Patent Abstract:
A welding method and apparatus are provided for forming a weld joint between first and second elements of a workpiece. The method includes heating the first and second elements to form an interface of material in a plasticized or melted state interface between the elements. The interface material is then allowed to cool to a plasticized state if previously in a melted state. The interface material, while in the plasticized state, is then mixed, for example, using a grinding/extruding process, to remove any dendritic-type weld microstructures introduced into the interface material during the heating process.

Full Description:
CROSS REFERENCE TO RELATED APPLICATION 
     This application is a division of application Ser. No. 09/994,506 filed on Nov. 27, 2001 now abandoned. 
    
    
     ORIGIN OF THE INVENTION 
     This invention was made by employees of the United States Government and may be manufactured and used by or for the Government for governmental purposes without the payment of any royalties. 
    
    
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to a welding method and apparatus, and in particular, to a welding method and apparatus which separately plasticizes or melts the surfaces to be joined followed by a subsequent weld matrix mixing process. 
     2. Background of the Invention 
     Welding processes can be classified into one of two categories, fusion welding and solid state welding. Fusion welding involves melting material to be welded and includes such processes as MIG, TIG and VPPA welding. Solid state welding joins materials without a melting step and include the processes of friction stir and inertia welding. Fusion weld processes typically result in a dendritic type weld microstructure exhibiting inferior mechanical and structural properties. Such inferior material properties are generally seen in metals subsequent to melting. Conversely, solid state weld processes result in a non-dendritic grain structure exhibiting properties superior to those produced with fusion welding processes. 
     Both fusion welding and solid state welding have respective limitations. As indicted above, fusion welding compromises the microstructure of the material and thus lessens the physical properties and characteristics of the material. Solid state welding such as inertia welding is limited to rounded structures such as pipe or rod structures. 
     A recent advancement was made when friction stir welding became available for the solid state welding of materials. Reference is made, for example, to U.S. Pat. Nos. 6,168,067 B1 to Waldron et al. and 6,053,391 to Heideman et al. With the use of friction stir welding, a solid state weld could, for the first time, be provided in applications requiring longitudinal welds, ranging from several inches to an unlimited length. As described in more detail in the aforementioned patents, the friction stir weld process uses a rotating shoulder/pin configuration. The shoulder produces frictional heat to bring the material into a plasticized state and forges the welded material with extremely large forces. To accomplish the necessary large forces for the forging effect, a very robust backing anvil is required for support. The welding pin spins inside the workpiece at the same rate as the shoulder. The dependent motion of the welding pin and shoulder restricts the speed of the welding process. 
     BRIEF SUMMARY OF THE INVENTION 
     In accordance with the present invention, a welding method and apparatus are provided for forming a weld joint. The method separates the welding process into separate and discrete steps, one providing heating of first and second abutting elements to be welded to form an interface therebetween of plasticized or melted material and a further matrix transformation step for processing the interface material after cooling to a plasticized phase. The heating process may use any conventional fusion welding process such as laser or plasma torch which initially melts the interface material. Subsequently, a separate grinding/extrusion element recrystallizes possible, undesirable dendritic matrix structures while the interface material is in the plasticized temperature state. Advantageously, separate heating sources can be used to plasticize or melt the respective first and second elements forming the weld joint independently. The independent melting feature provides for the joining of dissimilar metals such as copper and aluminum or stainless steel and titanium. 
     According to one aspect of the present invention, a welding method is provided for joining a workpiece comprising first and second elements in abutting relation along facing surfaces. The method includes heating the first and second element to plasticize or melt the elements at least at the facing surfaces so as to form an interface therebetween of material in a melted state. If the interface material is heated to a melted state, then the interface material is allowed to cool from the melted state to a plasticized state. Next, the interface material is mixed while in the plasticized state. 
     According to another aspect of the present invention, an apparatus is provided for forming a weld joint in a workpiece between first and second elements in abutting relation along facing surfaces. The apparatus includes a heating device for plasticizing or melting the first and second elements at least at the facing surfaces so as to form interface therebetween of material in a plasticized or melted state respectively. A mixing tool mixes the interface material when in a plasticized state. 
     Preferably, the apparatus further comprises forming means for exerting force on the elements to control forming thereof. Advantageously, the temperature of the forming means is controlled to provide heating or cooling of the elements. 
     In one preferred embodiment, the forming means comprises at least one forging plate. Advantageously, the apparatus further comprises control means for sensing the force exerted by the forging plate and for controlling feeding of the first and second elements based thereon. Preferably, the control means controls one of feed rate and travel speed to control feeding of the elements. 
     In another preferred embodiment, the forming means comprises a plurality of rollers. In this embodiment, the apparatus preferably further comprises control means for controlling the force exerted by the rollers and for controlling feeding of the first and second elements based thereon. Preferably, the control means controls one of feed rate and travel speed to control feeding of said elements. 
     Preferably, the apparatus further comprises control means for sensing energy input to the heating elements and for controlling one of feed rate or travel speed of the elements based thereon. 
