Patent Publication Number: US-8118934-B2

Title: Non-polar III-V nitride material and production method

Description:
FIELD OF THE INVENTION 
     The present invention is directed to methods of producing non-polar III nitride materials having both low defects density and low stress, and more particularly to a method utilizing a fabricated nano-pores and nano-network compliant layer with an HVPE, MOCVD, and integrated HVPE/MOCVD growth process. 
     BACKGROUND OF THE INVENTION 
     Wide band-gap III-V nitride materials are recognized to be among the most attractive compound semiconductors for use in a variety of devices. They are suitable for optoelectronic and microelectronic devices that operate in a wide spectral range, from visible to ultraviolet, and in the high temperature/high power applications area. The main advantage of nitride semiconductors in comparison with other wide-band-gap semiconductors is their low propensity to degrade at high temperature and high power when used for optical and microelectronic devices. 
     Current commercial nitride semiconductor products are typically based on c-axis polar III-V nitride materials. In c-axis-oriented hexagonal III-V nitride material, the spontaneous and strain-induced piezoelectric polarizations produce strong electric fields which result in band bending of the quantum wells and spatial separation of electrons and holes. Moreover, these properties remain even at the high carrier densities required for laser operation, as has been previously described in the art. (See, e.g., I. H. Brown et al, IEEE J. Quant. Elec. 42 1202, 2006). Consequently, when using these conventional materials the radiative recombination time increases at the expense of quantum efficiency and a red-shift of the emission occurs. Accordingly, non-polar III-Nitride materials, where these polarization fields and the resulting band bending are absent, would open up the possibility of fabricating high efficiency and high power UV-visible light emitters. 
     Epitaxial lateral overgrowth techniques (“ELOG”) and its modifications, such as facet initiated epitaxial lateral overgrowth (“FIELO”) and Pendeo (from the Latin to hang or be suspended) are the most widely used approaches employed for suppressing bending and the threading dislocations associated with these materials. Indeed, laterally overgrowing oxide (or metal) strips deposited on initially-grown GaN films has been shown to achieve about two orders of magnitude reduction in dislocation density, reducing it to the 10 7  cm −2  level. However, the low defect-density material only occurs in the wing region, located in the coalescence front, and represents only approximately one fifth of the whole wafer surface area. Large coalescence front tilting and tensile stress are both present in the overgrowth region. The same ELOG and Pendeo methods could also be used to reduce the defect density in non-polar GaN (on a- or m-plane), although the wing tilt resulting from the different growth rates of the Ga-polar and N-polar wing in these materials introduces further complexity at the coalescence boundaries. 
     Low defect-density free-standing c-axis polar GaN is currently one of the materials of choice to achieve the desired specification for optoelectronic and microelectronic devices. However, the use of non-polar III nitride materials for semiconductor devices such as high current density drive light-emitting diodes (LEDs) and laser diodes (LDs) may disrupt the current trend for polar materials. Bulk (melt or sublimation) and hydride vapour phase epitaxy (HVPE) are the two main techniques for growing free-standing and low defect-density c-axis polar and non-polar III nitride semiconductor materials. Bulk GaN growth techniques operating at a very high pressure of ˜15 kbar have been successful in growing low dislocation density (&lt;107 cm-2) material. Unfortunately, this technology suffers from a low growth rate and is limited to small diameter substrates, making these materials very expensive and uneconomic for commercial manufacturing. 
     HVPE is a reversible equilibrium-based hot-wall process with several advantages, including, high growth rate of up to about 400 μm/hr—more than 100 times faster than that of the metalorganic chemical vapour deposition (MOCVD) and molecular beam epitaxy (MBE) methods, low running costs, and lower defect densities in thick GaN as the result of the mutual annihilation of mixed dislocations. However, the HVPE technique still has the same inherent problems as other growth techniques due to its growth on foreign substrates. Therefore, the growth of thick GaN using HVPE in general has to overcome two critical issues, firstly, to reduce the bending and cracking of initial GaN thick films (30-100 μm) on foreign substrates, and secondly, to minimize the defect density of GaN. 
