Patent Publication Number: US-4836913-A

Title: Catalytic cracking process exploying a zeolite as catalysts and catalyst supports

Description:
This is a division of application Ser. No. 802,542, filed Nov. 27, 1985, which is a continuation-in-part of U.S. Ser. No. 657,858 filed Oct. 5, 1984, now abandoned, which is a continuation-in-part of U.S. Ser. No. 484,435 filed Apr. 13, 1983, now abandoned. 
    
    
     This application is a continuation-in-part of U.S. Ser. No. 657,858 filed Oct. 5, 1984 which is a continuation-in-part of U.S. Ser. No. 484,435, filed Apr. 13, 1983, now abandoned. 
     The present invention relates to the preparation of catalyst supports and catalysts used for the conversion of hydrocarbons, and more particularly to the preparation of hydrocarbon cracking and hydroprocessing catalysts that are particularly effective for the processing of residual hydrocarbon feedstocks. 
     Catalysts which are used for the conversion of hydrocarbons typically comprise particulate inorganic oxide supports combined with catalytically active metals and/or crystalline zeolites. Hydroprocessing catalysts generally contain Group VI and/or Group VIII metals combined with a formed support component which comprises alumina or silica-alumina. Cracking catalysts comprise crystalline zeolites such as Type Y faujasite or ZSM zeolites which are prepared by combining the crystalline zeolite in finely divided form with an appropriate inorganic oxide matrix which comprises silica, alumina and/or clay. Clay, due to its low cost and availability, is a particularly attractive raw material for the preparation of catalysts. 
     U.S. Pat. No. 2,939,764 describes a method for preparing artificial bauxite wherein kaolin clay is calcined at a temperature of about 900° to 1000° C. and then treated with sodium hydroxide solution to leach or remove silica as a soluble sodium silicate. 
     U.S. Pat. No. 3,932,268 describes fluid cracking catalysts which comprise an ion exchanged faujasite type Y zeolite and an amorphous matrix wherein the matrix comprises the alumina-silica residue of caustic leached kaolin clay. The zeolite component is prepared in situ within a preformed calcined clay particle by the treatment of calcined kaolin microspheres with caustic. The remaining alumina-silica residue which is not converted to zeolite remains and serves as a catalyst matrix. 
     U.S. Pat. No. 4,235,753 describes a method for preparing shaped crystalline aluminisilicate containing particles wherein calcined clay particles are reacted in an aqueous alkaline medium which contains aluminosilicate nucleation centers. 
     Brindley and Nakahira in Journal of the American Ceramic Society, Vol. 42, No. 7, pp. 319 to 323 (1959) disclose that kaolinite is converted to a spinel-type phase when heated to about 925° to 950° C. which subsequently is progressively converted to mullite when heated to about 1050° to 1100° C. 
     In recent years the refining industry has been processing increasing amounts of metal containing residual hydrocarbon feedstocks. The metal, primarily vanadia and nickel, tend to deactivate catalysts, and thereby increase the overall cost of processing residual feedstocks. Accordingly, a significant requirement exists for hydrocarbon conversion catalysts which are resistant to the deactivating effects of vanadia and nickel and which may be prepared from readily available inexpensive raw materials such as kaolin. 
     It is therefore an object of the present invention to provide improved hydrocarbon conversion catalysts and catalyst components. 
     It is another object to provide cracking catalysts which are active for the conversion of residual hydrocarbon feedstocks to valuable lower molecular weight products such as gasoline and diesel fuel. 
     It is another object to provide hydroconversion catalysts and catalyst supports which are economical to prepare on a commercial scale and which are particularly resistant to the deactivating effects of metals contained in residual type feedstocks. 
     These, and still further objects of the present invention will become readily apparent to one skilled in the art from the following detailed description and specific examples. 
     Broadly, our invention contemplates catalysts, catalyst components, and catalyst supports which contain or comprise caustic leached spinel compositions which may contain substantial quantities of mullite. 
     More specifically, we have found that valuable catalysts and catalyst components may be prepared from a caustic leached spinel and mullite (hereinafter frequently referred to as CLS/mullite) which has a high concentration of acid sites that are resistant to hydrothermal deactivation. 
     The preparation of calcined leached kaolin clays (including spinels) is generally disclosed in the prior art. However, the CLS/mullite used in the practice of the present invention is particularly characterized by the ability to retain a high degree of catalytic activity as measured by acid-site stability, i.e. retention of acid-sites subsequent to hydrothermal treatment. This high degree of stability is obtained by careful control of the caustic leaching conditions, and in particular it is found that where the spinel (calcined kaolin) is leached (reacted with sodium hydroxide solution) for a period in excess of about 6 hours, a substantial amount of hydrothermal stability is lost. Accordingly, the CLS/mullite contemplated for use in the present invention is obtained by the following process. 
     (1) Kaolin, which has the general composition 2.0SiO 2  :Al 2  O 3  :0.01 to 0.10MO:H 2  O wherein Mo represents metal oxides such as iron and titanium, is heated to a temperature of about 900° to 1300° C. for about one-tenth to 6 hours to obtain a reactive spinel/mullite type compound having a spinel to mullite mole ratio of from about 1:0 to about 1:0.5. Temperatures of from about 900° to 1050° C. results in the formation of a composition which is essentially 100% spinel, whereas temperatures of 1250° to 1300° C. result in the formation of compositions which contain up to 50% mullite. Calcination temperatures of 900° to 1200° result in the preferred spinel-mullite composition in which the spinel phase comprises 50 to 100 mole percent of the composition and the mullite phase comprises 0 to 50 mole percent. 
     
                       TABLE A                                                     
______________________________________                                    
Comparison of Lattice Spacings and                                        
Lattice Parameters of the Spinel-Type                                     
Phase from Kaolinite and of Gamma Alumina.sup.1                           
Inten-   Spinel-type phase                                                
                         Gamma Alumina                                    
hkl  sity.sup.2                                                           
             (1)       (2)       (1)   (2)                                
______________________________________                                    
400  S       1.971(7.884)                                                 
                       1.973(7.892)                                       
                               1.976(7.904)                               
                                       1.977(7.908)                       
440  VS      1.394(7.885)                                                 
                       1.394(7.885)                                       
                               1.397(7.900)                               
                                       1.398(7.906)                       
444  W       1.138(7.884)      1.141(7.905)                               
731  W                         1.030(7.911)                               
800  VW                      0.9879(7.903)                                
840  VW                      0.8845(7.910)                                
______________________________________                                    
 .sup.1 G. W. Brindley and M. Nakahira, &#34;III, The High Temperature Phase,&#34;
 J. AM. Ceram. Soc., 42(7), 319-24.                                       
 .sup.2 S = strong, VS = very strong, W = weak, VW = very weak.           
 .sup.3 Kaolinite calcined at 950° C.                              
 
