Patent Publication Number: US-2007123648-A1

Title: Method for preparing rubber-reinforced thermoplastic resin, and rubber-reinforced thermoplastic resin composition using the same

Description:
TECHNICAL FIELD  
      The present invention relates to a method for preparing a rubber-reinforced thermoplastic resin, a rubber-reinforced thermoplastic resin prepared by the same method, and a rubber-reinforced thermoplastic resin composition using the same, wherein the rubber-reinforced thermoplastic resin has excellent heat-sealability and thermal stability maintaining good mechanical properties.  
     BACKGROUND ART  
      The acrylonitrile-butadiene-styrene resin with rubber component added to improve the impact resistance of acrylonitrile-styrene copolymer, which has good dimensional stability, processability, and chemical resistance, is widely used as materials for monitor housings, game-machine housings, home appliances, office machines, automobile-lamp housings, etc.  
      In order to disperse the rubber component in acrylonitrile-styrene copolymer in the preparation of acrylonitrile-butadiene-styrene resin, either solution polymerization is done with a rubber component dissolved in acrylonitrile and styrene as monomers, and a solvent, or graft copolymerization is done with acrylonitrile and styrene on the rubber latex prepared by emulsion polymerization.  
      The impact resistance, chemical resistance, gloss, processability, heat-sealability, thermal stability, etc. of rubber-reinforced thermoplastic resins prepared by emulsion polymerization show big difference depending on rubber morphology, gel content, and molecular weight, graft ratio, and monomer composition of copolymer grafted on rubber latex.  
      The most of rubber-reinforced thermoplastic resins currently employed do not have good heat-sealability, while their impact resistance, chemical resistance, gloss, and processability have been improved.  
      The heat-sealability is the property required to make a final form of product by heating the sections of molded parts and joining them together. It requires clean surfaces of the joining sections.  
      In order to have good impact resistance, chemical resistance, gloss, mechanical properties such as processability, etc. of rubber-reinforced thermoplastic resins, technologies are disclosed with regard to various rubber morphology and gel content.  
      In general, the rubber-reinforced thermoplastic resins are prepared by blendng a graft copolymer prepared by copolymerization of one or more monomers on an emulsion-polymerized rubber latex, and a styrenic copolymer prepared by bulk polymerization or solution polymerization. Various kinds of the styrenic copolymer prepared by bulk polymerization or solution polymerization herein have been produced with diverse monomer compositions and molecular weights depending on the characteristics of the rubber-reinforced thermoplastic resin as a final product. Particularly their monomer composition has such a wide range of acrylonitrile content as from 22 to 34 weight %.  
      In Korea Laid-open Publication Patent Nos. 2002-7010992 and 2002-7010993, the monomer composition of the copolymer grafted to rubber latex has the acrylonitrile to styrene ratio of 27/73 by weight. This monomer composition ratio is the one to have effective blending of a graft copolymer prepared by emulsion polymerization and various styrenic copolymers prepared by bulk polymerization or solution polymerization.  
      The said Korea Laid-open Publication Patent No. 2002-7010992 (International Application No. PCT/EP2001/01494) discloses the use of a mixture comprising a rubber latex having average particle diameter of 0.15 to 0.22 μm and gel content of 50 to 85 weight % and a rubber latex having average particle diameter of 0.26 to 0.34 μm and gel content of 45 to 70 weight %.  
      Likewise, the said Korea Laid-open Publication Patent No. 2002-7010993 (International Application No. PCT/EP2001/01493) discloses the use of the mixture comprising a rubber latex having average particle diameter of 0.25 to 0.31 μm and gel content of 45 to 70 weight % and a rubber latex having average particle diameter of 0.36 to 0.46 μm and gel content of 60 to 85 weight %.  
      However, the said disclosed inventions are related only to good impact resistance, processability and gloss, and they do not refer to heat-sealability.  
      The present inventors studied assiduously to solve the said problems of prior arts and completed the present invention by discovering that heat-sealability and thermal stability can be improved without deteriorating the impact resistance, chemical resistance, gloss, mechanical properties such as processability, etc. of rubber-reinforced thermoplastic resin composition, on the basis of 100 weight parts of total monomer used to prepare graft copolymer, by using the mixture comprising 10 to 30 weight parts of a rubber latex having average particle diameter of 0.08 to 0.16 μm and gel content of 65 to 95 weight % and 15 to 45 weight parts of a rubber latex having average particle diameter of 0.26 to 0.34 μm and gel content of 55 to 85 weight %, keeping the weight ratio of vinyl cyanide compound including acrylonitrile to aromatic vinyl compound including styrene from 16/84 to 24/76 as a monomer composition grafted on rubber latex, and adjusting the graft ratio of graft copolymer, i.e. rubber-reinforced thermoplastic resin, from 25 to 65. 
    
