Patent Publication Number: US-2021162691-A1

Title: Multilayer Intrinsic Sealants Based on Ionic Butyl

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
     This application is a continuation-in-part of, and claims the benefit of, U.S. patent application Ser. No. 16/819,701, filed Mar. 16, 2020, which is entitled “Pneumatic Tire with In-Situ Generated Sealant Composition by Chain Cessation of Ionic Butyl,” which is a continuation-in-part of, and claims the benefit of, U.S. patent application Ser. No. 14/991,575, filed Jan. 8, 2016, which is entitled “Pneumatic Tire Having Sealant Layer,” which is a continuation-in-part of, and claims the benefit of, U.S. patent application Ser. No. 14/572,138, filed Dec. 16, 2014, which is entitled “Pneumatic Tire Having Multiple Built-In Sealant Layers and Preparation Therefore,” and is incorporated herein by reference. 
    
    
     BACKGROUND OF THE INVENTION 
     The present invention is directed to tires having inner sealant layers, and in particular to tires having an ionic butyl-containing sealant layers formed from sealant precursor layers. 
     Tires consist of multiple annular layers of different compounds, plies, belts, etc., and they are applied before cure in tire building drum for accurate alignment and for higher interlayer bond strengths. Joining and aligning layers before cure result in tire with better uniformity and durability. 
     Tire puncture is an inherent issue for rubber pneumatic tires. Because of that, sealants have been developed and placed as a layer inner to the tire tread and plies to minimize the impact of the puncture. The absence of suitable technology forces tire companies to apply annular sealant layers after the tires are cured. Examination of recent passenger car (PCR) sealant tires from major tire manufacturers showed no curing bladder markings at the innermost sealant cover layer thus indicating that annular sealant layers are applied after the tires are cured. 
     Moreover, the majority of commercially available PCR sealant tires have exposed sealant to tire cavity, which must have been applied after the tire was cured, otherwise, it would foul the curing bladder during tire cure. In addition, in tire where sealant is applied to cured tire, there is only physical bonding and absence of chemical bonding or interfacial cross-linking at the sealant and innerliner interface, which results in relatively poorer adhesion. Poor adhesion may lead to separation of sealant from innerliner, thus losing nail hole sealing capability. Due to poor interfacial bonding, sealant may slide thus creating tire balancing issues. 
     Application of sealant to a cured tire is cumbersome since the innerliner needs to be very clean prior to sealant application for better physical bonding of sealant-to-innerliner. The way most tires are manufactured, the innermost layer is mostly contaminated with silicones from inside tire paint and/or from curing bladder lubricant for easy removal of tire from bladder mold. Moreover, application of perfectly aligned sealant inside cured tire is cumbersome and time consuming. Tire building machines have laser guidance which help operators to perfectly align layers in tire building drum which is possible if sealant precursor is applied before tire is cured so that sealant precursor forms sealant during cure. 
     Sealants in cured tires need to have low viscosity (or low storage modulus, G′) so that the sealants can easily flow and plug nail holes. Such low viscosity material cannot be directly applied in tire building drum as they will shift, fall off, or deform if applied in tire building drum. Further, punctures can occur at any temperature. A single layer of sealant of low viscosity may work very well at low temperature, but at high temperatures, it might achieve a very low viscosity, which would allow it to flow and pass out of tire during use and pollute and/or damage roadways. By depleting the tire sealant, the tire loses its puncture sealing capacity. Likewise, a single layer of sealant of high viscosity may be very good for high temperature but might be almost solid at cold temperature and thus unable to flow to plug puncture in tires at cold temperature. Thus, one layer of high viscosity sealant may be good for summer tire but it may not be good for winter tire. Likewise, one layer of low viscosity sealant may be good for winter tire but it may not be good for summer tire as it may displace during use or pass out from puncture as viscosity becomes very low at high temperature. For all season tire, two-layer sealant is preferred, one for low temperature puncturing sealing and one for high temperature puncture sealing. Moreover, high viscosity sealant layer will tightly hold the low viscosity sealant layer due to interfacial bonding and prevent its movement even when its viscosity become very low in summer months. So, the bonding between the multiple sealant layers must be good to prevent sealant movement particularly the one with low viscosity. 
     Tires with built-in sealant layer are known in the art. Typically, these tire sealants are formed during tire cure by thermal degradation of peroxide-containing butyl-rubber-based sealant precursor layers, such as for example, U.S. Pat. Nos. 4,895,610; 6,962,181; 7,073,550; 7,674,344; and 8,293,049; and US Patent Publication Nos. 2005/0113502 and 2005/021568, the teachings of which are all hereby incorporated by reference. Sealant layers may be of black or non-black colors and may incorporate short fibers, such as polyester or polyurethane fibers, and other filler aggregate into sealant layers to help to plug nail hole punctures. 
     It is possible to produce a sealant using ionic butyl. However, simply substituting regular butyl with ionic butyl will not work in production environment. It may be possible to make such an arrangement work with an inefficient, time-consuming, carefully-crafted, hand-made tire, but for working in a production environment, building tack to self needs to be very good e.g. 5 lbs/inch or higher. Intrinsic sealant tires are built by wrapping the sealant layer in tire building drum, overlapping and stitching slightly the two ends. If tack to self is low, the overlapped area will separate causing tire building issues. Such desirable tack to self can be achieved by reducing filler content, changing plasticizer, and using rosin type tackifier alone or in combination with phenolic type. 
     One of the ways to apply sealant precursor layer is to apply calendered material rolled with a film. The sealant precursor should be removable from film with slight tension without distorting the sealant precursor. Calendered roll may sit in the inventory for several months before being used, so during that time, the tack needs to remain good. One of the ways for accelerated testing is to measure tack after exposing the test surface to air after removing the wrapped film for a short period of time, e.g., 24 hours, instead of waiting for several months or years to test the roll. If exposed tack is good, one can extrapolate that the tack in calendered roll will stay good for prolonged length of time. 
     BRIEF SUMMARY OF THE INVENTION 
     The invention is directed to a tire with in-situ generated two or more intrinsic puncture sealant layers based on ionic butyl with two or more different viscosities comprising a supporting tire carcass having one or more layers of ply, an outer circumferential tread, and a radially inner layer, a pair of beads, sidewalls extending radially inward from the axial outer edges of a tread portion to join the respective beads, a sealant comprising an outer layer of sealant and an inner layer of sealant, disposed radially inwardly from said radially inner layer of said tire carcass, wherein the outer layer of sealant and the inner layer of sealant have different viscosities, wherein said sealant provides self-sealing properties to the tire, and wherein said inner layer of sealant is in direct contact with and interfacially cross-linked to said outer layer of sealant with no barrier separating said inner and outer layers of sealant. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The foregoing and other features and advantages of the present invention will become apparent to those skilled in the art to which the present invention relates upon reading the following description with reference to the accompanying drawings, in which: 
         FIG. 1  is a cross-sectional view of a cured tire using the present invention, 
         FIG. 2  is a cross-sectional enlarged view of the tire in  FIG. 1  taken along line  2 - 2 , 
         FIG. 3  is a side cross-section of a prior art tire showing sealant pooling and sagging, and 
         FIG. 4  is a cross-section of prior art tire with compartments (U.S. Pat. No. 10,737,539). 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     The present invention is directed to a tire having two intrinsic (or integral, or built-in) sealant layers formed from two precursor layers during tire cure by chain scission of butyl ionomer compositions catalyzed by peroxide. Thus, the tire has two or more very low molecular weight butyl ionomer sealant layers disposed inside the tire formed from two or more very high molecular weight butyl ionomer sealant precursor layers. (As used herein, the term intrinsic is synonymous with integral or built-in). 
     When chain scission of high molecular weight ionic butyl polymer occurs, relatively lower molecular weight ionic butyl polymer is formed. Such extremely low molecular weight ionic butyl polymer can also be called liquid ionic butyl polymer or ionic butyl oligomer. As used herein, “oligomer” refers to a material having molecular weight significantly lower than the original polymer/rubber. Oligomers are tacky to touch and often are high viscous liquid. Degree of chain scission can be controlled by adjusting the amount of peroxide, type of peroxide, and combination of peroxides, and also by adjusting the levels and types of plasticizer or filler. 
     Most rubbers, like natural rubber (NR), nitrile rubber (NBR), styrene-butadiene rubber (SBR), bromobutyl rubber (BIIR), chlorobutyl rubber (CIIR), butadiene rubber (BR), etc., crosslink when heated with suitable peroxide and storage modulus (G′) increases after cure. One known exception is butyl rubber (IIR) where chain scission occurs resulting in decrease in viscosity or G′ after heating to tire cure temperature. 
     Ionic butyl is prepared by introducing ionic group in BIIR: 
     
