Patent Publication Number: US-10316218-B2

Title: Aqueous silica slurry compositions for use in shallow trench isolation and methods of using them

Description:
The present invention relates to aqueous chemical mechanical planarization (CMP) polishing compositions comprising one or more dispersions of a plurality of spherical colloidal silica particles, of elongated, bent, or nodular silica particles, or their mixtures which contain a cationic nitrogen atom, and a copolymer of a diallylamine salt having a cationic amine group, such as diallylammonium chloride and sulfur dioxide or a copolymer of a diallylalkylamine salt having a cationic amine group, such as diallylmonomethylammonium chloride and sulfur dioxide wherein the compositions have a pH of from 1 to 4.5. 
     In front-end-of-line (FEOL) semiconductor processing, shallow trench isolation (STI) is critical to the formation of gates in integrated circuit fabrication, such as prior to formation of the transistors. In STI, a dielectric such as tetraethyl orthosilicate (TEOS) or silicon dioxide is deposited in excess in openings formed in the silicon wafer, for example, a trench or isolation area which is isolated from the remainder of the integrated circuit by silicon nitride (SiN) barrier. A CMP process is then used to remove the excess dielectric, resulting in a structure in which a predetermined pattern of the dielectric is inlaid in the silicon wafer. CMP for STI requires the removal and planarization of the silicon dioxide overburden from the isolation areas, thereby resulting in a coplanar surface with the silicon dioxide-filled trenches. In STI, the silicon nitride film surfaces must be cleared of the silicon dioxide or oxide to allow subsequent removal of the nitride hard mask in downstream processing. An acceptable oxide:nitride removal rate ratio is necessary to prevent damage to the underlying Si active areas and provide an overpolish margin to ensure all pattern densities are cleared of the oxide. Further, dishing of the oxide in any trench must be avoided to prevent low threshold voltage leaks in finished gates. 
     Presently, users of aqueous chemical, mechanical planarization polishing (CMP polishing) compositions used with CMP polishing pads to polish substrates wish to avoid the use of ceria containing CMP polishing compositions. Ceria slurries show high selectivity for silicon dioxide over silicon nitride and avoid removal of oxide in the trench area upon exposure of silicon nitride, but are costly, have issues with removal rate (RR) and process stability, and are prone to causing defects during polishing. 
     Silica slurry formulations offer lower cost, defect-free solutions, but, to date, have suffered from unsatisfactory oxide dishing control and inadequate oxide:nitride selectivity for use in STI applications. 
     U.S. Pat. No. 9,303,188 B2, to Grumbine et al. discloses a chemical mechanical polishing composition for polishing a substrate having a tungsten layer, the composition comprising a water based liquid carrier, a cationically charged colloidal silica abrasive and a polycationic amine compound in solution in the liquid carrier. The compositions may include an amine based polymer chosen from polyamines and polymers containing amine functional groups, such as diallylammonium chloride. The compositions do not exhibit acceptable oxide dishing control and inadequate oxide:nitride selectivity for use in STI applications. 
     The present inventors have endeavored to solve the problem of providing aqueous silica slurries which enable acceptable oxide dishing control and oxide:nitride selectivity for use in STI applications, as well as methods for using the slurries. 
     STATEMENT OF THE INVENTION 
     1. In accordance with the present invention, aqueous chemical mechanical planarization polishing (CMP polishing) compositions comprise a dispersion of a plurality of elongated, bent or nodular colloidal silica particles which contain a cationic nitrogen atom or a mixture thereof with a dispersion of a plurality of spherical colloidal silica particles, for example, those having for the average particle an aspect ratio of the longest dimension of the particle to its diameter which is perpendicular to the longest dimension of from 1.8:1 to 3:1, and from 0.001 to 0.5 wt. % or, preferably, from 10 to 500 ppm of a cationic copolymer of a diallylamine salt having a cationic amine group, such as a diallylammonium salt, preferably, a halide salt, such as a copolymer of diallylammonium halide and sulfur dioxide, or a copolymer of diallylalkylamine salt having a cationic amine group, such as a diallylalkylammonium halide, preferably, diallylmonomethylammonium salt, such as, preferably, a halide salt, such as, preferably, diallylmonomethylammonium chloride, and sulfur dioxide, or mixtures thereof, wherein the compositions have a pH of from 1 to 4.5 or, preferably, from 2.5 to 4.3, and, further wherein, the amount of the dispersion of the elongated, bent or nodular silica particles, ranges from 0.5 to 30 wt. %, or, preferably, from 1 to 25 wt. %, or, more preferably, from 1 to 20 wt. %, as solids, based on the total weight of the composition. 