    
     DISCLOSURE OF THE INVENTION  
      The purpose of the present invention is to provide a method for preparing a rubber-reinforced thermoplastic resin, a rubber-reinforced thermoplastic resin thereby, and a rubber-reinforced thermoplastic resin composition using the same, wherein the rubber-reinforced thermoplastic resin has excellent heat-sealability and thermal stability maintaining good impact resistance, chemical resistance, gloss, and mechanical properties such as processability.  
      More specifically, a method for preparing the rubber-reinforced thermoplastic resin of the present invention is characterized in that it comprises,  
      on the basis of 100 weight parts of total monomer used to prepare graft copolymer, 
          a) the stage of charging 45 to 65 weight parts of the mixture into a polymerization reactor, comprising 10 to 30 weight parts of a rubber latex having average particle diameter of 0.08 to 0.16 μm and gel content of 65 to 95 weight % and 15 to 45 weight parts of a rubber latex having average particle diameter of 0.26 to 0.34 μm and gel content of 55 to 85 weight %, 5 to 15 weight parts of aromatic vinyl compound, 1 to 6 weight parts of vinyl cyanide compound, 0.3 to 0.8 weight part of emulsifier, 100 to 150 weight parts of deionized water, and 0.1 to 1.0 weight part of molecular weight control agent, raising the temperature of the polymerization reactor up to 40 to 50° C., starting the polymerization reaction by charging peroxide initiator and activator, and slowly raising the temperature of the polymerization reactor up to 60 to 70° C.;     b) the stage, after 30 to 60 minutes since the beginning of the polymerization and when the monomer conversion of the polymerization reaction at the stage a) reaches 70 to 90%, of charging the monomer emulsion comprising 20 to 30 weight parts of aromatic vinyl compound, 5 to 10 weight parts of vinyl cyanide compound, 0.5 to 1.5 weight part of emulsifier, and 20 to 30 weight parts of deionized water, and peroxide initiator into the reactant from said stage a) for 1 to 3 hours continuously, and maintaining the temperature of the polymerization reactor at the range from 70 to 80° C.; and     c) the stage, after completing the charging of the monomer emulsion and peroxide initiator at said stage b), of charging again peroxide initiator and activator at once and polymerizing it at 70 to 80° C. for 1 to 2 hours, wherein the monomer conversion is 99% or more, and the weight ratio of vinyl cyanide compound to aromatic vinyl compound at said stages a) and b) is from 16/84 to 24/76, and the graft ratio of copolymer grafted on the rubber latex is from 25 to 65 parts.        

