Patent Publication Number: US-2007099396-A1

Title: Method of forming pattern, film structure, electrooptical device and electronic equipment

Description:
BACKGROUND OF THE INVENTION  
      1. Technical Field  
      The present invention relates to a method of forming a pattern, a film structure, an electrooptical device and electronic equipment.  
      2. Related Art  
      A method of forming a conductive pattern by forming a hydrophilic part and a hydrophobic part on a surface of for example a glass substrate and then providing liquid containing metal particles onto the hydrophilic part has been recently developed. JP-A-2002-164635 is an example of related art. According to the example, the hydrophilic part is firstly formed by forming a hydrophobic film which is composed of organic molecules then removing a part of the hydrophobic film (the hydrophobic part). Subsequently, a conductive pattern is formed by filling a discharge head with a liquid that contains metal particles which are the material of the conductive pattern, then discharging the liquid onto the hydrophilic part as relatively moving the discharge head and a substrate.  
      Before such liquid discharge method is carried out, a mark called an alignment mark is provided on a substrate. A detection part of the liquid discharge device detects this alignment mark and the substrate is set to a designated position by adjusting the position of the substrate with reference to the alignment mark. In this way, the starting position where the discharge head starts to discharge the liquid is decided.  
      However, aforementioned technique has the following problem.  
      Where an alignment mark is formed by using resist and the like, a bank (partition wall) which has a configuration corresponding to the shape of the alignment mark is formed. The bank has a high transparency so that accuracy to recognize the alignment mark is low even with a microscope for alignment such as a CCD camera. This could lower the alignment accuracy,  
      Particularly where a wiring pattern composed of a stack film is formed or a thin film covering the whole face of a substrate is formed, accuracy to overlay with another layer to form the stack film tends to be lowered.  
     SUMMARY  
      An advantage of the present invention is to provide a method of forming a pattern in which a pattern can be formed with a high alignment precision. Another advantage of the present invention is to provide a film structure, an electrooptical device and electronic equipment manufactured by the pattern forming method.  
      A method of forming a pattern according to a first aspect of the invention includes forming mark partition walls that correspond to an alignment mark on a substrate before forming the pattern by providing a pattern forming material between partition walls, and providing a liquid material containing an alignment mark forming material between the mark partition walls.  
      In the method of forming a pattern according to one aspect of the invention, the alignment mark is formed by proving a liquid material containing an alignment mark forming material that has a low transparency between the mark partition walls. Therefore, it is possible to measure the alignment mark with high recognition accuracy This improves the alignment accuracy at the time of patterning and the pattern can be formed at a precise position.  
      The above described method is particularly effective where the pattern is a wiring pattern.  
      In this case, it is preferable that the method include a surface treatment process in which the surface of the substrate is treated.  
      This makes it possible to control the behavior of the droplets provided on the substrate. Accordingly, a desired pattern can be obtained.  
      It is also preferable that the method include judging an appropriateness of the surface treatment by measuring a length in which the liquid material containing the alignment mark forming material provided between the partition walls extends.  
      If the surface condition of the substrate is as fine as desired, the drawing can be subsequently carried out. If the surface condition of the substrate is not yet fine, the drawing can be suspended and the substrate can be reproduced. In this way, it is possible to prevent the material from being wasted.  
      In this case, the partition walls and the mark partition walls may be formed in a same process. Since these walls are simultaneously formed in the same process, the manufacturing efficiency can be improved.  
      The pattern may include a first pattern and a second pattern that is made of a different material from a material forming the first pattern, and the first pattern and the second pattern are formed in layers. In this case, it is possible to easily form a layered pattern with fine alignment accuracy.  
      In this case, the alignment mark may be formed of a same material as the material forming the first pattern. In this way, the preparation work can be simplified and the contamination can be prevented.  
      It is preferable that the first pattern be made of a material having a higher adhesion with the substrate than a material forming the second pattern.  
      In this way, a layer (interlayer) that imparts the adhesion can be placed in the first layer of the pattern. This improves the adhesion with the substrate and a defect such as coming off from the substrate is not likely to occur.  
      The method may include forming a semiconductor layer and a pixel electrode by using the alignment mark.  
      In this way, it is possible to accurately align the wiring pattern with the semiconductor layer and the pixel electrode.  
      According to a second aspect of the invention, a film structure includes a pattern formed by the above described method of forming a pattern. Since the alignment of the pattern form in the film can be accurately done, it is possible to increase the density of the patterns. In addition, the film structure can be formed at a reduced cost, because it is formed by the droplet discharge method.  
      According to a third aspect of the invention, an electrooptical device includes the above described film structure. The electrooptical device encompasses a liquid crystal display device, an organic electroluminescence display device and a plasma type display device. According to a fourth aspect of the invention, electronic equipment includes the above described electrooptical device.  
      According to the third and fourth aspects of the invention, it is possible to provide an electrooptical device and electronic equipment having a high quality pattern at reduced cost. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
      The invention will be described with reference to the accompanying drawings, wherein like numbers reference like elements.  
       FIG. 1  is an equivalent circuit diagram of a liquid crystal display device showing an embodiment of the invention.  
       FIG. 2  is a plan view of the liquid crystal display device showing its overall structure.  
       FIG. 3  is a plan diagram of the liquid crystal display device showing one pixel area.  
       FIG. 4  is a sectional view of the liquid crystal display device partially showing a TFT array substrate.  
       FIG. 5A  shows an example of a liquid discharge device and  FIG. 51B  schematically shows a discharge head.  
       FIG. 6  is a plan view of a substrate in a gate electrode formation process.  
       FIGS. 7A through 7C  are sectional views for explaining steps of a manufacturing method of a TFT array substrate.  
       FIGS. 8A and 8B  are sectional views for explaining steps of the manufacturing method of the TFT array substrate.  
       FIGS. 9A through 9C  are sectional views for explaining steps of the manufacturing method of the TFT array substrate.  
       FIGS. 10A and 10B  are sectional views for explaining steps of the manufacturing method of the TFT array substrate.  
       FIGS. 11A through 11C  are sectional views for explaining steps of the manufacturing method of the TFT array substrate.  
       FIG. 12  is an exploded perspective view showing an example of a plasma type display device to which an electrooptical device of the invention is applied.  
       FIGS. 13A through 13C  are perspective views of examples of electronic equipment,  
       FIGS. 14A through 14C  are plan views showing other shape examples of an alignment mark.  
       FIGS. 15A through 15G  are plan views showing other shape examples of the alignment mark. 
    
    
     DESCRIPTION OF EXEMPLARY EMBODIMENTS  
      Embodiments of the invention including a method of forming a pattern, a film structure, an electrooptical device and electronic equipment will be described with reference to  FIGS. 1 through 14   
      In the accompanying drawings, a scale size may be different by each member or layer in order to make the member or layer recognizable.  
      Electrooptical Device  
      An embodiment of an electrooptical device according to the invention is hereinafter described.  
       FIG. 1  is an equivalent circuit diagram of a liquid crystal display device  100  which is an embodiment of the electrooptical device of the invention. A plurality of dots that forms an image display area is arranged in matrix in the liquid crystal display device  100 . A pixel electrode  19  and a TFT  60  that is a switching element for controlling the pixel electrode  19  are formed in each dot. A data line (electrode wiring)  16  through which an image signal is supplied is electrically coupled to a source of the TFT  60 . Image signals S 1 , S 2 , . . . , Sn that are to be written into the data lines  16  can be sequentially supplied to each data line or can be provided to each group of the data lines  16  that are arranged next to each other. A scan line (electrode wiring)  18   a  is electrically coupled to a gate of the TFT  60 . Scan signals G 1 , G 2 , . . . , Gm are sequentially applied in a pulse form to the corresponding scan lines  18   a  at a designated timing. The pixel electrode  19  is electrically coupled to a drain of the TFT  60 . The image signals S 1 , S 2 , . . . , Sn supplied from the data lines  16  are written into the corresponding pixels at a predetermined timing by turning the TFTs  60  which are the switching elements on for a predetermined time period.  