     To reduce defect density (mainly threading dislocations) and strain, and to improve the surface morphology of the thick GaN films grown by HVPE, various techniques have been employed. For example, ELOG growth under lower reactor pressure and growth with TiN intermediate layers, porous Si x N y  layers, AlN/GaN superlattices, III nitride semiconductor nanopillars, or deep inverse pyramid etch pits on weakened Si, GaAs and other III-V single crystal wafers have all been used to try and address surface morphology. Various defects reduction methods using defects filter layers, porous interlayers and III nitride semiconductor nanopillars are described in U.S. Pat. Nos. 6,835,246; 6,596,377 and 6,844,569, as well as US Patent Publication Nos. 2004/0157358, 2006/0270201, 2003/0006211, 2002/0111044, 2004/0123796, 2004/0251519 and 2001/0055881. Additional exemplary disclosures may be found in foreign patent publication Nos. JP 2005136106, WO 02/44444, EP 1246233, and EP 1422748, as well as the following non-patent literature R. F. Davis et al, ‘Review of Pendeo-Epitaxial Growth and Characterization of Thin Films of GaN and AlGaN Alloys on 6H—SiC(0001) and Si(111) Substrates’, MRS Internet J. Nitride Semicond. Res. 6, 14, 1(2001); K. Kusakabe, A. Kikuchi, and K. Kishino, ‘Overgrowth of GaN layer on GaN nano-columns by RF-molecular beam epitaxy’, J. Crystl. Growth, 237-239, 988 (2002); C. C. Mitchell et at., ‘Mass transport in the epitaxial lateral overgrowth of gallium nitride’, J. Cryst. Growth., 222, 144 (2001); K. Hiramatsu., ‘Epitaxial lateral overgrowth techniques used in III-V nitride epitaxy’, J. Phys: Condens, Matter., 13, 6961 (2001) and R. P. Strittmatter, ‘Development of micro-electromechanical systems in GaN’, PhD Thesis, California Institute of Technology, P. 92 (2003). The disclosure of each of these references is incorporated herein by reference. 
     However, growth processes using these techniques are tedious, time consuming and expensive. Moreover, the GaN produced using such techniques still has the major disadvantage of being subject to bending and undesired residual strain. Accordingly, improved methods of producing non-polar III nitride materials having both low defect density and low stress are needed. 
     SUMMARY OF THE INVENTION 
     In one embodiment, the current invention is directed to method of producing non-polar III nitride materials having both low defect density and low stress. 
     In another embodiment, a combination of dry and wet etching is conducted to create nano-networks surrounding nano-pores consisting of layers of non-polar III nitride material and the substrate used to grow the non-polar III-V nitride materials. In such an embodiment, the nano-networks comprise a sacrificial layer of a mechanically weakened structure, or a structure with much higher photon absorption in certain selective wavelength, or a structure that can be selectively etched off by wet chemical, electrochemical or photochemical etching. 
     In still another embodiment, non-polar III-V nitride materials and/or devices are then deposited on the nano-networks surrounding the nano-pores by hydride vapour phase epitaxy (HVPE) and MOVPE (or MOCVD) methods. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       Specific embodiments of the invention will now be described with reference to the accompanying drawings, in which: 
         FIG. 1  shows a planar view of an anodic porous alumina pattern on top of a III-nitrides template; 
         FIG. 2  shows a cross-sectional view of etched nano-pores and nano-networks consisting of GaN (500 nm) and substrate; 
         FIGS. 3   a - b  schematically show the top view ( FIG. 3   a ) and cross-sectional view ( FIG. 3   b ) of a template including nano-pores and nano-networks; and 
         FIG. 4  schematically shows the effect of the initial nano-pendeo and further epitaxial growth processes on a template of a-GaN nano-networks and nano-pores. 
     
    
    
     To illustrate the invention more clearly, the following detailed description and various practical examples using techniques in accordance with the methods of the present invention are described below. 
     DETAILED DESCRIPTION OF THE INVENTION 
     The present invention provides a method suitable for growing flat, low defect density, and strain-free thick non-polar III-V nitride materials and devices on any suitable foreign substrates using a fabricated nano-pores and nano-network compliant layer with an HVPE, MOCVD, and integrated HVPE/MOCVD growth process in a manner that minimum growth will occur in the nano-pores. The key characteristic of the nano-networks of the current invention is that the network is continuous along the surface of the template. It should be understood that in the current invention the nano-networks comprise the non-polar III-V nitride material and the substrate used to grow it, and that the nano-pores can be of any shape, for example square, circular, triangular and polygonal. The use of fabricated nano-networks comprising the non-polar III-V nitride material layers and substrate, for example as the compliant layer, to grow thick non-polar GaN has several advantages. 
     First, using the method of the current invention the stress and dislocations of the material are mostly localized in the interface among the nano-network and the top lateral grown layer. As a result, growth leads to the top lateral overgrowth layer being nearly free of stress and dislocations. In addition, the topography of nano-pores with a narrow diameter permits coalescence with a very thin overgrown layer, specifically, typically only ˜0.2 m thickness is required for continuous overgrown GaN layers. This narrow air nano-pore also facilitates very fast coalescence to form continuous non-polar AlGaN by the epitaxial lateral overgrowth of AGalN onto these nano-pores. 
     With all the advantages described above, high-quality thick non-polar GaN can be grown on this fabricated nano-pore and nano-network compliant layer that has very little tilting in the coalesced front either on top of the nano-pores and nano-networks in comparison with materials made in accordance with other ELOG or Pendeo processes. 
     Non-polar GaN wafer bending due to the thermal expansion coefficient difference between the GaN and the substrate is also minimized by the balanced dimensions of the nano-pores and nano-networks, which functions to decouple and to relax the biaxial strain. Thick and flat non-polar GaN films can therefore be grown using this technique, including so-called non-polar GaN “boules”, which may be sufficiently thick to be sliced into multiple wafers. 
