Patent Abstract:
The present invention relates to new and novel tire construction and method of making same wherein the uncured elastomeric material that is laid upon the tire building drum during building of the tire preform will not experience substantially meridional stretch which would otherwise cause a decrease in the uniformity of ply thickness during expansion of the preform in the vulcanizing mold.

Full Description:
RELATED APPLICATIONS 
     This is a Divisional application of U.S. application Ser. No. 09/367,766 having a filing date of Aug. 19, 1999 now U.S. Pat. No. 6,261,399, and a common assignee with the present application. 
    
    
     TECHNICAL FIELD 
     The present invention relates to pneumatic tires and the method of making such tires. More particularly, the present invention relates to the construction of a preform tire using an inner liner formed of a plurality of overlaying plies. 
     BACKGROUND OF THE INVENTION 
     The automotive pneumatic tire is typically made using the flat band method of tire building wherein the various components, or plies, of the tire are applied, as flat stock, upon a rotating tire building drum forming a hollow, barrel shaped preform. In building the preform, the inner liner is first wrapped upon the drum followed by the carcass plies generally containing the tire reinforcement. The carcass plies are then followed by the belt plies, the side wall plies and the tread ply. The barrel shaped preform is then removed from the building drum and placed within a vulcanizing mold, having the general shape of the finished tire. The barrel shaped preform is next heated and expanded radially outward into the mold periphery typically by directing pressurized hot gas or steam into a bladder disposed within the preform. During the radial expansion of the preform within the mold, the cylindrically shaped plies must expand radially outward to radial dimensions much beyond those of the original preform. Therefore, the elastomeric material of each preform ply must stretchingly expand much like a balloon. During this expansion step the material thickness of the preform plies may be expected to decrease. 
     Of particular concern, in the present invention, is the inner liner ply. Typically the inner liner ply is laid upon the building drum as a flat piece of elastomeric stock having a uniform thickness. Thus, as the inner liner ply expands radially outward during the expansion step, the thickness of the inner liner is stretchingly thinned resulting in an inner liner ply having a thickness that progressively decreases from the tire bead area to the tire crown. 
     Therefore, to have a given inner liner thickness in the tire crown area, the thickness of the inner liner ply, when laid upon the tire building drum, must be oversized to allow for the stretching of the ply as the preform is expanded during the expansion step. Accordingly, the typical automotive tire structure exhibits an inner liner ply having excess material in the tire bead and side wall areas. 
     Prior art patent application WO-A-96 30221 also shows an air-permeation prevention layer (8) with layers (7) extending from the ends of a belt (6) toward the center (C). 
     PRIOR ART 
     To overcome the above described disadvantage, it has been a practice of the prior art to provide an elastomeric sheet having a variable thickness across its lateral width. Such inner liner sheet stock embodies a sheet thickness that progressively increases toward the center of the sheet from both sides. Thus, when such sheet stock is radially stretched during the expansion step, stretching occurs in the area of increased thickness thereby forming an inner liner having an approximate uniform thickness. However, such specialized sheet stock is more expensive than the uniform thickness sheet stock to manufacture and is unsuitable for rolling and storing on a feed spool prior to applying it upon the tire building drum. 
     SUMMARY OF THE INVENTION 
     It is an object of the present invention to provide a method and tire preform structure to eliminate the variable thickness of an automotive pneumatic tire inner liner when built by the flat band method of tire building. 
     Another object of the present invention is to provide a method and preform structure which results in a savings of elastomeric material in the tire inner liner that aids in weight reduction of a given tire. 
     In accord with the present invention, the standard practice of applying a single ply of elastomeric material upon the tire building drum to form the inner liner is replaced, in a first embodiment, by two overlapping plies of elastomeric material each having a uniform thickness. The two overlapping plies are laid upon the tire building drum such that when the tire preform is expanded radially outward during the expansion step, the gauge of the overlapping liners is reduced by stretching circumferentially to that necessary to prevent air penetration. Because of the minimal meridional (bead to bead) stretch during the expansion step, a single layer of the liner plies is sufficient. 
     As an alternative embodiment, the inner liner ply may be made-up of two separate elastomeric plies laid upon the building drum in a spaced relationship to each other with a third ply of elastomeric material being laid thereupon and overlapping the two spaced plies. As with the first embodiment, the three overlapping plies are laid upon the tire building drum such that when the tire preform is expanded radially outward during the expansion step, the gauge of the overlapping liners is reduced by stretching circumferentially to that necessary to prevent air penetration. Because of the minimal meridional (bead to bead) stretch during the expansion step, a single layer of the three liner plies is sufficient. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 presents a cross sectional view of a typical automotive tire construction, subsequent to expansion of the preform but before vulcanization has taken place, embodying the preferred embodiment of the present invention; 
     FIG. 2 presents a schematic perspective illustrating the flat band method of building a tire preform and showing application of the inner liner flat stock to the tire building drum in accord with the present invention; 
     FIG. 3 presents a cross sectional view taken along line  3 — 3  of FIG. 2 showing the inner liner, flat stock plies as laid upon the tire building drum; 
     FIG. 4 presents a cross sectional view of a typical automotive tire construction, subsequent to expansion of the preform but before vulcanization has taken place, embodying an alternate embodiment of the invention; 
