Patent Publication Number: US-10315749-B1

Title: Material for propeller occlusion of marine vessels

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
     The present application claims benefit of U.S. provisional patent application Ser. No. 62/134,511, titled “Material For Propeller Occlusion Of Marine Vessels,” filed Mar. 17, 2015, which is incorporated by reference herein in its entirety. 
    
    
     STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH FOR DEVELOPMENT 
     Embodiments disclosed herein may have been conceived or first actually reduced to practice in performance of work under the following Government contract: Performance Work Statement (PWS) for Polymer Kelp for Vessel Stopping which is contained within contract W91CRB-11-D-0001 dated Mar. 21, 2014, issued by US Army RDECOM ACQ CTR-W911N F, 4300 S. Miami Blvd, Durham N.C. 27703. As a result, the Government may have certain rights to those embodiments. 
    
    
     FIELD OF THE EMBODIMENTS 
     The present embodiments relate generally to novel propulsor occlusion devices for stopping, slowing or disabling a seafaring vessel, ship, boat or the like, and methods of manufacturing and using these novel devices. Specifically, the present embodiments relate to propulsor occlusion devices comprising novel fabrics formed from biodegradable and/or dissolvable materials, and methods of manufacturing and using the same. 
     BACKGROUND OF THE EMBODIMENTS 
     There are a variety of circumstances in which it may become necessary for an official to compel a marine vessel (e.g., a ship, boat, jet ski, submarine or the like) to slow or to come to a complete stop. For example, an official may need to slow or stop a vessel during a law enforcement, drug interdiction, migrant interdiction or marine environmental protection mission. 
     The problem is that operators engaged in illegal activities tend to run when confronted by law enforcement. Officials are precluded from using lethal means to stop fleeing vessel unless they are fired upon. Accordingly, a dangerous chase often ensues as officials attempt to stop the fleeing vessel with non-lethal entanglement devices. 
     As shown in  FIG. 1 , conventional entanglement devices  102  are primarily in the form of nets or line materials launched ahead of a fleeing vessel with the hope that the vessel will travel over the extended line and pull it into the vessel&#39;s propeller  101 . These systems suffer from a number of drawbacks. First, the vessel operator typically sees the entanglement device being launched and so they may elude it by simply steering away from the device in the water. Second, such devices work by entangling the propeller and causing the drive train to stop. Accordingly, the operator may cause significant damage to an entangled motor by increasing the power to attempt to continue forward motion. Third, such devices must be removed from the water quickly after they are deployed. Nets and lines pose a danger to wildlife (e.g., birds, fish and the like) and other vessels when left in the water for an extended period of time. 
     Recently, an attempt has been made to produce entanglement devices that dissolve or degrade when left in the water for an extended period of time. Unfortunately, many of these devices either lack the strength necessary to slow or stop marine vessels, or are made from poorly degrading plastic polymers such as polypropylene, polyethylene terephthalate, and/or aliphatic polyamides that have the potential to leave residual plastic debris in the waters for periods well beyond their intended use and purpose. 
     There remains a need for improved devices, materials, and methods to facilitate stopping or slowing of a maritime vessel. It would be beneficial if such materials had reduced deleterious effects on vessels and their operators so such devices could be deployed earlier in an engagement, even before hostile intent is established. It would be further beneficial if such devices were made from biodegradable and/or dissolvable materials so that they did not require officials to retrieve them after deployment. Such systems would need to be able to stop or slow specific maritime targets in different environments, under varying conditions, and in multiple scenarios. 
     BRIEF SUMMARY OF THE EMBODIMENTS 
     In accordance with the foregoing objectives and others, it is an object of the present embodiments to provide a system that can slow and/or stop a seagoing vessel via occlusion of its propulsor. 
     Another object of the present embodiments is to provide a system that can be deployed from above, below, and/or on the surface of a body of fresh or salt water. 
     Yet another object of the present embodiments is to provide a propulsor occlusion device incorporating a number of fabrics or yarns made from a combination of dissolvable and/or biodegradable materials manufactured in such a way as to provide a lightweight, compact and low-regret method to stop or slow marine vessels by occlusion of any type of marine propulsor. 
     In one aspect of the embodiments an propulsor occlusion device is provided for use in slowing a marine vessel in a body of water. The device may include one or more strips of fabric having a basis weight of from about 75 to about 150 g/m 2  (GSM), for example about 100 GSM. The strips of fabric may be made of bonded fibers that include from about 65% to about 80% by weight polyvinyl alcohol and from about 20% to about 35% by weight polylactic acid. The propulsor occlusion device may be adapted to adhere to a propulsor of a marine vessel to reduce the propulsor&#39;s thrust generation and thereby slow the marine vessel. 
     In another aspect of the embodiments, a propulsor occlusion system for use in slowing a marine vessel in a body of water is provided. The system includes a vacuum-sealable, flexible housing adapted to hold a propulsor occlusion device therein. In one embodiment, a propulsor occlusion device may be housed in the housing, and air may be removed to reduce the volume of the system. The device may include a fabric made from a plurality of bonded bicomponent fibers having a sheath of from about 65% to about 80% by weight polyvinyl alcohol and a core of from about 20% to about 35% by weight polylactic acid. The propulsor occlusion device may be adapted to adhere to a propulsor of a marine vessel to reduce the propulsor&#39;s thrust generation and thereby slow the marine vessel. 
     In yet another aspect of the embodiments, a spunbond nonwoven fabric for use in slowing a marine vessel in a body of water is provided. The fabric may be made up of a plurality of bonded fibers having a sheath-core geometry, with a sheath of about 70% by weight polyvinyl alcohol and a core of about 30% by weight polylactic acid. The fabric may also include one or more superabsorbent materials. The fabric may have a basis weight of about 100 GSM and a denier per filament of about 3. This fabric may be adapted to adhere to a propulsor of a marine vessel. 
     These and other aspects of the embodiments may be more clearly understood by reference to the following detailed description and the appended claims. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The preferred embodiments are illustrated by way of example and not limited to the following figures. 
         FIG. 1  shows a conventional entanglement device  102  wrapped around a propeller  101 . 
         FIG. 2  shows exemplary entanglement materials  210  deployed below the surface of the water  201  in a forward path of a marine vessel  220 . 
         FIGS. 3A-3B  show an exemplary marine propulsor  300  in a first state ( FIG. 3A ) before coming into contact with propulsor occlusion materials  310  and in a second state ( FIG. 3B ) after engagement with the materials  310 . 
         FIGS. 4A-4E  show a number of exemplary propulsor occlusion device geometries. 
         FIGS. 5A-5N , show exemplary cross-sections of mono- and multicomponent fibers useful for creating a number of exemplary propulsor occlusion device fabrics. 
         FIG. 6  shows a schematic of an exemplary spunbond line  100  that may be employed to create any number of nonwoven propulsor occlusion device fabrics. 
         FIG. 7  shows an exemplary buoyancy bag  700  according to an embodiment. 
         FIG. 8  shows an exemplary packaging that may be employed to house the buoyancy bag  700  of  FIG. 7  prior to deployment. 
         FIG. 9  shows an exemplary weaving pattern  1000  that may be employed to weave mono or multi-component fibers into exemplary propulsor occlusion device fabrics. 
         FIG. 10  illustrates the dimensions and physical characteristics of an exemplary spunbond propulsor occlusion fabric section  1100 . 
         FIG. 11  illustrates the dimensions and physical characteristics of an exemplary spunbond propulsor occlusion fabric section  1200 . 
         FIG. 12  illustrates the dimensions and physical characteristics of an exemplary spunbond propulsor occlusion fabric section  1300 . 
         FIG. 13  illustrates the dimensions and physical characteristics of an exemplary doublewide spunbond propulsor occlusion fabric section  1400  comprising two sections according to  FIG. 13  sewn together. 
     
    
    
