Patent Publication Number: US-2023150242-A1

Title: Radiative cooling metal plate, preparation method and application thereof

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
     This application is a 371 of international PCT patent application PCT/CN2020/087650 filed on Apr. 29, 2020, which claims all benefits accruing under 35 U.S.C. § 119 from China Patent Application No. 202010312422.8, filed on Apr. 20, 2020, with title of “RADIATIVE COOLING METAL PLATE, PREPARATION METHOD AND APPLICATION THEREOF”, in the China National Intellectual Property Administration, the content of which is hereby incorporated by reference. 
    
    
     TECHNICAL FIELD 
     The present disclosure relates to the technical field of radiative cooling, and in particular, to a radiative cooling metal plate, a preparation method and an application thereof. 
     BACKGROUND 
     A metal substrate can be pressed into profiled plates with various wave types by a cold roll forming method, which are suitable for industrial and civil buildings, warehouses, special buildings, roofing surfaces, wall surfaces and outer wall decorations of large-span houses with steel structure, and the like, and have advantages of light quality, high strength, convenient construction and rapid, shock resistance, fire protection, and rain protection. 
     A radiative cooling functional layer located on the metal substrate can achieve a passive temperature reduction effect. The radiative cooling functional layer has a high emissivity at a wavelength of 8 μm to 13 μm. Therefore, heat can be transmitted to the outside space through the atmospheric window in a form of electromagnetic waves, that is, the radiative cooling functional layer plays a role of cooling. Furthermore, the radiative cooling functional layer has a high reflectivity in the solar wave band, in order to prevent accumulation of heat of sunlight on the metal substrate. During an installation process of such radiative cooling metal plate including the radiative cooling functional layer and the metal substrate, the radiative cooling functional layer needs to be bent, installed and fixed, resulting in fracture and damage, thereby affecting a radiative cooling effect and the service life thereof. 
     SUMMARY 
     According to one aspect of the present disclosure, a radiative cooling metal plate is provided. The radiative cooling metal plate can include a metal substrate, a first adhesive layer and a radiative cooling functional layer stacked in order. The radiative cooling functional layer is located on a surface of the metal substrate. The first adhesive layer is arranged between the metal substrate and the radiative cooling functional layer, and an elongation at break of the radiative cooling functional layer is in a range of 1% to 300%. 
     In one embodiment, an average reflectivity of the radiative cooling functional layer at a wavelength of 0.3 μm to 2.5 μm is greater than or equal to 75% and an average emissivity of the radiative cooling functional layer at a wavelength of 8 μm to 13 μm is greater than or equal to 85%. 
     In one embodiment, under any one of three following conditions where a xenon lamp aging time is greater than or equal to 1000 hours, a wet heat aging time is greater than or equal to 1000 hours, and a salt spray aging time is greater than or equal to 600 hours, an attenuations of an average reflectivity of the radiative cooling metal plate at a wavelength of 0.3 μm to 2.5 μm is less than or equal to 20%, and an attenuations of an average emissivity of the radiative cooling metal plate at a wavelength of 8 μm to 13 μm is also less than or equal to 20%. 
     In one embodiment, an adhesive force of the radiative cooling functional layer is 0 grade tested by a scribe test method. 
     In one embodiment, a thickness of the radiative cooling functional layer is in a range of 50 μm to 300 μm. 
     In one embodiment, the radiative cooling functional layer comprises an emissive layer, a material of the emissive layer comprises a first polymer, a mass ratio of the first polymer to the emissive layer is in a range of 85% to 100% teflon. 
     In one embodiment, the radiative cooling functional layer further comprises a reflective layer and a first protective layer. 
     In one embodiment, the reflective layer is located between the emissive layer and the first adhesive layer, the first protective layer is disposed on a surface of the emissive layer away from the reflective layer, and a ratio of a thickness of the reflective layer to that of the radiative cooling functional layer is in a range of 0.01% to 0.1%. 
     In one embodiment, the reflective layer comprises a middle portion and a packaging portion disposed at both ends of the middle portion, the packaging portion is configured to insulate and protect for the middle portion, a material of the middle portion comprises at least one of silver, aluminum, stainless steel, titanium, gold and copper, and a material of the packaging portion comprises alloy and/or metal oxide. 
     In one embodiment, a material of the first protective layer comprises a second polymer and a third polymer, a material of the second polymer is at least one of high weather resistance polyester, polyvinylidene fluoride, ethylene-tetrafluoroethylene copolymer, teflon and fluorocarbon resin, a material of the third polymer is poly methyl methacrylate, a mass ratio of the second polymer to the third polymer is 50:45-75:10. 
     In one embodiment, a thickness of the first protective layer is in a range of 20 μm to 150 μm. 
     In one embodiment, the radiative cooling metal plate further comprises a second adhesive layer disposed between the emissive layer and the first protective layer. 
     In one embodiment, a material of the first adhesive layer is a solvent type adhesive comprising at least one of polyurethane, polyacrylate, organosilicon, rubber and epoxy. 
     In one embodiment, a material of the first adhesive layer is a film type hot melt adhesive comprising at least one of ethylene acrylic acid copolymer, ethylene-vinyl acetate copolymer, poly methyl methacrylate, maleic anhydride grafted polymer, hydrogenated styrene-butadiene block copolymer, styrene-isoprene-styrene block copolymer, polystyrene-butadiene copolymer, polyurethane, hydrogenated petroleum resin, rosin resin, ethylene-butene copolymer and ethylene-octene copolymer. 
     In one embodiment, a thickness of the first adhesive layer is in a range of 3 μm to 25 μm. 
     In one embodiment, the radiative cooling metal plate further comprises a second protective layer which is a release layer, the second protective layer is disposed on a surface of the first protective layer away from the emissive layer, a material of the second protective layer comprises one of polyethylene terephthalate, polyethylene and polypropylene, a bonding force of the second protective layer is in a range of 50 g/25 mm to 500 g/25 mm. 
     In one embodiment, a thickness of the metal substrate is in a range of 100 μm to 2000 μm. 
     According to another aspect of the present disclosure, a method for preparing the above radiative cooling metal plate is provided, including following steps: 
     providing the metal substrate; and 
     forming the first adhesive layer and the radiative cooling functional layer in order on the surface of the metal substrate. 
     In one embodiment, before the step of forming the first adhesive layer and the radiative cooling functional layer in order on the surface of the metal substrate, further comprising a step of cleaning the metal substrate. 
     According to another aspect of the present disclosure, a radiative cooling profiled metal plate is provided, wherein the radiative cooling profiled metal plate is formed by pressing the radiative cooling metal plate with a dedicated pressing device by a cold roll forming method. 
     Compared with the prior art, the preparation method of the present disclosure has the following advantages: 
     Firstly, the elongation at break of the radiative cooling functional layer is in a range of 1% to 300%, so that the radiative cooling functional layer can have sufficient ductility, and can have sufficient deformation to cope with the bending of the radiative cooling functional layer during pressing, biting and mounting. The radiative cooling functional layer will not be damaged or broken, thereby ensuring the structural integrity of the radiative cooling functional layer and great radiative cooling effect of the metal substrate. Secondly, the radiative cooling metal plate will not easy to thermal expansion, cold contraction or brittleness, and its structure is stable and reliable during outdoor use, and the radiative cooling metal plate has a relatively long service life. When the radiative cooling metal plate is applied, the indoor air temperature of a building can be decreased by about 5 degrees centigrade to 10 degrees centigrade without energy consumption than when the radiative cooling metal plate is not used, and energy consumption of an air conditioning can be decreased while the human body comfortability can be improved, which has a certain application prospect. Thirdly, the radiative cooling functional layer can be tightly attached to the metal substrate by the additional first adhesive layer, thus avoiding the problem that the radiative cooling functional layer is easily fall out when the radiative cooling functional layer can be directly contacted to the metal substrate with no additional adhesive layer. 
     The method for preparing the radiative cooling metal plate of the present disclosure is simple and reliable, and the obtained radiative cooling functional layer is prevented from being damaged or broken during the pressing process. 
     The radiative cooling metal plate of the present disclosure also has good radiative cooling effect, simple structure, easy transportation, high installation efficiency, and simple and reliable construction operations. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       For better description and illustration of embodiments and/or examples of the present disclosures herein, reference may be made to one or more of the figures. Additional details or examples for describing the figures should not be considered limiting of the scope of the present disclosure, the presently described embodiments and/or examples, and the best modes of the present disclosure as presently understood. 
         FIG.  1    is a schematic diagram of a radiative cooling metal plate in one embodiment of the present disclosure. 
         FIG.  2    is a schematic diagram of a reflective layer of a radiative cooling metal plate in another embodiment of the present disclosure. 
         FIG.  3    is a schematic diagram of a biting type radiative cooling profiled metal plate in another embodiment of the present disclosure. 
         FIG.  4    is a schematic diagram of a lapping type radiative cooling profiled metal plate in another embodiment of the present disclosure. 
         FIG.  5    is a schematic diagram of a fixed connection between a first biting portion and a second biting portion in another embodiment of the present disclosure. 
         FIG.  6    is a schematic diagram of a fixed connection between a first lapping portion and a second lapping portion in another embodiment of the present disclosure. 
     
