Patent Publication Number: US-11639292-B2

Title: Particulate composite materials

Description:
BACKGROUND 
     Technical Field 
     Embodiments of the present invention generally relate to particulate composite materials and devices comprising the same. 
     Description of the Related Art 
     CVI is a process wherein a gaseous substrate reacts within a porous scaffold material. This approach can be employed to produce composite materials, for instance silicon-carbon composites, wherein a silicon-containing gas decomposes at elevated temperature within a porous carbon scaffold. While this approach can be employed to manufacture a variety of composite materials, there is particular interest in silicon-carbon (Si—C) composite materials. Such Si—C composite materials have utility, for example as energy storage materials, for example as an anode material within a lithium ion battery (LIB). LIBs have potential to replace devices currently used in any number of applications. For example, current lead acid automobile batteries are not adequate for next generation all-electric and hybrid electric vehicles due to irreversible, stable sulfate formations during discharge. Lithium ion batteries are a viable alternative to the lead-based systems currently used due to their capacity, and other considerations. 
     To this end, there is continued strong interest in developing new LIB anode materials, particularly silicon, which has 10-fold higher gravimetric capacity than conventional graphite. However, silicon exhibits large volume change during cycling, in turn leading to electrode deterioration and solid-electrolyte interphase (SEI) instability. The most common amelioration approach is to reduce silicon particle size, for instance D v,50 &lt;150 nm, for instance D v,50 &lt;100 nm, for instance D v,50 &lt;50 nm, for instance D v,50 &lt;20 nm, for instance D v,50 &lt;10 nm, for instance D v,50 &lt;5 nm, for instance D v,50 &lt;2 nm, either as discrete particles or within a matrix. Thus far, techniques for creating nano-scale silicon involve high-temperature reduction of silicon oxide, extensive particle diminution, multi-step toxic etching, and/or other cost prohibitive processes. Likewise, common matrix approaches involve expensive materials such as graphene or nano-graphite, and/or require complex processing and coating. 
     It is known from scientific literature that non-graphitizable (hard) carbon is beneficial as a LIB anode material (Liu Y, Xue, J S, Zheng T, Dahn, J R. Carbon 1996, 34:193-200; Wu, Y P, Fang, S B, Jiang, Y Y. 1998, 75:201-206; Buiel E, Dahn J R. Electrochim Acta 1999 45:121-130). The basis for this improved performance stems from the disordered nature of the graphene layers that allows Li-ions to intercalate on either side of the graphene plane allowing for theoretically double the stoichiometric content of Li ions versus crystalline graphite. Furthermore, the disordered structure improves the rate capability of the material by allowing Li ions to intercalate isotropically as opposed to graphite where lithiation can only proceed in parallel to the stacked graphene planes. Despite these desirable electrochemical properties, amorphous carbons have not seen wide-spread deployment in commercial Li-ion batteries, owing primarily to low FCE and low bulk density (&lt;1 g/cc). Instead, amorphous carbon has been used more commonly as a low-mass additive and coating for other active material components of the battery to improve conductivity and reduce surface side reactions. 
     In recent years, amorphous carbon as a LIB battery material has received considerable attention as a coating for silicon anode materials. Such a silicon-carbon core-shell structure has the potential for not only improving conductivity, but also buffering the expansion of silicon as it lithiates, thus stabilizing its cycle stability and minimizing problems associated with particle pulverization, isolation, and SEI integrity (Jung, Y, Lee K, Oh, S. Electrochim Acta 2007 52:7061-7067; Zuo P, Yin G, Ma Y. Electrochim Acta 2007 52:4878-4883; Ng S H, Wang J, Wexler D, Chew S Y, Liu H K. J Phys Chem C 2007 111:11131-11138). Problems associated with this strategy include the lack of a suitable silicon starting material that is amenable to the coating process, and the inherent lack of engineered void space within the carbon-coated silicon core-shell composite particle to accommodate expansion of the silicon during lithiation. This inevitably leads to cycle stability failure due to destruction of core-shell structure and SEI layer (Beattie S D, Larcher D, Morcrette M, Simon B, Tarascon, J-M. J Electrochem Soc 2008 155:A158-A163). 
     An alternative to core shell structure is a structure wherein amorophous, nano-sized silicon is homogeously distributed within the porosity of a porous carbon scaffold. The porous carbon allows for desirable properties: (i) carbon porosity provides void volume to accommodate the expansion of silicon during lithiation thus reducing the net composite particle expansion at the electrode level; (ii) the disordered graphene network provides increased electrical conductivity to the silicon thus enabling faster charge/discharge rates, (iii) nano-pore structure acts as a template for the synthesis of silicon thereby dictating its size, distribution, and morphology. 
     To this end, the desired inverse hierarchical structure can be achieved by employing CVI wherein a silicon-containing gas can completely permeate nanoporous carbon and decompose therein to nano-sized silicon. The CVI approach confers several advantages in terms of silicon structure. One advantage is that nanoporous carbon provides nucleation sites for growing silicon while dictating maximum particle shape and size. Confining the growth of silicon within a nano-porous structure affords reduced susceptibility to cracking or pulverization and loss of contact caused by expansion. Moreover, this structure promotes nano-sized silicon to remain as amorphous phase. This property provides the opportunity for high charge/discharge rates, particularly in combination with silicon&#39;s vicinity within the conductive carbon scaffold. This system provides a high-rate-capable, solid-state lithium diffusion pathway that directly delivers lithium ions to the nano-scale silicon interface. Another benefit of the silicon provide via CVI within the carbon scaffold is the inhibition of formation of undesirable crystalline Li 15 Si 4  phase. Yet another benefit is that the CVI process provides for void space within the particle interior. 
     In order to gauge relative amount of silicon impregnated into the porosity of the porous carbon, thermogravimetric analysis (TGA) may be employed. TGA can be employed to assess the fraction of silicon residing within the porosity of porous carbon relative to the total silicon present, i.e., sum of silicon within the porosity and on the particle surface. As the silicon-carbon composite is heated under air, the sample exhibits a mass increase that intiates at about 300° C. to 500° C. that reflects initial oxidation of silicon to SiO2, and then the sample exhibits a mass loss as the carbon is burned off, and then the sample exhibits mass increase reflecting resumed conversion of silicon into SiO2 which increases towards an asymptotic value as the temperature approaches 1100° C. as silicon oxidizes to completion. For the purposes of this analysis, it is assumed that the minimum mass recorded for the sample as it heated from 800° C. to 1100° C. represents the point at which carbon buroff is complete. Any further mass increase beyond that point corresponds to the oxidation of silicon to SiO2 and that the total mass at completion of oxidation is SiO2. Thus, the percentage of unoxidized silicon after carbon burnoff as a proportion of the total amount of silicon can be determined using the formula:
 
Z=1.875×[( M 1100− M )/ M 1100]×100%
 
where M1100 is the mass of the sample at completion of oxidation at a temperature of 1100° C., and M is the minimum mass recorded for the sample as it is heated from 800° C. to 1100° C.
 
     Without being bound by theory, the temperature at which silicon is oxidized under TGA conditions relates to the length scale of the oxide coating on the silicon due to the diffusion of oxygen atoms through the oxide layer. Thus, silicon residing within the carbon porosity will oxidize at a lower temperature than deposits of silicon on a particle surface due to the necessarily thinner coating exisiting on these surfaces. In this fashion, calculation of Z is used to quantitatively assess the fraction of silicon not impreganted within the porosity of the porous carbon scaffold. 
     BRIEF SUMMARY 
     Composites comprising Group14 elements such as silicon and carbon, are disclosed, wherein said composites have novel properties that overcome the challenges for providing amorphous nano-sized silicon entrained within porous carbon. Said silicon-carbon composites may be produced via chemical vapor infiltration to impregnate amorphous, nano-sized silicon within the pores of a porous scaffold. Suitable porous scaffolds include, but are not limited to, porous carbon scaffolds, for example carbon having a pore volume comprising micropores (less than 2 nm), mesopores (2 to 50 nm), and/or macropores (greater than 50 nm). Suitable precursors for the carbon scaffold include, but are not limited to, sugars and polyols, organic acids, phenolic compounds, cross-linkers, and amine compounds. Suitable compositing materials include, but are not limited to, silicon materials. Precursors for the silicon include, but are not limited to, silicon containing gases such as silane, high-order silanes (such as di-, tri-, and/or tetrasilane), and/or chlorosilane(s) (such as mono-,di-, tri-, and tetrachlorosilane) and mixtures thereof. CVI to produce silicon within the pores of porous scaffold materials is accomplished by exposing said porous scaffold to silicon-containing gas (e.g., silane) at elevated temperatures. The porous carbon scaffold can be a particulate porous carbon. 
     A key outcome in this regard is to achieve the desired form of silicon in the desired form, namely amorphous nano-sized silicon. Furthermore, another key outcome is to achieve the silicon impregnation within the pores of the porous carbon. Such materials, for example, silicon-carbon composite materials, have utility as anode materials for energy storage devices, for example lithium ion batteries. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG.  1   . Relationship between Z and average Coulombic efficiency for various silicon-carbon composite materials. 
         FIG.  2   . Differential capacity vs voltage plot for Silicon-Carbon Composite 3 from 2′ cycle using a half-cell. 
         FIG.  3   . Differential capacity vs voltage plot for Silicon-Carbon Composite 3 from 2′ cycle to 5 th  cycle using a half-cell. 
         FIG.  4   . dQ/dV vs V plot for various silicon-carbon composite materials. 
         FIG.  5   . Example of Calculation of φ for Silicon-Carbon Composite 3. 
         FIG.  6   . Z vs φ plot for various silicon-carbon composite materials. 
     
    
    
