Patent Publication Number: US-2023150892-A1

Title: Method for producing a decorative mineral composite body, decorated mineral composite body and use of a multi-layer film

Description:
The present invention relates to a method for producing a decorated mineral composite body, a decorated mineral composite body and the use of a multilayer film for producing a decorated mineral composite body. 
     Mineral construction materials, such as for example concrete, mortar or sand-lime brick, are used for example in the production of buildings, in the construction of tunnels, bridges and retaining walls or foundations or of individual walls, ceilings, supports or ring beams, but also in the production of furniture or works of art. 
     The weather effects occurring outdoors can in particular lead to an impairment of the durability of mineral construction materials. 
     For example in Germany, the durability of concrete structures has the status of a legal requirement via the Building Products Act and the state building regulations. This means that stability, fitness for purpose and durability are preferably equally important criteria. According to DIN EN 1992-1-1/A1:2015-03 (“Eurocode  2 : Design of concrete structures - Part 1-1: General rules and rules for buildings”; German version EN 1992-1-1:2004/A1:2014, issue date 2015-03) structures are regarded as durable if, during the expected useful life, they perform their function with regard to load-bearing capacity and fitness for purpose without a substantial loss of use properties with an adequate maintenance effort. 
     The signs of impairment of the durability that are visible on the surface, for example in the case of concrete materials, are the appearance of spalling or flaking, the appearance of cracks and/or visible changes in the structure or the coloration of the surface. 
     In addition, high demands with regard to the surface condition, texture and/or resistance are made on mineral construction materials which are, for example, not rendered or faced and the visible surfaces of which perform design functions, for example. 
     The object of the present invention is therefore to provide a modified mineral construction material which has improved protection against corrosion, for example under the action of oxygen, carbon dioxide and/or moisture, and preferably has protection against crack formation. 
     Furthermore, the method is intended to make a cost-effective production of the modified mineral construction material possible and where appropriate be suitable for the finishing of mineral construction materials in interior and exterior construction. 
     The object of the present invention is achieved by the provision of a method according to  claim 1  for producing a decorated mineral composite body using at least one multilayer film, wherein the method comprises the following steps:
     a) providing at least one forming element, preferably formwork, with at least one outer surface and at least one inner surface,   b) applying a flowable or plastically deformable, mineral construction material mixture, which comprises water and at least one mineral binding agent, to the at least one inner surface of the forming element, preferably formwork,   c) at least partially solidifying the mineral construction material mixture to obtain a dimensionally stable, mineral green body, and   d) at least partially hardening the mineral construction material mixture, 
   wherein the multilayer film has a carrier ply and a transfer ply, which contains at least one decorative element, arranged on the carrier ply,   wherein the transfer ply has at least one polymer-containing primer layer, which comprises at least one polymer which has at least one dissociable functional group, on the side facing away from the carrier ply, and   wherein I), before step b), the at least one multilayer film is arranged with the side of the carrier ply facing away from the at least one polymer-containing primer layer on the at least one inner surface of the provided forming element, preferably formwork, and, in step b), the at least one polymer-containing primer layer is brought into contact, at least partially, with the flowable or plastically deformable, mineral construction material mixture, wherein, in step c), a decorated, dimensionally stable, mineral green body is obtained, and/or   wherein II), in and/or after step c), the at least one multilayer film is arranged with the at least one polymer-containing primer layer at least partially on the dimensionally stable, mineral green body, wherein a decorated, dimensionally stable, mineral green body is obtained, and   wherein, in alternatives I) and II), a decorated mineral composite body is obtained after step d).   
   

     Preferred embodiments of the method according to the invention are specified in dependent  claims 2 to 28 . 
     The object of the present invention is likewise achieved by the provision of a decorated mineral composite body according to  claim 29 , in particular produced according to a method of  claims 1 to 28 ,
     wherein the decorated mineral composite body comprises a mineral substrate and at least one transfer ply, which contains at least one decorative element, at least partially arranged on at least one surface of the substrate,   wherein the side of the transfer ply facing the substrate is formed by at least one polymer-containing primer layer, which is joined to the mineral substrate in at least a positive-locking manner and comprises at least one polymer which has at least one dissociable functional group.   

     Preferred embodiments of the decorated mineral composite body according to the invention are specified in dependent  claims 30 to 32 . 
     The object of the present invention is furthermore achieved by the provision of a use according to  claim 33  of a multilayer film for producing a decorated mineral composite body,
     wherein the multilayer film has a carrier ply and a transfer ply, which contains at least one decorative element, arranged on the carrier ply,   wherein the transfer ply has at least one polymer-containing primer layer, which comprises at least one polymer which has at least one dissociable functional group, on the side facing away from the carrier ply.   

