Patent Publication Number: US-2017369807-A1

Title: Ionic Liquid, Lubricant, and Magnetic Recording Medium

Description:
BACKGROUND OF THE INVENTION 
     Field of the Invention 
     The present invention relates to an ionic liquid, a lubricant containing the ionic liquid, and a magnetic recording medium using the lubricant. 
     Description of the Related Art 
     Conventionally, in a thin film magnetic recording medium, a lubricant is applied onto a surface of a magnetic layer for the purpose of reducing frictions between a magnetic head and the surface of the magnetic recording medium, or reducing abrasion. In order to avoid adhesion, such as sticktion, an actual film thickness of the lubricant is of a molecular order. Accordingly, it is not exaggeration to say that the most important thing for a thin film magnetic recording medium is to select a lubricant having excellent abrasion resistance in any environment. 
     During a life of a magnetic recording medium, it is important that a lubricant is present on a surface of the medium without causing desorption, spin-off, and chemical deteriorations. Making the lubricant present on a surface of a medium is more difficult, as the surface of the thin film magnetic recording medium is smoother. This is because the thin film magnetic recording medium does not have an ability of replenishing a lubricant as with a coating—type magnetic recording medium. 
     In the case where an adhesion force between a lubricant and a protective film disposed at a surface of a magnetic layer is weak, moreover, a film thickness of the lubricant is reduced during heating or sliding hence accelerating abrasion. Therefore, a large amount of the lubricant is required. The large amount of the lubricant is the mobile lubricant, and therefore a function of replenishing the lost lubricant can be provided. However, an excessive amount of the lubricant makes the film thickness of the lubricant larger than the surface roughness. Therefore, a problem associated with adhesion arises, and in a crucial case, sticktion arises to cause driving failures. 
     As illustrated in  FIG. 1 , although an increase rate of an areal density of a hard disk drive of a product have been reduced in the last few years, the increase rate has reached an anural rate of 25%, and has nearly reached 4 Tb/in 2 , which is one of targets, in Advances in Tribology Volume 2013, Article ID 521086. As illustrated in  FIG. 2 , it has been understood that a distance between head disk interfaces relative to an increase in the recording density reduces, but there is a need to always improve reliability corresponding to the reduction in the distance, which can be described, for example, in the following literatures. 
     (&lt;1&gt; C. M. Mate, Q. Dai, R. N. Payne, B. E. Knigge, and P. Baumgart, “Will the numbers add up for sub-7-nm magnetic spacings? Future metrology issues for disk drive lubricants, overcoats, and topographies,” IEEE Transactions on Magnetics, vol. 41, no. 2, pp. 626-631, 2005.
 
&lt;2&gt; B. Marchon and T. Olson, “Magnetic spacing trends: from LMR to PMR and beyond,” IEEE Transactions on Magnetics, vol. 45, no. 10, pp. 3608-3611, 2009, and
 
&lt;3&gt; J. Gui, “Tribology challenges for head-disk interface toward 1 Tb/in 2 ,” IEEE Transactions on Magnetics, vol. 39, no. 2, pp. 716-721, 2003.)
 
     A current recording density is about 1 Tb/in 2 , spacing is about 6 nm, and a thickness of a lubricant is 0.8 nm. The thickness of the lubricant needs to be reduced at the prospective recording density of 4 Tb/in 2 . In order to reduce a thickness of a film of a PFPE lubricant commonly used in the art, however, a molecular weight of the PFPE lubricant needs to be decreased. The smaller molecular weight of the PFPE lubricant has a problem that thermal stability is deteriorated. It has been understood that the above-described problems associated with reliability have not be sufficiently solved with common perfluoropolyether (PFPE)-based lubricants. 
     Particularly for a thin film magnetic recording medium having high surface smoothness, a novel lubricant is designed at a molecular level, and synthesized to solve the above-described trade-off. Moreover, there are a number of reports regarding lubricity of PFPE. As described, lubricants are very important in magnetic recording media. 
     Chemical structures of typical PFPE-based lubricants are depicted in Table 1. 
     
       
         
           
               
             
               
                 TABLE 1 
               
               
                   
               
             
            
               
                 Fomblin-based lubricants 
               
            
           
           
               
               
            
               
                   
                 X—CF 2 (OCF 2 CF 2 ) n (OCF 2 ) m OCF 2 —X(0.5 &lt; n/m &lt; 1) 
               
               
                 Z 
                 X = —OCF 3   
               
               
                 Z-DOL 
                 X = —CH 2 OH 
               
               
                 Z-DIAC 
                 X = —COOH 
               
               
                 Z-Tetraol 
                 X = —CH 2 OCH 2 CHCH 2 OH 
               
               
                   
                 OH 
               
               
                   
               
               
                 AM2001 
                 
                   
                     
                     
                         
                         
                     
                   
                 
               
               
                   
               
            
           
           
               
            
               
                 Other lubricants 
               
            
           
           
               
               
            
               
                 A20H 
                 
                   
                     
                     
                         
                         
                     
                   
                 
               
               
                   
               
               
                 Mono 
                 F—(CF 2 CF 2 CF 2 O) 1 —CF 2 CF 2 CH 2 —N(C 3 H 7 ) 2   
               
               
                   
               
            
           
         
       
     
     Z-DOL in Table 1 is one of lubricants typically used for thin-film magnetic recording media. Moreover, Z-tetraol (ZTMD) is a lubricant, in which a functional hydroxyl group is further introduced into a main chain of PFPE, and it has been reported that use of Z-tetraol enhances reliability of a drive while reducing a space at an interface between a head and a medium. It has been reported that A20H suppresses decomposition of the PFPE main chain with Lewis acid or Lewis base, and improves tribological properties. On the other hand, it has been reported that Mona has a different polymer main chain and different polar groups to those of the PFPE, and the polymer main chain and polar groups of Mono are respectively poly-n-propyloxy, and amine, and Mono reduces adhesion interactions at near contact. 
     However, a typical solid lubricant, which has a high melting point and is considered thermally stable, disturbs an electromagnetic conversion process that is extremely highly sensitive, and moreover, an abrasion powder scraped by a head is generated on a running track. Therefore, abrasion properties are deteriorated. As described above, the liquid lubricant has mobility that enables to move the adjacent lubricant layer to replenish the lubricant removed due to abrasion by the head. However, the lubricant is span-off from a surface of the disk especially at a high temperature during driving of the disk, because of the mobility of the lubricant, and thus the lubricant is reduced. As a result, a protection function is lost. Accordingly, a lubricant having a high viscosity and low volatility is suitably used, and use of such a lubricant enables to prolong a service life of a disk drive with suppressing an evaporation rate. 
     Considering the above-described lubricating systems, requirements for a low-friction and low-abrasion lubricant used for thin film magnetic recording media are as follows. 
     (1) Low volatility.
 
(2) Low surface tension for a surface filling function.
 
(3) Interaction between terminal polar groups and a surface of a disk.
 
(4) High thermal and oxidization stability in order to avoid decomposition or reduction over a service period.
 
(5) Chemically inactive with metals, glass, and polymers, and no abrasion powder generated from a head or a guide.
 
(6) No toxicity and no flammability.
 
(7) Excellent boundary lubricating properties.
 
(8) Soluble with organic solvents.
 
     Recently, an ionic liquid has been attracted attentions as one of solvents for synthesis of organic or inorganic materials and being friendly to the environments in the fields of electricity storage materials, a separation technology, and a catalyst technology. The ionic liquid is roughly classified as a molten salt having a low melting point. The ionic liquid is typically a molten salt having a melting point of 100° C. or lower, among the above-mentioned molten salts. The important properties of the ionic liquid used as a lubricant are low volatility, inflammability, thermal stability, and an excellent dissolving performance. 
     For example, abrasion and wear of a surface of a metal or ceramic may be reduced by using a certain ionic liquid compared to a conventional hydrocarbon-based lubricant. For example, there is a report that, in the case where an imidazole cation-based ionic liquid is synthesized by substituting with a fluoroalkyl group, and tetrafluoroboric acid salt or hexafluorophosphoric acid salt of alkyl imidazolium is used for steel, aluminium, copper, single crystal SiO 2 , silicon, or sialon ceramics (Si—Al—O—N), tribological properties more excellent than those of cyclic phosphazene (X-1P) or PFPE are exhibited. Moreover, there is a report that an ammonium-based ionic liquid reduces frictions more than a base oil in the region of elastohydrodynamic to boundary lubrication. Moreover, effects of the ionic liquid as an additive for a base oil have been studied, and a chemical or tribochemical reaction of the ionic liquid has been researched to understand lubricating systems. However, there are almost no application examples of the ionic liquid to magnetic recording media. 
     Among the ionic liquids, a perfluorooctanoic acid alkyl ammonium salt is a protic ionic liquid (PIL), and has been reported as having a significant effect of reducing frictions of magnetic recording media compared to Z-DOL mentioned above (for example, &lt;1&gt; Japanese Patent No. 2581090, &lt;2&gt; Japanese Patent No. 2629725, &lt;3&gt; Kondo, H., Seto, J., Haga. S., Ozawa, K. (1989) Novel Lubricants for Magnetic Thin Film Media, Magnetic Soc. Japan, Vol. 13, Suppl. No. 51, pp. 213-218, &lt;4&gt; Kondo, H., Seki, A., Watanabe, H., &amp; Seto, J., (1990). Frictional Properties of Novel Lubricants for Magnetic Thin Film Media, IEEE Trans. Magn. Vol. 26, No. 5, (September 1990), pp. 2691-2693, ISSN: 0018-9464, &lt;5&gt; Kondo, H., Seki, A., &amp; Kita, A., (1994a). Comparison of an Amide and Amine Salt as Friction Modifiers for a Magnetic Thin Film Medium. Tribology Trans. Vol. 37, No. 1, (January 1994), pp. 99-104, ISSN: 0569-8197). 
     However, the above-mentioned perfluorocarboxylic acid ammonium salts have weak interaction between a cation and an anion in the reaction represented by the following reaction formula (A). According to Le Chatelier&#39;s principle, the equilibrium of the reaction is sifted to the left side at a high temperature, and the perfluorocarboxylic acid ammonium salt becomes a dissociated neutral compound and hence thermal stability is deteriorated. Specifically, protons are transferred at a high temperature, the equilibrium is sifted to neutral substance and dissociation occurs (see, for example, Yoshizawa, M., Xu, W., Angell, C. A., Ionic Liquids by Proton Transfer: Vapor pressure, Conductivity, and the Relevance of ΔpKa from Aqueous Solutions, J. Am. Chem. Soc., Vol. 125, pp. 15411-15419 (2003)). 
       C n F 2n+1 COOH+C n F 2n+1 NH 2 ⇄C n F 2n+1 COO − H 3 N + C n H 2n+1   (A)
 
     Meanwhile, the limit of a surface recording density of a hard disk is said to be from 1 Tb/in 2  to 2.5 Tb/in 2 . Currently, the surface recording density is getting close to the limit, but developments of technology for increasing capacities have been actively conducted with a reduction in particle size of magnetic particles as a premise. As the technology for increasing capacities, there are a reduction in an effective flying height and introduction of Shingle Write (BMP). 
     Moreover, there is “thermally-assisted magnetic recording (heat assisted magnetic recording)” as the next-generation recording technology. The outline of the thermally-assisted magnetic recording is illustrated in  FIG. 3 . In  FIG. 3 , the referential numeral  1  is laser light, the referential numeral  2  is near field light, the referential numeral  3  is a recording head (PMR element), and the referential numeral  4  is a reproducing head (TMR element). The problems of the thermally-assisted magnetic recording include a deterioration of durability due to evaporation or deterioration of a lubricant on a surface of a magnetic layer because a recording area is heated by laser during recording and reproducing. Even though it is a short period, there is a possibility that a thin film magnetic recording medium is exposed to a high temperature, which is 400° C. or higher, in thermally-assisted magnetic recording. Therefore, there are concerns about thermal stability of a lubricant generally used for thin film magnetic recording media, such as Z-DOL and Z-TETRAOL. 
     A protic ionic liquid forms ions as described above, and is typically a material having high thermal stability. The equilibrium of the protic ionic liquid is represented by Scheme 1 below. 
     
