Patent Publication Number: US-2005129800-A1

Title: Method for the manufacturing of a matrix and a matrix manufactured according to said method

Description:
TECHNICAL FIELD  
      The present invention relates in the first place to a method for the manufacture of a matrix suitable for use as a mould-cavity insert in a compression-moulding, embossing and/or injection-moulding machine, and particularly to a matrix having one surface, or a part thereof, provided with a microstructure, which microstructure is reproducible on the surface of a plastic component as a complementary microstructure in a machine used, said component being formed of a plastic composite or plastic material used.  
      The invention relates in the second place to a matrix manufactured in accordance with the method, which is suitable for use in a compression-moulding, embossing and/or injection-moulding machine.  
      Matrices of the type under discussion can be manufactured by having a master or an original, with a (positive) microstructure on its surface coated with a number of layers of metal, removing the metal layers, with a (negative) micro structure, from the master, which thus forms a metal plate serving as a matrix or mould-cavity insert in the compression-moulding, embossing and/or injection-moulding machine.  
      The expression “positive” surface structure shall be understood to mean the surface structure that appears on a plastic component produced from the plastic material in a machine, and “negative” surface structure shall be understood to mean its inverse surface structure, i.e. the surface structure displayed by a matrix or mould-cavity insert in the machine used.  
      “Plastic composite” shall be taken to mean a mixture of a polymer material and a curable filler material, where the filler material is usually in excess.  
      The method associated with the present invention shall be deemed applicable for directly producing a matrix or mould-cavity insert for a machine for moulding plastic components, which may then be considered as an original, an original from which another matrix, an original, can be produced, from which a replicated original can be manufactured, etc.  
      A person skilled in this technical area will perceive that a method for manufacturing a matrix serving as a mould-cavity insert could very well be used for manufacturing an original, from which said matrix is formed, a superior original from which said original can be formed, and so on.  
     BACKGROUND ART  
      When replicating microstructures on plastic components manufactured in a machine of the type described in the introduction, it is known and usual to first manufacture an original or master in a suitable manner, and from this master manufacture a matrix in the form of a mould-cavity insert for the machine.  
      A known method of manufacturing such a master entails the use of known lithographic methods.  
      It is in this case advantageous to select lithographic methods that have been developed primarily for use in the micro-electric field.  
      One of these methods is based on performing etching and/or depositions on the surface of a semiconducting material.  
      Other methods are based on removing parts of the material with the aid of a laser, so-called laser ablation, using conventional NC machines, with the aid of a precision-controlled diamond cutter with high-speed spindle, with the aid of wire or electro-erosion and/or some other suitable method.  
      Such originals or masters are usually manufactured in a material suitable for the selected treating method.  
      In the case of lithographic processes, therefore, the material is usually a plate or a sheet of silicon, glass or quartz, whereas for laser ablation, the material selected is usually a plate or a sheet of a plastic composite and/or a polymer.  
      For material machining both plastic and relatively soft metals may be suitable.  
      It is well known that the demands placed on a selected replication process for a certain choice of material in the matrix or mould-cavity insert and the plastic component are not the same as those that must be placed on the original or the master.  
      It may thus be mentioned that when injection-moulding plastic components in a machine, in which one or more surface parts shall display a microstructure, mould halves pertaining to the machine and matrices or mould-cavity inserts used for one or both mould halves must be made of a stable material that will withstand the high pressures prevailing during the manufacturing process, and that will not be worn down unnecessarily quickly by the thermal and mechanical wear the mould parts and matrix are subjected to during the moulding process.  
      It is known to manufacture such matrices, particularly matrices used in microsystem context, by having the shape and surface structure of a master transfer to a metal sheet formed as a matrix.  
      Such manufacture is based on first manufacturing a master on the surface of a plate or sheet of glass, a semi-conducting material or metal, coating the surface with a light-sensitive layer and, via laser or the like, exposing selected surface sections of this light-sensitive layer, and then washing and cleaning these selected surface sections.  
      A metal layer is then applied on this exposed and cleaned surface by means of a sputtering process and/or a vaporising process and, if necessary, a plating process for a sufficient length of time for a metal sheet to be formed.  
      When the metal sheet is removed from the master it can display a first surface with a negative microstructure and can serve as a matrix or a mould-cavity insert, after additional machining, a plaining machining, of a second surface facing the mould half in the machine.  
      This is the method that is currently used for manufacturing a matrix or mould-cavity insert for inclusion in an injection moulding machine, intended for the manufacture of optical plates or discs.  