    
     If the composition is mostly in the silica-alumina spiral form the X-ray diffraction pattern of the compositions is similar to that described by Brindley and Nakahira as shown in Table A. If calcined at a higher temperature the compositions may contain a high level of mullite. Typical X-ray patterns (using only the strongest peaks) for these materials are shown in Table B: 
     
                       TABLE B                                                     
______________________________________                                    
SiO.sub.2 --Al.sub.2 O.sub.3 Spinel                                       
                         Mullite                                          
2 Q      Intensity       2 Q    Intensity                                 
______________________________________                                    
45.8     10              26.0   10                                        
67.3     10              40.8   8                                         
37.3     6               60.4   8                                         
39.5     6                                                                
46.5     6                                                                
______________________________________                                    
 
    
     (2) The reactive spinel/mullite obtained in step (1) is then combined with an alkali metal hydroxide solution, preferably sodium hydroxide solution in amounts which provide a spinel-mullite/NaOH/H 2  O reaction mixture having the following weight ratio ranges: 50 to 100 g spinel-mullite:1.0 to 60 g NaOH:65 to 1000 g H 2  O. 
     (3) The reaction mixture of step (2) is then heated at a temperature of about 50° to 100° C. for a period of one-quarter to 6 hours to extract (leach) from about 5 to 75 weight percent of the silica from the spinel as soluble sodium silicate. 
     (4) Subsequent to heating in step (3), the caustic leached spinel (CLS)/mullite is recovered by filtration and is washed with water and exchanged with mineral acids, ammonium or rare earth salts to remove Na +  and obtain a finely divided particulate CLS/mullite which has a silica to alumina mole ratio of from about 0.50 to 1.7, a nitrogen pore volume of 0.25 to 0.70, and an average pore diameter of from 50 to 100 Å, and an x-ray diffraction pattern very similar to gamma alumina. 
     Depending on the time and temperature of the initial calcination, varying amounts, i.e. 0 to 100% and preferably 0 to 50%, of the spinel may be converted to mullite, as determined by crystalographic X-ray diffraction analysis. As long as the calcination conditions (i.e. time, temperature) are such that the silica removed from the structure does not crystallize, a high surface area product which contains less than 0.20% Na 2  O is prepared. Since mullite is formed and decomposes at a higher temperature than the spinel phase, substantial conversion, ie. 10 to 50%, to mullite would be advantageous for use under severe process conditions. 
     To determine whether the CLS/mullite possesses the desired acid site concentration, a sample of CLS is subjected to temperature programmed desorption, using tertiary butyl amine, which is described as follows. 
     About 100 mg of catalyst is pretreated at 380° C. in flowing helium (He) (110 cc/min.) for one and one-half hours. After cooling to room temperature in flowing He, the catalyst is exposed to a He carrier stream (80 cc/min.) which passes through a tertiary butyl ammonium (TBA) saturator maintained at ice-water temperature until breakthrough of TBA is detected by a thermal conductivity (TC) cell. Excess TBA is then swept from the catalyst surface in flowing He and is assumed to be eluted when the TC response returns to baseline (about 5 minutes). The catalyst is then heated using a 12° C./min. rate to 380° C. in a flow of He (80 cc/min.). The resulting chromatogram consists of two (2) desorption peaks: a low temperature alpha peak associated with physisorbed TBA, and a high temperature beta peak associated with chemisorbed TBA. The area of the beta peak is a measure of the amount of &#34;strong&#34;  acidity; the temperature of the beta peak maximum is an index of acid site strength. Planimetered beta peak areas, corrected to a dry basis using loss on ignition at 954° C., were employed in the calculation of total strong acidity and acid site density. 
     To establish the resistance to hydrothermal degradation of the acid site content, i.e. stability, samples of CLS/mullite are typically heated to a temperature of 732° to 843° C. in the presence of saturated steam for a period of 5 to 12 hours. The acid site concentration is determined both prior and subsequent to hydrothermal deactivation, and it is found that the preferred CLS/mullite used in the practice of the present invention will retain at least about 70 percent of the acid-sites, and preferably from about 70 to 95 percent of the initial acid sites. 
     As indicated above, the CLS/mullite of the present invention is advantageously used in the preparation of hydrocarbon conversion catalysts and catalyst supports. In a preferred practice of the invention, the CLS/mullite is included as a component of fluid cracking catalysts (FCC) which comprises a zeolite such as type Y faujasite or ZSM zeo;lite, an inorganic oxide binder, such as silica alumina, silica alumina sols and hydrogels, the preparation of which are generally described in the following patents: U.S. Pat. Nos. 3,957,689, 3,912,619, 3,650,988, 4,144,194, and Canadian No. 967,136. Zeolites which may be included in the catalyst compositions are described in U.S. Pat. Nos. 3,293,192, 3,449,070, 3,402,996, 3,607,043, 3,676,368, 3,639,099, 3,808,326 and 4,164,551. 
     The techniques described in the aforesaid patents may be used in the preparation of catalysts including cracking catalysts which contain the CLS/mullite of the present invention. In a particularly preferred catalyst, the CLS/mullite is combined with a rare earth exchanged type Y zeolite, an alumina sol binder, and from about 20 to 80 parts by weight kaolin clay. Using the technique described in Canadian Pat. No. 967,136, catalysts which contain from about 5 to 50 weight percent zeolite, from about 10 to 20 percent alumina sol binder, from about 5 to 80 percent by weight CLS/mullite, from about 0 to 80 percent by weight kaolin clay are found to be particularly effective for the conversion of residual type hydrocarbons which contain substantial quantities of nickel and vanadium; sulfur and/or nitrogen. 
     In addition to using the CLS/mullite contemplated herein as a component for fluid cracking catalysts, it is also contemplated that the CLS/mullite may be formed into particles having a desired shape and size which are useful for the preparation of hydroprocessing catalysts. Typically, the CLS/mullite is formed using conventional extrusion, pilling, granulation, or sphere-forming techniques. 
     The hydroprocessing catalyst supports obtained using the CLS/mullite either alone or in combination with alumina and/or silica-alumina sols and gels, typically will possess the following characteristics: a surface area of 150 to 350 m 2  /g; a total pore volume 0.30 to 1.00 cc/g; a pore volume distribution wherein 0 to 0.1 cc/g is pores less than 20 Å in diameter, 0.20 to 0.60 cc/g in pores less than 100 Å in diameter, 0.05 to 0.20 cc/g in pores from 100 to 1000 Å in diameter, and 0.10 to 0.50 cc/g in pores greater than 1000 Å in diameter. The formed CLS/mullite-comprising particles may have particle size ranging from about 0.5 to 10 mm. In a particularly preferred form, the CLS/mullite is formed into spheres having a size as small as 0.5 to a size as large as 4 mm. 
     The hydroprocessing catalysts which may be obtained using the CLS/mullite supports of the present invention typically contain promoter metals selected from Group VI and Group VIII of the Periodic Table. In particular, it is found that metals such as cobalt, moly, nickel and tungsten, which are incorporated in the catalyst in amounts ranging from 0.5 to as much as 20 percent by weight are particularly effective for the hydroprocessing of residual type hydrocarbon feedstocks. Typically, these feedstocks, which contain substantial quantities of nickel and vanadia as well as sulfur and nitrogen, may be demetallized, desulfurized and/or denitrogenized using the catalysts contemplated herein. Conventional techniques for demetallization as well as desulfurization and denitrogenation involve treatment of the feedstock with hydrogen at pressure of 10 to 700 atm and temperatures of 300° to 600° C. in the presence of the catalyst described herein. 
     Having described the basic aspects of the present invention, the following examples are given to illustrate specific embodiments thereof. 
    
    
     EXAMPLE 1 
     This example shows that the starting kaolin must be calcined under conditions such that the 1750° F. exotherm observed in a DTA (differential thermal analysis) of kaolin is substantially reduced or eliminated. Samples of kaolin clay were heat treated for the time and temperature indicated in Table I. The samples were then aged at 100° C. under reflux or in sealed teflon bottles for the indicated time using different levels of NaOH. Calcined samples which still exhibited a substantial exotherm at about 1750° F. were not reactive as indicated by the low surface areas. The conversion of metakaolin to the spinel-like phase occurs fairly slowly at 1700° F. (about 2 hours or more), but is quite rapid (about 5 minutes) at 2000° F. Surface area of the caustic leached product is also dependent on caustic level, with increasing caustic level giving greater SiO 2  removal and hence increased surface areas. 
     
