Patent Publication Number: US-2022213338-A1

Title: Process of preparation of an aqueous gel ink with variable color comprising silver nanoparticles

Description:
The present invention concerns a process for preparing in situ an aqueous gel ink with variable color, and to aqueous gel inks with variable color comprising said ester(s) of retinol represented by formula (I) and silver nanoparticles, obtained according to the process of the invention, and free from any dye and pigment. The invention also concerns a writing instrument comprising an aqueous gel ink with variable color according to the invention. 
     In nature, changing colors are frequently observed in the animal&#39;s world, either for camouflage or for courting by respectively fading in or standing out from the environment. Numerous living organisms can rapidly alter their appearance in response to changes in the environment. The most well-known examples are chameleons that are able to quickly change the color of their skin by aggregating or dispersing pigments within dermal chromatophores (J. Teyssier et al., Nature Communications 6, 2014, 6368). 
     Currently, there are two types of change in color present in nature zo that researches focus on structural and plasmonic color. 
     The structural color is observable on the wings of the morpho butterflies or on some plants and fruits. The color change is due to the light reflecting on the microstructures. Their specific shape ensures that the angle by which the light hits the wing influences the color reflected. The plasmonic color effect is deeper than for the structural color. In fact, the change in color is due to both the light absorption by metallic nanoparticles and the spacing between them in the material. This effect can, for example, be observed amongst the chameleons. Indeed, the color of their skin can change if they get excited. The change of color is due to the guanine crystals contained in their skin, which get farther away from each other when they get angry. 
     Replicating the way animals change their color is not exactly practical for some types of objects, though it can be the inspiration for another approach of creating a color change in other matrix. 
     On this basis, the inventors have surprisingly found that it is possible to obtain new aqueous gel inks that are capable of changing color when writing by replacing former aqueous gel inks containing dyes and pigments by new ones that are nanoparticle-based. Therefore, one of the main objectives of the present invention is to replace all types of dyes and pigments normally present in aqueous gel inks, which have the disadvantage of being expensive and causing high production costs. Another objective of the present invention is to replace all types of dyes and pigments normally present in aqueous gel inks, which have the disadvantage of being irritating to biological membranes, for example skin and eyes, and may cause allergies. Furthermore, the inventors have surprisingly found that the new aqueous gel inks containing nanoparticle-based are also resistant to UV light thereby improving light stability over time. To this end, the inventors have developed a specific process through which it is possible to obtain new aqueous gel inks with variable color when writing by replacing former aqueous gel inks containing dyes and zo pigments by new ones that are nanoparticle-based. The process developed within the framework of the invention also presents the advantage of being performed in aqueous media, and therefore to be a “green process”. In addition, the process of the invention is performed at low temperature ranges, works in an ecologically viable manner, and also takes account of ecological requirements. 
     The present invention relates to a process for preparing in situ an aqueous gel ink with variable color comprising the following steps:
         (i) preparing a gel-based matrix of aqueous ink comprising 0.005 to 0.1 mol·L −1  of ester(s) of retinol represented by the following formula (I)       

     
       
         
         
             
             
         
       
         
         
           
             
               
                 Wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group and 
               
             
             (ii) adding a solution of 0.002 to 0.05 mol·L −1  silver salts (Ag + ) to the gel-based matrix of aqueous ink prepared in step (i), to obtain an aqueous gel ink with variable color with silver nanoparticles dispersed therein. 
           
         
       
