Patent Publication Number: US-2019177646-A1

Title: Sliding element for an engine comprising surface treated metal particulate

Description:
CROSS-REFERENCE TO RELATED APPLICATION 
     This application claims priority to Great Britain Application No. GB 1720441.3, filed on Dec. 7, 2017, the contents of which are hereby incorporated by reference in its entirety. 
     TECHNICAL FIELD 
     The present invention relates to sliding engine components having a polymer-based bearing “overlay” layer, and in particular to sliding engine components having a polymer-based bearing “overlay” layer which comprises surface treated metallic particulate. 
     Such sliding engine components may include bearing lining shells, bushes, bearing surfaces of crankshafts, bearing surfaces of camshafts, bearing surfaces of connecting rods, thrust washers, bearing surfaces of a bearing block, bearing surfaces of a bearing cap, and piston assembly components such as piston rings, piston skirts, and cylinder walls and cylinder liners. 
     BACKGROUND 
     In internal combustion engines, the bearing assemblies typically each comprise a pair of half bearings retaining a crankshaft that is rotatable about an axis. Each half bearing is a hollow generally semi-cylindrical bearing shell, and typically at least one is a flange half bearing, in which the bearing shell is provided with a generally semi-annular thrust washer extending outwardly (radially) at each axial end. In other bearing assemblies it is also known to use an annular or circular thrust washer. 
     The bearing surfaces of sliding bearings generally have a layered construction, in which a strong backing material is coated with one or more layers having preferred tribological properties, which provide the bearing surface that faces the cooperating moving part, in use. In known half bearings and thrust washers: the strong backing material may be steel, having a thickness of about 1 mm or more; the bearings surface is coated with a layer (the “overlay”) of 6 μm to 25 μm of a plastic polymer-based composite layer; and optionally at least one intervening layer (a “lining layer”) may be provided between the backing and the overlay layer, such as an aluminium-based material (e.g. aluminium-tin alloy) or a copper-based material (e.g. copper-tin bronze), adhered to the backing, and the thickness of the optional lining layer is generally in the range from about 0.1 mm to 0.5 mm (e.g. 300 μm of aluminium-tin alloy). 
     It is known in the field to use composite plastic polymer-based overlay layers on a steel backing, in which the overlay comprises a matrix of a polymer material, having distributed throughout the matrix mechanical performance enhancing additives, such as metal particles to improve wear resistance, silane compounds to improve adhesion to the underlying substrate, and dry lubricant particulate to enhance lubrication in the event of contact between the bearing surface and the cooperating moving part. The metal particles may be a silvery-coloured metal powder (e.g. aluminium), copper-coloured metal powder (e.g. copper). The metal particles may impart conformability and improve heat distribution throughout the overlay. Alternatively to the metal particles, or additionally, the wear resistance may be improved by the addition of other hard-wearing particulate. This typically results in a cured polymer matrix which is the same or similar in appearance to the steel backing 
     It is also known to add coloured pigment to the polymer-based matrix in order to colour the polymer-based overlay layer. The colour of the pigment may be chosen to provide the polymer-based overlay layer with a colour that is different to the colour of the underlying substrate. This allows the presence of the polymer-based overlay layer to be readily determined simply by looking at the bearing surface and observing the colour. 
     For example, WO 2015/024898 A2 describes a plastic polymer-based composite material for use as an overlay layer on a steel backing, in which the overlay comprises a matrix of a polyamide/imide-based polymer, having distributed throughout the matrix: from 10 to 15% vol pigment; from 1 to less than 15% vol of a metal particulate (e.g. metal powder and/or metal flakes); from 1 to 15% vol of a fluoropolymer, the balance being polyamide/imide resin apart from incidental impurities; and 3 to 6% vol of silane compound. For example, the polymer-based ovelayer may comprise 12.5% vol Al, 5.7% vol PTFE particulate, 4.8% vol silane, &lt;0.1% vol other components, and balance polyamide/imide, apart from incidental impurities. 
     However, while the coloured pigment imparts a chosen colour to the polymer-based matrix, it does not enhance any of the mechanical properties of the polymer-based overlay layer. In other words, the use of a coloured pigment introduces a quantity of non-functionality to the polymer-based matrix. Further, it has been found that the addition coloured pigment in the levels required to provide a polymer-based overlay layer with a colour that is different to the colour of the underlying substrate can compromise the structural integrity, the wear resistance, the fatigue properties, and the seizure resistance of the polymer matrix. It may also adversely affect the hardness and/or strength of the polymer matrix. By contrast, the use of coloured pigment in low levels does not alter the colour of the polymer-based matrix sufficiently for it to be distinguished from the underlying substrate. The range of colours and colour intensities is therefore limited when adding coloured pigments to colour polymer-based overlays. 
