Patent Publication Number: US-2019198725-A1

Title: Molded chip fabrication method and apparatus

Description:
This application is a continuation of and claims the benefit of U.S. patent application Ser. No. 12/506,989, to Leung et al., filed on Jul. 21, 2009, which claims the benefit of U.S. patent application Ser. No. 10/666,399 to Leung et al., filed on Sep. 18, 2003, now U.S. Pat. No. 7,915,085, issued on Mar. 29, 2011. 
    
    
     BACKGROUND OF THE INVENTION 
     Field of the Invention 
     This invention relates to coating of semiconductor devices and more particularly to a method and apparatus for coating light emitting diodes (LEDs) with a matrix material containing one or more light conversion materials. 
     Description of the Related Art 
     LEDs are solid-state devices that convert electric energy to light and they generally comprise an active layer of semiconductor material sandwiched between two oppositely doped layers. When a bias is applied across the doped layers, holes and electrons are injected into the active layer where they recombine to generate light that is emitted omnidirectionally from the active layer and from all surfaces of the LED. Recent advances in LEDs (such as Group III nitride based LEDs) have resulted in highly efficient light sources that surpass the efficiency of filament-based light sources, providing light with equal or greater brightness in relation to input power. 
     One disadvantage of conventional LEDs used for lighting applications is that they cannot generate white light from their active layers. One way to produce white light from conventional LEDs is to combine different wavelengths of light from different LEDs. For example, white light can be produced by combining the light from red, green and blue emitting LEDs, or combining the light from blue and yellow LEDs. 
     One disadvantage of this approach is that it requires the use of multiple LEDs to produce a single color of light, increasing the overall cost and complexity. The different colors of light are also generated from different types of LEDs fabricated from different material systems. Combining different LED types to form a white lamp can require costly fabrication techniques and can require complex control circuitry since each device may have different electrical requirements and may behave differently under varied operating conditions (e.g. with temperature, current or time). 
     More recently, the light from a single blue emitting LED has been converted to white light by coating the LED with a yellow phosphor, polymer or dye, with a typical phosphor being cerium-doped yttrium aluminum garnet (Ce:YAG). [See Nichia Corp. white LED, Part No. NSPW300BS, NSPW312BS, etc.; See also U.S. Pat. No. 5,959,316 to Hayden, “Multiple Encapsulation of Phosphor-LED Devices”]. The surrounding phosphor material “downconverts” the wavelength of some of the LED&#39;s blue light, changing its color to yellow. For example, if a nitride-based blue emitting LED is surrounded by a yellow phosphor, some of the blue light passes through the phosphor without being changed while a substantial portion of the light is downconverted to yellow. The LED emits both blue and yellow light, which combine to provide a white light. 
     One conventional method for coating an LED with a phosphor layer utilizes a syringe or nozzle for injecting a phosphor containing epoxy over the LED. One disadvantage of this method is that it is often difficult to control the phosphor layer&#39;s geometry and thickness. As a result, light emitting from the LED at different angles can pass through different amounts of conversion material, which can result in an LED with non-uniform color temperature as a function of viewing angle. Another disadvantage of the syringe method is that because the geometry and thickness is hard to control, it is difficult to consistently reproduce LEDs with the same or similar emission characteristics. 
     Another conventional method for coating an LED is by stencil printing, which is described in European Patent Application EP 1198016 A2 to Lowery. Multiple light emitting semiconductor devices are arranged on a substrate with a desired distance between adjacent LEDs. The stencil is provided having openings that align with the LEDs, with the holes being slightly larger than the LEDs and the stencil being thicker than the LEDs. A stencil is positioned on the substrate with each of the LEDs located within a respective opening in the stencil. A composition is then deposited in the stencil openings, covering the LEDs, with a typical composition being a phosphor in a silicone polymer that can be cured by heat or light. After the holes are filled, the stencil is removed from the substrate and the stenciling composition is cured to a solid state. 
     One disadvantage of this method is that, like the syringe method above, it can be difficult to control the geometry and layer thickness of the phosphor containing polymer. The stenciling composition may not fully fill the stencil opening such that the resulting layer is not uniform. The phosphor containing composition can also stick to the stencil opening which reduces the amount of composition remaining on the LED. These problems can result in LEDs having non-uniform color temperature and LEDs that are difficult to consistently reproduce with the same or similar emission characteristics. 
