Patent Abstract:
A method of forming a metal seed layer, preferably a copper layer, for subsequent electrochemical deposition. The metal seed layer is formed by the oxidation-reduction reaction of a metal salt with a reducing agent present in a layer on the substrate to be plated. Metal interconnects for semiconductor devices may be produced by the method, which has the advantage of forming the metal seed layer by a simple electrochemical plating process that may be combined with the plating of the interconnect itself as a single-bath operation.

Full Description:
FIELD OF THE INVENTION 
     The present invention relates to the field of electrochemical deposition, and in particular to a method of forming a metal seed layer by electroplating. 
     BACKGROUND OF THE INVENTION 
     The performance characteristics and reliability of integrated circuits have become increasingly dependent on the structure and attributes of the vias and interconnects which are used to carry electronic signals between semiconductor devices on integrated circuits or chips. Advances in the fabrication of integrated circuits have resulted in increases in the density and number of semiconductor devices contained on a typical chip. Interconnect structure and formation technology has lagged behind these advances, however, and is now a major limitation on the signal speed of integrated circuits. 
     Current techniques for forming vias and interconnects begin with preparation of the semiconductor wafer surface by formation of an interlevel dielectric layer (ILD), typically silicon dioxide. A mask may then be applied to pattern the deposition of the interconnect material on the wafer in the desired manner. Another typical process is to plate the interconnect material onto the surface of the wafer to a depth sufficient to fill the vias, followed by planarization to achieve the desired interconnect pattern. 
     Typically the preferred metal for use in the construction of integrated circuit interconnects has been aluminum. Aluminum is widely used because it is inexpensive, relatively easy to etch, and adheres well to ILDs such as silicon dioxide. Disadvantages of aluminum include significant electromigration effects, susceptibility to humidity-induced corrosion, and the tendency to “cold creep”. “Cold creep” is a process that creates cracks or spaces between the interconnect layer and the ILD due to large variances in the coefficient of thermal expansion between the two materials. 
     The disadvantages of aluminum interconnects have become more pronounced as the geometry of integrated circuits continues to shrink. Chip designers have attempted to utilize different materials to construct an interconnect system having the chemical and mechanical properties which will complement and enhance smaller and faster circuit systems. The ideal interconnect material is inexpensive, and has low resistivity, minimal electromigration effects, high corrosion resistance, and a similar coefficient of thermal expansion to the ILD and substrate material. Metals possessing these properties include gold, silver, and copper, and research has generally focused on these three metals as new via and interconnect materials. 
     Copper is the most attractive material for use in integrated circuits because of its desirable chemical and mechanical properties. It is an excellent conductor with a resistivity of 1.73 microOhms per centimeter, is inexpensive, and is easily processed. Copper also has fewer electromigration effects than aluminum and can therefore carry a higher maximum current density, permitting a faster rate of electron transfer. The high melting point and ductility of copper produce far less cold creep during the semiconductor fabrication process than many other metals, including aluminum. 
     Although copper has many favorable characteristics, it also has disadvantages that may create fabrication problems for chip designers. Copper is soluble in silicon and most common ILDs, and exhibits a high rate of diffusion at temperatures associated with integrated circuit manufacturing. This diffusion can result in the creation of intermetallic alloys which can cause malfunctioning of the active semiconductor devices. In addition, copper exhibits poor adhesion to silicon dioxide which can result in broken connections and failure of electrical contacts. 
     Use of an intermediate barrier layer between the ILD and the copper interconnect permits the successful use of copper in a silicon-based integrated circuit. The barrier layer serves to eliminate the diffusion that would otherwise occur at the copper-ILD junction, and thus prevents the copper from altering the electrical characteristics of the silicon-based semiconductor devices. Such barrier layers are well known in the art and may be formed of a variety of transition metals, transition metal alloys or silicides, metal nitrides, and ternary amorphous alloys. The most common barrier layer materials in use are titanium, tantalum, and tungsten alloys due to their demonstrated ability to effectively reduce copper diffusion. 