     There is therefore a need to provide a means for controlling the colour of a polymer-based overlay to a greater degree without compromising the mechanical properties of the overlay. 
     SUMMARY 
     According to a first aspect of the present invention, there is provided a sliding engine element having a polymer-based overlay layer on a metallic substrate, the polymer-based overlay layer comprising a polymer-based matrix and a metal particulate. The metal particulate is surface treated. 
     As used herein, the term “surface treated” or “surface functionalised” means that a surface of the metal particulate is somehow changed. The surface treatment may, for example, involve the addition of material to or the removal of material from to a surface of the metal particulate (e.g. applying a coating). The surface treatment may alternatively be the result of a chemical reaction (e.g. controlled oxidation) or a physical process (for example heat treatment) occurring at the surface of the metal particulate. 
     The skilled person will understand that the polymer-based overlay layer may not necessarily be in direct contact with the surface of the metallic substrate since, as discussed below, the sliding engine element may further comprise an intermediate layer or layers between the metallic substrate and the polymer-based overlay layer. 
     It has been observed that the surface treatment methods described below do not significantly alter the size or geometry of the metal particulate and the methods are also advantageously not expected to compromise the mechanical properties of the metal particulate. 
     Without wishing to be bound by theory, it is also expected that the surface treated metal particulate will advantageously have improved storage and sheer stability, improved resistance to weathering, and exhibit a lower tendency to agglomerate in the coating compared to equivalent metal particulate which has not been surface treated. 
     The addition of the surface treated metal particulate may avoid the requirement to apply identifying features to the surface of the component by a stamping process or through an additional printing or etching process, which would require additional manufacturing steps and may interfere with the operation of the component. For example, in the case of a bearing shell, an identification mark stamped into the outer surface risks bruising the inner surface, which is configured to cooperate with a rotating journal with very small tolerances. Similarly, printing or etching an identification mark onto the outside of a bearing shell may affect the way in which the bearing shell sits within its housing, in use, thereby affecting performance. 
     The metallic substrate is preferably from a strong metal to give the bearing element greater structural rigidity. Suitable metallic substrate materials include: steel, aluminium, bronze, brass, bismuth, copper, nickel, tin, zinc, silver, gold and iron, or alloys of such materials. The substrate may comprise a combination of two or more such materials or alloys. Particularly suitable substrate materials for bearing elements embodying the present invention include steel, iron, aluminium, copper alloy, bronze, and brass alloys. 
     The sliding engine element may further include an intermediate layer or bearing lining layer which may provide an improved surface for adhesion of the polymer-based overlay layer when certain metallic substrate materials are used. Suitable materials for the optional intermediate layer include aluminium, tin, nickel, silver, copper and/or iron or alloys comprising one or more of such materials. The optional intermediate layer may comprise a combination of two or more or such materials/alloys. The intermediate layer may also include an adhesion promoter and/or be subjected to a pre-treatment, for example a phosphating, chromating or silicating treatment. 
     The polymer-based matrix comprises a polymeric material. Examples of suitable polymeric materials include or may comprise: cross-linkable bonding agents; thermosetting plastics; high melting point thermoplastics; materials having a matrix of at least one high melting point thermoplastic material; fibre-reinforced plastics; any combination of these materials. Other suitable materials are envisaged and will be readily apparent to the skilled person. Particularly suitable polymeric materials include: PAI (polyamide imide); PI (polyimide); epoxy; epoxy resin; acrylate resin; polyurethane, fluoropolymer, polyetheretherketone, formaldehyde resin, PBI (Polybenzimideazole); phenolic resin; silicone resin; or a combination of any of these materials. These materials are characterised by high temperature resistance and excellent media resistance (such as chemical resistance to lubricants). One particularly preferred polymeric material for bearing elements embodying the present invention is polyamide imide (PAI). 
     In addition to the metal particulate, the polymer-based overlay layer may comprise hard particles dispersed throughout the polymer-based matrix. Suitable hard particles include: nitrides; carbides; borides; and oxides. Other suitable materials are envisaged and will be readily apparent to the skilled person. The provision of hard particles improves the wear resistance properties of the polymer-based overlay layer. 