      It is known to coat an electrically insulating plate or disc serving as master or matrix and having a microstructure, with a thin layer of metal by means of a sputtering and/or vaporising process.  
      It is known to coat an electrically insulating plate or disc or layer serving as matrix and having a microstructure, with a considerably thicker layer of metal by means of a plating process.  
      It is known via a plating process to coat a disc intended as matrix, with an electrically conducting layer such as nickel, silver, gold or the like.  
      It is also usual to have an applied metal layer contacted and a disc immersed in a solution consisting of, amongst other things, metal ions, whereupon a current is forced through the solution towards the disc and metal ions are precipitated out as a pure metal on the surface. It is thus possible to produce a structure in the metal that has a function inverse to the microstructure on the master.  
      It has been found that the method described above is simple to use for relatively flat structures, particularly when the depth of the microstructure is limited to and chosen less than approximately 0.2 μm.  
      In conclusion, it can be ascertained that different methods can be used to produce originals with different microstructures.  
      It is thus known, during working of one and the same material (silicon plate or disc) to create, in several processes, different micro and surface structures on different surface sections, to be transferred to a matrix.  
      The time it takes to manufacture an original is substantially the sum of the times required for each process used.  
      In the following description, thus, a first method is mentioned for manufacturing an original with a first type of microstructure, a second method for manufacturing an original with a second type of microstructure, and so on, in which a first matrix manufactured via the first original and a second matrix manufactured via the second original will be used.  
     DESCRIPTION OF THE PRESENT INVENTION  
      Technical Problems  
      Considering that the technical deliberations a person skilled in the art must perform in order to be able to offer a solution to one or more of the technical problems posed constitute initially an insight into the measures and/or the sequence of measures to be taken, and also a selection of the means required, the following technical problems should be relevant in developing the object of the present invention.  
      Considering the prior state of the art as described above, it would appear to be a technical problem to be able to propose a simple method for manufacturing a matrix adaptable for use in a compression-moulding, embossing and/or injection-moulding machine in which the matrix is provided with a negative microstructure on its surface and which microstructure is reproduced in the machine as a positive microstructure on a surface part of a plastic component produced via a utilised plastic composite or plastic material, thereby creating an inexpensive matrix with a sharp microstructure where the matrix may serve as mould-cavity insert and may display a microstructure section of a first type, or a second type, etc., like a hybrid.  
      It should also be considered a technical problem, with the aid of a number of originals, manufactured in accordance with individual manufacturing processes, and/or a number of matrices produced from these originals, to create such conditions that the time required for producing a mould-cavity insert can be substantially reduced, despite complex surface sections for said insert.  
      A technical problem is also entailed in being able, using simple means, to create such conditions that said mould-cavity insert can be assigned a microstructure-related first wear surface formed on a first layer, with an adaptable and relatively high wear resistance.  
      It is also a technical problem to be able, using simple means and measures, to create conditions enabling a matrix to be built up of at least two layers, a thin first wear layer displaying said microstructure-related surface, and a thicker layer reinforcing this thin layer, the thicker layer being termed “carrier” in the following.  
      It should also be deemed a technical problem to be able to advocate a method for manufacturing a matrix in which a first master, with a first chosen microstructure, can be produced via a first process and a second master, with a second chosen microstructure, can be manufactured via a second process, separate from the first, and in which the whole or selected parts of matrices manufactured from said first and second masters are combined to form said matrix.  
      It is also a technical problem to be able to perceive the significance of and the advantages associated with manufacturing said first master with a number of similar or dissimilar surface sections, each of these, transferred to a matrix, being removable to form a first matrix section.  
      It is also a technical problem to be able to perceive the significance of and the advantages associated with manufacturing said second master with a number of similar or dissimilar surface sections, each of these, transferred to a matrix, being removable to form a second matrix section.  
      It is also a technical problem to be able to perceive the significance of and the advantages associated with one or more first matrix sections and one or more second matrix sections being applied with their microstructured surfaces on a support, where a sheet of nickel such as a flat sheet with polished surface, a mirror surface, is chosen as support.  
      A technical problem is entailed in being able to perceive the conditions for and advantages associated with said first matrix or a first matrix section, and said second matrix or a second matrix section, and/or one or more additional matrices or matrix sections, being pressed against the support at least while they are being covered by a first wear layer.  
      It is furthermore a technical problem to be able, using simple measures, to create such conditions that the material of a first, thin layer and the material of a second, thick layer or carrier can be selected having such properties and/or thicknesses that they can fulfil predetermined requirements and conditions for a mould-cavity insert.  