       
         
         
             
             
         
       
     
     In Scheme 1, HA is Bronsted acid and B is Bronsted base. The acid (HA) and the base (B) are reacted as in Scheme 1 to generate a salt (A − HB+). 
     In Scheme 1, a dissociation constant K a1  of the acid and a dissociation constant K b2  of the base can be represented by Scheme 2 below in the form including the density. 
     
       
         
         
             
             
         
       
     
     The K a1  and K b2  largely differ depending on a substance. In some cases, the K a1  and K b2  may be large digits, which is inconvenient for handling. Therefore, it is often represented with a negative logarithm. Specifically, the acid dissociation constant is determined as −log 10  K a1 =pK a1  as represented by Scheme 3 below. Clearly, acidity is stronger, as the pK a1  is smaller. 
     A difference ΔpKa of the acid dissociation constants of the acid and the base is discussed. The acid-base reaction is influenced by both acidity of the acid and basicity of the base (or acidity of conjugate acid of the base), and the difference ΔpKa in the acidity of the acid and base is represented by Scheme 3 below. 
     
       
         
         
             
             
         
       
     
     It is indicated that the ΔpKa increases, as the base concentration [A − HB+] increases relative to the acid concentration and the base concentration. 
     Meanwhile, Yoshizawa et al. have reported that proton transfer tends to occur when a difference (ΔpKa) of pKa of acid and base is 10 or greater, 
       [AH]+[B] [A − HB+] 
     the equilibrium of the formula above is sifted to the ion side (right side), and stability is enhanced further (see, for example, Yoshizawa, M., Xu, W., Angell, C. A., Ionic Liquids by Proton Transfer: Vapor pressure, Conductivity, and the Relevance of ΔpKa from Aqueous Solutions, J. Am. Chem. Soc., Vol. 125, pp. 15411-15419 (2003)). Moreover, Watanabe et al. has reported that proton transfer and thermal stability of a protic ionic liquid largely depend on ΔpKa, and thermal stability of the ionic liquid is significantly improved by using the acid with which the difference in pKa between the acid and the base (ΔpKa) is 15 or greater when DBU (1,8-diazabicyclo[5,4,0]undec-7-ene) is used as a base (see, for example, Miran, M. S., Kinoshita, H., Yasuda, T., Susan, M. A. B. H., Watanabe, M., Physicochemical Properties Determined by ΔpKa for Protic Ionic Liquids Based on an Organic Super-strong Base with Various Bronsted Acids, Phys. Chem. Chem. Phys., Vol. 14, pp. 5178-5186 (2012)). Moreover, Kondo et al. have reported that a perfluorooctanesulfonic acid octadecyl ammonium salt-based protic ionic liquid having large ΔpKa improves durability of a magnetic recording medium (see, for example, &lt;1&gt; Hirofumi Kondo, Makiya Ito, Koki Hatsuda, Kyung Sung Yun and Masayoshi Watanabe, “Novel Ionic Lubricants for Magnetic Thin Film” Media, IEEE TRANSACTIONS ON MAGNETICS, VOL. 49, NO. 7, pp. 3756-3759, JULY (2013), &lt;2&gt; International Publication No. WO2014/104342). In the recent report of Kondo et al. related to thermal resistance of an ionic liquid, it has been reported that a decomposition temperature increases with up to certain degree of ΔpKa, and the decomposition temperature is not increased any further even when ΔpKa is increased from the above-described point (see, for example, &lt;1&gt; Hirofumi Kondo, Makiya Ito, Koki Hatsuda, Nobuo Tano, KyungSung Yun and Masayoshi Watanabe, IEEE International magnetic conference Dresden, Germany, May 4-8, 2014, and &lt;2&gt; Hirofumi Kondo, Makiya Ito, Koki Hatsuda, Nobuo Tano, Kyung Sung Yun and Masayoshi Watanabe, IEEE Trans. Magn., 2014, Vol. 50, Issue 11, Article#: 3302504). Moreover, it is reported that a pyrrolidinium-based ionic liquid including germinal dication may improve thermal resistance more than a typical ionic liquid of monocation (see Anderson, J. L., Ding R., Ellern A., Armstrong D. W., “Structure and Properties of High Stability Geminal Dicationic Ionic Liquids”, J. Am. Chem. Soc., 2005, 127, 593-604). As disclosed in the above literatures (Anderson, J. L., Ding R., Ellern A., Armstrong D. W., “Structure and Properties of High Stability Geminal Dicationiclonic Liquids”, J. Am. Chem. Soc., 2005, 127, 593-604.), however, a relationship between a molecular structure constituting the pyrrolidinium-based ionic liquid and physical or chemical characteristics has not been fully understood yet. A combination of a cation and an anion largely influences on physical or chemical characteristics of an ionic liquid. A variety of the anion site is many, but the relationship is not clear unless the cation is a cation structurally similar to the anion (see, for example, Dzyuba, S. V.; Bartsch, R. A., “Influence of Structural Variations in 1-Alkyl(aralkyl)-3-Methylimidazolium Hexafluorophosphates and Bis(trifluoromethylsulfonyl)imides on Physical Properties of the Ionic Liquids, Chem. Phys. Phys. Chem. 2002, 3, 161-166). For example, viscosity of the liquid increases, as hydrogen bonding strength of halogen is stronger (Cl&gt;Br&gt;I). However, the method for increasing the viscosity is not limited to the increase in the hydrogen bonding strength. For example, the viscosity can be increased by varying an alkyl chain of imidazole. Similarly, the combination of the anion and cation influences on a melting point, surface tension, and thermal stability, but a wide range of researches has not be conducted on an effect of the anion. Accordingly, it is possible to change physical or chemical characteristics of an ionic liquid by with a combination of cations or anions, but it is difficult to predict. 
     In the case where the lubricants for hard disks presented in Table 1 are considered, there is a need for solubility to fluorine-based solvents used in production lines (e.g., special solvent Vertrel available from Du Pont Co.) like in commercially available perfluoropolyethers. Note that, when using fluorine-based solvents, production lines do not need to be explosion proof. Thus, fluorine-based solvents have suitably been used as a solvent used for lubricants in production lines of hard discs. Ionic liquid compounds are easily soluble to polar solvents, but are generally poor in solubility to fluorine-based solvents. As a result, their applications to hard discs have been limited despite their good lubricating properties. 
     SUMMARY OF THE INVENTION 
     The present invention is proposed based on the above-described situations in the art, and provides an ionic liquid having excellent lubricity even at high temperatures and excellent suitability to production lines of magnetic recording media, a lubricant having excellent lubricity even at high temperatures and excellent suitability to production lines of magnetic recording media, and a magnetic recording medium having excellent practical properties. 
     &lt;1&gt; A lubricant including: 
     an ionic liquid including a conjugate base and a conjugate acid, wherein the conjugate acid is represented by General Formula (A) below, and wherein a pKa of an acid that is a source of the conjugate base in acetonitrile is 10 or less, 
     
       
         
         
             
             
         
       
     
     where, in General Formula (A), R is a group including a straight-chain hydrocarbon group having 6 or greater carbon atoms, and R 1  and R 2  are each independently a hydrocarbon group. 
     &lt;2&gt; The lubricant according to &lt;1&gt;, 
     wherein the conjugate base is represented by General Formula (X) or General Formula (Y) below, 
     
       
         
         
             
             
         
       
     
     where, in General Formula (X), 1 is an integer of 1 or greater but 6 or less, and where, in General Formula (Y), 1 is an integer of 1 or greater but 12 or less. 
     &lt;3&gt; A magnetic recording medium including: 
     a non-magnetic support; 
     a magnetic layer disposed on the non-magnetic support; and 
     the lubricant according to &lt;1&gt; or &lt;2&gt;, disposed on the magnetic layer. 
     &lt;4&gt; An ionic liquid including: 
     a conjugate base; and 
     a conjugate acid, 
     wherein the conjugate acid is represented by General Formula (A) below, and wherein a pKa of an acid that is a source of the conjugate base in acetonitrile is 10 or less, 
     
       
         
         
             
             
         
       
     
     where, in General Formula (A), R is a group including a straight-chain hydrocarbon group having 6 or greater carbon atoms, and R 1  and R 2  are each independently a hydrocarbon group. 
     &lt;5&gt; The ionic liquid according to &lt;4&gt;, 
     wherein the conjugate base is represented by General Formula (X) or General Formula (Y) below, 
     
       
         
         
             
             
         
       
     
     where, in General Formula (X), 1 is an integer of 1 or greater but 6 or less, and
 
where, in General Formula (Y), 1 is an integer of 1 or greater but 12 or less.
 
     The present invention can provide an ionic liquid having excellent lubricity even at high temperatures and excellent suitability to production lines of magnetic recording media, a lubricant having excellent lubricity even at high temperatures and excellent suitability to production lines of magnetic recording media, and a magnetic recording medium having excellent practical properties. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is a graph presenting a transition and prediction of an in-plane recording density of a hard disk drive; 
         FIG. 2  is a road map of a head media spacing (HMS) relative to an in-plane recording density of a hard disk; 
         FIG. 3  is a schematic view illustrating thermally-assisted magnetic recording; 
         FIG. 4  is a cross-sectional view illustrating one example of a hard disk according to one embodiment of the present invention; and 
         FIG. 5  is a cross-sectional view illustrating one example of a magnetic tape according to one embodiment of the present invention. 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Embodiments of the present invention are specifically described with reference to drawing hereinafter in the following order. 
     1. Lubricant and ionic liquid
 
2. Magnetic recording medium
 
     3. Examples 
     1. Lubricant and Ionic Liquid 
     A lubricant described as one embodiment of the present invention includes an ionic liquid including a conjugate acid and a conjugate base. 
     An ionic liquid described as one embodiment of the present invention includes a conjugate acid and a conjugate base. 
     In the ionic liquid, the conjugate acid is represented by General Formula (A) below. 
     
       
         
         
             
             
         
       
     
     In General Formula (A), R is a group including a straight-chain hydrocarbon group having 6 or greater carbon atoms, and R 1  and R 2  are each independently a hydrocarbon group. 
     In the ionic liquid, a pKa of an acid that is a source of the conjugate base in acetonitrile is 10 or less. 
     The ionic liquid in the present embodiment includes a conjugate acid and a conjugate base, where a pKa of an acid that is a source of the conjugate base in acetonitrile is 10 or less. Thus, the difference ΔpKa between the acid and the base becomes large and the bond between the ions is strong, which makes it possible for the ionic liquid to exhibit excellent thermal stability. The ionic liquid has a group including a straight-chain hydrocarbon group having 6 or greater carbon atoms in the cation portion and thus also has excellent lubricating properties. In addition, the ionic liquid is an ammonium based on a tertiary amine and thus has been improved in solubility to solvents. Since solubility is improved to CF 3 (CHF) 2 CF 2 CF 3  that is often used as a fluorine-based solvent in a lubricant applying step of hard discs, production lines of magnetic recording media do not need to be explosion proof, as a result. 
     Here, a lubricant containing an ionic liquid is generally used in a state where the concentration of the ionic liquid is about 0.05% by mass. Therefore, solubility of the ionic liquid to fluorine-based solvents needs to be 0.05% by mass or more. Also, depending on the situations where it is used, more solubility may be required. Furthermore, considering, for example, changes in use situations and storage conditions, solubility of 0.1% by mass or more is required [i.e., the ionic liquid is 0.1 parts by mass or more relative to 100 parts by mass of CF 3 (CHF) 2 CF 2 CF 3 ]. 
     The pKa is 10 or less, which is a strong acid, and is preferably 6.0 or less. 
     The lower limit of the pKa is not particularly limited and may be appropriately selected depending on the intended purpose, but the pKa is preferably −5.0 or greater. 
     In the present specification, “pKa” is an acid dissociation constant, and is an acid dissociation constant in acetonitrile. 
     &lt;&lt;Conjugate Base&gt;&gt; 
     The conjugate base is not particularly limited and may be appropriately selected depending on the intended purpose, as long as pKa of an acid that is a source of the conjugate base in acetonitrile is 10 or less. Examples of the conjugate base include a conjugate base represented by General Formula (X) below, a conjugate base represented by General Formula (Y) below, a conjugate base represented by General Formula (U) below, a conjugate base represented by General Formula (V) below, and a conjugate base represented by General Formula (W) below. Among the above-listed examples, a conjugate base represented by General Formula (X) below and a conjugate base represented by General Formula (Y) below are preferable because solubility of the ionic liquid to a solvent becomes high. 
     
