Patent Publication Number: US-2023137688-A1

Title: Rotor, method of producing the rotor, and motor

Description:
TECHNICAL FIELD 
     The present invention relates to a rotor of a motor, a method of producing the rotor, and a motor. 
     BACKGROUND ART 
     For example, in a high-output motor, a rare earth magnet containing, for example, neodymium as a main ingredient is used as a rotor magnet. In the case of producing a multipole magnet using a rare earth magnet, a segment magnet divided into segments on a per pole basis is used, instead of an annular magnet for achieving a lighter weight and lower cost. However, it is difficult to align, arrange, and fix the segment magnet at a predetermined position in the circumferential direction of the rotor yoke. The rare earth magnet has a stronger magnetic force than a ferrite magnet but tends to rust easily and therefore is nickel-plated for improving corrosion resistance and has its surface rust-proofed. A bonding surface, when coated with an adhesive and wet, has a lower frictional force and therefore the magnet tends to move easily. Particularly if an epoxy resin-based adhesive is used, the viscosity of the adhesive temporarily drops in the heat-curing process and therefore the magnet tends to be misaligned. If the magnet is misaligned, motor characteristics deteriorate, posing a risk of occurrence of motor vibration and noise. 
     As such, for example, in a rotor of an outer-rotor motor, each segment magnet  52  is positioned in a radial direction and an axial direction and bonded and fixed to a cylindrical rotor yoke  51 , using a positioning member  53  for positioning and holding a plurality of segment magnets  52 , as shown in  FIG.  6 A . In the positioning member  53 , pectinate partition members  53   b  are formed, standing up at a predetermined interval from an annular coupling part  53   a . The annular coupling part  53   a  prescribes the position in the axial direction of the segment magnets  52 , and the partition members  53   b  prescribe the position in the radial direction. After the positioning member  53  is inserted along an inner circumferential surface  51   a  from an opening at one end side of the rotor yoke  51 , the segment magnets  52  coated with an adhesive  54  are inserted and bonded between the partition members  53   b  from an opening at the other end side of the rotor yoke  51  (see  FIG.  6 A ). Then, the adhesive  54  is heat-cured, bonding and fixing the segment magnets  52  together with the positioning member  53  to the inner circumferential surface  51   a  of the rotor yoke  51  (see  FIG.  6 B ). After that, a rotor hub  56  assembled with a rotor shaft  55  in a unified manner is pressed into and fixed in the rotor yoke  51  (see  FIG.  6 C ), thus forming an outer-rotor-type rotor  57  rotatable about the rotor shaft  55  (see  FIG.  6 D ). 
     Similarly, in a rotor of an inner-rotor motor, after a positioning member  53  is attached from one side in the axial direction to an outer circumferential surface  51   b  of a columnar rotor yoke  51  having a rotor shaft  55  at its center, segment magnets  52  coated with an adhesive  54  are inserted and attached between partition members  53   b  from the other side in the axial direction (see  FIG.  7 A ). Then, the adhesive  54  is heat-cured, thus forming an inner-rotor-type rotor  57  in which the segment magnets  52  together with the positioning member  53  are bonded and fixed to the outer circumferential surface  51   b  of the rotor yoke  51  (see  FIG.  7 B ). 
     Also, a technique of strengthening a fixation retention force of a magnet attached inside a rotor yoke of an outer-rotor motor and thus preventing the magnet from falling during assembly and improving workability has been proposed. A cylindrical inner case is fitted to the inner surface side of a cylindrical rotor outer cylinder, and a resin holder ring with a plurality of magnets arranged via partition pieces is assembled in a unified manner along a circumferential direction between the rotor outer cylinder and the inner case (see PTL 1: JP-A-2003-304660). 
     CITATION LIST 
     Patent Literature 
     PTL 1: JP-A-2003-304660 
     SUMMARY OF INVENTION 
     Technical Problem 
     However, in  FIG.  6 D  and  FIG.  7 B  or PTL 1, the segment magnets  52  together with the positioning member  53  are bonded and fixed to the inner circumferential surface  51   a  or the outer circumferential surface  51   b  of the rotor yoke  51  and therefore the positioning member  53 , which is originally unnecessary, is bonded together with the segment magnets  52  to the rotor yoke  51  when the adhesive is heat-cured, and the positioning member  53  cannot be removed. Also, the resin holder ring in PTL 1 is used as an essential member for fixing the magnets. 
     In this way, incorporating the positioning member  53 , which is originally unnecessary, and the resin holder ring into the rotor  57  increases the number of components and therefore raises the production cost and also increases the weight of the motor. 
     Meanwhile, if the segment magnets  52  are bonded and fixed to the rotor yoke  51  without using the positioning member  53 , recessed parts  51   a  and protruding parts  51   b  for positioning the segment magnets  52  on the inner circumferential surface of the rotor yoke  51  need to be formed alternately in the circumferential direction, as shown in  FIG.  8 A . Alternatively, pectinate positioning members  56   a  need to be provided at an outer circumferential edge of the rotor hub  56  pressed into the rotor yoke  51 , as shown in  FIG.  8 B . In either case, the number of processing steps for components increases and therefore the production cost increases. 
