Patent Publication Number: US-11639472-B2

Title: Circular economy for plastic waste to polyethylene via oil refinery with filtering and metal oxide treatment of pyrolysis oil

Description:
The present application claims priority to U.S. Provisional Patent Application No. 63/014,004, filed Apr. 22, 2020, the contents of which are herein incorporated by reference in their entirety. 
    
    
     BACKGROUND 
     The world has seen extremely rapid growth of plastics production. According to PlasticsEurope Market Research Group, the world plastics production was 335 million tons in 2016, 348 million tons in 2017 and 359 million tons in 2018. According to McKinsey &amp; Company, the global plastics-waste volume was estimated about 260 million tons per year in 2016, and projected to be 460 million tons per year by 2030 if the current trajectory continues. 
     Single use plastic waste has become an increasingly important environmental issue. At the moment, there appear to be few options for recycling polyethylene and polypropylene waste plastics to value-added chemical and fuel products. Currently, only a small amount of polyethylene and polypropylene is recycled via chemical recycling, where recycled and cleaned polymer pellets are pyrolyzed in a pyrolysis unit to make fuels (naphtha, diesel), steam cracker feed or slack wax. 
     Processes are known which convert waste plastic into hydrocarbon lubricants. For example, U.S. Pat. No. 3,845,157 discloses cracking of waste or virgin polyolefins to form gaseous products such as ethylene/olefin copolymers which are further processed to produce synthetic hydrocarbon lubricants. U.S. Pat. No. 4,642,401 discloses the production of liquid hydrocarbons by heating pulverized polyolefin waste at temperatures of 150-500° C. and pressures of 20-300 bars (2-30 MPa). U.S. Pat. No. 5,849,964 discloses a process in which waste plastic materials are depolymerized into a volatile phase and a liquid phase. The volatile phase is separated into a gaseous phase and a condensate. The liquid phase, the condensate and the gaseous phase are refined into liquid fuel components using standard refining techniques. U.S. Pat. No. 6,143,940 discloses a procedure for converting waste plastics into heavy wax compositions. U.S. Pat. No. 6,150,577 discloses a process of converting waste plastics into lubricating oils. EP0620264 discloses a process for producing lubricating oils from waste or virgin polyolefins by thermally cracking the waste in a fluidized bed to form a waxy product, optionally using a hydrotreatment, then catalytically isomerizing and fractionating to recover a lubricating oil. 
     Other documents which relate to processes for converting waste plastic into lubricating oils include U.S. Pat. Nos. 6,288,296; 6,774,272; 6,822,126; 7,834,226; 8,088,961; 8,404,912; and 8,696,994; and U.S. Patent Publication Nos. 2019/0161683; 2016/0362609; and 2016/0264885. The foregoing patent documents are incorporated herein by reference in their entirety. 
     The current method of chemical recycling via pyrolysis cannot make a big impact for the plastics industry. The current pyrolysis operation produces poor quality fuel components (naphtha and diesel range products), but the quantity is small enough that these products can be blended into fuel supplies. However, this simple blending cannot continue if very large volumes of waste polyethylene and polypropylene are to be recycled to address environmental issues. The products as produced from a pyrolysis unit are of too poor quality to be blended in large amounts (for example 5-20 vol. % blending) in transportation fuels. 
     In order to achieve recycling of single use plastics in an industrially significant quantity to reduce its environmental impact, more robust processes are needed. The improved processes should establish “circular economy” for the waste polyethylene and polypropylene plastics where the spent waste plastics are recycled effectively back as starting materials for polymers and high value byproducts. 
     SUMMARY 
     Provided is a continuous process for converting waste plastic into recycle for polyethylene polymerization. The process comprises selecting waste plastics containing polyethylene and/or polypropylene. These waste plastics are then passed through a pyrolysis reactor to thermally crack at least a portion of the polyolefin waste and produce a pyrolyzed effluent. The pyrolyzed effluent is separated into offgas, a pyrolysis oil comprising naphtha, diesel and heavy fractions, and char. Pyrolysis wax can also be produced in addition to pyrolysis oil. 
     The incorporation of the process with an oil refinery is an important aspect of the present process, and allows the creation of a circular economy with a single use waste plastic such as polyethylene or polypropylene. Thus, the pyrolysis oil, for example, the entire liquid fraction from the pyrolysis unit, is passed to a refinery FCC unit from which can be recovered liquid petroleum olefin streams. These liquid petroleum olefin streams can be passed directly to a steam cracker for ethylene production. The ethylene is then passed to a polymerization unit for polyethylene production. 
     Another important aspect of the present process is the upgrading of the liquid pyrolysis product before the stream is integrated with a refinery unit. The pyrolysis oil and wax waste plastics contain contaminants that cannot be fed in a large quantity to refinery units, such as an FCC unit, as they deactivate the refining catalysts, cause plugging in the unit or cause corrosion in processing units, which are commonly made of carbon steel. The use of fine filtration followed by a metal oxide treatment has been found to be an effective treatment process to upgrade the pyrolysis products for then safely processing in refinery units. The use of the fine filtration and metal oxide treatment allows effective recycling in large volumes when integrated with a refinery. 
     In another embodiment, a continuous process for converting waste plastic comprising polyethylene into recycle for polyethylene polymerization is provided. The process comprises selecting waste plastics containing polyethylene and/or polypropylene and then passing the waste plastics through a pyrolysis reactor to thermally crack at least a portion of the polyolefin waste and produce a pyrolyzed effluent. The pyrolyzed effluent is separated into offgas, a pyrolysis oil comprising naphtha, diesel and heavy fractions, and char. The pyrolysis oil, the entire liquid fraction from the pyrolysis unit, is subjected to a fine filtration and then a metal oxide treatment. The resulting treated pyrolysis product is then safely passed to a refinery FCC unit. The FCC unit will convert the treated pyrolysis oil product into FCC hydrocarbon product. The FCC product is sent to a FCC unit separation section to produce offgas, C 3 , C 4 , FCC gasoline and heavy fractions. From the separation section, a clean C 3  liquid petroleum gas (LPG) fraction containing propane and propylene is collected. The C 3  stream is a good feed for a steam cracker. The C 3  stream is fed to a steam cracker distillation section to separate into propane and propylene. Then, propane is fed to the steam cracker to be converted to pure ethylene. The ethylene is then polymerized, and subsequently made into polyethylene products. 
     The FCC gasoline recovered is sent to a gasoline blending pool. The heavy portion of the hydrocarbon from the FCC unit distillation is sent to appropriate refinery units for upgrading into clean gasoline and diesel. The C 4  LPG fraction recovered contains butanes and butenes and can also be sent to various upgrading processes to make clean gasoline and diesel. 
     In one embodiment, the treated pyrolysis oil is passed to a refinery FCC Feed Pretreater Unit prior to the FCC unit. This unit is effective in removing sulfur, nitrogen, phosphorus, silica, dienes and metals that will hurt a FCC unit catalyst performance. Also this unit hydrogenates aromatics and improves the liquid yield of the FCC unit. 
     Among other factors, it has been found that by adding refinery operations one can upgrade the waste pyrolysis oil and wax to higher value products such as gasoline, diesel, and base oil. Also, by adding refinery operations it has been found that clean naphtha (C 5 -C 8 ) or C 4  or C 3  can be efficiently and effectively produced from the waste pyrolysis oil for ultimate polyethylene polymer production. Positive economics are realized for the overall process from recycled plastics to a polyethylene product with product quality identical to that of virgin polymer. It has been further discovered that a most effective process is achieved upon upgrading the pyrolysis oil prior to integration into the refinery operation. Utilizing a combination of fine filtration with a metal oxide treatment has been found most effective. Such filtration/metal oxide treatments of the pyrolysis oil safely allows much larger volumes of waste plastic recycle. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG.  1    depicts the current practice of pyrolyzing waste plastics to produce fuel or wax (base case). 
         FIG.  2    depicts a present process for filtration/metal oxide treatment of pyrolysis oil at a pyrolysis facility. 
         FIG.  3    depicts a present process for establishing a circular economy for waste plastics to recycled polyethylene in accordance with the present processes including filtration/metal oxide treatment of pyrolysis oil. 
         FIG.  4    depicts a present process for establishing a circular economy for waste plastics to recycled polyethylene in accordance with the present processes including filtration/metal oxide treatment of pyrolysis oil occurring in a refinery. 
         FIG.  5    depicts the plastic type classification for waste plastics recycling. 
     
