Patent Publication Number: US-2022223783-A1

Title: Insertion layers for perpendicularly magnetized heusler layers with reduced magnetic damping

Description:
CROSS REFERENCE TO OTHER APPLICATIONS 
     This application claims priority to U.S. Provisional Patent Application No. 63/136,570 entitled INSERTION LAYERS FOR PERPENDICULARLY MAGNETIZED HEUSLER FREE LAYER WITH LOW MAGNETIC DAMPING filed Jan. 12, 2021 which is incorporated herein by reference for all purposes. 
    
    
     BACKGROUND OF THE INVENTION 
     Magnetic memories such as magnetic random access memories (MRAMs) store information utilizing magnetic materials as an information storage medium. For example, a magnetic tunneling junction (MTJ) may be used in an MRAM, such as a spin transfer torque MRAM (STT-MRAM). The MTJ typically includes a reference layer, a free layer and a tunneling barrier layer between the reference and free layers. The reference and free layers are magnetic. The magnetic moment of the reference layer is generally fixed, or pinned, in a particular direction. The free layer has a changeable magnetic moment and is used to store information. A bottom contact below the MTJ and a top contact on the MTJ are used to drive current through the MTJ in a current-perpendicular-to-plane (CPP) direction in an STT-MRAM. In case of MTJs with positive tunnel magnetoresistance (TMR), when a sufficient current is driven in one direction perpendicular-to-plane (e.g. top to bottom), the free layer magnetic moment switches to be parallel to that of the reference layer. When a sufficient current is driven in the opposite direction (e.g. bottom to top), the free layer magnetic moment switches to be antiparallel to that of the reference layer. Different magnetic configurations correspond to different magnetoresistances and thus different logical states (e.g. a logical “0” and a logical “1”) of the MTJ. 
     Because of their potential for use in a variety of applications, research in magnetic memories is ongoing. Accordingly, what is needed is a method and system that may improve the performance of magnetic junctions. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       Various embodiments of the invention are disclosed in the following detailed description and the accompanying drawings. 
         FIGS. 1A-1C  depicts embodiments of magnetic structures including Heusler compounds and having reduced magnetic damping. 
         FIGS. 2A-2C  depict embodiments of magnetic junctions including Heusler compounds and having reduced magnetic damping. 
         FIGS. 3A-3B  depict embodiments of magnetic junctions including Heusler compounds and having reduced magnetic damping. 
         FIG. 4  is a flow chart depicting an embodiment of a method for providing a magnetic structure including a Heusler compound and having reduced magnetic damping. 
         FIG. 5  if a flow chart depicting an embodiment of a method for providing a magnetic device including a Heusler compound and having reduced magnetic damping. 
     
    
    
     DETAILED DESCRIPTION 
     The invention can be implemented in numerous ways, including as a process; an apparatus; a system; a composition of matter; a computer program product embodied on a computer readable storage medium; and/or a processor, such as a processor configured to execute instructions stored on and/or provided by a memory coupled to the processor. In this specification, these implementations, or any other form that the invention may take, may be referred to as techniques. In general, the order of the steps of disclosed processes may be altered within the scope of the invention. Unless stated otherwise, a component such as a processor or a memory described as being configured to perform a task may be implemented as a general component that is temporarily configured to perform the task at a given time or a specific component that is manufactured to perform the task. As used herein, the term ‘processor’ refers to one or more devices, circuits, and/or processing cores configured to process data, such as computer program instructions. 
     A detailed description of one or more embodiments of the invention is provided below along with accompanying figures that illustrate the principles of the invention. The invention is described in connection with such embodiments, but the invention is not limited to any embodiment. The scope of the invention is limited only by the claims and the invention encompasses numerous alternatives, modifications and equivalents. Numerous specific details are set forth in the following description in order to provide a thorough understanding of the invention. These details are provided for the purpose of example and the invention may be practiced according to the claims without some or all of these specific details. For the purpose of clarity, technical material that is known in the technical fields related to the invention has not been described in detail so that the invention is not unnecessarily obscured. 
     The exemplary embodiments are described in the context of particular methods, layers, devices, magnetic junctions and magnetic memories having certain components. One of ordinary skill in the art will readily recognize that the present invention is consistent with the use of devices, magnetic junctions and magnetic memories having other and/or additional components and/or other features not inconsistent with the present invention. The method and system are also described in the context of current understanding of various physical phenomena. Consequently, one of ordinary skill in the art will readily recognize that theoretical explanations of the behavior of the method and system are made based upon this current understanding of these physical phenomena. However, the method and system described herein are not dependent upon a particular physical explanation. One of ordinary skill in the art will also readily recognize that the method and system are described in the context of a structure having a particular relationship to the substrate. However, one of ordinary skill in the art will readily recognize that the method and system are consistent with other structures. In addition, the method and system are described in the context of certain layers being synthetic and/or simple. However, one of ordinary skill in the art will readily recognize that the layers could have another structure. Furthermore, the method and system are described in the context of magnetic junctions and/or substructures having particular layers. However, one of ordinary skill in the art will readily recognize that magnetic junctions and/or substructures having additional and/or different layers not inconsistent with the method and system could also be used. Moreover, certain components are described as being magnetic, ferromagnetic, and ferrimagnetic. As used herein, the term magnetic could include ferromagnetic, ferrimagnetic and/or like structures. As used herein, “in-plane” is substantially within or parallel to the plane of one or more of the layers of a magnetic junction. Conversely, “perpendicular” and “perpendicular-to-plane” corresponds to a direction that is substantially perpendicular to one or more of the layers of the magnetic junction. The method and system are also described in the context of certain alloys. Unless otherwise specified, if specific concentrations of the alloy are not mentioned, any stoichiometry not inconsistent with the method and system may be used. 
     Magnetic tunneling junctions (MTJs) may be used in memories such as magnetic random access memories (MRAMs). MTJs may be programmable by a current driven in a current-perpendicular-to-plane (CPP) direction and used in a spin-transfer torque MRAM (STT-MRAM). Some MTJs utilize tunnel barriers formed from MgO as well as free and reference layers that include alloys of Co, Fe and B (termed “CoFeB” herein, without requiring a specific stoichiometry). The magnetic moments of the free and reference layers may be desired to be oriented perpendicular to the layer (“perpendicular-to-plane”). For magnetic layers having a perpendicular-to-plane magnetic moment, the perpendicular magnetic anisotropy (PMA) energy of the magnetic layer exceeds the out-of-plane demagnetization energy. However, the PMA of such a CoFeB layer arises from the interfaces between the CoFeB layer and the tunneling barrier layer and/or the underlayer on which the CoFeB layer is deposited. However, this means that such CoFeB layers may not be thermally stable if the device size is reduced to below approximately twenty nanometers in size. As such, Co—Fe—B layers may be unsuitable for use in more dense memory applications. 