      The image signals S 1  S 2 , . . . , Sn of a predetermined level written into liquid crystal through the pixel electrodes  19  are retained between the pixel electrodes and a hereinafter described common electrode for a certain period. Light is modulated through variations in the orientation and the alignment of the liquid crystal molecule aggregates which are changed according to the level of the voltage applied to the electrode. Consequently, a tone display is realized. In order to prevent the image signals written into the liquid crystal from leaking, a storage capacitor  17  is added in parallel to liquid crystal capacitance formed between the pixel electrode  19  and the common electrode. Reference number  18   b  denotes a storage line coupled to the one electrode of the storage capacitor  17 .  
       FIG. 2  is a plan view of the liquid crystal display device  100  showing its overall structure. The liquid crystal display device  100  includes a TFT array substrate  10  and an opposing substrate  25  which are adhered together through a sealing member  52  that has a substantially rectangular frame shape when it is viewed in plan. The liquid crystal held between the substrates  10  and  25  is enclosed in the substrates by the sealing member  52 . As shown in  FIG. 2 , the peripheral of the opposing substrate  25  is lined with the peripheral of the sealing member  52  when they are viewed in plan.  
      In a region inside the sealing member  52 , a light shielding film (peripheral partition)  53  made of a light shielding material is formed in a rectangular frame shape. In a peripheral circuit region outside the sealing member  52 , a data line driving circuit  201  and mounting terminals  202  are formed along one side of the TFT array substrate  10 , and scan line driving circuits  104 ,  104  are formed along the two sides adjacent to that side of the TFT array substrate. On the remaining one side of the TFT array substrate  10 , a plurality of wirings  105  are provided for coupling the scanning line driving circuits  104 . A plurality of intra-substrate conductive members  106  which electrically couple the TFT array substrate  10  and the opposing substrate  25  is provided at the corners of the opposing substrate  25 .  
       FIG. 3  is a plan diagram for schematically showing a pixel structure of the liquid crystal display device  100 . A plurality of the scan lines  18   a  extends in one direction and a plurality of the data lines  16  extends in the direction orthogonal to the scan lines  18   a  in the display region of the liquid crystal display device  100 . An area surrounded by two scan lines  18   a  and two data lines  16 , which has a rectangular shape as viewed in plan, is a dot region as shown in  FIG. 3 . A color filter of one of the three primary colors is formed in each dot region. Three dot regions shown in the figure form a one pixel area which has three colored areas  22 R,  22 G,  22 B. These colored areas  22 R,  22 G,  22 B are repeatedly arranged in the display region of the liquid crystal display device  100 .  
      In each dot region shown in  FIG. 3 , the pixel electrode  19  that is made of a light transmissive conductive film such as indium tin oxide (ITO) and has a rectangular shape as viewed in plan is provided. Furthermore, the TFT  60  is provided among the pixel electrode  19 , the scan line  18   a  and the data line  16 . The TFT  60  includes a semiconductor layer  33 , a gate electrode  80  provided under (the side close to the substrate) the semiconductor layer  33 , a source electrode  34  provided above the semiconductor layer  33 , and a drain electrode  35 . A channel region of the TFT  60  is formed in the region between the semiconductor layer  33  and the gate electrode  80 . A source region and a drain region are respectively formed in semiconductor regions on the both sides of the channel region.  
      The gate electrode  80  is formed by ramifying a part of the scan line  18   a  in the direction where the data line  16  extends and its tip opposes the semiconductor layer  33  in the vertical direction of the page with an unshown insulating film (gate insulating film) interposed therebetween. The source electrode  34  is formed by ramifying a part of the data line  16  in the direction where the scan line  18   a  extends. The source electrode  34  is electrically coupled to the semiconductor layer  33  (the source region). One end (the left end in the figure) of the drain electrode  35  is electrically coupled to the semiconductor layer  33  (the drain region) and the other end (the right end in the figure) of the drain electrode  35  is electrically coupled to the pixel electrode  19 .  
      Such TFT  60  serves as a switching element for writing the image signal supplied through the data line  16  into the liquid crystal at a prescribed timing when it is turned on by an inputted gate signal from the scan line  18   a.    
       FIG. 4  is a sectional view of the TFT array substrate  10  along the line B-B′ in  FIG. 3  showing it main feature. The TFT array substrate  10  is a glass substrate (substrate) P whose inner side (the upper side in the figure) has the TFT  60  and the pixel electrode  19  according to the invention as shown in  FIG. 4 . A first bank B 1  that has an opening is formed on the glass substrate P. The gate electrode  80  and a part of a gate insulating film  83  that covers the gate electrode  80  are formed so as to fill the opening of the bank B 1 .  
      The gate electrode  80  includes a first electrode layer (first pattern)  80   a  that serves as an adhesion layer, a second electrode layer (second pattern)  80   b  that serves as a main conductive layer and a cap layer  81 , and these layers are laid over one another in this order on the glass substrate P. The first electrode layer  80   a  is made of a metal material such as Mn, Ti and W. The second electrode layer  80   b  is made of a metal material such as Ag, Cu and Al. The cap layer  81  is made of a metal material such as Ni and TiN.  
      A second bank B 2  is formed above the first bank B 1  with the gate insulating film  83  made of SiNx interposed therebetween. The second bank B 2  has an opening for exposing an area which includes the gate electrode  80 . The semiconductor layer  33  is formed in the opening where corresponds to the gate electrode  80  in plan with the gate insulating film  83  interposed therebetween. The semiconductor layer  33  includes an amorphous silicon layer  84  and an N +  silicon layer  85  formed on the amorphous silicon layer  84 . The N +  silicon layer  85  is divided into two parts with a certain space therebetween on the amorphous silicon layer  84 . One part of the N +  silicon layer  85  is electrically coupled to the source electrode  34  that is formed on the both of the gate insulating film  83  and the N +  silicon layer  85 . The other part of the N +  silicon layer  85  is electrically coupled to the drain electrode  35  that is formed on the both of the gate insulating film  83  and the N +  silicon layer  85 . The amorphous silicon layer  84  and the N +  silicon layer  85  that are for ohmic contact can be made by inkjet printing a liquid material containing a silicon compound and a dorpant, A specific example of the silicon compound is a high-order silane produced by photo-polymerizing silane having more than one cyclic structure such as cyclopentasilane with ultraviolet irradiation. As a specific example of the dorpant, a material containing an element in the group III such as phosphorus or the group V such as boron of the periodic table can be named.  
      The source electrode  34  and the drain electrode  35  are separated each other by a second bank B 3  formed in the opening of the second bank B 2 , and are formed in the areas defined by the second banks B 2 , B 3  by a hereinafter described droplet discharge method. Furthermore, an insulating material  86  is provided on the source electrode  34  and the drain electrode  35  so as to fill the opening. A contact hole  87  is formed in the insulating material  86 . The pixel electrode  19  formed on the second bank B 2  and the insulating material  86  is electrically coupled to the drain electrode  35  through the contact hole  87 . In the above-described manner, the TFT  60  of the invention is formed.  
      As shown in  FIG. 3 , the data line  16 , the source electrode  34 , the scan line  18   a  and the gate electrode  80  are formed so as to be integrated so that the data line  16  is also covered with the insulating material  86  in the same way as the source electrode  34  and the scan line  18   a  is covered with the cap layer  81  in the same way as the gate electrode  80 .  