     As described above, in polymer-based overlay layers of the prior art, metal particulate is typically added to the plastic polymer-based matrix solution as a dry powder. However, it has been found that where the metal particulate is a surface treated metal particulate, it is advantageous to add it to the plastic polymer-based matrix solution as a slurry. It has been found that the addition of the surface treated metal particulate as a slurry advantageously leads to a better distribution of the metal particulate resulting in better colour dispersion throughout the polymer-based matrix. 
     The polymer-based overlay layer is deposited as a mixture of a plastic polymer-based matrix material and suspended material, and may further comprise solvent, which may facilitate forming the mixture. Suitable solvents may be non-polar (e.g. xylene, toluene), polar aprotic (e.g. acetone, n-ethyl-2-pyrrolidone {NEP}, n-methyl-2-pyrrolidone {NMP}, gamma-butyrolactone, dipropylene glycol dimethyl ether) or polar protic (e.g. water, alcohol, glycol). The solvent can be employed in various proportions in order to achieve a particular desired viscosity of mixture for coating onto the substrate. 
     The polymer-based overlay layer may also comprise silane material. Silane materials have been found to promote stability of the polyamide/imide matrix and have also been found to promote adhesion of the polyamide/imide resin material to the substrate. A suitable silane material may be gamma-aminopropyltriethoxysilane (e.g. 3-aminopropyltriethoxysilane). A suitable alternative silane material may comprise bis-(gamma-trimethoxysilpropyl)amine. 
     The polymer-based overlay layer may further comprise from 1 to 20 wt % of a dry lubricant particulate, and a preferred range of 8 to 12 wt %. A dry lubricant particulate may be included in the overlay layer for its beneficial effect on material frictional properties and its self-lubricating effect. Suitable dry lubricant particulates include fluoropolymer, molybdenum disulfide (MoS 2 ), tungsten disulphide (WS 2 ), hexagonal boron nitride (h-BN), metal sulphides with layered structures, and graphite, or a combination of any of these materials. The fluoropolymer particulate addition may preferably be constituted by polytetrafluoroethylene (PTFE), as this is the most effective of the fluoropolymers in terms of reducing the friction coefficient and improving the self-lubricating properties of the polymer-based overlay layer. However, other suitable fluoropolymers, such as fluorinated ethylene-propylene (FEP), may be used if desired. Other suitable materials are envisaged and will be readily apparent to the skilled person. 
     Below 1 wt % of the dry lubricant particulate, the improvement in wear resistance and tribological properties is not significant. Above 20 wt % of the dry lubricant particulate, the structural integrity of the polymer-based overlay layer may be compromised. Particle size of the dry lubricant particulate desirably lies in the range from 1 μm to 5 μm, and a size range of 2 μm to 4 μm is preferred. 
     The polymer-based overlay layer may further comprise other components such as leveller. Where a leveller is present, it is present in an amount of less than 1 wt %, preferably less than 0.5 wt %. For example, the polymer-based overlay layer may comprise about 0.1 wt % leveller. The leveller is a surface coating additive designed to improve wetting of the polymer-based matrix on the metal substrate when the polymer-based matrix is applied to the substrate. Improved wetting advantageously results in a polymer-based overlay layer having a more even thickness. 
     Preferably, the surface treated metal particulate imparts a colour to the polymer-based overlay layer. 
     As used herein, the term “imparts a colour” means that the colour of the polymer-based overlay layer is substantially determined by the addition of the surface treated metal particulate. 
     Preferably, the colour of the polymer-based overlay is different from a colour of the metallic substrate. 
     The surface treatment of the metal particulate is selected such that it imparts a colour to the polymer-based overlay layer. 
     The provision of surface treated metal particulate material to impart colour to polymer-based overlay layers is advantageous since it removes the need for the addition of separate pigments which can compromise the mechanical properties of the overlay layer. The colour may be detectable by a machine or a human. 
     The provision of a surface treated metal particulate which provides the polymer-based overlay layer with a colour enables enhanced reliability during manufacturing, by facilitating a visual distinction between sliding engine components that have and have not been coated with a composite polymer-based overlay layer, and to distinguish between sliding engine components having different coatings. This facilitates distinguishing between sliding engine components of different colours in an automated quality control process. This can help prevent miss-assembly during manufacture. The colours caused by the surface treated metal particulate may be identifiable by machines such as assembly robots and may therefore assist with automated manufacture of automotive components 
     Preferably the colour is visually discernible from the colour of the metallic substrate. 