     Another conventional method for coating LEDs with a phosphor utilizes electrophoretic deposition. The conversion material particles are suspended in an electrolyte based solution. A plurality of LEDs are arranged on a conductive substrate that is then almost completely immersed in the electrolyte solution. One electrode from a power source is coupled to the conductive substrate at a location that is not immersed in the solution, and the other electrode is arranged in the electrolyte solution. The bias from the power source is applied across the electrodes, which causes current to pass through the solution to the substrate and its LEDs. This creates an electric field that causes the conversion material to be drawn to the LEDs, covering the LEDs with the conversion material. 
     One of the disadvantages of this method is that after the LEDs are covered by the conversion material, the substrate is removed from the electrolyte solution so that LEDs and their conversion material can be covered by a protective epoxy. This adds an additional step to the process and the conversion material (phosphor particles) can be disturbed prior to the application of the epoxy. Another disadvantage of this process is that the electric field in the electrolyte solution can vary such that different concentrations of conversion material can be deposited across the LEDs. The conversion particles can also settle in the solution which can also result in different conversion material concentrations across the LEDs. The electrolyte solution can be stirred to prevent settling, but this presents the danger of disturbing the particles already on the LEDs. 
     SUMMARY OF THE INVENTION 
     The present invention seeks to provide a method and apparatus for coating semiconductor devices wherein the geometry and thickness of the coating layer can be controlled. The methods and apparatus according to the present invention are particularly adapted to coating light emitting diodes (LEDs) with a controlled layer of “matrix material” having conversion particles. The methods and apparatus are simple and easy to use, and allow for the reproduction of coated semiconductor devices having coating layer geometry and thickness that are substantially the same. 
     One embodiment of a method for coating a plurality of semiconductor devices according to the present invention comprises providing a mold with a formation cavity. A plurality of semiconductor devices are mounted within the mold formation cavity and a coating material is injected into the mold to fill the mold formation cavity and at least partially cover the semiconductor devices. The coating material is cured or otherwise treated so that the semiconductor devices are at least partially embedded in the coating material. The cured coating material with the embedded semiconductor devices is removed from the formation cavity. The semiconductor devices are separated so that each is at least partially covered by a layer of the coating material. 
     Another embodiment of a method according to the present invention is particularly adapted to coating a plurality of light emitting diodes (LEDs) and comprises providing a mold with a formation cavity. A plurality of LEDs are mounted within the mold formation cavity and a matrix material is injected or otherwise introduced into the mold to fill the formation cavity and at least partially cover the LEDs. The matrix material is then cured or otherwise treated so that the LEDs are at least partially embedded in the matrix material. The matrix material with the embedded LEDs is removed from the formation cavity and the embedded LEDs are separated so that each is at least partially covered by a layer of the matrix material. 
     One embodiment of an apparatus for coating a plurality of semiconductor devices comprises a mold housing having a formation cavity arranged to hold semiconductor devices. The formation cavity is also arranged so that a coating material can be injected or otherwise introduced into and fills the formation cavity to at least partially cover the semiconductor devices. 
     Another embodiment of apparatus according to the present invention is particularly adapted to coating LEDs and comprises a mold housing having a formation cavity arranged to hold a plurality of LEDs. The formation cavity comprising at least a top and bottom surface with the LEDs arranged on the bottom or top surface. The mold housing is also arranged so that a matrix material can be injected into its formation cavity covering the LEDs and filling the formation cavity. 
     After the coated LEDs are separated according to the present invention, a bias can be applied to each causing light to be emitted omnidirectionally. LED light passes through the layer of matrix material where at least some of it is converted to a different wavelength of light by the conversion particles. The arrangement of the formation cavity and the location of cuts between adjacent LEDs allows for the geometry and thickness of the layer of matrix material on each of the separated LEDs to be controlled such that the light emitting from the LED at different points on its surface passes through essentially the same amount of conversion material. This results in an LED with a more uniform color temperature as a function of viewing angle. 
     These and other further features and advantages of the invention will be apparent to those skilled in the art from the following detailed description, taken together with the accompanying drawings, in which: 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is a flow diagram of one embodiment of a method for coating semiconductor devices according to the present invention; 
         FIG. 2  is a flow diagram of another embodiment of a method for coating semiconductor devices according to the present invention that is particularly adapted to coating light emitting diodes (LEDs); 
         FIG. 3  is a sectional view of one embodiment of a coating apparatus according to the present invention; 
         FIG. 4  is a sectional view of the coating apparatus in  FIG. 3 , with a matrix material injected into the formation cavity; 