      In an actual product, an alignment film which controls an initial orientation state of the liquid crystal is formed on the surface of the pixel electrode  19 , the second banks B 2 , B 3  and the insulating material  86 . Furthermore, a retardation plate and a deflection plate that control a polarization state of the light beam entering the liquid crystal layer are provided on the outer side of the glass substrate P. Where the liquid crystal display device is a transmissive type or a trans-reflective type, a backlight which is an illuminating means is provided on the outside of the TFT array substrate  10  (back side of a panel).  
      Though the opposing substrate  25  will not be illustrated in detail, the opposing substrate  25  has a color filter layer in which the colored areas  22 R,  22 G,  22 B as shown in  FIG. 3  are arranged and an opposing electrode made of a Rat light-transmissive conductive film. The color filter layer and the opposing electrode are formed in layers on the inner side of the substrate which is the similar one as the glass substrate P. An alignment film which is same as the one on the TFT array substrate is formed on the opposing electrode. A retardation plate and a deflection plate may be provided on the outer side of the substrate if needed.  
      The liquid crystal layer enclosed between the TFT array substrate  10  and the opposing substrate  25  is mainly composed of liquid crystal molecules. Any type of liquid crystal molecules such as a nematic liquid crystal and a smectic liquid crystal can be used for the liquid crystal layer as long as it can be oriented. However, in case of a TN type liquid crystal panel, ones forming the nematic liquid crystal are preferably used. As such liquid crystals, for example, there are a phenylcyclohexane derivative liquid crystal, a biphenyl derivative liquid crystal, a biphenylcyclohexane derivative liquid crystal, a terphenyl derivative liquid crystal, a phenylether derivative liquid crystal, a phenylester derivative liquid crystal, a bicyclohexane derivative liquid crystal, an azomethine derivative liquid crystal, an azoxy derivative liquid crystal, a pyrimidine derivative liquid crystal, a dioxane derivative liquid crystal, a cubane derivative liquid crystal and the like.  
      The liquid crystal display device  100  of the embodiment of the invention having the above-described structure can display any tone image by modulating the light entered from the back light through the liquid crystal layer whose orientation is controlled by the applied voltage. Furthermore, since the colored areas  22 R,  22 G,  22 B are provided in each dot, the liquid crystal display device  100  can display any colored image by mixing light beams colored in the three primary colors (R, G, B) by each pixel.  
      Method of Manufacturing Thin Film Transistor  
      Next, an embodiment of a pattern formation method of the invention is described based on a manufacturing method of the above described TFT  60 . The gate electrode  80 , the source electrode  34  and the drain electrode  35  of the TFT  60  are formed by patterning using the droplet discharge method. The pixel electrode  19  is also formed by the droplet discharge method.  
      Droplet Discharge Device  
      Firstly, a droplet discharge device used in the manufacturing method of the embodiment of the invention is described. According to the manufacturing method of the embodiment, ink (a functional liquid) containing conductive particles and other functional material is discharged in a droplet form from a nozzle of a droplet discharge head provided in the droplet discharge device so as to form elements composing the thin film transistor. The droplet discharge device having the structure shown in  FIG. 5  can be used in the manufacturing method according to the embodiment.  
       FIG. 5A  is a schematic perspective view showing a structure of a droplet discharge device IJ used in the embodiment.  
      The droplet discharge device IJ has a droplet discharge head  301 , an X-way drive axis  304 , a Y-way guide axis  305 , a controller CONT, a stage  307 , a cleaning mechanical section  308 , a table  309  and a heater  315 .  
      The stage  307  surmounts the substrate P to which the ink (functional liquid) is provided by the droplet discharge device IJ. The stage  307  has an unshown feature to fix the substrate P in a reference position.  
      The droplet discharge head  301  is a multi-nozzle type head equipped with a plurality of discharge nozzles. A Y-axis direction corresponds to the longitudinal direction of the droplet discharge head  301 . A discharge nozzle is provided in the plural number on a lower face of the droplet discharge head  301 . The nozzles align in the Y-axis direction and are provided with a regular space therebetween. From the nozzle of the droplet discharge head  301 , the above-mentioned ink (functional liquid) is discharged to the substrate P that is held by the stage  307 .  
      An X-way driving motor  302  is coupled to the X-way drive axis  304 . The X-way driving motor  302  is a stepping motor and the like, and rotates the X-way drive axis  304  when an X-way driving signal is provided from the controller CONT. When the X-way drive axis  304  is rotated, the droplet discharge head  301  moves in an X-axis direction.  
      The Y-way guide axis  305  is fixed in such a way that its position will not move relative to the table  309 . The stage  307  has a Y-way driving motor  303 . The Y-way driving motor  303  is a stepping motor and the like. When a Y-way driving signal is provided from the controller CONT, the Y-way driving motor  303  moves the stage  307  in the Y-axis direction.  
      The controller CONT supplies a voltage that controls the discharge of droplets to the droplet discharge head  301 . The controller CONT also supplies a drive pulse signal for controlling an X-axis direction movement of the droplet discharge head  301  to the X-way driving motor  302 . The controller CONT also supplies a drive pulse signal for controlling a Y-axis direction movement of the stage  307  to the Y-way driving motor  303 .  
      The cleaning mechanical section  308  cleans the droplet discharge head  301 . The cleaning mechanical section  308  has an unshown Y-directional driving motor. The cleaning mechanical section  308  is driven by the driving motor and moves along with the Y-way guide axis  305 . This movement of the cleaning mechanical section  308  is also controlled by the controller CONT.  
      The heater  315  is used to perform a heat treatment of the substrate P by lamp annealing. Solvent contained in the liquid material that is applied to the substrate P will be evaporated and dried with the heater  315 . Power on and off of this heater  315  is also controlled by the controller CONT.  
      The droplet discharge device IJ discharges a droplet to the substrate P as relatively moving the droplet discharge head  301  and the stage  307  that supports the substrate P. In the following description, the X-axis direction is the scan direction and the Y-axis direction which is orthogonal to the X-axis direction is a non-scan direction. Accordingly, the discharge nozzles of the droplet discharge head  301  align in the Y-axis direction or the non-scan direction and are provided with a regular space therebetween. Though the droplet discharge head  301  is placed orthogonal to the traveling direction of the substrate P as shown in  FIG. 5A , the installed angle of the droplet discharge head  301  can be adjusted so as to cross the traveling direction of the substrate P. By adjusting the angle of the droplet discharge head  301 , it is possible to control the pitch between the nozzles. Furthermore, the distance between the substrate P and the nozzle face may be made freely adjustable.  
       FIG. 5B  is a schematic diagram of the droplet discharge head for explaining the discharge mechanism of ink by a piezo method.  
      In  FIG. 5B , a piezo element  322  is provided adjacent to a liquid room  321  in which the ink (functional liquid) is kept. The ink is supplied to the liquid room  321  through a liquid material supply system  323  including a material tank that stores the ink. The piezo element  322  is coupled to a driving circuit  324 . Voltage is applied to the piezo element  322  through the driving circuit  324  and the piezo element  322  is deformed. The liquid room  321  is elastically deformed by the deformation of the piezo element  322 . Accordingly, the liquid material is discharged from a nozzle  325  due to the variation in the capacity of the liquid room at the time of the elastic deformation.  
      In this case, a degree of distortion of the piezo element  322  can be controlled by changing a value of the applied voltage. A distortion speed of the piezo element  322  can be controlled by changing a frequency of the applied voltage.  
      In the droplet discharge by the piezo method, the material will not be heated so that it has an advantage that composition of the material is hardly affected.  
