Patent Document

BACKGROUND OF THE INVENTION 
     The present invention relates to flame retardant open-celled porous plastics and natural products. The open-celled porous plastic products are made to be flame retardant by coating the cell wall with a flame retardant mixture of compounds containing phosphorus and/or boron, carbonization auxiliaries, auxiliary agents, fillers, and/or halogenated compounds. The flame retardant compounds maybe reacted with the plastic components, such as isocyanate-reactive compounds, polyepoxides, polyol, polyamines, and others then after the open-celled porous mass has been produced the open cells are coated with a liquid solution and/or emulsion of the flame retardant mixture. The excess liquid is then removed and the mass is dried. The flame retardants are left on the cell walls and/or in the cells. 
     The flame retardant open-celled porous plastic and natural products that are made flame retardant by coating the cell wall with flame retardant mixtures according to this invention are distinguished by having surprising good fire chacteristics in spite of being prepared without the use of flame retardant compounds in the production of the porous mass. There is some improvement in the good fire chacteristics of the cellular coated porous mass with the addition of flame retardant compounds utilized in the production of the porous masses. 
     There is a problem with organic open-celled porous masses because they are highly flammable, especially the flexible open-celled polyurethane foams, and they are the most difficult to make flame retardant. This problem is surprisingly solved by the process of this invention. This is achieved by coating the open cells with a flame retardant compound mixture even without adding flame retardant compounds in the production of the porous masses. When the treated porous masses are exposed to flames, a char and/or intumescent masses are produced. The char and/or intumescent mass stops the burning of the porous mass. 
     The open-celled polyurethane foams are the preferred porous mass to be flame retarded by the process of this invention. The open-celled flexible masses are the easiest to flame retard because they can be compressed before they are placed in the liquid containing the flame retardant compounds then decompressed while in the liquid therefore the flame retardants are vacuumed into the cells. The excess liquid then can be removed from the porous mass by compressing the mass. The rigid type open-celled porous must be left in the liquid until the liquid replaces the air in the cells. It is preferred that the flame retardants are carbonization agents. 
     The flame retardant open-celled porous masses may be used for insulation, for fireproofing, as cushioning, for sound proofing, and other uses commonly known in the polyurethane Art. The primary purpose of this invention is to produce flame retardant open-celled porous masses. Another object of this invention is to flame retard existing open-celled porous masses. 
     SUMMARY OF THE INVENTION 
     The novel process of this invention produces surprisingly good flame retardant open-celled porous products by coating the cell walls with a flame retardant mixture even without adding flame retardants in the production of the porous mass. The present invention thus relates to utilizing flame retardant mixtures that produces carbonization masses and/or charring containing carbonization auxiliaries, reactive compounds containing phosphorus and/or boron, fillers and other auxiliary agents. These flame retardant mixtures may be optionally be utilized in the production of the open-celled porous masses. Any suitable halogenated organic flame retardant compound, with or without antimony oxides, may be used as the flame retardant agent of this invention with or without carbonization auxiliaries. The powdered halogenated organic compound, with or without phosphorus radicals, are the preferred halogenated organic compound. Halogenated organic flame retardant compounds are well known in the Arts. 
     DETAIL DESCRIPTION OF THE INVENTION 
     Open-celled porous masses may be flame retarded by the process of this invention, such as, for example, natural sponges, plastic sponges, foamed rubber and plastics. The open-celled porous masses cell walls are coated and/or reacted with flame retardant agents in a liquid, preferably water containing an adhesive agent. The flame retardant agents in the liquid consist of: 
