Patent Publication Number: US-2021193546-A1

Title: Packaging of a semiconductor device with dual sealing materials

Description:
TECHNICAL FIELD 
     The present invention relates to a semiconductor device, and for example, to a semiconductor device that handles high frequency signals. 
     BACKGROUND ART 
     In recent years, speeding up communication of mobile communication devices such as mobile phones and smart phones has become a trend with the spread of the Internet. Also, demand for safety is increasing, such as necessity of transmission and reception of images through disaster prevention radio communication. Along with this, increasing the reliability of high frequency communication packages, which are key devices, is urgently needed. 
     High frequency packages are semiconductor devices that input and output signals of frequencies higher than several tens of MHz, while amplifying and matching the signals. With the demand for speeding up communication, high output of semiconductor devices is required. In a semiconductor device with a high output, a package structure with high heat dissipation is required. In a package structure with high heat dissipation, a base plate is adopted, the base plate being obtained by bonding an insulating layer such as glass epoxy to a heat dissipation plate formed of a material, such as copper (Cu), excellent in heat dissipation. 
     For such a base plate, a package is formed by: cutting the glass epoxy layer by machining or the like: die-bonding a semiconductor element to a metal plate exposed in a recess of a metal base substrate; forming wiring by wire bonding; and performing resin sealing for dustproof. 
     The thermal expansion coefficients of silicon (Si), gallium arsenide (GaAs), silicon carbide (SiC), gallium nitride (GaN), and the like, which are substrates of semiconductor elements, are within the range of about 3 ppm/K to about 6 ppm/K (inclusive). These values are remarkably small compared to the thermal expansion coefficient (16 ppm/K) of Cu that constitutes a base plate to be used for heat dissipation. Therefore, there is the possibility that a crack or the like may occur in a die-bonding portion where the semiconductor element and the base plate are bonded together, due to thermal stress generated: in a die-bonding step of a manufacturing process; in temperature cycles in reliability evaluation; or the like, so that heat dissipation deteriorates. Then, measures have been taken, the measures including sealing the semiconductor element with a sealing material, such as an epoxy resin, in which fillers are dispersed to reinforce the die-bonding portion, for example. However, there has been the possibility that the sealing material may be peeled off the base plate since a warp is caused in the base plate due to the difference between the expansion coefficients of the sealing material and the base plate. There is the concern that a wire bonding portion may be damaged due to the peeling of the sealing material. 
     For example, in Patent Document 1, a method is proposed, in which the periphery of a flip-chip mounted element and other portions are sealed with materials having different physical properties. In Patent Document 2, a method of ensuring reliability is provided, in which the periphery of an element is sealed with hard epoxy and the whole is with a flexible urethane resin. 
     PRIOR ART DOCUMENTS 
     Patent Documents 
     
         
         Patent Document 1: Japanese Patent Application Laid-Open No. H10-209344 (1998) 
         Patent Document 2: Japanese Patent Application Laid-Open No. 2006-351737 
       
    
     SUMMARY 
     Problem to be Solved by the Invention 
     As described above, with the speeding up of communication and higher output of semiconductor devices, the thermal stress generated in the semiconductor devices is also increasing. Therefore, the demand for semiconductor devices with improved reliability against thermal stress is further increasing. 
     The present invention has been made in order to solve the above problem, and an object of the invention is to provide a semiconductor device with further improved reliability against thermal stress. 
     Means to Solve the Problem 
     The present invention provides a semiconductor device including an insulating layer, a conductive layer bonded to one main surface of the insulating layer, a semiconductor element arranged such that an upper surface of the semiconductor element faces a direction same as the one main surface of the insulating layer, an upper electrode provided on the upper surface of the semiconductor element, a wiring member that has one end electrically bonded to the upper electrode of the semiconductor element and has another end electrically bonded to the conductive layer, and has a hollow portion, a first sealing material, and a second sealing material softer than the first sealing material, in which the first sealing material seals at least part of the semiconductor element so as to be in contact with the semiconductor element, and the second sealing material seals the wiring member so as to be in contact with the wiring member. 
     Effects of the Invention 
     In the semiconductor device according to the present invention, the semiconductor element is sealed with the relatively hard first sealing material, and hence peeling of the semiconductor element can be suppressed. Further, the wiring member is sealed with the relatively soft second sealing material, and hence the wiring member can be protected from dust and thermal stress to the wiring member can be reduced even if thermal stress is applied to the circumference of the wiring member due to a warp caused in the insulating layer and the conductive layer, or the like. Therefore, the reliability of the semiconductor device can be improved. Furthermore, in the semiconductor device according to the present invention, the first sealing material seals the semiconductor element so as to be in contact with the semiconductor element, and hence the semiconductor element can be uniformly sealed. Similarly, the second sealing material seals the wiring member so as to be in contact with the wiring member, and hence the wiring member can be uniformly sealed. Therefore, the reliability of the semiconductor device can be further improved. 
     The objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings. 
    
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
         FIG. 1  is a cross sectional view of a semiconductor device according to a first embodiment. 
         FIG. 2  is a plan view of the semiconductor device according to the first embodiment. 
         FIG. 3  is a cross sectional view of a semiconductor device according to a second embodiment. 
         FIG. 4  is a plan view of the semiconductor device according to the second embodiment. 
         FIG. 5  is a view illustrating a manufacturing step of the semiconductor device according to the second embodiment. 
         FIG. 6  is a view illustrating a manufacturing step of the semiconductor device according to the second embodiment. 
         FIG. 7  is a view illustrating a manufacturing step of the semiconductor device according to the second embodiment. 
         FIG. 8  is a view illustrating a manufacturing step of the semiconductor device according to the second embodiment. 
         FIG. 9  is a view illustrating a manufacturing step of the semiconductor device according to the second embodiment. 
         FIG. 10  is a cross sectional view of a semiconductor device according to a third embodiment. 
         FIG. 11  is a plan view of the semiconductor device according to the third embodiment. 
         FIG. 12  is a cross sectional view of a semiconductor device according to a variation of the third embodiment. 
         FIG. 13  is a cross sectional view of a semiconductor device according to a fourth embodiment. 
         FIG. 14  is a plan view of the semiconductor device according to the fourth embodiment. 
         FIG. 15  is a plan view of a semiconductor device according to a fifth embodiment. 
         FIG. 16  is a plan view of a semiconductor device according to a sixth embodiment. 
         FIG. 17  is a plan view of a semiconductor device according to a seventh embodiment. 
         FIG. 18  is a cross sectional view of the semiconductor device according to the seventh embodiment. 
         FIG. 19  is a plan view schematically illustrating an air bridge existing area. 
         FIG. 20  is a plan view of a semiconductor device according to a variation of the seventh embodiment. 
         FIG. 21  is a cross sectional view of the semiconductor device according to the variation of the seventh embodiment. 
     
    
    
     DESCRIPTION OF EMBODIMENTS 
     First Embodiment 
       FIG. 1  is a cross sectional view of a semiconductor device according to a first embodiment.  FIG. 2  is a plan view of the semiconductor device according to the first embodiment. The cross section of the semiconductor device illustrated in  FIG. 1  is taken along line A-A of  FIG. 2 . In  FIG. 2 , a second sealing material  72  and a cap  6  are illustrated by virtual lines for easy understanding of the drawing. 
     The semiconductor device according to the first embodiment includes an insulating layer  32 , a conductive layer  33 , a heat dissipation plate  31 , a semiconductor element  1 , a plurality of wiring members  4 , a first sealing material  71 , and the second sealing material  72 . A base substrate  3  is composed of the heat dissipation plate  31 , the insulating layer  32 , and the conductive layer  33 . The insulating layer  32  is bonded to the upper surface of the heat dissipation plate  31 . The conductive layer  33  is bonded to the upper surface of the insulating layer  32 . 
