Patent Publication Number: US-2022235076-A1

Title: Methods for making low bandgap perovskites

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
     This application claims priority from U.S. Provisional Patent Application No. 63/142,953 filed on Jan. 28, 2021, the contents of which are incorporated herein by reference in their entirety. 
    
    
     CONTRACTUAL ORIGIN 
     This invention was made with government support under Contract No. DE-AC36-08G028308 awarded by the Department of Energy. The government has certain rights in the invention. 
    
    
     BACKGROUND 
     Perovskite solar cells (PSCs) have emerged as a next generation photovoltaic (PV) technology, with the potential to displace many incumbent PV technologies in the future. The most efficient PSCs reported thus far are based on Pb-based halide perovskites, generally with bandgaps in a range between about 1.5 eV and about 1.7 eV. This bandgap range is substantially higher than that most suitable for single-junction solar cells, about 1.34 eV, according to the Shockley-Queisser (S-Q) calculation (˜1.34 eV), as well as for the bottom cell in all-perovskite tandem devices to go beyond the S-Q limit. Thus, there remains a need for new, lower bandgap perovskite compositions, and methods of making them, which will help enable the manufacture of high efficiency, stable PSCs on the industrial scale. 
     SUMMARY 
     An aspect of the present disclosure is a composition that includes a perovskite having a stoichiometry comprising A 1-x FA x Sn 1-y B y (I 1-z X z ) 3 , where A is a first cation, B is a second cation, X is a halide, and 0.5≤x≤0.9, 0.5≤y≤0.9, and 0≤z≤1. In some embodiments of the present disclosure, A may include at least one of cesium, guanidinium, and/or methylammonium. In some embodiments of the present disclosure, X may include at least one of bromide and/or chloride. In some embodiments of the present disclosure, z may be equal to zero. 
     In some embodiments of the present disclosure, the composition may be further characterized by a bandgap between about 1.1 eV and about 1.5 eV. In some embodiments of the present disclosure, the bandgap may be between about 1.3 eV and about 1.4 eV. In some embodiments of the present disclosure, the composition may be further characterized by at least one physical property having a characteristic value. In some embodiments of the present disclosure, the physical property may include a grain size with the characteristic value between about 300 nm and about 1500 nm. In some embodiments of the present disclosure, the grain size may be between about 750 nm and about 850 nm. In some embodiments of the present disclosure, the physical property may include a biaxial residual stress level with the characteristic value between about 0 MPa and about 100 MPa. In some embodiments of the present disclosure, the biaxial residual stress level may be between about 0 MPa and about 40 MPa. In some embodiments of the present disclosure, the physical property may include a dark carrier density with the characteristic value between about 1×10 13  cm −3  and about 1×10 17  cm −3 . In some embodiments of the present disclosure, the dark carrier density may be between about 5×10 14  cm −3  and about 5×10 16  cm −3 . In some embodiments of the present disclosure, the composition may include Cs 1-x FA x Sn 1-y Pb y I 3 . In some embodiments of the present disclosure, 0.6≤x≤0.8 and 0.6≤y≤0.8. 
     An aspect of the present disclosure is a method of making a perovskite, where the method includes combining a stoichiometric amount of at least one perovskite precursor that includes formamidinium (FA), tin, iodide, A, B, and X resulting in a mixture, adding an additive to the mixture, and treating the mixture. Further, the treating results in the forming of the perovskite having a stoichiometry comprising A 1-x FA x Sn 1-y B y (I 1-z X z ) 3 , where A is a first cation, B is a second cation, X is a halide, 0≤x≤1, 0≤y≤1, 0≤z≤1, and the additive includes FA and tin and at least one of fluoride and/or chloride. 
     In some embodiments of the present disclosure, the additive is added at a concentration between about 0.1 mol % and about 10 mol % relative to the stoichiometric amount. In some embodiments of the present disclosure, the concentration may be between about 0.1 mol % and about 5 mol %. In some embodiments of the present disclosure, the additive may include at least one of SnF 2 .xFACl or SnCl 2 .xFACl, where 1.5≤x≤4.5. In some embodiments of the present disclosure, 2.5≤x≤3.5. 
    
