Patent Abstract:
A rivetable adhesive for use in a joint between dissimilar materials, comprising a liquid epoxy resin, an expoxidized polysulfide, a flexibilizer, a solid epoxy CTBN adduct based upon bisphenol A, a phenoxy resin, an impact modifier including methacrylate-butadiene-styrene, a curing agent; and a blowing agent. The adhesive finds particular suitability for use in riveting aluminum panels to steel structures, such as for forming automotive vehicle roof structures.

Full Description:
TECHNICAL FIELD 
       [0001]    The present invention pertains generally to adhesives and more particularly to paste adhesives for bonding dissimilar materials (e.g., steel and aluminum) in automotive vehicle structures. 
       BACKGROUND 
       [0002]    In the automotive vehicle field there is an ongoing need for reducing weight of vehicle components. Traditionally, many vehicle body components have been made from steel. Joining such parts typically has been done by welding. In recent years, vehicle manufacturers have sought to substitute other materials for steel. For example, due to its relatively high strength to weight ratio, aluminum has been examined as a substitute material. When steel and aluminum are employed in combination, unfortunately, welding is an impractical solution. There is thus a need for forming a relatively high integrity joint between steel and aluminum for such applications. 
         [0003]    One particular application that involves forming joints between steel and aluminum is the formation of vehicle roof structures. For these structures, efforts have been made to join an aluminum roof panel structure to a steel frame structure using rivets. When aluminum is attached to steel using rivets as mechanical fasteners, and the assembly is subjected to thermal cycling (such as under paint bake conditions), there results a potential for distortion of the assembly due to differing coefficients of thermal expansion. For instance, the aluminum experiences a bowing effect that increases any gap that may exist between aluminum and steel components. 
         [0004]    Efforts have been made to employ pumpable adhesives between steel and aluminum. By their nature, pumpable adhesives tend to have a relatively low viscosity. As a result, when employed between steel and aluminum, there is a propensity for the steel and aluminum to come into contact with each other during riveting. This creates the potential for galvanic corrosion at the points of contact. Such adhesives also have made it necessary is some instances to employ secondary applications of sealant for assuring moisture protection at the joints. 
         [0005]    What is needed is an adhesive and system for applying it that has characteristics sufficient for allowing riveting while still maintaining a separation between the steel and aluminum components during riveting. 
       SUMMARY OF THE INVENTION 
       [0006]    The teachings herein meet the above need by providing an improved adhesive and a method for robotically applying the adhesive. Though the teachings find application in riveting aluminum roof panels to steel frames, other applications are possible as well. As can be appreciated, the teachings herein provide a way to avoid galvanic corrosion between aluminum and steel when those materials are riveted in an assembly. The teachings herein also provide for assuring that a bond is maintained between aluminum and steel structures during thermal cycling (e.g., as part of a paint bake operation), which would otherwise cause the aluminum and steel to separate from each other. As a result, it is possible to achieve good water sealing performance in the resulting assemblies during paint bake operations, and the need for subsequent sealing operations can be avoided. 
         [0007]    The advantages herein are made possible by the use of a paste adhesive that is thermally activatable to expand and fill any gaps between aluminum and steel components during a paint bake operation. 
         [0008]    In one aspect, the teachings envision a rivetable adhesive for use in a joint between dissimilar materials, comprising a liquid epoxy resin, an expoxidized polysulfide, a flexibilizer, a solid epoxy CTBN adduct based upon bisphenol A, a phenoxy resin, an impact modifier including methacrylate-butadiene-styrene, a curing agent; and a blowing agent. 
         [0009]    In a more specific example, the teachings herein contemplate a rivetable adhesive for use in a joint between dissimilar materials, comprising an admixture of about 15 to about 25 parts by weight of a liquid epoxy resin reaction product of epichlorohydrin and bisphenol A having an epoxide equivalent weight per ASTM D-1652-11e1 of about 182 to about 192; about 10 to about 20 parts by weight of an epoxidized polysulfide; about 3 to about 20 parts by weight of a liquid epoxy resin reaction product of an epichlorohydrin and a polypropylene glycol; about 1 to about 5 parts by weight of a flexibilizer; about 3 to about 15 parts by weight of a solid epoxy carboxyl terminated butadiene-acrylonitrile (CTBN) adduct based upon bisphenol A: about 15 to about 25 parts by weight of an impact modifier of methacrylate-butadiene-styrene about 15 to about 30 parts by weight of phenoxy resin; about 1 to about 5 parts by weight of a dicyandiamide curing agent; an aromatic substituted urea curing agent accelerator in an amount of about 0.3 to about 1 parts by weight; and a blowing agent having a decomposition temperature of about 190 to about 220° C. 
         [0010]    The adhesives herein may be robotically applied to a substrate. For example, the adhesives may be applied to a steel structure, an aluminum structure or both (or between some other combination of dissimilar materials), and the structures may be bonded together with the adhesive (e.g., after subjecting the adhesive to heat from a paint bake operation as described herein). A rivet may join the dissimilar materials. 
     
