Patent Abstract:
Techniques for fabricating an inkjet printhead include providing a printhead substrate, fabricating a thinfilm structure on the substrate, forming a break trench in a surface region of the substrate in which a feed slot is to be formed, and subsequently abrasively machining the substrate through the break trench to form the feed slot. The break trench can be formed by an etch process, prior to applying a barrier layer to the thinfilm structure in a preferred embodiment.

Full Description:
TECHNICAL FIELD OF THE INVENTION  
       [0001]     The present invention relates to substrates such as those used in inkjet printheads and the like.  
       BACKGROUND OF THE INVENTION  
       [0002]     Various inkjet printing arrangements are known in the art and include both thermally actuated printheads and mechanically actuated printheads. Thermal actuated printheads tend to use resistive elements or the like to achieve ink expulsion, while mechanically actuated printheads tend to use piezoelectric transducers of the like.  
         [0003]     A representative thermal inkjet printhead has a plurality of thin film resistors provided on a semiconductor substrate. A nozzle plate and barrier layer are provided on the substrate and define the firing chambers about each of the resistors. Propagation of a current or a “fire signal” through a resistor causes ink in the corresponding firing chamber to be heated and expelled through the appropriate nozzle.  
         [0004]     Ink is typically delivered to the firing chamber through a feed slot that is machined in the semiconductor substrate. The substrate usually has a rectangular shape, with the slot disposed longitudinally therein. Resistors are typically arranged in rows located on both sides of the slot and are preferably spaced approximately equal distances from the slot so that the ink channel length at each resistor is approximately equal. The width of the print swath achieved by one pass of a printhead is approximately equal to the length of the resistor rows, which in turn is approximately equal to the length of the slot.  
         [0005]     Feed slots have typically been formed by sand drilling (also known as “sand slotting”). This method is preferred because it is a rapid, relatively simple and scalable (many substrates may be processed simultaneously) process. While sand slotting affords these apparent benefits, sand slotting is also disadvantageous in that it causes micro cracks in the semiconductor substrate that significantly reduce the substrates fracture strength, resulting in significant yield loss due to cracked die. Low fracture strength also limits substrate length which in turn adversely impacts print swath height and overall print speed.  
         [0006]     Other techniques include ultrasonic diamond bit drilling, abrasive sand blasting, YAG laser machining, KOH etching, TMAH etching, and dry plasma etching.  
         [0007]     Ultrasonic diamond bit drilling is only suited for machining round holes. Moreover, this process creates large chips to glass and silicon on both the input and output side of the through hole. These chips are too large (hundreds of microns) to allow the resistors to be close to the ink feed slot.  
         [0008]     Abrasive sand blasting also has chipping problems, due to chipping of the wafer around the output side of the through slot. This chipping causes two separate issues. Normally the chipping is tens of microns large and limits how close the firing chamber can be placed to the edge of the slot. Occasionally the chipping is larger and causes yield loss in the manufacturing process. The chipping problem is more prevalent as the desired slot length increases and the desired slot width decreases. In this process the resulting shape of the slot is controlled by many factors. The variation of the slot edge position causes variation on the ink flow resistance. The slot position is controlled mechanically in a harsh environment, thus limiting the accuracy and repeatability of the slot positioning to about +/−15 microns.  
         [0009]     YAG laser machining also has disadvantages. The laser system is expensive to buy and maintain. The relatively small laser beam needs to be “paned,” i.e. moved, around the parameter of the desired slot area and needs multiple passes to cut through the wafer. The laser produces a small spot (around 10 to 50 microns in diameter) where the laser energy is focussed. This small active area requires that the laser spot be moved around the perimeter of the area that is to be cut while the laser is pulsed. It takes many laser pulses at each perimeter location to cut through the silicon wafer, which in an exemplary embodiment has a nominal thickness of 670 microns. Typical water processing time is 2 to 3 hours, limiting system capacity. As the laser burns through the silicon there is an area around the cut where the silicon is melted, not vaporized. This molten silicon is spattered around the edge of the drill slot causing problems with part adhesion and leaving globules or slag that can later break loose and clog the ink feed path. The area around the laser cutting zone gets hot enough to cause damage to the thinfilm and barrier material.  
