Patent Abstract:
A phase-change memory may be formed with at least two phase-change material layers separated by a barrier layer. The use of more than one phase-change layer enables a reduction in the programming volume while still providing adequate thermal insulation.

Full Description:
BACKGROUND  
         [0001]    This invention relates generally to memories that use phase-change materials.  
           [0002]    Phase-change materials may exhibit at least two different states. The states may be called the amorphous and crystalline states. Transitions between these states may be selectively initiated, for example, through temperature changes. The states may be distinguished because the amorphous state generally exhibits higher resistivity than the crystalline state. The amorphous state involves a more disordered atomic structure and the crystalline state involves a more ordered atomic structure. Generally, any phase-change material may be utilized; however, in some embodiments, thin-film chalcogenide alloy materials may be particularly suitable.  
           [0003]    The phase-change may be induced reversibly. Therefore, the memory may change from the amorphous to the crystalline state and may revert back to the amorphous state thereafter, or vice versa. In effect, each memory cell may be thought of as a programmable resistor that reversibly changes between higher and lower resistance states in response to temperature changes. The temperature changes may be induced by resistive heating.  
           [0004]    In some situations, the cell may have a large number of states. That is, because each state may be distinguished by its resistance, a number of resistance-determined states may be possible, allowing the storage of multiple bits of data in a single cell.  
           [0005]    A variety of phase-change alloys are known. Generally, chalcogenide alloys contain one or more elements from column VI of the periodic table. One particularly suitable group of alloys is GeSbTe alloys.  
           [0006]    A phase-change material may be formed within a passage or pore defined through a dielectric material. The phase-change material may be coupled to electrodes on either end of the passage. The contacts may pass current through the passage in order to program the cell through resistive heating or to read the programmed state of the cell.  
           [0007]    Current phase-change memories rely on the poor thermal conductivity of the chalcogenide phase-change memory material itself to thermally insulate the programmable volume from heat loss to the upper electrode. Consequently, in order to achieve better thermal isolation and, therefore, more energy efficient programming of the programmable volume, the thickness of the chalcogenide layer has to be increased. An increase of the thickness of the layer, however, also increases the volume of material that is capable of undergoing a phase-change during programming. Increasing the volume of material that undergoes the phase-change can adversely affect reliability, stability, and cycle life of the memory.  
           [0008]    Thus, there is a need for a phase-change memory with improved characteristics and performance. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0009]    [0009]FIG. 1 is an enlarged, cross-sectional view of one embodiment of the present invention;  
         [0010]    [0010]FIG. 2 is an enlarged, cross-sectional view of an initial stage of manufacturing of the device shown in FIG. 1 in accordance with one embodiment of the present invention;  
         [0011]    [0011]FIG. 3 is an enlarged, cross-sectional view of the embodiment shown in FIG. 2 at a later stage of manufacturing in accordance with one embodiment of the present invention;  
         [0012]    [0012]FIG. 4 is an enlarged, cross-sectional view of the embodiment shown in FIG. 3 at still a later stage of manufacturing in accordance with one embodiment of the present invention;  
         [0013]    [0013]FIG. 5 is an enlarged, cross-sectional view corresponding to FIG. 4 at still a later stage of manufacturing in accordance with one embodiment of the present invention; and  
         [0014]    [0014]FIG. 6 is an enlarged, cross-sectional view of the embodiment shown in FIG. 5 at a later stage of manufacturing in accordance with one embodiment of the present invention. 
     
    
     DETAILED DESCRIPTION  
       [0015]    Referring to FIG. 1, a phase-change memory  10  may be formed on an integrated circuit substrate  12 . The phase-change memory  10  may include a lower electrode  14  that in one embodiment may be made of cobalt silicide. An upper electrode  28  sandwiches a lower, programmable phase-change layer  22  and an upper phase-change layer  26 . Between the phase-change layers  22  and  26  is a chemical barrier layer  24 .  