     The plurality of the wiring members  4  include an input side wiring member  41  and an output side wiring member  42 . When the input side and the output side are not particularly distinguished, each of them is simply described as the wiring member  4 . The wiring member  4  is provided with a hollow portion  4   a . As illustrated in  FIG. 1 , the hollow portion  4   a  is a portion that exists between portions to which both the ends of the wiring member  4  are respectively bonded. 
     The conductive layer  33  is composed of a plurality of conductive patterns  331 ,  332 ,  333 , and  334  isolated from each other. Each of the plurality of the conductive patterns  331  is provided with an external electrode portion  331   a  to which a high frequency signal is to be input, and a wiring member bonding portion  331   b . Each of the plurality of the conductive patterns  332  is provided with a wiring member bonding portion  332   a . Each of the plurality of the conductive patterns  333  is provided with an external electrode portion  333   a  that outputs a high frequency signal. 
     The semiconductor element  1  is, for example, a power amplifier element of MHz band made of Si. The semiconductor element  1  is provided, on its upper surface, with a plurality of upper electrodes  9 . The upper electrodes  9  include an input side upper electrode  91  and an output side upper electrode  92 . When the input side and the output side are not particularly distinguished, each of them is simply described as the upper electrode  9 . The upper electrode  9  is made of an alloy containing, for example, aluminum (Al). The lower surface of the semiconductor element  1  is bonded to the conductive pattern  334  via a bonding material  2 . 
     The input side upper electrode  91  of the semiconductor element  1  and the conductive pattern  331  are electrically bonded with the wiring member  41 . That is, one end of the wiring member  41  is bonded to the input side upper electrode  91  of the semiconductor element  1 , and the other end of the wiring member  41  is bonded to the wiring member bonding portion  331   b  of the conductive pattern  331 . The output side upper electrode  92  of the semiconductor element  1  and the conductive pattern  332  are electrically bonded with the wiring member  42 . That is, one end of the wiring member  42  is electrically bonded to the output side upper electrode  92  of the semiconductor element  1 , and the other end of the wiring member  42  is electrically bonded to the wiring member bonding portion  332   a  of the conductive pattern  332 . In the first embodiment, the wiring member  4  is, for example, an Al wire having a diameter of 0.15 mm. 
     Each of the plurality of the conductive patterns  332  and a corresponding one of the plurality of the conductive patterns  333  are electrically connected via an electronic component  5  for adjusting high frequency characteristics. The external electrode portion  331   a  of the conductive pattern  331  is used as an external electrode of the semiconductor device. The external electrode portion  333   a  of the conductive pattern  333  is used as an external electrode of the semiconductor device. 
     As illustrated in  FIG. 1 , the semiconductor element  1  is sealed with the first sealing material  71 . The first sealing material  71  is, for example, an epoxy resin. The expansion coefficient is adjusted to about 16 ppm/K by dispersing silica fillers in the epoxy resin. 
     The surface of the semiconductor element  1  is sealed with the first sealing material  71 . The first sealing material  71  is in contact with the semiconductor element  1 . The upper surface of the conductive pattern  334  and the bonding material  2  are also sealed with the first sealing material  71 . The first sealing material  71  is also in contact with the conductive pattern  334  and the bonding material  2 . 
     The second sealing material  72  seals the wiring member  4  and the semiconductor element  1  sealed with the first sealing material  71 . The second sealing material  72  is softer than the first sealing material  71 . The second sealing material  72  is, for example, silicone gel. The second sealing material  72  is in contact with the surface of the wiring member  4 . 
     The cap  6  is fixed to the conductive layer  33  with an adhesive  61  so as to cover the semiconductor element  1 , the wiring member  4 , the first and second sealing materials  71  and  72 , and the like. The cap  6  is, for example, a polyphenylene sulfide (PPS) resin. The adhesive  61  is, for example, a silicone adhesive. 
     In the first embodiment, one semiconductor element  1  is arranged on the upper surface of the conductive pattern  334 , but a plurality of the semiconductor elements  1  may be arranged on the upper surface of the conductive pattern  334 . The semiconductor element  1  is a high frequency power amplifier that power amplifies a high frequency signal input via the input side upper electrode  91  and outputs the amplified high frequency signal from the output side upper electrode  92 . 
     As the semiconductor element  1  to be mounted in the package of the semiconductor device of the first embodiment, not only an element having the above power amplification function, but also an element having a high frequency signal switching function may be adopted. The high frequency signal is a signal of a frequency higher than several tens of MHz. The semiconductor element  1  may be, for example, a MOS-FET (Metal Oxide Semiconductor) or LDMOS (Lateral double Diffused MOSFET) containing silicon. Alternatively, the semiconductor element  1  may be a GaAs-HFET (Heterostructure Field Effect Transistor) or GaAs-HBT (Heterojunction Bipolar Transistor) containing gallium arsenide phosphide that is a compound semiconductor. Alternatively, the semiconductor element  1  may be a GaN-HFET (Heterostructure Field Effect Transistor) containing gallium nitride. A semiconductor element made of gallium nitride, which is a wide band gap semiconductor, has various merits including high electron velocity, high breakdown voltage because of wide band gap, being capable of high power operation, wide operating bandwidth, being capable of high temperature operation, low cost, and being capable of miniaturization. When a plurality of the semiconductor elements  1  are arranged on the upper surface of the conductive pattern  334 , the plurality of the semiconductor elements  1  may be composed of the same semiconductor elements or different semiconductor elements. 
     The heat dissipation plate  31  has a function of dissipating a lot of heat toward the outside, the heat being generated while the semiconductor element  1  is operating. Heat dissipation takes place both by heat transfer to the air due to convection and radiation and by heat conduction in which heat is transferred through objects in contact with each other. Therefore, the heat generated from the semiconductor element  1  can be effectively dissipated outside via the heat dissipation plate  31  by forming the heat dissipation plate  31  with a material excellent in thermal conductivity and by cooling a heat sink (not illustrated) arranged on a surface of the heat dissipation plate  31 , the surface being opposite to the semiconductor element  1 , with air cooling, water cooling, or the like. 
     In the first embodiment, the heat dissipation plate  31  made of Cu is used, but the material of the heat dissipation plate  31  is not limited to this. The heat dissipation plate  31  may be made, for example, of a metal material such as iron (Fe), tungsten (W), molybdenum (Mo), nickel (Ni), or cobalt (Co), or of an alloy material containing these metal materials. Alternatively, the heat dissipation plate  31  may be made of a composite material in which these metal materials or alloy materials are combined. 
     An alloy (Cu—W) of copper and tungsten is a composite material that combines the low thermal expansion of tungsten and the high thermal conductivity of copper. The thermal expansion coefficient can be adjusted in accordance with a surrounding material by changing the composition ratio of tungsten to copper. An alloy (Cu—Mo) of copper and molybdenum can be expected to have a higher thermal conductivity than Cu—W, and is a material whose thermal expansion coefficient and thermal conductivity can be similarly adjusted by changing the composition ratio of molybdenum to copper. Also, a clad material having a three-layer structure, obtained by using Cu—Mo as a core material and by bonding Cu to both the sides; and the like can be mentioned. Since the surface of this clad material is pure copper, surface heat dispersion can be increased. 
