Patent Abstract:
A method for forming a semiconductor device with more than two gates involves the forming of a stack of n-conductive gate electrodes, where n&gt;2. Silicon is formed around the gate stack and the silicon is doped to form source/drain regions. The multiple gates maximize the drive current for a given silicon area.

Full Description:
FIELD OF THE INVENTION  
         [0001]    The present invention relates to the field of semiconductor processing, and more particularly, to the formation of semiconductor devices with multiple gates.  
         BACKGROUND OF THE INVENTION  
         [0002]    A conventional MOSFET operates by driving current through the channel region between the source and drain of a device. The conductivity of the channel region is modulated by the application of a voltage on the conducting gate above the channel surface and insulated from it. Efforts are ongoing within many MOS integrated circuit manufacturing companies as well as at many universities and government laboratories to improve the speed and available drive currents of MOSFETS to reduce their power consumption, and to improve their reliability and radiation hardness for applications in harsh or remote environments, including space.  
           [0003]    Silicon-on-insulator (SOI) is a generic term describing technologies in which the MOSFET&#39;s or other active devices are built in a thin film of silicon over an insulating layer on a substrate. The presence of the insulator reduces the parasitic capacitances in the MOSFET compared to a bulk silicon device, resulting in an improvement in the speed and power dissipation of MOS integrated circuits, as well as improved immunity to single-upset of MOS memory elements in a radiation environment.  
           [0004]    One of the goals in semiconductor processing is to maximize the use of the available silicon area. This allows increased miniaturization of the electronic circuitry. In particular, it is desirable to maximize the drive current for a given silicon area. Dual gate devices in which the drive current is doubled or a given silicon area have been created. Further improvement in maximizing the drive current for a given silicon area is desirable.  
         SUMMARY OF THE INVENTION  
         [0005]    There is a need for a method of forming a MOS device with improved drive current performance for a given silicon area.  
           [0006]    These and other needs are met by embodiments of the present invention that provide a method of forming an n-gate semiconductor device where n is greater than 2, comprising the steps of forming a stack of n-conductive gate electrodes, where n is greater than 2. Silicon is formed around the gate stack and the silicon is doped to form source/drain regions. In certain embodiments of the invention, the formation of the stack includes forming n-polysilicon layers, with each polysilicon layer having a first oxide layer directly beneath the polysilicon layer and a second oxide layer directly above the polysilicon layer. In certain embodiments, nitride layers are formed between the polysilicon layers and the stack is formed by first anisotropically etching the polysilicon layers, the nitride layers and the oxide layers to form a stack precursor, and then removing the nitride layers and at least some of the oxide layers in the stack precursor to create gaps between the polysilicon layers and the stack precursor. A gate dielectric material may be formed on the polysilicon layers and the stack precursor.  
           [0007]    With the present invention, a greater number of gates than two can be formed in a stack of a semiconductor device. This n-gate device provide additional drive current for a given silicon area. For example, in the embodiments of the invention in which three gates are provided in the stack, four conductive channels are formed in the present invention and four times the drive current compared to a single conductive channel is achieved.  
           [0008]    The earlier stated needs are also met by other embodiments of the present invention which provide a method of forming a MOS device having more than two gates, comprising the steps of forming a plurality of polysilicon gates in a stack, the plurality including at least three said gates. Gate dielectric is formed on each of the gates and silicon is formed with source/drain regions adjacent the gates and gate dielectric.  
           [0009]    The foregoing and other features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.  
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0010]    [0010]FIG. 1 is a schematic depiction of a portion of a semiconductor device during one phase of manufacture in accordance with embodiments of the present invention.  
         [0011]    [0011]FIG. 2 depicts the structure of FIG. 1 following the oxidation of silicon layers in the stack precursor in accordance with embodiments of the present invention.  
         [0012]    [0012]FIG. 3 shows the structure of FIG. 2 following etching through of the buried oxide layer through a seed window in accordance with embodiments of the present invention.  
         [0013]    [0013]FIG. 4 depicts the structure of FIG. 3 following the removal of nitride layers in the stack precursor.  
