ISO 527)) 
     PBAT (melting point: 110 to 120 degrees C. (by DSC method), tensile modulus: 80 MPa (according to ISO 527)) 
     
       
         
           
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                 Table 1: Shape Stability and Yield 
               
               
                 Strain in Examples and Comparative 
               
            
           
           
               
               
               
               
               
               
            
               
                   
                   
                   
                   
                 Shape 
                   
               
               
                   
                 PLA(%) 
                 PBS(%) 
                 PBAT(%) 
                 Stability 
                 Yield Strain (%) 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 Comp. 1 
                 100 
                 0 
                 0 
                 C 
                 3.3 
               
               
                 Ex. 1 
                 70 
                 30 
                 0 
                 B 
                 4.0 
               
               
                 Ex. 2 
                 50 
                 50 
                 0 
                 B 
                 4.0 
               
               
                 Ex. 3 
                 30 
                 70 
                 0 
                 B 
                 4.0 
               
               
                 Ex. 4 
                 20 
                 80 
                 0 
                 A 
                 8.0 
               
               
                 Ex. 5 
                 10 
                 90 
                 0 
                 A 
                 11.5 
               
               
                 Ex. 6 
                 0 
                 100 
                 0 
                 A 
                 12.6 
               
               
                 Ex. 7 
                 0 
                 90 
                 10 
                 A 
                 15.8 
               
               
                 Ex. 8 
                 0 
                 70 
                 30 
                 A 
                 16.6 
               
               
                   
               
            
           
         
       
     
     Next, regarding the zipper tape  30  described above as the second exemplary embodiment, Table 2 shows a result of measurement of a sealing strength between the biodegradable resin composition (the second biodegradable resin composition) forming the second layers  312 A and  312 B including the seal surfaces of the respective base strips and the biodegradable resin composition (the third biodegradable resin composition) forming the sealant layer of the film  10 . Specifically, an evaluation sample, in which layers formed of the respective resin compositions were stacked and sealed for a sealing time of 1.0 second, at a sealing pressure of 2.0 MPa, and at a sealing temperature of 180 degrees C., was subjected to measurement of an interlayer heat sealing strength per width of 15 mm (N/15 mm) by using “Digital Force Gauge” manufactured by IMADA CO., LTD. It should be noted that with a tension rate during the sealing strength measurement set at 300 mm/min, a sealing strength of 20 (N/15 mm) or more is shown as “A” and a sealing strength less than 20 (N/15 mm) is shown as “C” in Table 2. 
     PBS (melting point: 115 degrees C. (by DSC method), flexural modulus: 650 MPa (according to ISO 178)) 
     PLA (melting point: 160 degrees C. (by DSC method), tensile modulus: 4500 MPa (according to ISO 527)) 
     PBAT (melting point: 110 to 120 degrees C. (by DSC method), tensile modulus: 80 MPa (according to ISO 527)) 
     PBSA (melting point: 84 degrees C. (by DSC method), tensile modulus: 250 MPa (according to ISO 527)) 
     
       
         
           
               
             
               
                 TABLE 2 
               
             
            
               
                   
               
               
                 Table 2: Sealing Strength between Film and Base Strip (1) 
               
            
           
           
               
               
            
               
                   
                 Sealant Layer of Film 
               
            
           
           
               
               
               
               
               
            
               
                   
                 Main 
                 Main Component 
                 PLA 
                 PBS 
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                   
                 Component 
                 PLA(%)/PBS(%) 
                 100/0 
                 80/20 
                 60/40 
                 40/60 
                 20/80 
                 0/100 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                 Seal 
                 PLA 
                 100/0  
                 A 
                 A 
                 A 
                 A 
                 C 
                 C 
               
               
                 Surface 
                   
                 80/20 
                 A 
                 A 
                 A 
                 A 
                 C 
                 C 
               
               
                 of Base 
                   
                 60/40 
                 A 
                 A 
                 A 
                 A 
                 A 
                 A 
               
               
                 Strip 
                 PBS 
                 40/60 
                 A 
                 A 
                 A 
                 A 
                 A 
                 A 
               
               
                   
                   
                 20/80 
                 A 
                 A 
                 A 
                 A 
                 A 
                 A 
               
               
                   