     The insulating layer  32  is a glass epoxy substrate such as FR (Flame Retardant)-4 or FR-5. The insulating layer  32  may be an alumina substrate. The material of the conductive layer  33  is not particularly limited as far as it has conductivity. The conductive layer  33  may be formed of a material mainly containing Cu, Al, and the like. Alternatively, the conductive layer  33  may be formed by plating a conductive material, such as Au or Ag, on the insulating layer  32 . 
     In the first embodiment, the wiring member bonding portions  331   b  are isolated from each other in the plurality of the conductive patterns  331 , as illustrated in  FIG. 2 , but the wiring member bonding portions  331   b  may be united without being isolated. In this case, when a wire as the wiring member  41  is wire bonded, it is sufficient to set the distance and height between the upper electrode  9  of the semiconductor element  1  and the wiring member bonding portion  331   b , and hence accurate alignment for each wiring member bonding portion  331   b  becomes unnecessary. Therefore, the time necessary for the wire bonding can be shortened. 
     When the wiring member bonding portion  331   b  is isolated for each wiring member  41 , as illustrated in  FIG. 2 , the area where the insulating layer  32  and the second sealing material  72  closely adhere to each other is increased, and hence reliability is improved. Thus, the shape of the wiring member bonding portion  331   b  may be determined in consideration of trade-off between takt time in manufacturing and reliability. Also, the shapes of the wiring member bonding portions  332   a  of the plurality of the conductive patterns  332  are determined in consideration of trade-off between takt time in manufacturing and reliability. 
     The number of the conductive patterns  334  may be one or more like the semiconductor element  1 , and in the first embodiment, the case where one conductive pattern  334  is provided is described. Although not described in the first embodiment, a solder resist may be formed on the insulating layer  32  in order to control the range of the wet spreading of a bonding material  51  for bonding the electronic component  5 . 
     The base substrate  3  is composed of the heat dissipation plate  31 , the insulating layer  32 , and the conductive layer  33 . The heat dissipation plate  31  is bonded to the insulating layer  32  via a fiber reinforced resin material like an epoxy resin reinforced by a glass cloth. It is desirable that the softening temperature of the fiber reinforced resin material is higher than the melting point of the bonding material  51 . 
     The electronic component  5  is, for example, a chip resistor. The chip resistor is mounted on the conductive layer  33  to adjust the high frequency characteristics of the semiconductor element  1 . In the first embodiment 1, a chip resistor is mounted as the electronic component  5 , but the electronic component  5  may be, for example, a chip capacitor or the like. One or more electronic components  5  are required, which is mounted on the conductive layer  33 . When a plurality of the electronic components  5  are mounted, they may be the same as or different from each other. The electronic component  5  is bonded to the conductive layer  33  with the bonding material  51 . The bonding material  51  is, for example, a solder paste. The solder paste is not limited to a Pb-based solder, and may be a Pb-free solder like SAC305. 
     The semiconductor element  1  is bonded to the conductive pattern  334  of the conductive layer  33  via the bonding material  2 . In the first embodiment, the bonding materials  2  is a solder alloy such as Au—Sn, Au—Ge, or Au—Si. The bonding material  2  is not limited to a solder alloy with a low melting point, and may be a conductive adhesive in which metal fillers with high thermal conductivity are dispersed. The conductive adhesive can be die-bonded at a low temperature lower than or equal to 200° C., which can reduce occurrence of thermal stress to be applied to the surrounding members and a warp, both possibly being caused during the die-bonding. Ag fillers are generally used as the metal fillers to be dispersed in the conductive adhesive, but metals other than Ag may be adopted and Cu fillers, Ni fillers, Au fillers, Pd fillers, carbon fillers, or the like can offer the same effects as Ag fillers. 
     In addition, as the bonding material  2 , a sinterable metal paste may be used, in which micro-sized metal particles, nano-sized metal particles, or micro-sized and nano-sized metal particles are mixed in a solvent. The sinterable metal paste can be die-bonded at about 200° C. like the conductive adhesive. Further, in a sinterable metal paste after sintering, metal particles are sinter-bonded together to produce a state close to a metal-bulk state, and hence very high heat resistance can be obtained. As a result, the reliability during high temperature operation at 175° C. or higher can be improved. As the sinterable metal paste, an Ag paste using Ag particles is generally used, but particles other than Ag may be used and a paste, in which Cu particles, Ni particles, Au particles, or the like are mixed in a solvent, can offer the same effects. 
     The epoxy resin to be used as the first sealing material  71  is a hard resin having a relatively high Young&#39;s modulus. Therefore, the reliability of the semiconductor device against thermal stress can be improved by covering and holding the semiconductor element  1  and the bonding material  2 . The flexural modulus of the epoxy resin is within the range of 100 MPa to 20000 MPa (inclusive), the glass transition temperature Tg is within the range of 140° C. to 210° C. (inclusive), and the thermal expansion coefficient al is within the range of 10×10′/K to 50×10 −6 /K (inclusive) at a temperature lower than or equal to Tg. The flexural modulus of the first sealing material  71  is more preferably about 150 MPa, the glass transition temperature Tg is more preferably within the range of 175° C. to 210° C. (inclusive), and the thermal expansion coefficient al is more preferably within the range of 10×10 −6 /K to 20×10 −6 /K (inclusive) at a temperature lower than or equal to Tg. When the glass transition temperature is 175° C. or higher, it can be avoided that the linear expansion coefficient may be rapidly increased by 2 to 4 times even at the maximum temperature during the operation of the semiconductor device, whereby the reliability during high temperature operation can be ensured. The first sealing material  71  is not limited to an epoxy resin, and a material having any molecular structure may be adopted as far as the above physical properties are satisfied. 
     Since the silicone gel to be used also as the second sealing material  72  is a relatively soft resin, deformation due to thermal stress can be absorbed. Therefore, it plays the role of protecting the wiring member  4  from dust without putting a heavy load on the wiring member  4 . The silicone gel is not particularly limited, but it is desirable that: the silicone gel is a one-liquid type that is easy to use; it sufficiently adheres to metals, ceramics, glass, and the like; the curing temperature is 200° C. or lower; the flexural modulus is within the range of 1 MPa to 5 MPa (inclusive); the viscosity is within the range of 10 Pa·s to 20 Pa·s (inclusive); and the penetration depth after curing is within the range of 30 to 100 (inclusive) (penetration depth is measured according to JIS K 6249). The second sealing material  72  is not limited to silicone gel, and a material having any molecular structure may be adopted as far as the above physical properties are satisfied. The above flexural moduli of the first and second sealing materials  71  and  72  are values based on the specification of JIS K 6911 (General Test Method for Thermosetting Plastics). 
     &lt;Manufacturing Method&gt; 
     A manufacturing method of the semiconductor device according to the first embodiment will be described. First, the base substrate  3  is provided. Next, the electronic component  5  is bonded to the conductive layer  33  by a reflow process. That is, the bonding material  51 , i.e., the solder paste is arranged on the conductive patterns  332  and  333  of the conductive layer  33  of the base substrate  3 , and the bonding material  51  is heated to be melted in a state where the electronic component  5  is mounted on the bonding material  51 . 
     Next, the semiconductor element  1  is bonded to the conductive pattern  334  with the bonding material  2 . The bonding material  2  is a conductive adhesive in which silver (Ag) fillers are dispersed in an epoxy resin. The bonding is performed by heating at 150° C. for 2 hours in a state where the semiconductor element  1  is arranged above the conductive pattern  334  via the bonding material  2 . 
     Next, the input side upper electrode  91  of the semiconductor element  1  and the conductive pattern  331  are bonded together with a wire, i.e., the wiring member  41  by wire bonding. Also, the output side upper electrode  92  of the semiconductor element  1  and the conductive pattern  332  are bonded together with a wire, i.e., the wiring member  42  by wire bonding. 
