Patent Publication Number: US-2019185664-A1

Title: Polycarbonate-polycarbonate/polysiloxane compositions having high flow, high impact, and good release properties

Description:
TECHNICAL FIELD 
     The present disclosure pertains to polycarbonate compositions designed to have high flow, high impact, and good release properties. 
     BACKGROUND 
     Trends in plastic part design are driving toward more thin, more complex parts with advanced styling. Materials with good flow and sufficient release are required to achieve such a narrow and complex structure with enhanced styling, while also maintaining high impact performance. 
     These and other shortcomings are addressed by aspects of the present disclosure. 
     SUMMARY 
     The disclosure concerns thermoplastic compositions containing a polycarbonate-siloxane copolymer comprising: from about 49.5 wt % to about 97.95 wt % of at least one polycarbonate polymer; from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer in an amount effective to provide a total siloxane content of about 1.0 wt % to about 5.0 wt % based on the total weight of the thermoplastic composition; and from about 0.05 wt % to about 1.0 wt % of at least one release agent. The thermoplastic composition exhibits a melt volume flow rate (MVR) of at least about 25 cubic centimeters per 10 minutes (cm 3 /10 min), as determined according to ISO 1133 at 300 degrees Celsius (° C.) using a 1.2 kilogram (kg) load. The thermoplastic composition also has a ductile/brittle transition temperature of less than or equal to 10° C. as determined in accordance with ISO 180-1A on a molded part having a thickness of 3 millimeters (mm). The thermoplastic composition further has good retention of high gloss after metallization with an increase in L* of about 30% or less compared to a reference thermoplastic composition without the polycarbonate-siloxane copolymer, as measured according to ASTM D1729 on a 3 mm thick metallized plaque in reflectance and specular excluded mode. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  shows applications for bezels, reflectors housings or box shapes which require high aesthetic gloss surfaces-parts which can normally only be molded by applying strictly the plastic design rules. 
         FIGS. 2 and 3  illustrate the unique combination of high flow and improved release characteristic that enables box, reflectors, housing or bezel designs with lower draft angles and larger ribs due to more rectangular walls with minimum release angle. 
         FIG. 4  illustrates how increased draft angle increases part dimension. 
         FIG. 5  shows an exemplary apparatus used for determining mold release force. The units 40, 30 and 20 are in millimeter (mm). 
         FIG. 6  shows an exemplary apparatus used for determining coefficient of friction. 
     
    
    
     DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS 
     For some applications in the market that require low temperature impact performance, blends of polycarbonate/polysiloxanes are used because compositions including these blends may have high impact and good aesthetics in addition to very good release properties compared with normal polycarbonate. Current commercial products are based on a blend of polycarbonate and a polysiloxane copolymer in different ratios; depending on these ratios, the properties of the final product, such as release performance, can vary. 
     It has been surprisingly found that blends including (i) a polycarbonate-siloxane copolymer in an amount effective to provide a total siloxane content of about 1.0 wt % to about 5.0 wt % based on the total weight of the blend and (ii) at least one polycarbonate have an improved balance of high flow, high impact at room temperature and lower temperatures, compared to substantially similar compositions without the polycarbonate-siloxane or polycarbonates with alternative impact modifiers, such as acrylic or silicone based core-shell rubbers. In addition, these compositions demonstrate good retention of high gloss after metallization and good retention of tensile properties after prolonged exposure to chemicals like sunscreen. 
     Thermoplastic Compositions 
     The disclosed thermoplastic compositions can exhibit, for example, improved mechanical, or impact, thermal, or flow and release, and/or morphological, or stylistic properties, without adversely affecting other mechanical and thermal properties. 
     In making plastic parts, materials are generally fed into the heated barrel of an injection molding machine, melted, and then injected under high pressure into a mold cavity. After this melt cools, a plastic component is realized. The process of cooling shrinks the melt on the mold core, necessitating an ejection force to demold the component from the mold of the machine. 
     In the ejection stage of injection molding the parts are mechanically forced to separate from the molding surfaces (especially from the cores). If the force required to remove the mold is too high (e.g., due to the strength with which the plastic sticks to the mold core), the machine&#39;s ejector pins may punch through and damage the plastic component. Ideally, the molded part should slip down easily from the mold core. The friction coefficient refers to the sticking or adhesive force that exists between the plastic part and the metal surface of the mold. Reduce this force, and demolding will be more efficient. Friction is normally understood as the resistance offered by bodies in contact to relative motion. In injection molding, the bodies in contact are steel molding surfaces and polymer moldings. 
     Aesthetics and functionality of products may require the use of small draft angles. Small draft angles, however, lead to an increase of the ejection forces. 
     In polymer injection molding, adhesion force(s) between part and the tool are a complex interaction due to the dependency of part geometry and process parameters such as temperature and pressure. Ejection force, also called release force, has been identified in literature as a total friction between the tool and the polymer interface. 
     Holding pressure and surface temperature may influence the ejection force. 
     It is known that very good, polished, mirror-like surfaces can be difficult to separate by the local formation of vacuum. The testing of demolding, particularly for those developing raw materials, has focused on speeding up cycle times and reducing the amount of release agents used in the thermoplastic. The typical percentage of a release agent in the melt is about 1.0%, or even about 0.5%. If this amount of release agent can be reduced to about 0.2%, a reduction of problems observed in the molding process that relate to high contents of release agents can be avoided. 
     A high gloss surface needs more draft than rough surfaces. For example, currently automotive bezels include a variety of materials, depending on the part design and the heat requirements, including polycarbonate (PC), Polybutylene terephthalate (PBT), high heat PC, polyethersulfones and polyetherimide. Amongst polycarbonates, typical market solutions for bezels include use of PC having a melt flow volume rate (MVR) of about 8 up to about 35 cm 3 /10 min as tested according to ISO 1133 at 300° C. using a 1.2 kg load. Such polycarbonates are available from Covestro and SABIC. PC resins with an MVR of greater than about 35 cm 3 /10 min are not currently used because the low Mw results in brittleness and consequently to de-molding failures or in-use part failures. 
     Friction between the thermoplastic part and the injection mold core not only depends on the mechanical relationship between the two surfaces, but also on an adhesive component inherent in the properties of the two materials at processing conditions. While the deformation (or mechanical) component of friction tends to be more easily defined, the adhesion component is rather more complex. 
     For polymers, the surface forces consist of van der Waals, coulombic and possibly hydrogen bonding forces. The higher the surface free energy of the polymer, the greater the adhesive force. 
     Equations developed for the ejection force for deep injection molded parts derive from the friction-based concept FR=f×pA×A, where FR is the ejection (or release) force, f is the coefficient of friction between the mold and the part, pA is the contact pressure of the part against the mold core, and A is the area of contact. 
     Contact pressure can be defined as p=E(T)×Δdr×sm, and therefore ejection force is: FR=Cf×E(T) Δdr×sm×2πL, where E(T) is the modulus of the thermoplastic part material at ejection temperature, Δdr is the relative change in diameter of the part immediately after ejection, sm, is the thickness of the part, and L is the length of the part in contact with the mold core. 
     Statistical analyses for demolding forces are used to determine the effects of packing time, cooling time and packing pressure on ejection force for materials or grade combinations. One common analysis is to do injection molding of sleeves, then measure the ejection force necessary to remove the sleeve from the core. At the opening of the mold, the part remains on the core due to the material contraction. At the end of the opening stroke, the ejector pins detach the part from the core. The force applied to the part for demolding is registered as the Mold Release Force (FR). 
     The friction properties of pairs of materials are usually represented by the coefficient of friction. The coefficient of friction is defined (e.g. in ASTM G40 test standard) as: μ=F/N In which, F is friction force and N is normal contact force. The same standard defines a coefficient of static friction, μs, corresponding to the maximum force that must be overcome to initiate macroscopic motion between the two bodies. A coefficient of kinetic friction is obtained from the average friction force necessary to maintain the macroscopic relative motion between the two bodies. It is represented by μk. 
     Plastic tends to stick over the surface of the cores. For example, the sidewalls that are perpendicular to the mold&#39;s parting line must be drafted. Draft angles increase the shape dimensions. Other areas that require draft angles include mounting flanges, gussets, holes, hollow bosses, louvers, other holes or ribs. As a result, dimensions like rib height are limited, and the wall thickness rib ratio is correlated to the draft angle. The plastic design rules define the shape of: a hole, a core, the rib height, the height of a side wall or the wall thickness rib ratio. 
     Mold drafts facilitate part removal from the mold. The draft is generally in an offset angle that is parallel to the mold opening and closing. The ideal draft angle for a given part depends on the depth of the part in the mold and its required end-use function. The mold part line will need to be located in a way that splits the draft in order to minimize it. If no draft is acceptable due to design/styling considerations, a side action mold (side slider) may be required in some aspects. 
     As a result, designers typically design parts according to the general plastic rules to ensure good manufacturing performance and aesthetics of the part. 
     Polycarbonate Polymer 
     The terms “polycarbonate” or “polycarbonates” as used herein include copolycarbonates, homopolycarbonates, (co)polyester carbonates and combinations thereof. 
     The term polycarbonate can be further defined as compositions have repeating structural units of the formula (1): 
     
       
         
         
             
             
         