     Localized stress between the nano-network and top lateral overgrown layer also allows the thick non-polar GaN to be readily separated from the substrate during the rapid cooling, particularly if a tensile-stressed thin sacrificial layer is included in the fabricated nano-network, or is grown on top of the nano-networks. An anodic electrochemical selective etch process for non-polar p-GaN can also be used to separate the non-polar GaN film from the substrate. The thick non-polar GaN, i.e., a boule, may then undergo slicing, grinding, lapping, and polishing processes as appropriate to produce standard thickness (˜350-500 m) non-polar GaN wafers in a process designed to produce commercial quantities. A non-polar III-V nitride wafer produced in this way may be used as the seed for a further process in accordance with the present invention. 
     In accordance with the current invention the nano-pores and nano-networks may be fabricated using a template with a non-polar III-V nitride layer that may be grown by MBE, MOCVD (such as metalorganic vapour phase epitaxy (MOVPE)), HVPE, or any other semiconductor growth methods onto a suitable substrate. Various vapour deposition methods suitable for growing GaN materials are described in U.S. Pat. Nos. 6,413,627; 5,980,632; 6,673,149; 6,616,757; 4,574,093 and 6,657,232, the disclosures of which are incorporated herein by reference. 
     The template can be made of a simple layer, of a heterostructure, or of superlattices consisting of non-polar n- and p-type doped and un-doped III-V nitride material such as non-polar In x Ga y Al 1-x-y N, where 0≦x≦1, 0≦y≦1, and 0≦x+y≦1. The total thickness of the grown non-polar III-V nitride layers in the template is preferably less than 3 μm. The thinner non-polar III-V nitride layers in the template will facilitate the lateral growth with less mass transport for the vertical downward growth. Examples of such templates can be substrate/AlN (˜20 nm)/GaN (0.1-1 μm), substrate/AlN (˜20 nm)/AlGaN (0.5 μm)/GaN (10-100 nm), substrate/GaN (100 nm)/GaN (300 nm), substrate/GaN/(AlGaN 2.5-10 nm/AlN 2.5-10 nm superlattices)/GaN (10-100 nm), substrate/GaN/(InGaN 2.5-10 nm/GaN 2.5-10 nm superlattices)/GaN (10-100 nm), substrate/Si 3 N 4 /AlN (˜20 nm)/GaN (1-3 μm)/p-GaN (10-100 nm). 
     In such embodiments of the invention, the dielectric material such as SiO 2  or Si 3 N 4 , which can be deposited by sputtering, e-beam evaporation, and plasma-enhanced chemical vapour deposition (PECVD), will serve as the mask, with the replicated pattern from the nanomasks produced by the above mentioned technologies. The thickness of the dielectric Layer depends on the etching selectivity between the dielectric materials and the semiconductor layer(s). 
     Dry etching of the non-polar III-V nitride layer(s) may be carried out by reactive ion etching (RIE) or inductively coupled plasma etching (ICP) using Ar, Cl 2 , BCl 3 , or H 2  gas mixtures. The preferred etch depth is to etch down to remove part of the substrate. Further wet etching using different acids and bases allows for the fine tuning of the nano-pore and nano-network dimensions. 
     In situ or ex situ nitridation or oxidation of the nano-networks can also be performed to reduce the coalescence of the nano-networks during lateral overgrowth, to consequently maintain the integrity of the nano-pores for decoupling the thermal expansion difference between the substrate and the lateral overgrown layer. 
     The fabricated non-polar III-Nitrides nano-pore and nano-network templates can be loaded for the initial thin continuous non-polar GaN nano-pendeo growth using MBE, MOCVD or HVPE. The thus-prepared templates can then be loaded for the thick non-polar thick GaN growth using HVPE. 
     The separation of the grown non-polar GaN can be achieved by the following methods. In brittle materials such as sapphire and III-V nitrides, cracking may occur easily when the stress exceeds a critical value. The fabricated III-nitrides nano-pores and nano-networks with their high aspect ratio and nano-dimensions, will facilitate the cracking mechanism between the substrate and the top thick GaN due to the large difference of the thermal expansion coefficient, particularly when rapid cooling is carried out after the growth. A further mechanical twisting will push the local stress to exceed the critical value to separate the thick film. Another method of separating the non-polar GaN from the substrate is to use anodic electrochemical etching. In this case, a thin p-GaN layer is deposited at the top of the non-polar III-V nitride layers. Nano-networks with a p-GaN tip may be fabricated by the etching processes. Using a suitable electrolyte and bias voltage results in p-GaN being selectively etched off, to leave the thick top GaN (undoped or n-doped) untouched. Wet chemical etching using H 3 PO 4  or KOH at high temperature is also very effective in etching off the AlN (especially amorphous AlN), HCl is effective in etching off (100) LiAlO 2 . 