      It is also a technical problem to be able to perceive the significance of and the advantages associated with said matrix being manufacturable by a master with a microstructure assigned to its surface being coated with metal by means of a metal coating process, and coating the thin metal layer with a plastic composite to form said carrier.  
      It is also a technical problem to be able, using simple means and measures, to manufacture a matrix formed substantially or exclusively from a plastic composite, usable in a machine, where the time required for manufacture of the matrix from a master is considerably reduced, partly by being able to entirely eliminate, or at least considerably reduce, the time required for forming a flat reverse side of a matrix from the plastic composite, which rear side can abut tightly against one of the two mould halves in the machine.  
      It is also a technical problem to be able to perceive the significance of using a master for the manufacture of the matrix, and applying a thin layer of metal to its positive microstructure surface, and for said metal layer, on the rear side of the microstructure, to display irregularities substantially corresponding to the microstructure, and to also perceive the advantages of filling said irregularities with a supporting plastic composite that, after curing or the like, forms a supporting carrier in the form of a layer, instead of building up the entire matrix with a thick metal layer.  
      It is also a technical problem to be able to perceive the significance of such filling of a chosen plastic composite and the formation of a carrier taking place in a special mould cavity.  
      It is also a technical problem to be able to perceive the significance of and the advantages associated with the plastic composite, and thus the carrier, being selected from a mixture of a plastic or polymer material and a filler material such as quartz or metal-filled epoxy or silicon polymer.  
      It is also a technical problem to be able to perceive the significance of and the advantages associated with the plastic composite used, and thus the carrier formed, being chosen with a coefficient of linear expansion and/or a heat transfer capability and/or a thermal capacitive capability suitable for a chosen process in the machine used.  
      A technical problem is also entailed in making use of a specifically chosen curing process in order to assign the chosen plastic composite a hardness and/or curing time dependent on the application by supplying heat to selected portions of the plastic composite or compound and/or illuminating the plastic composite or compound with UV light or, alternatively by the plastic composite being selected as a two-component type.  
      A technical problem is entailed in being able to perceive the significance of adapting a first wear layer and/or a thin metal layer and selecting the plastic composite, and thus the carrier, with a low heat transfer capability in order to keep the plastic compound pressed out into the machine and between the mould halves hot.  
      It is also a technical problem to be able to perceive the significance of and the advantages associated with, as well as the dimensioning rules required for, applying a second layer on the surface of the carrier facing away from the microstructured surface of the metal layer.  
      It is also a technical problem to be able to perceive the significance of selecting said second wear layer from a material displaying the properties of low friction against the flat surface of the mould half and high durability, such as titanium nitride or DLC (Diamond-Like-Carbon).  
      It is also a technical problem to be able to perceive the significance of said thin metal layer being applied on the master or original, if this consists of a non-electrically conducting material, by means of a sputtering process and/or a vaporising process or, if this consists of an electrically conducting material or an applied thin metal layer, by means of a plating process.  
      A technical problem is also entailed in, depending on the application in question, selecting the thickness of the metal layer in the injection-moulding machine within predetermined limits.  
      A technical problem is also entailed in being able to perceive the significance of and the advantages associated with creating such conditions that plaining of the rear side of the matrix and the carrier is considerably simplified and/or entirely eliminated.  
      Solution  
      To provide a solution to one or more of the technical problems listed above, the present invention is based on a method for the manufacture of a matrix, such as one provided with a (negative) microstructure on its surface, which microstructure is reproducible in a plastic composite or material as an inverted or complementary (positive) microstructure on a plastic component, in an injecting-moulding machine.  
      The invention is based on said matrix being manufactured by having a master or an original with a microstructure on its surface coated with a covering material.  
      The method in accordance with the invention relates particularly to a first master with a first chosen microstructure being produced via a first method, a second master with a second chosen microstructure being produced via a second method and, if necessary, one or more additional masters with chosen microstructures being produced via additional chosen methods.  
      It is also advocated that said first and second masters, or a matrix formed therefrom, be applied or placed with their microstructured surfaces adjacent.  
      Said first and second masters or matrices shall thereafter be covered with a layer pertaining to a first matrix, after which said layer is covered by a thicker layer, a carrier.  
      Said first and second first layers pertaining to the matrix, and said carrier, are now removed from said masters as a matrix-related unit.  
      Preferred embodiments falling within the scope of the present invention propose that said first master is produced having a number of similar or dissimilar surface sections, and that each of these, transferred to a matrix, is removed to form a first matrix section.  
