Patent Publication Number: US-11034885-B2

Title: Light emitting material, manufacture method thereof and organic light emitting diode using the light emitting material

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
     This is a divisional application of co-pending U.S. patent application Ser. No. 16/278,720, filed on Feb. 19, 2019, which is a divisional application of U.S. patent application Ser. No. 15/122,410, filed on Aug. 30, 2016 and now U.S. Pat. No. 10,280,365, which is a national stage of PCT Application No. PCT/CN2016/095615, filed on Aug. 17, 2016, claiming foreign priority of Chinese Patent Application No. 201610579646.9, filed on Jul. 20, 2016. 
    
    
     FIELD OF THE INVENTION 
     The present invention relates to a display technology field, and more particularly to a light emitting material, a manufacture method thereof and an organic light emitting diode using the light emitting material. 
     BACKGROUND OF THE INVENTION 
     The OLED (Organic Light-Emitting Diode) display, which is also named as the Organic light emitting display, is a new flat panel display device. Because it possesses advantages of simple manufacture process, low cost, low power consumption, high light emitting brightness, wide operating temperature range, thin volume, fast response speed, and being easy to achieve the color display and the large screen display, and being easy to achieve the match with the integrated circuit driver, and being easy to achieve the flexible display. Therefore, it has the broad application prospects. 
     The OLED display utilizes the organic light emitting diode for light emission. Thus, it is extremely important to improve the efficiency and lifetime of the organic light emitting diode. Now, the organic light emitting diode has already made considerable progress. With the fluorescence phosphorescence hybrid, the white light element with the simple structure and high efficiency can be obtained. The efficiency of such fluorescence phosphorescence hybrid element significantly relies on the efficiency of the fluorescence. Therefore, it still has vital significant meaning to develop the high efficiency fluorescence material. 
     In comparison with polymer, the small molecule light emitting molecule has the simple steps, the stable structure and can be purified, and then the higher element efficiency can be obtained for the possible commercial application. The method of manufacturing multiple layer element by implementing evaporation or solution process with small molecule has already drawn the great attention and the great progress has been made. However, the traditional organic fluorescence material only can utilize 25% of singlet excitons. Thus, there is extreme big restriction to the efficiency of the element. Recently, the Japanese Adachi research group utilizes the thermally activated delayed fluorescence mechanism to make the exciton availability of all organic material reach up to 100%, and the organic fluorescence element efficiency progresses significantly. Nevertheless, there is few for such kind of materials. Therefore, the type expansion for such kind of material has the significant meaning for the application in the future. For now, the organic small molecule light emitting material of simple structure, and possessing well performance and satisfying the commercialization requirement is still so limited. It is still profound to develop the light emitting material of low cost and excellent efficiency. 
     SUMMARY OF THE INVENTION 
     An objective of the present invention is to provide a light emitting material, in which the structure is unitary, and the formula weight is determined, and the better solubility and film formation are provided to be applied for small molecule organic light emitting diode. 
     Another objective of the present invention is to provide a manufacture method of the light emitting material, in which the steps are simple, and the production is high. 
     Another objective of the present invention is to provide an organic light emitting diode, in which the light emitting layer comprises the aforesaid light emitting material that has higher light emission efficiency and stability. 
     For realizing the aforesaid objectives, the present invention first provides a light emitting material, in which a constitutional formula is 
                         
wherein Ar 1  and Ar 2  are respectively selected from aromatic amine groups shown in formula (1), formula (2), formula (3), formula (4), formula (5), formula (6), formula (7);
 
     
       
         
         
             
             
         
       
     
     Ar 1  and Ar 2  are the same. 
     The light emitting material comprises one or more of following compounds: 
     
       
         
         
             
             
         
       
       
         
         
             
             
         
       
     
     The present invention further provides a manufacture method of light emitting material, comprising steps of: 
     step 1, manufacturing an intermediate 
     
       
         
         
             
             
         
       
     
     step 2, obtaining light emitting material with Ullmann reaction or Suzuki reaction of the intermediate 
                         
and an aromatic amine compound, in which a constitutional formula of the light emitting material is
 