     DETAILED DESCRIPTION 
     In the following description, certain specific details are set forth in order to provide a thorough understanding of various embodiments. However, one skilled in the art will understand that the invention may be practiced without these details. In other instances, well-known structures have not been shown or described in detail to avoid unnecessarily obscuring descriptions of the embodiments. Unless the context requires otherwise, throughout the specification and claims which follow, the word “comprise” and variations thereof, such as, “comprises” and “comprising” are to be construed in an open, inclusive sense, that is, as “including, but not limited to.” Further, headings provided herein are for convenience only and do not interpret the scope or meaning of the claimed invention. 
     Reference throughout this specification to “one embodiment” or “an embodiment” means that a particular feature, structure or characteristic described in connection with the embodiment is included in at least one embodiment. Thus, the appearances of the phrases “in one embodiment” or “in an embodiment” in various places throughout this specification are not necessarily all referring to the same embodiment. Furthermore, the particular features, structures, or characteristics may be combined in any suitable manner in one or more embodiments. Also, as used in this specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the content clearly dictates otherwise. It should also be noted that the term “or” is generally employed in its sense including “and/or” unless the content clearly dictates otherwise. 
     A. Porous Scaffold Materials 
     For the purposes of embodiments of the current invention, a porous scaffold may be used, into which silicon is to be impregnated. In this context, the porous scaffold can comprise various materials. In some embodiments the porous scaffold material primarily comprises carbon, for example hard carbon. Other allotropes of carbon are also envisioned in other embodiments, for example, graphite, amorphous carbon, diamond, C60, carbon nanotubes (e.g., single and/or multi-walled), graphene and/or carbon fibers. The introduction of porosity into the carbon material can be achieved by a variety of means. For instance, the porosity in the carbon material can be achieved by modulation of polymer precursors, and/or processing conditions to create said porous carbon material, and described in detail in the subsequent section. 
     In other embodiments, the porous scaffold comprises a polymer material. To this end, a wide variety of polymers are envisioned in various embodiments to have utility, including, but not limited to, inorganic polymer, organic polymers, and addition polymers. Examples of inorganic polymers in this context includes, but are not limited to homochain polymers of silicon-silicon such as polysilanes, silicon carbide, polygermanes, and polystannanes. Additional examples of inorganic polymers includes, but are not limited to, heterochain polymers such as polyborazylenes, polysiloxanes like polydimethylsiloxane (PDMS), polymethylhydrosiloxane (PMHS) and polydiphenylsiloxane, polysilazanes like perhydridopolysilazane (PHPS), polyphosphazenes and poly(dichlorophosphazenes), polyphosphates, polythiazyls, and polysulfides. Examples of organic polymers includes, but are not limited to, low density polyethylene (LDPE), high density polyethylene (HDPE), polypropylene (PP), polyvinyl chloride (PVC), polystyrene (PS), nylon, nylon 6, nylon 6,6, teflon (Polytetrafluoroethylene), thermoplastic polyurethanes (TPU), polyureas, poly(lactide), poly(glycolide) and combinations thereof, phenolic resins, polyamides, polyaramids, polyethylene terephthalate, polychloroprene, polyacrylonitrile, polyaniline, polyimide, poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PDOT:PSS), and others known in the arts. The organic polymer can be synthetic or natural in origin. In some embodiments, the polymer is a polysaccharide, such as starch, cellulose, cellobiose, amylose, amylpectin, gum Arabic, lignin, and the like. In some embodiments, the polysaccharide is derived from the carmelization of mono- or oligomeric sugars, such as fructose, glucose, sucrose, maltose, raffinose, and the like. 
     In certain embodiments, the porous scaffold polymer material comprises a coordination polymer. Coordination polymers in this context include, but are not limited to, metal organic frameworks (MOFs). Techniques for production of MOFs, as well as exemplary species of MOFs, are known and described in the art (“The Chemistry and Applications of Metal-Organic Frameworks, Hiroyasu Furukawa et al. Science 341, (2013); DOI: 10.1126/science.1230444). Examples of MOFs in the context include, but are not limited to, Basolite™ materials and zeolitic imidazolate frameworks (ZIFs). 
     Concomitant with the myriad variety of polymers envisioned with the potential to provide a porous substrate, various processing approaches are envisioned in various embodiments to achieve said porosity. In this context, general methods for imparting porosity into various materials are myriad, as known in the art, including, but certainly not limited to, methods involving emulsification, micelle creation, gasification, dissolution followed by solvent removal (for example, lyophilization), axial compaction and sintering, gravity sintering, powder rolling and sintering, isostatic compaction and sintering, metal spraying, metal coating and sintering, metal injection molding and sintering, and the like. Other approaches to create a porous polymeric material, including creation of a porous gel, such as a freeze dried gel, aerogel, and the like are also envisioned. 
     In certain embodiments, the porous scaffold material comprises a porous ceramic material. In certain embodiments, the porous scaffold material comprises a porous ceramic foam. In this context, general methods for imparting porosity into ceramic materials are varied, as known in the art, including, but certainly not limited to, creation of porous In this context, general methods and materials suitable for comprising the porous ceramic include, but are not limited to, porous aluminum oxide, porous zirconia toughened alumina, porous partially stabilized zirconia, porous alumina, porous sintered silicon carbide, sintered silicon nitride, porous cordierite, porous zirconium oxide, clay-bound silicon carbide, and the like. 
     In certain embodiments, the porous scaffold comprises porous silica or other silicon material containing oxygen. The creation of silicon gels, including sol gels, and other porous silica materials is known in the art. 
     In certain embodiments, the porous material comprises a porous metal. Suitable metals in this regard include, but are not limited to porous aluminum, porous steel, porous nickel, porous Inconcel, porous Hasteloy, porous titanium, porous copper, porous brass, porous gold, porous silver, porous germanium, and other metals capable of being formed into porous structures, as known in the art. In some embodiments, the porous scaffold material comprises a porous metal foam. The types of metals and methods to manufacture related to same are known in the art. Such methods include, but are not limited to, casting (including foaming, infiltration, and lost-foam casting), deposition (chemical and physical), gas-eutectic formation, and powder metallurgy techniques (such as powder sintering, compaction in the presence of a foaming agent, and fiber metallurgy techniques). 
     B. Porous Carbon Scaffold 
     Methods for preparing porous carbon materials from polymer precursors are known in the art. For example, methods for preparation of carbon materials are described in U.S. Pat. Nos. 7,723,262, 8,293,818, 8,404,384, 8,654,507, 8,916,296, 9,269,502, 10,590,277, and U.S. patent application Ser. No. 16/745,197, the full disclosures of which are hereby incorporated by reference in their entireties for all purposes. 
     Accordingly, in one embodiment the present disclosure provides a method for preparing any of the carbon materials or polymer gels described above. The carbon materials may be synthesized through pyrolysis of either a single precursor, for example a saccharide material such as sucrose, fructose, glucose, dextrin, maltodextrin, starch, amylopectin, amlyose, lignin, gum Arabic, and other saccharides known in the art, and combinations thereof. Alternatively, the carbon materials may be synthesized through pyrolysis of a complex resin, for instance formed using a sol-gel method using polymer precursors such as phenol, resorcinol, bisphenol A, urea, melamine, and other suitable compounds known in the art, and combinations thereof, in a suitable solvent such as water, ethanol, methanol, and other solvents known in the art, and combinations thereof, with cross-linking agents such as formaldehyde, hexamethylenetetramine, furfural, and other cross-lining agents known in the art, and combinations thereof. The resin may be acid or basic, and may contain a catalyst. The catalyst may be volatile or non-volatile. The pyrolysis temperature and dwell time can vary as known in the art. 
     In some embodiments, the methods comprise preparation of a polymer gel by a sol gel process, condensation process or crosslinking process involving monomer precursor(s) and a crosslinking agent, two existing polymers and a crosslinking agent or a single polymer and a crosslinking agent, followed by pyrolysis of the polymer gel. The polymer gel may be dried (e.g., freeze dried) prior to pyrolysis; however drying is not necessarily required. 
     The target carbon properties can be derived from a variety of polymer chemistries provided the polymerization reaction produces a resin/polymer with the necessary carbon backbone. Different polymer families include novolacs, resoles, acrylates, styrenics, ureathanes, rubbers (neoprenes, styrene-butadienes, etc.), nylons, etc. The preparation of any of these polymer resins can occur via a number of different processes including sol gel, emulsion/suspension, solid state, solution state, melt state, etc for either polymerization and crosslinking processes. 
     In some embodiments an electrochemical modifier is incorporated into the material as polymer. For example, the organic or carbon containing polymer, RF for example, is copolymerized with the polymer, which contains the electrochemical modifier. In one embodiment, the electrochemical modifier-containing polymer contains silicon. In one embodiment the polymer is tetraethylorthosiliane (TEOS). In one embodiment, a TEOS solution is added to the RF solution prior to or during polymerization. In another embodiment the polymer is a polysilane with organic side groups. In some cases these side groups are methyl groups, in other cases these groups are phenyl groups, in other cases the side chains include phenyl, pyrol, acetate, vinyl, siloxane fragments. In some cases the side chain includes a group 14 element (silicon, germanium, tin or lead). In other cases the side chain includes a group 13 element (boron, aluminum, boron, gallium, indium). In other cases the side chain includes a group 15 element (nitrogen, phosphorous, arsenic). In other cases the side chain includes a group 16 element (oxygen, sulfur, selenium). 
     In another embodiment the electrochemical modifier comprises a silole. In some cases it is a phenol-silole or a silafluorene. In other cases it is a poly-silole or a poly-silafluorene. In some cases the silicon is replaced with germanium (germole or germafluorene), tin (stannole or stannaflourene) nitrogen (carbazole) or phosphorous (phosphole, phosphafluorene). In all cases the heteroatom containing material can be a small molecule, an oligomer or a polymer. Phosphorous atoms may or may not be also bonded to oxygen. 
     In some embodiments the reactant comprises phosphorous. In certain other embodiments, the phosphorus is in the form of phosphoric acid. In certain other embodiments, the phosphorus can be in the form of a salt, wherein the anion of the salt comprises one or more phosphate, phosphite, phosphide, hydrogen phosphate, dihydrogen phosphate, hexafluorophosphate, hypophosphite, polyphosphate, or pyrophosphate ions, or combinations thereof. In certain other embodiments, the phosphorus can be in the form of a salt, wherein the cation of the salt comprises one or more phosphonium ions. The non-phosphate containing anion or cation pair for any of the above embodiments can be chosen for those known and described in the art. In the context, exemplary cations to pair with phosphate-containing anions include, but are not limited to, ammonium, tetraethylammonium, and tetramethylammonium ions. In the context, exemplary anions to pair with phosphate-containing cations include, but are not limited to, carbonate, dicarbonate, and acetate ions. 
     In some embodiments, the catalyst comprises a basic volatile catalyst. For example, in one embodiment, the basic volatile catalyst comprises ammonium carbonate, ammonium bicarbonate, ammonium acetate, ammonium hydroxide, or combinations thereof. In a further embodiment, the basic volatile catalyst is ammonium carbonate. In another further embodiment, the basic volatile catalyst is ammonium acetate. 
     In still other embodiments, the method comprises admixing an acid. In certain embodiments, the acid is a solid at room temperature and pressure. In some embodiments, the acid is a liquid at room temperature and pressure. In some embodiments, the acid is a liquid at room temperature and pressure that does not provide dissolution of one or more of the other polymer precursors. 
     The acid may be selected from any number of acids suitable for the polymerization process. For example, in some embodiments the acid is acetic acid and in other embodiments the acid is oxalic acid. In further embodiments, the acid is mixed with the first or second solvent in a ratio of acid to solvent of 99:1, 90:10, 75:25, 50:50, 25:75, 20:80, 10:90 or 1:90. In other embodiments, the acid is acetic acid and the first or second solvent is water. In other embodiments, acidity is provided by adding a solid acid. 
     The total content of acid in the mixture can be varied to alter the properties of the final product. In some embodiments, the acid is present from about 1% to about 50% by weight of mixture. In other embodiments, the acid is present from about 5% to about 25%. In other embodiments, the acid is present from about 10% to about 20%, for example about 10%, about 15% or about 20%. 
     In certain embodiments, the polymer precursor components are blended together and subsequently held for a time and at a temperature sufficient to achieve polymerization. One or more of the polymer precursor components can have particle size less than about 20 mm in size, for example less than 10 mm, for example less than 7 mm, for example, less than 5 mm, for example less than 2 mm, for example less than 1 mm, for example less than 100 microns, for example less than 10 microns. In some embodiments, the particle size of one or more of the polymer precursor components is reduced during the blending process. 
     The blending of one or more polymer precursor components in the absence of solvent can be accomplished by methods described in the art, for example ball milling, jet milling, Fritsch milling, planetary mixing, and other mixing methodologies for mixing or blending solid particles while controlling the process conditions (e.g., temperature). The mixing or blending process can be accomplished before, during, and/or after (or combinations thereof) incubation at the reaction temperature. 
     Reaction parameters include aging the blended mixture at a temperature and for a time sufficient for the one or more polymer precursors to react with each other and form a polymer. In this respect, suitable aging temperature ranges from about room temperature to temperatures at or near the melting point of one or more of the polymer precursors. In some embodiments, suitable aging temperature ranges from about room temperature to temperatures at or near the glass transition temperature of one or more of the polymer precursors. For example, in some embodiments the solvent free mixture is aged at temperatures from about 20° C. to about 600° C., for example about 20° C. to about 500° C., for example about 20° C. to about 400° C., for example about 20° C. to about 300° C., for example about 20° C. to about 200° C. In certain embodiments, the solvent free mixture is aged at temperatures from about 50 to about 250° C. 
     The reaction duration is generally sufficient to allow the polymer precursors to react and form a polymer, for example the mixture may be aged anywhere from 1 hour to 48 hours, or more or less depending on the desired result. Typical embodiments include aging for a period of time ranging from about 2 hours to about 48 hours, for example in some embodiments aging comprises about 12 hours and in other embodiments aging comprises about 4-8 hours (e.g., about 6 hours). 
     In certain embodiments, an electrochemical modifier is incorporated during the above described polymerization process. For example, in some embodiments, an electrochemical modifier in the form of metal particles, metal paste, metal salt, metal oxide or molten metal can be dissolved or suspended into the mixture from which the gel resin is produced 
     Exemplary electrochemical modifiers for producing composite materials may fall into one or more than one of the chemical classifications. In some embodiments, the electrochemical modifier is a lithium salt, for example, but not limited to, lithium fluoride, lithium chloride, lithium carbonate, lithium hydroxide, lithium benzoate, lithium bromide, lithium formate, lithium hexafluorophosphate, lithium iodate, lithium iodide, lithium perchlorate, lithium phosphate, lithium sulfate, lithium tetraborate, lithium tetrafluoroborate, and combinations thereof. 
     In certain embodiments, the electrochemical modifier comprises a metal, and exemplary species includes, but are not limited to aluminum isoproproxide, manganese acetate, nickel acetate, iron acetate, tin chloride, silicon chloride, and combinations thereof. In certain embodiments, the electrochemical modifier is a phosphate compound, including but not limited to phytic acid, phosphoric acid, ammonium dihydrogenphosphate, and combinations thereof. In certain embodiments, the electrochemical modifier comprises silicon, and exemplary species includes, but are not limited to silicon powders, silicon nanotubes, polycrystalline silicon, nanocrystalline silicon, amorpohous silicon, porous silicon, nano sized silicon, nano-featured silicon, nano-sized and nano-featured silicon, silicyne, and black silicon, and combinations thereof. 
     Electrochemical modifiers can be combined with a variety of polymer systems through either physical mixing or chemical reactions with latent (or secondary) polymer functionality. Examples of latent polymer functionality include, but are not limited to, epoxide groups, unsaturation (double and triple bonds), acid groups, alcohol groups, amine groups, basic groups. Crosslinking with latent functionality can occur via heteroatoms (e.g. vulcanization with sulfur, acid/base/ring opening reactions with phosphoric acid), reactions with organic acids or bases (described above), coordination to transition metals (including but not limited to Ti, Cr, Mn, Fe, Co, Ni, Cu, Zn, Zr, Nb, Mo, Ag, Au), ring opening or ring closing reactions (rotaxanes, spiro compounds, etc). 
     Electrochemical modifiers can also be added to the polymer system through physical blending. Physical blending can include but is not limited to melt blending of polymers and/or co-polymers, the inclusion of discrete particles, chemical vapor deposition of the electrochemical modifier and coprecipitation of the electrochemical modifier and the main polymer material. 
     In some instances the electrochemical modifier can be added via a metal salt solid, solution, or suspension. The metal salt solid, solution or suspension may comprise acids and/or alcohols to improve solubility of the metal salt. In yet another variation, the polymer gel (either before or after an optional drying step) is contacted with a paste comprising the electrochemical modifier. In yet another variation, the polymer gel (either before or after an optional drying step) is contacted with a metal or metal oxide sol comprising the desired electrochemical modifier. 
     In addition to the above exemplified electrochemical modifiers, the composite materials may comprise one or more additional forms (i.e., allotropes) of carbon. In this regard, it has been found that inclusion of different allotropes of carbon such as graphite, amorphous carbon, conductive carbon, carbon black, diamond, C60, carbon nanotubes (e.g., single and/or multi-walled), graphene and/or carbon fibers into the composite materials is effective to optimize the electrochemical properties of the composite materials. The various allotropes of carbon can be incorporated into the carbon materials during any stage of the preparation process described herein. For example, during the solution phase, during the gelation phase, during the curing phase, during the pyrolysis phase, during the milling phase, or after milling. In some embodiments, the second carbon form is incorporated into the composite material by adding the second carbon form before or during polymerization of the polymer gel as described in more detail herein. The polymerized polymer gel containing the second carbon form is then processed according to the general techniques described herein to obtain a carbon material containing a second allotrope of carbon. 
     In a preferred embodiment, the carbon is produced from precursors with little of no solvent required for processing (solven free). The structure of the polymer precursors suitable for use in a low solvent or essentially solvent free reaction mixture is not particularly limited, provided that the polymer precursor is capable of reacting with another polymer precursor or with a second polymer precursor to form a polymer. Polymer precursors include amine-containing compounds, alcohol-containing compounds and carbonyl-containing compounds, for example in some embodiments the polymer precursors are selected from an alcohol, a phenol, a polyalcohol, a sugar, an alkyl amine, an aromatic amine, an aldehyde, a ketone, a carboxylic acid, an ester, a urea, an acid halide and an isocyanate. 
     In one embodiment employing a low or essentially solvent free reaction mixture, the method comprises use of a first and second polymer precursor, and in some embodiments the first or second polymer precursor is a carbonyl containing compound and the other of the first or second polymer precursor is an alcohol containing compound. In some embodiments, a first polymer precursor is a phenolic compound and a second polymer precursor is an aldehyde compound (e.g., formaldehyde). In one embodiment, of the method the phenolic compound is phenol, resorcinol, catechol, hydroquinone, phloroglucinol, or a combination thereof; and the aldehyde compound is formaldehyde, acetaldehyde, propionaldehyde, butyraldehyde, benzaldehyde, cinnamaldehyde, or a combination thereof. In a further embodiment, the phenolic compound is resorcinol, phenol or a combination thereof, and the aldehyde compound is formaldehyde. In yet further embodiments, the phenolic compound is resorcinol and the aldehyde compound is formaldehyde. In some embodiments, the polymer precursors are alcohols and carbonyl compounds (e.g., resorcinol and aldehyde) and they are present in a ratio of about 0.5:1.0, respectively. 
     The polymer precursor materials suitable for low or essentially solvent free reaction mixture as disclosed herein include (a) alcohols, phenolic compounds, and other mono- or polyhydroxy compounds and (b) aldehydes, ketones, and combinations thereof. Representative alcohols in this context include straight chain and branched, saturated and unsaturated alcohols. Suitable phenolic compounds include polyhydroxy benzene, such as a dihydroxy or trihydroxy benzene. Representative polyhydroxy benzenes include resorcinol (i.e., 1,3-dihydroxy benzene), catechol, hydroquinone, and phloroglucinol. Other suitable compounds in this regard are bisphenols, for instance, bisphenol A. Mixtures of two or more polyhydroxy benzenes can also be used. Phenol (monohydroxy benzene) can also be used. Representative polyhydroxy compounds include sugars, such as glucose, sucrose, fructose, chitin and other polyols, such as mannitol. Aldehydes in this context include: straight chain saturated aldeydes such as methanal (formaldehyde), ethanal (acetaldehyde), propanal (propionaldehyde), butanal (butyraldehyde), and the like; straight chain unsaturated aldehydes such as ethenone and other ketenes, 2-propenal (acrylaldehyde), 2-butenal (crotonaldehyde), 3 butenal, and the like; branched saturated and unsaturated aldehydes; and aromatic-type aldehydes such as benzaldehyde, salicylaldehyde, hydrocinnamaldehyde, and the like. Suitable ketones include: straight chain saturated ketones such as propanone and 2 butanone, and the like; straight chain unsaturated ketones such as propenone, 2 butenone, and 3 butenone (methyl vinyl ketone) and the like; branched saturated and unsaturated ketones; and aromatic-type ketones such as methyl benzyl ketone (phenylacetone), ethyl benzyl ketone, and the like. The polymer precursor materials can also be combinations of the precursors described above. 
