Patent Publication Number: US-2022236176-A1

Title: Method and system to determine strength of dry wood products using near infrared imaging

Description:
RELATED APPLICATIONS 
     This application is a continuation-in-part of Bolton et al., U.S. patent application Ser. No. 16/687,311 (attorney docket number (BCC-003), filed on Nov. 18, 2019, entitled “METHOD AND SYSTEM FOR DETECTING MOISTURE LEVELS IN WOOD PRODUCTS USING NEAR INFRARED IMAGING,” which claims the benefit of David Bolton, U.S. 
     Provisional Patent Application No. 62/774,029, filed on Nov. 30, 2018, entitled “NEAR-INFRARED MOISTURE DETECTION IN WOOD PRODUCTS,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is related to Bolton et al., U.S. patent application Ser. No. 16/687,342 (attorney docket number BCC-006), filed on Nov. 18, 2019, entitled “METHOD AND SYSTEM FOR DETECTING MOISTURE LEVELS IN WOOD PRODUCTS USING NEAR INFRARED IMAGING AND MACHINE LEARNING,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 16/687,369 (attorney docket number BCC-007), filed on Nov. 18, 2019, entitled “METHOD AND SYSTEM FOR MOISTURE GRADING WOOD PRODUCTS USING SUPERIMPOSED NEAR INFRARED AND VISUAL IMAGES,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 16/205,027 (attorney docket number BCC-005), filed Nov. 29, 2018 and issuing Nov. 3, 2020 as U.S. Pat. No. 10,825,164, entitled “VISION SYSTEM FOR ANALYSIS OF WOOD PRODUCTS,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/074,956 (attorney docket number BCC-005CIP1), filed on Oct. 20, 2020 and issuing Dec. 14, 2021 as U.S. Pat. No. 11,200,663, entitled “METHOD AND SYSTEM FOR LAYERED WOOD PRODUCT PRODUCTION USING LOCAL ROBOTIC PANEL ASSEMBLY CELLS AND VISION SYSTEM ANALYSIS,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/084,397 (attorney docket number BCC-005CIP2), filed on Oct. 29, 2020 and issuing Jan. 11, 2022 as U.S. Pat. No. 11,222,419, entitled “METHOD AND SYSTEM FOR VENEER GRADING AND STACKING USING VISION SYSTEM ANALYSIS,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/523,578 (attorney docket number BCC-005CIP ICON), filed on Nov. 10, 2021, entitled “METHOD AND SYSTEM FOR LAYERED WOOD PRODUCT PRODUCTION USING LOCAL ROBOTIC PANEL ASSEMBLY CELLS AND VISION SYSTEM ANALYSIS,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/230,474 (attorney docket number BCC-013), filed on Apr. 14, 2021, entitled “METHOD AND SYSTEM FOR FULL VENEER SHEET GRADING AND STACKING,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/230,497 (attorney docket number BCC-017), filed on Apr. 14, 2021, entitled “METHOD AND SYSTEM FOR VENEER STRIP GRADING AND STACKING,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/513,416 (attorney docket number BCC-013CIP1), filed on Oct. 28, 2021, entitled “METHOD AND SYSTEM FOR PARTIAL VENEER SHEET GRADING AND STACKING,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 16/697,458 (attorney docket number BCC-004), filed on Nov. 27, 2019 and issuing Aug. 17, 2021 as U.S. Pat. No. 11,090,833, entitled “METHOD AND SYSTEM FOR ENSURING THE QUALITY OF A WOOD PRODUCT BASED ON SURFACE IRREGULARITIES USING NEAR INFRARED IMAGING,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/356,804 (attorney docket number BCC-004CIP1), filed on Jun. 24, 2021, entitled “METHOD AND SYSTEM FOR GRADING AND STACKING VENEER SHEETS USING NEAR INFRARED IMAGING,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/356,805 (attorney docket number BCC-004CIP2), filed on Jun. 24, 2021, entitled “METHOD AND SYSTEM FOR GRADING AND STACKING VENEER STRIPS USING NEAR INFRARED IMAGING,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/361,808 (attorney docket number BCC-004CIP3), filed on Jun. 29, 2021, entitled “METHOD AND SYSTEM FOR LAYERED WOOD PRODUCT PRODUCTION,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     This application is also related to Bolton et al., U.S. patent application Ser. No. 17/366,432 (attorney docket number BCC-004CIP4), filed on Jul. 2, 2021, entitled “METHOD AND SYSTEM FOR LAYERED WOOD PRODUCT PRODUCTION,” which is hereby incorporated by reference in its entirety as if it were fully set forth herein. 
    
    
     BACKGROUND 
     There are numerous classes and types of wood products currently used in a virtually limitless variety of construction and other applications. Wood product types include but are not limited to raw wood products such as logs, debarked blocks, green or dry veneer, and dimensional lumber; intermediate wood components, such as wood I-beam flanges and webs; and layered wood products such as laminated beams, plywood panels, Parallel Laminated Veneer (PLV) products and Laminated Veneer Lumber (LVL) products. 
     Layered wood products are one example of wood products that are now being used in new ways and for more and more structures. Layered wood products such as plywood, PLV, and LVL are composite products constructed in a factory from both natural wood and one or more chemically blended glues or resins. They are manufactured on a product assembly line and typically fabricated from multiple layers of thin wood, e.g., veneer sheets, assembled with one or more layers of adhesives bonding the veneer sheets together. 
     These layered wood products, sometimes referred to as “man-made” but more commonly referred to as “Engineered Wood,” offer several advantages over typical milled lumber. For instance, since layered wood products are fabricated and assembled in a factory under controlled conditions to a set of specific product specifications, they can be stronger, straighter, and more uniform than traditional sawn lumber. In addition, due to their composite nature, layered wood products are much less likely to warp, twist, bow, or shrink than traditional sawn lumber. Layered wood products can also benefit from the multiple grain orientations of the veneer layers and the resulting higher allowable stress capacities than a comparable milled lumber product. 
     However, as discussed herein, to achieve this potential it is often critical that the layers, such as veneer sheets, making up the layered wood products are accurately graded based on determined physical characteristics such as strength/density, surface texture, and moisture content to produce a panel of desired strength, thickness, and visual appearance. 
     The use of veneer, and particularly veneer that has uniform qualities such as consistent moisture content and strength/density, allows layered wood products of various dimensions to be created without milling a board of the desired thickness or dimension from a single log or single piece of lumber. This, in turn, allows for much more efficient use of natural resources. Indeed, without the use of various layered wood technologies, such as plywood, PLV, and LVL, the forests of the planet would have been depleted long ago simply to meet the construction needs of the ever-increasing world population. In addition, since layered wood products are fabricated in a factory under controlled specifications, layered wood products can be manufactured to virtually any dimensions desired, including dimensions such as length, width, and height well beyond dimensions that can be provided by milling from even the largest trees. 
     As noted above, the use of veneer layers in some layered wood products, such as plywood, PLV, and LVL, can also allow for better structural integrity since any imperfections in a given layer, such as a knot hole, can be mitigated by rotating and/or exchanging layers of veneer so that the imperfection is only one layer deep and is supported by layers of veneer below and above the imperfection in the layered wood products structure. However, these advantages are again dependent on the veneer layers being inspected for consistent features such as density/strength and moisture content. 
     As one specific illustrative example, veneer is a primary component of numerous intermediate and finished wood products. However, like most wood products, veneer can have widely varying levels of moisture and strength from sheet to sheet and even within the same sheet. Therefore, when working with veneer to produce intermediate or finished wood products, such as plywood or LVL, it is important to determine as accurately as possible the overall moisture content, distribution of moisture throughout a given sheet of veneer, and strength of the sheet of veneer. While this is particularly critical in the case of veneer, it is also important for any wood product and especially for those wood products used as layers or that are composed of layers. This is because the presence of various levels of moisture in these wood products and the strength of these wood products determines if the particular wood product under consideration will remain structurally sound during and after processing and to what purposes the wood products can be used to fulfill. 
     Veneer is typically created by peeling thin layers of wood from a parent log, or other lumber source, in a continuous manner. This process is similar to unrolling a bolt of cloth. The resulting relatively thin veneer layer or “ribbon” is then cut to specific veneer sheet dimensions. Typically, the resulting veneer sheets are then dried and stacked in layers and glued to each other under pressure and heat to produce a multilayer intermediate or finished wood product, such as LVL. 
     The use of veneer in this way is what allows wood products of various thickness and dimensions to be created without milling a board of the desired thickness or dimension from a single log or single piece of lumber. This, in turn, allows for much more efficient use of natural resources. However, the presence of excess moisture in veneer sheets can create serious problems. This is because, as noted above, the layers of veneer sheets, or any wood component used to produce a layered wood product, are glued together using heat and pressure. When the layers of veneer sheets, or other wood product, are stacked, moisture in the individual veneer layers can become trapped between these layers in moisture pockets. Then, when the stacked layers are subjected to pressure and heat, the moisture in the pockets becomes vaporized with no avenue of escape. Consequently, the vapor pressure can build to the point that pockets of trapped moisture create imperfections and bulges in the layered structure and/or the surface of the wood product. In some cases, the trapped vapor even causes cracks or structural blowouts in the layered wood product. This, of course, results in compromised structural integrity of the layered wood product and/or undesirable imperfections in the appearance of the layered wood product. 
     In addition, as noted, it is becoming more and more important to determine the strength of virtually every form of wood product due to new regulations and standards allowing the use of new types of wood products and new uses of existing wood products for various forms of construction. However, current methods and systems for determining the strength of a wood product are either non-existent or too inconsistent and unreliable to yield any consistently usable information. Therefore, current methods and systems for determining the strength of a wood product are largely ineffective for determining the best use of a wood product. Therefore, currently, many wood products are not put to their best, and most resource conserving use. 
     Therefore, there exists a long-standing technical problem of accurately determining the moisture level of wood products, and in particular, the moisture level of wood products, such as veneer sheets, that are to be used as components of layered wood products. In addition, any method or system used to detect moisture levels in wood products must also be effective and efficient enough to detect the moisture while not significantly slowing down the production process or otherwise adding to the cost of the end wood product. 
     In addition, there exists a long-standing technical problem of providing a reliable, consistent, and economically feasible method and system for determining the strength of wood products including veneer sheets and other wood products that are to be used as components of layered wood products. In addition, any method or system used to determine the strength of wood products must also be effective and efficient enough to detect strength related physical/mechanical parameters/characteristics while not significantly slowing down the production process or otherwise adding to the cost of the end wood product. 
     With respect to moisture detection, traditionally, the problem of detecting moisture levels in wood products such as veneer sheets has been addressed in one of two ways; using contact electrode moisture detection systems or using RF moisture detection systems. 
       FIG. 1A  is an illustration of one example of a prior art traditional contact electrode system  100 . 
     Using traditional contact electrode systems, such as traditional contact electrode system  100 , a veneer sheet  103 , or other wood product, is moved along a production conveyor belt or other conveyance system. At one or more points along the conveyor belt one or more high-voltage contact electrode structures  101  are positioned in physical contact with a surface  105  of the veneer sheet  103 , or other wood product. 
       FIG. 1B  is an illustration of one example of a contact electrode structure  101  of a prior art traditional contact electrode system. As seen in  FIG. 1B , in some cases, the contact electrodes structure  101  can take the form of metallic brushes whose electrode elements  102  are kept in contact with the surface  105  of the veneer sheet  103 , or other wood product, as the veneer sheet  103 , or other wood product, moves below the electrode elements  102 . 
     Various sub-systems  107  have historically been utilized to maintain contact pressure between the surface  105  of the veneer sheet  103 , or other wood product, and the contact electrode elements  102 . Traditionally, these include springs or weight loading. As discussed below, this configuration can represent a problem since this physical contact can damage either the surface  105  of the veneer sheet  103 , or other wood product, or damage the contact electrode structures  101 , or both. 
     Using traditional contact electrode systems, the electrodes must remain in contact with the surface of the veneer sheet being analyzed, and at specific distances from each other. This causes several issues given that the veneer sheet or other wood product moving beneath the electrodes is often uneven and therefore can easily damage and/or displace the electrodes, damage the surface of the veneer or other wood product, or damage both. This often results in damaged product and the need to replace electrodes. In addition, this physical contact configuration and the resulting damaged components also results in inconsistent readings and data. Further, maintaining a constant pressure of the electrodes with the surface of the veneer or other wood product is also difficult given the typically uneven surfaces of the veneer layer or wood product. 
       FIG. 1C  is a graphical representation of the placement and spacing of individual contact electrodes  101  using a typical traditional contact electrode system  100 . As seen in  FIG. 1C , contact electrodes  101  are spaced in rows  120  separated by row distances  121  and columns  130  separated by column distances  131 . Consequently, each row  120  defines a sample channel, such as sample channels 1 through 8, in  FIGS. 1C and 1D  (discussed below) as the surface  105  of the veneer sheet  103 , or other wood product, moves underneath contact electrodes  101  in direction  139 . 
       FIG. 1D  shows a typical sample sheet  140  generated using traditional contact electrode systems and the physical arrangement of  FIG. 1C . Referring to  FIGS. 1C and 1D , each sample channel 1 through 8 in  FIG. 1D  includes multiple sample areas  151 . In the specific illustrative example of  FIG. 1D  each sample channel 1 through 8 includes 16 sample areas  151 . Consequently, since there are 8 channels, there are 128 sample areas in this example of a typical configuration. In the specific illustrative example of  FIG. 1D , which is a typical traditional contact electrode system arrangement, each sample area  151  is of a width corresponding to the distance  121  between rows  120  of  FIG. 1C  and each individual sample area  151  is of a length corresponding to the distance  131  between columns  130  of  FIG. 1C . As a result, each sample area is distance  121  by distance  131  in dimensions or has an area of distance  131  by  121  square units. 
     In a typical configuration, distance  121  is 9″ and distance  131  is 3.″ Consequently, typical moisture measurements are taken in sample areas of approximately 9″×3″ simply because of the physical proximity and placement of contact electrodes  101 . 
     Consequently, the typical traditional contact electrode system structure shown in  FIG. 1C  presents another problematic issue associated with traditional contact electrode systems. This issue arises given that the approximately 9″×3″ dimensions of the sample areas  151  yields a of surface area of 27 square inches or so for each sample area  151 . This is a very low “resolution” in that pockets of moisture of surface areas less than 27 square inches can be missed entirely or given more weight than is warranted by the actual physical dimensions of the moisture pocket. Consequently, with only 128 sample points for a typical 4′ by 8′ sheet, the moisture levels of each of the 128 samples must be averaged to determine, at best, an average moisture level of the entire veneer sheet or wood product being analyzed. As a result of this, and several other inherent limitations of traditional contact electrode systems, the moisture level of a given veneer sheet or other wood product can consistently only be determined within about a ±5% margin of error using traditional contact electrode systems. In addition, the exact location of pockets of moisture cannot be accurately determined using traditional contact electrode systems. 
     These relatively large margins of error associated with traditional contact electrode systems, and the inability to determine the exact location of pockets of moisture, results in the need to be very conservative when determining the potential use of a given veneer sheet or other wood product. Therefore, using traditional contact electrode systems, wood products, such as veneer sheets, are often not put to their most cost effective and efficient use simply to ensure that the ±5% margin of error does not result in inferior or unsafe wood products. Clearly, this is an inefficient use of a valuable natural resource and a problematic situation for both the producer of the wood products and the end customer who inevitably must pay a higher price to take these inefficiencies into account. 
     Another issue associated with traditional contact electrode systems is the fact that these systems rely on high voltages. Therefore, traditional contact electrode systems can represent a danger to workers and other equipment. Consequently, various barriers and safety systems must be put into place when implementing contact electrode systems. In addition, the many repairs that are associated with these systems due to the physical contact requirements discussed above require shutting down the production line and ensuring various safety procedures are implemented and adhered to before the problem can be fixed. This results in lost time and further production inefficiencies. Further, the production of the high-voltages necessary to operate traditional contact electrode systems requires significant energy which, in turn, adds to the cost of production and the cost of the product. 
     The second type of traditional systems used to detect moisture in wood products are Radio Frequency (RF) systems. 
       FIG. 2A  is an illustration of one example of a prior art traditional RF moisture detection system  200 . 
     Traditional RF moisture detection systems, such as traditional RF moisture detection system  200 , rely on the generation of RF signals which are then transmitted using RF transmitters  205  onto the surface  203  of, and through, the veneer sheet  201  or other wood product to RF receivers  209 . RF moisture detection systems do represent an improvement over traditional contact electrode systems in that the RF moisture detection systems do not require physical contact with the surface of veneer sheet or other wood product. However, the distance  207  between the source of RF energy  205  and the surface  203  of the veneer sheet  201  or other wood product, and the distance  208  between the RF receiver  209  and surface  204  of veneer sheet  201  ( FIG. 2B ) must be relatively small and precisely maintained to avoid interference and to obtain accurate results. 
     This is graphically illustrated in  FIG. 2B  which shows a side view of RF transmitter  205  positioned a distance  207  above surface  203  of veneer sheet  201  and RF receiver  209  positioned a distance  208  below a surface  204  of veneer sheet  201 . Since distances  207  and  208  are often less than an inch, and veneer sheet  201  surfaces  203  and  204  are often rough and uneven, damage to the RF moisture detection system  200  and surfaces  203  and  204  of the veneer sheet  201  is still a frequently encountered problem as the veneer sheets move past/between the RF transmitter  205  and RF receiver  209 . 
       FIG. 2C  shows a graphic illustration of a typical arrangement of RF transmitters  205  over a surface  203  of a veneer sheet  201  moving in direction  220  via conveyor belts  221 , thereby creating sample channels 1 through 8. 
       FIG. 2D  shows a sample sheet  240  created using the RF transmitter arrangement shown in  FIG. 2C . As seen in  FIG. 2C , like traditional contact electrode systems, RF moisture detection systems are limited in the size of the sample  251  that can be tested on the surface of a veneer sheet or wood product. As seen in  FIG. 2D , each sample  251  area is of dimensions “x” by “y.” Traditionally, RF moisture detection systems utilize RF chambers that typically have a sample size of 12″×12.″ i.e., “x” is equal to 12″ as is “y.” Consequently, for a typical 4′×8′ veneer sheet, the number of samples  251  is typically 32 with each sample representing 144 square inches of surface area. 
     Therefore, like traditional contact electrode systems, RF moisture detection systems have relatively low “resolution” in that pockets of moisture of surface areas less than 144 square inches can be missed entirely or given more weight than is warranted by the actual physical dimensions of the moisture pocket. Consequently, with only 32 sample points for a typical 4′ by 8′ sheet, the moisture levels of each of the 32 samples  251  must be averaged to determine, at best, an average moisture level of the entire veneer sheet or wood product being analyzed. As a result of this, and several other inherent limitations of RF moisture detection systems, the moisture level of a given veneer sheet or other wood product can consistently only be determined within about a ±7.5% margin of error using RF moisture detection systems. Further, the exact location of pockets of moisture cannot be accurately determined using RF moisture detection systems. 
     In addition, RF moisture detection systems are subject to interference from spurious RF energy that is often present in an industrial environment such as a wood processing plant. 
     Consequently, like traditional contact electrode systems, while traditional RF-based moisture detection systems do give some indication of the moisture level of a veneer or wood product being analyzed, the relatively large margins of error and inability to determine the exact location of pockets of moisture results in the need to be very conservative when determining the potential use of a given veneer layer or other wood product. Therefore, as with traditional contact electrode systems, the use of traditional RF-based moisture detection systems often results in wood products such as veneer sheets not being put to their most cost effective and efficient use simply to ensure that the ±7.5% margin of error does not result in structurally unsound product. As noted above, this is neither an ideal situation for the producer of the wood products or the end customer who inevitably must pay a higher price to take into account these inefficiencies. 
     As noted, another important physical characteristic for virtually every form of wood product is the strength of the wood product. This has become an increasingly important parameter associated with wood products due to new regulations and standards allowing the use of new types of wood products and new uses of existing wood products for various forms of construction. In short, in order to put a given wood product to its best use, and thereby utilize natural resources most effectively, it is becoming more and more important to accurately and consistently determine the strength of the wood product. 