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
       Some embodiments are illustrated in referenced figures of the drawings. It is intended that the embodiments and figures disclosed herein are to be considered illustrative rather than limiting. 
         FIGS. 1A, 1B, and 1C  illustrate a perovskite, according to some embodiments of the present disclosure. 
         FIG. 2  illustrates 2D, 1D, and 0D perovskite structures, in Panels A, B, and C, respectively, according to some embodiments of the present disclosure. 
         FIG. 3A  illustrates UV-vis absorption spectra of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite thin films prepared with and without additives (5 mol %) as indicated, according to some embodiments of the present disclosure. 
         FIG. 3B  illustrates the Tauc plots corresponding to the UV-vis absorption spectra illustrated in  FIG. 3B  of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite thin films prepared with and without additives (5 mol %) as indicated, according to some embodiments of the present disclosure. 
         FIG. 4  illustrates a cross-sectional SEM image of a Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite solar cell made with SnCl 2 .3FACl additive (5 mol %), according to some embodiments of the present disclosure. 
         FIG. 5A  illustrates a comparison of typical J-V curves under 1-sun illumination for PSCs based on Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  thin films made with SnCl 2 .3FACl additive (5 mol %) and without (pristine) with both reverse scan (black symbols) and forward scan (lighter symbols), according to some embodiments of the present disclosure. Inset: SPO efficiencies. 
         FIG. 5B  illustrates a comparison of the corresponding EQE spectra for PSCs based on Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  thin films made with SnCl 2 .3FACl additive (5 mol %) and without (pristine) with both reverse scan (black symbols) and forward scan (lighter symbols), according to some embodiments of the present disclosure. 
         FIG. 5C  illustrates a comparison of PV-parameter statistics for PSCs made with SnCl 2 .3FACl additive (5 mol %) and without (pristine), according to some embodiments of the present disclosure. 
         FIG. 6  illustrates J-V curves of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite solar cells made without (pristine) and with 5 mol % SnCl 2 .xFACl additive (x=1.5, 3, and 4.5), according to some embodiments of the present disclosure. The SnCl 2 .3FACl and pristine devices are the same as shown in  FIGS. 5A and 5B , respectively. The SnCl 2 .1.5FACl device shows a PCE of 17.3% with a J sc  of 28.8 mA/cm 2 , V oc  of 0.765 V, and FF of 78.3%. The SnCl 2 .4.5FACl device shows a PCE of 15.8% with a J sc  of 28.6 mA/cm 2 , V oc  of 0.761 V, and FF of 72.7%. 
         FIG. 7  illustrates J-V curves of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite solar cells made without (pristine) and with SnCl 2 .3FACl with different concentrations as indicated, according to some embodiments of the present disclosure. The 5%-SnCl 2 .3FACl and pristine devices are the same as shown in  FIG. 5A . The 3%-SnCl 2 .3FACl device shows a PCE of 17.15% with a J sc  of 28.7 mA/cm 2 , V oc  of 0.770V, and FF of 77.6%. The 7%-SnCl 2 .3FACl device shows a PCE of 12.51% with a J sc  of 26.9 mA/cm 2 , V oc  of 0.728V, and FF of 63.9%. The 10%-SnCl 2 .3FACl device shows a PCE of 6.34% with a J sc  of 18.3 mA/cm 2 , V oc  of 0.554V, and FF of 62.5%. 
         FIG. 8  illustrates J-V curves of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite solar cells made without (pristine) and with different additives as indicated, according to some embodiments of the present disclosure. The 5%-SnCl 2 .3FACl and pristine devices were the same as shown in  FIGS. 1 , A and B, respectively. The 15%-FACl device shows a PCE of 16.2% with a J sc  of 28.2 mA/cm 2 , V oc  of 0.762 V, and FF of 75.5%. The 5%-SnCl 2  device shows a PCE of 10.1% with a J sc  of 24.4 mA/cm 2 , V oc  of 0.624 V, and FF of 66.1%. 
         FIG. 9A  illustrates a comparison of microstructure and physical properties of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite thin films with SnCl 2 .3FACl additive (5 mol %), Panel B, and without (pristine), Panel A, according to some embodiments of the present disclosure. Top-view SEM images (scale bar: 500 nm). 
         FIG. 9B  illustrates a comparison of indexed XRD patterns (* marks peaks from the underlying substrate) of perovskite films made with and without additive, according to some embodiments of the present disclosure. 
         FIGS. 9C, 9D, and 9E  illustrate a comparison of FET characterization of ‘dark’ carrier density, according to some embodiments of the present disclosure. 
         FIG. 10  illustrates a statistical comparison of apparent grain sizes for the pristine (no additive) and that made with SnCl 2 .3FACl additive (5 mol %), according to some embodiments of the present disclosure. 
         FIG. 11  illustrates an AFM analysis of a Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite thin film made with SnCl 2 .3FACl (5 mol %) additives, according to some embodiments of the present disclosure: Panel A topography; Panel B current. 
         FIG. 12A  illustrates current-voltage (I-V) curves of pristine, SnF 2 .3FACl, and SnCl 2 .3FACl (5 mol %) devices with 10-μm channel length (L ch ) under 1-V V DS  in the dark, inside a N 2 -filled glovebox, according to some embodiments of the present disclosure. 
         FIG. 12B  illustrates zoom-in view plots of current-voltage (I-V) curves illustrated in  FIG. 12A , according to some embodiments of the present disclosure. 
         FIG. 12C  illustrates FET transport curves of three types of perovskite devices under 1-V V DS  with the V GS  sweeping from +20 to −20 V with a fixed scanning rate 2.38 V/s in the dark, according to some embodiments of the present disclosure. 
         FIG. 12D  illustrates the calculated hole carrier densities of pristine, SnF 2 .3FACl, and SnCl 2 .3FACl perovskite samples, according to some embodiments of the present disclosure. 
         FIGS. 13A and 13B  illustrate comparisons of the XPS spectra of Sn3d core levels of perovskite thin films prepared without additive (pristine) and with 5% SnF 2 .3FACl or SnCl 2 .3FACl, according to some embodiments of the present disclosure. The Sn3d core levels show highly asymmetric peak shapes for the perovskite without additive, necessitating at least a two-component fit with a predominant contribution of a lower binding energy peak (˜486.1 eV), relative to the small fraction at high binding energy (˜487 eV). Inclusion of the 5% SnF 2 .3FACl showed a relative increase in the higher binding energy fraction, as evident by a reduction in the asymmetry of the Sn3d core levels and an increase in the overall full width half maximum of the peak, with maximum counts at 486.5 eV (see Table 2). Finally, use of the 5% SnCl 2 .3FACl additive showed a further increase in the higher binding energy component. 
         FIG. 14  illustrates XRD patterns of the Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite thin films prepared with SnCl 2 .3FACl (5 mol %), with SnF 2 .3FACl (5 mol %), and without additives, according to some embodiments of the present disclosure. 
         FIG. 15  illustrates J-V curves of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite solar cell made with SnF 2 .3FACl (5 mol %) additive), according to some embodiments of the present disclosure. The reverse-scan J-V curve yields a PCE of 17.1% with J sc  of 29.1 mA/cm 2 , V oc  of 0.765 V, and FF of 76.8%. The forward-scan J-V curve yields a PCE of 15.3% with a J sc  of 29.5 mA/cm 2 , V oc  of 0.756 V, and FF of 68.4%. The SPO efficiency is 16.6% (inset). 
         FIG. 16  illustrates a schematic of the XRD sin 2 ψ method for quantifying the residual stress in polycrystalline halide perovskite thin films, according to some embodiments of the present disclosure. 
         FIG. 17A  illustrates XRD d 220  vs. sin 2 ψ plots for the Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite thin films without (pristine) SnCl 2 .3FACl additive, according to some embodiments of the present disclosure. 
         FIG. 17B  illustrates XRD d 220  vs. sin 2 ψ plots for the Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite thin films with SnCl 2 .3FACl additive (5 mol %), according to some embodiments of the present disclosure. 
         FIG. 17C  illustrates a comparison of the residual stress in the Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite thin films without and with SnCl 2 .3FACl additive, according to some embodiments of the present disclosure. Five measurements per film were performed, and for each measurement both (D=0 and 90° orientations were used, indicating equi-biaxial state of the residual stress. 
         FIG. 17D  illustrates a schematic showing the proposed mechanism for reduced tensile residual stress (σ R ) using SnCl 2 .3FACl additive based on the supplementary results (see  FIGS. 19-21 ) from the film delamination tests), according to some embodiments of the present disclosure. (σ C  implies residual compression.) 
         FIG. 18  illustrates a statistical comparison of the residue stresses in the Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite thin films without additive, with SnF 2 .3FACl (5 mol %), and with SnCl 2 .3FACl (5 mol % additives), according to some embodiments of the present disclosure. Five measurements per film. 
         FIG. 19  illustrates an XRD comparison of perovskite films made by the methods described herein, according to some embodiments of the present disclosure. Pure perovskite phase formed immediately after the spin-coating process for both additive free (Panel A) and SnCl 2 .3FACl cases (Panel B). 
         FIG. 20  illustrates SEM images of the bottom and top fracture surfaces resulting from the delamination tests, according to some embodiments of the present disclosure. Three types of samples are shown: (Panels A, B) pristine; (Panels C, D) with SnF 2 .3FACl (5 mol %) additive; (Panels E, F) with SnCl 2 .3FACl (5 mol %) additive. 
         FIG. 21A  illustrates J-V curves (insets: corresponding SPOs) under 1-sun illumination of the Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3 -based champion PSC made with the SnCl 2 .3FACl additive (5 mol %), according to some embodiments of the present disclosure. 
         FIG. 21B  illustrates EQE spectra of the Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3 -based champion PSC made with the SnCl 2 .3FACl additive (5 mol %), according to some embodiments of the present disclosure. 
         FIG. 21C  illustrates MPP tracking of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  PSC made with the SnCl 2 .3FACl additive, under continuous 1-sun illumination, at about 45° C., in nitrogen atmosphere, according to some embodiments of the present disclosure. 
         FIG. 22  illustrates MPP tracking of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  PSCs made with SnF 2 .3FACl additive and without (pristine), under continuous 1-sun intensity illumination, at about 45° C., in nitrogen atmosphere, according to some embodiments of the present disclosure. 
         FIG. 23  illustrates UV-vis absorption spectrum and the corresponding Tauc plot (inset) of Cs 0.1 FA 0.9 Sn 0.3 Pb 0.7 I 3  perovskite thin film prepared with SnCl 2 .3FACl (5 mol %) additive, according to some embodiments of the present disclosure. The bandgap is ˜1.32 eV. 
         FIG. 24A  illustrates a J-V curve (insets: corresponding SPOs) under 1-sun illumination for a Cs 0.1 FA 0.9 Sn 0.3 Pb 0.7 I 3  based perovskite solar cell made with the SnCl 2 .3FACl additive (5 mol %), according to some embodiments of the present disclosure. 
         FIG. 24B  illustrates EQE spectra of the Cs 0.1 FA 0.9 Sn 0.3 Pb 0.7 I 3  PSC made with the SnCl 2 .3FACl additive (5 mol %), according to some embodiments of the present disclosure. 
         FIG. 24C  illustrates MPP tracking results measured under continuous 1-sun intensity illumination, at about 45° C. of the Cs 0.1 FA 0.9 Sn 0.3 Pb 0.7 I 3  PSC made with the SnCl 2 .3FACl additive (5 mol %), in a nitrogen atmosphere, according to some embodiments of the present disclosure. 
     
