Patent Publication Number: US-2007098889-A1

Title: Vacuum film deposition method and system, and filter manufactured by using the same

Description:
TECHNICAL FIELD  
      The present invention relates to a vacuum film deposition method and system for depositing a multi-layered film on a substrate in a vacuum chamber, and an optical filter manufactured by using the same.  
     BACKGROUND ART  
      Hitherto, various vacuum film deposition systems have been employed as apparatuses for manufacturing optical filters used for the purpose of transmitting light in predetermined wavelength band by forming a multi-layered film on the surface of a substrate such as glass plate.  
      As a vacuum film deposition system, for example, an ion plating system is suitably used. The ion plating system has a vacuum chamber capable of maintaining its inside substantially in vacuum state. The vacuum chamber has two or more evaporation sources for evaporating film materials at the bottom thereof, and opposite to the evaporation sources, a substrate holder is disposed. At a center region of the back of the substrate holder, a rotational shaft is provided by an insulating board, and the rotational shaft is penetrates the ceiling wall of the vacuum chamber and is connected to a rotation drive device disposed in the upper part of the vacuum chamber. That is, the substrate holder is rotatably supported by the rotational shaft and rotation drive device in the vacuum chamber. An annular contact element is buried in the outer periphery of a contact area of the insulating board and the substrate holder. This contact element is electrically connected to the substrate holder. A carbon brush contacts with the contact element, and the carbon brush is connected to a radio-frequency power source for supplying radio-frequency power to the substrate holder, and a direct-current power source for applying a bias voltage. To protect the rotational shaft and the rotation drive device, they are entirely surrounded by part of the vacuum chamber and the housing.  
      In this ion plating system, a substrate such as glass plate is mounted on the substrate holder, and then the rotation drive device is operated to rotate the substrate, and a radio-frequency power source and a direct-current power source are turned on. As a result, radio-frequency power and bias voltage are applied to the rotating substrate holder from the contact element, that is, the carbon brush. Consequently, a radio-frequency electric field is generated in the interior of the vacuum chamber, and a bias electric field is generated between the substrate holder and the vacuum chamber. Thereafter, electron beams are emitted from an electron gun toward the two or more evaporation sources. By emission of electron beams, the temperature of film materials disposed on the evaporation sources is raised, causing the film materials to be evaporated. When the evaporated film materials are diffused into the vacuum chamber in a predetermined order, the diffused film materials are sequentially excited by the plasma generated by the radio-frequency electric field, and the excited film materials are accelerated by the bias electric field, and impinged and adhered to the surface of the substrate in a predetermined order. Finally, a thin film having strong adhesivity is formed on the substrate to have a predetermined layered structure. That is, a multi-layered film having a predetermined optical characteristic is deposited on the substrate.  
      In the conventional ion plating system operating in this manner, the substrate such as glass plate on which the multi-layered film having predetermined optical characteristic is deposited is disposed opposite to the evaporation sources for evaporating the film materials. That is, a space is formed between the substrate and evaporation sources so that the film materials diffused from the evaporation sources may reach the substrate with being disturbed. Accordingly, when the temperature of evaporation sources is raised by emission of electron beams from the electron gun, the temperature of the substrate is raised extremely by radiation heat from the heated evaporation sources. As a result of this temperature rise, the substrate may be deformed or deteriorated, and the optical characteristic of the film deposited on the substrate may be degraded.  
      To avoid the problem that the temperature of the substrate rises extremely by radiation heat from the evaporation sources heated by the electron beams, a substrate cooling structure is proposed for preventing the temperature rise of the substrate by forming a passage of a coolant such as cooling water inside the substrate holder and flowing the coolant such as the cooling water in the passage at a predetermined flow rate (see, for example, Japanese Patent Application Laid-Open No. 2001-212446, FIG. 1).  
      Thus, by forming a passage of the coolant such as cooling water inside the substrate holder for holding the substrate and flowing the coolant such as cooling water in the passage at a predetermined flow rate, the substrate holder is cooled by the coolant, and the substrate such as glass plate is cooled below a predetermined temperature, and hence distortion or deformation of substrate may be effectively prevented. That is, the problem of degradation of optical characteristic of the thin film deposited on the substrate can be solved.  
      However, the ion plating system in which the passage of the coolant such as cooling water is formed in the substrate holder and the coolant such as cooling water is flowed in the passage at a predetermined flow rate is effective when the substrate is formed of glass plate or other material of high heat resistance, but is not effective when the substrate is made of resin or other material low in heat resistance. In particular, it is not effective when the multi-layered film includes a number of layers of 30 layers or more that are stacked on the deposition surface of substrate. The reason is as follows. In the case where temperature of evaporation sources is raised by emission of electron beams, and temperature of substrate is raised by radiation heat from the heated evaporation sources, if attempted to cool the substrate by the coolant such as cooling water, the substrate temperature may exceed the heat resistant temperature of the resins forming the substrate. Besides, as the number of layers of the multi-layered film deposited on the substrate is increased, the film forming time becomes longer, and heating of substrate by radiation heat is promoted, which further increases the risk of the substrate temperature exceeding the heat resistant temperature of the resins for forming the substrate.  
      That is, in the conventional ion plating system in which the passage of the coolant such as cooling water is formed in the substrate holder and the coolant such as cooling water is flowed in the passage at a predetermined flow rate, applicable substrates are limited to substrates made of heat resistant materials such as glass plate (resin substrate is not be able to be used), and when the resin substrates are used, the number of layers to be formed on the substrate is limited.  
     DISCLOSURE OF PRESENT INVENTION  
      The present invention has been made to solve the problem, and it is hence an object thereof to provide a vacuum film deposition method and system capable of forming a multi-layered film including a number of layers on a deposition surface of a resin substrate or a substrate having a resin layer in at least a surface layer thereof, and an optical filter manufactured by using the same.  
      To achieve the above mentioned object, the vacuum film deposition method and system of present invention are configured in such a manner that, in the vacuum film deposition method comprising the steps of mounting a substrate on a substrate holder that is disposed in a vacuum chamber and is provided with a passage in which predetermined heat medium flows; maintaining an inside of the vacuum chamber substantially in vacuum state; evaporating evaporation materials from two or more evaporation sources in the inside of the vacuum chamber; diffusing the evaporated evaporation materials in the inside of the vacuum chamber in a predetermined order; and depositing the diffused evaporation materials on a deposition surface of the substrate, thereby forming a multi-layered film made of the evaporation materials on the deposition surface of the substrate, an antifreezing fluid is used as the predetermined heat medium flowing in the passage of the substrate holder. In such a configuration, since the temperature of the substrate holder is set to a freezing point or lower by using the antifreezing fluid, the resin that is low in heat resistant temperature can be used as the substrate on which the multi-layered film is formed.  
      The antifreezing fluid used as the predetermined heat medium is controlled to have a temperature in a temperature range of −5° C. or higher to +30° C. or lower. In such a configuration, since the temperature of the substrate holder is adjustable in the temperature range of −5° C. or higher to +30° C. or lower, the temperature of the substrate is optimally adjusted during formation of the films.  
