Patent Publication Number: US-6337005-B2

Title: Depositing device employing a depositing zone and reaction zone

Description:
This is a division of cop ending parent application Ser. No. 08/893,578, filed Jul. 11, 1997, which will issue as U.S. Pat. No. 6,171,659 on Jan. 9, 2001. 
    
    
     FIELD OF INVENTION 
     The present invention relates to a process for the depositing, onto a substrate, of a coating mainly constituted of an electronic conductor compound. 
     BACKGROUND 
     According to one of the techniques known up to now, such a coating is formed by reactive cathode sputtering, also known as “reactive sputtering”. Such a process especially presents the disadvantage of a comparatively low deposition speed, resulting from the contamination of the used targets from which the pulverization is achieved. 
     Another known technique is the activated evaporation in a vacuum, called ARE (Activated Reactive Evaporation). This technique also has to cope with a problem of contamination of the evaporation system, which considerably reduces the efficiency of the depositing. 
     SUMMARY OF INVENTION 
     One of the essential aims of the present invention is to propose a process of the above-mentioned type, allowing to realize, at a high speed, a coating on a substrate, electrically conducting or not, and this essentially of a relatively significant thickness. 
     It concerns, more particularly, a process of mass production of layers of electrically conducting compounds with a thickness of the order of 1000 Å on a substrate formed, for example, of drawn steel, flat glass, a sheet of paper or a plastic film. 
     For this purpose, according to the invention, the said coating is formed by producing alternatively, on the one hand, in at least one depositing zone, one or several deposits of a determined thickness of an electronic conductor element, such as a metal, an alloy, a semi-conductor of the N-doped type, on the substrate, and, on the other hand, in at least one reaction zone, one or several reactions of the element thus deposited with the ions of a reactive gas which are implanted into the deposit of the aforesaid element approximately over the entire determined thickness in such a way that the said compound is formed with approximately the majority and preferably with the total quantity of this element, the aforesaid ions being submitted to a kinetic energy below 2000 V; preferably from 200 to 900 V, while the above-mentioned thickness of the deposit of the element is determined as a function of the applied kinetic energy in such a way that the implantation of these ions can be achieved over approximately this entire thickness. 
     Advantageously, the above-mentioned reaction of the element deposited on the substrate with the above-mentioned reactive gas is accomplished by creating, facing and in the proximity of the surface of the latter presenting the deposit of the element, a plasma in which the above-mentioned reactive gas is introduced, in such a way that ions are formed in it, penetrating into the deposit of the element, approximately over a depth corresponding to the thickness of this deposit in order to have them react with the deposited element. 
     According to a particular embodiment of the invention, a negative potential with regard to an anode is applied to the substrate, in the reaction zone. 
     According to an advantageous embodiment, the depositing of the element by evaporation, preferably in a vacuum, is followed by a condensation onto the substrate. 
     According to a particularly advantageous embodiment, the deposit of the element on the substrate is formed by cathode sputtering. 
     According to a preferred embodiment of the invention, on the substrate a coating is formed, consisting of a layer of a ceramic electronic conductor compound, for example a compound of the TiN, ZrN, TiCN, CrN, VN, NbN, InSnO type, which is obtained by the reaction of at least one metal and one reactive gas, by accomplishing first, in the depositing zone, a deposit of the said metal on the substrate, and thereafter, in the reaction zone, an ionization of the gas, in a plasma, formed facing this deposit, and an implantation of ionized particles of this gas into the metal deposit, a negative potential with regard to the ionized gas being applied to the latter. 
     The invention also concerns a particular device for the use of the above-mentioned process. 
     This device is characterized in that it includes at least one depositing zone in which a deposit of an electronic conductor element may be formed on the substrate, this depositing zone being followed by at least one reaction zone, separated from this depositing zone, where an implantation may be accomplished, into the aforesaid deposit, of particles which may react with this element in order to form the electronic conductor compound, means being provided for moving, preferably in a continuous way, the substrate from the depositing zone to the reaction zone. 
