Patent Publication Number: US-11024551-B1

Title: Metal replacement vertical interconnections for buried capacitance

Description:
BACKGROUND 
     The present invention relates generally to semiconductor devices, and more specifically, to metal replacement vertical interconnections for high-density buried capacitance. 
     Complementary metal-oxide-semiconductor (CMOS) technology is commonly used for fabricating field effect transistors (FETs) as part of advanced integrated circuits (IC), such as CPUs, memory, storage devices, and the like. At the core of FETs, a channel region is formed in an n-doped or p-doped semiconductor substrate on which a gate structure is formed. Depending whether the on-state current is carried by electrons or holes, the FET comes as an n-FET device or a p-FET device. The overall fabrication process can include forming a gate structure over a channel region connecting source-drain regions within the substrate on opposite sides of the gate, usually with some vertical overlap between the gate and the source-drain region. The dimensions of semiconductor FETs have been steadily shrinking, as scaling to smaller dimensions leads to continuing device performance improvements. An on-chip decoupling capacitor (DECAP) is desired in some applications. However, on-chip capacitors consume a significant chip area. Thus, with increased device scaling, new capacitor arrangements are being examined. 
     SUMMARY 
     In accordance with an embodiment, a method is provided for forming a multi-level of interconnects underneath a complementary metal oxide semiconductor (CMOS) device. The method includes forming a stack including alternating layers of first and second semiconductor materials, patterning a via in the stack to define a first stack portion and a second stack portion, depositing a first block material within one side of the via such that the first block material directly contacts all of the alternating layers of the first and second semiconductor materials of the first stack portion, depositing a second block material within another side of the via such that the second block material directly contacts one layer of the second semiconductor material of the second stack portion, removing exposed second semiconductor material layers from the second stack portion to form openings, filling the openings with a first conductive material, and performing vertical metallization between the first and second block materials. 
     In accordance with another embodiment, a method is provided for forming a multi-level of interconnects underneath a complementary metal oxide semiconductor (CMOS) device. The method includes forming a stack including alternating layers of a semiconductor material and a conductive material, patterning a via in the stack to define a first stack portion and a second stack portion, depositing a first block material within one side of the via such that the first block material directly contacts all of the alternating layers of the semiconductor material and the conductive material of the first stack portion, depositing a second block material within another side of the via such that the second block material directly contacts one layer of the conductive material of the second stack portion, and performing vertical metallization between the first and second block materials. 
     In accordance with yet another embodiment, a method is provided for forming a multi-level of interconnects underneath a complementary metal oxide semiconductor (CMOS) device. The method includes forming a stack including alternating layers of a semiconductor material and a first conductive material, patterning vias in the stack to define multiple stacks, depositing a first block material within each of the vias, forming a series of first block materials within a first via, forming a series of second block materials within a second via, the first and second vias being on opposed ends of a stack of the multiple stacks, and performing vertical metallization between the first block material and the series of first block materials in the first via, and between the first block material and the series of second block materials in the second via. 
     In accordance with an embodiment, a semiconductor device for forming a multi-level of interconnects underneath a complementary metal oxide semiconductor (CMOS) device is provided. The semiconductor device includes a first stack portion including alternating layers of first and second semiconductor materials, a second stack portion including a SiGe layer disposed between two conductive layers, the first and second stack portions disposed on a substrate, a first block material directly contacting a sidewall of the first stack portion, a second block material directly contacting the SiGe layer of the second stack portion, the second block being smaller than the first block, and a conductive material disposed between the first and second stack portions to define a single capacitor in the second stack portion. 
     In accordance with another embodiment, a semiconductor device for forming a multi-level of interconnects underneath a complementary metal oxide semiconductor (CMOS) device is provided. The semiconductor device includes a first stack portion including alternating layers of a semiconductor material and a first conductive material, a second stack portion including alternating layers of the semiconductor material and the first conductive material, the first and second stack portions disposed on a substrate, a first block material directly contacting a sidewall of the first stack portion, a second block material directly contacting a middle or central conductive layer of the second stack portion, the second block being smaller than the first block, and a second conductive material disposed between the first and second stack portions to define a dual capacitor in the second stack portion. 