      Hereinafter, the preparation method according to the present invention will be further described.  
      Though the preparation method of the present invention employs two kinds of rubber latex as Korea Laid-open Publication Patent Nos. 2002-7010992 and 2002-7010993, the present invention uses 45 to 65 weight parts of the mixture comprising 10 to 30 weight parts of a rubber latex having average particle diameter of 0.08 to 0.16 μm and gel content of 65 to 95 weight % and 15 to 45 weight parts of a rubber latex having average particle diameter of 0.26 to 0.34 μm and gel content of 55 to 85 weight %, to improve the heat-sealability without deteriorating the impact resistance, chemical resistance, gloss, mechanical properties such as processability, etc.  
      If less than 10 weight parts of the rubber latex having average particle diameter of 0.08 to 0.16 μm and gel content of 65 to 95 weight % are used, the gloss and heat-sealability are getting worse. If greater than 30 weight parts are used, the impact resistance, processability and thermal stability are getting worse.  
      Unlike said disclosed inventions, the preparation method according to the present invention improved the heat-sealability of the final product, rubber-reinforced thermoplastic resin composition, by keeping the weight ratio of vinyl cyanide compound to aromatic vinyl compound as the monomer composition grafted on rubber latex to be from 16/84 to 24/76.  
      If the weight ratio of vinyl cyanide compound in the monomer composition of the copolymer grafted on rubber latex is lower than said range, the gloss and heat-sealability of the final product, rubber-reinforced thermoplastic resin composition, are drastically getting worse. If it is higher than said range, the heat-sealability is getting worse.  
      Furthermore, the heat-sealability and thermal stability are improved in this invention maintaining the good impact resistance, chemical resistance, gloss, and processability by adjusting the graft ratio of graft copolymer to be from 25 to 65. If the graft ratio is lower than 25, the gloss and thermal stability of the final product, rubber-reinforced thermoplastic resin composition, are getting worse. If the graft ratio is higher than 65, the heat-sealability is getting worse.  
      The aromatic vinyl compound that can be used at said stages a) and b) may be one or more compounds selected from the group consisting of styrene, alpha-methylstyrene, alpha-ethylstyrene, and para-methylstyrene, and particularly styrene is preferable.  
      The vinyl cyanide compound that can be used at said stages a) and b) may be one or more compounds selected from the group consisting of acrylonitrile, methacrylonitrile, and ethacrylonitrile, and particularly acrylonitrile is preferable.  
      A third monomer may be used in addition to the aromatic vinyl compound and vinyl cyanide compound at said stages a) and b). The third monomer may be vinyl monomer in small amount such as maleimide, N-methylmaleimide, N-ethylmaleimide, N-propylmaleimide, N-phenylmaleimide, methyl methacrylate, methyl acrylate, butyl acrylate, acrylic acid, maleic anhydride, and a mixture thereof.  
      The peroxide initiator that can be used at said stages a), b) and c) may be an organic peroxide such as tertiary-butylhydroperoxide, cumene hydroperoxide, diisopropylbenzene hydroperoxide, etc., or an inorganic peroxide such as potassium persulfate salt, sodium persulfate salt, etc. It can be used as a single compound or a mixture thereof.  
      The total usage of said peroxide initiator may be 0.05 to 0.5 weight part. In the total usage of said peroxide initiator, 30 to 50 weight % may be used at said stage a), 30 to 50 weight % at said stage b), and 10 to 20 weight % at said stage c).  
      The activator at said stages a) and c) may be one or more compounds selected from the group consisting of sodium formaldehydesulfoxylate, sodium ethylenediaminetetraacetate, ferrous sulfate, dextrose, sodium pyrophospate, and sodium sulfite.  
      The said activator may include 0.03 to 0.3 weight part of dextrose, 0.03 to 0.3 weight part of sodium pyrophospate, and 0.001 to 0.01 weight part of sodium sulfite. In the total usage of said activator, 60 to 80 weight % may be used at said stage a) and 20 to 40 weight % at said stage c).  
      The said emulsifier may be a single compound or a mixture of compounds selected from the group consisting of alkylaryl sulfonate, alkalimetal alkylsulfate, sulfonated alkylester, fatty acid soap, and alkali salt of rosin acid.  