     Other details and characteristics of the invention will appear from the description given below, by way of unlimitative examples, of a few particular embodiments of the invention with reference to the appended figures. 
    
    
     BRIEF DESCRIPTION OF DRAWING 
     FIG. 1 is a schematic view of a vertical section of a first embodiment of the invention, a device for the formation of a coating on a substrate. 
     FIG. 2 is a schematic, analogous to the one of FIG. 1, of a second embodiment of the invention, of a device for the formation of a coating on a substrate. 
     FIG. 3 is also a schematic view, analogous to those of FIGS. 1 and 2, of a third embodiment of the invention, a device for the formation of a coating on a substrate. 
     FIG. 4 is yet another schematic view of a fourth embodiment of the invention, of a device for the formation of a coating on a substrate. 
     In the different figures, the same reference numbers refer to analogous or identical elements. 
    
    
     DETAILED DESCRIPTION 
     In a general way, the invention consists in proposing a process for the depositing, onto a substrate, of a coating essentially constituted of an electronic conductor compound. 
     The substrate may for example be made of drawn sheet steel, plates of flat glass, sheets of paper or plastic films. 
     The coating may be obtained by the mass production of layers, for example, of metallic or ceramic compounds, the thickness of which is generally of the order of 500 to 2000 Å. In this respect, the process according to the invention is characterized in that first a separate layer is formed on the substrate, in the depositing zone of an electronic conductor element, such as a metal, an alloy or a semi-conductor of the N-doped type, of a determined, comparatively reduced thickness. Then, in a reaction zone which is separated from the depositing zone, a reactive gas is created, containing ions which not only may react with the above-mentioned element, but which moreover possess enough kinetic energy to be able to implant themselves over the entire above-mentioned determined thickness of the deposit or layer of the element on the substrate. 
     This kinetic energy is advantageously maintained below 2000 V, preferably between 200 and 900 V, while the above-mentioned determined thickness is such that the implantation of the ions of the reactive gas may take place over approximately this entire thickness, and that these ions may react with the total quantity of the element forming this deposit layer. These depositing and subsequent reaction steps are repeated as many times as required for obtaining the desired final thickness of the coating. 
     According to an advantageous embodiment of the invention, a plasma is created, in the reaction zone, facing and close to the substrate. In this plasma, the above-mentioned reactive gas is introduced in such a way as to form ions in it, which may react, by implantation, with the element previously deposited onto the substrate. 
     In order to obtain the required kinetic energy for the implantation of the ions of the reactive gas into the deposit layer of the element, a negative potential is preferably applied to the substrate in the reaction zone, to negatively polarize the already formed deposit on the substrate, and, moreover, a magnetic confinement circuit is created for the electrons formed in the proximity of the surface of the substrate on which the coating is formed. 
     The deposit of the above-mentioned conductor element may be formed by evaporation, preferably in a vacuum, followed by a condensation onto the substrate, by cathode sputtering, by a combination of an evaporation and a cathode sputtering, or else by means of an ion gun. 
     The technique of combining an evaporation and a cathode sputtering forms the subject of the Belgian patent application no. 09501052 of the same applicant, while the other techniques generally constitute techniques known in themselves. In this respect, it should be noted that the ion gun is generally less interesting than the other techniques mentioned. 
     FIG. 1 shows a diagram of an embodiment in which the deposit of the element is formed by evaporation in a vacuum. It concerns a particular embodiment for the coating of one of the sides of a substrate  1  in the form of a continuous sheet, which is moving in an approximately continuous way in the sense of the arrow  2 , first through a first zone  3  where the evaporation in a vacuum of a metal  4 , kept in the molten state in a crucible  5 , takes place. In this zone, a film or a layer  6  of this metal is condensed onto the side of the sheet facing the crucible  5 . The substrate  1  with this film  6  is then moving to a second zone  7 , separate from the first one, in which a plasma  8  is produced, in a reactive gas, for example N 2 , CH 4 , said plasma allowing the formation of ions in this gas. These ions are implanted into the film  6  to react with the metal of which it is made up, and thus form a coating  9  of an electronic conductor compound obtained by the reaction of the metal forming the film with the produced ions. 