      Said second master may also be produced having a number of similar or dissimilar surface sections, each of these, transferred to a matrix, is removed to form a second matrix section.  
      One or more first matrix sections and one or more second matrix sections and/or further additional matrix sections are applied with their microstructured surfaces on a support.  
      A sheet of nickel may advantageously be chosen as the support, said sheet usually consisting of a flat sheet with polished surface, like a mirror surface.  
      Said first matrix or a first matrix section, and said second matrix or a second matrix section, etc., are pressed against a support at least while they are being covered by a first wear layer.  
      The first matrix or matrix section has been provided with a first type of one amongst several selectable microstructures, the second matrix or matrix section has been provided with a second type of one amongst several selectable microstructures, and so on.  
      In accordance with proposed embodiments of the present invention pouring in a plastic composite, in order to smooth out irregularities, may be performed in a mould cavity.  
      It is also proposed that the plastic composite, and thus the carrier, may be selected from a polymer material and a filler material such as quartz or metal-filled epoxy or silicon polymer.  
      The plastic composite, and thus the carrier formed, may also be chosen with a coefficient of linear expansion and/or a heat transfer capability and/or a thermal capacitive capability suitable for a chosen process in and the design of the injection-moulding machine.  
      The plastic composite shall be cured in a manner suitable for injection moulding, such as by the supply of heat and/or illuminated by means of UV light.  
      The plastic composite could also be selected as a two-component type.  
      In accordance with the present invention a plastic composite, and thus the carrier, located under a hard wear layer serving as wear surface, shall be selected with a suitable heat transfer and/or thermal capacitive capability for keeping the plastic compound in the machine hot, while at the same time achieving short cycle times.  
      Also in accordance with the invention said plastic composite, and thus the carrier, may be coated with a second wear layer on the surface facing away from the surface of the first wear layer, in order to reinforce the matrix construction against damage due to wear.  
      Said second wear layer could consist, for instance, of titanium nitride or DLC.  
      In accordance with the invention said thin first wear layer may very well consist of a metal layer and this metal layer shall be applied by means of a sputtering process and/or a vaporising process or, alternatively, a plating process.  
      In accordance with the invention the thickness of the first wear layer, such as the metal layer, shall be selected with care, depending on the application and the design of the injection-moulding machine.  
      The invention also relates to a matrix suitable for use in a compression-moulding, embossing and/or injection-moulding machine as described above.  
      Advantages  
      The advantages that may be primarily considered characteristic of a method for manufacturing a matrix in accordance with the present invention for a compression-moulding and/or injection-moulding machine are thus that conditions are thereby created for achieving simple manufacture of the matrix by manufacturing a first master via a first process, a second master via a second process and, if necessary, producing matrices from these masters and thereafter combining said matrices or parts thereof to a matrix which is therefore simpler to produce with extremely varied microstructure-related sections, deriving from different manufacturing methods for the originals or masters used.  
      Adaptation of heat transfer and/or thermal capability of the matrix is thus possible so that the replication ability is increased in the manufacturing process, such as the embossing and/or injection-moulding process, since the plastic material being moulded does not freeze as soon as it comes into contact with the microstructured surface of the matrix but retains its fluidity properties sufficiently long for the microstructure pertaining to the matrix to be efficiently replicated on the plastic component produced.  
      The features deemed to be primarily characteristic of a method in accordance with the present invention are defined in the characterising part of the appended claim  1 , and the features deemed most characteristic for a matrix in accordance with the present invention are defined in the characterising part of the appended claim  21 . 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
      A currently preferred embodiment of an injection-moulding machine in which a matrix significant for the invention could be used, and a method for manufacturing this matrix, as well as a matrix thus manufactured with the features significant for the invention, will now be described in more detail with reference to the accompanying drawings, in which  
       FIG. 1  shows schematically a side view of an injection-moulding machine, utilising two mould halves assuming a position co-operating with each other,  
       FIG. 2  shows the machine illustrated in  FIG. 1 , in a position where a heated plastic compound in the form of a plastic composite is pressed through a fixed mould half to a space, formed between two mould halves, in view of compression moulding a plastic component,  
       FIG. 3  shows the injection-moulding machine when a movable mould half is displaced some way from a fixed mould half and the flat plastic component is removed from the movable mould half,  
       FIG. 4  shows in perspective a matrix or a mould-cavity insert for insertion into the movable mould half, displaying a microstructure, the microstructure illustrated in simplified form in an enlarged partial view, not necessarily to scale,  
       FIG. 5  shows a side view and in section an example of a method for manufacturing a matrix of previously known design,  
       FIG. 6  shows a side view and in section an example of a method for manufacturing a matrix in accordance with the invention,  
       FIG. 7  shows in perspective a first master divided into a number of identical surface sections,  
       FIG. 8  shows in an enlarged view and in cross section, details of a matrix produced on the matrix illustrated in  FIG. 6 ,  
       FIG. 9  shows a partial section of a first embodiment of a matrix manufactured in accordance with the invention,  
       FIG. 10  shows a partial section of a second embodiment of a matrix manufactured in accordance with the invention,  
       FIG. 11  shows the use of a mould cavity for manufacturing a matrix with a flat rear surface, and  
       FIG. 12  shows a sequence for manufacturing a matrix in accordance with the invention. 