                         
wherein Ar 1  and Ar 2  are respectively selected from aromatic amine groups shown in formula (1), formula (2), formula (3), formula (4), formula (5), formula (6), formula (7);
 
     
       
         
         
             
             
         
       
     
     Ar 1  and Ar 2  are the same. 
     The light emitting material comprises one or more of following compounds: 
     
       
         
         
             
             
         
       
       
         
         
             
             
         
       
     
     The step 1 comprises: 
     step 11, obtaining 
                         
with a reaction of p-bromothiophenol and 4-Bromo-2-fluorobenzonitrile;
 
     step 12, hydrolyzing 
                         
in an alkaline condition, and acidizing the same to obtain
 
     
       
         
         
             
             
         
       
     
     step 13, generating dehydration condensation reaction to 
                         
to obtain
 
     
       
         
         
             
             
         
       
     
     step 14, obtaining the intermediate 
                         
with a reaction of
 
                         
and hydrogen peroxide.
 
     The present invention provides an organic light emitting diode, comprising a substrate, and an anode, a Hole Injection Layer, a Hole Transporting Layer, a light emitting layer, an Electron Transport Layer, an Electron Injection Layer and a cathode stacking up on the substrate from bottom to top in order; 
     the light emitting layer comprises light emitting material, in which a constitutional formula is 
     
       
         
         
             
             
         
       
     
     wherein Ar 1  and Ar 2  are respectively selected from aromatic amine groups shown in formula (1), formula (2), formula (3), formula (4), formula (5), formula (6), formula (7); 
     
       
         
         
             
             
         
       
     
     Ar 1  and Ar 2  are the same. 
     The light emitting material comprises one or more of following compounds: 
     
       
         
         
             
             
         
       
       
         
         
             
             
         
       
     
     The benefits of the present invention are: the present invention provides a light emitting material, in which the structure is unitary, and the formula weight is determined, and the better solubility and film formation are provided, and the thin film status is stable; it possesses a very high decomposition temperature and a lower sublimation temperature, and is easy to sublime to be light emitting material of high purity, and can be applied for small molecule organic light emitting diode; by changing the aromatic amine group, which is connected, the physical property can be improved in advance to promote the performance of the photoelectric element of the light emitting material. The present invention provides a manufacture method of the light emitting material. p-bromothiophenol and 4-Bromo-2-fluorobenzonitrile are employed to be starting materials, and the intermediate of the light emitting material is obtained with a series of simple reactions, and finally, the light emitting material is obtained with Ullmann reaction or Suzuki reaction, and the steps are simple and the production is high. The present invention provides an organic light emitting diode, in which the light emitting layer comprises the aforesaid light emitting material that has higher light emission efficiency and stability. 
     In order to better understand the characteristics and technical aspect of the invention, please refer to the following detailed description of the present invention is concerned with the diagrams, however, provide reference to the accompanying drawings and description only and is not intended to be limiting of the invention. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The technical solution and the beneficial effects of the present invention are best understood from the following detailed description with reference to the accompanying figures and embodiments. 
       In drawings, 
         FIG. 1  is a flowchart of a manufacture method of light emitting material according to the present invention; 
         FIG. 2  is a structure diagram of an organic light emitting diode according to the present invention. 
     
    
    
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS 
     For better explaining the technical solution and the effect of the present invention, the present invention will be further described in detail with the accompanying drawings and the specific embodiments. 
     The present invention first provides a light emitting material, in which a constitutional formula is 
                         
wherein Ar 1  and Ar 2  are respectively selected from aromatic amine groups shown in formula (1), formula (2), formula (3), formula (4), formula (5), formula (6), formula (7);
 
     
       
         
         
             
             
         
       
     
     Preferably, Ar 1  and Ar 2  are the same. 
     Specifically, the light emitting material comprises one or more of following compounds: 
     
       
         
         
             
             
         
       
       
         
         
             
             
         
       