       
         
         
             
             
         
       
     
     In General Formula (X), 1 is an integer of 1 or greater but 6 or less, and is preferably an integer of 1 or greater but 4 or less. 
     In General Formula (Y), 1 is an integer of 1 or greater but 12 or less, and is preferably an integer of 1 or greater but 6 or less. 
     As the acid that is a source of the conjugate base (HA), Bronsted acids regarded as super acid, such as bis((perfluoroalkyl)sulfonyl)imide [(C 1 F 21+1 SO 2 ) 2 NH] (pKa=0 to 0.3), perfluorocyclopropane sulfoimide (pKa=−0.8), perfluoroalkyl sulfonic acid (C m F 2m÷1 SO 3 H) (pKa=0.7), tris(perfluoroalkanesulfonyl)methide compounds [(CF 3 SO 2 ) 3 CH] (pKa=−3.7), tricyanomethane (pKa=5.1), inorganic acids [e.g., nitric acid (pKa=9.4) and sulfuric acid (pKa=8.7)], tetrafluoroboric acid (pKa=1.8), and hexafluorophosphate, are preferable. The pKa of the above-listed acids are introduced, for example, in J. Org. Chem. Vol. 76, No. 2, p. 394. 
     &lt;&lt;Conjugate Acid&gt;&gt; 
     The conjugate acid is represented by General Formula (A) below. 
     
       
         
         
             
             
         
       
     
     In General Formula (A), R is a group including a straight-chain hydrocarbon group having 6 or greater carbon atoms, and R 1  and R 2  are each independently a hydrocarbon group. 
     —Substituent R— 
     The number of carbon atoms in the hydrocarbon group is not particularly limited and may be appropriately selected depending on the intended purpose so long as it is 6 or greater. However, it is preferably 10 or greater. 
     The upper limit of the number of carbon atoms in the straight-chain hydrocarbon group having 6 or greater carbon atoms is not particularly limited and may be appropriately selected depending on the intended purpose. The upper limit of the number of carbon atoms is preferably 30 or less, more preferably 25 or less, and particularly preferably 20 or less in view of availability of raw materials. When the hydrocarbon group has a long chain, lubricity can be improved, with reducing a coefficient of friction. 
     The group including a straight-chain hydrocarbon group having 6 or greater carbon atoms is preferably a straight-chain hydrocarbon group having 6 or greater carbon atoms. The group including a straight-chain hydrocarbon group having 6 or greater carbon atoms may include a partially fluorinated hydrocarbon, a branched hydrocarbon, an aromatic ring, and a heterocyclic ring. 
     Since the solubility to solvents tends to be low when the number of carbon atoms is large, the number of carbon atoms of the hydrocarbon group is determined in view of both an effect of reducing a coefficient of friction, and solubility to solvents. 
     The hydrocarbon group may be a saturated hydrocarbon group, or an unsaturated hydrocarbon group partially including a double bond, or an unsaturated branched hydrocarbon group partially including a branched structure, as long as the hydrocarbon group is a straight-chain hydrocarbon group. Among the above-listed examples, an alkyl group, which is a saturated hydrocarbon group, is preferably in view of abrasion resistance. Moreover, the hydrocarbon group is preferably a straight-chain hydrocarbon group that does not include a branched structure even at part. Needless to say that the hydrocarbon group may be a hydrocarbon group partially including a branched structure. 
     —Substituents R 1  and R 2 — 
     The number of carbon atoms in the hydrocarbon group of the R 1  and R 2  is not particularly limited and may be appropriately selected depending on the intended purpose. However, the number of carbon atoms is preferably from 1 to 20, more preferably from 1 to 15. 
     &lt;&lt;Preferable Examples of Ionic Liquid&gt;&gt; 
     Preferable examples of the ionic liquid are an ionic liquid represented by General Formula (1-1) below and an ionic liquid represented by General Formula (1-2) below. 
     
       
         
         
             
             
         
       
     