    
     
       DESCRIPTION OF THE DRAWINGS 
         [0011]      FIG. 1  illustrates performance data in accordance with the present teachings. 
       
    
    
     DETAILED DESCRIPTION 
       [0012]    This application claims the benefit of the filing date of U.S. Provisional Application Ser. No. 61/816,394 filed Apr. 26, 2013, the contents of such application being hereby incorporated by reference for all purposes. 
         [0013]    The explanations and illustrations presented herein are intended to acquaint others skilled in the art with the teachings, its principles, and its practical application. Those skilled in the art may adapt and apply the teachings in its numerous forms, as may be best suited to the requirements of a particular use. Accordingly, the specific embodiments of the present teachings as set forth are not intended as being exhaustive or limiting of the teachings. The scope of the teachings should, therefore, be determined not with reference to the above description, but should instead be determined with reference to the appended claims, along with the full scope of equivalents to which such claims are entitled. The disclosures of all articles and references, including patent applications and publications, are incorporated by reference for all purposes. Other combinations are also possible as will be gleaned from the following claims, which are also hereby incorporated by reference into this written description. 
         [0014]    The teachings herein make advantageous use of an improved composition for bonding dissimilar materials, and particularly for bonding steel and aluminum. The teachings herein also make advantageous use of an improved method for bonding dissimilar materials, where the method employs robotic application of a paste adhesive between components (e.g., components made of dissimilar materials, such as steel and aluminum) to be joined. Use of a rivet for joining is also contemplated. 
         [0015]    The adhesive material may be a polymeric material that is activated to flow, seal, expand or any combination thereof. It may be a material that forms a foam (e.g., an acoustic foam or a structural foam). It may expand from its original volume to at least 50%, or even at least about 100% (e.g., in the range of about 80 to about 100%) or larger of its original volume. 
         [0016]    The adhesive material may be applied through a die associated with a robot arm. It may be applied at about room temperature. The adhesive may be heated to be applied above room temperature, but below a temperature at which it would be activated for curing, expanding or both. 
         [0017]    The adhesive material may be activated when subjected to heat during paint shop baking operations. In applications where the adhesive material is a heat activated, thermally expanding material, an important consideration involved with the selection and formulation of the material comprising the adhesive material is the temperature at which a material reaction or expansion, and possibly curing, will take place. For instance, in most applications, it is undesirable for the material to be reactive at room temperature or otherwise at the ambient temperature in a production line environment. More typically, the adhesive material becomes reactive at higher processing temperatures, such as those encountered in an automobile assembly plant, when the material is processed along with the automobile components at elevated temperatures or at higher applied energy levels, e.g., during paint or e-coat curing or baking steps. While temperatures encountered in an automobile assembly operation may be in the range of about 148.89° C. to 204.44° C. (about 300° F. to 400° F.), body and paint shop applications are commonly about 93.33° C. (about 200° F.) or slightly higher. Following activation of the adhesive material, the material will typically cure. Thus, it may be possible that the adhesive material may be heated, it may then expand, and may thereafter cure to form a resulting foamed material. 
       Examples 
       [0018]    Among the following examples are examples that illustrate materials that may are rivetable and exhibit attractive characteristics for the present application. The amounts shown are in preferred parts by weight. The teachings herein contemplate such amounts as well as amounts that are +/−10%, 20%, 30%, 40% or even 50% of those shown. Examples 2 and 3 exhibit particularly attractive viscosity characteristics and exhibit good riveting characteristics. Example 1 is included by way of comparison. The compositions need not necessarily employ the specific commercial examples as set forth in the following Table 1. The compositions may employ the general components as described in the following Table 1. The composition may employ ingredients that exhibit the characteristics set forth in the following Table 1. Even if not explicitly specified, relative proportions of ingredients are within the scope of the teachings herein. 
         [0000]    
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
             
           
               
                 TABLE 1 
               
               
                   
               
               
                   
                   
                   
                 Example 1 
                 Example 2 
                 Example 3 
               
               
                   
                   
                 Commercial 
                 (in parts 
                 (in parts 
                 (in parts 
               
               
                 Component 
                 Characteristic 
                 Example 
                 by weight) 
                 by weight) 
                 by weight) 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 Liquid epoxy resin 
                 Epoxide 
                 DER 331 
                 — 
                 16.48 
                 20.60 
               
               
                 reaction product 
                 equivalent 
                 from The 
               
               
                 of epichlorohydrin 
                 weight (g/eq) 
                 Dow 
               
               
                 and bisphenol A 
                 per ASTM D- 
                 Chemical 
               
               
                   