         [0016]    The pore of the phase-change memory  10  may be defined by sidewall spacer  20 . That is, the region of contact between the lower electrode  14  and the phase-change layer  22  may be of a size determined through the imposition of the cylindrical sidewall spacer  20 . In one embodiment, the pore, including the phase-change layers  22  and  26 , may be defined within an opening formed in a pair of insulator layers, such as the upper insulating layer  18  and the lower insulating layer  16 . The upper insulating layer  18  may be silicon dioxide in one embodiment, and the lower insulating layer  16  may be silicon nitride in one embodiment.  
         [0017]    While a structure is illustrated in which two layers of phase-change material are utilized, more layers may be utilized in other embodiments. The thickness of the first phase-change layer  22  may be in the range of 300 to 500 Angstroms. The thickness of this layer may be chosen so as to reduce the vertical dimension of the programmed volume. The phase-change layer  22  may be deposited in a cup-shaped opening formed by the sidewall spacer  20 , resulting in a cup-shaped phase-change layer  22 . A similar shape is therefore defined for the barrier layer  24  and the overlying phase-change layer  26 . In one embodiment, the phase-change layers  22  and  26  may be formed using vapor deposition.  
         [0018]    The barrier layer  24  provides a chemical barrier between the underlying programmable phase-change layer  22  and the overlying phase-change layer  26 . The overlying phase-change layer  26  may be provided primarily for thermal isolation in some embodiments. The barrier layer  24  may have adequate electrical conductivity so that the programming current passing through the programmable phase-change layer  22  can flow laterally around any resistive region of the thermal isolation phase-change layer  26  and may contact to the conductive regions of this layer distant from the programming region.  
         [0019]    Typical thickness of the barrier layer  24  may be in the range of 50 to 200 Angstroms. The thermally insulating phase-change material layer  26  may also be vapor deposited in situ onto the barrier layer  24 . The thermally insulating phase-change material layer  26  can be made of the same composition as the programmable phase-change layer  22  or it can be chosen from a range of available chalcogenide materials with poor thermal conductivity. In one embodiment, it is advantageous that the layer  26  has a thermal conductivity of less than 1E-2 W/cm.K and good electrical conductivity, for example, greater than 40 Ω −1  cm −1 . The thickness of the layer  26  can be in the range of from 100 to more than 1,000 Angstroms.  
         [0020]    Referring to FIG. 2, a mask  30  may be defined on a stack including the substrate  12  covered by the lower electrode  14 , the first insulating layer  16 , the second insulating layer  18 .  
         [0021]    Turning next to FIG. 3, an opening  32  may be etched through the insulating layers  16  and  18 , stopping on the lower electrode  14 . In one embodiment, an etchant that is selective to the layers  16  and  18  and that is less effective against the electrode  14  may be utilized. Thereafter, the insulating material  20  may be deposited into the pore and over the layer  18 , as shown in FIG. 4. A variety of insulating layers may be utilized including oxide. In one embodiment, a tetraethylorthosilicate (TEOS) oxide deposition process may be utilized. The deposited layer  20  is then subjected to an anisotropic etch to form the cylindrical sidewall spacer  20  as shown in FIG. 5.  
         [0022]    The sidewall spacer  20  and insulating layer  18  may then be coated with the programmable phase-change layer  22 . The layer  22  may then be coated with the barrier layer  24  and the insulating phase-change layer  26 . Finally, the upper electrode  28  may be deposited. Because of the imposition of the sidewall spacer  20 , each of the layers  22 ,  24 ,  26  and  28 , to some degree, may be defined in a cup-shaped configuration. The structure shown in FIG. 6 may then be subjected to patterning and etching to result in the structure shown in FIG. 1 in some embodiments.  
         [0023]    Through the use of multiple chalcogenide layers, the memory cell  10  benefits from the enhanced thermal isolation. At the same time, the volume of material that undergoes a phase-change during programming may be relatively limited. In other words, the insulating effect of the combined layers  22  and  26  may reduce heat loss from the memory  10 , improving programming performance. At the same time, it is not necessary to program the insulating layer  26 , reducing the volume of material that must undergo the phase-change during programming. This may improve reliability, stability, and cycle life of the memory  10  in some embodiments.  
         [0024]    While the present invention has been described with respect to a limited number of embodiments, those skilled in the art will appreciate numerous modifications and variations therefrom. It is intended that the appended claims cover all such modifications and variations as fall within the true spirit and scope of this present invention.