         FIG. 5  is a sectional view of a sheet of LEDs and matrix material according to the present invention; 
         FIG. 6  is a sectional view of one embodiment of two coated LEDs according to the present invention separated from the sheet in  FIG. 5 ; 
         FIG. 7  is a sectional view another embodiment of two coated LEDs according to the present invention separated from the sheet in  FIG. 5 ; 
         FIG. 8  is a perspective view of one the LEDs shown in  FIG. 7 ; 
         FIG. 9  is a sectional view of another embodiment of a coating apparatus according to the present invention for coating square devices; 
         FIG. 10  is a sectional view of the coating apparatus in  FIG. 9 , with a matrix material injected into the formation cavity; 
         FIG. 11  is a sectional view of a sheet of LEDs and matrix material according to the present invention; 
         FIG. 12  is a sectional view of one embodiment of two coated LEDs according to the present invention separated from the sheet in  FIG. 11 ; 
         FIG. 13  is a sectional view of another coating apparatus according to the present invention; 
         FIG. 14  is a sectional view of the coating apparatus of  FIG. 13  with a matrix material injected into the formation cavity; 
         FIG. 15  is a sectional view of a sheet of LEDs and matrix material according to the present invention; 
         FIG. 16  is a sectional view of one embodiment of two coated LEDs according to the present invention separated from the sheet in  FIG. 11 ; 
         FIG. 17  is a sectional view of another embodiment of two coated LEDs according to the present invention separated from the sheet in  FIG. 11 ; 
         FIG. 18  is a perspective view of one of the LEDs shown in  FIG. 13 . 
         FIG. 19  is a sectional view of another coating apparatus according to the present invention for coating square devices; 
         FIG. 20  is a sectional view of the coating apparatus of  FIG. 19  with a matrix material injected into the formation cavity; 
         FIG. 21  is a sectional view of a sheet of LEDs and matrix material according to the present invention; and 
         FIG. 22  is a sectional view of one embodiment of two coated LEDs according to the present invention separated from the sheet in  FIG. 11 ; 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Coating Methods 
       FIG. 1  shows one embodiment of a method  10  for coating semiconductor devices according to the present invention and comprises a first step  12  of providing a mold. A preferred mold comprises a formation cavity that is arranged so that semiconductor devices can be held within it and a coating material can be injected or otherwise introduced into it to cover the devices. The cavity can have many different shapes and is preferably defined by at least upper and lower parallel surfaces. In other embodiments the cavity can be further defined by side surfaces running between the upper and lower surfaces. The different shapes of the formation cavity including, but are not limited to, disk, box or lens shaped. The side surfaces can run around the entire edge of the upper and lower surfaces or can be intermittent. 
     In step  14 , semiconductor devices are arranged within the formation cavity and in the preferred method  10 , the devices are precisely arranged in a predetermined pattern. The devices can be arranged in many different ways within the formation cavity using many different methods. In a preferred arrangement method the devices are placed on the lower surface by separating the upper surface from the lower and placing the devices using a precision pick and place system. Alternatively, the devices can be placed on the lower surface using a template such as a thin metal foil having a size and shape similar to the lower surface and openings corresponding to desired locations of the semiconductor devices. The foil can be placed on the lower surface and the semiconductor devices can be arranged within the foil openings. After the devices are placed, the foil can be removed. In both methods the upper surface can then be returned over the lower surface after the devices are placed. As further described below, the lateral space between adjacent devices and the space between the upper and lower surfaces provides the desired coating thickness over the semiconductor devices. 
     In step  16  a coating material is injected or otherwise introduced into the mold&#39;s formation cavity, filling the cavity and covering the semiconductor devices. In step  18  the coating material is processed and stabilized resulting in the hardening of the coating material and the semiconductors becoming at least partially embedded in the coating material. A sheet of semiconductor devices and coating material is formed. In a preferred method  10 , the coating material is as an epoxy, silicone or other polymer and the preferred processing and stabilizing step  18  includes curing using conventional methods dictated by the coating material&#39;s curing schedule. This can include heat curing, optical curing or curing in room temperature. Alternatively, the matrix or coating material may comprise any variety of thermoset, thermoplast, injection molding, or other polymers or related materials. 
     In step  20 , the sheet of semiconductor devices and coating material is removed from the mold&#39;s formation cavity for further processing. In step  22  the individual semiconductor devices are separated by cutting through the coating material between devices. This can be accomplished using many different methods such as conventional sawing or dicing, or by using a scribe and break. 