      The antifreezing fluid used as the predetermined heat medium when mounting or dismounting the substrate on or from the substrate holder is controlled to have a temperature in a temperature range of ±0° C. or higher to +30° C. or lower. In such a configuration, since the temperature of the substrate is set to a temperature substantially equal to a room temperature when mounting and dismounting the substrate on and from the substrate holder, water condensation on the substrate is prevented.  
      The antifreezing fluid used as the predetermined heat medium in a period until the inside of the vacuum chamber is held substantially in the vacuum state is controlled to have a temperature in a temperature range of ±0° C. or higher to +30° C. or lower. In such a configuration, since the temperature of the substrate is set to a temperature substantially equal to the room temperature, water or the like adsorbed onto the surface of the substrate is effectively removed during a process for evacuating the inside of the vacuum chamber to the substantially vacuum state.  
      The antifreezing fluid used as the predetermined heat medium when depositing the multi-layered film on the deposition surface of the substrate in the inside of the vacuum chamber is controlled to have a temperature in a temperature range of −5° C. or higher to ±0° C. or lower. In such a configuration, since the substrate is cooled by the antifreezing fluid, temperature rise due to radiation heat from the evaporation source is prevented.  
      A vacuum film deposition method comprises the steps of mounting a substrate on a substrate holder that is disposed in a vacuum chamber and is provided with a passage in which predetermined heat medium flows; maintaining an inside of the vacuum chamber substantially in vacuum state; evaporating evaporation materials from two or more evaporation sources in the inside of the vacuum chamber; diffusing the evaporated evaporation materials in the inside of the vacuum chamber in a predetermined order; and depositing the diffused evaporation materials on a deposition surface of the substrate, thereby forming a multi-layered film made of the evaporation materials on the deposition surface of the substrate; wherein the passage includes one passages and opposite passages that are arranged radially, and the multi-layered film is formed on the deposition surface of the substrate while flowing the predetermined heat medium into the one passage from an end portion of the substrate holder toward a center portion of the substrate holder, and flowing the predetermined heat medium into the opposite passage from the center portion of the substrate holder toward the end portion of the substrate holder. In such a configuration, the end portion of the substrate holder that tends to increase its temperature is efficiently cooled during film formation. In addition, since an in-plane temperature distribution of the substrate holder is improved, the optical characteristic of the multi-layered film such as an infrared cut filter formed on the deposition surface of the substrate is improved.  
      A film deposition system comprises a vacuum chamber that maintains an inside thereof substantially in vacuum state; a rotational shaft rotatably penetrating through the vacuum chamber; a heat medium supply unit connected to a heat medium supply passage in which a predetermined heat medium flows; a substrate holder fixed to an end portion of the rotational shaft, for holding the substrate having the passage in which the predetermined heat medium flows; and two or more evaporation sources including evaporation materials deposited to form a multi-layered film on a deposition surface of the substrate held on the substrate holder; wherein the rotational shaft has a groove formed to extend over an entire circumference of an outer periphery, the groove is connected to the passage of the substrate holder through a plurality of holes, and the groove is maintained in a sealed state with respect to the heat medium supply unit by a predetermined seal means. In such a configuration, the heat medium is supplied to the substrate holder from the periphery of the rotational shaft.  
      The film deposition system further comprises a tubular housing for accommodating a region of the rotational shaft in which the groove is provided; wherein a penetrating hole forming the heat medium supply unit is formed in a region of an inner peripheral surface of the housing that corresponds to the groove of the rotational shaft, and wherein a seal member is disposed between the housing and the rotational shaft, and the groove is maintained in a sealed state with respect to the penetrating hole by the seal member. In such a configuration, the heat medium is supplied to the substrate holder from the periphery of the rotational shaft.  
      A vacuum film deposition method comprises the steps of: mounting a substrate on a substrate holder that is disposed in a vacuum chamber; maintaining an inside of the vacuum chamber substantially in vacuum state; evaporating evaporation materials from two or more evaporation sources in the inside of the vacuum chamber; diffusing the evaporated evaporation materials in the inside of the vacuum chamber in a predetermined order; and depositing the diffused evaporation materials on a deposition surface of the substrate, thereby forming a multi-layered film made of the evaporation materials on the deposition surface of the substrate; wherein the multi-layered film is formed on the substrate mounted on the substrate holder with a heat conductive adapter interposed between the substrate and the substrate holder. Also, a film deposition system comprises a vacuum chamber that maintains an inside thereof substantially in vacuum state; a substrate holder for holding a substrate in the inside of the vacuum chamber; and two or more evaporation sources including evaporation materials deposited to form a multi-layered film on a deposition surface of the substrate held on the substrate holder; wherein a heat conductive adapter for increasing heat conductivity between the substrate and substrate holder is disposed on a surface of the substrate holder on which the substrate is held. In such a configuration, since heat conductivity between the substrate holder and the substrate is improved, the temperature of the substrate is precisely controlled.  
      A contact area of the heat conductive adapter and the substrate per predetermined area decreases as the contact area is closer to an end portion of the substrate. In such a configuration since the heat conductivity from the substrate holder to the substrate is controlled according to the contact area, the temperature is made substantially equal at a center region and an end region of the resin lens when forming the multi-layered film on the surface of the resin lens.  
      An optical filter of the present invention comprises a resin layer in at least a surface layer of a substrate, and two types of thin films with different light refractive indices that are alternately stacked on the resin layer to form an alternate layer, wherein the alternate layer is comprised of the films of at least 30 layers. In such a configuration, since the optical filter includes the resin layer, the weight of the optical filter is reduced. In addition, the optical characteristic of the optical filter is improved.  
      These and other objects of present invention, as well as the features and advantages thereof will be more clearly disclosed in the following specific examples explained along with the accompanying drawings. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       FIG. 1  is a view schematically showing a vacuum film deposition system in first embodiment of present invention.  
       FIG. 2  is a magnified view schematically showing a rotation drive unit of the vacuum film deposition system shown in  FIG. 1 .  
       FIGS. 3A and 3B  are sectional views of a structure in which an infrared ray cut filter formed on a substrate, in which  FIG. 3A  is a schematic sectional view of structure of the infrared ray cut filter formed on a silicon wafer, and  FIG. 3B  is a schematic sectional view of structure of infrared ray cut filter formed on a resin lens.  
       FIG. 4  is a view vacuum film deposition system in second embodiment of present invention.  
       FIG. 5  is a magnified view schematically showing the rotation drive unit of the vacuum film deposition system shown in  FIG. 4 .  
       FIGS. 6A and 6B  are schematic views of a heat conductive adapter, in which  FIG. 6A  is a plan view thereof, and  FIG. 6B  is a sectional view along line VI-VI of  FIG. 6A .  
       FIGS. 7A and 7B  are graphs schematically showing the optical characteristic of infrared ray cut filter, in which  FIG. 7A  shows the optical characteristic when the filter is comprised of 48 layers,  FIG. 7B  shows the optical characteristic when the filter is comprised of 40 layers,  FIG. 7C  shows the optical characteristic when the filter is comprised of 30 layers, and  FIG. 7D  shows the optical characteristic when the filter is comprised of 16 layers. 
    
    
     BEST MODE FOR CARRYING OUT PRESENT INVENTION  
      The best mode for carrying out present invention is described below by referring to the accompanying drawings.  