    
    
     DESCRIPTION OF PREFERRED EMBODIMENT  
      The present invention relates to a method for manufacturing a matrix  2  for a compression-moulding, embossing and/or injection-moulding machine  1 .  
      This matrix or mould-cavity insert  2  is provided with a “negative” microstructure  2   a  on its surface, which microstructure  2   a  is reproducible in the injection-moulding machine  1  on a plastic component  3  produced from a plastic material, as a “positive” microstructure  3   a.    
      The method for manufacturing a matrix  2  suitable as a mould-cavity insert will be described in more detail, primarily with reference to  FIGS. 6, 7 ,  8  and  12 .  
      For the sake of simplicity the following description assumes that only the movable mould half  1   c  is provided with a mould-cavity insert  2  having a microstructure  2   a . However, a person skilled in the art will realise that also the fixed mould half  1   d  could be provided with such a mould-cavity insert.  
       FIGS. 1-3  show schematically an injection-moulding machine  1  provided with an ejection rod  1   a , a number (three) ejection pins  1   b , a movable mould half  1   c  and a fixed mould half  1   d.    
      A cavity  1   e , shaped to conform with a flat plastic component  3  produced by injection moulding, is formed between the movable form half  1   c  and the fixed mould half  1   d  and displays an inlet  1   f.    
       FIG. 1  also illustrates the use of a “torpedo” or “pine apple”  1   g , a cylinder wall  1   h , a heating element  1   i , an injection ram  1   j  and a feeding funnel  1   k  for granulate or powder  1   m.    
       FIG. 2  illustrates how a heated, fluid plastic compound or plastic material  4  surrounds the torpedo  1   g  and is pressed by a ram  1   j  through the inlet  1   f  to the cavity and into the cavity  1   e , the mould halves  1   c ,  1   d  assuming the united position shown in  FIG. 1 .  
       FIG. 3  shows that the movable mould half  1   c  is moved a suitable distance from the mould half  1   d  and, with the aid of the ejector rod  1   a  and ejector pins  1   b  the flat plastic component  3  is released from the movable mould  1   c  and the plastic component  3  falls out of the mould half  1   c.    
       FIG. 4  shows, greatly simplified and in perspective, a matrix  2  shaped to a plate or disc and provided with an upwardly facing microstructure  2   a  assigned to the surface.  
      This microstructure is usually extremely complex. However, a very simplified embodiment is illustrated in  FIG. 4 , enlarged but without any claim of being to scale.  
      For the sake of simplicity and clarity the following description will relate only to a first raised part  21 , an intermediate recess  22  and a second raised part  23 , all pertaining to the microstructure.  
      The matrix or mould-cavity insert  2  is thus provided with a negative microstructure  2   a  on its surface.  
      The matrix  2  comprises a disc or plate with a flat lower surface  2   b , usually a flat, machined surface  2   b , and rests against a flat support surface  1   c ′ in the movable mould half  1   c.    
      It is important here that a flat surface  2   b  pertaining to the matrix is suitable for resting against a flat surface  1   c ′ of the mould half  1   c , or opposing curved surfaces, so that the matrix  2  can withstand the compressive forces that will be exerted during a manufacturing process, i.e. an injection-moulding process.  
       FIG. 5  shows a cross section through a part of a known matrix  2 , the cross section being taken through the raised portions  21  and  23 , and the recess  22 .  
      According to the known method, shown in  FIG. 5 , said matrix  2  can be produced by a master  5 , with a positive microstructured surface, being coated in known manner with a metal surface, by using only a plating process.  
      Metal layer upon metal layer is thus built up by the plating process, or equivalent process, on the microstructured surface section  5   a  of the master  5 , so that a first metal layer will be able to cover even the lowest point of the microstructured surface part  5   a.    