       
         
         
             
             
         
       
     
     Unlike BIIR, ionic butyl undergoes chain scission when heated with suitable peroxide. This new property generated by converting BIIR into ionic butyl can be used to make a sealant precursor which can be applied in the tire building drum that undergoes chain scission during tire cure forming sealant layer. This allows for a suitable much less cumbersome, manufacturing-friendly PCR tire where sealant precursor layer is applied in tire building drum which is converted into a sealant layer during tire cure. Small amount of double bond present in ionic butyl undergoes crosslinking reaction thus enhancing inter-layer bond strengths e.g. sealant cover layer to sealant layer, between the multiple sealant layers, and sealant layer to innerliner. 
     Viscosity is dependent on temperature and it reduces with increasing temperature. High viscosity sealant may be good for summer months but if the viscosity is too low, it will pass out from tire puncture like passing of air/liquid. Low viscosity sealant is good for winter months but if viscosity is too high, it may be like other tire layers will not flow and plug nail hole causing flat tire. Thus, it can be beneficial to use multilayer sealant of different viscosities. 
     Multiple viscosity sealant can be generated by using different type of peroxide, quantity of peroxide, and their combination, or by changing type and amount of filler or plasticizer. The sealant precursor composition must be tacky to self for user-friendliness for the tire-builder. Sealant compositions based on regular butyl has been described in previous patents. 
     When regular butyl was replaced with ionic butyl, the building tack to self of the ionic butyl sealant composition was negligible relative to regular butyl. Tires are built by putting layer in tire building drum and the ends are slightly overlapped and stitched with a roller. If tack to self is low, separation at the overlapped area occurs, causing tire building issues. To improve building tack, a large number of experiments were conducted using many tackifiers and combination of tackifiers to find suitable tackifier or combination of tackifiers for ionic butyl. 
     For tire-builder user-friendliness (i.e. ease of use), high building tack is desired otherwise ends of sealant precursor overlapped slightly and stitched with a roller can separate causing building issues. Tackifiers commonly used with regular butyl do not work with ionic butyl. While regular butyl tack is very high, corresponding ionic butyl tack is very low (Table 4). During early experiments, it was found that phenolic-type tackifier (SP1068) in combination with Novares C10 plasticizer imparts higher unexposed tack than when naphthenic oil is used as plasticizer (4.23 lbs/inch vs 0.76 lbs/inch, Table 5). Thus for ionic butyl rubber, Novares C10 is a better plasticizer than most commonly and naturally used oil as plasticizer for compounding tire layer. Thus use of Novares C10 for plasticizing ionic butyl is considered as new finding. Sealant materials rolled with a film during calendering must retain tack during the aging of the roll so that the tack to self remains good when ready to use. One way to determine tack loss with storage is by accelerated test using sealant layer exposed to air for 24 hours. As noted above, if the sealant tack to self remains good after 24 hours, it means that the sealant tack will remain good when rolled with film and not exposed to air for several months or even years. 
     The tire comprises a supporting tire carcass comprised of one or more layers of ply, an outer circumferential tread, and a radially innermost innerliner layer, a pair of beads, sidewalls extending radially inward from the axial outer edges of the tread portion to join the respective beads, two or more sealant layers, and a cover layer, disposed on said tire carcass innermost layer, wherein the sealants are formed during tire cure due to high temperature and pressure by chain scission of butyl ionomer based compounds in the presence of peroxide to form an inner layer of low molecular weight butyl ionomer sealant, disposed inwardly from said tire carcass inner layer, to provide self-sealing properties to the tire. 
     As used herein, the term “sealant precursor” means the compound by itself is not a sealant, but it is transformed into sealant by chain scission during the curing step of tire construction. The “precursor layer” is the layer of sealant precursor. The precursor layer can be 100% ionic butyl rubber or can be ionic butyl rubber blended with other rubbers that can be transformed into a sealant, such as a mixture or both butyl ionomer and butyl rubber, which also undergo chain scission during tire curing at high temperature to form low molecular weight, easy to flow, tacky sealants. 
     In the present invention, two or more sealant precursor layers are assembled into an unvulcanized rubber tire (generally called a “green tire”) using conventional tire building techniques. After an unvulcanized tire is built, including such a sealant precursor layer, the tire is vulcanized employing standard methods. Such a sealant precursor layer is assembled into the tire inwardly from the tire&#39;s supporting carcass and outwardly from an innerliner layer (which can be an air barrier layer) in the unvulcanized tire. Alternatively, the sealant precursor layer can also be placed inner to tire innerliner, and, in this case a sealant cover layer is needed, inner to sealant precursor layer with width greater than the sealant precursor layer. The purpose of the sealant cover layer is to prevent thinning of the sealant layer by pressure of the tire curing bladder and to prevent contamination of the tire curing bladder by the tacky sealant. Even after the tire is cured, sealant cover layer protects the tacky sealant from capturing contaminants or even small animals or birds if not appropriately stored. 
     The physical nature of the sealant precursor layer is that its viscosity is high enough to permit easy handling during the standard steps in the construction of an unvulcanized tire, that is, the sealant precursor layer has enough uncured strength (modulus) to retain its shape during building, and enough tack to self so that the two overlapped ends after stitching with a roller in a tire building drum do not easily separate and also preferably enough tack to stick to adjacent layers during green tire building. After high temperature and pressure vulcanization, sealant layer with low G′ is sandwiched between cured layers of significantly higher G′. A typical change of G′ at 80° C. of sealant precursor layer (chain scission) and sealant cover layer (crosslinking reaction) by applicants own experimentations is shown below: 
     