     In General Formula (1-1), R is a group including a straight-chain hydrocarbon group having 6 or greater carbon atoms, R 1  and R 2  are each independently a hydrocarbon group, and 1 is an integer of 1 or greater but 6 or less. 
     In General Formula (1-2), R is a group including a straight-chain hydrocarbon group having 6 or greater carbon atoms, R 1  and R 2  are each independently a hydrocarbon group, and 1 is an integer of 1 or greater but 12 or less. 
     A preferable scope of R in the general formulae of the ionic liquid is the same as the preferable scope of R in the general formula of the corresponding conjugate acid. 
     Preferable scopes of R 1  and R 2  in the general formulae of the ionic liquid are the same as the preferable scopes of R 1  and R 2  in the general formula of the corresponding conjugate acid. 
     A preferable scope of 1 in the general formulae of the ionic liquid is the same as the preferable scope of 1 in the general formula of the corresponding conjugate base. 
     A synthesis method of the ionic liquid is not particularly limited and may be appropriately selected depending on the intended purpose. For example, various types of the ionic liquid can be synthesized with reference to the method disclosed in Examples below. 
     The lubricant of the present embodiment may use the above-described ionic liquid alone or in combination with a conventional lubricant. Examples of the lubricant used in combination include long-chain carboxylic acid, long-chain carboxylic acid ester, perfluoroalkyl carboxylic acid ester, perfluoroalkyl carboxylate, perfluoroalkyl perfluoroalkylcarboxylate, and a perfluoropolyether derivative. 
     Moreover, an extreme pressure agent may be used in combination at a blending ratio of about 30:70 to about 70:30 in a mass ratio in order to maintain a lubricating effect under severe conditions. The extreme pressure agent reacts with a surface of a metal with friction heat generated when the lubricant is partially in contact with the metal in a boundary lubrication region, and forms a coating film of a reaction product. As a result, friction and abrasion are prevented. As the extreme pressure agent, for example, any of a phosphorus-based extreme pressure agent, a sulfur-based extreme pressure agent, a halogen-based extreme pressure agent, an organic metal-based extreme pressure agent, or a complex extreme pressure agent can be used. 
     Moreover, an anti-rust agent may be optionally used in combination. The anti-rust agent may be any anti-rust agent typically used for this kind of magnetic recording media. Examples of the anti-rust agent include phenols, naphthols, quinones, heterocyclic compounds containing a nitrogen atom, heterocyclic compounds containing an oxygen atom, and heterocyclic compounds containing a sulfur atom. Moreover, the anti-rust agent may be mixed with the lubricant. Alternatively, the anti-rust agent and the lubricant may be deposited as two or more layers by forming a magnetic layer on a non-magnetic support, and applying an anti-rust agent layer on the upper part of the magnetic layer, followed by applying a lubricant layer. 
     As a solvent of the lubricant, for example, a single use or a combination of alcoholic solvents, such as isopropyl alcohol (IPA), and ethanol, can be used. For example, a mixture of a hydrocarbon-based solvent, such as normal-hexane, and a fluorine-based solvent can be used. 
     The solvent is preferably a fluorine-based solvent. Examples of the fluorine-based solvent include hydrofluoroethers [e.g., C 3 F 7 OCH 3 , C 4 F 9 OCH 3 , C 4 F 9 OC 2 H 5 , C 2 F 5 CF(OCH 3 )C 3 F 7 , and CF 3 (CHF) 2 CF 2 CF 3 ]. The fluorine-based solvent may be used as a mixture with alcohol, such as IPA, ethanol, and methanol. 
     The fluorine-based solvent may be a commercially available product. Examples of the commercially available product include: Novec™ 7000, 7100, 7200, 7300, and 71IPA available from 3M Company; and Vertrel XF, and X-P10 available from Du Pont-Mitsui Fluorochemicals Company, Ltd. 
     2. Magnetic Recording Medium 
     Next, a magnetic recording medium using the above-described lubricant is described. A magnetic recording medium described as one embodiment of the present invention includes at least a magnetic layer on a non-magnetic support, and the above-described lubricant is held on the magnetic layer. 
     The lubricant of the present embodiment can be applied for so-called a thin film-metal-type magnetic recording medium, in which a magnetic layer formed on a non-magnetic support by a method, such as vapor deposition and sputtering. Moreover, the lubricant can be also applied for a magnetic recording medium having a structure, in which a base layer is disposed between a non-magnetic support and a magnetic layer. Examples of such a magnetic recording medium include a magnetic disk, and a magnetic tape. 
       FIG. 4  is a cross-sectional view illustrating one example of a hard disk. The hard disk has a structure, in which a substrate  11 , a base layer  12 , a magnetic layer  13 , a protective carbon layer  14 , and a lubricant layer  15  are sequentially laminated. 
     Moreover,  FIG. 5  is a cross-sectional view illustrating one example of a magnetic tape. The magnetic tape has a structure, in which a back-coating layer  25 , a substrate  21 , a magnetic layer  22 , a protective carbon layer  23 , and a lubricant layer  24  are sequentially laminated. 
     In the magnetic disk illustrated in  FIG. 4 , each of the substrate  11  and the base layer  12  corresponds to the non-magnetic support. In the magnetic tape illustrated in  FIG. 5 , the substrate  21  corresponds to the non-magnetic support. In the case where a rigid substrate, such as an Al alloy plate, and a glass plate, is used as the non-magnetic support, a surface of the substrate may be made hard by forming an oxidized film, such as anodizing or a Ni—P coating on the surface of the substrate. 
     Each of the magnetic layers  13  and  22  is formed as a continuous film by a method, such as plating, sputtering, vacuum deposition, and plasma CVD. Examples of the magnetic layers  13  and  22  include: longitudinal magnetic recording metal magnetic films formed of metals (e.g., Fe, Co, and Ni), Co—Ni-based alloys, Co—Pt-based alloys, Co—Ni—Pt-based alloys, Fe—Co-based alloys, Fe—Ni-based alloys, Fe—Co—Ni-based alloys, Fe—Ni—B-based alloys, Fe—Co—B-based alloys, or Fe—Co—Ni—B-based alloys; and perpendicular magnetic recording metal magnetic thin films, such as Co—Cr-based alloy thin films, and Co—O-based thin films. 
     In the case where a longitudinal magnetic recording metal magnetic thin film is formed, particularly, a non-magnetic material, such as Bi, Sb, Pb, Sn, Ga, In, Ge, Si, and Tl, is formed as a base layer  12  on a non-magnetic support in advance, and a metal magnetic material is deposited through vapor deposition or sputtering in a perpendicular direction to diffuse the non-magnetic material into the magnetic metal thin film, to thereby improve a coercive force as well as eliminating orientation to assure in-plane isotropy. 
     Moreover, a hard protective layer  14  or  23 , such as a carbon film, a diamond-formed carbon film, a chromium oxide film, and SiO 2  film, may be formed on a surface of the magnetic layer  13  or  22 . 
     Examples of a method for applying the above-mentioned lubricant to such a metal thin film magnetic recording medium include a method for top-coating a surface of the magnetic layer  13  or  22 , or a surface of the protective layer  14  or  23  with the lubricant, as illustrated in  FIGS. 4 and 5 . A coating amount of the lubricant is preferably from 0.1 mg/m 2  to 100 mg/m 2 , more preferably from 0.5 mg/m 2  to 30 mg/m 2 , and particularly preferably from 0.5 mg/m 2  to 20 mg/m 2 . 
     As illustrated in  FIG. 5 , moreover, a metal thin film magnetic tape may optionally have a back-coating layer  25 , other than a metal magnetic thin film, which is the magnetic layer  22 . 
     The back-coating layer  25  is formed by adding a carbon-based powder for imparting conductivity, or an inorganic pigment for controlling a surface roughness to a resin binder, and applying the resin binder mixture. In the present embodiment, the above-described lubricant may be internally added to the back-coating layer  25 , or applied to the back-coating layer  25  as top coating. Moreover, the above-described lubricant may be internally added to both the magnetic layer  22  and the back-coating layer  25 , or applied to both the magnetic layer  22  and the back-coating layer  25  as top coating. 
     As another embodiment, moreover, the lubricant can be applied for a so-called coating-type magnetic recording medium, in which a magnetic coating film is formed as a magnetic layer by applying a magnetic coating material onto a surface of a non-magnetic support. In the coating-type magnetic recording medium, the non-magnetic support, a magnetic powder constituting the magnetic coating film, and the resin binder for use can be selected from any of those known in the art. 
     Examples of the non-magnetic support include: polymer substrates formed of polymer materials, such as polyesters, polyolefins, cellulose derivatives, vinyl-based resins, polyimides, polyamides, and polycarbonate; metal substrates formed of aluminium alloys, or titanium alloys; ceramic substrates formed of alumina glass; and glass substrates. Moreover, a shape of the non-magnetic support is not particularly limited, and may be any form, such as a tape, a sheet, and a drum. Furthermore, the non-magnetic support may be subjected to a surface treatment to form fine irregularities in order to control surface properties of the non-magnetic support. 
     Examples of the magnetic powder include: ferromagnetic iron oxide-based particles, such as γ-Fe 2 O 3 , cobalt-coated γ-Fe 2 O 3 ; ferromagnetic chromium dioxide; ferromagnetic metal-based particles formed of a metal, such as Fe, Co, and Ni, or an alloy containing any of the above-listed metals; and hexagonal ferrite particles in the form of hexagonal plates. 
     Examples of the resin binder include: polymers, such as vinyl chloride, vinyl acetate, vinyl alcohol, vinylidene chloride, acrylic acid ester, methacrylic acid ester, styrene, butadiene, and acrylonitrile; copolymers combining two or more selected from the above-listed polymers; polyurethane resins; polyester resins; and epoxy resins. In order to improve dispersibility of the magnetic powder, a hydrophilic polar group, such as a carboxylic acid group, a carboxyl group, and a phosphoric acid group, may be introduced into any of the above-listed binders. 
     Other than the magnetic powder and the resin binder, additives, such as a dispersing agent, an abrasive, an antistatic agent, and an anti-rust agent, may be added to the magnetic coating film. 
     As a method for retaining the above-described lubricant in the coating-type magnetic recording medium, there are a method where the lubricant is internally added to the magnetic layer constituting the magnetic coating film formed on the non-magnetic support, a method where the lubricant is applied on a surface of the magnetic layer as top coating, and a combination of the above-listed methods. In the case where the lubricant is internally added into the magnetic coating film, the lubricant is added in an amount of from 0.2 parts by mass to 20 parts by mass relative to 100 parts by mass of the resin binder. 
     In the case where a surface of the magnetic layer is top-coated with the lubricant, moreover, a coating amount of the lubricant is preferably from 0.1 mg/m 2  to 100 mg/m 2 , and more preferably from 0.5 mg/m 2  to 20 mg/m 2 . As a deposition method in the case where the lubricant is applied as top coating, the ionic liquid is dissolved in a solvent, and the obtained solution may be applied or sprayed, or a magnetic recording medium may be dipped in the solution. 
     The magnetic recording medium, to which the lubricant of the present embodiment is applied, exhibits excellent running performances, abrasion resistance, and durability because of a lubricating effect, and can further improve thermal stability. 
     EXAMPLES 
     3. Examples 
     Specific examples of the present invention are explained below. In the examples, ionic liquids were synthesized, and lubricants including the ionic liquids were produced. Then, solubility of the ionic liquids to Vertrel [CF 3 (CHF) 2 CF 2 CF 3 ], which was a fluorine-based solvent were determined. Then, the lubricant solutions were applied surfaces of the magnetic disks and magnetic tapes and durability of each disk and durability of each tape were evaluated. Production of a magnetic disk, a durability test of the disk, production of a magnetic tape, and a durability test of the tape were performed in the following manner. Note that, the present invention is not limited to these examples. 
     &lt;Production of Magnetic Disk&gt; 
     A magnetic thin film was formed on a glass substrate to produce a magnetic disk as illustrated in  FIG. 4 , for example, according to International Publication No. WO2005/068589. Specifically, a chemically reinforced glass disk, which was formed of aluminium silicate glass and had an outer diameter of 65 mm, an inner diameter of 20 mm, and a disk thickness of 0.635 mm, was prepared, and a surface of the glass disk was polished so that Rmax of the surface was to be 4.8 nm, and Ra of the surface was to be 0.43 nm. The glass substrate was subjected to ultrasonic cleaning for 5 minutes each in pure water and in isopropyl alcohol (IPA) having the purity of 99.9% or greater, and the washed glass substrate was left to stand in saturated IPA steam for 1.5 minutes, followed by drying. The resultant glass substrate was provided as a substrate  11 . 
     On the substrate  11 , a NiAl alloy (Ni: 50 mol %, Al: 50 mol %) thin film in the thickness of 30 nm as a seed layer, a CrMo alloy (Cr: 80 mol %, Mo: 20 mol %) thin film in the thickness of 8 nm as a base layer  12 , and a CoCrPtB alloy (Co: 62 mol %, Cr: 20 mol %, Pt: 12 mol %, B: 6 mol %) thin film in the thickness of 15 nm as a magnetic layer  13  were sequentially formed by DC magnetron sputtering. 
     Subsequently, a 5 nm-thick protective carbon layer  14  formed of amorphous diamond-like carbon was formed by plasma CVD, and the resultant disk sample was subjected to ultrasonic cleaning for 10 minutes in isopropyl alcohol (IPA) having the purity of 99.9% or greater inside a cleaner to remove impurities on a surface of the disk, followed by drying. Thereafter, a n-hexane/ethanol mixed solution of an ionic liquid was applied on a surface of the disk by dip coating in the environment of 25° C. and 50% in relative humidity (RH), to form about 1 nm of a lubricant layer  15 . 
     &lt;Measurement of Thermal Stability&gt; 
     In the TG/DTA measurement, the measurement was performed by means of EXSTAR6000 available from Seiko Instruments Inc. at a temperature range of from 30° C. to 600° C. at a heating rate of 10° C./min with introducing air at a flow rate of 200 mL/min. 
     The endothermic peak temperature in the measurement was defined as a melting point. 
     &lt;Disk Durability Test&gt; 
     A CSS durability test was performed by means of a commercially available strain-gauge-type disk friction-abrasion tester in the following manner. A hard disk was mounted on a rotatable spindle with tightening torque of 14.7 Ncm. Thereafter, a head slider was attached on the hard disk in a manner that a center of an air bearing surface at the inner circumference side of the head slider relative to the hard disk was 17.5 mm from a center of the hard disk. The head used for the measurement was an IBM3370-type inline head, a material of the slider was Al 2 O 3 —TiC, and the head load was 63.7 mN. In the test, the maximum value of friction force was monitored per CSS (contact, start, and stop) in the environment of 100 in cleanliness, 25° C., and 60% RH. The number of times when a coefficient of friction was greater than 1.0 was determined as a result of the CSS durability test. When a result of the CSS durability test was greater than 50,000, the result was represented as “&gt;50,000.” Moreover, a CSS durability test was similarly performed after performing a heating test for 3 minutes at a temperature of 300° C., in order to study heat resistance. 
     &lt;Production of Magnetic Tape&gt; 
     A magnetic tape having a cross-sectional structure as illustrated in  FIG. 5  was produced. First, Co was deposited on a substrate  21  formed of a 5 μm-thick MICTRON (aromatic polyamide) film available from TORAY INDUSTRIES, INC. by oblique deposition to form a magnetic layer  22  formed of a ferromagnetic metal thin film having a film thickness 100 nm. Next, a protective carbon layer  23  formed of a 10 nm-thick diamond-like carbon was formed on a surface of the ferromagnetic metal thin film by plasma CVD, followed by cutting the resultant into a strip having a width of 6 mm. An ionic liquid dissolved in IPA was applied onto the protective carbon layer  23  in a manner that a film thickness of the ionic liquid solution was about 1 nm. In this manner, a lubricant layer  24  is formed on the magnetic layer to thereby produce a sample tape. 
     &lt;Tape Durability Test&gt; 
     Each sample tape was subjected to a measurement of still durability in an environment having a temperature of −5° C. and in an environment having a temperature of 40° C. and 30% RH, and measurements of a coefficient of friction and shuttle durability in an environment having a temperature of −5° C. and in an environment having a temperature of 40° C. and 90% RH. The still durability was evaluated by a decay time of an output in a paused state decayed by −3 dB. The shuttle resistant was evaluated by the number of shuttles taken until an output was reduced by 3 dB when repeated shuttle run was performed for 2 minutes per time. Moreover, a durability test was similarly performed after performing a heating test for 10 minutes at a temperature of 100° C., in order to study heat resistance. 
     The ionic liquid in the present embodiment includes a conjugate base and a conjugate acid, where a pKa of an acid that is a source of the conjugate base in acetonitrile is 10 or less. Moreover, the ionic liquid uses, in the conjugate acid (the cation portion), a tertiary amine having a group including a hydrocarbon group having 6 or greater carbon atoms. Thermal stability of the ionic liquid and durability of magnetic recording media using the ionic liquid were studied. In addition, solubility to fluorine-based solvents was also studied. 
     In the present specification, the measurement of FTIR was performed by means of FT/IR-460 available from JASCO Corporation according to a transmission method using KBr plates or KBr pellets. The resolution of the measurement was 1 cm −1 . 
     The  1 H-NMR and  13 C-NMR spectra were measured by means of Varian Mercury Plus 300 nuclear magnetic resonance spectrometer (available from Varian, Inc.). A chemical shift of  1 HNMR was represented with ppm comparing with an internal standard (TMS or deuterated solvent peak at 0 ppm). Splitting patterns were presented by denoting a singlet as s, a doublet as d, a triplet as t, a quartet as q, a quintet as quint, a multiplet as m, and a broad peak as br. 
     Example 1A 
     Synthesis of bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-octadecyl ammonium 
     A synthesis of bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-octadecyl ammonium was performed according to the following scheme. 
     
       
         
         
             
             
         
       
     
     N,N-Dimethyloctadecylamine was dissolved in ethanol, and an ethanol solution of an equimolar amount of bis(nonafluorobutanesulfonyl)imide was added thereto. The resultant was heated under reflux for 1 hour. After cooling, the solvent was removed. The residue was extracted with dichloromethane, and the organic layer was sufficiently washed with water. After drying the resultant with anhydrous sodium sulfate, the solvent was removed to thereby obtain colorless crystals of bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-octadecyl ammonium. The yield was 91.1%. 
     The FTIR absorbance peaks of the product and the assignments are presented below. 
     The symmetric stretching vibrations of SO 2  bonds were observed at 1,080 cm −1 , the symmetric stretching vibrations of CF 2  were observed at 1,158 cm −1 , 1,197 cm −1 , and 1,234 cm −1 , the asymmetric stretching vibrations of SO 2  bonds were observed at 1,356 cm −1 , the bending vibrations of CH 2  bonds were observed at 1,471 cm −1 , the symmetric stretching vibrations of CH 2  bonds were observed at 2,853 cm −1 , the asymmetric stretching vibrations of CH 2  bonds were observed at 2,922 cm −1 , and the NH stretching vibrations were observed at 3,170 cm −1 . 
     Peaks of the proton ( 1 H)NMR and carbon ( 13 C)NMR in CDCl 3  of the obtained compound are presented below. 
       1 H-NMR (CDCl 3 , δ ppm); 0.857 (t/J=6.8 Hz, 3H), 1.180-1.350 (m, 30H), 1.661-1.739 (m, 2H), 2.859 (d/J=5.2 Hz, 6H), 2.990-3.046 (m, 2H), 7.703 (brs, 1H) 
       13 C-NMR(CDCl 3 , δ ppm); 14.089, 22.675, 24.266, 26.212, 28.923, 29.220, 29.345, 29.403, 29.518, 29.613, 29.642, 29.680, 31.913, 43.815, 59.186 
     The product was determined as bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-octadecyl ammonium from the spectra above. 
     Note that, a pKa of an acid [bis(nonafluorobutanesulfonyl)imide] that was a source of the conjugate base in the bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-octadecyl ammonium was 0.0 in acetonitrile. 
     Example 2A 
     Synthesis of bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-dodecyl ammonium 
     A synthesis of bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-dodecyl ammonium was performed according to the following scheme. 
     