    
    
     In the drawings: 
       100  represents a radiative cooling metal plate,  10  represents a metal substrate,  20  represents a first adhesive layer,  30  represents a radiative cooling functional layer,  31  represents an emissive layer,  32  represents a first protective layer,  33  represents a reflective layer,  331  represents a middle portion,  332  represents a packaging portion,  40  represents a second protective layer,  51  represents a first biting portion,  52  represents a second biting portion,  61  represents a first lapping portion,  62  represents a second lapping portion,  60  represents a fastener,  70  represents a seal element, and  80  represents a mounting bracket. 
     DETAILED DESCRIPTION 
     The technical proposals of the embodiments of the present disclosure will be clearly and completely described below by combining with drawings. It is obvious that the described embodiments are only a part and not all of the embodiments of the present disclosure. All other embodiments obtained by one skilled in the art based on the embodiments of the present disclosure without any creative efforts are within the scope of the present disclosure. 
     Unless otherwise defined, all technical and scientific terms used herein are the same as commonly understood by those skilled in the art. The terms used herein in the description of the present disclosure are for the purpose of describing particular embodiments only and are not intended to be limiting the scope of the present disclosure. As used herein, the term “and/or” includes any and all combinations of one or more related listed items. 
     The terms “first”, “second” and the like herein are used to distinguish different objects, rather than to describe a particular order. Furthermore, the terms “comprising” and “having” and any variations thereof herein are intended to cover non-exclusive inclusion. 
     Radiative cooling is characterized by emitting heat from an object or a surface in a form of heat radiation, thereby lowering the temperature of the object or the surface, or maintaining a relatively low temperature when operating in a steady state. The heat radiation emitted from the non-zero temperature surface (with unit as K) depends on the continuous wavelength or spectrum of the surface temperature. The heat radiation emitted by objects near room temperature is mostly in the infrared regions of the electromagnetic spectrum. 
     The radiative cooling metal plate provided by the present disclosure can convert heat into an electromagnetic wave of a specific wavelength band (in a wavelength range of 8 μm to 13 μm), and radiate heat energy through an “atmospheric window” of the Earth (in a wavelength range of 8 μm to 13 μm) to outside space in a heat radiation manner. 
     Referring to  FIG.  1   , it is a schematic structural view of a radiative cooling metal plate  100  provided by a preferred embodiment of the present disclosure. 
     The radiative cooling metal plate  100  can include a metal substrate  10 , a first adhesive layer  20  and a radiative cooling functional layer  30  stacked in order. The radiative cooling functional layer  30  is disposed on a surface of the metal substrate  10 . And the first adhesive layer  20  is disposed between the metal substrate and the radiative cooling functional layer  30 . 
     The radiative cooling functional layer  30  has an elongation at break of 1% to 300%. There are two reasons for selecting the elongation at break with this range. Firstly, sufficient ductility can lead to a sufficient deformation in order to cope with the bending of the radiative cooling functional layer  30  during a pressing process, so that the radiative cooling functional layer  30  will not be damaged or broken, thereby ensuring a structural integrity of the radiative cooling functional layer  30  and a radiative cooling effect of the radiative cooling metal plate  100 . Secondly, in the process of disposing the radiative cooling functional layer  30  on the metal substrate  10 , if the ductility of the radiative cooling functional layer  30  is too high, the radiative cooling functional layer  30  is more stretched; and after disposing, the radiative cooling functional layer  30  may shrink due to its own stress. However, the metal substrate  10  is relatively stable, and then the radiative cooling functional layer  30  and the metal substrate  10  may generate a large stress difference. Thus, the radiative cooling functional layer  30  may be peeled off from the metal substrate  10 . In order to avoid such a phenomenon, the elongation at break of the radiative cooling functional layer  30  specifically selects such described range. 
     When the radiative cooling metal plate  100  is applied, the indoor air temperature of a building can be decreased by about 5 degrees centigrade to 10 degrees centigrade without energy consumption than when the radiative cooling metal plate  100  is not used. And energy consumption of the air conditioning can be decreased while the human body comfort is raised, which has a certain economic application prospect. 
     The ductility of the radiative cooling functional layer  30  is proportional to the elongation at break thereof. The higher the elongation at break is, the better the ductility is. And preferably, the elongation at break of the radiative cooling functional layer  30  is in a range of 20% to 100%. 
     Because in the radiative cooling metal plate  100 , the metal substrate  10  is passively cooled by the radiative cooling functional layer  30 , the radiative cooling functional layer  30  has an average reflectivity of 75% in the wavelength of 0.3 μm to 2.5 μm, and an average emissivity of 85% in the wavelength of 8 μm to 13 μm. The radiative cooling effect of the radiative cooling functional layer  30  can greatly protect the metal substrate  10 , such that the metal substrate  10  will not heat-expand and contract due to ambient temperature change during outdoor use, thereby it is not easy to brittle. Both the structure and performance of the radiative cooling metal plate  100  can be stable and reliable, and the service life can be extended. 
     Furthermore, there will be a good bonding force between the radiative cooling functional layer  30  and the metal substrate  10 , and an adhesion force of the radiative cooling functional layer  30  is tested to be 0 grade by a scribe test method. 
     Furthermore, the radiative cooling functional layer  30  has a great passive cooling effect, and can also ensure that the first adhesive layer  20  has a better stability, and improve the bonding force between the radiative cooling functional layer  30  and the metal substrate  10 . 
     Considering the radiative cooling metal plate  100  may be applied in outdoor, properties of certain corrosion resistance and weather resistance may be required when installing and using. Therefore, under any one of three following conditions where a xenon lamp aging time is greater than or equal to 1000 hours, a wet heat aging time is greater than or equal to 1000 hours, and a salt spray aging time is greater than or equal to 600 hours, an attenuations of an average reflectivity of the radiative cooling metal plate  100  at a wavelength of 0.3 μm to 2.5 μm is less than or equal to 20%, and an attenuations of an average emissivity of the radiative cooling metal plate  100  at a wavelength of 8 μm to 13 μm is also less than or equal to 20%. 
     Because the radiative cooling functional layer  30  is better to have hydrophobic and dustproof performances, a contact angle between the radiative cooling functional layer  30  and water in a preferred embodiment is greater than or equal to 90°. Generally, the larger the contact angle is, the smaller the wettability is, and the smaller the spreading is. Accordingly, a larger contact angle indicates that the radiative cooling functional layer  30  has a better hydrophobic effect. Preferably, the contact angle between the radiative cooling functional layer  30  and water is greater than or equal to 100 degrees. 
     In the present preferred embodiment, the radiative cooling functional layer  30  comprises a reflective layer  33 , an emissive layer  31  and a first protective layer  32 . The first protective layer  32  is disposed on a surface of the emissive layer  31  away from the reflective layer  33 , so as to form a weather resistance protection for the reflective layer  33  and the emissive layer  31 . The reflective layer  33  is disposed between the emissive layer  31  and the first adhesive layer  20 . The radiative cooling functional layer  30  may break during pressing, and specifically, the elongation at break of the radiative cooling functional layer  30  depends on the emissive layer  31  and the first protection layer  32 . When one of the emissive layer  31  and the first protection layer  32  is damaged, it can be determined that the radiative cooling functional layer  30  is damaged. 
     Furthermore, a material of the emissive layer  31  can include a first polymer. The first polymer can include at least one of poly (4-methyl-1-pentene), polyethylene terephthalate, polyethylene naphthalate, poly 1,4-cyclohexylene dimethylene terephthalate, poly (ethylene terephthalateco-1, 4-cyclohexylene dimethylene terephthalate), poly (ethylene terephthalate-acetate), poly methyl methacrylate, polycarbonate, acrylonitrile styrene copolymer, acrylonitrile-butadiene styrene terpolymer, polyvinyl chloride, polypropylene, polyethylene, polyamide, ethylene-methyl acrylate copolymer, polyhydroxyethyl methacrylate, teflon, perfluoro(ethylene-propylene) copolymer, polyperfluoroalkoxy resin, polytrifluorochloroethylene, ethylene-chlorotrifluoroethylene copolymer, ethylene-tetrafluoroethylene copolymer, polyvinylidene fluoride,polyfluoroethylene, thermoplastic polyurethane, and polystyrene. 
     Preferably, the material of the emissive layer  31  can include at least one of poly (4-methyl-1-pentene), polyethylene terephthalate, polyethylene naphthalate, poly 1,4-cyclohexylene dimethylene terephthalate, poly (ethylene terephthalateco-1, 4-cyclohexylene dimethylene terephthalate), poly (ethylene terephthalate-acetate), poly methyl methacrylate, polycarbonate, ethylene-tetrafluoroethylene copolymer, polyvinylidene fluoride, polyfluoroethylene, and polystyrene. 
     Furthermore, the mass fraction of the first polymer to the emissive layer  31  is in a range of 85% to 100%. 
     In the present embodiment, a process of preparing the emissive layer  31  can include: conveying raw material, drying at a temperature of 50 degrees centigrade to 150 degrees centigrade, melt extruding at a processing temperature of 240 degrees centigrade to 280 degrees centigrade, casting, cooling at a cold roll temperature of 20 degrees centigrade to 150 degrees centigrade, drawing and winding in a range of a longitudinal drawing ratio of 4:1 to 10:1. 
     Considering the elongation at break of the radiative cooling functional layer  30  may be directly affected by the elongation at break of the emissive layer  31 , in the present preferred embodiment, the elongation at break of the emissive layer  31  can be in a range of 20% to 280%, wherein a longitudinal elongation at break of the emissive layer  31  can be in a range of 20% to 280%, and a transverse elongation at break of the emissive layer  31  can be a range of 20% to 280%. More preferably, the elongation at break of the emissive layer  31  can be in a range of 20% to 160%, wherein the longitudinal elongation at break of the emissive layer  31  can be in a range of 40% to 160%, and the transverse elongation at break of the emissive layer  31  can be in a range of 20% to 120%. It can be understood that the minimum and maximum values of the elongation at break of the emissive layer  31  are determined by the minimum and maximum values of the transverse elongation at break and the longitudinal elongation at break thereof, respectively. 
     Furthermore, the emissive layer  31  can further include a filler. The filler can include at least one of an inorganic filler and an organic filler. The organic filler can be one or more of acrylic resin particles, silicone resin particles, and polystyrene resin particles. The inorganic filler can be one or more of silicon dioxide, silicon carbide, silicon nitride, aluminum hydroxide, aluminum oxide, zinc oxide, barium sulfide, magnesium silicate, barium sulfate, calcium carbonate, titanium dioxide, and titanium nitride. A particle size of the filler can be in a range of 0.1 μm to 20 μm. 
     Considering the filler and the first polymer uniformity dispersing in the emissive layer  31  and the emissivity of the emissive layer  31 , the filler is preferably one or more of silicon dioxide, silicon carbide, silicon nitride, titanium nitride, titanium dioxide, silicone-based resin particles and polystyrene-based resin particles. The particle size of the filler is preferably in a range of 1 μm to 10 μm. The main influence factors of the elongation at break of the emissive layer  31  include a mass fraction of the filler in the emissive layer  31 , the processing temperature of the emissive layer  31 , and the longitudinal drawing ratio in processing. For example, if the mass fraction of the filler in the emissive layer  31  is increased, the emissivity of the emissive layer  31  may be increased, and if the mass fraction of the filler is decreased, the elongation at break of the emissive layer  31  may be increased; if the longitudinal drawing ratio after the casting is increased, the molecular orientation may be increased, and the molecular chain of the emissive layer  31  may be easily broken, such that the elongation at break may be decreased; and if the longitudinal drawing ratio after the casting is decreased, the transparency of the emissive layer  31  may be affected, and the appearance of the emissive layer  31  may further be affected; if the processing temperature is increased, the molecular chain of the emissive layer  31  may be easily broken and the elongation at break may be decreased; if the processing temperature is low, the fluidity of high molecular compound may be poor and the appearance of the emissive layer  31  may be affected. Therefore, in the present disclosure, the mass fraction of the filler in the emissive layer  31  is selected to be in a range of 0.1% to 10%, the processing temperature is in a range of 240 degrees centigrade to 280 degrees centigrade, and the longitudinal drawing ratio is in a range of 4:1 to 10:1. 
     Specifically, a plurality of experiments are also taken to prove the relationship between the main influence factors of the elongation at break of the emissive layer  31  and the elongation at break thereof as shown in Table 1 below. 
     