         [0010]     KOH (Potassium hydroxide) etching can damage the thin films, since KOH is a corrosive basic chemical which will etch silicon, and will attack the thinfilms used in many types of inkjet printheads. To avoid the KOH etch attack of the thinfilms, the etch process needs to occur prior to the thinfilm processing. This processing order causes problems because trenched wafers can not be handled by many of the thinfilm processing tools. For an anisotropic etch, the etch rate is different for different crystalline planes; therefor the etch geometry is defined by the crystalline planes. Etch angles cause the backside opening of a slot to be very large and limit how close the slots can be placed to each other and the edge of the die.  
         [0011]     TMAH (Tetra Methyl Ammonium Hydroxide) is another anisotropic etchant for silicon. TMAH etching techniques on &lt;100&gt; silicon employ etch angles causing the backside opening of a slot to be very large, and thus limit how close the slots can be placed to each other and the edge of the die. An anisotropic etch, the TMAH etch rate is different for different crystalline planes, and therefore the etch geometry is defined by the crystalline planes. Etch rates are only about 1 micron per minute. Typical wafer etch rates are about 8 hours if etched from both sides and 12 hours if etched from one side. Wafers can be batch processed. The masking films are drastically undercut as a result of the extended etching time. These films can break and become a mobile contaminant that can block ink flow in the pen. The etch blocking oxides around the edge of the wafer are scraped and damaged during wafer handling. Where the oxide layer on the wafer has been damaged, etching occurs, causing problems for wafer fragility and handling in subsequent process steps. Slots in the wafer causes thinning of the barrier material.  
         [0012]     Dry plasma etching techniques utilize relatively slow etch rates. Etch rates are only about 2 micron per minute. Typical wafer etch rates are about 3 hours if etched from both sides and 6 hours if etched from one side. Wafers can not be batch processed. Long etches cause damage to thinfilms that are used in inkjet. Dry plasma etchers are very expensive. Slots in the wafer causes thinning of the barrier material.  
       SUMMARY OF THE INVENTION  
       [0013]     A method of fabricating an inkjet printhead is described, and includes providing a printhead substrate, fabricating a thinfilm structure on the substrate, forming a break trench in a surface region of the substrate in which a feed slot is to be formed, and subsequently abrasively machining the substrate through the break trench to form the feed slot.  
         [0014]     In accordance with an aspect of the invention, the break trench is formed by an etch process. The etch process is performed prior to applying a barrier layer to the thinfilm structure in a preferred embodiment. 
     
    
     BRIEF DESCRIPTION OF THE DRAWING  
       [0015]     These and other features and advantages of the present invention will become more apparent from the following detailed description of exemplary embodiments thereof, as illustrated in the accompanying drawings, in which:  
         [0016]      FIG. 1A  is a top plan view of the printhead structure after the first step of the printhead fabrication process, i.e. after the inkjet thin film structure has been formed on the silicon substrate.  FIG. 1B  is a cross-sectional view of the printhead structure of  FIG. 1A  after a further step of the fabrication process, the TMAH etch process, has been performed to create a slot break trench.  
         [0017]      FIG. 2A  illustrates in top plan view the top of the substrate after the thin film fabrication step on the substrate, for a first alternate embodiment of the fabrication process.  FIG. 2B  is a cross-sectional view of the printhead structure of  FIG. 2A , after the TMAH etch process has been performed for this alternate embodiment.  
         [0018]      FIG. 3A  illustrates in top plan view for a second alternate embodiment of a printhead fabrication process the top of the substrate after the thin film fabrication step on the substrate.  FIG. 3B  is a cross-sectional view of the printhead structure of  FIG. 3A , after the TMAH etch process has been performed to create a break trench.  
