Patent Abstract:
A drill bit having steel teeth is provided with a combination of hardfacing materials on the teeth. The bases of the teeth are hardfaced with nickel-based materials to significantly reduce any potential cracking therein. Portions of the supporting cones adjacent the teeth also may be fabricated with the nickel-based hardfacing. All other portions of the teeth are hardfaced with iron-based materials.

Full Description:
BACKGROUND OF THE INVENTION 
   1. Technical Field 
   The present invention relates in general to drill bits and, in particular, to an improved system, method, and apparatus for a steel tooth drill bit having enhanced tooth breakage resistance. 
   2. Description of the Related Art 
   In the prior art, steel tooth drill bits are great tools for drilling multiple formations due to the ability of their teeth to flex when encountering hard formations. However, this ability to provide flexure can cause cracking at the base of the teeth in the weld deposit and carburized area under the iron-based hardfacing deposits. Moreover, the cracks can grow during service or can aggravate pre-existing thermal cracks from the initial manufacturing process. 
   The manufacturing cracks can be caused by a variety of sources, but are primarily from the thermal stresses induced during the welding process while using iron-based hardfacing materials at the base of the teeth and subsequent hardening and carburization of the cone. The hardfacing can relieve the stress in the form of a crack. The cracks can propagate directly into the base steel of the teeth and/or the cone shell. The extent of the cracking is dependent upon the thermal management of the cone during the heat-up, welding, and the cooling down of the cone. Another factor affecting the extent of the cracking is how brittle the carburized case is underneath the hardfacing deposit. 
   During operation, the combination of the flexing of the teeth, formations drilled, operating parameters, and the corrosive environment can cause the cracks to grow while the drill bit is in service. This crack propagation can cause the teeth to eventually break off or cause the cracks to grow into the cone shell, both of which impede performance. 
   It is known that nickel-based hardfacing minimizes the transport of carbon into the steel substrate and generally does not produce a carburized case in the steel underneath the hardfacing deposit. In addition, the thermal stresses in nickel-based hardfacing are not as great as in iron-based hardfacing, such that nickel-based hardfacing is less likely to have thermal cracks. Nickel-based hardfacing is also very corrosion resistant compared to iron-based hardfacing. 
   SUMMARY OF THE INVENTION 
   In general, if cracks occur in nickel-based hardfacing they typically arrest in the hardfacing deposit and generally do not propagate into the steel substrate. This is primarily due to the round blunt tip crack of nickel-based materials, contrasted with the sharp tip crack in iron-based materials. However, iron-based hardfacing materials are more durable than current nickel-based hardfacing materials. The area of the teeth that receives most of the damage due to impacting is at or near the top of the teeth. Therefore, the crest and a portion of the flanks require a highly durable iron-based hardfacing. Since the bases of the teeth do not receive significant impacting those portions are very suitable for nickel-based hardfacing. By placing the nickel-based hardfacing at least at the bases of the teeth and/or the surrounding cone shell, the overall durability of the drill bit is improved. 
   Typically, the hardfacing is applied by an oxygen acetylene welding process, but other welding or coating processes of applying the hardfacing material may be used. Some high-content nickel alloys with hard component materials also may be used. 
   The bases of the teeth are provided with nickel-based hardfacing to significantly reduce any potential cracking therein and in the adjacent areas of the cone. All other portions of the teeth are hardfaced with iron-based materials such that all surfaces of the teeth are protected with one or the other type of hardfacing. In addition, manufacturers of drill bits prefer to weld with nickel-based materials due to ease of heat management in the teeth base and cone surface areas of the cutting structure. 
   The foregoing and other objects and advantages of the present invention will be apparent to those skilled in the art, in view of the following detailed description of the present invention, taken in conjunction with the appended claims and the accompanying drawings. 

   
     BRIEF DESCRIPTION OF THE DRAWINGS 
     So that the manner in which the features and advantages of the present invention, which will become apparent, are attained and can be understood in more detail, more particular description of the invention briefly summarized above may be had by reference to the embodiments thereof that are illustrated in the appended drawings which form a part of this specification. It is to be noted, however, that the drawings illustrate only some embodiments of the invention and therefore are not to be considered limiting of its scope as the invention may admit to other equally effective embodiments. 
       FIG. 1  is an isometric view of one embodiment of a drill bit constructed in accordance with the invention; 
       FIG. 2  is an enlarged photographic image of one embodiment of a cutter on the drill bit of  FIG. 1  and is constructed in accordance with the invention; 
       FIG. 3  is an enlarged photographic image of another embodiment of a cutter on the drill bit of  FIG. 1  and is constructed in accordance with the invention; and 
       FIG. 4  is a high level flow diagram of one embodiment of a method constructed in accordance with the invention. 
   