     Although the method in accordance with the present invention has been described generally above, turning to the details of the process in one embodiment the method in accordance with the present invention generally comprises the steps of:
         (a) providing a template material comprising at least one layer of non-polar III-V nitride semiconductor material;   (b) creating a mask on top of the template material; and   (c) using the mask to form at least one nano-pore and one nano-network in the template material; and optionally   (d) growing non-polar III-V nitride semiconductor material onto the nano-pores and nano-networks.       

     Regarding step (a), the template material may be selected from the group consisting of non-polar (m-, or a-plane), p-type doped, n-type doped or undoped III-V nitride compounds. The III-V material layer may comprise a simple layer, multiple layers, a heterostructure, or superlattices of the non-polar III-V nitride compound. The semiconductor layer may comprise one of non-polar In x Ga y Al 1-x-y N, where 0≦x≦1, 0≦y≦1, and 0≦x+y≦1. In turn, the layer structure of the template can be made of a simple layer, multiple layers, of a heterostructure, or of superlattices consisting of non-polar n- and p-type doped and un-doped semiconductors such as AlxGayIn1-x-y N with 1≧x≧0, 1≧y≧0. In a preferred embodiment, the template material may comprise a sacrificial layer of non-polar p-GaN. 
     In one embodiment, the template non-polar III-V nitride semiconductor layer is formed by deposition onto a substrate by epitaxial growth methods. In such an embodiment, the total thickness of the grown non-polar III-V nitride layers is preferably less than 3 μm. Examples of such templates can be substrate/amorphous AlN (˜20 to 500 nm)/GaN (50-100 nm), substrate/AlN (˜20 nm)/AlGaN (˜0.5 μm)/InGaN (10-100 nm)/GaN (10-100 nm), substrate/GaN/p-GaN (10-100 nm)/n-GaN (10-100 nm). The thinner the non-polar III-V nitride material in the template, the faster lateral coalescence will occur during the growth of top non-polar III-V nitride material on the nano-networks. 
     In another embodiment the substrate may comprise a material selected from the group consisting of r-plane sapphire, m-plane silicon carbide, LiAlO 2  (100), or other suitable substrates for non-polar III-V nitride materials growth. Alternatively, the substrate may comprise a material selected from the group consisting of non-polar III-V nitride undoped, n-type or p-type materials. 
     In step (b), the mask or nano-mask may be created using any available mask-making technology, for example one of anodic porous alumina, e-Beam lithography, interferometry, holography, photolithography or a nano-imprint method. The mask pattern may be random or predetermined, which will depend on the mask fabrication process used, as outlined below, to achieve desired physical or chemical properties. For example, the mask may be created by depositing a layer of dielectric material onto the template material, e.g., either a semiconductor layer or the substrate. The mask may also be formed by imprinting onto the dielectric material using a nano-imprint method. Alternatively, a layer of metal may be applied onto the layer of dielectric material. In this case, the mask may be formed by removing regions of the metal layer. 
     In step (c), the nano-pores may be formed by etching the template material, which may be by wet, dry or combined wet and dry etching. The etching is preferably used to remove part of the substrate. In other words, in such an embodiment the depth of etching extends below the upper surface of the substrate. After etching, any remaining metal and/or dielectric material on the nano-networks may be removed. In a preferred embodiment, the method includes subjecting the nano-networks to a nitridation or oxidation process, which may be either in-situ or ex-situ. 
     Regardless of the technique used, the nano-network is preferably continuous in the template. The nano-pores may comprise a shape selected from the group consisting of circular, square, rectangular, triangular, trapezoidal, and other polygons. 
     Preferably each of the nano-networks may comprise one sacrificial layer of a mechanically weakened structure, a structure comprising a high photon absorption material in certain selective wavelength, or a structure comprising a less chemically resistant material that can either be one of the layers of non-polar III-V nitride material or the insulating or material used to grow the non-polar III-V nitride material. In the example of m-plane nitride grown on (100) LiAlO2, the LiAlO2 can be readily etched by HCl solution and thinned down with the wall thickness of the nano-networks much thinner that of top grown m-plane nitride layers. This mechanically weakened LiAlO2 sacrificial layer in the substrate can be used to separate the top grown m-plane non-polar materials from the substrate very easily by rapid cooling or mechanical twisting. In the example of γ-plane Sapphire, the top grown non-polar a-plane III-V nitride may contain an InGaN layer, which will strongly absorb the photon of wavelength shorter than 360 nm due to smaller band-gap. Therefore, laser ablation using laser of wavelength shorter than 360 nm will be strongly absorbed by this sacrificial layer, resulting in decomposition into In and Ga metal droplets, which can be easily separated from the substrate. 
     Step (d) may comprise laterally growing an initial layer of non-polar III-V nitride material by nano-pendeo on the nano-networks, then vertically growing the non-polar III-V nitride material onto the initial layer. The lateral growth of non-polar III-V nitride material may be carried out by a MOCVD, a MBE, or an HVPE method. The lateral growth may comprise combined low temperature (100-500° C.) and high temperature growth processes (700-1400° C.). Alternatively, the lateral growth of non-polar III-V nitride material may be carried out by an integrated pulsed growth and normal method. The vertical growth of non-polar III-V nitride material may be carried out by an HVPE method. The non-polar III-V nitride material in step (d) may be undoped, or n- or p-type doped. 