     Deposition of a metallization layer generally occurs through one of the following techniques: chemical vapor deposition (CVD); physical vapor deposition (PVD), also known as sputtering; or electrochemical deposition. CVD involves high temperatures which can lead to cold creep effects and an increased chance of impurity contamination over other methods, and sputtering has problems yielding sufficient step coverage and density at small line widths. Electrochemical deposition, however, offers a more controlled environment to reduce the chance of contamination, and a process that takes place with minor temperature fluctuations. Electrochemical deposition provides more thorough coverage, fewer physical flaws, and reduces separation between the layers. 
     There are several known electrochemical deposition processes used to form copper interconnects onto barrier layers, each having various disadvantages. Direct deposition of copper onto the barrier layer typically results in porous films with poor adhesion and inconsistent densities. Annealing of the deposited copper at low temperatures may be performed to improve adhesion, but it increases cold creep effects and fails to provide a consistently dense copper structure. A copper seed layer may be formed over the barrier layer by CVD or PVD to produce an adhesive surface, and then electrochemical deposition may be carried out on the seed layer. This method involves multiple steps and increases production costs by requiring several different types of machines to form each interconnect layer. 
     What is needed, therefore, is a simple and inexpensive method of forming a metal seed layer that requires only a minimum number of steps for its production. 
     SUMMARY OF THE INVENTION 
     The present invention provides a method of forming a metal seed layer, preferably a copper layer, for subsequent electrochemical deposition. The metal seed layer is formed by the oxidation-reduction reaction of a metal salt or complex such as copper sulfate in acid solution, with a reducing agent such as elemental silicon that is present in a layer on the substrate to be plated. 
     Preferably the reducing agent is present in a sacrificial layer on the substrate. The method is particularly suited to forming metal interconnects for semiconductor devices, because the metal seed layer and the plating of the interconnect itself may be combined into a single-bath operation. 
     Additional advantages and features of the present invention will be apparent from the following detailed description and drawings which illustrate preferred embodiments of the invention. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a cross-sectional view of a semiconductor wafer undergoing the process of a preferred embodiment of the present invention. 
     FIG. 2 shows the wafer of FIG. 1 at a processing step subsequent to that shown in FIG.  1 . 
     FIG. 3 shows the wafer of FIG. 1 at a processing step subsequent to that shown in FIG.  2 . 
     FIG. 4 shows the wafer of FIG. 1 at a processing step subsequent to that shown in FIG.  3 . 
     FIG. 5 shows the wafer of FIG. 1 at a processing step subsequent to that shown in FIG.  4 . 
     FIG. 6 shows the wafer of FIG. 1 at a processing step subsequent to that shown in FIG.  5 . 
     FIG. 7 is a cross-sectional view of a semiconductor wafer undergoing the process of a second preferred embodiment of the present invention. 
     FIG. 8 shows the wafer of FIG. 7 at a processing step subsequent to that shown in FIG.  7 . 
     FIG. 9 shows the wafer of FIG. 7 at a processing step subsequent to that shown in FIG.  8 . 
     FIG. 10 shows the wafer of FIG. 7 at a processing step subsequent to that shown in FIG.  9 . 
     FIG. 11 shows the wafer of FIG. 7 at a processing step subsequent to that shown in FIG.  10 . 
     FIG. 12 shows the wafer of FIG. 7 at a processing step subsequent to that shown in FIG.  11 . 
    
    
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS 
     In the following detailed description, reference is made to the accompanying drawings which form a part hereof, and in which is shown by way of illustration specific embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention, and it is to be understood that other embodiments may be utilized, and that structural, logical, electrical and chemical changes may be made without departing from the spirit and scope of the present invention. 
     The terms “wafer” and “substrate” are to be understood as including silicon-on-insulator (SOI) or silicon-on-sapphire (SOS) technology, doped and undoped semiconductors, epitaxial layers of silicon supported by a base semiconductor foundation, and other semiconductor structures. Furthermore, when reference is made to a “wafer” or “substrate” in the following description, previous process steps may have been utilized to form regions or junctions in the base semiconductor structure or foundation. When referring to aqueous solutions described herein, the term “percent” refers to the percent measured by weight, e.g., a 10% hydrofluoric acid solution is 10% by weight hydrofluoric acid. 
     The following description is, therefore, not to be taken in a limiting sense, and the scope of the present invention is defined by the appended claims. 