     Next, an epoxy resin is supplied with a dispenser as the first sealing material  71  for the semiconductor element  1 . The epoxy resin is cured by heating at 130° C. for 1.5 hours. As a result, the semiconductor element  1  is sealed with the first sealing material  71 . 
     Next, silicone gel is applied, from the outside of the first sealing material  71 , to the periphery of the semiconductor element as the second sealing material  72 . The silicone gel is cured by heating at 130° C. for 30 minutes. As a result, the semiconductor element  1  is sealed from the outside of the first sealing material  71  with the second sealing material  72 . Also, the wiring member  4  is sealed with the second sealing material  72 . 
     Finally, the cap  6  is adhered to the conductive layer  33  with the adhesive  61  so as to cover the semiconductor element  1 , the wiring member  4 , the electronic component  5 , and the like. The adhesive  61  is, for example, a silicone adhesive and is cured by heating at 120° C. for 1 hour. 
     &lt;Effects&gt; 
     The semiconductor device according to the first embodiment includes the insulating layer  32 , the conductive layer  33  bonded to one main surface of the insulating layer  32 , and the semiconductor element  1  arranged such that the upper surface of the semiconductor element  1  faces a direction same as the one main surface of the insulating layer  32 , and the semiconductor device further includes the upper electrode  9  provided on the upper surface of the semiconductor element  1 , the wiring member  4  that has one end electrically bonded to the upper electrode  9  of the semiconductor element  1  and has another end electrically bonded to the conductive layer  33 , and has the hollow portion  4   a , the first sealing material  71 , and the second sealing material  72  softer than the first sealing material  71 , in which the first sealing material  71  seals at least part of the semiconductor element  1  so as to be in contact with the semiconductor element  1 , and the second sealing material  72  seals the wiring member  4  so as to be in contact with the wiring member  4 . 
     In the semiconductor device according to the first embodiment, the semiconductor element  1  is sealed with the relatively hard first sealing material  71 , and hence peeling of the semiconductor element  1  can be suppressed. Further, the wiring member  4  is sealed with the relatively soft second sealing material  72 , and hence the wiring member  4  can be protected from dust and stress to the wiring member  4  can be reduced even if stress is applied to the circumference of the wiring member  4  due to a warp caused in the insulating layer  32  and the conductive layer  33 , or the like. Therefore, the reliability of the semiconductor device can be improved. 
     Furthermore, in the semiconductor device according to the first embodiment, the first sealing material  71  seals the semiconductor element  1  so as to be in contact with the semiconductor element  1 , and hence the semiconductor element  1  can be uniformly sealed. Similarly, the wiring member  4  can be uniformly sealed by the second sealing material  72  sealing the wiring member  4  so as to be in contact with the wiring member  4 . Therefore, the reliability of the semiconductor device can be further improved. 
     In the semiconductor device according to the first embodiment, an area of the wiring member  4  where the wiring member  4  is in contact with the second sealing material  72  is larger than an area of the wiring member  4  where the wiring member  4  is in contact with the first sealing material  71 . That is, in the first embodiment, the periphery of a portion of the wiring member  4 , in the portion the wiring member  4  being bonded to the upper electrode  9  of the semiconductor element  1 , is sealed with the first sealing material  71 , but most part of the wiring members  4  is sealed with the second sealing material  72 , as illustrated in  FIG. 1 . Since most part of the wiring member  4  is sealed with the relatively soft second sealing material  72 , thermal stress to the wiring member  4  can be reduced. 
     In the semiconductor device according to the first embodiment, the wiring member  4  is a wire Wires are generally susceptible to damage from external forces, such as disconnection. In the first embodiment, thermal stress to the wiring member  4  can be reduced by sealing the wire with the relatively soft second sealing material  72 , even if a warp is caused in the base substrate  3 . 
     In the semiconductor device according to the first embodiment, the flexural modulus of the second sealing material  72  is smaller than that of the first sealing material  71 . For example, the flexural modulus of the second sealing material  72  is set to be within the range of 1 MPa to 5 MPa (inclusive), and that of the first sealing material  71  is set to about 150 MPa, in the first embodiment. The semiconductor element  1  can be firmly held to the conductive pattern  334  via the bonding material  2  by sealing the semiconductor element  1  with the first sealing material  71  that has a relatively large flexural modulus, i.e., that is relatively hard. Further, thermal stress to the wiring member  4  can be reduced by sealing the wiring member  4  with the second sealing material  72  that has a relatively small flexural modulus, i.e., that is relatively soft. 
     Second Embodiment 
       FIG. 3  is a cross sectional view of a semiconductor device according to a second embodiment.  FIG. 4  is a plan view of the semiconductor device according to the second embodiment. The cross section of the semiconductor device illustrated in  FIG. 3  is taken along line B-B of  FIG. 4 . In  FIG. 4 , a second sealing material  72  and a cap  6  are illustrated by virtual lines for easy understanding of the drawing. 
     In the second embodiment, an opening  8  is provided in almost the center of a base substrate  3 . Since the length of a wiring member  4 , one of the factors that reduce high frequency characteristics, can be shortened by providing the opening  8 , a structure suitable for a high frequency semiconductor device can be achieved. 
     A heat dissipation plate  31  is not covered with an insulating layer  32  in the opening  8 . The opening  8  is formed by cutting the insulating layer  32 , for example, by machining. In the second embodiment, the opening  8  is provided in the base substrate  3 , and hence a conductive layer  33  has a configuration in which the conductive pattern  334  described in the first embodiment is not included. In the second embodiment, the lower surface of a semiconductor element  1  is bonded to a heat dissipation plate  31  via a bonding material  2  in the opening  8  of the base substrate  3 . 
     The opening  8  of the base substrate  3  and the semiconductor element  1  are sealed with a first sealing material  71 . The first sealing material  71  is, for example, an epoxy resin. The first sealing material  71  has the physical characteristics described in the first embodiment. 
     The periphery of the opening  8  is sealed with a second sealing material  72 . The second sealing material  72  is softer than the first sealing material  71 . The second sealing material  72  is, for example, silicone gel. The second sealing material  72  seals the wiring member  4 . The second sealing material  72  also seals the semiconductor element  1  from the outside of the first sealing material  71 . The second sealing material  72  has the physical characteristics described in the first embodiment. 
     The semiconductor element  1  is arranged in the opening  8  of the base substrate  3 . In the second embodiment, one semiconductor element  1  is arranged in the opening  8 , but a plurality of the semiconductor elements  1  may be arranged in the opening  8 . When a plurality of the semiconductor elements  1  are arranged in the opening  8 , the plurality of the semiconductor elements  1  may be composed of the same semiconductor elements or different semiconductor elements. 
     The insulating layer  32  has the opening  8  having a depth reaching up to the heat dissipation plate  31 , so that when the base substrate  3  alone is viewed in plan, the heat dissipation plate  31  is exposed outside. The number of the openings  8  may be one or more like the semiconductor element  1 , and in the second embodiment, the case where one opening  8  is provided is described. 
     Since other configurations of the semiconductor device of the second embodiment are the same as the semiconductor device of the first embodiment, description thereof will be omitted. 
     &lt;Manufacturing Method&gt; 
       FIGS. 5 to 9  are views each illustrating a manufacturing step of the semiconductor device according to the second embodiment. First, the base substrate  3  is provided. Next, an electronic component  5  is bonded to the conductive layer  33  by a reflow process, as illustrated in  FIG. 5 . That is, the bonding material  51 , i.e., the solder paste is arranged on the conductive patterns  332  and  333  of the conductive layer  33  of the base substrate  3 , and the bonding material  51  is heated to be melted in a state where the electronic component  5  is mounted on the bonding material  51 . 