     In some embodiments, one polymer precursor in the low or essentially solvent free reaction mixture is an alcohol-containing species and another polymer precursor is a carbonyl-containing species. The relative amounts of alcohol-containing species (e.g., alcohols, phenolic compounds and mono- or poly-hydroxy compounds or combinations thereof) reacted with the carbonyl containing species (e.g. aldehydes, ketones or combinations thereof) can vary substantially. In some embodiments, the ratio of alcohol-containing species to aldehyde species is selected so that the total moles of reactive alcohol groups in the alcohol-containing species is approximately the same as the total moles of reactive carbonyl groups in the aldehyde species. Similarly, the ratio of alcohol-containing species to ketone species may be selected so that the total moles of reactive alcohol groups in the alcohol containing species is approximately the same as the total moles of reactive carbonyl groups in the ketone species. The same general 1:1 molar ratio holds true when the carbonyl-containing species comprises a combination of an aldehyde species and a ketone species. 
     In other embodiments, the polymer precursor in the low or essentially solvent free reaction mixture is a urea or an amine containing compound. For example, in some embodiments the polymer precursor is urea, melamine, hexamethylenetetramine (HMT) or combination thereof. Other embodiments include polymer precursors selected from isocyanates or other activated carbonyl compounds such as acid halides and the like. 
     Some embodiments of the disclosed methods include preparation of low or solvent-free polymer gels (and carbon materials) comprising electrochemical modifiers. Such electrochemical modifiers include, but are not limited to nitrogen, silicon, and sulfur. In other embodiments, the electrochemical modifier comprises fluorine, iron, tin, silicon, nickel, aluminum, zinc, or manganese. The electrochemical modifier can be included in the preparation procedure at any step. For example, in some the electrochemical modifier is admixed with the mixture, the polymer phase or the continuous phase. 
     The blending of one or more polymer precursor components in the absence of solvent can be accomplished by methods described in the art, for example ball milling, jet milling, Fritsch milling, planetary mixing, and other mixing methodologies for mixing or blending solid particles while controlling the process conditions (e.g., temperature). The mixing or blending process can be accomplished before, during, and/or after (or combinations thereof) incubation at the reaction temperature. 
     Reaction parameters include aging the blended mixture at a temperature and for a time sufficient for the one or more polymer precursors to react with each other and form a polymer. In this respect, suitable aging temperature ranges from about room temperature to temperatures at or near the melting point of one or more of the polymer precursors. In some embodiments, suitable aging temperature ranges from about room temperature to temperatures at or near the glass transition temperature of one or more of the polymer precursors. For example, in some embodiments the solvent free mixture is aged at temperatures from about 20° C. to about 600° C., for example about 20° C. to about 500° C., for example about 20° C. to about 400° C., for example about 20° C. to about 300° C., for example about 20° C. to about 200° C. In certain embodiments, the solvent free mixture is aged at temperatures from about 50 to about 250° C. 
     The porous carbon material can be achieved via pyrolysis of a polymer produced from precursors materials as described above. In some embodiments, the porous carbon material comprises an amorphous activated carbon that is produced by pyrolysis, physical or chemical activation, or combination thereof in either a single process step or sequential process steps. 
     The temperature and dwell time of pyrolysis can be varied, for example the dwell time van vary from 1 min to 10 min, from 10 min to 30 min, from 30 min to 1 hour, for 1 hour to 2 hours, from 2 hours to 4 hours, from 4 hours to 24 h. The temperature can be varied, for example, the pyrolysis temperature can vary from 200 to 300 C, from 250 to 350 C, from 350 C to 450 C, from 450 C to 550 C, from 540 C to 650 C, from 650 C to 750 C, from 750 C to 850 C, from 850 C to 950 C, from 950 C to 1050 C, from 1050 C to 1150 C, from 1150 C to 1250 C. The pyrolysis can be accomplished in an inert gas, for example nitrogen, or argon. 
     In some embodiments, an alternate gas is used to further accomplish carbon activation. In certain embodiments, pyrolysis and activation are combined. Suitable gases for accomplishing carbon activation include, but are not limited to, carbon dioxide, carbon monoxide, water (steam), air, oxygen, and further combinations thereof. The temperature and dwell time of activation can be varied, for example the dwell time van vary from 1 min to 10 min, from 10 min to 30 min, from 30 min to 1 hour, for 1 hour to 2 hours, from 2 hours to 4 hours, from 4 hours to 24 h. The temperature can be varied, for example, the pyrolysis temperature can vary from 200 to 300 C, from 250 to 350 C, from 350 C to 450 C, from 450 C to 550 C, from 540 C to 650 C, from 650 C to 750 C, from 750 C to 850 C, from 850 C to 950 C, from 950 C to 1050 C, from 1050 C to 1150 C, from 1150 C to 1250 C. 
     Either prior to the pyrolysis, and/or after pyrolysis, and/or after activation, the carbon may be subjected to a particle size reduction. The particle size reduction can be accomplished by a variety of techniques known in the art, for example by jet milling in the presence of various gases including air, nitrogen, argon, helium, supercritical steam, and other gases known in the art. Other particle size reduction methods, such as grinding, ball milling, jet milling, water jet milling, and other approaches known in the art are also envisioned. 
     The porous carbon saffold may be in the form of particles. The particle size and particle size distribution can be measured by a variety of techniques known in the art, and can be described based on fractional volume. In this regard, the Dv,50 of the carbon scaffold may be between 10 nm and 10 mm, for example between 100 nm and 1 mm, for example between 1 um and 100 um, for example between 2 um and 50 um, example between 3 um and 30 um, example between 4 um and 20 um, example between 5 um and 10 um. In certain embodiments, the Dv,50 is less than 1 mm, for example less than 100 um, for example less than 50 um, for example less than 30 um, for example less than 20 um, for example less than 10 um, for example less than 8 um, for example less than 5 um, for example less than 3 um, for example less than 1 um. In certain embodiments, the Dv,100 is less than 1 mm, for example less than 100 um, for example less than 50 um, for example less than 30 um, for example less than 20 um, for example less than 10 um, for example less than 8 um, for example less than 5 um, for example less than 3 um, for example less than 1 um. In certain embodiments, the Dv,99 is less than 1 mm, for example less than 100 um, for example less than 50 um, for example less than 30 um, for example less than 20 um, for example less than 10 um, for example less than 8 um, for example less than 5 um, for example less than 3 um, for example less than 1 um. In certain embodiments, the Dv,90 is less than 1 mm, for example less than 100 um, for example less than 50 um, for example less than 30 um, for example less than 20 um, for example less than 10 um, for example less than 8 um, for example less than 5 um, for example less than 3 um, for example less than 1 um. In certain embodiments, the Dv,0 is greater than 10 nm, for example greater than 100 nm, for example greater than 500 nm, for example greater than 1 um, for example greater than 2 um, for example greater than 5 um, for example greater than 10 um. In certain embodiments, the Dv,1 is greater than 10 nm, for example greater than 100 nm, for example greater than 500 nm, for example greater than 1 um, for example greater than 2 um, for example greater than 5 um, for example greater than 10 um. In certain embodiments, the Dv,10 is greater than 10 nm, for example greater than 100 nm, for example greater than 500 nm, for example greater than 1 um, for example greater than 2 um, for example greater than 5 um, for example greater than 10 um. 
     In some embodiments, the surface area of the porous carbon scaffold can comprise a surface area greater than 400 m2/g, for example greater than 500 m2/g, for example greater than 750 m2/g, for example greater than 1000 m2/g, for example greater than 1250 m2/g, for example greater than 1500 m2/g, for example greater than 1750 m2/g, for example greater than 2000 m2/g, for example greater than 2500 m2/g, for example greater than 3000 m2/g. In other embodiments, the surface area of the porous carbon scaffold can be less than 500 m2/g. In some embodiments, the surface area of the porous carbon scaffold is between 200 and 500 m2/g. In some embodiments, the surface area of the porous carbon scaffold is between 100 and 200 m2/g. In some embodiments, the surface area of the porous carbon scaffold is between 50 and 100 m2/g. In some embodiments, the surface area of the porous carbon scaffold is between 10 and 50 m2/g. In some embodiments, the surface area of the porous carbon scaffold can be less than 10 m2/g. 
     In some embodiments, the pore volume of the porous carbon scaffold is greater than 0.4 cm3/g, for example greater than 0.5 cm3/g, for example greater than 0.6 cm3/g, for example greater than 0.7 cm3/g, for example greater than 0.8 cm3/g, for example greater than 0.9 cm3/g, for example greater than 1.0 cm3/g, for example greater than 1.1 cm3/g, for example greater than 1.2 cm3/g, for example greater than 1.4 cm3/g, for example greater than 1.6 cm3/g, for example greater than 1.8 cm3/g, for example greater than 2.0 cm3/g. In other embodiments, the pore volume of the porous silicon scaffold is less than 0.5 cm3, for example between 0.1 cm3/g and 0.5 cm3/g. In certain other embodiments, the pore volume of the porous silicon scaffold is between 0.01 cm3/g and 0.1 cm3/g. 
     In some other embodiments, the porous carbon scaffold is an amorphous activated carbon with a pore volume between 0.2 and 2.0 cm3/g. In certain embodiments, the carbon is an amorphous activated carbon with a pore volume between 0.4 and 1.5 cm3/g. In certain embodiments, the carbon is an amorphous activated carbon with a pore volume between 0.5 and 1.2 cm3/g. In certain embodiments, the carbon is an amorphous activated carbon with a pore volume between 0.6 and 1.0 cm3/g. 
     In some other embodiments, the porous carbon scaffold comprises a tap density of less than 1.0 g/cm3, for example less than 0.8 g/cm3, for example less than 0.6 g/cm3, for example less than 0.5 g/cm3, for example less than 0.4 g/cm3, for example less than 0.3 g/cm3, for example less than 0.2 g/cm3, for example less than 0.1 g/cm3. 
     The surface functionality of the porous carbon scaffold can vary. One property which can be predictive of surface functionality is the pH of the porous carbon scaffold. The presently disclosed porous carbon scaffolds comprise pH values ranging from less than 1 to about 14, for example less than 5, from 5 to 8 or greater than 8. In some embodiments, the pH of the porous carbon is less than 4, less than 3, less than 2 or even less than 1. In other embodiments, the pH of the porous carbon is between about 5 and 6, between about 6 and 7, between about 7 and 8 or between 8 and 9 or between 9 and 10. In still other embodiments, the pH is high and the pH of the porous carbon ranges is greater than 8, greater than 9, greater than 10, greater than 11, greater than 12, or even greater than 13. 
     The pore volume distribution of the porous carbon scaffold can vary. For example, the % micropores can comprise less than 30%, for example less than 20%, for example less than 10%, for example less than 5%, for example less than 4%, for example less than 3%, for example less than 2%, for example less than 1%, for example less than 0.5%, for example less than 0.2%, for example, less than 0.1%. In certain embodiments, there is no detectable micropore volume in the porous carbon scaffold. 
     The mesopores comprising the porous carbon scaffold scaffold can vary. For example, the % mesopores can comprise less than 30%, for example less than 20%, for example less than 10%, for example less than 5%, for example less than 4%, for example less than 3%, for example less than 2%, for example less than 1%, for example less than 0.5%, for example less than 0.2%, for example, less than 0.1%. In certain embodiments, there is no detectable mesopore volume in the porous carbon scaffold. 
     In some embodiments, the pore volume distribution of the porous carbon scaffold scaffold comprises more than 50% macropores, for example more than 60% macropores, for example more than 70% macropores, for example more than 80% macropores, for example more than 90% macropores, for example more than 95% macropores, for example more than 98% macropores, for example more than 99% macropores, for example more than 99.5% macropores, for example more than 99.9% macropores. 
     In certain preferred embodiments, the pore volume of the porous carbon scaffold comprises a blend of micropores, mesopores, and macropores. Accordingly, in certain embodiments, the porous carbon scaffold comprises 0-20% micropores, 30-70% mesopores, and less than 10% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-20% micropores, 0-20% mesopores, and 70-95% macropores. In certain other embodiments, the porous carbon scaffold comprises 20-50% micropores, 50-80% mesopores, and 0-10% macropores. In certain other embodiments, the porous carbon scaffold comprises 40-60% micropores, 40-60% mesopores, and 0-10% macropores. In certain other embodiments, the porous carbon scaffold comprises 80-95% micropores, 0-10% mesopores, and 0-10% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-10% micropores, 30-50% mesopores, and 50-70% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-10% micropores, 70-80% mesopores, and 0-20% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-20% micropores, 70-95% mesopores, and 0-10% macropores. In certain other embodiments, the porous carbon scaffold comprises 0-10% micropores, 70-95% mesopores, and 0-20% macropores. 
     In certain embodiments, the % of pore volume in the porous carbon scaffold representing pores between 100 and 1000 A (10 and 100 nm) comprises greater than 30% of the total pore volume, for example greater than 40% of the total pore volume, for example greater than 50% of the total pore volume, for example greater than 60% of the total pore volume, for example greater than 70% of the total pore volume, for example greater than 80% of the total pore volume, for example greater than 90% of the total pore volume, for example greater than 95% of the total pore volume, for example greater than 98% of the total pore volume, for example greater than 99% of the total pore volume, for example greater than 99.5% of the total pore volume, for example greater than 99.9% of the total pore volume. 
     In certain embodiments, the pycnometry density of the porous carbon scaffold ranges from about 1 g/cc to about 3 g/cc, for example from about 1.5 g/cc to about 2.3 g/cc. In other embodiments, the skeletal density ranges from about 1.5 cc/g to about 1.6 cc/g, from about 1.6 cc/g to about 1.7 cc/g, from about 1.7 cc/g to about 1.8 cc/g, from about 1.8 cc/g to about 1.9 cc/g, from about 1.9 cc/g to about 2.0 cc/g, from about 2.0 cc/g to about 2.1 cc/g, from about 2.1 cc/g to about 2.2 cc/g or from about 2.2 cc/g to about 2.3 cc/g, from about 2.3 cc to about 2.4 cc/g, for example from about 2.4 cc/g to about 2.5 cc/g. 
     C. Silicon Production Via Chemical Vapor Infiltration (CVI) 
     Chemical vapor deposition (CVD) is a process wherein a substrate provides a solid surface comprising the first component of the composite, and the gas thermally decomposes on this solid surface to provide the second component of composite. Such a CVD approach can be employed, for instance, to create Si—C composite materials wherein the silicon is coating on the outside surface of silicon particles. Alternatively, chemical vapor infiltration (CVI) is a process wherein a substrate provides a porous scaffold comprising the first component of the composite, and the gas thermally decomposes on into the porosity (into the pores) of the porous scaffold material to provide the second component of composite. 
     In an embodiment, silicon is created within the pores of the porous carbon scaffold by subjecting the porous carbon particles to a silicon containing precursor gas at elevated temperature and the presence of a silicon-containing gas, preferably silane, in order to decompose said gas into silicon. The silicon containing precursor gas can be mixed with other inert gases, for example, nitrogen gas. The temperature and time of processing can be varied, for example the temperature can be between 200 and 900 C, for example between 200 and 250 C, for example between 250 and 300 C, for example between 300 and 350 C, for example between 300 and 400 C, for example between 350 and 450 C, for example between 350 and 400 C, for example between 400 and 500 C, for example between 500 and 600 C, for example between 600 and 700 C, for example between 700 and 800 C, for example between 800 and 900 C, for example between 600 and 1100 C. 
     The mixture of gas can comprise between 0.1 and 1% silane and remainder inert gas. Alternatively, the mixture of gas can comprise between 1% and 10% silane and remainder inert gas. Alternatively, the mixture of gas can comprise between 10% and 20% silane and remainder inert gas. Alternatively, the mixture of gas can comprise between 20% and 50% silane and remainder inert gas. Alternatively, the mixture of gas can comprise above 50% silane and remainder inert gas. Alternatively, the gas can essentially be 100% silane gas. Suitable inert gases include, but are not limited to, hydrogen, nitrogen, argon, and combinations thereof. 
     The pressure for the CVI process can be varied. In some embodiments, the pressure is atmospheric pressure. In some embodiments, the pressure is below atmospheric pressure. In some embodiments, the pressure is above atmospheric pressure. 
     D. Physico- and Electrochemical Properties of Silicon-Carbon Composite 
     While not wishing to be bound by theory, it is believed that the nano sized silicon achieved as a result of filling in certain, desired pore volume structure of the porous carbon scaffold (for instance, silicon filling pores in the range of 5 to 1000 nm, or other range as disclosed elsewhere herein), along with the advantageous properties of the other components of the composite, including low surface area, low pycnometry density, yield composite materials having different and advantageous properties, for instance electrochemical performance when the composite comprises an anode of a lithium ion energy storage device. 
     In certain embodiments, the embedded silicon particles embedded within the composite comprise nano-sized features. The nano-sized features can have a characteristic length scale of preferably less than 1 um, preferably less than 300 nm, preferably less than 150 nm, preferably less than 100 um, preferably less than 50 nm, preferably less than 30 nm, preferably less than 15 nm, preferably less than 10 nm, preferably less than 5 nm. 
     In certain embodiments, the silicon embedded within the composite is spherical in shape. In certain other embodiments, the porous silicon particles are non-spherical, for example rod-like, or fibrous in structure. In some embodiments, the silicon exists as a layer coating the inside of pores within the porous carbon scaffold. The depth of this silicon layer can vary, for example the depth can between 5 nm and 10 nm, for example between 5 nm and 20 nm, for example between 5 nm and 30 nm, for example between 5 nm and 33 nm, for example between 10 nm and 30 nm, for example between 10 nm and 50 nm, for example between 10 nm and 100 nm, for example between 10 and 150 nm, for example between 50 nm and 150 nm, for example between 100 and 300 nm, for example between 300 and 1000 nm. 
     In some embodiments, the silicon embedded within the composite is nano sized, and resides within pores of the porous carbon scaffold. For example, the embedded silicon can be impregnated, deposited by CVI, or other appropriate process into pores within the porous carbon particle comprising pore sizes between 5 and 1000 nm, for example between 10 and 500 nm, for example between 10 and 200 nm, for example between 10 and 100 nm, for example between 33 and 150 nm, for example between and 20 and 100 nm. Other ranges of carbon pores sizes with regards to fractional pore volume, whether micropores, mesopores, or macropores, are also envisioned. 
     In some embodiments, the carbon scaffold pore volume distribution can be described as the number or volume distribution of pores as determined as known in the art based on gas sorption analysis, for example nitrogen gas sorption analysis. In some embodiments the pore size distribution can be expressed in terms of the pore size at which a certain frction of the total pore volume resides at or below. For example, the pore size at which 10% of the pores reside at or below can be expressed at DPv10. 
     The DPv10 for the porous carbon scaffold can vary, for example DPv10 can be between 0.01 nm and 100 nm, for example between 0.1 nm and 100 nm, for example between 1 nm and 100 nm, for example between 1 nm and 50 nm, for example between 1 nm and 40 nm, for example between 1 nm and 30 nm, for example between 1 nm and 10 nm, for example between 1 nm and 5 nm. 
     The DPv50 for the porous carbon scaffold can vary, for example DPv50 can be between 0.01 nm and 100 nm, for example between 0.1 nm and 100 nm, for example between 1 nm and 100 nm, for example between 1 nm and 50 nm, for example between 1 nm and 40 nm, for example between 1 nm and 30 nm, for example between 1 nm and 10 nm, for example between 1 nm and 5 nm. In other embodiments, the DPv50 is between 2 and 100, for example between 2 and 50, for example between 2 and 30, for example between 2 and 20, for example between 2 and 15, for example between 2 and 10. 
     The DPv90 for the porous carbon scaffold can vary, for example DPv90 can be between 0.01 nm and 100 nm, for example between 0.1 nm and 100 nm, for example between 1 nm and 100 nm, for example between 1 nm and 50 nm, for example between 1 nm and 50 nm, for example between 1 nm and 40 nm, for example between 1 nm and 30 nm, for example between 1 nm and 10 nm, for example between 1 nm and 5 nm. In other embodiments, the DPv50 is between 2 nm and 100 nm, for example between 2 nm and 50 nm, for example between 2 nm and 30 nm, for example between 2 nm and 20 nm, for example between 2 nm and 15 nm, for example between 2 nm and 10 nm. 
     In some embodiments, the DPv90 is less than 100 nm, for example less than 50 nm, for example less than 40 nm, for example less than 30 nn, for example less than 20 nn, for example less than 15 nm, for example less than 10 nm. In some embodiments, the carbon scaffold comprises a pore volume with greater than 70% micropores (and DPv90 less than 100 nm, for example DPv90 less than 50 nm, for example DPv90 less than 40 nm, for example DPv90 less than 30 nm, for example DPv90 less than 20 nm, for example DPv90 less than 15 nm, for example DPv90 less than 10 nm, for example DPv90 less than 5 nm, for example DPv90 less than 4 nm, for example DPv90 less than 3 nm. In other embodiments, the carbon scaffold comprises a pore volume with greater than 80% micropores and DPv90 less than 100 nm, for example DPv90 less than 50 nm, for example DPv90 less than 40 nm, for example DPv90 less than 30 nm, for example DPv90 less than 20 nm, for example DPv90 less than 15 nm, for example DPv90 less than 10 nm, for example DPv90 less than 5 nm, for example DPv90 less than 4 nm, for example DPv90 less than 3 nm. 
     The DPv99 for the porous carbon scaffold can vary, for example DPv99 can be between 0.01 nm and 1000 nm, for example between 0.1 nm and 1000 nm, for example between 1 nm and 500 nm, for example between 1 nm and 200 nm, for example between 1 nm and 150 nm, for example between 1 nm and 100 nm, for example between 1 nm and 50 nm, for example between 1 nm and 20 nm. In other embodiments, the DPv99 is between 2 nm and 500 nm, for example between 2 nm and 200 nm, for example between 2 nm and 150 nm, for example between 2 nm and 100 nm, for example between 2 nm and 50 nm, for example between 2 nm and 20 nm, for example between 2 nm and 15 nm, for example between 2 nm and 10 nm. 
     Embodiments of the composite with extremely durable intercalation of lithium disclosed herein improves the properties of any number of electrical energy storage devices, for example lithium ion batteries. In some embodiments, the silicon-carbon composite disclosed herein exhibits a Z less than 10, for example a Z less than 5, for example a Z less than 4, for example a Z less than 3, for example a Z less than 2, for example a Z less than 1, for example a Z less than 0.1, for example a Z less than 0.01, for example a Z less than 0.001. In certain embodiments, the Z is zero. 
     In certain preferred embodiment, the silicon-carbon composite comprises desirably low Z in combination with another desired physicochemical and/or electrochemical property or in combination with more than one other desired physicochemical and/or electrochemical properties. Table 1 provides a description of certain embodiments for combination of properties for the silicon-carbon composite. Surface area can be determined as known in the art, for example, by nitrogen gas sorption analysis. Silicon content can be determined as known in the art, for example by TGA. The property Z can be determined from TGA according to the current disclosure. First cycle efficiency can be determined as known in the art, for example calculated based on first cycle charge and discharge capacity in a full cell or half cell. For example, first cycle efficiency can be determined in a half cell for the voltage window of 5 mV to 0.8 V, or alternatively, 5 mV to 1.5 V. Reversible capacity can be described as the maximum reversible capacity or maximum capacity, and can be determined as known in the art, for example in a half cell for the voltage window of 5 mV to 0.8 V, or alternatively, 5 mV to 1.5 V. 
     