                                           TABLE I                                 
__________________________________________________________________________
Effect of Clay Calcination Temperature and Time on Caustic Leached        
Spinel                                                                    
                Time at Reflux                                            
                        Caustic Leach Conditions                          
                                     Surface Area                         
                                            1750° F.               
Sample No.                                                                
      Clay Calcination                                                    
                (Hrs.)  (g NaOH/g Clay/g H.sub.2 O)                       
                                     (m.sup.2 /g)                         
                                            on Exotherm                   
__________________________________________________________________________
1     3 hrs. @ 1350° F.                                            
                2       0.27/1/4.0    4     Yes                           
2     1/2hr. @ 1650° F.                                            
                2       0127/1/4.0    23    Yes                           
3     1 hr. @ 1700° F.                                             
                2       0.27/1/4.0    18    Yes                           
4     1/4hr. @ 1800° F.                                            
                2       0.23/1.4.0    46    Yes                           
5     1/2hr. @ 1800° F.                                            
                2       0.23/1/4.0    85    Sma                           
6     3/4hr. @ 1800° F.                                            
                2       0.23/1/4.0   125    None                          
7     1 hr. @ 1800° F.                                             
                2       0.23/1/4.0   108    None                          
8     11/2hrs. @ 1800° F.                                          
                2       0.23/1/4.0   127    None                          
9     1 hr. @ 1800° F.                                             
                2       0.63/1/4.0   204    None                          
10    2 hrs. @ 1800° F.                                            
                1       0.63/1/4.0   312    None                          
11    4 hrs. @ 1800° F.                                            
                1       0.63/1/4.0   279    None                          
12    6 hrs. @ 1800° F.                                            
                1       0.63/1/4.0   263    None                          
__________________________________________________________________________
 
    
     EXAMPLE 2 
     This example shows the higher caustic levels with less water produces a somewhat higher surface area caustic leached spinel. Kaolin clay was calcined for 1 hour at 1800° F. and then added to sodium hydroxide solutions at weight ratios given in Table II. After 2  hours of boiling under reflux the slurries were filtered and then washed on the filter twice with 5 g hot deionized water per g of starting clay. Thirty g of each of these products was then exchanged 3 times with 15 g ammonium sulfate in 300 g water. After each exchange the product was washed with hot deionized water, and oven dried. As shown by the data, even the lower surface area materials have substantial cracking activity after hydrothermal deactivation. 
     
                       TABLE II                                                    
______________________________________                                    
Effect of Caustic and Water Level on                                      
Caustic Leached Spinel Product                                            
        Caustic Leach Conditions                                          
                           Surface                                        
Sample No.                                                                
        (g NaOH/g Clay/g H.sub.2 O)                                       
                           Area, m.sup.2 /g                               
                                     MA.sup.1                             
______________________________________                                    
1       0.36/1/2.7         137       59                                   
2       0.36/1/3.4         108       40                                   
3       0.45/1/2.7         152       51                                   
4       0.45/1/3.4         130       54                                   
5       0.63/1/2.7         204       55                                   
6       0.63/1/3.4         181       54                                   
______________________________________                                    
 .sup.1 Microactivity at 930° F., 16 WHSV, 3 C/O after an 8 hour,  
 1350° F., 100% steam treatment on West Texas Heavy Gas Oil, volume
 % conversion.                                                            
 
    
     EXAMPLE 3 
     This example shows that sodium (Na 2  O) can be substantially eliminated from the caustic leached spinel by reaction with dilute sulfuric acid without substantial loss in alumina content of the product. 250 g of kaolin clay (calcined 1 hour at 1800° F.) was added to 675 ml H 2  O containing 157 g NaOH and boiled one-half hour under reflux. The slurry was filtered and the caustic leached product was washed with hot deionized H 2  O. After this wash the filter cake has about 4.5-5.5% Na 2  O and 76 weight % Al 2  O 3 . Samples of the above filter cake, equivalent to 50 g of the original calcined clay were reslurried in 200 ml solution of varying H 2  SO 4  concentration for one-half hour at approximately 150° F., filtered and washed with hot deionized H 2  O. The data in Table III indicate that most of the Na 2  O can be removed without substantial loss in the Al 2  O 3  content of the caustic leached product. 
     
                       TABLE III                                                   
______________________________________                                    
Effect of Acid Level on Na.sub.2 O                                        
Removal in Caustic Leached Spinel                                         
                           wt. %   wt. %                                  
Sample No.                                                                
         Acid Reslurry Conditions                                         
                           Na.sub.2 O                                     
                                   Al.sub.2 O.sub.3                       
______________________________________                                    
1        200 ml 0.50 M H.sub.2 SO.sub.4 /50 g                             
                           0.093   72.56                                  
         original spinel                                                  
2        200 ml 0.40 M H.sub.2 SO.sub.4 /50 g                             
                           0.12    73.69                                  
         original spinel                                                  
3        200 ml 0.30 M H.sub.2 SO.sub.4 /50 g                             
                           0.052   73.84                                  
         original spinel                                                  
4        200 ml 0.20 M H.sub.2 SO.sub.4 /50 g                             
                           0.038   74.87                                  
         original spinel                                                  
5        200 ml 0.10 M H.sub.2 SO.sub.4 /50 g                             
                           1.14    76.23                                  
         original spinel                                                  
______________________________________                                    
 
    
     EXAMPLE 4 
     This example shows the catalytic cracking activity which is retained by the CLS after thermal and hydrothermal deactivation. The data in Table IV indicates the caustic leached spinel, prepared as described below, loses little or no catalytic activity after a two hour 1800° F. thermal treatment or a 1550° F., 5 hour, 100% steam deactivation. It is noted for comparative purposes that an all-synthetic 25% Al 2  O 3  silica alumina cracking catalyst has a typical MA of about 27 after a 2 hour, 1800° F. thermal treatment. This sample was prepared by addition of 600 g kaolin clay (calcined 1 hour at 1800° F.) to a solution of 376.8 g NaOH in 1.62 liters deionized H 2  O. After boiling 1 hour under reflux, the caustic leached spinel was filtered, and washed 3 times with 1.0 liters hot deionized H 2  O. The filter cake was redispersed in 2.5 liters 1M H 2  SO 4 , filtered, washed on the filter 3 times with 2.0 liters hot deionized H 2  O and dried at 250° F. The dried product was crushed through a 30 mesh screen and then given the indicated thermal or hydrothermal treatments. 
     
                       TABLE IV                                                    
______________________________________                                    
Catalytic Cracking Activity of Caustic Leached Spinel                     
            Deactivation                                                  
Sample No.  Pre-Treatment      MA.sup.1                                   
______________________________________                                    
1           2 hrs. @ 1250° F.                                      
                               58.0                                       
2           2 hrs. @ 1400° F.                                      
                               66.9                                       
3           2 hrs. @ 1500° F.                                      
                               55.5                                       
4           2 hrs. @ 1600° F.                                      
                               63.2                                       
5           2 hrs. @ 1800° F.                                      
                               66.0                                       
6           5 hrs. @ 1500° F., 100% steam                          
                               60.4                                       
7           5 hrs. @ 1550° F., 100% steam                          
                               56.4                                       
______________________________________                                    
 .sup.1 Microactivity at 930° F., 16 WHSV, 3 C/O after the indicate
 thermal or hydrothermal treatment, volume % conversion.                  
 
    
     EXAMPLE 5 
     This example shows that commercially calcined clays which do not have a significant exotherm at about 1750° F. as measured by DTA are useful for producing the caustic leached spinel. Table V summarizes data on caustic leaching of various commercially available calcined kaolin clays. For all three samples, leaching with caustic increased alumina content from about 42 to about 70%, and loss of silica from the structure increased the surface area to greater than 300 m 2  /g. It is believed that these clays are calcined at approximately 1900° F. for about 10 minutes. 
     
                       TABLE V                                                     
______________________________________                                    
Caustic Leaching of Commercially Available Calcined Clays                 
Commercial Clay                     Al.sub.2 O.sub.3                      
Sample No.  Leach Conditions                                              
                            SA*     (wt. %)                               
______________________________________                                    
1           31.4 g NaOH/50 g clay,                                        
                            452     77.62                                 
            1 hr. at reflux                                               
2           31.4 g NaOH/50 g clay,                                        
                            304     75.48                                 
            1 hr. at reflux                                               
3           31.4 g NaOH/50 g clay,                                        
                            304     71.81                                 
______________________________________                                    
 *SA = Surface Area, m.sup.2 /g as determined by N.sub.2 adsorption.      
 