     In order to give the ions the required kinetic energy for penetrating into the entire thickness of the film  6 , a negative potential is applied to the substrate  1 , in zone  7 , with respect to an anode  10  arranged facing this substrate. 
     Reference is also made to the fact that the reactive gas is introduced into the plasma  8  through injectors  11 , schematically represented in FIG. 1, and generally called “showers”. 
     The density of the ions penetrating the film  6  is further increased by the presence of a magnetic confinement circuit on the side of the substrate covered by this film. This magnetic circuit is created by permanent magnets or possibly by electromagnets  12 , mounted onto a soft steel plate, represented schematically in FIG. 1, installed near the substrate  1 , on the side opposite to the one on which the film  6  is formed. 
     FIG. 2 is a schematic representation of a second embodiment of the invention which relates to the formation of a coating on one of the sides of rigid plates, in particular of glass plates  1 , which are moving in an approximately continuous way in the sense of the arrow  2  on earthed following rollers  13 , successively through the depositing zone  3  and the reaction zone  7 . 
     In this embodiment, the depositing of the film  6  in the depositing zone  3  is accomplished by cathode sputtering. 
     According to this technique, which is known in itself, in this zone  3 , facing the glass plates  1 , is provided a target of microwave cathode sputtering  14  provided on the side directed toward these glass plates, with a layer of the metal of which the film  6  is made up. This layer of the target  14  is bombarded by inert gas ions, such as argon ions, formed in a plasma  15 , which eject metal atoms from this target  14  and form the above-mentioned film  6  on the substrate. This inert gas is introduced into the depositing zone  3  by injectors  18  inclined downward. 
     The target  14  is connected to a negative potential, while the rollers  13  are also earthed. 
     The reaction zone  7 , where the ions originating from the reactive gas are implanted into this film, is almost identical to the one in FIG. 1, and is separated from the depositing zone by a wall  20 , in which an opening  21  is made for the glass plates  1  to pass from the depositing zone  3  to the reaction zone  7 . 
     FIG. 3 is a schematic representation of a third embodiment, which differs from the one shown in FIG. 2 by the nature of the substrate  1 , by the technique applied for the formation of the metal film  6  in the depositing zone, and by the means of transport of the substrate  1  through the depositing zones  3  and  7 . In this third embodiment, the substrate is formed of a flexible sheet  1 , a metal sheet, or a supple sheet of paper or a plastic matter, such as polyethylene or polypropylene, which is driven by drums  16  revolving in synchronism around their axis  17  in the sense of the arrows  2 . 
     In the depositing zone  3  the film  6  is formed on the substrate  1  by the use of the combined technique of vacuum evaporation and cathode sputtering, as described in the Belgian patent application 09501052 of Dec. 20, 1996 of the same applicant. 
     Accordingly, in this case the metal  4  is maintained in the liquid state in a crucible S maintained at a negative potential, under which magnets  12  are installed forming a magnetic circuit, exactly as in the reaction zone  7  of the preceding embodiments. 
     The reaction zone  7 , which follows the depositing zone  3 , is separated from the latter by a wall  20 , as in the second embodiment. This reaction zone  7  differs from the preceding embodiments in that the sheet  1  constituting the substrate is driven by a drum  16  and that the magnets  12 , forming the magnetic circuit, are installed within the drum, facing the spot where the sheet  1  is in contact with the latter. 
     One of the advantages of the device according to FIG. 3 is that it allows an easy cooling of the substrate, both in the depositing and the reaction zones by means of a cooling liquid circulating within the drums. This may be useful in certain cases, for example for the treatment of substrates with comparatively low softening points or subject to phase transformations. 
     FIG. 4 is a schematic representation of a fourth embodiment of the invention, in which the formation of the film  6  on the substrate  1  in the depositing zones  3  may be carried out for example as in the preceding forms of embodiment. 