    
    
     DETAILED DESCRIPTION 
     The embodiments described herein should not necessarily be construed as limited to addressing any of the particular problems or deficiencies discussed herein. References in the specification to “one embodiment”, “an embodiment”, “an example embodiment”, “some embodiments”, etc., indicate that the embodiment described may include a particular feature, structure, or characteristic, but every embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an embodiment, it is submitted that it is within the knowledge of one skilled in the art to affect such feature, structure, or characteristic in connection with other embodiments whether or not explicitly described. 
     As used herein the term “substantially” is used to indicate that exact values are not necessarily attainable. By way of example, one of ordinary skill in the art will understand that in some chemical reactions 100% conversion of a reactant is possible, yet unlikely. Most of a reactant may be converted to a product and conversion of the reactant may asymptotically approach 100% conversion. So, although from a practical perspective 100% of the reactant is converted, from a technical perspective, a small and sometimes difficult to define amount remains. For this example of a chemical reactant, that amount may be relatively easily defined by the detection limits of the instrument used to test for it. However, in many cases, this amount may not be easily defined, hence the use of the term “substantially”. In some embodiments of the present invention, the term “substantially” is defined as approaching a specific numeric value or target to within 20%, 15%, 10%, 5%, or within 1% of the value or target. In further embodiments of the present invention, the term “substantially” is defined as approaching a specific numeric value or target to within 1%, 0.9%, 0.8%, 0.7%, 0.6%, 0.5%, 0.4%, 0.3%, 0.2%, or 0.1% of the value or target. 
     As used herein, the term “about” is used to indicate that exact values are not necessarily attainable. Therefore, the term “about” is used to indicate this uncertainty limit. In some embodiments of the present invention, the term “about” is used to indicate an uncertainty limit of less than or equal to ±20%, ±15%, ±10%, ±5%, or ±1% of a specific numeric value or target. In some embodiments of the present invention, the term “about” is used to indicate an uncertainty limit of less than or equal to ±1%, ±0.9%, ±0.8%, ±0.7%, ±0.6%, ±0.5%, ±0.4%, ±0.3%, ±0.2%, or ±0.1% of a specific numeric value or target. 
     Among other things, the present disclosure relates to the use of one or more additives during the formation of a perovskite, resulting in improved final physical properties and/or performance metrics of the finally formed perovskite. In addition to the improved quality of the finally formed perovskite, for the example of a film of perovskite, the residual stresses in films appear to play an important role in influencing both the stability and efficiency of perovskite solar cells (PSCs) incorporating the perovskite films. For example, as described herein, a novel tin (Sn)-halide-complex (SHC) additive, SnCl 2 .xFACl (where x is optimized to about 3 at a 5 mol % addition relative to the amount of SnI 2  provided in the formulation used to make the target perovskite composition), the residual stress was effectively reduced in an exemplary MA-free, Cs-FA-based Sn—Pb halide perovskite film of composition (FAPbI 3 ) 0.7 (CsSnI 3 ) 0.3  (or Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3 ) having a bandgap ˜1.34 eV (FA is formamidinium). As shown herein, it was determined that the SnCl 2 .3FACl additive enables the formation of a high-quality perovskite-substrate interface during room-temperature solution processing. The use of this exemplary additive also reduced the defect density by two orders of magnitude compared to identical perovskite synthesis in the absence of the additive (referred to herein as a “pristine” perovskite) and it further improved the structural and optoelectronic properties of the thin perovskite films. Using this approach, the power-conversion efficiency (PCE) values of the resulting PSCs approached nearly 20%, which to date, is the highest for MA-free Sn—Pb-based PSCs having a bandgap in the range of about 1.34 eV. In addition, a promising operational stability was demonstrated with greater than 80% of the initial PCE maintained after 750 hours under continuous operation at about 45° C. with maximum-power-point tracking under 1-sun illumination. 
       FIGS. 1A, 1B, and 1C  illustrate that perovskites  100 , for example halide perovskites, may organize into cubic crystalline structures with corner-sharing octahedra, as well as other crystalline structures such as tetragonal, hexagonal, and orthorhombic with either edge- or face-sharing octahedra, and may be described by the general formula ABX 3 , where X ( 130 ) is an anion and A ( 110 ) and B ( 120 ) are cations, typically of different sizes. In some embodiments of the present disclosure, a perovskite may have a layered structure that includes 3D structures described above positioned between sheets of organic cations; these are often termed 2D perovskites. Mixture of the 2D and 3D phases are also possible.  FIG. 1A  illustrates that a perovskite  100  may be organized into eight octahedra surrounding a central A-cation  110 , where each octahedra is formed by six X-anions  130  surrounding a central B-cation  120 .  FIG. 1B  illustrates that a perovskite  100  may be visualized as a cubic unit cell, where the B-cation  120  is positioned at the center of the cube, an A-cation  110  is positioned at each corner of the cube, and an X-anion  130  is face-centered on each face of the cube.  FIG. 1C  illustrates that a perovskite  100  may also be visualized as a cubic unit cell, where the B-cation  120  resides at the eight corners of a cube, while the A-cation  110  is located at the center of the cube and with 12 X-anions  130  centrally located between B-cations  120  along each edge of the unit cell. For both unit cells illustrated in  FIGS. 1B and 1C , the A-cations  110 , the B-cations  120 , and the X-anions  130  balance to the general formula ABX 3 , after accounting for the fractions of each atom shared with neighboring unit cells. For example, referring to  FIG. 1B , the single B-cation  120  atom is not shared with any of the neighboring unit cells. However, each of the six X-anions  130  is shared between two unit cells, and each of the eight A-cations  110  is shared between eight unit cells. So, for the unit cell shown in  FIG. 1B , the stoichiometry simplifies to B=1, A=8*0.125=1, and X=6*0.5=3, or ABX 3 . Similarly, referring again to  FIG. 1C , since the A-cation is centrally positioned, it is not shared with any of the unit cells neighbors. However, each of the 12 X-anions  130  is shared between four neighboring unit cells, and each of the eight B-cations  120  is shared between eight neighboring unit cells, resulting in A=1, B=8*0.125=1, and X=12*0.25=3, or ABX 3 . Referring again to  FIG. 1C , the X-anions  130  and the B-cations  120  are shown as aligned along an axis; e.g., where the angle at the X-anion  130  between two neighboring B-cations  120  is exactly 180 degrees, referred to herein as the tilt angle. However, a perovskite  100  may have a tilt angle not equal to 180 degrees. For example, some embodiments of the present disclosure may have a tilt angle between 153 and 180 degrees. 
     Typical inorganic perovskites include calcium titanium oxide (calcium titanate) minerals such as, for example, CaTiO 3  and SrTiO 3 . In some embodiments of the present invention, the A-cation  110  may include a nitrogen-containing organic compound such as an alkyl ammonium compound. The B-cation  120  may include a metal and the X-anion  130  may include a halogen. Additional examples for the A-cation  110  include organic cations and/or inorganic cations, for example Cs, Rb, K, Na, Li, and/or Fr. Organic A-cations  110  may be an alkyl ammonium cation, for example a C 1-20  alkyl ammonium cation, a C 1-6  alkyl ammonium cation, a C 2-6  alkyl ammonium cation, a C 1-5  alkyl ammonium cation, a C 1-4  alkyl ammonium cation, a C 1-3  alkyl ammonium cation, a C 1-2  alkyl ammonium cation, and/or a C 1  alkyl ammonium cation. Further examples of organic A-cations  110  include methylammonium (CH 3 NH 3   + ), ethylammonium (CH 3 CH 2 NH 3   + ), propylammonium (CH 3 CH 2 CH 2 NH 3   + ), butylammonium (CH 3 CH 2 CH 2 CH 2 NH 3   + ), formamidinium (NH 2 CH═NH 2   + ), hydrazinium, acetylammonium, dimethylammonium, imidazolium, guanidinium, benzylammonium, phenethylammonium, butylammonium and/or any other suitable nitrogen-containing or organic compound. In other examples, an A-cation  110  may include an alkylamine. Thus, an A-cation  110  may include an organic component with one or more amine groups. For example, an A-cation  110  may be an alkyl diamine halide such as formamidinium (CH(NH 2 ) 2 ). Thus, the A-cation  110  may include an organic constituent in combination with a nitrogen constituent. In some cases, the organic constituent may be an alkyl group such as straight-chain or branched saturated hydrocarbon group having from 1 to 20 carbon atoms. In some embodiments, an alkyl group may have from 1 to 6 carbon atoms. Examples of alkyl groups include methyl (C 1 ), ethyl (C 2 ), n-propyl (C 3 ), isopropyl (C 3 ), n-butyl (C 4 ), tert-butyl (C 4 ), sec-butyl (C 4 ), iso-butyl (C 4 ), n-pentyl (C 5 ), 3-pentanyl (C 5 ), amyl (C 5 ), neopentyl (C 5 ), 3-methyl-2-butanyl (C 5 ), tertiary amyl (C 5 ), and n-hexyl (C 6 ). Additional examples of alkyl groups include n-heptyl (C 7 ), n-octyl (C 8 ) and the like. 