     
     In the aforesaid light emitting material, the structure is unitary, and the formula weight is determined, and the better solubility and film formation are provided, and the thin film status is stable; it possesses a very high decomposition temperature and a lower sublimation temperature, and is easy to sublime to be light emitting material of high purity, and can be applied for small molecule organic light emitting diode; by changing the aromatic amine group, which is connected, the physical property can be improved in advance to promote the performance of the photoelectric element of the light emitting material. 
     Please refer to  FIG. 1 . The present invention further provides a manufacture method of light emitting material, comprising steps of: 
     step 1, manufacturing an intermediate 
     
       
         
         
             
             
         
       
     
     A synthetic route of the intermediate 
                         
is:
 
     
       
         
         
             
             
         
       
     
     Specifically, the step 1 comprises steps of: 
     step 11, obtaining 
                         
with a reaction of p-bromothiophenol and 4-Bromo-2-fluorobenzonitrile.
 
     The specific implementing steps of the step 11 are: 
     In 250 ml boiling flask-3-neck, 0.73 g (30 mmol) NaH is slowly added in 20 ml dry dimethylformamide (DMF) dissolved with 4.6 g (25 mmol) p-bromothiophenol, and then 20 ml dry dimethylformamide dissolved with 5 g (25 mmol) 4-Bromo-2-fluorobenzonitrile is dropped into it. Under the protection of nitrogen, 20 h heating reflux reaction is implemented, and the temperature drops to the room temperature after the reaction is completed, and then the reaction fluid is poured in 50 ml 1M NaOH solution, and extracted in dichloromethane (DCM) to be decompressed to remove the solvent, and through silicagel column, white color solid 5.2 g, i.e. the compound b1 is obtained. Molecular formula: C 13 H 7 Br 2 NS, and MS: 366.87, and elemental analysis: C, 42.31; H, 1.91; Br, 43.30; N, 3.80; S, 8.69. 
     step 12, hydrolyzing 
                         
in an alkaline condition, and acidizing the same to obtain
 
     
       
         
         
             
             
         
       
     
     The specific implementing steps of the step 12 are: 
     In 250 ml boiling flask-3-neck, 80 ml deionized water, 15 g KOH and 80 ml alcohol are added, and 5.2 g compound b1 is added in reaction bottle to reflow overnight under protection of nitrogen. After the reaction is completed, the reaction solution is cooled to the room temperature, and added in 100 ml 6M hydrochloric acid, the white solid is separated out with ice bath, and extracted and filtered, and then dried to obtain white solid 5.1 g, i.e. the compound b2. Molecular formula: C 13 H 8 Br 2 O 2 S, and MS: 385.86, and elemental analysis: C, 40.23; H, 2.08; Br, 41.18; O, 8.25; S, 8.26. 
     step 13, generating dehydration condensation reaction to 
                         
to obtain
 
     
       
         
         
             
             
         
       
     
     The specific implementing steps of the step 13 are: 
     In 500 ml boiling flask, 2.75 g (10 mmol) compound b2 is added, and 500 ml chloroform is added to be solvent, and 3.2 g (20 mmol, 2 equ) trifluoroacetic anhydride is dropped, and stirred 10 min in the room temperature, and then 0.5 g Boron trifluoride etherate is added, and the ice bath is removed for reacting 12 h at the room temperature. After the reaction is completed, sodium sulfite saturated aqueous solution is added to quench redundant trifluoroacetic anhydride, and separated, and reduced pressure distilled to remove the solvent, and through column, 
                         
is obtained. Molecular formula: C 13 H 8 Br 2 O 2 S; MS: 385.86; elemental analysis: C, 40.23; H, 2.08; Br, 41.18; O, 8.25; S, 8.26.
 
     step 14, obtaining the intermediate 
                         
with a reaction of
 
                         
and hydrogen peroxide.
 