         [0014]    [0014]FIG. 5 depicts the structure of FIG. 4 following the removal of oxide layers and the oxidized regions of the polysilicon layers in the stack precursor in accordance with embodiments of the present invention.  
         [0015]    [0015]FIG. 6 shows the structure of FIG. 5 after gate dielectric has been formed on the silicon layers of the stack precursor, in accordance with embodiments of the present invention.  
         [0016]    [0016]FIG. 7 shows the structure of FIG. 6 after the growth of a silicon layer and polishing of the silicon layer in accordance with embodiments of the present invention.  
         [0017]    [0017]FIG. 8 depicts the structure of FIG. 7 after the silicon has been doped and etched in accordance with embodiments of the present invention.  
         [0018]    [0018]FIG. 9 shows the structure of FIG. 8 following the filling of the recesses in the buried oxide layer and formation of a layer of oxide and polishing, in accordance with embodiments of the present invention.  
         [0019]    [0019]FIG. 10 shows the structure of FIG. 9 after a silicidation process has been performed to create silicide regions, in accordance with embodiments of the present invention. 
     
    
     DETAILED DESCRIPTION OF THE INVENTION  
       [0020]    The present invention addresses and solves problems related to maximizing the drive current for a given silicon area in the formation of MOS devices. This is achieved, in part, by the provision of a method of forming a MOS device with a greater number of gates, such as three gates or more. The multiple gates of the MOS device are formed by creating a stack of silicon layers, nitride layers and oxide layers and then etching to form a stack precursor. The nitride layers and oxide layers are removed. Dielectric is then formed around the polysilicon layers as a silicon region is formed around the gate dielectric and the polysilicon gates. After doping and silicidation, a semiconductor device having at least three gates is created.  
         [0021]    [0021]FIG. 1 schematically depicts a portion of a semiconductor wafer constructed in accordance with embodiments of the present invention during one phase of manufacture. A silicon substrate  10  is provided with an insulator layer  12  formed thereon. The insulator layer  12  may be a buried oxide layer, for example. In certain preferred embodiments of the invention, the buried oxide layer may  12  be between 100 to 200 nm thick.  
         [0022]    A series of layers are formed on the buried oxide layer  12  and then etched anisotropically to form a stack precursor  14  as depicted in FIG. 1. The anisotropic etching may be performed by conventional methodologies, including, for example, employing reactive ion etches with suitable etch recipes for the various materials in the different layers.  
         [0023]    The stack precursor  14  includes a number of polysilicon layers  16   a - c , a number of nitride layers  18   a - b  and a number of oxide layers  20   a - e . In certain preferred embodiments of the invention, the thickness of the polysilicon layers  16   a - 16   c  is between 25 to 35 nm. In certain embodiments of the invention, the top polysilicon layer  16 C has a greater thickness than the polysilicon layers  16   a - 16   b . For example, the upper polysilicon layer  16   c  may have a thickness of between about 35 to about 45 nm.  
         [0024]    The thickness of the oxide layers  20   a - 20   d  may be between about 1 to about 10 nm in exemplary embodiments of the invention, with a preferred thickness of about 2 nm. Nitride layers  18   a - 18   b , in exemplary embodiments of the invention, have a thickness of between about 2 to about 5 nm. In other embodiments of the invention, the thickness of the nitride is between about 5 to about 10 nm.  
         [0025]    In certain embodiments of the invention, the thickness of the top oxide layer  20   e  is between about 40 to about 60 nm, with a preferred thickness of about 50 nm. It should be recognized that all of the above thickness ranges are exemplary only, as other thicknesses may be employed without departing from the scope of the present invention.  
         [0026]    Following the formation of the stack precursor  14 , the polysilicon layers  16   a - 16   c  are oxidized at a temperature of between about 900 to about 1000° C. in order to grow oxide on the sides of the polysilicon layers  16   a - 16   c . This is depicted in FIG. 2 in which approximately 10 to approximately 15 nm of oxide  22  is formed on the sides of the polysilicon layers  16   a - 16   c.    