      Mercaptans are frequently used as a molecular weight control agent and tertiary-dodecyl mercaptan is preferable. The usage of the molecular weight control agent may be 0.1 to 1.0 weight part.  
      The powder form of rubber-reinforced thermoplastic resin may be obtained by coagulating, washing, dehydrating and drying the latex polymerized by the method of the present invention with a widely-known coagulant such as sulfuric acid, MgSO 4 , CaCl 2 , Al 2 (SO 4 ) 3 , etc.  
      The present invention also provides the rubber-reinforced thermoplastic resin composition, on the basis of 100 weight parts of rubber-reinforced thermoplastic resin composition, comprising a) 20 to 80 weight parts of the rubber-reinforced thermoplastic resin prepared by the method of the present invention, and b) 20 to 80 weight parts of the styrenic copolymer of weight-average molecular weight of 80,000 to 200,000.  
      The said styrenic copolymer may be prepared by bulk polymerization or solution polymerization, and the weight ratio of vinyl cyanide compound in the monomer composition is preferably from 20 to 35.  
      Specifically the styrenic copolymer in said stage b) may be acrylonitrile-styrene copolymer having acrylonitrile content of 20 to 35 weight %, acrylonitrile-styrene-alpha-methylstyrene terpolymer having acrylonitrile content of 20 to 35 weight %, alpha-methylstyrene content of 60 to 70 weight %, and styrene content of 1 to 10 weight %, or a mixture thereof.  
      The said rubber-reinforced thermoplastic resin composition may additionally include one or more as additives selected from the group consisting of light-stabilizer, lubricator, UV-absorber, plasticizer, colorant, flame retardant, reinforcing agent, compatibilizer, foaming agent, wood powder, filler, metal powder, bactericide, fungicide, silicone oil, and coupling agent.  
     MODES FOR CARRYING OUT THE INVENTION  
      Hereinafter, the present invention will be further described in the following examples, but the scope of the present invention is not limited to these examples.  
      &lt;Preparation of Rubber-Reinforced Thermoplastic Resin&gt; 
     EXAMPLE 1  
      Into a polymerization reactor installed with a heating equipment were charged 20 weight parts of a rubber latex having average particle diameter of 0.095 μm and gel content of 83 weight %, 35 weight parts of a rubber latex having average particle diameter of 0.31 μm and gel content of 75 weight %, 120 weight parts of deionized water, 3.0 weight parts of acrylonitrile, 12 weight parts of styrene, 0.5 weight part of potassium rosinate, and 0.1 weight part of tertiary-dodecyl mercaptan. The temperature of the reactor was then raised.  
      When the internal temperature of the reactor reached at 45° C., the polymerization reaction was started by charging 0.1 weight part of tertiary-butyl hydroperoxide and 0.25 weight part of an activator comprising dextrose, sodium pyrophospate, and ferrous sulfate in the ratio of 50/40/1.The temperature of the reactor was then increased to 70° C. in 60 minutes. The polymerization conversion herein was 73%. (Stage a)  
      In a separate mixing equipment, an emulsion was prepared by mixing 6 weight parts of acrylonitrile, 24 weight parts of styrene, 25 weight parts of deionized water, and 1.2 weight part of potassium rosinate. This monomer emulsion was continuously charged into the reactor for approximately 2 hours. Separately 0.15 weight part of tertiary-butyl hydroperoxide was continuously charged into the reactor for approximately 2 hours. The polymerization temperature herein was kept to 70° C. (Stage b)  
      After completing the monomer emulsion charging, 0.12 weight part of an activator comprising dextrose, sodium pyrophospate, and ferrous sulfate in the ratio of 50/40/1, and 0.05 weight part of tertiary-butyl hydroperoxide were charged into the reactor at once. The temperature of the reactor was then raised to 80° C. in an hour and the reaction was terminated. The polymerization conversion herein was 99%. (Stage c)  
      To the completely reacted latex was charged 0.7 weight part of IR-1076 (a hindered phenol-type antioxidant manufactured by Ciba). The rubber-reinforced thermoplastic resin in powder form was obtained by coagulating with 10% sulfuric acid solution, washing and drying.  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 48.  
      In order to measure the graft ratio, the styrenic copolymer not grafted to rubber component was dissolved by mixing 2 g of rubber-reinforced thermoplastic resin in powder form in 100 In of acetone for 24 hours with stirring. The sol and gel were then separated by ultracentrifuge. The graft ratio was calculated by the following equation: 
 