     The specific implementing steps of the step 14 are: 
     In 250 ml boiling flask-3-neck, 5 g (13.59 mmol), 50 mL dichloromethane 
                         
20 mL ethylic acid, 3 mL (5 equ) hydrogen peroxide are added. The reaction last 8 hours at 80° C., and the temperature is lowered after the reaction is completed, and water is used to remove redundant hydrogen peroxide for extraction. Through column, 4.6 g intermediate
 
                         
is obtained, and productivity is 85%. Molecular formula: C 13 H 6 Br 2 O 3 S; M/Z=399.84; theoretic value: 402.06; elemental analysis: 401.84 (100.0%), 399.84 (50.0%), 403.84 (48.1%), 402.84 (15.0%), 404.84 (7.8%), 400.84 (7.5%), 403.83 (4.4%), 405.83 (2.2%).
 
     step 2, obtaining light emitting material with Ullmann reaction or Suzuki reaction of the intermediate 
                         
and an aromatic amine compound, in which a constitutional formula of the light emitting material is
 
                         
wherein Ar 1  and Ar 2  are respectively selected from aromatic amine groups shown in formula (1), formula (2), formula (3), formula (4), formula (5), formula (6), formula (7);
 
     
       
         
         
             
             
         
       
     
     Preferably, Ar 1  and Ar 2  are the same. 
     Specifically, the light emitting material comprises one or more of following compounds: 
     
       
         
         
             
             
         
       
       
         
         
             
             
         
       
     
     Specifically, in the step 2, the aromatic amine compound comprises one or more of carbazol, diphenylamine, 9,9-diMethylacridan, 4-carbazoleBenzene borate ester, 4-phenylcarbazole borate ester, 4-triphenylamine borate ester, 4-phenylthiophene-S,S-dioxide borate ester; 
     a constitutional formula of the carbazol is 
     
       
         
         
             
             
         
       
     
     a constitutional formula of the diphenylamine is 
     
       
         
         
             
             
         
       
     
     a constitutional formula of the 9,9-diMethylacridan is 
     
       
         
         
             
             
         
       
     
     a constitutional formula of the 4-carbazoleBenzene borate ester is 
     
       
         
         
             
             
         
       
     
     a constitutional formula of the 4-phenylcarbazole borate ester is 
     
       
         
         
             
             
         
       
     
     a constitutional formula of the 4-triphenylamine borate ester is 
     
       
         
         
             
             
         
       
     
     a constitutional formula of the 4-phenylthiophene-S,S-dioxide borate ester is 
     
       
         
         
             
             
         
       
     
     The specific implementing method of the step 2 is described below in detail with combination of the specific embodiment. 
     Embodiment 1: 
                         
is obtained with Ullmann reaction of intermediate
 
                         
and carbazol, and the reaction formula is:
 
     
       
         
         
             
             
         
       
     
     The specific implementing steps are: 
     Under the protection of nitrogen, in boiling flask-3-neck, 100 ml methylbenzene, 0.72 g (2 mmol) intermediate 
                         
0.67 g (4 mmol) carbazol are added, and 0.3 g sodium tert-butoxide is added in stirring, and then 20 mg tris(dibenzylideneacetone)dipalladium (Pd2(dba)3) is added, and then 0.3 ml 10% tri-tert-butylphosphine hexane solution is added, and heated reflux to react overnight. The temperature is lowered, and extracted in dichloromethane in organic phase, and spin dried, and through column. White color solid product 0.81 g is obtained, and productivity is 75%. Molecular formula: C 37 H 22 N 2 O 3 S; M/S=574.14; theoretic value: 574.65; elemental analysis: 574.14 (100.0%), 575.14 (40.4%), 576.14 (9.2%), 576.13 (4.5%), 577.13 (1.8%), 575.13 (1.5%), 577.15 (1.0%).
 
