Patent Publication Number: US-4544936-A

Title: Heat-sensitive recording sheet

Description:
FIELD OF THE INVENTION 
     The present invention relates to a heat-sensitive recording sheet and, in particular, to an improvement of heat-sensitive recording sheets comprising a heat-sensitive layer on a base where the heat-sensitive layer which contains, as main components, a color former and a developer which colors the color former upon heating of the recording sheet. 
     BACKGROUND OF THE INVENTION 
     Heat-sensitive recording sheets are used, for example, in facsimile receivers and printers. Such sheets contain, as main components, a heat-sensitive layer containing a color former and a developer. The heat-sensitive recording sheet is imagewise heated by, for example, a heat generation element such as a thermal head to carry out image recording by a thermal color forming reaction of the color former and the developer. 
     Hitherto, heat-sensitive recording sheeets have been prepared by applying an aqueous dispersion of a mixture of a colorless or light colored color former such as Crystal Violet lactone, etc. and a developer such as a phenolic compound, etc. to a paper or plastic film as the base and drying the applied dispersion to form a heat-sensitive layer. Further, the recording layer often contains various additives such as wax particles, wax emulsions, fatty acid metal salts, fatty acid amides, etc. for the purpose of improving color forming characteristics, pressure-sensitive color forming properties, lubrication properties, etc. or contains white pigments such as clay, talc, titanium oxide, etc. for the purpose of improving whiteness or writability of the surface of recording layer. Such heat-sensitive recording sheets are described in, for example, U.S. Pat. No. 4,265,978. 
     The foregoing heat-sensitive recording sheets form a color image on the heated part when imagewise heated by a heating element. However, the color image discolors or fades with heat or humidity. Moreover, the image fades after several days even at a room temperature, if touched 2 or 3 times by the fingers. Consequently, it becomes impossible to read the letters. Various attempts for preventing the fading phenomenon have been tried, as described in U.S. Pat. No. 4,255,491. For example, heat-sensitive recording sheets comprising 3-diethylamino-6-methyl-7-anilinofluoran or 3-pyrrolidino-6-methyl-7-anilinofluoran as the color former are known to minimize stains caused by heat or humidity. However, such heat-sensitive recording sheets have other faults in that they have low whiteness and the background thereof is easily fogged. 
     OBJECTS OF THE INVENTION 
     An object of the present invention is to provide a heat-sensitive recording sheet which overcomes the above described prior art faults. Another object of the present invention is to provide a heat-sensitive recording sheet, the color image of which fades less under the influence of heat or humidity and which has high whiteness and less fogging of the background. 
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS OF THE IVENTION 
     The objects of the present invention can be attained by using a mixture of at least one compound (A) selected from compounds represented by the following formulas (I) or (II) and at least one compound (B) selected from compounds represented by the following formulas (III) or (IV) as a color former used in the heat-sensitive recording layer. ##STR1## (wherein R 1  represents a hydrogen atom, a methyl group, an ethyl group, a halogenated methyl group, a halogenated ethyl group, an alkoxyalkyl group preferably having 2 to 12 carbon atoms (e.g., --C 2  H 5  OCH 3 ), an acyloxyalkyl group preferably having 3 to 13 carbon atoms (e.g., --CH 3  OCOCH 3 ), an allyl group, a propargyl group, a cyclohexyl group, an acetoxy group, a benzyl group which may be substituted by a lower alkyl group preferably having 1 to 6 carbon atoms, a lower alkoxy group preferably having 1 to 6 carbon atoms, a halogen atom or a nitro group, or a phenyl group which may be substituted by a lower alkyl group preferably having 1 to 6 carbon atoms, a lower alkoxy group preferably having 1 to 6 carbon atoms, a halogen atom or a nitro group, and R 3  represents a hydrogen atom, a lower alkyl group preferably having 1 to 6 carbon atoms (e.g., --C 3  H 7 ), an alkoxy group preferably having 1 to 12 carbon atoms (e.g., --OC 2  H 5 ), an aryl group, a halogen atom, a halogenated lower alkyl group preferably having 1 to 6 carbon atoms (e.g., --C 3  H 6  Cl) or an acetoxy group), ##STR2## (wherein R 3  is as defined above, R 5  represents a pyrrolidino group or a piperidino group, and R 6  represents a hydrogen atom, a lower alkyl group preferably having 1 to 6 carbon atoms (e.g., --C 3  H 7 ), an alkoxy group preferably having 1 to 12 carbon atoms (e.g., --OC 2  H 5 ) or a halogen atoms), ##STR3## (wherein R 3  is as defined above, R 2  represents a hydrogen atom, a lower alkyl group preferably having 1 to 6 carbon atoms (e.g., --C 3  H 7 ), a haloalkyl group preferably having 1 to 12 carbon atoms (e.g., --C 6  H 10  I), an alkoxyalkyl group preferably having 2 to 12 carbon atoms (e.g., --C 2  H 5  OCH 3 ), an acyloxyalkyl group preferably having 3 to 13 carbon atoms (e.g., --CH 3  OCOCH 3 ), an alkoxy group preferably having 1 to 12 carbon atoms (e.g., --OC 2  H 5 ), an allyl group, a propargyl group, a cyclohexyl group, a benzyl group which may be substituted by a lower alkyl group preferably having 1 to 6 carbon atoms, a lower alkoxy group preferably having 1 to 6 carbon atoms, a halogen atom or a nitro group, or a phenyl group which may be substituted by a lower alkyl group preferably having 1 to 6 carbon atoms, a lower alkoxy group preferably having 1 to 6 carbon atoms, a halogen atom or a nitro group, and R 7  represents a lower alkyl group preferably having 1 to 6 carbon atoms (e.g., --C 3  H 7 ), an alkoxy group preferably having 1 to 12 carbon atoms (e.g., --OC 2  H 5 ) or a halogen atom), and ##STR4## (wherein R 3  is as defined above, and R 8  represents an alkyl group having 3 or more carbon atoms, preferably not more than 12 carbon atoms (e.g., --C 10  H 21 ), or a halogenated alkyl group having 3 or more carbon atoms, preferably not more than 12 carbon atoms (e.g., --C 3  H 6  Cl). 
     These compounds are generally called fluoran dyes. In the present invention, at least two kinds of fluoran dyes selected from different groups are used as the color former. 
     Further, a mixture of three kinds of fluoran dyes may be used as the color former by mixing a fluoran dye compound (C) represented by the following formula (V) with the above described two kinds of fluoran dye compounds (A) and (B). ##STR5## (wherein R 2  and R 3  are as defined above and R 4  represents a substituent selected from the the same group as described above for R 2 , but is a substituent different than the R 2  substituent in the formula (V)). 
     Examples of fluoran dyes represented by the formulas (I)-(V) include the following: ##STR6## 
     When at least two kinds of compounds consisting of the compound (A) selected from the first group consisting of compounds represented by the formulas (I) and (II) and the compound (B) selected from the second group consisting of compounds represented by the formulas (III) and (IV) are used as the color formers, they are preferably used as a mixture in amounts of 1 to 50% by weight, preferably 20 to 40% by weight, of the compound (A) and 50 to 99% by weight, preferably 60 to 80% by weight, of the compound (B) based on the total amount of the color formers. 