     Solution to Problem 
     The present invention has been made in order to address the foregoing issue and aims to provide a rotor that achieves a reduction in the number of components, a reduction in the production cost, and a lighter weight, to provide a method of producing a rotor that enables plate-like magnets to be positioned in the radial direction and the axial direction and assembled to a rotor yoke and thus achieves high assemblability, and to provide a motor that is inexpensive, has high assemblability, and can maintain motor characteristics, by using the rotor. 
     In order to address the foregoing issue, the present invention has at least the following configuration. 
     In a rotor having a plurality of plate-like magnets divided in a circumferential direction at a predetermined interval at a circumferential surface of a rotor yoke, a first bonding part coated with a first adhesive curing in a predetermined time and a second bonding part coated with a second adhesive taking a longer curing time than the first adhesive but having a higher bonding strength are formed next to each other at a bonding surface of each plate-like magnet, and the plurality of plate-like magnets are partially bonded at the first bonding part at a predetermined interval to the circumferential surface of the rotor yoke by curing the first adhesive via a positioning member for positioning in a radial direction and in an axial direction, and the second adhesive is cured in a state where the positioning member is removed, thus bonding and fixing the plurality of plate-like magnets at the second bonding part via a predetermined gap between the plate-like magnets in the circumferential direction. 
     Since the bonding surface of the plate-like magnets is thus coated with the first adhesive curing in a predetermined time, the plate-like magnets can be positioned in the radial direction and the axial direction via the positioning member and partially bonded at the first bonding part to the rotor yoke, and the plurality of plate-like magnets are bonded and fixed at the second bonding part via a predetermined gap between the plate-like magnets in the circumferential direction by curing the second adhesive taking a longer curing time than the first adhesive but having a higher bonding strength, after the positioning member is removed from the rotor yoke. This can reduce the positioning member, which is originally unnecessary, reduce the production cost, and achieve a lighter weight of the rotor. 
     Also, since the plurality of plate-like magnets are bonded and fixed at a predetermined interval to the rotor yoke using the positioning member, cost reduction can be achieved, compared with an annular magnet, and the plate-like magnets can be assembled with high position accuracy in the radial direction and the axial direction to the rotor yoke and therefore without misalignment. 
     It is preferable that the plate-like magnet is a rare earth magnet with a rust-proofed surface and that the first adhesive and the second adhesive are provided in a gap between the rotor yoke and the magnet. 
     Thus, a high-output plate-like magnet can be bonded and fixed to the rotor yoke without misalignment, using different types of adhesives. 
     It is preferable that, with respect to the areas of the first bonding part coated with the first adhesive and the second bonding part coated with the second adhesive at the bonding surface of the plate-like magnet, the second bonding part has an area equivalent to or greater than the area of the first bonding part. 
     Thus, the ultimate bonding strength of the plate-like magnet to the rotor yoke can be maintained. 
     At least one of an ultraviolet-curing or anaerobic-curing adhesive and a quick-setting adhesive may be used as the first adhesive and a thermosetting adhesive may be used as the second adhesive. 
     Thus, simply casting ultraviolet rays onto the first adhesive layer provided between the plate-like magnet and the rotor yoke, creating an anaerobic state, bringing the plate-like magnet and the rotor yoke into contact with each other via a quick-setting adhesive, or combining these measures, cures the first adhesive and therefore enables the plate-like magnet to be easily partially bonded to the rotor yoke. Also, when the second adhesive is heat-cured, the plate-like magnet has been partially bonded with the first adhesive and therefore does not become misaligned. 
     The plate-like magnet may be a flat plate-like magnet, and an adhesive layer may be formed, using a void formed between a curved surface of the rotor yoke and a flat surface of the plate-like magnet as an adhesive reservoir of the first adhesive and the second adhesive. 
     In this case, since no particular processing is needed for the bonding of the plate-like magnet, the production cost can be reduced and the void formed with the curved surface, which is the bonding surface of the rotor yoke, can be used as the adhesive reservoir of the first adhesive and the second adhesive and therefore as a sufficient bonding space. Thus, the strength of partial bonding and fixed bonding can be maintained. Particularly if ultraviolet rays are cast at the time of partial bonding, a sufficient space for casting ultraviolet rays from the gap between the curved surface and the flat surface can be secured. 
     The rotor may be a rotor of an outer-rotor motor in which a plurality of plate-like magnets divided in a circumferential direction are fixed at a predetermined interval to an inner circumferential surface of a rotor yoke formed in a cup-like shape, or a rotor of an inner-rotor motor in which a plurality of plate-like magnets divided in a circumferential direction are fixed at a predetermined interval to an outer circumferential surface of a rotor yoke formed in a columnar shape. 
     Cost reduction and lighter weight are achieved, compared with an annular magnet, and the plate-like magnets can be assembled with high position accuracy in the radial direction and the axial direction to the rotor yoke, regardless of whether it is an outer-rotor type or an inner-rotor type. 