     Magnetic materials that have a PMA arising from a volume effect and which may have a perpendicular-to-plane magnetic moment at small thicknesses include Heusler compounds. Heusler compounds may have the chemical formula X 2 YZ or X′X′″YZ; where X, X′, X″, and Y may be transition metals or lanthanides (rare earth metals) and Z may be from a main group metal. Heusler compounds can have a structure of the type Cu 2 MnAl in which the elements are disposed on four interpenetrating face-centered cubic (fcc) lattices. Heusler compounds form a structure defined by the space group symmetry L2 1  (or D0 22  when they are tetragonally distorted). The properties of Heusler compounds are strongly dependent on the chemical ordering of the elements constituting the compounds. Many Heusler compounds are known to have a structure of the type Cu 2 MnAl. Some of these Heusler compounds are ferromagnetic or ferrimagnetic due to magnetic moments on the X and/or Y sites. Some parent Heusler compounds are cubic and exhibit weak or no significant magnetic anisotropy. However, the structure of some magnetic Heusler compounds is tetragonally distorted. Such a tetragonal Heusler compound has a crystal structure that is tetragonal instead of cubic. A tetragonal Heusler compound may also be magnetic. Due to the tetragonal distortion the magnetization exhibited by these compounds may be preferably aligned along the tetragonal axis. Thin films formed from such materials may exhibit PMA due to a magneto-crystalline anisotropy associated with their tetragonally distorted structure. For example, such tetragonal Heusler compounds include Mn 3 Z where Z═Ga, Ge, Sn, and Sb. Some such tetragonal Heusler compounds may be grown at smaller thicknesses and maintain their PMA. For example, with underlayers such as Mn x N (where x is generally within range of 2 to 4.5) and CoAl (usually nominally 1:1 composition ratio), some tetragonal Mn-containing Heusler compounds possessing PMA may be grown with smaller thicknesses. Similarly, magnetic L1 0  compounds containing Mn may be grown at smaller thicknesses. Such magnetic L1 0  compounds include MnSb alloys, MnAl alloys, MnSn alloys and MnGa alloys. Similarly tetragonal C38 phase of Mn containing compounds such as MnAlGe, MnGaGe, MnAlGa, MnGeIn, and MnGaSn, etc. which are ferromagnetic and low moment can also be used as free layer within MTJ device. 
     In addition to a large PMA, magnetic layers are also desired to have a low magnetic moment. A low magnetic moment allows for a lower switching current and a narrow switching pulse width (e.g. twenty nanoseconds and/or less). Heusler compounds may fulfill these criteria. For example, Heusler compounds grown on certain metallic underlayers, such as CoAl (e.g. B2 CoAl formed from alternating layers of Co and Al) may have a large PMA and a low magnetic moment. However, magnetic junctions employing such Heusler compounds may have a higher magnetic damping than desired. For example, in some cases, such Heusler compounds may have a magnetic damping on the order of that found in CoFeB. A high magnetic damping increases the switching current, which is undesirable. Consequently, a mechanism for decreasing the switching current of magnetic junctions while maintaining their PMA is desirable. 
     A magnetic structure, a magnetic device incorporating the magnetic structure and a method for providing the magnetic structure are described. The magnetic structure includes a magnetic layer, a templating structure and a resistive insertion layer. The magnetic layer includes a Heusler compound and has a perpendicular magnetic anisotropy energy exceeding an out-of-plane demagnetization energy. The templating structure has a crystal structure configured to template the resistive insertion layer and/or the Heusler compound. The magnetic layer is on the templating structure. The resistive insertion layer is configured to reduce magnetic damping for the Heusler compound and allow for templating of the Heusler compound. 
     In some embodiments, the resistive insertion layer has a location selected from a first location, a second location, and a third location. The first location is between the templating structure and the magnetic layer. The second location is such that the templating structure is between the resistive insertion layer and the magnetic layer. The third location is on the magnetic layer such that the magnetic layer is between the templating structure and the resistive interlayer. 
     For the resistive insertion layer being at the first location, the resistive interlayer has a lattice mismatch of not more than ten percent for the Heusler compound. Thus, the resistive insertion layer at the first location is crystalline. For the resistive insertion layer having the first location, the resistive insertion layer may also have a (001) texture and a thickness of not more than 2 nanometers. In such embodiments, the Heusler compound may have a Heusler thickness of at least five nanometers. In such embodiments, the templating layer is configured to template at least the resistive insertion layer. 
     For the resistive insertion layer being at the second location, the resistive interlayer has not more than ten percent lattice mismatch with the Heusler compound. Thus, the resistive insertion layer at the second location is crystalline. The templating structure may have a thickness of not more than twenty Angstroms. In some such embodiments, the templating structure has a lattice mismatch with the Heusler compound of not more than ten percent and is configured to template the Heusler compound. In some embodiments, the templating structure has a thickness of at least one Angstrom and not more than twenty Angstroms. In some such embodiments, the templating structure has a thickness of not more than ten Angstroms. The thickness of the templating structure may be not more than five Angstroms. In some embodiments, the magnetic structure includes an additional templating structure. The resistive insertion layer is between the templating structure and the additional templating structure. The additional templating structure may be on and in physical contact with the Mn x N-containing layer-seed layer. 
     For the resistive insertion layer having the third location, the magnetic structure may also include a tunneling barrier layer. The templating structure is on the tunneling barrier layer and the resistive interlayer is further from a substrate than the magnetic layer. The templating structure is magnetic and may have the thickness of not more than twenty Angstroms. In some embodiments, the templating structure includes Co (1-x) Al x , where x is less than 0.4. In such embodiments, the templating structure is configured to template the Heusler compound. In some such embodiments, the thickness of the templating structure is not more than ten Angstroms. In some embodiments, a Mn x N-containing layer (e.g. a seed layer) is included. 
     A magnetic device is also described. The magnetic device may include the magnetic structure. For example, the magnetic device may include a free layer, a nonmagnetic spacer layer, a reference layer, a resistive insertion layer and a templating structure. The nonmagnetic spacer layer is between the free and reference layers. The free layer, templating structure and resistive insertion layer may be analogous to the magnetic layer, templating structure and resistive insertion layer of the magnetic structure. Thus, the free layer includes a Heusler compound and has a perpendicular magnetic anisotropy energy exceeding an out-of-plane demagnetization energy. The templating structure and resistive insertion layer are analogous to those described for the magnetic structure. Thus, the templating structure has a crystal structure configured to template the Heusler compound and/or the resistive insertion layer. The free layer is on the templating structure. The resistive insertion layer is configured to reduce magnetic damping for the Heusler compound and allow for templating of the Heusler compound. For example, in some embodiments, the Heusler compound includes at least one of Mn 3 Ge, Mn 3 Al, Mn 3 Sb, Mn 3 Ga, Mn 3 Sn, Mn 3 In, and Mn 2 CoSn. The resistive insertion layer may include at least one of MgO, Mg-Al-Oxide, Mg-Ti-Oxide, Mg-Fe-Oxide, Mg-Zn-Oxide, Mg-Mn-Oxide, MgAl 2 O 4 , CaTiO 3 , SrTiO 3 , BaTiO 3 , LaAlO 3 , BaSnO 3 , NaCl, LiF, GaAs, ZnSe, Cu(In x Ga 1-x )Se 2 , AlN and ScN. The templating structure may include at least one of Ta, Ru, Fe, Ir, CoFeB, MgO, Ta—N, Ti—N, Mn—N, VN, Cu—N, Sc—N, CoSn, CoGe, NiAl, FeAl, CoAl, RuAl, IrAl, Cr, CuZn, AgZn, Ag—Mg, and Cr—Ru. 
     The resistive insertion layer has a location selected from a first location, a second location, and a third location analogous to the first, second and third locations for the magnetic structure. For the resistive insertion layer at the first location, the resistive interlayer has a lattice mismatch of not more than ten percent for the Heusler compound. In such embodiments, the templating layer is configured to template at least the resistive insertion layer. In some such embodiments, the nonmagnetic spacer layer has a nonmagnetic spacer layer resistance, the resistive insertion layer has a (001) texture and a resistance of not more than twenty percent of the nonmagnetic spacer layer resistance. In some such embodiments, the resistive insertion layer has a resistance of not more than ten percent of the nonmagnetic spacer layer resistance. The Heusler compound may also have a Heusler thickness of at least five nanometers in such embodiments. 
