Patent Publication Number: US-11398358-B2

Title: Electrolytic capacitor and manufacturing method therefor

Description:
BACKGROUND 
     1. Technical Field 
     The present disclosure relates to an electrolytic capacitor used in various electronic apparatuses. 
     2. Background Art 
     With digitalization of electronic apparatuses, there is a demand for capacitors having a small size, a large capacitance, and a small equivalent series resistance (hereinafter, abbreviated as “ESR”) in a high frequency region to be used at a power supply output side of circuits such as, for example, a smoothing circuit and a control circuit. As such capacitors, electrolytic capacitors using a fluid electrolyte typically such as an electrolyte solution have been used. Furthermore, recently, solid electrolytic capacitors using a solid electrolyte such as manganese dioxide, a TCNQ complex salt, or an electroconductive polymer such as polypyrrole, polythiophene, and polyaniline have been used. 
     The solid electrolytic capacitor is excellent in that it has a particularly low ESR as compared with a liquid-type electrolytic capacitor. However, the solid electrolytic capacitor is poor in repairing a defective part in anodic oxide film as a dielectric body. Therefore, leakage current may increase, and, in the worst case, a short circuit may occur. 
     Meanwhile, particularly, in recent AV apparatuses and automobile electrical equipment, high reliability has been increasingly demanded. Therefore, also in solid electrolytic capacitors, low leakage current and a short-circuit resistance property, in addition to performance such as having a small size, a large capacitance, and a low ESR, are being demanded. In order to meet such demands, a so-called hybrid-type electrolytic capacitor using an electrolyte solution, as material for an electrolyte, that is excellent in repairing a defective part in an anodic oxide film that is a dielectric body in addition to a solid electrolyte such as an electroconductive polymer has been proposed. 
       FIG. 4  is a sectional view showing a configuration of a hybrid-type electrolytic capacitor (having wound-type capacitor element) as an example of conventional electrolytic capacitor.  FIG. 5  is a development perspective view of a capacitor element of the hybrid-type electrolytic capacitor. As shown in  FIG. 4 , the hybrid-type electrolytic capacitor includes capacitor element  2  as a function element, a pair of lead wires  1 A and  1 B, and outer package  5 . One end portion of each of lead wires  1 A and  1 B is connected to capacitor element  2 . Outer package  5  encloses capacitor element  2  and an electrolyte solution (not shown) in such a manner that the other end portion of each of lead wires  1 A and  1 B is led to the outside. 
     Outer package  5  includes bottomed cylindrical case  3  and seal member  4 . Case  3  accommodates capacitor element  2  impregnated with the electrolyte solution. Seal member  4  is provided with through holes  4 A and  4 B through which lead wires  1 A and  1 B are inserted, respectively. Seal member  4  is compressed by drawing processing part  3 A provided on the outer peripheral surface of case  3  so as to seal an opening of case  3 . Seal member  4  is made of rubber packing. 
     As shown in  FIG. 5 , capacitor element  2  includes anode foil  2 A, cathode foil  2 B, and separator  2 C. Anode foil  2 A is formed by roughing a foil made of a valve metal such as aluminum by etching, and forming an anodic oxide film (not shown) as a dielectric body thereon by anodization. Cathode foil  2 B is formed of a valve metal such as aluminum. Separator  2 C is disposed between anode foil  2 A and cathode foil  2 B. In this state, anode foil  2 A, cathode foil  2 B and separator  2 C are laminated and wound so as to form capacitor element  2 . A solid electrolyte layer (not shown) made of an electroconductive polymer such as polythiophene is formed between anode foil  2 A and cathode foil  2 B. 
     One end portion of lead wire  1 A is connected to anode foil  2 A, and one end portion of lead wire  1 B is connected to cathode foil  2 B. The other end portions thereof are led out from one end surface of capacitor element  2 . 
     The electrolyte solution includes a solvent, a solute, and additives, and it is based on an electrolyte solution that has been used in a conventional liquid-type electrolytic capacitor using only a liquid electrolyte. The liquid-type electrolytic capacitors are roughly classified into electrolytic capacitors having a low withstand voltage in which a rated voltage is not greater than 100 W.V. and having a low ESR, and electrolytic capacitors having a high withstand voltage in which a rated voltage is, for example, 250 W.V., 350 W.V., and 400 W.V. Mainly, the former electrolytic capacitors are used in a smoothing circuit and a control circuit at the power supply output side, and the latter electrolytic capacitors are used in a smoothing circuit at a power supply input side. These are largely different from each other in various properties of an electrolyte solution to be used in each electrolytic capacitor because roles in the circuit and material compositions are different from each other. Therefore, these electrolyte solutions cannot be used compatibly. 
     On the other hand, the hybrid-type electrolytic capacitor is used in a smoothing circuit and a control circuit at the power supply output side because it has an ESR as low as that of a solid-type electrolytic capacitor and has a limitation with respect to a withstand voltage. Therefore, a conventional hybrid-type electrolytic capacitor employs an electrolyte solution having high electric conductivity and an excellent low-temperature characteristic, which is applicable for conventional liquid-type electrolytic capacitors. Specific examples of the electrolyte solution is an electrolyte solution including γ-butyrolactone, ethylene glycol or the like as a main solvent, and amidine phthalate, tetramethylammonium phthalate, ammonium adipate, triethylamine phthalate or the like as a solute. 
     In a conventional hybrid-type electrolytic capacitor configured as mentioned above, an electrolyte solution enters into pores in the solid electrolyte layer of an electroconductive polymer formed in capacitor element  2 , and thus, a contact state between a dielectric oxide film and the electrolyte is improved. Therefore, the capacitance is increased, the ESR is lowered, repairing of a defective part in the dielectric oxide film is promoted by the effect of the electrolyte solution, and thus leakage current is reduced. Such an electrolytic capacitor is disclosed in, for example, Japanese Patent Application Unexamined Publication No. H11-186110 and No. 2008-10657. 
     Electrolytic capacitors used in AV apparatuses and automobile electrical equipment require high reliability over a long period of time. Such electrolytic capacitors are used under a harsh environment at high temperatures, for example, at a maximum working temperature of 85° C. to 150° C. for a long time. Meanwhile, a conventional hybrid-type electrolytic capacitor has a configuration in which an opening of a case accommodating a capacitor element and an electrolyte solution is sealed by sealing material such as rubber and epoxy resin, and therefore lifetime design becomes important. 
     However, a solvent of the electrolyte solution used in a conventional hybrid-type electrolytic capacitor is a volatile organic solvent such as γ-butyrolactone, ethylene glycol, and sulfolane. Therefore, when the electrolytic capacitor is exposed to a high temperature, the solvent gradually penetrates into a gap between the seal member and the case, a gap between the seal member and the lead wires, or the seal member itself, and gradually vaporizes and volatilizes. In general, an electrolytic capacitor is designed to have a guaranteed lifetime such that a range in which stable properties can be maintained with variation of the physical properties of material to be used or manufacturing conditions taken into consideration. However, if the electrolytic capacitor is used for a long time beyond the guaranteed lifetime, a solvent in the electrolyte solution is finally lost. Therefore, a function of self-repairing a defective part in the dielectric oxide film is lost. 
     In a conventional liquid-type electrolytic capacitor using only liquid electrolyte, even if the solvent of the electrolyte solution is lost, since the dielectric oxide film and the cathode foil are insulated from each other by the separator, electrolytic capacitor is only to be in an open mode and not in a short circuit. 
     On the other hand, in the hybrid-type electrolytic capacitor, even if the solvent of the electrolyte solution is lost, an electroconductive solid electrolyte layer remains between the dielectric oxide film and the cathode foil. Therefore, when an effect of the electrolyte solution is lost, an increase in leakage current is caused. As a result, in a worst case, a short circuit occurs. 
     SUMMARY 
     An electrolytic capacitor of an aspect of the present disclosure includes a capacitor element. The capacitor element includes an anode including a dielectric layer thereon and a cathode member including a conductive polymer and in contact with the dielectric layer. The capacitor element is impregnated with a liquid containing at least one of polyalkylene glycol and derivatives of polyalkylene glycol. The liquid further contains an oxidation inhibitor. 
    