     As described above, in the preferred step  14  the semiconductor devices are placed on the lower surface with a uniform lateral distance between adjacent devices. The upper and lower surfaces of the formation cavity are also preferably parallel. If similar semiconductor devices having the same height are placed on the lower surface of the formation cavity, the distance between the top of each of the devices and the upper surface should be the same. This results in the thickness of the layer of coating material on the top of each of the devices that is substantially the same. When the devices are separated, the cut is preferably located such that the resulting layer covering the sides of each of the devices has the same thickness. In one embodiment of a method according to the present invention, the cut is equal distance between adjacent devices. This process produces devices that have a nearly uniform layer of coating material and the process can be repeated to produce similar devices. In other embodiments different types of cuts can be made at different angles to change the coating material thickness at different locations over the semiconductor devices. 
     The method  10  can be used to coat many different types of semiconductor devices, with a preferred device being a solid state light emitter such as a light emitting diode (LED). The preferred coating material in the method for covering LEDs is a “matrix material” that comprises a curable material and one or more light conversion materials (further described below). 
       FIG. 2  shows a flow diagram for a method  30  according to the present invention that is similar to the method  10 , but is used to coat a plurality of LEDs. In step  32  a mold is provided having a formation cavity having at least upper and lower surfaces that are parallel, although the formation cavity can have many different shapes. The mold surfaces are preferably flat and comprise a material which does not adhere strongly to matrix materials or the LED during processing steps such as curing. By not adhering the upper and lower surfaces can be removed from the matrix material and LEDs without damage that could result in a non-uniform layer of matrix material over the LEDs. The upper and lower surfaces can be made of by many different materials and can be provided by sheet metal or glass slides. 
     To further reduce the danger that the upper and lower surfaces would adhere to the matrix material or LEDs, the surfaces of the formation cavity can also be covered with a coating or film layer that resists adhering to the matrix material and can also withstand heat from processing and curing. The film should be tacky enough on both sides to stick to glass or metal that forms the upper and lower surfaces and to stick to semiconductor materials that form the LEDs. The film should not bond to these materials or the matrix material which allows the semiconductor devices and cured matrix material to be easily separated from the mold surfaces without damage. Many different films can be used with a preferred film being a commercially available tape referred to as Gel-Pak®, provided by Gel-Pak, LLC. 
     In step  34  the LEDs are placed in a predefined array or pattern within the mold&#39;s formation cavity and in a preferred embodiment the film layer is arranged between the LEDs and the cavity&#39;s surface. The LEDs are preferably arranged on the lower surface of the formation cavity and can be placed using the same methods as used in step  14  of the method  10  described above. 
     It is desirable to have sufficient adhesion between the LEDs and the surface of the formation cavity such that underflow of the matrix materials is avoided between the LEDs and surface. Lateral LEDs have contacts on one surface and this surface is typically adjacent to a formation cavity surface (or film layer). Vertical LEDs typically have contacts on opposite surfaces, both of which can be adjacent to a formation cavity surface. It is desirable to avoid matrix material underflow that can cover the contacts so that after processing the LED can be electrically contacted. If underflow occurs, the matrix material must be removed from the contact surface, typically by etching, which can damage the LED and the contacts. One method to improve adhesion and reduce underflow is to apply a small amount of low tack adhesive such as silicone between the LED and the mold surface or film. This additional layer prevents underflow and can also serve as surface protection for the contacts during heat processing steps such as curing. Silicone can be removed by using convention cleaning processes that do not damage the LED or contacts. 
     In step  36  the matrix material is injected or otherwise introduced into and fills the mold&#39;s cavity, covering the LEDs. The matrix material can be made of many different compounds but preferably contains one or more light sensitive conversion materials such as phosphors distributed in an epoxy or silicone binder that can be thermally or optically curable, or cured at room temperature. To achieve uniform LED light emission, the conversion material should be distributed uniformly throughout the epoxy or silicone. For embodiments where it is desirable to emit non-uniform light, the conversion material can be non-uniform in the matrix material such that LED light emitting at different angles passes through different amounts of matrix material. Alternatively, the matrix material may exhibit or contain materials which exhibit a variety of useful properties such as high index of refraction to increase light extraction from the LED. 
     The following is a list of only some of the phosphors and that can be used alone or in combination as the conversion material, grouped by the re-emitted color that each emits following excitation. 
     Red 
     