     In the prior art, the strength of a wood product was either assumed or estimated based on related physical/mechanical parameters associated with the wood product. One important physical/mechanical parameter for determining the strength of virtually every form of wood product using prior art systems is the density and resulting strength of the wood product. 
     However, the currently used methods and systems for determining the density, and therefore the strength, of wood products, including veneer sheets, and various other materials is antiquated and extremely inefficient and ineffective in terms of the accuracy of density measurements. This inaccuracy of prior art methods and systems for determining the density of material is due in large part to the rather antiquated mechanical components used with prior art methods and systems for determining the density of material. 
     For example, one established method and system for determining the density, and therefore strength, of a sheet of material, such as a sheet of veneer or other wood product, involves the use of prior art contact electrode systems and ultrasonic density detection systems similar to the RF detection systems used for moisture detection discussed above. When measuring density, these prior art systems are commonly referred to as stress wave analyzers or ultrasonic density detection systems. In their simplest form, prior art ultrasonic density detection systems convey a sheet of material, such as veneer, on a conveyor belt to a density analysis station. At the density analysis station, the sheet of material is run between a rubber lined lift wheel and a transmitter or receiver transducer wheel including a transmitting or receiving transducer element. In this way a portion of the sheet of material is maintained or “pinched” between the lift wheel and the transmitter or receiver transducer wheel. 
     Herein the term transducer includes either a transmitter, receiver, or both. Consequently, the terms transducer and transmitting transducer can be used interchangeably as can the terms transducer and receiving transducer. Therefore, as a specific example, a transmitting transducer wheel can also be referred to generically as a transducer wheel and a receiving transducer wheel can also be generically as a transducer wheel. 
     Using typical ultrasonic density detection systems, a minimum of two transducer wheels, and two lift wheels, are utilized in pairs of transmitting transducer wheel/lift wheel and pairs of receiving transducer wheel/lift wheel. In some embodiments two or more transducer wheels and/or lift wheels are used. The sheet of material, e.g., sheet of veneer, is then conveyed by the conveyor belt between the transmitting transducer wheel and lift wheel and the receiving transducer wheel and lift wheel so that a first portion of the sheet of material is in contact with the transmitting transducer wheel and lift wheel at the same time a second portion of the sheet of material is in contact with the receiving transducer wheel and lift wheel. The transmitting transducer wheel and lift wheel pair and the receiving transducer wheel and lift wheel are typically separated by a precisely defined distance, often around six feet. 
     Once the first portion of the sheet of material is between the transmitting transducer wheel and lift wheel and, at the same time, the second portion of the sheet of material is between with the receiving transducer wheel and lift wheel, the transmitting transducer wheel emits an ultrasonic signal (typically in pulses). By separating the transmitting transducer wheel and receiver transducer wheel the defined fixed distance apart, an ultrasonic pulse transmitted into the first portion of the sheet of material by the transmitting transducer wheel then travels through the sheet of material and can be received by the receiving transducer wheel at the second portion of the sheet of material by passing through the sheet of material between the transmitting transducer wheel and receiver transducer wheel. 
     Since the distance between the transmitting transducer wheel and receiver transducer wheel is known, the density of the sheet of material can be determined by measuring the time it takes the ultrasonic pulse to travel from the transmitting transducer wheel, through the known distance in the sheet of material, to the receiver transducer wheel. The density of the sheet of material can then be determined based on the pulse travel time with shorter travel times indicating higher densities and longer travel times indicating lower densities. The correlation of pulse travel time to density will vary from material to material. 
     Once the density of the sheet of material is known, this can be used to determine a relative strength of the sheet of material with higher densities generally equating to higher strength and lower densities generally equating to lower strength. The correlation of the density of the sheet of material to the strength of the sheet of material will also vary from material to material. 
     As the sheet of material moves through the prior art ultrasonic density detection systems and the transmitting transducer wheel/lift wheel and receiver transducer wheel/lift wheel pairs, multiple density readings are captured at multiple locations along the sheet of material, such as veneer. A reading taken every one to two inches along the sheet of material is common. 
     Once the density of the sheet of material is determined by prior art ultrasonic density detection systems, this information can be used to determine a relative strength of the sheet of material, with higher densities generally equating to higher strength and lower densities generally equating to lower strength. 
     Most of the basic design and components of prior art ultrasonic density detection systems discussed above have not significantly changed in over forty years. Consequently, while prior art ultrasonic density detection systems can be used to gain a general indication of the strength of a sheet of material, such as veneer, the accuracy and consistency of the measurements obtained from prior art ultrasonic density detection systems are far from ideal. As discussed above, it is now often critical that a very accurate measure of the density/strength of a sheet of material, such as veneer, be made. Unfortunately, prior art ultrasonic density detection systems, such as prior art ultrasonic density detection systems, often fail to rise to the standards of accuracy and consistency required for newer materials and structures. 
     It is important to note that the accuracy and reliability of density measurements taken using prior art ultrasonic density detection systems is almost entirely dependent on keeping a constant pressure on a transducer wheel, and therefore keeping the pressure/force of transducer wheel on the surface of a sheet of material constant. Any variation in this pressure/force will result in less accurate density readings, with larger variations resulting in larger inaccuracies. Using prior art ultrasonic density detection systems this is problematic for several reasons. 
     First, as a relatively antiquated mechanical/pneumatic system, the accuracy and consistency of the pressure/force provided to the transducer wheel on the surface of the sheet of material by prior art ultrasonic density detection systems is not only of questionable accuracy but is also highly inconsistent and subject to significant and unacceptable error and interference. 
     When a typical prior art ultrasonic density detection system is used to analyze sheets of veneer, the prior art ultrasonic density detection system uses a pneumatic position system air bag as part of the mechanical/pneumatic system that keeps the transducer wheel on the surface of the sheet of material. This pneumatic position system air bag is typically kept at a pressure of twenty-five to thirty PSI as read by a standard pressure gauge. Between inaccuracies in gauge reading and the physical make up of prior art pneumatic position system air bag, there is often a three PSI or more error in the actual PSI and gauge PSI at any given time. Consequently, as an illustrative example, anytime the gauge reads a desired twenty-six PSI, the actual PSI can be anywhere between twenty two PSI and twenty nine PSI. This, in turn can result in a variance of twelve to sixteen percent in the actual pressure applied by transducer wheel on the surface of sheet of material. Of course, this can result in a significant variance in density readings from actual density from pulse to pulse in the same sheet of material and can result in a ten percent or more inaccuracy of the measured density of the sheet of material, in this case veneer. For this reason alone, prior art ultrasonic density detection systems are unable to provide the accuracy and consistency now required. 
     Another problem arises when the sheet of material first enters the position between transmitting transducer wheel and its lift wheel. When the transducer wheels are lifted by the introduction of the sheet of material this “shock” can cause prior art a traditional transducer lever arm to over pivot, bounce back and forth, and cause transducer wheels to bounce up and down. During this bounce/recovery time, no reliable density reading can be obtained. In many instances, such as when the sheet of material is veneer, the sheet of material can be moving at a relative high rate of speed, as noted up to seven hundred and fifty feet per minute. Consequently, during this bounce/recovery time, as much as ten percent of the length of the sheet of material  133  passes by while no accurate density reading can be obtained. 
     In addition, the physical shape of lift wheels used with prior art ultrasonic density detection systems is subject eccentricity due to manufacturing imperfections and wear and tear resulting from the rebound force associated with the significant mass of prior art ultrasonic density detection systems. These factors also cause a variation in applied force/pressure on transducer wheel that cannot be effectively identified, measured, or compensated for using prior art ultrasonic density detection systems. 
     As discussed above, prior art ultrasonic density detection systems are largely incapable of providing the consistent and accurate density readings. This, in turn, means prior art ultrasonic density detection systems are often unable to determine wood product strength within the margins of error now required in many industries. In addition, prior art ultrasonic density detection systems have many parts and components that are subject to failure, add unnecessary weight to the systems, require significant maintenance, and are subject to failure. Consequently, prior art ultrasonic density detection systems are antiquated, largely ineffective, and are inefficient and expensive to operate. 
     Therefore, in addition to the need for a technical solution to the long-standing technical problem of accurately and efficiently detecting moisture levels and moisture pocket locations in an entire sheet or surface of a wood product, such as veneer sheets, there is also the need for a technical solution to the long-standing technical problem of providing a reliable, consistent, and economically feasible method and system for determining the strength of wood products including veneer sheets and other wood products that are to be used as components of layered wood products. 
     In addition, any method or system used to determine the strength of wood products must also be effective and efficient enough to detect strength related physical/mechanical parameters/characteristics while not significantly slowing down the production process or otherwise adding to the cost of the end wood product. 
     SUMMARY 
     Embodiments of the present disclosure provide an effective and efficient technical solution to the technical problem of accurately and efficiently detecting moisture levels and moisture locations in an entire sheet or surface of a wood product, such as veneer sheets. In addition, the disclosed technical solution is capable of detecting the moisture levels of an entire surface of a wood product in a single pass. Consequently, the disclosed embodiments can be implemented without significantly slowing down the production process or increasing the cost of the finished wood product. 
     In addition, embodiments of the present disclosure provide an effective and efficient technical solution to the technical problem of providing a method and system for determining the strength of a wood product that is reliable, consistent, and economically feasible to implement. 
     To this end, embodiments of the present disclosure utilize Near InfraRed (NIR) technology, including Near InfraRed/Short Wave InfraRed (NIR/SWIR) cameras and detectors, to accurately identify moisture content, the specific locations of the moisture in a veneer sheet or other wood product, and the strength of the wood product. In addition, embodiments of the present disclosure utilize Near InfraRed (NIR) technology, including Near InfraRed/Short Wave InfraRed (NIR/SWIR) cameras and detectors, to accurately determine the strength of both green and dry wood products. 
     In one embodiment, an NIR analysis station is provided for accurately identifying moisture content and the specific locations of the moisture in a veneer sheet or other wood product. In one embodiment, the NIR analysis station includes one or more sources of illumination positioned to illuminate at least one surface of a veneer sheet or other wood product. In one embodiment, the NIR analysis station includes one or more NIR/SWIR cameras, hereafter referred to as simply NIR cameras, positioned to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. 
     In one embodiment, a veneer sheet or other wood product to be analyzed is positioned in, or passed through, the NIR analysis station such that a surface of the veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. The one or more NIR cameras are then used to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. 
     In one embodiment, the one or more NIR images of the illuminated surface of the veneer sheet or other wood product are converted to NIR greyscale images with different greyscale values indicating different moisture levels in the illuminated surface of the veneer sheet or other wood product. 
     In one embodiment, the greyscale values shown in the NIR greyscale images are processed using the moisture level to greyscale mapping database to identify moisture levels over the entire surface of the veneer sheet or other wood product analyzed. 
     In one embodiment, the veneer sheet or other wood product is then graded based on the identified moisture levels and their positions/locations over the entire surface of the veneer sheet or other wood product. In one embodiment, based, at least in part, on the grade assigned to the veneer sheet or other wood product being analyzed, one or more actions are taken with respect to the veneer sheet or other wood product. 
     As discussed in more detail below, in some embodiments, one or more machine learning based moisture level detection models are trained using NIR image data for one or more wood products along with various other production parameters and corresponding empirically determined moisture levels for the one or more wood products. 
     In one embodiment, an NIR analysis station is provided for accurately identifying moisture content and the specific locations of the moisture in a veneer sheet or other wood product that includes one or more sources of illumination positioned to illuminate a surface of a wood product and one or more NIR cameras positioned to capture one or more NIR images of the illuminated surface of the wood product. 
     In one embodiment, a wood product to be analyzed is positioned, or passed through, the NIR analysis station such that a first surface of the wood product to be analyzed is illuminated by the one or more illumination sources. 
     In one embodiment, one or more NIR images of the illuminated first surface of the wood product are then captured using the one or more NIR cameras and the one or more NIR images of the illuminated first surface of the wood product are processed to generate NIR image data for the illuminated first surface of the wood product. 
     In one embodiment, the NIR image data for the illuminated first surface of the wood product is then provided to the one or more trained machine learning based moisture level detection models and moisture level prediction data for the wood product is obtained from the one or more trained machine learning based moisture level detection models. 
     In one embodiment, a grade is assigned to the wood product based on the moisture level prediction data for the wood product and, based, at least in part, on the grade assigned to the wood product, one or more actions are taken with respect to the wood product. 
     As discussed in more detail below, in some embodiments, a moisture level to greyscale mapping database is generated that maps moisture level to NIR image greyscale values for one or more wood products, such as, but not limited to, one or more types of veneer sheets. In one embodiment, the moisture level to greyscale mapping database includes mapping data obtained via controlled empirical methods. 
     In one embodiment, an NIR analysis station for accurately identifying moisture content and the specific locations of the moisture in a veneer sheet or other wood product is provided. In one embodiment, the NIR analysis station includes one or more sources of illumination positioned to illuminate at least one surface of a veneer sheet or other wood product. In one embodiment, the NIR analysis station includes one or more NIR/SWIR cameras, hereafter referred to as simply NIR cameras, positioned to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. 
     In one embodiment, a veneer sheet or other wood product to be analyzed is positioned in, or passed through, the NIR analysis station such that a surface of the veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. The one or more NIR cameras are then used to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. 
     In one embodiment, the one or more NIR images of the illuminated surface of the veneer sheet or other wood product are converted to NIR greyscale images with different greyscale values indicating different moisture levels in the illuminated surface of the veneer sheet or other wood product. 
     In one embodiment, the greyscale values shown in the NIR greyscale images are processed using the moisture level to greyscale mapping database to identify moisture levels over the entire surface of the veneer sheet or other wood product analyzed. 
     In one embodiment, one or more visual image cameras are provided and positioned to capture visual images of the first surface of the wood product. In one embodiment, the one or more visual image cameras are used to capture one or more visual images of the first surface of the wood product. 
     In one embodiment, the one or more NIR greyscale images and the one or more visual images of the first surface of the wood product are processed to generate NIR greyscale and visual superimposed images of the first surface of the wood product indicating different moisture levels and proximity of visual elements in the first surface of the wood product. 
     In one embodiment, a grade is assigned to the wood product based on the identified moisture levels, proximate visual elements in the first surface of the wood product, and the determined strength of the wood product based. Then, based at least in part on the grade assigned to the wood product, one or more actions are taken with respect to the wood product. 
     The disclosed embodiments utilize NIR cameras to scan the surface of a wood product for moisture and strength and create an NIR image of the surface of the wood product. Since essentially each pixel of camera image data is a sample point, the resolution and accuracy of the moisture detection process is only limited by the number of pixels the camera has covering the field of view, e.g., the entire first surface of a wood product. Consequently, in the case where a 1.3 mega pixel camera is used there are essentially 1,300,000 individual measurement points on the surface of the wood product. Consequently, the use of NIR cameras as disclosed herein results in resolutions and accuracy that simply cannot be achieved using traditional moisture detection systems such as traditional contact electrode systems or RF moisture detection systems. 
     As noted, using traditional moisture detection systems such as traditional contact electrode systems or RF moisture detection systems accuracy levels are subject to, at best, ±5.0% or ±7.5% margin of error. This resulted in the need to be very conservative when determining the potential use of a given veneer sheet or other wood product and often resulted in wood products, such as veneer sheets, not being put to their most cost effective and efficient use simply to ensure that the ±5.0% or ±7.5% margin of error did not result in inferior or unsafe wood products. 
     In contrast, using the disclosed NIR camera-based systems, accuracy on the order of ±0.1% is readily achieved. Therefore, the highest value use of a given veneer sheet or other wood product can be accurately, and confidently determined so that the wood products, such as veneer sheets, can be put to their most cost effective and efficient use. 
     In addition, when, as disclosed herein, NIR cameras are used as the moisture detection mechanism, if greater or less resolution is deemed necessary, a higher or lower mega-pixel camera can be selected to achieve the desired resolution for the process. This can be accomplished in a relatively simple and quick camera switch out procedure. In addition, unlike tradition contact electrode and RF moisture detection systems, NIR camera placement with respect to the sample under analysis can be adjusted such that a quality image can be obtained as long as there is a clear field of view between the wood product surface and NIR camera. Horizontal, vertical, or angled placements have no impact on the functionality of the NIR camera. Further, combinations of NIR cameras and lenses can provide opportunities to perform measurements that are currently prohibitive due to the need for a conveyor section to convey the material through a sensing array of contact electrodes or RF instruments. 
     The use of NIR cameras, are disclosed herein, eliminates the need for any physical contact with the wood product by any part of the moisture detection device, or even the need for the moisture detection device, i.e., the NIR camera, to be close to the surface of a wood product. Not only does this fact eliminate wear and tear on both the sample taking device and the wood product, but, as discussed above, it allows for more flexible placement of the sample taking device, i.e., the NIR camera. 
     In addition, unlike RF moisture detection devices and contact electrodes, NIR cameras are virtually immune to static electricity or spurious RF emissions. Consequently, use of NIR cameras as disclosed herein is far more suitable for a physical production line environment. 
     Finally, unlike traditional contact electrode systems that require high voltages and represent a danger to workers, NIR technology has been determined to be safe, i.e., representing no hazards to workers or other devices, by several testing and safety agencies. Consequently, the use of the disclosed NIR based moisture detection systems results in a safer and more comfortable and efficient workplace and production floor. 
     In one embodiment, one or more NIR green strength analysis systems, including one or more NIR green wood product strength analysis stations, are provided. In one embodiment, before moisture analysis is performed, the green veneer sheet, ribbon, or other wood product to be analyzed is positioned in, or passed through, the NIR green wood product strength analysis station such that a surface of the green veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. In one embodiment, the green veneer ribbon or sheet to be analyzed is passed from one a log peeling/veneer creation mechanism to the NIR green wood product strength analysis station. 
     In one embodiment, the NIR strength analysis stations include one or more NIR/SWIR cameras, hereafter referred to as simply NIR cameras, positioned to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. In one embodiment, the one or more NIR cameras of the NIR green wood product strength analysis stations are then used to capture one or more NIR images of the illuminated surface of the green veneer sheet or other wood product. 
     In some embodiments, strength analysis models are created, and the data obtained from NIR images can be correlated with the strength properties of the green wood product using these models. 
     It has been found that these correlations apply to moving ribbons and/or sheets of veneer using a reduced spectral range. Consequently, in one embodiment, the one or more sources of illumination positioned to illuminate at least one surface of a veneer sheet or other wood product are selected to provide a reduced spectral range, in one embodiment between 650 and 1050 nm. This enables very rapid collection of the NIR spectra. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, a veneer sheet or other wood product to be analyzed is positioned in, or passed through, the NIR green wood product strength analysis station such that a surface of the green veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. The one or more NIR cameras are then used to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product including NIR reflectance spectrum data. 
     In one embodiment, a reduced spectral range between 650 and 1050 nm is utilized to enable very rapid collection of the NIR data including NIR reflectance spectrum data. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, the NIR reflectance spectrum data is provided to a processor for comparing and analyzing the NIR reflectance spectrum data using the one or more strength models, and/or data, and/or machine learning modules. 
     In one embodiment, secondary NIR green strength data processing is used for analysis of green wood products to compensate for the strong absorbance bands of water/moisture in the NIR region. 
     As discussed in more detail below, in various embodiments, different methods can be used to correlate the NIR image data, i.e., NIR reflectance spectrum data, of a green wood product to a selected property of that green wood product to create the strength models and/or machine learning modules. 
     Consequently, using the disclosed NIR green strength analysis it is possible to collect high quality NIR spectra of wood products, including full size ribbons and/or sheets of green veneer that contain information and data regarding the mechanical properties of wood product, including strength of the wood product. 
     In one embodiment, a grade is assigned to the green wood product based on the determined strength of the green wood product. Then, based at least in part on the grade assigned to the green wood product, one or more actions are taken with respect to the green wood product. 
     Consequently, some disclosed embodiments use NIR technology to predict the strength of a green sheet of veneer from the NIR spectra of green veneer. This allows for the gradings and sorting of green veneer before drying and moisture analysis to provide enhanced grading technology and more accurate grading. 