     For the second location, the resistive interlayer may have a lattice mismatch and the templating structure has a thickness of not more than twenty Angstroms. Thus, the resistive insertion layer is crystalline. In some such embodiments, the templating structure is at least one Angstrom and not more than ten Angstroms thick. In some embodiments, the thickness of the templating structure is not more than five Angstroms. The templating structure is also configured to template the Heusler compound. The magnetic device may also include an additional templating structure. The resistive insertion layer is between the templating structure and the additional templating structure. In such embodiments, the additional templating structure is thicker than the templating structure. The magnetic device may also include a seed layer on which the additional templating structure resides and shares an interface with. For example, the seed layer may include Mn x N, where x is at least 2 and not more than 4.75. In some such embodiments, x is at least 2 and not more than 4. 
     For the third location, the resistive interlayer is further from a substrate than the free layer. In some such embodiments, the nonmagnetic spacer layer is a tunneling barrier layer and the templating structure is on the tunneling barrier layer. In such embodiments, the templating structure may be magnetic and is configured to template the Heusler compound. The templating structure may have the thickness of not more than twenty Angstroms. In some embodiments, the templating structure includes Co (1-x) Al x , where x is less than 0.4 and the thickness is not more than ten Angstroms. The resistive insertion layer may be amorphous. For example, the amorphous resistive insertion layer may include one or more of amorphous Al-Oxide, Al-rich Mg-Al-Oxide, Ga-Oxide, Mg-Ga-Oxide, In-Zn-Oxide, and In-Ga-Zn-Oxide. 
     A method for providing a magnetic structure and/or magnetic device is also described. The method includes providing a templating structure having a crystal structure configured to template at least one of a resistive insertion layer and a Heusler compound. The method also includes providing, on the templating structure, a magnetic layer including the Heusler compound. The magnetic layer has a perpendicular magnetic anisotropy energy exceeding an out-of-plane demagnetization energy. A resistive insertion layer configured to reduce magnetic damping for the Heusler compound and allow for templating of the Heusler compound is also provided. In some embodiments, the method includes providing the resistive insertion layer at the first, second, and/or third location described above. For the resistive insertion layer being at the first location, the resistive interlayer has a lattice mismatch of not more than ten percent for the Heusler compound. For the resistive insertion layer being at the second location, the resistive interlayer may have a lattice mismatch and the templating structure has a thickness of not more than twenty Angstroms. For the resistive insertion layer being at the third location, the resistive interlayer is further from a substrate than the magnetic layer. 
       FIGS. 1A-1C  depicts embodiments of magnetic structures  100 A,  100 B, and  100 C including Heusler compounds and having reduced magnetic damping.  FIGS. 1A-1C  are not to scale and additional layers (not shown) may be present in some embodiments. The magnetic structure  100 A,  100 B and/or  100 C may be used in a variety of magnetic devices and, therefore, a variety of electronic devices. For example, the magnetic structure may be used in a magnetic junction such as a magnetic tunneling junction (MTJ) that may be included in a magnetic random access memory (MRAM). 
     Referring to  FIG. 1A , magnetic structure  100 A includes templating structure  110 A, resistive insertion layer  120 , and magnetic layer  130 . Magnetic layer  130  includes a Heusler compound having a high perpendicular magnetic anisotropy (PMA). In some embodiments, magnetic layer  130  includes only Heusler compound(s). For example, magnetic layer  130  may be a layer consisting of a Heusler compound. In other embodiments, magnetic layer  130  may be a multilayer including one or more Heusler compounds and/or other materials. Magnetic layer  130 , and the Heusler compound(s) therein, each has a PMA energy that exceeds the out-of-plane demagnetization energy. Thus, magnetic moment  132  of magnetic layer  130  has stable states perpendicular to plane. One such stable state is shown in  FIG. 1A . In some embodiments, magnetic layer  130  includes or consists of particular Mn-based Heusler compounds. For example, the Heusler compound(s) used may include or be composed of one or more of Mn 3 Ge, Mn 3 Al, Mn 3 Sb, Mn 3 Ga, Mn 3 Sn, Mn 3 In, and/or Mn 2 CoSn. Although these Heusler alloys are most likely to be stable in tetragonal phase (D0 22 ), the formation of a distorted cubic phase having a high PMA is still possible if resistive insertion layer  120  has an in-plane lattice constant significantly larger than that of the magnetic layer  130 . This situation may occur for resistive insertion layer  120  including rock-salt oxide(s). In some embodiments, other high PMA Heusler compounds may be used. The Heusler compound, and thus magnetic layer  130 , are sufficiently thick that any issues due to the lattice mismatch with resistive insertion layer  120  may be resolved. For example, the Heusler compound of magnetic layer  130  may be at least five nanometers thick. In some embodiments, the Heusler compound of magnetic layer is at least one nanometer thick, but may be less than five nanometers thick. In some such embodiments, the Heusler compound is at least two nanometers thick. Other thicknesses may be possible. 
     Templating structure  110 A is used to template resistive insertion layer  120 . Because resistive insertion layer  120  is used to template magnetic layer  130 , templating structure  110 A may also be considered to template the Heusler compound of magnetic layer  130 . Thus, templating structure  110 A is configured to have the appropriate structure (e.g. lattice constant, symmetry and/or texture) for growing or otherwise providing one or more layers on templating structure  110 A. For example, templating structure  130  may have a (001) texture and a small lattice mismatch (e.g. not more than ten percent in some embodiments and not more than five percent in some such embodiments) with resistive insertion layer  120 . This allows resistive insertion layer  120  to be provided such that resistive insertion layer  120  can template the desired structure of the Heusler compound(s) of magnetic layer  130 . Templating structure  110 A is a single layer in some embodiments. In other embodiments, templating structure  110 A is a multilayer. Materials for templating structure  110 A may include or consist of one or more of Ta, Ru, Fe, Ir, CoFeB, MgO, Ta—N, Ti—N, Mn—N, VN, Cu—N, Sc—N, CoSn, CoGe, NiAl, FeAl, CoAl (including B2 CoAl having alternating layers of Co and Al), RuAl, IrAl, Cr, and Cr—Ru. In some embodiments, templating structure  110 A is at least five Angstroms and not more than six hundred Angstroms thick. In some embodiments, templating structure  110 A is not more than three hundred Angstroms thick. In some such embodiments, templating structure  110 A may be not more than ten Angstroms thick. In some embodiments, templating structure  110 A may reside on and be in physical contact with (e.g. share an interface with) a seed layer (not shown) such as a Mn x N seed layer (e.g. where x is at least 2 or 2.5 and not more than 4 or 4.75). In some embodiments, such a seed layer may be at least five nanometers and not more than thirty nanometers thick. 
     Resistive insertion layer  120  is configured to reduce magnetic damping for the Heusler compound and allow for templating of the Heusler compound. Resistive insertion layer  120  may be a single layer in some embodiments. Other structures may be possible. Resistive insertion layer  120  is adjacent to magnetic layer  130 . In the embodiment shown, resistive insertion layer  120  shares an interface with magnetic layer  130 . Resistive insertion layer  120  may thus share an interface with the Heusler compound of magnetic layer  130 . 
