Patent Publication Number: US-2011059401-A1

Title: Method for preparing lithographic printing plates

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS  
     This application is a 371 National Stage Application of PCT/EP2009/053355, filed Mar. 23, 2009. This application claims the benefit of U.S. Provisional Application No. 61/039,442, filed Mar. 26, 2008, which is incorporated by reference herein in its entirety. In addition, this application claims the benefit of European Application No. 08102922.5, filed Mar. 26, 2008, which is also incorporated by reference herein in its entirety. 
    
    
     BACKGROUND OF THE INVENTION  
     1. Field of the Invention 
     The present invention relates to a method of preparing a photopolymer printing plate. 
     2. Description of the Related Art 
     In lithographic printing, a so-called printing master such as a printing plate is mounted on a cylinder of the printing press. The master carries a lithographic image on its surface and a printed copy is obtained by applying ink to the image and then transferring the ink from the master onto a receiver material, typically paper. In conventional, so-called “wet” lithographic printing, ink as well as an aqueous fountain solution (also called dampening liquid) are supplied to the lithographic image consisting of oleophilic (or hydrophobic, i.e. ink-accepting, water-repelling) areas as well as hydrophilic (or oleophobic, i.e. water-accepting, ink-repelling) areas. In so-called “driographic” printing, the lithographic image consists of ink-accepting and ink-abhesive (ink-repelling) areas and during driographic printing only ink is supplied to the master. 
     The so-called “analogue” printing plates are generally obtained by first applying a so-called computer-to-film (CtF) method, wherein various pre-press steps such as typeface selection, scanning, color separation, screening, trapping, layout and imposition are accomplished digitally and each color selection is transferred to graphic arts film using an image-setter. After processing, the film can be used as a mask for the exposure of an imaging material called plate precursor and after plate processing, a printing plate is obtained which can be used as a master. Since about 1995, the so-called “computer-to-plate” (CtP) method has gained a lot of interest. This method, also called “direct-to-plate”, bypasses the creation of film because the digital document is transferred directly to a printing plate precursor by means of a plate-setter. A printing plate precursor for CtP is often called a digital plate. 
     Digital plates can roughly be divided in three categories: (i) silver plates, working according to the silver salt diffusion transfer mechanism; (ii) photopolymer plates containing a photopolymerizable composition that hardens upon exposure to light and (iii) thermal plates of which the imaging mechanism is triggered by heat or by light-to-heat conversion. 
     Photopolymer plate precursors can be sensitized for blue, green or red light (i.e. wavelength range between 450 and 750 nm), for violet light (i.e. wavelength range between 350 and 450 nm) or for infrared light (i.e. wavelength range between 750 and 1500 nm). Lasers have become the predominant light source used to expose photopolymer printing plate precursors. Typically, an Ar laser (488 nm) or a FD-YAG laser (532 nm) can be used for exposing a visible light sensitized photopolymer plate precursor. The wide-scale availability of low cost blue or violet laser diodes, originally developed for data storage by means of DVD, has enabled the production of plate-setters operating at shorter wavelength. More specifically, semiconductor lasers emitting from 350 to 450 nm have been realized using an InGaN material. For this reason, photopolymer plates having their maximal sensitivity in the 350 nm to 450 nm region have been developed during the last years. An advantage of violet photopolymer technology is the reliability of the laser source and the possibility of handling the non-developed photopolymer plate precursors in yellow safelight conditions. The use of infrared lasers also became more important in the last years, for example the Nd-YAG laser emitting around 1060 nm but especially the infrared laser diode emitting around 830 nm. For these laser sources, infrared sensitive photopolymer plate precursors have been developed. The major advantage of infrared photopolymer technology is the possibility to handle the non-developed photopolymer plate precursors in daylight conditions. 
     After exposure of a photopolymer plate precursor a rather complex processing is typically carried out. A pre-heat step is usually carried out to enhance the polymerization and/or crosslinking in the imaged areas. Then during a pre-wash step, typically with plain water, the protective layer of the photopolymer plate precursor is removed. After the pre-wash step the non-imaged parts are removed in a development step, typically with an alkaline developer having a pH&gt;10. After the development step, a rinse step, typically with plain water, and a gumming step is carried out. Gumming protects the printing plate during the time between development and printing against contamination for example by oxidation, fingerprints, fats, oil or dust, or against damage, for example during handling of the plate. Such processing of photopolymer plates is usually carried out in automatic processors having a pre-heat section, a pre-wash section, a development section, a rinse and gum section and a drying section. 
     To avoid this complex, time consuming and environmentally unfriendly processing of photopolymer plate precursors several alternatives have been described. 
