Volume # 2(117), March - April 2018 — "Application of alkaline metal fluorides for doping of aluminum "
Skachkov V.М., Pasechnik L.А., Yatsenko S.P.
Abstract. High-temperature exchange reactions between liquid aluminum and fluoride salt systems containing scandium, yttrium, zirconium, and hafnium compounds have been studied. High-temperature reactions in other salt systems have been compared. Advantages and disadvantages of application of alkaline metal fluorides for doping of aluminum have been shown.
In construction, mechanical engineering, aircraft building, rocket production, and many other sectors of the national economy they use mainly aluminum alloys since pure aluminum has poor technical characteristics, and doping of aluminum alloys with rare-earth scattered elements finds an ever-greater application, which considerably improves their service properties [1,2]. Small additions of scandium, yttrium, zirconium, and hafnium restrict grain growth of aluminum alloys, stabilize the crystal structure at high temperatures, increase the mechanical and corrosion properties, and improve weldability and plasticity. The presence of only 0.3 wt.% Sc increases the tensile strength of annealed aluminum sheets from 55 to 240 MPa, and in Al-5%Mg alloy – from 260 to 400 MPa. The effect of scandium manifests itself at smaller concentrations in the presence of zirconium. Yttrium additions of not more than 0.1 wt.% reduce the oxidation rate, especially in hard aluminum alloys. Hafnium in aluminum alloys binds such harmful impurities as iron, alkaline metals etc. into intermetallic compounds (IMC). The introduction of 1 wt.% Hf leads to the production of ultrastrong alloys exhibiting enhanced resistance to vibrational damage; such alloys have a grain size of ~ 40-50 nm [3-10]. Aluminum is usually doped by introducing master alloys, that can be obtained by different methods, into a melt. A good review of scandium doping methods is given by researchers of the Institute of High-Temperature Electrochemistry UB RAS in work . The aluminothermal method for doping of aluminum and aluminum-based alloys, both castable and wrought, holds much promise. It is not obvious that high-temperature exchange reactions in salt melts can be used to introduce refractory, scattered, and rare metals into aluminum. The authors have doped aluminum with small additions (less than 1 wt.%) of scandium, yttrium, zirconium, and hafnium.
Melting of salts and high-temperature exchange reactions were carried out in a Nabertherm L 9/11 muffle furnace. X-ray phase analysis (XPA) of melted (reaction) salts was performed on Shimadzu and DRON-2.0 diffractometers in CuK radiation with the angle interval 10° ≤ 2Θ ≤ 70°, a scanning step of 0.03°, and 2 s time in point. The phases were identified using the Powder Diffraction File JCPDSD-ICDD PDF2 (sets 1-47). The produced reaction salts were ground in an agate mortar and stored in an desiccator. The high-temperature exchange reactions were carried out in alundum crucibles at 750-780 °С; the salts were fed into the aluminum melt by means of a laboratory-scale injection plant (Fig. 1), and bottled carbon dioxide served as a transporting agent. The elemental analysis of the melts was performed on a Spectromass 2000 mass-spectrometer with inductively bound plasma.
Granular aluminum (p.a.) TU 6-09-02-529-92; NaF (p.a.) GOST 4463-76; KF (pure) GOST 20 848-75; Sc2O3 (pure) TU 48-4-417-87; Y2O3 (pure) TU 48-4-191-72; ZrO2 (pure) TU 6-09-2486-77; HfO2 (pure) TU 48-4-201-72 were used for synthesis.
The application of aluminothermal methods for the production of master alloys and alloys by injection of a gas-powder suspension through aluminum melt has been comprehensively examined by the authors and described in . The suspension consists of inert gas (argon Ar or carbon dioxide CO2) and a ground salt mixture of sodium fluoride and potassium chloride with additions of aluminum fluoride, which contains oxides or fluorides of metals introduced into the alloy at 700-900 С. A corresponding patent  has been acquired, and aluminum-scandium alloys have been obtained by the injection method in industrial furnaces at JS KUMZ, which was described in .