       
         
           
               
               
             
               
                   
                 TABLE 1 
               
             
            
               
                   
                   
               
               
                   
                 Elongation at break/% 
               
            
           
           
               
               
               
            
               
                 Influence factors (range) 
                 Transverse 
                 Longitudinal 
               
               
                   
               
            
           
           
               
               
               
               
            
               
                 Mass fraction of the filler in the emissive 
                 0.1%-10%  
                  1-280 
                 20-300 
               
               
                 layer 
               
               
                 (wherein the processing temperature is 260 
               
               
                 degrees centigrade and the longitudinal 
               
               
                 drawing ratio is 6:1) 
               
               
                 Processing temperature (wherein the mass 
                 240 degrees 
                 20-280 
                 40-300 
               
               
                 fraction of the filler in the emissive layer is 
                 centigrade- 
               
               
                 1% and the longitudinal drawing ratio is 6:1) 
                 280 degrees 
               
               
                   
                 centigrade 
               
               
                 Longitudinal drawing ratio (wherein the 
                  4:1-10:1 
                 30-280 
                 50-300 
               
               
                 processing temperature is 260 degrees 
               
               
                 centigrade and the mass fraction of the filler 
               
               
                 in the emissive layer is 1%) 
               
               
                   
               
            
           
         
       
     
     Preferably, a plurality of experiments are also taken to prove the relationship between the main influence factors of the elongation at break of the emissive layer  31  and the elongation at break thereof as shown in Table 2 below. 
     
       
         
           
               
               
             
               
                   
                 TABLE 2 
               
             
            
               
                   
                   
               
               
                   
                 Preferable elongation at 
               
               
                   
                 break/% 
               
            
           
           
               
               
               
            
               
                 Influence factors (Preferable range) 
                 Transverse 
                 Longitudinal 
               
               
                   
               
            
           
           
               
               
               
               
            
               
                 Mass fraction of the filler in the emissive 
                 0.5%-8%   
                 20-120 
                 40-160 
               
               
                 layer 
               
               
                 (wherein the processing temperature is 260 
               
               
                 degrees centigrade and the longitudinal 
               
               
                 drawing ratio is 6:1) 
               
               
                 Processing temperature (wherein the mass 
                 170 degrees 
                 40-120 
                 60-160 
               
               
                 fraction of the filler in the emissive layer is 
                 centigrade- 
               
               
                 1% and the longitudinal drawing ratio is 6:1) 
                 250 degrees 
               
               
                   
                 centigrade 
               
               
                 Longitudinal drawing ratio (wherein the 
                 5:1-8:1 
                 40-120 
                 60-160 
               
               
                 processing temperature is 260 degrees 
               
               
                 centigrade and the mass fraction of the filler 
               
               
                 in the emissive layer is 1%) 
               
               
                   
               
            
           
         
       
     
     Of course, in addition to the first polymer and the filler, the emissive layer  31  can further include an additive. The additive is a processing aid, and the processing aid can be one or more of an antioxidant, a flame retardant, a plasticizer, a heat stabilizer, a light stabilizer, and an antistatic agent. 
     Furthermore, in order to improve the weather resistance of the first protective layer  32 , a material of the first protective layer  32  includes a second polymer and a third polymer. A material of the second polymer is at least one of high weather resistance polyester, polyvinylidene fluoride, ethylene-tetrafluoroethylene copolymer, teflon and fluorocarbon resin. A material of the third polymer is poly methyl methacrylate. A mass ratio of the second polymer to the third polymer is 50:45-75:10. Of course, the first protective layer  32  may further include other additives. 
     Furthermore, a process of preparing the first protective layer  32  can include: conveying raw material, drying at a temperature of 50 degrees centigrade to 150 degrees centigrade, melt extruding at a processing temperature of 185 degrees centigrade to 235 degrees centigrade, casting, cooling at a cold roll temperature of 20 degrees centigrade to 150 degrees centigrade, drawing and winding in a range of a longitudinal drawing ratio of 4:1 to 8:1. 
     Considering that the elongation at break of the radiative cooling functional layer  30  is directly affected by the elongation at break of the first protective layer  32 , in a preferred embodiment, the elongation at break of the first protective layer  32  can be in a range of 1% to 300%, wherein a longitudinal elongation at break of the first protective layer  32  can be in a range of 30% to 300%, and a transverse elongation at break of the first protective layer  32  can be in a range of 1% to 150%. More preferably, the elongation at break of the first protective layer  32  can be in a range of 20% to 200%, wherein the longitudinal elongation at break of the first protective layer  32  can be in a range of 50% to 200%, and the transverse elongation at break of the first protective layer  32  can be in a range of 20% to 100%. It can be understood that the minimum value of the elongation at break of the first protective layer  32  is determined by the minimum value of the transverse elongation at break thereof, and the maximum value of the elongation at break of the first protective layer  32  is determined by the maximum value of the longitudinal elongation at break. 
     Furthermore, the main influence factors of the elongation at break of the first protective layer  32  include the mass ratio of the second polymer to the third polymer in the first protective layer  32 , the processing temperature of the first protective layer  32 , and the longitudinal drawing ratio during processing. In the present disclosure, the mass ratio of the second polymer to the third polymer in the first protective layer  32  is (50-75):(10-45), the processing temperature is in a range of 185 degrees centigrade to 235 degrees centigrade, and the longitudinal drawing ratio is in a range of 4:1 to 8:1. Specifically, a plurality of experiments are also taken to prove the relationship between the main influence factors of the elongation at break of the first protective layer  32  and the elongation at break thereof as shown in Table 3 below. 
     
       
         
           
               
               
             
               
                   
                 TABLE 3 
               
             
            
               
                   
                   
               
               
                   
                 Elongation at break/% 
               
            
           
           
               
               
               
            
               
                 Influence factors (range) 
                 Transverse 
                 Longitudinal 
               
               
                   
               
            
           
           
               
               
               
               
            
               
                 Mass ratio of the second polymer to the third 
                 (50-75):(10- 
                  1-150 
                 30-300 
               
               
                 polymer 
                 45) 
               
               
                 (wherein the processing temperature is 200 
               
               
                 degrees centigrade and the longitudinal 
               
               
                 drawing ratio is 6:1) 
               
               
                 Processing temperature (wherein the mass 
                 185 degrees 
                 30-150 
                 50-300 
               
               
                 ratio of the second polymer to the third 
                 centigrade- 
               
               
                 polymer is 60:20 and the longitudinal 
                 235 degrees 
               
               
                 drawing ratio is 6:1) 
                 centigrade 
               
               
                 Longitudinal drawing ratio (wherein the mass 
                 4:1-8:1 
                 50-150 
                 80-300 
               
               
                 ratio of the second polymer to the third 
               
               
                 polymer is 60:20 and the processing 
               
               
                 temperature is 200 degrees centigrade) 
               
               
                   
               
            
           
         
       
     
     Preferably, a plurality of experiments are also taken to prove the relationship between the main influence factors of the elongation at break of the first protective layer  32  and the elongation at break thereof as shown in Table 4 below. 
     