     In accordance with yet another embodiment, a semiconductor device for forming a multi-level of interconnects underneath a complementary metal oxide semiconductor (CMOS) device is provided. The semiconductor device includes a stack including alternating layers of a semiconductor material and a first conductive material, a first block material formed on opposed ends of the stack, the first block material extending an entire length of the stack, a series of first block materials disposed adjacent the first block material on one side of the stack, a series of second block materials disposed adjacent the second block material on the other side of the stack, and a second conductive material disposed between the first block material and the series of first block materials on one side of the stack, and between the first block material and the series of second block materials on the other side of the stack. 
     It should be noted that the exemplary embodiments are described with reference to different subject-matters. In particular, some embodiments are described with reference to method type claims whereas other embodiments have been described with reference to apparatus type claims. However, a person skilled in the art will gather from the above and the following description that, unless otherwise notified, in addition to any combination of features belonging to one type of subject-matter, also any combination between features relating to different subject-matters, in particular, between features of the method type claims, and features of the apparatus type claims, is considered as to be described within this document. 
     These and other features and advantages will become apparent from the following detailed description of illustrative embodiments thereof, which is to be read in connection with the accompanying drawings. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The invention will provide details in the following description of preferred embodiments with reference to the following figures wherein: 
         FIG. 1  is a replacement metal plate process flow for forming a vertical interconnect to a buried capacitor (referred to as a 2-electrode decoupling capacitor), in accordance with an embodiment of the present invention; 
         FIG. 2  is a blocked metal plate process flow for forming a vertical interconnect to a buried capacitor (referred to as a 3-electrode decoupling capacitor), in accordance with an embodiment of the present invention; 
         FIG. 3  is a cross-sectional view of a semiconductor structure where a 15-plate electrode stack is patterned to define vias, block materials are deposited within the vias, and an organic planarization layer (OPL) material is selectively deposited, in accordance with an embodiment of the present invention; 
         FIG. 4  is a cross-sectional view of the semiconductor structure of  FIG. 3  where a second block material is selectively deposited within adjacent electrode layers within one via, in accordance with an embodiment of the present invention; and 
         FIG. 5  is a cross-sectional view of the semiconductor structure of  FIG. 4  where a second block material is selectively deposited within adjacent electrode layers within the other via, and the vias are metallized, in accordance with an embodiment of the present invention. 
     
    
    
     Throughout the drawings, same or similar reference numerals represent the same or similar elements. 
     DETAILED DESCRIPTION 
     Embodiments in accordance with the present invention provide methods and devices for a buried multi-level capacitor under the device level with vertical interconnections to different levels of the capacitor. Decoupling capacitors are necessary for noise reduction on supply voltages in high speed circuits, yet consume chip area. Existing capacitor structures fall into two main categories, that is, front end-of-the-line (FEOL) caps and back end-of-the-line (BEOL) caps. FEOL caps are limited by fin and gate patterning, as well as ground rules to achieve certain capacitance per unit area (density). FEOL caps further tend to utilize significant chip area. BEOL caps are limited in that BEOL stacks waste far BEOL routing resources (possible area penalty) and are naturally large in size due to placement in the stack, thus causing risk of breakdown in the field, as well as chip failure. 
     Embodiments in accordance with the present invention alleviate such complications in existing decoupling capacitors by providing methods and devices that do not waste any FEOL device area or routing resources by employing self-contained devices with connections through existing bottom contact rails. The pre-patterning of capacitor devices allows for a controllable plate area to limit risk of breakdown in the field. Further, connecting locally to devices allows for better proximity to switching field effect transistors (FETs) due to a potential reduction in series resistance. Moreover, a selectable number of plates (layers) enables scalable performance benefit versus conventional devices. 