         
         Y 2 O 2 S :Eu 3+ , Bi 3+   
         YVO4:Eu 3+ , Bi 3+   
         SrS:Eu 2+   
         SrY 2 S 4 :Eu 2+   
         CaLa 2 S 4 :Ce 3+   
         (Ca, Sr) S:Eu 2+   
         Y 2 O 3 :Eu 3+ , Bi 3+   
         Lu 2 O 3 :Eu 3+   
         (Sr 2-x La x ) (Ce 1−x Eu x )O 4    
         Sr 2 Ce 1−x Eu x O 4    
         Sr 2-x Eu x CeO 4    
         Sr 2 CeO 4    
         SrTiO 3 :Pr 3+ , Ga 3+   
       
    
     Orange 
     
         
         SrSiO 3 :Eu,Bi 
       
    
     Yellow/green 
     
         
         YBO 3 :Ce 3+ , Tb 3+   
         BaMgAl 10 O 17 :Eu 2+ ,Mn 2+   
         (Sr, Ca, Ba) (Al, Ga) 2 S 4 :Eu 2+   
         ZnS:Cu + , Al 3+   
         LaPO 4 :Ce,Tb 
         Ca 8 Mg (SiO 4 ) 4 Cl 2 :Eu 2+ , Mn 2+   
         ((Gd,Y,Lu,Se,La,Sm) 3 (Al,Ga,In) 5 O 12 :Ce 3+   
         ((Gd,Y) 1-x Sm x ) 3 (Al 1-y Ga y ) 5 O 12 :Ce 3+   
         (Y 1-p-q-r Gd p Ce q Sm r ) 3 (Al 1-y Ga y ) 5 O 12    
         Y 3 (Al 1-s Ga s ) 5 O 12 :Ce 3+   
         (Y,Ga,La) 3 Al 5 O 12 :Ce 3+   
         Gd 3 In 5 O 12 :Ce 3+   
         (Gd,Y) 3 Al 5 O 12 :Ce 3+ , Pr 3+   
         Ba 2 (Mg,Zn) Si 2 O 7 :Eu 2+   
         (Y,Ca,Sr) 3 (Al,Ga,Si) 5 (O,S) 12    
         Gd 0.46 Sr 0.31 Al 1.23 O x F 1.38 :E 2+   0.06    
         (Ba 1-x-y Sr x Ca y )SiO 4 :Eu 
         Ba 2 SiO 4 :Eu 2+   
       
    
     Blue 
     
         
         ZnS:Ag,Al 
       
    
     Combined Yellow/Red 
     
         
         Y 3 Al 5 O 12 :Ce 3+ ,Pr 3+   
       
    
     White 
     
         
         SrS:Eu 2− ,Ce 3+ ,K +   
       
    
     It should be understood that many other phosphors and other materials can be used as the conversion material according to the present invention. 
     From the list above, the following phosphors are preferred for use as the conversion material based on certain desirable characteristic. Each is excited in the blue and/or UV emission spectrum, provides a desirable peak emission, has efficient light conversion, and has acceptable Stokes shift. 
     Red 
     
         
         Lu 2 O 3 :Eu 3+   
         (Sr 2-x La x )(Ce 1-x Eu x )O 4    
         Sr 2 Ce 1-x Eu x O 4    
         Sr 2-x Eu x CeO 4    
         SrTiO 3 :Pr 3+ , Ga 3+   
       
    
     Yellow/Green 
     
         
         (Sr,Ca,Ba)(A 1 ,Ga) 2 S 4 :Eu 2+   
         Ba 2 (Mg,Zn)Si 2 O 7 :Eu 2+   
         Gd 0.46 Sr 0.31 Al 1.23 O x F 1.38 :E 2+ Eu 2+   2.06    
         (Ba 1-x-y Sr x Ca y )SiO 4 :Eu 
         Ba 2 SiO 4  :Eu 2+ 
 
To further improve the uniformity of light emission from the covered LED, the matrix material can also include scattering particles to randomly refract the light as it passes through the matrix material. To effectively scatter light, the diameter of the scattering particles should be approximately one half of the wavelength of the light being scattered. Light from the LEDs pass through the particles and is refracted to mix and spread the light. Preferred scattering particles do not substantially absorb LED light and have a substantially different index of refraction than the material in which it is embedded (for example, epoxy). The scattering particles should have as high of an index of refraction as possible. Suitable scattering particles can be made of titanium oxide (TiO 2 ) which has a high index of refraction (n=2.6 to 2.9). Other elements such as small voids or pores could also be used as to scatter the light.
 
       
    