     Examples of metal B-cations  120  include, for example, lead, tin, germanium, and or any other 2+ valence state metal that can charge-balance the perovskite  100 . Further examples include transition metals in the 2+ state such as Mn, Mg, Zn, Cd, and/or lanthanides such as Eu. B-cations may also include elements in the 3+ valence state, as described below, including for example, Bi, La, and/or Y. Examples for X-anions  130  include halogens: e.g., fluorine, chlorine, bromine, iodine and/or astatine. In some cases, the perovskite halide may include more than one X-anion  130 , for example pairs of halogens; chlorine and iodine, bromine and iodine, and/or any other suitable pairing of halogens. In other cases, the perovskite  100  may include two or more halogens of fluorine, chlorine, bromine, iodine, and/or astatine. 
     Thus, the A-cation  110 , the B-cation  120 , and X-anion  130  may be selected within the general formula of ABX 3  to produce a wide variety of perovskites  100 , including, for example, methylammonium lead triiodide (CH 3 NH 3 PbI 3 ), and mixed halide perovskites such as CH 3 NH 3 PbI 3-x Cl x  and CH 3 NH 3 PbI 3-x Br x . Thus, a perovskite  100  may have more than one halogen element, where the various halogen elements are present in non-integer quantities; e.g., x is not equal to 1, 2, or 3. In addition, perovskite halides, like other organic-inorganic perovskites, can form three-dimensional (3-D), two-dimensional (2-D), one-dimensional (1-D) or zero-dimensional (0-D) networks, possessing the same unit structure. As described herein, the A-cation  110  of a perovskite  100 , may include one or more A-cations, for example, one or more of cesium, FA, MA, etc. Similarly, the B-cation  120  of a perovskite  100 , may include one or more B-cations, for example, one or more of lead, tin, germanium, etc. Similarly, the X-anion  130  of a perovskite  100  may include one or more anions, for example, one or more halogens (e.g., at least one of I, Br, Cl, and/or F), thiocyanate, and/or sulfur. Any combination is possible provided that the charges balance. 
     For example, a perovskite having the basic crystal structure illustrated in  FIGS. 1A-1C , in at least one of a cubic, orthorhombic, and/or tetragonal structure, may have other compositions resulting from the combination of the cations having various valence states in addition to the 2+ state and/or 1+ state described above for lead and alkyl ammonium cations; e.g., compositions other than AB 2+ X 3  (where A is one or more cations, or for a mixed perovskite where A is two or more cations). Thus, the methods described herein may be utilized to create novel mixed cation materials having the composition of a double perovskite, A 2 B 1+ B 3+ X 6 , with an example of such a composition being Cs 2 BiAgCl 6  and Cs 2 CuBiI 6 . Another example of a composition covered within the scope of the present disclosure is described by A 2 B 4+  X 6 , for example Cs 2 PbI 6  and Cs 2 SnI 6 . Yet another example is described by A 3 B 2   3+ X 9 , for example Cs 3 Sb 2 I 9 . For each of these examples, A is one or more cations, or for a mixed perovskite, A is two or more cations. 
     In addition, perovskite halides, like other organic-inorganic perovskites, can form a three-dimensional (3D) network, a two-dimensional (2D) network, a one-dimensional (1D) network and/or a zero-dimensional (0D) network, possessing the same unit structure. A perovskite&#39;s 3D network is illustrated in  FIGS. 1A, 1B, and 1C .  FIG. 2  illustrates a 2D perovskite network, a 1D perovskite network, and a 0D perovskite network, in Panels A, B, and C, respectively. As described above, a 3D perovskite may adopt a general chemical formula of ABX 3 , in which the A-cation may be a monovalent cation (e.g., methylammonium and/or formamidinium CH(NH 2 ) 2   + ), the B-cation may be a divalent cation (e.g., Pb 2+  and/or Sn 2+ ), and the X-anion may be a halide anion (I − , Br − , and/or Cl − ). In this formula, the 3D network of perovskites may be constructed by linking all corner sharing BX 6  octahedra, with the A-cation filling the space between eight octahedral unit cells to balance the crystal charge. 
     Referring to Panel A of  FIG. 2 , through the chemically accomplished dimensional reduction of the 3D crystal lattice, 2D perovskites, (A′) m (A) n-1 B n X 3n+1 , may adopt a new structural and compositional dimension, A′ (not shown), where monovalent (m=2) or divalent (m=1) cations can intercalate between the X-anions of the 2D perovskite sheets. Referring to Panel B of  FIG. 2 , 1D perovskites are constructed by BX 6  octahedral chained segments spatially isolated from each other by surrounding bulky organic cations (not shown), leading to bulk assemblies of paralleled octahedral chains. Referring to Panel C of  FIG. 2 , typically, the 0D perovskites are constructed of isolated inorganic octahedral clusters and surrounded by small cations (not shown) which are connected via hydrogen bonding. 
     Sn—Pb PSCs with SnCl 2 .3FACl additive. An exemplary MA-free perovskite composition of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  was chosen, partially for its favorable bandgap of about 1.34 eV (see  FIGS. 3A and 3B ) and to avoid the possible deleterious effect of MA +  volatility, which may limit the long-term operational stability of PSCs. A new method was utilized for fabricating perovskite films in the presence of SnCl 2 .3FACl. Briefly, a stoichiometric perovskite precursor solution with about 5 mol % excess SnCl 2 .3FACl additive was spin-coated, followed by thermal annealing. The exemplary PSC device stacks tested were prepared with an “inverted” device structure comprising glass/ITO/PEDOT:PSS/perovskite/C60/BCP/Ag, which corresponds to substrate/current collector/hole transport layer (PEDOT:PSS)/active layer/electron transport layer (C60/BCP)/current collector. The cross-sectional SEM image of this exemplary device stack is shown in  FIG. 4 . Note: An additive&#39;s molar ratio was calculated relative to the amount of SnI 2  molar amounts in a given recipe. For example, 5 mol % of SnCl2-3FACl additive means 5% of excess Sn and 15% of excess FA relative to SnI 2  used in this precursor. The 0.3 of Sn in Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  was based on the amount of SnI 2 . The amount of additive was not considered in the stoichiometry calculation. “Stoichiometric” and “stoichiometric amount” refers to adding the specific molar amounts/ratios to attain the desired final perovskite composition. For example, to obtain Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3 , one would mix 0.3 moles of Cs, 0.7 moles of FA, 0.3 moles of tin, 0.7 moles of lead, and three moles of iodine. 
     The typical current density-voltage (J-V) curves, and the corresponding external quantum efficiency (EQE) spectra, for PSCs made with and without the SnCl 2 .3FACl additive are shown in  FIGS. 5A and 5B , respectively. The PSC made with SnCl 2 .3FACl additive shows a reverse-scan PCE of 18.3% with a short-circuit current density (J SC ) of 29.1 mA/cm 2 , an open-circuit voltage (V OC ) of 0.787 V, and a fill factor (FF) of 79.9%. The forward scan of the same device shows a PCE of 17.6% and the stabilized power output (SPO; see  FIG. 5A , inset) efficiency is 18.3%. For comparison, the PSC without the SnCl 2 .3FACl additive shows a PCE of 14.7% for reverse scan, 13.1% for forward scan, and SPO efficiency of 14.2%. The detailed device parameters are given in Table 1. The significant improvement in device performance can be attributed largely to the higher V OC  and FF. All these observations are statistically reproducible based on PV parameters from 20 devices for each device condition (see  FIG. 5C ). There is a negligible impact of the additive on J SC , which is consistent with the device EQE spectra (see  FIG. 5B ) and the optical absorption results (see  FIGS. 3A and 3B ). The slight increase of the bandgap achieved with the use of the SnCl 2 .3FACl additive is consistent with the blue shift of the onset of the EQE spectrum on the long wavelength side. However, there is also a slight change of the EQE spectra in the shorter wavelength range. These changes are relatively small with opposite effects, leading to comparable J SC  values in the two devices. 
     
