Patent Publication Number: US-4652314-A

Title: Process for producing products of Al-Li-Mg-Cu alloys having high levels of ductility and isotropy

Description:
The invention concerns a process for producing products of Al-base alloys essentially containing Li, Mg and Cu as main alloy elements and having a high level of ductility and isotropy. 
     The conventional production ranges schedule which comprise in particular an operation for homogenization of the initial products which are obtained either by casting or by powder metallurgy, optionally a scalping operation, hot transformation, cold transformation with one or more intermediate annealing operations if required, solution treatment and tempering, with an optional cold working operation for stress relief between the last two operations mentioned, when used in relation to alloys of the family Al-Li-Mg-Cu, result in mechanical tensile characteristics (tensile strength Rm, yield strength Rp 0.2 and ductility A%) which vary very substantially in dependence on the direction of measurement with respect to the principal direction of hot and cold transformation (long direction) of the products. 
     That is particularly true in regard to flat products such as plates, billets, strips or sheets. It results in well-known disadvantages in the subsequent operation of shaping the products, for example when pressing or stamping a sheet (the earing formation, local ruptures, etc . . . ) or upon final utilization thereof. 
     The method according to the invention makes it possible substantially to improve the isotropy of the mechanical characteristics of products of alloy type Al-Li-Mg-Cu, while also enhancing their ductility. 
     The method comprises subjecting a homogenized product to a hot transformation operation at a temperature of less than 420° C., in general between 100° and 400° C. and preferably between 300° and 350° C., to the desired final dimensions or to intermediate dimensions. When the final dimensions are directly attained, this &#34;tepid&#34; transformation operation is followed by conventional solution treatments (in general between 500° and 550° C. according to the alloy) and thermo-mechanical treatments for producing structural hardening. 
     The intermediate product is generally brought to the final dimensions by cold transformation, effecting one or more intermediate annealing operations, if that is required. Such operations may be carried out just before the cold transformation operation and/or in the course thereof. In that case, one of the above-mentioned annealing operations is carried out in a temperature range of between 200° and 550° C. The temperature hold times are of the order of from a few minutes to several hours, the shortest periods generally being associated with the highest temperatures. 
     It was observed that the rate of cooling after the intermediate annealing operation or operations is an important parameter of the process and is preferably to be between 1500° C./second and 30° C./hour. Rates higher than 1500° C./second are difficult to attain on an industrial scale, except in relation to a product of very small thickness, and rates of less than 30° C./hour do not provide any substantial improvement in isotropy. 
     As is known, the intermediate annealing operation or operations may be carried out in salt bath furnaces (nitrite-nitrate, nitrate-nitrate), or in static ventilated air furnaces, or in tunnel furnaces. 
     After the cold transformation operation, the products are subjected to the usual solution treatment, quenching and thermomechanical treatment for structural hardening, the solution treatment ipso facto constituting the final annealing operation. 
     The invention will be better appreciated by means of the following Examples relating to sheets, it being appreciated that it can be applied to other forms of worked products such as forged, die-stamped or extruded products. 
    
    
     FIGS. 1 and 2 show in polar coordinates the variations in the mechanical tensile characteristics obtained on sheets, according to the direction of measurement, in accordance with the conventional ranges (references A to F) or in accordance with the invention (references 1 and 2). 
    