      Ink (Functional Liquid)  
      Here, the ink (functional liquid) used for forming conductive patterns of the gate electrode  80 , the source electrode  34  and the drain electrode  35  in the manufacturing method of the embodiment will be described.  
      The ink for the conductive pattern used in this embodiment is a dispersion liquid in which conductive particles are dispersed in a dispersion medium or a solution of its precursor. As the conductive particles, for example, metal particles which contain gold, silver, copper, palladium, niobium or nickel, precursors, alloys and oxides of these metal particles, a conductive polymer, particles of indium tin oxide (ITO) and the like can be used. To increase the dispersibility of these conductive particles, the surface of each particle may be coated with an organic material. The diameter of the conductive particle is preferably about 1 nm-0.1 um. When it is larger than 0.1 μm, not only there is a concern of clogging at the nozzle of the liquid discharge head  301 , but also the density of the obtained film could be deteriorated. When it is smaller than 1 nm, the volume ratio of the coating material to the particle becomes large and the ratio of the organic matter which can be obtained in the film could become excessive.  
      The dispersion medium is not particularly limited as long as it can disperse the above-mentioned conductive particles therein without condensation. For example, the examples include, in addition to water; alcohol such as methanol, ethanol, propanol and butanol; hydrocarbon compounds such as n-heptane, n-octane, decane, dodecane, tetradecane, toluene, xylene, cymene, dulene, indent, dipentene, tetrahydronaphthalene, decahydronaphthalene and cyclohexylbenzene; ether compounds such as ethyleneglycoldimethyl ether, ethyleneglycoldiethvl ether, ethyleneglycolmethylethyl ether, diethyleneglycoldimethyl ether, diethylenglycoldiethyl ether, diethyleneglycolmethylethyl ether, 1,2-dirnethoxyethane, bis (2-methoxyethyl)ether, and p-dioxane; and polar compounds such as propylene carbonate, [gamma]-butyrolactone, N-methyl-2-pyrolidone, dimethylformamide, dimethylsulfoxide and cyclohexanone. Among these, water, alcohols, hydrocarbon compounds and ether compounds are preferable in terms of the dispersibility of the particles, stability of the dispersion liquid, and easy application to the droplet discharge method (inkjet method). Water and hydrocarbon compounds are especially preferable as the dispersion medium.  
      It is preferable that the surface tension of the dispersion liquid of the above-mentioned conductive particles is in the range of 0.02 N/m to 0.07 N/m. This is because when liquid is discharged by the droplet discharge method, if the surface tension is less than 0.02 N/m, the wettability of the ink composition with respect to the nozzle surface increases so that the discharge direction tends to deviate. If the surface tension exceeds 0.07 N/m, the shape of the meniscus at the tip of the nozzle becomes unstable, making it difficult to control the discharge amount and the discharge timing. A good way to adjust the surface tension is to add a small amount of a fluorine based, silicon based or nonionic based surface tension modifier to the above-mentioned dispersion liquid to an extent not to largely decrease the contact angle with the substrate. The nonionic surface tension modifier increases the wettability of the liquid on the substrate, improves the leveling property of the film, and helps to prevent the occurrence of minute ruggedness on the film. The above-mentioned surface tension modifier may contain organic compounds such as alcohol, ether, ester, ketone, and the like according to need.  
      The viscosity of the above-mentioned dispersion liquid is preferably above 1 mPa·s and below 50 mPa·s. This is because when liquid material is discharged in the droplet form by the droplet discharge method, if the viscosity is smaller than 1 mPa·s, the area around the nozzle is easily contaminated by the leakage of the ink. If the viscosity is higher than 50 mPa·s, the frequency of clogging occurring at the nozzle hole increases, this not only makes it difficult to smoothly discharge droplets but also decrease the amount of the droplet discharged from the nozzle.  
      For example, a polysilazane solution can be used for forming the first bank B 1  and the second bank B 2 . This polysilazane solution is mainly composed of a solid polysilazane. As such polysilazane solution, a photosensitive polysilazane solution containing the polysilazane and a photo-oxidation product can be employed This photosensitive polysilazane solution serves as a positive resist and it can be directly patterned by exposure and processing. As such photosensitive polysilazane, for example, the polysilazane disclosed in JP-A-2002-72504 can be named. An example of the photo-oxidation product contained in the polysilazane is also disclosed in JP-A-2002-72504.  
      In a case that the polysilazane is a polymethylsilazane presented by chemical formula (1) written below, a part of the polymethylsilazane is hydrolyzed by a hydration treatment which is described later as shown in chemical formula (2) and chemical formula (3). By further conducting a heat treatment lower than 350° C., it is condensed as shown in chemical formulas (4) through (6) and turns into polymethylsiloxane [—(SiCH 3 O 1.5 )n—]. If a heat treatment higher than 350° C. is carried out, desorption of a side-chain methyl group occurs. Especially, the heat treatment higher of 400-450° C. desorbs almost all the side-chain methyl groups and the polymethylsilazane turns into polysiloxane, though its chemical reaction is not shown as the chemical formulae here. It is note that chemical formulas (2) through (6) are simplified and only basic constituent units (repeat units) in the chemical compounds are shown in order to simply explain the reaction mechanism.  
      The polymethylsiloxane or the polysiloxane produced in the above-described way has the polysiloxane skeleton which is inorganic so that a film of these compounds becomes sufficiently dense. Accordingly, the surface of the layer (film) becomes appropriately flat and even. In addition, it has a high heat resistance, and this film is appropriate for the bank material.  
      Chemical Formulae  
      (1) —(SiCH 3 (NH) 1.5 )n— 
      (2) SiCH 3 (NH) 1.5 +H 2 O→SiCH 3 (NH)(OH)+0.5NH 3    
      (3) SiCH 3 (NH) 1.5 +2H 2 O→SiCH 3 (NH) 0.5 (OH) 2 +NH 3    
      (4) SiCH 3 (NH) (OH)+SiCH 3 (NH) (OH)+H 2 O→2SiCH 3 O 1.5 +2NH 3    
      (5) SiCH 3 (NH) (OH)+SiCH 3 (NH) 0.5 (OH) 2 →2SiCH 3 O 1.5 +1.5NH 3    
      (6) SiCH 3 (NH) 0.5 (OH) 2 +SiCH 3 (NH) 0.5 (OH) 2 →2SiCH 3 O 1.5 +NH 3 +H 2 O  
      A Manufacturing Method of TFT Array Substrate  
      Processes of manufacturing method of the TFT array  10  including the method of manufacturing the TFT  60  is hereinafter described with reference to  FIGS. 6 through 11 .  FIGS. 7A through 11C  are a series of sectional views showing processes in the manufacturing method of the invention.  
      Gate Electrode Forming Process  
      In this process, the gate electrode  80  (and the scan line  18   a ) and a plurality of cross-shape alignment marks AM (seven of them in  FIG. 6 ) are formed on the substrate P. The alignment marks AM are used in the processes of forming the gate electrode  80  and the TFT  60 .  
      The alignment marks AM are usually provided in three positions (upper left, upper right and lower right in  FIG. 6 ) in order to carry out alignment in the direction where the scan line  18   a  extends (a X direction), in a Y direction orthogonal to this direction with respect to the substrate P, and in an axial direction (a Z direction) perpendicular to the face of the substrate P. Here, more than one alignment mark is formed in each place (though only the alignment marks positioned at the upper left are shown in the plural number in  FIG. 6 ) because these alignment marks are used at the time when the second electrode layer  80   b  and the semiconductor layer  33  are formed.  