                 1652 of about 
                 Company 
               
               
                   
                 182-192 
               
               
                 Expoxidized 
                 Epoxide 
                 Thioplast 
                 8.00 
                 17.01 
                 15.36 
               
               
                 Polysulfide 
                 equivalent 
                 EPS-350 
               
               
                 including epoxy 
                 weight (g/eq) 
                 from Akzo 
               
               
                 terminated 
                 per ASTM D- 
                 Nobel 
               
               
                 polymer with 
                 1652-11e1 of 
               
               
                 diglycidyl ether of 
                 about 320 
               
               
                 bisphenol A and 
               
               
                 chains with 
               
               
                 polysulfide 
               
               
                 Liquid epoxy resin 
                 Epoxide 
                 DER 732 
                 6.70 
                 6.70 
                 12.92 
               
               
                 reaction product 
                 equivalent 
                 from The 
               
               
                 of epichlorohydrin 
                 weight (g/eq) 
                 Dow 
               
               
                 and 
                 per ASTM D- 
                 Chemical 
               
               
                 polypropylene 
                 1652-11e1 of 
                 Company 
               
               
                 glycol 
                 about 310-330 
               
               
                 Flexibilizer 
                 Polyurethane 
                 DY 965 from 
                 2.50 
                 2.50 
                 2.25 
               
               
                   
                 polyol 
                 Huntsman 
               
               
                 Solid epoxy resin 
                 Epoxide 
                 DER 662 
                 11.00 
                 — 
                 — 
               
               
                 reaction product 
                 equivalent 
                 from The 
               
               
                 of epichlorohydrin 
                 weight (g/eq) 
                 Dow 
               
               
                 and bisphenol A 
                 per ASTM D- 
                 Chemical 
               
               
                   
                 1652-11e1 of 
                 Company 
               
               
                   
                 about 590-630 
               
               
                 Solid epoxy 
                 Epoxide 
                 Araldite 
                 16.00 
                 5.00 
                 4.52 
               
               
                 carboxyl 
                 equivalent 
                 1522 ES 
               
               
                 terminated 
                 weight (g/eq) 
               
               
                 butadiene- 
                 per ASTM D- 
               
               
                 acrylontirile 
                 1652-11e1 of 
               
               
                 (CTBN) adduct 
                 about 1560- 
               
               
                 based upon 
                 1820 
               
               
                 bisphenol A 
               
               
                 Impact modifier of 
                   
                 Paraloid 
                 20.98 
                 20.98 
                 18.73 
               
               
                 methacrylate- 
                   
                 2691A from 
               
               
                 butadiene-styrene 
                   
                 the Dow 
               
               
                 (core-shell) 
                   
                 Chemical 
               
               
                   
                   
                 company 
               
               
                 Phenoxy Resin 
                   
                 TMEP-70 
                 24.77 
                 24.77 
                 19.35 
               
               
                   
                   
                 from 
               
               
                   
                   
                 Springfield 
               
               
                   
                   
                 Indus. 
               
               
                 Dicyandiamide 
                   
                 Dycanex 
                 2.85 
                 3.40 
                 3.40 
               
               
                 curing agent 
                   
                 1400B from 
               
               
                   
                   
                 Air Products 
               
               
                 Aromatic 
                 Melting point 
                 Omicure U- 
                 0.76 
                 0.76 
                 0.69 
               
               
                 substituted urea 
                 of 220-230° C. 
                 52M from 
               
               
                 curing accelerator 
                   
                 Emerald 
               
               
                 (e.g., [4,4′- 
               
               
                 Methylene bis 
               
               
                 (Phenyl Dimethyl 
               
               
                 Urea]) 
               
               
                 Calcined kaolin 
                 pH of about 6 
                 Satintone W 
                 5.49 
                 1.47 
                 1.25 
               
               
                   
                 and average 
                 from BASF 
               
               
                   
                 particle size of 
               
               
                   
                 about 1.3 μm 
               
               
                 Blowing agent of 
                 Decomposition 
                 Celogen 
                 0.90 
                 — 
                 — 
               
               
                 Activated 
                 temperature of 
                 754A from 
               
               
                 azodicarbonamide 
                 about 165 to 
                 Lion 
               
               
                   
                 180° C. 
                 Copolymer 
               
               
                 Blowing agent of 
                 Decomposition 
                 Celogen AZ- 
                 — 
                 0.90 
                 0.90 
               
               
                 Activated 
                 temperature of 
                 120 from 
               
               
                 azodicarbonamide 
                 about 190 to 
                 Lion 
               
               
                   
                 220° C. 
                 Copolymer 
               
               
                 Colorant 
                   
                 Pigment 
                 0.05 
                 0.03 
                 0.03 
               
               
                   