     Examples of semiconductor materials that can be used in forming such structures include silicon (Si), germanium (Ge), silicon germanium alloys (SiGe), silicon carbide (SiC), silicon germanium carbide (SiGeC), III-V compound semiconductors and/or II-VI compound semiconductors. III-V compound semiconductors are materials that include at least one element from Group III of the Periodic Table of Elements and at least one element from Group V of the Periodic Table of Elements. II-VI compound semiconductors are materials that include at least one element from Group II of the Periodic Table of Elements and at least one element from Group VI of the Periodic Table of Elements. 
     It is to be understood that the present invention will be described in terms of a given illustrative architecture; however, other architectures, structures, substrate materials and process features and steps/blocks can be varied within the scope of the present invention. It should be noted that certain features cannot be shown in all figures for the sake of clarity. This is not intended to be interpreted as a limitation of any particular embodiment, or illustration, or scope of the claims. 
       FIG. 1  is a replacement metal plate process flow for forming a vertical interconnect to a buried capacitor (referred to as a 2-electrode decoupling capacitor), in accordance with an embodiment of the present invention. 
     Structure  5  includes a semiconductor substrate  10 . A nanosheet stack  20  can be formed over the substrate  10 . The nanosheet stack  20  can include, e.g., alternating layers of a first semiconductor material  22  and a second semiconductor material  24 . The first semiconductor material  22  can be, e.g., silicon (Si) and the second semiconductor material  24  can be, e.g., silicon germanium (SiGe). 
     The substrate  10  can be crystalline, semi-crystalline, microcrystalline, or amorphous. The substrate  10  can be essentially (e.g., except for contaminants) a single element (e.g., silicon), primarily (e.g., with doping) of a single element, for example, silicon (Si) or germanium (Ge), or the substrate  10  can include a compound, for example, GaAs, SiC, or SiGe. The substrate  10  can also have multiple material layers. In some embodiments, the substrate  10  includes a semiconductor material including, but not necessarily limited to, silicon (Si), silicon germanium (SiGe), silicon carbide (SiC), Si:C (carbon doped silicon), silicon germanium carbide (SiGeC), carbon doped silicon germanium (SiGe:C), III-V (e.g., GaAs, AlGaAs, InAs, InP, etc.), II-V compound semiconductor (e.g., ZnSe, ZnTe, ZnCdSe, etc.) or other like semiconductor. In addition, multiple layers of the semiconductor materials can be used as the semiconductor material of the substrate  10 . In some embodiments, the substrate  10  includes both semiconductor materials and dielectric materials. The semiconductor substrate  10  can also include an organic semiconductor or a layered semiconductor such as, for example, Si/SiGe, a silicon-on-insulator or a SiGe-on-insulator. A portion or entire semiconductor substrate  10  can be amorphous, polycrystalline, or monocrystalline. In addition to the aforementioned types of semiconductor substrates, the semiconductor substrate  10  employed in the present invention can also include a hybrid oriented (HOT) semiconductor substrate in which the HOT substrate has surface regions of different crystallographic orientation. 
     Examples of semiconductor materials that can be used in forming such nanosheet structures  20  include at least silicon (Si), germanium (Ge), silicon germanium alloys (SiGe), silicon carbide (SiC), silicon germanium carbide (SiGeC), III-V compound semiconductors and/or II-VI compound semiconductors. One skilled in the art can contemplate a number of different semiconductor materials for forming the nanosheet structures  20 . 
     In structure  30 , the stack  20  is patterned such that two stacks  20 ′ are created. A recess  32  separates the two stacks  20 ′. A top surface  11  of the substrate  10  is also exposed. 
     In structure  35 , an organic planarization layer (OPL)  36  is deposited over one of the stacks  20 ′. The OPL  36  directly contacts a top surface and a sidewall of one stack  20 ′. A gap  38  remains between the OPL  36  and the other stack  20 ′ that is not covered by any OPL. 
     In structure  40 , a first block material  42  is deposited in the gap  38 . The first block material  42  is etched back such that the first block material  42  extends to a top surface of the stacks  20 ′. The first block material  42  will prevent subsequent removal of SiGe layers  24  from the right-hand stack  20 ′ that is directly contacts. The first block material  42  directly contacts the sidewalls of all of the SiGe layers  24  of the right-hand stack  20 ′. 
