Patent Publication Number: US-11648759-B2

Title: Electroconductive film, touch panel, and image display device

Description:
CROSS-REFERENCE TO RELATED APPLICATION 
     The present application enjoys the benefit of priority to the prior Japanese Patent Application Nos. 2016-195230 (filed on Sep. 30, 2016), 2016-195231 (filed on Sep. 30, 2016), 2016-195233 (filed on Sep. 30, 2016), 2016-195234 (filed on Sep. 30, 2016), and 2017-74413 (filed on Apr. 4, 2017), the entire disclosures of which are incorporated herein by reference. 
     TECHNICAL FIELD 
     The present invention relates to an electroconductive film, a touch panel, and an image display device. 
     BACKGROUND ART 
     Recent image display devices such as smartphone and tablet terminal may comprise a touch panel system that enables direct input of information by touching an image display screen with a finger or the like. 
     A touch panel typically comprises an electroconductive film that comprises an electroconductive part provided on a light-transmitting base material and indium tin oxide (ITO) is mainly used as an electroconductive material for such electroconductive parts of light-transmitting electroconductive films. However, ITO lacks flexibility, and an electroconductive part using ITO is thus prone to crack in cases where a flexible base material is used as the light-transmitting base material. 
     Accordingly, the use of metallic nanowire such as silver nanowire instead of ITO is currently studied as an electroconductive material to constitute the electroconductive part (see, for example, WO 2013/118643). 
     SUMMARY OF THE INVENTION 
     
         
         (1) Currently, an electroconductive film using metallic nanowires as electroconductive materials is desired to achieve a lower haze value and a lower surface resistance value. In this respect, it is envisaged that the amount of metallic nanowires contained in an electroconductive part is increased to achieve a low surface resistance value because the surface resistance tends to decrease with increasing content of metallic nanowires, but an increased content of metallic nanowires results in a higher haze value. Because of this problem, an electroconductive film having a low haze value and a low surface resistance value has not yet been obtained. 
       
    
     Additionally, in cases where many metallic nanowires are exposed on the surface of an electroconductive part, the metallic nanowires are likely to react with, for example, sulfur, oxygen, and/or halogens in the air, so that the electrical conductivity is reduced.
     (2) As described above, an electroconductive film using metallic nanowires as electroconductive materials is desired to achieve a lower haze value and a lower surface resistance value. However, when an electroconductive film is formed by using metallic nanowires, a difference in electrical resistance depending on the in-plain direction or area of an electroconductive part occurs. If the electrical resistance is different depending on the in-plain direction or area of the electroconductive part and the electroconductive film is used as an electrode for a touch panel sensor, the patterning of the electrode and/or the resulting IC chips may be limited, as well as the electroconductive film is limited in imposition and is thus prone to be wasted.   (3) As described above, an electroconductive film using metallic nanowires as electroconductive materials is desired to achieve a lower haze value and a lower surface resistance value. An underlayer is often provided on at least one surface of a light-transmitting resin base material for the purpose of, for example, improving adhesion to other layers, inhibiting the electroconductive film from sticking to itself when the electroconductive film is rolled, and/or inhibiting cissing of a coating liquid applied for forming another layer.   

     However, in cases where an electroconductive part is formed by using a metallic nanowire-containing composition containing metallic nanowires and a dispersion medium on the surface of an underlayer, permeation of the dispersion medium into the underlayer, the extent of which varies depending on the type of the dispersion medium, such as an aqueous dispersion medium or a solvent-based dispersion medium, used for dispersion of the metallic nanowires, may cause transfer of the metallic nanowires into the underlayer to increase the surface resistance value. A large amount of metallic nanowires is needed to achieve a low surface resistance value under this condition and is thus likely to result in a high haze value. 
     On the other hand, in cases where a layer impermeable to the dispersion medium is provided on the light-transmitting resin base material to prevent the transfer of the metallic nanowires into the underlayer, a layer having excellent hardness, specifically a hard coat layer, is generally provided. However, a hard coat layer provided on the light-transmitting resin base material causes a lack of flexibility, which may cause cracks in the resulting electroconductive film when the electroconductive film is folded.
     (4) As described above, an electroconductive film using metallic nanowires as electroconductive materials is desired to achieve a lower haze value and a lower surface resistance value. In the electroconductive film, enough flexibility to fold may currently be required. However, the electroconductive film using metallic nanowires often comprises a hard coat layer provided between a light-transmitting base material and an electroconductive part for providing hardness, which may cause cracks in the electroconductive film (particularly, the hard coat layer) when the electroconductive film is folded and also cause an increased resistance value of the electroconductive part due to the crack formation in the electroconductive film.   

     Additionally, in cases where an electroconductive film is used in a touch panel, electric wirings that adhere to an electroconductive part of the electroconductive film are located behind a bezel of the touch panel. Although the electric wirings are generally formed by using an electroconductive paste (for example, a silver paste), electric wirings composed of a cured electroconductive paste may have poor adhesion to an electroconductive film depending on the type of the electroconductive paste. Thus, an electroconductive film is currently desired to have excellent adhesion to an electroconductive paste, regardless of the type of the electroconductive paste. 
     The present invention is designed to solve the above problems. That is, an object of the present invention is to provide (1) an electroconductive film that can achieve a low haze value and a low surface resistance value and prevent reduction in electrical conductivity due to the reaction of electroconductive fibers with substances in the atmosphere, (2) an electroconductive film that can achieve a low haze value and a low surface resistance value and has reduced the difference in electrical resistance value depending on the in-plain direction of an electroconductive part, (3) an electroconductive film that can achieve a low haze value and a low surface resistance value and has flexibility, or (4) an electroconductive film that can achieve a low haze value and a low surface resistance value and has flexibility and can increase choices of electroconductive pastes, and to provide a touch panel and an image display device comprising any of these electroconductive films. 
     The first aspect of the present invention provides a light-transmitting electroconductive film comprising a light-transmitting base material and an electroconductive part provided on one surface of the light-transmitting base material, wherein the electroconductive part comprises a light-transmitting resin and plural electroconductive fibers incorporated in the light-transmitting resin; the electroconductive part can conduct electricity from the surface of the electroconductive part; the electroconductive fibers as a whole are unevenly distributed on the light-transmitting base material side than the position located at half the film thickness of the electroconductive part in the electroconductive part; the electroconductive part has a surface resistance value of 200Ω/□ or less; and the electroconductive film has a haze value of 5% or less. 
     The second aspect of the present invention provides a light-transmitting electroconductive film comprising a light-transmitting base material and an electroconductive part provided on one surface of the light-transmitting base material, wherein the electroconductive part comprises a light-transmitting resin and plural electroconductive fibers incorporated in the light-transmitting resin; the ratio of the electrical resistance in a first direction to that in a second direction is 1 or more and less than 2 when the electrical resistance values on the surface of the electroconductive part are measured in a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface of the electroconductive part, wherein a direction in which the electroconductive part shows the lowest electrical resistance value is designated as the first direction, and a direction which is perpendicular to the first direction is designated as the second direction; the electroconductive part has a surface resistance value of 200Ω/□ or less; and the electroconductive film has a haze value of 5% or less. 
     The third aspect of the present invention provides a light-transmitting electroconductive film comprising a light-transmitting resin base material and an electroconductive part provided on at least one surface of the light-transmitting resin base material, wherein the electroconductive part comprises a light-transmitting resin and plural electroconductive fibers incorporated in the light-transmitting resin; the electroconductive part can conduct electricity from the surface of the electroconductive part; the electroconductive part is provided directly on at least one surface of the light-transmitting resin base material; the electroconductive part has a surface resistance value of 200Ω/□ or less; and the electroconductive film has a haze value of 5% or less. 
     The fourth aspect of the present invention provides a light-transmitting electroconductive film comprising an underlayer and an electroconductive part in this order on at least one surface of a light-transmitting resin base material, wherein the electroconductive part comprises a light-transmitting resin and plural electroconductive fibers incorporated in the light-transmitting resin; the underlayer is provided directly on at least one surface of the light-transmitting resin base material; the electroconductive part is provided directly on the underlayer; the electroconductive part has a surface resistance value of 200Ω/□ or less; and the electroconductive film has a haze value of 5% or less. 
     In the above second to fourth electroconductive films, the electroconductive part preferably contains no particles having a particle size larger than the film thickness of the light-transmitting resin. 
     In the above second to fourth electroconductive films, the electroconductive part preferably contains no particles. 
     In the above third and fourth electroconductive films, the ratio of the electrical resistance in a first direction to that in a second direction may be 1 or more and less than 2 when the electrical resistance values on the surface of the electroconductive part are measured in a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface of the electroconductive part, wherein a direction in which the electroconductive part shows the lowest electrical resistance value is designated as the first direction, and a direction which is perpendicular to the first direction is designated as the second direction. 
     In the above first, the third, and the fourth electroconductive films, the ratio of the electrical resistance in a first direction to that in a second direction may be 2 or more when the electrical resistance values on the surface of the electroconductive part are measured in a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface of the electroconductive part, wherein a direction in which the electroconductive part shows the lowest electrical resistance value is designated as the first direction, and a direction which is perpendicular to the first direction is designated as the second direction. 
     In the above first to fourth electroconductive films, the electroconductive film may have a total light transmittance of 80% or more. 
     In the above first to fourth electroconductive films, the electroconductive fibers may be one or more types of fibers selected from the group consisting of electroconductive carbon fibers, metallic fibers, and metal-coated synthetic fibers. 
     In the above first, the third, and the fourth electroconductive films, the electroconductive fibers may have a fiber diameter of 200 nm or less and a fiber length of 1 μm or more. 
     In the above fourth electroconductive film, the electroconductive fibers may have a fiber diameter of 200 nm or less and a fiber length of 10 μm or more and less than 30 μm. 
     In the above second to fourth electroconductive films, the electroconductive fibers as a whole may be unevenly distributed on the light-transmitting base material side than the position located at half the film thickness of the electroconductive part in the electroconductive part. 
     Another aspect of the present invention provides a touch panel comprising the above-described electroconductive film. 
     Another aspect of the present invention provides an image display device comprising the above-described touch panel. 
     Another aspect of the present invention provides a method of producing the above-described electroconductive film, wherein the method of producing a light-transmitting electroconductive film comprising a light-transmitting base material and an electroconductive part provided on at least one surface of the light-transmitting base material comprises the steps of: applying and drying an electroconductive fiber-containing composition containing electroconductive fibers and an organic dispersion medium on at least one surface of the light-transmitting base material to place the electroconductive fibers on the one surface; and covering the electroconductive fibers with a light-transmitting resin after placing the electroconductive fibers on the one surface. 
     Another aspect of the present invention provides a method of producing the above-described electroconductive film, comprising the steps of: applying an electroconductive fiber-containing composition containing electroconductive fibers and an organic dispersion medium directly on at least one surface of a light-transmitting resin base material and drying the electroconductive fiber-containing composition to place the electroconductive fibers directly on the one surface; and covering the electroconductive fibers with a light-transmitting resin after placing the electroconductive fibers directly on the one surface. 
     Another aspect of the present invention provides a method of producing the above-described electroconductive film, comprising the steps of: applying an electroconductive fiber-containing composition containing electroconductive fibers and a dispersion medium directly on a surface of an underlayer in a laminate, which comprises a light-transmitting resin base material and the underlayer provided directly on at least one surface of the light-transmitting resin base material, and drying the electroconductive fiber-containing composition to place the electroconductive fibers on the surface of the underlayer: and covering the electroconductive fibers with a light-transmitting resin after placing the electroconductive fibers directly on the surface of the underlayer. 
     ADVANTAGEOUS EFFECTS OF THE INVENTION 
     According to the first aspect of the present invention, an electroconductive film can achieve a low haze value and a low surface resistance value and prevent reduction in electrical conductivity due to the reaction of the electroconductive fibers with substances in the atmosphere, since the electroconductive part comprises a light-transmitting resin and plural electroconductive fibers incorporated in the light-transmitting resin; the electroconductive part can conduct electricity from the surface of the electroconductive part; the electroconductive fibers as a whole are unevenly distributed on the light-transmitting base material side than the position located at half the film thickness of the electroconductive part in the electroconductive part; the electroconductive part has a surface resistance value of 200Ω/□ or less; and the electroconductive film has a haze value of 5% or less. According to the second aspect of the present invention, an electroconductive film that can achieve a low haze value and low surface resistance value and has reduced the difference in electrical resistance depending on the in-plain direction of the electroconductive part can be provided, since the ratio of the electrical resistance in a first direction to that in a second direction is 1 or more and less than 2 when the electrical resistance values on the surface of the electroconductive part are measured in a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface of the electroconductive part, wherein a direction in which the electroconductive part shows the lowest electrical resistance value is designated as the first direction, and a direction which is perpendicular to the first direction is designated as the second direction; the electroconductive part has a surface resistance value of 200Ω/□ or less; and the electroconductive film has a haze value of 5% or less. According to the third aspect of the present invention, an electroconductive film that can achieve a low haze value and a low surface resistance value and has flexibility can be provided, since an electroconductive part is provided directly on at least one surface of a light-transmitting resin base material; the electroconductive part has a surface resistance value of 200Ω/□ or less; and the electroconductive film has a haze value of 5% or less. According to the fourth aspect of the present invention, an electroconductive film that can achieve a low haze value and a low surface resistance value and has flexibility and can increase choices of electroconductive pastes can be provided, since underlayer is provided directly on at least one surface of a light-transmitting resin base material; an electroconductive part is provided directly on the underlayer; the electroconductive part has a surface resistance value of 200Ω/□ or less; and the electroconductive film has a haze value of 5% or less. Additionally, according to a touch panel and an image display device of other aspects of the present invention, a touch panel and an image display device comprising such the electroconductive film can be provided. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG.  1    depicts a schematic diagram of an electroconductive film according to the first embodiment. 
         FIG.  2    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  1   . 
         FIG.  3    depicts a layout drawing of samples excised from the electroconductive film according to the embodiment. 
         FIG.  4    depicts a plane view of a sample measured for electrical resistance. 
         FIG.  5    depicts a schematic diagram of another electroconductive film according to the first embodiment. 
         FIG.  6    depicts a schematic plane view of the electroconductive film shown in  FIG.  5   . 
         FIG.  7    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  5   . 
         FIG.  8    depicts a schematic diagram of another electroconductive film according to the first embodiment. 
         FIG.  9    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  8   . 
         FIGS.  10 (A) and  10 (B)  schematically illustrate the process for producing the electroconductive film according to the first embodiment. 
         FIGS.  11 (A) and  11 (B)  schematically illustrate the process for producing the electroconductive film according to the first embodiment. 
         FIGS.  12 (A) and  12 (B)  schematically illustrate the process for producing the electroconductive film according to the first embodiment. 
         FIG.  13    depicts a schematic diagram of an image display device according to the first embodiment. 
         FIG.  14    depicts a schematic plane view of a touch panel according to the first embodiment. 
         FIG.  15    depicts an enlarged view of a part of the electroconductive film on the side of the display panel shown in  FIG.  13   . 
         FIG.  16    depicts a schematic diagram of an electroconductive film according to the second embodiment. 
         FIG.  17    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  16   . 
         FIG.  18    depicts a schematic diagram of another electroconductive film according to the second embodiment. 
         FIG.  19    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  18   . 
         FIG.  20    depicts a schematic diagram of an image display device according to the second embodiment. 
         FIG.  21    depicts a schematic diagram of an electroconductive film according to the third embodiment. 
         FIG.  22    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  21   . 
         FIGS.  23 (A),  23 (B) and  23 (C)  schematically illustrate each step of the foldability test. 
         FIG.  24    depicts a schematic diagram of another electroconductive film according to the third embodiment. 
         FIG.  25    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  24   . 
         FIGS.  26 (A),  26 (B) and  26 (C)  schematically illustrate the process for producing the electroconductive film according to the third embodiment. 
         FIGS.  27 (A) and  27 (B)  schematically illustrate the process for producing the electroconductive film according to the third embodiment. 
         FIG.  28    depicts a schematic diagram of an image display device according to the third embodiment. 
         FIG.  29    depicts a schematic diagram of an electroconductive film according to the fourth embodiment. 
         FIG.  30    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  29   . 
         FIG.  31    depicts a schematic diagram of another electroconductive film according to the fourth embodiment. 
         FIG.  32    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  31   . 
         FIGS.  33 (A),  33 (B) and  33 (C)  schematically illustrate the process for producing the electroconductive film according to the fourth embodiment. 
         FIGS.  34 (A) and  34 (B)  schematically illustrate the process for producing the electroconductive film according to the fourth embodiment. 
         FIG.  35    depicts a schematic diagram of an image display device according to the fourth embodiment. 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     First Embodiment 
     Now, the electroconductive film, touch panel, and image display device according to the first embodiment of the present invention will be described below with reference to the drawings. The term “light-transmitting” as used herein refers to a property of transmitting light. Additionally, the term “light-transmitting” does not necessarily refer to transparency and may refer to translucency.  FIG.  1    depicts a schematic diagram of an electroconductive film according to the present embodiment, while  FIG.  2    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  1   .  FIG.  3    depicts a layout drawing of samples excised from the electroconductive film according to the present embodiment, while  FIG.  4    depicts a plain view of a sample measured for electrical resistance.  FIGS.  5  and  8    depict schematic diagrams of other electroconductive films according to the present embodiment;  FIG.  6    depicts a schematic plain view of the electroconductive film shown in  FIG.  5   ;  FIG.  7    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  5   ; and  FIG.  9    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  8   .  FIGS.  10  to  12    schematically illustrate the process for producing the electroconductive film according to the present embodiment. 
     &lt;&lt;&lt;Electroconductive Film&gt;&gt;&gt; 
     The electroconductive film  10  shown in  FIG.  1    is light transmissive and comprises a light-transmitting base material  11 , a light-transmitting functional layer  12  provided on at least one surface of the light-transmitting base material  11 , and an electroconductive part  13  provided and patterned on a surface of the light-transmitting functional layer  12  opposite to the light-transmitting base material  11  side surface. However, the electroconductive film  10  should comprise the light-transmitting base material  11  and the electroconductive part  13 , and may not comprise the light-transmitting functional layer  12 . The absence of the light-transmitting functional layer  12  can improve the flexibility. The light-transmitting functional layer  12  is provided between the light-transmitting base material  11  and the electroconductive part  13 ; a light-transmitting functional layer may be provided not between the light-transmitting base material  11  and the electroconductive part  13  but on a surface of the light-transmitting base material  11  opposite to the electroconductive part  13  side surface, or may be provided both between the light-transmitting base material  11  and the electroconductive part  13  and on a surface of the light-transmitting base material  11  opposite to the electroconductive part  13  side surface. Additionally, in the electroconductive film  10  shown in  FIG.  1   , the electroconductive part  13  is provided on only one surface of the electroconductive film, but electroconductive parts may be provided on both surfaces of the electroconductive film. 
     The electroconductive part  13  shown in  FIG.  1    is a film with no pattern, namely a so-called plain film. The surface  10 A of the electroconductive film  10  is constituted by the surface  13 A of the electroconductive part  13 . 
     The electroconductive film  10  has a haze value (total haze value) of 5% or less. In cases where the electroconductive film  10  has a haze value of more than 5%, the electroconductive film may suffer from insufficient optical properties. The haze value can be measured using a haze meter (product name “HM-150”; manufactured by Murakami Color Research Laboratory Co., Ltd.) according to JIS K7136: 2000. The haze value is a value measured on the whole electroconductive film and is also determined as the arithmetic mean of three measurement values obtained from one electroconductive film, wherein a sample having a size of 50 mm×100 mm is cut from the electroconductive film and the sample without curl or wrinkle and without fingerprints or dust then placed in the haze meter in such a manner that the electroconductive part faces in the direction opposite to the light source (this shall not apply to an electroconductive film comprising electroconductive parts on the both sides). The term “three measurements” as used herein does not mean three measurements at the same location and shall mean measurements at three different locations. The surface  10 A of the electroconductive film  10  is visually determined to be flat, and the laminated layers, such as the electroconductive part  13 , likewise have a flat surface, and the deviation of film thickness is also within ±10%. Thus, the measurement of haze value at three different locations on the cut electroconductive film is considered to provide a rough average of the haze values measured on the whole electroconductive film. Additionally, if a sample having the above-described size cannot be cut from the electroconductive film, a sample having a size equal to or greater than a diameter of 21 mm is required because, for example, the HM-150 haze meter has an entrance port aperture having a diameter of 20 mm for use in the measurement. Thus, a sample having a size of 22 mm×22 mm or larger may be cut from the electroconductive film as appropriate. In cases where the electroconductive film is small in size, the electroconductive film is gradually shifted or turned in such an extent that the light source spot is within the electroconductive film, and three points of measurement are thereby obtained. The electroconductive film  10  has a haze value of 3% or less, 2% or less, 1.5% or less, 1.2% or less, or 1.1% or less in ascending order of preference (a lower value is more preferred). The deviation of the obtained haze value is within ±10% even though the measurement object has such a long size as a size of 1 m×3000 m or has almost the same size as that of a 5-inch smartphone; in cases where the deviation is within the above-described range, a low haze value and a low resistance value are more easily obtained. Additionally, although the electroconductive part of the electroconductive film  10  is not patterned, the total light transmittance is 5% or less, 3% or less, 2% or less, 1.5% or less, 1.2% or less, or 1.1% or less in ascending order of preference (a lower value is more preferred) even in an electroconductive film comprising a patterned electroconductive part. Additionally, also in a whole multi-layered laminate such as a touch panel sensor comprising an electroconductive film, the haze value is preferred to be the same as described above. 
     The electroconductive film  10  preferably has a total light transmittance of 80% or more. In cases where the electroconductive film has a total light transmittance of less than 80%, the electroconductive film may suffer from insufficient optical properties. The total light transmittance can be measured using a haze meter (product name “HM-150”; manufactured by Murakami Color Research Laboratory Co., Ltd.) according to JIS K7361-1: 1997. The total light transmittance is a value measured on the whole electroconductive film and is also determined as the arithmetic mean of three measurement values obtained from one electroconductive film, wherein a sample having a size of 50 mm×100 mm is cut from the electroconductive film and the sample without curl or wrinkle and without fingerprints or dust is then placed in the haze meter in such a manner that the electroconductive part faces in the direction opposite to the light source (this shall not apply to an electroconductive film comprising electroconductive parts on the both sides). The surface  10 A of the electroconductive film  10  is visually determined to be flat, and the laminated layers, such as the electroconductive part  13 , likewise have a flat surface, and the deviation of film thickness is also within ±10%. Thus, the measurement of total light transmittance at three different locations on the excised electroconductive film is considered to provide a rough average of the total light transmittance values measured on the whole electroconductive film. Additionally, if a sample having the above-described size cannot be cut from the electroconductive film, a sample having a size equal to or greater than a diameter of 21 mm is required because, for example, the HM-150 haze meter has an entrance port aperture having a diameter of 20 mm for use in the measurement. Thus, a sample having a size of 22 mm×22 mm or larger may be cut from the electroconductive film as appropriate. In cases where the electroconductive film is small in size, the electroconductive film is gradually shifted or turned in such an extent that the light source spot is within the electroconductive film, and three points of measurement are thereby obtained. The electroconductive film  10  has a total light transmittance of 85% or more, 88% or more, or 89% or more in ascending order of preference (a higher value is more preferred). Additionally, although the electroconductive part of the electroconductive film  10  is not patterned, the total light transmittance is 80% or more, 85% or more, 88% or more, or 89% or more in ascending order of preference (a higher value is more preferred) even in an electroconductive film comprising a patterned electroconductive part. The deviation of the obtained total light transmittance is within ±10% even though the measurement object has such a long size as a size of 1 m×3000 m or has almost the same size as that of a 5-inch smartphone; in cases where the deviation is within the above-described range, a low haze value and a low resistance value are more easily obtained. Additionally, also in a whole multi-layered laminate such as a touch panel sensor comprising an electroconductive film, the total light transmittance is preferred to be the same as described above. 
     The application of the electroconductive film according to the present invention, including the below-described electroconductive films  20 ,  30 ,  100 ,  110 ,  150 ,  160 ,  250 , and  260  as well as the electroconductive film  10 , is not limited to a particular application, and may be used in various applications, for example, in which a transparent electroconductive film is used. Additionally, the electroconductive film of the present invention may be used for electrical appliances and windows for use in houses and vehicles (including all types of vehicles such as trains and heavy-duty vehicles) as well as for products related to image display devices (including smartphone, tablet terminal, wearable terminal, personal computer, television, digital signage, public information display (PID), vehicle display, and the like). In particular, the electroconductive film of the present invention can suitably be used for products in which transparency is critical. Additionally, the electroconductive film of the present invention can suitably be used for electrical appliances in which not only technical features, such as transparency, but also designs are essential. Specific examples of the application of the electroconductive film according to the present invention include defrosters, antennas, solar cells, audio systems, loudspeakers, electric fans, interactive whiteboards, and carrier films for semiconductors and the like. 
     The electroconductive film of the present invention may be cut into a piece having a desired size or be rolled. In cases where the electroconductive film of the present invention has been cut into a piece having a desired size, the size of the electroconductive film piece is not limited to a particular size, and the size is appropriately determined depending on the display size of an image display device. Specifically, the electroconductive film piece may be, for example, 5 inches or more and 500 inches or less in size. The term “inch” as used herein shall mean the length of a diagonal when the electroconductive film is rectangular and to the length of a diameter when the electroconductive film is circular and to the average of major and minor axes when the electroconductive film is elliptical. In this respect, when the electroconductive film is rectangular, the aspect ratio of the electroconductive film which is measured to have the above-described inches is not limited to a particular aspect ratio as long as no problem is found with the electroconductive film to be used for the display screen of an image display device. Examples of the aspect ratio include height-to-width ratios of 1:1, 4:3, 16:10, 16:9, and 2:1. However, particularly in electroconductive films used for vehicle display and digital signage which are rich in designs, the aspect ratio is not limited to the above-described aspect ratios. Additionally, in cases where the electroconductive film  10  is large in size, the electroconductive film is appropriately trimmed starting at an arbitrary position to an easy-handling size such as A4 size (210 mm×297 mm) or A5 size (148 mm×210 mm) and then trimmed to fit size requirements of each measurement item. 
     &lt;&lt;Light-Transmitting Base Material&gt;&gt; 
     The light-transmitting base material  11  is not limited to a particular light-transmitting base material as long as it is light transmissive. Examples of the constituent material of the light-transmitting base material  11  include light-transmitting resins, such as polyolefin resins, polycarbonate resins, polyacrylate resins, polyester resins, aromatic polyetherketone resins, polyethersulfone resins, polyimide resins, polyamide resins, and polyamide-imide resins. Among those light-transmitting resins, polyester resins are preferred because a light-transmitting base material composed of a polyester resin is hardly damaged even upon contacting to a coating machine and is thus capable of inhibiting increase of haze value though the light-transmitting base material is contacted to a coating machine for coating of a light-transmitting functional layer or the like and thus likely to be damaged, as well as a light-transmitting base material composed of a polyester resin has superior heat resistance, barrier property, and water resistance to those of light-transmitting base materials composed of any light-transmitting resin other than polyester resins; additionally, polyimide resins and polyamide resins are preferred in terms of flexibility. 
     Examples of the polyolefin resin include resins composed of at least one of, for example, polyethylene, polypropylene, and cyclic polyolefin base materials. Examples of the cyclic polyolefin resin include resins having the norbornene backbone. 
     Examples of the polycarbonate resin include aromatic polycarbonate resins containing a bisphenol (such as bisphenol A) as a base material, and aliphatic polycarbonate resins such as diethylene glycol bis(allyl carbonate). 
     Examples of the polyacrylate resin include methyl poly(meth)acrylate base materials, ethyl poly(meth)acrylate base materials, and methyl (meth)acrylate-butyl (meth)acrylate copolymers. 
     Examples of the polyester resin include resins composed of at least one of polyethylene terephthalate (PET), polypropylene terephthalate, polybutylene terephthalate, and polyethylene naphthalate (PEN). 
     Examples of the aromatic polyetherketone resin include polyether ether ketone (PEEK). 
     A polyimide resin can be obtained from the reaction between a tetracarboxylic component and a diamine component. Preferably, a tetracarboxylic component and a diamine component are polymerized to form a polyamic acid, which is then imidized. The imidization may be heat imidization or chemical imidization. Additionally, a polyimide resin can also be produced by a combinational method of heat imidization and chemical imidization. The polyimide resin may be an aliphatic polyimide resin, and is preferably an aromatic polyimide resin containing aromatic rings. The aromatic polyimide resin is composed of a tetracarboxylic component and a diamine component, at least one of which is an aromatic ring-containing component. Tetracarboxylic dianhydride are suitably used as specific examples of the tetracarboxylic component, and may be used individually or in combination of two or more. Diamines produced by substitution of some or all hydrogen atoms in an aromatic ring of any of the diamines with a substituent(s) selected from fluoro, methyl, methoxy, trifluoromethyl, and trifluoromethoxy groups can also be used. These may be used individually or in combination of two or more. 
     For improving the light transmittance and the rigidity, the polyimide resin preferably contains an aromatic ring and at least one selected from the group consisting of: (i) a fluorine atom, (ii) an aliphatic ring, and (iii) a linking group that interrupts the electron conjugation between donor and acceptor aromatic rings; more preferably contains at least one of (i) and (iii). In a polyimide resin, the presence of an aromatic ring enhances the orientation of the polyimide resin itself and increases the rigidity but tends to decrease the transmittance depending on the absorption wavelength of the aromatic ring. In cases where the polyimide resin contains (i) a fluorine atom, the fluorine atom can give the polyimide backbone an electron configuration to inhibit electron transfer, and consequently improves the light transmittance. Also, in cases where the polyimide resin contains (ii) an aliphatic ring, the aliphatic ring can interrupt the pi-electron conjugation within the polyimide backbone to inhibit electron transfer within the backbone, and consequently improves the light transmittance. Furthermore, in cases where the polyimide resin contains (iii) a linking group that interrupts the electron conjugation between donor and acceptor aromatic rings, the linking group can interrupt the pi-electron conjugation within the polyimide backbone to inhibit electron transfer within the backbone, and consequently improves the light transmittance. Examples of such a linking group that interrupts the electron conjugation between donor and acceptor aromatic rings include ether linkage, thioether linkage, carbonyl linkage, thiocarbonyl linkage, amide linkage, sulfonyl linkage, and, sulfinyl linkage, as well as divalent linking groups such as alkylene groups optionally substituted by fluorine. 
     Among those polyimide resins, a polyimide resin containing an aromatic ring and a fluorine atom is preferably used in terms of improving the light transmittance and the rigidity. In the fluorine atom-containing polyimide resin, the ratio of fluorine atom number (F) to carbon atom number (C), F/C, is preferably 0.01 or more, further preferably 0.05 or more, when those atom numbers are determined by analyzing the surface of the polyimide resin by X-ray photoelectron spectroscopy. On the other hand, an excessively high content of fluorine atom is likely to result in reduction of, for example, the heat resistance inherent to the polyimide resin, and the ratio of fluorine atom number (F) to carbon atom number (C), F/C, is thus preferably 1 or less, further preferably 0.8 or less. In this respect, the above-described ratio obtained by X-ray photoelectron spectroscopy (XPS) can be calculated from the atom percentages of the respective atoms measured using an X-ray photoelectron spectrometer (for example, Theta Probe, Thermo Scientific Inc.). 
     Additionally, a polyimide resin in which 70% or more of the hydrogen atoms bound to the carbon atoms are directly bound to the aromatic rings is preferably used in terms of improving the light transmittance and the rigidity. In the polyimide resin, the ratio of the (number of) hydrogen atoms directly bound to the aromatic rings to the total (number of) hydrogen atoms bound to the carbon atoms is further preferably 80% or more, more preferably 85% or more. A polyimide in which 70% or more of the hydrogen atoms bound to the carbon atoms are directly bound to the aromatic rings is preferred because optical properties, particularly total light transmittance and yellow index (YI), vary less in the resulting optical film even after a heating process in the atmosphere, such as a stretching process at a temperature of 200° C. or higher. A polyimide resin in which 70% or more of the hydrogen atoms bound to the carbon atoms are directly bound to the aromatic rings has a low reactivity with oxygen, from which the chemical structure of the polyimide resin is predicted to hardly change. A base material composed of a polyimide resin is often used in devices that require taking advantage of the high heat resistance of the polyimide resin for a processing process involving a heating process in the production of the devices. A polyimide resin in which 70% or more of the hydrogen atoms bound to the carbon atoms are directly bound to the aromatic rings does not need the later stage processes performed in inert atmosphere to maintain the transparency of the resulting optical film, and can advantageously save costs for equipment and for maintenance of the atmosphere. In this respect, the ratio of the (number of) hydrogen atoms directly bound to the aromatic rings to the total (number of) hydrogen atoms bound to the carbon atoms in a polyimide resin can be determined by analyzing degradation products of the polyimide using high-performance liquid chromatography, a gas chromatograph mass spectrometer, and NMR. For example, a sample is degraded with an aqueous alkaline solution or supercritical methanol and the obtained degradation products are separated by high-performance liquid chromatography. Each separated peak is qualitatively analyzed using a gas chromatograph mass spectrometer, NMR, and the like, while quantitatively analyzed using high-performance liquid chromatography, whereby the ratio of the (number of) hydrogen atoms directly bound to the aromatic rings to the total (number of) hydrogen atoms bound to the carbon atoms in the polyimide can be determined. 
     Additionally, the polyimide resin preferably has at least one structure selected from the group consisting of the structures represented by the general formula (1) below and the general formula (3) below, among others, in terms of improving the light transmittance and the rigidity. 
     
       
         
         
             
             
         
       
     
     In the above-described general formula (1), R 1  represents a tetracarboxylic acid residue as a tetravalent group; R 2  represents at least one divalent group selected from the group consisting of trans-cyclohexanediamine residue, trans-1,4-bismethylene cyclohexanediamine residue, 4,4′-diaminodiphenyl sulfone residue, 3,4′-diaminodiphenyl sulfone residue, and divalent groups represented by the general formula (2) below; n represents the number of repeating units, which is 1 or more. In this specification, the “tetracarboxylic acid residue” refers to a residue remaining after subtracting four carboxylic groups from a tetracarboxylic acid, and represents the same structure as a residue remaining after subtracting the acid dianhydride structure from a tetracarboxylic dianhydride. Additionally, the “diamine residue” refers to a residue remaining after subtracting two amino groups from a diamine. 
     
       
         
         
             
             
         
       
     
     In the above-described general formula (2), R 3  and R 4  each independently represent a hydrogen atom, alkyl group, or perfluoroalkyl group. 
     
       
         
         
             
             
         
       
     
     In the above-described general formula (3), R 5  represents at least one tetravalent group selected from the group consisting of cyclohexane tetracarboxylic acid residue, cyclopentane tetracarboxylic acid residue, a dicyclohexane-3,4,3′,4′-tetracarboxylic acid residue, and a 4,4′-(hexafluoroisopropylidene)diphthalic acid residue; R 6  represents a diamine residue as a divalent group; n′ represents the number of repeating units, which is 1 or more. 
     In the above-described general formula (1), R 1  refers to a tetracarboxylic acid residue and can represent, as indicated above, a residue remaining after subtracting the acid dianhydride structure from a tetracarboxylic dianhydride. As R 1  in the above-described general formula (1), at least one selected from the group consisting of 4,4′-(hexafluoroisopropylidene)diphthalic acid residue, 3,3′,4,4′-biphenyl tetracarboxylic acid residue, pyromellitic residue, 2,3′,3,4′-biphenyl tetracarboxylic acid residue, 3,3′,4,4′-benzophenone tetracarboxylic acid residue, 3,3′,4,4′-diphenylsulfone tetracarboxylic acid residue, 4,4′-oxydiphthalic acid residue, cyclohexane tetracarboxylic acid residue, and cyclopentane tetracarboxylic acid residue is preferably contained, among others, in terms of improving the light transmittance and the rigidity. At least one selected from the group consisting of 4,4′-(hexafluoroisopropylidene)diphthalic acid residue, 4,4′-oxydiphthalic acid residue, and 3,3′,4,4′-diphenylsulfone tetracarboxylic acid residue is further preferably contained. 
     As R 1 , those suitable residues are contained in total preferably at a content of 50% by mole or more, further preferably 70% by mole or more, and still further preferably 90% by mole or more. 
     Additionally, a combination of at least one selected from a group of tetracarboxylic acid residues suitable for improving the rigidity (group A), such as the group consisting of 3,3′,4,4′-biphenyl tetracarboxylic acid residue, 3,3′,4,4′-benzophenone tetracarboxylic acid residue, and pyromellitic residue, and at least one selected from a group of tetracarboxylic acid residues suitable for improving the transparency (group B), such as the group consisting of 4,4′-(hexafluoroisopropylidene)diphthalic acid residue, 2,3′,3,4′-biphenyl tetracarboxylic acid residue, 3,3′,4,4′-diphenylsulfone tetracarboxylic acid residue, 4,4′-oxydiphthalic acid residue, cyclohexane tetracarboxylic acid residue, and cyclopentane tetracarboxylic acid residue, is preferably used as R 1 . 
     For the content ratio of the group of tetracarboxylic acid residues suitable for improving the rigidity (group A) to the group of tetracarboxylic acid residues suitable for improving the transparency (group B) in that case, preferably 0.05 moles or more and 9 moles or less, further preferably 0.1 moles or more and 5 moles or less, still further preferably 0.3 moles or more and 4 moles or less, of the group of tetracarboxylic acid residues suitable for improving the rigidity (group A) are combined with 1 mole of the group of tetracarboxylic acid residues suitable for improving the transparency (group B). 
     In the above-described general formula (1), R 2  preferably represents at least one divalent group selected from the group consisting of 4,4′-diaminodiphenyl sulfone residue, 3,4′-diaminodiphenyl sulfone residue, and divalent groups represented by the above-described general formula (2), further preferably at least one divalent group selected from the group consisting of 4,4′-diaminodiphenyl sulfone residue, 3,4′-diaminodiphenyl sulfone residue, and divalent groups represented by the above-described general formula (2) where R 3  and R 4  each represent a perfluoroalkyl group, among others, in terms of improving the light transmittance and the rigidity. 
     As R 5  in the above-described general formula (3), 4,4′-(hexafluoroisopropylidene)diphthalic acid residue, 3,3′,4,4′-diphenylsulfone tetracarboxylic acid residue, and oxydiphthalic acid residue are preferably contained, among others, in terms of improving the light transmittance and the rigidity. 
     As R 5 , those suitable residues are contained preferably at a content of 50% by mole or more, further preferably 70% by mole or more, and still further preferably 90% by mole or more. 
     In the above-described general formula (3), R 6  refers to a diamine residue and can represent, as indicated above, a residue remaining after subtracting two amino groups from a diamine. As R 6  in the above-described general formula (3), preferably at least one divalent group selected from the group consisting of 2,2′-bis(trifluoromethyl)benzidine residue, bis[4-(4-aminophenoxy)phenyl]sulfone residue, 4,4′-diaminodiphenyl sulfone residue, 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane residue, bis[4-(3-aminophenoxy)phenyl]sulfone residue, 4,4′-diamino-2,2′-bis(trifluoromethyl)diphenyl ether residue, 1,4-bis[4-amino-2-(trifluoromethyl)phenoxy]benzene residue, 2,2-bis[4-(4-amino-2-trifluoromethylphenoxy)phenyl]hexafluoropropane residue, 4,4′-diamino-2-(trifluoromethyl)diphenyl ether residue, 4,4′-diaminobenzanilide residue, N,N′-bis(4-aminophenyl)terephthalamide residue, and 9,9-bis(4-aminophenyl)fluorene residue, further preferably at least one divalent group selected from the group consisting of 2,2′-bis(trifluoromethyl)benzidine residue, bis[4-(4-aminophenoxy)phenyl]sulfone residue, and 4,4′-diaminodiphenyl sulfone residue, is contained, among others, in terms of improving the light transmittance and the rigidity. 
     As R 6 , those suitable residues are contained in total preferably at a content of 50% by mole or more, further preferably 70% by mole or more, and still further preferably 90% by mole or more. 
     Additionally, a combination of at least one selected from a group of diamine residues suitable for improving the rigidity (group C), such as the group consisting of bis[4-(4-aminophenoxy)phenyl]sulfone residue, 4,4′-diaminobenzanilide residue, N,N′-bis(4-aminophenyl)terephthalamide residue, paraphenylenediamine residue, methaphenylenediamine residue, and 4,4′-diaminodiphenylmethane residue, and at least one selected from a group of diamine residues suitable for improving the transparency (group D), such as the group consisting of 2,2′-bis(trifluoromethyl)benzidine residue, 4,4′-diaminodiphenyl sulfone residue, 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane residue, bis[4-(3-aminophenoxy)phenyl]sulfone residue, 4,4′-diamino-2,2′-bis(trifluoromethyl)diphenyl ether residue, 1,4-bis[4-amino-2-(trifluoromethyl)phenoxy]benzene residue, 2,2-bis[4-(4-amino-2-trifluoromethylphenoxy)phenyl]hexafluoropropane residue, 4,4′-diamino-2-(trifluoromethyl)diphenyl ether residue, and 9,9-bis(4-aminophenyl)fluorene residue, is preferably used as R 6 . 
     For the content ratio of the group of diamine residues suitable for improving the rigidity (group C) to the group of diamine residues suitable for improving the transparency (group D) in that case, preferably 0.05 moles or more and 9 moles or less, further preferably 0.1 moles or more and 5 moles or less, more preferably 0.3 moles or more and 4 moles or less, of the group of diamine residues suitable for improving the rigidity (group C) are combined with 1 mole of the group of diamine residues suitable for improving the transparency (group D). 
     For the structures represented by the above-described general formulae (1) and (3), n and n′ each independently represent the number of repeating units, which is 1 or more. The number of repeating units, n, in the polyimide may be appropriately selected depending on the structure to allow the polyimide to have a preferred glass transition temperature as described below, and is not limited to a particular number. The average number of repeating units is typically 10 to 2,000, further preferably 15 to 1,000. 
     Additionally, the polyimide resin may partially contain a polyamide structure. Examples of the polyamide structure that may be contained include a polyamide-imide structure containing a tricarboxylic acid residue such as trimellitic anhydride, and a polyamide structure containing a dicarboxylic acid residue such as terephthalic acid. 
     The polyimide resin preferably has a glass transition temperature of 250° C. or higher, further preferably 270° C. or higher, in terms of heat resistance, while the polyimide resin preferably has a glass transition temperature of 400° C. or lower, further preferably 380° C. or lower, in terms of ease of stretching and of reducing the baking temperature. 
     Specific examples of the polyimide resin include compounds having the structure represented by the formula below. In the formula below, n represents the number of repeating units, which is an integer of 2 or more. 
     