      The glass substrate P made of non-alkali glass and the like is provided. And the first bank B 1  is firstly formed on one face of the substrate as shown  FIG. 7 . The gate electrode  80  is formed in an opening  30  by dropping a prescribed ink (the functional liquid) into the opening  30  formed in the first bank B 1  as shown in  FIG. 8 . This gate electrode forming process includes a bank formation process, a hydrophobicity imparting process, a first electrode layer formation process, a second electrode layer formation process and a baking process.  
      First Bank Formation Process  
      Firstly, in order to form the gate electrode  80  (and the scan line  18   a ) having a designated pattern on the glass substrate, the first bank having the opening in a predetermined pattern is formed on the glass substrate P. This first bank is a partition member that comparts the substrate face in plan. A photolithography method is especially preferable for forming the bank. Specifically describing, the above-mentioned photosensitive polysilazane solution is applied according to the height of the bank formed on the glass substrate P by spin coating, spray coating, roll coating, dye coating, dip coating or the like as shown in  FIG. 7A , forming a polysilazane thin film BL 1 .  
      Subsequently, the obtained polysilazane thin film BL 1  is pre-baked by for example a hotplate at 110° C. for about one minute.  
      The polysilazane thin film BL 1  is then exposed by using a mask M as shown in  FIG. 7B . This mask M has an opening M 1  and an opening M 2 . The opening M 1  is formed at the position and has the shape corresponding to the gate electrode  80  (and the scan line  18   a ). The opening M 2  is formed at the position and has the shape corresponding to the alignment mark AM.  
      Since the polysilazane thin film BL 1  serves as the positive resist at this point as described above, the areas where should be removed in a later performed developing process are selectively exposed. A light source used in this exposure process is adequately selected in consideration of the photosensitivity and the composition of the photosensitive polysilazane solution. Such light source can be selected from the ones used in a common exposure of photoresist such as a high-pressure mercury lamp, a low-pressure mercury lamp, a metal halide lamp, a xenon lamp, an excimer laser, X-rays, electron rays and the like. The amount of energy of the irradiation depends on the employed light source and the film thickness, though it is preferably set to be 0.05 mJ/cm 2  or more, more preferably 0.1 mJ/cm 2  or more. There is no specific upper limit however it is not practical to set a large amount of irradiation energy in terms of processing time. Therefore, it is usually set to smaller than 10,000 mJ/cm 2 . The exposure is usually performed in an ambient atmosphere (the air) or in a nitrogen atmosphere. In stead of these, an oxygen-enriched atmosphere may be used in order to promote decomposition of the polysilazane.  
      After the above-described exposure process is performed to the photosensitive polysilazane thin film BL 1  which contains the photo-oxidation product, acid is selectively generated in the film especially where was exposed and this cleaves a Si—N bond in the polysilazane. It then reacts with water in the atmosphere and the polysilazane thin film BL 1  is partially hydrolyzed as shown in the above chemical formula (2) or chemical formula (3). Eventually, a silanol (Si—OH) bond is formed and the polysilazane is decomposed.  
      Next, in order to further promote the generation of such silanol (Si—OH) bond and the decomposition of the polysilazane, a humidification treatment under a condition of for example 25° C. and 85% relative humidity is performed for about five minutes to the polysilazane thin film BL 1  after the exposure as shown in  FIG. 7C , When water is continuously supplied into the polysilazane thin film BL 1  in this way, the acid which contributed to the cleavage of the Si—N bond in the polysilazane repeatedly works as the cleavage catalyst This Si—OH bond is also generated in the exposure process. However, the humidification treatment after the exposure of the film further promotes the generation of the Si—OH bonds in the polysilazane.  
      The higher the humidity in the atmosphere of the humidification treatment is, the faster the speed of the Si—OH generation can be. However, when the humidity is too high, dew condensation could occur on the surface of the film. In this respect, the relative humidity is practically set to 90% or less. Such humidification treatment can be carried out by contacting the polysilazane thin film BL 1  with the air containing moisture. More specifically, the substrate P after the exposure is placed in humidification treatment equipment and the moisture containing air is successively introduced into the humidification treatment equipment, Alternatively, the substrate P after the exposure is placed in the humidification treatment equipment in which the moisture containing air is already introduced and adjusted to an adequate humidity, and then the substrate is left in the equipment for a certain time period.  
      Next, the polysilazane thin film BL 1  after the humidification treatment is developed with for example 2.38% tetramethylammoniumhydroxide (TMAH) solution at 25° C., and the unexposed part is selectively removed. In this way, a first bank precursor BP 1  having the opening  30  that corresponds to the forming region of the gate electrode  80  and an opening  31  that corresponds to the forming region of the alignment mark AM is formed in this one process. The first bank precursor BP 1  serves as a marking partition wall at the time when the gate electrode  80  and the alignment mark AM are formed. In addition to TMAH, alkaline developers such as choline, sodium silicate, sodium hydroxide and potassium hydroxide can be used.  
      Hydrophobicity Imparting Process  
      Next, after the precursor is rinsed with deionized water if required, a hydrophobicity imparting process is performed so as to impart the hydrophobicity to the surface of the first bank precursor BP 1 . As a method of imparting the hydrophobicity, for example, a plasma treatment (CF 4  plasma treatment) using tetrafluoromethane as a treatment gas in an atmosphere can be adopted. Conditions of the CF 4  plasma treatment in this embodiment are set, for example, as follows; 50-1000 kW of plasma power, 50-100 ml/min of a tetrafluoromethane gas flow rate, 0.5-1020 mm/sec of a substrate transport speed relative to a plasma discharge electrode, and 70-90° C. of the substrate temperature. As the treatment gas, in addition to tetrafluoromethane, other fluorocarbon based gases can be used.  
      By performing such hydrophobic treatment, a fluorine group is introduced into the alkyl group composing the first bank precursor BP 1  and a high hydrophobicity is imparted to the first bank precursor BP 1 .  
      It is preferable that an ashing treatment using O 2  plasma or an ultraviolet (UV) irradiation treatment is performed prior to the above-mentioned hydrophobicity imparting process in order to clean the surface of the substrate P which is exposed on the bottom of the openings  30 ,  31 . With this treatment, remaining of the bank material on the surface of the substrate P can be removed and it is possible to increase a difference in the contact angle between the first bank precursor BP 1  and the substrate surface after the hydrophobic treatment. Consequently, droplets which are provided on the openings  30 ,  31  in a later process can be accurately enclosed inside the openings  30 ,  31 .  
      The above-mentioned O 2  ashing treatment can be performed by irradiating the substrate P with oxygen plasma discharged from the plasma discharge electrode. Conditions of the O 2  ashing treatment are set for example as follows: 50-1000 W of the plasma power, 50-100 ml/min of an oxygen gas flow rate, 0.510-10 mm/sec of the substrate transport speed relative to the plasma discharge electrode, and 70-90° C. of the substrate temperature.  
      The hydrophobicity imparting process (the CF 4  plasma treatment) of the first bank precursor BP 1  has a little affect on the surface of the substrate P where hydrophilicity is given by the above-mentioned remaining removal treatment. However, especially in the case of the glass substrate, the fluorine group is not so much introduced in to the substrate P by the hydrophobicity imparting process. Therefore, the hydrophilicity or wettability of the substrate P will not be lost in a practical sense.  
      First Electrode Layer Formation Process  
      Next, a first electrode layer forming ink (not shown in the figure) and an alignment mark forming ink which is the same material as that of the first electrode layer forming ink are discharged from the liquid discharge head  301  of the droplet discharge device IJ onto the opening  31 . Here, the ink containing the conductive particles made of manganese (Mn) and a tetradecane solvent (dispersion medium) is discharged. At this point, the hydrophobicity is imparted to the surface of the first bank B 1  and the hydrophilicity is given to the substrate surface in the bottom of the opening  31 . Accordingly, even if a part of the discharged droplets is placed on the first bank B 1 , the bank surface respells the droplets and they slip into the opening  31 .  