       
         
           
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                 J-V parameters of perovskite solar cells based on Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3   
               
               
                 perovskite films made without additives (pristine), with SnCl 2 •3FACl  
               
               
                 (5 mol %), and with SnF 2 • 3FACl (5 mol %) additives. 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                   
                 J sc   
                 V oc   
                 FF 
                 PCE 
                 SPO 
               
               
                 Device 
                   
                 (mA/cm 2 ) 
                 (V) 
                 (%) 
                 (%) 
                 (%) 
               
               
                   
               
               
                 Pristine 
                 Reverse 
                 29.4 
                 0.706 
                 70.6 
                 14.7 
                 14.2 
               
               
                   
                 Forward 
                 29.1 
                 0.689 
                 65.2 
                 13.1 
                   
               
               
                 SnF 2 •3FACl 
                 Reverse 
                 29.1 
                 0.765 
                 76.8 
                 17.1 
                 16.6 
               
               
                   
                 Forward 
                 29.5 
                 0.756 
                 68.4 
                 15.3 
                   
               
               
                 SnCl 2 •3FACl 
                 Reverse 
                 29.1 
                 0.787 
                 79.9 
                 18.3 
                 18.3 
               
               
                   
                 Forward 
                 29.5 
                 0.784 
                 75.9 
                 17.6 
               
               
                   
               
            
           
         
       
     
     Note that the PSCs prepared with the SnCl 2 .xFACl additive, with x ranging from 1.5 to 4.5, all showed enhanced device performance compared to the PSCs without the additive (see  FIG. 6 ), but x=3 resulted in the highest performance improvement. In addition, about 5 mol % of SnCl 2 .3FACl (i.e., x about 3) addition was found to provide the best result (see  FIG. 7 ). The best value of x equal to about 3, i.e., SnCl 2 .˜3FACl, corresponds to a maximum; both x less than about 3 and x more than about 3 resulted in reduced device performances. So, the device performance versus the stoichiometry of SnCl 2  to FACl was not just a simple linear relationship. In addition, it can be seen that the large performance improvements were more than what would be expected from the simple additive effects of the individual additive components, i.e., SnCl 2  and FACl (see  FIG. 8 ). Further, referring again to  FIG. 7 , the best value of about 5 mol % of SnCl 2 .3FACl corresponds to a maximum; both less than about 5 mol % and more than about 5 mol % of the additive resulted in reduced device performances. So, the device performance versus additive concentration was not just a simple linear relationship. 
     Physical properties of pristine and SnCl 2 .3FACl-added Sn—Pb perovskites. To understand the origin of the significantly improved device performance associated with using the SnCl 2 .3FACl additive (5 mol %), a set of physical and optoelectronic properties of the films were characterized. The top-view scanning electron microscope (SEM) images in  FIG. 9A  show that the apparent grain size increased from a few hundred nanometers to about a micron with the additive. The statistical distribution of the apparent grain sizes of the pristine sample and that made with the SnCl 2 .3FACl additive are further compared in  FIG. 10 . This can be attributed to the FACl component in the additive in facilitating the grain-boundary migration during the film growth. The indexed X-ray diffraction (XRD) patterns in  FIG. 9B  confirm the pure perovskite phase in both films, with and without SnCl 2 .3FACl additive, but the film with the additive demonstrates about a 10-fold increase in the intensity on the same scale, and a 20% reduction in the FWHM (full width at half maximum) of the 100 peak, which indicates improved crystallinity. Furthermore, the SnCl 2 .3FACl additive may passivate the grain boundaries by decorating them with SnCl 2  via a thermal decomposition process. The grain-boundary passivated microstructure was confirmed using conductive atomic force microscopy as shown in  FIG. 11 , where the grain boundaries are coated continuously with less conductive SnCl 2  phases. The electrical measurement based on a field-effect transistor (FET) configuration shows that the “dark” carrier density of the films was reduced by two orders of magnitude with the use of SnCl 2 .3FACl additive (see  FIGS. 9C-9E  and  FIGS. 12A-12D ), which is indicative of a very low defect density in that film. These results correlate well with X-ray photoelectron spectroscopy (XPS) analysis of the corresponding perovskite films (see  FIGS. 13A and 13B  and Table 2). 
     
       
         
           
               
             
               
                 TABLE 2 
               
             
            
               
                   
               
               
                 XPS analysis of perovskite films prepared with and without using additives. 
               
            
           
           
               
               
               
               
               
            
               
                   
                   
                   
                 Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  + 
                 Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  + 
               
            
           
           
               
               
               
               
            
               
                   
                 Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3   
                 5% SnF 2 •3FACl 
                 5% SnCl 2 •3FACl 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                   
                 Binding 
                   
                 Binding 
                   
                 Binding 
               
               
                   
                   
                 Energy (eV) 
                   
                 Energy (eV) 
                   
                 Energy (eV) 
               
               
                 Elemental 
                   
                 at Maximum 
                   
                 at Maximum 
                   
                 at Maximum 
               
               
                 region 
                 Atomic % 
                 Counts 
                 Atomic % 
                 Counts 
                 Atomic % 
                 Counts 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 Pb4f 7/2   
                 11.2 
                 137.8 
                 14.5 
                 138.0 
                 13.8 
                 138.0 
               
               
                 Cs3d 5/2   
                 4.2 
                 724.5 
                 4.6 
                 724.5 
                 4.6 
                 724.5 
               
               
                 N1s* 
                 23.8 
                 400.1 
                 16.5 
                 400.1 
                 17.7 
                 400.2 
               
               
                 Sn3d 5/2   
                 5.1 
                 486.1 
                 9.4 
                 486.5 
                 9.3 
                 486.4 
               
               
                 I3d 5/2   
                 55.8 
                 618.8 
                 49.9 
                 618.9 
                 48.1 
                 618.9 
               
               
                 Cl2p 3/2   
                 undetectable 
                 NA 
                 5.2 
                 198.3 
                 6.5 
                 198.1 
               
               
                 F1s 
                 undetectable 
                 NA 
                 undetectable 
                 NA 
                 undetectable 
                 NA 
               
               
                   
               
               
                 *N1s used to infer FA (only one peak). 
               