       
         
         
             
             
         
       
       
         
         
             
             
         
       
       
         
         
             
             
         
       
     
     The weight average molecular weight of the above-described polyimide resin preferably ranges from 3,000 to 500,000 inclusive, more preferably from 5,000 to 300,000, and further preferably from 10,000 to 200,000 inclusive. In cases where the weight average molecular weight is 3,000 or more, the resin can have enough strength; in cases where the weight average molecular weight is 500,000 or less, the resin can prevent increase of viscosity and reduction of solubility, which in turn results in success to provide a film material with smooth surface and homogeneous film thickness. In this specification, the “weight average molecular weight” is measured by gel permeation chromatography (GPC) as a value in terms of polystyrene. 
     Among the above-described polyimide resins, the polyimide or polyamide resins having structures that inhibit intramolecular or intermolecular charge transfer are preferred due to the excellent transparency, specifically including the fluorinated polyimide resins represented by, for example, the above-described formulae (4) to (11), and the polyimide resins containing alicyclic structures represented by, for example, the above-described formulae (13) to (16). 
     Additionally, the fluorinated polyimide resins represented by, for example, the above-described formulae (4) to (11) each contain a fluorinated structure and thus have a high heat resistance, which protects a polyimide film composed of any of the polyimide resins from coloration by the heat generated during the synthesis and helps the polyimide film to maintain excellent transparency. 
     The concept of polyamide resin includes aromatic polyamides (aramids) as well as aliphatic polyamides. The polyamide resin generally refers to a resin having the backbone represented by the formula (21) or (22) below, and examples of the above-described polyamide resin include a compound represented by the formula (23) below. In the formula below, n represents the number of repeating units, which is an integer of 2 or more. 
     
       
         
         
             
             
         
       
     
     A commercially available base material may be used as a base material composed of the polyimide or polyamide resin represented by any of the above-described formulae (4) to (20) and (23). Examples of a commercially available base material composed of the above-described polyimide resin include Neopulim and the like manufactured by Mitsubishi Gas Chemical Company, Inc., while examples of a commercially available base material composed of the above-described polyamide resin include Mictron and the like manufactured by Toray Industries, Inc. 
     Additionally, a base material synthesized by a known method may be used as a base material composed of the polyimide or polyamide resin represented by any of the above-described formulae (4) to (20) and (23). For example, the polyimide resin represented by the above-described formula (4) is synthesized by a method described Japanese Patent Application Publication No. 2009-132091 and can be obtained, specifically, by a reaction of 4,4′-hexafluoropropylidenebisphthalic dianhydride (FPA) and 2,2′-bis(trifluoromethyl)-4,4′-diaminobiphenyl (TFDB), as represented by the formula (24) below. 
     
       
         
         
             
             
         
       
     
     The weight average molecular weight of the above-described polyimide or polyamide resin preferably ranges from 3,000 to 500,000 inclusive, more preferably from 5,000 to 300,000, and further preferably from 10,000 to 200,000 inclusive. In cases where the weight average molecular weight is less than 3,000, the resin may not have enough strength; in cases where the weight average molecular weight is more than 500,000, the resin has an increased viscosity and a reduced solubility, which in turn may result in failure to provide a base material with smooth surface and homogeneous film thickness. In this specification, the “weight average molecular weight” is measured by gel permeation chromatography (GPC) as a value in terms of polystyrene. 
     Among the above-described polyimide and polyamide resins, the polyimide or polyamide resins having structures that inhibit intramolecular or intermolecular charge transfer are preferred due to the excellent transparency, specifically including the fluorinated polyimide resins represented by, for example, the above-described formulae (4) to (11), the polyimide resins containing alicyclic structures represented by, for example, the above-described formulae (13) to (16), and the halogenated polyamide resin represented by, for example, the above-described formula (23). 
     Additionally, the fluorinated polyimide resins represented by, for example, the above-described formulae (4) to (11) each contain a fluorinated structure and thus have a high heat resistance, which protects a base material composed of any of the polyimide resins from coloration by the heat generated during the synthesis of the polyimide resin and helps the polyimide resin to maintain excellent transparency. 
     For the light-transmitting base material  11 , a base material composed of the fluorinated polyimide resin represented by, for example, any of the above-described formulae (4) to (11) or composed of halogenated polyamide resin represented by, for example, the above-described formula (23) is preferably used in terms of the ability to achieve excellent hardness. Among those base materials, a base material composed of the polyimide resin represented by the above-described formula (4) is more preferably used because use of the base material can provide very excellent hardness to the resulting optical film. 
     The thickness of the light-transmitting base material  11  is not limited to a particular thickness, and the thickness can be 3 μm or more and 500 μm or less; the minimum thickness of the light-transmitting base material  11  is 10 μm or more or 20 μm or more in ascending order of preference (a higher value is more preferred) from the viewpoint of, for example, handling properties. The maximum thickness of the light-transmitting base material  11  is 250 μm or less, 100 μm or less, 80 μm or less, 60 μm or less, or 40 μm or less in ascending order of preference (a lower value is more preferred) from the viewpoint of thinning the electroconductive film. The thickness of the light-transmitting base material can be measured by the same measurement method as for the film thickness of the below-described electroconductive part. 
     The light-transmitting base material  11  may have a surface treated by a physical treatment such as corona discharge treatment or oxidation treatment to improve the adhesiveness. Additionally, the light-transmitting base material  11  may have an underlayer on at least one surface for the purpose of improving adhesion to other layers, preventing the electroconductive film from sticking to itself when the electroconductive film is rolled, and/or inhibiting cissing of a coating liquid applied for forming another layer. In this specification, however, the underlayer provided on at least one surface of the light-transmitting base material and attached to the light-transmitting base material will be an integral part of the light-transmitting base material and will never be a part of the light-transmitting functional layer. 
     The underlayer contains, for example, an anchoring agent and/or a priming agent. As the anchoring agent and the priming agent, at least any of, for example, polyurethane resins, polyester resins, polyvinyl chloride resins, polyvinyl acetate resins, vinyl chloride-vinyl acetate copolymers, acrylic resins, polyvinyl alcohol resins, polyvinyl acetal resins, copolymers of ethylene and vinyl acetate or acrylic acid, copolymers of ethylene and styrene and/or butadiene, thermoplastic resins such as olefin resins and/or modified resins thereof, polymers of radiation-polymerizable compounds, polymers of thermopolymerizable compounds, and the like can be used. 
     The underlayer may contain particles of a lubricant or the like for the purpose of preventing the electroconductive film from sticking to itself when the electroconductive film is rolled, as described above. Examples of the particles include silica particles. 
     &lt;&lt;Light-Transmitting Functional Layer&gt;&gt; 
     The light-transmitting functional layer  12  is placed between the light-transmitting base material  11  and the electroconductive part  13 . The term “light-transmitting functional layer” as used herein refers to a layer transmitting light and intended to achieve some functions in the electroconductive film. Specific examples of the light-transmitting functional layer include layers which exhibit functions, such as hard coat properties, refractive index modulation, and/or color modulation. The light-transmitting functional layer may have a monolayer structure or a multilayer structure composed of two or more laminated layers. In cases where the light-transmitting functional layer is a laminate composed of two or more layers, each layer may have the same or a different function. In this embodiment, the light-transmitting functional layer  12  is described as a layer having hard coat properties, namely a hard coat layer. 
     The light-transmitting functional layer  12  functions as a hard coat layer, as described above, and the light-transmitting functional layer  12  exhibits a hardness of “H” or harder in the pencil hardness test (at a load of 4.9 N) specified by JIS K5600-5-4: 1999. By limiting the pencil hardness to a hardness of “H” or harder, the resulting electroconductive film  10  can have sufficient hardness and increase durability. The maximum pencil hardness of the surface  13 A of the electroconductive part  13  is preferably around 4 H in terms of the toughness of the light-transmitting functional layer and from the viewpoint of inhibiting curling. 
     The light-transmitting functional layer  12  preferably has a film thickness of 0.5 μm or more and 15 μm or less. By limiting the film thickness to a value within the above range, the light-transmitting functional layer  12  can achieve a desired hardness. The film thickness of the light-transmitting functional layer can be measured by the same measurement method as for the film thickness of the below-described electroconductive part. The minimum film thickness of the light-transmitting functional layer  12  is 1 μm or more, 1.5 μm or more, or 2 μm or more in ascending order of preference (a higher value is more preferred) from the viewpoint of inhibiting curling. Additionally, the maximum film thickness of the light-transmitting functional layer  12  is 12 μm or less, 10 μm or less, 7 μm or less, or 5 μm or less in ascending order of preference (a lower value is more preferred) from the viewpoint of inhibiting cracks from occurring in the light-transmitting functional layer. 
     The light-transmitting functional layer  12  can be composed of at least a light-transmitting resin. The light-transmitting functional layer  12  may additionally contain inorganic particles, organic particles, and a leveling agent, in addition to a light-transmitting resin. 
     &lt;Light-Transmitting Resin&gt; 
     The light-transmitting resin in the light-transmitting functional layer  12  includes resins containing a polymer (a cured or cross-linked product) of a polymerizable compound. The light-transmitting resin may contain a resin which cures by solvent evaporation, in addition to a polymer of a polymerizable compound. Examples of the polymerizable compound include radiation-polymerizable compounds and/or thermopolymerizable compounds. 
     The radiation-polymerizable compound refers to a compound having at least one radiation-polymerizable functional group in one molecule. The term “radiation-polymerizable functional group” as used herein refers to a functional group which can undergo radiation-induced polymerization. Examples of the radiation-polymerizable functional groups include ethylenic unsaturated groups such as (meth)acryloyl group, vinyl group, and allyl group. Both “acryloyl group” and “methacryloyl group” are meant by the word “(meth)acryloyl group.” In addition, the types of ionizing radiation applied to induce polymerization of a radiation-polymerizable compound include visible light, ultraviolet light, X ray, electron beam, α ray, β ray, and γ ray. 
     Examples of the radiation-polymerizable compound include radiation-polymerizable monomers, radiation-polymerizable oligomers, and radiation-polymerizable prepolymers; these compounds can be used as appropriate. A combination of a radiation-polymerizable monomer and a radiation-polymerizable oligomer or prepolymer is preferred as the radiation-polymerizable compound. 
     Examples of the radiation-polymerizable monomer include monomers containing a hydroxyl group(s), such as 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, and 2-ethylhexyl (meth)acrylate; and (meth)acrylate esters, such as ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate, triethylene glycol di(meth)acrylate, tetraethylene glycol di(meth)acrylate, tetramethylene glycol di(meth)acrylate, trimethylolpropane tri(meth)acrylate, trimethylolethane tri(meth)acrylate, pentaerythritol di(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol tetra(meth)acrylate, dipentaerythritol hexa(meth)acrylate, and glycerol (meth)acrylate. 
     A polyfunctional oligomer having two or more functional groups, for example a polyfunctional oligomer having three or more radiation-polymerizable functional group (i.e., trifunctional or higher), is preferred as the radiation-polymerizable oligomer. Examples of the above-described polyfunctional oligomer include polyester (meth)acrylate, urethane (meth)acrylate, polyester-urethane (meth)acrylate, polyether (meth)acrylate, polyol (meth)acrylate, melamine (meth)acrylate, isocyanurate (meth)acrylate, and epoxy (meth)acrylate. 
     The radiation-polymerizable prepolymer has a weight average molecular weight of more than 10,000, preferably a weight average molecular weight of 10,000 or more and 80,000 or less, and more preferably a weight average molecular weight of 10,000 or more and 40,000 or less. In cases where the weight average molecular weight is more than 80,000, the radiation-polymerizable prepolymer has a high viscosity and thus reduces the suitability as a coating material, which may deteriorate the appearance of the resulting light-transmitting resin. Examples of the polyfunctional prepolymer include urethane (meth)acrylate, isocyanurate (meth)acrylate, polyester-urethane (meth)acrylate, and epoxy (meth)acrylate. 
     The thermopolymerizable compound refers to a compound having at least one thermopolymerizable functional group in one molecule. The term “thermopolymerizable functional group” as used herein refers to a functional group which can undergo heat-induced polymerization with the same type of functional group or with other types of functional groups. Examples of the thermopolymerizable functional group include hydroxyl group, carboxyl group, isocyanate group, amino group, cyclic ether group, and mercapto group. 
     The thermopolymerizable compound is not limited to a particular thermopolymerizable compound, and examples of the thermopolymerizable compound include epoxy compounds, polyol compounds, isocyanate compounds, melamine compounds, urea compounds, and phenol compounds. 
     The resin which cures by solvent evaporation refers to a resin, such as a thermoplastic resin, which forms a coat film when a solvent added to the resin for adjusting the content of solids for coating process is evaporated. In the preparation of the light-transmitting functional layer  12 , addition of a resin which cures by solvent evaporation can effectively prevent failure in coating on a surface where a coating liquid is applied. The resin which cures by solvent evaporation is not limited to a particular resin, and a thermoplastic resin can generally be used as the resin which cures by solvent evaporation. 
     Examples of the thermoplastic resin can include styrene resins, (meth)acrylic resins, vinyl acetate resins, vinyl ether resins, halogen-containing resins, alicyclic olefin resins, polycarbonate resins, polyester resins, polyamide resins, cellulose derivatives, silicone resins, and rubber or elastomer materials. 
     The thermoplastic resin is preferably amorphous and soluble in an organic solvent (particularly, a solvent which can generally dissolve plural polymers or curable compounds). In particular, for example, styrene resins, (meth)acrylic resins, alicyclic olefin resins, polyester resins, and cellulose derivatives (such as cellulose esters) are preferred in terms of transparency and/or weather resistance. 
     &lt;Inorganic Particles&gt; 
     The inorganic particles are a component intended to increase the mechanical strength and pencil strength of the light-transmitting functional layer  12 , and examples of the inorganic particles include inorganic oxide particles, such as silica (SiO 2 ) particles, alumina particles, titania particles, tin oxide particles, antimony-doped tin oxide (abbreviation: ATO) particles, and zinc oxide particles. Among those particles, silica particles are preferred from the viewpoint of further increasing the hardness. Examples of the silica particles include spherical silica particles and differently shaped silica particles; among those silica particles, differently shaped silica particles are preferred. In this specification, the “spherical particle” refers to, for example, a spherical or ellipsoidal particle, while “deformed particle” refers to a particle with a randomly rough surface as observed on potato tubers. The surface area of the above-described deformed shaped particle is larger than that of a spherical particle, and the presence of such deformed particles thus increases the contact area with, for example, the above-described polymerizable compound and successfully improves the pencil hardness of the light-transmitting functional layer  12  to a higher level. Observation of a cross-section of the light-transmitting functional layer  12  with a transmission electron microscope (TEM) or a scanning transmission electron microscope (STEM) can confirm whether the silica particles contained in the light-transmitting functional layer  12  are deformed silica particles or not. In cases where spherical silica particles are used, spherical silica particles with smaller particle diameters lead to higher hardness in the light-transmitting functional layer. On the other hand, deformed silica particles can achieve a hardness equivalent to that of commercially available spherical silica particles with the smallest particle diameter even if those deformed silica particles are not as small as those spherical silica particles. 
     The average primary particle diameter of the deformed silica particles is preferably 1 nm or more and 100 nm or less. Even if deformed silica particles have an average primary particle diameter within the above-described range, the deformed silica particles can achieve a hardness equivalent to that of spherical silica particles with an average primary particle diameter of 1 nm or more and 45 nm or less. The average primary particle diameter of deformed silica particles is determined as the arithmetic mean of the particle diameters of 20 particles, wherein each particle diameter is obtained as the average between the maximum (major axis) and the minimum (minor axis) values of the distance between two points on the circumference of each particle measured on a cross-sectional image of a light-transmitting functional layer acquired using a transmission electron microscope (TEM) or a scanning transmission electron microscope (STEM). Additionally, the average particle diameter of spherical silica particles is determined as the arithmetic mean of the particle diameters of 20 particles, wherein the particle diameters of 20 particles are measured on cross-sectional images of particles acquired using a transmission electron microscope (TEM) or a scanning transmission electron microscope (STEM) at a magnification of 10,000 to 100,000 times. When cross-sections are imaged using a scanning transmission electron microscope (STEM) (product name “S-4800 (Type 2)”; manufactured by Hitachi High-Technologies Corporation), the cross-sections are observed by setting the detector switch (signal selection) to “TE,” the accelerating voltage to “30 kV,” and the emission current to “10 μA.” As other imaging conditions for acquiring images of cross-sections by STEM, the below-described conditions can be referenced. Additionally, the average primary particle diameter can be determined by binarizing and calculating the image data as described below. 
     The content of inorganic particles in the light-transmitting functional layer  12  is preferably 20% by mass or more and 70% by mass or less. In cases where the content of inorganic particles is less than 20% by mass, securing a sufficient hardness is challenging; additionally, in cases where the content of inorganic particles is more than 70% by mass, the filling ratio is increased excessively, which reduces the adhesion between the inorganic particles and the resin component and conversely results in reduced hardness of the light-transmitting functional layer. 
     As the inorganic particles, inorganic particles having photopolymerizable functional groups on the surface (reactive inorganic particles) are preferably used. Such inorganic particles having photopolymerizable functional groups on the surface can be produced by surface treatment of inorganic particles with, for example, a silane coupling agent. Examples of the method of treating the surface of inorganic particles with a silane coupling agent include a dry method in which the silane coupling agent is sprayed over the inorganic particles, and a wet method in which the inorganic particles are dispersed in a solvent and the silane coupling agent is then added to the solvent and allowed to react with the inorganic particles. 
     &lt;Organic Particles&gt; 
     The organic particles are also a component intended to increase the mechanical strength and pencil strength of the light-transmitting functional layer  12 , and examples of the organic particles include plastic beads. Specific examples of the plastic beads include polystyrene beads, melamine resin beads, acrylic beads, acrylic-styrene beads, silicone beads, benzoguanamine beads, benzoguanamine-formaldehyde condensation beads, polycarbonate beads, and polyethylene beads. 
     &lt;&lt;Electroconductive Part&gt;&gt; 
     The electroconductive part  13  comprises a light-transmitting resin  15  and plural electroconductive fibers  16  incorporated in the light-transmitting resin  15 , as shown in  FIG.  2   . The term “electroconductive part” as used herein refers to a layer containing electroconductive fibers, which are found by observing a cross-section of the electroconductive film with a scanning transmission electron microscope (STEM) or a transmission electron microscope (TEM). If the boundary surface of the electroconductive part is hard to be observed, the surface of the electroconductive part should undergo any pretreatment process commonly used for electron microscopy, such as formation of a metal layer of Pt—Pd, Au, or the like by sputtering. Additionally, the whole electroconductive film may be embedded in a resin and then stained with osmium tetraoxide, ruthenium tetraoxide, phosphotungstic acid, or the like because such staining enables easier observation of the interface between organic layers. Additionally, the term “electroconductive fiber” as used herein refers to a fiber having electrical conductivity and a length much longer than the thickness (for example, the diameter); for example, the electroconductive fiber will include a fiber having electrical conductivity and a length that is approximately equal to or more than five times as long as the thickness. Additionally, the term “electroconductive part” refers a part comprising a light-transmitting resin and plural electroconductive fibers incorporated in the light-transmitting resin and being capable of conducting electricity from the surface, and the concept includes both layered and non-layered structures. Additionally, as shown in  FIG.  3   , the light-transmitting resin  15  in the electroconductive part  13  may be communicated with the light-transmitting resin  15  in the nonconductive part  15 . The electroconductive part  13  preferably further comprises a reaction inhibitor which is contained in the light-transmitting resin  15 . 
     The electroconductive part  13  can conduct electricity from the surface  13 A of the electroconductive part  13 . Measurement of the surface resistance value of an electroconductive part can determine whether or not the electroconductive part can conduct electricity from the surface of the electroconductive part. The method of measuring the surface resistance value of an electroconductive part will be described hereinafter and the description of the method is omitted here. In cases where the arithmetic mean of the surface resistance values of an electroconductive part is less than 1×10 6 Ω/□, the electroconductive part can be determined to conduct electricity from the surface. Although a majority of the electroconductive fibers  16  are distributed from the position HL, which is located at half the film thickness of the electroconductive part  13 , to the light-transmitting base material  11 , as described below, the remaining electroconductive fibers  16  are stacked on the electroconductive fibers  16  which are distributed on the light-transmitting base material  11  side, and consequently distributed from the position HL, which is located at half the film thickness of the electroconductive part  13 , to the surface  13 A, and also exposed on the surface  13 A of the electroconductive part  13 . Thus, the electroconductive part  13  can conduct electricity from the surface  13 A. 
     In the electroconductive part  13 , the electroconductive fibers  16  are unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13  (the light-transmitting resin  15 ), as shown in  FIG.  2   . The determination of whether or not the electroconductive fibers  16  are unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13 , can be achieved as follows. First, samples for observing a cross-section are prepared from an electroconductive film. More specifically, a cut piece of electroconductive film having a size of 2 mm×5 mm is placed in an embedding plate made of silicone, into which an epoxy resin is later poured to embed the whole electroconductive film in the resin. Then, the embedding resin is left to stand at 65° C. for 12 hours or longer and cured. Subsequently, ultra-thin sections are prepared using an ultramicrotome (product name “Ultramicrotome EM UC7”; manufactured by Leica Microsystems GmbH) at a feeding rate of 100 nm. The prepared ultra-thin sections are collected on collodion-coated meshes (150 meshes) to obtain STEM samples. If these samples conduct no electricity, images observed by STEM will appear blurry. Thus, the samples are preferably sputtered with Pt—Pd for about 20 seconds. The sputtering time can be appropriately adjusted but needs careful attention; a period of 10 seconds is too short, and a period of 100 seconds is so long that the metal used for sputtering is observed as particulate foreign bodies. Then, a cross-sectional image of the electroconductive part in a STEM sample is photographed using a scanning transmission electron microscope (STEM) (product name “S-4800 (Type 2)”; manufactured by Hitachi High-Technologies Corporation). The cross-section is observed and imaged under STEM at a magnification of 5,000 to 200,000 times by setting the detector switch (signal selection) to “TE,” the accelerating voltage to “30 kV,” and the emission current to “10 μA,” and appropriately adjusting the focus, contrast, and brightness so that each layer can be identified. The magnification is preferably in the range from 10,000 to 100,000 times, more preferably in the range from 10,000 to 50,000 times, and most preferably in the range from 25,000 to 50,000 times. The cross-section may be imaged by additionally setting the beam monitor aperture to 3 and the objective lens aperture to 3, and also setting the WD to 8 mm. Then, the cross-sectional images at 10 locations photographed as described above are prepared. Upon completion of photographing the cross-sectional images of the electroconductive part, the position located at half the film thickness of the electroconductive part is determined on each cross-sectional image. Then, it is determined whether or not electroconductive fibers appearing on each cross-sectional image are distributed on the light-transmitting base material side than the half-length position. Specifically, first of all, electroconductive fibers in the above-described electron microscopic cross-sectional images of the electroconductive part are visualized as darker areas (for example, in black) compared to the light-transmitting resin, so that electroconductive fibers can be identified in the cross-sectional images of the electroconductive part. Meanwhile, by enlarging each cross-sectional image, pixels that make up the image become visible. All pixels are the same size and are arranged into a grid (lattice). The numbers of pixels covering the electroconductive fibers distributed on the the light-transmitting base material side than the above-described half-length position and covering the electroconductive fibers distributed on the surface side of the electroconductive part than the above-described half-length position are counted in each cross-sectional image to determine the ratio of the number of pixels covering the electroconductive fibers distributed on the the light-transmitting base material side than the above-described half-length position relative to the total number of pixels covering the electroconductive fibers. In this respect, for the pixels covering an electroconductive fiber, each pixel on the line running through the above-described half-length position will be divided into a portion located on the light-transmitting base material side than the above-described half-length position and the remaining portion located on the surface side of the electroconductive part than the above-described position, to divide one pixel based on the area ratio between the divided portions. Then, the above-described ratio determined from the cross-sectional images is determined as the existence ratio of electroconductive fibers distributed on the light-transmitting base material side than the position located at half the film thickness of the electroconductive part. In cases where the existence ratio is 55% or more, the electroconductive fibers are determined to be unevenly distributed on the light-transmitting base material side than the position located at half the film thickness of the electroconductive part. The existence ratio should be the arithmetic mean of the existence ratio values determined from the cross-sectional images. Incidentally, a low surface resistance value represents even distribution of electroconductive fibers in an electroconductive part. Therefore, the existence ratio of electroconductive fibers determined using cross-sectional images of a portion of the electroconductive part is considered as the existence ratio of electroconductive fibers in the whole electroconductive part. The existence ratio of electroconductive fibers distributed on the light-transmitting base material side than the position located at half the film thickness of the electroconductive part, which is determined from the above-described cross-sectional images, is preferably 70% or more, more preferably 80% or more. 
     The determination of whether or not the electroconductive fibers  16  are unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13 , can also be achieved as follows. First, a first sample of the electroconductive film in which a metal layer of Pt—Pd, Pt, Au, or the like has been formed by sputtering on the surface of the electroconductive part and a second sample of the same electroconductive film in which a metal layer is not formed on the surface are prepared. Then, the film thickness of the electroconductive part  13  is determined using the first sample by the below-described measurement method. Additionally, the second sample is used to photograph cross-sectional images of the electroconductive part by the above-described method, and the photographed cross-sectional image data is loaded to and binarized by image analysis and measurement software (product name “WinROOF Version 7.4”; manufactured by Mitani Corporation). In STEM observations, the difference in intensity of the transmitted electron beam produces image contrast. Metals having high density are hard to transmit a beam of electrons and thus are visualized in black, and organic materials, which have a lower density than metals, are visualized in white. Thus, the portions visualized in black are determined as electroconductive fibers and the remaining portions visualized in gray to white in the image data are determined as a light-transmitting resin. Accordingly, in cases where the ratio of a black-colored area in the area located on the light-transmitting base material side than the position located at half the film thickness of the electroconductive part is larger than the ratio of a black-colored area in the area located on the surface side of the electroconductive part than the above-described half-length position, the electroconductive fibers  16  can be determined to be unevenly distributed on the light-transmitting base material side than the position HL, which is located at half the film thickness of the electroconductive part  13 . The portions visualized in black can be extracted based on the luminance. Additionally, the difference in contrast between images of metals and organic materials is so clear that the area of each portion can be determined by an automated area measurement system alone. 
     The above-described binarization-mediated area measurement is performed as follows. First, a cross-sectional image is loaded to the above-described software and displayed on the image window of the software program. Then, either below or above the position located at half the film thickness in ROI (processing area) as subjects of image processing are selected in the image window and then binarized to calculate the total areas covered by electroconductive fibers. The selection of a processing area is carried out by clicking the rectangular ROI selection button in the image tool bar and setting a rectangular ROI in the image window. The above-described software outputs each measured value in pixel unit, which can be converted and outputted as a real length after calibration. When an area ratio is calculated, the measured value in pixel unit is not needed to be converted to a real length for the purpose of determining whether or not electroconductive fibers are unevenly distributed on the light-transmitting base material side, but calibration is required for measuring the surface resistance value and the haze value and for imaging the presence of fibers in the electroconductive film. Each STEM image displays a scale, which can be used to perform the ROI calibration. Specifically, the line ROI selection button in the image tool bar is clicked to draw a line having a length equal to the scale displayed in each STEM image, and the calibration dialog box is then displayed to choose the drawn line and to input the length value of the scale displayed in the STEM image and the unit for the length value. In binarization, the areas covering electroconductive fibers are separated from other areas. Specifically, binarization with two thresholds is selected from the menu of binarization. Because each electroconductive fiber has a high density and is visualized in black and the remaining region is visualized in white to gray, appropriately selected two density (brightness) thresholds (for example, 0 and 80) are inputted to perform binarization with two thresholds. If the area covered by electroconductive fibers in an actual STEM image does not exactly match with the area covered by the same electroconductive fibers (colored in, for example, green) in a binarized image produced by applying the thresholds to convert the image into two colors, the binarized image is corrected by appropriately changing the values of the thresholds until a binarized image most closely resembling the STEM image is obtained. For example, the difference between the STEM image and the binarized image can be appropriately corrected by the fill function and/or the delete function selected from the binarization menu. Any uncolored area inside or any excess colored area outside a binarized electroconductive fiber identified by the comparison with the same actual electroconductive fiber will be filled with a color or deleted. For the addition or deletion of a colored area, an area of interest can be filled with a color or be deleted by adjusting the threshold value for the area. Clicking an area to be deleted gives a threshold value suitable for deleting the area. The binarized image would be corrected as much as possible by other functions in the binarization menu as necessary, so that the resulting binarized image is matched with the STEM image. Additionally, an excess colored area in the binarized image can also be manually selected and deleted using the eraser tool button. In addition, an area can also be filled with a color for correction using the pen tool button through manual painting in the window. Upon completion of this task, one of the shape features in the analysis menu is selected to choose areas to be measured. The summed areas of electroconductive fibers can be determined, as well as the area of each of the electroconductive fibers is measured. By the above-described operation, the total areas below and above the position located at half the film thickness of the electroconductive layer are determined, and the areas of the ROIs located below and above the position at half the film thickness are further determined by manual measurement, and the above-described ratio is thereby calculated. The manual measurement can be performed by selecting the line length measurement function from the manual measurement functions in the analysis menu and choosing all the line length measurement items. Tools in the line length tool palette can be appropriately used to measure the length of a line and the area of a ROI selected by dragging the cursor from a start point to an end point with a mouse button. The details of the task will be according to the WinROOF Version 7.4 Users Manual. 
     The electroconductive part  13  has a surface resistance value of 200Ω/□ or less. In cases where the electroconductive part  13  has a surface resistance value of more than 200Ω/□, particularly problems such as slow response speed may occur in touch panel applications. The surface resistance value of the electroconductive part  13  is a surface resistance value measured on the surface  13 A of the electroconductive part  13 . The surface resistance can be measured using either a contact-type resistivity meter (product name “Loresta-AX MCP-T370”; Manufactured by Mitsubishi Chemical Analytech Co., Ltd., Type of sensor: ASP-probe) according to JIS K7194: 1994 (Testing method for resistivity of conductive plastics with a four-point probe array) or a non-destructive (based on the eddy current method) resistivity meter (product name “EC-80P”; manufactured by Napson Corporation; https://www.napson.co.jp/wp/wp-content/uploads/2016/08/Napson_EC80P_leaflet_160614.pdf), and preferably measured using a non-destructive resistivity meter, which can accurately measure the surface resistance independently of the film thickness of an electroconductive part. The non-destructive resistivity meter can start measurement at an arbitrary position on a sample by simple contact of a probe with the sample and without damaging the sample. From this point, it may be referred to as non-contact-type resistivity meter. The surface resistance value of an electroconductive part should be measured with a non-destructive resistivity meter by placing a cut piece of the electroconductive film having a size of 80 mm×50 mm on a flat glass plate with the electroconductive part facing upward and bring a probe into contact with the electroconductive part. For the measurement of surface resistance value with the EC-80P, the type SW2 is selected and the mode M-H sheet resistance (Ω/□) measurement is selected. Additionally, a probe can be easily switched with another type of probe depending on the range of measurement, and probes for the measurement ranges from 10 to 1000Ω/□ and from 0.5 to 10Ω/□ are used in the present embodiment. A resistivity meter EC-80P-PN (manufactured by Napson Corporation) can be used instead of a resistivity meter EC-80P to perform the measurement in the same manner, and P-type conduction may be selected from P-type and N-type conductions for the measurement using this instrument. Additionally, the surface resistance value of an electroconductive part should be measured with a contact-type resistivity meter by placing a cut piece of the electroconductive film having a size of 80 mm×50 mm on a flat glass plate with the electroconductive part facing upward and then placing an ASP-probe on the center of the electroconductive part and evenly pressing all the electrode pins on the electroconductive part. For the measurement of surface resistance value with the contact-type resistivity meter, the mode “Ω/□” as a sheet resistance measurement mode is selected. Once the start button is pushed and the instrument is held, the result of the measurement will be displayed. The measurement of surface resistance value should be performed in an environment at a temperature of 23° C. and a relative humidity of 55% independently of the type of a resistivity meter. Additionally, although an electroconductive film to be measured for surface resistance value is placed on a horizontal benchtop, independently of the type of a resistivity meter, to perform the measurement on a flat and even surface, a curled electroconductive film that is unable to keep the surface evenly flat should be fixed with tape or the like on a glass plate to perform the measurement. Three measurement locations are in the central part of the electroconductive film and the arithmetic mean of the surface resistance values at the three locations is determined as the surface resistance value. In this respect, the number of measurement location is 1, 5, or 9 in cases of totally following JIS K7194: 1994. However, once the electroconductive film is actually cut into a size of 80 mm×50 mm and measured as shown in  FIG.  5    in JIS K7194: 1994, the electroconductive film may give variable measurement values. Thus, the measurement should be performed on three locations in the central part of the electroconductive part, differing from JIS K7194: 1994. For example, the surface resistance value is measured at the position  1 , at a position located between the positions  1  and  7  (preferably, a position close to the position  1 ), and at a position located between the positions  1  and  9  (preferably, a position close to the position  1 ) shown in  FIG.  5    in JIS K7194: 1994. The preference of a position near the central a sample for the measurement of surface resistance value is also reported in Daichi Isaka and a coworker, “Resistivity measurements for conducting thin films by four-point probe method electroconductive,” The Tokyo branch Students&#39; Conference, the Institute of Electronics, Information, and Communication Engineers, 2009 (https://www.ieice.org/tokyo/gakusei/kenkyuu/14/pdf/120.pdf). The minimum surface resistance value of the electroconductive film  10  is 1Ω/□ or more, 5Ω/□ or more, or 10Ω/□ or more in ascending order of preference (a higher value is more preferred), while the maximum surface resistance value of the electroconductive film  10  is 100Ω/□ or less, 70Ω/□ or less, 60Ω/□ or less, or 50Ω/□ or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive part  13  preferably has a film thickness of less than 300 nm. In cases where the electroconductive part  13  has a film thickness of 300 nm or more, the film thickness of the light-transmitting resin  15  is accordingly too thick and all the electroconductive fibers are covered with the light-transmitting resin, so that it is likely that none of the electroconductive fibers are exposed on the surface of the electroconductive part and no electricity is conducted from the surface of the electroconductive part. The thicker the film thickness of the electroconductive part is, the more frequently the electroconductive fibers overlap with each other and a low surface resistance value of 1Ω/□ or more and 10Ω/□ or less can be achieved. However, excessive overlap of the electroconductive fibers may result in difficulty in maintenance of a low haze value. Thus, the film thickness is preferably 300 nm or less. The electroconductive part is preferably a thin film in terms of optical properties and from the viewpoint of thinning the electroconductive film, as long as it can maintain a low surface resistance value. The maximum film thickness of the electroconductive part  13  is 145 nm or less, 140 nm or less, 120 nm or less, 110 nm or less, 80 nm or less, or 50 nm or less in ascending order of preference (a lower value is more preferred) from the viewpoint of thinning the electroconductive film and obtaining excellent optical properties such as a low haze value. Additionally, the minimum film thickness of the electroconductive part  13  is preferably 10 nm or more. In cases where the electroconductive part has a film thickness of less than 10 nm, the film thickness of the light-transmitting resin  15  is accordingly too thin, so that it is likely that some electroconductive fibers are removed from the electroconductive part, or the durability of the electroconductive part is reduced, or the abrasion resistance is reduced. Additionally, each electroconductive fiber preferably has a relatively large fiber diameter to control the instabilities, such as higher tendency for breakage. The fiber diameter that allows each electroconductive fiber to keep stably its form is considered to be 10 nm or more or 15 nm or more. On the other hand, the minimum film thickness of the electroconductive part  13  is more preferably 20 nm or more or 30 nm or more because two or more electroconductive fibers are desired to overlap with and contact with each other to obtain stable electrical conductivity. 
     The film thickness of the electroconductive part  13  is determined as the arithmetic mean of the thickness values measured at randomly selected 10 locations, wherein the thickness values are determined at the 10 locations in cross-sectional images of the electroconductive part photographed using a scanning transmission electron microscope (STEM) or a transmission electron microscope (TEM). A specific method of photographing cross-sectional images will be described below. First, samples for observing a cross-section are prepared from an electroconductive film by the same method as described above. If these samples conduct no electricity, images observed by STEM will appear blurry. Thus, the samples are preferably sputtered with Pt—Pd for about 20 seconds. The sputtering time can be appropriately adjusted but needs careful attention; a period of 10 seconds is too short, and a period of 100 seconds is so long that the metal used for sputtering is observed as particulate foreign bodies. Then, a cross-sectional image of a STEM sample is photographed using a scanning transmission electron microscope (STEM) (product name “S-4800 (Type 2)”; manufactured by Hitachi High-Technologies Corporation). The cross-section is observed and imaged under STEM by setting the detector switch (signal selection) to “TE,” the accelerating voltage to “30 kV,” and the emission current to “10 μA.” The focus, contrast, and brightness are appropriately adjusted at a magnification of 5,000 to 200,000 times so that each layer can be identified. The magnification is preferably in the range from 10,000 to 100,000 times, more preferably in the range from 10,000 to 50,000 times, and most preferably in the range from 25,000 to 50,000 times. The cross-section may be imaged by additionally setting the beam monitor aperture to 3 and the objective lens aperture to 3, and also setting the WD to 8 mm. For the measurement of the film thickness of the electroconductive part, it is important that the contrast at the interface between the electroconductive part and another layer (such as the light-transmitting functional layer or the embedding resin) can be observed as clearly as possible upon observation of a cross-section. If the interface is hard to be observed due to a lack of contrast, the surface of the electroconductive part may undergo any pretreatment process commonly used for electron microscopy, such as formation of a metal layer of Pt—Pd, Pt, Au, or the like by sputtering. In addition, the sample may be stained with osmium tetraoxide, ruthenium tetraoxide, phosphotungstic acid, or the like because such staining enables easier observation of the interface between organic layers. Additionally, the contrast of the interface may be hard to be observed at a higher magnification. In that case, the sample is also observed at a lower magnification at the same time. For example, a pair of magnifications consisting of a higher magnification and a lower magnification, such as 25,000 and 50,000 times or 50,000 and 100,000 times, is used for observation to obtain the above-described arithmetic means at both the magnifications, and the further averaged value is determined as the film thickness of the electroconductive part. 
     As described below, the electroconductive part  13  is prepared by applying, drying, and curing a light-transmitting resin composition containing a polymerizable compound to form the light-transmitting resin  16  on a cured coating film of an electroconductive fiber-containing composition containing the electroconductive fibers  16 ; in cases, for example, where an electroconductive part is prepared only by applying and drying an electroconductive fiber-containing composition containing electroconductive fibers, the film thickness of the electroconductive part can be simply obtained from the amount of the applied electroconductive fiber-containing composition by using the following theoretical formula (see, for example, https://www.nipponpaint.co.jp/biz1/large/pdf/tech04.pdf): 
     
       
         
           
             T 
             = 
             
               
                 X 
                 
                   d 
                   ⁢ 
                   p 
                 
               
               - 
               
                 
                   X 
                   ⁡ 
                   
                     ( 
                     
                       1 
                       - 
                       
                         N 
                         ⁢ 
                         V 
                       
                     
                     ) 
                   
                 
                 
                   d 
                   ⁢ 
                   s 
                 
               
             
           
         
       
     
     In the above-described formula, T represents the dry film thickness (μm) of an electroconductive part; X represents the theoretical amount (g/m 2 ) of an applied electroconductive fiber-containing composition to obtain a dry film thickness of T (μm); dp represents the specific gravity of the electroconductive fiber-containing composition; ds represents the specific gravity of the volatile component in the electroconductive fiber-containing composition; and NV represents the ratio of the non-volatile component in the electroconductive fiber-containing composition (a ratio by weight). 
     The electroconductive part  13  preferably contains no particles, such as inorganic particles, having a particle size larger than the film thickness of the light-transmitting resin  15 . If the electroconductive part contains such particles, some of the particles are protruded from the surface of the light-transmitting resin and cause to increase the film thickness of the electroconductive part. In this respect, if a particle is protruded from the surface of the light-transmitting resin, the film thickness of the electroconductive part is determined as the distance from the surface of the electroconductive part on the side of the light-transmitting base material to the top of the particle. Additionally, the electroconductive part  13  more preferably contains no particles, such as inorganic particles, regardless of the size of the particles. However, for example, metallic core particle residues obtained during an intermediate process to prepare electroconductive fibers  16  or any modifying materials for the electroconductive fibers are considered as an integral part of the electroconductive fibers and, thus, should not be included in the above-described particles. 
     The electroconductive part  13  preferably has a Martens hardness of 970 N/mm 2  or more and 1050 N/mm 2  or less at an indentation amount of 10 nm from the surface  13 A. Additionally, the electroconductive part  13  preferably has a Martens hardness of 130 N/mm 2  or more and 300 N/mm 2  or less at an indentation amount of 100 nm from the surface  13 A. In general, the indentation amount is preferably within 10% of the film thickness of a measurement subject for the measurement with a microhardness tester. That is, the Martens hardness at a position of 10 nm in the present embodiment means the exact hardness of the electroconductive part, wherein the value of the hardness is hardly influenced by the layer beneath the electroconductive part. Additionally, the Martens hardness at a position of 100 nm means the hardness of the electroconductive part required in a film product since the electroconductive part is typically not provided alone but provided as a film comprising the electroconductive part and various layers, such as a base material, laminated on the lower side, depending on the type of a product. The resulting electroconductive film will be hardly broken or cracked, as long as the electroconductive part satisfies the above-described Martens hardness requirement even if any layer is deposited below the electroconductive part. 
     In cases where the Martens hardness of the electroconductive part  13  at the above-described indentation amount of 10 nm is less than 970 N/mm 2 , the electroconductive part may be easily damaged during the production process for an electroconductive film; additionally in cases where the above-described Martens hardness is more than 1050 N/mm 2 , etching rate for forming a pattern on the electroconductive part may be slowed down or the electroconductive film may be cracked when folded. In the electroconductive part  13 , the minimum Martens hardness at the above-described indentation amount of 10 nm is 980 N/mm 2  or more, 1000 N/mm 2  or more, or 1015 N/mm 2  or more in ascending order of preference (a higher value is more preferred); the maximum Martens hardness at the above-described indentation amount of 10 nm is 1040 N/mm 2  or less, 1030 N/mm 2  or less, or 1020 N/mm 2  or less in ascending order of preference (a lower value is more preferred). Additionally, in cases where the Martens hardness at the above-described indentation amount of 100 nm is less than 130 N/mm 2 , the electroconductive film may be easily fractured; additionally, in cases where the Martens hardness is more than 150 N/mm 2 , the electroconductive film may be broken when folded. In the electroconductive part  13 , the minimum Martens hardness at the above-described indentation amount of 100 nm is 140 N/mm 2  or more, 150 N/mm 2  or more, or 170 N/mm 2  or more in ascending order of preference (a higher value is more preferred); the maximum Martens hardness at the above-described indentation amount of 100 nm is 280 N/mm 2  or less, 250 N/mm 2  or less, or 200 N/mm 2  or less in ascending order of preference (a lower value is more preferred). 
     In the present invention, at least one of the Martens hardness requirements at the above-described indentations amount of 10 nm or 100 nm is preferably satisfied. By satisfying both the Martens hardness requirements, physical properties which are so suitable as to prevent any breakage, crack, or the like are achieved, as described above. Additionally, it is important that the Martens hardness is not excessively low or excessively high. For example, at least a certain level of hardness is required to avoid the electroconductive part easily damaged during the production process for an electroconductive film. In addition, the electroconductive part is etched for pattern geometry. The etching process includes dry etching processes, such as laser dry etching, and wet etching processes, such as a process comprising immersion in an etching liquid and based on a broadly used photolithography technique. In either etching process, an excessively high hardness of the electroconductive part results in a problem of a slow etching rate, which in turn requires a longer period for processing. Thus, the upper limit of the above-described Martens hardness should be specified. 
     The Martens hardness at an indentation amount of 10 nm or 100 nm from the surface of the electroconductive part will be measured by the following method. First, a cut piece of an electroconductive film having a size of 20 mm×20 mm is fixed with an adhesive resin (product name “Aron Alpha® General type”; manufactured by Toagosei Co., Ltd.) on a commercially available slide glass with the electroconductive part facing upward. Specifically, a drop of the above-described adhesive resin is placed at the center of a slide glass  1  (product name “Slide glass (Strainer), 1-9645-11”; manufactured by AS One Corporation). In this step, the adhesive resin is not spread over the slide glass, and a drop of the adhesive resin is applied so that the adhesive resin does not extend beyond the electroconductive film when pressed as described below. Subsequently, the slide glass is contacted with the cut piece of the electroconductive film having the above-described size with the electroconductive part facing upward and with the center of the electroconductive film located on the adhesive resin, and the adhesive resin is spread between the slide glass  1  and the electroconductive film for temporary adhesion. Then, another new slide glass  2  is placed on the electroconductive film to obtain a laminate composed of the slide glass  1 , the adhesive resin, the electroconductive film, and the slide glass  2 . Subsequently, a weight of 30 g to 50 g is left to stand on the slide glass  2  for 12 hours at room temperature. Then, the weight and the slide glass  2  are removed from the laminate to prepare a measurement sample. The four corners electroconductive film fixed with the adhesive resin may further be fixed with tape (product name “Cello Tape®”; manufactured by Nichiban Co., Ltd.). The measurement sample is fixed on the measurement stage of a microhardness tester (product name “PICODENTOR HM500”, manufactured by Fischer Instruments K.K.; following 15014577-1 and ASTM E2546) placed horizontally on a vibration isolation table. Any method, such as putting tape (product name “Cello Tape®”; manufactured by Nichiban Co., Ltd.) on the four edges, is available to fix the slide glass  1 , as long as the measurement sample does not move. Additionally, in cases where the microhardness tester is equipped with an air suction system, the measurement sample may be fixed with the air suction system. After the measurement sample is fixed on the measurement stage of the microhardness tester, the Martens hardness is measured under the following measurement conditions at indentation amounts of 10 nm and 100 nm on the surface of the electroconductive part. The Martens hardness is measured at five arbitrary locations near the center on the surface of the electroconductive part in the measurement sample to determine the arithmetic mean of the obtained five hardness values as the Martens hardness. However, the measured five arbitrary locations should be selected on the area having a surface as flat as possible in the electroconductive part by observing the electroconductive part at a magnification of 50 to 500 times using a microscope accessory to the PICODENTOR HM500, avoiding areas with extreme projections due to overlapped electroconductive fibers and, on the contrary, areas with extreme depressions. Even in a patterned electroconductive part of an electroconductive film, five arbitrary measurement locations are selected in the same manner as described above. Additionally, when the Martens hardness is calculated, “HM” (Martens hardness) is selected as a type of hardness to be measured on the PICODENTOR HM500 to start automatic calculation. 
     (Measurement Conditions) 
     
         
         
           
             Type of an indenter: Vickers (quadrangular pyramid diamond indenter, having an apex part with an angle of 136 degrees between opposite faces); 
             Load control mode: up to 40 mN; 
             Loading time: 20 seconds; 
             Creep time: 5 seconds; 
             Unloading time: 20 seconds; 
             Indentation: 10 nm (for measuring the Martens hardness at an indentation amount of 10 nm) and 100 nm (for measuring the Martens hardness at an indentation amount of 100 nm); 
             Measurement temperature: 25° C.; 
             Measurement humidity: 50%. 
           