      (First Embodiment)  
       FIG. 1  is a view of vacuum film deposition system in first embodiment of present invention.  FIG. 2  is a magnified view schematically showing a rotation drive unit of the vacuum film deposition system shown in  FIG. 1 . In this embodiment of present invention, an ion plating system is illustrated as the vacuum film deposition system.  
      Referring first to  FIG. 1  and  FIG. 2 , the structure of ion plating system in the first embodiment of present invention is specifically described below.  
      As shown in  FIG. 1 , the ion plating system  100  comprises evaporation sources  2   a  and  2   b  for evaporating film materials disposed inside a vacuum chamber  1  made of conductive material, and a circular substrate holder  6   a  made of a conductive material that is disposed opposite to the evaporation sources  2   a  and  2   b . A substrate  21   a , a silicon wafer herein, is fixed on the substrate holder  6   a  on the substrate mounting surface of the substrate holder  6   a  by means of a predetermined fixing member  36 . The evaporation sources  2   a  and  2   b  herein are comprised of a hearth  5   a  that disposes a film material, and an electron gun not shown disposed near the hearth  5   a . Above the evaporation sources  2   a  and  2   b , movable shutters  3   a  and  3   b  are pivotally disposed by means of rotational shafts  4   a  and  4   b . On the back side of the substrate holder  6   a , a columnar rotational shaft element  7   a  formed of conductive material extends. This rotational shaft element  7   a  is disposed to extend to outside through a wall  1   a  of the vacuum chamber  1 . A portion of the rotational shaft element  7   a  protruding outward from the wall la (hereinafter called protruding portion) is rotatably supported on the housing  10  by a cross roller bearing  9  and an oil seal  19  so as to be driven to rotate by a rotation drive device  8 . Since the oil seal  19  is disposed between the rotational shaft element  7   a  and the housing  10 , the inside of the vacuum chamber  1  is kept in predetermined vacuum state.  
      As shown in  FIG. 1  and  FIG. 2 , to apply a radio-frequency power and a direct-current power specified below to a current feeding ring  7   t  disposed on the outer circumference at the tip end of the protruding portion of the rotational shaft element  7   a , a carbon brush  11  is disposed to contact directly the current feeding ring  7   t  as power transmission structure. This carbon brush  11  is fixed at a predetermined position on the housing  10  by a predetermined fixing means. As a result, the carbon brush  11  and the rotational shaft element  7   a  are held in electrically conducting state. Further, as shown in  FIG. 1 , the carbon brush  11  is connected to a direct-current blocking capacitor Co and a radio-frequency blocking choke coil Lo through a cable  12 . The direct-current blocking capacitor Co is connected to a radio-frequency power source  14  through a matching circuit  13 . The radio-frequency blocking choke coil Lo is connected to a direct-current power source  15 . One terminal of the radio-frequency power source  14 , positive terminal of the direct-current power source  15 , and vacuum chamber  1  are respectively grounded. On the outer periphery of tip end of protruding portion of the rotational shaft element  7   a , a cylindrical gear  16  to be engaged with a spur gear  8   a  of the rotation drive device  8  including, for example, motor M is mounted. By engagement between the spur gear  8   a  and the gear  16 , the rotation drive device  8  operates to rotate the spur gear  8   a , and rotation of the spur gear  8   a  causes the rotational shaft element  7   a  to rotate. When the rotation drive device  8  operates, the substrate holder  6   a  rotates, and the substrate  21   a  rotates about a rotation center c. The rotation drive device  8  is fixed at predetermined position of the housing  10  by a predetermined fixing method.  
      The housing  10  made of a conductive material is disposed so as to cover a part of the carbon brush  11 , the protruding portion of the rotational shaft element  7   a , and the rotation drive device  8 . The housing  10  has a substantially cylindrical shape closed at an upper end and opened at the bottom. It is fixed on the wall  1   a  of the vacuum chamber  1  by a fixing member  17  with an electric insulating member  18  interposed between them. Therefore, the housing  10  and the vacuum chamber  1  are held in electrically insulated state. Thereby, the radio-frequency power and the direct-current power are applied to the carbon brush  11 , and the radio-frequency power and the direct-current power are applied to the housing  10  through the rotational shaft element  7   a  and the cross roller bearing  9 . As a result, the vacuum chamber  11  is always kept in electrically grounded state.  
      Referring now to  FIG. 2 , the cooling passage of the substrate holder in the ion plating system in the first embodiment of the present invention is specifically described below.  
      As shown in FIG., grooves  7   b  and  7   c  are formed at predetermined positions on the outer periphery of the protruding portion of the rotational shaft element  7   a . These grooves  7   b  and  7   c  are formed like a ring over the entire circumference of the rotational shaft element  7   a . In the upper part and lower part of the grooves  7   b  and  7   c , O-rings  20   a  to  20   c  are disposed. These O-rings  20   a  to  20   c  are disposed between the rotational shaft element  7   a  and the housing  10 . That is, the grooves  7   b  and  7   c  are closed by the O-rings  20   a  to  20   c  and the housing  10 . Openings are formed in the bottom of the grooves  7   b  and  7   c , and these openings communicate with pipe rings  7   d  and  7   e  formed concentrically with the rotation center c. From the pipe rings  7   d  and  7   e , pipes  7   f  and  7   g  extend in the radial direction of the rotational shaft element  7   a , and these pipes  7   f  and  7   g  extend from predetermined positions in the rotational shaft direction of the rotational shaft element  7 . The pipes  7   f  and  7   g  reach the substrate holder  6   a , and are connected to pipe rings  7   h  and  7   i  formed concentrically with the rotation center substantially in the center of the substrate holder  6   a . Inside the substrate holder  6   a , a plurality of cooling pipes  7   j  are disposed to extend in U-shape in the radial direction of the substrate holder  6 . These cooling pipes  7   j  are provided inside the substrate holder  6   a  so as to communicate with the pipe rings  7   h  and  7   i . That is, the cooling pipes  7   j  extend radially from the outer periphery of the pipe ring  7   h  toward the end portion of the substrate holder  6   a , and turn at the end portion of substrate holder  6   a  to extend in the opposite direction toward the pipe ring  7   i  so as to be connected to the outer periphery of the pipe ring  7   i . In the grooves  7   b  and  7   c  formed concentrically with the rotation center c on the outer periphery of the rotational shaft element  7   a , a discharge pipe  22  and a supply pipe  23  are disposed in the housing  10  to communicate with the grooves  7   b  and  7   c  in order to supply predetermined heat medium used for controlling the temperature of the substrate holder  6   a.    
      As shown in  FIG. 2 , a connection pipe  24  indicated by solid line is connected to the discharge pipes  2  and a connection pipe  25  indicated by solid line is connected to the supply pipe  23 . Further, as shown in  FIG. 1 , the connection pipe  24  is connected to a three-way valve  26 , and two connection pipes extending from the three-way valve  26  are connected to a warm brine tank  29   a  and a cold brine tank  29   b . A liquid feed pump  27  is disposed at a position of the connection pipe  25  extending from the supply pipe  23 . The connection pipe  25  is connected to a three-way valve  28 . Two connection pipes extending from the three-way valve  28  are connected to the warm brine tank  29   a  and the cold brine tank  29   b . Antifreezing fluid is contained in the warm brine tank  29   a  and the cold brine tank  29   b . In the warm brine tank  29   a , the antifreezing fluid is controlled to have a temperature of about 25° C. by a predetermined temperature controller not shown so that the liquid temperature may be about 25° C. In the cold brine tank  29   b , the antifreezing fluid is controlled to have a temperature of about −5° C. by a predetermined temperature controller not shown so that the liquid temperature may be about −5° C.  