            
           
         
       
     
     The improved microstructure and crystallinity of perovskite films are often important factors that contribute to enhancing PSC performance. In this context, another set of Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite films and devices were prepared using a different additive, SnF 2 .3FACl (5 mol %). In comparison with the pristine films without any additive, the use of SnF 2 .xFACl additive also enhanced the crystallinity (see  FIG. 14 ) and apparent grain size significantly, to a degree similar to that observed in the SnCl 2 .3FACl additive case. The optical bandgap and absorption are also similar for films prepared using SnCl 2 .3FACl and SnF 2 .3FACl additives (see  FIGS. 3A and 3B ). However, the SnF 2 .3FACl-additive-based film exhibited about 3-fold higher dark carrier density (see  FIGS. 12A-12D ), compared to the SnCl 2 .3FACl-additive-based film. Furthermore, the SnF 2 .3FACl-additive-based device only reached an SPO efficiency of about 16.6% (see  FIG. 15  and Table 1), which is higher than the pristine device (14.2%, see  FIG. 5A ), but is significantly lower than the SnCl 2 .3FACl-additive device (18.3%, see  FIG. 5A ). These results indicate that improved morphology and crystallinity alone may not be sufficient to account for the significant improvements in the PSC performance observed using the SnCl 2 .3FACl-additive. 
     Strain relaxation due to SnCl 2 .3FACl additive. Recently can affect charge transport and chemical stability of perovskite films. There is often a biaxial tensile residual stress in solution-processed perovskite films, associated with the film formation process and the coefficient of thermal expansion (CTE) mismatch between the film and the substrate. In general, such strain is detrimental to PSC operation as it can increase charge recombination, decrease perovskite stability, and reduce mechanical reliability. In order to evaluate the possible effect of residual stress, Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite films without additive (pristine) and with the SnCl 2 .3FACl additive (5 mol %) were characterized using the well-established XRD sin 2 ψ method, as illustrated in  FIG. 16 . In  FIGS. 17A and 17B , (220) interplanar spacing (d 220 ) is plotted as a function of sin 2 ψ for Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite films without and with the SnCl 2 .3FACl additive, respectively. A positive slope of the linear fit to the d 220 −sin 2 ψ data for the pristine film indicates the presence of biaxial tensile residual stress (or strain). In contrast, the film synthesized with the SnCl 2 .3FACl additive shows a much lower positive slope. The biaxial residual stress (GR) can be estimated from the sin 2  ψ data in  FIGS. 17A and 17B  using the relation: 
     
       
         
           
             
               
                 
                   
                     
                       σ 
                       R 
                     
                     = 
                     
                       
                         ( 
                         
                           
                             E 
                             
                               〈 
                               220 
                               〉 
                             
                           
                           
                             1 
                             + 
                             v 
                           
                         
                         ) 
                       
                       ⁢ 
                       
                         ( 
                         
                           m 
                           
                             d 
                             n 
                           
                         
                         ) 
                       
                     
                   
                   , 
                 
               
               
                 
                   ( 
                   1 
                   ) 
                 
               
             
           
         
       
     
     where m is the slope of the linear fit to the data, d a  is the d 220  spacing at sin 2  ψ=0 (y-intercept), E &lt;220&gt;  is the Young&#39;s modulus in the &lt;220&gt; direction, and v is the Poisson&#39;s ratio. E &lt;220&gt;  is estimated as 18.5 GPa, as shown in the Supplementary Materials. The typical v value of 0.33 is assumed. The calculated residual stresses for Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  perovskite films with and without SnCl 2 .3FACl additive are presented in  FIG. 17C . Overall, the tensile GR in the pristine film (i.e., no additive used in its synthesis) is estimated at 42-51 MPa, which is reduced to only 19-24 MPa for the SnCl 2 .3FACl case. In addition, it was found that replacing the SnCl 2 .3FACl additive with SnF 2 .3FACl can also reduce the residual stress to some extent, but not as much as SnCl 2 .3FACl (see  FIG. 18 ). Based on these results, the reduced residual stresses in the film associated with the SnCl 2 .3FACl additive is likely to be an important factor contributing to the exceptional device performance, in addition to the microstructural considerations. 
     To elucidate the possible mechanisms responsible for the low residual stresses due to the SnCl 2 .3FACl additive mechanical delamination tests were performed. Residual stresses in perovskite films typically develop when the perovskite phase crystallizes from the as-spun film during the thermal annealing process, where the perovskite film attaches to the substrate at high temperatures and is subsequently cooled down. The significantly higher CTE of perovskite compared to that of glass results in the tensile nature of the residual stresses in the film after cooling (see  FIG. 17D ). It was determined that the pure perovskite phase formed immediately after the spin-coating process (without heat-treatment) both without and with the SnCl 2 .3FACl additive (see  FIG. 19 ). However, the structural integrity of the perovskite-substrate interface during this stage is strikingly different. In the additive-free case, it is found that the delamination occurs primarily at the perovskite-substrate interface, whereas the film fractures within the bulk film in the SnCl 2 .3FACl additive case (see  FIG. 20 ). This indicates that the SnCl 2 .3FACl additive promotes the bonding between the perovskite film and the substrate before heating, reducing the development of residual stresses upon the subsequent heating-cooling cycle. This proposed mechanism is illustrated schematically in  FIG. 17D . 
     Composition-specific performance and stabilities of Sn—Pb PSCs with SnCl 2 .3FACl additives.  FIG. 21A  shows the J-V curves of the champion device based on Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  using the additive SnCl 2 .xFACl (x=3). It shows a PCE of 19.3% in reverse scan, 18.5% in forward scan, and SPO efficiency of 19.1% (see  FIG. 21A , inset). The detailed PV parameters are shown in Table 3. The EQE spectra along with the integrated J SC  are shown  FIG. 21B , where the latter is 28.3 mA/cm 2 , which is within 3% −4 % of the J-V measurement. To test the impact of the SnCl 2 .3FACl additive on the device stability, the continuous operation (see  FIG. 21C ) with maximum-power-point (MPP) tracking of unencapsulated Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  devices under 1-sun illumination was evaluated, in nitrogen atmosphere, with ambient temperature of about 45° C. (ISOS-L-1 stability). A comparison of the pristine device to the SnF 2 .3FACl-additive-based device (see  FIG. 22 ) illustrates that the SnCl 2 .3FACl-additive-based device showed much improved operational stability with a T80 of about 750 hours, where T80 refers to the duration at 80% retention of the initial PCE. This continuous 1-sun operation stability is approaching that for PSCs based on Pb-only, and it represents the best reported operational stability for high-efficiency (19-20%) Sn—Pb ideal-bandgap PSCs. It is worth pointing out that the T90 is ˜690 hours in  FIG. 21C . The observed increasing degradation rate starting at ˜650 hours is likely associated with the use of the Ag contact, which can migrate to induce degradation. PEDOT:PSS is also known to cause device degradation in Sn—Pb PSCs. Thus, contact layer optimization strategies are expected to further increase the device stability in the future. 
     
       
         
           
               
             
               
                 TABLE 3 
               
             
            
               
                   
               
               
                 J-V parameters of champion perovskite solar cells based on  
               
               
                 Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  and Cs 0.1 FA 0.9 Sn 0.3 Pb 0.7 I 3  perovskite films  
               
               
                 made with SnCl 2 •3FACl (5 mol %) additive. 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                   
                 J sc   
                 V oc   
                 FF 
                 PCE 
                 SPO 
               
               
                 Device 
                   
                 (mA/cm 2 ) 
                 (V) 
                 (%) 
                 (%) 
                 (%) 
               
               
                   
               
               
                 Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3    
                 Reverse 
                 29.4 
                 0.804 
                 81.8 
                 19.3 
                 19.1 
               
               
                   
                 Forward 
                 29.5 
                 0.788 
                 79.7 
                 18.5 
                   
               
               
                 Cs 0.1 FA 0.9 Sn 0.3 Pb 0.7 I 3   
                 Reverse 
                 30.2 
                 0.825 
                 80.1 
                 20.0 
                 19.5 
               
               
                   
                 Forward 
                 30.1 
                 0.823 
                 78.8 
                 19.5 
               
               
                   
               
            
           
         
       
     