     In a preferred embodiment, in step (d), the growth of non-polar III-V nitride material is performed while rotating and maintaining the distance between the surface of the template and gas outlets in a growth chamber. 
     Although not explicitly set forth above, it should be understood that the non-polar III-V nitride material grown in step (d) may comprise a different material from the nano-networks. 
     Although not explicitly set forth in the process outline provided above, it should be understood that the method of the current invention may also include the step of forming at least one semiconductor device onto the non-polar III-V nitride material. Such devices may comprise, for example, light emitting diodes (LEDs), laser diodes (LDs), and photodiodes (PDs). The non-polar III-V nitride material may be bonded to a sub-mount with good thermal management property, such as good thermal conductivity. In such an embodiment, an n-contact may then be deposited on the non-polar n-GaN for the devices. 
     The method may further comprise the step of separating the non-polar III-V nitride material from the substrate. The non-polar III-V nitride material may be separated from the substrate through the sacrificial layer of the nano-networks by rapidly cooling the material, or by mechanical separation, photochemical etching, wet etching, electrochemical etching or laser ablation. In the case of laser ablation, the laser may be directed toward the substrate-material interface from the side of the substrate. 
     In addition, the method may further comprise the step of slicing, grinding, lapping and/or polishing the non-polar III-V nitride material to a predetermined thickness. The grown non-polar III-V nitride material may be sliced to produce a non-polar III-V nitride material layer of pre-selected thickness. The non-polar III-V nitride wafer produced in such manner can be used as the seed material for the further growth of thick non-polar III-V nitride material. 
     Although the above method is described for use in forming non-polar III-V nitride materials and devices using a provided template, it should be understood that the template material may comprise a material previously produced by the method. Likewise, the non-polar III-V nitride semiconductor nano-networks may be formed by a method according to the first aspect. Finally, a non-polar III-V nitride single-crystal material grown using the method according to the first aspect. 
     Turning now to the details of step (b), as described above, the mask (also termed a “nano-mask” due to the dimensions involved) can be produced by a metal annealing method, the anodic porous alumina interferometry method, e-Beam lithography, interferometry, holography, photolithography, nano-imprint or any other suitable method. As also described above, the pattern of nano-pores formed may either by random or pre-determined depending on the process employed. For example, the anodic alumina method may produce both random and determined hexagonal patterns depending on the stress of the processes used, e.g. whether or not a pre-indentation mark is used. Anodic porous alumina nano-mask fabrication processes involve:
         (a) depositing dielectric materials onto the template material, the template material for example comprising a non-polar III-V nitride material layer structure;   (b) depositing thin Al onto the dielectric layer;   (c) anodizing the Al under controlled electrolyte, temperature and voltage to form high density anodic porous alumina nano-masks;   (f) dry and wet etching the materials using the anodic alumina and dielectric nano-masks to form a high density of nano-pores and nano-networks.       

     Finally, photolithography, interferometry and nano-imprinting can all also produce custom patterns. Nano-imprint nano-mask fabrication processes involve:
         (a) depositing dielectric materials onto the template material, the template material for example comprising a non-polar III-V nitride material layer structure;   (b) nano-imprinting and developing the nano-holes masks onto the dielectric materials;   (c) dry and wet etching the dielectric materials using metal nano-masks;   (d) dry and wet etching the materials using the metal and dielectric nano-masks to form a high density of nano-pores and nano-networks.       

     In nano-imprint nano-mask fabrication technology, the “master” mask can be produced by methods such as interferometry, E-beam lithography, sub-micrometer photolithography, or x-ray lithography. The mask pattern can be custom-designed to consist of a photonic crystal structure, high symmetry photonic quasicrystal, gratings, and any other patterns for desired optical effects. 
     In all of the above embodiments, the substrate may comprise a material selected from the group consisting of r-plane sapphire, m-plane silicon carbide, LiAlO 2  (100), or other suitable substrates for non-polar III-V nitride materials growth. In some cases, the template may comprise a semiconductor material substrate only, i.e., without any semiconductor layer grown on top of the substrate. In such cases, the mask is fabricated directly onto the substrate. 
     A dielectric material such as SiO 2  or Si 3 N 4 , which can be deposited by sputtering, e-beam evaporation or plasma-enhanced chemical vapour deposition (PECVD), may serve as the mask with the replicated pattern from the nano-masks produced by the above-mentioned technologies. The thickness of the dielectric layer depends on the etching selectivity between the dielectric materials and the III-V nitride material layers to be etched. 