    
     In the sense of the invention, the term “in situ” means that the silver nanoparticles present in the aqueous gel ink of the invention are synthetized directly in the gel-based matrix of the aqueous ink. 
     In the sense of the invention, the term “variable color” is intended to mean that the color of the aqueous gel ink by visual observation is not the same before application on absorbing support, and after application on absorbing support, specifically paper, cardboard or textiles. 
     In fact, the change of color is preferably immediately observed (in particular in less than 5 seconds, preferably less than one second) by visual observation when the aqueous gel ink according to the invention is deposited on absorbing support. 
     For the purposes of the present invention, the term “ink” is intended to mean a “writing ink” which is intended to be used in a writing instrument, and in particular in a pen. A writing ink should not be confused with a “printing ink” which is used in printing machines and which does not have the same technical constraints and thus the same specifications. Indeed, a writing ink must not contain solid particles of which the size is greater than the channels of the writing instrument, in order to avoid blocking them, which would inevitably lead to writing being irreversibly stopped. In addition, it must allow an ink flow rate suitable for the writing instrument used, in particular a flow rate of between 100 and 500 mg/200 m of writing, and advantageously between 150 and 400 mg/200 m of writing. It must also dry sufficiently rapidly to avoid smudging the writing medium. It must also avoid the problems of migration (bleeding) over time. Thus, the ink according to the present invention will be suitable for the writing instrument for which it is intended, in particular for a pen. 
     In addition, a “writing ink” must not be too fluid, so as to avoid leaks during writing. However, it must be sufficiently fluid to facilitate the flow of the writing action. 
     In the particular case of the invention, the writing ink can be more specifically a “gel ink” (which corresponds therefore to a thixotropic ink), in particular the viscosity measured at rest (at a shear rate of 0.01 s −1 ) at 20° C. is different and in particular higher than the viscosity measured with a shear rate of 100 s −1  at 20° C. using the same rheometer such as a cone-and-plate rheometer for example Malvern KINEXUS with a cone of 60 mm and an angle of 1° . In a particular embodiment, the viscosity of the gel ink according to the present invention measured under these conditions ranges from 1,000 to 7,000 mPa·s, advantageously from 2,000 to 5,000 mPa·s, and more advantageously from 2,500 to 3,500 mPa·s, with a shear rate of 1 s −1 , and advantageously from 5 to 50 mPa·s, more advantageously from 7 to 40 mPa·s, and still more advantageously from 10 to 20 mPa·s with a shear rate of 5,000 s −1 . Advantageously, such a viscosity is stable during storage for at least three months at 40° C. and 20% relative humidity, in particular the viscosity will not have a more than 50% decrease. More advantageously, the return to viscosity at rest after shear is very quick, advantageously at most a few minutes, in order to avoid the static leakage in the minutes after writing. In the present invention, the gel-based matrix of aqueous ink prepared in step (i) may comprise from 50 to 95%, preferably from 60 to 90%, and more preferably from 70 to 85%, by weight of water. 
     The gel-based matrix of aqueous ink prepared in step (i) may also comprise classic gel ink ingredients such as solvents, antimicrobial agents, corrosion inhibitors, antifoam agents, rheology modifiers, etc. The gel ink ingredients used to prepare the gel-based matrix of aqueous ink of step (i) io will be largely described below, in relation with the subject-matter of the aqueous gel ink with variable color of the invention. 
     According to a preferred embodiment of the invention, the process for preparing in situ an aqueous gel ink with variable color comprises the following steps:
         (i) preparing a gel-based matrix of aqueous ink comprising 0.005 to 0.1 mol·L −1  of ester(s) of retinol represented by the following formula M       

     
       
         
         
             
             
         
       
         
         
           
             
               
                 Wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group, and 
               
             
             (ii) adding a solution of 0.002 to 0.05 mol·L −1  silver salts (Ag + ) to the gel-based matrix of aqueous ink prepared in step (i), to obtain an aqueous gel ink with variable color with silver nanoparticles dispersed therein 
           
         
       
    
     In the most preferred embodiment of the invention, the process for preparing in situ an aqueous gel ink with variable color comprises the following steps:
         (i) preparing a gel-based matrix of aqueous ink comprising 0.005 to 0.1 mol·L −1  of ester(s) of retinol represented by the following formula (I)       

     
       
         
         
             
             
         
       
         
         
           
             
               
                 Wherein R represents a methyl group, 
               
             
             (ii) adding a solution of 0.002 to 0.05 mol·L −1  silver salts (Ag + ) to the gel-based matrix of aqueous ink prepared in step (i), to obtain an aqueous gel ink with variable color with silver nanoparticles dispersed therein. 
           