     Next, the semiconductor element  1  is bonded to the heat dissipation plate  31  with the bonding material  2 , as illustrated in  FIG. 6 . The bonding material  2  is a conductive adhesive in which silver (Ag) fillers are dispersed in an epoxy resin. The bonding is performed by heating at 150° C. for 2 hours in a state where the semiconductor element  1  is arranged above the heat dissipation plate  31  via the bonding material  2 . 
     Next, an input side upper electrode  91  of the semiconductor element  1  and a conductive pattern  331  are bonded together with a wire, i.e., a wiring member  41  by wire bonding, as illustrated in  FIG. 7 . Also, the output side upper electrode  92  of the semiconductor element  1  and the conductive pattern  332  are bonded together with a wire, i.e., the wiring member  42  by wire bonding. 
     Next, an epoxy resin is supplied with a dispenser as the first sealing material  71  for the opening  8 , as illustrated in  FIG. 8 . The epoxy resin is cured by heating at 130° C. for 1.5 hours. As a result, the opening  8  and the semiconductor element  1  is sealed with the first sealing material  71 . 
     Next, the silicone gel is applied, from the outside of the first sealing material  71 , to the periphery of the semiconductor element as the second sealing material  72 , as illustrated in  FIG. 9 . The silicone gel is cured by heating at 130° C. for 30 minutes. As a result, the semiconductor element  1  is sealed from the outside of the first sealing material  71  with the second sealing material  72 . Also, the wiring member  4  is sealed with the second sealing material  72 . 
     Finally, the cap  6  is adhered to the conductive layer  33  with the adhesive  61  so as to cover the semiconductor element  1 , the wiring member  4 , the electronic component  5 , and the like. The adhesive  61  is cured by heating at 120° C. for 1 hour. The semiconductor device illustrated in  FIG. 3  is obtained through the above manufacturing steps. 
     &lt;Effects&gt; 
     The semiconductor device according to the second embodiment further includes the heat dissipation plate  31 , in which: another main surface of the insulating layer  32  is bonded to one main surface of the heat dissipation plate  31 ; the opening  8 , where the heat dissipation plate  31  is not covered with the insulating layer  32 , is provided on the one main surface of the heat dissipation plate  31 ; the lower surface of the semiconductor element  1  is bonded to the one main surface of the heat dissipation plate  31  in the opening  8 ; and the first sealing material  71  seals at least part of the semiconductor element  1  and the opening  8 . 
     In the semiconductor device according to the second embodiment, a structure is adopted, in which the semiconductor element  1  is bonded directly onto the heat dissipation plate  31 . Therefore, in a die-bonding step of the manufacturing steps or temperature cycles in reliability evaluation, large thermal stress is generated in a die-bonding portion (i.e., the bonding material  2  that bonds the semiconductor element  1  and the heat dissipation plate  31 ) due to a mismatch between the thermal expansion coefficients of the semiconductor element  1  and the heat dissipation plate  31 . As a result, there is the possibility that a crack or the like may occur in the die-bonding portion so that heat dissipation deteriorates. 
     If the area ranging from the inside of the opening  8  to the wiring member  4  is sealed, for example, only with silicone gel, the force by which the semiconductor element  1  and a bonding material  2  are held is small since the silicone gel is relatively soft, and the deterioration of the bonding material  2  cannot be suppressed. 
     Alternatively, if the area ranging from the inside of the opening  8  to the wiring member  4  is sealed, for example, only with an epoxy resin, the thermal expansion coefficient of the epoxy resin, adjusted to the thermal expansion coefficient of Cu that forms the heat dissipation plate  31 , is within the range of 15 ppm/K to 20 ppm/K (inclusive). On the other hand, the thermal expansion coefficient in the thickness direction of glass epoxy that forms the insulating layer  32  is about 60 ppm/K, and hence peeling is likely to occur at the interface between the epoxy resin and the glass epoxy during temperature cycles. Since the peeling propagates toward the outside of the peeled portion, the outside having large thermal stress, there is high possibility that the wiring member  4  bonded to the surface of the conductive layer  33  may be damaged. Further, the epoxy resin is also peeled between the epoxy resin and the conductive layer  33  in a reliability test such as a thermal shock test or an intermittent current test, and hence it has been confirmed that it is difficult to extend the life of the semiconductor device. Since the adhesion of a common epoxy resin to the conductive layer  33  formed of Au or the like is not so good, it is considered that the peeling has occurred by the thermal stress continuously applied in the above reliability test. In addition, an epoxy resin has a high Young&#39;s modulus and the adhesion to the wiring member  4  is relatively good, and hence when the epoxy resin is peeled off the conductive layer  33 , it lifts the wiring member  4  together. This is the same even in a structure in which the opening  8  is not provided like the first embodiment, and if the wiring member  4  is covered with an epoxy resin such that the end of the wiring member  4  is the starting point or end point, the peeling of the epoxy resin occurs with the conductive layer  33  located directly below it as the starting point. 
     In the second embodiment, the inside of the opening  8  of a base substrate  3  is sealed with the relatively hard first sealing material  71 , and the wiring member  4  outside the opening  8  is sealed with the relatively soft second sealing material  72 , as illustrated in  FIG. 3 . The bonding material  2 , which is susceptible to the influence of the thermal stress occurring due to the difference between the thermal expansion coefficients of the semiconductor element  1  and the heat dissipation plate  31 , is reinforced by the relatively hard first sealing material  71 . Further, by sealing the wiring member  4  with the relatively soft second sealing material  72 , the wiring member  4  can be protected from dust and thermal stress to the wiring member  4  can be reduced even if a warp is caused in the base substrate  3 . Therefore, the reliability of the semiconductor device can be improved. 
     In the opening  8  in the semiconductor device according to the second embodiment, one main surface of the insulating layer  32 , i.e., the upper surface of the insulating layer  32  is arranged to be higher than the upper surface of the semiconductor element  1 . By arranging the upper surface of the insulating layer  32  so as to be higher than the upper surface of the semiconductor element  1 , the semiconductor element  1  can be sealed just enough with the first sealing material  71  without the first sealing material  71  greatly swelling from the opening  8 . 
     In the semiconductor device according to the second embodiment, the insulating layer  32  is glass epoxy and the first sealing material  71  is an epoxy resin. Since an epoxy resin has high adhesion to glass epoxy, the first sealing material  71  satisfactorily adheres to a side surface  32   a  of the insulating layer  32  in the opening  8 . As a result, peeling of the first sealing material  71  from the heat dissipation plate  31 , which may be caused due to the thermal stress or a warp that may be caused: in a die-bonding step of the manufacturing steps; in temperature cycles in reliability evaluation; or the like, can be suppressed. 
     In the semiconductor device according to the second embodiment, the first sealing material  71  is an epoxy resin and the second sealing material  72  is silicone gel. Since the thermal conductivity of an epoxy resin is generally higher than that of silicone gel, the heat dissipation of the semiconductor device is improved by sealing the semiconductor element  1  with an epoxy resin. 