     In one embodiment, one or more NIR dry strength analysis systems, including one or more NIR dry wood product strength analysis stations, are provided. In one embodiment, a dry veneer sheet or other wood product to be analyzed is positioned in, or passed through, the NIR dry wood product strength analysis station such that a surface of the dry veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. 
     In one embodiment, the dry veneer sheet or other wood product to be analyzed is passed from one of the NIR analysis stations discussed above used for moisture analysis after the moisture analysis is performed. In some embodiments, the NIR analysis stations discussed above used for moisture analysis and the NIR dry strength analysis system are located at the same NIR analysis position along a processing line. 
     In one embodiment, the disclosed NIR dry strength analysis system includes an NIR dry wood product strength analysis station. In one embodiment, the NIR dry wood product strength analysis station includes one or more sources of illumination positioned to illuminate at least one surface of a veneer sheet or other wood product. In one embodiment, the sources of illumination are selected to provide a reduced spectral range, in one embodiment between 650 and 1050 nm. This enables very rapid collection of the NIR spectra data. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, the NIR dry wood product strength analysis stations include one or more NIR/SWIR cameras, hereafter referred to as simply NIR cameras, positioned to capture one or more NIR images of the illuminated surface of the dry veneer sheet or other wood product. In one embodiment, the one or more NIR cameras of the NIR dry wood product strength analysis stations are then used to capture one or more NIR images of the illuminated surface of the dry veneer sheet or other wood product. 
     In some embodiments, strength analysis models are created, and the data obtained from NIR images can be correlated with the strength properties of the wood product using these models. It has been found that these correlations apply to moving 4 ft. by 8 ft. sheets of veneer using a reduced spectral range. 
     In one embodiment, a dry veneer sheet or other wood product to be analyzed is positioned in, or passed through, the NIR dry wood product strength analysis station such that a surface of the veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. The one or more NIR cameras are then used to capture one or more NIR images of the illuminated surface of the dry veneer sheet or other wood product including NIR reflectance spectrum data. 
     As noted, in one embodiment, a reduced spectral range, in one embodiment between 650 and 1050 nm, is analyzed to enable very rapid collection of the NIR reflectance spectrum data. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In some embodiments, strength analysis models are created, and the data obtained from NIR images can be correlated with the strength properties of the wood product using these models. It has been found that these correlations apply to moving 4 ft. by 8 ft. sheets of veneer using a reduced spectral range. 
     In one embodiment, this NIR reflectance spectrum data is provided to a processor for comparing and analyzing the NIR reflectance spectrum data using one or more strength models and/or machine learning modules. 
     As discussed in more detail below, in various embodiments, different methods can be used to correlate the NIR strength data, i.e., NIR spectra, of a wood product to a selected property of that wood product to create the strength models and/or machine learning modules. 
     Consequently, using the disclosed NIR strength analysis it is possible to collect high quality NIR spectra of wood products, including full size sheets of green and dry veneer that contain information and data regarding the mechanical properties of wood product, including strength of the wood product. 
     In one embodiment, a grade is assigned to the dry wood product based on the determined strength of the dry wood product. Then, based at least in part on the grade assigned to the dry wood product, one or more actions are taken with respect to the wood product. 
     Consequently, some disclosed embodiments use NIR technology to predict the strength of a sheet of veneer from the NIR spectra of green and/or dry veneer. This allows for the gradings and sorting of green veneer before drying and moisture analysis and/or dry veneer after moisture analysis to provide enhanced grading technology and more accurate wood product grading. 
     The disclosed embodiments utilize NIR cameras to scan the surface of a wood product for moisture and strength and create an NIR image of the surface of the wood product. Since essentially each pixel of camera image data is a sample point, the resolution and accuracy of the moisture detection process is only limited by the number of pixels the camera has covering the field of view, e.g., the entire first surface of a wood product. Consequently, in the case where a 1.3 mega pixel camera is used there are essentially 1,300,000 individual measurement points on the surface of the wood product. Consequently, the use of NIR cameras as disclosed herein results in resolutions and accuracy that simply cannot be achieved using traditional moisture detection or strength systems such as traditional contact electrode systems or RF moisture detection systems. 
     As noted, using traditional moisture detection systems such as traditional contact electrode systems or RF moisture detection systems accuracy levels are subject to, at best, ±5.0% or ±7.5% margin of error. This resulted in the need to be very conservative when determining the potential use of a given veneer sheet or other wood product and often resulted in wood products, such as veneer sheets, not being put to their most cost effective and efficient use simply to ensure that the ±5.0% or ±7.5% margin of error did not result in inferior or unsafe wood products. 
     In contrast, using the disclosed NIR camera-based systems, accuracy on the order of ±0.1% is readily achieved. Therefore, the highest value use of a given veneer sheet or other wood product can be accurately, and confidently determined so that the wood products, such as veneer sheets, can be put to their most cost effective and efficient use. 
     In addition, when, as disclosed herein, NIR cameras are used as the moisture detection mechanism, if greater or less resolution is deemed necessary, a higher or lower mega-pixel camera can be selected to achieve the desired resolution for the process. This can be accomplished in a relatively simple and quick camera switch out procedure. In addition, unlike tradition contact electrode and RF moisture detection systems, NIR camera placement with respect to the sample under analysis can be adjusted such that a quality image can be obtained as long as there is a clear field of view between the wood product surface and NIR camera. Horizontal, vertical, or angled placements have no impact on the functionality of the NIR camera. Further, combinations of NIR cameras and lenses can provide opportunities to perform measurements that are currently prohibitive due to the need for a conveyor section to convey the material through a sensing array of contact electrodes or RF instruments. 
     The use of NIR cameras, are disclosed herein, eliminates the need for any physical contact with the wood product by any part of the moisture detection device, or even the need for the moisture detection device, i.e., the NIR camera, to be close to the surface of a wood product. Not only does this fact eliminate wear and tear on both the sample taking device and the wood product, but, as discussed above, it allows for more flexible placement of the sample taking device, i.e., the NIR camera. 
     In addition, unlike RF moisture detection devices and contact electrodes, NIR cameras are virtually immune to static electricity or spurious RF emissions. Consequently, use of NIR cameras as disclosed herein is far more suitable for a physical production line environment. 
     In addition, unlike traditional contact electrode systems that require high voltages and represent a danger to workers, NIR technology has been determined to be safe, i.e., representing no hazards to workers or other devices, by several testing and safety agencies. Consequently, the use of the disclosed NIR based moisture detection systems results in a safer and more comfortable and efficient workplace and production floor. 
     In addition, using the disclosed NIR strength analysis systems, the antiquated and extremely inefficient and ineffective currently used prior art methods and systems for determining the density, and therefore the strength, of wood products, including veneer sheets, and various other materials is not requited. 
     For example, using the disclosed NIR strength analysis systems the use of prior art contact electrode systems and ultrasonic density detection systems similar to the RF detection systems used for moisture detection discussed above is no longer needed. Therefore, the shortcomings inefficiencies, and inaccuracies of prior art ultrasonic density detection systems discussed above are avoided. 
     Consequently, in contrast to prior art ultrasonic density detection systems, the disclosed NIR strength analysis systems are quite capable of determining wood product strength within the margins of error now required in many industries. In addition, in contrast to prior art ultrasonic density detection systems, the disclosed NIR strength analysis systems have relatively few moving parts and components so they are less subject to failure, lighter, require significantly less maintenance, than the antiquated, largely ineffective, and inefficient prior art ultrasonic density detection systems. 
     As a result of these and other disclosed features, which are discussed in more detail below, the disclosed embodiments address the short comings of the prior art. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawing(s) will be provided by the Office upon request and payment of the necessary fee. 
         FIG. 1A  is an illustration of one example of a prior art traditional contact electrode system. 
         FIG. 1B  is an illustration of one example of a contact electrodes of a prior art traditional contact electrode structure. 
         FIG. 1C  is a graphical representation of the placement and spacing of individual contact electrodes using a typical traditional contact electrode system. 
         FIG. 1D  shows a typical sample sheet generated using traditional contact electrode systems and the physical arrangement of  FIG. 1C . 
         FIG. 2A  is an illustration of one example of a prior art traditional RF moisture detection system. 
         FIG. 2B  shows a side view of an RF transmitter positioned above surface of a veneer sheet and an RF receiver positioned a distance below a surface of the veneer sheet. 
         FIG. 2C  shows a graphic illustration of a typical arrangement of RF transmitters over a surface of a veneer sheet moving via conveyor belts, thereby creating sample channels. 
         FIG. 2D  shows a sample sheet created using the RF transmitter arrangement shown in  FIG. 2C . 
         FIG. 3A  is simplified block diagram of a system for detecting moisture levels in a wood product using NIR technology in accordance with one embodiment. 
         FIG. 3B  shows one example of a physical system for detecting moisture levels in a wood product using NIR technology in accordance with one embodiment. 
         FIG. 4A  shows a first surface of a dry veneer sheet as seen in a visual image of the dry veneer sheet and as seen in an NIR greyscale image of the dry veneer sheet. 
         FIG. 4B  shows a first surface of a veneer sheet, including a small moisture pocket, as seen in a visual image of the veneer sheet and as seen in an NIR greyscale image of the veneer sheet. 
         FIG. 4C  shows a first surface of a veneer sheet, including a larger moisture pocket, as seen in a visual image of the veneer sheet and as seen in an NIR greyscale image of the veneer sheet. 
         FIG. 5  is flow chart of a process for detecting moisture levels in a wood product using NIR technology in accordance with one embodiment. 
         FIG. 6  is simplified block diagram of a system for detecting moisture levels in a wood product using NIR technology and visual data in accordance with one embodiment. 
         FIG. 7A  shows a black and white visual image of a wood product first surface of a veneer sheet including physical features which, in this specific illustrative example, are knots and knot holes. 
         FIG. 7B  shows a color visual image of the wood product first surface of the veneer sheet of  FIG. 7A  including physical features which, in this specific illustrative example, are knots and knot holes of  FIG. 7A . 
         FIG. 7C  shows a superimposed composite image of the wood product first surface the of the wood product including the visual images of the physical features of  FIG. 7A or 7B  with an NIR greyscale image including NIR greyscale images of high moisture superimposed. 
         FIG. 7D  shows a color enhanced superimposed composite image of the wood product first surface the of the wood product of  FIG. 7C . 
         FIG. 8  is flow chart of a process for detecting moisture levels in a wood product using NIR technology and visual data in accordance with one embodiment. 
         FIG. 9  is simplified block diagram of a system for detecting moisture levels in a wood product using NIR technology and machine learning methods in accordance with one embodiment. 
         FIG. 10  is a simplified block diagram of a process for determining the strength of a green wood product using NIR technology in accordance with one embodiment. 
         FIG. 11  is a simplified block diagram of a NIR green wood product strength analysis system using NIR technology in accordance with one embodiment. 
         FIG. 12  is a flow chart of a process for determining the strength of a green wood product using NIR technology in accordance with one embodiment. 
         FIG. 13  is a simplified block diagram of a process for determining the strength of a dry wood product using NIR technology in accordance with one embodiment. 
         FIG. 14  is a simplified block diagram of a NIR dry wood product strength analysis system in accordance with one embodiment. 
         FIG. 15  is a flow chart of a process for determining the strength of a dry wood product using NIR technology in accordance with one embodiment. 
     
    
    
     Common reference numerals are used throughout the figures and the detailed description to indicate like elements. One skilled in the art will readily recognize that the above figures are merely illustrative examples and that other architectures, modes of operation, orders of operation, and elements/functions can be provided and implemented without departing from the characteristics and features of the invention, as set forth in the claims. 
     DETAILED DESCRIPTION 
     Embodiments will now be discussed with reference to the accompanying figures, which depict one or more exemplary embodiments. Embodiments may be implemented in many different forms and should not be construed as limited to the embodiments set forth herein, shown in the figures, or described below. Rather, these exemplary embodiments are provided to allow a complete disclosure that conveys the principles of the invention, as set forth in the claims, to those of skill in the art. 
     Embodiments of the present disclosure utilize Near InfraRed (NIR) technology, including Near InfraRed/Short Wave InfraRed (NIR/SWIR) cameras and detectors, to accurately identify moisture content, the specific locations of the moisture in a veneer sheet or other wood product, and the strength of the wood product. In addition, embodiments of the present disclosure utilize Near InfraRed (NIR) technology, including Near InfraRed/Short Wave InfraRed (NIR/SWIR) cameras and detectors, 
     As discussed in more detail below, using some disclosed embodiments accurate identification of moisture is accomplished by providing a NIR analysis station for the identification of moisture including one or more illumination sources and one or more NIR cameras. 
     A wood product, such as a veneer sheet is then positioned in, and/or is passed through, the NIR analysis station. At the NIR analysis station an entire first surface of the veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources and the one or more NIR cameras are used to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. 
     The one or more NIR images of entire first surface of the veneer sheet or other wood product are then analyzed and moisture levels over the entire first surface of the veneer sheet or other wood product are identified. In one example, this is accomplished with the aid of a moisture level to greyscale mapping database containing empirical data. In another embodiment, this is accomplished using the greyscale mapping database containing empirical data and a greyscale to color mapping database. In another embodiment, this is accomplished using one or more machine learning based models. 
     Once the moisture levels over the entire first surface of the veneer sheet or other wood product are identified, a grade is assigned to the wood product based on the identified moisture levels for the wood product and based, at least in part, on the grade assigned to the wood product, one or more actions are taken with respect to the wood product. 
     The one or more actions can include one or more of: sorting the wood product into a bin/location associated with the grade assigned to the wood product; restricting the use of the wood product based on grade assigned to the wood product; rejecting the wood product based on the grade assigned to the wood product; sending the wood product back for further processing based on the grade assigned to the wood product; adjusting one or more processing parameters of a production line based on grades assigned to one or more wood products; adjusting drying temperatures on a production line based on grades assigned to one or more wood products; and adjusting drying times on a production line based on grades assigned to one or more wood products. 
     As also discussed in more detail below, using some disclosed embodiments, strength determination is accomplished by providing, one or more NIR green strength analysis systems, including one or more NIR green wood product strength analysis stations. In one embodiment, before moisture analysis is performed, the green veneer sheet, ribbon, or other wood product to be analyzed is positioned in, or passed through, the NIR green wood product strength analysis station such that a surface of the green veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. In one embodiment, the green veneer ribbon or sheet to be analyzed is passed from a log peeling/veneer creation mechanism to the NIR green wood product strength analysis station. 
     In one embodiment, the NIR green wood product strength analysis stations include one or more NIR/SWIR cameras, hereafter referred to as simply NIR cameras, positioned to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. In one embodiment, the one or more NIR cameras of the NIR green wood product strength analysis stations are then used to capture one or more NIR images of the illuminated surface of the green veneer sheet or other wood product. 
     In some embodiments, strength analysis models are created, and the data obtained from NIR images can be correlated with the strength properties of the green wood product using these models. 
     It has been found that these correlations apply to moving ribbons and/or sheets of veneer using a reduced spectral range. Consequently, in one embodiment, the one or more sources of illumination positioned to illuminate at least one surface of a veneer sheet or other wood product are selected to provide a reduced spectral range, in one embodiment between 650 and 1050 nm. This enables very rapid collection of the NIR spectra. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, a veneer sheet or other wood product to be analyzed is positioned in, or passed through, NIR green wood product strength analysis station such that a surface of the veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. The one or more NIR cameras are then used to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product including NIR reflectance spectrum data. 
     In one embodiment, a reduced spectral range between 650 and 1050 nm is utilized to enable very rapid collection of the NIR data including NIR reflectance spectrum data. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, the NIR reflectance spectrum data is provided to a processor for comparing and analyzing the NIR reflectance spectrum data using the one or more strength models and/or machine learning modules. 
     In one embodiment, secondary NIR green strength data processing is used for analysis of green wood products to compensate for the strong absorbance bands of water/moisture in the NIR region. 
     As discussed in more detail below, in various embodiments, different methods can be used to correlate the NIR data, i.e., NIR reflectance spectrum data, of a green wood product to a selected property of that green wood product to create the strength models and/or machine learning modules. 
     Consequently, using the disclosed NIR green strength analysis it is possible to collect high quality NIR spectra of wood products, including full size ribbons and/or sheets of green veneer, that contain information and data regarding the mechanical properties of wood product, including the strength of the wood product. 
     In one embodiment, a grade is assigned to the green wood product based on the determined strength of the green wood product based. Then, based at least in part on the grade assigned to the green wood product, one or more actions are taken with respect to the wood product. 
     Consequently, some disclosed embodiments use NIR technology to predict the strength of a sheet of veneer from the NIR spectra of green veneer. This allows for the gradings and sorting of green veneer before drying and moisture analysis to provide enhanced grading technology and more accurate wood product grading. 
     As also discussed in more detail below, using some disclosed embodiments strength determination is accomplished by providing one or more NIR dry strength analysis systems, including one or more NIR dry wood product strength analysis stations. In one embodiment, a dry veneer sheet or other wood product to be analyzed is positioned in, or passed through, the NIR dry wood product strength analysis station such that a surface of the dry veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. 
     In one embodiment, the dry veneer sheet or other wood product to be analyzed is passed from one of the NIR analysis stations discussed above used for moisture analysis after the moisture analysis is performed. In some embodiments, the NIR analysis stations discussed above used for moisture analysis and the NIR dry wood product strength analysis station are located at the same NIR analysis station. 
     In one embodiment, the disclosed NIR dry wood product strength analysis system includes one or more NIR dry wood product strength analysis stations. In one embodiment, the NIR dry wood product strength analysis stations include one or more sources of illumination positioned to illuminate at least one surface of a dry veneer sheet or other wood product. In one embodiment, the sources of illumination are selected to provide a reduced spectral range between 650 and 1050 nm. This enables very rapid collection of the NIR spectra. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, the NIR dry wood product strength analysis stations include one or more NIR/SWIR cameras, hereafter referred to as simply NIR cameras, positioned to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. In one embodiment, the one or more NIR cameras of the NIR dry wood product strength analysis stations are then used to capture one or more NIR images of the illuminated surface of the dry veneer sheet or other wood product. 
     In some embodiments, strength analysis models are created, and the data obtained from NIR images can be correlated with the strength properties of the wood product using these models. It has been found that these correlations apply to moving 4 ft. by 8 ft. sheets of veneer using a reduced spectral range. 
     In one embodiment, a veneer sheet or other wood product to be analyzed is positioned in, or passed through, the NIR dry wood product strength analysis station such that a surface of the veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. The one or more NIR cameras are then used to capture one or more NIR images of the illuminated surface of the dry veneer sheet or other wood product including NIR reflectance spectrum data. 
     As noted, in one embodiment, a reduced spectral range between 650 and 1050 nm is analyzed to enable very rapid collection of the NIR reflectance spectrum data. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In some embodiments, strength analysis models are created, and the data obtained from NIR images can be correlated with the strength properties of the wood product using these models. It has been found that these correlations apply to moving 4 ft. by 8 ft. sheets of veneer using a reduced spectral range. 
     In one embodiment, this NIR reflectance spectrum data is provided to a processor for comparing and analyzing the NIR reflectance spectrum data using one or more strength models and/or machine learning modules. 
     As discussed in more detail below, in various embodiments, different methods can be used to correlate the NIR strength data, i.e., NIR spectra, of a wood product to a selected property of that wood product to create the strength models and/or machine learning modules. 
     Consequently, using the disclosed NIR strength analysis it is possible to collect high quality NIR spectra of wood products, including full size sheets of green and dry veneer that contain information and data regarding the mechanical properties of wood product, including strength of the wood product. 
     In one embodiment, a grade is assigned to the dry wood product based on the determined strength of the dry wood product. Then, based at least in part on the grade assigned to the dry wood product, one or more actions are taken with respect to the wood product. 
     Consequently, some disclosed embodiments use NIR technology to predict the strength of a sheet of veneer from the NIR spectra of green and/or dry veneer. This allows for the gradings and sorting of green veneer before drying and moisture analysis and/or dry veneer after moisture analysis to provide enhanced grading technology and more accurate wood product grading. 