     This is advantageous where the polymer-based overlay layer might otherwise match or be similar to the colour of the metallic substrate (e.g. an otherwise silver-coloured layer on a silver-coloured substrate). Furthermore, since the colour of the polymer-based overlay layer is visually discernible from a colour of the metallic substrate, a user is able to identify sliding elements embodying the present invention by simple visual inspection. This may also help a user to visually distinguish between several components which have been provided with different coatings, one of which is the polymer-based overlay layer of preferred embodiments of the present invention. This may advantageously help prevent miss-assembly during manufacture. 
     Preferably, the surface treated metal particulate appears a different colour to the same metal particulate without the surface treatment. 
     This allows the surface treated metal particulate itself to be distinguished from metal particulate which has not been surface treated which may simplify manufacture of the polymer-based overlay layer. 
     Preferably, the surface treated metal particulate causes the polymer-based overlay layer to appear a different colour to the colour the overlay layer would appear if it comprised the same metal particulate but without the surface treatment, with all other elements of the polymer-based overlay layer being kept the same. 
     This may advantageously enable different overlay layers with the same or similar mechanical performance enhancing additives to be distinguished (e.g. use of the surface treated metal particulate can enable manual or automatic identification of different curing regimes). The addition of a surface treated metal particulate enables the sliding engine components to be distinguished from those of a different provenance, so enhancing traceability. 
     Preferably, the surface treated metal particulate causes the polymer-based overlay layer to appear a colour other than silver, white, or grey. 
     This is advantageous since the metallic substrate itself can appear silver, white, or grey meaning that the overlay layer will be clearly distinguished from the metallic substrate itself 
     Preferably, the surface treated metal particulate causes the polymer-based overlay layer to appear gold, orange, or yellow. Optionally, the surface treated metal particulate may cause the polymer-based overlay layer to appear pale yellow in colour. 
     The provision of these colours is advantageous since they are all very different to the colours of both the metallic substrate and the polymer-based matrix without the surface treated metal particulate. The presence of a particular polymer-based overlay layer will therefore be clearly apparent where any of these colours is used. 
     Preferably, the polymer-based overlay layer comprises between about 5 wt % and about 40 wt % of the surface treated metal particulate. More preferably, between about 10 wt % and about 30 wt % of the surface treated metal particulate. More preferably, between about 24 wt % and about 28 wt % of the surface treated metal particulate. For example, the polymer-based overlay layer may comprise 26 wt % of the surface treated metal particulate. 
     As used herein, quantities of components described in weight percentages (wt %) refer to the weight percent of the components in the final cured coating, i.e. when the solvent has been removed and the polymer matrix has cured. 
     Advantageously, the metal particulate enhances the thermal conductivity of the overlay layer. The metal particulate may further enhance the fatigue and seizure resistance of the overlay layer. Below 5 wt % of the metal particulate, the improvement in fatigue and seizure resistance are not significant. Above about 40 wt % of the metal particulate, the structural integrity of the polymer-based overlay layer may be compromised. 
     The metal particulate may be chosen from: aluminium, aluminium alloys, copper, copper alloys, silver, tungsten, stainless steel. We have found that aluminium particulate gives the best results. The metal particulate may be any metal particulate but preferably comprises metal flakes. The flake-like nature of the particulate generally results in the maximum area of metal particulate being exposed to a co-operating shaft journal by virtue of the plane of the flakes orientating generally parallel to the bearing surface. The provision of flakes within the polymer-based overlay layer that are generally parallel to the bearing surface may be provided by spray deposition of the polymer-based overlay layer. 
     A further advantage of the platelet flake morphology of the metal particulate is that the flakes are more securely bonded to the polymer-based matrix by virtue of the relatively large surface area of each individual flake, and thus resists metal flakes becoming plucked from the polymer-based matrix during engine operation. 
     Preferably, the metal particulate comprises aluminium flakes. 
     Preferably, the surface treated aluminium flakes have a D50 size of between about 5 μm and about 30 μm along the maximal dimension. More preferably, a D50 size of between about 10 μm and about 20 μm along the maximal dimension. This has been found to provide a particularly suitable form of metal particulate addition. D50 is the median diameter of the particle size distribution of the aluminium flakes. 