     Finally, the effect of tuning the cesium content on device performance was tested. By reducing the cesium content to 10%, the resulting perovskite Cs 0.1 FA 0.9 Sn 0.3 Pb 0.7 I 3  had a bandgap of ˜1.32 eV (see  FIG. 23 ), which is also near the ideal bandgap (˜1.34 eV) for single-junction devices.  FIGS. 24A, 24B, and 24C  illustrate the device characteristics of the champion Cs 0.1 FA 0.9 Sn 0.3 Pb 0.7 I 3  device by using the SnCl 2 .3FACl additive (5 mol %). The device efficiency was slightly higher (SPO=19.5%; Table 3), but the stability was slightly reduced to a T80 of ˜430 hours, compared to Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  devices. These results suggest that adjusting/improving Sn—Pb perovskite absorber layer is important for enhancing Sn—Pb perovskite device efficiency and stability. These results also indicate the importance of not only improving the thin-film microstructure but also reducing residual stresses in Sn—Pb film when developing Sn—Pb-based ideal-bandgap PSCs having simultaneously high PCE and long operational stability. 
     Perovskite Precursor Preparation 
     All the perovskite solution and films depositions were conducted in a N 2  glovebox with 02 level&lt;1 ppm, H 2 O&lt;1 ppm. A “baseline” perovskite, Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3 , was prepared by making a solution by mixing 76.1 mg FAI (Greatcell, Australia), 203.9 mg PbI 2  (anhydrous, Sigma-Aldrich, USA), 49.3 mg CsI (anhydrous, Sigma-Aldrich, USA), and 70.7 mg SnI 2  (anhydrous, bead, Sigma-Aldrich, USA) in 263 μl DMF (anhydrous, Sigma-Aldrich, USA) and 88 μl DMSO (anhydrous, Sigma-Aldrich). For preparing SnF 2 .3FACl or SnCl 2 .3FACl additives, SnF 2  (Sigma-Aldrich, USA) or SnCl 2  (Sigma-Aldrich, USA) were mixed with FACl powders in a molar ratio of 1:3 in a DMF solvent, followed by a drying process using rotary evaporator. The SnF 2 .3FACl or SnCl 2 .3FACl additives were added to the perovskite precursor with different molar ratios relative to the SnI 2  molar amounts. For example, the precursor with 5 mol % SnCl 2 .3FACl additive was prepared by adding 4.1 mg SnCl 2 .3FACl into the abovementioned baseline perovskite precursor solution. 
     Device Fabrication 
     The prepatterned ITO substrates were sequentially cleaned three times by ultrasonication in acetone and isopropanol (a first treatment in a first mixture of acetone, followed by a second treatment in a second mixture of IPA, this sequence repeated three times). The ITO/glass substrates were then dried with N 2  gun and UV-ozone treated for 15 minutes. The PEDOT:PSS (CLEVIOS™ P VP Al 4083, filtered through a 0.45 m Nylon filter) were spin coated onto ITO substrates at 3000 rpm for 30 seconds and annealed on a hot plate at 150° C. for 30 minutes in air. After that, the substrates were transferred to a nitrogen glovebox (02 level&lt;1 ppm, H 2 O&lt;1 ppm) to prepare the Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3 . The perovskite films were deposited by spin-coating the solution as described above at 5000 rpm for 60 s. N 2  stream was blown over the spinning substrate for 30 s during the spinning procedure to assist the formation of perovskite film. Films were then annealed at 150° C. for 15 minutes. Finally, C60 (25 nm)/Bathocuproine (6 nm)/Ag (120 nm) were sequentially deposited by thermal evaporation to complete the PSC devices. 
     Materials Characterization 
     X-ray diffraction (XRD) was performed using an X-ray diffractometer (D-8 Discover, Bruker, Germany) with Cu Kα1 radiation (λ=1.5406 Å) at a step size of 0.02°. XRD patterns for the confirmation of the perovskite phase were collected using a Ge (002) monochrometer, at a step time of 2 s. Diffraction patterns were collected as a function of θ angle of the film, using two different orthogonal orientations (φ=0° and 90°) for confirming the isotropic nature of the residue stresses. The d-spacings (220) for the well-defined XRD peaks at the highest 2q angle (˜40.6°) were used to generate the sin 2 ψ plots. Time-integrated photoluminescence spectra were excited at 405 nm and measured with a CCD camera. X-ray photoelectron spectroscopy (XPS) was performed with a Kratos Axis Ultra X-ray photoelectron spectrometer with a monochromatic Al Kα source (1486.6 eV) at a base pressure of 10 −9  Torr. Photoelectrons were collected in a hemispherical analyzer and detected with a photodiode array. A 20-eV pass energy was used for all element specific spectral acquisitions. Resulting XPS spectra were first baseline corrected using linear subtraction methods for acquired Sn3d, Cl2p, and F1s spectra, and with Shirley baseline corrections for Pb4f, Cs3d, N1s, and I3d spectra. The Sn3d spectra were fit using a 30% Gaussian, 70% Lorentzian peak shape, with spin orbit coupling constrained using energetic separations of 8.4 eV, peak ratios of 3:2 (Sn3d 5/2 :Sn3d 3/2 ), and equivalent FWHMs with an average of 1.03 eV±0.11 eV between samples. 
     SEM and Optical Absorbance 
     The morphologies and microstructures of the prepared perovskite films and the cross-sectional structures and thickness of the solar cells were investigated using a field-emission scanning electron microscopy (FESEM, Nova 630 NanoSEM, FEI). The optical absorbance spectra of perovskite films were measured using an ultraviolet-visible (UV-vis) spectrophotometer (Cary-6000i, Agilent). 
     Delamination Experiments 
     For the delamination test, the as-deposited Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  films were coated with thin layer (˜160 nm) of polymethylmethacrylate (PMMA) for protection by spin-coating 50 μL of a 10 wt % PMMA (Sigma-Aldrich, USA) solution in chlorobenzene at 4000 rpm for 30 s. Subsequently, A thin layer of epoxy (Hysol, USA) was then applied onto the PMMA layer to ‘glue’ another cleaned glass substrate on top. The ‘sandwich’ specimens were then cured in a N 2 -filled glovebox for 12 h, and the excess epoxy at the edges was cleaned off with a razor blade. Then, A planar crack was introduced and propagated by inserting a razor blade ‘wedge’ into the ‘sandwich’ specimen slowly until the full delamination is achieved. The two mating fracture surfaces were observed using scanning electron microscope (LEO 1530 VP, Zeiss, Germany). 
     Estimation of E &lt;220&gt;   
     The following approach is used to arrive at a reasonable estimate. The Youngs&#39; modulus, E, of FAPbI 3  is assumed to be ˜17.8 GPa 34  and that of CsSnI 3  to be ˜20.2 GPa. 35  Since these E values are reasonably close, the rule-of-mixtures approximation is used to calculate an E˜18.5 GPa for the Cs 0.3 FA 0.7 Sn 0.3 Pb 0.7 I 3  solid-solution perovskite. Since E of halide perovskites are not very anisotropic, 26,28  the average E˜18.5 GPa is used in Eqn. 1 in lieu of E &lt;220&gt; . 
     Device Characterization 
     Devices were tested using a Newport Oriel Sol3A solar simulator with a xenon lamp inside a nitrogen glove box. The intensity of the solar simulator was calibrated using J sc  produced in a certified KG2-filtered silicon photodiode. By measuring the external quantum efficiency curve of the solar cell (conducted on a Newport system in ambient air), the spectral mismatch factor was calculated and used to appropriately adjust the intensity of the solar simulator lamp to provide 1-sun illumination. Through this procedure, we verified that the J sc  measured corresponded correctly to that the solar cells generated under AM1.5G solar illumination. The light current density-voltage (J-V) characteristic were taken from both forward bias to reverse bias and reverse bias to forward bias, with the step size of 10 mV and step delay of 10 ms, unless otherwise stated. The device area was 0.1 cm 2  and was masked with a metal aperture to define an active area of 0.058 cm 2 . The stable power output (SPO) of the devices was measured by monitoring the photocurrent current density output with the biased voltage set near the maximum power point. External quantum efficiency (EQE) measurements were taken using a Newport Oriel IQE200. 
     Stability Testing 
     For device operational stability test, PSCs were placed in a sealed cell holder with a transparent quartz cover. A continuous flow of N 2  gas was passed through the holder to minimize the water and oxygen content in the atmosphere. J-V curves were performed every hour. The temperature of the devices was maintained at ˜45° C. under continuous one-sun-intensity white-LED illumination. Between the J-V measurements, the PSCs were biased at the maximum-power-point voltage using a potentiostat under illumination. 