     Thus, resistive insertion layer  120  is configured to have the appropriate structure (e.g. lattice constant, symmetry and/or texture) for growing or otherwise providing the Heusler compound(s) of magnetic layer  130  residing on resistive insertion layer  120 . Stated differently, resistive insertion layer  120  is configured to template the Heusler compound(s) of magnetic layer  130 . To template of the Heusler compound (e.g. provide the appropriate lattice constant, symmetry and/or orientation for growing the Heusler compound(s) having the desired structure), resistive insertion layer  120  may include one or more insulating and/or semiconducting compounds that have small in-plane lattice mismatch with the Heusler compound(s) of magnetic layer  130 . Thus, resistive insertion layer  120  is crystalline. In some embodiments, the lattice mismatch between the Heusler compound of magnetic layer  130  and resistive interlayer is not more than ten percent (e.g. the in-plane lattice constant of resistive insertion layer  120  is within ten percent of the in-plane lattice constant for the Heusler compound of magnetic layer  130 ). In some embodiments, the lattice mismatch between the Heusler compound of magnetic layer  130  and resistive insertion layer  120  is not more than eight percent. In some embodiments, the lattice mismatch between the Heusler compound of magnetic layer  130  and resistive insertion layer  120  is not more than five percent. Further, the symmetry of resistive insertion layer  120  sufficiently matches the desired symmetry of the Heusler compound(s) in magnetic layer  130 . The symmetry of resistive insertion layer  120  may be cubic for a Heusler compound having cubic symmetry. For example, resistive insertion layer  120  may be a cubic oxide, a cubic nitride, and/or a cubic semiconductor. Thus, the Heusler compound of magnetic layer  130  having a (001) orientation and the desired crystal structure may be provided on resistive insertion layer  120 . In some embodiments, resistive insertion layer  120  includes one or more of rock-salt oxides such as MgO, Mg-Al-Oxide, Mg-Ti-Oxide, Mg-Fe-Oxide, Mg-Zn-Oxide, and Mg-Mn-Oxide; spinel oxides such as MgAl 2 O 4 ; perovskite oxides that may have the form ABO 3 , where A and B are cations of different sizes, such as CaTiO 3 , SrTiO 3 , BaTiO 3 , LaAlO 3 , BaSnO 3 ; and halides such as NaCl and LiF; non-oxides (e.g. semiconductors) such as GaAs, ZnSe, and Cu(In x Ga (1-x) )Se 2 , and resistive nitrides such as AlN and ScN 
     Although it is a resistive layer, the total resistance of resistive insertion layer  120  is desired to have a small effect on operation of a device employing magnetic structure  100 A. Thus, the resistance of resistive insertion layer  120  is desired to be relatively small in comparison to other layer(s) of a device incorporating magnetic structure  100 A. For example, in magnetic tunneling junctions (MTJs) in which magnetic structure  100 A is incorporated, the resistance of resistive insertion layer  120  may be not more than twenty percent of the tunneling barrier resistance. In some such embodiments, the resistance of resistive insertion layer  120  is not more than ten percent of the tunneling barrier resistance. In some embodiments, the resistance of resistive insertion layer  120  may be not more than five percent of the tunneling barrier resistance. In some such embodiments, the resistance of resistive insertion layer  120  may be not more than two percent of the tunneling barrier resistance. The resistance area product of resistive insertion layer  120  is thus smaller than the resistance area product of the tunneling barrier layer. Consequently, the parasitic resistance due to resistive insertion layer  120  may be reduced. For similar reasons, resistive insertion layer  120  may be not more than 2 nanometers thick in some embodiments. In some embodiments, resistive insertion layer  120  is not more than 1 nanometer thick. 
     In the absence of resistive insertion layer  120 , magnetic layer  130  may have a high magnetic damping. For example, in spin transfer torque (STT) programming, a spin polarized current is driven through magnetic layer  130  to switch the state of magnetic moment  132 . Electrons in the spin polarized current transfer their angular momentum to magnetic layer  130 , causing magnetic moment  132  to switch directions to its other stable state (e.g. toward the bottom of the page in  FIG. 1A ). However, absent resistive insertion layer  120 , electrons from magnetic layer  130  may readily travel to templating structure  110 A. These electrons share their (polarized) angular momentum with the nonmagnetic templating structure  110 A. Magnetic damping occurs. As a result, the current required to switch magnetic moment  132  between stable states (e.g. the direction shown in  FIG. 1A  and one hundred and eighty degrees from this direction) using STT is greater than desired. Further, longer current pulses may be required in such a case. 
     The presence of resistive insertion layer  120  may reduce magnetic damping. Resistive insertion layer  120  may reduce the movement of electrons between magnetic layer  130  and templating structure  110 A. In the STT programming example above, a spin polarized current is still driven through magnetic layer  130 . Electrons in the spin polarized current still transfer their angular moment to magnetic layer  130 . However, the relatively higher resistance of resistive insertion layer  120  reduces or precludes the movement of electrons from magnetic layer  130  to templating structure  110 A and/or other conductive structures. Thus, magnetic damping may be reduced. Magnetic layer  130  may be written using a smaller magnitude write current and/or a shorter current pulse width. Thus, performance of a device incorporating magnetic structure  100 A may be improved. 
     Referring to  FIG. 1B , magnetic structure  100 B includes templating structure  110 B, resistive insertion layer  120 , and magnetic layer  130 . Templating structure  110 B, resistive insertion layer  120  and magnetic layer  130  of magnetic structure  100 B are analogous to Templating structure  110 A, resistive insertion layer  120  and magnetic layer  130 , respectively, of magnetic structure  100 A depicted in  FIG. 1A . However, templating structure  110 B is between resistive insertion layer  120  and magnetic layer  130 . Thus, templating structure  110 B is used to template magnetic layer  130 . In some embodiments, the composition and structure of templating structure  110 B may differ from that of templating structure  110 A. 
     Magnetic layer  130  of magnetic structure  100 B depicted in  FIG. 1B  is analogous to magnetic layer  130  of magnetic structure  100 A. Thus, magnetic layer  130  includes or consists of a Heusler compound having a high PMA and magnetic moment  132  that is stable perpendicular to plane. In some embodiments, magnetic layer  130  includes only Heusler compound(s). Because templating structure  110 B may share an interface with magnetic layer  130 , and thus may share an interface with the Heusler compound contained therein, magnetic layer  130  may be better templated to the desired structure. Therefore, the Heusler compound(s) of magnetic layer  130  may be thinner. For example, the Heusler compound(s) (and thus magnetic layer  130 ) may be less than five nanometers thick. In some embodiments, the Heusler compound(s) may be at least two nanometers thick and not more than five nanometers thick. In some embodiments, the Heusler compound(s) are not more than two nanometers thick and at least one nanometer thick in some embodiments. Other thicknesses may be possible. 
     Templating structure  110 B is used to template the Heusler compound(s) of magnetic layer  130 . Templating structure  110 B may, therefore, share an interface with magnetic layer  130  and the Heusler compound(s) therein. Further, templating structure  110 B has a structure (e.g. lattice constant, symmetry, and/or orientation) that promote growth of the Heusler compound(s) for magnetic layer  130 . Templating structure  110 B may have analogous structure, properties, and composition as for at least some embodiments of templating structure  110 A. For example, templating layer  110 B may include or be composed of any one or more of B2 binary alloys such as CoAl, CoGa, CoGe, CoSn, NiAl, FeAl, IrAl, RuAl, CuZn, and AgZn and/or other cubic-based ordered alloys (e.g. Ag—Mg) having a small (e.g. not more than ten percent and not more than five percent in some embodiments) in-plane lattice mismatch with the Heusler compound of magnetic layer  130 . In some embodiments, templating structure  110 B has a small lattice mismatch with resistive insertion layer  120  on which templating structure  110 B is situated. Templating structure  110 B may be significantly thinner in magnetic structure  100 B than templating structure  110 A of magnetic structure  100 A. In some embodiments, templating structure  110 B of magnetic structure  100 B is not more than twenty Angstroms thick. For example, templating structure  110 B of magnetic structure  100 B may be at least five Angstroms and not more than twenty Angstroms. In some such embodiments, templating structure  110 B of magnetic structure  100 B may be not more than ten Angstroms at least five Angstroms. Templating structure  110 B of magnetic structure  100 B may be not more than ten Angstroms at least one Angstrom. In some embodiments, templating structure  110 B is at least one Angstrom and not more than five Angstroms. 