     Embodiment 2: 
                         
is obtained with Ullmann reaction of intermediate
 
                         
and diphenylamine, and the reaction formula is:
 
     
       
         
         
             
             
         
       
     
     The specific implementing steps are: 
     Under the protection of nitrogen, in boiling flask-3-neck, 100 ml methylbenzene, 0.72 g (2 mmol) intermediate 
                         
0.84 g (4 mmol) diphenylamine are added, and 0.3 g sodium tert-butoxide is added in stirring, and then 20 mg tris(dibenzylideneacetone)dipalladium (Pd2(dba)3) is added, and then 0.3 ml 10% tri-tert-butylphosphine hexane solution is added, and heated reflux to react overnight. The temperature is lowered, and extracted in dichloromethane in organic phase, and spin dried, and through column. White color solid product 0.81 g is obtained, and productivity is 75%. Molecular formula: C 37 H 26 N 2 O 3 S; M/S=578.17; theoretic value: 578.68; elemental analysis: 578.17 (100.0%), 579.17 (41.2%), 580.17 (9.1%), 580.16 (4.5%), 581.17 (2.2%), 581.18 (1.0%).
 
     Embodiment 3: 
                         
is obtained with Ullmann reaction of intermediate
 
                         
and 9,9-diMethylacridan, and the reaction formula is:
 
     
       
         
         
             
             
         
       
     
     The specific implementing steps are: 
     Under the protection of nitrogen, in boiling flask-3-neck, 100 ml methylbenzene, 0.72 g (2 mmol) intermediate 
                         
0.84 g (4 mmol) 9,9-diMethylacridan are added, and 0.3 g sodium tert-butoxide is added in stirring, and then 20 mg tris(dibenzylideneacetone)dipalladium (Pd2(dba)3) is added, and then 0.3 ml 10% tri-tert-butylphosphine hexane solution is added, and heated reflux to react overnight. The temperature is lowered, and extracted in dichloromethane in organic phase, and spin dried, and through column. White color solid product 0.85 g is obtained, and productivity is 79%. Molecular formula: C 43 H 34 N 2 O 3 S; M/S=658.23; theoretic value: 658.81; elemental analysis: 658.23 (100.0%), 659.23 (48.2%), 660.24 (10.8%), 660.22 (4.5%), 661.23 (2.2%), 661.24 (2.0%), 660.23 (1.3%).
 
     Embodiment 4: 
                         
is obtained with Suzuki reaction of intermediate
 
                         
and 4-carbazoleBenzene borate ester, and the reaction formula is:
 
     
       
         
         
             
             
         
       
     
     The specific implementing steps are: 
     Under the atmosphere of nitrogen, in 250 ml boiling flask, 96 ml methylbenzene, 32 ml alcohol, 16 ml 2M potassium carbonate aqueous solution, 0.72 g (2 mmol) intermediate 
                         
2.06 g (1.2 equ) 4-carbazoleBenzene borate ester are added, and stirred at the room temperature, and then 100 mg triphenylphosphineplatinum (catalyzer) is added and 96° C. reflows for 24 hours. It is cooled to the room temperature, and extracted in dichloromethane, and dried in anhydrous magnesium sulfate. White color solid product 0.86 g is obtained, and productivity is 79%. Molecular formula: C 49 H 30 N 2 O 3 S; M/S=726.2; theoretic value: 726.84; elemental analysis: 726.20 (100.0%), 727.20 (54.3%), 728.20 (15.2%), 728.19 (4.5%), 729.21 (2.7%), 729.20 (2.6%).
 
     Embodiment 5: 
                         
is obtained with Suzuki reaction of intermediate
 
                         
and 4-phenylcarbazole borate ester, and the reaction formula is:
 
     
       
         
         
             
             
         
       
     
     The specific implementing steps are: 
     Under the atmosphere of nitrogen, in 250 ml boiling flask, 96 ml methylbenzene, 32 ml alcohol, 16 ml 2M potassium carbonate aqueous solution, 0.72 g (2 mmol) intermediate 
                         
2.32 g (1.2 equ) 4-phenylcarbazole borate ester are added, and stirred at the room temperature, and then 100 mg triphenylphosphineplatinum (catalyzer) is added and 96° C. reflows for 24 hours. It is cooled to the room temperature, and extracted in dichloromethane, and dried in anhydrous magnesium sulfate. White color solid product 0.92 g is obtained, and productivity is 83%. Molecular formula: C 49 H 30 N 2 O 3 S; M/S=726.2; theoretic value: 726.84; elemental analysis: 726.20 (100.0%), 727.20 (54.3%), 728.20 (15.2%), 728.19 (4.5%), 729.21 (2.7%), 729.20 (2.6%).
 