     By the term “dissociable functional group” is preferably meant a functional group which is covalently bonded to the at least one polymer and, on contact with an acidic aqueous, neutral aqueous or alkaline aqueous medium, reacts in such a way that anionic and/or cationic charges can be generated at least in equilibrium. For example, dissociable functional group means that partial structures of the dissociable functional group, on contact with an acidic aqueous, neutral aqueous or alkaline aqueous medium, can react to form at least two or more molecules and/or positively and/or negatively charged ions in equilibrium. A suitable dissociable functional group can for example release at least one proton, wherein an anionic functional group is formed, or accept a proton, wherein a cationic functional group is formed. 
     A multilayer film to be used according to the invention, which can preferably be formed as a transfer film or laminating film, comprises a carrier ply and a transfer ply, which contains at least one decorative element, arranged on the carrier ply, wherein the transfer ply is preferably arranged detachably on the carrier ply when the multilayer film is designed as a transfer film. When the multilayer film is designed as a laminating film, the transfer ply is preferably arranged securely and non-detachably on the carrier ply. 
     A transfer film to be used according to the invention is preferably used to transfer a transfer ply onto an object, wherein at least one surface of the object is at least partially joined to at least one surface of the transfer ply facing away from the carrier ply, to obtain a decorated object. 
     After arranging the transfer ply on at least partial areas of the at least one surface of the object, when the multilayer film is designed as a transfer film the carrier ply is preferably removed from the transfer ply, preferably completely, with the result that only the transfer ply is arranged on at least partial areas of the surface of the decorated object, preferably at least partially forms the surface of the decorated object. Preferably, the transfer ply arranged on at least partial areas of the surface of the decorated object forms a further preferably closed coating. 
     In the process the detachment of the carrier ply from the transfer ply is preferably effected at a layer boundary between the carrier ply and the transfer ply. 
     A detachment layer which makes it easier to detach the transfer ply from the carrier ply can in particular be arranged at this layer boundary. The detachment layer can be part of the transfer ply and/or part of the carrier film here and be arranged on the transfer ply and/or on the carrier film after the detachment. 
     When the multilayer film is designed as a laminating film, after arranging the transfer ply on at least partial areas of the at least one surface of the object, the carrier film preferably remains joined to the transfer ply, with the result that the carrier film is arranged on at least partial areas of the surface of the decorated object, preferably at least partially forms the surface of the decorated object. Preferably, the transfer ply arranged on at least partial areas of the surface of the decorated object and the carrier film form a further preferably closed coating. 
     The multilayer film formed as a laminating film can, for example after arranging the multilayer film on at least partial areas of the at least one surface of the decorated object, make it possible to join two or more objects decorated according to the invention, for example with the aid of joining by forming and/or joining under the influence of heat and/or pressure, wherein two or more adjacent multilayer films can preferably be joined, for example by welding, adhesive bonding, hot stamping, laminating or combinations thereof. 
     At least one decorative element is transferred onto the object together with the transfer ply, wherein the at least one decorative element is arranged on at least partial areas of the surface of the decorated object after the transfer of the transfer ply and, depending on the design of the at least one decorative element, can influence the physical properties, preferably the haptic and/or the optical and/or the electrical and/or the mechanical properties, and/or the chemical properties of the surface of the decorated object. 
     For example, the at least one decorative element can influence the surface texture and/or color of the decorated object, for example by providing embossings and/or roughening and/or patterns and/or a smoothness and/or by providing reflection-determining properties such as transparency and/or gloss and/or matting and/or by providing a color. 
     For example, the at least one decorative element can influence the mechanical properties of the decorated object, for example by providing a surface hardness, surface elasticity and/or breaking strength of the surface. For example, the at least one decorative element can influence the absorbing capacity and/or permeability of the decorated object for water and/or water vapor, for example by providing a water-and/or water vapor-repellent coating. 
     For example, the at least one decorative element can influence the chemical properties of the decorated object, for example by providing a resistance of the surface to the ingress of substances and/or the action of acids and/or bases. For example, the at least one decorative element can improve the resistance of the decorated object to freeze-thaw cycle stress, for example in the presence of de-icing salt. 
     The at least one decorative element can preferably be formed as a motif, as a decoration, for example individual image decoration or endless decoration, as a pattern, or a combination thereof. 
     The at least one decorative element can preferably be opaque and/or translucent and/or transparent, at least in areas. 
     For example, the at least one decorative element can be formed as an optically active surface structure or one generating optical effects, wherein a suitable surface structure is preferably selected from the group which consists of diffractive surface structure, in particular hologram, zero-order diffraction structure, matte structure, in particular isotropic or anisotropic matte structure, blazed grating, lens structure, microlens structure, microprism structure, micromirror structure, or a combination of two or more of these surface structures. 
     For example, the at least one decorative element can be formed as an optically active and/or optically variable substance, which are preferably present as a dye, liquid crystal material, pigment, or a mixture thereof. Suitable pigments are, for example, interference layer pigments, liquid crystal pigments, diffractive pigments, metallic pigments, thermochromic pigments, photochromic pigments or mixtures thereof. The substance can display in each case different or also similar optical effects in particular in different wavelength ranges, for example in the infrared range and/or in the ultraviolet range and/or in the visible range. The substance can display in each case different or also similar optical effects in particular also at or in different illumination and/or observation angles or directions. 
     The decorative element preferably has at least one decorative layer. The decorative element preferably has several decorative layers. 
     Preferably, the at least one decorative layer comprises or consists of, independently of one another, at least partially arranged, preferably full-surface, protective layers, at least partially arranged barrier layers, at least partially arranged reflective layers, at least partially arranged conductive layers, at least partially arranged adhesion-promoter layers, at least partially arranged adhesive layers, at least partially arranged metal layers, at least partially arranged layers with relief structures, at least partially arranged color layers, at least partially arranged interference layers or combinations thereof. 
     The at least one decorative layer can preferably be opaque and/or translucent and/or transparent, at least in areas. The decorative layers can, independently of one another, in each case have different degrees of transparency. 
     Further preferably, the at least one decorative layer is selected from the group which consists of transparent and/or colored varnish layers, in particular comprising one or more dyes and/or pigments, replication layers with a molded optically active surface structure, reflective layers, in particular opaque reflective layers, transparent reflective layers, metallic reflective layers or dielectric reflective layers, optically variable layers, optically active layers, interference multilayer systems, volume hologram layers, liquid crystal layers, in particular cholesteric liquid crystal layers, electrically conductive layers, antenna layers, electrode layers, magnetic layers, magnetic storage layers, barrier layers and combinations thereof. 
     A mineral construction material is an inorganic non-metallic construction material consisting of preferably crystalline constituents. These can be natural minerals, such as ashlar, sand or loam, or a shaped mixture of substances consisting of screened or ground minerals, which obtains the desired strength through crystallization of preferably mineral binding agents or mineral binding agent constituents. 
     In particular, the inventors have found that by finishing a mineral construction material with at least one multilayer film to be used according to the invention the occurrence of corrosion, for example concrete corrosion, can be prevented. 
     By applying a film coating the decorated mineral construction material in the form of the composite body according to the invention preferably obtains a barrier against oxygen and/or carbon dioxide and/or moisture. 
     Furthermore, the method according to the invention preferably provides protection from carbonation. 
     A chemical reaction which takes place in concrete in the presence of carbon dioxide and moisture is preferably called carbonation. 
     This process does not damage the concrete directly. The strength is preferably even increased by the formation of limestone during the carbonation. In the case of reinforced concrete, however, the loss of the alkaline environment (depassivation) of the reinforcement caused by the process can make corrosion possible, which can result in severe damage to the structural component. 
     The decorated mineral composite body preferably produced with the method according to the invention has a barrier against acid substances as well as protection from swelling and dissolving attacks. 
     Concrete substantially consists, for example, of natural stone cemented using cement. Cement stone is, as a basic product, preferably not very resistant to acids. Lime-alumina compounds in the cement stone can for example be converted by acids into water-soluble compounds which can be worn away by water and/or atmospheric effects. As a result the cohesion between aggregate and cement stone is preferably initially loosened and if the attack progresses destroyed. So long as the concrete surface is intact, an attack can only start from the surface. The larger the attack surface area becomes as the opening and fissuring of the concrete outer skin progresses, the faster the destruction can progress. 
     In the long term concrete can also be leached by rainwater and other types of very soft water with a hardness of approximately less than 3°dH (German degree of hardness). Lime- and magnesium-deficient water running over the concrete can dissolve calcium hydroxide and wash it out. Then a hydrolytic decomposition of the hydrate phases can be effected. 
     A swelling attack is present if the substances acting on the concrete form new reaction products with a much larger volume in the reaction with the cement stone, in some cases also with the aggregates. The greater required space can then lead to the concrete blowing out from inside. 
     A typical example of this is sulfate swelling. If sulfate-containing gases or solutions act on concrete, a reaction between sulfates and the tricalcium aluminate of the cement stone (C3A) can preferably result in the formation of ettringite. In the process, the volume of the reaction products can increase to eight times the original volume of the starting materials and the concrete is blown out from inside. This damage often occurs in the case of concrete sewer tunnels. Here, under the conditions prevailing above all in deep tunnel systems (low flow rate, relatively high temperature and lack of ventilation), hydrogen sulfide gas smelling of rotten eggs forms due to bacterial decomposition of the sulfur-containing organic substances (such as proteins) contained in the sewage. This gas can be oxidized by other bacteria or by atmospheric oxygen to give sulfates and these can cause the sulfate swelling. 
     The decorated mineral composite body preferably produced with the method according to the invention preferably furthermore has a barrier against de-icing agents, for example chloride ion-containing de-icing salts. 
     If chloride ions reach the reinforcement for example, there is a danger of pitting corrosion, in particular for the sensitive prestressing steel. Bridge structures and parking levels, for example, are particularly at risk. The damage processes do not take place on the surface, where they are easy to identify, but rather inside the structural component on the reinforcement through destruction at specific points. At the point in time at which they are identified, they may therefore already have led to severe impairment of the stability. 
     The method according to claim 1 according to the invention for producing a decorated mineral composite body using at least one multilayer film comprises the following steps:
     a) providing at least one forming element, preferably formwork, with at least one outer surface and at least one inner surface,   b) applying a flowable or plastically deformable, mineral construction material mixture, which comprises water and at least one mineral binding agent, to the at least one inner surface of the forming element, preferably formwork,   c) at least partially solidifying the mineral construction material mixture to obtain a dimensionally stable, mineral green body, and   d) at least partially hardening the mineral construction material mixture.   

     The at least one multilayer film used in the method according to the invention has a carrier ply and a transfer ply, which contains at least one decorative element, arranged on the carrier ply, wherein the transfer ply has at least one polymer-containing primer layer, which comprises at least one polymer having at least one dissociable group, on the side facing away from the carrier ply, 
     wherein I), before step b), the at least one multilayer film is arranged with the side of the carrier ply facing away from the at least one polymer-containing primer layer on the at least one inner surface of the provided forming element, preferably formwork, and, in step b), the at least one polymer-containing primer layer is brought into contact, at least partially, with the flowable or plastically deformable, mineral construction material mixture, wherein, in step c), a decorated, dimensionally stable, mineral green body is obtained, and/or   wherein II), in and/or after step c), the at least one multilayer film is arranged with the at least one polymer-containing primer layer at least partially on the dimensionally stable, mineral green body, wherein a decorated, dimensionally stable, mineral green body is obtained, and   wherein, in alternatives I) and II), a decorated mineral composite body is obtained after step d).   

     In the method according to the invention, the at least one multilayer film is preferably: 
     I) arranged, before step b), with the side of the carrier ply facing away from the at least one polymer-containing primer layer on the at least one inner surface of the provided forming element, preferably formwork, wherein, in step b), the at least one polymer-containing primer layer of the multilayer film is brought into contact, at least partially, with the flowable or plastically deformable, mineral construction material mixture, wherein, in step c), a decorated, dimensionally stable, mineral green body is obtained, or   II) arranged, in and/or after step c), with the side of the at least one polymer-containing primer layer facing away from the carrier ply on the dimensionally stable, mineral green body, wherein a decorated, dimensionally stable, mineral green body is obtained through the at least partial solidification of the mineral construction material mixture.   