     DETAILED DESCRIPTION OF THE EMBODIMENTS 
     Various embodiments will be described with reference to details discussed below, and the accompanying drawings will illustrate the various embodiments. The following description and drawings are illustrative and are not to be construed as limiting the embodiments. Numerous specific details are described to provide a thorough understanding of various embodiments. However, in certain instances, well-known or conventional details are not described in order to provide a concise discussion of the embodiments. 
     As required, detailed embodiments are disclosed herein. However, it is to be understood that the disclosed embodiments are merely exemplary. The figures are not necessarily to scale, and some features may be exaggerated or minimized to show details of particular components. Therefore, specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a basis for the claims and as a representative basis for teaching one skilled in the art to variously employ the embodiments. While best mode is described, not all embodiments contain all features described herein. The individual features described herein relate to an exemplary composite of various embodiments. 
     All terms used herein are intended to have their ordinary meaning in the art unless otherwise provided. Where reference is made to the composition of the propulsor occlusion devices, the components are given in terms of “% by weight,” which refers to the weight percent of each component based on the weight of the entire composition. 
     Generally speaking, the present embodiments are directed to a new, non-lethal watercraft immobilizing devices and system, including novel fabrics that make up the systems, and methods of manufacturing the same. The propulsor occlusion devices comprise one or more fabrics made from fibers comprising biodegradable and/or dissolvable materials. 
     The disclosed propulsor occlusion devices can be deployed from a position above, below or on the surface of a body of water. Marine propulsors are designed to propel a watercraft by moving water in various ways, for example, through open or enclosed propellers, through jet engines and through cooling systems. It will be appreciated that the disclosed propulsor occlusion devices may move with this water to occlude a vessel&#39;s propulsor. 
     Embodiments of propulsor occlusion devices comprise a combination of hydrophilic, dissolvable and/or biodegradable materials manufactured in such a way as to provide a lightweight, compact and low-regret method to slow or stop marine platforms by occlusion of any type of marine propulsor. 
     The propulsor occlusion devices must meet a number of performance requirements that, taken together, impose significant constraints on the formulation not met by currently available materials. For example, propulsor occlusion materials must meet requirements relating to: water absorption rate, tensile strength, shape factors, thermal properties, strength in water, degradation in water, buoyancy in water, changes due to salinity and/or temperature variations, and/or biodegradability. 
     Referring to  FIG. 2 , a number of propulsor occlusion devices  210  are illustrated as being deployed in a body of water  201 . As shown, the propulsor occlusion materials  210  may be deployed near the surface of the water  201  in a forward path of a marine vessel  220 . One or more propulsor occlusion devices  210  may be deployed such that a single device or a combination of devices extend across the beam of the target vessel, ensuring intercept. 
     The propulsor occlusion devices  210  typically create a projected, but discontinuous barrier. Rather than creating a perimeter of the material, discrete lengths may be employed to target singular encounters. 
     Ideally, the materials are deployed such that the vessel  220  will travel directly over the material. Upon deployment, the total density of the wetted material should be at or just slightly below the density of water if it is to remain on or within close proximity of the surface. Moreover, the propulsor occlusion material may be diaphanous, such that it moves easily with the surrounding water. This may increase the likelihood that the material becomes entrapped by a vessel&#39;s propulsor. 
     Referring to  FIGS. 3A-3B , a propeller  300  having multiple airfoil-shaped blades  305  is illustrated in a first state ( FIG. 3A ) before it comes into contact with propulsor occlusion materials  310  and in a second state ( FIG. 3B ) after coming into contact with the materials ( FIG. 3B ). 
     The propeller  300  comprises a “diameter” D equal to the diameter of a circle located at the distal-most ends of the propeller blades  305 . Generally, the propeller transmits power by converting rotational motion into thrust. A pressure difference is produced between the forward and rear surfaces of each blade, and water is accelerated behind the blade. 
     As shown, the propulsor occlusion materials  310  may be drawn into the propeller blades  305  and may become fastened, adhered or stuck thereto. The added mass and irregular volume of the materials interfere with propeller&#39;s capability to generate thrust. The stopping power of the propulsor occlusion materials thus cannot be overcome by increasing power. Importantly, the propulsor occlusion materials do not prevent the propeller from rotating like conventional entanglement device, so increasing power may not result in damage to an engine or drivetrain. 
     The inventive propulsor occlusion devices may be employed to occlude any type of inboard or outboard marine propeller systems, including but not limited to twin, contra-rotating, controllable-pitch, and nozzle-style propellers. Moreover, the propulsor occlusion devices may be employed to stop and/or slow vessels having twin, triple or quadruple blade propellers. 
     In certain embodiments, the propulsor occlusion device may be capable of stopping a vessel having any number of propellers, each of up to about 10 inches, about 15 inches, about 20 inches, about 30 inches, about 35 inches, about 40 inches, about 45 inches or about 50 inches in diameter. The propulsor occlusion materials are capable of occluding propellers having any blade contour and pitch. 
     Although a propeller is depicted, it will be appreciated that the propulsor occlusion materials be an effective non-lethal means of stopping and/or slowing a vessel having any type and/or number of propulsors, such as but not limited to propellers and/or jet drives. The material is effective at stopping and/or slowing vessels having displacement hulls or those having planing hulls. 
     In order to maintain the occlusion mechanism, the propulsor occlusion materials should comprise a tensile strength that is strong enough to hold together under the forces generated at the lifting surfaces of a vessel&#39;s propulsor(s). In certain embodiments, the propulsor occlusion device may be designed such that it will break if put under strong tensile forces to assure is does not stop a vessel&#39;s drive train. The tensile strength of the material may be engineered for specific engagements. 
     Tensile strength of the propulsor occlusion materials may be measured according to ASTM Standard D2256, Standard Test Method for Tensile Properties of Yarns by the Single-Strand Method; and/or ASTM Standard D2731 Standard Test Method for Elastic Properties of Elastomeric Yarns (CRE Type Tensile Testing Machines). 
     Characterization of the tensile strength of the material in water is different from dry tensile strength. Although tensile strength data can be obtained quantitatively in the dry state, measurement in the wet state is more difficult. There is no standard method for measuring tensile strength in water. However semi-quantitative measurements may be correlated with effectiveness in occlusion. 
     Referring to  FIGS. 4A-4E , a number of exemplary propulsor occlusion device geometries are illustrated. As shown, the propulsor occlusion devices comprise one or more strips, sections or pieces of a propulsor occlusion fabric material  410 . A single fabric section may be employed, or a number of sections may be fastened together to form a shape for the device. It will be appreciated that the illustrated shapes are exemplary and any geometry may be employed as long as the resulting device meets the requirements described herein. 
     Referring to  FIG. 4A , an exemplary engagement device  401  is illustrated having a number of material strips  410  fastened together at or near a single end of each strip, via a fastening means  420 . Any number of material strips may be employed in the illustrated configuration. 
     The fastening means  420  may comprise one or more of: rope, yarn, thread, ties, crimps, staples, chemical adhesives, thermal bonding techniques and the like. In one preferred embodiment, the strip ends may be sewn together using biodegradable and/or dissolvable materials having any desired or required strength. 
     Referring to  FIG. 4B , the exemplary engagement device  401  of  FIG. 4A  is shown, wherein the strips  410  are braided, twisted or otherwise combined to reduce the volume of the device before it is deployed. 
     Although the strips  410  are shown as being braided together, it will be appreciated that the shape of the device  401  may change substantially when submerged in water. Typically, the strips  410  absorb water quickly upon deployment, and the non-fastened ends will expand and separate from each other. The fastening means may remain attached to one end of the strips for a period of time before the materials dissolve and/or biodegrade. 
     Referring to  FIG. 4C , an exemplary engagement device is illustrated comprising a number of material sections  410  fastened together along a side thereof, via a fastening means  420 . The material strips are combined to form a “double-wide” configuration. It will be appreciated that any number of strips may be fastened together to increase the width (and/or length) of the engagement device. 
     Referring to  FIG. 4D , an exemplary propulsor occlusion device is shown wherein a number of material piece  410  are attached via a fastening means  420  at both a top end and bottom end thereof to form a spherical shape. Although four fabric strips are depicted, it will be appreciated that any number of strips may be employed to increase or decrease the overall density of the device. 
     Referring to  FIG. 4E , an exemplary propulsor occlusion device is shown wherein a number of material strips  410  are attached to form of a net-like structure. Any number of fabric pieces may be combined into such a shape, depending on the desired length and/or width of the net. Again, the multiple strips of material  410  may be fastened together via one or more of the above-described fastening means  420 . 
     Although not shown, multiple propulsor occlusion devices may be attached via an attachment means to create a grouping of propulsor occlusion devices. Any attachment means may be employed, including but not limited to, rope, yarn, thread, ties or the like. Preferably, the attachment means is dissolvable and/or biodegradable. The attachment means may be physically connected to a fabric strip of each device, or may be attached to a fastening means present on each propulsor occlusion device. A grouping of propulsor occlusion devices may be preferred in certain situations, such as when it is desired to cover a large area, a strong current is present, or when multiple vessels are targeted. 
     The propulsor occlusion device geometry may be selected such that the device may move with the surrounding water. Accordingly, the geometry of the propulsor occlusion device may allow for it to be pliable and/or drapable. The drapability of the device (i.e., a radius of curvature of the drape) may be specifically engineered based on the characteristics of the propulsor desired to be occluded. For example, large propellers may not require the drapability that smaller ones do. 
     It will be appreciated that the propulsor occlusion materials may simply be employed as a single strip of material. A number of exemplary single-strip devices are shown in  FIGS. 10-13  and are discussed in detail below. Moreover, a fastening means may not be employed, as the material strips may simply be tied together to allow for separation after deployment. 
     Selection of appropriate dimensions for the fabric strips or panels is important, as it affects the probability of prop occlusion and a number of environmental factors, such as degradation of material (discussed below). Generally, a larger volume of material increases the probability of the material being entrapped by a propulsor. But, it is advantageous to keep the volume of material to a minimum so that it can be more easily stored, transported, handled and/or deployed. Chemical composition and physical attributes of exemplary fabric strips are discussed in detail below and numerous examples are provided (see, Examples 2-5, Tables 1-8 and  FIGS. 10-13 ). 
     It will also be appreciated that the device configurations of  FIGS. 4A-4E  represent exemplary dry-state geometries, before the device is deployed. It is desirable for the propulsor occlusion materials to quickly expand upon coming into contact with water, and the device geometry will therefore change significantly over time. 
     In certain embodiments, the propulsor occlusion material must rapidly absorb water to become effective at disabling a vessel within a short time, such as about 10 seconds, about 30 seconds, about 1 minute, about 5 minutes, about 10 minutes, about 15 minutes, about 30 minutes, about 45 minutes, about 1 hour, about 1.5 hours or about 2 hours. 
     ASTM Active Standard ASTM D570 covers the determination of the relative rate of absorption of water by plastics when immersed. However propulsor occlusion materials cannot be classified strictly as a plastic and because of the unique water-related properties of the materials, ASTM D570 may not be applicable. Accordingly, water absorption rate may be determined by immersing a weighed sample of the material in water for a predetermined time. The sample may then be withdrawn from the water and allowed to drain until no discernable drainage continues. The sample may then be weighed again. This procedure may be repeated until no further change occurs or the sample begins to lose mass. 
     Composition of the Propulsor Occlusion Devices 
     As discussed above, the novel propulsor occlusion devices typically comprise one or more strips, pieces or sections of fabric. Each strip may comprise one or more types of fabric and optional additional materials. The fabrics, in turn, are made from any number of fibers, which comprise one or more constituents. As discussed in detail below, exemplary materials may be produced via woven or nonwoven processes, and a number of exemplary materials are disclosed in Examples 1-10 and Tables 1-3 and 5-8. 
     Unlike typical entanglement devices, the propulsor occlusion fabrics of the embodiments may comprise benign materials that are recognized as generally safe for use (“GRAS”), as defined in 21 C.F.R. 170.30(b), incorporated by reference herein in its entirety. Such materials are non-toxic to humans, invertebrate, fish, and/or phyto plankton. Moreover, the disclosed propulsor occlusion materials may meet all requirements of each of the enumerated laws and regulations in Table 9, below. 
     Each of the propulsor occlusion components may be dissolvable and/or biodegradable such that they do not cause a significant short-term or long-term impact to the environment. The propulsor occlusion components interact chemically and physically with the water environment into which they are introduced: initially swelling with contact and over a short period of time dispersing. 
     In one embodiment, the materials may degrade or dissolve by biotic and chemical mechanisms in a matter of hours or days to non-toxic mineralized products. The composition of seawater is not significantly altered from the small mass of added minerals that might occur during the use of the propulsor occlusion devices. Moreover, the buoyant residual materials may be contained in the upper water column (i.e., the infra-littoral zone), where they will not affect reef and benthic environments. 
     Discharges occurring in the use of propulsor occlusion devices are small in mass and extent. The product may be deployed as a solid polymer of high molecular weight that is significantly insoluble. The amount of propulsor occlusion materials discharged to address discrete engagements is expected to be small and in widely dispersed locations. 
     In one embodiment, the propulsor occlusion materials may dissolve and/or biodegrade such that will not be a hazard to navigation after about 12 hours. In certain embodiments, the propulsor occlusion material may degrade and/or dissipate into pieces of less than 2 inches in length within about 6 hours, about 12 hours, about 24 hours, about 36 hours, about 48 hours, about 60 hours or within about 72 hours. 
     The exemplary propulsor occlusion fabrics may maintain a tensile strength capable of stopping and/or slowing a vessel for about 1 hour, about 2 hours, about 5 hours, about 10 hours, about 12 hours, about 24 hours, about 36 hours, or about 48 hours. Once the propulsor occlusion materials dissipate, dissolve and/or degrade to the point that a device is no longer capable of stopping and/or slowing a vessel, the materials will no longer remain a hazard to vessels and/or wildlife. 
     The diameter of the fibers used to make the fabrics of the engagement device may affect the time it takes for the material to dissipate. The dissolution, or dissipation, rate is dependent on the surface area of the fibers. The surface to volume ratio (S/V) scales as 1/(ΔL) where ΔL is the change in the length scale. Accordingly, as the fibers become thicker, the time it takes the propulsor occlusion device to dissolve will become longer. Such fibers are discussed in detail below. 
     The above described method of calculating water absorption may also be used to determine the rate of dissolution of the materials. The mass of a propulsor occlusion material sample may be recorded as a function of time and the dissolution rate may be determined by observation of the mass change with time. The sample is then dried after the measurement is complete and the total change in dry mass is determined. 
     The dissolution rate may be difficult to measure—measuring the weight loss of the material by removing it from the water is complicated by absorption of water into the material. An alternative approach to determining the dissolution rate comprises looking at the actual dissolved material in the water using either a spectrophotometric technique or nuclear magnetic resonance. 
     As used herein, material degradation includes a combination of dissolution, dissipation and biodegradation. A number of standard testing procedures may be employed to determine degradation, including but not limited to: ASTM Standard D6691, Standard Test Method for Determining Aerobic Biodegradation of Plastic Materials in the Marine Environment by a Defined Microbial Consortium or Natural Sea Water Inoculum; ASTM Standard D5511, Standard Test Method for Determining Anaerobic Biodegradation of Plastic Materials under High Solids Anaerobic Digestion Conditions; ASTM Standard D7473, Standard Test Method for Weight Attrition of Plastic Materials in the Marine Environment; and ASTM Standard 5988, Standard Test Method for Determining Aerobic Biodegradation of Plastic Materials in Soil. It will be appreciated that the degradation/dissolution rate may be effected by a number of factors, including but not limited to chemical makeup, physical form, water temperature, water salinity and agitation. 
     The principle components of the inventive propulsor occlusion fibers and fabrics are polyvinyl alcohol (PVA) polymer, polylactic acid (PLA) polymer and/or superabsorbent materials (SAMs), including superabsorbent polymers (SAPs) and superabsorbent fibers (SAFs). The inventive fabrics may be made from fibers comprising one or more of these components according to the processes described below. Such fabrics and/or fibers may also comprise one or more of the following additional, optional ingredients: sodium alginate; multivalent cation and/or anion salts; mineral wool or mineral fibers; thickening agents; fillers; plasticizers; antioxidants; and/or pigments. The precise construct and combination of these constituent materials confer novel and surprising properties when wet. 
     Typically, the fabrics may comprise from about 10% by weight PVA to about 100% by weight PVA. More typically, the fibers may comprise from about 20% to about 80% by weight PVA. 
     In certain embodiments, the fabrics may comprise a single PVA constituent. In alternative embodiments, multiple PVA constituents with different properties may be included, each present in any amount. For example, fabrics may comprise 25% by weight of a first PVA and 75% by weight of a second PVA. As another example, fabrics may comprise 50% by weight of a first PVA and 50% by weight of a second PVA. 
     It will be appreciated that exemplary fabrics may not comprise any amount of PVA. On the other hand, fibers may comprise about 100% by weight PVA. 
     PVA is a hydrophilic synthetic polymer having the following idealized chemical formula: 
     
       
         
         
             
             
         
       
     
     Generally, PVA has excellent film forming, emulsifying and adhesive properties. When dry, PVA has high tensile strength and flexibility, as well as high oxygen barrier properties. Water acts as a plasticizer upon PVA, and the material loses tensile strength, but gains elongation and tear strength when wetted. 
     PVA is produced commercially from polyvinyl acetate, usually by a continuous process, such as hydrolysis, alcoholysis or saponification. The acetate groups are hydrolyzed by ester interchange with methanol in the presence of anhydrous sodium methylate or aqueous sodium hydroxide. Following gradual addition of the aqueous saponification agent, PVA is precipitated, washed and dried. The degree of hydrolysis is determined by the time the saponification reaction is stopped. 
     The physical characteristics and specific functional uses of particular PVA polymers depend on the degree of polymerization, the degree of hydrolysis and the molecular weight. PVA is classified into two classes: partially hydrolyzed and fully hydrolyzed. 
     In the broadest aspect of the embodiments, there is essentially no restriction on the nature of the PVA employed. What is considered important is that the PVA comprises as high a tensile strength as possible, while still biodegrading and/or dissolving in water within a reasonable period of time, and that it is capable of adhering to metal propellers when wet. 
     PVA polymers that are typically employed may comprise a viscosity of from about 3 to about 35 mPa s; a degree of hydrolysis between about 92 and about 99 mol. %; a pH of from about 4.0 to about 7.0; and/or a melt point of from about 150 to about 210 degrees C. In certain embodiments, PVA polymers may be employed having one or more crosslinking agents. 
     PVA polymers engineered to have low crystallinity with high hydrogen bond strength are preferred. Such materials may have relatively low melting points, high stretching characteristics and high gas barrier performance, as well as low foaming, aqueous solution stability and emulsification performance. 
     A number of PVA polymer products have been found to be useful in producing propulsor occlusion fabrics, including but not limited to: NICHIGO G-POLYMER OKS-8041P, produced by Nippon Synthetic Chemical industry Co., Ltd. (“Nippon”); NICHIGO G-POLYMER™ OK-8070P PVA, produced by Nippon; EXCEVAL™ (CP4104) PVA, produced by Kuraray Europe GmbH (“Kuraray”); NICHIGO G-POLYMER™ OK-8071 PVA, produced by Nippon; NICHIGO G-POLYMER™ OK-8112 PVA, produced by Nippon; NICHIGO G-POLYMER™ OK-8042 PVA, produced by Nippon; and MOWIFLEX™ PVA, produced by Kuraray. 
     The second principal component of the inventive propulsor occlusion composition is polylactic acid (PLA). Typically, the fabrics may comprise from about 10% by weight PLA to about 100% by weight PLA. More typically, the fabrics may comprise from about 20% to about 80% by weight PLA. 
     In certain embodiments, the fabrics may comprise a single PLA constituent. In alternative embodiments, multiple PLA constituents with different properties may be included, each present in any amount. For example, fabrics (and/or fibers) may comprise 25% by weight of a first PLA material and 75% by weight of a second PLA material. As another example, fabrics may comprise 50% by weight of a first PLA material and 50% by weight of a second PLA material. 
     It will be appreciated that, in some embodiments, the fabrics may not comprise any amount of PLA. In alternative embodiments, fabrics may comprise about 100% by weight PLA. 
     Polylactic acid is a biodegradable, high-strength, low-solubility polymer having the following chemical formula: 
     
       
         
         
             
             
         
       
     
     PLA exists as a polymeric helix, with an orthorhombic unit cell. The tensile properties of PLA can vary widely, depending on whether or not it is annealed or oriented or what its degree of crystallinity is. PLA&#39;s stereo-chemical makeup is easily controlled by polymerization with D-lactide, D,L-lactide, or meso-lactide, to form random or block stereo-copolymers, while the molecular weight is directly controlled by the addition of hydroxylic compounds (i.e., lactic acid, water, alcohols). 
     The ability to control the sterochemical architecture allows precise control over the speed and degree of crystallinity, the mechanical properties, and the processing temperatures of the material. For example, although highly crystalline PLA may have a very high tensile strength, it may take months or years to hydrolyze fully to lactic acid, whereas an amorphous sample may be degraded quickly. 
     In the broadest aspect of the embodiments, there is essentially no restriction on the nature of the PLA employed. What is considered important is: the PLA comprises as high a tensile strength as possible while still being biodegradable within a reasonable period of time; the PLA is capable of adhering to metallic propellers; and the PLA can be processed into the desired or required fabrics and fibers. 
     Typical PLA polymers may comprise a specific gravity of from about 1 to about 2 (e.g., about 1.25); a relative viscosity of from about 2.5 to about 4.5; a melt index of about 15 to about 3 at 210 C; a melt density of from about 1 to about 2 at 230 C; a glass transition temperature of from about 50 to about 65 C; and a crystalline melt temperature of from about 150 to about 175 C. 
     A number of PLA polymer products have been found to be useful in producing propulsor occlusion fabrics, including but not limited to INGEO™ 6400D and 6202D, both produced by Nature Works LLC. 
     In preferred embodiments, the propulsor occlusion fabrics may comprise both PVA and PLA. The fabrics typically comprise a PVA to PLA weight ratio varying from about 9:1 to about 1:9. Exemplary fabrics (and/or fibers) may comprise 90% by weight PVA and 10% by weight PLA; 80% by weight PVA and 20% by weight PLA; 75% by weight PVA and 25% by weight PLA; 70% by weight PVA and 30% by weight PLA; 50% by weight PVA and 50% by weight PLA; 30% by weight PVA and 70% by weight PLA; 25% by weight PVA and 75% by weight PLA; 20% by weight PVA and 80% by weight PLA; or 10% by weight PVA and 90% by weight PLA. 
     The PVA/PLA fibers may comprise from about 20% to about 35% by weight PVA and from about 65% to about 80% by weight PLA. For example, the PVA/PLA bicomponent fibers discussed in Example 5 comprise 70% by weight PVA and a 30% by weight PLA. These fibers may comprise a core/sheath geometry, with a PLA core and PVA sheath. A number of exemplary PVA/PLA fibers and method for producing the same are disclosed in Examples 1-6 and in Tables 1-9, below. 
     Preferred for use in the propulsor occlusion compositions of the embodiments are super absorbent polymers. SAPs are water-absorbing polymers that absorb aqueous solutions through hydrogen bonding with water molecules. The chemical compound of SAPs may be shown as: 
     