       
     
     in which at least 60 percent of the total number of R1 groups are aromatic organic radicals and the balance thereof are aliphatic, alicyclic, or aromatic radicals. In a further aspect, each R1 is an aromatic organic radical and, in particular, a radical of the formula (2): 
       -A1-Y1-A2-  (2),
 
     wherein each of A1 and A2 is a monocyclic divalent aryl radical and Y1 is a bridging radical having one or two atoms that separate A1 from A2. In various aspects, one atom separates A1 from A2. For example, radicals of this type include, but are not limited to, radicals such as —O—, —S—, —S(O)—, —S(O2)-, —C(O)—, methylene, cyclohexyl-methylene, 2-[2.2.1]-bicycloheptylidene, ethylidene, isopropylidene, neopentylidene, cyclohexylidene, cyclopentadecylidene, cyclododecylidene, and adamantylidene. The bridging radical Y1 may be a hydrocarbon group or a saturated hydrocarbon group such as methylene, cyclohexylidene, or isopropylidene. 
     Polycarbonate materials include materials disclosed and described in U.S. Pat. No. 7,786,246, which is hereby incorporated by reference in its entirety for the specific purpose of disclosing various polycarbonate compositions and methods for manufacture of same. Polycarbonate polymers can be manufactured by means known to those skilled in the art. 
     Some polycarbonates are linear bisphenol-A polycarbonates produced by melt polymerization. The melt polycarbonate process is based on continuous reaction of a dihydroxy compound and a carbonate source in a molten stage. The reaction can occur in a series of reactors where the combined effect of catalyst, temperature, vacuum, and agitation allows for monomer reaction and removal of reaction by-products to displace the reaction equilibrium and effect polymer chain growth. A common polycarbonate made in melt polymerization reactions is derived from bisphenol A (BPA) via reaction with diphenyl carbonate (DPC). This reaction can be catalyzed by, for example, tetra methyl ammonium hydroxide (TMAOH) or tetrabutyl phosphonium acetate (TBPA), which can be added into a monomer mixture prior to being introduced to a first polymerization unit and sodium hydroxide (NaOH), which can be added to the first reactor or upstream of the first reactor and after a monomer mixer. 
     The melt polycarbonate in some aspects may have a molecular weight (Mw) of about 15,000 to about 40,000 Dalton when measured using GPC methods on a polycarbonate basis. The melt polycarbonate product may have an endcap level of about 45% to about 80%. Some polycarbonates have an endcap level of about 45% to about 75%, about 55% to about 75%, about 60% to about 70% or about 60% to about 65%. Certain polycarbonates have at least 200 ppm of hydroxide groups. Certain polycarbonates have 200-1100 parts per million (ppm) or 950 to 1050 ppm hydroxide groups. 
     The polycarbonate polymer may contain endcapping agents. Any suitable endcapping agents can be used provided that such agents do not significantly adversely impact the desired properties of the polycarbonate composition (transparency, for example). Endcapping agents include mono-phenolic compounds, mono-carboxylic acid chlorides, and/or mono-chloroformates. Mono-phenolic endcapping agents are exemplified by monocyclic phenols such as phenol and C1-C22 alkyl-substituted phenols such as p-cumyl-phenol, resorcinol monobenzoate, and p- and tertiary-butyl phenol; and monoethers of diphenols, such as p-methoxyphenol. 
     Apart from the main polymerization reaction in polycarbonate production, there is a series of side reactions consisting of chain rearrangements of the polymer backbone that lead to branching that are often referred to as Fries rearrangement. Some of these polycarbonates include from about 200 to about 2000 ppm, or from about 250 to about 1800 ppm Fries products. The Fries species specifically found in bisphenol A melt polycarbonates include the ester type of structures A, B, and C. 
     A. Linear Fries: 
     
       
         
         
             
             
         
       
     
     B. Branched Fries: 
     
       
         
         
             
             
         
       
     
     C. Acid Fries: 
     
       
         
         
             
             
         
       
     
     The Fries reaction is induced by the combined effect of basic catalysts, temperature, and residence time, which generally result in melt-produced polycarbonates being branched as compared with the interfacial polycarbonates since their manufacturing temperatures are lower. Because high branching levels in the resin can have a negative effect on the mechanical properties of the polycarbonate (for example, on impact strength), a product with lower branched Fries product may be desirable. 
     In some aspects the polycarbonate polymer is a linear bisphenol-A polycarbonate produced by a melt polymerization process. In other aspects the polycarbonate polymer is a linear bisphenol-A polycarbonate produced by an interfacial polymerization process. 
     In some compositions, the polycarbonate polymer comprises at least one polycarbonate polymer having a molecular weight (Mw) of at least 20,000 grams per mole (g/mol) and a second polycarbonate polymer have a molecular weight (Mw) of less than 20,000 g/mol. In some compositions, the molar ratio of said first polycarbonate polymer to said second polycarbonate polymer is about 1.4:1 to about 3.2:1. In other compositions, the molar ratio of said first polycarbonate polymer to said second polycarbonate polymer is about 1.5:1 to about 3.0:1. 
     In certain aspects, polycarbonate produced by interfacial polymerization may be utilized. In some processes, bisphenol A and phosgene are reacted in an interfacial polymerization process. Typically, the disodium salt of bisphenol A is dissolved in water and reacted with phosgene which is typically dissolved in a solvent that not miscible with water (such as a chlorinated organic solvent like methylene chloride). 
     In some aspects, the polycarbonate comprises interfacial polycarbonate having a weight average molecular weight of from about 10,000 Daltons to about 50,000 Daltons, preferably about 15,000 to about 45,000 Daltons. Some interfacial polycarbonates have an endcap level of at least 90% or preferably 95%. 
     Polycarbonate-Polysiloxane Copolymer 
     As used herein, the term “polycarbonate-polysiloxane copolymer” is equivalent to polysiloxane-polycarbonate copolymer, polycarbonate-polysiloxane polymer, or polysiloxane-polycarbonate polymer. In various aspects, the polycarbonate-polysiloxane copolymer can be a block copolymer comprising one or more polycarbonate blocks and one or more polysiloxane blocks. In some aspects, the polysiloxane-polycarbonate copolymer comprises polydiorganosiloxane blocks comprising structural units of the general formula (3) below: 
     
       
         
         
             
             
         
       
     
     wherein the polydiorganosiloxane block length (E) is from 10 to 100, preferably 20 to 60, more preferably 30 to 50; wherein each R group can be the same or different, and is selected from a C1-13 monovalent organic group; wherein each M can be the same or different, and is selected from a halogen, cyano, nitro, C1-C8 alkylthio, C1-C8 alkyl, C1-C8 alkoxy, C2-C8 alkenyl, C2-C8 alkenyloxy group, C3-C8 cycloalkyl, C3-C8 cycloalkoxy, C6-C10 aryl, C6-C10 aryloxy, C7-C12 aralkyl, C7-C12aralkoxy, C7-C12 alkylaryl, or C7-C12 alkylaryloxy, and where each n is independently 0, 1, 2, 3, or 4. 
     The polysiloxane-polycarbonate copolymer also comprises polycarbonate blocks comprising structural units of the general formula (4) below: 
     
       
         
         
             
             
         
       
     
     wherein at least 60 percent of the total number of R1 groups comprise aromatic moieties and the balance thereof comprise aliphatic, alicyclic, or aromatic moieties. 
     Certain polycarbonate-polysiloxane resins comprise allylphenol capped siloxanes. Such resins comprise the structure of the formula (5) below: 
     
       
         
         
             
             
         
       
     
     where R is an alkyl group having 1-3 carbon atoms, n1 is an integer of from 2 to 4 and n2 is an integer of from 1 to 200. Polycarbonate-polysiloxane copolymers comprising such structures can be found in European Patent Application No. 1757634 which is hereby incorporated by reference in its entirety for the specific purpose of disclosing various compositions and methods for manufacture of same. 
     In a particular aspect the poly(carbonate-siloxane) copolymer comprises bisphenol carbonate units of the formula (6) below: 
     
       
         
         
             
             
         
       
     
     wherein R a  and R b  are each independently C 1-12  alkyl, C 1-12  alkenyl, C 3-8  cycloalkyl, or C 1-12  alkoxy, 
     p and q are each independently 0 to 4, and 
     X a  is a single bond, —O—, —S—, —S(O)—, —S(O) 2 —, —C(O)—, a C 1-11  alkylidene of formula —C(R c )(R d )— wherein R c  and R d  are each independently hydrogen or C 1-10  alkyl, or a group of the formula —C(═R e )— wherein R e  is a divalent C 1-10  hydrocarbon group; and siloxane units of the formulae (7), (8) below: 
     
       
         
         
             
             
         
       
     
     or a combination comprising at least one of the foregoing, wherein
         R is each independently a C 1-13  monovalent hydrocarbon group,   Ar is each independently a C 6-30  aromatic group,   R 2  is each independently a C 2-8  alkylene group, and   E has an average value of 10 to 200.       