     Further, when at least one kind of compound (C) represented by the formula (V) is used together with the compound (A) and the compound (B), they are preferably used as a mixture in amounts of 30 to 90% by weight, preferably 35 to 65% by weight, of the compound (A), 2.5 to 30% by weight, preferably 10 to 25% by weight, of the compound (B) and 2.5 to 40% by weight, preferably 25 to 40% by weight, of the compound (C) based on the total amount of the color former by weight. 
     The developer used in the present invention is an acid substance which causes coloration of the above described fluoran dyes when heated. As such acid substances, there are phenolic compounds and colorless solid organic acids which liquefy or volatilize at 50° C. or more, such as stearic acid, benzoic acid, gallic acid, salicyclic acid, etc. or metal salts thereof, such as aluminium salts, zinc salts, etc. The acid substances capable of preferably being used include the above described phenolic compounds and benzoic acid esters. Typical examples of the phenolic compounds include 4,4&#39;-isoproylidenediphenol (bisphenol A), 4,4&#39;-isopropylidene-bis(2-chlorophenol), 4,4&#39;-isopropylidene-bis(2-tert-butylphenol), 4,4&#39;-sec-butylidenediphenol, 4,4&#39;-cyclohexylidenediphenol, 4,4&#39;-isopropylidene-bis(2,6-dibromophenol), 4,4&#39;-isopropylidene-bis(2,6-dichlorophenol), 4,4&#39;-isopropylidenebis(2-methylphenol), 4,4&#39;-isopropylidene-bis(2,6-dimethylphenol), 4,4&#39;-sec-butylidene-bis(2-methylphenol), 4,4&#39;-cyclohexylidene-bis(2-methylphenol), 4,4&#39;-methylene-bis(2,6-di-tert-butylphenol), 4,4&#39;-butylidene-bis(4-methyl-6-tert-butylphenol) and 4,4&#39;-thiobis(4-methyl-6-tert-butylphenol). Examples of the benzoic acid esters include esters of 4-hydroxybenzoic acid or 3-chloro-4-hydroxybenzoic acid such as benzyl, p-chlorobenzyl, ethyl, propyl, isopropyl, butyl, isobutyl, methylbenzyl ester, and phthalic acid monoanilido 4-ethoxybenzoic acid. Further, the phenolic compounds and the benzoic acid esters may be used together. 
     Further, additives may be added to the heat-sensitive color forming layer in order to improve various properties. As additives for further improving fading or fogging of the background during storage, there are rosin-modified phenol resins and/or terephthalic acid ester compounds. The rosin-modified phenol resins are commercially available under Tamanol 135, 135F, 145, 340, 350, 351, 352, 353, 354 and 361 produced by Arakawa Rinsan Co. Examples of the terephthalic acid esters include dimethyl terephthalate, diethyl terephthalate, monoethyl terephthalate, diisopropyl terephthalate, monopropyl terephthalate, dibutyl terephthalate, monobutyl terephthalate, di-tert-butyl terephthalate, monooctyl terephthalate, bis-(3,5,5-trimethylhexyl)terephthalate, dimethyl 2-methoxyterephthalate, dimethyl 2-methylterephthalate, dimethyl 2-chloroterephthalate, dimethyl 2,5-dichloroterephthalate, diethyl 2-chloro-5-bromoterephthalate, dimethyl tetrachloroterephthalate, diphenyl terephthalate, etc. 
     These additives are preferably added as a mixture of at least two components consisting of at least one kind of a rosin-modified phenol resin and at least one kind of a terephthalic acid ester compound. 
     Further, in order to prevent adhesion of dregs to the facsimile head, inorganic or organic pigments, binders and other additives such as surface active agents, waxes, etc. may be used. As these additives, known additives may be used. Examples of the pigments include aluminium hydroxide, heavy and light calcium carbonate, zinc oxide, titanium oxide, barium sulfate, silica gel, activated clay, talc, clay, titanium white, kaolinite, calcined kaolinite, diatom earth, synthetic kaolinite, polyolefin particles, polystyrene particles, ureaformaldehyde resin particles, etc. 
     Examples of the binders may include casein, styrene-maleic acid anhydride resin, polyvinyl alcohol, modified polyvinyl alcohol, starch, modified starch, isobutylene-maleic acid anhydride resin, diisobutylenemaleic acid anhydride resin, polyacrylamide, modified polyacrylamide, carboxymethyl cellulose, methyl vinyl ether-maleic acid copolymer, hydroxyethyl cellulose, hydroxypropyl cellulose, carboxyl modified polyethylene, methyl cellulose, gum arabic, gelatin, polyvinylpyrrolidone, polyacrylic acid salt, terpene resin, petroleum resin, etc. A binder capable of particularly suitable use in the present invention is a water soluble binder, a typical example of which may be polyvinyl alcohol. 
     As the surface active agents, nonionic and anionic types may be used. Ampholytic agents and cationic agents are not generally used, because some of them cause aggregation of the coating solution. 
     Further, as the waxes, it is possible to use stearic acid amide, palmitic acid amide, oleic acid amide, lauric acid amide, ethylenebisstearoamide, methylenebisstearoamide, methylol stearoamide, paraffin wax, higher alcohols and higher resin acids. 
     In addition, it is possible to add fatty acid metal salts such as calcium stearate as a lubricant. 
     These materials used for the heat-sensitive color forming layer are applied as a mixed aqueous dispersion to a base such as paper, plastic film, etc. The mixed dispersion may be prepared using 15 to 25% by weight of the color former, 25 to 35% by weight of the developer, 15 to 20% by weight of the binder and 10 to 20% by weight of the pigment, based on the total weight of the components for the color forming layer (solid basis). When the rosin-modified phenol resins and/or the terephthalic acid esters are used for improving fading or fogging as described above, they may be added in an amount of 1 to 10% by weight. Further, the surface active agents, the waxes and the fatty acid metal salts may be added in the total amount of 5 to 15% by weight. 
     This mixed aqueous dispersion is applied to a base by a known process such as an air knife coating process, a bar coating process, a roll coating process, a kiss coating process, etc., and dried to obtain the heat-sensitive recording sheet of the present invention. The coating is carried out so that the dry weight may be 3 to 12 g/m 2 , preferably 5 to 8 g/m 2 . 
     This heat-sensitive recording sheet is imagewise heated by a heating element such as a thermal head to cause color formation, by which image recording can be carried out. 
     The recording sheet having a heat-sensitive recording layer containing the color former of the present invention and the developer which causes coloration of the color former by heating has such characteristics that fading of the color image due to temperature or humidity is remarkably reduced. Moreover, the whiteness is high and the fogging of the texture or background is small. Further, the recording sheet has high stability to barely cause a change of whiteness of the texture even when the sheet is stored for a long time. Further, the image does not fade even if animal or vegetable oils, cosmetics or oils from the fingers adhere to the image on the recording sheet. 
     In the following, the heat-sensitive recording sheet of the present invention is illustrated with reference to examples and comparative examples, but the present invention is not limited to these examples. 
    