     Conductive Atomic Force Microscope (AFM) 
     The Conductive-AFM measurements were performed on a Bruker Icon AFM system in Ar-filled glovebox. A Pt—Ir coated tip (Nanosensor PPP-EFM) scans in contact mode, where the tip virtually grounded, and a 600-mV bias voltage was applied to the sample. The scans were in 2×2 μm 2 , with 1024 points in the fast-scan axis and 256 lines in the slow-scan axis. The mappings were done at least on 3 random locations to ensure reliable results. Note that the experiments were done within a few hours after film deposition. 
     Field-Effect Transistor (FET) and IV Measurement 
     FET device fabrication. The typical device was fabricated on the 200 nm thickness SiO 2 /highly doped Si wafer (1-10 Ωcm −1 ) purchased from MTI corporation by using the standard optical lithography technique, and then the 5 nm thickness Ti/20 nm thickness Au electrodes were deposited on the patterned sample by using the thermal evaporation deposition system, and the gate electrode was directly contacted with highly doped Si wafer, all the procedures were performed in the cleanroom. The designed channel lengths (L ch ) of the typical device is 10 μm and the channel width (W ch ) is 1000 μm. The perovskite films were then prepared by spin coating the precursor solution on to the prefabricated device by using a spin-rate of 3000 rpm for 30 s, followed by annealing at 150° C. for 30 min on the hotplate in the Nitrogen-filled glovebox. 
     FET and IV measurement. The standard FET measurement was performed inside the N 2  filled glovebox by using two Keithley 2400 source meters with LabVIEW control program. One sourcemeter was used to supply the source-drain voltage (VDS) and monitor the channel current (IDS), the other sourcemeter was used to supply the gate voltage (VGS) and monitor the gate leakage current. And the standard IV measurement was performed by using one Keithley 2400 sourcemeter with LabVIEW control program. 
     EXAMPLES 
     Example 1. A composition comprising: a perovskite having a stoichiometry comprising A 1-x FA x Sn 1-y B y (I 1-z X z ) 3 , wherein: A is a first cation, B is a second cation, X is a halide, and 0.5&lt;x≤0.9, 0.5≤y≤0.9, and 0≤z≤1. 
     Example 2. The composition of Example 1, wherein A comprises at least one of cesium, guanidinium, or methylammonium. 
     Example 3. The composition of either Example 1 or Example 2, wherein X comprises at least one of bromide or chloride. 
     Example 4. The composition of any one of Examples 1-3, wherein z equals zero. 
     Example 5. The composition of any one of Examples 1-4, further comprising a bandgap between about 1.1 eV and about 1.5 eV. 
     Example 6. The composition of any one of Examples 1-5, wherein the bandgap is between about 1.3 eV and about 1.4 eV. 
     Example 7. The composition of any one of Examples 1-6, wherein the composition further comprises at least one physical property with a characteristic value. 
     Example 8. The composition of any one of Examples 1-7, wherein the physical property comprises a grain size with the characteristic value between about 300 nm and about 1500 nm. 
     Example 9. The composition of any one of Examples 1-8, wherein the grain size is between about 750 nm and about 850 nm. 
     Example 10. The composition of any one of Examples 1-9, wherein the physical property comprises a biaxial residual stress level with the characteristic value between about 0 MPa and about 100 MPa. 
     Example 11. The composition of any one of Examples 1-10, wherein the biaxial residual stress level is between about 0 MPa and about 40 MPa. 
     Example 12. The composition of any one of Examples 1-11, wherein the physical property comprises a dark carrier density with the characteristic value between about 1×10 13  cm −3  and about 1×10 17  cm −3 . 
     Example 13. The composition of any one of Examples 1-12, wherein the dark carrier density is between about 5×10 14  cm −3  and about 5×10 16  cm −3 . 
     Example 14. The composition of any one of Examples 1-13, comprising Cs 1-x FA x Sn 1-y Pb y I 3 . 
     Example 15. The composition of any one of Examples 1-14, wherein 0.6≤x≤0.8 and 0.6≤y≤0.8. 
     Example 16. A method of making a perovskite, the method comprising: combining a stoichiometric amount of at least one perovskite precursor comprising formamidinium (FA), tin, iodide, A, B, and X resulting in a mixture; adding an additive to the mixture; and treating the mixture, wherein: the treating results in the forming of the perovskite having a stoichiometry comprising A 1-x FA x Sn 1-y B y (I 1-z X z ) 3 , A is a first cation, B is a second cation, X is a halide, 0≤x≤1, 0≤y≤1, 0≤z K 1, and the additive comprises FA and tin and at least one of fluoride or chloride. 
     Example 17. The method of Example 16, wherein the additive is added at a concentration between about 0.1 mol % and about 10 mol % relative to the stoichiometric amount. 
     Example 18. The method of either Example 16 or Example 17, wherein the concentration is between about 0.1 mol % and about 5 mol %. 
     Example 19. The method of any one of Examples 16-18, wherein the mixture is substantially in a liquid phase. 
     Example 20. The method of any one of Examples 16-19, wherein the mixture is substantially in a solid phase 
     Example 21. The method of any one of Examples 16-20, wherein the mixture is substantially in a gas phase. 
     Example 22. The method of any one of Examples 16-21, wherein the mixture includes a solvent. 
     Example 23. The method of any one of Examples 16-22, wherein the solvent includes at least one of dimethylformamide, dimethyl sulfoxide, N-methyl-2-pyrrolidone, gamma-butyrolactone, acetonitrile, 2-methoxyethanol, or N,N-dimethylacetamide. 
     Example 24. The method of any one of Examples 16-23, wherein: the additive comprises at least one of SnF 2-x FACl or SnCl 2-x FACl, and 1.5≤x≤4.5. 
     Example 25. The method of any one of Examples 16-24, wherein 2.5≤x≤3.5. 
     Example 26. The method of any one of Examples 16-25, wherein: the at least one perovskite precursor comprises SnI 2 , and the additive is present at a molar ratio between about 0.1% and about 10% or between about 3% and about 6% (optimum about 5%) relative to the amount of SnI 2 . 
     Example 27. The method of any one of Examples 16-26, wherein at least one of the combining or adding are performed at a first temperature between about 20° C. and about 50° C. 
     Example 28. The method of any one of Examples 16-27, wherein the treating comprises exposing the mixture to at least one of heat or vacuum. 
     Example 29. The method of any one of Examples 16-28, wherein the treating is performed at a second temperature between about 100° C. and about 180° C. 
     Example 30. The method of any one of Examples 16-29, wherein the second temperature is between about 100° C. and about 150° C. 
     Example 31. The method of any one of Examples 16-30, wherein the second temperature is between about 130° C. and about 150° C. 
     Example 32. The method of any one of Examples 16-31, wherein treating is performed at an absolute pressure between about 0.1 atm and about 1.1 atm. 
     The foregoing discussion and examples have been presented for purposes of illustration and description. The foregoing is not intended to limit the aspects, embodiments, or configurations to the form or forms disclosed herein. In the foregoing Detailed Description for example, various features of the aspects, embodiments, or configurations are grouped together in one or more embodiments, configurations, or aspects for the purpose of streamlining the disclosure. The features of the aspects, embodiments, or configurations, may be combined in alternate aspects, embodiments, or configurations other than those discussed above. This method of disclosure is not to be interpreted as reflecting an intention that the aspects, embodiments, or configurations require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive aspects lie in less than all features of a single foregoing disclosed embodiment, configuration, or aspect. While certain aspects of conventional technology have been discussed to facilitate disclosure of some embodiments of the present invention, the Applicants in no way disclaim these technical aspects, and it is contemplated that the claimed invention may encompass one or more of the conventional technical aspects discussed herein. Thus, the following claims are hereby incorporated into this Detailed Description, with each claim standing on its own as a separate aspect, embodiment, or configuration.