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
         FIG. 1  is a sectional view showing a configuration of a hybrid-type electrolytic capacitor (having wound-type capacitor element) of an example of an electrolytic capacitor in accordance with an exemplary embodiment of the present disclosure. 
         FIG. 2  is a developed perspective view of a capacitor element of the hybrid-type electrolytic capacitor shown in  FIG. 1 . 
         FIG. 3  is an enlarged conceptual view of a principal part of the capacitor element shown in  FIG. 2 . 
         FIG. 4  is a sectional view showing a configuration of a hybrid-type electrolytic capacitor (having wound-type capacitor element) of an example of a conventional electrolytic capacitor. 
         FIG. 5  is a developed perspective view of a capacitor element of the hybrid-type electrolytic capacitor shown in  FIG. 4 . 
     
    
    
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS 
     Firstly, a configuration of an electrolytic capacitor in accordance with this exemplary embodiment is described with reference to  FIGS. 1 and 2 .  FIG. 1  is a sectional view showing a configuration of a hybrid-type electrolytic capacitor (having wound-type capacitor element) of an example of an electrolytic capacitor in accordance with an exemplary embodiment of the present disclosure, and  FIG. 2  is a developed perspective view of a capacitor element of the hybrid-type electrolytic capacitor. 
     As shown in  FIG. 1 , the electrolytic capacitor includes capacitor element  12 , first lead wire  11 A and second lead wire  11 B (hereinafter, referred to as “lead wires  11 A and  11 B”), and outer package  15 . As shown in  FIG. 2 , capacitor element  12  includes anode foil  12 A, cathode foil  12 B, and separator  12 C disposed between anode foil  12 A and cathode foil  12 B. Lead wire  11 A is connected to anode foil  12 A, and lead wire  11 B is connected to cathode foil  12 B. That is to say, one end portion of lead wire  11 A is connected to anode foil  12 A, and one end portion of lead wire  11 B is connected to cathode foil  12 B. The other end portions of lead wires  11 A and  11 B are led out from the same end surface of capacitor element  12 . Outer package  15  encloses capacitor element  12  such that the other end portions of lead wires  11 A and  11 B are led to the outside. 
     Outer package  15  includes bottomed cylindrical case  13  and seal member  14 . Case  13  accommodates capacitor element  12  impregnated with an electrolyte solution mentioned below. Seal member  14  is provided with through holes  14 A and  14 B through which lead wires  11 A and  11 B are inserted, respectively. Seal member  14  is disposed at an opening of case  13 , and is compressed to seal (close) the opening of case  13  when the outer peripheral surface of case  13  is subjected to drawing processing by drawing processing part  13 A. 
     Next, a configuration of the capacitor element is described with reference to  FIG. 3 .  FIG. 3  is an enlarged conceptual view of a principal part of the capacitor element shown in  FIG. 2 . Capacitor element  12  includes solid electrolyte layer  122  in addition to the above-mentioned anode foil  12 A, cathode foil  12 B and separator  12 C. Furthermore, capacitor element  12  is impregnated with electrolyte solution  16 . 
     Anode foil  12 A is formed by roughing a foil made of a valve metal such as aluminum by etching, and forming a dielectric anodic oxide film thereon by anodization. That is to say, anode foil  12 A has dielectric layer  121  on the surface thereof. Cathode foil  12 B is formed of a valve metal such as aluminum. Anode foil  12 A and cathode foil  12 B are laminated and wound with separator  12 C interposed therebetween. 
     Furthermore, solid electrolyte layer  122  made of an electroconductive polymer such as polythiophene and derivatives thereof is formed between anode foil  12 A and cathode foil  12 B. That is to say, solid electrolyte layer  122  is in contact with dielectric layer  121  and cathode foil  12 B. Solid electrolyte layer  122  is not dense but porous such that there are pores inside thereof, and electrolyte solution  16  enters into the pores. 
     Note here that capacitor element  12  may be configured by laminating a plurality of anode foils  12 A and cathode foils  12 B via separators  12 C. 
     Seal member  14  can be made by using resin material such as an epoxy resin in addition to rubber material such as EPT and IIR. Separator  12 C can be made by using a nonwoven fabric containing cellulose, kraft, polyethylene terephthalate, polybutylene terephthalate, polyphenylene sulfide, nylon, aromatic polyamide, polyimide, polyamide-imide, polyether imide, rayon, and glass. 
     Electrolyte solution  16  is prepared by dissolving a solute in a solvent. Examples of the solute include an ammonium salt of inorganic acid, an amine salt of inorganic acid, and an alkyl-substituted amidine salt of inorganic acid or quaternized products thereof, as well as an ammonium salt of organic acid, an amine salt of organic acid, and an alkyl-substituted amidine salt of organic acid or quaternized products thereof. Examples of inorganic acid compounds include a boric acid compound, a phosphoric acid compound, and the like. Examples of organic acid compounds include aliphatic carboxylic acid such as adipic acid, and aromatic carboxylic acid such as phthalic acid, benzoic acid, salicylic acid, trimellitic acid, and pyromellitic acid. Examples of ammonium compounds include ammonia, and dihydroxy ammonium; and examples of amine compounds include triethyl amine, methyl diethyl amine, trishydroxymethyl amino methane, and the like. Examples of the alkyl-substituted amidine salt or the quaternized products thereof include a quaternized product of 1,2,3,4-tetramethyl imidazolinium and compounds such as 1-ethyl-2,3-dimethyl imidazolinium and 1-ethyl-3-methyl imidazolium. 
     Electrolyte solution  16  includes at least one low-volatile solvent selected from polyalkylene glycol and a derivative of polyalkylene glycol as solvent material. Polyalkylene glycols are substantially non-volatile (low-volatile). Specific examples include polyethylene glycol, polyethylene glycol glyceryl ether or polyethylene glycol diglyceryl ether or polyethylene glycol sorbitol ether, polypropylene glycol, polypropylene glycol glyceryl ether, polypropylene glycol diglyceryl ether, polypropylene glycol sorbitol ether, polybutylene glycol, copolymers of ethylene glycol and propylene glycol, copolymers of ethylene glycol and butylene glycol, and copolymers of propylene glycol and butylene glycol. These can be used singly or in combination of two or more of them. 
     Furthermore, among polyalkylene glycol or derivatives thereof, in particular, polyethylene glycol or derivatives thereof hardly evaporate in the below-mentioned acceleration test and, in other words, they exhibit extremely great low-volatility, when the mean molecular weight is 300 or more. Meanwhile, when the mean molecular weight is more than 1000, although the low-volatility is maintained, viscosity is increased and an effective capacitance rate is lowered, and it is largely lowered particularly at a low temperature. Therefore, an optimum mean molecular weight is in a range from 300 to 1000, inclusive. 
     Furthermore, since polypropylene glycol or derivative thereof have a large propylene structure as a basic unit, they hardly evaporate in the same acceleration test and exhibit extremely great low-volatility when the mean molecular weight is 200 or more. Meanwhile, since the propylene structure is more hydrophobic than the ethylene structure, the viscosity can be kept low until the mean molecular weight is about 5000. Therefore, the effective capacitance rate of the capacitor at low temperature is excellent. However, when the mean molecular weight is more than 5000, the low volatility is obtained but the viscosity is increased, and thus the effective capacitance rate of the capacitor is lowered and it is largely lowered particularly at a low temperature. Therefore, an optimum mean molecular weight is in a range from 200 to 5000, inclusive. 
     In a single polymerized product (homopolymer) such as polyethylene glycol or polypropylene glycol, the molecular weight can be controlled easily at the time of polymerization. Therefore, molecular weight distribution is stabilized, excellent thermal stability can be exhibited, and the long lifetime can be achieved. Furthermore, in the case of a polymerized product having a molecular weight of 200 or more, the interaction between molecules becomes stronger and thus the thermal stability is more improved. Therefore, such a polymerized product is optimum for capacitors having a long guaranteed lifetime. 
     As mentioned above, an electrolyte solution, which has been used in a conventional hybrid-type electrolytic capacitor used in a smoothing circuit or a control circuit at the power supply output side, includes a volatile organic solvent such as γ-butyrolactone and ethylene glycol as a solvent. Therefore, if a conventional hybrid-type electrolytic capacitor is continued to be used under a high-temperature environment of a maximum working temperature of 85° C. to 150° C. for a long time beyond the guaranteed lifetime, the solvent of electrolyte solution  16  is lost by vaporization and volatilization. As a result, an effect of repairing a dielectric oxide film cannot be exhibited. 
     On the other hand, the electrolytic capacitor in accordance with this exemplary embodiment includes liquid-state polyalkylene glycol as a low-volatile solvent. This liquid-state polyalkylene glycol hardly volatilizes even under a high-temperature environment of a maximum working temperature of 85° C. to 150° C. Consequently, even if it is used under a high temperature as mentioned above for a long time beyond the guaranteed lifetime, electrolyte solution  16  can be allowed to remain in capacitor element  12 . Therefore, the repairing effect of the dielectric oxide film can be maintained. 
     Furthermore, the content of polyalkylene glycol or derivatives thereof as the low-volatile solvent in electrolyte solution  16  is 15 wt. % or more, this low-volatile solvent can cover an entire part of the dielectric oxide film on the surface of anode foil  12 A. Furthermore, this low-volatile solvent can move along separator  12 C and a solid electrolyte existing between the dielectric oxide film and cathode foil  12 B and reach cathode foil  12 B. Consequently, defective parts over the dielectric oxide film can be repaired, and thus an extremely excellent short-circuit resistance property can be exhibited. 
     As the upper limit of the content of polyalkylene glycol or derivatives thereof, all of the solvent excluding a solute and additives may be liquid state polyalkylene glycol or derivatives thereof. However, as the impregnation property of electrolyte solution  16  into capacitor element  12  is taken into consideration, electrolyte solution  16  may be prepared by mixing the other solvents, for example, γ-butyrolactone, ethylene glycol, and sulfolane, having volatility and low viscosity. 
     Furthermore, solid electrolyte layer  122  is an electroconductive polymer such as polythiophene or derivatives thereof, for example, poly(3,4-ethylenedioxythiophene). The electroconductive polymer incorporates dopant. The dopant has a role of expressing electric conductivity. As the typical dopant, acids such as p-toluenesulfonic acid and polystyrenesulfonic acid are used. 