         
       
    
     In the measurement profile, the applied load will increase from 0 mN to 40 mN over 20 seconds, keep at 40 mN for 5 seconds, and then decrease from 40 mN to 0 mN over 20 seconds. 
     In cases where the electroconductive film  10  is used as an electrode for a touch panel sensor, the ratio of the electrical resistance value in a second direction to that in a first direction (the ratio is hereinafter referred to as “electrical resistance value ratio”) is preferably 1 or more and less than 2 when the electrical resistance values on the surface  13 A of the electroconductive part  13  are measured in a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees in the surface of the electroconductive part, wherein a direction in which the electroconductive part shows the lowest electrical resistance value is designated as the first direction, and a direction which is orthogonal to the first direction is designated as the second direction. The electrical resistance value ratio can be obtained, for example, as follows. First, as shown in  FIG.  2   , an arbitrary direction AD is determined in the surface of the electroconductive part  13  and samples S having a predetermined size (for example, in a rectangular shape having a size of 110 mm length×5 mm width; a sample S excluding the below-described silver paste  17  has a size of 100 mm length×5 mm width) and extending in six different directions including the arbitrary direction AD, which are each an angle of 30 degrees to the arbitrary direction AD, are cut from the electroconductive film  10 . In consideration of providing a silver paste, each sample S is cut with a margin of about 10 mm in the length direction. After the samples S are cut from the electroconductive film  10 , a silver paste (product name “DW-520H-14”; manufactured by Toyobo Co., Ltd.) is applied, as shown in  FIG.  3   , on both longitudinal ends of each sample S (for example, each end having a size of 5 mm length×5 mm width) to prevent any change in distance between points for measuring the electrical resistance value and in a manner that enables a post-curing film thickness of 5 μm or more and 10 μm or less, and heated at 130° C. for 30 minutes to obtain the sample S retaining the cured silver pastes  17  on both the terminal regions. The distance between the points where the silver paste  17  has been applied (the length of the portion carrying no silver paste  17 ) is the distance between points for measuring the electrical resistance in each sample S (for example, 100 mm), which should be constant among the samples S. Although a recommendable aspect ratio of the sample S without the silver paste  17  is 20:1, a sample having a size of 60 mm length×5 mm width (the sample without the silver paste  17  has a size of 50 mm length×5 mm width) may be used in cases where only a small sample can be prepared, because the recommendable aspect ratio of a sample without the silver paste  17  can be reduced to 10:1. Additionally, although the samples S in the present embodiment are withdrawn in six different directions for each an angle of 30 degrees to the arbitrary direction AD, samples may be cut from any portions in the electroconductive film as long as a long side of each sample extends at an angle differently from any line parallel to the arbitrary direction AD. Then, the electrical resistance value of each sample S retaining the cured silver pastes  17  on both the terminal regions is measured using a tester (product name “Digital MΩ Hitester 3454-11”; manufactured by Hioki E.E. Corporation). Specifically, first of all, since the Digital MΩ Hitester 3454-11 comprises a black probe terminal and a red probe terminal (both are pin-type terminals), the black probe terminal is connected to the EARTH terminal and the red probe terminal is connected to the LINE terminal. After selecting the function selector to “Ω,” the MEASURE LOCK/STOP key is pressed for 2 seconds. This allows the measurement of electrical resistance value to start automatically every time the probe terminals are connected to a sample. Under this condition, the red probe terminal is contacted with the cured silver paste  17  provided on one of the ends and the black probe terminal is contacted with the cured silver paste  17  provided on the other end to measure the electrical resistance value. The measurement of electrical resistance should be performed in an environment at a temperature of 23° C. and a relative humidity of 55%. The electrical resistance value is preferably measured in a sample provided with an amount of a silver paste enough to achieve a post-curing film thickness of 10 μm because poor coating of a silver paste may cause unstable results in electrical resistance value measurement and also display abnormal values clearly different from expected resistance values. Then, a sample S showing the lowest electrical resistance value is identified among the samples S cut from the electroconductive film  10 . The direction of cutting the sample S showing the lowest electrical resistance value from the electroconductive film is designated as a first direction, and a sample S cut in a second direction orthogonal to the first direction is identified, and the ratio of the electrical resistance of the sample S in the second direction to that of the sample S in the first direction is calculated. The arithmetic mean of three measurements is determined as the electrical resistance value ratio. The maximum electrical resistance value ratio is 1.8 or less, 1.5 or less, or 1.3 or less in ascending order of preference (a lower value is more preferred). By limiting the maximum electrical resistance value ratio to be within the above-described range, a uniform resistance value can be obtained over the surface. Products manufactured using an electroconductive film (for example, smartphone) use a small area of the electroconductive film. However, any deviation of electrical resistance in the surface of the electroconductive film in one article may cause problems to occur in actions as an image display screen or a touch panel. Thus, the limited maximum electrical resistance value ratio can prevent such problems. 
     In cases where an electroconductive part is patterned to form several electric wirings as in the cases of the below-described electroconductive parts  22  and  31 , the electrical resistance value ratio can be obtained, for example, as follows. First, six arbitrary areas are selected as measurement areas on the surface of the electroconductive film. The six measurement areas should have the same size (the same length) and be separated from one another. Additionally, the above-described six measurement areas are determined such that, for example, three areas are located on the first edge positioned in the extending direction of each electric wiring in the electroconductive film and three areas are located on the second edge positioned in the extending direction of each electric wiring and opposite to the first edge. Specifically, the above-described measurement areas are provided such that two out of the three areas on the first edge and two out of the three areas on the second edge are located in close proximity to the four corners of the electroconductive film, and the remaining one out of the three areas on the first edge and the remaining one out of the three areas on the second edge are respectively located at the middle of the first and second edges. Then, a silver paste (product name “DW-520H-14”; manufactured by Toyobo Co., Ltd.) is applied on the outside of both ends of each area located in the above-described extending direction of each electric wiring in a manner that enables a post-curing film thickness of 5 μm or more and 10 μm or less and prevents any contact with an adjacent electric wiring, and heated at 130° C. for 30 minutes to cure the silver paste. The distance between the cured silver pastes located on the outside of both ends of each area (measurement length) should be identical among the areas, while the width of the silver pastes on both ends should be in total within 10 mm. Then, the cured silver pastes located on the outside of both ends of each area are contacted with probe terminals of a tester (product name “Digital MΩ Hitester 3454-11”; manufactured by Hioki E.E. Corporation) to measure the line resistance value. For example, in cases where the Digital MΩ Hitester 3454-11 is used as a tester, the Digital MΩ Hitester 3454-11 comprises two probe terminals (a red probe terminal and a black probe terminal; both are pin-type terminals) and, therefore, the red probe terminal is contacted with the silver paste located on the outside of one end of a measurement area and the black probe terminal is contacted with the cured silver paste located on the outside of the other end of the measurement area to measure the line resistance value. Then, among those line resistant values of the six measurement areas, the highest line resistance value will be divided by the lowest line resistance value to obtain the electrical resistance value ratio. Although line widths of an electroconductive part in, for example, 5-inch smartphones are very narrows, silver pastes provided on an electroconductive part (electric wirings) enable measurement of line resistance value in the electroconductive part even if the line widths are very narrow. 
     For the measurement of the above-described line resistance value, the line width is in the order of micrometers at the narrowest portion in small-sized products such as 5-inch smartphones. In that case, each measurement area will be selected to have a measurement length as long as possible independently of the aspect ratio. In cases where an electroconductive film is in a shape of long rectangle, a measurement area is preferably selected to have a measurement length equal to about half the length of the long side of the electroconductive film. On the other hand, in cases of products having a size of 20 inches or more, the line width is in the order of millimeters and a measurement area is preferably selected to have an aspect ratio of 1:20. 
     In cases where the electrical resistance value or surface resistance value of a manufactured product is measured, the following pretreatment should be appropriately performed. The pretreatment method is not limited to the following method as long as the pretreated product becomes available for the measurement, and it is critical to avoid any influence on electroconductive fibers. That is, in cases where an electroconductive part is already clearly visible and the thickness of an adhesive layer can be presumed to be very thin, measurement can be performed without any further treatment and there is no need to peel off the electroconductive part entirely by force. However, the manufactured product is preferably pretreated to reduce the thickness as thin as possible. For example, in cases where an electroconductive film is used as a touch panel sensor, a cover film or glass is layered on the electroconductive film through an adhesive layer. Thus, a cutter blade is first inserted into the adhesive layer from the edge to remove the cover film or glass. When the cover film or glass is not easily removed, the electroconductive film proceeds to the next step without removing the cover film or glass by force. Next, the electroconductive film is immersed in and withdrawn from warm water at 40° C. for 10 seconds three times. Then, detachment of the adhesive layer is checked with a cutter or the like, and in some cases the electroconductive film is immersed in and withdrawn from warm water at 40° C. for 10 seconds further three times. Subsequently, the adhesive layer is slowly peeled off with a tool which will never damage the electroconductive part (a thin and flat tool without a blade). The adhesive layer need not be removed entirely as long as the adhesive layer at measurement locations is removed. The present pretreatment can also be used for measuring anything other than electrical resistance value and surface resistance value. 
     On the other hand, in cases of obtaining an electroconductive film which provides a much lower electrical resistance value in a particular direction, the above-described electrical resistance value ratio is preferably 2 or more when the electrical resistance value on the surface  31 A of the electroconductive part  31  is measured in a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface  31 A of electroconductive part  31 . The arithmetic mean of three measurements is determined as the electrical resistance value ratio. The minimum electrical resistance value ratio is more preferably 3 or more. The maximum electrical resistance value ratio is 10 or less, or 8 or less in ascending order of preference (a lower value is more preferred) from the viewpoint of obtaining a uniform resistance value on the surface. 
     Such an electroconductive part having an electrical resistance value ratio of 1 or more and less than 2 or an electrical resistance value ratio of 2 or more can be obtained, for example, by appropriately modifying the fiber length of electroconductive fibers, the type or film thickness of a resin that constitutes the below-described organic protective layer, and/or the temperature for drying the electroconductive fiber-containing composition. 
     &lt;Light-Transmitting Resin&gt; 
     The light-transmitting resin  15  covers electroconductive fibers  16  to prevent removal of the electroconductive fibers  16  from the electroconductive part  13  and to improve the durability or scratch resistance of the electroconductive part  13 , and covers electroconductive fibers  16  to such an extent that the electroconductive part  13  can conduct electricity from the surface  13 A. Specifically, the light-transmitting resin  15  preferably covers electroconductive fibers  16  in a manner that will leave some of the electroconductive fibers  16  exposed on the surface  13 A of the electroconductive part  13 , because it is likely that the electroconductive part can conduct no electricity from the surface, as described above, when some electroconductive fibers are not exposed on the surface of the electroconductive part. For example, the film thickness of the light-transmitting resin  15  should be adjusted to cover electroconductive fibers  16  with the light-transmitting resin  15  in a manner that will leave some of the electroconductive fibers  16  exposed on the surface  13 A of the electroconductive part  13 . 
     The light-transmitting resin  15  preferably has a film thickness of less than 300 nm from the viewpoint of thinning the electroconductive film. The film thickness of the light-transmitting resin  15  can be measured by the same measurement method as for the film thickness of the electroconductive part  13 . The maximum film thickness of the light-transmitting resin  15  is 145 nm or less, 140 nm or less, 120 nm nm, 110 nm or less, 80 nm or less, or 50 nm or less in ascending order of preference (a lower value is more preferred). Additionally, the minimum film thickness of the light-transmitting resin  15  is preferably 10 nm or more. 
     The light-transmitting resin  15  is not limited to a particular light-transmitting resin as long as it is a light-transmissive resin, and examples of the light-transmitting resin include polymers of polymerizable compounds and thermoplastic resins. Polymerizable compounds similar to those described for the light-transmitting functional layer  12  are included as examples of the polymerizable compound, and further description is thus omitted here. 
     &lt;Reaction Inhibitor&gt; 
     A reaction inhibitor is a substance that prevents reduction in electrical conductivity after application of the light-transmitting resin composition due to the reaction of the electroconductive fibers  16  with substances in the atmosphere. Examples of the reaction inhibitor include nitrogen-containing compounds, such as benzoazole compounds, triazole compounds, tetrazole compounds, isocyanurate compounds, and aniline compounds. Examples of the nitrogen-containing compound used as a reaction inhibitor include 1-amino-benzoazole, 5-methylbenzotriazole, 1,2,3-benzotriazole, 1-methyl-1H-tetrazole-5-amine, DL-α-tocopherol, 1-octadecanethiol, 2-mercapto-5-(trifluoromethyl)pyridine, diallyl isocyanurate, diallyl propyl isocyanurate, 6-anilino-1,3,5-triazine-2,4-dithiol, thiocyanuric acid, 3,5-dimethyl-1H-1,2,4-triazole, 4-(1,2,4-triazol-1-ylmethyl)aniline, 6-(dibutylamino)-1,3,5-triazine-2,4-dithiol, 4-(1,2,4-triazol-1-yl)aniline, 2-methylthio-benzothiazole, 1-phenyl-5-mercapto-1H-tetrazole, 5-mercapto-1-methyltetrazole, 5-(methylthio)-1H-tetrazole, 5-amino-1H-tetrazole, 1-(2-dimethylaminoethyl)-5-mercaptotetrazole, 1-(2-dimethylaminoethyl)-5-mercaptotetrazole, 1-(4-hydroxyphenyl)-5-mercapto-1H-tetrazole, 3-amino-5-mercapto-1,2,4-triazole, and 3,5-diamino-1,2,4-triazole. 
     The content of a reaction inhibitor in the electroconductive part  13  is preferably 0.01% by mass or more and 10% by mass or less. In cases where the content of the reaction inhibitor is less than 0.01% by mass, the electroconductive fibers may react with substances in the atmosphere, which in turn results in reduced electrical conductivity. Additionally, although the reaction inhibitor reacts with the surface of electroconductive fibers and thus inactivates the surface of electroconductive fibers, and renders the resulting electroconductive fibers less prone to react with substances in the atmosphere, the reaction inhibitor may react not only with the surface of electroconductive fibers but also with the inside of the electroconductive fibers, which in turn results in reduced electrical conductivity in cases where the content of the reaction inhibitor is more than 10% by mass. 
     &lt;Electroconductive Fibers&gt; 
     Although the electroconductive fibers  16  are unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13 , the electroconductive fibers  16  contact with each other in the thickness direction of the electroconductive part  13 , as indicated by the ability of the electroconductive part  13  to conduct electricity from the surface  13 A. 
     The electroconductive fibers  16  preferably contact with each other to form a network structure (meshwork) to the surface direction (two-dimensional direction) of the electroconductive part  13  in the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13 . Formation of a network structure by the electroconductive fibers  16  enables efficient creation of a conductive path with the electroconductive fibers  16  even in a small amount. 
     Some of the electroconductive fibers  16  are preferably exposed on the surface  13 A of the electroconductive part  13 . The phrase “some of the electroconductive fibers are exposed on the surface of the electroconductive part” as used herein should refer to exposure of some electroconductive fibers on the surface of the electroconductive part in such an extent that the electroconductive fibers are anchored to the electroconductive part, including electroconductive fibers protruded from the surface of the electroconductive part. In cases where some electroconductive fibers are not exposed on the surface of the electroconductive part, the electroconductive part may conduct no electricity from the surface. Once electrical conduction from the surface  13 A of the electroconductive part  13  is identified by the above-described measurement method, some of the electroconductive fibers  16  can thus be determined to be exposed on the surface  13 A of the electroconductive part  13 . 
     The electroconductive fibers  16  preferably have a fiber diameter of 200 nm or less. In cases where the electroconductive fibers have a fiber diameter of more than 200 nm, the resulting electroconductive film may have a higher haze value or a poor light transmittance. The minimum fiber diameter of the electroconductive fibers  16  is more preferably 10 nm or more from the viewpoint of the electrical conductivity of the electroconductive part  13 , and a more preferred range of fiber diameter in the electroconductive fibers  16  is 15 nm or more and 50 nm or less. The electroconductive fibers  16  most preferably have a fiber diameter of 30 nm or less. 
     The fiber diameter of the electroconductive fibers  16  will be obtained as the arithmetic mean of the fiber diameters of 100 electroconductive fibers in 50 images photographed at a magnification of 100,000 to 200,000 times, for example, using a transmission electron microscope (TEM) (product name “H-7650”; manufactured by Hitachi High-Technologies Corporation), which are measured on the photographed images by a software program accessory to the TEM. The fiber diameters are measured using the above-described H-7650 by setting the accelerating voltage to “100 kV,” the emission current to “10 μA,” the condenser lens aperture to “1,” the objective lens aperture to “0,” the observation mode to “HC,” and the Spot to “2.” Additionally, the fiber diameters of the electroconductive fibers can also be measured by a scanning transmission electron microscope (STEM) (product name “S-4800 (Type 2)”; manufactured by Hitachi High-Technologies Corporation). In that case, the fiber diameter of the electroconductive fibers will be obtained as the arithmetic mean of the fiber diameters of 100 electroconductive fibers in 50 images photographed at a magnification of 100,000 to 200,000 times using the STEM, which are measured on the acquired images by a software program accessory to the STEM. The fiber diameters are measured using the above-described S-4800 (Type 2) by setting the signal selection to “TE,” the accelerating voltage to “30 kV,” the emission current to “10 μA,” the probe current to “Norm,” the focus mode to “UHR,” the condenser lens  1  to “5.0,” the WD to “8 mm,” and the Tilt to “0°.” 
     When the fiber diameter of the electroconductive fibers  16  is determined, a measurement sample prepared by the following method is used. In this respect, TEM measurement is performed at high magnifications and it is consequently critical to reduce the concentration of the electroconductive fiber-containing composition as much as possible for the purpose of inhibiting overlap of the electroconductive fibers as much as possible. Specifically, the electroconductive fiber-containing composition is preferably diluted with water or alcohol depending on the dispersion medium used in the composition to reduce the concentration of electroconductive fibers to 0.05% by mass or less or to reduce the content of solids to 0.2% by mass or less. Furthermore, a drop of the diluted electroconductive fiber-containing composition is applied on a grid mesh with a carbon supporting film for TEM or STEM observation, dried at room temperature, and then observed under the above-described conditions, and the resulting observation image data is used to calculate the arithmetic mean. As the grid mesh with a carbon supporting film, a Cu grid with the model “#10-1012, Elastic Carbon Film ELS-C10 in the STEM Cu100P grid specification” is preferred, and any grid having better resistance against electron beam exposure and a higher electron beam transmittance than a plastic supporting film, and thus being suitable for observation at a high magnification, and having better resistance against organic solvents is also preferred. Additionally, a drop of the diluted electroconductive fiber-containing composition could be applied on a grid mesh placed on a slide glass because the grid mesh is so small that it is difficult to apply the drop of the diluted electroconductive fiber-containing composition on a plain grid mesh. 
     The above-described fiber diameter can be obtained by image-based measurement or may be calculated from the binarized image data. In the case of actual measurement, images may be printed or enlarged as appropriate. In that case, each electroconductive fiber is visualized in darker black than other components. Measurement points are selected on the outer counter of each fiber as a starting point and an end point. The concentration of electroconductive fibers will be obtained based on the ratio of the mass of the electroconductive fibers to the total mass of the electroconductive fiber-containing composition, while the content of solids will be obtained based on the ratio of the mass of all components except for the dispersion medium (including the electroconductive fibers, the resin component, and other additives) to the total mass of the electroconductive fiber-containing composition. 
     The electroconductive fibers  16  preferably have a fiber length of 1 μm or more. In cases where the electroconductive fibers  16  have a fiber length of less than 1 μm, an electroconductive layer having a sufficient electrical conductivity may not be formed and aggregation may occur, which may in turn result in a higher haze value and a low light transmittance. The maximum fiber length of the electroconductive fibers  16  may be 500 μm or less, 300 μm or less, or 30 μm or less, while the minimum fiber length of the electroconductive fibers  16  may be 3 μm or more, or 10 μm or more. 
     In cases where the electroconductive fibers  16  have a fiber length of 30 μm or more, electroconductive fibers are easily aligned along the below-described MD direction, which causes a tendency to increase the difference in electrical resistance value depending on the direction on a surface. Thus, the electroconductive fibers  16  preferably have a fiber length of, for example, 1 μm or more and less than 30 μm in cases of obtaining an electroconductive part having an electrical resistance value ratio of 1 or more and less than 2, while the electroconductive fibers  16  preferably have a fiber length of, for example, 30 μm or more in cases of obtaining an electroconductive part having an electrical resistance value ratio of 2 or more. In cases of obtaining an electroconductive part having an electrical resistance value ratio of 1 or more and less than 2, the electroconductive fibers  16  preferably have a minimum fiber length of 10 μm or more and a maximum fiber length of 20 μm or less from the viewpoint of obtaining a low surface resistance value. 
     The fiber length of the electroconductive fibers  16  will be obtained as the arithmetic mean of the fiber lengths of 100 electroconductive fibers in 10 images photographed at a magnification of 500 to 20,000,000 times, for example, using a scanning electron microscope (SEM) (product name “S-4800 (Type 2)”; manufactured by Hitachi High-Technologies Corporation) on the SEM mode, which are measured on the acquired images by an accessory software program. The fiber lengths are measured using the above-described S-4800 (Type 2) together with a 45° pre-tilted sample stub by setting the signal selection to “SE,” the accelerating voltage to “3 kV,” the emission current to “10 μA to 20 μA,” the SE detector to “Mixed,” the probe current to “Norm,” the focus mode to “UHR,” the condenser lens  1  to “5.0,” the WD to “8 mm,” and the Tilt to “30°.” Because no TE detector is used for SEM observation, it is essential to remove the TE detector before SEM observation. Although either the STEM mode or the SEM mode can be selected as an operation mode of the above-described S-4800, the SEM mode will be used for the measurement of the above-described fiber length. 
     When the fiber length of the electroconductive fibers  16  is determined, a measurement sample prepared by the following method is used. First, the electroconductive fiber-containing composition is applied on an untreated surface of a polyethylene terephthalate (PET) film in B5 size having a thickness of 50 μm at an application dose of 10 mg/m 2 , and dried to evaporate the dispersion medium and to place electroconductive fibers on the surface of the PET film, and an electroconductive film is thereby prepared. A piece having a size of 10 mm×10 mm is cut from the central part of the electroconductive film. Then, the cut electroconductive film is attached flat against the tilted surface of a 45° pre-tilted SEM sample stub (model number “728-45”; manufactured by Nissin EM Co., Ltd.; 45° pre-tilted sample stub; 15 mm diameter×10 mm height; made of M4 aluminum) using a silver paste. Furthermore, the cut electroconductive film is sputtered with Pt—Pd for 20 to 30 seconds to obtain electrical conductivity. Because an image of the sample without a suitable sputtered film may not be clearly visible, the sputtering process is appropriately modified in that case. 
     The above-described fiber length can be obtained by image-based measurement or may be calculated from the binarized image data. In the case of image-based measurement, the measurement will be performed by the same method as described above. 
     The electroconductive fibers  16  are preferably at least one type of fibers selected from the group consisting of electroconductive carbon fibers, metallic fibers such as metallic nanowires, metal-coated organic fibers, metal-coated inorganic fibers, and carbon nanotubes. 
     Examples of the above-described electroconductive carbon fiber include vapor grown carbon fiber (VGCF), carbon nanotube, wire cup, and wire wall. These electroconductive carbon fibers may be used individually or in combination of two or more. 
     As the above-described metallic fibers, fibers produced by, for example, a wire drawing process or coil shaving process that prepares a thin and long wire of a metal, such as stainless steel, iron, gold, silver, aluminium, nickel, or titanium, can be used. Such metallic fibers may be used individually or in combination of two or more. The metallic fibers are preferably metallic nanowires having a fiber diameter of 200 nm or less, preferably 50 nm or less, more preferably 30 nm or less, and a fiber length of 1 μm or more, preferably 15 μm or more, more preferably 20 μm or more. 
     Examples of the above-described metal-coated synthetic fibers include acrylic fibers coated with a metal such as gold, silver, aluminium, nickel, or titanium. Such metal-coated synthetic fibers may be used individually or in combination of two or more. 
     &lt;&lt;Other Electroconductive Films&gt;&gt; 
     For the electroconductive film  10  shown in  FIG.  1   , the electroconductive part  13  is a film with no pattern, namely a so-called plain film, but the electroconductive part may be patterned depending on applications. Specifically, the electroconductive film may be an electroconductive film  20 , as shown in  FIGS.  5  to  7   , comprising an electroconductive layer  21  which is composed of plural electroconductive parts  22  and plural nonconductive parts  23  located between the electroconductive parts  22 , or an electroconductive film  30  comprising plural electroconductive parts  31  and plural gaps  32  existing between the electroconductive parts  31 . The surface  20 A of the electroconductive film  20  comprises the surfaces  22 A of the electroconductive parts  22  and the surfaces  23 A of the nonconductive parts  23 , while the surface  30 A of the electroconductive film  30  comprises the surfaces of the electroconductive parts  31  and one surface of the light-transmitting functional layer. For example, the physical property values of the electroconductive films  20  and  30  are similar to those of the electroconductive film  10 . In  FIGS.  5  to  9   , the elements indicated by the same reference numbers as in  FIGS.  1  and  2    are the same as those indicated in  FIGS.  1  and  2   , and further description is thus omitted. 
     &lt;Electroconductive Part&gt; 
     The electroconductive parts  22  and  31  are the same as the electroconductive part  13 , except that the former electroconductive parts are patterned. That is, the electroconductive parts  22  and  31  each comprise a light-transmitting resin  15  and plural electroconductive fibers  16  incorporated in the light-transmitting resin  15 , as shown respectively in  FIGS.  7  and  9   . The electroconductive parts  22  and  31  can conduct electricity from the surfaces. In the electroconductive parts  22  and  31 , the electroconductive fibers  16  are preferably unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive parts  22  and the parts  23 , as shown respectively in  FIGS.  7  and  9   . Other configurations, materials, physical properties values, and the like of the electroconductive parts  22  and  31  are also the same as those of the electroconductive part  13 . 
     The electroconductive parts  22  function, for example, as electrode lines in the X direction in a projected capacitive touch panel and comprise plural sensing portions  22 B aligned in the X direction and plural connectors (not shown) that are connected to the sensing portions  22 B, as shown in  FIG.  6   . Each sensing portion  22 B is located at a rectangular active area for sensing a touch position, while each connector is located at a non-active area adjacent to and surrounding the active area. 
     Each sensing portion  22 B comprise a straight extending linear portion  22 C and an expanded portion  22 D extending from the linear portion  22 C. In  FIG.  6   , linear portions  22 C extend straight along a direction intersecting with the arrangement direction of sensing portions  22 B. The expanded portion  22 D is an outwardly expanded portion extending from a linear portion  22 C on the surface of the light-transmitting functional layer  12 . Thus, the width of each sensing portion  22 B is broadened at an area where an expanded portion  22 D is provided. In the present embodiment, each expanded portion  22 D has an outer contour in a substantially square shape. The shape of each expanded portion  22 D is not limited to a substantially square shape and it may take a diamond shape or a stripe shape. 
     The surface resistance values (Ω/□) of the electroconductive parts  22  and  31  can be measured in pieces of the electroconductive parts  22  and  31  each having a large area (for example, a bezel in a manufactured product). The surface resistance values of the electroconductive parts  22  and  31  are preferably measured using a contact-type resistivity meter (product name “Loresta-AX MCP-T370”; Mitsubishi Chemical Analytech Co., Ltd.) in accordance with JIS K7194: 1994 (Testing method for resistivity of conductive plastics with a four-point probe array), though it depends on the shape and/or size of the patterned electroconductive part  22  or  31 . However, a non-destructive type (eddy current) resistivity meter (product name “EC-80P”; manufactured by Napson Corporation) may be used to measure the surface resistance value in cases where the electroconductive part  22  or  31  has a shape and/or a size that allows the measurement of surface resistance value using the non-destructive resistivity meter. The methods of measuring the surface resistance values of the electroconductive parts  22  and  31  with a contact-type resistivity meter and a non-destructive resistivity meter are the same as those of measuring the surface resistance value of the electroconductive part  13  with a contact-type resistivity meter and a non-destructive resistivity meter, and the description of the methods is omitted here. Although the type of a probe terminal for a Loresta-AX MCP-T370 resistivity meter is typically the ASP-probe type (4-pin probe, inter-pin distance=5 mm, pin-head radius=0.37 mm), a probe terminal of the PSP probe type (4-pin probe, inter-pin distance=1.5 mm, pin-head radius=0.26 mm) or the TFP probe type (4-pin probe, inter-pin distance=1 mm, pin-head radius=0.04 mm) is preferably used in cases where samples obtained from the electroconductive parts  22  and  31  are small in size. 
     &lt;Nonconductive Part&gt; 
     The nonconductive parts  23  are parts located between electroconductive parts  22  and having no electrical conductivity. As shown in  FIG.  7   , the nonconductive parts  23  contain substantially no electroconductive fibers  16 . The phrase “a nonconductive part contains substantially no electroconductive fibers” as used herein means that the nonconductive part may contain a small amount of electroconductive fibers under a condition where an electrical short circuit between electroconductive parts is not formed even if metal ions from the electroconductive parts migrate to and permeated into the nonconductive part. The nonconductive parts  23  preferably contain none of the electroconductive fibers  16 . When electroconductive fibers  16  are removed from the nonconductive parts  23  by sublimating the electroconductive fibers  16  through exposure to laser light as described below or by wet etching based on photolithography, a certain amount of an electroconductive material as a component of the electroconductive fibers  16  may be left as a residue. However, the residual electroconductive materials are not considered as electroconductive fibers because those residual materials are not in fiber form. 
     Because the nonconductive parts  23  are formed together with the electroconductive parts  21  as an integrated body, the film thickness of the nonconductive parts is preferably less than 300 nm, regardless of whether or not an underlayer or a light-transmitting functional layer is provided on a light-transmitting base material. The phrase “the film thickness of nonconductive part” as used herein means the film thickness of a part laminated directly to a basement (such as a light-transmitting base material, underlayer, or light-transmitting functional layer) to which an electroconductive part containing electroconductive fibers identified by observation of a cross-section is also laminated. The maximum film thickness of the nonconductive parts  23  is 145 nm or less, 140 nm or less, 120 nm or less, 110 nm or less, 80 nm or less, 50 nm or less, 30 nm or less, or 10 nm or less in ascending order of preference (a lower value is more preferred). Additionally, the minimum film thickness of the nonconductive parts  23  is preferably 10 nm or more. The film thickness of the nonconductive parts  23  will be measured by the same method as for the film thickness of the electroconductive parts  22 . 
     As shown in  FIG.  7   , the nonconductive parts  23  comprise the light-transmitting resin  15 . The nonconductive parts  23  may be formed by removing electroconductive fibers  16  through sublimation and may have the resulting voids  23 B which are not filled with electroconductive fibers. In that case, the sublimated electroconductive fibers  16  burst out through areas to be the nonconductive parts  23  during the formation of the nonconductive parts  23  and the resulting nonconductive parts  23  have rough surfaces. The light-transmitting resin  15  in the nonconductive parts  23  is the same as the light-transmitting resin  15  in the electroconductive part  13 , and the description of the light-transmitting resin is omitted here. 
     &lt;&lt;Production Methods of Electroconductive Films&gt;&gt; 
     The electroconductive film  10  can be produced, for example, as follows. First, a light-transmitting functional layer composition is applied on one surface of the light-transmitting base material  11  and dried to form a coating film  35  of the light-transmitting functional layer composition, as shown in  FIG.  10 (A) . 
     The light-transmitting functional layer composition contains a polymerizable compound, and may contain the above-described inorganic particles, the above-described leveling agent, a solvent, and a polymerization initiator as necessary. Furthermore, the light-transmitting functional layer composition may be supplemented with, for example, a conventionally known dispersing agent, surfactant, silane coupling agent, thickener, coloring inhibitor, coloring agent (pigment and dye), antifoam agent, flame retardant, ultraviolet absorber, adhesion promoter, polymerization inhibitor, antioxidant, surface modifier, and/or lubricant in accordance with various purposes of, for example, increasing hardness, reducing cure shrinkage, and/or controlling refractive index in the light-transmitting functional layer. 
     &lt;Solvent&gt; 
     Examples of the solvent include alcohols (such as methanol, ethanol, propanol, isopropanol, n-butanol, s-butanol, t-butanol, benzyl alcohol, PGME, and ethylene glycol), ketones (such as acetone, methyl ethyl ketone (MEK), cyclohexanone, methyl isobutyl ketone, diacetone alcohol, cycloheptanone, and diethyl ketone), ethers (such as 1,4-dioxane, dioxolane, diisopropyl ether dioxane, and tetrahydrofuran), aliphatic hydrocarbons (such as hexane), alicyclic hydrocarbons (such as cyclohexane), aromatic hydrocarbons (such as toluene and xylene), halocarbons (such as dichloromethane and dichloroethane), esters (such as methyl formate, methyl acetate, ethyl acetate, propyl acetate, butyl acetate, and ethyl lactate), cellosolves (such as methyl cellosolve, ethyl cellosolve, and butyl cellosolve), cellosolve acetates, sulfoxides (such as dimethyl sulfoxide), amides (such as dimethylformamide and dimethylacetamide), and combinations thereof. 
     &lt;Polymerization Initiator&gt; 
     The polymerization initiator is a component that generates radicals upon degradation induced by exposure to light or heat and initiates or promotes the polymerization (cross-linking) of a polymerizable compound. Examples of a polymerization initiator used in the light-transmitting functional layer composition include photopolymerization initiators (for example, photo-radical polymerization initiators, photo-cationic polymerization initiators, photo-anionic polymerization initiators), thermal polymerization initiators (for example, thermal radical polymerization initiators, thermal cationic polymerization initiators, thermal anionic polymerization initiators), and combinations thereof. 
     Examples of the above-described photo-radical polymerization initiator include benzophenone-based compounds, acetophenone-based compounds, acylphosphine oxide-based compounds, titanocene-based compounds, oxime ester-based compounds, benzoin ether-based compounds, and thioxantone. 
     Among the above-described photo-radical polymerization initiators, commercially available photo-radical polymerization initiators include, for example, Irgacure 184, Irgacure 369, Irgacure 379, Irgacure 651, Irgacure 819, Irgacure 907, Irgacure 2959, Irgacure OXE01, and Lucirin TPO (all are manufactured by BASF Japan Ltd.); NCI-930 (manufactured by ADEKA Corporation); SpeedCure EMK (manufactured by Nihon SiberHegner K.K.); and benzoin methyl ether, benzoin ethyl ether, and benzoin isopropyl ether (all are manufactured by Tokyo Chemical Industry Co., Ltd.). 
     Examples of the above-described photo-cationic polymerization initiator include aromatic diazonium salts, aromatic iodonium salts, and aromatic sulfonium salts. Among the above-described photo-cationic polymerization initiators, commercially available photo-cationic polymerization initiators include, for example, Adeka Optomer SP-150 and Adeka Optomer SP-170 (both are manufactured by ADEKA Corporation). 
     Examples of the above-described thermal radical polymerization initiator include peroxides and azo compounds. Among those, high-molecular-weight azo initiators consisting of high-molecular-weight azo compounds are preferred. Examples of the high-molecular-weight azo initiator include high-molecular-weight azo initiator having a structure composed plural units of, for example, a polyalkylene oxide or a polydimethyl siloxane linked to each other via an azo group. 
     Examples of the above-described high-molecular-weight azo initiator having a structure composed of plural units of, for example, a polyalkylene oxide linked to each other via an azo group include a polycondensate of 4,4′-azobis(4-cyanopentanoic acid) and a polyalkylene glycol, and a polycondensate of 4,4′-azobis(4-cyanopentanoic acid) and a polydimethyl siloxane having a terminal amino group. 
     Examples of the above-described peroxide include ketone peroxide, peroxy ketal, hydroperoxide, dialkyl peroxide, peroxy esters, diacyl peroxide, and peroxy dicarbonate. 
     Among the above-described thermal radical polymerization initiators, examples of commercially available thermal radical polymerization initiators include Perbutyl O, Perhexyl O, and Perbutyl PV (manufactured by NOF Corporation); V-30, V-501, V-601, VPE-0201, VPE-0401, and VPE-0601 (manufactured by Wako Pure Chemical Industries, Ltd.). 
     Examples of the above-described thermal cationic polymerization initiator include various onium salts, such as quaternary ammonium salts, phosphonium salts, and sulfonium salts. Among the above-described thermal cationic polymerization initiators, examples of commercially available thermal cationic polymerization initiators include ADEKA Opton CP-66, and ADEKA Opton CP-77 (manufactured by ADEKA Corporation); SAN AID SI-60L, SAN AID SI-80L, SAN AID SI-100L (manufactured by Sanshin Chemical Industry Co., Ltd.); and CI series (manufactured by Nippon Soda Co., Ltd.). 
     The content of a polymerization initiator in the light-transmitting functional layer composition is preferably 0.5 parts by mass or more and 10.0 parts by mass or less relative to 100 parts by mass of the polymerizable compound. By limiting the content of the polymerization initiator to a value within the above range, hard coat properties can be well maintained and cure inhibition can be inhibited. 
     The method of applying the light-transmitting functional layer composition include known coating methods, such as spin coating, dipping, spraying, slide coating, bar coating, roll coating, gravure coating, and die coating methods. 
     Next, the coating film  35  is exposed to light such as ultraviolet light or heated, as shown in  FIG.  10 (B) , to polymerize (cross-link) the polymerizable compound and to cure the coating film  35 , whereby the light-transmitting functional layer  12  is formed. 
     In cases where ultraviolet light is used as the light to cure the light-transmitting functional layer composition, the ultraviolet light or the like emitted from, for example, a super high pressure mercury lamp, high pressure mercury lamp, low pressure mercury lamp, carbon arc lamp, xenon arc lamp, or metal halide lamp can be used. Additionally, the wavelength range from 190 to 380 nm can be used as the wavelength of ultraviolet light. Specific examples of the source of electron beam include various types of electron beam accelerators, such as Cockcroft-Walton type, Van de Graft type, resonant transformer type, insulating core transformer type, linear type, Dynamitron type, and high frequency type accelerators. 
     After the light-transmitting functional layer  12  is formed on the light-transmitting base material  11 , an electroconductive fiber-containing composition containing electroconductive fibers  16  and an organic dispersion medium is applied on a surface of the light-transmitting functional layer  12  opposite to the light-transmitting base material  11  side surface, and dried to place a plurality of the electroconductive fibers  16  on the light-transmitting functional layer  12 , as shown in  FIG.  11 (A) . The organic dispersion medium may contain water of less than 10% by mass. The electroconductive fiber-containing composition may contain a resin material consisting of a thermoplastic resin or a polymerizable compound, in addition to the electroconductive fibers  16  and the organic dispersion medium. However, in cases where the content of the resin material in the electroconductive fiber-containing composition is excessively high, the resin material permeates into the space between the electroconductive fibers and the electrical conductivity of the electroconductive part is consequently deteriorated. Thus, the content of the resin material is needed to be appropriately adjusted. The term “resin material” as used herein inclusively refers to a component such as polymerizable compound that can be polymerized to a resin, in addition to a resin (however, excluding a resin (for example, polyvinylpyrrolidone) as a component of an organic protective layer that is formed surrounding electroconductive fibers in the preparation of the electroconductive fibers, for the purpose of, for example, preventing the electroconductive fibers from weld anchoring to each other or from reacting with substances in the atmosphere). Additionally, the resin material in the electroconductive fiber-containing composition becomes an integral part of the light-transmitting resin  15  after the formation of the electroconductive part  13 . 
     The organic dispersion medium is not limited to a particular organic dispersion medium, and is preferably a hydrophilic organic dispersion medium. Examples of the organic dispersion medium include saturated hydrocarbons, such as hexane; aromatic hydrocarbons, such as toluene and xylene; alcohols, such as methanol, ethanol, propanol, and butanol; ketones, such as acetone, methyl ethyl ketone (MEK), methyl isobutyl ketone, and diisobutyl ketone; esters, such as ethyl acetate and butyl acetate; ethers such as tetrahydrofuran, dioxane, and diethyl ether; amides, such as N,N-dimethylformamide, N-methylpyrrolidone (NMP), and N,N-dimethylacetamide; and halogenated hydrocarbons, such as ethylene chloride and chlorobenzene. Among those organic dispersion media, alcohols are preferred in terms of the stability of the electroconductive fiber-containing composition. 
     Examples of a thermoplastic resin that may be contained in the electroconductive fiber-containing composition include acrylic resins; polyester resins, such as polyethylene terephthalate; aromatic resins, such as polystyrene, polyvinyl toluene, polyvinyl xylene, polyimide, polyamide, and polyamide-imide; polyurethane resins; epoxy resins; polyolefin resins; acrylonitrile-butadiene-styrene copolymer (ABS); cellulose-based resins; polyvinyl chloride resins; polyacetate resins; polynorbornene resins; synthetic rubber; and fluorine-based resins. 
     Examples of a polymerizable compound that may be contained in the electroconductive fiber-containing composition include polymerizable compounds similar to that described for the light-transmitting functional layer  12 , and the description of the polymerizable compound is omitted here. 
     After a plurality of the electroconductive fibers  16  are placed on the light-transmitting functional layer  12 , a light-transmitting resin composition containing a polymerizable compound and a solvent is applied on it and dried to form a coating film  36  of the light-transmitting resin composition, as shown in  FIG.  11 (B) . The light-transmitting resin composition containing the polymerizable compound and the solvent may additionally contain a polymerization initiator and the above-described reaction inhibitor as necessary. In this respect, although a reaction inhibitor can be added to an electroconductive fiber-containing composition, the addition of the reaction inhibitor to the electroconductive fiber-containing composition may cause coating of the surface of electroconductive fibers with the reaction inhibitor before the electroconductive fibers form a network structure, which in turn deteriorates the electrical conductivity. Thus, a reaction inhibitor is preferably added to the light-transmitting resin composition. 
     Next, the coating film  36  is exposed to ionizing radiation such as ultraviolet light, as shown in  FIG.  12 (A) , to polymerize (cross-link) the polymerizable compound and to cure the coating film  36 , whereby the light-transmitting resin  15  is formed. 
     Because the electroconductive part  13  of the electroconductive film  10  shown in  FIG.  1    is a plain film, the electroconductive film  10  is obtained in the above-described process. On the other hand, because the electroconductive film  20  shown in  FIG.  5    is patterned, the patterning step will be described below. 
     After the light-transmitting resin  15  is formed, areas to be the nonconductive parts  23  are exposed to laser light (for example, infrared laser) to form a pattern on the electroconductive part  13 , as shown in  FIG.  12 (B) . Upon irradiation of laser light to the regions of the prospective nonconductive parts  23 , electroconductive fibers  16  included in the regions are sublimated by the heat of the laser light. The sublimated electroconductive fibers  16  burst out through the light-transmitting resin  15 . Thus, an electroconductive film  10  comprising the electroconductive part  13  shown in  FIG.  1    and further comprising the nonconductive parts  23  can be obtained. The patterning of the electroconductive part  13  described above is performed by exposure to laser light, while the patterning of the electroconductive part  13  may be performed by photolithography because electroconductive fibers  16  can also be removed by photolithography from areas to be the nonconductive parts  23 . 
     According to the present embodiment, since the electroconductive fibers  16  as a whole in the electroconductive part  13  or parts  22  or  31  are unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13  or parts  22  or  31 , the contact points between the electroconductive fibers  16  can be increased. This allows ensuring electrical conduction from the surface  13 A of the electroconductive part  13  or the surfaces of the electroconductive parts  22  and  31  and thus for achieving a low surface resistance value of 200Ω/□ or less, even if the content of electroconductive fibers  16  is low. Additionally, a low haze value of 5% or less can be achieved because the content of electroconductive fibers  16  can be reduced. 
     In a thin electroconductive part, since the amount of electroconductive fibers is accordingly reduced, the electroconductive part is prone to increase the surface resistance value. According to the present embodiment, the electroconductive fibers  16  as a whole in the electroconductive part  13  or parts  22  or  31  are unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13  or parts  22  or  31 , to increase the contact points between the electroconductive fibers  16 , whereby a low haze value of 5% or less and a low surface resistance value of 200Ω/□ or less can be achieved even if the electroconductive part  13  or parts  22  or  31  have a thin film thickness of less than 300 nm or a very thin film thickness of 145 nm or less. 
     According to the present embodiment, since the electroconductive fibers  16  in the electroconductive part  13  or parts  22  or  31  are unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13  or parts  22  or  31 , a majority of the electroconductive fibers  16  are covered with the light-transmitting resin  15 . This allows inhibiting the electroconductive fibers  16  from reducing the electrical conductivity due to the reaction with sulfur, oxygen, and/or halogens in the air. 
     According to the present embodiment, since the electroconductive fibers  16  in the electroconductive part  13  or parts  22  or  31  are unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13  or parts  22  or  31 , a maximally excellent surface resistance value can be obtained with a minimum amount of electroconductive fibers. Additionally, the uneven distribution of the electroconductive fibers  16  as described above enables optical properties with a lower haze value. Furthermore, uneven distribution, rather than homogeneous dispersion, of electroconductive fibers  16  enables easier adjustment of the Martens hardness. Additionally, the dense presence of electroconductive fibers  16  in the light-transmitting resin  15  enables increasing the hardness of the light-transmitting resin and also enables obtaining a light-transmitting resin which is neither too hard nor too soft by devising the composition of the light-transmitting resin  15 . In addition, the light-transmitting resin having an appropriate Martens hardness could achieve excellent flexibility for folding or rolling. That is, by combining features of the present invention, physical properties suitable for the requirements of various applications can be imparted. 
     Even in conventional electroconductive films, some electroconductive films have an electroconductive part comprising a light-transmitting resin and electroconductive fibers incorporated in the light-transmitting resin, and the electroconductive parts of those electroconductive films are formed using an electroconductive fiber-containing composition containing electroconductive fibers and a resin material. In this respect, an aqueous dispersion medium is mainly used as a dispersion medium in an electroconductive fiber-containing composition used for a conventional electroconductive part. The term “aqueous dispersion medium” as used herein shall mean a dispersion medium having a water concentration of 10% by mass or more. For using an aqueous dispersion medium, an electroconductive fiber-containing composition contains a large content of a resin material in view of storage stability and ability to provide a homogeneous coating film upon application. Because of this, even if an electroconductive part is formed using an electroconductive fiber-containing composition, electroconductive fibers as a whole are currently not enabled to distribute unevenly on the light-transmitting base material side than the position located at half the film thickness of the electroconductive part. On the other hand, in cases where an organic dispersion medium is used as the dispersion medium, the ability to provide a homogeneous coating film upon application is superior, which enables to reduce the content of the resin material. In the present embodiment, an organic dispersion medium is used as a dispersion medium for an electroconductive fiber-containing composition, and the electroconductive fiber-containing composition contains no resin material or, alternatively, a smaller amount of a resin material than the conventional amount of the resin material. Accordingly, in the electroconductive part  13  or parts  22  or  31 , the electroconductive fibers  16  can be unevenly distributed on the light-transmitting base material  11  side than the position HL, which is located at half the film thickness of the electroconductive part  13  or parts  22  or  31 , as well as the electroconductive part  13  or parts  22  or  31  can have a film thickness of less than 300 nm or a very thin film thickness of 145 nm or less. 
     In cases where an electroconductive film is formed using electroconductive fibers, the electrical resistance value is likely to be different depending on the in-plain direction of an electroconductive part. If the electrical resistance value is different depending on the in-plain direction of the electroconductive part and the electroconductive film is used as an electrode for a touch panel sensor, the patterning of the electrode may have to be changed, as well as the electroconductive film is limited in partitioning and is thus prone to be wasted. The inventors found that, in an electroconductive part containing electroconductive fibers formed on a light-transmitting base material by coating process (particularly, by roll-to-roll process), the electroconductive fibers tend to align along the flow direction of the light-transmitting base material (MD direction) and the electrical resistance value in the MD direction is accordingly reduced; on the other hand, the electrical resistance value observed in a direction (TD direction) orthogonal to the MD direction on the surface of the electroconductive part tends to be higher than that observed in the MD direction, which causes a difference in electrical resistance value depending on the in-plain direction. Depending on the way of defining an arbitrary direction AD, a first direction in which the lowest electrical resistance value is provided is highly likely to be the MD direction or a direction which is inclined at an angle of less than 30 degrees from the MD direction. Accordingly, in cases where the first direction is the MD direction, a second direction perpendicular to the first direction is the TD direction. According to the present embodiment, the electroconductive part  13  is provided directly on the light-transmitting base material  11  by coating process; the difference in electrical resistance value depending on the in-plain direction of the electroconductive part  13  can be reduced if the above-described electrical resistance value ratio is 1 or more and less than 2 in the electroconductive part  13 . In cases where the electroconductive film is used for an electrode for a touch panel sensor, limitations on the pattern of the electrode, IC chips, and partitioning are reduced with the reduced difference in electrical resistance. 
     Meanwhile, image display devices are increasing application examples and image display devices with various shapes (for example, an elongate shape) are under development. An image display device may not conduct electricity equally in all two-dimensional directions but conduct more electricity in a particular direction although it depends on the shape of the image display device. Thus, an electroconductive film incorporated into an image display device may also have a low electrical resistance value in a particular direction on the surface and higher electrical resistance values in other directions. According to the present embodiment, the electroconductive part  13  has a high electrical resistance value in the second direction and a low electrical resistance value in the first direction in cases where the above-described electrical resistance value ratio is 2 or more. Thus, the electroconductive film  30  showing a further lower electrical resistance value in a particular direction (first direction) can be provided. 
     According to the present embodiment, the light-transmitting resin  15  in the electroconductive part  13  or parts  22  or  31  contains a reaction inhibitor, and can consequently prevent the electroconductive fibers  16  from reducing the electrical conductivity due to the reaction with sulfur, oxygen, and/or halogens in the atmospheric air. 
     An electroconductive part will be contacted with a light-transmitting adhesive layer when an electroconductive film is incorporated into an image display device. When the electroconductive part in contact with the light-transmitting adhesive layer is tested in a humidity/heat resistance test by leaving them for 240 hours, for example, in an environment at a temperature of 60° C. and a relative humidity of 90%, an environment at a temperature of 85° C. and a relative humidity of 85%, or an environment at a higher temperature and a higher relative humidity, electroconductive fibers may react with components of the light-transmitting adhesive layer (for example, an acidic component that constitutes the adhesive layer itself, and/or an additive that has been added to the adhesive layer) depending on the type of the light-transmitting adhesive layer, which in turn increases the surface resistance value of the electroconductive part. In this respect, according to the present embodiment, a reaction inhibitor contained in the electroconductive part  13  or parts  22  or  31  can control the reaction of the electroconductive fibers  16  with components of a light-transmitting adhesive layer, even if the electroconductive part  13  or parts  22  or  31  in contact with the light-transmitting adhesive layer are tested by the humidity/heat resistance test. Accordingly, the number of light-transmitting adhesive layer choices can be increased. 
     The application of an electroconductive film according to the present embodiment is not limited to a particular application and can be incorporated into an image display device comprising a touch panel and be used. Additionally, the electroconductive film can be used, for example, as an electro-magnetic interference shield.  FIG.  13    depicts a schematic diagram of an image display device according to the present embodiment;  FIG.  14    depicts a schematic plain view of a touch panel according to the present embodiment; and  FIG.  15    depicts an enlarged view of a part of the electroconductive film on the side of the display panel shown in  FIG.  13   . 
     &lt;&lt;&lt;Image Display Device&gt;&gt;&gt; 
     As shown in  FIG.  13   , an image display device  40  mainly comprises a display panel  50  for displaying images, a backlight unit  60  placed on the back surface of the display panel  50 , a touch panel  70  placed on the observer&#39;s side of the display panel  50 , and a light-transmitting adhesion layer  90  intervening between the display panel  50  and the touch panel  70 . In the present embodiment, the display panel  50  is a liquid-crystal display panel and the image display device  40  thus comprises the backlight unit  60  but may not comprise the backlight unit  60  depending on the type of the display panel (display element). 
     &lt;&lt;Display Panel&gt;&gt; 
     The display panel  50  has a laminate structure, as shown in  FIG.  13   , composed of a protective film  51  made of, for example, a triacetyl cellulose film (TAC film) or a cycloolefin polymer film, a polarizer  52 , a protective film  53 , a light-transmitting adhesive layer  54 , a display element  55 , a light-transmitting adhesive layer  56 , a protective film  57 , a polarizer  58 , and a protective film  59  in this order from the backlight unit  60  to the observer&#39;s side. The display panel  50  should comprise the display element  55  and may not comprise the protective film  51  or the like. 
     The display element  55  is a liquid-crystal display element. However, the display element  55  is not limited to a liquid-crystal display element, and may be a display element using, for example, an organic light-emitting diode (OLED), an inorganic light-emitting diode, and/or a quantum dot light-emitting diode (QLED). The liquid-crystal display element comprises, for example, a liquid-crystal layer, an alignment film, an electrode layer, and a color filter located between two glass base materials. 
     &lt;&lt;Backlight Unit&gt;&gt; 
     The backlight unit  60  illuminates the display panel  50  from the back surface of the display panel  50 . Any known backlight unit can be used as the backlight unit  60 , and, moreover, the backlight unit  60  may be either an edge light-type or a direct light-type backlight unit. 
     &lt;&lt;Touch Panel&gt;&gt; 
     The touch panel  70  comprises an electroconductive film  80 , an electroconductive film  20  placed on the observer&#39;s side of the electroconductive film  80 , a light-transmitting cover member  71 , such as a cover glass, placed on the observer&#39;s side of the electroconductive film  20 , a light-transmitting adhesive layer  72  intervening between the electroconductive film  80  and the electroconductive film  10 , and a light-transmitting adhesive layer  73  intervening between the electroconductive film  20  and the light-transmitting cover member  71 . 