Graft Ratio=[(Gel Weight−Rubber Weight)/(Rubber Weight)]×100 
 
     EXAMPLE 2  
      Into a polymerization reactor installed with a heating equipment were charged 20 weight parts of a rubber latex having average particle diameter of 0.12 μm and gel content of 89 weight %, 40 weight parts of a rubber latex having average particle diameter of 0.30 μm and gel content of 74 weight %, 120 weight parts of deionized water, 3.5 weight parts of acrylonitrile, 11.5 weight parts of styrene, 0.5 weight part of potassium rosinate, and 0.1 weight part of tertiary-dodecyl mercaptan. The temperature of the reactor was then raised.  
      When the internal temperature of the reactor reached at 45° C., the polymerization reaction was started by charging 0.1 weight part of tertiary-butyl hydroperoxide and 0.25 weight part of an activator comprising dextrose, sodium pyrophospate, and ferrous sulfate in the ratio of 50/40/1.The temperature of the reactor was then raised to 70° C. in 60 minutes. The polymerization conversion herein was 73%. (Stage a)  
      In a separate mixing equipment, an emulsion was prepared by mixing 7.2 weight parts of acrylonitrile, 22.8 weight parts of styrene, 25 weight parts of deionized water, and 1.2 weight part of potassium rosinate. This monomer emulsion was continuously charged into the reactor for approximately 2 hours. Separately 0.15 weight part of cumene hydroperoxide was continuously charged into the reactor for approximately 2 hours. The polymerization temperature herein was kept to 70° C. (Stage b)  
      Hereinafter, Stage c and the coagulation, washing and drying process was the same as in Example 1.  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 46.  
     EXAMPLE 3  
      The rubber-reinforced thermoplastic resin was prepared in the same manner as in Example 1 except that cumene hydroperoxide was used as a peroxide initiator in Stage b).  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 56.  
     EXAMPLE 4  
      The rubber-reinforced thermoplastic resin was prepared by the same manner as in Example 1 except that diisopropylbenzene hydroperoxide was used as a peroxide initiator in Stage b).  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 63.  
     EXAMPLE 5  
      The rubber-reinforced thermoplastic resin was prepared in the same manner as in Example 1 except that an emulsion prepared separately was continuously charged into the reactor for 90 minutes, and, separately, cumene hydroperoxide instead of tertiary-butyl hydroperoxide was continuously charged for 90 minutes, and the polymerization temperature herein was slowly raised to 75° C. in Stage b).  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 51.  
     COMPARATIVE EXAMPLE 1  
      The rubber-reinforced thermoplastic resin was prepared in the same manner as in Example 1 except that 5 weight parts of a rubber latex having average particle diameter of 0.095 μm and gel content of 83 weight % and 50 weight parts of a rubber latex having average particle diameter of 0.31 μm and gel content of 75 weight % were employed in Stage a).  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 32.  
     COMPARATIVE EXAMPLE 2  
      The rubber-reinforced thermoplastic resin was prepared in the same manner as in Example 1 except that 35 weight parts of a rubber latex having average particle diameter of 0.095 μm and gel content of 83 weight % and 20 weight parts of a rubber latex having average particle diameter of 0.31 μm and gel content of 75 weight % were employed in Stage a).  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 67.  
     COMPARATIVE EXAMPLE 3  
      The rubber-reinforced thermoplastic resin was prepared in the same manner as in Example 1 except that 4.2 weight parts of acrylonitrile and 10.8 weight parts of styrene were used in Stage a) and 8.4 weight parts of acrylonitrile and 21.6 weight parts of styrene were used in Stage b).  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 52.  
     COMPARATIVE EXAMPLE 4  
      The rubber-reinforced thermoplastic resin was prepared in the same manner as in Example 1 except that 2.1 weight parts of acrylonitrile and 12.9 weight parts of styrene were used in Stage a) and 4.2 weight parts of acrylonitrile and 25.8 weight parts of styrene were used in Stage b).  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 52.  
     COMPARITIVE EXAMPLE 5  
      The rubber-reinforced thermoplastic resin was prepared in the same manner as in Example 1 except that potassium persulfate salt was used as a peroxide initiator in every stage.  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 24.  
     COMPARATIVE EXAMPLE 6  
      The rubber-reinforced thermoplastic resin was prepared in the same manner as in Example 1 except that an emulsion prepared separately was continuously charged into the reactor for 3 hours in Stage b), and, separately, diisopropylbenzene hydroperoxide was continuously charged for 3 hours, and the polymerization temperature herein was slowly raised to 75° C.  
      The graft ratio of the rubber-reinforced thermoplastic resin thus obtained was 68.  
      &lt;Preparation of Styrenic Copolymer&gt; 
      Styrenic Copolymer Resin 1  
      A stryrene-acrylonitrile copolymer having a styrene to acrylonitrile weight ratio of 72/28 and a weight-average molecular weight of 110,000 was prepared by solution polymerization.  
      Styrenic Copolymer Resin 2  
      A stryrene-alpha-methylstyrene-acrylonitrile terpolymer having a styrene to alpha-methylstyrene to acrylonitrile weight ratio of 5/67/28 and a weight-average molecular weight of 120,000 was prepared by solution polymerization.  
      &lt;Preparation of Rubber-Reinforced Thermoplastic Resin Composition&gt; 
      The said polymer composition was blended and pelletized according to the ratio given in Table 1. Mechanical properties, thermal stability and heat-sealability were measured with test specimens prepared thereby. The test results are shown in Table 2.  
      Test Methods  
      (1) IZOD impact strength  
      IZOD impact strength was measured in accordance with ASTM D256.The thickness of test specimen was ¼ inch.  
      (2) Melt Flow Rate  
      Melt Flow Rate was measured in accordance with ASTM D1238 under the measuring condition of 220° C. and 10 Kg load.  
      (3) Surface Gloss  
      Surface Gloss was measured in accordance with ASTM D528 under 45 degree angle.  
      (4) Heat-Sealability  
      Heat-sealability was expressed in mm unit by the length of resin remained at the contacting surface of specimen and glass plate when the surface gloss specimen was pressed to the glass plate at 350° C. by 10 Kg load for 10 seconds, followed by separating them by the speed of 5 cm/minute.  
      (5) Thermal Stability  
      The decrease ratio of surface gloss was measured when a resin was extruded after staying for 15 minutes in the screw of the extruder set at 270° C. The less the decrease ratio of surface gloss is, the better the thermal stability 10 of the product is.  
                                                                   TABLE 1                       Compo-                                                           sition   E. 6   E. 7   E. 8   E. 9   E. 10   C. 7   C. 8   C. 9   C. 10   C. 11   C. 12   E. 11   E. 12                                                                                            RR   E. 1   30   —   —   —   —   —   —   —   —   —   —   25   —       TR   E. 2   —   30   —   —   —   —   —   —   —   —   —   —   25           E. 3   —   —   30   —   —   —   —   —   —   —   —   —   —           E. 4   —   —   —   30   —   —   —   —   —   —   —   —   —           E. 5   —   —   —   —   30   —   —   —   —   —   —   —   —           C. 1   —   —   —   —   —   30   —   —   —   —   —   —   —           C. 2   —   —   —   —   —   —   30   —   —   —   —   —   —           C. 3   —   —   —   —   —   —   —   30   —   —   —   —   —           C. 4   —   —   —   —   —   —   —   —   30   —   —   —   —           C. 5   —   —   —   —   —   —   —   —   —   30   —   —   —           C. 6   —   —   —   —   —   —   —   —   —   —   30   —   —       SR   1   70   70   70   70   70   70   70   70   70   70   70   —   —           2   —   —   —   —   —   —   —   —   —   —   —   75   75                 E.: Example,            C.: Comparative Example,            RRTR: Rubber-Reinforced Thermoplstic Resin,            SR: Styrenic Resin             
 