     Referring now to the drawings, where like elements are designated by like reference numerals, an embodiment of the present invention for manufacturing an integrated circuit having a metal interconnect is illustrated by FIGS. 1 through 6. The process creates a metal seed layer for subsequent electrochemical deposition by a oxidation-reduction (“redox”) reaction between a reducing agent present in a sacrificial layer of material, and a metal salt or complex. For illustrative purposes the invention is described as a method of plating copper by a reaction in which the reducing agent is silicon, but the use of other metals and reaction mechanisms is to be understood as within the scope of the invention. 
     The process begins subsequent to the formation of a semiconductor device  20  containing devices  24 , which may be transistors, capacitors, word lines, bit lines or the like, and active areas  26  on a silicon substrate  22 , as shown in FIG. 1. A protective layer  28  of a material such as borophosphosilicate glass (BPSG), phosphosilicate glass (PSG), borosilicate glass (BSG), or silicon dioxide has been formed over the device  20  by chemical vapor deposition (CVD) or other suitable means. 
     The process of the present invention begins by applying a photoresist and mask (not shown), and by using photolithographic techniques to define areas to be etched out. Referring to FIG. 2, a directional etching process such as reactive ion etching (RIE) is used to etch through the protective layer  28  to form vias  30 . T he etchant used may be any suitable etchant that selectively etches t he material of the protective layer  28  and not the active areas  26 , the devices  24 , or the material of sidewall or cap insulators on the devices  24 . 
     FIG. 3 depicts the next step of the process, in which a barrier layer  32  is formed so that it overlies the protective layer  28  and lines the inside of the vias  30 . Barrier layers are typically used with metal interconnect material to optimize performance of the interconnect s, and to prevent diffusion of the metal interconnect material into the substrate. The barrier layer  32  may be formed of any suitable material such as titanium, titanium nitride, tantalum, tantalum nitride, tungsten nitride, tungsten-tantalum, tantalum silicon nitride, or other ternary compounds, and should be of a thickness within the range of 50 to 500 Angstroms, and preferably approximately 300 Angstroms thick. Chemical vapor deposition, physical vapor deposition (PVD), or other suitable means may be used to form the barrier layer  32 . 
     Next, a sacrificial oxide layer  34  is formed over the barrier layer  32  and lining the inside of the vias  30 , as shown in FIG.  4 . The sacrificial oxide layer  34  is a layer of silicon-containing material such as silicon dioxide or silicon monoxide that is formed by means such as CVD, PVD, oxidation of the wafer in an ozone-containing rinse bath, or the like. Preferably the oxide is a chemical oxide. The sacrificial oxide layer  34  has a thickness within the range of 10 to 200 Angstroms, preferably 10 to 50 Angstroms, and should have a silicon-tooxygen ratio of greater than  0 . 5 . Depending on the reaction mechanism, a sacrificial oxide layer  34  may not be required, and a reactive barrier layer  32  may be used if there is a sufficient amount of the reducing agent present in the barrier layer  32 . 
     FIG. 5 depicts the next step of the process, in which a metal seed layer  36  is now formed on the surface of the barrier layer  32  in the vias  30  by a redox plating process. The plating process is carried out by exposing the wafer  20  to a first plating solution by means such as immersion of the wafer  20  into a plating bath, or by spraying the plating solution onto the wafer  20 . The first plating solution is an aqueous solution of an acid such as hydrofluoric acid or sulfuric acid, and a metal salt or complex that is soluble in the acid used. A redox reaction occurs between the metal ions in the solution, e.g., cupric ions (Cu 2+ ) and the reducing agent of the sacrificial oxide layer  34 , e.g., silicon, leading to reduction of the metal ions and subsequent plating onto the barrier layer  32 . 
     For example, in a copper plating process, a dilute solution of hydrofluoric acid (HF) and a salt such as copper sulfate (CuSO 4 ) is used to carry out the reaction with a sacrificial oxide layer  34  containing silicon as a reducing agent. Preferably a solution containing approximately 1 part hydrofluoric acid per 100 parts water, and about 3 grams of copper sulfate per liter is used, and the reaction is allowed to proceed at room temperature for approximately 2 to 2.5 minutes for a sacrificial oxide layer  34  that is approximately 50 Angstroms thick. The time and temperature may be adjusted as necessary for the thickness of the sacrificial oxide layer  34 , and to affect the rate of the reaction. The precise reaction that occurs in the copper plating process is unknown, but is currently believed to be: 
     
       
         Si+2Cu 2+ +6F→SiF 6   2− +2Cu  
       
     
     The plating bath in a preferred embodiment is electroless, but an electrolytic bath may also be used. An electrolytic bath permits formation of a thicker metal seed layer  36  than an electroless bath, because electrons are continuously replaced by the electric current applied and therefore the metal ions, which have an electron affinity, may continuously plate to the barrier layer  32 . If desired, the plating process may begin as an electroless process, and a voltage may later be applied to carry out an electrolytic plating process. 