    
     EXAMPLES 
     The following dispersions A-I were prepared as base dispersions of heat-sensitive coatings. 
     Dispersion A: 
     3-Diethylamino-6-methyl-7-anilinofluoran: 150 g 
     5% aqueous solution of PVA (polyvinyl alcohol): 150 g 
     Water: 450 g 
     The mixture was blended and dispersed by a ball mill for 48 hours. 
     Dispersion B: 
     3-N-Methylcyclohexylamino-6-methyl-7-anilinofluoran: 150 g 
     5% aqueous solution of PVA: 150 g 
     Water: 450 g 
     The mixture was blended and dispersed by a ball mill for 48 hours. 
     Dispersion C: 
     3-Pyrrolizino-6-methyl-7-anilinofluoran: 150 g 
     5% aqueous solution of PVA: 150 g 
     Water: 450 g 
     The mixture was blended and dispersed by a ball mill for 48 hours. 
     Dispersion D: 
     3-Diethylamino-7-o-chloroanilinofluoran: 150 g 
     5% aqueous solution of PVA: 150 g 
     Water: 450 g 
     The mixture was blended and dispersed by a ball mill for 48 hours. 
     Dispersion E: 
     3-Di-n-butylamino-6-methyl-7-anilinofluoran: 150 g 
     5% aqueous solution of PVA: 150 g 
     Water: 450 g 
     The mixture was blended and dispersed by a ball mill for 48 hours. 
     Dispersion F: 
     Benzyl p-hydroxybenzoate: 150 g 
     Stearic acid amide: 50 g 
     Zinc stearate: 50 g 
     5% aqueous solution of PVA: 200 g 
     Water: 300 g 
     The mixture was blended and dispersed by a ball mill for 24 hours. 
     Dispersion G: 
     Bisphenol A: 150 g 
     Stearic acid amide: 50 g 
     Zinc stearate: 50 g 
     5% aqueous solution of PVA: 200 g 
     Water: 300 g 
     The mixture was blended and dispersed by a ball mill for 24 hours. 
     Dispersion H: 
     150 g of water-insoluble rosin-modified phenol resin having a softening point of 80° to 190° C., 150 g of 5% aqueous solution of PVA and 200 g of water were dispersed by a ball mill for 24 hours. 
     Dispersion I: 
     80 g of terephthalic acid ester, 500 g of 5% aqueous solution of PVA and 100 g of water were dispersed by a ball mill for 48 hours. 
     Using the above described dispersions, calcium carbonate and 5% PVA, heat-sensitive coating for Examples 1-8 and Comparative Examples 1-7 having compositions shown in Table 1 were prepared. 
     Rosin-modified phenol resins and terephthalic acid esters used in Dispersions H and I in Table 1 are shown in Table 2. 
     