     &lt;Electroconductive Film&gt; 
     The electroconductive film  80  has almost the same structure as that of the electroconductive film  20 . That is, the electroconductive film  80  comprises a light-transmitting base material  81 , a light-transmitting functional layer  82  provided on one surface of the light-transmitting base material  81 , and electroconductive parts  84  provided and patterned on a surface of the light-transmitting functional layer  82  opposite to the light-transmitting base material  81  side surface, as shown in  FIG.  13   . The electroconductive parts  84  are an integral part of an electroconductive layer  83 . The electroconductive layer  83  is composed of plural electroconductive parts  84  and nonconductive parts  85  located between the electroconductive parts  84 . The light-transmitting base material  81  is similar to the light-transmitting base material  11  and the light-transmitting functional layer  82  is likewise similar to the light-transmitting functional layer  82 , and further descriptions is thus omitted here. 
     (Electroconductive Part and Nonconductive Part) 
     The electroconductive parts  84  have the same structure as that of the electroconductive parts  22 . That is, the electroconductive parts  84  comprise a light-transmitting resin  86  and electroconductive fibers  87 , as shown in  FIG.  15   . The nonconductive parts  85  comprise the light-transmitting resin  86  and contain substantially no electroconductive fibers  87 . The nonconductive parts  85  shown in  FIG.  15    comprise voids  85 A in the light-transmitting resin  86 , similarly to the nonconductive parts  23 . Additionally, the electroconductive fibers  87  are unevenly distributed on the light-transmitting base material  81  side than the position HL, which is located at half the film thickness of the electroconductive parts  84 , and the electroconductive parts  84  can conduct electricity from the surfaces  84 A. 
     The electroconductive parts  84  function as electrode lines in the Y direction in a projected capacitive touch panel and comprise plural sensing electrodes  84 B and plural connectors (not shown) that are connected to the sensing electrodes  84 B, as shown in  FIG.  14   . The sensing electrodes  84 B have the same structure as that of the sensing electrodes  84 B but extend in the Y direction. The electroconductive parts  84  have the same structure as that of the electroconductive part  13  but the electroconductive parts  84  may not need to have the same structure as that of the electroconductive parts  22 . 
     &lt;Light-Transmitting Adhesive Layer&gt; 
     Examples of the light-transmitting adhesive layers  72  and  73  include adhesive sheets, such as OCA (optical clear adhesive) sheets. Light-transmitting adhesion layers may be used instead of the light-transmitting adhesive layers  72  and  73 . 
     &lt;&lt;Light-Transmitting Adhesion Layer&gt;&gt; 
     The light-transmitting adhesion layer  90  intervenes between the display panel  50  and the touch panel  70 , and is attached to both the display panel  50  and the touch panel  70 . Thus, the display panel  50  and the touch panel  70  are bonded together. The light-transmitting adhesion layer  90  comprises a cured product of, for example, a liquid curable adhesion layer composition comprising a polymerizable compound such as an OCR (optically clear resin). 
     The light-transmitting adhesion layer  90  preferably has a film thickness of 10 μm or more and 150 μm or less. In cases where the light-transmitting adhesion layer has a film thickness of less than 10 μm, the light-transmitting adhesion layer is so thin that troubles such as jamming of foreign bodies or poor gap filling performance may easily occur; additionally, in cases where the light-transmitting adhesion layer has a film thickness of more than 150 μm, the production cost is too high. The film thickness of the light-transmitting adhesion layer is determined as the arithmetic mean of the film thickness values measured at randomly selected 10 locations, wherein the film thickness values are determined at the 10 locations in cross-sectional images of the light-transmitting adhesion layer acquired using an optical microscope. A light-transmitting adhesive layer may be used instead of the light-transmitting adhesion layer  90 . 
     Second Embodiment 
     Now, the electroconductive film, touch panel, and image display device according to the second embodiment of the present invention will be described below with reference to the drawings.  FIG.  16    depicts a schematic diagram of an electroconductive film according to the present embodiment;  FIG.  17    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  16   ;  FIG.  18    depicts a schematic diagram of another electroconductive film according to the present embodiment; and  FIG.  19    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  18   . 
     &lt;&lt;&lt;Electroconductive Film&gt;&gt;&gt; 
     The electroconductive film  100  shown in  FIG.  16    is light transmissive and comprises a light-transmitting base material  101 , a light-transmitting functional layer  102  provided on one surface of the light-transmitting base material  101 , and an electroconductive part  103  provided on a surface of the light-transmitting functional layer  102  opposite to the light-transmitting base material  101  side surface. However, the electroconductive film  100  should comprise the light-transmitting base material  101  and the electroconductive part  103 , and may not comprise the light-transmitting functional layer  102 . The light-transmitting functional layer  102  shown in  FIG.  16    is provided between the light-transmitting base material  101  and the electroconductive part  103 ; a light-transmitting functional layer may be provided not between the light-transmitting base material  101  and the electroconductive part  103  but on a surface of the light-transmitting base material  101  opposite to the electroconductive part  103  side surface, or may be provided both between the light-transmitting base material  101  and the electroconductive part  103  and on a surface of the light-transmitting base material  101  opposite to the electroconductive part  103  side surface. Additionally, in the electroconductive film  100  shown in  FIG.  16   , the electroconductive part  103  is provided on only one surface of the electroconductive film, but electroconductive parts may be provided on both surfaces of the electroconductive film. 
     The electroconductive film  100  has a haze value (total haze value) of 5% or less for the same reason as described for the electroconductive film  10 . The haze value of the electroconductive film  100  can be measured by the same method as for the haze value of the electroconductive film  10 . The electroconductive film  100  has a haze value of 3% or less, 2% or less, 1.5% or less, 1.2% or less, or 1.1% or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive film  100  preferably has a total light transmittance of 80% or more for the same reason as described for the electroconductive film  10 . The total light transmittance of the electroconductive film  100  can be measured by the same method as for the total light transmittance of the electroconductive film  10 . The electroconductive film  10  has a total light transmittance of 85% or more, 88% or more, or 89% or more in ascending order of preference (a higher value is more preferred). 
     &lt;&lt;Light-Transmitting Resin Base Material&gt;&gt; 
     The light-transmitting base material  101  is not limited to a particular light-transmitting base material as long as it is a base material composed of a light-transmissive resin. The light-transmitting base material  101  is the same as the light-transmitting base material  11 . Thus, the constituent materials and thickness of the light-transmitting base material  101  are also the same as those of the light-transmitting base material  11 . The light-transmitting base material  101  is similar to the light-transmitting base material  11 , and the description is thus omitted here. 
     &lt;&lt;Light-Transmitting Functional Layer&gt;&gt; 
     The light-transmitting functional layer  102  is placed between the light-transmitting base material  101  and the electroconductive part  103 . The light-transmitting functional layer  102  is the same as the light-transmitting functional layer  12 . For example, specific examples, the pencil hardness, the film thickness, the constituent materials, and the additives of the light-transmitting functional layer  102  are also the same as those of the light-transmitting base material  11 . The light-transmitting functional layer  102  is similar to the light-transmitting functional layer  12 , and the description is thus omitted here. 
     &lt;&lt;Electroconductive Part&gt;&gt; 
     The surface  100 A of the electroconductive film  100  is constituted by the surface  103 A of the electroconductive part  103 . The electroconductive part  103  comprises a light-transmitting resin  104  and plural electroconductive fibers  105  incorporated in the light-transmitting resin  104 , as shown in  FIG.  17   . The electroconductive part  103  preferably further comprises a reaction inhibitor which is contained in the light-transmitting resin  104 . 
     The ratio of the electrical resistance value in a second direction to that in a first direction (the ratio is hereinafter referred to as “electrical resistance value ratio”) is 1 or more and less than 2 when the electrical resistance values are measured in samples having a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface  103 A of the electroconductive part  103 , wherein a direction in which the electroconductive part shows the lowest electrical resistance value is designated as the first direction, and a direction which is perpendicular to the first direction is designated as the second direction. The electrical resistance value ratio can be determined by a method similar to the electric resistance measurement method described for the electroconductive part  13 . The maximum electrical resistance value ratio is 1.8 or less, 1.5 or less, 1.3 or less, or 1.2 or less in ascending order of preference (a lower value is more preferred). 
     Such an electroconductive part  103  having an electrical resistance value ratio of 1 or more and less than 2 can be obtained, for example, by modifying the fiber length of the below-described electroconductive fibers  105 , the type or film thickness of a resin that constitutes the below-described organic protective layer, and/or the temperature for drying the electroconductive fiber-containing composition. 
     The electroconductive part  103  can conduct electricity from the surface  103 A of the electroconductive part  103 . Measurement of the surface resistance value of the electroconductive part  103  can determine, as in the case of the electroconductive part  13 , whether or not the electroconductive part can conduct electricity from the surface of the electroconductive part. The method of measuring the surface resistance of the electroconductive part  103  and the criteria to evaluate whether or not the electroconductive part  103  can conduct electricity from the surface  103 A of the electroconductive part  103  are the same as those described for the electroconductive part  13 , and the description of the measurement method and the evaluation criteria is thus omitted here. Although a majority of the electroconductive fibers  105  are distributed from the position HL, which is located at half the film thickness of the electroconductive part  103 , to the light-transmitting base material  101 , as described below, the remaining electroconductive fibers  105  are stacked on the electroconductive fibers  105  which are distributed on the light-transmitting base material  101  side, and consequently distributed from the position HL, which is located at half the film thickness of the electroconductive part  103 , to the surface  103 A, and also exposed on the surface  103 A of the electroconductive part  103 . Thus, the electroconductive part  103  can conduct electricity from the surface  103 A. 
     In the electroconductive part  103 , the electroconductive fibers  105  are preferably unevenly distributed on the light-transmitting base material  101  side than the position HL, which is located at half the film thickness of the electroconductive part  103 , as shown in  FIG.  17   . The determination of whether or not the electroconductive fibers  105  are unevenly distributed on the light-transmitting base material  101  side than the position HL, which is located at half the film thickness of the electroconductive part  103 , is achieved by the evaluation method described for the electroconductive part  13 , and the description of the method is omitted here. The existence ratio of electroconductive fibers distributed on the light-transmitting base material  101  side than the position located at half the film thickness of the electroconductive part, which is determined from cross-sectional images photographed using a scanning transmission electron microscope (STEM) or a transmission electron microscope (TEM), is 70% or more or 80% or more in ascending order of preference (a higher value is more preferred). 
     The surface resistance of the electroconductive part  103  is 200Ω/□ or less for the same reason as described for the electroconductive part  13 . The surface resistance of the electroconductive part  103  is a surface resistance value measured on the surface  103 A of the electroconductive part  103 . The surface resistance of the electroconductive part  103  can be measured by the same method as for the surface resistance of the electroconductive part  13 . The minimum surface resistance value of the electroconductive part  103  is 1Ω/□ or more, 5Ω/□ or more, or 10Ω/□ or more in ascending order of preference (a higher value is more preferred), while the maximum surface resistance value of the electroconductive part  103  is 100Ω/□ or less, 70Ω/□ or less, 60Ω/□ or less, or 50Ω/□ or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive part  103  preferably has a film thickness of less than 300 nm from the viewpoint of thinning the electroconductive film. The film thickness of the electroconductive part  103  can be measured by the same method as for the film thickness of the electroconductive part  13 . The maximum film thickness of the electroconductive part  103  is 145 nm or less, 140 nm or less, 120 nm or less, 110 nm or less, 80 nm or less, or 50 nm or less in ascending order of preference (a lower value is more preferred). Additionally, the minimum film thickness of the electroconductive part  103  is preferably 10 nm or more for the same reason as described for the electroconductive part  13 . 
     The electroconductive part  103  preferably has a Martens hardness of 970 N/mm 2  or more and 1050 N/mm 2  or less at an indentation amount of 10 nm from the surface  103 A for the same reason as described for the electroconductive part  13 . In the electroconductive part  103 , the minimum Martens hardness at the above-described indentation amount of 10 nm is 980 N/mm 2  or more, 1000 N/mm 2  or more, or 1015 N/mm 2  or more in ascending order of preference (a higher value is more preferred); the maximum Martens hardness at the above-described indentation amount of 10 nm is 1040 N/mm 2  or less, 1030 N/mm 2  or less, or 1020 N/mm 2  or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive part  103  preferably has a Martens hardness of 130 N/mm 2  or more and 300 N/mm 2  or less at an indentation amount of 100 nm from the surface  103 A for the same reason as described for the electroconductive part  13 . In the electroconductive part  103 , the minimum Martens hardness at the above-described indentation amount of 100 nm is 140 N/mm 2  or more, 150 N/mm 2  or more, or 170 N/mm 2  or more in ascending order of preference (a higher value is more preferred); the maximum Martens hardness at the above-described indentation amount of 100 nm is 280 N/mm 2  or less, 250 N/mm 2  or less, or 200 N/mm 2  or less in ascending order of preference (a lower value is more preferred). 
     &lt;Light-Transmitting Resin&gt; 
     The light-transmitting resin  104  covers electroconductive fibers  105 , similarly to the light-transmitting resin  15 , to prevent removal of the electroconductive fibers  105  from the electroconductive part  103  and to improve the durability or abrasion resistance of the electroconductive part  103 , and, also in the present embodiment, covers electroconductive fibers  105  to such an extent that the electroconductive part  103  can conduct electricity from the surface  103 A. The light-transmitting resin  104  is the same as the light-transmitting resin  15 . Thus, the film thickness and constituent materials of the light-transmitting resin  104  are also the same as those of the light-transmitting resin  15 . The light-transmitting resin  104  is similar to the light-transmitting resin  15 , and the description is thus omitted here. 
     &lt;Reaction Inhibitor&gt; 
     A reaction inhibitor is a substance that prevents reduction in electrical conductivity after application of the light-transmitting resin composition due to the reaction of the electroconductive fibers  105  with substances in the atmosphere. The reaction inhibitor and the content of the reaction inhibitor are the same as those described in the first embodiment, and the description of the reaction inhibitor and the content is thus omitted here. 
     &lt;Electroconductive Fibers&gt; 
     In cases where the electroconductive fibers  105  are unevenly distributed on the light-transmitting base material  101  side than the position HL, which is located at half the film thickness of the electroconductive part  103 , the electroconductive fibers  105  contact with each other in the thickness direction of the electroconductive part  103 , as indicated by the ability of the electroconductive part  103  to conduct electricity from the surface  103 A. 
     The electroconductive fibers  105  preferably contact with each other to form a network structure (meshwork) to the surface direction (two-dimensional direction) of the electroconductive part  103  in the light-transmitting base material  101  side than the position HL, which is located at half the film thickness of the electroconductive part  103 . Formation of a network structure by the electroconductive fibers  105  enables efficient creation of a conductive path with the electroconductive fibers  105  even in a small amount. 
     Some of the electroconductive fibers  105  are preferably exposed on the surface  103 A of the electroconductive part  103 . Once electrical conduction from the surface  103 A of the electroconductive part  103  is identified by the above-described measurement method, some of the electroconductive fibers  105  can thus be determined to be exposed on the surface  103 A of the electroconductive part  103 . 
     The electroconductive fibers  105  preferably have a fiber diameter of 200 nm or less for the same reason as described for the electroconductive fibers  16 . The minimum fiber diameter of the electroconductive fibers  105  is more preferably 10 nm or more from the viewpoint of the electroconductive of the electroconductive part  103 , and a more preferred range of fiber diameter in the electroconductive fibers  105  is from 15 nm to 180 nm inclusive. The fiber diameter of the electroconductive fibers  105  can be obtained by the same method as for the fiber diameter of the electroconductive fibers  16 . 
     The electroconductive fibers  105  preferably have a fiber length of 1 μm or more and less than 30 μm. In cases where the electroconductive fibers  105  have a fiber length of less than 1 μm, the surface resistance value is increased, which may result in failure to form an electroconductive part having a sufficient electrical conductivity. The amount of added electroconductive fibers having a fiber length of less than 1 μm may be increased to reduce the surface resistance. However, an increase of the added amount of such electroconductive fibers leads to reduction in surface resistance value but may result in a higher haze value and a low light transmittance. Additionally, in cases where the electroconductive fibers  105  have a fiber length of 30 μm or more, electroconductive fibers are easily aligned along the below-described MD direction, which causes a tendency to increase the difference in electrical resistance value depending on the direction on a surface, or leads to a difficulty in coating during the preparation of an electroconductive part by coating process. The electroconductive fibers  105  preferably have a minimum fiber length of 10 μm or more and a maximum fiber length of 20 μm or more. The fiber length of the electroconductive fibers  105  can be obtained by the same method as for the fiber length of the electroconductive fibers  16 . 
     The constituent fibers of the electroconductive fibers  105  are the same as those of the electroconductive fibers  16 , and the description of the constituent fibers is thus omitted here. 
     &lt;&lt;Other Electroconductive Films&gt;&gt; 
     For the electroconductive film  100  shown in  FIG.  16   , the electroconductive part  103  is a film with no pattern, namely a so-called plain film, but the electroconductive part may be patterned depending on applications. Specifically, the electroconductive film may be an electroconductive film  110 , as shown in  FIG.  18   , comprising an electroconductive layer  111  which is composed of plural electroconductive parts  112  and plural nonconductive parts  113  located between the electroconductive parts  112 , or an electroconductive film comprising, as shown in  FIG.  4   , plural electroconductive parts and plural gaps existing between the electroconductive parts. The surface  110 A of the electroconductive film  110  comprises the surfaces  112 A of the electroconductive parts  112  and the surfaces  113 A of the nonconductive parts  113 , while the surface of the electroconductive film comprising gaps existing between electroconductive parts comprises the surfaces of the electroconductive parts and one surface of the light-transmitting functional layer. For example, the physical property values of the electroconductive film  110  and the electroconductive film comprising gaps existing between electroconductive parts are similar to those of the electroconductive film  100 . In  FIG.  18   , the elements indicated by the same reference numbers as in  FIG.  16    are the same as those indicated in  FIG.  16   , and further description is thus omitted. 
     &lt;Electroconductive Part&gt; 
     The electroconductive parts  112  are the same as the electroconductive part  103 , except that the former electroconductive parts are patterned. That is, the electroconductive parts  112  comprise a light-transmitting resin  104  and plural electroconductive fibers  105  incorporated in the light-transmitting resin  104 , as shown in  FIG.  19   . The electroconductive parts  112  can conduct electricity from the surfaces  112 A. In the electroconductive parts  112 , the electroconductive fibers  105  are preferably unevenly distributed on the light-transmitting base material  101  side than from the position HL, which is located at half the film thickness of the electroconductive parts  112 , as shown in  FIG.  19   . Other configurations, materials, physical properties values, and the like of the electroconductive parts  112  are also the same as those of the electroconductive part  10 , and further description is thus omitted here. 
     &lt;Nonconductive Part&gt; 
     The nonconductive parts  113  are parts located between electroconductive parts  112  and having no electrical conductivity. As shown in  FIG.  19   , the nonconductive parts  113  contain substantially no electroconductive fibers  105 . 
     Because the nonconductive parts  113  are formed together with the electroconductive parts  112  as an integrated body, the film thickness of the nonconductive parts is less than 300 nm. The maximum film thickness of the nonconductive parts  23  is 145 nm or less, 140 nm or less, 120 nm or less, 110 nm or less, 80 nm or less, or 50 nm or less in ascending order of preference (a lower value is more preferred). Additionally, the minimum film thickness of the nonconductive parts  23  is preferably 10 nm or more. The film thickness of the nonconductive parts  113  will be measured by the same method as for the film thickness of the electroconductive part  103 . 
     As shown in  FIG.  19   , the nonconductive parts  113  comprise the light-transmitting resin  104 . The nonconductive parts  113  may be formed by removing electroconductive fibers  105  through sublimation and may have the resulting voids  113 B which are not filled with electroconductive fibers. In that case, the sublimated electroconductive fibers  105  burst out through areas to be the nonconductive parts  113  during the formation of the nonconductive parts  113  and the resulting nonconductive parts  113  have rough surfaces  113 A. The light-transmitting resin  104  in the nonconductive parts  113  is the same as the light-transmitting resin  104  in the electroconductive part  103 , and the description is thus omitted here. 
     &lt;&lt;Production Methods of Electroconductive Films&gt;&gt; 
     The electroconductive film  100  can be produced, for example, as follows. First, a light-transmitting functional layer composition is applied on one surface of the light-transmitting base material  11  and dried to form a coating film of the light-transmitting functional layer composition. The light-transmitting functional layer composition is the same as that used in the first embodiment, and the description of the light-transmitting functional layer composition is thus omitted here. 
     Next, the coating film is exposed to ionizing radiation such as ultraviolet light or heated to polymerize (cross-link) a polymerizable compound and to cure the coating film, whereby the light-transmitting functional layer  102  is formed. 
     After the light-transmitting functional layer  102  is formed on the light-transmitting base material  101 , an electroconductive fiber-containing composition containing electroconductive fibers  105  and an organic dispersion medium is applied on a surface of the light-transmitting functional layer  102  opposite to the light-transmitting base material  101  side surface, and dried to place a plurality of the electroconductive fibers  105  on the light-transmitting functional layer  102 . The electroconductive fiber-containing composition is the same as that used in the first embodiment, and the description of the electroconductive fiber-containing composition is thus omitted here. 
     After a plurality of the electroconductive fibers  105  are placed on the light-transmitting functional layer  102 , a light-transmitting resin composition containing a polymerizable compound and a solvent is applied on the electroconductive fibers  105  and dried to form a coating film of the light-transmitting resin composition. The light-transmitting resin composition is the same as that used in the first embodiment, and the description of the light-transmitting resin composition is thus omitted here. 
     Next, the coating film is exposed to ionizing radiation such as ultraviolet light to polymerize (cross-link) the polymerizable compound and to cure the coating film, whereby the light-transmitting resin  104  is formed. Thus, an electroconductive film  10  as shown in  FIG.  16    can be obtained. The electroconductive film  110  shown in  FIG.  18    is patterned and can be obtained similarly to the first embodiment, for example, by irradiating laser light (for example, infrared laser) to areas to be the nonconductive parts  113  for the generation of patterns of the electroconductive parts  112 . 
     According to the present embodiment, the electroconductive part  103  or  112  is provided directly on the light-transmitting base material  101  by coating process; the difference in electrical resistance value depending on the in-plain direction of the electroconductive part  103  or  112  can be reduced due to the same reason as described in the first embodiment, because the above-described electrical resistance value ratio is 1 or more and less than 2 in the electroconductive part  103  or  112 . In cases where the electroconductive film is used for an electrode for a touch panel sensor, limitations on the pattern of the electrode and on IC chips are reduced, and the patterning of the electrode for a touch panel sensor needs not be changed, and limitations on partitioning is also reduced. 
     In the present embodiment, the contact points between the electroconductive fibers  105  can be increased in cases where the electroconductive fibers  105  as a whole in the electroconductive part  103  or parts  112  are unevenly distributed on the light-transmitting base material  101  side than the position HL, which is located at half the film thickness of the electroconductive part  103  or parts  112 . This allows ensuring electrical conduction from the surface  103 A of the electroconductive part  103  or the surfaces  112 A of the electroconductive parts  112  through the electroconductive fibers  105  exposed on the surface  103 A or the surfaces  112 A and thus for achieving a lower surface resistance value, even if the content of electroconductive fibers  105  is low. Additionally, a low haze value of 5% or less can be achieved because the content of electroconductive fibers  105  can be reduced. 
     In a thin electroconductive part, the amount of electroconductive fibers is accordingly reduced and the electroconductive part is thus prone to increase the surface resistance. A according to the present embodiment, the contact points between the electroconductive fibers  105  are increased in cases where the electroconductive fibers  105  as a whole in the electroconductive part  103  or parts  112  are unevenly distributed on the light-transmitting base material  101  side than the position HL, which is located at half the film thickness of the electroconductive part  103  or parts  112 , and a low haze value of 5% or less and a low surface resistance value of 200Ω/□ or less can consequently be achieved even if the electroconductive part  103  or parts  112  have a thin film thickness of less than 300 nm or a very thin film thickness of 145 nm or less. 
     According to the present embodiment, a majority of the electroconductive fibers  105  in the electroconductive part  103  are covered with the light-transmitting resin  104  in cases where the electroconductive fibers  105  are unevenly distributed on the light-transmitting base material  101  side than the position HL, which is located at half the film thickness of the electroconductive part  103 . This enables reducing the corrosion of the electroconductive fibers  105  by sulfur and/or oxygen in the air. 
     In the present embodiment, a maximally excellent surface resistance value can be obtained with a minimum amount of electroconductive fibers in cases where the electroconductive fibers  105  as a whole in electroconductive part  103  or parts  112  are unevenly distributed on the light-transmitting base material  101  side than the position HL, which is located at half the film thickness of the electroconductive part  103  or parts  112 . Additionally, the uneven distribution of the electroconductive fibers  105  as described above enables optical properties with a lower haze value. Furthermore, uneven distribution, rather than homogeneous dispersion, of electroconductive fibers  105  enables easier adjustment of the Martens hardness. Additionally, the dense presence of electroconductive fibers  105  in the light-transmitting resin  104  enables increasing the hardness of the light-transmitting resin and also enables obtaining a light-transmitting resin which is neither too hard nor too soft by devising the composition of the light-transmitting resin  104 . In addition, the light-transmitting resin having an appropriate Martens hardness could achieve excellent flexibility for folding or rolling. 
     In the present embodiment, an organic dispersion medium is used as a dispersion medium for an electroconductive fiber-containing composition, and the electroconductive fiber-containing composition contains no resin material or, alternatively, a smaller amount of a resin material than the conventional amount of the resin material. Accordingly, in the electroconductive part  103  or parts  112 , the electroconductive fibers  105  can be unevenly distributed on the light-transmitting base material  10  side than the position HL, which is located at half the film thickness of the electroconductive part  103  or parts  112 , due to the same reason as described in the first embodiment. 
     According to the present embodiment, the light-transmitting resin  104  in the electroconductive part  103  or parts  112  contains a reaction inhibitor, and can consequently prevent the electroconductive fibers  105  from reducing the electrical conductivity due to the reaction with sulfur, oxygen, and/or halogens in the atmospheric air. 
     According to the present embodiment, a reaction inhibitor contained in the electroconductive part  103  or parts  112  can control the reaction of the electroconductive fibers  105  with components of a light-transmitting adhesive layer due to the same reason as described in the first embodiment, even if the electroconductive part  103  or parts  112  in contact with the light-transmitting adhesive layer are tested by the humidity/heat resistance test. Accordingly, the number of light-transmitting adhesive layer choices can be increased. 
     According to the present embodiment, the use of electroconductive fibers  105 , differing from ITO, enables providing an electroconductive film  10  which is hardly broken when folded. Thus, the electroconductive films  100  and  110  can be incorporated into a foldable image display device and then used. 
     The electroconductive films  100  and  110  have been described above; the above-described electroconductive film comprising gaps existing between electroconductive parts can likewise obtain the same effects as those of the electroconductive films  100  and  110 . 
     The electroconductive film  100  according to the present embodiment can be incorporated into, for example, an image display device and then used.  FIG.  20    depicts a schematic diagram of an image display device according to the present embodiment. In  FIG.  20   , the elements indicated by the same reference numbers as in  FIG.  13    are the same as those indicated in  FIG.  13   , and further description is thus omitted. 
     &lt;&lt;&lt;Image Display Device&gt;&gt;&gt; 
     As shown in  FIG.  20   , an image display device  120  mainly comprises a display panel  50  for displaying images, a backlight unit  60  placed on the back surface of the display panel  50 , a touch panel  130  placed on the observer&#39;s side of the display panel  50 , and a light-transmitting adhesion layer  90  intervening between the display panel  50  and the touch panel  130 . In the present embodiment, the display panel  50  is a liquid-crystal display panel and the image display device  40  thus comprises the backlight unit  60  but may not comprise the backlight unit  60  depending on the type of the display panel (display element). 
     &lt;&lt;Touch Panel&gt;&gt; 
     The touch panel  130  comprises an electroconductive film  140 , an electroconductive film  110  placed on the observer&#39;s side of the electroconductive film  140 , a light-transmitting cover member  71 , such as a cover glass, placed on the observer&#39;s side of the electroconductive film  110 , a light-transmitting adhesive layer  72  intervening between the electroconductive film  140  and the electroconductive film  110 , and a light-transmitting adhesive layer  73  intervening between the electroconductive film  110  and the light-transmitting cover member  71 . 
     &lt;Electroconductive Film&gt; 
     The electroconductive film  140  has almost the same structure as that of the electroconductive film  110 . That is, the electroconductive film  14   l  comprises a light-transmitting base material  141 , a light-transmitting functional layer  142  provided on one surface of the light-transmitting base material  141 , and electroconductive parts  134  provided and patterned on a surface of the light-transmitting functional layer  142  opposite to the light-transmitting base material  141  side surface, as shown in  FIG.  20   . The electroconductive parts  134  are an integral part of an electroconductive layer  143 . The electroconductive layer  143  is composed of plural electroconductive parts  134  and nonconductive parts  135  located between the electroconductive parts  134 . The light-transmitting base material  141  is similar to the light-transmitting base material  101  and the light-transmitting functional layer  142  is likewise similar to the light-transmitting functional layer  102 , and further descriptions is thus omitted here. 
     (Electroconductive Part and Nonconductive Part) 
     The electroconductive parts  134  have the same structure as that of the electroconductive parts  112 . That is, the electroconductive parts  134  comprise a light-transmitting resin and electroconductive fibers, as shown in  FIG.  20   . The nonconductive parts  135  comprise a light-transmitting resin and contain substantially no electroconductive fibers. Additionally, the electroconductive fibers in the electroconductive parts  134  are unevenly distributed on the light-transmitting base material  141  side than the position HL, which is located at half the film thickness of the electroconductive parts  134 , and the electroconductive parts  134  can conduct electricity from the surfaces  144 A. The electroconductive parts  134  have the same structure as that of the electroconductive parts  112  but the electroconductive parts  134  may not need to have the same structure as that of the electroconductive parts  112 . 
     The electroconductive parts  112  of the electroconductive film  110  function as electrode lines in the X direction in a projected capacitive touch panel, while the electroconductive parts  134  of the electroconductive film  140  function as electrode lines in the Y direction in a projected capacitive touch panel and have the same top view as shown in  FIG.  14   . 
     The electroconductive films used in touch panel applications have been described in the above embodiment, but the electroconductive films are not limited to particular applications. For example, the electroconductive film  100  and  110  can also be used for connection with IC chips or as electric wirings. 
     Third Embodiment 
     Now, the electroconductive film, touch panel, and image display device according to the third embodiment of the present invention will be described below with reference to the drawings.  FIG.  21    depicts a schematic diagram of an electroconductive film according to the present embodiment;  FIG.  22    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  21   ; and  FIG.  23    schematically illustrates each step of the foldability test.  FIG.  24    depicts a schematic diagram of another electroconductive films according to the present embodiment, while  FIG.  25    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  24   .  FIGS.  26  and  27    schematically illustrate the process for producing the electroconductive film according to the present embodiment. 
     &lt;&lt;&lt;Electroconductive Film&gt;&gt;&gt; 
     The electroconductive film  150  shown in  FIG.  21    is light transmissive and comprises a light-transmitting base material  151 , and an electroconductive part  152  provided directly on one surface of the light-transmitting base material  151 . The surface  150 A of the electroconductive film  150  is constituted by the surface  152 A of the electroconductive part  152 . 
     The electroconductive film  150  further comprises an underlayer  153  provided directly on the other surface  151 B of the light-transmitting resin base material  151  opposite to the one surface  151 A. In addition, although the electroconductive part  152  shown in  FIG.  21    is provided only on the one surface  151 A of the light-transmitting resin base material  151 , an electroconductive part may additionally be provided on the other surface  151 B of the light-transmitting resin base material  151 . In that case, it is preferred not to provide the underlayer  153  and to provide an electroconductive part directly on the other surface  151 B of the light-transmitting resin base material  151 . However, in cases where electroconductive parts are provided on both surfaces of the light-transmitting resin base material, an electroconductive part should be provided directly on one surface of the light-transmitting resin base material and another electroconductive part may not need to be provided directly on the other surface of the light-transmitting resin base material. 
     The electroconductive film  150  has a haze value (total haze value) of 5% or less for the same reason as described for the electroconductive film  10 . The haze value of the electroconductive film  150  can be measured by the same method as for the haze value of the electroconductive film  10 . The electroconductive film  150  has a haze value of 3% or less, 2% or less, 1.5% or less, 1.2% or less, or 1.1% or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive film  150  preferably has a total light transmittance of 80% or more for the same reason as described for the electroconductive film  10 . The total light transmittance of the electroconductive film  150  can be measured by the same method as for the total light transmittance of the electroconductive film  10 . The electroconductive film  150  has a total light transmittance of 85% or more, 88% or more, or 89% or more in ascending order of preference (a higher value is more preferred). 
     The electroconductive film  150  has flexibility. Preferably, even if the electroconductive film  150  is folded at 180 degrees in a manner that leaves a gap of 3 mm between the opposite edges of the electroconductive film  150  and the process (foldability test) is repeated one hundred thousand times, the below-described ratio between the electrical resistance values measured before and after the foldability test on the surface  152 A of the electroconductive part  152  of the electroconductive film  150  is 3 or less; more preferably, the ratio between the electrical resistance values measured before and after the foldability test on the surface  152 A of the electroconductive part  152  of the electroconductive film  150  is 3 or less even if the foldability test is repeated two hundred thousand times; further preferably, the ratio between the electrical resistance values measured before and after the foldability test on the surface  152 A of the electroconductive part  152  of the electroconductive film  150  is 3 or less even if the foldability test is repeated one million times. In cases where the ratio between the electrical resistance values measured before and after the foldability test on the surface of an electroconductive part of an electroconductive film is more than 3 after repeating the foldability test on the electroconductive film one hundred thousand times, the value of the ratio indicates the possibility that the electroconductive film is cracked or otherwise damaged, which in turn means that the electroconductive film has poor flexibility. In this respect, any crack or other damage to the electroconductive film by the foldability test reduces the electrical conductivity, which causes the electrical resistance value measured after the foldability test on the surface of the electroconductive part of the electroconductive film to be higher than that measured before the foldability test on the surface of the electroconductive part of the electroconductive film. Because of this respect, the determination of whether or not an electroconductive film is cracked or otherwise damaged can be achieved by determining the ratio between the electrical resistance values measured before and after the foldability test on the surface of the electroconductive part of the electroconductive film. If a hard coat layer is provided between a light-transmitting resin base material and an electroconductive part, it is highly likely that the hard coat layer is cracked by the foldability test after repeating the foldability test the number of times as specified above and the ratio of the electrical resistance value measured after the foldability test on the surface of the electroconductive part of the electroconductive film exceeds 3. In cases where the foldability test is repeated the number of times as specified above, the ratio between the electrical resistance values measured before and after the foldability test on the surface  152 A of the electroconductive part  152  of the electroconductive film  150  is more preferably 1.5 or less, regardless of whether a hard coat layer is provided or not. The foldability test may be carried out by folding the electroconductive film  150  with the electroconductive part  152  facing either inward or outward. In either case, the ratio between the electrical resistance values measured before and after the foldability test on the surface  152 A of the electroconductive part  152  of the electroconductive film  150  is preferred to be 3 or less. 
     Specifically, first of all, samples similar to those prepared for the measurement of the electrical resistance as described in the first embodiment are prepared. Specifically, as in the case of the electroconductive film  30  shown in  FIG.  8   , an arbitrary direction AD is determined in the surface of the electroconductive part  152  and samples S having a predetermined size (for example, in a rectangular shape having a size of 125 mm length×50 mm width) and extending in six different directions including the arbitrary direction AD, which are each an angle of 30 degrees to the arbitrary direction, are cut from the electroconductive film  150  before the foldability test. If samples having a size of 125 mm length×50 mm width cannot be cut, samples having a size of, for example, 110 mm length×50 mm width may be cut from the electroconductive film. After six samples S are cut from the electroconductive film before the foldability test, each of the samples S before the foldability test is measured for electrical resistance on the surface of the electroconductive part. Specifically, as in the case of  FIG.  9   , a silver paste (product name “DW-520H-14”; manufactured by Toyobo Co., Ltd.) is applied on both longitudinal ends of each sample S (for example, each end having a size of 10 mm length×50 mm width) to prevent any change in distance between points for measuring the electrical resistance, and heated at 130° C. for 30 minutes to provide a cured silver paste to each end of the sample, and the electrical resistance of the sample is then measured using a tester (product name “Digital MΩ Hitester 3454-11”; manufactured by Hioki E.E. Corporation). When the electrical resistance is measured, probe terminals of the tester are individually contacted with either of the cured silver pastes provided on both ends. After the electrical resistance on the surface  152 A of the electroconductive part  152  is measured in each sample before the foldability test, a sample S exhibiting the lowest electrical resistance value is selected among the samples S. Subsequently, the foldability test is performed on the selected sample S. 
     The foldability test is carried out as follows. The foldability test starts with fixing the edge S 1  and opposite edge S 2  of the selected sample S to fixing members  156  arranged in parallel to each other, as shown in  FIG.  23 (A) . In addition, the fixing members  156  can slide in the horizontal direction, as shown in  FIG.  23 (A) . 
     Next, the fixing members  156  are moved close to each other to fold and deform the sample S at the center part S 3 , as shown in  FIG.  23 (B) ; the fixing members  156  are further moved until a gap between the two opposing edges S 1  and S 2  of the sample S fixed to the fixing members  156  reaches 3 mm, as shown in  FIG.  23 (C) ; subsequently, the fixing members  156  are moved in opposite directions to resolve the deformation of the sample S. 
     As shown  FIG.  23 (A)  to (C), the fixing members  156  can be moved to fold the sample S at the center part S 3  at 180 degrees. In addition, a gap of 3 mm can be maintained between the two opposing edges S 1  and S 2  of the sample S by carrying out the foldability test in a manner that prevents the bent part S 4  of the sample S from being forced out beyond the lower edges of the fixing members  156  and controls the fixing members  156  to keep a distance of 3 mm when they approach closest each other. In this case, the outer width of the bent part S 4  is considered as 3 mm. The thickness of the sample S is small enough as compared with the gap between the fixing members  156  (3 mm). Thus, it seems unlikely that a difference in the thickness of the sample S affects the result of the foldability test on the sample S. 
     After the foldability test is performed, the sample S after the foldability test is measured for electrical resistance on the surface of the electroconductive part, similarly to the sample S before the foldability test. Then, the ratio of the electrical resistance value measured after the foldability test on the selected sample S to that measured before the foldability test on the same sample S (the electrical resistance of the selected sample before the foldability test/the electrical resistance of the same sample after the foldability test) is calculated. The arithmetic mean of three measurements is determined as the electrical resistance value ratio. 
     &lt;&lt;Light-Transmitting Resin Base Material&gt;&gt; 
     The light-transmitting resin base material  151  is not limited to a particular light-transmitting resin base material as long as it is a base material composed of a light-transmissive resin. Examples of the light-transmitting resin as a component of the light-transmitting resin base material  151  include the same light-transmitting resins as those described for the light-transmitting base material  11 . The thickness of the light-transmitting base material  151  is the same as that of the light-transmitting base material  11 . However, although some light-transmitting resin base materials have an underlayer for the purpose of improving adhesion to other layers, preventing the electroconductive film from sticking to itself when the electroconductive film is rolled, and/or inhibiting cissing of a coating liquid applied for forming another layer, the term “light-transmitting resin base material” in the present embodiment will be used to refer to a light-transmitting resin base material without an underlayer. The light-transmitting resin base material  151  may have a surface treated by a physical treatment such as corona discharge treatment or oxidation treatment to improve the adhesiveness. 
     &lt;&lt;Electroconductive Part&gt;&gt; 
     The electroconductive part  152  is provided directly on one surface  151 A of the light-transmitting resin base material  151 . The phrase “provided directly on” in this context means that the electroconductive part is in direct contact with one surface of the light-transmitting resin base material. That is, no underlayer is provided between the light-transmitting resin base material  151  and the electroconductive part  152 . The determination of whether or not an electroconductive part is provided directly on one surface of a light-transmitting resin base material, or whether or not an underlayer is provided between a light-transmitting resin base material and an electroconductive part can be achieved by observing a cross-section near the interface between the light-transmitting resin base material and the electroconductive part using a scanning electron microscope (SEM), a scanning transmission electron microscope (STEM), or a transmission electron microscope (TEM) at a magnification of 1,000 to 500,000 times. The underlayer may contain particles as, for example, lubricant additives for the purpose of preventing an electroconductive film from sticking to itself when the electroconductive film is rolled; accordingly, the layer between the light-transmitting resin base material and the electroconductive part can be identified as an underlayer by the presence of the particles in the layer. As the electron microscopy conditions for the measurement in this case, the conditions for measuring the film thickness of, for example, the electroconductive part  13  can be used. 
     The electroconductive part  152  comprises a light-transmitting resin  154  and plural electroconductive fibers  155  incorporated in the light-transmitting resin  154 , as shown in  FIG.  22   . The electroconductive part  152  preferably further comprises a reaction inhibitor which is contained in the light-transmitting resin  154 . 
     The electroconductive part  152  can conduct electricity from the surface  152 A. The determination of whether or not the electroconductive part  152  can conduct electricity from the surface  152 A of the electroconductive part  152  can be achieved by measuring the surface resistance value of the electroconductive part  152 , as in the case of the electroconductive part  13 . The method of measuring the surface resistance value of the electroconductive part  152  and the criteria to evaluate whether or not the electroconductive part  152  can conduct electricity from the surface  152 A of the electroconductive part  152  are the same as those described for the electroconductive part  13 , and the description of the measurement method and the evaluation criteria is thus omitted here. Although a majority of the electroconductive fibers  155  are distributed on the light-transmitting resin base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152 , as described below, the remaining electroconductive fibers  155  are stacked on the electroconductive fibers  155  which are distributed on the light-transmitting resin base material  151  side, and consequently distributed on the surface  152 A side than the position HL, which is located at half the film thickness of the electroconductive part  152 , and also located on the surface  152 A of the electroconductive part  152 . Thus, the electroconductive part  152  can conduct electricity from the surface  152 A. 
     In the electroconductive part  152 , the electroconductive fibers  155  are preferably unevenly distributed on the light-transmitting base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152 , as shown in  FIG.  22   . The determination of whether or not the electroconductive fibers  155  are unevenly distributed on the light-transmitting base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152 , is achieved by the evaluation method described for the electroconductive part  13 , and the description of the method is omitted here. The existence ratio of electroconductive fibers distributed on the the light-transmitting base material side than the position located at half the film thickness of the electroconductive part, which is determined from cross-sectional images photographed using a scanning transmission electron microscope (STEM) or a transmission electron microscope (TEM), is preferably 70% or more, more preferably 80% or more. 
     The surface resistance value of the electroconductive part  152  is 200Ω/□ or less for the same reason as described for the electroconductive part  13 . The surface resistance value of the electroconductive part  152  is a surface resistance value measured on the surface  152 A of the electroconductive part  152 . The surface resistance of the electroconductive part  152  can be measured by the same method as for the surface resistance of the electroconductive part  13 . The minimum surface resistance value of the electroconductive part  152  is 1Ω/□ or more, 5Ω/□ or more, or 10Ω/□ or more in ascending order of preference (a higher value is more preferred), while the maximum surface resistance value of the electroconductive part  152  is 100Ω/□ or less, 70Ω/□ or less, 60Ω/□ or less, or 50Ω/□ or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive part  152  preferably has a film thickness of less than 300 nm from the viewpoint of thinning the electroconductive film. The maximum film thickness of the electroconductive part  152  is 145 nm or less, 140 nm or less, 120 nm or less, 110 nm or less, 80 nm or less, or 50 nm or less in ascending order of preference (a lower value is more preferred). Additionally, the minimum film thickness of the electroconductive part  152  is preferably 10 nm or more for the same reason as described for the electroconductive part  13 . The film thickness of the electroconductive part  152  can be measured by the same method as for the film thickness of the electroconductive part  13 . 
     The electroconductive part  152  preferably has a Martens hardness of 970 N/mm 2  or more and 1050 N/mm 2  or less at an indentation amount of 10 nm from the surface  152 A for the same reason as described for the electroconductive part  13 . In the electroconductive part  152 , the minimum Martens hardness at the above-described indentation amount of 10 nm is 980 N/mm 2  or more, 1000 N/mm 2  or more, or 1015 N/mm 2  or more in ascending order of preference (a higher value is more preferred); the maximum Martens hardness at the above-described indentation amount of 10 nm is 1040 N/mm 2  or less, 1030 N/mm 2  or less, or 1020 N/mm 2  or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive part  152  preferably has a Martens hardness of 130 N/mm 2  or more and 300 N/mm 2  or less at an indentation amount of 100 nm from the surface  152 A for the same reason as described for the electroconductive part  13 . In the electroconductive part  152 , the minimum Martens hardness at the above-described indentation amount of 100 nm is 140 N/mm 2  or more, 150 N/mm 2  or more, or 170 N/mm 2  or more in ascending order of preference (a higher value is more preferred); the maximum Martens hardness at the above-described indentation amount of 100 nm is 280 N/mm 2  or less, 250 N/mm 2  or less, or 200 N/mm 2  or less in ascending order of preference (a lower value is more preferred). 
     In cases where the electroconductive film  150  is used as an electrode for a touch panel sensor, the ratio of the electrical resistance in the second direction to that in the first direction (the ratio is hereinafter referred to as “electrical resistance value ratio”) is preferably 1 or more and less than 2 when the electrical resistance values are measured in a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface  152 A of the electroconductive part  152 , wherein a direction in which the electroconductive part shows the lowest electrical resistance value is designated as the first direction, and a direction which is orthogonal to the first direction is designated as the second direction. The electrical resistance value ratio can be determined by a method similar to the electric resistance measurement method described for the electroconductive part  13 . The maximum electrical resistance value ratio is preferably 1.8 or less, more preferably 1.5 or less, and most preferably 1.3 or less. 
     On the other hand, in cases of obtaining an electroconductive film which provides a much lower electrical resistance value in a particular direction, the above-described electrical resistance value ratio is preferably 2 or more when the electrical resistance values are measured in a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface  31 A of the electroconductive part  31 . The arithmetic mean of three measurements is determined as the electrical resistance value ratio. The minimum electrical resistance value ratio is more preferably 3 or more. The maximum electrical resistance value ratio is 10 or less, or 8 or less in ascending order of preference (a lower value is more preferred) from the viewpoint of obtaining a uniform resistance value on the surface. 
     Such an electroconductive part having an electrical resistance value ratio of 1 or more and less than 2 or an electrical resistance value ratio of 2 or more can be obtained, for example, by appropriately modifying the fiber length of electroconductive fibers, the type or film thickness of a resin that constitutes the below-described organic protective layer, and/or the temperature for drying the electroconductive fiber-containing composition. 
     &lt;Light-Transmitting Resin&gt; 
     The light-transmitting resin  154  covers electroconductive fibers  155 , similarly to the light-transmitting resin  15 , to prevent removal of the electroconductive fibers  155  from the electroconductive part  152  and to improve the durability or scratch resistance of the electroconductive part  152 , and, also in the present embodiment, covers electroconductive fibers  155  to such an extent that the electroconductive part  152  can conduct electricity from the surface  152 A. 
     The light-transmitting resin  154  is the same as the light-transmitting resin  15 . Thus, the film thickness and constituent materials of the light-transmitting resin  154  are also the same as those of the light-transmitting resin  15 . The light-transmitting resin  154  is similar to the light-transmitting resin  15 , and the description is thus omitted here. However, in cases where the electroconductive part  152  is provided directly on one surface  151 A of the light-transmitting resin base material  151 , and the light-transmitting resin  154  has a refractive index lower than that of the light-transmitting resin base material  151 , and the light-transmitting resin  154  has a film thickness of 60 nm or more and 130 nm or less, the electroconductive part  152  can exhibit substantially the same effect as that of a low-refractive-index layer in an anti-reflection film to reduce the reflectance of the surface  152 A of the electroconductive part  152 . This enables reducing the light reflection Y-value as well as increasing the total light transmittance. In that case, the absolute difference in refractive index between the light-transmitting resin  154  and the light-transmitting resin base material  151  is preferably 0.05 or more. 
     &lt;Reaction Inhibitor&gt; 
     A reaction inhibitor is a substance that prevents reduction in electrical conductivity after application of the light-transmitting resin composition due to the reaction of the electroconductive fibers  15  with substances in the atmosphere. The reaction inhibitor and the content of the reaction inhibitor are the same as those described in the first embodiment, and the description of the reaction inhibitor and the content is thus omitted here. 
     &lt;Electroconductive Fibers&gt; 
     In cases where the electroconductive fibers  155  are unevenly distributed on the light-transmitting base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152 , the electroconductive fibers  155  contact with each other in the thickness direction of the electroconductive part  152 , as indicated by the ability of the electroconductive part  152  to conduct electricity from the surface  152 A. 
     The electroconductive fibers  155  preferably contact with each other to the surface direction (two-dimensional direction) of the electroconductive part  152  to form a network structure (meshwork) in the light-transmitting resin base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152 . Formation of a network structure by the electroconductive fibers  155  enables efficient creation of a conductive path with the electroconductive fibers  155  even in a small amount. 
     Some of the electroconductive fibers  155  are preferably exposed on the surface  152 A of the electroconductive part  152 . Once electrical conduction from the surface  152 A of the electroconductive part  152  is identified by the above-described measurement method, some of the electroconductive fibers  155  can thus be determined to be exposed on the surface  152 A of the electroconductive part  152 . 
     The electroconductive fibers  155  preferably have a fiber diameter of 200 nm or less for the same reason as described for the electroconductive fibers  16 . The minimum fiber diameter of the electroconductive fibers  155  is more preferably 10 nm or more from the viewpoint of the electroconductive of the electroconductive part  152 , and a more preferred range of fiber diameter in the electroconductive fibers  155  is 15 nm or more to 180 nm or less. The fiber diameter of the electroconductive fibers  155  can be obtained by the same method as for the fiber diameter of the electroconductive fibers  16 . 
     The electroconductive fibers  155  preferably have a fiber length of 1 μm or more for the same reason as described for the electroconductive fibers  16 . The maximum fiber length of the electroconductive fibers  155  may be 500 μm or less, 300 μm or less, or 30 μm or less, while the minimum fiber length of the electroconductive fibers  155  may be 3 μm or more, or 10 μm or more. The fiber length of the electroconductive fibers  155  can be obtained by the same method as for the fiber length of the electroconductive fibers  16 . 
     Similarly to the electroconductive fibers  16 , the electroconductive fibers  155  preferably have a fiber length of, for example, 1 μm or more and less than 30 μm in cases of obtaining an electroconductive part having an electrical resistance value ratio of 1 or more and less than 2, while the electroconductive fibers  155  preferably have a fiber length of, for example, 30 μm or more in cases of obtaining an electroconductive part having an electrical resistance value ratio of 2 or more. In cases of obtaining an electroconductive part having an electrical resistance value ratio of 1 or more and less than 2, the electroconductive fibers  155  preferably have a minimum fiber length of 10 μm or more and a maximum fiber length of 20 μm or less from the viewpoint of obtaining a low surface resistance value. 