     In structure  50 , the OPL  36  is mostly removed such that an OPL section  36 ′ remains between the left-hand stack  20 ′ and the first block material  42 . The recess of the OPL  36  results in exposure of the upper semiconductor layers  22 / 24  of the right-hand stack  20 ′. 
     In structure  55 , another OPL  57  is deposited. The OPL  57  directly contacts the top surface of the right-hand stack  20 ′ and the sidewall of the first block material  42 . 
     In structure  60 , a second block material  62  is deposited. The second block material  62  is formed between the left-hand stack  20 ′ and the OPL  57 . The second block material  62  is smaller than the first block material  42 . The second block material  62  has a different shape than the first block material  42 . The second block material  62  directly contacts the sidewall of one SiGe layer  24  of the left-hand stack  20 ′. For example, the second block material  62  directly contacts a sidewall of a middle or central SiGe layer  24 . 
     In structure  65 , the OPL  57  is completely removed such that a gap region  67  is formed directly between the stacks  20 ′. The removal of the OPL  57  results in exposure of the first block material  42  and the second block material  62 . The first block material  42  continues to directly contact the sidewalls of all the SiGe layers  24  of the right-hand stack  20 ′ and the second block material  62  continues to directly contact a sidewall of only a single middle or central SiGe layer  24  of the left-hand stack  20 ′. Thus, sidewalls of two SiGe layers  24  are exposed in the left-hand side stack  20 ′. 
     In structure  70 , the exposed SiGe layers  24  are removed and metal layers  72  fill in such gaps. Metals layers  72  are thus formed adjacent opposed ends of the SiGe layer  24  that was blocked by the second block material  62 . Thus, the exposed SiGe layers  24  are replaced with a conductive material  72 . 
     In structure  75 , a conductive material  76  is deposited between the stacks  20 ′ such that the conductive material  76  covers the exposed portions of the first and second block materials  42 ,  62 . The conductive material  76  directly contacts the sidewalls of the metal layers  72 . The conductive material  76  and the metal layers  72  can be formed from the same material. This vertical metallization results in a single capacitor with one space. The one space can be defined directly between the metal layers  72 . The structure  75  can be referred to as a 2-plate metal-insulator-metal (MIM) capacitor or a two electrode decoupling capacitor. Thus, this a buried capacitor under the device level with vertical connections to different levels of the capacitor. 
     The OPL  36  can be formed at a predetermined thickness to provide reflectivity and topography control during etching of the layers below. The OPL  36  can include an organic material, such as a polymer. Exemplary organic planarization materials include, but are not limited to, near-frictionless carbon (NFC) material, diamond-like carbon, polyarylene ether, and polyimide. The thickness of the OPL  36  can be in a range from about 10 nm to about 300 nm. In one example, the thickness of the OPL  36  is about 100 nm-150 nm. 
     Block materials  42 ,  62  can be deposited by conventional deposition methods such as atomic layer deposition (ALD), chemical vapor deposition (CVD), low pressure CVD (LPCVD), molecular layer deposition (MLD), PECVD or any other known or later developed methods. Block materials  42 ,  62  can include any barrier material such as a nitride, high temperature oxide (HTO), hafnium oxide, hafnium silicon oxide or other materials or combinations of materials that have a high selectivity on oxide. Block materials  42 ,  62  can have a thickness in a range from about 30 angstroms to about 170 angstroms depending upon if only nitride or nitride plus HTO are used, but can be thinner or thicker. Block materials  42 ,  62  protects SiGe layers  24  where metallization does not occur. 
     The conductive materials  72 ,  76  can be any conductive materials known in the art, such as, for example, copper (Cu), aluminum (Al), tungsten (W), ruthenium (Ru) or cobalt (Co). The conductive materials  72 ,  76  can be fabricated using any technique known in the art, such as, for example, a single or dual damascene technique. In an embodiment, the conductive materials  72 ,  76  can be copper (Cu) and can include a metal liner, where the metal liner can be metals, such as, for example, tantalum nitride and tantalum (TaN/Ta), titanium, titanium nitride, cobalt, ruthenium, and manganese. 