     Consequently, disclosed herein is an effective and efficient technical solution to the technical problem of accurately and efficiently detecting moisture level and moisture pockets in an entire sheet or surface of a wood product, such as veneer sheets or other wood products. In addition, since, in one embodiment, the disclosed embodiments use NIR cameras to take NIR images of an entire wood product surface the technical solution is capable of accurately analyzing an entire surface of a wood product, such as a veneer sheet, in a single pass. Consequently, the embodiments can be implemented without significantly slowing down the production process or increasing the cost of the finished wood product. 
     In addition, embodiments of the present disclosure provide an effective and efficient technical solution to the technical problem of providing a method and system for determining the strength of a wood product that is reliable, consistent, and economically feasible to implement. 
       FIG. 3A  is simplified block diagram of one embodiment of a system  300  for detecting moisture levels in a wood product using NIR technology in accordance with one embodiment. 
     In one embodiment, system  300  for detecting moisture levels in wood products includes a production environment  301  and a computing environment  350 . 
     As seen in  FIG. 3A , production environment  301  includes NIR analysis station  320  and selected action implementation module  396 . As seen in  FIG. 3A , NIR analysis station  320  includes one or more illumination sources, such as illumination source  322 , positioned to illuminate a surface of a wood product. In various embodiments, the one or more illumination sources, such as illumination source  322 , can include one or more LED light sources. In other embodiments, the one or more illumination sources, such as illumination source  322 , can include, but are not limited to, halogen, halogen and tungsten light sources, or any other light sources, as discussed herein, and/or as known in the art at the time of filing, and/or as developed after the time of filing. 
     As seen in  FIG. 3A , NIR analysis station  320  also includes one or more NIR cameras, such as NIR camera  324 , positioned to capture NIR image data  362  representing one or more NIR images of the illuminated surface of the wood product. In one embodiment, the one or more NIR cameras, such as NIR camera  324 , are adjustably positioned and adjustably focused to capture any desired one or more NIR images of the illuminated surface of the wood product. 
     As used herein, the terms Near InfraRed (NIR) and Short-Wave InfraRed (SWIR) are used interchangeably to include wavelength in the range of 750 nanometers (nm) to 3500 nm. In addition, all stated wave lengths herein are assumed to include values within 10% of the stated value. 
     As seen in  FIG. 3A , and as discussed below, a wood product  330  to be analyzed in the NIR analysis station  320  is positioned in NIR analysis station  320 . In various embodiments, the wood product  330  can be any wood product as discussed herein, and/or as known in the art at the time of filing and/or as becomes known after the time of filing. In one embodiment, the wood product  330  to be analyzed is a veneer sheet. 
     In one embodiment, the wood product  330  to be analyzed is positioned such that a wood product first surface  332  of the wood product  330  to be analyzed is illuminated by the illumination source  322  and the entire wood product first surface  332  is within view and focus of NIR camera  324 . In one embodiment, the wood product  330  is positioned in the NIR analysis station  320  by passing the wood product  330  through the NIR analysis station  320  on a conveyor system (not shown in  FIG. 3A  but shown as  321  in  FIG. 3B  and discussed below). 
     In various embodiments, the one or more NIR cameras, such as NIR camera  324 , can be of any resolution desired. As noted above, when the one or more NIR cameras, such as NIR camera  324 , are used to scan the wood product first surface  332  of a wood product  330  for moisture and create an NIR image data  362  of the wood product first surface  332 , essentially each pixel generated by NIR camera  324  is a sample point. Consequently, the resolution and accuracy of the moisture detection process is only limited by the number of pixels the NIR camera  324  has covering the field of view, e.g., the entire wood product first surface  332  of wood product  330 . Consequently, in the case where NIR camera  324  is a 1.3 mega pixel camera, there are essentially 1,300,000 individual measurement points on the wood product first surface  332 . Consequently, using NIR cameras, such as NIR camera  324 , results in resolutions and accuracy that simply cannot be achieved using traditional moisture detection systems such as traditional contact electrode systems or RF moisture detection systems. 
     As seen in  FIG. 3A , computing environment  350  includes computing system  352 . As seen in  FIG. 3A , in one embodiment, computing system  352  includes moisture to greyscale mapping database  310  containing mapping data  312  that maps moisture level to Near InfraRed (NIR) image greyscale values for one or more wood products. 
     Using NIR images, extremely granular differences in moisture levels can be detected. In general, locations with different levels of moisture absorb/reflect different amounts of NIR radiation at specific frequencies. For moisture detection the NIR frequencies of 1450 nm, 1900 nm and 2400 nm are found to yield the best results. 
     In operation, when NIR radiation of a given frequency is applied to a wood product first surface  332  of wood product  330 , more NIR energy is absorbed at locations having moisture than those that are dry, with greater amounts of NIR energy being absorbed at locations having greater moisture. When the NIR camera  324  takes an image of the wood product first surface  332 , the NIR camera  324  picks up the NIR energy reflected off wood product first surface  332 . Consequently, when the NIR camera  324  takes an image of the wood product first surface  332 , the areas of moisture, which absorb more NIR energy and therefore reflect less NIR energy, appear darker than dry areas. In addition, the more moisture that is present the darker the area appears because less NIR energy is reflected to be captured by the NIR camera  324 . 
     Using this fact, NIR image data  362  captured by the NIR camera  324  can be processed into NIR greyscale image data  364 . Greyscale images can be of varying resolution, or bit, types. A 16-bit integer grayscale image provides 65535 available tonal steps from 0 (black) to 65535 (white). A 32-bit integer grayscale image theoretically will provide 4,294,967,295 tonal steps from 0 (black) to 4294967295 (white). Converting an NIR image based on these number of greyscale tonal steps results in a margin of error of significantly less than 0.1%. This is in sharp contrast to the ±7.5% margin of error obtained using traditional moisture detection systems such as traditional contact electrode systems or RF moisture detection systems. 
     Using these facts, in one embodiment, the mapping data  312  is obtained through one or more empirical and/or manual processes. For instance, in one embodiment, sample wood products are first dried in a kiln or similar environment while the weight of the sample wood product is monitored. As the sample wood product dries, i.e., loses moisture, the weight of the sample wood product deceases. Once the weight of the wood product stabilizes for a defined period, such as 24 hours, the sample wood product is determined to contain minimal moisture. 
     Then the sample wood product is brought up in moisture content in defined increments, such as one percent of the dry sample wood product weight. At each increment, an NIR image of the sample wood product is taken and the greyscale value at that increment of moisture is determined. The greyscale value determined is then correlated to the specific moisture level at that increment. 
     This process is continued for multiple increments until a maximum moisture content is obtained and greyscale data for each increment is determined and correlated to the respective moisture content increment. In this way, mapping data  312  mapping each specific moisture content to specific greyscale values is generated for the sample wood product. The process can then be repeated for different wood products, different types of wood, and under varying parameters and conditions. 
     As seen in  FIG. 3A , computing system  352  also includes physical memory  360 . In one embodiment, the physical memory  360  includes NIR image data  362  representing one or more NIR images of the illuminated wood product first surface  332  of the wood product  330  captured using NIR camera  324 . 
     As seen in  FIG. 3A , in one embodiment, computing system  352  includes one or more processors  370  for processing the NIR image data representing one or more NIR images of the illuminated wood product first surface  332  of the wood product  330  to generate NIR greyscale image data  364  indicating different moisture levels in the illuminated wood product first surface  332  of the wood product  330 . 
     In one embodiment, processor  370  processes the NIR greyscale image data  364  using the mapping data  312  from moisture to greyscale mapping database  310  to identify moisture levels for the wood product first surface  332  of the wood product  330 . 
     As seen in  FIG. 3A , in one embodiment, computing system  352  includes a grade assignment module  380  for assigning a grade to the wood product  330  based on the identified moisture levels for the wood product first surface  332 . As seen in  FIG. 3A , grade assignment module  380  includes moisture analysis module  374  which, along with processor  370 , processes the NIR greyscale image data  364  using the mapping data  312  from moisture to greyscale mapping database  310  data to identify moisture levels for the wood product first surface  332  of the wood product  330 . As a result of the processing by moisture analysis module  374  and processor  370 , grade assignment data  382  is generated. 
     As seen in  FIG. 3A , in one embodiment, grade assignment data  382  is provided to action selection and activation module  390  which selects an appropriate action of the actions represented in available actions data  392  based, at least in part on the grade indicated by grade assignment data  382 . As seen in  FIG. 3A , in one embodiment, the determined appropriate action is represented by selected action data  394 . 
     As seen in  FIG. 3A , in one embodiment, selected action data  394  is forwarded to an action activation module such as selected action implementation module  396  in production environment  301  to initialize one or more actions with respect to the wood product  330  based, at least in part, on the grade represented by grade assignment data  382  and assigned to the wood product  330  by action selection and activation module  390 . 
     In one embodiment, one or more actions that can be taken represented in available actions data  392  include, but are not limited to: sorting the wood product  330  into a bin or location associated with the grade represented by grade assignment data  382  and assigned to the wood product  330 ; restricting the use of the wood product  330  based on the grade represented by grade assignment data  382  and assigned to the wood product  330 ; rejecting the wood product  330  based on the grade represented by grade assignment data  382  and assigned to the wood product  330 ; sending the wood product  330  back for further processing based on the grade represented by grade assignment data  382  and assigned to the wood product  330 ; adjusting one or more processing parameters of a production line in production environment  301  based, at least in part, on the grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products; adjusting drying temperatures on a production line in production environment  301  based, at least in part, on grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products; adjusting drying times on a production line in production environment  301  based, at least in part, on grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products; and selecting a type and amounts of glues used on a production line in production environment  301  based, at least in part, on grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products. 
     As a specific illustrative example a signal representing a grade assigned to the wood product  330  and/or the grades assigned other wood products can be provided to a wood product gluing station (not shown) in a production line so that a glue appropriate to adhere wood products having the assigned grade can be selected and made available to glue the wood product when it reaches the gluing station. 
       FIG. 3B  shows one example of one embodiment of a physical system layout for detecting moisture levels in a wood product using NIR technology in accordance with one embodiment. 
     Referring to  FIGS. 3A and 3B  together, shown in  FIG. 3B  is a specific illustrative example of one embodiment of a physical production environment  301 . As seen in  FIG. 3B , in this in this specific illustrative example, production environment  301  includes NIR analysis station  320  and computing system  352 . 
     As seen in  FIG. 3B , NIR analysis station  320  includes illumination sources  322 , in this specific illustrative embodiment two LED light sources, and NIR camera  324 . 
     As seen in  FIG. 3B , wood product  330 , in this specific illustrative example a veneer sheet, is passed through NIR analysis station  320  via conveyor system  321  such that wood product first surface  332  is illuminated by illumination source  322 . Then NIR camera  324  captures NIR image data  362  and forwards this data to computing system  352  for processing as discussed above. 
     Those of skill in the art will ready recognize that the specific illustrative examples of one embodiment of a production environment  301  and components shown in  FIGS. 3A and 3B  are but specific examples of numerous possible production environments and arrangement of physical components. Consequently, the specific illustrative example of embodiments of a production environment  301  and components shown in  FIGS. 3A and 3B  is not intended to limit the scope of the invention as set forth in the claims below. 
       FIGS. 4A, 4B, and 4C  are specific illustrative examples of the operation of part of the system  300  for moisture detection of  FIG. 3A .  FIG. 4A  shows a first surface  332  of a veneer sheet  330 A as seen in a visual image  410  of the veneer sheet  330 A and as seen in an NIR greyscale image  420  of the veneer sheet  330 A. In the example of  FIG. 4A , veneer sheet  330 A has an average moisture level that is less than 5% and is therefore considered a dry veneer sheet. 
     It is worth noting that visual image  410  and NIR greyscale image  420  can be images of the entire wood product first surface  332  of veneer sheet  330 A, i.e., can be a 4′×8′ sample. In addition, as noted above, using a standard 1.3 mega pixel camera to obtain NIR greyscale image  420  of the entire wood product first surface  332  of veneer sheet  330 A there are as many as 1,300,000 data points, i.e., each pixel is a data point. This, in turn, gives rise to very high resolution and is in sharp contrast to the 128 9″×3″ samples of traditional contact electrode systems or 32 12″×12″ samples of traditional RF systems that, as discussed above, yielded ±5.0% or ±7.5% margins of error, respectively. 
     As seen in  FIG. 4A , the visual image  410  of the wood product first surface  332  of veneer sheet  330 A is relatively uniform in appearance and coloration, i.e., no moisture can be readily detected visually in visual image  410  of the wood product first surface  332  of veneer sheet  330 A. Likewise, since in this specific example veneer sheet  330 A is a dry veneer sheet, the NIR greyscale image  420  of wood product first surface  332  of veneer sheet  330 A is also relatively uniform in appearance and greyscale coloration. 
       FIG. 4B  shows a first surface  332  of a veneer sheet  330 B as seen in a visual image  430  of the veneer sheet  330 B and as seen in an NIR greyscale image  440  of the veneer sheet  330 B. In the example of  FIG. 4B , veneer sheet  330 B has an average moisture level that is less than 6% but includes a very high moisture pocket  490 . 
     It is again worth noting that visual image  430  and NIR greyscale image  440  can be images of the entire wood product first surface  332  of veneer sheet  330 B, i.e., can be a 4′×8′ sample. In addition, as noted above, using a standard 1.3 mega pixel camera to obtain NIR greyscale image  440  of the entire wood product first surface  332  of veneer sheet  330 B there are as many as 1,300,000 data points, i.e., each pixel is a data point. This, in turn, gives rise to resolutions unheard of using traditional moisture detection systems and accuracy previously unknown in the art. 
     This is in sharp contrast to the 128 9″×3″ samples of traditional contact electrode systems or the 32 12″×12″ samples of traditional RF systems that, as discussed above, yielded ±5.0% or ±7.5% margins of error, respectively. Indeed, using these traditional moisture detection systems, very high moisture pocket  490  could easily be missed or determined to be larger than it actually is because of these large sample sizes and large margins of error. 
     As seen in  FIG. 4B , the visual image  430  of the wood product first surface  332  of veneer sheet  330 B is relatively uniform in visual appearance and coloration, i.e., no moisture can be readily detected visually in visual image  430  of the wood product first surface  332  of veneer sheet  330 B. However, in this specific example, NIR greyscale image  440  of wood product first surface  332  of veneer sheet  330 B clearly shows very high moisture pocket  490  as a dark region of a higher greyscale value. Consequently, though virtually invisible to the eye, high moisture pocket  490  can readily be seen/detected in NIR greyscale image  440 . 
     According to the disclosed embodiments, the level of moisture in very high moisture pocket  490  can then be determined by mapping the NIR greyscale image data  364  representing NIR greyscale image  440  and using the mapping data  312  from moisture to greyscale mapping database  310  to identify moisture levels for very high moisture pocket  490  and the wood product  330 B. 
     Grade assignment module  380  can then assign a grade to the wood product  330 B based on the identified moisture levels for very high moisture pocket  490  and the wood product  330 B. As discussed above, action selection and activation module  390  can then select an appropriate action based, at least in part, on the grade indicated by grade assignment data  382 . 
       FIG. 4C  shows a first surface  332  of a veneer sheet  330 C as seen in a visual image  450  of the veneer sheet  330 C and as seen in an NIR greyscale image  460  of the veneer sheet  330 C. In the example of  FIG. 4C , veneer sheet  330 C has an average moisture level that is less than 10% but includes a high moisture pocket  495 . 
     As seen in  FIG. 4C , the visual image  450  of the wood product first surface  332  of veneer sheet  330 C is still relatively uniform in visual appearance and coloration, i.e., no moisture can be readily detected visually in visual image  450  of the wood product first surface  332  of veneer sheet  330 C. However, in this specific example, NIR greyscale image  460  of wood product first surface  332  of veneer sheet  330 C clearly shows high moisture pocket  495  as a dark region of a higher greyscale value than the surrounding areas. Consequently, though virtually invisible to the eye, high moisture pocket  495  can readily be seen/detected in NIR greyscale image  460 . 
     According to the disclosed embodiments, the level of moisture in high moisture pocket  495  can then be determined by mapping the NIR greyscale image data  364  representing NIR greyscale image  460  and using the mapping data  312  from moisture to greyscale mapping database  310  to identify moisture levels for high moisture pocket  460  and wood product  330 C. 
     Grade assignment module  380  can then assign a grade to the wood product  330 C based on the identified moisture levels for high moisture pocket  495  and the wood product  330 C. Action selection and activation module  390  can then select an appropriate action based, at least in part, on the grade indicated by grade assignment data  382 . 
     Those of skill in the art will ready recognize that the specific illustrative examples of one embodiment of  FIGS. 3A, 4A, 4B, and 4C  are but specific examples of numerous possible production environments, arrangement of components, and images. Consequently, the specific illustrative examples of one embodiment shown in  FIGS. 3A, 4A, 4B, and 4C  are not intended to limit the scope of the invention as set forth in the claims below. 
     As a specific illustrative example of potential variations, in various embodiments, the NIR analysis station  320  can include one or more illumination sources  322  positioned to illuminate two or more surfaces of a wood product and one or more NIR cameras  324  positioned to capture one or more NIR images of the two or more illuminated surfaces of the wood product. 
     As a further specific illustrative example of variations possible, additional input data can be considered such as current ambient temperature and humidity. The combination of these parameters can be analyzed by an AI/ML algorithm to further refine the control process for material drying optimization and overall process efficiency. 
     As a another illustrative example of variations possible, multiple NIR cameras can be placed at one or more locations relative to the wood product to capture an image of the entire wood product or a portion of the wood product being subjected to moisture testing; such as at one or more of (i) above a wood product; (ii) below a wood product; (iii) at one or both sides of the wood product and/or at a position to capture an image of the product at an angle, such as at an angle of 20° to 45° (e.g. 30°) from either above or below the wood product or both. The multiple images captured from each of these cameras can be combined to form a composite image. This can smooth out any variations in detected moisture content from the actual moisture content that could be detected by capturing an image only from a single angle. 
     As another illustrative example of variations possible, multiple NIR cameras can be used and operated, for example, at respective different wavelengths from one another within this NIR range to provide more information about the moisture content of the wood product being analyzed. A specific more desirable wavelength at which the NIR cameras can be operated can be at one or more wavelengths in the range of, or in the range of about, from 1350 nm to 1550 nm. In some examples, the NIR camera can operate at a wavelength in the range of, or in the range of about, from 1400 nm to 1450 nm. 
     These and numerous other variations are possible and contemplated by the inventors to be within the scope of the invention as set forth in the claims below. 
       FIG. 3B  shows one example of one embodiment of a physical system layout for detecting moisture levels in a wood product using NIR technology in accordance with one embodiment. 
     Those of skill in the art will ready recognize that the specific illustrative example of one embodiment of a physical production environment  301  and components shown in  FIG. 3B  is but one example of numerous possible production environments and arrangement of physical components. Consequently, the specific illustrative example of one embodiment of a physical production environment  301  and components shown in  FIG. 3B  is not intended to limit the scope of the invention as set forth in the claims below. 
       FIG. 5  is flow chart of a process  500  for detecting moisture levels in a wood product using NIR technology in accordance with one embodiment. 
     As seen in  FIG. 5 , process  500  begins at BEGIN operation  502  and then process proceeds to operation  504 . In one embodiment, at operation  504  a moisture level to greyscale mapping database is generated such as any database discussed above with respect to  FIGS. 3A and 3B . In one embodiment, the moisture level to greyscale mapping database contains mapping data that maps moisture level to Near InfraRed (NIR) image greyscale values for one or more wood products. 
     In one embodiment, the mapping data is obtained through one or more empirical and/or manual processes. In one embodiment, sample wood products as first dried in a kiln or similar environment while the weight of the sample wood product is monitored. As the sample wood product dries, i.e., loses moisture, the weight of the sample wood product deceases. Once the weight of the wood product stabilizes for a defined period, such as 24 hours, the sample wood product is determined to contain minimal moisture. 