     The constituent fibers of the electroconductive fibers  155  are the same as those of the electroconductive fibers  16 , and the description of the constituent fibers is thus omitted here. 
     &lt;&lt;Underlayer&gt;&gt; 
     The underlayer  153  is a layer for the purpose of improving adhesion to other layers, preventing the electroconductive film from sticking to itself when the electroconductive film is rolled, and/or inhibiting cissing of a coating liquid applied for forming another layer. The underlayer  153  contains, for example, an anchoring agent and/or a priming agent. As the anchoring agent and the priming agent, at least any of, for example, polyurethane resins, polyester resins, polyvinyl chloride resins, polyvinyl acetate resins, vinyl chloride-vinyl acetate copolymers, acrylic resins, polyvinyl alcohol resins, polyvinyl acetal resins, copolymers of ethylene and vinyl acetate or acrylic acid, copolymers of ethylene and styrene and/or butadiene, thermoplastic resins such as olefin resins and/or modified resins thereof, polymers of radiation-polymerizable compounds, polymers of thermopolymerizable compounds, and the like can be used. 
     The underlayer  153  may contain particles of a lubricant or the like for the purpose of preventing the electroconductive film from sticking to itself when the electroconductive film is rolled, as described above. Examples of the particles include silica particles. 
     The underlayer  153  preferably has a film thickness of 10 nm or more and 1 μm or less. In cases where the underlayer has a film thickness of less than 10 nm, the underlayer may function insufficiently; additionally, in cases where the underlayer has a film thickness of more than 1 μm, the underlayer may adversely affect the optical properties or may fail to provide excellent adhesion. The film thickness of the underlayer  153  is determined as the arithmetic mean of the thickness values measured at randomly selected 10 locations, wherein the thickness values are determined at the 10 locations in cross-sectional images of the underlayer photographed using a scanning electron microscope (SEM), a scanning transmission electron microscope (STEM), or a transmission electron microscope (TEM) at a magnification of 1,000 to 500,000 times (preferably, a magnification of 25,000 to 50,000 times). The underlayer  153  more preferably has a minimum film thickness of 30 nm or more and a maximum film thickness of 150 nm or less. The film thickness of the underlayer  153  can also be measured by the same method as for the film thickness of the electroconductive part  13 . 
     &lt;&lt;Other Electroconductive Films&gt;&gt; 
     For the electroconductive film  150  shown in  FIG.  21   , the electroconductive part  152  is a film with no pattern, namely a so-called plain film, but the electroconductive part may be patterned depending on applications. Specifically, the electroconductive film may be an electroconductive film  160 , as shown in  FIG.  24   , comprising an electroconductive layer  161  which is composed of plural electroconductive parts  162  and plural nonconductive parts  163  located between the electroconductive parts  162 , or an electroconductive film comprising, as shown in  FIG.  4   , plural electroconductive parts and plural gaps existing between the electroconductive parts. The surface  160 A of the electroconductive film  160  comprises the surfaces  162 A of the electroconductive parts  162  and the surfaces  163 A of the nonconductive parts  163 , while the surface of the electroconductive film having gaps existing between electroconductive parts comprises the surfaces of the electroconductive parts and one surface of the light-transmitting resin base material. For example, the physical property values of the electroconductive film  160  and the electroconductive film having gaps existing between electroconductive parts are similar to those of the electroconductive film  150 . In  FIG.  24   , the elements indicated by the same reference numbers as in  FIG.  21    are the same as those indicated in  FIG.  21   , and further description is thus omitted. 
     &lt;Electroconductive Part&gt; 
     The electroconductive parts  162  are the same as the electroconductive part  152 , except that the former electroconductive parts are patterned. That is, the electroconductive parts  162  are provided directly on one surface  151 A of the light-transmitting resin base material  151 . Additionally, the electroconductive parts  162  comprise a light-transmitting resin  154  and plural electroconductive fibers  155  incorporated in the light-transmitting resin  154 , as shown in  FIG.  25   . The electroconductive parts  162  can conduct electricity from the surfaces  162 A. In the electroconductive parts  162 , the electroconductive fibers  165  are preferably unevenly distributed on the light-transmitting base material  151  side than the position HL, which is located at half the film thickness of the electroconductive parts  162 , as shown in  FIG.  25   . Other configurations, materials, physical properties values, and the like of the electroconductive parts  162  are also the same as those of the electroconductive part  152 , and further description is thus omitted here. 
     &lt;Nonconductive Part&gt; 
     The nonconductive parts  163  are parts located between electroconductive parts  162  and having no electrical conductivity. As shown in  FIG.  25   , the nonconductive parts  163  contain substantially no electroconductive fibers  155 . The nonconductive parts  163  preferably contain none of the electroconductive fibers  155 . 
     Because the nonconductive parts  163  are prepared together with the electroconductive parts  162  as an integrated body, the film thickness of the nonconductive parts is less than 300 nm. The maximum film thickness of the nonconductive parts  163  is 145 nm or less, 140 nm or less, 120 nm or less, 110 nm or less, 80 nm or less, or 50 nm or less in ascending order of preference (a lower value is more preferred). Additionally, the minimum film thickness of the nonconductive parts  163  is preferably 10 nm or more. The film thickness of the nonconductive parts  163  will be measured by the same method as for the film thickness of the electroconductive part  13 . 
     As shown in  FIG.  25   , the nonconductive parts  163  comprise the light-transmitting resin  154 . The nonconductive parts  163  may be prepared by removing electroconductive fibers  155  through sublimation and may have the resulting voids  163 B which are not filled with electroconductive fibers. In that case, the sublimated electroconductive fibers  155  burst out through areas to be the nonconductive parts  163  during the preparation of the nonconductive parts  163  and the resulting nonconductive parts  163  have rough surfaces  163 A. The light-transmitting resin  154  in the nonconductive parts  163  is the same as the light-transmitting resin  154  in the electroconductive parts  162 , and the description is thus omitted here. 
     &lt;&lt;Production Methods of Electroconductive Films&gt;&gt; 
     The electroconductive film  160  can be produced, for example, as follows. As shown in  FIG.  26 (A) , a light-transmitting resin base material  151  carrying an underlayer  153  not on one surface  151 A but on the other surface  151 B is first formed. Incidentally, a light-transmitting resin base material having no underlayer on both surfaces may alternatively be prepared. 
     Next, an electroconductive fiber-containing composition containing electroconductive fibers  155  and an organic dispersion medium is applied directly on the one surface  151 A of the light-transmitting resin base material  151 , and dried to place a plurality of the electroconductive fibers  155  directly on the one surface  151 A of the light-transmitting resin base material  151 , as shown in  FIG.  26 (B) . The electroconductive fiber-containing composition is the same as that used in the first embodiment, and the description of the electroconductive fiber-containing composition is thus omitted here. 
     After a plurality of the electroconductive fibers  155  are placed directly on the one surface  151 A of the light-transmitting resin base material  151 , a light-transmitting resin composition containing a polymerizable compound and a solvent is applied on it and dried to form a coating film  157  of the light-transmitting resin composition, as shown in  FIG.  26 (C) . The light-transmitting resin composition is the same as that used in the first embodiment, and the description of the light-transmitting resin composition is thus omitted here. 
     Next, the coating film  157  is exposed to ionizing radiation such as ultraviolet light, as shown in  FIG.  27 (A) , to polymerize (cross-link) the polymerizable compound and to cure the coating film  157 , whereby the light-transmitting resin  154  is prepared. 
     Because the electroconductive part  31  of the electroconductive film  150  shown in  FIG.  21    is a plain film, the electroconductive film  150  is obtained in the above-described process. The electroconductive film  160  shown in  FIG.  23    is patterned and can be obtained similarly to the first embodiment, for example, by irradiating laser light (for example, infrared laser) to areas to be the nonconductive parts  163  for the generation of patterns of the electroconductive parts  162 , as shown in  FIG.  27 (B) . 
     According to the present embodiment, the electroconductive part  152  or parts  162  are provided directly on the one surface  151 A of the light-transmitting resin base material  151 , that is, no underlayer is provided between the light-transmitting resin base material  151  and the electroconductive part  152  or parts  162 , so that no electroconductive fibers  155  are incorporated in an underlayer. Thus, the electroconductive fibers  155  hardly spread in the thickness direction of the electroconductive film  150  or  160  and the contact points between the electroconductive fibers  155  are consequently increased. Accordingly, the electroconductive film can achieve a low surface resistance. Additionally, the content of electroconductive fibers  155  can be reduced and a low haze value of 5% or less can consequently be achieved because the contact points between the electroconductive fibers  155  can be increased. 
     In a thin electroconductive part, the amount of electroconductive fibers is accordingly reduced and the electroconductive part is thus prone to increase the surface resistance. According to the present embodiment, the contact points between the electroconductive fibers  155  are increased in cases where the electroconductive fibers  155  as a whole in the electroconductive part  152  or parts  162  are unevenly distributed on the light-transmitting base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152  or parts  162 , and a low haze value of 5% or less and a low surface resistance value of 200Ω/□ or less can consequently be achieved even if the electroconductive part  152  or parts  162  have a thin film thickness of less than 300 nm or a very thin film thickness of 145 nm or less. 
     According to the present embodiment, the electroconductive part  152  or parts  162  are provided directly on the one surface  151 A of the light-transmitting resin base material  151 , that is, no hard coat layer is provided between the light-transmitting resin base material  151  and the electroconductive part  152  or parts  162 , so that excellent flexibility is achieved in the electroconductive film  150  or  160 . 
     According to the present embodiment, the electroconductive fibers  155  as a whole in the electroconductive part  152  or parts  162  are unevenly distributed on the light-transmitting base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152  or parts  162 , and the contact points between the electroconductive fibers  155  can consequently be increased. This allows ensuring electrical conduction from the surface  152 A of the electroconductive part  152  or the surfaces  162 A of the electroconductive parts  162  and thus for achieving a lower surface resistance value, even if the content of electroconductive fibers  155  is low. Additionally, a lower haze value can be achieved because the content of electroconductive fibers  155  can be reduced. Furthermore, the electroconductive fibers  155  in the electroconductive part  152  or parts  162  are unevenly distributed on the light-transmitting base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152  or parts  162 , and a majority of the electroconductive fibers  155  are consequently covered with the light-transmitting resin  154 . This allows preventing the electroconductive fibers  155  from reducing the electrical conductivity due to the reaction with sulfur, oxygen, and/or halogens in the air. 
     In the present embodiment, an organic dispersion medium is used as a dispersion medium for an electroconductive fiber-containing composition, and the electroconductive fiber-containing composition contains no resin material or, alternatively, a smaller amount of a resin material than the conventional amount of the resin material. Accordingly, in the electroconductive part  152  or parts  162 , the electroconductive fibers  155  can be unevenly distributed on the light-transmitting base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152  or parts  162 , due to the same reason as described in the first embodiment. 
     According to the present embodiment, the electroconductive part  152  is provided directly on one surface  151 A of the light-transmitting resin base material  151  by coating process; the difference in electrical resistance depending on the in-plain direction of the electroconductive part  152  can be reduced if the above-described electrical resistance value ratio is 1 or more and less than 2 in the electroconductive part  152 , due to the same reason as described in the first embodiment. In cases where the electroconductive film is used for an electrode for a touch panel sensor, limitations on the pattern of the electrode, IC chips, and partitioning are reduced with the reduced difference in electrical resistance. 
     According to the present embodiment, the electroconductive part  152  has a high electrical resistance value in the second direction and a low electrical resistance value in the first direction in cases where the above-described electrical resistance value ratio is 2 or more. Thus, the electroconductive film  10  showing a further lower electrical resistance value in a particular direction (first direction) due to the same reason as described in the first embodiment can be provided. 
     According to the present embodiment, the light-transmitting resin  154  in the electroconductive part  152  or parts  162  contains a reaction inhibitor, and can consequently inhibit the electroconductive fibers  155  from reducing the electrical conductivity due to the reaction with sulfur, oxygen, and/or halogens in the atmospheric air, on the same basis as described in the first embodiment. 
     According to the present embodiment, a maximally excellent surface resistance value can be obtained with a minimum amount of electroconductive fibers because the electroconductive fibers  155  as a whole in the electroconductive part  152  or parts  162  are unevenly distributed on the light-transmitting base material  151  side than the position HL, which is located at half the film thickness of the electroconductive part  152  or parts  162 . Additionally, the uneven distribution of the electroconductive fibers  155  as described above enables optical properties with a lower haze value. Furthermore, uneven distribution, rather than homogeneous dispersion, of electroconductive fibers  155  enables easier adjustment of the Martens hardness. Additionally, the dense presence of electroconductive fibers  155  in the light-transmitting resin  154  enables increasing the hardness of the light-transmitting resin and also enables obtaining a light-transmitting resin which is neither too hard nor too soft by devising the composition of the light-transmitting resin  154 . In addition, the light-transmitting resin having an appropriate Martens hardness could achieve excellent flexibility for folding or rolling. 
     According to the present embodiment, a reaction inhibitor contained in the electroconductive part  152  can control the reaction of the electroconductive fibers  155  with components of a light-transmitting adhesive layer due to the same reason as described in the first embodiment, even if the electroconductive part  152  or parts  162  in contact with the light-transmitting adhesive layer are tested by the humidity/heat resistance test. Accordingly, the number of light-transmitting adhesive layer choices can be increased. 
     The electroconductive films  150  and  160  have been described above; the above-described electroconductive film comprising gaps existing between electroconductive parts can likewise obtain the same effects as those of the electroconductive films  150  and  160 . 
     The application of an electroconductive film according to the present embodiment is not limited to a particular application and can be incorporated into an image display device comprising a touch panel and be used. Additionally, the electroconductive film can be used, for example, as an electromagnetic shield.  FIG.  28    depicts a schematic diagram of an image display device according to the present embodiment. In  FIG.  28   , the elements indicated by the same reference numbers as in  FIG.  13    are the same as those indicated in  FIG.  13   , and further description is thus omitted. 
     &lt;&lt;&lt;Image Display Device&gt;&gt;&gt; 
     As shown in  FIG.  28   , an image display device  170  mainly comprises a display panel  180  for displaying images, a touch panel  190  placed on the observer&#39;s side of the display panel  180 , and a light-transmitting adhesion layer  90  intervening between the display panel  180  and the touch panel  190 . In the present embodiment, the display panel  180  is an organic light-emitting diode (OLED) panel and the image display device  170  thus comprises no backlight unit but may comprise a backlight unit depending on the type of the display panel (display element). 
     &lt;&lt;Display Panel&gt;&gt; 
     The display panel  180  is an organic light-emitting diode (OLED) panel, as described above, and thus comprises an organic light-emitting diode as a display element. The display panel may be a liquid-crystal display panel, an inorganic light-emitting diode panel, or a quantum dot light-emitting diode (QLED) panel. 
     &lt;&lt;Touch Panel&gt;&gt; 
     The touch panel  190  comprises an electroconductive film  200 , an electroconductive film  160  placed on the observer&#39;s side of the electroconductive film  200 , a light-transmitting cover member  71 , such as a cover glass, placed on the observer&#39;s side of the electroconductive film  160 , a light-transmitting adhesive layer  72  intervening between the electroconductive film  200  and the electroconductive film  160 , and a light-transmitting adhesive layer  73  intervening between the electroconductive film  160  and the light-transmitting cover member  71 . 
     &lt;Electroconductive Film&gt; 
     The electroconductive film  200  has almost the same structure as that of the electroconductive film  160 . That is, the electroconductive film  200  comprises a light-transmitting resin base material  201  and electroconductive parts  203  provided directly and patterned on one surface  201 A of the light-transmitting resin base material  201 , as shown in  FIG.  28   . The electroconductive part  203  shown in  FIG.  28    is an integral part of an electroconductive layer  202 . The electroconductive layer  202  is composed of plural electroconductive parts  203  and nonconductive parts  204  located between the electroconductive parts  203 . Additionally, the electroconductive film  200  further comprises an underlayer  205  provided directly on the other surface  201 B of the light-transmitting resin base material  201 . The light-transmitting resin base material  201  and the underlayer  205  are similar to the light-transmitting resin base material  151  and the underlayer  153 , and the description is thus omitted here. 
     (Electroconductive Part and Nonconductive Part) 
     The electroconductive parts  203  have the same structure as that of the electroconductive parts  162 . That is, the electroconductive parts  203  comprise a light-transmitting resin and electroconductive fibers. The nonconductive parts  204  comprise a light-transmitting resin and contain substantially no electroconductive fibers. The electroconductive part  203  can conduct electricity from the surface of the electroconductive part  203 . Additionally, the electroconductive fibers in the electroconductive parts  203  are preferably unevenly distributed on the light-transmitting base material  201  side than the position HL, which is located at half the film thickness of the electroconductive parts  203 . The electroconductive parts  203  have the same structure as that of the electroconductive parts  162  but the electroconductive parts  203  may not need to have the same structure as that of the electroconductive parts  162 . 
     The electroconductive parts  162  of the electroconductive film  160  function as electrode lines in the X direction in a projected capacitive touch panel, while the electroconductive parts  203  of the electroconductive film  200  function as electrode lines in the Y direction in a projected capacitive touch panel and have the same top view as shown in  FIG.  14   . 
     Fourth Embodiment 
     Now, the electroconductive film, touch panel, and image display device according to the fourth embodiment of the present invention will be described below with reference to the drawings.  FIG.  29    depicts a schematic diagram of an electroconductive film according to the present embodiment;  FIG.  30    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  29   ;  FIG.  31    depicts a schematic diagram of another electroconductive film according to the present embodiment;  FIG.  32    depicts an enlarged view of a part of the electroconductive film shown in  FIG.  31   .  FIGS.  33  and  34    schematically illustrate the process for producing the electroconductive film according to the present embodiment. 
     &lt;&lt;&lt;Electroconductive Film&gt;&gt;&gt; 
     An electroconductive film  250  is light transmissive and comprises an underlayer  252  and an electroconductive part  254  in this order on one surface  251 A of a light-transmitting resin base material  251  and further comprises an underlayer  253  on the other surface  251 B, as shown in  FIG.  29   . Specifically, the electroconductive film  250  comprises a light-transmitting resin base material  251 , an underlayer  252  provided directly on one surface  251 A of the light-transmitting resin base material  251 , an underlayer  253  provided directly on the other surface  251 B of the light-transmitting resin base material  251 , and an electroconductive part  254  provided directly on the surface  252 B (hereinafter referred to as “the other surface of the underlayer”), of the underlayer  252  opposite to the light-transmitting resin base material  251  side surface  252 A (hereinafter referred to as “the one surface of the underlayer”). The surface  250 A of the electroconductive film  250  is constituted by the surface  254 A of the electroconductive part  254 . Incidentally, the electroconductive film  250  may not comprise the underlayer  253 . 
     Additionally, although the electroconductive part  254  shown in  FIG.  29    is provided only on the other surface  252 B of the underlayer  252 , an electroconductive part may additionally be provided on a surface of the underlayer  253  opposite to the light-transmitting resin base material  251  side surface. However, in cases where electroconductive parts are provided on both surfaces of the light-transmitting resin base material, an electroconductive part should be provided directly on a surface of one underlayer opposite to the light-transmitting resin base material side surface but electroconductive parts may not need to be provided directly on both surfaces of underlayers opposite to the light-transmitting resin base material side surface. 
     The electroconductive film  250  has a haze value (total haze value) of 5% or less for the same reason as described for the electroconductive film  10 . The haze value of the electroconductive film  250  can be measured by the same method as for the haze value of the electroconductive film  10 . The electroconductive film  250  has a haze value of 3% or less, 2% or less, 1.5% or less, 1.2% or less, or 1.1% or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive film  250  preferably has a total light transmittance of 80% or more for the same reason as described for the electroconductive film  10 . The total light transmittance of the electroconductive film  250  can be measured by the same method as for the total light transmittance of the electroconductive film  10 . The electroconductive film  250  has a total light transmittance of 85% or more, 88% or more, or 89% or more in ascending order of preference (a higher value is more preferred). 
     The electroconductive film  250  has flexibility. For the same reason as that described for the electroconductive film  150 , such as cracks of an electroconductive film, preferably, in cases where the electroconductive film  250  is folded at 180 degrees in a manner that leaves a gap of 3 mm between the opposite edges of the electroconductive film  10  and the process (foldability test) is repeated one hundred thousand times, the below-described ratio between the electrical resistance values measured before and after the foldability test on the surface  254 A of the electroconductive part  254  of the electroconductive film  250  is 3 or less; more preferably, the ratio between the electrical resistance values measured before and after the foldability test on the surface  254 A of the electroconductive part  254  of the electroconductive film  250  is 3 or less in cases where the foldability test is repeated two hundred thousand times; further preferably, the ratio between the electrical resistance values measured before and after the foldability test on the surface  254 A of the electroconductive part  254  of the electroconductive film  250  is 3 or less in cases where the foldability test is repeated one million times. If a hard coat layer is provided between a light-transmitting resin base material and an electroconductive part, it is highly likely that the hard coat layer is cracked by the foldability test after repeating the foldability test the number of times as specified above and the ratio of the electrical resistance value measured after the foldability test on the surface of the electroconductive part of the electroconductive film exceeds 3. In cases where the foldability test is repeated the number of times as specified above, the ratio between the electrical resistance values measured before and after the foldability test on the surface  254 A of the electroconductive part  254  of the electroconductive film  250  is more preferably 1.5 or less, regardless of whether a hard coat layer is provided or not. The foldability test may be carried out by folding the electroconductive film  250  with the electroconductive part  254  facing either inward or outward. In either case, the ratio between the electrical resistance values measured before and after the foldability test on the surface  254 A of the electroconductive part  254  of the electroconductive film  250  is preferred to be 3 or less. The electrical resistance measurement and the foldability test will be performed in the same manner as described for the electroconductive film  150 . 
     &lt;&lt;Light-Transmitting Resin Base Material&gt;&gt; 
     The light-transmitting resin base material  251  is not limited to a particular light-transmitting resin base material as long as it is a base material composed of a light-transmissive resin. Examples of the light-transmitting resin as a component of the light-transmitting resin base material  251  include the same light-transmitting resins as those described for the light-transmitting base material  11 . The thickness of the light-transmitting base material  251  is the same as that of the light-transmitting base material  11 . However, although some light-transmitting resin base materials have an underlayer for the purpose of improving adhesion to other layers, preventing the electroconductive film from sticking to itself when the electroconductive film is rolled, and/or inhibiting cissing of a coating liquid applied for forming another layer, the term “light-transmitting resin base material” in the present embodiment will be used to refer to a light-transmitting resin base material without an underlayer. The light-transmitting resin base material  251  may have a surface treated by a physical treatment such as corona discharge treatment or oxidation treatment to improve the adhesiveness. 
     &lt;&lt;Underlayer&gt;&gt; 
     The underlayers  252  and  253  are layers for the purpose of improving adhesion to other layers, preventing the electroconductive film from sticking to itself when the electroconductive film is rolled, and/or inhibiting cissing of a coating liquid applied for forming another layer. The underlayer  252  is provided directly on one surface  251 A of the light-transmitting resin base material  251 , while the underlayer  253  is provided directly on the other surface  251 B of the light-transmitting resin base material  251 . The phrase “provided directly on” in this context means that the underlayer is in direct contact with one surface or the other surface of the light-transmitting resin base material. That is, no other layers are provided between the light-transmitting resin base material  251  and the underlayer  252  or  253 . The determination of whether or not an underlayer is provided directly on one surface or the other surface of a light-transmitting resin base material, or whether or not another layer is provided between a light-transmitting resin base material and an underlayer can be achieved by observing a cross-section near the interface between the light-transmitting resin base material and the electroconductive part using a scanning electron microscope (SEM), a scanning transmission electron microscope (STEM), or a transmission electron microscope (TEM) at a magnification of 1,000 to 500,000 times. The underlayer may contain particles as, for example, lubricant additives for the purpose of preventing an electroconductive film from sticking to itself when the electroconductive film is rolled; accordingly, the layer between the light-transmitting resin base material and the electroconductive part can be identified as an underlayer by the presence of the particles in the layer. As the electron microscopy conditions for the measurement in this case, the conditions for measuring the film thickness of, for example, the electroconductive part  13  can be used. 
     The underlayer  252  preferably contains substantially none of the below-described electroconductive fibers  256 . The phrase “the underlayer contains substantially no electroconductive fiber” in this context means that the underlayer may contain a small amount of electroconductive fibers as long as the electroconductive part exhibits a surface resistance value of up to 1000Ω/□ or less. The underlayer  252  more preferably contains none of the electroconductive fibers  16 . The determination of whether or not the underlayer  252  contains electroconductive fibers  256  can be achieved by observing a cross-section near the interface between the underlayer and the electroconductive part using a scanning electron microscope (SEM), a scanning transmission electron microscope (STEM), or a transmission electron microscope (TEM) at a magnification of 1,000 to 500,000 times. To achieve substantially no electroconductive fibers  256  in the underlayer  252 , a dispersion medium that rarely infiltrates into the underlayer  252  can be used as a dispersion medium in the below-described electroconductive fiber-containing composition. As the electron microscopy conditions for the measurement in this case, the conditions for measuring the film thickness of, for example, the electroconductive part  13  can be used. 
     The underlayers  252  and  253  contain, for example, an anchoring agent and/or a priming agent. The anchoring agent and the priming agent are the same as those described for the underlayer, and further description is thus omitted here. 
     The underlayers  252  and  253  may contain particles of a lubricant or the like for the purpose of preventing the electroconductive film from sticking to itself when the electroconductive film is rolled, as described above. Examples of the particles include silica particles. 
     The underlayers  252  and  253  preferably have a film thickness of 10 nm or more and 1 μm or less for the same reason as described for the underlayer  153 . Additionally, film thicknesses of the underlayers  252  and  253  will be measured by the same method as for the film thickness of the underlayer  153 . The underlayers  252  and  253  each more preferably have a minimum film thickness of 30 nm or more and a maximum film thickness of 150 nm or less. 
     &lt;&lt;Electroconductive Part&gt;&gt; 
     The electroconductive part  254  is provided directly on the underlayer  252 . The phrase “provided directly on” in this context means that the electroconductive part is in direct contact with the underlayer. That is, no other layer is provided between the underlayer  252  and the electroconductive part  254 . The determination of whether or not an electroconductive part is provided directly on an underlayer, or whether or not any other layer is provided between an underlayer and an electroconductive part can be achieved by observing a cross-section near the interface between the underlayer and the electroconductive part using a scanning electron microscope (SEM), a scanning transmission electron microscope (STEM), or a transmission electron microscope (TEM) at a magnification of 1,000 to 500,000 times. As the electron microscopy conditions for the measurement in this case, the conditions for measuring the film thickness of, for example, the electroconductive part  13  can be used. 
     The electroconductive part  254  comprises a light-transmitting resin  255  and plural electroconductive fibers  256  incorporated in the light-transmitting resin  255 , as shown in  FIG.  30   . The electroconductive part  254  preferably further comprises a reaction inhibitor which is contained in the light-transmitting resin  15 . 
     The electroconductive part  254  can conduct electricity from the surface  254 A. Measurement of the surface resistance of the electroconductive part  254  can determine, as in the case of the electroconductive part  13 , whether or not the electroconductive part  254  can conduct electricity from the surface  254 A of the electroconductive part  254 . The method of measuring the surface resistance of the electroconductive part  254  and the criteria to evaluate whether or not the electroconductive part  254  can conduct electricity from the surface  254 A of the electroconductive part  254  are the same as those described for the electroconductive part  13 , and the description of the measurement method and the evaluation criteria is thus omitted here. Although a majority of the electroconductive fibers  256  are distributed on the light-transmitting resin base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254 , as described below, the remaining electroconductive fibers  256  are stacked on the electroconductive fibers  256  which are distributed on the light-transmitting resin base material  251  side, and consequently distributed on the surface  254  side than the position HL, which is located at half the film thickness of the electroconductive part  254 , and also located on the surface  254 A of the electroconductive part  254 . Thus, the electroconductive part  254  can conduct electricity from the surface  254 A. 
     In the electroconductive part  254 , the electroconductive fibers  256  are preferably unevenly distributed on the light-transmitting base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254 , as shown in  FIG.  30   . The determination of whether or not the electroconductive fibers  256  are unevenly distributed on the light-transmitting base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254 , is achieved by the evaluation method described for the electroconductive part  13 , and the description of the method is omitted here. The existence ratio of electroconductive fibers distributed from the position located at half the film thickness of the electroconductive part to the light-transmitting base material, which is determined from cross-sectional images acquired using a scanning transmission electron microscope (STEM) or a transmission electron microscope (TEM), is preferably 70% or more, more preferably 80% or more. 
     The surface resistance of the electroconductive part  254  is 200Ω/□ or less for the same reason as described for the electroconductive part  13 . The surface resistance of the electroconductive part  254  is a surface resistance value measured on the surface  254 A of the electroconductive part  254 . The surface resistance of the electroconductive part  254  can be measured by the same method as for the surface resistance of the electroconductive part  13 . The minimum surface resistance value of the electroconductive part  254  is 1Ω/□ or more, 5Ω/□ or more, or 10Ω/□ or more in ascending order of preference (a higher value is more preferred), while the maximum surface resistance value of the electroconductive part  254  is 100Ω/□ or less, 70Ω/□ or less, 60Ω/□ or less, or 50Ω/□ or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive part  254  preferably has a film thickness of less than 300 nm from the viewpoint of thinning the electroconductive film. The maximum film thickness of the electroconductive part  254  is 145 nm or less, 140 nm or less, 120 nm or less, 110 nm or less, 80 nm or less, or 50 nm or less in ascending order of preference (a lower value is more preferred). Additionally, the minimum film thickness of the electroconductive part  254  is preferably 10 nm or more for the same reason as described for the electroconductive part  13 . The film thickness of the electroconductive part  254  can be measured by the same method as for the film thickness of the electroconductive part  13 . 
     The electroconductive part  254  preferably has a Martens hardness of 970 N/mm 2  or more and 1050 N/mm 2  or less at an indentation amount of 10 nm from the surface  254 A for the same reason as described for the electroconductive part  13 . In the electroconductive part  254 , the minimum Martens hardness at the above-described indentation amount of 10 nm is 980 N/mm 2  or more, 1000 N/mm 2  or more, or 1015 N/mm 2  or more in ascending order of preference (a higher value is more preferred); the maximum Martens hardness at the above-described indentation amount of 10 nm is 1040 N/mm 2  or less, 1030 N/mm 2  or less, or 1020 N/mm 2  or less in ascending order of preference (a lower value is more preferred). 
     The electroconductive part  254  preferably has a Martens hardness of 130 N/mm 2  or more and 300 N/mm 2  or less at an indentation amount of 100 nm from the surface  254 A for the same reason as described for the electroconductive part  13 . In the electroconductive part  254 , the minimum Martens hardness at the above-described indentation amount of 100 nm is 140 N/mm 2  or more, 150 N/mm 2  or more, or 170 N/mm 2  or more in ascending order of preference (a higher value is more preferred); the maximum Martens hardness at the above-described indentation amount of 100 nm is 280 N/mm 2  or less, 250 N/mm 2  or less, or 200 N/mm 2  or less in ascending order of preference (a lower value is more preferred). 
     In cases where the electroconductive film  250  is used as an electrode for a touch panel sensor, the ratio of the electrical resistance value in the second direction to that in the first direction (the ratio is hereinafter referred to as “electrical resistance value ratio”) is preferably 1 or more and less than 2 when the electrical resistance values are measured in a predetermined size in six different directions including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface  254 A of the electroconductive part  254 , wherein a direction in which the electroconductive part shows the lowest electrical resistance value is designated as the first direction, and a direction which is orthogonal to the first direction is designated as the second direction. The electrical resistance value ratio can be determined by a method similar to the electric resistance measurement method described for the electroconductive part  13 . The maximum electrical resistance value ratio is 1.8 or less, 1.5 or less, 1.3 or less in ascending order of preference (a lower value is more preferred). 
     On the other hand, in cases of obtaining an electroconductive film which provides a much lower electrical resistance value in a particular direction, the above-described electrical resistance value ratio is preferably 2 or more when the electrical resistance values are measured in a predetermined size in six different including an arbitrary direction for each an angle of 30 degrees to the arbitrary direction in the surface  254 A of the electroconductive part  254 . The arithmetic mean of three measurements is determined as the electrical resistance value ratio. The minimum electrical resistance value ratio is more preferably 3 or more. The maximum electrical resistance value ratio is 10 or less, or 8 or less in ascending order of preference (a lower value is more preferred) from the viewpoint of obtaining a uniform resistance value on the surface. 
     Such an electroconductive part having an electrical resistance value ratio of 1 or more and less than 2 or an electrical resistance value ratio of 2 or more can be obtained, for example, by appropriately modifying the fiber length of electroconductive fibers, the type or film thickness of a resin that constitutes the below-described organic protective layer, and/or the temperature for drying the electroconductive fiber-containing composition. 
     &lt;Light-Transmitting Resin&gt; 
     The light-transmitting resin  255  covers electroconductive fibers  256 , similarly to the light-transmitting resin  15 , to prevent removal of the electroconductive fibers  256  from the electroconductive part  254  and to improve the durability or abrasion resistance of the electroconductive part  254 , and, also in the present embodiment, covers electroconductive fibers  256  to such an extent that the electroconductive part  254  can conduct electricity from the surface  254 A. 
     The light-transmitting resin  255  is the same as the light-transmitting resin  15 . Thus, the film thickness and constituent materials of the light-transmitting resin  255  are also the same as those of the light-transmitting resin  15 . The light-transmitting resin  255  is similar to the light-transmitting resin  15 , and the description is thus omitted here. 
     &lt;Reaction Inhibitor&gt; 
     A reaction inhibitor is a substance that prevents reduction in electrical conductivity after application of the light-transmitting resin composition due to the reaction of the electroconductive fibers  256  with substances in the atmosphere. The reaction inhibitor and the content of the reaction inhibitor are the same as those described in the first embodiment, and the description of the reaction inhibitor and the content is thus omitted here. 
     &lt;Electroconductive Fibers&gt; 
     In cases where the electroconductive fibers  256  are unevenly distributed on the light-transmitting base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254 , the electroconductive fibers  256  contact with each other in the thickness direction of the electroconductive part  254 , as indicated by the ability of the electroconductive part  254  to conduct electricity from the surface  254 A. 
     The electroconductive fibers  256  preferably contact with each other in the surface direction (two-dimensional direction) of the electroconductive part  254  to form a network structure (meshwork) in the light-transmitting resin base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254 . Formation of a network structure by the electroconductive fibers  256  enables efficient creation of a conductive path with the electroconductive fibers  256  even in a small amount. 
     Some of the electroconductive fibers  256  are preferably exposed on the surface  254 A of the electroconductive part  254 . Once electrical conduction from the surface  254 A of the electroconductive part  254  is identified by the above-described measurement method, some of the electroconductive fibers  256  can thus be determined to be exposed on the surface  254 A of the electroconductive part  254 . 
     The electroconductive fibers  256  preferably have a fiber diameter of 200 nm or less for the same reason as described for the electroconductive fibers  16 . The minimum fiber diameter of the electroconductive fibers  256  is more preferably 10 nm or more from the viewpoint of the electroconductive of the electroconductive part  13 , and a more preferred range of fiber diameter in the electroconductive fibers  256  is 15 nm or more and 180 nm or less. The fiber diameter of the electroconductive fibers  256  can be obtained by the same method as for the fiber diameter of the electroconductive fibers  16 . 
     The electroconductive fibers  256  preferably have a fiber length of 1 μm or more for the same reason as described for the electroconductive fibers  16 . The maximum fiber length of the electroconductive fibers  256  may be 500 μm or less, 300 μm or less, or 30 μm or less, while the minimum fiber length of the electroconductive fibers  256  may be 3 μm or more, or 10 μm or more. The fiber length of the electroconductive fibers  256  can be obtained by the same method as for the fiber length of the electroconductive fibers  16 . 
     Similarly to the electroconductive fibers  16 , the electroconductive fibers  256  preferably have a fiber length of, for example, 1 μm or more and less than 30 μm in cases of obtaining an electroconductive part having an electrical resistance value ratio of 1 or more and less than 2, while the electroconductive fibers  256  preferably have a fiber length of, for example, 30 μm or more in cases of obtaining an electroconductive part having an electrical resistance value ratio of 2 or more. In cases of obtaining an electroconductive part having an electrical resistance value ratio of 1 or more and less than 2, the electroconductive fibers  256  preferably have a minimum fiber length of 10 μm or more and a maximum fiber length of 20 μm or less from the viewpoint of obtaining a low surface resistance value. 
     The constituent fibers of the electroconductive fibers  256  are the same as those of the electroconductive fibers  16 , and the description of the constituent fibers is thus omitted here. 
     &lt;&lt;Other Electroconductive Films&gt;&gt; 
     For the electroconductive film shown in  FIG.  29   , the electroconductive part  254  is a film with no pattern, namely a so-called plain film, but the electroconductive part may be patterned depending on applications. Specifically, the electroconductive film may be an electroconductive film  260 , as shown in  FIG.  31   , comprising an electroconductive layer  261  which is composed of plural electroconductive parts  262  and plural nonconductive parts  263  located between the electroconductive parts  262 , or an electroconductive film comprising, as shown in  FIG.  4   , plural electroconductive parts and plural gaps existing between the electroconductive parts. The surface  260 A of the electroconductive film  260  comprises the surfaces  262 A of the electroconductive parts  262  and the surfaces  263 A of the nonconductive parts  263 , while the surface of the electroconductive film having gaps existing between electroconductive parts comprises the surfaces of the electroconductive parts and one surface of the light-transmitting resin base material. For example, the physical property values of the electroconductive film  260  and the electroconductive film having gaps existing between electroconductive parts are similar to those of the electroconductive film  250 . In  FIG.  31   , the elements indicated by the same reference numbers as in  FIG.  29    are the same as those indicated in  FIG.  29   , and further description is thus omitted. 
     &lt;Electroconductive Part&gt; 
     The electroconductive parts  262  are the same as the electroconductive part  254 , except that the former electroconductive parts are patterned. That is, the electroconductive parts  262  are provided directly on the other surface  252 B of the underlayer  252 . Additionally, the electroconductive parts  262  comprise a light-transmitting resin  255  and plural electroconductive fibers  256  incorporated in the light-transmitting resin  255 , as shown in  FIG.  32   . The electroconductive parts  262  can conduct electricity from the surfaces  262 A. In the electroconductive parts  262 , the electroconductive fibers  256  are preferably unevenly distributed on the light-transmitting base material  251  side than the position HL, which is located at half the film thickness of the electroconductive parts  262 , as shown in  FIG.  32   . Other configurations, materials, physical properties values, and the like of the electroconductive parts  262  are also the same as those of the electroconductive part  254 , and further description is thus omitted here. 
     &lt;Nonconductive Part&gt; 
     The nonconductive parts  263  are parts located between electroconductive parts  262  and having no electrical conductivity. As shown in  FIG.  32   , the nonconductive parts  263  contain substantially no electroconductive fibers  256 . 
     Because the nonconductive parts  263  are prepared together with the electroconductive parts  262  as an integrated body, the film thickness of the nonconductive parts is less than 300 nm. The maximum film thickness of the nonconductive parts  263  is 145 nm or less, 140 nm or less, 120 nm or less, 110 nm or less, 80 nm or less, or 50 nm or less in ascending order of preference (a lower value is more preferred). Additionally, the minimum film thickness of the nonconductive parts  263  is preferably 10 nm or more. The film thickness of the nonconductive parts  263  will be measured by the same method as for the film thickness of the electroconductive part  13 . 
     As shown in  FIG.  32   , the nonconductive parts  263  comprise the light-transmitting resin  255 . The nonconductive parts  263  may be formed by removing electroconductive fibers  256  through sublimation and may have the resulting voids  263 B which are not filled with electroconductive fibers. In that case, the sublimated electroconductive fibers  256  burst out through areas to be the nonconductive parts  23  during the preparation of the nonconductive parts  263  and the resulting nonconductive parts  263  have rough surfaces  263 A. The light-transmitting resin  255  in the nonconductive parts  263  is the same as the light-transmitting resin  255  in the electroconductive part  254 , and the description is thus omitted here. 
     &lt;&lt;Production Methods of Electroconductive Films&gt;&gt; 
     The electroconductive film  250  can be produced, for example, as follows. As shown in  FIG.  33 (A) , a light-transmitting resin base material  251  carrying an underlayer  252  on one surface  251 A and an underlayer  253  on the other surface  251 B is first formed. Incidentally, a light-transmitting resin base material carrying an underlayer on one surface but not on the other surface may alternatively be prepared. 
     Next, an electroconductive fiber-containing composition containing electroconductive fibers  256  and a dispersion medium is applied directly on the other surface  252 B of the underlayer  252 , and dried to place a plurality of the electroconductive fibers  256  directly on the other surface  252 B of the underlayer  252 , as shown in  FIG.  33 (B) . The electroconductive fiber-containing composition is the same as that used in the first embodiment, and the description of the electroconductive fiber-containing composition is thus omitted here. 
     After a plurality of the electroconductive fibers  256  are placed directly on the other surface  252 B of the underlayer  252 , a light-transmitting resin composition containing a polymerizable compound and a solvent is applied on it and dried to prepare a coating film  257  of the light-transmitting resin composition, as shown in  FIG.  33 (C) . The light-transmitting resin composition is the same as that used in the first embodiment, and the description of the light-transmitting resin composition is thus omitted here. 
     Next, the coating film  257  is exposed to ionizing radiation such as ultraviolet light, as shown in  FIG.  34 (A) , to polymerize (cross-link) the polymerizable compound and to cure the coating film  257 , whereby the light-transmitting resin  255  is prepared. 
     Because the electroconductive part  254  of the electroconductive film  250  shown in  FIG.  29    is a plain film, the electroconductive film  250  is obtained in the above-described process. The electroconductive film  260  shown in  FIG.  31    is patterned and can be obtained similarly to the first embodiment, for example, by irradiating laser light (for example, infrared laser) to areas to be the nonconductive parts  263  for the generation of patterns of the electroconductive parts  262 , as shown in  FIG.  34 (B) . 
     According to the present embodiment, the underlayer  252  is provided directly on one surface  251 A of the light-transmitting resin base material  251  and the electroconductive part  254  or parts  262  are provided directly on the other surface  252 B of the underlayer  252 . That is, no hard coat layers are provided both between the light-transmitting resin base material  251  and the underlayer  252  and between the underlayer  252  and the electroconductive part  254  or parts  262 . Consequently, excellent flexibility is achieved in the resulting electroconductive film. Additionally, the electroconductive part  254  or parts  262  are provided directly on the other surface  252 B of the underlayer  252  and the resulting laminate demonstrates stronger interlayer adhesion and is less prone to delamination, as compared to an electroconductive part provided directly on a light-transmitting base material. Thus, even if electric wirings are formed on the surface  254 A of the electroconductive part  254  or the surfaces  262 A of the electroconductive parts  262  by using various electroconductive pastes (for example, silver paste), the electric wirings would be less prone to be peeled off from the surface  254 A of the electroconductive part  254  or the surfaces  262 A of the electroconductive parts  262 . Accordingly, the number of electroconductive paste choices can be increased. Examples of the silver paste include DW-520H-14, DW-520H-18, and DW-520H-19 manufactured by Toyobo Co., Ltd.; and PA-LTP-AW03 manufactured by Phoenix Materials Co., Ltd. 
     According to the present embodiment, the contact points between the electroconductive fibers  256  can be increased in cases where the electroconductive fibers  256  as a whole in the electroconductive part  254  or parts  262  are unevenly distributed on the light-transmitting base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254  or parts  262 . This allows ensuring electrical conduction from the surface  254 A of the electroconductive part  254  or the surfaces  262 A of the electroconductive parts  262  and thus for achieving a low haze value of 5% or less, even if the content of electroconductive fibers  256  is low. Additionally, formation of the electroconductive part or parts on the surface of the underlayer results in incorporation of the electroconductive fibers  256  into the underlayer and consequently tends to induce the increase of surface resistance value but can reduce the content of the electroconductive fibers and consequently achieve a lower surface resistance value. 
     In a thin electroconductive part, the amount of electroconductive fibers is accordingly reduced and the electroconductive part is thus prone to increase the surface resistance value. According to the present embodiment, the contact points between the electroconductive fibers  256  are increased in cases where the electroconductive fibers  256  as a whole in the electroconductive part  254  or parts  262  are unevenly distributed on the light-transmitting base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254  or parts  262 , and a low haze value of 5% or less and a low surface resistance value of 200Ω/□ or less can consequently be achieved even if the electroconductive part  254  or parts  262  have a thin film thickness of less than 300 nm or a very thin film thickness of 145 nm or less. 
     According to the present embodiment, the electroconductive fibers  256  in the electroconductive part  254  or parts  262  are unevenly distributed on the light-transmitting base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254  or parts  262 , and a majority of the electroconductive fibers  256  are consequently covered with the light-transmitting resin  255 . This allows preventing the electroconductive fibers  256  from reducing the electrical conductivity due to the reaction with sulfur, oxygen, and/or halogens in the air. 
     According to the present embodiment, the electroconductive fibers  256  in the electroconductive part  254  or parts  262  are unevenly distributed on the light-transmitting base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254  or parts  262 , and a maximally excellent surface resistance value can consequently be obtained with a minimum amount of electroconductive fibers. Additionally, the uneven distribution of the electroconductive fibers  256  as described above enables optical properties with a lower haze value. Furthermore, uneven distribution, rather than homogeneous dispersion, of electroconductive fibers  256  enables easier adjustment of the Martens hardness. Additionally, the dense presence of electroconductive fibers  256  in the light-transmitting resin  254  enables increasing the hardness of the light-transmitting resin and also enables obtaining a light-transmitting resin which is neither too hard nor too soft by devising the composition of the light-transmitting resin  254 . In addition, the light-transmitting resin having an appropriate Martens hardness could achieve excellent flexibility for folding or rolling. 
     In the present embodiment, an organic dispersion medium is used as a dispersion medium for an electroconductive fiber-containing composition, and the electroconductive fiber-containing composition contains no resin material or, alternatively, a smaller amount of a resin material than the conventional amount of the resin material. Accordingly, in the electroconductive part  254  or parts  262 , the electroconductive fibers  256  can be unevenly distributed on the light-transmitting base material  251  side than the position HL, which is located at half the film thickness of the electroconductive part  254  or parts  262 , due to the same reason as described in the first embodiment. 
     According to the present embodiment, the electroconductive part  254  is provided directly on the other surface  252 B of the underlayer  252  by coating process; the difference in electrical resistance value depending on the in-plain direction of the electroconductive part  254  can be reduced if the above-described electrical resistance value ratio is 1 or more and less than 2 in the electroconductive part  254 , due to the same reason as described in the first embodiment. In cases where the electroconductive film is used for an electrode for a touch panel sensor, limitations on the pattern of the electrode, IC chips, and partitioning are reduced with the reduced difference in electrical resistance. 
     According to the present embodiment, the electroconductive part  254  has a high electrical resistance value in the second direction and a low electrical resistance value in the first direction in cases where the above-described electrical resistance value ratio is 2 or more. Thus, the electroconductive film  250  showing a further lower electrical resistance value in a particular direction (first direction) due to the same reason as described in the first embodiment can be provided. 
     According to the present embodiment, the light-transmitting resin  255  in the electroconductive part  254  or parts  262  contains a reaction inhibitor, and can consequently prevent the electroconductive fibers  256  from reducing the electrical conductivity due to the reaction with sulfur, oxygen, and/or halogens in the atmospheric air, on the same basis as described in the first embodiment. 
     According to the present embodiment, a reaction inhibitor contained in the electroconductive part  254  can control the reaction of the electroconductive fibers  256  with components of a light-transmitting adhesive layer due to the same reason as described in the first embodiment, even if the electroconductive part  254  or parts  262  in contact with the light-transmitting adhesive layer are tested by the humidity/heat resistance test. Accordingly, the number of light-transmitting adhesive layer choices can be increased. 
     The electroconductive films  250  and  260  have been described above; the above-described electroconductive film comprising gaps existing between electroconductive parts can likewise obtain the same effects as those of the electroconductive films  250  and  260 . 
     The application of an electroconductive film according to the present embodiment is not limited to a particular application and can be incorporated into an image display device comprising a touch panel and be used. Additionally, the electroconductive film can be used, for example, as an electromagnetic shield.  FIG.  35    depicts a schematic diagram of an image display device according to the present embodiment. In  FIG.  35   , the elements indicated by the same reference numbers as in  FIG.  28    are the same as those indicated in  FIG.  28   , and further description is thus omitted. 
     &lt;&lt;&lt;Image Display Device&gt;&gt;&gt; 
     As shown in  FIG.  35   , an image display device  270  mainly comprises a display panel  180  for displaying images, a touch panel  280  placed on the observer&#39;s side of the display panel  180 , and a light-transmitting adhesion layer  90  intervening between the display panel  180  and the touch panel  280 . 
     &lt;&lt;Touch Panel&gt;&gt; 
     The touch panel  280  comprises an electroconductive film  290 , an electroconductive film  260  placed on the observer&#39;s side of the electroconductive film  290 , a light-transmitting cover member  71 , such as a cover glass, placed on the observer&#39;s side of the electroconductive film  260 , a light-transmitting adhesive layer  72  intervening between the electroconductive film  290  and the electroconductive film  260 , and a light-transmitting adhesive layer  73  intervening between the electroconductive film  260  and the light-transmitting cover member  71 . 
     &lt;Electroconductive Film&gt; 
     The electroconductive film  290  has almost the same structure as that of the electroconductive film  260 . That is, the electroconductive film  290  comprises a light-transmitting resin base material  291 , an underlayer  292  provided directly on one surface  291 A of the light-transmitting resin base material  291 , an underlayer  293  provided directly on the other surface  291 B of the light-transmitting resin base material  291 , and electroconductive parts  295  provided directly and patterned on the surface  292 B of the underlayer  292  opposite to the light-transmitting resin base material  291  side surface  292 A, as shown in  FIG.  35   . The electroconductive parts  295  shown in  FIG.  35    are an integral part of an electroconductive layer  294 . The electroconductive layer  294  is composed of plural electroconductive parts  295  and nonconductive parts  296  located between the electroconductive parts  295 . The light-transmitting resin base material  291  and the underlayers  292  and  293  are similar to the light-transmitting resin base material  251  and the underlayers  252  and  253 , and the description is omitted here. 
     (Electroconductive Part and Nonconductive Part) 
     The electroconductive parts  295  have the same structure as that of the electroconductive parts  262 . That is, the electroconductive parts  295  comprise a light-transmitting resin and electroconductive fibers. The nonconductive parts  296  comprise a light-transmitting resin and contain substantially no electroconductive fibers. The electroconductive parts  295  can conduct electricity from the surfaces  295 A of the electroconductive parts  295 . Additionally, the electroconductive fibers in the electroconductive parts  295  are preferably unevenly distributed on the light-transmitting base material  291  side than the position HL, which is located at half the film thickness of the electroconductive parts  295 . The electroconductive parts  295  have the same structure as that of the electroconductive parts  262  but the electroconductive parts  295  may not need to have the same structure as that of the electroconductive parts  262 . 
     The electroconductive parts  262  of the electroconductive film  260  function as electrode lines in the X direction in a projected capacitive touch panel, while the electroconductive parts  295  of the electroconductive film  290  function as electrode lines in the Y direction in a projected capacitive touch panel and have the same top view as shown in  FIG.  13   . 
     EXAMPLES 
     Now, the present invention will be described in more detail by way of examples. However, the present invention is not limited to those examples. 
     &lt;Preparation of a Hard Coat Layer Composition&gt; 
     First, the following components were combined to meet the composition requirements indicated below and thereby obtain a hard coat layer composition 1. 
     (Hard Coat Layer Composition 1) 
     
