Patent Abstract:
A method of surface pre-treatment of a variety of ink-receiving substrates of different types includes applying treatment energy to the surface of the substrates in a controlled atmosphere that contains nitrogen and oxygen. The amount of energy per surface area is adjusted dependent upon the type of substrate. The ratio of oxygen to nitrogen in the controlled atmosphere is adjusted dependent upon the type of substrate.

Full Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
       [0001]    This application is a Continuation of International Application No. PCT/EP2014/057808, filed on Apr. 16, 2014, and for which priority is claimed under 35 U.S.C. §120. PCT/EP2014/057808 claims priority under 35 U.S.C. §119(a) to Application Nos. 13165163.0 and 13166468.2, filed in Europe on Apr. 24, 2013 and May 3, 2013, respectively. The entire contents of each of the above-identified applications are hereby incorporated by reference into the present application. 
     
    
     BACKGROUND OF THE PRESENT INVENTION 
       [0002]    1. Field of the Invention 
         [0003]    The present invention relates to a method of surface pre-treatment of a variety of ink-receiving substrates of different types, wherein treatment energy is applied to the surface of the substrates in a controlled atmosphere that contains nitrogen and oxygen, and the amount of energy per surface area is adjusted dependent upon the type of substrate. 
         [0004]    2. Description of Background Art 
         [0005]    When liquid ink is to be applied to the surface of the substrate, e.g. in an ink jet printer, it is frequently desired or necessary to pre-treat the substrate in order to increase the surface energy of the substrate to such a level that the surface can be wetted with the liquid ink. The pre-treatment may for example be a plasma treatment in which a plasma jet is directed onto the surface of the substrate so that ions contained in the plasma will react with the substrate surface. In another embodiment, the pre-treatment may include a corona discharge. In any case, the pre-treatment includes a transfer of energy to the surface of the substrate in order to induce a reaction that modifies the chemical and/or physical properties of the substrate surface. 
         [0006]    U.S. Pat. No. 7,150,901 discloses a method of the type indicated above, wherein a plasma treatment is performed in the presence of ambient air or in a pure nitrogen atmosphere. 
         [0007]    JP 6 041 337 A discloses a method for controlling the surface energy of a plastic substrate by means of a plasma or corona treatment with a mixed gas containing a fluorine-containing compound, while adjusting the mixing ratio of the components of the mixed gas. 
         [0008]    When an ink droplet is applied to the surface of the substrate, the size of the resulting ink dot will depend upon the speed with which the liquid ink spreads over the surface of the substrate, in relation to the speed with which the ink dries-out by evaporation of the solvent, and in relation to the speed with which the liquid is absorbed into the substrate. 
         [0009]    The surface treatment may have an influence on the absorption speed, especially in case of porous substrates, but will mainly have an effect on the speed with which the liquid spreads, because the contact angle which the liquid/air meniscus of the droplet forms with the surface of the substrate will be dependent upon an equilibrium between the surface tensions of the liquid-to-air surface, the liquid-to-substrate surface and the substrate-to-air surface. In general, the spreading speed of the liquid and, consequently, the dot size will increase when the intensity of the pre-treatment is increased. Thus, the pre-treatment provides a possibility to control the dot size of the ink dots on the substrate. 
       SUMMARY OF THE INVENTION 
       [0010]    It is an object of the present invention to provide a method that improves the control of the dot size on a variety of substrates. 
         [0011]    In order to achieve this object, the method according to the present invention includes a step of adjusting the ratio of oxygen to nitrogen in the controlled atmosphere dependent upon the type of substrate. 
         [0012]    Thus, according to the present invention, the oxygen content of the controlled atmosphere is used as another parameter, in addition to the treatment energy, for controlling the pre-treatment conditions. This permits adjustment of the pre-treatment more adequately to the respective types of substrate. 
         [0013]    When the controlled atmosphere consists essentially of nitrogen, i.e. when the atmosphere is practically free of oxygen, and when the intensity of the pre-treatment is gradually increased, while all other conditions are left unchanged, the resulting dot size will increase and will then reach a certain level. When the intensity is increased further, the dot size will not increase further but will essentially stay on the level that has been reached. In other words, the dot size curve as a function of the treatment intensity shows a plateau for large intensities. 