       
         
           
               
               
               
             
               
                   
                   
               
               
                   
                 Sealant Precursor * 
                 Sealant Cover Layer 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
            
               
                 G′ at 80° C./5%/1 Hz (MPa) 
                 0.16 
                 0.12 
               
               
                 Tire cure at high temperature 
                 Chain scission to 
                 Crosslinking 
               
               
                 and pressure 
                 form sealant 
                 reaction 
               
               
                 G′ at 80° C./5%/1 Hz (MPa) 
                 0.002-0.1 
                 2.5  
               
               
                   
               
               
                 * Varied amount and type of peroxide 
               
            
           
         
       
     
     As the green tire is heated for cure with sealant precursor layers, sealant layers are formed in situ, by chain scission of ionic butyl. In effect, the ionic butyl rubber in the sealant precursor layer formed a low viscosity (or low G′), easy to flow tacky material by chain scission reaction, which has puncture sealing properties. Thus, the sealant precursor layer is transformed into a puncture sealant layer during the high temperature curing of the tire. The chain scission of the sealant precursor layer is effectuated by the presence of one or more peroxides which acts as a catalyst. 
     Unlike the instant patent application where sealant precursor based on ionic butyl without any solvent is applied in tire building drum for subsequent chain scission, in prior art, Kaszas et al. (2016/0068031) tried to apply crosslinked butyl swelled in a high boiling liquid inside cured tire. Kaszas et al. never demonstrated sealant formation using peroxide but it appears the authors assumed a crosslinking reaction would take place with peroxide, but apparently never actually tested it. Had Kaszas et al. tried peroxide, they would have found that chain scission would have occurred resulting in the formation of a very low viscosity fluid with less viscosity than original solvent polymer mixture. This low viscosity fluid could not have been used as tire sealant and would have rapidly passed out of tire puncture. 
     Most rubber, including halobutyl rubber, crosslinks with peroxide. Since ionic butyl is derived from halobutyl, Kaszas et al. apparently thought that ionic butyl would also crosslink with peroxide. However, through experimentation, the inventors of the instant application discovered that ionic butyl undergoes chain scission and hence can be utilized for intrinsic/built-in sealant tire. If Kaszas et al. had put peroxide as crosslinking agent in their experimentation, ionic butyl would have undergone chain scission instead of crosslinking as they thought would have occurred resulting is very low viscosity sealant that would have instantly passed out of tire causing flat and polluting the roadway. 
     Butyl ionomers are derived from halobutyl rubber. Halobutyl rubbers are derived from butyl rubber. Butyl rubber is produced by copolymerizing isobutylene with small amounts of isoprene. Generally, butyl rubber contains from about 0.5 to 4 mole % isoprene and from about 96 to 99.5 mole % percent isobutylene unit. The butyl rubber that can be employed in the polymer composition of the tires of this invention has a number average molecular weight in the range of 200,000 to 600,000 and preferably in the range of about 300,000 to about 500,000. Butyl rubber is then converted to bromobutyl rubber, which is then transformed to butyl ionomers by converting the bromine functionalities into ionic imidazolium bromide groups which results in the formation of reversible ionic associations that exhibit physical cross-linking ability. 
     At least one butyl ionomer is available from Arlanxeo with trade name X_Butyl™ I4565P that has ML(1+8) value of 56±4 MU at 125° C. and ion content of 0.4±1 mole %, total reactive bromine content of 0.5±0.2 mole % and 1,4-isoprene content of 0.5±0.2 mole %. 
     Compositions based on 100 phr butyl ionomer rubber can be used in making sealant precursor. Butyl ionomer can be used in combination with other elastomers that degrade at tire cure temperature. One example of such polymer is butyl rubber. Thus, 100 to 5 phr ionic butyl in combination with 0 to 95 phr butyl rubber can be used to create tire puncture sealant composition. 
     It is preferable for the polymer composition layer assembled into the tires of this invention to have the following composition in parts per hundred rubber (phr): 
     100 phr butyl ionomer rubber e.g. X_butyl™ I4565P from Arlanxeo 
     about 10 to 80 phr of silicon dioxide e.g. Silene 732D or other filler 
     about 1 to 30 phr of tackifier or combination of tackifiers e.g. gum rosin, SP-25 
     about 20 to 200 phr calcium carbonate e.g. Hubercarb Q3 from Huber 
     about 5 to 35 phr Novares C10 plasticizer, and 
     from about 4 to 16 phr suitable peroxide. 
     Any peroxide or combination of peroxides that catalyze the chain scission of ionic butyl based precursor compound at tire cure temperature (130°−210° C.) can be employed. Preferably peroxide compounds are employed which only disintegrate at high temperatures, that is, above about 100° C. (212° F.). Examples of such peroxides are tert-butyl perbenzoate and dialkyl peroxides with the same or different radicals, such as dialkylbenzene peroxides, and alkyl peresters. Preferably the peroxide vulcanizing agent employed will contain two peroxide groups. Frequently the peroxide groups are attached to a tertiary butyl group. The basic moiety on which the two peroxide groups are suspended can be aliphatic, cycloaliphatic, or aromatic radicals. Some representative examples of such peroxide vulcanizing agents include: 2,5-bis(t-butyl peroxy)-2,5-dimethyl hexane; 1,1-di-t-butyl peroxy-3,3,5-trimethyl cyclohexane; 2,5-dimethyl-2,5-di(t-butyl peroxy) hexyne-3; p-chlorobenzyl peroxide; 2,4-dichlorobenzyl peroxide; 2,2-bis-(t-butyl peroxy)-butane; di-t-butyl peroxide; benzyl peroxide; 2,5-bis(t-butyl peroxy)-2,5-dimethyl hexane, dicumyl peroxide; and 2,5-dimethyl-2,5-di(t-butyl peroxy) hexane. Such peroxide catalyst for chain scission can be added to the polymer composition layer in pure form (100 percent active peroxide) or on an inert, free-flowing mineral carrier. Calcium carbonate and silica are some examples of inert carrier. Such carrier composition containing from about 35 to 60 weight percent active ingredient (peroxide) can be employed very successfully. For example, 40 percent by weight dicumylperoxide on an inert carrier can be employed as the peroxide in the polymer composition layer with good results. 