     In the method according to the invention, at least one first multilayer film and at least one second multilayer film can preferably be used, wherein, before step b), the at least first multilayer film is arranged with the side of the carrier ply of the at least first multilayer film facing away from the at least one polymer-containing primer layer on the at least one inner surface of the provided forming element, preferably formwork, wherein, in step b), the at least one polymer-containing primer layer of the at least first multilayer film is brought into contact, at least partially, with the flowable or plastically deformable, mineral construction material mixture, and wherein, in and/or after step c), the at least second multilayer film is arranged with a side of the at least one polymer-containing primer layer of the at least second multilayer film facing away from the carrier ply on the dimensionally stable, mineral green body, wherein a decorated, dimensionally stable, mineral green body is obtained through the at least partial solidification of the mineral construction material mixture. 
     Further preferably, in alternative II) of the method according to the invention, before step d), the at least one multilayer film is arranged with the side of the at least one polymer-containing primer layer facing away from the carrier ply on the dimensionally stable, mineral green body. 
     Through the method according to the invention a decorated mineral composite body is obtained, preferably in or after step d), which comprises or consists of an at least partially hardened mineral substrate and at least one transfer ply, which contains at least one decorative element, at least partially arranged on at least one surface of the mineral substrate, wherein the side of the transfer ply facing the mineral substrate is formed by at least one polymer-containing organic primer layer, which is joined to the mineral substrate in at least a positive-locking manner. 
     The mineral substrate of the decorated mineral composite body preferably comprises or consists of at least one solidified, preferably cured, mineral construction material, optionally at least one aggregate and/or at least one non-volatile additive as well as optionally at least one reinforcement element. 
     A mineral construction material is preferably an inorganic non-metallic material consisting of at least partially crystalline constituents. These can be natural minerals, such as ashlar, sand, clay or loam, or a shaped mixture of substances consisting of screened and/or ground minerals, which preferably obtains the desired strength in the presence of water through crystallization of at least one mineral binding agent. 
     In step b) of the method according to the invention, a flowable or plastically deformable, mineral construction material mixture, which comprises water and at least one mineral binding agent, is used which, in step c) of the method according to the invention, at least partially solidifies to obtain a dimensionally stable, mineral green body. 
     The at least partial solidification of the mineral construction material mixture can also be called setting, wherein the solidification, in particular in the case of cement paste, constitutes the defined increase in viscosity due to water binding, preferably incorporation of water of crystallization, in concrete or mortar. 
     Through the at least partial solidification of the mineral construction material mixture, a mineral green body which is at least dimensionally stable is preferably obtained. The green body preferably has a lower strength than the at least partially cured mineral composite body. 
     The strength of mineral construction materials, for example concrete, arises as a result of the, preferably exothermic, reaction in which constituents of the mineral binding agent used crystallize out, for example clinker constituents of cement, preferably with absorption of water. In this process, crystal needles preferably grow, which can become firmly interlocked. 
     The crystal growth can continue over a relatively long period in the case of a mineral construction material, with the result that the final strength of a mineral composite body is preferably not achieved until after a certain period of time. 
     For example, cement paste preferably solidifies over a period of twelve hours. Then the hardening phase preferably takes place, wherein cement paste is preferably converted into cement stone in concrete or mortar. With normal temperature and humidity conditions, cement preferably reaches standard strength after 28 days. 
     The at least one mineral binding agent used in the method according to the invention is preferably selected from the group which consists of calcium silicate hydrates, cement, lime, clay, gypsum, loam, magnesia binder and combinations thereof. 
     The at least one mineral binding agent preferably comprises or consists of a hydraulic binding agent, a non-hydraulic binding agent or a mixture thereof. 
     A non-hydraulic binding agent is preferably an inorganic, non-metallic, finely ground substance, which hardens in air after being brought into contact, preferably mixed, with water. Non-hydraulic binding agents are not water-resistant in the hardened state. 
     A non-hydraulic binding agent is preferably air hardening lime, which hardens in the presence of water with a simultaneous supply of air as the carbon dioxide from the air, with water, forms carbonic acid which is used for the carbonation of the calcium hydroxide (slaked lime). 
     A further non-hydraulic binding agent is preferably gypsum (CaSO 4  × 2 H 2 O), which can be used as binding agent in the form of hemihydrate (CaSO 4  × ½ H 2 O) or anhydrite (CaSO 4 ). During the hardening the binding agent absorbs water. In the course of this hydration needle-shaped gypsum crystals of the formula CaSO 4  × 2 H 2 O form, which become matted with each other and grow together. 
     A further non-hydraulic binding agent is preferably magnesia binder, which can be produced by mixing caustic calcined magnesite (magnesia, MgO) with magnesium chloride (MgCl 2 ) dissolved in water. The hardening is effected by the fine crystal needles of the forming magnesium hydroxide interpenetrating and becoming matted with each other. The hardening is completed in a few hours. 
     A hydraulic binding agent is preferably an inorganic, non-metallic, finely ground substance which solidifies and hardens by itself after being brought into contact, preferably mixed, with water as a result of chemical reactions with the water and, after the hardening, preferably remains solid and volumetrically stable, even under water. 
     Hydraulic binding agents consist of compounds between a non-hydraulic base, for example lime (CaO), magnesia (MgO) or mixtures thereof, and so-called hydraulizing substances, for example silicon dioxide (SiO 2 ), aluminum oxide/alumina (Al 2 O 3 ), iron oxide (Fe 2 O 3 ) or mixtures thereof. 
     Hydraulic binding agents include, for example, all types of cement according to DIN EN 197-1:2011-11 (“Cement - Part 1: Composition, specifications and conformity criteria for common cements”; German version EN 197-1:2011, issue date 2011-11), DIN 1164-10:2013-03 (“Special cement - Part 10: Composition, specification and conformity evaluation for cement with low effective alkali content”, issue date 2013-03) and DIN 1164-11:2003-11 (“Special cement - Part 11: Composition, specification and conformity evaluation for cement with short solidification time”, issue date 2003-11) as well as hydraulic lime according to DIN EN 459-1:2015-07 (“Building lime -Part  1 : Definitions, specifications and conformity criteria”, German version EN 459- 1:2015, issue date 2015-07). 
     Further preferably, the at least one mineral binding agent is selected from the group which consists of Portland cement, Portland blast-furnace slag cement, Portland silicate cement, Portland pozzolana cement, Portland fly ash cement, Portland shale cement, Portland limestone cement, Portland composite cement, blast-furnace slag cement, pozzolanic cement, composite cement, alumina cement and mixtures thereof. 
     The molar contents of reactive calcium oxide (CaO), silicon dioxide (SiO 2 ) and/or aluminum oxide (Al 2 O 3 ), which can form calcium silicate hydrates (CSH) or calcium aluminate hydrates capable of hardening in the presence of water, are preferably decisive for the hydraulic effectiveness of a binding agent. 
     A hydraulic binding agent preferably contains calcium oxide (CaO) and silicon dioxide (SiO 2 ) in a CaO/SiO 2  molar ratio greater than 1.5. 
     A latent hydraulic substance contains calcium oxide (CaO) and silicon dioxide (SiO 2 ) in a CaO/SiO 2  molar ratio from a range of from 0.5 to 1.5. 
     Latent hydraulic substances can therefore harden hydraulically only when an activator is added, e.g. calcium hydroxide (Ca(OH) 2 ) or substances with a similar action. 
     Latent hydraulic substances harden hydraulically by themselves after fine grinding and being brought into contact, preferably mixed, with water because when they react with water without other additions strength-forming, lime-containing hydration products form through hydration. 
     However, this reaction proceeds very slowly and is therefore preferably accelerated by an activator for technical use. The most important latent hydraulic substance for concrete technology is preferably granulated blast-furnace slag. 
     As latent hydraulic substances are not binding agents by themselves, they count among concrete additives when used as a starting material of concrete. 
     Pozzolans are siliceous or siliceous and aluminous substances. 
     Pozzolans, unlike latent hydraulic substances, contain only a little calcium oxide (CaO). Pozzolans contain calcium oxide (CaO) and silicon dioxide (SiO 2 ) in a CaO/SiO 2  molar ratio of less than 0.5. 
     Pozzolans can therefore form hydration products that are capable of hardening only in conjunction with a substance which, after being brought into contact, preferably mixed, with water, yields calcium hydroxide (Ca(OH) 2 ). 
     Rocks and earths, which are preferably dried at temperatures of at most approximately 150° C., are called natural pozzolans. They are, like trass, lava, pozzolana and Santorin earth, usually of volcanic origin. 
     Rocks and earths, which are technically calcined (tempered) at higher temperatures in order to develop a sufficient pozzolanic reactivity, are called artificial or natural tempered pozzolans. Tempered clay, brick dust, silica fume and fly ash can have pozzolanic properties. 
     Important pozzolans are fly ash, brick dust, silica fume, rice husk ash, clinkstone, calcined clay and metakaolin. 
     In concrete technology terms, concrete additives also include pozzolans. 
     The mineral construction material mixture preferably comprises or consists of concrete, mortar, sand-lime brick, ceramic or a combination thereof. 
     By the term “ceramic” is preferably meant silicate ceramic, oxide ceramic, non-oxide ceramic and combinations thereof, preferably silicate ceramic and oxide ceramic. 
     In a preferred embodiment of the method according to the invention, the mineral construction material mixture comprises concrete or mortar, wherein the at least one mineral binding agent comprises or consists of cement, and wherein the mineral construction material mixture furthermore comprises aggregate. 
     By the term “aggregate” is preferably meant a mixture of broken or unbroken grains of natural and/or artificial mineral substances of the same or different sizes. 
     The properties and quality of suitable aggregates for concrete and mortar are specified, for example, by the following standards:
     DIN EN 12620:2008-07 (“Aggregates for concrete”; issue date 2008-07),   DIN EN 13139:2002-08 (“Aggregates for mortar”; issue date 2002-08).   