     The etching can include a dry etching process such as, for example, reactive ion etching, plasma etching, ion etching or laser ablation. The etching can further include a wet chemical etching process in which one or more chemical etchants are used to remove portions of the OPL  36 ,  57 . 
     In general, regarding the etching of any materials, such materials can be removed by a dry etching process, for example, ashing. Ashing is performed using a suitable reaction gas, for example, O 2 , N 2 , H 2 /N 2 , O 3 , CF 4 , or any combination thereof. The dry etching process can be combined with a wet etching process. The wet etching process can be performed, for example, with a wet etchant, such as sulfuric acid and hydrogen peroxide. In various example embodiments, the OPL  36 ,  57  is etched. The etch can, for example, include a wet etch such as a phosphoric acid (H 3 PO 4 ) (wet chemistry) etch or a diluted hydrogen fluoride (HF) etch. 
       FIG. 2  is a blocked metal plate process flow for forming a vertical interconnect to a buried capacitor (referred to as a 3-electrode decoupling capacitor), in accordance with an embodiment of the present invention. 
     Structure  100  includes a semiconductor substrate  10 . A stack  120  can be formed over the substrate  10 . The stack  120  can include, e.g., alternating layers of a first semiconductor material  122  and a first conductive material  124 . The first semiconductor material  122  can be, e.g., silicon (Si). 
     In structure  130 , the stack  120  is patterned such that two stacks  120 ′ are created. A recess  132  separates the two stacks  120 ′. A top surface  11  of the substrate  10  is also exposed. 
     In structure  135 , an organic planarization layer (OPL)  136  is deposited over one of the stacks  120 ′. The OPL  136  directly contacts a top surface and a sidewall of one stack  120 ′. A gap  138  remains between the OPL  136  and the other stack  120 ′ that is not covered by any OPL. 
     In structure  140 , a first block material  142  is deposited in the gap  138 . The first block material  142  is etched back such that the first block material  142  extends to a top surface of the stacks  120 ′. The first block material  142  will prevent subsequent removal of semiconductor layers  122  from the right-hand stack  120 ′ that is directly contacts. The first block material  142  directly contacts the sidewalls of all of the semiconductor layers  122  of the right-hand stack  120 ′. 
     In structure  150 , the OPL  136  is mostly removed such that an OPL section  136 ′ remains between the left-hand stack  120 ′ and the first block material  142 . The recess of the OPL  136  results in exposure of the upper semiconductor layers  122  and upper conductive layers  124  of the right-hand stack  120 ′. 
     In structure  155 , another OPL  157  is deposited. The OPL  157  directly contacts the top surface of the right-hand stack  120 ′ and the sidewall of the first block material  142 . 
     In structure  160 , a second block material  162  is deposited. The second block material  162  is formed between the left-hand stack  120 ′ and the OPL  157 . The second block material  162  is smaller than the first block material  142 . The second block material  162  has a different shape than the first block material  142 . The second block material  162  directly contacts the sidewall of one conductive layer  124  of the left-hand stack  120 ′. For example, the second block material  162  directly contacts a sidewall of a middle or central conductive layer  124 . 
     In structure  165 , the OPL  157  is completely removed such that a gap region  167  is formed directly between the stacks  120 ′. The removal of the OPL  157  results in exposure of the first block material  142  and the second block material  162 . The first block material  142  continues to directly contact the sidewalls of all the conductive layers  124  of the right-hand stack  120 ′ and the second block material  162  continues to directly contact a sidewall of only a single middle or central conductive layer  124  of the left-hand stack  120 ′. Thus, sidewalls of two conductive layers  124  are exposed in the left-hand side stack  120 ′. 
     In structure  170 , a conductive material  176  is deposited between the stacks  120 ′ such that the conductive material  176  covers the exposed portions of the first and second block materials  142 ,  162 . The conductive material  176  directly contacts the sidewalls of the exposed conductive layers  124 . The conductive material  176  and the exposed conductive layers  124  can be formed from the same material. This vertical metallization results in a dual capacitor with two spaces. The spaces can be defined directly between the conductive layers  124 . The structure  170  can be referred to as a 3-plate metal-insulator-metal (MIM) capacitor or a three electrode decoupling capacitor. Thus, this a buried capacitor under the device level with vertical connections to different levels of the capacitor. 