     1. carbonization auxiliaries; 25 to 75 parts by weight per 100 parts by weight of liquid 
     2. optionally halogenated organic compounds; 0 to 75 parts by weight per 100 parts by weight of liquid 
     3. optionally halogenated organic phosphorus compounds; 0 to 75 parts by weight per 100 parts by weight of liquid 
     4. fillers; 0 to 200 parts by weight per 100 parts by weight of liquid 
     5. adhesives; 0 to 10 parts by weight per 100 parts by weight of liquid 
     The liquid solution and/or suspension or emulsion of carbonization auxiliaries and/or flame retardant agents utilized in this invention are produced by adding one or more carbonization auxiliaries and/or flame retardant agents to a liquid, preferably water, to produce a solution and/or suspension or emulsion. The carbonization auxiliaries and/or flame retardant agents are added in an amount of 25 to 75 parts by weight to 100 parts by weight of the liquid. An adhesive agent is added to this liquid in the amount up to 10 parts by weight to 100 parts by weight of the liquid. Any suitable adhesive agent may be utilized such as modified starch, urea-formaldehyde resin, phenol-formaldehyde resin, furan resins, polyfurfural resin, polyfurfuryl alcohol resin, aqueous suspension of vinyl acetate, vinyl latex, polyepoxide resin, alkali metal silicates, methyl cellulose, polyacrylate resin, casein, polysulfide resin, rosin, polyimide resins, polyamide resins, polyester resins, clay, etc. 
     This liquid for flame retarding open-celled porous masses may contain fillers such as amino compounds, e.g., urea, melamine, dicyandiamide, and other cyanuric derivatives or their formaldehyde resins, phenol resin powder powdered synthetic resins, sawdust, carbohydrates, bituminous additives, graphite, and graphite compounds, powdered coke, alkaline metal earth silicates, metal silicates, metals and metal carbonates, oxides, sulphates, phosphates, borates and mixtures thereof. 
     The carbonization auxiliaries are compounds that in the presence of fire assist the formation of a carbonization foam or char such as additives that produce acidic components in the pyrolysis mixture, such as phosphorus acids, boric acid or sulfuric acids. These acidic components are compounds such, for example, acids or salts, or their derivatives of sulfur, boron and phosphorus, such as, boron-phosphates, phosphates and polyphosphates of ammonia, amines, polyamines, amino compounds and alkylanolamines, but boric acid and its salts, boron-phosphate and its salts, sulfates, elementally sulphur, phosphorus, phosphonic acids and their derivatives, organic phosphorus compounds and their salts, halogenated organic phosphorus compounds, their salts and their derivatives may also be used for this purpose. The carbonization auxiliaries and other flame retardant agent may be used in quantities of 0 to 50 percent by weight of the porous mass when utilized in the production of the porous masses. The additives may be solid or liquid. The boron-phosphate salts such as ammonium boron-phosphate, ammonium boron-polyphosphate, amino boron-phosphate and ammonium polyphosphate are particularly preferred, and amino of phosphorus acids, organic phosphorus compounds and esters of methylphosphonic acids and of phosphoric acids may also be utilized. 
     Flame retardant open-celled porous masses are preferably of the type produced by the reaction of: 
     1. polyisocyanate; 10% to 60% by weight 
     2. compounds with 2 or more active hydrogens and/or polyepoxides which will react with isocyanates; 25% to 70% by weight 
     3. carbonization auxiliaries and/or halogen flame retardant compounds; 0% to 50% by weight 
     4. urethane catalyst, stabilizers, emulsifiers, color components; 0% to 10% by weight 
     5. fillers; 0% to 200% by weight 
     6. blowing agents; 0% to 50% by weight 
     Percentages are based on the weight of the polyurethane reactants. Suitable polyisocyanates for the present invention are those which are well know in polyurethane chemistry. Those polyisocyanates are for example, aliphatic, cycloaliphatic, araliphatic, aromatic and heterocyclic polyisocyanates, such as described, for example, by W. Siefken in Justus Liebigs Annalen der Chemie, 562, 75-136, particularly those of the formula: 
     