     Before step b), the at least one multilayer film is preferably arranged with the side of the carrier ply facing away from the at least one polymer-containing primer layer on at least one formwork inner surface, with the result that the at least one polymer-containing primer layer of the multilayer film preferably points away from the at least one formwork inner surface. 
     In step b), the at least one polymer-containing primer layer of the carrier ply is brought into contact, at least partially, with the flowable mineral construction material mixture, wherein, in step c), through the at least partial solidification of the mineral construction material mixture a decorated, dimensionally stable, mineral green body is obtained, in which the at least one polymer-containing primer layer of the multilayer film is joined to the at least partially solidified mineral construction material mixture in preferably a positive-locking manner. 
     After the formwork is removed, a decorated mineral composite body is preferably obtained through at least partial hardening of the mineral construction material mixture. 
     Concrete is preferably a construction material which is blended as a dispersion with the addition of liquid, preferably water, consisting of a binding agent and aggregates. In some contexts the cured concrete is also called artificial stone. 
     Concrete preferably contains cement as binding agent and aggregate as ballast. The added water preferably initiates the chemical setting process. In order to influence the processability and further properties of the concrete, concrete additives and/or concrete admixtures can be added to the construction material mixture. The majority of the water is preferably chemically bound. 
     Preferably, the concrete- or mortar-comprising mineral construction material mixture furthermore contains additives, concrete admixtures, concrete additives and mixtures thereof. 
     Concrete is preferably used as a composite material in combination with at least one reinforcement element, for example a high-tensile reinforcement. A suitable reinforcement element is for example concrete reinforcement steel or prestressing steel, for example in the form of a mat, rod, wire, ring, lattice girder, or a combination thereof, wherein reinforced concrete or prestressed concrete, respectively, is preferably obtained. Suitable reinforcement elements can likewise be made of steel, synthetic and/or glass fibers as well as knitted fabrics made of alkali-resistant (AR) glass and/or carbon fibers. 
     Suitable reinforcement elements are known to a person skilled in the art. 
     Suitable types of concrete are for example: top concrete layer, cast-in-place concrete, pumped concrete, spun concrete, sprayed concrete, tamped concrete, roller compacted concrete, underwater concrete, vacuum concrete, screed concrete, blue concrete, fiber- and textile-reinforced concrete, foam glass concrete, glass-reinforced concrete, high performance and ultra-high performance concrete (UHPC), infra-lightweight concrete and ultra-lightweight concrete, concrete concrete, air-entrained concrete (AE concrete)/foamed concrete, lean concrete, eco concrete, papercrete, polymer concrete and mineral casting, recycled concrete, acid-resistant concrete, self-cleaning concrete, self-compacting concrete (SCC), exposed concrete, structural concrete, textural concrete and photographic concrete, chipping and pervious concrete, reinforced concrete, prestressed concrete, steel fiber-reinforced concrete, translucent concrete (light-transmitting concrete), exposed aggregate concrete, waterproof concrete, fresh concrete, colored concrete, dense structure concrete, porous lightweight concrete, heavyweight concrete/loaded concrete, wood-concrete, carbon concrete, architectural concrete, autoclaved aerated concrete, fiber-reinforced concrete, glass concrete, asphalt concrete, wet mix aggregate, sulfur concrete, resin-based concrete, single-grain concrete, or combinations thereof. 
     Mortar is preferably a construction material which consists of a binding agent, for example lime or cement, aggregate with a grain size of preferably at most 4 mm and added water, if necessary also of concrete additives and admixtures, and which hardens through a chemical reaction of the binding agents. 
     Suitable mortars are, for example, masonry mortar, render, fire-resistant mortar, resin-based mortar, screed mortar, grouting mortar, swelling mortar, hydraulic mortar as well as mineral sealing slurries or combinations thereof. 
     Within the mineral construction materials, a distinction can furthermore be made between preformed construction materials, for example stone or brick, and non-preformed construction materials, for example concrete or mortar. 
     In the case of preformed construction materials, autoclaved construction materials, such as for example sand-lime brick, autoclaved aerated concrete, fiber cement, CSH insulation material, are used, which contain calcium silicate hydrate (CSH) phases as essential component. 
     For example, autoclaved aerated concrete is an autoclaved construction material preferably with a bulk density of from 300 kg/m 3  to 800 kg/m 3 , which can preferably be produced from the raw materials quicklime (CaO) as mineral binding agent, water and quartz sand, wherein a small quantity of a pore forming material, preferably aluminum powder or paste, is added. The construction material mixture is preferably poured into a forming element, in which the metallic, fine-particle aluminum generates hydrogen gas in the alkaline suspension. 
     In the industrial manufacture of sand-lime bricks, quicklime (CaO) and sand (predominantly quartz sand) are preferably mixed with addition of water. 
     When the quicklime is converted using water, preferably to calcium silicate hydrate, the mixture can in each case preferably be molded by means of pressing to give a dimensionally stable green body. 
     In a preferred embodiment of the method according to the invention, the mineral construction material mixture comprises or consists of sand-lime brick or autoclaved aerated concrete, wherein the at least one mineral binding agent comprises or consists of a calcium silicate hydrate,
     wherein, in step c), a dimensionally stable, mineral green body is obtained by means of pressing,   wherein, in and/or after step c), the at least one multilayer film is at least partially arranged with the at least one polymer-containing primer layer on at least one surface of the dimensionally stable, mineral green body, wherein a decorated, dimensionally stable, mineral green body is obtained, and   wherein, in step, the decorated, dimensionally stable, mineral green body is hydrothermally hardened, preferably at a temperature from a range of from 150° C. to 250° C. in the presence of steam; preferably with a pressure of at least 5 bar, and for a period of at least 3 h, to obtain a decorated mineral composite body.   

     In a preferred embodiment of the method according to the invention, the mineral construction material mixture comprises or consists of a ceramic, preferably silicate ceramic, preferably porcelain, oxide ceramic and non-oxide ceramic, preferably silicate ceramic and oxide ceramic, wherein the at least one mineral binding agent comprises or consists of a clay mineral, preferably kaolinite. 
     Preferably, in step c), a dimensionally stable, mineral green body is obtained by means of pressing, slip casting, injection molding, film casting, modeling and/or extruding, wherein, in and/or after step c), the at least one multilayer film is at least partially arranged with the at least one polymer-containing primer layer on at least one surface of the dimensionally stable, mineral green body, to obtain a decorated, dimensionally stable, mineral green body. 
     Preferably, in step d), the decorated, dimensionally stable, mineral green body is fired, preferably at a temperature of 850° C. or higher for a period of at least 12 h, to obtain a decorated mineral composite body. 
     Further preferably, the at least one multilayer film comprises at least one fireproof decorative element, preferably one or more fireproof pigments and/or one or more molded surface reliefs. 
     A multilayer film to be used according to the invention has a carrier ply and a transfer ply, which contains at least one of the above-named decorative element, arranged on the carrier ply, wherein the transfer ply has at least one polymer-containing primer layer on the side facing away from the carrier ply. 
     Preferably, in the method according to the invention the at least one polymer-containing primer layer of the multilayer film to be used according to the invention is: 
     I) in step b), brought into contact, at least partially, with the flowable or plastically deformable, mineral construction material mixture, which comprises water and at least one mineral binding agent, wherein, in step c), a decorated, dimensionally stable, mineral green body is obtained, and/or   II) in and/or after step c), at least partially arranged on at least one surface of the dimensionally stable, mineral green body obtained by at least partially solidifying the mineral construction material mixture.   