         [0019]      FIG. 4A  illustrates in top plan view for a third alternate embodiment of a printhead fabrication process the top of the substrate after the thin film fabrication step on the substrate.  FIG. 4B  is a cross-sectional view of the printhead structure of  FIG. 4A , after the TMAH etch process has been performed to create a break trench and after the barrier layer is applied.  
         [0020]      FIG. 5A  illustrates in top plan view for a fourth alternate embodiment the top of the substrate after the thin film fabrication step on the substrate.  FIG. 5B  is a cross-sectional view of the printhead structure of  FIG. 5A  taken along line  5 B- 5 B of  FIG. 5A , after the TMAH etch process has been performed to create a break trench and after the barrier layer is applied.  FIG. 5C  is a cross-sectional view of the printhead structure of  FIG. 5A  taken along line  5 C- 5 C of  FIG. 5A , after the TMAH etch process has been performed to create a break trench and after the barrier layer is applied.  
         [0021]      FIG. 6A  diagrammatically depicts in a top view of a substrate a further embodiment, wherein trenches serving as chip stop bars are not connected at the corners.  FIG. 6B  is a cross-sectional view taken along line  6 B- 6 B of  FIG. 6A .  
         [0022]      FIG. 7A  illustrates in a top view a further embodiment of a break trench process, similar to the embodiment of  FIG. 6A , except that the top and bottom chip stop bars are omitted.  FIG. 7B  is a cross-sectional view taken along line  7 B- 7 B of  FIG. 7A . 
     
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS  
       [0023]     An exemplary embodiment of a process in accordance with aspects of this invention uses the thinfilm materials and processes heretofore employed in inkjet printhead construction. The changes to this process involve the redesign of the artwork on the photomask set to allow for the silicon wafer to be uncovered in the desired area for a TMAH (Tetra Methyl Ammonium Hydroxide) etching of the trenches in accordance with this aspect of the invention. TMAH is an anisotropic etchant for silicon. For an anisotropic etch, the etch rate is different for different crystalline planes, and thus the etch geometry is defined by the crystalline planes. This etching of the trenches happens after the thinfilm processes are complete and before the barrier material is applied. This TMAH etch process includes a few short steps:  
         [0024]     1. Wafer Surface cleaning in the Backside Oxide Etch (BOE).  
         [0025]     2. De-ionized water Rinse.  
         [0026]     3. TMAH Etching.  
         [0027]     4. De-ionized water Rinse.  
         [0028]     The wafers are then subjected to the current processing to complete the pen construction. The abrasive drill process is tuned to match the shape and size required to work with the trench design. A simplified process flow for creating the printhead is shown below for each process.  
         [0029]     1. Create Inkjet Thinfilm Structure  
         [0030]     2. Perform TMAH Etch Process  
         [0031]     3. E-test Thinfilm  
         [0032]     4. Apply and Pattern Barrier  
         [0033]     5. Create Inkfeed Slot with Abrasive Machining  
         [0034]     6. Attach Orifice  
         [0035]     7. Saw Wafer  
         [0036]     8. Attach Printhead to Flex Circuit  
         [0037]     Steps 1 and 3-8 are the steps in the state of the art process described above. Step 2 is the new trench etch step described above.  
         [0038]     Aspects of the invention solve several problems, including the following. The chipping that is normally caused by the abrasive machining process is contained and stopped by the parameter etch trench. In many cases, the etch trench defines the crack location site. Therefore the slot edge can be moved closer to the resistor to give a faster ink refill rate along with a low scrap rate regardless of slot width and length.  