Mixtures of alkaline metal salts dissolve oxides and fluorides of other metals during melting forming complex compounds that easily interact with molten aluminum. This makes it possible not to use such expensive compounds as for example potassium fluozirconates (hafnates). The application of sodium and potassium fluoride melts for the dissolution of oxides holds much promise, which is demonstrated with an example of scandium oxide solubility in different salt systems (Fig. 2, curve 8). It was determined from the XPA data (Fig. 3) that scandium oxide dissolves during melting with sodium and potassium fluorides forming 2-potassium sodium hexafluoroscandiate (scandium cryolite-elpasolite) K2NaScF6. Yttrium oxide behaves in similar salt mixtures like scandium oxide. Zirconium and hafnium dissolve giving rise to oxyfluorides of variable composition, in much the same way as they behave during the formation of oxyfluorides from their dioxides when treated with concentrated solutions of hydrofluoric acid. As a result, Hf(Zr)F4∙nH2O is precipitated, and oxyfluorides are formed during drying in air at 200-250 С. The products of their thermal decomposition are Hf4F12O2 and Zr4F10O3.
A large number of salt systems (Fig. 2) based on fluoride-chloride salts of alkaline (Li, Na, K) and alkaline-earth (Сa) metals with introduced scandium, yttrium, zirconium, and hafnium fluorides or oxides have been studied to search for the optimal conditions of their displacement with more active aluminum. The eutectics melting temperatures vary depending on the composition of salt mixtures from 454 °С (for LiF-NaF-KF) to 965 °C (cryolite Na3AlF6) . The use of calcium salts allows a considerable reduction of the concentration of sodium in the final alloy, whose admixture may substantially increase the volume of rejects in the production of rolled stock. We have established the solubility values of scandium fluoride and oxide as a function of temperature; the application of scandium oxide lowers slightly its direct yield in the solution compared with scandium fluoride. For example, at 800 °С the solubility value in a calcium salt mixture is 0.6 wt.% for Sc2O3 and 3.4 wt.% for ScF3.
The application of sodium and potassium fluorides instead of chlorides not only increases the reactivity in high-temperature exchange reactions, but also reduces metal loss during evaporation since fluorides are less volatile than chlorides, although fluorides have higher melting temperatures (Table 1) [16,17].
The eutectic 0.4NaF + 0.6KF melts at 721 °С , which allows the exchange reactions to be carried out at temperatures below 800 °С. The thermodynamic calculations for the displacement reaction, for example, displacement of scandium by aluminum into alloy at 800 °С, give a value of yield of ~80%. It was determined experimentally that an increase in the temperature of interaction lowers the yield of scandium from the salt melt, whereas the process temperature of 700-750 °С provides a direct yield of scandium into alloy of 95% and more.
The economic effectiveness of production of alloys with unique properties (mechanical, thermal, corrosion, radiation etc.) can be enhanced by injection of prepared reaction powder into liquid aluminum. Vigorous agitation of alloy during injection promotes uniform distribution of introduced components and acceleration of the high-temperature reaction, which considerably reduces the doping time in whole. Besides, some impurities are removed from aluminum. The chemical composition of the alloy impurities during doping of A85 grade aluminum was determined as (initial Al – numerator, after melting – denominator, wt.%): Cu - 0.01/0.0019; Mg - 0.01/0.0007; Zn - 0.01/0.001; Mn - 0.01/0.003; Si - 0.05/0.038; Na - 0.0014/0.0012; and hydrogen < 0.29 m3/100 g.
On completing the injection with carbon dioxide and 5 min exposure, the slag was discharged (730-750 °С) and the obtained alloy was poured out into a cast-iron mold lined with hexagonal boron nitride. An averaged alloy sample was taken and analyzed; the results are presented in Table 2.
Note: The presented results are average data of three identical meltings.
The mass ratio of the fluoride melt to the aluminum melt during melting was determined by the solubility of the chosen metal oxides. For the salt/metal ratios less than 0.5 for Zr, 0.8 for Sc, and 1.0 for Y and Hf, the process of reduction of rare metals is inhibited, therefore the components pass into the alloy to a lesser extent, while salt/metal ratios of more than 1.2 lead to efficiency loss and a larger volume of recycling salts. Replacement of oxides to fluorides and oxyfluorides of the metals of the input increases direct access from 2 to 7%.