         [0014]    However, when the pre-treatment is performed at ambient air, it has been found that, at least for some substrates, the dot size curve reaches a maximum and then starts to decrease again without ever reaching the plateau for pure nitrogen when the intensity is increased further. It is presumed that the reason for this effect is that the oxygen contained in the air reacts with the substrate to form acidic groups on the substrate surface. This has the consequence that latex or pigment inks, that are generally alkaline, tend to react with the acidic groups, and these chemical reactions compromise the spreading of the liquid, so that, when the substrate surface becomes more and more acidic with increased treatment energy, the spreading speed is reduced to such an extent that the dot size decreases. 
         [0015]    It is generally desired that the pre-treatment energy is kept in a range in which the dot size curve is essentially flat, i.e. at a value close to the maximum of the dot size curve in case of an ambient air and to a value within the plateau in case of pure nitrogen. This has the advantage that the dot size will be independent of any possible fluctuations of the treatment intensity, which may be caused for example by a surface roughness or other surface irregularities of the substrate. 
         [0016]    The present invention now offers the possibility to use the oxygen content as a parameter for changing the height of the peak of the dot size curve. In this way, it becomes possible to keep the treatment intensity in a range where the dot size curve is flat, and nevertheless obtain essentially the same dot size for all substrates, irrespective of the different types of substrates. The great advantage is that the pigment concentration of the ink can be optimized for that dot size. This permits optimization of the color gamut and a more consistent color management irrespective of differences between the various types of substrates. 
         [0017]    More specific optional features of the present invention are indicated in the dependent claims. 
         [0018]    The composition of the treatment atmosphere may be controlled in any suitable way, e.g. by supplying pure nitrogen gas and pure oxygen gas to the treatment zone with suitably adjusted flow rates. In a preferred embodiment, however, the gas composition is controlled by forcing ambient air to pass through a gas separation membrane that in general has a higher permeability for nitrogen than for oxygen. Without wanting to be bound to any theory, it is believed to be caused by the fact that nitrogen has a smaller molecular size than oxygen. Then, the nitrogen content of the gas that has passed through the membrane (i.e. at the permeation side of the membrane) will depend upon the thickness of the membrane, the flow-rate of the ambient air and/or the pressure with which the gas has been forced through the membrane. Due to selective permeation of nitrogen, the gas on the permeation side of the membrane will be nitrogen enriched. The gas that has not passed through the membrane, i.e. at the retention side of the membrane, consequently is oxygen enriched. In view of this, the method can be carried out while using just ambient air and without any need for a supply of pure gases. 
         [0019]    In an embodiment, a tubular gas separation membrane is used as the membrane. If a tubular gas separation membrane is used, depending on the pressure and flow-rate of the ambient (pressurized) air through the tubular membrane, the permeation side of the membrane provides nitrogen enriched air and the retention side of the membrane provides oxygen enriched air. 
         [0020]    Preferably, the pre-treatment may be carried out under a gas douche. 
         [0021]    An apparatus for carrying out the present invention has a user interface adapted to input information on the type of substrate being used and a controller adapted to automatically adjust the oxygen content of the controlled atmosphere to the type of substrate. The controller may include or may have access to an electronic table that links the various types of substrates to the corresponding values of the oxygen content and the treatment energy. 
         [0022]    The pre-treatment apparatus may be a stand-alone device or may be integrated in a printer. 
         [0023]    Further scope of applicability of the present invention will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the present invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the present invention will become apparent to those skilled in the art from this detailed description. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0024]    The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus are not limitative of the present invention, and wherein: 
           [0025]      FIG. 1A  is a schematic view of an ink jet printer with an integrated pre-treatment apparatus according to the present invention; 
           [0026]      FIG. 1B  is a schematic view of a pre-treatment apparatus as used in an embodiment of the present invention; 
           [0027]      FIG. 1C  is a schematic view of a gas membrane module as used in an embodiment of the present invention; 
           [0028]      FIGS. 2 and 3  illustrate the shapes of ink droplets on a treated and a non-treated substrate surface, respectively; and 
           [0029]      FIGS. 4 and 5  are diagrams showing dot size curves for different pre-treatment atmosphere compositions. 
