Patent Publication Number: US-4321319-A

Title: Photosensitive compositions containing polyamides acid with photosensitive groups

Description:
TECHNICAL FIELD 
     The present invention relates to a new photosensitive polymer composition and to a support having thereon a cured film of this polymer composition. 
     BACKGROUND ART 
     As regards photosensitive polyimide, there have so far been known (a) the one prepared by coating a base plate with a mixture of 95-99 wt% of a polyamide acid type intermediate and 1-5 wt% of a dichromate, the coating being then irradiated with ultraviolet light, developed, if necessary, with hexamethylphosphoramide, and heated at 250° C. (U.S. Pat. No. 3,623,870), and (b) the other one prepared by coating a base plate with a polyamide acid intermediate having a photosensitive group in the molecule, the coating being then cured in the same way as in the case of (a) (DE-OS No. 2308830). 
     However, the above-said composition (a) has difficulty of handling due to instability of said mixture and problem of insulating properties due to the remaining dichromate in the cured coating. Also, in the above-said (b), it was necessary to use pure materials (1) and (2) below in case, for example, where said photosensitive polyamide acid intermediate is synthesized by addition polycondensation or by polycondensation of an isomeric mixture of dicarboxylic acid dichloride derivatives represented by the following formula (1) having photosensitive groups ##STR1## (wherein R* is a group ##STR2## with the polyfunctional ring compound of the following formula (2), ##STR3## in order to increase the molecular weight of the resulting photosensitive polyamide acid intermediate. However, the above compounds (1) are difficult to purify because of the high viscousness and the moisture-labile character; in addition, compound (1) has a disadvantage of requiring a high cost for their production, which is practiced in many steps through the following reactions (3): ##STR4## (wherein R* is a group ##STR5## 
     The object of this invention is to provide an inexpensive composition of photosensitive polymer without any of such disadvantages of the prior arts and to provide cured film thereof formed on a supporting material. 
     DISCLOSURE OF INVENTION 
     This invention is characterized in that a diamine having a photosensitive group is essentially used. That is, this invention is achieved by in the following process comprising: 
     (a) preparing a photosensitive polymer composition by blending a photosensitive polyamide acid intermediate solution in an inert organic solvent with a sensitizer (in a ratio of 80-99.5 wt% of said intermediate to 0.5-20 wt% of the sensitizer), said intermediate being obtained by reacting in an inert solvent; a first compound comprising 100-5 wt% preferably 100-60 wt% of a photosensitive group-containing diamine, which is represented by the general formula ##STR6## (wherein R 1  is a trivalent or tetravalent group having at least 2 carbon atoms, R 2  is a photosensitive group, 
     Y is a radical selected from ##STR7## and --CH 2  O--, and X is a --Y--R 2  group or H atom) and 0-95 wt%, preferably 0-40 wt% of a diamine having no photosensitive group, which is represented by the general formula 
     