       
         
           
               
               
             
               
                   
                 TABLE 4 
               
             
            
               
                   
                   
               
               
                   
                 Preferable elongation at 
               
               
                   
                 break/% 
               
            
           
           
               
               
               
            
               
                 Influence factors (Preferable range) 
                 Transverse 
                 Longitudinal 
               
               
                   
               
            
           
           
               
               
               
               
            
               
                 Mass ratio of the second polymer to the third 
                 (55-70):(20- 
                 20-100 
                 50-200 
               
               
                 polymer 
                 40) 
               
               
                 (wherein the processing temperature is 200 
               
               
                 degrees centigrade and the longitudinal 
               
               
                 drawing ratio is 6:1) 
               
               
                 Processing temperature (wherein the mass 
                 195 degrees 
                 20-100 
                 50-200 
               
               
                 ratio of the second polymer to the third 
                 centigrade- 
               
               
                 polymer is 60:20 and the longitudinal 
                 225 degrees 
               
               
                 drawing ratio is 6:1) 
                 centigrade 
               
               
                 Longitudinal drawing ratio (wherein the mass 
                 5:1-7:1 
                 20-100 
                 50-200 
               
               
                 ratio of the second polymer to the third 
               
               
                 polymer is 60:20 and the processing 
               
               
                 temperature is 200 degrees centigrade) 
               
               
                   
               
            
           
         
       
     