     In the semiconductor device according to the second embodiment, the bonding material  2  that bonds the semiconductor element  1  and the heat dissipation plate  31  is a conductive resin, and the conductive resin contains one of an epoxy resin, an acrylic resin, and silicone rubber, and metal fillers. As the bonding material  2  that bonds the semiconductor element  1  and the heat dissipation plate  31 , a conductive adhesive containing metal fillers such as Ag, Au, or Cu may be used. When the conductive adhesive is used, not only the metal fillers but also an epoxy resin, a silicone resin, or an acrylic resin exist in the surface of a fillet portion, and the adhesion of the conductive adhesive to the first sealing material  71  is more excellent compared to a solder fillet. Therefore, the first sealing material  71  can hold the bonding material  2  more firmly, and the reliability of the semiconductor device can be further improved. 
     In the semiconductor device according to the second embodiment, the bonding material  2  that bonds the semiconductor element  1  and the heat dissipation plate  31  may be a sinterable bonding material. The surface of the bonding material  2  may also be porous. 
     As the bonding material  2  that bonds the semiconductor element  1  and the heat dissipation plate  31 , a sinterable metal paste may be used, in which micro-sized metal particles, nano-sized metal particles, or micro-sized and nano-sized metal particles are mixed in a solvent. The sinterable metal (e.g., Ag, Au, Cu, or the like) paste can be die-bonded at a low temperature lower than or equal to about 200° C. like the conductive adhesive, and in addition metal particles are sinter-bonded together after sintering to produce a state close to a metal-bulk state, and hence very high-adhesion, -thermal conductivity, and -heat resistance can be obtained. As a result, the reliability during high temperature operation at 175° C. or higher can be improved. When the metal sintering material is used, many holes, from which the volatilized solvent has been released at the time of sintering, are formed on the surface of a fillet portion, and hence the fillet portion has a porous structure. Therefore, the first sealing material  71  injected into the opening  8  of the base substrate  3  penetrates into the holes of the fillet portion, which improves adhesion by an anchor effect. Therefore, the first sealing material  71  can hold the bonding material  2  more firmly, and the reliability of the semiconductor device can be further improved. 
     There are two types of the above sinterable metal paste, including one type that needs pressure during sintering and the other type that does not need pressure. In the case of the type that needs pressure, it is necessary to provide a shock absorber between the chip-shaped semiconductor element  1  and a pressure unit of a pressure apparatus since pressure cannot be applied directly to the surface of the semiconductor element  1  by the pressure apparatus. In addition, any foreign matter attached to the surface of the semiconductor element  1  can cause a scratch in the semiconductor element  1 , and hence the type that needs pressure is not so suitable for the bonding material  2  to be used in a high frequency semiconductor element with a delicate surface. On the other hand, in the case of a sinterable metal paste, the other type that does not need pressure, the tackiness of the paste is lost when temporarily sintered and its bonding strength, which is small compared to that of the pressure type, becomes still smaller, and hence it is desirable to complete sintering by one-time heating. 
     Third Embodiment 
       FIG. 10  is a cross sectional view of a semiconductor device according to a third embodiment.  FIG. 11  is a plan view of the semiconductor device according to the third embodiment. The cross section of the semiconductor device illustrated in  FIG. 10  is taken along line C-C of  FIG. 11 . In  FIG. 11 , a second sealing material  72  and a cap  6  are illustrated by virtual lines for easy understanding of the drawing. 
     In the third embodiment, an opening  8  of a base substrate  3  is also sealed with a first sealing material  71  like the second embodiment. In the third embodiment, the opening  8  is further filled with the first sealing material  71  to a height higher than or equal to the height of one main surface (i.e., the upper surface) of an insulating layer  32 , as illustrated in  FIG. 10 . The first sealing material  71  is arranged such that it may be in contact with the side surface of a conductive layer  33  but it is not in contact with the upper surface of the conductive layer  33 . 
       FIG. 12  is a cross sectional view illustrating a variation of the semiconductor device according to the third embodiment. As illustrated in  FIG. 12 , a second sealing material  72  may be arranged in a divided shape. In this case, the second sealing material  72  is applied in two steps in a manufacturing step. Since the second sealing material  72  is applied in two steps, an application amount per step can be reduced, which makes it easy to adjust an application amount for sealing the wiring member  4  just enough. 
     Since other configurations of the semiconductor devices of the third embodiment and the variation of the third embodiment are the same as the semiconductor device of the second embodiment, description thereof will be omitted. 
     &lt;Effects&gt; 
     In the semiconductor device according to the third embodiment, the opening  8  is filled with the first sealing material  71  to a height higher than or equal to the height of the one main surface of the insulating layer  32 . Thereby, the contact area between the first sealing material  71  and a side surface  32   a  of the insulating layer  32  is increased, and hence the adhesion between the first sealing material  71  and a heat dissipation plate  31  is increased and the reliability of the semiconductor device can be further improved. In particular, when the insulating layer  32  is glass epoxy and the first sealing material  71  is an epoxy resin, an epoxy resin has high adhesion to glass epoxy, and hence the first sealing material  71  satisfactorily adheres to the side surface  32   a  of the insulating layer  32  in the opening  8 . Therefore, the adhesion between the first sealing material  71  and the heat dissipation plate  31  is further improved, and the reliability of the semiconductor device can be further improved. 
     In order to confirm effects of improving the adhesion in the third embodiment 3, a resin adhesion strength test (i.e., a pudding-cup test) was carried out. In the resin adhesion strength test, a first sample was made, in which a stainless steel cup (diameter: 6 mm, height: 4 mm) was mounted on a copper plate whose surface was plated with Ni or Au and then an epoxy resin was applied. Then, a second sample was made, in which a stainless steel cup was mounted on a glass epoxy plate and an epoxy resin was applied. The epoxy resin of each sample was cured under the recommended conditions. As a result of carrying out a shear test for the first sample in each of a room temperature atmosphere and 150° C. atmosphere, shear strength was 20 kg and 10 kg. As a result of carrying out a shear test for the second sample in each of a room temperature atmosphere and 150° C. atmosphere, shear strength was 42 kg and 38 kg. From the above results, it was found that the adhesion of the epoxy resin to the glass epoxy plate was two times or more than the adhesion to the copper plate. It was also found that high adhesion was maintained even in a high temperature atmosphere as high as 150° C. From the above tests, it was confirmed that the reliability of the semiconductor device can be improved by increasing the contact area between the epoxy resin as the first sealing material  71  and the glass epoxy as the insulating layer  32 . 
     Fourth Embodiment 
       FIG. 13  is a cross sectional view of a semiconductor device according to a fourth embodiment.  FIG. 14  is a plan view of the semiconductor device according to the fourth embodiment. The cross section of the semiconductor device illustrated in  FIG. 13  is taken along line D-D of  FIG. 14 . In  FIG. 14 , a second sealing material  72  and a cap  6  are illustrated by virtual lines for easy understanding of the drawing. 
     In the fourth embodiment, an opening  8  of a base substrate  3  is also sealed with a first sealing material  71  like the second embodiment. In the fourth embodiment, the first sealing material  71  seals part of a semiconductor element  1  so as not to be in contact with a wiring member  4 . A second sealing material  72  seals the whole of the wiring member  4 . 
     That is, the first sealing material  71  is arranged such that it may be in contact with the side surface of the semiconductor element  1  but may not be in contact with the upper surface of the semiconductor element  1 . However, unless the first sealing material  71  is not in contact with a hollow portion  4   a  of the wiring member  4 , the first sealing material  71  may cover the upper surface of the semiconductor element  1 . The second sealing material  72  may be in contact with at least the whole of the hollow portion  4   a  of the wiring member  4 . 