     In U.S. Pat. No. 6,027,857, U.S. Pat. No. 6,171,735, U.S. Pat. No. 6,420,089, U.S. Pat. No. 6,071,675, U.S. Pat. No. 6,245,481, U.S. Pat. No. 6,387,595, U.S. Pat. No. 6,482,571, U.S. Pat. No. 6,576,401 and U.S. Pat. No. 6,548,222 a method is disclosed for preparing a lithographic printing plate wherein a photopolymer plate precursor, after image-wise exposure, is mounted on a press and processed on-press by applying ink and fountain solution to remove the unexposed areas from the support. Also US 2003/16577 and US 2004/13968 disclose a method wherein a plate precursor including a photopolymerizable layer can be processed on-press with fountain solution and ink or with a non-alkaline aqueous developer. 
     In WO 2005/111727 a method is disclosed wherein a photopolymer plate precursor is developed by applying a gum solution to the plate. The gum solution, for example a gum solution used in the gumming step of a conventional processing method, is used for both developing, i.e. removing the non-imaged parts of the coating, and gumming the exposed photopolymer plates. So, according to this method, no pre-wash step, no rinse step and no additional gum step is needed anymore during processing. This method provides a simplified processing of photopolymer plate precursors and in addition, since on the one hand no highly alkaline developer is used anymore and on the other hand much less processing liquids are used altogether (no pre-wash, no rinse and no separate gum), provides an environmentally more friendly processing. WO 2007/057334 also discloses a method to prepare photopolymer plates wherein the development is carried out in a gum solution. However, in this method a pre-wash is carried out before development with the gum solution. Other methods, all using a gum solution to develop photopolymer plates, are disclosed in for example WO 2007/057335 and WO 2007/057349. WO 2007/057348 and WO 2007/057336 disclose a method wherein a gum solution is used to develop a photopolymer plate and wherein a pre-heat step is carried out after exposure and before development. In WO 2007/057336, the pre-heat section and the development section are combined in one single apparatus. Development with the gum solution in the above mentioned methods is usually carried out at room temperature. 
     A problem observed with a method of preparing photopolymer plates wherein immediately after a pre-heat step development is carried out with a gum solution, especially when both pre-heat and development are combined in one single apparatus, is an inconsistency of the lithographic properties of the obtained printing plates. While not changing the exposure conditions, it has been observed that when a substantial number of photopolymer plates are produced, the individual plates may have different properties such as different dot rendering, especially in the highlights, and a different press life. 
     It has now been found that this inconsistency is the result of fluctuations of the temperature of the gum solution. When the time between pre-heat and development is limited, as in practical conditions, the pre-heated printing plates upon entering the gum solution increase the temperature of the gum solution. When several printing plates are processed within a short time, such an increase in temperature of the gum solution may become substantial, for example more than 10° C. and even up to 20° C. During the time wherein no printing plates are produced the temperature of the gum solution will decrease again. These fluctuations in temperature may give rise to inconsistent lithographic properties of the obtained printing plates, which is of course unacceptable in practice. 
     In conventional processing of photopolymer plate precursors, this problem is not observed since the pre-heated printing plates are first subjected to a pre-wash before entering the developing section. 
     Typically conventional processors have some means, present in the development section, to control the temperature of the developer, i.e. heating elements to increase and cooling means to decrease the temperature of the developer. These conventional means are however not sufficient to control the temperature of the developer when the printing plate precursor, after pre-heat, immediately enters the developer, i.e. without carrying out a pre-wash. Providing conventional processors with more efficient means in the development section to cope with the increases in temperature as described above due to the absence of a pre-wash between pre-heat and development of the printing plate precursor, would result in a substantial increase in cost price of such conventional processors. 
     SUMMARY OF THE INVENTION  
     A preferred embodiment of the present invention provides a method of preparing photopolymer printing plates wherein after a pre-heat step the printing plate precursors are developed with a gum solution with which printing plates having consistent lithographic properties are obtained. 
     This is realised by methods described below wherein between the pre-heat step and the development step an accelerated cooling of the printing plate precursor is carried out. 
     Other preferred embodiments of the present invention are defined below. 
     The above and other elements, features, steps, characteristics and advantages of the present invention will become more apparent from the following detailed description of the preferred embodiments with reference to the attached drawing. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS  
         FIG. 1  is a schematic drawing of an embodiment of an automatic processor adapted to be used in the method of preparing printing plates according to the present invention. 
     