     FIG. 5 presents a schematic perspective illustrating the flat band method of building a tire preform and showing application of the inner liner flat stock to the tire building drum in accord with an alternate embodiment of present invention; and 
     FIG. 6 presents a cross sectional view taken along line  6 — 6  of FIG. 5 showing the inner liner flat stock plies as laid upon the tire building drum. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     To best illustrate the present invention, FIG. 1 shows a typical automotive tire preform  10 , in cross-section, as it exists after expansion of the tire preform but prior to complete vulcanization. Tire preform  10  generally comprises two bead areas  12  and  13 , side walls  16  and  17 , tread or crown region  20 , and an inner liner  21  having two distinct plies  24  and  25 , in accordance with the present invention. For clarity of the present invention, the typical carcass reinforcing, extending between bead areas  12  and  13 , the belt structure in the crown area under the tread, and the bead ring structure are not shown. The preform has an inner meridional width L extending about the interior surface  23  of preform  10  from the outer edge of bead area  12  to the outer edge of bead area  13 , as shown in FIG.  1 . 
     As illustrated in FIGS. 2 and 3, the uncured inner liner  21  comprises two separate and distinct plies  24  and  25  of flat elastomeric material each having a uniform thickness and a width less than width L but greater than one half of width L. During the tire preform building stage, the inner liner plies  24  and  25  are laid upon the tire building drum  22 , as illustrated in FIGS. 2 and 3, wherein the first ply  24  extends from one edge  27  of preform width L to a predetermined position  28  on drum  22  beyond the midpoint  29  of width L. The second ply  25  is applied to the drum extending from the opposite edge  30  of preform width L to a predetermined position on drum  22  beyond the midpoint  29  of width L to overlap ply  24 . Plies  24  and  25  are arranged to overlap one another by the length X. The length X will necessarily vary depending upon tire size and the desired amount of overlap X′ in the expanded tire, as shown in FIG.  1 . For clarity of the invention, the additional plies typically applied to the tire preform upon the building drum  22  are not shown. 
     When a flat band tire preform  10  is built with the inner liner plies  24  and  25  laid upon the tire building drum  22 , as shown in FIGS. 2 and 3, and is expanded in the vulcanizing mold, plies  24  and  25 , being anchored at beads  12  and  13 , respectively, will stretch circumferentially in an amount proportional to the final diameter divided by the diameter of the tire preform prior to expansion. This stretch is responsible for the reduction in the gauge of the plies  24 ,  25 . Typically, during expansion of preform tire  10 , there is no substantial meridional, i.e. bead to bead, stretch of the plies. It is preferred that the amount of overlap X′, after expansion of the preform, extends across crown  20  and to the breaker or shoulder regions  14  and  15 , as illustrated in FIG.  1 . 
     Referring now to FIGS. 4,  5 , and  6 , an alternate embodiment of the present invention is illustrated. A typical automotive tire preform  40 , in cross section, is again shown as it exists after expansion of the tire preform but prior to complete vulcanization. Tire preform  40  generally comprises beads  42  and  43 , side walls  46  and  47 , a tread or crown region  50 , and an inner liner having three distinct plies  54 ,  55 , and  56 . For improved clarity of the present invention, the typical carcass reinforcement extending between the beads  42  and  43 , i.e., the belt structure in the crown area under the tread and the bead ring structure, are not shown. The preform  40  has an inner meridional width M extending about the inner width of surface  49  from the outer edge of bead area  42  to the outer edge of bead area  43 . 
     As illustrated in FIGS. 5 and 6, and in accord with the present invention, the tire inner liner in the uncured stage, comprises three separate and distinct plies  54 ,  55 , and  56  which are shown with a reduced width as compared with FIG.  4 . Ply  54  has a width W which is less than inner meridional width M. Ply  55  has a width Y, typically equal to width W. Ply  56  has a predetermined width Z. The plies  54  and  56  are generally of uniform thickness and the middle ply  56  can be thicker. With this construction, the thickness of ply  56  can be selected so that it will be close to the thickness of plies  54  and  55  after the plies are stretched circumferentially in the vulcanizing mold. It is also within the terms of the invention for the three plies to be of the same thickness. During the tire preform building stage, the inner liner plies  54 ,  55 , and  56  are laid upon the tire building drum  22 , as illustrated in FIGS. 5 and 6, wherein the first ply  54  extends from one edge  57  of preform width M to a predetermined position  58  on drum  22 . The second ply  55  is applied to drum  22  extending from the opposite edge  59  of preform width M to position  61 . Ply  56  equally overlaps plies  54  and  55  by a desired amount of overlap D and E, respectively, as shown in FIG.  4 . It is preferred that the amount of overlap D and E, after expansion of preform  40 , extends across crown  50  and to the breaker regions  44  and  45 , as illustrated in FIG.  4 . For clarity of the invention the additional plies typically applied to the tire preform upon the building drum  22  are not shown. 
     When a flat band tire preform  40  is built with the inner liner plies  54 ,  55  and  56  laid upon the tire building drum  22 , as shown in FIGS. 5 and 6, and is expanded in the vulcanizing mold, plies  54 ,  55  and  56  will stretch circumferentially in an amount proportional to the final diameter divided by the diameter of the tire preform prior to expansion. This stretch is responsible for the reduction in the gauge of the plies  54 ,  55  and  56 . Typically, during expansion of preform tire  40 , there is no substantial meridional, i.e. bead to bead, stretch of the plies. 
     While the invention has been described in combination with embodiments thereof, it is evident that many alternatives, modifications, and variations will be apparent to those skilled in the art in light of the foregoing teachings. Accordingly, the invention is intended to embrace all such alternatives, modifications and variations as fall within the scope of the appended claims.

Technology Classification (CPC): 8