     Resistive insertion layer  120  is configured to reduce magnetic damping for the Heusler compound and allow for templating of the Heusler compound and templating structure  110 B. Resistive insertion layer  120  of magnetic structure  100 B is analogous to resistive insertion layer  120  of magnetic structure  100 A. Thus, the structure and materials used for resistive insertion layer  120  of magnetic structure  100 B are analogous to that of resistive insertion layer  120  of magnetic structure  100 A. For example, resistive insertion layer  120  may include of MgO, Mg-Al-Oxide, Mg-Ti-Oxide, Mg-Fe-Oxide, Mg-Zn-Oxide, Mg-Mn-Oxide, MgAl 2 O 4 , CaTiO 3 , SrTiO 3 , BaTiO 3 , LaAlO 3 , BaSnO 3 , NaCl, LiF, GaAs, ZnSe, and/or Cu(In x Ga 1-x) Se 2 . The total resistance of resistive insertion layer  120  is desired to have a small effect on operation of a device employing magnetic structure  100 B. Thus, the resistance and/or resistance-area product of resistive insertion layer  120  of magnetic structure  100 B is analogous to that of resistive insertion layer  120  of magnetic structure  100 A. 
     In some embodiments, resistive insertion layer  120  resides on an additional templating structure (not shown) that is analogous to templating structure  110 B but may be thicker. In such cases, resistive insertion layer  120  may be viewed as being within a thicker templating structure. Such an additional templating layer may provide templating (e.g. (001) texture) for resistive insertion layer  120 . The additional templating layer may also provide templating for templating layer  110 B and/or magnetic layer  130 . For example, such an additional templating layer may include Ta, Ru, Fe, Ir, CoFeB, MgO, Ta—N, Ti—N, Mn—N, VN, Cu—N, ScN, IrAl, CoGe, CoSn, NiAl, FeAl, CoAl, RuAl, Cr, and Cr—Ru. Magnetic layer  130  may, therefore, grow with a (001) orientation. An additional seed layer (not shown) may underlie and share an interface with the additional templating structure. For example, the seed layer (not shown) may be a Mn x N seed layer (e.g. where x is at least 2 or 2.5 and not more than 4 or 4.75). 
     The presence of resistive insertion layer  120  in magnetic structure  100 B may reduce magnetic damping. Resistive insertion layer  120  may reduce the movement of electrons between magnetic layer  130  and layers under resistive insertion layer  120 . Although electrons may still move between magnetic layer  130  and templating structure  110 B of magnetic structure  100 B, templating structure  110 B is thin. Consequently, the amount of angular momentum imparted to templating structure  110 B may be significantly reduced. Magnetic damping may thus be reduced. Consequently, magnetic layer  130  may be written using a smaller magnitude write current and/or a shorter current pulse width. Thus, performance of a device incorporating magnetic structure  100 B may be improved. 
       FIG. 1C  depicts magnetic structure  100 C. Magnetic structure  100 C includes templating structure  110 C, resistive insertion layer  120 , and magnetic layer  130 . Templating structure  110 C, resistive insertion layer  120  and magnetic layer  130  of magnetic structure  100 C are analogous to those of magnetic structure(s)  100 A and/or  100 B. However, magnetic layer  130  is between templating structure  110 C and resistive insertion layer  120 . 
     Magnetic layer  130  of magnetic structure  100 C depicted in  FIG. 1C  is analogous to magnetic layer  130  of magnetic structure(s)  100 A and/or  100 B. Thus, magnetic layer  130  includes or consists of one or more Heusler compounds having a high PMA. Magnetic layer  130  also has magnetic moment  132  that is stable perpendicular to plane. Because templating structure  110 C may share an interface with magnetic layer  130 , and thus may share an interface with the Heusler compound contained therein, magnetic layer  130  may be better templated to the desired structure. Therefore, the Heusler compound of magnetic layer  130  may be thinner. For example, the Heusler compound may be less than five nanometers thick. In some embodiments, the Heusler compound may be at least two nanometers thick. In some embodiments, the Heusler compound is not more than two nanometers thick. The Heusler compound is at least one nanometer thick in some embodiments. Other thicknesses may be possible. 
     Templating structure  110 C is used to template the Heusler compound(s) of magnetic layer  130  and may share an interface with magnetic layer  130  and the Heusler compound(s) therein. However, in some embodiments, templating structure  110 C might be omitted. When magnetic structure  100 C is used in connection with a top free layer MTJ, magnetic layer  130  may be the free layer. In such embodiments, templating structure  110 C resides on the tunneling barrier layer or other nonmagnetic spacer layer. In such embodiments, templating structure  110 C may not only be thin, but also magnetic. In some embodiments, templating structure  110 C is not more than twenty Angstroms thick. For example, templating structure  110 C of magnetic structure  100 C may be at least five Angstroms and not more than twenty Angstroms. In some such embodiments, the templating structure  110 C of magnetic structure  100 C may be not more than ten Angstroms. In some embodiments, templating structure  110 C is at least one Angstrom and not more than five Angstroms. Templating structure  110 C of magnetic structure  100 C may be not more than ten Angstroms at least one Angstrom thick. 
     Templating structure  110 C of magnetic structure  100 C may also be magnetic. Use of a magnetic templating structure  110 C may help preserve the magnetoresistance for the MTJ incorporating magnetic structure  100 C. However, templating structure  110 C is still desired to template the Heusler compound(s) of magnetic layer  130 . Thus, the crystal structure (e.g. in-plane lattice constant, symmetry and/or texture) of templating structure  110 C is desired to be analogous to those described above, particularly templating structure  110 B. For example, templating structure  110 C may include or consist of Co (1-x) Al x , where x is less than 0.4. Such an alloy is magnetic and may have the desired crystal structure for promoting growth of magnetic layer  130 . 
     Resistive insertion layer  120  of magnetic structure  100 C is configured to reduce magnetic damping and is analogous to resistive insertion layer(s)  120  of magnetic structure(s)  100 A and/or  100 B. Thus, the structure and materials used for resistive insertion layer  120  of magnetic structure  100 C are analogous to that of resistive insertion layer(s)  120  of magnetic structure(s)  100 A and/or  100 B. However, in some embodiments, resistive insertion layer  120  may be amorphous. This is because templating of magnetic layer  130  may be achieved by templating structure  110 C. Thus, the materials used for resistive insertion layer  120  of magnetic structure  100 C may also include any amorphous compounds that are semiconducting or insulating in nature. For example, Al-Oxide, Al-rich Mg-Al-Oxide, Ga-Oxide, Mg-Ga-Oxide, In-Zn-Oxide, and/or In-Ga-Zn-Oxide may be used. The total resistance of resistive insertion layer  120  is still desired to have a small effect on operation of a device employing magnetic structure  100 C. Thus, the resistance and/or resistance-area product of resistive insertion layer  120  of magnetic structure  100 C is analogous to that of resistive insertion layer(s)  120  of magnetic structure(s)  100 A and/or  100 B. 