     The surface treatment may comprise any surface treatment process which alters the colour of the resulting polymer-based overlay layer. 
     Preferably, the metal particulate is surface treated by a controlled oxidation process. For example, aluminium flakes may be oxidised under controlled conditions to form a layer of aluminium oxide on the surface of the flakes. It has been found that the provision in polymer-based overlay layers of aluminium flakes which have been oxidised under controlled conditions can give the overlay layer a yellow or pale yellow colour. 
     Where aluminium flakes are to be oxidised, the controlled oxidation may, for example, be carried out in an aqueous alkali solution resulting in a layer comprising aluminium oxide and aluminium hydroxide. 
     Alternatively or in addition, the metal particulate is surface treated by coating the surface of the metal particulate in another material. Metal oxides are particularly suitable materials for coating the particulate. The coating may be applied using any suitable method, for example spraying or dipping the particulate. 
     The metal oxide may be any metal oxide but preferably, the metal oxide is of a different metal to the metal of the metal particulate. This advantageously provides a greater choice of colours for the polymer-based overlay layer. 
     Preferably, the metal oxide is a coloured transition metal oxide. 
     It has been found that the provision in polymer-based overlay layers of aluminium flakes surface coated in a coloured transition metal oxide can give the overlay layer a gold, or orange colour. 
     Examples of coloured transition metal oxides include but are not limited to: iron oxide, nickel oxide, chromium oxide, and copper oxide. 
     The metal particulate may comprise a plurality of different surface treated metal particulates. For example, the metal particulate may comprise aluminium flakes which have undergone controlled oxidation and aluminium flakes coated with a coloured transition metal oxide. The metal particulate may further comprise metal particles which are not surface treated. For example, the metal particulate may comprise aluminium flakes which are not surface treated. 
     The relative quantities metal particulate having different surface treatments as well as metal particulate having no surface treatment may be chosen so as to customise the colour of the polymer-based overlay layer. It is conceivable that the thermal conductivity of the surface treated metal particulate may differ from the thermal conductivity of equivalent metal particulate without surface treatment. Accordingly, the relative quantities of metal particulate with and without surface treatment may be chosen so as to customise the thermal conductivity of the polymer-based overlay. 
     Preferably, the polymer-based overlay layer has a thickness of between about 3 μm and about 17 μm. More preferably, between about 6 μm and about 12 μm. For example, the polymer-based overlay layer may have a thickness of about 10 μm. 
     In a second aspect of the present invention, there is provided an engine comprising a sliding engine element according to the first aspect of the present invention. 
     In a third aspect of the present invention, there is provided a method of producing a sliding engine element. The method comprises steps of, providing a polymer-based matrix, providing a slurry comprising a surface treated metal particulate, combining the slurry and the polymer-based matrix, applying the polymer-based matrix and slurry combination to a metal substrate, curing the polymer-based matrix and slurry combination to form a polymer-based overlay layer comprising surface treated metal particulate, wherein the surface treated metal particulate causes the polymer-based overlay layer to appear a different colour to the surface of the metallic substrate. 
     The polymer-based matrix may be applied to the metal substrate by a number of different methods. Suitable methods include spraying, pad printing (an indirect offset printing process, e.g. in which a silicone pad transfers a patterned layer of the plastic polymer composite material onto the sliding bearing substrate), screen printing, or by a transfer rolling process. The deposition step may comprise the deposition of several sub-layers to build up the overall polymer-based overlay layer. The method may further comprise a flash-off phase between each sub-layer deposition to remove the solvent. Each sub-layer may comprise the same composition of polymer-based matrix. Alternatively, each sub-layer may comprise different compositions of the polymer-based matrix. 
     The curing step may take place at about 140° C. to 300° C. The thermal curing may be provided by baking in an oven or irradiating the sliding engine element with infrared radiation. Alternatively, the polymer-based overlay layer may be cured by a non-thermal process, for example being cured by exposure to ultraviolet light. The curing step may take between about 2 mins and about 2.5 hours. For example, the curing step may take about 2 hours. 
     It should be appreciated that any feature in one aspect of the invention may be applied to other aspects of the invention, in any appropriate combination. In particular, method aspects may be applied to apparatus aspects, and vice versa. Furthermore, any, some and/or all features in one aspect can be applied to any, some and/or all features in any other aspect, in any appropriate combination. 
     It should also be appreciated that particular combinations of the various features described and defined in any aspects of the invention can be implemented and/or supplied and/or used independently. 