    
     EXAMPLE 1 
     An alloy containing (by weight) 2.76% Li-1.32% Cu-1.04% Mg-0.11% Zr-0.02% Fe-0.02% Si, with the balance Al, was cast in the form of a plate measuring 300×100 mm, homogenized at 533° C. for 24 hours, scalped and hot rolled at 470° C.-420° C. to a thickness of 5 mm. 
     Taking that blank, the hot and cold transformation operations, down to a thickness of 1.6 mm, were carried out under the conditions set forth in Table I, in accordance with a conventional range, the hot rolling operation (HR) being performed at from 470° to 420° C. approximately and the cold rolling operation (CR) being performed at ambient temperature. 
     The sheets were then subjected to a solution treatment at 533° C. for 30 minutes (ventilated furnace), quenching with cold water, a controlled traction of 3.5%, then tempering for 24 hours at 190° C. 
     Tensile testpieces were taken off in the directions 0° (long direction L), 30°, 60° and 90° (long transverse direction LT) with respect to the direction of rolling. 
     Schedule 
     Annealing in a salt bath 533° C.-7 min 
     Quenching: cold water 
     Rolling: cold, to 1.6 mm 
     Solution treatment: 30&#39; at 533° C. in a salt bath 
     Quenching: cold water 
     Traction: controlled 3.5% 
     Tempering: 24 hours at 190° C. 
     Schedule 
     Annealing in a furnace in air 533° C.-7 min 
     Cooling: slow (25° C./hour) 
     Rolling: cold, to 1.6 mm 
     Solution treatment: 30&#39; at 533° C. in a salt bath 
     Quenching: cold water 
     Controlled traction: 3.5% 
     Tempering: 24 hours at 190° C. 
     Schedule 
     Annealing in a furnace in air 350° C.-1 hour 30 minutes 
     Cooling: slow (25° C./hour) 
     Rolling: cold, to 1.6 mm 
     Solution treatment: 30&#39; at 533° C. in salt bath 
     Quenching: cold water 
     Traction: controlled 3.5% 
     Tempering: 24 hours at 190° C. 
     The tensile testpieces were taken off under the same conditions as above. 
     The results obtained are set forth in Table II and are shown in graph form in FIGS. 1 and 2. 
     EXAMPLE 2 
     An alloy containing (% by weight) 2.10% Li-2.38% Cu-1.30% Mg-0.11% Zr-0.02% Fe-0.02% Si, the balance Al, was cast in plate form (300×100 mm), homogenized at 526° C. for 24 hours, rolled between 350° and 300° C. to a thickness of 3.2 mm, annealed at 350° C. for 1 hour 30 minutes in a furnace in air, subjected to slow cooling (20° C./hour), cold rolled to 1.6 mm in thickness, subjected to solution treatment at 526° C. for 30 minutes, quenched with cold water, subjected to 2% traction and subjected to tempering for 20 hours at 190° C. 
     The results of traction tests obtained in different directions are set forth in Table III. 
     EXAMPLE 3 
     An alloy containing (% by weight) 2.7% Li-1.6% Cu-1.0% Mg-0.11% Zr-0.04% Fe-0.03% Si, with the balance Al, was cast and transformed in accordance with the conditions specified in relation to Example 2, except as regards the controlled traction operation which was performed after quenching, which was at 5%. 
     The traction results obtained are set forth in Table IV. 
     The Examples according to the invention clearly show that the applied range results in highly isotropic products, the degree of elongation of which is generally higher than 7%. 
     