     Certain polysiloxane-polycarbonates materials include materials disclosed and described in U.S. Pat. No. 7,786,246, which is hereby incorporated by reference in its entirety for the specific purpose of disclosing various compositions and methods for manufacture of same. 
     The polycarbonate-siloxane copolymer comprises about 10 wt % to about 40 wt % siloxane. In particular aspects, the polycarbonate-siloxane copolymer comprises about 15 to about 25 wt % siloxane. Certain polycarbonate-polysiloxane copolymers have a polydiorganosiloxane block having from about 20 to about 60 diorganosiloxane units. The polycarbonate-siloxane copolymer is present in an amount effective to provide a total siloxane content of 1 wt % to 5 wt % based on the total weight of the composition. 
     In some aspects, the polycarbonate in the polycarbonate-siloxane copolymer is a linear bisphenol-A polycarbonate produced by a melt polymerization process. In other aspects the polycarbonate in the polycarbonate-siloxane copolymer is a linear bisphenol-A polycarbonate produced by an interfacial polymerization process. 
     In some aspects, the composition comprises from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer. 
     Release Agent 
     Examples of mold release agents include both aliphatic and aromatic carboxylic acids and their alkyl esters, for example, stearic acid, behenic acid, pentaerythritol stearate, glycerin tristearate, and ethylene glycol distearate. Polyolefins such as high-density polyethylene, linear low-density polyethylene, low-density polyethylene, and similar polyolefin homopolymers and copolymers can also be used a mold release agents. Some compositions use pentaerythritol tetrastearate, glycerol monostearate, glycerol tristearate, a wax or a poly-alpha-olefin. 
     Mold release agents are typically present in the composition at 0.05 wt % to 1 wt %, based on total weight of the composition, and in particular aspects from about 0.1 wt % to about 0.7 wt %, from about 0.1 wt % to about 0.5 wt %, or from about 0.1 wt % to about 0.4 wt %. Particular aspects have less than about 0.3 wt %, or even less than about 0.2 wt % release agent. 
     In some aspects the mold release agents will have high molecular weight, typically greater than 300, to prevent loss of the release agent from the molten polymer mixture during melt processing. 
     Additional Components 
     The additive composition can include an impact modifier, flow modifier, antioxidant, heat stabilizer, light stabilizer, ultraviolet (UV) light stabilizer, UV absorbing additive, plasticizer, lubricant, antistatic agent, anti-fog agent, antimicrobial agent, colorant (e.g., a dye or pigment), surface effect additive, flame retardant, radiation stabilizer, anti-drip agent (e.g., a PTFE-encapsulated styrene-acrylonitrile copolymer (TSAN)), or a combination thereof. For example, a combination of a heat stabilizer and ultraviolet light stabilizer can be used. In general, the additives are used in the amounts generally known to be effective. For example, the total amount of the additive composition can be from about 0.001 wt % to about 10.0 wt %, or from about 0.01 wt % to about 5 wt %, each based on the total weight of all ingredients in the composition. 
     The composition can include various additives ordinarily incorporated into polymer compositions of this type, with the proviso that the additive(s) are selected so as to not significantly adversely affect the desired properties of the thermoplastic composition (good compatibility for example). Such additives can be mixed at a suitable time during the mixing of the components for forming the composition. 
     Examples of impact modifiers include natural rubber, fluoroelastomers, ethylene-propylene rubber (EPR), ethylene-butene rubber, ethylene-propylene-diene monomer rubber (EPDM), acrylate rubbers, hydrogenated nitrile rubber (HNBR), silicone elastomers, styrene-butadiene-styrene (SBS), styrene-butadiene rubber (SBR), styrene-(ethylene-butene)-styrene (SEBS), acrylonitrile-butadiene-styrene (ABS), acrylonitrile-ethylene-propylene-diene-styrene (AES), styrene-isoprene-styrene (SIS), styrene-(ethylene-propylene)-styrene (SEPS), methyl methacrylate-butadiene-styrene (MBS), high rubber graft (HRG), and the like. Some suitable impact modifies include PC (polycarbonate)/ABS (such as Cycoloy PC/ABS) and MBS type formulations. 
     The polycarbonate compositions may optionally include flame retardants. Various types of flame retardants can be utilized. In one aspect, the flame retardant additives include, for example, flame retardant salts such as alkali metal salts of perfluorinated C1-C16 alkyl sulfonates such as potassium perfluorobutane sulfonate (Rimar salt), potassium perfluoroctane sulfonate, tetraethylammonium perfluorohexane sulfonate, potassium diphenylsulfone sulfonate (KSS), and the like, sodium benzene sulfonate, sodium toluene sulfonate (NATS) and the like; and salts formed by reacting for example an alkali metal or alkaline earth metal (for example lithium, sodium, potassium, magnesium, calcium and barium salts) and an inorganic acid complex salt, for example, an oxo-anion, such as alkali metal and alkaline-earth metal salts of carbonic acid, such as Na2CO3, K2CO3, MgCO3, CaCO3, and BaCO3 or fluoro-anion complex such as Li3AlF6, BaSiF6, KBF4, K3AlF6, KAlF4, K2SiF6, and/or Na3AlF6 or the like. Rimar salt and KSS and NATS, alone or in combination with other flame retardants, are particularly useful in the compositions disclosed herein. 
     Some aspects of the composition disclosed herein may comprise a halogen containing flame retardant additive. 
     In some aspects, the flame retardant additive may comprise from about 0.1 wt % to about 25 wt % of the composition disclosed herein. 
     The polycarbonate compositions can optionally include a colorant composition containing pigment and/or dye additives. Useful pigments can include, for example, inorganic pigments such as metal oxides and mixed metal oxides such as zinc oxide, titanium dioxides, iron oxides, or the like; sulfides such as zinc sulfides, or the like; aluminates; sodium sulfo-silicates sulfates, chromates, or the like; carbon blacks; zinc ferrites; ultramarine blue; organic pigments such as azos, di-azos, quinacridones, perylenes, naphthalene tetracarboxylic acids, flavanthrones, isoindolinones, tetrachloroisoindolinones, anthraquinones, enthrones, dioxazines, phthalocyanines, and azo lakes; Pigment Red 101, Pigment Red 122, Pigment Red 149, Pigment Red 177, Pigment Red 179, Pigment Red 202, Pigment Violet 29, Pigment Blue 15, Pigment Blue 60, Pigment Green 7, Pigment Yellow 119, Pigment Yellow 147, Pigment Yellow 150, and Pigment Brown 24; or combinations comprising at least one of the foregoing pigments. 
     Dyes are generally organic materials and include coumarin dyes such as coumarin 460 (blue), coumarin 6 (green), nile red or the like; lanthanide complexes; hydrocarbon and substituted hydrocarbon dyes; polycyclic aromatic hydrocarbon dyes; scintillation dyes such as oxazole or oxadiazole dyes; aryl- or heteroaryl-substituted poly (C2-8) olefin dyes; carbocyanine dyes; indanthrone dyes; phthalocyanine dyes; oxazine dyes; carbostyryl dyes; napthalenetetracarboxylic acid dyes; porphyrin dyes; bis(styryl)biphenyl dyes; acridine dyes; anthraquinone dyes; cyanine dyes; methine dyes; arylmethane dyes; azo dyes; indigoid dyes, thioindigoid dyes, diazonium dyes; nitro dyes; quinone imine dyes; aminoketone dyes; tetrazolium dyes; thiazole dyes; perylene dyes, perinone dyes; bis-benzoxazolylthiophene (BBOT); triarylmethane dyes; xanthene dyes; thioxanthene dyes; naphthalimide dyes; lactone dyes; fluorophores such as anti-stokes shift dyes which absorb in the near infrared wavelength and emit in the visible wavelength, or the like; luminescent dyes such as 7-amino-4-methylcoumarin; 3-(2′-benzothiazolyl)-7-diethylaminocoumarin; 2-(4-biphenylyl)-5-(4-t-butylphenyl)-1,3,4-oxadiazole; 2,5-bis-(4-biphenylyl)-oxazole; 2,2′-dimethyl-p-quaterphenyl; 2,2-dimethyl-p-terphenyl; 3,5,3″″,5″″-tetra-t-butyl-p-quinquephenyl; 2,5-diphenylfuran; 2,5-diphenyloxazole; 4,4′-diphenylstilbene; 4-dicyanomethylene-2-methyl-6-(p-dimethylaminostyryl)-4H-pyran; 1,1′-diethyl-2,2′-carbocyanine iodide; 3,3′-diethyl-4,4′,5,5′-dibenzothiatricarbocyanine iodide; 7-dimethylamino-1-methyl-4-methoxy-8-azaquinolone-2; 7-dimethylamino-4-methylquinolone-2; 2-(4-(4-dimethylaminophenyl)-1,3-butadienyl)-3-ethylbenzothiazolium perchlorate; 3-diethylamino-7-diethyliminophenoxazonium perchlorate; 2-(1-naphthyl)-5-phenyloxazole; 2,2′-p-phenylen-bis(5-phenyloxazole); rhodamine 700; rhodamine 800; pyrene, chrysene, rubrene, coronene, or the like; or combinations comprising at least one of the foregoing dyes. 
     Heat stabilizer additives include organophosphites (e.g. triphenyl phosphite, tris-(2,6-dimethylphenyl)phosphite, tris-(mixed mono- and di-nonylphenyl)phosphite or the like), phosphonates (e.g., dimethylbenzene phosphonate or the like), phosphates (e.g., trimethyl phosphate, or the like), or combinations comprising at least one of the foregoing heat stabilizers. The heat stabilizer can be tris(2,4-di-t-butylphenyl) phosphate available as Irgafos® 168. Heat stabilizers are generally used in amounts of from about 0.01 wt % to about 5 wt %, based on the total weight of polymer in the composition. 
     There is considerable overlap among plasticizers, lubricants, and mold release agents, which include, for example, glycerol tristearate (GTS), phthalic acid esters (e.g., octyl-4,5-epoxy-hexahydrophthalate), tris-(octoxycarbonylethyl)isocyanurate, tristearin, di- or polyfunctional aromatic phosphates (e.g., resorcinol tetraphenyl diphosphate (RDP), the bis(diphenyl) phosphate of hydroquinone and the bis(diphenyl) phosphate of bisphenol A); poly-alpha-olefins; epoxidized soybean oil; silicones, including silicone oils (e.g., poly(dimethyl diphenyl siloxanes); esters, for example, fatty acid esters (e.g., alkyl stearyl esters, such as, methyl stearate, stearyl stearate, and the like), polyethylene, waxes (e.g., beeswax, montan wax, paraffin wax, or the like), or combinations comprising at least one of the foregoing plasticizers, lubricants, and mold release agents. These are generally used in amounts of from about 0.01 wt % to about 5 wt %, based on the total weight of the polymer in the composition. 
     Light stabilizers, in particular ultraviolet light (UV) absorbing additives, also referred to as UV stabilizers, include hydroxybenzophenones (e.g., 2-hydroxy-4-n-octoxy benzophenone), hydroxybenzotriazines, cyanoacrylates, oxanilides, benzoxazinones (e.g., 2,2′-(1,4-phenylene)bis(4H-3,1-benzoxazin-4-one, commercially available under the trade name CYASORB UV-3638 from Cytec), aryl salicylates, hydroxybenzotriazoles (e.g., 2-(2-hydroxy-5-methylphenyl)benzotriazole, 2-(2-hydroxy-5-tert-octylphenyl)benzotriazole, and 2-(2H-benzotriazol-2-yl)-4-(1,1,3,3-tetramethylbutyl)-phenol, commercially available under the trade name CYASORB 5411 from Cytec) or combinations comprising at least one of the foregoing light stabilizers. The UV stabilizers can be present in an amount of from about 0.01 to about 1 wt %, specifically, from about 0.1 wt % to about 0.5 wt %, and more specifically, from about 0.15 wt % to about 0.4 wt %, based upon the total weight of polymer in the composition. 