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS  
     The present invention provides a method of preparing a lithographic printing plate including the steps of: 
     providing a lithographic printing plate precursor, the precursor including a photopolymerizable coating provided on a hydrophilic support; 
     image-wise exposing the precursor; 
     pre-heating the exposed precursor; 
     developing the exposed precursor in a gum solution; 
     characterized in that after pre-heating and before developing the precursor an accelerated cooling of the precursor is carried out and the cooling does not essentially remove a part of the coating of the precursor. 
     Pre-Heat  
     Providing a pre-heat step after exposure and before processing of a photopolymer printing plate precursor is well known in the art. The pre-heat treatment accelerates the polymerization and/or crosslinking in the imaged parts of the precursor, thereby increasing the durability and improving the uniformity of the hardness of the imaged parts. This may result in an increased run length, i.e. number of high quality prints that can be made with a single printing plate. During pre-heat, the plate is typically kept at a plate surface temperature, measured on the back side of the plate, ranging from 70° C. to 150° C. for a period of one second to 5 minutes, preferably from 80° C. to 140° C. for 5 seconds to 1 minute, more preferably from 90° C. to 130° C. for 10 seconds to 30 seconds. The back side of the plate is that side of the support that is opposite to the side of the support whereupon the photopolymerizable coating is applied. 
     The time between exposure and pre-heat is preferably less than 10 minutes, more preferably less than 5 minutes, most preferably less than 1 minute. There is no particular time limit before the pre-heat may start after exposure. Typically, the pre-heat is carried out as soon as possible after exposure, i.e. within the time needed to transport the plate from the exposure unit to the pre-heat section. 
     Examples of heating devices that may be used in the pre-heat section include a conventional convection oven, IR lamps, UV lamps, an IR laser, IR tiles, a microwave apparatus or heated rollers, for example metal rollers. 
     The temperature values referred to above are measured on the back side of the plate. During the pre-heat treatment, especially when using IR tiles, temperatures at the surface of the coating may reach substantially higher values. 
     To minimize the rise in temperature of the developing solution, due to the pre-heat immediately before development, a moderate pre-heat may be used in a preferred embodiment of the present invention. Such a moderate pre-heat may be carried out at a plate surface temperature ranging from 30° C. to 90° C., more preferably from 40° C. to 80° C., most preferably from 50° C. to 70° C. To enable the use of such a moderate pre-heat treatment and still realize a sufficient press life of the obtained printing plate, an especially designed printing plate precursor may be used, for example including adhesion promoting agents as disclosed in WO 2007/057333 or including a binder having a low Tg as disclosed in EP-A 1 757 981. 
     Accelerated Cooling  
     The accelerated cooling referred to in the present invention means that the printing plate precursor upon leaving the pre-heat section is cooled at a higher rate than under ambient conditions. This implies the use of special devices to obtain such an accelerated cooling. The cooling does not essentially remove a part of the coating of the precursor. Preferably at most 25%, more preferably at most 10%, most preferably at most 5%, particularly preferred none of the coating is removed during the accelerated cooling. 
     A preferred way of achieving the accelerated cooling is the use of an air flow. The air flow may be directed on the top side or on the back side of the plate precursor or on both. The air may have the ambient temperature or may be cooled, i.e. having a temperature that is less than the ambient temperature. Any device capable of generating an air flow on the plate precursor may be used. The air flow may be directed on the plate precursor by an air knife, one or more air fans or one or more air nozzles. When cooling is carried out with ambient air, the source of which is situated within the processor housing, the cooling may become less effective as more and more plates are processed consecutively, since the ambient air within the processor housing may increase in temperature. It is therefore preferred to use air from outside the processor housing for the accelerated cooling. 
     Another way to achieve the accelerated cooling is contact cooling for example by cooled transport rollers or by contacting the precursor with a cooled platen. Such a contact cooling may be incorporated in an automatic processor between the pre-heat and the development section. The cooled transport rollers or platen may contact the top side or the back side of the plate precursor or both. The rollers may be cooled by circulating a fluid through the inside of the rollers or by contacting their outer side with a fluid, preferably a circulating fluid. The fluid may have ambient temperature or a lower temperature. 