     As a motor, an outer-rotor motor or an inner-rotor motor that has one of the foregoing rotors and a stator having a stator pole tooth opposite the plate-like magnet of the rotor and is therefore inexpensive and light-weight, has high assemblability and can maintain motor characteristics, can be provided. 
     A method of producing a rotor includes: a step of coating a bonding surface of each of a plurality of divided plate-like magnets with a first adhesive curing in a predetermined time; a step of coating the bonding surface of each of the plate-like magnets with a second adhesive taking a longer curing time than the first adhesive but having a higher bonding strength; a step of attaching a positioning member having pectinate partition members coupled in an annular form for positioning the plate-like magnets in a radial direction and an axial direction, to a circumferential surface of a rotor yoke; a step of positioning the plate-like magnets between the partition members of the rotor yoke with the positioning member attached, and arranging the plate-like magnets at a predetermined interval at the circumferential surface of the rotor yoke via the first adhesive and the second adhesive; a step of curing the first adhesive coating the plate-like magnets, and thus partially bonding the plate-like magnets to the rotor yoke at a first bonding part; a step of extracting the positioning member from the rotor yoke; and a step of curing the second adhesive and thus bonding and fixing the plate-like magnets to the rotor yoke at a second bonding part. 
     The application of the first adhesive and the second adhesive coating the bonding surface of the plate-like magnets includes both a case where these adhesives are directly applied to the bonding surface and a case where these adhesives are supplied in advance to a surface to be bonded and are then indirectly applied. The plate-like magnet, as a term, is not limited to a flat plate but includes various forms such as a curved plate, provided that it is a plate member with a predetermined thickness. 
     According to the method of producing the rotor, attaching the positioning member having the pectinate partition members coupled in an annular form for positioning in the radial direction and the axial direction, to the rotor yoke, enables the positioning and arrangement of the plate-like magnets in the radial direction and the axial direction between the partition members. 
     Also, the positioning member can be extracted from the rotor yoke after the plate-like magnets are partially bonded to the rotor yoke at the first bonding part by curing the first adhesive coating the plate-like magnets, and therefore a reduction in the number of components, a reduction in the production cost, and a lighter weight can be achieved by omitting the positioning member, which is originally unnecessary. 
     Also, since the plate-like magnets are bonded and fixed to the rotor yoke at the second bonding part by curing the second adhesive coating the plate-like magnets after the positioning member is removed from the rotor yoke, the plate-like magnets can be bonded and fixed with high position accuracy. 
     The method may be a method of producing a rotor of an outer-rotor motor, including: a step of attaching a positioning member having pectinate partition members coupled to an annular coupling part for positioning the plate-like magnets in the radial direction and the axial direction, to an inner circumferential surface of a cylindrical rotor yoke; a step of inserting each of the plurality of plate-like magnets between the partition members and positioning and arranging the plate-like magnets at a predetermined interval at the inner circumferential surface of the rotor yoke via the first adhesive and the second adhesive; and a step of assembling a rotor hub and a rotor shaft to the rotor yoke in a unified manner. 
     Alternatively, the method may be a method of producing a rotor of an inner-rotor motor, including: a step of attaching a positioning member having pectinate partition members coupled to an annular coupling part for positioning the plate-like magnets in the radial direction and the axial direction, to an outer circumferential surface of a rotor yoke having a rotor shaft at its center; and a step of inserting each of the plurality of plate-like magnets between the partition members and positioning and arranging the plate-like magnets at a predetermined interval at the outer circumferential surface of the rotor yoke via the first adhesive and the second adhesive. 
     The plate-like magnets may be partially bonded to the rotor yoke, using at least one of an ultraviolet-curing or anaerobic-curing adhesive and a quick-setting adhesive as the first adhesive. 
     Thus, casting ultraviolet rays onto the first adhesive layer provided between the plate-like magnets and the rotor yoke, creating an anaerobic state, bringing into contact with the magnet bonding surface, or combining these measures, cures the first adhesive and therefore enables the plate-like magnets to be easily partially bonded to the rotor yoke. 
     The plurality of plate-like magnets may be magnetized before being bonded inside the rotor yoke or may be magnetized after being bonded inside the rotor yoke. 
     While the plate-like magnets, if magnetized in advance, may attract each other and stick to each other when inserted in the rotor yoke, using the positioning member eliminates the occurrence of such an inconvenience. 
     Also, if the plate-like magnets are magnetized after being bonded inside the rotor yoke, the work of assembling the plate-like magnets is easier and is less susceptible to the influence of thermal demagnetization. 
     Advantageous Effects of Invention 
     As described above, a rotor that achieves a reduction in the number of components, a reduction in the production cost, and a lighter weight, can be provided. 
     Also, a method of producing a rotor that enables a plurality of plate-like magnets to be positioned in the radial direction and the axial direction and to be bonded and fixed to a rotor yoke with high position accuracy and thus achieves high assemblability, can be provided. 
     Also, a motor that is inexpensive, has high assemblability, and can maintain motor characteristics by using the rotor, can be provided. 