     In semiconductor devices handling high frequency signals, a coplanar line type MMIC (Monolithic Microwave Integrated Circuit) is known as one of the common configurations of MMICs in which an active element and a passive element can be collectively formed on a semiconductor substrate. In the coplanar line type MIMIC, a fine air bridge of about several μm may be arranged on the surface of the semiconductor element  1 . As illustrated in  FIG. 19  described later, the semiconductor element  1  is provided with an air bridge existing area  100  between upper electrodes  91  and  92 . The air bridge is provided above the air bridge existing area  100 . The case is considered, in which the air bridge, which is one wiring structure, is covered with a hard resin like an epoxy resin. In this case, there is the possibility that the fine air bridge may be crushed by the hardness of the cured epoxy resin or by the stress of the epoxy resin occurring during cure shrinkage. 
     Therefore, it is preferable that the first sealing material  71  seals part of the semiconductor element  1  so as not to be in contact with the air bridge and the upper surface of the semiconductor element  1  without covering the entire surface of the semiconductor element  1 , as illustrated in  FIG. 14 . 
     Since other configurations of the semiconductor device of the fourth embodiment are the same as the semiconductor device of the second embodiment, description thereof will be omitted. 
     &lt;Effects&gt; 
     In the semiconductor device according to the fourth embodiment, the first sealing material  71  seals at least part of the semiconductor element  1  so as not to be in contact with the hollow portion  4   a  of the wiring member  4 , and the second sealing material  72  is in contact with the whole of the hollow portion  4   a  of the wiring member  4 . 
     At the interface where a hard sealing material and a soft sealing material are in contact with each other, there is the possibility that the stress, occurring due to the differences between the Young&#39;s moduli of the two sealing materials and between the thermal expansions thereof, may concentrate during a temperature cycle test and a power cycle test. Also, the amount of moisture absorbed from the outside is increased at the interface, even though the hard sealing material and the soft sealing material adhere together. There is the possibility that a wire may deteriorate due to a lot of moisture absorption, so that wire disconnection is accelerated. In the fourth embodiment, the second sealing material  72  is in contact with the hollow portion  4   a  of the wiring member. That is, the interface between the first sealing material  71  and the second sealing material  72  is not in contact with the hollow portion  4   a  of the wiring member  4 , and hence disconnection of the wiring member  4 , which may be caused by stress, can be suppressed. Further, deterioration of the wiring member  4 , which may be caused by moisture, can be suppressed. Furthermore, the whole of the hollow portion  4   a  of the wiring member  4  is sealed with the soft second sealing material  72 , and hence the influence of stress given to the wiring member  4  can be reduced, and the reliability of the semiconductor device can be further improved. 
     Fifth Embodiment 
       FIG. 15  is a plan view of a semiconductor device according to a fifth embodiment. In  FIG. 15 , a second sealing material  72  and a cap  6  are illustrated by virtual lines for easy understanding of the drawing. In the second embodiment, the whole of the opening  8  of the base substrate  3  is sealed with the first sealing material  71 . 
     On the other hand, in the fifth embodiment, a semiconductor element  1  has a rectangular shape in plan view, and the four corners and the short sides facing each other of the semiconductor element  1  are sealed with a first sealing material  71 , as illustrated in  FIG. 15 . The first sealing material  71  is also in contact with a side surface  32   a  of an insulating layer  32  near to the short side of the semiconductor element  1 , and the first sealing material  71  has sufficient adhesion strength. Also, in the fifth embodiment, it is desirable to arrange the first sealing material  71  so as not to be in contact with a hollow portion  4   a  of a wiring member  4  like the fourth embodiment. 
     As illustrated in  FIG. 15 , a portion of the opening  8  that is not sealed with the sealing material  71  is sealed with the second sealing material  72 . Also, the wiring member  4  is sealed with the second sealing material  72 . Since other configurations of the semiconductor device of the fifth embodiment are the same as the semiconductor device of the second embodiment, description thereof will be omitted. 
     &lt;Effects&gt; 
     In the fifth embodiment, the semiconductor element  1  has a rectangular shape in plan view, and the first sealing material  71  seals the four corners of the semiconductor element  1 , and the first sealing material  71  extends, of two pairs of the sides facing each other in plan view, along any one of the pairs of the sides facing each other. 
     Therefore, by the first sealing material  71  sealing both the four corners of the semiconductor element  1  and, of two pairs of the sides facing each other, any one of the pairs of the sides facing each other, the semiconductor element  1  can be firmly adhered and fixed to a heat dissipation plate  31  with a smaller amount of the sealing material compared to the case where the whole of the semiconductor element  1  is sealed with the first sealing material  71 . 
     Air is generally likely to be involved when a resin such as an epoxy resin is poured into a recess of a substrate in a manufacturing step. Therefore, there is the possibility that a void, i.e., a bubble may be formed in a sealed portion after the epoxy resin is cured. As measures against this, for example, the viscosity of the resin is lowered by warming the substrate in advance, which can suppress the involvement of air. Alternatively, a vacuuming mechanism is added, which can remove a void before curing. However, additional capital investment through equipment remodeling and addition of a manufacturing step are needed in any measure. Then, the first sealing material  71  is arranged only in the minimum required places in the opening  8 , as in the fifth embodiment, which can greatly reduce the amount of the first sealing material  71  to be used for sealing. By reducing the amount of the first sealing material  71  to be arranged, the possibility that a void may be formed in the first sealing material  71  can be reduced without additional capital investment and addition of a manufacturing step. 
     In the semiconductor device according to the fifth embodiment, the first sealing material  71  extends, of two pairs of the sides facing each other in plan view of the semiconductor element  1 , along a pair of the shorter sides facing each other. When the first sealing material  71  is arranged along the short sides facing each other, as illustrated in  FIG. 15 , the amount of the first sealing material  71  arranged is smaller compared to when the first sealing material  71  is arranged along the long sides facing each other. Therefore, the possibility that a void may be caused in the first sealing material  71  can be further reduced. Further, the four corners of the semiconductor element  1 , where stress is generated, are covered with the first sealing material  71 , and hence the reliability of the semiconductor device is sufficiently ensured. 
     Sixth Embodiment 
       FIG. 16  is a plan view of a semiconductor device according to a sixth embodiment. In  FIG. 16 , a second sealing material  72  and a cap  6  are illustrated by virtual lines for easy understanding of the drawing. In the fifth embodiment, the four corners and the short sides facing each other of the semiconductor element  1  are sealed with the first sealing material  71 . On the other hand, in the sixth embodiment, the four corners and the long sides facing each other of a semiconductor element  1  are sealed with a first sealing material  71 . Since other configurations of the semiconductor device of the sixth embodiment are the same as the semiconductor device of the fifth embodiment, description thereof will be omitted. 
     &lt;Effects&gt; 
     In the semiconductor device according to the sixth embodiment, the first sealing material  71  extends, of two pairs of the sides facing each other in plan view of the semiconductor element  1 , along a pair of the longer sides facing each other. In the sixth embodiment, the long sides facing each other are sealed with the first sealing material  71  instead of the short sides facing each other, and hence the semiconductor element  1  and a bonding material  2  can be held more firmly with a small amount of the first sealing material  71 . Therefore, a reduction in the possibility that a void may be generated in the first sealing material  71  and high reliability of the semiconductor device can be both achieved. 
     Seventh Embodiment 
       FIG. 17  is a plan view of a semiconductor device according to the seventh embodiment.  FIG. 18  is a cross sectional view of the semiconductor device according to the seventh embodiment. The cross section of the semiconductor device illustrated in  FIG. 18  is taken along line E-E of  FIG. 17 . In  FIG. 17 , a second sealing material  72  and a cap  6  are illustrated by virtual lines for easy understanding of the drawing.  FIG. 19  is a plan view schematically illustrating an air bridge existing area  100 . In  FIG. 19 , a first sealing material  71  is not illustrated. 