       
         
           
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                 Embodiments for silicon-carbon composite 
               
               
                 with embodied properties. 
               
            
           
           
               
               
            
               
                   
                 In some embodiments the silicon-carbon 
               
               
                   
                 composite comprises. . . 
               
               
                   
               
               
                 Z 
                 &lt;10, &lt;5, &lt;4, &lt;3, &lt;2, &lt;1, &lt;0.1, &lt;0.01, &lt;0.01, 0 
               
               
                 Surface Area 
                 &lt;100 m2/g, &lt;50 m2/g, &lt;30 m2/g, &lt;20 m2/g, &lt;10 m2/g, 
               
               
                   
                 &lt;5 m2/g, &lt;4 m2/g, &lt;3 m2/g, &lt;2 m2/g, &lt;1 m2/g; 
               
               
                 First Cycle 
                 &gt;75%, &gt;80%, &gt;85%, &gt;90%, &gt;91%, &gt;92%, &gt;93%, &gt;94%, 
               
               
                 Efficiency 
                 &gt;95%, &gt;96%, &gt;97%, &gt;98%, &gt;99%; 
               
               
                 Reversible 
                 &gt;1300 mAh/g, &gt;1600 mAh/g, &gt;1700 mAh/g, &gt;1800 mAh/g, 
               
               
                 Capacity 
                 &gt;1900 mAh/g, &gt;2000 mAh/g, &gt;2100 mAh/g, &gt;2200 mAh/g, 
               
               
                   
                 &gt;2300 mAh/g, &gt;2400 mAh/g, &gt;2500 mAh/g, &gt;2600 mAh/g, 
               
               
                   
                 &gt;2700 mAh/g, &gt;2800 mAh/g, &gt;2900 mAh/g, &gt;3000 mAh/g; 
               
               
                   
                 and/or 
               
               
                 Silicon 
                 10%-90%, 15-85%, 20%-80%, 30%-70%, 40%-60%. 
               
               
                 Content 
                   
               
               
                 by weight 
               
               
                   
               
            
           
         
       
     
     According to Table 1, the silicon-carbon composite may comprise combinations of various properties. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 100 m2/g, a first cycle efficiency greater than 80%, and a reversible capacity of at least 1300 mAh/g. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 100 m2/g, a first cycle efficiency greater than 80%, and a reversible capacity of at least 1600 mAh/g. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 20 m2/g, a first cycle efficiency greater than 85%, and a reversible capacity of at least 1600 mAh/g. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 85%, and a reversible capacity of at least 1600 mAh/g. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 90%, and a reversible capacity of at least 1600 mAh/g. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 90%, and a reversible capacity of at least 1800 mAh/g. 
     The silicon-carbon composite can comprise a combination of the aforementioned properties, in addition to also comprising a carbon scaffold comprising properties also described within this proposal. Accordingly, Table 2 provides a description of certain embodiments for combination of properties for the silicon-carbon composite. 
     
       
         
           
               
             
               
                 TABLE 2 
               
             
            
               
                   
               
               
                 Embodiments for silicon-carbon composite 
               
               
                 with embodied properties. 
               
            
           
           
               
               
            
               
                   
                 In some embodiments the silicon-carbon 
               
               
                   
                 composite comprises. . . 
               
               
                   
               
               
                 Z 
                 &lt;10, &lt;5, &lt;4, &lt;3, &lt;2, &lt;1, &lt;0.1, &lt;0.01, &lt;0.01, 0 
               
               
                 Surface Area 
                 &lt;100 m2/g, &lt;50 m2/g, &lt;30 m2/g, &lt;20 m2/g, &lt;10 m2/g, 
               
               
                   
                 &lt;5 m2/g, &lt;4 m2/g, &lt;3 m2/g, &lt;2 m2/g, &lt;1 m2/g; 
               
               
                 First Cycle 
                 &gt;75%, &gt;80%, &gt;85%, &gt;90%, &gt;91%, &gt;92%, &gt;93%, &gt;94%, 
               
               
                 Efficiency 
                 &gt;95%, &gt;96%, &gt;97%, &gt;98%, &gt;99%; 
               
               
                 Reversible 
                 &gt;1300 mAh/g, &gt;1600 mAh/g, &gt;1700 mAh/g, &gt;1800 mAh/g, 
               
               
                 Capacity 
                 &gt;1900 mAh/g, &gt;2000 mAh/g, &gt;2100 mAh/g, &gt;2200 mAh/g, 
               
               
                   
                 &gt;2300 mAh/g, &gt;2400 mAh/g, &gt;2500 mAh/g, &gt;2600 mAh/g, 
               
               
                   
                 &gt;2700 mAh/g, &gt;2800 mAh/g, &gt;2900 mAh/g, &gt;3000 mAh/g; 
               
               
                 Average 
                 ≥0.9969, ≥0.9970, ≥0.9975, ≥0.9980, ≥0.9985, 
               
               
                 Coulombic 
                 ≥0.9990, ≥0.9995, ≥0.9999 
               
               
                 efficiency 
                   
               
               
                 Silicon 
                 10%-90%, 15-85%, 20%-80%, 30%-70%, 40%-60%, 
               
               
                 Content 
                 30%-60% 
               
               
                 by weight 
                   
               
               
                 Carbon 
                 0.1-1.5 cm3/g, 0.2-1.2 cm3/g, 0.3-1.1 cm3/g, 0.4-1.0 
               
               
                 Scaffold 
                 cm3/g, 0.4-1.0 cm3/g, 0.5-1.0 cm3/g, 0.6-1.0 cm3/g, 
               
               
                 pore 
                 0.5-0.9 cm3/g, 0.4-1.0 cm3/g, &gt;0.1 cm3/g, &gt;0.2 cm3/g, 
               
               
                 volume 
                 &gt;0.4 cm3/g, &gt;0.6 cm3/g, &gt;0.8 cm3/g; 
               
               
                 % silicon 
                 15%-25%, 25%-35%, 20%-40%, 25%-50%, 30%-70%, 
               
               
                 content 
                 30%-60%, 60%-80%, 80%-100%; 
               
               
                 Scaffold 
                 &lt;1 nm, 1-5 nm, 5-1000 nm, 10-500 nm, 10-200 nm, 
               
               
                 pore size 
                 10-100 nm, 33-150 nm, 20-100 nm 
               
               
                 range 
                   
               
               
                 Percentage 
                 &gt;20%/&gt;30%/&gt;30%, &lt;10/&gt;30/&gt;30, &lt;5/&gt;30/&gt;30, &lt;5/&gt;40/&gt;40, 
               
               
                 of micro- 
                 &lt;1/&gt;40/&gt;40, &lt;10/&gt;70/&gt;20, &lt;10/&gt;20/&gt;70, &gt;10/&gt;10/&gt;80, 
               
               
                 porosity/ 
                 &lt;10/&gt;80/&gt;10, &lt;5/&gt;70/&gt;20, &lt;5/&gt;20/&gt;70,&lt;5/&gt;5/&gt;80, 
               
               
                 meso- 
                 &lt;5/&gt;80/&gt;10, &gt;80%/&lt;20%/&lt;20%, &gt;70/&lt;30/&lt;10, 
               
               
                 porosity/ 
                 &gt;70/&lt;30/&lt;5, &gt;70/&lt;20/&lt;10, &gt;70/&lt;10/&lt;10, &gt;70/&lt;10/&lt;5, 
               
               
                 macro- 
                 &gt;70/&lt;5/&lt;5, &gt;80/&lt;20/&lt;10, &gt;80/&lt;20/&lt;5, &gt;80/&lt;20/&lt;1, 
               
               
                 porosity 
                 &gt;80/&lt;10/&lt;10, &gt;80/&lt;10/&lt;5, &gt;80/&lt;10/&lt;1, &gt;90/&lt; 10/&lt;10, 
               
               
                 expressed as 
                 &gt;90/&lt;10/&lt;5, &gt;90/&lt;10/&lt;1, &gt;90/&lt;5/&lt;1, &gt;95/&lt;5/&lt;5, &gt;90/&lt;5/&lt;1 
               
               
                 percentage 
                   
               
               
                 of total pore 
                   
               
               
                 volume 
               
               
                   
               
            
           
         
       
     