      In the ion plating system thus constructed, the operation will be described by referring to  FIG. 1  and  FIG. 2 .  
      When forming a multi-layered film on the deposition surface of the substrate by using the ion plating system  100 , an operator mounts, before depositing the film, the substrate  21   a  such as a silicon wafer on the substrate mounting surface of the substrate holder  6   a  by using predetermined fixing member  36 . The substrate  21   a  is mounted on the substrate holder  6   a  so that the back surface of the substrate  21   a  may contact the substrate mounting surface of the substrate holder  6   a . When mounting the substrate  21   a  on the substrate holder  6   a , in order to prevent moisture in the atmosphere from water condensation on the substrate holder  6   a , the three-way valve  26  and the three-way valve  28  are manipulated appropriately to operate the liquid feed pump  27 , and the antifreezing fluid (for example, ethylene glycol) contained in the warm brine tank  29   a  and controlled to have a temperature of about 25° C. is flowed to the connection pipe  25 . The antifreezing fluid of about 25° C. supplied to the supply pipe  23  through the connection pipe  25  is first filled into the groove  7   c . Then, the antifreezing is filled into the inside of the pipe ring  7   e . The antifreezing fluid flows in the pipe  7   g  and further flows in the plural cooling pipes  7   j  from the center of the substrate holder  6   a  toward the end portion. Then, the antifreezing fluid flowing in the cooling pipes  7   j  from the end portion toward the center in the substrate holder  6   a  flows in the pipe  7   f , and is filled into the pipe ring  7   d . The antifreezing fluid filled in the pipe ring  7   d  is filled into the groove  7   b , and flows in the connection pipe  24  through the discharge pipe  22 . The antifreezing fluid flowing in the connection pipe  24  is returned to the warm brine tank  29   a  by the three-way valve  26 . Thus, since the substrate holder  6   a  is warmed by the antifreezing fluid of about 25° C., water condensation due to moisture in the atmosphere can be prevented. After the substrate  21   a  is mounted on the substrate holder  6   a , the inside of the vacuum chamber  1  is evacuated to a predetermined degree of vacuum by operating a predetermined exhaust means not shown. In this case, in order to easily release the gas of the substrate  21   a  during the evacuation, the antifreezing fluid controlled to have a temperature of about 25° C. is supplied continuously from the warm brine tank  29   a  toward the substrate holder  6   a . As a result, the gas adsorbed on the substrate  21   a  can be effectively removed. This supply of antifreezing fluid to the substrate holder  6   a  continues until evacuation is completed. Thereafter, when it is confirmed that the vacuum chamber  1  becomes substantially vacuum, the rotation drive device  8  is operated, and the spur gear  8   a  is rotated at predetermined speed. As the rotation drive device  8  operates, the spur gear  8   a  rotates, and by the rotation of the spur gear  8   a , the rotational shaft element  7   a  rotates about the rotation center c. As a result, the substrate holder  6   a  attached to the lower end of the rotational shaft element  7   a  rotates, and the substrate  21   a  rotates about the rotation center c.  
      Meanwhile, the radio-frequency power source  14  and the direct-current power source  15  are turned on. The radio-frequency power generated by the radio-frequency power source  14  is supplied to the cable  12  through the matching circuit  13  and the direct-current blocking capacitor Co. The direct-current power generated by the direct-current power source  15  is supplied to the cable  12  through the choke coil Lo for radio-frequency blocking. The radio-frequency power and the direct-current power are supplied to the carbon brush  11  through the cable  12 . Thus, the radio-frequency power and the direct-current power are supplied to the carbon brush  11 , and further are supplied to the current feeding ring  7   t  in contact with the carbon brush  11 . The radio-frequency power and the direct-current power transmitted to the current feeding ring  7   t  are transmitted to the substrate holder  6   a  through the conductive rotational shaft element  7   a . As a result, the radio-frequency power and the direct-current power are supplied between the substrate holder  6   a  and the vacuum chamber  1 .  
      Then, in the evaporation sources  2   a  and  2   b , the electron guns are operated, and electron beams are emitted to film materials in the hearths  5   a  and  5   b  at predetermined intensity. The film materials are preheated to a predetermined temperature by the energy of emitted electron beams. When diffusing the film materials alternately inside the vacuum chamber  1 , the emission intensity of the electron beams emitted from the electron guns in the evaporation sources  2   a  and  2   b  are increased alternately, and thereby the film materials in the hearths  5   a  and  5   b  are dissolved alternately. At this time, by alternately rotating the rotational shafts  4   a  and  4   b  so that only the upper part of the dissolved film materials may be opened, the shutters  3   a  and  3   b  are alternately moved above the evaporation sources  2   a  and  2   b . Since the inside of the vacuum chamber  1  is already in substantially vacuum state, the film materials are alternately diffused from the evaporation sources  2   a  and  2   b  into the vacuum chamber  1 . The diffused film materials are excited by the plasma generated by the radio-frequency power, and the excited film materials are accelerated by the electric field between the substrate holder  6   a  and vacuum chamber  1  generated by the direct-current power, and are impinged onto and adhered to the surface of the substrate  21   a . Hence, dense thin films are formed alternately on the deposition surface of the substrate  21   a . That is, the multi-layered thin film comprised of the dense thin films is formed on the deposition surface of the substrate  21   a . When forming the multi-layered film, in order to prevent excess temperature rise of substrate  21   a  due to radiation heat from the evaporation sources  2   a  and  2   b , the three-way valve  28  and the three-way valve  26  are manipulated appropriately, and the liquid feed pump  27  is operated to flow the antifreezing fluid controlled to have a temperature of about −5° C. contained in the cold brine tank  29   b  into the connection pipe  25  at a predetermined flow rate. Thereby, the antifreezing fluid controlled to have a temperature of about −5° C. is supplied to flow in the pipes  7   f  and  7   g , and the cooling pipes  7   j  formed inside the rotational shaft element  7   a  and the substrate holder  6   a . That is, the substrate  21   a  is indirectly cooled by the cooling of the substrate holder  6   a  by the antifreezing fluid controlled to have a temperature of about −5° C., so that temperature rise can be prevented effectively.  
      After a predetermined number of layers are formed on the deposition surface of the substrate  21   a , atmospheric air is introduced into the vacuum chamber  1  to return it to an atmospheric pressure. At this time, in order to prevent water condensation on the substrate  21   a  due to the moisture in the atmosphere, the three-way valve  28  and the three-way valve  26  are manipulated appropriately, and the liquid feed pump  27  is operated to flow the antifreezing fluid filled in the warm brine tank  29   a  and controlled to have a temperature of about 25° C. into the connection pipe  25 . As a result, the antifreezing fluid controlled to have a temperature of about 25° C. is supplied to flow in the pipes  7   f  and  7   g , and the cooling pipes  7   j  formed inside the rotational shaft element  7   a  and the substrate holder  6   a . That is, the substrate  21   a  is indirectly warmed by warming of the substrate holder  6   a  by the antifreezing fluid controlled to have a temperature of about 25° C., so that water condensation can be prevented effectively.  