     However, when dedoping proceeds because an electroconductive polymer is exposed to an alkaline atmosphere due to electrolysis of water existing in the surroundings, or because an electroconductive polymer reacts with a base component in electrolyte solution  16 , the conductivity may be lowered. Thus, it is preferable that the dissolved components such as a solute and additives dissolved in the low-volatile solvent include more of the acid than the base. Thanks to the more acid, since the surrounding environment of solid electrolyte layer  122  continues to be maintained at the acidic state by electrolyte solution  16 , dedoping is suppressed, and change in the ESR of the electrolytic capacitor can be reduced. Furthermore, since polyalkylene glycol or derivatives thereof continue to remain as the solvent, the solute and the additives can continue to exhibit their functions in the solvent. 
     Examples of acids constituting these dissolved components include aromatic organic carboxylic acid, for example, phthalic acid, benzoic acid, nitrobenzoic acid, salicylic acid, trimellitic acid, and pyromellitic acid. Among them, trimellitic acid and pyromellitic acid containing at least three carboxyl groups are particularly preferable because they have a larger number of carboxyl groups and can be more acidic as compared with conventional phthalic acid. Furthermore, inorganic acid such as boric acid and phosphoric acid and compounds thereof are more stable even at a high temperature. Furthermore, since a complex of mannitol and boric acid is more acidic, it exhibits a special advantageous effect with respect to a dedoping reaction at a high temperature. 
     When a strongly acidic solute or additives are used, dedoping can be suppressed efficiently. However, there is a problem that aluminum as an electrode body is dissolved with the strongly acidic solute or additives. Therefore, in order to ensure reliability, it is important to control the dedoping reaction by selecting weak acid such as organic carboxylic acid and boric acid. 
     Furthermore, electrolyte solution  16  can contain appropriate additives for the purpose of absorbing gas, stabilizing a withstand voltage, adjusting pH, preventing oxidization, and the like. For example, polyalkylene glycol and/or derivatives thereof may contain an oxidation inhibitor. As the oxidation inhibitor, amine-based oxidation inhibitors, benzotriazole-based oxidation inhibitors, phenol-based oxidation inhibitors, and phosphorus-based oxidation inhibitors are effective for applications of use of capacitors. Examples thereof include diphenyl amine, naphthol, nitrophenol, catechol, resorcinol, hydroquinone, pyrogallol, and the like. Among them, hydroquinone and pyrogallol include a plurality of OH groups, and have a high oxidation inhibiting effect. Such additives may be used singly or in combination thereof. 
     Next, a method for manufacturing the electrolytic capacitor configured as mentioned above in accordance with an exemplary embodiment is described with reference to  FIGS. 1 and 2 . Firstly, anode foil  12 A having dielectric layer  121  of oxide film on the surface thereof and made of a valve metal such as aluminum, cathode foil  12 B and separator  12 C are cut into a predetermined width and length. Then, one end portions of lead wires  11 A and  11 B are respectively connected to anode foil  12 A and cathode foil  12 B by a method such as caulking, or a method using ultrasonic waves. After that, as shown in  FIG. 2 , anode foil  12 A and cathode foil  12 B are wound in a roll form with separator  12 C interposed therebetween to be formed into an approximately cylindrical shape, and the side surface of the outer periphery is fixed with insulating tape and the like (not shown). Thus, capacitor element  12  is formed. 
     Note here that it is preferable that the surface of anode foil  12 A is subjected to etching, vapor deposition of metal particles, or the like, so that the surface area of anode foil  12 A is appropriately enlarged. Dielectric layer  121  made of an oxide film is formed as a dielectric oxide film by subjecting a valve metal such as aluminum as electrode material to anodic oxidation. In addition, dielectric layer  121  may be formed on electrode material by vapor deposition or coating. 
     Note here that it is preferable that the surface of cathode foil  12  B is subjected to surface treatment such as etching, formation of an oxide film, vapor deposition of metal particles, and attachment of electrically conductive particles such as carbon, if necessary, in order to improve the contact state with respect to solid electrolyte layer  122 . 
     After that, an oxide film on the surface of anode foil  12 A may be repaired by applying a voltage to lead wires  11 A and  11 B after immersing the formed capacitor element  12  in an anodization solution. 
     Next, lead wires  11 A and  11 B led out from capacitor element  12  are inserted into through holes  14 A and  14 B provided in seal member  14 , respectively, and seal member  14  is mounted on capacitor element  12 . Seal member  14  may be mounted before capacitor element  12  is immersed in an anodization solution. 
     After that, solid electrolyte layer  122  is formed between anode foil  12 A and cathode foil  12 B of capacitor element  12 . For solid electrolyte layer  122 , for example, poly(3,4-ethylenedioxythiophene) (PEDOT) as an electroconductive polymer is used. In this case, electrolyte layer  122  is formed by, for example, allowing capacitor element  12  to be impregnated with a dispersion solution in which PEDOT is dispersed, followed by lifting up capacitor element  12  and drying thereof. Alternatively, PEDOT may be formed by a chemical polymerization reaction in capacitor element  12  by using a solution of a monomer such as 3,4-ethylenedioxythiophene, an oxidizer solution containing ferric p-toluenesulfonate and the like, and ethanol and the like as a solvent, and impregnating capacitor element  12  with these solutions. 
     Next, capacitor element  12  is accommodated in case  13  together with electrolyte solution  16  and disposed at an opening of case  13 . In order to allow capacitor element  12  to be impregnated with electrolyte solution  16 , a predetermined amount of electrolyte solution  16  is previously injected in case  13 , and capacitor element  12  is impregnated with electrolyte solution  16  when it is accommodated in case  13 . Alternatively, capacitor element  12  may be immersed in an impregnation tank storing electrolyte solution  16  and lifted up, and then it may be accommodated in case  13 . Furthermore, the pressure of the surrounding may be occasionally reduced at the time of impregnation. Note here that an excess amount of electrolyte solution  16  that cannot be used for impregnation of capacitor element  12  may be kept in case  13 . 
     Next, drawing processing part  13 A is formed by winding and tightening case  13  from the outer peripheral side surface, thereby an opening of case  13  is sealed. As an outer package, capacitor element  12  is covered with an insulating coating resin made of, for example, an epoxy resin, and the other end portions of lead wires  11 A and  11 B may be led to the outer part of the outer package material. 
     Furthermore, an electrolytic capacitor may be, for example, a surface mount type as mentioned below. Firstly, an insulating terminal plate (not shown) is disposed so that it is in contact with an opening of case  13 . Then, the other end portions of lead wires  11 A and  11 B led out from the outer surface of seal member  14  sealing the opening of case  13  are inserted into a pair of through holes (not shown) provided in the insulating terminal plate. Then, lead wires  11 A and  11 B are bent at about a right angle in mutually different directions and accommodated in recess portions (not shown) provided on the outer surface of the insulating terminal plate. 
     Note here that after the opening of case  13  is sealed, or after the insulating terminal plate is attached, a voltage may be applied appropriately between lead wires  11 A and  11 B, and thus, re-anodization may be carried out. 
     As mentioned above, an electrolytic capacitor in this exemplary embodiment includes electrolyte solution  16  containing polyalkylene glycol or derivatives thereof, and solid electrolyte layer  122  of, for example, an electroconductive polymer. Therefore, an electrolytic capacitor having a small size, a large capacitance, and a low ESR is achieved. The volatility of polyalkylene glycol or derivatives thereof is extremely low. Therefore, even if the electrolytic capacitor is used under a high-temperature environment of a maximum working temperature of 85° C. to 150° C. for a long time beyond the guaranteed lifetime, electrolyte solution  16  having an effect of repairing a defective part occurring in a dielectric oxide film can be continued to be maintained. As a result, in the electrolytic capacitor in this exemplary embodiment, an increase in leakage current is suppressed and an excellent short-circuit resistance property can be ensured. 
     Hereinafter, advantageous effects of this exemplary embodiment are described with reference to specific samples E1 to E18. 
     (Sample E1) 
     As sample E1 of an electrolytic capacitor in accordance with an exemplary embodiment of the present disclosure, a hybrid-type electrolytic capacitor having a wound-type capacitor element (diameter: 6.3 mm, height: 5.8 mm, and guaranteed lifetime: 5,000 hours at 105° C.) having a rated voltage of 35 V and a capacitance of 27 μF is prepared. 
     Firstly, as shown in  FIG. 2 , anode foil  12 A made of aluminum and having dielectric layer  121  of aluminum oxide film on the surface thereof, cathode foil  12 B, and separator  12 C are cut into a predetermined width and length. Then, one end portions of lead wires  11 A and  11 B are respectively connected to anode foil  12 A and cathode foil  12 B by needle-caulking. After that, anode foil  12 A and cathode foil  12 B are wound in a roll form with separator  12 C interposed therebetween to be formed into an approximately cylindrical shape. Furthermore, the outer peripheral side surface is fixed with insulating tape (not shown). Thus, capacitor element  12  is formed. 
     Note here that the surface area of anode foil  12 A is enlarged by an etching process. Furthermore, dielectric layer  121  made of aluminum oxide film is formed by an anodic oxidation process. Also, the surface area of cathode foil  12 B is enlarged by an etching process. Note here that separator  12 C is made of a nonwoven fabric mainly containing cellulose. 
     Next, lead wires  11 A and  11 B led out from capacitor element  12  are inserted into through holes  14 A and  14 B provided in seal member  14  of rubber packing, and seal member  14  is mounted on capacitor element  12 . 
     After that, capacitor element  12  is immersed in an anodization solution that is kept at 60° C., a voltage of 63 V is applied between lead wires  11 A and  11 B for 10 minutes, and thus, an oxide film on the surface of anode foil  12 A is repaired. 
     Next, solid electrolyte layer  122  made of poly(3,4-ethylenedioxythiophene) (PEDOT) is formed between anode foil  12 A and cathode foil  12 B of capacitor element  12 . Specifically, after capacitor element  12  is impregnated with a dispersion solution in which PEDOT is dispersed in an aqueous solution, capacitor element  12  is lifted up and dried at 110° C. for 30 minutes. In the PEDOT, polystyrene sulfonic acid is used as dopant. 
     On the other hand, various electrolyte solutions shown in Tables 1 to 4 are prepared. Among them, electrolyte solution B is injected into bottomed cylindrical case  13  made of aluminum. Electrolyte solution B contains ethyldimethylamine phthalate, and 5 wt. % of polyethylene glycol (molecular weight: 300) as a solvent. 
     