    
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
         FIGS.  1 A to  1 E  are explanatory views showing a process of producing a rotor of an outer-rotor motor. 
         FIGS.  2 A to  2 D  are explanatory views showing the process of producing the outer-rotor motor, continued from  FIGS.  1 A to  1 E . 
       FIGS.  3 A 1  to  3 B 3  are explanatory views showing forms of plate-like magnets bonded and fixed to a rotor yoke. 
         FIGS.  4 A to  4 C  are explanatory views showing a process of producing a rotor of an inner-rotor motor. 
         FIGS.  5 A and  5 B  are explanatory views showing a bonding area of a first bonding part and a second bonding part of a plate-like magnet. 
         FIGS.  6 A to  6 D  are process charts showing a method of producing a rotor of an outer-rotor motor according to the related art. 
         FIGS.  7 A and  7 B  are process charts showing a method of producing a rotor of an inner-rotor motor according to the related art. 
         FIGS.  8 A and  8 B  are explanatory views showing a required configuration of a rotor yoke and a rotor hub. 
     
    
    
     DESCRIPTION OF EMBODIMENTS 
     An embodiment of a rotor, a method of producing the rotor, and a motor according to the present invention will now be described with reference to the accompanying drawings. First, a schematic configuration of the motor is described with reference to  FIGS.  1 A to  1 E . In this embodiment, a brushless DC motor of an outer-rotor type, or an inner-rotor type, described later, is used as an example of the motor. 
     As shown in  FIGS.  2 C and  2 D , an outer-rotor motor M having a rotor  1  and a stator  2  is used as the brushless DC motor. A rotor hub  4  linked to a rotor shaft  3  is fitted in to close an opening at one end of a cylindrical rotor yoke  5  (magnetic material such as iron or stainless steel), thus forming the rotor  1  in a cup-like shape. To an inner circumferential surface  5   a  of the rotor yoke  5  (see  FIG.  2 A ), a plurality of divided plate-like magnets  6  (rotor magnets) magnetized to alternately have an N pole and an S pole in the circumferential direction are bonded and fixed (see  FIG.  2 B ). Each plate-like magnet  6  is arranged opposite a stator pole tooth  7   b  of a stator core  7 , described later. The plate-like magnet  6 , as a term, is not limited to a flat plate shape (see FIG.  3 B 1 ) but includes various forms such as a curved plate (see FIG.  3 A 1 ), provided that it is a magnetic plate member having a predetermined thickness. 
     As shown in  FIG.  2 C , in the stator  2 , the stator core  7  is assembled to the outer circumference of a bearing housing  2   a . In the stator core  7 , a plurality of stator pole teeth  7   b  are provided, protruding outward in the radial direction from an annular core back part  7   a . The stator core  7  may be a laminated core formed by lamination-pressing electromagnetic steel sheets or may be a block core made of a magnetic metal block. In the stator core  7 , the peripheries of the stator pole teeth  7   b  are covered with an insulator (insulation bobbin)  7   c , and a coil  7   d  is wound on the periphery of each insulator  7   c . The rotor  1  is rotatably assembled by having the rotor shaft  3  inserted in the bearing housing  2   a  of the stator  2  and having the plate-like magnets  6  arranged opposite the stator pole teeth  7   b  of the stator core  7  (see  FIG.  2 D ). 
     The configuration of the rotor  1  will now be described in detail. 
     As shown in FIG.  3 A 3  and FIG.  3 B 3 , the plurality of plate-like magnets  6  divided in the circumferential direction are provided at a predetermined interval and spaced apart from each other at the inner circumferential surface  5   a  of the cylindrical rotor yoke  5 . As the plate-like magnets  6 , a rear earth magnet (for example, a neodymium magnet) having a rust-proofed surface is used, and the plate-like magnets  6  are bonded with a first adhesive  8   a  and a second adhesive  8   b  provided in the gap between the rotor yoke  5  and the flat plate-shaped plate-like magnets  6 . Thus, the high-output plate-like magnets  6  can be bonded and fixed to the rotor yoke  5  without misalignment, using different types of adhesives, as will be described later. 
     At a bonding surface  6   c  of each plate-like magnet  6 , a first bonding part  6   a  coated with the first adhesive  8   a  curing in a predetermined time and a second bonding part  6   b  coated with the second adhesive  8   b  for bonding and fixation that takes a longer curing time than the first adhesive  8   a  but has a higher bonding strength, are formed next to each other, as shown in  FIGS.  5 A and  5 B . As the first adhesive  8   a , for example, at least one of an ultraviolet-curing or anaerobic-curing adhesive and a quick-setting adhesive is used, and as the second adhesive  8   b , for example, a thermosetting epoxy resin-based adhesive is used. Thus, casting ultraviolet rays onto the first adhesive  8   a  provided between the plate-like magnets  6  and the rotor yoke  5 , creating an anaerobic state, bringing into contact with the bonding surface  6   c , or combining these measures, cures the first adhesive  8   a  and therefore enables the plate-like magnet  6  to be easily partially bonded to the rotor yoke  5  in a relatively short time. FIG.  3 B 3  shows the state where the plate-like magnets  6  are bonded to the inner circumferential surface  5   a  of the rotor yoke  5 . The application of the first adhesive  8   a  coating the first bonding part  6   a  of the plate-like magnets  6  and the second adhesive  8   b  coating the second bonding part  6   b  includes both a case where these adhesives are directly applied to the bonding surface  6   c  and a case where these adhesives are supplied in advance to a surface to be bonded (the inner circumferential surface  5   a  of the rotor yoke  5 ) and are then indirectly applied. 