         
       
    
     The ester of retinol represented by the formula (I), wherein R represents a methyl group, is commonly known retinyl acetate. The retinyl acetate (CAS number: 127-47-9), also known as vitamin A acetate, may be purchased via Sigma-Aldrich. The retinyl acetate may be added in the zo form of a solution or in the form of powder. 
     The ester (s) of retinol represented by the following formula (I) wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group reduces the silver salts to elemental metal (i.e. oxidation state: 0). 
     In a preferred embodiment, the concentration of ester (s) of retinol represented by formula (I) wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group in the gel-based matrix of aqueous ink of step (i) ranges from 0.01 to 0.08 mo1.1= 1 , and preferably from 0.02 to 0.05 mo1.1= 1 . 
     In the present invention, the solution of silver salts (Ag + ) is advantageously a solution of nitrate silver AgNO 3 . Silver nanoparticles are formed when contacting the solution of silver salts with the ester (s) of retinol represented by formula (I) wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group 
     In a preferred embodiment, the concentration of silver salts (Ag + ) in the gel-based matrix of aqueous ink of step (ii) ranges from 0.01 to 0.03 mol·L −1 . 
     The addition of a solution of silver salts (Ag + ) to the gel-based matrix of aqueous ink prepared in step (i) can be made by continuous injection. 
     In a preferred embodiment, the silver nanoparticles have the shape of spheres or polyhedral shape, preferably polyhedral shape, and more preferably triangular, square, rectangular shapes. 
     In a preferred embodiment, the molar ratio between the silver salts (Ag + ) and ester(s) of retinol represented by formula (I) wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group ranges from 0.10:1 to 1:1, and preferably from 0.15:1 to 0.50:1. 
     The present invention also concerns an aqueous gel ink with variable color obtained according to the process of the invention, said aqueous gel comprising ester of retinol (I) represented by formula (I) wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group and silver nanoparticles. 
     The process according to the invention enables to obtain an aqueous ink composition which exhibits a plasmon effect (plasmon color). 
     In a preferred embodiment, the present inventions concerns an aqueous gel ink with variable color obtained according to the process of the invention, said aqueous gel comprising retinyl acetate and silver nanoparticles. 
     The ester(s) of retinol represented by formula (I) wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group and silver nanoparticles of the aqueous gel ink of the invention are as defined above in relation with the subject-matter of the process of the invention. 
     Depending on their size, shape, and distance, the color of the dispersion of the silver nanoparticles can change, as well as its properties. This is due to the plasmon resonance. The exposure of the silver nanoparticles to a certain frequency of waves brings the electrons to gather in a certain place, which changes in accordance with the size and shape of the silver nanoparticles. This agglomeration of electrons provokes an anisotropy of the silver nanoparticles, which will then lead to a change of light absorption and scattering, resulting in a specific color. Plasmon resonance is also affected by the distance between the silver nanoparticles due to the coupling of said silver nanoparticles. Indeed, the closer the silver nanoparticles are, the more they will interact with each other, which will increase their coupling effect also called plasmon effect. In the same way, the shape influences the plasmon resonance. 
     In the aqueous gel ink with variable color of the invention, the amount of ester(s) of retinol represented by formula (I) wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group advantageously ranges from 1 to 10%, and more advantageously from 2 to 5%, by weight relative to the total weight of the aqueous gel ink. 
     In the aqueous gel ink with variable color of the invention, the silver nanoparticles have the shape of spheres or polyhedral shape, preferably polyhedral shape 
     In the aqueous gel ink with variable color of the invention, the silver nanoparticles of the invention have preferably an average particle size ranging from 20 to 150 nm, and more preferably from 50 to 100 nm. This average particle size is determined by analysis of 2D images (microscope: JEOL ARM 200), according to the standard IS09001:2015. 
     In the aqueous gel ink with variable color of the invention, the amount of silver nanoparticles advantageously ranges from 0.05 to 0.5%, and more advantageously from 0.08 to 0.4%, by weight relative to the total weight of the aqueous gel ink. 