     
       
         
           
               
               
               
               
               
               
             
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                   
               
               
                   
                 Impact 
                 Melt Flow 
                 Surface 
                 Heat- 
                 Thermal 
               
               
                   
                 Strength 
                 Rate 
                 Gloss 
                 Sealability 
                 Stability 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 E. 6 
                 22 
                 15 
                 95 
                 0.0 
                 10 
               
               
                 E. 7 
                 23 
                 15 
                 95 
                 0.0 
                 10 
               
               
                 E. 8 
                 24 
                 16 
                 96 
                 0.2 
                 8 
               
               
                 E. 9 
                 25 
                 17 
                 97 
                 0.2 
                 8 
               
               
                 E. 10 
                 22 
                 15 
                 95 
                 0.0 
                 10 
               
               
                 C. 7 
                 19 
                 13 
                 85 
                 2.0 
                 5 
               
               
                 C. 8 
                 14 
                 18 
                 98 
                 0.0 
                 50 
               
               
                 C. 9 
                 23 
                 17 
                 97 
                 1.5 
                 10 
               
               
                 C. 10 
                 19 
                 13 
                 82 
                 0.0 
                 30 
               
               
                 C. 11 
                 10 
                 8 
                 60 
                 0.0 
                 15 
               
               
                 C. 12 
                 24 
                 18 
                 98 
                 1.5 
                 8 
               
               
                 E. 11 
                 17 
                 12 
                 99 
                 0.0 
                 10 
               
               
                 E. 12 
                 18 
                 13 
                 99 
                 0.0 
                 10 
               
               
                   
               
               
                   E.: Example,    
               
               
                   C.: Comparative Example    
               
            
           
         
       
     
     INDUSTRIAL APPLICABILITY  
      As apparent from the test data of rubber-reinforced thermoplastic resin composition given in the above Table 2, the heat-sealability and thermal stability of rubber-reinforced thermoplastic resin composition according to the present invention can be improved maintaining good impact resistance, processability and surface gloss.  
      While the present invention has been particularly shown and described with reference to the exemplary embodiments thereof, it is apparent to those of ordinary skill in the art that various modifications and revisions therein are possible without departing from the spirit and scope of the present invention. It is also apparent that these modifications and revisions are included within the boundary of the following claims.