       
         
           
               
               
               
               
               
             
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                 electrolyte 
                   
                   
                   
               
               
                   
                 solution 
                 PEG(wt %) 
                 GBL(wt %) 
                 SL(wt %) 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
            
               
                   
                 A 
                 0 
                 50 
                 25 
               
               
                   
                 B 
                 5 
                 45 
                 25 
               
               
                   
                 C 
                 10 
                 40 
                 25 
               
               
                   
                 D 
                 15 
                 35 
                 25 
               
               
                   
                 E 
                 50 
                 0 
                 25 
               
               
                   
                 F 
                 75 
                 0 
                 0 
               
               
                   
                   
               
               
                   
                 PEG: polyethylene glycol (molecular weight: 300) 
               
               
                   
                 GBL: γ-butyrolactone 
               
               
                   
                 SL: sulfolane 
               
               
                   
                 *Each electrolyte solution contains 24 wt % of ethyldimethylamine phthalate and 1 wt % of nitrobenzoic acid. 
               
            
           
         
       
     
     
       
         
           
               
               
               
             
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                 electrolyte 
                 molecular weight of 
               
               
                   
                 solution 
                 polyethylene glycol 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
            
               
                   
                 G 
                 200 
               
               
                   
                 H 
                 400 
               
               
                   
                 I 
                 600 
               
               
                   
                 J 
                 1000 
               
               
                   
                 K 
                 1500 
               
               
                   
                 L 
                 2000 
               
               
                   
                   
               
               
                   
                 * The composition is as following: 15 wt % of polyethylene glycol, 35 wt % of γ-butyrolactone, 25 wt % of sulfolane, 24 wt % of ethyldimethylamine phthalate and 1 wt % of nitrobenzoic acid. 
               
            
           
         
       
     
     
       
         
           
               
               
               
               
               
               
             
               
                 TABLE 3 
               
               
                   
               
               
                 electrolyte 
                 FEDMA 
                 NBA 
                 boric acid 
                 PA 
                 PG 
               
               
                 solution 
                 (wt %) 
                 (wt %) 
                 (wt %) 
                 (wt %) 
                 (wt %) 
               
               
                   
               
             
            
               
                 M 
                 20 
                 1 
                 4 
                 — 
                 — 
               
               
                 N 
                 20 
                 1 
                 — 
                 4 
                 — 
               
               
                 O 
                 16 
                 1 
                 — 
                 4 
                 4 
               
               
                   
               
               
                 FEDMA: ethyldimethylamine phthalate 
               
               
                 NBA: nitrobenzoic acid 
               
               
                 PA: pyromellitic acid 
               
               
                 PG: pyrogallol 
               
               
                 * Each electrolyte solution contains 15 wt % of polyethylene glycol (molecular weight: 300), 35 wt % of □-butyrolactone and 25 wt % sulfolane. 
               
            
           
         
       
     
     
       
         
           
               
               
               
             
               
                   
                 TABLE 4 
               
               
                   
                   
               
               
                   
                 electrolyte 
                 molecular weight of 
               
               
                   
                 solution 
                 polypropylene glycol 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
            
               
                   
                 P 
                 100 
               
               
                   
                 Q 
                 200 
               
               
                   
                 R 
                 5000 
               
               
                   
                 S 
                 6000 
               
               
                   
                   
               
               
                   
                 * The composition is as following: 15 wt % of polypropylene glycol, 35 wt % of γ-butyrolactone, 25 wt % of sulfolane, 24 wt % of ethyldimethylamine phthalate and 1 wt % of nitrobenzoic acid. 
               
            
           
         
       