       
         
         
             
             
         
       
     
     There are many methods to prepare SAPs with various starting materials, such as copolymerizing hydrophilic monomer with a cross-linking agent, grafting monomer with starch, cellulose, synthetic fiber, and polysaccharide, cross-linking linear hydrophilic polymer with polyvalent metal ions or organic multifunctional group materials etc. SAPs can be in the form of small particles, powder, fiber, membrane, microbeads and even liquid. 
     A SAP&#39;s ability to absorb water is a factor of the ionic concentration of the aqueous solution. In deionized and distilled water, a SAP may absorb 300 times its weight (from 30 to 60 times its own volume) and can become up to 99.9% liquid, but when put into a 0.9% saline solution, the absorbency drops to about 50 times its weight. The presence of valence cations in the solution impedes the polymer&#39;s ability to bond with the water molecule. 
     The total absorbency and swelling capacity are controlled by the type and degree of cross-linkers used to make the gel. Low-density, cross-linked SAPs generally have a higher absorbent capacity and swell to a larger degree. These types of SAPs also have a softer and stickier gel formation. High cross-link density polymers exhibit lower absorbent capacity and swell, but the gel strength is firmer and can maintain particle shape even under modest pressure. 
     SAPs are now commonly made from the polymerization of acrylic acid blended with sodium hydroxide in the presence of an initiator to form a poly-acrylic acid sodium salt (“sodium polyacrylate”). Sodium polyacrylate is an anionic polyelectrolyte with negatively charged carboxylic groups in the main chain. 
     While sodium neutralized polyacrylic acids are the most common form used in industry, there are also other salts available including potassium, lithium and ammonium. SAPs made from other materials may be employed such as those made from one or more of: polyacrylamide copolymer, ethylene maleic anhydride copolymer, cross-linked carboxymethylcellulose, polyvinyl alcohol copolymers, cross-linked polyethylene oxide, and starch grafted copolymer of polyacrylonitrile to name a few. 
     Incorporation SAPs into the propulsor occlusion device fabrics may allow for quicker water absorption upon deployment and added volume of the material. Although SAPs generally become weak when saturated with water, their expansion provides a driving force for causing the propulsor occlusion material to “bloom.” Accordingly, the effectiveness of the materials may be increased by incorporated SAPs. 
     The propulsor occlusion fabrics may comprise one or more of the above-described SAPs. For example, granules of SAPs may be adhered to the inventive fibers via any mechanical, thermal or chemical means, or may be extruded with the PVA and/or PLA materials. In certain embodiments, SAP fibers may be created and incorporated into woven and/or nonwoven fabrics via sewing or bonding (i.e., thermal, chemical, mechanical, etc). 
     In the broadest aspect of the embodiments, there is essentially no restriction on the nature of the SAPs. What is considered important is that a SAP comprises high water absorption, while having as high a tensile strength as possible and while still being biodegradable and/or dissolvable within an acceptable period of time. 
     In one embodiment, the propulsor occlusion fabrics may comprise an amount of an alginate material, such as sodium alginate, as a stabilizer, thickener, gelling agent, and/or emulsifier. Sodium alginate is a natural polysaccharide from brown seaweed and its empirical formula is (C 6 H 7 NaO 6 ) n . This material is a natural product, and is biodegradable. 
     Sodium alginate dissolves slowly in water, forming a viscous solution. Regions of guluronate monomers (“G-blocks”), in one alginate molecule can be linked to similar region in another alginate molecule by means of calcium ions or other multivalent cations. The divalent calcium cation fits into the G-block structure, binding the alginate polymers together by forming junction zones, resulting in gelation of the solution. 
     Another valuable property of alginates is that they are soluble in cold water and do not need a heating and cooling cycle to form gels (in the presence of calcium). By selecting an appropriate grade and/or formulation, alginates can be customized so that their gel-forming characteristics facilitate matrix and structural building properties. Moreover, in presence of calcium, the material forms a gel without the need of heat. 
     An alginate&#39;s type, counter-ion, calcium source and the sequestering agent control the gelling system structure and the rate at which gel forms. Hydration and uniform distribution of the alginate are also important to optimize gel formation. 
     In one embodiment, the propulsor occlusion composition may comprise one or more multivalent cation and/or anion salts, such as but not limited to: sodium borate (“borax”), copper sulfate, sodium sulfate, calcium oxide, aluminum oxide, sodium bicarbonate, alginic acid, citric acid aluminum acetate and the like. Such materials may be employed to increase positive buoyancy through gas production, as well as increase strength, duration, and/or ability of the propulsor occlusion device to adhere to a metallic prop. These materials may crosslink PVA to form a sticky gel having strong adhesion properties. 
     In certain embodiments, such additives may be included in an amount of from about 0.1% to about 0.6% by weight, from about 0.2% to about 0.5% by weight, or from about 0.3% to about 0.4% by weight. In one particular embodiment, about 0.3% by weight borax may be included. 
     The fabrics may also comprise an amount of citric acid and sodium bicarbonate. The combination of citric acid and sodium bicarbonate may be employed to create CO 2  for buoyancy. This combination may be included in the same fibers, or may be added to different fibers that are combined to form a fabric. Creating two fibers of different polymers side-by-side offers the possibility of creating CO 2  over a period of time (e.g., about 10 to about 20 minutes) directly from the fiber when exposed to water. This may eliminate or reduce the need for the buoyancy bags, discussed in detail below. Various concentrations of these additives may be combined with PVA, PLA and/or SAP solutions and extruded into fibers using, the below described methods (e.g., using a dry spinning extruder). 
     In another embodiment, the fabrics may include an amount of beeswax. The combination of borax and beeswax may be employed to create an emulsion. 
     In one embodiment, the fabrics may comprise one or more plasticizers. Exemplary plasticizers include, but are not limited to acetylated monoglyceride, alkyl citrates and/or epoxidized soybean oil (ESBO). 
     In another embodiment, the fabrics may comprise one or more antioxidants. Such antioxidants may prevent oxidative degradation of the propulsor occlusion products during storage that would otherwise cause a loss of strength. Exemplary antioxidants include, but are not limited to, natural antioxidants such as ascorbic acid and tocopherols; and synthetic antioxidants such as propylgallate, tertiary butylhydroquinone, butylated hydroxyanisole and butylated hydroxytoluene. 
     In yet another embodiment, the fabrics may comprise an amount of mineral wool or mineral fibers. Such materials are formed by spinning or drawing molten minerals such as basalt. Mineral fibers may be engineered to hold large amounts of water, and so may be employed to increase water absorption of the fabric. 
     Optionally, other ingredients may be incorporated into a spinnable composition from which a fabric is made. Such optional materials may be used to modify the processability and/or performance characteristics, such as opacity, elasticity, tensile strength, wet strength, and modulus of the final product. Other benefits include, but are not limited to, stability, including oxidative stability, brightness, color, flexibility, resiliency, workability, processing aids, viscosity modifiers, and odor control. Examples of optional materials include, but are not limited to, filler(s) such as quartz, calcite, clay, talc, barite, and/or NA-AL-silicate, and the like; pigments like titanium dioxide, lithopone and other inorganic pigments; dispersants such as polyphosphates, polyacrylates, phosphonates, napthene and lignin sulfonates, to name a few; wetting agents, including anionic, cationic, amphoteric and/or non-ionic surfactants; defoamers such as, for example, silicon emulsions, hydrocarbons and long-chain alcohols; stabilizers, including for example mostly cationic compounds; coalescing agents including, without limitation, alkali-stable esters, glycols, and hydrocarbons; rheological additives like cellulose derivatives (e.g., carboxymethylcellulose and/or hydroxyethylcellulose), xanthan gum, polyurethane, polyacrylate, modified starch, bentone and other lamellar silicates; water repellents such as alkyl siliconates, siloxanes, wax emulsions, fatty acid Li salts; and conventional fungicide or biocide. 
     Manufacturing Fibers &amp; Fabrics 
     Referring to  FIGS. 5A-5N , cross-sections of a number of acceptable fiber geometries are illustrated. The mono and multiconstituent fibers of the present embodiments comprise the above-described materials and may be in many different configurations. 
     Exemplary extruded fibers can have virtually any transverse cross-sectional shape, including, but not limited to: x-shaped ( FIG. 5I ), elongated x-shaped ( FIG. 5G ), cross shaped ( FIG. 5K ), Y-shaped ( FIG. 5H ), star shaped ( FIG. 5J ), round, elliptical, ribbon shaped, dog bone shaped, and other multilobal cross-sectional shapes. Multilobal fibers worth mentioning include, but are not limited to solid or hollow: octolobal ( FIG. 5L ), starfish ( FIG. 5M ), caterpillar ( FIG. 5N ), trilobal, delta shaped, square, star or elliptical fibers. 
     The mono or multiconstituent fibers may also be multicomponent in configuration. A “component,” may be defined as a separate part of a particular fiber that has a spatial relationship to another part of the fiber. The main objective of producing multicomponent fibers is to exploit capabilities not existing in any single component alone. 
     Multicomponent fibers according to an embodiments, may be in any cross sectional shape or geometry, such as but not limited to, a side-by-side ( FIG. 5E ), sheath-core ( FIG. 5F ), sheath-sheath-core, segmented pie ( FIG. 5D ), hollow pie wedge ( FIG. 5C ), three island ( FIG. 5A ) or island-in-the-sea ( FIG. 5B ) configurations. Alternatively, the multicomponent fibers may be mixed homo or single component fibers. The sheath of any fiber may be non-continuous or continuous around the core. If present, a hollow region in the fiber may be singular in number or multiple. The hollow region may be produced by a spinneret design or possibly by dissolving out a water-soluble component such as PVA. 
     Generally, the fabrics of the embodiments may be produced by combining the above-described fibers and any optional additional components into fabrics via any number of woven or nonwoven processes. Nonwoven fabrics are broadly defined as sheet or web structures bonded together by entangling or interlocking fiber or filaments mechanically, thermally or chemically. They are flat or tufted porous sheets that are made directly from separate fibers, molten plastic or plastic film. They are not made by weaving or knitting and do not require converting the fibers to yarn. However, woven fabrics may be combined with non-woven fabrics via one of the below described bonding processes. 
     An exemplary nonwoven process begins with converting the PVA, PLA and/or SAM polymer(s) being spun into a fluid state. If the polymer is a thermoplastic then it can be simply melted, otherwise it is dissolved in a solvent or chemically treated to form soluble or thermoplastic derivatives. Any of the optional additives discussed above may be spun with the polymer(s) or may be added after spinning. 
     The molten polymer(s) is then forced through a spinneret to form a desired fiber shape and the resulting web is allowed to cool to a rubbery state and then a solidified state. If a polymer solution is used, then the solvent is removed after being forced through the spinneret. 
     Generally, any spinning process may be employed to create the initial web. For example, wet, dry, dry jet-wet, melt (extrusion, direct, etc.), gel and/or electrospinning spinning techniques may be employed. 
     In one embodiment, dry spinning may be employed. The polymers are dissolved in a solvent, and solidification may be achieved through evaporation of the solvent. Evaporation may be achieved via a stream of air or inert gas. Because there is no precipitating liquid involved, the fiber does not need to be dried, and the solvent is more easily recovered. 
     In another embodiment, melt spinning is employed for forming the mixed filament products described herein. For example, bicomponent spinning involves the extrusion of two different types of the same polymer or two different polymers through a spinneret, respectively. 
     A number of spinning techniques for multicomponent and/or multiconstituent spinning of PVA, PLA and/or SAP materials may be employed to produce the fibers. The following discussion is framed in terms of bicomponent spinning, however it relates to any number of components and/or constituents. 
     One method of manufacturing bicomponent fibers is the side-by-side extrusion of two polymers through one spinneret hole. As the two polymers cool and solidify they adhere together as one filament. The filament is composed of both the fibers. 
     Another means of manufacture of bicomponent fiber is that of using one spinneret inside another. A first polymer is pumped through a center or core spinneret while a second is pumped though an outer or surrounding spinneret. Both polymers emerge as one through the common hole of the surrounding spinneret so that the fiber is formed of a core of one polymer surrounded by a sheath or ring of another. 
     The third method of producing bicomponent fiber is the distribution of drops of a first molten polymer into a second molten polymer. This composite mixture is then extruded through a single spinneret hole. The result is a matrix or conglomerate, of minute short strands of one fiber suspended inside another. 
     Whatever spinning process is applied, the fibers are then attenuated and collected (i.e., drawn) to increase strength and orientation. This may be done while the polymer is still in the process of solidifying or after it has completely cooled down. Drawing pulls the molecular chains together and orients them along the fiber axis, resulting in a stronger web. 
     The web fibers are then combined or bonded together using at least one of heat, pressure, a chemical binder, mechanical entanglement, hydraulic entanglement, and combinations thereof resulting in the formation of a nonwoven fibrous fabric. 
     Thermal bonding may include the use of a heat sealer, a large oven for curing, and/or calendaring through heated rollers. In one preferred process, the nonwoven fabrics may be prepared using a spunbond method that employs calendaring through heated rollers (“calendars”). The calendars can be smooth faced for an overall bond or patterned for a softer, more tear resistant bond. 
     In one embodiment, chemical bonding, or a wetlaid processes, may be employed. Such process includes the use of binders to chemically join the fibers. In one embodiment, binder fibers or powders may be melted to hold non-melting fibers together. In another example, sodium hydroxide or the like may be employed to shrink bond the fibers. 
     In another embodiment, a melt-blown process may be employed where fiber is bonded as air attenuated fibers intertangle with themselves during simultaneous fiber and web formation. In one example, a spunbond process may be combined with a melt-blown binding process to produce a spun-melt-spun layered product. 
     In another embodiment, mechanical bonding, such as needle-punching, may be employed. Generally, mechanical bonding comprises penetrating the web with an array of barbed needles that carry tufts of the web&#39;s own fibers into a vertical direction through the web. A controlled ratio of low melt fiber may be incorporated into a base nonwoven fabric by heating the material enough to soften it to the point that it binds to the main fibers where those fibers intersect, thereby locking the fibers together. 
     The propulsor occlusion materials formed in accordance with the present embodiments may comprise a single layer of bonded fabric, but typically comprise a number of layers. As used herein, a “layer” is part of a fibrous fabric that is produced in a separate fiber laydown or forming step and will typically have the same combination of fibers and any additive materials intimately mixed throughout the layer. It will be appreciated that a single layer may have a combination of different fiber shapes, diameters, configurations, and compositions. 
     The layers may be consolidated by thermal point-bonding or any other of the above described bonding techniques to attain strength, integrity and certain aesthetic characteristics. The single layer of shaped fibers of the present embodiments may be utilized by itself as a propulsor occlusion fabric, or the layer may be combined with other nonwoven layers or a film layer to produce a laminate. As used herein, a “laminate” is defined as a two or more layers contacting along at least a portion of their respective planar faces with or without interfacial mixing. 
     Exemplary equipment that can be used to produce any of the inventive fibers and fabrics is described in US Patent Application Pub. No. 2006/0012072 to Hagewood et al., incorporated by reference herein in its entirety. Exemplary equipment includes the following main parts: (1) Extruders and/or melt pumps to melt, mix and meter the polymer component, (2) a spin pack system or assembly comprising a polymer melt distribution system and spinneret that delivers a polymer melt(s) to capillaries that have shaped orifices, (3) attenuation device driven by pneumatic air, positive pressure, direct force and/or vacuum by which air drag forces act on a polymer stream to attenuate the fiber diameter to smaller than the orifice overall geometric shape, (4) fiber laydown region where fibers are collected underneath the attenuation device in a random orientation, and (5) fiber bonding system that prevents long range collective fiber movement. Numerous companies manufacture fiber and fabric making technologies that can be used for the present embodiments, and some non limiting examples include Hills Inc., Reifenhauser GmbH, Rieter Corporation, Neumag GmbH, Nordson Fiber Systems and others. 
     Referring to  FIG. 6 , a schematic of a typical spunbond system  100  utilizing a single polymer source is shown. Briefly, an exemplary spunbond system may include a hopper  110  into which pellets of polymer are placed. The polymer is fed from hopper  110  to a screw extruder  112 , where the polymer is melted. The molten polymer flows through heated pipe  114  into metering pump  116  and spin pack assembly  118 , including a spinneret  120  with orifices through which fibers  122  are extruded. The extruded fibers  122  are quenched with a quenching medium  124  (e.g., air), and are subsequently directed into a drawing unit  126  (e.g., aspirator). Upon exiting the drawing unit  126 , the attenuated fibers  128  are laid down upon a continuous screen belt  130  supported and driven by rolls  132  and  134 . The screen belt conveys the prebonded web of fibers from the laydown location to calendar rolls  144  and  146 . The extruder and melt pumps are chosen based on the polymers desired. Finally, the produced fabric may be introduced to a winder (not shown) to create rolls that may be transported. 
     It will be appreciated that the above-described optional materials my be incorporated into PVA and/or PLA fabrics by adding the material to the initial spinning step or by bonding the material to one or more fabric layers. As an example, SAP granules may be extruded with, or bonded to, PVA/PLA fibers. In one particular embodiment, SAP fibers may be created and then either (1) sewn into woven PVA/PLA fabrics or (2) crimped, cut to staple length, carded and needle punch formed into nonwoven fabrics. 
     Nonwoven fabrics may be post-processed in order to be used as a propulsor occlusion device. Post-processing may comprise one or more of: cutting and/or shaping fibers into predetermined lengths, cutting apertures into the fabric, and/or incorporating strength members therein. Strength members may be incorporated into fabrics by sewing or heat fusing the material. 
     It will be appreciated that although a nonwoven process is described above, any woven process may alternatively or additionally be employed to produce the inventive fabrics. Weaving has the advantage of easily adding in materials for particular functionality. For example, a fill yarn comprising any of the above-described materials may be created and weaved into a particular fabric. Moreover, any fiber construct can be fabricated by laminating sheets of woven materials together and/or laminating a woven fiber with a nonwoven fiber. An exemplary woven process is discussed in detail below in Example 2. 
     Deployment &amp; Buoyancy Control 
     The disclosed propulsor occlusion devices may be deployed in any number of ways, including in, on, or above water. For example, the device may be deployed by a diver or underwater vehicle. As another example, the device may be deployed via a seagoing vessel, such as by dropping, throwing or launching. As yet another example, the device may be dropped or launched via manned or unmanned aircraft. Upon deployment, the total density of the wetted material should be at or just slightly below the density of water if it is to remain on or within close proximity of the surface. 
     When the propulsor occlusion material is deployed from below the water, it must float to a position at or just slightly below the surface of the water. Providing a pre-constructed, fixed volume of material for flotation greatly increases the amount of ballast required to initially submerge the containment system prior to deployment. Accordingly, having a compact, inflatable source of buoyancy would help to minimize the pre-deployment volume necessary to submerge. 
     The disclosed fabrics may have a negative buoyancy (not including entrapped air), and so a deployment apparatus may be employed to provide beneficial positive buoyancy. In certain embodiments, the propulsor occlusion materials may comprise one or more materials and/or be shaped in such a way as to be provided with a controlled buoyancy. 
     Referring to  FIG. 7 , an exemplary inflatable buoyancy bag  700  is illustrated. The buoyancy bag may comprises a number of components that generate one or more gasses (e.g., carbon dioxide) upon submersion in water. 
     It has surprisingly been found that spun bond materials made from certain PVA polymers, such as EXCEVAL™ (CP4104) PVA, produced by Kuraray Europe GmbH, are gas permeable when dry, but quickly become gas impermeable when hydrated. This phenomenon may be exploited to employ an inflatable bag assembly to provide flotation. 
     Rectangular-shaped bags having a length (L) longer than their width (W) were sewn. The maximum internal volume of an exemplary bag is approximated by equation 1.
 