     In a preferred implementation, the apparatus further comprises a pre-weld tack welding means located upstream of the mixing tool for tack welding the two elements together prior to mixing by the mixing tool. 
     Advantageously, the mixing tool is retractable so as to enable complete withdrawal thereof from the first and second elements. 
     Preferably, the apparatus further comprises containment forging plates for containing the first and second elements during mixing by the mixing tool. 
     According to yet another aspect of the present invention, a joined workpiece has a first element comprising a first metal material having a first plasticized temperature and a second element comprising a second metal material having a second plasticized temperature different from the first plasticized temperature. A longitudinal weld joint is formed between the first metal element and the second metal element. The weld joint has a recrystallized fine grain matrix. 
     A key feature of the present invention relates to the separation of a heating process to form a plasticized or melted interface material between two elements to be joined and a mixing process for mixing the interface material together while in a plasticized state. This separation enables each of the respective materials being joined to be heated and plasticized/melted independently. One advantage of this feature is that the invention enables dissimilar metals to be welded together which previously were not able to be joined, i.e., metals such as copper/aluminum, stainless steel/copper, and stainless steel/titanium. For example, a copper/aluminum weld can be achieved by providing independent temperature control as each alloy is brought up to its respective plasticized/melted state. A further advantage of separating the heating process from the weld matrix transformation process is that comparatively high workpiece travel rates during welding can be obtained. In this regard, the present invention is not inherently limited with respective to travel rates as is the case with a friction stir welding process. 
     An additional important feature of the present invention is that the invention provides matrix transformation of the interface material from dendritic to fine grained material. More specifically, the present invention provides for transforming grain structure from the dendritic-type weld microstructure formed as a result of the heating process to a recrystallized fine, non-dendritic grain structure. As a consequence, the resulting final grain structure is typically that of a solid state weld material and thus exhibits excellent mechanical material properties. 
     A further advantage of the present invention is that the invention can provide long longitudinal welds of varying material thickness. 
     Yet another advantage of the present invention is that the invention can be used to form longitudinal welds exhibiting a solid state weld material property without a backing anvil such as is required in stir welding. 
     Further features and advantages of the present invention will be set forth in, or apparent from, the detailed description of preferred embodiments thereof which follows. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWING 
         FIG. 1  is a longitudinal cross sectional view of a welding apparatus according to a preferred embodiment of the present invention; 
         FIG. 2  is an end elevational view of the welding apparatus of  FIG. 1 ; and 
         FIG. 3  is a longitudinal cross sectional view, partially broken away, of a further embodiment of the invention. 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Referring now to  FIG. 1  and  FIG. 2 , there is shown a welding device, generally denoted  10 , which is adapted to join together first and second elements  14  and  16  of a workpiece  12 . The welding device  10  includes heating elements  18  and  20 . 
     Heating element  18  provides sufficient heat to plasticize or melt the material of element  14  and may comprise such conventional heating devices as lasers or plasma torches or other suitable devices known in the art. Similarly, heating element  20  provides sufficient heat to plasticize or melt the material of element  16 . As a result, together, heating elements  18  and  20  transform a portion of the solid material of the workpiece  12 , viz., respective abutting portions of elements  14 ,  16  to form an interface  34  (see  FIG. 2 ) in a plasticized or melted phase, between the elements  14 ,  16 . 
     The heating elements  18  and  20  can be controlled individually for providing heating at a desired separate temperature. For example, where elements  14  and  16  comprise dissimilar materials having different melting points, heating element  18 , preferably provides heating at the plasticizing or melting temperature of element  14  whereas heating element  20  preferably provides heating at the plasticizing or melting temperature of the material of element  16 . 
     The material of element  14  and element  16  may be formed of the same or different metal material. For example, element  14  may be copper or stainless steel, and element  16  may be aluminum, copper or titanium, so that when joined together, elements  14  and  16  form a workpiece  12  formed of copper/aluminum, or stainless steel/copper or stainless steel/titanium or another combination. 
     In an alternative embodiment, additional heating elements (not shown) of the type of heating elements  18 ,  20  may be disposed adjacent to the heating elements  18 ,  20  and/or below workpiece  12 , to assist in plasticizing/melting the abutting portions of the elements  14 ,  16 . An optional tack weld heater  22 , disposed upstream, relative to the heaters  18  and  20 , provides sufficient heat to form an initial tack weld between the elements  14 ,  16 . 
     As shown in  FIG. 2 , a pair of clamping elements  36 ,  38  apply a respective force on the workpiece  12  towards each other. The force applied maintains elements  14  and  16  in proper alignment with each other. 
     A mixing tool such as toothed grinding/extruding member  40  is positioned in the path of the interface  34  between elements  14  and  16  and rotates to mix the material of interface  34  when in a plasticized phase. The grinding/extruding member  40  allows plasticized metal of the interface  34  to flow and extrude through the individual teeth, which are indicated at  40   a , of member  40 . The teeth  40   a  are angled, thus forcing the plasticized material to flow downwards or upwards depending upon the angle of the teeth  40   a . As a result, the grinding/extruding member  40  will recrystallize the dendritic matrix structure which may have been formed in the material of interface  34  as a result of the melting process. Grinding/extruding member  40  is retractable as indicated by arrow A and can be completely withdrawn from the workpiece formed by elements  14  and  16 . 