       
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
       [0030]    The present invention will now be described with reference to the accompanying drawings. 
         [0031]    The ink jet printer shown in  FIG. 1A  has three bins  10  for accommodating stacks of sheets of print substrates  12 ,  14  and  16 . Each bin  10  may be assumed to contain substrates of a different type, e.g. different qualities of paper, plastic film transparencies and the like. 
         [0032]    A substrate transport path  18  is constituted by a motor-driven endless conveyor belt. A feed mechanism  20  is provided for withdrawing the substrate sheets one by one from the top of the stack in one of the bins  10  and feeding the sheets into the substrate transport path  18 . 
         [0033]    The bins  10  are mounted on a lift mechanism  22  arranged to lift a selected one of the bins  10  into a position in which it is level with the transport path  18 , so that the substrate sheets may be drawn-in from that bin. The feed mechanism  20  can be tilted away into a position in which it does not interfere with the vertical movements of the bins  10 . 
         [0034]    An ink jet printhead  24  is arranged above the substrate transport path  18  for printing an image onto each of the substrates passing through. A pre-treatment station  26  is arranged at the transport path  18  in a position upstream of the printhead  24 . 
         [0035]    The pre-treatment station  26  includes a pre-treatment device which, in this example, comprises a plasma treatment unit  140  (see  FIG. 1B ). 
         [0036]      FIG. 1B  is a side view of the plasma treatment unit  140  present in the pre-treatment station  26  (see  FIG. 1A ) that can be used in a method according to an embodiment of the present invention. Please note that the media transport direction through the pre-treatment device is represented opposite to the media transport direction as shown in  FIG. 1A . In practice, the transport directions are the same. A sheet of recording substrate P is transported by a sheet transporting mechanism through a transport path  148  in the direction indicated by arrow X along the plasma treatment unit  140 . The transport path  148  has a height H, which is sufficient to accommodate the thickness of the transported cut sheet material. It should be noted that the transport path height H in  FIG. 1B  is shown schematically and is typically in the range of from 1 to 3 mm. The sheet transport mechanism comprises a driving roller  158  and a free rotatable roller  157 , which together form a transport pinch. The plasma treatment unit  140  comprises a body  146 , a plasma generating mechanism comprising a high voltage electrode  142 , and a sheet guide  144 . The sheet guide  144  is positioned between the high voltage electrode  142  and the transport path  148 . The sheet guied  144  provides a predetermined distance PD guid  between the transport path  148  and the high voltage electrode  142 . The predetermined distance PD guid  in  FIG. 1B  is shown schematically and is typically in the range of between 1 and 3 mm, preferably about 1.5 mm. The sheet guide  144  may be constituted of a ceramic material, such as aluminium oxide (Al 2 O 3 ), silicon nitride (Si 3 N 4 ) or silicon carbide (SiC). The plasma generating mechanism further comprises a counter electrode  150 . The counter electrode  150  is electrically grounded. Further, the sheet transport mechanism comprises a sheet supporting surface  152  for supporting the sheet P during transport in the direction of the sheet transport path  148  along the high voltage electrode  142 . 
         [0037]    An air flow indicated by arrows A is provided inside of the plasma treatment unit  140 . The air flow removes air contaminations, which are generated between the high voltage electrode  142  and the counter electrode  150 , and directs the contaminations towards an air pump device (not shown). The air pump device further contains a filter in order to remove the air contaminations, such as ozone, from the air flow (gas douche). 
         [0038]    In this embodiment, a sheet of a recording substrate may be transported between the high voltage electrode and the counter electrode. In this configuration, the gas present in the pores (e.g. air-pockets) of the substrate is also ionized and hence the whole thickness of the substrate is plasma treated, unlike the treatment with a plasma gun wherein the counter electrode is comprised in the gun. 
         [0039]    In another embodiment, the sheet supporting surface  152  comprises an electrical insulating layer, for example a ceramic layer, such as a glass layer, or a polymeric layer. The electrical insulating layer arranged in between the counter electrode  150  and the transport path  148  provides that the surface treatment of the sheet of recording substrate P during the plasma treatment process of the high voltage electrode  142  towards the surface of the cut sheet material attains a certain treatment widening. This improves the uniformity and quality of the surface treatment of the sheet of recording substrate P. 