       
         
         
             
             
         
       
     
     N,N-Dimethyldodecylamine was dissolved in ethanol, and an ethanol solution of an equimolar amount of bis(nonafluorobutanesulfonyl)imide was added thereto. The resultant was heated under reflux for 1 hour. After cooling, the solvent was removed. The residue was extracted with dichloromethane, and the organic layer was sufficiently washed with water. After drying the resultant with anhydrous sodium sulfate, the solvent was removed to thereby obtain colorless crystals of bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-dodecyl ammonium. The yield was 96.1%. 
     The FTIR absorbance peaks of the product and the assignments are presented below. 
     The symmetric stretching vibrations of SO 2  bonds were observed at 1,157 cm −1 , the symmetric stretching vibrations of CF 2  were observed at 1,197 cm −1 , 1,216 cm −1 , and 1,233 cm −1 , the asymmetric stretching vibrations of SO 2  bonds were observed at 1,355 cm −1 , the bending vibrations of CH 2  bonds were observed at 1,480 cm −1 , the symmetric stretching vibrations of CH 2  bonds were observed at 2,857 cm −1 , the asymmetric stretching vibrations of CH 2  bonds were observed at 2,927 cm −1 , and the NH stretching vibrations were observed at 3,172 cm −1 . 
     Peaks of the proton ( 1 H)NMR and carbon ( 13 C)NMR in CDCl 3  of the obtained compound are presented below. 
       1 H-NMR (CDCl 3 , δ ppm); 0.852 (t/J=7.0 Hz, 3H), 1.180-1.350 (m, 18H), 1.640-1.740 (m, 2H), 2.855 (d/J=4.8 Hz), 2.990-3.045 (m, 2H), 7.629 (brs, 1H) 
       13 C-NMR (CDCl 3 , δ ppm); 14.051, 22.637, 24.285, 26.164, 28.904, 29.201, 29.268, 29.374, 29.489, 29.537, 31.856, 43.767, 59.119 
     The product was determined as bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-dodecyl ammonium from the spectra above. 
     Note that, a pKa of an acid [bis(nonafluorobutanesulfonyl)imide] that was a source of the conjugate base in the bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-dodecyl ammonium was 0.0 in acetonitrile. 
     Example 3A 
     Synthesis of trifluoromethanesulfonic acid-N,N,N-tridodecyl ammonium 
     A synthesis of trifluoromethanesulfonic acid-N,N,N-tridodecyl ammonium was performed according to the following scheme. 
     
       
         
         
             
             
         
       
     
     N,N,N-tridodecylamine was dissolved in ethanol, and an ethanol solution of an equimolar amount of trifluoromethanesulfonic acid was added thereto. The resultant was heated under reflux for 1 hour. After cooling, the solvent was removed. The residue was extracted with dichloromethane, and the organic layer was sufficiently washed with water. After drying the resultant with anhydrous sodium sulfate, the solvent was removed to thereby obtain trifluoromethanesulfonic acid-N,N,N-tridodecyl ammonium. The yield was 95.1%. 
     The FTIR absorbance peaks of the product and the assignments are presented below: 
     The symmetric stretching vibrations of SO 2  bonds were observed at 1,031 cm −1 , the symmetric stretching vibrations of CF 3  were observed at 1,160 cm −1  and 1284 cm −1 , the bending vibrations of CH 2  bonds were observed at 1,467 cm −1 , the symmetric stretching vibrations of CH 2  bonds were observed at 2,855 cm −1 , the asymmetric stretching vibrations of CH 2  bonds were observed at 2,924 cm −1 , and the NH stretching vibrations were observed at 3,060 cm −1 . 
     Peaks of the proton ( 1 H)NMR and carbon ( 13 C)NMR in CDCl 3  of the obtained compound are presented below. 
       1 H-NMR (CDCl 3 , δ ppm); 0.857 (t/J=6.8 Hz, 9H), 1.200-1.360 (m, 54H), 1.648-1.705 (m, 6H), 2.968-3.022 (m, 6H), 8.947 (brs, 1H) 
       13 C-NMR (CDCl 3 , δ ppm); 14.080, 22.656, 23.327, 26.585, 28.971, 29.288, 29.412, 29.556, 31.875, 52.976 
     The product was determined as trifluoromethanesulfonic acid-N,N,N-tridodecyl ammonium from the spectra above. 
     Note that, a pKa of an acid [trifluoromethanesulfonic acid] that was a source of the conjugate base in the trifluoromethanesulfonic acid-N,N,N-tridodecyl ammonium was 0.7 in acetonitrile. 
     Comparative Example 1A 
     Synthesis of nonafluorobutanesulfonic acid-octadecyl ammonium 
     A synthesis of nonafluorobutanesulfonic acid-octadecyl ammonium was performed according to the following scheme. 
     
       
         
         
             
             
         
       
     
     Octadecylamine was dissolved in ethanol, and an ethanol solution of an equimolar amount of nonafluorobutanesulfonic acid was added thereto. The resultant was heated under reflux for 1 hour. After cooling, the solvent was removed. The residue was extracted with dichloromethane, and the organic layer was sufficiently washed with water. After drying the resultant with anhydrous sodium sulfate, the solvent was removed and the resultant was recrystallized from a mixed solvent of n-hexane and ethanol, to thereby obtain colorless crystals of nonafluorobutanesulfonic acid-octadecyl ammonium. The yield was 95.0%. 
     The FTIR absorbance peaks of the product and the assignments are presented below. 
     The symmetric stretching vibrations of SO 2  bonds were observed at 1,136 cm −1 , the symmetric stretching vibrations of CF 2  were observed at 1,252 cm −1 , the asymmetric stretching vibrations of SO 2  bonds were observed at 1,355 cm −1 , the bending vibrations of CH 2  bonds were observed at 1,471 cm −1 , the out-of-plane bending vibrations of NH 4   +  were observed at 1,625 cm −1 , the symmetric stretching vibrations of CH 2  bonds were observed at 2,850 cm −1 , the asymmetric stretching vibrations of CH 2  bonds were observed at 2,920 cm −1 , and the NH stretching vibrations were observed at 3,184 cm −1 . 
     Peaks of the proton ( 1 H)NMR and carbon ( 13 C)NMR in CD 3 OD of the obtained compound are presented below. 
       1 H-NMR (CD 3 OD, δ ppm); 0.890 (t/J=6.8 Hz, 3H), 1.225-1.400 (m, 30H), 1.639 (quint/J=7.5 Hz, 2H), 2.900 (t/J=7.5 Hz, 2H), 4.840 (brs) 
       13 C-NMR (CD 3 OD, δ ppm); 14.444, 23.740, 27.433, 28.547, 30.226, 30.486, 30.654, 30.791, 33.081, 40.804 
     The product was determined as nonafluorobutanesulfonic acid-octadecyl ammonium from the spectra above. 
     Note that, a pKa of an acid (nonafluorobutanesulfonic acid) that was a source of the conjugate base in the nonafluorobutanesulfonic acid-octadecyl ammonium was 0.7 in acetonitrile. 
     Comparative Example 2A 
     Synthesis of bis(nonafluorobutanesulfonyl)imide-octadecyl ammonium 
     For comparison, a synthesis of bis(nonafluorobutanesulfonyl)imide-octadecyl ammonium was performed according to the following scheme. 
     
       
         
         
             
             
         
       
     
     Octadecylamine was dissolved in ethanol, and an ethanol solution of an equimolar amount of bis(nonafluorobutanesulfonyl)imide was added thereto. The resultant was heated under reflux for 1 hour. After cooling, the solvent was removed. The residue was extracted with dichloromethane, and the organic layer was sufficiently washed with water. After drying the resultant with anhydrous sodium sulfate, the solvent was removed and the resultant was recrystallized from a mixed solvent of n-hexane and ethanol, to thereby obtain colorless crystals of bis(nonafluorobutanesulfonyl)imide-octadecyl ammonium. The yield was 95.0%. 
     The FTIR absorbance peaks of the product and the assignments are presented below. 
     The asymmetric stretching vibrations of SNS bonds were observed at 1,031 cm −1 , the symmetric stretching vibrations of CF were observed at 1,141 cm −1  and 1,200 cm −1 , the asymmetric stretching vibrations of SO 2  bonds were observed at 1,355 cm −1 , the bending vibrations of CH 2  bonds were observed at 1,471 cm −1 , the out-of-plane bending vibrations of NH 3   +  were observed at 1,616 cm −1 , the symmetric stretching vibrations of CH 2  bonds were observed at 2,856 cm −1 , the asymmetric stretching vibrations of CH 2  bonds were observed at 2,926 cm −1 , and the NH 3  stretching vibrations were observed at 3,248 cm −1 . 
     Peaks of the proton ( 1 H)NMR and carbon ( 13 C)NMR in CD 3 OD of the obtained compound are presented below. 
       1 H-NMR (CD 3 OD, δ ppm); 0.889 (t/J=6.8 Hz, 3H), 1.225-1.400 (m, 30H), 1.635 (m, 2H), 2.896 (t/J=7.5 Hz, 2H), 4.867 (brs) 
       13 C-NMR (CD 3 OD, δ ppm); 14.414, 23.709, 27.403, 28.563, 30.196, 30.471, 30.623, 30.776, 33.065, 40.819 
     The product was determined as bis(nonafluorobutanesulfonyl)imide-octadecyl ammonium from the spectra above. 
     Note that, a pKa of an acid [bis(nonafluorobutanesulfonyl)imide] that was a source of the conjugate base in the bis(nonafluorobutanesulfonyl)imide-octadecyl ammonium was 0.0 in acetonitrile. 
     Comparative Example 3A 
     Synthesis of hexafluorocyclopropane-1,3-bis(sulfonyl)imide-octadecyl ammonium 
     Hexafluorocyclopropane-1,3-bis(sulfonyl)imide-octadecyl ammonium was synthesized according to the following scheme 1. 
     
       
         
         
             
             
         
       
     
     Octadecylamine was dissolved in ethanol, and an ethanol solution of an equimolar amount of hexafluorocyclopropane-1,3-bis(sulfonyl)imide was added thereto. The resultant was heated under reflux for 1 hour. After cooling, the solvent was removed. The residue was extracted with dichloromethane, and the organic layer was sufficiently washed with water. After drying the resultant with anhydrous sodium sulfate, the solvent was removed and the resultant was recrystallized from a mixed solvent of n-hexane and ethanol, to thereby obtain colorless crystals of hexafluorocyclopropane-1,3-bis(sulfonyl)imide-octadecyl ammonium. The yield was 93.2%. 
     The FTIR absorbance peaks of the product and the assignments are presented below. 
     The asymmetric stretching vibrations of SNS bonds were observed at 1,043 cm −1 , the symmetric stretching vibrations of SO 2  bonds were observed at 1,096 cm −1 , the symmetric stretching vibrations of CF were observed at 1,154 cm −1  and 1,188 cm −1 , the asymmetric stretching vibrations of SO 2  bonds were observed at 1,348 cm −1 , the bending vibrations of CH 2  bonds were observed at 1,471 cm −1 , the out-of-plane bending vibrations of NH 3   +  were observed at 1,608 cm −1 , the symmetric stretching vibrations of CH 2  bonds were observed at 2,850 cm −1 , the asymmetric stretching vibrations of CH 2  bonds were observed at 2,920 cm −1 , and the NH 3  stretching vibrations were observed at 3,186 cm −1  and 3,245 cm −1 . 
     Peaks of the proton ( 1 H)NMR and carbon ( 13 C)NMR in CD 3 OD of the obtained compound are presented below. 
       1 H-NMR (CD 3 OD, δ ppm); 0.889 (t/J=6.8 Hz, 3H), 1.225-1.400 (m, 30H), 1.634 (quint/J=7.5 Hz, 2H), 2.898 (t/J=7.5 Hz, 2H), 4.883 (brs) 
       13 C-NMR (CD 3 OD, δ ppm); 14.444, 23.709, 27.372, 28.532, 30.181, 30.455, 30.608, 30.761, 33.050, 40.804 
     The product was determined as hexafluorocyclopropane-1,3-bis(sulfonyl)imide-octadecyl ammonium from the spectra above. 
     Note that, a pKa of an acid [hexafluorocyclopropane-1,3-bis(sulfonyl)imide] that was a source of the conjugate base in the hexafluorocyclopropane-1,3-bis(sulfonyl)imide-octadecyl ammonium was −0.8 in acetonitrile. 
     Comparative Example 4A 
     Synthesis of nonafluorobutanesulfonic acid-N-methyloctadecyl ammonium 
     Nonafluorobutanesulfonic acid-N-methyloctadecyl ammonium was synthesized according to the following scheme. 
     