    
    
     DETAILED DESCRIPTION 
     In the present process, provided is a method to recycle waste polyethylene and/or polypropylene back to virgin polyethylene and establish a circular economy by combining distinct industrial processes. A substantial portion of polyethylene and polypropylene polymers are used in single use plastics and get discarded after its use. The single use plastic waste has become an increasingly important environmental issue. At the moment, there appear to be few options for recycling polyethylene and polypropylene waste plastics to value-added chemicals and fuel products. Currently, only a small amount of polyethylene/polypropylene is recycled via chemical recycling, where recycled and cleaned polymer pellets are pyrolyzed in a pyrolysis unit to make fuels (naphtha, diesel), steam cracker feed or slack wax. 
     Ethylene is the most produced petrochemical building block. Ethylene is produced in hundreds of millions of tons per year via steam cracking. The steam crackers use either gaseous feedstocks (ethane, propane and/or butane) or liquid feed stocks (naphtha or gas oil). It is a noncatalytic cracking process operating at very high temperatures, up to 850° C. 
     Polyethylene is used widely in various consumer and industrial products. Polyethylene is the most common plastic, over 100 million tonnes of polyethylene resins are produced annually. Its primary use is in packaging (plastic bags, plastic films, geomembranes, containers including bottles, etc.). Polyethylene is produced in three main forms: high-density polyethylene (HDPE, ˜0.940-0.965 g/cm −3 ), linear low-density polyethylene (LLDPE, ˜0.915-0.940 g/cm −3 ) and low-density polyethylene (LDPE, (&lt;0.930 g/cm −3 ), with the same chemical formula (C 2 H 4 ) n  but different molecular structure. HDPE has a low degree of branching with short side chains while LDPE has a very high degree of branching with long side chains. LLDPE is a substantially linear polymer with significant numbers of short branches, commonly made by copolymerization of ethylene with short-chain alpha-olefins. 
     Low density polyethylene (LDPE) is produced via radical polymerization at 150-300° C. and very high pressure of 1,000-3,000 atm (101-304 MPa). The process uses a small amount of oxygen and/or organic peroxide initiator to produce polymer with about 4,000-40,000 carbon atoms per the average polymer molecule, and with many branches. High density polyethylene (HDPE) is manufactured at relatively low pressure (10-80 atm, 1-8 MPa) and 80-150° C. temperature in the presence of a catalyst. Ziegler-Natta organometallic catalysts (titanium(III) chloride with an aluminum alkyl) and Phillips-type catalysts (chromium(IV) oxide on silica) are typically used, and the manufacturing is done via a slurry process using a loop reactor or via a gas phase process with a fluidized bed reactor. Hydrogen is mixed with ethylene to control the chain length of the polymer. Manufacturing conditions of linear low-density polyethylene (LLDPE) is similar to those of HDPE except copolymerization of ethylene with short-chain alpha-olefins (1-butene or 1-hexene). 
     Today, only a small portion of spent polyethylene and polypropylene products are collected for recycling efforts due to the inefficiencies discussed above. The present process allows larger volumes of single use plastic waste to be safely recycled by using a process integrated with a refinery. A circular economy is effectively established by the present process. 
       FIG.  1    shows a diagram of pyrolysis of waste plastics fuel or wax that is generally operated in the industry today. As noted above, generally, polyethylene and polypropylene wastes are sorted together  1 . The cleaned polyethylene/polypropylene waste  2  is converted in a pyrolysis unit  3  to offgas  4  and pyrolysis oil (liquid product). The offgas  4  from the pyrolysis unit is used as fuel to operate the pyrolysis unit. A distillation unit in the pyrolysis unit separates the pyrolysis oil to produce naphtha and diesel  5  products which are sold to fuel markets. The heavy pyrolysis oil fraction  6  is recycled back to the pyrolysis unit  3  to maximize the fuel yield. Char  7  is removed from the pyrolysis unit  3 . The heavy fraction  6  is rich in long chain, linear hydrocarbons, and is very waxy (i.e., forms paraffinic wax upon cooling to ambient temperature). Wax can be separated from the heavy fraction  6  and sold to the wax markets. 
     It has been discovered that an upgrading of the pyrolysis oil prior to introduction into refinery units improves the effectiveness and safety of the overall process. More specifically, critical materials that need to be removed from the pyrolysis products for co-feeding to a refinery unit includes components such as residual char, metals and chlorides. Pyrolysis products with these impurities cannot be fed in large quantity to refinery units as chars and inorganic solids will cause plugging in the unit, metals will deactivate the refining catalysts permanently and chlorides will cause corrosion in processing equipment. Reduction of chloride impurity is particularly important prior to feeding to refinery units as chlorides may cause severe corrosion on bare carbon steel with which most of refinery units are constructed. The chloride induced corrosion will be particularly accelerated at elevated temperatures above 500° F. (260° C.), where most of refinery units are operating. 
     The pyrolysis product treatment of the present process can be done efficiently in conjunction with the pyrolysis unit during the pyrolysis oil and wax manufacturing. Or the treatment can be done at the refinery before feeding the pyrolysis oil and wax to the refinery units. The present fine filtration and metal oxide treatment process does not reduce S and N impurities, nor olefin and diene contents. In the present process for circular economy establishment, conversion of these compounds are effectively achieved by refinery units such as a fluid catalytic cracking (FCC) unit, a FCC feed pretreater, refinery crude unit, coker, distillate hydrotreater or hydrocracker. 
     The present process converts pyrolyzed polyethylene and/or polypropylene waste plastic in large quantities by integrating the waste polymer pyrolysis product streams into an oil refinery operation. The resulting processes produce the feedstocks for the polymers (naphtha or C 3 -C 4  or C 3  only for an ethylene cracker), high quality gasoline, jet and diesel fuel, and/or quality base oil. 
     Generally, the present process provides a circular economy for polyethylene plants. Polyethylene is produced via polymerization of pure ethylene. Clean ethylene can be made using a steam cracker. Either naphtha or a C 3  or C 4  stream can be fed to the steam cracker. The ethylene is then polymerized to create polyethylene. 
     By adding refinery operations to upgrade the waste pyrolysis oil to higher value products (gasoline and diesel, base oil) and to produce clean LPG and naphtha for a steam cracker for ultimate polyethylene polymer production, one is able to create positive economics for the overall process from recycled plastics to polyethylene product with quality identical to that of the virgin polymer. 
     A pyrolysis unit produces poor quality products containing contaminants, such as calcium, magnesium, chlorides, nitrogen, sulfur, phosphorus, silicon, dienes, and heavy components, which products cannot be used in large quantity for blending in transportation fuels. It has been discovered that by having these products go through the refinery units, the contaminants can be captured in pre-treating units and their negative impacts diminished. The fuel components can be further upgraded with appropriate refinery units with chemical conversion processes, with the final transportation fuels produced by the integrated process being of higher quality and meeting the fuels quality requirements. The present process will upgrade the wax into valuable gasoline, diesel and base oil. The integrated process will generate much cleaner naphtha stream as steam cracker feedstock for ethylene generation and polyethylene production. These large on-spec productions allow “cyclical economy” for the recycle plastics feasible. 
     However, it has been discovered, and is an important aspect of the present process, that upgrading of the pyrolysis product is still needed before the stream is integrated with a refinery unit. The pyrolysis oil and wax waste plastics contain contaminants that cannot be fed in large quantity to refinery units as they deactivate the refining catalysts or cause plugging in the unit or cause severe corrosion in processing units which are commonly made of bare carbon steel. 
       FIG.  2    depicts a process sequence of a fine filtration and metal oxide treatment. In  FIG.  2   , the cleaned polyethylene/polypropylene waste  22  is passed through a pyrolysis reactor  23  to thermally crack at least a portion of the polyolefin waste and produce a pyrolyzed effluent. Char  26  is generally removed from the pyrolysis reactor  23 . The effluent is passed through a heat exchange  60  for partial cooling and then to a gas-liquid separation unit  61 . Offgas  24  can be used as fuel to operate the pyrolysis unit. The liquid product from the pyrolysis effluent is then passed to a fine filtration unit  27 - 1 . Optionally, any pyrolysis wax produced can also be passed to the fine filtration (and metal oxide treatment). 
     The fine filtration unit removes solids in the pyrolysis oil, particularly chars created by the pyrolysis process and inorganic solids arising from contamination. Metals are often present as inorganic solids in the form of metal chlorides, metals or metal oxides. Thus, the fine filtration process reduces the contaminants coming from chars, metals, metal oxides and metal chlorides. A very fine filter medium needs to be used, preferentially less than 5 micron, more preferentially less than 2.5 micron and most preferentially less than 1 micron nominal-rated filter. Multiple filter units with different size filter elements may be used in series. These filter media are well known for industrial uses. The filter media must be able to withstand the temperature of the pyrolysis oil as well as the chemical nature of especially the contaminants. The residual solid content can be measured, for example, by the Heptane Insolubles test, ASTM D-3279 method. The content of Heptane Insolubles needs to be reduced to less than 0.5 wt. %, preferably less than 0.1%. 
     After the filtration, the filtered liquid effluent is passed to metal oxide treatment  27 - 2 . The metal oxide treatment removes organic chlorides and metals from the filtered pyrolysis oil. The chloride and impurity removal is more effective when the metal oxide treatment temperature is done above 200° F. (93° C.), preferentially above 300° F. (149° C.), and most preferentially above 400° F. (204° C.). Preferred pressure range is from atmospheric pressure to 1000 psig, preferentially from 0 psig to 600 psig. To reduce fouling of metal oxide and to improve the performance, optionally H 2  gas may be added to the treating process. The preferred amount of H 2  gas flow is ranging from 0 to 2000 scf/bbl of pyrolysis oil. Metal oxides with high surface area can also capture additional contaminants. Metal oxides such as Cao, ZnO, MgO, alumina, silica, clay, and silica-alumina are effective for chloride removal. Mixed metal oxides made of Mg, Ca, Al or Zn, or combination of these are particularly effective for organic chloride removal. It is desirable to reduce the chloride content to less than 10 ppm, preferably less than 5 ppm and most preferably less than 1 ppm. Metal oxides made of Ni, Mo, phosphate, alumina, silica and silica-alumina or combination of these are particularly effective for residual metals removal while they can also remove other contaminants such as chlorides, nitrogen, phosphorus and silicon. It is desirable to reduce the total residual metals content to less than 10 ppm, preferably less than 5 ppm. Combination of different metal oxides can be used for effective removal of impurities. 
     The treated effluent can then be cooled in heat exchanger  62 , with the entire treated, liquid product (naphtha, distillate and heavy fraction)  25  then passed on to refinery unit  63 . 
       FIG.  3    and  FIG.  4    show the present integrated process, the filtering and metal oxide treatment, and the integrating of refinery operations with recycle for effective polyethylene production. The same numbers in  FIG.  2   ,  FIG.  3   , and  FIG.  4    refer to the same type of units and product streams. In  FIG.  3    and  FIG.  4   , mixed waste plastics are sorted together  21 . The cleaned waste plastic  22  is converted in a pyrolysis unit  23  to offgas  24  and a pyrolysis oil (liquid product), and at times a wax (solid product at ambient temperature). The offgas  24  from the pyrolysis unit can be used as fuel to operate the pyrolysis unit  23 . The pyrolysis oil, the entire liquid product  25 , comprises the naphtha/diesel distillate/heavy fractions. Char  26  is removed from the pyrolysis unit  23  after completion of the pyrolysis step. 