     However, what is typical in this fourth embodiment is, that a determined depositing zone is separated from the subsequent depositing zone by at least two consecutive distinct consecutive reaction zones. Thus in FIG. 4 three consecutive reaction zones  7   a ,  7   b ,  7   c  are shown between two depositing zones  3 , where the substrate  1  is submitted to a potential which differs from one reaction zone to the subsequent one, preferably to a decreasing potential, in the sense of the movement  2  of the substrate  1  from one reaction zone to the following reaction zone. Actually, the potential difference in the zone  7   a  may for example be of the order of 3000 V, the one in the zone  7   b  of 1000 V and the one in the zone  7   c  of 500 V. 
     The invention is further illustrated by a few concrete examples of embodiment described below. 
     EXAMPLE 1 
     This example concerns the formation of a decorative coating of zirconium nitride on sheet steel using a device such as illustrated by FIG. 1, in which however a zirconium film  6  is deposited on the sheet  1 , from a zirconium target  14 , by cathode sputtering, as in the device shown in FIG.  2 . 
     The sheet with a thickness of 0.2 mm was moving through the zones  3  and  7  at a speed of the order of 400 m/minute. The width of the zirconium target  14  in the reaction zones  3  in the sense of the movement  2  of the sheet  1 , was 30 cm. Thus, the passing time of the sheet  1  in front of the target  14  was 0.045 sec. 
     In this depositing zone  3 , argon was injected at a pressure of 5.10 −3  Torr, while the density of the power dissipated at the target amounted to 75 W/cm 2 . 
     In the reaction zone  7 , also called the implantation zone, nitrogen was infected, also at a pressure of 5.10 −3  Torr, while the density of the power dissipated at the substrate during the implantation of the zirconium film amounted to 20 W/cm 2 . The tension between the sheet and the anode amounted to 450 V. 
     By passing the sheet successively through ten sections of this type, i.e. a depositing zone followed by a reaction zone, a sheet was obtained covered with a homogeneous final layer of zirconium nitride with a total thickness of 700 Å, which would be perfectly suitable for decoration. 
     EXAMPLE 2 
     This example concerns the formation of a layer of indium and tin oxyde (InSnO), also called “ITO”, on sheet glass, using the device as illustrated schematically in FIG. 2, but in which however the depositing zone  3  corresponded with the one of the embodiment shown in FIG.  1 . Thus, two successive crucibles were provided, forming the targets, one crucible containing liquid tin, the other containing liquid indium. The surface of the liquid metal in each of these crucibles, exposed to the sheet glass rolling along in front of the latter, was 30 cm wide in the sense of the movement. As in the first example, the moving speed of the sheets was 400 m/minute. 
     In the depositing zone, argon was injected at a pressure of 5.10 −3  Torr, while the density of the power dissipation at the targets amounted to 50 W/cm 2 . 
     The width of the reaction zone, more particularly of the magnetic circuit defined by the magnets forming a magnetron, was 30 cm. 
     In this zone, oxygen was injected at a pressure of 5.10 −3  Torr. 
     The voltage in this zone between the film composed of indium and tin, previously formed in the depositing zone on the sheet glass entering the reaction zone, amounted to 600 V and the density of the power dissipation on the substrate amounted to 30 W/cm 2 . 
     As in Example 1, the sheet glass was passed through ten identical depositing zones, a same reaction zone being inserted between each of them. This allowed to obtain sheet glass covered with a homogeneous and transparent final layer of indium and tin oxyde with a thickness of 1000 Å. 
     EXAMPLE 3 
     This example concerns the formation of a titanium nitride coating onto a flexible sheet of aluminium with a thickness of 0.3 mm, using an Device of the type shown in FIG.  3 . 
     The operating conditions and parameters in the depositing and reaction zones approximately corresponded to those of Example 1. This allowed to obtain a homogeneous coating of titanium nitride with a thickness of 500 Å after ten successive passages through a depositing zone and a reaction zone.