 V=W   2   *L/π   (1)
 
     This assumes a cylinder of length L and cross sectional area W2/π, no loss of volume due to the seams, etc., and represents a maximum. The longer the cylinder, the closer this will be to the actual volume. 
     In order to generate gas to fill the “cylinder” an aqueous reaction of sodium bicarbonate (NaHCO 3 ) and citric acid (C 6 H 8 O 7 ) may be employed to generate carbon dioxide (CO 2 ). The chemicals react according to equation 2 (ignoring additional ions in solution).
 
3 NaHCO 3(aq) +C 6 H 8 O 7(aq) →CO 2(g) +H 2 O+Na 3 C 6 H 5 O 7(aq)   (2)
 
     Since the CO 2  is lost to the solution as a gas, the reaction is driven to the right. Given the molecular weights of the reactants and the stoichiometry of 3 moles of NaHCO 3  reacting with one mole of C 6 H 8 O 7  to produce one mole of CO 2 , one gram of NaHCO 3  should react with 0.76 grams of C 6 H 8 O 7  to yield 0.52 grams (0.0119 moles) of CO 2 . Under expected conditions (e.g., 30 feet or less in depth, maximum 2 atm, and water temperature of 20° C.) the CO 2  gas produced should approximately follow the ideal gas law (equation 3).
 
 P*V=n*R*T   (3)
 
     Under these conditions, with a 1:1 (w/w) ratio of bicarbonate to citric acid (20% excess by weight of citric acid), one gram of bicarbonate will produce 143 cm 3  of gas. Assuming an approximate water density of 1 g/cm 3  the CO 2  produced should provide the equivalent of 143 g buoyant force (note that buoyancy should be measured in force, however, gravity can be cancelled out). 
     As an example, a bag may comprise dimensions of 4 inches by 8 inches (10 cm by 20 cm). This would have a theoretical volume of 637 cm 3  and provide flotation for 637 grams or 1.4 pounds, and measurements agreed with such predictions (about 1.5 pounds). The amount of bicarbonate required to fill this volume of gas would be 4.45 grams. 
     In practice, bags were fabricated in a production line mode. Citric acid and sodium bicarbonate were premixed in equal amounts and 10 grams of the mixture was added to each bag. The bags retained buoyancy for several hours before sinking (most likely due to slow gas permeability of the wetted fabric). 
     In field tests it was noted that bags filled with SAPs also seemed to provide flotation. Laboratory attempts were undertaken to replicate this observation. A bag was fabricated as described above, and 2.89 g of SAF was placed in the bag instead of the citric acid/sodium bicarbonate mixture. As shown in  FIG. 8 , the bag  700  was sealed in a food-saver vacuum bag  800 . The vacuum bag  800  was then opened under water and the SAF was allowed to absorb water for about one minute. The bag “inflated” and was neutrally buoyant. 
     Self Assembling 3D Structure &amp; Shape 
     A factor in the probability of intercept of a propulsor occlusion composition is the extension/expansion of the material in the water column. The material needs to be compact prior to deployment, but must expand quickly after deployment. 
     It was observed that the use of superabsorbent materials (SAMs), including SAPs and SAFs, caused the propulsor occlusion materials to “bloom” in the water due to a rapid increase in volume of the SAM upon wetting. SAMs absorb many times their mass in water a result of osmotic pressure. 
     As shown in Example 9 below, OASIS SAF® 6032 sliver from Technical Absorbents, Inc. was investigated. This material comprises a 50:50 weight ratio of SAF to polyethylene terephthalate (PET). It was found that, as the SAF absorbs water, the material expands and the fibers of PET were separated. Unfortunately as previously discussed, the swollen SAF fibers became weak and under the pressure from a propeller, the SAF sloughed off. 
     Just as a balloon assumes a particular shape when inflated, the osmotic pressure of the SAF or the pneumatic pressure of carbon dioxide formation may be used to cause a propulsor occlusion assembly to assume a shape in the water. 
     The hoop stress is the force tangent to the cylinder and perpendicular to the radius, σΘ. The stress along the axis of the cylinder is the longitudinal stress, σZ. The approximate magnitude of these stresses is given by equations 4 and 5, where P is the internal pressure, r is the radius of the cylinder and t is the thickness of the wall.
 
σθ= Pr/t   (4)
 
σ z=Pr/ 2 t   (5)
 
     Comparing two cylinders made of the same material (wall thickness) one can see that the stress on the surface, the restoring force, is proportional to the radius. That is, at the same pressure, a larger cylinder will have more force to make it assume a fully extended shape. The force is also proportional to the pressure, so, as is intuitively obvious, higher pressure will exert more force to assume an extended shape. 
     With the buoyancy bags that were previously described, the internal pressure depends on the amount of gas producing material added. The osmotic pressure will increase until the containment of the bag forces it to stop. 
     When a cylinder is rolled up, it may be more difficult for it to unroll than if it is folded into an accordion shape. Accordingly, it is possible to use pneumatic and/or osmotic forces to attain an expanded shape. 
     Referring to  FIG. 8 , an exemplary vacuum packing material  800  for use in limiting the pre-deployment volume of the propulsor occlusion device is shown. As discussed above, the volume of the propulsor occlusion device before deployment should be minimized. Moreover, in some situations, such as when deployed via a diver, the device may need to be submerged for deployment but not in intimate contact with the aqueous media prior to engagement. 
     Accordingly, a vacuum packing material  800  may be employed to contain the device before use. Such packing material may comprise any material having desired or required properties. Exemplary materials include, but are not limited to water-soluble PVA, polypropylenes and other packaging materials. Such packaging can be made strong enough to contain the volume of the propulsor occlusion materials when dry, while dissolving within a predetermined period of time within coming in contact with water to allow the propulsor occlusion device to quickly absorb water. 
     Such packaging imparts a number of benefits. First, it minimizes the volume and allows pre-deployed propulsor occlusion devices to be more easily handled. Second, if the mechanism for deployment is air drop or gun, the denser packing of the material will make it more aerodynamic. Third, it has surprisingly been found that removing air from between the fibers of the propulsor occlusion device allows more rapid ingress of water into the fabric. 
     EXAMPLES 
     The below terms are used throughout the Examples and are defined as follows:
         “PVA A” refers to NICHIGO G-POLYMER OKS-8041P, produced by Nippon Synthetic Chemical Industry Co., Ltd. (“Nippon”)   “PVA B” refers to NICHIGO G-POLYMER™ OK-8070P PVA, produced by Nippon.   “PVA C” refers to EXCEVAL™ (CP4104) PVA, produced by Kuraray Europe GmbH (“Kuraray”).   “PVA D” refers to NICHIGO G-POLYMER™ OK-8071 PVA, produced by Nippon.   “PVA E” refers to NICHIGO G-POLYMER™ OK-8112 PVA, produced by Nippon.   “PVA F” refers to NICHIGO G-POLYMER™ OK-8042 PVA, produced by Nippon.   “PVA G” refers to MOWIFLEX™ PVA, produced by Kuraray.   “PLA A” refers to INGEO™ Biopolymer 6400D, produced by Nature Works LLC.   “PLA B” refers to INGEO™ Biopolymer 6202D, produced by Nature Works LLC.   “PEO” refers to Polyethylene       

     Example 1—Multiple Yarn Samples 
     As shown in Table 1, below, a number of fibers were extruded and tested at Clemson University. As shown, each of the mono and/or multiconstituent samples comprises a number of single or multi-component fibers (Component 1, Component 2) having one of any number of cross-sectional geometries (e.g., round, segmented pie, caterpillar, starfish, octopus, hollow, core/sheath). Also noted in Table 1 is the yarn denier (gpd) and measurements of the tensile strength (kgf) and elongation of the yarn/fiber type produced in the extrusion process as well as detail and explanation of the experimental rationale for producing the various materials. As discussed below, a number of the samples were further processed into fabrics via woven and nonwoven processes. 
     