     2. In accordance with the aqueous CMP polishing compositions as set forth in item 1, above, compositions comprise a mixture of a dispersion of a plurality of elongated, bent or nodular colloidal silica particles which contain a cationic nitrogen atom with a dispersion of a plurality of spherical colloidal silica particles, wherein the amount of the dispersion of the elongated, bent or nodular colloidal silica particles ranges from 80 to 99.9 wt. %, or, preferably, from 95 to 99.9 wt. %, based on the total solids weight of the colloidal silica particles in the compositions. 
     3. In accordance with the aqueous CMP polishing compositions as set forth in any one of items 1 or 2, above, wherein the weight average particle sizes (CPS) of the silica particles in the dispersion of silica particles or a weighted average of such particle sizes of a mixture thereof ranges from 10 nm to 200 nm, or, preferably, from 25 nm to 80 nm. 
     4. In accordance with the aqueous CMP polishing compositions as set forth in any one of items 1, 2 or 3, above, wherein the cationic copolymer of the diallylammonium salt, and sulfur dioxide comprises a copolymer of 45 to 55 mole % or, preferably, from 48 to 52 mole % of the diallylamine salt having a cationic amine group, such as a diallylammonium salt, such as, preferably, a halide salt, and from 45 to 55 mole % or, preferably, from 48 to 52 mole % of the sulfur dioxide, or the cationic copolymer of a diallylalkylamine salt having a cationic amine group, such as a diallylalkylammonium salt, or a diallylalkylammonium halide, preferably, diallylmonomethylammonium salt, such as, preferably, a halide salt, such as, preferably, diallylmonomethylammonium chloride, and sulfur dioxide comprises a copolymer of 45 to 55 mole % or, preferably, from 48 to 52 mole % of the diallylmonomethylammonium salt and from 45 to 55 mole % or, preferably, from 48 to 52 mole % of the sulfur dioxide. 
     5. In accordance with the aqueous CMP polishing compositions as set forth in any one of items 1, 2, 3, or 4, above, wherein the cationic copolymer of the diallylamine salt having a cationic amine group, preferably, a halide salt, and sulfur dioxide or the cationic copolymer of diallylalkylamine salt having a cationic amine group, preferably, a halide salt, or, more preferably, an ammonium halide, and sulfur dioxide, or the weighted average of a mixture thereof, has a weight average molecular weight of from 1,000 to 15,000 or, preferably, from 2,000 to 12,000. 
     6. In accordance with another aspect of the present invention, methods of using the aqueous CMP polishing compositions comprise polishing a substrate with a CMP polishing pad and an aqueous CMP polishing composition as set forth in any one of items 1 to 5, above. 
     7. In accordance with the methods of the present invention as set forth in item 6, above, wherein the substrate comprises both silicon dioxide or tetraethyl orthosilicate (TEOS) and silicon nitrides, as SiN or Si 3 N 4  or their mixtures, and the polishing results in an oxide:nitride removal rate ratio of at least 3:1, for example, from 3:1 to 25:1 or, preferably, from 8:1 to 18:1, for example, at least 8:1. 
     8. In accordance with the methods of the present invention for polishing a substrate as in any one of items 6 or 7, above, wherein the polishing downforce ranges from 6.9 kPa (1 psi) to 41.5 kPa (6 psi) or, preferably, from 12 kPa (1.8 psi) to 36 kPa (5.2 psi). 
     9. In accordance with the methods of the present invention for polishing a substrate as in any one of items 6, 7 or 8, above, wherein the CMP polishing composition comprises a total of from 0.5 to 5 wt. %, or, preferably, from 1 to 3 wt. %, total solids content of the dispersion of the elongated, bent or nodular colloidal silica particles, spherical colloidal silica particles, or their mixture. The CMP polishing compositions may be stored and shipped as a concentrate and then diluted with water at the time of polishing the substrate. 
     Unless otherwise indicated, conditions of temperature and pressure are ambient temperature and standard pressure. All ranges recited are inclusive and combinable. 
     Unless otherwise indicated, any term containing parentheses refers, alternatively, to the whole term as if no parentheses were present and the term without them, and combinations of each alternative. 
     All ranges are inclusive and combinable. For example, the term “a range of 50 to 3000 cPs, or 100 or more cPs” would include each of 50 to 100 cPs, 50 to 3000 cPs and 100 to 3000 cPs. 
     As used herein, the term “ASTM” refers to publications of ASTM International, West Conshohocken, Pa. 
     As used herein, the term “colloidally stable” means that a given composition does not gel or precipitate, and remains clear upon visible inspection after a given time and at a given temperature. 