     In step  38 , the matrix material is cured such that the LEDs are at least partially embedded in the matrix material. In the embodiment where the formation cavity comprises parallel upper and lower surfaces, LEDs and matrix material form a sheet with the LEDs at least partially embedded in the matrix material. The matrix material is allowed to cure by the material&#39;s curing schedule either in room temperature, under light for optical curing, or at an elevated temperature for heat curing. In a preferred embodiment of the method  30 , all surfaces of the LEDs are covered except for their bottom surface. In step  40  the sheet of LEDs and matrix material is removed from the molds formation cavity, with one method being separating the upper and lower surfaces of the mold to release the sheet, although many other methods can also be used. In step  42 , each LED can be singulated, preferably by separating the LEDs in the sheet into individual devices each of which has a similar thickness of matrix material around it. The methods described under step  20  of method  10  can be used, including sawing or dicing or scribe-and-break. 
     The mold is designed such that the distance between the formation cavity&#39;s upper and lower surfaces and the lateral separation between adjacent LEDs results in the desired uniform matrix material thickness on each of the separated LEDs. This results in coated LEDs that emit uniform color temperature and LEDs that can be consistently reproduced with the same or similar emission characteristics. 
     As more fully described below, depending on the type of LED being coated, the mold can be arranged differently. For lateral devices, where both the positive and negative terminals are on the same LED surface, the LEDs can be arranged with the contacts adjacent to the cavity&#39;s lower surface. Spacers can be included between the upper and lower surfaces to maintain the desired distance between the two such that there is a space between the top of the LEDs and the upper surface of the formation cavity. When the cavity is filled with the matrix material, that top surface of each of the LEDs is covered by a layer of matrix material having a similar thickness. 
     For LEDs having vertical contact geometry, one contact can be on each LED&#39;s top surface and the other contact can be on the LED&#39;s bottom surface. The top contact terminal should be protected during injection of the matrix material so that it is not covered by the matrix material. In one embodiment, the cavity&#39;s upper surface rests on the top surface contacts of the LEDs, with the contact point between the two preventing the top contacts from being fully covered by the injected matrix material. 
     For each of the above methods, the mold&#39;s formation cavity can be provided without a top surface. In those embodiments the matrix should be applied carefully and in a more controlled fashion to provide the desired thickness for the top layer in lateral LEDs and to prevent covering the top contact surface in vertical LEDs. 
     Coating Apparatus 
       FIGS. 3 and 4  show one embodiment of a compact coating apparatus  50  according to the present invention that can be used to compact coat many different semiconductor devices, but is particularly adapted to compact coating lateral LEDs with a matrix material. The apparatus  50  includes a mold housing  51  comprising a lower section  52  that includes a bottom rigid support block  54  having LEDs  55  arranged on its top surface. The top surface  56  the bottom support block  54  is preferably flat and the block  54  can be made of many different materials with many different thicknesses. The block material should not adhere to the LED or matrix material during the curing process. Suitable materials include aluminum, glass and stainless steel, and the bottom support block  54  should be thick enough that it does not flex during the layer formation process. 
     The LEDs  55  can be placed on the support block using the precision placement methods described above. A double sided adhesive film  58  can also be included between the LEDs  55  and the bottom block&#39;s flat surface  56 . As described above, the film  58  sticks to the block surface  56  and also provides a tacky surface that holds the LEDs  55 . The film  58  also withstands processing and curing steps while not adhering to the matrix material, with a suitable material for film  58  being Gel-Pak® (described above in the method  10  of  FIG. 1 ). The film  58  helps to reduce the amount of matrix material that sticks to the surface of the bottom support block  54 . In the embodiment shown with lateral LEDs  55 , the positive and negative terminals  59 ,  60  for each of the LEDs  55  are on the surface of each LED that is adjacent to the first film  58  so that when the matrix material is injected into the mold  50 , the positive and negative terminals are not covered by the matrix material. 
     The mold housing  50  also includes an upper section  61  arranged over the lower section  52 . The upper section  61  comprises a top rigid support block  62  that provides a flat top surface  64  and can be made of the same material with the same or different thickness as the bottom rigid support block  54 . A second layer of adhesive film  63  can also be included on the flat top surface  64  to provide a surface that does resists adhesion to the matrix material, and withstands the processing and curing steps. 
     The upper section  61  is arranged over the lower section  52  with the space between the two at least partially defining the mold&#39;s formation cavity  68 . The space between the two should be large enough to provide a space between the top of the LEDs  55  and the second adhesive film  63 . Referring to  FIG. 4 , a matrix material  70  can be injected or otherwise introduced into the formation cavity  68  such that it fills the space between the upper and lower section  52  and  61  and each of the LEDs is covered by the matrix material  70 . The positive and negative terminals  59 ,  60  are protected from being covered by the matrix material and after the individual LEDs are separated (singulated) the terminals  59 ,  60  are available for contacting. 