     The plate-like magnet  6  is flat plate-shaped and an adhesive reservoir of the first adhesive  8   a  and the second adhesive  8   b  is formed in a void  9  formed between the curved inner circumferential surface  5   a  of the rotor yoke  5  and the bonding surface  6   c  of the flat plate-shaped plate-like magnet  6 , as shown in FIG.  3 B 2 . In this case, since no particular processing is needed for the plate-like magnet  6 , the production cost can be reduced and the void  9  formed with the inner circumferential surface  5   a  (curved surface), which is the bonding surface of the rotor yoke  5 , can be used as the adhesive reservoir of the first adhesive  8   a  and the second adhesive  8   b  and therefore the strength of partial bonding and fixed bonding can be maintained. Particularly if ultraviolet rays are cast at the time of partial bonding, a sufficient space for casting ultraviolet rays from the gap between the inner circumferential surface  5   a  (curved surface) and the end surface of the flat plate-shaped plate-like magnet  6  can be secured. 
     As shown in  FIGS.  5 A and  5 B , it is preferable that, with respect to the bonding area formed at the bonding surface  6   c  of the plate-like magnet  6 , the second bonding part  6   b  has an area equivalent to the area of the first bonding part  6   a  (see  FIG.  5 A ) or greater (the second bonding part  6   b &gt;the first bonding part  6   a ) (see  FIG.  5 B ). Thus, the bonding strength of the plate-like magnet  6  to the rotor yoke  5  can be maintained. 
     As described above, at least one of an ultraviolet-curing or anaerobic-curing adhesive and a quick-setting adhesive is used as the first adhesive  8   a  and a thermosetting epoxy resin-based adhesive is used as the second adhesive  8   b . Thus, casting ultraviolet rays onto the first adhesive  8   a  provided between the plate-like magnet  6  and the rotor yoke  5 , creating an anaerobic state, bringing these into contact with each other via a quick-setting adhesive, or combining these measures, cures the first adhesive  8   a  and therefore enables the plate-like magnet  6  to be easily partially bonded to the rotor yoke  5 . Also, when the second adhesive  8   b  is heat-cured, the plate-like magnet  6  has been partially bonded to the rotor yoke  5  with the first adhesive  8   a  and therefore the plate-like magnet  6  does not become misaligned even if the viscosity of the second adhesive  8   b  temporarily drops in the heat-curing process. 
     While the case where the plate-like magnet  6  is a flat plate-shaped has been described, the plate-like magnet  6  may be in the shape of a curved plate with the bonding surface  6   c  having the same curvature as the rotor yoke  5 , as shown in FIG.  3 A 1 . In this case, the adhesive layer formed between the curved inner circumferential surface  5   a  of the rotor yoke  5  and the bonding surface  6   c  of the plate-like magnet  6  is formed uniformly in the circumferential direction of the bonding surface  6   c , as shown in FIG.  3 A 2 . 
     This case is similar to the case of the flat plate-like magnet in that the first bonding part  6   a  coated with the first adhesive  8   a  for partial bonding and the second bonding part  6   b  coated with the second adhesive  8   b  for bonding and fixation that is heat-cured are formed next to each other at the bonding surface  6   c  of the plate-like magnet  6 , as shown in  FIGS.  5 A and  5 B . FIG.  3 A 3  shows the state where the plate-like magnets  6  are bonded to the inner circumferential surface  5   a  of the rotor yoke  5 . 
     Also, as shown in  FIGS.  1 C and  1 C ′, a positioning member  10  made of a resin for positioning, bonding, and fixing the plurality of plate-like magnets  6  to the inner circumferential surface  5   a  of the rotor yoke  5  is used. A resin-molded member is used as the positioning member  10 , and the positioning member  10  has an annular coupling part  10   a  coupled in an annular shape and a plurality of partition members  10   b  that are formed, standing up in a pectinate shape from the annular coupling part  10   a . The interval between the partition members  10   b  is approximately equivalent to or broader than the width dimension of the plate-like magnet  6 . Also, at the annular coupling part  10   a , a flange part  10   c  for positioning by coming into contact with an opening end of the rotor yoke  5  is provided, extending outward in the radial direction. 
     As shown in  FIG.  1 D , the positioning member  10  (partition members  10   b ) is inserted to the inner circumferential surface  5   a  from an opening at one end of the rotor yoke  5 , and the plate-like magnets  6  are inserted between the partition members  10   b  from an opening at the other end and thus positioned in the radial direction and the axial direction to the inner circumferential surface  5   a.    