     Antioxidant additives include organophosphites such as tris(nonyl phenyl)phosphite, tris(2,4-di-t-butylphenyl)phosphite, bis(2,4-di-t-butylphenyl)pentaerythritol diphosphite, distearyl pentaerythritol diphosphite; alkylated monophenols or polyphenols; alkylated reaction products of polyphenols with dienes, such as tetrakis[methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)] methane; butylated reaction products of para-cresol or dicyclopentadiene; alkylated hydroquinones; hydroxylated thiodiphenyl ethers; alkylidene-bisphenols; benzyl compounds; esters of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of beta-(5-tert-butyl-4-hydroxy-3-methylphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of thioalkyl or thioaryl compounds such as distearylthiopropionate, dilaurylthiopropionate, ditridecylthiodipropionate, octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate; amides of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid, or combinations comprising at least one of the foregoing antioxidants. Antioxidants are used in amounts of from about 0.01 wt % to about 0.1 wt %, based on 100 parts by weight of the total composition, excluding any filler. 
     Anti-drip agents can also be used in the composition, for example a fibril forming or non-fibril forming fluoropolymer such as polytetrafluoroethylene (PTFE). The anti-drip agent can be encapsulated by a rigid copolymer, for example styrene-acrylonitrile copolymer (SAN). PTFE encapsulated in SAN is known as TSAN. A TSAN comprises about 50 wt % PTFE and about 50 wt % SAN, based on the total weight of the encapsulated fluoropolymer. The SAN can comprise, for example, about 75 wt % styrene and about 25 wt % acrylonitrile based on the total weight of the copolymer. Anti-drip agents can be used in amounts of about 0.1 to about 10 parts by weight, based on 100 parts by weight of the total composition, excluding any filler. 
     Polymer Mixtures 
     The polymer compositions can be formed by techniques known to those skilled in the art. Extrusion and mixing techniques, for example, may be utilized to combine the components of the polymer composition. 
     The polymer composition may comprise from about 49.5 wt % to about 97.95 wt % of at least one polycarbonate polymer; from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer; and from about 0.05 wt % to about 1.0 wt % of at least one release agent, wherein the composition exhibits a melt volume flow rate (MVR) of at least about 25 cm 3 /10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load and a ductile/brittle transition temperature of less than or equal to 10° C. as determined in accordance with ISO 180-1A on a molded part having a thickness of 3 mm; In some aspects, certain polymer compositions exhibit melt volume ratios of at least about 35 or 45 cm 3 /10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load. 
     In some aspects, the polymer composition disclosed herein may exhibit a heat distortion temperature (HDT) of 120 degrees Celsius at 1.8 megapascals (MPa) as determined by ISO 75/Ae. 
     The composition may comprise siloxane content of about 1 wt % to about 5 wt %. In some aspects, the composition has a siloxane content of about 1 wt % to 2 wt %. 
     The composition may be a notched Izod impact strength of at least about 40 kilojoules per square meter (kJ/m 2 ) at 23° C., as determined according to ISO 1801/A on 3 mm thick samples. In some aspects, certain compositions exhibit a notched Izod impact strength of at least about 40 kJ/m 2  at 10° C. or lower temperatures, as determined according to ISO 1801/A on 3 mm thick samples. 
     In some aspects, the composition may also exhibit good chemical resistance to certain compounds and critical fluids such as sunscreen. Environmental Stress Cracking Resistance (“ESCR”) describes the accelerated failure of polymeric materials, as a combined effect of environment, temperature, and stress. The failure mainly depends on the characteristics of the material, chemical, exposure condition, and the magnitude of the stress. ESCR may be determined according to the ISO 22088-3 standard according to the procedure described below. In some aspects, the compositions have retention of tensile strength of 80% or higher after exposure to sunscreen (e.g., Banana Boat® sunscreen) for 24 hours at room temperature under 1% strain. 
     Molds 
     Molds for forming molded articles are well known to those skilled in the art and can be formed from conventional materials. In the instant disclosure, molded parts may include draft angles of about 0.1 degree to about 7 degrees. In some aspects, molded parts include draft angles that are less than about 5 degrees or less than about 0.1 degrees or less than about 1 degree or less than about 3 degrees. 
     In some aspects, the disclosure concerns heating a composition and feeding the heated composition into a heated barrel of an injection molding machine and allowing the composition to melt. The melted composition can then be injected at elevated pressure into a mold cavity. Once the composition solidifies (either by passive or active cooling) forming a molded composition, the molded composition may be ejected from the mold. In some aspects, a demolding ejection force of less than about 400 Newtons (N), or less than about 350 N, or less than about 300 N, or even less than about 250 N is required to remove the molded composition from the mold. 
     In some aspects, a demolding coefficient of friction of less than about 20, or less than about 18, or less than about 16, or even less than about 14 is measured according to UL410. 
     As illustrated in  FIG. 1 , molded articles according to aspects of the present disclosure allow reduced draft, enabling new shapes, and lower part volumes or improved optical surface areas. As further illustrated in  FIGS. 2 and 3 , molded articles according to aspects of the present disclosure have high flow and improved release characteristic that enable box designs with lower draft angles ( FIG. 3 ) and larger ribs ( FIG. 2 ) due to more rectangular walls with minimum release angle. 
     The composition disclosed herein may require an ejection force at least 50% lower than an ejection force required for a substantially identical reference article without a polycarbonate-polysiloxane copolymer. 
     In some aspects, the composition may exhibit a coefficient of friction for removal of at least 15% lower than a coefficient of friction for removal of a substantially identical reference article without a polycarbonate-polysiloxane copolymer. 
     Metallization 
     The compositions can be used to manufacture a variety of articles, and in particular, metallized articles suited for automotive bezels or reflectors. The thermoplastic compositions are preferably directly metallizable for use in manufacture of metallized articles (e.g., metallized bezels or housing for consumer devices). 
     For purposes of the present disclosure a “metallized” surface is a surface that is covered with a coating including one or more metals. The metallizing step can, in various aspects, be performed using conventional techniques. For example, in one aspect, an electroless copper plating bath is used during the metallization step in the manufacturing process. Thus, in various aspects, plating a metal layer onto the thermoplastic composition or article(s) formed therefrom is metallization. In certain aspects the composition/article may be metallized by vapor deposition, non-conducting vacuum metallization or overmolding. The metal can be any metal allowing for good adhesion to the composition/article and imparting good cosmetic appearance. The composition/article can retain its properties and structural integrity after being exposed to various metallization processes to be coated, for example, with aluminum or other metals providing good adhesion to the composition/article and impart good cosmetic appearance. 
     Definitions 
     It is to be understood that the terminology used herein is for the purpose of describing particular aspects only and is not intended to be limiting. As used in the specification and in the claims, the term “comprising” can include the aspects “consisting of” and “consisting essentially of.” Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. In this specification and in the claims which follow, reference will be made to a number of terms which shall be defined herein. 
     As used in the specification and the appended claims, the singular forms “a,” “an” and “the” include plural equivalents unless the context clearly dictates otherwise. Thus, for example, reference to “a polycarbonate polymer” includes mixtures of two or more polycarbonate polymers. 
     Ranges can be expressed herein as from one value (first value) to another value (second value). When such a range is expressed, the range includes in some aspects one or both of the first value and the second value. Similarly, when values are expressed as approximations, by use of the antecedent ‘about,’ it will be understood that the particular value forms another aspect. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint. It is also understood that there are a number of values disclosed herein, and that each value is also herein disclosed as “about” that particular value in addition to the value itself. For example, if the value “10” is disclosed, then “about 10” is also disclosed. It is also understood that each unit between two particular units are also disclosed. For example, if 10 and 15 are disclosed, then 11, 12, 13, and 14 are also disclosed. When more than one range for a particular value is disclosed, the ranges are combinable to form additional aspects. 
     As used herein, the terms “about” and “at or about” mean that the amount or value in question can be the designated value, approximately the designated value, or about the same as the designated value. It is generally understood, as used herein, that it is the nominal value indicated+5% variation unless otherwise indicated or inferred. The term is intended to convey that similar values promote equivalent results or effects recited in the claims. That is, it is understood that amounts, sizes, formulations, parameters, and other quantities and characteristics are not and need not be exact, but can be approximate and/or larger or smaller, as desired, reflecting tolerances, conversion factors, rounding off, measurement error and the like, and other factors known to those of skill in the art. In general, an amount, size, formulation, parameter or other quantity or characteristic is “about” or “approximate” whether or not expressly stated to be such. It is understood that where “about” is used before a quantitative value, the parameter also includes the specific quantitative value itself, unless specifically stated otherwise. 
     References in the specification and concluding claims to parts by weight of a particular element or component in a composition or article denotes the weight relationship between the element or component and any other elements or components in the composition or article for which a part by weight is expressed. Thus, in a compound containing 2 parts by weight of component X and 5 parts by weight component Y, X and Y are present at a weight ratio of 2:5, and are present in such ratio regardless of whether additional components are contained in the compound. 
     As used herein the terms “weight percent,” “weight %,” and “wt %” of a component, which can be used interchangeably, unless specifically stated to the contrary, are based on the total weight of the formulation or composition in which the component is included. For example if a particular element or component in a composition or article is said to have 8% by weight, it is understood that this percentage is relative to a total compositional percentage of 100% by weight. 
     As used herein, the terms “weight average molecular weight” or “Mw” can be used interchangeably, and are defined by the formula: 
     