      Next, a structure of the multi-layered film formed on the substrate by the above mentioned operation of the ion plating system will be described below by referring to  FIG. 3 .  
       FIG. 3A  is a schematic sectional view of a structure in which an infrared ray cut filter formed on a silicon wafer.  
      In  FIG. 3A , a silicon wafer 30 has a shape of a flat plate of, for example, 3 to 12 inches in diameter, and 0.3 to 0.6 mm in thickness. In the center region of a principal surface of the silicon wafer  30 , a photo resist  31  of a flat plate shape is formed in advance by predetermined manufacturing process. This photo resist  31  is circular to have a maximum diameter A, and its thickness is substantially uniform. The photo resist  31  is formed of thermoplastic polymer resin, and its heat resistant temperature is about 100° C. Therefore, when forming a multi-layered film functioning as infrared ray cut filter on the surface of the silicon wafer  30  and the photo resist  31 , it is required to cool the silicon wafer  30  and the photo resist  31  to temperatures to preferably 90° C. or lower. In the embodiment, as mentioned above, the silicon wafer  30  and the photo resist  31  are cooled by flowing the antifreezing fluid controlled to have a temperature of about −5° C. inside the substrate holder  6   a . Hence, on the surface of the silicon wafer  30  and the photo resist  31 , an infrared ray cut filter  32  is formed. This infrared ray cut filler  32  is comprised of 30 layers or more, or preferably 40 layers or more of two different kinds of thin films with different light transmission characteristics. These two different kinds of films are preferably silicon dioxide and tantalum pentoxide, or silicon dioxide and neodymium pentoxide. Because of a stacked structure as mentioned above, the infrared cut filter  32  functions to block passing of an infrared ray in a predetermined wavelength range. After forming the infrared ray cut filter  32  on the surface of silicon wafer  30  and the photo resist  31 , the photo resist  31  is peeled off.  
      Generally, the optical characteristic (light transmission characteristic) of the infrared ray cut filter  32  varies significantly depending on the number of layers of the infrared ray cut filter. The optical characteristics of the infrared ray cut filters are explained below by referring to the drawings.  
       FIGS. 7A  to  7 D are graphs schematically showing examples of measured data of the optical characteristic (light transmission characteristic) of the infrared ray cut filter.  FIG. 7A  shows the optical characteristic of the filter comprised of 48 layers,  FIG. 7B  shows the optical characteristic of the filter comprised of 40 layers,  FIG. 7C  shows the optical characteristic of the filter comprised of 30 layers, and  FIG. 7D  shows the optical characteristic of the filter comprised of 16 layers. In the graphs in  FIG. 7A  to  FIG. 7D , the axis of abscissas denotes the wavelength (nm) of light, and the axis of ordinates represents the light transmissivity (%). Here, the examples of measurement of the infrared ray cut filter having the structure shown in  FIG. 3  are illustrated.  
      Typically, an infrared ray is an electromagnetic wave in a wavelength range from the lower limit of about 750 nm at longer wavelength end of visible ray of light to the upper limit of about 1 mm. Therefore, the infrared ray cut filter is strongly required to have an optical characteristic for sharply cutting off the infrared ray in a wavelength range of about 650 nm to 700 nm. The reason is that if using an infrared ray cut filter slowly declining in the transmissivity in a wavelength range of, for example, about 600 nm to 700 nm, the longer wavelength side of the visible ray of light is undesirably cut off due to the effects of the slowing declining transmissivity, and the color balance is worsened visually. As shown by line L 4  in  FIG. 7D , in the case of the infrared ray cut filter comprised of 16 layers, the inclination of line L 4  in the range of 600 nm to 700 nm is moderate, and a specific peak is present near 920 nm. That is, the infrared ray cut filter comprised of 16 layers does not satisfy the above mentioned requirements, and is unable to sufficiently cut the infrared ray with a wavelength of about 920 nm. Therefore, it is judged that the infrared cut filter comprised of 16 layers is hard to use. On the other hand, as shown in  FIG. 7C , in the case of the infrared ray cut filter comprised of 30 layers, the optical characteristic L 3  is sharply lowered in transmissivity in a wavelength range of about 650 nm to 700 nm, and the transmissivity of about 900 nm is lowered significantly as compared with that shown in  FIG. 7D . That is, the optical characteristic of the infrared cut filter comprised of 30 layers satisfies the required optical characteristic demanded of the infrared ray cut filter. Further, the optical characteristics L 2  and L 1  respectively corresponding to the infrared cut filters comprised of 40 layers and 48 layers are further lowered sharply in the transmissivity in a wavelength range of about 650 nm to 700 nm, and its transmissivity with a wavelength of about 900 nm is further lowered as compared with that of  FIG. 7D . That is, the optical characteristics of the infrared cut filters comprised of 48 and 40 layers well satisfy the required optical characteristic of the infrared ray cut filter. Thus, the optical characteristic of the infrared ray cut filter varies significantly depending on the number of layers being stacked. To satisfy sufficiently the required optical characteristic of the infrared ray cut filter, it is necessary to manufacture an infrared ray cut filter comprised of at least 30 stacked layers, preferably 40 stacked layers. Because the infrared ray cut filter 32 shown in  FIG. 3A  in the embodiment is comprised of 40 layers, it may be very useful as an infrared ray cut filter of excellent optical characteristic.  
      By using the vacuum film deposition system of the present invention having the construction and configured to operated as described above, the following effects are obtained.  