                                           TABLE 1                                 
__________________________________________________________________________
Example                    Comparative Example                            
1       2 3 4  5  6  7  8  1 2 3 4 5 6  7                                 
__________________________________________________________________________
Dispersion                                                                
(g)                                                                       
A     10                                                                  
        11                                                                
          --                                                              
            10 -- -- -- -- 20                                             
                             10                                           
                               --                                         
                                 --                                       
                                   --                                     
                                     -- --                                
B      6                                                                  
         6                                                                
          --                                                              
            7  7  -- --  1 --                                             
                             10                                           
                               10                                         
                                 --                                       
                                   20                                     
                                     -- --                                
C     --                                                                  
        --                                                                
          10                                                              
            -- 9   3  2  3 --                                             
                             --                                           
                               --                                         
                                 --                                       
                                   --                                     
                                     10 --                                
D      4                                                                  
        --                                                                
          10                                                              
            -- --  7  8  6 --                                             
                             --                                           
                               10                                         
                                 --                                       
                                   --                                     
                                     -- 10                                
E     --                                                                  
         3                                                                
          --                                                              
            3  4  -- -- -- --                                             
                             --                                           
                               --                                         
                                 20                                       
                                   --                                     
                                     -- --                                
F     30                                                                  
        30                                                                
          30                                                              
            25 30 -- -- -- 30                                             
                             30                                           
                               30                                         
                                 --                                       
                                   --                                     
                                     -- --                                
G     --                                                                  
        --                                                                
          --                                                              
            5  -- 50 50 50 --                                             
                             --                                           
                               --                                         
                                 40                                       
                                   40                                     
                                     50 50                                
H     --                                                                  
        --                                                                
          --                                                              
            -- -- 20 18 12 --                                             
                             --                                           
                               --                                         
                                 --                                       
                                   --                                     
                                     -- --                                
I     --                                                                  
        --                                                                
          --                                                              
            -- --  8 10 16 --                                             
                             --                                           
                               --                                         
                                 --                                       
                                   --                                     
                                     -- --                                
Calcium                                                                   
       4                                                                  
         4                                                                
           4                                                              
            4  4  30 30 30  4                                             
                              4                                           
                                4                                         
                                  4                                       
                                    4                                     
                                     30 30                                
Carbonate                                                                 
(g)                                                                       
5% PVA                                                                    
      80                                                                  
        80                                                                
          80                                                              
            80 80 260                                                     
                     255                                                  
                        260                                               
                           80                                             
                             80                                           
                               80                                         
                                 85                                       
                                   85                                     
                                     240                                  
                                        240                               
(g)                                                                       
__________________________________________________________________________
 