         [0039]     The slot or trench shape can be accurately and repeatedly defined through a photolithography process and the crystalline planes of the silicon which define the trench shape. TMAH has dramatically different etch rates for the different crystalline planes. Due to this fact, for an etching from the b &lt; 100 &gt; plane at the surface of the silicon wafer, the etch will proceed down into the wafer until it reaches the &lt;111&gt; plane. The  &lt;111&gt;l plane is at a  53 degree angle to the &lt;100&gt; plane, and will therefore etch a “V” shaped notch in cross section. On the &lt;100&gt; plane, the &lt;111&gt; planes intersect at 90 degree angles, and therefore square or rectangular patterns can be readily formed to the molecular level with trenches having the “V” trench cross-section. The photolithography process which defines the trench position also allows the trench slot edge positions to be accurately and repeatedly placed.  
         [0040]     The etched silicon trenches are shallow and etch relatively quickly. Typical wafer etching time is 20-50 minutes for a batch of 25 wafers. Typical wafer abrasive drill time is 50-70 minutes. The etch times are short enough that no significant damage occurs to the wafer edge. This process does not create sufficient heat to cause damage to surrounding thinfilms or inkjet materials.  
         [0041]     Barrier thinning is minimized by the narrow and relatively shallow etched trench used by this process technology. The TMAH etch and relatively short etch times prevent damage to the thinfilms on the inkjet printhead. Control of the chipping outside of the etched trench minimizes thinfilm damage due to chipping.  
         [0042]     Several exemplary trench designs are illustrated in  FIGS. 1A-7 , in which like reference numbers refer to like elements, and described below.  
         
       [0043]     Break-Trench Slot Embodiment ( FIGS. 1A-1B )  
         [0044]     In the break-trench embodiment, a v-trench is etched around the perimeter of the ink feed slot area prior to the abrasive drill process. This trench works as a crack initiation site to control the breakthrough location for the abrasive machining, in this embodiment, an abrasive drill process. In addition, this trench stops the propagation of the shallow chipping experienced with the abrasive drill process.  
         [0045]      FIG. 1A  is a top plan view of the printhead structure  100  after the first step of the fabrication process, i.e. after the inkjet thin film structure has been formed on the silicon substrate.  FIG. 1B  is a cross-sectional view of the printhead structure  100  after the TMAH etch process has been performed to create a break trench and after the barrier layer  112  is applied.  
         [0046]     The printhead structure  100  includes a silicon substrate  102  on which various patterned layers have been formed to fabricate the thin film structure, shown generally as  101  in  FIG. 1B . The thin film structure details will vary in dependence on the particular printhead design.  FIGS. 1A-1B  illustrate in simplified form some of the patterned layers defining an exemplary thin film structure. These include a field oxide layer  104 , a polysilicon layer  106 , a passivation layer  108  including silicon carbide and silicon nitride layers, a tantalum layer  110  to define heating resistors for the printhead. Not shown, for example is an aluminum layer defining wiring traces.  
         [0047]     The location of the desired feed slot for the printhead is indicated by dashed line  120  in  FIG. 1A , which marks the periphery of the desired slot. The printhead material within this line  120  is to be removed to provide the feed slot for the printhead. The field oxide (FOX) layer in the area of the feed slot will serve as a mask for the TMAH etching, and has been removed in the region  122  about the line  120 , in preparation for the TMAH trench etch process. The FOX layer is typically removed to obtain substrate contacts to the silicon in the thermal inkjet fabrication process. However, in the past, the FOX layer has remained in the ink feed slot area. TMAH will not etch the FOX layer, and thus the FOX needs to be selectively removed to allow the etching of the silicon substrate to occur. The photomask design for the contact etch is changed, from the prior design, so that the FOX will be removed for the substrate contacts and the break trench at the same time. This area is then kept open throughout the remaining thinfilm processing before going through the TMAH etch process to create the breaktrench.  
         [0048]     Alternatively, instead of using the FOX layer as the mask for the TMAH etching process, the passivation layer (SiN/SiC) can be employed for this purpose. In one exemplary alternate embodiment, this passivation layer is extended so that it overlaps the edge of the FOX layer by about 3 microns.  