    
     EXAMPLE 6 
     This example shows that reflux time can be very brief. 200 g kaolin clay (calcined 1 hour at 1800° F.) was added to 540 ml H 2  O containing 125.6 g NaOH and 400 g of the same material also added to 1,080 ml H 2  O containing 201.0 g NaOH. The slurries were boiled under reflux with portions removed after the indicated time at reflux. After filtering and washing, these samples were exchanged to low Na 2  O with 3 exchanges at 150° F. using 20 g (NH 4 ) 2  SO 4  per 50 g clay starting material in 250 ml hot D.I. h 2  O. After each exchange the product was washed 1  time with 250 ml hot D.I. H 2  O and 3X after the third exchange. The results, given in Table IX, indicate very good catalytic cracking activities even at very short reflux times. 
     
                       TABLE VI                                                    
______________________________________                                    
Effect of Short Reflux Time on Surface Area of                            
Caustic Leached Spinel                                                    
Sample                                                                    
      Time at                                                             
No.   Reflux (Hrs.)                                                       
                 g NaOH/G Clay/g H.sub.2 O.sup.1                          
                                  SA.sup.2                                
                                        MA.sup.3                          
______________________________________                                    
1     1/4        0.5/1.0/2.7      190   55                                
2     1/2        &#34;                182   54                                
3     3/4        &#34;                178   52                                
4     1          &#34;                168   52                                
5     11/4       &#34;                161   55                                
6     11/2       &#34;                156   52                                
7     1/4        0.63/1.0/2.7     192   46                                
8     1/2        &#34;                212   52                                
9     3/4        &#34;                215   60                                
10    11/4       &#34;                199   58                                
11    11/2       &#34;                190   55                                
______________________________________                                    
 .sup.1 Clay used was kaolin calcined 1 hour at 1800° F.           
 .sup.2 Surface Area, m.sup.2 /g.                                         
 .sup.3 Microactivity data after (NH.sub.4).sub.2 SO.sub.4 exchange to les
 than 0.1% Na.sub.2 O after an 8 hour, 1350° F., 100% steam        
 treatment at 930° F., 16 WHSV, 3 C/O, vol. % conversion.          
 
    
     EXAMPLE 7 
     This example shows the surface properties of the caustic leached spinal powder. The caustic leached spinel was prepared by adding 100 g kaolin clay (calcined 1 hour at 1800° F.) to 196 ml solution containing 50.4 g potassium hydroxide and hot aging 2 hours in a sealed teflon bottle. The product was filtered, washed 2 times with hot deionized water and oven dried overnight at 250° F. The dried product was exchanged 3 times with 50 g (NH 4 ) 2  SO 4  in 500 ml) H 2  O for 1/2 hour at 160° F. The product was washed 1 time with 1 liter hot deionized H 2  O after the first and second exchanges, and 3 times with 1.0 liters after the third exchange to remove residual salts. 
     The data in Table VII summarizes the surface/hydrothermal properties of the caustic leached spinel. 
     
                       TABLE VII                                                   
______________________________________                                    
Surface/Hydrothermal Stability Properties of                              
Caustic Leached Spinel                                                    
                            2                                             
Sample N.sub.2 1            (8 hr. @ 1350° F.                      
(treatment)    (2 hr. @ 1000° F.)                                  
                            100% steam)                                   
______________________________________                                    
SA, total      182          164                                           
Total N.sub.2 PV                                                          
               0.756        0.780                                         
N.sub.2 PV 600 Å                                                      
               0.385        0.428                                         
N.sub.2 PV 20-600 Å                                                   
               0.371        0.352                                         
N.sub.2 PV 20 Å                                                       
                0            0                                            
SA in 20-100 Å Pores (%)                                              
               about 83     about 81                                      
______________________________________                                    
 SA = surface area (m.sup.2 /g)                                           
 PV = pore volume (cc/g)                                                  
 N.sub.2 PV 600 Å = nitrogen pore volume in pores greater than 600    
 Å in diameter.                                                       
 
    
     EXAMPLE 8 
     This example describes the use of the caustic leached spinel as an additive to SiO 2  sol bound catalysts as disclosed in U.S. Pat. No. 3,867,308, 11,250 g of kaolin was added to a solution of 7,065 g NaOH in 30 liters H 2  O. The slurry was boiled one hour, filtered, washed twice with 10 gallons hot H 2  O. After oven drying the solid was reslurried in 30 l 0.50M H 2  SO 4  for one-quarter hour at 150° F., filtered, washed twice with 10 gallons hot H 2  O, redispersed in 20 gallons hot H 2  o, refiltered and oven dried. 750 g dry basis of the above and 900 g SiO 2  --Al 2  O 3  basis Na-Y were dispersed in the minimum H 2  o in a blender, the pH adjusted to 4.0 using mixed H 2  SO 4  /alum solution and this slurry added to a slurry of 25.3 lbs. pH 3.0 SiO 2  sol (about 10% SiO 2 ) and 2200 g dry basis kaolin clay. After mixing the two slurries, the product was spray dried immediately. 
     EXAMPLE 9 
     This example describes the use of the caustic leached spinel as an additive to alumina sol bound catalysts. 600 g of low Na 2  O (about 0.3 wt.%) calcined rare earth Y zeolite, 650 g of the caustic leached spinel made in a similar manner to that in example 17 were blended together and added to 2,128 g of aluminum chlorhydroxide (23.5% Al 2  O 3 ) and 2,300 g dry basis kaolin clay as described in Canadian No. 967,136. The slurry was spray dried and the product calcined 1 hour at 1000° F. This product had good physical properties (Average Bulk Density/CD 0.76/0.81, Davison Index/Jersey Index 21/1.8), and excellent cracking activity (84.1 versus 67.8 for standard commercial catalyst). 
     EXAMPLE 10 
     This example shows that when the caustic leached spinel product is reslurried in acidic media, gelation can be brought about by addition of a base. Though gelation does not change the pore structure or cracking activity, it does produce a highly porous gel which filters and washes readily so that soluble salts can be readily removed. Many of the finer caustic leached spinels become peptized and difficult to filter upon reslurrying in acid due to slow filtration or they pass through filter paper. 11,250 g of kaolin was added to 30; l H 2  O containing 7,065 g NaOH and boiled 1 hour at constant volume. After filtering and washing twice with 10 gallons hot H 2  O, the filter cake was reslurried in 30 l 0.75M H 2  SO 4 . A portion was filtered and virtually all the product went through the filter paper. A separate portion of this slurry was treated with 30% NH 4  OH to pH 9.5, was filtered and then washed with hot H 2  O. This product had a surface area of 310 m 2  /g, % Al 2  O 3  of 69.84, % SO 4  of 0.23 and % Na 2  O of 0.12. This sample had a microactivity of 60.9 at 930° F., 16 Weight Hour Space Velocity, 3 C/O after an 8 hour, 1350° F., 100% steam treatment. 
     EXAMPLE 11 
     This example shows that the caustic leached spinel has substantial ability to resist deactivation by metals. 500 g kaolin clay was calcined 1 hour at 1800° F., boiled under reflux for 1 and one-quarter hours in 1.35 l H 2  O containing 314 g NaOH, filtered, and washed twice with 1.5 l hot H 2  O. The product was reslurried in 2 l 0.5M H 2  SO 4  for one-half hour at 150° F., filtered, washed 3 times with one 1 hot H 2  O, reslurried in one 1 pH 9.0 H 2  O (adjusted with 14% NH 3 ) for one-half hour, filtered and washed twice with 2 l hot H 2  O. These samples of the above product were calcined, impregnated with Ni+V in pentane solution and recalcined prior to steam deactivation and activity tests. The results, given in Table XIV, show substantial activity retention even at a high (1%) metals level. 
     