     Throughout the description and claims of this specification, the words “comprise” and “contain” and variations of them mean “including but not limited to”, and they are not intended to (and do not) exclude other moieties, additives, components, integers or steps. Throughout the description and claims of this specification, the singular encompasses the plural unless the context otherwise requires. In particular, where the indefinite article is used, the specification is to be understood as contemplating plurality as well as singularity, unless the context requires otherwise. 
     Features, integers, characteristics, compounds, chemical moieties or groups described in conjunction with a particular aspect, embodiment or example of the invention are to be understood to be applicable to any other aspect, embodiment or example described herein unless incompatible therewith. All of the features disclosed in this specification (including any accompanying claims, abstract and drawings), and/or all of the steps of any method or process so disclosed, may be combined in any combination, except combinations where at least some of such features and/or steps are mutually exclusive. The invention is not restricted to the details of any foregoing embodiments. The invention extends to any novel one, or any novel combination, of the features disclosed in this specification (including any accompanying claims, abstract and drawings), or to any novel one, or any novel combination, of the steps of any method or process so disclosed. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWING 
       The invention will further be described by way of example only with reference to the accompanying drawing, in which: 
         FIG. 1  shows a perspective view of a bearing shell according to preferred embodiments of the present invention. The figure provided herein is schematic and not to scale. 
     
    
    
     DETAILED DESCRIPTION 
       FIG. 1  schematically illustrates a sliding bearing  100  (e.g. a sliding engine component) in the form of a hollow semi-cylindrical bearing lining shell (commonly referred to as a “half bearing”). Many alternative shapes and configurations of the bearing element are envisaged and will be readily apparent to the skilled person. The sliding bearing  100  has a metallic substrate  102  formed from steel. The sliding bearing  100  further comprises a bearing lining layer  104  on the concave inner surface of the metallic substrate  102 . Bearing lining layer  104  comprises an aluminium-tin alloy. A polymer-based overlay layer  106  is provided on the substrate  102 . The overlay layer  106  is configured to provide a running surface over the lifetime of the sliding bearing  100 . The overlay layer  106  is the innermost layer of the half bearing, which is configured to face a cooperating moving part (not shown) in a bearing assembly (e.g. the overlay layer receives a journaled shaft in an assembled bearing, which mutually cooperate, with an intervening film of lubricating oil). 
     The overlay layer  106  comprises a polymer-based matrix formed from polyamide imide (PAI). The overlay layer  106  further comprises aluminium flakes which have been coated in a layer of coloured transition metal oxide to form a surface treated metal particulate. Alternatively, a surface of the aluminium flakes may have been subjected to a controlled oxidation process. The aluminium flakes have a D50 size of between about 10 μm and about 20 μm along the maximal dimension. The overlay layer  106  comprises 26 wt % of the aluminium flakes dispersed evenly throughout the polymer-based matrix. The overlay layer  106  further comprises 10 wt % polytetrafluoroethylene (PTFE) to act as a dry lubricant. The dry lubricant has a particle size of about 3 μm. The overlay layer  106  further comprises less than 0.5 wt % leveller and silane as an adhesion agent. 
     The overlay layer  106  has a thickness of about 10 μm and appears gold in colour due to the coated aluminium flakes. 
     To form the sliding bearing  100  having a polymer based overlay layer  106 , the polymer (PAI) is added to a premixed solvent blend to form a solution. The dry lubricant and the leveller are added to the solution to form a suspension. The aluminium flakes are made into a slurry with a premixed solvent blend and this slurry added to the solution. The silane is then added to the solution. 
     The polymer-based matrix solution is then applied to the metallic substrate  102  which may already have a bearing lining layer  104  on its inner surface. The polymer-based matrix solution is applied by spraying to form a series of sub-layers. After the deposition of each sub-layer, the solvent is removed by a flash-off phase. After deposition, the polymer-based matrix solution is cured by heating the sliding bearing  100 . 
     Although illustrated in  FIG. 1  in relation to a half bearing shell, the present invention equally applies to other sliding engine components, including semi-annular, annular or circular thrust washers, and bushes. The mechanical performance enhancing additives (e.g. dry lubricant particulate, silane and metal particulate) dispersed within the polymer-based matrix provide significant enhancements to the mechanical performance of the sliding engine component, such as wear resistance, adhesion promotion, fatigue resistance, and frictional properties.