                   
                  0/100 
                 C 
                 A 
                 A 
                 A 
                 A 
                 A 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
             
               
                 TABLE 3 
               
             
            
               
                   
               
               
                 Table 3: Sealing Strength between Film and Base Strip (2) 
               
            
           
           
               
               
            
               
                   
                 Sealant Layer of Film 
               
            
           
           
               
               
               
               
               
            
               
                   
                 Main 
                 Main Component 
                   
                   
               
               
                   
                 Component 
                 PBS(%)/PBSA(%) 
                 PBS 
                 PBSA 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                 Seal 
                 PBS 
                 100/0  
                 B 
                 B 
               
               
                 Surface 
                 PBS 
                 80/20 
                 A 
                 A 
               
               
                 of Base 
                 PBS 
                 60/40 
                 A 
                 A 
               
               
                 Strip 
                 PBSA 
                 40/60 
                 A 
                 A 
               
               
                   
                 PBSA 
                 20/80 
                 A 
                 A 
               
               
                   
                 PBSA 
                  0/100 
                 A 
                 A 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
             
               
                 TABLE 4 
               
             
            
               
                   
               
               
                 Table 4: Sealing Strength between Film and Base Strip (3) 
               
            
           
           
               
               
            
               
                   
                 Sealant Layer of Film 
               
            
           
           
               
               
               
               
               
            
               
                   
                 Main 
                 Main Component 
                   
                   
               
               
                   
                 Component 
                 PBS(%)/PBAT(%) 
                 PBS 
                 PBAT 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                 Seal 
                 PBS 
                 70/30 
                 B 
                 B 
               
               
                 Surface 
               
               
                 of Base 
               
               
                 Strip 
               
               
                   
               
            
           
         
       
     
     It has been demonstrated from the result shown above in Table 2 that in a case where the biodegradable resin composition forming the seal surfaces of the base strips contains 40% to 80% of PBS, a favorable sealing strength is achievable irrespective of whether the biodegradable resin composition forming the sealant layer of the film  10  contains PLA or PBS as a main component. Further, it has been demonstrated that in a case where the biodegradable resin composition forming the seal surfaces of the base strips contains 40% or more of PLA, a particularly favorable sealing strength is achievable as long as the biodegradable resin composition forming the sealant layer of the film  10  contains PLA as a main component. Further, it has been demonstrated that in a case where the biodegradable resin composition forming the seal surfaces of the base strips contains 20% or more of PBS, a particularly favorable sealing strength is achievable as long as the biodegradable resin composition forming the sealant layer of the film  10  contains PBS as a main component. 
     Further, it has been demonstrated from the result shown above in Table 3 that in a case where the biodegradable resin composition forming the seal surfaces of the base strips is a mixture containing PBS and PBSA at a desired ratio, a favorable sealing strength is achievable irrespective of whether the biodegradable resin composition forming the sealant layer of the film  10  contains PBS or PBSA as a main component. Further, it has been demonstrated from the result shown above in Table 3 that by means of combined use of PBS and PBSA as the biodegradable resin composition forming the sealant layer of the film  10 , a more favorable sealing strength is achievable as compared with in a case where the biodegradable resin composition consists of PBS. 
     Further, it has been demonstrated from the result shown above in Table 4 that in a case where the biodegradable resin composition forming the seal surfaces of the base strips is a mixture containing PBS and PBAT at a desired ratio, a sealing strength comparable to that in a case where the biodegradable resin composition consists of PBS as shown in Table 3 above is achievable. 
     The preferred exemplary embodiments of the invention are described above in detail with reference to the attached drawings; however, the invention is not limited to these examples. It is obvious to those skilled in the art to which the invention pertains that a variety of modifications or alterations are conceivable within the scope of the technical idea according to claims and it should be understood that these are also, of course, within the technical scope of the invention. 
     EXPLANATION OF CODE(S) 
     
         
         
           
               1 ,  2  . . . zipper-tape-equipped bag,  10  . . . film,  12  . . . bottom seal portion,  13  . . . side seal portion,  14  . . . opening,  20 ,  30  . . . zipper tape,  21 A,  21 B . . . base strip,  22 A,  22 B . . . engagement portion,  311 A,  311 B . . . first layer,  312 A,  312 B . . . second layer