    
     
                       TABLE 2                                                     
______________________________________                                    
        Example                                                           
          6         7          8                                          
______________________________________                                    
Dispersion H                                                              
          Tamanol 135 Tamanol 350                                         
                                 Tamanol 145                              
(rosin-modi-                                                              
          (produced by                                                    
fied phenol                                                               
          Arakawa                                                         
resin)    Rinsan Co.                                                      
Dispersion I                                                              
          Dimethyl    Diethyl    Diphenyl                                 
(terephtha-                                                               
          terephthalate                                                   
                      terephthalate                                       
                                 terephthalate                            
lic acid                                                                  
ester)                                                                    
______________________________________                                    
 
    
     The heat-sensitive coatings for Examples 1-8 and Comparative Examples 1-7 prepared as described above were applied to paper bases having an areal weight of 50 to 53 g/m 2  so that the coating amount after drying was 5 g/m 2 . After dried, they were allowed to pass through a super-calender to obtain heat-sensitive sheets having a Bekk smoothness (JIS (Japanese Industrial Standard) P-8119) of 150 to 250 seconds. 
     Results of quality tests for the heat-sensitive sheets in Examples 1-8 and Comparative Examples 1-7 are shown in Tables 3 and 4. 
     
                       TABLE 3                                                     
______________________________________                                    
                               *4                                         
                     *3        Image  *5                                  
                     White-    residual                                   
                                      Finger-                             
       *1            ness after                                           
                               rate after                                 
                                      print                               
       White-                                                             
             *2      heat-     heat-  resisting                           
       ness  Print   treatment treatment                                  
                                      property                            
       (%)   density (%)       (%)    of image                            
______________________________________                                    
Example                                                                   
1        80.5    1.20    73.2    93     A                                 
2        79.8    1.24    72.8    94     A                                 
3        77.5    1.28    72.5    87     B                                 
4        78.7    1.15    70.4    90     A                                 
5        77.9    1.26    71.9    94     A                                 
Comparative                                                               
Example                                                                   
1        78.5    1.22    60.4    84     C                                 
2        80.1    1.21    48.2    93     B                                 
3        76.6    1.19    72.2    76     C                                 
4        83.6    1.14    78.7    62     C                                 
5        72.8    1.22    58.7    92     C                                 
______________________________________                                    
 
    
     