         [0049]     After the TMAH etch process, a break trench  124  ( FIG. 1B ) is formed in the substrate  102 . In an exemplary embodiment, the trench is 80 microns wide to a target depth of 58 microns, although the width and depth of the trench may be different for different slot sizes or applications. Now the remaining steps 3-8 in the fabrication process can be performed. These include the electronic testing of the thin film structure, and the application and patterning of the barrier layer  112  ( FIG. 2B ). The barrier layer is typically a polymer layer.  
         [0050]     After the barrier layer is fabricated on the printhead structure, the ink feed slot is created by abrasive machining, in this case by abrasive drilling from the underside of the substrate  102  (opposite side from the thinfilm layer side) along a drill slot  126 . The abrasive drilling process in an exemplary embodiment utilizes a sand blasting system that mixes a fine aluminum oxide abrasive into a high-pressure air stream. This mixture of abrasive and air is then plumed to a nozzle that is sized and shaped to create the desired cut profile in the substrate. The abrasive drilling cutting time, cutting pressure and nozzle separation for the silicon substrate is adjusted to obtain an appropriate slot through the silicon substrate.  
         [0051]     The drill slot  126  preferably enters the bottom of the trench  14 . Now the substrate material enveloped within the drill slot, indicated in  FIG. 1A  as  102 A, is completely separated from the remainder of the substrate, and can be removed to create the feed slot for the printhead.  
         [0052]     Now the printhead structure  100  can be passed through the remaining fabrication steps, including attachment of the orifice plate, wafer sawing and the attachment of the printhead to a flexible circuit, typically a TAB circuit, for attachment to a printhead pen body.  
         
       [0053]     Break-Trench and Drill Guide Trench Slot Embodiment ( FIGS. 2A-2B )  
         [0054]     In this embodiment, the initial breakthrough occurs along a deeper “drill guide” trench and then grows out to the perimeter etch trench. The perimeter etch trench is used primarily as a chip stop feature. Thus, with this process, the sand slotting process will first break through the wafer at the location of the center trench. The sand slotting will then be continued until the through slot has grown to the size of the outer break-trench A chip stop feature is one that will stop the propagation of shallow chips by allowing them to be terminated by breaking through the inside wall of the trench. When the chips or cracks break through the inside wall, the chip will stop as it can not propagate the stress through the gap.  
         [0055]      FIG. 2A  illustrates in top plan view the top of the substrate  102  after the thin film fabrication step on the substrate. The structure illustrated in  FIG. 2A  is similar to that shown in  FIG. 1A , but the field oxide layer in the center of the location of the feed slot is also removed, so that the silicon substrate surface is also exposed at  122 A. The TMAH trench etch process is then performed, to define a perimeter etch trench  134  which follows the outline of dashed line  120  ( FIG. 2A ), as well as a deeper drill guide trench  132  in the central region  122 A. In an exemplary embodiment, the perimeter trench is approximately 60 microns wide by 43 microns deep at its maximum depth, and the drill guide trench is approximately 80 microns wide by 53 microns deep at its maximum depth.  
         [0056]     The width of the etch mask will determine the terminal depth of the trenches produced by the TMAH. This is due to the low etch rate of the &lt;111&gt; plane in the silicon crystalline structure. The shallow perimeter trench will reach a stopping point when the &lt;111&gt; planes terminate in a sharp “V”. The wider center trench will not have reached this termination point and will continue to etch at the higher etch rate.  
         [0057]     After the TMAH etch process has been performed, and the two trenches  132 ,  134  formed, as illustrated in  FIG. 2B , the remaining steps in the fabrication process are performed. The abrasive drilling occurs along drill slot  136 , and an initial breakthrough of the silicon substrate  50  occurs along the deeper drill guide trench  132 . The removal of material then grows out to the perimeter etch trench  134 . The size of the through trench will be determined by the mechanical sand slotting process.  
         
       [0058]     Center-Trench Full Slot Embodiment ( FIGS. 3A-3B )  
         [0059]     In this embodiment, the abrasive drill slot is small enough to be placed in the center of the TMAH etch trench, and the sloped sides of the trench are used to contain the chipping and define the slot shape and position.  