     While the mechanism may not be fully understood, it is within the scope of the present invention to employ an activating agent, such as 2,2,6,6-tetra alkyl piperidine based hindered amine, which will activate the organoperoxide, and in a sense, enable a reduction in the amount of the organoperoxide to more efficiently degrade the butyl ionomer rubber during the formation of the sealant layer. Such activating agents are known in the art, such as U.S. Pat. No. 7,674,344 to D&#39;Sidocky et al., the disclosure of which is incorporated by reference. 
     One representative example of such 2,2,6,6-tetra alkyl piperidine based hindered amine is, for example, a 50/50 mixture of poly[[6-[1,1,3,3,-tetramethylbutyl)amino]-s-triazine-2,4-diyl][2,2,6,6,-tetramethyl-4-piperidyl)imino] hexamethylene[(2,2,6,6-tetramethyl-4-piperidyl)imino]] compound (referred to herein as “PTP”) and bis(hydrogenated tallow alkyl), amines oxidized and sold as Irgastab® FS410 FF from BASF. 
     Another example of peroxide activating agent is a mixture of PTP, bis(hydrogenated tallow alkyl) amies oxidized, and bis(2,2,6,6-tetramethyl-4-piperidinyl) sebacate sold as Irgastab® FS811 from BASF. 
     Another example of peroxide activating agent is poly[[6-[1,1,3,3,-tetramethylbutyl)amino]-1,3,5-triazine-2,4-diyl][2,2,6,6,-tetramethyl-4-piperidyl)imino]-1,6-hexanediyl[(2,2,6,6-tetramethyl-4-piperidinyl)imino]] available as Chimassorb® 944 FDL from BASF. 
     In practice, exemplary of composites that contain, and therefore are comprised of, said PTP, which may also comprise said bis(2,2,6,6-tetramethyl-4-piperidinyl)sebacate and which may also optionally contain an oxidized bis(halogenated tallow alkyl amine). In practice, the aspect of utilizing said 2,2,6,6-tetra alkyl piperidine based hindered amines, and particularly said PTP or composites of 2,2,6,6-tetra alkyl piperidine based hindered amines which contain (include) said PTP to activate the organoperoxide in the chain scission of the butyl ionomer rubber of the sealant precursor is considered herein to be important in order to reduce as much as possible the concentration of the organoperoxide in the sealant precursor based on butyl ionomer rubber-based composition. 
     The various components of the sealant layer can be mixed together using any convenient rubber mixing equipment, such as a Banbury mixer. This rubber composition used in the sealant layer has sufficient viscosity (or G′) and unvulcanized tack to enable its incorporation into an unvulcanized tire without departing from standard, long standing tire building techniques and without the use of complicated, expensive tire building equipment. 
     The strip of butyl ionomer based sealant precursor composition should extend from one shoulder of the tire to the other, in other words, it should cover the crown area of the tire. The thickness of the sealant precursor layer can vary depending on tire size. Generally, the thickness of the polymer composition layer will range from about 0.1 cm (0.04 inches) to about 0.635 cm (0.25 inches). It is generally preferred for the polymer composition layer to have a thickness of 0.2 cm (0.08 inches) to 0.4 cm (0.16 inches). In passenger tires it is normally most preferred for the polymer composition layer to have a thickness of about 0.25 cm (0.1 inches). 
     After the unvulcanized pneumatic rubber tires of this invention are assembled, they are vulcanized using a normal tire cure cycle. The tires of this invention can be cured over a wide temperature range. However, it is generally preferred for the tires of this invention to be cured at a temperature ranging from about 132° C. (270° F.) to about 166° C. (330° F.). It is more preferred for the tires of this invention to be cured at a temperature ranging from a 143° C. (290° F.) to 177° C. (350° F.). 
     Sealant Cover Layer 
     In commercially available passenger (PCR) sealant tires, no bladder mark on sealant cover layer or the sealant has no sealant cover layer indicating that sealant is applied after the tire is cured. In commercially available Duraseal™ truck bus radial (TBR) tire, innerliner has bladder mark thus indicating that the sealant is applied after the tire is cured and placed underneath the innerliner or outer to innerliner. Since TBR innerliner is very thick for tire air retention, such innermost layer cannot stretch and plug nail holes. When there is a sealant underneath innerliner, there is a layer between sealant and ply to prevent sealant to enter between the cords of the ply. It is preferred that the sealant be placed inner to innerliner and covered with a readily stretchable thin sealant cover layer so that in some cases it can stretch and plug nail holes. 
     Compositions of three different sealant cover layers are shown in Table 1 and one of the sealant cover layers is same as tire innerliner. Three-layer laminates were stitched together with a roller followed by bladder molding details of which are shown in Table 2. When the sealant cover layers were based on 100BIIR or 50BIIR/50NR, bulging of the laminate occurred when they come out hot fresh out of mold. When the sealant cover layer was based on 50BR/50NR bulging of the laminate did not occur when they come out hot fresh out of mold (insert in Table 2). 
     