     The presence of resistive insertion layer  120  in magnetic structure  100 C may reduce magnetic damping. Insertion layer  120  may reduce the movement of electrons between magnetic layer  130  and overlying layers. Magnetic damping may also be reduced. Consequently, magnetic layer  130  may be written using a smaller magnitude write current and/or a shorter current pulse width. Thus, performance of a device incorporating magnetic structure  100 C may be improved. 
     As discussed above, magnetic structure(s)  100 A,  100 B and/or  100 C may be incorporated in magnetic devices, such as magnetic junctions and magnetic memories using the magnetic junctions. Examples of such magnetic junctions are depicted in  FIGS. 2A-2C and 3A-3B . 
       FIGS. 2A-2C  depict embodiments of magnetic devices  200 A,  200 B and  200 C including Heusler compounds and having reduced magnetic damping. For clarity,  FIGS. 2A-2C  are not to scale. In the embodiments shown, magnetic devices  200 A,  200 B, and  200 C are bottom free layer magnetic junctions. Thus, the free layer is closer to the substrate than the reference layer in such magnetic junctions. Magnetic devices  200 A,  200 B and/or  200 C may be used in a variety of electronic devices, such as MRAMs. Although particular layers are shown, other and/or different structures may be included. 
       FIG. 2A  depicts magnetic junction  200 A residing on substrate  201 . Magnetic junction  200 A includes templating structure  210 A, resistive insertion layer  220 , free layer  230 , nonmagnetic spacer layer  240 , and reference layer  250 . Reference layer  250  and free layer  230  are magnetic, having magnetic moments  252  and  232 , respectively. In the embodiment shown, each of free layer  230  and reference layer  250  have a PMA anisotropy energy that exceeds the out-of-plane demagnetization energy. Consequently, magnetic moments  232  and  252  are shown as perpendicular to plane. Magnetic moment  232  of free layer  230  may be programmed to be in one of multiple stable states. Consequently, magnetic moment  232  is shown as dual headed arrow. Magnetic moment  252  of reference layer  250  is stable in the embodiment shown. Consequently, magnetic moment  252  is shown as a single arrow. Although shown in a particular direction (toward the bottom of the page), magnetic moment  252  may be stable in another direction (e.g. toward the top of the page). Magnetic junction  200 A may also include optional polarization enhancement layer(s) (PEL(s)) having a high spin polarization. For example, a PEL might include Fe, CoFe and/or CoFeB. The PEL may be between reference layer  250  and nonmagnetic spacer layer  240  and/or between nonmagnetic spacer layer  240  and free layer  230 . Also shown are optional seed layer(s)  204  and optional capping layer(s)  260 . Capping layer  260  may include or be composed of any one or a combination of Ta, Ru, Mo, W, CoFeB, Pt, and metallic nitrides (e.g. Ta—N, Ti—N, Mo—N etc.). Seed layer  204  includes seed layer(s) used for providing templating structure  210 A. For example, seed layer  204  may include a Ta layer on substrate  201 , a CoFeB layer on the Ta layer, and a seed layer such as Mn x N (e.g. where 2 or 2.5≤x≤4 or 4.75) used for templating structure  210 A. 
     Nonmagnetic spacer layer  240  separates free layer  230  from reference layer  250 . In some embodiments, nonmagnetic spacer layer is a tunneling barrier layer, such as crystalline MgO. In some embodiments, nonmagnetic spacer layer  240  may be a conductive or other layer. A magnetoresistance depending upon the relative orientations of magnetic moments  232  and  252  is developed across nonmagnetic spacer layer  240 . For example, for magnetic junction  200 A being an MTJ, a tunneling magnetoresistance across tunneling barrier layer  240  is high if magnetic moments  232  and  252  are antiparallel and low if magnetic moments  232  and  252  are parallel (this describes the case where both magnetic layers have positive spin polarization). 
     Reference layer magnetic moment  252  may be fixed by the magnetic properties of reference layer  250 . In the embodiment shown, for example, reference layer  250  has a stable magnetic moment  252  perpendicular-to-plane. In other embodiments, an optional pinning layer (not shown) may be used to fix the magnetization (not shown) of reference layer  250 . The optional pinning layer may be an AFM layer or multilayer that pins the magnetic moment  252  of reference layer  250  by an exchange-bias interaction. Although shown as a simple layer, reference layer  250  may be a synthetic layer. Reference layer  250  may thus contain or consist of a synthetic antiferromagnetic or synthetic ferrimagnetic structure. For example, reference layer  250  may include multiple magnetic layers separated by and antiferromagnetically coupled through nonmagnetic layer(s). For example, reference layer  250  may include two magnetic layers antiferromagnetically coupled through a nonmagnetic layer via the Ruderman-Kittel-Kasuya-Yosida (RKKY) interaction. Other multilayered structures can be used in or for reference layer  250 . For example, reference layer  250  may be or include a multilayered structure including or composed of a combination of ferromagnetic metals (e.g. CoFeB, Fe, Co, and/or CoFe), refractory metals (e.g. Ta, Mo, and/or W), exchange coupling metals (e.g. Ir, Ru, Rh, and/or Cr) and/or Co-based hard magnets (e.g. CoPt, Co/Pt, CoNi, Co/Ni, CoPd, Co/Pd). Reference layer  250  may contain synthetic antiferromagnetic or synthetic ferrimagnetic structure. 
     Reference layer  250  may also include one or more Heusler compounds. For example, reference layer  250  may be a multilayered structure including or composed of any one or more of perpendicularly magnetized Heusler alloys (e.g. Mn 3 Ge, Mn 3 Al, Mn 3 Sb, Mn 3 Ga, Mn 3 Sn, Mn 3 In, Mn 2 CoSn), L1 0  ordered alloys (e.g. FePt, FePd, MnAl, MnSb, MnGa, MnSn, MnGe), and exchange coupling metals (Ir, Ru, Rh, Cr, RuAl, IrAl). In such a case, Reference layer may use a seed layer. For example, the seed layer may include or consist of one of more of Ta, Ru, Fe, Ir, CoFeB, MgO, Ta—N, Ti—N, Mn—N, VN, Cu—N, ScN, IrAl, CoGe, CoSn, NiAl, FeAl, CoAl, RuAl, Cr, and Cr—Ru. 
     Free layer  230 , resistive insertion layer  220  and templating structure  210 A are analogous to magnetic layer  130 , resistive insertion layer  120  and templating structure  110 A, respectively, of magnetic structure  100 A. Free layer  230  includes a Heusler compound having a high PMA. In some embodiments, free layer  230  includes only Heusler compound(s). Thus, the structure, composition, and properties of templating structure  210 A, resistive insertion layer  220  and free layer  230  are analogous to those of templating structure  110 A, resistive insertion layer  120 , and magnetic layer  130 , respectively. 
     Although it is a resistive layer, the total resistance of resistive insertion layer  220  is desired to have a small effect on operation of magnetic junction  200 A. Thus, the resistance of resistive insertion layer  220  is desired to be relatively small in comparison to tunneling barrier layer  240 . For example, the resistance of resistive insertion layer  220  may be not more than ten percent of the tunneling barrier resistance. In some embodiments, the resistance of resistive insertion layer  220  may be not more than five percent of the resistance of tunneling barrier layer  240 . In some such embodiments, the resistance of resistive insertion layer  220  may be not more than two percent of the tunneling barrier resistance. The resistance area product of resistive insertion layer  220  is thus smaller than the resistance area product of tunneling barrier layer  240 . Consequently, the parasitic resistance due to resistive insertion layer  220  may be reduced. 