                                           TABLE I                                 
__________________________________________________________________________
Ref.                                                                      
Thickness                                                                 
      A     B     C     D     E     F                                     
__________________________________________________________________________
5  mm Annealing                                                           
            ↓                                                      
                  ↓                                                
                        ↓                                          
                              ↓                                    
                                    ↓                              
      ↓                                                            
            HR    ↓                                                
                        ↓                                          
                              ↓                                    
                                    ↓                              
      ↓                                                            
            ↓                                                      
                  HR    ↓                                          
                              ↓                                    
                                    ↓                              
4  mm CR    Annealing                                                     
                  ↓                                                
                        ↓                                          
                              ↓                                    
                                    ↓                              
      ↓                                                            
            ↓                                                      
                  ↓                                                
                        HR    ↓                                    
                                    ↓                              
3.2                                                                       
   mm ↓                                                            
            ↓                                                      
                  Annealing                                               
                        ↓                                          
                              ↓                                    
                                    ↓                              
      ↓                                                            
            ↓                                                      
                  ↓                                                
                        ↓                                          
                              HR    HR                                    
      ↓                                                            
            CR    ↓                                                
                        ↓                                          
                              ↓                                    
                                    ↓                              
2.5                                                                       
   mm Annealing                                                           
            ↓                                                      
                  ↓                                                
                        Annealing                                         
                              ↓                                    
                                    ↓                              
      ↓                                                            
            ↓                                                      
                  CR    ↓                                          
                              ↓                                    
                                    ↓                              
      CR    ↓                                                      
                  ↓                                                
                        ↓                                          
                              Annealing                                   
                                    ↓                              
2.0                                                                       
   mm ↓                                                            
            Annealing                                                     
                  ↓                                                
                        CR    ↓                                    
                                    ↓                              
      ↓                                                            
            CR    ↓                                                
                        ↓                                          
                              HR    ↓                              
1.6                                                                       
   mm ↓                                                            
            ↓                                                      
                  ↓                                                
                        ↓                                          
                              ↓                                    
                                    ↓                              
__________________________________________________________________________
 Annealing: 1 hour at 300° C., slow cooling (20 to 25°      
 C./hour) to 100° C.                                               
 
    
     
                                           TABLE II                                
__________________________________________________________________________
Directions                                                                
Long (0°)                                                          
               30° 60° Long transverse (90°)         
    Rp 0.2                                                                
        Rm     Rp 0.2                                                     
                   Rm     Rp 0.2                                          
                              Rm     Rp 0.2                               
                                         Rm                               
Range                                                                     
    (MPa)                                                                 
        (MPa)                                                             
            A %                                                           
               (MPa)                                                      
                   (MPa)                                                  
                       A %                                                
                          (MPa)                                           
                              (MPa)                                       
                                  A %                                     
                                     (MPa)                                
                                         (MPa)                            
                                             A %                          
__________________________________________________________________________
A   411 497 4.5                                                           
               413 492 6.2                                                
                          346 452 16.6                                    
                                     450 504 4.0                          
B   407 500 3.8                                                           
               411 470 4.5                                                
                          349 462 15.9                                    
                                     417 486 2.9                          
C   388 484 5.0                                                           
               412 472 5.0                                                
                          349 461 13.6                                    
                                     420 490 5.0                          
D   386 474 3.0                                                           
               412 489 6.6                                                
                          344 459 15.6                                    
                                     441 493 3.4                          
E   381 449 3.0                                                           
               418 479 4.0                                                
                          347 467 15.2                                    
                                     436 496 3.6                          
F   373 437 2.8                                                           
               408 466 3.4                                                
                          352 489 13.6                                    
                                     444 496 2.3                          
1   429 506 7.8                                                           
               414 499 8.1                                                
                          414 500  8.9                                    
                                     405 499 6.8                          
2 or 3                                                                    
    451 505 10.1                                                          
               452 510 10.1                                               
                          448 506 10.5                                    
                                     450 506 9.1                          
__________________________________________________________________________
 
    
     
                       TABLE III                                                   
______________________________________                                    
Angle between the direction                                               
of taking a testpiece and                                                 
the rolling direction                                                     
                 Rp 0.2 (MPa)                                             
                            Rm (MPa)  A %                                 
______________________________________                                    
 0°       406        457       12.0                                
30°       411        457       12.9                                
60°       399        458       13.2                                
90°       403        460       12.1                                
______________________________________                                    
 
    
     
                       TABLE IV                                                    
______________________________________                                    
Angle between the direction                                               
of taking a testpiece and                                                 
the rolling direction                                                     
                 Rp 0.2 (MPa)                                             
                            Rm (MPa)  A %                                 
______________________________________                                    
 0°       504        552       7.6                                 
30°       506        552       7.2                                 
60°       498        498       7.0                                 
90°       505        551       6.8                                 
______________________________________