     In the aqueous gel ink with variable color of the invention, the amount of water advantageously ranges from 50 to 95%, more advantageously from 60 to 90%, and even more advantageously from 70 to 85%, by weight relative to the total weight of the aqueous gel ink. 
     The aqueous gel ink with variable color of the invention may also comprise classic gel ink ingredients such as solvents, antimicrobial agents, corrosion inhibitors, antifoam agents, rheology modifiers, as described below. These gel ink ingredients are added to the gel-based matrix of aqueous ink in step (i) of the process of the invention. 
     The aqueous gel ink of the invention may comprise a solvent. Among the solvents that can be used, mention may be made of polar solvents miscible in water such as: 
     glycol ethers such as triethylene glycol, polyethylene glycol, diethylene glycol monoethyl ether, diethylene-glycol-mono butyl ether, dipropyleneglycol monobutyl ether, tripropylene glycol monomethyl ether, phenoxyethanol, phenoxypropanol, 
     alcohols: linear or branched alcohol in C 1 -C 15  such as isopropanol, butanol, isobutanol, pentanol, benzyl alcohol, glycerin, diglycerin, polyglycerin, 
     esters such as ethyl acetate or propyl acetate, carbonate esters such as propylene carbonate or ethylene carbonate, 
     ketones such as methylisobutylketone (MIBK), acetone or zo cyclohexanone, and 
     mixtures thereof. 
     In a preferred embodiment, the solvent is chosen in the group consisting of glycol ethers, and more preferably is chosen in the group consisting of triethylene glycol, polyethylene glycol, diethylene glycol monoethyl ether, diethylene-glycol-mono butyl ether, dipropyleneglycol monobutyl ether, tripropylene glycol monomethyl ether, phenoxyethanol, phenoxypropanol, and mixtures thereof. In a further advantageous embodiment the solvent is chosen in the group consisting of triethylene glycol, polyethylene glycol, and mixture thereof. 
     Advantageously, the solvent is present in the aqueous gel ink of the invention in an amount ranging from 5 to 35%, more advantageously from 9 to 30%, and even more advantageously from 11 to 25%, by weight relative to the total weight of the aqueous gel ink. 
     The aqueous gel ink of the invention may comprise an antimicrobial agent such as isothiazolinone (ACTICIDE from Thor), preferably chosen in the group consisting of 1,2-benzisothiazolin-3-one, 2-methyl-4-isothiazolin-3-one, and mixture thereof. 
     Advantageously, the antimicrobial agent is present in the aqueous gel ink of the invention in an amount ranging from 0.01 to 0.5%, and more advantageously from 0.1 to 0.2%, by weight relative to the total weight of the aqueous gel ink. 
     The aqueous gel ink of the invention may comprise a corrosion inhibitor, preferably chosen in the group consisting of tolytriazole, benzotriazole, and mixture thereof. 
     Advantageously, the corrosion inhibitor is present in the aqueous gel ink of the invention in an amount ranging from 0.05 to 1%, more advantageously from 0.07 to 0.5%, and even more preferably from 0.08 to 0.15%, by weight relative to the total weight of the aqueous gel ink. 
     The aqueous gel ink of the invention may comprise an antifoam agent, preferably a polysiloxane-based antifoam agent, and more zo preferably an aqueous emulsion of modified polysiloxane (such as MOUSSEX® from Synthron, TEGO® Foamex from Evonik). 
     Advantageously, the antifoam agent is present in the aqueous gel ink of the invention in an amount ranging from 0.05 to 1%, more advantageously from 0.1 to 0.5%, and even more advantageously from 0.2 to 0.4%, by weight relative to the total weight of the aqueous gel ink. 
     The aqueous gel ink of the invention may comprise a rheology modifier capable of generating a gelling effect, preferably chosen in the group consisting of xanthan gum, gum arabic, and mixture thereof. 
     Advantageously, the rheology modifier is present in an amount ranging from 0.08 to 2%, more preferably from 0.2 to 0.8%, and even more preferably from 0.3 to 0.6%, by weight relative to the total weight of the aqueous gel ink. 
     The aqueous gel ink with variable color of the invention may also comprise other additives such as: 
     pH regulators like sodium hydroxide and triethanolamine, 
     lubricants, 
     coalescing agents, 
     crosslinking agents, 
     wetting agents, 
     plasticizers, 
     antioxidants, and 
     UV stabilizers. 
     When present, these additives are added to the gel-based matrix of aqueous ink in step (i) of the process of the invention. 
     In one aspect, the invention relates to a process for preparing in situ an aqueous ink, more specifically an aqueous ink, with variable color comprising the following steps:
         (i) preparing a matrix of aqueous ink, comprising 0.005 to 0.1 mol·L −1  of ester(s) of retinol represented by the following formula (I)       