     Then the sample wood product is brought up in moisture content in defined increments, such as one percent of the dry sample wood product weight. At each increment, an NIR image of the sample wood product is taken and the greyscale value at that increment of moisture is determined. The greyscale value determined is then correlated to the specific moisture level at that increment. 
     This process is continued for multiple increments until a maximum moisture content is obtained and greyscale data for each increment is determined and correlated to the respective moisture content increment. In this way, mapping data  312  mapping each specific moisture content to a specific greyscale value is generated for the sample wood product. The process can then be repeated for different wood products, different types of wood, and under varying parameters and conditions. 
     Once a moisture level to greyscale mapping database is generated at operation  504 , process flow proceeds to operation  506 . At operation  506 , an NIR analysis station is provided. In one embodiment, the NIR analysis station is substantially similar to any NIR analysis station discussed above with respect to  FIGS. 3A and 3B . As discussed above, in one embodiment, the NIR analysis station includes one or more sources of illumination positioned to illuminate a surface of a wood product and one or more NIR cameras positioned to capture one or more NIR images of the illuminated surface of the wood product. 
     Once an NIR analysis station is provided at operation  506 , process flow proceeds to operation  508 . In one embodiment, at operation  508 , a wood product to be analyzed is positioned in the NIR analysis station of operation  506  such that a first surface of the wood product to be analyzed is illuminated by the one or more illumination sources using any of the methods and systems discussed above with respect to  FIGS. 3A and 3B . 
     Once the wood product to be analyzed is positioned in the NIR analysis station at  508 , process flow proceeds to operation  510 . In one embodiment, at operation  510  the one or more NIR cameras of NIR analysis station take one or more NIR images of the illuminated first surface of the wood product using any of the methods and systems discussed above with respect to  FIGS. 3A and 3B . 
     Once the one or more NIR cameras of NIR analysis station take one or more NIR images of the illuminated first surface of the wood product at operation  510 , process flow proceeds to operation  512 . 
     In one embodiment, at operation  512 , the one or more NIR images of the illuminated first surface of the wood product of operation  510  are processed using any of the methods and systems discussed above with respect to  FIGS. 3A and 3B , to generate NIR greyscale images indicating different moisture levels in the illuminated first surface of the wood product. 
     Once the one or more NIR images of the illuminated first surface of the wood product are processed to generate NIR greyscale images indicating different moisture levels in the illuminated first surface of the wood product at operation  512 , process flow proceeds to operation  514 . 
     In one embodiment, at operation  514 , the NIR greyscale images are processed using the moisture level to greyscale mapping database to identify moisture levels for the first surface of the wood product by any of the methods and systems discussed above with respect to  FIGS. 3A and 3B . 
     Once the NIR greyscale images are processed using the moisture level to greyscale mapping database to identify moisture levels for the first surface of the wood product at operation  514 , process flow proceeds operation  516 . 
     In one embodiment, at operation  516  a grade is assigned to the wood product based on the identified moisture levels for the first surface of the wood product using any of the methods and systems discussed above with respect to  FIGS. 3A and 3B . 
     Once a grade is assigned to the wood product based on the identified moisture levels for the first surface of the wood product at operation  516 , process flow proceeds to operation  518 . In one embodiment, at operation  518 , based, at least in part, on the grade assigned to the wood product, one or more actions are taken with respect to the wood product including any of the actions discussed above with respect to the methods and systems discussed above with respect to  FIGS. 3A and 3B . 
     Once one or more actions with respect to the wood product at operation  518 , process flow proceeds to END operation  524  where process  500  is exited to await new samples and/or data. 
     In some embodiments, one or more visual cameras are implemented along with the one or more NIR camera to provide the capability to generate superimposed image data representing a visual/NIR composite image of wood product and correlating moisture levels with physical features of the surfaces of the wood product. 
       FIG. 6  is simplified block diagram of one embodiment of a system  600  for detecting moisture levels in a wood product using NIR technology and visual data in accordance with one embodiment. 
     In one embodiment, system  600  for detecting moisture levels in wood products, like system  300  of  FIG. 3A  and  FIG. 3B , includes a production environment  301  and a computing environment  350 . 
     As seen in  FIG. 6 , as in system  300  of  FIG. 3A  and  FIG. 3B , production environment  301  includes NIR analysis station  320  and selected action implementation module  396 . As seen in  FIG. 6 , like system  300  of  FIG. 3A  and  FIG. 3B , NIR analysis station  320  includes one or more illumination sources, such as illumination source  322 , positioned to illuminate a wood product first surface  332  of a wood product  330 . In various embodiments, the one or more sources of illumination can include one or more LED light sources. In other embodiments, the one or more illumination sources, such as illumination source  322 , can include, but are not limited to, halogen or halogen and tungsten light sources, or any other light sources, as discussed herein, and/or as known in the art at the time of filing, and/or as developed after the time of filing. 
     As seen in  FIG. 6 , like system  300  of  FIG. 3A  and  FIG. 3B , NIR analysis station  320  also includes one or more NIR cameras, such as NIR camera  324 , positioned to capture NIR image data  362  representing one or more NIR images of the illuminated wood product first surface  332  of the wood product  330 . In one embodiment, one or more NIR cameras, such as NIR camera  324 , are adjustably positioned and adjustably focused to capture one or more NIR images of the illuminated wood product first surface  332  of the wood product  330 . 
     However, unlike like system  300  of  FIG. 3A  and  FIG. 3B , system  600  includes one or more visual cameras, such as visual camera  624 , used to take visual images of wood product first surface  332  of wood product  330  and generate visual image data  662 . 
     As discussed in more detail below, the combination of visual image data  662  and NIR image data  362  allows for the generation of superimposed image data  664  representing a visual/NIR composite image of wood product first surface  332  of wood product  330 . The visual/NIR composite image of wood product first surface  332  of wood product  330  indicates not only the presence and location of moisture, as was done using system  300 , but also the location of any physical features in wood product first surface  332  of wood product  330  and the physical proximity of these features to the moisture detected in wood product first surface  332  of wood product  330 . 
     This can be an important capability because, as explained above, it is trapped pockets of moisture that, when heated, become vapor and cause the bulges and/or damage to the wood product structure as the vapor tires to expand and escape. However, if the detected moisture is physical proximate to an open physical feature, such as a knot, knot hole, or side of the wood product, then the open physical feature provides the vapor an avenue for escape without causing damage to wood product. 
     Consequently, by analyzing the visual/NIR composite image represented by superimposed image data  664 , moisture pockets near an open physical feature that, absent the presence open physical feature would be a problem, can be identified and ignored. 
     As seen in  FIG. 6 , and as discussed below, a wood product  330  to be analyzed in the NIR analysis station  320  is positioned in NIR analysis station  320 . In various embodiments, the wood product  330  can be any wood product as discussed herein, and/or as known in the art at the time of filing and/or as becomes known after the time of filing. In one embodiment, the wood product  330  to be analyzed is a veneer sheet. 
     In one embodiment, the wood product  330  to be analyzed is positioned such that a wood product first surface  332  of the wood product  330  to be analyzed is illuminated by the illumination source  322  and is within view and focus of NIR camera  324  and visual camera  624 . In one embodiment, the wood product  330  is positioned in the NIR analysis station  320  by passing the wood product through the NIR analysis station  320  on a conveyor system (not shown in  FIG. 6  but shown as  321  in  FIG. 3B  and discussed above). 
     As seen in  FIG. 6 , computing environment  350  includes computing system  352 . As seen in  FIG. 6 , as with system  300  of  FIGS. 3A and 3B , in one embodiment, computing system  352  includes moisture to greyscale mapping database  310  containing mapping data  312  that maps moisture level to Near InfraRed (NIR) image greyscale values for one or more wood products. 
     As seen in  FIG. 6 , as with system  300  of  FIGS. 3A and 3B , computing system  352  includes physical memory  360 . For use with system  600 , physical memory  360  includes NIR image data  362  representing one or more NIR images of the illuminated wood product first surface  332  of the wood product  330  captured using NIR camera  324 , visual image data  662  representing one or more visual images of the illuminated wood product first surface  332  of the wood product  330  captured using visual camera  624 , and superimposed image data  664  representing a visual/NIR composite image of wood product first surface  332  of wood product  330 , as discussed above. 
     As seen in  FIG. 6 , in one embodiment, computing system  352  includes one or more processors  370  for processing the NIR image data  362  representing one or more NIR images of the illuminated wood product first surface  332  of the wood product  330  to generate NIR greyscale image data  364  indicating different moisture levels in the illuminated wood product first surface  332  of the wood product  330 . 
     In one embodiment, processor  370  processes the NIR greyscale image data  364  using the mapping data  312  from moisture to greyscale mapping database  310  data to identify moisture levels for the wood product first surface  332  of the wood product  330 . 
     In the specific embodiment of  FIG. 6 , processors  370  also process visual image data  662  and NIR greyscale image data  364  to generate superimposed image data  664  representing a visual/NIR composite image of wood product first surface  332  of wood product  330 , as discussed above. 
       FIG. 7A  shows a black and white visual image  701  of a wood product first surface  732  of a veneer sheet  730 . As seen in  FIG. 7A , wood product first surface  732  includes physical features  712  which, in this specific illustrative example, are knots and knot holes. 
       FIG. 7B  shows a color visual image  711  of wood product first surface  732  of veneer sheet  730 , including physical features  712  which, as noted, in this specific illustrative example, are knots and knot holes. 
       FIG. 7C  shows a superimposed composite image  721  of the wood product first surface  732  of the wood product  730 . As seen in  FIG. 7C , superimposed composite image  721  includes the visual images of physical features  712  of either black and white visual image  701  or color visual image  711 . However, superimposed on these visual images is a NIR greyscale image including NIR greyscale images of high moisture pockets  750 ,  751 , and  752 . 
     The superimposed composite image  721  not only shows the areas of high moisture, i.e., high moisture pockets  750 ,  751 , and  752 , but also their proximity to physical features  712  which, in this specific illustrative example, are knots and knot holes. By analyzing the superimposed composite image  721 , moisture pockets near an open physical feature, such as high moisture pockets  750  and  752  that, absent the presence open physical features/knots  712 , would be a problem can be identified and ignored. 
       FIG. 7D  shows a color enhanced superimposed composite image  731  that is created using a greyscale to color mapping database to provide even more pronounced visualization of the high moisture pockets  750 ,  751 , and  752 . 
     It is worth noting again that visual images  701 ,  711 ,  721 , and  731  can be images of the entire wood product first surface  732  of veneer sheet  730 , i.e., can be a 4′×8′ sample. In addition, as noted above, using a standard 1.3 mega pixel camera to obtain images  701 ,  711 ,  721 , and  731  of the entire wood product first surface  732  of veneer sheet  730  there are as many as 1,300,000 data points, i.e., each pixel is a data point. This, in turn, gives rise to very high resolution and is in sharp contrast to the 128 9″×3″ samples of traditional contact electrode systems or 32 12″×12″ samples of traditional RF systems that, as discussed above, yielded ±5.0% or ±7.5% margins of error, respectively. 
     As seen in  FIG. 6 , in one embodiment, computing system  352  includes a grade assignment module  380  for assigning a grade to the wood product  330  based on the identified moisture levels and visual data of superimposed image data  664  for the wood product first surface  332 . As seen in  FIG. 3A , grade assignment module  380  includes moisture analysis module  374  which, along with processor  370 , processes superimposed image data  664  for the wood product first surface  332  to identify moisture levels and open features for the wood product first surface  332  of the wood product  330 . As a result of the processing by moisture analysis module  374  and processor  370 , grade assignment data  382  is generated. 
     As seen in  FIG. 6 , in one embodiment, grade assignment data  382  is provided to action selection and activation module  390  which selects an appropriate action of the actions represented in available actions data  392  based, at least in part on the grade indicated by grade assignment data  382 . As seen in  FIG. 6 , in one embodiment, the determined appropriate action is represented by selected action data  394 . 
     As seen in  FIG. 6 , in one embodiment, selected action data  394  is forwarded to an action activation module such as selected action implementation module  396  in production environment  301  to initialize one or more actions with respect to the wood product  330  based, at least in part, on the grade represented by grade assignment data  382  and assigned to the wood product  330  by action selection and activation module  390 . 
     In one embodiment, one or more actions that can be taken represented in available actions data  392  include, but are not limited to: sorting the wood product  330  into a bin or location associated with the grade represented by grade assignment data  382  and assigned to the wood product  330 ; restricting the use of the wood product  330  based on the grade represented by grade assignment data  382  and assigned to the wood product  330 ; rejecting the wood product  330  based on the grade represented by grade assignment data  382  and assigned to the wood product  330 ; sending the wood product  330  back for further processing based on the grade represented by grade assignment data  382  and assigned to the wood product  330 ; adjusting one or more processing parameters of a production line in production environment  301  based, at least in part, on the grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products; adjusting drying temperatures on a production line in production environment  301  based, at least in part, on grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products; adjusting drying times on a production line in production environment  301  based, at least in part, on grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products; and; and selecting a type and amounts of glues used on a production line in production environment  301  based, at least in part, on grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products. 
     Those of skill in the art will ready recognize that the specific illustrative examples of embodiments of  FIGS. 6, 7A, 7B, 7C, and 7D  are but specific example of numerous possible production environments, arrangement of components, and images. Consequently, the specific illustrative examples of embodiments of  FIGS. 6, 7A, 7B, 7C, and 7D  are not intended to limit the scope of the invention as set forth in the claims below. 
     As a specific illustrative example of potential variations, in various embodiments, the NIR analysis station  320  can include one or more illumination sources  322  positioned to illuminate two or more surfaces of a wood product and one or more NIR cameras  324  positioned to capture one or more NIR images of the two or more illuminated surfaces of the wood product. In one embodiment, one or visual cameras  624  can be positioned to capture one or more NIR images of the two or more illuminated surfaces of the wood product. 
       FIG. 8  is flow chart of a process  800  for detecting moisture levels in a wood product using NIR technology and visual data in accordance with one embodiment. 
     As seen in  FIG. 8 , process  800  begins at BEGIN operation  802  and then process proceeds to operation  804 . In one embodiment, at operation  804  a moisture level to greyscale mapping database is generated such as any database discussed above with respect to  FIGS. 3A, 3B and 6 . In one embodiment, the moisture level to greyscale mapping database contains mapping data that maps moisture level to Near InfraRed (NIR) image greyscale values for one or more wood products. 
     Once a moisture level to greyscale mapping database is generated at operation  804 , process flow proceeds to operation  806 . At operation  806 , an NIR analysis station is provided. In one embodiment, the NIR analysis station is substantially similar to any NIR analysis station discussed above with respect to  FIGS. 3A, 3B, and 6 . As discussed above, in one embodiment, the NIR analysis station includes one or more sources of illumination positioned to illuminate a surface of a wood product and one or more NIR cameras positioned to capture one or more NIR images of the illuminated surface of the wood product. 
     Returning to  FIG. 8 , once an NIR analysis station is provided at operation  806 , process flow proceeds to operation  808 . In one embodiment, at operation  808  a visual analysis station is provided including one or more visual image cameras such as any visual cameras discussed above with respect to  FIG. 6 . In one embodiment, one or more visual image cameras are adjustably positioned to capture visual images of the first surface of the wood product using any method or system as discussed above with respect to  FIGS. 3A, 3B, and 6 . 
     In one embodiment, once one or more visual image cameras are provided at operation  808 , process flow proceeds to operation  810 . In one embodiment, at operation  810 , a wood product to be analyzed is positioned in the NIR analysis station of operation  806  such that a first surface of the wood product to be analyzed is illuminated by the one or more illumination sources using any of the methods and systems discussed above with respect to  FIGS. 3A, 3B and 6 . 
     Once the wood product to be analyzed is positioned in the NIR analysis station at operation  810 , process flow proceeds to operation  812 . In one embodiment, at operation  812  the one or more NIR cameras of NIR analysis station take one or more NIR images of the illuminated first surface of the wood product using any of the methods and systems discussed above with respect to  FIGS. 3A, 3B and 6 . 
     Once the one or more NIR cameras of NIR analysis station take one or more NIR images of the illuminated first surface of the wood product at operation  812 , process flow proceeds to operation  814 . 
     In one embodiment, at operation  814 , the one or more NIR images of the illuminated first surface of the wood product of operation  812  are processed using any of the methods and systems discussed above with respect to  FIGS. 3A, 3B and 6 , to generate NIR greyscale images indicating different moisture levels in the illuminated first surface of the wood product. 
     Once the one or more NIR images of the illuminated first surface of the wood product are processed to generate NIR greyscale images indicating different moisture levels in the illuminated first surface of the wood product at operation  814 , process flow proceeds to operation  816 . 
     In one embodiment, at operation  816 , the NIR greyscale images are processed using the moisture level to greyscale mapping database to identify moisture levels for the first surface of the wood product by using any of the methods and systems discussed above with respect to  FIGS. 3A, 3B and 6 . 
     Once the NIR greyscale images are processed using the moisture level to greyscale mapping database to identify moisture levels for the first surface of the wood product at operation  816 , process flow proceeds operation  818 . 
     In one embodiment, at operation  818 , the wood product is positioned in the visual analysis station of operation  808  such that one or more visual images of the first surface of the wood product can be captured using the one or more visual image cameras of operation  808  and using any of the methods and systems discussed above with respect to  FIGS. 3A, 3B and 6 . 
     Once the wood product is positioned such that one or more visual images of the first surface of the wood product can be captured at operation  818 , process flow proceeds to operation  820 . In one embodiment at operation  820  one or more visual images of the first surface of the wood product are captured using the one or more visual image cameras of operation  808  and using any of the methods and systems discussed above with respect to  FIGS. 3A, 3B and 6 . 
     Once one or more visual images of the first surface of the wood product are captured at operation  820 , process flow proceeds to operation  822 . In one embodiment, at operation  822  the one or more NIR greyscale images and the one or more visual images of the first surface of the wood product are processed to generate NIR greyscale and visual superimposed images of the first surface of the wood product correlating different moisture levels and visual elements in the first surface of the wood product using any of the methods and systems discussed above with respect to  FIGS. 3A, 3B and 6 . 
     As noted above, the combination of visual image data and NIR image data allows for the generation of superimposed image data and a visual/NIR composite image of the wood product first surface. The visual/NIR composite image of the wood product first surface indicates not only the presence and location of moisture, as was done using process  500 , but also the location of any physical features in wood product first surface of the wood product and the physical proximity of these features to the moisture detected in wood product first surface. 
     This can be critical feature because, as explained above, it is trapped pockets of moisture that, when heated, become vapor and cause the bulges and/or damage to the wood product structure as the vapor tires to expand and escape. However, if the detected moisture is physical proximate to open physical feature, such as a knot, knot hole, or side of the wood product, then the open physical feature provides the vapor an avenue for escape without causing damage to wood product. 
     Consequently, by analyzing the visual/NIR composite image represented by superimposed image data of operation  822  at operation  824  discussed below, moisture pockets near an open physical feature that, absent the presence of the open physical feature would be an issue, can be identified and ignored. 
     Once the one or more NIR greyscale images and the one or more visual images of the first surface of the wood product are processed to generate NIR greyscale and visual superimposed images of the first surface of the wood product correlating different moisture levels and visual elements in the first surface of the wood product at operation  822 , process flow proceeds to operation  824 . 
     In one embodiment, at operation  824  a grade is assigned to the wood product based on the identified moisture levels and visual elements in the first surface of the wood product using any of the methods and systems discussed above with respect to  FIGS. 3A, 3B and 6 . 
     Once a grade is assigned to the wood product based on the identified moisture levels and visual elements in the first surface of the wood product at operation  824 , process flow proceeds to operation  826 . In one embodiment, at operation  826 , based, at least in part, on the grade assigned to the wood product, taking one or more actions with respect to the wood product including any of the actions discussed above with respect to the methods and systems discussed above with respect to  FIGS. 3A, 3B and 6 . 
     Once one or more actions with respect to the wood product at operation  818 , process flow proceeds to END operation  834  where process  800  is exited to await new samples and/or data. 
     In some embodiments, machine leaning based models are used to predict moisture levels and behavior of wood products based on NIR image data for a wood product under analysis. 