         [0027]    [0027]FIG. 3 shows the structure of FIG. 2 after a seed window mask has been formed and patterned and an etch is made to etch recesses  24  in the buried oxide layer  12 , stopping on the silicon substrate  10 . A conventional etch recipe may be employed to etch the buried oxide layer  12  to create the recesses  24 . The seed window is then removed, resulting in the structure of FIG. 3.  
         [0028]    Following the etching of the recesses  24  into the buried oxide layer  12 , the nitride layers  18   a - 18   b  are removed by a wet etch, such as hot phosphoric acid. This results in the structure of FIG. 4 in which gaps are created between the oxide layers  20   c - 20   d  and  20   a - 20   b.    
         [0029]    Next, as seen in FIG. 5, the relatively thin oxide layers  20   a - 20   d  and the oxidized regions  22  on the silicon layers  16   a - 16   c  are partially removed. The thicker oxide layer  20   e  and the buried oxide layer  12  may be etched slightly, but substantially remain after the etching. A buffered oxide etch may be used to remove the oxide layers  20   a - 20   d  and the oxidized polysilicon regions  22 .  
         [0030]    As seen in FIG. 6, a gate dielectric  26  is grown around each of the silicon layers  16   a - 16   c . The gate dielectric  26  may be a conventional gate dielectric, such as silicon dioxide. A conventional thermal process may be employed to form the gate dielectric  26 . Alternatively, high k material, such as HfO 2  or Hf silicate, can be deposited as the gate dielectric  26 .  
         [0031]    Silicon is then epitaxially grown to form a silicon layer  28 , as depicted in FIG. 7. The silicon layer  28  in FIG. 7 has been polished, with the polishing stopping on the oxide layer  20   e . A thickness of between about 2500 to about 5000 Å may be formed in exemplary embodiments of the present invention. A conventional method for epitaxially growing silicon may be employed.  
         [0032]    An anisotropic etch of the silicon layer  28  is then performed. This may be done in a conventional manner, such as by creating a mask of photoresist material and etching the silicon layer  28  in accordance with the pattern formed in the mask. The photoresist mask is then removed. The results of the etching are depicted in FIG. 8.  
         [0033]    In FIG. 9, an insulative material, such as oxide, is formed at an insulating layer  30 . The oxide may be derived from TEOS, for example. The oxide fills the recesses  24  in the buried oxide layer  12 . After creation of the insulating layer  30 , a polishing step is performed to remove excess oxide.  
         [0034]    The doping of the silicon may then be performed, either after the FIG. 9 structure has been reached, or after previous structures have been created, such as those in FIGS. 7 and 8 in alternate embodiments. Doping provides dopants, such as boron or arsenic, or other known dopants, into the silicon  28 . For boron, an exemplary implantation energy may be between about 30 to about 50 KeV. For arsenic, an exemplary implantation energy is about 150 to about 250 KeV. The dopants are activated by an annealing step, as is conventionally is performed.  
         [0035]    In FIG. 10, the multiple gate transistor is depicted with silicide regions formed in the source and drain regions  32  of the now-formed transistor  36 . The silicide regions  34  are formed in a self-aligned silicidation process, as is conventionally known. For example, a metal layer is deposited over the wafer and annealing steps are performed to cause the metal to react with the underlying silicon  28  and form low resistivity silicon regions  34 . Exemplary metals for the metal layer include, but are not limited to, cobalt, titanium, tungsten, nickel, platinum, palladium, molybdenum, etc. The silicide  34  provides low resistivity contacts to the source and drain regions  32  of the transistor  36 . Any unreacted metal is removed following the rapid thermal anneal or laser thermal anneal that is performed to create silicide regions  34 . FIG. 10 depicts the structure after the metal layer has been removed.  
         [0036]    The present invention thus provides a transistor with more than two gates, thereby maximizing the drive current for the silicon area. An embodiment in which a semiconductor device has three gates is depicted and described, but the process can be readily extended to produce transistors having a number of gates greater than three.  
         [0037]    Although the present invention has been described and illustrated in detail, it is to be clearly understood that the same is by way of illustration and example and is not to be taken by way of limitation, the scope of the present invention being limited only by the terms of the appended claims.