     The pyrolysis unit can be located near the waste plastics collection site, which site could be away from a refinery, near a refinery, or within a refinery. If the pyrolysis unit is located away from the refinery, then pyrolysis oil (naphtha/diesel and heavies) can be transferred to the refinery by truck, barge, rail car or pipeline. It is preferred, however, that the pyrolysis unit is within the waste plastics collection site or within the refinery. 
     In  FIG.  3   , a fine filtration and metal oxide treatment  27  is effected at the pyrolysis facility. The whole liquid pyrolysis product  25  from the pyrolysis unit  23  is sent to the filtration unit followed by an oxide treatment. It is preferred that the hot pyrolysis liquid is filtered and treated with the metal oxide before it is completely cooled to ambient temperature for storage and/or transfer. Thus, it is preferred for the filtration and metal oxide treatment to occur at the pyrolysis facility after the whole liquid product  25  is recovered, or to occur simultaneously with the whole liquid product collection step. The treated liquid product can then be transferred to the refinery. 
     In  FIG.  4   , in another embodiment, the whole liquid product  25  is transferred to a refinery. The fine filtration and metal oxide treatment  27  is completed at the refinery. 
     The preferred starting material for the present process is sorted waste plastics containing predominantly polyethylene and polypropylene (plastics recycle classification types  2 ,  4 , and  5 ). The pre-sorted waste plastics are washed and shredded or pelleted to feed to a pyrolysis unit for thermal cracking.  FIG.  5    depicts the plastic type classification for waste plastics recycling. Classification types  2 ,  4 , and  5  are high density polyethylene, low density polyethylene and polypropylene, respectively. Any combination of the polyethylene and polypropylene waste plastics can be used. For the present process, at least some polyethylene waste plastic is preferred. 
     Proper sorting of waste plastics is very important in order to minimize contaminants such as N, Cl, and S. Plastics waste containing polyethylene terephthalate (plastics recycle classification type  1 ), polyvinyl chloride (plastics recycle classification type  3 ) and other polymers (plastics recycle classification type  7 ) need to be sorted out to less than 5%, preferably less than 1% and most preferably less than 0.1%. The present process can tolerate a moderate amount of polystyrene (plastics recycle classification type  6 ). Waste polystyrene needs to be sorted out to less than 30%, preferably less than 20% and most preferably less than 5%. 
     Washing of waste plastics removes metal contaminants such as sodium, calcium, magnesium, aluminum, and non-metal contaminants coming from other waste sources. Non-metal contaminants include contaminants coming from the Periodic Table Group IVA, such as silica, contaminants from Group VA, such as phosphorus and nitrogen compounds, contaminants from Group VIA, such as sulfur compounds, and halide contaminants from Group VIIA, such as fluoride, chloride, and iodide. The residual metals, non-metal contaminants, and halides need to be removed to less than 50 ppm, preferentially less than 30 ppm and most preferentially to less than 5 ppm. 
     The pyrolyzing is carried out by contacting a plastic material feedstock in a pyrolysis zone at pyrolysis conditions, where at least a portion of the feed(s) is cracked, thus forming a pyrolysis zone effluent comprising primarily 1-olefins and n-paraffins. Pyrolysis conditions include a temperature of from about 400° C. to about 700° C., preferably from about 450° C. to about 650° C. Conventional pyrolysis technology teaches operating conditions of above-atmospheric pressures. See e.g., U.S. Pat. No. 4,642,401. Additionally, it has been discovered that by adjusting the pressure downward, the yield of a desired product can be controlled. See, e.g., U.S. Pat. No. 6,150,577. Accordingly, in some embodiments where such control is desired, the pyrolysis pressure is sub-atmospheric. 
     It has been discovered that the use of the fine filtration, e.g., 5.0 micron or less pore size filter, preferably 1.0 micron or less, and in one embodiment 0.5 micron, followed by the metal oxide treatment is quite beneficial to achieving a feed stream that can be passed efficiently through a refinery without causing problems such as corrosion, plugging or deactivation of catalysts. The treatment thereby allows larger amounts of the waste plastic pyrolysis liquid product to be passed through the refinery for a most effective recycling process. 
       FIG.  3    shows the present integrated process where the entire pyrolysis oil (naphtha, distillate and heavy fractions) after filtering and metal oxide treatment  27 , is sent to a fluid catalytic cracking (FCC) unit  28 . Optionally, only a portion of pyrolysis oil (the distillate and heavy fractions only or the heavy fraction only) can be sent to the FCC unit. In  FIG.  3   , the filtering and metal oxide treatment  27  occurs at the pyrolysis facility. 
     The fluid catalytic cracking (FCC) process is widely used in the refining industry for conversion of atmospheric gas oil, vacuum gas oil, atmospheric residues and heavy stocks recovered from other refinery operations into high-octane gasoline, light fuel oil, heavy fuel oil, olefin-rich light gas (LPG) and coke. FCC uses a high activity zeolite catalyst to crack the heavy hydrocarbon molecules at a 950-990° F. (510-532° C.) reactor temperature in a riser with a short contact time of a few minutes or less. LPG streams containing olefins (propylene, butylene) are commonly upgraded to make alkylate gasoline, or to be used in chemicals manufacturing. A conventional FCC unit is used. 
     Cracking of the pyrolysis liquid oil combined with petroleum derived oil in the FCC unit produces liquefied petroleum gas (LPG) olefin streams  31  and  32 , as well as a gasoline  29  and heavy fraction  30 . A C 2   −  offgas  33  is also produced. 
     The refinery will generally have its own hydrocarbon feed from petroleum derived oil flowing through the refinery units. The flow volume of pyrolysis oil generated from the pyrolysis of waste plastic to the refinery units can comprise any practical or accommodating volume % of the total flow to the refinery units. Generally, the flow of the pyrolysis oil (and wax) generated from the waste plastic pyrolysis, for practical reasons, can be up to about 50 vol. % of the total flow, i.e., the refinery flow and the pyrolysis flow. In one embodiment, the flow of the pyrolysis oil is an amount up to about 20 vol. % of the total flow. In another embodiment, the flow of the pyrolysis oil is an amount up to about 10 vol. % of the total flow. About 20 vol. % has been found to be an amount that is quite practical in its impact on the refinery while also providing excellent results and being an amount that can be accommodated. The amount of pyrolysis oil and wax generated from the pyrolysis can of course be controlled so that the fraction passed to the refinery units provide the desired volume % of the flow. 
     The LPG olefin stream  31  is a C 3  liquid petroleum gas (LPG) fraction containing propane and propylene. This C 3  stream is a good feed for a steam cracker. The C 3  stream  31  is fed to a steam cracker  34 . The C 3  stream can also be fed to a steam cracker distillation section to separate into propane and propylene. In the steam cracker  34 , the propane stream is converted to pure ethylene which is then polymerized  40 . The polyethylene can then be used to produce polyethylene products  41 . 
     The FCC gasoline  29  can be sent to a gasoline blending pool. The heavy portion  30  recovered from the FCC unit  28  is sent to appropriate refinery units  38  (such as hydrotreating, hydrocracking and/or coker units) for upgrading into clean gasoline and diesel  39 . The C 4  stream  32  is either sent to a gasoline blending pool or further upgraded (via processes such as alkylation or C 4  olefin dimerization or ether synthesis) into clean gasoline. 
     In another embodiment, the treated pyrolysis oil is first sent to an FCC feed pretreater (not shown) before the FCC unit. The FCC feed pretreater typically uses a bimetallic (NiMo or CoMo) alumina catalyst in a fixed bed reactor to hydrogenate the feed with H 2  gas flow at a 660-780° F. (349-415° C.) reactor temperature and 1,000-2,000 psi (6.89-13.79 MPa) pressure. The refinery FCC feed pretreater unit is effective in removing sulfur, nitrogen, phosphorus, silica, dienes and metals that will hurt the FCC unit catalyst performance. Also this unit hydrogenates aromatics and improves the liquid yield of the FCC unit. 
       FIG.  4    shows the present integrated process where the entire pyrolysis oil (naphtha, distillate and heavy fractions) is sent to a fluid catalytic cracking (FCC) unit  28 . Optionally, only a portion of pyrolysis oil (the distillate and heavy fractions only or the heavy fraction only) can be sent to the FCC unit. Prior to being sent to the FCC unit, the pyrolysis oil is fine filtered and subjected to a metal oxide treatment  27 . In  FIG.  4   , the filtering and metal oxide treatment occur in the refinery. The pyrolysis oil  25  is transferred to the refinery for treatment  27 . 
     Similar to  FIG.  3   , cracking of the treated pyrolysis liquid oil combined with petroleum derived oil in the FCC unit produces liquefied petroleum gas (LPG) olefin streams  31  and  32 , as well as a gasoline  29  and heavy fraction  30 . A C 2   −  offgas  33  is also produced. 
     The LPG olefin stream  31  is a C 3  liquid petroleum gas (LPG) fraction containing propane and propylene. This C 3  stream is a good feed for a steam cracker. The C 3  stream  31  is fed to a steam cracker  34 . In the steam cracker  34 , the C 3  stream is converted to pure ethylene which is then polymerized  40 . The polyethylene can then be used to produce polyethylene products  41 . 
     The LPG olefin stream  32  is a C 4  liquid petroleum gas (LPG) fraction containing butanes and butenes. This fraction can be sent to a refinery alkylation unit  35  (not shown). 
     The FCC gasoline  29  can be sent to a gasoline blending pool. The heavy portion  30  recovered from the FCC unit  28  is sent to appropriate refinery units  38  for upgrading into clean gasoline and diesel  39 . 
     In another embodiment, the treated pyrolysis oil is first sent to an FCC feed pretreater (not shown). The FCC feed pretreater typically uses a bimetallic (NiMo or CoMo) alumina catalyst in a fixed bed reactor to hydrogenate the feed with H2 gas flow at a 660-780° F. (349-415° C.) reactor temperature and 1,000-2,000 (6.89-13.79 MPa) psi pressure. The refinery FCC feed pretreater unit is effective in removing sulfur, nitrogen, phosphorus, silica, dienes and metals that will hurt the FCC unit catalyst performance. Also this unit hydrogenates aromatics and improves the liquid yield of the FCC unit. 
     Alternatively, instead of sending the C 3  olefin/paraffin mix  31 , recovered from the FCC unit, directly to the steam cracker  34 , the C 3  olefin/paraffin mix stream  31  is directed to a propane/propylene (PP) splitter which is a high efficiency distillation column. A pure propane stream is recovered from the propane/propylene splitter. The pure propane fraction is then passed to the steam cracker  34  for ethylene production. The propylene may be separately polymerized and made into polypropylene consumer products. 
     The ethylene polymerization unit is preferably located near the refinery so that the feedstocks (propane, butane, naphtha) can be transferred via pipeline. For a petrochemical plant located away from the refinery, the feedstock can be delivered via truck, barge, rail car, or pipeline. 
     The carbon in and out of the refinery operations are “transparent,” meaning that all the molecules from the waste plastic do not necessarily end up in the exact olefin product cycled back to the polyolefin plants, but are nevertheless assumed as “credit” as the net “green” carbon in and out of the refinery is positive. With these integrated processes, the amount of virgin feeds needed for polyethylene plants will be reduced substantially. 
     The benefits of a circular economy and an effective and efficient recycling campaign are realized by the present integrated process. The use of the fine filtering and metal oxide treatment permits larger volumes of feed to be circulated safely and efficiently through the refinery. 
     The following non-limiting examples are illustrative of the present process and its benefits. 
     Example 1 
     Properties of Pyrolysis Oil and Wax From Commercial Sources 
     Pyrolysis oil and wax samples were obtained from commercial sources and their properties are summarized in Table 1. These pyrolysis samples were prepared from waste plastics containing mostly polyethylene and polypropylene via thermal decomposition in a pyrolysis reactor at around 400-600° C., near atmospheric pressure without any added gas or a catalyst. A pyrolysis unit typically produces gas, liquid oil product, optionally wax product, and char. The pyrolysis unit&#39;s overhead gas stream containing thermally cracked hydrocarbon was cooled to collect condensate as pyrolysis oil (liquid at ambient temperature) and/or pyrolysis wax (solid at ambient temperature). The pyrolysis oil is the main product of the pyrolysis units. Some units produce pyrolysis wax as a separate product in addition to the pyrolysis oil. 
     