       
         
           
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                 Three different sealant cover layers investigated 
               
               
                 (All ingredients in parts per hundred rubber (phr)) 
               
            
           
           
               
               
               
               
            
               
                   
                 Innerliner 
                 0C007D 
                 0C028C 
               
               
                   
                   
               
            
           
           
               
            
               
                 1 st  Step 
               
            
           
           
               
               
               
               
            
               
                 High cis BR (Buna CB 1220) 
                   
                   
                 50 
               
               
                 BIIR 
                 100 
                 50 
               
               
                 NR (SMRL) 
                   
                 50 
                 50 
               
               
                 Agilon 400G 
                   
                 50 
                 30 
               
               
                 N 660 Carbon Black 
                 60 
               
               
                 Austin Black 325 
                 15 
               
               
                 TiO 2  (Rutile) 
                   
                 2 
               
               
                 Akrosprerse 4283 Red 
                   
                 2 
               
               
                 Naphthenic oil (Stanplas 150) 
                 10 
                 10 
                 6 
               
               
                 Struktol 40MS 
                 5 
               
               
                 Stearic acid 
                 2 
                 2 
               
               
                 MgO 
                 1 
                 1 
               
               
                 SP1048 
                 6 
                 4.5 
               
               
                 Clay 
                   
                 20 
               
               
                 Wingtack 86 
                   
                 8 
               
               
                 TMQ 
                   
                   
                 1.5 
               
               
                 Perkalink 900 
                   
                 2 
                 2 
               
               
                 6 PPD 
                   
                   
                 1.5 
               
               
                 Microcrystalline wax (Akrowax Micro 23) 
                   
                   
                 2 
               
            
           
           
               
            
               
                 2 nd  Step 
               
            
           
           
               
               
               
               
            
               
                 CBS/CBTS (A) 
                   
                   
                 1 
               
               
                 ZnO 
                 3 
                 3.72 
                 1.25 
               
               
                 RM Sulfur (S) 
                 0.5 
                 0.22 
                 0.75 
               
               
                 75% DPG 
                   
                 1.33 
               
               
                 MBTS 
                 1.5 
                 1.7 
                   
               
               
                 TOTAL 
                   
                   
                 146 
               
               
                 Estimated Sp. Gravity 
                   
                   
                 0.94 
               
            
           
           
               
            
               
                 Physical Properties 
               
            
           
           
               
               
               
               
            
               
                 Cure time at 150° C. 
                   
                   
                 30 
               
               
                 Duro 
                 56 
                 38 
                 32 
               
               
                 M300 
                 599 
                 245 
                 242 
               
               
                 Tensile Strength (psi) 
                 1244 
                 1444 
                 1783 
               
               
                 Elongation (%) 
                 709 
                 834 
                 791 
               
               
                 Die C Tear (lb/inch) 
                 210 
                 120 
                 234 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
             
               
                 TABLE 2 
               
               
                   
               
               
                 Bladder molding of laminates of innerliner - 
               
               
                 sealant precursor - sealant cover 
               
               
                 (350° F./220 psi/12 min) 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
               
            
               
                 Innerliner Layer 
                 6″ × 6″ × 0.15″ 
               
               
                 (0C015A) 
               
               
                 Sealant Precursor 
                 4″ × 4″ × 0.1″  
               
               
                 Layer (0C020C) 
               
            
           
           
               
               
               
               
            
               
                 Sealant cover Layer 
                 100BIIR 
                 50BIIR/50NR 
                 50BR/50NR 
               
               
                 (6″ × 6″ × 0.15″) 
               
            
           
           
               
            
               
                 Laminate immediately after coming out from bladder mold 
               
            
           
           
               
               
               
               
            
               
                 Appearance 
                 Bulging 
                 Bulging 
                 No bulging 
               
               
                 Picture 
                 
                   
                 
                 
                   
                 
                 
                   
                 
               
               
                   
               
            
           
         
       
     
     In prior art, it was mentioned that bulging can be prevented by drilling hole in innerliner followed by attachment of a non-woven layer so that gases escape without contaminating the curing bladder (See, Majumdar et al. U.S. Pat. No. 8,316,903) and was reduced to practice. However, prevention of bulging by using a thin layer of rubber composition based on 50BR/50NR never has been experimentally tried and hence never been reduced to practice. 
     Interpretation of Bulging of Sealant Cover Layer 
     During heat treatment of sealant precursor layer, chain scission of ionic butyl leads to the formation of lower molecular weight ionic butyl. During the reaction of peroxides with ionic butyl, some volatiles and gaseous byproducts are also produced resulting in bulging at high temperature of the first two laminates. However, the third laminate did not bulge. It is hypothesized that volatiles produced permeated through 50BR/50NR sealant cover layer but could not permeate immediately through the other two sealant cover layers based on 100BIIR or 50BIIR/50NR. Hypothesis is supported by permeation data of rubbers obtained from ExxonMobil web site and are shown in Table 3 (Exxon Mobile Chemicals, https://3.imimg.com/data3/EE/JO/MY-8754992/butyl-rubb er-sheets.pdf) 
     
       
         
           
               
             
               
                 TABLE 3 
               
             
            
               
                   
               
               
                 Permeability of various elastomers used in tires to gases at 25° 
               
               
                 C. relative to natural rubber gum vulcanizates = 100 
               
            
           
           
               
               
               
               
               
            
               
                 Elastomer 
                 O 2   
                 N 2   
                 CO 2   
                 Air 
               
               
                   
               
            
           
           
               
               
               
               
               
            
               
                 Natural rubber (NR) 
                 100 
                 100 
                 100 
                 100 
               
               
                 Polybutadiene or Butadiene Rubber (BR) 
                 82 
                 80 
                 105 
                 81 
               
               
                 Styrene-butadiene Rubber (SBR) 
                 73 
                 78 
                 94 
                 76 
               
               
                 Butyl Rubber (HR) 
                 5.6 
                 5 
                 4 
                 4.8 
               
               
                   
               
            
           
         
       
     