     As used in herein, the percentage “microporosity,” “mesoporosity” and “macroporosity” refers to the percent of micropores, mesopores and macropores, respectively, as a percent of total pore volume. For example, a carbon scaffold having 90% microporosity is a carbon scaffold where 90% of the total pore volume of the carbon scaffold is formed by micropores. 
     According to Table 2, the silicon-carbon composite may comprise combinations of various properties. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 100 m2/g, a first cycle efficiency greater than 80%, a reversible capacity of at least 1600 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of 0.2-1.2 cm3/g wherein the scaffold pore volume comprises &gt;80% micropores, &lt;20% mesopores, and &lt;10% macropores. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 20 m2/g, a first cycle efficiency greater than 85%, and a reversible capacity of at least 1600 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of 0.2-1.2 cm3/g wherein the scaffold pore volume comprises &gt;80% micropores, &lt;20% mesopores, and &lt;10% macropores. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 85%, and a reversible capacity of at least 1600 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of 0.2-1.2 cm3/g wherein the scaffold pore volume comprises &gt;80% micropores, &lt;20% mesopores, and &lt;10% macropores. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 90%, and a reversible capacity of at least 1600 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of 0.2-1.2 cm3/g wherein the scaffold pore volume comprises &gt;80% micropores, &lt;20% mesopores, and &lt;10% macropores. For example, the silicon-carbon composite may comprise a Z less than 10, surface area less than 10 m2/g, a first cycle efficiency greater than 90%, and a reversible capacity of at least 1800 mAh/g, a silicon content of 15%-85%, a carbon scaffold total pore volume of 0.2-1.2 cm3/g wherein the scaffold pore volume comprises &gt;80% micropores, &lt;20% mesopores, and &lt;10% macropores. 
     Also according to Table 2, the silicon-carbon composite may comprise a carbon scaffold with &gt;80% micropores, silicon content of 30-60%, average Coulombic efficiency of ≥0.9969, and Z&lt;10. For example, the silicon-carbon composite may comprise a carbon scaffold with &gt;80% micropores, silicon content of 30-60%, average Coulombic efficiency of ≥0.9970, and Z&lt;10. For example, the silicon-carbon composite may comprise a carbon scaffold with &gt;80% micropores, silicon content of 30-60%, average Coulombic efficiency of ≥0.9975, and Z&lt;10. For example, the silicon-carbon composite may comprise a carbon scaffold with &gt;80% micropores, silicon content of 30-60%, average Coulombic efficiency of ≥0.9980, and Z&lt;10. For example, the silicon-carbon composite may comprise a carbon scaffold with &gt;80% micropores, silicon content of 30-60%, average Coulombic efficiency of &gt;0.9985, and Z&lt;10. For example, the silicon-carbon composite may comprise a carbon scaffold with &gt;80% micropores, silicon content of 30-60%, average Coulombic efficiency of ≥0.9990, and Z&lt;10. For example, the silicon-carbon composite may comprise a carbon scaffold with &gt;80% micropores, silicon content of 30-60%, average Coulombic efficiency of ≥0.9995, and Z&lt;10. For example, the silicon-carbon composite may comprise a carbon scaffold with &gt;80% micropores, silicon content of 30-60%, average Coulombic efficiency of ≥0.9970, and Z&lt;10. For example, the silicon-carbon composite may comprise a carbon scaffold with &gt;80% micropores, silicon content of 30-60%, average Coulombic efficiency of ≥0.9999, and Z&lt;10. 
     Without being bound by theory, the filling of silicon within the pores of the porous carbon traps porosity within the porous carbon scaffold particle, resulting in inaccessible volume, for example volume that is inaccessible to nitrogen gas. Accordingly, the silicon-carbon composite material may exhibit a pycnometry density of less than 2.1 g/cm3, for example less than 2.0 g/cm3, for example less than 1.9 g/cm3, for example less than 1.8 g/cm3, for example less than 1.7 g/cm3, for example less than 1.6 g/cm3, for example less than 1.4 g/cm3, for example less than 1.2 g/cm3, for example less than 1.0 g/cm3. 
     In some embodiments, the silicon-carbon composite material may exhibit a pycnometry density between 1.7 g·cm3 and 2.1 g/cm3, for example between 1.7 g·cm3 and 1.8 g/cm3, between 1.8 g·cm3 and 1.9 g/cm3, for example between 1.9 g·cm3 and 2.0 g/cm3, for example between 2.0 g·cm3 and 2.1 g/cm3. In some embodiments, the silicon-carbon composite material may exhibit a pycnometry density between 1.8 g·cm3 and 2.1 g/cm3. In some embodiments, the silicon-carbon composite material may exhibit a pycnometry density between 1.8 g·cm3 and 2.0 g/cm3. In some embodiments, the silicon-carbon composite material may exhibit a pycnometry density between 1.9 g·cm3 and 2.1 g/cm3. 
     The pore volume of the composite material exhibiting extremely durable intercalation of lithium can range between 0.01 cm3/g and 0.2 cm3/g. In certain embodiments, the pore volume of the composite material can range between 0.01 cm3/g and 0.15 cm3/g, for example between 0.01 cm3/g and 0.1 cm3/g, for example between 0.01 cm3/g and 0.05 cm2/g. 
     The particle size distribution of the composite material exhibiting extremely durable intercalation of lithium is important to both determine power performance as well as volumetric capacity. As the packing improves, the volumetric capacity may increase. In one embodiment the distributions are either Gaussian with a single peak in shape, bimodal, or polymodal (&gt;2 distinct peaks, for example trimodal). The properties of particle size of the composite can be described by the DO (smallest particle in the distribution), Dv50 (average particle size) and Dv100 (maximum size of the largest particle). The optimal combined of particle packing and performance will be some combination of the size ranges below. The particle size reduction in the such embodiments can be carried out as known in the art, for example by jet milling in the presence of various gases including air, nitrogen, argon, helium, supercritical steam, and other gases known in the art. 
     In one embodiment the Dv0 of the composite material can range from 1 nm to 5 microns. In another embodiment the Dv0 of the composite ranges from 5 nm to 1 micron, for example 5-500 nm, for example 5-100 nm, for example 10-50 nm. In another embodiment the Dv0 of the composite ranges from 500 nm to 2 microns, or 750 nm to 1 um, or 1-2 um. microns to 2 microns. In other embodiments, the Dv0 of the composite ranges from 2-5 um, or &gt;5 um. 
     In some embodiments the Dv50 of the composite material ranges from 5 nm to 20 um. In other embodiments the Dv50 of the composite ranges from 5 nm to 1 um, for example 5-500 nm, for example 5-100 nm, for example 10-50 nm. In another embodiment the Dv50 of the composite ranges from 500 nm to 2 um, 750 nm to 1 um, 1-2 um. In still another embodiments, the Dv50 of the composite ranges from 1 to 1000 um, for example from 1-100 um, for example from 1-10 um, for example 2-20 um, for example 3-15 um, for example 4-8 um. Incertain embodiments, the Dv50 is &gt;20 um, for example &gt;50 um, for example &gt;100 um. 
     The span (Dv50)/(Dv90-Dv10), wherein Dv10, Dv50 and Dv90 represent the particle size at 10%, 50%, and 90% of the volume distribution, can be varied from example from 100 to 10, from 10 to 5, from 5 to 2, from 2 to 1; in some embodiments the span can be less than 1. In certain embodiments, the composite comprising carbon and porous silicon material particle size distribution can be multimodal, for example, bimodal, or trimodal. 
     The surface functionality of the presently disclosed the composite material exhibiting extremely durable intercalation of lithium may be altered to obtain the desired electrochemical properties. One property which can be predictive of surface functionality is the pH of the composite materials. The presently disclosed composite materials comprise pH values ranging from less than 1 to about 14, for example less than 5, from 5 to 8 or greater than 8. In some embodiments, the pH of the composite materials is less than 4, less than 3, less than 2 or even less than 1. In other embodiments, the pH of the composite materials is between about 5 and 6, between about 6 and 7, between about 7 and 8 or between 8 and 9 or between 9 and 10. In still other embodiments, the pH is high and the pH of the composite materials ranges is greater than 8, greater than 9, greater than 10, greater than 11, greater than 12, or even greater than 13. 
     The silicon-carbon composite material may comprise varying amounts of carbon, oxygen, hydrogen and nitrogen as measured by gas chromatography CHNO analysis. In one embodiment, the carbon content of the composite is greater than 98 wt. % or even greater than 99.9 wt % as measured by CHNO analysis. In another embodiment, the carbon content of the silicon-carbon composite ranges from about 10-90%, for example 20-80%, for example 30-70%, for example 40-60%. 
     In some embodiments, silicon-carbon composite material comprises a nitrogen content ranging from 0-90%, example 0.1-1%, for example 1-3%, for example 1-5%, for example 1-10%, for example 10-20%, for example 20-30%, for example 30-90%. 
     In some embodiments, the oxygen content ranges from 0-90%, example 0.1-1%, for example 1-3%, for example 1-5%, for example 1-10%, for example 10-20%, for example 20-30%, for example 30-90%. 
     The silicon-carbon composite material may also incorporate an electrochemical modifier selected to optimize the electrochemical performance of the non-modified composite. The electrochemical modifier may be incorporated within the pore structure and/or on the surface of the porous carbon scaffold, within the embedded silicon, or within the final layer of carbon, or conductive polymer, coating, or incorporated in any number of other ways. For example, in some embodiments, the composite materials comprise a coating of the electrochemical modifier (e.g., silicon or Al 2 O 3 ) on the surface of the carbon materials. In some embodiments, the composite materials comprise greater than about 100 ppm of an electrochemical modifier. In certain embodiments, the electrochemical modifier is selected from iron, tin, silicon, nickel, aluminum and manganese. 
     In certain embodiments the electrochemical modifier comprises an element with the ability to lithiate from 3 to 0 V versus lithium metal (e.g. silicon, tin, sulfur). In other embodiments, the electrochemical modifier comprises metal oxides with the ability to lithiate from 3 to 0 V versus lithium metal (e.g. iron oxide, molybdenum oxide, titanium oxide). In still other embodiments, the electrochemical modifier comprises elements which do not lithiate from 3 to 0 V versus lithium metal (e.g. aluminum, manganese, nickel, metal-phosphates). In yet other embodiments, the electrochemical modifier comprises a non-metal element (e.g. fluorine, nitrogen, hydrogen). In still other embodiments, the electrochemical modifier comprises any of the foregoing electrochemical modifiers or any combination thereof (e.g. tin-silicon, nickel-titanium oxide). 
     The electrochemical modifier may be provided in any number of forms. For example, in some embodiments the electrochemical modifier comprises a salt. In other embodiments, the electrochemical modifier comprises one or more elements in elemental form, for example elemental iron, tin, silicon, nickel or manganese. In other embodiments, the electrochemical modifier comprises one or more elements in oxidized form, for example iron oxides, tin oxides, silicon oxides, nickel oxides, aluminum oxides or manganese oxides. 
     The electrochemical properties of the composite material can be modified, at least in part, by the amount of the electrochemical modifier in the material, wherein the electrochemical modifier is an alloying material such as silicon, tin, indium, aluminum, germanium, gallium. Accordingly, in some embodiments, the composite material comprises at least 0.10%, at least 0.25%, at least 0.50%, at least 1.0%, at least 5.0%, at least 10%, at least 25%, at least 50%, at least 75%, at least 90%, at least 95%, at least 99% or at least 99.5% of the electrochemical modifier. 
     The particle size of the composite material may expand upon lithiation as compared to the non-lithiated state. For example, the expansion factor, defined as ratio of the average particle size of particles of composite material comprising a porous silicon material upon lithiation divided by the average particle size under non-lithiated conditions. As described in the art, this expansion factor can be relatively large for previously known, non-optimal silicon-containing materials, for example about 4× (corresponding to a 400% volume expansion upon lithiation). The current inventors have discovered composite materials comprising a porous silicon material that can exhibit a lower extent of expansion, for example, the expansion factor can vary from 3.5 to 4, from 3.0 to 3.5, from 2.5 to 3.0, from 2.0 to 2.5, from 1.5 to 2.0, from 1.0 to 1.5. 
     It is envisioned that composite materials in certain embodiments will comprise a fraction of trapped pore volume, namely, void volume non-accessible to nitrogen gas as probed by nitrogen gas sorption measurement. Without being bound by theory, this trapped pore volume is important in that it provides volume into which silicon can expand upon lithiation. 
     In certain embodiments, the ratio of trapped void volume to the silicon volume comprising the composite particle is between 0.1:1 and 10:1. For example, the ratio of trapped void volume to the silicon volume comprising the composite particle is between 1:1 and 5:1, or 5:1 to 10:1. In embodiments, the ratio of ratio trapped void volume to the silicon volume comprising the composite particle is between 2:1 and 5:1, or about 3:1, in order to efficiently accommodate the maximum extent of expansion of silicon upon lithiation. 
     In certain embodiments, the electrochemical performance of the composite disclosed herein is tested in a half-cell; alternatively the performance of the composite with extremely durable intercalation of lithium disclosed herein is tested in a full cell, for example a full cell coin cell, a full cell pouch cell, a prismatic cell, or other battery configurations known in the art. The anode composition comprising the composite with extremely durable intercalation of lithium disclosed herein can further comprise various species, as known in the art. Additional formulation components include, but are not limited to, conductive additives, such as conductive carbons such as Super C45, Super P, Ketjenblack carbons, and the like, conductive polymers and the like, binders such as styrene-butadiene rubber sodium carboxymethylcellulose (SBR-Na-CMC), polyvinylidene difluoride (PVDF), polyimide (PI), polyacrylic acid (PAA) and the like, and combinations thereof. In certain embodiments, the binder can comprise a lithium ion as counter ion. 
     Other species comprising the electrode are known in the art. The % of active material in the electrode by weight can vary, for example between 1 and 5%, for example between 5 and 15%, for example between 15 and 25%, for example between 25 and 35%, for example between 35 and 45%, for example between 45 and 55%, for example between 55 and 65%, for example between 65 and 75%, for example between 75 and 85%, for example between 85 and 95%. In some embodiments, the active material comprises between 80 and 95% of the electrode. In certain embodiment, the amount of conductive additive in the electrode can vary, for example between 1 and 5%, between 5 and 15%, for example between 15 and 25%, for example between 25 and 35%. In some embodiments, the amount of conductive additive in the electrode is between 5 and 25%. In certain embodiments, the amount of binder can vary, for example between 1 and 5%, between 5 and 15%, for example between 15 and 25%, for example between 25 and 35%. In certain embodiments, the amount of conductive additive in the electrode is between 5 and 25%. 
     The silicon-carbon composite material may be prelithiated, as known in the art. In certain embodiments, the prelithiation is achieved electrochemically, for example in a half cell, prior to assembling the lithiated anode comprising the porous silicon material into a full cell lithium ion battery. In certain embodiments, prelithiation is accomplished by doping the cathode with a lithium-containing compound, for example a lithium containing salt. Examples of suitable lithium salts in this context include, but are not limited to, dilithium tetrabromonickelate(II), dilithium tetrachlorocuprate(II), lithium azide, lithium benzoate, lithium bromide, lithium carbonate, lithium chloride, lithium cyclohexanebutyrate, lithium fluoride, lithium formate, lithium hexafluoroarsenate(V), lithium hexafluorophosphate, lithium hydroxide, lithium iodate, lithium iodide, lithium metaborate, lithium perchlorate, lithium phosphate, lithium sulfate, lithium tetraborate, lithium tetrachloroaluminate, lithium tetrafluoroborate, lithium thiocyanate, lithium trifluoromethanesulfonate, lithium trifluoromethanesulfonate, and combinations thereof. 
     The anode comprising the silicon-carbon composite material can be paired with various cathode materials to result in a full cell lithium ion battery. Examples of suitable cathode materials are known in the art. Examples of such cathode materials include, but are not limited to LiCoO 2  (LCO), LiNi 0.8 Co 0.15 Al 0.05 O 2  (NCA), LiNi 1/3 Co 1/3 Mn 1/3 O 2  (NMC), LiMn 2 O 4  and variants (LMO), and LiFePO 4  (LFP). 
     For the full cell lithium ion battery comprising an anode further comprising the silicon-carbon composite material, pairing of cathode to anode can be varied. For example, the ratio of cathode-to-anode capacity can vary from 0.7 to 1.3. In certain embodiments, the ratio of cathode-to-anode capacity can vary from 0.7 to 1.0, for example from 0.8 to 1.0, for example from 0.85 to 1.0, for example from 0.9 to 1.0, for example from 0.95 to 1.0. In other embodiments, the ratio of cathode-to-anode capacity can vary from 1.0 to 1.3, for example from 1.0 to 1.2, for example from 1.0 to 1.15, for example from 1.0 to 1.1, for example from 1.0 to 1.05. In yet other embodiments, the ratio of cathode-to-anode capacity can vary from 0.8 to 1.2, for example from 0.9 to 1.1, for example from 0.95 to 1.05. 
     For the full cell lithium ion battery comprising an anode further comprising the silicon-carbon composite material, the voltage window for charging and discharging can be varied. In this regard, the voltage window can be varied as known in the art, depending on various properties of the lithium ion battery. For instance, the choice of cathode plays a role in the voltage window chosen, as known in the art. Examples of voltage windows vary, for example, in terms of potential versus Li/Li+, from 2.0 V to 5.0 V, for example from 2.5 V to 4.5V, for example from 2.5V to 4.2V. 
     For the full cell lithium ion battery comprising an anode further comprising the silicon-carbon composite material, the strategy for conditioning the cell can be varied as known in the art. For example, the conditioning can be accomplished by one or more charge and discharge cycles at various rate(s), for example at rates slower than the desired cycling rate. As known in the art, the conditioning process may also include a step to unseal the lithium ion battery, evacuate any gases generated within during the conditioning process, followed by resealing the lithium ion battery. 
     For the full cell lithium ion battery comprising an anode further comprising the silicon-carbon composite material, the cycling rate can be varied as known in the art, for example, the rate can between C/20 and 20 C, for example between C10 to 10 C, for example between C/5 and 5 C. In certain embodiments, the cycling rate is C/10. In certain embodiments, the cycling rate is C/5. In certain embodiments, the cycling rate is C/2. In certain embodiments, the cycling rate is 1 C. In certain embodiments, the cycling rate is 1 C, with periodic reductions in the rate to a slower rate, for example cycling at 1 C with a C/10 rate employed every 20 th  cycle. In certain embodiments, the cycling rate is 2 C. In certain embodiments, the cycling rate is 4 C. In certain embodiments, the cycling rate is 5 C. In certain embodiments, the cycling rate is 10 C. In certain embodiments, the cycling rate is 20 C. 
     The first cycle efficiency of the composite with extremely durable intercalation of lithium disclosed herein be determined by comparing the lithium inserted into the anode during the first cycle to the lithium extracted from the anode on the first cycle, prior prelithiation modification. When the insertion and extraction are equal, the efficiency is 100%. As known in the art, the anode material can be tested in a half-cell, where the counter electrode is lithium metal, the electrolyte is a 1M LiPF 6  1:1 ethylene carbonate:diethylcarbonate (EC:DEC), using a commercial polypropylene separator. In certain embodiments, the electrolyte can comprise various additives known to provide improved performance, such as fluoroethylene carbonate (FEC) or other related fluorinated carbonate compounds, or ester co-solvents such as methyl butyrate, vinylene carbonate, and other electrolyte additives known to improve electrochemical performance of silicon-comprising anode materials. 
     Coulombic efficiency can be averaged, for example averaged over cycles 7 to cycle 25 when tested in a half cell. Coulombic efficiency can be averaged, for example averaged over cycles 7 to cycle 20 when tested in a half cell. In certain embodiments, the average efficiency of the composite with extremely durable intercalation of lithium is greater than 0.9, or 90%. In certain embodiments, the average efficiency is greater than 0.95, or 95%. In certain other embodiments, the average efficiency is 0.99 or greater, for example 0.991 or greater, for example 0.992 or greater, for example 0.993 or greater, for example 0.994 or greater, for example 0.995 or greater, for example 0.996 or greater, for example 0.997 or greater, for example 0.998 or greater, for example 0.999 or greater, for example 0.9991 or greater, for example 0.9992 or greater, for example 0.9993 or greater, for example 0.9994 or greater, for example 0.9995 or greater, for example 0.9996 or greater, for example 0.9997 or greater, for example 0.9998 or greater, for example 0.9999 or greater. 
     In still other embodiments the present disclosure provides a composite material exhibiting extremely durable intercalation of lithium, wherein when the composite material is incorporated into an electrode of a lithium-based energy storage device the composite material has a volumetric capacity at least 10% greater than when the lithium based energy storage device comprises a graphite electrode. In some embodiments, the lithium based energy storage device is a lithium ion battery. In other embodiments, the composite material has a volumetric capacity in a lithium-based energy storage device that is at least 5% greater, at least 10% greater, at least 15% greater than the volumetric capacity of the same electrical energy storage device having a graphite electrode. In still other embodiments, the composite material has a volumetric capacity in a lithium based energy storage device that is at least 20% greater, at least 30% greater, at least 40% greater, at least 50% greater, at least 200% greater, at least 100% greater, at least 150% greater, or at least 200% greater than the volumetric capacity of the same electrical energy storage device having a graphite electrode. 
     The composite material may be prelithiated, as known in the art. These lithium atoms may or may not be able to be separated from the carbon. The number of lithium atoms to 6 carbon atoms can be calculated by techniques known to those familiar with the art:
 