       
         
           
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                 Properties of As-Received Oil and Wax from Pyrolysis of Waste Plastics 
               
            
           
           
               
               
               
               
               
               
            
               
                   
                 Pyrolysis Oil 
                 Pyrolysis Oil 
                 Pyrolysis Oil 
                 Pyrolysis Oil 
                 Pyrolysis Wax 
               
               
                   
                 Sample A 
                 Sample B 
                 Sample C 
                 Sample D 
                 Sample E 
               
               
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 Specific Gravity at 60° F. 
                 0.814 
                 0.820 
                 0.774 
                 — 
                 0.828 
               
               
                 Simulated Distillation, ° F. 
                   
                   
                   
                   
                   
               
               
                 0.5% (Initial Boiling Point) 
                 87 
                 299 
                 18 
                 86 
                 325 
               
               
                    5% 
                 179 
                 306 
                 129 
                 154 
                 475 
               
               
                   10% 
                 214 
                 309 
                 156 
                 210 
                 545 
               
               
                   30% 
                 322 
                 346 
                 285 
                 304 
                 656 
               
               
                   50% 
                 421 
                 447 
                 392 
                 421 
                 733 
               
               
                   70% 
                 545 
                 585 
                 517 
                 532 
                 798 
               
               
                   90% 
                 696 
                 798 
                 663 
                 676 
                 894 
               
               
                   95% 
                 772 
                 883 
                 735 
                 743 
                 939 
               
               
                 99.5% (Final Boiling Point) 
                 942 
                 1079 
                 951 
                 888 
                 1064 
               
               
                 Carlo-Erba Hydrocarbon Analysis 
                   
                   
                   
                   
                   
               
               
                 Carbon, wt % 
                 87.6 
                 84.21 
                 85.46 
                 85.97 
                 85.94 
               
               
                 Hydrogen, wt % 
                 12.7 
                 12.25 
                 14.1 
                 14.0 
                 14.15 
               
               
                 Sum of C + H, wt % 
                 100.3 
                 96.46 
                 99.5 
                 100.0 
                 100.1 
               
               
                 H/C Molar Ratio 
                 1.73 
                 1.75 
                 1.98 
                 1.96 
                 1.98 
               
               
                 Bromine Number, g/100 g 
                 49 
                 60 
                 40 
                 44 
                 14 
               
               
                 Hydrocarbon Type 
                   
                   
                   
                   
                   
               
               
                 Total Aromatics, vol % 
                 23.3 
                 22.8 
                 5.1 
                 8.7 
                 13.3 
               
               
                 Total Olefins &amp; Naphthenes, vol % 
                 39.0 
                 50.2 
                 42.4 
                 38.2 
                 42.1 
               
               
                 Total Paraffins, vol % 
                 37.7 
                 27 
                 52.5 
                 53.1 
                 44.6 
               
               
                 Contaminants 
                   
                   
                   
                   
                   
               
               
                 Total S, ppm 
                 48 
                 29 
                 7.8 
                 99 
                 6.3 
               
               
                 Total N, ppm 
                 751 
                 1410 
                 318 
                 353 
                 237 
               
               
                 Total Cl, ppm (by CIC) 
                 113 
                 62 
                 41 
                 70 
                 4.7 
               
               
                 Total O, ppm 
                 250 
                 — 
                 574 
                 — 
                 — 
               
               
                 Trace Elemental Impurities 
                   
                   
                   
                   
                   
               
               
                 Al, ppm 
                 &lt;1.1 
                 &lt;0.56 
                 0.6 
                 &lt;0.53 
                 &lt;0.68 
               
               
                 Ca, ppm 
                 1.4 
                 11.5 
                 &lt;0.5 
                 &lt;0.53 
                 &lt;0.68 
               
               
                 Fe, ppm 
                 4.9 
                 11.9 
                 1.6 
                 &lt;1.1 
                 3.1 
               
               
                 Mg, ppm 
                 &lt;0.51 
                 1.3 
                 &lt;0.52 
                 &lt;0.53 
                 &lt;0.68 
               
               
                 Na, ppm 
                 2.5 
                 &lt;0.54 
                 &lt;1.1 
                 &lt;2.2 
                 &lt;2.7 
               
               
                 Ni, ppm 
                 &lt;0.51 
                 &lt;0.54 
                 &lt;0.52 
                 2 
                 &lt;0.68 
               
               
                 V, ppm 
                 &lt;0.51 
                 &lt;0.54 
                 &lt;0.52 
                 4 
                 &lt;0.68 
               
               
                 P, ppm 
                 8.2 
                 9.9 
                 &lt;1.6 
                 &lt;2.2 
                 20.2 
               
               
                 Si, ppm 
                 82.5 
                 49.6 
                 13 
                 17 
                 3.1 
               
               
                   
               
            
           
         
       
     
     ASTM D4052 method was used for specific gravity measurements. Simulated boiling point distribution curve was obtained using ASTM D2887 method. Carlo-Erba analysis for carbon and hydrogen was based on ASTM D5291 method. Bromine number measurement was based on ASTM D1159 method. Hydrocarbon-type analysis was done using a high resolution magnetic mass spectrometer using the magnet scanned from 40 to 500 Daltons. Total sulfur was determined using XRF per ASTM D2622 method. The nitrogen was determined using a modified ASTM D5762 method using chemiluminescence detection. The total chloride content was measured typically using combustion ion chromatography (CIC) instrument using modified ASTM 7359 method. The oxygen content in naphtha and distillate boiling range was estimated using GC by GC/MS measurements with electron ionization detector for m/Z range of 29-500. Trace metal and non-metal elements in oil were determined using inductively coupled plasma-atomic emission spectrometry (ICP-AES). 
     Industrial pyrolysis process of sorted plastics, sourced predominantly from polyethylene and polypropylene waste, produced quality hydrocarbon streams with specific gravity ranging 0.7 to 0.9, and a boiling range from 18 to 1100° F. as in pyrolysis oil or pyrolysis wax. 
     The pyrolysis product is rather pure hydrocarbon made of mostly carbon and hydrogen. The hydrogen to carbon molar ratio varies from 1.7 to near 2.0. The Bromine Number is in the range of 14 through 60 indicating varying degrees of unsaturation coming from olefins and aromatics. The aromatic content is in the range of 5 to 23 volume % with a higher severity unit producing more aromatics. Depending on the process conditions of the pyrolysis unit, the pyrolysis products show paraffinic content ranging from mid-20 vol. % to mid-50 vol. %. The pyrolysis product contains a substantial amount of olefins. Samples A and B, pyrolysis oil produced under more severe conditions such as higher pyrolysis temperature and/or longer residence time, contain higher aromatic and lower paraffinic components, resulting H/C molar ratio of around 1.7 and high Bromine Number of 50-60. Samples C and D were produced at less severe conditions, and the pyrolysis oils are more paraffinic, resulting H/C molar ratio of close to 2.0 and Bromine Number around 40. Sample E, pyrolysis wax, is mostly paraffinic, saturated hydrocarbon with a substantial amount of normal hydrocarbons (as opposed to branched hydrocarbons) with low Bromine Number of only 14. 
     Example 2 
     Contaminants in Pyrolysis Oils and Micro Filtration to Remove Solids 
     Pyrolysis oils or wax products contain residual solids and other impurities that could negatively affect the performance of conversion units in a refinery. As received pyrolysis oil samples were vacuum filtered through 0.7 micron glass fiber filter paper to remove residual solids and the results are summarized in Table 2. 
     The residual solid content can be measured by the Heptane Insolubles test, ASTM D-3279 method. For chloride analysis, X-ray fluorescence (XRF) method was used. 
     