     The presence of resistive insertion layer  220  may reduce magnetic damping for magnetic junction  200 A. Insertion layer  220  may reduce the movement of electrons between free layer  230  and templating structure  210 A. To program magnetic junction  200 A using STT, a spin polarized current is driven through free layer  230 . For example, for a current driven from substrate  201  to capping layer  260 , electrons travel through reference layer  250  and become spin polarized in the direction of magnetic moment  252 . Electrons in the spin polarized current transfer their angular moment to free layer  230 . The relatively higher resistance of resistive insertion layer  220  reduced or precludes the movement of electrons from free layer  230  to templating structure  210 A. Thus, magnetic damping may be reduced. Free layer  230  may be written using a smaller magnitude write current and/or a shorter current pulse width. Thus, performance of a magnetic junction  200 A may be improved. 
       FIG. 2B  depicts magnetic junction  200 B residing on substrate  201 . Magnetic junction  200 B includes resistive insertion layer  220 , free layer  230 , nonmagnetic spacer layer  240 , reference layer  250 , and capping layer  260  that are analogous to resistive insertion layer  220 , free layer  230 , nonmagnetic spacer layer  240  reference layer  250 , and capping layer  260  depicted in  FIG. 2A , respectively. Further, resistive insertion layer  220 , templating structure  210 B and free layer  230  are analogous to resistive insertion layer  120 , templating structure  110 B and magnetic layer  130 , respectively, of magnetic structure  100 B. For example, free layer  230  includes or is composed of Heusler compound(s) such as those in magnetic layer  130 . Similarly, templating structure  210 B may be thin (e.g. not more than twenty Angstroms thick in some embodiments) and include any one or more of B2 binary alloys such as CoAl, CoGa, CoGe, CoSn, NiAl, FeAl, IrAl, RuAl, CuZn, and AgZn and/or other cubic-based ordered alloys (e.g. Ag-Mg) having a small (e.g. not more than ten percent and not more than five percent in some embodiments) in-plane lattice mismatch with the Heusler compound of free layer  230 . Resistive insertion layer  220  is configured to reduce magnetic damping for the Heusler compound and allow for templating of the Heusler compound and templating structure  110 . Further, the resistance of resistive insertion layer  220  is sufficiently low that the parasitic resistance due to resistive insertion layer  220  may not adversely affect operation of magnetic junction  200 B. Optional seed layer  204  is used in templating insertion layer  220 . Optional seed layer  204  may include one or more of Ta, Ru, Fe, Ir, CoFeB, MgO, Ta—N, Ti—N, Mn—N, VN, Cu—N, Sc—N, CoSn, CoGe, NiAl, FeAl, CoAl, RuAl, IrAl, Cr, and Cr—Ru. 
     The presence of resistive insertion layer  220  may reduce magnetic damping for magnetic junction  200 B. Insertion layer  220  may reduce the movement of electrons from free layer  230  and templating structure  210 B to seed layer  204  and other layers. Thus, magnetic damping may be reduced. Free layer  230  may be written using a smaller magnitude write current and/or a shorter current pulse width. Thus, performance of a magnetic junction  200 B may be improved. 
       FIG. 2C  depicts magnetic junction  200 C residing on substrate  201 . Magnetic junction  200 C includes resistive insertion layer  220 , free layer  230 , nonmagnetic spacer layer  240 , reference layer  250 , and capping layer  260  that are analogous to resistive insertion layer  220 , free layer  230 , nonmagnetic spacer layer  240  reference layer  250 , and capping layer  260  depicted in  FIG. 2A , respectively. Free layer  230 , resistive insertion layer  220  and templating structure  210 C are analogous to magnetic layer  130 , resistive insertion layer  120  and templating structure  100 B. Resistive insertion layer  220 , templating structure  210 C and free layer  230  are analogous to resistive insertion layer  220 , templating structure  210 B and magnetic layer  230 . 
     Magnetic junction  200 C also includes additional templating structure  270 . Additional templating structure  270  is analogous to templating structure  210 C. Thus, additional templating structure  270  may include any one or more of B2 binary alloys such as CoAl, CoGa, CoGe, CoSn, NiAl, FeAl, IrAl, RuAl, CuZn, and AgZn and/or other cubic-based ordered alloys (e.g. Ag—Mg) having a small (e.g. not more than ten percent and not more than five percent in some embodiments) in-plane lattice mismatch with the Heusler compound of free layer  230 . 
     Resistive insertion layer  220  may reduce magnetic damping for magnetic junction  200 C. Insertion layer  220  may reduce the movement of electrons from free layer  230  and templating structure  210 C to seed layer  204  and other layers. Thus, magnetic damping may be reduced. Free layer  230  may be written using a smaller magnitude write current and/or a shorter current pulse width. Thus, performance of a magnetic junction  200 C may be improved. 
       FIGS. 3A-3B  depict embodiments of magnetic devices  300 A and  300 B including Heusler compounds and having reduced magnetic damping. For clarity,  FIGS. 3A-3B  are not to scale. In the embodiments shown, magnetic devices  300 A and  300 B are top free layer magnetic junctions. Thus, the free layer is further from the substrate than the reference layer in such magnetic junctions. Magnetic devices  300 A and/or  300 B may be used in a variety of electronic devices, such as MRAMs. Although particular layers are shown, other and/or different structures may be included. 
       FIG. 3A  depicts magnetic junction  300 A residing on substrate  301 . Magnetic junction  300 A includes resistive insertion layer  320 , free layer  330 , nonmagnetic spacer layer  340 , and reference layer  350 . Reference layer  350  and free layer  330  are magnetic, having magnetic moments  352  and  332 , respectively. In the embodiment shown, each of free layer  330  and reference layer  350  have a PMA anisotropy energy that exceeds the out-of-plane demagnetization energy. Consequently, magnetic moments  332  and  352  are shown as perpendicular to plane. Magnetic moment  332  of free layer  330  may be programmed to be in one of multiple stable states. Magnetic moment  332  is shown as dual headed arrow. Magnetic moment  352  of reference layer  350  is stable in the embodiment shown. Consequently, magnetic moment  352  is shown as a single arrow. Although shown in a particular direction (toward the top of the page), magnetic moment  352  may be stable in another direction (e.g. toward the bottom of the page). Magnetic junction  300 A may also include optional polarization enhancement layer(s) (PEL(s)) having a high spin polarization. For example, a PEL might include Fe, CoFe and/or CoFeB. The PEL may be between reference layer  350  and nonmagnetic spacer layer  340  and/or between nonmagnetic spacer layer  340  and free layer  330 . Also shown are optional seed layer(s)  304  and optional capping layer(s)  360 . Optional capping layer  360  is analogous to optional capping layer  260 . Optional seed layer  304  is appropriate for forming reference layer  350 . For example, reference layer  350  may be a multilayered structure including or composed of a combination of ferromagnetic metals (e.g. CoFeB, Fe, Co, and/or CoFe), refractory metals (e.g. Ta, Mo, and/or W), exchange coupling metals (e.g. Ir, Ru, Rh, and/or Cr) and/or Co-based hard magnets (e.g. CoPt, Co/Pt, CoNi, Co/Ni, CoPd, Co/Pd). In some embodiments, reference layer  350  may contain synthetic antiferromagnetic or synthetic ferrimagnetic structure. In such a case, seed layer  304  may include or be composed of any one or more of a combination of Ta, Ru, Ir, Pt, CoFeB, and metallic nitrides (e.g. Ta—N, Ti—N, Mo—N, Cu—N and the like). In some such magnetic junctions, an additional nonmagnetic spacer layer and an additional reference layer may be interposed between free layer  330  and capping layer  360 . Thus, dual magnetic junctions may be formed. 