         [0060]      FIG. 3A  illustrates in top plan view the top of the substrate  102  after the thin film fabrication step on the substrate.  FIG. 3B  shows in cross-section the substrate  102  after the TMAH etch process has been performed, and after the barrier layer  112  has been applied. The structure illustrated in  FIG. 3A  is similar to that shown in  FIG. 1A , but the field oxide layer  104  in the location of the feed slot is also removed to near the edges, leaving border region  104 C of the field oxide layer, so that the silicon substrate surface is also exposed at area  156 . The TMAH trench etch process is then performed, to define an etch trench  152  which follows the outline of dashed line  120  ( FIG. 3A ).  
         [0061]     After the TMAH etch process has been performed, and the trenches  152  formed, the remaining steps in the fabrication process are performed. The abrasive drilling occurs along drill slot  154 , and the removal of material inside the drill slot provides the ink fill slot. This embodiment can provide a narrower fill slot than the first two embodiments in some applications.  
         
       [0062]     Center-Trench Multiple Slot Embodiment ( FIGS. 4A-4B )  
         [0063]     This embodiment is similar to the center trench embodiment described with respect to  FIGS. 3A-3B , but multiple small slots are employed so that additional silicon is left in the center of the printhead die to increase die strength.  
         [0064]      FIG. 4A  illustrates in top plan view the top of the substrate  102  after the thin film fabrication step on the substrate.  FIG. 4B  is a cross-sectional view of the printhead structure  170  after the TMAH etch process has been performed to create a break trench and after the barrier layer  112  is applied. The structure illustrated in  FIG. 4A  is similar to that shown in  FIG. 3A , with the field oxide layer  104  in the location of the feed slot removed to near the edges, leaving border region  104 C of the field oxide layer. Dashed lines  172 A- 172 D indicate the desired perimeters of the multiple ink feed slots. The TMAH trench etch process is then performed, to define one etch trench in the region  178 .  
         [0065]     After the. TMAH etch process has been performed, and the trench  174  formed, the remaining steps in the fabrication process are performed. The abrasive drilling occurs along a drill slot for each slot location  172 A- 172 D, including drill slot  176 C for slot location  172 C, and the removal of material inside the drill slots provides the multiple slots. Thus, a nozzle with a plurality of slots fed from a single source would be produced to drill the desired pattern in a single process step. In an exemplary embodiment, the small rectangular openings are approximately 200 microns wide by 1500 microns long, with 1500 microns spacing between the nozzle openings. Therefore the nozzle produces a series of smaller slots.  
         
       [0066]     Island Trench Multi-Slot Embodiment (FIGS.  5 A-SC)  
         [0067]     In this design, Islands are left between the ink feed slots to help support the barrier, give additional die strength and promote the removal of air bubbles. The wedge shape of the island to slot edge forces the air bubbles towards the ink feed slots as they grow.  
         [0068]      FIG. 5A  illustrates in top plan view the top of the substrate  102  after the thin film fabrication step on the substrate.  FIG. 5B  is a cross-sectional view of the printhead structure  190  after the TMAH etch process has been performed to create a break trench and after the barrier layer  112  is applied. The structure illustrated in  FIG. 5A  is similar to that shown in  FIG. 4A , except that pyramid-shaped islands  104 D 1 - 104 D 3  of the field oxide layer  104  are left in the feed slot area. These islands will mask the underlying areas of the silicon substrate from the TMAH etching process. Dashed lines  172 A- 172 D indicate the desired perimeters of the multiple ink feed slots.  
         [0069]     The TMAH trench etch process is then performed, to define a patterned etch trench  192  in the region  178 .  
         [0070]     After the TMAH etch process has been performed, and the trench  192  formed, the remaining steps in the fabrication process are performed. When the barrier layer  112  is applied, the barrier will cover the pyramid-shaped islands  104 D 1 - 104 D 3 , as indicated in  FIG. 5C . The abrasive drilling occurs along a drill slot for each slot location  172 A- 172 D, including drill slot  176 C for slot location  172 C, and the removal of material inside the drill slots provides the multiple slots.  