       
         
           
               
             
               
                 TABLE 1 
               
             
            
               
                   
               
               
                 Preliminary Yarns &amp; Fibers 
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                   
                 Comp. 
                 Comp. 
                   
                 den 
                 FILA 
                 ELONG 
                 STR 
                   
               
               
                 Run 
                 1 
                 2 
                 Shape 
                 (gpd) 
                 (#) 
                 (%) 
                 (kgf) 
                 Notes 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
               
               
            
               
                 1 
                 PVA A 
                 — 
                   
                 3421 
                 1 
                 1.252 
                 0.494 
                 To establish the 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 ability to spin PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 and maximize the 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 denier. Quenched in 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 hexane 
               
               
                 2 
                 PVA A 
                 — 
                   
                 4817 
                 1 
                 3.124 
                 2.705 
                 Increased denier 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 and eliminated 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 quench to increase 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 denier and tenacity 
               
               
                 3 
                 PVA A 
                 — 
                   
                 5872 
                 1 
                 2.534 
                 2.715 
                 Decreased length 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 from spinneret to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 winder 
               
               
                 4 
                 PVA A 
                 PLA A 
                 Seg. 
                 684 
                 19 
                 2.950 
                 0.218 
                 Determined 
               
               
                   
                   
                   
                 Pie 
                   
                   
                   
                   
                 feasibility of 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 spinning PLA/PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 segmented pie 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 (“Seg. Pie”) 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 geometries 
               
               
                 5 
                 PVA B 
                 PLA A 
                 Seg. 
                 733 
                 19 
                 267.3 
                 0.309 
                 Increased strength 
               
               
                   
                   
                   
                 Pie 
                   
                   
                   
                   
                 by using high MW 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PVA 
               
               
                 6 
                 PVA B 
                 — 
                 CAT 
                 12425 
                 1 
                 351.2 
                 1.582 
                 Cateripillar 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 (“CAT”) shape. 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 Maximize adhesion 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 and denier, also 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 high MW PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 drastically 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 increased 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 elongation 
               
               
                 7 
                 PVA B 
                 — 
                   
                 70087 
                 1 
                 349.6 
                 18.690 
                 To increase denier 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 the sample was 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 collected by free 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 fall and not wound 
               
               
                 8 
                 PVA B 
                 — 
                 STAR 
                 12134 
                 1 
                 270.3 
                 1.941 
                 Determine strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 and self-adhesion of 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 starfish (“STAR”) 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 geometry 
               
               
                 9 
                 PVA B 
                 — 
                 CAT 
                 31969 
                 1 
                 432 
                 5.604 
                 Caterpillar PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 was collected as 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 free-fall to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 maximize denier 
               
               
                 10 
                 PVA B 
                 — 
                 CAT 
                 4455 
                 1 
                 295.2 
                 1.278 
                 Caterpillar PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.4 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 11 
                 PVA B 
                 — 
                 CAT 
                 2705 
                 1 
                 187.7 
                 1.139 
                 Caterpillar PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.8 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 12 
                 PVA B 
                 — 
                 CAT 
                 3104 
                 2 
                 109.6 
                 0.689 
                 Caterpillar PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 1.6 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 13a 
                 PLA A 
                 — 
                   
                 3286 
                 1 
                 9.576 
                 1.501 
                 Pure racemic PLA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 to assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 for future 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 applications 
               
               
                 14 
                 5% 
                 10% 
                   
                 6197 
                 1 
                 1.890 
                 1.500 
                   
               
               
                   
                 Alginate 
                 CaCl2 
                   
                   
                   
                   
                   
                   
               
               
                   
                   
                 bath 
                   
                   
                   
                   
                   
                   
               
               
                 15 
                 25% 
                 75% 
                 CAT 
                 3579 
                 1 
                 307.6 
                 0.276 
                 PVA was collected 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 at draw rate 0.8 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 16 
                 25% 
                 75% 
                 CAT 
                 5753 
                 1 
                 391.8 
                 0.903 
                 Caterpillar PVA 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.4 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 17 
                 25% 
                 75% 
                 CAT 
                 10086 
                 1 
                 363.6 
                 1.756 
                 Caterpillar PVA 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.2 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 18 
                 25% 
                 75% 
                 CAT 
                 44189 
                 1 
                 3.163 
                 11.989 
                 Caterpillar PVA in 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 free fall was 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 collected to assess 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 strength scaling 
               
               
                 18a 
                 25% 
                 75% 
                 CAT 
                 44309 
                 1 
                 622.500 
                 9.096 
                 Sample #18 was 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 reanalyzed a day 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 later to ascertain 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 tensile effects of 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 moisture gain 
               
               
                 19 
                 50% 
                 50% 
                 CAT 
                 12311 
                 1 
                 6.562 
                 5.261 
                 Caterpillar PVA 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.2 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 19a 
                 50% 
                 — 
                 CAT 
                 11486 
                 1 
                 309.5 
                 0.749 
                 Sample #19 was 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 reanalyzed a day 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 later to ascertain 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 tensile effects of 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 moisture gain 
               
               
                 20 
                 50% 
                 — 
                 CAT 
                 5920 
                 1 
                 57.880 
                 1.423 
                 Caterpillar PVA 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.4 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 20a 
                 50% 
                 — 
                 CAT 
                 7407 
                 1 
                 211.700 
                 1.383 
                 Sample #20 was 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 reanalyzed a day 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 later to ascertain 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 tensile effects of 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 moisture gain 
               
               
                 21 
                 50% 
                 — 
                 CAT 
                 2771 
                 1 
                 129.8 
                 0.374 
                 Caterpillar PVA 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.8 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 22 
                 50% 
                 — 
                 CAT 
                 36567 
                 1 
                 6.883 
                 15.208 
                 Caterpillar PVA in 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 free fall was 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 collected to assess 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 strength scaling 
               
               
                 22a 
                 50% 
                 — 
                 CAT 
                 60325 
                 1 
                 6.071 
                 21.571 
                 Sample #22 was 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 used to test the 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 affect the moisture 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 on the tensile 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 properties. 
               
               
                 22b 
                 50% 
                 — 
                 CAT 
                 45072 
                 1 
                 6.265 
                 13.925 
                 Sample #22 was 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 used to test the 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 affect the moisture 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 on the tensile 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 properties. 
               
               
                 22c 
                 50% 
                 — 
                 CAT 
                 47938 
                 1 
                 7.247 
                 11.338 
                 Sample #22 was 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 used to test the 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 affect the moisture 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 on the tensile 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 properties. 
               
               
                 22d 
                 50% 
                 — 
                 CAT 
                 60621 
                 1 
                 337.287 
                 9.736 
                 Sample #22 was 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 used to test the 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 affect the moisture 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 on the tensile 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 properties. 
               
               
                 22e 
                 50% 
                 — 
                 CAT 
                 54342 
                 1 
                 446.608 
                 4.379 
                 Sample #22 was 
               
               
                   
                 PVA A 
                   
                   
                   
                   
                   
                   
                 used to test the 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 affect the moisture 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 on the tensile 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 properties. 
               
               
                 23 
                 PVA A 
                 — 
                 CAT 
                 3676 
                 1 
                 127.2 
                 0.783 
                 Caterpillar PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.8 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 23a 
                 PVA A 
                 — 
                 CAT 
                 2967 
                 1 
                 87 
                 0.404 
                 Sample #23 was 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 reanalyzed a day 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 later to ascertain 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 tensile effects of 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 moisture gain 
               
               
                 24 
                 PVA A 
                 — 
                 CAT 
                 5490 
                 1 
                 69.427 
                 1.132 
                 Caterpillar PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.4 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 25 
                 PVA A 
                 — 
                 CAT 
                 93795 
                 1 
                 46.076 
                 6.010 
                 Caterpillar PVA in 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 free fall was 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 collected to assess 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 strength scaling 
               
               
                 26 
                 75% 
                 25% 
                 CAT 
                 2038 
                 1 
                 179.282 
                 0.299 
                 Caterpillar PVA 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 1.6 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 27 
                 75% 
                 25% 
                 CAT 
                 3140 
                 1 
                 132.927 
                 0.246 
                 Caterpillar PVA 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.8 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 28 
                 75% 
                 25% 
                 CAT 
                 7309 
                 1 
                 168.698 
                 0.684 
                 Caterpillar PVA 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.4 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 29 
                 75% 
                 25% 
                 CAT 
                 9056 
                 1 
                 75.531 
                 1.426 
                 Caterpillar PVA 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 was collected at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw rate 0.2 to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 assess strength 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 scaling 
               
               
                 30 
                 75% 
                 25% 
                 CAT 
                 72398 
                 1 
                 89.899 
                 4.708 
                 Caterpillar PVA in 
               
               
                   
                 PVA A 
                 PVA B 
                   
                   
                   
                   
                   
                 free fall was 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 collected to assess 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 strength scaling 
               
               
                 31 
                 PVA B 
                   
                   
                 1053 
                 30 
                 209.762 
                 0.652 
                 High MW PVA was 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 extruded with the 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 #30 filament 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 spinneret to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 potentially be made 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 into a “rope” 
               
               
                 32 
                 5% 
                 10% 
                 Round 
                 1503 
                 100 
                 11.3 
                 0.198 
                 Alginate was spun 
               
               
                   
                 Alginate 
                 CaCl2 
                   
                   
                   
                   
                   
                 into many filaments 
               
               
                   
                   
                 bath 
                   
                   
                   
                   
                   
                 for potential rope. 
               
               
                 33 
                 5% 
                 10% 
                 Round 
                 1604 
                 1 
                 20.817 
                 1.126 
                 Alginate was spun 
               
               
                   
                 Alginate 
                 CaCl2 
                   
                   
                   
                   
                   
                 as a larger round 
               
               
                   
                   
                 bath 
                   
                   
                   
                   
                   
                 fiber for potential 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 rope use. 
               
               
                 34 
                 5% 
                 10% 
                 Round 
                 1314 
                 1 
                 12.400 
                 1.124 
                   
               
               
                   
                 Alginate 
                 CaCl2 
                   
                   
                   
                   
                   
                   
               
               
                   
                   
                 bath 
                   
                   
                   
                   
                   
                   
               
               
                 35 
                 PVA B 
                   
                 STAR 
                 14355 
                 1 
                 429.048 
                 1.989 
                 PVA spun using 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 starfish and free fall 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 to replicate a large 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 amount similar to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sample #9. 
               
               
                 36 
                 PVA B 
                 OCTO 
                 7651 
                   
                 1 
                 454.872 
                 2.001 
                 PVA spun using 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 octopus (“OCTO”) 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 and free fall to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 produce a large 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 amount similar to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sample #9 
               
               
                 37 
                 PVA B 
                   
                 OCTO 
                 10864 
                 1 
                 368.520 
                 2.148 
                 PVA spun using 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 octopus and free 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 fall to produce a 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 large amount 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 similar to sample #9 
               
               
                 38 
                 PVA B 
                   
                 Hollow 
                 9671 
                 1 
                 408.948 
                 3.370 
                 Hollow fiber PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 spun to produce a 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 fiber with positive 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 buoyancy in a 3D 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 construct 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 application. 
               
               
                 39 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 40 
                 PVA B 
                 PLA A 
                 S/C 
                 755.1 
                 19 
                 730.021 
                 0.198 
                 First attempt at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 spinning a 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 bicomponent 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 (“bico”) sheath/core 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 (“S/C”) fiber with 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PVA core and thin 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA sheath. 
               
               
                 41 
                 PVA B 
                   
                 Round 
                 1111 
                 30 
                 66.463 
                 0.919 
                 Respun round PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 fiber since first roll 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 was not usable. 
               
               
                 42 
                 PVA B 
                 PLA A 
                 S/C 
                 844.2 
                 19 
                 872.913 
                 0.152 
                 Spun bico 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA/PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sheath/core fiber at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 a ratio of 5:15 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sheath to core. 
               
               
                 43 
                 PVA B 
                 PLA A 
                 S/C 
                 1054 
                 19 
                 491.490 
                 0.216 
                 Spun bico 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA/PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sheath/core fiber at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 a ratio of 3:17 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sheath to core. 
               
               
                 44 
                 PVA B 
                 PLA A 
                 S/C 
                 1275 
                 19 
                 326.000 
                 0.512 
                 Large bico 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA/PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sheath/core fiber at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 a ratio of 5:30 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sheath to core. 
               
               
                 45 
                 PVA B 
                 PLA A 
                 S/C 
                 1352 
                 19 
                 356.400 
                 0.501 
                 Large bico 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA/PVA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sheath/core fiber at 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 a ratio of 10:30 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 sheath to core. 
               
               
                 46 
                 PVA B 
                 PLA A 
                 S/C 
                 327 
                 19 
                 26.000 
                 0.528 
                 Lower PVA content 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with multiple PLA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 ratios, 20:10, 4:1 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw ratio 
               
               
                 47 
                 PVA B 
                 PLA A 
                 S/C 
                 320 
                 19 
                 30.100 
                 0.502 
                 Lower PVA content 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with multiple PLA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 ratios, 20:8, 4:1 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw ratio 
               
               
                 48 
                 PVA B 
                 PLA A 
                 S/C 
                 320 
                 19 
                 33.900 
                 0.475 
                 Lower PVA content 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with multiple PLA 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 ratios, 20:6, 4:1 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 draw ratio 
               
               
                 49 
                 PVA B 
                 PLA A 
                 S/C 
                 665 
                 19 
                 105.600 
                 0.523 
                 Lower PVA content 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with varied draw 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 ratios PLA ratios, 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 20:10, 2:1 draw 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 ratio 
               
               
                 50 
                 PVA B 
                 PLA A 
                 S/C 
                 410 
                 19 
                 58.400 
                 0.645 
                 Lower PVA content 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with varied draw 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 ratios PLA ratios, 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 20:10, 3:1 draw 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 ratio 
               
               
                 51 
                 PVA B 
                 PLA A 
                 S/C 
                 410 
                 19 
                 58.420 
                 0.645 
                 Same as #50 except 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 that the fiber was 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 cut perpendicularly 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 from the roll to 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 create a nonwoven 
               
               
                 52 
                 PVA B 
                 PLA A 
                 S/C 
                 — 
                 19 
                 — 
                 — 
                 Sheath core with 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 melt speeds at 20 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PVA/15 PLA rpm, 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 then meltblown and 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 calendared 
               
               
                 53 
                 PVA B 
                 PLA A 
                 Round 
                 30 
                   
                   
                   
                 Pure PLA extruded 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 at 30 rpm 
               
               
                 54 
                 PVA B 
                 PLA A 
                 S/C 
                 568 
                 19 
                 59.810 
                 0.320 
                 Sheath core with 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 melt speeds at 4 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PVA/16 PLA rpm 
               
               
                 55 
                 PVA B 
                 PLA A 
                 S/C 
                 621 
                 19 
                 26.040 
                 8.150 
                 Sheath core with 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 melt speeds at 10 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PVA/10 PLA rpm 
               
               
                 56 
                 PVA B 
                 PLA A 
                 S/C 
                 0 
                 19 
                 — 
                 — 
                 Sheath core with 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 melt speeds at 20 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PVA/10 PLA rpm 
               
               
                 57 
                 PVA B 
                 PLA A 
                 S/C 
                 0 
                 19 
                 — 
                 — 
                 Nonwoven created 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with 20 PVA/20 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA rpm, aspirated 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 onto a moving belt 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 and pressed firmly 
               
               
                 58 
                 PVA B 
                 PLA A 
                 S/C 
                 0 
                 19 
                 — 
                 — 
                 Nonwoven created 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with 20 PVA/20 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA rpm, aspirated 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 onto a moving belt 
               
               
                 59 
                 PVA B 
                 PLA A 
                 S/C 
                 0 
                 19 
                 — 
                 — 
                 Nonwoven created 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with 20 PVA/10 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA rpm, aspirated 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 onto a moving belt 
               