      In the present invention, the antifreezing fluid is used as a heat medium for cooling the substrate. By using the antifreezing fluid, the temperature of the substrate holder can be kept below the freezing point (for example, −5° C. or higher to ±0° C. or lower). So, the substrate is indirectly cooled by the antifreezing fluid, and temperature rise of substrate due to radiation heat from the evaporation sources can be effectively prevented. Hence, it is possible to use resin material that is low in heat resistant temperature to form the substrate on which a multi-layered film is deposited. Also, even if the substrate itself is not formed of resin, the present invention is very effective when a resin layer or the like is formed on the substrate as shown in the embodiment. That is, on the substrate having at least the resin layer, 30 or more layers of the infrared ray cut filter is able to be formed. By forming the multi-layered film on the resin, the weight of the optical filter can be significantly reduced. Further, by controlling the temperature of the antifreezing fluid flowing in the passage formed inside the substrate holder in a temperature range of −5° C. or higher to +30° C. or lower, the temperature of the substrate holder can be adjusted in a temperature range of −5° C. or higher to +30° C. or lower. As a result, the temperature of the substrate can be adjusted to have an optimum temperature during film formation. When mounting or dismounting the substrate on or from the substrate holder, by controlling the temperature of the antifreezing fluid in a temperature range of ±0° C. or higher to +30° C. or lower, the temperature of the substrate can be adjusted to be substantially equal to a room temperature. As a result, water condensation on the substrate can be prevented effectively. This becomes very effective means for enhancing the quality of the multi-layered film formed on the deposition surface of substrate. In a time period until the inside of the vacuum chamber is substantially held in vacuum state, by controlling the antifreezing fluid in a temperature range of −0° C. or higher to +30° C. or lower, the temperature of the substrate and substrate holder can be controlled to be substantially equal to the room temperature. So, in the process for evacuating the inside of the vacuum chamber substantially in vacuum state, moisture or the like adsorbed onto the surface of the substrate and the substrate holder can be removed effectively. Also, when forming the multi-layered film on the substrate, the antifreezing fluid used to cool the substrate is flowed into the passage of the substrate holder from the end to the center region of the substrate holder, the end portion of the substrate holder that tends to increase its temperature is efficiently cooled during film depositing process. Since the substrate is cooled by the cooling of the substrate holder in the film depositing process, distortion or deformation of substrate can be prevented, and the optical characteristic of the multi-layered film formed on the deposition surface of the substrate can be improved. In addition, since the vacuum film deposition system of the present invention has grooves on the outer periphery of the rotational shaft, a plurality of holes are formed in the grooves, pipes of predetermined shapes communicate with the plurality of holes, and the pipes are connected to the passages formed inside the substrate holder, the heat medium such as the antifreezing fluid can be supplied to the substrate holder from the periphery of the rotational shaft.  
      (Second Embodiment)  
       FIG. 4  is a cross-sectional view schematically showing a construction of a vacuum film deposition system in second embodiment of present invention.  FIG. 5  is a magnified cross-sectional view schematically showing a rotation drive unit of the vacuum film deposition system shown in  FIG. 4 . In this embodiment, also, an ion plating system is illustrated as the vacuum deposition system.  
      Referring first to  FIG. 4  and  FIG. 5 , the structure of the ion plating system in the second embodiment of present invention will be described. The vacuum film deposition system of this embodiment is basically similar to the vacuum film deposition system of the first embodiment, except for the internal structure of the rotational shaft element and the substrate holder, and the feed mechanism of antifreezing fluid. So, explanation of same parts is omitted.  
      As shown in  FIG. 4 , as in the first embodiment, the ion plating system  200  comprises the evaporation sources  2   a  and  2   b  disposed inside the vacuum chamber  1  made of a conductive material to evaporate film materials. Opposite to the evaporation sources  2   a  and  2   b , a circular substrate holder  6   a  made of a conductive material is disposed. From the back side of the substrate holder  6   b , a rotational shaft element  7   u  extends. A substrate  21   b  which is a lens formed of resin is mounted and fixed on the substrate mounting surface of the substrate holder  6   b  by the fixing member  36  with a heat conductive adapter  35  described below interposed between them. That is, the back surface of the substrate  21   b , and the heat conductive adapter  35  and the substrate mounting surface of the substrate holder  6   b  contact each other. Other structure is the same as that described the first embodiment.  
       FIGS. 6A and 6B  are schematic views of the heat conductive adapter  35 , in which  FIG. 6A  is a plan view thereof, and  FIG. 6B  is a sectional view along line VI-VI of  FIG. 6A .  
      As shown in  FIG. 6A  and  FIG. 6B , the heat conductive adapter  35  is formed to have a diameter substantially equal to the diameter of the lens mounted thereon. The heat conductive adapter  35  has a curved surface  35   a  formed according to the radius of curvature of the lens to be mounted thereon, and a stepped part  35   b  having a predetermined flat surface at a position lower than the curved surface  35   a . The stepped part  35   b  is formed in a taper shape from the outer periphery toward the center of the heat conductive adapter  35  in a plan view, so as not to contact the lens to be mounted thereon. The stepped part  35   b  is formed in the heat conductive adapter  35  in order to make a uniform in-plane temperature distribution in the transition state of temperature change of the lens to be mounted thereon. For example, in the case where a convex lens is used, because the convex lens is thick in the central part and thin in the peripheral part, its heat capacity decreases from the central part to the peripheral part. Accordingly, by forming the stepped part  35   b  in the heat conductive adapter  35 , the transmission heat from the heat conductive adapter  35  is made less at the peripheral part, and difference in heat capacity in the in-plane temperature distribution of the lens is canceled. Since the curved surface  35   a  of the heat conductive adapter  35  is formed according to the radius of curvature of the lens to be mounted thereon, the heat conductive adapter  35  is prepared for every kind of lenses to be mounted thereon. The forming material of the heat conductive adapter  35  is not particularly limited as long as it is highly heat conductive. Herein, stainless steel is used for forming the heat conductive adapter  35 .  
      Referring now to  FIG. 5 , the cooling passage of substrate holder in the ion plating system of the second embodiment of present invention is described specifically below.  
      As shown in  FIG. 5 , grooves  7   k ,  7   l ,  7   b ,  7   c  are formed at predetermined positions on the outer periphery of the protruding portion of the rotational shaft element  7   u . These grooves  7   k ,  7   l ,  7   b , and  7   c  are formed like rings over the entire circumference of the rotational shaft element  7   u . O-rings  20   a  to  20   e  are disposed in upper and lower parts of these grooves  7   k ,  7   l ,  7   b , and  7   c . These O-rings  20   a  to  20   e  are disposed between the rotational shaft element  7   u  and the housing  10 . That is, the grooves  7   k ,  7   l ,  7   b , and  7   c  are closed by the O-rings  20   a  to  20   e  and the housing  10 . Openings are formed in the bottom of the respective of the grooves  7   k ,  7   l ,  7   b , and  7   c , and communicate with pipe rings  7   p ,  7   o ,  7   d , and  7   e  formed concentrically with the rotation center c. From these pipe rings  7   p ,  7   o ,  7   d , and  7   e , pipes  7   n ,  7   m ,  7   f , and  7   g  extend in the radial direction of the rotational shaft element  7   u . Furthermore, these pipes  7   n ,  7   m ,  7   f , and  7   g  extend in the rotational shaft direction of the rotational shaft  7   u  from predetermined positions. The pipes  7   n ,  7   m ,  7   f , and  7   g  reach the substrate holder  6   b  and are connected to pipe rings  7   s ,  7   r ,  7   h , and  7   i  formed concentrically with the rotation center c in substantially the central part. Inside the substrate holder  7   b , a plurality of cooling pipes  7   j  and warming pipes  7   q  are disposed to extend in U-shape in the radial direction of the substrate holder  6   b , and these cooling pipes  7   j  and the warming pipes  7   q  are provided inside of the substrate holder  6   b  so as to communicate with the pipe rings  7   s ,  7   r ,  7   h , and  7   i . That is, the plurality of cooling pipes  7   j  and the plurality of warming pipes  7   q  extend radially from the outer peripheries of the pipe rings  7   s  and  7   h  toward the end portion of the substrate holder  6   b , and further extend in the opposite direction at the end portion of the substrate holder  6   b  toward the pipe rings  7   r  and  7   i  to be connected to the outer peripheries of the pipe rings  7   r  and  7   i . Further, to supply predetermined heat medium used for controlling the temperature of the substrate holder  6   b  to the grooves  7   k ,  7   l ,  7   b , and  7   c  formed concentrically with the rotation center c on the outer periphery of the rotational shaft element  7   u , discharge pipes  22   a  and  23   b  and supply pipes  23   a  and  22   b  are disposed in the housing  10  so as to communicate with the grooves  7   k ,  7   l ,  7   b , and  7   c.    