         [0071]     The island trench design uses different artwork on the FOX (hardmask) level to pattern islands in the center of the ink feed slot area. This photomask is designed to leave pyramid shaped islands in the center of the ink feed slot area, as shown in  FIG. 5A . As in the foregoing embodiments, the barrier layer is then laminated and patterned, and in this case the barrier layer material is left covering the top of the pyramid-shaped islands to help support the orifice plate that is applied at a later time. The drill process is performed as in the embodiment of  FIGS. 4A-4B , in that a number of small through slots are created between the islands as shown in  FIG. 5B . The through slots in cross-section have a shallow trench at the center of the island that becomes deeper and wider as it approaches the cross-section at  5 B- 5 B.  
         
       [0072]     Chip Stop Bars  
         [0073]      FIGS. 6A-6B  diagrammatically depict a further embodiment, wherein trenches serving as chip stop bars are not connected at the corners.  FIG. 6A  is a diagrammatic top view of the substrate  220  after fabrication step 2, i.e. after the silicon substrate with the thinfilm layers have been subjected to the TMAH etching process, to form side trenches  226 A,  226 B and top and bottom trenches  228 A,  228 B. The drill slot is indicated by dashed line  222 . All substrate within line  222  is to be removed during the abrasive machining process conducted along drill slot  232  ( FIG. 6B ) to form the feed slot. In an exemplary embodiment, the side trenches are 80 microns wide by 8300 microns long, and the top and bottom trenches are 160 microns wide by 80 microns high. The separation of the side trenches, outside to outside, is 260 microns; the separation of the top and bottom trenches, outside to outside, is 8480 microns. The trenches have a target depth of 58 microns for this embodiment.  
         [0074]     Field oxide layer regions  104 A and  104 E 1 -E 4  ( FIG. 6A ) provide separation definition between the side trenches  226 A- 226 B and the top and bottom trenches  228 A- 228 B.  
         [0075]     The embodiment of  FIG. 6A  provides several advantages. Barrier thinning differences between the slot center and ends should be reduced, since the trench at the ends of the slot would not etch as deeply or as wide as in the embodiment of  FIG. 1A . Protection from die chipping is still in place on all sides of the die. A possible disadvantage is that the increased number of sharply etched corners may lead to reduced die strength.  
         
       [0076]     Side Trench Design  
         [0077]      FIGS. 7A-7B  illustrate a further embodiment of a break trench process, similar to the embodiment of  FIGS. 6A-6B , except that the top and bottom chip stop bars are omitted.  FIG. 7A  is a diagrammatic top view of the substrate  240  after fabrication step 2, i.e. after the silicon substrate with the thinfilm layers have been subjected to the TMAH etching process, to form side trenches  246 A,  246 B. As in  FIG. 6A , the nominal drill slot is indicated by dashed line  222 , and in an exemplary embodiment this feature can have the same nominal size as indicated above for the exemplary embodiment described regarding  FIG. 6A . For the substrate  240 , only the side chip stop bars  246 A,  246 B are employed, and are separated by FOX layer region  104 F ( FIG. 7A ) . Thus, etch trenches are provided at both sides of the slot area, but no etch trenches are provided at the top and bottom of the slot. In one exemplary embodiment, the side trenches can have a width of 80 microns and a length of 8430 microns. In another exemplary embodiment, the trenches are left somewhat short of the end of the slot to provide increased die strength, and have a length of 8100 microns. The substrate material within line  222  is to be removed during the subsequent abrasive machining process conducted along drill slot  250  ( FIG. 7B ).  
         [0078]     It is understood that the above-described embodiments are merely illustrative of the possible specific embodiments which may represent principles of the present invention. Other arrangements may readily be devised in accordance with these principles by those skilled in the art without departing from the scope and spirit of the invention.

Technology Classification (CPC): 1