#Li= Q× 3.6× MM /( C %× F )
 
     wherein Q is the lithium extraction capacity measured in mAh/g between the voltages of 5 mV and 2.0V versus lithium metal, MM is 72 or the molecular mass of 6 carbons, F is Faraday&#39;s constant of 96500, C % is the mass percent carbon present in the structure as measured by CHNO or XPS. 
     The composite material can be characterized by the ratio of lithium atoms to carbon atoms (Li:C) which may vary between about 0:6 and 2:6. In some embodiments the Li:C ratio is between about 0.05:6 and about 1.9:6. In other embodiments the maximum Li:C ratio wherein the lithium is in ionic and not metallic form is 2.2:6. In certain other embodiments, the Li:C ratio ranges from about 1.2:6 to about 2:6, from about 1.3:6 to about 1.9:6, from about 1.4:6 to about 1.9:6, from about 1.6:6 to about 1.8:6 or from about 1.7:6 to about 1.8:6. In other embodiments, the Li:C ratio is greater than 1:6, greater than 1.2:6, greater than 1.4:6, greater than 1.6:6 or even greater than 1.8:6. In even other embodiments, the Li:C ratio is about 1.4:6, about 1.5:6, about 1.6:6, about 1.6:6, about 1.7:6, about 1.8:6 or about 2:6. In a specific embodiment the Li:C ratio is about 1.78:6. 
     In certain other embodiments, the composite material comprises an Li:C ratio ranging from about 1:6 to about 2.5:6, from about 1.4:6 to about 2.2:6 or from about 1.4:6 to about 2:6. In still other embodiments, the composite materials may not necessarily include lithium, but instead have a lithium uptake capacity (i.e., the capability to uptake a certain quantity of lithium, for example upon cycling the material between two voltage conditions (in the case of a lithium ion half cell, an exemplary voltage window lies between 0 and 3 V, for example between 0.005 and 2.7 V, for example between 0.005 and 1 V, for example between 0.005 and 0.8 V). While not wishing to be bound by theory, it is believed the lithium uptake capacity of the composite materials contributes to their superior performance in lithium based energy storage devices. The lithium uptake capacity is expressed as a ratio of the atoms of lithium taken up by the composite. In certain other embodiments, the composite material exhibiting extremely durable intercalation of lithium comprise a lithium uptake capacity ranging from about 1:6 to about 2.5:6, from about 1.4:6 to about 2.2:6 or from about 1.4:6 to about 2:6. 
     In certain other embodiments, the lithium uptake capacity ranges from about 1.2:6 to about 2:6, from about 1.3:6 to about 1.9:6, from about 1.4:6 to about 1.9:6, from about 1.6:6 to about 1.8:6 or from about 1.7:6 to about 1.8:6. In other embodiments, the lithium uptake capacity is greater than 1:6, greater than 1.2:6, greater than 1.4:6, greater than 1.6:6 or even greater than 1.8:6. In even other embodiments, the Li:C ratio is about 1.4:6, about 1.5:6, about 1.6:6, about 1.6:6, about 1.7:6, about 1.8:6 or about 2:6. In a specific embodiment the Li:C ratio is about 1.78:6. 
     EXAMPLES 
     Example 1. Production of Silicon-Carbon Composite Material by CVI 
     The properties of the carbon scaffold (Carbon Scaffold 1) employed for producing the silicon-carbon composite is presented in Table 3. Employing Carbon Scaffold 1, the silicon-carbon composite (Silicon-Carbon Composite 1) was produced by CVI as follows. A mass of 0.2 grams of amorphous porous carbon was placed into a 2 in.×2 in. ceramic crucible then positioned in the center of a horizontal tube furnace. The furnace was sealed and continuously purged with nitrogen gas at 500 cubic centimeters per minute (ccm). The furnace temperature was increased at 20° C./min to 450° C. peak temperature where it was allowed to equilibrate for 30 minutes. At this point, the nitrogen gas is shutoff and then silane and hydrogen gas are introduced at flow rates of 50 ccm and 450 ccm, respectively for a total dwell time of 30 minutes. After the dwell period, silane and hydrogen were shutoff and nitrogen was again introduced to the furnace to purge the internal atmosphere. Simultaneously the furnace heat is shutoff and allowed to cool to ambient temperature. The completed Si—C material is subsequently removed from the furnace. 
     
       
         
           
               
             
               
                 TABLE 3 
               
             
            
               
                   
               
               
                 Description of carbon scaffold employed for Example 1. 
               
            
           
           
               
               
               
               
               
               
            
               
                 Carbon 
                 Surface 
                 Pore 
                 % 
                 % 
                 % 
               
               
                 Scaffold 
                 Area 
                 Volume 
                 Micro- 
                 Meso- 
                 Macro- 
               
               
                 # 
                 (m2/g) 
                 (cm3/g) 
                 pores 
                 pores 
                 pores 
               
               
                   
               
               
                 1 
                 1710 
                 0.762 
                 93.1 
                 6.8 
                 0.1 
               
               
                   
               
            
           
         
       
     
     Example 2. Analysis of Various Silicon-Composite Materials 
     A variety of carbon scaffold materials were employed, and the carbon scaffold materials were characterized by nitrogen sorption gas analysis to determine specific surface area, total pore volume, and fraction of pore volume comprising micropores, mesopores, and macropores. The characterization data for the carbon scaffold materials is presented in Table 4, namely the data for carbon scaffold surface area, pore volume, and pore volume distribution (% micropores, % mesopores, and % macropores), all as determined by nitrogen sorption analysis. 
     
       
         
           
               
             
               
                 TABLE 4 
               
             
            
               
                   
               
               
                 Properites of various carbon scaffold materials. 
               
            
           
           
               
               
               
               
               
               
            
               
                 Carbon 
                 Surface 
                 Pore 
                 % 
                 % 
                 % 
               
               
                 Scaffold 
                 Area 
                 Volume 
                 Micro- 
                 Meso- 
                 Macro- 
               
               
                 # 
                 (m2/g) 
                 (cm3/g) 
                 pores 
                 pores 
                 pores 
               
               
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 1 
                 1710 
                 0.762 
                 93.1 
                 6.8 
                 0.1 
               
               
                 2 
                 1744 
                 0.72 
                 97.2 
                 2.7 
                 0.1 
               
               
                 3 
                 1581 
                 0.832 
                 69.1 
                 30.9 
                 0.1 
               
               
                 4 
                 1710 
                 0.817 
                 80.1 
                 19.9 
                 0 
               
               
                 5 
                 1835 
                 0.9 
                 82.2 
                 17.8 
                 0 
               
               
                 6 
                 1475 
                 1.06 
                 52.4 
                 47.6 
                 0 
               
               
                 7 
                 453 
                 0.5 
                 3.9 
                 91.1 
                 5.1 
               
               
                 8 
                 787 
                 2.284 
                 0 
                 59.1 
                 40.9 
               
               
                 9 
                 1713 
                 0.76 
                 91 
                 9 
                 0 
               
               
                   
               
            
           
         
       
     
     The carbons scaffold sample as described in Table 4 were employed to produce a variety of silicon-carbon composite materials employing the CVI methodology in a static bed configuration as generally described in Example 1. These silicon-carbon samples were produced employing a range of process conditions: silane concentration 1.25% to 100%, diluent gas nitrogen or hydrogen, carbon scaffold starting mass 0.2 g to 700 g. 
     The surface area for the silicon-carbon composites was determined. The silicon-carbon composites were also analyzed by TGA to determine silicon content and the Z. Silicon-carbon composite materials were also tested in half-cell coin cells. The anode for the half-cell coin cell can comprise 60-90% silicon-carbon composite, 5-20% Na-CMC (as binder) and 5-20% Super C45 (as conductivity enhancer), and the electrolyte can comprise 2:1 ethylene carbonate:diethylene carbonate, 1 M LiPF6 and 10% fluoroethylene carbonate. The half-cell coin cells can be cycled at 25° C. at a rate of C/5 for 5 cycles and then cycled thereafter at C/10 rate. The voltage can be cycled between 0 V and 0.8 V, alternatively, the voltage can be cycled between 0 V and 1.5 V. From the half-cell coin cell data, the maximum capacity can be measured, as well as the average Coulombic efficiency (CE) over the range of cycles from cycle 7 to cycle 20. Physicochemical and electrochemical properties for various silicon-carbon composite materials are presented in Table 5. 
                     TABLE 5                  Properites of various silicon-carbon materials.                                         Silicon-                               Carbon   Carbon   Surface   Si       Max   Average       Composite   Scaffold   Area   content       Capacity   CE       #   #   (m2/g)   (%)   Z   (mAh/g)   (7-20)                                                 1   1   7   45.0   0.2   1433   0.9981       2   1   7   45.4   0.6   1545   0.9980       3   1   6   45.8   0.6   1510   0.9975       4   2   3.06   50.1   1.0   1665   0.9969       5   2   1.96   51.3   2.0   1662   0.9974       6   3   140   43.1   3.2   832   0.9941       7   2   1.61   48.7   2.8   1574   0.9977       8   2   2   48.5   3.0   1543   0.9972       9   1   8   46.3   0.2   1373   0.9976       10   4   44   51.2   6.2   1614   0.9975       11   5   94   48.9   6.2   1455   0.9969       12   6   61   52.1   10.6   2011   0.9869       13   7   68.5   34.6   17.2   1006   0.9909       14   8   20   74   33.5   2463   0.9717       15   8   149   57.7   34.5   1892   0.9766       16   8   61.7   68.9   38.7   2213   0.9757       17   9   11   46.1   0.8   1675   0.9990       18   9   11   46.7   2.0   1739   0.9985       19   9   15.1   46.8   1.7   1503   0.9980       20   9   4.1   47.9   4.2   1790   0.9953       21   9   5   48.1   4.6   1861   0.9962                    
A plot of the average Coulombic efficiency as a function of the Z is presented in  FIG.  1   . As can seen there was dramatic increase in the average Coulombic efficiency for silicon-carbon samples with low Z. In particular, all silicon-carbon samples with Z below 10.0 exhibited average Coulombic efficiency ≥0.9941, and all silicon-carbon samples with Z above 10 (Silicon-Carbon Composite Sample 12 through Silicon-Carbon Composite Sample 16) were observed to have average Coulombic efficiency ≤0.9909. Without being bound by theory, higher Coulombic efficiency for the silicon-carbon samples with Z&lt;10 provides for superior cycling stability in full cell lithium ion batteries. Further inspection of Table reveals the surprising and unexpected finding that the combination of silicon-carbon composite samples with Z&lt;10 and also comprising carbon scaffold comprising ≥70 microporosity provides for average Coulombic efficiency ≥0.9950.
 
     Therefore, in a preferred embodiment, the silicon-carbon composite material comprises a Z less than 10, for example less Z less than 5, for example less Z less than 3, for example less Z less than 2, for example less Z less than 1, for example less Z less than 0.5, for example less Z less than 0.1, or Z of zero. 
     In certain preferred embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;70% microporosity, for example Z less than 10 and &gt;80% microporosity, for example Z less than 10 and &gt;90% microporosity, for example Z less than 10 and &gt;95% microporosity, for example Z less than 5 and &gt;70% microporosity, for example Z less than 5 and &gt;80% microporosity, for example Z less than 5 and &gt;90% microporosity, for example Z less than 5 and &gt;95% microporosity, for example Z less than 3 and &gt;70% microporosity, for example Z less than 3 and &gt;80% microporosity, for example Z less than 3 and &gt;90% microporosity, for example Z less than 3 and &gt;95% microporosity, for example Z less than 2 and &gt;70% microporosity, for example Z less than 2 and &gt;80% microporosity, for example Z less than 2 and &gt;90% microporosity, for example Z less than 2 and &gt;95% microporosity, for example Z less than 1 and &gt;70% microporosity, for example Z less than 1 and &gt;80% microporosity, for example Z less than 1 and &gt;90% microporosity, for example Z less than 1 and &gt;95% microporosity, for example Z less than 0.5 and &gt;70% microporosity, for example Z less than 0.5 and &gt;80% microporosity, for example Z less than 0.5 and &gt;90% microporosity, for example Z less than 0.5 and &gt;95% microporosity, for example Z less than 0.1 and &gt;70% microporosity, for example Z less than 0.1 and &gt;80% microporosity, for example Z less than 0.1 and &gt;90% microporosity, for example Z less than 0.1 and &gt;95% microporosity, for example Z of zero and &gt;70% microporosity, for example Z of zero and &gt;80% microporosity, for example Z of zero and &gt;90% microporosity, for example Z of zero and &gt;95% microporosity. 
     In certain preferred embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 100 m2/g, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 50 m2/g, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 30 m2/g, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 10 m2/g, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 5 m2/g, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 50 m2/g, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 30 m2/g, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 10 m2/g, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 5 m2/g, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 50 m2/g, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 30 m2/g, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 10 m2/g, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 5 m2/g, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 50 m2/g, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 30 m2/g, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 10 m2/g, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 15%-85% silicon, and surface area less than 5 m2/g. 
     In certain preferred embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g. 
     In certain preferred embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, surface area less than 30 m2/g, and average Coulombic efficiency ≥0.9969. For example, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, surface area less than 30 m2/g, and average Coulombic efficiency ≥0.9970. For example, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, surface area less than 30 m2/g, and average Coulombic efficiency ≥0.9975. For example, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, surface area less than 30 m2/g, and average Coulombic efficiency ≥0.9980. For example, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, surface area less than 30 m2/g, and average Coulombic efficiency ≥0.9985. For example, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, surface area less than 30 m2/g, and average Coulombic efficiency ≥0.9990. For example, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, surface area less than 30 m2/g, and average Coulombic efficiency ≥0.9995. For example, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, surface area less than 30 m2/g, and average Coulombic efficiency ≥0.9999. 
     Example 3. dV/dQ for Various Silicon-Composite Materials 
     Differential capacity curve (dQ/dV vs Voltage) is often used as a non-destructive tool to understand the phase transition as a function of voltage in lithium battery electrodes (M. N. Obrovac et al. Structural Changes in Silicon Anodes during Lithium Insertion/Extraction, Electrochemical and Solid-State Letters, 7 (5) A93-A96 (2004); Ogata, K. et al. Revealing lithium-silicide phase transformations in nano-structured silicon-based lithium ion batteries via in situ NMR spectroscopy. Nat. Commun. 5:3217). Differential capacity plots presented here is calculated from the data obtained using galvanostatic cycling at 0.1 C rate between 5 mV to 0.8V in a half-cell coin cell at 25° C. Typical differential capacity curve for a silicon-based material in a half-cell vs lithium can be found in many literature references (Loveridge, M. J. et al. Towards High Capacity Li-Ion Batteries Based on Silicon-Graphene Composite Anodes and Sub-micron V-doped LiFePO4 Cathodes. Sci. Rep. 6, 37787; doi: 10.1038/srep37787 (2016); M. N. Obrovac et al. Li15Si4Formation in Silicon Thin Film Negative Electrodes, Journal of The Electrochemical Society, 163 (2) A255-A261 (2016); Q. Pan et al. Improved electrochemical performance of micro-sized SiO-based composite anode by prelithiation of stabilized lithium metal powder, Journal of Power Sources 347 (2017) 170-177). First cycle lithiation behavior is dependent on the crystallinity of the silicon and oxygen content among other factors. 
     After first cycle, previous amorphous silicon materials in the art exhibit two specific phase transition peaks in the dQ/dV vs V plot for lithiation, and correspondingly two specific phase transition peaks in the dQ/dV vs V plot for delithiation. For lithiation, one peak corresponding to lithium-poor Li—Si alloy phase occurs between 0.2-0.4 V and another peak corresponding to a lithium-rich Li—Si alloy phase occurs below 0.15 V. For delithiation, one delithiation peak corresponding to the extraction of lithium occurs below 0.4 V and another peak occurs between 0.4 V and 0.55 V. If the Li15Si4 phase is formed during lithiation, it is delithiated at −0.45V and appears as a very narrow sharp peak. 
       FIG.  2    depicts the dQ/dV vs Voltage curve for cycle 2 for the silicon-carbon composite material corresponding to Silicon-Carbon Composite 3 from Example 1. Silicon-Carbon Composite 3 comprises a Z of 0.6. For ease of identification, the plot is divided into regimes I, II, II, IV, V, and VI. Regimes I (0.8 V to 0.4 V), II (0.4 V to 0.15 V), III (0.15 V to 0 V) comprise the lithiation potentials and Regimes IV (0 V to 0.4 V), V (0.4 V to 0.55 V), VI (0.55 V to 0.8 V) comprise the delithiation potential. As described above, previous amorphous silicon-based materials in the art exhibit phase-transition peaks for two regimes (Regime II and Regime III) in the lithiation potential and two regimes (Regime IV and Regime V) in the dethiation potentials. 
     As can be seen in  FIG.  2   , the dQ/dV vs Voltage curve reveals surprising and unexpected result that Silicon-Carbon Composite 3, which comprises a Z of 0.6, comprises two additional peaks in the dQ/dV vs Voltage curve, namely Regime I in the lithiation potential and Regime VI in the delithiation potential. All 6 peaks are are reversible and observed in the subsequent cycles as well, as shown in  FIG.  3   . 
     Without being bound by theory, such trimodal behavior for the dQ/dV vs V curve is novel, and likewise reflects a novel form of silicon. 
     Notably, the novel peaks observed in Regime I and Regime VI are more pronounced in certain scaffold matrixes and completely absent in others samples illustrating the prior art (silicon-carbon composite samples with Z&gt;10, see explanation and table below). 
       FIG.  4    presents the dQ/dV vs V curve for Silicon-Carbon Composite 3, wherein the novel peaks in Regime I and Regime VI are evident, in comparison to Silicon-Carbon Composite 15, Silicon-Carbon Composite 16, and Silicon-Carbon Composite 14, all three of which comprise Z&gt;10 and whose dQ/dV vs V curves are devoid of the any peaks in Regime I and Regime VI. 
     Without being bound by theory, these novel peaks observed in Regime I and Regime VI relate to the properties of the silicon impregnated into the porous carbon scaffold, i.e., related to the interactions between and among the properties of the porous carbon scaffold, the silicon impregnated into the porous carbon scaffold via CVI, and lithium. In order to provide a quantitative analysis, we herein define the parameter φ, which is calculated as the normalized peak I with respect to peak III as:
 