     A material of the reflective layer  33  may be metal or any other solar reflective material, such as at least one of silver, aluminum, stainless steel, titanium, gold, and copper. In a preferred embodiment, the material of the reflective layer  33  can include at least one of silver, aluminum, gold and copper. 
     In a preferred embodiment, as shown in  FIG.  2   , the reflective layer  33  includes a middle portion  331  and a packaging portion  332  disposed at both ends of the middle portion  331 . And the packaging portion  332  is configured to protect the middle portion  331  from corrosion caused by permeation of gas or water molecules. 
     Preferably, a material of the middle portion  331  can include at least one of silver, aluminum, stainless steel, titanium, gold and copper, and a material of the packaging portion  332  can include at least one of an alloy and a metal oxide. The alloy of the package region  332  can include at least two of an Rn element, a Co element, a Cu element, an In element, an Nd element, a Ge element, an Sn element, an Si element, a Pt element, a Pd element, a Zn element, a Cd element, and an Au element. In this way, the obtained reflective layer  33  can extend the service life of the reflective layer  33  and prevent a problem of yellow edge aging in the middle portion  331  due to the alloy material of the packaging region  332 . 
     Preferably, a thickness of the radiative cooling functional layer  30  is in a range of 50 μm to 300 μm, and a thickness of the first protection layer  32  is in a range of 20 μm to 150 μm. 
     Furthermore, a ratio of the thickness of the reflective layer  33  to that of the radiative cooling functional layer  30  can be in a range of 0.01% to 0.1%. 
     In a preferred embodiment, the reflective layer  33  can be a thin layer, which is deposited on a surface of the emissive layer  31  by magnetron sputtering, evaporating a coating film, ion sputtering, electroplating or electron beam coating. The influence of the reflective layer  33  on the elongation at break of the radiative cooling functional layer  30  is small, which may not be considered. 
     Due to the material of the emissive layer  31  including the first polymer, the emissive layer  31  can provide better ductility and ensure that the radiative cooling functional layer  30  does not break when the radiative cooling functional layer  30  is pressed. 
     Because the radiative cooling functional layer  30  should have a good adhesive effect with the metal substrate  10  during use to avoid degumming, the attenuation of the adhesive performance of the first adhesive layer  20  on the metal substrate in a present preferred embodiment is less than or equal to 2 grades under any condition of the xenon lamp aging time of greater than or equal to 1000 h, the wet heat aging time of greater than or equal to 1000 hours, and the salt spray aging time of greater than or equal to 600 hours. 
     When the thickness of the first adhesive layer  20  exceeds a certain value, phenomena of bubbling and wrinkling may show on a surface of the radiative cooling profiled metal plate, resulting in effecting the performance of the radiative cooling metal plate. The reason is that in a rolling process of the radiative cooling metal plate  100 , the first adhesive layer  20  therein may be deformed due to stress; especially when the first adhesive layer  20  is thicker, the deformation are obvious. So that the phenomena of bubbling and wrinkling will show on the surface of the radiative cooling metal plate. Therefore, in order to avoid such phenomena, the thickness of the first adhesive layer  20  is preferably in a range of 3 μm to 25 μm. More preferably, the thickness of the first adhesive layer  20  is in a range of 5 μm to 20 μm. In general, the thickness of the first adhesive layer  20  is proportional to the adhesive force, the larger the thickness of the first adhesive layer  20  is, the larger the adhesive force between the radiative cooling functional layer  30  and the metal substrate  10  is. In a preferable embodiment, the material of the first adhesive layer  20  may be a solvent type adhesive, and the first adhesive layer  20  is formed by coating the solvent type adhesive on a surface of the metal substrate  10  and solidifying the solvent type adhesive. The material of the first adhesive layer  20  can include at least one of polyurethane, polyacrylate, organosilicon, rubber and epoxy. 
     In another preferable embodiment, the material of the first adhesive layer may be a film type hot melt adhesive, for example, a double-sided adhesive, which is used for bonding the radiative cooling functional layer  30  and the metal substrate  10  together. The material of the first adhesive layer  20  can include at least one of ethylene acrylic acid copolymer (EAA), ethylene-vinyl acetate copolymer (EVA), poly methyl methacrylate (PMMA), maleic anhydride grafted polymer, hydrogenated styrene-butadiene block copolymer (SEBS), styrene-isoprene-styrene block copolymer (SIS), polystyrene-butadiene copolymer (SBS), polyurethane (TPU), hydrogenated petroleum resin, rosin resin, ethylene-butene copolymer and ethylene-octene copolymer. 
     Specifically, when the first adhesive layer  20  is made of the film type hot melt adhesive, the adhesive temperature of the film type hot melt adhesive is in a range of 70 degrees centigrade to 150 degrees centigrade, and the adhesive pressure thereof is in a range of 0.1 MPa to 3 MPa. 
     Furthermore, the radiative cooling functional layer  30  further comprises a second adhesive layer disposed between the emissive layer  31  and the first protection layer  32 . In order to improve the service life of the second adhesive layer, the second adhesive layer can further include an ultraviolet barrier, and the ultraviolet barrier can absorb ultraviolet lights and prevent aging of the emissive layer  31  and the reflective layer  33 . The ultraviolet barrier can include at least one of benzophenones, benzotriazoles, and hindered amines. 
     In a preferred embodiment, a material of the metal substrate  10  can include at least one of an aluminum alloy, an aluminum magnesium manganese, a zinc plating plate, a tin plating plate, a composite steel, and a color coating steel. Preferably, a thickness of the metal substrate  10  is in a range of 100 μm to 2000 μm. 
     Further, in order to better protect the radiative cooling functional layer  30  and prevent the radiative cooling functional layer  30  from being damaged or broken by bending during subsequent pressing and installation, the radiative cooling metal plate  100  further can include a second protective layer  40 . The second protective layer  40  can be a release layer, which is detachably disposed on one side of the first protective layer  32  away from the radiative cooling functional layer  30 . And a material of the second protective layer  40  can include one of polyethylene terephthalate (PET), polyethylene (PE), and polypropylene (PP). 
     The second protection layer  40  can effectively protect the radiative cooling functional layer  30 . In general, the second protective layer  40  may be peeled off from the surface of the radiative cooling functional layer  30  after the mounting is completed. 
     A pencil hardness of the second protective layer  40  is in a range of H to  4 H, such that the second protective layer  40  can be pressed together with the radiative cooling functional layer  30 , and the radiative cooling functional layer  30  can be prevented from scratching during pressing and mounting. 
     Preferably, a thickness of the second protective layer  40  is in a range of 30 μm to 100 μm, and more preferably, in a range of 40 μm to 75 μm. 
     Preferably, an adhesive force of the second protective layer  40  is in a range of 50 g/25 mm to 500 g/25 mm, and more preferably, in a range of 100 g/25 mm to 300 g/25 mm. 
     Due to the radiative cooling functional layer  30 , the radiative cooling metal plate  100  of the present disclosure can have both high emissivity and high reflectivity and dissipate heat to the external space in highly efficiency without substantially absorbing solar heat, and meanwhile has the advantages of easy processing, transportation and disassembly because of the metal substrate  10 , such that it is applicable to construct various types of buildings and repair peripheral shielding structures of buildings, for example, exterior walls and roofs of airports, high-speed railway stations, factories, warehouses and outdoor equipment such as electric cabinets. 
     Because a surface of the metal substrate  10  is generally rough, if the radiative cooling functional layer  30  is directly disposed thereon, the radiative cooling functional layer  30  may be easy to fall off because of poor adhesive effect. So that it is better to clean the surface of the metal substrate  10  firstly to remove impurities by a cleaning agent. Then the radiative cooling functional layer  30  and the metal substrate  10  can be easily bonded to each other, thereby making coating the radiative cooling functional layer  30  on the metal substrate  10  easier and accelerating the processing speed. In addition, the surface of the metal substrate  10  after cleaning is relatively smooth. When the radiative cooling functional layer  30  is bonded to the metal substrate  10 , air bubbles between the two are relatively small, and the service life of the radiative cooling functional layer  30  can be avoided from being affected by water and oxygen. 
     A preferred embodiment of the present disclosure provides a method for preparing a radiative cooling metal plate  100 . The method includes the following steps: 
     (1) providing a metal substrate  10 ; and 
     (2) forming a first adhesive layer  20  and a radiative cooling functional layer  30  on a surface of the metal substrate  10  sequentially. 
     Furthermore, the method can further include: 
     (3) cleaning the surface of the metal substrate  10  before the step of forming the first adhesive layer  20  and the radiative cooling functional layer  30  on the surface of the metal substrate  10  sequentially. 
     In a preferred embodiment, the step of cleaning the surface of the metal can further include: 
     (3.1) providing a cleaning agent, and wetting the surface of the metal substrate  10  by the cleaning agent; 
     (3.2) brushing the surface of the metal substrate  10 ; 
     (3.3) spraying the surface of the metal substrate  10  with the cleaning agent; 
     (3.4) drying the cleaned metal substrate  10 ; and/or, 
     (3.5) purging the surface of the metal substrate  10  using an external fan. 
     After the cleaning process, a roughness of the surface of the metal substrate  10  can be significantly reduced; specifically the dyne value of the metal substrate  10  is greater than 42 mN/m. In this way, when the radiative cooling functional layer  30  and the metal substrate  10  are bonded to each other, air bubbles can be significantly reduced between the radiative cooling functional layer  30  and the metal substrate  10  and they are easily adhere to each other. 
     In one embodiment, the step (2) of forming the first adhesive layer  20  and the radiative cooling functional layer  30  sequentially on the surface of the metal substrate  10  can further include: 
     (2.1) providing a solvent type adhesive, coating solvent type adhesive on the surface of the metal substrate  10 , and baking the solvent type adhesive until the solvent in the solvent type adhesive evaporates to be a semi-dry state, and forming the first adhesive layer  20 ; 
     (2.2) providing the radiative cooling functional layer  30  and disposing the radiative cooling functional layer  30  on a surface of the first adhesive layer  20 .Or, 
     In another embodiment, the step (2) of forming the first adhesive layer  20  and the radiative cooling functional layer  30  sequentially on the surface of the metal substrate  10  can further include: 
     (2.3) providing a film type hot melt adhesive, and casting the film type hot melt adhesive to the surface of the radiative cooling functional layer  30  to form the first adhesive layer  20 , and heating a steel plate to bond the first adhesive layer  20  on the steel plate; 
     (2.4) heating the metal substrate  10 , transferring and disposing the radiative cooling functional layer  30  to the surface of the metal substrate  10  through the first adhesive layer  20 . 
     Furthermore, the method can further include: 
     (4) providing a second protective layer  40 , disposing the second protective layer  40  on a side of the radiative cooling functional layer  30  away from the first adhesive layer  20 . 
     The preparation method of the radiative cooling metal plate  100  of the present disclosure is simple and reliable. The radiative cooling functional layer  30  can be effectively protected from being damaged and does not easily fall off during the pressing process. 
     It should be noted that various steps in the flowcharts herein are not necessarily performed sequentially in the order of the reference signs. The execution of these steps is not limited in strict order unless expressly described herein, and these steps may be performed in other order. Moreover, at least a part of the steps in the flowchart may include a plurality of sub-steps or a plurality of stages. These sub-steps or stages are not necessarily performed at the same time. Instead, it can be executed at different moments. The execution order of these sub-steps or stages is not necessarily performed successively. Instead, it may be performed alternatively or alternatively with. at least a portion of other steps or the sub-steps or stages of other steps. 
     Referring to  FIGS.  3  to  5    together, a preferred embodiment of the present disclosure provides a radiative cooling profiled metal plate. The radiative cooling profiled metal plate is pressed by the above radiative cooling metal plate  100 . Specifically, a process of pressing the radiative cooling metal plate  100  can include: 
     providing the radiative cooling metal plate  100 , pressing the radiative cooling metal plate  100  with a dedicated pressing device by a cold roll forming method, forming a wavy interface along a width direction of the radiative cooling metal plate  100 , and obtaining a radiative cooling profiled metal plate. According to a watt type and a connection manner, the radiative cooling profiled metal plate is divided into a biting type radiative cooling profiled metal plate and a lapping type radiative cooling profiled metal plate. 
       FIG.  3    shows the schematic diagram of the biting type radiative cooling profiled metal plate, and  FIG.  5    shows a connection manner of a biting type radiative cooling profiled metal plate. 