     The nano-pores and nano-networks thus fabricated preferably have an aspect ratio (i.e., average diameter of the nano-pores versus the average wall thickness of the nano-networks) much larger than one. The etching process preferably etches the non-polar III-V nitride material layers off until the desired thickness of the substrate is also etched. Therefore, the nano-networks comprise both the non-polar III-V nitride material and the substrate used to grow non-polar III-V nitride material. The nano-networks preferably include a sacrificial layer, which may be, for example, mechanically weakened, or a material with much higher photon absorption in certain selective wavelength, or which can be selectively etched off by wet chemical, electrochemical and photochemical etching. 
     The air nano-pores may have different shapes such as circular, square, rectangular, triangular, trapezoidal, and other polygons. The dimension of the nano-pores can be modified by further wet etching. Such treatment allows the fine tuning of the diameter of the nano-pores and nano-networks for optimized lateral overgrowth and ready separation of such grown thick freestanding non-polar III-V nitride materials from the substrate. 
     A further ex-situ or in-situ nitridation can prevent the coalescence of the nano-networks in the root, hence maximizing the decoupling mechanism of the nano-pores and nano-networks to reduce the defect density and cracks of the top lateral-grown thick layers. One example of the layer structure of the nano-networks comprises layers such as (100) LiAlO 2 /amorphous GaN (˜50-100 nm)/n-Al 0.06 GaN 0.94 (˜10 nm)/n-GaN (300 nm). The nano-pores may then be fabricated by etching down to expose about 600 nm (100) LiAlO 2 . Further wet etching using HCl will weaken the (100) LiAlO 2  by reducing its diameter. A PECVD nitridation process may then be used to deposit Si 3 N 4  onto the nano-pores helps to prevent the lateral growth of GaN at the bottom of the nano-pores. The integrity of the voids between the nano-networks facilitates the formation of low stress and low defect density top layers during the subsequent lateral epitaxial growth. The continuous nano-networks facilitate the surface diffusion of GaN, and hence enhance the lateral growth with minimum growth in the bottom of the nano-pores. 
     EXAMPLES 
     A general exemplary method in accordance with the invention utilizes HVPE to grow high quality flat and thick non-polar III-V nitride material onto foreign substrates using nano-network compliant layers. Examples of suitable nano-pores include nano-pores of different shapes, for example circular, square, triangular, or other polygons which have varying diameter along their major dimensions. Nano-pores and nano-networks of non-polar III-V nitride materials can be fabricated on any foreign substrates with the initial non-polar III-V nitride layers grown by MBE, CVD, MOCVD (MOVPE) or HVPE methods. Such nano-pores may typically have a diameter of about 20 to 500 nm. Further growth of continuous non-polar III-V nitride thick films or wafer can be achieved by epitaxial lateral overgrowth using MOCVD or HVPE. Compound semiconductor thick film and wafer bending due to the lattice mismatch and the thermal expansion coefficient difference between the compound materials and the substrate can be minimized by a balanced dimension of the air nano-pores and nano-networks, which functions to decouple the impact of the substrate. Thick and flat freestanding non-polar III-V nitride materials can therefore be grown using this technique. 
     Nano-pendeo lateral overgrowth using these nano-pores and nano-networks will minimize the defects on the top non-polar III-V nitride thick film through the defects bending mechanism in the interface of nano-networks and lateral grown layer. The small dimension of the nano-pores will also minimize the facet tilt in the grain boundary of lateral overgrown layer. The controlled dimension of the nano-pores and the nano-networks and the localized stress between the nano-networks and lateral-grown layer also allows the thick non-polar III-V nitride material, for example a-GaN, to be readily separated from the substrate during rapid cooling. An anodic electrochemical selective etch process for non-polar p-GaN can also be used to separate the non-polar GaN film from the substrate when the etched nano-pores include a thin non-polar p-GaN top layer. The thick non-polar GaN may then undergo slicing, grinding, lapping and polishing processes to produce non-polar III-V nitride wafers. Such produced non-polar GaN can be used as the seed for further growth of thick freestanding non-polar GaN because of the uniform crystal orientation from the centre to the edge of the wafer and low defect density. Hence the method can provide a very economical mass production technology for freestanding non-polar III-V nitride materials. 
     Although the growth of specific materials will be described below, it should be understood that the growth processes provided by the invention can be applied to the entire family of III-V nitride compounds, generally of the formula In x Ga y Al 1-x-y N, where 0≦x≦1, 0≦y≦1, and 0≦x+y≦1. Throughout the following description, the invention is described using GaN as an example of a non-polar epitaxial III-V nitride layer as the material for convenience, though any suitable non-polar III-V nitride material may be used. For example, the same growth method described above can also be applied to the growth of other non-polar III-V nitride materials. For example, thick, flat, and low defect non-polar AlN and AlGaN can be grown using AlCl 3  and GaCl precursors formed by passing HCl through Al and Ga. Non-polar AlN is very difficult to coalesce under normal ELOG growth technique, but using a nano-column compliant layer with nano-size air-gap in accordance with the present invention will facilitate the very fast coalescence for non-polar AlN and AlGaN. AlN is also very difficult to coalesce under normal ELOG growth technique, but using a nano-pore and nano-network compliant layer with nano-size nano-pores in accordance with the present invention will facilitate the very fast coalescence for non-polar AlN and AlGaN. 