     This is a significant advancement in built-in-sealant or intrinsic sealant technology. Now it is possible to build tire with a very thin layer of sealant cover layer without worrying about its tear or catastrophic burst as tires comes out of mold or trapped volatiles between sealant and sealant cover layer. No longer a thick innerliner is needed to contain the sealant as in commercially available Durseal™ tire produced by built-in sealant technology based on regular butyl. Volatiles and liquids formed as byproducts coexist with sealants in Duraseal™ tire may result in movement of sealant thus impairing tire balance which require expensive compartmentalization (U.S. Pat. No. 10,737,539), see  FIG. 4 . Thin layer of sealant cover, means less rubber use thus reducing the overall tire weight which translates to higher fuel economy from such built-in sealant tire and less heat built-up translate to longer tire durability. Moreover, when a vehicle is at rest, sealant will not sag or concentrate at bottom due to gravity which may occur in tires without sealant cover layer particularly during summer months when the viscosity is low (see  FIG. 3 ). 
       FIG. 4 . shows a prior art tire (U.S. Pat. No. 10,737,539) with sealants in 9 compartments. During tire rotation, due to centrifugal force, sealant tend to flow into the central crown area, near the center point (CP) leaving the areas near the shoulder unprotected. The same sealant is used thoughout, but in many compartments  11 ,  20 ,  21 ,  22  to prevent depletion at two edges. In the present invention, no significant air pocket or liquid chain scission product is present to move sealant layer. Therefore, the compartments as shown in  FIG. 4  are not needed in the present invention. In the instant patent application, sealant is tightly contained and covered with sealant cover layer with no space to move to a different location. 
     Determination of Unexposed Tack 
     Sealant precursor of thickness 0.08 inches is formed between two films. Film from one side was removed from two pieces. Precursor sides of two pieces of materials are stitched with a roller keeping some area for the test equipment jaw. Then 180° angle peel strength was determined at room temperature as is well known to those familiar with the art. 
     Determination of Exposed Tack 
     Similar process as unexposed tack determination except that two pieces are exposed to air in a conditioned room for approximately 24 hours and then two pieces are stitched with a roller followed by determination of 180° angle peel strength. 
     Sealant Precursor Based on Regular Butyl Vs Ionic Butyl 
     Sealant precursor based on regular butyl and corresponding ionic butyl are mixed, details of which are shown in Table 4. Unexposed and exposed tack to self were determined and recorded in Table 4. It shows that while tack to self of regular butyl sealant precursor is good to build tires while tack to self of ionic butyl sealant is negligible and building tires will be cumbersome. 
     After sealant formation, tan δ at 80° C. of regular butyl is 1.56 while tan δ of ionic butyl at 80° C. is 94% lower with a value of 0.09. It is well known to those familiar with tire material compounding, lower tan δ is preferred for lower heat built-up during flexing. This shows that in built-in sealant based on ionic butyl, heat rise from flexes during tire use is expected to be significantly lower in sealant based on ionic butyl than sealant based on regular butyl like in Duraseal™ tires. This translates to higher durability of built-in sealant tire based on ionic butyl than the ones based on regular butyl. 
     
       
         
           
               
             
               
                 TABLE 4 
               
             
            
               
                   
               
               
                 Sealant precursors based on regular butyl and ionic butyl 
               
               
                 (All ingredients in parts per hundred rubber (phr)) 
               
            
           
           
               
               
               
            
               
                   
                 Regular Butyl 
                 Ionic Butyl 
               
               
                   
                   
               
            
           
           
               
               
               
               
            
               
                   
                 Regular butyl 
                 100 
                   
               
               
                   
                 Ionic Butyl 
                   
                 100 
               
               
                   
                 Naphthenic Oil 
                 18 
                 18 
               
               
                   
                 Silene 732D 
                 20 
                 20 
               
               
                   
                 SP1068 
                 10 
                 10 
               
               
                   
                 Struktol 40MS 
                 5 
                 5 
               
               
                   
                 Akrosperse 409 Green 
                 0.5 
                 0.5 
               
               
                   
                 Calcium Carbonate 
                 100 
                 100 
               
               
                   
                 AkroChem VC 40K 
                 5 
                 5 
               
            
           
           
               
            
               
                 PRECURSOR PROPERTIES 
               
            
           
           
               
               
               
               
            
               
                   
                 Unexposed Tack (lbs/inch) 
                 11.26 
                 0.76 
               
               
                   
                 Exposed Tack (lbs/inch) 
                 7.02 
                 0 
               
            
           
           
               
            
               
                 PROPERTIES OF SEALANT 
               
            
           
           
               
               
               
               
            
               
                   
                 Tan δ at 80° C. 
                 1.56 
                 0.09 
               
               
                   
                 G′ (MPa) 
                 0.036 
                 0.043 
               
               
                   
                   
               
            
           
         
       
     
     Table 5 shows effect of replacing naphthnic oil with Novares C10 liquid. The unexposed tack improves from 0.76 lb/inch to 4.23 lbs/inch. As higher building tack is needed from ionic butyl-based sealant precursor, substitution of oil with Novares C-10 liquid makes sense, although, composition need to be further improved to get higher exposed tack 
     
       
         
           
               
             
               
                 TABLE 5 
               
             
            
               
                   
               
               
                 Naphthenic oil vs oil substitute (Novares C10) 
               
               
                 in sealant precursor based on ionic butyl 
               
               
                 (All ingredients in parts per hundred rubber (phr)) 
               
            
           
           
               
               
               
            
               
                   
                 Naphthenic oil 
                 Novares C-10 
               
               
                   
                   
               
            
           
           
               
               
               
               
            
               
                   
                 Ionic butyl 
                 100 
                 100 
               
               
                   
                 Naphthenic Oil 
                 18 
               
               
                   
                 Novares C10 
                   
                 18 
               
               
                   
                 Silene 732D 
                 20 
                 20 
               
               
                   
                 SP1068 
                 10 
                 10 
               
               
                   
                 Struktol 40MS 
                 5 
                 5 
               
               
                   
                 Akrosperse 409 Green 
                 0.5 
                 0.5 
               
               
                   
                 Calcium Carbonate 
                 100 
                 100 
               
               
                   
                 AkroChem VC 40K 
                 5 
                 5 
               
            
           
           
               
            
               
                 PRECURSOR PROPERTIES 
               
            
           
           
               
               
               
               
            
               
                   
                 Unexposed Tack (lbs/inch) 
                 0.76 
                 4.23 
               
               
                   
                 Exposed Tack (lbs/inch) 
                 0 
                 0 
               
            
           
           
               
            
               
                 PROPERTIES OF SEALANT 
               
            
           
           
               
               
               
               
            
               
                   
                 Tan δ at 80° C. 
                 0.09 
                 0.084 
               
               
                   
                 G′ (MPa) 
                 0.043 
                 0.06 
               
               
                   
                   
               
            
           
         
       
     
     To improve building tack, a large number of tackifiers were tried, details of which are shown in Table 6. Some tackifiers showed better than others and exposed tack were not yet satisfactory as maximum value obtained was 1.87 lbs/inch which is still not sufficient. 
     