       
         
           
               
             
               
                 TABLE 2 
               
             
            
               
                   
               
               
                 Impurity Removal of Pyrolysis Oil by Filtration 
               
            
           
           
               
               
               
               
            
               
                   
                 As-Received 
                 Feed Pretreating 
                 % Reduction 
               
               
                   
                 Pyrolysis 
                 Filtration with 
                 of Impurities 
               
               
                   
                 Oil Feed 
                 0.7 Micron Filter 
                 by Filtration 
               
               
                   
               
            
           
           
               
               
               
               
               
            
               
                 Example 2-1 
                 Heptane Insoluble Solids, ppm 
                 1200 
                 57 
                 95% 
               
               
                   
                 Contaminants Cl, ppm 
                 67 
                 8.4 
                 93% 
               
               
                 Example 2-2 
                 Heptane Insoluble Solids, ppm 
                 3000 
                 61 
                 98% 
               
               
                   
                 Contaminants Cl, ppm 
                 125 
                 8.5 
                 93% 
               
               
                 Example 2-3 
                 Heptane Insoluble Solids, ppm 
                 2400 
                 33 
                 99% 
               
               
                   
                 Contaminants Cl, ppm 
                 235 
                 8.2 
                 97% 
               
               
                 Example 2-4 
                 Contaminants Cl, ppm 
                 2173 
                 1375 
                 37% 
               
               
                 Example 2-5 
                 Contaminants Cl, ppm 
                 9.1 
                 10.4 
                  0% 
               
               
                   
               
            
           
         
       
     
     In the study, it was found that the pore size of the filter is important for impurity removal. When a 25 micron filter was used, the filter paper was plugged and the filtration of the three pyrolysis oils could not be completed. With a 0.7 micron filter, the filtration reduced the content of heptane insoluble solids by 90% or higher. The study indicated filtration with small pore size filter, for example 1.0 micron or less, such as the 0.7 micron filter used, is effective in removing residual solids. Surprisingly, the filtration also removed chloride impurities effectively (Examples 2-1 through 2-4), except one case (Example 2-5). The data suggests that a pyrolysis oil product contains varying amounts of inorganic chloride species and filtration can reduce the impurity level substantially. In Example 2-5, however, no reduction of chloride species was observed. This suggests that some chloride species are organic in nature and further treatment would be needed beyond the filtration process. 
     Example 3 
     Pyrolysis Oil Pretreating by Filtration Followed by CaO/ZnO/Clay Metal Oxide Treatment 
     As-received pyrolysis oil, Sample F, was filtered through a continuous filtration unit containing 0.5 micron nominal filter cartridge to prepare a filtered oil, Sample F-1. The samples were analyzed for general feedstock properties and impurities, as shown in Table 3. 
     
       
         
           
               
             
               
                 TABLE 3 
               
             
            
               
                   
               
               
                 Impurity Removal of Pyrolysis Oil by Continuous Filtration 
               
            
           
           
               
               
               
            
               
                   
                 Feed Pre-Treating 
                   
               
            
           
           
               
               
               
               
            
               
                   
                 Pyrolysis Oil 
                 Pyrolysis Oil 
                   
               
               
                   
                 Sample F 
                 Sample F-1 
                 % Reduction 
               
               
                   
                 As-Received 
                 Filtration with 0.5 
                 of Impurities 
               
               
                   
                 Pyrolysis Oil 
                 micron nominal filter 
                 by Filtration 
               
               
                   
               
            
           
           
               
               
               
               
            
               
                 Heptane Insoluble Solids, ppm 
                 ~2400 
                 314 
                 87% 
               
               
                 Contaminants 
                   
                   
                   
               
               
                 Total S, ppm 
                 67 
                 — 
                 — 
               
               
                 Total N, ppm 
                 212 
                 165 
                 22% 
               
               
                 Total Cl, ppm 
                 2317 
                 1848 
                 20% 
               
               
                 Trace Elemental Impurities 
                   
                   
                   
               
               
                 Fe, ppm 
                 17.6 
                 9.3 
                 47% 
               
               
                 P, ppm 
                 4.6 
                 3.6 
                 22% 
               
               
                 Si, ppm 
                 36.4 
                 24.4 
                 33% 
               
               
                 Specific Gravity at 60° F. 
                 0.7866 
                 0.7857 
                 — 
               
               
                 Bromine Number, g/100 g 
                 — 
                 67 
                 — 
               
               
                 Simulated Distillation, ° F. 
                   
                   
                   
               
               
                 0.5% (Initial Boiling Point) 
                 — 
                 22 
                 — 
               
               
                   5% 
                 — 
                 148 
                 — 
               
               
                  10% 
                 — 
                 180 
                 — 
               
               
                  30% 
                 — 
                 294 
                 — 
               
               
                  50% 
                 — 
                 401 
                 — 
               
               
                  70% 
                 — 
                 518 
                 — 
               
               
                  90% 
                 — 
                 664 
                 — 
               
               
                  95% 
                 — 
                 735 
                 — 
               
               
                  99% (Final Boiling Point) 
                 — 
                 859 
                 — 
               
               
                   
               
            
           
         
       
     
     The continuous filtration unit with 0.5 micron nominal filter cartridge was effective and reduced the content of heptane insoluble solids by 87% to produce the filtered oil, Sample F-1, with 314 residual heptane insoluble solids. The filtration also removed a substantial amount of other impurities such as nitrogen, chloride, iron, phosphorus and silicon. 
     Sample F-1 was further treated by passing it through a fixed bed reactor containing metal oxide adsorbent made of CaO/ZnO/Clay. The metal oxide treating experiments were carried out at 600 psig reactor pressure and 1 LHSV flow, with the temperature varying from 200 to 400° F. 1500 SCF/BBL of hydrogen was fed to the reactor with the oil. The results are summarized below in Table 4. 
     
       
         
           
               
             
               
                 TABLE 4 
               
             
            
               
                   
               
               
                 Treating of Pyrolysis Oil Feed (Sample F-1) with 
               
               
                 CaO/ZnO/Clay Metal Oxide for Impurity Removal 
               
            
           
           
               
               
            
               
                   
                 Example No. 
               
            
           
           
               
               
               
               
               
            
               
                   
                 Example 
                 Example 
                 Example 
                 Example 
               
               
                   
                 4-1 
                 4-2 
                 4-3 
                 4-4 
               
            
           
           
               
               
               
            
               
                   
                 Base Case 
                 Metal Oxide Treating Temperature, F. 
               
            
           
           
               
               
               
               
               
            
               
                 Feed Pretreating 
                 No treating 
                 200 
                 300 
                 400 
               
               
                   
               
            
           
           
               
            
               
                 Impurities in Pyrolysis Oil, ppm 
               
            
           
           
               
               
               
               
               
            
               
                 N, ppm 
                 165 
                 98 
                 106 
                 99 
               
               
                 Cl, ppm 
                 1848 
                 742 
                 487 
                 288 
               
               
                 Fe, ppm 
                 9.3 
                 2.2 
                 1.7 
                 &lt;1.1 
               
               
                 P, ppm 
                 3.6 
                 &lt;3 
                 3.1 
                 3.3 
               
               
                 Si, ppm 
                 24.4 
                 23.4 
                 23.7 
                 19.9 
               
            
           
           
               
            
               
                 % Reduction of Impurities by Metal Oxide Treating 
               
            
           
           
               
               
               
               
               
            
               
                 N, % 
                 Base case 
                 41% 
                 36% 
                 40% 
               
               
                 Cl, % 
                 Base case 
                 60% 
                 74% 
                 84% 
               
               
                 Fe, % 
                 Base case 
                 76% 
                 82% 
                 &gt;88%  
               
               
                 P, % 
                 Base case 
                 ~20%  
                 14% 
                  8% 
               
               
                 Si, % 
                 Base case 
                  4% 
                  3% 
                 18% 
               
               
                   
               
            
           
         
       
     
     The metal oxide treatment step removed a substantial amount of metal (Fe) and other non-metals (N, Cl, P, Si) that could negatively affect the performance of conversion units in a refinery. CaO and ZnO containing metal oxides were particularly effective for chloride and iron removal. The removal became more efficient at a higher temperature. 
     Example 4 
     Pyrolysis Oil Pretreating by Filtration Followed by NiO/MoO 3 /PO 4 /Alumina Metal Oxide Treatment 
     As-received pyrolysis oil, Sample G, was filtered through a continuous filtration unit containing 0.5 micron nominal filter cartridge to prepare a filtered oil, Sample G-1. The samples were analyzed for general feedstock properties and impurities, as shown in Table 5. 
     