         H.sub.2 N--R.sub.3 --NH.sub.2 
    
     (wherein R 3  is a divalent group having at least 2 carbon atoms and the two amino groups are bound to different carbon atoms in R 3 , respectively); with a second compound selected from at least one compound of a tetracarboxylic acid dianhydride represented by the general formula ##STR8## (wherein R 4  is a tetravalent group having at least 4 carbon atoms), and a tricarboxylic acid anhydride monohalide represented by the general formula ##STR9## (wherein R 5  is a trivalent group having at least 2 carbon atoms, and Z is a halogen atom), and (b) irradiating said photosensitive polymer composition with ultraviolet light to bind the photosensitive polyamide acid intermediate molecules with one another into crosslinked molecules and further heating the resulting composition to about 200° C. or more, preferably at 200°-350° C. (where heating between 200° and 350° C. is carried out in an inert gas), to transform the composition into a polyimide through the intra-molecular dehydrating reaction. 
     In this case, the intrinsic viscosity of said polyamide acid intermediate used is at least 0.1, preferably 0.3-5.0, wherein the intrinsic viscosity is calculated according to the following equation through the determination of viscosities at 30° C. of N,N-dimethylacetoamide solution containing 0.5% of the photosensitive polyamide acid intermediate and of N,N-dimethylacetamide (solvent): ##EQU1## (where C is the concentration of the photosensitive polyamide acid intermediate in gram/100 ml of the solution). 
     The melting point of the photosensitive polyamide acid intermediate having such a value of intrinsic viscosity does not indicate a fixed value. 
     The photosensitive polymer composition used in this invention can be prepared in the following way: Either a mixture (the first compound) of 100-5 wt% of a diamine having a photosensitive group and 0-95 wt% of a diamine having no photosensitive group or at least one compound (the second compound) selected from the tetracarboxylic acid dianhydrides and the tricarboxylic anhydride monohalides is dissolved in an inert organic solvent sufficiently as completely as possible. While the temperature of the reaction system is kept below about 80° C., preferably at room temperature or less, another component is added thereto and the mixture is stirred. Thereby the reaction proceeds fast and the viscosity of the reaction mixture increases gradually with formation of a photosensitive polyamide acid intermediate, giving its solution in an inert organic solvent. A sensitizer is added thereto (in a ratio of 80-99.5 wt% of the intermediate to 0.5-20 wt% of the sensitizer) to make up the objective photosensitive polymer composition. 
     This photosensitive polymer composition is then applied onto a support, dried (preferably at a temperature below 100° C.; any heating means can be applied) to vaporize the solvent, and thereafter irradiated with ultraviolet light and further heated at least at 200° C. In case of forming a pattern, a suitable mask is placed on the coating and the system is irradiated with ultraviolet light, subsequently treated with a developer and a rinsing liquid, and further heated at least at 200° C. 
     Therein, the irradiation with ultraviolet light is carried out, for example, by means of 1 kW high-voltage mercury lamp, but any other light source that generates actinic ray can be used. The intensity of the incident light is desirable to be 3-50 mW/cm 2  and the time of exposure is about 30 sec to 10 min. 
     The above-mentioned chemical reactions are shown in chemical reaction equation as follows: ##STR10## 
     The photosensitive polyamide acid intermediates thus obtained exist in various different forms as shown in the following general formulae, depending upon the kinds of the first and second compound used. ##STR11## (wherein R 1  is a trivalent or tetravalent group having at least 2 carbon atoms, R 2  is a photosensitive group, Y is a radical selected from ##STR12## and --CH 2  O--, R 3  is a divalent group having at least 2 carbon atoms, R 4  is a tetravalent group having at least 4 carbon atoms, R 5  is a trivalent group having at least 2 carbon atoms, X is a --Y--R 2  group or H, x is a number between 0 and 95 inclusive, and n is a positive integer). 
     The materials used in this invention are illustrated below: 
     As the diamines having a photosensitive group, for example, the following compounds are cited: ##STR13## (wherein Y is a radical selected from ##STR14## or others). 
     As examples of the diamine having no photosensitive group, the following compounds are cited: m-phenylenediamine, p-phenylenediamine, 4,4&#39;-diaminodiphenyl ether, 4,4&#39;-diaminodiphenylpropane, 4,4&#39;-diaminodiphenyl sulfone, 4,4&#39;-diaminodiphenyl sulfide, benzidine, 4,4&#39;-di(m-aminophenoxy)diphenyl sulfone, 4,4&#39;-di(p-aminophenoxy)diphenylpropane, 1,5-diaminonaphthalene, 3,3&#39;-dimethyl-4,4&#39;-diphenyldiamine, 3,3&#39;-dimethoxybenzidine, m-xylylenediamine, p-xylylenediamine, hexamethylenediamine, heptamethylenediamine, octamethylenediamine, ##STR15## 
     The reason for specifying the blending ratio of the diamine having a photosensitive group to the diamine having no photosensitive group as 100-5 wt% of the former to 0-95 wt% of the latter is due to the fact that, when the latter content exceeds 95 wt%, the photosensitive polymer composition is less sensitive to ultraviolet light and at the same time the resistance against a developer, of the portions exposed to ultraviolet irradiation is poorer. 
     The reason for specifying the preferred blending ratio of the diamine having a photosensitive group to the diamine having no photosensitive group as 100-60 wt% of the former to 0-40 wt% of the latter is due to the fact that this range gives best sensitivity and best resistance against a developer. 