       FIG. 3  is a cross-sectional view of a semiconductor structure where a 15-plate electrode stack is patterned to define vias, block materials are deposited within the vias, and an organic planarization layer (OPL) material is selectively deposited, in accordance with an embodiment of the present invention. 
     Structure  205  includes a semiconductor substrate  10 . A stack  220  can be formed over the substrate  10 . The stack  220  can include, e.g., alternating layers of a semiconductor material  222  and a first conductive material  224 . The first semiconductor material  222  can be, e.g., silicon (Si). The stack  220  is etched to form vias extending to a top surface  11  of the substrate  10 . The stack includes 15 layers of the first conductive material  224 . 
     In structure  230 , a block material  232  is formed within each opening  231  and adjacent portions of stack  220 . The block material  232  directly contacts all of the semiconductor layers  222  and all of the conductive layers  224 . 
     In structure  235 , an organic planarization layer (OPL)  237  is deposited over portions of the stacks  220 . The OPL  237  directly contacts a top surface of all the stacks  220  and sidewalls of some of the stacks  220 . A gap  239  remains between the OPL  237  and one section of stack  220 . A second block material  234  is deposited within the gap  239  such that it sits on a portion of OPL. 
       FIG. 4  is a cross-sectional view of the semiconductor structure of  FIG. 3  where a second block material is selectively deposited within adjacent electrode layers within one via, in accordance with an embodiment of the present invention. 
     In structure  240 , an OPL section  242  is deposited over the second block material  234 . Then another block material  234  is deposited over the OPL section  242 . This sequence of alternately depositing second block material  234  and OPL sections  242  is repeated until a second block material  234  reaches a topmost region of the stack  220 . 
     In structure  245 , the second block material  234  has reached the topmost region of the stack  220 . The second block material directly contacts sidewalls of alternate conductive layers  224 . A gap  247  remains between the first block material  232  and the series of second block materials  234 . The OPL  237  is also completely removed such that the first block materials  232  are fully exposed within the openings  247 . 
     In structure  250 , another OPL  252  is deposited such that a gap  253  is formed on the left-hand side of the stack  220 . A third block material  236  is deposited within the gap  253  such that it sits on a portion of OPL. 
       FIG. 5  is a cross-sectional view of the semiconductor structure of  FIG. 4  where a second block material is selectively deposited within adjacent electrode layers within the other via, and the vias are metallized, in accordance with an embodiment of the present invention. 
     In structure  260 , an OPL section  262  is deposited over the third block material  236 . Then another third block material  236  is deposited over OPL section  262 . This sequence of alternately depositing third block material  236  and OPL sections  262  is repeated until a third block material  236  reaches a topmost region of the stack  220 . 
     In structure  265 , the third block material  236  has reached the topmost region of the stack  220 . The third block material  236  directly contacts sidewalls of alternate conductive layers  224 . A gap  267  remains between the first block material  232  and the series of third block materials  236 . Thus, the series of second block materials  234  directly contacts one side of each of the alternate conductive layers  224  and the series of third block materials  236  directly contacts the other side of each of the alternate conductive layers  224 . Therefore, the alternate conductive layers  224  are blocked on opposed ends thereof by the second and third block materials  234 ,  236 . Moreover, one gap  267  includes a first block material  232  and the series of second block materials  234  and the other gap  267  includes a first block material  232  and the series of third block materials  236 . The OPL  252  is further removed. 
     In structure  270 , a conductive material  272  is deposited within the gaps  247 ,  267 . The conductive material  272  directly contacts the entire exposed sidewall of the first block material  232  and directly contacts all of the second and third block materials  234 ,  236 . 
     The series of first block materials  234  is horizontally offset from the series of second block materials  236 . In other words, the series of first block materials  234  directly contacts sidewalls of conductive layers 2, 4, 6, 8, 10, 12, 14, whereas the series of second block materials  236  directly contacts sidewalls of conductive layers 1, 3, 5, 7, 9, 11, 13, and 15. As a result, alternating layers are blocked in one via and a different set of alternating layers are blocked in another via. 