     At this point, since the plate-like magnets  6  are coated with the first adhesive  8   a  at the first bonding part  6   a , the plate-like magnets  6  can be positioned in the radial direction and the axial direction to the rotor yoke  5  and partially bonded by curing the first adhesive  8   a  (for example, by casting ultraviolet rays). 
     Also, in the state where the plate-like magnets  6  have been partially bonded to the inner circumferential surface  5   a  of the rotor yoke  5 , the positioning member  10 , which is no longer necessary, can be extracted and removed from the rotor yoke  5 , as shown in  FIG.  1 E . After the positioning member  10  is removed from the rotor yoke  5 , the epoxy resin-based second adhesive  8   b  is heat-cured, for example, at 100° C. to 180° C., thus bonding and fixing the plate-like magnets  6  at the second bonding part  6   b . Although the viscosity of the second adhesive  8   b  temporarily drops in the heat curing process, the plate-like magnets  6  have been partially bonded with the first adhesive  8   a  and therefore do not become misaligned. 
     This can reduce the positioning member  10 , which is originally unnecessary, reduce the production cost, and achieve a lighter weight of the rotor  1 . 
     Also, since the plurality of plate-like magnets  6  are bonded and fixed at a predetermined interval to the rotor yoke  5 , using the positioning member  10 , cost reduction can be achieved, compared with an annular magnet, and the plate-like magnets  6  can be assembled to the rotor yoke  5  with high position accuracy in the radial direction and the axial direction and without misalignment. 
     In this way, the rotor  1  of the outer-rotor motor, in which the plurality of plate-like magnets  6  divided in the circumferential direction are fixed at a predetermined interval to the inner circumferential surface  5   a  of the rotor yoke  5 , may be formed. 
     Meanwhile, as shown in  FIGS.  4 A and  4 A ′, the positioning member  10  may be used for positioning, bonding, and fixing the plurality of plate-like magnets  6  (curved plates) to an outer circumferential surface  5   b  of the rotor yoke  5  of an inner-rotor motor. The positioning member  10  is made of a resin-molded member and has the annular coupling part  10   a  coupled in an annular shape and the plurality of partition members  10   b  that are formed, standing up in a pectinate shape from the annular coupling part  10   a . The flange part  10   c  may be not provided. 
     As shown in  FIGS.  4 A and  4 A ′, the partition members  10   b  of the positioning member  10  are fitted with the outer circumferential surface  5   b  from one end side in the axial direction of the rotor yoke  5  and the annular coupling part  10   a  is brought into contact with and attached to one end surface of the rotor yoke  5 . The plurality of plate-like magnets  6  are each inserted between the partition members  10   b  from the other end surface side of the rotor yoke  5  and thus positioned in the radial direction and the axial direction. 
     At this point, since the plate-like magnets  6  are coated with the first adhesive  8   a  at the bonding surface  6   c , the plate-like magnets  6  can be positioned to the rotor yoke  5  and partially bonded by curing the first adhesive  8   a  (for example, by casting ultraviolet rays). 
     In the state where the plate-like magnets  6  have been partially bonded, the positioning member  10 , which is no longer necessary, can be extracted and removed from the rotor yoke  5 . After the positioning member  10  is removed from the rotor yoke  5 , the second adhesive  8   b  is heat-cured, for example, at 100° C. to 180° C., thus bonding and fixing the plate-like magnets  6  at the second bonding part  6   b . Although the viscosity of the second adhesive  8   b  temporarily drops in the heat curing process, the plate-like magnets  6  have been partially bonded with the first adhesive  8   a  and therefore do not become misaligned. 
     In this way, the rotor  1  of the inner-rotor motor, in which the plurality of plate-like magnets  6  divided in the circumferential direction are fixed at a predetermined interval to the outer circumferential surface  5   b  of the rotor yoke  5  formed in a columnar shape, is provided, as shown in  FIG.  4 B . 
     The foregoing configurations of the rotor  1  achieve cost reduction and lighter weight, compared with an annular magnet, and enables the plate-like magnets  6  to be assembled with high position accuracy in the radial direction and the axial direction to the rotor yoke  5  regardless of whether it is an outer-rotor type or an inner-rotor type. 
     Also, the motor M has one of the foregoing rotors  1 , and the stator  2  having the stator pole teeth  7   b  opposite the plate-like magnets  6  of the rotor  1 , and thus can provide an outer-rotor motor or an inner-rotor motor that is inexpensive and light weight, has high assemblability, and can maintain motor characteristics. 
     The process of producing the rotor  1  of the outer-rotor motor will now be described with reference to  FIGS.  1 A to  1 E  and  FIGS.  2 A to  2 D . In  FIG.  1 A , the rotor shaft  3  is fitted in a center part of the rotor hub  4  and assembled in a unified manner. As shown in  FIG.  1 B , the first bonding part  6   a  of the plurality of divided plate-like magnets  6  is each coated with the first adhesive  8   a  curing in a predetermined time. As the first adhesive  8   a , for example, at least one of an ultraviolet-curing or anaerobic-curing adhesive and a quick-setting adhesive is used. Also, the second bonding part  6   b  next to the first bonding part  6   a  of the plate-like magnets  6  is each coated with the second adhesive  8   b  taking a longer curing time than the first adhesive  8   a  but having a higher bonding strength. As the second adhesive  8   b , for example, a thermosetting epoxy resin-based adhesive is used. 