     As the carboxylic acid dianhydride, there are mentioned, for example, dianhydride of pyromellitic acid, 2,2-bis(3,4-dicarboxyphenyl) propane, bis(3,4-dicarboxyphenyl) ether, bis(3,4-dicarboxyphenyl) sulfone, 3,3&#39;,4,4&#39;-benzophenone tetracarboxylic acid, 3,3&#39;,4,4&#39;-biphenyltetracarboxylic acid, 2,2&#39;,3,3&#39;-biphenyltetracarboxylic acid, 1,2,5,6-naphthalene tetracarboxylic acid, 2,3,6,7-naphthalene tetracarboxylic acid, 3,4,9,10-perylene tetracarboxylic acid, 2,2&#39;,6,6&#39;-biphenyl tetracarboxylic acid, 2,2-bis(3,4-dicarboxyphenyl) hexafluoropropane or others. 
     As the tricarboxylic acid anhydride monohalide, there are mentioned, for example, monohalides of the following compounds such as trimellitic anhydride, 2,3,6-naphthalene tricarboxylic anhydride, 2,3,5-naphthalene tricarboxylic anhydride, 2,2&#39;,3-biphenyl tricarboxylic anhydride, 3,4,4&#39;-biphenyl tricarboxylic anhydride, 2-(3,4-dicarboxyphenyl)-2-(3-carboxyphenyl) propane anhydride, 1,2,4-naphthalene tricarboxylic anhydride, 1,4,5-naphthalene tricarboxylic anhydride, 2-(2,3-dicarboxyphenyl)-2-(3-carboxyphenyl) propane anhydride, 1-(2,3-dicarboxyphenyl)-1-(3-carboxyphenyl) ethane anhydride, 1-(3,4-dicarboxyphenyl)-1-(4-carboxy-phenyl) ethane anhydride, (2,3-dicarboxyphenyl)(2-carboxyphenyl) methane anhydride, 1,2,3-benzene tricarboxylic anhydride, 3,3&#39;,4-tricarboxybenzophenone anhydride, etc. 
     When a first compound comprising a diamine having a photosensitive group and a diamine having no photosensitive group in a ratio of 100-5 wt% to 0-95 wt%, preferably 100-60 wt% of the former to 0-40 wt% of the latter is blended with an equivalent amount of a second compound consisting of at least one compound selected from tetracarboxylic dianhydrides and tricarboxylic anhydride monocarboxylic acid halides, the polymerization degree of the photosensitive polyamide acid intermediate is favorably larger, but it is unobjectionable to use either of the first and second compounds in somewhat excess amount. 
     The inert organic solvent used is required to be capable of dissolving all components of the first and second compounds mentioned above. A particularly favorable one is a solvent capable of dissolving the resulting photosensitive polyamide acid intermediate, such as, for example, N-methyl-2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone, N,N-dimethylacetamide, N-methylformamide, N,N-dimethylformamide, dimethyl sulfoxide, hexamethylphosphoramide, tetramethylene sulfone, dimethyl sulfone, pyridine, tetramethylurea, N-acetyl-2-pyrrolidone, etc. 
     These solvents can be used each alone or in combination with one another or with a solvent such as benzene, toluene, nitrotoluene, chlorobenzene, cyclohexanone, etc, added. As regards the amount of the solvent used for the polymerization, there is no particular restriction as far as it is sufficient to give a good polymerization system. When the solvent is used in such an amount that the solute content in the resulting solution is in the range from 0.1 to 40 wt%, a high molecular weight photosensitive polyamide acid intermediate can usually be obtained. 
     The photosensitive polymer composition of this invention contains a sensitizer. In the presence of a sensitizer, though the stability of the composition depends on the kind of the photosensitive group, the composition is always stable under the light-shielded condition at room temperature. It is also possible to add a stabilizer such as, for example, hydroquinone or tert-butyl catechol, to increase the stability. 
     At least one of sensitizers such as the following examples may be used: anthraquinone, 2-methylanthraquinone, 2-ethylanthraquinone, benzoquinone, 1,2-naphthoquinone, 1,4-naphthoquinone, 1,2-benzoanthraquinone, acetophenone, benzophenone, p,p&#39;-diaminobenzophenone, p,p&#39;-diamethylamino benzophenone, p,p&#39;-tetramethyldiaminobenzophenone (Michler&#39;s ketone), 2-nitrofluorene, 5-nitroacenaphthene, 4-nitro-1-naphthylamine, N-acetyl-4-nitro-1-naphthylamine-p-nitroaniline, 2-chloro-4-nitroaniline, pycramide, 2-t-butylanthraquinone, 1,2-benzanthraquinone, anthrone, 1,9-benzoanthrone, 3-methyl-1,3-diaza-1,9-benzoanthrone, dibenzalacetone, etc. 
     The blending ratio of the sensitizer to the photosensitive polyamide acid intermediate is desirably 0.5-20 wt% of the former to 80-99.5 wt% of the latter. When the sensitizer content is less than 0.5 wt%, the sensitizing effect does not appear, while, if the content exceeds 20 wt%, an adverse effect appears on the characteristics of the cured film. The photosensitive polymer of this invention may be incorporated with a dyestuff, a pigment, or a colorant. 
     The supports usable in this invention are, for example, metals, glass, semiconductors (for example, silicon wafer and germanium wafer), ceramics, plastics, paper, conductive films (for example, In 2  O 3 ), metal oxide insulators (for example, TiO 2 , Ta 2  O 5 , silicon oxides), silicon nitride, etc. 
     The application of the photosensitive polymer composition on an above-said support is carried out by a usual means such as spinner coating, immersion, spraying, printing or the like. Such application means are chosen according to the solid concentration and viscosity of the photosensitive polymer composition. The cured film thickness can be controlled by application means, and the solid concentration and viscosity of the photosensitive polymer composition. 
     The development after irradiation with ultraviolet light, of the coating on the support is carried out by a polymerization solvent such as, for example, N-methyl-2-pyrrolidone, N,N-diamethylacetoamide, N,N-dimethylformamide, etc. Such a solvent can optionally be used in incorporation with acetone, ethanol, or the like. 
     The rinsing liquid serves to wash away the developer solvent and it is preferable to use as the rinsing liquid a solvent such as toluene, acetone or ethanol, which is relatively well compatible with the developer solvent. 
    