         Q(NCO)m 
    
     in which, 
     m represents a number from 2 to 4, preferably 2.0 to 3.0, and 
     Q represents an aliphatic hydrocarbon radical having 2 to 18, preferably 6 to 10, C atoms, a cycloaliphatic hydrocarbon radical having 4 to 15, preferably 5 to 10, C atoms, an aromatic hydrocarbon radical having 6 to 15, preferably 6 to 13, C atoms or an araliphatic hydrocarbon radical having 8 to 15, preferably 8 to 13, C atoms are suitable. 
     The polyisocyanates which are readily available in the industry are preferred, for example, 2,4- and 2,6-tolulene diisocyanate and any mixtures of these isomers (&#34;TDI&#34;), polyisocyanates of the MDI type, for example, 4,4&#39;- and/or 2,4&#39;-diphenylmethane diisocyanate and/or polyphenylpolymethylene polyisocyanates, as are prepared by aniline/formaldehyde condensation and subsequent phosgenation (&#34;crude MDI&#34;) and polyisocyanates which have carbodiimide groups, urethane groups, allophanate groups, isocyanurate groups, urea groups or biuret (modified polyisocyanates), those modified polyisocyanates which are derived from 2,4- and/or 2,6-toluylene diisocyanate or from 4,4&#39;- and/or 2,4-diphenylmethane diisocyanate are preferred. The distillation residue having isocyanate groups which is produced during industrial production of isocyanates may be dissolved in a polyisocyanate and used in this invention. The monoisocyanates may also be used with the polyisocyanates in an amount of up to 30 percent by weight. The polyisocyanates are utilized in the amount of 10% to 60%, percentage based on weight of the polyurethane reactants. 
     Compounds with two or more active hydrogens may be used to react with the polyisocyanates to produce polyurethane foams, preferable open-celled rigid, semi-rigid or flexible foams. The compounds with two or more active hydrogens are, for example, polyols polyamines, polycarboxylic acids, phosphorus containing polyols, polyesters, polyethers, aldehydes, etc. 
     Suitable polyols which will react with polyisocyanates are those having 2 to 8 hydroxyl groups, having a molecular weight of 400 to 10,000, in particular polyesters and polyethers. Hydroxyl-containing polyesters are reaction products of polyhydric alcohols with polyhydric carboxylic acids. Suitable polyethers polyols are produced by polymerization of epoxides such as ethylene oxide, propylene oxide, butylene oxide, tetrahydrofuran, styrene oxide or epichlorohydrin with themselves or by the addition reaction of the epoxides with starting components having reactive hydrogen atoms such as water, alcohols, polyols, ammonia, or amines. 
     The polyols may contain phosphorus. Salts of amines containing hydroxyl groups and the various phosphorus acids, and amides of various phosphorus acids containing hydroxyl groups or NH groups may also be used. Polyols having a molecular weight of 32 to 40 may be used as chain-lengthing agents or crosslinking agents. The isocyanate active compounds that may be utilized in this invention may act as built-in carbonific, for example, as a source of carbon or intumescent foam and may contain the propellants such as nitrogen, nitrogen oxide, carbon monoxide, carbon dioxide, steam and/or other conventional propellants. 
     In the production of open-celled flexible polyurethane foam, the mixture to be foamed include at least one polyether polyol, at least one organic polyisocyanate, at least one blowing agent, and at least one catalyst. The mixture may also include other known additives and compounding ingredients for the preparation of polyurethane foams. Such additives include, for example, surfactants, foam stabilizers, cell openers, lubricants, microbicides, pigments, etc, The polyaxyalkylene polyether polyols are most commonly used to produce flexible foams. The polyether polyols may have dispersion of a polyurea or a polyhydrazodicarbonamide. The significant reactants in carrying out the urethane polymerization reactions are the isocyanate groups and the active hydrogen groups. The compounds with active hydrogen groups are utilized in the amount of 25% to 70% by weight, percentage based on the weight of the polyurethane reactants. 
     The preferred blowing agent for general use in the production of the flexible polyurethane foams is water. Other blowing agents such as certain halogen-substituted aliphatic or cyclo-aliphatic hydrocarbons having boiling points between -40 degree and +100 degree C. may also be used with or without water. These halogen-substituted hydrocarbons are usually used as the blowing agent in rigid foams with or without waters. The blowing agent us utilized in an amount up to 50% of the weight of the polyurethane reactants. 
     Suitable catalysts in the polyurethane foam art include tertiary amines and metallic compounds. The tertiary amines are will known in the polyurethane art. Tin compounds are particularly useful. The catalyst may be utilized in the amount up to 10% by weight of the polyurethane reactants. Surfactants, such as, organo-silicon surfactants are useful in polyurethane foam production and are utilized in an amount up to 20% of the weight of the polyurethane reactants. 
     The fillers that may be utilized in the flame retardant mixture are usually insoluble in the reaction mixtures to produce the open-celled masses. They may be organic substances, such as, amino compounds, such as, urea, melamine, dicyandiamide, and other cyanuric derivatives or their formaldehyde resins, phenol resin powder, powdered synthetic resins, sawdust, carbohydrates, polyhydric alcohols and their oligomers, bituminous additives, graphite and graphite compounds and powdered coke. 
     Inorganic fillers may be alkali metal silicates, alkaline earth metal silicates, metal silicates, metals, oxides, carbonates, sulphates, phosphates, borates, glass beads or hollow glass beads. These compounds may be either anhydrous or contain water of crystallization or split off water. Hydrated aluminum oxide is preferred. The fillers may be used in an amount of up to 200% of the weight of the polyurethane reactants. 
    