     The inventors have found that by at least partially solidifying the mineral construction material mixture a dimensionally stable, mineral green body is formed, which has pores into which the at least one polymer comprising at least one dissociable functional group, preferably after dissociation of at least one dissociable functional group, contained in the polymer-containing primer layer can mechanically “interlock”. 
     The further the solidification of the construction material mixture progresses, i.e. the growth of the needle-shaped calcium silicate hydrate crystals preferably increases, the more the adhesion of the primer layer to the solidified construction material mixture increases. The adhesion preferably correlates with the curing duration, as after one or two days the adhesion is lower than after several days. 
     The adhesion of the multilayer film and/or of the transfer ply of the multilayer film to the solidified construction material mixture or the composite body according to the invention can be determined using a cross-cut according to DIN EN ISO 2409: 2013- 06 (Paints and varnishes - Cross-cut test (ISO 2409:2013), German version of EN ISO 2409:2013, issue date: 2013-06). 
     In particular, the inventors have found that a polymer molecule which is contained in the at least one polymer-containing primer layer and has at least one dissociable functional group, after dissociation of at least one dissociable functional group, preferably to form at least one anionic functional group, further preferably anionic acid group, adheres particularly well to the flowable or plastically deformable, mineral construction material mixture or to the dimensionally stable, mineral green body obtained by at least partially solidifying the mineral construction material mixture. 
     In this connection, it is preferably assumed that the at least one polymer having at least one dissociable functional group, after dissociation of at least one of the dissociable functional groups at the molecular level, preferably has at least one anionic functional group, for example a deprotonated acid group, wherein the at least one anionic functional group of the polymer can form coordinate bonds with metal ions, in particular Ca 2+  ions, of the mineral construction material mixture, preferably in the presence of bound water. 
     Further preferably, the aqueous polymer dispersion or polymer solution, which is used to produce the polymer-containing primer layer, has a pH of from 1.0 to 9.0, preferably from 1.5 to 7.0, preferably from 2.0 to 6.0, preferably from 2.5 to 5.5, preferably from 3.0 to 5.0, in each case measured at a temperature of 25° C. and a pressure of 1013 mbar. 
     Alternatively, to produce the polymer-containing primer layer a non-aqueous polymer dispersion or polymer solution can be used, which, in addition to the at least one polymer having at least one dissociable functional group, preferably furthermore comprises at least one organic solvent which is selected, for example, from alcohols, carboxylic acid esters, ethers, ketones, alkanes, aromatic hydrocarbons, halogenated aliphatic hydrocarbons, lactones, lactams, nitriles, nitro compounds, tertiary carboxylic acid amides, sulfoxides, glycol ethers or mixtures thereof. 
     The at least one polymer-containing primer layer preferably comprises at least one polymer which has at least one dissociable functional group which, in each case independently of one another, is further preferably an amino group and/or a hydroxyl group and/or a free acid group and/or a blocked acid group and/or a combination thereof, preferably a free acid group and/or a blocked acid group and/or a combination thereof. 
     Further preferably, the at least one polymer, having at least one dissociable functional group, of the at least one polymer-containing primer layer, in each case independently of one another, comprises at least one free amino group and/or at least one free hydroxyl group and/or at least one free acid group, which is preferably selected from the group which consists of carboxyl group, sulfonic acid group, which can also be called sulfo group, sulfuric acid monoester group, phosphonic acid group, phosphoric acid monoester group and combinations thereof, preferably carboxyl group, sulfonic acid group, phosphonic acid group and combinations thereof, further preferably carboxyl group, sulfonic acid group and combinations thereof, further preferably carboxyl group, and/or at least one blocked acid group, which is preferably selected from the group which consists of carboxylic acid ester group, carboxylic acid anhydride group, carboxylic acid halide group, sulfonic acid ester group, sulfonic acid anhydride group, sulfonic acid halide group, phosphonic acid ester group and combinations thereof, further preferably carboxylic acid ester group, carboxylic acid anhydride group, sulfonic acid ester group and combinations thereof, further preferably carboxylic acid ester group, sulfonic acid ester group and combinations thereof, further preferably carboxylic acid ester group. 
     Further preferably, the at least one polymer, having at least one dissociable functional group, of the at least one polymer-containing primer layer, in each case independently of one another, comprises at least one free acid group, which, in each case independently of one another, is preferably selected from the group which consists of carboxyl group, sulfonic acid group, which can also be called sulfo group, sulfuric acid monoester group, phosphonic acid group, phosphoric acid monoester group and combinations thereof, preferably carboxyl group, sulfonic acid group, phosphonic acid group and combinations thereof, further preferably carboxyl group, sulfonic acid group and combinations thereof, further preferably carboxyl group, and/or at least one blocked acid group, which, in each case independently of one another, is preferably selected from the group which consists of carboxylic acid ester group, carboxylic acid anhydride group, carboxylic acid halide group, sulfonic acid ester group, sulfonic acid anhydride group, sulfonic acid halide group, phosphonic acid ester group and combinations thereof, further preferably carboxylic acid ester group, carboxylic acid anhydride group, sulfonic acid ester group and combinations thereof, further preferably carboxylic acid ester group, carboxylic acid anhydride group and combinations thereof, further preferably carboxylic acid ester group, sulfonic acid ester group and combinations thereof, further preferably carboxylic acid ester group. 
     A polymer, which has at least one free, anionic, functional group, can for example be selected from the group which consists of anionically functionalized epoxide polymers and copolymers, anionically functionalized acrylic polymers and copolymers, anionically functionalized methacrylic polymers and copolymers, anionically functionalized polyurethane polymers and copolymers and mixtures thereof, preferably anionically functionalized acrylic polymers, anionically functionalized methacrylic polymers, anionically functionalized polyurethane polymers, copolymers thereof and mixtures thereof. 
     Anionically functionalized polymers and copolymers can be incorporated, for example via suitable chain extenders which have corresponding ionic groups, into the at least one polymer, in order to stabilize it as a particle dispersed in water. 
     A typical representative in the case of polyurethane polymers is for example dimethylolpropionic acid for carboxyl functionality and diol sulfonates for pendant sulfonic acid groups. The polymer obtained is preferably permanently hydrophilic and can further preferably be easily dispersed. 
     Likewise, anionically functionalized epoxy resins can for example be derived from one epoxy resin or several epoxy resins. 
     Anionic functionalized groups can be introduced into epoxy resin molecules by different methods. Typically, epoxy resins contain hydroxyl groups as well as epoxide groups. These groups can be reacted with various reagents, which contain the desired anionic functional group or a precursor thereof, for example by varying the ratio of dicarboxylic acid to the starting epoxy resin. 
     Another means of adding anionic functional groups to the epoxy resin consists of reacting the epoxy resin with a functionalizing agent which contains at least one anionic functional group or a precursor thereof and at least one functional group which is capable of reacting with epoxide groups and/or hydroxyl groups, wherein the epoxy resin to be reacted preferably contains hydroxyl groups. 
     Non-exclusive examples of such functionalizing agents comprise compounds which have at least one sulfonate functionality and/or at least one carboxylate functionality as well as further preferably at least one aromatic hydroxyl functionality. 
     The alkali metal salts of hydroxybenzenesulfonic acid and hydroxybenzoic acid are representative compounds of this type. 
     Alternatively, the starting epoxy resin can be derived by reaction with phosphorylating, sulfating and/or sulfonating reagents such as superphosphoric acid, sulfuric acid and the like. 
     Polyacrylates and polymethacrylates preferably have free deprotonated carboxylate groups. 
     Suitable polymer dispersion are commercially available from DSM Coating Resins B.V. (Zwolle, NL), for example, under the type designation NeoCryl®, which are aqueous polyacrylate polymer and copolymer dispersions, and NeoRez®, which are aqueous polyurethane polymer and copolymer dispersions. 
     By the term “free acid group” is preferably meant a covalently bonded functional group which can preferably release at least one proton. A free acid group is preferably uncharged and, in each case independently of one another, is further preferably selected from the group which consists of carboxyl group, sulfonic acid group, sulfuric acid monoester group, phosphonic acid group, phosphoric acid monoester group and combinations thereof, preferably carboxyl group, sulfonic acid group, phosphonic acid group and combinations thereof, further preferably carboxyl group, sulfonic acid group and combinations thereof, further preferably carboxyl group. 
     The at least one polymer which has at least one free acid group is further preferably selected from the group which consists of epoxide polymers and copolymers, in each case with at least one free acid group, acrylic polymers and copolymers, with in each case at least one free acid group, methacrylic polymers and copolymers, with in each case at least one free acid group, polyurethane polymers and copolymers, with in each case at least one free acid group, and mixtures thereof, preferably acrylic polymers, with in each case at least one free acid group, methacrylic polymers, with in each case at least one free acid group, polyurethane polymers, with in each case at least one free acid group, copolymers thereof and mixtures thereof. 
     Suitable polymers with at least one free acid group can for example be produced from the above-named polymers with at least one free, anionic, functional group, preferably by altering the pH, for example by acidification. 
     Suitable polymers and polymer dispersions with at least one free acid group are commercially available from MUNZING CHEMIE GmbH (Abstatt, DE), for example, under the type designation WÜKOSEAL®, preferably WÜKOSEAL® VP Ku, which is a vinyl acetate-ethylene copolymer, or are commercially available from the Lubrizol Coporation (Wickliffe, Ohio, US), for example, under the type designation Carbopol®, which are polyacrylic acids. 
     The at least one polymer which has at least one blocked acid group is further preferably selected from the group which consists of epoxide polymers and copolymers, with in each case at least one blocked acid group, acrylic polymers and copolymers, with in each case at least one blocked acid group, methacrylic polymers and copolymers, with in each case at least one blocked acid group, polyurethane polymers and copolymers, with in each case at least one blocked acid group, and mixtures thereof, styrene polymers and copolymers, with in each case at least one blocked acid group, preferably acrylic polymers and copolymers, with in each case at least one blocked acid group, methacrylic polymers and copolymers, with in each case at least one blocked acid group, polyurethane polymers and copolymers, with in each case at least one blocked acid group, styrene polymers and copolymers, with in each case at least one blocked acid group, and mixtures thereof. 
     By the term “blocked acid group” is preferably meant a functional group which further preferably releases at least one acid group, preferably in the form of the deprotonated anion of the corresponding acid group, at least when and/or after the corresponding polymer of the primer layer is brought into contact with the flowable or plastically deformable, mineral construction material mixture. 
     Suitable polymers with at least one blocked acid group which, in each case independently of one another, is preferably selected from the group which consists of carboxylic acid ester group, carboxylic acid anhydride group, carboxylic acid halide group, sulfonic acid ester group, sulfonic acid anhydride group, sulfonic acid halide group, phosphonic acid ester group and combinations thereof, further preferably carboxylic acid ester group, carboxylic acid anhydride group, sulfonic acid ester group and combinations thereof, further preferably carboxylic acid ester group, carboxylic acid anhydride group and combinations thereof, further preferably carboxylic acid ester group, sulfonic acid ester group and combinations thereof, further preferably carboxylic acid ester group, are known to a person skilled in the art and can for example be produced according to synthesis methods known in the state of the art. 
     For example, polymers with at least one ester group, preferably carboxylic acid ester group, sulfonic acid ester group, phosphonic acid ester group, combinations thereof or mixtures thereof, can be produced by reacting a polymer with at least one corresponding acid group, preferably carboxyl group, sulfonic acid group, phosphonic acid group, combinations thereof or mixtures thereof, and/or at least one corresponding acid halide group, preferably carboxylic acid chloride group, sulfonic acid chloride group, or combinations thereof, and/or at least one corresponding acid anhydride group, preferably carboxylic acid anhydride, sulfonic acid anhydride or combinations thereof, with at least one alcohol, preferably aliphatic alcohol having 1 to 6 C atoms, aromatic alcohol having 6 or more C atoms or mixtures thereof, further preferably aliphatic alcohol having 1 to 3 C atoms, according to methods known to a person skilled in the art, for example using an acid as catalyst. 
     Polymers with at least one acid halide group, preferably carboxylic acid halide group, which can also be called halogen carbonyl group, sulfonic acid halide group, which can also be called halogen sulfonyl group, or combinations thereof, are known to a person skilled in the art. 
     Preferably, acid halide groups are suitably selected from the group which consists of carboxylic acid chloride group, which can also be called chlorocarbonyl group, sulfonic acid chloride group, which can also be called chlorosulfonyl group, and combinations and can likewise be produced according to synthesis methods known in the state of the art. 
     Suitable polymers with at least one carboxylic acid chloride group can for example be synthesized by reaction of the corresponding polymer having at least one carboxyl group with thionyl chloride (SOCl 2 ), phosgene (COCl 2 ), phosphorus(III) chloride or phosphorus(V) chloride. 
     Polymers with at least one acid anhydride group, preferably carboxylic acid anhydride group, sulfonic acid anhydride group, or combinations thereof, further preferably carboxylic acid anhydride group, are known to a person skilled in the art and can likewise be produced according to synthesis methods known in the state of the art. 
     Polymers with at least one acid anhydride group can for example be produced by reaction of one of the above-named polymers with at least one acid chloride group, preferably carboxylic acid chloride group, sulfonic acid chloride group, or a combination thereof, with the salt of a carboxylic acid or by elimination of water using a strong dehydrating agent, wherein suitable polymeric polycarboxylic acids or polymeric polysulfonic acids can further preferably be used. 
     Polymers with at least one acid anhydride group, preferably carboxylic acid anhydride group, can preferably also be produced using at least one suitable unsaturated polycarboxylic acid, such as preferably maleic acid, fumaric acid, methylmaleic acid (citraconic acid), methylfumaric acid (mesaconic acid), methylenebutanedioic acid (itaconic acid), tetrahydrophthalic acid or aconitic acid, as well as corresponding anhydrides thereof and/or monoesters thereof and/or bis-esters thereof, by homopolymerization or copolymerization with preferably at least one ethylenically unsaturated monomer, further preferably acrylic acid and its esters, methacrylic acid and its esters, ethylene, vinylethylene, vinyl ethers, vinyl esters, vinyl halides, phenylvinyl derivatives, for example styrene, allyl esters, methallyl esters, esters of cinnamic acid, acrylamides or methacrylamides, alpha-olefins, or N-vinylpyrrolidone, preferably under the action of at least one radical initiator, gamma and/or UV radiation, at least one ionic catalyst, electric current and/or pressure and/or temperature. 
     Suitable polymers with at least one acid anhydride group, preferably carboxylic acid anhydride group, are for example maleic acid anhydride-functionalized polymers, such as for example styrene-maleic acid anhydride copolymer. 
     Preferably, the at least one polymer-containing primer layer has a non-volatile content of from 5 wt.-% to 70 wt.-%, preferably 10 wt.-% to 50 wt.-%, in each case relative to the total weight of all constituents of the polymer-containing primer layer. 
     In a preferred embodiment, the at least one polymer-containing primer layer has a residual moisture content, i.e. water content, of at most 15% wt.-%, preferably of at most 10 wt.-%, preferably of at most 8 wt.-%, further preferably of at most 5 wt.-%, further preferably of at most 3.5 wt.-%, further preferably of at most 1.9 wt.-%, in each case relative to the total weight of all constituents of the polymer-containing primer layer. 
     Further preferably, the at least one polymer-containing primer layer has a thickness of from 50 nm to 1000 µm, preferably from 1 µm to 100 µm, further preferably from 5 µm to 50 µm. 
     The abbreviation “wt.-%” used in the present patent application denotes the specification of content “percent by weight”. 
    