       
         
           
             
               
                 M 
                 w 
               
               = 
               
                 
                   Σ 
                    
                   
                       
                   
                    
                   
                     N 
                     i 
                   
                    
                   
                     M 
                     i 
                     2 
                   
                 
                 
                   Σ 
                    
                   
                       
                   
                    
                   
                     N 
                     i 
                   
                    
                   
                     M 
                     i 
                   
                 
               
             
             , 
           
         
       
     
     where Mi is the molecular weight of a chain and Ni is the number of chains of that molecular weight. Mw can be determined for polymers, e.g. polycarbonate polymers, by methods well known to a person having ordinary skill in the art using molecular weight standards, e.g. polycarbonate standards or polystyrene standards, and in particular certified or traceable molecular weight standards. Polystyrene basis refers to measurements using a polystyrene standard. 
     The term “siloxane” refers to a segment having a Si—O—Si linkage. 
     The term “flowable” means capable of flowing or being flowed. Typically a polymer is heated such that it is in a melted state to become flowable. 
     ° C. is degrees Celsius, m is micrometer, kG is kilogram. 
     “Interfacial polycarbonate” is produced by a process where typically the disodium salt of bisphenol A (BPA) is dissolved in water and reacted with phosgene which is typically dissolved in a solvent that not miscible with water. 
     “Melt polycarbonate” is produced by a process where BPA reacts with diphenyl carbonate (DPC) in a molten state without the solvent. 
     Melt Volume Flow Rate (MVR) is measured according to ISO 1133 at 300° C. using a 1.2 kg load. 
     Ejection force may be measured by injection molding sleeves in a core and then measuring the force necessary to remove the sleeve from the core. At the opening of the mold, the sleeve remains on the core due to the material contraction. At the end of the opening stroke, the ejector pins detach the sleeve from the core. The force applied to the sleeve for demolding is measured as the mold release force. The surface temperature of the sleeve is kept constant so that an accurate comparison of ejection forces can be made. 
     “Draft angle” concerns the slope of the wall of a mold as depicted in, e.g.,  FIG. 4 . 
     Aspects 
     Aspect 1. A thermoplastic composition comprising: 
     (a) from about 49.5 wt % to about 97.95 wt % of at least one polycarbonate polymer; 
     (b) from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer in an amount effective to provide a total siloxane content of about 1.0 wt % to about 5.0 wt % based on the total weight of the thermoplastic composition; and 
     (c) from about 0.05 wt % to about 1.0 wt % of at least one release agent, 
     wherein the composition exhibits a melt volume flow rate (MVR) of at least about 25 cm 3 /10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load; 
     a ductile/brittle transition temperature of less than or equal to 10° C. as determined in accordance with ISO 180-1A on a molded part having a thickness of 3 mm; and 
     an L* that is less than about 30% higher compared to a reference thermoplastic composition without the polycarbonate-siloxane copolymer, as measured according to ASTM D1729 on a 3 mm thick metallized plaque in reflectance and specular excluded mode. 
     Aspect 2. A thermoplastic composition comprising: 
     (a) from about 49.5 wt % to about 97.95 wt % of at least one polycarbonate polymer; 
     (b) from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer in an amount effective to provide a total siloxane content of about 1.0 wt % to about 5.0 wt % based on the total weight of the thermoplastic composition; and 
     (c) from about 0.05 wt % to about 1.0 wt % of at least one release agent, 
     wherein the composition exhibits 
     a melt volume flow rate (MVR) of at least about 25 cm 3 /10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load; 
     a ductile/brittle transition temperature of less than or equal to 10° C. as determined in accordance with ISO 180-1A on a molded part having a thickness of 3 mm; and 
     an L* that is about 10 or lower, as measured according to ASTM D1729 on a 3 mm thick metallized plaque in reflectance and specular excluded mode. 
     Aspect 3. A thermoplastic composition comprising: 
     (a) from about 49.5 wt % to about 97.95 wt % of at least one polycarbonate polymer; 
     (b) from about 2.0 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer in an amount effective to provide a total siloxane content of about 1.0 wt % to about 5.0 wt % based on the total weight of the thermoplastic composition; and 
     (c) from about 0.05 wt % to about 1.0 wt % of at least one release agent, 
     wherein the composition exhibits 
     a melt volume flow rate (MVR) of at least about 25 cm 3 /10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load; 
     a ductile/brittle transition temperature of less than or equal to 10° C. as determined in accordance with ISO 180-1A on a molded part having a thickness of 3 mm; and 
     a tensile yield strength retention of 80% and higher after exposure of an ISO tensile bar for 24 hours to sunscreen under 1% strain compared to a non-exposed reference tested according to ISO 22088-3. 
     Aspect 4. The thermoplastic composition of any one of Aspects 1-3, wherein the polycarbonate polymer is a melt polycarbonate polymer, an interfacial polycarbonate polymer, or a combination thereof. 
     Aspect 5. The thermoplastic composition of any one of Aspects 1-4, wherein the poly(carbonate-siloxane) copolymer comprises bisphenol carbonate units of the formula 
     
       
         
         
             
             
         
       
     
     wherein R a  and R b  are each independently C 1-12  alkyl, C 1-12  alkenyl, C 3-8  cycloalkyl, or C 1-12  alkoxy, 
     p and q are each independently 0 to 4, and 
     X a  is a single bond, —O—, —S—, —S(O)—, —S(O) 2 —, —C(O)—, a C 1-11  alkylidene of formula —C(R c )(R d )— wherein R c  and R d  are each independently hydrogen or C 1-10  alkyl, or a group of the formula —C(═R e )— wherein R e  is a divalent C 1-10  hydrocarbon group; and siloxane units of the formulas 
     
       
         
         
             
             
         
       
     
     or a combination comprising at least one of the foregoing, wherein
         R is each independently a C 1-13  monovalent hydrocarbon group,   Ar is each independently a C 6-30  aromatic group,   R 2  is each independently a C 2-8  alkylene group, and   E has an average value of 10 to 200.       

     Aspect 6. The thermoplastic composition of Aspect 1 or 2, wherein the composition is incorporated into an automotive bezel or automotive reflector. 
     Aspect 7. The thermoplastic composition of Aspect 3, wherein the composition is incorporated into a housing for a consumer device. 
     Aspect 8. The thermoplastic composition of Aspect 7, wherein the consumer device is a cellular phone, a tablet computer, a laptop computer, a desktop computer, a television, a battery or an adapter. 
     Aspect 9. The thermoplastic composition of any one of Aspects 1 to 8, wherein the release agent comprises pentaerythrityl tetrastearate. 
     Aspect 10. The thermoplastic composition of any one of Aspects 1 to 8, wherein the release agent comprises glycerol tristearate. 
     Aspect 11. The thermoplastic composition of any one of Aspects 1 to 10, further comprising a processing aid, a heat stabilizer, an antioxidant, an ultra violet light absorber, or a combination thereof. 
     Aspect 12. The thermoplastic composition of any one of Aspects 1 to 11, wherein the composition comprises a MVR of at least about 35 cm 3 /10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load. 
     Aspect 13. The thermoplastic composition of any one of Aspects 1 to 12, wherein the composition comprises a MVR of at least about 45 cm 3 /10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load. 
     Aspect 14. The thermoplastic composition of any one of Aspects 1 to 13, wherein the composition exhibits a heat distortion temperature of at least about 120° C. at about 1.8 MPa, as determined according to ISO 75/Ae. 
     Aspect 15. The thermoplastic composition of any one of Aspects 1 to 14, wherein the composition comprises a notched Izod impact strength of at least about 40 kJ/m 2  at 23° C., as determined according to ISO 180/1A on a 3 mm thick bar. 
     Aspect 16. The thermoplastic composition of any one of Aspects 1 to 15, wherein the composition comprises a notched Izod impact strength of at least about 40 kJ/m 2  at 10° C., as determined according to ISO 180/1A on a 3 mm thick bar. 
     Aspect 17. The thermoplastic composition of any one of Aspect 1 to 16, wherein the composition further comprises a flame retardant, an anti-drip agent, or a combination thereof, wherein optionally the flame retardant comprising an alkali metal salt of a perfluorinated C 1 -C 16  alkyl sulfonate, an inorganic acid complex salt, or a combination thereof. 
     Aspect 18. The thermoplastic composition of any one of Aspects 1 to 17, wherein the composition has a coefficient of friction of less than about 20 as determined by UL410. 
     Aspect 19. The thermoplastic composition of anyone of anyone of Aspects 1 to 18, wherein a demolding ejection force of less than about 400 N, or less than about 350 N, or less than about 300 N, or less than about 250 N is required to remove the composition from a mold. 
     Aspect 20. A method for forming an article, comprising: 
     forming a thermoplastic composition comprising:
         (a) from about 49.5 wt % to about 97.95 wt % of at least one polycarbonate polymer;   (b) from about 2 wt % to about 49.5 wt % of at least one polycarbonate-siloxane copolymer in an amount effective to provide a total siloxane content of about 1.0 wt % to about 5 wt % based on the total weight of the thermoplastic composition; and   (c) from about 0.05 wt % to about 1.0 wt % of at least one release agent,       

     wherein the composition exhibits a melt volume flow rate (MVR) of at least about 25 cm 3 /10 min, as determined according to ISO 1133 at 300° C. using a 1.2 kg load; 
     a ductile/brittle transition temperature of less than or equal to 10° C. as determined in accordance with ISO 180-1A on a molded part having a thickness of 3 mm; and 
     injection molding, extruding, rotational molding, blow molding or thermoforming the mixture in a mold to form the article. 
     Aspect 21. The method of Aspect 20, further comprising removing the article from the mold, wherein the removal requires an ejection force at least about 50% lower than the ejection force required for a substantially identical reference article without a polycarbonate-polysiloxane copolymer. 
     Aspect 22. The method of Aspect 21, wherein the coefficient of friction for the removal is at least about 15% lower than the coefficient of friction for removal of a substantially identical reference article without a polycarbonate-polysiloxane copolymer. 
     Aspect 23. The method of any one of Aspects 20 to 22, wherein the mold comprises at least one draft angle from about greater than 00 to about 3°. 
     Aspect 24. The method of any one of Aspects 20 to 23, wherein the polycarbonate polymer is a melt polycarbonate polymer, an interfacial polycarbonate polymer, or a combination thereof. 
     EXAMPLES 
     The following non-limited examples illustrate certain aspects of the disclosure. 
     The ingredients utilized in the examples are shown in Table 1: 
     
       
         
           
               
             
               
                 TABLE 1 
               
               
                   