The injection method of alloy production allows one to combine necessary amounts of different ingredients in the form of fluoride and oxide compounds in the injected powder. Metals, that are electrochemically more positive than aluminum, can be reduced simultaneously, for example, scandium and zirconium, scandium and hafnium, yttrium and zirconium, yttrium and hafnium etc., which further facilitates the technology of alloy production. Note that the reaction powder should be produced by preliminary alloying of fluorides with the corresponding oxides or fluorides and subsequent grinding. Ground powder is very hygroscopic and should be used immediately or stored in a damp-proof place.
The work was carried out in accordance with the state assignment and R&D plans of the ISSC UB RAS (No. AAAA-A16-116122810213-2).
Fridlyander I. N. Modern aluminum and magnesium alloys and composite materials on their basis // Moscow: VIAM. 2002. P. 19.
Kablov E. N. No new materials – no future // Metallurg. 2013. No. 12. Pp. 4-8.
Zakharov V. V. Influence of scandium on the structure and properties of aluminum alloys // Metallovedenie i termicheskaya obrabotka metallov (Metallography and heat treatment of metals). 2003. No. 7. Pp. 7-15.
Zakharov V. V. On joint alloying of aluminium alloys with scandium and zirconium // Metallovedenie i termicheskaya obrabotka metallov (Metallography and heat treatment of metals). 2014. No. 6. Pp. 3-8.
Popova E. A., Shubin A. B., Kotenkov P. V., Brodova L. E. et al. Ligature Al-Sc-Zr and estimation of its modifying abilities // Rasplavy (Alloys). 2011. No. 1. Pp. 12-15.
Belov N. A. Alabin A. N. Prospective aluminum alloys with zirconium and scandium additions // Tsventye metally (Non-ferrous metals). 2007. No. 2. Pp. 99-106.
Fanhao Zeng, Changging Xia, Yi Gu. The 430 C isothermal section of the Al-4Mg-Sc-Zr quaternary system in the Al-rich range // J. Alloys and Compounds, 2004, v. 363, p.175-181.
Ibrokhimov N. F., Ganieva N. I., Berdiev A. E. Influence of yttrium on oxidation kinetics of solid alloy AMg2 // Doklady Akademii nauk Respubliki Tadzhikiskan, Fizicheskaya khimiya (Proceedings of the Academy of Sciences of the Republic of Tajikistan, Physical chemistry). 2013. Vol. 56. No. 7. Pp. 559-563.
Skorobagatko Yu. P. Modification of hypereutectic aluminum alloys with active additives // Metall i lityo Ukrainy (Metal and casting of Ukraine). 2009. No. 9. Pp. 19-28.
Kubaschewski O., Von Galdbeck. Phase diagram Hf-Al. In book: Hafnium: Physico-chemical Properties of its compounds and alloys. Atomic Energy Review, Special issue No. 8, IAEA, Vienna. 1981, p.58-60.
Suzdaltsev A. V., Nikolaev A. Yu., Zaikov Yu. P. Review of modern methods for producing Al – Sc master alloys // Tsvetnye metally (Non-ferrous metals). 2018. No. 1. Pp. 69-73.
Skachkov V. M., Yatsenko S. P. Production of Sc, Zr, Hf, Y alloys based on aluminium by high-temperature exchange reactions in salt melts // Tsvetnye metally (Non-ferrous metals). 2014. No. 3. Pp. 22-26.
Skachkov V. M., Varchenya P. A., Ovsyannikov B. V., Yatsenko S. P. Injection of scandium-containing process powders into aluminium alloys // Tsvetnye metally (Non-ferrous metals). 2013. No. 12. Pp. 81-86.
Ovsyannikov B. V., Yatsenko S. P., Varchenya P. A. et al. Production of aluminum-scandium alloys by injection of process powders into melt // Tekhnologiya metallov (Technology of metals). 2011. No. 5. Pp. 23-29.
Rabinovich V. A., Khavin Z. Ya. Quick Reference Handbook in Chemistry // 2nd revised and enlarged edition L.: Khimiya. 1978. P. 392.
Reference book under the editorship of V. I. Posypaiko and E. A. Alekseeva // Diagrams of fusibility of salt systems. V. II. M.: Metallurgiya. 1977. P. 304.