    
     
       In the following the invention is explained with reference to several embodiment examples utilizing the attached drawings by way of example. 
         FIG.  1    to  FIG.  4    show schematic representations of a transfer film. 
         FIG.  5    schematically shows the arrangement of a transfer film in a forming element. 
         FIG.  6    and  FIG.  7    show schematic representations of a decorated mineral composite body. 
         FIG.  8    shows a decorated mineral composite body produced in Example 1. 
         FIG.  9    and  FIG.  10    show SEM micrographs of the detached transfer ply of the composite body produced in Example 1. 
         FIG.  11    shows a composite body produced in Comparison Example 2. 
     
    
    
     A multilayer film  1 ,  1 ′ to be used according to the invention has a carrier ply  10 ,  10 ′ and a transfer ply  13 ,  13 ′, which contains at least one decorative element, arranged on the carrier ply  10 ,  10 ′, wherein the transfer ply  13 ,  13 ′ has at least one polymer-containing primer layer  15  on the side facing away from the carrier ply  10 ,  10 ′. 
     Preferably, the carrier ply  10 ,  10 ′ comprises at least one carrier layer  11  made of preferably a polyester, for example a polylactide (PLA) or polyethylene terephthalate (PET), a polyolefin, for example polypropylene (PP) or polyethylene (PE), or a combination thereof, in particular made of PET. 
     Optionally, the carrier ply  10 ,  10 ′ has at least one detachment layer on the rear side, which comprises or consists of at least one wax, preferably montan ester wax, at least one silicone, at least one polyurethane or a combination thereof, on the side facing away from the transfer ply  13 ,  13 ′. 
     Preferably, an arrangement of at least one detachment layer on the rear side of the carrier ply  10 ,  10 ′ prevents the layers from adhering during the production of a multilayer film  1 ,  1 ′ to be used according to the invention. 
     Further preferably, the at least one carrier layer  11  of the carrier ply  10 ,  10 ′ has a layer thickness of between 4 µm and 100 µm, preferably between 10 µm and 50 µm. 
     Optionally, the carrier ply  10 ,  10 ′ can furthermore comprise at least one detachment layer  12 , which is arranged on the side of the carrier ply  10 ,  10 ′ facing the transfer ply  13 ,  13 ″. 
     Preferably, the at least one detachment layer  12  can comprise at least one wax, preferably montan ester wax, at least one silicone, at least one polyurethane or a combination thereof. 
     Further preferably, the at least one decorative element influences the surface texture, the color of the surface, the mechanical properties and/or the chemical properties of the decorated mineral composite body  2 , wherein the at least one decorative element is preferably formed as a motif, as a decoration, for example individual image decoration or endless decoration, as a pattern, or a combination thereof. 
     In a preferred embodiment, at least one functional layer  14  is arranged between the at least one polymer-containing primer layer  15  and the carrier ply  10 ,  10 ′, wherein the at least one decorative element is preferably arranged in the at least one functional layer  14 . 
     Preferably, the at least one functional layer  14  arranged between the at least one polymer-containing primer layer  15  and the carrier ply  10 ,  10 ′ comprises or consists of at least one metal and/or semi-metal, alloys thereof or mixture thereof, preferably aluminum, iron, chromium, indium, copper, tin, zinc, silicon, alloys thereof or mixtures thereof, at least one polymer, preferably selected from cellulose-based polymers, chlorinated polyolefins, chlorinated rubbers, colophony resins, epoxy resins, EVA copolymers, formaldehyde resins, hydrocarbon resins, ketone/aldehyde resins, maleinate resins, melamine resins, phenolic resins, acrylates, polyacrylates, polyacrylate dispersions, polyester dispersions, polyurethane dispersions, polyether dispersions, polyamide resins, polyester resins, polyisocyanates, polyolefin resins, polystyrene resins, polyurethane resins, polyvinyl acetals, polyvinyl acetates, polyvinyl alcohols, polyvinyl butyrals, polyvinyl chlorides, polyvinyl propionates, polyvinylpyrrolidones, polyvinylidene chlorides, polyvinylidene fluorides, shellacs, silicone resins, styrene acrylate dispersions, sulfonamide resins, urea resins, acrylonitrile-1,3-butadiene-styrene (ABS) resins and mixtures thereof. 
     The at least one functional layer  14  arranged between the at least one polymer-containing primer layer  15  and the carrier ply  10 ,  10 ′ can preferably furthermore comprise at least one additive which is preferably selected from the group which consists of hydrophobing agents, flow additives, defoamers, colorants, preferably selected from dyes, organic pigments, inorganic pigments and mixtures thereof, fillers, rheology additives, plasticizers, stabilizers, light stabilizers, antioxidants, flame retardants, reinforcing substances and mixtures thereof. 
     The at least one functional layer  14  arranged between the at least one polymer-containing primer layer  15  and the carrier ply  10 ,  10 ′ is further preferably selected from the group which consists of transparent and/or colored varnish layers, in particular comprising one or more dyes and/or pigments, replication layers with a molded optically active surface structure, reflective layers, in particular opaque reflective layers, transparent reflective layers, metallic reflective layers or dielectric reflective layers, optically variable layers, optically active layers, interference multilayer systems, volume hologram layers, liquid crystal layers, in particular cholesteric liquid crystal layers, electrically conductive layers, antenna layers, electrode layers, magnetic layers, magnetic storage layers, barrier layers and combinations thereof. 
     Preferably, a protective ply  18  can be arranged on the side of the at least one polymer-containing primer layer  15  facing away from the carrier ply  10 ,  10 ′. The protective ply  18  preferably prevents damage and/or contamination of the primer layer  15 , for example during the transport of a transfer film  1  to be used according to the invention, and can be peeled off the primer layer  15  before use of the transfer film  1 , preferably, in alternative I), before the at least one polymer-containing primer layer  15  is brought into contact, at least partially, with the flowable or plastically deformable, mineral construction material mixture, and/or 
     in alternative II), before the at least one multilayer film  1 ,  1 ′ is arranged, in and/or after step c), with the at least one polymer-containing primer layer  15  at least partially on the dimensionally stable, mineral green body  3   a . 
     Preferably, the protective ply  18  comprises at least one carrier layer  19   a  made of preferably a polyester, a polyolefin, a polyurethane or a combination thereof, in particular made of PET. 
     In an alternative embodiment, the protective ply  18  can be an in particular self-supporting varnish layer. The varnish layer is for example made of polyurethane with a thickness of between 10 µm and 250 µm and can be peeled off the primer layer  15  before use of the transfer film  1 . 
     In an alternative embodiment, the protective ply  18  can be an in particular non-self-supporting varnish layer. The varnish layer has binding agents for example based on polyester and/or on maleinate resins and/or on polycarbonates and has a thickness of between 0.1 µm and 5 µm, preferably 0.5 µm and 2 µm, and can remain on the primer layer  15  during the use of the transfer film  1  and in particular at least partially dissolves when the primer layer  15  is brought into contact with the still flowable construction material mixture. 
     Further preferably, the at least one carrier layer  10   a  of the protective ply  18  has a layer thickness of between 4 µm and 100 µm, preferably between 10 µm and 50 µm. 
     Optionally, the protective ply  18  can furthermore comprise at least one detachment layer  19   b , which is arranged on the side of the protective ply  18  facing the primer layer  15 . 
     Preferably, the at least one detachment layer  19   b  can comprise at least one wax, preferably montan ester wax, at least one silicone, at least one polyurethane or a combination thereof. 
     The method according to the invention for producing a decorated mineral composite body  2  using at least one multilayer film  1 ,  1 ′ comprises the following steps:
     a) providing at least one forming element  30 , preferably formwork, with at least one outer surface and at least one inner surface  31 ,   b) applying a flowable or plastically deformable, mineral construction material mixture, which comprises water and at least one mineral binding agent, to the at least one inner surface  31  of the forming element  30 , preferably formwork,   c) at least partially solidifying the mineral construction material mixture to obtain a dimensionally stable, mineral green body  3   a , and   d) at least partially hardening the mineral construction material mixture to obtain a mineral composite body  2 ,   
 wherein the multilayer film  1 ,  1 ′ has a carrier ply  10 ,  10 ′ and a transfer ply  13 ,  13 ′, which contains at least one decorative element, arranged on the carrier ply  10 ,  10 ′,
   wherein the transfer ply  13 ,  13 ′ has at least one polymer-containing primer layer  15  on the side facing away from the carrier ply  10 ,  10 ′, and   wherein I), before step b), the at least one multilayer film  1 ,  1 ′ is arranged with the side of the carrier ply  10 ,  10 ′ facing away from the at least one polymer-containing primer layer  15  on the at least one inner surface  31  of the provided forming element  30 , preferably formwork, with the result that the at least one polymer-containing primer layer  15  of the multilayer film  1 ,  1 ′ preferably points away from the at least one inner surface  31  of the forming element  30 , preferably formwork, and wherein, in step b), the at least one polymer-containing primer layer  15  is brought into contact, at least partially, with the flowable or plastically deformable, mineral construction material mixture, wherein, in step c), a decorated, dimensionally stable, mineral green body  3  is obtained, and/or   wherein II), in and/or after step c), the at least one multilayer film  1 ,  1 ′ is arranged with the at least one polymer-containing primer layer  15  on the dimensionally stable, mineral green body  3   a , wherein a decorated, dimensionally stable, mineral green body  3  is obtained, and   wherein, in alternatives I) and II), a decorated mineral composite body  2  is obtained after step d).   