φ=(Max peak height  dQ/dV  in Regime  I )/(Max peak height  dQ/dV  in Regime  III )
 
where dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V; the half-cell coin cell is produced as known in the art. If the Si—C sample shows peaks associated with graphite in regime III of the differential curve, it is omitted in favor of Li—Si related phase transition peaks for the calculation of D factor. For this example, the half-cell coin cell comprises an anode comprising 60-90% silicon-carbon composite, 5-20% SBR—Na-CMC, and 5-20% Super C45. An example for φ calculation is shown in  FIG.  5    for Silicon-Carbon Composite 3. In this instance, the maximum peak height in the regime I is −2.39 and is found at voltage 0.53V. Similarly, maximum peak height in regime III is −9.71 at 0.04V. In this instance, φ can be calculated using the above formula, yielding φ=−2.39/−9.71=0.25. The value of φ was determined from the half-cell coin cell data for the various silicon-carbon composites presented in Example 2. These data are summarized in Table 6. Table 6 also includes data for the first cycle efficiency, as measured in half cell coin cells cycled from 5 mV to 0.8 V.
 
     
       
         
           
               
             
               
                 TABLE 6 
               
             
            
               
                   
               
               
                 Properites of various silicon-carbon carbon scaffold materials. 
               
            
           
           
               
               
               
               
               
               
               
            
               
                 Silicon- 
                   
                   
                   
                   
                   
                 First 
               
               
                 Carbon 
                 Surface 
                 Si 
                   
                 Average 
                   
                 Cycle 
               
               
                 Composite 
                 Area 
                 content 
                   
                 CE 
                   
                 Effi- 
               
               
                 # 
                 (m2/g) 
                 (%) 
                 Z 
                 (7-20) 
                 φ 
                 ciency 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 1 
                 7 
                 45.0 
                 0.2 
                 0.9981 
                 0.24 
                 76.3 
               
               
                 2 
                 7 
                 45.4 
                 0.6 
                 0.9980 
                 0.24 
                 76.8 
               
               
                 3 
                 6 
                 45.8 
                 0.6 
                 0.9975 
                 0.25 
                 75.5 
               
               
                 4 
                 3.06 
                 50.1 
                 1.0 
                 0.9969 
                 0.18 
                 80.9 
               
               
                 5 
                 1.96 
                 51.3 
                 2.0 
                 0.9974 
                 0.18 
                 80.3 
               
               
                 6 
                 140 
                 43.1 
                 3.2 
                 0.9941 
                 0.13 
                 52.3 
               
               
                 7 
                 1.61 
                 48.7 
                 2.8 
                 0.9977 
                 0.19 
                 79.2 
               
               
                 8 
                 2 
                 48.5 
                 3.0 
                 0.9972 
                 0.19 
                 78.3 
               
               
                 9 
                 8 
                 46.3 
                 0.2 
                 0.9976 
                 0.20 
                 73.3 
               
               
                 10 
                 44 
                 51.2 
                 6.2 
                 0.9975 
                 0.13 
                 78.1 
               
               
                 11 
                 94 
                 48.9 
                 6.2 
                 0.9969 
                 0.15 
                 72.7 
               
               
                 12 
                 61 
                 52.1 
                 10.6 
                 0.9869 
                 0 
                 80.2 
               
               
                 13 
                 68.5 
                 34.6 
                 17.2 
                 0.9909 
                 0 
                 64 
               
               
                 14 
                 20 
                 74 
                 33.5 
                 0.9717 
                 0 
                 85 
               
               
                 15 
                 149 
                 57.7 
                 34.5 
                 0.9766 
                 0 
                 69 
               
               
                 16 
                 61.7 
                 68.9 
                 38.7 
                 0.9757 
                 0 
                 79.3 
               
               
                 17 
                 11 
                 46.1 
                 0.8 
                 0.9990 
                 0.35 
                 82.2 
               
               
                 18 
                 11 
                 46.7 
                 2.0 
                 0.9985 
                 0.34 
                 82.5 
               
               
                   
                   
                   
                   
                   
                   
                 (92.1*) 
               
               
                 19 
                 15.1 
                 46.8 
                 1.7 
                 0.9980 
                 0.34 
                 79.9 
               
               
                   
                   
                   
                   
                   
                   
                 (90.3*) 
               
               
                 20 
                 4.1 
                 47.9 
                 4.2 
                 0.9953 
                 0.33 
                 83.3 
               
               
                   
                   
                   
                   
                   
                   
                 (92.6*) 
               
               
                 21 
                 5 
                 48.1 
                 4.6 
                 0.9962 
                 0.30 
                 82.9 
               
               
                   
                   
                   
                   
                   
                   
                 (92.2*) 
               
               
                   
               
               
                 These data for first cycle effiency in parenthesis were measured for voltage window of 5 mV to 1.5 V. 
               
            
           
         
       
     
     The data in Table 6 reveal an unexpected relationship between decreasing Z and increasing φ. All silicon-carbon composites with Z&lt;10 had φ≥0.13, and all silicon-carbon composites with Z&gt;10 had φ&lt;0.13, indeed, all silicon-carbon composites with where Z&gt;10 had φ=0. This relationship is also evidenced in  FIG.  6   . Without being bound by theory, silicon materials comprising φ≥0.10, for example φ≥0.13, for example φ≥0.15, for example φ≥0.20, for example φ≥0.25, for example φ≥0.30, correspond to a novel form of silicon. Alternatively, silicon materials comprising φ&gt;0 correspond to a novel form of silicon. The silicon-carbon composite material comprising silicon comprising φ≥0.10, for example φ≥0.13, for example φ≥0.15, for example φ≥0.20, for example φ≥0.25, for example φ≥0.30, correspond to a novel silicon-carbon composite material. Alternatively, silicon-carbon composite materials comprising φ&gt;0 corresponds to a novel silicon-carbon composite material. 
     In certain embodiments, the silicon-carbon composite comprises a φ≥0.1, φ≥0.11, φ≥0.12, φ≥0.13, φ≥0.14, φ≥0.15, φ≥0.16, φ≥0.17, φ≥0.18, φ≥0.19, φ≥0.20, φ≥0.24, φ≥0.24, φ≥0.25, φ≥0.30 or φ≥0.35. Im come embodiment, φ&gt;0. In some embodiments, φ≥0.001, φ≥0.01, φ≥0.02, φ≥0.05, φ≥0.1, φ≥0.11, or φ≥0.12. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, and φ≥0.1, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 50 m2/g, and φ≥0.1, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ&gt;0.1, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ&gt;0, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, and φ&gt;0, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ&gt;0, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ&gt;0, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ&gt;0. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ&gt;0, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 50 m2/g, and φ&gt;0, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ&gt;0, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ&gt;0, for example Z less than 10 and &gt;70% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ&gt;0. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, and φ≥0.1, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 50 m2/g, and φ≥0.1, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ&gt;0, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, and φ&gt;0, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ&gt;0, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ&gt;0, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ&gt;0. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ&gt;0, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 50 m2/g, and φ&gt;0, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ&gt;0, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ&gt;0, for example Z less than 10 and &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ&gt;0. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, and φ≥0.1, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 50 m2/g, and φ≥0.1, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ&gt;0, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, and φ&gt;0, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ&gt;0, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ&gt;0, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ&gt;0. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ&gt;0, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 50 m2/g, and φ&gt;0, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ&gt;0, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ&gt;0, for example Z less than 10 and &gt;90% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ&gt;0. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, and φ≥0.1, for example Z less than 5 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 50 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 100 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 50 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 10 m2/g, and φ≥0.1, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 5 m2/g, and φ≥0.1. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 100 m2/g, and φ&gt;0, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 50 m2/g, and φ&gt;0, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 30 m2/g, and φ&gt;0, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 10 m2/g, and φ&gt;0, for example Z less than 10 and &gt;95% microporosity, and wherein the silicon-carbon composite also comprises 40%-60% silicon, and surface area less than 5 m2/g, and φ&gt;0. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.15, and an average Coulombic efficiency ≥0.9969, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g,  ≥0.15, and an average Coulombic efficiency ≥0.9970, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.15, and an average Coulombic efficiency ≥0.9975, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.15, and an average Coulombic efficiency ≥0.9980, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.15, and an average Coulombic efficiency ≥0.9985, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.15, and an average Coulombic efficiency ≥0.9990, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.15, and an average Coulombic efficiency ≥0.9995, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.15, and an average Coulombic efficiency ≥0.9999. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.20, and an average Coulombic efficiency ≥0.9969, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.20, and an average Coulombic efficiency ≥0.9970, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.20, and an average Coulombic efficiency ≥0.9975, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.20, and an average Coulombic efficiency ≥0.9980, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.20, and an average Coulombic efficiency ≥0.9985, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.20, and an average Coulombic efficiency ≥0.9990, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.20, and an average Coulombic efficiency ≥0.9995, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.20, and an average Coulombic efficiency ≥0.9999. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.25, and an average Coulombic efficiency ≥0.9969, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.25, and an average Coulombic efficiency ≥0.9970, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.25, and an average Coulombic efficiency ≥0.9975, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.25, and an average Coulombic efficiency ≥0.9980, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.25, and an average Coulombic efficiency ≥0.9985, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.25, and an average Coulombic efficiency ≥0.9990, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.25, and an average Coulombic efficiency ≥0.9995, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.25, and an average Coulombic efficiency ≥0.9999. 
     In certain embodiments, the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.3, and an average Coulombic efficiency ≥0.9969, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.3, and an average Coulombic efficiency ≥0.9970, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.3, and an average Coulombic efficiency ≥0.9975, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.3, and an average Coulombic efficiency ≥0.9980, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.3, and an average Coulombic efficiency ≥0.9985, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.3, and an average Coulombic efficiency ≥0.9990, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.3, and an average Coulombic efficiency ≥0.9995, for example the silicon-carbon composite material comprises a Z less than 10 and a carbon scaffold with &gt;80% microporosity, and wherein the silicon-carbon composite also comprises 30%-60% silicon, and surface area less than 30 m2/g, φ≥0.3, and an average Coulombic efficiency ≥0.9999. 
     Example 4. Particle Size Distribution for Various Carbon Scaffold Materials 
     The particle size distribution for the various carbon scaffold materials was determined by using a laser diffraction particle size analyzer as known in the art. Table 7 presented the data, specifically the Dv,1, Dv10, Dv50, and Dv,90, and Dv,100. 
     
       
         
           
               
             
               
                 TABLE 4 
               
             
            
               
                   
               
               
                 Properites of various carbon scaffold materials. 
               
            
           
           
               
               
            
               
                 Carbon Scaffold 
                   
               
               
                 # 
                 Particle Size Characteristics 
               
               
                   
               
               
                 1 
                 Dv, 1 = 1.2 um, Dv, 10 = 2.5 um, Dv, 50 = 6.9 um, 
               
               
                   
                 Dv90 = 11.5 um, Dv100 = 20.1 um 
               
               
                 2 
                 Dv, 1 = 1.09, Dv10 = 3.4 um, Dv50 = 7.67 um, 
               
               
                   
                 Dv, 90 = 13.3 um, Dv100 = 17.8 
               
               
                 4 
                 Dv, 1 = 0.81, Dv10 = 1.9 um, Dv50 = 6.4 um, 
               
               
                   
                 Dv, 90 = 16.6 um, Dv100 = 26.5 
               
               
                 5 
                 Dv, 1 = 0.62, Dv10 = 1.1 um, Dv50 = 4.2 um, 
               
               
                   
                 Dv, 90 = 15.8 um, Dv100 = 29.8 
               
               
                 8 
                 Dv, 1 = 1.3, Dv10 = 3.7 um, Dv50 = 16 um, 
               
               
                   
                 Dv, 90 = 35.2 um, Dv100 = 50.7 
               
               
                 9 
                 Dv, 1 = 1.2 um, Dv, 10 = 2.7 um, Dv, 50 = 7.6 um, 
               
               
                   
                 Dv, 90 = 12.3 um, Dv100 = 20.7 um 
               
               
                   
               
            
           
         
       
     