    
     BEST MODE FOR CARRYING THE INVENTION 
     The invention is further illustrated by way of the following Examples. 
     EXAMPLE 1 
     In a 100-ml flask equipped with a thermometer, a stirrer, a calcium chloride tube, and a nitrogen inlet tube, 2.64 g (0.01 mol) of 2-(3&#39;,5&#39;-diaminobenzoyloxy) ethylmethacrylate and 48.2 g of N-methyl-2-pyrrolidone were placed and thoroughly stirred to dissolve the former. After the dissolution had been completed, 1.1 g (0.005 mol) of pyromellitic dianhydride and 1.61 g (0.005 mol) of 3,3&#39;,4,4&#39;-benzophenone tetracarboxylic dianhydride were added slowly under cooling of the flask with ice. Thereafter, the reaction was conducted at 15° C. for 6 hours, whereby an inert organic solvent solution of a photosensitive polyamide acid intermediate (a photosensitive polymer composition) was obtained. 
     The intrinisc viscosity of the photosensitive polyamide acid intermediate thus obtained was 0.85 (0.5% N,N-dimethylacetamide solution at 30° C.). 
     The viscosity of said photosensitive polymer composition was adjusted to 1000 cp (25° C.), and the resulting composition was applied on a silicon wafer by means of a spinner. The coated wafer was dried at 80° C. for 40 minutes to volatilize the solvent away and to complete the coating. This coating was covered with a mask having a desired pattern and irradiated with ultraviolet light at an incident beam intensity of 20 mW/cm 2  for 5 minutes by the use of a high-voltage mercury lamp to give a crosslinked polyamide acid coating. 
     Subsequently, the crosslinked coating was developed with a mixture of 3 volumes of N-methyl-2-pyrrolidone and 1 volume of ethanol and washed with a rinsing liquid (ethanol). Thereafter, the crosslinked coating was heated at 250° C. for 60 minutes to give a polyimide coating pattern. 
     This coating was flat and uniform (good coating quality), and the precision of the pattern was also good. 
     EXAMPLE 2 
     Starting materials were formulated as shown in Table 1, Nos. 1-3, and thereafter were processed in the same way as in Example 1. The results obtained are shown in Table 2, Nos. 1-3. From these results, it is proved that good blending ratios of the diamine having a photosensitive group to the diamine having no photosensitive group are in the range of 100-5 wt% of the former to 0-95 wt% of the latter. 
     EXAMPLE 3 
     Starting materials were formulated as shown in Table 1, Nos. 4-7, and thereafter were processed in the same way as in Example 1. The results obtained are shown in Table 2, Nos. 4-7. From these results and the results of Example 1, it is proved that good blending ratios of the sensitizer to the photosensitive polyamide acid intermediate is in the range of 0.5-20 wt% of the former to 80-95 wt% of the latter. 
     EXAMPLE 4 
     Various starting materials were formulated as shown in Table 3, Nos. 8-15, in Table 5, Nos. 16-23, in Table 7, Nos. 24-31, and in Table 9, Nos. 32-38, and thereafter were processed in the same way as in Example 1. The results obtained are shown in Table 4, Nos. 8-15, in Table 6, Nos. 16-23, in Table 8, Nos. 24-31, and in Table 10, Nos. 32-38. 
     