               
                 60 
                 PVA B 
                 PLA A 
                 S/C 
                 0 
                 19 
                 — 
                 — 
                 Nonwoven created 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with 20 PVA/20 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA rpm, aspirated 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 into the collecting 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 bag 
               
               
                 61 
                 PVA B 
                 PLA A 
                 S/C 
                 0 
                 19 
                 — 
                 — 
                 Nonwoven created 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with 20 PVA/4 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA rpm, aspirated 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 into the collecting 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 bag 
               
               
                 62 
                 PVA B 
                 PLA A 
                 S/C 
                 0 
                 19 
                 — 
                 — 
                 Nonwoven created 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with 20 PVA/10 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA rpm, aspirated 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 into the collecting 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 bag 
               
               
                 63 
                 PVA B 
                 PLA A 
                 S/C 
                 0 
                 19 
                 — 
                 — 
                 Nonwoven created 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 with 20 PVA/20 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 PLA rpm, aspirated 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 onto a moving belt, 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 treated with heat 
               
               
                 49c 
                 PVA B 
                 PLA A 
                   
                 577 
                 19 
                 137.370 
                 0.830 
                   
               
               
                 65 
                 PVA B 
                 PLA A 
                   
                 290 
                 19 
                 32.385 
                 0.860 
                   
               
               
                 66 
                 PVA B 
                 PLA A 
                   
                 384 
                 19 
                 60.325 
                 0.840 
                   
               
               
                 67 
                 PVA B 
                 PLA A 
                   
                 320 
                 19 
                 62.018 
                 0.776 
                   
               
               
                 68 
                 PVA B 
                 PLA A 
                   
                 243 
                 19 
                 24.977 
                 0.780 
                   
               
               
                 69 
                 PVA B 
                 PLA A 
                   
                 — 
                 19 
                 — 
                   
                   
               
               
                 70 
                 PVA B 
                   
                   
                 2553 
                 30 
                 17.145 
                 1.808 
                   
               
               
                 71 
                 PVA B 
                   
                   
                 1429 
                 30 
                 136.271 
                 1.288 
               
               
                   
               
            
           
         
       
     
     Example 2—Woven Fabrics 
     Referring to  FIG. 9 , a number of the yarns listed in Table 1 were woven into fabrics according to the illustrated weaving pattern  1000  by Inman Mills, Inc. The pattern comprises a number of warp  1001  threads running in a warp direction (Y). As shown, the Ends per Inch (EPI), or number of warp threads per inch of woven fabric, was set at 18. 
     The pattern comprises a number of pick or fill threads  1002  running in a fill direction (X) perpendicular to the warp direction (Y). As shown, the Picks per Inch (ppi), or number of fill threads per inch of woven fabric, was set to 18. 
     The pattern further comprises one or more gaps  1003 , where fill threads were not included. As shown, a gap  1003  was included about every 0.5 inches. In order to achieve this, 9 fill yarns  1002  of the same type of material were woven, and then a 0.5 inch gap  1003  without fill yarns was skipped. 
     The weavings used extruded sample #55, as detailed in Table 1, as the warp yarn. Sample 55 comprises a bicomponent fiber having a 70% by weight PVA B core and a 30% by weight PLA A sheath. The PLA sheath was intended to keep the PVA from sticking to itself during the subsequent weaving process. 
     As shown in Table 2, a number of woven fabrics were created with varied filler materials. The identity of the fill yarns are documented in Table 2 where the OHMSETT 1 test matrix is documented (Tests 60-74). As an example, the first test in the OHMSETT 1 Tests (Test 60) refers to 44B which is a woven sample according to the pattern in  FIG. 9 , and having Sample 44 yarn from Table 1 as the fill yarn. Sample 44 yarn comprises a bicomponent fiber having a PVA B core and a PLA A sheath in a weight ratio of about 30:5. 
                     TABLE 2                  Consolidated Testing                                 Test   Type   Details                        1   Outboard Tank   Presoaked Sliver            2   Outboard Tank   18″ Unsoaked Sliver            3   Outboard Tank   8.83 g Presoaked/Pre-wrapped Sliver            4   Outboard Tank   Plastic            5   Outboard Tank   0.3 mil 8.8 g sheet            6   Outboard Tank   Presoaked Yarn (wet weight)            7   Outboard Tank   Unsoaked yarn            8   Outboard Tank   PVA Y-Fiber            9   Outboard Tank   PVA bags           10   Outboard Tank   Sample 13B           11   Outboard Tank   Chi Fiber           12   Outboard Tank   H Fiber           13   Outboard Tank   X Fiber           14   Outboard Tank   Octolobal           15   Outboard Tank   Plastic           16   Outboard Tank   H Fiber 3.86 g           17   Outboard Tank   H Fiber 8.16 g           18   Outboard Tank   6032 Sliver           19   Outboard Tank   SAF           20   Outboard Tank   Netted SAF           21   Outboard Tank   Oasis           22   Outboard Tank   Heavy Needled PET           23   Outboard Tank   Light Need led PET           24   Ddata Summary   Silver - all kinds           25   Ddata Summary   #40 square           26   Ddata Summary   #39 square           27   Ddata Summary   #38 square           28   Ddata Summary   #38 square           29   Ddata Summary   #40 tentacles           30   Ddata Summary   Scrim           31   Ddata Summary   SAF/Scrim           32   Ddata Summary   cotton tentacles           33   Ddata V4   E-CTP-1           34   Ddata V4   C-CTP-7           35   Ddata V4   C-CTP-8           36   Ddata V4   C-CTP-9           37   Ddata V4   C-WIN-1           38   Ddata V4   C-WIN-2           39   Ddata V4   Alma-2           40   Ddata V4   Alma-1           41   Ddata V4   D-CTP-1           42   Ddata V4   D-CTP-2           43   Ddata V4   D-CTP-3           44   Ddata V4   E-CTP-2           45   Ddata V4   E-CTP-3           46   Ddata V4   E-CTP-4           47   Ddata V4   E-CTP-5           48   Ddata V4   White Caterpillar           49   Ddata V4   E-SQR-1           50   Ddata V4   H&#39;s CAT           51   Aberdeen   PVA007           52   Aberdeen   PVA 035           53   Aberdeen   PVA 035 + SAF Bottom Edge           54   Aberdeen   PVA 035 + SAF           55   Aberdeen   PVA 009 + SAF           56   Aberdeen   PVA 009 + 035 + 003 + SAF           57   Aberdeen   PVA 003 + 011 + 012 + SAF           58   Aberdeen   PVA 010 + 011 + 003 + SAF           59   Aberdeen   Mixed PVA + SAF + Borax/Castor oil           60   OHMSETT 1   44B woven           61   OHMSETT 1   53A woven           62   OHMSETT 1   45 woven           63   OHMSETT 1   Hills Fabric 1           64   OHMSETT 1   NWH spunbond           65   OHMSETT 1   Fabric FAB           66   OHMSETT 1   Fabric woven + spun bond           67   OHMSETT 1   Woven           68   OHMSETT 1   OOIB-1067           69   OHMSETT 1   FAB PVA           70   OHMSETT 1   Woven (Hills)           71   OHMSETT 1   Spunbond           72   OHMSETT 1   Woven tentacles           73   OHMSETT 1   heart + star           74   OHMSETT 1   2 Rolls PVA           75   OHMSETT 2   6 × 5 × 1           76   OHMSETT 2   5 × 5 × 1           77   OHMSETT 2   4 × 5 × 1           79   OHMSETT 2   2 × 5 × 1           80   OHMSETT 2   1 × 5 × 1           81   OHMSETT 2   1 × 5 × 3 Tetris           82   OHMSETT 2   5 × 5 × 3 Tetris           83   OHMSETT 2   10 × 5 × 1           84   OHMSETT 2   15 × 5 × 1           85   OHMSETT 2   15 × 5 × 1           86   OHMSETT 2   20 × 5 × 1           87   OHMSETT 2   25 × 5 × 1           88   OHMSETT 2   30 × 5 × 1           89   OHMSETT 2   7 × 5 × 1           90   OHMSETT 2   31 × 5 × 1           91   OHMSETT 2   45 × 5 × 1                        
Results
 
     There was some difficulty in the weaving process because the yarn appeared to be drawing during the weaving process. It was found that the PLA fibers suffer from self-adhesion, which impeded the weaving process. 
     It was thought that with a thin sheath that the interior PVA would be easily exposed. However, initial testing showed that the PVA/PLA core/sheath configuration made the woven material hydrophobic, so much so that it did not wet and actually floated the cloth for an extended period of time. It was found that surfactants (e.g., soap) helped to wet out the material. Laboratory testing demonstrated that such surfactants helped to break the surface tension, reducing the hydrophobicity on the surface and allowed wetting of the material. 
     The woven materials showed limited success, so the nonwoven techniques of needle punch and spunbond were employed to make larger amounts of material moving forward. 
     Example 3—Nonwoven Fibers &amp; Fabrics 
     As shown in Table 3, below, a number of fabric samples were produced at Hills, Inc. comprising fibers having a PVA/PLA or PLA/PVA core/sheath structure. Table 4 provides exemplary general parameters for a nonwoven process (the “BRD” Process) used to produce one or more fabric samples. 
     
       
         
           
               
             
               
                 TABLE 3 
               
             
            
               
                   
               
               
                 Nonwoven Fibers &amp; Fabric Samples 
               
            
           
           
               
               
               
               
               
               
               
            
               
                   
                   
                 Comp. 1 
                 Comp. 2 
                 Filaments 
                   
                   
               
               
                 Sample 
                 Structure 
                 (Core) 
                 (Sheath) 
                 (No.) 
                 Line 
                 Notes 
               
               
                   
               
            
           
           
               
               
               
               
               
               
               
            
               
                 1 
                 Core/Sheath 
                 80% PVA B 
                 20% PLA B 
                 288 
                 BRD 
                   
               
               
                 2 
                 Core/Sheath 
                 80% PVA F 
                 20% PLA B 
                 288 
                 BRD 
                   
               
               
                 3 
                 Core/Sheath 
                 30% PLA B 
                 70% PVA C 
                 504 
                 BRD-3 
                 3 dpf, 30 
               
               
                   
                   
                   
                   
                   
                   
                 GSM 
               
               
                 4 
                 Core/Sheath 
                 50% PEO 
                 50% PLA B 
                 19 
                 LBRD 
                   
               
               
                 5 
                 Core/Sheath 
                 50% PEO 
                 50% PLA B 
                 19 
                 LBRD 
                   
               
               
                 6 
                 Core/Sheath 
                 50% PVA C 
                 50% PLA B 
                 19 
                 LBRD 
                   
               
               
                 7 
                 Core/Sheath 
                 50% PVA C 
                 50% PVA D 
                 19 
                 LBRD 
                   
               
               
                 8 
                 Core/Sheath 
                 30% PVA C 
                 70% PVA D 
                 19 
                 LBRD 
                   
               
               
                 9 
                 Core/Sheath 
                 30% PVA C 
                 70% PVA D 
                 19 
                 LBRD 
                   
               
               
                 10 
                 Core/Sheath 
                 30% PVA C 
                 70% PVA D 
                 19 
                 LBRD 
                 With Borax 
               
               
                 11 
                 Core/Sheath 
                 30% PVA C 
                 70% PVA D 
                 19 
                 LBRD 
                 With Borax 
               
               
                 12 
                 Core/Sheath 
                 30% PLA B 
                 70% PVA C 
                 504 
                 BRD-3 
                 150 GSM 
               
               
                 13 
                 Core/Sheath 
                 50% PVA G 
                 50% PLA B 
                 144 
                 BRD 
                 Freefall 
               
               
                 14 
                 Hollow 
                 — 
                 50% PLA B 
                 144 
                 BRD 
                   
               
               
                 15 
                 Core/Sheath 
                 50% PVA C 
                 50% PVA D 
                 144 
                 BRD 
                   
               
               
                 16 
                 Core/Sheath 
                 50% PVA C 
                 50% PVA D 
                 144 
                 BRD 
                   
               
               
                 17 
                 Delta 
                 PLA B 
                 — 
                 288 
                 BRD 
                   
               
               
                 18 
                 Core/Sheath 
                 30% PLA B 
                 70% PVA E 
                 504 
                 BRD-3 
                 100 GSM 
               
               
                 19 
                 Core/Sheath 
                 30% PLA B 
                 70% PVA E 
                 504 
                 BRD-3 
                 100 GSM 
               
               
                 20 
                 Core/Sheath 
                 30% PLA B 
                 70% PVA E 
                 504 
                 BRD-3 
                 100 GSM 
               
               
                 21 
                 Segmented Pie 
                 30% PLA B 
                 70% PVA E 
                 504 
                 BRD-3 
                 100 GSM 
               
               
                 22 
                 Core/Sheath 
                 30% PLA B 
                 70% PVA E 
                 504 
                 BRD-3 
                 100 GSM 
               
               
                   
               
            
           
         
       
     
     
       
         
           
               
             
               
                 TABLE 4 
               
               
                   
               
               
                 BRD Nonwoven Process - General Parameters 
               
               
                 General Parameters 
               
               
                   
               
             
            
               
                   
               
            
           
           
               
               
               
            
               
                   
                 Holes No. 
                 288 
               
               
                   
                 Holes Shape 
                 Round 
               
               
                   
                 Hole Diam. 
                 0.35 
               
               
                   
                 Spinneret 
                 288 FILS 
               
               
                   
                 P1 MP Size 
                 4.8 CC 
               
               
                   
                 P2 MP Size 
                 4.8 CC 
               
               
                   
                 Denier 
                 1250/4.3 
               
               
                   
                 Tenacity 
                 1.5 
               
               
                   
                 Elongation 
                 26% 
               
               
                   
                 Spin Finish Type 
                 3771 @ 12% 
               
               
                   
                 SF Source 
                 Metered 
               
               
                   
                 Notes 
                 Intermingler @ 30 PSI 
               
               
                   
                   
                 2nd Pack with 0.004″ SPACER 
               
               
                   
                   
                 BRD 
               
               
                   
                   
               
            
           
         
       