     The connecting manner of the biting type radiative cooling profiled metal plate is as follows: providing a mounting bracket  80  and the biting type radiative cooling profiled metal plate, wherein an edge of the biting type radiative cooling metal plate are respectively provided with a first biting portion  51  and a second biting portion  52 , and the first biting portion  51  and the second biting portion  52  extend along a longitudinal direction of the biting type radiative cooling profiled metal plate; and fixedly connecting the first biting portion  51  of one biting type radiative cooling profiled metal plate with the second biting portion  52  of another adjacent biting type radiative cooling profiled metal plate via the mounting bracket  80 . 
       FIG.  4    shows a schematic diagram of a lapping type radiative cooling profiled metal plate in another embodiment of the present disclosure, and  FIG.  6    shows a connection manner of the lapping type radiative cooling profiled metal plate. 
     The connection manner of the lapping type radiative cooling profiled metal plate is as follows. The edges of the lapping type radiative cooling profiled metal plate are respectively provided with a first lapping portion  61  and a second lapping portion  62 . The first lapping portion  61  and the second lapping portion  62  extend along the longitudinal direction of the lapping radiative cooling profiled metal plate. The first lapping portion  61  of one lapping type radiative cooling profiled metal plate is connected to the second lapping portion  62  of another adjacent lapping type radiative profiled metal plate by lapping. A fastener  60  is fixed to a building at a flat position of the lapping type radiative cooling profiled metal plate. 
     In one embodiment, the radiative cooling metal plate  100  is protected by the second protective layer  40  adhered outside of the radiative cooling functional layer  30  during the pressing process. After the pressing process, the second protection layer  40  can be peeled off from the surface of the radiative cooling functional layer  30 . Furthermore, if the surface of the radiative cooling functional layer  30  after the peeling is detected to check whether it is damaged, and coating transparent repair paint at the damaged portion for repairing. 
     Preferably, if the surface of the peeled radiative cooling functional layer  30  is damaged, the transparent repair paint may be applied at the damaged portion, and a material of the transparent repair paint includes polyurethane. Furthermore, the coating operation can be repeated at least one time to avoid further enlargement of an area of the damaged portion. 
     Referring to  FIGS.  3  and  5   , the edges of the biting type radiative cooling profiled metal plate are respectively provided with the first biting portion  51  and the second biting portion  52 . The first biting portion  51  and the second biting portion  52  respectively extend in the width direction of the biting type radiative cooling profiled metal plate. The first biting portion  51  is used for fixedly connecting with the second biting portion  52  of the adjacent biting type radiative cooling profiled metal plate via the mounting bracket  80 . By fixedly biting, the biting type radiative cooling metal plate does not need the fastener  60 , so that the biting type radiative cooling profiled metal plate has better wind resistance and waterproof performance. It should be noted that, the first biting portion  51  and the second biting portion  52  may be 180 degrees biting, or 360 degrees biting, resulting in being applied in construction of various types of warehouses and factories. 
     Referring to  FIGS.  4  and  6   , the edges of the lapping type radiative cooling profiled metal plate are respectively provided with the first lapping portion  61  and the second lapping portion  62 . The first lapping portion  61  and the second lapping portion  62  extend along the longitudinal direction of the lapping type radiative cooling profiled metal plate. The first lapping portion  61  is connected to the second lapping portion  62  of the adjacent lapping type radiative cooling profiled metal plate by lapping. The fastener  60  is fixed to the building at a flat position of the lapping type radiative cooling profiled metal plate. 
     Furthermore, the lapping type radiative cooling profiled metal plate can include a seal element  70  disposed between the fastener  60  and the first lapping portion. The fastener  60 , the seal element  70  and the structural adhesive are used for sealing and waterproof treating at the junction, so as to prevent water vapor from entering, and obtain good wind resistance and waterproof performance. The lapping type radiative cooling profiled metal plate can be widely applied to outer wall surfaces of various industrial buildings, and roof structures of small-sized civil buildings or partial industrial buildings, such as factory, carport or warehouses. 
     The methods for mounting the biting type radiative cooling profiled metal plate and the lapping type radiative cooling profiled metal plate of the present disclosure has high efficiency, the construction operation is simple and reliable, and does not affect the radiative cooling effect and the service life. 
     Hereinafter, for better understanding of the present disclosure, preferred embodiments and comparative embodiments are provided. However, they are merely for illustrating the present disclosure and are not limited the scope thereof. 
     Embodiment 1 
     The radiative cooling metal plate can include: 
     an aluminum alloy metal substrate with a thickness of 100 μm; 
     a solvent type adhesive made of polyurethane with a thickness of 3 μm; and 
     a second protective layer made of polyethylene terephthalate with a thickness of 30 μm; 
     a radiative cooling functional layer including: 
     a reflective layer including a middle portion made of pure silver and an alloy layer disposed at both ends of the middle portion and having a thickness of 0.05 μm; 
     an emissive layer including a first polymer including poly 4-methyl-1-pentene, a filler being silica with a particle size of 3 μm, and the remaining being an additive, wherein a mass fraction of the poly 4-methyl-1-pentene in the emissive layer is 92%, a mass fraction of the filler in the emissive layer is 6%, and the thickness of the emissive layer is 50 μm; 
     a first protective layer including a high weather resistance polyester and poly methyl methacrylate, wherein a mass ratio of the high weather resistance polyester to the poly methyl methacrylate is 50:20, and a thickness of the first protective layer is 50 μm; and 
     a second adhesive layer including a benzophenone-based ultraviolet barrier. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 2 
     The radiative cooling metal plate can include: 
     a magnesium aluminum manganese metal substrate with a thickness of 400 μm; 
     a solvent type adhesive made of polyacrylate with a thickness of 4 μm; and 
     a second protective layer made of polyethylene with a thickness of 50 μm; 
     a radiative cooling functional layer including: 
     a reflective layer including a middle portion made of stainless steel and a metal oxide layer disposed at both ends of the middle portion and having a thickness of 0.1 μm; 
     an emissive layer including a first polymer including polyethylene terephthalate, a filler being silicon nitride with a particle size of 5 μm, and the remaining being an additive, wherein a mass fraction of the polyethylene terephthalate in the emissive layer is 88%, a mass fraction of the filler in the emissive layer is 7%, and a thickness of the emissive layer is 100 μm; 
     a first protective layer including polyvinylidene fluoride and poly methyl methacrylate, wherein a mass ratio of polyvinylidene fluoride to poly methyl methacrylate is 60:25, and a thickness of the first protective layer is 20 μm; and 
     a second adhesive layer including a benzotriazole ultraviolet barrier. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 3 
     The radiative cooling metal plate can include: 
     a galvanized metal substrate with a thickness of 900 μm; 
     an solvent type adhesive made of organosilicon with a thickness of 5 μm; and 
     a second protective layer made of polypropylene with a thickness of 100 μm; 
     a radiative cooling functional layer including: 
     a reflective layer including a middle portion made of stainless steel and an alloy layer disposed at both ends of the middle portion and having a thickness of 0.2 μm; 
     an emissive layer including a first polymer including polyethylene naphthalate, a filler being silicon carbide and silicone-based resin particles with a particle size of 0.1 μm (a mass ratio of the silicon carbide to silicone-based resin particles is 1:1), and the remaining being an additive, wherein a mass fraction of the polyethylene naphthalate in the emissive layer is 98%, a mass fraction of the filler in the emissive layer is 0.9%, and a thickness of the emissive layer is 300 μm; 
     a first protective layer including an ethylene-tetrafluoroethylene copolymer and poly methyl methacrylate, wherein a mass ratio of the ethylene-tetrafluoroethylene copolymer to the poly methyl methacrylate is 70:10, and a thickness of the first protective layer is 110 μm; and a second bonding layer including a hindered amine-based ultraviolet barrier. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 4 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a tin-plated metal substrate with a thickness of 1300 μm; 
     a rubber-based solvent type adhesive with a thickness of 6 μm; 
     a radiative cooling functional layer including: 
     a reflective layer including a titanium middle portion and a metal oxide layer disposed at both ends of the titanium middle portion, and having a thickness of 0.12 μm; 
     an emissive layer including a first polymer including a 1,4-cyclohexanedimethanol polyterephthalate, a filler being a silicone-based resin particle with a particle size of 10 μm, and the rest being an additive, wherein a mass fraction of the 1,4-cyclohexanedimethanol polyterephthalate in the emissive layer is 97%, a mass fraction of the filler in the emissive layer is 0.5%, and a thickness of the emissive layer is 200 μm; 
     a first protective layer including teflon and poly methyl methacrylate, wherein a mass ratio of teflon and poly methyl methacrylate is 55:25, and a thickness of the first protective layer is 150 μm. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 5 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a composite steel metal substrate with a thickness of 1700 μm; 
     an solvent type adhesive made of epoxy resin with a thickness of 8 μm; 
     a radiative cooling functional layer including: 
     a reflective layer including a gold middle portion and an alloy layer disposed at both ends of the gold middle portion, and having a thickness of 0.15 μm; 
     an emissive layer including a first polymer including polyethylene terephthalate-1,4-cyclohexanedimethanol ester, a filler being polystyrene-based resin with a particle size of 20 μm, and the rest being an additive, wherein a mass fraction of the polyethylene terephthalate-1,4-cyclohexanedimethanol ester in the emissive layer is 99%, a mass fraction of the filler in the emissive layer is 0.8%; 
     a first protective layer including fluorocarbon resin and poly methyl methacrylate, wherein a mass ratio of the fluorocarbon resin to the poly methyl methacrylate is 75:10, and a thickness of the first protective layer is 120 μm. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 6 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a coated colorful steel metal substrate with a thickness of 2000 μm; 
     a film type adhesive made of ethylene acrylic copolymer with a thickness of 10 μm; 
     a radiative cooling functional layer including: 
     a reflective layer including a copper middle portion and a metal oxide layer disposed at both ends of the copper middle portion, and having a thickness of 0.2 μm; 
     an emissive layer including a first polymer including polyethylene terephthalate, a filler being titanium dioxide and silica (a mass ratio of the titanium dioxide to the silica being 1:1) with a particle size being 15 μm, and the rest being an additive, wherein a mass fraction of the polyethylene terephthalate in the emissive layer is 88%, a mass fraction of the filler in the emissive layer is 8%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 7 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a film type adhesive made of poly methyl methacrylate with a thickness of 12 μm; 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including poly methyl methacrylate, and the rest being an additive, wherein a mass fraction of the poly methyl methacrylate in the emissive layer is 92%, and a mass fraction of the filler in the emissive layer is 5%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 8 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a film type adhesive made of maleic anhydride grafted polymer with a thickness of 15 μm; 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polycarbonate, and the rest being an additive, wherein a mass fraction of the polycarbonate in the emissive layer is 97%, and a mass fraction of the filler in the emissive layer is 1%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 9 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate can include: 