       FIG. 9  is simplified block diagram of one embodiment of a system  900  for detecting moisture levels in a wood product using NIR technology and machine learning methods in accordance with one embodiment. 
     In one embodiment, system  900  for detecting moisture levels in wood products, like system  300  of  FIGS. 3A and 3B , includes production environment  301  and a computing environment  350 . 
     As seen in  FIG. 9 , like system  300  of  FIGS. 3A and 3B , production environment  301  includes NIR analysis station  320  and selected action implementation module  396 . As seen in  FIG. 9 , NIR analysis station  320  includes one or more illumination sources, such as illumination source  322 , positioned to illuminate a wood product first surface  332  of a wood product  330 . In various embodiments, the one or more sources of illumination, such as illumination source  322 , can include one or more LED light sources. In other embodiments, the one or more illumination sources, such as illumination source  322 , can include, but are not limited to, halogen or halogen and tungsten light sources, or any other light sources, as discussed herein, and/or as known in the art at the time of filing, and/or as developed after the time of filing. 
     As seen in  FIG. 9 , NIR analysis station  320  also includes one or more NIR cameras, such as NIR camera  324 , positioned to capture NIR image data  362  representing one or more NIR images of the illuminated wood product first surface  332  of the wood product  330 . In one embodiment, one or more NIR cameras, such as NIR camera  324 , are adjustably positioned and adjustably focused to capture one or more NIR images of the illuminated wood product first surface  332  of the wood product  330 . 
     As seen in  FIG. 9 , and as discussed below, the wood product  330  to be analyzed in the NIR analysis station  320  is positioned in NIR analysis station  320 . In various embodiments, the wood product  330  can be any wood product as discussed herein, and/or as known in the art at the time of filing and/or as becomes known after the time of filing. In one embodiment, the wood product  330  to be analyzed is a veneer sheet. 
     In one embodiment, the wood product  330  to be analyzed is positioned such that the wood product first surface  332  of the wood product  330  to be analyzed is illuminated by the illumination source  322  and is within view and focus of NIR camera  324 . In one embodiment, the wood product  330  is positioned in the NIR analysis station  320  by passing the wood product  330  through the NIR analysis station  320  on a conveyor system (not shown in  FIG. 9  but shown as  321  in  FIG. 3B  and discussed below). 
     As seen in  FIG. 9 , like system  300  of  FIGS. 3A and 3B , computing environment  350  includes computing system  352 . However, unlike system  300  of  FIGS. 3A and 3B , as seen in  FIG. 9 , in one embodiment, computing system  352  of system  900  does not include moisture to greyscale mapping database  310  but instead includes moisture prediction module  910 . 
     In one embodiment, moisture prediction module  910  includes one or more trained Machine Learning (ML) based moisture level detection models, such as Machine Learning (ML) based moisture detection model  912 . In various embodiments the one or more trained machine learning based moisture level detection models, such as machine learning based moisture detection model  912 , are trained using NIR image data for one or more wood products and corresponding determined moisture levels for the one or more wood products. 
     Various types of machine learning based models are well known in the art. Consequently the one or more trained machine learning based moisture level detection models, such as machine learning based moisture detection model  912 , can be any machine learning based model type or use any machine learning based algorithm, as discussed herein, and/or as known in the art at the time of filing, and/or as becomes known or available after the time of filing. 
     Specific illustrative examples of machine learning based model types and machine learning based algorithms that can be used for, or with, the one or more trained machine learning based moisture level detection models of moisture prediction module  910 , such as machine learning based moisture detection model  912 , include, but are not limited to: supervised machine learning-based models; semi-supervised machine learning-based models; unsupervised machine learning-based models; classification machine learning-based models; logistical regression machine learning-based models; neural network machine learning-based models; and deep learning machine learning-based models. 
     In various embodiments, and largely depending on the machine-learning based models used, the NIR image data for one or more wood products, including in some cases various environmental and production parameters, and corresponding determined moisture levels for the one or more wood products can be processed using various methods known in the machine learning arts to identify elements and vectorize the NIR image data and/or corresponding determined moisture levels data. As a specific illustrative example, in a case where the machine leaning based model is a supervised model, the NIR image data can be analyzed and processed into elements found to be indicative of a wood product moisture levels and product performance. Then these elements are used to create vectors in multidimensional space which are, in turn, used as input data for one or more machine learning models. The correlated determined moisture levels data for each NIR image data vector is then used as a label for the resulting vector. This process is repeated for multiple, often millions, of correlated pairs of NIR image data vector and determined moisture levels data with the result being one or more trained machine learning based moisture level detection models. 
     Then when new NIR image data is obtained, this new NIR image data is also vectorized and the new NIR image vector data is provided as input data to the one or more trained machine learning based moisture level detection models. The new NIR image vector data is then processed to find a distance between the new NIR image vector and previously labeled NIR image vectors, whose associated moisture level data is known. Based on a calculated distance between the new NIR image vector data and the previously labeled NIR image vector data, a probability that the new NIR image vector data correlates to a moisture level associated with the previously labeled NIR image vector data can be calculated. This results in a probability score for the wood product being analyzed. 
     Those of skill in the art will readily recognize that there are many different types of machine learning based models known in the art. Consequently, the specific illustrative example of a specific supervised machine learning based model discussed above is not limiting. 
     As seen in  FIG. 9 , computing system  352  also include physical memory  360 . in one embodiment, the physical memory  360  includes NIR image data  362  representing one or more NIR images of the illuminated wood product first surface  332  of the wood product  330  captured using NIR camera  324 . 
     As seen in  FIG. 9 , in one embodiment, computing system  352  includes one or more processors, such as processor  370 , for generating the NIR image data  362  representing one or more NIR images of the illuminated wood product first surface  332  of the wood product  330  from NIR camera  324 . 
     In one embodiment, NIR image data  362  is provided to moisture prediction module  910  where it is processed/vectorized and provided to machine learning based moisture level detection model  912 . 
     Machine learning based moisture level detection model  912  then processes the vectorized NIR image data  362  as discussed above and generates moisture level prediction data  914  for the wood product  330 . 
     As seen in  FIG. 9 , moisture level prediction data  914  for the wood product  330  is then provided to grade assignment module  380 . As discussed above, grade assignment module  380  then assigns a grade to the wood product  330  based on moisture level prediction data  914  for the wood product  330 . 
     As seen in  FIG. 9 , grade assignment module  380  includes moisture analysis module  374  which, along with processor  370 , processes moisture level prediction data  914  for the wood product  330  and generates grade assignment data  382  based on this processing 
     As seen in  FIG. 9 , in one embodiment, grade assignment data  382  is provided to action selection and activation module  390  which selects an appropriate action of the actions represented in available actions data  392  based, at least in part on the grade indicated by grade assignment data  382 . As seen in  FIG. 9 , in one embodiment, the determined appropriate action is represented by selected action data  394 . 
     As seen in  FIG. 9 , in one embodiment, selected action data  394  is forwarded to an action activation module, such as selected action implementation module  396  in production environment  301  to initialize one or more actions with respect to the wood product  330  based, at least in part, on the grade represented by grade assignment data  382  and assigned to the wood product  330  by action selection and activation module  390 . 
     In one embodiment, one or more actions that can be taken represented in available actions data  392  include, but are not limited to: sorting the wood product  330  into a bin or location associated with the grade represented by grade assignment data  382  and assigned to the wood product  330 ; restricting the use of the wood product  330  based on the grade represented by grade assignment data  382  and assigned to the wood product  330 ; rejecting the wood product  330  based on the grade represented by grade assignment data  382  and assigned to the wood product  330 ; sending the wood product  330  back for further processing based on the grade represented by grade assignment data  382  and assigned to the wood product  330 ; adjusting one or more processing parameters of a production line in production environment  301  based, at least in part, on the grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products; adjusting drying temperatures on a production line in production environment  301  based, at least in part, on grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products; adjusting drying times on a production line in production environment  301  based, at least in part, on grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products; and selecting a type and amount of glues used on a production line in production environment  301  based, at least in part, on grade represented by grade assignment data  382  and assigned to the wood product  330  and/or the grades assigned other wood products. 
     Those of skill in the art will ready recognize that the specific illustrative example of one embodiment of  FIG. 9  is but one example of numerous possible production environments and arrangement of components. Consequently, the specific illustrative example of one embodiment shown in  FIG. 9  is not intended to limit the scope of the invention as set forth in the claims below. 
     As a specific illustrative example of possible variations, in some embodiments, the NIR analysis station  320  can include one or more illumination sources  322  positioned to illuminate two or more surfaces of a wood product and one or more NIR cameras  324  positioned to capture one or more NIR images of the two or more illuminated surfaces of the wood product. 
     As noted above, embodiments of the present disclosure also provide an effective and efficient technical solution to the technical problem of providing a method and system for determining the strength of a wood product that is reliable, consistent, and economically feasible to implement. 
     Embodiments of the present disclosure utilize Near InfraRed (NIR) technology, including Near InfraRed/Short Wave InfraRed (NIR/SWIR) cameras and detectors, to accurately determine the strength of green and/or dry the wood products, such as veneer. To this end, in one embodiment, one or more NIR green strength analysis systems, including one or more NIR green wood product strength analysis stations, are provided. 
       FIG. 10  is simplified block diagram of a NIR green wood product strength analysis process  1000  for determining the strength of a green wood product in accordance with one embodiment. 
     As seen in  FIG. 10 , in one embodiment, the green wood product is green veneer created by peeling thin layers of wood from a peeler log  1001 , or other lumber source, in a continuous manner. This process is similar to unrolling a bolt of cloth. Also shown in  FIG. 10  is pressure bar  1002 , knife  1004 , lathe chuck  105 , conveyor  1010 , and green veneer ribbon  1013 . 
     The resulting green wood product, in this case relatively thin green veneer layer or “ribbon”  1013  is then provided to NIR green wood product strength analysis system  1020  by conveyor  1010 . In one embodiment, green veneer ribbon  1013  is analyzed by NIR green wood product strength analysis system  1020  as discussed below and a grade is assigned to the veneer ribbon  1013 . 
     The veneer ribbon  1013  is then cut to individual green veneer sheets of specific green veneer sheet dimensions at cutting station  1030 . The individual green veneer sheets  1043  are then stacked into green veneer sheet stacks  1053  at automated stacking station  1040 . In one embodiment, at automated stacking station  1040  the individual green veneer sheets  1043  are stacked according to the grade assigned to the parent veneer ribbon section. 
     In one embodiment, at automated stacking station  1040  the individual green veneer sheets  1043  are stacked according to the grade assigned to the parent green veneer ribbon using any of the stacking systems described in related applications Bolton et al., U.S. application Ser. No. 16/697,458 filed on Nov. 27, 2019 and issuing Aug. 17, 2021 as U.S. Pat. No. 11,090,833; Bolton et al., U.S. application Ser. No. 17/356,804 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/356,805 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/361,808 filed on Jun. 29, 2021; and Bolton et al., U.S. application Ser. No. 17/366,432, filed Jul. 2, 2021, which are hereby incorporated by reference in their entirety as if they were fully set forth herein. 
     In one embodiment, at automated stacking station  1040  the individual green veneer sheets  1043  are stacked according to the grade assigned to the parent veneer ribbon using any stacking system discussed herein, and/or as known in the art at the time of filing, and/or are become known after the time of filing. 
     Consequently, using the disclosed NIR green strength analysis it is possible to collect high quality NIR spectra of wood products, including full size ribbons and/or sheets of green veneer, that contain information and data regarding the mechanical properties of wood product, including strength of the wood product, before moisture analysis is performed. 
       FIG. 11  is simplified block diagram of a NIR green wood product strength analysis system  1020 , including NIR green wood product strength analysis station  1121 , in accordance with one embodiment. 
     Referring now to  FIGS. 10 and 11 , in one embodiment, NIR green wood product strength analysis system  1020  includes a production environment  1101  and a computing environment  1150 . 
     As seen in  FIG. 11 , production environment  1101  includes NIR green wood product strength analysis station  1121  and selected action implementation module  1196 . As seen in  FIG. 11 , NIR green wood product strength analysis station  1121  includes one or more illumination sources, such as illumination source  1122 , positioned to illuminate a surface of a wood product. In various embodiments, the one or more illumination sources, such as illumination source  1122 , can include one or more LED light sources. In other embodiments, the one or more illumination sources, such as illumination source  1122 , can include, but are not limited to, halogen, halogen and tungsten light sources, or any other light sources, as discussed herein, and/or as known in the art at the time of filing, and/or as developed after the time of filing. 
     As used herein, the terms Near InfraRed (NIR) and Short-Wave InfraRed (SWIR) are used interchangeably to include wavelength in the range of 750 nanometers (nm) to 11500 nm. In addition, all stated wave lengths herein are assumed to include values within 10% of the stated value. 
     In one embodiment, the one or more illumination sources, such as illumination source  1122 , are selected to provide a reduced spectral range between 650 and 1050 nm. This enables very rapid collection of the NIR spectra. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     As seen in  FIG. 11 , NIR green wood product strength analysis station  1121  also includes one or more NIR cameras, such as NIR camera  1124 , positioned to capture NIR image data  1162  representing one or more NIR images of the illuminated surface of the green wood product/veneer ribbon  1013 . In one embodiment, the one or more NIR cameras, such as NIR camera  1124 , are adjustably positioned and adjustably focused to capture any desired one or more NIR images of the illuminated, of first, surface  1114  of the green wood product/veneer ribbon  1013 . 
     As seen in  FIG. 11 , and as discussed below, a green wood product/veneer ribbon  1013  to be analyzed in the NIR green wood product strength analysis station  1121  is positioned in NIR green wood product strength analysis station  1121 . In various embodiments, the green wood product/veneer ribbon  1013  can be any green wood product as discussed herein, and/or as known in the art at the time of filing and/or as becomes known after the time of filing. In one embodiment, the green wood product/veneer ribbon  1013  to be analyzed is a green veneer ribbon of multiple veneer sheet lengths  1043 . 
     In one embodiment, the green wood product/veneer ribbon  1013  to be analyzed is positioned such that a wood product first surface  1114  of the green wood product/veneer ribbon  1013  to be analyzed is illuminated by the illumination source  1122  and the entire wood product first surface  1114  is within view and focus of NIR camera  1124 . In one embodiment, the green wood product/veneer ribbon  1013  is positioned in the NIR green wood product strength analysis station  1121  by passing the green wood product/veneer ribbon  1013  through the NIR green wood product strength analysis station  1121  on a conveyor system. 
     In various embodiments, the one or more NIR cameras, such as NIR camera  1124 , can be of any resolution desired. As noted above, when the one or more NIR cameras, such as NIR camera  1124 , are used to scan the wood product first surface  1114  of a green wood product/veneer ribbon  1013  for strength and create NIR image data  1162  of the wood product first surface  1114 , essentially each pixel generated by NIR camera  1124  is a sample point. Consequently, the resolution and accuracy of the strength detection process is only limited by the number of pixels the NIR camera  1124  has covering the field of view, e.g., the entire wood product first surface  1114  of green wood product/veneer ribbon  1013 . Consequently, in the case where NIR camera  1124  is a 1.3 mega pixel camera, there are essentially 1,110,000 individual measurement points on the wood product first surface  1114 . Consequently, using NIR cameras, such as NIR camera  1124 , results in resolutions and accuracy that simply cannot be achieved using traditional detection systems. 
     In some embodiments, strength analysis models are created, and the data obtained from NIR images can be correlated with the strength properties of the green wood product using these models. 
     As seen in  FIG. 11 , computing environment  1150  includes computing system  1152 . As seen in  FIG. 11 , in one embodiment, computing system  1152  includes strength model database  1110  containing one or more strength analysis models and mechanical properties model data  1112 . 
     In one embodiment, the one or more strength analysis models and mechanical properties model data  1112  include models and/or data to predict the Metriguard number, and the actual Modulus Of Rupture (MOR) or stiffness Modulus Of Elasticity (MOE) of veneer values of wood products, such as green or dry veneers and/or for one or more other green wood products. 
     In various embodiments, different methods can be used to correlate the NIR data, i.e., NIR reflectance spectrum data, of a green wood product to a selected property of that green wood product to create the strength models and/or machine learning modules included in strength analysis models and mechanical properties model data  1112 . 
     These correlations have been demonstrated empirically on various different commercial softwoods and hardwoods. These correlations have also been demonstrated on green wood. It has been found that these same correlations also apply to moving 4 ft. by 8 ft. sheet of green veneer using a reduced spectral range. 
     In some embodiment, the NIR spectra of green veneers can be evaluated off-line using two or more different NIR spectrometers. The veneers were then dried in the commercial process and the NIR spectra were collected on the dry veneers. 
     There are a number of methods that can be used to correlate the NIR reflectance spectrum data of a wood sample to some property of that wood sample. One common method is Projection of Latent Structures (PLS) analysis. In some cases, the NIR reflectance spectrum data of the sample are correlated with a response variable, e.g., some measure of the mechanical properties of the wood sample. Since it is not practical to measure the mechanical properties of a full size sheet of veneer, the response variable used for this work was the Metriguard number of the veneer sheet. 
     The Metriguard numbers on the full sized sheets of veneer can be measured using the commercial systems. There are several different ways to generate these PLS correlations and to measure the “quality” of the correlation model. All of these PLS models can be constructed using full cross validation techniques. There are also several different “data pretreatments” that can be applied to the NIR reflectance spectrum data prior to constructing a PLS model. 
     For the NIR reflectance spectrum data measured on green veneers a common data pretreatment known as Orthogonal Signal Correction (OSC) can be used to mathematically “dry” the green samples prior to construction of the PLS models. The procedure for construction of the PLS models involves using about half of the samples to construct a calibration (CALM) model that correlates the measured or “true” Metriguard number with the NIR reflectance spectrum data. This model is then used to predict the Metriguard number from the NIR reflectance spectrum data of a second of samples that were not contained in the original model. These predicted Metriguard numbers are then compared to the measured Metriguard numbers of this second set of samples. 
     Those of skill in the art will also readily recognize that these models can be supplemented and/or replaced with various machine learning and artificial intelligence methods and modules, or any other methods and systems for correlating data, such as the NIR reflectance spectrum data, of a green wood product to a selected property of that green wood product. 
     Empirical results show a correlation coefficient (r) between the measured Metriguard number and the Metriguard number predicted with NIR analysis are relatively good for a heterogeneous substrate like wood, 0.83 and 0.69 respectively. The spectral range was between 650 and 1050 nm which is the range required for rapid acquisition times. 
     There are several general conclusions that can be drawn from these empirical results. The first general conclusion is that the PLS models constructed using the reduced spectral range 650-1050 nm are as good as or better than those constructed using the full spectral range. This is critically important since the use of this reduced spectral range is required for the rapid acquisition times that will be needed for on-line process monitoring. 
     The second general conclusion is that the correlations based on NIR spectra collected from dry veneers is higher than those based on green veneers. 
     A third general conclusion is that that OSC of the NIR data before construction of the PLS models significantly improves the quality of the correlations. There are many different ways to actually construct the PLS models from OSC data and the preferred method will be impacted by the conditions used to collected the NIR spectra. 
     It may be impractical to measure the actual strength MOR or stiffness MOE of a full size sheet of veneer. To better understand the correlations between these two measures of veneer quality a series of 2 ft. by 2 ft. Douglas Fir veneer samples were cut from full size sheets and sent to NREL. These samples were further cut into samples 6 inches wide and 2 ft. long. 
     A portable Metriguard system was used to obtain a Metriguard number for these small samples. The true MOR and MOE were measured in three point bending. 
     Based on the empirical results of this work it is possible to collect high quality NIR reflectance spectrum data of full size sheets of veneers. It is also clear that the NIR reflectance spectrum data contains information on the mechanical properties of veneer. It is also clear that the NIR spectra of either green or dry veneer can be used to construct models that predict the Metriguard number, and the actual MOE and MOR values of veneers. Models based on the reduced spectral range 650-1050 nm are as good as or better than those constructed using the full spectral range. 