     Still another manner to achieve the accelerated cooling is applying, for example spraying, jetting or coating, a fluid on the plate precursor. It is preferred that the coating of the printing plate precursor does not substantially dissolve in the cooling fluid used. Again, the fluid may be applied on the top side or on the back side of the plate precursor or on both. The applied fluid may be at ambient temperature or may be at a temperature lower than ambient temperature. The fluid may be for example a low boiling solvent. Either the lower temperature and/or the evaporation of such a low boiling solvent may induce accelerated cooling. The applied fluid may not have an adverse effect on the lithographic properties of the obtained printing plates. The fluid may preferably be collected after application to the plate and reused. 
     Liquid nitrogen may be used in the accelerated cooling. It may be applied as a liquid on the plate precursor, upon which it will immediately evaporate, or as a vapour. 
     Still another method to achieve accelerated cooling is applying a solid having a temperature lower than ambient temperature on the plate precursor, for example dry ice, i.e. solid CO 2 . When dry ice is used, upon applying it on the plate precursor it will sublime. Dry ice vapour may also be used to cool the plate precursor. 
     Different devices described above to achieve an accelerated cooling may be combined. Depending on the number of plates produced within a given time interval, a different cooling device or a combination of different cooling devices may be necessary. 
     Preferably the accelerated cooling results in a temperature of the plate precursor, just before entering the developing section, that corresponds with the temperature of the gum solution used to develop the plate precursor. Preferably the accelerated cooling results in a temperature of the precursor, just before entering the developing section, of not higher than 50° C., more preferably not higher than 40° C., most preferably not higher than 30° C. 
     Development  
     Development is carried out with a gum solution. During development, an optional overcoat and the non-imaged areas of an image-recording layer are removed. Development is preferably carried out in an automatic processor using spray or dip development. Spray development involves spraying a developing solution on the plate precursor, for example with one or more spray bars. Dip development involves immersion of the plate into a developing solution. The development may be a batch development, i.e. development is carried out with a batch of developer until development is no longer sufficient. At that moment a new batch of developer is introduced in the processor. Development may also be carried out with regeneration of the developer, whereby a given amount of fresh developer is added to the development solution as function of the number of plates already developed. The composition and/or concentration of the fresh developer added during regeneration may be the same or different to that of the initial developer. 
     The developing step with the gum solution may be combined with mechanical rubbing, preferably by one or more rotating brushes, to better remove the non-imaged parts of an image-recording layer. Preferred rotating brushes are described in US 2007/0184387 (paragraphs [0255] to [0257]) and EP-A 1 755 002 (paragraphs [0025] to [0034]). Good results may also be obtained with “flat” brushes. These “flat” brushes may have a width of for example 5.0 to 10 cm and may be equipped with polypropylene or nylon bristles. The length of the bristles may be from 5 to 15 mm. Typically, these “flat” brushes are rubbing the plate precursor by moving back and forth in a direction perpendicular to the plate conveying direction through the processor. Rubbing may be realized by up to 120 movements per minute. 
     A gum solution is essentially an aqueous solution including a surface protective compound capable of protecting the lithographic image of a printing plate against contamination. Suitable examples of such compounds are film-forming hydrophilic polymers or surfactants. A layer that remains on the plate after development with the gum solution preferably includes more than 0.01 g/m 2  of a surface protective compound. 
     The gum solution may be supplied as a ready-to-use developer or as a concentrated solution, which is diluted by the end user with water to a ready-to-use developer according to the instructions of the supplier: typically 1 part of the gum is diluted with 1 to 10 parts of water. 
     A preferred composition of the gum solution is disclosed in WO 2005/111727 (page 6, line 5 to page 11, line 35) and EP-A 1 621 339 (paragraphs [0014] to [0061]). 
     Preferred surfactants are for example block copolymers based on ethylene oxide and propylene oxide such as the commercially available PLURONIC® surfactants such as PLURONIC 9400. Other preferred surfactants are tristyrylphenol ethoxylates such as the EMULSOGEN® surfactants, for example EMULSOGEN TS160 or TS200. Highly preferred, a combination of both these surfactants is used. 
     Besides the surface protective compound the gum solution preferably includes a salt formed by reaction of an acid, containing a phosphorous atom, with a di- or tri-alkanolamine as disclosed in the unpublished EP-A 07 108 228.3 (filed on 2007 May 15). 