     Free layer  330  and resistive insertion layer  320  are analogous to magnetic layer  130  and resistive insertion layer  120  of magnetic structure  100 C. However, a structure analogous to templating structure  110 C has been omitted. Magnetic junction  300 A thus has no templating structure for free layer  330 . The presence of resistive insertion layer  320  may reduce magnetic damping for magnetic junction  300 A in a manner analogous to that described above. 
     Resistive insertion layer  320  may reduce the unwanted movement of electrons. To program magnetic junction  300 A using STT, a spin polarized current is driven through free layer  330 . Electrons in the spin polarized current transfer their angular moment to free layer  330 . The relatively higher resistance of resistive insertion layer  320  reduced or precludes the movement of electrons from free layer  330 . Thus, magnetic damping may be reduced. Free layer  330  may be written using a smaller magnitude write current and/or a shorter current pulse width. Thus, performance of a magnetic junction  300 A may be improved. 
       FIG. 3B  includes magnetic junction  300 B that is analogous to magnetic junction  300 A. Magnetic junction  300 B includes resistive insertion layer  320 , free layer  330 , nonmagnetic spacer layer  340 , and reference layer  350  analogous to those used for magnetic junction  300 B. However, magnetic junction  300 B includes a templating structure  310 B. Further, templating structure  310 B may be magnetic. Free layer  330 , templating structure  310  and resistive insertion layer  320  are analogous to magnetic layer  130 , templating structure  110 C and resistive insertion layer  120 . Thus, the structure, composition and performance of layers  330 ,  320  and  310 B are analogous to layers  130 ,  120 , and  110 C, respectively. For example, templating structure  310 B may be thin, magnetic and include Co (1-x) Al x , where xis less than 0.4. 
     The presence of resistive insertion layer  320  may reduce magnetic damping for magnetic junction  300 A. Insertion layer  320  may reduce the unwanted movement of electrons. Thus, magnetic damping may be reduced. Free layer  330  may be written using a smaller magnitude write current and/or a shorter current pulse width. Thus, performance of a magnetic junction  300 B may be improved. 
       FIG. 4  is a flow chart depicting an embodiment of method  400  for fabricating magnetic structure. For simplicity, some steps may be omitted, performed in another order, include substeps and/or combined. Although described in the context of single components, multiple components may be fabricated. For example, multiple magnetic structures may be fabricated. Further, the method  400  may start after other steps in forming a magnetic device including the magnetic structure have been performed. For simplicity, the method  400  is described in the context of the magnetic structures  100 A,  100 B and  100 C. However, other magnetic structures may be formed. 
     A templating structure is provided, at  402 . For magnetic structures  100 A and  100 C, providing the templating structure is performed prior to formation of the magnetic and resistive insertion layers. For magnetic structure  100 B, resistive insertion layer  120  is provided first. The templating structure formed at  402  is appropriate for the magnetic structure being fabricated. In some embodiments,  402  includes depositing or growing one or more layers of the templating structure. The layers may be deposited at a particular temperature range. For example, the templating structure may be deposited at a specific temperature or at a specific range of temperature. In some embodiments, the templating structure is provided within a range of temperatures including temperature(s) of not less than 70K and not more than 700K. Deposition methods may include but are not limited to PVD sputtering, pulse lased deposition, atomic layer deposition, ion-beam deposition, plasma enhanced chemical vapor deposition and/or other deposition mechanism(s). The fabrication of a layer may include annealing the layer. In-situ annealing (e.g. in vacuum or in any specific gas environment) may be performed right after deposition of any layer shown in each embodiment. Annealing may also occur later in fabrication (e.g. while the surface of the layer is exposed or after deposition of other layer(s)). The range of temperatures for in-situ annealing includes but may not be limited to at least 350K through not more than 700K. 
     A magnetic layer including one or more Heusler compounds is provided, at  404 . In some embodiments, such as when method  400  is used to form magnetic structure  100 C,  404  is performed before formation of the resistive insertion layer. In other embodiments, such as for fabricating magnetic structure  100 A or  100 B,  404  is performed after  402  and formation of the resistive insertion layer. In some embodiments,  404  may be performed using the same techniques, temperature ranges and processes as described for  402 . 
     A resistive insertion layer is provided, at  406 . In some embodiments, such as for fabricating magnetic structure  100 B,  406  is performed before formation of the templating structure and the magnetic layer including Heusler compound(s). In other embodiments, such as for fabricating magnetic structure  100 A or  100 C,  406  is performed later. If magnetic structure  100 C is formed,  406  may include fabricating an amorphous resistive insertion layer. In some embodiments,  406  may be performed using the same techniques, temperature ranges and processes as described for  402 . 
     Thus, using method  400 , magnetic structures  100 A,  100 B, and/or  100 C may be formed. Thus, the benefits described herein may be achieved. In particular, a high PMA (e.g. stable magnetic moment perpendicular to plane), high TMR may be achieved with reduced magnetic damping. 
       FIG. 5  is a flow chart depicting an embodiment of method  500  for fabricating magnetic device, such as magnetic junctions written using spin transfer torque and including a magnetic structure. For simplicity, some steps may be omitted, performed in another order, include substeps and/or combined. Although described in the context of single components, multiple components may be fabricated. For example, multiple magnetic junctions may be formed. Further, the method  500  may start after other steps in forming a magnetic device have been performed. 
     A seed layer may optionally be provided, at  502 . In some embodiments,  502  provides the appropriate seed for the particular embodiment being fabricated. For example, in some embodiments,  502  includes providing a Mn x N seed layer.  502  may also include fabricating an additional templating layer, such as templating structure  270  of magnetic device  200 B. 
     A templating structure is provided, at  504 . In some embodiments,  504  is analogous to  402 . The layers may be deposited at a particular temperature range. For example, the templating structure may be deposited at a specific temperature or at a specific range of temperature. In some embodiments, the templating structure is provided within a range of temperatures including temperature(s) of not less than 70K and not more than 700K. Deposition methods may include but are not limited to PVD sputtering, pulse lased deposition, atomic layer deposition, ion-beam deposition, plasma enhanced chemical vapor deposition and/or other deposition mechanism(s). The fabrication of a layer may include annealing the layer. In-situ annealing (e.g. in vacuum or in any specific gas environment) may be performed right after deposition of any layer shown in each embodiment. Annealing may also occur later in fabrication (e.g. while the surface of the layer is exposed or after deposition of other layer(s)). The range of temperatures for in-situ annealing includes but may not be limited to at least 350K through not more than 700K. 
     A resistive insertion layer is provided, at  506 . In some embodiments,  506  is analogous to  406 . In some embodiments, such as for fabricating magnetic junction  200 B,  506  is performed before formation of the templating structure and the magnetic layer including Heusler compound(s). In other embodiments, such as for fabricating magnetic junctions  200 A or  300 C,  506  is performed later. In some embodiments,  506  may be performed using the same techniques, temperature ranges and processes as described for  406 . 
     A free layer including one or more Heusler compounds is provided, at  508 . In some embodiments  508  is analogous to  404 . A nonmagnetic spacer layer, such as a tunneling barrier layer, and a reference layer are provided, at  510  and  512 , respectively. 
     Thus, using method  500 , magnetic devices  200 A,  200 B,  200 C,  300 A and/or  300 B may be formed. Thus, the benefits described herein may be achieved. In particular, a high PMA (e.g. stable magnetic moment perpendicular to plane), high TMR may be achieved with reduced magnetic damping. 
     Although the foregoing embodiments have been described in some detail for purposes of clarity of understanding, the invention is not limited to the details provided. There are many alternative ways of implementing the invention. The disclosed embodiments are illustrative and not restrictive.