   DETAILED DESCRIPTION OF THE INVENTION 
   Referring to  FIG. 1 , one embodiment of a system, method, and apparatus for an earth boring bit  11  constructed in accordance with the invention is shown. Earth boring bit  11  includes a bit body  13  having threads  15  at its upper end for connecting bit  11  into a drill string (not shown). Bit  11  is depicted with three legs, and each leg of bit  11  is provided with a lubricant compensator  17 . At least one nozzle  19  is provided in bit body  13  for spraying cooling and lubricating drilling fluid from within the drill string to the bottom of the bore hole. 
   At least one cutter is rotatably secured to each leg of the bit body  13 . Preferably three cutters  21 ,  23  (one cutter being obscured from view in the perspective view of  FIG. 1 ) are rotatably secured to the bit body  13 . A plurality of teeth  25  are arranged in generally circumferential rows on cutters  21 ,  23 . Teeth  25  may be integrally formed from the material of cutters  21 ,  23 , which is typically steel. 
   Referring now to  FIGS. 2 and 3 , two embodiments of earth boring bits having cutters  21 ,  23  or roller cones that employ the novel elements of the invention are shown. Although the cutters  21 ,  23  and teeth  25  are shown with certain types of geometry, those skilled in the art will recognize that the invention is not limited to the illustrated embodiments. 
   For example, in the enlarged view of  FIG. 2 , the teeth  25  on the cutter  21  of the earth boring bit are shown with two different types of hardfacing materials  31 ,  33  formed thereon. The invention may be applied to only some of the teeth or all of the teeth, and on one of the cutters or all of the cutters. Furthermore, the invention also may be applied to other teeth or other portions of the drill bit other than the cutters. The first type of hardfacing  31  is formed from a nickel-based material and is located on proximal or base portions  35  of at least some of the teeth  25 . Optionally, the first hardfacing may comprise an alloy, such as a nickel alloy, or an alloy having a high nickel content with some hard component materials such as, for example, monocrystalline WC, sintered WC (crushed or spherical), cast WC (crushed or spherical), and/or with a matrix of Ni—Cr—B—Si. In the embodiment of  FIG. 2 , the first hardfacing  31  also is located on surfaces of the cutter  21  adjacent the aforementioned teeth  25 , such that the first hardfacing  31  smoothly transitions from the cutter  21  to the teeth  25 . 
   The second type of hardfacing  33  is formed from an iron-based material and is located on distal or upper portions of the same teeth with hardfacing  31 . Thus, all surfaces of the teeth  25  and, optionally, portions or the entire surface of the cutter  21  itself is protected with hardfacing materials. The second hardfacing  33  may be located at and adjacent to the top portions of the teeth  25 , such as on the crests and portions of the flanks of the teeth. Optionally, and as shown in  FIG. 3 , only the base portions of teeth  45  on cutter  40  may be provided with the first hardfacing  41  (i.e., without application of hardfacing  41  directly to the surfaces of cutter  40 ). The remaining portions of teeth  45  are protected by the second hardfacing  43 , as described herein. 
   Referring now to  FIG. 4 , the invention also comprises a method of fabricating a cutter for an earth boring bit. The method begins as indicated at step  51 , and comprises providing a cutter with teeth extending from the cutter (step  53 ); applying a first hardfacing on portions of at least some of the teeth (step  55 ); applying a second hardfacing that differs from the first hardfacing on other portions of said at least some of the teeth (step  57 ); before ending as indicated at step  59 . 
   Alternatively, the method may comprise one or more of the following steps, including: applying the first hardfacing on base portions of said at least some of the teeth, and/or on surfaces of the cutters adjacent said at least some of the teeth; and/or applying the second hardfacing to crests and portions of flanks of said at least some of the teeth. In addition, one embodiment of the method may comprise sequentially applying nickel-based hardfacing (e.g., a high-content nickel alloy with hard component materials) as the second hardfacing, after applying iron-based hardfacing as the first hardfacing. 
   While the invention has been shown or described in only some of its forms, it should be apparent to those skilled in the art that it is not so limited, but is susceptible to various changes without departing from the scope of the invention.

Technology Classification (CPC): 4