     As used herein, the term “hard base” refers to metal hydroxides, including alkali(ne earth) metal hydroxides, such as NaOH, KOH, or Ca(OH) 2 . 
     As used herein, the term “ISO” refers to publications of the International Organization for Standardization, Geneva, CH. 
     As used herein, the term “Particle size (CPS)” means the weight average particle size of a composition as determined by a CPS Instruments (The Netherlands) disc centrifuge system. The particles are separated by size using centrifugal forces in a solvent and quantified using optical light scattering. 
     As used herein, the term “cationic amine group” includes a salt of amine hydroxide group that forms in aqueous media. 
     As used herein, the term “Shore D hardness” is the 2 second hardness of a given material as measured according to ASTM D2240-15 (2015), “Standard Test Method for Rubber Property, Durometer Hardness”. Hardness was measured on a Rex Hybrid hardness tester (Rex Gauge Company, Inc., Buffalo Grove, Ill.), equipped with a D probe. Six samples were stacked and shuffled for each hardness measurement; and each pad tested was conditioned by placing it in 50 percent relative humidity for five days at 23° C. before testing and using methodology outlined in ASTM D2240-15 (2015) to improve the repeatability of the hardness tests. In the present invention, the Shore D hardness of the polyurethane reaction product of the polishing layer or pad includes the Shore D hardness of that reaction product. 
     As used herein, the term “silica particle solids” or “silica solids” means, for a given composition, the total amount of spherical silica particles, plus the total amount of elongated, bent or nodular silica particles, including anything with which any of those particles are treated. 
     As used herein, the term “solids” means any material other than water or ammonia that does not volatilize in use conditions, no matter what its physical state. Thus, liquid silanes or additives that do not volatilize in use conditions are considered “solids”. 
     As used herein, the term “strong acid” refers to protic acids having a pK a  of 2 or less, such as inorganic acids like sulfuric or nitric acid. 
     As used herein, the term “use conditions” means the temperature and pressure at which a given composition is used, including increases in temperature and pressure during or as a result of use. 
     As used herein, the term “weight fraction silica” means the total wt. % of silica, based on the total weight of the composition/100%. Thus, 30 wt. % silica equates to a weight fraction of 0.3. 
     As used herein, the term “weighted average” means the average of two or more measures (e.g. average particle size or molecular weight) from different compositions (e.g. a dispersion of spherical colloidal silica particles and a dispersion of elongated colloidal silica particles) resulting from multiplying each by its solids weight fraction wherein the total solids weight fraction adds up to unity (1.00). 
     As used herein, the term “wt. %” stands for weight percent. 
     As used herein, the term “elongated, bent or nodular colloidal silica particles” refers to silica particles having, in the average particle, an aspect ratio of longest dimension to the diameter which is perpendicular to the longest dimension of from 1.8:1 to 3:1 as determined by any methods known to the ordinary skilled artisan, such as transmission electron microscopy (TEM) or as reported by a manufacturer of the dispersion of particles. 
     The present inventors have surprisingly found that an aqueous CMP polishing composition of a dispersion of elongated, bent or nodular colloidal silica particles having a cationic charge and up to 0.5 wt. %, based on the total weight of the composition, of a cationic copolymer of a diallylamine salt having a cationic amine group, such as a diallylammonium salt, or a diallylalkylamine salt having a cationic amine group, such as a diallylalkylammonium salt, for example, a diallylalkylammonium halide, preferably, a diallylmonomethylammonium salt and sulfur dioxide is particularly well-suited for planarizing or polishing a substrate, such as a silicon wafer that has undergone shallow trench isolation (STI) processing. Pressure response characterizations on blanket silicon wafers revealed that these slurries polish silicon oxide in a non-Prestonian manner: Oxide removal rate is negligible at a low down-force and increases with increasing down-force, at pressures higher than a “turn on” pressure. The x-intercept of such a non-Prestonian oxide RR (y axis) vs. down-force (x axis) curve is non-zero. The aqueous CMP polishing compositions of the present invention enable the CMP polishing of silicon dioxide with a satisfactory removal rate, and provide acceptable selectivity for silicon oxides over silicon nitrides both on blanket and pattern wafers. Most significantly, the compositions enable improved trench oxide loss and dishing over time compared to other silica slurries. 