               
               
                 Ingredient List 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
               
            
               
                 PC1 
                 Linear Bisphenol A Polycarbonate homopolymer, 
               
               
                   
                 produced via interfacial polymerization, Mw of 
               
               
                   
                 about 18,800 g/mol as determined by GPC using 
               
               
                   
                 polycarbonate standards, para-cumylphenol (PCP) 
               
               
                   
                 end-capped 
               
               
                 PC2 
                 Linear Bisphenol A Polycarbonate homopolymer, 
               
               
                   
                 produced via interfacial polymerization, Mw of 
               
               
                   
                 about 21,800 g/mol as determined by GPC using 
               
               
                   
                 polycarbonate standards, para-cumylphenol (PCP) 
               
               
                   
                 end-capped 
               
               
                 PC3 
                 Branched Bisphenol A Polycarbonate homopolymer, 
               
               
                   
                 produced via melt polymerization, Mw of about 
               
               
                   
                 18,000 g/mol as determined by GPC using 
               
               
                   
                 polycarbonates standards, Fries level 250-350 
               
               
                   
                 ppm, BPA/Phenol end-capped 
               
               
                 PC4 
                 Branched Bisphenol A Polycarbonate homopolymer, 
               
               
                   
                 produced via melt polymerization, Mw of about 
               
               
                   
                 20,600 g/mol as determined by GPC using 
               
               
                   
                 polycarbonates standards, Fries level about 
               
               
                   
                 350 ppm. BPA/Phenol end-capped 
               
               
                 PC-Si 
                 PDMS (polydimethylsiloxane) - Bisphenol A 
               
               
                   
                 Polycarbonate copolymer, produced via interfacial 
               
               
                   
                 polymerization, 20 wt % siloxane, average PDMS block 
               
               
                   
                 length of 45 units (D45), Mw about 30,000 g/mol as 
               
               
                   
                 determined by GPC using polycarbonate standards, 
               
               
                   
                 para-cumylphenol (PCP) end-capped 
               
               
                 Irgafos 
                 Tris(2,4-ditert-butylphenyl)phosphite (Irgafos 168) 
               
               
                 IM1 
                 Butylacrylate-methylmethacrylate core-shell rubber, 
               
               
                   
                 Paraloid EXL3300 
               
               
                 IM2 
                 Silicone Polymer, KANEKA MR02 
               
               
                 IM3 
                 Methylmethacrylate Butadiene (MBS) shell-core 
               
               
                   
                 copolymer, Paraloid EXL2650A 
               
               
                 PETS 
                 PETS - Pentaerythritol tetrastearate, &gt;90% esterified 
               
               
                 GTS 
                 Octadecanoic acid, 1,2,3-propanetriyl ester 
               
               
                   
                 (glycerol tristearate) 
               
               
                 CB 
                 Carbon black 
               
               
                   
               
            
           
         
       
     
     Unless stated otherwise, the compositions were made by the following procedures. All solid additives (e.g., stabilizers, colorants) were dry blended off-line as concentrates using one of the primary polymer powders as a carrier and starve-fed via gravimetric feeder(s) into the feed throat of the extruder. The remaining polymer(s) were starve-fed via gravimetric feeder(s) into the feed throat of the extruder as well. 
     Extrusion of all materials was performed on a 25 mm Werner-Pfleiderer ZAK twin-screw extruder (L/D ratio of 33/1) with a vacuum port located near the die face. The extruder had 9 zones, which were set at temperatures of 40° C. (feed zone), 200° C. (zone 1), 250° C. (zone 2), 270° C. (zone 3), and 280° C. (zone 4 to 8). Screw speed was 300 revolutions per minute (rpm) and throughput was between 15 and 25 kilograms per hour (kg/hr). 
     The compositions were molded after drying at 120° C. for 2 hours on a 45-ton Engel molding machine with a 22 mm screw or a 75-ton Engel molding machine with a 30 mm screw operating at a temperature around 300° C. with a mold temperature of 80° C. 
     Physical testing (e.g., Vicat softening temperature, heat deflection temperature, melt volume flow rate, melt flow rate, melt viscosity, Izod notched impact, multiaxial impact) was performed according to ISO or ASTM standards. Unless specified to the contrary herein, all test standards are the most recent standard in effect at the time of filing this application. 
     Notched Izod Impact (INI) Strength may be used to compare the impact resistances of plastic materials. For these examples, notched Izod impact strength was determined using a 3 mm thick molded, notched Izod impact bar according to ISO 180-2000. Tests were conducted at room temperature (23° C.) and at low temperatures (10° C. and lower). Ductile to brittle transition temperature (Temp D/B) was determined as the temperature at which the material changes from ductile fracture with high impact energy above 30 kJ/m 2  to brittle fracture with low impact energy below 20 kJ/m 2 . 
     Heat deflection temperature (HDT) was determined as flatwise under a 0.45 MPa loading with a 4 mm thickness bar according to ISO75-2013. 
     Melt volume rate (MVR) was measured at 300° C./1.2 kg per ISO 1133-2011. 
     Spiral flow was measured under a molding temperature of 300° C., a mold temperature of 80° C., and an injection pressure of 2200 bar/s. The resulting molded parts had a thickness of 1 mm. 
     Environmental Stress Cracking Resistance (“ESCR”) describes the accelerated failure of polymeric materials, as a combined effect of environment, temperature, and stress. The failure mainly depends on the characteristics of the material, chemical, exposure condition, and the magnitude of the stress. The tests followed ISO 22088-3 standard and used ISO tensile bars under 1% strain for 24 hours at room temperature with chemical Banana Boat® sunscreen applied on the surface. After 24 hours, the retention of tensile strength and elongation to break, measured according to ISO 527, compared to the non-exposed reference. 
     Metallization was performed on molded parts from a film gate injection set-up having dimensions 60 mm×60 mm and a thickness of 3 mm using the physical vapor deposition (PVD) process. This process deposited a 100-150 nanometer (nm) thick aluminum layer onto one side of the molded part under vacuum, followed by a protective plasma-deposited siloxane hard-coat of 50 nm. 
     Color data was acquired on an X-rite 1-7 spectrophotometer in the range 360 nm to 750 nm. The reflection data was acquired in specular excluded mode using a 25 mm aperture according to ASTM D1003 using D65 illumination and a 10 degree observer angle. A mirror image has a high level of specular reflection. Hence when specular reflection is excluded from the measurement, a highly reflective, mirror like metallized surface will give low L*. A decrease in mirror like reflectivity will give more diffuse light scattering and hence give a higher L*. 
     Ejection force was measured by injection molding sleeves in a core and then measuring the force necessary to remove the sleeve from the core. At the opening of the mold, the sleeve remained on the core due to the material contraction. At the end of the opening stroke, the ejector pins detached the sleeve from the core. The force applied to the sleeve for demolding was measured as the ejection force. The surface temperature of the sleeve was kept constant so that an accurate comparison of ejection force could be made. An exemplary sleeve suitable for determining ejection force is shown in  FIG. 5 . Ejection force was measured with a composition formed into the exemplary sleeve/mold of  FIG. 5 . Dimensions of are in millimeters (mm) for the sleeve 202 configured to the sprue 204. It should be noted that other sleeves/molds with other dimensions could be used for comparing the compositions of the disclosure to the reference compositions. Measurement process parameters were as follows. 
     
       
         
           
               
               
               
               
             
               
                   
                   
               
             
            
               
                   
                 Melt temperature 
                 300° 
                 C. 
               
               
                   
                 Surface temperature of the core 
                 95° 
                 C. 
               
            
           
           
               
               
               
            
               
                   
                 Ejection speed 
                 70 mm/second (s) 
               
            
           
           
               
               
               
               
            
               
                   
                 Cycle time 
                 20.1 
                 s 
               
               
                   
                 Overall cooling time 
                 13.6 
                 s 
               
            
           
           
               
               
               
            
               
                   
                 Pre-drying 
                 120° C., 4 hours (h) 
               
            
           
           
               
               
               
               
            
               
                   
                 Max. injection pressure 
                 1000 
                 bar 
               
               
                   
                 Injection speed 
                 25 
                 cm 3 /s 
               
               
                   
                 Changeover pressure 
                 100 
                 bar 
               
               
                   
                 Temperature injection plate 
                 89° 
                 C. 
               
               
                   
                 IM3 
                 97° 
                 C. 
               
               
                   
                   
               
            
           
         
       
     
     An exemplary apparatus suitable for determining coefficient of friction is shown in  FIG. 6 . Coefficient of friction was measured according to UL 410. A specialized mold insert was designed for the measurement of the CoF. A concave disc was molded and after a fixed cooling time, the mold opened slightly to allow rotation of the disc while maintaining a constant normal pressure on the part. The friction core exerted a constant pressure onto the disc. The disc itself was rotated by an electro-motor driven belt, while the resulting torque of the disc onto the friction core was measured. By the concave shape of the disc, the contact surface area is limited to an outer ring with a fixed surface area. For each material, the coefficient of friction is determined as the average over 10 discs/measurements. It should be noted that other discs/molds with other dimensions could be used for comparing the compositions of the disclosure to the reference compositions. Measurement process parameters were as follows. 
     
       
         
           
               
               
               
             
               
                   
                   
               
             
            
               
                   
                 Molding machine 
                 Arburg 370 
               
            
           
           
               
               
               
               
            
               
                   
                 Screw diameter 
                 25 
                 mm 
               
               
                   
                 Injection speed 
                 40 
                 mm/s 
               
            
           
           
               
               
               
            
               
                   
                 Drying 
                 Vacuum drying (120° C., 5 hrs) 
               
               
                   
                   
                 or hot air drying (120° C., 3 hrs) 
               
            
           
           
               
               
               
               
            
               
                   
                 Melt temperature 
                 300° 
                 C. 
               
               
                   
                 Mold temperature 
                 90° 
                 C. 
               