     A conductive layer  38  is now formed in the vias  30  to serve as an interconnect layer, as shown in FIG.  6 . The conductive layer  38  is a layer of metal, which may be the same metal as the metal seed layer  36 , or a different metal. Preferably the metal seed layer  36  and the conductive layer  38  are layers of the same metal. The conductive layer  38  is formed by an electrochemical deposition process such as electrolytic or electroless plating. 
     Preferably the conductive layer is formed by exposing the wafer  20  to a second plating solution by means such as immersion of the wafer  20  into a plating bath, or by spraying the second plating solution onto the wafer  20 . The second plating solution is typically an aqueous solution of an acid such as sulfuric acid, a metal salt or complex that is soluble in the acid used, and several additives. Either electroless or electrolytic plating, or a combination of the two may be performed as desired for certain applications. In addition, any number of semiconductor wafers may be simultaneously processed by using a large bath, thereby reducing the cost of manufacture. 
     If the metal seed layer  36  and the conductive layer  38  are formed from the same metal, then the plating process may be carried out in the same plating bath that was used for formation of the metal seed layer  36 , and may use the same plating solution. If the metal seed layer  36  and the conductive layer  38  are formed from different metals, then the same tank may be used for both plating processes if the first and second plating solutions are cycled through the tank. Subsequent to the plating process, conventional processing methods, such as planarization of the wafer  20  to isolate the conductive layer  38  into individual contact plugs, may then be used to create a functional circuit from the semiconductor wafer  20 . 
     A second embodiment of the present invention is illustrated by FIGS. 7 through 12. Referring to FIG. 7, a semiconductor device  120  contains devices  24 , active areas  26 , and field oxide regions  40  on a silicon substrate  22 . A protective layer  28  has been formed over the device  120 , and conductive plugs  42  extend through the protective layer  28  to contact the active areas  26 . A protective layer  44  of a material such as BPSG, PSG, BSG, or silicon dioxide has been formed over the device  120  by CVD or other suitable means. 
     Photolithographic techniques and subsequent etching are then used to define and form a damascene opening or trench  30 , as shown in FIG.  8 . Referring now to FIG. 9, a barrier layer  32  is now formed so that it overlies the protective layer  44  and lines the inside of the trench  30 , as explained with reference to FIG. 3 above. Next, a sacrificial oxide layer  34  is formed over the barrier layer  32  and lining the inside of the trench  30 , as shown in FIG. 10, and as further described with reference to FIG. 4 above. 
     FIG. 11 depicts the next step of the process, in which a metal seed layer  36  is now formed on the surface of the barrier layer  32  in the trench  30  by a redox plating process, as is described further above in reference to FIG.  5 . Lastly, a conductive layer  38  is formed in the trench  30  to serve as an interconnect layer, as shown in FIG.  12 . The conductive layer  38  is a layer of metal formed by an electrochemical process, as is described more fully with reference to FIG. 6 above. Subsequent to the plating process, conventional processing methods, such as planarization of the wafer  120 , may then be used to create a functional circuit from the semiconductor wafer  120 . 
     As can be seen by the embodiments described herein, the present invention encompasses methods of forming a metal seed layer via a redox reaction with a reducing agent. The reducing agent may be present in a sacrificial layer on the substrate to be plated, or may be in a non-sacrificial layer. 
     It should again be noted that although the invention has been described with specific reference to semiconductor wafers, the invention has broader applicability, and may be used in any plating application in which a thin self-limiting seed layer is used. 
     The above description and drawings are only illustrative of preferred embodiments which achieve the objects, features and advantages of the present invention. It is not intended that the present invention be limited to the illustrated embodiments. Any modification of the present invention which comes within the spirit and scope of the following claims should be considered part of the present invention.

Technology Classification (CPC): 7