       
         
           
               
             
               
                 TABLE 5 
               
             
            
               
                   
               
               
                 Impurity Removal of Pyrolysis Oil by Continuous Filtration 
               
            
           
           
               
               
               
            
               
                   
                 Feed Pre-Treating 
                   
               
            
           
           
               
               
               
               
            
               
                   
                 Pyrolysis Oil 
                 Pyrolysis Oil 
                   
               
               
                   
                 Sample G 
                 Sample G-1 
                 % Reduction 
               
               
                   
                 As-Received 
                 Filtration with 0.5 
                 of Impurities 
               
               
                   
                 Pyrolysis Oil 
                 micron nominal filter 
                 by Filtration 
               
               
                   
               
            
           
           
               
               
               
               
            
               
                 Contaminants 
                   
                   
                   
               
               
                 Total S, ppm 
                 66 
                 65 
                  2% 
               
               
                 Total N, ppm 
                 1490 
                 1320 
                 11% 
               
               
                 Total Cl, ppm 
                 533 
                 57 
                 89% 
               
               
                 Trace Elemental Impurities 
                   
                   
                   
               
               
                 Ca, ppm 
                 58.1 
                 4.9 
                 92% 
               
               
                 Cr, ppm 
                 9.1 
                 7.8 
                 14% 
               
               
                 Fe, ppm 
                 29.0 
                 13.8 
                 52% 
               
               
                 Mg, ppm 
                 2.9 
                 0.7 
                 75% 
               
               
                 P, ppm 
                 18.0 
                 18.1 
                 −1% 
               
               
                 Si, ppm 
                 25.8 
                 21.5 
                 17% 
               
               
                 Specific Gravity at 60° F. 
                 — 
                 0.8481 
                 — 
               
               
                 Bromine Number, g/100 g 
                 — 
                 36 
                 — 
               
               
                 Simulated Distillation, ° F. 
                   
                   
                   
               
               
                 0.5% (Initial Boiling Point) 
                 — 
                 324 
                 — 
               
               
                   5% 
                 — 
                 473 
                 — 
               
               
                  10% 
                 — 
                 531 
                 — 
               
               
                  30% 
                 — 
                 625 
                 — 
               
               
                  50% 
                 — 
                 691 
                 — 
               
               
                  70% 
                 — 
                 766 
                 — 
               
               
                  90% 
                 — 
                 936 
                 — 
               
               
                  95% 
                 — 
                 1029 
                 — 
               
               
                  99% (Final Boiling Point) 
                 — 
                 1161 
                 — 
               
               
                   
               
            
           
         
       
     
     The data in Table 5 show that the continuous filtration unit with 0.5 micron nominal filter cartridge was effective in reducing impurities such as nitrogen, chloride, calcium, chrome, iron, magnesium and silicon. However, the filtration did not remove any sulfur and phosphorus impurities. 
     Sample G-1 was further treated by passing it through a fixed bed reactor containing metal oxide adsorbent made of NiO/MoO 3 /PO 4 /Alumina. The metal oxide treating experiments were carried out at 400 psig reactor pressure and 1 LHSV flow, with the temperature varying from 500 to 550° F. 1500 SCF/BBL of hydrogen was fed to the reactor with the oil. The results are summarized below in Table 6. 
     
       
         
           
               
             
               
                 TABLE 6 
               
             
            
               
                   
               
               
                 Treating of Pyrolysis Oil (Sample G-1) with 
               
               
                 NiO/MoO 3 /PO 4 /Alumina Metal Oxide for Impurity Removal 
               
            
           
           
               
               
            
               
                   
                 Example No. 
               
            
           
           
               
               
               
               
            
               
                   
                 Example 
                 Example 
                 Example 
               
               
                   
                 4-1 
                 4-2 
                 4-3 
               
            
           
           
               
               
               
            
               
                   
                 Base Case 
                 Metal Oxide Treating Temperature, ° F. 
               
            
           
           
               
               
               
               
            
               
                 Feed Pretreating 
                 No treating 
                 500 
                 550 
               
               
                   
               
            
           
           
               
               
               
               
            
               
                 Bromine Number, 
                 36 
                 33 
                 31 
               
               
                 g/100 g 
                   
                   
                   
               
            
           
           
               
            
               
                 Impurities in Pyrolysis Oil, ppm 
               
            
           
           
               
               
               
               
            
               
                 N, ppm 
                 1320 
                 1090 
                 1050 
               
               
                 Cl, ppm 
                 57 
                 5.1 
                 &lt;5 
               
               
                 Ca, ppm 
                 4.9 
                 &lt;0.51 
                 &lt;0.52 
               
               
                 Cr, ppm 
                 7.8 
                 2.1 
                 0.75 
               
               
                 Fe, ppm 
                 13.8 
                 5.4 
                 5.4 
               
               
                 Mg, ppm 
                 0.7 
                 &lt;0.51 
                 &lt;0.52 
               
               
                 P, ppm 
                 18.1 
                 15.7 
                 15.4 
               
               
                 Si, ppm 
                 21.5 
                 16.0 
                 14.2 
               
            
           
           
               
            
               
                 % Reduction of Impurities by Metal Oxide Treating 
               
            
           
           
               
               
               
               
            
               
                 N, % 
                 Base case 
                 17% 
                 20% 
               
               
                 Cl, % 
                 Base case 
                 91% 
                 &gt;90%  
               
               
                 Ca, % 
                 Base case 
                 &gt;90%  
                 &gt;90%  
               
               
                 Cr, % 
                 Base case 
                 74% 
                 90% 
               
               
                 Fe, % 
                 Base case 
                 61% 
                 61% 
               
               
                 Mg, % 
                 Base case 
                 &gt;30%  
                 &gt;30%  
               
               
                 P, % 
                 Base case 
                 13% 
                 15% 
               
               
                 Si, % 
                 Base case 
                 26% 
                 34% 
               
               
                   
               
            
           
         
       
     
     The metal oxide treatment step removed a substantial amount of metals (Fe, Ca, Cr, Mg) and other non-metals (N, Cl, P, Si) that could negatively affect the performance of conversion units in a refinery. MoO 3  and NiO containing metal oxides were particularly effective for metals removal at about 500-550° F. 
     The following Examples 5 through 8 show the evaluation of waste plastics pyrolysis oil for transportation fuel. 
     Example 5 
     Fractionation of Pyrolysis Oil for Evaluation as Transportation Fuel 
     Sample D was distilled to produce hydrocarbon cuts representing gasoline (350° F. − ), jet (350-572° F.), diesel (572-700° F.) and the heavy (700° F. + ) fractions. Table 7 summarizes the boiling point distribution and impurity distributions among the distilled product fractions. 
     
       
         
           
               
             
               
                 TABLE 7 
               
             
            
               
                   
               
               
                 Distillation of Pyrolysis Oil into Fuel Fractions 
               
            
           
           
               
               
               
               
               
               
            
               
                 Sample ID 
                 Sample D 
                 Sample H 
                 Sample I 
                 Sample J 
                 Sample K 
               
               
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 Intended Fraction 
                   
                 Gasoline Cut 
                 Jet Cut 
                 Diesel Cut 
                 Unconverted 
               
               
                 Cut Point Target, ° F. 
                   
                     350 −   
                 350-572 
                 572-700 
                     700 +   
               
               
                 Distillation Actual Yields, 
                   
                   37.2 
                 38.0 
                 15.0 
                    9.3 
               
               
                 wt % 
                   
                   
                   
                   
                   
               
               
                 Simulated Distillation, F. 
                   
                   
                   
                   
                   
               
               
                 IBP (0.5 wt %) 
                 86 
                  27 
                 299 
                 539 
                 640 
               
               
                  5 wt % 
                 154 
                  98 
                 345 
                 557 
                 684 
               
               
                 10 wt % 
                 210 
                 147 
                 365 
                 574 
                 696 
               
               
                 30 wt % 
                 304 
                 222 
                 416 
                 597 
                 727 
               
               
                 50 wt % 
                 421 
                 270 
                 457 
                 619 
                 758 
               
               
                 70 wt % 
                 532 
                 291 
                 492 
                 644 
                 808 
               
               
                 90 wt % 
                 676 
                 337 
                 546 
                 674 
                 898 
               
               
                 95 wt % 
                 743 
                 347 
                 554 
                 683 
                 953 
               
               
                 FBP (99.5 wt %) 
                 888 
                 385 
                 591 
                 711 
                 1140  
               
               
                 Total S, ppm 
                 99 
                  52 
                 35 
                 80 
                 320 
               
               
                 Total N, ppm 
                 353 
                 215 
                 556 
                 232 
                 467 
               
               
                 Total Cl, ppm 
                 70 
                 181 
                 27 
                 12 
                  13 
               
               
                   
               
            
           
         
       
     
     Example 6 
     Evaluation of Pyrolysis Oil Cut for Gasoline Fuel 
     Sample H, a pyrolysis oil cut for gasoline fuel boiling range, was evaluated to assess its potential for use as a gasoline fuel. Sample H has the carbon number range of C5-C12, typical of a gasoline fuel. 
     Due to the olefinic nature of the pyrolysis oil, oxidation stability (ASTM D525) and gum forming tendency (ASTM D381) were identified as the most critical properties to examine. Research octane number (RON) and motor octane number (MON) are also the critical properties for engine performance. The RON and MON values were estimated from detailed hydrocarbon GC analysis. 
     