     Development is typically carried out at temperatures of the developing solution between 20° C. and 50° C., preferably between 20° C. and 40° C., most preferably between 20° C. and 30° C. In the method according to a preferred embodiment of the present invention, the temperature of the developing solution changes preferably not more than 15° C., more preferably not more than 10° C., most preferably not more than 5° C. 
     When the time between the preparation of the printing plate and mounting that printing plate on a press to start printing is sufficiently short so that no severe contamination may take place, the development may be carried out with any aqueous solution having preferably a pH between 3 and 9, even plain water. Also commonly used press room chemicals, for example fountain solutions or aqueous plate cleaners and/or conditioners may be used, if necessary after proper dilution. 
     Processing Apparatus  
     The method of a preferred embodiment of the present invention includes a pre-heat step and a development step characterized in that after pre-heating and before developing the precursor an accelerated cooling of the precursor is carried out. Preferably these steps are integrated in a dedicated automatic processor. Such a dedicated processor, essentially including a pre-heat section, an accelerated cooling section, a development section and a drying section, is compared to conventional processors of photopolymer plates, less complex and needs less floor space. 
     In  FIG. 1 , a schematic drawing of an embodiment of an automatic processor adapted to be used in the method of preparing printing plates according to a preferred embodiment of the present invention is shown. 
     The automatic processor has four sections: section A is the pre-heat section; section B is the accelerated cooling section; section C is the developing section and section D is the drying section. An exposed printing plate precursor is automatically transported between the different sections, starting with the pre-heat section A. According to another embodiment, an exposure unit may also be incorporated in the automatic processor, i.e. an exposure section before the pre-heat section. 
     In the development section C, the precursor is developed in a dip tank using a gum solution E. The solution is typically kept at room temperature, but a higher temperature such as 30° C. or 40° C., may also be implemented by means of proper heating elements. 
     Between the development section C and the pre-heat section A an accelerated cooling section B is provided to enable an accelerated cooling of the pre-heated precursor before entering the development section C. In this cooling section, the cooling devices described above are implemented. 
     After the development section C, a drying section D is provided to ensure that the printing plates are substantially dry upon leaving the automatic processor. Any conventional drying device, at present used in conventional processing units may be used in the drying section. 
     As described above, an especially adapted automatic processor has some advantages over a conventional photopolymer processor, i.e. is less complicated and requires less floor space. However, since a lot of conventional processors are available on the market, these processors may also be used to carry out the methods of the present invention, after proper adaptation. A conventional processor includes a pre-heat section, a pre-wash section, a developing section, a rinse and gum section and a drying section. To adapt such a processor to the present invention, the pre-wash section and/or the rinse and gum section may be deactivated. An accelerated cooling is carried out between the pre-heat section and the development section. 
     It has been observed that when a conventional processor is adapted to carry out the methods of the present invention, transport rollers in contact with the top side of the plates, i.e. the side carrying a photopolymerizable coating, running dry and positioned after the development section, for example between the development section and the non-active rinse and gum section, may adversely influence the quality of the obtained printing plates. To avoid such problems, those rollers may be wetted by applying water or preferably a gum solution, most preferably the same gum solution used as developer, to those rollers. The solution may be applied to the rollers with a spray bar and collected in a drip tank/tray and reused. The solution may be applied directly onto the rollers or via an additional contact roller. Such a contact roller may supply the solution to more than one transport rollers. 
     Photopolymer Printing Plate Precursor  
     Any photopolymer printing plate precursor capable of being developed with a gum solution may be used in the present invention. The photopolymer printing plate precursors are preferably sensitized for violet light, i.e. for light having a wavelength ranging from 350 nm to 450 nm, or for infrared light, i.e. light having a wavelength ranging from 750 nm to 1500 nm. 
     A typical photopolymer printing plate precursor typically includes a photopolymerizable coating provided on a hydrophilic support. 