                                           TABLE 1                                 
__________________________________________________________________________
    Diamine having a photo-                                               
                     Diamine having no                  Polymer in        
    sensitive group  photosensitive  Acid anhydride     solution          
No. g (mol)          group g (mol)   g (mol)            wt%               
__________________________________________________________________________
     ##STR16##                                                            
                      ##STR17##                                           
                                      ##STR18##         N-methyl-2-       
                                                        pyrrolidone 10    
2                                                                         
     ##STR19##                                                            
                      ##STR20##      &#34;                  N-methyl-2-       
                                                        pyrrolidone 10    
3                                                                         
     ##STR21##                                                            
                      ##STR22##      &#34;                  N-methyl-2-       
                                                        pyrrolidone 10    
4                                                                         
     ##STR23##                                                            
                      ##STR24##      &#34;                  N-methyl-2-       
                                                        pyrrolidone 10    
5   &#34;                &#34;               &#34;                  N-methyl-2-       
                                                        pyrrolidone       
                                                        10                
6   &#34;                &#34;               &#34;                  N-methyl-2-       
                                                        pyrrolidone       
                                                        10                
7   &#34;                &#34;               &#34;                  N-methyl-2-       
                                                        pyrrolidone       
                                                        10                
__________________________________________________________________________
 
    
     