     During the injection of the matrix material  70  and subsequent processing/curing steps, the distance between the lower and upper sections  52  and  61  should be maintained. The lower and upper sections  52  and  61  can have first and second vertical spacers  65 ,  66  (shown in  FIGS. 2 and 4 ) running between them. The spacers  65 ,  66  are arranged to maintain the distance between the lower and upper sections  52  and  61  so that the desired matrix material layer thickness is achieved on the top surface of the LEDs  54 . The spacers  65 ,  66  can be arranged in many different ways and can be formed as a single spacer around the edge of the entire formation cavity  68 , or multiple spacers can be used. 
     The inside surfaces of the spacers  65 ,  66  further define the formation cavity  68  into which the matrix material  70  is injected. The matrix material  70  can be injected or introduced into the cavity  68  by many different methods according to the present invention. One such method comprises removing the upper section  61 , injecting the material  70  into the cavity using a syringe, and replacing the upper section  61 . Alternatively, the mold  50  can have an access opening through one of its rigid blocks  54 ,  62  or through one its spacers  65 ,  66  so that the matrix material  70  can be injected into the cavity without removing either the lower and upper sections  52 ,  61  or one of the spacers  65 ,  66 . The matrix material  70  can be made of the same material as described in step  36  of the method  30  above and preferably comprises phosphor conversion particles of one or more different type distributed uniformly throughout a curable epoxy, silicone or other polymer. 
     After the matrix material  70  is injected into the formation cavity  68 , the matrix material  70  is cured using a process dictated by the type of epoxy or silicone such as heat curing, light curing or room temperature cooling. After the curing process is complete the matrix material  70  and LEDs  55  form a sheet that can be removed from the mold&#39;s formation cavity  68  by removing one or both of the lower and upper sections  52 ,  61 , and/or one or both of the spacers  65 ,  66 . 
       FIG. 5  shows a sheet  72  of matrix material  70  and LEDs  55  after it is removed from the formation cavity  68  of the mold apparatus  50 . The sheet can now be separated into individual coated LEDs by sawing, dicing or using a scribe and break. 
       FIG. 6  shows two coated LEDs  76  separated from the sheet  72  shown in  FIG. 5 . In the embodiment shown, each of the coated LEDs  76  is separated by making vertical cuts through the matrix material between adjacent LEDs  55 . The matrix material can be cut in many different ways such that the layer has different thickness over the LEDs  55  or different LEDs  55  cut from the same sheets can have layers with different thicknesses. The coated LEDs  76  shown in  FIG. 6  are cube shaped and the matrix material cut is preferably made at a midpoint between adjacent LEDs  55  so that the side thickness of the matrix material on each coated LED  76  is the same. In other embodiments the cut can be made off midpoint or two cuts can be made, each of which is off midpoint but closer to one of the adjacent LEDs  55  such that the side thickness of the matrix material is still the same for each LED. This type of cubed shaped arrangement is particularly applicable to LEDs that are square, although it can also be used with LEDs having angled surfaces as shown. 
     For different shaped LEDs, the matrix material can also be cut so that the matrix material layer conforms to the shape of the LED.  FIGS. 7 and 8  show individually coated angled side surface coated LEDs  79  that have a layer of matrix material  80  that more closely conforms to the shape of each LED  55 . Angled side surfaces are typically included to increase the LEDs light extraction. The shape of the matrix layer  80  can be obtained using different methods, with a preferred method being cutting through the matrix material to a depth  84  using a wider sawing (dicing) blade having an angled point. The remainder of the matrix material can then be cut using a standard narrow sawing (dicing) blade. The layer  80  conforms more closely to the shape of the LED such that light emitting from the LED  55  passes through substantially the same amount of matrix material. Accordingly, light emitted from the coated LED  79  is more uniform and total internal reflection is reduced. Each of the coated LEDs  79  have both contacts on the bottom, uncoated surface  86  and  FIG. 8  also shows first and second conductors  88 ,  89  that can be used to apply a bias across the contacts, causing the LED  55  to emit light. 
       FIGS. 9 and 10  show another embodiment of a compact coating apparatus  90  according to the present invention that comprises many of the same features as the apparatus  50  shown in  FIGS. 3 and 4 , with the apparatus  90  used to coat square LEDs  92 . The features of the apparatus  90  that are the same as those in the apparatus  50  use the same reference numerals in  FIGS. 9 and 10 . Accordingly, the reference numerals and many of the corresponding features are not introduced or described again in the referring to  FIGS. 9 and 10 . 
     Like the LEDs  55  in  FIGS. 3 and 4 , the square LEDs  92  are arranged on either the top surface  56  of the support block  54 , or in the embodiment shown with a first film  58 , on the top surface of the adhesive film  58  such that portions of the film are sandwiched between the LEDs and the support block  54 . The LEDs  92  have bottom contacts  93  whose top surface is protected by the block  54  or film  58  from being covered by the matrix material. Referring to  FIG. 10 , a matrix material  94  can be injected into the formation cavity  68  covering the LEDs  92  and the matrix material  94  can be cured such that the LEDs  92  become embedded in the matrix material  94 . 
       FIG. 11  shows the sheet  96  of LEDs  92  and matrix material  94  after being removed from the formation cavity by the methods described during the discussion of  FIGS. 4 and 5  above.  FIG. 12  shows the individual coated LEDs  98  after being separated from the sheet  96  using the separation methods described above, with each of the square LEDs  92  having a nearly uniform layer of matrix material  94  so that the coated LEDs  98  emit similar light. 