                       TABLE VIII                                                  
______________________________________                                    
Effect of Ni + V on Activity of Caustic Leached Spinel                    
Sample No.                                                                
          Wt. % Ni + V (1 Ni/2 V)                                         
                           Microactivity.sup.1                            
______________________________________                                    
1         0                68.0                                           
2         0.50             61.0                                           
3         1.00             54.9                                           
______________________________________                                    
 .sup.1 Microactivity catalytic cracking at 930° F., 16 WHSV, 3 C/O
 after an 8 hour, 1350° F., 100% steam treatment, volume %         
 conversion.                                                              
 
    
     EXAMPLE 12 
     This example shows that the caustic leached spinel can be produced with high surface areas at verying alumina content by changing the caustic leaching time. Separate samples of kaolin clay (calcined 1 hour at 1800° F.) were boiled for various amounts of time under reflux at 0.63 g NaOH/g calcined clay/2.7 g H 2  O. The products were filtered, washed twice with 5 g H 2  O/g clay, reslurried in 4 ml 0.5M H 2  OSO 4  /g clay for one-half hour at 150° F., filtered, washed twice with 5 g H 2  O/g clay and oven dried at 250° F. The data in Table XV indicate the caustic leached spinel produced has decreasing amounts of alumina as reflux time is extended, while still maintaining much of the surface area formed after 1 hour at reflux. 
     
                       TABLE IX                                                    
______________________________________                                    
Use of Increased Reflux Time to Reduce Al.sub.2 O.sub.3                   
Content in Caustic Leached Spinel                                         
Sample               Wt. %                                                
No.   Time at Reflux (Hrs.)                                               
                     Al.sub.2 O.sub.3                                     
                               Surface Area (m.sup.2 /g)                  
______________________________________                                    
1      1             about 70.0                                           
                               about 270                                  
2      4             61.1      242                                        
3      6             59.4      265                                        
4     24             52.6      186                                        
5     48             44.8      126                                        
______________________________________                                    
 
    
     EXAMPLE 13 
     Measurement of acidities of various caustic leached spinels (CLS) are summarized in Table X. These measurements were made using temperature programmed desorption with t-butylamine described previously. The results indicate the CLS prepared with a short hot age time retain a greater percentage of acid sites after steaming, i.e. have greater steam stability, than do samples prepared with long reflux times. We do not known why the stability is reduced with longer hot age. However, we observe that longer aging causes readsorption of some of the silicate originally removed from the clay and this may migrate on steam deactivation resulting in blocking (encapsulation) of the acid sites. 
     
                       TABLE X                                                     
______________________________________                                    
Effect of Reflux Time on Stability of Acid Sites                          
in Caustic Leached Spinel                                                 
Time at  g NaOH/100 Acidity/g  % Re-                                      
Reflux (hrs.)                                                             
         g Clay     Fresh   S13.5                                         
                                 tention                                  
                                       % Al.sub.2 O.sub.3                 
______________________________________                                    
1        10         20.6    14.6 71    about 50.6                         
1        15         17.5    16.2 93    about 54.3                         
1        44         40.3    30.2 75    about 70                           
6        62.8       51.6    12.2 24    59.4                               
24       41         29.7    15.6 52    48.0                               
______________________________________                                    
 
    
     EXAMPLE 14 
     This example shows that high surface area alumina rich materials can be produced from calcined clays which contain substantial amounts of mullite. Samples of kaolin were calcined for one-half hour at various temperatures and then caustic leached. 25 g of each material was slurried in 62.5 ml water containing 10.25 g sodium hydroxide, boiled under reflux for 1 hour, filtered, wased on the filter twice with 500 ml hot water, reslurried in 200 ml 0.25M H 2  SO 4  for one-quarter hour at 150° F., filtered, washed twice with 500 ml hot water and oven dried. The data is summarized in Table XI. 
     
                                           TABLE XI                                
__________________________________________________________________________
Sample No.                                                                
      Calcination Temperature (°F.)                                
                     Predominant Phases (X-ray).sup.2                     
                                   Surface Area (m.sup.2 /g)              
                                             % Al.sub.2 O.sub.3           
__________________________________________________________________________
1     2000           90% spinel (gamma alumina-                           
                                   391       74.22                        
                     like phase) and 10% mullite                          
2     2100           75% spinel and 25% mullite                           
                                   245       74.99                        
3     2200           75% mullite and 25% spinel                           
                                   108       69.24                        
__________________________________________________________________________
 .sup.1 All samples for onehalf hour at temperature.                      
 .sup.2 Anatase, quartz were also present as impurities, quantities of    
 spinel and mullite estimated by Xray diffraction.                        
 
    
     EXAMPLE 15 
     This example describes the preparation of silica sol bound catalysts containing a high level of caustic leached spinel and low zeolite level in order to produce high yields of light cycle oil. 
     (a) A large preparation of caustic leached spinel (CLS) was prepared by adding 15 Kg of kaolin clay (calcined for about 45 minutes at 1800°-1900° F. in a rotary kiln) to 40 l H 2  O containing 6 Kg NaOH. The slurry was hot aged 1 hour at 200° F., filtered, washed one time with 15 gallons hot deionized H 2  O, reslurried in 20 l H 2  O, adjusted the pH to 2.75 with 20% H 2  SO 4 , aged 15 minutes at pH 2.75, filtered, washed three times with 15 gallons hot deionized H 2  O and saved as a wet cake. The CLS product had the following analysis: 
     
         ______________________________________                                    
Total Volatiles      55.95                                                
Wt. % Na.sub.2 O     0.067                                                
Wt. % Al.sub.2 O.sub.3                                                    
                     68.51                                                
Surface Area (m.sup.2 /g)                                                 
                     276                                                  
Nitrogen Pore Volume (cc/g)                                               
                     0.37                                                 
______________________________________                                    
 
    
     (b) 1,800 g dry basis of the CLS along with 270 g SiO 2  /AL 2  O 3  basis calcined rare earth Y zeolite were dispersed in a blender in sufficient H 2  O to give a slurry of approximately 30% by weight solids. This slurry was then milled at a rate of 150 ml/minute, and then added to 33.1 lbs. of a silica sol at pH 3.0. This sol was prepared by pumping together a 12 Wt.% sodium silicate solution along with an acid alum solution (a mixture of 8.4 L of 77.2 g Al 2  O 3  from aluminum sulfate and 13.2 L of 20 Wt.% H 2  SO 4 ) through a mixing point. To the SiO 2  sol, (contaning 10 Wt.% SiO 2 ) CLS/zeolite slurry was added 2,430.4 g. dry basis kaolin clay, the slurry homogenized briefly by recirculation through a pump and then spray dried. 1 Kg of spray dried product was reslurried in 3.75 l H 2  O and filtered, the filter cake washed three times with 1 l 3% (NH 4 ) 2  SO 4  solution. The filter cake was then reslurried in 3.0 l H 2  O at approximately 70° C., filtered, rinsed on the filter with 1 l 70° C. H 2  O three times and oven dried overnight at 120° C. (Catalyst I). A second preparation (Catalyst II) was made using the same silica sol and calcined rare earth zeolite but increased level of CLS and reduced level of kaolin clay. The physical properties of these preparations are summarized in Table I and indicate these preparations have excellent density and attrition resistance. 
     (c) Microactivity results, summarized in Table XII indicated that Catalyst I and II have excellent coke selectivity, gasoline+distillate yields and light cycle oil yields greater than a silica sol bound catalyst containing only rare earth Y and kaolin (Catalyst III) and approximately the same as a SiO 2  --MgO+CREY catalyst known to be a good light cycle oil producer (Catalyst IV). 
     