     
       
         
         
             
             
         
       
         
         
           
             
               
                 Wherein R represents a C1-C6 aliphatic group, said aliphatic group being optionally substituted with at least one hydroxy, halogen, amino, C1-C3 alkyl and/or C1-C3 alkoxy group, said aliphatic group being preferably a C1-C6 alkyl group, preferably a C1-C4 alkyl group, preferably unsubstituted, preferably a methyl group and 
               
             
             (ii) adding a solution of 0.002 to 0.05 mol·L −1  silver salts (Ag + ) to the matrix of aqueous ink, prepared in step (i), to obtain an aqueous ink, with variable color with silver nanoparticles dispersed therein. 
           
         
       
    
     In one aspect, the invention relates to an aqueous ink with variable color obtained according to the process of the invention, in particular said aqueous ink comprising ester of retinol (I) represented by formula (I) and silver nanoparticles, in particular which are as defined in the present disclosure. 
     The aqueous ink with variable color of the invention may also comprise classic ink ingredients as described previously such as solvents, antimicrobial agents, corrosion inhibitors, antifoam agents, rheology modifiers. These ingredients are added to the matrix of aqueous ink in step (i) of the process of the invention. 
     In one aspect, the invention relates to the use of the aqueous ink, more specifically of the aqueous gel ink, of variable color as defined above for writing onto an absorbing support. In one embodiment, the absorbing zo support is a porous substrate, specifically paper, cardboard, or textiles. 
     The present invention also concerns a method of writing with an aqueous ink, more specifically with an aqueous gel ink, of variable color comprising the step of writing onto an absorbing support, wherein the absorbing support is a porous substrate, specifically paper, cardboard or textiles, with an aqueous ink with variable color according to the invention. 
     After writing onto an absorbing support with the aqueous gel ink of variable color of the invention, the distance between the silver nanoparticles within the aqueous gel ink applied on absorbing support is lower than 1 pm, preferably varies from 50 nm to 800 nm, and more preferably varies from 100 nm to 500 nm. 
     Finally, the present invention concerns a writing instrument comprising: 
     an axial barrel containing the aqueous ink, more specifically the aqueous gel ink, according to the invention, and 
     a pen body which delivers the aqueous ink stored in the axial barrel. 
     The writing instrument of the invention may be chosen in the group consisting of gel pens, felt pens, correction fluid, markers, and preferably gel pens. 
     In addition to the foregoing, the invention also comprises other provisions which will emerge from the additional description which follows, which relates to the preparation of aqueous gel inks with variable color according to the process of the invention and comparative examples. 
    