     
     Then, capacitor element  12  is inserted into case  13 , capacitor element  12  is impregnated with electrolyte solution  16 , and seal member  14  mounted on capacitor element  12  is disposed at an opening of case  13 . 
     Next, case  13  is wound and tightened from the outer peripheral side surface around the opening to form drawing processing part  13 A, thus generating a compressive stress on seal member  14  that is a rubber elastic body. Thus, an opening of case  13  is sealed. 
     Thereafter, re-anodization is carried out by applying a voltage of 40 V between lead wires  11 A and  11 B led out to the outside for 60 minutes. Thus, an electrolytic capacitor of sample E1 is produced. 
     Relative to the configuration of sample E1, in samples E2 to E18, compositions of the electrolyte solution are changed, and electrolyte solutions C to S shown in Tables 1 to 4 are used, respectively. In samples E2 to E5 (electrolyte solutions C to F), the ratio (wt. %) of polyethylene glycol contained in electrolyte solution  16  is changed. In samples E6 to E11 (electrolyte solutions G to L), the molecular weight of polyethylene glycol is changed. In samples E12 to E14 (electrolyte solutions M to O), a solute and additives are further added. In samples E15 to E18 (electrolyte solutions P to S), polyalkylene glycol contained in electrolyte solution  16  is polypropylene glycol, and the molecular weight of polypropylene glycol is changed. Hereinafter, samples E2 to E18 are described in detail. 
     (Sample E2) 
     As sample E2, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E1 except that electrolyte solution C shown in Table 1 is used instead of electrolyte solution B used in sample E1, and electrolyte solution C contains ethyldimethylamine phthalate and nitrobenzoic acid and contains 10 wt. % of polyethylene glycol (molecular weight: 300) as a solvent. 
     (Sample E3) 
     As sample E3, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E1 except that electrolyte solution D shown in Table 1 is used instead of electrolyte solution B used in sample E1, and electrolyte solution D contains ethyldimethylamine phthalate and nitrobenzoic acid and contains 15 wt. % of polyethylene glycol (molecular weight: 300) as a solvent. 
     (Sample E4) 
     As sample E4, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E1 except that electrolyte solution E shown in Table 1 is used instead of electrolyte solution B used in sample E1, and electrolyte solution E contains ethyldimethylamine phthalate and nitrobenzoic acid, and contains 50 wt. % of polyethylene glycol (molecular weight: 300) as a solvent. 
     (Sample E5) 
     As sample E5, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E1 except that electrolyte solution F shown in Table 1 is used instead of electrolyte solution B used in sample E1, and electrolyte solution F contains ethyldimethylamine phthalate and nitrobenzoic acid, and contains 75 wt. % of polyethylene glycol (molecular weight: 300) as a solvent. 
     (Sample E6) 
     As sample E6, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample E3 except that electrolyte solution G shown in Table 2 is used instead of electrolyte solution D used in sample E3, and the molecular weight of polyethylene glycol is changed from 300 to 200 in electrolyte solution G as compared with electrolyte solution D. 
     (Sample E7) 
     As sample E7, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample E3 except that electrolyte solution H shown in Table 2 is used instead of electrolyte solution D used in sample E3, and the molecular weight of polyethylene glycol is changed from 300 to 400 in electrolyte solution H as compared with electrolyte solution D. 
     (Sample E8) 
     As sample E8, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample E3 except that electrolyte solution I shown in Table 2 is used instead of electrolyte solution D used in sample E3, and the molecular weight of polyethylene glycol is changed from 300 to 600 in electrolyte solution I as compared with electrolyte solution D. 
     (Sample E9) 
     As sample E9, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E3 except that electrolyte solution J shown in Table 2 is used instead of electrolyte solution D used in sample E3, and the molecular weight of polyethylene glycol is changed from 300 to 1000 in electrolyte solution J as compared with electrolyte solution D. 
     (Sample E10) 
     As sample E10, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E3 except that electrolyte solution K shown in Table 2 is used instead of electrolyte solution D used in sample E3, and the molecular weight of polyethylene glycol is changed from 300 to 1500 in electrolyte solution K as compared with electrolyte solution D. 
     (Sample E11) 
     As sample E11, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μD is produced in the same manner as in sample E3 except that electrolyte solution L shown in Table 2 is used instead of electrolyte solution D used in sample E3, and the molecular weight of polyethylene glycol is changed from 300 to 2000 in electrolyte solution L as compared with electrolyte solution D. 
     (Sample E12) 
     As sample E12, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E3 except that electrolyte solution M shown in Table 3 is used instead of electrolyte solution D used in sample E3, and as compared with electrolyte solution D, electrolyte solution M additionally contains boric acid (4 wt. %) and the weight content of ethyldimethylamine phthalate is reduced by the that of boric acid. 
     (Sample E13) 
     As sample E13, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample E3 except that electrolyte solution N shown in Table 3 is used instead of electrolyte solution D used in sample E3, and as compared with electrolyte solution D, electrolyte solution N additionally contains pyromellitic acid (4 wt. %) and the weight content of ethyldimethylamine phthalate is reduced by that of pyromellitic acid. 
     (Sample E14) 
     As sample E14, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E3 except that electrolyte solution O shown in Table 3 is used instead of electrolyte solution D used in sample E3, and as compared with electrolyte solution D, electrolyte solution O additionally contains pyromellitic acid (4 wt. %) and pyrogallol (4 wt. %), and the weight contents of ethyldimethylamine phthalate is reduced by that of pyromellitic acid and pyrogallol. 
     (Sample E15) 
     As sample E15, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample E3 except that electrolyte solution P shown in Table 4 is used instead of electrolyte solution D used in sample E3, and polyalkylene glycol contained in the electrolyte solution is changed from polyethylene glycol (molecular weight: 300) to polypropylene glycol (molecular weight: 100) in electrolyte solution P as compared with electrolyte solution D. 
     (Sample E16) 
     As sample E16, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E15 except that electrolyte solution Q shown in Table 4 is used instead of electrolyte solution P used in sample E15, and polyalkylene glycol contained in the electrolyte solution is changed from polypropylene glycol (molecular weight: 100) to polypropylene glycol (molecular weight: 200) in electrolyte solution Q as compared with electrolyte solution P. 
     (Sample E17) 
     As sample E17, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample E15 except that electrolyte solution R shown in Table 4 is used instead of electrolyte solution P used in sample E15, and polyalkylene glycol contained in the electrolyte solution is changed from polypropylene glycol (molecular weight: 100) to polypropylene glycol (molecular weight: 5000) in electrolyte solution R as compared with electrolyte solution P. 
     (Sample E18) 
     As sample E18, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample E15 except that electrolyte solution S shown in Table 4 is used instead of electrolyte solution P used in sample E15, and polyalkylene glycol contained in the electrolyte solution is changed from polypropylene glycol (molecular weight: 100) to polypropylene glycol (molecular weight: 6000) in electrolyte solution S as compared with electrolyte solution P. 
     Furthermore, electrolytic capacitors are produced for comparison with samples E1 to E18. Sample C  1  is a hybrid-type electrolytic capacitor which does not contain polyethylene glycol in an electrolyte solution. Sample C2 is a solid-type electrolytic capacitor which includes a solid electrolyte of PEDOT as an electrolyte, and which does not includes an electrolyte solution. Sample C3 is a liquid-type electrolytic capacitor which includes only an electrolyte solution that does not contain polyethylene glycol, as an electrolyte. In other words, sample C3 does not include a solid electrolyte. Also, sample C3 is configured to be used for electrolytic capacitors having a low withstand voltage in which a rated voltage is at most 100 W.V. and has a low ESR, which is used in a smoothing circuit and a control circuit at the power supply output side. 
     Note here that for comparison, as samples C4 to C7, liquid-type electrolytic capacitors, which include, as an electrolyte, only an electrolyte solution containing polyethylene glycol and which does not include a solid electrolyte are produced. Hereinafter, these samples C1 to C7 are described. 
     (Sample C1) 
     As sample C1, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E1 except that electrolyte solution A shown in Table 1 is used instead of electrolyte solution B used in sample E1, and as compared with electrolyte solution B, electrolyte solution A does not contain polyethylene glycol in a solvent and the weight content of γ-butyrolactone is increased by that of polyethylene glycol. 
     (Sample C2) 
     Sample C2 includes only a solid electrolyte made of PEDOT without including electrolyte solution B used in sample E1. With such a configuration, a solid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced. 
     (Sample C3) 
     As sample C3, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample E1 except that solid electrolyte made of PEDOT used in sample E1 is not included and electrolyte solution A shown in Table 1 is used instead of electrolyte solution B, and as compared with electrolyte solution B, electrolyte solution A does not contain polyethylene glycol in a solvent and the weight content of γ-butyrolactone is increased by that of polyethylene glycol. 
     (Sample C4) 
     As sample C4, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μF is produced in the same manner as in sample C3 except that electrolyte solution B shown in Table 1 is used instead of electrolyte solution A used in sample C3, and as compared with electrolyte solution A, electrolyte solution B contains 5 wt % of polyethylene glycol in a solvent and the weight content of γ-butyrolactone is reduced by that of polyethylene glycol. 
     (Sample C5) 
     As sample C5, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample C3 except that electrolyte solution C shown in Table 1 is used instead of electrolyte solution A used in sample C3, and as compared with electrolyte solution A, electrolyte solution C contains 10 wt % of polyethylene glycol in a solvent and the weight content of γ-butyrolactone is reduced by that of polyethylene glycol. 
     (Sample C6) 
     As sample C6, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample C3 except that electrolyte solution D shown in Table 1 is used instead of electrolyte solution A used in sample C3, and as compared with electrolyte solution A, electrolyte solution D contains 15 wt % of polyethylene glycol in a solvent and the weight content of γ-butyrolactone is reduced by that of polyethylene glycol. 
     (Sample C7) 
     As sample C7, a hybrid-type electrolytic capacitor including a wound-type capacitor element and having a rated voltage of 35 V and a capacitance of 27 μI′ is produced in the same manner as in sample C3 except that electrolyte solution E shown in Table 1 is used instead of electrolyte solution A used in sample C3, and as compared with electrolyte solution A, electrolyte solution E contains 50 wt % of polyethylene glycol in a solvent and the weight content γ-butyrolactone is reduced by that of polyethylene glycol. 
     Configurations of the solid electrolytes and the electrolyte solutions in the electrolytic capacitors in the above-mentioned samples E1 to E18 and samples C1 to C7 are shown in Table 5. Furthermore, 30 samples of electrolytic capacitors of each of samples E1 to E18 and samples C1 to C7 are produced, and the initial properties are measured. The measurement results are shown in Table 6. 
     As the initial properties, capacitance values, ESR values, and leakage current values are measured and the average values thereof are calculated. The capacitance value is measured at 120 Hz, the ESR value is measured at 100 kHz, and the leakage current value is measured as a value after the rated voltage is applied for two minutes. Measurement is carried out in a 20° C. environment. 
     