     In accordance with the present invention, suitable colloidal silica compositions may comprise a dispersion of silica made by conventional sol gel polymerization or by the suspension polymerization of water glass so as to produce a plurality of elongated, bent or nodular silica particles in a distribution or mixture that may include spherical silica particles. 
     Suitable dispersions of elongated, bent or nodular colloidal silica particles are made from suspension polymerization by hydrolytic condensation of silanols formed in a known manner from precursors like tetraethoxysilane (TEOS) or tetramethoxysilane (TMOS). Processes for making the elongated, bent or nodular silica particles are known and can be found, for example, U.S. Pat. No. 8,529,787 to Higuchi et al. The hydrolytic condensation comprises reacting the precursors in aqueous suspension in the presence of a basic catalyst, such as an alkylammonium hydroxides, alkoxyalkyl amines, such as ethoxypropylamine (EOPA), alkylamines or KOH, preferably, tetramethylammonium hydroxide; the hydrolytic condensation process may incorporate one or more cationic nitrogen atoms into the elongated, bent or nodular silica particles. Preferably, the elongated, bent or nodular silica particles are cationic at a pH of 4 or below. 
     Suitable dispersions of bent or nodular colloidal silica particles are available from Fuso Chemical Co., Ltd., Osaka, JP (Fuso) under the tradenames HL-2, HL-3, HL-4, PL-2, PL-3 or BS-2 and BS-3 slurries. The HL and BS series particles from Fuso contain one or more nitrogen atoms which impart a cationic charge at pH 4 or below. 
     To insure colloidal stability of the aqueous CMP polishing compositions of the present invention, the compositions have a pH ranging from 1 to 4.5 or, preferably, from 2.5 to 4. The compositions tend to lose their stability above the desired pH range. The cationic diallylamine salt or diallylalkylamine salt having a cationic amine group and sulfur dioxide copolymer of the present invention aids in selectivity and in preventing dishing in polishing. Amounts of the cationic copolymer range up to 0.5 wt. %, based on the total weight of the composition. Too much of the cationic copolymer can passivate the dielectric or silica surface of the substrates. 
     The cationic copolymer of the present invention may be made by addition polymerization in the presence of or in the absence of an acid, such as hydrochloric acid or glycolic acid and a radical polymerization initiator, such as ammonium persulfate, in a polar solvent such as water. Such polymerization methods are detailed, for example, in U.S. Pat. No. 9,006,383 B2 to Yusuke et al. 
     The aqueous CMP polishing compositions of the present invention may include pH adjusters, such as inorganic acids, for example, nitric acid, or organic acids, such as citric acid. 
     The aqueous CMP polishing compositions of the present invention may comprise other cationic additives, such as polyamines, in amounts of up to 1 wt. %, based on total solids. 
     Suitable additives may also include, for example, quaternary ammonium compounds and diquaternary ammonium compounds, such as, for example, N,N,N,N′,N′,N′-hexabutyl-1,4-butanediammonium dihydroxide, 98 wt. % (Sachem, Austin, Tex.); and cationic aminosilanes, such as, for example, N-(2-aminoethyl)-3-aminopropyltrimethoxysilane, 98% (Gelest Inc., Morrisville, Pa.) or N,N-diethylaminomethyl)triethoxysilane, 98%, (Gelest Inc.). 
     Preferably, the aqueous CMP polishing compositions consist essentially of the inventive copolymer of the diallylamine salt or the diallylalkylamine salt having a cationic amine group and sulfur dioxide and the cationic abrasive and do not include materials which would further interact with the abrasive components or the copolymer. Such compositions preferably do not include diquaternary ammonium compounds that interacts with silica; and they do not include anionic compounds and nonionic surfactants that interact with the copolymer. The aqueous CMP polishing compositions may be diluted with water or with another liquid miscible with water. 
     Desirably, the CMP polishing of the present invention is carried out in STI processing with the CMP polishing composition of the invention, preferably such that the silicon nitride is not substantially removed and the silicon dioxide is adequately planarized without excessive erosion or dishing of dielectric or silicon dioxide within the trenches. 
     In use, STI processing of a wafer substrate involves providing a silicon substrate on which is deposited a layer of silicon nitride. Following photolithography, trenches are etched onto the substrate comprising an overlying layer of silicon nitride, and an excess of dielectric, for example, silicon dioxide, is deposited thereon. The substrate is then subjected to planarization until the surface layer of silicon nitride is exposed but not substantially removed, such that the dielectric or silicon oxide remaining in the trenches is approximately level with the edges of the silicon nitride. 
    