         
         
           
             A mixture of pentaerythritol triacrylate and pentaerythritol tetraacrylate (product name “KAYARAD PET-30”; manufactured by Nippon Kayaku Co., Ltd.): 30 parts by mass; 
             A polymerization initiator (product name “Irgacure 184”; manufactured by BASF Japan Ltd.): 1.5 parts by mass; 
             Methyl ethyl ketone (MEK): 50 parts by mass; 
             Cyclohexanone: 18.5 parts by mass.
 
&lt;Preparation of Silver Nanowire-Containing Compositions&gt;
 
(Silver Nanowire-Containing Composition 1)
 
           
         
       
    
     Ethylene glycol (EG) as a reducing agent and polyvinylpyrrolidone (PVP; having an average molecular weight of 1,300,000; manufactured by Aldrich) as a shape controlling and protecting colloid agent were used to perform the following individual steps of core formation and particle growth to prepare a silver nanowire-containing composition. 
     1. Core Formation Step 
     To 100 mL of EG maintained at a temperature of 160° C. in a reaction vessel, 2.0 mL of a silver nitrate solution in EG (having a silver nitrate concentration of 1.0 mol/L) was added at a constant rate with stirring over one minute. Then, silver core particles were prepared by reducing silver ions while the temperature was maintained at 160° C. for 10 minutes. The reaction liquid was yellow in color due to the surface plasmon absorption in nano-sized silver particles, confirming the reduction of silver ions and the subsequent formation of silver microparticles (core particles). Then, 10.0 mL of a PVP solution in EG (having a PVP concentration of 3.0×10 −1  mol/L) was added to the reaction liquid at a constant rate over 10 minutes. 
     2. Particle Growth Step 
     After the above-described core formation step was completed, the reaction liquid containing the core particles was maintained at a temperature of 160° C. with stirring, to which 100 mL of a silver nitrate solution in EG (having a silver nitrate concentration of 1.0×10 −1  mol/L) and 100 mL of a PVP solution in EG (having a PVP concentration of 3.0×10 −1  mol/L) were added at a constant rate over 120 minutes by using the double-jet technique. In the course of the particle growth step, an aliquot was withdrawn every 30 minutes from the reaction liquid to perform electron microscopic observation. The observation indicated that the core particles formed in the core formation step grew into the shape of wires with the passage of time but no microparticles were generated during the particle growth step. Measurement of fiber diameter and fiber length in finally obtained silver nanowires indicated that the silver nanowires had a fiber diameter of 30 nm and a fiber length of 15 μm. 
     3. Desalting/Washing Step 
     After completion of the particle growth step, the reaction liquid was cooled down to room temperature and then applied to an ultrafiltration membrane with a molecular weight cut-off of 0.2 μm for desalting/washing and for solvent exchange to ethanol. Subsequently, the reaction liquid was concentrated to a volume of 100 mL to obtain a dispersion of silver nanowires. Finally, the concentrated reaction liquid was diluted with ethanol to achieve a silver nanowire concentration of 0.1% by mass, whereby the silver nanowire-containing composition 1 was obtained. 
     Measurement of fiber diameter and fiber length in silver nanowires in the silver nanowire-containing composition 1 indicated that the silver nanowires had a fiber diameter of 30 nm and a fiber length of 15 μm. The fiber diameter of the silver nanowires was obtained as the arithmetic mean of the fiber diameters of 100 electroconductive fibers in 50 images photographed at a magnification of 100,000 to 200,000 times using a transmission electron microscope (TEM) (product name “H-7650”; manufactured by Hitachi High-Technologies Corporation), which were measured on the photographed images by a software program accessory to the TEM. The above-described fiber diameters were measured by setting the accelerating voltage to “100 kV,” the emission current to “10 μA,” the condenser lens aperture to “1,” the objective lens aperture to “0,” the observation mode to “HC,” and the Spot to “2.” Additionally, the fiber length of the silver nanowires was obtained as the arithmetic mean of the fiber lengths of 100 silver nanowires measured using a scanning electron microscope (SEM) (product name “S-4800 (Type 2)”; manufactured by Hitachi High-Technologies Corporation) at a magnification of 500 to 20,000,000 times. The above-described fiber lengths were measured by setting the signal selection to “SE,” the accelerating voltage to “3 kV,” the emission current to “10 μA,” and the SE detector to “Mixed.” The fiber length of the silver nanowires was obtained as the arithmetic mean of the fiber lengths of 100 silver nanowires in 10 images acquired at a magnification of 500 to 20,000,000 times using a scanning electron microscope (SEM) (product name “S-4800 (Type 2)”; manufactured by Hitachi High-Technologies Corporation) on the SEM mode, which were measured on the acquired images by an accessory software program. The above-described fiber length were measured using a 45° pre-tilted sample table by setting the signal selection to “SE,” the accelerating voltage to “3 kV,” the emission current to “10 μA to 20 μA,” the SE detector to “Mixed,” the probe current to “Norm,” the focus mode to “UHR,” the condenser lens  1  to “5.0,” the WD to “8 mm,” and the Tilt to “30°.” The TE detector was removed from the microscope system prior to the observation. When the fiber diameter of the silver nanowires was determined, a measurement sample prepared by the following method was used. First, the silver nanowire-containing composition 1 was diluted with ethanol depending on the type of the dispersion medium in the composition to reduce the concentration of silver nanowires to 0.05% by mass or less. Furthermore, a drop of the diluted silver nanowire-containing composition 1 was applied on a carbon-coated grid mesh for TEM or STEM observation (a Cu grid with the model “#10-1012, Elastic Carbon Film ELS-C10 in the STEM Cu100P grid specification”), dried at room temperature, and then observed under the above-described conditions, and the resulting observation image data was used to calculate the arithmetic mean. When the fiber length of the silver nanowire was determined, a measurement sample prepared by the following method was used. First, the silver nanowire-containing composition 1 was applied on an untreated surface of a polyethylene terephthalate (PET) film in B5 size having a thickness of 50 μm at an application dose of 10 mg/m 2 , and dried to evaporate the dispersion medium and to place electroconductive fibers on the surface of the PET film, and an electroconductive film was thereby prepared. A piece having a size of 10 mm×10 mm was cut from the central part of the electroconductive film. Then, the excised electroconductive film was attached flat against the tilted surface of a 45° pre-tilted SEM sample table (model number “728-45”; manufactured by Nissin EM Co., Ltd.; 45° pre-tilted sample table; 15 mm diameter×10 mm; made of M4 aluminum) using a silver paste. Furthermore, the cut electroconductive film was sputtered with Pt—Pd for 20 to 30 seconds to obtain electrical conductivity. The fiber diameters and fiber lengths of the below-described silver nanowires were determined in the same manner. 
     (Silver Nanowire-Containing Composition 2) 
     The silver nanowire-containing composition 2 was obtained in the same manner as the silver nanowire-containing composition 1, except that the silver nanowire dispersion liquid was supplemented with 0.1 parts by mass of the mixture of pentaerythritol triacrylate and pentaerythritol tetraacrylate (product name “KAYARAD PET-30”; manufactured by Nippon Kayaku Co., Ltd.) and 0.005 parts by mass of polymerization initiator (product name “Irgacure 184”; manufactured by BASF SE) and diluted with ethanol to achieve a silver nanowire concentration of 0.1% by mass. 
     (Silver Nanowire-Containing Composition 3) 
     The silver nanowire-containing composition 3 was obtained in the same manner as the silver nanowire-containing composition 1, except that the silver nanowire dispersion liquid was diluted with ethanol to achieve a silver nanowire concentration of 0.2% by mass. 
     (Silver Nanowire-Containing Composition 4) 
     The silver nanowire-containing composition 4 was obtained in the same manner as the silver nanowire-containing composition 2, except that the silver nanowire dispersion liquid was diluted with ethanol to achieve a silver nanowire concentration of 0.2% by mass. 
     (Silver Nanowire-Containing Composition 5) 
     The silver nanowire-containing composition 5 was obtained in the same manner as the silver nanowire-containing composition 1, except that the reaction time in the particle growth step was prolonged to obtain silver nanowires having a fiber length of 40 μm. 
     (Silver Nanowire-Containing Composition 6) 
     The silver nanowire-containing composition 6 having a silver nanowire concentration of 0.1% by mass was obtained in the same manner as the silver nanowire-containing composition 1, except that the silver nanowire dispersion liquid was supplemented with 1 part by mass of the mixture of pentaerythritol triacrylate and pentaerythritol tetraacrylate (product name “KAYARAD PET-30”; manufactured by Nippon Kayaku Co., Ltd.) and 0.05 parts by mass of polymerization initiator (product name “Irgacure 184”; manufactured by BASF SE). 
     (Silver Nanowire-Containing Composition 7) 
     The silver nanowire-containing composition 7 was obtained in the same manner as the silver nanowire-containing composition 1, except that the silver nanowire dispersion liquid was supplemented with 1 part by mass of the mixture of pentaerythritol triacrylate and pentaerythritol tetraacrylate (product name “KAYARAD PET-30”; manufactured by Nippon Kayaku Co., Ltd.) and 0.05 parts by mass of polymerization initiator (product name “Irgacure 184”; manufactured by BASF SE) and diluted with ethanol to achieve a silver nanowire concentration of 0.2% by mass. 
     (Silver Nanowire-Containing Composition 8) 
     The silver nanowire-containing composition 8 was obtained in the same manner as the silver nanowire-containing composition 1, except that the silver nanowire dispersion liquid was supplemented with 1 part by mass of the mixture of pentaerythritol triacrylate and pentaerythritol tetraacrylate (product name “KAYARAD PET-30”; manufactured by Nippon Kayaku Co., Ltd.) and 0.05 parts by mass of polymerization initiator (product name “Irgacure 184”; manufactured by BASF SE) and diluted with ethanol to achieve a silver nanowire concentration of 1% by mass. 
     (Silver Nanowire-Containing Composition 9) 
     The silver nanowire-containing composition 9 was obtained in the same manner as the silver nanowire-containing composition 1, except that the silver nanowire dispersion liquid was diluted with a mixture of ethanol and isopropyl alcohol (IPA) instead of ethanol to achieve a silver nanowire concentration of 0.1% by mass. The ratio of IPA relative to the whole composition was 30% by mass. 
     (Silver Nanowire-Containing Composition 10) 
     The silver nanowire-containing composition 10 was obtained in the same manner as the silver nanowire-containing composition 9, except that the reaction time in the particle growth step was prolonged to obtain silver nanowires having a fiber length of 25 μm. 
     (Silver Nanowire-Containing Composition 11) 
     The silver nanowire-containing composition 11 was obtained in the same manner as the silver nanowire-containing composition 9, except that the reaction time in the particle growth step was shortened to obtain silver nanowires having a fiber length of 10 μm. 
     (Silver Nanowire-Containing Composition 12) 
     The silver nanowire-containing composition 12 was obtained in the same manner as the silver nanowire-containing composition 9, except that the concentration of polyvinylpyrrolidone was reduced by increasing the number of iterations of the desalting/washing step, as compared to that in the silver nanowire-containing composition 1. 
     (Silver Nanowire-Containing Composition 13) 
     The silver nanowire-containing composition 13 was obtained in the same manner as the silver nanowire-containing composition 9, except that anone was used instead of isopropyl alcohol (IPA) and the reaction time in the particle growth step was prolonged to obtain silver nanowires having a fiber length of 25 μm. The ratio of anone relative to the whole composition was 30% by mass. 
     (Silver Nanowire-Containing Composition 14) 
     The silver nanowire-containing composition 14 was obtained in the same manner as the silver nanowire-containing composition 9, except that the reaction time in the particle growth step was shortened to obtain silver nanowires having a fiber length of 5 μm. 
     (Silver Nanowire-Containing Composition 15) 
     The silver nanowire-containing composition 15 was obtained in the same manner as the silver nanowire-containing composition 9, except that the reaction time in the particle growth step was prolonged to obtain silver nanowires having a fiber length of 40 μm. 
     (Silver Nanowire-Containing Composition 16) 
     The silver nanowire-containing composition 16 was obtained in the same manner as the silver nanowire-containing composition 9, except that the concentration of polyvinylpyrrolidone was increased by reducing the number of iterations of the desalting/washing step, as compared to that in the silver nanowire-containing composition 1. 
     (Silver Nanowire-Containing Composition 17) 
     The silver nanowire-containing composition 17 was obtained in the same manner as the silver nanowire-containing composition 9, except that the silver nanowire dispersion liquid was diluted with a mixture of ethanol and isopropyl alcohol to achieve a silver nanowire concentration of 0.2% by mass. 
     (Silver Nanowire-Containing Composition 18) 
     The silver nanowire-containing composition 18 was obtained in the same manner as the silver nanowire-containing composition 9, except that ethanol was used instead of a mixture of ethanol and isopropyl alcohol. 
     (Silver Nanowire-Containing Composition 19) 
     The silver nanowire-containing composition 19 was obtained in the same manner as the silver nanowire-containing composition 1, except that the silver nanowire dispersion liquid was diluted with a mixture of ethanol and anone instead of ethanol to achieve a silver nanowire concentration of 0.1% by mass and an anone ratio of 30% by mass in the solvent after the dilution. 
     (Silver Nanowire-Containing Composition 20) 
     The silver nanowire-containing composition 20 was obtained in the same manner as the silver nanowire-containing composition 19, except that the silver nanowire dispersion liquid was supplemented with 0.1 parts by mass of the mixture of pentaerythritol triacrylate and pentaerythritol tetraacrylate (product name “KAYARAD PET-30”; manufactured by Nippon Kayaku Co., Ltd.) and 0.005 parts by mass of polymerization initiator (product name “Irgacure 184”; manufactured by BASF SE) and diluted with a mixture of ethanol and anone to achieve a silver nanowire concentration of 0.1% by mass and an anone ratio of 30% by mass in the solvent after the dilution. 
     (Silver Nanowire-Containing Composition 21) 
     The silver nanowire-containing composition 21 was obtained in the same manner as the silver nanowire-containing composition 19, except that the silver nanowire dispersion liquid was diluted with a mixture of ethanol and anone to achieve a silver nanowire concentration of 0.2% by mass and an anone ratio of 30% by mass in the solvent after the dilution. 
     (Silver Nanowire-Containing Composition 22) 
     The silver nanowire-containing composition 22 was obtained in the same manner as the silver nanowire-containing composition 20, except that the silver nanowire dispersion liquid was diluted with a mixture of ethanol and anone to achieve a silver nanowire concentration of 0.2% by mass and an anone ratio of 30% by mass in the solvent after the dilution. 
     (Silver Nanowire-Containing Composition 23) 
     The silver nanowire-containing composition 23 was obtained in the same manner as the silver nanowire-containing composition 19, except that the reaction time in the particle growth step was prolonged to obtain silver nanowires having a fiber length of 40 μm. 
     &lt;Light-Transmitting Resin Composition&gt; 
     The following components were combined to meet the composition requirements indicated below and thereby obtain a light-transmitting resin layer composition 1. 
     (Light-Transmitting Resin Composition 1) 
     
         
         
           
             A mixture of pentaerythritol triacrylate and pentaerythritol tetraacrylate (product name “KAYARAD PET-30”; manufactured by Nippon Kayaku Co., Ltd.): 5 parts by mass; 
             A polymerization initiator (product name “Irgacure 184”; manufactured by BASF Japan Ltd.): 0.25 parts by mass; 
             Methyl ethyl ketone (MEK): 70 parts by mass; 
             Cyclohexanone: 24.75 parts by mass.
 