                                           TABLE XII                               
__________________________________________________________________________
SiO.sub.2 Sol Bound CLS/Zeolite Catalysts.sup.1                           
                   Catalyst I       Catalyst II                           
__________________________________________________________________________
Composition        25% SiO.sub.2 Sol                                      
                                    25% SiO.sub.2 Sol                     
                   4.5% Calcined Rare Earth Y                             
                                    4.5% Calcined Rare Earth Y            
                   30% CLS          45% CLS                               
                   40.5% Kaolin Clay                                      
                                    25.5% Kaolin Clay                     
Total Volatiles (Wt %)                                                    
                   4.5              4.5                                   
Na.sub.2 O (Wt. %) 0.9              0.06                                  
SO.sub.4 (Wt. %)   0.27             0.24                                  
Average Bulk Density Index (g/cc)                                         
                   0.90             0.83                                  
Davison Index/Jersey Index                                                
                   6/0.5            10/0.8                                
SA (m.sup.2 /g)    113              133                                   
__________________________________________________________________________
Microactivity Comparison of SiO.sub.2 Sol Bound CLS/Zeolite Catalysts     
            Catalyst I                                                    
                      Catalyst II                                         
                                Catalyst III                              
                                          Catalyst IV                     
__________________________________________________________________________
Composition 25% SiO.sub.2 Sol                                             
                      25% SiO.sub.2 Sol                                   
                                66.9% SiO.sub.2 --MgO                     
                                          20% SiO.sub.2 Sol               
(Wt %)      4.5% Calcined Rey                                             
                      4.5% Calcined REY                                   
                                4.5% Calcined REY                         
                                          17% REY                         
            30% Caustic                                                   
                      45% Caustic                                         
                                28.6% Kaolin Clay                         
                                          63% Kaolin Clay                 
            Leached Clay                                                  
                      Leached Clay                                        
            40.5% Kaolin Clay                                             
                      25.5% Clay                                          
Microactivity Test Conditions:                                            
               500° C., 16 WHSV, 3 c/o on WTHGO after an 8 hour,   
               732° C., 100% steam deactivation.                   
Conversion  63.51     66.4      63.6      65.7                            
(Vol. %)                                                                  
H.sub.2 (W %)                                                             
            0.087     0.094     0.081     0.042                           
Total C.sub.1 + C.sub.2                                                   
            0.95      1.00      1.86      1.46                            
(W %)                                                                     
Total C.sub.3 (%)                                                         
            5.7       6.1       5.2       6.3                             
Total C.sub.4 (Wt %)                                                      
            7.9       8.7       8.2       7.9                             
C.sub.5.sup.+  Gaso. (%)                                                  
            60.5      61.8      57.9      57.2                            
Light Cycle Oil (%)                                                       
            16.9      17.4      17.6      13.0                            
Total Gasoline                                                            
            77.4      79.2      75.6      70.3                            
Distillate (%)                                                            
640° F. + Bottoms (%)                                              
            19.6      16.2      18.8      5.6                             
Coke (W % of Feed)                                                        
            1.4       1.7       2.5       1.92                            
Coke/Kinetic                                                              
            0.80      0.86      1.43                                      
Conversion                                                                
__________________________________________________________________________
 .sup.1 Samples pretreated for 2 hours at 1000° F. prior to analysi
                                                                          
 
    
     EXAMPLE 16 
     This example shows that addition of CLS to a silica sol bound catalyst allows reduction in usage of a low activity, and costly ultrastable zeolite, i.e. Z14US as described in U.S. Pat. Nos. 3,293,192 and 3,449,070. 
     (a) 2.4 Kg of a CLS (prepared as described in Example 15) and 1.6 Kg (dry basis) of ultrastable Y were dispersed in a blender at 30% solids and sandmilled together at 150 ml/min. This slurry was added to a pH 3.0 silica sol (2.0 Kg SiO 2  basis), 2.0 Kg kaolin clay added, the slurry mixed briefly and spray dried. This sample was exchanged to low Na 2  O by the same procedure used in Example 15. 
     (b) Microactivity results on this sample are compared in Table XIII to a preparation containing twice as much ultrastable Y zeolite and exchanged in the same manner. This sample with the caustic leached calcined clay had similar activity and coke yield compared to the base catalyst, but much improved bottom (feed boiling above 482° C.) conversion. This improved heavy ends conversion is useful where resids or other heavy, high molecular weight feeds are used. The increased H 2  yield may be an indication of increased olefin production which could indicate a higher octane gasoline. 
     
                       TABLE XIII                                                  
______________________________________                                    
Microactivity Comparison of SiO.sub.2 Sol Bound Ultrastable Y             
With/Without CLS                                                          
             Catalyst I Catalyst II                                       
______________________________________                                    
Composition (Wt %)                                                        
               25% SiO.sub.2 Sol                                          
                            25% SiO.sub.2 Sol                             
               20% Ultra-   40% Ultra-                                    
               stable Y     stable Y                                      
               30% Caustic  35% Kaolin Clay                               
               Leached Clay                                               
               25% Kaolin Clay                                            
Conversion (Vol. %)                                                       
               64.8         64.1                                          
H.sub.2 (W %)  0.107        0.054                                         
Coke (W % Feed)                                                           
               1.58         1.43                                          
Total Conversion (W %)                                                    
               74.2         77.4                                          
% 482° C. + Conv.                                                  
               93.2         90.0                                          
______________________________________                                    
 Microactivity Test Conditions 500° C., 16 WHSV, 3 c/o on a West   
 Texas Heavy Gas Oil after an 8 hour, 732° C., 100% steam          
 deactivation.                                                            
 
    
     EXAMPLE 17 
     This example shows that addition of CLS to a silica sol bound catalyst enhances tolerance to vanadium deactivation. 
     (a) Samples of catalyst were prepared by milling a 30 Wt % solids slurry of calcined rare earth Y or calcined rare earth Y with caustic leached calcined clay, adding this to a silica sol prepared as in Example 15, adding kaolin clay, mixing and spray drying. Both catalysts were exchanged to a low Na 2  O level using the same procedure as in Example 15. 
     (b) The composition and microactivity results summarized in Table XIV at 0, 0.67 Wt.% show: (1) addition of the caustic leached calcined clay component enhances activity (with/without V), and (2) addition of the caustic leached calcined clay component does not significantly change the coke yield on a coke/kinetic conversion basis). 
     
                       TABLE XIV                                                   
______________________________________                                    
Effect of CLS Additive for Vanadium Tolerance                             
           Catalyst I  Catalyst II                                        
______________________________________                                    
Composition (Wt %)                                                        
             20% SiO.sub.2 Sol                                            
                           20% SiO.sub.2 Sol                              
             22% Calcined RE Y                                            
                           22% Calcined RE Y                              
             58% Kaolin Clay                                              
                           15% Caustic Leached                            
                           Calcined Clay                                  
Wt. % V (added                                                            
             0.67          0.67                                           
before steaming)                                                          
Conversion (Vol. %)                                                       
             39.8          52.8                                           
H.sub.2 (W %)                                                             
             0.15          0.33                                           
H.sub.2 /Kinetic Conversion                                               
             0.23          0.29                                           
Coke (Wt %)  1.42          2.67                                           
Coke/Kinetic 2.15          2.39                                           
Conversion                                                                
Wt. % V      0             0                                              
Conversion (Vol. %)                                                       
             67.1          76.3                                           
H.sub.2 (W %)                                                             
             0.035         0.063                                          
Coke (W %)   3.8           4.4                                            
Coke/Kinetic 1.86          1.37                                           
Conversion                                                                
______________________________________                                    
 Microactivity Test Conditions 500° C., 16 WHSV, 3 c/o on a West   
 Texas Heavy Gas Oil after an 8 hour, 732° C., 100% steam          
 deactivation.                                                            
 
    
     (c) Physical properties for these samples are given in Table XV. The addition of the caustic leached clay additive causes no substantial change in density or attrition resistance, however surface area is significantly increased. 
     