       FIG. 13  shows another embodiment of a mold apparatus  100  that can also be used to compact coat different semiconductor devices, but is particularly adapted to coating semiconductor devices that have a contact on their top surface. One such device is a vertical LED  102  having a first contact  103  on its bottom surface and a second contact  104  on its top surface. The apparatus  100  comprises a mold housing  101  including a lower section  106  that is similar to the lower section  54  described in  FIG. 3 , and comprises a bottom support block  108  and a first double sided adhesive film  110  (e.g. Gel-Pak®). Vertical LEDs  102  are arranged on the layer  110  with their first contact  103  adjacent to the layer  110 . 
     The apparatus  100  also comprises an upper section  112  that is similar to the upper section  61  described in  FIGS. 3 and 4 , and comprises a top rigid block  114  and a second double sided adhesive film  116 . However, in apparatus  100  there are no spacers. Instead, the second adhesive film  116  rests on the second contacts  104  of the LEDs  102 , which maintains the appropriate distance between the lower and upper sections  106 ,  112  and also protects the top of the contacts  94  from being covered by the matrix material. If desired, the apparatus  100  can include side surfaces (not shown) to further define the formation cavity  119 . 
       FIG. 14  shows the apparatus  100  with the matrix material  118  injected or otherwise introduced between the lower and upper sections  106 ,  112 , that at least partially define a formation cavity  119 . The matrix material  118  can then be cured using the processes described above, so that the LEDs  102  and matrix material  118  form a sheet  120 . The first contact  103  of each LED  102  is protected from being covered by the matrix material  118  by the first adhesive film  110  and second contact  104  is protected from being fully covered by the matrix material by the second adhesive film  116 . Accordingly, both the first and second contacts  103 ,  104  are available for electrical contact without further processing or etching. 
       FIG. 15  shows the sheet  120  after it has been removed from the apparatus  100 .  FIG. 16  shows individual coated LEDs  122  after they have been separated, with the preferred separation method being vertical cuts through the matrix material between adjacent LEDs  102  to form cube shaped devices.  FIGS. 17 and 16  show LEDs  123  after being cut to match the angled sides of the LEDs  92 . This can be accomplished using the two cut method described above wherein a wider saw with and angled blade is used to cut the matrix material to a first depth  124  and a standard narrower blade is used to cut through the remainder of the matrix material.  FIG. 18  shows the second contact  104  available for contacting with a first conductor  128  coupled to the second contact  104 . A bottom conductor  129  is coupled to the LED&#39;s first contact  103  (shown in  FIG. 17 ). A bias applied across conductors  128  and  129  causes the coated LED  102  to emit light. 
       FIGS. 19 and 20  show another embodiment of a compact coating apparatus  130  according to the present invention that comprises many of the same features as the apparatus  100  shown in  FIGS. 13 and 14 , with the apparatus  130  used to coat square LEDs  132 . The features of the apparatus  130  in  FIGS. 19 and 20  that are the same as those in the apparatus  100  in  FIGS. 13 and 14  use the same reference numerals for the same features. Accordingly, the reference numerals and many of the corresponding features are not introduced or described again in the referring to  FIGS. 19 and 20 . 
     Like the LEDs  102  in  FIGS. 13 and 14 , the square LEDs  132  have a first contact  133  and a second contact  134  and the LEDs  132  are arranged on either the top surface of the block  108 , or in the embodiment shown with a first film  110 , on the top surface of the adhesive film  110 . Portions of the film  110  are sandwiched between the LEDs  132  and the block  108 , with their first contacts  133  protected. The upper section  112  is arranged on the LEDs second contacts  134  such that they are also protected. 
     Referring to  FIG. 20 , a matrix material  136  can be injected or otherwise introduced into the formation cavity covering the LEDs  123  and the matrix material  136  can be cured such that the LEDs  132  become embedded in the matrix material  136 . 
       FIG. 21  shows the sheet  138  of LEDs  132  and matrix material  136  after being removed from the formation cavity by the methods described in the discussion of  FIGS. 4 and 5  above.  FIG. 22  shows the individual coated LEDs  139  after being separated from the sheet  138  using the methods described above in the discussion of  FIGS. 6, 7 and 8 . Each of the square LEDs  132  has a similar layer of matrix material  136  so that the LEDs  132  emit similar light. 
     Each of the apparatus described above can include a small amount of low tack adhesive such as silicone between the LED contacts and the mold surface or film as described in the method  10  of  FIG. 1 . As described above, this additional layer prevents underflow and can also serve as surface protection for the contacts during heat processing steps such as curing. Silicone can then be removed by using convention cleaning processes that do not damage the LED or contacts. 
     Although the present invention has been described in considerable detail with reference to certain preferred configurations thereof, other versions are possible. Different curable materials and light conversion particles can be used. The molds can take different shapes, can have different components and the semiconductor devices can be arranged differently in the mold&#39;s formation cavity. The individual LEDs can be separated from the sheet using many different sawing or dicing methods, with the cuts being straight or angled through the matrix material. The different coating apparatus described above can be provided without an upper section and in those embodiments the matrix material should be introduced in a careful and controlled manner to provide the desired layer of matrix material. Therefore, the spirit and scope of the appended claims should not be limited to their preferred versions contained therein.