      After the droplets of the alignment mark forming ink are discharged, a drying process is performed in order to remove the dispersion medium if required. The drying process can be performed by a commonly used heating means to heat the substrate P, for example, a hot plate and an electric furnace. In this embodiment, for example, heating of 180° C. for about 60 minutes is carried out. This heating is not necessarily performed in the air but can be performed in a nitrogen gas atmosphere and the like.  
      This drying process can also be performed by lamp annealing. Light source of the lamp annealing is not particularly limited, though an infrared lamp, a xenon lamp, a YAG laser, an argon laser, a carbon dioxide gas laser, and excimer lasers such as XeF, XeCl, XeBr, KrF, KrCl, ArF and ArCl can be used as the light source. These light sources are generally used in an output range of above 10 W and below 5000 W. However one in a-range of above 100 W and below 1000 W is sufficient for this embodiment. By performing this intermediate drying process, the solid alignment mark AM is formed in the opening  31  as shown in  FIG. 8B .  
      Next, the alignment mark AM formed in the previous process is imaged by an unshown CCD camera and the like, and the droplet discharge head  301  is aligned with the substrate P with reference to the result of the imaging. After that, the ink droplets made of the same material as that of the alignment mark AM are discharged into the opening  30  and then the above-described drying process is performed. In this way, the solid first electrode layer  80   a  is formed in the opening  30  as shown in  FIG. 9A .  
      Second Electrode Layer Formation Process  
      Next, a second electrode layer forming ink (not shown in the figure) is discharged by the droplet discharge method using the droplet discharge device and the ink is placed in the opening  30  of the first bank precursor BP 1 . At this point, the alignment mark AM formed in the previous process is also imaged by the unshown CCD camera and the like, and the droplet discharge head  301  is aligned with the substrate P with reference to the result of the imaging.  
      Here, the ink containing the conductive particles made of silver (Ag) and a diethylene glycol diethylether solvent (dispersion medium) is discharged. At this point, the hydrophobicity is already imparted to the surface of the first bank precursor BP 1  and the hydrophilicity is given to the substrate surface in the bottom of the opening  30 . Accordingly, even if a part of the discharged droplets is placed on the precursor BP 1 , the bank surface respells the droplet and it slips into the opening  30 . It is note that the surface of the first electrode layer  80   a  which is formed in the opening  30  ahead does not always have a high affinity for the ink that is discharged in this process. In that case, an interlayer that improves the wettability of the ink may be formed on the first electrode layer  80   a  prior to the ink discharge. A material for the interlayer is selected according to the type of the dispersion medium of the ink. Where the ink uses aqueous dispersion medium like this embodiment, an interlayer made of for example titanium oxide is formed so as to obtain a fine wettability at the surface of the interlayer.  
      After the droplets are discharged, the same drying process as the above-described one is preformed in order to remove the dispersion medium if required. The drying process can be performed by a commonly used heating means to heat the substrate P, for example, a hot plate and an electric furnace. In this embodiment, the heating conditions are for example 180° C. for about 60 minutes. This heating is not necessarily performed in the air but can be performed in the nitrogen gas atmosphere and the like.  
      This drying process can also be performed by the lamp annealing. As the light source of the lamp annealing, the above-mentioned ones used in the intermediate drying process after the first electrode layer formation process can be used. The power of the heating can also be in the range of above 100 W and below 1000 W, By carrying out this intermediate drying process, the solid second electrode layer  80   b  is formed on the first electrode layer  80   a  as shown in  FIG. 9B .  
      After that, in the same manner as the first electrode layer  80   a  and the second electrode layer  8 Db, an ink containing conductive particles of Ni and the like dispersed in an organic dispersion medium is discharged into the opening  30  and the drying process is subsequently performed. In this way, the cap layer  81  is formed on the second electrode layer  80   b  as shown in  FIG. 9C .  
      Baking Process  
      The dispersion medium should be completely removed from the dried film after the discharged process in order to improve the electric contact among conductive particles. In case that the surface of the conductive particle is coated with an organic coating agent and the like in order to improve the dispersibility in the solution, this coating should be removed. For this purpose, the substrate after the discharge process is treated with heat and/or light.  
      This heat treatment and/or the light treatment are normally performed in the air. However, it may be performed in an inert gas atmosphere such as hydrogen, nitrogen, argon and helium. The temperature of the heat treatment and/or the light treatment is determined considering the boiling point (vapor pressure) of the dispersion medium, the type and the pressure of the atmosphere gas, the thermal behavior such as the dispersibility or the oxidizing property of the particles, the presence/absence of the coating, and the heat resistant temperature of the substrate. In this embodiment, the first electrode layer  80   a , the second electrode layer  80   b  and the cap layer  81  are made of the above-mentioned materials so that the baking temperature is set to less than 300° C.  
      By conducting the above-described processes, the dried film after the discharge process turns into the conductive film in which the electric contact is secured among the particles, and the gate electrode  80  having the layered structure composed of the first electrode layer  80   a , the second electrode layer  80   b  and the cap layer  81  is formed as shown in  FIG. 9C . The scan line  18   a  integrated with the gate electrode  80  is also formed on the glass substrate P through the above-described processes as shown in  FIG. 3 .  
      Semiconductor Layer Formation Process  
      Next, as shown in  FIG. 10A , the gate insulating film  83  made of SiNx and the semiconductor layer  33  including the amorphous silicon layer  84  and the N +  silicon layer  85  are formed by a plasma chemical vapor deposition (CVD) method in which material gases and the plasma conditions are adequately selected. The amorphous silicon layer  84  and the N +  silicon layer  85  are formed by depositing an amorphous silicon film and a N +  silicon film by the CVD method and then patterning them into a prescribed pattern by a photolithography method. This patterning is performed by selectively providing a resist having a substantially concave shape which is similar to the side cross-sectional configuration of the semiconductor layer  33  shown in the figure on the surface of the N +  silicon film, and then conducting an etching using this resist as a mask. By this patterning, the area of the N +  silicon layer  85  where overlaps the gate electrode  80  in plan is selectively removed to be divided into two regions, These N +  silicon layers  85 ,  85  are respectively turned into a source contact region and a drain contact region.  
      In a bank formation process in the second layer following the semiconductor layer formation process, the second bank B 2  is formed on the gate insulating film  83  as shown in  FIG. 10B . At the same time, the second bank B 3  is formed over the area between the divided N +  silicon layers  85 ,  85  by patterning by the photolithography method. The second bank B 3  electrically isolates between the N +  silicon layers  85 ,  85 .  
      When the patterning by the photolithography method is performed in the above-described semiconductor layer formation process and the second layer bank formation process, the mask is aligned with the substrate P by measuring the above-mentioned alignment mark AM.  
      The CCD camera imaging the alignment mark AM preferably has a light source which has a high transparency with the gate insulating film  83  made of SiNx, the amorphous silicon film and the N +  silicon film and has a low transparency with the alignment mark AM (Mn) so that it becomes easier to recognize the alignment mark AM. Since this alignment mark AM is further used in a later process, it is preferable that the amorphous silicon film and the N +  silicon film be removed from the alignment mark AM formed area at the time of the patterning of the amorphous silicon film and the N +  silicon film.  
      Electrode Formation Process  
      Next, the source electrode  34  and the drain electrode  35  shown in  FIG. 4  is formed on the glass substrate P on which the semiconductor layer  33 .  