     The conductive material  272  and the conductive layers  224  can be formed from the same material. This vertical metallization results in a multi-capacitor. The structure  270  can be referred to as a 15-plate metal-insulator-metal (MIM) capacitor or a fifteen electrode decoupling capacitor. Thus, this a buried capacitor under the device level with vertical connections to different levels of the capacitor. The 15-plate MIM capacitor can have at least a 10% performance benefit over conventional MIM capacitors. 
     The conductive materials  224 ,  272  can be any conductive materials known in the art, such as, for example, copper (Cu), aluminum (Al), tungsten (W), ruthenium (Ru) or cobalt (Co). The conductive materials  224 ,  272  can be fabricated using any technique known in the art, such as, for example, a single or dual damascene technique. In an embodiment, the conductive materials  224 ,  272  can be copper (Cu) and can include a metal liner, where the metal liner can be metals, such as, for example, tantalum nitride and tantalum (TaN/Ta), titanium, titanium nitride, cobalt, ruthenium, and manganese. 
     In summary, the device structure of the exemplary embodiments of the present invention includes a scalable multi-level interconnect through a vertical via (pillar) below complementary metal oxide semiconductor (CMOS) device levels. The structure includes multiple levels of patterned connections between metal layers. The method of the exemplary embodiments of the present invention includes forming a multi-level of interconnects underneath the CMOS device level where the metal plates are formed directly or through replacement metallization. The method further connects both sequential and non-sequential order multi-level buried metal plates underneath a CMOS device level. 
     Regarding  FIGS. 1-5 , deposition is any process that grows, coats, or otherwise transfers a material onto the wafer. Available technologies include, but are not limited to, thermal oxidation, physical vapor deposition (PVD), chemical vapor deposition (CVD), electrochemical deposition (ECD), molecular beam epitaxy (MBE) and more recently, atomic layer deposition (ALD) among others. As used herein, “depositing” can include any now known or later developed techniques appropriate for the material to be deposited including but not limited to, for example: chemical vapor deposition (CVD), low-pressure CVD (LPCVD), plasma-enhanced CVD (PECVD), semi-atmosphere CVD (SACVD) and high density plasma CVD (HDPCVD), rapid thermal CVD (RTCVD), ultra-high vacuum CVD (UHVCVD), limited reaction processing CVD (LRPCVD), metal-organic CVD (MOCVD), sputtering deposition, ion beam deposition, electron beam deposition, laser assisted deposition, thermal oxidation, thermal nitridation, spin-on methods, physical vapor deposition (PVD), atomic layer deposition (ALD), chemical oxidation, molecular beam epitaxy (MBE), plating, evaporation. 
     The term “processing” as used herein includes deposition of material or photoresist, patterning, exposure, development, etching, cleaning, stripping, implanting, doping, stressing, layering, and/or removal of the material or photoresist as needed in forming a described structure. 
     It is to be understood that the present invention will be described in terms of a given illustrative architecture; however, other architectures, structures, substrate materials and process features and steps/blocks can be varied within the scope of the present invention. 
     It will also be understood that when an element such as a layer, region or substrate is referred to as being “on” or “over” another element, it can be directly on the other element or intervening elements can also be present. In contrast, when an element is referred to as being “directly on” or “directly over” another element, there are no intervening elements present. It will also be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements can be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present. 
     The present embodiments can include a design for an integrated circuit chip, which can be created in a graphical computer programming language, and stored in a computer storage medium (such as a disk, tape, physical hard drive, or virtual hard drive such as in a storage access network). If the designer does not fabricate chips or the photolithographic masks used to fabricate chips, the designer can transmit the resulting design by physical mechanisms (e.g., by providing a copy of the storage medium storing the design) or electronically (e.g., through the Internet) to such entities, directly or indirectly. The stored design is then converted into the appropriate format (e.g., GDSII) for the fabrication of photolithographic masks, which include multiple copies of the chip design in question that are to be formed on a wafer. The photolithographic masks are utilized to define areas of the wafer (and/or the layers thereon) to be etched or otherwise processed. 