      Since such a plating process will provide a metal layer in which the upper surface is irregular due to the surface structure  5   a , the plating process must continue to apply metal layer upon metal layer to a total thickness which, over the entire surface, will exceed a predetermined value or a plane designated  6  in  FIG. 5 .  
      In practice, the previously known method now requires all the metal material placed above the surface  6 , designed  6   a , to be ground away in some way or another.  
      The plating process for layers as thick as is the case here takes an extremely long time, as well as grinding the excess metal material  6   a  down to the plane  6  also being time-consuming.  
      The present invention also uses a master  5  for manufacturing a matrix or mould-cavity insert  2 . This master could in principle be manufactured in the same way as the master  5  in  FIG. 5 .  
      The present invention comprises in the first place a method for the manufacture of a matrix or mould-cavity insert  2  provided with a microstructure on its surface, which microstructure is reproducible in a plastic material as an inverted microstructure in a machine used, said microstructure being manufactured by having a master with a microstructure on its surface coated with a layer, and in the second place to a matrix thus manufactured.  
      The invention is shown in  FIG. 6  using a first master  51  with a microstructure  51   a , manufactured via a first method or a matrix  51 ′ manufactured from such a master, and a second master  52  with a microstructure  52   a  produced via a second method or a matrix  52 ′ manufactured from such a master, these being combined to form a hybrid matrix.  
      A hybrid matrix is a matrix that has a microstructured surface emanating from two or more masters or matrices produced from two or more manufacturing methods, each appropriate for a chosen microstructure.  
      Said first matrix  51  and second matrix  52 , or matrix parts  51 ′,  52 ′, can now be applied, with their microstructured surfaces  51   a ,  52   a , against a support  60 .  
      Said first and second matrix parts  51 ′,  52 ′ can now be coated with a first layer, here designated a support layer  7 .  
      Said layer  7  shall then be covered by a thicker layer, a carrier  8 .  
      Said first and second matrix parts  51 ′,  52 ′, together with said first layer  7  and said carrier  8  are now removed from the support  60  as a matrix-related unit.  
      Should the surfaces,  71 ,  72 ,  73  and  74  thus exposed not be suitable for direct application in a unit for forming plastic components, it is suggested that the surfaces  71 ,  72 ,  73  and  74  in  FIG. 6  be provided with a wear layer  7 ′, or the surfaces  71 ,  72 ,  73  and  74  may form surfaces for manufacturing a new matrix.  
      This method is associated with the method shown and described in Swedish patent application 99 03232-8, filed 10 Sep. 1999 under the title “A method for the manufacture of a matrix and a matrix manufactured according to said method”.  
       FIG. 7  illustrates that a first master  51  can be manufactured in a first manufacturing process, with a number of identical surface sections  51 : 1 ,  51 : 2 , whereupon a matrix manufactured from this master will also display a corresponding number of identical surface sections, two of which have been designated  51 ′: 1 ,  51 ′: 2 , and each of these can be separated in order to form matrix sections, such as a first matrix section  51 ′: 1  in  FIG. 4 .  
      Said second master can also be manufactured having a number of identical surface sections, and a matrix manufactured for this master can also display a corresponding number of identical surface sections, and each of these  52 ′: 1  can be separated to form a second matrix section. This is not shown in more detail but is obvious to one skilled in the art.  
      One or more first matrix sections, one or more second matrix sections, one or more additional matrix sections are applied with their microstructured surfaces against said support  60  in an order and an orientation that will conform with the desired result on a matrix and/or a plastic material produced.  
      A sheet of nickel is chosen as support  60 , said nickel sheet preferably consisting of a flat sheet with a polished surface  60   a , like the surface of a mirror.  
      Said first master or a first matrix section and said second master or a second matrix section, etc., are pressed against the support  60 , at least while they are being covered by a first layer  7  by means not shown in detail.  
      The first matrix  51  or matrix section  51 : 1  has been provided with a first type of one among several selectable microstructures.  
      The second matrix  52  or matrix section  52 : 1  has been provided with a second type of one among several selectable microstructures, and so on.  
      In accordance with the present invention these microstructured surfaces  51   a ,  52   a  may be covered with a thick wear layer.  
       FIG. 6  shows, somewhat exaggerated, that parts of a machined matrix material, such as the surfaces  71 ,  72 ,  51   a  and  52   a , form islands in an applied layer  7 .  