     Example 1 
     A γ-plane-oriented sapphire substrate of about 2 inches (5.08 cm) in diameter with MOCVD-deposited a-plane AlN (20 nm) and GaN of about 0.6 μm is loaded onto the substrate holder of a HVPE vertical reactor. Before loading, the a-plane GaN template is degreased in KOH for a few seconds, rinsed in deionized water, etched in a H 2 SO 4 /H 3 PO 4 =3:1 solution at 80° C. for a few minutes, then rinsed in deionized water. It is then necessary to create a mask onto the template. Firstly, a thin dielectric layer of SiO 2  or Si 3 N 4  of ˜200 nm is deposited by PECVD onto the GaN template. Then a thin Al metal of about 60-200 nm is deposited by e-beam evaporation or sputtering onto the dielectric layer. A two step anodization process is used. A first anodization is conducted under 0.3 M oxalic acid solution at 5° C. with current ˜100 mA and 20 V for about 6 hours to form a layer of oxide (alumina) on top of the aluminum layer. The surface texture of the aluminum is changed by the anodization process to produce concavities. Then the oxide is removed by a mixture of about 6 wt % H 3 PO 4  and 1.8 wt % H 2 CrO 4  at about 60° C. for 1-1.5 hours. A second anodization is conducted under the same oxalic solution at ˜100 mA and 40 V for about 5 hours. The second anodization is required to create a more uniform nano-mask pattern. Trace aluminum may then be removed from the alumina layer. 5 wt % H 3 PO 4  is used to smooth and enlarge the pores of the anodic porous alumina.  FIG. 1  shows the anodic porous alumina pattern on top of the template following the two step anodization process. The dimension for the pores and watts is of 74 nm and 32 nm respectively. The next stage is to create the nano-pores with the continuous non-polar a-GaN network. Reactive ion etching (RIE) using Ar and CHF 3  is used to etch the dielectric materials using the alumina mask. Then ICP etching using a gas mixture of Ar, H 2 , Cl 2 , or BCl 3  is carried out to etch a-plane GaN materials and sapphire substrate using the alumina and dielectric nano-mask to form a high density of nano-pores, as shown in  FIG. 2 . An aspect ratio (diameter of the nano-pores versus the thickness of the wall of the nano-networks) of more than one can be seen on the structure. 
     Residual anodic alumina are removed using phosphoric acid. Residual dielectric materials of SiO 2  or Si 3 N 4  are removed by buffered oxide etch solution and phosphoric acid respectively. Further wet etching using KOH is used to fine tune the dimension of the nano-pores. 
     An ex-situ nitridation process is carried out using PECVD with silane and NH 3  gas. The nitridated surface has an anti-surfactant effect which inhibits the lateral growth of a-plane GaN. Using nitridation on nano-pores therefore prevents quick coalescence in the root of the nano-pores, which would destroy the de-coupling mechanism possible by using nano-pores. The tip of the nitridated nano-pores is slightly etched off by RIE, as illustrated by  FIG. 3 . 
     The initial epitaxial lateral overgrowth is carried out by the MOCVD growth process. The nitridated a-plane GaN nanocolumn template is loaded into the reactor. The substrate temperature is then raised to about 1020° C. with the NH 3  flow of about 2000 sccm and Trimethylgallium (TMG) flow to about 5 sccm. After about 60 minutes growth, the TMG flow is set to about 10 sccm for about 20 minutes&#39; growth, then to about 20 sccm for about 30 minutes&#39; growth. The continuous a-plane GaN is fully coalesced within about the first 60 minutes. 
     The nano-pendeo grown a-plane GaN template is then loaded into the HVPE reactor for the bulk a-plane GaN growth. The gas heater is heated to temperature of about 500° C. The pressure of the growth chamber is maintained at about 200 mbar. N 2  is introduced through all gas injectors for about 30 minutes to purge the reactor. The nano-pendeo a-plane GaN templates is heated to about 350° C. NH 3  flow at about 1000 sccm is introduced into the chamber. The GaCl gas precursor is produced by passing about 10% HCl in N 2  through a Ga bubbler heated to about 800° C. The conversion rate is nearly 100% for GaCl. Then the template is heated to a temperature of about 1050° C. The pressure of the growth chamber is raised to about 300 mbar. Gas delivery to the growth chamber is set as follows for the growth process: NH 3  flow at about 2500 sccm, GaCl flow at about 60 sccm and N 2  and H 2  to make the rest of the gas. A steady total gas flow of about 3500 sccm is maintained throughout the whole growth process. The growth continues until a GaN epitaxial layer of sufficient thickness is produced. During the growth, the template is rotated to maintain the substantially constant distance between the gas outlets and the surface of the bulk a-plane GaN. For a growth with the V/III ratio set between 10 and 40 in the vertical HVPE reactor, a growth rate of between about 20160 m/hour can be achieved. Uniformity of the growth without the aided rotation is better than 2% from edge to edge in a 2 inch (5.08 cm) wafer. 