                       TABLE 2                                                     
______________________________________                                    
     Intrinsic               Coating                                      
     viscosity               quality   Preci-                             
     of       Sensitizer (wt %                                            
                             (supporting                                  
                                       sion of                            
No.  polymer  based on polymer)                                           
                             material) pattern                            
______________________________________                                    
1    0.87     2-methylanthraquinone                                       
                             good      good                               
              (8)            (silicon wafer)                              
2    0.90     2-methylanthraquinone                                       
                             good      good                               
              (8)            (silicon wafer)                              
3    1.01     2-methylanthraquinone                                       
                             good      inferior                           
              (8)            (silicon wafer)                              
4    0.85     2-methylanthraquinone                                       
                             good      inferior                           
                (0.1)        (silicon wafer)                              
5    &#34;        2-methylanthraquinone                                       
                             good      good                               
                (0.5)        (silicon wafer)                              
6    &#34;        2-methylanthraquinone                                       
                             good      good                               
               (20)          (silicon wafer)                              
7    &#34;        2-methylanthraquinone                                       
                             good      inferior                           
               (30)          (silicon wafer)                              
______________________________________                                    
 
    
     
         TABLE 3
   Diamine having a photo- Diamine having no  Polymer in  sensitive group
 photosensitive Acid anhydride solution No. g (mol) group g (mol) g (mol)
 wt%
        8
  ##STR25##
  ##STR26##
  ##STR27##
  N-methyl-2-pyrroli-done14.0 9
  ##STR28##
  --
  ##STR29##
  N-methyl-2-pyrroli-done15.0 10
  ##STR30##
  --
  ##STR31##
  N,N-di-methyl-acetamide15.0 11
  ##STR32##
  ##STR33##
  &#34; N-methyl-2-pyrroli-done15.0 12
  ##STR34##
  ##STR35##
  ##STR36##
  N-methyl-2-pyrroli-done13.0 13
  ##STR37##
  ##STR38##
  ##STR39##
  N-methyl-2-pyrroli-done15.0 14
  ##STR40##
  &#34;
  ##STR41##
  N-methyl-2-pyrroli-done9.2 15
  ##STR42##
  --
  ##STR43##
  N-methyl-2-pyrroli-done15.3
 
    
     
                       TABLE 4                                                     
______________________________________                                    
     Intrinsic               Coating                                      
     viscosity               quality   Preci-                             
     of       Sensitizer (wt %                                            
                             (supporting                                  
                                       sion of                            
No.  polymer  based on polymer)                                           
                             material) pattern                            
______________________________________                                    
 8   0.77     2-methylanthraquinone                                       
                             good      good                               
              (8)            (silicon wafer)                              
 9   0.85     Michler&#39;s ketone                                            
                             good      good                               
              (6)            (silicon wafer)                              
10   0.80     Michler&#39;s ketone                                            
                             good      good                               
              (6)            (silicon wafer)                              
11   0.76     N-acetyl-4-nitro-1-                                         
                             good      good                               
              naphthylamine  (aluminum)                                   
              (5)                                                         
12   0.61     N-acetyl-4-nitro-1-                                         
                             good      good                               
              naphthylamine  (ceramic)                                    
              (5)                                                         
13   0.59     N-acetyl-4-nitro-1-                                         
                             good      good                               
              naphthylamine  (silicon wafer)                              
              (5)                                                         
14   1.38     2-methylanthraquinone                                       
                             good      good                               
              (6)            (silicon wafer)                              
15   0.61     Michler&#39;s ketone                                            
                             good      good                               
              (6)            (silicon wafer)                              
______________________________________                                    
 
    
     
         TABLE 5
   Diamine having a photo- Diamine having no  Polymer in  sensitive group
 photosensitive Acid anhydride solution No. g (mol) group g (mol) g (mol)
 wt %
         16
  ##STR44##
  4.18 g(0.01) --
  ##STR45##
  N-methyl-2-pyrroli-done16.1
  ##STR46##
  17
  ##STR47##
  2.09 g(0.005)
  ##STR48##
  ##STR49##
  N-methyl-2-pyrroli-done(15.3)
  ##STR50##
  ##STR51##
      1.61 g (0.005) 18
  ##STR52##
  3.2 g(0.0076)
  ##STR53##
  &#34; N-methyl-2-pyrroli-done(15.3)
  ##STR54##
  19
  ##STR55##
  1.63 g(0.005) -- &#34; N,N-di-methyl-acet-amide(15.2)
  ##STR56##
  2.09 g(0.005)
  ##STR57##
  20
  ##STR58##
  1.32 g(0.005) -- &#34; N-methyl-2-pyrroli-done16
  ##STR59##
  1.78 g(0.005)
  ##STR60##
  21
  ##STR61##
  2.06 g(0.01) -- &#34; N-methyl-2-pyrroli-done18.0 22
  ##STR62##
  1.65 g(0.008)
  ##STR63##
  &#34; &#34; 23
  ##STR64##
  1.92 g(0.01) -- &#34; N-methyl-2-pyrroli-done 12.0
 