     
     As an example, a fabric was produced according to the nonwoven BRD-3 process comprising fibers having a core/sheath geometry, with a 30% by weight PLA B core and a 70% by weight PVA C sheath (see Table 3 at Sample 3). The fabric comprised 504 filaments, with a DPF of ˜3 and a basis weight of 150 GSM. 
     Based on the Example 2 results, it was decided that the core/sheath orientation should be reversed, such that subsequent extrusions had a PLA core with PVA sheath. In a spunbond line, the adhesion of the filaments to each other does not interfere with the process so PVA could be employed as the sheath. 
     Referring to  FIG. 10 , the spunbond materials were post-processed at Clemson Apparel Research, as shown, to make samples  1100  suitable for particular target vessels. 85% of the nonwoven fabric was made into 5-ply, 1-roll width (20 inches), 10-ft long sections. The other 15% of the material was made into 1-ply, 1-roll width, 10-ft long sections. Samples  1100  were sewn  1110  at 3 stitches per inch, lockstitch, along the two long sides. For each sample, three rows of 2 inch×2 inch square windows  1120  were cut, separated by 3 inch muntins  1130 . The “muntins” are analogous to the strips of wood separating and holding together panes of glass in a window. 
     The fabrics were then tested at the Oil Spill Responsible Research &amp; Renewable Energy Test Facility (OHMSETT) in Leonardo, N.J. to determine a number of properties. OHMSETT&#39;s above ground concrete test tank is measures 203 meters long by 20 meters wide by 3.4 meters deep. The tank is filled with 2.6 million gallons of crystal clear saltwater. The test tank allows testing of full-scale equipment, and the tank&#39;s wave generator creates realistic sea environments, while state-of-the-art data collection and video systems record test results. 
     Results 
     Although the materials were capable of occluding propulsors, it was found that the 150 GSM basis weight was slightly heavy. Moreover, the square holes caused the material to tear at the corners of the holes. 
     In subsequent laboratory testing it was found that the bonds in the material made by the calendaring process went away as the PVA dissolved. This caused the material to become less of a coherent fabric than a mass of filaments. 
     Example 4—Intermediate Scale Testing of Woven Fabrics 
     As shown in Table 3, the fabrics comprised fibers having a core/sheath geometry, with a 30% by weight PLA B core and a 70% by weight PVA E sheath. The fabrics comprised 504 filaments, with a DPF of about 3 and a reduced basis weight of about 100 GSM. 
     Referring to  FIG. 11 , the spunbond material were then post-processed, as shown, to make samples  1200  suitable for particular target vessels. In one test, 100% of the material was made into 15-ply, 1-roll width (20 inches), 22-ft long sections. Each sample  1200  was sewn at 3 stitches per inch, lockstitch, down the two long sides  1210 . Reinforcement was also added to the assemblies by cross stitching  1211  the material. In each sample, three rows of 2 inch diameter windows  1220  were cut, separated by 3 inch muntins. It was decided to make circular holes  1220  in the fabric rather than square holes (see  FIG. 10  at  1120 ) to eliminate tearing at the corners of the holes. The total amount of material delivered was about 5,000 yards of spunbond fabrics. 
     The materials were then tested at OHMSETT to determine a number of properties, including occlusion, wet-strength, water absorption, etc. 
     Results 
     Intermediate scale testing showed that 22 foot long samples were too short to effectively stop or slow a Landing Craft Mechanized, Mark 8 (“LCM8”) target vessel. The LCM-8 is a river boat and mechanized landing craft used that weighs 135,000 pounds. LCM-8s are constructed from welded steel and powered by two 12V71 diesel engines, twin propellers, and rudders. 
     It was found that sewn fabrics comprising the core/sheath fabrics held together well. However, subsequent laboratory testing determined that the point bonds from the calendaring process were formed in the PVA sheath of the fiber. Since the PVA material dissolves quickly, the point bonds did not provide the material with a desired strength. 
     Based on this laboratory observation, it was determined to switch to a segmented pie fiber cross-section to increase the time the material stayed intact (see Table 3, Sample 21). The calendaring temperature was also increased to increase bonding. This material held together better but was more hydrophobic and “papery.” 
     Example 5—Full Scale Testing of Woven Fabrics 
     A number of fabrics were produced at Hills, Inc. according to a spunbond nonwoven process. The fabrics comprised fibers corresponding to Samples 18-20 and 22 of Table 3. 
     Bicomponent, biconstituent fibers were produced comprising a core/sheath geometry, with a 30% by weight PLA B core and a 70% by weight PVA E sheath. The fibers were processed into fabrics according to the BRD-3 spunbond process, and the fabrics comprised 504 filaments, with a DPF of about 3 and a basis weight of 100 GSM. 
     Referring to  FIGS. 12 and 13 , upon completion of the spunbond process the spunbond material was then post-processed, as shown, to make sections  1300  suitable for particular target vessels. 100% of the material was made into 15-ply, 1-roll width, 33-ft long sections  1300 . The length of the sections  1300  was increased from 22-ft to 33-ft based on the results of the above experiment (see  FIG. 11 ). 
     As shown, a number of the sections were used to create 15-ply, 2-roll width (“doublewide”), 33-ft long sections  1400 . The doublewide samples  1400  were obtained by sewing  1440  together first  1301  and second  1302  1-roll-wide sections along one of the longer sides thereof. 
     It was found in intermediate scale testing that the sewn materials of the core/sheath fabric held together fairly well and it was therefore decided to modify the lockstitch pattern to take further exploit fabric longevity. Each sample was sewn at 3 stitches per inch, lockstitch, with ten seams down the length  1310  and diagonally across the width  1312 . In each sample, three rows of 2 inch×2 inch circular windows  1320  were cut, separated by 3 inch muntins  1330 . The total amount of material delivered was about 10,000 meters of spunbond fabric and the material was then tested at Panama City Beach. 
     Example 6—Material Buoyancy 
     A number of the materials listed in Tables 1-3, above, were tested to determine buoyancy and dissipation characteristics. 
     In one test, the inherent buoyancy of the materials was determined. A temperature-controlled water bath was provided and a weighed sample was suspended from a hook resting on an analytical balance. The material and hook were then submerged in the water bath for a predetermined time period. Care was taken to account for the amount of water displaced by the hook itself. The hook was weighed before and after immersion in the water. 
     During sample processing, stitching and mechanical cutting fused layers of material, trapping air pockets in some of the samples. Additionally, small bubbles can sometimes adhere to a fabric and makes it appear more buoyant. Tongs were used to gently squeeze the material in order to release bubbles trapped between layers. 
     The buoyancy of a material is simply the dry weight of the material minus the weight of the water that it displaces. Measurements can be complicated by the fact that some of these materials are water soluble, the weight changes with time. This characteristic was utilized to determine the rate of dissolution of the materials. 
     Results 
     Table 5, below, shows the apparent density of a number of materials used in this project. The measured weight, dry and submerged, are reported and the apparent density is calculated by dividing the dry weight by the amount of water displaced. The amount of water displaced is equal to the dry weight minus the buoyant weight. This number is a mass, but converts to volume using the density of fresh water as 1.0 grams per cm 3  at 25 C. 
     
       
         
           
               
             
               
                 TABLE 5 
               
             
            
               
                   
               
               
                 Apparent Density of Propulsor Occlusion Materials 
               
            
           
           
               
               
               
               
               
            
               
                   
                   
                 Dry 
                 Buoyant 
                 Apparent 
               
               
                   
                   
                 Weight 
                 Weight 
                 Density 
               
               
                   
                 Material 
                 (g) 
                 (g) 
                 (g/cc) 
               
               
                   
               
            
           
           
               
               
               
               
               
            
               
                  1 
                 45 ply spunbond 5 × 5 × 1 cm 
                 3.44 
                 0.76 
                 1.22 
               
               
                  2 
                 Inman Mills woven fabric 
                 3.5 
                 0.41 
                 1.12 
               
               
                  3 
                 Hills nonwoven fabric  
                 3.6 
                 −1.68 
                 0.53 
               
               
                   
                 (30 GSM PLA sheath) 
                   
                   
                   
               
               
                  4 
                 Oasis 6032 
                 3.35 
                 0.92 
                 1.27 
               
               
                  5 
                 150 GSM 
                 4.99 
                 0.96 
                 1.19 
               
               
                  6 
                 100 GSM 
                 4.81 
                 0.99 
                 1.21 
               
               
                  7 
                 Segmented Pie GSM 
                 5.18 
                 0.68 
                 1.13 
               
               
                  8 
                 Foundations 
                 5.1 
                 −0.97 
                 0.81 
               
               
                  9 
                 Orange Laundry bag 
                 5.04 
                 0.46 
                 1.09 
               
               
                 10 
                 8071 PVA/Exceval 70/30 
                 4.41 
                 0.74 
                 1.17 
               
               
                 11 
                 8071 PVA/Exceval 50/50 
                 5.02 
                 0.78 
                 1.16 
               
               
                 12 
                 segmented pie PLANichigo G 
                 2.09 
                 0.63 
                 1.30 
               
               
                 13 
                 core sheath PLA/Nichigo G 
                 2.18 
                 0.41 
                 1.19 
               
               
                 14 
                 core sheath PLA/Nichigo G 
                 4.57 
                 0.88 
                 1.19 
               
               
                   
                 which has been sewn together 
                   
                   
                   
               
               
                 15 
                 New material 20141101 
                 4.72 
                 0.89 
                 1.19 
               
               
                 16 
                 Circles (cut edges intact) 
                 5.29 
                 0.99 
                 1.19 
               
               
                 17 
                 Circles (plies separated) 
                 5.36 
                 1.02 
                 1.19 
               
               
                 18 
                 Exceval/PLA 
                 5.59 
                 0.93 
                 1.17 
               
               
                 19 
                 Clemson #7 (dipped in surfactant) 
                 5.3 
                 0.94 
                 1.18 
               
               
                 20 
                 Clemson #9 (dipped in surfactant) 
                 5.05 
                 0.52 
                 1.10 
               
               
                 21 
                 3314.1/6202 PLA 70/30 
                 5 
                 1.03 
                 1.21 
               
               
                 22 
                 3314.1/6202 PLA 50/50 
                 6.4 
                 1.37 
                 1.21 
               
               
                 23 
                 3.088 DPF 50/50 
                 6.83 
                 1.39 
                 1.20 
               
               
                 24 
                 3.088 DPF 70/30 
                 5.33 
                 1.16 
                 1.22 
               
               
                   
               
            
           
         
       
     
     In order for the propulsor occlusion material to stay at or near the top of the water column, the overall density of the material in water must be equal to or slightly less dense than water. The density of fresh water is 1.00 g/cm 3  and seawater is 1.03 g/cm 3 . 
     As shown in the above Table 5, only two materials showed “positive buoyancy”—Samples 3 and 8. However, both of these samples had obvious air entrapped. 
     Excluding the outliers of the two materials that showed positive buoyancy, the average value is 1.18±0.05. This number helps to estimate the amount of buoyancy that will be required for a sample to make it neutrally buoyant. For instance, if one is deploying 10 kg of propulsor occlusion material the material displaces 8.5 liters of water (10 kg/1.18 kg/L). So, the effective weight of the material in water will be 1.5 kg. This means for it to be neutrally buoyant, one would have to add an additional 1.5 liters of displacement. 
     One of the largest samples tested at OHMSETT consisted of 150 plies of 150 GSM fabric that was 3 by 0.5 meters. The mass was 33.75 kg (150×0.15×3×0.5), which would displace 28.125 liters of water. The effective weight in water of the material would be 5.625 kg. So, in order for the sample to be neutrally buoyant, an additional 5.626 liters of water would need to be displaced. 
     As discussed above, one of the disclosed exemplary buoyancy bags displaces about 0.64 liters of water. To make this large sample buoyant would require 9 of these bags (e.g., 5.626 kg/0.64 L)=8.79 kg/L, round up to 9). 
     Example 7—Needle Punch Fabrics 
     Three needle punch fabrics were also tested to determine buoyancy properties. The fabrics were:
         1. 80/20 SAF/PLA comprising Palmetto Synthetics PLA (2 inch fiber length) 100 strokes/min on needle loom   2. 90/10 SAF/PLA (same fiber as above) 100 strokes/min on needle loom   3. 90/10 SAF/PLA (same fiber as above) 150 strokes/min on needle loom       

     It was found that these fabrics did not have the tensile strength to keep from tearing apart when saturated with water so hanging on a hook to measure water absoprtion was not possible. To accommodate the difficulty dealing with the needle punch material a different approach was utilized.
         1. A square of fabric was cut out and weighed.   2. The square was placed in a sieve which was lowered into water submerging the fabric (non-buoyant) and allowed to soak undisturbed for 5 minutes.   3. After 5 minutes the sieve was carefully lifted from the water such that the SAF did not break free.   4. Unabsorbed water was allowed to drain from the fabric for approximately 15 seconds and then the sample weighed. Although an apparent density could not be calculated, the multiple of water weight absorbed by the sample could be estimated.   5. The fabric was then physically manipulated under gently running water by rubbing between fingers or rubbing over the mesh screen to wash away the shorter SAF leaving only the PLA.   6. The PLA was then dried in an oven and weighed.
 
Results
       

     This process allowed for calculation of a percentage of the starting weight of material that would need to be accounted for in buoyancy accommodation. A triplicate analysis of these three needle punch fabrics is shown below in Table 6. The density of PLA as reported in the literature is 1.210-1.430 g/cc. 
     
       
         
           
               
             
               
                 TABLE 6 
               
             
            
               
                   
               
               
                 SAF/PLA Water Absorption 
               
            
           
           
               
               
               
               
               
               
            
               
                   
                 Sample 
                 Sample 
                 Sample 
                   
                   
               
               
                   
                 1 
                 2 
                 3 
                 AVG 
                 STDEV 
               
               
                   
               
            
           
           
               
            
               
                 80/20 SAF/PLA 100 strokes/min 
               
            
           
           
               
               
               
               
               
               
            
               
                 Multiple of water  
                 89.86 
                 86.97 
                 81.37 
                 86.07 
                  4.32 
               
               
                 weight absorbed 
                   
                   
                   
                   
                   
               
               
                 Percentage of  
                  8.70 
                  8.55 
                  8.33 
                  8.53 
                  0.18 
               
               
                 ending vs initial 
                   
                   
                   
                   
                   
               
            
           
           
               
            
               
                 90/10 SAF/PLA 100 strokes/min 
               
            
           
           
               
               
               
               
               
               
            
               
                 Multiple of water  
                 57.56 
                 68.88 
                 78.90 
                 68.45 
                 10.68 
               
               
                 weight absorbed 
                   
                   
                   
                   
                   
               
               
                 Percentage of ending  
                 11.06 
                 10.70 
                 10.77 
                 10.84 
                  0.19 
               
               
                 vs initial 
                   
                   
                   
                   
                   
               
            
           
           
               
            
               
                 90/10 SAF/PLA 150 strokes/min 
               
            
           
           
               
               
               
               
               
               
            
               
                 Multiple of water  
                 68.37 
                 69.85 
                 86.25 
                 74.82 
                  9.92 
               
               
                 weight absorbed 
                   
                   
                   
                   
                   
               
               
                 Percentage of ending  
                 13.66 
                 13.61 
                 13.33 
                 13.53 
                  0.18 
               
               
                 vs initial 
               
               
                   
               
            
           
         
       
     
     Example 8—Sap Wet-Strength 
     As an experiment, the aqueous solution shown in Table 7 was mixed and then dried under nitrogen to create an amorphous mass. The dry compound was then submerged in water for enough time to allow for approximately maximum water absorption. The compound was then removed and measurements were taken to determine the mass thereof. 
                     TABLE 7                  PVA/SAP Compositions                             Component   % by Weight                       Water   80%           PVA   10%           SAP   10%                        
Results
 