     Also, the process of applying the first and second adhesives  8   a ,  8   b  is not limited to the case where these adhesives are directly applied to the bonding surface  6   c  of the plate-like magnets  6 , as shown in  FIG.  1 B , but also includes a case where at least one of the adhesives is indirectly applied to the surface to be bonded (the inner circumferential surface  5   a ) of the rotor yoke  5 . That is, in  FIG.  1 B ′, the first adhesive  8   a  may be applied in a circular manner to the inner circumferential surface corresponding to the first bonding part  6   a  from the side of the opening at one end of the rotor yoke  5 , and the second adhesive  8   b  may be applied to the second bonding part  6   b  of the plate-like magnets  6 . 
     Next, as shown in  FIGS.  1 C and  1 C ′, the positioning member  10  having the pectinate partition members  10   b  coupled to the annular coupling part  10   a  for positioning the plate-like magnets  6  in the radial direction and the axial direction is attached to the inner circumferential surface  5   a  of the rotor yoke  5 . The partition members  10   b  are inserted from the side of the opening at the other end of the rotor yoke  5  and inserted until the flange part  10   c  comes into contact with the opening end. 
     Next, the plate-like magnets  6  are each inserted between the partition members  10   b  of the rotor yoke  5  with the positioning member  10  attached, from the side of the opening at the one end, and are arranged at a predetermined interval at the inner circumferential surface  5   a  of the rotor yoke  5  via the first adhesive  8   a  and the second adhesive  8   b .  FIG.  1 D  shows the state where the plate-like magnets  6  have been bonded to the rotor yoke  5 . 
     In the state shown in  FIG.  1 D , the first adhesive  8   a  coating the plate-like magnets  6  is cured, thus partially bonding the plate-like magnets  6  at the first bonding part  6   a  to the rotor yoke  5 . Specifically, ultraviolet rays are cast onto the first adhesive  8   a  in the case of an ultraviolet-curing adhesive, the adhesive is shut off from the outside air in the case of an anaerobic-curing adhesive, and the adhesive is brought into contact with the plate-like magnets  6  and then cured in the case of a quick-setting adhesive, thus partially bonding the plate-like magnets  6  to the rotor yoke  5 . 
     At least one of an ultraviolet-curing or anaerobic-curing adhesive and a quick-setting adhesive may be used as the first adhesive  8   a , and for example, a mixture of an ultraviolet-curing adhesive and an anaerobic-curing adhesive may be used. In this case, as the adhesive at the end surface of the plate-like magnets  6  is cured by ultraviolet irradiation and thus becomes shut off from the outside air, and therefore the adhesive inside (inside the void  9 , see FIG.  3 B 2 ) is put in an anaerobic state and cured. 
     Next, as shown in  FIG.  1 E , the unnecessary positioning member  10  is extracted from the rotor yoke  5  with the plate-like magnets  6  partially bonded, via the opening at the other end. 
     Next, as shown in  FIG.  2 A , the rotor hub  4  and the rotor shaft  3  assembled together as shown in  FIG.  1 A  are fitted in the opening at the one end of the rotor yoke  5  and assembled in a unified manner, thus assembling the rotor  1 .  FIG.  2 B  shows the assembled state of the rotor  1 . 
     Next, the epoxy resin-based second adhesive  8   b  is heat-cured at a predetermined temperature within a range of 100° C. to 180° C., thus bonding and fixing the plate-like magnets  6  at the second bonding part  6   b  to the inner circumferential surface of the rotor yoke  5 . 
     The plurality of plate-like magnets  6  may be magnetized before being bonded inside the rotor yoke  5  or may be magnetized after being bonded inside the rotor yoke  5 . 
     While the plate-like magnets  6 , if magnetized in advance, may attract each other and stick to each other when inserted in the rotor yoke  5 , using the positioning member  10  eliminates the occurrence of such an inconvenience. Also, if the plate-like magnets  6  are magnetized after being bonded to the inner circumferential surface  5   a  of the rotor yoke  5 , the work of assembling the plate-like magnets  6  is easier and is less susceptible to the influence of thermal demagnetization. 
     In this way, the rotor  1  is produced and assembled to the stator  2  and the motor M is thus produced. Specifically, as shown in  FIG.  2 C , the rotor  1  has the rotor shaft  3  inserted in the bearing housing  2   a  of the stator  2  and is rotatably supported by a bearing, not illustrated. The plate-like magnets  6  of the rotor yoke  5  are arranged opposite the stator pole teeth  7   b  of the stator core  7  and are rotatably assembled.  FIG.  2 D  shows the motor M having the rotor  1  assembled to the stator  2 . 