       
         
           
               
             
               
                 TABLE 6 
               
             
            
               
                   
               
               
                 Evaluation of several tackifiers in sealant precursor composition based on ionic butyl 
               
               
                 (All ingredients in parts per hundred rubber (phr)) 
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                   
                 26A1 
                 26A2 
                 26A3 
                 26A4 
                 26A5 
                 26B1 
                 26A7 
                 26A8 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                 1 st  Mixing Step 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 (Drop 160° C.) 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Butyl Ionomer 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
               
               
                 Novares C-10 
                 23 
                 23 
                 23 
                 23 
                 23 
                 23 
                 23 
                 23 
               
               
                 R40 
                 10 
                   
                   
                   
                   
                   
                   
                   
               
               
                 R98 
                   
                 10 
                   
                   
                   
                   
                   
                   
               
               
                 M130 
                   
                   
                 10 
                   
                   
                   
                   
                   
               
               
                 HXL100 
                   
                   
                   
                 10 
                   
                   
                   
                   
               
               
                 RP103 
                   
                   
                   
                   
                 10 
                   
                   
                   
               
               
                 SP-25 
                   
                   
                   
                   
                   
                 15 
                   
                   
               
               
                 D95 
                   
                   
                   
                   
                   
                   
                 10 
                   
               
               
                 Gum Rosin 
                   
                   
                   
                   
                   
                   
                   
                 10 
               
               
                 Akrosperse 409 Green 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
               
               
                 EPMB 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Silene 732D 
                 20 
                 20 
                 20 
                 20 
                 20 
                 20 
                 20 
                 20 
               
               
                 Calcium Carbonate 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
               
               
                 2 nd  Mixing Step 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 (Drop 110° C.) 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Akrochem VC-40K 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
               
               
                 TOTAL 
                   
                   
                   
                   
                   
                   
                   
                   
               
            
           
           
               
            
               
                 Tack to self (a) in lbs/inch—1-days after test pieces preparation (M = Medium) 
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                 Unexposed 
                 4.98 
                 1.48 
                 0.67 
                 0.85 
                 1.45 
                 2.32 
                 3.50 
                 1.03 
               
               
                 24 h Exposed 
                 1.35 
                 1.87 
                 0.44 
                 0.99 
                 0.52 
                 0.36 
                 0.69 
                 0.52 
               
               
                   
               
               
                 (a) All of them show adhesive failure 
               
            
           
         
       
     
     Next several combinations of tackifiers were investigated. Combination of SP-25 (phenolic type) with other class of tackifiers are shown in Table 7. Satisfactory unexposed and exposed tack values were obtained when 5 phr SP-25 in combination with 15 phr gum rosin was investigated (compound 0C031B). 
     
       
         
           
               
             
               
                 TABLE 7 
               
             
            
               
                   
               
               
                 Evaluation of several combinations of tackifiers in sealant  
               
               
                 precursor compositions based on ionic butyl 
               
               
                 (All ingredients in parts per hundred rubber (phr)) 
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                   
                 26B2 
                 26B3 
                 26B4 
                 26B5 
                 26B6 
                 26B7 
                 0C031A 
                 0C031B 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                 1 st  Mixing Step 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 (Drop 160° C.) 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Butyl Ionomer 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
               
               
                 Novares C-10 
                 23 
                 23 
                 23 
                 23 
                 23 
                 23 
                 23 
                 23 
               
               
                 Akrosperse 409 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
               
               
                 Green EPMB 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Silene 732D 
                 20 
                 20 
                 20 
                 20 
                 20 
                 20 
                 20 
                 20 
               
               
                 Calcium Carbonate 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
                 100 
               
               
                 SP-25 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
               
               
                 R40 
                 5 
                   
                   
                   
                   
                   
                   
                   
               
               
                 R98 
                   
                 5 
                   
                   
                   
                   
                   
                   
               
               
                 M130 
                   
                   
                 5 
                   
                   
                   
                   
                   
               
               
                 HXL 100 
                   
                   
                   
                 5 
                   
                   
                   
                   
               
               
                 D95 
                   
                   
                   
                   
                 5 
                   
                   
                   
               
               
                 Gum Rosin 
                   
                   
                   
                   
                   
                 5 
                 10 
                 15 
               
               
                 2 nd  Mixing Step 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 (Drop 110° C.) 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Akrochem VC-40K 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
                 5 
               
               
                 Unexposed 
                 3.71 
                 0.31 
                 2.55 
                 2.59 
                 1.82 
                 8.79 
                 3.83 
                 12.03 
               
               
                 24 h Exposed 
                 0.53 
                 0.56 
                 1.22 
                 0.64 
                 0.22 
                 0.71 
                 4.06 
                 &gt;17.78 
               
               
                   
               
               
                 (a) All of them show adhesive failure except the exposed sample with value of &gt;17.78 which showed cohesive failure 
               
            
           
         
       
     
     Sealant Properties in Commercial Tires 
     Two commercial PCR tires from two different major manufactures were purchased and inspected. One tire had exposed sealant to tire cavity thus indicating that the sealant was applied after tire cure. The second tire sealant was covered with a thin film the ends of which was overlapped and not joined together. The film had no bladder mark thus indicating that the sealant was also applied after the tire was cured. 
     
       
         
           
               
             
               
                 TABLE 8 
               
             
            
               
                   
               
               
                 Sealant Properties in Commercial Tires 
               
            
           
           
               
               
               
               
            
               
                   
                   
                 Tire # 1 
                 Tire # 2 
               
               
                   
                 Property 
                 (Continental) 
                 (Pirelli) 
               
               
                   
                   
               
            
           
           
               
               
               
               
            
               
                   
                 Mooney viscosity at 100° C. 
                 3.1 
                 14.8 
               
               
                   
                 G′ at 80° C./1 Hz/10% Strain 
                 3.7 
                 29.6 
               
               
                   
                   
               
            
           
         
       
     
     Above table confirms that Mooney viscosity is related to G′. Commercial tires are compromised. Tire #1 is expected to be better than tire #2 in colder temperature puncture due to high viscosity. Tire #2 is expected to be better than tire #1 in warmer temperature puncture due to low viscosity and it is a summer tire. 
     Following table shows that sealant of lower viscosity can be generated by using Vul-Cup® peroxide relative to same phr of Di-Cup® peroxide. 
     