     The support is preferably a grained and anodized aluminum support, well known in the art. Suitable supports are for example disclosed in EP-A 1 843 203 (paragraphs [0066] to [0075]). The grained and anodized aluminum support may be subjected to so-called post-anodic treatments, for example a treatment with polyvinylphosphonic acid or derivatives thereof, a treatment with polyacrylic acid, a treatment with potassium fluorozirconate or a phosphate, a treatment with an alkali metal silicate, or combinations thereof. Besides an aluminum support, a plastic support, for example a polyester support, provided with one or more hydrophilic layers may also be used. 
     The coating provided on a hydrophilic support includes a photopolymerizable layer, also referred to as the image-recording layer. The coating may further include an overcoat and/or an undercoat, the latter also referred to as an intermediate layer or an interlayer. 
     The overcoat, provided on the photopolymerizable image-recording layer, also referred to as a toplayer or a protective layer, acts as an oxygen barrier layer. Preferred binders which can be used in the top layer are disclosed in WO 2005/029190 (page 36 line 3 to page 39 line 25), US 2007/0020563 (paragraph [0158]) and EP 1 288 720 (paragraphs [0148] and [0149]). The most preferred binders for the overcoat are polyvinylalcohol and polyvinylpyrrolidone. 
     The photopolymerizable layer or image-recording layer typically includes at least one polymerizable monomer or oligomer, at least one polymeric binder, a photo-initiator and a sensitizer. The photo-initiator-sensitizer system is choosen as function of the exposure wavelength. The photopolymerizable layer may further include a contrast dye or pigment, a polymerization inhibitor, a chain transfer agent, adhesion promoting agents interacting with the aluminum surface and other ingredients which may further optimize the properties of the printing plate precursors. 
     The coating may also include one or more intermediate layers, provided between the photopolymerizable image-recording layer and the support. Such an intermediate layer may further optimize the interaction between the image-recording layer and the support, i.e. enable the complete removal of non-imaged parts and a sufficient adhesion of the imaged parts of the image-recording layer. 
     Preferred violet sensitive printing plate precursors are disclosed in WO 2005/111727, WO 2005/029187, WO 2007/113083, WO 2007/057333, WO 2007/057442 and the unpublished EP-As 07 108 955, 07 108 957 and 07 108 953, all filed on 25 May 2007. Other violet sensitive printing plate precursors that may be used in the method of the present invention are those disclosed in EP-A 1 793 275, US 2007/0184387 and EP-A 1 882 585. 
     Preferred IR sensitive printing plate precursors are disclosed in WO 2005/111727, EP-As 1 788 448 and 1 788 449 and the unpublished EP-A 07 120 845 (filed on 2007 Nov. 16). Other IR sensitive printing plate precursors that may be used in the method of the present invention are those disclosed in EP-As 1 602 982, 1 621 339, 1 630 618 and 1 695 822. 
     EXAMPLES  
     Materials  
     All materials used in the examples were readily available from standard sources such as Aldrich Chemical Co. (Belgium) and Acros (Belgium) unless otherwise specified. 
     PVA-1: partially hydrolyzed poly(vinyl alcohol); degree of saponification is 88 mol %; viscosity of a 4 wt % aqueous solution at 20° C. is 4 mPa·s; available as MOWIOL 4/88 from Kururay. 
     PVA-2: fully hydrolyzed poly(vinyl alcohol); degree of saponification is 98 mol %; viscosity of an aqueous solution of 4 wt % at 20° C. is 4 mPa·s; available as MOWIOL 4/98 from Kururay. 
     Acticide: Acticide LA 1206, a biocide commercially available from THOR. 
     Lutensol A8: 90 wt % solution of a surface active agent, commercially available from BASF. 
     Advantage S: a vinylpyrrolidone-vinylcaprolactam-dimethyl-aminoethyl methacrylate copolymer commercially available from ISP. 
     FST426R: a solution containing 88.2 wt % of a reaction product from 1 mole of 2,2,4-trimethyl-hexamethylenediisocyanate and 2 moles of hydroxyethylmethacrylate (kinematic viscosity 3.30 mm 2 /s at 25° C.). 
     Mono Z1620: a solution in MEK containing 30.1 wt % of a reaction product from 1 mole of hexamethylenediisocyanate, 1 mole of 2-hydroxyethylmethacrylate and 0.5 mole of 2-(2-hydroxyethyl-piperidine (kinematic viscosity 1.7 mm 2 /s at 25° C.). 
     Heliogene Blue: dispersion in Dowanol PM/MEK/γ-butyrolactone containing 5 wt % of Heliogen blau D7490 pigment and 2.5 wt % of KL7177 and 2.5 wt % KOMA30 NEU as dispersants. Heliogen blau D7490 is commercially available from BASF. 
     KL7177, methacrylic acid-metylmethacrylate copolymer, commercially available from Clariant. 
     Hostanox 03: a phenolic antioxidant, commercially available from CLARIANT. 
     HABI: 2-(2-chlorophenyl)-4,5-diphenyl bisimidazole, commercially available from SUMITOMO. 
     MBT: 2-mercaptobenzthiazole. 
     Tegoglide 410: a polydimethylsilixane-polyether surfactant commercially available from GOLDSCHMIDT. 
     Sensitizer: a violet sensitizer mixture consisting of the following compounds: 
     