       
         
         
             
             
         
       
     
     N-Methyloctadecylamine was dissolved in ethanol, and an ethanol solution of an equimolar amount of nonafluorobutanesulfonic acid was added thereto. The resultant was heated under reflux for 1 hour. After cooling, the solvent was removed. The residue was extracted with dichloromethane, and the organic layer was sufficiently washed with water. After drying the resultant with anhydrous sodium sulfate, the solvent was removed and the resultant was recrystallized from a mixed solvent of n-hexane and ethanol, to thereby obtain colorless crystals of nonafluorobutanesulfonic acid-N-methyloctadecyl ammonium. The yield was 92.1%. 
     The FTIR absorbance peaks of the product and the assignments are presented below. 
     The symmetric stretching vibrations of SO 2  bonds were observed at 1,136 cm −1 , the symmetric stretching vibrations of CF 2  were observed at 1,231 cm −1  and 1,266 cm −1 , the asymmetric stretching vibrations of SO 2  bonds were observed at 1,355 cm −1 , the bending vibrations of CH 2  bonds were observed at 1,473 cm −1 , the symmetric stretching vibrations of CH 2  bonds were observed at 2,851 cm −1 , the asymmetric stretching vibrations of CH 2  bonds were observed at 2,917 cm −1 , and the NH 2   +  stretching vibrations were observed at 3,078 cm −1 . 
     Peaks of the proton ( 1 H)NMR and carbon ( 13 C)NMR in CDCl 3  of the obtained compound are presented below. 
       1 H-NMR (CD 3 OD, δ ppm); 0.864 (t/J=6.8 Hz, 3H), 1.180-1.390 (m, 30H), 1.699 (quint/J=7.7 Hz, 2H), 2.726 (t/J=5.6 Hz, 3H), 2.918-2.987 (m, 2H), 7.537 (brs, 2H) 
       13 C-NMR (CDCl 3   − , δ ppm); 14.041, 22.675, 25.675, 26.259, 28.962, 29.278, 29.345, 29.479, 29.575, 29.661, 29.700, 31.932, 33.581, 50.168 
     The product was determined as nonafluorobutanesulfonic acid-N-methyloctadecyl ammonium from the spectra above. 
     Note that, a pKa of an acid (nonafluorobutanesulfonic acid) that was a source of the conjugate base in the nonafluorobutanesulfonic acid-N-methyloctadecyl ammonium was 0.7 in acetonitrile. 
     Comparative Example 5A 
     Synthesis of nonafluorobutanesulfonic acid-trimethyloctadecyl ammonium 
     Nonafluorobutanesulfonic acid-trimethyloctadecyl ammonium was synthesized according to the following scheme. 
     
       
         
         
             
             
         
       
     
     In water, 5.51 g of trimethyloctadecyl ammonium bromide was dissolved. The resultant solution was added to an aqueous solution of 4.61 g of lithium nonafluorobutanesulfonate. The resultant was heated under reflux for 1 hour. The precipitates formed after cooling were extracted with dichloromethane, followed by sufficiently washing with water until a result of the AgNO 3  test of the wash liquid became negative. After drying the organic layer with anhydrous sodium sulfate, the solvent was removed to thereby obtain 8.14 g of colorless crystals of nonafluorobutanesulfonic acid-trimethyloctadecyl ammonium. The yield was 94.8%. The resultant was recrystallized from a mixed solvent of n-hexane and ethanol. 
     The FTIR absorbance peaks of the product and the assignments are presented below. 
     The symmetric stretching vibrations of SO 2  bonds were observed at 1,133 cm −1 , the symmetric stretching vibrations of CF 2  were observed at 1,263 cm −1 , the asymmetric stretching vibrations of SO 2  bonds were observed at 1,353 cm −1 , the bending vibrations of CH 2  bonds were observed at 1,485 cm −1 , the symmetric stretching vibrations of CH 2  bonds were observed at 2,852 cm −1 , and the asymmetric stretching vibrations of CH 2  bonds were observed at 2,920 cm −1 . 
     Peaks of the proton ( 1 H)NMR and carbon ( 13 C)NMR in CD 3 OD of the obtained compound are presented below. 
       1 H-NMR (CD 3 OD, δ ppm); 0.851 (t/J=6.8 Hz, 3H), 1.170-1.340 (m, 30H), 1.640-1.730 (m, 2H), 3.181 (s, 9H), 3.291-3.334 (m, 2H) 
       13 C-NMR (CDCl 3 , δ ppm); 14.089, 22.666, 23.068, 25.972, 29.067, 29.316, 29.335, 29.412, 29.565, 29.680, 31.904, 53.043, 66.996 
     The product was determined as nonafluorobutanesulfonic acid-trimethyloctadecyl ammonium from the spectra above. 
     Note that, a pKa of an acid (nonafluorobutanesulfonic acid) that was a source of the conjugate base in the nonafluorobutanesulfonic acid-trimethyloctadecyl ammonium was 0.7 in acetonitrile. 
     Comparative Example 6A 
     Synthesis of pentadecafluorooctanoic acid octadecyl ammonium 
     For comparison, a synthesis of pentadecafluorooctanoic acid octadecyl ammonium was performed according to the following scheme. 
       C 7 F 15 —COOH+C 18 H 37 —NH 2 →C 7 F 15 —COO − H 3 N + —C 18 H 37  
 
     In ethanol, 4.14 g of pentadecafluorooctanoic acid and 2.69 g of octadecylamine were added, and the resultant mixture was heated under reflux for 1 h. After removing the solvent from the resultant, the resultant was recrystallized from a mixed solvent of n-hexane and ethanol, to thereby obtain 6.23 g of colorless plate crystals. The yield was 92.0%. 
     The FTIR absorbance peaks of the product and the assignments are presented below. 
     The symmetric stretching vibrations of CF 2  were observed at 1,141 cm −1 , 1,201 cm −1 , and 1,232 cm −1 , the bending vibrations of CH 2  were observed at 1,473 cm −1 , the stretching vibrations of C═O were observed at 1,677 cm −1 , the symmetric stretching vibrations of CH 2  were observed at 2,851 cm −1 , the asymmetric stretching vibrations of CH 2  were observed at 2,918 cm −1 , and the stretching vibrations of NH 3   +  were observed in the range between 3,000 cm −1  and 3,325 cm −1 . 
     Moreover, peaks of the proton ( 1 H)NMR and carbon ( 13 C)NMR in deuterated chloroform are presented below. 
       1 H-NMR (CD 3 OD, δ ppm); 0.890 (t/J=6.6 Hz, 3H), 1.214-1.408 (m, 30H), 1.590-1.690 (m, 2H), 2.896 (t/J=7.5 Hz, 2H), 4.891 (brs, 1H) 
       13 C-NMR (CD 3 OD, δ ppm); 14.444, 23.740, 27.464, 28.578, 30.242, 30.486, 30.516, 30.669, 30.791, 33.081, 40.758 
     The product was determined as pentadecafluorooctanoic acid octadecyl ammonium from the spectra above. 
     Note that, a pKa of an acid [pentadecafluorooctanoic acid] that was a base of the conjugate base in the pentadecafluorooctanoic acid octadecyl ammonium was 12.7 in acetonitrile. 
     The ionic liquids synthesized in Examples and Comparative Examples above are summarized below. 
     
       
         
         
             
             
         
       
     
     Example 1B to Example 3B and Comparative Example 1B to Comparative Example 8B 
     &lt;Solubility Measurement Results to Solvents&gt; 
     Solubility tests were performed on the ionic liquids synthesized in Examples and Comparative Examples, Z-DOL, and Z-TETRAOL, using, as a fluorine-based solvent, Vertrel XF [CF 3 (CHF) 2 CF 2 CF 3 ] available from Du Pont-Mitsui Fluorochemicals Company, Ltd., and special grade chemical n-hexane and ethanol available from JUNSEI CHEMICAL CO., LTD. 
     To a predetermined amount of Vertrel XF, n-hexane, or ethanol, the ionic liquid was added. Ultrasonic waves were applied to the resultant mixture for 5 minutes, followed by leaving the mixture to stand for 1 day. The solubility was visually observed. 
     Specifically, 0.2 parts by mass of each ionic liquid, Z-DOL, or Z-TETRAOL was added to 100 parts by mass of Vertrel XF (25° C.). After applying ultrasonic waves to the resultant for 5 minutes, the resultant was left to stand for 1 day. Thereafter, the solubility was visually observed and evaluated based on the following evaluation criteria. 
     In the case of n-hexane or ethanol, similarly, 0.5 parts by mass of each ionic liquid, Z-DOL, or Z-TETRAOL was added to 100 parts by mass of n-hexane at 25° C. Similarly, after applying ultrasonic waves to the resultant for 5 minutes, the resultant was left to stand for 1 day. Thereafter, the solubility was visually observed and evaluated based on the following evaluation criteria. 
     Note that, the solubility was visually observed, and it was judged as soluble when it was transparent. Moreover, it was judged as not soluble (insoluble) when it was opaque or insoluble components were observed. 
     The results are presented in Table 2. 
     [Evaluation Criteria] 
     &lt;&lt;Vertrel XF&gt;&gt; 
     
         
         
           
             0.2% by mass or greater: 
           
         
       
    
     Soluble with addition of 0.2 parts by mass
         Less than 0.2% by mass:       

     Insoluble with addition of 0.2 parts by mass 
     &lt;&lt;n-Hexane and Ethanol&gt;&gt;
         0.5% by mass or greater:       

     Soluble with addition of 0.5 parts by mass
         Less than 0.5% by mass:       

     Insoluble with addition of 0.5 parts by mass 
     
       
         
           
               
               
             
               
                   
                 TABLE 2 
               
             
            
               
                   
                   
               
               
                   
                 Solubility 
               
            
           
           
               
               
               
               
               
            
               
                   
                 Synthesized 
                 Fluorine-based 
                   
                   
               
               
                 Examples 
                 product 
                 solvent 
                 n-Hexane 
                 Ethanol 
               
               
                   
               
               
                 Ex. 1B 
                 Ex. 1A 
                 0.2% by mass or 
                 0.5% by mass or 
                 0.5% by mass or 
               
               
                   
                   
                 greater 
                 greater 
                 greater 
               
               
                 Ex. 2B 
                 Ex. 2A 
                 0.2% by mass or 
                 0.5% by mass or 
                 0.5% by mass or 
               
               
                   
                   
                 greater 
                 greater 
                 greater 
               
               
                 Ex. 3B 
                 Ex. 3A 
                 0.2% by mass or 
                 0.5% by mass or 
                 0.5% by mass or 
               
               
                   
                   
                 greater 
                 greater 
                 greater 
               
               
                 Comp. Ex. 1B 
                 Comp. Ex. 1A 
                 less than 0.2% by 
                 less than 0.5% by 
                 0.5% by mass or 
               
               
                   
                   
                 mass 
                 mass 
                 greater 
               
               
                 Comp. Ex. 2B 
                 Comp. Ex. 2A 
                 less than 0.2% by 
                 less than 0.5% by 
                 0.5% by mass or 
               
               
                   
                   
                 mass 
                 mass 
                 greater 
               
               
                 Comp. Ex. 3B 
                 Comp. Ex. 3A 
                 less than 0.2% by 
                 less than 0.5% by 
                 0.5% by mass or 
               
               
                   
                   
                 mass 
                 mass 
                 greater 
               
               
                 Comp. Ex. 4B 
                 Comp. Ex. 4A 
                 less than 0.2% by 
                 less than 0.5% by 
                 0.5% by mass or 
               
               
                   
                   
                 mass 
                 mass 
                 greater 
               
               
                 Comp. Ex. 5B 
                 Comp. Ex. 5A 
                 less than 0.2% by 
                 less than 0.5% by 
                 0.5% by mass or 
               
               
                   
                   
                 mass 
                 mass 
                 greater 
               
               
                 Comp. Ex. 6B 
                 Comp. Ex. 6A 
                 less than 0.2% by 
                 0.5% by mass or 
                 0.5% by mass or 
               