    
     
                       TABLE 6                                                     
______________________________________                                    
     Intrinsic               Coating                                      
     viscosity               quality   Preci-                             
     of       Sensitizer (wt %                                            
                             (supporting                                  
                                       sion of                            
No.  polymer  based on polymer)                                           
                             material) pattern                            
______________________________________                                    
16   0.55     p,p&#39;-tetramethyl                                            
                             good      good                               
              diaminobenzophenone                                         
                             (Electrode                                   
              (6)            Pattern: SiO.sub.x)                          
17   0.63     5-nitrofluorene                                             
                             good      good                               
              (10)                                                        
18   0.58     5-nitrofluorene                                             
                             good      good                               
              (10)           (quartz glass)                               
19   0.65     5-nitroacenaphthene                                         
                             good      good                               
              (8)            (silicon wafer)                              
20   0.79     Benzoin iso-   good      good                               
              propyl ether   (silicon wafer)                              
              (4)                                                         
21   1.23     2-methylanthraquinone                                       
                             good      good                               
              (4)            (silicon wafer)                              
22   1.01     N-acetyl-4-nitro-1-                                         
                             good      good                               
              naphthylamine  (silicon wafer)                              
              (8)                                                         
23   0.65     2-methylanthraquinone                                       
                             good      good                               
              (4)            (silicon wafer)                              
______________________________________                                    
 
    
     
                                           TABLE 7                                 
__________________________________________________________________________
                                                           Poly-          
                                                           mer in         
   Diamine having a photo-  Diamine having no              solu-          
   sensitive group          photosensitive  Acid anhydride tion           
No.                                                                       
   g (mol)                  group g (mol)   g (mol)        wt             
__________________________________________________________________________
                                                           %              
24                                                                        
    ##STR65##               --                                            
                                             ##STR66##     N- meth- yl-   
                                                           2-pyr- roli-   
                                                           done 10.0      
                                             ##STR67##                    
25                                                                        
    ##STR68##               --              &#34;              N- meth- yl-   
                                                           2-pyr- roli-   
                                                           done 10.1      
26                                                                        
    ##STR69##               --              &#34;              N- meth- yl-   
                                                           2-pyr- roli-   
                                                           done 15.0      
27                                                                        
    ##STR70##               --              &#34;              N,N- di- meth- 
                                                           l-ace- toam-   
                                                           ide 20.0       
28                                                                        
    ##STR71##               --              &#34;              1,3-di- meth-  
                                                           yl-2- imid-    
                                                           azo- lidi-     
                                                           none 10.0      
29 &#34;                        --                                            
                                             ##STR72##     N- meth- yl-   
                                                           2-pyr- roli-   
                                                           done 14.0      
                                             ##STR73##                    
30                                                                        
    ##STR74##                                                             
                             ##STR75##                                    
                                             ##STR76##     N- meth- yl-   
                                                           2-pyr- roli-   
                                                           done 12.0      
                                             ##STR77##                    
31                                                                        
    ##STR78##               --              &#34;              N- meth- yl-   
                                                           2-pyr- roli-   
                                                           done 21.0      
    ##STR79##                                                             
__________________________________________________________________________
 
    
     