       
         
         
             
             
         
       
     
     Texapon 842: sodium octylsulphate commercially available from COGNIS. 
     Emulsogen TS160: a 2,4,6-tris-(1-phenylethyl)-polyglycolether having approximately 15 ethyleneoxyde units, commercially available from CLARIANT. 
     Dowanol PM: methoxy propanol, commercially available from DOW CHEMICAL COMPAGNY. 
     Dowanol PPH: phenoxy isopropanol, commercially available from DOW CHEMICAL COMPAGNY. 
     MEK: methylethylketone. 
     Triethanolamine, commercially available from BASF. 
     Dextrine, commercially available from ROQUETTE FRERES. 
     H 3 PO 4 , commercially available from MERCK. 
     KOMA30 NEU, copolymer consisting of 64 mol % vinyl butyral—26 mol % vinyl alcohol—2 mol % vinyl acetate—8 mol % esterification product of vinylalcohol and trimellitic acid anhydride. 
     Support 
     A 0.3 mm thick aluminum foil was degreased by spraying with an aqueous solution containing 26 g/l NaOH at 65° C. for 2 seconds and rinsed with demineralised water for 1.5 seconds. The foil was then electrochemically grained during 10 seconds using an alternating current in an aqueous solution containing 15 g/l HCl, 15 g/l SO4 2−  ions and 5 g/l Al 3+  ions at a temperature of 37° C. and a current density of about 100 A/dm 2 . Afterwards, the aluminum foil was desmutted by etching with an aqueous solution containing 5.5 g/l NaOH at 36° C. for 2 seconds and rinsed with demineralised water for 2 seconds. The foil was subsequently subjected to anodic oxidation during 15 seconds in an aqueous solution containing 145 g/l of sulfuric acid at a temperature of 50° C. and a current density of 17 A/dm 2 , then washed with demineralised water for 11 seconds and post-treated for 3 seconds (by spray) with a solution containing 2.2 g/l PVPA at 70° C., rinsed with demineralised water for 1 seconds and dried at 120° C. for 5 seconds. 
     The support thus obtained was characterised by a surface roughness Ra of 0.35-0.4 μm (measured with interferometer NT1100) and had an anodic weight of 3.0 g/m 2 . 
     Photopolymerizable Layer  
     The photopolymerizable layer was prepared by coating a solution of the ingredients listed in Table 1 in a DOWANOL PM/MEK (62/38) mixture on the above described support. The wet coating thickness was 20 μm. After drying, a dry coating weight of 1.2 g/m 2  was obtained. The dry amounts after coating of the ingredients are shown in Table 1. 
     