      There is nothing to prevent a thin wear layer  7 ′ (see  FIG. 8 ) from being applied on the surfaces  71 ,  72 ,  51   a  and  52   a , as well as the layer  7 , after the matrix has been removed from the support  60 .  
      This thin wear layer  7 ′ shall display an outer first wear surface  7   a . (By “wear surface”  7   a  is here meant a surface against which the hot liquid plastic material shall be pressed and against which wear surface the plastic component  3  shall be moulded before being fed out of the mould halves  1   c ,  1   d .)  
      This wear layer  7 ′, which forms the first wear surface  7   a , shall be so thin say up to 2 μm, that it will display a negative outer microstructure  2   a  corresponding directly to the positive microstructure  5   a  of the master  5 .  
      Persons skilled in the art are well aware that methods and procedures used here result in different thicknesses for the layer  7  and  7 ′, and a thickness and a method must be selected that are suitable for the chosen application.  
      This first wear layer  7  and  7 ′ could consist of a plastic composite or other hard material. However, the following description is aimed at illustrating this thin first metal layer or wear layer  7 ,  7 ′ as a metal layer  7 ′.  
      This metal layer  7 ,  7 ′ can be applied using known technology, such as sputtering or vaporisation.  
      In accordance with the invention the uppermost surface  7   b  of said thin metal layer  7  in  FIG. 6  will display microstructured parts  51 ,  52  corresponding substantially to the irregularities  7   b.    
      In accordance with the invention, said irregularities  7   b  shall be filled in a second step with a chosen plastic composite  8 ′. The plastic compound for this plastic composite  8 ′ shall be hot and thinly fluid so that it will be able to cover all the recesses  7   c  and so that the plastic composite can form a smooth upper surface  8   a.    
       FIG. 6  illustrates an embodiment in which a plastic composite  8 ′ is poured in in order to form a carrier  8  so that a small amount  8   a ′ will be situated above the plane  6  and an imagined flat surface  8   a , and the raised plastic material  8   a ′ can easily be removed by a mechanical plaining process.  
      The matrix  2 , in the form of a carrier  8  and a thin first wear surface  7   a , is applied in the movable mould half  1   c , with the surface  2   b  ( 6 ) in contact with the surface  1   c′.    
      The invention also assumes that pouring in the plastic-composite  8 ′ to form a carrier  8  can very well be performed under pressure in a mould cavity in such a way that machining of the rear side will not be necessary.  
      This third step in the manufacturing process is described in more detail with reference to  FIG. 11 .  
      Many opportunities for adaptation are offered by advocating the use of a plastic composite  8 ′ and a carrier  8  formed therefrom.  
      It is well known that various polymer materials and mixtures thereof mixed with different filler materials and mixtures thereof give different properties, and also that the curing process and curing time chosen affect the final properties of the plastic composite.  
      These known directives offer a number of different possibilities applied on a matrix in accordance with the invention.  
      It is thus possible to select a plastic composite  8 ′ from a polymer material mixed with a filler, such as a quartz or metal-filled epoxy or silicon polymer.  
      The present invention also proposes that the plastic composite  8 ′ and a carrier  8  formed therefrom may be chosen with a coefficient of linear expansion and/or a heat transfer-capability and/or a thermal capacitive capability suitable for a chosen process and/or nature of the machine used.  
      The plastic composite  8 ′ may be cured by the supply of heat and/or illumination by means of UV light. These curing possibilities can be used with advantage so that the required degree of curing and rigidity of the plastic composite can be adjusted.  
      There is nothing to prevent the plastic composite being selected from two-component types.  
       FIGS. 9 and 10  illustrate that a selected plastic composite  8 ′ for forming a carrier  8 , placed against the hard metal layer  7  serving as a first wear surface  7   a , is selected with a suitably low heat transfer capability and/or a suitably high thermal capacitive capability so that this plastic composite  8 ′ and carrier  8  will be able to serve as thermal insulation against the mould half  1   c  and thus keep the compression-moulded plastic compound material in the machine hot for the time required for producing the microstructured pattern  3   a  in the plastic component  3 .  
      In many cases, to ensure exact microstructure-related transfer, the heat and temperature of a compression-moulded plastic material must be retained in the plastic material without being passed over too quickly to the mould half  1   c.    
      Also in accordance with the invention said matrix  2 , as shown in  FIGS. 9 and 10 , is coated with or applied on a second wear layer  9  with a second wear surface  9   a . This layer  9  is coated on the surface  8   a  of the carrier  8  facing away from the metal layer  7 , and may consist of a durable layer and/or a heat-insulating layer.  