     The at least one forming element  30  used in the method according to the invention comprises at least one outer surface and at least one inner surface  30 , wherein the at least one inner surface  31  of the forming element  30  can preferably have a two-dimensional or three-dimensional geometric shape. The inner surface  31  of the forming element  30  can alternatively or additionally also have a structuring in the form of a macroscopic and/or microscopic structure. 
     Preferably, the at least one multilayer film  1 ,  1 ′ to be used according to the invention can be at least partially decorated using at least one decorative roller or can contain at least one decorative pattern. 
     In the method according to the invention, a protective ply  18  optionally arranged on the side of the at least one polymer-containing primer layer  15  facing away from the carrier ply  10 ,  10 ′ is at least partially, preferably completely, removed, in alternative I), preferably before the at least one polymer-containing primer layer  15  is brought into contact, at least partially, with the flowable or plastically deformable, mineral construction material mixture, and/or, in alternative II), preferably before the at least one polymer-containing primer layer  15  is arranged on the dimensionally stable, mineral green body  3   a . 
     A decorated, dimensionally stable, mineral green body  3  preferably comprises an at least partially solidified mineral construction material mixture and at least one transfer ply  13 ,  13 ′, which contains at least one decorative element, at least partially arranged on at least one surface of the green body  3 , wherein the side of the transfer ply  13 ,  13 ′ facing the green body  3  is formed by at least one polymer-containing primer layer  15 , which is joined to the green body  3  in at least a positive-locking manner. Optionally, at least one carrier ply  10 ,  10 ′ is furthermore arranged on the at least one transfer ply  13 ,  13 ′ on the side of the transfer ply  13 ,  13 ′ facing away from the green body  3 . 
     A decorated mineral composite body  2  according to the invention, in particular produced according to a method of claims 1 to 26, comprises a mineral substrate S and at least one transfer ply  13 ,  13 ′, which contains at least one decorative element, at least partially arranged on at least one surface of the substrate S, wherein the side of the transfer ply  13 ,  13 ″ facing the substrate S is formed by at least one polymer-containing primer layer  15 , which is joined to the substrate S in at least a positive-locking manner. 
     Preferably, the mineral substrate S of the decorated mineral composite body  2  according to the invention comprises or consists of at least one at least partially hardened mineral construction material which is selected from the group which consists of concrete, mortar, sand-lime brick, ceramic and combinations thereof. 
     Further preferably, at least one carrier ply  10 ,  10 ′ is arranged on the at least one transfer ply  13 ,  13 ′, wherein the at least one transfer ply  13 ,  13 ″ and the at least one carrier ply  10 ,  10 ′ form a multilayer film  1 ,  1 ′, which is preferably formed as a laminating film. 
     A multilayer film  1 ,  1 ′, which is preferably formed as a laminating film, can preferably be designed to be smaller than the at least one surface of the substrate S on which the transfer ply  13 ,  13 ′, which contains at least one decorative element, is at least partially arranged, preferably bonded. 
     Alternatively, a multilayer film  1 ,  1 ′, which is preferably formed as a laminating film, can be designed to be the same size as the at least one surface of the substrate S on which the transfer ply  13 ,  13 ′, which contains at least one decorative element, is at least partially arranged, preferably bonded. 
     Alternatively, a multilayer film  1 ,  1 ′, which is preferably formed as a laminating film, can be designed to be larger than the at least one surface of the substrate S on which the transfer ply  13 ,  13 ′, which contains at least one decorative element, is at least partially arranged, preferably bonded, wherein the multilayer film  1 ,  1 ′ further preferably forms an overhang at least at one edge of the decorated mineral composite body  2 . 
     Preferably, the overhang of the multilayer film  1 ,  1 ′ can, after arranging the multilayer film  1 ,1′ on at least partial areas of the at least one surface of the decorated object, make it possible to join two or more composite bodies  2  decorated according to the invention through a joining manufacturing process, for example by crimping, folding and/or bending. 
     Preferably, the transfer ply  13 ,  13 ′ and/or the transfer ply  10 ,  10 ′ can be modified after application to the decorated mineral composite body  2 , for example by at least partial application, preferably overprinting and/or dousing and/or flooding, of at least one further layer, for example protective layer and/or varnish layer, by printing and/or casting methods known to a person skilled in the art. 
     A multilayer film  1 ,  1 ′ to be used according to the invention is preferably produced by sequential, preferably full-surface or partial, application of the individual layers of the transfer ply  13 ,  13 ′ to the transfer ply  10 ,  10 ′ by methods known in the state of the art, for example by printing methods such as gravure printing and/or screen printing and/or digital printing and/or flexographic printing and/or inkjet printing and/or offset printing, and/or by casting methods such as slot casting. 
     The layers produced with these methods are for example protective layers, barrier layers, decorative layers, adhesion-promoter layers, adhesive layers, detachment layers, color layers, which can be present in each case over the whole surface and/or partially. 
     Furthermore, the preferably full-surface or partial application of vapor-deposited and/or printed-on metal layers and/or metal oxide layers as decorative element or decorative layer is possible. Vapor-deposited metal and/or metal oxide layers can, for example, be applied by methods known in the state of the art, for example physical vapor deposition (PVD) or chemical vapor deposition (CVD). 
     The layers produced with these methods are for example reflective layers, conductive layers, barrier layers, decorative layers, which can be present in each case over the whole surface and/or partially. 
     Further preferably, after molding an optically active surface structure into a replication layer, at least one decorative layer is vapor-deposited, preferably in each case in areas or over the whole surface, on the replication layer. 
     The application over the whole surface followed by a removal of the at least one decorative layer in areas by means of known methods such as washing methods or lift-off varnishes or etching methods or mask exposure methods with the aid of a photoresist layer is also possible. 
     Preferably, the at least one polymer-containing primer layer  15  of the transfer ply  13 ,  13 ′ is first arranged on or applied to the transfer ply  10 ,  10 ′, which can comprise at least one carrier layer made of a polyester, a polyolefin or a combination thereof, in particular made of PET, by at least one of the above-named printing and/or casting methods, wherein the at least one polymer-containing primer layer  15  is further preferably applied with an application weight from a range of from 0.5 g/m 2  to 500 g/m 2 , preferably from 1 g/m 2  to 50 g/m 2 , preferably from 5 g/m 2  to 25 g/m 2 , preferably from 9 g/m 2  to 15 g/m 2 , in each case relative to the total weight of all constituents of the polymer-containing primer layer  15 . 
     Further preferably, the at least one polymer-containing primer layer  15  is produced using an aqueous polymer dispersion which a pH of from 1.0 to 9.0, preferably from 1.5 to 7.0, preferably from 2.0 to 6.0, preferably from 3.0 to 5.0, in each case measured at a temperature of 25° C. and a pressure of 1013 mbar, on. 
     Example 1 
     A PET carrier (thickness of the PET carrier of from 5 µm to 150 µm, preferably from 7 µm to 100 µm) as carrier ply, coated with an at least 50 nm thick layer of a montan ester wax, was coated with an aqueous primer coat made of WÜKOSEAL® VP Ku (MUNZING CHEMIE GmbH), which is an aqueous dispersion of a vinyl acetate-ethylene copolymer with a pH of 4.5 ± 1 as specified by the manufacturer, in a mixture of water and isopropanol, solids approx. 15%, typically with an application weight of 10 g/m 2 . 
     The coating was dried to constant weight in a standard atmosphere (air temperature of 23° C. and a relative atmospheric humidity of 50%) according to DIN EN ISO 291:2008-08 (“Plastics - Standard atmospheres for conditioning and testing (ISO 291:2008) - German version EN ISO 291:2008, issue date: 2008-08) and formed a closed transfer ply of the transfer film. 
     In each case 50 g EB screed concrete from quick-mix Gruppe GmbH &amp; Co. KG (Osnabrück, DE) was prepared with 6.5 g water. The transfer film was arranged with the transfer ply on a panel made of ABS material with a thickness of 1 mm and the prepared screed concrete was applied in each case to the transfer film on the side of the primer coat. 
     After the screed concrete had cured completely at room temperature, a mineral composite body formed which had been coated on one side with the transfer film used in each case. A very good adhesive tape strength was achieved after approx. 5 days’ curing time. 
     The PET carrier was then detached from the concrete, wherein the transfer ply remained adhering to the concrete and formed a smooth coating on the composite body. 
       FIG.  8    depicts a produced composite body, wherein the upper side of the composite body has been formed by the transfer ply adhering to the concrete. 
     The adhesion of the transfer ply to the concrete was tested by means of a cross-cut according to DIN EN ISO 2409: 2013-06. 
     In each case 6 cuts were made vertically and 6 cuts were made horizontally (at an angle of 90° to the vertical cuts) in the coating as far as the substrate with the aid of a blade and preferably with the aid of a template. The width of the cut was dependent on the layer thickness of the coating. In the case of coatings with a layer thickness of less than 60 µm the distance between the cuts is preferably approximately 1 mm. 
     A clear adhesive tape or an adhesive crepe tape with an adhesiveness of from 6 N/25 mm to 10 N/25 mm was stuck to the resulting square of cuts (measurement area). This was peeled off in a time of from 0.5 to 1 second at an angle of 60 °. 
     The evaluation was effected in accordance with DIN EN ISO 2409: 2013-06 by visual assessment of the measurement area and classification into cross-cut characteristic values of from 0 (very good adhesion) to 5 (very poor adhesion), abbreviated to GT 0 to GT 5, or in accordance with ASTM D 3359 - 09, test method B. 
     The criteria for a classification of the corresponding characteristic values are summarized in the following table: 
     