       
         
           
               
               
               
               
             
               
                 TABLE 5 
               
               
                   
               
               
                   
                 solid 
                   
                   
               
               
                   
                 electrolyte 
                 electrolyte 
               
               
                 sample 
                 layer 
                 solution 
                 remarks 
               
               
                   
               
             
            
               
                 E1 
                 PEDOT 
                 B 
                 PEG(Mw300)5 wt % 
               
               
                 E2 
                 PEDOT 
                 C 
                 PEG(Mw300)10 wt % 
               
               
                 E3 
                 PEDOT 
                 D 
                 PEG(Mw300)15 wt % 
               
               
                 E4 
                 PEDOT 
                 E 
                 PEG(Mw300)50 wt % 
               
               
                 E5 
                 PEDOT 
                 F 
                 PEG(Mw300)75 wt % 
               
               
                 E6 
                 PEDOT 
                 G 
                 PEG(Mw200)15 wt % 
               
               
                 E7 
                 PEDOT 
                 H 
                 PEG(Mw400)15 wt % 
               
               
                 E8 
                 PEDOT 
                 I 
                 PEG(Mw600)15 wt % 
               
               
                 E9 
                 PEDOT 
                 J 
                 PEG(Mw1000)15 wt % 
               
               
                 E10 
                 PEDOT 
                 K 
                 PEG(Mw1500)15 wt % 
               
               
                 E11 
                 PEDOT 
                 L 
                 PEG(Mw2000)15 wt % 
               
               
                 E12 
                 PEDOT 
                 M 
                 PEG(Mw300)15 wt % + boric acid 
               
               
                 E13 
                 PEDOT 
                 N 
                 PEG(Mw300)15 wt % + PA 
               
               
                 E14 
                 PEDOT 
                 0 
                 PEG(Mw300)15 wt % + PA + PG 
               
               
                 E15 
                 PEDOT 
                 P 
                 PPG(Mw100)15 wt % 
               
               
                 E16 
                 PEDOT 
                 Q 
                 PPG(Mw200)15 wt % 
               
               
                 E17 
                 PEDOT 
                 R 
                 PPG(Mw5000)15 wt % 
               
               
                 E18 
                 PEDOT 
                 S 
                 PPG(Mw6000)15 wt % 
               
               
                 C1 
                 PEDOT 
                 A 
                 without polyalkylene glycol 
               
               
                 C2 
                 PEDOT 
                 — 
                 without electrolyte solution 
               
               
                 C3 
                 — 
                 A 
                 without solid electrolyte layer, 
               
               
                   
                   
                   
                 without polyalkylene glycol 
               
               
                 C4 
                 — 
                 B 
                 without solid electrolyte layer, 
               
               
                   
                   
                   
                 PEG(Mw300)5 wt % 
               
               
                 C5 
                 — 
                 C 
                 without solid electrolyte layer, 
               
               
                   
                   
                   
                 PEG(Mw300)10 wt % 
               
               
                 C6 
                 — 
                 D 
                 without solid electrolyte layer, 
               
               
                   
                   
                   
                 PEG(Mw300)15 wt % 
               
               
                 C7 
                 — 
                 E 
                 without solid electrolyte layer, 
               
               
                   
                   
                   
                 PEG(Mw300)50 wt % 
               
               
                   
               
               
                 PEG: polyethylene glycol 
               
               
                 Mw: molecular weight 
               
               
                 PPG: polypropylene glycol 
               
               
                 PA: pyromellitic acid 
               
               
                 PG: pyrogallol 
               
               
                 PEDOT: poly(3,4-ethylenedioxythiophene) 
               
            
           
         
       
     
     
       
         
           
               
               
             
               
                   
                 TABLE 6 
               
             
            
               
                   
                   
               
               
                   
                 initial property 
               
            
           
           
               
               
               
               
               
            
               
                   
                 sample 
                 capacitance (μF) 
                 ESR(Ω) 
                 leakage current (μA) 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                   
                 E1 
                 27.0 
                 0.023 
                 0.5 
               
               
                   
                 E2 
                 26.9 
                 0.022 
                 0.6 
               
               
                   
                 E3 
                 26.9 
                 0.023 
                 0.5 
               
               
                   
                 E4 
                 26.9 
                 0.021 
                 0.6 
               
               
                   
                 E5 
                 27.0 
                 0.022 
                 0.7 
               
               
                   
                 E6 
                 27.1 
                 0.022 
                 0.6 
               
               
                   
                 E7 
                 27.0 
                 0.023 
                 0.6 
               
               
                   
                 E8 
                 27.0 
                 0.022 
                 0.5 
               
               
                   
                 E9 
                 26.9 
                 0.023 
                 0.7 
               
               
                   
                 E10 
                 24.2 
                 0.021 
                 0.6 
               
               
                   
                 E11 
                 23.9 
                 0.023 
                 0.7 
               
               
                   
                 E12 
                 27.0 
                 0.021 
                 0.5 
               
               
                   
                 E13 
                 26.8 
                 0.023 
                 0.7 
               
               
                   
                 E14 
                 26.9 
                 0.022 
                 0.5 
               
               
                   
                 E15 
                 27.0 
                 0.021 
                 0.6 
               
               
                   
                 E16 
                 27.1 
                 0.022 
                 0.6 
               
               
                   
                 E17 
                 26.9 
                 0.023 
                 0.5 
               
               
                   
                 E18 
                 24.3 
                 0.022 
                 0.5 
               
               
                   
                 C1 
                 26.9 
                 0.023 
                 0.6 
               
               
                   
                 C2 
                 20.1 
                 0.023 
                 10.1 
               
               
                   
                 C3 
                 27.0 
                 2.130 
                 0.7 
               
               
                   
                 C4 
                 27.0 
                 2.450 
                 0.8 
               
               
                   
                 C5 
                 26.9 
                 2.882 
                 0.6 
               
               
                   
                 C6 
                 26.8 
                 3.160 
                 0.6 
               
               
                   
                 C7 
                 27.0 
                 4.301 
                 0.5 
               
               
                   
                   
               
            
           
         
       