(Light-Transmitting Resin Composition 2)
 
             A mixture of pentaerythritol triacrylate and pentaerythritol tetraacrylate (product name “KAYARAD PET-30”; manufactured by Nippon Kayaku Co., Ltd.): 5 parts by mass; 
             2-Methylthio-benzothiazole (manufactured by Tokyo Chemical Industry Co., Ltd.): 0.1 parts by mass; 
             A polymerization initiator (product name “Irgacure 184”; manufactured by BASF Japan Ltd.): 0.25 parts by mass; 
             Methyl ethyl ketone (MEK): 70 parts by mass; 
             Cyclohexanone: 24.75 parts by mass. 
           
         
       
    
     Examples A and Comparative Examples A 
     Example A1 
     First, a polyethylene terephthalate film (product name “Cosmoshine A4100”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having an underlayer on one surface was prepared as a light-transmitting base material, and the hard coat layer composition 1 was applied on the underlayer of the polyethylene terephthalate film to form a coating film. Subsequently, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to cure the coating film, whereby a hard coat layer having a film thickness of 2 μm was formed as a light-transmitting functional layer. 
     After the hard coat layer was formed, the silver nanowire-containing composition 1 was applied at an application dose of 10 mg/m 2  on an untreated surface of the polyethylene terephthalate film opposite to the surface facing the hard coat layer. Then, the dispersion medium in the silver nanowire-containing composition 1 was evaporated by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the applied silver nanowire-containing composition 1 to place silver nanowires on the surface of the hard coat layer. 
     Subsequently, the above-described light-transmitting resin composition 1 was applied to cover the silver nanowires and to form a coating film. Then, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to form a light-transmitting resin having a film thickness of 100 nm by curing the coating film, whereby an electroconductive film that comprised an electroconductive part having a film thickness of 100 nm and comprising the light-transmitting resin and the silver nanowires incorporated in the light-transmitting resin was obtained. The electroconductive part according to Example A1 was a plain film with no pattern. 
     The film thickness of the electroconductive part according to Example A1 was determined as the arithmetic mean of the thickness values measured at randomly selected 10 locations, wherein the thickness values were determined at the 10 locations in cross-sectional images of the electroconductive part photographed using a scanning transmission electron microscope (STEM) or a transmission electron microscope (TEM). Specifically, the cross-sectional images were photographed by the following method. First, samples for observing a cross-section were prepared from the electroconductive film. More specifically, a cut piece of the electroconductive film having a size of 2 mm×5 mm was placed in an embedding plate made of silicone, into which an epoxy resin was later poured to embed the whole electroconductive film in the resin. Then, the embedding resin was left to stand at 65° C. for 12 hours or longer and cured. Subsequently, ultra-thin sections were prepared using an ultramicrotome (product name “Ultramicrotome EM UC7”; manufactured by Leica Microsystems GmbH) at a feeding rate of 100 nm. The prepared ultra-thin sections were collected on collodion-coated meshes (150 meshes) to obtain STEM samples. Then, a cross-sectional image of a STEM sample was photographed using a scanning transmission electron microscope (STEM) (product name “S-4800 (Type 2)”; manufactured by Hitachi High-Technologies Corporation). The cross-sectional image was photographed by setting the detector switch (signal selection) to “TE,” the accelerating voltage to 30 kV, and the emission current to “10 μA.” The focus, contrast, and brightness were appropriately adjusted at a magnification of 5,000 to 200,000 times so that each layer could be identified. The magnification is preferably in the range from 10,000 to 50,000 times, further preferably in the range from 25,000 to 40,000 times. An interface between layers photographed at an extremely high magnification is represented by pixels in a coarse resolution image and appears obscure. Thus, the magnification should not be increased excessively during the measurement of film thickness. The cross-section was imaged by additionally setting the beam monitor aperture to 3 and the objective lens aperture to 3, and also setting the WD to 8 mm. The film thickness of an electroconductive part was measured by the above method not only in Example A1 but also in the following Examples and Comparative Examples. 
     Example A2 
     In Example A2, an electroconductive film was obtained in the same manner as in Example A1, except that the light-transmitting resin composition 2 was used instead of the light-transmitting resin composition 1. 
     Example A3 
     In Example A3, an electroconductive film was obtained in the same manner as in Example A1, except that the silver nanowire-containing composition 2 was used instead of the silver nanowire-containing composition 1 and the application dose of the light-transmitting resin composition was modified to achieve a film thickness of 100 nm across the whole electroconductive part. During the production process, the silver nanowire-containing composition 2 was applied and dried to form a coating film containing silver nanowires and a resin material. 
     Example A4 
     In Example A4, an electroconductive film was obtained in the same manner as in Example A1, except that the silver nanowire-containing composition 3 was used instead of the silver nanowire-containing composition 1. 
     Example A5 
     In Example A5, an electroconductive film was obtained in the same manner as in Example A1, except that the silver nanowire-containing composition 4 was used instead of the silver nanowire-containing composition 1 and the application dose of the light-transmitting resin composition was modified to achieve a film thickness of 100 nm across the whole electroconductive part. During the production process, the silver nanowire-containing composition 4 was applied and dried to form a coating film containing silver nanowires and a resin material. 
     Example A6 
     In Example A6, a polyethylene terephthalate film (product name “Cosmoshine A4300”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having underlayers on both surfaces was prepared as a light-transmitting base material, and the hard coat layer composition 1 was applied on one of the underlayers of the polyethylene terephthalate film to form a coating film. Subsequently, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to cure the coating film, whereby a hard coat layer having a film thickness of 2 μm was formed as a light-transmitting functional layer. Then, a hard coat layer was also formed on the other underlayer of the polyethylene terephthalate film in the same manner as described above to prepare a film comprising hard coat layers on both surfaces. Subsequently, the silver nanowire-containing composition 1 was applied on the hard coat layer formed on the above-described other underlayer to form an electroconductive part having a film thickness of 100 nm in the same manner as in Example A1, whereby an electroconductive film was obtained. The electroconductive part according to Example A6 was a plain film with no pattern. 
     Example A7 
     In Example A7, an electroconductive film was obtained in the same manner as in Example A6, except that the silver nanowire-containing composition 2 was used instead of the silver nanowire-containing composition 1 and the application dose of the light-transmitting resin composition was modified to achieve a film thickness of 100 nm across the whole electroconductive part. During the production process, the silver nanowire-containing composition 2 was applied and dried to form a coating film containing silver nanowires and a resin material. 
     Example A8 
     In Example A8, an electroconductive film was obtained in the same manner as in Example A6, except that the silver nanowire-containing composition 3 was used instead of the silver nanowire-containing composition 1. 
     Example A9 
     In Example A9, an electroconductive film was obtained in the same manner as in Example A6, except that the silver nanowire-containing composition 4 was used instead of the silver nanowire-containing composition 1 and the application dose of the light-transmitting resin composition was modified to achieve a film thickness of 100 nm across the whole electroconductive part. During the production process, the silver nanowire-containing composition 4 was applied and dried to form a coating film containing silver nanowires and a resin material. 
     Example A10 
     In Example A10, an electroconductive film was obtained in the same manner as in Example A1, except that the silver nanowire-containing composition 5 was used instead of the silver nanowire-containing composition 1. 
     Comparative Example A1 
     In Comparative Example A1, an electroconductive film was obtained in the same manner as in Example A1, except that the silver nanowire-containing composition 6 was used instead of the silver nanowire-containing composition 1. 
     Comparative Example A2 
     In Comparative Example A2, an electroconductive film was obtained in the same manner as in Example A1, except that the silver nanowire-containing composition 7 was used instead of the silver nanowire-containing composition 1. 
     Comparative Example A3 
     In Comparative Example A3, an electroconductive film was obtained in the same manner as in Example A1, except that the silver nanowire-containing composition 8 was used instead of the silver nanowire-containing composition 1. 
     Comparative Example A4 
     In Comparative Example A4, an electroconductive film was obtained in the same manner as in Example A6, except that the silver nanowire-containing composition 6 was used instead of the silver nanowire-containing composition 1. 
     Comparative Example A5 
     In Comparative Example A5, an electroconductive film was obtained in the same manner as in Example A1, except that no light-transmitting resin was formed. 
     Comparative Example A6 
     In Comparative Example A6, an electroconductive film was obtained in the same manner as in Example A1, except that the film thickness of the light-transmitting resin was changed from 100 nm to 50 nm. 
     Comparative Example A7 
     In Comparative Example A7, an electroconductive film was obtained in the same manner as in Example A1, except that the film thickness of the light-transmitting resin was changed from 100 nm to 400 nm. 
     &lt;Evaluation of Uneven Silver Nanowire Distribution&gt; 
     For the electroconductive films according to Examples A1 to A10 and Comparative Examples A1 to A4, and A6 and A7, it was examined whether or not the silver nanowires as a whole in each electroconductive part were unevenly distributed on the polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part. Specifically, first of all, samples for observing a cross-section were prepared from each electroconductive film. More specifically, a cut piece of the electroconductive film having a size of 2 mm×5 mm was placed in an embedding plate made of silicone, into which an epoxy resin was later poured to embed the whole electroconductive film in the resin. Then, the embedding resin was left to stand at 65° C. for 12 hours or longer and cured. Subsequently, ultra-thin sections were prepared using an ultramicrotome (product name “Ultramicrotome EM UC7”; manufactured by Leica Microsystems GmbH) at a feeding rate of 100 nm. The prepared ultra-thin sections were collected on collodion-coated meshes (150 meshes) to obtain STEM samples. Then, a cross-sectional image of a STEM sample was acquired using a scanning transmission electron microscope (STEM) (product name “S-4800 (Type 2)”; manufactured by Hitachi High-Technologies Corporation). The cross-section was observed and imaged under STEM at a magnification of 5,000 to 200,000 times by setting the detector switch (signal selection) to “TE,” the accelerating voltage to “30 kV,” and the emission current to “10 μA,” and appropriately adjusting the focus, contrast, and brightness so that each layer could be identified. The magnification is preferably in the range from 10,000 to 100,000 times, more preferably in the range from 10,000 to 50,000 times, and most preferably in the range from 25,000 to 50,000 times. Additionally, the cross-section was imaged by additionally setting the beam monitor aperture to “3” and the objective lens aperture to “3,” and also setting the WD to “8 mm.” Then, the cross-sectional images at 10 locations photographed as described above were prepared. Next, each image of the cross-section was enlarged to the pixel resolution, and the numbers of pixels covering the silver nanowires distributed from the position located at half the film thickness of the electroconductive part to the polyethylene terephthalate film and covering the silver nanowires distributed from the position located at half the film thickness of the electroconductive part to the surface of the electroconductive part were counted in each cross-sectional image to determine the ratio of the number of pixels covering the silver nanowires distributed from the above-described half-length position to the polyethylene terephthalate film relative to the total number of pixels covering all the silver nanowires. For the pixels covering a silver nanowire, each pixel on the line running through the above-described half-length position would be divided into a portion located from the above-described half-length position to the polyethylene terephthalate film and the remaining portion located from the above-described position to the surface of the electroconductive part, to divide one pixel based on the area ratio between the divided portions. Then, the above-described ratio determined from each cross-sectional image was determined as the existence ratio of electroconductive fibers distributed on the polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part, and the arithmetic mean of the existence ratio determined from the cross-sectional images was calculated. In cases where the arithmetic mean was 55% or more, the electroconductive fibers were determined to be unevenly distributed on the polyethylene terephthalate film side. The electroconductive film according to Comparative Example A5 comprised no light-transmitting resin and was thus not subjected to the evaluation. 
     &lt;Measurement of Total Light Transmittance&gt; 
     For the electroconductive films according to the above-described Examples A1 to A10 and Comparative Examples A1 to A7, the total light transmittance was measured using a haze meter (product name “HM-150”; manufactured by Murakami Color Research Laboratory Co., Ltd.) according to JIS K7361-1: 1997. The total light transmittance was a value measured on the whole electroconductive film and is also determined as the arithmetic mean of three measurement values obtained from one electroconductive film, wherein a sample having a size of 50 mm×100 mm is cut from the electroconductive film and the sample without curl or wrinkle and without any dirt such as fingerprints or dust is then placed in the haze meter in such a manner that the electroconductive part faces in the direction opposite to the light source. 
     &lt;Measurement of Haze Value&gt; 
     For the electroconductive films according to the above-described Examples A1 to A10 and Comparative Examples A1 to A7, the haze value (total haze value) of each electroconductive film was measured using a haze meter (product name “HM-150”; manufactured by Murakami Color Research Laboratory Co., Ltd.) according to JIS K7136: 2000. The haze value was a value measured on the whole electroconductive film and is also determined as the arithmetic mean of three measurement values obtained from one electroconductive film, wherein a sample having a size of 50 mm×100 mm was cut from the electroconductive film and the sample without curl or wrinkle and without any dirt such as fingerprints or dust was then placed in the haze meter in such a manner that the electroconductive part faced in the direction opposite to the light source. 
     &lt;Measurement of Surface Resistance Value&gt; 
     For the electroconductive films according to the above-described Examples A1 to A10 and Comparative Examples A1 to A7, the surface resistance of an electroconductive part was measured using a contact-type resistivity meter (product name “Loresta-AX MCP-T370”; Manufactured by Mitsubishi Chemical Analytech Co., Ltd., Type of sensor: ASP-probe) according to JIS K7194: 1994 (Testing method for resistivity of conductive plastics with a four-point probe array). The surface resistance was measured with the contact-type resistivity meter by placing a cut piece of the electroconductive film having a size of 80 mm×50 mm on a flat glass plate to create an uniformly flat surface, and then placing an ASP-probe on the center of the electroconductive part facing upward and evenly pressing all the electrode pins on the electroconductive part. For the measurement with the contact-type resistivity meter, the mode “Ω/□” as a sheet resistance measurement mode was selected. Subsequently, the start button was pushed and the instrument was held to obtain the result of the measurement. Additionally, a very high resistance value may be obtained when the surface resistance of a light-transmitting resin having a large film thickness is measured with the above-described resistivity meter. In that case, a high resistance value resulting from reduction of electrical conduction through silver nanowires due to the light-transmitting resin is indistinguishable from a high resistance value resulting from lack of electrical conduction from the surface of the electroconductive part. Thus, the surface resistance of an electroconductive part was also measured with a non-destructive resistivity meter (product name “EC-80P”; manufactured by Napson Corporation) based on the eddy current method. The surface resistance was measured with the non-destructive resistivity meter by placing a cut piece of the electroconductive film having a size of 80 mm×50 mm on a flat glass plate to create an uniform flat surface and bringing a probe into contact with the electroconductive part facing upward. For the measurement with the non-destructive resistivity meter, the type SW2 was selected for the measurement in the mode M-H sheet resistance (Ω/□) measurement, and a probe for the measurement range from 10 to 1000Ω/□ or from 0.5 to 10Ω/□ was used. Three locations for the measurement of surface resistance were in the central part of the electroconductive film and the arithmetic mean of the surface resistance values at the three locations was determined as the surface resistance value. The measurement of surface resistance value was performed in an environment at a temperature of 23° C. and a relative humidity of 55% independently of the type of a resistivity meter. The measurement of resistance value was performed using electroconductive films which had not been subjected to the below-described shelf test. 
     &lt;Shelf Test&gt; 
     For the electroconductive films according to the above-described Examples A1 to A10 and Comparative Examples A1 to A7, a shelf test was performed by leaving each electroconductive film in the air at room temperature. Specifically, for the purpose of speeding up the evaluation, pieces of adhesive tape (product number “7210F”; manufactured by Nitto Denko Corporation; 24 mm width) containing a high sulfur content were attached to polyethylene terephthalate films (product name “A4300”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and the resulting laminates were placed on each electroconductive film in such a manner that the surface of the adhesive tape was brought into contact with the electroconductive part, and were then left to stand for one week. Each adhesive tape piece was positioned at the center of an area having a size of 80 mm×50 mm on the electroconductive film, which was later cut. In the electroconductive films according to Examples A1 to A10 and Comparative Examples A1 to A6, the pieces of each electroconductive film having a size of 80 mm×50 mm were cut either before or after the shelf test in an environment at a temperature of 23° C. and a relative humidity of 55% and measured for surface resistance value (unit: Ω/□) on the electroconductive part using a contact-type resistivity meter (product name “Loresta-AX MCP-T370”; Manufactured by Mitsubishi Chemical Analytech Co., Ltd., Type of sensor: ASP-probe) according to JIS K7194: 1994 (Testing method for resistivity of conductive plastics with a four-point probe array) to evaluate the increase of the surface resistance value after the shelf test to the surface resistance value before the shelf test. Additionally, the electroconductive films according to Comparative Example A7 had a light-transmitting resin with a large film thickness and the surface resistance value of the electroconductive part measured with the contact-type resistivity meter was consequently too high, which was likely to compromise accurate determination of increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test. Thus, a non-destructive resistivity meter (product name “EC-80P”; manufactured by Napson Corporation) based on the eddy current method was used instead of a contact-type resistivity meter to measure and evaluate the surface resistance value of the electroconductive part before and after the shelf test as described above. In the Loresta-AX MCP-T370, probe “Low” should be selected for the measurement of a surface resistance value of 0.01Ω/□ or more and less than 0.5Ω/□, probe “Middle” should be selected for the measurement of a surface resistance value of 0.5Ω/□ or more and less than 10Ω/□, probe “High” should be selected for the measurement of a surface resistance value of 10Ω/□ or more and less than 1000Ω/□, and probe “Super High” should be selected for the measurement of a surface resistance value of 1000Ω/□ or more and 3000Ω/□ or less. Additionally, in the EC-80P, probes for the measurement ranges from 10 to 1000Ω/□ and from 0.5 to 10Ω/□ should be used. The evaluation criteria were as described below. The increase rate of surface resistance value was calculated based on the following formula, where A represents the increase rate of surface resistance value, B represents the surface resistance value of the electroconductive part before the shelf test, and C represents the surface resistance value of the electroconductive part after the shelf test. Additionally, the surface resistance value B before the shelf test and the surface resistance value C after the shelf test were each measured at three locations in the central part of the electroconductive part in the cut pieces of the electroconductive film, and each of the surface resistance values was determined as the arithmetic mean of the surface resistance values determined at those three locations. The arithmetic mean of the surface resistance values measured at randomly selected 10 locations on the surface of the electroconductive part before the shelf test was used as the surface resistance value B before the shelf test, while the arithmetic mean of the surface resistance values measured at randomly selected 10 locations on the surface of the electroconductive part after the shelf test was used as the surface resistance value C after the shelf test.
 
 A =( C−B )/ B× 100
     ∘: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was 10% or less;   Δ: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was more than 10% and 50% or less;   x: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was more than 50%.
 
&lt;Measurement of Martens hardness&gt;
   

     For the electroconductive films according to the above-described Examples A1 to A7 and Comparative Examples A1 to A7, the Martens hardness of each electroconductive part was measured individually at indentation amounts of 10 nm and 100 nm from the surface of the electroconductive part. Specifically, first of all, a cut piece of each electroconductive film having a size of 20 mm×20 mm was fixed with an adhesive resin (product name “Aron Alpha® General type”; manufactured by Toagosei Co., Ltd.) on a commercially available slide glass with the electroconductive part facing upward. Specifically, a drop of the above-described adhesive resin was placed at the center of a slide glass  1  (product name “Slide glass (Strainer), 1-9645-11”; manufactured by AS One Corporation). In this step, the adhesive resin was not spread over the slide glass, and a drop of the adhesive resin was applied so that the adhesive resin did not extend beyond the electroconductive film when pressed as described below. Subsequently, the slide glass was contacted with the cut piece of the electroconductive film having the above-described size with the electroconductive part facing upward and with the center of the electroconductive film located on the adhesive resin, and the adhesive resin was spread between the slide glass  1  and the electroconductive film for temporary adhesion. Then, another new slide glass  2  was placed on the electroconductive film to obtain a laminate composed of the slide glass  1 , the adhesive resin, the electroconductive film, and the slide glass  2 . Subsequently, a weight of 30 to 50 g was left to stand on the slide glass  2  for 12 hours at room temperature. Then, the weight and the slide glass  2  were removed from the laminate to prepare a measurement sample. The measurement sample was fixed on the measurement stage of a microhardness tester (product name “PICODENTOR HM500”, manufactured by Fischer Instruments K.K.; following ISO14577-1 and ASTM E2546) placed horizontally on an vibration isolation table. The slide glass  1  was fixed by putting tape (product name “Cello Tape®”; manufactured by Nichiban Co., Ltd.) on the four edges. After the measurement sample was fixed on the measurement stage of the microhardness tester, the Martens hardness was measured under the following measurement conditions at indentation amounts of 10 nm and 100 nm on the surface of the electroconductive part. The Martens hardness was measured at five arbitrary locations near the center on the surface of the electroconductive part in the measurement sample to determine the arithmetic mean of the obtained five hardness values as the Martens hardness. However, the measured five arbitrary locations were selected on the area having a surface as flat as possible in the electroconductive part by observing the electroconductive part at a magnification of 50 to 500 times using a microscope accessory to the PICODENTOR HM500, avoiding areas with extreme projections due to overlapped electroconductive fibers and, on the contrary, areas with extreme depressions. Additionally, when the Martens hardness was calculated, Martens hardness “HM” was selected as a type of hardness to be measured on the PICODENTOR HM500. 
     (Measurement Conditions) 
     
         
         
           
             Type of an indenter: Vickers (quadrangular pyramid diamond indenter, having an apex part with an angle of 136 degrees between opposite faces); 
             Load control mode: up to 40 mN; 
             Loading time: 20 seconds; 
             Creep time: 5 seconds; 
             Unloading time: 20 seconds; 
             Indentation: 10 nm (for measuring the Martens hardness at an indentation amount of 10 nm) and 100 nm (for measuring the Martens hardness at an indentation amount of 100 nm); 
             Measurement temperature: 25° C.; 
             Measurement humidity: 50%. 
           
         
       
    
     In the measurement profile, the applied load increased from 0 mN to 40 mN over 20 seconds, kept at 40 mN for 5 seconds, and then decreased from 40 mN to 0 mN over 20 seconds. 
     &lt;Determination of Electrical Resistance value Ratio&gt; 
     An arbitrary direction was determined in the surface of each of the electroconductive films according to Examples A1 to A10, and rectangular samples having a size of 110 mm length×5 mm width and extending in six different directions including the arbitrary direction, which were each an angle of 30 degrees to the arbitrary direction, were cut from the electroconductive film. After the samples were cut from the electroconductive film, a silver paste (product name “DW-520H-14”; manufactured by Toyobo Co., Ltd.) was applied on the surfaces of both longitudinal ends of each sample, having a size of 5 mm length×5 mm width, in a manner that enabled a post-curing film thickness of 5 μm or more and 10 μm or less, and heated at 130° C. for 30 minutes to obtain the sample retaining the cured silver pastes on both the terminal regions. The distance between points for measuring the electrical resistance was constantly kept at 100 mm in each sample retaining the cured silver pastes on both the terminal regions. Then, the electrical resistance value of each sample retaining the cured silver pastes on both the terminal regions was measured using a tester (product name “Digital MΩ Hitester 3454-11”; manufactured by Hioki E.E. Corporation). Specifically, because the Digital MΩ Hitester 3454-11 comprised two probe terminals (a red probe terminal and a black probe terminal; both are pin-type terminals), the red probe terminal and the black probe terminal were respectively contacted with the cured silver paste provided on one terminal region and that provided on the other terminal region to measure the electrical resistance value. Then, a sample showing the lowest electrical resistance value was identified among the samples cut in the six directions. The direction of excising the sample from the electroconductive film was designated as a first direction, and a sample excised in a second direction perpendicular to the first direction was identified, and the ratio of the electrical resistance of the sample in the second direction to that of the sample in the first direction was obtained. The measurement of electrical resistance was performed in an environment at a temperature of 23° C. and a relative humidity of 55%. The arithmetic mean of three measurements was determined as the electrical resistance value ratio. 
     The results are shown in Tables 1 and 2 below. 
     
       
         
           
               
               
               
               
               
               
               
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                   
                 Silver nanowire 
                   
                   
                 Surface resistance  
                   
                   
                   
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                   
                 Existence 
                 Uneven 
                   
                   
                 value (Ω/□) 
                   
                 Martens hardness  
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                   
                 ratio on the 
                 distribution 
                 Total light 
                 Haze  
                   
                 Non-  
                   
                 (N/nm 2 ) 
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                   
                 PET side 
                 on the PET 
                 transmittance 
                 value 
                 Contact- 
                 destructive 
                 Shelf  
                 Indentation 
                 Indentation 
               
               
                   
                 (%) 
                 side 
                 (%) 
                 (%) 
                 type 
                 type 
                 test 
                 of 10 nm 
                 of 100 nm 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 Example A1 
                 82 
                 ○ 
                 91.0 
                 1.0 
                 50 
                 49 
                 ○ 
                 1018 
                 180 
               
               
                 Example A2 
                 82 
                 ○ 
                 91.0 
                 1.0 
                 50 
                 49 
                 ○ 
                 1018 
                 180 
               
               
                 Example A3 
                 78 
                 ○ 
                 91.0 
                 1.0 
                 60 
                 61 
                 ○ 
                 1018 
                 180 
               
               
                 Example A4 
                 92 
                 ○ 
                 90.5 
                 1.8 
                 30 
                 32 
                 ○ 
                 1018 
                 180 
               
               
                 Example A5 
                 85 
                 ○ 
                 90.5 
                 1.8 
                 36 
                 37 
                 ○ 
                 1018 
                 180 
               
               
                 Example A6 
                 79 
                 ○ 
                 90.5 
                 1.0 
                 51 
                 50 
                 ○ 
                 1018 
                 190 
               
               
                 Example A7 
                 75 
                 ○ 
                 90.5 
                 1.0 
                 59 
                 58 
                 ○ 
                 1018 
                 190 
               
               
                 Example A8 
                 90 
                 ○ 
                 90.0 
                 1.8 
                 29 
                 30 
                 ○ 
                 1018 
                 190 
               
               
                 Example A9 
                 88 
                 ○ 
                 90.0 
                 1.8 
                 32 
                 32 
                 ○ 
                 1018 
                 190 
               
               
                 Example A10 
                 78 
                 ○ 
                 91.0 
                 1.1 
                 38 
                 39 
                 ○ 
                 1018 
                 190 
               
               
                 Comparative 
                 32 
                 x 
                 91.0 
                 1.0 
                 132 
                 138 
                 Δ 
                 1018 
                 180 
               
               
                 Example A1 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 48 
                 x 
                 90.5 
                 1.8 
                 72 
                 75 
                 Δ 
                 1018 
                 180 
               
               
                 Example A2 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 78 
                 ○ 
                 84.8 
                 5.2 
                 15 
                 14 
                 Δ 
                 1018 
                 180 
               
               
                 Example A3 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 42 
                 x 
                 91.0 
                 1.0 
                 142 
                 140 
                 Δ 
                 1018 
                 190 
               
               
                 Example A4 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 — 
                 — 
                 90.5 
                 1.3 
                 55 
                 54 
                 x 
                 968 
                 123 
               
               
                 Example A5 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 53 
                 x 
                 90.5 
                 1.2 
                 53 
                 51 
                 Δ 
                 988 
                 150 
               
               
                 Example A6 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 95 
                 ○ 
                 90.5 
                 1.0 
                 10 6  or more 
                 50 
                 ○ 
                 2000 
                 260 
               
               
                 Example A7 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
             
               
                   
                 TABLE 2 
               
             
            
               
                   
                   
               
               
                   
                   
                 Electrical resistance value (Ω)  
                 Electrical 
               
            
           
           
               
               
               
               
               
            
               
                   
                   
                 First  
                 Second 
                 resistance  
               
               
                   
                   
                 direction 
                 direction 
                 value ratio 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                   
                 Example A1 
                 98 
                 135 
                 1.38 
               
               
                   
                 Example A2 
                 99 
                 137 
                 1.38 
               
               
                   
                 Example A3 
                 119 
                 156 
                 1.31 
               
               
                   
                 Example A4 
                 59 
                 75 
                 1.27 
               
               
                   
                 Example A5 
                 72 
                 92 
                 1.28 
               
               
                   
                 Example A6 
                 97 
                 134 
                 1.38 
               
               
                   
                 Example A7 
                 115 
                 156 
                 1.36 
               
               
                   
                 Example A8 
                 58 
                 73 
                 1.26 
               
               
                   
                 Example A9 
                 57 
                 71 
                 1.24 
               
               
                   
                 Example A10 
                 40 
                 147 
                 3.68 
               
               
                   
                   
               
            
           
         
       
     
     In each of the electroconductive films according to Comparative Examples A1, A2, and A4, the silver nanowires were not unevenly distributed on the polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part, and a lower haze value and a higher surface resistance value were consequently achieved. This is considered to be due to a high content of a resin material in each electroconductive fiber-containing composition and the resulting insertion of the resin material into the space between silver nanowires. Additionally, a large increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test was observed. This is considered to be due to a thin film thickness of each light-transmitting resin and the resulting reduction in electrical conductivity resulting from the reaction of the silver nanowires with sulfur, oxygen, and/or halogens in the air. 
     In the electroconductive film according to Comparative Example A3, the silver nanowires were unevenly distributed on the polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part and a low surface resistance value was consequently achieved because the content of a resin material was high but the content of silver nanowires was increased in the electroconductive fiber-containing composition. However, the content of silver nanowires was high, and a high haze value was consequently achieved. Additionally, a large increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test was observed. 
     In each of the electroconductive films according to Comparative Examples A5 and A6, the silver nanowires were not unevenly distributed on the the polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part and a quite large increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test was consequently observed because no light-transmitting resin was formed or the film thickness of the light-transmitting resin was small. 
     In the electroconductive film according to Comparative Example 7, the silver nanowires were unevenly distributed on the polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part, but the film thickness of the light-transmitting resin was large and the surface of the electroconductive part consequently failed to ensure electrical conduction from the surface. Thus, a low haze value and a very high surface resistance value were achieved. 
     In each of the electroconductive films according to Examples A1 to A10, on the other hand, the silver nanowires were unevenly distributed on the polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part and the electroconductive part successfully ensured electrical conductivity from the surface, and a low haze value and a low surface resistance value were consequently achieved. Additionally, in each of the electroconductive films according to Example A1 to A8, the reaction of the metallic nanowires with, for example, sulfur, oxygen, and/or halogens in the air and the reduction in electrical conductivity in the electroconductive part were successfully controlled because the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test was small. 
     For the electroconductive films according to Example A1 and A2, a humidity/heat resistance test was performed by leaving each electroconductive film in an environment at a temperature of 85° C. and a relative humidity of 85% for 240 hours, wherein a light-transmitting adhesive sheet (product name “OCA8146-2”; manufactured by 3M Japan Ltd.) was attached to the surface of the electroconductive part. The increase rate of the surface resistance value after the humidity/heat resistance test to the surface resistance value before the humidity/heat resistance test in the electroconductive part was 10% in the electroconductive film according to Example A1, while the increase rate of the surface resistance value after the humidity/heat resistance test to the surface resistance value before the humidity/heat resistance test in the electroconductive part was 5% in the electroconductive films according to Example A2. The surface resistance value and the increase rate of the surface resistance value were determined by the same methods as for the surface resistance value and the increase rate of the surface resistance determined in the above-described shelf test. 
     When 5.5-inch rectangular samples (length:width=16:9) were prepared from each of the patterned electroconductive parts of the electroconductive films according to Examples A1 to A10 and the surface resistance value was measured on the bezel by the procedure described in the above embodiment, the surface resistance value ranged from 40Ω/□ to 60Ω/□. Additionally, when the line resistance was measured at six locations on the electroconductive part by the procedure described in the above embodiment, the electrical resistance value ratio ranged from 1.21 to 1.35. 
     Examples B and Comparative Examples B 
     Example B1 
     First, a polyethylene terephthalate film (product name “Cosmoshine A4100”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having an underlayer on one surface was prepared as a light-transmitting base material, and the hard coat layer composition 1 was applied on the underlayer of the polyethylene terephthalate film to form a coating film. Subsequently, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to cure the coating film, whereby a hard coat layer having a film thickness of 2 μm was formed as a light-transmitting functional layer. 
     After the hard coat layer was formed, the silver nanowire-containing composition 9 was applied at an application dose of 10 mg/m 2  on an untreated surface of the polyethylene terephthalate film opposite to the surface facing the formed hard coat layer. Then, the dispersion medium in the silver nanowire-containing composition 9 was evaporated by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the applied silver nanowire-containing composition 9 to place silver nanowires on the surface of the hard coat layer. 
     Subsequently, the above-described light-transmitting resin composition 1 was applied to cover the silver nanowires and to form a coating film. Then, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to form a light-transmitting resin having a film thickness of 100 nm by curing the coating film, whereby an electroconductive film that comprised an electroconductive part having a film thickness of 100 nm and comprising the light-transmitting resin and the silver nanowires incorporated in the light-transmitting resin was obtained. The electroconductive part according to Example B1 was a plain film with no pattern. 
     Example B2 
     In Example B2, an electroconductive film was obtained in the same manner as in Example B1, except that the light-transmitting resin composition 2 was used instead of the light-transmitting resin composition 1. 
     Example B3 
     In Example B3, an electroconductive film was obtained in the same manner as in Example B1, except that the silver nanowire-containing composition 10 was used instead of the silver nanowire-containing composition 9. 
     Example B4 
     In Example B4, an electroconductive film was obtained in the same manner as in Example B1, except that the silver nanowire-containing composition 11 was used instead of the silver nanowire-containing composition 9. 
     Example B5 
     In Example B5, an electroconductive film was obtained in the same manner as in Example B1, except that the silver nanowire-containing composition 12 was used instead of the silver nanowire-containing composition 9. 
     Example B6 
     In Example B6, an electroconductive film was obtained in the same manner as in Example B1, except that both the temperatures for drying the applied silver nanowire-containing composition 9 were 40° C. 
     Example B7 
     In Example B7, an electroconductive film was obtained in the same manner as in Example B1, except that the silver nanowire-containing composition 13 was used instead of the silver nanowire-containing composition 9. 
     Example B8 
     In Example 8, an electroconductive film was obtained in the same manner as in Example B1, except that the silver nanowire-containing composition 14 was used instead of the silver nanowire-containing composition 9. 
     Comparative Example B1 
     In Comparative Example B1, an electroconductive film was obtained in the same manner as in Example B1, except that the silver nanowire-containing composition 15 was used instead of the silver nanowire-containing composition 9. 
     Comparative Example B2 
     In Comparative Example B2, an electroconductive film was obtained in the same manner as in Example B1, except that the silver nanowire-containing composition 16 was used instead of the silver nanowire-containing composition 9. 
     Comparative Example B3 
     In Comparative Example B3, an electroconductive film was obtained in the same manner as in Example B1, except that the silver nanowire-containing composition 17 was used instead of the silver nanowire-containing composition 9 and the application dose of the silver nanowire-containing composition 17 was changed to 5 mg/m 2 . 
     Comparative Example B4 
     In Comparative Example B4, an electroconductive film was obtained in the same manner as in Example B1, except that the silver nanowire-containing composition 18 was used instead of the silver nanowire-containing composition 9. 
     Comparative Example B5 
     In Comparative Example B5, an electroconductive film was obtained in the same manner as in Example B1, except that both the temperatures for drying the applied silver nanowire-containing composition 9 were 100° C. 
     &lt;Determination of Electrical Resistance Value Ratio&gt; 
     In the surface of each of the electroconductive films according to Examples B1 to B8 and Comparative Examples B1 to B5, the electrical resistance value ratio was measured under the same measurement conditions as those in Example A to determine the ratio of the electrical resistance value of a sample cut in the second direction to that of a sample cut in the first direction. 
     &lt;Evaluation of Uneven Silver Nanowire Distribution&gt; 
     For the electroconductive films according to Examples B1 to B8 and Comparative Examples B1 to B5, it was examined, under the same conditions as those in Example A, whether or not the silver nanowires as a whole in each electroconductive part were unevenly distributed on the polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part. 
     &lt;Measurement of Total Light Transmittance&gt; 
     For the electroconductive films according to the above-described Examples B1 to B8 and Comparative Examples B1 to B5, the total light transmittance was measured under the same measurement conditions as those in Example A. 
     &lt;Measurement of Haze Value&gt; 
     For the electroconductive films according to the above-described Examples B1 to B8 and Comparative Examples B1 to B5, the haze value (total haze value) of each electroconductive film was measured under the same measurement conditions as those in Example A. 
     &lt;Measurement of Surface Resistance Value&gt; 
     In each of the electroconductive films according to the above-described Examples B1 to B8 and Comparative Examples B1 to B5, the resistance on the surface of the electroconductive part was measured under the same measurement conditions as those in Example A. 
     &lt;Shelf Test&gt; 
     For the electroconductive films according to the above-described Examples B1 to B8 and Comparative Examples B1 to B5, the shelf test was performed under the same conditions as those in Example A to evaluate the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the same manner as in Example A1. The evaluation criteria were as described below.
     ∘: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was 10% or less;   Δ: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was more than 10% and 50% or less;   x: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was more than 50%.
 
&lt;Measurement of Martens Hardness&gt;
   

     For the electroconductive films according to the above-described Examples B1 to B8 and Comparative Examples B1 to B5, the Martens hardness of each electroconductive part was measured individually at indentation amounts of 10 nm and 100 nm from the surface of the electroconductive part under the same conditions as those in Example A. 
     The results are shown in Tables 3 and 4 below. 
     