      As shown in  FIG. 5 , connection pipes  24   a  and  25   b  indicated by solid line are connected to the discharge pipes  22   a  and  23   b , and connection pipes  25   a  and  24   b  indicated by solid line are connected to the supply pipes  23   a  and  22   b . Further, as shown in  FIG. 4 , the connection pipe  24   a  and the connection pipe  25   a  are each connected to the cold brine tank  29   b . At a position of the connection pipe  25   a , the liquid feed pump  27   a  is disposed. The connection pipe  24   b  and the connection pipe  25   b  are connected to the warm brine tank  29   a . At a position of the connection pipe  24   b , the liquid feed pump  27   b  is disposed. Antifreezing fluid is contained in the warm brine tank  29   a  and the cold brine tank  29   b . In the warm brine tank  29   a , the antifreezing fluid is controlled to have a temperature of about 25° C. by a predetermined temperature controller not shown. In the cold brine tank  29   b , the antifreezing fluid is controlled to have a temperature of about −5° C. by a predetermined temperature controller not shown.  
      Subsequently, the operation of the ion plating system thus constructed will be described by referring to  FIG. 4  and  FIG. 5 .  
      When forming a multi-layered film on the deposition surface of the substrate by using the ion plating system  200 , the operator mounts, before depositing the film, the substrate  21   b  which is the resin lens on the substrate mounting surface of the substrate holder  6   b  by using a predetermined fixing member  36  with the heat conductive adapter  35  interposed between them. In this case, the substrate  21   b  is mounted on the substrate holder  6   b  with the heat conductive adapter  35  interposed between them so that the back surface of the substrate  21   b  may contact the heat conductive adapter  35  and the substrate mounting surface of the substrate holder  6   b . When mounting the substrate  21   b  on the substrate holder  6   b , in order to prevent water condensation on the substrate holder  6   b  due to moisture in the atmosphere, the liquid feed pump  27   b  is operated to flow the antifreezing fluid controlled to have a temperature of about 25° C. contained in the warm brine tank  29   a  to the connection pipe  24   b . The antifreezing fluid with about 25° C. flowing in the connection pipe  24   b  and supplied to the supply pipe  22   b  is first filled into the groove  7   k . Then, the antifreezing fluid is supplied into the pipe ring  7   p . The antifreezing fluid flows in the pipe  7   n  and further in the plural cooling pipes  7   q  from the center of the substrate holder  6   b  toward the end portion thereof. Then, the antifreezing fluid flows in the cooling pipes  7   q  from the end portion toward the center portion in the substrate holder  6   b  and flows in the pipe  7   m  to be filled into the pipe ring  7   o . The antifreezing fluid filled in the pipe ring  7   o  is filled into the groove  7   l , and flows in the connection pipe  25   b  through the discharge pipe  23   b . The antifreezing fluid flowing in the connection pipe  25   b  is returned to the warm brine tank  29   a . Thus, since the substrate holder  6   b  is warmed by the antifreezing fluid with a temperature of about 25° C., water condensation due to moisture in the atmosphere can be prevented. After the substrate  21   b  is mounted on the substrate holder  6   b , the inside of the vacuum chamber  1  is evacuated to the predetermined degree of vacuum by operating a predetermined exhaust means not shown. During the evacuation, in order to easily release the gas of the substrate  21   a , the antifreezing fluid controlled to have a temperature of about 25° C. is supplied continuously from the warm brine tank  29   a  toward the substrate holder  6   b . As a result, the gas adsorbed on the substrate  21   b  can be effectively removed. This supply of antifreezing fluid to the substrate holder  6   b  continues until evacuation is completed. When it is confirmed that the vacuum chamber  1  becomes substantially vacuum, the rotation drive device  8  is operated, and the spur gear  8   a  is rotated at a predetermined speed. As the rotation drive device  8  operates, the spur gear  8   a  rotates, and by the rotation of the spur gear  8   a , the rotational shaft element  7   u  rotates about the rotation center c. As a result, the substrate holder  6   b  attached to the lower end of the rotational shaft element  7   u  rotates, and thereby the substrate  21   b  rotates about the rotation center c.  
      The radio-frequency power source  14  and the direct-current power source  15  are turned on. The radio-frequency power generated by the radio-frequency power source  14  is supplied to the cable  12  through the matching circuit  13  and the direct-current blocking capacitor Co. The direct-current power generated by the direct-current power source  15  is supplied to the cable  12  through the choke coil Lo for radio-frequency blocking. The radio-frequency power and the direct-current power are supplied to the carbon brush  11  through the cable  12 . The radio-frequency power and the direct-current power are supplied to the carbon brush  11 , and further are transmitted to the current feeding ring  7   t  in contact with the carbon brush  11 . The radio-frequency power and the direct-current power transmitted to the current feeding ring  7   t  are transmitted to the substrate holder  6   b  through the conductive rotational shaft element  7   u.    
      In the evaporation sources  2   a  and  2   b , the electron guns are operated, and electron beams are emitted to film materials in the hearths  5   a  and  5   b  at predetermined intensity. The film materials are preheated to predetermined temperature by the energy of the emitted electron beams. When diffusing the film materials alternately in the vacuum chamber  1 , the emission intensity of electron beams emitted from electron guns in the evaporation sources  2   a  and  2   b  are increased alternately, and the film materials in the hearths  5   a  and  5   b  are dissolved alternately. At this time, by alternately rotating the rotational shafts  4   a  and  4   b  so that only the upper part of the dissolved film materials may be opened, the shutters  3   a  and  3   b  are alternately moved above the evaporation sources  2   a  and  2   b . Since the inside of the vacuum chamber  1  is already in substantially vacuum state, the film materials are alternately diffused from the evaporation sources  2   a  and  2   b  into the vacuum chamber  1 . The diffused film materials are excited by the plasma generated by the radio-frequency power, and the excited film materials are accelerated by the electric field between the substrate holder  6   b  and the vacuum chamber  1  that is generated by the direct-current power, and are impinged onto and adhered to the surface of the substrate  21   b . Hence, dense thin films are formed alternately on the deposition surface of the substrate  21   b . That is, the multi-layered thin film comprised of the dense thin films is formed on the deposition surface of the substrate  21   a . When depositing the multi-layered film, in order to prevent excess temperature rise of substrate  21   b  due to radiation heat from the evaporation sources  2   a  and  2   b , the liquid feed pump  27   a  is operated to flow the antifreezing fluid controlled to have a temperature of about −5° C. contained in the cold brine tank  29   b  into the connection pipe  25   a  at a predetermined flow rate. Thereby, the antifreezing fluid controlled to have a temperature of about −5° C. is supplied to flow in the pipes  7   g  formed inside the rotational shaft element  7   u , and further flows in the cooling pipes  7   j  formed inside the substrate holder  6   b  from the center to the end portion of the substrate holder  6   b . The antifreezing fluid reaching the end portion of the substrate holder  6   b  flows in the opposite direction at the end portion, flows toward the center of the substrate holder  6   b , flows in the pipes  7   f  formed inside the rotational shaft element  7   u , and is discharged from the discharge pipe  22   a . At this time, the liquid feed pump  27   b  is operated to flow the antifreezing fluid controlled to have a temperature of about 25° C. contained in the warm brine tank  29   a  into the supply pipe  22   b  at a predetermined flow rate. Thereby, the antifreezing fluid controlled to have a temperature of about 25° C. flows in the pipe  7   n  formed inside the rotational shaft element  7   u , and flows in the warming pipe  7   q  formed inside the rotational shaft element  7   u  from the center to the end portion of the substrate holder  6   b . The antifreezing fluid reaching the end portion of the substrate holder  6   b  flows in the opposite direction at the end portion, then flows toward the center of the substrate holder  6   b , flows in the pipe  7   m  formed inside the rotational shaft element  8   u , and is discharged from the discharge pipe  23   b . Thus, in the film deposition process, by supplying cold brine and warm brine to the substrate holder  6   b , the substrate  21   b  is cooled indirectly and uniformly in-plane by cooling of the substrate holder  6   b.    