    
     EXAMPLES 
     The following examples illustrate the various features of the present invention. 
     In the Examples that follow, unless otherwise indicated, conditions of temperature and pressure are ambient or room temperature and standard pressure. 
     The following materials, including those listed in Table A, below, were used in the Examples that follow: 
     
       
         
           
               
             
               
                 TABLE A 
               
             
            
               
                   
               
               
                 Silica and Other Abrasive Particles 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                   
                   
                 Particle 
                   
                   
                 Concen- 
               
               
                 Aqueous 
                   
                   
                 size 
                   
                 Raw 
                 tration 
               
               
                 Silica 
                   
                   
                 (CPS, 
                   
                 Mate- 
                 (wt. % 
               
               
                 Slurry 
                 Source 
                 pH 3   
                 nm) 
                 Morphology 
                 rials 
                 solids) 
               
               
                   
               
               
                 Slurry A 
                 HL-3 ™ ,1   
                 7.8 
                 55 
                 Elongated, 
                 TMOS 
                 20 
               
               
                   
                   
                   
                   
                 cationic 2   
                   
                   
               
               
                   
                   
                   
                   
                 particle 
                   
                   
               
            
           
           
               
               
               
            
               
                 Slurry B 
                 Ceria 
                 (see separate listing, below) 
               
               
                   
               
               
                   1 Fuso Chemical, Osaka, JP; 
               
               
                   2 Charge determined at pH of 3.0 and cationic particles formed with TMOS and an amine containing alkaline catalyst, such as tetramethylammonium hydroxide; 
               
               
                   3 pH as delivered from source. 
               
            
           
         
       