               
                   
                   
                 mass 
                 greater 
                 greater 
               
               
                 Comp. Ex. 7B 
                 Z-DOL 
                 0.2% by mass or 
                 less than 0.5% by 
                 less than 0.5% by 
               
               
                   
                   
                 greater 
                 mass 
                 mass 
               
               
                 Comp. Ex. 8B 
                 Z-TETRAOL 
                 0.2% by mass or 
                 less than 0.5% by 
                 less than 0.5% by 
               
               
                   
                   
                 greater 
                 mass 
                 mass 
               
               
                   
               
            
           
         
       
     
     The solubility of the ionic liquid of Example 1A was 0.2% by mass or greater to the fluorine-based solvent, 0.5% by mass or greater to n-hexane, and 0.5% by mass or greater to ethanol. 
     The solubility of the ionic liquid of Example 2A was 0.2% by mass or greater to the fluorine-based solvent, 0.5% by mass or greater to n-hexane, and 0.5% by mass or greater to ethanol. 
     The solubility of the ionic liquid of Example 3A was 0.2% by mass or greater to the fluorine-based solvent, 0.5% by mass or greater to n-hexane, and 0.5% by mass or greater to ethanol. 
     The solubility of the ionic liquids of Comparative Example 1A to Comparative Example 5A was 0.5% by mass or greater to ethanol but was less than 0.2% by mass to the fluorine-based solvent and less than 0.5% by mass to n-hexane. The solubility of the ionic liquid of Comparative Example 6A was less than 0.2% by mass to the fluorine-based solvent but was 0.5% by mass or greater to n-hexane and ethanol. The solubility of Z-DOL and Z-TETRAOL was 0.2% by mass or greater to the fluorine-based solvent but was less than 0.5% by mass to n-hexane and ethanol. 
     As is understood from this, the ionic liquids formed from the primary amine, the secondary amine, and the quaternary ammonium salt presented in the Comparative Examples were poor in solubility to fluorine-based solvents and hydrocarbon-based solvents, while the ionic liquids of the Examples formed from the tertiary amines was greatly improved in solubility, although they are the same sulfonic acid octadecyl ammonium salts. Being soluble to hexane means that the ionic liquids can exhibit effects as additives by virtue of their compatibility, considering the fact that the materials widely used as lubricants are long-chain fatty acid or ester of long-chain fatty acid. Also, since the ionic liquids of the Examples were soluble to Vertrel XF which is a fluorine-based solvent, they are sufficient to be used for productions of micromachines and hard disks. Z-DOL and Z-TETRAOL, having a perfluoropolyether skeleton, are high in solubility to fluorine-based solvents but are low in solubility to hydrocarbon-based solvents or alcohols. 
     In general, effects of molecular structures on solubility are very complicated and are difficult to predict. However, the present inventors have found based on their studies that the ionic liquids formed from the tertiary amines were improved in solubility to fluorine-based solvents as compared with the ionic liquids formed from the primary amine, the secondary amine, and the quaternary ammonium salt. 
     Example 1C 
     &lt;Measurement Result of Thermal Stability&gt; 
     The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-octadecyl ammonium were 315.7° C., 337.0° C., and 356.7° C., respectively. Compared with the commercial products, perfluoropolyether Z-DOL (Comparative Example 7C) and Z-TETRAOL (Comparative Example 8C), it was found that the thermal stability was improved by 130° C. or greater and 75° C. or greater, respectively. 
     Example 2C 
     &lt;Measurement Result of Thermal Stability&gt; 
     The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of bis(nonafluorobutanesulfonyl)imide-N,N-dimethyl-dodecyl ammonium were 308.5° C., 331.5° C., and 353.4° C., respectively. Compared with the commercial products, perfluoropolyether Z-DOL (Comparative Example 7C) and Z-TETRAOL (Comparative Example 8C), it was found that the thermal stability was improved by 130° C. or greater and 70° C. or greater, respectively. 
     Example 3C 
     &lt;Measurement Result of Thermal Stability&gt; 
     The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of trifluoromethanesulfonic acid-N,N,N-tridodecyl ammonium were 286.0° C., 333.3° C., and 364.5° C., respectively. Compared with the commercial products, perfluoropolyether Z-DOL (Comparative Example 7C) and Z-TETRAOL (Comparative Example 8C), it was found that the thermal stability was improved by 120° C. or greater and 45° C. or greater, respectively. 
     Comparative Example 1C 
     &lt;Measurement Result of Thermal Stability&gt; 
     The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of nonafluorobutanesulfonic acid-octadecyl ammonium were 338.8° C., 355.2° C., and 370.4° C., respectively. Since the nonafluorobutanesulfonic acid-octadecyl ammonium was an ionic liquid, the thermal stability was high compared with the commercial products, perfluoropolyether Z-DOL (Comparative Example 7C) and Z-TETRAOL (Comparative Example 8C). 
     Comparative Example 2C 
     &lt;Measurement Result of Thermal Stability&gt; 
     The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of bis(nonafluorobutanesulfonyl)imide-octadecyl ammonium were 311.8° C., 329.8° C., and 348.0° C., respectively. Since the bis(nonafluorobutanesulfonyl)imide-octadecyl ammonium was an ionic liquid, the thermal stability was high compared with the commercial products, perfluoropolyether Z-DOL (Comparative Example 7C) and Z-TETRAOL (Comparative Example 8C). 
     Comparative Example 3C 
     &lt;Measurement Result of Thermal Stability&gt; 
     The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of hexafluorocyclopropane-1,3-bis(sulfonyl)imide-octadecyl ammonium were 329.6° C., 347.0° C., and 365.1° C., respectively. Since the hexafluorocyclopropane-1,3-bis(sulfonyl)imide-octadecyl ammonium was an ionic liquid, the thermal stability was high compared with the commercial products, perfluoropolyether Z-DOL (Comparative Example 7C) and Z-TETRAOL (Comparative Example 8C). 
     Comparative Example 4C 
     &lt;Measurement Result of Thermal Stability&gt; 
     The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of nonafluorobutanesulfonic acid-N-methyloctadecyl ammonium were 346.8° C., 364.0° C., and 381.1° C., respectively. Since the nonafluorobutanesulfonic acid-N-methyloctadecyl ammonium was an ionic liquid, the thermal stability was high compared with the commercial products, perfluoropolyether Z-DOL (Comparative Example 7C) and Z-TETRAOL (Comparative Example 8C). 
     Comparative Example 5C 
     &lt;Measurement Result of Thermal Stability&gt; 
     The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of nonafluorobutanesulfonic acid-trimethyloctadecyl ammonium were 340.5° C., 356.2° C., and 371.9° C., respectively. Since the nonafluorobutanesulfonic acid-trimethyloctadecyl ammonium was an ionic liquid, the thermal stability was high compared with the commercial products, perfluoropolyether Z-DOL (Comparative Example 7C) and Z-TETRAOL (Comparative Example 80. 
     Comparative Example 6C 
     &lt;Measurement Result of Thermal Stability&gt; 
     The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of pentadecafluorooctanoic acid octadecyl ammonium were 206.9° C., 215.8° C., and 223.4° C., respectively. Although the pentadecafluorooctanoic acid octadecyl ammonium salt was an ionic liquid, the bonding strength between ions was weak because the pKa of the acid was greater than 10, and hence the pentadecafluorooctanoic acid octadecyl ammonium salt lacked thermal stability. In the case of this Comparative Example, the pentadecafluorooctanoic acid octadecyl ammonium salt was an ionic liquid, but the thermal stability did not significantly improve compared to the commercial products, perfluoropolyether Z-DOL (Comparative Example 7C) and Z-TETRAOL (Comparative Example 8C). 
     Comparative Example 7C 
     &lt;Measurement Result of Thermal Stability&gt; 
     A measurement of a commercial product perfluoropolyether Z-DOL having a hydroxyl group at a terminal and a molecular weight of about 2,000 as Comparative Example 7C was performed. As a result, the 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of Z-DOL were 165.0° C., 197.0° C., and 226.0° C., respectively. The weight reduction was caused by evaporation. 
     Comparative Example 8C 
     &lt;Measurement Result of Thermal Stability&gt; 
     Perfluoropolyether (Z-TETRAOL) having a few hydroxyl groups at a terminal and a molecular weight of about 2,000, which was a commercial product and typically used as a lubricant for magnetic recording media was used as a lubricant of Comparative Example 8C. The 5% weight reduction temperature, 10% weight reduction temperature, and 20% weight reduction temperature of Z-TETRAOL were 240.0° C., 261.0° C., and 282.0° C., respectively. Similar to Z-DOL, the weight reduction was caused by evaporation. 
     The results of Examples 1C to 3C and Comparative Examples 1C to 8C are summarized in Table 3 together with their melting points. 
     
       
         
           
               
               
               
               
             
               
                   
                 TABLE 3 
               
             
            
               
                   
                   
               
               
                   
                 Synthesis Examples 
                 Weight reduction 
                   
               
               
                   
                 or 
                 temperature (° C.) 
                 Melting 
               
            
           
           
               
               
               
               
               
               
            
               
                 Examples 
                 Compound Names 
                 5% 
                 10% 
                 20% 
                 point/° C. 
               
               
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 Ex. 1C 
                 Ex. 1A 
                 315.7 
                 337.0 
                 356.7 
                 86.5 
               
               
                 Ex. 2C 
                 Ex. 2A 
                 308.5 
                 331.5 
                 353.4 
                 78.7 
               
               
                 Ex. 3C 
                 Ex. 3A 
                 286.0 
                 333.3 
                 364.5 
                 liquid 
               
               
                 Comp. Ex. 1C 
                 Comp. Ex. 1A 
                 338.8 
                 355.2 
                 370.4 
                 111.7 
               
               
                 Comp. Ex. 2C 
                 Comp. Ex. 2A 
                 311.8 
                 329.8 
                 348.0 
                 118.8 
               
               
                 Comp. Ex. 3C 
                 Comp. Ex. 3A 
                 329.6 
                 347.0 
                 365.1 
                 92.9 
               
               
                 Comp. Ex. 4C 
                 Comp. Ex. 4A 
                 346.8 
                 364.0 
                 381.1 
                 97.2 
               
               
                 Comp. Ex. 5C 
                 Comp. Ex. 5A 
                 340.5 
                 356.2 
                 371.9 
                 114.3 
               
               
                 Comp. Ex. 6C 
                 Camp. Ex. 6A 
                 206.9 
                 215.8 
                 223.4 
                 61.7 
               
               
                 Comp. Ex. 7C 
                 Z-DOL 
                 165.0 
                 197.0 
                 226.0 
                 &lt;25.0 
               
               
                 Comp. Ex. 8C 
                 Z-TETRAOL 
                 240.0 
                 261.0 
                 282.0 
                 &lt;25.0 
               
               
                   
               
            
           
         
       
     
     As is understood from the above, the lubricants based on the ionic liquids, excluding Comparative Example 6A, are much more excellent in thermal stability than commercially available perfluoropolyethers (Z-DOL and Z-TETRAOL). In terms of the melting point as well, Comparative Examples having a straight-chain octadecyl group, excluding Comparative Example 6A, are all 90° C. or higher, but Examples 1A to 3A formed from the tertiary amines are all low; i.e., 90° C. or lower, and Example 3A is a liquid. As described above, the ionic liquids formed from the tertiary amines are remarkably improved in thermal stability and additionally have the effect of reducing the melting point. This is expected to lead to the effect of reducing friction at low temperatures. 
     Example 1D to Example 3D and Comparative Example 1D to Comparative Example 5D 
     &lt;Disk Durability Test&gt; 
     Magnetic disks were produced by applying lubricants including the ionic liquids of Examples 1A to 3A and Comparative Examples 1A to 5A, respectively. As presented in Table 4, the CSS measurements of the magnetic disks were greater than 50,000 times, and the CSS measurements after the heating test were also greater than 50,000 times, and the magnetic disks exhibited excellent durability. 
     Comparative Example 6D 
     &lt;Disk Durability Test&gt; 
     The magnetic disk was produced using a lubricant including pentadecafluorooctanoic acid octadecyl ammonium salt. As presented in Table 4, the CSS measurement of the magnetic disk was greater than 50,000 times but the CSS measurement of the heating test was 891 times and the durability of the magnetic disk was deteriorated by the heating test. As presented with Comparative Example 12, the pentadecafluorooctanoic acid octadecyl ammonium salt was an ionic liquid, but the pKa of the acid was greater than 10. Therefore, the bonding strength between ions was weak and the thermal stability was deteriorated, and therefore it was considered that the properties after the heating test were deteriorated. 
     Comparative Example 7D 
     &lt;Disk Durability Test&gt; 
     The magnetic disk was produced using a lubricant including Z-DOL. As presented in Table 4, the CSS measurement of the magnetic disk was greater than 50,000 times but the CSS measurement of the heating test was the CSS measurement of the heating test was 12,000 times and the durability of the magnetic disk was deteriorated by the heating test. 
     Comparative Example 8D 
     &lt;Disk Durability Test&gt; 
     The magnetic disk was produced using a lubricant including Z-TETRAOL. As presented in Table 4, the CSS measurement of the magnetic disk was greater than 50,000 times but the CSS measurement of the heating test was the CSS measurement of the heating test was 36,000 times and the durability of the magnetic disk was deteriorated by the heating test. 
     The results of Examples 1D to 3D, and Comparative Examples 1D to 8D are summarized in Table 4. 
     