     While the PVA/SAP mixture absorbed approximately 12 times its mass, there was an inverse relationship with the material&#39;s durability. After absorbing its dry weight in water, the gel had little structural integrity. Accordingly, it may be preferred to employ encapsulated SAP to provide additional wet-strength to the material. 
     Example 9—SAF Wet Strength 
     Technical Absorbents Limited (TAL) of Grimsby, North East Lincolnshire, United Kingdom produces a number of SAFs under their Oasis Superabsorbent Fibers (OASIS SAF®) line. The OASIS SAF® products comprises a cross-linked terpolymer of acrylic acid, methylacrylate and an amount of a special acrylate/methacrylate monomer in which the acrylic acid is partially neutralized to the sodium salt of acrylic acid. The cross-links between the polymer chains are formed as ester groups by reaction between the acid groups in the acrylic acid and the hydroxyl groups in the hydroxypropylmethacrylate. OASIS SAF® is available with variable degrees of cross-linking and in two general fiber types and sizes: long staple products (52 mm length &amp; 10 dtex denier) and short staple products (6 mm length &amp; 10 dtex denier). 
     As an experiment, the aqueous solution shown in Table 8 was mixed and then dried to create an amorphous mass. The SAF material used was TAL OASIS SAF® 6032, which comprises a 50:50 blend of SAF and polyester terapthalate (PET). It is was provided in sliver form (i.e., untwisted roving). 
     An exemplary propulsor occlusion fabric may be prepared including TAL OASIS SAF® 6032 material, which comprises as 50:50 ratio SAF and PET. Although these materials may break apart somewhat easily when put under hydrodynamic pressure on a propeller, the remaining PET fiber may be effective in occluding the propeller. 
     The dry compound was then submerged in water and a water soluble dye was added so that images could be obtained. The material was submerged for enough time to allow for approximately maximum water absorption and images were taken of the submerged compound. The compound was then removed so water absorption could be determined. 
                     TABLE 8                  SAF/PVA Compositions                             Component   % by Weight                       Water   90%           SAF   10%           (PET/SAP)                        
Results
 
     Throughout multiple tests, it was noted that SAPs are difficult to dissolve due to extreme hydrophilicity, and likely cross-linking by manufactures to ensure discreet granules. However, hand mixing PVA fibers with SAP into a nearly homogenous construct did show that PVA could contain the SAP, creating an expanding sticky mass when submerged in water. 
     To create more homogenous SAP solutions, the SAP may be dissolved in water at an elevated temperature. The ratio of water to fiber necessary for complete dissolution may be on the order of larger than about 400:1, about 500:1, about 600:1, about 700:1, about 800:1, about 900:1 or about 1000:1. This may necessitate a concentration step to create a solution capable of being wet spun into fibers and fabrics. 
     It was surprisingly found that co-extruding SAP and PVA polymers created a uniformly entangled yarn. Since SAP cannot be melt extruded into fibers, both polymers may be extruded from an aqueous solution in a process called dry spinning, so named because the removal of the solvent (water) via in-line heating creates a solid fiber. This yarn can then be either collected continuously on a bobbin, or extruded onto a belt to create a nonwoven fabric. The fabric can then be used to enhance propulsor occlusion constructs, or as a stand-alone device, depending on the final tensile properties required or desired. 
     In one embodiment, a homo-homo yarn extrusion process may be employed to incorporate SAPs into the exemplary PVA and/or PLA fabrics. The process incorporates wet spinning to simultaneously extrude SAP and PVA. The intent is for the PVA to provide strength and protection for the SAP. In another embodiment, graft copolymerization or formulations of mixtures of polymers may be employed to incorporate the SAPs in fabrics. 
     Example 10—Multivalent Cation/Anion Salts 
     Experiments were conducted to assess the attributes of additives that could potentially provide positive buoyancy through gas production, as well as added strength, duration, and ability to adhere to a metallic prop. To bypass the complexities of dry spinning, aqueous solutions were extruded into acetone by a syringe pump to create fibers in a process called wet spinning. 
     Wet spinning is an excellent bench top method for exploring fiber properties on a small scale, but is difficult to scale up and carries the risk of releasing trace amounts of solvent into the ocean. This process creates fibers that are collected in a beaker, and then dried in an oven under nitrogen to create a fibrous mass. The dried samples were then submerged in water, and their properties were noted over time. 
     Using this method, a number of multivalent cation and anion salts were combined with aqueous solutions of 10% by weight PVA and fibers were created. The experiments included borax, copper sulfate, sodium sulfate, calcium oxide, aluminum oxide, sodium bicarbonate, alginic acid, citric acid, and aluminum acetate. Solutions of 10% by weight PVA and 0.5%, 0.4%, 0.3% and 0.2% by weight of each additive were prepared and dried. 
     Each of the compounds were then processed into fibers via an extrusion process. The fibers were then observed and subjected to moisture to determine specific characteristics. 
     Results 
     Borax and sodium sulfate both were both found to be self-adhesive when exposed to water, and borax was mildly adhesive to steel. The 0.5% borax solution was too thick to be extruded, while the 0.4% solution created an excellent fiber. However, the 0.4% borax fiber was too resilient to water absorption, delaying its sticky properties for 10 minutes. The 0.3% and 0.2% borax solutions were both instantly sticky and very malleable. After 25 minutes the 0.3% borax fiber created a self-adhesive mass similar to dried rubber cement, and the 0.2% borax fiber had little structural integrity left. 
     The sodium sulfate samples were found to be self-adhesive when exposed to water. However, all of the sodium sulfate samples were more brittle than the borax samples. 
     Example 11—Toxicity &amp; Environmental Compliance 
     In order to determine the toxicity of exemplary propulsor occlusion embodiments, samples were prepared as follows:
         1. 50 g of fabric was weighed out and cut in to 1-2″ squares.   2. Cut squares were added to deionized water, heated to approximately 90° C. with stirring heat plate.   3. After 3 hours of dissolution/extraction for 3 hours at 70-75° C., the heat was turned off and water was cooled in an ice bath.   4. Water was strained through a wire sieve to remove the remaining solids.   5. The chilled liquid was aliquoted into bottles for testing.       

     Tests were conducted according to the following standards to determine toxicity and environmental compliance:
         1. Eden Research Testing, RCRA Toxicity Characteristic Leaching Procedure (TCLP) for VOCs, SVOCs, Chlorinated Pesticides and Herbicides, and Metals by SW-846 Method 1311 and Analysis   2. 5511 Standard Test Method for Determining Anaerobic Biodegradation of Plastic Materials Under High-Solids Anaerobic-Digestion Condition   3. 5988 Standard Test Method for Determining Aerobic Biodegradation of Plastic Materials in Soil.
 
Results
       

     It was found that use of the inventive propulsor occlusion devices does not adversely affect public health or safety, does not involve effects on the human environment that are uncertain, does not threaten a violation of law applicable to the Department of the Navy, involve unique or unknown risk or are scientifically controversial. 
     Testing found no concentrations of concern, confirming assertions made in the record of categorical exclusion. Specifically: VOC, SVCOCs, chlorinated herbicides, organo-chlorinated pesticides, TCLP priority metals and other TCLP components were tested by EPA, or other ELAP, methods. 
     The propulsor occlusion devices may meet all requirements of each of the enumerated laws and regulations in Table 9, below. 
     
       
         
           
               
             
               
                 TABLE 9 
               
             
            
               
                   
               
               
                 Federal &amp; State Environmental Laws and Regulations 
               
            
           
           
               
               
               
               
            
               
                   
                 Federal or 
                   
                   
               
               
                 Environmental Law 
                 State Law 
                 Responsible Agency 
                 Regulated Activity and Resource 
               
               
                   
               
               
                 California Coastal Act 
                 State 
                 CCC/BCDC 
                 Activities that modify land or 
               
               
                 (CCA) 
                   
                   
                 water use in the coastal zone 
               
               
                 (PRC §30000 et. seq.) 
                   
                   
                   
               
               
                 California Endangered 
                 State 
                 CDFW 
                 Activities affecting state- 
               
               
                 Species Act (CESA) 
                   
                   
                 listed species 
               
               
                 (FGC § 2081 &amp; 2090) 
                   
                   
                   
               
               
                 California Environmental 
                 State 
                 OPR and SCH 
                 Discretionary actions 
               
               
                 Quality Act (CEQA) 
                   
                 (oversight) 
                 proposed to be carried out or 
               
               
                 (PRC § 21000-21177) 
                   
                   
                 approved by California public 
               
               
                   
                   
                   
                 agencies 
               
               
                 Section 401, Clean Water 
                 Federal 
                 SWRCB 
                 Discharges requiring a federal 
               
               
                 Act (CWA) 
                   
                 (EPA oversight) 
                 license or permit to comply 
               
               
                 (33 USC 1341) 
                   
                   
                 with state or federal water 
               
               
                   
                   
                   
                 quality standards 
               
               
                 Section 402, Clean Water 
                 Federal 
                 SWRCB 
                 Point source discharges to 
               
               
                 Act (CWA) 
                   
                   
                 surface waters of the U.S. 
               
               
                 (33 USC 1342) 
                   
                   
                   
               
               
                 Coastal Zone 
                 Federal 
                 NOAA 
                 Project modifies land or water 
               
               
                 Management Act (CZMA) 
                   
                   
                 use in the coastal zone of a 
               
               
                 (16 USC 1451) 
                   
                   
                 state with an approved CMP 
               
               
                 Section 7 &amp; 10, 
                 Federal 
                 USFWS/NMFS 
                 Activities affecting species 
               
               
                 Endangered Species Act 
                   
                   
                 listed as threatened or 
               
               
                 (16 USC 1531-1544) 
                   
                   
                 endangered under the ESA 
               
               
                 Marine Mammal 
                 Federal 
                 USFWS/NMFS 
                 Activities affecting marine 
               
               
                 Protection Act (MMPA) 
                   
                   
                 mammals and their products 
               
               
                 (16 USC 1361 et. seq.) 
                   
                   
                   
               
               
                 National Environmental 
                 Federal 
                 CEQ and EPA 
                 Major federal actions 
               
               
                 Policy Act (NEPA) 
                   
                 oversight 
                 significantly affecting the 
               
               
                 (42 USC 4312) 
                   
                   
                 quality of the human 
               
               
                   
                   
                   
                 environment 
               
               
                 Porter-Cologne Water 
                 State 
                 SWRCB 
                 Activities that may affect 
               
               
                 Quality Control Act 
                   
                   
                 surface or groundwater 
               
               
                 (Division 7, California 
                   
                   
                 quality 
               
               
                 Water Code) 
                   
                   
                   
               
               
                 Vessel General Permit, 
                 Federal 
                 EPA 
                 26 general discharges from 
               
               
                 402, 33 U.S.C. 1342. 
                   
                   
                 the normal operations of 
               
               
                   
                   
                   
                 vessels 
               
               
                 MARPOL, Act to Prevent 
                 Federal 
                 EPA 
                 Compliance by typically 
               
               
                 Pollution from Ships (Act 
                   
                   
                 Excluded vessels which 
               
               
                 to Prevent Pollution from 
                   
                   
                 include those from US Navy 
               
               
                 Ships, 33 U.S.C. §§ 1901- 
                   
                   
                 and Coast Guard 
               
               
                 1915) 
                   
                   
                   
               
               
                 Uniform National 
                 Federal 
                 DoD 
                 Discharges from military and 
               
               
                 Discharge Standards 33 
                   
                   
                 coast guard vessels from the 
               
               
                 U.S.C. § 312(n) 
                   
                   
                 coast to 12 miles at sea 
               
               
                 California Ocean Plan, 
                 State 
                 SWRCB 
                 Point Source and Vessel 
               
               
                 State Water Resources 
                   
                   
                 discharges, areas of special 
               
               
                 Control Board, CH&amp;S 
                   
                   
                 biological significance 
               
               
                 25117 et. seq. 
                   
                   
                 Delineated, standards set 
               
               
                 Resource Conservation 
                 Federal 
                 EPA 
                 Ocean Discharge and 
               
               
                 Recovery Act - 42 U.S.C. 
                   
                   
                 Dumping 
               
               
                 ch. 82 § 6901 et seq 
               
               
                   
               
               
                 Acronyms: 
               
               
                 ACHP - Advisory Council on Historic Preservation 
               
               
                 BCDC - San Francisco Bay Conservation and Development Commission 
               
               
                 CCC - California Coastal Commission 
               
               
                 CDFW - California Department of Fish and Wildlife 
               
               
                 CEQ - Council on Environmental Quality 
               
               
                 EPA - Environmental Protection Agency 
               
               
                 NMFS - National Marine Fisheries Service 
               
               
                 NOAA - National Oceanic &amp; Atmospheric Administration 
               
               
                 OCRM - Office of Ocean &amp; Coastal Resource Management 
               
               
                 OPR - Office of Planning and Research 
               
               
                 RWQCB - Regional Water Quality Control Board 
               
               
                 SCH - State Clearinghouse 
               
               
                 SHPO - State Historic Preservation Officer 
               
               
                 SWRCB - State Water Resources Control Board 
               
               
                 USACE - U.S. Army Corps of Engineers 
               
               
                 USFWS - U.S. Fish and Wildlife Service 
               
            
           
         
       
     
     As discussed above, the advantages of the present embodiments are numerous. Propulsor occlusion device embodiments are provided that can slow and/or incapacitate a marine vessel without harming or destroying the vessel&#39;s propulsion system and without seriously injuring any of the occupants of the vessel. The exemplary compositions have been shown to be an effective non-lethal means of stopping or slowing a vessel. The propulsor occlusion devices can be deployed safely by a diver, a seagoing vessel or an aircraft well before a chase ensues. Moreover, the deployed materials may be safely left in the water for extended periods of time, as they comprise GRAS materials that dissolve and/or biodegrade with a relatively short time period. 
     The effectiveness of the materials has been shown to increase by incorporating one or more superabsorbent materials (e.g., SAPs and SAFs). Moreover, the adhesiveness has been shown to increase when combining SAPs with PVA polymer. Such materials were shown to gel quickly and dissolve more slowly. 
     The exemplary embodiments can relate to one or more propulsor occlusion devices for performing one or more of the functions described herein. This device(s) may be specially constructed for the required purpose. Other exemplary embodiments can relate to one or more components that make up the propulsor occlusion device, such as a single fabric or a number of fabrics in combination. 
     The embodiments described and claimed herein is not to be limited in scope by the specific examples herein disclosed since these examples are intended as illustrations of several aspects of the embodiments. Any equivalent examples are intended to be within the scope of the embodiments. Indeed, various modifications of the embodiments in addition to those shown and described herein will become apparent to those skilled in the art from the foregoing description. Such modifications are also intended to fall within the scope of the appended claims. All references including patents, patent applications and publications cited herein are incorporated herein by reference in their entirety and for all purposes to the same extent as if each individual publication or patent or patent application was specifically and individually indicated to be incorporated by reference in its entirety for all purposes.