     
     Copolymer 1 is a 1:1 copolymer of diallylammonium chloride and sulfur dioxide, having a weight average molecular weight (MW) (GPC using polyethylene glycol standards) of 5,000 as reported by manufacturer (PAS-92A, Nitto Boseke Co. Ltd, Fukushima, JP); 
     Copolymer 2 is a 1:1 copolymer of diallylmonomethylammonium chloride and sulfur dioxide, having a weight average molecular weight (MW) (GPC using polyethylene glycol standards) of 3,000 as reported by manufacturer (PAS-2201CL, Nitto Boseke Co. Ltd, Fukushima, JP); 
     Slurry B: Ceria slurry, pH 5.2, polyacrylic acid dispersant, 0.75 wt. % ceria solids undiluted, 1:3 dilution as used. 
     Slurry A is positively charged below pH 4.5. 
     The various silica particles used in the Examples are listed in Table A, above. 
     The following abbreviations were used in the Examples that follow: 
     POU: Point of use; RR: Removal rate; 
     The following test methods were used in the Examples that follow: 
     pH at POU: 
     The pH at point of use (pH at POU) was that measured during removal rate testing after dilution of the indicated concentrate compositions with water to the indicated solids content. 
     Removal Rate: 
     In a removal rate test, a Mirra™ (200 mm) polishing machine or “Mirra RR” (Applied Materials, Santa Clara, Calif.) polishing device with an IC1010™ σr other indicated CMP polishing pad (The Dow Chemical Company, Midland, Mich. (Dow)) was used to polish an STI pattern wafer substrate having a specified feature % (which corresponds to the area of active or high areas in the wafer relative to the total area thereof) with an MIT mask (SKW-3 wafers, SKW, Inc. Santa Clara, Calif.) using the CMP polishing compositions defined in Table 1, below, at a 20.7 kPa (3 psi) down-force, slurry flow rate of 150 mL/min, a 93 rpm platen speed and an 87 rpm carrier speed. During polishing, the pad was conditioned with a Kinik™ AD3CS-211250-1FN conditioning disk (Kinik Company, Taiwan) at a 3.17 kg (7 lbf) pressure, using 100% in situ conditioning. 
     Multi-Step CMP Polishing—P1 (First Step) and P2 (Subsequent Steps): 
     CMP polishing was conducted such that, in the first step or P1 process, the overburden high density plasma oxide (HDP) film was removed. The film was polished using a VP6000™ polyurethane CMP polishing pad (Dow, Shore D (2 second) hardness: 53) and Slurry E and by applying a polishing down-force of 20.7 kPa (3 psi) and platen speed of 93 rpm. P1 polishing was stopped when complete planarization was achieved on the 50% pattern density (PD) feature on the middle die of the wafer. At this point, ˜500 Å of HDP film remained on the 50% feature. On the smaller features, such as the 10% and 20% PD features, however, the HDP film was completely removed and the underlying nitride film was exposed. Features with &gt;50% PD still had significant dielectric film over the nitride film. Before moving to P2, the patterned wafer was cleaned using SP100 cleaning chemistry (TMAH containing) on a OnTrak DSS-200 Synergy™ tool (Lam Research, Fremont, Calif.) to remove ceria particles from the wafer. P2 polishing was performed using an IC™ polyurethane polishing pad (Dow, Shore D (2 second) hardness: 70) with 1010™ groove design (Dow) and the indicated slurry composition, using a polishing down-force of 20.7 kPa (3 psi) and a platen speed of 93 rpm. For the 50% pattern density feature, the polishing endpoint was defined as the time at which the HDP was cleared and the nitride film was exposed. Trench oxide loss was monitored on the 50% pattern density feature for each step-polishing event. The HDP oxide removal on the 100% pattern density feature was also measured. Overpolish is defined as the amount of HDP film removed on the 100% feature after silicon nitride was exposed on the 50% pattern density feature. Selectivity was calculated as the ratio of silicon nitride removal rate to the ratio of HDP oxide removal rate on the 100% feature. All dielectric film thicknesses and removal rates were determined by measuring the film thickness before and after polishing using a KLA-Tencor™ FX200 metrology tool (KLA Tencor, Milpitas, Calif.) using a 49 point spiral scan with a 3 mm edge exclusion. Further polishing details are set forth in Table B, below. 
     
       
         
           
               
             
               
                 TABLE B 
               
               
                   
               
               
                 Polishing Parameters 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
               
            
               
                 Pads 
                 P1: VP6000 2 mm (0.080) SIV 508 mm (20″); 
               
               
                   
                 D18AR; SG 0.8 
               
               
                   
                 P2: IC1010 2 mm (0.080) SIV 508 mm (20″); 1010; 
               
               
                   
                 SG 0.8 
               
               
                 Slurry 
                 P1: ceria Slurry E (1:3) 
               
               
                   
                 P2: Silica STI formulations 
               
               
                 Polishing 
                 20.7 kPa (3 psi), 93/87 rpm, 150 mL/min 
               
               
                 Process 
               
               
                 Polishing Tool 
                 Applied Materials Mirra ™ 
               
               
                 Thin Film 
                 KLA-Tencor ™ FX200, 49 point spiral scan w/ 3 mm 
               
               
                 Metrology 
                 edge exclusion 
               
               
                 Break-in Recipe 
                 P1: 3.17 kg (7 lbf) for 40 min 
               
               
                   
                 P2: 3.17 kg (7 lbf) for 40 min 
               
               
                 Conditioning 
                 P1: 100% in situ at 3.17 kg (7 lbf) 
               
               
                   
                 P2: 100% in situ at 3.17 kg (7 lbf) 
               
               
                 Slurry Drop Point 
                 ~9.53 cm (~3.75″) from pad center 
               
               
                   
               
            
           
         
       
     