       
         
           
               
             
               
                 TABLE 8 
               
             
            
               
                   
               
               
                 Evaluation of Pyrolysis Oil Naphtha Fraction for Gasoline Fuel 
               
            
           
           
               
               
               
               
               
            
               
                   
                 Oxidation 
                 Washed 
                   
                   
               
               
                   
                 Stability, 
                 Gum, mg/ 
                   
                   
               
               
                   
                 min 
                 100 mL 
                 RON 
                 MON 
               
               
                   
               
            
           
           
               
               
               
               
               
            
               
                 Sample H 
                 90 
                 5.0 
                 71.4 
                 67.7 
               
               
                 Reference gasoline 
                 &gt;1440 
                 1 
                 95.8 
                 86.2 
               
               
                 4/96 vol. % Blend of Sample 
                 &gt;1440 
                 2.0 
                 94.5 
                 85.1 
               
               
                 H with reference gasoline 
                   
                   
                   
                   
               
               
                 15/85 vol. % Blend of Sample 
                 &gt;1440 
                 2.2 
                 91.8 
                 83.1 
               
               
                 H with reference gasoline 
               
               
                   
               
            
           
         
       
     
     Sample H, a pyrolysis oil cut for gasoline fuel boiling range, cannot be used by itself as automotive gasoline fuel due to its poor quality. The gasoline fraction from the pyrolysis oil showed very poor oxidation stability in that Sample H failed only after 90 min compared to the target stability of longer than 1440 minutes. The pyrolysis gasoline exceeded the wash gum target of 4 mg/100 mL suggesting severe gum forming tendency. The pyrolysis gasoline has poor octane numbers compared to the reference gasoline. A premium unleaded gasoline was used as the reference gasoline. 
     The potential of blending the pyrolysis gasoline cut in a limited amount with the reference gasoline was also examined. The study showed that possibly up to 15 volume % of Sample H can be blended with the refinery gasoline while still meeting the fuels property targets. By integrating the pyrolysis gasoline product with a refinery fuel, the overall product quality can be maintained. 
     These results indicate that the as-produced gasoline fraction of pyrolysis oil has limited utility as gasoline fuel. Upgrading in a refinery unit is needed to convert the gasoline fraction of the pyrolysis oil into a hydrocarbon that meets the gasoline fuel property targets. 
     Example 7 
     Evaluation of Pyrolysis Oil Cut for Jet Fuel 
     Sample I, a pyrolysis oil cut for jet fuel boiling range, was evaluated to assess its potential for use as jet fuel. Sample I has the carbon number range of C9-C18, typical of the jet fuel. 
     Due to the olefinic nature of the pyrolysis oil, jet fuel thermal oxidation test (D3241) was considered as an important test. The pyrolysis oil jet cut as-is, Sample I, had only 36 minutes of oxidation stability, suggesting that the pure pyrolysis jet cut is unsuitable for use as jet fuel. 
     A 5 volume % blend of pyrolysis jet cut (Sample I) with refinery produced jet was prepared. The blend still failed the jet fuel oxidation test as shown in Table 9. 
     
       
         
           
               
             
               
                 TABLE 9 
               
             
            
               
                   
               
               
                 Evaluation of Pyrolysis Oil Jet Fraction for Jet Fuel 
               
            
           
           
               
               
            
               
                   
                 Jet Fuel Thermal 
               
               
                   
                 Oxidation Test 
               
               
                   
               
            
           
           
               
               
               
            
               
                   
                 Reference jet fuel 
                 Passed 
               
               
                   
                 5/95 vol. % Blend of Sample I  
                 Failed 
               
               
                   
                 with reference jet fuel 
               
               
                   
               
            
           
         
       
     
     These results indicate that the as-produced jet fraction of pyrolysis oil is completely unsuitable for jet fuel, and upgrading in a refinery unit is required to convert this jet fraction of the pyrolysis oil into a hydrocarbon that meets the jet fuel property targets. 
     Example 8 
     Evaluation of Pyrolysis Oil Cut for Diesel Fuel 
     Sample J, a pyrolysis oil cut for diesel fuel boiling range, was evaluated to assess its potential for use as diesel fuel. Sample J has the carbon number range of C14-C24, typical of a diesel fuel. 
     Sample J contains a substantial amount of normal hydrocarbons. Since normal hydrocarbons tend to exhibit waxy characteristics, cold flow properties such as pour point (ASTM D5950-14) and cloud points (ASTM D5773) were considered as the most critical tests. 
     Two blends were prepared at 10 and 20 volume % of Sample J with refinery produced diesel fuel. However, both blends still failed the target pour point of less than −17.8° C. (0° F.) pour points. 
     
       
         
           
               
             
               
                 TABLE 10 
               
             
            
               
                   
               
               
                 Evaluation of Pyrolysis Oil Diesel Fraction for Diesel Fuel 
               
            
           
           
               
               
               
               
            
               
                   
                 Cloud Point 
                 Pour Point 
                 Pour Point 
               
               
                   
                 (° C.) 
                 (° C.) 
                 Test 
               
               
                   
               
            
           
           
               
               
               
               
            
               
                 Reference diesel fuel 
                 −17.1 
                 −19.0 
                 Passed 
               
               
                 10/90 vol. % Blend of Sample J 
                 −11.1 
                 −12.0 
                 Failed 
               
               
                 with reference diesel fuel 
                   
                   
                   
               
               
                 20/80 vol. % Blend of Sample J 
                 −5.5 
                 −7.0 
                 Failed 
               
               
                 with reference diesel fuel 
               
               
                   
               
            
           
         
       
     
     These results indicate that the pyrolysis oil as-is is completely unsuitable for diesel fuel, and upgrading in a refinery unit is required to covert the diesel fraction of pyrolysis oil into hydrocarbon that meets the diesel fuel property targets. 
     Example 9 
     Coprocessing of Pyrolysis Product to FCC Unit 
     By feeding the entire pyrolysis feedstock to a FCC unit after the feed pretreating as shown in  FIG.  3   , the pyrolysis oil and wax are converted into offgas, LPG paraffins and olefins, FCC gasoline and heavy hydrocarbon components. The FCC gasoline is a valuable gasoline blending component. The heavy fractions, light cycle oil (LCO) and heavy cycle oil (HCO) are converted further in the subsequent conversion units including jet hydrotreating unit, diesel hydrotreating unit, hydrocracking unit and/or coker unit to make more gasoline, jet, and diesel fuel with satisfactory product properties. The LPG paraffins and olefins can be either processed further in an alkylation unit or in part used for petrochemicals production with a recycle content. 
     The following Examples 10 and 11 demonstrate the conversion of waste plastics pyrolysis product into quality transportation fuel in a refinery conversion unit, using a FCC unit as an example. 
     Example 10 
     Conversion of Pyrolysis Oil in FCC 
     To study the impact of coprocessing of waste plastics pyrolysis oil in a FCC, a series of laboratory tests were carried out with Samples A and C. Vacuum gas oil (VGO) is the typical feed for FCC. FCC performances of 20 volume % blend of pyrolysis oil with VGO and pure pyrolysis oil were compared with that of the pure VGO feed. 
     The FCC experiments were carried out on a Model C ACE (advanced cracking evaluation) unit fabricated by Kayser Technology Inc. using regenerated equilibrium catalyst (Ecat) from a refinery. The reactor was a fixed fluidized reactor using N 2  as a fluidization gas. Catalytic cracking experiments were carried out at the atmospheric pressure and 900° F. reactor temperature. The cat/oil ratio was varied between 5 to 8 by varying the amount of the catalyst. A gas product was collected and analyzed using a refinery gas analyzer (RGA), equipped with GC with FID detector. In-situ regeneration of a spent catalyst was carried out in the presence of air at 1300° F., and the regeneration flue gas was passed through a LECO unit to determine the coke yield. A liquid product was weighted and analyzed in a GC for simulated distillation (D2887) and C 5   −  composition analysis. With a material balance, the yields of coke, dry gas components, LPG components, gasoline (C5-430° F.), light cycle oil (LCO, 430-650° F.) and heavy cycle oil (HCO, 650° F. + ) were determined. The results are summarized below in Table 11. 
     
       
         
           
               
             
               
                 TABLE 11 
               
             
            
               
                   
               
               
                 Evaluation of Pyrolysis Oil Cofeeding to FCC 
               
            
           
           
               
               
            
               
                   
                 Feed 
               
            
           
           
               
               
               
               
               
               
            
               
                   
                   
                 20/80 vol 
                 20/80 vol 
                   
                   
               
               
                   
                   
                 % blend, 
                 % blend, 
                 100% 
                 100% 
               
               
                   
                 100% 
                 Sample 
                 Sample 
                 Sample 
                 Sample 
               
               
                   
                 VGO 
                 A/VGO 
                 C/VGO 
                 A 
                 C 
               
               
                   
               
            
           
           
               
               
               
               
               
               
            
               
                 Cat/Oil, wt/wt 
                 6.0 
                 6.0 
                 6.0 
                 6.0 
                 6.0 
               
               
                 Conversion, wt %* 
                 81.3 
                 83.15 
                 83.09 
                 76.1 
                 78.82 
               
               
                 WLP Impurity** 
                   
                   
                   
                   
                   
               
               
                 Total O, ppm 
                 81 
                 76 
                 62 
                 54 
                 67 
               
               
                 Total N, ppm 
                 27 
                 30 
                 33 
                 50 
                 21 
               
               
                 Yields 
                   
                   
                   
                   
                   
               
               
                 Coke, wt % 
                 4.45 
                 4.35 
                 4.20 
                 3.56 
                 2.90 
               
               
                 Total Dry Gas, wt % 
                 2.08 
                 1.96 
                 1.93 
                 1.55 
                 1.43 
               
               
                 Hydrogen 
                 0.16 
                 0.12 
                 0.12 
                 0.05 
                 0.04 
               
               
                 Methane 
                 0.68 
                 0.65 
                 0.64 
                 0.50 
                 0.46 
               
               
                 Ethane 
                 0.44 
                 0.43 
                 0.41 
                 0.33 
                 0.28 
               
               
                 Ethylene 
                 0.76 
                 0.74 
                 0.72 
                 0.63 
                 0.61 
               