       
         
           
               
             
               
                 TABLE 9 
               
             
            
               
                   
               
               
                 Peroxide concentration and type in sealant 
               
               
                 composition and G′ of sealant after heat treatment 
               
               
                 (All ingredients in parts per hundred rubber (phr)) 
               
            
           
           
               
               
               
               
            
               
                   
                 19CA594, 595 
                 19CA598 
                 19CA599 
               
               
                   
                   
               
            
           
           
               
               
               
               
            
               
                 Ionic butyl 
                 100 
                 100 
                 100 
               
            
           
           
               
               
            
               
                 Other Ingredient 
                 Same 
               
            
           
           
               
               
               
               
            
               
                 Di-Cup ® 40KE 
                 9 
                 0 
                 9 
               
               
                 Vul-Cup ® 40 KE 
                 3 
                 9 
                 0 
               
               
                 G′ at 80° C./1 Hz/10% 
                 0.18 
                 0.19 
                 0.18 
               
               
                 Strain (precursor) 
               
               
                 G′ at 80° C./1 Hz/10% 
                 0.004 
                 0.005 
                 0.011 
               
               
                 Strain (sealant) 
               
               
                   
               
               
                 Di-Cup ® 40KE is 40 weight % dicumyl peroxide in inert filler 
               
               
                 Vul-Cup ® 40KE is 40 weight % a,a′-bis(tert-butylperoxy(diisopropylbenzene in inert filler. 
               
            
           
         
       
     
     Following table shows that sealant viscosity can be reduced by increasing the concentration of peroxide in tacky sealant precursor composition (like compound 0C031B in Table 7). 
     
       
         
           
               
             
               
                 TABLE 10 
               
             
            
               
                   
               
               
                 Effect of peroxide on G′ of sealant formed in RPA 
               
               
                 (All ingredients in parts per hundred rubber (phr)) 
               
            
           
           
               
               
               
               
               
               
            
               
                 Ingredients 
                 21KB001 
                 21KB002 
                 21KB003 
                 21KB004 
                 21KB005 
               
               
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 Ionomer 
                 100 
                 100 
                 100 
                 100 
                 100 
               
               
                 Silene 732D 
                 20 
                 20 
                 20 
                 20 
                 20 
               
               
                 409 Green 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
                 0.5 
               
               
                 MB 
               
               
                 Novares C10 
                 23 
                 23 
                 23 
                 23 
                 23 
               
               
                 SP-25 
                 5 
                 5 
                 5 
                 5 
                 5 
               
               
                 Gum Rosin 
                 15 
                 15 
                 15 
                 15 
                 15 
               
               
                 CaCO3 
                 100 
                 100 
                 100 
                 100 
                 100 
               
               
                 TOTAL 
                 263.5 
                 263.5 
                 263.5 
                 263.5 
                 263.5 
               
               
                 2 nd  step 
               
               
                 mixing 
               
               
                 VC 40K 
                 0 
                 3 
                 5 
                 7 
                 9 
               
               
                 (Peroxide) 
               
            
           
           
               
            
               
                 PRECURSOR (RPA before 210° C. heat) at 80° C./1 Hz 
               
            
           
           
               
               
               
               
               
               
            
               
                 G′ (MPa) 
                 0.211 
                 0.182 
                 0.182 
                 0.177 
                 0.166 
               
            
           
           
               
            
               
                 SEALANT (RPA after 11 minutes at 
               
               
                 210° C./10% strain/1 Hz) at 80° C./1 Hz 
               
            
           
           
               
               
               
               
               
               
            
               
                 G′ (MPa) 
                 0.184 
                 0.129 
                 0.107 
                 0.089 
                 0.062 
               
               
                   
               
            
           
         
       
     
     For ease of illustration, some internal materials of the tire have been omitted from the drawings, such as belts and plies, but they remain in the finished tire. 
       FIG. 1  and the expanded view through  2 - 2  shown in  FIG. 2  illustrates the use of the present invention. It is a simplified illustration of the sealant and sealant cover layers in a cured tire  10 , where the layers are not shown to scale since it is the ordering of the layers, not the specific widths and thicknesses that is important. The width can range from full tire width, down to a small strip along the center of the tire. Sealant layers  102  and  103  formed from two precursor layers and a sealant cover layer or innerliner  104  are shown in a general form. Width of the sealant cover layer  104  is to be wider than the width of the sealant layers  102 ,  103  to cover the entire sealant. Once the tire is vulcanized, the sealants  102  and  103  form from precursor layer.  FIG. 1  also illustrates the present invention in which the sealant layers are between innerliner  104  and a layer of squeegee  108 . Squeegee layer  108  is between the innermost layer of supporting carcass  116  and the sealant layers  102 ,  103 , formed from precursor layers during tire cure. The use of a squeegee layer is known in the art and is optional and employed as needed in the process of creating the sealant layer.  FIG. 1  also shows tread  114 , carcass ply  116 , and the inextensible beads  118 , and tire sidewalls  106  which are part of the tire. 
       FIG. 2 . shows a cross-section of cured tire showing interfacial cross-linking  120  between sealant layers  102  and  103 , as well as the interfacial cross-linking  120  between the squeegee layer  108  and sealant layer  102 , and between cover layer  104  and sealant layer  103 . Such interfacial cross-linking  120  does not occur in tires where sealant is applied inside cured tire resulting in relatively poor inter-layer bonding and thus creating inferior tire. 
     It is well known that sealant is made of ionic butyl has very good barrier properties. So, it was found that it is possible to reduce the thickness of the innerliner layer underneath the sealant layer. Thus, it was found that the barrier properties from innerliner were not required, so the innerliner is not needed in this location. This will reduce tire weight, reduce material use and reduce heat generation thus prolonging tire life. 
     The foregoing embodiments of the present invention have been presented for the purposes of illustration and description. These descriptions and embodiments are not intended to be exhaustive or to limit the invention to the precise form disclosed, and obviously many modifications and variations are possible in light of the above disclosure. The embodiments were chosen and described in order to best explain the principle of the invention and its practical applications to thereby enable others skilled in the art to best utilize the invention in its various embodiments and with various modifications as are suited to the particular use contemplated.