     Polishing was continued for the indicated time intervals or to the extent of the indicated overpolish amount. In each of Tables 3, 4, and 5, below, Performance Criterion A is trench oxide loss (Å): Acceptable trench oxide loss is less than 250 Å at a 500 Å overpolish amount, preferably, less than 215 Å at 500 Å overpolish amount; Performance Criterion B is SiN loss (Å): Acceptable SiN loss is less than 200 Å at a 500 Å overpolish amount, preferably, less than 150 Å at a 500 Å overpolish amount; and Performance Criterion A is dishing (Å): Acceptable dishing is less than 200 Å at 500 Å overpolish amount, preferably, less than 175 Å at 500 Å overpolish amount. 
     Where otherwise indicated, the polished substrate was a recycled tetraethoxylsilicate (TEOS) wafer (TENR) used for blanket wafer studies. 
     
       
         
           
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                 Slurry Formulation Details 
               
            
           
           
               
               
               
               
               
            
               
                   
                   
                 Slurry/ 
                   
                   
               
               
                   
                   
                 Amount 
                   
                 pH 
               
               
                   
                   
                 (wt. % 
                 Copolymer 
                 (adjusted with 
               
               
                   
                 Slurry 
                 solids) 
                 (ppm) 
                 HNO 3 ) 
               
               
                   
                   
               
            
           
           
               
               
               
               
               
            
               
                   
                 1* 
                 A/1 
                 none 
                 3.3 
               
               
                   
                 2 
                 A/3 
                 10 ppm of 
                 3.3 
               
               
                   
                   
                   
                 copolymer 1 
               
               
                   
                 3 
                 A/3 
                 20 ppm of 
                 3.3 
               
               
                   
                   
                   
                 copolymer 2 
               
               
                   
                   
               
               
                   
                 *Denotes Comparative Example. 
               
            
           
         
       
     
     Example: Polishing Results 
     Polishing was performed using the indicated slurries listed in Table 1, above, on an STI Wafer substrate having a 50% PD feature. Polishing was conducted in multiple steps using the indicated slurry. Results are shown in Table 2, below. Performance Criterion A is trench oxide loss (Å); Performance Criterion B is SiN loss (Å); and Performance Criterion A is dishing (Å). 
     
       
         
           
               
             
               
                 TABLE 2 
               
             
            
               
                   
               
               
                 Copolymer Performance 
               
            
           
           
               
               
            
               
                   
                 Slurry 
               
            
           
           
               
               
               
               
            
               
                   
                 1* 
                 2 
                 3 
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 Performance Parameter 
                 A 
                 B 
                 C 
                 A 
                 B 
                 C 
                 A 
                 B 
                 C 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
               
            
               
                 Oxide 
                 113 
                   
                   
                   
                   
                   
                   
                 52 
                 29 
                 23 
               
               
                 Overpolish 
                 218 
                   
                   
                   
                 111 
                 54 
                 57 
                   
                   
                   
               
               
                 Amount, Å 
                 274 
                   
                   
                   
                   
                   
                   
                 127 
                 81 
                 46 
               
               
                   
                 302 
                 171 
                 51 
                 121 
                   
                   
                   
                   
                   
                   
               
               
                   
                 403 
                   
                   
                   
                 167 
                 100 
                 67 
                   
                   
                   
               
               
                   
                 433 
                   
                   
                   
                   
                   
                   
                 236 
                 145 
                 91 
               
               
                   
                 530 
                 303 
                 95 
                 208 
                   
                   
                   
                   
                   
                   
               
               
                   
                 587 
                   
                   
                   
                   
                   
                   
                 307 
                 195 
                 112 
               
               
                   
                 727 
                   
                   
                   
                   
                   
                   
                 359 
                 208 
                 150 
               
               
                   
                 730 
                   
                   
                   
                 280 
                 156 
                 124 
                   
                   
                   
               
               
                   
                 804 
                 446 
                 147 
                 299 
                   
                   
                   
                   
                   
                   
               
               
                   
                 1071 
                 609 
                 208 
                 401 
               
               
                   
               
            
           
         
       
     
     As shown in Table 2, above, copolymer 1 provides excellent polishing performance and improves all of trench oxide loss A, SiN loss B and dishing C versus the same slurry without the copolymer in Comparative Example 1. 
     Compared to the composition of Comparative Example 1*, the compositions of Examples 2 and 3 show better dishing and trench oxide loss.