       
         
           
               
               
               
               
             
               
                 TABLE 4 
               
               
                   
               
               
                   
                 Synthesis 
                   
                   
               
               
                   
                 Examples 
               
               
                   
                 or Compound 
                   
                 CSS durability after 
               
               
                 Examples 
                 Names 
                 CSS durability 
                 heating 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 Ex. 1D 
                 Ex. 1A 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 &gt;50,000 
               
               
                   
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Ex. 2D 
                 Ex. 2A 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 &gt;50,000 
               
               
                   
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Ex. 3D 
                 Ex. 3A 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 &gt;50,000 
               
               
                   
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Comp. 
                 Comp. Ex. 1A 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 &gt;50,000 
               
               
                 Ex. 1D 
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Comp. 
                 Comp. Ex. 2A 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 &gt;50,000 
               
               
                 Ex. 2D 
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Comp. 
                 Comp. Ex. 3A 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 &gt;50,000 
               
               
                 Ex. 3D 
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Comp. 
                 Comp. Ex. 4A 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 &gt;50,000 
               
               
                 Ex. 4D 
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Comp. 
                 Comp. Ex. 5A 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 &gt;50,000 
               
               
                 Ex. 5D 
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Comp. 
                 Comp. Ex. 6A 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 891 
               
               
                 Ex. 6D 
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Comp. 
                 Z-DOL 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 12,000 
               
               
                 Ex. 7D 
                   
                 60% RH 
                   
                 60% RH 
               
               
                 Comp. 
                 Z-TETRAOL 
                 25° C., 
                 &gt;50,000 
                 25° C., 
                 36,000 
               
               
                 Ex. 8D 
                   
                 60% RH 
                   
                 60% RH 
               
               
                   
               
            
           
         
       
     
     Example 1E to Example 3E and Comparative Example 1E to Comparative Example 8E 
     After producing magnetic tapes using lubricants including the ionic liquids of Examples 1A to 3A, the ionic liquids of Comparative Examples 1A to 6A, Z-DOL, and Z-Tetraol, respectively, the following measurements were performed.
         Coefficient of friction of magnetic tape after shuttle run of 100 times:       

     In the environment having a temperature of −5° C., or in the environment having a temperature of 40° C. and relative humidity of 90%.
         Still durability test:       

     In the environment having a temperature of −5° C., or in the environment having a temperature of 40° C. and relative humidity of 30%.
         Shuttle durability test:       

     In the environment having a temperature of −5° C., or in the environment having a temperature of 40° C. and relative humidity of 90%.
         Coefficient of friction of magnetic tape after shuttle run of 100 times after heating test:       

     In the environment having a temperature of −5° C., or in the environment having a temperature of 40° C. and relative humidity of 90%.
         Still durability test after heating test:       

     In the environment having a temperature of −5° C., or in the environment having a temperature of 40° C. and relative humidity of 30%.
         Shuttle durability test after heating test:       

     In the environment having a temperature of −5° C., or in the environment having a temperature of 40° C. and relative humidity of 90%. 
     The results of Examples 1E to 3E and Comparative Examples 1E to 8E are summarized in Tables 5-1 and 5-2. 
     
       
         
           
               
               
               
               
               
               
               
               
             
               
                   
                 TABLE 5-1 
               
               
                   
                   
               
               
                   
                   
                   
                   
                   
                 Coefficient 
                   
                   
               
               
                   
                   
                   
                   
                   
                 of friction 
                 Still durability 
                 Shuttle durability 
               
               
                   
                   
                 Coefficient of 
                   
                 Shuttle 
                 after 100 
                 after 
                 after 
               
               
                   
                   
                 friction 
                 Still durability/ 
                 durability/ 
                 runs after 
                 heating test/ 
                 heating/ 
               
               
                   
                 Compound 
                 after 100 runs 
                 min 
                 times 
                 heating test 
                 min 
                 times 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
               
               
               
               
            
               
                 Ex. 1E 
                 Ex. 1A 
                 −5° C. 
                 0.21 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
                 −5° C. 
                 0.21 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
               
               
                   
                   
                 40° C., 
                 0.23 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
                 40° C., 
                 0.23 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                 Ex. 2E 
                 Ex. 2A 
                 −5° C. 
                 0.24 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
                 −5° C. 
                 0.24 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
               
               
                   
                   
                 40° C., 
                 0.26 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
                 40° C., 
                 0.26 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                 Ex. 3E 
                 Ex. 3A 
                 −5° C. 
                 0.24 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
                 −5° C. 
                 0.24 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
               
               
                   
                   
                 40° C., 
                 0.24 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
                 40° C., 
                 0.25 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
               
               
               
               
             
               
                   
                 TABLE 5-2 
               
               
                   
                   
               
               
                   
                   
                   
                   
                   
                 Coefficient of 
                 Still durability 
                 Shuttle durability 
               
               
                   
                   
                 Coefficient of 
                   
                   
                 friction after 
                 after 
                 after 
               
               
                   
                   
                 friction after 100 
                 Still durability/ 
                 Shuttle durability/ 
                 100 runs after 
                 heating test/ 
                 heating/ 
               
               
                   
                 Compound 
                 runs 
                 min 
                 times 
                 heating test 
                 min 
                 times 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
               
               
               
               
            
               
                 Comp. Ex. 
                 Comp. Ex. 1A 
                 −5° C. 
                 0.19 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
                 −5° C. 
                 0.20 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
               
               
                 1E 
                   
                 40° C., 
                 0.23 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
                 40° C., 
                 0.23 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                 Comp. Ex. 
                 Comp. Ex. 2A 
                 −5° C. 
                 0.20 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
                 −5° C. 
                 0.21 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
               
               
                 2E 
                   
                 40° C., 
                 0.22 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
                 40° C., 
                 0.24 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                 Comp. Ex. 
                 Comp. Ex. 3A 
                 −5° C. 
                 0.21 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
                 −5° C. 
                 0.21 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
               
               
                 3E 
                   
                 40° C., 
                 0.24 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
                 40° C., 
                 0.24 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                 Comp. Ex. 
                 Comp. Ex. 4A 
                 −5° C. 
                 0.20 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
                 −5° C. 
                 0.21 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
               
               
                 4E 
                   
                 40° C., 
                 0.22 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
                 40° C., 
                 0.23 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                 Comp. Ex. 
                 Comp. Ex. 5A 
                 −5° C. 
                 0.20 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
                 −5° C. 
                 0.20 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
               
               
                 5E 
                   
                 40° C., 
                 0.23 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
                 40° C., 
                 0.24 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                 Comp. Ex. 
                 Comp. Ex. 6A 
                 −5° C. 
                 0.21 
                 −5° C. 
                 &gt;60 
                 −5° C. 
                 &gt;200 
                 −5° C. 
                 0.45 
                 −5° C. 
                 12 
                 −5° C. 
                 30 
               
               
                 6E 
                   
                 40° C., 
                 0.25 
                 40° C., 
                 &gt;60 
                 40° C., 
                 &gt;200 
                 40° C., 
                 0.51 
                 40° C., 
                 16 
                 40° C., 
                 23 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                 Comp. Ex. 
                 Z-DOL 
                 −5° C. 
                 0.25 
                 −5° C. 
                 12 
                 −5° C. 
                 59 
                 −5° C. 
                 0.32 
                 −5° C. 
                 12 
                 −5° C. 
                 46 
               
               
                 7E 
                   
                 40° C., 
                 0.30 
                 40° C., 
                 48 
                 40° C., 
                 124 
                 40° C., 
                 0.35 
                 40° C., 
                 15 
                 40° C., 
                 58 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                 Comp. Ex. 
                 Z-TETRAOL 
                 −5° C. 
                 0.22 
                 −5° C. 
                 25 
                 −5° C. 
                 65 
                 −5° C. 
                 0.28 
                 −5° C. 
                 23 
                 −5° C. 
                 55 
               
               
                 8E 
                   
                 40° C., 
                 0.26 
                 40° C., 
                 35 
                 40° C., 
                 156 
                 40° C., 
                 0.32 
                 40° C., 
                 31 
                 40° C., 
                 126 
               
               
                   
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
                   
                 90% RH 
                   
                 30% RH 
                   
                 90% RH 
               
               
                   
               
            
           
         
       
     
     In the tables, “&gt;60” of the still durability denotes greater than 60 minutes. 
     In the tables, “&gt;200” of the shuttle durability denotes greater than 200 times. 
     The following facts were confirmed. 
     It was found that the magnetic tapes to which the lubricants including the ionic liquids of Examples 1A to 3A were applied, respectively, had excellent friction resistance, still durability, and shuttle durability. 
     It was found that the magnetic tapes to which the lubricants including the ionic liquids of Comparative Examples 1A to 5A were applied, respectively, had excellent friction resistance, still durability, and shuttle durability. Since the lubricants in Comparative Examples 1A to 5A were the ionic liquids, the magnetic tapes had excellent durability even after the heating test. 
     It was found that the magnetic tape to which the lubricant including the ionic liquid of Comparative Example 6A was applied had excellent friction resistance, still durability, and shuttle durability. The lubricant in Comparative Example 6A caused significant deterioration of the magnetic tape after the heating test. 
     It was found that the magnetic tape to which Z-DOL was applied had significant deterioration in still durability and shuttle durability (Comparative Example 7E). 
     It was found that the magnetic tape to which Z-Tetraol was applied had significant deterioration in still durability and shuttle durability (Comparative Example 8E). 
     It was found from Tables 5-1 and 5-2 that excellent heat resistance, and durability of the magnetic tape and magnetic disk could be obtained when the lubricant included the ionic liquid including a conjugate base and a conjugate acid, the conjugate acid was a tertiary amine in which at least one of the hydrocarbons was a straight-chain hydrocarbon group having 6 or greater carbon atoms, and a pKa of an acid that was a source of the conjugate base was 10 or less in acetonitrile. 
     Not only achieving excellent thermal resistance and durability of a magnetic recording medium, such lubricants dissolved to n-hexane as a diluent as well as the ionic liquid, which meant that the lubricants could exhibit an effect as an additive to long-chain fatty acid or ester of long-chain fatty acid, which were widely used as lubricants. The lubricants were soluble to Vertrel that was a fluorine-based solvent, and thus use of such lubricants on production process was not problem, particularly when the lubricants were used for hard disks and micromachines. 
     As is clear from the descriptions above, an ion liquid-based lubricant, which includes an ionic liquid including a conjugate base and a conjugate acid, where the conjugate acid is a tertiary amine in which at least one of the hydrocarbons was a straight-chain hydrocarbon group having 6 or greater carbon atoms, and a pKa of an acid that is a source of the conjugate base is 10 or less in acetonitrile, has a high decomposition temperature, and high 5%, 10%, and 20% weight reduction temperatures, and has excellent thermal stability. Moreover, the lubricant can maintain excellent lubricity under high temperature conditions compared to conventional perfluoropolyether, and can maintain lubricity over a long period. Accordingly, a magnetic recording medium using the lubricant including the ionic liquid can obtain excellent running performances, abrasion resistance, and durability. 