    
     DESCRIPTION OF PREFERRED EMBODIMENTS 
     My invention will be illustrated in greater detail in the specific examples which follow, which details the preferred embodiment of my process. It should be understood that the scope of my invention is not limited to the specific processes set out in the examples. Parts and percentages are by weight, unless otherwise indicated. 
     EXAMPLE 1 
     About 10 parts by weight of boric acid are mixed with 50 parts by weight of phosphoric acid then heated until a thick liquid boron-polyphosphate condensation product is formed, then 20 parts by weight of ammonium carbonate are added, mixed and reacted to produce an ammonium boron-polyphosphate condensation product. About 25 parts by weight of the ammonium boron-polyphosphate condensation product are mixed with 100 part by weight of water, then a 4&#34;×8&#34;×8&#34; piece of open-celled polyurethane flexible foam, which was produced from polyether triol and TDI without flame retardants, is compressed and then placed in the said aqueous emulsion. The foam expands and vacuum the emulsion into the cells. The foam is then compressed to remove the excess aqueous emulsion and then air dried. 
     The dried flame retardant foam is weighed then flame tested (California TB133) by placing a 100 gms wood crib on the foam. The wood crib is burned and the foam is re-weighed. There was a 52 gms weight loss. The flames did not travel. There was less smoke produced. 
     EXAMPLE 2 
     Example 1 was modified by using a flexible, open-celled, polyurethane foam produced by using MDI and polyether triol without flame retardants in place of the TDI foam. After the 100 gms of wood burned on the foam there was a weight loss of 45 gms. 
     EXAMPLE 3 
     Example 1 was modified wherein a flexible, open-celled polyurethane foam produced using polymeric MDI and polyether triol without flame retardants was used in place of the TDI foam. After the 100 gms of wood burned on the foam there was a 49 gms weight loss. 
     EXAMPLE 4 
     Example 1 was modified wherein another compound is used in place of ammonium carbonate and selected from the list below: 
     
         ______________________________________    a)  ammonium phosphate    b)  ammonium borate    c)  melamine    d)  urea    e)  guanidine    f)  dicyandiamide    g)  ethyl urea    h)  ethylamine    I)  thiourea    j)  diethylenediamine    k)  ethylenediamine    l)  ammonia    m)  ammonium molybdate    n)  mixtures of the above______________________________________ 
    
     EXAMPLE 5 
     Example 1 was modified wherein another open-celled porous mass was used in place of the polyurethane flexible foam and selected from the list below: 
     a) natural sponge 
     b) cellulose sponge 
     c) foamed rubber latex 
     d) foamed flexible polyepoxy plastic 
     e) foamed flexible polyester plastic 
     f) foamed phenol-formaldehyde plastic 
     g) foamed urea-formaldehyde plastic 
     h) open-celled semi-rigid polyurethane foam 
     i) open-celled rigid polyurethane foam 
     j) foamed poly(methyl methylacrylate) plastic 
     k) foamed poly(vinyl chloride) plastic 
     l) foamed polystyrene plastic 
     m) foamed butadiene-styrene plastic 
     n) foamed polychloroprene plastic 
     o) foamed polyisoprene plastic 
     p) foamed poly(butadiene-acrylonitrile) plastic 
     q) foamed polyethylene plastic 
     r) foamed poly(vinyl acetate) plastic 
     s) foamed poly(ethylene-vinyl) plastic. 
     EXAMPLE 6 
     Example 1 was modified wherein 10 parts by weight of a powdered metal containing compound are added to the aqueous emulsion of ammonium boron-polyphosphate condensation product and selected from the list below: 
     
         ______________________________________a)        magnesium oxideb)        magnesium chloridec)        talcumd)        antimony trioxidee)        zinc oxidef)        zinc borateg)        alumina trihydrateh)        alumina magnesium calcium silicatei)        sodium silicatej)        zeolitek)        magnesium hydroxidel)        sodium carbonatem)        calcium carbonaten)        ammonium molybdateo)        iron oxidep)        copper oxideq)        zinc phosphater)        zinc chlorides)        clayt)        sodium dihydrogen phosphateu)        tinv)        molybdenumw)        zincx)        and mixtures of the above______________________________________ 
    