    
     EXAMPLES 
     Example 1 
     Preparation of an Aqueous Gel Ink With Variable Color Based on Retinyl Acetate and Silver Nanoparticles, According to the Process of the Present Invention 
     In a first step (i), a gel-based matrix of aqueous ink was prepared by mixing 15 g of triethylene glycol (solvent), 4 g of polyethylene glycol zo (solvent), 0.19 g of Acticide® MBS (antimicrobial agent), and 0.10 g of Additie RC8221 (corrosion inhibitor). The mixture was homogeneized with a homogeneizer mixer at a speed of 15 m·s −1  during 15 minutes and heated at a temperature of 35° C. Then, 0.40 g of xanthan gum (rheology modifier) was added to the mixture. The mixture was homogenized with a homogenizing mixer at a speed of 15 m·s −1  during 15 minutes at a temperature of 35° C. 80.01 g of deionized water was slowly added to the mixture. The mixture was left to stand for 2h30. Then, 0.30 g of Moussee S 9092 (antifoam agent) was added. The mixture was homogenized with a homogenizing mixer at a speed of 15 m·s −1  during 30 minutes at a temperature of 35° C. The gel-based matrix of aqueous ink obtained was cooled at room temperature (25° C.). Then, 1 mL of the obtained gel-based matrix of aqueous ink was mixed with 0.025 g of retinyl acetate (Sigma-Aldrich). The mixture was homogeneized with a homogeneizer mixer at a speed of 400 rpm during 15 minutes. 
     In a second step (ii), 100 μL of a solution of silver nitrate (Carl Roth) (100 mM) was introduced into the mixture at a speed of 400 rpm during 15 minutes. 
     After the addition of the solution of silver nitrate by continuous injection, the color of the aqueous gel ink was dark grey. 
     The average particle size of the silver nanoparticles present within the aqueous gel ink is of 70 nm by analysis of 2D images (microscope: JEOL ARM 200), according to the standard 1509001:2015. 
     When the obtained aqueous gel ink with variable color was written on cellulosic paper, the color changed from dark grey to brown immediately (&lt;1second) through a dissemination process of the silver nanoparticles on cellulosic paper. 
     Thus, the color of the ink is not the same before application on cellulosic paper and after application on cellulosic paper. 
     Comparative Example 1 
     Preparation of an Aqueous Gel Ink Based on Retinyl Palmitate and Silver Nanoparticles 
     In a first step, a gel-based matrix of aqueous ink was prepared by mixing 15 g of triethylene glycol (solvent), 4 g of polyethylene glycol (solvent), 0.19 g of Acticide® MBS (antimicrobial agent), and 0.10 g of Additie RC8221 (corrosion inhibitor). The mixture was homogeneized with a homogeneizer mixer at a speed of 15 m·s −1  during 15 minutes and heated at a temperature of 35° C. Then, 0.40 g of xanthan gum (rheology modifier) was added to the mixture. The mixture was homogenized with a homogenizing mixer at a speed of 15 m·s −1  during 15 minutes at a temperature of 35° C. 80.01 g of deionized water was slowly added to the mixture. The mixture was left to stand for 2h30. Then, 0.30 g of Moussee S 9092 (antifoam agent) was added. The mixture was homogenized with a homogenizing mixer at a speed of 15 m·s −1  during 30 minutes at a temperature of 35° C. The gel-based matrix of aqueous ink obtained was cooled at room temperature (25° C.). Then, 1 mL of the obtained gel-based matrix of aqueous ink was mixed with 0.025 g of retinyl palmitate (CAS number: 79-81-2, from Sigma-Aldrich). The mixture was homogeneized with a homogeneizer mixer at a speed of 400 rpm during 10 minutes. 
     In a second step, 100 μL of a solution of silver nitrate (Carl Roth) (100 mM) was introduced into the mixture at a speed of 400 rpm during 5 to 10 minutes. After the addition of the solution of silver nitrate by continuous injection, the color of the aqueous gel ink was greyish white color. 
     The average particle size of the silver nanoparticles present within the aqueous gel ink is of 20 nm by analysis of 2D images (microscope: JEOL ARM 200), according to the standard IS09001:2015. 
     When the obtained aqueous gel ink was written on cellulosic paper, the color did not change and remained greyish white color. 
     Thus, the color of the ink is the same before application on cellulosic paper and after application on cellulosic paper. 
     Comparative Example 2 
     Preparation of an Aqueous Gel Ink with Fixed Color Based on Retinyl Acetate and Gold Nanoparticles 
     In a first step (i), a gel-based matrix of aqueous ink was prepared by mixing 15 g of triethylene glycol (solvent), 4 g of polyethylene glycol (solvent), 0.19 g of Acticide® MBS (antimicrobial agent), and 0.10 g of Additie RC8221 (corrosion inhibitor). The mixture was homogeneized with a homogeneizer mixer at a speed of 15 m·s −1  during 15 minutes and heated at a temperature of 35° C. Then, 0.40 g of xanthan gum (rheology modifier) was added to the mixture. The mixture was homogenized with a homogenizing mixer at a speed of 15 m·s −1  during 15 minutes at a temperature of 35° C. 80.01 g of deionized water was slowly added to the mixture. The mixture was left to stand for 2h30. Then, 0.30 g of Moussex S 9092 (antifoam agent) was added. The mixture was homogenized with a homogenizing mixer at a speed of 15 m·s −1  during 30 minutes at a temperature of 35° C. The gel-based matrix of aqueous ink obtained was cooled at room temperature (25° C.). Then, 1 mL of the obtained gel-based matrix of aqueous ink was mixed with 0.05 g of retinyl acetate (Sigma-Aldrich). The mixture was homogeneized with a homogeneizer mixer at a speed of 400 rpm during 15 minutes. 
     In a second step (ii), 100 μL of a solution of gold (III) chloride trihydrate (520918-1G from Sigma-Aldrich) (200 mM) was introduced into the mixture at a speed of 400 rpm during 15 minutes. 
     After the addition of the solution of gold (III) chloride trihydrate by continuous injection, the color of the aqueous gel ink was dark blue. 
     The average particle size of the gold nanoparticles present within the aqueous gel ink is of 50 nm by analysis of 2D images (microscope: JEOL ARM 200), according to the standard IS09001:2015. 
     When the obtained aqueous gel ink was written on cellulosic paper, the color did not change and remained dark blue. 
     Thus, the color of the ink is the same before application on cellulosic paper and after application on cellulosic paper.