     Consequently, using the disclosed NIR green strength analysis it is possible to collect high quality NIR reflectance spectrum data of wood products, including full size ribbons and/or sheets of green veneer that contain information and data regarding the mechanical properties of wood product, including strength of the wood product. 
     As seen in  FIG. 11 , computing system  1152  also includes physical memory  1160 . In one embodiment, the physical memory  1160  includes NIR image data  1162  representing one or more NIR images of the illuminated wood product first surface  1114  of the green wood product/veneer ribbon  1013  captured using NIR camera  1124 . 
     As seen in  FIG. 11 , in one embodiment, computing system  1152  includes one or more processors  1170  for processing the NIR image data  1162  representing one or more NIR images of the illuminated wood product first surface  1114  of the green wood product/veneer ribbon  1013  using the one or more strength analysis models and mechanical properties model data  1112  of strength model database  1110 . 
     As noted above, in one embodiment, the one or more strength analysis models and mechanical properties model data  1112  predict the Metriguard number, and the actual MOE and MOR values of wood products, such as green or dry veneers and/or for one or more other wood products. 
     In one embodiment, processor  1170  processes the NIR image data  1162  using the mechanical properties model data  1112  of strength model database  1110  to determine/predict various mechanical properties of the green wood product/veneer ribbon  1013  and therefore the strength of the green wood product/veneer ribbon  1013 . 
     As seen in  FIG. 11 , in one embodiment, computing system  1152  includes a grade assignment module  1180  for assigning a grade to the green wood product/veneer ribbon  1013  based on determined/predicted mechanical properties of the green wood product/veneer ribbon  1013 . 
     As seen in  FIG. 11 , grade assignment module  1180  includes strength analysis module  1174  which, along with processor  1170 , processes the NIR image data  1162  using the mechanical properties model data  1112  of strength model database  1110  to determine/predict various mechanical properties of the green wood product/veneer ribbon  1013  and therefore the strength of the green wood product/veneer ribbon  1013 . As a result of the processing by strength analysis module  1174  and processor  1170 , grade assignment data  1182  is generated. 
     As seen in  FIG. 11 , in one embodiment, grade assignment data  1182  is provided to action selection and activation module  1190  which selects an appropriate action of the actions represented in available actions data  1192  based, at least in part on the grade indicated by grade assignment data  1182 . As seen in  FIG. 11 , in one embodiment, the determined appropriate action is represented by selected action data  1194 . 
     As seen in  FIG. 11 , in one embodiment, selected action data  1194  is forwarded to an action activation module such as selected action implementation module  1196  in production environment  1101  to initialize one or more actions with respect to the green wood product/veneer ribbon  1013  based, at least in part, on the grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013  by action selection and activation module  1190 . 
     In one embodiment, one or more actions that can be taken represented in available actions data  1192  include, but are not limited to: sorting the green wood product/veneer ribbon  1013  into a bin, location or stack associated with the grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013 ; restricting the use of the green wood product/veneer ribbon  1013  based on the grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013 ; rejecting the green wood product/veneer ribbon  1013  based on the grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013 ; sending the green wood product/veneer ribbon  1013  back for further processing based on the grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013 ; adjusting one or more processing parameters of a production line in production environment  1101  based, at least in part, on the grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013  and/or the grades assigned other wood products; adjusting various processing parameters on a production line in production environment  1101  based, at least in part, on grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013  and/or the grades assigned other wood products; and selecting a type and amounts of glues used on a production line in production environment  1101  based, at least in part, on grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013  and/or the grades assigned other wood products. 
     As noted, in one embodiment, the action taken by selected action implementation module  1196  includes sorting the green wood product/veneer ribbon  1013  into a bin, location or stack associated with the grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013 . 
     In one embodiment, sorting the green wood product/veneer ribbon  1013  into a bin, location or stack associated with the grade represented by grade assignment data  1182  and assigned to the green wood product/veneer ribbon  1013  is performed at automated stacking station  1040 . 
     In one embodiment, at automated stacking station  1040 , the individual veneer sheets  1043  stacked according to the grade assigned to the parent veneer ribbon section using any of the stacking systems described in related applications Bolton et al., U.S. application Ser. No. 16/697,458 filed on Nov. 27, 2019 and issuing Aug. 17, 2021 as U.S. Pat. No. 11,090,833; Bolton et al., U.S. application Ser. No. 17/356,804 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/356,805 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/361,808 filed on Jun. 29, 2021; and Bolton et al., U.S. application Ser. No. 17/366,432, filed Jul. 2, 2021, which are hereby incorporated by reference in its entirety as if they were fully set forth herein. 
       FIG. 12  is a flow chart of a process  1200  for determining the strength of a green wood product using NIR technology in accordance with one embodiment. 
     Referring to  FIGS. 10, 11 and 12 , as seen in  FIG. 12 , process  1200  begins at operation  1202  and then proceeds to operation  1203 . 
     In one embodiment, at operation  1203 , strength analysis models and/or mechanical properties model data are created. In one embodiment, data obtained from NIR images can be correlated with the strength properties of the green wood product using the strength analysis models and/or mechanical properties model data. 
     As discussed above, in various embodiments, different methods can be used to correlate the NIR data, i.e., NIR reflectance spectrum data, of a green wood product to a selected property of that green wood product to create the strength models and/or machine learning modules. 
     Consequently, using the disclosed NIR green strength analysis it is possible to collect high quality NIR spectra of wood products, including full size ribbons and/or sheets of green veneer that contain information and data regarding the mechanical properties of wood product, including strength of the wood product. 
     It has been found that these correlations apply to moving ribbons and/or sheets of veneer using a reduced spectral range if a reduced spectral range is processed. Consequently, as discussed above, in one embodiment, one or more sources of illumination positioned to illuminate at least one surface of a veneer sheet or other wood product are selected to provide a reduced spectral range between 650 and 1050 nm. This enables very rapid collection of the NIR spectra. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     As discussed above, in one embodiment, the one or more strength analysis models and mechanical properties model data predict the Metriguard number, and the actual MOE and MOR values of wood products, such as green or dry veneers and/or for one or more other wood products. 
     In one embodiment, once strength analysis models and/or mechanical properties model data are created at operation  1203 , process flow proceeds to operation  1204 . 
     In one embodiment, at operation  1204  one or more NIR green wood product strength analysis systems, including one or more NIR green wood product strength analysis stations, such as those discussed above are provided. 
     In one embodiment, once one or more NIR green wood product strength analysis systems are provided at operation  1204 , process flow proceeds to operation  1206 . 
     In one embodiment, at operation  1206 , the green veneer sheet, ribbon, or other wood product to be analyzed is positioned in, or passed through, an NIR green wood product strength analysis system, including an NIR green wood product strength analysis station, for analysis. 
     In one embodiment, at operation  1206 , the green veneer sheet, ribbon, or other wood product to be analyzed is positioned in, or passed through, an NIR green wood product strength analysis station such that a surface of the green veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. In one embodiment, the green veneer ribbon or sheet to be analyzed is passed from a log peeling/veneer creation station to the NIR green wood product strength analysis station. 
     As noted above, in one embodiment, the one or more illumination sources are selected to provide a reduced spectral range between 650 and 1050 nm is utilized to enable very rapid collection of the NIR data including NIR reflectance spectrum data. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, the NIR green wood product strength analysis station of operation  1206  include one or more NIR/SWIR cameras, hereafter referred to as simply NIR cameras, positioned to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. 
     In one embodiment, at operation  1206 , the one or more NIR cameras are then used to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product including NIR reflectance spectrum data. In one embodiment, a reduced spectral range, in one embodiment between 650 and 1050 nm, is processed to enable very rapid collection of the NIR data including NIR reflectance spectrum data. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, at operation  1206 , the NIR reflectance spectrum data is provided to a processor for comparing and analyzing the NIR reflectance spectrum data using the one or more strength models and/or machine learning modules of operation  1203 . 
     In one embodiment, at operation  1206 , secondary NIR green strength data processing is also performed for analysis of green wood products to compensate for the strong absorbance bands of water/moisture in the NIR region. 
     In one embodiment, once the green veneer sheet, ribbon, or other wood product to be analyzed is positioned in, or passed through, an NIR green wood product strength analysis station for analysis at operation  1206 , process flow proceeds to operation  1208 . 
     In one embodiment, at operation  1208  a grade is assigned to the green wood product based on the determined strength of the green wood product. 
     In one embodiment, once a grade is assigned to the green wood product based on the determined strength of the green wood product process flow proceeds to operation  1210 . 
     In one embodiment, at operation  1210 , one or more actions are taken with respect to the green wood product based, at least in part, on the grade assigned to the green wood product at operation  1208 . 
     In one embodiment, one or more actions that can be taken at operation  1210  include, but are not limited to: sorting the wood product/veneer ribbon into a bin, location or stack associated with the assigned grade; restricting the use of the wood product/veneer ribbon based on the grade assigned to the wood product/veneer ribbon; rejecting the wood product/veneer ribbon based on the grade assigned to the wood product/veneer ribbon; sending the wood product/veneer ribbon back for further processing based on the grade assigned to the wood product/veneer ribbon; adjusting one or more processing parameters of a production line based, at least in part, on the grade assigned to the wood product/veneer ribbon and/or the grades assigned other wood products; adjusting various processing parameters on a production line based, at least in part, on grade assigned to the wood product/veneer ribbon and/or the grades assigned other wood products; and selecting a type and amounts of glues used on a production line based, at least in part, on grade assigned to the wood product/veneer ribbon and/or the grades assigned other wood products. 
     As noted, in one embodiment, the action taken at  1210  can include sorting the wood product/veneer ribbon into a bin, location or stack associated with the grade assigned to the wood product/veneer ribbon. 
     In one embodiment, sorting the wood product/veneer ribbon into a bin, location or stack associated with the grade assigned to the wood product/veneer ribbon is performed at an automated stacking station. 
     In one embodiment, at the automated stacking station, the individual veneer sheets are stacked according to the grade assigned to the parent veneer ribbon section using any of the stacking systems described in related applications Bolton et al., U.S. application Ser. No. 16/697,458 filed on Nov. 27, 2019 and issuing Aug. 17, 2021 as U.S. Pat. No. 11,090,833; Bolton et al., U.S. application Ser. No. 17/356,804 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/356,805 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/361,808 filed on Jun. 29, 2021; and Bolton et al., U.S. application Ser. No. 17/366,432, filed Jul. 2, 2021, which are hereby incorporated by reference in its entirety as if it were fully set forth herein. 
     Consequently, some disclosed embodiments use NIR technology to predict the strength of a sheet of veneer from the NIR spectra of green veneer. This allows for the gradings and sorting of green veneer before drying and moisture analysis to provide enhanced grading technology and more accurate wood product grading. 
     Once one or more actions with respect to the wood product at operation  1220 , process flow proceeds to END operation  1234  where process  1200  is exited to await new samples and/or data. 
     As noted above, embodiments of the present disclosure also provide an effective and efficient technical solution to the technical problem of providing a method and system for determining the strength of a dry wood product that is reliable, consistent, and economically feasible to implement. 
       FIG. 13  is simplified block diagram of a NIR dry wood product strength analysis process  1300  for determining the strength of a dry wood product in accordance with one embodiment. 
     As seen in  FIG. 13 , in one embodiment, the wood product is dry veneer sheets, or another dry wood product,  1313 . In one embodiment, the dry wood product/dry veneer sheets  1313  are provided to NIR dry wood product strength analysis process  1300  from a dryer by conveyor  1390 . 
     In one embodiment, the resulting dry wood product/veneer sheets  1313  are then provided to an NIR moisture analysis station  1310  such as any of the NIR analysis stations discussed with respect to  FIG. 3A, 6 , or  9 . In one embodiment, the dry wood product/veneer sheets  1313  are analyzed at NIR moisture analysis station  1310  using any of the systems or methods described above with respect to  FIGS. 3A through 9 . 
     In one embodiment, the dry wood product/veneer sheets  1313  are then provided to NIR dry wood product strength analysis system  1320  by conveyor  1390 . 
     The dry wood product/veneer sheets  1313  are then analyzed by NIR dry wood product strength analysis system  1320  as discussed below. 
     In one embodiment, the dry wood product/veneer sheets  1313  are then provided to visual defect analysis station  1330  by conveyor  1390 . In one embodiment, visual defect analysis station  1330  is used detect visual defects in or on the surface of dry wood product/veneer sheets  1313 . In one embodiment, visual defect analysis station  1330  is any visual defect analysis system discussed herein, and/or as known in the art at the time of filing, and/or as developed after the time of filing, for detecting visual defects in or on the surface of a wood product. 
     In one embodiment, the visual defect analysis station  1330  can be any of the visual defect analysis systems set forth in related applications Bolton et al., U.S. application Ser. No. 16/205,027 filed on Nov. 29, 2018 and issuing on Nov. 3, 2020 as U.S. Pat. No. 10,825,164; Bolton et al., U.S. application Ser. No. 17/074,956 filed on Oct. 20, 2020 and issuing on Dec. 14, 2021 as U.S. Pat. No. 11,200,663; Bolton et al., U.S. application Ser. No. 17/084,397 filed on Oct. 29, 2020 and issuing on Jan. 11, 2022 as U.S. Pat. No. 11,222,419; and Bolton et al., U.S. application Ser. No. 17/523,528 filed on Nov. 19, 2021,_which are hereby incorporated by reference in their entirety as if they were fully set forth herein. 
     In one embodiment, based on the analysis of NIR moisture analysis station  1310 , and/or NIR dry wood product strength analysis system  1320  and/or visual defect analysis station  1330 , a grade is assigned to the dry wood product/veneer sheets  1313 . 
     In one embodiment, the individual dry wood product/veneer sheets  1313  are then stacked into veneer sheet stacks  1353  at automated stacking station  1340 . In one embodiment, at automated stacking station  1340  the individual veneer sheets  1343  stacked according to the grade assigned to the dry wood product/veneer sheets  1313 . 
     In one embodiment, at automated stacking station  1340  the individual dry wood product/veneer sheets  1313  are stacked according to the grade assigned to the dry wood product/veneer sheets  1313  using any of the stacking systems described in related applications Bolton et al., U.S. application Ser. No. 16/697,458 filed on Nov. 27, 2019 and issuing Aug. 17, 2021 as U.S. Pat. No. 11,090,833; Bolton et al., U.S. application Ser. No. 17/356,804 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/356,805 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/361,808 filed on Jun. 29, 2021; and Bolton et al., U.S. application Ser. No. 17/366,432, filed Jul. 2, 2021, which are hereby incorporated by reference in their entirety as if they were fully set forth herein. 
     In one embodiment, at automated stacking station  1340  the individual dry wood product/veneer sheets  1313  are stacked according to the grade assigned to the dry wood product/veneer sheets  1313  using any stacking system discussed herein, and/or as known in the art at the time of filing, and/or are become known after the time of filing. 
     Consequently, using the disclosed NIR dry strength analysis it is possible to collect high quality NIR spectra of wood products, including full size sheets of dry veneer that contain information and data regarding the mechanical properties of wood product, including strength of the wood product, after drying and/or moisture analysis is performed. 
       FIG. 14  is simplified block diagram of a NIR dry wood product strength analysis system  1320 , including NIR dry wood product strength analysis station  1421 , in accordance with one embodiment. 
     Referring now to  FIGS. 13 and 14 , in one embodiment, NIR dry wood product strength analysis system  1320  includes a production environment  1401  and a computing environment  1450 . 
     As seen in  FIG. 14 , production environment  1401  includes NIR dry wood product strength analysis station  1421  and selected action implementation module  1496 . As seen in  FIG. 14 , NIR dry wood product strength analysis station  1421  includes one or more illumination sources, such as illumination source  1422 , positioned to illuminate a surface  1414  of a dry wood product/veneer sheet  1313 , such as a dry sheet of veneer. 
     In various embodiments, the one or more illumination sources, such as illumination source  1422 , can include one or more LED light sources. In other embodiments, the one or more illumination sources, such as illumination source  1422 , can include, but are not limited to, halogen, halogen and tungsten light sources, or any other light sources, as discussed herein, and/or as known in the art at the time of filing, and/or as developed after the time of filing. 
     As used herein, the terms Near InfraRed (NIR) and Short-Wave InfraRed (SWIR) are used interchangeably to include wavelength in the range of 750 nanometers (nm) to 14500 nm. In addition, all stated wave lengths herein are assumed to include values within 13% of the stated value. 
     In one embodiment, the one or more illumination sources, such as illumination source  1422 , are selected to provide a reduced spectral range, in one embodiment between 650 and 1350 nm. This enables very rapid collection of the NIR spectra. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     As seen in  FIG. 14 , NIR dry wood product strength analysis station  1421  also includes one or more NIR cameras, such as NIR camera  1424 , positioned to capture NIR image data  1462  representing one or more NIR images of the illuminated surface  1414  of the dry wood product/veneer sheet  1313 . In one embodiment, the one or more NIR cameras, such as NIR camera  1424 , are adjustably positioned and adjustably focused to capture any desired one or more NIR images of the illuminated, or first, surface  1414  of the dry wood product/veneer sheet  1313 . 
     As seen in  FIG. 14 , and as discussed below, a dry wood product/veneer sheet  1313  to be analyzed in the NIR dry wood product strength analysis station  1421  is positioned in NIR dry wood product strength analysis station  1421 . In various embodiments, the dry wood product/veneer sheet  1313  can be any wood product as discussed herein, and/or as known in the art at the time of filing and/or as becomes known after the time of filing. In one embodiment, the dry wood product/veneer sheet  1313  to be analyzed are dry veneer sheets. 
     In one embodiment, the dry wood product/veneer sheet  1313  to be analyzed is positioned such that a dry wood product first surface  1414  of the dry wood product/veneer sheet  1313  to be analyzed is illuminated by the illumination source  1422  and the entire dry wood product first surface  1414  is within view and focus of NIR camera  1424 . In one embodiment, the dry wood product/veneer sheet  1313  is positioned in the NIR dry wood product strength analysis station  1421  by passing the dry wood product/veneer sheet  1313  through the NIR dry wood product strength analysis station  1421  on a conveyor system (not shown in  FIG. 14  but shown as  1310  in  FIG. 13  and discussed above). 
     In various embodiments, the one or more NIR cameras, such as NIR camera  1424 , can be of any resolution desired. As noted above, when the one or more NIR cameras, such as NIR camera  1424 , are used to scan the dry wood product first surface  1414  of a dry wood product/veneer sheet  1313  for strength and create NIR image data  1462  of the wood product first surface  1414 , essentially each pixel generated by NIR camera  1424  is a sample point. Consequently, the resolution and accuracy of the strength detection process is only limited by the number of pixels the NIR camera  1424  has covering the field of view, e.g., the entire wood product first surface  1414  of dry wood product/veneer sheet  1313 . Consequently, in the case where NIR camera  1424  is a 1.3 mega pixel camera, there are essentially 1,110,000 individual measurement points on the wood product first surface  1414 . Consequently, using NIR cameras, such as NIR camera  1424 , results in resolutions and accuracy that simply cannot be achieved using traditional detection systems. 
     In some embodiments, strength analysis models are created, and the data obtained from NIR images can be correlated with the strength properties of the dry wood product using these models. 
     As seen in  FIG. 14 , computing environment  1450  includes computing system  1452 . As seen in  FIG. 14 , in one embodiment, computing system  1452  includes strength model database  1410  containing one or more strength analysis models and mechanical properties model data  1412 . 
     In one embodiment, the one or more strength analysis models and mechanical properties model data  1412  predict the Metriguard number, and the actual MOE and MOR values of wood products, such as green or dry veneers and/or for one or more other wood products. 
     In various embodiments, different methods can be used to correlate the NIR data, i.e., NIR reflectance spectrum data, of a dry wood product to a selected property of that dry wood product to create the strength models and/or machine learning modules. 
     These correlations have been demonstrated empirically on various different commercial softwoods and hardwoods. These correlations have also been demonstrated on dry wood. It has been found that these same correlations also apply to moving 4 ft. by 8 ft. sheet of dry veneer using a reduced spectral range. 
     In some embodiment, the NIR spectra of dry veneers can be evaluated off-line using two different NIR spectrometers. 