     EXAMPLE 7 
     Example 1 is modified wherein and adhesive in the amount of 5 parts by weight are added to the aqueous emulsion of ammonium boron-polyphosphate condensation product and selected from the list below: 
     
         ______________________________________a)        modified starchb)        urea-formaldehyde resinc)        phenol-formaldehyde resind)        aqueous suspension of vinyl acetatee)        flexible polyepoxy resinf)        flexible polyepoxy resing)        polyamide resinh)        aqueous polyurethane resini)        polyvinyl alcoholj)        melamine-formaldehyde resinl)        resorcinol resinm)        sodium silicaten)        methyl celluloseo)        polyacrylate resinp)        caseinq)        polysulfide resinr)        polymethacrylates)        and mixtures of the above______________________________________ 
    
     EXAMPLE 8 
     110 gms of a ethylene oxide modified polypropylene triol (Miles&#39; Multranol 7057), 3 gms of water, 1 gm silicone surfactant (Union Carbide&#39;s L6020), 0.25 gm amine catalyst (Air Products&#39; Dabco R8020) and 0.1 gm of tin catalyst (Air Products&#39; T12) are mixed then mixed with 50 gms of TDI (Miles&#39; Mondur TDI). The mixture expands and cures into an open-celled flexible foam of about 1.5 lbs/cu.ft. The flexible foam is cured for 1 week. 
     The cured flexible foam is compressed and placed into an aqueous emulsion containing 20% ammonium polyphosphate and 20% melamine phosphate. The aqueous emulsion is vacuumed into the open cells. The foam is removed from the aqueous emulsion then compressed to remove the excess fluids. The foam is then air dried. After the foam has dried it is weighed then tested (California TB 133) by burning 100 gms of wood on top of the foam. After the wood has burned and charcoals removed the foam is weighed, There was a 49 gms weight loss. The flame did not spread and there was a decrease in the amount of smoke. 
     EXAMPLE 9 
     Example 8 is modified wherein 10 parts by weight of a powdered filler is added to the polyol and selected from the list below: 
     
         ______________________________________  a)  wood powder  b)  expandable graphite  c)  phenol-formaldehyde resin  d)  urea-formaldehyde resin  e)  melamine  f)  urea  g)  dicyandiamide  h)  carbohydrate  i)  coke  j)  melamine-formaldehyde resin  k)  fuel ash  l)  glass beads  m)  silicate beads  n)  ammonium borate  o)  gypsum  p)  mica  q)  chalk  r)  apatite  s)  aluminum hydroxide  t)  calcium borate  u)  aluminum silicate hollow beads  v)  boron oxide  w)  magnesium phosphate  x)  and mixtures of the above______________________________________ 
    
     EXAMPLE 10 
     Example 8 is modified wherein 15 parts by weight of a flame retardant compound is added to the polyol in place of dimethyl methyl phosphonate and selected from the list below: 
     
         ______________________________________a)      ammonium polyphosphateb)      urea phosphatec)      melamine pyrophosphated)      melamine salt of boron-polyphosphatee)      ammonium salt of boron-polyphosphatef)      melamine orthophosphateg)      ammonium urea phosphateh)      ammonium melamine phosphatei)      urea salt of dimethyl methyl phosphonatej)      melamine salt of dimethyl methyl phosphonatek)      melamine salt of dimethyl hydrogen phosphitel)      brominated epoxy oligmerm)      polypentabromobenzyl acrylaten)      decabromodiphenyl oxideo)      pentabromodiphenyl oxidep)      2,3-dibromopropanolq)      octabromodiphenyl oxider)      tris(2-chloroethyl) phosphites)      diethyl phosphitet)      tris(dichlorobropropyl) phosphiteu)      dicyandiamide pyrophosphatev)      triphenyl phosphitew)      ammonium dimethyl phosphatex)      and mixtures of the above______________________________________ 
    
     EXAMPLE 11 
     Example 8 is modified wherein a flame retardant compound is utilized in place of ammonium polyphosphate in the aqueous emulsion and selected from the list below: 
     
