Patent Publication Number: US-4253884-A

Title: Treating nickel base alloys

Description:
The present invention relates to a method for heat treating and coating a nickel-base superalloy. 
     Most superalloys are variations of the basic nickel-chromium matrix containing varying amounts of titanium and aluminum, hardened by γ&#39;[Ni 3  (Al, Ti)], with optional additions such as cobalt, molybdenum, tungsten, boron and zirconium. Two such superalloys are disclosed in U.S. Pat. Nos. 4,083,734 and 4,093,476. Each of these alloys are characterized by a highly desirable combination of hot corrosion resistance, hot impact resistance, strength, creep resistance, phase stability and stress rupture life. 
     As alloys such as those disclosed in U.S. Pat. Nos. 4,083,734 and 4,093,476 are often coated with a dissimilar alloy to enhance their value and are usually heat treated to develop gamma prime particles of a desirable and beneficial morphology; it would be desirable to develop a precipitation hardening heat treatment which incorporates a coating operation. Obvious problems can occur when these alloys are coated prior to or subsequent to heat treating. 
     Through the present invention there is provided a series of operations through which the alloys of U.S. Pat. Nos. 4,083,734 and 4,093,476 are simultaneously heat treated and coated. The alloys are coated with a dissimilar alloy which enhances their value while being heat treated to develop gamma prime particles of a desirable and beneficial morphology. A coating operation has been successfully incorporated into a precipitation hardening heat treatment. 
     Heat treatments for a dissimilar class of nickel-base superalloys are disclosed in U.S. Pat. No. 3,653,987. One of the treatments comprises the steps of: (1) heating at a temperature of 2135° F. for 4 hours and cooling; (2) heating at a temperature of 1975° F. for 4 hours and cooling; (3) heating at a temperature of 1550° F. for 24 hours and cooling; and (4) heating at a temperature of 1400° F. for 16 hours and cooling. Another, differs from the first in that it utilizes a lower temperature during the second stage of the treatment. The maximum second stage temperature is 1850° F. A coating operation is not, however, a part of either of these treatments. U.S. Pat. No. 3,653,987 does not disclose a precipitation hardening heat treatment which incorporates a coating operation. 
     Treatments similar to that disclosed in U.S. Pat. No. 3,653,987, are disclosed in heretofore referred to U.S. Pat. Nos. 4,083,734 and 4,093,746. As with U.S. Pat. No. 3,653,987, U.S. Pat. Nos. 4,083,734 and 4,093,746 do not disclose a process wherein a coating operation is incorporated within a precipitation hardening heat treatment. 
     It is accordingly an object of the present invention to provide a precipitation hardening heat treatment which incorporates a coating operation. 
     The present invention provides a method for heat treating and coating nickel base alloys consisting essentially of, by weight, from 12.0 to 20.0% chromium, from 4.0 to 7.0% titanium, from 1.2 to 3.5% aluminum, from 12.0 to 20.0% cobalt, from 2.0 to 4.0% molybdenum, from 0.5 to 2.5% tungsten, from 0.005 to 0.048% boron, from 0.005 to 0.15% carbon, up to 0.75% manganese, up to 0.5% silicon, up to 1.5% hafnium, up to 0.1% zirconium, up to 1.0% iron, up to 0.2% of rare earth elements that will not lower the incipient melting temperature below the solvus temperature of the gamma prime present in the alloy, up to 0.1% of elements from the group consisting of magnesium, calcium, strontium and barium, up to 6.0% of elements from the group consisting of rhenium and ruthenium, balance essentially nickel; with the titanium and aluminum content being from 6.0 to 9.0% in a titanium to aluminum ratio of from 1.75:1 to 3.5:1. The method comprises the steps of heating the alloy at a temperature of at least 2050° F.; cooling the alloy; treating (heating) the alloy within the temperature range of between 1800 and 2000° F.; cooling the alloy; treating the alloy within the temperature range of between 1500° and 1800° F.; coating the alloy; treating the coated alloy at a temperature of at least 1600° F.; cooling the alloy; and treating the alloy within the temperature range of between 1300° and 1500° F. In a particular embodiment, the alloy has at least 0.031% boron as boron within the range of from 0.031 to 0.048% has been found to improve stress rupture life. In another embodiment the alloy has at least 0.015% zirconium as zirconium has been found to further improve stress rupture properties. Carbon levels are preferably kept below 0.045%, as the alloys impact strength has been found to deteriorate at higher levels after prolonged high temperature service exposure. 
     The alloy is heated at a temperature of at least 2050° F. for the primary purpose of putting most of the coarse gamma prime particles into solution. Temperatures employed are usually in excess of 2100° F. Some carbides and borides are also put into solution during this treatment. Time of treatment cannot be specified for this or any of the other treatments of this invention, as it and they are dependent upon several variables including the specific temperature employed and the size of the alloy being treated. 
     Treatment within the temperature range of between 1800° and 2000° F. is for the primary purpose of initiating the formation of and forming randomly dispersed gamma prime particles; and for the secondary purpose, of precipitating discrete (as opposed to continuous) carbide (M 23  C 6 ) and boride (M 3  B 2 ) particles at the grain boundaries. Temperatures employed are usually at least 1900° F. 
     The alloy is treated within the temperature range of between 1500° and 1800° F. to precipitate fine gamma prime particles, to coarsen existing gamma prime particles and to precipitate discrete carbide particles. Temperatures employed are usually between 1520° and 1600° F. 
     Coatings can be applied in any number of ways which include plasma spraying, vapor deposition and dipping. Those skilled in the art are well aware of the various coating techniques. As for the coating itself, it is a cobalt, nickel or iron base alloy. A cobalt, nickel or iron base alloy is one in which the primary element is cobalt, nickel or iron. Choice of a particular coating is dependent upon the purpose for which it is to be used. Coatings are applied for a variety of purposes which include hot corrosion resistance, oxidation resistance and wear resistance. 
     In order to lessen the sharp differentials which exist between the chemistry of the coating and the chemistry of the alloy, the coated alloy is treated at a temperature of at least 1600° F. to permit the coating to diffuse into the alloy. In general, this temperature is at least 1800° F. It is usually below 2000° F. 
     The alloy is treated within the temperature range of between 1300° and 1500° F. subsequent to coating and diffusion of the coating into the alloy, for the purpose of precipitating fine gamma prime particles and discrete carbide particles (M 23  C 6 ) at the grain boundaries, while substantially precluding gamma prime growth. This treatment is usually within the temperature range of between 1350° and 1450° F. 
     A treatment within the temperature range of between 1300° and 1500° F. may optionally be included after the heretofore referred to treatment between 1500° and 1800° F. and prior to coating. This treatment, like the heretofore discussed 1300° to 1500° F. treatment, is for the purpose of precipitating fine gamma prime particles and discrete carbide particles (M 23  C 6 ) at the grain boundaries, while substantially precluding gamma prime growth. It is usually within the temperature range of between 1350° and 1450° F. 
     As the series of operations described hereinabove produce a desirable alloy, it is also within the scope of the present invention to heat treat the alloys of U.S. Pat. Nos. 4,083,734 and 4,093,476 in accordance therewith, but without applying a coating thereto. In such a situation, the alloys are treated within the temperature range of between 1600° and 2000° F. (preferably 1800° and 2000° F.) subsequent to the treatment between 1500° and 1800° F. and prior to the treatment between 1300° and 1500° F. A treatment within the temperature range of between 1300° and 1500° F. may optionally be included prior to the 1600° to 2000° F. treatment. 
    