                                           TABLE XV                                
__________________________________________________________________________
Physical Properties of SiO.sub.2 Sol Bound Caustic Leached Calcined Clay  
              Catalyst I Catalyst II                                      
__________________________________________________________________________
Composition (Wt %)                                                        
              20% SiO.sub.2 Sol                                           
                         20% SiO.sub.2 Sol                                
              22% Calcined RE Y                                           
                         22% Calcined RE Y                                
              58% Kaolin Clay                                             
                         15% Caustic Leached                              
                         Calcined Clay                                    
                         43% Kaolin Clay                                  
Average Bulk Density/                                                     
              0.88/0.96  0.85/0.89                                        
Compressed Density (g/cc)                                                 
Davison Index/Jersey Index                                                
                6/0.5      4/0.5                                          
Pore Volume: N.sub.2 /H.sub.2 O                                           
              0.05/.26   0.11/0.26                                        
(cc/g)                                                                    
Surface Area (m.sup.2 /g)                                                 
              122        188                                              
__________________________________________________________________________
 
    
     EXAMPLE 18 
     This example shows the use of a silica sol bound CLS particle as a physical blend component. 
     (a) A milled slurry of 4.0 Kg (dry basis) CLS (prepared as in Example 15) was added to pH 3.0 silica sol (2.0 Kg SiO 2  basis) and then 2.0 of kaolin clay was added, the slurry was briefly mixed and spray dried. This sample was exchanged to low Na 2  O by the same procedure as in Example 15. 
     (b) Physical properties and microactivity data are given in Table XVI. 
     
                       TABLE XVI                                                   
______________________________________                                    
Physical Properties and Microactivity Results on a 25%                    
Silica Sol Bound 50% CLS Blend Component                                  
                 Blend Component                                          
______________________________________                                    
Composition (Wt %)     25% SiO.sub.2 Sol                                  
                       25% Kaolin Clay                                    
                       50% CLS                                            
Physical Properties                                                       
Davison Index/Jersey Index                                                
                   7/0.6                                                  
Surface Area (m.sup.2 /g)                                                 
                   127                                                    
N.sub.2 Pore Volume (cc/g)                                                
                   0.16                                                   
Average Bulk Density (g/cc)                                               
                   0.85                                                   
Na.sub.2 O (Wt %)  0.031                                                  
Al.sub.2 O.sub.3 (Wt %)                                                   
                   49.17                                                  
Microactivity (MA)                                                        
Conversion (Vol. %)                                                       
                   54.9                                                   
H.sub.2, (%)       0.17                                                   
Coke, (Wt %)       3.56                                                   
______________________________________                                    
 MA Conditions: 500° C., 16 WHSV, 3 c/o on a West Texas Heavy Gas  
 Oil after an 8 hour, 732° C., 100% steam calcination              
 
    
     (c) A blend was prepared using this particle (80% by weight) along with a particle containing 24% SiO 2  sol binder, 35% calcined rare earth Y, 41% kaolin clay (20% by weight in the blend). 
     (d) Microactivity results on the blend (Catalyst I), summarized in Table XVII, indicate the blend produced similar LCO, G+D, and 338° C.+bottoms to the SiO 2  --MgO+CREY catalyst (Catalyst II) at significantly lower coke yield, and significantly higher LCO, G+D yields than a silica sol bound rare earth Y/kaolin catalyst (Catalyst III). 
     
                                           TABLE XVII                              
__________________________________________________________________________
Microactivity Comparison Using a Silica Sol Bound CLS Particle            
as a Blend Component with Zeolite FCC Catalyst to                         
Produce High LCO Yield With Good Coke Selectivity                         
          Catalyst I    Catalyst II                                       
                                   Catalyst III                           
__________________________________________________________________________
Composition                                                               
          Blend of      66.9% SiO.sub.2 --MgO                             
                                   20% SiO.sub.2 Sol                      
                        4.5% Calcined RE Y                                
                                   17% RE Y                               
                        28.6% Kaolin Clay                                 
                                   63% Kaolin Clay                        
             25% SiO.sub.2 Sol                                            
          80%                                                             
             25% Kaolin Clay                                              
             50% Caustic Leached                                          
             Calcined Clay                                                
             24% SiO.sub.2 Sol                                            
          20%                                                             
             35% Calcined RE Y                                            
             41% Kaolin Clay                                              
Conversion                                                                
          63.8          63.6       65.7                                   
(Vol. %)                                                                  
H.sub.2 (W %)                                                             
          0.079         0.081      0.042                                  
Total C.sub.1 + C.sub.2                                                   
          0.91          1.86       1.46                                   
(W %)                                                                     
Total C.sub.3 (%)                                                         
          5.9           5.2        6.3                                    
Total C.sub.4 (Wt %)                                                      
          11.3          8.2        7.9                                    
C.sub.5.sup.+  Gaso. (%)                                                  
          58.4          57.9       57.2                                   
Light Cycle Oil (%)                                                       
          17.7          17.6       13.0                                   
Total Gasoline                                                            
          76.1          75.6       70.3                                   
Distillate (%)                                                            
640° C. + Bottoms,                                                 
          18.5          18.8       21.3                                   
(%)                                                                       
Coke (W % of Feed)                                                        
          2.0           2.5        5.6                                    
Coke/Kinetic                                                              
          1.14          1.43       2.92                                   
Conversion                                                                
__________________________________________________________________________
 Microactivity Test Conditions: 500° C., 16 WHSV, 3 c/o on WTHGO   
 after an 8 hour, 732° C., 100% steam deactivation.                
 
    
     EXAMPLE 19 
     This example shows the good coke selectivity, octane enhancing capability and improved bottoms cracking of the SiO 2  sol bound ultrastable Y/caustic leached calcined clay combination. 
     (a) Table XVIII summarizes the physical properties of these catalysts. These catalysts were prepared by co-milling a 30% solids slurry containing the ultrastable Y and the CLS component, adding this to pH 3.0 silica sol, adding kaolin clay, mixing and spray drying. 
     (b) The exchange procedure on this series was modified from that in Example 15 in that some RE+ 3  is incoporated. 1.0 Kg of the spray dried product for Catalysts I and II in Table XVIII were exchanged as follows: (1) slurry in 3.8 l 70° C. H 2  O+filter; (2) Rinse on the filter 3 times with 1 l 3% (NH 4 ) 2  SO 4  ; (3) reslurry in 3.0 l 70° C. H 2  O and filter; (4) rinse on the filter 3 times 1.0 l 70°°C. H 2  O; (5) reslurry in 3.0 l H 2  O containing 31.2 grams mixed RECl 3  solution (30 Wt. % Re 2  O 3 ) and aged for 20 minutes at 66° C. at pH 4.9-5.0 (adjust pH as required with 3% NH 4  OH); (6) filter and  rinse on the filter 3 times with 1.0 l 70° C. H 2  O and oven dry overnight at 120° C. 
     Catalyst III in Table XVIII was prepared and exchanged in the same manner, except that the 91.3 grams RECl 3  solution was used for the rare earth exchange. 
     
                                           TABLE XVIII                             
__________________________________________________________________________
Physical and Chemical Properties of SiO.sub.2 Sol Bound Catalysts         
Containing Ultrastable Y and CLS                                          
          Catalyst I Catalyst II                                          
                                Catalyst III                              
__________________________________________________________________________
Composition                                                               
          20% SiO.sub.2 Sol                                               
                     20% SiO.sub.2 Sol                                    
                                20% SiO.sub.2 Sol                         
(Wt %)    25% Ultrastable Y                                               
                     25% Ultrastable Y                                    
                                17% Ultrastable Y                         
          10% Caustic Leached                                             
                     20% Caustic Leached                                  
                                55% Kaolin Clay                           
             Calcined Clay                                                
                        Calcined Y                                        
          45% Kaolin Clay                                                 
Na.sub.2 O (Wt. %)                                                        
          0.17       0.17       0.41                                      
Al.sub.2 O.sub.3                                                          
          34.34      35.67      30.65                                     
SO.sub.4 (Wt. %)                                                          
          0.20       0.16       0.37                                      
Re.sub.2 O.sub.3 (Wt. %)                                                  
          1.22       1.13       4.73                                      
Surface Area                                                              
          206        209        150                                       
(m.sup.2 /gm)                                                             
N.sub.2 Pore Volume/                                                      
          .14/.32    .13/.38    .10/.20                                   
H.sub.2 O Pore Volume                                                     
Average Bulk                                                              
          0.83       0.75       0.92                                      
Density (g/cc)                                                            
Davison Index/                                                            
            4/0.3    10/0.8       2/0.3                                   
Jersey Index                                                              
(g/cc)                                                                    
__________________________________________________________________________
 
    
     (c) Microactivity results summarized in Table XIX, indicate Catalyst I and II, the samples with the CLS component have improved bottoms (482° C.+) conversion, increased LCO and G+D, with no significant change in coke or gas yields. 
     