     In the nitride growth termination, GaCl gas is switched off, the flow of NH 3  is maintained at the same level and N 2  flow is increased to make up the steady total gas flow. The substrate cool-down is very fast at the first stage between 1050° C. and 500° C. The flow of NH 3  is then switched off below the temperature of 500° C. The cool-down continues with a rate faster than 100° C./min between 500° C. and room temperature. During this time, the gas heater maintains the temperature at about 150° C. and the substrate is lowered down from the chamber to obtain fast cooling-down. Following the conclusion of the growth processes, a structure is obtained as shown in  FIG. 4 . 
     Once the substrate is cooled and removed from the reactor, the γ-sapphire substrate can be seen totally or partially separated from the thick a-plane GaN epitaxial layer. A further mechanical twist is sufficient to separate the partially separated a-GaN layer. 
     Example 2 
     Here, the initial MOCVD epitaxial lateral overgrowth process described in Example 1 is replaced by a combined pulsed and normal MOCVD growth method. In this method, the flow sequence of reagent gases is on (NH 3  and TMG on) and off (TMG on and NH 3  off) in turn for the enhanced lateral growth mode. The time for the on and off period is set to be around 20-60 seconds and 10-15 seconds respectively. The a-plane n-GaN growth step is continued until a continuous a-plane n-GaN epitaxial layer is produced. Then a full non-polar LED device structure is grown on top of the a-plane GaN. Then a Ni (10 nm)/Au(10 nm) contact is deposited, annealed in O2 at 550° C. for 1 minute. Ti/Al/Ti/Au with Al as the reflector is then deposited on top of the Ni/Au contact. The non-polar device is then solder bonded to a submount for good thermal management. The submount may comprise SiC, CVD diamond, AlN, metals, alloys or Silicon. The substrate/template is then removed as before. 
     Example 3 
     In this Example, the thick non-polar m-plane n-GaN is grown on the nano-pores and nano-networks template, wherein the nano-network surrounding the nano-pores comprises non-polar m-plane GaN, AlN, and (100) LiAlO 2 . (100) LiAlO 2  is weakened by further wet etching using diluted HCl. The thick m-plane n-GaN is separated from the substrate through the mechanical cracking of the weakened (100) LiAlO 2  nano-networks. 
     Example 4 
     Similarly to Example 1, the initial epitaxial lateral overgrowth is carried out by a MOCVD growth process. The a-plane III-V nitride material in the template includes a InGaN sacrificial layer for laser ablation separation. Epitaxial growth of the full device is then conducted to grow wide quantum well green LEDs. In this case an LED epitaxial growth is continued in the MOCVD reactor. The LED structure grown comprises the following layers: an n-type Si-doped a-AlGaN layer (about 1.5-2 μm), a InxGa1-xN barrier/InyGa1-yaN MQW active region (about 80 Å/80 Å, 2-6 pairs, and x˜0.03, and y≧x+0.25), an AlGaN:Mg capping layer (˜200 Å), and p-type Mg-doped GaN (about 0.2-0.3 μm). The electron and hole concentration in the GaN:Si and GaN:Mg layers are about 10 18  cm −3  and 6×10 17  cm −3  respectively produced are suitable for producing light of UV region wavelength. 
     SUMMARY 
     It will be apparent to those skilled in the art that a wide range of methods and process parameters can be accommodated within the scope of the invention, not just those explicitly described above. For example, nano-pores may be fabricated in a variety of ways, which will be apparent to those skilled in the art. The mask for example may be produced using any suitable method, and not just those listed in detail above. The nano-pores may be fabricated so as to have various shapes, chosen as appropriate for the application in hand. The material of the nano-networks surrounding the nano-pores does not have to be constant, for example the alloy content may be varied along its height so that its properties are most suitable for the specific application. For example, the alloy content may be selected so as to optimise absorption during a laser ablation separation process. Alternatively, a change in the alloy content may optimise the lattice constant for the overgrown semiconductor. Furthermore, the nano-network material need not be identical to that of the overgrown compound semiconductor. 
     In the specific examples described, nano-pores are fabricated from the non-polar III-V nitride material template before overgrowth of the material. However, use of a nano-network layer may permit relatively easy removal of the semiconductor, without causing undue damage to the underlying substrates. The material can then be prepared to be used as the seed for further growth of the material by HVPE. The full benefit of the defects annihilation in HVPE growth can be used to achieve the material with the lowest defect by the use of a previously-grown semiconductor as the seed. In other words, the nano-pores and nano-network fabrication processes may need to be done only once, then the semiconductor may be used as a seed for the overgrowth of materials. This would have significant cost savings for the second and each subsequent overgrowth. 
     In summary, while preferred embodiments of the foregoing invention have been set forth for purposes of illustration, the foregoing description should not be deemed a limitation of the invention herein. Accordingly, various modifications, adaptations and alternatives may occur to one skilled in the art without departing from the spirit and scope of the present invention.