     In the case of the rotor  1  of the inner-rotor motor, the rotor  1  can be produced by a similar process that differs only in the method of applying the first and second adhesives  8   a ,  8   b , as shown in  FIGS.  4 A and  4 A ′. 
     That is, the positioning member  10  having the pectinate partition members  10   b  coupled to the annular coupling part  10   a  for positioning the plate-like magnets  6  in the radial direction and the axial direction is attached to the outer circumferential surface  5   b  of the rotor yoke  5  assembled in a columnar shape having the rotor shaft  3  at its center, as shown in  FIGS.  4 A and  4 A ′. As shown in  FIG.  4 A , the first adhesive  8   a  may be applied in a circular manner to the outer circumferential surface  5   b  corresponding to the first bonding part  6   a  of the rotor yoke  5 , and the second adhesive  8   b  may be applied to the bonding surface  6   c  corresponding to the second bonding part  6   b  of the plate-like magnets  6 . Alternatively, as shown in  FIG.  4 A ′, the first adhesive  8   a  for partial bonding may be applied to the bonding surface  6   c  of each plate-like magnet  6  and the second adhesive  8   b  may be applied to the second bonding part  6   b  of each plate-like magnet  6 . 
     Next, as shown in  FIGS.  4 A and  4 A ′, the positioning member  10  having the pectinate partition members  10   b  coupled to the annular coupling part  10   a  for positioning the plate-like magnets  6  in the radial direction and the axial direction is attached to the outer circumferential surface  5   b  of the rotor yoke  5 . The partition members  10   b  are fitted along the outer circumferential surface  5   b  of the rotor yoke  5  and are fitted until the annular coupling part  10   a  comes into contact with the end surface of the rotor yoke  5 . 
     Next, the plate-like magnets  6  are each inserted between the partition members  10   b  of the rotor yoke  5  with the positioning member  10  attached, and are positioned and arranged at a predetermined interval at the outer circumferential surface  5   b  of the rotor yoke  5  via the first adhesive  8   a  and the second adhesive  8   b .  FIG.  4 B  shows the state where the plate-like magnets  6  have been bonded to the rotor yoke  5 . 
     In the state shown in  FIG.  4 B , the first adhesive  8   a  coating the plate-like magnets  6  is cured, thus partially bonding the plate-like magnets  6  at the first bonding part  6   a  to the rotor yoke  5 . Specifically, ultraviolet rays are cast onto the first adhesive  8   a  in the case of an ultraviolet-curing adhesive, the adhesive is shut off from the outside air in the case of an anaerobic-curing adhesive, and the adhesive is brought into contact with the plate-like magnets  6  and then cured in the case of a quick-setting adhesive, thus partially bonding the plate-like magnets  6  to the rotor yoke  5 . 
     Next, as shown in  FIG.  4 C , the unnecessary positioning member  10  is extracted from the rotor yoke  5  with the plate-like magnets  6  partially bonded, via the opening at the other end, thus assembling the rotor  1 . 
     Finally, the epoxy resin-based second adhesive  8   b  is heat-cured at a predetermined temperature within a range of 100° C. to 180° C., thus bonding and fixing the plate-like magnets  6  at the second bonding part  6   b  to the outer circumferential surface  5   b  of the rotor yoke  5 . In this way, the rotor  1  of the inner-rotor motor is produced. 
     The plurality of plate-like magnets  6  may be magnetized before being bonded to the rotor yoke  5  or may be magnetized after being bonded inside the rotor yoke  5 . 
     According to the foregoing method of producing the rotor  1 , attaching the positioning member  10  having the pectinate partition members  10   b  coupled to the annular coupling part  10   a  for positioning in the radial direction and the axial direction, to the rotor yoke  5 , enables the positioning and arrangement of the plate-like magnets  6  in the radial direction and the axial direction between the partition members  10   b.    
     Also, the positioning member  10  can be extracted from the rotor yoke  5  after the plate-like magnets  6  are partially bonded to the rotor yoke  5  at the first bonding part  6   a  by curing the first adhesive  8   a  coating the plate-like magnets  6 , and therefore a reduction in the number of components, a reduction in the production cost, and a lighter weight of the rotor  1  can be achieved by omitting the positioning member  10 , which is originally unnecessary. 
     Also, since the plate-like magnets  6  are bonded and fixed to the rotor yoke  5  by heat-curing the second adhesive  8   b  coating the plate-like magnets  6  after the positioning member  10  is removed from the rotor yoke  5 , the plate-like magnets  6  can be bonded and fixed with high position accuracy. 
     As described above, the rotor  1  that achieves a reduction in the number of components, a reduction in the production cost, and a lighter weight, can be provided. Also, a method of producing a rotor that enables the plurality of plate-like magnets  6  to be positioned in the radial direction and the axial direction and bonded and fixed to the rotor yoke  5  with high position accuracy and thus achieves high assemblability, can be provided. 
     Also, the motor M that is inexpensive, has high assemblability, and can maintain motor characteristics, by using the rotor  1 , can be provided.