         ______________________________________a)        ureab)        melaminec)        cyanoquanidined)        ethylenediamine salt of phosphonic acide)        ethanolamine dimethyl phosphatef)        ammonium carbonateg)        diammonium phosphateh)        urea-formaldehyde resini)        ammonium urea polyphosphatej)        boric acidk)        thioureal)        diethylenediamine polyphosphatem)        dicyandiamide polyphosphaten)        ethyl ureao)        melamine formaldehyde resinp)        methylamine boron-phosphateq)        potassium ammonium phosphater)        ammonium silicates)        quaternary ammonium hydroxidet)        aniline phosphateu)        ammonium oxalatev)        ammonium boratew)        cyanuramide phosphatex)        mixtures of the above______________________________________ 
    
     EXAMPLE 12 
     Example 8 is modified wherein another polyisocyanate is used in place of TDI and selected from the list below: 
     a) 55 gms of diphenylmethane-4,4&#39;-diisocyanate (MDI) 
     b) 60 gms of polymeric MDI (Mondur MR by Miles) 
     c) 55 gms of modified polymeric polyisocyanate (Mondur E-448 by Miles) 
     d) 55 gms of Mondur T-422 by Miles 
     e) 60 gms polymeric MDI (PAPI 27 by DOW) 
     EXAMPLE 13 
     Example 8 is modified wherein another polyol is used in place of Multranol 7057 and selected from the list below: 
     a) 50% multranol 7057 and 50% multranol 3900 by Miles 
     b) Polyol-G 3056 by Olin 
     c) polyol L56 by ARCO 
     d) 25% Polybid liquid resin and 75% polyol L56 by ARCO 
     e) 25% Poly-G 55-173 and 75% Poly-G 32-56 by Olin 
     f) propylene oxide/ethylene oxide adduct having a hydroxyl No. 56 and contains 9% ethylene oxide 
     g) propylene oxide adduct of trimethylol propane having a hydroxyl No. 56 
     EXAMPLE 14 
     Example 8 is modified wherein another flame retardant compound is used in place of ammonium polyphosphate and melamine phosphate in the aqueous emulsion and selected from the list below: 
     a) 15% urea borate and 15% ammonium boron-polyphosphate 
     b) 15% urea phosphate, 20% ammonium polyphosphate and 3% polyvinyl chloride latex 
     c) 10% boric acid and 20% melamine 
     d) 20% ammonium boron-polyphosphoric, 10% decabromodiphenyl oxide, 5% antimony trioxide 
     e) 20% urea borate, 20% dimelamine phosphate and 3% clay 
     f) 30% magnesium and ammonium salt of boron-polyphosphoric acid and 3% starch 
     g) 10% boron oxide, 10% melamine phosphate and 10% ammonium polyphosphate 
     h) 20% ammonium salt of boron-polyphosphoric acid and 10% talcum powder 
     i) 10% ammonium polyphosphate, 10% melamine phosphate, 10% alumina hydrate and 5% phenol-formaldehyde resin 
     j) 10% boric acid, 10% hydrated sodium silicates powder and 10% ammonium polyphosphorate 
     k) 10% melamine, 10% boric acid and 10% sodium silicate powder 
     l) 10% zinc phosphate powder, 10% boron oxide powder, 10% melamine and 5% magnesium hydroxide 
     m) 5% zinc chloride, 10% ammonium boron-phosphorate, 10% melamine phosphate and 3% polylacrylic acid emulsion 
     n) 5% zeolite powder, 10% ammonium urea phosphate, 5% ammonium molybdate and 3% polyvinyl acetate emulsion 
     o) 5% ammonium sulfate, 10% dicyandiamide, 5% urea phosphate and 5% urea-formaldehyde resin 
     p) 10% ethylenediamine phosphorate, 5% melamine-formaldehyde resin, 5% boric acid, 5% melamine polyphosphorate and 3% polyamide resin 
     q) 25% magnesium ammonium boron-phosphate and 3% flexible polyepoxy resin 
     r) 20% ammonium melamine phosphate, 5% ammonium polyphosphate and 3% polymethylacrylate 
     s) 20% melamine salt of dimethyl methyl phosphonate and 5% melamine-formaldehyde resin 
     The following abbreviations are employed in the following examples: 
     Polyol A is a propylene oxide/ethylene oxide adduct having a hydroxyl number of 56 and containing 9% ethylene oxide. 
     Polyol B is a propylene oxide/ethylene oxide of glycerine having a hydroxyl number of 35 and containing 16.5% ethylene oxide. 
     Polyol C is a propylene oxide adduct of trimethylolpropane having a hydroxyl number of 29 and containing 15% ethylene oxide. 
     Polyol D is a propylene oxide adduct of trimethyolpropane having a hydroxyl number of 56. 
     T12 is dibutyltin dilaurate. 
     DMEA is dimethylethanolamine. 
     Dabco 33lv is a 33% solution of triethylenediamine in dipropylene glycol. 
     Silicon L6020 is a silicone surfactant manufactured by Union Carbide. 
     Silicon L5420 is a silicone surfactant manufactured by Union Carbide. 
     Niax A1 is an amine catalyst manufactured by Union Carbide. 
     TDI is toluene diisocyanate (Mondur TDI by Miles). 
     Mondur MR is a polymeric MDI manufactured by Miles. 
     DE6OF is pentabromodiphenyl oxide. 
     DMMP is dimethyl methyl phosphonate 
     Mel is melamine 
     Mel phos is melamine phosphate 
     Mel-DMMP is melamine salt of dimethyl methyl phosphonate urea phos is urea phosphate 
     APP is ammonium polyphosphate boron-phos is boron-phosphate condensation product 
     MgO is magnesium oxide 
     FR is the flame retardant in the aqueous solution for after treatment to the foam. 
     Examples 15-25 was prepared by the following procedures: 
     Component A, is composed of the polyol, water, silicone surfactant, Freon 11, catalyst, DMEA, filler and flame retardant. The mixture was agitated on a mixing machine for 30 minutes, in the proportions listed in grams. 
     Component B, composed of a polyisocyanate in the proportions listed in grams. 
     Components A and B were mixed for 10 seconds then poured into a plastic mold. The foams were cured for 1 week then the open-celled foam was compressed and placed in an aqueous solution and/or emulsion containing 40% flame retardant. The foam was then expanded and the aqueous emulsion was vacuumed into the cells. The foam was then compressed to remove the excess aqueous emulsion then air dried. 
     