      Hydrophobicity Imparting Process  
      The hydrophobicity imparting process is performed so as to impart the hydrophobicity to the surface to the second banks B 2 , B 3 . As the method of imparting the hydrophobicity, for example, the plasma treatment (CF 4  plasma treatment) using tetrafluoromethane as the treatment gas in an atmosphere can be adopted.  
      Electrode Film Formation Process  
      Next, the ink (functional liquid) for forming the source electrode  34  and the drain electrode  35  shown in  FIG. 4  is discharged into the area surrounded by the second bank parts B 2 , B 3  by the above-mentioned droplet discharge device IJ. Before conducting the discharge, the droplet discharge device IJ is aligned with the substrate P by using the above-mentioned alignment mark AM. Here, the ink containing the conductive particles made of silver and the diethylene glycol diethylether solvent (dispersion medium) is discharged. After the droplets are discharged, the drying process is preformed in order to remove the dispersion medium if required. The drying process can be performed by a commonly used heating means to heat the substrate P, for example, a hot plate and an electric furnace. In this embodiment, the heating conditions are for example 180° C. for about 60 minutes. This heating is not necessarily performed in the air but can be performed in the nitrogen gas atmosphere and the like.  
      This drying process can also be performed by the lamp annealing. As the light source of the lamp annealing, the above-mentioned ones used in the intermediate drying process after the first electrode layer formation process can be used. The power of the heating can also be in the range of above 100 W and below 1000 W.  
      Baking Process  
      The dispersion medium should be completely removed from the dried film after the discharged process in order to improve the electric contact among conductive particles. In case that the surface of the conductive particle is coated with an organic coating agent and the like in order to improve the dispersibility in the solution, this coating should be removed. For this purpose, the substrate after the discharge process is treated with heat and/or light. Conditions of this heat and/or light treatment can be the same as those of the above described baking process in the formation of the gate electrode  80 .  
      By conducting the above-described processes, the dried film after the discharge process turns into the conductive film in which the electric contact is secured among the particles, and the source electrode  34  which conductively couples with one N +  silicon layers  85  and the drain electrode  35  which conductively couples with the other N +  silicon layers  85  as shown in  FIG. 11A  are formed.  
      Next, the insulating material  86  is provided in a concave portion (opening) defined by the second banks B 2 , B 3  and in which the source electrode  34  and the drain electrode  35  are formed so as to fill the concave portion (opening) as shown in  FIG. 11B .  
      Next, the contact hole  87  is formed in the insulating material  86  where is closed to the drain electrode  35  as shown in  FIG. 11C . Subsequently, a transparent electrode layer made of ITO and the like is formed by a liquid phase method such as the droplet discharge method (ink-Jet method) or a gas phase method such sputtering and a vapor deposition method, and then it is patterned if required to form the pixel electrode  19 .  
      In any step of the above-mentioned processes, the substrate P is aligned with reference to the result of observation of the above-mentioned alignment mark AM.  
      Through the above described processes, the TFT  60  according to the embodiment of the invention is formed on the inner side (the upper side in the figure) of the glass substrate P, and the TFT array substrate  10  having the film structure including the pixel electrode  19  and the TFT can be obtained.  
      As described above, this embodiment forms the alignment mark AM having a low transparency is formed in the opening  31  of the first bank B 1 . Therefore, it is possible to recognize the alignment mark AM with a high recognition accuracy. Accordingly, it is possible to accurately align the substrate P with the droplet discharge head  301  and the mask used in the photolithography process and the like according to the embodiment. As a result, the patterns of the gate electrode  80 , the semiconductor layer  33  and the like can be formed with a high precision.  
      Furthermore, the patterns overlaid on the substrate P are formed by using the same alignment mark AM in this embodiment. This makes it possible to improve the accuracy to overlay the pattern (wirings such as the gate electrode  80  and the semiconductor layer  33 ) formed in each layer.  
      Moreover, the alignment mark AM is made of the same material as that of the first electrode layer  80   a  formed by the droplet discharge method right after the formation of the alignment mark AM in this embodiment. Therefore, a preparation work such as ink change is not necessary and this improves the manufacturing efficiency as well as prevents the contamination of the ink. In addition, the same bank B 1  is used in the formation of the alignment mark AM and the gate electrode  80  (the scan line  18   a ) in the same manufacturing process according to the embodiment. This can further improve the manufacturing efficiency.  
      Furthermore, the first electrode layer  80 a is formed of a material having a higher adhesion with the substrate P than that of the second electrode layer  80   b  according to the embodiment. Accordingly, it is possible to form the gate electrode  80  which has the high adhesion with the substrate P and a defect such as coming off from the substrate is not likely to occur.  
      Next, a plasma type display device is described as an example of the electrooptical device of the invention.  
       FIG. 12  is an exploded perspective view of a plasma type display device  500  of this embodiment.  
      The plasma type display device  500  includes glass substrates  501 ,  502  that oppose each other and an electric discharge display part  510  formed between the glass substrates  501 ,  502 .  
      Address electrodes  511  are formed in a stripe form with a predetermined space therebetween on the upper face of the glass substrate  501  A dielectric layer  519  is formed so as to cover the upper faces of the address electrodes  511  and the glass substrate  501 . A partition wall  515  is formed between two address electrodes  511 ,  511  so as to extend along the address electrode  511  on the dielectric layer  519 . A fluorescent material  517  is provided in a strip area defined by the partition walls  515 . The fluorescent material  517  produces a fluorescence light colored in one of red, green and blue. A red fluorescent material  517  (R) is provided on the bottom and the side faces of a red discharge room  516  (R), a green fluorescent material  517  (G) is provided on the bottom and the side faces of a green discharge room  516  (G), and a blue fluorescent material  517  (B) is provided on the bottom and the side faces of a blue discharge room  516  (B).  
      A display electrode  512  which is a plurality of transparent conductive films formed in a stripe form in the direction orthogonal to the direction where the address electrodes  511  extends with a certain space therebetween is formed on the glass substrate  502 . A bus electrode  512   a  supporting the display electrode  512  that has a high resistance is formed on the display electrode  512 . A dielectric layer  513  is formed so as to cover the above-mentioned elements and a protection film  514  made of MgO and the like is further formed.  
      The glass substrate  501  and the glass substrate  502  are adhered together so as to oppose each other in such a way that the address electrodes  511  orthogonally cross the display electrodes  512 .  
      The electric discharge display part  510  includes a plurality of the discharge rooms  516 . One pixel is an area surrounded by a group of three discharge rooms  516 , that are the red discharge room  516  (R), the green discharge room  516  (G) and the blue discharge room  516  (B), and a pair of the display electrodes.  
      The address electrodes  511  and the display electrodes  512  are coupled to an unshown alternating current (AC) source. The fluorescent material is excited and emits light in the electric discharge display part  510  when current is applied to each electrode. In this way, a color display is realized.  
      In this embodiment, the bus electrode  512   a  and the address electrodes  511  are formed by the above described patterning method. Accordingly, the adhesion of the bus electrode  512   a  and the address electrodes  511  are high and defects in the wiring are hardly happened. In addition, these elements are aligned with a high precision. It is also possible to densely provide wirings because the accurate alignment of the wirings is possible. An alignment mark is formed by the droplet discharge method so that the formation process is much simpler relative to that of the photolithography technique and it is possible to reduce the production cost of the device.  
      Where the interlayer is made of a manganese compound (manganese oxide), a necessary electric conductivity between the display electrodes  512  and the bus electrode  512   a  can be secured by making the manganese layer very thin and porous even though the manganese oxide is not conductive. In this case, the interlayer shows a color of black. Such interlayer can serve like a black matrix and this can improve the display contrast.  