               
                 Total LPG, wt % 
                 21.25 
                 21.08 
                 21.50 
                 20.17 
                 24.40 
               
               
                 Propane 
                 1.78 
                 1.76 
                 1.72 
                 1.47 
                 1.53 
               
               
                 Propylene 
                 5.53 
                 5.51 
                 5.56 
                 5.57 
                 6.75 
               
               
                 n-Butane 
                 1.56 
                 1.56 
                 1.54 
                 1.29 
                 1.34 
               
               
                 Isobutane 
                 6.61 
                 6.48 
                 6.64 
                 5.43 
                 6.61 
               
               
                 C4 olefins 
                 5.77 
                 5.77 
                 6.04 
                 6.41 
                 8.16 
               
               
                 Gasoline, wt % 
                 53.53 
                 55.75 
                 55.46 
                 62.53 
                 61.75 
               
               
                 LCO, wt % 
                 12.89 
                 12.23 
                 11.93 
                 10.37 
                 8.03 
               
               
                 HCO, wt % 
                 5.81 
                 4.63 
                 4.98 
                 1.82 
                 1.50 
               
               
                 Octane Number*** 
                 88.05 
                 84.57 
                 82.79 
                 73.75 
                 75.41 
               
               
                   
               
               
                 *Conversion - conversion of 430° F. +  fraction to 430° F. −   
               
               
                 **Impurity level of N and O in whole liquid product in fuels boiling range by GC × GC, ppm 
               
               
                 ***Octane number, (R + M)/2, was estimated from detailed hydrocarbon GC of FCC gasoline. 
               
            
           
         
       
     
     The results in Table 11 show that up to 20 volume % cofeeding of pyrolysis oil only makes very slight changes in the FCC unit performance indicating coprocessing of pyrolysis oil up to 20% is readily feasible. The 20 volume % blending of Sample A or Sample C led to very slight reduction of coke and dry gas yields, slight increase in gasoline yield and slight decrease in LCO and HCO, which are favorable in most situations. With paraffinic nature of pyrolysis oil, the 20% blends of A and C lowered the Octane number by about 3-5 numbers. With refinery operational flexibility, these octane number debits can be compensated with blending or feeding location adjustments. 
     The FCC unit cracks the pyrolysis oil info fuel range hydrocarbons, reduces impurities, and isomerize n-paraffins to isoparaffins. All these chemistry will improve the fuel properties of the pyrolysis oil and wax. By cofeeding the pyrolysis oil through the FCC process unit with a zeolite catalyst, the oxygen and nitrogen impurities in the fuel range were reduced substantially, from about 300-1400 ppm N to about 30 ppm N and from about 250-540 ppm O to about 60-80 ppm O. The hydrocarbon composition of all these cofeeding products are well within the typical FCC gasoline range. 
     The FCC runs of 100% pyrolysis oil showed substantial debits of Octane numbers by about 13-14 numbers. This shows that coprocessing of pyrolysis oil is preferred over processing of pure 100% pyrolysis oil. 
     Example 11 
     Coprocessing of Pyrolysis Wax in a FCC 
     To study the impact of coprocessing of waste plastics pyrolysis wax in a FCC, a series of laboratory tests were carried out with Sample E and VGO. FCC performances of 20% blend of pyrolysis wax with VGO and pure pyrolysis wax were compared with that of the pure VGO feed, similar to Example 10. The results are summarized below in Table 12. 
     
       
         
           
               
             
               
                 TABLE 12 
               
             
            
               
                   
               
               
                 Evaluation of Pyrolysis Wax Cofeeding to FCC 
               
            
           
           
               
               
            
               
                   
                 Feed 
               
            
           
           
               
               
               
               
            
               
                   
                 100% 
                 20/80 vol % blend, 
                 100% 
               
               
                   
                 VGO 
                 Sample E/VGO 
                 Sample E 
               
               
                   
               
            
           
           
               
               
               
               
            
               
                 Cat/Oil, wt/wt 
                 6.5 
                 6.5 
                 6.5 
               
               
                 Conversion, wt %* 
                 82.75 
                 84.17 
                 91.31 
               
               
                 Yields 
                   
                   
                   
               
               
                 Coke, wt % 
                 4.78 
                 4.76 
                 4.26 
               
               
                 Total Dry Gas, wt % 
                 2.11 
                 2.05 
                 1.79 
               
               
                 Hydrogen 
                 0.16 
                 0.14 
                 0.07 
               
               
                 Methane 
                 0.69 
                 0.67 
                 0.58 
               
               
                 Ethane 
                 0.44 
                 0.43 
                 0.37 
               
               
                 Ethylene 
                 0.78 
                 0.77 
                 0.73 
               
               
                 Total LPG, wt % 
                 21.71 
                 23.15 
                 31.79 
               
               
                 Propane 
                 1.87 
                 1.93 
                 2.28 
               
               
                 Propylene 
                 5.54 
                 5.98 
                 8.59 
               
               
                 n-Butane 
                 1.65 
                 1.74 
                 2.15 
               
               
                 Isobutane 
                 6.91 
                 7.25 
                 8.88 
               
               
                 C4 olefins 
                 5.74 
                 6.25 
                 9.89 
               
               
                 Gasoline, wt % 
                 54.16 
                 54.21 
                 53.47 
               
               
                 LCO, wt % 
                 12.42 
                 11.59 
                 6.71 
               
               
                 HCO, wt % 
                 4.83 
                 4.24 
                 1.99 
               
               
                 Octane Number** 
                 89.95 
                 88.38 
                 83.52 
               
               
                   
               
               
                 *Conversion - conversion of 430° F. +  fraction to 430° F. −   
               
               
                 **Octane number, (R + M)/2, was estimated from detailed hydrocarbon GC of FCC gasoline. 
               
            
           
         
       
     
     The results in Table 12 shows that up to 20 volume % cofeeding of pyrolysis wax only makes very slight changes in the FCC unit performance indicating coprocessing of pyrolysis wax up to 20% is readily feasible. The 20 volume % blending of Sample E led to very slight reduction to no change of coke and dry gas yields, noticeable increase in LPG olefin yield, very slight increase in gasoline yield and slight decrease in LCO and HCO, which are all favorable in most situations. With paraffinic nature of pyrolysis wax, the 20% blend of Sample E lowered the Octane number slightly by 1.5 number. With refinery blending flexibility, this octane number debit can be easily compensated with minor blending adjustments. 
     The FCC run of 100% pyrolysis wax showed substantial increase in conversion, and debit of the Octane number by 6. This shows that coprocessing of pyrolysis wax is preferred over processing of 100% pyrolysis wax. 
     Example 12 
     Feeding of Recycled C 3  LPG Stream to Steam Cracker for Ethylene Production, Followed by Productions of Polyethylene Resin and Polyethylene Consumer Products 
     A C 3  LPG stream containing propane and propylene, produced via cofeeding of pyrolysis products to a FCC unit, is separated and fed to a steam cracker for production of ethylene with a recycle content, as shown in  FIG.  3   . The ethylene is then processed to a polymerization unit to produce polyethylene resin containing some recycled-polyethylene/polypropylene derived materials while the quality of the newly produced polyethylene is indistinguishable to the virgin polyethylene made entirely from virgin petroleum resources. The polyethylene resin with the recycled material is then further processed to produce various polyethylene products to fit the needs of consumer products. These polyethylene consumer products now contains chemically recycled, circular polymer while the quality of the polyethylene consumer products are indistinguishable from those made entirely from virgin polyethylene polymer. These chemically recycled polymer products are different from the mechanically recycled polymer products whose qualities are inferior to the polymer products made from virgin polymers. 
     Example 13 
     Quality Gasoline, Jet and Diesel Product Production with Recycle Content 
     Cofeeding of pyrolysis oil and/or wax to a FCC unit, as shown in Examples 10 and 11, produces a substantial amount of C 3 -C 5  olefins with a recycle content, as well as the gasoline, jet, diesel products. A C 4  only or C 4 -C 5  stream containing recycled olefins is separated from FCC light-end recovery units, and then fed to an alkylation unit. Reaction of LPG olefins and isobutane in the alkylation reactor produces n-butane and alkylate gasoline with recycle contents. Alkylate gasoline and n-butane are valuable gasoline blending components. The heavy fraction is further upgraded in a hydrocracking unit to produce quality gasoline, jet and diesel products. 
     The foregoing examples together clearly showed a new effective way to recycle a large quantity of polyethylene and polypropylene derived waste plastics via chemical recycling through pyrolysis followed by cofeeding of the pyrolysis products in a refinery via efficient integration. The examples also demonstrate the benefits of a filtration/metal oxide treatment prior to an FCC unit. This integration allows quality fuels and circular polymer productions. 
     As used in this disclosure the word “comprises” or “comprising” is intended as an open-ended transition meaning the inclusion of the named elements, but not necessarily excluding other unnamed elements. The phrase “consists essentially of” or “consisting essentially of” is intended to mean the exclusion of other elements of any essential significance to the composition. The phrase “consisting of” or “consists of” is intended as a transition meaning the exclusion of all but the recited elements with the exception of only minor traces of impurities. 
     All patents and publications referenced herein are hereby incorporated by reference to the extent not inconsistent herewith. It will be understood that certain of the above-described structures, functions, and operations of the above-described embodiments are not necessary to practice the present invention and are included in the description simply for completeness of an exemplary embodiment or embodiments. In addition, it will be understood that specific structures, functions, and operations set forth in the above-described referenced patents and publications can be practiced in conjunction with the present invention, but they are not essential to its practice. It is therefore to be understood that the invention may be practiced otherwise that as specifically described without actually departing from the spirit and scope of the present invention as defined by the appended claims.