      The properties of this second wear layer  9  shall be to display a wear surface  9   a  with low friction against the surface  1   c ′ of the mould half  1   c , and high wear resistance, since the pressure between matrix  2  and mould half  1   c  is considerable during the moulding process and thermal stresses tend to displace the matrix  2  in relation to the mould half  1   c.    
      The second wear layer  9  may here advantageously consist of titanium nitride or DLC (Diamond-Like-Carbon).  
      For certain applications there is nothing to prevent a chosen material for the second wear layer  9  also constituting the material for the thin fist wear layer  7   a , with a carrier  8  made of plastic placed between them.  
      The thin metal layer  7  may be applied by means of a sputtering process and/or a vaporising process or, alternatively, a plating process.  
       FIG. 10  shows an alternative embodiment with a wear-resistant second wear layer  9 , a carrier  8  formed from a plastic composite  8 ′, and a thin first wear layer in the form of a metal layer  7 , where a recess  22  having been added to the dimension shown in  FIG. 4  and an adjacent recess  24  having been chosen considerably deeper than the recess  22  without, however, departing from the significant features of the invention.  
      Furthermore, a carrier  8  with carrier surface  8   b  for the thin first wear layer  7  and/or this layer  7  may consist of a plastic composite  8 ′ with a coefficient of linear expansion and/or a heat transfer capability and/or a thermal capacitive capability suitable for a chosen process and/or to the relevant embodiment of the injection-moulding machine used.  
      The carrier  8  may also consist of a plastic composite that can be assigned different degrees of curing ability by supplying different degrees of heat and/or illumination by means of UV light.  
      The carrier  8  may also consist of a material with low heat transfer capability and high thermal insulation and/or thermal capacitive capability.  
      There is nothing to prevent the carrier  8  being reinforced using means known per se. The carrier  8  can thus be reinforced with an additional wear-resistant layer  9  on its surface facing away from the metal surface  7 .  
      Although the invention is described in the above embodiment by way of example in that a thin wear layer  7  is supported by a thicker plastic layer or carrier  8 , it may be suitable in certain applications for these two wear layers to consist of the same plastic material.  
      There is nothing to prevent allowing the wear layer  7  to harden first, preferably at a high degree of curing, and the supporting plastic layer or carrier  8  later, at a lower degree of curing.  
       FIG. 11  shows the possibility of applying the plastic composite  8 ′ to a mould cavity  90  in the form of a mould  91 , by means of an overpressure from a ram  92  so that the surface  8   a  of the carrier  8  becomes flat, conforming with the surface section  91   a  of the mould  91 .  
      This flat surface  8   a  can now be applied directly against the support surface  1   c ′ of the mould half  1   c.    
      As regards the thickness of the layer  7 , a basic rule is that it shall be thick enough not to collapse or crack for a chosen number of casting cycles. In practice this means a thickness of 1-5 μm.  
      More generally, it is probably advisable for the thickness to be chosen between 1 and 50 μm, preferably less than 20 μm.  
      However, for certain applications layers as thin as about 0.1 μm can be accepted, depending partly on the choice of material in the carrier  8 .  
      The thickness of the wear layer  9  may be chosen between 1 and 50 μm, preferably less than 20 μm.  
      The microstructure  2   a  may vary in depth between 0.1 and 1000 μm, preferably over 100 μm.  
       FIG. 12  shows an alternative embodiment of the application of the invention.  
      A first matrix  121  with a fine microstructure  121   a  is manufactured in a first master (not shown), and a second matrix  122  with a coarse microstructure  122   a  is manufactured in a second master.  
      A surface section  121   b  is punched out of the matrix  121  and removed.  
      A corresponding surface section  122   b  is punched out of the matrix  122  and placed where the surface section  121   b  was previously.  
      A matrix  123  has thus been created, in which large surface areas have a fine microstructure, with an island of a coarse microstructure.  
      The method shown in  FIG. 12  involves the following process steps: 
      1. Manufacturing a first original with a fine microstructure, for instance, by means of lithography, with the aid of a laser, etching processes, precipitation, mechanical micromachining.     2. Manufacturing a second original with a coarse microstructure, for instance.     3. Manufacturing a matrix ( 121 ,  122 ) from the first and the second original.     4. Manufacturing a matrix original ( 123 ) containing parts of the first and the second matrices.    

      It is here suitable to reinforce the matrix original with a carrier or form a matrix from the matrix original.  
      The invention is naturally not limited to the embodiment described above by way of example, but may be modified within the scope of the inventive concept as defined in the appended claims.