                                           TABLE 4                                 
__________________________________________________________________________
                                                Oil-resisting             
                                                resi-*.sup.7              
                               Oil-resisting resi-*.sup.6                 
                                                dual rate of image (2)    
                        Image resi-*.sup.4                                
                               dual rate of image (1)                     
                                                Kanabo                    
                                                     Shiseido             
                 Whiteness*.sup.3                                         
                        dual rate af-   Cotton  Eroika                    
                                                     Bravas               
                                                          Lion            
       White-*.sup.1                                                      
                 after heat-                                              
                        ter heat-                                         
                               Olive                                      
                                   Gamellia                               
                                        seed    hair hair Vitalis         
       ness Print*.sup.2                                                  
                 treatment                                                
                        treatment                                         
                               oil oil  oil  Lard                         
                                                liquid                    
                                                     cream                
                                                          V 7             
       (%)  density                                                       
                 (%)    (%)    (%) (%)  (%)  (%)                          
                                                (%)  (%)  (%)             
__________________________________________________________________________
Example                                                                   
6      77.0 0.95 73.0   98     89  87   84   88 82   84   85              
7      80.5 0.90 74.8   91     82  83   81   84 82   80   81              
8      81.5 1.01 75.4   96     91  94   92   89 88   91   92              
Comparative                                                               
Example                                                                   
6      62.5 1.08 47.8   100    95  96   94   92 94   95   93              
7      83.2 0.84 81.5   28     11  18    9   21 24   13    8              
__________________________________________________________________________
 *.sup.1 Whiteness was determined by measuring brightness by Hunter       
 according to JIS P8123. As a filter, an Amber filter was used.           
 *.sup.2 Print density was determined by printing with a facsimile test   
 chart No. 2 by means of Xerox telecopier 495 and measuring the density of
 the full black part by Macbeth RD514. (Wratten filter 106).              
 *.sup.3 Whiteness after heattreatment was determined by measuring the    
 whiteness of the unrecorded heatsensitive sheet in the same manner as in 
 *1 after being allowed to stand in a chamber at 60° C. and humidit
 (RH) 30% for 24 hours.                                                   
 *.sup.4 Image residual rate after heattreatment: Recording was carried ou
 by Telecopier 495 to obtain a full black part and the density of it was  
 measured by Macbeth RD514 in the same manner as in *2 to obtain D.sub.1. 
 Then, the resulting recorded sample was allowed to stand at 60° C.
 and humidity (RH) 30% for 24 hours. The density of the sample after being
 allowed to so stand was measured by Macbeth RD514 to obtain D.sub.2.     
 D.sub.2 /D.sub.1 × 100 was calculated as % to obtain the image     
 residual rate.                                                           
 *.sup.5 Recording was carried out with a facsimile test chart No. 4 by   
 Xerox Telecopier 495, and the image part of the recorded sample was      
 brought into contact with the palm of the hand or fingers of ten persons 
 several times. After being allowed to stand under an environment of      
 30° C. and RH 65% for 2 weeks, the degree of difficulty of reading
 the image was determined.                                                
 A: the state where the image is hardly different from that just after    
 recording.                                                               
 B: the state where the image can be easily read though fading is observed
 C: the state where fading of the image part is remarkable and the image  
 can not be read.                                                         
 *.sup.6 Oilresisting residual rate of image (1): Density D.sub.1 was     
 determined in the same manner as in *4. Then, an animal or vegetable oil 
 was allowed to adhere to the image part of the recorded sample in a      
 thickness of 2 μm. Namely, 0.2 cc of the animal or vegetable oil was  
 weighed out and applied to a drum of an IGT ink kneading apparatus, and  
 the rolls were revolved by the same operation as the ink kneading        
 operation to uniformly apply the oil (corresponding to an oil membrane   
 having 2 μm thickness on calculation). This oil membrane was          
 transferred to the recorded sample by a rubber stamp, etc. Then, the     
 recorded sample was allowed to stand in a chamber at 20° C. and   
 humidity (RH) 65% for 10 days. After 10 days, the oil adhesion part of th
 recorded sample was measured by Macbeth RD514 to obtain a density D.sub.3
 D.sub.3 /D.sub.1 × 100 was calculated as % to obtain an oilresistin
 residual rate of image (1).                                              
 *.sup.7 Oilresisting residual rate of image (2): The same procedure as in
 *5 was carried out using available hair cosmetics as the oil (Kanebo     
 Eroika hair liquid, Shiseido Bravas hair cream oil, and Lion Vitalis V7).
 
    
     It is obvious from the results shown in Tables 3 and 4 that the heat-sensitive recording sheets of the present invention are remarkably excellent as compared with the recording sheets in the comparative examples. 
     While the invention has been described in detail and with reference to specific embodiment thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.