     
     As shown in Table 5, hybrid-type electrolytic capacitors shown in samples E1 to E18 include electrolyte solution  16  containing polyalkylene glycol or derivatives thereof and a solid electrolyte made of an electroconductive polymer, as the electrolyte. Therefore, as shown in Table 6, samples E1 to E18 have an ESR that is as low as that of sample C2 using a solid electrolyte. Furthermore, they exhibit greater capacitance and an extremely low leakage current property as compared with sample C2. 
     Sample C1 is a hybrid-type electrolytic capacitor including electrolyte solution A that has been used in a conventional liquid-type electrolytic capacitor having a rated voltage of at most 100 W.V. applicable to a smoothing circuit and a control circuit at the power supply output side. Samples E1 to E18 show the same level of the initial properties as compared with sample C1. 
     Note here that electrolyte solutions B to E used in samples E1 to E4 contain polyethylene glycol as a solvent. Electrolyte solutions B to E are also used in samples C3 to C7. As is apparent from the results of samples C3 to C7, when electrolyte solutions B to E are used in a conventional liquid-type electrolytic capacitor, an ESR is extremely large. Thus, electrolyte solutions B to E cannot be used in liquid-type electrolytic capacitors having a low ESR and a low withstand voltage of a rated voltage of at most 100 W.V. applicable to circuits at the power supply output side, for example, a smoothing circuit or a control circuit. 
     Next, an acceleration test is carried out for evaluating electrolytic capacitors of samples E1 to E18 and samples C1 to C7 in the conditions beyond the guaranteed lifetime. Then, 30 samples of electrolytic capacitors of each of samples E1 to E18 and samples C1 to C7 are produced for carrying out an acceleration test. 
     The acceleration test is carried out in a state in which capacitor element  12  is opened without using outer package  15  in order to accelerate vaporization and volatilization of the solvent of electrolyte solution  16 . That is to say, in the samples for the acceleration test, similar to the production procedure of each of the above-mentioned samples, solid electrolyte layer  122  made of PEDOT is formed in capacitor element  12  if necessary and furthermore impregnated with a predetermined amount of each of the electrolyte solutions shown in Tables 1 to 4. After that, capacitor element  12  is not accommodated in case  13  but maintained to be opened (exposed in atmosphere). 
     When capacitor element  12  is immersed in an anodization solution to carry out repairing anodization, or when capacitor element  12  is impregnated with a dispersion solution of an electroconductive polymer, in order to enhance the workability for the purpose of preventing the anodization solution or dispersion solution from attaching to lead wires, seal member  14  may be mounted on capacitor element  12 . 
     Then, in the samples in this state, while a rated voltage is applied between lead wires  11 A and  11 B, the samples are left in a constant temperature chamber at a temperature of 125° C. for three hours. That is to say, in the acceleration test, while a rated voltage is applied between anode foil  12 A and cathode foil  12 B, the samples are left under 125° C. for three hours. As evaluation results of the acceleration test, measured initial properties and properties after the acceleration test are shown in Table 7. As the properties after the acceleration test, a change rate of capacitance, a change rate of ESR, a leakage current value, and an occurrence rate of short circuit are calculated. Furthermore, change of the weight of electrolyte solution  16  before and after the acceleration test is shown in Table 8. 
     
       
         
           
               
               
             
               
                   
                 TABLE 7 
               
             
            
               
                   
                   
               
               
                   
                 properties after acceleration test 
               
            
           
           
               
               
               
               
               
            
               
                   
                   
                   
                   
                 occurrence 
               
               
                   
                 change in 
                 change in 
                 leakage 
                 rate of short 
               
               
                   
                 capacitance 
                 ESR 
                 current 
                 circuit 
               
               
                 sample 
                 (%) 
                 (%) 
                 (μA) 
                 (%) 
               
               
                   
               
            
           
           
               
               
               
               
               
            
               
                 E1 
                 −39 
                 35 
                 6.1 
                 0 
               
               
                 E2 
                 −34 
                 32 
                 3.5 
                 0 
               
               
                 E3 
                 −32 
                 32 
                 0.6 
                 0 
               
               
                 E4 
                 −21 
                 31 
                 0.5 
                 0 
               
               
                 E5 
                 −16 
                 29 
                 0.7 
                 0 
               
               
                 E6 
                 −38 
                 34 
                 2.5 
                 0 
               
               
                 E7 
                 −30 
                 29 
                 0.5 
                 0 
               
               
                 E8 
                 −28 
                 28 
                 0.6 
                 0 
               
               
                 E9 
                 −27 
                 28 
                 0.5 
                 0 
               
               
                 E10 
                 −24 
                 26 
                 0.6 
                 0 
               
               
                 E11 
                 −20 
                 25 
                 0.4 
                 0 
               
               
                 E12 
                 −30 
                 21 
                 0.1 
                 0 
               
               
                 E13 
                 −30 
                 20 
                 0.1 
                 0 
               
               
                 E14 
                 −31 
                 15 
                 0.1 
                 0 
               
               
                 E15 
                 −35 
                 32 
                 0.6 
                 0 
               
               
                 E16 
                 −33 
                 30 
                 0.6 
                 0 
               
               
                 E17 
                 −20 
                 26 
                 0.5 
                 0 
               
               
                 E18 
                 −16 
                 25 
                 0.5 
                 0 
               
               
                 C1 
                 unmeasurable 
                 unmeasurable 
                 unmeasurable 
                 100 
               
               
                 C2 
                 unmeasurable 
                 unmeasurable 
                 unmeasurable 
                 100 
               
               
                 C3 
                 −100  
                 unmeasurable 
                 0.8 
                 0 
               
               
                 C4 
                 −40 
                 unmeasurable 
                 0.7 
                 0 
               
               
                 C5 
                 −35 
                 unmeasurable 
                 0.8 
                 0 
               
               
                 C6 
                 −29 
                 unmeasurable 
                 0.7 
                 0 
               
               
                 C7 
                 −22 
                 unmeasurable 
                 0.8 
                 0 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
             
               
                   
                 TABLE 8 
               
             
            
               
                   
                   
               
               
                   
                 properties after acceleration test 
               
               
                   
                 remaining amount with respect to initial 
               
            
           
           
               
               
               
            
               
                   
                 initial state 
                 electrolyte solution 
               
            
           
           
               
               
               
               
            
               
                   
                 amount within initial electrolyte 
                   
                 remaining 
               
               
                   
                 solution 
                   
                 rate of 
               
            
           
           
               
               
               
               
               
            
               
                   
                 volatile 
                 low-volatile 
                 low-volatile 
                 low-volatile 
               
               
                   
                 solvent 
                 solvent 
                 solvent 
                 solvent 
               
               
                 sample 
                 (wt %) 
                 (wt %) 
                 (wt %) 
                 (%) 
               
               
                   
               
            
           
           
               
               
               
               
               
            
               
                 E1 
                 70.0 
                 5.0 
                 4.9 
                 98.0 
               
               
                 E2 
                 65.0 
                 10.0 
                 9.8 
                 98.0 
               
               
                 E3 
                 60.0 
                 15.0 
                 14.8 
                 98.7 
               
               
                 E4 
                 25.0 
                 50.0 
                 49.7 
                 99.4 
               
               
                 E5 
                 0  
                 75.0 
                 74.6 
                 99.5 
               
               
                 E6 
                 60.0 
                 15.0 
                 12.9 
                 86.0 
               
               
                 E7 
                 60.0 
                 15.0 
                 14.9 
                 99.3 
               
               
                 E8 
                 60.0 
                 15.0 
                 14.9 
                 99.3 
               
               
                 E9 
                 60.0 
                 15.0 
                 15.0 
                 100 
               
               
                 E10 
                 60.0 
                 15.0 
                 15.0 
                 100 
               
               
                 E11 
                 60.0 
                 15.0 
                 15.0 
                 100 
               
               
                 E12 
                 60.0 
                 15.0 
                 14.8 
                 98.7 
               
               
                 E13 
                 60.0 
                 15.0 
                 14.9 
                 99.3 
               
               
                 E14 
                 60.0 
                 15.0 
                 14.9 
                 99.3 
               
               
                 E15 
                 60.0 
                 15.0 
                 14.6 
                 97.3 
               
               
                 E16 
                 60.0 
                 15.0 
                 14.9 
                 99.3 
               
               
                 E17 
                 60.0 
                 15.0 
                 15.0 
                 100 
               
               
                 E18 
                 60.0 
                 15.0 
                 15.0 
                 100 
               
               
                 C1 
                 75.0 
                 0 
                 0 
                 — 
               
               
                 C2 
                 — 
                 — 
                 — 
                 — 
               
               
                 C3 
                 75.0 
                 0 
                 0 
                 — 
               
               
                 C4 
                 70.0 
                 5.0 
                 4.9 
                 98.0 
               
               
                 C5 
                 65.0 
                 10.0 
                 9.8 
                 98.0 
               
               
                 C6 
                 60.0 
                 15.0 
                 14.9 
                 99.3 
               
               
                 C7 
                 25.0 
                 50.0 
                 49.7 
                 99.4 
               
               
                   
               
            
           
         
       
     