                                           TABLE XIX                               
__________________________________________________________________________
Microactivity Results on SiO.sub.2 Sol Bound CLS/Zeolite/Clay Catalysts   
          Catalyst I Catalyst II                                          
                                Catalyst III                              
__________________________________________________________________________
Composition                                                               
          20% SiO.sub.2 Sol                                               
                     20% SiO.sub.2 Sol                                    
                                20% SiO.sub.2 Sol                         
(Wt %)    25% Ultrastable Y                                               
                     25% Ultrastable Y                                    
                                17% Ultrastable Y                         
          10% Caustic Leached                                             
                     20% Caustic Leached                                  
                                55% Kaolin Clay                           
          Calcined Clay                                                   
                        Calcined Y                                        
          45% Kaolin Clay                                                 
                     35% Kaolin Clay                                      
Conversion                                                                
          65.5       73.2       67.1                                      
(Vol. %)                                                                  
H.sub.2 (W %)                                                             
          0.063      0.083      0.063                                     
Total C.sub.1 + C.sub.2                                                   
          0.92       1.26       1.32                                      
(W %)                                                                     
Total C.sub.3 (%)                                                         
          6.1        7.7        7.5                                       
Total C.sub.4 (Wt %)                                                      
          11.0       13.6       12.6                                      
C.sub.5.sup.+  Gaso. (%)                                                  
          60.6       65.4       59.1                                      
Light Cycle Oil (%)                                                       
          15.4       15.1       13.6                                      
Total Gasoline                                                            
          76.0       80.5       72.7                                      
Distillate (%)                                                            
338° C. + Bottoms, (%)                                             
          19.1       11.7       19.3                                      
Coke (W % of Feed)                                                        
          1.5        2.0        2.1                                       
Coke/Kinetic                                                              
          0.79       0.73       1.03                                      
Conversion                                                                
Total Conversion                                                          
          78.3       86.2       78.3                                      
482° C. + COnv.                                                    
          92.1       96.2       88.6                                      
__________________________________________________________________________
 Microactivity Test Conditions: 500° C., 16 WHSV, 3 c/o on a West  
 Texas Heavy Gas Oil after an 8 hour, 732° C., 100% steam treatment
                                                                          
 
    
     (d) Table XX compares the second catalyst from Table XIX with a commerical cracking catalyst in a riser unit test on Gas Oil. The CLS/clay/ultrastable Y catalyst bound with SiO 2  sol compared to the commercial catalyst yields the following observations: (1) gasoline of increased octane; (2) significantly reduced coke yields; and (3) better bottoms conversion as indicated by API gravity and aniline point. 
     
                       TABLE XX                                                    
______________________________________                                    
Riser Pilot Unit Comparison of SiO.sub.2 Sol Bound                        
Catalyst with Commercial Catalyst                                         
             CLS/Zeolite/Clay                                             
             Catalyst I    Catalyst II                                    
______________________________________                                    
Composition    20% SiO.sub.2       Commercial                             
               25% Ultrastable Y                                          
               20% CLS                                                    
               35% Kaolin Clay                                            
Conversion (Vol %)           70                                           
H.sub.2 (W %)  0.08                0.15                                   
Total C.sub.1 + C.sub.2 (W %)                                             
               1.7                 1.7                                    
Total C.sub.3 (%)                                                         
               8.5                 7.9                                    
Total C.sub.4 (%)                                                         
               12.1                11.5                                   
C.sub.5.sup.+  Gasoline (%)                                               
               62.5                63.0                                   
Research Octane Numbers                                                   
               91.2                89.4                                   
Motor Octane Numbers                                                      
               79.5                79.5                                   
Light Cycle Oil (V %)                                                     
               16.0                16.0                                   
Coke (W %)     3.0                 4.2                                    
HCO                                                                       
API Gravity    7.5                 11.0                                   
Aniline Pt.    130                 145                                    
______________________________________                                    
 Riser Unit Test Cond. 550° C., 8 seconds contact time, Sohio Gas  
 Oil, 6 c/o, 75 WHSV, yields interpolated to 70% conversion               
 Deactivation: 12 Hrs., 827° C., 20% steam equilibrium             
 
    
     EXAMPLE 20 
     This example shows that combining a low level of rare earth exchange with a low level of ultrastable Y and a high level of CLS allows a dramatic decrease in the amount of zeolite used while maintaining activity and high olefin yields which implies enhanced gasoline octane. Table XXI gives the formulation of two silica sol bound catalysts prepared by the general method of Example 15. The sample with the caustic leached calcined clay was given a final rare earth exchange (16.9 g. mixed RECl 3  solution @ 30% RE 2  O 3  /900 g. spray dried product) while the sample with ultrastable Y alone was only (NH 4 ) 2  SO 4  exchanged. The microactivity results set forth in Table XXI indicate the low rare earth exchanged CLS containing catalyst gave: (1) at least equal conversion; (2) no significant change in coke, gas yields; (3) increased G+D, gasoline and LCO, (4) reduced 338° C.+bottoms yields, and (5 ) at least equal gasoline octane as indicated by the high level of C 4  = /Tot. C 4 . 
     
                       TABLE XXI                                                   
______________________________________                                    
Microactivity Comparision of Ultrastable Y/CLS in SiO.sub.2               
Sol with Ultrastable Y alone                                              
           Catalyst I  Catalyst II                                        
______________________________________                                    
Composition (Wt %)                                                        
             20% SiO.sub.2 Sol                                            
                           20% SiO.sub.2 Sol                              
             15% Ultrastable Y                                            
                           40% Ultrastable Y                              
             40% CLS       35% Kaolin Clay                                
             20% Kaolin Clay                                              
Wt. % RE.sub.2 O.sub.3                                                    
             1.11          0.0                                            
Conversion (Vol %)                                                        
             64.5          60.0                                           
H.sub.2 (W %)                                                             
             0.096         0.094                                          
Total C.sub.1 + C.sub.2 (W %)                                             
             1.02          0.99                                           
Total C.sub.4 (%)                                                         
             11.5          11.5                                           
C.sub.4 =/Tot. C.sub.4                                                    
             0.55          0.49                                           
C.sub.5.sup.+  Gasoline (%)                                               
             58.7          53.0                                           
Light Cycle Oil (%)                                                       
             15.8          13.7                                           
Total Gasoline Distillate (%)                                             
             74.4          66.7                                           
338° C. + Bottoms                                                  
             19.8          26.4                                           
(%)                                                                       
Coke (W % Feed))                                                          
             1.9           1.5                                            
Coke/Kinetic Conv.                                                        
             1.05          1.00                                           
Total Conversion                                                          
             78.5          70.8                                           
% 482° C. + Conv.                                                  
             92.8          86.4                                           
______________________________________                                    
 Ma Conditions: 500° C., 16 WHSV, 3 c/o, on a West Texas Heavy Gas 
 Oil after an 8 hour, 732° C., 100% steam treatment.               
 
    
     The above examples clearly indicate that valuable hydrocarbon processing catalysts and catalyst supports may be obtained using the teachings of the present invention.