         [0040]    The gas douche is provided for creating, in the operating range of the pr-treatment device (the plasma treatment unit  140 ), an atmosphere that is mainly formed by a mixture of nitrogen and oxygen with a controlled oxygen content. 
         [0041]    The oxygen content in the air may be controlled with a gas separation membrane as shown in  FIG. 1C . 
         [0042]    In the example shown, the oxygen content is controlled by means of a blower  200 , which sucks-in ambient air (arrow B) and forces the air through a tubular gas separation membrane  203  of which the exit permeation side  204  is connected to the body  146  (see  FIG. 1B ) of the plasma treatment unit  140 , such that the composition of the gas that is ionized in the plasma region can be controlled. 
         [0043]    The pressure and/or the mass flow rate in the feed line of the tubular gas separation membrane  203  is measured with a sensor  202  and with this signal the feed flow-rate of the gas separation membrane  203  is controlled. 
         [0044]    The air-flow that is pressed through the gas separation membrane  203  (indicated with arrow D), is nitrogen enriched. The air flow that passes through the retention side of the membrane (indicated with arrow C) comprises oxygen enriched air. The design characteristics, including the thickness of the gas separation membrane  203 , are selected such that a desired range of nitrogen contents can be covered by varying the pressure and flow-rate at the entrance of the gas separation membrane. 
         [0045]    In an embodiment, the gas separation membrane can be operated in a steady state, i.e. the out-coming gas flows (indicated with arrows C and D in  FIG. 1C ) have a constant nitrogen content (C: Oxygen enriched; D: Nitrogen enriched). The desired concentration of nitrogen and oxygen can be obtained by mixing the permeated gas flow (D) with the outcoming gas flow (C) and/or with ambient air. 
         [0046]    An electronic controller  36  (see  FIG. 1A ) is provided for controlling the various components of the ink jet printer, including the printhead  24 , the sheet conveying mechanism (motor-driven endless conveyor belt), the lift mechanism  22  and also the pre-treatment station  26  having the blower  200 , a mass flow controller  201  and pre-treatment device (the plasma treatment unit  140 ). 
         [0047]    A user interface  38  (see  FIG. 1A ) is connected to the controller  36  and includes a display screen  40  and an input section  42  permitting a user to specify (among other things) the types of the substrates  12 ,  14  and  16  that are presently contained in the bins  10 . The bins and the loaded types of substrate are shown on the display screen  40 , permitting the user to select one of the bins and the corresponding type of substrate for printing. 
         [0048]    The controller  36  includes an electronic table  44  that stores, for each of the substrates  12 ,  14  and  16 , an associated value for the treatment energy to be delivered by the pre-treatment device (plasma treatment unit  140 ) and an associated value for the oxygen content of the atmosphere to be created in the gas douche. In this example, the oxygen content may be indicated implicitly by corresponding values for the displacement or output pressure of the blower  200 . The table  44  may also include additional data sets for other types of substrate that might be loaded into the bins  10  in place of the substrates  12 ,  14 ,  16 . 
         [0049]    When the user has selected a specific bin and, therewith, a specific type of substrate, the controller  36  will automatically control the pre-treatment device (plasma treatment unit  140 ) and the blower  200  so as to provide the required pre-treatment conditions. 
         [0050]    The effect of the pre-treatment of the substrates is illustrated in  FIGS. 2 and 3 . 
         [0051]    In  FIG. 2 , an ink droplet  46  has been jetted onto the surface of a substrate sheet  14   a  that has not been pre-treated. In this case, the surface energy of the substrate is small in comparison to the surface tension of the liquid ink in the droplet  46 . This means that the substrate surface is hydrophobic (in case of water-based inks) and the adhesion force between the substrate and the liquid ink is smaller than the cohesion force of the liquid, with the result that the ink does not wet the substrate, and the contact angle a between the ink droplet and the substrate surface is smaller than 90°. 
         [0052]    For comparison,  FIG. 3  shows an ink droplet  48  on a substrate sheet  14   b  that has been pre-treated and therefore has a higher surface energy. In this case, the difference in surface tension between the substrate-to-air surface of the substrate sheet and the substrate-to-liquid surface of the substrate sheet is larger than the surface tension of the ink droplet  48  (liquid-to-air), so that the substrate surface is wetted with ink and the ink droplet  48  is spread until an equilibrium condition is reached at a contact angle a that is significantly larger than 90°. 