     Note here that being in an opened state at 125° C. for three hours corresponds to being in a closed (sealed) state at 105° C. for 10000 hours. This is a value that is much more than a guaranteed lifetime of an electrolytic capacitor of 5000 hours at 105° C. This correlation can be understood from the correlation between data of temperatures and speeds at which each electrolyte solution vaporizes and volatilizes when capacitor element  12  is in an opened state and data of temperatures and speeds at which each electrolyte solution permeates and disperses from seal member  14  when capacitor element  12  is tightly closed in case  13  made of aluminum and seal member  14  of rubber packing. 
     As is apparent from Table 7, in hybrid-type electrolytic capacitors of samples E1 to E18, as compared with sample C  1 , in particular, the leakage current value and the occurrence rate of short circuit are remarkably reduced after acceleration test. As shown in Table 8, the solvent of electrolyte solution A used in sample C  1  is only volatile γ-butyrolactone and sulfolane, so that vaporization and volatilization proceed under a high-temperature environment. As a result, after the acceleration test, the weight cannot be measured, and a solvent is lost. Consequently, a function of repairing a defective part in the dielectric oxide film by the electrolyte solution cannot be maintained, the leakage current value is increased and the occurrence rate of short circuit is higher. 
     On the other hand, since electrolyte solutions B to S used in samples E1 to E18 contain polyalkylene glycol as a solvent, as shown in Table 8, vaporization and volatilization of the electrolyte solution are suppressed even under a high temperature. Although not shown in Table 8, in any samples, a remaining amount of a volatile solvent after the acceleration test cannot be measured. 
     Thus, even after the acceleration test, in other words, even beyond the guaranteed lifetime, samples E1 to E18 maintain the function of repairing a defective part in the dielectric oxide film by the electrolyte solution. Consequently, the leakage current value and the occurrence rate of short circuit are suppressed. Therefore, samples E1 to E18 have extremely high reliability. 
     Furthermore, as shown in the evaluation results of samples E3 to E5, when the content amount of polyethylene glycol contained in the electrolyte solution is made to be at least 15 wt. %, an increase in leakage current and the occurrence rate of short circuit can be more reduced as compared with those of samples E1 and E2. In this way, when the content amount of polyethylene glycol is made to be at least 15 wt. %, even if the electrolytic capacitor is exposed to a high-temperature environment beyond the guaranteed lifetime, it is thought that the performance and amount of an electrolyte solution sufficient to repair defective parts occurring on the entire surface of dielectric layer  121  can be maintained. Therefore, an excellent short-circuit resistance property can be ensured. 
     Furthermore, in samples E3, and E6 to E11, the molecular weight of polyethylene glycol contained in the electrolyte solution is changed. From the results of samples E3, E7, E8, and E9, it is shown that when the molecular weight of polyethylene glycol is in a range from 300 to 1000, inclusive, the increase in leakage current and the occurrence rate of short circuit can be particularly reduced. When the molecular weight of polyethylene glycol is in a range from 300 to 1000, inclusive, a function of the solvent can be exhibited in a liquid state, low volatility is exhibited and the weight is hardly reduced even under a high-temperature environment as in an acceleration test. Therefore, an effect of repairing a defective part in a dielectric oxide film by a nonvolatile solute dissolved in the solvent can be maintained. 
     On the other hand, as shown in sample E6, even if the molecular weight of polyethylene glycol is 200, a function of a liquid-state solvent can be exhibited. However, under a high-temperature environment, polyethylene glycol is vaporized and volatilized gradually although very slightly as compared with volatile solvents such as γ-butyrolactone and sulfolane. In other words, among samples E1 to E18, a sample having the smallest remaining rate of the low-volatile solvent is sample E6. Even in this case, the leakage current and the occurrence rate of short circuit are remarkably reduced as compared with those of sample C1. Therefore, electrolyte solution  16  may have a composition so that at least 86% of the low-volatile solvent remains after the electrolytic capacitor is left under 125° C. for three hours while outer package  15  is opened and a rated voltage of the electrolytic capacitor is applied between lead wires  11 A and  11 B. 
     Note here that this example describes a case in which polyethylene glycol having a molecular weight of 200 is used as the low-volatile solvent. However, any other low-volatile solvents may be used as long as at least 86% of the low-volatile solvent remains after the acceleration test. Furthermore, since the volatility of the solvent is affected by interaction with respect to other components contained in the electrolyte solution, the remaining rate may be achieved by a factor of components of the electrolyte solution other than the physical property of the low-volatile solvent itself. 
     On the other hand, as shown in samples E10 and E11, when the molecular weight of polyethylene glycol is increased to 1500 and 2000, the solvent shows low volatility and the weight thereof is hardly reduced even under a high-temperature environment. However, viscosity is extremely increased and the impregnation property with respect to capacitor element  12  is lowered, and thus the effective capacitance rate is low. 
     That is to say, even in the case where the molecular weight of polyethylene glycol is 200 or less and in the case where the molecular weight of polyethylene glycol is 1500 or more, as compared with a conventional hybrid-type electrolytic capacitor, when the electrolytic capacitor is exposed to a high-temperature environment beyond the guaranteed lifetime, it is possible to remarkably improve electric properties and to reduce occurrence rate of short circuit. However, in order to achieve a stably effective capacitance and an effect of suppressing the increase in leakage current and occurrence of short circuit, it is preferable that the molecular weight of polyethylene glycol is in a range from 300 to 1000, inclusive. 
     Furthermore, as shown in samples E15 to E18, when polypropylene glycol is used as a low-volatile solvent contained in the electrolyte solution, the same effect can be achieved as in the case where polyethylene glycol is used. That is to say, after the acceleration test, in other words, even beyond the guaranteed lifetime, a function of repairing a defective part in dielectric layer  121  can be maintained. As a result, the leakage current value and the occurrence of short circuit can be suppressed. Thus, an electrolytic capacitor with extremely high reliability can be achieved. 
     Note here that as shown in sample E15, even if the molecular weight of polypropylene glycol is 100 or less, a function of a liquid state solvent can be exhibited. However, under a high-temperature environment, polypropylene glycol is vaporized and volatilized gradually although very slightly as compared with volatile solvents such as γ-butyrolactone and sulfolane. 
     Furthermore, as shown in sample E18, when the molecular weight of polypropylene glycol is 6000 or more, the solvent shows low volatility and the weight thereof is hardly reduced even under a high-temperature environment. However, viscosity is extremely increased and the impregnation property with respect to capacitor element  12  is lowered, and thus the effective capacitance rate is low. 
     Therefore, similar to the case of polyethylene glycol, in order to achieve a stably effective capacitance and an effect of suppressing the increase in leakage current and occurrence of short circuit, it is preferable that the molecular weight of polypropylene glycol is in a range from 200 to 5000, inclusive. 
     Furthermore, electrolyte solution M used in sample E12 contains boric acid in a component element, and electrolyte solution N used in sample E13 contains pyromellitic acid in a component element. In addition, electrolyte solutions M and N are formed so that the ratio of the acid and the base contained in the solute and additives dissolved in the solvent shows that the acid is more than the base, and they are in contact with the circumference of PEDOT of solid electrolyte layer  122 . That is to say, components dissolved in the low-volatile solvent include a base and an acid more than the base. Therefore, electrolyte solutions M and N can suppress dedoping of polystyrene sulfonic acid as the dopant contained in PEDOT. Furthermore, since the solvent is low-volatile, even after the acceleration test, that is, even beyond the guaranteed lifetime, the effect against dedoping can be maintained. As a result, in samples E12 and E13, the change of ESR is suppressed. In other words, samples E12 and E13 exhibit extremely high reliability. 
     Furthermore, in sample E14, electrolyte solution O contains pyrogallol as an oxidation inhibitor, and it is in contact with the circumference of PEDOT of solid electrolyte layer  122 . Therefore, electrolyte solution O can suppress deterioration of PEDOT due to oxidation. Furthermore, since the solvent is low-volatile, after the acceleration test, that is, even beyond the guaranteed lifetime, the effect of suppressing deterioration due to oxidation can be maintained. As a result, in sample E14, the change of ESR is suppressed. That is to say, sample E14 exhibits extremely high reliability. 
     An electrolytic capacitor of the present disclosure includes an electrolyte solution, and a solid electrolyte such as an electroconductive polymer. Therefore, the electrolytic capacitor of the present disclosure has a small size, a large capacitance, and a low ESR. Furthermore, the electrolyte solution has an effect of repairing a defective part occurring in a dielectric layer provided on the surface of the anode foil. The electrolyte solution of the electrolytic capacitor of the present disclosure contains polyalkylene glycol or derivatives thereof having extremely low volatility. Therefore, even if the electrolytic capacitor is used under a high-temperature environment of a maximum working temperature of 85° C. to 150° C. for a long time beyond the guaranteed lifetime, a defective part occurring in the dielectric layer can still be repaired. 
     Therefore, the electrolytic capacitor of the present disclosure has a small size, a large capacitance, and a low ESR, as well as can suppress the increase in leakage current, and ensure an excellent short-circuit resistance property. Therefore, the electrolytic capacitor of the present disclosure is useful as electrolytic capacitors used in a smoothing circuit or a control circuit at the power supply output side of electrical apparatus which require high reliability for a long time, for example, AV apparatus or electrical apparatus mounted on vehicles.