     a film type adhesive made of hydrogenated styrene-butadiene block copolymer with a thickness of 18 μm; 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including acrylonitrile styrene copolymer, and the rest being an additive, wherein a mass fraction of the acrylonitrile styrene copolymer in the emissive layer is 99%, a mass fraction of the filler in the emissive layer is 0.1%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 10 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a film type adhesive made of styrene-isoprene-styrene block copolymer with a thickness of 20 μm; 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including acrylonitrile-butadiene styrene terpolymer, and the rest being an additive, wherein a mass fraction of the acrylonitrile-butadiene styrene terpolymer in the emissive layer is 89%, and a mass fraction of the filler in the emissive layer is 8%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 11 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a film type adhesive made of polystyrene-butadiene copolymer with a thickness of 22 μm; 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polyvinyl chloride, and the rest is an additive, wherein a mass fraction of the polyvinyl chloride in the emissive layer is 91%, and a mass ratio of the filler in the emissive layer is 6%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 12 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a film type adhesive made of polyurethane with a thickness of 25 μm; 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polypropylene, and the rest being an additive, wherein a mass fraction of the polypropylene in the emissive layer is 97%, and a mass fraction of the filler in the emissive layer is 0.9%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 13 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a film type adhesive made of hydrogenated petroleum resin with a thickness of 15 μm; 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polyethylene, and the rest being an additive, wherein a mass fraction of the polyethylene in the emissive layer is 93%, and a mass ratio of the filler in the emissive layer is 4%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 14 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a film type adhesive made of rosin resin with a thickness of 18 μm; 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polyvinylidene fluoride, and the rest being an additive, wherein a mass fraction of the polyvinylidene fluoride in the emissive layer is 89%, and a mass fraction of the filler in the emissive layer is 6%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 15 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a film type adhesive made of ethylene-butene copolymer with a thickness of 12 μm; 
     a radiative cooling functional layer include: 
     an emissive layer including a first polymer including polyvinyl fluoride, and the rest being an additive, wherein a mass fraction of the polyvinyl fluoride in the emissive layer is 88%, and a mass fraction of the filler in the emissive layer is 9%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 16 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling metal plate including: 
     a film type adhesive made of ethylene-octene copolymer with a thickness of 16 μm; 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polyamide, and the rest being an additive, wherein a mass fraction of the polyamide in the emissive layer is 94%, a mass fraction of the filler in the emissive layer is 2%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 17 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polyethylene, and the rest being an additive, wherein the mass fraction of the polyethylene in the emissive layer is 92%, and a mass fraction of filler in the emissive layer is 5%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 18 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including ethylene-methyl acrylate copolymer, and the rest being an additive, wherein a mass fraction of the ethylene-methyl acrylate copolymer in the emissive layer is 87%, and a mass fraction of the filler in the emissive layer is 8%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 19 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polyhydroxyethyl methacrylate, and the rest being an additive, wherein a mass fraction of the polyhydroxyethyl methacrylate in the emissive layer is 93%, and a mass fraction of the filler in the emissive layer is 3%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 20 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including teflon, and the rest being an additive, wherein a mass fraction of the teflon in the emissive layer is 95%, and a mass fraction of the filler in the emissive layer is 0.8%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 21 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including perfluoro(ethylene-propylene) copolymer, and the rest being an additive, wherein a mass fraction of the perfluoro(ethylene-propylene) copolymer in the emissive layer is 99%, and a mass fraction of the filler in the emissive layer is 0.1%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 22 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polyperfluoroalkoxy resin, and the rest being an additive, wherein a mass fraction of the polyperfluoroalkoxy resin in the emissive layer is 85%, and a mass ratio of the filler in the emissive layer is 10%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 23 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polytrifluorochloroethylene, and the rest being an additive, wherein a mass fraction of the polytrifluorochloroethylene in the emissive layer is 93%, and a mass ratio of the filler in the emissive layer is 3%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 24 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including ethylene-chlorotrifluoroethylene copolymer, and the rest being an additive, wherein a mass fraction of the ethylene-trifluorochloroethylene copolymer in the emissive layer is 96%, and a mass fraction of the filler in the emissive layer is 0.5%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 25 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including ethylene-tetrafluoroethylene copolymer, and the rest being an additive, wherein a mass fraction of the ethylene-tetrafluoroethylene copolymer in the emissive layer is 99.8%, and a mass fraction of the filler in the emissive layer is 0.1%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 26 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polyvinylidene fluoride and polyfluoroethylene, and the rest being an additive, wherein a mass fraction of a total of the polyvinylidene fluoride and the polyfluoroethylene in the emissive layer is 86%, and a mass fraction of the filler in the emissive layer is 10%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 27 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including thermoplastic polyurethane, and the rest being an additive, wherein a mass fraction of the thermoplastic polyurethane in the emissive layer is 95%, a mass fraction of the filler in the emissive layer is 1%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 28 
     This embodiment is substantially the same as Embodiment 1, except that: 
     a radiative cooling functional layer including: 
     an emissive layer including a first polymer including polyethylene, wherein a mass ratio of the polyethylene in the emissive layer being 100%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 29 
     This embodiment is substantially the same as Embodiment 1, except that the radiative cooling functional layer in this embodiment does not include any first protection layer. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 30 
     This embodiment is substantially the same as Embodiment 1, except that the radiative cooling functional layer in this embodiment does not include any second adhesive layer. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 31 
     This embodiment is substantially the same as Embodiment 1, except that the radiative cooling functional layer has a thickness of 10 μm. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 32 
     This embodiment is substantially the same as Embodiment 1, except that the reflective layer in the radiative cooling functional layer is a pure silver layer. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     Embodiment 33 
     This embodiment is substantially the same as Embodiment 1, except that the radiative cooling metal plate does not include any second protective layer. 
     Embodiment 34 
     This embodiment is substantially the same as Embodiment 2, except that a pencil hardness of a release protective film in the radiative cooling metal plate is  6 B. 
     Embodiment 35 
     This embodiment is substantially the same as Embodiment 1, except that a pencil hardness in a release protective film in the radiative cooling metal plate is  9 H. 
     Comparative Embodiment 1 
     This embodiment is substantially the same as Embodiment 1, except that an elongation at break of the radiative cooling functional layer is 312%, a material of the emissive layer is poly methyl methacrylate, and a mass fraction of the poly methyl methacrylate in the emissive layer is 92%, a material of the first protective layer includes poly methyl methacrylate and polyethylene terephthalate, wherein a mass ratio of poly methyl methacrylate to polyethylene terephthalate is 80:20, the elongation at break of the radiative cooling functional layer is 0.8%. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     It was found that the radiative cooling functional layer of the radiative cooling metal plate was broken. 
     Comparative Embodiment 2 
     This embodiment is substantially the same as Embodiment 1, except that an elongation at break of the radiative cooling functional layer is 312%, a material of the emissive layer is an ethylene-vinyl acetate copolymer, and a mass fraction of the ethylene-vinyl acetate copolymer in the emissive layer is 92%. A material of the first protective layer can include an ethylene-vinyl acetate copolymer and a polyethylene, wherein a mass ratio of the ethylene-vinyl acetate copolymer to the polyethylene is 80:20. 
     The radiative cooling metal plate can be pressed into a radiative cooling profiled metal plate with a dedicated pressing device by a cold roll forming method. 
     It was found that: a phenomenon that the radiative cooling functional layer and an aluminum alloy metal substrate were separated from each other was appeared in the radiative cooling metal plate in use. 
     The radiative cooling metal plates prepared in Embodiments 1 to 35 and Comparative embodiments 1 to 2 were tested for the following performance, and the test standard and the test result are shown below. 
     Hardness test can be taken in reference of national standard GB/T6739-2006. 
     Elongation at break test can be taken in reference of national standard GB/T13022-1991. The radiative cooling functional layer is sandwiched between two clamps of a clamp. The two clamps will take relative movement. A force value sensor located on the moving chucks and a displacement sensor in a machine will collect force value changes and displacement changes during the test. When the force value is suddenly changed, it can be determined that the sample is broken. Thus, the elongation at break of the radiative cooling functional layer can be calculated. 
     Reflectivity R test can be taken as following. The reflectivity of a surface of the radiative cooling profiled metal plate can be measured with a spectrophotometer lambda 950 of Platinum Elmer at an incident angle of 5° and an average reflectivity of the whole spectrum (wavelength range of 0.3 μm to 2.5 μm) was calculated. The incident angle refers to an angle of light relative to a straight line perpendicular to the surface of the radiative cooling profiled metal plate. 
     Infrared wavelength band emissivity E test can be taken as follows: placing a the radiative cooling profiled metal plate into an infrared spectrometer of Bruker Invenior; and measuring an absorption degree of the radiative cooling profiled metal plate in a wavelength range of 8 μm to 13 μm, and measuring an interval of 1 nm. An average value of the absorbance of the radiative cooling profiled metal plate in the wavelength band of 8 μm to 13 μm is taken as the average absorbance A of the radiative cooling profiled metal plate. An average emissivity E is equal to the average absorbance A. 
     Xenon lamp aging time test can be taken as follows: after being sealed, the radiative cooling profiled metal plate is aged according to the circulation serial number 1 in Table 3 of 6.3 in the national standard GB/T16422, and the aging time is 1000 hours. 
     An attenuation value of the emissivity E of the radiative cooling profiled metal plate, an attenuation value of the reflectivity R of the radiative cooling profiled metal plate, and the attenuation value of the adhesion force of the radiative cooling functional layer can be tested after aging. The attenuation value refers to the performance before aging minus the performance after aging. 
     Humid heat aging time test is taken as follows. Referring to national standard GB/T1740, after being sealed, the radiative cooling profiled metal plate is tested under conditions of 60 degrees centigrade and 90% RH (that is, relative humidity), wherein the aging/testing time was 1000 hours. 
     An attenuation value of the emissivity E of the radiative cooling profiled metal plate, an attenuation value of the reflectivity R of the radiative cooling profiled metal plate, and the attenuation value of the adhesion force of the radiative cooling functional layer can be tested after aging. The attenuation value refers to the performance before aging minus the performance after aging. 
     Salt spray aging time test can be tested as follows. After being sealing, the radiative cooling profiled metal plate can be tested according to 5.2 neutral salt Atomization test in national standard GB/T10125, wherein a test time is 600 hours. 
     An attenuation value of the emissivity E of the radiative cooling profiled metal plate, an attenuation value of the reflectivity R of the radiative cooling profiled metal plate, and the attenuation value of the adhesion force of the radiative cooling functional layer can be tested after aging. The attenuation value refers to the performance before aging minus the performance after aging. 
     Adhesive force performance test can be taken as follows. Referring to 13 c scribe tests in national standard GB/T13448 and 14.5.2 cupping test after scribe test. The adhesive force between the metal substrate and the radiative cooling functional layer is characterized by a scribe test grade. 
     When edges of the radiative cooling functional layer are completely smooth, and no checkers fall off from the grid, the level of the scribe test can be regarded as 0 grade; 
     When the radiative cooling functional layer has a small sheet-like shedding at an intersection point, and a shedding area occupies no more than 5% of a grid area, the level of the scribe test can be regarded as 1 grade; 
     When the radiative cooling functional layer has a small sheet shedding along the edge of the cutout and the intersection, and a shedding area occupies 6% to 15% of the grid area, the level of the scribe test can be regarded as 2 grade; 
     When the radiative cooling functional layer falls along the side elongated strip of the cutout, the checkerboard is partially fall off, and the shedding area occupies 16% to 35% of the grid area, the level of the scribe test can be regarded as 3 grade; 
     When the radiative cooling functional layer falls along the side elongated strip of the cutout, the checkerboard is partially fall off, and the shedding area occupies 36% to 65% of the grid area, the level of the scribe test can be regarded as 4 grade; 
     When the radiative cooling functional layer is severely fall off, and the shedding area occupies more than 65%, the level of the scribe test can be regarded as 5 grade. 
     A materials and parameters of Embodiments 1 to 35 and Comparative embodiments 1 and 2 are shown in Table 5. 
     