            
           
           
               
               
               
            
               
                   
                 Reference material 
                 BMS Makrolon 2808 
               
               
                   
                   
               
            
           
         
       
     
     The improvement in the balance of flow, impact, and aesthetics and/or the balance of flow, impact, and chemical resistance to sunscreen resulting from adding different amounts of polysiloxane copolymer to polycarbonate, compared to the addition of alternative core-shell impact modifiers is illustrated in Table 2: 
     
       
         
           
               
               
               
               
               
               
               
               
               
               
             
               
                 TABLE 2 
               
               
                   
               
               
                   
                   
                 CE1 
                 E2 
                 E3 
                 E4 
                 CE5 
                 CE6 
                 CE7 
                 CE8 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 PC3 
                 % 
                 49.49 
                 57.99 
                 36.99 
                   
                 57.99 
                 36.99  
                 36.99 
                 36.99 
               
               
                 PC4 
                 % 
                 50 
                 35 
                 50 
                   
                 35 
                 50 
                 50 
                 50 
               
               
                 PC1 
                 % 
                   
                   
                   
                 57.99 
                   
                   
                   
                   
               
               
                 PC2 
                 % 
                   
                   
                   
                 35 
                   
                   
                   
                   
               
               
                 PC-Si 
                 % 
                   
                 6.5 
                 12.5 
                 6.5 
                   
                   
                   
                   
               
               
                 IM1 
                 % 
                   
                   
                   
                   
                 2.8 
                 5.3 
                   
                   
               
               
                 IM2 
                 % 
                   
                   
                   
                   
                   
                   
                 3.22 
                   
               
               
                 IM3 
                 % 
                   
                   
                   
                   
                   
                   
                   
                 2.65 
               
               
                 PETS 
                 % 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 Irgafos 168 
                 % 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
               
               
                 CB 
                 % 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
               
               
                 MVR 
                 cc/10’ 
                 42 
                 42 
                 29 
                 37 
                 45 
                 35 
                 35 
                 33 
               
               
                 spiral flow at 
                 cm 
                 17 
                 18 
                 16 
                 17 
                 19 
                 18 
                 17 
                 17 
               
               
                 1 mm 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 (2200 bar/300° C.) 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 INI energy 
                 kJ/m 2   
                 8 
                 45 
                 53 
                 51 
                 44 
                 44 
                 46 
                 46 
               
               
                 @23° C. 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 INI energy 
                 kJ/m 2   
                 8 
                 16 
                 47 
                 34 
                 19 
                 40 
                 16 
                 24 
               
               
                 @0° C. 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 INI energy −10° C. 
                 kJ/m 2   
                 8 
                 14 
                 40 
                 17 
                 16 
                 37 
                 14 
                 13 
               
               
                 HDT 0.45 MPa 
                 ° C. 
                 134 
                 133 
                 133 
                 134 
                 133 
                 133 
                 133 
                 133 
               
               
                 L* metallized 
                 — 
                 6.2 
                 6.9 
                 7.6 
                 7.0 
                 12.3 
                 16.9 
                 14.3 
                 12.9 
               
               
                 part 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 ΔL* vs CE1 
                 % 
                 NA 
                 11 
                 23 
                 13 
                 98 
                 173 
                 131 
                 108 
               
               
                 Banana Boat ® 
                 % 
                 100% 
                 NA 
                 100 
                 NA 
                 NA 
                 0 
                 0 
                 0 
               
               
                 1%—1 Day— 
                   
                 break 
                   
                   
                   
                   
                   
                   
                   
               
               
                 TS % 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Banana Boat ® 
                 % 
                 100% 
                 NA 
                 44 
                 NA 
                 NA 
                 6 
                 4 
                 1 
               
               
                 1%—1 Day— 
                   
                 break 
                   
                   
                   
                   
                   
                   
                   
               
               
                 EB % 
               
               
                   
               
            
           
         
       
     
     As demonstrated by the data: 
     1. Pure melt polycarbonate with 42 MVR (CE1) had good gloss after metallization as indicated by low L* of 6.2, but has poor impact with low INI energy at room temperature of 8 kJ/m 2  and had brittle fracture.
 
2. The impact of polycarbonate was improved by the addition of sufficient quantity of an impact modifier (CE5-CE8), selected from acrylic (e.g., IM1), silicone (e.g., IM2) and MBS (e.g., IM3) core shell impact modifiers, resulting in ductile impact at room temperature with INI energy above 40 kJ/m 2 , while maintaining MVR above 30 and spiral flow comparable to CE1. However, in all cases, the L* of the metallized part was significantly increased by 100% or more, to values above 10, indicating that the high gloss metallized layer is lost to significant extent.
 
3. The impact of polycarbonate was also improved by the addition of PC-Si (E2 and E3), similar to IM1 (CE5 and CE6) and more efficient than IM2 and IM3 (CE7 and CE8), resulting in ductile impact at room temperature with INI energy above 40 kJ/m 2  (E2) or even at lower temperature (40 kJ/m 2  at −10° C. for E3, which contains higher amounts of PC-Si), while maintaining MVR above 29 and spiral flow comparable to CE1. However, PC-Si behaved in a different way than IM1-3 on aesthetics as an optimized and unexpected balance for gloss and impact improvement, given that PC-Si addition had significantly less negative effect on L* of the metallized part, which changes less than 25%, and remains below a value of 10, compared to 100% or more increase and values of above 10 for other impact modifiers.
 
4. Similar performance was achieved when interfacial PC (E4) was used instead of melt PC (E2) at same PC-Si loading, indicating polycarbonates from both interfacial and melt polymerization processes can be used.
 
5. Pure polycarbonate with 42 MVR (CE1) had limited resistance to exposure to sunscreen (e.g., Banana Boat®) and broke within 24 hours exposure under 1% strain. Compositions with impact modifiers had slightly improved chemical resistance and did not break during exposure, but have &lt;10% retention of yield stress (YS %) and elongation to break (EB %) (CE6-8). The only sample with good retention of yield stress (100%) and elongation to break (&gt;40%) was the composition containing PC and PC-Si (E3), and therefore offers a good balance of high flow and good chemical resistance.
 
     This demonstrates that the compositions containing PC and PC-Si can achieve a good balance of impact (ductile Izod notched impact at room temperature or lower temperatures), high flow (indicated by high MVR and/or spiral flow) and good gloss retention after metallization. 
     This also demonstrates that the compositions containing PC and PC-Si can achieve a good balance of impact (ductile Izod notched impact at room temperature or lower temperatures), high flow (indicated by high MVR and/or spiral flow) and good chemical resistance to chemicals such as, but not limited to, sunscreen. 
     
       
         
           
               
             
               
                 TABLE 3 
               
             
            
               
                   
               
               
                 Example and Control Compositions 
               
            
           
           
               
               
               
               
               
               
               
            
               
                 Component 
                 CE9 
                 CE10 
                 CE11 
                 E12 
                 E13 
                 E14 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 PC3 
                 5 
                 5 
                 5 
                 35.09 
                 35.09 
                 34.89 
               
               
                 PC4 
                 94.79 
                 94.49 
                 94.59 
                 55 
                 55 
                 55 
               
               
                 PC-Si 
                 0 
                 0 
                 0 
                 9.5 
                 9.5 
                 9.5 
               
               
                 PETS 
                 0 
                 0.3 
                   
                 0.25 
                   
                 0.3 
               
               
                 GTS 
                 0 
                   
                 0.2 
                   
                 0.2 
                 0.1 
               
               
                 Irgafos 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
               
               
                 CB 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
               
               
                 % Siloxane 
                 0 
                 0 
                 0 
                 1.9 
                 1.9 
                 1.9 
               
               
                 MVR 
                 30 
                 31 
                 30 
                 31 
                 31 
                 31 
               
               
                 Coefficient of 
                 49 
                 28 
                 35 
                 15 
                 13 
                 15 
               
               
                 Friction 
                   
                   
                   
                   
                   
                   
               
               
                 Ejection force 
                 646 
                 435 
                 506 
                 316 
                 312 
                 281 
               
               
                   
               
            
           
         
       
     
     As demonstrated by the data: 
     1. The coefficient of friction and ejection force were very high for pure melt polycarbonate with MVR of 30 with values around 50 and 650, respectively (CE9).
 
2. The coefficient of friction and ejection force were improved when release agents were added to melt polycarbonate with MVR of 30, such as PETS (CE10) and GTS (CE11), but values were still relatively high with a coefficient of friction of 28 (CE10) and 35 (CE11), and an ejection force of 435 (CE10) and 506 (CE11).
 
3. The addition of PC-Si to compositions containing melt polycarbonate and release agent (PETS, GTS or PETS and GTS, E12, E13 and E14 respectively) resulted in a significantly lower coefficient of friction and ejection force compared to similar compositions with PC-Si (CE10 and CE11) and similar for polycarbonate compositions with 0.3% release agent (PETS). Values for coefficient of friction of 15 and lower were achieved for E12-14 compared to values above 25 for CE10 and CE11, and values for ejection force of 320 and lower were achieved for E12-14 compared to values above 430 for CE10 and CE11.
 