     Methods as described herein can be used in the fabrication of integrated circuit chips. The resulting integrated circuit chips can be distributed by the fabricator in raw wafer form (that is, as a single wafer that has multiple unpackaged chips), as a bare die, or in a packaged form. In the latter case, the chip is mounted in a single chip package (such as a plastic carrier, with leads that are affixed to a motherboard or other higher level carrier) or in a multichip package (such as a ceramic carrier that has either or both surface interconnections or buried interconnections). In any case, the chip is then integrated with other chips, discrete circuit elements, and/or other signal processing devices as part of either (a) an intermediate product, such as a motherboard, or (b) an end product. The end product can be any product that includes integrated circuit chips, ranging from toys and other low-end applications to advanced computer products having a display, a keyboard or other input device, and a central processor. 
     It should also be understood that material compounds will be described in terms of listed elements, e.g., SiGe. These compounds include different proportions of the elements within the compound, e.g., SiGe includes Si x Ge 1-x  where x is less than or equal to 1, etc. In addition, other elements can be included in the compound and still function in accordance with the present embodiments. The compounds with additional elements will be referred to herein as alloys. Reference in the specification to “one embodiment” or “an embodiment” of the present invention, as well as other variations thereof, means that a particular feature, structure, characteristic, and so forth described in connection with the embodiment is included in at least one embodiment of the present invention. Thus, the appearances of the phrase “in one embodiment” or “in an embodiment”, as well any other variations, appearing in various places throughout the specification are not necessarily all referring to the same embodiment. 
     It is to be appreciated that the use of any of the following “/”, “and/or”, and “at least one of”, for example, in the cases of “A/B”, “A and/or B” and “at least one of A and B”, is intended to encompass the selection of the first listed option (A) only, or the selection of the second listed option (B) only, or the selection of both options (A and B). As a further example, in the cases of “A, B, and/or C” and “at least one of A, B, and C”, such phrasing is intended to encompass the selection of the first listed option (A) only, or the selection of the second listed option (B) only, or the selection of the third listed option (C) only, or the selection of the first and the second listed options (A and B) only, or the selection of the first and third listed options (A and C) only, or the selection of the second and third listed options (B and C) only, or the selection of all three options (A and B and C). This can be extended, as readily apparent by one of ordinary skill in this and related arts, for as many items listed. 
     The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of example embodiments. As used herein, the singular forms “a,” “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises,” “comprising,” “includes” and/or “including,” when used herein, specify the presence of stated features, integers, steps, operations, elements and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components and/or groups thereof. 
     Spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper,” and the like, can be used herein for ease of description to describe one element&#39;s or feature&#39;s relationship to another element(s) or feature(s) as illustrated in the FIGS. It will be understood that the spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the FIGS. For example, if the device in the FIGS. is turned over, elements described as “below” or “beneath” other elements or features would then be oriented “above” the other elements or features. Thus, the term “below” can encompass both an orientation of above and below. The device can be otherwise oriented (rotated 90 degrees or at other orientations), and the spatially relative descriptors used herein can be interpreted accordingly. In addition, it will also be understood that when a layer is referred to as being “between” two layers, it can be the only layer between the two layers, or one or more intervening layers can also be present. 
     It will be understood that, although the terms first, second, etc. can be used herein to describe various elements, these elements should not be limited by these terms. These terms are only used to distinguish one element from another element. Thus, a first element discussed below could be termed a second element without departing from the scope of the present concept. 
     Having described preferred embodiments of metal replacement vertical interconnections for high-density buried capacitance (which are intended to be illustrative and not limiting), it is noted that modifications and variations can be made by persons skilled in the art in light of the above teachings. It is therefore to be understood that changes may be made in the particular embodiments described which are within the scope of the invention as outlined by the appended claims. Having thus described aspects of the invention, with the details and particularity required by the patent laws, what is claimed and desired protected by Letters Patent is set forth in the appended claims.