       
         
           
               
               
               
               
               
               
               
               
               
               
             
               
                   
                 TABLE 5 
               
               
                   
                   
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 Contact 
                   
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 angle 
               
               
                   
                   
                   
                   
                   
                   
                 Adhesive 
                 Pencil 
                 between the 
                 Elongation 
               
               
                   
                 Attenuation 
                 Attenuation 
                 Attenuation 
                   
                   
                 force of 
                 hardness 
                 radiative 
                 at break of 
               
               
                   
                 of xenon 
                 of wet 
                 of salt 
                   
                   
                 radiative 
                 of the 
                 cooling 
                 radiative 
               
               
                   
                 lamp aging 
                 heat aging 
                 spray aging 
                   
                   
                 cooling 
                 second 
                 functional 
                 cooling 
               
               
                   
                 time of 
                 time of 
                 time of 
                   
                   
                 functional 
                 protective 
                 layer and 
                 functional 
               
               
                   
                 1000 h 
                 1000 h 
                 600 h 
                 R/% 
                 E/% 
                 layer 
                 layer 
                 water 
                 layer/% 
               
               
                   
                   
               
             
            
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
               
            
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.2 
                 92.4 
                 0 grade 
                 2H 
                 115 
                 31 
               
               
                 1 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 2% 
                 R: 2% 
                 82.1 
                 95.0 
                 0 grade 
                 3B 
                 85 
                 32 
               
               
                 2 
                 E: 3% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 2% 
                 R: 2% 
                 R: 3% 
                 85.4 
                 91.3 
                 0 grade 
                 2B 
                 96 
                 45 
               
               
                 3 
                 E: 3% 
                 E: 2% 
                 E: 2% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 2% 
                 R: 1% 
                 R: 2% 
                 87.0 
                 90.6 
                 0 grade 
                 2H 
                 120 
                 43 
               
               
                 4 
                 E: 1% 
                 E: 2% 
                 E: 1% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 2% 
                 R: 2% 
                 R: 1% 
                 91.6 
                 90.4 
                 0 grade 
                 2H 
                 105 
                 55 
               
               
                 5 
                 E: 2% 
                 E: 1% 
                 E: 2% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 2% 
                 R: 2% 
                 88.0 
                 95.2 
                 0 grade 
                 2H 
                 115 
                 30 
               
               
                 6 
                 E: 2% 
                 E: 2% 
                 E: 2% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.6 
                 91.3 
                 0 grade 
                 2H 
                 115 
                 35 
               
               
                 7 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.4 
                 91.3 
                 0 grade 
                 2H 
                 115 
                 58 
               
               
                 8 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.6 
                 88.4 
                 0 grade 
                 2H 
                 115 
                 65 
               
               
                 9 
                 E: 3% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 2% 
                 R: 2% 
                 90.2 
                 93.4 
                 0 grade 
                 2H 
                 115 
                 30 
               
               
                 10 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.4 
                 92.5 
                 0 grade 
                 2H 
                 115 
                 35 
               
               
                 11 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.3 
                 90.0 
                 0 grade 
                 2H 
                 115 
                 240 
               
               
                 12 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 3% 
                 90.5 
                 90.4 
                 0 grade 
                 2H 
                 115 
                 44 
               
               
                 13 
                 E: 3% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 3% 
                 90.1 
                 91.2 
                 0 grade 
                 2H 
                 115 
                 30 
               
               
                 14 
                 E: 3% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.9 
                 93.1 
                 0 grade 
                 2H 
                 115 
                 28 
               
               
                 15 
                 E: 3% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.3 
                 91.4 
                 0 grade 
                 2H 
                 115 
                 40 
               
               
                 16 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.1 
                 91.0 
                 0 grade 
                 2H 
                 115 
                 40 
               
               
                 17 
                 E: 3% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 3% 
                 90.5 
                 92.4 
                 0 grade 
                 2H 
                 115 
                 38 
               
               
                 18 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 3% 
                 90.4 
                 90.5 
                 0 grade 
                 2H 
                 115 
                 65 
               
               
                 19 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 3% 
                 90.2 
                 91.2 
                 0 grade 
                 2H 
                 115 
                 75 
               
               
                 20 
                 E: 3% 
                 E: 2% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.5 
                 87.6 
                 0 grade 
                 2H 
                 115 
                 72 
               
               
                 21 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.1 
                 93.5 
                 0 grade 
                 2H 
                 115 
                 38 
               
               
                 22 
                 E: 2% 
                 E: 2% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.5 
                 92.4 
                 0 grade 
                 2H 
                 115 
                 55 
               
               
                 23 
                 E: 3% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.0 
                 89.1 
                 0 grade 
                 2H 
                 115 
                 78 
               
               
                 24 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 90.8 
                 88.7 
                 0 grade 
                 2H 
                 115 
                 77 
               
               
                 25 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 3% 
                 R: 2% 
                 89.2 
                 93.2 
                 0 grade 
                 2H 
                 115 
                 36 
               
               
                 26 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 3% 
                 R: 2% 
                 R: 2% 
                 90.5 
                 90.2 
                 0 grade 
                 2H 
                 115 
                 100 
               
               
                 27 
                 E: 2% 
                 E: 3% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 6% 
                 R: 6% 
                 R: 5% 
                 90.6 
                 88.3 
                 0 grade 
                 2H 
                 115 
                 274 
               
               
                 28 
                 E: 4% 
                 E: 4% 
                 E: 3% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 6% 
                 R: 6% 
                 R: 4% 
                 90.2 
                 92.1 
                 0 grade 
                 2H 
                 90 
                 27 
               
               
                 29 
                 E: 5% 
                 E: 5% 
                 E: 5% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 1 
                 force: 2 
                 force: 2 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 8% 
                 R: 3% 
                 R: 5% 
                 90.5 
                 91.4 
                 0 grade 
                 2H 
                 115 
                 28 
               
               
                 30 
                 E: 3% 
                 E: 4% 
                 E: 5% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 4% 
                 R: 4% 
                 R: 3% 
                 90.8 
                 85.9 
                 0 grade 
                 2H 
                 115 
                 24 
               
               
                 31 
                 E: 3% 
                 E: 5% 
                 E: 4% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 7% 
                 R: 7% 
                 R: 7% 
                 90.2 
                 91.8 
                 0 grade 
                 2H 
                 115 
                 31 
               
               
                 32 
                 E: 5% 
                 E: 6% 
                 E: 6% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 0 
                 force: 0 
                 force: 0 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 8% 
                 R: 9% 
                 R: 7% 
                 90.5 
                 91.7 
                 0 grade 
                 3B 
                 115 
                 33 
               
               
                 33 
                 E: 9% 
                 E: 7% 
                 E: 8% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 1 
                 force: 1 
                 force: 1 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 6% 
                 R: 5% 
                 R: 7% 
                 82.3 
                 94.6 
                 0 grade 
                 6B 
                 115 
                 30 
               
               
                 34 
                 E: 5% 
                 E: 6% 
                 E: 8% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 1 
                 force: 1 
                 force: 1 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Embodiment 
                 R: 6% 
                 R: 8% 
                 R: 6% 
                 90.2 
                 92.3 
                 0 grade 
                 9H 
                 115 
                 29 
               
               
                 35 
                 E: 7% 
                 E: 6% 
                 E: 7% 
               
               
                   
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 1 
                 force: 1 
                 force: 1 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Comparative 
                 R: 22% 
                 R: 25% 
                 R: 21% 
                 90.2 
                 93.2 
                 0 grade 
                 2H 
                 115 
                 0.8 
               
               
                 embodiment 
                 E: 22% 
                 E: 23% 
                 E: 14% 
               
               
                 1 
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 3 
                 force: 3 
                 force: 3 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                 Comparative 
                 R: 23% 
                 R: 24% 
                 R: 23% 
                 90.2 
                 81.0 
                 2 grade 
                 4B 
                 65 
                 312 
               
               
                 embodiment 
                 E: 22% 
                 E: 21% 
                 E: 24% 
               
               
                 2 
                 adhesive 
                 adhesive 
                 adhesive 
               
               
                   
                 force: 2 
                 force: 2 
                 force: 3 
               
               
                   
                 grade 
                 grade 
                 grade 
               
               
                   
               
            
           
         
       
     
     It can be seen from Embodiments 1 to 35 and Comparative embodiments 1 and 2 in Table 5, that when the radiative cooling functional layer has an elongation at break in the range of 1% to 300%, the radiative cooling metal plate is resistant to bending; and the attenuation of the emissivity E of the radiative cooling profiled metal plate is less than or equal to 9%, the attenuation of the reflectivity R of the radiative cooling profiled metal plate is less than or equal to 9%, and the attenuation of the adhesion of the radiative cooling functional layer is less than or equal to 1 level. The radiative cooling profiled metal plate has great aging resistance. 
     The respective technical features of the above embodiments can be combined arbitrarily, and for the sake of brevity of description, all possible combinations of the respective technical features in the above embodiments are not described; however, the respective technical features should be considered to be within the scope of disclosure disclosed in the present description as long as the combination of these technical features is not contradictive. 
     The embodiments described above merely express several embodiments of the present disclosure, and the description thereof is more specific and detailed, but cannot be construed as limiting the scope of the present disclosure. It should be noted that, for a person of ordinary skill in the art, several modifications and improvements can also be made without departing from the inventive concept, which all belong to the scope of protection of the present disclosure. Therefore, the scope of protection of the present disclosure should be regarded by the appended claims.