     A plurality of force actuators  42  are located downstream of grinding member  40  and used to apply a force on a pair of forging plates  44 ,  46  which are located on opposite sides of workpiece  12 . Force actuators  42  include rollers  42   a  which engage and bear against plates  44 ,  46 . In an alternative embodiment, plates  44 ,  46  can be eliminated and rollers  42   a  used to bear directly on the workpiece, i.e., either rollers, or plates, can be used separately to exert the required force to further form the workpiece. Further, the rollers or forging plates can be heated or cooled (e.g., by water cooling) to control the temperature of the workpiece material. 
     As indicated in the drawings, the heating elements described above and the grinding member  40  extend through forging plates  44 ,  46  so as to permit them to perform their respective functions. The force exerted upon the forging plates  44 ,  46  by the force actuators  42  is constant for a workpiece having constant thickness, while a variable force is exerted on the forging plates  44 ,  46  by the actuators  42  to accommodate workpieces of a tapered thickness. 
     A pair of motion control devices indicated separately at  48  control the amount of movement of the forging plates  44 ,  46 . The motion control devices  48  each may comprise a LVDT, a laser device or other suitable motion control device known in the art. 
     During the operation of the welding device  10 , the workpiece  12  is inserted into an entrance  50  of a housing  52  which houses the various elements and units described above. As set forth hereinbefore, the heating elements  18 ,  20  provide the desired heating of elements  14  and  16 , to form the plasticized or melted phase interface  34 . 
     During the heating process, undesirable dendritic-type Weld microstructures may be introduced into the matrix of the interface material  34 . Advantageously, the heating process takes place in an inert environment. For example, nitrogen gas can be pumped into housing  52  to provide an inert environment, thereby reducing or eliminating the oxidation of the material of workpiece  12  during the heating process. 
     The workpiece  12  proceeds through the welding device  10  in a direction denoted by arrow  54 . The material of interface  34  is in a plasticized or melted state while in the area generally indicated by reference numeral  56 . As the workpiece  12  proceeds along direction  54 , if the interface was heated to a melted state, the melted interface is transformed into a plasticized state. The transition point where the melted interface becomes plasticized is denoted by a dashed line  58 . The workpiece  12  transitions from the melted state to the plasticized state due to the absence of applied heat. Alternatively, if the material of interface  34  is merely heated to a plasticized state, the interface material remains in a plasticized state as the workpiece proceeds past dashed line  58 . 
     The workpiece  12  then proceeds to the location the grinding/extruding member  40 . The interface  34 , now in the plasticized state, is processed by the grinding/extruding teeth  40   a  of member  40  and the plasticized material of interface  34  flows and is extruded through the teeth  40   a . As indicated above, this processing of the interface material dramatically recrystallizes the grain structure, thus producing a fine grained weld matrix when fully cooled. 
     As shown in the drawings, member  40  includes a central mixing portion comprising the grinding/extruding teeth  40   a  extending along the length thereof and support portions directly connected to the central portion. Considering, for example, the upper support portion, this portion extends through an opening in forging plate  44  which terminates at a major surface at plate  44 , as illustrated. 
     The workpiece  12  next travels past the grinding/extruding member  40  to a location where the hot interface material, which is still in a plasticized state, is forged under pressure by the forging plates  44 ,  46 . 
     In an advantageous embodiment, a controller or control system  60  is employed which controls the feed rate or travel speed of the workpiece formed by elements  14  and  16  by controlling the force exerted by either the forging plates  44 ,  46  and/or rollers  42   a  (whether used separately or in combination, as indicated schematically by the dashed lines in  FIG. 1 ). Although a separate controller  60  is shown, the control system could directly control force actuators  42 . 
     Alternatively, or in addition, a control system or controller  62  is also provided which controls the material feed rate or travel speed by monitoring or sensing the energy input to the heating elements  18  and  20 , or as illustrated, the energy input to a further heating element  64 . The overall control system could also include a sensor  66  for sensing feed rate or travel speed and supplying a corresponding input signal to controller  62 . 
     Referring to  FIG. 3 , in accordance with a further important feature of the invention, separate containment forging plates  68  and  70  are provided closely adjacent to or, in one embodiment, in surrounding relation to, the mixing tool  40  so as to contain the heated material of elements  14 ,  16  during rotation of the grinding teeth  40   a  of mixing tool  40 . 
     It should be apparent to those of ordinary skill that the present device and process offers important advantages over previous welding methods. These advantages include the ability to weld together dissimilar alloys which previously could not be joined due to differences in their respective melted and plasticized phase temperatures. Further, the separation of the plasticizing/melting process and interface matrix transformation process results in significantly enhanced welding speeds. 
     Although the invention has been described above in relation to preferred embodiments thereof, it will be understood by those skilled in the art that variations and modifications can be effected in these preferred embodiments without departing from the scope and spirit of the invention.