       
         
           
               
               
               
               
             
               
                 Description 
                 Surface 
                 Characteristic value ISO 
                 Characteristic value ASTM 
               
             
            
               
                 The edges of the cuts are completely smooth, no section of the coating has flaked. 
                 - 
                 GT0 
                 5B 
               
               
                 Small flakes of the coating have detached at the intersections of the cut lines; flaked area approximately 5% of the sections. 
                 
                   
                 
                 GT1 
                 4B 
               
               
                 The coating has flaked along the edges of the cuts and/or at the intersections of the cut lines; flaked area approximately 15% of the sections. 
                 
                   
                 
                 GT 2 
                 3B 
               
               
                 The coating has flaked partially or completely in broad strips along the edges of the cuts and/or the coating has flaked completely or partially on individual sections; flaked area approximately 35% of the sections. 
                 
                   
                 
                 GT 3 
                 2B 
               
               
                 The coating has flaked in broad strips along the edges of the cuts and/or completely or partially on individual sections; flaked area approximately 65% of the sections. 
                 
                   
                 
                 GT 4 
                 1B 
               
               
                 Flaked area more than 65% of the sections. 
                 - 
                 GT 5 
                 0B 
               
            
           
         
       
     
     After a curing time of 28 days, cross-cut characteristic values of between 5B and 4B were measured on the produced composite bodies. 
     For the assessment of the adhesion of the multilayer film and/or of the transfer ply of the multilayer film, a so-called adhesive tape test was also carried out. A self-adhesive adhesive strip (brand Tesa, type 4657) in particular with a length of 45 mm and a width of 25 mm was stuck in the middle to a solidified construction material mixture coated with the multilayer film and/or the transfer ply of the multilayer film free from wrinkles and bubbles and pressed on manually. 
     The solidified and coated construction material mixture was clamped in a Z005 material testing machines from ZwickRoell GmbH &amp; Co. KG (Ulm, DE). At a peel angle of 90°, the adhesive strip was peeled off at a speed of 500 mm/min and in the process the force which was necessary in order to detach the adhesive strip from the multilayer film and/or the transfer ply of the multilayer film was measured. 
     The tests surprisingly showed that the multilayer film and/or the transfer ply of the multilayer film remained substantially completely on the solidified construction material mixture and only the adhesive strip was peeled off again. The force measured in the process was between 400 cN and 1000 cN. 
     The adhesiveness between the multilayer film and/or the transfer ply of the multilayer film and the solidified construction material mixture should accordingly be higher than this measured adhesiveness as, below this measured adhesiveness, still no defects occurred on the multilayer film and/or the transfer ply of the multilayer film after the adhesive strip had been detached from the multilayer film and/or the transfer ply. 
     Furthermore, SEM micrographs of parts of the composite bodies were produced, and are represented in  FIG.  9    and  FIG.  10   . 
     For the SEM micrographs, in each case an approx. 10 x 10 x 5 mm (10 x 10 mm base area, thickness 5 mm) test piece was broken off the coated composite body to be examined and coated with gold by sputtering. 
     In the SEM micrographs, in each case the break-off edges of the test piece were examined. 
     The SEM micrographs were in each case recorded with the following parameters: 8 kV voltage, 20 mm distance between the test pieces, spot size  39 , observation angle 80°. 
     As can easily be seen in  FIG.  9    and  FIG.  10   , the polymer layer of the transfer ply had a strong adhesion to the concrete. At some tearing edges/breaking edges a thin layer of concrete clearly remained adhering to the polymer. It was furthermore evident that the concrete was mechanically “anchored” in the polymer layer. It was evident in particular that the polymer layer formed a closed and smooth surface which seals the concrete. 
     Comparison Example 2 
     In order to test what influence the transfer ply has on the stability and adhesiveness of the transfer ply, 50 g EB screed concrete was prepared with water as described above and the moist mixture was put on a panel made of ABS material with a thickness of 1 mm as substrate. The surface of the mixture lying opposite the ABS panel was smoothed out and coated with an aqueous primer coat made of WÜKOSEAL® VP Ku in a mixture of water and isopropanol, solids approx. 15%, by means of brushing. 
     In order to obtain a coating that is as complete as possible, a much higher application weight was necessary. 
     After the coated concrete mixture had dried out, as specified above in Example  1 , the test piece obtained was examined visually. 
     In spite of the higher application weight of the coating, a closed film did not form on the coated surface after the concrete had dried out, as can be seen in  FIG.  11   . 
     List of Reference Numbers 
     
       
         
           
               
               
            
               
                   1 ,  1 ′ 
                 multilayer film 
               
               
                 
                   2 
                 
                 decorated mineral composite body 
               
               
                 
                   3 
                 
                 decorated, dimensionally stable, mineral green body 
               
               
                 
                   3 
                   a 
                 
                 dimensionally stable, mineral green body 
               
               
                   10 ,  10 ′ 
                 carrier ply 
               
               
                 
                   11 
                 
                 carrier layer 
               
               
                 
                   12 
                 
                 detachment layer 
               
               
                   13 ,  13 ′ 
                 transfer ply 
               
               
                 
                   14 
                 
                 functional layer 
               
               
                 
                   15 
                 
                 polymer-containing primer layer 
               
               
                 
                   18 
                 
                 protective ply 
               
               
                 
                   19 
                   a 
                 
                 carrier layer 
               
               
                 
                   19 
                   b 
                 
                 detachment layer 
               
               
                 
                   30 
                 
                 forming element 
               
               
                 
                   31 
                 
                 inner surface 
               
               
                 S 
                 mineral substrate