     In the fifth embodiment, the four corners and the short sides facing each other of the semiconductor element  1  are sealed with the first sealing material  71 , and in the sixth embodiment, the four corners and the long sides facing each other of the semiconductor element  1  are sealed with the first sealing material  71 . On the other hand, in the seventh embodiment, the four corners of a semiconductor element  1  are only sealed with the first sealing material  71 . 
     That is, in the semiconductor device of the seventh embodiment, the semiconductor element  1  has a rectangular shape in plan view, the first sealing material  71  seals the four corners of the semiconductor element  1 , the first sealing material  71  is discrete in each of the four corners of the semiconductor element  1 , and the first sealing material  71  is present in the four places. 
     The first sealing material  71  seals each of the four corners of the semiconductor element  1  such that each corner is not exposed. Also, the first sealing material  71  only seals the four corners of the semiconductor element  1 , the four corners being the minimum required places, and hence it is necessary that the first sealing material  71  is surely in contact with the semiconductor element  1 , a bonding material  2 , and a heat dissipation plate  31  in an opening  8 . 
     On the other hand, it is preferable that the first sealing material  71  seals such that it is not in contact with the air bridge existing area  100  illustrated in  FIG. 19 , in order to prevent the deterioration of high frequency characteristics as much as possible. Since the first sealing material  71  in the seventh embodiment is formed to be discrete in each of the four corners, it is not in contact with the air bridge existing area  100  between upper electrodes  91  and  92  and the semiconductor element  1  can be sealed with the first sealing material  71 . 
     The semiconductor element  1  to be used in a high frequency semiconductor device often has a rectangular shape, and hence the semiconductor element  1  is more likely to tilt along the longitudinal direction of the semiconductor element  1  after being die-bonded to form the bonding material  2 , compared to a square shape. 
       FIG. 20  is a plan view of a semiconductor device according to a variation of the seventh embodiment.  FIG. 21  is a cross sectional view of the semiconductor device according to the variation of the seventh embodiment. The cross section of the semiconductor device illustrated in  FIG. 21  is taken along line F-F of  FIG. 20 . In  FIG. 20 , a second sealing material  72  and a cap  6  are illustrated by virtual lines for easy understanding of the drawing. In the variation of the seventh embodiment, a structure is adopted, in which it is assumed that a semiconductor element  1  tilts along the longitudinal direction. 
     As illustrated in  FIGS. 20 and 21 , a structure is adopted, in which the bonding material  2  is provided such that, of two pairs of sides facing each other in plan view of the semiconductor element  1 , the thickness of the bonding material  2 , on one side of a pair of the shorter sides facing each other, is smaller than the thickness thereof on another side of the pair. That is, in the variation of the seventh embodiment, it is assumed that a structure is adopted, in which the bonding material  2  is provided such that, of the short sides facing each other in plan view of the semiconductor element  1 , the thickness of the bonding material  2 , on one side of the short sides, is smaller than the thickness thereof on the other side of the short sides. 
     In the seventh embodiment, the first sealing material  71  is formed to be isolated in the four corners of the semiconductor element  1  by a dispensing apparatus. That is, the first sealing material  71  is composed of two first sealing materials  711  and  711  and two first sealing materials  712  and  712 . And, as illustrated in  FIG. 21 , an application amount is changed between the first sealing materials  711  and  712 , corresponding to the tilt of the semiconductor element  1 . 
     As illustrated in  FIGS. 20 and 21 , of the four corners of the semiconductor element  1 , in two corners in each of which the bonding material  2 , which is a die-bonding layer, is formed to be relatively thin, a relatively large application amount of the first sealing material  712 , is provided, and in two corners in each of which the bonding material  2  is formed to be relatively thick, a relatively small application amount of the first sealing material  711  is provided, the application amount being a formation amount. 
     Thus, the variation of the seventh embodiment has the feature that the application amount of the first sealing material  712 , in each of the two corners on one side of the short sides, where the bonding material  2  is formed to be relatively thin, is larger than the application amount of the first sealing material  711  in each of the two corners on the other side of the short sides, where the bonding material  2  is formed to be relatively thick, the application amount being a formation amount. That is, in the variation of the seventh embodiment, the first sealing material  71  composed of the two first sealing materials  711  and the two first sealing materials  712  is provided such that the formation amount in each of the two corners on one side of the short sides is larger than the formation amount in each of the two corners on the other side of the short sides. 
     As a result, the thermal stress applied to the bonding material  2  between the first sealing materials  711  and  712  can be entirely balanced. It is also desirable that the height of the first sealing materials  711  and  712  is smaller than the formation height of an insulating layer  32 , and the first sealing materials  711  and  712  are contained in an opening  8 . The application amount of each of the first sealing materials  711  and  712  can be determined before being manufactured based on the thickness of the bonding material  2  in each corner, after approximate stress to be applied to the bonding material  2  is estimated in advance by using simulation or the like and then the stress is accurately predicted by a test using a real device since the stress applied to the bonding material  2  varies depending on the physical properties and size of each member. 
     Since other configurations of the semiconductor device of the seventh embodiment are the same as the semiconductor devices of the fifth embodiment and the sixth embodiment, description thereof will be omitted. 
     &lt;Effects&gt; 
     The semiconductor element to be used in a high frequency semiconductor device often has a rectangular shape in plan view, and hence the semiconductor element  1  is more likely to tilt along the longitudinal direction of the semiconductor element  1  after being die-bonded to form the bonding material  2 , compared to a square shape. Therefore, the thickness of the bonding material  2 , which is a die-bonding layer, varies also in the four corners of the semiconductor element  1 , as described above. Generally speaking, stress relaxation is large when the thickness of the bonding material  2  is large, and is small when the thickness of the bonding material  2  is small. Therefore, if the thickness of the bonding material  2  in the four corners of the semiconductor element  1  varies, the reliability on a thermal shock test in the four corners, or the like also varies, whereby the bonding material  2  may deteriorate from the weakest corner, so that the reliability is limited by the weakest corner. 
     Then, as illustrated in  FIG. 21 , by setting different application amounts of the first sealing materials  711  and  712  corresponding to the tilt of the semiconductor element  1 , i.e., to the thickness of the bonding material  2 , the stress relaxation in the four corners can be equalized, the application amounts being formation amounts. Thus, high reliability can be obtained. 
     In the seventh embodiment, the first sealing material  71  is provided to be isolated in each of the four corners of the semiconductor element  1 . Therefore, when it is assumed that a structure is adopted, in which the bonding material  2  is provided to have a different thickness in each of the four corners facing each other in plan view of the semiconductor element  1 , the application amount of the first sealing material  71  in each of the four corners of the semiconductor element  1  can be set to a different amount, corresponding to the thickness of the bonding material  2 . As a result, in the semiconductor device of the seventh embodiment, the stress relaxation of the bonding material  2  in the four corners can be equalized even when the bonding material  2  is provided to have a different thickness in each of the four corners. 
     In each of the first embodiment through the seventh embodiment, the first sealing material  71  may seal at least part of the semiconductor element  1  so as to be in directly contact with the semiconductor element  1 . The second sealing material  72  may seal the wiring member  4  so as to be in directly contact with the wiring member  4 . In the present invention, each embodiment can be freely combined or can be appropriately modified or omitted, within the scope of the present invention. 
     Although the present invention has been described in detail, the above description is an exemplification in all aspects, and the present invention is not limited thereto. It is understood that countless variations not illustrated can be conceived of without departing from the scope of the present invention.