       
         
           
               
               
               
             
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                 Ingredients 
                 g/m 2   
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
            
               
                   
                 Tegoglide 410 
                 0.0012 
               
               
                   
                 Sensitizer 
                 0.0516 
               
               
                   
                 FST426R 
                 0.1369 
               
               
                   
                 Mono Z1620 
                 0.4931 
               
               
                   
                 Heliogene Blue 
                 0.0960 * 
               
               
                   
                 Hostanox 03 
                 0.0006 
               
               
                   
                 HABI 
                 0.0780 
               
               
                   
                 MBT 
                 0.0036 
               
               
                   
                 KOMA30 NEU 
                 0.3390 
               
               
                   
                   
               
               
                   
                 * pigment + dispersants 
               
            
           
         
       
     
     Preparation of the Overcoat Layer  
     The overcoat layer, also referred to as the top layer, was applied on the photopolymerizable layer described above from an aqueous solution, containing the ingredients listed in Table 2. The wet coating thickness was 45 μm. After drying at 110° C. for 2 minutes a dry coverage weight of 1.16 g/m 2  was obtained. The dry amounts, after coating, of the ingredients of the overcoat layer are shown in Table 2. 
     
       
         
           
               
               
               
             
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                 Ingredients 
                 g/m 2   
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
            
               
                   
                 PVA-1 
                 0.7106 
               
               
                   
                 PVA-2 
                 0.4284 
               
               
                   
                 Acticide 
                 0.0020 
               
               
                   
                 Advantage S 
                 0.0116 
               
               
                   
                 Lutensol A8 
                 0.0089 
               
               
                   
                   
               
            
           
         
       
     
     Processing of the Printing Plate Precursors  
     The above described printing plate precursor was developed in an automatic processor unit having a pre-heat section, an optional cooling section, a development section and a drying section. To simulate practical conditions, every 2 seconds a printing plate precursor was processed. These conditions simulate, for example, practical conditions used in the newspaper business. The dip tank of the development section was filled with the developing solution having the composition as outlined in Table 3. 
                                 TABLE 3                       Ingredients   g/l                                                    Texapon 842   9.00           Emulsogen TS160   17.50           H 3 PO 4     2.60           Dowanol PPH   10.00           Triethanolamine   7.40           Dextrine   25.00           Water   928.50           pH   6.5-7.5                        
At the start of the experiment, the temperature of the developer was room temperature.
 
     In Table 4, the temperature of the developer is given as a function of the amount of printing plate precursors developed, both for an apparatus with an active and an inactive accelerated cooling section. Cooling in the cooling section was realized by blowing air having ambient temperature from outside the processor housing with an air knife over the printing plate precursors, between the pre-heat section and the development section. All precursors had a size of 745 mm×605 mm and a thickness of 0.30 mm (the precursors were processed in the 605 mm direction). The amount of developer used was 40 liter, the processing speed was 1.2 m/min. The pre-heat temperature, measured on the back side of the precursors with strips available from Thermographic Measurements Ltd, was 110° C. 
     The dwell time between exit from the pre-heat section and entrance in the development section was 12 seconds. 
     
       
         
           
               
               
             
               
                 TABLE 4 
               
             
            
               
                   
               
               
                 # Printing 
                 Temperature developing solution (° C.) 
               
            
           
           
               
               
               
            
               
                 plates 
                 Inactive cool 
                 Active cool  
               
               
                 processed 
                 section 
                 section 
               
               
                   
               
            
           
           
               
               
               
            
               
                 0 
                 23.6 
                 23.6 
               
               
                 20 
                 25.5 
                 25.0 
               
               
                 40 
                 28.2 
                 27.0 
               
               
                 60 
                 30.1 
                 28.3 
               
               
                 80 
                 31.5 
                 29.5 
               
               
                 100 
                 32.9 
                 30.5 
               
               
                 120 
                 34.7 
                 31.3 
               
               
                   
               
            
           
         
       
     
     From Table 4 it is clear that the temperature of the developing solution increases upon processing of a substantial amount of precursors within a short time interval. 
     From Table 4 is also clear that the temperature of the developing solution rises to a lesser extent when an active cooling section is provided. Since lithographic properties depends on the temperature of the developing solution, a rise of the temperature to a lesser extent results in more consistent lithographic properties of the printing plate so obtained. 
     While preferred embodiments of the present invention have been described above, it is to be understood that variations and modifications will be apparent to those skilled in the art without departing the scope and spirit of the present invention. The scope of the present invention, therefore, is to be determined solely by the following claims.