      Next, specific examples of electronic equipment of the invention are described.  
       FIG. 13A  is a perspective view of a mobile phone as an example. In  FIG. 13A , reference numeral  600  refers to a body of the mobile phone and reference numeral  601  refers to a liquid crystal display part in which the above-described liquid crystal device is employed.  
       FIG. 13B  is a perspective view of a portable information-processing device such as a word processor and a personal computer as an example. In  FIG. 13B , reference numeral  700  refers to the information-processing device, reference numeral  701  refers to an input unit such as a keyboard, reference numeral  703  refers to a body of the information-processing device, and reference numeral  702  refers to a liquid crystal display part in which the above-described liquid crystal device is employed.  
       FIG. 13C  is a perspective view of watch type electronic equipment as an example. In  FIG. 13C , reference numeral  800  refers to a body of the watch and reference numeral  801  refers to a liquid crystal display part in which the above-described liquid crystal device is employed.  
      The electronic equipment showed in  FIGS. 13A through 13C  have the liquid crystal display devices of the embodiment as a display means. Therefore, it is possible to obtain high quality electronic equipment.  
      Though the electronic equipments of the embodiment have the liquid crystal device, it can have other electrooptical device such as an organic electroluminescence display device and a plasma type display device instead.  
      Although the embodiments of the invention have been fully described by way of example with reference to the accompanying drawings, it is to be understood that the embodiments described above do not in any way limit the scope of the invention. Configuration or combination of the above-mentioned members in the embodiments is just an example, and various changes and modifications will be applied within the scope and spirit of the invention in compliance of demands.  
      For example, though the droplet discharge process for forming the alignment mark AM is separated from the droplet discharge process for forming the first electrode layer  80   a  in the above described embodiment, these processes may be performed in one process in order to improve the manufacturing rate.  
      Though the wiring pattern has two layered structure of the first electrode layer  80   a  and the second electrode layer  80   b  in the above described embodiment, the wiring pattern can be made of a single layer or a multilayered structure of more than two layers. Where the pattern is the multilayered structure of more than two layers, it is preferable that a layer having a most strong adhesion with the substrate be placed as the first layer (or closest to the substrate). This is because the adhesion between the substrate and the pattern can be increased in this way and the defect of coming off will less occur.  
      Though the configuration of the alignment mark AM is the cross shape when viewed in plan in the above described embodiment, the configuration can be other shapes. For example, the alignment mark AM can be made of two parts such as a larger part AM 1  which has a wide width and a smaller part AM 2  which has a narrow width as shown  FIGS. 14A through 14C .  
      In this case, droplets can be discharged into the larger part AM 1  and then the droplets can autonomously flow into the smaller part to fill there. In this way, it is possible to shorten the time to provide the droplets.  
      The alignment mark AM may have other configurations. Such configurations are for example shown in  FIGS. 15A through 15G . As shown in  FIG. 15A , a first line pattern  901  crosses a second line pattern  902 . The alignment mark AM is composed of the larger part AM 1  which has a wide width and a smaller part AM 2  which has a narrow width. In this case, the larger part AM 1  is the landing point of the droplets. Here, the size of the smaller part AM 2  is denoted as a width “b” and the size of the larger part AM 1  is denoted as a diameter “D”. The diameter “D” is larger than (&gt;) the width “b” as shown in the figure. The length of the smaller part AM 2  is decided according to the surface property (wettability) of the glass substrate P. When the wettability of the glass substrate P is fine (shows a high hydrophilicity), the length of the smaller part AM 2  will be long. Contrary, when the wettability of the glass substrate P is not fine (shows a high hydrophobicity), the length of the smaller part AM 2  will be short. It is possible to judge whether a desired surface treatment is performed to the surface of the glass substrate P or not from the length of the smaller part AM 2 . This judgment can be further used to decide whether drawing on the glass substrate P can be subsequently performed or not. If the surface condition of the glass substrate P is as fine as desired, the drawing can be subsequently carried out. If the surface condition of the glass substrate P is not yet fine, the drawing can be suspended and the substrate can be reproduced. In this way, it is possible to prevent the material from being wasted and to perform a wasteful work. The alignment mark shown in  FIG. 15B  has two landing points of the droplets, and the first line pattern  901  crosses the second line pattern  902 . The alignment mark has two larger parts AM 1  which are wide and two smaller parts AM 2  which are narrow. The alignment mark shown in  FIG. 15C  has one landing point of the droplets, and the first line pattern  901  crosses the second line pattern  902 . The alignment mark has one wide larger part AM 1  and two narrow smaller parts AM 2 . The alignment mark shown in  FIG. 15D  has two landing point of the droplets that have a rectangular shape, and the first line pattern  901  crosses the second line pattern  902 . The alignment mark has two larger parts AM 1  that are formed in a wide rectangular shape and two smaller parts AM 2  that are formed in a narrow rectangular shape. Here, the size of the smaller part AM 2  is denoted as a width “b” and the size of the larger part AM 1  having the rectangular shape is denoted as a width “B”. The alignment mark shown in  FIG. 15E  has two landing points of the droplets, and the first line pattern  901  crosses the second line pattern  902 . The alignment mark has two larger parts AM 1  which are wide and two smaller parts AM 2  which are narrow. As shown in the figure, the alignment mark AM is arranged diagonal to the side face of the substrate when viewed in plan. The alignment mark shown in  FIG. 15F  has two landing points of the droplets, and the first line pattern  901  crosses the second line pattern  902 . The alignment mark has two larger parts AM 1  which are wide and two smaller parts AM 2  which are narrow. The angle a between the first line pattern  901  and the second line pattern  902  is smaller than 90° as shown in the figure. The alignment mark shown in  FIG. 15G  has two landing points of the droplets, and the first line pattern  901  crosses the second line pattern  902 . The alignment mark has two larger parts AM 1  which are wide and two smaller parts AM 2  which are narrow. The width “b 2 ” of the second line pattern  902  is smaller than the width “b 1 ” of the first line pattern  901  as shown in the figure. Meanwhile, as for the material for the alignment mark, a material having a high reflectivity can be used since the reflection rate of illumination light can be made high, making the contrast higher when it is imaged by a CCD camera and the like. In this way, it is preferable that the material forming the alignment mark is adequately selected based on imaging properties of the imaging means.  
      Technical ideas encompassed in the above described embodiments will be hereinafter described.  
      First Technical Idea  
      According to the patterning method described any of Claims  1  through  11 , the patterning method forms the alignment mark having the first line pattern and the second line pattern that crosses the first line pattern.  
      In this way, the alignment can be easily done by utilizing the first line pattern  90 l and the second line pattern  902  because the first line pattern  901  is provided so as to cross the second line pattern  902 .  
      Second Technical Idea  
      According to the patterning method described any of Claims  1  through  11 , the patterning method forms the alignment mark having the first line pattern and the second line pattern that crosses the first line pattern, and the width of the first line pattern and the width of the second line pattern are smaller than the size of the droplet landing area.  
      In this way, the alignment can be precisely performed by utilizing the first line pattern  901  and the second line pattern  902  because the width “d” is smaller than the diameter “D” of the larger part AM 1  which is the landing point of the droplets. Consequently, it is possible to provide the liquid crystal display device  100  with a good quality.  
      Third Technical Idea  
      According to the patterning method described any of Claims  1  through  11 , the patterning method forms the alignment mark having the first line pattern and the second line pattern that crosses the first line pattern, and the width of one of the first line pattern or the second line pattern is made narrower than the other.  
      In this way, it is possible to handle wiring patterns with various widths by making the width of one of the first line pattern or the second line pattern narrower. Consequently, it is possible to provide various kinds of the liquid crystal display device  100 .