                       TABLE I______________________________________  Examples  15    16      17      18    19    20______________________________________FormulationPolyol A 200     100     50    25    125Polyol B         100     150   175   75    200Water    8.0     7.0     9.0   6.0   8.0   7.0L6020    2.0     2.0     2.0   2.0   2.0   2.0Dabco 33LV    0.4     0.5     0.4   0.4   0.4   0.4T12      0.5     0.5     0.5   0.5   0.5   0.5DMMP     15      20      15    10    18    20TDI      110     100     95    35          90Polymeric MDI                  65    130Density PCF    1.5     1.6     1.7   1.7   1.5   1.8FRmel phos 30%             20%mel              15%                 10%boric acid    10%     5%            10%boron-phos               10%         20%   20%APP              20%     10%   10%   10%   20%urea phos                      20%Flame testingCalif. TB 133weight loss    52 gms  49 gms  48 gms                          45 gms                                35 gms                                      52 gms______________________________________ 
    
     
                       TABLE II______________________________________   Examples   21     22       23      24     25______________________________________FormulationPolyol C  150               150   50     100Polyol D  50       200      50    150    100water     7.5      8.0      8.5   8.0    9.0silicone L6020     2.0      2.0      2.0   2.0    2.0Dabco 33LV     0.4      0.2      0.4   0.4    0.4Niax A1            0.2      0.1          0.1DMEA      0.8      0.4      0.6   0.5    0.8TDI       100               50           60Polymeric MDI      130      65    130    50Mel       5                       5AlOH                              5APP       15                      10     5Mel-phos                                 5DMMP      5DE60F                       10    10Mel-DMMP           25       20           10Boron-phos     5                              5Density PCF     1.7      1.5      1.8   1.6    1.7FRAPP       25       5                     15Boron-phos         10       25           15boric acid     5        5mel                         10urea phos 10                      10     5MgO                5        5     5      5mel phos                          25Flame testing(CaliforniaTB 133)wt, loss  52 gms   32 gms   48 gms                             54 gms 45 gms______________________________________

Technology Category: 8