                       TABLE 8                                                     
______________________________________                                    
     Intrinsic               Coating                                      
     viscosity               quality   Preci-                             
     of       Sensitizer (wt %                                            
                             (supporting                                  
                                       sion of                            
No.  polymer  based on polymer)                                           
                             material) pattern                            
______________________________________                                    
24   1.51     Benzoin iso-   good      good                               
              propyl ether   (silicon wafer)                              
              (8)                                                         
25   0.89     5-nitroacenaphthene                                         
                             good      good                               
              (10)           (silicon nitride)                            
26   1.05     2-methylanthraquinone                                       
                             good      good                               
              (8)            (ceramic)                                    
27   0.81     2-methylanthraquinone                                       
                             good      good                               
              (8)            (silicon wafer)                              
28   0.77     2-methylanthraquinone                                       
                             good      good                               
              (8)            (silicon wafer)                              
29   0.93     2-ethylanthraquinone                                        
                             good      good                               
              (8)            (aluminum)                                   
30   1.39     2-ethylanthraquinone                                        
                             good      good                               
              (8)            (silicon wafer)                              
31   0.83     p,p&#39;-tetramethyl-                                           
                             good      good                               
              diaminobenzophenone                                         
                             (silicon wafer)                              
              (5)                                                         
______________________________________                                    
 
    
     
                                           TABLE 9                                 
__________________________________________________________________________
   Diamine having a photo-                                                
                       Diamine having no                 Polymer in       
   sensitive group     photosensitive   Acid anyhydride  solution         
No.                                                                       
   g (mol)             group g (mol)    g (mol)          wt%              
__________________________________________________________________________
32                                                                        
    ##STR80##          --                                                 
                                         ##STR81##       N-methyl-        
                                                         2-pyrro- lidone  
                                                         10.0             
33                                                                        
    ##STR82##                                                             
                        ##STR83##       &#34;                N-methyl-        
                                                         2-pyrro- lidone  
                                                         14.0             
34                                                                        
    ##STR84##          --                                                 
                                         ##STR85##       N-methyl-        
                                                         2-pyrro- lidone  
                                                         12.0             
35                                                                        
    ##STR86##                                                             
                        ##STR87##       &#34;                N-methyl-        
                                                         2-pyrro- lidone  
                                                         20.0             
36                                                                        
    ##STR88##                                                             
                        ##STR89##                                         
                                         ##STR90##       N-methyl-        
                                                         2-pyrro- lidone  
                                                         16.0             
37                                                                        
    ##STR91##                                                             
                        ##STR92##                                         
                                         ##STR93##       N-methyl-        
                                                         2-pyrro- lidone  
                                                         15.0             
38                                                                        
    ##STR94##          &#34;                &#34;                N-methyl-        
                                                         2-pyrro- lidone  
                                                         11.0             
__________________________________________________________________________
 
    
     
                       TABLE 10                                                    
______________________________________                                    
     Intrinsic               Coating                                      
     viscosity               quality   Preci-                             
     of       Sensitizer (wt %                                            
                             (supporting                                  
                                       sion of                            
No.  polymer  based on polymer)                                           
                             material) pattern                            
______________________________________                                    
32   0.99     p,p&#39;-tetramethyl-                                           
                             good      good                               
              diaminobenzophenone                                         
                             (quartz glass)                               
              (5)                                                         
33   0.94     2-methylanthraquinone                                       
                             good      good                               
              (7)            (silicon wafer)                              
34   0.78     2-methylanthraquinone                                       
                             good      good                               
              (7)            (silicon wafer)                              
35   1.11     5-nitroacenaphthene                                         
                             good      good                               
              (9)            (SiO.sub.x glass)                            
36   1.09     Michler&#39;s ketone                                            
                             good      good                               
              (5)            (silicon wafer)                              
37   0.80     Michler&#39;s ketone                                            
                             good      good                               
              (5)            (silicon wafer)                              
38   0.58     Michler&#39;s ketone                                            
                             good      good                               
              (5)            (silicon wafer)                              
______________________________________