      As in the first embodiment, after the predetermined multi-layered film is formed on the deposition surface of the substrate  21   b , atmospheric air is introduced into the vacuum chamber  1 , which is thereby returned to an atmospheric pressure. At this time, to prevent water condensation at the substrate  21   b  due to the moisture in the atmosphere, the liquid feed pump  27   a  is stopped and the liquid feed pump  27   b  is operated to flow the antifreezing fluid controlled to have a temperature of about 25° C. contained in the warm brine tank  29   a  into the connection pipe  24   b . Thereby, the antifreezing fluid controlled to have a temperature of about 25° C. flows in the pipes  7   n  and  7   m  and the warming pipes  7   q  formed inside the rotational shaft element  7   u  and the substrate holder  6   b . That is, since the substrate  21   b  is warmed indirectly by warming of the substrate holder  6   b  by the antifreezing fluid controlled to have a temperature of about 25° C., water condensation can be prevented effectively.  
      A structure of the multi-layered film deposited on the substrate by such operation of the ion plating system will be described below by referring to  FIG. 3 .  
       FIG. 3B  is a schematic sectional view of a structure in which an infrared ray cut filter is formed on a resin optical lens.  
      In  FIG. 3B , an optical lens  33  has a convex lens shape of, for example, 5 to 40 mm in diameter, and 5 mm to 10 mm in maximum thickness in the center. This optical lens  33  is made of a thermoplastic polymer resin such as Zeonor or Arton, and its heat resistant temperature is about 100° C. Therefore, when forming a multi-layered film functioning as an infrared ray cut filter on the surface of the optical lens  33 , the optical lens  33  is required to be cooled preferably to 90° C. or lower. In this embodiment, as described above, the optical lens  33  is cooled by flowing the antifreezing fluid controlled to have a temperature about −5° C. to the inside of the substrate holder  6   b . As shown in  FIG. 3B , an infrared ray cut filter  34  is formed on the surface of the optical lens  33 . This infrared ray cut filler  34  is comprised of a longer wavelength cut filter  34   b  and a shorter wavelength cut filter  34   a . The longer wavelength cut filter  34   b  and the shorter wavelength cut filter  34   a  are each structured in such a manner that thin films with different light refractive indices are alternately stacked in 20 layers. That is, this optical lens  33  is provided with the infrared ray cut filter  34  of stacked 40 layers. Since the infrared ray cut filter  34  has a stacked structure having 40 layers, it functions to block transmission of infrared ray in a predetermined wavelength range. As described in the first embodiment, the optical characteristic of the infrared ray cut filter changes significantly-depending on the number of layers to be stacked. For example, as described in  FIG. 7 , when the infrared ray cut filter is comprised of about 16 layers, sufficient optical characteristic of the infrared ray cut filter is not obtained, and at least 30 layers or more are required to be stacked. The optical lens  33  of the embodiment is provided with the infrared ray cut filter of 40 layers, and therefore functions sufficiently as infrared ray cut filter.  
      The optical lens  33  of the embodiment is made of acrylic polymer resin. On the surface of the optical lens  33 , the infrared ray cut filter of 40 layers is formed. So, the present invention is able to provide an optical lens with the infrared ray cut filter with light weight and excellent optical characteristic. More specifically, the optical lens with the infrared ray cut filter is suitably used in optical systems such as portable video cameras using a CCD element. Typically, the CCD element has the peak of light receiving sensitivity in a infrared ray region. So, by using the optical lens with the infrared ray cut filter, a video image excellent in color balance can be provided. In the conventional optical lens with the infrared ray cut filter, since the infrared ray cut filter is formed on the surface of a glass lens, reduction of weight of portable video camera or the like is impeded by its weight. In contrast, in the optical lens with the infrared ray cut filter of present invention, since the lightweight resin lens is used, the portable video camera or the like can be further reduced in weight. In the embodiment, further, the substrate  21   b  is mounted on the substrate holder  6   b  with the heat conductive adapter  35  interposed between them to enhance the heat conduction of the substrate  21   b  and the substrate holder  6   b . By using the heat conductive adapter  35 , heat conductivity of the substrate  21   b  and the substrate holder  6   b  is improved. As a result, the temperature of the substrate  21   b  can be controlled easily and efficiently. In the heat conductive adapter  35 , a contact area of the heat conductive adapter  35  and the substrate  21   b  per predetermined area decreases as it is closer to the end portion of the substrate  21   b . Because of the shape of the heat conductive adapter  35 , the temperature is controlled efficiently at the central part of the substrate  21   b , and moderately at the end portion of the substrate  21   b . The substrate  21   b  is slow in temperature change at the central part and fast in temperature change at the end portion because of the influence of its cross-sectional shape. Accordingly, when cooling the substrate  21   b , it is possible to make a uniform in-plane temperature distribution in the transition state of temperature change of the substrate  21   b.    
      The present invention is configured as mentioned above, and provides the vacuum film deposition method and system capable of forming a multi-layered film including a number of layers on the deposition surface of the resin substrate or the substrate having at least the resin layer in the surface layer, and an optical filter manufactured by using the same.  
      In the foregoing description, the ion plating system has been illustrated as the vacuum film deposition system, but it is not limited to the ion plating system in particular. The present invention can be generally carried out in and applied to vacuum film deposition systems for forming a multi-layered film on the resin substrate or on the substrate having the resin layer by mounting the substrate on the substrate holder.  
      Numerous modifications and alternative embodiments of the present invention will be apparent to those skilled in the art in view of the foregoing description. Accordingly, the description is to be construed as illustrative only, and is provided for the purpose of teaching those skilled in the art the best mode of carrying out the invention. The details of the structure and/or function may be varied substantially without departing from the sprit of the invention.  
     INDUSTRIAL APPLICABILITY  
      A vacuum film deposition method, a system and an optical filter manufactured by using the same of present invention are useful as the vacuum film deposition method, the system and the optical filter capable of forming a multi-layered film a deposition surface of a resin substrate or a substrate having at least a resin layer in a surface layer.