     Example 5. Lithium-Silicon Batteries Comprising Anode Comprising a Composite Comprising Group14 Elements Silicon and Carbon 
     The novel composite comprising Group14 elements silicon and carbon has utility for dramatically improving the performance of lithium silicon batteries. As known in the art, the lithium silicon battery comprises various other attributes as described in this example. 
     The lithium silicon battery comprises an anode comprising a composite comprising Group14 elements silicon and carbon. The concentration of composite comprising Group14 elements silicon and carbon by dry weight in the anode can vary, for example from 1% to 90%, for example 5% to 95%, for example 10% to 70%. In certain embodiments, the concentration of composite comprising Group14 elements silicon and carbon by dry weight in the anode is 5% to 25% or 25% to 35%, or 35% to 50%, or 50% to 70%, or greater than 70%. 
     The anode may further comprise other components. These other components include graphite, conductive carbon additive, and binder, and combinations thereof. 
     In some embodiments, the lithium-silicon battery comprises an anode that comprises graphite, or combinations thereof. Exemplary graphites in this regard include, but are not limited to, natural graphite, synthetic graphite, nano-graphite, or combinations thereof. The concentration by dry weight of graphite in the anode may vary, example 5% to 95%, for example 10% to 70%, for example 20% to 60%, for example 30% to 50%. In certain embodiments, the lithium-silicon battery comprises an anode that is devoid of graphite. 
     In preferred embodiments, the lithium-silicon battery comprises an anode that comprises conductive carbon additive, or combinations thereof. Exemplary conductive carbon additives include, but are not limited to, carbon black, conductive carbon black, superconductive carbon black, extraconductive carbon black, ultraconductive carbon black, Super C, Super P, Super [C45 or C65], Ketjenblack carbon, acetylene black, fullerine, graphene, carbon fibers, carbon nanofibers, carbon nanotubes, or combinations thereof. The concentration by dry weight of conductive carbon additive in the anode may vary, for example from 0.1% to 20%, for example 1% to 10%, for example 2% to 8%, for example 3% to 6%. In certain embodiments, for example wherein the anode is devoid of graphite, the concentration by dry weight of conductive carbon additive may range from 5% to 20%, for example 10% to 20%, for example 14% to 16%. 
     In preferred embodiments, the lithium-silicon battery comprises an anode that comprises a binder, or combinations thereof. Exemplary binders included, but are not limited to, polyvinylidene difluoride (PVDF), styrene butadiene rubber (SBR), sodium carboxymethyl cellulose (Na-CMC), polyacrylonitrile (PAN), polyacrylic latex, polyacrylic acid (PAA), polyvinyl alcohol (PVA), polyethylene glycol (PEG), polyamide imide (PAI), polyimide (PI), and combinations thereof. In certain embodiments, the binder can comprise a lithium ion as counter ion. The concentration by dry weight of binder in the anode may vary, for example from 0.1% to 20%, for example 1% to 10%, for example 2% to 8%, for example 3% to 6%. In certain embodiments, for example wherein the anode is devoid of graphite, the concentration by dry weight of binder may range from 5% to 20%, for example 10% to 20%, for example 14 to 16%. 
     The anode of the lithium-silicon battery comprises a composite comprising Group14 elements silicon and carbon, wherein said anode also comprises a porosity in the dry state. The porosity of the dry anode may vary, for example between 10% and 90%, for example 20% to 80%, for example 30% to 70%, for example 40% to 60%. In certain preferred embodiments, the porosity of the dry anode is 30% to 50%. In certain preferred embodiments, the porosity of the dry anode is 10% to 50%. 
     The lithium-silicon battery comprises a anode comprising a composite comprising Group14 elements silicon and carbon, wherein said lithium silicon battery also comprises a cathode. Exemplary cathodes include, but are not limited to, lithium cobalt oxide (LiCoO 2 ) (LCO), lithium manganese oxide (LiMn 2 O 4 ) (LMO), lithium iron phosphate (LiFePO 4 ) (LFP), lithium nickel cobalt aluminum oxide (LiNiCoAlO 2 ) (NCA), lithium titanate (Li 2 TiO 3 ) (LTO), lithium nickel manganese cobalt oxide (LiNi x Mn y Co z O 2 ) (NMC, with x+y+z=1, x:y:z=3:3:3 (NMC333), 4:3:3 (NMC433), 5:3:2 (NMC532), 6:1:1 (NMC611), 6:2:2 (NMC622), 8:1:1 (NMC811)). In certain preferred embodiments, the cathode is NMC811. 
     The lithium-silicon battery comprises a ratio known as the N/P ratio that describes the capacity ratio between the anode and cathode electrodes in the battery cell). The N/P is important for determining the energy density of the lithium-silicon battery. Without being bound by theory, a lower N/P ratio provides for less excess anode hence higher energy density of the lithium-silicon battery. The average discharge potential for silicon-carbon anodes is higher than graphite anodes. Without being bound by theory, presence of φ in the anode enables one to reduce the excess anode needed in the cell to avoid plating. Accordingly, and without being bound by theory, the novel anode material described herein comprising φ&gt;0, for example φ≥0.15, for example φ≥0.2, for example φ≥0.25, for example φ≥0.3, allows for lower N/P ratio and hence higher energy density of the lithium-silicon battery. In certain embodiments, the N/P ratio &gt;1.1, for example N/P ratio &gt;1.2, for example N/P ratio &gt;1.3, for example N/P ratio &gt;1.4, for example N/P ratio &gt;1.5, for example N/P ratio &gt;2.0. In certain preferred embodiments, the N/P ratio ≤2.0, for example N/P ratio ≤1.5, for example N/P ratio ≤1.4, for example N/P ratio ≤1.3, for example N/P ratio ≤1.2, for example N/P ratio ≤1.1, for example N/P ratio ≤1.0, for example N/P ratio ≤0.9, for example N/P ratio ≤0.8. 
     The lithium-silicon battery comprises an electrolyte, wherein the electrolyte comprises various components including solvent, solvent additives, and electrolyte ions. Exemplary electrolyte components include, but are not limited to, ethylene carbonate (EC), diethylcarbonate (DEC), propylene carbonate (PC), dimethyl carbonate (DMC), ethyl methyl carbonate (EMC), ethyl propyl ether (EPE), fluorinated cyclic carbonate (F-AEC), fluorinated linear carbonate (F-EMC), Dimethylacrylamide (DMAA), Succinic anhydride (SA), tris(trimethylsilyl) borate (TTMB), tris(trimethylsilyl) phosphate (TTSP), 1,3-propane sultone (PS), fluorinated ether (F-EPE), fluoroethylene carbonate (FEC), performance enhancing organosilicon electrolyte materials sch as OS3, vinylene carbonate (VC), LiPF6, LiBF4, LiBOB, LiTFSI, LiFSI, LiClO4 and combinations thereof. In certain embodiments, the electrolyte salts concentration &gt;1.0 M, for example salt concentration &gt;1.2, for example salt concentration &gt;1.3, for example salt concentration &gt;1.4, for example salt concentration &gt;1.5, for example salt concentration &gt;2.0. In certain preferred embodiments, the electrolyte salt concentration &lt;2.0, for example electrolyte salt concentration &lt;1.5, for example electrolyte salt concentration &lt;1.4, for example electrolyte salt concentration &lt;1.3, for example electrolyte salt concentration &lt;1.2, for example electrolyte salt concentration &lt;1.1, for example electrolyte salt concentration &lt;1.0, for example electrolyte salt concentration &lt;0.9. 
     The lithium-silicon battery comprising a composite comprising Group14 elements silicon and carbon also comprises a separator that maintains the separation of anode and cathode. Separator can be made of one layer or multiple layers of polymer material, or coated with aramid, ceramic or fluoride materials. Examplary separator materials include, but are not limited to, nonwoven fibers (cotton, nylon, polyesters, glass), polymer films (polyethylene, polypropylene, poly (tetrafluoroethylene), polyvinyl chloride), ceramic, and naturally occurring substances (rubber, asbestos, wood). In certain preferred embodiments, the separator comprises a polymer, wherein exemplary polymers include, but are not limited to, polyolefin based materials with semi-crystalline structure, polyethylene, polypropylene, graft polymers including micro-porous poly(methyl methacrylate)-grafted and siloxane grafted polyethylene, polyvinylidene fluoride (PVDF) nanofiber webs, and polytriphenylamine (PTPA). 
     The lithium-silicon battery comprising a composite comprising Group14 elements silicon and carbon is cycled during battery use between the lower and upper bounds of the lithium-silicon battery operating voltage window. Without being bound by theory, decreasing the lower bound of the operating voltage window provides for higher energy density of the lithium-silicon battery. Accordingly, and without being bound by theory, the novel anode material described herein comprising φ&gt;0, for example φ≥0.15, for example φ≥0.2, for example φ≥0.25, for example φ≥0.3, allows for decreasing the lower bound voltage window and hence higher energy density of the lithium-silicon battery. In certain embodiments, the lower bound of the voltage window is ≤3.0 V, for example ≤2.9V, for example ≤2.8V, for example ≤2.7V, for example ≤2.6V, for example ≤2.5V, for example ≤2.4V, for example ≤2.3V. The upper bound of the voltage window for cycling the lithium-silicon battery can be varied. For example, the upper bound of the voltage window can vary, for example ≥4.0 V, for example 4.0V, or 4.1 V, or 4.2 V, or 4.3 V, or 4.4V, or 4.5 V, or 4.6 V, or 4.7V, or 4.8, or 4.9 V, or 5.0V. 
     Representative Embodiments 
     Embodiment 1 
     A material comprising Group14 elements silicon and carbon comprising φ&gt;0, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 2 
     A material comprising Group14 elements silicon and carbon comprising φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 3 
     A material comprising Group14 elements silicon and carbon comprising φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 4 
     A material comprising Group14 elements silicon and carbon comprising φ≥0.25, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 5 
     A material comprising Group14 elements silicon and carbon comprising φ≥0.3, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 6 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10 and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 7 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10 and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 8 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10 and φ≥0.25, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 9 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10 and φ≥0.3, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 9 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10, surface area &lt;50 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 10 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10, surface area &lt;50 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 11 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10, surface area &lt;30 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 12 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10, surface area &lt;30 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 13 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 14 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 15 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 16 
     A material comprising Group14 elements silicon and carbon comprising a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 17 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;50 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 18 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;50 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 19 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;30 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 20 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;30 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 21 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 22 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 23 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 24 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V. 
     Embodiment 25 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;50 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;70% microporosity. 
     Embodiment 26 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;50 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;70% microporosity. 
     Embodiment 27 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;30 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;70% microporosity. 
     Embodiment 28 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;30 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;70% microporosity. 
     Embodiment 29 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;70% microporosity. 
     Embodiment 30 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;70% microporosity. 
     Embodiment 31 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;70% microporosity. 
     Embodiment 32 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;70% microporosity. 
     Embodiment 33 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;30 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;80% microporosity. 
     Embodiment 34 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;30 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;80% microporosity. 
     Embodiment 35 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;80% microporosity. 
     Embodiment 36 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;80% microporosity. 
     Embodiment 37 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;80% microporosity. 
     Embodiment 38 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;80% microporosity. 
     Embodiment 39 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;30 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;90% microporosity. 
     Embodiment 40 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;30 m2/g, and ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;90% microporosity. 
     Embodiment 41 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;90% microporosity. 
     Embodiment 42 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;10 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;90% microporosity. 
     Embodiment 43 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.15, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;90% microporosity. 
     Embodiment 44 
     A material comprising Group14 elements silicon and carbon comprising 30% to 60% silicon by weight, a Z&lt;10, surface area &lt;5 m2/g, and φ≥0.2, φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and regime I is 0.8V-0.4V and Regime III is 0.15V-0V, and a carbon scaffold comprising a pore volume, wherein the pore volume comprises &gt;90% microporosity. 
     Embodiment 45 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 44 wherein the material comprising Group14 elements silicon and carbon comprises a Dv50 between 5 nm and 20 microns. 
     Embodiment 46 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon comprises a capacity of greater than 900 mA/g. 
     Embodiment 47 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises a capacity of greater than 1300 mA/g. 
     Embodiment 48 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises a capacity of greater than 1600 mA/g. 
     Embodiment 49 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises an average Coulobmic efficiency of ≥0.9970. 
     Embodiment 50 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises an average Coulobmic efficiency of ≥0.9975. 
     Embodiment 51 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises an average Coulobmic efficiency of ≥0.9980. 
     Embodiment 52 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises an average Coulobmic efficiency of ≥0.9980. 
     Embodiment 53 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises an average Coulobmic efficiency of ≥0.9985. 
     Embodiment 54 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises an average Coulobmic efficiency of ≥0.9990. 
     Embodiment 55 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises an average Coulobmic efficiency of ≥0.9995. 
     Embodiment 56 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises an average Coulobmic efficiency of ≥0.9999. 
     Embodiment 57 
     The material comprising Group14 elements silicon and carbon of any of the embodiments from Embodiment 1 to Embodiment 45 wherein the material comprising Group14 elements silicon and carbon composite comprises an average Coulobmic efficiency of ≥0.9999. 
     Embodiment 57 
     An energy storage device comprising a silicon-carbon composite described by any of the embodiments from Embodiment 1 to Embodiment 56. 
     Embodiment 58 
     A lithium ion battery comprising a silicon-carbon composite described by any of the embodiments from Embodiment 1 to Embodiment 56. 
     Embodiment 59 
     A particulate composite, comprising Group14 elements selected from silicon and carbon, wherein:
         A) the carbon comprises:
           i) a porous carbon scaffold comprising:
               a) amorphous carbon;   b) a pore volume, wherein greater than 70% of the pore volume resides in pores having a diameter less than 2 nm; and   c) a DPv90 less 50 nm;   
               
           B) the silicon comprises:
           i) amorphous, nano-sized silicon embedded within the pore volume of the carbon scaffold; and   
           C) the composite comprises:
           i) a surface area less than 30 m 2 /g;   ii) a capacity of greater than 1300 mA/g;   iii) an average Coulombic efficiency of greater than or equal to 0.9980, as measured in a half cell;   iv) a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis; and   v) a φ of greater than or equal to 0.15, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V-0V.   
               

     Embodiment 60 
     The particulate composite of Embodiment 59, wherein the surface area of the composite is less than 10 m 2 /g. 
     Embodiment 61 
     The particulate composite of any one of Embodiments 59 or 60, wherein the composite comprises from 30% to 70% by weight of the silicon. 
     Embodiment 62 
     The particulate composite any one of Embodiments 59 or 60, wherein the composite comprises from 40% to 60% by weight of the silicon. 
     Embodiment 63 
     The particulate composite of any one of Embodiments 59-62, wherein the Z is less than 5. 
     Embodiment 64 
     The particulate composite of any one of Embodiments 59-63, wherein the y is greater than or equal to 0.25. 
     Embodiment 65 
     The particulate composite of any one of Embodiments 59-64, wherein the average Coulombic efficiency is greater than or equal to 0.9985, as measured in a half cell. 
     Embodiment 66 
     The particulate composite of any one of Embodiments 59-65, wherein the pore volume of the porous carbon scaffold, in the absence of the embedded silicon, is greater than 0.5 cm 3 /g. 
     Embodiment 67 
     The particulate composite of any one of Embodiments 59-66, wherein the particulate composite comprises a first cycle efficiency of greater than 75%, as measured in a half cell coin cell cycled from 5 mV to 0.8 V. 
     Embodiment 68 
     The particulate composite of any one of Embodiments 59-67, having a Dv50 particle size ranging from 2 microns to 20 microns. 
     Embodiment 69 
     A particulate composite, comprising Group14 elements selected from silicon and carbon, wherein:
         A) the carbon comprises:
           i) a porous carbon scaffold comprising:
               a) amorphous carbon;   b) a pore volume of greater than 0.5 cm 3 /g; and   c) greater than 70% of the pore volume residing in pores having a diameter less than 2 nm;   
               
           B) the silicon comprises:
           i) amorphous, nano-sized silicon embedded within the pore volume of the carbon scaffold; and   
           C) the composite comprises:
           i) a surface area less than 30 m 2 /g;   ii) a capacity of greater than 1300 mA/g;   iii) an average Coulombic efficiency of greater than or equal to 0.9980, as measured in a half cell;   iv) a Z of less than 10, wherein Z=1.875×[(M1100−M)/M1100]×100%, wherein M1100 is a mass of the silicon-carbon composite at 1100° C. and M is the minimum mass of the silicon-carbon composite between 800° C. and 1100° C. when the silicon-carbon composite is heated under air from about 25° C. to about 1100° C., as determined by thermogravimetric analysis; and   v) a φ of greater than or equal to 0.15, wherein φ=(Max peak height dQ/dV in Regime I)/(Max peak height dQ/dV in Regime III), wherein dQ/dV is measured in a half-cell coin cell, and Regime I is 0.8V-0.4V and Regime III is 0.15V−0V.   
               

     Embodiment 70 
     The particulate composite of Embodiment 69, wherein the surface area of the composite is less than 10 m 2 /g. 
     Embodiment 71 
     The particulate composite of any one of Embodiments 69 or 70, wherein the composite comprises from 30% to 70% by weight of the silicon. 
     Embodiment 72 
     The particulate composite of any one of Embodiments 69 or 70, wherein the composite comprises from 40% to 60% by weight of the silicon. 
     Embodiment 73 
     The particulate composite of any one of Embodiments 69-72, wherein the Z is less than 5. 
     Embodiment 74 
     The particulate composite of any one of Embodiments 69-73, wherein the φ is greater than or equal to 0.25. 
     Embodiment 75 
     The particulate composite of any one of Embodiments 69-74, wherein the average Coulombic efficiency is greater than or equal to 0.9985, as measured in a half cell. 
     Embodiment 76 
     The particulate composite of any one of Embodiments 69-75, wherein the pore volume of the porous carbon scaffold, in the absence of the embedded silicon, is greater than 0.7 cm 3 /g. 
     Embodiment 77 
     The particulate composite of any one of Embodiments 69-76, wherein the particulate composite comprises a first cycle efficiency of greater than 75%, as measured in half cell coin cells cycled from 5 mV to 0.8 V. 
     Embodiment 78 
     The particulate composite of any one of Embodiments 69-78, having a Dv50 particle size ranging from 2 microns to 20 microns. 
     From the foregoing it will be appreciated that, although specific embodiments of the invention have been described herein for purposes of illustration, various modifications may be made without deviating from the spirit and scope of the invention. Accordingly, the invention is not limited except as by the appended claims.