     As discussed above, there are a number of methods that can be used to correlate the NIR reflectance spectrum data of a wood sample to some property of that wood sample. One common method is Projection of Latent Structures (PLS) analysis. In some cases, the NIR reflectance spectrum data of the sample are correlated with a response variable, e.g., some measure of the mechanical properties of the wood sample. Since it is not practical to measure the mechanical properties of a full size sheet of veneer, the response variable used for this work was the Metriguard number of the veneer sheet. 
     The Metriguard numbers on the full sized sheets of veneer can be measured using the commercial systems. There are several different ways to generate these PLS correlations and to measure the “quality” of the correlation model. All of these PLS models can be constructed using full cross validation techniques. There are also several different “data pretreatments” that can be applied to the NIR reflectance spectrum data prior to constructing a PLS model. 
     In one instance, for the NIR reflectance spectrum data measured on green veneers a common data pretreatment known as Orthogonal Signal Correction (OSC) was used to mathematically “dry” the green samples prior to construction of the PLS models. The procedure for construction of the PLS models involves using about half of the samples to construct a calibration (CALM) model that correlates the measured or “true” Metriguard number with the NIR reflectance spectrum data. This model is then used to predict the Metriguard number from the NIR reflectance spectrum data of a second of samples that were not contained in the original model. These predicted Metriguard numbers are then compared to the measured Metriguard numbers of this second set of samples. 
     Those of skill in the art will also readily recognize that these models can be supplemented and/or replaced with various machine learning and artificial intelligence methods and modules, or any other methods and systems for correlating data, such as the NIR reflectance spectrum data, of a green wood product to a selected property of that green wood product. 
     Empirical results show a correlation coefficient (r) between the measured Metriguard number and the Metriguard number predicted with NIR analysis are relatively good for a heterogeneous substrate like wood, 0.83 and 0.69 respectively. The spectral range was between 650 and 1050 nm which is the range required for rapid acquisition times. 
     There are several general conclusions that can be drawn from these empirical results. The first general conclusion is that the PLS models constructed using the reduced spectral range of 650-1050 nm are as good as or better than those constructed using the full spectral range. This is critically important since the use of this reduced spectral range is required for the rapid acquisition times that will be needed for on-line process monitoring. 
     The second general conclusion is that the correlations based on NIR spectra collected from dry veneers is higher than those based on green veneers. 
     A third general conclusion is that that OSC of the NIR data before construction of the PLS models significantly improves the quality of the correlations. There are many different ways to actually construct the PLS models from OSC data and the preferred method will be impacted by the conditions used to collected the NIR spectra. 
     It is may be impractical to measure the actual strength MOR or stiffness MOE of a full size sheet of veneer. To better understand the correlations between these two measures of veneer quality a series of 2 ft. by 2 ft. Douglas Fir veneer samples were cut from full size sheets and sent to NREL. These samples were further cut into samples 6 inches wide and 2 ft. long. 
     A portable Metriguard system was used to obtain a Metriguard number for these small samples. The true MOR and MOE were measured in three point bending. 
     Based on the empirical results of this work it is possible to collect high quality NIR reflectance spectrum data of full size sheets of veneers. It is also clear that the NIR reflectance spectrum data contains information on the mechanical properties of veneer. It is also clear that the NIR spectra of either green or dry veneer can be used to construct models that predict the Metriguard number, and the actual MOE and MOR values of veneers. Models based on the reduced spectral range of 650-1050 nm are as good as or better than those constructed using the full spectral range. Empirical results also indicate that the Metriguard number is poorly correlated with the actual mechanical properties of veneers. 
     Consequently, using the disclosed NIR green strength analysis it is possible to collect high quality NIR reflectance spectrum data of wood products, including full size ribbons and/or sheets of green veneer that contain information and data regarding the mechanical properties of wood product, including strength of the wood product. 
     As seen in  FIG. 14 , computing system  1452  also includes physical memory  1460 . In one embodiment, the physical memory  1460  includes NIR image data  1462  representing one or more NIR images of the illuminated wood product first surface  1414  of the dry wood product/veneer sheet  1313  captured using NIR camera  1424 . 
     As seen in  FIG. 14 , in one embodiment, computing system  1452  includes one or more processors  1470  for processing the NIR image data  1462  representing one or more NIR images of the illuminated wood product first surface  1414  of the dry wood product/veneer sheet  1313  using the one or more strength analysis models and mechanical properties model data  1412  of strength model database  1410 . 
     As noted above, in one embodiment, the one or more strength analysis models and mechanical properties model data  1412  predict the Metriguard number, and the actual MOE and MOR values of wood products, such as dry or dry veneers and/or for one or more other wood products. 
     In one embodiment, processor  1470  processes the NIR image data  1462  using the using the mechanical properties data  1412  of strength model database  1410  to determine/predict various mechanical properties of the dry wood product/veneer sheet  1313  and therefore the strength of the dry wood product/veneer sheet  1313 . 
     As seen in  FIG. 14 , in one embodiment, computing system  1452  includes a grade assignment module  1480  for assigning a grade to the dry wood product/veneer sheet  1313  based on determined/predicted mechanical properties of the dry wood product/veneer sheet  1313 . 
     As seen in  FIG. 14 , grade assignment module  1480  includes strength analysis module  1474  which, along with processor  1470 , processes the NIR image data  1462  using the using the mechanical properties data  1412  of strength model database  1410  to determine/predict various mechanical properties of the dry wood product/veneer sheet  1313  and therefore the strength of the dry wood product/veneer sheet  1313 . As a result of the processing by strength analysis module  1474  and processor  1470 , grade assignment data  1482  is generated. 
     As seen in  FIG. 14 , in one embodiment, grade assignment data  1482  is provided to action selection and activation module  1490  which selects an appropriate action of the actions represented in available actions data  1492  based, at least in part on the grade indicated by grade assignment data  1482 . As seen in  FIG. 14 , in one embodiment, the determined appropriate action is represented by selected action data  1494 . 
     As seen in  FIG. 14 , in one embodiment, selected action data  1494  is forwarded to an action activation module such as selected action implementation module  1496  in production environment  1401  to initialize one or more actions with respect to the dry wood product/veneer sheet  1313  based, at least in part, on the grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313  by action selection and activation module  1490 . 
     In one embodiment, one or more actions that can be taken represented in available actions data  1492  include, but are not limited to: sorting the dry wood product/veneer sheet  1313  into a bin, location or stack associated with the grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313 ; restricting the use of the dry wood product/veneer sheet  1313  based on the grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313 ; rejecting the dry wood product/veneer sheet  1313  based on the grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313 ; sending the dry wood product/veneer sheet  1313  back for further processing based on the grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313 ; adjusting one or more processing parameters of a production line in production environment  1401  based, at least in part, on the grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313  and/or the grades assigned other wood products; adjusting various processing parameters on a production line in production environment  1401  based, at least in part, on grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313  and/or the grades assigned other wood products; and selecting a type and amounts of glues used on a production line in production environment  1401  based, at least in part, on grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313  and/or the grades assigned other wood products. 
     As noted, in one embodiment, the action taken by selected action implementation module  1496  includes sorting the dry wood product/veneer sheet  1313  into a bin, location or stack associated with the grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313 . 
     In one embodiment, sorting the dry wood product/veneer sheet  1313  into a bin, location or stack associated with the grade represented by grade assignment data  1482  and assigned to the dry wood product/veneer sheet  1313  is performed at automated stacking station  1340 . 
     In one embodiment, at automated stacking station  1340 , the individual veneer sheets  1343  stacked according to the grade assigned to dry wood product/veneer sheet  1313  using any of the stacking systems described in related applications Bolton et al., U.S. application Ser. No. 16/697,458 filed on Nov. 27, 2019 and issuing Aug. 17, 2021 as U.S. Pat. No. 11,090,833; Bolton et al., U.S. application Ser. No. 17/356,804 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/356,805 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/361,808 filed on Jun. 29, 2021; and Bolton et al., U.S. application Ser. No. 17/366,432, filed Jul. 2, 2021, which are hereby incorporated by reference in its entirety as if it were fully set forth herein. 
       FIG. 15  is a flow chart of a process for determining the strength of a dry wood product using NIR technology in accordance with one embodiment. 
     Referring to  FIGS. 13, 14 and 15 , as seen in  FIG. 15 , process  1500  begins at operation  1502  and then process proceeds to operation  1503 . 
     In one embodiment, at operation  1503 , strength analysis models and/or mechanical properties model data are created. In one embodiment, data obtained from NIR images can be correlated with the strength properties of the dry wood product using the strength analysis models and/or mechanical properties model data. 
     In various embodiments, different methods can be used to correlate the NIR data, i.e., NIR reflectance spectrum data, of a dry wood product to a selected property of that dry wood product to create the strength models and/or machine learning modules. 
     Consequently, using the disclosed NIR dry strength analysis it is possible to collect high quality NIR spectra of wood products, including full size sheets of dry veneer that contain information and data regarding the mechanical properties of wood product, including strength of the wood product. 
     It has been found that these correlations apply to moving ribbons and/or sheets of veneer using a reduced spectral range if a reduced spectral range is processed. Consequently, as discussed below, in one embodiment, one or more sources of illumination positioned to illuminate at least one surface of a veneer sheet or other wood product are selected to provide a reduced spectral range, in one embodiment between 650 and 1350 nm. This enables very rapid collection of the NIR spectra. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     As discussed above, in one embodiment, the one or more strength analysis models and mechanical properties model data predict the Metriguard number, and the actual MOE and MOR values of wood products, such as dry or dry veneers and/or for one or more other wood products. 
     In one embodiment, once strength analysis models and/or mechanical properties model data are created at operation  1503 , process flow proceeds to operation  1504 . 
     In one embodiment, at operation  1504  one or more NIR dry wood product strength analysis systems, including one or more NIR dry wood product strength analysis stations, such as any of the NIR dry wood product strength analysis systems, including one or more NIR dry wood product strength analysis stations, discussed above herein are provided. 
     In one embodiment, once one or more NIR dry wood product strength analysis systems are provided at operation  1504 , process flow proceeds to operation  1506 . 
     In one embodiment, at operation  1506 , the dry veneer sheet or other wood product to be analyzed is positioned in, or passed through, an NIR dry wood product strength analysis system, including an NIR dry wood product strength analysis station for analysis. 
     In one embodiment, at operation  1506 , the dry veneer sheet, or other wood product, to be analyzed is positioned in, or passed through, an NIR dry wood product strength analysis station such that a surface of the dry veneer sheet or other wood product to be analyzed is illuminated by the one or more illumination sources. In one embodiment, the dry veneer sheet to be analyzed is passed from a moisture detection system to the NIR dry wood product strength analysis station. 
     As noted above, in one embodiment, the one or more illumination sources are selected to provide a reduced spectral range, in one embodiment between 650 and 1350 nm, are utilized to enable very rapid collection of the NIR data including NIR reflectance spectrum data. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, the NIR dry wood product strength analysis stations of operation  1506  include one or more NIR/SWIR cameras, hereafter referred to as simply NIR cameras, positioned to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product. 
     In one embodiment, at operation  1506 , the one or more NIR cameras are then used to capture one or more NIR images of the illuminated surface of the veneer sheet or other wood product including NIR reflectance spectrum data. In one embodiment, a reduced spectral range, in one embodiment between 650 and 1350 nm, is processed to enable very rapid collection of the NIR data including NIR reflectance spectrum data. This rapid collection is required for the evaluation of veneer in the manufacturing process. 
     In one embodiment, at operation  1506 , the NIR reflectance spectrum data is provided to a processor for comparing and analyzing the NIR reflectance spectrum data using the one or more strength models and/or machine learning modules of operation  1503 . 
     In one embodiment, at operation  1506 , secondary NIR dry strength data processing is also performed for analysis of dry wood products to compensate for the strong absorbance bands of water/moisture in the NIR region. 
     In one embodiment, once the dry veneer sheet, or other wood product, to be analyzed is positioned in, or passed through, an NIR dry wood product strength analysis station for analysis at operation  1506 , process flow proceeds to operation  1508 . 
     In one embodiment, at operation  1508  a grade is assigned to the dry wood product based on the determined strength of the dry wood product. 
     In one embodiment, once a grade is assigned to the dry wood product based on the determined strength of the dry wood product process flow proceeds to operation  1510 . 
     In one embodiment, at operation  1510 , one or more actions are taken with respect to the dry wood product based, at least in part, on the grade assigned to the dry wood product at operation  1508 . 
     In one embodiment, one or more actions that can be taken at operation  1510  include, but are not limited to: sorting the dry wood product/veneer sheet into a bin, location or stack associated with the assigned grade; restricting the use of the dry wood product/veneer sheet based on the grade assigned to the dry wood product/veneer sheet; rejecting the dry wood product/veneer sheet based on the grade assigned to the dry wood product/veneer sheet; sending the dry wood product/veneer sheet back for further processing based on the grade assigned to the dry wood product/veneer sheet; adjusting one or more processing parameters of a production line based, at least in part, on the grade assigned to the dry wood product/veneer sheet and/or the grades assigned other wood products; adjusting various processing parameters on a production line based, at least in part, on grade assigned to the dry wood product/veneer sheet and/or the grades assigned other wood products; and selecting a type and amounts of glues used on a production line based, at least in part, on grade assigned to the dry wood product/veneer sheet and/or the grades assigned other wood products. 
     As noted, in one embodiment, the action taken at  1510  can include sorting the dry wood product/veneer sheet into a bin, location or stack associated with the grade assigned to the dry wood product/veneer sheet. 
     In one embodiment, sorting the dry wood product/veneer sheet into a bin, location or stack associated with the grade assigned to the dry wood product/veneer sheet is performed at an automated stacking station. 
     In one embodiment, at the automated stacking station, the individual veneer sheets are stacked according to the grade assigned to the veneer sheet using any of the stacking systems described in related applications Bolton et al., U.S. application Ser. No. 16/697,458 filed on Nov. 27, 2019 and issuing Aug. 17, 2021 as U.S. Pat. No. 11,090,833; Bolton et al., U.S. application Ser. No. 17/356,804 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/356,805 filed on Jun. 24, 2021; Bolton et al., U.S. application Ser. No. 17/361,808 filed on Jun. 29, 2021; and Bolton et al., U.S. application Ser. No. 17/366,432, filed Jul. 2, 2021, which are hereby incorporated by reference in their entirety as if it were fully set forth herein. 
     Consequently, some disclosed embodiments use NIR technology to predict the strength of a sheet of veneer from the NIR spectra of dry veneer. This allows for the gradings and sorting of dry veneer after drying and moisture analysis to provide enhanced grading technology and more accurate wood product grading. 
     Once one or more actions with respect to the wood product at operation  1520 , process flow proceeds to END operation  1534  where process  1500  is exited to await new samples and/or data. 
     As shown above, the disclosed embodiments utilize NIR cameras to scan the surface of a wood product for moisture and create an NIR image of the surface of the wood product. Since essentially each pixel of camera image data is a sample point, the resolution and accuracy of the moisture detection process is the number of pixels the camera has covering the field of view, e.g., the entire first surface of a wood product. Consequently, in the case where a 1.3 mega pixel camera is there are essential 1,300,000 individual measurement points on the surface of the wood product. Consequently, using NIR cameras, as disclosed herein, results in resolutions and accuracy that simply cannot be achieved using traditional moisture detection systems such as traditional contact electrode systems or RF moisture detection systems. 
     As noted, using traditional moisture detection systems such as traditional contact electrode systems or RF moisture detection systems accuracy levels are at best subject to the ±5% or the ±7.5% margin of error, respectively. This resulted in the need to be very conservative when determining the potential use of a given veneer sheet or other wood product and often resulted in wood products, such as veneer sheets, not being put to their most cost effective and efficient use simply to ensure that the ±5% or the ±7.5% margin of error did not result in inferior or unsafe wood products. 
     In contrast, using the disclosed NIR-based systems, accuracy on the order of ±0.1% is readily achieved. Therefore, the highest value use of a given veneer sheet or other wood product can be accurately determined and the wood products, such as veneer sheets, can be confidently put to their most cost effective and efficient use. 
     In addition, when, as disclosed herein, NIR cameras are used as the moisture detection mechanism, when greater or less resolution is deemed necessary, a higher or lower mega-pixel camera can be selected to achieve the desired resolution for the process. In addition, unlike tradition contact electrode and RF moisture detection systems, NIR camera placement with respect to the sample under analysis can be adjusted such that a quality image can be obtained as long as there is a clear field of view between the wood product surface and NIR camera. Horizontal, vertical, or angled placements have no impact on the functionality of the NIR camera. Further, combinations of NIR cameras and lenses can provide opportunities to perform measurements that are currently prohibitive due to the need for a conveyor section to convey the material through a sensing array of contact electrodes or RF instruments. 
     The use of NIR cameras, are disclosed herein, eliminates the need for any physical contact with the wood product by any part of the moisture detection device, or even the need for the moisture detection device, i.e., the NIR camera, to be close to the wood product surface. Not only does this fact eliminate wear and tear on both the sample taking device and the wood product, but as discussed above it allows for more flexible placement of the sample taking device, i.e., the NIR camera. 
     In addition, unlike RF moisture detection devices and contact electrodes, NIR cameras are virtually immune to static electricity or spurious RF emissions. Consequently, use of NIR cameras as disclosed herein is far more suitable for a physical production line environment. 
     In addition, unlike traditional contact electrode systems that require high voltages and represent a danger to workers, NIR technology has been deemed to represent no hazards to workers or other devices by several testing and safety agencies. Consequently, the use of the disclosed NIR based moisture detection systems results in a safer and more comfortable and efficient workplace and production floor. 
     In addition, using the disclosed NIR strength analysis systems, the antiquated and extremely inefficient and ineffective currently used prior art methods and systems for determining the density, and therefore the strength, of wood products, including veneer sheets, and various other materials is not requited. 
     For example, using the disclosed NIR strength analysis systems the use of prior art contact electrode systems and ultrasonic density detection systems similar to the RF detection systems used for moisture detection discussed above is no longer needed. Therefore, the shortcomings inefficiencies, and inaccuracies of prior art ultrasonic density detection systems discussed above are avoided. 
     Consequently, in contrast to prior art ultrasonic density detection systems, the disclosed NIR strength analysis systems are quite capable of determining wood product strength within the margins of error now required in many industries. In addition, in contrast to prior art ultrasonic density detection systems, the disclosed NIR strength analysis systems have relatively few moving parts and components so they are less subject to failure, lighter, require significantly less maintenance, than the antiquated, largely ineffective, and inefficient prior art ultrasonic density detection systems. 
     The present invention has been described in particular detail with respect to specific possible embodiments. Those of skill in the art will appreciate that the invention may be practiced in other embodiments. For example, the nomenclature used for components, capitalization of component designations and terms, the attributes, data structures, or any other programming or structural aspect is not significant, mandatory, or limiting, and the mechanisms that implement the invention or its features can have various different names, formats, or protocols. Further, the system or functionality of the invention may be implemented via various combinations of software and hardware, as described, or entirely in hardware elements. Also, particular divisions of functionality between the various components described herein are merely exemplary, and not mandatory or significant. Consequently, functions performed by a single component may, in other embodiments, be performed by multiple components, and functions performed by multiple components may, in other embodiments, be performed by a single component. 
     Some portions of the above description present the features of the present invention in terms of algorithms and symbolic representations of operations, or algorithm-like representations, of operations on information/data. These algorithmic or algorithm-like descriptions and representations are the means used by those of skill in the art to most effectively and efficiently convey the substance of their work to others of skill in the art. These operations, while described functionally or logically, are understood to be implemented by computer programs or computing systems. Furthermore, it has also proven convenient at times to refer to these arrangements of operations as steps or modules or by functional names, without loss of generality. 
     In addition, the operations shown in the figures, or as discussed herein, are identified using a particular nomenclature for ease of description and understanding, but other nomenclature is often used in the art to identify equivalent operations. 
     Therefore, numerous variations, whether explicitly provided for by the specification or implied by the specification or not, may be implemented by one of skill in the art in view of this disclosure.