               
             
          
         
       
     
         [0019]      FIG. 1  illustrates capillary viscosity data obtainable using the compositions of the teachings herein. As seen, the Example 1 formulation has a much higher viscosity than the viscosity of the Example 2 and 3 formulations. Two different test temperatures are used to cover the range of viscosities among the three materials. The reference test method for capillary viscosity employed is ASTM D 3835-08, pursuant to which the test parameters for the capillaries are as follows: diameter=1 mm, length=16 mm. 
         [0020]    As seen from  FIG. 1 , Examples 2 and 3 exhibit a capillary viscosity well below 1000 PaS at temperatures of 70 or 90° C. and a shear rate (sec−1) of 200 or higher. For use herein, it is desirable for materials to exhibit a capillary viscosity in the range of about 100 to about 700 PaS for a shear rate (sec−1) of about 100 to about 1000 at a temperature of 70 or 90° C. For example, it is desirable for materials to exhibit a capillary viscosity in the range of about 100 to about 700 PaS for a shear rate (sec−1) of about 100 to about 1000 at a temperature of 70 or 90° C. Materials may exhibit a capillary viscosity in the range of about 100 to about 400 PaS for a shear rate (sec−1) of about 400 to about 1000 at a temperature of 70 or 90° C. For certain applications it is desirable that the materials (at 70 or 90° C.) will have a capillary viscosity at shear rate (sec−1) in the range of about 200 to about 400 that is less than 700 PaS, or even less than 500 PaS. The materials (at 70 or 90° C.) will typically exhibit a capillary viscosity of at least about 100 PaS at a shear rate (sec−1) of about 200 to about 1000. 
         [0021]    As used herein, unless otherwise stated, the teachings envision that any member of a genus (list) may be excluded from the genus; and/or any member of a Markush grouping may be excluded from the grouping. 
         [0022]    Unless otherwise stated, any numerical values recited herein include all values from the lower value to the upper value in increments of one unit provided that there is a separation of at least 2 units between any lower value and any higher value. As an example, if it is stated that the amount of a component, a property, or a value of a process variable such as, for example, temperature, pressure, time and the like is, for example, from 1 to 90, preferably from 20 to 80, more preferably from 30 to 70, it is intended that intermediate range values such as (for example, 15 to 85, 22 to 68, 43 to 51, 30 to 32 etc.) are within the teachings of this specification. Likewise, individual intermediate values are also within the present teachings. For values which are less than one, one unit is considered to be 0.0001, 0.001, 0.01 or 0.1 as appropriate. These are only examples of what is specifically intended and all possible combinations of numerical values between the lowest value and the highest value enumerated are to be considered to be expressly stated in this application in a similar manner. As can be seen, the teaching of amounts expressed as “parts by weight” herein also contemplates the same ranges expressed in terms of percent by weight. Thus, an expression in the of a range in terms of “x parts by weight of the resulting polymeric blend composition” also contemplates a teaching of ranges of same recited amount of “x” in percent by weight of the resulting polymeric blend composition.” 
         [0023]    Unless otherwise stated, all ranges include both endpoints and all numbers between the endpoints. The use of “about” or “approximately” in connection with a range applies to both ends of the range. Thus, “about 20 to 30” is intended to cover “about 20 to about 30”, inclusive of at least the specified endpoints. 
         [0024]    The disclosures of all articles and references, including patent applications and publications, are incorporated by reference for ail purposes. The term “consisting essentially of to describe a combination shall include the elements, ingredients, components or steps identified, and such other elements ingredients, components or steps that do not materially affect the basic and novel characteristics of the combination. The use of the terms “comprising” or “including” to describe combinations of elements, ingredients, components or steps herein also contemplates embodiments that consist of, or consist essentially of the elements, ingredients, components or steps. 
         [0025]    Plural elements, ingredients, components or steps can be provided by a single integrated element, ingredient, component or step. Alternatively, a single integrated element, ingredient, component or step might be divided into separate plural elements, ingredients, components or steps. The disclosure of “a” or “one” to describe an element, ingredient, component or step is not intended to foreclose additional elements, ingredients, components or steps. 
         [0026]    It is understood that the above description is intended to be illustrative and not restrictive. Many embodiments as well as many applications besides the examples provided will be apparent to those of skill in the art upon reading the above description. The scope of the invention should, therefore, be determined not with reference to the above description, but should instead be determined with reference to the appended claims, along with the full scope of equivalents to which such claims are entitled. The disclosures of all articles and references, including patent applications and publications, are incorporated by reference for all purposes. The omission in the following claims of any aspect of subject matter that is disclosed herein is not a disclaimer of such subject matter, nor should it be regarded that the inventors did not consider such subject matter to be part of the disclosed inventive subject matter.

Technology Classification (CPC): 2