       
         
           
               
               
               
               
               
             
               
                 TABLE 3 
               
             
            
               
                   
               
               
                   
                 Electrical  
                   
                 Silver nanowire 
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                 resistance value 
                 Electrical 
                 Existence 
                 Uneven 
                   
                   
               
               
                   
                 (Ω) 
                 resistance 
                 ratio on 
                 distribution 
                 Total light 
                 Haze 
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                   
                 First 
                 Second 
                 value 
                 the PET 
                 on the 
                 transmittance 
                 value 
               
               
                   
                 direction 
                 direction 
                 ratio  
                 side (%) 
                 PET side 
                 (%) 
                 (%) 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                 Example B1 
                 98 
                 135 
                 1.38 
                 82 
                 ○ 
                 91.1 
                 1.0 
               
               
                 Example B2 
                 99 
                 136 
                 1.37 
                 83 
                 ○ 
                 91.1 
                 1.0 
               
               
                 Example B3 
                 85 
                 135 
                 1.59 
                 80 
                 ○ 
                 91.1 
                 1.1 
               
               
                 Example B4 
                 113 
                 126 
                 1.12 
                 79 
                 ○ 
                 91.0 
                 0.9 
               
               
                 Example B5 
                 88 
                 107 
                 1.22 
                 75 
                 ○ 
                 91.1 
                 1.0 
               
               
                 Example B6 
                 101 
                 123 
                 1.22 
                 82 
                 ○ 
                 90.9 
                 1.0 
               
               
                 Example B7 
                 110 
                 126 
                 1.15 
                 81 
                 ○ 
                 90.9 
                 1.1 
               
               
                 Example B8 
                 2650 
                 2782 
                 1.05 
                 80 
                 ○ 
                 90.8 
                 0.9 
               
               
                 Comparative 
                 40 
                 147 
                 3.68 
                 78 
                 ○ 
                 91.0 
                 1.1 
               
               
                 Example B1 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 75 
                 169 
                 2.25 
                 77 
                 ○ 
                 91.0 
                 1.1 
               
               
                 Example B2 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 70 
                 141 
                 2.01 
                 80 
                 ○ 
                 91.2 
                 1.1 
               
               
                 Example B3 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 68 
                 145 
                 2.13 
                 83 
                 ○ 
                 91.1 
                 1.1 
               
               
                 Example B4 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 72 
                 161 
                 2.24 
                 82 
                 ○ 
                 91.0 
                 1.1 
               
               
                 Example B5 
                   
                   
                   
                   
                   
                   
                   
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
             
               
                 TABLE 4 
               
             
            
               
                   
               
               
                   
                 Surface resistance 
                   
                   
               
               
                   
                 value (Ω/□)  
                   
                 Martens hardness 
               
            
           
           
               
               
               
               
               
            
               
                   
                   
                 Non- 
                   
                 (N/nm 2 ) 
               
            
           
           
               
               
               
               
               
               
            
               
                   
                 Contact- 
                 destructive 
                 Shelf 
                 Indentation 
                 Indentation 
               
               
                   
                 type 
                 type 
                 test 
                 of 10 nm 
                 of 100 nm 
               
               
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 Example B1 
                 50 
                 52 
                 ○ 
                 1080 
                 180 
               
               
                 Example B2 
                 50 
                 52 
                 ○ 
                 1080 
                 180 
               
               
                 Example B3 
                 43 
                 41 
                 ○ 
                 1080 
                 180 
               
               
                 Example B4 
                 58 
                 57 
                 ○ 
                 1080 
                 180 
               
               
                 Example B5 
                 45 
                 45 
                 ○ 
                 1080 
                 180 
               
               
                 Example B6 
                 51 
                 50 
                 ○ 
                 1080 
                 180 
               
               
                 Example B7 
                 56 
                 55 
                 ○ 
                 1080 
                 180 
               
               
                 Example B8 
                 1352 
                 1395 
                 ○ 
                 1080 
                 180 
               
               
                 Comparative 
                 38 
                 39 
                 ○ 
                 1080 
                 180 
               
               
                 Example B1 
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 68 
                 65 
                 ○ 
                 1080 
                 180 
               
               
                 Example B2 
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 51 
                 50 
                 ○ 
                 1080 
                 180 
               
               
                 Example B3 
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 53 
                 51 
                 ○ 
                 1080 
                 180 
               
               
                 Example B4 
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 51 
                 52 
                 ○ 
                 1080 
                 180 
               
               
                 Example B5 
               
               
                   
               
            
           
         
       
     
     As shown in Table 3, the electroconductive film according to Comparative Example B1 had an electrical resistance value ratio of 2 or more, and the difference in electrical resistance depending on the in-plain direction of the electroconductive part was consequently not reduced. This is considered to be due to the tendency of the silver nanowires to align in a particular direction immediately after the application of the silver nanowire-containing composition, the very long fiber length of the silver nanowires, and the resulting failure to eliminate the alignment of the silver nanowires during drying though the alignment is usually relaxed during drying. 
     The electroconductive film according to Comparative Example B2 had an electrical resistance value ratio of 2 or more, and the difference in electrical resistance depending on the in-plain direction of the electroconductive part was consequently not reduced. This is considered to be due to an increased viscosity in early drying stage resulting from an excessively high content of polyvinylpyrrolidone and the resulting failure to eliminate the alignment of the silver nanowires during drying. 
     The electroconductive film according to Comparative Example B3 had an electrical resistance value ratio of 2 or more, and the difference in electrical resistance depending on the in-plain direction of the electroconductive part was consequently not reduced. This is considered to be due to a high concentration of silver nanowires in the silver nanowire-containing composition and a quick drying of the silver nanowire-containing composition resulting from a small application dose, and the resulting failure to eliminate the alignment of the silver nanowires during drying. 
     The electroconductive film according to Comparative Example B4 had an electrical resistance value ratio of 2 or more, and the difference in electrical resistance depending on the in-plain direction of the electroconductive part was consequently not reduced. This is considered to be due to a quick drying of ethanol as compared to isopropyl alcohol and the resulting failure to eliminate the alignment of the silver nanowires during drying. 
     The electroconductive film according to Comparative Example B5 had an electrical resistance value ratio of 2 or more, and the difference in electrical resistance depending on the in-plain direction of the electroconductive part was consequently not reduced. This is considered to be due to a quick drying of the silver nanowire-containing composition for high drying temperature and the resulting failure to eliminate the alignment of the silver nanowires during drying. 
     On the other hand, as shown in Table 3, each of the electroconductive films according to Examples B1 to B8 had an electrical resistance value ratio of 1 or more and less than 2, and the difference in electrical resistance depending on the in-plain direction of the electroconductive part was consequently reduced and a low surface resistance value was consequently achieved. The high surface resistance value observed in the electroconductive film according to Example B8 is considered to be due to the very short fiber length of the silver nanowires. 
     For the electroconductive films according to Example B1 and B2, a humidity/heat resistance test was performed by leaving each electroconductive film in an environment at a temperature of 85° C. and a relative humidity of 85% for 240 hours, wherein a light-transmitting adhesive sheet (product name “OCA8146-2”; manufactured by 3M Japan Ltd.) was attached to the surface of the electroconductive part. The increase rate of the surface resistance value after the humidity/heat resistance test to the surface resistance value before the humidity/heat resistance test in the electroconductive part was 10% in the electroconductive films according to Example B1, while the increase rate of the surface resistance value after the humidity/heat resistance test to the surface resistance value before the humidity/heat resistance test in the electroconductive part was 5% in the electroconductive films according to Example B2. The surface resistance value and the increase rate of the surface resistance value were determined by the same methods as for the surface resistance value and the increase rate of the surface resistance determined in the above-described shelf test. 
     When 5.5-inch rectangular samples (length:width=16:9) were prepared from each of the patterned electroconductive parts of the electroconductive films according to Examples B1 to B8 and the surface resistance was measured on the bezel by the procedure described in the above embodiment, the surface resistance ranged from 40Ω/□ to 60Ω/□. Additionally, when the line resistance was measured at six locations on the electroconductive part by the procedure described in the above embodiment, the electrical resistance value ratio ranged from 1.21 to 1.35. 
     Examples C and Comparative Examples C 
     Example C1 
     First, a polyethylene terephthalate film (product name “Cosmoshine A4100”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having an underlayer on one surface was prepared as a light-transmitting resin base material, and the silver nanowire-containing composition 19 was applied at an application dose of 10 mg/m 2  directly on the surface having no underlayer of the polyethylene terephthalate film. Subsequently, the dispersion medium in the silver nanowire-containing composition 19 was evaporated by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the applied silver nanowire-containing composition 1 to place silver nanowires directly on the surface having no underlayer of the polyethylene terephthalate film. 
     Subsequently, the above-described light-transmitting resin composition 1 was applied to cover the silver nanowires and to form a coating film. Then, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to prepare a light-transmitting resin having a film thickness of 100 nm by curing the coating film, whereby an electroconductive film that comprised an electroconductive part having a film thickness of 100 nm and comprising the light-transmitting resin and the silver nanowires incorporated in the light-transmitting resin and provided directly on the surface having no underlayer of the polyethylene terephthalate film was obtained. The electroconductive part according to Example 1 was a plain film with no pattern. 
     Example C2 
     In Example C2, an electroconductive film was obtained in the same manner as in Example C1, except that the light-transmitting resin composition 2 was used instead of the light-transmitting resin composition 1. 
     Example C3 
     In Example C3, an electroconductive film was obtained in the same manner as in Example 1, except that the silver nanowire-containing composition 20 was used instead of the silver nanowire-containing composition 19 and the application dose of the light-transmitting resin composition 1 was modified to achieve a thickness of 100 nm across the whole electroconductive part. During the production process, the silver nanowire-containing composition 20 was applied and dried to form a coating film containing silver nanowires and a resin material. 
     Example C4 
     In Example C4, an electroconductive film was obtained in the same manner as in Example C1, except that the silver nanowire-containing composition 21 was used instead of the silver nanowire-containing composition 19. 
     Example C5 
     In Example C5, an electroconductive film was obtained in the same manner as in Example C1, except that the silver nanowire-containing composition 22 was used instead of the silver nanowire-containing composition 19 and the application dose of the light-transmitting resin composition was modified to achieve a film thickness of 100 nm across the whole electroconductive part. During the production process, the silver nanowire-containing composition 22 was applied and dried to form a coating film containing silver nanowires and a resin material. 
     Example C6 
     In Example C6, an electroconductive film was obtained in the same manner as in Example C1, except that the silver nanowire-containing composition 23 was used instead of the silver nanowire-containing composition 19. 
     Example C7 
     In Example C7, an electroconductive film was obtained in the same manner as in Example C1, except that a cycloolefin polymer base material (product name “ZF-16”; manufactured by Zeon Corporation) having a thickness of 47 μm and having no underlayers on both surfaces was used instead of the polyethylene terephthalate film. 
     Example C8 
     In Example C8, an electroconductive film was obtained in the same manner as in Example C1, except that a polycarbonate base material (product name “C110-100”; manufactured by Teijin Ltd.) having a thickness of 100 μm and having no underlayers on both surfaces was used instead of the polyethylene terephthalate film. 
     Comparative Example C1 
     In Comparative Example C1, an electroconductive film was obtained in the same manner as in Example C1, except that a polyethylene terephthalate film (product name “Cosmoshine A4300”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having underlayers on both surfaces as a light-transmitting resin base material was used instead of the polyethylene terephthalate film (product name “Cosmoshine A4100”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having an underlayer on one surface and the silver nanowire-containing composition 19 was applied on the surface of one of the underlayers of the polyethylene terephthalate film. 
     Comparative Example C2 
     In Comparative Example C2, an electroconductive film was obtained in the same manner as in Comparative Example C1, except that the silver nanowire-containing composition 20 was used instead of the silver nanowire-containing composition 19. 
     Comparative Example C3 
     In Comparative Example C3, an electroconductive film was obtained in the same manner as in Comparative Example 1, except that the silver nanowire-containing composition 21 was used instead of the silver nanowire-containing composition 19. 
     Comparative Example C4 
     In Comparative Example C4, an electroconductive film was obtained in the same manner as in Comparative Example 1, except that the silver nanowire-containing composition 22 was used instead of the silver nanowire-containing composition 19. 
     Comparative Example C5 
     In Comparative Example C5, an electroconductive film was obtained in the same manner as Comparative Example C1, except that no light-transmitting resin was formed. 
     Comparative Example C6 
     In Comparative Example C6, an electroconductive film was obtained in the same manner as in Comparative Example C1, except that the film thickness of the light-transmitting resin was changed from 100 nm to 400 nm. 
     Comparative Example C7 
     First, a polyethylene terephthalate film (product name “Cosmoshine A4300”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having underlayers on both surfaces was prepared as a light-transmitting resin base material, and the hard coat layer composition 1 was applied on the surface of one of the underlayers of the polyethylene terephthalate film to form a coating film. Subsequently, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to cure the coating film, whereby a hard coat layer having a film thickness of 2 μm was formed. 
     After the hard coat layer was formed, the silver nanowire-containing composition 19 was applied at an application dose of 10 mg/m 2  directly on the surface of the hard coat layer. Then, the dispersion medium in the silver nanowire-containing composition 1 was evaporated by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the applied silver nanowire-containing composition 19 to place silver nanowires on the surface of the hard coat layer. 
     Subsequently, the above-described light-transmitting resin composition 1 was applied to cover the silver nanowires and to form a coating film. Then, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to form a light-transmitting resin having a film thickness of 100 nm by curing the coating film, whereby an electroconductive film that comprised an electroconductive part having a film thickness of 100 nm and comprising the light-transmitting resin and the silver nanowires incorporated in the light-transmitting resin and provided on the hard coat layer was obtained. The electroconductive part according to Comparative Example C7 was a plain film with no pattern. 
     &lt;Measurement of Surface Resistance Value&gt; 
     In each of the electroconductive films according to the above-described Examples C1 to C8 and Comparative Examples C1 to C7, the resistance on the surface of the electroconductive part was measured under the same measurement conditions as those in Example A. 
     &lt;Measurement of Total Light Transmittance&gt; 
     For the electroconductive films according to the above-described Examples C1 to C8 and Comparative Examples C1 to C7, the total light transmittance was measured under the same measurement conditions as those in Example A. 
     &lt;Measurement of Haze Value&gt; 
     For the electroconductive films according to the above-described Examples C1 to C8 and Comparative Examples C1 to C7, the haze value (total haze value) of each electroconductive film was measured under the same measurement conditions as those in Example A. 
     &lt;Evaluation of Uneven Silver Nanowire Distribution&gt; 
     For the electroconductive films according to Examples C1 to C8 and Comparative Examples C1 to C4, and C6 and C7, it was examined, under the same conditions as those in Example A, whether or not the silver nanowires as a whole in each electroconductive part were unevenly distributed on the base material such as polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part. The electroconductive film according to Comparative Example C5 comprised no light-transmitting resin and was thus not subjected to the evaluation. 
     &lt;Evaluation of Flexibility&gt; 
     For the electroconductive films according to Examples C1 to C8 and Comparative Examples C1 to C7, a foldability test was performed to evaluate the flexibility. Specifically, first of all, an arbitrary direction was determined in the surface of the electroconductive part in each electroconductive film, and six rectangular samples having a size of 125 mm length×50 mm width and extending in six different directions including the arbitrary direction, which were each an angle of 30 degrees to the arbitrary direction, were cut from the electroconductive film. After the samples were cut from the electroconductive film, a silver paste (product name “DW-520H-14”; manufactured by Toyobo Co., Ltd.) was applied on the surfaces of both longitudinal ends of each sample, having a size of 10 mm length×50 mm width, and heated at 130° C. for 30 minutes to obtain the sample retaining the cured silver pastes on both the terminal regions. The distance between points for measuring the electrical resistance was constantly kept at 105 mm in each sample retaining the cured silver pastes on both the terminal regions. Then, the electrical resistance of each sample retaining the cured silver pastes on both the terminal regions was measured using a tester (product name “Digital MΩ Hitester 3454-11”; manufactured by Hioki E.E. Corporation). Specifically, because the Digital MΩ Hitester 3454-11 comprised two probe terminals (a red probe terminal and a black probe terminal; both are pin-type terminals), the red probe terminal was contacted with the cured silver paste provided on one terminal region and the black probe terminal was contacted with the cured silver paste provided on the other terminal region to measure the electrical resistance. Then, a sample showing the lowest electrical resistance value was selected among the samples cut in the six directions. Subsequently, the selected sample having the short edges (50 mm) fixed with fixing members was mounted to an endurance testing machine (product name “DLDMLH-FS”; manufactured by Yuasa System Co., Ltd.) in such a manner that the minimum distance between the two opposing edges was 3 mm (the outer width of the bent part: 3.0 mm), as shown in  FIG.  5 (C) , and the sample with the electroconductive part facing inward was folded at 180 degrees and then unfolded (a foldability test performed on the sample with the electroconductive part facing inward and the base material facing outward), and the process was repeated one hundred thousand times. After the foldability test was performed, the sample after the foldability test was measured for electrical resistance on the surface of the electroconductive part, similarly to the sample before the foldability test. Then, the electrical resistance value ratio, namely the ratio of the electrical resistance value measured after the foldability test on the selected sample to that measured before the foldability test on the same sample (the electrical resistance of the selected sample before the foldability test/the electrical resistance of the same sample after the foldability test), was calculated. Additionally, a sample cut from each of the electroconductive films according to Examples and Comparative Examples and selected based on the measured electrical resistance value in the same manner as described above was mounted to the above-described endurance testing machine in the same manner as described above, and the sample with the base material facing inward was folded at 180 degrees and then unfolded (a foldability test performed on the sample with the electroconductive part facing outward and the base material facing inward), and the process was repeated one hundred thousand times, and the sample after the foldability test was similarly measured for electrical resistance on the surface of the electroconductive part to calculate the electrical resistance value ratio. Then, the results of the foldability tests were evaluated as the flexibility based on the following evaluation criteria. The arithmetic mean of three measurements was determined as the electrical resistance value ratio. 
     ⊙: the electrical resistance value ratio was 1.5 or less in both of the foldability tests; 
     ∘: the electrical resistance value ratio was more than 1.5 and 3 or less in both of the foldability tests; 
     Δ: the electrical resistance value ratio was more than 3 in either of the foldability tests. 
     &lt;Determination of Electrical Resistance Value Ratio&gt; 
     In the surface of each of the electroconductive films according to the Examples, the electrical resistance value ratio was measured under the same measurement conditions as those in Example A to determine the ratio of the electrical resistance of a sample cut in the first direction to that of a sample cut in the second direction. 
     &lt;Shelf Test&gt; 
     For the electroconductive films according to the above-described Examples C1 to C8 and Comparative Examples C1 to C7, the shelf test was performed under the same conditions as those in Example A to evaluate the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the same manner as in Example A. The evaluation criteria were as described below.
     ∘: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was less than 10% or less;   Δ: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was more than 10% and 50% or less;   x: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was more than 50%.
 
&lt;Measurement of Martens Hardness&gt;
   

     For the electroconductive films according to the above-described Examples C1 to C8 and Comparative Examples C1 to C7, the Martens hardness of each electroconductive part was measured individually at indentation amounts of 10 nm and 100 nm from the surface of the electroconductive part under the same conditions as those in Example A. 
     The results are shown in Tables 5 and 6 below. 
     
       
         
           
               
               
               
               
               
               
               
               
             
               
                 TABLE 5 
               
             
            
               
                   
               
               
                   
                 Surface  
                   
                   
                 Silver nanowire 
                   
                   
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                   
                 resistance value 
                   
                   
                 Existence 
                 Uneven 
                   
                   
                   
               
               
                   
                 (Ω/□) 
                   
                   
                 ratio on the 
                 distribution 
                   
                   
                 Martens hardness 
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                   
                   
                 Non-  
                 Total light 
                 Haze 
                 base 
                 on the base 
                   
                   
                 (N/nm 2 ) 
               
            
           
           
               
               
               
               
               
               
               
               
               
               
               
            
               
                   
                 Contact-  
                 destructive 
                 transmittance 
                 value 
                 material 
                 material 
                   
                 Shelf  
                 Indentation 
                 Indentation 
               
               
                   
                 type 
                 type 
                 (%) 
                 (%) 
                 side (%) 
                 side 
                 Flexibility 
                 test 
                 of 10 nm 
                 of 100 nm 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
               
            
               
                 Example C1 
                 51 
                 50 
                 90.3 
                 1.2 
                 83 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 180 
               
               
                 Example C2 
                 50 
                 50 
                 90.4 
                 1.2 
                 85 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 180 
               
               
                 Example C3 
                 61 
                 60 
                 90.3 
                 1.2 
                 78 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 180 
               
               
                 Example C4 
                 31 
                 30 
                 89.5 
                 2.0 
                 91 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 180 
               
               
                 Example C5 
                 37 
                 38 
                 89.6 
                 2.0 
                 85 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 180 
               
               
                 Example C6 
                 39 
                 40 
                 90.0 
                 1.3 
                 76 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 180 
               
               
                 Example C7 
                 52 
                 52 
                 91.0 
                 1.0 
                 75 
                 ○ 
                 ◯ 
                 ○ 
                 1018 
                 160 
               
               
                 Example C8 
                 54 
                 53 
                 90.5 
                 1.0 
                 73 
                 ○ 
                 ◯ 
                 ○ 
                 1018 
                 150 
               
               
                 Comparative 
                 143 
                 162 
                 89.5 
                 1.2 
                 79 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 160 
               
               
                 Example C1 
                   
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 189 
                 185 
                 89.5 
                 1.2 
                 75 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 160 
               
               
                 Example C2 
                   
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 93 
                 95 
                 88.8 
                 1.2 
                 85 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 160 
               
               
                 Example C3 
                   
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 112 
                 110 
                 88.7 
                 1.9 
                 83 
                 ○ 
                 ⊙ 
                 ○ 
                 1018 
                 160 
               
               
                 Example C4 
                   
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 142 
                 152 
                 89.5 
                 1.5 
                 — 
                 — 
                 ⊙ 
                 x 
                 968 
                 123 
               
               
                 Example C5 
                   
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 10 6  or 
                 163 
                 89.5 
                 1.2 
                 95 
                 ○ 
                 ⊙ 
                 ○ 
                 2000 
                 260 
               
               
                 Example C6 
                 more 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 52 
                 52 
                 89.6 
                 1.2 
                 82 
                 ○ 
                 x 
                 ○ 
                 1018 
                 190 
               
               
                 Example C7 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
             
               
                   
                 TABLE 6 
               
             
            
               
                   
                   
               
               
                   
                   
                   
                 Electrical 
               
               
                   
                   
                 Electrical resistance value (Ω)  
                 resistance  
               
            
           
           
               
               
               
               
               
            
               
                   
                   
                 First  
                 Second  
                 value 
               
               
                   
                   
                 direction 
                 direction 
                 ratio 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                   
                 Example C1 
                 97 
                 115 
                 1.19 
               
               
                   
                 Example C2 
                 95 
                 115 
                 1.22 
               
               
                   
                 Example C3 
                 106 
                 127 
                 1.20 
               
               
                   
                 Example C4 
                 58 
                 65 
                 1.12 
               
               
                   
                 Example C5 
                 73 
                 83 
                 1.14 
               
               
                   
                 Example C6 
                 42 
                 127 
                 3.02 
               
               
                   
                 Example C7 
                 98 
                 120 
                 1.22 
               
               
                   
                 Example C8 
                 100 
                 121 
                 1.21 
               
               
                   
                   
               
            
           
         
       
     
     As shown in Table 5, each of the electroconductive films according to Comparative Examples C1 to C6 had an underlayer provided between the base material, such as the polyethylene terephthalate base material, and the electroconductive part, and a high surface resistance value was consequently achieved. This is considered to be due to incorporation of silver nanowires into the underlayer. 
     The electroconductive film according to Comparative Example C7 had a hard coat layer provided between the base material, such as the polyethylene terephthalate base material, and the electroconductive part, and poor flexibility and a high electrical resistance value ratio between before and after the foldability test were consequently achieved. This is considered to be due to a crack or fracture formed by the foldability test in the electroconductive film and the resulting reduction in electrical conductivity. 
     On the other hand, as shown in Table 5, each of the electroconductive films according to Examples C1 to C8 had an electroconductive part provided directly on the surface of a base material, such as a polyethylene terephthalate base material, and a low surface resistance value was consequently achieved. Additionally, excellent flexibility was achieved in each of the electroconductive films because no hard coat layer was provided between the base material and the electroconductive part. 
     For the electroconductive films according to Example C1 and C2, a humidity/heat resistance test was performed by leaving each electroconductive film in an environment at a temperature of 85° C. and a relative humidity of 85% for 240 hours, wherein a light-transmitting adhesive sheet (product name “OCA8146-2”; manufactured by 3M Japan Ltd.) was attached to the surface of the electroconductive part. The increase rate of the surface resistance value after the humidity/heat resistance test to the surface resistance value before the humidity/heat resistance test in the electroconductive part was 10% in the electroconductive films according to Example C1, while the increase rate of the surface resistance value after the humidity/heat resistance test to the surface resistance value before the humidity/heat resistance test in the electroconductive part was 5% in the electroconductive films according to Example C2. The surface resistance value and the increase rate of surface resistance value were determined by the same methods as for the surface resistance value and the increase rate of surface resistance determined in the above-described shelf test. 
     When 5.5-inch rectangular samples (length:width=16:9) were prepared from each of the patterned electroconductive parts of the electroconductive films according to Examples C1 to C8 and the surface resistance value was measured on the bezel by the procedure described in the above embodiment, the surface resistance value ranged from 40Ω/□ to 60Ω/□. Additionally, when the line resistance was measured at six locations on the electroconductive part by the procedure described in the above embodiment, the electrical resistance value ratio ranged from 1.21 to 1.35. 
     Examples D and Comparative Examples D 
     Example D1 
     First, a polyethylene terephthalate film (product name “Cosmoshine A4300”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having underlayers on both surfaces was prepared as a light-transmitting resin base material, and the silver nanowire-containing composition 1 was applied at an application dose of 10 mg/m 2  directly on the surface of one of the underlayers of the polyethylene terephthalate film. Then, the dispersion medium in the silver nanowire-containing composition 1 was evaporated by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the applied silver nanowire-containing composition 1 to place silver nanowires directly on the surface of the one underlayer of the polyethylene terephthalate film. 
     Subsequently, the above-described light-transmitting resin composition 1 was applied to cover the silver nanowires and to form a coating film. Then, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to form a light-transmitting resin having a film thickness of 100 nm by curing the coating film, whereby an electroconductive film that comprised an electroconductive part having a film thickness of 100 nm and comprising the light-transmitting resin and the silver nanowires incorporated in the light-transmitting resin and provided directly on the surface of the one underlayer of the polyethylene terephthalate film was obtained. The electroconductive part according to Example D1 was a plain film with no pattern. 
     Example D2 
     In Example D2, an electroconductive film was obtained in the same manner as in Example D1, except that the light-transmitting resin composition 2 was used instead of the light-transmitting resin composition 1. 
     Example D3 
     In Example D3, an electroconductive film was obtained in the same manner as in Example D1, except that the silver nanowire-containing composition 2 was used instead of the silver nanowire-containing composition 1 and the application dose of the light-transmitting resin composition 1 was modified to achieve a thickness of 100 nm across the whole electroconductive part. During the production process, the silver nanowire-containing composition 2 was applied and dried to prepare a coating film containing silver nanowires and a resin material. 
     Example D4 
     In Example D4, an electroconductive film was obtained in the same manner as in Example D1, except that the silver nanowire-containing composition D3 was used instead of the silver nanowire-containing composition 1. 
     Example D5 
     In Example D5, an electroconductive film was obtained in the same manner as in Example D1, except that the silver nanowire-containing composition 4 was used instead of the silver nanowire-containing composition 1 and the application dose of the light-transmitting resin composition was modified to achieve a film thickness of 100 nm across the whole electroconductive part. During the production process, the silver nanowire-containing composition 4 was applied and dried to form a coating film containing silver nanowires and a resin material. 
     Example D6 
     In Example D6, an electroconductive film was obtained in the same manner as in Example D1, except that the silver nanowire-containing composition 5 was used instead of the silver nanowire-containing composition 1. 
     Example D7 
     In Example D7, an electroconductive film was obtained in the same manner as in Example D1, except that the silver nanowire-containing composition 19 was used instead of the silver nanowire-containing composition 1. 
     Comparative Example D1 
     First, a polyethylene terephthalate film (product name “Cosmoshine A4300”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having underlayers on both surfaces was prepared as a light-transmitting resin base material, and the hard coat layer composition 1 was applied on the surface of one of the underlayers of the polyethylene terephthalate film to form a coating film. Subsequently, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to cure the coating film, whereby a hard coat layer having a film thickness of 2 μm was formed. 
     After the hard coat layer was formed, the silver nanowire-containing composition 1 was applied at an application dose of 10 mg/m 2  directly on the surface of the hard coat layer. Then, the dispersion medium in the silver nanowire-containing composition 1 was evaporated by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the applied silver nanowire-containing composition 1 to place silver nanowires on the surface of the hard coat layer. 
     Subsequently, the above-described light-transmitting resin composition 1 was applied to cover the silver nanowires and to form a coating film. Then, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to form a light-transmitting resin having a film thickness of 100 nm by curing the coating film, whereby an electroconductive film that comprised an electroconductive part having a film thickness of 100 nm and comprising the light-transmitting resin and the silver nanowires incorporated in the light-transmitting resin and provided on the hard coat layer was obtained. The electroconductive part according to Comparative Example D1 was a plain film with no pattern. 
     Comparative Example D2 
     In Comparative Example D2, an electroconductive film was obtained in the same manner as in Comparative Example D1, except that the silver nanowire-containing composition 2 was used instead of the silver nanowire-containing composition 1. 
     Comparative Example D3 
     In Comparative Example D3, an electroconductive film was obtained in the same manner as in Comparative Example D1, except that the silver nanowire-containing composition 3 was used instead of the silver nanowire-containing composition 1. 
     Comparative Example D4 
     In Comparative Example D4, an electroconductive film was obtained in the same manner as in Comparative Example D1, except that the silver nanowire-containing composition 4 was used instead of the silver nanowire-containing composition 1. 
     Comparative Example D5 
     In Comparative Example D5, an electroconductive film was obtained in the same manner as Comparative Example D1, except that no light-transmitting resin was formed. 
     Comparative Example D6 
     In Comparative Example D6, an electroconductive film was obtained in the same manner as in Comparative Example D1, except that the film thickness of the light-transmitting resin was changed from 100 nm to 400 nm. 
     Comparative Example D7 
     First, a polyethylene terephthalate film (product name “Cosmoshine A4100”; manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and having a underlayer on one surface was prepared as a light-transmitting resin base material, and the silver nanowire-containing composition 1 was applied at an application dose of 10 mg/m 2  directly on the surface having no underlayer of the polyethylene terephthalate film. Then, the dispersion medium in the silver nanowire-containing composition 1 was evaporated by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the applied silver nanowire-containing composition 1 to place silver nanowires directly on the surface having no underlayer of the polyethylene terephthalate film 
     Subsequently, the above-described light-transmitting resin composition 1 was applied to cover the silver nanowires and to form a coating film. Then, the formed coating film was dried by dry air blowing at 50° C. at a flow rate of 0.5 m/s for 15 seconds and subsequent dry air blowing at 70° C. at a flow rate of 10 m/s for 30 seconds over the coating film to evaporate the solvent in the coating film, and then exposed to ultraviolet light to a cumulative light dose of 100 mJ/cm 2  to prepare a light-transmitting resin having a film thickness of 100 nm by curing the coating film, whereby an electroconductive film that comprised an electroconductive part comprising the light-transmitting resin and the silver nanowires incorporated in the light-transmitting resin and provided directly on the surface having no underlayer of the polyethylene terephthalate film was obtained. The electroconductive part according to Comparative Example D7 was a plain film with no pattern. 
     &lt;Evaluation of Flexibility&gt; 
     For the electroconductive films according to Examples D1 to D7 and Comparative Examples D1 to D7, the foldability test was performed to measure the electrical resistance value under the same measurement conditions as those in Example C and to evaluate the flexibility in the same manner as in Example C. The evaluation criteria were as described below. 
     ⊙: the electrical resistance value ratio was 1.5 or less in both of the foldability tests; 
     ∘: the electrical resistance value ratio was more than 1.5 and 3 or less in both of the foldability tests; 
     x: the electrical resistance value ratio was more than 3 in either of the foldability tests. 
     &lt;Adhesion Test&gt; 
     For the electroconductive films according to Examples D1 to D7 and Comparative Examples D1 to D7, adhesion to a cured silver paste was evaluated. Specifically, first of all, three pieces of electroconductive film having a size of 150 mm×150 mm were cut from each of the electroconductive films according to Examples D1 to D7 and Comparative Examples D1 to D7, and a silver paste  1  (product name “DW-520H-14”; manufactured by Toyobo Co., Ltd.) was applied by screen printing technique on the first piece of electroconductive film, and a silver paste  2  (product name “DW-520H-19”; manufactured by Toyobo Co., Ltd.) was applied by screen printing technique on the surfaces of the electroconductive parts of the second piece of electroconductive film, and a silver paste  3  (product name “DW-520H-18”; manufactured by Toyobo Co., Ltd.) was applied by screen printing technique on the surfaces of the electroconductive parts of the third piece of electroconductive film. After each silver paste was applied on the surface of each electroconductive part, each electroconductive film retaining the applied silver paste was heated at 130° C. for 30 minutes to form a cured silver paste having a film thickness of 7 μm on the surface of the electroconductive part of the electroconductive film. Then, a cross-cut test was performed on each electroconductive film retaining the cured silver paste in an environment at a temperature of 23° C. and a relative humidity of 55% to evaluate the adhesion between the electroconductive film and the cured silver paste. Specifically, the cured silver paste formed on each electroconductive part was inscribed using a cutter knife to create a grid of 10×10, wherein the vertical and horizontal grid lines were spaced 1 mm apart and were orthogonal to each other. The incisions were deep enough to penetrate the cured silver paste and to reach the polyethylene terephthalate film. A piece of adhesive tape (model number “405”; manufactured by Nichiban Co., Ltd.; 24 mm width) was attached to the surface of the cured silver paste with the inscribed grid lines to cover the entire area of the grid, and the attached adhesive tape was quickly removed the surface of the cured silver paste by holding a part of the adhesive tape and pulling it vertically. The process of attaching and removing the adhesive tape was consecutively repeated five times and the number of square coating films left in the grid was counted after the five trials to evaluate the adhesion. The evaluation results were based on the following evaluation criteria. In cases where the number of remaining square coating films was 100, that is, no square coating film was peeled off and removed, it was expressed as 100/100; in cases where all the square coating films were removed, it was expressed as 0/100. 
     ∘: 100/100; 
     Δ: 80/100 to 99/100; 
     x: 0/100 to 79/100. 
     &lt;Measurement of Surface Resistance Value&gt; 
     In each of the electroconductive films according to the above-described Examples D1 to D7 and Comparative Examples D1 to D7, the resistance value on the surface of the electroconductive part was measured under the same measurement conditions as those in Example A. 
     &lt;Measurement of Total Light Transmittance&gt; 
     For the electroconductive films according to the above-described Examples D1 to D7 and Comparative Examples D7 to D7, the total light transmittance was measured under the same measurement conditions as those in Example A. 
     &lt;Measurement of Haze Value&gt; 
     For the electroconductive films according to the above-described Examples D1 to D7 and Comparative Examples D1 to D7, the haze value (total haze value) of each electroconductive film was measured under the same measurement conditions as those in Example A. 
     &lt;Evaluation of Uneven Silver Nanowire Distribution&gt; 
     For the electroconductive films according to Examples D1 to D7 and Comparative Examples D1 to D4, and D6 and D7, it was examined, under the same conditions as those in Example A, whether or not the silver nanowires as a whole in each electroconductive part were unevenly distributed on the base material such as the polyethylene terephthalate film side than the position located at half the film thickness of the electroconductive part. The electroconductive film according to Comparative Example D5 comprised no light-transmitting resin and was thus not subjected to the evaluation. 
     &lt;Determination of Electrical Resistance Value Ratio&gt; 
     In the surface of each of the electroconductive films according to Examples D1 to D7, the electrical resistance value ratio was measured under the same measurement conditions as those in Example A to determine the ratio of the electrical resistance value of a sample cut in the second direction to that of a sample cut in the first direction. 
     &lt;Shelf Test&gt; 
     For the electroconductive films according to the above-described Examples D1 to D7 and Comparative Examples D1 to D7, the shelf test was performed under the same conditions as those in Example A to evaluate the increase in surface resistance value after the shelf test to the surface resistance value before the shelf test in the same manner as in Example A. The evaluation criteria were as described below.
     ∘: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was less than 10% or less;   Δ: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was more than 10% and 50% or less;   x: the increase rate of the surface resistance value after the shelf test to the surface resistance value before the shelf test in the electroconductive part was more than 50%.
 
&lt;Measurement of Martens Hardness&gt;
   

     For the electroconductive films according to the above-described Examples D1 to D7 and Comparative Examples D1 to D7, the Martens hardness of each electroconductive part was measured individually at indentation amounts of 10 nm and 100 nm from the surface of the electroconductive part under the same conditions as those in Example A. 
     The results are shown in Tables 7 to 9 below. 
     
       
         
           
               
               
               
               
             
               
                 TABLE 7 
               
             
            
               
                   
               
               
                   
                   
                   
                 Surface resistance  
               
               
                   
                   
                   
                 value (Ω/□) 
               
            
           
           
               
               
               
               
               
            
               
                   
                   
                 Adhesion 
                   
                 Non- 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                   
                 Silver 
                 Silver 
                 Silver 
                 Contact-  
                 destructive 
               
               
                   
                 Flexibilty 
                 paste 1 
                 paste 2 
                 paste 3 
                 type 
                 type 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 Example D1 
                 ⊙ 
                 ○ 
                 ○ 
                 ○ 
                 52 
                 51 
               
               
                 Example D2 
                 ⊙ 
                 ○ 
                 ○ 
                 ○ 
                 51 
                 53 
               
               
                 Example D3 
                 ⊙ 
                 ○ 
                 ○ 
                 ○ 
                 63 
                 65 
               
               
                 Example D4 
                 ⊙ 
                 ○ 
                 ○ 
                 ○ 
                 30 
                 32 
               
               
                 Example D5 
                 ⊙ 
                 ○ 
                 ○ 
                 ○ 
                 37 
                 38 
               
               
                 Example D6 
                 ⊙ 
                 ○ 
                 ○ 
                 ○ 
                 41 
                 43 
               
               
                 Example D7 
                 ⊙ 
                 ○ 
                 ○ 
                 ○ 
                 143 
                 162 
               
               
                 Comparative 
                 x 
                 ○ 
                 ○ 
                 ○ 
                 53 
                 54 
               
               
                 Example D1 
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 x 
                 ○ 
                 ○ 
                 ○ 
                 63 
                 62 
               
               
                 Example D2 
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 x 
                 ○ 
                 ○ 
                 ○ 
                 33 
                 32 
               
               
                 Example D3 
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 x 
                 ○ 
                 ○ 
                 ○ 
                 38 
                 39 
               
               
                 Example D4 
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 x 
                 ○ 
                 ○ 
                 ○ 
                 53 
                 55 
               
               
                 Example D5 
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 x 
                 ○ 
                 ○ 
                 ○ 
                 10 6  or 
                 53 
               
               
                 Example D6 
                   
                   
                   
                   
                 more 
                   
               
               
                 Comparative 
                 ⊙ 
                 ○ 
                 ○ 
                 Δ 
                 51 
                 50 
               
               
                 Example D7 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
               
               
               
             
               
                 TABLE 8 
               
             
            
               
                   
               
               
                   
                   
                   
                 Silver nanowire 
                   
                   
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                   
                   
                 Existence 
                 Uneven 
                   
                 Martens hardness 
               
               
                   
                 Total light 
                 Haze 
                 ratio on 
                 distribution 
                   
                 (N/nm 2 ) 
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                   
                 transmittance 
                 value 
                 the PET 
                 on the 
                 Shelf 
                 Indentation  
                 Indentation 
               
               
                   
                 (%) 
                 (%) 
                 side (%) 
                 PET side 
                 test  
                 of 10 nm 
                 of 100 nm 
               
               
                   
               
               
                 Example D1 
                 89.6 
                 1.2 
                 82 
                 ○ 
                 ○ 
                 1018 
                 160 
               
               
                 Example D2 
                 89.5 
                 1.3 
                 80 
                 ○ 
                 ○ 
                 1018 
                 160 
               
               
                 Example D3 
                 89.5 
                 1.2 
                 78 
                 ○ 
                 ○ 
                 1018 
                 160 
               
               
                 Example D4 
                 88.8 
                 2.0 
                 89 
                 ○ 
                 ○ 
                 1018 
                 160 
               
               
                 Example D5 
                 88.7 
                 1.9 
                 88 
                 ○ 
                 ○ 
                 1018 
                 160 
               
               
                 Example D6 
                 88.9 
                 1.3 
                 77 
                 ○ 
                 ○ 
                 1018 
                 160 
               
               
                 Example D7 
                 89.5 
                 1.2 
                 79 
                 ○ 
                 ○ 
                 1018 
                 160 
               
               
                 Comparative 
                 89.5 
                 1.2 
                 79 
                 ○ 
                 ○ 
                 1018 
                 190 
               
               
                 Example D1 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 89.5 
                 1.2 
                 75 
                 ○ 
                 ○ 
                 1018 
                 190 
               
               
                 Example D2 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 88.9 
                 1.2 
                 88 
                 ○ 
                 ○ 
                 1018 
                 190 
               
               
                 Example D3 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 88.8 
                 1.9 
                 86 
                 ○ 
                 ○ 
                 1018 
                 190 
               
               
                 Example D4 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 89.5 
                 1.5 
                 — 
                 — 
                 x 
                 1018 
                 190 
               
               
                 Example D5 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 89.5 
                 1.2 
                 95 
                 ○ 
                 ○ 
                 2000 
                 260 
               
               
                 Example D6 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 90.3 
                 1.2 
                 83 
                 ○ 
                 ○ 
                 1018 
                 180 
               
               
                 Example D7 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
             
               
                   
                 TABLE 9 
               
             
            
               
                   
                   
               
               
                   
                   
                 Electrical resistance value (Ω)  
                 Electrical 
               
            
           
           
               
               
               
               
               
            
               
                   
                   
                 First  
                 Second 
                 resistance 
               
               
                   
                   
                 direction 
                 direction 
                 value ratio 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                   
                 Example D1 
                 98 
                 136 
                 1.39 
               
               
                   
                 Example D2 
                 97 
                 136 
                 1.40 
               
               
                   
                 Example D3 
                 104 
                 142 
                 1.37 
               
               
                   
                 Example D4 
                 53 
                 67 
                 1.26 
               
               
                   
                 Example D5 
                 72 
                 90 
                 1.25 
               
               
                   
                 Example D6 
                 40 
                 151 
                 3.78 
               
               
                   
                 Example D7 
                 270 
                 324 
                 1.20 
               
               
                   
                   
               
            
           
         
       
     
     As shown in Table 7, each of the electroconductive films according to Comparative Examples D1 to D6 had a hard coat layer provided between the underlayer and the electroconductive part, and poor flexibility was consequently achieved. On the other hand, as shown in Table 7, each of the electroconductive films according to Examples D1 to D7 had an electroconductive part provided directly on the surface of an underlayer, and excellent flexibility was consequently achieved. 
     Additionally, as shown in Table 7, the electroconductive film according to Comparative Example D7 had an electroconductive part provided directly on a polyethylene terephthalate film, and excellent adhesion to the cured silver pastes  1  and  2  and poor adhesion to the cured silver paste  3  were consequently achieved. On the other hand, each of the electroconductive films according to Examples D1 to D7 had an electroconductive part provided directly on the surface of an underlayer, and excellent adhesion to all the cured silver pastes  1  to  3  was consequently achieved. 
     The high surface resistance value observed by a contact-type resistivity meter in Comparative Example D6 is considered to be due to the presence of a light-transmitting resin with an extremely large film thickness, while the relatively high surface resistance observed in Example D7 is considered to be due to the influence of anone as a dispersion medium that permeates into the underlayer and the resulting incorporation of silver nanowires into the underlayer. 
     For the electroconductive films according to Example D1 and D2, a humidity/heat resistance test was performed by leaving each electroconductive film in an environment at a temperature of 85° C. and a relative humidity of 85% for 240 hours, wherein a light-transmitting adhesive sheet (product name “OCA8146-2”; manufactured by 3M Japan Ltd.) was attached to the surface of the electroconductive part. The increase rate of the surface resistance value after the humidity/heat resistance test to the surface resistance value before the humidity/heat resistance test in the electroconductive part was 10% in the electroconductive films according to Example D1, while the increase rate of the surface resistance value after the humidity/heat resistance test to the surface resistance value before the humidity/heat resistance test in the electroconductive part was 5% in the electroconductive films according to Example D2. The surface resistance value and the increase rate of the surface resistance were determined by the same methods as for the surface resistance value and the increase rate of the surface resistance determined in the above-described shelf test. 
     When 5.5-inch rectangular samples (length:width=16:9) were prepared from each of the patterned electroconductive parts of the electroconductive films according to Examples D1 to D7 and the surface resistance was measured on the bezel by the procedure described in the above embodiment, the surface resistance value from 40Ω/□ to 60Ω/□. Additionally, when the line resistance was measured at six locations on the electroconductive part by the procedure described in the above embodiment, the electrical resistance value ratio ranged from 1.21 to 1.35. 
     LIST OF REFERENCE NUMERALS 
     
         
           10 ,  20 ,  30 ,  80 ,  100 ,  110 ,  140 ,  150 ,  160 ,  200 ,  250 ,  260 ,  290 . Electroconductive film 
           10 A,  20 A,  30 A,  100 A,  110 A,  140 A,  150 A,  160 A,  250 A,  260 A. Surface 
           11 ,  81 ,  101 ,  141 . Light-transmitting base material 
           12 ,  82 ,  102 ,  142 . Light-transmitting functional layer 
           13 ,  22 ,  31 ,  84 ,  103 ,  112 ,  144 ,  152 ,  162 ,  203 ,  254 ,  262 ,  295 . Electroconductive part 
           15 ,  86 ,  104 ,  154 ,  255 . Light-transmitting resin 
           16 ,  87 ,  105 ,  155 ,  256 . Electroconductive fiber 
           21 ,  83 ,  111 ,  143 ,  161 ,  202 ,  261 ,  294 . Electroconductive layer 
           40 ,  120 ,  170 ,  270 . Image display device 
           50 ,  180 . Display panel 
           55 . Display element 
           70 ,  130 ,  190 ,  280 . Touch panel 
           151 ,  201 ,  251 ,  291 . Light-transmitting resin base material