     Embodiment 6: 
                         
is obtained with Suzuki reaction of intermediate
 
                         
and 4-triphenylamine borate ester, and the reaction formula is:
 
     
       
         
         
             
             
         
       
     
     The specific implementing steps are: 
     Under the atmosphere of nitrogen, in 250 ml boiling flask, 96 ml methylbenzene, 32 ml alcohol, 16 ml 2M potassium carbonate aqueous solution, 0.72 g (2 mmol) intermediate 
                         
2.32 g (1.2 equ) 4-triphenylamine borate ester are added, and stirred at the room temperature, and then 100 mg triphenylphosphineplatinum (catalyzer) is added and 96° C. reflows for 24 hours. It is cooled to the room temperature, and extracted in dichloromethane, and dried in anhydrous magnesium sulfate. White color solid product 0.96 g is obtained, and productivity is 87%. Molecular formula: C 49 H 34 N 2 O 3 S; M/S=730.23; theoretic value: 730.87; elemental analysis: 730.23 (100.0%), 731.23 (54.7%), 732.24 (14.0%), 732.22 (4.5%), 733.24 (2.8%), 733.23 (2.5%), 732.23 (1.4%).
 
     Embodiment 7: 
                         
is obtained with Suzuki reaction of intermediate
 
                         
and 4-phenylthiophene-S,S-dioxide borate ester, and the reaction formula is:
 
     
       
         
         
             
             
         
       
     
     The specific implementing steps are: 
     Under the atmosphere of nitrogen, in 250 ml boiling flask, 96 ml methylbenzene, 32 ml alcohol, 16 ml 2M potassium carbonate aqueous solution, 0.72 g (2 mmol) intermediate 
                         
2.06 g (1.2 equ) 4-phenylthiophene-S,S-dioxide borate ester are added, and stirred at the room temperature, and then 100 mg triphenylphosphineplatinum (catalyzer) is added and 96° C. reflows for 24 hours. It is cooled to the room temperature, and extracted in dichloromethane, and dried in anhydrous magnesium sulfate. White color solid product 0.96 g is obtained, and productivity is 87%. Molecular formula: C 49 H 30 N 2 O 7 S 3 ; M/S=854.12; theoretic value: 854.97; elemental analysis: 854.12 (100.0%), 855.12 (56.1%), 856.13 (15.5%), 856.12 (15.3%), 857.12 (7.5%), 857.13 (3.7%), 858.12 (2.3%).
 
     In the aforesaid manufacture method of the light emitting material, p-bromothiophenol and 4-Bromo-2-fluorobenzonitrile are employed to be starting materials, and the intermediate of the light emitting material is obtained with a series of simple reactions, and finally, the light emitting material is obtained with Ullmann reaction or Suzuki reaction, and the steps are simple and the production is high. 
     Please refer to  FIG. 2 . The present invention further provides an organic light emitting diode, comprising a substrate  10 , and an anode  20 , a Hole Injection Layer  30 , a Hole Transporting Layer  40 , a light emitting layer  50 , an Electron Transport Layer  60 , an Electron Injection Layer  70  and a cathode  80  stacking up on the substrate  10  from bottom to top in order; 
     the light emitting layer  50  comprises light emitting material, in which a constitutional formula is 
     
       
         
         
             
             
         
       
     
     wherein Ar 1  and Ar 2  are respectively selected from aromatic amine groups shown in formula (1), formula (2), formula (3), formula (4), formula (5), formula (6), formula (7); 
     
       
         
         
             
             
         
       
     
     Preferably, Ar 1  and Ar 2  are the same. 
     Specifically, the light emitting material comprises one or more of following compounds: 
     
       
         
         
             
             
         
       
       
         
         
             
             
         
       
     
     Preferably, in material of the light emitting layer  50 , a mass percentage of the light emitting material is 1%. 
     Specifically, the light emitting layer  50  can emit red light, yellow light, green light or blue light. 
     Specifically, material of the anode  20  comprises transparent metal oxide. The transparent metal oxide is preferably to be Indium Tin Oxide (ITO). 
                         