    
     The following examples are illustrative of several aspects of the invention. 
     Six samples (Samples A, A&#39;, B, B&#39;, C, C&#39;) of the following chemistry: 
     
         ______________________________________                                    
Cr   Ti     Al     Co   Mo   W    C    B    Zr   Ni                       
______________________________________                                    
18.0 4.94   2.54   14.8 3.10  1.29                                        
                                  0.034                                   
                                       0.035                              
                                            0.026                         
                                                 Bal                      
______________________________________                                    
 
    
     were treated as follows: 
     
         ______________________________________                                    
A, A&#39;                                                                     
       2135° F. - 4 Hours - Air Cool                               
       1975° F. - 4 Hours - Air Cool                               
       1550° F. - 24 Hours - Air Cool                              
       1400° F. - 16 Hours - Air Cool                              
       1900° F. - 14 Hours - Furnace Cool*                         
       1400° F. - 16 Hours - Air Cool                              
B, B&#39;                                                                     
         2135° F. - 4 Hours - Air Cool                             
         1975° F. - 4 Hours - Air Cool                             
         1550° F. - 24 Hours - Air Cool                            
         1400° F. - 16 Hours - Air Cool                            
         1900° F. - 14 Hours - Furnace Cool*                       
         1750° F. - 0.5 Hour - Air Cool                            
         1975° F. - 4 Hours - Air Cool                             
         1750° F. - 0.5 Hour - Air Cool                            
         1925° F. - 1.5 Hours - Air Cool                           
         1400° F. - 16 Hours - Air Cool                            
C, C&#39;                                                                     
       2135° F. - 4 Hours - Air Cool                               
       1975° F. - 4 Hours - Air Cool                               
       1550° F. - 24 Hours - Air Cool                              
       1900° F. - 14 Hours - Furnace Cool*                         
       1400° F. - 16 Hours - Air Cool                              
______________________________________                                    
 *simulated coating cycle                                                 
 
    
     The samples were subsequently tested for rupture life at a stress of 20 ksi and a temperature of 1800° F., as well as for elongation and reduction in area. The test results are as follows: 
     
         ______________________________________                                    
                                 Reduction                                
          Life       Elongation  in Area                                  
Sample    (hours)    (%)         (%)                                      
______________________________________                                    
A         45.1       12.4        16.0                                     
A&#39;        62.5       15.3        20.8                                     
B         51.4       14.4        17.8                                     
B&#39;        55.5       15.5        18.4                                     
C         60.0       21.9        26.2                                     
C&#39;        58.2       20.4        25.5                                     
______________________________________                                    
 
    
     The test results clearly demonstrate that the process of the present invention successfully incorporates coating cycle into a precipitation hardening heat treatment. Excellent properties are achieved even though a coating cycle is incorporated therein. 
     It will be apparent to those skilled in the art that the novel principles of the invention disclosed herein in connection with specific examples thereof will suggest various other modifications and applications of the same. It is accordingly desired that in construing the breadth of the appended claims they shall not be limited to the specific examples of the invention described herein.