         [0053]    In the course of time, the solvent in the liquid will evaporate, and part of the ink may also be absorbed into the depth of the substrate sheet, so that what is finally left on the surface of the substrate is an ink dot of a predetermined size. This dot size will depend critically upon the speed with which the ink droplet  48  spreads due to the mechanism described above. Consequently, the surface tension of the substrate sheet  14   b,  as it results from the pre-treatment, has an important influence on the dot size. 
         [0054]    On the other hand, the spreading of the ink droplet  48  and the resulting dot size is also influenced by the chemistry at the surface of the substrate sheet. When the substrate surface is acidic, while the ink is alkaline (as is the case for most latex and pigment inks), chemical reactions between the substrate and the ink will tend to slow down the spreading of the ink droplet  48  and reduce the resulting dot size. The chemistry of the treated substrate surface will depend on the intensity (energy per unit area) of the treatment, but also the composition, especially the oxygen content, of the atmosphere in the treatment zone. 
         [0055]      FIG. 4  illustrates examples of dot size curves indicating the dot size as a function of the treatment intensity for a specific type of substrate (e.g. the substrate  14  in  FIG. 1A ) and for oxygen contents of 0% (pure nitrogen), 5%, 10% and 21% (ambient air), respectively. 
         [0056]    It can be seen that, in the presence of oxygen, the dot size has a peak at a certain treatment intensity and then tends to decrease again when the intensity is increased further. The height of the peak is generally lower when the oxygen content is higher. 
         [0057]      FIG. 5  shows corresponding dot size curves for a different type of substrate (e.g. the substrate  16  in  FIG. 1A ). Although the general shape of the dot size curves is similar, the heights of the peaks and the intensity values where the maximum is reached are different, due to different surface properties of the substrate. 
         [0058]    The controller  36  will control the pre-treatment conditions such that a uniform dot size (of e.g. 90 μm in this example) will be achieved for all types of substrates (if the volume of the ink droplets and all other conditions are the same). In principle, as can be seen in  FIGS. 4 and 5 , this could be achieved with a pure nitrogen atmosphere (dot size curves for 0%), simply by appropriately adjusting the treatment intensity (to about 20 W min/m 2  in  FIG. 4  and approximately 30 W min/m 2  in  FIG. 5 ). However, in this intensity range, the dot size curves for 0% are very steep, which means that the dot size would depend critically upon the exact value of the treatment intensity, and even minor fluctuations in the intensity would lead to visible fluctuations of the dot size and, consequently, to a poor image quality. 
         [0059]    This is why, according to the present invention, the dot size is controlled by adjusting both the treatment intensity and the oxygen content of the atmosphere. In  FIG. 4 , an atmosphere with an oxygen content of 10% is used, and the intensity is adjusted such that the dot size reaches its maximum of 90 μm. In this range, the dot size curve for 10% is flat, so that the dot size is largely insensitive to fluctuations of the treatment intensity. 
         [0060]    In  FIG. 5 , the same dot size of 90 μm is achieved by using an atmosphere with an oxygen content of only 5% and adjusting the intensity to the maximum of the dot size curve for 5%. Again, this curve is flat in the vicinity of the selected intensity value, so that the dot size will also be insensitive to intensity fluctuations. 
         [0061]    It will be understood that, by varying the oxygen content of the atmosphere and appropriately adjusting the treatment intensity, the resulting dot size may be varied in a relatively wide range, and still the dot size will be the same for all types of substrates being used. In general, in order for the dot size to be insensitive to intensity fluctuations, it is sufficient that the dot size curve is flat in the vicinity of the selected intensity value, i.e., the curve must have a point of zero derivative which may also be a local minimum or a saddle point rather than a local maximum or peak. 
         [0062]    The present invention being thus described, it will be obvious that the same may be varied in many ways. Such variations are not to be regarded as a departure from the spirit and scope of the present invention, and all such modifications as would be obvious to one skilled in the art are intended to be included within the scope of the following claims.

Technology Classification (CPC): 1