Specifically, material of the Hole Injection Layer  30  comprises 2,3,6,7,10,11-Hexacyano-1,4,5,8,9,12-hexaazatriphenylene (HAT-CN), and a constitutional formula of the 2,3,6,7,10,11-Hexacyano-1,4,5,8,9,12-hexaazatriphenylene is.
 
     Specifically, material of the Hole Transporting Layer  40  comprises 1,1-Bis[4-[N,N-di(p-tolyl)amino]phenyl]cyclohexane (TAPC), and a constitutional formula of the 1,1-Bis[4-[N,N-di(p-tolyl)amino]phenyl]cyclohexane is 
     
       
         
         
             
             
         
       
     
     Specifically, material of the light emitting layer  50  further comprises 4,4′-Bis(N-carbazolyl)-1,1′-biphenyl (CBP), and a constitutional formula of the 4,4′-Bis(N-carbazolyl)-1,1′-biphenyl is 
     
       
         
         
             
             
         
       
     
     Specifically, material of the Electron Transport Layer  60  comprises 1,3,5-tri[(3-pyridyl)-phen-3-yl]benzene (TmPyPB), and a constitutional formula of the 1,3,5-tri[(3-pyridyl)-phen-3-yl]benzene is 
     
       
         
         
             
             
         
       
     
     Specifically, material of the Electron Injection Layer  70  comprises Lithium fluoride (LiF). 
     Specifically, material of cathode  80  comprises aluminum (Al). 
     Preferably, a thickness of the anode  20  is 95 mm, and a thickness of the Hole Injection Layer  30  is 5 mm, and a thickness of the Hole Transporting Layer  40  is 20 mm, and a thickness of the light emitting layer  50  is 35 mm, and a thickness of the Electron Transport Layer  60  is 55 mm, and a thickness of the Electron Injection Layer  70  is 1 mm, and a thickness of the cathode  80  is larger than 80 nm. 
     The manufacture process of the organic light emitting diode is: putting Indium Tin Oxide transparent conductive glass in the cleaner for the ultrasonic process, and using the deionized water for cleaning to employ ultrasound to remove oil in the mixture solution of acetone/ethanol, and then, baking the same in the clean environment until the water is completely removed, and then, using ultraviolet light and ozone for cleaning, and employing low energy cation to bombard the same to obtain the anode  20 , and putting the transparent conductive glass with the anode  20  in the vacuum chamber, and vacuuming to 1×10 −5 -9×10 −3  Pa, and next, sequentially evaporating the Hole Injection Layer  30 , the Hole Transporting Layer  40 , the plurality of light emitting layer  50 , the Electron Transport Layer  60 , the Electron Injection Layer  70  and the cathode  80  on the anode  20 , and ultimately obtaining the organic light emitting diode of this embodiment. 
     In conclusion, the present invention provides a light emitting material, in which the structure is unitary, and the formula weight is determined, and the better solubility and film formation are provided, and the thin film status is stable; it possesses a very high decomposition temperature and a lower sublimation temperature, and is easy to sublime to be light emitting material of high purity, and can be applied for small molecule organic light emitting diode; by changing the aromatic amine group, which is connected, the physical property can be improved in advance to promote the performance of the photoelectric element of the light emitting material. The present invention provides a manufacture method of the light emitting material. p-bromothiophenol and 4-Bromo-2-fluorobenzonitrile are employed to be starting materials, and the intermediate of the light emitting material is obtained with a series of simple reactions, and finally, the light emitting material is obtained with Ullmann reaction or Suzuki reaction, and the steps are simple and the production is high. The present invention provides an organic light emitting diode, in which the light emitting layer comprises the aforesaid light emitting material that has higher light emission efficiency and stability. 
     Above are only specific embodiments of the present invention, the scope of the present invention is not limited to this, and to any persons who are skilled in the art, change or replacement which is easily derived should be covered by the protected scope of the invention. Thus, the protected scope of the invention should go by the subject claims.