     This demonstrates that compositions containing PC, Si—PC and release (PETS and/or GTS) have a good performance in having high flow, with MVR above 30, and good release performance, far outperforming similar compositions without PC-Si, having a coefficient of friction below 20 and ejection force below 400, which was not achieved by the comparative examples. As such, these compositions are more suitable for molds with relatively sharp draft angles. 
     Tables 4A and 4B: Example and Control Compositions 
     
       
         
           
               
               
               
               
               
               
               
               
             
               
                 TABLE 4A 
               
               
                   
               
               
                 Component 
                 CE16 
                 CE17 
                 E18 
                 E19 
                 E20 
                 E21 
                 E22 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                 PC1 
                 25 
                 30 
                 28 
                 28 
                 30 
                 30 
                 35 
               
               
                 PC2 
                 74.79 
                 65.29 
                 64.89 
                 64.79 
                 62.99 
                 62.79 
                 55.04 
               
               
                 PC-Si 
                 0 
                 6.5 
                 6.5 
                 6.5 
                 6.5 
                 6.5 
                 9.5 
               
               
                 PETS 
                 0 
                 0 
                 0.4 
                 0.5 
                   
                   
                 0.25 
               
               
                 GTS 
                 0 
                 0 
                   
                   
                 0.3 
                 0.5 
                   
               
               
                 AD1 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
               
               
                 AD2 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
               
               
                 % Siloxane 
                 0 
                 1.3 
                 1.3 
                 1.3 
                 1.3 
                 1.3 
                 1.9 
               
               
                 MVR 
                 30 
                 30 
                 31 
                 29 
                 32 
                 28 
                 29 
               
               
                 Coefficient of Friction  
                 62 
                 20 
                 17 
                 13 
                 16 
                 10 
                 16 
               
               
                 Ejection force 
                 631 
                 565 
                 351 
                 261 
                 350 
                 275 
                 332 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
               
               
               
               
               
               
               
             
               
                 TABLE 4B 
               
               
                   
               
               
                 Component 
                 E23 
                 E24 
                 E25 
                 E26 
                 E27 
                 E28 
                 E29 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
            
               
                 PC1 
                 35 
                 35 
                 30 
                 30 
                 30 
                 30 
                 30 
               
               
                 PC2 
                 55.09 
                 54.89 
                 57.19 
                 56.79 
                 57.19 
                 56.99 
                 56.79 
               
               
                 PC-Si 
                 9.5 
                 9.5 
                 12.5 
                 12.5 
                 12.5 
                 12.5 
                 12.5 
               
               
                 PETS 
                   
                 0.3 
                 0.1 
                 0.5 
                   
                   
                   
               
               
                 GTS 
                 0.2 
                 0.1 
                   
                   
                 0.1 
                 0.3 
                 0.5 
               
               
                 AD1 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
               
               
                 AD2 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
               
               
                 % Siloxane 
                 1.9 
                 1.9 
                 2.5 
                 2.5 
                 2.5 
                 2.5 
                 2.5 
               
               
                 MVR 
                 29 
                 30 
                 26 
                 25 
                 26 
                 27 
                 26 
               
               
                 Coefficient of friction  
                 15 
                 16 
                 15 
                 12 
                 14 
                 12 
                 9 
               
               
                 Ejection force 
                 330 
                 292 
                 329 
                 242 
                 341 
                 291 
                 235 
               
               
                   
               
            
           
         
       
     
     As demonstrated by the data: 
     1. The coefficient of friction and ejection force were very high for pure interfacial polycarbonate with MVR of 29 with values around 60 and 630 respectively (CE16).
 
2. The coefficient of friction and ejection force were improved when PC-Si was added to interfacial polycarbonate (CE17), though the coefficient of friction of 20 and especially the ejection force of 565 were still relatively high.
 
3. When using the combination of PC-Si and release agent selected from PETS, GTS or their combination (E18-E29), a significantly improved release performance was obtained with a coefficient of friction typically below 20 and ejection force below 350, compared to significantly higher values for CE16 and CE17.
 
4. Coefficient of friction and ejection force was optimized by increasing the release content and/or the PC-Si content, which allowed coefficient of friction values below 15 or even below 10 and ejection force below 300 or even 250.
 
     This demonstrates that compositions containing PC, Si—PC and release (PETS and/or GTS) have a good performance in having high flow, with MVR above 25, and good release performance, far outperforming similar compositions without PC-Si or release, having a coefficient of friction below 20, more preferred below 15 or even 10, and ejection force below 400, more preferred below 300 or even 250, which was not achieved by the comparative examples. As such, these compositions are more suitable for molds with relatively sharp draft angles. 
     
       
         
           
               
             
               
                 TABLE 5 
               
             
            
               
                   
               
               
                 Example and Control Compositions 
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 Component 
                 CE30 
                 CE31 
                 E32 
                 E33 
                 E34 
                 E35 
                 E36 
                 E37 
                 E38 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 PC1 
                 83.79 
                 50 
                 83 
                 50 
                 83 
                 43 
                 57 
                 37 
                 34 
               
               
                 PC2 
                 15.6 
                 44.99 
                 10.99 
                 42.99 
                 9.99 
                 49.99 
                 29.99 
                 49.99 
                 50.49 
               
               
                 PC-Si 
                 0 
                 4.5 
                 5.5 
                 6.5 
                 6.5 
                 6.5 
                 12.5 
                 12.5 
                 15 
               
               
                 PETS 
                 0.4 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 Irgafos 168 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
               
               
                 CB 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
               
               
                 Siloxane % 
                 0.0 
                 0.9 
                 1.1 
                 1.3 
                 1.3 
                 1.3 
                 2.5 
                 2.5 
                 3.0 
               
               
                 MVR 
                 28 
                 37 
                 44 
                 35 
                 44 
                 49 
                 32 
                 41 
                 38 
               
               
                 Flow 1.5 mm, 
                 26 
                 31 
                 32 
                 31 
                 31 
                 37 
                 29 
                 35 
                 34 
               
               
                 2200 bar) 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 INI@23° C. 
                 56 
                 52 
                 48 
                 57 
                 50 
                 50 
                 60 
                 53 
                 55 
               
               
                 INI@0° C. 
                 12 
                 21 
                 41 
                 44 
                 45 
                 21 
                 54 
                 49 
                 52 
               
               
                 Temp D/B ° C. 
                 5 
                 5 
                 −5 
                 −5 
                 −5 
                 0 
                 −25 
                 −15 
                 −30 
               
               
                 Gloss Units for 
                 1760 
                 NA 
                 NA 
                 NA 
                 NA 
                 1758 
                 NA 
                 1702 
                 1709 
               
               
                 metallized part 
                   
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                   
               
            
           
         
       
     
     As demonstrated by the data: 
     1. A composition based on interfacial PC and no impact modifier had an MVR of 28, and a ductile/brittle (D/B) transition of +5° C. Gloss of the metallized part was excellent visually and gives high value of 1760 (CE30).
 
2. The addition of PC-Si at relatively low siloxane content below 1% (CE31) in the total composition still resulted in relatively poor D/B transition of 5° C., very similar to CE30.
 
3. The addition of higher amounts of PC-Si resulted in siloxane contents in the composition above 1% (E32-E38), significantly improved D/B transition of 0° C. and lower, at MVR values of 30 and higher, while still retaining the high gloss values above 1700, for siloxane loadings ranging from 1.3% (E35) to 2.5 (E37) and 3.0 (E38).
 
4. Impact was further optimized via increasing the siloxane loading of the composition, comparing E36-E38 to E32-E35, with D/B transitions as low as −30° C., while still maintaining MVR above 30 and good metallization as indicated by very similar gloss, with values above 1700.
 
     This demonstrates that compositions containing PC, PC—Si and release (PETS and/or GTS) have a good performance in having high flow and impact performance and gloss retention after metallization for siloxane loadings of 1% and higher in the total composition. 
     
       
         
           
               
             
               
                 TABLE 6 
               
             
            
               
                   
               
               
                 Example and Control Compositions 
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                 Component 
                 CE39 
                 CE40 
                 E41 
                 E42 
                 E43 
                 E44 
                 E45 
                 E46 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                 PC3 
                 25 
                 50 
                 83 
                 50 
                 83 
                 0 
                 0 
                 0 
               
               
                 PC4 
                 74.29 
                 46.99 
                 10.99 
                 42.99 
                 9.99 
                 92.99 
                 86.99 
                 84.49 
               
               
                 PC-Si 
                 0 
                 2.5 
                 5.5 
                 6.5 
                 6.5 
                 6.5 
                 12.5 
                 15 
               
               
                 PAO 
                 0.5 
                 0 
                 0 
                 0 
                 0 
                 0 
                 0 
                 0 
               
               
                 PETS 
                 0 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 Irgafos 168 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
                 0.06 
               
               
                 CB 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
                 0.15 
               
               
                 Siloxane % 
                 0.0 
                 0.5 
                 1.1 
                 1.3 
                 1.3 
                 1.3 
                 2.5 
                 3.0 
               
               
                 MVR 
                 35 
                 40 
                 47 
                 36 
                 46 
                 58 
                 48 
                 43 
               
               
                 INI@23° C. 
                 15 
                 17 
                 33 
                 58 
                 43 
                 41 
                 49 
                 51 
               
               
                 INI@0° C. 
                 9 
                 13 
                 15 
                 23 
                 16 
                 23 
                 42 
                 44 
               
               
                 Temp D/B 
                 &gt;23 
                 23 
                 5 
                 −5 
                 5 
                 5 
                 −10 
                 −15 
               
               
                 Gloss Units on 
                 1777 
                 NA 
                 NA 
                 NA 
                 NA 
                 1769 
                 1726 
                 1757 
               
               
                 metallized part 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 Flow(1.5 mm, 
                 30 
                 30 
                 34 
                 31 
                 33 
                 37 
                 35 
                 35 
               
               
                 2200 bar) 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                   
               
            
           
         
       
     
     As demonstrated by the data: 
     1. A composition based on melt PC and no impact modifier had an MVR of 35, and a D/B transition of +23° C. Gloss of the metallized part was excellent visually and gave a high value of 1777 (CE39).
 
2. The addition of PC-Si at relatively low siloxane content of 0.5% (CE40) in the total composition resulted in relatively poor D/B transition of 23° C., very similar to CE39.
 
3. The addition of higher amounts of PC-Si resulting in siloxane contents in the composition above 1% (E41-E44) resulted in significantly improved D/B transition of 5° C. and lower, at MVR values of 30 and higher, while still retaining the high gloss values above 1700, for siloxane loadings ranging from 1.3% (E44) to 2.5 (E45) and 3.0 (E46).
 
4. Impact was further optimized by increasing the siloxane loading of the composition, comparing E45 and E46 to E41-E44, with D/B transitions as low as −15° C., while still maintaining MVR above 30 and good metallization as indicated by very similar gloss, with values above 1700.
 
     This demonstrates that compositions containing PC, PC—Si and release (PETS and/or GTS) have a good performance in having high flow and impact performance and gloss retention after metallization for siloxane loadings of 1% and higher in the total composition.